A cross-shear deformation for optimizing the strength and ductility of AZ31 magnesium alloys

PubMed Central

Hamad, Kotiba; Ko, Young Gun

2016-01-01

Magnesium alloys have recently attracted great interest due their lightweight and high specific strength. However, because of their hexagonal close-packed structure, they have few active slip systems, resulting in poor ductility and high mechanical anisotropy at room temperature. In the present work, we used a cross-shear deformation imposed by a differential speed rolling (DSR) technique to improve the room temperature strength and ductility of AZ31 magnesium alloy sheets. To introduce the cross-shear deformation, the sheets were rotated 180° around their longitudinal axis between the adjacent passes of DSR. The sheets of the AZ31 alloy subjected to the cross-shear deformation showed a uniform fine microstructure (1.2 ± 0.1 μm) with weak basal textures. The fabricated sheets showed a simultaneous high ultimate tensile strength and elongation-to-failure, i.e., ~333 MPa and ~21%, respectively. These were explained based on the structural features evolved due to the cross-shear deformation by DSR. The high strength was attributed to the uniform fine microstructure, whereas the high ductility was explained based on the basal texture weakening. PMID:27406685

76 FR 60582 - Buy America Waiver Notification

Federal Register 2010, 2011, 2012, 2013, 2014

2011-09-29

... 1/ 2'' x 0.008 steel fiber with ultimate tensile strength of 290ksi for experimental use in Ultra... 0.008 steel fiber with ultimate tensile strength of 290ksi for experimental use in UHPC in Iowa. In... potential domestic manufacturers for 1/2'' x 0.008 steel fiber with ultimate tensile strength of 290ksi for...

78 FR 63563 - Buy America Waiver Notification

Federal Register 2010, 2011, 2012, 2013, 2014

2013-10-24

.... steel fibers with ultimate tensile strength of 290 ksi. in Ultra High Performance Concrete (UHPC) at the... appropriate to use UHPC 0.5 in. x 0.008 in. steel fibers with ultimate tensile strength 290 ksi. on Federal... for the use of non-domestic UHPC 0.5 in. x 0.008 in. steel fibers with ultimate tensile strength of...

Relationship between mechanical properties of one-step self-etch adhesives and water sorption.

PubMed

Hosaka, Keiichi; Nakajima, Masatoshi; Takahashi, Masahiro; Itoh, Shima; Ikeda, Masaomi; Tagami, Junji; Pashley, David H

2010-04-01

The purpose of this study was to evaluate the relationship between changes in the modulus of elasticity and ultimate tensile strength of one-step self-etch adhesives, and their degree of water sorption. Five one-step self-etch adhesives, Xeno IV (Dentsply Caulk), G Bond (GC Corp.), Clearfil S3 Bond (Kuraray Medical Inc.), Bond Force (Tokuyama Dental Corp.), and One-Up Bond F Plus (Tokuyama Dental Corp.) were used. Ten dumbelled-shaped polymers of each adhesive were used to obtain the modulus of elasticity by the three-point flexural bending test and the ultimate tensile strength by microtensile testing. The modulus of elasticity and the ultimate tensile strength were measured in both dry and wet conditions before/after immersion in water for 24h. Water sorption was measured, using a modification of the ISO-4049 standard. Each result of the modulus of elasticity and ultimate tensile strength was statistically analyzed using a two-way ANOVA and the result of water sorption was statistically analyzed using a one-way ANOVA. Regression analyses were used to determine the correlations between the modulus of elasticity and the ultimate tensile strength in dry or wet states, and also the percent decrease in these properties before/after immersion of water vs. water sorption. In the dry state, the moduli of elasticity of the five adhesive polymers varied from 948 to 1530 MPa, while the ultimate tensile strengths varied from 24.4 to 61.5 MPa. The wet specimens gave much lower moduli of elasticity (from 584 to 1073 MPa) and ultimate tensile strengths (from 16.5 to 35.0 MPa). Water sorption varied from 32.1 to 105.8 g mm(-3). The moduli of elasticity and ultimate tensile strengths of the adhesives fell significantly after water-storage. Water sorption depended on the constituents of the adhesive systems. The percent decreases in the ultimate tensile strengths of the adhesives were related to water sorption, while the percent reductions in the moduli of elasticity of the adhesives were not related to water sorption. Copyright (c) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

14 CFR 25.305 - Strength and deformation.

Code of Federal Regulations, 2013 CFR

2013-01-01

... strength is shown by dynamic tests simulating actual load conditions, the 3-second limit does not apply. Static tests conducted to ultimate load must include the ultimate deflections and ultimate deformation....305 Aeronautics and Space FEDERAL AVIATION ADMINISTRATION, DEPARTMENT OF TRANSPORTATION AIRCRAFT...

14 CFR 25.305 - Strength and deformation.

Code of Federal Regulations, 2012 CFR

2012-01-01

... strength is shown by dynamic tests simulating actual load conditions, the 3-second limit does not apply. Static tests conducted to ultimate load must include the ultimate deflections and ultimate deformation....305 Aeronautics and Space FEDERAL AVIATION ADMINISTRATION, DEPARTMENT OF TRANSPORTATION AIRCRAFT...

14 CFR 25.305 - Strength and deformation.

Code of Federal Regulations, 2014 CFR

2014-01-01

... strength is shown by dynamic tests simulating actual load conditions, the 3-second limit does not apply. Static tests conducted to ultimate load must include the ultimate deflections and ultimate deformation....305 Aeronautics and Space FEDERAL AVIATION ADMINISTRATION, DEPARTMENT OF TRANSPORTATION AIRCRAFT...

14 CFR 25.305 - Strength and deformation.

Code of Federal Regulations, 2010 CFR

2010-01-01

... strength is shown by dynamic tests simulating actual load conditions, the 3-second limit does not apply. Static tests conducted to ultimate load must include the ultimate deflections and ultimate deformation....305 Aeronautics and Space FEDERAL AVIATION ADMINISTRATION, DEPARTMENT OF TRANSPORTATION AIRCRAFT...

14 CFR 25.305 - Strength and deformation.

Code of Federal Regulations, 2011 CFR

2011-01-01

... strength is shown by dynamic tests simulating actual load conditions, the 3-second limit does not apply. Static tests conducted to ultimate load must include the ultimate deflections and ultimate deformation....305 Aeronautics and Space FEDERAL AVIATION ADMINISTRATION, DEPARTMENT OF TRANSPORTATION AIRCRAFT...

Positive psychology in rehabilitation medicine: a brief report.

PubMed

Bertisch, Hilary; Rath, Joseph; Long, Coralynn; Ashman, Teresa; Rashid, Tayyab

2014-01-01

The field of positive psychology has grown exponentially within the last decade. To date, however, there have been few empirical initiatives to clarify the constructs within positive psychology as they relate to rehabilitation medicine. Character strengths, and in particular resilience, following neurological trauma are clinically observable within rehabilitation settings, and greater knowledge of the way in which these factors relate to treatment variables may allow for enhanced treatment conceptualization and planning. The goal of this study was to explore the relationships between positive psychology constructs (character strengths, resilience, and positive mood) and rehabilitation-related variables (perceptions of functional ability post-injury and beliefs about treatment) within a baseline data set, a six-month follow-up data set, and longitudinally across time points. Pearson correlations and supplementary multiple regression analyses were conducted within and across these time points from a starting sample of thirty-nine individuals with acquired brain injury (ABI) in an outpatient rehabilitation program. Positive psychology constructs were related to rehabilitation-related variables within the baseline data set, within the follow-up data set, and longitudinally between baseline positive psychology variables and follow-up rehabilitation-related data. These preliminary findings support relationships between character strengths, resilience, and positive mood states with perceptions of functional ability and expectations of treatment, respectively, which are primary factors in treatment success and quality of life outcomes in rehabilitation medicine settings. The results suggest the need for more research in this area, with an ultimate goal of incorporating positive psychology constructs into rehabilitation conceptualization and treatment planning.

Mechanical behavior of post-processed Inconel 718 manufactured through the electron beam melting process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kirka, Michael M.; Medina, Frank; Dehoff, Ryan R.

Here, the electron beam melting (EBM) process was used to fabricate Inconel 718. The microstructure and tensile properties were characterized in both the as-fabricated and post-processed state transverse (T-orientation) and longitudinal (L-orientation) to the build direction. Post-processing involved both a hot isostatic pressing (HIP) and solution treatment and aging (STA) to homogenize the microstructure. In the as-fabricated state, EBM Inconel 718 exhibits a spatially dependent microstructure that is a function of build height. Spanning the last few layers is a cored dendritic structure comprised of the products (carbides and Laves phase) predicted under equilibrium solidification conditions. With increasing distance frommore » the build's top surface, the cored dendritic structure becomes increasingly homogeneous with complete dissolution of the secondary dendrite arms. Further, temporal phase kinetics are observed to lead to the dissolution of the strengthening γ"γ" and precipitation of networks of fine δ needles that span the grains. Microstructurally, post-processing resulted in dissolution of the δ networks and homogeneous precipitation of γ'"γ'" throughout the height of the build. In the as-fabricated state, the monotonic tensile behavior exhibits a height sensitivity within the T-orientation at both 20 and 650 °C. Along the L-orientation, the tensile behavior exhibits strength values comparable to the reference wrought material in the fully heat-treated state. After post-processing, the yield strength, ultimate strength, and elongation at failure for the EBM Inconel 718 were observed to have beneficially increased compared to the as-fabricated material. Further, as a result of post-processing the spatial variance of the ultimate yield strength and elongation at failure within the transverse direction decreased by 4 and 3× respectively.« less

Mechanical behavior of post-processed Inconel 718 manufactured through the electron beam melting process

DOE PAGES

Kirka, Michael M.; Medina, Frank; Dehoff, Ryan R.; ...

2016-10-21

Here, the electron beam melting (EBM) process was used to fabricate Inconel 718. The microstructure and tensile properties were characterized in both the as-fabricated and post-processed state transverse (T-orientation) and longitudinal (L-orientation) to the build direction. Post-processing involved both a hot isostatic pressing (HIP) and solution treatment and aging (STA) to homogenize the microstructure. In the as-fabricated state, EBM Inconel 718 exhibits a spatially dependent microstructure that is a function of build height. Spanning the last few layers is a cored dendritic structure comprised of the products (carbides and Laves phase) predicted under equilibrium solidification conditions. With increasing distance frommore » the build's top surface, the cored dendritic structure becomes increasingly homogeneous with complete dissolution of the secondary dendrite arms. Further, temporal phase kinetics are observed to lead to the dissolution of the strengthening γ"γ" and precipitation of networks of fine δ needles that span the grains. Microstructurally, post-processing resulted in dissolution of the δ networks and homogeneous precipitation of γ'"γ'" throughout the height of the build. In the as-fabricated state, the monotonic tensile behavior exhibits a height sensitivity within the T-orientation at both 20 and 650 °C. Along the L-orientation, the tensile behavior exhibits strength values comparable to the reference wrought material in the fully heat-treated state. After post-processing, the yield strength, ultimate strength, and elongation at failure for the EBM Inconel 718 were observed to have beneficially increased compared to the as-fabricated material. Further, as a result of post-processing the spatial variance of the ultimate yield strength and elongation at failure within the transverse direction decreased by 4 and 3× respectively.« less

A mechanical property and stress corrosion evaluation of Custom 455 stainless steel alloy

NASA Technical Reports Server (NTRS)

Montano, J. W.

1972-01-01

The mechanical and stress corrosion properties are presented of vacuum melted Custom 455 stainless steel alloy bar (1.0-inch diameter) and sheet (0.083-inch thick) material aged at 950 F, 1000 F, and 1050 F. Low temperature mechanical properties were determined at temperatures of 80 F, 0 F, -100 F, and -200 F. For all three aging treatments, the ultimate tensile and 0.2 percent offset yield strengths increased with decreasing test temperatures while the elongation held fairly constant down to -100 F and decreased at -200 F. Reduction in Area decreased moderately with decreasing temperature for the longitudinal round (0.250-inch diameter) specimens. Notched tensile strength and charpy V-notched impact strength decreased with decreasing test temperature. For all three aging treatments, no failures were observed in the unstressed specimens or the specimens stressed to 50, 75, and 100 percent of their yield strengths for 180 days of alternate immersion testing in a 3.5 percent NaCl solution. As indicated by the results of tensile tests performed after alternate immersion testing, the mechanical properties of Custom 455 alloy were not affected by stress or exposure under the conditions of the evaluation.

Effects of conventional welding and laser welding on the tensile strength, ultimate tensile strength and surface characteristics of two cobalt-chromium alloys: a comparative study.

PubMed

Madhan Kumar, Seenivasan; Sethumadhava, Jayesh Raghavendra; Anand Kumar, Vaidyanathan; Manita, Grover

2012-06-01

The purpose of this study was to evaluate the efficacy of laser welding and conventional welding on the tensile strength and ultimate tensile strength of the cobalt-chromium alloy. Samples were prepared with two commercially available cobalt-chromium alloys (Wironium plus and Diadur alloy). The samples were sectioned and the broken fragments were joined using Conventional and Laser welding techniques. The welded joints were subjected to tensile and ultimate tensile strength testing; and scanning electron microscope to evaluate the surface characteristics at the welded site. Both on laser welding as well as on conventional welding technique, Diadur alloy samples showed lesser values when tested for tensile and ultimate tensile strength when compared to Wironium alloy samples. Under the scanning electron microscope, the laser welded joints show uniform welding and continuous molt pool all over the surface with less porosity than the conventionally welded joints. Laser welding is an advantageous method of connecting or repairing cast metal prosthetic frameworks.

Cryogenic Properties of Aluminum Beryllium and Beryllium Materials

NASA Technical Reports Server (NTRS)

Gamwell, Wayne R.; McGill, Preston B.

2003-01-01

Ultimate tensile strength, yield strength, and elongation were obtained for the aluminum-beryllium alloy, AlBeMetl62 (38%Al-62%Be), at cryogenic (-195.5 C (-320 F) and (-252.8 C) (-423 F)) temperatures, and for an optical grade beryllium, O-30H (99%Be), at -252.8 C. AlBeMetl62 material was purchased to the requirements of SAE-AMS7912, "Aluminum-Beryllium Alloy, Extrusions." O-30H material was purchased to the requirements of Brush Wellman Inc. specification O-30H Optical Grade Beryllium. The ultimate tensile and yield strengths for extruded AlBeMetl62 material increased with decreasing temperature, and the percent elongation decreased with decreasing temperature. Design properties for the ultimate tensile strength, yield strength, and percent elongation for extruded AlBeMetl62 were generated. It was not possible to distinguish a difference in the room and cryogenic ultimate strength for the hot isostatically pressed (HIP'ed) O-30H material. The O30H elongation decreased with decreasing temperature.

Optimization and Prediction of Ultimate Tensile Strength in Metal Active Gas Welding.

PubMed

Ampaiboon, Anusit; Lasunon, On-Uma; Bubphachot, Bopit

2015-01-01

We investigated the effect of welding parameters on ultimate tensile strength of structural steel, ST37-2, welded by Metal Active Gas welding. A fractional factorial design was used for determining the significance of six parameters: wire feed rate, welding voltage, welding speed, travel angle, tip-to-work distance, and shielded gas flow rate. A regression model to predict ultimate tensile strength was developed. Finally, we verified optimization of the process parameters experimentally. We achieved an optimum tensile strength (558 MPa) and wire feed rate, 19 m/min, had the greatest effect, followed by tip-to-work distance, 7 mm, welding speed, 200 mm/min, welding voltage, 30 V, and travel angle, 60°. Shield gas flow rate, 10 L/min, was slightly better but had little effect in the 10-20 L/min range. Tests showed that our regression model was able to predict the ultimate tensile strength within 4%.

[The effects of different welding wires on the mechanical properties of laser welding joints].

PubMed

Huang, Qing-feng; Zhang, Jian-zhong; Jiang, Wei-dong; Li, Quan; Yu, Jin-xing

2006-08-01

To evaluate the mechanical properties and microstructure of laser-welded joints with different welding wires for clinical use of welding wire. The standard tensile test and three-point bending test rods were made from Co-Cr and Ni-Cr alloy, and were laser-welded with different welding wire (commercially welding wire and casting wire). Then the tensile rods were tested for the ultimate tensile strength (UTS), and the bending rods for the ultimate bending strength (UBS). The results was analyzed by one-way ANOVA. The tensile fracture surface were examined by scanning electron microscopy (SEM). Metallurgical analysis were also performed on polished longitudinal sectioned samples. For Co-Cr alloy, the UTS of casting wire group and commercially welding wire group was respectively (606.40+/-82.53)MPa and (693.61+/-47.68)MPa; the UBS was respectively (997.95+/-88.89)MPa and (1160.76+/-91.59)MPa. ANOVA showed a significant difference of UTS and UBS between the two groups at the 0.05 level (P<0.05). For Ni-Cr alloy, the UTS of casting wire group and commercially welding wire group was respectively (558.14+/-46.75)MPa and (582.32+/-35.43)MPa; the UBS was respectively (1084.75+/-46.02)MPa and (1078.29+/-36.25)MPa. There was no significant difference between the two groups (P>0.05). SEM and metallurgical examination showed the welded zone exhibiting more cracks in the casting wire group than in the commercially welding wire group. It would be advisable to work with commercially welding wire for the joints that need better strength.

Long Term Displacement Data of Woven Fabric Webbings Under Constant Load for Inflatable Structures

NASA Technical Reports Server (NTRS)

Kenner, Winfred S.; Jones, Thomas C.; Doggett, William R.; Lucy, Melvin H.; Grondin, Trevor A.; Whitley, Karen S.; Duncan, Quinton; Plant, James V.

2014-01-01

Inflatable modules for space applications offer weight and launch volume savings relative to current metallic modules. Limited data exist on the creep behavior of the restraint layer of inflatable modules. Long-term displacement and strain data of two high strength woven fabric webbings, Kevlar and Vectran, under constant load is presented. The creep behavior of webbings is required by designers to help determine service life parameters of inflatable modules. Four groups of different webbings with different loads were defined for this study. Group 1 consisted of 4K Kevlar webbings loaded to 33% ultimate tensile strength and 6K Vectran webbings loaded to 27% ultimate tensile strength, group 2 consisted of 6K Kevlar webbings loaded to 40% and 43% ultimate tensile strength, and 6K Vectran webbings loaded to 50% ultimate tensile strength, group 3 consisted of 6K Kevlar webbings loaded to 52% ultimate tensile strength and 6K Vectran webbings loaded to 60% ultimate tensile strength, and group 4 consisted of 12.5K Kevlar webbings loaded to 22% ultimate tensile strength, and 12.5K Vectran webbings loaded to 22% ultimate tensile strength. The uniquely designed test facility, hardware, displacement measuring devices, and test data are presented. Test data indicate that immediately after loading all webbings stretch an inch or more, however as time increases displacement values significantly decrease to fall within a range of several hundredth of an inch over the remainder of test period. Webbings in group 1 exhibit near constant displacements and strains over a 17-month period. Data acquisition was suspended after the 17th month, however webbings continue to sustain load without any local webbing damage as of the 21st month of testing. Webbings in group 2 exhibit a combination of initial constant displacement and subsequent increases in displacement rates over a 16-month period. Webbings in group 3 exhibit steady increases in displacement rates leading to webbing failure over a 3-month period. Five of six webbings experienced local damage and subsequent failure in group 3. Data from group 4 indicates increasing webbing displacements over a 7-month period. All webbings in groups 1, 2, and 4 remain suspended without any local damage as of the writing of this paper. Variations in facility temperatures over test period seem to have had limited effect on long-term webbing displacement data.

Transverse and longitudinal tensile properties at 760 C of several oxide dispersion strengthened nickel-base alloys

NASA Technical Reports Server (NTRS)

Anglin, A. E., Jr.

1979-01-01

The transverse and longitudinal tensile properties of the oxide dispersion strengthened nickel-base alloys were determined at 760 C. The alloys with small amounts of gamma prime have strength levels suitable for turbine vane applications, while other highly alloyed, gamma prime strengthened superalloys have strengths typical of turbine blade materials. These alloys were produced by mechanical alloying and extrusion and the turbine blade alloys were also directionally recrystallized. Resultant grain aspect ratios varied from 1:1 to over 20:1. Longitudinal tensile strengths ranged from 285 to 1175 MPa, while longitudinal elongations were in excess of 4 percent for all alloys. Transverse tensile strengths were comparable to longitudinal strengths, but transverse ductility levels were generally less than 2 percent elongation. Tensile and yield strengths increased with increasing strain rate over the range 0.001 to 0.05 per second. Ductility in both orientations was not strain rate sensitive but could be related to grain size and grain aspect ratio.

Numerical Study on Section Constitutive Relations of Members Reinforced by Steel-BFRP Composite Bars

NASA Astrophysics Data System (ADS)

Xiao, Tongliang; Qiu, Hongxing

2017-06-01

Steel-Basalt FRP Composite Bar (S-BFCB) is a new kind of substitute material for longitudinal reinforcement, with high elastic modulus, stable post-yield stiffness and excellent corrosive resistance. Based on mechanical properties of S-BFCB and the plane cross-section assumption, the moment-curvature curves of beam and column members are simulated. Some parameters such as equivalent rebar ratio, postyeild stiffness, concrete strength and axial compression ratio of column were discussed. Results show that the constitutive relation of the cross section is similar with RC member in elastic and cracking stages, while different in post-yield stage. With the increase of postyeild stiffness ratio of composite bar, the ultimate bearing capacity of component improved observably, member may turn out over-reinforced phenomenon, concrete crushing may appear before the fibersarefractured. The effect of concrete strength increase in lower postyeild stiffness ratio is not obvious than in higher. The increase of axial compression ratio has actively influence on bearing capacity of column, but decreases on the ductility.

Improved stud configurations for attaching laminated wood wind turbine blades

NASA Technical Reports Server (NTRS)

Fadoul, J. R.

1985-01-01

A series of bonded stud design configurations was screened on the basis of tension-tension cyclic tests to determine the structural capability of each configuration for joining a laminated wood structure (wind turbine blade) to a steel flange (wind turbine hub). Design parameters which affected the joint strength (ultimate and fatigue) were systematically varied and evaluated through appropriate testing. Two designs showing the most promise were used to fabricate addiate testing. Two designs showing the most promise were used to fabricate additional test specimens to determine ultimate strength and fatigue curves. Test results for the bonded stud designs demonstrated that joint strengths approaching the 10,000 to 12,000 psi ultimate strength and 5000 psi high cycle fatigue strength of the wood epoxy composite could be achieved.

Dentin bond strength of two resin-ceramic computer-aided design/computer-aided manufacturing (CAD/CAM) materials and five cements after six months storage.

PubMed

Flury, Simon; Schmidt, Stefanie Zita; Peutzfeldt, Anne; Lussi, Adrian

2016-10-01

The aim was to investigate dentin bond strength of two resin-ceramic materials and five cements after 24 h and six months storage. Cylinders (n=15/group) of Lava Ultimate (3M ESPE) and VITA ENAMIC (VITA Zahnfabrik) were cemented to mid-coronal dentin of 300 extracted human molars with RelyX Ultimate (3M ESPE), PANAVIA F2.0 (Kuraray), Variolink II (Ivoclar Vivadent), els cem (Saremco Dental), or Ketac Cem Plus (3M ESPE). Shear bond strength (SBS) was measured after 24 h or six months storage (37°C, 100% humidity) and statistically analyzed (significance level: α=0.05). SBS varied markedly between Lava Ultimate and VITA ENAMIC, between the five cements, and between storage of either 24 h or six months. After six months, SBS was highest when Lava Ultimate was cemented with RelyX Ultimate and when VITA ENAMIC was cemented with RelyX Ultimate or with Variolink II. Lava Ultimate was somewhat more sensitive to storage than was VITA ENAMIC.

Probabilistic Modeling of Ceramic Matrix Composite Strength

NASA Technical Reports Server (NTRS)

Shan, Ashwin R.; Murthy, Pappu L. N.; Mital, Subodh K.; Bhatt, Ramakrishna T.

1998-01-01

Uncertainties associated with the primitive random variables such as manufacturing process (processing temperature, fiber volume ratio, void volume ratio), constituent properties (fiber, matrix and interface), and geometric parameters (ply thickness, interphase thickness) have been simulated to quantify the scatter in the first matrix cracking strength (FMCS) and the ultimate tensile strength of SCS-6/RBSN (SiC fiber (SCS-6) reinforced reaction-bonded silicon nitride composite) ceramic matrix composite laminate at room temperature. Cumulative probability distribution function for the FMCS and ultimate tensile strength at room temperature (RT) of (0)(sub 8), (0(sub 2)/90(sub 2), and (+/-45(sub 2))(sub S) laminates have been simulated and the sensitivity of primitive variables to the respective strengths have been quantified. Computationally predicted scatter of the strengths for a uniaxial laminate have been compared with those from limited experimental data. Also the experimental procedure used in the tests has been described briefly. Results show a very good agreement between the computational simulation and the experimental data. Dominating failure modes in (0)(sub 8), (0/90)(sub s) and (+/-45)(sub S) laminates have been identified. Results indicate that the first matrix cracking strength for the (0)(sub S), and (0/90)(sub S) laminates is sensitive to the thermal properties, modulus and strengths of both the fiber and matrix whereas the ultimate tensile strength is sensitive to the fiber strength and the fiber volume ratio. In the case of a (+/-45)(sub S), laminate, both the FMCS and the ultimate tensile strengths have a small scatter range and are sensitive to the fiber tensile strength as well as the fiber volume ratio.

Mental Health Promotion in Public Health: Perspectives and Strategies From Positive Psychology

PubMed Central

Seligman, Martin E.P.; Peterson, Christopher; Diener, Ed; Zack, Matthew M.; Chapman, Daniel; Thompson, William

2011-01-01

Positive psychology is the study of what is “right” about people—their positive attributes, psychological assets, and strengths. Its aim is to understand and foster the factors that allow individuals, communities, and societies to thrive. Cross-sectional, experimental, and longitudinal research demonstrates that positive emotions are associated with numerous benefits related to health, work, family, and economic status. Growing biomedical research supports the view that positive emotions are not merely the opposite of negative emotions but may be independent dimensions of mental affect. The asset-based paradigms of positive psychology offer new approaches for bolstering psychological resilience and promoting mental health. Ultimately, greater synergy between positive psychology and public health might help promote mental health in innovative ways. PMID:21680918

Impact of High-Temperature, High-Pressure Synthesis Conditions on the Formation of the Grain Structure and Strength Properties of Intermetallic Ni3Al

NASA Astrophysics Data System (ADS)

Ovcharenko, V. E.; Ivanov, K. V.; Boyangin, E. N.; Krylova, T. A.; Pshenichnikov, A. P.

2018-01-01

The impact of the preliminary load on 3Ni+Al powder mixture and the impact of the duration of the delay in application of compacting pressure to synthesis product under the conditions of continuous heating of the mixture up to its self-ignition on the grain size and strength properties of the synthesized Ni3Al intermetallide material have been studied. The grain structure of the intermetallide synthesized under pressure was studied by means of metallography, transmission electron microscopy and EBSD analysis, with the dependence of ultimate tensile strength on the grain size in the synthesized intermetallide having been investigated at room temperature and at temperatures up to 1000°C. It is shown that an increase in the pressure preliminarily applied to the initial mixture compact results in reduced grain size of the final intermetallide, whereas an increase in pre-compaction time makes the grain size increased. A decrease in the grain size increases the ultimate tensile strength of the intermetallide. The maximum value of the ultimate tensile strength in the observed anomalous temperature dependence of this strength exhibits a shift by 200°C toward higher temperatures, and the ultimate strength of the synthesized intermetallide at 1000°C increases roughly two-fold.

Inner strength and its relationship to health threats in ageing-A cross-sectional study among community-dwelling older women.

PubMed

Boman, Erika; Lundman, Berit; Nygren, Björn; Årestedt, Kristofer; Santamäki Fischer, Regina

2017-11-01

To explore the relationship between inner strength and health threats among community-dwelling older women. Inner strength is described as a resource that promotes experiences of health, despite adversities. Inner strength and its dimensions (i.e. connectedness, creativity, firmness and flexibility) can be assessed using the Inner Strength Scale (ISS). Exploring attributes of weaker inner strength may yield valuable information about areas to focus on in enhancing a person's inner strength and may ultimately lead to the perception of better health. Cross-sectional questionnaire survey. The study is based on responses from 1270 community-dwelling older women aged 65 years and older; these were collected in the year 2010 and describe the situation that still exists today for older women. The questionnaire included the ISS, background characteristics and explanatory variables known to be health threats in ageing. Data were analysed using descriptive and inferential statistics. Poorer mental health was related to weaker inner strength in total and in all the dimensions. Symptoms of depressive disorders and feeling lonely were related to three of the dimensions, except firmness and creativity respectively. Furthermore, poor physical health was associated with the dimensions firmness and flexibility. Other health threats were significantly related to only one of the dimensions, or not associated at all. Mental ill health has overall the strongest association with weaker inner strength. Longitudinal studies are recommended to confirm the results. However, the ISS does not only estimate inner strength but can also be a tool for discovering where (i.e. dimension) interventions may be most profitable. © 2017 John Wiley & Sons Ltd.

Ultimate Tensile Strength as a Function of Test Rate for Various Ceramic Matrix Composites at Elevated Temperatures

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Bansal, Narottam P.; Gyekenyesi, John P.

2002-01-01

Ultimate tensile strength of five different continuous fiber-reinforced ceramic composites, including SiC/BSAS (2D 2 types), SiC/MAS-5 (2D), SiC/SiC (2D enhanced), and C/SiC(2D) was determined as a function of test rate at I 100 to 1200 'C in air. All five composite materials exhibited a significant dependency of ultimate strength on test rate such that the ultimate strength decreased with decreasing test rate, similar to the behavior observed in many advanced monolithic ceramics at elevated temperatures. The application of the preloading technique as well as the prediction of life from one loading configuration (constant stress rate) to another (constant stress loading) for SiC/BSAS suggested that the overall macroscopic failure mechanism of the composites would be the one governed by a power-law type of damage evolution/accumulation, analogous to slow crack growth commonly observed in advanced monolithic ceramics.

Associations between aging-related changes in grip strength and cognitive function in older adults: A systematic review.

PubMed

Zammit, Andrea R; Robitaille, Annie; Piccinin, Andrea; Muniz-Terrera, Graciela; Hofer, Scott M

2018-03-08

Grip strength and cognitive function reflect upper body muscle strength and mental capacities. Cross-sectional research has suggested that in old age these two processes are moderately to highly associated, and that an underlying common cause drives this association. Our aim was to synthesize and evaluate longitudinal research addressing whether changes in grip strength are associated with changes in cognitive function in healthy older adults. We systematically reviewed English-language research investigating the longitudinal association between repeated measures of grip strength and of cognitive function in community-dwelling older adults to evaluate the extent to which the two indices decline concurrently. We used four search engines: Embase, PsychINFO, PubMed, and Web of Science. Of 459 unique citations, 6 met our full criteria: 4 studies reported a longitudinal association between rates of change in grip strength and cognitive function in older adults, 2 of which reported the magnitudes of these associations as ranging from low to moderate; 2 studies reported significant cross-sectional but not longitudinal associations among rates of change. All studies concluded that cognitive function and grip strength declined, on average, with increasing age, although with little to no evidence for longitudinal associations among rates of change. Future research is urged to expand the study of physical and cognitive associations in old age using a within-person and multi-study integrative approach to evaluate the reliability of longitudinal results with greater emphasis on the magnitude of this association.

Effects of water during cure on the properties of a carbon/phenolic system

NASA Technical Reports Server (NTRS)

Penn, B. G.; Clemons, J. M.; Ledbetter, F. E., III; Daniels, J. G.; Thompson, L. M.

1984-01-01

The effects of prepreg water contamination on interlaminar shear strength, tranverse compressive strength, and longitudinal compressive strength were determined. Decreases in these properties due to water contamination were sugstantial: 28 percent for the interlaminar shear strength, 21 percent for the transverse compressive strength and 31 percent for the longitudinal compressive strength. Since voids were not detected by X-ray analysis, the most likely cause for these results is fiber-matrix debounding in the laminate.

Ultimate Strength of Ferro-Geopolymer Composite Built-Up I Joist

NASA Astrophysics Data System (ADS)

Vipin, K. T.; Ganesan, N.; Indira, P. V.

2017-07-01

An experimental study was carried out to study the behaviour of ferro-geopolymer built-up I- joist with different types of mesh reinforcements under flexure. Mesh reinforcements considered in this study are square welded meshes, square woven meshes and hexagonal meshes. First crack load as well as ultimate strength of ferro-geopolymer built-up I-joist in flexure was obtained. An attempt was made to predict the first crack load and ultimate moment capacity of the specimen.

Residual Strength Pressure Tests and Nonlinear Analyses of Stringer- and Frame-Stiffened Aluminum Fuselage Panels with Longitudinal Cracks

NASA Technical Reports Server (NTRS)

Young, Richard D.; Rouse, Marshall; Ambur, Damodar R.; Starnes, James H., Jr.

1999-01-01

The results of residual strength pressure tests and nonlinear analyses of stringer- and frame-stiffened aluminum fuselage panels with longitudinal cracks are presented. Two types of damage are considered: a longitudinal crack located midway between stringers, and a longitudinal crack adjacent to a stringer and along a row of fasteners in a lap joint that has multiple-site damage (MSD). In both cases, the longitudinal crack is centered on a severed frame. The panels are subjected to internal pressure plus axial tension loads. The axial tension loads are equivalent to a bulkhead pressure load. Nonlinear elastic-plastic residual strength analyses of the fuselage panels are conducted using a finite element program and the crack-tip-opening-angle (CTOA) fracture criterion. Predicted crack growth and residual strength results from nonlinear analyses of the stiffened fuselage panels are compared with experimental measurements and observations. Both the test and analysis results indicate that the presence of MSD affects crack growth stability and reduces the residual strength of stiffened fuselage shells with long cracks.

Residual Strength Pressure Tests and Nonlinear Analyses of Stringer-and Frame-Stiffened Aluminum Fuselage Panels with Longitudinal Cracks

NASA Technical Reports Server (NTRS)

Young, Richard D.; Rouse, Marshall; Ambur, Damodar R.; Starnes, James H., Jr.

1998-01-01

The results of residual strength pressure tests and nonlinear analyses of stringer- and frame-stiffened aluminum fuselage panels with longitudinal cracks are presented. Two types of damage are considered: a longitudinal crack located midway between stringers, and a longitudinal crack adjacent to a stringer and along a row of fasteners in a lap joint that has multiple-site damage (MSD). In both cases, the longitudinal crack is centered on a severed frame. The panels are subjected to internal pressure plus axial tension loads. The axial tension loads are equivalent to a bulkhead pressure load. Nonlinear elastic-plastic residual strength analyses of the fuselage panels are conducted using a finite element program and the crack-tip-opening-angle (CTOA) fracture criterion. Predicted crack growth and residual strength results from nonlinear analyses of the stiffened fuselage panels are compared with experimental measurements and observations. Both the test and analysis results indicate that the presence of MSD affects crack growth stability and reduces the residual strength of stiffened fuselage shells with long cracks.

Thermal stress effects in intermetallic matrix composites

NASA Technical Reports Server (NTRS)

Wright, P. K.; Sensmeier, M. D.; Kupperman, D. S.; Wadley, H. N. G.

1993-01-01

Intermetallic matrix composites develop residual stresses from the large thermal expansion mismatch (delta-alpha) between the fibers and matrix. This work was undertaken to: establish improved techniques to measure these thermal stresses in IMC's; determine residual stresses in a variety of IMC systems by experiments and modeling; and, determine the effect of residual stresses on selected mechanical properties of an IMC. X ray diffraction (XRD), neutron diffraction (ND), synchrotron XRD (SXRD), and ultrasonics (US) techniques for measuring thermal stresses in IMC were examined and ND was selected as the most promising technique. ND was demonstrated on a variety of IMC systems encompassing Ti- and Ni-base matrices, SiC, W, and Al2O3 fibers, and different fiber fractions (Vf). Experimental results on these systems agreed with predictions of a concentric cylinder model. In SiC/Ti-base systems, little yielding was found and stresses were controlled primarily by delta-alpha and Vf. In Ni-base matrix systems, yield strength of the matrix and Vf controlled stress levels. The longitudinal residual stresses in SCS-6/Ti-24Al-llNb composite were modified by thermomechanical processing. Increasing residual stress decreased ultimate tensile strength in agreement with model predictions. Fiber pushout strength showed an unexpected inverse correlation with residual stress. In-plane shear yield strength showed no dependence on residual stress. Higher levels of residual tension led to higher fatigue crack growth rates, as suggested by matrix mean stress effects.

Effect of a heat treatment on the precipitation behavior and tensile properties of alloy 690 steam generator tubes

NASA Astrophysics Data System (ADS)

Lee, Tae-Hyuk; Suh, Ho-Young; Han, Seul-Ki; Noh, Jae-Soo; Lee, Jong-Hyeon

2016-10-01

The intergranular carbide precipitation behavior and its effect on the tensile properties were investigated in alloy 690. The precipitation of intergranular carbides, identified as Cr-rich M23C6, was retarded on the low-angle grain boundaries and the coincidence-site lattice boundaries. The M23C6 carbides have a cube-cube orientation relationship with the matrix. The ultimate tensile strength, yield strength, and elongation of the solution annealed alloy 690 are 648.2 ± 8.2 MPa, 242.8 ± 10.5 MPa and 44.9 ± 2.3%, respectively. The ultimate tensile strength and the yield strength increased to 764.8 ± 7.8 MPa and 364.8 ± 10.2 MPa until the aging time reached 16 h. This increase is ascribed to the M23C6 carbide acting as reinforcements. However, when the aging time exceed 16 h, these properties gradually decreased with increasing aging time. The decrease in ultimate tensile strength, yield strength, and elongation were mainly caused by the intergranular cracking due to the low bond strength between the carbide and the matrix.

A comparative study to check fracture strength of provisional fixed partial dentures made of autopolymerizing polymethylmethacrylate resin reinforced with different materials: An in vitro study.

PubMed

Gupt, Parikshit; Nagpal, Archana; Samra, Rupandeep Kaur; Verma, Ramit; Kaur, Jasjeet; Abrol, Surbhi

2017-01-01

The purpose of the study was to evaluate the fracture strength of provisional fixed partial dentures made of autopolymerizing polymethylmethacrylate (PMMA) resin using different types of reinforcement materials to determine the best among them. Fifty samples were made (10 samples for each group) with autopolymerizing PMMA resin using reinforcement materials (stainless steel wire: looped and unlooped and glass fiber: loose and unidirectional) as 3-unit posterior bridge. The test specimens were divided into five groups depending on the reinforcing material as Group I, II, III, IV, and V; Group I: PMMA unreinforced (control group), Group II: PMMA reinforced with stainless steel wire (straight ends), Group III: PMMA reinforced with stainless steel wire (looped ends), Group IV: PMMA reinforced with unidirectional glass fibers, and Group V: PMMA reinforced with randomly distributed glass fibers. Universal testing machine was used to evaluate and compare the fracture strength of samples. Comparison of mean ultimate force and ultimate stress was done employing one-way analysis of variance and Tukey's post hoc tests. The highest and lowest mean ultimate force and mean ultimate stress were of Group IV and I, respectively. Tukey's post hoc honestly significant difference multiple comparison for mean ultimate force and stress shows the increase in strength to be statistically significant ( P < 0.05) except for the samples reinforced with randomly distributed glass fibers ( P > 0.05). Unidirectional glass fibers showed the maximum strength, which was comparable to mean values of both stainless steel wire groups. Low cost and easy technique of using stainless steel wire make it the material of choice over the unidirectional glass fiber for reinforcement in nonesthetic areas where high strength is required.

Experimental and analytical investigation of the fracture processes of boron/aluminum laminates containing notches

NASA Technical Reports Server (NTRS)

Johnson, W. S.; Bigelow, C. A.; Bahei-El-din, Y. A.

1983-01-01

Experimental results for five laminate orientations of boron/aluminum composites containing either circular holes or crack-like slits are presented. Specimen stress-strain behavior, stress at first fiber failure, and ultimate strength were determined. Radiographs were used to monitor the fracture process. The specimens were analyzed with a three-dimensional elastic-elastic finite-element model. The first fiber failures in notched specimens with laminate orientation occurred at or very near the specimen ultimate strength. For notched unidirectional specimens, the first fiber failure occurred at approximately one-half of the specimen ultimate strength. Acoustic emission events correlated with fiber breaks in unidirectional composites, but did not for other laminates. Circular holes and crack-like slits of the same characteristic length were found to produce approximately the same strength reduction. The predicted stress-strain responses and stress at first fiber failure compared very well with test data for laminates containing 0 deg fibers.

The Assessment of the Ultimate Hull Girder Strength of RO-RO Ship after Damages

NASA Astrophysics Data System (ADS)

Zubair Muis Alie, Muhammad; Sitepu, Ganding; Izaak Latumahin, Samuel

2018-03-01

Many accidents of Ro-Ro ships happen in Indonesia such as collision and grounding. When the collision or grounding takes place on the Ro-Ro ship, the ultimate strength of hull structure after damage becomes decrease. Car and passenger decks are critical location since collision and/or grounding occur. In the present study, the assessment of the ultimate hull girder strength is conducted. The cross section of Ro-Ro ship is taken to be analyzed. The collision and grounding damages are assumed to be palced on the side and bottom area, respectively. The damages are created by removing the element from the side shell and bottom part. Finally, the result obtained is compared with one another.

The ultimate state of polymeric materials and laminated and fibrous composites under asymmetric high-cycle loading

NASA Astrophysics Data System (ADS)

Golub, V. P.; Pogrebniak, A. D.; Kochetkova, E. S.

2008-01-01

The prediction of the high-cycle fatigue strength of polymeric and composite materials in asymmetric loading is considered. The problem is solved on the basis of a nonlinear model of ultimate state allowing us to describe all typical forms of the diagrams of ultimate stresses. The material constants of the model are determined from the results of fatigue tests in symmetric reversed cycling, in a single fatigue test with the minimum stress equal to zero, and in a short-term strength test. The fatigue strength characteristics of some polymers, glass-fiber laminates, glass-fiber-reinforced plastics, organic-fiber-reinforced plastics, and wood laminates in asymmetric tension-compression, bending, and torsion have been calculated and approved experimentally.

Declines in Strength and Mortality Risk Among Older Mexican Americans: Joint Modeling of Survival and Longitudinal Data.

PubMed

Peterson, Mark D; Zhang, Peng; Duchowny, Kate A; Markides, Kyriakos S; Ottenbacher, Kenneth J; Snih, Soham Al

2016-12-01

Grip strength is a noninvasive method of risk stratification; however, the association between changes in strength and mortality is unknown. The purposes of this study were to examine the association between grip strength and mortality among older Mexican Americans and to determine the ability of changes in strength to predict mortality. Longitudinal data were included from 3,050 participants in the Hispanic Established Population for the Epidemiological Study of the Elderly. Strength was assessed using a hand-held dynamometer and normalized to body mass. Conditional inference tree analyses were used to identify sex- and age-specific weakness thresholds, and the Kaplan-Meier estimator was used to determine survival estimates across various strata. We also evaluated survival with traditional Cox proportional hazard regression for baseline strength, as well as with joint modeling of survival and longitudinal strength change trajectories. Survival estimates were lower among women who were weak at baseline for only 65- to 74-year-olds (11.93 vs 16.69 years). Survival estimates were also lower among men who were weak at baseline for only ≥75-year-olds (5.80 vs 7.39 years). Lower strength at baseline (per 0.1 decrement) was significantly associated with mortality (hazard ratio [HR]: 1.10; 95% confidence interval [CI]: 1.01-1.19) for women only. There was a strong independent, longitudinal association between strength decline and early mortality, such that each 0.10 decrease in strength, within participants over time, resulted in a HR of 1.12 (95% CI: 1.00-1.25) for women and a HR of 1.15 (95% CI: 1.04-1.28) for men. Longitudinal declines in strength are significantly associated with all-cause mortality in older Mexican Americans. © The Author 2016. Published by Oxford University Press on behalf of The Gerontological Society of America. All rights reserved. For permissions, please e-mail: journals.permissions@oup.com.

Fatigue Life of Bovine Meniscus under Longitudinal and Transverse Tensile Loading

PubMed Central

Creechley, Jaremy J.; Krentz, Madison E.; Lujan, Trevor J.

2017-01-01

The knee meniscus is composed of a fibrous matrix that is subjected to large and repeated loads. Consequently, the meniscus is frequently torn, and a potential mechanism for failure is fatigue. The objective of this study was to measure the fatigue life of bovine meniscus when applying cyclic tensile loads either longitudinal or transverse to the principal fiber direction. Fatigue experiments consisted of cyclic loads to 60, 70, 80 or 90% of the predicted ultimate tensile strength until failure occurred or 20,000 cycles was reached. The fatigue data in each group was fit with a Weibull distribution to generate plots of stress level vs. cycles to failure (S-N curve). Results showed that loading transverse to the principal fiber direction gave a two-fold increase in failure strain, a three-fold increase in creep, and a nearly four-fold increase in cycles to failure (not significant), compared to loading longitudinal to the principal fiber direction. The S-N curves had strong negative correlations between the stress level and the mean cycles to failure for both loading directions, where the slope of the transverse S-N curve was 11% less than the longitudinal S-N curve (longitudinal: S=108–5.9ln(N); transverse: S=112–5.2ln(N)). Collectively, these results suggest that the non-fibrillar matrix is more resistant to fatigue failure than the collagen fibers. Results from this study are relevant to understanding the etiology of atraumatic radial and horizontal meniscal tears, and can be utilized by research groups that are working to develop meniscus implants with fatigue properties that mimic healthy tissue. PMID:28088070

Construction strength analysis of landing craft tank conversion to passenger ship using finite element method

NASA Astrophysics Data System (ADS)

Nurul Misbah, Mohammad; Setyawan, Dony; Murti Dananjaya, Wisnu

2018-03-01

This research aims to determine the longitudinal strength of passenger ship which was converted from Landing Craft Tank with 54 m of length as stated by BKI (Biro Klasifikasi Indonesia / Indonesian Classification Bureau). Verification of strength value is done to 4 (four) loading conditions which are (1) empty load condition during sagging wave, (2) empty load condition during hogging wave, (3) full load condition during sagging wave and (4) full load condition during hogging wave. Analysis is done using Finite Element Analysis (FEA) software by modeling the entire part of passenger ship and its loading condition. The back and upfront part of ship centerline were used as the boundary condition. From that analysis it can be concluded that the maximum stress for load condition (1) is 72,393 MPa, 74,792 MPa for load condition (2), 129,92 MPa for load condition (3), and 132,4 MPa for load condition (4). Longitudinal strength of passenger ship fulfilled the criteria of empty load condition having smaller stress value than allowable stress which is 90 MPa, and during full load condition with smaller stress value than allowable stress which is 150 MPa. Analysis on longitudinal strength comparison with entire ship plate thickness variation of ± 2 mm from initial plate was also done during this research. From this research it can be concluded that plate thickness reduction causes the value of longitudinal strength to decrease, while plate thickness addition causes the value of longitudinal strength to increase.

Temperature effects on the mechanical properties of annealed and HERF 304L stainless steel.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Antoun, Bonnie R.

2004-11-01

The effect of temperature on the tensile properties of annealed 304L stainless steel and HERF 304L stainless steel forgings was determined by completing experiments over the moderate range of -40 F to 160 F. Temperature effects were more significant in the annealed material than the HERF material. The tensile yield strength of the annealed material at -40 F averaged twenty two percent above the room temperature value and at 160 F averaged thirteen percent below. The tensile yield strength for the three different geometry HERF forgings at -40 F and 160 F changed less than ten percent from room temperature.more » The ultimate tensile strength was more temperature dependent than the yield strength. The annealed material averaged thirty six percent above and fourteen percent below the room temperature ultimate strength at -40 F and 160 F, respectively. The HERF forgings exhibited similar, slightly lower changes in ultimate strength with temperature. For completeness and illustrative purposes, the stress-strain curves are included for each of the tensile experiments conducted. The results of this study prompted a continuation study to determine tensile property changes of welded 304L stainless steel material with temperature, documented separately.« less

Evaluation of the adhesion on the nano-scaled polymeric film systems.

PubMed

Park, Tae Sung; Park, Ik Keun; Yoshida, Sanichiro

2017-04-01

We applied scanning acoustic microscopy known as the V(z) curve technique to photoresist thin-film systems for the evaluation of the adhesive strength at the film-substrate interface. Through the measurement of the SAW (Surface Acoustic Wave) velocity, the V(z) curve analysis allows us to quantify the stiffness of the film-substrate interface. In addition, we conducted a nano-scratch test to quantify the ultimate strength of the adhesion through the evaluation of the critical load. To vary the adhesive conditions, we prepared thin-film specimens with three different types of pre-coating surface treatments, i.e., oxygen-plasma bombardment, HMDS (Hexametyldisilazane) treatment and untreated. The magnitudes of the quantified stiffness and ultimate strength are found consistent with each other for all the specimens tested, indicating that the pre-coating surface treatment can strengthen both the stiffness and ultimate strength of the adhesion. The results of this study demonstrate the usefulness of the V(Z) analysis as a nondestructive method to evaluate the adhesion strength of nano-structured thin-film systems. Copyright © 2017 Elsevier B.V. All rights reserved.

Strategies for Longitudinal Analysis of the Career Paths of Beginning Teachers: Results from the First through Fourth Waves of the 2007-08 Beginning Teacher Longitudinal Study. Research and Development Report. NCES 2013-336

ERIC Educational Resources Information Center

Gray, Lucinda; Brauen, Marsha

2013-01-01

To learn more about the early career patterns of beginning teachers, the National Center for Education Statistics (NCES) of the Institute of Education Sciences within the U.S. Department of Education undertook the Beginning Teacher Longitudinal Study (BTLS). The ultimate purpose of this report is to develop a strategy for the longitudinal analysis…

Failure Behavior and Strength of Composite I-Section Beam with Double Cutouts and Stiffener Reinforcement

NASA Astrophysics Data System (ADS)

Zhang, Jian; Liu, Wei; Gao, Weicheng

2018-02-01

This work is carried out to study the influence of double cutouts and stiffener reinforcements on the performance of I-section Carbon Fibre/Epoxy composites beam, including buckling, post-buckling behavior and the ultimate failure. The cantilever I-section beam with two diamond-shaped cutouts in the web and three longitudinal L-shaped stiffeners bonded to one side is subjected to a shear load at free end. Both numerical modelling and Experiment of I-section CFRP beam are performed. In numerical analysis, Tsai-Wu failure criterion is utilized to detect the first-ply-failure load in nonlinear analysis by predicting the load-deflection response. Good agreements are obtained from comparison between the numerical simulations and test results. For the double-hole beam web, the two cutouts show close surface deformation amplitude, which indicates that the stiffeners make the force transformation more effective. Comparing to the numerical result of corresponding beam with single cutout and stiffener reinforcement, the longitudinal stiffeners can not only play a significant role in improving the structural stability (increase about 30%), but also take effects to improve the deformation compatibility of structure. Local buckling happened within the sub-webs partioned by the stiffener and the buckling load is different but close. With post-buckling regime, the two areas show similar deformation characteristic, while the sub-web close to fixed end bears more shear load than the sub-web close to loading end with the increase of normal deformation of structure. The catastrophic failure load is approximate 75.6% higher comparing to buckling load. Results illustrate that the tensile fracture of the fiber is the immediate cause of the ultimate failure of the structure.

The strength of polyaxial locking interfaces of distal radius plates.

PubMed

Hoffmeier, Konrad L; Hofmann, Gunther O; Mückley, Thomas

2009-10-01

Currently available polyaxial locking plates represent the consequent enhancement of fixed-angle, first-generation locking plates. In contrast to fixed-angle locking plates which are sufficiently investigated, the strength of the new polyaxial locking options has not yet been evaluated biomechanically. This study investigates the mechanical strength of single polyaxial interfaces of different volar radius plates. Single screw-plate interfaces of the implants Palmar 2.7 (Königsee Implantate und Instrumente zur Osteosynthese GmbH, Allendorf, Germany), VariAx (Stryker Leibinger GmbH & Co. KG, Freiburg, Germany) und Viper (Integra LifeSciences Corporation, Plainsboro, NJ, USA) were tested by cantilever bending. The strength of 0 degrees, 10 degrees and 20 degrees screw locking angle was obtained during static and dynamic loading. The Palmar 2.7 interfaces showed greater ultimate strength and fatigue strength than the interfaces of the other implants. The strength of the VariAx interfaces was about 60% of Palmar 2.7 in both, static and dynamic loading. No dynamic testing was applied to the Viper plate because of its low ultimate strength. By static loading, an increase in screw locking angle caused a reduction of strength for the Palmar 2.7 and Viper locking interfaces. No influence was observed for the VariAx locking interfaces. During dynamic loading; angulation had no influence on the locking strength of Palmar 2.7. However, reduction of locking strength with increasing screw angulation was observed for VariAx. The strength of the polyaxial locking interfaces differs remarkably between the examined implants. Depending on the implant an increase of the screw locking angle causes a reduction of ultimate or fatigue strength, but not in all cases a significant impact was observed.

A Simplified Model for the Effect of Weld-Induced Residual Stresses on the Axial Ultimate Strength of Stiffened Plates

NASA Astrophysics Data System (ADS)

Chen, Bai-Qiao; Guedes Soares, C.

2018-03-01

The present work investigates the compressive axial ultimate strength of fillet-welded steel-plated ship structures subjected to uniaxial compression, in which the residual stresses in the welded plates are calculated by a thermo-elasto-plastic finite element analysis that is used to fit an idealized model of residual stress distribution. The numerical results of ultimate strength based on the simplified model of residual stress show good agreement with those of various methods including the International Association of Classification Societies (IACS) Common Structural Rules (CSR), leading to the conclusion that the simplified model can be effectively used to represent the distribution of residual stresses in steel-plated structures in a wide range of engineering applications. It is concluded that the widths of the tension zones in the welded plates have a quasi-linear behavior with respect to the plate slenderness. The effect of residual stress on the axial strength of the stiffened plate is analyzed and discussed.

Ultimate pier and contraction scour prediction in cohesive soils at selected bridges in Illinois

USGS Publications Warehouse

Straub, Timothy D.; Over, Thomas M.; Domanski, Marian M.

2013-01-01

The Scour Rate In COhesive Soils-Erosion Function Apparatus (SRICOS-EFA) method includes an ultimate scour prediction that is the equilibrium maximum pier and contraction scour of cohesive soils over time. The purpose of this report is to present the results of testing the ultimate pier and contraction scour methods for cohesive soils on 30 bridge sites in Illinois. Comparison of the ultimate cohesive and noncohesive methods, along with the Illinois Department of Transportation (IDOT) cohesive soil reduction-factor method and measured scour are presented. Also, results of the comparison of historic IDOT laboratory and field values of unconfined compressive strength of soils (Qu) are presented. The unconfined compressive strength is used in both ultimate cohesive and reduction-factor methods, and knowing how the values from field methods compare to the laboratory methods is critical to the informed application of the methods. On average, the non-cohesive method results predict the highest amount of scour, followed by the reduction-factor method results; and the ultimate cohesive method results predict the lowest amount of scour. The 100-year scour predicted for the ultimate cohesive, noncohesive, and reduction-factor methods for each bridge site and soil are always larger than observed scour in this study, except 12% of predicted values that are all within 0.4 ft of the observed scour. The ultimate cohesive scour prediction is smaller than the non-cohesive scour prediction method for 78% of bridge sites and soils. Seventy-six percent of the ultimate cohesive predictions show a 45% or greater reduction from the non-cohesive predictions that are over 10 ft. Comparing the ultimate cohesive and reduction-factor 100-year scour predictions methods for each bridge site and soil, the scour predicted by the ultimate cohesive scour prediction method is less than the reduction-factor 100-year scour prediction method for 51% of bridge sites and soils. Critical shear stress remains a needed parameter in the ultimate scour prediction for cohesive soils. The unconfined soil compressive strength measured by IDOT in the laboratory was found to provide a good prediction of critical shear stress, as measured by using the erosion function apparatus in a previous study. Because laboratory Qu analyses are time-consuming and expensive, the ability of field-measured Rimac data to estimate unconfined soil strength in the critical shear–soil strength relation was tested. A regression analysis was completed using a historic IDOT dataset containing 366 data pairs of laboratory Qu and field Rimac measurements from common sites with cohesive soils. The resulting equations provide a point prediction of Qu, given any Rimac value with the 90% confidence interval. The prediction equations are not significantly different from the identity Qu = Rimac. The alternative predictions of ultimate cohesive scour presented in this study assume Qu will be estimated using Rimac measurements that include computed uncertainty. In particular, the ultimate cohesive predicted scour is greater than observed scour for the entire 90% confidence interval range for predicting Qu at the bridges and soils used in this study, with the exception of the six predicted values that are all within 0.6 ft of the observed scour.

Bonding Effectiveness of Luting Composites to Different CAD/CAM Materials.

PubMed

Peumans, Marleen; Valjakova, Emilija Bajraktarova; De Munck, Jan; Mishevska, Cece Bajraktarova; Van Meerbeek, Bart

To evaluate the influence of different surface treatments of six novel CAD/CAM materials on the bonding effectiveness of two luting composites. Six different CAD/CAM materials were tested: four ceramics - Vita Mark II; IPS Empress CAD and IPS e.max CAD; Celtra Duo - one hybrid ceramic, Vita Enamic, and one composite CAD/CAM block, Lava Ultimate. A total of 60 blocks (10 per material) received various mechanical surface treatments: 1. 600-grit SiC paper; 2. sandblasting with 30-μm Al2O3; 3. tribochemical silica coating (CoJet). Subsequent chemical surface treatments involved either no further treatment (control), HF acid etching (HF), silanization (S, or HF acid etching followed by silanization (HF+S). Two specimens with the same surface treatment were bonded together using two dual-curing luting composites: Clearfil Esthetic Cement (self-etching) or Panavia SA Cement (self-adhesive). After 1 week of water storage, the microtensile bond strength of the sectioned microspecimens was measured and the failure mode was evaluated. The bonding performance of the six CAD/CAM materials was significantly influenced by surface treatment (linear mixed models, p < 0.05). The luting cement had a significant influence on bond strength for Celtra Duo and Lava Ultimate (linear mixed models, p < 0.05). Mechanical surface treatment significantly influenced the bond strength for Celtra Duo (p = 0.0117), IPS e.max CAD (p = 0.0115), and Lava Ultimate (p < 0.0001). Different chemical surface treatments resulted in the highest bond strengths for the six CAD/CAM materials: Vita Mark II and IPS Empress CAD: S, HF+S; Celtra Duo: HF, HF+S; IPS e.max CAD: HF+S; Vita Enamic: HF+S, S. For Lava Ultimate, the highest bond strengths were obtained with HF, S, HF+S. Failure analysis showed a relation between bond strength and failure type: more mixed failures were observed with higher bond strengths. Mainly adhesive failures were noticed if no further surface treatment was done. The percentage of adhesive failures was higher for CAD/CAM materials with higher flexural strength (Celtra Duo, IPS e.max CAD, and Lava Ultimate). The bond strength of luting composites to novel CAD/CAM materials is influenced by surface treatment. For each luting composite, an adhesive cementation protocol can be specified in order to obtain the highest bond to the individual CAD/CAM materials.

Sensory and motor peripheral nerve function and longitudinal changes in quadriceps strength.

PubMed

Ward, Rachel E; Boudreau, Robert M; Caserotti, Paolo; Harris, Tamara B; Zivkovic, Sasa; Goodpaster, Bret H; Satterfield, Suzanne; Kritchevsky, Stephen; Schwartz, Ann V; Vinik, Aaron I; Cauley, Jane A; Newman, Anne B; Strotmeyer, Elsa S

2015-04-01

Poor peripheral nerve function is common in older adults and may be a risk factor for strength decline, although this has not been assessed longitudinally. We assessed whether sensorimotor peripheral nerve function predicts strength longitudinally in 1,830 participants (age = 76.3 ± 2.8, body mass index = 27.2 ± 4.6kg/m(2), strength = 96.3 ± 34.7 Nm, 51.0% female, 34.8% black) from the Health ABC study. Isokinetic quadriceps strength was measured semiannually over 6 years. Peroneal motor nerve conduction amplitude and velocity were recorded. Sensory nerve function was assessed with 10-g and 1.4-g monofilaments and average vibration detection threshold at the toe. Lower-extremity neuropathy symptoms were self-reported. Worse vibration detection threshold predicted 2.4% lower strength in men and worse motor amplitude and two symptoms predicted 2.5% and 8.1% lower strength, respectively, in women. Initial 10-g monofilament insensitivity predicted 14.2% lower strength and faster strength decline in women and 6.6% lower strength in men (all p < .05). Poor nerve function predicted lower strength and faster strength decline. Future work should examine interventions aimed at preventing declines in strength in older adults with impaired nerve function. © The Author 2014. Published by Oxford University Press on behalf of The Gerontological Society of America. All rights reserved. For permissions, please e-mail: journals.permissions@oup.com.

Compressive Strength of Notched Poly(Phenylene Sulfide) Aerospace Composite: Influence of Fatigue and Environment

NASA Astrophysics Data System (ADS)

Niitsu, G. T.; Lopes, C. M. A.

2013-08-01

The purpose of this work is to evaluate the influences of fatigue and environmental conditions (-55 °C, 23 °C, and 82 °C/Wet) on the ultimate compression strength of notched carbon-fiber-reinforced poly(phenylene sulfide) composites by performing open-hole compression (OHC) tests. Analysis of the fatigue effect showed that at temperatures of -55 and 23 °C, the ultimate OHC strengths were higher for fatigued than for not-fatigued specimens; this could be attributed to fiber splitting and delamination during fatigue cycling, which reduces the stress concentration at the hole edge, thus increasing the composite strength. This effect of increasing strength for fatigued specimens was not observed under the 82 °C/Wet conditions, since the test temperature near the matrix glass transition temperature ( T g) together with moisture content resulted in matrix softening, suggesting a reduction in fiber splitting during cycling; similar OHC strengths were verified for fatigued and not-fatigued specimens tested at 82 °C/Wet. Analysis of the temperature effect showed that the ultimate OHC strengths decreased with increasing temperature. A high temperature together with moisture content (82 °C/Wet condition) reduced the composite compressive strengths, since a temperature close to the matrix T g resulted in matrix softening, which reduced the lateral support provided by the resin to the 0° fibers, leading to fiber instability failure at reduced applied loads. On the other hand, a low temperature (-55 °C) improved the compressive strength because of possible fiber-matrix interfacial strengthening, increasing the fiber contribution to compressive strength.

Longitudinal Changes in Hip Strength and Range of Motion in Female Youth Soccer Players: Implications for ACL Injury, A Pilot Study.

PubMed

Nguyen, Anh-Dung; Zuk, Emma F; Baellow, Andrea L; Pfile, Kate R; DiStefano, Lindsay J; Boling, Michelle C

2017-09-01

Risk of anterior cruciate ligament (ACL) injuries in young female athletes increases with age, appearing to peak during maturation. Changes in hip muscle strength and range of motion (ROM) during this time may contribute to altered dynamic movement patterns that are known to increase risk of ACL injuries. Understanding the longitudinal changes in hip strength and ROM is needed to develop appropriate interventions to reduce the risk of ACL injuries. To examine the longitudinal changes in hip strength and ROM in female youth soccer players. Longitudinal descriptive study. Field setting. 14 female youth soccer athletes (14.1 ± 1.1 y, 165.8 ± 5.3 cm, 57.5 ± 9.9 kg) volunteered as part of a multiyear risk factor screening project. Clinical measures of hip strength and ROM were collected annually over 3 consecutive years. Passive hip internal rotation (IR), external rotation (ER), abduction (ABD), and adduction (ADD) ROM were measured with a digital inclinometer. Isometric hip ABD and extension (EXT) strength were evaluated using a hand-held dynamometer. Separate repeated-measures ANOVAs compared hip strength and ROM values across 3 consecutive years (P < .05). As youth female soccer players increased in age, there were no changes in normalized hip ABD (P = .830) or EXT strength (P = .062) across 3 consecutive years. Longitudinal changes in hip ROM were observed with increases in hip IR (P = .001) and ABD (P < .001), while hip ADD (P = .009) and ER (P < .001) decreased. Anatomical changes at the hip occur as youth female soccer players increase in age. While there are no changes in hip strength, there is an increase in hip IR and ABD ROM with a concomitant decrease in hip ER and ADD ROM. The resulting asymmetries in hip ROM may decrease the activation and force producing capabilities of the hip muscles during dynamic activities, contributing to altered lower extremity mechanics known to increase the risk of ACL injuries.

Mechanical properties of Ti-6Al-4V specimens produced by shaped metal deposition

PubMed Central

Baufeld, Bernd; van der Biest, Omer

2009-01-01

Shaped metal deposition is a novel technique to build near net-shape components layer by layer by tungsten inert gas welding. Especially for complex shapes and small quantities, this technique can significantly lower the production cost of components by reducing the buy-to-fly ratio and lead time for production, diminishing final machining and preventing scrap. Tensile testing of Ti-6Al-4V components fabricated by shaped metal deposition shows that the mechanical properties are competitive to material fabricated by conventional techniques. The ultimate tensile strength is between 936 and 1014 MPa, depending on the orientation and location. Tensile testing vertical to the deposition layers reveals ductility between 14 and 21%, whereas testing parallel to the layers gives a ductility between 6 and 11%. Ultimate tensile strength and ductility are inversely related. Heat treatment within the α+β phase field does not change the mechanical properties, but heat treatment within the β phase field increases the ultimate tensile strength and decreases the ductility. The differences in ultimate tensile strength and ductility can be related to the α lath size and orientation of the elongated, prior β grains. The micro-hardness and Young’s modulus are similar to conventional Ti-6Al-4V with low oxygen content. PMID:27877271

Molecular-Level Study of the Effect of Prior Axial Compression/Torsion on the Axial-Tensile Strength of PPTA Fibers

NASA Astrophysics Data System (ADS)

Grujicic, M.; Yavari, R.; Ramaswami, S.; Snipes, J. S.; Yen, C.-F.; Cheeseman, B. A.

2013-11-01

A comprehensive all-atom molecular-level computational investigation is carried out in order to identify and quantify: (i) the effect of prior longitudinal-compressive or axial-torsional loading on the longitudinal-tensile behavior of p-phenylene terephthalamide (PPTA) fibrils/fibers; and (ii) the role various microstructural/topological defects play in affecting this behavior. Experimental and computational results available in the relevant open literature were utilized to construct various defects within the molecular-level model and to assign the concentration to these defects consistent with the values generally encountered under "prototypical" PPTA-polymer synthesis and fiber fabrication conditions. When quantifying the effect of the prior longitudinal-compressive/axial-torsional loading on the longitudinal-tensile behavior of PPTA fibrils, the stochastic nature of the size/potency of these defects was taken into account. The results obtained revealed that: (a) due to the stochastic nature of the defect type, concentration/number density and size/potency, the PPTA fibril/fiber longitudinal-tensile strength is a statistical quantity possessing a characteristic probability density function; (b) application of the prior axial compression or axial torsion to the PPTA imperfect single-crystalline fibrils degrades their longitudinal-tensile strength and only slightly modifies the associated probability density function; and (c) introduction of the fibril/fiber interfaces into the computational analyses showed that prior axial torsion can induce major changes in the material microstructure, causing significant reductions in the PPTA-fiber longitudinal-tensile strength and appreciable changes in the associated probability density function.

A uni-extension study on the ultimate material strength and extreme extensibility of atherosclerotic tissue in human carotid plaques.

PubMed

Teng, Zhongzhao; Feng, Jiaxuan; Zhang, Yongxue; Sutcliffe, Michael P F; Huang, Yuan; Brown, Adam J; Jing, Zaiping; Lu, Qingsheng; Gillard, Jonathan H

2015-11-05

Atherosclerotic plaque rupture occurs when mechanical loading exceeds its material strength. Mechanical analysis has been shown to be complementary to the morphology and composition for assessing vulnerability. However, strength and stretch thresholds for mechanics-based assessment are currently lacking. This study aims to quantify the ultimate material strength and extreme extensibility of atherosclerotic components from human carotid plaques. Tissue strips of fibrous cap, media, lipid core and intraplaque hemorrhage/thrombus were obtained from 21 carotid endarterectomy samples of symptomatic patients. Uni-extension test with tissue strips was performed until they broke or slid. The Cauchy stress and stretch ratio at the peak loading of strips broken about 2mm away from the clamp were used to characterize their ultimate strength and extensibility. Results obtained indicated that ultimate strength of fibrous cap and media were 158.3 [72.1, 259.3] kPa (Median [Inter quartile range]) and 247.6 [169.0, 419.9] kPa, respectively; those of lipid and intraplaque hemorrhage/thrombus were 68.8 [48.5, 86.6] kPa and 83.0 [52.1, 124.9] kPa, respectively. The extensibility of each tissue type were: fibrous cap - 1.18 [1.10, 1.27]; media - 1.21 [1.17, 1.32]; lipid - 1.25 [1.11, 1.30] and intraplaque hemorrhage/thrombus - 1.20 [1.17, 1.44]. Overall, the strength of fibrous cap and media were comparable and so were lipid and intraplaque hemorrhage/thrombus. Both fibrous cap and media were significantly stronger than either lipid or intraplaque hemorrhage/thrombus. All atherosclerotic components had similar extensibility. Moreover, fibrous cap strength in the proximal region (closer to the heart) was lower than that of the distal. These results are helpful in understanding the material behavior of atherosclerotic plaques. Copyright © 2015 The Authors. Published by Elsevier Ltd.. All rights reserved.

The Shock Behaviour of a SiO2-Li2O Transparent Glass-Ceramic Armour Material

NASA Astrophysics Data System (ADS)

Pickup, I. M.; Millett, J. C. F.; Bourne, N. K.

2004-07-01

The dynamic behaviour of a transparent glass-ceramic material, Transarm, developed by Alstom UK for the UK MoD has been studied. Plate impact experiments have been used to measure the materials Hugoniot characteristics and failure behaviour. Longitudinal stresses have been measured using embedded and back surface mounted Manganin gauges. Above a threshold stress of ca. 4 GPa, the longitudinal stress histories exhibit a significant secondary rise, prior to attaining their Hugoniot stress. Lateral stresses were also measured by embedding Manganin gauges in longitudinal cuts. Significant secondary rises in stress were observed when the applied longitudinal stress exceeded the 4 GPa threshold, indicating the presence of a failure front. The dynamic shear strength of the glass has been measured using the longitudinal and lateral data. Even though significant strength drops have been measured before and behind the failure front, the material has a high post-failure strength compared to non- crystalline glasses.

The benefits of personal strengths in mental health of stressed students: A longitudinal investigation.

PubMed

Duan, Wenjie

2016-11-01

This study used a two-wave longitudinal research design to explore the role of individual strengths, including interpersonal strength, intellectual strength, and temperance strength, in affecting the mental health of stressed college students. A total of 404 stressed Chinese college students were screened to participate in this 12-month longitudinal study. At the beginning of the study (Time 1), students who had not experienced stressful events within the last 12 months were invited to assess their strengths, psychological well-being, and psychological symptoms. After 12 months (Time 2), 404 students who reported stressful experiences completed the scales again and were retained for the final analyses. Academics-related stressors were the most endorsed life events among college students, whose states of mental health showed downward trends from Time 1 to Time 2. Three strengths had weak to modest correlations to mental health at both Time 1 and Time 2. Although the additional variances of mental health explained by the three strengths were very modest, the mediational roles of the strengths were identified. The perceived stress completely mediated the relationship between the strengths and the psychological symptoms and partly mediated the relationship between the strengths and psychological well-being. Individual strengths may function as a defense against perceived stress and are protective factors of mental health. These strengths maintain mental health by enhancing the psychological well-being and reducing the psychological symptoms of individuals.

On the Contribution of Curl-Free Current Patterns to the Ultimate Intrinsic Signal-to-Noise Ratio at Ultra-High Field Strength.

PubMed

Pfrommer, Andreas; Henning, Anke

2017-05-01

The ultimate intrinsic signal-to-noise ratio (SNR) is a coil independent performance measure to compare different receive coil designs. To evaluate this benchmark in a sample, a complete electromagnetic basis set is required. The basis set can be obtained by curl-free and divergence-free surface current distributions, which excite linearly independent solutions to Maxwell's equations. In this work, we quantitatively investigate the contribution of curl-free current patterns to the ultimate intrinsic SNR in a spherical head-sized model at 9.4 T. Therefore, we compare the ultimate intrinsic SNR obtained with having only curl-free or divergence-free current patterns, with the ultimate intrinsic SNR obtained from a combination of curl-free and divergence-free current patterns. The influence of parallel imaging is studied for various acceleration factors. Moreover results for different field strengths (1.5 T up to 11.7 T) are presented at specific voxel positions and acceleration factors. The full-wave electromagnetic problem is analytically solved using dyadic Green's functions. We show, that at ultra-high field strength (B 0 ⩾7T) a combination of curl-free and divergence-free current patterns is required to achieve the best possible SNR at any position in a spherical head-sized model. On 1.5- and 3T platforms, divergence-free current patterns are sufficient to cover more than 90% of the ultimate intrinsic SNR. Copyright © 2017 John Wiley & Sons, Ltd.

A Guide to Using State Longitudinal Data for Applied Research. NCEE 2015-4013

ERIC Educational Resources Information Center

Levesque, Karen; Fitzgerald, Robert; Pfeiffer, Jay

2015-01-01

State longitudinal data systems (SLDSs) promise a rich source of data for education research. SLDSs contain statewide student data that can be linked over time and to additional data sources for education management, reporting, improvement, and research, and ultimately for informing education policy and practice. Authored by Karen Levesque, Robert…

A mechanical property and stress corrosion evaluation of VIM-ESR-VAR work strengthened and direct double aged Inconel 718 bar material

NASA Technical Reports Server (NTRS)

Montano, J. W.

1986-01-01

Presented are the mechanical properties and the stress corrosion resistance of triple melted vacuum induction melted (VIM), electro-slag remelted (ESR), and vacuum arc remelted (VAR), solution treated, work strengthened and direct double aged Inconel 718 alloy bars 4.00 in. (10.16) and 5.75 in. (14.60 cm) diameter. Tensile, charpy v-notched impact, and compact tension specimens were tested at ambient temperature in both the longitudinal and transverse directions. Longitudinal tensile and yield strengths in excess of 220 ksi (1516.85 MPa) and 200 ksi (1378.00 MPa) respectively, were realized at ambient temperature. Additional charpy impact and compact tension tests were performed at -100 F (-73 C). Longitudinal charpy impact strength equalled or exceeded 12.0 ft-lbs (16.3 Joules) at ambient and at -100 F(-73 C) while longitudinal compact (LC) tension fracture toughness strength remained above 79 ksi (86.80 MPa) at ambient and at -100 F(-73 C) temperatures. No failures occurred in the longitudinal or transverse tensile specimens stressed to 75 and 100 percent of their respective yield strengths and exposed to a salt fog environment for 180 days. Tensile tests performed after the stress corrosion test indicated no mechanical property degradation.

Evaluation of Rhenium Joining Methods

NASA Technical Reports Server (NTRS)

Reed, Brian D.; Morren, Sybil H.

1995-01-01

Coupons of rhenium-to-Cl03 flat plate joints, formed by explosive and diffusion bonding, were evaluated in a series of shear tests. Shear testing was conducted on as-received, thermally-cycled (100 cycles, from 21 to 1100 C), and thermally-aged (3 and 6 hrs at 1100 C) joint coupons. Shear tests were also conducted on joint coupons with rhenium and/or Cl03 electron beam welded tabs to simulate the joint's incorporation into a structure. Ultimate shear strength was used as a figure of merit to assess the effects of the thermal treatment and the electron beam welding of tabs on the joint coupons. All of the coupons survived thermal testing intact and without any visible degradation. Two different lots of as-received, explosively-bonded joint coupons had ultimate shear strengths of 281 and 310 MPa and 162 and 223 MPa, respectively. As-received, diffusion-bonded coupons had ultimate shear strengths of 199 and 348 MPa. For the most part, the thermally-treated and rhenium weld tab coupons had shear strengths slightly reduced or within the range of the as-received values. Coupons with Cl03 weld tabs experienced a significant reduction in shear strength. The degradation of strength appeared to be the result of a poor heat sink provided during the electron beam welding. The Cl03 base material could not dissipate heat as effectively as rhenium, leading to the formation of a brittle rhenium-niobium intermetallic.

Static and dynamic behaviours of railway prestressed concrete sleepers with longitudinal through hole

NASA Astrophysics Data System (ADS)

Ngamkhanong, C.; Kaewunruen, S.; Remennikov, A. M.

2017-10-01

As the crosstie beam in railway track systems, the prestressed concrete sleepers (or railroad ties) are principally designed in order to carry wheel loads from the rails to the ground. Their design takes into account static and dynamic loading conditions. It is evident that prestressed concrete has played a significant role as to maintain the high endurance of the sleepers under low to moderate repeated impact loads. In spite of the most common use of the prestressed concrete sleepers in railway tracks, there have always been many demands from rail engineers to improve serviceability and functionality of concrete sleepers. For example, signalling, fibre optic, equipment cables are often damaged either by ballast corners or by tamping machine. There has been a need to re-design concrete sleeper to cater cables internally so that they would not experience detrimental or harsh environments. Accordingly, this study will investigate the effects of through hole or longitudinal hole on static and dynamic behaviours of concrete sleepers under rail shock loading. The modified compression field theory for ultimate strength design of concrete sleepers will be highlighted in this study. The outcome of this study will enable the new design and calculation methods for prestressed concrete sleepers with holes and web opening that practically benefits civil, track and structural engineers in railway industry.

Social Risk Factors of Black and White Adolescents' Substance Use: The Differential Role of Siblings and Best Friends.

PubMed

Rowan, Zachary R

2016-07-01

Efforts to understand peer influence among adolescents have established the robust relationship between having substance using peers and future substance use. Still, research suggests that peer influence affects different types of adolescents in different ways. Black adolescents may be less susceptible to friends compared to white adolescents and possess stronger family-orientation, suggesting that siblings may affect deviance of Black adolescents whereas friends will have a minimal impact. This study used data from the first two waves of the National Longitudinal Study of Adolescent to Adult Health to evaluate the relative strength of best friend and siblings' influence as risk factors for Black and White adolescents' alcohol and cigarette use. Approximately 182 Black sibling pairs (37 % male) and 657 white sibling pairs (46 % male) that ranged in ages from 11 to 19 were in the longitudinal analyses for the current study. The findings demonstrated that sibling and best friends' substance use explained white adolescents' cigarette and alcohol use, whereas Black adolescents' cigarette and alcohol use was predominantly explained by siblings' substance use. Ultimately, the results indicated the nuanced role that two types of peers have in explaining variation in substance use across Black and White adolescents.

A unified approach for determining the ultimate strength of RC members subjected to combined axial force, bending, shear and torsion

PubMed Central

Huang, Zhen

2017-01-01

This paper uses experimental investigation and theoretical derivation to study the unified failure mechanism and ultimate capacity model of reinforced concrete (RC) members under combined axial, bending, shear and torsion loading. Fifteen RC members are tested under different combinations of compressive axial force, bending, shear and torsion using experimental equipment designed by the authors. The failure mechanism and ultimate strength data for the four groups of tested RC members under different combined loading conditions are investigated and discussed in detail. The experimental research seeks to determine how the ultimate strength of RC members changes with changing combined loads. According to the experimental research, a unified theoretical model is established by determining the shape of the warped failure surface, assuming an appropriate stress distribution on the failure surface, and considering the equilibrium conditions. This unified failure model can be reasonably and systematically changed into well-known failure theories of concrete members under single or combined loading. The unified calculation model could be easily used in design applications with some assumptions and simplifications. Finally, the accuracy of this theoretical unified model is verified by comparisons with experimental results. PMID:28414777

Gifted Girls and Nonmathematical Aspirations: A Longitudinal Case Study of Two Gifted Korean Girls

ERIC Educational Resources Information Center

Lee, Kyeong Hwa; Sriraman, Bharath

2012-01-01

In this longitudinal study of two gifted Korean girls, experiences with early admittance into a gifted program are charted alongside their family and societal experiences that ultimately influenced their career choices in nonmathematical fields. The 8-year-long qualitative study involved extensive interviews with the two gifted girls and their…

75 FR 27584 - Notice of Availability of Funds and Solicitation for Grant Applications (SGA) to Fund...

Federal Register 2010, 2011, 2012, 2013, 2014

2010-05-17

... be used to design and develop workforce data systems that are longitudinal and which are designed to... is explained in detail in Section IV of this SGA. A pre-recorded Webinar for prospective applicants... ultimately create longitudinal data systems with individual-level information from pre-kindergarten (pre-K...

The added value of measuring thumb and finger strength when comparing strength measurements in hypoplastic thumb patients.

PubMed

Molenaar, H M Ties; Selles, Ruud W; de Kraker, Marjolein; Stam, Henk J; Hovius, Steven E R

2013-10-01

When interventions to the hand are aimed at improving function of specific fingers or the thumb, the RIHM (Rotterdam Intrinsic Hand Myometer) is a validated tool and offers more detailed information to assess strength of the involved joints besides grip and pinch measurements. In this study, strength was measured in 65 thumbs in 40 patients diagnosed with thumb hypoplasia. These 65 thumbs were classified according to Blauth. Longitudinal radial deficiencies were also classified. The strength measurements comprised of grip, tip, tripod and key pinch. Furthermore palmar abduction and opposition of the thumb as well as abduction of the index and little finger were measured with the RIHM. For all longitudinal radial deficiency patients, grip and pinch strength as well as palmar abduction and thumb opposition were significantly lower than reference values (P<0.001). However, strength in the index finger abduction and the little finger abduction was maintained or decreased to a lesser extent according to the degree of longitudinal radial deficiency. All strength values decreased with increasing Blauth-type. Blauth-type II hands (n=15) with flexor digitorum superficialis 4 opposition transfer including stabilization of the metacarpophalangeal joint showed a trend toward a higher opposition strength without reaching statistical significance (P=0.094),however compared to non-operated Blauth-type II hands (n=6) they showed a lower grip strength (P=0.019). The RIHM is comparable in accuracy to other strength dynamometers. Using the RIHM, we were able to illustrate strength patterns on finger-specific level, showing added value when evaluating outcome in patients with hand related problems. © 2013.

Effect of Strain Rate on Mechanical Properties of Wrought Sintered Tungsten at Temperatures above 2500 F

NASA Technical Reports Server (NTRS)

Sikora, Paul F.; Hall, Robert W.

1961-01-01

Specimens of wrought sintered commercially pure tungsten were made from 1/8-inch swaged rods. All the specimens were recrystallized at 4050 F for 1 hour prior to testing at temperatures from 2500 to 4000 F at various strain rates from 0.002 to 20 inches per inch per minute. Results showed that, at a constant temperature, increasing the strain rate increased the ultimate tensile strength significantly. The effects of both strain rate and temperature on the ultimate tensile strength of tungsten may be correlated by the linear parameter method of Manson and Haferd and may be used to predict the ultimate tensile strength at higher temperatures, 4500 and 5000 F. As previously reported, ductility, as measured by reduction of area in a tensile test, decreases with increasing temperature above about 3000 F. Increasing the strain rate at temperatures above 3000 F increases the ductility. Fractures are generally transgranular at the higher strain rates and intergranular at the lower strain rates.

Data of the properties of rebar steel brands in Lagos, Nigerian market used in reinforced concrete applications.

PubMed

Joshua, Opeyemi; Olusola, Kolapo O; Oyeyemi, Kehinde D; Ogunde, Ayodeji O; Amusan, Lekan M; Nduka, David O; Abuka-Joshua, Joyce

2018-04-01

The data presented herein are compilations of the research summary of "Assessment of the Quality of Steel Reinforcement Bars Available in Nigerian Market" (Joshua et al., 2013) [1]. This data article provides information on the properties and cost of steel rebars used in reinforced concrete in Lagos, Nigeria. The data is based on the properties of 12 mm rebar brands which are the most used steel diameter in construction and they include actual diameters, yield strengths, ultimate strengths, ultimate/yield strength ratio, ductility and the cost of each brand. This data also contains the limiting standard properties of the highlighted properties in this data.

Study on the Connecting Length of CFRP

NASA Astrophysics Data System (ADS)

Liu, Xiongfei; Li, Yue; Li, Zhanguo

2018-05-01

The paper studied the varying mode of shear stress in the connecting zone of CFRP. Using epoxy resin (EP) as bond material, performance of specimens with different connecting length of CFRP was tested to obtain the conclusion. CFRP-confined concrete column was tested subsequently to verify the conclusion. The results show that: (1) The binding properties of modified epoxy resin with CFRP is good; (2) As the connecting length increased, the ultimate tensile strength of CFRP increased as well in the range of the experiment parameters; (3) Tensile strength of CFRP can reach the ultimate strength when the connecting length is 90mm;(4) The connecting length of 90mm of CFRP meet the reinforcement requirements.

Ultimate strength capacity of a square hollow section filled with fibrous foamed concrete

NASA Astrophysics Data System (ADS)

Amirah Azra Khairuddin, Siti; Rahman, Norashidah Abd; Jamaluddin, Norwati; Jaini, Zainorizuan Mohd; Ali, Noorwirdawati

2017-11-01

Concrete-filled sections used as building columns have become popular due to their architectural and structural elements. In recent years, there has been a renewed call for the improvement of materials used as concrete to fill the composite columns. Among these materials, foamed concrete has received great attention due to its structural characteristics and its potential as a construction material used in hollow sections. However, its behaviors as infill material in a hollow section, such as its strength and failure mode, should be investigated. In this study, experimental research was conducted to compare the experimental and theoretical values of its ultimate strength capacity. Eight specimens of hollow steel sections with two different thicknesses were filled with fibrous foamed concrete and then subjected to compression load. The obtained results were compared with those obtained from a hollow section with the same thicknesses, but were filled with normal foamed concrete. Results show that the ultimate strength capacity of the experimental value is the same as that of the theoretical value based on Eurocode 4. The largest percentage values between theoretical and experimental results for thicknesses of 2 and 4 mm are 58% and 55%, respectively.

Acoustic emission analysis of fiber-reinforced composite in flexural testing.

PubMed

Alander, Pasi; Lassila, Lippo V J; Tezvergil, Arzu; Vallittu, Pekka K

2004-05-01

The aim of this study was to examine the emission of acoustic signals from six commercially available fiber-reinforced composites (FRC) used in the frameworks of fixed partial dentures in material bending. FRC test specimens were made of six commercially available fiber products of polyethylene or glass and five light-curing resins. FRC test specimens were polymerized with a hand light-curing unit or with a light-curing oven. The flexural test for determination of ultimate flexural strength of test specimens (n = 6) was based on the ISO 10477 standard after the specimens were stored in air or in water for two weeks. The acoustic emission (AE) signals were monitored during three-point loading test of the test specimens using a test with increasing loading levels until the specimens fractured. Generally, stress level required for the AE activity initiation ranged from 107 MPa (Ribbond) to 579 MPa (everStick). The ultimate flexural strength of FRC specimens were higher, ranging from 132 to 764 MPa, being highest with everStick and Vectris FRC, and lowest with Ribbond FRC. ANOVA showed a statistically significant difference between the initiation of AE activity and the ultimate flexural strength according to the brand (p < 0.001) storing conditions (p < 0.001) and polymerization procedure (p < 0.001). AE activity and ultimate flexural strength correlated significantly (p < 0.010, r = 0.887). The result of this study suggested that AE activity in FRC specimens started at a 19-32% lower stress level than occurred at final fracture.

Design variables for mechanical properties of bone tissue scaffolds.

PubMed

Howk, Daniel; Chu, Tien-Min G

2006-01-01

The reconstruction of segmental defect in long bone is a clinical challenge. Multiple surgeries are typically required to restore the structure and function of the affected defect site. In order to overcome this defect a biodegradable bone tissue engineering scaffold is used. This scaffold acts as a carrier of proteins and growth factors, while also supporting the load that the bone would normally sustain, until the natural bone can regenerate in its place. Work was done to optimize an existing solid free-form scaffold design. The goal of the optimization was to increase the porosity of the scaffold while maintaining the strength of a previously-tested prototype design. With this in mind, eight new designs were created. These designs were drawn using CAD software and then through the use of finite element analysis the theoretical ultimate compressive strength of each design was obtained. Each scaffold design was constructed by casting a thermal-curable poly(propylene fumarate)/tricalcium phosphate (PPF/TCP) suspension into wax molds fabricated on inkjet printing rapid prototyping machine. The constructs were then experimentally tested by applying a uniaxial compressive load. The theoretical and experimental values of ultimate compressive strength and specific strength of each design were compared. Theoretically, the best scaffold design produced from this work improved upon the current design by increasing the porosity by 46% and also increasing the ultimate compressive strength by 27%. The experimental data was found to match the theoretical strength in four designs, but deviate from the theoretical strength in five designs. The reasons for the deviations and their relation to the rapid prototyping manufacturing technique were discussed. The results of this work show that it is possible to increase the porosity and strength of a bone tissue engineering scaffold through simple iterations in architectural design.

Shear strength of fillet welds in aluminum alloy 2219. [for use on the solid rocket motor and external tank

NASA Technical Reports Server (NTRS)

Lovoy, C. V.

1978-01-01

Fillet size is discussed in terms of theoretical or design dimensions versus as-welded dimensions, drawing attention to the inherent conservatism in the design load sustaining capabilities of fillet welds. Emphasis is placed on components for the solid rocket motor, external tank, and other aerospace applications. Problems associated with inspection of fillet welds are addresses and a comparison is drawn between defect counts obtained by radiographic inspection and by visual examination of the fracture plane. Fillet weld quality is related linearly to ultimate shear strength. Correlation coefficients are obtained by simple straight line regression analysis between the variables of ultimate shear strength and accumulative discontinuity summation. Shear strength allowables are found to be equivalent to 57 percent of butt weld A allowables (F sub tu.)

The effects of embedded piezoelectric fiber composite sensors on the structural integrity of glass-fiber-epoxy composite laminate

NASA Astrophysics Data System (ADS)

Konka, Hari P.; Wahab, M. A.; Lian, K.

2012-01-01

Piezoelectric fiber composite sensors (PFCSs) made from micro-sized lead zirconate titanate (PZT) fibers have many advantages over the traditional bulk PZT sensors for embedded sensor applications. PFCSs as embedded sensors will be an ideal choice to continuously monitor the stress/strain levels and health conditions of composite structures. PFCSs are highly flexible, easily embeddable, have high compatibility with composite structures, and also provides manufacturing flexibility. This research is focused on examining the effects of embedding PFCS sensors (macro-fiber composite (MFC) and piezoelectric fiber composite (PFC)) on the structural integrity of glass-fiber-epoxy composite laminates. The strengths of composite materials with embedded PFCSs and conventional PZT sensors were compared, and the advantages of PFCS sensors over PZTs were demonstrated. Initially a numerical simulation study is performed to understand the local stress/strain field near the embedded sensor region inside a composite specimen. High stress concentration regions were observed near the embedded sensor corner edge. Using PFCS leads to a reduction of 56% in longitudinal stress concentration and 38% in transverse stress concentration, when compared to using the conventional PZTs as embedded sensors. In-plane tensile, in-plane tension-tension fatigue, and short beam strength tests are performed to evaluate the strengths/behavior of the composite specimens containing embedded PFCS. From the tensile test it is observed that embedding PFCS and PZT sensors in the composite structures leads to a reduction in ultimate strength by 3 and 6% respectively. From the fatigue test results it is concluded that both embedded PFCS and PZT sensors do not have a significant effect on the fatigue behavior of the composite specimens. From the short beam strength test it is found that embedding PFCS and PZT sensors leads to a reduction in shear strength by 7 and 15% respectively. Overall the pure PZT sensors seem to have low compatibility with composites when compared to PFCSs.

Effects of joint configuration for the arc welding of cast Ti-6Al-4V alloy rods in argon.

PubMed

Taylor, J C; Hondrum, S O; Prasad, A; Brodersen, C A

1998-03-01

Titanium and its alloys are more commonly used in prosthodontics and welding has become the most common modality for their joining. Studies on the welding of titanium and its alloys have not quantified this value, though its importance has been suggested. This study compared the strength and properties of the joint achieved at various butt joint gaps by the arc-welding of cast Ti-6Al-4V alloy tensile bars in an argon atmosphere. Forty of 50 specimens were sectioned and welded at four gaps. All specimens underwent tensile testing to determine ultimate tensile strength and percentage elongation, then oxygen analysis and scanning electron microscopy. As no more than 3 samples in any group of 10 actually fractured in the weld itself, a secondary analysis that involved fracture location was initiated. There were no differences in ultimate tensile strength or percentage elongation between specimens with weld gaps of 0.25, 0.50, 0.75, and 1.00 mm and the as-cast specimens. There were no differences in ultimate tensile strength between specimens fracturing in the weld and those fracturing in the gauge in welded specimens; however, as-cast specimens demonstrated a higher ultimate tensile strength than welded specimens that fractured in the weld. Specimens that fractured in the weld site demonstrated less ductility than those that fractured in the gauge in both welded and as-cast specimens, as confirmed by scanning electron microscopy examination. The weld wire showed an oxygen scavenging effect from the as-cast parent alloy. The effects of the joint gap were not significant, whereas the characteristics of the joint itself were, which displayed slightly lower strength and significantly lower ductility (and thus decreased toughness). The arc-welding of cast titanium alloy in argon atmosphere appears to be a reliable and efficient prosthodontic laboratory modality producing predictable results, although titanium casting and joining procedures must be closely controlled to minimize heat effects and oxygen contamination.

Increase in Ductility of High Carbon Steel Due to Accelerated Precipitation of Cementite

NASA Astrophysics Data System (ADS)

Ali, Muhammad; UlHaq, Ehsan; Ibrahim, Ather; Abdul Karim, Muhammad Ramzan; Ali, A.; Fayyaz, M.; Khera, F. K.

2017-09-01

Eutectoid steel AISI 1080 is studied after annealing at 850°C and thermal cycling treatment (TCT) that involves heating at a rate of 10 K/min to 775°C, holding for 10 min, and cooling at a rate of 95 K/min. An increase is established in the content of cementite precipitating over austenite grain boundaries, and relative elongation with retention of yield and ultimate strengths with an increase in number of TCT cycles. After five cycles relative elongation reaches 29% with ultimate strength of 670 MPa.

FE Analysis of Buckling Behavior Caused by Welding in Thin Plates of High Tensile Strength Steel

NASA Astrophysics Data System (ADS)

Wang, Jiangchao; Rashed, Sherif; Murakawa, Hidekazu

2014-12-01

The target of this study was to investigate buckling behavior during the entire welding process which consists of the heating and the cooling processes. For thin plate structures made of high tensile strength steel, not only residual buckling during or after cooling down but also transient buckling during heating may occur. The thermal elastic plastic FE analysis to investigate welding-induced buckling during the entire welding process is presented. Because of the high yield stress of high tensile strength steel, larger longitudinal compressive thermal stress is produced near the welding line compared with that in the case of carbon steel. Therefore, the plate may buckle due to thermal expansion, before the material nears yielding. During cooling down, the longitudinal compressive thermal stress close to the welding line disappears, and longitudinal tensile residual stress is produced due to contraction. Meanwhile, longitudinal compressive residual stress occurs far from the welding line to balance the tensile stress close to the welding line. This distribution of longitudinal residual stress would change the deformed dish shape of transient buckling into a saddle buckling type when the stress exceeds the critical buckling condition.

Size effects on elasticity, yielding, and fracture of silver nanowires: In situ experiments

NASA Astrophysics Data System (ADS)

Zhu, Yong; Qin, Qingquan; Xu, Feng; Fan, Fengru; Ding, Yong; Zhang, Tim; Wiley, Benjamin J.; Wang, Zhong Lin

2012-01-01

This paper reports the quantitative measurement of a full spectrum of mechanical properties of fivefold twinned silver (Ag) nanowires (NWs), including Young's modulus, yield strength, and ultimate tensile strength. In-situ tensile testing of Ag NWs with diameters between 34 and 130 nm was carried out inside a scanning electron microscope (SEM). Young's modulus, yield strength, and ultimate tensile strength all increased as the NW diameter decreased. The maximum yield strength in our tests was found to be 2.64 GPa, which is about 50 times the bulk value and close to the theoretical value of Ag in the 110 orientation. The size effect in the yield strength is mainly due to the stiffening size effect in the Young's modulus. Yield strain scales reasonably well with the NW surface area, which reveals that yielding of Ag NWs is due to dislocation nucleation from surface sources. Pronounced strain hardening was observed for most NWs in our study. The strain hardening, which has not previously been reported for NWs, is mainly attributed to the presence of internal twin boundaries.

Indirect and direct tensile behavior of Devonian oil shales

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chong, K.P.; Chen, J.L.; Dana, G.F.

1984-03-01

Ultimate indirect tensile strengths of Devonian oil shales across the bedding planes is a mechanical property parameter important to predicting how oil shale will break. This is particularly important to in-situ fragmentation. The Split Cylinder Test was used to determine the indirect tensile strengths between the bedding planes. Test specimens, cored perpendicular to the bedding planes, representing oil shales of different oil yields taken from Silver Point Quad in DeKalb County, Tennessee and Friendship in Scioto County, Ohio, were subjected to the Split Cylinder Test. Linear regression equations relating ultimate tensile strength across the bedding planes to volume percent ofmore » organic matter in the rock were developed from the test data. In addition, direct tensile strengths were obtained between the bedding planes for the Tennessee oil shales. This property is important for the design of horizontal fractures in oil shales. Typical results were presented.« less

Interlaboratory study for nickel alloy 625 made by laser powder bed fusion to quantify mechanical property variability.

PubMed

Brown, Christopher U; Jacob, Gregor; Stoudt, Mark; Moylan, Shawn; Slotwinski, John; Donmez, Alkan

2016-08-01

Six different organizations participated in this interlaboratory study to quantify the variability in the tensile properties of Inconel 625 specimens manufactured using laser-powder-bed-fusion additive manufacturing machines. The tensile specimens were heat treated and tensile tests conducted until failure. The properties measured were yield strength, ultimate tensile strength, elastic modulus, and elongation. Statistical analysis revealed that between-participant variability for yield strength, ultimate tensile strength, and elastic modulus values were significantly higher (up to 4 times) than typical within-participant variations. Only between-participant and within-participant variability were both similar for elongation. A scanning electron microscope was used to examine one tensile specimen for fractography. The fracture surface does not have many secondary cracks or other features that would reduce the mechanical properties. In fact, the features largely consist of microvoid coalescence and are entirely consistent with ductile failure.

Effect of heat treatment on microstructure and mechanical properties of Mg-4Y-1.6Nd-1Sm-0.5Zr alloy

NASA Astrophysics Data System (ADS)

Jia, Guilong; Guo, Erjun; Feng, Yicheng; Wang, Liping; Wang, Changliang

2018-03-01

Microstructure and mechanical properties of Mg-4Y-1.6Nd-1Sm-0.5Zr alloy during heat treatments were investigated, while the room-temperature tensile fractographs were observed and analyzed. The results show that the eutectic phases almost dissolve into the matrix after being solutionized at 525 °C for 8 h. The ultimate tensile strength, yield strength and elongation reach 300 MPa, 219 MPa, 6.5% respectively after being under-aged at 200 °C for 16 h. The ultimate tensile strength and yield strength of the alloy decrease gradually, while the elongation increases gradually with increasing the test temperatures. The room-temperature tensile fracture modes of the as-cast alloy, solutionized alloy, aged alloy are mixed fracture of transgranular and intergranular, transgranular cleavage fracture, transgranular fracture, respectively.

Interlaboratory study for nickel alloy 625 made by laser powder bed fusion to quantify mechanical property variability

PubMed Central

Brown, Christopher U.; Jacob, Gregor; Stoudt, Mark; Moylan, Shawn; Slotwinski, John; Donmez, Alkan

2017-01-01

Six different organizations participated in this interlaboratory study to quantify the variability in the tensile properties of Inconel 625 specimens manufactured using laser-powder-bed-fusion additive manufacturing machines. The tensile specimens were heat treated and tensile tests conducted until failure. The properties measured were yield strength, ultimate tensile strength, elastic modulus, and elongation. Statistical analysis revealed that between-participant variability for yield strength, ultimate tensile strength, and elastic modulus values were significantly higher (up to 4 times) than typical within-participant variations. Only between-participant and within-participant variability were both similar for elongation. A scanning electron microscope was used to examine one tensile specimen for fractography. The fracture surface does not have many secondary cracks or other features that would reduce the mechanical properties. In fact, the features largely consist of microvoid coalescence and are entirely consistent with ductile failure. PMID:28243032

Interlaboratory Study for Nickel Alloy 625 Made by Laser Powder Bed Fusion to Quantify Mechanical Property Variability

NASA Astrophysics Data System (ADS)

Brown, Christopher U.; Jacob, Gregor; Stoudt, Mark; Moylan, Shawn; Slotwinski, John; Donmez, Alkan

2016-08-01

Six different organizations participated in this interlaboratory study to quantify the variability in the tensile properties of Inconel 625 specimens manufactured using laser powder bed fusion-additive manufacturing machines. The tensile specimens were heat treated and tensile tests were conducted until failure. The properties measured were yield strength, ultimate tensile strength, elastic modulus, and elongation. Statistical analysis revealed that between-participant variability for yield strength, ultimate tensile strength, and elastic modulus values were significantly higher (up to four times) than typical within-participant variations. Only between-participant and within-participant variability were both similar for elongation. A scanning electron microscope was used to examine one tensile specimen for fractography. The fracture surface does not have many secondary cracks or other features that would reduce the mechanical properties. In fact, the features largely consist of microvoid coalescence and are entirely consistent with ductile failure.

Development of Laser Fabricated Ti-6Al-4V

NASA Technical Reports Server (NTRS)

deGroh, Henry C., III

2006-01-01

Laser Engineered Net Shaping (LENS) depositions with Ti-6Al-4V gas-atomized powder were accomplished at five different temperatures, ranging from 30 to 400 C, imposed on the base plate. These base plate temperatures were employed in an effort to relieve stresses which develop during the deposition. Warpage of the base plate was monitored. Only a slight decline in warpage was observed as the base plate temperature was increased. Results indicate that substrate temperatures closer to the stress relief minimum of 480 C would relieve deposition stresses, though process parameters would likely need to be modified to compensate for the higher base plate temperature. The compositions of the as-received powder and the LENS deposited material were chemically analyzed. The oxygen content of the LENS material was 0.154 wt.% which is less than the maximum impurity limit of 0.2 percent for commercial Ti-6Al-4V alloys, but is over the limit allowed in ELI grade (0.13 percent). The level of oxygen in the commercial base plate used was only 0.0635 percent. Tensile specimens were machined from the LENS deposited material and tested in tension at room temperature. The ultimate and yield tensile stresses of the LENS material were about 1200 and 1150 MPa respectively, which is about 20 percent higher than the strengths of wrought Ti-6Al-4V. The higher strength of the LENS material was due to its fine structure and high oxygen content. The LENS deposits were not fully dense; voids were frequent at the interfaces between deposited layers. These dispersed sheets of voids were parallel to the longitudinal axis of the resulting tensile specimens. Apparently there was sufficient continuous, fully dense material longitudinally to enable the high strengths. Ductility was low in the LENS material. Percent elongation at failure in the LENS material was near 4 percent, which is less than half of what is usually expected from Ti-6Al-4V. The low ductility was caused by high oxygen levels, and the presence of voids. It is likely that the relatively high scan speeds used in our depositions contributed to the lack of full density in our LENS material.

Evaluation of the tensile strength of the human ureter - Preliminary results.

PubMed

Shilo, Yaniv; Pichamuthu, Joseph E; Averch, Timothy D; Vorp, David A

2014-09-15

Introduction: Ureteral injuries such as avulsion are directly related to mechanical damage of the ureter. Understanding the tensile strength of this tissue may assist in prevention of iatrogenic injuries. Few published studies have looked at the mechanical properties of the animal ureter, and of those none have determined the tensile strength of the human ureter. Therefore, the purpose of this work was to determine the tensile strength of the human ureter. Materials and Methods: We harvested 11 human proximal ureters from patients who were undergoing nephrectomy for either kidney tumors or non-functioning kidney. The specimens were then cut into multiple circumferentially and longitudinally-oriented tissue strips for tensile testing. Strips were uniaxially stretched to failure in a tensile testing machine. The corresponding force and displacement were recorded. Finally, stress at failure was noted as the tensile strength of the sample. Circumferential tensile strength was also compared in the proximal and distal regions of the specimens. Results: The tensile strength of the ureter in circumferential and longitudinal orientations was found to be 457.52±33.74 Ncm-2 and 902.43±122.08 Ncm-2, respectively (p<0.001). The circumferential strength in the proximal portion of the ureter was 409.89±35.13 Ncm-2 in comparison to 502.89±55.85 Ncm-2 in the distal portion (p=0.08). Conclusions: The circumferential tensile strength of the ureter was found to be significantly lower than the longitudinal strength. Circumferential tensile strength was also lower with more proximal parts of the ureter. This information may be important for the design of "intelligent" devices and simulators in order to prevent complications.

Evaluation of the tensile strength of the human ureter--preliminary results.

PubMed

Shilo, Yaniv; Pichamuthu, Joseph E; Averch, Timothy D; Vorp, David A

2014-12-01

Ureteral injuries such as avulsion are directly related to mechanical damage of the ureter. Understanding the tensile strength of this tissue may assist in prevention of iatrogenic injuries. Few published studies have looked at the mechanical properties of the animal ureter and, of those, none has determined the tensile strength of the human ureter. Therefore, the purpose of this work was to determine the tensile strength of the human ureter. We harvested 11 human proximal ureters from patients who were undergoing nephrectomy for either kidney tumors or nonfunctioning kidney. The specimens were then cut into multiple circumferentially and longitudinally oriented tissue strips for tensile testing. Strips were uniaxially stretched to failure in a tensile testing machine. The corresponding force and displacement were recorded. Finally, stress at failure was noted as the tensile strength of the sample. Circumferential tensile strength was also compared in the proximal and distal regions of the specimens. The tensile strength of the ureter in circumferential and longitudinal orientations was found to be 457.52±33.74 Ncm(-2) and 902.43±122.08 Ncm(-2), respectively (P<0.001). The circumferential strength in the proximal portion of the ureter was 409.89±35.13 Ncm(-2) in comparison with 502.89±55.85 Ncm(-2) in the distal portion (P=0.08). The circumferential tensile strength of the ureter was found to be significantly lower than the longitudinal strength. Circumferential tensile strength was also lower with more proximal parts of the ureter. This information may be important for the design of "intelligent" devices and simulators to prevent complications.

Fabrication and Analysis of the Wear Properties of Hot-Pressed Al-Si/SiCp + Al-Si-Cu-Mg Metal Matrix Composite

NASA Astrophysics Data System (ADS)

Bang, Jeongil; Oak, Jeong-Jung; Park, Yong Ho

2016-01-01

The aim of this study was to characterize microstructures and mechanical properties of aluminum metal matrix composites (MMC's) prepared by powder metallurgy method. Consolidation of mixed powder with gas atomized Al-Si/SiCp powder and Al-14Si-2.5Cu-0.5Mg powder by hot pressing was classified according to sintering temperature and sintering time. Sintering condition was optimized using tensile properties of sintered specimens. Ultimate tensile strength of the optimized sintered specimen was 228 MPa with an elongation of 5.3% in longitudinal direction. In addition, wear properties and behaviors of the sintered aluminum-based MMC's were analyzed in accordance with vertical load and linear speed. As the linear speed and vertical load of the wear increased, change of the wear behavior occurred in order of oxidation of Al-Si matrix, formation of C-rich layer, Fe-alloying to matrix, and melting of the specimen

Behavior of Tilted Angle Shear Connectors

PubMed Central

Khorramian, Koosha; Maleki, Shervin; Shariati, Mahdi; Ramli Sulong, N. H.

2015-01-01

According to recent researches, angle shear connectors are appropriate to transfer longitudinal shear forces across the steel-concrete interface. Angle steel profile has been used in different positions as L-shaped or C-shaped shear connectors. The application of angle shear connectors in tilted positions is of interest in this study. This study investigates the behaviour of tilted-shaped angle shear connectors under monotonic loading using experimental push out tests. Eight push-out specimens are tested to investigate the effects of different angle parameters on the ultimate load capacity of connectors. Two different tilted angles of 112.5 and 135 degrees between the angle leg and steel beam are considered. In addition, angle sizes and lengths are varied. Two different failure modes were observed consisting of concrete crushing-splitting and connector fracture. By increasing the size of connector, the maximum load increased for most cases. In general, the 135 degrees tilted angle shear connectors have a higher strength and stiffness than the 112.5 degrees type. PMID:26642193

ZM-21 magnesium alloy corrosion properties and cryogenic to elevated temperature mechanical properties

NASA Technical Reports Server (NTRS)

Montana, J. W.; Nelson, E. E.

1972-01-01

The mechanical properties of bare ZM-21 magnesium alloy flat tensile specimens were determined for test temperatures of +400 F, +300 F, +200 F, +80 F, 0 F, -100 F, -200 F, and -320 F. The ultimate tensile and yield strengths of the material increased with decreasing temperature with a corresponding reduction in elongation values. Stress corrosion tests performed under: (1) MSFC atmospheric conditions; (2) 95% relative humidity; and (3) submerged in 100 ppm chloride solution for 8 weeks indicated that the alloy is not susceptible to stress corrosion. The corrosion tests indicated that the material is susceptible to attack by crevice corrosion in high humidity and chemical type attack by chloride solution. Atmospheric conditions at MSFC did not produce any adverse effects on the material, probably due to the rapid formation of a protective oxide coating. In both the mechanical properties and the stress corrosion evaluations the test specimens which were cut transverse to the rolling direction had superior properties when compared to the longitudinal properties.

Behavior of Tilted Angle Shear Connectors.

PubMed

Khorramian, Koosha; Maleki, Shervin; Shariati, Mahdi; Ramli Sulong, N H

2015-01-01

According to recent researches, angle shear connectors are appropriate to transfer longitudinal shear forces across the steel-concrete interface. Angle steel profile has been used in different positions as L-shaped or C-shaped shear connectors. The application of angle shear connectors in tilted positions is of interest in this study. This study investigates the behaviour of tilted-shaped angle shear connectors under monotonic loading using experimental push out tests. Eight push-out specimens are tested to investigate the effects of different angle parameters on the ultimate load capacity of connectors. Two different tilted angles of 112.5 and 135 degrees between the angle leg and steel beam are considered. In addition, angle sizes and lengths are varied. Two different failure modes were observed consisting of concrete crushing-splitting and connector fracture. By increasing the size of connector, the maximum load increased for most cases. In general, the 135 degrees tilted angle shear connectors have a higher strength and stiffness than the 112.5 degrees type.

The effect of adhesive strength of hydroxyapatite coating on the stability of hydroxyapatite-coated prostheses in vivo at the early stage of implantation

PubMed Central

Duan, Yonghong; Zhu, Shu; Guo, Fei; Zhu, Jinyu; Li, Mao; Ma, Jie

2012-01-01

Introduction With the increase in joint revision surgery after arthroplasty, defects of hydroxyapatite (HA)-coated prostheses have been observed increasingly often. These defects adversely affect the prosthetic stability in vivo. This study has analyzed the potential effect of the adhesive strength of HA coating on the stability of HA-coated prostheses in vivo after its implantation. Material and methods Sixty experimental rabbits were divided into HA- and Ti-coated groups. HA-coated prostheses were implanted into the bilateral epicondyle of rabbits femurs. Ti-coated prostheses were implanted as control. At different time points(4, 9, and 15 weeks) after implantation, bone tissue samples were fetched out respectively for histomorphometric analysis. Push-out testing was used to detect the ultimate shear strength at the bone-prosthesis interface. Scanning electron microscope (SEM) observation and energy-dispersive X-ray spectroscopy (EDX) analysis were used to observe the changes in surface composition of the prostheses after the ultimate shear strength testing. The coating adhesive strength of two kinds of coatings were also examined by scratch testing. Results Hydroxyapatite coating has an obvious advantage in facilitating osteogenesis and its plays a critical role in the stability of prostheses. However, the ultimate shear strength of HA-coated prostheses is much lower than that of Ti-coated implants (p < 0.01). Further study has demonstrated that the stability of HA-coated prostheses in vivo is affected by the relatively low adhesive strength between coating and substrate. Conclusions Obvious advantage in facilitating osteogenesis around HA-coated prostheses is not the only factor that determines the stability of prostheses in vivo. PMID:22661990

The Ultimate Strength of Double Hull Oil Tanker Due to Grounding and Collision

NASA Astrophysics Data System (ADS)

Izaak Latumahina, Samuel; Zubair Muis Alie, Muhammad; Sitepu, Ganding

2018-02-01

The damaged tanker by grounding and collision may totally collapse if loss its buoyancy, stability and suffer structural failure. The objective of the present study is to investigate the ultimate strength of double hull oil tanker under vertical bending moments due to grounding and collision. The damages are modelled by removing the elements consist of stiffened and unstiffened plates from the damages part. One-frame space of the double hull oil tanker is taken to be analysed. Two damages cases are considered in the analyses those are grounding and collision. The transversal damage extent for grounding are 10%, 25%, 40% and 55%. The groundings are placed at symmetric position on the outer bottom part. For the case of collision, the vertical damage extent are taken as 10%, 20%, 40% and 60%. The transversal damages extent is taken to be B/16 and it is constant for all collision damages. The investigation of the ultimate strength is performed by the Non-Linear Finite Element Analysis method under moment control. The boundary condition is applied with fully constrained on all nodes at the aft-end, while the rigid linked on all nodes is attached at the fore-end with respect to the reference point on the neutral axis. The initial imperfection, welding residual stress and crack are not considered in the analyses. The results obtained by Non-Linear Finite Element Analyses for the ultimate strength are compared with the in-house program using Smith’s method implemented in HULLST. The stress distribution and deformation for every case of damages including intact are also discussed in the present study.

Evaluation of the Elastic Properties of Thirteen Silicone Interocclusal Recording Materials

PubMed Central

Zietek, Marek

2016-01-01

Background. Addition silicones are popular as dental impression materials and are used in bite registration procedures. Objective. This study aimed to compare the postsetting elasticities and other mechanical properties of thirteen addition silicone interocclusal recording materials. Materials and Methods. The following materials were investigated: Colorbite D, Futar D, Genie Bite, Jet Blue Bite fast, Memoreg 2, O-Bite, Occlufast Rock, Omni-Bite Plus, Regidur i, Registrado X-tra, Regofix transparent, StoneBite, and Variotime Bite. Thirty specimens of each material were tested. The elasticities and strengths of the materials were measured with a universal testing machine, and computer software was used to determine the E-moduli, ultimate tensile strengths, and ultimate elongations of the specimens. Results. The results were subjected to statistical analysis using the Kruskal-Wallis test (p ≤ 0.05). The statistics revealed that the mean E-modulus values varied significantly across the materials (p = 0.000) and were highest for the StoneBite and Registrado X-tra and lowest for the Regofix transparent. The ultimate tensile strengths were highest for the Regofix transparent and Registrado X-tra (p = 0.000) and lowest for the Jet Blue Bite fast and Memoreg 2 (p = 0.000). The elongation percentages at the point of breaking varied significantly across the materials (p = 0.000); the lowest value was observed for the StoneBite, whereas the Regofix transparent nearly doubled original length. Conclusions. The authors concluded that materials with the high E-moduli and great ultimate tensile strengths may be most useful clinically. Registrado X-tra and StoneBite best met these criteria. PMID:27747239

Strain rate effects on mechanical properties of fiber composites, part 3

NASA Technical Reports Server (NTRS)

Daniel, I. M.; Liber, T.

1976-01-01

An experimental investigation was conducted to determine the strain rate effects in fiber composites. Unidirectional composite specimens of boron/epoxy, graphite/epoxy, S-glass/epoxy and Kevlar/epoxy were tested to determine longitudinal, transverse and intralaminar (in-plane) shear properties. In the Longitudinal direction the Kevlar/epoxy shows a definite increase in both modulus and strength with strain rate. In the transverse direction, a general trend toward higher strength with strain rate is noticed. The intralaminar shear moduli and strengths of boron/epoxy and graphite/epoxy show a definite rise with strain rate.

Development of FRP composite structural biomaterials: ultimate strength of the fiber/matrix interfacial bond in in vivo simulated environments.

PubMed

Latour, R A; Black, J

1992-05-01

Fiber reinforced polymer (FRP) composites are being developed as alternatives to metals for structural orthopedic implant applications. FRP composite fracture behavior and environmental interactions are distinctly different from those which occur in metals. These differences must be accounted for in the design and evaluation of implant performance. Fiber/matrix interfacial bond strength in a FRP composite is known to strongly influence fracture behavior. The interfacial bond strength of four candidate fiber/matrix combinations (carbon fiber/polycarbonate, carbon fiber/polysulfone, polyaramid fiber/polycarbonate, polyaramid fiber/polysulfone) were investigated at 37 degrees C in dry and in vivo simulated (saline, exudate) environments. Ultimate bond strength was measured by a single fiber-microdroplet pull-out test. Dry bond strengths were significantly decreased following exposure to either saline or exudate with bond strength loss being approximately equal in both the saline and exudate. Bond strength loss is attributed to the diffusion of water and/or salt ions into the sample and their interaction with interfacial bonding. Because bond degradation is dependent upon diffusion, diffusional equilibrium must be obtained in composite test samples before the full effect of the test environment upon composite mechanical behavior can be determined.

Bootstrap calculation of ultimate strength temperature maxima for neutron irradiated ferritic/martensitic steels

NASA Astrophysics Data System (ADS)

Obraztsov, S. M.; Konobeev, Yu. V.; Birzhevoy, G. A.; Rachkov, V. I.

2006-12-01

The dependence of mechanical properties of ferritic/martensitic (F/M) steels on irradiation temperature is of interest because these steels are used as structural materials for fast, fusion reactors and accelerator driven systems. Experimental data demonstrating temperature peaks in physical and mechanical properties of neutron irradiated pure iron, nickel, vanadium, and austenitic stainless steels are available in the literature. A lack of such an information for F/M steels forces one to apply a computational mathematical-statistical modeling methods. The bootstrap procedure is one of such methods that allows us to obtain the necessary statistical characteristics using only a sample of limited size. In the present work this procedure is used for modeling the frequency distribution histograms of ultimate strength temperature peaks in pure iron and Russian F/M steels EP-450 and EP-823. Results of fitting the sums of Lorentz or Gauss functions to the calculated distributions are presented. It is concluded that there are two temperature (at 360 and 390 °C) peaks of the ultimate strength in EP-450 steel and single peak at 390 °C in EP-823.

Theoretical Model of the Effect of Crack Tip Blunting on the Ultimate Tensile Strength of Welds in 2219-T87 Aluminum

NASA Technical Reports Server (NTRS)

Beil, R. J.

1982-01-01

A theoretical model representing blunting of a crack tip radius through diffusion of vacancies is presented. The model serves as the basis for a computer program which calculates changes, due to successive weld heat passes, in the ultimate tensile strength of 2219-T81 aluminum. In order for the model to yield changes of the same order in the ultimate tensile strength as that observed experimentally, a crack tip radius of the order of .001 microns is required. Such sharp cracks could arise in the fusion zone of a weld from shrinkage cavities or decohered phase boundaries between dendrites and the eutectic phase, or, possibly, from plastic deformation due to thermal stresses encountered during the welding process. Microstructural observations up to X2000 (resolution of about .1 micron) did not, in the fusion zone, show structural details which changed significantly under the influence of a heat pass, with the exception of possible small changes in the configuration of the interdendritic eutectic and in porosity build-up in the remelt zone.

Baseline and longitudinal change in isometric muscle strength prior to radiographic progression in osteoarthritic and pre-osteoarthritic knees--data from the Osteoarthritis Initiative.

PubMed

Eckstein, F; Hitzl, W; Duryea, J; Kent Kwoh, C; Wirth, W

2013-05-01

To test whether cross-sectional or longitudinal measures of thigh muscle isometric strength differ between knees with and without subsequent radiographic progression of knee osteoarthritis (KOA), with particular focus on pre-osteoarthritic female knees (knees with risk factors but without definite radiographic KOA). Of 4,796 Osteoarthritis Initiative participants, 2,835 knees with Kellgren Lawrence grade (KLG) 0-3 had central X-ray readings, annual quantitative joint space width (JSW) and isometric muscle strength measurements (Good strength chair). Separate slope analysis of covariance (ANCOVA) models were used to determine differences in strength between "progressor" and "non-progressor" knees, after adjusting for age, body mass index, and pain. 466 participant knees exceeded the smallest detectable JSW change during each of two observation intervals (year 2→4 and year 1→3) and were classified as progressors (213 women, 253 men; 128 KLG0/1, 330 KLG2/3); 946 participant knees did not exceed this threshold in either interval and were classified as non-progressors (588 women, 358 from men; 288KLG0/1, 658KLG2/3). Female progressor knees, including those with KLG0/1, tended to have lower extensor and flexor strength at year 2 and at baseline than those without progression, but the difference was not significant after adjusting for confounders. No significant difference was observed in longitudinal change of muscle strength (baseline→year 2) prior to radiographic progression. No significant differences were found for muscle strength in men, and none for change in strength concomitant with progression. This study provides no strong evidence that (changes in) isometric muscle strength precedes or is associated with structural (radiographic) progression of KOA. Copyright © 2013 Osteoarthritis Research Society International. Published by Elsevier Ltd. All rights reserved.

Baseline and Longitudinal Change in Isometric Muscle Strength Prior to Radiographic Progression in Osteoarthritic and Pre-Osteoarthritic Knees- Data from the Osteoarthritis Initiative

PubMed Central

Eckstein, Felix; Hitzl, Wolfgang; Duryea, Jeff; Kwoh, C. Kent; Wirth, Wolfgang

2013-01-01

OBJECTIVE To test whether cross-sectional or longitudinal measures of thigh muscle isometric strength differ between knees with and without subsequent radiographic progression of knee osteoarthritis (KOA), with particular focus on pre-osteoarthritic female knees (knees with risk factors but without definite radiographic KOA). METHODS Of 4796 Osteoarthritis Initiative participants, 2835 knees with Kellgren Lawrence grade (KLG) 0–3 had central X-ray readings, annual quantitative joint space width (JSW) and isometric muscle strength measurements (Good strength chair). Separate slope ANCOVA models were used to determine differences in strength between “progressor” and “non- progressor” knees, after adjusting for age, body mass index, and pain. RESULTS 466 participant knees exceeded the smallest detectable JSW change during each of two observation intervals (year 2→4 and year 1→3) and were classified as progressors (213 women, 253 men; 128 KLG0/1, 330 KLG2/3); 946 participant knees did not exceed this threshold in either interval and were classified as non-progressors (588 women, 358 from men; 288KLG0/1, 658KLG2/3). Female progressor knees, including those with KLG0/1, tended to have lower extensor and flexor strength at year2 and at baseline than those without progression, but the difference was not significant after adjusting for confounders. No significant difference was observed in longitudinal change of muscle strength (baseline→year2) prior to radiographic progression. No significant differences were found for muscle strength in men, and none for change in strength concomitant with progression. CONCLUSION This study provides no strong evidence that (changes in) isometric muscle strength precedes or is associated with structural (radiographic) progression of KOA. PMID:23473978

Design optimization of continuous partially prestressed concrete beams

NASA Astrophysics Data System (ADS)

Al-Gahtani, A. S.; Al-Saadoun, S. S.; Abul-Feilat, E. A.

1995-04-01

An effective formulation for optimum design of two-span continuous partially prestressed concrete beams is described in this paper. Variable prestressing forces along the tendon profile, which may be jacked from one end or both ends with flexibility in the overlapping range and location, and the induced secondary effects are considered. The imposed constraints are on flexural stresses, ultimate flexural strength, cracking moment, ultimate shear strength, reinforcement limits cross-section dimensions, and cable profile geometries. These constraints are formulated in accordance with ACI (American Concrete Institute) code provisions. The capabilities of the program to solve several engineering problems are presented.

The Strength and Characteristics of VPPA Welded 2219-T87 Aluminum Alloy

NASA Technical Reports Server (NTRS)

Jemian, W. A.

1985-01-01

A study of the variable polarity plasma arc (VPPA) welding process and those factors that control the structure and properties of VPPA welded aluminum alloy 2219-T87 was conducted. The importance of joint preparation, alignment of parts and welding process variables are already established. Internal weld defects have been eliminated. However, a variation of properties was found to be due to the size variation of interdendritic particles in the fusion zone. These particles contribute to the void formation process, which controls the ultimate tensile strength of the welded alloy. A variation of 150 microns in particle size correlated with a 10 ksi variation of ultimate tensile strength. It was found that all fracture surfaces were of the dimple rupture type, with fracture initiating within the fusion zone.

The Literacy Factor in the Optimal Age Discussion: A Five-Year Longitudinal Study

ERIC Educational Resources Information Center

Pfenninger, Simone E.

2016-01-01

This study examines the impact of L2 literacy on the development of writing proficiency in the L3, as related to age of onset (AO) of instruction, as well as the effects of AO on ultimate L3 attainment at the end of the period of normal schooling. Using longitudinal data for the same student cohort (200 Swiss learners of English) at the beginning…

Fracture and crack growth in orthotropic laminates

NASA Technical Reports Server (NTRS)

Goree, James G.; Kaw, Autar K.

1985-01-01

A mathematical model based on the classical shear-lag assumptions is used to study the residual strength and fracture behavior of composite laminates with symmetrically placed buffer strips. The laminate is loaded by a uniform remote longitudinal tensile strain and has initial damage in the form of a transverse crack in the parent laminate between buffer strips. The crack growth behavior as a function of material properties, number of buffer-strip plies, spacing, width of buffer strips, longitudinal matrix splitting, and debonding at the interface is studied. Buffer-strip laminates are shown to arrest fracture and increase the residual strengths significantly over those of one material laminates, with S-glass being a more effective buffer strip material than Kevlar in increasing the damage tolerance of graphite/epoxy panels. For a typical graphite/epoxy laminate with S-glass buffer-strips, the residual strength is about 2.4 times the residual strength of an all graphite/epoxy panel with the same crack length. Approximately 50% of this increase is due to the S-glass/epoxy buffer-strips, 40% due to longitudinal splitting of the buffer strip interface and 10% due to bonding.

SU-E-T-155: Calibration of Variable Longitudinal Strength 103Pd Brachytherapy Sources

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reed, J; Radtke, J; Micka, J

Purpose: Brachytherapy sources with variable longitudinal strength (VLS) allow for a customized intensity along the length of the source. These have applications in focal brachytherapy treatments of prostate cancer where dose boosting can be achieved through modulation of intra-source strengths. This work focused on development of a calibration methodology for VLS sources based on measurements and Monte Carlo (MC) simulations of five 1 cm {sup 10} {sup 3}Pd sources each containing four regions of variable {sup 103}Pd strength. Methods: The air-kerma strengths of the sources were measured with a variable-aperture free-air chamber (VAFAC). Source strengths were also measured using amore » well chamber. The in-air azimuthal and polar anisotropy of the sources were measured by rotating them in front of a NaI scintillation detector and were calculated with MC simulations. Azimuthal anisotropy results were normalized to their mean intensity values. Polar anisotropy results were normalized to their average transverse axis intensity values. The relative longitudinal strengths of the sources were measured via on-contact irradiations with radiochromic film, and were calculated with MC simulations. Results: The variable {sup 103}Pd loading of the sources was validated by VAFAC and well chamber measurements. Ratios of VAFAC air-kerma strengths and well chamber responses were within ±1.3% for all sources. Azimuthal anisotropy results indicated that ≥95% of the normalized values for all sources were within ±1.7% of the mean values. Polar anisotropy results indicated variations within ±0.3% for a ±7.6° angular region with respect to the source transverse axis. Locations and intensities of the {sup 103}Pd regions were validated by radiochromic film measurements and MC simulations. Conclusion: The calibration methodology developed in this work confirms that the VLS sources investigated have a high level of polar uniformity, and that the strength and longitudinal intensity can be verified experimentally and through MC simulations. {sup 103}Pd sources were provided by CivaTech Oncology, Inc.« less

Interrelationships of serum testosterone and free testosterone index with FFM and strength in aging men.

PubMed

Roy, Tracey Ann; Blackman, Marc R; Harman, S Mitchell; Tobin, Jordan D; Schrager, Matthew; Metter, E Jeffery

2002-08-01

Muscle mass and strength losses during aging may be associated with declining levels of serum testosterone (T) in men. Few studies have shown a direct relationship between T and muscle mass and strength. Subjects were 262 men, aged 24-90 yr, from the Baltimore Longitudinal Study of Aging, who had T and sex hormone-binding globulin sex hormone-binding globulin (SHBG) measurements, from which the free T index (FTI) was calculated (T/SHBG) from serum samples collected longitudinally since 1963, total body fat mass and arm and leg fat-free mass (FFM) by dual-energy X-ray absorptiometry and arm and leg strength by dynanomometry. Mixed-effects models estimated T and FTI at the time of mass and strength measurements. Age, total body fat, arm and leg FFM, T, and FTI were significantly associated with concentric and eccentric strength. FTI, not T, was modestly, but directly, related to arm and leg strength after fat, arm and leg FFM, height, and age were accounted for and indirectly through body mass. FTI is a better predictor of arm and leg strength than T in aging men.

Nuclear magnetic relaxation by the dipolar EMOR mechanism: General theory with applications to two-spin systems.

PubMed

Chang, Zhiwei; Halle, Bertil

2016-02-28

In aqueous systems with immobilized macromolecules, including biological tissue, the longitudinal spin relaxation of water protons is primarily induced by exchange-mediated orientational randomization (EMOR) of intra- and intermolecular magnetic dipole-dipole couplings. We have embarked on a systematic program to develop, from the stochastic Liouville equation, a general and rigorous theory that can describe relaxation by the dipolar EMOR mechanism over the full range of exchange rates, dipole coupling strengths, and Larmor frequencies. Here, we present a general theoretical framework applicable to spin systems of arbitrary size with symmetric or asymmetric exchange. So far, the dipolar EMOR theory is only available for a two-spin system with symmetric exchange. Asymmetric exchange, when the spin system is fragmented by the exchange, introduces new and unexpected phenomena. Notably, the anisotropic dipole couplings of non-exchanging spins break the axial symmetry in spin Liouville space, thereby opening up new relaxation channels in the locally anisotropic sites, including longitudinal-transverse cross relaxation. Such cross-mode relaxation operates only at low fields; at higher fields it becomes nonsecular, leading to an unusual inverted relaxation dispersion that splits the extreme-narrowing regime into two sub-regimes. The general dipolar EMOR theory is illustrated here by a detailed analysis of the asymmetric two-spin case, for which we present relaxation dispersion profiles over a wide range of conditions as well as analytical results for integral relaxation rates and time-dependent spin modes in the zero-field and motional-narrowing regimes. The general theoretical framework presented here will enable a quantitative analysis of frequency-dependent water-proton longitudinal relaxation in model systems with immobilized macromolecules and, ultimately, will provide a rigorous link between relaxation-based magnetic resonance image contrast and molecular parameters.

Buckling of a Longitudinally Jointed Curved Composite Panel Arc Segment for Next Generation of Composite Heavy Lift Launch Vehicles: Verification Testing Analysis

NASA Technical Reports Server (NTRS)

Farrokh, Babak; Segal, Kenneth N.; Akkerman, Michael; Glenn, Ronald L.; Rodini, Benjamin T.; Fan, Wei-Ming; Kellas, Sortiris; Pineda, Evan J.

2014-01-01

In this work, an all-bonded out-of-autoclave (OoA) curved longitudinal composite joint concept, intended for use in the next generation of composite heavy lift launch vehicles, was evaluated and verified through finite element (FE) analysis, fabrication, testing, and post-test inspection. The joint was used to connect two curved, segmented, honeycomb sandwich panels representative of a Space Launch System (SLS) fairing design. The overall size of the resultant panel was 1.37 m by 0.74 m (54 in by 29 in), of which the joint comprised a 10.2 cm (4 in) wide longitudinal strip at the center. NASTRAN and ABAQUS were used to perform linear and non-linear analyses of the buckling and strength performance of the jointed panel. Geometric non-uniformities (i.e., surface contour imperfections) were measured and incorporated into the FE model and analysis. In addition, a sensitivity study of the specimens end condition showed that bonding face-sheet doublers to the panel's end, coupled with some stress relief features at corner-edges, can significantly reduce the stress concentrations near the load application points. Ultimately, the jointed panel was subjected to a compressive load. Load application was interrupted at the onset of buckling (at 356 kN 80 kips). A post-test non-destructive evaluation (NDE) showed that, as designed, buckling occurred without introducing any damage into the panel or the joint. The jointed panel was further capable of tolerating an impact damage to the same buckling load with no evidence of damage propagation. The OoA cured all-composite joint shows promise as a low mass factory joint for segmented barrels.

Nuclear magnetic relaxation by the dipolar EMOR mechanism: General theory with applications to two-spin systems

NASA Astrophysics Data System (ADS)

Chang, Zhiwei; Halle, Bertil

2016-02-01

In aqueous systems with immobilized macromolecules, including biological tissue, the longitudinal spin relaxation of water protons is primarily induced by exchange-mediated orientational randomization (EMOR) of intra- and intermolecular magnetic dipole-dipole couplings. We have embarked on a systematic program to develop, from the stochastic Liouville equation, a general and rigorous theory that can describe relaxation by the dipolar EMOR mechanism over the full range of exchange rates, dipole coupling strengths, and Larmor frequencies. Here, we present a general theoretical framework applicable to spin systems of arbitrary size with symmetric or asymmetric exchange. So far, the dipolar EMOR theory is only available for a two-spin system with symmetric exchange. Asymmetric exchange, when the spin system is fragmented by the exchange, introduces new and unexpected phenomena. Notably, the anisotropic dipole couplings of non-exchanging spins break the axial symmetry in spin Liouville space, thereby opening up new relaxation channels in the locally anisotropic sites, including longitudinal-transverse cross relaxation. Such cross-mode relaxation operates only at low fields; at higher fields it becomes nonsecular, leading to an unusual inverted relaxation dispersion that splits the extreme-narrowing regime into two sub-regimes. The general dipolar EMOR theory is illustrated here by a detailed analysis of the asymmetric two-spin case, for which we present relaxation dispersion profiles over a wide range of conditions as well as analytical results for integral relaxation rates and time-dependent spin modes in the zero-field and motional-narrowing regimes. The general theoretical framework presented here will enable a quantitative analysis of frequency-dependent water-proton longitudinal relaxation in model systems with immobilized macromolecules and, ultimately, will provide a rigorous link between relaxation-based magnetic resonance image contrast and molecular parameters.

High Temperature Mechanical Characterization of Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Gyekenyesi, John Z.

1998-01-01

A high temperature mechanical characterization laboratory has been assembled at NASA Lewis Research Center. One contribution of this work is to test ceramic matrix composite specimens in tension in environmental extremes. Two high temperature tensile testing systems were assembled. The systems were assembled based on the performance and experience of other laboratories and meeting projected service conditions for the materials in question. The systems use frames with an electric actuator and a center screw. A PC based data acquisition and analysis system is used to collect and analyze the data. Mechanical extensometers are used to measure specimen strain. Thermocouples, placed near the specimen, are used to measure the specimen gage section temperature. The system for testing in air has a resistance element furnace with molybdenum disilicide elements and pneumatic grips with water cooling attached to hydraulic alignment devices. The system for testing in an inert gas has a graphite resistance element furnace in a chamber with rigidly mounted, water cooled, hydraulically actuated grips. Unidirectional SiC fiber reinforced reaction bonded Si3N4 and triaxially woven, two dimensional, SiC fiber reinforced enhanced SiC composites were tested in unidirectional tension. Theories for predicting the Young's modulus, modulus near the ultimate strength, first matrix cracking stress, and ultimate strength were applied and evaluated for suitability in predicting the mechanical behavior of SiC/RBSN and enhanced SiC/SiC composites. The SiC/RBSN composite exhibited pseudo tough behavior (increased area under the stress/strain curve) from 22 C to 1500 C. The rule of mixtures provides a good estimate of the Young's modulus of the SiC/RBSN composite using the constituent properties from room temperature to 1440 C for short term static tensile tests in air or nitrogen. The rule of mixtures significantly overestimates the secondary modulus near the ultimate strength. The ACK theory provides the best approximation of the first matrix cracking stress when residual stresses are ignored. The theory of Cao and Thouless, based on Weibull statistics, gave the best prediction for the composite ultimate strength. The enhanced SiC/SiC composite exhibited nonlinear stress/strain behavior from 24 C to 1370 C in air with increased ultimate strain when compared to monolithic SiC. The theory of Yang and Chou with the assumption of a frictional fiber/matrix interface provided the best estimate of the Young's modulus. The theory of Cao and Thouless gave the best estimate for the ultimate strength.

Riveting in metal airplane construction. Part II : riveting methods and equipment (concluded)

NASA Technical Reports Server (NTRS)

Pleines, Wilhelm

1930-01-01

This report includes descriptive material on rivet inspection, types of rivets and sizes. Tabular data on shearing strength of rivets at failure, ultimate shear of various rivets, tensile tests of rivet plate, and tensile strength values of riveted joints.

Age- and sex-related regional compressive strength characteristics of human lumbar vertebrae in osteoporosis

PubMed Central

Kurutz, Márta; Donáth, Judit; Gálos, Miklós; Varga, Péter; Fornet, Béla

2008-01-01

Objective To obtain the compressive load bearing and energy absorption capacity of lumbar vertebrae of osteoporotic elderly for the everyday medical praxis in terms of the simple diagnostic data, like computed tomography (CT), densitometry, age, and sex. Methods Compressive test of 54 osteoporotic cadaver vertebrae L1 and L2, 16 males and 38 females (age range 43–93, mean age 71.6 ± 13.3 years, mean bone mineral density (BMD) 0.377 ± 0.089 g/cm2, mean T-score −5.57 ± 0.79, Z-score −4.05 ± 0.77) was investigated. Based on the load-displacement diagrams and the measured geometrical parameters of vertebral bodies, proportional, ultimate and yield stresses and strains, Young’s modulus, ductility and energy absorption capacity were determined. Three vertebral regions were distinguished: superior, central and inferior regions, but certain parameters were calculated for the upper/ lower intermediate layers, as well. Cross-sectional areas, and certain bone tissue parameters were determined by image analysis of CT pictures of vertebrae. Sex- and age-related decline functions and trends of strength characteristics were determined. Results Size-corrected failure load was 15%–25% smaller in women, proportional and ultimate stresses were about 30%–35% smaller for women in any region, and 20%–25% higher in central regions for both sexes. Young’s moduli were about 30% smaller in women in any region, and 20%–25% smaller in the central region for both sexes. Small strains were higher in males, large strains were higher in females, namely, proportional strains were about 25% larger in men, yield and ultimate strains were quasi equal for sexes, break strains were 10% higher in women. Ultimate energy absorption capacity was 10%–20% higher in men; the final ductile energy absorption capacity was quasi equal for sexes in all levels. Age-dependence was stronger for men, mainly in central regions (ultimate load, male: r = −0.66, p < 0.01, female: r = −0.52, p < 0.005; ultimate stress, male: r = −0.69, p < 0.01, female: r = −0.50, p < 0.005; Young’s modulus, male: r = −0.55, p < 0.05, female: r = −0.52, p < 0.005, ultimate stiffness, male: r = −0.58, p < 0.05, female: r = −0.35, p < 0.03, central ultimate absorbed energy density, male: r = −0.59, p < 0.015, female: r = −0.29, p < 0.08). Conclusions For the strongly osteoporotic population (BMD < 0.4 g/cm2, T-score < −4) the statical variables (loads, stresses) showed significant correlation; mixed variables (stiffness, Young’s modulus, energy) showed moderate correlation; kinematical variables (displacements, strains) showed no correlation with age. The strong correlation of men between BMD and aging (r = −0.82, p < 0.001) and betwen BMD and strength parameters (r = 0.8–0.9, p < 0.001) indicated linear trends in age-related strength loss for men; however, the moderate correlation of women between BMD and aging (r = −0.47, p < 0.005) and between BMD and strength parameters (r = 0.4–0.5, p < 0.005) suggested the need of nonlinear (quadratic) approximation that provided the better fit in age-related strength functions of females modelling postmenopausal disproportionalities. PMID:21197342

Investigation on mechanical behavior and material characteristics of various weight composition of SiCp reinforced aluminium metal matrix composite

NASA Astrophysics Data System (ADS)

Pichumani, Sivachidambaram; Srinivasan, Raghuraman; Ramamoorthi, Venkatraman

2018-02-01

Aluminium - silicon carbide (Al - SiC) metal matrix composite is produced with following wt % of SiC reinforcement (4%, 8% & 12%) using stir casting method. Mechanical testing such as micro hardness, tensile testing and bend testing were performed. Characterizations, namely micro structure, X-ray diffraction (XRD) analysis, inductive coupled plasma - optical emission spectroscopy (ICP-OES) and scanning electron microscopy (SEM) analysis, were carried out on Al - SiC composites. The presence of SiC on Al - SiC composite is confirmed through XRD technique and microstructure. The percentage of SiC was confirmed through ICP-OES technique. Increase in weight percentage of SiC tends to increase micro hardness, ultimate strength & yield strength but it reduces the bend strength and elongation (%) of the material. SEM factrography of tensile tested fractured samples of Al - 8% SiC & Al - 12% SiC showed fine dimples on fractured surface & coarse dimples fractured surface respectively. This showed significant fracture differences between Al - 8% SiC & Al - 12% SiC. From the above experiment, Al - 8% SiC had good micro hardness, ultimate strength & yield strength without significant loss in elongation (%) & bend strength.

Does artificial aging affect mechanical properties of CAD/CAM composite materials.

PubMed

Egilmez, Ferhan; Ergun, Gulfem; Cekic-Nagas, Isil; Vallittu, Pekka K; Lassila, Lippo V J

2018-01-01

The purpose of this study was to determine the flexural strength and Weibull characteristics of different CAD/CAM materials after different in vitro aging conditions. The specimens were randomly assigned to one of the six in vitro aging conditions: (1) water storage (37°C, 3 weeks), (2) boiling water (24h), (3) hydrochloric acid exposure (pH: 1.2, 24h), (4) autoclave treatment (134°C, 200kPa, 12h), (5) thermal cycling (5000 times, 5-55°C), (6) cyclic loading (100N, 50,000 cycles). No treatment was applied to the specimens in control group. Three-point bending test was used for the calculation of flexural strength. The reliability of the strength was assessed by Weibull distribution. Surface roughness and topography was examined by coherence scanning interferometry. Evaluated parameters were compared using the Kruskall-Wallis or Mann-Whitney U test. Water storage, autoclave treatment and thermal cycling significantly decreased the flexural strength of all materials (p<0.05), whereas HCl exposure or cyclic loading did not affect the properties (p>0.05). Weibull moduli of Cerasmart™ and Lava™ Ultimate were similar with control. Vita Enamic ® exhibited similar Weibull moduli in all aging groups except the HCl treated group (p>0.05). R a values of Cerasmart™ and Lava™ Ultimate were in the range of 0.053-0.088μm in the aged groups. However R a results of Vita Enamic ® were larger than 0.2μm. Flexural strength of newly developed restorative CAD/CAM materials was significantly decreased by artificial aging. Cyclic loading or HCl exposure does not affect to the flexural strength and structural reliability of Cerasmart™ and Lava™ Ultimate. Copyright © 2017 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

Composite impact strength improvement through a fiber/matrix interphase

NASA Technical Reports Server (NTRS)

Cavano, P. J.; Winters, W. E.

1975-01-01

Research was conducted to improve the impact strength and toughness of fiber/resin composites by means of a fiber coating interphase. Graphite fiber/epoxy resin composites were fabricated with four different fiber coating systems introduced in a matrix-fiber interphase. Two graphite fibers, a high strength and a high modulus type, were studied with the following coating systems: chemical vapor deposited boron, electroless nickel, a polyamide-imide resin and a thermoplastic polysulfone resin. Evaluation methods included the following tests: Izod, flexure, shear fracture toughness, longitudinal and transverse tensile, and transverse and longitudinal compression. No desirable changes could be effected with the high strength fiber, but significant improvements in impact performance were observed with the polyamide-imide resin coated high modulus fiber with no loss in composite modulus.

Length and temperature dependence of the mechanical properties of finite-size carbyne

NASA Astrophysics Data System (ADS)

Yang, Xueming; Huang, Yanhui; Cao, Bingyang; To, Albert C.

2017-09-01

Carbyne is an ideal one-dimensional conductor and the thinnest interconnection in an ultimate nano-device and it requires an understanding of the mechanical properties that affect device performance and reliability. Here, we report the mechanical properties of finite-size carbyne, obtained by a molecular dynamics simulation study based on the adaptive intermolecular reactive empirical bond order potential. To avoid confusion in assigning the effective cross-sectional area of carbyne, the value of the effective cross-sectional area of carbyne (4.148 Å2) was deduced via experiment and adopted in our study. Ends-constraints effects on the ultimate stress (maximum force) of the carbyne chains are investigated, revealing that the molecular dynamics simulation results agree very well with the experimental results. The ultimate strength, Young's Modulus and maximum strain of carbyne are rather sensitive to the temperature and all decrease with the temperature. Opposite tendencies of the length dependence of the overall ultimate strength and maximum strain of carbyne at room temperature and very low temperature have been found, and analyses show that this originates in the ends effect of carbyne.

Yttria Nanoparticle Reinforced Commercially Pure (CP) Titanium

DTIC Science & Technology

2011-09-01

nanoparticles as well as titanium boride (TiB) reinforcements were produced through gas atomization. After consolidation and extrusion, room temperature...pure FE iron O oxygen Ti titanium TiB titanium boride TYS tensile yield strength UTS ultimate tensile strength wt% weight percent Y2O3

Weld bead reinforcement removal: A method of improving the strength and ductility of peaked welds in 2219-T87 aluminum alloy plate

NASA Technical Reports Server (NTRS)

Lovoy, C. V.

1979-01-01

The results of a study to determine the degree to which the ductility and tensile properties of peaked welds could be enhanced by removing the reinforcing bead and fairing the weld nugget into the adjacent parent metal are presented. The study employed 2219-T87 aluminum alloy plate, tungsten inert gas (TIG) welding, and 2319 filler wire. The study concluded that significant improvements in peak weld, ultimate strength, and ductility can be obtained through removal and fairing of the weld reinforcing bead. The specimens so treated and tested in this program exhibited ultimate strength improvements of 2 to 3 percent for peak angles of 5.8 to 10 degrees and 10 to 22 percent for welds with peak angles of 11.7 to 16.9 degrees. It was also determined that removal of the weld bead enhanced the ability of peaked welds to straighten when exposed to cyclic loading at stress levels above the yield strength.

Effect of Load Rate on Ultimate Tensile Strength of Ceramic Matrix Composites at Elevated Temperatures

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Gyekenyesi, John P.

2001-01-01

The strengths of three continuous fiber-reinforced ceramic composites, including SiC/CAS-II, SiC/MAS-5 and SiC/SiC, were determined as a function of test rate in air at 1100 to 1200 C. All three composite materials exhibited a strong dependency of strength on test rate, similar to the behavior observed in many advanced monolithic ceramics at elevated temperatures. The application of the preloading technique as well as the prediction of life from one loading configuration (constant stress-rate) to another (constant stress loading) suggested that the overall macroscopic failure mechanism of the composites would be the one governed by a power-law type of damage evolution/accumulation, analogous to slow crack growth commonly observed in advanced monolithic ceramics. It was further found that constant stress-rate testing could be used as an alternative to life prediction test methodology even for composite materials, at least for short range of lifetimes and when ultimate strength is used as the failure criterion.

Advanced composites structural concepts and materials technologies for primary aircraft structures: Structural response and failure analysis

NASA Technical Reports Server (NTRS)

Dorris, William J.; Hairr, John W.; Huang, Jui-Tien; Ingram, J. Edward; Shah, Bharat M.

1992-01-01

Non-linear analysis methods were adapted and incorporated in a finite element based DIAL code. These methods are necessary to evaluate the global response of a stiffened structure under combined in-plane and out-of-plane loading. These methods include the Arc Length method and target point analysis procedure. A new interface material model was implemented that can model elastic-plastic behavior of the bond adhesive. Direct application of this method is in skin/stiffener interface failure assessment. Addition of the AML (angle minus longitudinal or load) failure procedure and Hasin's failure criteria provides added capability in the failure predictions. Interactive Stiffened Panel Analysis modules were developed as interactive pre-and post-processors. Each module provides the means of performing self-initiated finite elements based analysis of primary structures such as a flat or curved stiffened panel; a corrugated flat sandwich panel; and a curved geodesic fuselage panel. This module brings finite element analysis into the design of composite structures without the requirement for the user to know much about the techniques and procedures needed to actually perform a finite element analysis from scratch. An interactive finite element code was developed to predict bolted joint strength considering material and geometrical non-linearity. The developed method conducts an ultimate strength failure analysis using a set of material degradation models.

Study on axial strength of a channel-shaped pultruded GFRP member

NASA Astrophysics Data System (ADS)

Matsumoto, Yukihiro; Satake, Chito; Nisida, Kenji

2017-10-01

Fiber reinforced polymers (FRP) are widely used in vehicle and aerospace applications because of their lightweight and high-strength characteristics. Additionally, FRPs are increasingly applied to building structures. However, the elastic modulus of glass fiber reinforced polymers (GFRPs) is lower than that of steel. Hence, the evaluating the buckling strength of GFRP members for design purpose is necessary. The buckling strength is determined by Euler buckling mode as well as local buckling. In this study investigated the compressive strength of GFRP members subjected to axial compression through experiments and theoretical calculations. The adopted GFRP member was a channel-shaped GFRP, which was molded via pultrusion, at various lengths. Although, the mechanical properties as longitudinal elastic modulus and fiber volume fraction and strength of GFRP members subjected, to axial can be easily evaluated, evaluating transverse elastic modulus and shear modulus in typical material tests is difficult in standard section. Therefore the composite law was used in this study. As a result, we confirmed that the axial strength of a GFRP member could be calculated by a theoretical evaluation method utilizing longitudinal elastic modulus and fiber volume fraction.

Static behavior and the effects of thermal cycling in hybrid laminates

NASA Technical Reports Server (NTRS)

Liber, T. M.; Daniel, I. M.; Chamis, C. C.

1977-01-01

Static stiffness, strength and ultimate strain after thermal cycling were investigated for graphite/Kevlar 49/epoxy and graphite/S-glass/epoxy angle-ply laminates. Tensile stress-strain curves to failure and uniaxial tensile properties were determined, and theoretical predictions of modulus, Poisson's ratio and ultimate strain, based on linear lamination theory, constituent ply properties and measured strength, were made. No significant influence on tensile stress properties due to stacking sequence variations was observed. In general, specimens containing two 0-degree Kevlar or S-glass plies were found to behave linearly to failure, while specimens containing 4 0-degree Kevlar or S-glass plies showed some nonlinear behavior.

Al2O3 Nanoparticle Addition to Commercial Magnesium Alloys: Multiple Beneficial Effects

PubMed Central

Paramsothy, Muralidharan; Chan, Jimmy; Kwok, Richard; Gupta, Manoj

2012-01-01

The multiple beneficial effects of Al2O3 nanoparticle addition to cast magnesium based systems (followed by extrusion) were investigated, constituting either: (a) enhanced strength; or (b) simultaneously enhanced strength and ductility of the corresponding magnesium alloys. AZ31 and ZK60A nanocomposites containing Al2O3 nanoparticle reinforcement were each fabricated using solidification processing followed by hot extrusion. Compared to monolithic AZ31 (tension levels), the corresponding nanocomposite exhibited higher yield strength (0.2% tensile yield strength (TYS)), ultimate strength (UTS), failure strain and work of fracture (WOF) (+19%, +21%, +113% and +162%, respectively). Compared to monolithic AZ31 (compression levels), the corresponding nanocomposite exhibited higher yield strength (0.2% compressive yield strength (CYS)) and ultimate strength (UCS), lower failure strain and higher WOF (+5%, +5%, −4% and +11%, respectively). Compared to monolithic ZK60A (tension levels), the corresponding nanocomposite exhibited lower 0.2% TYS and higher UTS, failure strain and WOF (−4%, +13%, +170% and +200%, respectively). Compared to monolithic ZK60A (compression levels), the corresponding nanocomposite exhibited lower 0.2% CYS and higher UCS, failure strain and WOF (−10%, +7%, +15% and +26%, respectively). The capability of Al2O3 nanoparticles to enhance the properties of cast magnesium alloys in a way never seen before with micron length scale reinforcements is clearly demonstrated. PMID:28348301

A “fullerene-carbon nanotube” structure with tunable mechanical properties

NASA Astrophysics Data System (ADS)

Ji, W. M.; Zhang, L. W.; Liew, K. M.

2018-03-01

Carbon-based nanostructures have drawn tremendous research interest and become promising building blocks for the new generation of smart sensors and devices. Utilizing a bottom-up strategy, the chemical interconnecting sp 3 covalent bond between carbon building blocks is an efficient way to enhance its Young's modulus and ductility. The formation of sp 3 covalent bond, however, inevitably degrades its ultimate tensile strength caused by stress concentration at the junction. By performing a molecular dynamics simulation of tensile deformation for a fullerene-carbon nanotube (FCNT) structure, we propose a tunable strategy in which fullerenes with various angle energy absorption capacities are utilized as building blocks to tune their ductile behavior, while still maintaining a good ultimate tensile strength of the carbon building blocks. A higher ultimate tensile strength is revealed with the reduction of stress concentration at the junction. A brittle-to-ductile transition during the tensile deformation is detected through the structural modification. The development of ductile behavior is attributed to the improvement of energy propagation ability during the fracture initiation, in which the released energy from bonds fracture is mitigated properly, leading to the further development of mechanical properties.

Longitudinal sensitivity to change of MRI-based muscle cross-sectional area versus isometric strength analysis in osteoarthritic knees with and without structural progression: pilot data from the Osteoarthritis Initiative.

PubMed

Dannhauer, Torben; Sattler, Martina; Wirth, Wolfgang; Hunter, David J; Kwoh, C Kent; Eckstein, Felix

2014-08-01

Biomechanical measurement of muscle strength represents established technology in evaluating limb function. Yet, analysis of longitudinal change suffers from relatively large between-measurement variability. Here, we determine the sensitivity to change of magnetic resonance imaging (MRI)-based measurement of thigh muscle anatomical cross sectional areas (ACSAs) versus isometric strength in limbs with and without structural progressive knee osteoarthritis (KOA), with focus on the quadriceps. Of 625 "Osteoarthritis Initiative" participants with radiographic KOA, 20 had MRI cartilage and radiographic joint space width loss in the right knee isometric muscle strength measurement and axial T1-weighted spin-echo acquisitions of the thigh. Muscle ACSAs were determined from manual segmentation at 33% femoral length (distal to proximal). In progressor knees, the reduction in quadriceps ACSA between baseline and 2-year follow-up was -2.8 ± 7.9 % (standardized response mean [SRM] = -0.35), and it was -1.8 ± 6.8% (SRM = -0.26) in matched, non-progressive KOA controls. The decline in extensor strength was more variable than that in ACSAs, both in progressors (-3.9 ± 20%; SRM = -0.20) and in non-progressive controls (-4.5 ± 28%; SRM = -0.16). MRI-based analysis of quadriceps muscles ACSAs appears to be more sensitive to longitudinal change than isometric extensor strength and is suggestive of greater loss in limbs with structurally progressive KOA than in non-progressive controls.

Improved Warm-Working Process For An Iron-Base Alloy

NASA Technical Reports Server (NTRS)

Cone, Fred P.; Cryns, Brendan J.; Miller, John A.; Zanoni, Robert

1992-01-01

Warm-working process produces predominantly unrecrystallized grain structure in forgings of iron-base alloy A286 (PWA 1052 composition). Yield strength and ultimate strength increased, and elongation and reduction of area at break decreased. Improved process used on forgings up to 10 in. thick and weighing up to 900 lb.

Effects of porosity on weld-joint tensile strength of aluminum alloys

NASA Technical Reports Server (NTRS)

Lovoy, C. V.

1974-01-01

Tensile properties in defect-free weldments of aluminum alloys 2014-T6 and 2219-T87 (sheet and plate) are shown to be related to the level or concentration of induced simulated porosity. The scatter diagram shows that the ultimate tensile strength of the weldments displays the most pronounced linear relationship with the level of porosity. The relationships between yield strength or elongation and porosity are either trivial or inconsequential in the lower and intermediate levels of porosity content. In highly concentrated levels of porosity, both yield strength and elongation values decrease markedly. Correlation coefficients were obtained by simple straight line regression analysis between the variables of ultimate tensile strength and pore level. The coefficients were greater, indicating a better correlation, using a pore area accumulation concept or pore volume accumulation than the accumulation of the pore diameters. These relationships provide a useful tool for assessing the existing aerospace radiographic acceptance standards with respect to permissible porosity. In addition, these relationships, in combination with known design load requirements, will serve as an engineering guideline in determining when a weld repair is necessary based on accumulative pore level as detected by radiographic techniques.

Behaviour of square FRP-Confined High-Strength Concrete Columns under Eccentric Compression

NASA Astrophysics Data System (ADS)

Fallah Pour, Ali; Gholampour, Aliakbar; Zheng, Junai; Ozbakkaloglu, Togay

2018-01-01

This paper presents the results of an experimental study on the effect of load eccentricity on the axial compressive behaviour of carbon fibre-reinforced polymer (CFRP)- confined high-strength concrete (HSC) columns with a square cross-section. The axial loading was applied to the specimens at six different load eccentricities ranging from zero to 50 mm. The results show that the load eccentricity significantly influences the axial load-displacement and axial stress-strain behaviour of FRP-confined HSC. Increasing the load eccentricity leads to an increase in the ultimate axial strain but a decrease in the ultimate axial stress and second branch slope of the axial stress-strain curve.

Multiscale structure and damage tolerance of coconut shells.

PubMed

Gludovatz, B; Walsh, F; Zimmermann, E A; Naleway, S E; Ritchie, R O; Kruzic, J J

2017-12-01

We investigated the endocarp of the fruit of Cocos nucifera (i.e., the inner coconut shell), examining the structure across multiple length scales through advanced characterization techniques and in situ testing of mechanical properties. Like many biological materials, the coconut shell possesses a hierarchical structure with distinct features at different length scales that depend on orientation and age. Aged coconut was found to have a significantly stronger (ultimate tensile strength, UTS = 48.5MPa), stiffer (Young's modulus, E = 1.92GPa), and tougher (fracture resistance (R-curve) peak of K J = 3.2MPa m 1/2 ) endocarp than the younger fruit for loading in the latitudinal orientation. While the mechanical properties of coconut shell were observed to improve with age, they also become more anisotropic: the young coconut shell had the same strength (17MPa) and modulus (0.64GPa) values and similar R-curves for both longitudinal and latitudinal loading configurations, whereas the old coconut had 82% higher strength for loading in the latitudinal orientation, and >50% higher crack growth toughness for cracking on the latitudinal plane. Structural aspects affecting the mechanical properties across multiple length scales with aging were identified as improved load transfer to the cellulose crystalline nanostructure (identified by synchrotron x-ray diffraction) and sclerification of the endocarp, the latter of which included closing of the cell lumens and lignification of the cell walls. The structural changes gave a denser and mechanically superior micro and nanostructure to the old coconut shell. Additionally, the development of anisotropy was attributed to the formation of an anisotropic open channel structure throughout the shell of the old coconut that affected both crack initiation during uniaxial tensile tests and the toughening mechanisms of crack trapping and deflection during crack propagation. Copyright © 2017 Elsevier Ltd. All rights reserved.

Matrix density effects on the mechanical properties of SiC/RBSN composites

NASA Technical Reports Server (NTRS)

Bhatt, Ramakrishna T.; Kiser, James D.

1990-01-01

The room temperature mechanical properties were measured for SiC fiber reinforced reaction-bonded silicon nitride composites (SiC/RBSN) of different densities. The composites consisted of approx. 30 vol percent uniaxially aligned 142 micron diameter SiC fibers (Textron SCS-6) in a reaction-bonded Si3N4 matrix. The composite density was varied by changing the consolidation pressure during RBSN processing and by hot isostatically pressing the SiC/RBSN composites. Results indicate that as the consolidation pressure was increased from 27 to 138 MPa, the average pore size of the nitrided composites decreased from 0.04 to 0.02 microns and the composite density increased from 2.07 to 2.45 gm/cc. Nonetheless, these improvements resulted in only small increases in the first matrix cracking stress, primary elastic modulus, and ultimate tensile strength values of the composites. In contrast, HIP consolidation of SiC/RBSN resulted in a fully dense material whose first matrix cracking stress and elastic modulus were approx. 15 and 50 percent higher, respectively, and ultimate tensile strength values were approx. 40 percent lower than those for unHIPed SiC/RBSN composites. The modulus behavior for all specimens can be explained by simple rule-of-mixture theory. Also, the loss in ultimate strength for the HIPed composites appears to be related to a degradation in fiber strength at the HIP temperature. However, the density effect on matrix fracture strength was much less than would be expected based on typical monolithic Si3N4 behavior, suggesting that composite theory is indeed operating. Possible practical implications of these observations are discussed.

Matrix density effects on the mechanical properties of SiC fiber-reinforced silicon nitride matrix properties

NASA Technical Reports Server (NTRS)

Bhatt, Ramakrishna T.; Kiser, Lames D.

1990-01-01

The room temperature mechanical properties were measured for SiC fiber reinforced reaction-bonded silicon nitride composites (SiC/RBSN) of different densities. The composites consisted of approx. 30 vol percent uniaxially aligned 142 micron diameter SiC fibers (Textron SCS-6) in a reaction-bonded Si3N4 matrix. The composite density was varied by changing the consolidation pressure during RBSN processing and by hot isostatically pressing the SiC/RBSN composites. Results indicate that as the consolidation pressure was increased from 27 to 138 MPa, the average pore size of the nitrided composites decreased from 0.04 to 0.02 microns and the composite density increased from 2.07 to 2.45 gm/cc. Nonetheless, these improvements resulted in only small increases in the first matrix cracking stress, primary elastic modulus, and ultimate tensile strength values of the composites. In contrast, HIP consolidation of SiC/RBSN resulted in a fully dense material whose first matrix cracking stress and elastic modulus were approx. 15 and 50 percent higher, respectively, and ultimate tensile strength values were approx. 40 percent lower than those for unHIPed SiC/RBSN composites. The modulus behavior for all specimens can be explained by simple rule-of-mixture theory. Also, the loss in ultimate strength for the HIPed composites appears to be related to a degradation in fiber strength at the HIP temperature. However, the density effect on matrix fracture strength was much less than would be expected based on typical monolithic Si3N4 behavior, suggesting that composite theory is indeed operating. Possible practical implications of these observations are discussed.

Strain rate, temperature, and humidity on strength and moduli of a graphite/epoxy composite

NASA Technical Reports Server (NTRS)

Lifshitz, J. M.

1981-01-01

Results of an experimental study of the influence of strain rate, temperature and humidity on the mechanical behavior of a graphite/epoxy fiber composite are presented. Three principal strengths (longitudinal, transverse and shear) and four basic moduli (E1, E2, G12 and U12) of a unidirectional graphite/epoxy composite were followed as a function of strain rate, temperature and humidity. Each test was performed at a constant tensile strain rate in an environmental chamber providing simultaneous temperature and humidity control. Prior to testing, specimens were given a moisture preconditioning treatment at 60 C. Values for the matrix dominated moduli and strength were significantly influenced by both environmental and rate parameters, whereas the fiber dominated moduli were not. However, the longitudinal strength was significantly influenced by temperature and moisture content. A qualitative explanation for these observations is presented.

Effects of magnetic field strength and particle aggregation on relaxivity of ultra-small dual contrast iron oxide nanoparticles

NASA Astrophysics Data System (ADS)

Ta, Hang T.; Li, Zhen; Wu, Yuao; Cowin, Gary; Zhang, Shaohua; Yago, Anya; Whittaker, Andrew K.; Xu, Zhi Ping

2017-11-01

This study aims to compare the relaxivities of ultra-small dual positive and negative contrast iron oxide nanoparticles (DCION) at different magnetic field strengths ranging from 4.7 to 16.4 T at physiological temperatures; and to investigate the effect of particle aggregation on relaxivities. Relaxivities of DCIONs were determined by magnetic resonance imaging scanners at 4.7, 7, 9.4, and 16.4 T. Both longitudinal (T 1) and transverse relaxation times (T 2) were measured by appropriate spin-echo sequences. It has been found that both longitudinal and transverse relaxivities are significantly dependent on the magnetic field strength. Particle aggregation also strongly affects the relaxivities. Awareness of the field strength and particle colloid stability is crucial for the comparison and evaluation of relaxivity values of these ultra-small iron oxide nanoparticles, and also for their medical applications as contrast agents.

Reduced diaphyseal strength associated with high intracortical vascular porosity within long bones of children with Osteogenesis Imperfecta

PubMed Central

Jameson, John; Smith, Peter; Harris, Gerald

2015-01-01

Osteogenesis Imperfecta is a genetic disorder resulting in bone fragility. The mechanisms behind this fragility are not well understood. In addition to characteristic bone mass deficiencies, research suggests that bone material properties are compromised in individuals with this disorder. However, little data exists regarding bone properties beyond the microstructural scale in individuals with this disorder. Specimens were obtained from long bone diaphyses of nine children with osteogenesis imperfecta during routine osteotomy procedures. Small rectangular beams, oriented longitudinally and transversely to the diaphyseal axis, were machined from these specimens and elastic modulus, yield strength, and maximum strength were measured in three-point bending. Intracortical vascular porosity, bone volume fraction, osteocyte lacuna density, and volumetric tissue mineral density were determined by synchrotron micro-computed tomography, and relationships among these mechanical properties and structural parameters were explored. Modulus and strength were on average 64–68% lower in the transverse vs. longitudinal beams (P<0.001, linear mixed model). Vascular porosity ranged between 3–42% of total bone volume. Longitudinal properties were associated negatively with porosity (P≤0.006, linear regressions). Mechanical properties, however, were not associated with osteocyte lacuna density or volumetric tissue mineral density (P≥0.167). Bone properties and structural parameters were not associated significantly with donor age (p≥0.225, linear mixed models). This study presents novel data regarding bone material strength in children with osteogenesis imperfecta. Results confirm that these properties are anisotropic. Elevated vascular porosity was observed in most specimens, and this parameter was associated with reduced bone material strength. These results offer insight towards understanding bone fragility and the role of intracortical porosity on the strength of bone tissue in children with osteogenesis imperfecta. PMID:24928496

Reduced diaphyseal strength associated with high intracortical vascular porosity within long bones of children with osteogenesis imperfecta.

PubMed

Albert, Carolyne; Jameson, John; Smith, Peter; Harris, Gerald

2014-09-01

Osteogenesis imperfecta is a genetic disorder resulting in bone fragility. The mechanisms behind this fragility are not well understood. In addition to characteristic bone mass deficiencies, research suggests that bone material properties are compromised in individuals with this disorder. However, little data exists regarding bone properties beyond the microstructural scale in individuals with this disorder. Specimens were obtained from long bone diaphyses of nine children with osteogenesis imperfecta during routine osteotomy procedures. Small rectangular beams, oriented longitudinally and transversely to the diaphyseal axis, were machined from these specimens and elastic modulus, yield strength, and maximum strength were measured in three-point bending. Intracortical vascular porosity, bone volume fraction, osteocyte lacuna density, and volumetric tissue mineral density were determined by synchrotron micro-computed tomography, and relationships among these mechanical properties and structural parameters were explored. Modulus and strength were on average 64-68% lower in the transverse vs. longitudinal beams (P<0.001, linear mixed model). Vascular porosity ranged between 3 and 42% of total bone volume. Longitudinal properties were associated negatively with porosity (P≤0.006, linear regressions). Mechanical properties, however, were not associated with osteocyte lacuna density or volumetric tissue mineral density (P≥0.167). Bone properties and structural parameters were not associated significantly with donor age (P≥0.225, linear mixed models). This study presents novel data regarding bone material strength in children with osteogenesis imperfecta. Results confirm that these properties are anisotropic. Elevated vascular porosity was observed in most specimens, and this parameter was associated with reduced bone material strength. These results offer insight toward understanding bone fragility and the role of intracortical porosity on the strength of bone tissue in children with osteogenesis imperfecta. Copyright © 2014 Elsevier Inc. All rights reserved.

Effect of open hole on tensile failure properties of 2D triaxial braided textile composites and tape equivalents

NASA Technical Reports Server (NTRS)

Norman, Timothy L.; Anglin, Colin; Gaskin, David; Patrick, Mike

1995-01-01

The unnotched and notched (open hole) tensile strength and failure mechanisms of two-dimensional (2D) triaxial braided composites were examined. The effect of notch size and notch position were investigated. Damage initiation and propagation in notched and unnotched coupons were also examined. Theory developed to predict the normal stress distribution near an open hole and failure for tape laminated composites was evaluated for its applicability to triaxial braided textile composite materials. Four fiber architectures were considered with different combinations of braid angle, longitudinal and braider yam size, and percentage of longitudinal yarns. Tape laminates equivalent to textile composites were also constructed for comparison. Unnotched tape equivalents were stronger than braided textiles but exhibited greater notch sensitivity. Notched textiles and tape equivalents have roughly the same strength at large notch sizes. Two common damage mechanisms were found: braider yams cracking and near notch longitudinal yarn splitting. Cracking was found to initiate in braider yarns in unnotched and notched coupons, and propagate in the direction of the braider yarns until failure. Longitudinal yarn splitting occurred in three of four architectures that were longitudinally fiber dominated. Damage initiation stress decreased with increasing braid angle. No significant differences in prediction of near notch stress between measured and predicted stress were weak for textiles with large braid angle. Notch strength could not be predicted using existing anisotropic theory for braided textiles due to their insensitivity to notch.

Low temperature mechanical properties, fractographic and metallographic evaluation of several alloy steels

NASA Technical Reports Server (NTRS)

Montano, J. W.

1973-01-01

The mechanical properties are presented of alloy steels, 4130, 4140, 4340, 6150, and 8740. Test specimens were manufactured from approximately 1.00 inch (2.54 cm) diameter bar stock which had been heat treated to two different hardness levels. The following mechanical tests were performed at temperatures of 80 F (+26.7 C), 0 F (-17.8 C), -100 F (-73 C), and -200 F (-129 C): (1) tensile test (Ultimate, yield, modulus, elongation, and reduction of area), (2) notched tensile test, (3) charpy V-notched impact test (impact energy), and (4) double shear strength test (ultimate and yield). The test data indicate excellent tensile strength, notched/unnotched tensile ratios, ductility, impact, and shear properties at all test temperatures, except at -200 F (-129 C) where the impact strength of the higher strength group of alloy steels, 4130 (Rc-37) and 4140 (Rc-44) decreased to approximately 9 ft. lbs. (12 joules) and 6 ft. lbs. (8 joules), respectively. Chemical, metallographic, and fractographic analyses were also performed to evaluate microstructure, microhardness and the effect of decrease in temperature on the ductile to brittle failure transition.

Effect of ZnO nanoparticles to mechanical properties of thixoformed Mg-Al-Zn alloy

NASA Astrophysics Data System (ADS)

Kusharjanto; Soepriyanto, Syoni; Ardian Korda, Akhmad; Adi Dwiwanto, Supono

2018-03-01

Magnesium alloys are lightweight metallic materials with low mechanical properties. Therefore, in order to meet the requirements in various industrial sector applications such as automotive, aerospace and electronic frame, improvement strength and ductility is required. The purpose of this research is to investigate the effect of adding ZnO nanoparticles to changes in microstructure, hardness, mechanical properties regarding with yield and ultimate strength. In this research, the molten Mg-Al-Zn alloy is added ZnO nanoparticles with a various range of 0, 1; 3 and 5 wt% and then cooling in the room temperature. Futhermore, Mg-Al-Zn-ZnO is heated at a temperature of 530 °C (in the semi-solid temperature range 470 °C–595 °C or 53% solid fraction) and then thixoforming process is performed. The characterization results of the thixoforming product show that, the microstructure is globular in shape with maximum hardness value of 107.14 VHN, the yield strength of 214.87 MPa, and the ultimate tensile strength of 311.25 MPa in 5 wt% ZnO nanoparticles.

Alloys For Corrosive, Hydrogen-Rich Environments

NASA Technical Reports Server (NTRS)

Mcpherson, William B.; Bhat, Biliyar N.; Chen, Po-Shou; Kuruvilla, A. K.; Panda, Binayak

1993-01-01

"NASA-23" denotes class of alloys resisting both embrittlement by hydrogen and corrosion. Weldable and castable and formed by such standard processes as rolling, forging, and wire drawing. Heat-treated to obtain desired combinations of strength and ductility in ranges of 100 to 180 kpsi yield strength, 120 to 200 kpsi ultimate tensile strength, and 10 to 30 percent elongation at break. Used in place of most common aerospace structural alloy, Inconel(R) 718.

Stent longitudinal integrity bench insights into a clinical problem.

PubMed

Ormiston, John A; Webber, Bruce; Webster, Mark W I

2011-12-01

Standardized bench-top compression and elongation testing was undertaken to assess the longitudinal strength of contemporary stents. Insights gained may improve clinical stent choice and deployment techniques, and facilitate future stent design improvements. The hoops of coronary stents provide radial support, and connectors hold hoops together. Strut material, shape, and thickness, along with connector number and configuration, provide the balance between stent flexibility and longitudinal integrity. Longitudinal distortion manifests as length change, strut overlap, strut separation, malapposition, and luminal obstruction. These may predispose to restenosis and stent thrombosis, obstruct passage of devices, be misinterpreted as strut fracture, and require additional stenting. The force required to compress and to elongate 7 contemporary stents was measured with an Instron universal testing machine (Norwood, Massachusetts). Stents deployed in a silicone phantom damaged by a balloon or guide catheter were imaged by microcomputed tomography to understand better the appearances and effects of longitudinal distortion. Stents with 2 connectors (Boston Scientific [Natick, Massachusetts] Omega and Medtronic [Santa Rosa, California] Driver) required significantly less force to be compressed up to 5 mm and elongated by 1 mm than designs with more connectors. The 6-connector Cypher Select required significantly more force to be elongated 5 mm than other designs. Stents with 2 connectors between hoops have less longitudinal strength when exposed to compressing or elongating forces than those with more connectors. This independent, standardized study may assist stent selection in clinical situations where longitudinal integrity is important, and may aid future design improvements. Stent longitudinal strength, the resistance to shortening or elongation, appears related to the number of connectors between hoops. Using a standardized testing protocol, designs with 2 connectors were more likely to shorten or elongate than those with more connectors. Distortion may be recognized clinically as bunching or separation of struts, and may be confused with strut fracture. Without post-dilation or further stent deployment, the patient may be at increased risk for adverse clinical events. A stent design change ensuring 3 connectors, especially at the proximal end of a stent, should increase longitudinal integrity, but perhaps at the expense of stent flexibility. Copyright © 2011 American College of Cardiology Foundation. Published by Elsevier Inc. All rights reserved.

Sock Shaped Internal Strength Member for Towed Arrays

DTIC Science & Technology

hose -shaped sheath. The member has a plurality of longitudinally extending high strength cords formed of braids or strands of high tensile strength...interfering with the sensors’ acoustic sensing capabilities. The hose -shaped sheath contains the tubular-shaped strength member in a non-compressive...relationship to reduce the problems normally associated with flow noise. The cords are braided together in an eye-splice where they are wrapped about

Influence of different luting protocols on shear bond strength of computer aided design/computer aided manufacturing resin nanoceramic material to dentin

PubMed Central

Poggio, Claudio; Pigozzo, Marco; Ceci, Matteo; Scribante, Andrea; Beltrami, Riccardo; Chiesa, Marco

2016-01-01

Background: The purpose of this study was to evaluate the influence of three different luting protocols on shear bond strength of computer aided design/computer aided manufacturing (CAD/CAM) resin nanoceramic (RNC) material to dentin. Materials and Methods: In this in vitro study, 30 disks were milled from RNC blocks (Lava Ultimate/3M ESPE) with CAD/CAM technology. The disks were subsequently cemented to the exposed dentin of 30 recently extracted bovine permanent mandibular incisors. The specimens were randomly assigned into 3 groups of 10 teeth each. In Group 1, disks were cemented using a total-etch protocol (Scotchbond™ Universal Etchant phosphoric acid + Scotchbond Universal Adhesive + RelyX™ Ultimate conventional resin cement); in Group 2, disks were cemented using a self-etch protocol (Scotchbond Universal Adhesive + RelyX™ Ultimate conventional resin cement); in Group 3, disks were cemented using a self-adhesive protocol (RelyX™ Unicem 2 Automix self-adhesive resin cement). All cemented specimens were placed in a universal testing machine (Instron Universal Testing Machine 3343) and submitted to a shear bond strength test to check the strength of adhesion between the two substrates, dentin, and RNC disks. Specimens were stressed at a crosshead speed of 1 mm/min. Data were analyzed with analysis of variance and post-hoc Tukey's test at a level of significance of 0.05. Results: Post-hoc Tukey testing showed that the highest shear strength values (P < 0.001) were reported in Group 2. The lowest data (P < 0.001) were recorded in Group 3. Conclusion: Within the limitations of this in vitro study, conventional resin cements (coupled with etch and rinse or self-etch adhesives) showed better shear strength values compared to self-adhesive resin cements. Furthermore, conventional resin cements used together with a self-etch adhesive reported the highest values of adhesion. PMID:27076822

Influence of different luting protocols on shear bond strength of computer aided design/computer aided manufacturing resin nanoceramic material to dentin.

PubMed

Poggio, Claudio; Pigozzo, Marco; Ceci, Matteo; Scribante, Andrea; Beltrami, Riccardo; Chiesa, Marco

2016-01-01

The purpose of this study was to evaluate the influence of three different luting protocols on shear bond strength of computer aided design/computer aided manufacturing (CAD/CAM) resin nanoceramic (RNC) material to dentin. In this in vitro study, 30 disks were milled from RNC blocks (Lava Ultimate/3M ESPE) with CAD/CAM technology. The disks were subsequently cemented to the exposed dentin of 30 recently extracted bovine permanent mandibular incisors. The specimens were randomly assigned into 3 groups of 10 teeth each. In Group 1, disks were cemented using a total-etch protocol (Scotchbond™ Universal Etchant phosphoric acid + Scotchbond Universal Adhesive + RelyX™ Ultimate conventional resin cement); in Group 2, disks were cemented using a self-etch protocol (Scotchbond Universal Adhesive + RelyX™ Ultimate conventional resin cement); in Group 3, disks were cemented using a self-adhesive protocol (RelyX™ Unicem 2 Automix self-adhesive resin cement). All cemented specimens were placed in a universal testing machine (Instron Universal Testing Machine 3343) and submitted to a shear bond strength test to check the strength of adhesion between the two substrates, dentin, and RNC disks. Specimens were stressed at a crosshead speed of 1 mm/min. Data were analyzed with analysis of variance and post-hoc Tukey's test at a level of significance of 0.05. Post-hoc Tukey testing showed that the highest shear strength values (P < 0.001) were reported in Group 2. The lowest data (P < 0.001) were recorded in Group 3. Within the limitations of this in vitro study, conventional resin cements (coupled with etch and rinse or self-etch adhesives) showed better shear strength values compared to self-adhesive resin cements. Furthermore, conventional resin cements used together with a self-etch adhesive reported the highest values of adhesion.

Biomechanical characteristics of single-row repair in comparison to double-row repair with consideration of the suture configuration and suture material.

PubMed

Baums, M H; Buchhorn, G H; Spahn, G; Poppendieck, B; Schultz, W; Klinger, H-M

2008-11-01

The aim of the study was to evaluate the time zero mechanical properties of single- versus double-row configuration for rotator cuff repair in an animal model with consideration of the stitch technique and suture material. Thirty-two fresh-frozen sheep shoulders were randomly assigned to four repair groups: suture anchor single-row repair coupled with (1) braided, nonabsorbable polyester suture sized USP No. 2 (SRAE) or (2) braided polyblend polyethylene suture sized No. 2 (SRAH). The double-row repair was coupled with (3) USP No. 2 (DRAE) or (4) braided polyblend polyethylene suture No. 2 (DRAH). Arthroscopic Mason-Allen stitches were used (single-row) and combined with medial horizontal mattress stitches (double-row). Shoulders were cyclically loaded from 10 to 180 N. Displacement to gap formation of 5- and 10-mm at the repair site, cycles to failure, and the mode of failure were determined. The ultimate tensile strength was verified in specimens that resisted to 3,000 cycles. DRAE and DRAH had a lower frequency of 5- (P = 0.135) and 10-mm gap formation (P = 0.135). All DRAE and DRAH resisted 3,000 cycles while only three SRAE and one SRAH resisted 3,000 cycles (P < 0.001). The ultimate tensile strength in double-row specimens was significantly higher than in others (P < 0.001). There was no significant variation in using different suture material (P > 0.05). Double-row suture anchor repair with arthroscopic Mason-Allen/medial mattress stitches provides initial strength superior to single-row repair with arthroscopic Mason-Allen stitches under isometric cyclic loading as well as under ultimate loading conditions. Our results support the concept of double-row fixation with arthroscopic Mason-Allen/medial mattress stitches in rotator cuff tears with improvement of initial fixation strength and ultimate tensile load. Use of new polyblend polyethylene suture material seems not to increase the initial biomechanical aspects of the repair construct.

Global strength assessment in oblique waves of a large gas carrier ship, based on a non-linear iterative method

NASA Astrophysics Data System (ADS)

Domnisoru, L.; Modiga, A.; Gasparotti, C.

2016-08-01

At the ship's design, the first step of the hull structural assessment is based on the longitudinal strength analysis, with head wave equivalent loads by the ships' classification societies’ rules. This paper presents an enhancement of the longitudinal strength analysis, considering the general case of the oblique quasi-static equivalent waves, based on the own non-linear iterative procedure and in-house program. The numerical approach is developed for the mono-hull ships, without restrictions on 3D-hull offset lines non-linearities, and involves three interlinked iterative cycles on floating, pitch and roll trim equilibrium conditions. Besides the ship-wave equilibrium parameters, the ship's girder wave induced loads are obtained. As numerical study case we have considered a large LPG liquefied petroleum gas carrier. The numerical results of the large LPG are compared with the statistical design values from several ships' classification societies’ rules. This study makes possible to obtain the oblique wave conditions that are inducing the maximum loads into the large LPG ship's girder. The numerical results of this study are pointing out that the non-linear iterative approach is necessary for the computation of the extreme loads induced by the oblique waves, ensuring better accuracy of the large LPG ship's longitudinal strength assessment.

Longitudinal Profiles of Adaptive Behavior in Fragile X Syndrome

PubMed Central

Quintin, Eve-Marie; Jo, Booil; Lightbody, Amy A.; Hazlett, Heather Cody; Piven, Joseph; Hall, Scott S.; Reiss, Allan L.

2014-01-01

OBJECTIVE: To examine longitudinally the adaptive behavior patterns in fragile X syndrome. METHOD: Caregivers of 275 children and adolescents with fragile X syndrome and 225 typically developing children and adolescents (2–18 years) were interviewed with the Vineland Adaptive Behavior Scales every 2 to 4 years as part of a prospective longitudinal study. RESULTS: Standard scores of adaptive behavior in people with fragile X syndrome are marked by a significant decline over time in all domains for males and in communication for females. Socialization skills are a relative strength as compared with the other domains for males with fragile X syndrome. Females with fragile X syndrome did not show a discernible pattern of developmental strengths and weaknesses. CONCLUSIONS: This is the first large-scale longitudinal study to show that the acquisition of adaptive behavior slows as individuals with fragile X syndrome age. It is imperative to ensure that assessments of adaptive behavior skills are part of intervention programs focusing on childhood and adolescence in this condition. PMID:25070318

46 CFR 42.15-25 - Hatchways closed by portable covers and secured weathertight by tarpaulins and battening devices.

Code of Federal Regulations, 2010 CFR

2010-10-01

... maximum stress thus calculated and the factor 4.25 shall not exceed the minimum ultimate strength of the... foot on hatchways in position 2 and the product of the maximum stress thus calculated and the factor 5... product of the maximum stress thus calculated and the factor 5 shall not exceed the minimum ultimate...

46 CFR 42.15-25 - Hatchways closed by portable covers and secured weathertight by tarpaulins and battening devices.

Code of Federal Regulations, 2011 CFR

2011-10-01

... maximum stress thus calculated and the factor 4.25 shall not exceed the minimum ultimate strength of the... foot on hatchways in position 2 and the product of the maximum stress thus calculated and the factor 5... product of the maximum stress thus calculated and the factor 5 shall not exceed the minimum ultimate...

46 CFR 42.15-25 - Hatchways closed by portable covers and secured weathertight by tarpaulins and battening devices.

Code of Federal Regulations, 2012 CFR

2012-10-01

... maximum stress thus calculated and the factor 4.25 shall not exceed the minimum ultimate strength of the... foot on hatchways in position 2 and the product of the maximum stress thus calculated and the factor 5... product of the maximum stress thus calculated and the factor 5 shall not exceed the minimum ultimate...

46 CFR 42.15-25 - Hatchways closed by portable covers and secured weathertight by tarpaulins and battening devices.

Code of Federal Regulations, 2014 CFR

2014-10-01

... maximum stress thus calculated and the factor 4.25 shall not exceed the minimum ultimate strength of the... foot on hatchways in position 2 and the product of the maximum stress thus calculated and the factor 5... product of the maximum stress thus calculated and the factor 5 shall not exceed the minimum ultimate...

46 CFR 42.15-25 - Hatchways closed by portable covers and secured weathertight by tarpaulins and battening devices.

Code of Federal Regulations, 2013 CFR

2013-10-01

... maximum stress thus calculated and the factor 4.25 shall not exceed the minimum ultimate strength of the... foot on hatchways in position 2 and the product of the maximum stress thus calculated and the factor 5... product of the maximum stress thus calculated and the factor 5 shall not exceed the minimum ultimate...

Repair of earthquake damaged bridge columns with fractured bars.

DOT National Transportation Integrated Search

2013-07-01

The objective of this study is to repair three, half-scale RC bridge columns that will be tested to failure under slow cyclic loading. : These columns will have fractured longitudinal and transverse steel. The ultimate goal is to develop repair metho...

Strength and deformability of compressed concrete elements with various types of non-metallic fiber and rods reinforcement under static loading

NASA Astrophysics Data System (ADS)

Nevskii, A. V.; Baldin, I. V.; Kudyakov, K. L.

2015-01-01

Adoption of modern building materials based on non-metallic fibers and their application in concrete structures represent one of the important issues in construction industry. This paper presents results of investigation of several types of raw materials selected: basalt fiber, carbon fiber and composite fiber rods based on glass and carbon. Preliminary testing has shown the possibility of raw materials to be effectively used in compressed concrete elements. Experimental program to define strength and deformability of compressed concrete elements with non-metallic fiber reinforcement and rod composite reinforcement included design, manufacture and testing of several types of concrete samples with different types of fiber and longitudinal rod reinforcement. The samples were tested under compressive static load. The results demonstrated that fiber reinforcement of concrete allows increasing carrying capacity of compressed concrete elements and reducing their deformability. Using composite longitudinal reinforcement instead of steel longitudinal reinforcement in compressed concrete elements insignificantly influences bearing capacity. Combined use of composite rod reinforcement and fiber reinforcement in compressed concrete elements enables to achieve maximum strength and minimum deformability.

Micro-Mechanical Analysis About Kink Band in Carbon Fiber/Epoxy Composites Under Longitudinal Compression

NASA Astrophysics Data System (ADS)

Zhang, Mi; Guan, Zhidong; Wang, Xiaodong; Du, Shanyi

2017-10-01

Kink band is a typical phenomenon for composites under longitudinal compression. In this paper, theoretical analysis and finite element simulation were conducted to analyze kink angle as well as compressive strength of composites. Kink angle was considered to be an important character throughout longitudinal compression process. Three factors including plastic matrix, initial fiber misalignment and rotation due to loading were considered for theoretical analysis. Besides, the relationship between kink angle and fiber volume fraction was improved and optimized by theoretical derivation. In addition, finite element models considering fiber stochastic strength and Drucker-Prager constitutive model for matrix were conducted in ABAQUS to analyze kink band formation process, which corresponded with the experimental results. Through simulation, the loading and failure procedure can be evidently divided into three stages: elastic stage, softening stage, and fiber break stage. It also shows that kink band is a result of fiber misalignment and plastic matrix. Different values of initial fiber misalignment angle, wavelength and fiber volume fraction were considered to explore the effects on compressive strength and kink angle. Results show that compressive strength increases with the decreasing of initial fiber misalignment angle, the decreasing of initial fiber misalignment wavelength and the increasing of fiber volume fraction, while kink angle decreases in these situations. Orthogonal array in statistics was also built to distinguish the effect degree of these factors. It indicates that initial fiber misalignment angle has the largest impact on compressive strength and kink angle.

The Cryogenic Tensile Properties of an Extruded Aluminum-Beryllium Alloy

NASA Technical Reports Server (NTRS)

Gamwell, W. R.

2002-01-01

Basic mechanical properties; i.e., ultimate tensile strength, yield strength, percent elongation, and elastic modulus, were obtained for the aluminum-beryllium alloy, AlBeMet162, at cryogenic (-195.5 C (-320 F) and -252.8 C (-423 F)) temperatures. The material evaluated was purchased to the requirements of SAE-AMS7912, "Aluminum-Beryllium Alloy, Extrusions."

Hypersonic Wind Tunnel Nozzle Survivability for T&E

DTIC Science & Technology

2007-03-01

Room-Temperature Compression Tests ..............................................................43 10. Strength of Hot-Rolled Inconel 600 (Ni-16Cr...6Fe, wt %) ...................................................45 11. Physical Properties of Inconel 600...Table 10. Strength of Hot-Rolled Inconel 600 (Ni-16Cr-6Fe, wt%) T, °C 0.2% Yield Stress (MPa) Ultimate Tensile Stress (MPa) 20 250 590 400 185 560

Fibre-matrix bond strength studies of glass, ceramic, and metal matrix composites

NASA Technical Reports Server (NTRS)

Grande, D. H.; Mandell, J. F.; Hong, K. C. C.

1988-01-01

An indentation test technique for compressively loading the ends of individual fibers to produce debonding has been applied to metal, glass, and glass-ceramic matrix composites; bond strength values at debond initiation are calculated using a finite-element model. Results are correlated with composite longitudinal and interlaminar shear behavior for carbon and Nicalon fiber-reinforced glasses and glass-ceramics including the effects of matrix modifications, processing conditions, and high-temperature oxidation embrittlement. The data indicate that significant bonding to improve off-axis and shear properties can be tolerated before the longitudinal behavior becomes brittle. Residual stress and other mechanical bonding effects are important, but improved analyses and multiaxial interfacial failure criteria are needed to adequately interpret bond strength data in terms of composite performance.

Shear bond strength of computer-aided design and computer-aided manufacturing feldspathic and nano resin ceramics blocks cemented with three different generations of resin cement.

PubMed

Ab-Ghani, Zuryati; Jaafar, Wahyuni; Foo, Siew Fon; Ariffin, Zaihan; Mohamad, Dasmawati

2015-01-01

To evaluate the shear bond strength between the dentin substrate and computer-aided design and computer-aided manufacturing feldspathic ceramic and nano resin ceramics blocks cemented with resin cement. Sixty cuboidal blocks (5 mm × 5 mm × 5 mm) were fabricated in equal numbers from feldspathic ceramic CEREC(®) Blocs PC and nano resin ceramic Lava™ Ultimate, and randomly divided into six groups (n = 10). Each block was cemented to the dentin of 60 extracted human premolar using Variolink(®) II/Syntac Classic (multi-steps etch-and-rinse adhesive bonding), NX3 Nexus(®) (two-steps etch-and-rinse adhesive bonding) and RelyX™ U200 self-adhesive cement. All specimens were thermocycled, and shear bond strength testing was done using the universal testing machine at a crosshead speed of 1.0 mm/min. Data were analyzed using one-way ANOVA. Combination of CEREC(®) Blocs PC and Variolink(®) II showed the highest mean shear bond strength (8.71 Mpa), while the lowest of 2.06 Mpa were observed in Lava™ Ultimate and RelyX™ U200. There was no significant difference in the mean shear bond strength between different blocks. Variolink(®) II cement using multi-steps etch-and-rinse adhesive bonding provided a higher shear bond strength than the self-adhesive cement RelyX U200. The shear bond strength was not affected by the type of blocks used.

High Temperature Tensile Properties of Unidirectional Hi-Nicalon/Celsian Composites In Air

NASA Technical Reports Server (NTRS)

Gyekenyesi, John Z.; Bansal, Narottam P.

2000-01-01

High temperature tensile properties of unidirectional BN/SiC-coated Hi-Nicalon SiC fiber reinforced celsian matrix composites have been measured from room temperature to 1200 C (2190 F) in air. Young's modulus, the first matrix cracking stress, and the ultimate strength decreased from room temperature to 1200 C (2190 F). The applicability of various micromechanical models, in predicting room temperature values of various mechanical properties for this CMC, has also been investigated. The simple rule of mixtures produced an accurate estimate of the primary composite modulus. The first matrix cracking stress estimated from ACK theory was in good agreement with the experimental value. The modified fiber bundle failure theory of Evans gave a good estimate of the ultimate strength.

Individual and Environmental Characteristics Associated with Cognitive Development in Down Syndrome: A Longitudinal Study

ERIC Educational Resources Information Center

Couzens, Donna; Haynes, Michele; Cuskelly, Monica

2012-01-01

Background: Associations among cognitive development and intrapersonal and environmental characteristics were investigated for 89 longitudinal study participants with Down syndrome to understand developmental patterns associated with cognitive strengths and weaknesses. Materials and Methods: Subtest scores of the Stanford-Binet IV collected…

Addition of zinc methacrylate in dental polymers: MMP-2 inhibition and ultimate tensile strength evaluation.

PubMed

Henn, Sandrina; de Carvalho, Rodrigo Varella; Ogliari, Fabrício Aulo; de Souza, Ana Paula; Line, Sergio Roberto Peres; da Silva, Adriana Fernandes; Demarco, Flávio Fernando; Etges, Adriana; Piva, Evandro

2012-04-01

This study evaluated the effect of zinc methacrylate (ZM) on the inhibition of matrix metalloproteinase 2 (MMP-2) and the ultimate tensile strength (UTS) of an experimental polymer. Enzymes secreted from mouse gingival tissues were analyzed by gelatin zymography in buffers containing 5 mM CaCl(2) (Tris-CaCl(2)) in 50 mM Tris-HCl buffer with various concentrations of ZM (0.5, 1, 2, 4, 8, and 16 mM). The matrix metalloproteinases present in the conditioned media were characterized by immunoprecipitation. The polymer UTS evaluation was performed in eight groups with various concentrations of ZM (0, 0.5, 1, 2.5, 5, 10, 20, and 30 wt.%), in a mechanical testing machine. MMP-2 (62 kDa) was detected in the zymographic assays and inhibited by ZM in all tested concentrations. UTS data were submitted to one-way ANOVA and Tukey's test (α = 0.05), and no significant differences were observed among groups, except in the polymer containing 30% ZM, presenting a significantly lower value when compared with the control group (p < 0.05). The results suggest that ZM inhibits MMP-2 expression in all concentrations tested, while small concentrations did not affect the ultimate tensile strength of the polymer. Zinc methacrylate is a metalloproteinase inhibitor that can be copolymerized with other methacrylate monomers. Yet, the addition of ZM did not affect the resin bond strength. Thus, in vivo tests should be performed to evaluate the performance of this material.

Study of fatigue behavior of longitudinal welded pipes

NASA Astrophysics Data System (ADS)

Simion, P.; Dia, V.; Istrate, B.; Hrituleac, G.; Hrituleac, I.; Munteanu, C.

2016-08-01

During transport and storage of the various fluids, welded pipes are subjected to cyclic loading due to pressure fluctuations that often exceed the prescribed values for normal operation. These cyclic loading can significantly reduce the life of the pipes; as a result the design should be based on the fatigue strength not only on static resistance. In general the fatigue strength of pipes is dependent by strength, pipe geometry and surface quality. In case of the electric longitudinal welded pipes, the fatigue strength is significantly limited by concentration of residual stress and the size of existing defects in the weld seam. This paper presents the fatigue behaviour of the electric welded pipes by high frequency, under conditions that simulate real operating conditions pipes. Fatigue testing was performed on welded pipes made of micro alloyed carbon steels. Some of these pipes were previously subjected to a heat treatment of normalization, in order to also determine the influence of heat treatment on the fatigue strength of welded pipes. To determine and correlate the different factors affecting the fatigue strength, welded pipes were also subjected to various tests: tensile tests, impact tests, measurement of micro hardness, microstructural analysis by optical microscopy and scanning electron microscopy.

The ROOTS study: a 10-year review of findings on adolescent depression, and recommendations for future longitudinal research.

PubMed

Lewis, Gemma; Jones, Peter B; Goodyer, Ian M

2016-02-01

The purpose of this study is to review longitudinal findings on adolescent mental health from the 'ROOTS study', and provide directions and recommendations for future longitudinal research. To do this, we discuss relevant findings from the ROOTS study, and review its strengths and limitations. We examined all publications from the ROOTS study up to July 2015, selected those examining adolescent mental health, and classified them as investigating (a) childhood risk factors for adolescent depression, (b) genetic and cognitive vulnerability to depression in adolescence, (c) genetic markers, childhood adversities, and neuroendophenotypes, (d) morning cortisol and depression, (e) physical activity and depression symptoms, and (f) the underlying structure of mental health in adolescence. We reviewed the strengths and limitations of the ROOTS study, and how they feed into recommendations for future longitudinal research. There was evidence supporting a putative hormonal biomarker for the emergence of depression in boys. Environmental pathways from child adversity to adolescent depression were confirmed in girls, partly accounted for by negative life events in early adolescence. The preceding role of automatic cognitive biases assessed using behavioural tasks was substantiated, with evidence for genetic susceptibility. Novel latent statistical models of child adversity, depression, anxiety, and psychotic experiences were produced, with concurrent and prospective validity. Our experiences conducting the ROOTS study resulted in a set of strengths, limitations, and recommendations for future longitudinal studies. The ROOTS study has advanced knowledge on the aetiology of adolescent depression by investigating environmental, genetic, hormonal, and neural risk factors. Findings provide a foundation for future research integrating cognitive neuroscience with epidemiology.

Evaluation of peripheral muscle strength of patients undergoing elective cardiac surgery: a longitudinal study

PubMed Central

Santos, Kelli Maria Souza; de Cerqueira Neto, Manoel Luiz; Carvalho, Vitor Oliveira; de Santana Filho, Valter Joviniano; da Silva Junior, Walderi Monteiro; Araújo Filho, Amaro Afrânio; Cerqueira, Telma Cristina Fontes; Cacau, Lucas de Assis Pereira

2014-01-01

Introduction Peripheral muscle strength has been little explored in the literature in the context of cardiac rehabilitation. Objective To evaluate the peripheral muscle strength of patients undergoing elective cardiac surgery. Methods This was a longitudinal observational study. The peripheral muscle strength was measured using isometric dynamometry lower limb (knee extensors and flexors) at three different times: preoperatively (M1), the day of discharge (M2) and hospital discharge (M3). Participants received physiotherapy pre and postoperatively during the days of hospitalization during the morning and afternoon. Results Twenty-two patients were evaluated. The values of peripheral muscle strength of knee extensors preoperative found were about 50% lower than those predicted for the healthy population. When comparing muscle strength prior (M1), with the remaining evaluation, found himself in a fall of 29% for the movement of knee extension and 25% for knee flexion in M2 and a decrease of 10% movement for knee extension and 13% for knee flexion in M3 when comparing with M1. Conclusion The values of peripheral muscle strength prior of the study patients were lower than predicted for the healthy population of the same age. After the surgical event this reduction is even more remarkable, being reestablished until the time of discharge, to values close to baseline. PMID:25372909

Evaluation of peripheral muscle strength of patients undergoing elective cardiac surgery: a longitudinal study.

PubMed

Santos, Kelli Maria Souza; Cerqueira Neto, Manoel Luiz de; Carvalho, Vitor Oliveira; Santana Filho, Valter Joviniano de; Silva Junior, Walderi Monteiro da; Araújo Filho, Amaro Afrânio; Cerqueira, Telma Cristina Fontes; Cacau, Lucas de Assis Pereira

2014-01-01

Peripheral muscle strength has been little explored in the literature in the context of cardiac rehabilitation. To evaluate the peripheral muscle strength of patients undergoing elective cardiac surgery. This was a longitudinal observational study. The peripheral muscle strength was measured using isometric dynamometry lower limb (knee extensors and flexors) at three different times: preoperatively (M1), the day of discharge (M2) and hospital discharge (M3). Participants received physiotherapy pre and postoperatively during the days of hospitalization during the morning and afternoon. Twenty-two patients were evaluated. The values of peripheral muscle strength of knee extensors preoperative found were about 50% lower than those predicted for the healthy population. When comparing muscle strength prior (M1), with the remaining evaluation, found himself in a fall of 29% for the movement of knee extension and 25% for knee flexion in M2 and a decrease of 10% movement for knee extension and 13% for knee flexion in M3 when comparing with M1. The values of peripheral muscle strength prior of the study patients were lower than predicted for the healthy population of the same age. After the surgical event this reduction is even more remarkable, being reestablished until the time of discharge, to values close to baseline.

Responsiveness of performance-based outcome measures for mobility, balance, muscle strength and manual dexterity in adults with myotonic dystrophy type 1.

PubMed

Kierkegaard, Marie; Petitclerc, Émilie; Hébert, Luc J; Mathieu, Jean; Gagnon, Cynthia

2018-02-28

To assess changes and responsiveness in outcome measures of mobility, balance, muscle strength and manual dexterity in adults with myotonic dystrophy type 1. A 9-year longitudinal study conducted with 113 patients. The responsiveness of the Timed Up and Go test, Berg Balance Scale, quantitative muscle testing, grip and pinch-grip strength, and Purdue Pegboard Test was assessed using criterion and construct approaches. Patient-reported perceived changes (worse/stable) in balance, walking, lower-limb weakness, stair-climbing and hand weakness were used as criteria. Predefined hypotheses about expected area under the receiver operating characteristic curves (criterion approach) and correlations between relative changes (construct approach) were explored. The direction and magnitude of median changes in outcome measures corresponded with patient-reported changes. Median changes in the Timed Up and Go test, grip strength, pinch-grip strength and Purdue Pegboard Test did not, in general, exceed known measurement errors. Most criterion (72%) and construct (70%) approach hypotheses were supported. Promising responsiveness was found for outcome measures of mobility, balance and muscle strength. Grip strength and manual dexterity measures showed poorer responsiveness. The performance-based outcome measures captured changes over the 9-year period and responsiveness was promising. Knowledge of measurement errors is needed to interpret the meaning of these longitudinal changes.

Tensile strengths of polyamide based 3D printed polymers in liquid nitrogen

NASA Astrophysics Data System (ADS)

Cruz, P.; Shoemake, E. D.; Adam, P.; Leachman, J.

2015-12-01

Advances in additive manufacturing technology have made 3D printing a viable solution for many industries, allowing for the manufacture of designs that could not be made through traditional subtractive methods. Applicability of additive manufacturing in cryogenic applications is hindered, however, by a lack of accurate material properties information. Nylon is available for printing using fused deposition modeling (FDM) and selective laser sintering (SLS). We selected 5 SLS (DuraForm® EX, DuraForm® HST, DuraForm® PA, PA 640-GSL, and PA 840-GSL) and 2 FDM (Nylon 12, ULTEM) nylon variants based on the bulk material properties and printed properties at room temperature. Tensile tests were performed on five samples of each material while immersed in liquid nitrogen at approximately 77 Kelvin. Samples were tested in XY and, where available, Z printing directions to determine influence on material properties. Results show typical SLS and FDM nylon ultimate strength retention at 77 K, when compared to (extruded or molded) nylon ultimate strength.

Biaxial Normal Strength Behavior in the Axial-Transverse Plane for Human Trabecular Bone—Effects of Bone Volume Fraction, Microarchitecture, and Anisotropy

PubMed Central

Sanyal, Arnav; Keaveny, Tony M.

2013-01-01

The biaxial failure behavior of the human trabecular bone, which has potential relevance both for fall and gait loading conditions, is not well understood, particularly for low-density bone, which can display considerable mechanical anisotropy. Addressing this issue, we investigated the biaxial normal strength behavior and the underlying failure mechanisms for human trabecular bone displaying a wide range of bone volume fraction (0.06–0.34) and elastic anisotropy. Micro-computer tomography (CT)-based nonlinear finite element analysis was used to simulate biaxial failure in 15 specimens (5 mm cubes), spanning the complete biaxial normal stress failure space in the axial-transverse plane. The specimens, treated as approximately transversely isotropic, were loaded in the principal material orientation. We found that the biaxial stress yield surface was well characterized by the superposition of two ellipses—one each for yield failure in the longitudinal and transverse loading directions—and the size, shape, and orientation of which depended on bone volume fraction and elastic anisotropy. However, when normalized by the uniaxial tensile and compressive strengths in the longitudinal and transverse directions, all of which depended on bone volume fraction, microarchitecture, and mechanical anisotropy, the resulting normalized biaxial strength behavior was well described by a single pair of (longitudinal and transverse) ellipses, with little interspecimen variation. Taken together, these results indicate that the role of bone volume fraction, microarchitecture, and mechanical anisotropy is mostly accounted for in determining the uniaxial strength behavior and the effect of these parameters on the axial-transverse biaxial normal strength behavior per se is minor. PMID:24121715

The compressive failure of graphite/epoxy plates with circular holes

NASA Technical Reports Server (NTRS)

Knauss, J. F.; Starnes, J. H., Jr.; Henneke, E. G., II

1978-01-01

The behavior of fiber reinforced composite plates containing a circular cutout was characterized in terms of geometry (thickness, width, hole diameter), and material properties (bending/extensional stiffness). Results were incorporated in a data base for use by designers in determining the ultimate strength of such a structure. Two thicknesses, 24 plies and 48 plies were chosen to differentiate between buckling and strength failures due to the presence of a cutout. Consistent post-buckling strength was exhibited by both laminate configurations.

The Tension and Puncture Properties of HDPE Geomembrane under the Corrosion of Leachate.

PubMed

Xue, Qiang; Zhang, Qian; Li, Zhen-Ze; Xiao, Kai

2013-09-17

To investigate the gradual failure of high-density polyethylene (HDPE) geomembrane as a result of long-term corrosion, four dynamic corrosion tests were conducted at different temperatures and durations. By combining tension and puncture tests, we systematically studied the variation law of tension and puncture properties of the HDPE geomembrane under different corrosion conditions. Results showed that tension and puncture failure of the HDPE geomembrane was progressive, and tensile strength in the longitudinal grain direction was evidently better than that in the transverse direction. Punctures appeared shortly after puncture force reached the puncture strength. The tensile strength of geomembrane was in inversely proportional to the corrosion time, and the impact of corrosion was more obvious in the longitudinal direction than transverse direction. As corrosion time increased, puncture strength decreased and corresponding deformation increased. As with corrosion time, the increase of corrosion temperature induced the decrease of geomembrane tensile strength. Tensile and puncture strength were extremely sensitive to temperature. Overall, residual strength had a negative correlation with corrosion time or temperature. Elongation variation increased initially and then decreased with the increase in temperature. However, it did not show significant law with corrosion time. The reduction in puncture strength and the increase in puncture deformation had positive correlations with corrosion time or temperature. The geomembrane softened under corrosion condition. The conclusion may be applicable to the proper designing of the HDPE geomembrane in landfill barrier system.

Influence of Welding Strength Matching Coefficient and Cold Stretching on Welding Residual Stress in Austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Lu, Yaqing; Hui, Hu; Gong, Jianguo

2018-05-01

Austenitic stainless steel is widely used in pressure vessels for the storage and transportation of liquid gases such as liquid nitrogen, liquid oxygen, and liquid hydrogen. Cryogenic pressure vessel manufacturing uses cold stretching technology, which relies heavily on welding joint performance, to construct lightweight and thin-walled vessels. Residual stress from welding is a primary factor in cases of austenitic stainless steel pressure vessel failure. In this paper, on the basis of Visual Environment 10.0 finite element simulation technology, the residual stress resulting from different welding strength matching coefficients (0.8, 1, 1.2, 1.4) for two S30408 plates welded with three-pass butt welds is calculated according to thermal elastoplastic theory. In addition, the stress field was calculated under a loading as high as 410 MPa and after the load was released. Path 1 was set to analyze stress along the welding line, and path 2 was set to analyze stress normal to the welding line. The welding strength matching coefficient strongly affected both the longitudinal residual stress (center of path 1) and the transverse residual stress (both ends of path 1) after the welding was completed. However, the coefficient had little effect on the longitudinal and transverse residual stress of path 2. Under the loading of 410 MPa, the longitudinal and transverse stress decreased and the stress distribution, with different welding strength matching coefficients, was less diverse. After the load was released, longitudinal and transverse stress distribution for both path 1 and path 2 decreased to a low level. Cold stretching could reduce the effect of residual stress to various degrees. Transverse strain along the stretching direction was also taken into consideration. The experimental results validated the reliability of the partial simulation.

Transverse stresses and modes of failure in tree branches and other beams.

PubMed

Ennos, A R; van Casteren, A

2010-04-22

The longitudinal stresses in beams subjected to bending also set up transverse stresses within them; they compress the cross section when the beam's curvature is being increased and stretch it when its curvature is being reduced. Analysis shows that transverse stresses rise to a maximum at the neutral axis and increase with both the bending moment applied and the curvature of the beam. These stresses can qualitatively explain the fracture behaviour of tree branches. Curved 'hazard beams' that are being straightened split down the middle because of the low transverse tensile strength of wood. By contrast, straight branches of light wood buckle when they are bent because of its low transverse compressive strength. Branches of denser wood break, but the low transverse tensile strength diverts the crack longitudinally when the fracture has only run half-way across the beam, to produce their characteristic 'greenstick fracture'. The bones of young mammals and uniaxially reinforced composite beams may also be prone to greenstick fracture because of their lower transverse tensile strength.

A method of calculating the ultimate strength of continuous beams

NASA Technical Reports Server (NTRS)

Newlin, J A; Trayer, George W

1931-01-01

The purpose of this study was to investigate the strength of continuous beams after the elastic limit has been passed. As a result, a method of calculation, which is applicable to maximum load conditions, has been developed. The method is simpler than the methods now in use and it applies properly to conditions where the present methods fail to apply.

Vitamin K2 improves femoral bone strength without altering bone mineral density in gastrectomized rats.

PubMed

Iwamoto, Jun; Sato, Yoshihiro; Matsumoto, Hideo

2014-01-01

Gastrectomy (GX) induces osteopenia in rats. The present study examined the skeletal effects of vitamin K2 in GX rats. Thirty male Sprague-Dawley rats (12 wk old) were randomized by the stratified weight method into the following three groups of 10 animals each: sham operation (control) group; GX group; and GX+oral vitamin K2 (menatetrenone, 30 mg/kg, 5 d/wk) group. Treatment was initiated at 1 wk after surgery. After 6 wk of treatment, the bone mineral content (BMC), bone mineral density (BMD), and mechanical strength of the femoral diaphysis and distal metaphysis were determined by peripheral quantitative computed tomography and mechanical strength tests, respectively. GX induced decreases in the BMC, BMD, and ultimate force of the femoral diaphysis and distal metaphysis. Vitamin K2 did not significantly influence the BMC or BMD of the femoral diaphysis or distal metaphysis in GX rats, but attenuated the decrease in the ultimate force and increased the stiffness of the femoral diaphysis. The present study showed that administration of vitamin K2 to GX rats improved the bone strength of the femoral diaphysis without altering the BMC or BMD, suggesting effects of vitamin K2 on the cortical bone quality.

Parametric Optimization Of Gas Metal Arc Welding Process By Using Grey Based Taguchi Method On Aisi 409 Ferritic Stainless Steel

NASA Astrophysics Data System (ADS)

Ghosh, Nabendu; Kumar, Pradip; Nandi, Goutam

2016-10-01

Welding input process parameters play a very significant role in determining the quality of the welded joint. Only by properly controlling every element of the process can product quality be controlled. For better quality of MIG welding of Ferritic stainless steel AISI 409, precise control of process parameters, parametric optimization of the process parameters, prediction and control of the desired responses (quality indices) etc., continued and elaborate experiments, analysis and modeling are needed. A data of knowledge - base may thus be generated which may be utilized by the practicing engineers and technicians to produce good quality weld more precisely, reliably and predictively. In the present work, X-ray radiographic test has been conducted in order to detect surface and sub-surface defects of weld specimens made of Ferritic stainless steel. The quality of the weld has been evaluated in terms of yield strength, ultimate tensile strength and percentage of elongation of the welded specimens. The observed data have been interpreted, discussed and analyzed by considering ultimate tensile strength ,yield strength and percentage elongation combined with use of Grey-Taguchi methodology.

Immobilization in cement mortar of chromium removed from water using titania nanoparticles.

PubMed

Husnain, Ahmed; Qazi, Ishtiaq Ahmed; Khaliq, Wasim; Arshad, Muhammad

2016-05-01

Because of the high toxicity of chromium, particularly as Cr (VI), it is removed from industrial effluents before their discharge into water bodies by a variety of techniques, including adsorption. Ultimate disposal of the sludge or the adsorbate, however, is a serious problem. While titania, in nanoparticle form, serves as a very good adsorbent for chromium, as an additive, it also helps to increase the compressive strength of mortar and concrete. Combining these two properties of the material, titania nanoparticles were used to adsorb chromium and then added to mortar up to a concentration of 20% by weight. The compressive strength of the resulting mortar specimens that replaced 15% of cement with chromium laden titania showed an improved strength than that without titania, thus confirming that this material had positive effect on the mortar strength. Leachate tests using the Toxicity Characteristics Leaching Procedure (TCLP) confirmed that the mortar sample chromium leachate was well within the permissible limits. The proposed technique thus offers a safe and viable method for the ultimate disposal of toxic metal wastes, in general, and those laden waste chromium, in particular. Copyright © 2016 Elsevier Ltd. All rights reserved.

Cellular interactions and biomechanical properties of a unique vascular-derived scaffold for periodontal tissue regeneration.

PubMed

Goktas, Selda; Pierre, Nicolas; Abe, Koki; Dmytryk, John; McFetridge, Peter S

2010-03-01

These investigations describe the development of a novel ex vivo three-dimensional scaffold derived from the human umbilical vein (HUV), and its potential as a regenerative matrix for tissue regeneration. Unique properties associated with the vascular wall have shown potential to function as a surgical barrier for guided tissue regeneration, particularly with the regeneration of periodontal tissues. HUV was isolated from umbilical cords using a semiautomated machining technology, decellularized using 1% sodium dodecyl sulfate, and then opened longitudinally to form tissue sheets. Uniaxial tensile testing, stress relaxation, and suture retention tests were performed on the acellular matrix to evaluate the HUV's biomechanical properties, followed by an evaluation of cellular interactions by seeding human gingival fibroblasts to assess adhesion, metabolic function, and proliferation on the scaffold. The scaffold's biomechanical properties were shown to display anisotropic behavior, which is attributed to the ex vivo material's composite structure. Detailed results indicated that the ultimate tensile strength of the longitudinal strips was significantly higher than that of the circumferential strips (p < 0.001). The HUV also exhibited significantly higher stress relaxation response in the longitudinal direction than in the circumferential orientation (p < 0.05). The ablumenal and lumenal surfaces of the material were also shown to differentially influence cell proliferation and metabolic activity, with both cellular functions significantly increased on the ablumenal surface (p < 0.05). Human gingival fibroblast migration into the scaffold was also influenced by the organization of extracellular matrix components, where the lumenal surface inhibits cell migration, acting as a barrier, while the ablumenal surface, which is proposed to interface with the wound site, promotes cellular invasion. These results show the HUV bioscaffold to be a promising naturally derived surgical barrier that may function well as a resorbable guided tissue regeneration membrane as well as in other clinical applications.

The stress corrosion resistance and the cryogenic temperature mechanical properties of hot rolled Nitronic 32 bar material

NASA Technical Reports Server (NTRS)

Montano, J. W. L.

1977-01-01

The ambient and cryogenic temperature mechanical properties and the ambient temperature stress corrosion properties of hot rolled and centerless ground Nitronic 32 stainless steel bar material are presented. The mechanical properties of longitudinal specimens were evaluated at test temperatures from ambient to liquid hydrogen. The tensile test data indicated increasing smooth tensile strength with decreasing temperature to liquid hydrogen temperature. However, below -200 F (-129.0 C) the notched tensile strength decreased slightly and below -320 F (-196.0 C) the decrease was significant. The elongation and reduction of area decreased drastically at temperatures below -200 F (-129.0 C). The Charpy V-notched impact energy decreased steadily with decreasing test temperature. Stress corrosion tests were performed on longitudinal tensile specimens stressed to 0, 75, and 90 percent of the 0.2 percent yield strength and on transverse 'C'-ring specimens stressed to 75 and 90 percent of the yield strength and exposed to: alternate immersion in a 3.5 percent NaCl bath, humidity cabinet environment, and a 5 percent salt spray atmosphere. The longitudinal tensile specimens experienced no corrosive attack; however, the 'C'-rings exposed to the alternate immersion and to the salt spray experienced some shallow etching and pitting, respectively. Small cracks appeared in two of the 'C'-rings after one month exposure to the salt spray.

A human pericardium biopolymeric scaffold for autologous heart valve tissue engineering: cellular and extracellular matrix structure and biomechanical properties in comparison with a normal aortic heart valve.

PubMed

Straka, Frantisek; Schornik, David; Masin, Jaroslav; Filova, Elena; Mirejovsky, Tomas; Burdikova, Zuzana; Svindrych, Zdenek; Chlup, Hynek; Horny, Lukas; Daniel, Matej; Machac, Jiri; Skibová, Jelena; Pirk, Jan; Bacakova, Lucie

2018-04-01

The objective of our study was to compare the cellular and extracellular matrix (ECM) structure and the biomechanical properties of human pericardium (HP) with the normal human aortic heart valve (NAV). HP tissues (from 12 patients) and NAV samples (from 5 patients) were harvested during heart surgery. The main cells in HP were pericardial interstitial cells, which are fibroblast-like cells of mesenchymal origin similar to the valvular interstitial cells in NAV tissue. The ECM of HP had a statistically significantly (p < 0.001) higher collagen I content, a lower collagen III and elastin content, and a similar glycosaminoglycans (GAGs) content, in comparison with the NAV, as measured by ECM integrated density. However, the relative thickness of the main load-bearing structures of the two tissues, the dense part of fibrous HP (49 ± 2%) and the lamina fibrosa of NAV (47 ± 4%), was similar. In both tissues, the secant elastic modulus (Es) was significantly lower in the transversal direction (p < 0.05) than in the longitudinal direction. This proved that both tissues were anisotropic. No statistically significant differences in UTS (ultimate tensile strength) values and in calculated bending stiffness values in the longitudinal or transversal direction were found between HP and NAV. Our study confirms that HP has an advantageous ECM biopolymeric structure and has the biomechanical properties required for a tissue from which an autologous heart valve replacement may be constructed.

Sex differences and growth-related adaptations in bone microarchitecture, geometry, density and strength from childhood to early adulthood: a mixed longitudinal HR-pQCT study

PubMed Central

Gabel, Leigh; Macdonald, Heather M.; McKay, Heather A.

2016-01-01

Sex differences in bone strength and fracture risk are well-documented. However, we know little about bone strength accrual during growth and adaptations in bone microstructure, density and geometry that accompany gains in bone strength. Thus, our objectives are to 1) describe growth related adaptations in bone microarchitecture, geometry, density and strength at the distal tibia and radius in boys and girls; 2) compare differences in adaptations in bone microarchitecture, geometry, density and strength between boys and girls. We used HR-pQCT at the distal tibia (8% site) and radius (7% site) in 184 boys and 209 girls (9–20y at baseline). We aligned boys and girls on a common maturational landmark (age at peak height velocity; APHV) and fit a mixed effects model to these longitudinal data. Importantly, boys demonstrated 28–63% greater estimated bone strength across 12 years of longitudinal growth. Boys demonstrated 28–80% more porous cortices compared with girls at both sites across all biological ages, except at the radius at 9 years post-APHV. However, cortical density was similar between boys and girls at all ages at both sites, except at 9 years post-APHV at the tibia when girls’ values were 2% greater than boys’. Boys demonstrated 13–48% greater cortical and total bone area across growth. Load-to-strength ratio was 26–27% lower in boys at all ages, indicating lower risk of distal forearm fracture compared with girls. Contrary to previous HR-pQCT studies that did not align boys and girls at the same biological age, we did not observe sex differences in Ct.BMD. Boys’ superior bone size and strength compared with girls may confer them a protective advantage. However, boys’ consistently more porous cortices may contribute to boys’ higher fracture incidence during adolescence. Large prospective studies using HR-pQCT that target boys and girls who have sustained a fracture are needed to verify this. PMID:27556581

Experimental and Theoretical Research on the Compression Performance of CFRP Sheet Confined GFRP Short Pipe

PubMed Central

Zhao, Qilin; Chen, Li; Shao, Guojian

2014-01-01

The axial compressive strength of unidirectional FRP made by pultrusion is generally quite lower than its axial tensile strength. This fact decreases the advantages of FRP as main load bearing member in engineering structure. A theoretical iterative calculation approach was suggested to predict the ultimate axial compressive stress of the combined structure and analyze the influences of geometrical parameters on the ultimate axial compressive stress of the combined structure. In this paper, the experimental and theoretical research on the CFRP sheet confined GFRP short pole was extended to the CFRP sheet confined GFRP short pipe, namely, a hollow section pole. Experiment shows that the bearing capacity of the GFRP short pipe can also be heightened obviously by confining CFRP sheet. The theoretical iterative calculation approach in the previous paper is amended to predict the ultimate axial compressive stress of the CFRP sheet confined GFRP short pipe, of which the results agree with the experiment. Lastly the influences of geometrical parameters on the new combined structure are analyzed. PMID:24672288

Self-Healable and Reprocessable Polysulfide Sealants Prepared from Liquid Polysulfide Oligomer and Epoxy Resin.

PubMed

Gao, Wentong; Bie, Mengyao; Liu, Fu; Chang, Pengshan; Quan, Yiwu

2017-05-10

Polysulfide sealants have been commercially applied in many industrial fields. In this article, we study the self-healing property of the epoxy resin-cured polysulfide sealants for the first time. The obtained sealants showed a flexible range of ultimate elongation of 157-478% and a tensile strength of 1.02-0.75 MPa corresponding to different polysulfide oligomers. By taking advantage of the dynamic reversible exchange of disulfide bonds, polysulfide sealants exhibited good self-healing ability under a moderate thermal stimulus. A higher molecular weight and a lower degree of cross-linking of polysulfide oligomer were helpful in improving the ultimate elongation and healing efficiency of the polysulfide sealants. After subjecting to a temperature of 75 °C for 60 min, both the tensile strength and ultimate elongation of a fully cut sample, LP55-F, were restored to 91% of the original values, without affecting the sealing property. Furthermore, the sample exhibited excellent reshaping and reprocessing abilities. These outcomes offer a paradigm toward sustainable industrial applications of the polysulfide-based sealants.

Thermal degradation of the tensile strength of unidirectional boron/aluminum composites

NASA Technical Reports Server (NTRS)

Grimes, H. H.; Lad, R. A.; Maisel, J. E.

1977-01-01

The variation of ultimate tensile strength with thermal treatment of B-Al composite materials and of boron fibers chemically removed from these composites in an attempt to determine the mechanism of the resulting strength degradation was studied. Findings indicate that thermally cycling B-Al represents a more severe condition than equivalent time at temperature. Degradation of composite tensile strength from about 1.3 GN/m squared to as low as 0.34 GN/m squared was observed after 3,000 cycles to 420 C for 203 micrometers B-1100 Al composite. In general, the 1100 Al matrix composites degraded somewhat more than the 6061 matrix material studied. Measurement of fiber strengths confirmed a composite strength loss due to the degradation of fiber strength. Microscopy indicated a highly flawed fiber surface.

A preliminary mechanical property and stress corrosion evaluation of VIM-VAR work strengthened and direct aged Inconel 718 bar material

NASA Technical Reports Server (NTRS)

Montano, J. W.

1987-01-01

This report presents a preliminary mechanical property and stress corrosion evaluation of double melted (vacuum induction melted (VIM), and vacuum arc remelted (VAR)), solution treated, work strengthened and direct aged Inconel 718 alloy bar (5.50 in. (13.97 cm) diameter). Two sets of tensile specimens, one direct single aged and the other direct double aged, were tested at ambient temperature in both the longitudinal and transverse directions. Longitudinal tensile and yield strengths in excess of 200 ksi (1378.96 MPa) and 168 ksi (1158.33 MPa), respectively, were realized at ambient temperature, for the direct double aged specimen. No failures occurred in the single or double edged longitudinal and transverse tensile specimens stressed to 75 and 100 percent of their respective yield strengths and exposed to a salt fog environment for 180 days. Tensile tests performed after the stress corrosion test showed no mechanical property degradation.

Longitudinal Associations between Externalizing Behavior and Dysfunctional Eating Attitudes and Behaviors: A Community-Based Study

ERIC Educational Resources Information Center

Marmorstein, Naomi R.; von Ranson, Kristin M.; Iacono, William G.; Succop, Paul A.

2007-01-01

This study investigated longitudinal associations between externalizing behavior and dysfunctional eating attitudes and behaviors. Participants were girls drawn from the community-based Minnesota Twin Family Study and assessed at ages 11, 14, and 17. Cross-sectional correlations indicated that the strength of the associations between externalizing…

The Importance of Longitudinal Pretest-Posttest Designs in Estimating College Impact

ERIC Educational Resources Information Center

Seifert, Tricia A.; Pascarella, Ernest T.; Erkel, Sherri I.; Goodman, Kathleen M.

2010-01-01

In this chapter, the authors discuss the issue of research design in conducting inquiry on college impact and demonstrate the importance of longitudinal pretest-posttest designs in maximizing the internal validity of findings. They begin by discussing the strengths and weaknesses of different types of research design in the college impact…

Analysis and Tests of Reinforced Carbon-Epoxy/Foam-Core Sandwich Panels with Cutouts

NASA Technical Reports Server (NTRS)

Baker, Donald J.; Rogers, Charles

1996-01-01

The results of a study of a low-cost structurally efficient minimum-gage shear-panel design that can be used in light helicopters are presented. The shear-panel design is based on an integrally stiffened syntactic-foam stabilized-skin with an all-bias-ply tape construction for stabilized-skin concept with an all-bias-ply tape construction for the skins. This sandwich concept is an economical way to increase the panel bending stiffness weight penalty. The panels considered in the study were designed to be buckling resistant up to 100 lbs/in. of shear load and to have an ultimate strength of 300 lbs/in. The panel concept uses unidirectional carbon-epoxy tape on a syntactic adhesive as a stiffener that is co-cured with the skin and is an effective concept for improving panel buckling strength. The panel concept also uses pultruded carbon-epoxy rods embedded in a syntactic adhesive and over-wrapped with a bias-ply carbon-epoxy tape to form a reinforcing beam which is an effective method for redistributing load around rectangular cutout. The buckling strength of the reinforced panels is 83 to 90 percent of the predicted buckling strength based on a linear buckling analysis. The maximum experimental deflection exceeds the maximum deflection predicted by a nonlinear analysis by approximately one panel thickness. The failure strength of the reinforced panels was two and a half to seven times of the buckling strength. This efficient shear-panel design concept exceeds the required ultimate strength requirement of 300 lbs/in by more than 100 percent.

Longitudinal Tracking of Academic Progress during Teacher Preparation

ERIC Educational Resources Information Center

Corcoran, Roisin P.; O'Flaherty, Joanne

2017-01-01

Background: Given that the ultimate academic goal of many education systems in the developed world is for students to graduate from college, grades have a considerable bearing on how effective colleges are in meeting their primary objective. Prior academic performance informs predominantly the selection and retention of teacher candidates.…

Service Provisions for Youth with Emotional and Behavioral Disorders

ERIC Educational Resources Information Center

Dean, Latoya Lavan

2012-01-01

Youth with emotional or behavioral disorders (EBD) have poorer outcomes compared to their peers with and without disabilities. As a result, the federal government has mandated transition services to improve supports and ultimately student outcomes. Using data from the National Longitudinal Transition Study-2 (NLTS-2), this secondary analysis…

Tensile strength comparison of presoldered and postsoldered joints.

PubMed

Monday, J J; Asgar, K

1986-01-01

Twenty half-dumbbell shaped rods were cast in a silverless gold-palladium alloy that contained a minimum of 42% fresh alloy and the rest once-melted alloy. Each pair of half-dumbbells was assembled and either presoldered or postsoldered using a vacuum-oven and a torch-soldering technique. There was no significant difference in the ultimate tensile strength values between the presoldered and postsoldered joints within the same technique group, but the torch-soldered joints for the same solder were significantly stronger (p less than .01). It was believed that slow heating and cooling has deleterious effects on the ultimate tensile strength joints (UTS) possibly because of the microstructural changes and the highly oxidizable content of the postsolder used. Another 15 samples cast using once, twice, and three-times remelted parent alloy were presoldered and postsoldered with the torch only. In each of these groups, specimens joined by presolder showed significantly higher strength than those joined by postsolder (p less than .02). Remelting the parent alloy affected the strength differences between the presoldered and postsoldered joints. It was assumed that on remelting, the nature of the parent alloy is changed because some original elements are volatilized and newly formed oxides dissolved into it. Because it contains copper, the postsolder is more affected by this contamination than presolder. The UTS of the parent alloy, as well as that of the presolder and postsolder, were also determined. As expected, the parent alloy possessed the highest strength and the postsolder, the lowest.

Impact Melt Emplacement on Mercury

NASA Astrophysics Data System (ADS)

Daniels, J. W.; Neish, C. D.

2018-05-01

This work proposes that fresh craters on rocky bodies may deposit impact melt externally ultimately according to the strength of its surface gravity, regardless of the body's surface topography and melt abundance.

Mechanical design of mussel byssus: material yield enhances attachment strength

PubMed

Bell; Gosline

1996-01-01

The competitive dominance of mussels in the wave-swept rocky intertidal zone is in part due to their ability to maintain a secure attachment. Mussels are tethered to the substratum by a byssus composed of numerous extracellular, collagenous threads secreted by the foot. Each byssal thread has three serially arranged parts: a corrugated proximal region, a smooth distal region and an adhesive plaque. This study examines the material and structural properties of the byssal threads of three mussel species: Mytilus californianus, M. trossulus, and M. galloprovincialis. Tensile tests in general reveal similar material properties among species: the proximal region has a lower initial modulus, a lower ultimate stress and a higher ultimate strain than the distal region. The distal region also yields at a stress well below its ultimate value. In whole thread tests, the proximal region and adhesive plaque are common sites of structural failure and are closely matched in strength, while the distal region appears to be excessively strong. We propose that the high strength of the distal region is the byproduct of a material designed to yield and extend before structural failure occurs. Experimental and theoretical evidence is presented suggesting that thread yield and extensibility provide two important mechanisms for increasing the overall attachment strength of the mussel: (1) the reorientation of threads towards the direction of applied load, and (2) the 'recruitment' of more threads into tension and the consequent distribution of applied load over a larger cross-sectional area, thereby reducing the stress on each thread. This distal region yield behavior is most striking for M. californianus and may be a key to its success in extreme wave-swept environments.

Longitudinal (4 year) change of thigh muscle and adipose tissue distribution in chronically painful vs. painless knees – data from the Osteoarthritis Initiative

PubMed Central

Ruhdorfer, Anja; Wirth, Wolfgang; Dannhauer, Torben; Eckstein, Felix

2015-01-01

Objective To evaluate 4-year longitudinal change in thigh muscle and adipose tissue content in chronically painful versus painless knees. Methods Knees from Osteoarthritis Initiative participants with non-acceptable symptom status (numerical rating scale ≥4) and frequent pain (≥6 months at baseline, year 2 and year 4 follow-up) were studied. These were matched with painless controls (bilateral NRS pain intensity≤1 and ≤infrequent pain at all 3 timepoints). 4-year longitudinal changes in thigh muscle anatomical cross-sectional areas (CSAs), isometric muscle strength, and in subcutaneous (SCF) and intermuscular fat (IMF) CSAs were obtained from magnetic resonance images (MRI) and were compared between groups (paired t-tests). Results 43 participants fulfilled the inclusion criteria of chronic pain, had complete thigh muscle MRI acquisitions and strength measurements, and a matched control. Quadriceps CSAs, but not extensor strength, showed a significant longitudinal decrease in chronically painful knees (-3.9%; 95%confidence interval [95 CI] -6.3%,-1.5%) and in painless controls (-2.4%; 95% CI -4.1%, -0.7%); the difference in change was not statistically significant (p=0.33). There was a significant 4-year gain in SCF in painful knees (8.1%; 95% CI 3.1%, 13%) but not in controls (0.0%; 95%CI -4.4%, +4.4%) with the difference in change being significant (p=0.03). The gain in IMF (∼5.2%) was similar between painful and painless knees. Conclusion This is the first paper to show a significant impact of (chronic) knee pain on longitudinal change in local subcutaneous adipose tissue. The effect of pain on subcutaneous fat appeared stronger than that on intermuscular adipose tissue and on muscle status. PMID:25887367

Microcracking, microcrack-induced delamination, and longitudinal splitting of advanced composite structures

NASA Technical Reports Server (NTRS)

Nairn, John A.

1992-01-01

A combined analytical and experimental study was conducted to analyze microcracking, microcrack-induced delamination, and longitudinal splitting in polymer matrix composites. Strain energy release rates, calculated by a variational analysis, were used in a failure criterion to predict microcracking. Predictions and test results were compared for static, fatigue, and cyclic thermal loading. The longitudinal splitting analysis accounted for the effects of fiber bridging. Test data are analyzed and compared for longitudinal splitting and delamination under mixed-mode loading. This study emphasizes the importance of using fracture mechanics analyses to understand the complex failure processes that govern composite strength and life.

Longitudinal Associations of Student-Teacher Relationships and Behavioural and Emotional Strengths on Academic Achievement

ERIC Educational Resources Information Center

Sointu, Erkko T.; Savolainen, Hannu; Lappalainen, Kristiina; Lambert, Matthew C.

2017-01-01

Positive student-teacher relationships are related to students' academic achievement and behavioural and emotional adjustment. How a student's behavioural and emotional strengths are associated with these relationships and how the relationships influence students' academic performance remains unknown. We examined this framework using a…

Microstructures and properties of aluminum die casting alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

M. M. Makhlouf; D. Apelian; L. Wang

1998-10-01

This document provides descriptions of the microstructure of different aluminum die casting alloys and to relate the various microstructures to the alloy chemistry. It relates the microstructures of the alloys to their main engineering properties such as ultimate tensile strength, yield strength, elongation, fatigue life, impact resistance, wear resistance, hardness, thermal conductivity and electrical conductivity. Finally, it serves as a reference source for aluminum die casting alloys.

Time-Dependent Behavior of High-Strength Kevlar and Vectran Webbing

NASA Technical Reports Server (NTRS)

Jones, Thomas C.; Doggett, William R.

2014-01-01

High-strength Kevlar and Vectran webbings are currently being used by both NASA and industry as the primary load-bearing structure in inflatable space habitation modules. The time-dependent behavior of high-strength webbing architectures is a vital area of research that is providing critical material data to guide a more robust design process for this class of structures. This paper details the results of a series of time-dependent tests on 1-inch wide webbing including an initial set of comparative tests between specimens that underwent realtime and accelerated creep at 65 and 70% of their ultimate tensile strength. Variability in the ultimate tensile strength of the webbings is investigated and compared with variability in the creep life response. Additional testing studied the effects of load and displacement rate, specimen length and the time-dependent effects of preconditioning the webbings. The creep test facilities, instrumentation and test procedures are also detailed. The accelerated creep tests display consistently longer times to failure than their real-time counterparts; however, several factors were identified that may contribute to the observed disparity. Test setup and instrumentation, grip type, loading scheme, thermal environment and accelerated test postprocessing along with material variability are among these factors. Their effects are discussed and future work is detailed for the exploration and elimination of some of these factors in order to achieve a higher fidelity comparison.

Effect of evaporation on the shelf life of a universal adhesive.

PubMed

Pongprueksa, P; Miletic, V; De Munck, J; Brooks, N R; Meersman, F; Nies, E; Van Meerbeek, B; Van Landuyt, K L

2014-01-01

The purpose of this study was to evaluate how evaporation affects the shelf life of a one-bottle universal adhesive. Three different versions of Scotchbond Universal (SBU, 3M ESPE, Seefeld, Germany) were prepared using a weight-loss technique. SBU0 was left open to the air until maximal weight loss was obtained, whereas SBU50 was left open until 50% of evaporation occurred. In contrast, SBU100 was kept closed and was assumed to contain the maximum concentration of all ingredients. The degree of conversion (DC) was determined by using Fourier transform infrared spectroscopy on different substrates (on dentin or glass plate and mixed with dentin powder); ultimate microtensile strength and microtensile bond strength to dentin were measured as well. DC of the 100% solvent-containing adhesive (SBU100) was higher than that of the 50% (SBU50) and 0% (SBU0) solvent-containing adhesives for all substrates. DC of the adhesive applied onto glass and dehydrated dentin was higher than that applied onto dentin. Even though the ultimate microtensile strength of SBU0 was much higher than that of SBU50 and SBU100, its bond strength to dentin was significantly lower. Evaporation of adhesive ingredients may jeopardize the shelf life of a one-bottle universal system by reducing the degree of conversion and impairing bond strength. However, negative effects only became evident after more than 50% evaporation.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Crabtree, D.J.

Three types of boron/epoxy prepreg tape were prestressed to fracture weak sites along the fiber by winding over 0.3- to 0.6-inch diameter rollers prior to lamination. The prestressed prepreg was then laminated, and design allowable testing was conducted to determine if mechanical strength properties are increased and data scatter is reduced by prestressing. The types of prepreg studied were standard 'Rigidite' 5505/4 prepreg, carbon substrate boron fiber prepreg, and a prepreg made from 'defect' tungsten substrate boron that was manufactured in a high-speed, low-cost, production process. The strength of angleply composites of both 'Rigidite' 5505/4 and carbon substrate boron compositesmore » were unaffected by prestressing. A study was made to determine if prepreg costs could be reduced by manufacturing low-cost 'defect' boron fiber and prestressing it to improve its properties. The results of this study were inconclusive. The test results show prestressing marginally improved some composite properties while others were reduced. On 'Rigidite' 5505/4 unidirectional composites, fatigue strength was significantly improved by prestressing, while longitudinal tensile strength was reduced at room temperature and 350 F. On unidirectional carbon substrate boron composites, the longitudinal tensile strength at room temperature and 350F was increased with attendant variability, while fatigue strength at high stress levels was reduced but not affected at low stress levels.« less

Polyimide Composites from 'Salt-Like' Solution Precursors

NASA Technical Reports Server (NTRS)

Cano, Roberto J.; Hou, Tan H.; Weiser, Erik S.; SaintClair, Terry L.

2001-01-01

Four NASA Langley-developed polyimide matrix resins, LaRC(TM)-IA, LaRC(TM)-IAX, LaRC(TM)-8515 and LaRC(TM)-PETI-5, were produced via a 'saltlike' process developed by Unitika Ltd. The salt-like solutions (65% solids in NMP) were prepregged onto Hexcel IM7 carbon fiber using the NASA LaRC multipurpose tape machine. Process parameters were determined and composite panels fabricated. The temperature dependent volatile depletion rates, the thermal crystallization behavior and the resin rheology were characterized. Composite molding cycles were developed which consistently yielded well consolidated, void-free laminated parts. Composite mechanical properties such as the short beam shear strength; the longitudinal and transverse flexural strength and flexural modulus; the longitudinal compression strength and modulus; and the open hole compression strength and compression after impact strength were measured at room temperature and elevated temperatures. The processing characteristics and the composite mechanical properties of the four intermediate modulus carbon fiber/polyimide matrix composites were compared to existing data on the same polyimide resin systems and IM7 carbon fiber manufactured via poly(amide acid) solutions (30-35% solids in NMP). This work studies the effects of varying the synthetic route on the processing and mechanical properties of the polyimide composites.

Magnetic field of longitudinal gradient bend

NASA Astrophysics Data System (ADS)

Aiba, Masamitsu; Böge, Michael; Ehrlichman, Michael; Streun, Andreas

2018-06-01

The longitudinal gradient bend is an effective method for reducing the natural emittance in light sources. It is, however, not a common element. We have analyzed its magnetic field and derived a set of formulae. Based on the derivation, we discuss how to model the longitudinal gradient bend in accelerator codes that are used for designing electron storage rings. Strengths of multipole components can also be evaluated from the formulae, and we investigate the impact of higher order multipole components in a very low emittance lattice.

Probabilistic simulation of uncertainties in composite uniaxial strengths

NASA Technical Reports Server (NTRS)

Chamis, C. C.; Stock, T. A.

1990-01-01

Probabilistic composite micromechanics methods are developed that simulate uncertainties in unidirectional fiber composite strengths. These methods are in the form of computational procedures using composite mechanics with Monte Carlo simulation. The variables for which uncertainties are accounted include constituent strengths and their respective scatter. A graphite/epoxy unidirectional composite (ply) is studied to illustrate the procedure and its effectiveness to formally estimate the probable scatter in the composite uniaxial strengths. The results show that ply longitudinal tensile and compressive, transverse compressive and intralaminar shear strengths are not sensitive to single fiber anomalies (breaks, intergacial disbonds, matrix microcracks); however, the ply transverse tensile strength is.

Effects of soldering methods on tensile strength of a gold-palladium metal ceramic alloy.

PubMed

Ghadhanfari, Husain A; Khajah, Hasan M; Monaco, Edward A; Kim, Hyeongil

2014-10-01

The tensile strength obtained by conventional postceramic application soldering and laser postceramic welding may require more energy than microwave postceramic soldering, which could provide similar tensile strength values. The purpose of the study was to compare the tensile strength obtained by microwave postceramic soldering, conventional postceramic soldering, and laser postceramic welding. A gold-palladium metal ceramic alloy and gold-based solder were used in this study. Twenty-seven wax specimens were cast in gold-palladium noble metal and divided into 4 groups: laser welding with a specific postfiller noble metal, microwave soldering with a postceramic solder, conventional soldering with the same postceramic solder used in the microwave soldering group, and a nonsectioned control group. All the specimens were heat treated to simulate a normal porcelain sintering sequence. An Instron Universal Testing Machine was used to measure the tensile strength for the 4 groups. The means were analyzed statistically with 1-way ANOVA. The surface and fracture sites of the specimens were subjectively evaluated for fracture type and porosities by using a scanning electron microscope. The mean (standard deviation) ultimate tensile strength values were as follows: nonsectioned control 818 ±30 MPa, microwave 516 ±34 MPa, conventional 454 ±37 MPa, and laser weld 191 ±39 MPa. A 1-way ANOVA showed a significant difference in ultimate tensile strength among the groups (F3,23=334.5; P<.001). Follow-up multiple comparisons showed a significant difference among all the groups. Microwave soldering resulted in a higher tensile strength for gold and palladium noble metals than either conventional soldering or laser welding. Conventional soldering resulted in a higher tensile strength than laser welding. Under the experimental conditions described, either microwave or conventional postceramic soldering would appear to satisfy clinical requirements related to tensile strength. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

The Tension and Puncture Properties of HDPE Geomembrane under the Corrosion of Leachate

PubMed Central

Xue, Qiang; Zhang, Qian; Li, Zhen-Ze; Xiao, Kai

2013-01-01

To investigate the gradual failure of high-density polyethylene (HDPE) geomembrane as a result of long-term corrosion, four dynamic corrosion tests were conducted at different temperatures and durations. By combining tension and puncture tests, we systematically studied the variation law of tension and puncture properties of the HDPE geomembrane under different corrosion conditions. Results showed that tension and puncture failure of the HDPE geomembrane was progressive, and tensile strength in the longitudinal grain direction was evidently better than that in the transverse direction. Punctures appeared shortly after puncture force reached the puncture strength. The tensile strength of geomembrane was in inversely proportional to the corrosion time, and the impact of corrosion was more obvious in the longitudinal direction than transverse direction. As corrosion time increased, puncture strength decreased and corresponding deformation increased. As with corrosion time, the increase of corrosion temperature induced the decrease of geomembrane tensile strength. Tensile and puncture strength were extremely sensitive to temperature. Overall, residual strength had a negative correlation with corrosion time or temperature. Elongation variation increased initially and then decreased with the increase in temperature. However, it did not show significant law with corrosion time. The reduction in puncture strength and the increase in puncture deformation had positive correlations with corrosion time or temperature. The geomembrane softened under corrosion condition. The conclusion may be applicable to the proper designing of the HDPE geomembrane in landfill barrier system. PMID:28788321

Total Longitudinal Moment Calculation and Reliability Analysis of Yacht Structures

NASA Astrophysics Data System (ADS)

Zhi, Wenzheng; Lin, Shaofen

In order to check the reliability of the yacht in FRP (Fiber Reinforce Plastic) materials, in this paper, the vertical force and the calculation method of the overall longitudinal bending moment on yacht was analyzed. Specially, this paper focuses on the impact of speed on the still water bending moment on yacht. Then considering the mechanical properties of the cap type stiffeners in composite materials, the ultimate bearing capacity of the yacht has been worked out, finally the reliability of the yacht was calculated with using response surface methodology. The result can be used in yacht design and yacht driving.

Association between muscle strength and metabolic syndrome in older Korean men and women: the Korean Longitudinal Study on Health and Aging.

PubMed

Yang, Eun Joo; Lim, Soo; Lim, Jae-Young; Kim, Ki Woong; Jang, Hak Chul; Paik, Nam-Jong

2012-03-01

The objective of the study was to investigate the association between metabolic syndrome (MS) and muscle strength in community-dwelling older men and women in Korea. Korean men and women 65 years and older living in a single, typical South Korean city (n = 647) were enrolled in the Korean Longitudinal Study on Health and Aging study. The diagnosis of MS was evaluated according to the definition of the National Cholesterol Education Program Adult Treatment Panel III. Isokinetic muscle strength of the knee extensors, as determined by peak torque per body weight (newton meter per kilogram) and hand-grip strength per body weight (newton per kilogram), was measured. Participants without MS had greater leg muscle strength and grip strength per weight. The effect of MS on muscle strength was more prominent in men than in women in our study population. Only men showed a significant interaction between MS and age for muscle strength (P = .014), and the effect was greater in men aged 65 to 74 years compared with those older than 75 years (119.2 ± 31.2 vs 134.5 ± 24.3 N m/kg). Participants with MS had weaker knee extensor strength after controlling the covariates (β = -90.80, P = .003), and the interaction term (age × MS × male sex) was significant (β = 1.00, P = .017). Metabolic syndrome is associated with muscle weakness, and this relationship is particularly pronounced in men. Age can modify the impact of MS on muscle strength. Men aged 65 to 74 years with MS need a thorough assessment of muscle strength to prevent disability. Copyright © 2012 Elsevier Inc. All rights reserved.

Novel and emerging strategies for longitudinal data collection.

PubMed

Udtha, Malini; Nomie, Krystle; Yu, Erica; Sanner, Jennifer

2015-03-01

To describe novel and emerging strategies practiced globally in research to improve longitudinal data collection. In research studies, numerous strategies such as telephone interviews, postal mailing, online questionnaires, and electronic mail are traditionally utilized in longitudinal data collection. However, due to technological advances, novel and emerging strategies have been applied to longitudinal data collection, such as two-way short message service, smartphone applications (or "apps"), retrieval capabilities applied to the electronic medical record, and an adapted cloud interface. In this review, traditional longitudinal data collection strategies are briefly described, emerging and novel strategies are detailed and explored, and information regarding the impact of novel methods on participant response rates, the timeliness of participant responses, and cost is provided. We further discuss how these novel and emerging strategies affect longitudinal data collection and advance research, specifically nursing research. Evidence suggests that the novel and emerging longitudinal data collection strategies discussed in this review are valuable approaches to consider. These strategies facilitate collecting longitudinal research data to better understand a variety of health-related conditions. Future studies, including nursing research, should consider using novel and emerging strategies to advance longitudinal data collection. A better understanding of novel and emerging longitudinal data collection strategies will ultimately improve longitudinal data collection as well as foster research efforts. Nurse researchers, along with all researchers, must be aware of and consider implementing novel and emerging strategies to ensure future healthcare research success. © 2014 Sigma Theta Tau International.

Floating Breakwaters: State-of-the-Art Literature Review.

DTIC Science & Technology

1981-10-01

transmission Mooring loads 20. / . 20. STR ACT (Continue on reverse ide If necessary and Identify by block number) A multitude of conceptual models of...are designed by finding the ultimate lateral resistance of the pile-soil system and increasing the lateral mooring load , Ft, by a fac- tor of safety...Fs, to determine the design lateral load on the pile. The ultimate lateral resistance of the anchor pile is reached when either the passive strength of

Tensile properties of titanium electrolytically charged with hydrogen

NASA Technical Reports Server (NTRS)

Smith, R. J.; Otterson, D. A.

1971-01-01

Yield strength, ultimate tensile strength, and elongation were studied for annealed titanium electrolytically charged with hydrogen. The hydrogen was present as a surface hydride layer. These tensile properties were generally lower for uncharged titanium than for titanium with a continuous surface hydride; they were greater for uncharged titanium than for titanium with an assumed discontinuous surface hydride. We suggest that the interface between titanium and titanium hydride is weak. And the hydride does not necessarily impair strength and ductility of annealed titanium. The possibility that oxygen and/or nitrogen can embrittle titanium hydride is discussed.

49 CFR 238.405 - Longitudinal static compressive strength.

Code of Federal Regulations, 2012 CFR

2012-10-01

... crash refuge for crewmembers occupying the cab of a power car, the underframe of the cab of a power car... volumes of a power car or a trailer car designed to crush as part of the crash energy management design...) The underframe of the occupied volume of each trailer car shall resist a minimum longitudinal static...

49 CFR 238.405 - Longitudinal static compressive strength.

Code of Federal Regulations, 2014 CFR

2014-10-01

... crash refuge for crewmembers occupying the cab of a power car, the underframe of the cab of a power car... volumes of a power car or a trailer car designed to crush as part of the crash energy management design...) The underframe of the occupied volume of each trailer car shall resist a minimum longitudinal static...

49 CFR 238.405 - Longitudinal static compressive strength.

Code of Federal Regulations, 2013 CFR

2013-10-01

... crash refuge for crewmembers occupying the cab of a power car, the underframe of the cab of a power car... volumes of a power car or a trailer car designed to crush as part of the crash energy management design...) The underframe of the occupied volume of each trailer car shall resist a minimum longitudinal static...

Understanding Teacher Effectiveness: Providing Feedback to Teacher Preparation Programs. Data for Action 2013

ERIC Educational Resources Information Center

Data Quality Campaign, 2014

2014-01-01

Teachers need longitudinal student-level data, such as attendance history, course-taking patterns, grades, and test scores, to tailor instruction to individual students' strengths and weaknesses.This factsheet uses the findings from the Data for Action 2013 analysis to discuss how states can provide teachers with student-level longitudinal data,…

Muscle Fiber Size and Function in Elderly Humans: A Longitudinal Study

USDA-ARS?s Scientific Manuscript database

Cross-sectional studies are likely to underestimate age-related changes in skeletal muscle strength and mass. The purpose of this longitudinal study was to assess whole muscle and single muscle fiber alterations in the same cohort of 12 older (mean age: start of study=71.1+/-5.4 yrs and end of study...

Analysis of acoustic emission cumulative signal strength of steel fibre reinforced concrete (SFRC) beams strengthened with carbon fibre reinforced polymer (CFRP)

NASA Astrophysics Data System (ADS)

Abdul Hakeem, Z.; Noorsuhada, M. N.; Azmi, I.; Noor Syafeekha, M. S.; Soffian Noor, M. S.

2017-12-01

In this study, steel fibre reinforced concrete (SFRC) beams strengthened with carbon fibre reinforced polymer (CFRP) were investigated using acoustic emission (AE) technique. Three beams with dimension of 150 mm width, 200 mm depth and 1500 mm length were fabricated. The results generated from AE parameters were analysed as well as signal strength and cumulative signal strength. Three relationships were produced namely load versus deflection, signal strength versus time and cumulative signal strength with respect to time. Each relationship indicates significant physical behaviour as the crack propagated in the beams. It is found that an addition of steel fibre in the concrete mix and strengthening of CFRP increase the ultimate load of the beam and the activity of signal strength. Moreover, the highest signal strength generated can be identified. From the study, the occurrence of crack in the beam can be predicted using AE signal strength.

14 CFR 31.27 - Strength.

Code of Federal Regulations, 2010 CFR

2010-01-01

... to withstand the ultimate loads for at least three seconds without failure. For the envelope, a test... conditions. There must be no distortion or failure that is likely to cause serious injury to the occupants. A...

Calculation of cracking under pulsed heat loads in tungsten manufactured according to ITER specifications

NASA Astrophysics Data System (ADS)

Arakcheev, A. S.; Skovorodin, D. I.; Burdakov, A. V.; Shoshin, A. A.; Polosatkin, S. V.; Vasilyev, A. A.; Postupaev, V. V.; Vyacheslavov, L. N.; Kasatov, A. A.; Huber, A.; Mertens, Ph; Wirtz, M.; Linsmeier, Ch; Kreter, A.; Löwenhoff, Th; Begrambekov, L.; Grunin, A.; Sadovskiy, Ya

2015-12-01

A mathematical model of surface cracking under pulsed heat load was developed. The model correctly describes a smooth brittle-ductile transition. The elastic deformation is described in a thin-heated-layer approximation. The plastic deformation is described with the Hollomon equation. The time dependence of the deformation and stresses is described for one heating-cooling cycle for a material without initial plastic deformation. The model can be applied to tungsten manufactured according to ITER specifications. The model shows that the stability of stress-relieved tungsten deteriorates when the base temperature increases. This proved to be a result of the close ultimate tensile and yield strengths. For a heat load of arbitrary magnitude a stability criterion was obtained in the form of condition on the relation of the ultimate tensile and yield strengths.

Factors associated with grip strength decline in older adults.

PubMed

Sternäng, Ola; Reynolds, Chandra A; Finkel, Deborah; Ernsth-Bravell, Marie; Pedersen, Nancy L; Dahl Aslan, Anna K

2015-03-01

Few studies have examined associations of multi-faceted demographic, health and lifestyle factors with long-term change in grip strength performance across the adult lifespan. The aim of this study was to examine the associations of risk factors in specific parts of the adult lifespan (e.g. in early midlife, in late midlife and in old adulthood) separately for women and men. Data came from the longitudinal Swedish Adoption/Twin Study of Aging (SATSA). Grip strength performance was followed in 849 participants who were 50-88 years of age at baseline. The follow-up period with seven waves of data of grip strength was 22 years, and the risk factors were measured up to 20 years before the assessment of grip strength. Latent growth modelling was used for the longitudinal analyses. A gender difference in the type of factors associated with grip strength performance and development across the adult lifespan was found. Significant factors for the age slopes for women were stress, smoking and dementia. For men, marital status, mean arterial pressure, physical activity at work and having a chronic disorder were of importance. These factors varied in their associations with grip strength across the adult lifespan. Factors measured earlier in adulthood were associated with grip strength decline in late midlife and old adulthood. Gender-specific patterns of risk factors suggest that it may be worthwhile to conduct research on grip and muscle strength (and biological vitality) separately for men and women. © The Author 2014. Published by Oxford University Press on behalf of the British Geriatrics Society. All rights reserved. For Permissions, please email: journals.permissions@oup.com.

Fractography of the high temperature hydrogen attack of a medium carbon steel

NASA Technical Reports Server (NTRS)

Nelson, H. G.; Moorhead, R. D.

1976-01-01

Results are reported for an experimental study of the microscopic fracture processes associated with hydrogen attack of a commercially produced plain carbon steel in a well-controlled high-temperature hydrogen environment of high purity. In the experiments, sheet samples were exposed to laboratory-grade hydrogen at a pressure of 3.5 MN/sq m and a temperature of 575 C. The fractography of gas-filled fissures and failed tension specimens is analyzed in an effort to identify any predominant microstructural defect associated with fissure formation, the prevalent modes of fracture, and the contribution of gas-filled fissures to the overall failure process. It is found that the tensile properties of the examined steel were significantly degraded after as few as 136 hr of exposure to a high-purity hydrogen atmosphere at 575 C; that the yield strength, ultimate strength, and elongation at fracture were all reduced progressively with increasing exposure time; and that the yield and ultimate strengths were reduced more than 40% after 408 hr while elongation was reduced to less than 2%.

High temperature tensile behavior and microstructure of Al-SiC nanocomposite fabricated by mechanical milling and hot extrusion technique

NASA Astrophysics Data System (ADS)

Soltani, Mohammadreza; Atrian, Amir

2018-02-01

This paper investigates the high-temperature tensile behavior of Al-SiC nanocomposite reinforced with 0, 1.5, and 3 vol% SiC nano particles. To fabricate the samples, SiC nano reinforcements and aluminum (Al) powders were milled using an attritor milling and then were cold pressed and hot extruded at 500 °C. Afterward, mechanical and microstructural characteristics were studied in different temperatures. To this end, tensile and compressive tests, micro-hardness test, microscopic examinations, and XRD analysis were performed. The results showed significant improvement of mechanical properties of Al-SiC nanocomposite in room temperature including 40% of ultimate tensile strength (UTS), 36% of ultimate compressive strength (UCS), and 44% of micro-hardness. Moreover, performing tensile tests at elevated temperatures (up to 270 °C) decreased the tensile strength by about 53%, 46%, and 45% for Al-0 vol% SiC, Al-1.5 vol% SiC, and Al-3 vol% SiC, respectively. This temperature rise also enhanced the elongation by about 11% and 133% for non-reinforced Al and Al-3 vol% SiC, respectively.

Low-velocity impact tests on fibrous composite sandwich structures

NASA Technical Reports Server (NTRS)

Sharma, A. V.

1981-01-01

The effect of low-velocity projectile impact on the load-carrying ability of the composite sandwich structural components is investigated experimentally, the impact simulating the damage caused by runway debris and the accidental dropping of hand tools during servicing on secondary aircraft structures made with composites. The sandwich-type beam specimens were fabricated with graphite/epoxy face sheets, aluminum honeycomb core, and a steel (back) plate. A four-point beam-loading apparatus was used, and the ultimate strength, ultimate strain, and residual strength of the composites were determined. A faired curve is presented indicating the lower bound of the failure threshold for each of the laminate configurations tested in compression and tension as a function of the projectile impact energy. It is shown that strength degradation due to impact is dependent on the laminate configuration and the fiber/matrix combination. The laminates having more angle plies near the impact surface and unidirectional plies elsewhere seem to show extensive interply and intraply fiber delaminations at failure relative to the laminates with a cross-ply on the impact surface.

Line defects in graphene: How doping affects the electronic and mechanical properties

NASA Astrophysics Data System (ADS)

Berger, Daniel; Ratsch, Christian

2016-06-01

Graphene and carbon nanotubes have extraordinary mechanical and electronic properties. Intrinsic line defects such as local nonhexagonal reconstructions or grain boundaries, however, significantly reduce the tensile strength, but feature exciting electronic properties. Here, we address the properties of line defects in graphene from first principles on the level of full-potential density-functional theory, and assess doping as one strategy to strengthen such materials. We carefully disentangle the global and local effect of doping by comparing results from the virtual crystal approximation with those from local substitution of chemical species, in order to gain a detailed understanding of the breaking and stabilization mechanisms. We find that doping primarily affects the occupation of the frontier orbitals. Occupation through n -type doping or local substitution with nitrogen increases the ultimate tensile strength significantly. In particular, it can stabilize the defects beyond the ultimate tensile strength of the pristine material. We therefore propose this as a key strategy to strengthen graphenic materials. Furthermore, we find that doping and/or applying external stress lead to tunable and technologically interesting metal/semiconductor transitions.

Facile Fabrication of Multifunctional Aramid Nanofiber Films by Spin Coating

NASA Astrophysics Data System (ADS)

Lyu, Jing; Liu, Lehao; Zhao, Xing; Shang, Yudong; Zhao, Tingkai; Li, Tiehu

2016-11-01

Polymer matrices with excellent mechanical properties, thermal stability and other features are highly demanded for the effective utilization within nanocomposites. Here, we fabricate free-standing aramid nanofiber films via spin coating of an aramid nanofiber/dimethyl sulfoxide solution. Compared with traditional film fabrication methods, this process is time-saving and also able to easily tune the thickness of the films. The resultant films show greatly improved stretchability than that of Kevlar threads and relatively high mechanical strength. Typically, these films with a thickness of 5.5 µm show an ultimate strength of 182 MPa with an ultimate tensile strain of 10.5%. We also apply a finite element modeling to simulate the strain and strength distributions of the films under uniaxial tension, and the results of the simulation are in accordance with the experimental data. Furthermore, the aramid nanofiber films exhibit outstanding thermostability (decomposition at 550 °C under N2 atmosphere and 500 °C in air) and chemical inertness, which would endure acid and alkali. The simple method demonstrated here provides an important way to prepare high-performance aramid nanofiber films for designing new composite systems.

Teaching with a Technological Twist: Exit Tickets via Twitter in Literacy Classrooms

ERIC Educational Resources Information Center

Amaro-Jiménez, Carla; Hungerford-Kresser, Holly; Pole, Kathryn

2016-01-01

In this article, the authors describe, reflect, and analyze the implementation of a commonly used teaching strategy with a technological twist: exit tickets via Twitter. Longitudinal data collected over the course of three years demonstrated that using Twitter to reinvent a nondigital teaching practice ultimately demonstrated a better…

Initial Steps in Creating a Developmentally Valid Tool for Observing/Assessing Rope Jumping

ERIC Educational Resources Information Center

Roberton, Mary Ann; Thompson, Gregory; Langendorfer, Stephen J.

2017-01-01

Background: Valid motor development sequences show the various behaviors that children display as they progress toward competence in specific motor skills. Teachers can use these sequences to observe informally or formally assess their students. While longitudinal study is ultimately required to validate developmental sequences, there are earlier,…

Age associated declines in muscle mass, strength, power, and physical performance: impact on fear of falling and quality of life

USDA-ARS?s Scientific Manuscript database

SUMMARY: This 3 year longitudinal study among older adults showed that declining muscle mass, strength, power, and physical performance are independent contributing factors to increased fear of falling, while declines of muscle mass and physical performance contribute to deterioration of quality of ...

Transverse stresses and modes of failure in tree branches and other beams

PubMed Central

Ennos, A. R.; van Casteren, A.

2010-01-01

The longitudinal stresses in beams subjected to bending also set up transverse stresses within them; they compress the cross section when the beam's curvature is being increased and stretch it when its curvature is being reduced. Analysis shows that transverse stresses rise to a maximum at the neutral axis and increase with both the bending moment applied and the curvature of the beam. These stresses can qualitatively explain the fracture behaviour of tree branches. Curved ‘hazard beams’ that are being straightened split down the middle because of the low transverse tensile strength of wood. By contrast, straight branches of light wood buckle when they are bent because of its low transverse compressive strength. Branches of denser wood break, but the low transverse tensile strength diverts the crack longitudinally when the fracture has only run half-way across the beam, to produce their characteristic ‘greenstick fracture’. The bones of young mammals and uniaxially reinforced composite beams may also be prone to greenstick fracture because of their lower transverse tensile strength. PMID:20018786

Inclusion of inhomogeneous deformation and strength characteristics in the problem on zonal disintegration of rocks

NASA Astrophysics Data System (ADS)

Chanyshev, AI; Belousova, OE

2018-03-01

The authors determine stress and deformation in a heterogeneous rock mass at the preset displacement and Cauchy stress vector at the boundary of an underground excavation. The influence of coordinates on Young’s modulus, shear modulus and ultimate strength is shown. It is found that regions of tension and compression alternate at the excavation boundary—i.e. zonal rock disintegration phenomenon is observed.

Preliminary study of the biomechanical behavior and physical characteristics of tantalum (Ta)-coated prostheses.

PubMed

Duan, Yonghong; Liu, Lie; Wang, Ling; Guo, Fei; Li, Haoping; Shi, Lei; Li, Mao; Yin, Dayu; Jiang, Chi; Zhu, Qingsheng

2012-03-01

Use of Ta biomaterials in medicine started in the middle of the last century. The good biocompatibility and chemical stability, and the unique physical characteristics of Ta metal have resulted in many possible developments of Ta biomaterials. In this study, histopathological observation, histomorphometric analysis, scanning electron microscope (SEM) observation, energy-dispersive X-ray spectroscopy (EDX) analysis, biomechanical testing, and examination of the coating's mechanical strength have been used to evaluate the value of clinical application of Ta-coated prostheses prepared by a plasma-spraying process. Histopathological observation has demonstrated that the periprosthetic new bone tissues tightly and stably adhere to the Ta coating after the implantation, with no signs of loosening. Early after implantation, there is no significant difference in periprosthetic bone volume and ultimate shear strength between Ta-coated and Ti-coated prostheses (P > 0.05). EDX analysis suggests that the ultimate shear stress does not damage Ta coating. Mechanical strength testing shows that the adhesive strength and Vicker's surface hardness (HV) of the Ta coating are significantly higher than those of the Ti coating (P < 0.01). Ta coating has good stability and bone biocompatibility; the extraordinary physical characteristics of Ta coating have great significance in maintaining prosthetic stability and surface porosity after implantation.

Effects of extrusion and heat treatment on the mechanical properties and biocorrosion behaviors of a Mg-Nd-Zn-Zr alloy.

PubMed

Zhang, Xiaobo; Yuan, Guangyin; Mao, Lin; Niu, Jialin; Fu, Penghuai; Ding, Wenjiang

2012-03-01

Mechanical properties at room temperature and biocorrosion behaviors in simulated body fluid (SBF) at 37 °C of a new type of patented Mg-3Nd-0.2Zn-0.4Zr (hereafter, denoted as JDBM) alloy prepared at different extrusion temperatures, as well as heat treatment, were studied. The mechanical properties of this magnesium alloy at room temperature were improved significantly after extrusion and heat treatment compared to an as-cast alloy. The results of mechanical properties show that the yield strength (YS) decreases with increasing extrusion temperature. The tensile elongation decreases a little while the ultimate tensile strength (UTS) has no obvious difference. The yield strength and ultimate tensile strength were improved clearly after heat treatment at 200 °C for 10 h compared with that at the extrusion state, which can be mainly contributed to the precipitation strengthening. The biocorrosion behaviors of the JDBM alloy were studied using immersion tests and electrochemical tests. The results reveal that the extruded JDBM alloy and the aging treatment on the extruded alloy show much better biocorrosion resistance than that at solid solution state (T4 treatment), and the JDBM exhibited favorable uniform corrosion mode in SBF. Copyright © 2011 Elsevier Ltd. All rights reserved.

Strengthening of σ phase in a Fe20Cr9Ni cast austenite stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Y.Q., E-mail: yqwang@ahut.edu.cn; School of Materials Science and Engineering, Anhui University of Technology, Maanshan, Anhui, 243002; Han, J.

2013-10-15

The strengthening mechanism of σ phase in a Fe20Cr9Ni cast austenite stainless steel used for primary coolant pipes of nuclear power plants has been investigated. The yield and ultimate tensile strengths of aged specimens increased comparing with those of the unaged ones. It was found that the increase of strengths is due to the hard and brittle (σ + γ{sub 2}) structure which decomposed from α phase in the steel. Fracture surfaces of specimens after in situ tensile test showed that the inhibition of (σ + γ{sub 2}) structure on the dislocation movements was more significant than ferrite although cracksmore » started predominately at σ/γ{sub 2} interfaces. The (σ + γ{sub 2}) structure behaves like a fiber reinforced composite material. - Highlights: • The strengthening mechanism of σ phase in a Fe20Cr9Ni CASS is investigated. • The yield and ultimate tensile strengths increase with increasing of σ phase. • The increase of strengths is due to hard and brittle (σ + γ{sub 2}) structure. • The (σ + γ{sub 2}) structure in CASS behaves like a fibre reinforced composite material. • The σ/γ{sub 2} and α/σ/γ{sub 2} boundaries hinder the movement of dislocation.« less

Failure models for textile composites

NASA Technical Reports Server (NTRS)

Cox, Brian

1995-01-01

The goals of this investigation were to: (1) identify mechanisms of failure and determine how the architecture of reinforcing fibers in 3D woven composites controlled stiffness, strength, strain to failure, work of fracture, notch sensitivity, and fatigue life; and (2) to model composite stiffness, strength, and fatigue life. A total of 11 different angle and orthogonal interlock woven composites were examined. Composite properties depended on the weave architecture, the tow size, and the spatial distributions and strength of geometrical flaws. Simple models were developed for elastic properties, strength, and fatigue life. A more complicated stochastic model, called the 'Binary Model,' was developed for damage tolerance and ultimate failure. These 3D woven composites possessed an extraordinary combination of strength, damage tolerance, and notch insensitivity.

The influence of cyclic shear fatigue on the bracket-adhesive-enamel complex: an in vitro study.

PubMed

Daratsianos, Nikolaos; Musabegovic, Ena; Reimann, Susanne; Grüner, Manfred; Jäger, Andreas; Bourauel, Christoph

2013-05-01

To describe the effect of fatigue on the strength of the bracket-adhesive-enamel complex and characterize the fatigue behavior of the materials tested. Upper central incisor brackets (Discovery(®), Dentaurum) were bonded with a light-curing (Transbond XT™, 3M Unitek) and a chemically-curing adhesive (Concise™, 3M Unitek) on bovine teeth embedded in cylindrical resign bases and stored in water at 37(±2)°C for 24 (±2)h. The first 15 specimens were tested with a universal testing machine ZMART.PRO(®) (Zwick GmbH & Co. KG, Ulm, Germany) for ultimate shear bond strength according to the DIN-13990-2-standard. The remaining three groups of 20 specimens underwent fatigue staircase testing of 100, 1000 and 3000 cycles at 1Hz with a self-made testing machine. The survived specimens were subjected to shear strength testing. The fatigued specimens showed decreased shear strength with both adhesives at all cycle levels. The shear strength after fatigue for 100, 1000 and 3000 cycles was in the Concise™-groups 34.8%, 59.0%, 47.3% and in the Transbond™ XT-groups 33.6%, 23.1%, 27.3% relative to the ultimate shear strength. The fatigue life of the Concise™-groups decreased with increasing stress and Transbond™ XT showed lower fatigue ratio with no obvious trend. The specimens bonded with Transbond™ XT showed typically favorable fracture modes in contrary to Concise™. Fatigue of the bracket-adhesive-enamel complex decreased its shear strength. The staircase method can provide a standardized experimental protocol for fatigue studies, however testing at various cycle numbers is recommended. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Local time, seasonal, and solar cycle dependency of longitudinal variations of TEC along the crest of EIA over India

NASA Astrophysics Data System (ADS)

Sunda, Surendra; Vyas, B. M.

2013-10-01

global wave number 4 structure in the Indian longitudinal region spanning from ~70 to 95°E forming the upward slope of the peak in the total electron content (TEC) are reported along the crest of equatorial ionization anomaly (EIA). The continuous and simultaneous measurements from five GPS stations of GPS Aided Geo Augmented Navigation (GAGAN) network are used in this study. The long-term database (2004-2012) is utilized for examining the local time, seasonal, and solar cycle dependency on the longitudinal variations of TEC. Our results confirm the existence of longitudinal variations of TEC in accordance with wave number 4 longitudinal structure including its strength. The results suggest that these variations, in general, start to develop at ~09 LT, achieve maximum strength at 12-15 LT, and decay thereafter, the decay rate depending on the season. They are more pronounced in equinoctial season followed by summer and winter. The longitudinal variations persist beyond midnight in equinox seasons, whereas in winter, they are conspicuously absent. Interestingly, they also exhibit significant solar cycle dependence in the solstices, whereas in the equinoxes, they are independent of solar activity. The comparison of crest-to-trough ratio (CTR) in the eastern (92°E) and western (72°E) extreme longitudes reveals higher CTR on the eastern side than over the western extreme, suggesting the role of nonmigrating tides in modulating the ExB vertical drift and the consequential EIA crest formation.

THIGH MUSCLE CROSS-SECTIONAL AREAS AND STRENGTH IN KNEES WITH EARLY VS KNEES WITHOUT RADIOGRAPHIC KNEE OSTEOARTHRITIS: A BETWEEN-KNEE, WITHIN-PERSON COMPARISON

PubMed Central

Ruhdorfer, AS; Dannhauer, T; Wirth, W; Cotofana, S; Roemer, F; Nevitt, M; Eckstein, F

2014-01-01

Objective To compare cross-sectional and longitudinal side-differences in thigh muscle anatomical cross-sectional areas (ACSAs), muscle strength, and specific strength (strength/ACSA), between knees with early radiographic change vs. knees without radiographic knee osteoarthritis (RKOA), in the same person. Design 55 (of 4796) Osteoarthritis Initiative participants fulfilled the inclusion criteria of early RKOA in one limb (definite tibiofemoral osteophytes; no radiographic joint space narrowing [JSN]) vs. no RKOA (no osteophyte; no JSN) in the contralateral limb. ACSAs of the thigh muscles and quadriceps heads were determined using axial MRIs at 33%/30% femoral length (distal to proximal). Isometric extensor and flexor muscle strength were measured (Good Strength Chair). Baseline quadriceps ACSA and extensor (specific) strength represented the primary analytic focus, and two-year changes of quadriceps ACSAs the secondary focus. Results No statistically significant side-differences in quadriceps (or other thigh muscle) ACSAs, muscle strength, or specific strength were observed between early RKOA vs. contralateral limbs without RKOA (p≥0.44), neither in men nor in women. The two-year reduction in quadriceps ACSA in limbs with early RKOA was −0.9±6% (mean ± standard deviation) vs. −0.5±6% in limbs without RKOA (statistical difference p=0.85). Conclusion Our results do not provide evidence that early unilateral radiographic changes, i.e. presence of osteophytes, are associated with cross-sectional or longitudinal differences in quadriceps muscle status compared with contralateral knees without RKOA. At the stage of early unilateral RKOA there thus appears to be no clinical need for countervailing a potential dys-balance in quadriceps ACSAs and strength between both knees. PMID:25278072

[Design and fabrication of the custom-made titanium condyle by selective laser melting technology].

PubMed

Chen, Jianyu; Luo, Chongdai; Zhang, Chunyu; Zhang, Gong; Qiu, Weiqian; Zhang, Zhiguang

2014-10-01

To design and fabricate the custom-made titanium mandibular condyle by the reverse engineering technology combined with selective laser melting (SLM) technology and to explore the mechanical properties of the SLM-processed samples and the application of the custom-made condyle in the temporomandibular joint (TMJ) reconstruction. The three-dimensional model of the mandibular condyle was obtained from a series of CT databases. The custom-made condyle model was designed by the reverse engineering software. The mandibular condyle was made of titanium powder with a particle size of 20-65 µm as the basic material and the processing was carried out in an argon atmosphere by the SLM machine. The yield strength, ultimate strength, bending strength, hardness, surface morphology and roughness were tested and analyzed. The finite element analysis (FEA) was used to analyze the stress distribution. The complex geometry and the surface of the custom-made condyle can be reproduced precisely by the SLM. The mechanical results showed that the yield strength, ultimate strength, bending strength and hardness were (559±14) MPa, (659±32) MPa, (1 067±42) MPa, and (212±4)HV, respectively. The surface roughness was reduced by sandblast treatment. The custom-made titanium condyle can be fabricated by SLM technology which is time-saving and highly digitized. The mechanical properties of the SLM sample can meet the requirements of surgical implant material in the clinic. The possibility of fabricating custom-made titanium mandibular condyle combined with the FEA opens new interesting perspectives for TMJ reconstruction.

The influence of heat treatments on several types of base-metal removable partial denture alloys.

PubMed

Morris, H F; Asgar, K; Rowe, A P; Nasjleti, C E

1979-04-01

Four removable partial denture alloys, Vitallium (Co-Cr alloy), Dentillium P.D. (Fe-Cr alloy), Durallium L.G. (Co-Cr-Ni alloy), and Ticonium 100 (Ni-Cr alloy), were evaluated in the as-cast condition and after heat treatment for 15 minutes at 1,300 degrees, 1,600 degrees, 1,900 degrees, and 2,200 degrees F followed by quenching in water. The following properties were determined and compared for each alloy at each heat treatment condition: the yield strengths at 0.01%, 0.1%, and 0.2% offsets, the ultimate tensile strength, the percent elongation, the modulus of elasticity, and the Knoop microhardness. The results were statistically analyzed. Photomicrographs were examined for each alloy and test condition. The following conclusions were made: 1. The "highest values" were exhibited by the as-cast alloy. 2. Heat treatment of the partial denture alloys tested resulted in reductions in strength, while the elongations varied. This study demonstrates that, in practice, one should avoid (a) prolonged "heat-soaking" while soldering and (b) grinding or polishing of the casting until the alloy is "red hot". 3. Durallium L.G. was the least affected by the various heat treatment conditions. 4. Conventional reporting of the yield strength at 0.2% offset, the ultimate tensile strength, and percent elongation are not adequate to completely describe and compare the mechanical behavior of alloys. The reporting of the yield strength at 0.01% offset, in addition to the other reported properties, will provide a more complete description of the behavior of the dental alloys.

Compression Properties and Electrical Conductivity of In-Situ 20 vol.% Nano-Sized TiCx/Cu Composites with Different Particle Size and Morphology

PubMed Central

Zhang, Dongdong; Bai, Fang; Sun, Liping; Wang, Yong; Wang, Jinguo

2017-01-01

The compression properties and electrical conductivity of in-situ 20 vol.% nano-sized TiCx/Cu composites fabricated via combustion synthesis and hot press in Cu-Ti-CNTs system at various particles size and morphology were investigated. Cubic-TiCx/Cu composite had higher ultimate compression strength (σUCS), yield strength (σ0.2), and electric conductivity, compared with those of spherical-TiCx/Cu composite. The σUCS, σ0.2, and electrical conductivity of cubic-TiCx/Cu composite increased by 4.37%, 20.7%, and 17.8% compared with those of spherical-TiCx/Cu composite (526 MPa, 183 MPa, and 55.6% International Annealed Copper Standard, IACS). Spherical-TiCx/Cu composite with average particle size of ~94 nm exhibited higher ultimate compression strength, yield strength, and electrical conductivity compared with those of spherical-TiCx/Cu composite with 46 nm in size. The σUCS, σ0.2, and electrical conductivity of spherical-TiCx/Cu composite with average size of ~94 nm in size increased by 17.8%, 33.9%, and 62.5% compared with those of spherical-TiCx/Cu composite (417 MPa, 121 MPa, and 40.3% IACS) with particle size of 49 nm, respectively. Cubic-shaped TiCx particles with sharp corners and edges led to stress/strain localization, which enhanced the compression strength of the composites. The agglomeration of spherical-TiCx particles with small size led to the compression strength reduction of the composites. PMID:28772859

Individual and social determinants of multiple chronic disease behavioral risk factors among youth.

PubMed

Alamian, Arsham; Paradis, Gilles

2012-03-22

Behavioral risk factors are known to co-occur among youth, and to increase risks of chronic diseases morbidity and mortality later in life. However, little is known about determinants of multiple chronic disease behavioral risk factors, particularly among youth. Previous studies have been cross-sectional and carried out without a sound theoretical framework. Using longitudinal data (n = 1135) from Cycle 4 (2000-2001), Cycle 5 (2002-2003) and Cycle 6 (2004-2005) of the National Longitudinal Survey of Children and Youth, a nationally representative sample of Canadian children who are followed biennially, the present study examines the influence of a set of conceptually-related individual/social distal variables (variables situated at an intermediate distance from behaviors), and individual/social ultimate variables (variables situated at an utmost distance from behaviors) on the rate of occurrence of multiple behavioral risk factors (physical inactivity, sedentary behavior, tobacco smoking, alcohol drinking, and high body mass index) in a sample of children aged 10-11 years at baseline. Multiple behavioral risk factors were assessed using a multiple risk factor score. All statistical analyses were performed using SAS, version 9.1, and SUDAAN, version 9.01. Multivariate longitudinal Poisson models showed that social distal variables including parental/peer smoking and peer drinking (Log-likelihood ratio (LLR) = 187.86, degrees of freedom (DF) = 8, p < .001), as well as individual distal variables including low self-esteem (LLR = 76.94, DF = 4, p < .001) increased the rate of occurrence of multiple behavioral risk factors. Individual ultimate variables including age, sex, and anxiety (LLR = 9.34, DF = 3, p < .05), as well as social ultimate variables including family socioeconomic status, and family structure (LLR = 10.93, DF = 5, p = .05) contributed minimally to the rate of co-occurrence of behavioral risk factors. The results suggest targeting individual/social distal variables in prevention programs of multiple chronic disease behavioral risk factors among youth.

High-Strength Low-Alloy Steel Strengthened by Multiply Nanoscale Microstructures

NASA Astrophysics Data System (ADS)

Shen, Y. F.; Zuo, L.

Recently, we have being focused on improving the strength without sacrificing ductility of High-strength low-alloy (HSLA) steels by designing nanostructures. Several developments have been obtained, summarized as the following three parts: (a) Depressively nanoscale precipitates: A ferritic steel with finely dispersed precipitates reveals a yield strength of 760 MPa, approximately three times higher than that of conventional Ti-bearing high strength hot-rolled sheet steels, and its ultimate tensile strength reaches 850 MPa with an elongation-to-failure value of 18%. The finely dispersed TiC precipitates in the matrix provide matrix strengthening. The estimated magnitude of precipitation strengthening is around 458 MPa. The effects of the particle size, particle distribution and intrinsic particle strength have been investigated through dislocation dynamics (DD) simulations. The DD results show that strengthening is not only a function of the density of the nano-scale precipitates but also of their size. (b) Ultrafinely ferritic plate: An interstitial-free (IF) steel sheet with a cold-rolling reduction of 75% shows a high tensile strength (710MPa) while preserving a considerable plastic strain (13%). The ductility recovery with increasing the rolling reduction up to 75% is related with the decreasing both in lamellar spacings and cell blocks sizes. (c) Parallel nano-laminated austenite: A composite microstructure consisting of ferrite, bainitic ferrite (BF) laths and retained austenite (RA) platelets has been found for the steel with a chemical composition of 0.19C-0.30Si-1.76Mn-1.52Al (in mass fraction), processed with annealing and bainitic holding. The sample annealed at 820oC (for 120s) and partitioned at 400oC (for 300s) has the best combination of ultimate tensile strength (UTS, 682 MPa) and elongation to failure ( 70%) with about 26% of BF plates 16% RA in its microstructure.

Analysis of the rivets from the RMS Titanic using experimental and theoretical techniques

NASA Astrophysics Data System (ADS)

Hooper, Jennifer Jo

Earlier studies of Titanic wrought iron rivets revealed an anisotropic, inhomogeneous composite material composed of glassy iron silicate (slag) particles embedded in a ferrite matrix. Micrographs indicated a directional character to the slag "stringers" that follows the method of processing---aligned parallel to the shaft in the center of the rivet, but oriented perpendicular to the shaft within the inner section of each head. It was proposed that the re-orientation of large slag particles in the rivet head weakened this region, predisposing the rivets to fail as a result of collision with the iceberg. Using quantitative metallography, mechanical testing, and a combination of modeling techniques, this hypothesis was tested using 35 Titanic rivets and additional contemporary wrought iron. Results revealed that the wrought iron microstructure showed a high slag content that was very coarse and unevenly distributed. Results from micro structural, chemical and mechanical analysis, as well as supporting historical evidence, suggested that two types of rivets, both wrought iron and steel, were used on the Titanic. Tensile testing results indicated that the longitudinal orientation in wrought iron possesses an average of 20% higher tensile strength and nearly four times the ductility of the transverse orientation. Results for Titanic rivet steel suggest a 100MPa enhancement in yield strength and tensile strength over wrought iron. Sequential imaging during mechanical testing, supported by micromechanical modeling predictions, indicated that the mechanical behavior of wrought iron is strongly affected by the orientation, distribution and content of slag within the matrix. Finite element analysis of a wrought iron rivet with anisotropic properties demonstrated that, because of poor ductility produced by the re-orientation of slag within the head, a Titanic rivet could not withstand a 5mm displacement of the hull's steel plates. Due to its low ultimate tensile strength, the wrought iron rivet would fail after an additional load that is 2.5 times less than that required for the steel rivet failure. This evidence suggests that as a result of the collision with the iceberg, failure at the junction of the head and shaft caused "popping" of rivet's heads and the opening of riveted seams.

Experimentation and analysis of mechanical behavior modification of titanium matrix composites through controlled fiber placement

NASA Astrophysics Data System (ADS)

Bowman, Cheryl Lynne

Titanium composites reinforced with SiC fibers in a uniaxial direction are being considered for various high temperature applications which require high specific strength or stiffness in the primary loading direction. However the very low tensile and creep strength of these composites in the transverse direction (loading perpendicular to the fiber axis) limits their use in many practical applications. Recent advances in composite fabrication techniques have provided not only better control of fiber volume fraction and distribution, but also the ability to control the relative fiber placement. The goal of this research was produce continuously reinforced SiC/Ti composites with precise fiber arrangement in order to ascertain the significance of fiber arrangements on transverse mechanical properties. In this study, TIMETAL 21S and Ti-6-4 composites reinforced with SCS-6 SiC fibers were produced with six distinct fiber placement arrangements. The effect of fiber placement on uniaxial tensile and creep behaviors was assessed and the results compared to analytical predictions. Consistent with analytical predictions, the fiber arrangements used in this study did not significantly change the longitudinal tensile behavior, but differences were obtained in the transverse loading response. For example, a diamond (non-equilateral triangle) fiber packing was found to have a higher transverse ultimate tensile strength and better transverse creep resistance than a rectangular fiber packing arrangement for a given volume fraction and fiber spacing (within-ply vs. between-ply). Initially this result appeared to be in contrast to previous computational and analytical simulations which predicted more favorable mechanical behavior for rectangular-type arrangements. However, this experimental/predictive conflict was resolved, in part, by simply defining a fiber spacing ratio which could describe both rectangular type and diamond-type arrangements. The computationally efficient Micromechanical Analysis Code based on the Generalized Method of Cells captured the correct behavior trends for these fiber arrangements and thus can be used to estimate the optimum fiber arrangement for a given materials system. Although this research utilized SiC/titanium alloy composites, the results should be relevant to any composite with a continuous reinforcement, a ductile matrix, and a finite fiber/matrix interfacial bond strength.

Concurrent and Longitudinal Links between Children's and Their Friends' Antisocial and Prosocial Behavior in Preschool

ERIC Educational Resources Information Center

Eivers, Areana R.; Brendgen, Mara; Vitaro, Frank; Borge, Anne I. H.

2012-01-01

Concurrent and longitudinal links between children's own and their nominated best friends' antisocial and prosocial behavior were studied in a normative sample of 3-5-year-olds (N = 203). Moderating effects of age and gender were also explored. Subscales of the Strength and Difficulties Questionnaire (SDQ) were used to obtain teacher ratings of…

Instability of Longitudinal Wave in Magnetized Strongly Coupled Dusty Plasma

NASA Astrophysics Data System (ADS)

Xie, Bai-Song

2003-12-01

Instability of longitudinal wave in magnetized strongly coupled dusty plasmas is investigated. The dust charging relaxation is taken into account. It is found that there exists threshold of interdust distance for the instability of wave, which is determined significantly by the dust charging relaxation, the coupling parameter of high correlation of dust as well the strength of magnetic field.

Tuning the mechanical properties of glass fiber-reinforced bismaleimide–triazine resin composites by constructing a flexible bridge at the interface

PubMed Central

Zeng, Xiaoliang; Yu, Shuhui; Lai, Maobai; Sun, Rong; Wong, Ching-Ping

2013-01-01

We demonstrate a new method that can simultaneously improve the strength and toughness of the glass fiber-reinforced bismaleimide–triazine (BT) resin composites by using polyethylene glycol (PEG) to construct a flexible bridge at the interface. The mechanical properties, including the elongation, ultimate tensile stress, Young’s modulus, toughness and dynamical mechanical properties were studied as a function of the length of PEG molecular chain. It was found that the PEG molecule acts as a bridge to link BT resin and glass fiber through covalent and non-covalent bondings, respectively, resulting in improved interfacial bonding. The incorporation of PEG produces an increase in elongation, ultimate tensile stress and toughness. The Young’s modulus and Tg were slightly reduced when the length of the PEG molecular chain was high. The elongation of the PEG-modified glass fiber-reinforced composites containing 5 wt% PEG-8000 increased by 67.1%, the ultimate tensile stress by 17.9% and the toughness by 78.2% compared to the unmodified one. This approach provides an efficient way to develop substrate material with improved strength and toughness for integrated circuit packaging applications. PMID:27877621

Ultrasonic Corrosion Fatigue Behavior of High Strength Austenitic Stainless Steels

NASA Astrophysics Data System (ADS)

Ebara, R.; Yamaguchi, Y.; Kanei, D.; Yamamoto, Y.

Ultrasonic corrosion fatigue tests were conducted for high strength austenitic stainless steels such as YUS270 and SUS304N2 in 3%NaCl aqueous solution. The reduction of giga-cycle corrosion fatigue strength of YUS270 and SUS304N2 was not observed at all, while the reduction of corrosion fatigue life was observed at higher stress amplitude. Corrosion pit was observed on corrosion fatigue crack initiation area. Striation was predominantly observed on crack propagation area in air and in 3% NaCl aqueous solution. The reduction of corrosion fatigue strength of high strength austenitic stainless steels such as YUS270 and SUS304N2 is due to the corrosion pit formation at corrosion fatigue crack initiation area. It can be concluded that the higher the ultimate tensile strength of austenitic stainless steels the higher the giga-cycle corrosion fatigue strength in 3%NaCl aqueous solution is.

Global longitudinal strain by two-dimensional speckle tracking imaging predicts exercise capacity in patients with chronic heart failure.

PubMed

Kou, Seisyou; Suzuki, Kengo; Akashi, Yoshihiro J; Mizukoshi, Kei; Takai, Manabu; Izumo, Masaki; Shimozato, Takashi; Hayashi, Akio; Ohtaki, Eiji; Osada, Naohiko; Omiya, Kazuto; Nobuoka, Sachihiko; Miyake, Fumihiko

2011-06-01

Left ventricular ejection fraction (LVEF) predicts mortality in patients with chronic heart failure (CHF). However, a weak correlation was found between LVEF and peak oxygen uptake ([Formula: see text]) in CHF patients. Global longitudinal strain measured by two-dimensional (2D) strain is regarded as a more useful predictor of cardiac events than LVEF. We investigated whether 2D strain obtained at rest could predict peak [Formula: see text] in patients with CHF. Fifty-one patients (mean age of 54.0 ± 12.0 years, 14 females, LVEF 46.0 ± 15.0%) with stable CHF underwent resting echocardiography and cardiopulmonary exercise testing. Leg muscle strength was measured for the evaluation of peripheral factors. Global longitudinal strain (GLS) in the apical 4-, 3-, and 2-chamber views and global circumferential strain (GCS) in the parasternal mid short-axis view were measured. In all patients, peak [Formula: see text] correlated with leg muscle strength (r = 0.55, p < 0.0001), LVEF (r = 0.46, p < 0.001), GLS (r = -0.45, p < 0.001), and GCS (r = -0.41, p = 0.005), respectively. No significant correlation was found between the ratio of early transmitral velocity to peak early diastolic mitral annulus velocity (E/E') and peak [Formula: see text]. In the patients with heart failure and reduced LVEF, a multiple stepwise linear regression analysis based on leg muscle strength, LVEF, E/E', GLS, and GCS was performed to identify independent predictors of peak [Formula: see text], resulting in leg muscle strength and GLS (R (2) = 0.888) as independent predictors of peak [Formula: see text]. Global longitudinal strain at rest could possibly predict exercise capacity, which appeared to be more useful than LVEF, E/E', and GCS in CHF patients with reduced LVEF.

Analysis of the vector magnetic fields of complex sunspots

NASA Technical Reports Server (NTRS)

Patty, S. R.

1981-01-01

An analysis of the vector magnetic field in the delta-configurations of two complex sunspot groups is presented, noting several characteristics identified in the delta-configurations. The observations of regions 2469 (S12E80) and 2470 (S21E83) took place in May, 1980 with a vector magnetograph, verified by optical viewing. Longitudinal magnetic field plots located the delta-configurations in relation to the transverse field neutral line. It is shown that data on the polarization yields qualitative information on the magnetic field strengths, while the azimuth of the transverse field can be obtained from the relative intensities of linear polarization measurements aligned with respect to the magnetograph analyses axis at 0 and 90 deg, and at the plus and minus 45 deg positions. Details of the longitudinal fields are discussed. A strong, sheared transverse field component is found to be a signature of strong delta. A weak delta is accompanied by a weak longitudinal gradient with an unsheared transverse component of variable strength.

Reliability analysis of structures under periodic proof tests in service

NASA Technical Reports Server (NTRS)

Yang, J.-N.

1976-01-01

A reliability analysis of structures subjected to random service loads and periodic proof tests treats gust loads and maneuver loads as random processes. Crack initiation, crack propagation, and strength degradation are treated as the fatigue process. The time to fatigue crack initiation and ultimate strength are random variables. Residual strength decreases during crack propagation, so that failure rate increases with time. When a structure fails under periodic proof testing, a new structure is built and proof-tested. The probability of structural failure in service is derived from treatment of all the random variables, strength degradations, service loads, proof tests, and the renewal of failed structures. Some numerical examples are worked out.

Tendon material properties vary and are interdependent among turkey hindlimb muscles

PubMed Central

Matson, Andrew; Konow, Nicolai; Miller, Samuel; Konow, Pernille P.; Roberts, Thomas J.

2012-01-01

SUMMARY The material properties of a tendon affect its ability to store and return elastic energy, resist damage, provide mechanical feedback and amplify or attenuate muscle power. While the structural properties of a tendon are known to respond to a variety of stimuli, the extent to which material properties vary among individual muscles remains unclear. We studied the tendons of six different muscles in the hindlimb of Eastern wild turkeys to determine whether there was variation in elastic modulus, ultimate tensile strength and resilience. A hydraulic testing machine was used to measure tendon force during quasi-static lengthening, and a stress–strain curve was constructed. There was substantial variation in tendon material properties among different muscles. Average elastic modulus differed significantly between some tendons, and values for the six different tendons varied nearly twofold, from 829±140 to 1479±106 MPa. Tendons were stretched to failure, and the stress at failure, or ultimate tensile stress, was taken as a lower-limit estimate of tendon strength. Breaking tests for four of the tendons revealed significant variation in ultimate tensile stress, ranging from 66.83±14.34 to 112.37±9.39 MPa. Resilience, or the fraction of energy returned in cyclic length changes was generally high, and one of the four tendons tested was significantly different in resilience from the other tendons (range: 90.65±0.83 to 94.02±0.71%). An analysis of correlation between material properties revealed a positive relationship between ultimate tensile strength and elastic modulus (r2=0.79). Specifically, stiffer tendons were stronger, and we suggest that this correlation results from a constrained value of breaking strain, which did not vary significantly among tendons. This finding suggests an interdependence of material properties that may have a structural basis and may explain some adaptive responses observed in studies of tendon plasticity. PMID:22771746

Tendon material properties vary and are interdependent among turkey hindlimb muscles.

PubMed

Matson, Andrew; Konow, Nicolai; Miller, Samuel; Konow, Pernille P; Roberts, Thomas J

2012-10-15

The material properties of a tendon affect its ability to store and return elastic energy, resist damage, provide mechanical feedback and amplify or attenuate muscle power. While the structural properties of a tendon are known to respond to a variety of stimuli, the extent to which material properties vary among individual muscles remains unclear. We studied the tendons of six different muscles in the hindlimb of Eastern wild turkeys to determine whether there was variation in elastic modulus, ultimate tensile strength and resilience. A hydraulic testing machine was used to measure tendon force during quasi-static lengthening, and a stress-strain curve was constructed. There was substantial variation in tendon material properties among different muscles. Average elastic modulus differed significantly between some tendons, and values for the six different tendons varied nearly twofold, from 829±140 to 1479±106 MPa. Tendons were stretched to failure, and the stress at failure, or ultimate tensile stress, was taken as a lower-limit estimate of tendon strength. Breaking tests for four of the tendons revealed significant variation in ultimate tensile stress, ranging from 66.83±14.34 to 112.37±9.39 MPa. Resilience, or the fraction of energy returned in cyclic length changes was generally high, and one of the four tendons tested was significantly different in resilience from the other tendons (range: 90.65±0.83 to 94.02±0.71%). An analysis of correlation between material properties revealed a positive relationship between ultimate tensile strength and elastic modulus (r(2)=0.79). Specifically, stiffer tendons were stronger, and we suggest that this correlation results from a constrained value of breaking strain, which did not vary significantly among tendons. This finding suggests an interdependence of material properties that may have a structural basis and may explain some adaptive responses observed in studies of tendon plasticity.

Torsion Tests of 24S-T Aluminum-alloy Noncircular Bar and Tubing

NASA Technical Reports Server (NTRS)

Moore, R L; Paul, D A

1943-01-01

Tests of 24S-T aluminum alloy have been made to determine the yield and ultimate strengths in torsion of noncircular bar and tubing. An approximate basis for predicting these torsional strength characteristics has been indicated. The results show that the torsional stiffness and maximum shearing stresses within the elastic range may be computed quite closely by means of existing formulas based on mathematical analysis and the membrane analogy.

Shear Bond Strength of Metal Brackets to Zirconia Conditioned with Various Primer-Adhesive Systems

DTIC Science & Technology

2016-07-01

Reynolds, 1979 ). Bonding orthodontic brackets to ceramic restorative materials poses a unique challenge. Abu et al. measured the strength between...forth by Reynolds and 34 others (Reynolds, 1979 ). The pertinent question is the following: should brackets be chemically bonded to zirconia...conditioned with a new silane coupling agent. Eur J Orthod. 2013 Feb;35(1):103-9. 40 Giannini M, Soares CJ, de Carvalho RM. Ultimate tensile

Exploratory Development of Improved Fatigue Strength Adhesives

DTIC Science & Technology

1974-11-01

fiber reinforced adhesives. A fifty-fold in-j crease in fatigue life at equivalent stress levels was achieved when a woven high modulus graphite...the stress level which could survive 10’ fatigue cycles was increased from approximately 30 percent of the ultimate shear strength with nylor knit...supports to as much as fifty percent with the high modulus fiber bond line reinforcement. The stress level which could withstand 10’ fatigue cycles

Density matrix solutions for the susceptibilities of a three-level system with arbitrary relaxation rates and field strengths

NASA Technical Reports Server (NTRS)

Ryan, J. C.; Lawandy, N. M.

1986-01-01

The susceptibilities for a three-level system with arbitrary pump and signal field strengths are derived for arbitrary longitudinal and transverse relaxation rates. The results are of interest in connection with the calculation of the Raman gain in systems where resonance enhancement plays a dominant role.

Associations between Family Relationships and Symptoms/Strengths at Kindergarten Age: What Is the Role of Children's Parental Representations?

ERIC Educational Resources Information Center

Stadelmann, Stephanie; Perren, Sonja; von Wyl, Agnes; von Klitzing, Kai

2007-01-01

Background: The quality of the family relationships plays an important role in the development of children's psychopathology and in their socio-emotional development. This longitudinal study aims to investigate whether family relationships are related to children's symptoms/strengths at kindergarten, and whether family relationships are predictors…

Microhardness Testing of Aluminum Alloy Welds

NASA Technical Reports Server (NTRS)

Bohanon, Catherine

2009-01-01

A weld is made when two pieces of metal are united or fused together using heat or pressure, and sometimes both. There are several different types of welds, each having their own unique properties and microstructure. Strength is a property normally used in deciding which kind of weld is suitable for a certain metal or joint. Depending on the weld process used and the heat required for that process, the weld and the heat-affected zone undergo microstructural changes resulting in stronger or weaker areas. The heat-affected zone (HAZ) is the region that has experienced enough heat to cause solid-state microstructural changes, but not enough to melt the material. This area is located between the parent material and the weld, with the grain structure growing as it progresses respectively. The optimal weld would have a short HAZ and a small fluctuation in strength from parent metal to weld. To determine the strength of the weld and decide whether it is suitable for the specific joint certain properties are looked at, among these are ultimate tensile strength, 0.2% offset yield strength and hardness. Ultimate tensile strength gives the maximum load the metal can stand while the offset yield strength gives the amount of stress the metal can take before it is 0.2% longer than it was originally. Both of these are good tests, but they both require breaking or deforming the sample in some way. Hardness testing, however, provides an objective evaluation of weld strengths, and also the difference or variation in strength across the weld and HAZ which is difficult to do with tensile testing. Hardness is the resistance to permanent or plastic deformation and can be taken at any desired point on the specimen. With hardness testing, it is possible to test from parent metal to weld and see the difference in strength as you progress from parent material to weld. Hardness around grain boundaries and flaws in the material will show how these affect the strength of the metal while still retaining the sample. This makes hardness testing a good test for identifying grain size and microstructure.

Ultimate strength analysis of inland tank barges

DOT National Transportation Integrated Search

1997-06-16

In an effort to understand the cause of recent catastrophic failures of inland tank barges and reduce the possibility of future casualties, the Coast Guard Marine Safety Center (MSC) studied the buckling" phenomenon. In conclusion, inland tank barges...

Increase of reliability of contact networks of electric transport, due to increase of strength of the joint unit of pipes of different diameters

NASA Astrophysics Data System (ADS)

Sabitov, L. S.; Kashapov, N. F.; Gilmanshin, I. R.; Gatiyatov, I. Z.; Kuznetsov, I. L.

2017-09-01

The feature of the stress state of the supports of the contact networks is the presence of a joint of pipes of different diameters, the ultimate state of which is determined, as a rule, the strength of the weld. The proposed unit allows to increase the reliability and strength of the connection and also exclude the presence of a weld bead on the outer surface of the pipe of smaller diameter in the place of its attachment to the upper end of the support ring.

High strain rate properties of off-axis composite laminates, part 2

NASA Technical Reports Server (NTRS)

Daniel, I. M.

1991-01-01

Unidirectional off-axis graphite/epoxy and graphite/S-glass/epoxy laminates were characterized in uniaxial tension at strain rates ranging from quasi-static to over 500 s(sup -1). Laminate ring specimens were loaded by internal pressure with the tensile stress at 22.5, 30, and 45 degrees relative to the fiber direction. Results were presented in the form of stress-strain curves to failure. Properties determined included moduli, Poisson's ratios, strength, and ultimate strain. In all three laminates of both materials the modulus and strength increase sharply with strain rate, reaching values roughly 100, 150, and 200 percent higher than corresponding static values for the 22.5(sub 8), 30(sub 8), and 45(sub 8) degree laminates, respectively. In the case of ultimate strain no definite trends could be established, but the maximum deviation from the average of any value for any strain rate was less than 18 percent.

Carbon fiber reinforced root canal posts. Mechanical and cytotoxic properties.

PubMed

Torbjörner, A; Karlsson, S; Syverud, M; Hensten-Pettersen, A

1996-01-01

The aim of this study was to compare the mechanical properties of a prefabricated root canal post made of carbon fiber reinforced composites (CFRC) with metal posts and to assess the cytotoxic effects elicited. Flexural modulus and ultimate flexural strength was determined by 3 point loading after CRFC posts had been stored either dry or in water. The bending test was carried out with and without preceding thermocycling of the CFRC posts. The cytotoxicity was evaluated by an agar overlay method after dry and wet storage. The values of flexural modulus and ultimate flexural strength were for dry stored CFRC post 82 +/- 6 GPa and 1154 +/- 65 MPa respectively. The flexural values decreased significantly after water storage and after thermocycling. No cytotoxic effects were observed adjacent to any CFRC post. Although fiber reinforced composites may have the potential to replace metals in many clinical situations, additional research is needed to ensure a satisfying life-span.

An experimental investigation on the ultimate strength of epoxy repaired braced partial infilled RC frames

NASA Astrophysics Data System (ADS)

Dubey, Shailendra Kumar Damodar; Kute, Sunil

2014-09-01

Due to earthquake, buildings are damaged partially or completely. Particularly structures with soft storey are mostly affected. In general, such damaged structures are repaired and reused. In this regard, an experimental investigation was planned and conducted on models of single-bay, single-storey of partial concrete infilled reinforced concrete (RC) frames up to collapse with corner, central and diagonal steel bracings. Such collapsed frames were repaired with epoxy resin and retested. The initiative was to identify the behaviour, extent of restored ultimate strength and deflection of epoxy-retrofitted frames in comparison to the braced RC frames. The performance of such frames has been considered only for lateral loads. In comparison to bare RC frames, epoxy repaired partial infilled frames have significant increase in the lateral load capacity. Central bracing is more effective than corner and diagonal bracing. For the same load, epoxy repaired frames have comparable deflection than similar braced frames.

Diversity, Situated Social Contexts, and College Enrollment: Multilevel Modeling to Examine Student, High School, and State Influences

ERIC Educational Resources Information Center

Kim, Dongbin; Nuñez, Anne-Marie

2013-01-01

Whether and where students begin college after high school profoundly affects their degree completion and ultimate educational attainment. Students' college access is influenced not only by individual characteristics, but also by economic, social, and schooling contexts. Accordingly, using data from the Educational Longitudinal Study, 2002…

Centaur Standard Shroud (CSS) static ultimate load structural tests

NASA Technical Reports Server (NTRS)

1975-01-01

A series of tests were conducted on the jettisonable metallic shroud used on the Titan/Centaur launch vehicle to verify its structural capabilities and to evaluate its structural interaction with the Centaur stage. A flight configured shroud and the interfacing Titan/Centaur structural assemblies were subjected to tests consisting of combinations of applied axial and shear loads to design ultimate values, including a set of tests on thermal conditions and two dynamic response tests to verify the analytical stiffness model. The strength capabilities were demonstrated at ultimate (125 percent of design limit) loads. It was also verified that the spring rate of the flight configured shroud-to-Centaur forward structural deflections of the specimen became nonlinear, as expected, above limit load values. This test series qualification program verified that the Titan/Centaur shroud and the Centaur and Titan interface components are qualified structurally at design ultimate loads.

High strength nickel-chromium-iron austenitic alloy

DOEpatents

Gibson, Robert C.; Korenko, Michael K.

1980-01-01

A solid solution strengthened Ni-Cr-Fe alloy capable of retaining its strength at high temperatures and consisting essentially of 42 to 48% nickel, 11 to 13% chromium, 2.6 to 3.4% niobium, 0.2 to 1.2% silicon, 0.5 to 1.5% vanadium, 2.6 to 3.4% molybdenum, 0.1 to 0.3% aluminum, 0.1 to 0.3% titanium, 0.02 to 0.05% carbon, 0.002 to 0.015% boron, up to 0.06 zirconium, and the balance iron. After solution annealing at 1038.degree. C. for one hour, the alloy, when heated to a temperature of 650.degree. C., has a 2% yield strength of 307 MPa, an ultimate tensile strength of 513 MPa and a rupture strength of as high as 400 MPa after 100 hours.

Longitudinal analysis of the strengths and difficulties questionnaire scores of the Millennium Cohort Study children in England using M-quantile random-effects regression.

PubMed

Tzavidis, Nikos; Salvati, Nicola; Schmid, Timo; Flouri, Eirini; Midouhas, Emily

2016-02-01

Multilevel modelling is a popular approach for longitudinal data analysis. Statistical models conventionally target a parameter at the centre of a distribution. However, when the distribution of the data is asymmetric, modelling other location parameters, e.g. percentiles, may be more informative. We present a new approach, M -quantile random-effects regression, for modelling multilevel data. The proposed method is used for modelling location parameters of the distribution of the strengths and difficulties questionnaire scores of children in England who participate in the Millennium Cohort Study. Quantile mixed models are also considered. The analyses offer insights to child psychologists about the differential effects of risk factors on children's outcomes.

CVD silicon carbide monofilament reinforced SrO-Al2O3-2SiO2 (SAS) glass-ceramic composites

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.

1995-01-01

Unidirectional CVD SiC fiber-reinforced SrO.Al2O3.2SiO2 (SAS) glass-ceramic matrix composites have been fabricated by hot pressing at various combinations of temperature, pressure and time. Both carbon-rich surface coated SCS-6 and uncoated SCS-0 fibers were used as reinforcements. Almost fully dense composites have been obtained. Monoclinic celsian, SrAl2Si2O8, was the only crystalline phase observed in the matrix from x-ray diffraction. During three point flexure testing of composites, a test span to thickness ratio of approximately 25 or greater was necessary to avoid sample delamination. Strong and tough SCS-6/SAS composites having a first matrix crack stress of approximately 300 MPa and an ultimate bend strength of approximately 825 MPa were fabricated. No chemical reaction between the SCS-6 fibers and the SAS matrix was observed after high temperature processing. The uncoated SCS-0 fiber-reinforced SAS composites showed only limited improvement in strength over SAS monolithic. The SCS-0/SAS composite having a fiber volume fraction of 0.24 and hot pressed at 1400 deg C exhibited a first matrix cracking stress of approximately 231 +/- 20 MPa and ultimate strength of 265 +/- 17 MPa. From fiber push-out tests, the fiber/matrix interfacial debonding strength (tau(sub debond)) and frictional sliding stress (tau(sub friction)) in the SCS-6/SAS system were evaluated to be approximately 6.7 +/- 2.3 MPa and 4.3 +/- 0.6 MPa, respectively, indicating a weak interface. However, for the SCS-0/SAS composite, much higher values of approximately 17.5 +/- 2.7 MPa for tau(sub debond) and 11.3 +/- 1.6 MPa for tau(sub friction) respectively, were observed; some of the fibers were so strongly bonded to the matrix that they could not be pushed out. Examination of fracture surfaces revealed limited short pull-out length of SCS-0 fibers. The applicability of various micromechanical models for predicting the values of first matrix cracking stress and ultimate strength of these composites were examined.

In-Plane Cracking Behavior and Ultimate Strength for 2D Woven and Braided Melt-Infiltrated SiC/SiC Composites Tensile Loaded in Off-Axis Fiber Directions

NASA Technical Reports Server (NTRS)

Morscher, Gregory N.; Yun, Hee Mann; DiCarlo, James A.

2007-01-01

The tensile mechanical properties of ceramic matrix composites (CMC) in directions off the primary axes of the reinforcing fibers are important for architectural design of CMC components that are subjected to multi-axial stress states. In this study, 2D-woven melt-infiltrated (MI) SiC/SiC composite panels with balanced fiber content in the 0 degree and 90 degree directions were tensile loaded in-plane in the 0 degree direction and at 45 degree to this direction. In addition, a 2D triaxially-braided MI composite panel with balanced fiber content in the plus or minus 67 degree bias directions and reduced fiber content in the axial direction was tensile loaded perpendicular to the axial direction tows (i.e., 23 degrees from the bias fibers). Stress-strain behavior, acoustic emission, and optical microscopy were used to quantify stress-dependent matrix cracking and ultimate strength in the panels. It was observed that both off-axis loaded panels displayed higher composite onset stresses for through-thickness matrix cracking than the 2D-woven 0/90 panels loaded in the primary 0 degree direction. These improvements for off-axis cracking strength can in part be attributed to higher effective fiber fractions in the loading direction, which in turn reduces internal stresses on critical matrix flaws for a given composite stress. Also for the 0/90 panel loaded in the 45 degree direction, an improved distribution of matrix flaws existed due to the absence of fiber tows perpendicular to the loading direction. In addition, for the +67/0/-67 braided panel, the axial tows perpendicular to the loading direction were not only low in volume fraction, but were also were well separated from one another. Both off-axis oriented panels also showed relatively good ultimate tensile strength when compared to other off-axis oriented composites in the literature, both on an absolute strength basis as well as when normalized by the average fiber strength within the composites. Initial implications are discussed for constituent and architecture design to improve the directional cracking of SiC/SiC CMC components with MI matrices.

Test and Analysis of a Hyper-X Carbon-Carbon Leading Edge Chine

NASA Technical Reports Server (NTRS)

Smith, Russell W.; Sikora, Joseph G.; Lindell, Michael C.

2005-01-01

During parts production for the X43A Mach 10 hypersonic vehicle nondestructive evaluation (NDE) of a leading edge chine detected on imbedded delamination near the lower surface of the part. An ultimate proof test was conducted to verify the ultimate strength of this leading edge chine part. The ultimate proof test setup used a pressure bladder design to impose a uniform distributed pressure field over the bi-planar surface of the chine test article. A detailed description of the chine test article and experimental test setup is presented. Analysis results from a linear status model of the test article are also presented and discussed. Post-test inspection of the specimen revealed no visible failures or areas of delamination.

Study of a trussed girder composed of a reinforced plastic.

DOT National Transportation Integrated Search

1974-01-01

The structural behavior of a series of laboratory test specimens was investigated to determine the ultimate strength, the deformation characteristics, and the mode of failure of a trussed girder composed of glass fiber reinforced polyester resin. Com...

Optimized design and structural mechanics of a single-piece composite helicopter driveshaft

NASA Astrophysics Data System (ADS)

Henry, Todd C.

In rotorcraft driveline design, single-piece composite driveshafts have much potential for reducing driveline mass and complexity over multi-segmented metallic driveshafts. The singlepiece shaft concept is enabled by the relatively high fatigue strain capacity of fiber reinforced polymer composites over metals. Challenges for single-piece driveshaft design lie in addressing the self-heating behavior of the composite due to the material damping, as well as, whirling stability, torsional buckling stability, and composite strength. Increased composite temperature due to self-heating reduces the composite strength and is accounted for in this research. The laminate longitudinal stiffness ( Ex) and strength (Fx) are known to be heavily degraded by fiber undulation, however, both are not well understood in compression. The whirling stability (a function of longitudinal stiffness) and the composite strength are strongly influential in driveshaft optimization, and thus are investigated further through the testing of flat and filament wound composite specimens. The design of single-piece composite driveshafts, however, needs to consider many failure criteria, including hysteresis-induced overheating, whirl stability, torsional buckling stability, and material failure by overstress. The present investigation uses multi-objective optimization to investigate the design space which visually highlights design trades. Design variables included stacking sequence, number of laminas, and number of hanger bearings. The design goals were to minimize weight and maximize the lowest factor of safety by adaptively generating solutions to the multi-objective problem. Several design spaces were investigated by examining the effect of misalignment, ambient temperature, and constant power transmission on the optimized solution. Several materials of interest were modeled using experimentally determined elastic properties and novel temperature-dependent composite strength. Compared to the baseline multi-segmented metallic driveline, weight reductions of 43% and 48% were obtained for single-piece flexible and rigid matrix composite shafts. The rigid matrix weight reduction was slightly lower than that seen in the literature due to consideration of shaft misalignment. In filament wound composites, the existence of fiber undulation introduces unique challenges in the prediction of compressive modulus and strength using traditional laminated composite theories. In the current investigation, novel full field strain measurements of compressively loaded specimens were used to evaluate local strain distributions in the region of a 0-deg. undulated lamina in a [0n/90n] s laminate (n=2,4,6) and a 30-deg. undulated lamina in a [30n/-60n] s laminate (n=2,4). Unique to this research, specimens were fabricated with carbon fibers, various amplitudes of undulation, and matrix materials with three different moduli of elasticity. Full-field strains were measured on the free edge and across the width of the compressively loaded specimens using two-dimensional digital image correlation (DIC). The observed strains were highly influenced by the undulation geometry. The longitudinal modulus of a [0n/90n] s laminate was more sensitive to reinforcement undulation when the matrix was flexible rather than rigid. An undulation with an amplitude/length ratio of 0.1 (low for a filament wound cylinder) reduces the average longitudinal modulus of elasticity in the undulation region by approximately 43% and 3% in laminates with flexible and rigid matrices, respectively, relative to a similar material without undulation. Observations of strain on the free edge revealed that fiber undulation caused elevated out-of-plane shear (gamma xz) and through-thickness normal (epsilonzz) strains in regions eventually involved in the fiber microbuckling failure process. A new three dimensional method was derived for the homogenization of a heterogeneous composite laminate consisting of individual anisotropic lamina for which structural coupling (Bij) may occur due to in- and out-of-plane (undulation) fiber reinforcement orientation. Threedimensional elastic constants were calculated by considering a representative volume element taken from the heterogeneous laminate. Three-dimensional elastic constant predictions were validated through comparison with established methods, both two- and three- dimensional. When the new derived three dimensional theory was applied to experimental results, the modulus and strength predictions compared favorably. A series of [+/-theta/89/+/-theta] cylinders with multiple helical fiber angles, winding patterns, and matrix materials were fabricated and tested in compression. Digital image correlation was used for the first time to measure outside surface displacements and strains. Longitudinal and hoop direction strain fluctuations between the undulated and non-undulated regions were found to be of the order of 20-30% of the mean values throughout the cylinders. Qualitatively, these fluctuations can be related to non-classical elastic couplings (Bij) in the anti-symmetric regions of the filament winding pattern. Failure of the cylinder occurred by fiber microbuckling, which initiated near the crossing of circumferential and helical cross-over bands. Based on a statistical analysis of surface strains in the local fiber coordinate system, it was determined that longitudinal compressive and in-plane longitudinal shear strains at incipient microbuckling were two to four times greater than their respective global counterparts. These results indicate the magnitude of strain concentration existing in the cylinders immediately before final failure (possibly during local failure) and highlight the importance of longitudinal compressive (epsilon11) and in-plane longitudinal shear strains (gamma12) in the failure process. A novel local-global approach was used in predicting the longitudinal modulus and strength of filament wound cylinders. Several representative volume elements were chosen to represent the filament winding rhombus, and were used as a basis for homogenization. Strength predictions were augmented with empirical critical distance factors. The average Ex and nu xy prediction error for Conathane DPRN 30917 was 6.8 % and 21 % and the average error for EPON 862 was 9.7 % and 14 % respectively. The strength prediction error was approximately 7.7 % and 24 % for 30917 and EPON 862 with failure location typically at the circumferential undulation by mode sigma 6 (tau12). The failure mode prediction was consistent with experimental observations from filament wound cylinders and flat-undulated specimens of similar lamination arrangement. Additional comparison with previous Adiprene LF750 filament wound cylinder testing produced prediction error of 11.8 % and 8.9 % for longitudinal modulus and strength respectively. The average absolute value of the error, considering every material, for modulus, strength, and Poisson's ratio was 14 %. Application of critical distance factors to flat undulated specimens was deemed unadvisable due to considerably higher strain intensity at failure compared to filament wound cylinders.

Predicting the tensile strength of A UD basalt/ epoxy composite used for the confinement of concrete structures

NASA Astrophysics Data System (ADS)

Ciniņa, I.; Zīle, O.; Andersons, J.

2013-01-01

The principal aim of the present research was to predict the strength of UD basalt fiber/epoxy matrix composites in tension along the reinforcement direction. Tension tests on single basalt fibers were performed to determine the functional form of their strength distribution and to evaluate the parameters of the distribution. Also, microbond tests were carried out to assess the interfacial shear strength of the fibers and polymer matrix. UD composite specimens were produced and tested for the longitudinal tensile strength. The predicted strength of the composite was found to exceed the experimental values by ca. 20%, which can be explained by imperfections in the fiber alignment, impregnation, and adhesion in the composite specimens.

Biomechanical fatigue analysis of an advanced new carbon fiber/flax/epoxy plate for bone fracture repair using conventional fatigue tests and thermography.

PubMed

Bagheri, Zahra S; El Sawi, Ihab; Bougherara, Habiba; Zdero, Radovan

2014-07-01

The current study is part of an ongoing research program to develop an advanced new carbon fiber/flax/epoxy (CF/flax/epoxy) hybrid composite with a “sandwich structure” as a substitute for metallic materials for orthopedic long bone fracture plate applications. The purpose of this study was to assess the fatigue properties of this composite, since cyclic loading is one of the main types of loads carried by a femur fracture plate during normal daily activities. Conventional fatigue testing, thermographic analysis, and scanning electron microscopy (SEM) were used to analyze the damage progress that occurred during fatigue loading. Fatigue strength obtained using thermography analysis (51% of ultimate tensile strength) was confirmed using the conventional fatigue test (50–55% of ultimate tensile strength). The dynamic modulus (E⁎) was found to stay almost constant at 47 GPa versus the number of cycles, which can be related to the contribution of both flax/epoxy and CF/epoxy laminae to the stiffness of the composite. SEM images showed solid bonding at the CF/epoxy and flax/epoxy laminae, with a crack density of only 0.48% for the plate loaded for 2 million cycles. The current composite plate showed much higher fatigue strength than the main loads experienced by a typical patient during cyclic activities; thus, it may be a potential candidate for bone fracture plate applications. Moreover, the fatigue strength from thermographic analysis was the same as that obtained by the conventional fatigue tests, thus demonstrating its potential use as an alternate tool to rapidly evaluate fatigue strength of composite biomaterials.

Biomechanical fatigue analysis of an advanced new carbon fiber/flax/epoxy plate for bone fracture repair using conventional fatigue tests and thermography.

PubMed

Bagheri, Zahra S; El Sawi, Ihab; Bougherara, Habiba; Zdero, Radovan

2014-07-01

The current study is part of an ongoing research program to develop an advanced new carbon fiber/flax/epoxy (CF/flax/epoxy) hybrid composite with a "sandwich structure" as a substitute for metallic materials for orthopedic long bone fracture plate applications. The purpose of this study was to assess the fatigue properties of this composite, since cyclic loading is one of the main types of loads carried by a femur fracture plate during normal daily activities. Conventional fatigue testing, thermographic analysis, and scanning electron microscopy (SEM) were used to analyze the damage progress that occurred during fatigue loading. Fatigue strength obtained using thermography analysis (51% of ultimate tensile strength) was confirmed using the conventional fatigue test (50-55% of ultimate tensile strength). The dynamic modulus (E(⁎)) was found to stay almost constant at 47GPa versus the number of cycles, which can be related to the contribution of both flax/epoxy and CF/epoxy laminae to the stiffness of the composite. SEM images showed solid bonding at the CF/epoxy and flax/epoxy laminae, with a crack density of only 0.48% for the plate loaded for 2 million cycles. The current composite plate showed much higher fatigue strength than the main loads experienced by a typical patient during cyclic activities; thus, it may be a potential candidate for bone fracture plate applications. Moreover, the fatigue strength from thermographic analysis was the same as that obtained by the conventional fatigue tests, thus demonstrating its potential use as an alternate tool to rapidly evaluate fatigue strength of composite biomaterials. Copyright © 2014 Elsevier Ltd. All rights reserved.

Study of high performance alloy electroforming

NASA Technical Reports Server (NTRS)

Malone, G. A.

1985-01-01

More panels electroformed with intentional variations of pulse plating parameters are being made. Pulse plating frequency was noted to have a significant effect regarding mechanical properties. The use of a high pulse frequency (assuming fixed duty cycles) results in an increase in ductility and a decrease in ultimate and yield strengths. Electroforming to intermediate frequencies is being done to obtain the best possible combination of ductility and strength. Results of some tests from high frequency specimens are tabulated.

Engineering and design properties of thallium-doped sodium iodide and selected properties of sodium-doped cesium iodide

NASA Technical Reports Server (NTRS)

Forrest, K.; Haehner, C.; Heslin, T.; Magida, M.; Uber, J.; Freiman, S.; Hicho, G.; Polvani, R.

1984-01-01

Mechanical and thermal properties, not available in the literature but necessary to structural design, using thallium doped sodium iodide and sodium doped cesium iodide were determined to be coefficient of linear thermal expansion, thermal conductivity, thermal shock resistance, heat capacity, elastic constants, ultimate strengths, creep, hardness, susceptibility to subcritical crack growth, and ingot variation of strength. These properties were measured for single and polycrystalline materials at room temperature.

Strength and Microstructure of Ceramics.

DTIC Science & Technology

1987-11-01

triangular slab. 12-mm edge length and 2-mm thickness. to produce crack 7 mm long. Starter notch length portantly. the strength plateau at small flaw sizes...however. a tapered the starter notch tip. "Pop-in" behavior of this kind is not uncom- geometry was used. width increasing in the direction of ultimate...mon in notched specimens, of course: in such cases the initial crack propagation. The main crack was started at a sawcut notch fracture response can be

Evaluation of five CAD/CAM materials by microstructural characterization and mechanical tests: a comparative in vitro study.

PubMed

Sonmez, Nesrin; Gultekin, Pinar; Turp, Volkan; Akgungor, Gokhan; Sen, Deniz; Mijiritsky, Eitan

2018-01-08

Polymer infiltrated ceramics and nano-ceramic resins are the new restorative materials which have been developed in order to enhance the adverse properties of glass-matrix ceramics and resin composites. The aim of the present in vitro study was to evaluate the characteristics of various CAD/CAM materials through mechanical, microstructural, and SEM analysis. Five test groups (n = 22) were formed by using the indicated CAD/CAM blocks: VITA Enamic (VITA Zahnfabrik), Lava Ultimate (3 M ESPE), IPS e.max CAD (Ivoclar Vivadent), IPS Empress CAD (Ivoclar Vivadent), and VITA Mark II (VITA Zahnfabrik). Two specimens from each test group were used for XRD and EDS analysis. Remaining samples were divided into two subgroups (n = 10). One subgroup specimens were thermocycled (5 °C to 55 °C, 30s, 10,000 cycles) whereas the other were not. All of the specimens were evaluated in terms of flexural strength, Vickers hardness, and fracture toughness. Results were statistically analyzed using two-way ANOVA, one-way ANOVA, Tukey's HSD, and Student's t tests (α = .05). Fractured specimens were evaluated using SEM. The highest Vickers microhardness value was found for VITA Mark II (p < .001), however flexural strength and fracture toughness results were lowest conversely (p < .05). IPS e.max CAD was found to have the highest flexural strength (p < .001). Fracture toughness of IPS e.max CAD was also higher than other tested block materials (p < .001). Lava Ultimate and VITA Enamic's mechanical properties were affected negatively from thermocycling (p < .05). Microhardness, flexural strength, and fracture toughness values of Lava Ultimate and VITA Enamic were found to be similar to VITA Mark II and IPS Empress CAD groups. It should be realised that simulated aging process seem to affect ceramic-polymer composite materials more significantly than glass ceramics.

Tensile Behavior of As-Fabricated and Burner-Rig Exposed SiC/SiC Composites with Hi-Nicalon Type-S Fibers

NASA Technical Reports Server (NTRS)

Yun, H. M.; Dicarlo, J. A.; Ogbuji, L. T.; Chen, Y. L.

2002-01-01

Tensile stress-strain curves were measured at room temperature and 1315 C for 2D-woven SiC/BN/SiC ceramic matrix composites (CMC) reinforced by two variations of Hi-Nicalon Type-S SiC fibers. These fibers, which contained a thin continuous carbon-rich layer on their as-produced surface, provided the as-fabricated CMC with good composite behavior and an ultimate strength and strain of -350 MPa and -0.5%, respectively. However, after un-stressed burner-rig exposure at 815 C for -100 hrs, CMC tensile specimens with cut edges and exposed interphases showed a significant decrease in ultimate properties with effectively no composite behavior. Microstructural observations show that the degradation was caused by internal fiber-fiber oxide bonding after removal of the carbon-rich fiber surface layer by the high-velocity combustion gases. On the other hand, SiC/BN/SiC CMC with Sylramic-iBN fibers without carbon-rich surfaces showed higher as-fabricated strength and no loss in strength after the same burner rig exposure. Based on the strong role of the carbon layer in these observations, a process method was developed and demonstrated for achieving better strength retention of Hi-Nicalon Type-S CMC during burner rig exposure. Other general approaches for minimizing this current deficiency with as-produced Type-S fibers are discussed.

Tracking Emotional and Behavioral Changes in Childhood: Does the Strength and Difficulties Questionnaire Measure the Same Constructs across Time?

ERIC Educational Resources Information Center

Sosu, Edward M.; Schmidt, Peter

2017-01-01

R. Goodman's Strength and Difficulties Questionnaire (SDQ) is widely used to measure emotional and behavioral difficulties in childhood and adolescence. In the present study, we examined whether the SDQ measures the same construct across time, when used for longitudinal research. A nationally representative sample of parents (N = 3,375) provided…

Processing and properties of fiber reinforced polymeric matrix composites: I. IM7/LARC(TM)-PETI-7 polyimide composites

NASA Technical Reports Server (NTRS)

Hou, Tan-Hung

1995-01-01

A phenylethynyl terminated imide oligomer formed from the reaction of benzophenone tetracarboxylic acid dianhydride, an 75:25 molar ratio of 4,4'-oxydianiline and meta-phenylenediamine and 4-phenylethynylphthalic anhydride as the endcapper at a theoretical number average molecular weight (Mn) of approximately 3,700 g/mol was evaluated as a composite resin matrix. A glass transition temperature (Tg) of 315 deg C was reached after 250 deg C/1 hr annealing of the matrix resin. Unidirectional prepreg was made by coating an N-methylpyrrolidinone solution of the amide acid oligomer onto unsized IM7 graphite fibers. The thermal and rheological properties and the solvent/volatile depletion rates of the amide acid/NMP system were determined. This information was used to successfully design a molding cycle for composite fabrication. Composites molded under 800 Psi at 371 C consistently yielded good consolidation as measured by C-scan and optical photomicrography. The composite's short beam shear strength (SBS), longitudinal and transverse flexural strengths and moduli were measured at various temperatures. These composites exhibited excellent room temperature (RT) longitudinal flexural strength and modulus and RT SBS strength retention at 177 C.

Double row equivalent for rotator cuff repair: A biomechanical analysis of a new technique.

PubMed

Robinson, Sean; Krigbaum, Henry; Kramer, Jon; Purviance, Connor; Parrish, Robin; Donahue, Joseph

2018-06-01

There are numerous configurations of double row fixation for rotator cuff tears however, there remains to be a consensus on the best method. In this study, we evaluated three different double-row configurations, including a new method. Our primary question is whether the new anchor and technique compares in biomechanical strength to standard double row techniques. Eighteen prepared fresh frozen bovine infraspinatus tendons were randomized to one of three groups including the New Double Row Equivalent, Arthrex Speedbridge and a transosseous equivalent using standard Stabilynx anchors. Biomechanical testing was performed on humeri sawbones and ultimate load, strain, yield strength, contact area, contact pressure, and a survival plots were evaluated. The new double row equivalent method demonstrated increased survival as well as ultimate strength at 415N compared to the remainder testing groups as well as equivalent contact area and pressure to standard double row techniques. This new anchor system and technique demonstrated higher survival rates and loads to failure than standard double row techniques. This data provides us with a new method of rotator cuff fixation which should be further evaluated in the clinical setting. Basic science biomechanical study.

Effect of thermomechanical treatment on the microstructure, phase composition, and mechanical properties of Al-Cu-Mn-Mg-Zr alloy

NASA Astrophysics Data System (ADS)

Zuiko, I. S.; Gazizov, M. R.; Kaibyshev, R. O.

2016-09-01

The effect of the thermomechanical treatment on the microstructure, phase composition, and mechanical properties of heat-treatable AA2519 aluminum alloy (according to the classification of the Aluminum Association) has been considered. After solid-solution treatment, quenching, and artificial aging (T6 treatment) at 180°C for the peak strength, the yield stress, ultimate tensile strength, and elongation to failure are ~300 MPa, 435 MPa, and 21.7%, respectively. It has been shown that treatments that include intermediate plastic deformations with degrees of 7 and 15% (T87 and T815 treatments, respectively) have a significant effect on the phase composition and morphology of strengthening particles precipitated during peak aging T8X type, where X is pre-strain percent, treatments initiate the precipitation of significant amounts of particles of the θ'- and Ω-phases. After T6 treatment, predominantly homogeneously distributed particles of θ″-phase have been observed. Changes in the microstructure and phase composition of the AA2519 alloy, which are caused by intermediate deformation, lead to a significant increase in the yield stress and ultimate tensile strength (by ~40 and ~8%, respectively), whereas the plasticity decreases by 40-50%.

Microstructure and Tensile/Corrosion Properties Relationships of Directionally Solidified Al-Cu-Ni Alloys

NASA Astrophysics Data System (ADS)

Rodrigues, Adilson V.; Lima, Thiago S.; Vida, Talita A.; Brito, Crystopher; Garcia, Amauri; Cheung, Noé

2018-03-01

Al-Cu-Ni alloys are of scientific and technological interest due to high strength/high temperature applications, based on the reinforcement originated from the interaction between the Al-rich phase and intermetallic composites. The nature, morphology, size, volume fraction and dispersion of IMCs particles throughout the Al-rich matrix are important factors determining the resulting mechanical and chemical properties. The present work aims to evaluate the effect of the addition of 1wt%Ni into Al-5wt%Cu and Al-15wt%Cu alloys on the solidification rate, macrosegregation, microstructure features and the interrelations of such characteristics on tensile and corrosion properties. A directional solidification technique is used permitting a wide range of microstructural scales to be examined. Experimental growth laws relating the primary and secondary dendritic spacings to growth rate and solidification cooling rate are proposed, and Hall-Petch type equations are derived relating the ultimate tensile strength and elongation to the primary dendritic spacing. Considering a compromise between ultimate tensile strength and corrosion resistance of the examined alloys samples from both alloys castings it is shown that the samples having more refined microstructures are associated with the highest values of such properties.

Chemical Vapor Deposited SiC (SCS-0) Fiber-Reinforced Strontium Aluminosilicate Glass-Ceramic Composites

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.

1997-01-01

Unidirectional SrO Al2O3 2SiO2 glass-ceramic matrix composites reinforced with uncoated Chemical Vapor Deposited (CVD) SiC (SCS-0) fibers have been fabricated by hot-pressing under appropriate conditions using the glass-ceramic approach. Almost fully dense composites having a fiber volume fraction of 0.24 have been obtained. Monoclinic celsian, SrAl2Si2O8, was the only crystalline phase observed in the matrix by x-ray diffraction. No chemical reaction was observed between the fiber and the matrix after high temperature processing. In three-point flexure, the composite exhibited a first matrix cracking stress of approx. 231 +/- 20 MPa and an ultimate strength of 265 +/- 17 MPa. Examination of fracture surfaces revealed limited short length fiber pull-out. From fiber push-out, the fiber/matrix interfacial debonding and frictional strengths were evaluated to be approx. 17.5 +/- 2.7 MPa and 11.3 +/- 1.6 MPa, respectively. Some fibers were strongly bonded to the matrix and could not be pushed out. The micromechanical models were not useful in predicting values of the first matrix cracking stress as well as the ultimate strength of the composites.

Experimental Tests on the Composite Foam Sandwich Pipes Subjected to Axial Load

NASA Astrophysics Data System (ADS)

Li, Feng; Zhao, QiLin; Xu, Kang; Zhang, DongDong

2015-12-01

Compared to the composite thin-walled tube, the composite foam sandwich pipe has better local flexural rigidity, which can take full advantage of the high strength of composite materials. In this paper, a series of composite foam sandwich pipes with different parameters were designed and manufactured using the prefabricated polyurethane foam core-skin co-curing molding technique with E-glass fabric prepreg. The corresponding axial-load compressive tests were conducted to investigate the influence factors that experimentally determine the axial compressive performances of the tubes. In the tests, the detailed failure process and the corresponding load-displacement characteristics were obtained; the influence rules of the foam core density, surface layer thickness, fiber ply combination and end restraint on the failure modes and ultimate bearing capacity were studied. Results indicated that: (1) the fiber ply combination, surface layer thickness and end restraint have a great influence on the ultimate load bearing capacity; (2) a reasonable fiber ply combination and reliable interfacial adhesion not only optimize the strength but also transform the failure mode from brittle failure to ductile failure, which is vital to the fully utilization of the composite strength of these composite foam sandwich pipes.

Prediction of Composite Laminate Strength Properties Using a Refined Zigzag Plate Element

NASA Technical Reports Server (NTRS)

Barut, Atila; Madenci, Erdogan; Tessler, Alexander

2013-01-01

This study presents an approach that uses the refined zigzag element, RZE(exp2,2) in conjunction with progressive failure criteria to predict the ultimate strength of composite laminates based on only ply-level strength properties. The methodology involves four major steps: (1) Determination of accurate stress and strain fields under complex loading conditions using RZE(exp2,2)-based finite element analysis, (2) Determination of failure locations and failure modes using the commonly accepted Hashin's failure criteria, (3) Recursive degradation of the material stiffness, and (4) Non-linear incremental finite element analysis to obtain stress redistribution until global failure. The validity of this approach is established by considering the published test data and predictions for (1) strength of laminates under various off-axis loading, (2) strength of laminates with a hole under compression, and (3) strength of laminates with a hole under tension.

Study on Predicting Axial Load Capacity of CFST Columns

NASA Astrophysics Data System (ADS)

Ravi Kumar, H.; Muthu, K. U.; Kumar, N. S.

2017-11-01

This work presents an analytical study and experimental study on the behaviour and ultimate load carrying capacity of axially compressed self-compacting concrete-filled steel tubular columns. Results of tests conducted by various researchers on 213 samples concrete-filled steel tubular columns are reported and present authors experimental data are reported. Two theoretical equations were derived for the prediction of the ultimate axial load strength of concrete-filled steel tubular columns. The results from prediction were compared with the experimental data. Validation to the experimental results was made.

Large-deflection-theory Analysis of the Effect of Web Initial Curvature on the Ultimate Strength of Steel Plate Girder

NASA Astrophysics Data System (ADS)

Kala, Jiří; Kala, Zdeněk

2011-09-01

The objective of the paper is to analyze the influence of initial imperfections on the behaviour of thin-walled girders welded of slender plate elements. In parallel with experiments, one of the ultimate load tests was computer modelled. In so doing, the girder was modelled, using the geometrically and materially non-linear variant of the shell finite element method, by the ANSYS program. The shape changing during loading process is often accompanying with sudden "snap-through" i. e. rapid curvature change.

Some physical and mechanical properties of recycled polyurethane foam blends

NASA Astrophysics Data System (ADS)

Bledzki, A. K.; Zicans, J.; Merijs Meri, R.; Kardasz, D.

2008-09-01

Blends of secondary rigid polyurethane foams (RPUFs) with soft polyurethane foams (SPUFs) were investigated. The effect of SPUF content and its chemical nature on some physical and mechanical properties of the blends was evaluated. Owing to the stronger intermolecular interaction and higher values of cohesion energy, the blends of RPUFs with polyester SPUFs showed higher mechanical properties than those with polyether SPUFs. The density, hardness, ultimate strength, and the tensile, shear, and flexural moduli increased, while the impact toughness, ultimate elongation, and damping characteristics decreased with increasing RPUF content in the blends.

Tensile strength/yield strength (TS/YS) ratios of high-strength steel (HSS) reinforcing bars

NASA Astrophysics Data System (ADS)

Tavio, Anggraini, Retno; Raka, I. Gede Putu; Agustiar

2018-05-01

The building codes such as American Concrete Institute (ACI) 318M-14 and Standard National Indonesia (SNI) 2847:2013 require that the ratio of tensile strength (TS) and yield strength (YS) should not less than 1.25. The requirement is based on the assumption that a capability of a structural member to develop inelastic rotation capacity is a function of the length of the yield region. This paper reports an investigation on various steel grades, namely Grades 420, 550, 650, and 700 MPa, to examine the impact of different TS/YS ratios if it is less or greater than the required value. Grades 550, 650, and 700 MPa were purposely selected with the intention to examine if these higher grades are still promising to be implemented in special structural systems since they are prohibited by the building codes for longitudinal reinforcement, whereas Grade 420 MPa bars are the maximum limit of yield strength of reinforcing bars that is allowable for longitudinal reinforcement of special structural systems. Tensile tests of these steel samples were conducted under displacement controlled mode to capture the complete stress-strain curves and particularly the post-yield response of the steel bars. From the study, it can be concluded that Grade 420 performed higher TS/YS ratios and they were able to reach up to more than 1.25. However, the High Strength Still (HSS) bars (Grades 550, 600, and 700 MPa) resulted in lower TS/YS ratios (less than 1.25) compared with those of Grade 420 MPa.

Determination of Material Strengths by Hydraulic Bulge Test.

PubMed

Wang, Hankui; Xu, Tong; Shou, Binan

2016-12-30

The hydraulic bulge test (HBT) method is proposed to determine material tensile strengths. The basic idea of HBT is similar to the small punch test (SPT), but inspired by the manufacturing process of rupture discs-high-pressure hydraulic oil is used instead of punch to cause specimen deformation. Compared with SPT method, the HBT method can avoid some of influence factors, such as punch dimension, punch material, and the friction between punch and specimen. A calculation procedure that is entirely based on theoretical derivation is proposed for estimate yield strength and ultimate tensile strength. Both conventional tensile tests and hydraulic bulge tests were carried out for several ferrous alloys, and the results showed that hydraulic bulge test results are reliable and accurate.

Parametric Study of Shear Strength of Concrete Beams Reinforced with FRP Bars

NASA Astrophysics Data System (ADS)

Thomas, Job; Ramadass, S.

2016-09-01

Fibre Reinforced Polymer (FRP) bars are being widely used as internal reinforcement in structural elements in the last decade. The corrosion resistance of FRP bars qualifies its use in severe and marine exposure conditions in structures. A total of eight concrete beams longitudinally reinforced with FRP bars were cast and tested over shear span to depth ratio of 0.5 and 1.75. The shear strength test data of 188 beams published in various literatures were also used. The model originally proposed by Indian Standard Code of practice for the prediction of shear strength of concrete beams reinforced with steel bars IS:456 (Plain and reinforced concrete, code of practice, fourth revision. Bureau of Indian Standards, New Delhi, 2000) is considered and a modification to account for the influence of the FRP bars is proposed based on regression analysis. Out of the 196 test data, 110 test data is used for the regression analysis and 86 test data is used for the validation of the model. In addition, the shear strength of 86 test data accounted for the validation is assessed using eleven models proposed by various researchers. The proposed model accounts for compressive strength of concrete ( f ck ), modulus of elasticity of FRP rebar ( E f ), longitudinal reinforcement ratio ( ρ f ), shear span to depth ratio ( a/ d) and size effect of beams. The predicted shear strength of beams using the proposed model and 11 models proposed by other researchers is compared with the corresponding experimental results. The mean of predicted shear strength to the experimental shear strength for the 86 beams accounted for the validation of the proposed model is found to be 0.93. The result of the statistical analysis indicates that the prediction based on the proposed model corroborates with the corresponding experimental data.

Handgrip strength and its prognostic value for mortality in Moscow, Denmark, and England

PubMed Central

Demakakos, Panayotes; Shkolnikova, Maria; Thinggaard, Mikael; Vaupel, James W.; Christensen, Kaare; Shkolnikov, Vladimir M.

2017-01-01

Background This study compares handgrip strength and its association with mortality across studies conducted in Moscow, Denmark, and England. Materials The data collected by the Study of Stress, Aging, and Health in Russia, the Study of Middle-Aged Danish Twins and the Longitudinal Study of Aging Danish Twins, and the English Longitudinal Study of Ageing was utilized. Results Among the male participants, the age-standardized grip strength was 2 kg and 1 kg lower in Russia than in Denmark and in England, respectively. The age-standardized grip strength among the female participants was 1.9 kg and 1.6 kg lower in Russia than in Denmark and in England, respectively. In Moscow, a one-kilogram increase in grip strength was associated with a 4% (hazard ratio [HR] = 0.96, 95% confidence interval [CI]: 0.94, 0.99) reduction in mortality among men and a 10% (HR = 0.90, 95%CI: 0.86, 0.94) among women. Meanwhile, a one-kilogram increase in grip strength was associated with a 6% (HR = 0.94, 95%CI: 0.93, 0.95) and an 8% (HR = 0.92, 95%CI: 0.90, 0.94) decrease in mortality among Danish men and women, respectively, and with a 2% (HR = 0.98, 95%CI: 0.97, 0.99) and a 3% (HR = 0.97, 95%CI: 0.95, 0.98) reduction in mortality among the English men and women, respectively. Conclusion The study suggests that, although absolute grip strength values appear to vary across the Muscovite, Danish, and English samples, the degree to which grip strength is predictive of mortality is comparable across national populations with diverse socioeconomic and health profiles and life expectancy levels. PMID:28863174

Emergence of the neural network underlying phonological processing from the prereading to the emergent reading stage: A longitudinal study.

PubMed

Yu, Xi; Raney, Talia; Perdue, Meaghan V; Zuk, Jennifer; Ozernov-Palchik, Ola; Becker, Bryce L C; Raschle, Nora M; Gaab, Nadine

2018-05-01

Numerous studies have shown that phonological skills are critical for successful reading acquisition. However, how the brain network supporting phonological processing evolves and how it supports the initial course of learning to read is largely unknown. Here, for the first time, we characterized the emergence of the phonological network in 28 children over three stages (prereading, beginning reading, and emergent reading) longitudinally. Across these three time points, decreases in neural activation in the left inferior parietal cortex (LIPC) were observed during an audiovisual phonological processing task, suggesting a specialization process in response to reading instruction/experience. Furthermore, using the LIPC as the seed, a functional network consisting of the left inferior frontal, left posterior occipitotemporal, and right angular gyri was identified. The connection strength in this network co-developed with the growth of phonological skills. Moreover, children with above-average gains in phonological processing showed a significant developmental increase in connection strength in this network longitudinally, while children with below-average gains in phonological processing exhibited the opposite trajectory. Finally, the connection strength between the LIPC and the left posterior occipitotemporal cortex at the prereading level significantly predicted reading performance at the emergent reading stage. Our findings highlight the importance of the early emerging phonological network for reading development, providing direct evidence for the Interactive Specialization Theory and neurodevelopmental models of reading. © 2018 Wiley Periodicals, Inc.

Middle Childhood Success and Economic Mobility. The Social Genome Project

ERIC Educational Resources Information Center

Aber, J. Lawrence; Grannis, Kerry Searle; Owen, Stephanie; Sawhill, Isabel V.

2013-01-01

This study uses data from the Early Childhood Longitudinal Study, Kindergarten Class of 1998-1999 (ECLS-K) to analyze competencies that children need to master by the end of elementary school, the extent to which they are doing so, what might be done to improve their performance, and how this might affect their ultimate ability to earn a living…

Longitudinal decline of lower extremity muscle power in healthy and mobility-limited older adults: influence of muscle mass, strength, composition, neuromuscular activation and single fiber contractile properties

USDA-ARS?s Scientific Manuscript database

This longitudinal study examined the major physiological mechanisms that determine the age related loss of lower extremity muscle power in two distinct groups of older humans. We hypothesized that after ~3 years of follow-up, mobility-limited older adults (mean age: 77.2 +/- 4, n = 22, 12 females) w...

Longitudinal in vivo muscle function analysis of the DMSXL mouse model of myotonic dystrophy type 1.

PubMed

Decostre, Valérie; Vignaud, Alban; Matot, Béatrice; Huguet, Aline; Ledoux, Isabelle; Bertil, Emilie; Gjata, Bernard; Carlier, Pierre G; Gourdon, Geneviève; Hogrel, Jean-Yves

2013-12-01

Myotonic dystrophy is the most common adult muscle dystrophy. In view of emerging therapies, which use animal models as a proof of principle, the development of reliable outcome measures for in vivo longitudinal study of mouse skeletal muscle function is becoming crucial. To satisfy this need, we have developed a device to measure ankle dorsi- and plantarflexion torque in rodents. We present an in vivo 8-month longitudinal study of the contractile properties of the skeletal muscles of the DMSXL mouse model of myotonic dystrophy type 1. Between 4 and 12 months of age, we observed a reduction in muscle strength in the ankle dorsi- and plantarflexors of DMSXL compared to control mice although the strength per muscle cross-section was normal. Mild steady myotonia but no abnormal muscle fatigue was also observed in the DMSXL mice. Magnetic resonance imaging and histological analysis performed at the end of the study showed respectively reduced muscle cross-section area and smaller muscle fibre diameter in DMSXL mice. In conclusion, our study demonstrates the feasibility of carrying out longitudinal in vivo studies of muscle function over several months in a mouse model of myotonic dystrophy confirming the feasibility of this method to test preclinical therapeutics. Copyright © 2013 Elsevier B.V. All rights reserved.

A narrow linewidth tunable single longitudinal mode Ga-EDF fiber laser

NASA Astrophysics Data System (ADS)

Mohamed Halip, N. H.; Abu Bakar, M. H.; Latif, A. A.; Muhd-Yasin, S. Z.; Zulkifli, M. I.; Mat-Sharif, K. A.; Omar, N. Y. M.; Mansoor, A.; Abdul-Rashid, H. A.; Mahdi, M. A.

2018-05-01

A tunable ring cavity single longitudinal mode (SLM) fiber laser incorporating Gallium-Erbium co-doped fiber (Ga-EDF) gain medium and several mode filtration techniques is demonstrated. With Ga-EDF, high emission power was accorded in short fiber length, allowing shorter overall cavity length and wider free spectral range. Tunable bandpass filter, sub-ring structure, and cascaded dissimilar fiber taper were utilized to filter multi-longitudinal modes. Each of the filter mechanism was tested individually within the laser cavity to assess its performance. Once the performance of each filter was obtained, all of them were deployed into the laser system. Ultimately, the 1561.47 nm SLM laser achieved a narrow linewidth laser, optical signal-to-noise ratio, and power fluctuation of 1.19 kHz, 61.52 dB and 0.16 dB, respectively. This work validates the feasibility of Ga-EDF to attain a stable SLM output in simple laser configuration.

High strain rate properties of angle-ply composite laminates, part 3

NASA Technical Reports Server (NTRS)

Daniel, I. M.

1991-01-01

Angle-ply graphite/epoxy and graphite/S-glass/epoxy laminates were characterized in uniaxial tension at strain rates ranging from quasi-static to over 500 s(sup -1). Laminate ring specimens of +/-15(sub 2s), +/-22.5(sub 2s), +/-30(sub 2s), +/-45(sub 2s), +/-60(sub 2s), +/-67.5(sub 2s), and +/-75(sub 2s) degree layups were loaded under internal pressure. Results were presented in the form of stress-strain curves to failure. Properties determined included moduli, Poisson's ratios, strength, and ultimate strain. In all seven laminates for the two materials tested the modulus and strength increase with strain rate. The effect of strain rate varies with layup, being lowest for the fiber dominated +/-15(sub 2s) degree laminates and highest for the matrix dominated +/-75(sub 2s) degree laminates. The highest increments over the static values are 10 to 25 percent for the +/-15(sub 2s) degree layup and 200 to 275 percent for the +/-75(sub 2s) degree layup. Ultimate strains do not show any significant trends with strain rate. In almost all cases the ultimate strain values are within +/-20 percent of the mean value and in half of the cases the deviation from the mean are less than 10 percent.

High temperature tensile properties of V-4Cr-4Ti

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zinkle, S.J.; Rowcliffe, A.F.; Stevens, C.O.

Tensile tests have been performed on V-4Cr-4Ti at 750 and 800 C in order to extend the data base beyond the current limit of 700 C. From comparison with previous measurements, the yield strength is nearly constant and tensile elongations decrease slightly with increasing temperature between 300 and 800 C. The ultimate strength exhibits an apparent maximum near 600 C (attributable to dynamic strain aging) but adequate strength is maintained up to 800 C. The reduction in area measured on tensile specimens remained high ({approximately}80%) for test temperatures up to 800 C, in contrast to previous reported results.

Combined Intercritical Annealing and Q&P Processing of Medium Mn Steel

NASA Astrophysics Data System (ADS)

De Cooman, Bruno C.; Lee, Seon Jong; Shin, Sunmi; Seo, Eun Jung; Speer, John G.

2017-01-01

The microstructure and mechanical properties of intercritically annealed medium Mn steel are dependent on the selection of the intercritical annealing (IA) temperature. While the yield strength (YS) decreases with increasing IA temperature, the ultimate tensile strength increases with increasing IA temperature. Strain aging phenomena, both static and dynamic, are also often observed. The present contribution shows that, by combining IA with the quench and partitioning processing of the intercritical austenite, it is possible to obtain non-aging mechanical properties which combine a high YS with an ultra-high tensile strength. These properties are particularly suitable for automotive parts related to passenger safety.

Mechanical tensile testing of titanium 15-3-3-3 and Kevlar 49 at cryogenic temperatures

NASA Astrophysics Data System (ADS)

James, B. L.; Martinez, R. M.; Shirron, P.; Tuttle, J.; Galassi, N. M.; McGuinness, D. S.; Puckett, D.; Francis, J. J.; Flom, Y.

2012-06-01

Titanium 15-3-3-3 and Kevlar 49 are highly desired materials for structural components in cryogenic applications due to their low thermal conductivity at low temperatures. Previous tests have indicated that titanium 15-3-3-3 becomes increasingly brittle as the temperature decreases. Furthermore, little is known regarding the mechanical properties of Kevlar 49 at low temperatures, most specifically its Young's modulus. This testing investigates the mechanical properties of both materials at cryogenic temperatures through cryogenic mechanical tensile testing to failure. The elongation, ultimate tensile strength, yield strength, and break strength of both materials are provided and analyzed here.

Mechanical Tensile Testing of Titanium 15-3-3-3 and Kevlar 49 at Cryogenic Temperatures

NASA Technical Reports Server (NTRS)

James, Bryan L.; Martinez, Raul M.; Shirron, Peter; Tuttle, Jim; Galassi, Nicholas M.; Mcguinness, Daniel S.; Puckett, David; Francis, John J.; Flom, Yury

2011-01-01

Titanium 15-3-3-3 and Kevlar 49 are highly desired materials for structural components in cryogenic applications due to their low thennal conductivity at low temperatures. Previous tests have indicated that titanium 15-3-3-3 becomes increasingly brittle as the temperature decreases. Furthermore, little is known regarding the mechanical properties of Kevlar 49 at low temperatures, most specifically its Young's modulus. This testing investigates the mechanical properties of both materials at cryogenic temperatures through cryogenic mechanical tensile testing to failure. The elongation, ultimate tensile strength, yield strength, and break strength of both materials are provided and analyzed here.

The Brittleness and Chemical Stability of Optimized Geopolymer Composites

PubMed Central

Steinerova, Michaela; Matulova, Lenka; Vermach, Pavel; Kotas, Jindrich

2017-01-01

Geopolymers are known as high strength and durable construction materials but have a brittle fracture. In practice, this results in a sudden collapse at ultimate load, without any chance of preventing the breakdown of parts or of withstanding the stress for some time. Glass fiber usage as a total anisotropic shape acting as a compact structure component should hinder the fracture mechanism. The optimized compositions in this study led to a significant reinforcement, especially in the case of flexural strength, but also in terms of the compressive strength and notch toughness. The positive and negative influence of the fibers on the complex composite properties provided chemical stability. PMID:28772756

The Brittleness and Chemical Stability of Optimized Geopolymer Composites.

PubMed

Steinerova, Michaela; Matulova, Lenka; Vermach, Pavel; Kotas, Jindrich

2017-04-09

Geopolymers are known as high strength and durable construction materials but have a brittle fracture. In practice, this results in a sudden collapse at ultimate load, without any chance of preventing the breakdown of parts or of withstanding the stress for some time. Glass fiber usage as a total anisotropic shape acting as a compact structure component should hinder the fracture mechanism. The optimized compositions in this study led to a significant reinforcement, especially in the case of flexural strength, but also in terms of the compressive strength and notch toughness. The positive and negative influence of the fibers on the complex composite properties provided chemical stability.

Movement compatibility for configurations of displays located in three cardinal orientations and ipsilateral, contralateral and overhead controls.

PubMed

Chan, Alan H S; Hoffmann, Errol R

2012-01-01

Stereotype strength and reversibility were determined for displays that were in the Front, Right and Left orientations relative to the operator, along with rotary, horizontally and vertically-moving controls located in the overhead, left-sagittal and right-sagittal planes. In each case, responses were made using the left and right hands. The arrangements used were (i) rotary control with a circular display (ii) horizontal/transverse control moving forward/rearward in the left and right-sagittal planes or transversely in the overhead plane and (iii) vertical/longitudinal control moving vertically in the left and right-sagittal planes and longitudinally in the overhead plane. These are all combinations not previously researched. Stereotype strength varied with display plane, type of control and plane of control. Models for the stereotype strength are developed, showing the contribution of various components to the overall stereotype strength. The major component for horizontally-moving controls comes from the "visual field" model of Worringham and Beringer (1998); for the rotary control important factors are "clockwise-for-clockwise" and the hand/control location effect (Hoffmann, 2009a). Vertically-moving controls are governed by a simple 'up-for-up' relationship between displays and controls. Overall stereotype strength is a maximum when all components add positively. Copyright © 2011 Elsevier Ltd and The Ergonomics Society. All rights reserved.

Grain-refining heat treatments to improve cryogenic toughness of high-strength steels

NASA Technical Reports Server (NTRS)

Rush, H. F.

1984-01-01

The development of two high Reynolds number wind tunnels at NASA Langley Research Center which operate at cryogenic temperatures with high dynamic pressures has imposed severe requirements on materials for model construction. Existing commercial high strength steels lack sufficient toughness to permit their safe use at temperatures approaching that of liquid nitrogen (-320 F). Therefore, a program to improve the cryogenic toughness of commercial high strength steels was conducted. Significant improvement in the cryogenic toughness of commercial high strength martensitic and maraging steels was demonstrated through the use of grain refining heat treatments. Charpy impact strength at -320 F was increased by 50 to 180 percent for the various alloys without significant loss in tensile strength. The grain sizes of the 9 percent Ni-Co alloys and 200 grade maraging steels were reduced to 1/10 of the original size or smaller, with the added benefit of improved machinability. This grain refining technique should permit these alloys with ultimate strengths of 220 to 270 ksi to receive consideration for cryogenic service.

High-Tensile Strength Tape Versus High-Tensile Strength Suture: A Biomechanical Study.

PubMed

Gnandt, Ryan J; Smith, Jennifer L; Nguyen-Ta, Kim; McDonald, Lucas; LeClere, Lance E

2016-02-01

To determine which suture design, high-tensile strength tape or high-tensile strength suture, performed better at securing human tissue across 4 selected suture techniques commonly used in tendinous repair, by comparing the total load at failure measured during a fixed-rate longitudinal single load to failure using a biomechanical testing machine. Matched sets of tendon specimens with bony attachments were dissected from 15 human cadaveric lower extremities in a manner allowing for direct comparison testing. With the use of selected techniques (simple Mason-Allen in the patellar tendon specimens, whip stitch in the quadriceps tendon specimens, and Krackow stitch in the Achilles tendon specimens), 1 sample of each set was sutured with a 2-mm braided, nonabsorbable, high-tensile strength tape and the other with a No. 2 braided, nonabsorbable, high-tensile strength suture. A total of 120 specimens were tested. Each model was loaded to failure at a fixed longitudinal traction rate of 100 mm/min. The maximum load and failure method were recorded. In the whip stitch and the Krackow-stitch models, the high-tensile strength tape had a significantly greater mean load at failure with a difference of 181 N (P = .001) and 94 N (P = .015) respectively. No significant difference was found in the Mason-Allen and simple stitch models. Pull-through remained the most common method of failure at an overall rate of 56.7% (suture = 55%; tape = 58.3%). In biomechanical testing during a single load to failure, high-tensile strength tape performs more favorably than high-tensile strength suture, with a greater mean load to failure, in both the whip- and Krackow-stitch models. Although suture pull-through remains the most common method of failure, high-tensile strength tape requires a significantly greater load to pull-through in a whip-stitch and Krakow-stitch model. The biomechanical data obtained in the current study indicates that high-tensile strength tape may provide better repair strength compared with high-tensile strength suture at time-zero simulated testing. Published by Elsevier Inc.

Political Culture versus Socioeconomic Approaches to Predicting Police Strength in U.S. Police Agencies: Results of a Longitudinal Study, 1993 to 2003

ERIC Educational Resources Information Center

Zhao, Jihong; Ren, Ling; Lovrich, Nicholas P.

2012-01-01

A variety of theories have emerged that offer plausible explanations, one from the political institutional perspective and others from sociological perspective. There has been renewed interest in the effect of local political structure on police strength in the policing literature. The purpose of this study, therefore, is to assess the two main…

Estimation of strength parameters of small-bore metal-polymer pipes

NASA Astrophysics Data System (ADS)

Shaydakov, V. V.; Chernova, K. V.; Penzin, A. V.

2018-03-01

The paper presents results from a set of laboratory studies of strength parameters of small-bore metal-polymer pipes of type TG-5/15. A wave method was used to estimate the provisional modulus of elasticity of the metal-polymer material of the pipes. Longitudinal deformation, transverse deformation and leak-off pressure were determined experimentally, with considerations for mechanical damage and pipe bend.

Trident sign trumps Aquaporin-4-IgG ELISA in diagnostic value in a case of longitudinally extensive transverse myelitis.

PubMed

Jolliffe, Evan A; Keegan, B Mark; Flanagan, Eoin P

2018-04-21

Longitudinally-extensive T2-hyperintense spinal cord lesions (≥3 vertebral segments) are associated with neuromyelitis optical spectrum disorder but occur with other disorders including spinal cord sarcoidosis. When linear dorsal subpial enhancement is accompanied by central cord/canal enhancement the axial post-gadolinium sequences may reveal a "trident" pattern that has previously been shown to be strongly suggestive of spinal cord sarcoidosis. We report a case in which the patient was initially diagnosed with neuromyelitis optical spectrum disorder, but where the "trident" sign ultimately led to the correct diagnosis of spinal cord sarcoidosis. Copyright © 2018. Published by Elsevier B.V.

Illuminating Cancer Systems With Genetically-Engineered Mouse Models and Coupled Luciferase Reporters In Vivo

PubMed Central

Kocher, Brandon; Piwnica-Worms, David

2013-01-01

Bioluminescent imaging (BLI) is a powerful non-invasive tool that has dramatically accelerated the in vivo interrogation of cancer systems and longitudinal analysis of mouse models of cancer over the past decade. Various luciferase enzymes have been genetically engineered into mouse models (GEMMs) of cancer which permit investigation of cellular and molecular events associated with oncogenic transcription, post-transcriptional processing, protein-protein interactions, transformation and oncogene addiction in live cells and animals. Luciferase-coupled GEMMs ultimately serve as a non-invasive, repetitive, longitudinal, and physiological means by which cancer systems and therapeutic responses can be investigated accurately within the autochthonous context of a living animal. PMID:23585416

Spherical powder for retaining thermosetting acrylic resin veneers.

PubMed

Tanaka, T; Atsuta, M; Uchiyama, Y; Nakabayashi, N; Masuhara, E

1978-03-01

1. Nine different sizes of spherical powder were prepared, and their effectiveness as retentive devices was evaluated against those available commercially. 2. Smaller-diameter spherical powder (No. 5) gave the best results of all retaining devices tested. 3. The physical properties of the resins play an important role in the retentive strength with No. 5 retention beads. The retentive strength was reduced when brittle resin was used. 4. The retentive strength of the resin veneer was greatly affected by the angle of stress at the incisal resin. The retentive strength increased as the angle between the longitudinal axis of the specimen and the direction of stress decreased.

Developmental Changes in Isometric Strength: Longitudinal Study in Adolescent Soccer Players.

PubMed

Duarte, Joao P; Valente-Dos-Santos, João; Coelho-E-Silva, Manuel J; Malina, R M; Deprez, Dieter; Philippaerts, Renaat; Lenoir, Matthieu; Vaeyens, Roel

2018-06-20

This study aimed to examine longitudinal changes in isometric strength of the knee extensors (ImKE) and knee flexors (ImKF) at 30° and 60°. The sample was composed of 67 players aged 11.0-13.9 years at baseline over five years. Stature, body mass, skinfolds, and isometric strength (ImKE30°, ImKF30°, ImKE60° and ImKF60°) were measured. Fat mass and fat-free mass (FFM) were derived from skinfolds. Skeletal age was obtained using TW2 RUS. Multilevel random effects regression analyses extracted developmental polynomial models. An annual increment on chronological age (CA) corresponded to 5.6 N (ImKE30°: ), 2.7 N (ImKF30°: ), 4.6 N (ImKE60°: ) and 1.5 N (ImKF60°). An increment of 1 kg in FFM predicted isometric strength as follows: 1.2 N (ImKE30°), 2.1 N (ImKF30°), 3.1 N (ImKE60°) and 2.0 N (ImKF60°). The following equations were obtained: ImKE30°=5.759×CA+1.163×FFM; ImKF30°=-19.369+2.691×CA+0.693×CA 2 +2.108×FFM; ImKE60°=4.553×CA+3.134×FFM; and, ImKF60°=-19.669+1.544×CA+2.033×FFM. Although skeletal maturity had a negligible effect on dependent variables, age and body size, based on FFM, were relevant longitudinal predictors. During adolescence, systematic assessment of knee extensors and knee flexors are strongly recommended to prevent impairment of knee muscle groups. © Georg Thieme Verlag KG Stuttgart · New York.

Tensile and pack compressive tests of some sheets of aluminum alloy, 1025 carbon steel, and chromium-nickel steel

NASA Technical Reports Server (NTRS)

Atchison, C S; Miller, James A

1942-01-01

Tensile and compressive stress-strain curves, stress-deviation curves, and secant modulus-stress curves are given for longitudinal and transverse specimens of 17S-T, 24S-T, and 24S-RT aluminum-alloy sheet in thicknesses from 0.032 to 0.081 inch, 1025 carbon steel sheet in thicknesses of 0.054 and 0.120 inch, and chromium-nickel steel sheet in thicknesses form 0.020 to 0.0275 inch. Significant differences were found between the tensile and the compressive stress-strain curves, and also the corresponding corollary curves; similarly, differences were found between the curves for the longitudinal and transverse directions. These differences are of particular importance in considering the compressive strength of aircraft structures made of thin sheet. They are explored further for the case of compression by giving tangent modulus-stress curves in longitudinal and transverse compression and dimensionless curves of the ratio of tangent modulus to Young's modulus and of the ratio of reduced modulus for a rectangular section to Young's modulus, both plotted against the ratio of stress to secant yield strength.

Optimizing concrete mix designs to produce cost effective paving mixes.

DOT National Transportation Integrated Search

2009-09-01

This research is designed to determine the effect of the mechanically activated fly ash on fresh : concrete properties and the ultimate strength of the hardened concrete. Six types of fly ash that are : locally available in the state of Oklahoma were...

Train crashworthiness design for occupant survivability

DOT National Transportation Integrated Search

1995-11-01

Studies were conducted evaluating the effectiveness of alternative strategies for providing crashworthiness of the vehicle structures. Conventional practice results in cars of essentially uniform : longitudinal strength. The crash energy management a...

Muscular strength is associated with self-esteem in college men but not women.

PubMed

Ciccolo, Joseph T; SantaBarbara, Nicholas J; Dunsiger, Shira I; Busch, Andrew M; Bartholomew, John B

2016-12-01

Muscular strength is a well-known predictor of morbidity and mortality. Similarly, self-esteem is a predictor of health and well-being. The relationship between these two variables, however, is currently unknown. This study examined the cross-sectional relationship between maximal muscular strength (i.e. handgrip and one-repetition-maximum (1-RM) squat) and global self-esteem in 126 college students. Significant correlations were found between both measures of muscular strength and self-esteem. Further analyses revealed that these relationships were only significant for men. Based on these results, additional research is needed to further explore the relationship between muscular strength and self-esteem, especially in other demographic groups and longitudinally. © The Author(s) 2015.

Mechanical properties and flexure behaviour of lightweight foamed concrete incorporating coir fibre

NASA Astrophysics Data System (ADS)

Mohamad, Noridah; Afif Iman, Muhamad; Othuman Mydin, M. A.; Samad, A. A. A.; Rosli, J. A.; Noorwirdawati, A.

2018-04-01

This paper presents an experimental investigation on the mechanical properties and flexural behaviour of lightweight foamed concrete (LFC) with added coir fibre as filler. The compressive strength (Pt), tensile strength (Ft), modulus of elasticity (E), ultimate load and crack pattern of the foamed concrete were determined. The coir fibre was added to the foamed concrete mixture at 0.1%, 0.2% and 0.3% of the total weight of cement. Effects of various percentage of coir fibre used on foam concrete’s mechanical and properties and flexural behaviour were studied and analysed. It was found that the increase percentage of fibre resulted in increase in compressive strength, tensile strength and modulus of elasticity of LFC mixture. LFC with added coir of 0.3% experienced the smallest crack propagation.

The Structure and Mechanical Properties of High-Strength Bulk Ultrafine-Grained Cobalt Prepared Using High-Energy Ball Milling in Combination with Spark Plasma Sintering

PubMed Central

Marek, Ivo; Vojtěch, Dalibor; Michalcová, Alena; Kubatík, Tomáš František

2016-01-01

In this study, bulk ultrafine-grained and micro-crystalline cobalt was prepared using a combination of high-energy ball milling and subsequent spark plasma sintering. The average grain sizes of the ultrafine-grained and micro-crystalline materials were 200 nm and 1 μm, respectively. Mechanical properties such as the compressive yield strength, the ultimate compressive strength, the maximum compressive deformation and the Vickers hardness were studied and compared with those of a coarse-grained as-cast cobalt reference sample. The bulk ultrafine-grained sample showed an ultra-high compressive yield strength that was greater than 1 GPa, which is discussed with respect to the preparation technique and a structural investigation. PMID:28773514

Structural tests on space shuttle thermal protection system constructed with nondensified and densified Li 900 and LI 2200 tile

NASA Technical Reports Server (NTRS)

Williams, J. G.

1981-01-01

Structural tests were conducted on thermal protection systems (TPS) LI 900 and LI 2200 tiles and .41 cm and .23 cm thick strain isolation pads. The bond surface of selected tiles was densified to obtain improved strength. Four basic types of experiments were conducted including tension tests, substrate mismatch (initial imperfection) tests, tension loads eccentrically applied, and pressure loads applied rapidly to the tile top surface. A small initial imperfection mismatch (2.29 m spherical radius on the substrate) did not influence significantly the ultimate failure strength. Densification of the tile bond region improved the strength of TPS constructed both of LI 900 tile and of LI 2200 tile. Pressure shock conditions studied did not significantly affect the TPS strength.

Behavior of standard hook anchorage with corrosion resistant reinforcement : final report, June 2008.

DOT National Transportation Integrated Search

2008-06-01

The objective of this study was to evaluate the behavior of standard books that are made using corrosion resistant reinforcement, which typically have higher yield and ultimate strengths than that of ASTM A615 Grade 60 reinforcement. Two steel types ...

Evidence Report: Risk of Bone Fracture due to Spaceflight-Induced Changes to Bone

NASA Technical Reports Server (NTRS)

Sibonga, Jean D.; Evans, Harlan J.; Smith, Scott A.; Spector, Elisabeth R.; Yardley, Greg; Myer, Jerry

2017-01-01

Given that spaceflight may induce adverse changes in bone ultimate strength with respect to mechanical loads during and post-mission, there is a possibility a fracture may occur for activities otherwise unlikely to induce fracture prior to initiating spaceflight.

Effects of Vacancy Concentration and Temperature on Mechanical Properties of Single-Crystal γ-TiAl Based on Molecular Dynamics Simulation

NASA Astrophysics Data System (ADS)

Ruicheng, Feng; Hui, Cao; Haiyan, Li; Zhiyuan, Rui; Changfeng, Yan

2018-01-01

Molecular dynamics simulation is used to analyze tensile strength and elastic modulus under different temperatures and vacancy concentrations. The effects of temperature and vacancy concentration on the mechanical properties of γ-TiAl alloy are investigated. The results show that the ultimate stress, ultimate strain and elastic modulus decrease nonlinearly with increasing temperature and vacancy concentration. As the temperature increases, the plastic of material is reinforced. The influence of temperature on strength and elastic modulus is larger than that of vacancy concentration. The evolution process of vacancy could be observed clearly. Furthermore, vacancies with different concentrations develop into voids first as a function of external forces or other factors, micro cracks evolve from those voids, those micro cracks then converge to a macro crack, and fracture will finally occur. The vacancy evolution process cannot be observed clearly owing to the thermal motion of atoms at high temperature. In addition, potential energy is affected by both temperature and vacancy concentration.

Effect of rotation speed and welding speed on Friction Stir Welding of AA1100 Aluminium alloy

NASA Astrophysics Data System (ADS)

Raja, P.; Bojanampati, S.; Karthikeyan, R.; Ganithi, R.

2018-04-01

Aluminum AA1100 is the most widely used grade of Aluminium due to its excellent corrosion resistance, high ductility and reflective finish, the selected material was welded with Friction Stir Welding (FSW) process on a CNC machine, using a combination of different tool rotation speed (1500 rpm, 2500 rpm, 3500 rpm) and welding speed (10 mm/min, 30 mm/min, 50 mm/min) as welding parameters. The effect of FSW using this welding parameter was studied by measuring the ultimate tensile strength of the welded joints. A high-speed steel tool was prepared for welding the Aluminium AA1100 alloy having an 8mm shoulder diameter and pin dimension of 4mm diameter and 2.8 mm length. The welded joints were tested using the universal testing machine. It was found that Ultimate Tensile Strength of FSW specimen was highest with a value of 98.08 MPa when the weld was performed at rotation speed of 1500 RPM and welding speed of 50 mm/min.

Hot pressing titanium metal matrix composites reinforced with graphene nanoplatelets through an in-situ reactive method

NASA Astrophysics Data System (ADS)

Mu, X. N.; Zhang, H. M.; Cai, H. N.; Fan, Q. B.; Wu, Y.; Fu, Z. J.; Wang, Q. X.

2017-05-01

This study proposed an in-situ reactive method that uses graphene as a reinforcement to fabricate titanium metal matrix composites (TiMMCs) through powder metallurgy processing route. The volume fraction of graphene nanoplatelets was 1.8%vol, and the pure titanium was used as a matrix. The Archimedes density, hardness, microstructure and mechanical properties of specimens were compared under different ball milling times (20 min and 2.5 h) and hot pressing temperatures (900°C, 1150°C, and 1300°C,). The ultimate tensile strength of 630 MPa, which demonstrated a 27.3% increase compared with pure Ti, was achieved under a ball milling time of 20 min. Elongation increased with increasing temperature. When the ball milling time and hot pressing temperature were increased to 2.5 h and 1300 °C, respectively, the ultimate tensile strength of the composites reached 750 MPa, showing an increase of 51.5% compared with pure Ti.

Mechanical Strength of the Side-to-Side Tendon Attachment for Mismatched Tendon Sizes and Shapes

PubMed Central

Fridén, Jan; Tirrell, Timothy F.; Bhola, Siddharth; Lieber, Richard L.

2015-01-01

Summary Certain combinations are advised against in tendon transfers due to size or shape mismatches between donor and recipient tendons. In this study, ultimate load, stiffness and Young’s modulus were measured in two tendon-to-tendon attachments with intentionally mismatched donor and recipient tendons - pronator teres (PT)-to-extensor carpi radialis brevis (ECRB) and flexor carpi ulnaris (FCU)-to-extensor digitorum communis (EDC). FCU-EDC attachments failed at higher loads than PT-to-ECRB attachments but they had similar modulus and stiffness values. Ultimate tensile strength of the tendon attachments exceeded the maximum predicted contraction force of any of the affected muscles, with safety factors of 4x and 2x for the FCU-to-EDC and PT-to-ECRB constructs, respectively. This implies that size and shape mismatch should not be a contraindication to tendon attachment in transfers. Further, these safety factors strongly suggest that no postoperative immobilization of these attachments is necessary. PMID:24413573

Tensile experiments and SEM fractography on bovine subchondral bone.

PubMed

Braidotti, P; Bemporad, E; D'Alessio, T; Sciuto, S A; Stagni, L

2000-09-01

Subchondral bone undecalcified samples, extracted from bovine femoral heads, are subjected to a direct tensile load. The Young's modulus of each sample is determined from repeated tests within the elastic limit. In a last test, the tensile load is increased up to the specimen failure, determining the ultimate tensile strength. The investigation is performed on both dry and wet specimens. The measured Young's modulus for dry samples is 10.3+/-2.5GPa, while that of wet samples is 3.5+/-1.2GPa. The ultimate tensile strengths are 36+/-10 and 30+/-7.5MPa for dry and wet specimens, respectively. SEM micrographs of failure surfaces show characteristic lamellar bone structures, with lamellae composed of calcified collagen fibers. Rudimentary osteon-like structures are also observed. Failure surfaces of wet samples show a marked fiber pull-out, while delamination predominates in dry samples. The obtained results are interpreted on the basis of the deformation mechanisms typical of fiber-reinforced laminated composite materials.

Effect of Copper Coated SiC Reinforcements on Microstructure, Mechanical Properties and Wear of Aluminium Composites

NASA Astrophysics Data System (ADS)

Kori, P. S.; Vanarotti, Mohan; Angadi, B. M.; Nagathan, V. V.; Auradi, V.; Sakri, M. I.

2017-08-01

Experimental investigations are carried out to study the influence of copper coated Silicon carbide (SiC) reinforcements in Aluminum (Al) based Al-SiC composites. Wear behavior and mechanical Properties like, ultimate tensile strength (UTS) and hardness are studied in the present work. Experimental results clearly revealed that, an addition of SiC particles (5, 10 and 15 Wt %) has lead in the improvement of hardness and ultimate tensile strength. Al-SiC composites containing the Copper coated SiC reinforcements showed better improvement in mechanical properties compared to uncoated ones. Characterization of Al-SiC composites are carried out using optical photomicrography and SEM analysis. Wear tests are carried out to study the effects of composition and normal pressure using Pin-On Disc wear testing machine. Results suggested that, wear rate decreases with increasing SiC composition, further an improvement in wear resistance is observed with copper coated SiC reinforcements in the Al-SiC metal matrix composites (MMC’s).

Identification of strengthening phases in Al-Cu-Li alloy Weldalite (tm) 049

NASA Technical Reports Server (NTRS)

1991-01-01

Microstructure property relationships were determined for a family of ultrahigh strength weldable Al-Cu-Li based alloys referred to as Weldalite (tm) alloys. The highest strength variant of this family, Weldalite 049, has a high Cu/Li wt pct. ratio with a nominal composition of Al-6.3Cu-1.3Li-0.4Ag-0.4Mg-0.14Zr. Increasing the alloy's lithium content above 1.3 wt pct. resulted in a decrease in both yield and ultimate tensile strength. Strength was shown to be strongly dependent on lithium content, with a maximum in strength occurring in the range of about 1.1 to 1.4 wt pct. lithium. The strengthening phases present in Weldalite 049 (1.3Li) and an Al-6.3Cu-1.9Li-0.4Mg-0.14Zr alloy were identified using transmission electron microscopy (TEM).

Comparative characterization of a novel cad-cam polymer-infiltrated-ceramic-network

PubMed Central

Pascual, Agustín; Camps, Isabel; Grau-Benitez, María

2015-01-01

Background The field of dental ceramics for CAD-CAM is enriched with a new innovative material composition having a porous three-dimensional structure of feldspathic ceramic infiltrated with acrylic resins.The aim of this study is to determine the mechanical properties of Polymer-Infiltrated-Ceramic-Network (PICN) and compare its performance with other ceramics and a nano-ceramic resin available for CAD-CAM systems. Material and Methods In this study a total of five different materials for CAD-CAM were investigated. A polymer-infiltrated ceramic (Vita Enamic), a nano-ceramic resin (Lava Ultimate), a feldspathic ceramic (Mark II), a lithium disilicate ceramic (IPS-e max CAD) and finally a Leucite based ceramic (Empress - CAD). From CAD-CAM blocks, 120 bars (30 for each material cited above) were cut to measure the flexural strength with a three-point-bending test. Strain at failure, fracture stress and Weibull modulus was calculated. Vickers hardness of each material was also measured. Results IPS-EMAX presents mechanical properties significantly better from the other materials studied. Its strain at failure, flexural strength and hardness exhibited significantly higher values in comparison with the others. VITA ENAMIC and LAVA ULTIMATE stand out as the next most resistant materials. Conclusions The flexural strength, elastic modulus similar to a tooth as well as having less hardness than ceramics make PICN materials an option to consider as a restorative material. Key words:Ceramic infiltrated with resin, CAD-CAM, Weibull modulus, flexural strength, micro hardness. PMID:26535096

Dependency of Shear Strength on Test Rate in SiC/BSAS Ceramic Matrix Composite at Elevated Temperature

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Bansal, Narottam P.; Gyekenyesi, John P.

2003-01-01

Both interlaminar and in-plane shear strengths of a unidirectional Hi-Nicalon(TM) fiber-reinforced barium strontium aluminosilicate (SiC/BSAS) composite were determined at 1100 C in air as a function of test rate using double notch shear test specimens. The composite exhibited a significant effect of test rate on shear strength, regardless of orientation which was either in interlaminar or in in-plane direction, resulting in an appreciable shear-strength degradation of about 50 percent as test rate decreased from 3.3 10(exp -1) mm/s to 3.3 10(exp -5) mm/s. The rate dependency of composite's shear strength was very similar to that of ultimate tensile strength at 1100 C observed in a similar composite (2-D SiC/BSAS) in which tensile strength decreased by about 60 percent when test rate varied from the highest (5 MPa/s) to the lowest (0.005 MPa/s). A phenomenological, power-law slow crack growth formulation was proposed and formulated to account for the rate dependency of shear strength of the composite.

Biomechanical and clinical factors related to stage I posterior tibial tendon dysfunction.

PubMed

Rabbito, Melissa; Pohl, Michael B; Humble, Neil; Ferber, Reed

2011-10-01

Case control. To investigate differences in arch height, ankle muscle strength, and biomechanical factors in individuals with stage I posterior tibial tendon dysfunction (PTTD) in comparison to healthy individuals. PTTD is a progressive condition, so early recognition and treatment are essential to help delay or reverse the progression. However, no previous studies have investigated stage I PTTD, and no single study has measured static anatomical structure, muscle strength, and gait mechanics in this population. Twelve individuals with stage I PTTD and 12 healthy, age- and gender-matched control subjects, who were engaged in running-related activities, participated in this study. Measurements of arch height index, maximum voluntary ankle invertor muscle strength, and 3-dimensional rearfoot and medial longitudinal arch kinematics during walking were obtained. The runners with PTTD demonstrated significantly lower seated arch height index (P = .02) and greater (P = .03) and prolonged (P = .05) peak rearfoot eversion angle during gait, compared to the healthy runners. No differences were found in standing arch height index values (P = .28), arch rigidity index (P = .06), ankle invertor strength (P = .49), or peak medial longitudinal arch values (P = .49) between groups. The increased foot pronation is hypothesized to place greater strain on the posterior tibialis muscle, which may partially explain the progressive nature of this condition.

Long-term thermal degradation and alloying constituent effects on five boron/aluminum composites

NASA Technical Reports Server (NTRS)

Olsen, G. C.

1982-01-01

Thermal exposure effects on the properties of five boron/aluminum composite systems were experimentally investigated. The composite systems were 49 volume percent boron fibers (203 micron diameter) in aluminum-alloy matrices 1100 Al, 2024 Al, 3003 Al, 5052 Al, and 6061 Al. Specimens were thermally exposed up to 10,000 hours at 500 K and 590 K, up to 500 hours at 730 K, and up to 10,000 hours at 500 K and 590 K, up to 500 hours at 730 K, and up to 2000 thermal cycles between 200 K and 590 K. Composite longitudinal and transverse tensile strengths, longitudinal compression strength, and in-plane shear strength were determined. None of the systems was severely degraded by exposure at 590 K. The best performing system was B-2024 Al. Effects of matrix alloys on degradation mechanisms were experimentally investigated. Composite specimens and individual fibers were metallurgically analyzed with a scanning electron microscope and an electron microprobe to determine failure characteristics, chemical element distribution, and reaction layer morphology. Alloying constituents were found to be affect the composite degradation mechanisms as follows: alloys containing iron, but without manganese as a stabilizer, caused increased low-temperature degradation; alloys containing magnesium, iron, or manganese caused increased degradation; and alloys containing copper caused increased fiber strength.

Prediction of shear critical behavior of high-strength reinforced concrete columns using finite element methods

NASA Astrophysics Data System (ADS)

Alrasyid, Harun; Safi, Fahrudin; Iranata, Data; Chen-Ou, Yu

2017-11-01

This research shows the prediction of shear behavior of High-Strength Reinforced Concrete Columns using Finite-Element Method. The experimental data of nine half scale high-strength reinforced concrete were selected. These columns using specified concrete compressive strength of 70 MPa, specified yield strength of longitudinal and transverse reinforcement of 685 and 785 MPa, respectively. The VecTor2 finite element software was used to simulate the shear critical behavior of these columns. The combination axial compression load and monotonic loading were applied at this prediction. It is demonstrated that VecTor2 finite element software provides accurate prediction of load-deflection up to peak at applied load, but provide similar behavior at post peak load. The shear strength prediction provide by VecTor 2 are slightly conservative compare to test result.

Method of forming biaxially textured alloy substrates and devices thereon

DOEpatents

Goyal, Amit; Specht, Eliot D.; Kroeger, Donald M.; Paranthaman, Mariappan

2000-01-01

Specific alloys, in particular Ni-based alloys, that can be biaxially textured, with a well-developed, single component texture are disclosed. These alloys have a significantly reduced Curie point, which is very desirable from the point of view of superconductivity applications. The biaxially textured alloy substrates also possess greatly enhanced mechanical properties (yield strength, ultimate tensile strength) which are essential for most applications, in particular, superconductors. A method is disclosed for producing complex multicomponent alloys which have the ideal physical properties for specific applications, such as lattice parameter, degree of magnetism and mechanical strength, and which cannot be in textured form. In addition, a method for making ultra thin biaxially textured substrates with complex compositions is disclosed.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Samoylenko, Vitaliy V., E-mail: samoylenko.vitaliy@mail.ru; Lenivtseva, Olga G., E-mail: lenivtseva-olga@mail.ru; Polyakov, Igor A., E-mail: status9@mail.ru

In this paper structural investigations and mechanical tests of Ti-Ta-Zr coatings obtained on surfaces of cp-titanium workpieces were carried out. It was found that the coatings had a dendrite structure; investigations at high-power magnifications revealed a platelet structure. An increase of tantalum concentration led to refinement of structural components. The microhardness level of all coatings, excepting a specimen with the maximum tantalum content, was 370 HV. The microhardness of this coating reached 400 HV. The ultimate tensile strength of cladded layers varied from 697 to 947 MPa. Adhesion tests showed that bimetallic composites were characterized by high bond strength of claddedmore » layers to the substrate, which exceeded cp-titanium strength characteristics.« less

Human versus non-cross-linked porcine acellular dermal matrix used for ventral hernia repair: comparison of in vivo fibrovascular remodeling and mechanical repair strength.

PubMed

Campbell, Kristin Turza; Burns, Nadja K; Rios, Carmen N; Mathur, Anshu B; Butler, Charles E

2011-06-01

Human acellular dermal matrix (HADM) and non-cross-linked porcine acellular dermal matrix (ncl-PADM) are clinically useful for complex ventral hernia repair. Direct comparisons between the two in vivo are lacking, however. This study compared clinically relevant early outcomes with these bioprosthetic materials when used for ventral hernia repair. Seventy-two guinea pigs underwent inlay repair of surgically created hernias with HADM (n = 37) or ncl-PADM (n = 35). Repair sites were harvested at 1, 2, or 4 weeks postoperatively. Adhesions were graded and quantified. Mechanical testing and histologic and immunohistologic (factor VIII) analyses of cellular and vascular infiltration were performed. No infections or recurrent hernias occurred. No difference was observed in mean adhesion surface area or tenacity between groups. Mean cellular infiltration (p < 0.002, weeks 1 and 4; p < 0.006, week 2) and vascular infiltration (p < 0.0003, week 1; p < 0.0001, weeks 2 and 4) were greater in HADM. Ultimate tensile strength at the implant-musculofascia interface increased over time with both materials, but no difference was observed at 4 weeks. The mean ultimate tensile strength of explanted ncl-PADM itself was consistently greater than that of HADM. The elastic modulus (stiffness) did not differ between groups at the interface but was greater in explanted ncl-PADM (p < 0.0001, weeks 1 and 2; p < 0.02, week 4). Both HADM and ncl-PADM become infiltrated with host cells and blood vessels within 4 weeks and have similar musculofascia-bioprosthetic interface strength. However, HADM has greater cellular and vascular infiltration. Longer-term studies will help determine whether later differences in material strength, stiffness, and remodeling affect hernia and/or bulge incidence.

Effect of Incorporation of Antifungal Agents on the Ultimate Tensile Strength of Temporary Soft Denture Liners.

PubMed

Neppelenbroek, Karin Hermana; Lima, Jozely Francisca Mello; Hotta, Juliana; Galitesi, Lucas Lulo; Almeida, Ana Lucia Pompéia Fraga; Urban, Vanessa Migliorini

2018-02-01

To investigate the ultimate tensile strength of temporary soft denture liners modified by minimum inhibitory concentrations (MICs) of antifungal agents for Candida albicans biofilm (SC5314) determined in previous microbiological research. Dumbbell-shaped specimens (n = 7) with a central cross-sectional area of 6 × 3 × 33 mm were produced by Softone and Trusoft, without (control) or with incorporation of drugs in powder form at MICs for C. albicans biofilm (per g of material powder): nystatin (0.032 g), chlorhexidine diacetate (0.064 g), ketoconazole (0.128 g), miconazole (0.256 g), and itraconazole (0.256 g). After plasticization, specimens were immersed in distilled water at 37°C for 24 hours, 7 or 14 days, and then tested in tension in a universal testing machine at 40 mm/min. Data of tensile strength (MPa) and elongation percentage (%) were submitted to 3-way ANOVA and Tukey's test (α = 0.05). At the end of 14 days, the tensile strength for both materials was significantly lower in the groups modified by miconazole and itraconazole compared to the other groups (p < 0.0001), which showed no significant difference between them (p > 0.05). After 7 and 14 days in water, miconazole and itraconazole added into both materials resulted in significantly lower elongation percentages compared to the other antifungal agents and control (p < 0.0001), which were similar to each other (p > 0.05). The addition of the nystatin, chlorhexidine, and ketoconazole at MICs for C. albicans biofilm resulted in no harmful effects on the tensile strength and elongation percentage of the temporary soft denture liner materials up to 14 days. © 2017 by the American College of Prosthodontists.

Load response and gap formation in a single-row cruciate suture rotator cuff repair.

PubMed

Huntington, Lachlan; Richardson, Martin; Sobol, Tony; Caldow, Jonathon; Ackland, David C

2017-06-01

Double-row rotator cuff tendon repair techniques may provide superior contact area and strength compared with single-row repairs, but are associated with higher material expenses and prolonged operating time. The purpose of this study was to evaluate gap formation, ultimate tensile strength and stiffness of a single-row cruciate suture rotator cuff repair construct, and to compare these results with those of the Mason-Allen and SutureBridge repair constructs. Infraspinatus tendons from 24 spring lamb shoulders were harvested and allocated to cruciate suture, Mason-Allen and SutureBridge repair groups. Specimens were loaded cyclically between 10 and 62 N for 200 cycles, and gap formation simultaneously measured using a high-speed digital camera. Specimens were then loaded in uniaxial tension to failure, and construct stiffness and repair strength were evaluated. Gap formation in the cruciate suture repair was significantly lower than that of the Mason-Allen repair (mean difference = 0.6 mm, P = 0.009) and no different from that of the SutureBridge repair (P > 0.05). Both the cruciate suture repair (mean difference = 15.7 N/mm, P = 0.002) and SutureBridge repair (mean difference = 15.8 N/mm, P = 0.034) were significantly stiffer than that of the Mason-Allen repair; however, no significant differences in ultimate tensile strength between repair groups were discerned (P > 0.05). The cruciate suture repair construct, which may represent a simple and cost-effective alternative to double-row and double-row equivalent rotator cuff repairs, has comparable biomechanical strength and integrity with that of the SutureBridge repair, and may result in improved construct longevity and tendon healing compared with the Mason-Allen repair. © 2017 Royal Australasian College of Surgeons.

Optimization of BI test parameters to investigate mechanical properties of Grade 92 steel

NASA Astrophysics Data System (ADS)

Barbadikar, Dipika R.; Vincent, S.; Ballal, Atul R.; Peshwe, Dilip R.; Mathew, M. D.

2018-04-01

The ball indentation (BI) testing is used to evaluate the tensile properties of materials namely yield strength, strength coefficient, ultimate tensile strength, and strain hardening exponent. The properties evaluated depend on a number of BI test parameters. These parameters include the material constants like yield slope (YS), constraint factor (CF), yield offset parameter (YOP). Number of loading/unloading cycles, preload, indenter size and depth of penetration of indenter also affects the properties. In present investigation the effect of these parameters on the stress-strain curve of normalized and tempered Grade 92 steel is evaluated. Grade 92 is a candidate material for power plant application over austenitic stainless steel and derives its strength from M23C6, MX precipitates and high dislocation density. CF, YS and YOP changed the strength properties considerably. Indenter size effect resulted in higher strength for smaller indenter. It is suggested to use larger indenter diameter and higher number of loading cycles for GRADE 92 steel to get best results using BI technique.

The synchronous improvement of strength and plasticity (SISP) in new Ni-Co based disc superalloys by controling stacking fault energy.

PubMed

Xu, H; Zhang, Z J; Zhang, P; Cui, C Y; Jin, T; Zhang, Z F

2017-08-14

It is a great challenge to improve the strength of disc superalloys without great loss of plasticity together since the microstructures benefiting the strength always do not avail the plasticity. Interestingly, this study shows that the trade-off relationship between strength and plasticity can be broken through decreasing stacking fault energy (SFE) in newly developed Ni-Co based disc superalloys. Axial tensile tests in the temperature range of 25 to 725 °C were carried out in these alloys with Co content ranging from 5% to 23% (wt.%). It is found that the ultimate tensile strength (UTS) and uniform elongation (UE) are improved synchronously when microtwinning is activated by decreasing the SFE at 650 and 725 °C. In contrast, only UTS is improved when stacking fault (SF) dominates the plastic deformation at 25 and 400 °C. These results may be helpful for designing advanced disc superalloys with relatively excellent strength and plasticity simultaneously.

46 CFR 42.15-30 - Hatchways closed by weathertight covers of steel or other equivalent material fitted with gaskets...

Code of Federal Regulations, 2012 CFR

2012-10-01

... of 4.25 shall not exceed the minimum ultimate strength of the material. They shall be so designed as... the initial surveys, and may be required at periodical surveys and at annual surveys or at more...

46 CFR 42.15-30 - Hatchways closed by weathertight covers of steel or other equivalent material fitted with gaskets...

Code of Federal Regulations, 2014 CFR

2014-10-01

... of 4.25 shall not exceed the minimum ultimate strength of the material. They shall be so designed as... the initial surveys, and may be required at periodical surveys and at annual surveys or at more...

46 CFR 42.15-30 - Hatchways closed by weathertight covers of steel or other equivalent material fitted with gaskets...

Code of Federal Regulations, 2011 CFR

2011-10-01

... of 4.25 shall not exceed the minimum ultimate strength of the material. They shall be so designed as... the initial surveys, and may be required at periodical surveys and at annual surveys or at more...

46 CFR 42.15-30 - Hatchways closed by weathertight covers of steel or other equivalent material fitted with gaskets...

Code of Federal Regulations, 2010 CFR

2010-10-01

... of 4.25 shall not exceed the minimum ultimate strength of the material. They shall be so designed as... the initial surveys, and may be required at periodical surveys and at annual surveys or at more...

46 CFR 42.15-30 - Hatchways closed by weathertight covers of steel or other equivalent material fitted with gaskets...

Code of Federal Regulations, 2013 CFR

2013-10-01

... of 4.25 shall not exceed the minimum ultimate strength of the material. They shall be so designed as... the initial surveys, and may be required at periodical surveys and at annual surveys or at more...

14 CFR 23.572 - Metallic wing, empennage, and associated structures.

Code of Federal Regulations, 2012 CFR

2012-01-01

... principal structural element, and that the remaining structure is able to withstand a static ultimate load... TRANSPORTATION AIRCRAFT AIRWORTHINESS STANDARDS: NORMAL, UTILITY, ACROBATIC, AND COMMUTER CATEGORY AIRPLANES... experience: (1) A fatigue strength investigation in which the structure is shown by tests, or by analysis...

14 CFR 23.572 - Metallic wing, empennage, and associated structures.

Code of Federal Regulations, 2013 CFR

2013-01-01

... principal structural element, and that the remaining structure is able to withstand a static ultimate load... TRANSPORTATION AIRCRAFT AIRWORTHINESS STANDARDS: NORMAL, UTILITY, ACROBATIC, AND COMMUTER CATEGORY AIRPLANES... experience: (1) A fatigue strength investigation in which the structure is shown by tests, or by analysis...

14 CFR 23.572 - Metallic wing, empennage, and associated structures.

Code of Federal Regulations, 2014 CFR

2014-01-01

... principal structural element, and that the remaining structure is able to withstand a static ultimate load... TRANSPORTATION AIRCRAFT AIRWORTHINESS STANDARDS: NORMAL, UTILITY, ACROBATIC, AND COMMUTER CATEGORY AIRPLANES... experience: (1) A fatigue strength investigation in which the structure is shown by tests, or by analysis...

14 CFR 23.572 - Metallic wing, empennage, and associated structures.

Code of Federal Regulations, 2011 CFR

2011-01-01

... principal structural element, and that the remaining structure is able to withstand a static ultimate load... TRANSPORTATION AIRCRAFT AIRWORTHINESS STANDARDS: NORMAL, UTILITY, ACROBATIC, AND COMMUTER CATEGORY AIRPLANES... experience: (1) A fatigue strength investigation in which the structure is shown by tests, or by analysis...

14 CFR 23.572 - Metallic wing, empennage, and associated structures.

Code of Federal Regulations, 2010 CFR

2010-01-01

... principal structural element, and that the remaining structure is able to withstand a static ultimate load... TRANSPORTATION AIRCRAFT AIRWORTHINESS STANDARDS: NORMAL, UTILITY, ACROBATIC, AND COMMUTER CATEGORY AIRPLANES... experience: (1) A fatigue strength investigation in which the structure is shown by tests, or by analysis...

Review of "Charting New Territory"

ERIC Educational Resources Information Center

Trujillo, Tina

2011-01-01

"Charting New Territory: Tapping Charter Schools to Turn Around the Nation's Dropout Factories" argues for a more prominent role for charter operators in turning around perennially low-performing high schools. However, the report's ultimate findings and conclusions are out of proportion to the strength of the research evidence on school…

Correlation of Fiber Composite Tensile Strength with the Ultrasonic Stress Wave Factor

NASA Technical Reports Server (NTRS)

Vary, A.; Lark, R. F.

1978-01-01

An ultrasonic-acoustic technique was used to indicate the strength variations of tensile specimens of a graphite-epoxy composite. A stress wave factor was determined and its value was found to depend on variations of the fiber-resin bonding as well as fiber orientation. The fiber orientations studied were 0 deg (longitudinal), 10 deg (off-axis), 90 deg (transverse), 0 deg + or - 45 deg/0 deg symmetrical, and + or - 45 deg] symmetrical. The stress wave factor can indicate variations of the tensile and shear strengths of composite materials. The stress wave factor was also found to be sensitive to strength variations associated with microporosity and differences in fiber-resin ratio.

Mechanical performance and parameter sensitivity analysis of 3D braided composites joints.

PubMed

Wu, Yue; Nan, Bo; Chen, Liang

2014-01-01

3D braided composite joints are the important components in CFRP truss, which have significant influence on the reliability and lightweight of structures. To investigate the mechanical performance of 3D braided composite joints, a numerical method based on the microscopic mechanics is put forward, the modeling technologies, including the material constants selection, element type, grid size, and the boundary conditions, are discussed in detail. Secondly, a method for determination of ultimate bearing capacity is established, which can consider the strength failure. Finally, the effect of load parameters, geometric parameters, and process parameters on the ultimate bearing capacity of joints is analyzed by the global sensitivity analysis method. The results show that the main pipe diameter thickness ratio γ, the main pipe diameter D, and the braided angle α are sensitive to the ultimate bearing capacity N.

The Effect of Fiber Strength Stochastics and Local Fiber Volume Fraction on Multiscale Progressive Failure of Composites

NASA Technical Reports Server (NTRS)

Ricks, Trenton M.; Lacy, Jr., Thomas E.; Bednarcyk, Brett A.; Arnold, Steven M.

2013-01-01

Continuous fiber unidirectional polymer matrix composites (PMCs) can exhibit significant local variations in fiber volume fraction as a result of processing conditions that can lead to further local differences in material properties and failure behavior. In this work, the coupled effects of both local variations in fiber volume fraction and the empirically-based statistical distribution of fiber strengths on the predicted longitudinal modulus and local tensile strength of a unidirectional AS4 carbon fiber/ Hercules 3502 epoxy composite were investigated using the special purpose NASA Micromechanics Analysis Code with Generalized Method of Cells (MAC/GMC); local effective composite properties were obtained by homogenizing the material behavior over repeating units cells (RUCs). The predicted effective longitudinal modulus was relatively insensitive to small (8%) variations in local fiber volume fraction. The composite tensile strength, however, was highly dependent on the local distribution in fiber strengths. The RUC-averaged constitutive response can be used to characterize lower length scale material behavior within a multiscale analysis framework that couples the NASA code FEAMAC and the ABAQUS finite element solver. Such an approach can be effectively used to analyze the progressive failure of PMC structures whose failure initiates at the RUC level. Consideration of the effect of local variations in constituent properties and morphologies on progressive failure of PMCs is a central aspect of the application of Integrated Computational Materials Engineering (ICME) principles for composite materials.

Strength analysis and design of adhesive joints between circular elements made of metal and reinforced polymer materials

NASA Astrophysics Data System (ADS)

Pelekh, B. L.; Marchuk, M. V.; Kogut, I. S.

1992-06-01

The stress-strain state of an adhesive joint between cylindrical components made of a metal (steel) and a cross-reinforced filament-wound composite (glass/polymer or basalt/polymer) was investigated under static axial loading using newly proposed experimental techniques and a refined mathematical model. Analytical expressions are obtained for contact stresses in the adhesive joint. The maximum permissible load and the ultimate shear strength of the joint are determined. The experimental results are found to be in satisfactory agreement with model predictions.

Development of Fuel Hose for Use in the Arctic.

DTIC Science & Technology

1983-12-01

Teonsil* Strength. psi (min) 1500 1500 AST" D-412 eStress (100% elongation), psi record record AST4 D-412 .Ultimate Elongation, t (min) I(i 150 ASTM D-412...0.5 hr 94 hras + 0.5 hr AST14 D-47173.40F + 3.60F for: - - .Tensile Strength Retained, % (min) 60 40 ASTM D-471 eStress (1001 elongation) Retained...or fracture at -600 F, it was stiff. Moreover, it was very difficult to process and a cure temperature in excess of 302OF is necessary. Present hose

An Investigation of Physico-Mechanical Properties of Ultrafine-Grained Magnesium Alloys Subjected to Severe Plastic Deformation

NASA Astrophysics Data System (ADS)

Kozulyn, A. A.; Skripnyak, V. A.; Krasnoveikin, V. A.; Skripnyak, V. V.; Karavatskii, A. K.

2015-01-01

The results of investigations of physico-mechanical properties of specimens made from the structural Mg-based alloy (Russian grade Ma2-1) in its coarse-grained and ultrafine-grained states after SPD processing are presented. To form the ultrafine-grained structure, use was made of the method of orthogonal equal-channel angular pressing. After four passes through the die, a simultaneous increase was achieved in microhardness, yield strength, ultimate tensile strength and elongation to failure under conditions of uniaxial tensile loading.

Development of near β titanium alloy with high strength and superplastic properties

NASA Astrophysics Data System (ADS)

Naydenkin, E. V.; Ratochka, I. V.; Mishin, I. P.; Lykova, O. N.

2017-12-01

Ultrafine-grained (UFG) structure with an average element size of about 0.25 µm was obtained in a near β titanium alloy under severe plastic deformation by abc pressing. It is shown that the formation of such structure greatly increases the ultimate strength of the alloy compared to its coarse-grained state (up to 1610 MPa). In addition, the UFG alloy features improved superplastic characteristics under tension at temperatures of 973-1073 K: its elongation to failure exceeds 1300% and the flow stress decreases to several MPa.

Some Effects of Nitrates on the Tensile Properties of Al 7075-T7351.

DTIC Science & Technology

1988-03-01

SORNSOIG IO 8b OFFICE SYMBOL 7aRO NA10 MDFN %1% ST% RuMEN IENT, ON NME ORGAiZtION Reerh ru (if applicable) Sc. ADDRESS (City, State and ZIP Code) 7t0 ADRES...grains in products with significant grain directionality TUS Tensile Ultimate Strength TYS Tensile Yield Strength wt Weight TABLE OF CONTENTS Page...CONFIGURATION NI A- NI 6. 44. 6.0 .1 rl il i I I APPENDIX B CONTROL SETS - TENSILE TEST DATA Contents L -T C ontro ls

A new high strength alloy for hydrogen fueled propulsion systems

NASA Technical Reports Server (NTRS)

Mcpherson, W. B.

1986-01-01

This paper describes the development of a high-strength alloy (1241 MPa ultimate and 1103 MPa yield, with little or no degradation in hydrogen) for application in advanced hydrogen-fueled rocket engines. Various compositions of the Fe-Ni-Co-Cr system with elemental additions of Cb, Ti and Al are discussed. After processing, notched tensile specimens were tested in 34.5-MPa hydrogen at room temperature, as the main screening test. The H2/air notch tensile ratio was used as the selection/rejection criterion. The most promising alloys are discussed.

Retention Strength of PMMA/UDMA-Based Crowns Bonded to Dentin: Impact of Different Coupling Agents for Pretreatment

PubMed Central

Stawarczyk, Bogna; Teuss, Simona; Eichberger, Marlis; Roos, Malgorzata; Keul, Christine

2015-01-01

Computer aided design/computer aided manufacturing (CAD/CAM) polymers for long-term dental restorations benefit from enhanced mechanical properties. However, the quantification of their bonding properties on teeth is lacking. Therefore, the aim of this study was to determine the retention strength (RS) of differently pretreated new developed polymethylmethacrylate/urethanedimethacrylate-based CAD/CAM polymer bonded on dentin. In summary, 120 human caries-free molars were prepared, and polymeric crowns were milled and pretreated (n = 20): visio.link (VL), Scotchbond Universal (SU), Monobond Plus/Heliobond (MH), Margin Bond (MB), Margin Bond mixed with acetone (1:1) (MBA) or not pretreated (CG). Half of the specimens were cemented using Variolink II and the other half with RelyX Ultimate. Specimens were stored for 24 h in distilled water and thermal cycled (5000 ×, 5 °C/55 °C). The retention load was measured and failure types were defined. RS was calculated and analyzed using both two- and one-way ANOVA with a post-hoc Scheffé-test, unpaired t-test, Kaplan–Meier with Breslow–Gehan test and chi-squared test (p < 0.05). Crowns bonded using RelyX Ultimate showed higher RS than those bonded using Variolink II. The pretreatment showed no impact on the RS. However, survival analysis within Variolink II found an impact of pretreatment. The median RS for MH was the lowest and statistically different from MB, MBA and CG. For Variolink II MH had the poorest survival as the estimated cumulative failure function of the debonded crown increased very quickly with increasing TBS. Within the RelyX Ultimate groups, no significant differences were determined. The newly developed CAD/CAM polymer showed the highest bonding properties after cementation using RelyX Ultimate. PMID:28793651

29 CFR 1926.500 - Scope, application, and definitions applicable to this subpart.

Code of Federal Regulations, 2012 CFR

2012-07-01

... protection requirements for employees performing steel erection work (except for towers and tanks) are... protection systems, except in relation to steel erection activities and the use of equipment covered by... refusal, breakage, or separation of component parts. Load refusal is the point where the ultimate strength...

29 CFR 1926.500 - Scope, application, and definitions applicable to this subpart.

Code of Federal Regulations, 2011 CFR

2011-07-01

... protection requirements for employees performing steel erection work (except for towers and tanks) are... protection systems, except in relation to steel erection activities and the use of equipment covered by... refusal, breakage, or separation of component parts. Load refusal is the point where the ultimate strength...

29 CFR 1926.500 - Scope, application, and definitions applicable to this subpart.

Code of Federal Regulations, 2010 CFR

2010-07-01

...) Fall protection requirements for employees performing steel erection work (except for towers and tanks... protection systems, except in relation to steel erection activities. (b) Definitions. Anchorage means a... component parts. Load refusal is the point where the ultimate strength is exceeded. Free fall means the act...

29 CFR 1926.500 - Scope, application, and definitions applicable to this subpart.

Code of Federal Regulations, 2013 CFR

2013-07-01

... protection requirements for employees performing steel erection work (except for towers and tanks) are... protection systems, except in relation to steel erection activities and the use of equipment covered by... refusal, breakage, or separation of component parts. Load refusal is the point where the ultimate strength...

Transforming Literacy Assessment Practices through an Action Research Professional Learning Community

ERIC Educational Resources Information Center

Grierson, Arlene L.; Woloshyn, Vera E.

2005-01-01

Researchers and educators acknowledge that early reading instruction is of critical importance, with interventions and remedial programming most effective in the primary grades. Integral to this programming are educators' abilities to assess students' reading strengths and needs, with inconsistent and/or inaccurate practices ultimately threatening…

46 CFR 72.05-20 - Stairways, ladders, and elevators.

Code of Federal Regulations, 2010 CFR

2010-10-01

... factor of safety of 4 based on the ultimate strength. (j) The stringers, treads, and all platforms and... means of an intermediate landing of rectangular or nearly rectangular shape based on the actual...) Except as further noted the provisions of this section apply to all vessels. (2) For small vessels...

46 CFR 72.05-20 - Stairways, ladders, and elevators.

Code of Federal Regulations, 2011 CFR

2011-10-01

... factor of safety of 4 based on the ultimate strength. (j) The stringers, treads, and all platforms and... means of an intermediate landing of rectangular or nearly rectangular shape based on the actual...) Except as further noted the provisions of this section apply to all vessels. (2) For small vessels...

Raspberry supplementation alleviates age-related motor dysfunction in select populations

USDA-ARS?s Scientific Manuscript database

Age-related declines in balance, muscle strength and coordination often lead to a higher incidence of falling. Among older adults, falls are the leading cause of distress, pain, injury, loss of confidence, and ultimately, loss of independence and death. Previous studies in our laboratory have demons...

Raspberry differentially improves age-related declines in psychomotor function dependent on baseline motor ability

USDA-ARS?s Scientific Manuscript database

Among older adults, falls are a leading cause of distress, pain, injury, loss of confidence, and ultimately, loss of independence and death. Previous studies in our laboratory have demonstrated that berry supplementation improves the age-related declines in balance, muscle strength, and coordination...

TRIP effect in austenitic-martensitic VNS9-Sh steel at various strain rates

NASA Astrophysics Data System (ADS)

Terent'ev, V. F.; Slizov, A. K.; Prosvirnin, D. V.

2016-10-01

The mechanical properties of austenitic-martensitic VNS9-Sh (23Kh15N5AM3-Sh) steel are studied at a static strain rate from 4.1 × 10-5 to 17 × 10-3 s-1 (0.05-20 mm/min). It is found that, as the strain rate increases, the ultimate tensile strength decreases and the physical yield strength remains unchanged (≈1400 MPa). As the strain rate increases, the yield plateau remains almost unchanged and the relative elongation decreases continuously. Because of high microplastic deformation, the conventional yield strength is lower than the physical yield strength over the entire strain rate range under study. The influence of the TRIP effect on the changes in the mechanical properties of VNS9-Sh steel at various strain rates is discussed.

Parametric Methods for Determining the Characteristics of Long-Term Metal Strength

NASA Astrophysics Data System (ADS)

Nikitin, V. I.; Rybnikov, A. I.

2018-06-01

A large number of parametric methods were proposed to calculate the characteristics of the long-term strength of metals. All of them are based on the fact that temperature and time are mutually compensating factors in the processes of metal degradation at high temperature under the action of a constant stress. The analysis of the well-known Larson-Miller, Dorn-Shcherby, Menson-Haferd, Graham-Wallace, and Trunin parametric equations is performed. The widely used Larson-Miller parameter was subjected to a detailed analysis. The application of this parameter to the calculation of ultimate long-term strength for steels and alloys is substantiated provided that the laws of exponential dependence on temperature and power dependence on strength for the heat resistance are observed. It is established that the coefficient C in the Larson- Miller equation is a characteristic of the heat resistance and is different for each material. Therefore, the use of a universal constant C = 20 in parametric calculations, as well as an a priori presetting of numerical C values for each individual group of materials, is unacceptable. It is shown in what manner it is possible to determine an exact value of coefficient C for any material of interest as well as to obtain coefficient C depending on stress in case such a dependence is manifested. At present, the calculation of long-term strength characteristics can be performed to a sufficient accuracy using Larson-Miller's parameter and its refinements described therein as well as on the condition that a linear law in logσ- P dependence is observed and calculations in the interpolation range is performed. The use of the presented recommendations makes it possible to obtain a linear parametric logσ- P dependence, which makes it possible to determine to a sufficient accuracy the values of ultimate long-term strength for different materials.

The stress corrosion resistance and the cryogenic temperature mechanical properties of annealed Nitronic 60 bar material

NASA Technical Reports Server (NTRS)

Montano, J. W. L.

1977-01-01

Ambient and cryogenic temperature mechanical properties and the ambient temperature stress corrosion properties of annealed, straightened, and centerless ground Nitronic 60 stainless steel alloy bar material are presented. The mechanical properties of longitudinal specimens were evaluated at test temperatures from ambient to liquid hydrogen. The tensile test data indicated increasing strength with decreasing temperature to -196 C. Below liquid nitrogen temperature the smooth tensile and notched tensile strengths decreased slightly while the elongation and reduction of area decreased drastically. The Charpy V-notched impact energy decreased steadily with decreasing test temperature. Stress corrosion tests were performed on longitudinal tensile specimens and transverse C-ring specimens exposed to: alternate immersion in a 3.5% NaCl bath; humidity cabinet; and a 5% salt spray atmosphere. The longitudinal tensile specimens experienced no corrosive attack. Approximately 3/4 of the transverse C-rings exposed to alternate immersion and to salt spray experienced a pitting attack on the top and bottom ends. Additional stress corrosion tests were performed on transverse tensile specimens. No failures occurred in the 90% stressed specimens exposed for 90 days in the alternate immersion and salt spray environments

The Brain Health Registry: An internet-based platform for recruitment, assessment, and longitudinal monitoring of participants for neuroscience studies.

PubMed

Weiner, Michael W; Nosheny, Rachel; Camacho, Monica; Truran-Sacrey, Diana; Mackin, R Scott; Flenniken, Derek; Ulbricht, Aaron; Insel, Philip; Finley, Shannon; Fockler, Juliet; Veitch, Dallas

2018-05-08

Recruitment, assessment, and longitudinal monitoring of participants for neuroscience studies and clinical trials limit the development of new treatments. Widespread Internet use allows data capture from participants in an unsupervised setting. The Brain Health Registry, a website and online registry, collects data from participants and their study partners. The Brain Health Registry obtains self and study partner report questionnaires and neuropsychological data, including the Cogstate Brief Battery, Lumos Labs Neurocognitive Performance Test, and MemTrax Memory Test. Participants provide informed consent before participation. Baseline and longitudinal data were obtained from nearly 57,000 and 28,000 participants, respectively. Over 18,800 participants were referred to, and nearly 1800 were enrolled in, clinical Alzheimer's disease and aging studies, including five observational studies and seven intervention trials. Online assessments of participants and study partners provide useful information at relatively low cost for neuroscience studies and clinical trials and may ultimately be used in routine clinical practice. Copyright © 2018 the Alzheimer's Association. All rights reserved.

Can Perspective-Taking Reduce Crime? Examining a Pathway Through Empathic-Concern and Guilt-Proneness

PubMed Central

Martinez, Andres G.; Stuewig, Jeffrey; Tangney, June

2015-01-01

We describe and test a theoretical model in which individual differences in perspective-taking eventuate in crime reduction. Specifically, it is hypothesized that perspective-taking propensities influence the tendency to feel empathic-concern, thereby heightening proneness for guilt, which then ultimately inhibits criminal behavior (perspective-taking → empathic-concern → guilt-proneness → crime desistance). Data from two sources were analyzed: (1) a cross-sectional college sample and (2) a longitudinal sample of jail inmates. Overall, results lend credence to this model. Perspective-taking propensities ultimately “put the brakes” on criminal behavior via an affective pathway of empathic-concern and guilt-proneness. Discussion focuses on the nature of perspective-taking, its generative role in moral emotions, as well as potential applications for crime prevention. PMID:25324328

Structure-property relationships in oxide-dispersed iron-beryllia alloys

NASA Technical Reports Server (NTRS)

Wolf, S.; Grant, N. J.

1977-01-01

Two BeO dispersed iron alloys containing about 2.5 and 5.5 v/o dispersoid were produced by attritting, internally oxidizing, and extruding dilute, prealloyed Fe-Be powders. As-extruded alloys were given various thermomechanical treatments involving room temperature swaging and annealing above and below the allotropic transformation temperature. The elevated temperature rupture strengths were measured and correlated with changes in structure; strengthening trends were examined in the light of proposed models for such strengthening. The results obtained showed that the elevated temperature strength was determined by the oxide interparticle spacing (IPS) in recrystallized material and IPS as well as prior deformation in swaged specimens. In fact, a parametric correlation was found between rupture strength values in the longitudinal direction with prestrain during swaging. The overall pattern in strength and microstructural observations were more consistent with a strength-stored energy (substructure) dependence than a strength-grain shape (grain aspect ratio) relation.

Quantitative evaluation of the mechanical strength of titanium/composite bonding using laser-generated shock waves

NASA Astrophysics Data System (ADS)

Ducousso, M.; Bardy, S.; Rouchausse, Y.; Bergara, T.; Jenson, F.; Berthe, L.; Videau, L.; Cuvillier, N.

2018-03-01

Intense acoustic shock waves were applied to evaluate the mechanical strength of structural epoxy bonds between a TA6V4 titanium alloy and a 3D woven carbon/epoxy composite material. Two bond types with different mechanical strengths were obtained from two different adhesive reticulations, at 50% and 90% of conversion, resulting in longitudinal static strengths of 10 and 39 MPa and transverse strengths of 15 and 35 MPa, respectively. The GPa shock waves were generated using ns-scale intense laser pulses and reaction principles to a confined plasma expansion. Simulations taking into account the laser-matter interaction, plasma relaxation, and non-linear shock wave propagation were conducted to aid interpretation of the experiments. Good correlations were obtained between the experiments and the simulation and between different measurement methods of the mechanical strength (normalized tests vs laser-generated shock waves). Such results open the door toward certification of structural bonding.

The dynamic behavior of mortar under impact-loading

NASA Astrophysics Data System (ADS)

Kawai, Nobuaki; Inoue, Kenji; Misawa, Satoshi; Tanaka, Kyoji; Hayashi, Shizuo; Kondo, Ken-Ichi; Riedel, Werner

2007-06-01

Concrete and mortar are the most fundamental structural material. Therefore, considerable interest in characterizing the dynamic behavior of them under impact-loading exists. In this study, plate impact experiments have been performed to determine the dynamic behavior of mortar. Longitudinal and lateral stresses have been directly measured by means of embedded polyvinylidene fluoride (PVDF) gauges up to 1 GPa. A 200 mm-cal. powder gun enable us to measure longitudinal and lateral stresses at several point from the impact surface, simultaneously. The shear strength under impact-loading has been obtained from measured longitudinal and lateral stresses. The longitudinal stress profile shows a two-wave structure. It is indicated that this structure is associated with the onset of pore compaction and failure of mortar by comparing with hydrocode simulations using an elastic-plastic damage model for concrete.

Load rating of Bibb Graves Concrete Arch Bridge.

DOT National Transportation Integrated Search

2014-07-01

To assess the strength of the Bibb Graves Concrete Arch Bridge, the Alabama Department of Transportation sponsored an : investigation by Auburn University. In one of the spans, the arches are experiencing severe longitudinal cracking from Alkali-Sili...

Structural Evaluation of Exo-Skeletal Engine Fan Blades

NASA Technical Reports Server (NTRS)

Kuguoglu, Latife; Abumeri, Galib; Chamis, Christos C.

2003-01-01

The available computational simulation capability is used to demonstrate the structural viability of composite fan blades of innovative Exo-Skeletal Engine (ESE) developed at NASA Glenn Research Center for a subsonic mission. Full structural analysis and progressive damage evaluation of ESE composite fan blade is conducted through the NASA in-house computational simulation software system EST/BEST. The results of structural assessment indicate that longitudinal stresses acting on the blade are in compression. At a design speed of 2000 rpm, pressure and suction surface outer most ply stresses in longitudinal, transverse and shear direction are much lower than the corresponding composite ply strengths. Damage is initiated at 4870 rpm and blade fracture takes place at rotor speed of 7735 rpm. Damage volume is 51 percent. The progressive damage, buckling, stress and strength results indicate that the design at hand is very sound because of the factor of safety, damage tolerance, and buckling load of 6811 rpm.

Region of Interest Correction Factors Improve Reliability of Diffusion Imaging Measures Within and Across Scanners and Field Strengths

PubMed Central

Venkatraman, Vijay K; Gonzalez, Christopher E.; Landman, Bennett; Goh, Joshua; Reiter, David A.; An, Yang; Resnick, Susan M.

2017-01-01

Diffusion tensor imaging (DTI) measures are commonly used as imaging markers to investigate individual differences in relation to behavioral and health-related characteristics. However, the ability to detect reliable associations in cross-sectional or longitudinal studies is limited by the reliability of the diffusion measures. Several studies have examined reliability of diffusion measures within (i.e. intra-site) and across (i.e. inter-site) scanners with mixed results. Our study compares the test-retest reliability of diffusion measures within and across scanners and field strengths in cognitively normal older adults with a follow-up interval less than 2.25 years. Intra-class correlation (ICC) and coefficient of variation (CoV) of fractional anisotropy (FA) and mean diffusivity (MD) were evaluated in sixteen white matter and twenty-six gray matter bilateral regions. The ICC for intra-site reliability (0.32 to 0.96 for FA and 0.18 to 0.95 for MD in white matter regions; 0.27 to 0.89 for MD and 0.03 to 0.79 for FA in gray matter regions) and inter-site reliability (0.28 to 0.95 for FA in white matter regions, 0.02 to 0.86 for MD in gray matter regions) with longer follow-up intervals were similar to earlier studies using shorter follow-up intervals. The reliability of across field strengths comparisons was lower than intra- and inter-site reliability. Within and across scanner comparisons showed that diffusion measures were more stable in larger white matter regions (> 1500 mm3). For gray matter regions, the MD measure showed stability in specific regions and was not dependent on region size. Linear correction factor estimated from cross-sectional or longitudinal data improved the reliability across field strengths. Our findings indicate that investigations relating diffusion measures to external variables must consider variable reliability across the distinct regions of interest and that correction factors can be used to improve consistency of measurement across field strengths. An important result of this work is that inter-scanner and field strength effects can be partially mitigated with linear correction factors specific to regions of interest. These data-driven linear correction techniques can be applied in cross-sectional or longitudinal studies. PMID:26146196

Longitudinal course of disease in a large cohort of myositis patients with autoantibodies recognizing the signal recognition particle

PubMed Central

Werner, Jessie L.; Albayda, Jemyma; Paik, Julie; Danoff, Sonye K.; Casciola-Rosen, Livia; Christopher-Stine, Lisa; Mammen, Andrew L.

2016-01-01

Objective Patients with immune-mediated necrotizing myopathy (IMNM) often have autoantibodies recognizing the signal recognition particle (SRP) or HMG-CoA reductase (HMGCR). Here, we studied a cohort of anti-SRP patients to identify factors associated with disease severity and clinical improvement; we also compared the severity of weakness in those with anti-SRP versus anti-HMGCR autoantibodies. Methods All anti-SRP patients in the Johns Hopkins Myositis Cohort from 2002 to 2015 were included. Longitudinal information regarding proximal muscle strength, creatine kinase (CK) levels, and immunosuppressive therapy were recorded at each visit. Univariate and multivariate multilevel regression models were used to assess prognostic factors influencing recovery. Strength in the anti-SRP patients was compared to strength in 49 previously described anti-HMGCR subjects. Results Data from 37 anti-SRP patients and 380 total clinic visits was analyzed. Younger age at onset was associated with more severe weakness at the first visit (p=0.02) and all subsequent visits (p=0.002). Only 50% of patients reached near-full or full strength after 4 years of treatment and most of these continued to have elevated CK levels. Rituximab appeared to be effective in 13 of 17 anti-SRP patients. Anti-SRP patients were significantly weaker than those with anti-HMGCR autoantibodies (−1.3 strength points, p=0.001). Conclusions Younger age at onset is associated with more severe weakness in anti-SRP myositis. Furthermore, even among anti-SRP patients whose strength improved with immunosuppression, most had ongoing disease activity as demonstrated by elevated CK levels. Finally, anti-SRP patients were significantly weaker than anti-HMGCR patients, providing evidence that these autoantibodies are associated with distinct forms of IMNM. PMID:27111848

Porcelain monolayers and porcelain/alumina bilayers reinforced by Al2O3/GdAlO3 fibers.

PubMed

Sgura, Ricardo; Medeiros, Igor Studart; Cesar, Paulo Francisco; Campos, Adeliani Almeida; Hernandes, Antonio Carlos

2012-01-01

This work tested the effect of the addition of Al(2)O(3)/GdAlO(3) longitudinal fibers in different contents to veneering porcelain of two dental all ceramic systems. Fibers (0.5 mm diameter) obtained by the Laser Heated Pedestal Growth (LHPG) method were added to bar-shaped specimens made by veneer porcelain (monolayers) or both the veneer and the core ceramic (bilayers) of two all-ceramic systems: In-Ceram Alumina-glass infiltrated alumina composite (GIA) and In-Ceram 2000 AL Cubes-alumina polycrystal (AP) (VITA Zahnfabrik). The longitudinal fibers were added to veneering porcelain (VM7) in two different proportions: 10 or 17 vol%. The bars were divided into nine experimental conditions (n=10) according to material used: VM7 porcelain monolayers, VM7/GIA, VM7/AP; and according to the amount of fibers within the porcelain layer: no fibers, 10 vol% or 17 vol%. After grinding and polishing the specimens were submitted to a three point bending test (crosshead speed = 0.5 mm/min) with porcelain positioned at tensile side. Data were analyzed by means of one-way ANOVA and a Tukey's test (α=5%). Scanning electronic microscopy (SEM) was conducted for fractographic analysis. Regarding the groups without fiber addition, VM7/AP showed the highest flexural strength (MPa), followed by VM7/GIA and VM7 monolayers. The addition of fibers led to a numerical increase in flexural strength for all groups. For VM7/GIA bilayers the addition of 17 vol% of fibers resulted in a significant 48% increase in the flexural strength compared to the control group. Fractographic analysis revealed that the crack initiation site was in porcelain at the tensile surface. Cracks also propagated between fibers before heading for the alumina core. The addition of 17 vol% of Al(2)O(3)/GdAlO(3) longitudinal fibers to porcelain/glass infiltrated alumina bilayers significantly improved its flexural strength. 10 vol% or 17 vol% of fibers inclusion increased the flexural strength for all groups. Copyright © 2011 Elsevier Ltd. All rights reserved.

Site-specific, adult bone benefits attributed to loading during youth: A preliminary longitudinal analysis.

PubMed

Scerpella, Tamara A; Bernardoni, Brittney; Wang, Sijian; Rathouz, Paul J; Li, Quefeng; Dowthwaite, Jodi N

2016-04-01

We examined site-specific bone development in relation to childhood and adolescent artistic gymnastics exposure, comparing up to 10years of prospectively acquired longitudinal data in 44 subjects, including 31 non-gymnasts (NON) and 13 gymnasts (GYM) who participated in gymnastics from pre-menarche to ≥1.9years post-menarche. Subjects underwent annual regional and whole-body DXA scans; indices of bone geometry and strength were calculated. Anthropometrics, physical activity, and maturity were assessed annually, coincident with DXA scans. Non-linear mixed effect models centered growth in bone outcomes at menarche and adjusted for menarcheal age, height, and non-bone fat-free mass to evaluate GYM-NON differences. A POST-QUIT variable assessed the withdrawal effect of quitting gymnastics. Curves for bone area, mass (BMC), and strength indices were higher in GYM than NON at both distal radius metaphysis and diaphysis (p<0.0001). At the femoral neck, greater GYM BMC (p<0.01), narrower GYM endosteal diameter (p<0.02), and similar periosteal width (p=0.09) yielded GYM advantages in narrow neck cortical thickness and buckling ratio (both p<0.001; lower BR indicates lower fracture risk). Lumbar spine and sub-head BMC were greater in GYM than NON (p<0.036). Following gymnastics cessation, GYM slopes increased for distal radius diaphysis parameters (p≤0.01) and for narrow neck BR (p=0.02). At the distal radius metaphysis, GYM BMC and compressive strength slopes decreased, as did slopes for lumbar spine BMC, femoral neck BMC, and narrow neck cortical thickness (p<0.02). In conclusion, advantages in bone mass, geometry, and strength at multiple skeletal sites were noted across growth and into young adulthood in girls who participated in gymnastics loading to at least 1.9years post-menarche. Following gymnastics cessation, advantages at cortical bone sites improved or stabilized, while advantages at corticocancellous sites stabilized or diminished. Additional longitudinal observation is necessary to determine whether residual loading benefits enhance lifelong skeletal strength. Copyright © 2016 Elsevier Inc. All rights reserved.

The Effect of Artificial Aging on the Tensile Properties of Alclad 24S-T and 24S-T Aluminum Alloy

NASA Technical Reports Server (NTRS)

Kotanchik, Joseph N.; Woods, Walter; Zender, George W.

1943-01-01

An experimental study was made to determine the effect of artificial aging on the tensile properties of alclad 24S-T and 24S-T aluminum-alloy sheet material. The results of the tests show that certain combinations of aging time and temperature cause a marked increase in the yield strength and a small increase in the ultimate strength; these increases are accompanied by a very large decrease in elongation. A curve is presented that shows the maximum yield strengths that can be obtained by aging this material at various combinations of time and temperature. The higher values of yield stress are obtained in material aged at relatively longer times and lower temperatures.

Structure and mechanical properties of coatings fabricated by nonvacuum electron beam cladding of Ti-Ta-Zr powder mixtures

NASA Astrophysics Data System (ADS)

Samoylenko, Vitaliy V.; Lenivtseva, Olga G.; Polyakov, Igor A.; Laptev, Ilya S.

2015-10-01

In this paper structural investigations and mechanical tests of Ti-Ta-Zr coatings obtained on surfaces of cp-titanium workpieces were carried out. It was found that the coatings had a dendrite structure; investigations at high-power magnifications revealed a platelet structure. An increase of tantalum concentration led to refinement of structural components. The microhardness level of all coatings, excepting a specimen with the maximum tantalum content, was 370 HV. The microhardness of this coating reached 400 HV. The ultimate tensile strength of cladded layers varied from 697 to 947 MPa. Adhesion tests showed that bimetallic composites were characterized by high bond strength of cladded layers to the substrate, which exceeded cp-titanium strength characteristics.

Method of forming biaxially textured alloy substrates and devices thereon

DOEpatents

Goyal, Amit; Specht, Eliot D.; Kroeger, Donald M.; Paranthaman, Mariappan

1999-01-01

Specific alloys, in particular Ni-based alloys, that can be biaxially textured, with a well-developed, single component texture are disclosed. These alloys have a significantly reduced Curie point, which is very desirable from the point of view of superconductivity applications. The biaxially textured alloy substrates also possess greatly enhanced mechanical properties (yield strength, ultimate tensile strength) which are essential for most applications, in particular, superconductors. A method is disclosed for producing complex multicomponent alloys which have the ideal physical properties for specific applications, such as lattice parameter, degree of magnetism and mechanical strength, and which cannot be fabricated in textured form. In addition, a method for making ultra thin biaxially textured substrates with complex compositions is disclosed.

Tension Strength, Failure Prediction and Damage Mechanisms in 2D Triaxial Braided Composites with Notch

NASA Technical Reports Server (NTRS)

Norman, Timothy L.; Anglin, Colin

1995-01-01

The unnotched and notched (open hole) tensile strength and failure mechanisms of two-dimensional (2D) triaxial braided composites were examined. The effect of notch size and notch position were investigated. Damage initiation and propagation in notched and unnotched coupons were also examined. Theory developed to predict the normal stress distribution near an open hole and failure for tape laminated composites was evaluated for its applicability to 2D triaxial braided textile composite materials. Four different fiber architectures were considered; braid angle, yarn and braider size, percentage of longitudinal yarns and braider angle varied. Tape laminates equivalent to textile composites were also constructed for comparison. Unnotched tape equivalents were stronger than braided textiles but exhibited greater notch sensitivity. Notched textiles and tape equivalents have roughly the same strength at large notch sizes. Two common damage mechanisms were found: braider yarn cracking and near notch longitudinal yarn splitting. Cracking was found to initiate in braider yarns in unnotched and notched coupons, and propagate in the direction of the braider yarns until failure. Damage initiation stress decreased with increasing braid angle. No significant differences in prediction of near notch strain between textile and tape equivalents could be detected for small braid angle, but the correlations were weak for textiles with large braid angle. Notch strength could not be predicted using existing anisotropic theory for braided textiles due to their insensitivity to notch.

Psychiatry in the Harvard Medical School-Cambridge Integrated Clerkship: an innovative, year-long program.

PubMed

Griswold, Todd; Bullock, Christopher; Gaufberg, Elizabeth; Albanese, Mark; Bonilla, Pedro; Dvorak, Ramona; Epelbaum, Claudia; Givon, Lior; Kueppenbender, Karsten; Joseph, Robert; Boyd, J Wesley; Shtasel, Derri

2012-09-01

The authors present what is to their knowledge the first description of a model for longitudinal third-year medical student psychiatry education. A longitudinal, integrated psychiatric curriculum was developed, implemented, and sustained within the Harvard Medical School-Cambridge Integrated Clerkship. Curriculum elements include longitudinal mentoring by attending physicians in an outpatient psychiatry clinic, exposure to the major psychotherapies, psychopharmacology training, acute psychiatry "immersion" experiences, and a variety of clinical and didactic teaching sessions. The longitudinal psychiatry curriculum has been sustained for 8 years to-date, providing effective learning as demonstrated by OSCE scores, NBME shelf exam scores, written work, and observed clinical work. The percentage of students in this clerkship choosing psychiatry as a residency specialty is significantly greater than those in traditional clerkships at Harvard Medical School and greater than the U.S. average. Longitudinal integrated clerkship experiences are effective and sustainable; they offer particular strengths and opportunities for psychiatry education, and may influence student choice of specialty.

Responsiveness, Sensitivity, and Minimally Detectable Difference of the Graded and Redefined Assessment of Strength, Sensibility, and Prehension, Version 1.0.

PubMed

Kalsi-Ryan, Sukhvinder; Beaton, Dorcas; Ahn, Henry; Askes, Heather; Drew, Brian; Curt, Armin; Popovic, Milos R; Wang, Justin; Verrier, Mary C; Fehlings, Michael G

2016-02-01

As spinal cord injury (SCI) trials begin to involve subjects with acute cervical SCI, establishing the property of an upper limb outcome measure to detect change over time is critical for its usefulness in clinical trials. The objectives of this study were to define responsiveness, sensitivity, and minimally detectable difference (MDD) of the Graded Redefined Assessment of Strength, Sensibility, and Prehension (GRASSP). An observational, longitudinal study was conducted. International Standards of Neurological Classification of SCI (ISNCSCI), GRASSP, Capabilities of Upper Extremity Questionnaire (CUE-Q), and Spinal Cord Independence Measure (SCIM) were administered 0-10 days, 1, 3, 6, and 12 months post-injury. Standardized Response Means (SRM) for GRASSP and ISNCSCI measures were calculated. Longitudinal construct validity was calculated using Pearson correlation coefficients. Smallest real difference for all subtests was calculated to define the MDD values for all GRASSP subtests. Longitudinal construct validity demonstrated GRASSP and all external measures to be responsive to neurological change for 1 year post-injury. SRM values for the GRASSP subtests ranged from 0.25 to 0.85 units greater than that for ISNCSCI strength and sensation, SCIM-SS, and CUE-Q. MDD values for GRASSP subtests ranged from 2-5 points. GRASSP demonstrates good responsiveness and excellent sensitivity that is superior to ISNCSCI and SCIM III. MDD values are useful in the evaluation of interventions in both clinical and research settings. The responsiveness and sensitivity of GRASSP make it a valuable condition-specific measure in tetraplegia, where changes in upper limb neurological and functional outcomes are essential for evaluating the efficacy of interventions.

Estimates of the effective compressive strength

NASA Astrophysics Data System (ADS)

Goldstein, R. V.; Osipenko, N. M.

2017-07-01

One problem encountered when determining the effective mechanical properties of large-scale objects, which requires calculating their strength in processes of mechanical interaction with other objects, is related to the possible variability in their local properties including those due to the action of external physical factors. Such problems comprise the determination of the effective strength of bodies one of whose dimensions (thickness) is significantly less than the others and whose properties and/or composition can vary with the thickness. A method for estimating the effective strength of such bodies is proposed and illustrated with example of ice cover strength under longitudinal compression with regard to a partial loss of the ice bearing capacity in deformation. The role of failure localization processes is shown. It is demonstrated that the proposed approach can be used in other problems of fracture mechanics.

Longitudinal development of manual motor ability in autism spectrum disorder from childhood to mid-adulthood relates to adaptive daily living skills.

PubMed

Travers, Brittany G; Bigler, Erin D; Duffield, Tyler C; Prigge, Molly D B; Froehlich, Alyson L; Lange, Nicholas; Alexander, Andrew L; Lainhart, Janet E

2017-07-01

Many individuals with autism spectrum disorder (ASD) exhibit motor difficulties, but it is unknown whether manual motor skills improve, plateau, or decline in ASD in the transition from childhood into adulthood. Atypical development of manual motor skills could impact the ability to learn and perform daily activities across the life span. This study examined longitudinal grip strength and finger tapping development in individuals with ASD (n = 90) compared to individuals with typical development (n = 56), ages 5 to 40 years old. We further examined manual motor performance as a possible correlate of current and future daily living skills. The group with ASD demonstrated atypical motor development, characterized by similar performance during childhood but increasingly poorer performance from adolescence into adulthood. Grip strength was correlated with current adaptive daily living skills, and Time 1 grip strength predicted daily living skills eight years into the future. These results suggest that individuals with ASD may experience increasingly more pronounced motor difficulties from adolescence into adulthood and that manual motor performance in ASD is related to adaptive daily living skills. © 2016 John Wiley & Sons Ltd.

Parametric Analysis and Safety Concepts of CWR Track Buckling.

DOT National Transportation Integrated Search

1993-12-01

The report presents a comprehensive study of continuous welded rail (CWR) track buckling strength as influenced by the range of all key parameters such as the lateral, torsional and longitudinal resistance, vehicle loads, etc. The parametric study pr...

Mechanical properties of as-cast and heat-treated ZA-27 alloy/short glass fiber composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sharma, S.C.; Girish, B.M.; Satish, B.M.

1998-02-01

This paper reports on the mechanical properties of as-cast and heat-treated ZA-27 alloy composites reinforced with glass fibers from 1 to 5 wt%. The composites were fabricated using the Compocasting method, in which short glass fibers were introduced into the vortex created in the molten alloy through an impeller rotated at 500 rpm. The molten mass was thoroughly stirred and poured into permanent molds and squeezed under pressure. The specimens were heat treated at 320 C for 1, 2, 3, and 4 h. The tests on the as-cast composites revealed that as the glass content in the composites was increased,more » the ultimate tensile strength (UTS), compressive strength, and hardness of the composite increased, while the ductility and impact strength were decreased. Heat treatment was found to improve significantly the ductility, compressive strength, and impact strength, while the hardness and UTS were reduced. This paper discusses the behavior of these composites.« less

Investigation into the effect of some additives on the mechanical strength, quality and thermal conductivity of clay bricks

NASA Astrophysics Data System (ADS)

Zaid, Adnan I. O.; Qandil, A.; Qattous, M. A. A.

2016-08-01

It was repeatedly reported that the clay bricks industry in Jordan is facing both weak mechanical strength and poor quality which caused marketing problems where it is expected to serve the increasing demand of housing in the country especially after the political crises in the neighboring countries Iraq and Syria. It is therefore anticipated that improvement of the mechanical strength and quality of the produced clay evaluation of the brick industry in Jordan is worth investigating. In this paper, theoretical and experimental investigation obtained from field visits to the factories producing clay bricks were carried out. Furthermore, the effect of using some additives from locally available materials namely: Battn El-Ghoul Clay, Suweileh sand and Olive extracts on the mechanical strength, thermal conductivity and surface quality of the produced bricks is investigated and discussed. The experimental results indicated that thermal conductivity, color and durability were all enhanced and the ultimate compressive strength was reduced but remained higher than the acceptable value for brickwork.

29 CFR 1926.500 - Scope, application, and definitions applicable to this subpart.

Code of Federal Regulations, 2014 CFR

2014-07-01

... CC of this part. (iii) Fall protection requirements for employees performing steel erection work... for training in the installation and use of fall protection systems, except in relation to steel... component parts. Load refusal is the point where the ultimate strength is exceeded. Free fall means the act...

46 CFR 108.550 - Survival craft launching and recovery arrangements: General.

Code of Federal Regulations, 2011 CFR

2011-10-01

... must be designed, based on the ultimate strength of the construction material, to be at least 4.5 times...-MOBILE OFFSHORE DRILLING UNITS DESIGN AND EQUIPMENT Lifesaving Equipment § 108.550 Survival craft... approved under approval series 160.132, with a winch approved under approval series 160.115. Each launching...

46 CFR 108.550 - Survival craft launching and recovery arrangements: General.

Code of Federal Regulations, 2010 CFR

2010-10-01

... must be designed, based on the ultimate strength of the construction material, to be at least 4.5 times...-MOBILE OFFSHORE DRILLING UNITS DESIGN AND EQUIPMENT Lifesaving Equipment § 108.550 Survival craft... approved under approval series 160.132, with a winch approved under approval series 160.115. Each launching...

14 CFR 29.685 - Control system details.

Code of Federal Regulations, 2012 CFR

2012-01-01

... ultimate bearing strength of the softest material used as a bearing: (1) 3.33 for push-pull systems other... must be means to prevent the slapping of cables or tubes against other parts. (d) Cable systems must be designed as follows: (1) Cables, cable fittings, turnbuckles, splices, and pulleys must be of an acceptable...

14 CFR 29.685 - Control system details.

Code of Federal Regulations, 2011 CFR

2011-01-01

... ultimate bearing strength of the softest material used as a bearing: (1) 3.33 for push-pull systems other... must be means to prevent the slapping of cables or tubes against other parts. (d) Cable systems must be designed as follows: (1) Cables, cable fittings, turnbuckles, splices, and pulleys must be of an acceptable...

14 CFR 29.685 - Control system details.

Code of Federal Regulations, 2014 CFR

2014-01-01

... ultimate bearing strength of the softest material used as a bearing: (1) 3.33 for push-pull systems other... must be means to prevent the slapping of cables or tubes against other parts. (d) Cable systems must be designed as follows: (1) Cables, cable fittings, turnbuckles, splices, and pulleys must be of an acceptable...

46 CFR 32.63-20 - Hull structure-B/ALL.

Code of Federal Regulations, 2011 CFR

2011-10-01

... condition such that the forward rake bulkhead rests upon a pinnacle at the water surface, the maximum hull bending stress shall not exceed the following limits: (1) Independent tanks may be installed in such a... stress shall not exceed either 50 percent of the minimum ultimate tensile strength of the material or 70...

46 CFR 32.63-20 - Hull structure-B/ALL.

Code of Federal Regulations, 2010 CFR

2010-10-01

... bending stress shall not exceed the following limits: (1) Independent tanks may be installed in such a... stress shall not exceed either 50 percent of the minimum ultimate tensile strength of the material or 70... reduction in hull stress when independent tanks are installed in such a manner as to contribute to the...

A Carbon Nanotube Cable for a Space Elevator

ERIC Educational Resources Information Center

Bochnícek, Zdenek

2013-01-01

In this paper the mechanical properties of carbon nanotubes are discussed in connection with the possibility to use them for the construction of a space elevator. From the fundamental information about the structure of a carbon nanotube and the chemical bond between carbon atoms, Young's modulus and the ultimate tensile strength are…

49 CFR 238.219 - Truck-to-car-body attachment.

Code of Federal Regulations, 2011 CFR

2011-10-01

... 49 Transportation 4 2011-10-01 2011-10-01 false Truck-to-car-body attachment. 238.219 Section 238... I Passenger Equipment § 238.219 Truck-to-car-body attachment. Passenger equipment shall have a truck-to-car-body attachment with an ultimate strength sufficient to resist without failure the following...

49 CFR 238.219 - Truck-to-car-body attachment.

Code of Federal Regulations, 2012 CFR

2012-10-01

... 49 Transportation 4 2012-10-01 2012-10-01 false Truck-to-car-body attachment. 238.219 Section 238... I Passenger Equipment § 238.219 Truck-to-car-body attachment. Passenger equipment shall have a truck-to-car-body attachment with an ultimate strength sufficient to resist without failure the following...

49 CFR 238.219 - Truck-to-car-body attachment.

Code of Federal Regulations, 2010 CFR

2010-10-01

... 49 Transportation 4 2010-10-01 2010-10-01 false Truck-to-car-body attachment. 238.219 Section 238... I Passenger Equipment § 238.219 Truck-to-car-body attachment. Passenger equipment shall have a truck-to-car-body attachment with an ultimate strength sufficient to resist without failure the following...

49 CFR 238.219 - Truck-to-car-body attachment.

Code of Federal Regulations, 2013 CFR

2013-10-01

... 49 Transportation 4 2013-10-01 2013-10-01 false Truck-to-car-body attachment. 238.219 Section 238... I Passenger Equipment § 238.219 Truck-to-car-body attachment. Passenger equipment shall have a truck-to-car-body attachment with an ultimate strength sufficient to resist without failure the following...

49 CFR 238.219 - Truck-to-car-body attachment.

Code of Federal Regulations, 2014 CFR

2014-10-01

... 49 Transportation 4 2014-10-01 2014-10-01 false Truck-to-car-body attachment. 238.219 Section 238... I Passenger Equipment § 238.219 Truck-to-car-body attachment. Passenger equipment shall have a truck-to-car-body attachment with an ultimate strength sufficient to resist without failure the following...

Local Strain Measurement of Kevlar Strand with Fiber Optic Bragg Grating

NASA Technical Reports Server (NTRS)

Banks, Curtis E.; Grant, Joseph; Russell, Sam; Arnett, Shawn

2008-01-01

1987 DuPont manufactured 4560 denier Kevlar/Epoxy Strands were instrumented with nine and three sensors each. Stress tests were performed at 30,45,60,70 and 80% of ultimate strength with dwell times of 10,000 seconds. FBG showed uneven stress levels which is contrary to conventional observation.

Local strain measurement of Kevlar strand with fiber optic Bragg grating

NASA Astrophysics Data System (ADS)

Banks, Curtis E.; Grant, Joseph; Russell, Sam; Arnett, Shawn

2008-03-01

1987 DuPont manufactured 4560 denier Kevlar/Epoxy Strands were instrumented with nine and three sensors each. Stress tests were performed at 30,45,60,70 and 80% of ultimate strength with dwell times of 10,000 seconds. FBG showed uneven stress levels which is contrary to conventional observation.

30 CFR 77.403-1 - Mobile equipment; rollover protective structures (ROPS).

Code of Federal Regulations, 2010 CFR

2010-07-01

... WORK AREAS OF UNDERGROUND COAL MINES Safeguards for Mechanical Equipment § 77.403-1 Mobile equipment... surface coal mines or the surface work areas of underground coal mines shall be provided with rollover... complying with paragraph (d) (1) (iii) (A) of this section. Stresses shall not exceed the ultimate strength...

30 CFR 77.403-1 - Mobile equipment; rollover protective structures (ROPS).

Code of Federal Regulations, 2011 CFR

2011-07-01

... WORK AREAS OF UNDERGROUND COAL MINES Safeguards for Mechanical Equipment § 77.403-1 Mobile equipment... surface coal mines or the surface work areas of underground coal mines shall be provided with rollover... complying with paragraph (d) (1) (iii) (A) of this section. Stresses shall not exceed the ultimate strength...

Science Indicators, 1972.

ERIC Educational Resources Information Center

National Science Foundation, Washington, DC. National Science Board.

In this report the National Science Board presents the first results from a newly initiated effort to develop indicators of the state of the scientific enterprise in the Unite States. The ultimate goal of this effort is a set of indices which will reveal the strengths and weaknesses of U.S. science and technology, in terms of the capacity and…

46 CFR 32.63-20 - Hull structure-B/ALL.

Code of Federal Regulations, 2012 CFR

2012-10-01

... bending stress shall not exceed the following limits: (1) Independent tanks may be installed in such a... stress shall not exceed either 50 percent of the minimum ultimate tensile strength of the material or 70... reduction in hull stress when independent tanks are installed in such a manner as to contribute to the...

46 CFR 32.63-20 - Hull structure-B/ALL.

Code of Federal Regulations, 2014 CFR

2014-10-01

... bending stress shall not exceed the following limits: (1) Independent tanks may be installed in such a... stress shall not exceed either 50 percent of the minimum ultimate tensile strength of the material or 70... reduction in hull stress when independent tanks are installed in such a manner as to contribute to the...

46 CFR 32.63-20 - Hull structure-B/ALL.

Code of Federal Regulations, 2013 CFR

2013-10-01

... bending stress shall not exceed the following limits: (1) Independent tanks may be installed in such a... stress shall not exceed either 50 percent of the minimum ultimate tensile strength of the material or 70... reduction in hull stress when independent tanks are installed in such a manner as to contribute to the...

Method of Construction for Geopolymer Soil Stabilized Platforms

DTIC Science & Technology

2017-12-20

of the geopolymer core compressive strength tests. The degree of seepage varied from pavement to pavement due to mix design and additives, ultimately...Department of the Army position unless so designated by other authorized documents. DESTROY THIS REPORT WHEN NO LONGER NEEDED. DO NOT RETURN IT TO THE...20 3.5 Test pavement ................................................................................................ 23

Effect of particle Alignment on mechanical properties of neat cellulose nanocrystal films

Treesearch

Alexander B. Reising; Robert J. Moon; Jeffrey P. Youngblood

2012-01-01

Shear-based film casting methods were used to cast neat films from wood-based cellulose nanocrystal (CNC) suspensions. The degree of CNC alignment in dried films was characterized using the Hermans order parameter (S), and the film elastic modulus (E), ultimate tensile strength (σf ), elongation at failure (εf...

Yahoo! Cataloging the Web.

ERIC Educational Resources Information Center

Callery, Anne

The Internet has the potential to be the ultimate information resource, but it needs to be organized in order to be useful. This paper discusses how the subject guide, "Yahoo!" is different from most web search engines, and how best to search for information on Yahoo! The strength in Yahoo! lies in the subject hierarchy. Advantages to…

Fracture mechanics and parapsychology

NASA Astrophysics Data System (ADS)

Cherepanov, G. P.

2010-08-01

The problem of postcritical deformation of materials beyond the ultimate strength is considered a division of fracture mechanics. A simple example is used to show the relationship between this problem and parapsychology, which studies phenomena and processes where the causality principle fails. It is shown that the concept of postcritical deformation leads to problems with no solution

Mechanical characterization of bulk Sylgard 184 for microfluidics and microengineering

NASA Astrophysics Data System (ADS)

Johnston, I. D.; McCluskey, D. K.; Tan, C. K. L.; Tracey, M. C.

2014-03-01

Polydimethylsiloxane (PDMS) elastomers are extensively used for soft lithographic replication of microstructures in microfluidic and micro-engineering applications. Elastomeric microstructures are commonly required to fulfil an explicit mechanical role and accordingly their mechanical properties can critically affect device performance. The mechanical properties of elastomers are known to vary with both curing and operational temperatures. However, even for the elastomer most commonly employed in microfluidic applications, Sylgard 184, only a very limited range of data exists regarding the variation in mechanical properties of bulk PDMS with curing temperature. We report an investigation of the variation in the mechanical properties of bulk Sylgard 184 with curing temperature, over the range 25 °C to 200 °C. PDMS samples for tensile and compressive testing were fabricated according to ASTM standards. Data obtained indicates variation in mechanical properties due to curing temperature for Young's modulus of 1.32-2.97 MPa, ultimate tensile strength of 3.51-7.65 MPa, compressive modulus of 117.8-186.9 MPa and ultimate compressive strength of 28.4-51.7 GPa in a range up to 40% strain and hardness of 44-54 ShA.

Microstructure and Mechanical Property of 12Cr Oxide Dispersion Strengthened Steel

NASA Astrophysics Data System (ADS)

Xu, Haijian; Lu, Zheng; Jia, Chunyan; Gao, Hao; Liu, Chunming

2016-03-01

Nanostructured oxide dispersion strengthened (ODS) steels with nominal compositions (wt%): Fe-12Cr-2W-0.3Ti-0.3Y2O3 were produced by mechanical alloying and hot isostatic pressing. The microstructure was characterized by means of electron microscopy (EBSD, TEM and HRTEM) and the hardness and the tensile properties at different temperatures were measured. The results showed that the ultimate tensile strength of the fabricated 12Cr-ODS steel reached nearly 1,100 MPa at room temperature and maintained around 340 MPa at 700°C. Nano-oxide particles with size ranging from several nm to 30 nm and the number density was 3.6 × 1020/m3 were observed by TEM. Following heat treatment, including normalizing at 1,100°C for 1 h and tempering at 750°C for 2 h, the average grain size was a little decreased. The number of nano-oxide particles increased and the number density was 8.9 × 1020/m3. Specimens showed much higher ductility and there was a slight increase of ultimate tensile strength and Vickers hardness at the same time.

Effects of ion irradiation on the mechanical properties of several polymers

NASA Astrophysics Data System (ADS)

Sasuga, Tsuneo; Kawanishi, Shunichi; Nishii, Masanobu; Seguchi, Tadao; Kohno, Isao

The effects of high-energy ion irradiation (8 MeV protons, 30 MeV He 2+, 80 MeV C 4+, and N 4+) on the tensile properties of polymers were studied under conditions in which ions should pass completely through the specimen and the results were compared with 2 MeV electron irradiation effects. Experiments were carried out on polymers having various constituents and molecular structures, i.e. eight aliphatic polymers and four aromatic polymers. In the aliphatic polymers studied (PE, PP, PVdF, ETFE, EVA, nylon-6, EPDM, and PE-TPE), there was scarcely any difference in the dose dependence of the tensile strength and ultimate elongation between proton and electron irradiation. In aromatic polymers (PET, PES, U-PS, and U-polymer), however, the decrements in the tensile strength and ultimate elongation vs proton dose were less than those for electron irradiation. In heavy-ion irradiation, the radiation damage of PE (an aliphatic polymer) decreased with increase of LET, but no obvious LET effects were observed in PES (an aromatic polymer).

Thermo-mechanical treatment of low-cost alloy Ti-4.5Al-6.9Cr-2.3Mn and microstructure and mechanical characteristics

NASA Astrophysics Data System (ADS)

Chen, Guangyao; Kang, Juyun; Wang, Shusen; Wang, Shihua; Lu, Xionggang; Li, Chonghe

2018-04-01

In this study, the thermo-mechanical treatment process for low-cost Ti-4.5Al-6.9Cr-2.3Mn alloy were designed on the basis of assessment of Ti-Al-Cr-Mn thermodynamic system. The microstructure and mechanical properties of Ti-4.5Al-6.9Cr-2.3Mn forging and sheet were investigated by using the OM, SEM and universal tensile testing machine. The results show that both the forging and sheet were consisted of α + β phase, which is consistent with the expectation, and no element Cr and Mn existed in the grain boundaries of the sheet after quenching, and the C14 laves phase was not detected. The average ultimate tensile strength (σ b), 0.2% proof strength (σ 0.2) and elongation (EI) of alloy sheet after quenching can reach 1059 MPa, 1051 MPa and 24.6 Pct., respectively. Moreover, the average ultimate tensile strength of Ti-4.5Al-6.9Cr-2.3Mn forgings can reach 1599 MPa and the average elongation can reach 11.2 Pct., and a more excellent property of Ti-4.5Al-6.9Cr-2.3Mn forging is achieved than that of TC4 forging. It provides a theoretical support for further developing this low-cost alloy.

Effects of different etching methods and bonding procedures on shear bond strength of orthodontic metal brackets applied to different CAD/CAM ceramic materials.

PubMed

Buyuk, S Kutalmış; Kucukekenci, Ahmet Serkan

2018-03-01

To investigate the shear bond strength (SBS) of orthodontic metal brackets applied to different types of ceramic surfaces treated with different etching procedures and bonding agents. Monolithic CAD/CAM ceramic specimens (N = 120; n = 40 each group) of feldspathic ceramic Vita Mark II, resin nanoceramic Lava Ultimate, and hybrid ceramic Vita Enamic were fabricated (14 × 12 × 3 mm). Ceramic specimens were separated into four subgroups (n = 10) according to type of surface treatment and bonding onto the ceramic surface. Within each group, four subgroups were prepared by phosphoric acid, hydrofluoric acid, Transbond XT primer, and Clearfill Ceramic primer. Mandibular central incisor metal brackets were bonded with light-cure composite. The SBS data were analyzed using three-way analysis of variance (ANOVA) and Tukey HSD tests. The highest SBS was found in the Vita Enamic group, which is a hybrid ceramic, etched with hydrofluoric acid and applied Transbond XT Adhesive primer (7.28 ± 2.49 MPa). The lowest SBS was found in the Lava Ultimate group, which is a resin nano-ceramic etched with hydrofluoric acid and applied Clearfill ceramic primer (2.20 ± 1.21 MPa). CAD/CAM material types and bonding procedures affected bond strength ( P < .05), but the etching procedure did not ( P > .05). The use of Transbond XT as a primer bonding agent resulted in higher SBS.

Strength of inserts in titanium alloy machining

NASA Astrophysics Data System (ADS)

Kozlov, V.; Huang, Z.; Zhang, J.

2016-04-01

In this paper, a stressed state of a non-worn cutting wedge in a machined titanium alloy (Ti6Al2Mo2Cr) is analyzed. The distribution of contact loads on the face of a cutting tool was obtained experimentally with the use of a ‘split cutting tool’. Calculation of internal stresses in the indexable insert made from cemented carbide (WC8Co) was carried out with the help of ANSYS 14.0 software. Investigations showed that a small thickness of the cutting insert leads to extremely high compressive stresses near the cutting edge, stresses that exceed the ultimate compressive strength of cemented carbide. The face and the base of the insert experience high tensile stresses, which approach the ultimate tensile strength of cemented carbide and increase a probability of cutting insert destruction. If the thickness of the cutting insert is bigger than 5 mm, compressive stresses near the cutting edge decrease, and tensile stresses on the face and base decrease to zero. The dependences of the greatest normal and tangential stresses on thickness of the cutting insert were found. Abbreviation and symbols: m/s - meter per second (cutting speed v); mm/r - millimeter per revolution (feed rate f); MPa - mega Pascal (dimension of specific contact loads and stresses); γ - rake angle of the cutting tool [°] α - clearance angle of the sharp cutting tool [°].

Utilization of the Generalized Method of Cells to Analyze the Deformation Response of Laminated Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Goldberg, Robert K.

2012-01-01

In order to practically utilize ceramic matrix composites in aircraft engine components, robust analysis tools are required that can simulate the material response in a computationally efficient manner. The MAC/GMC software developed at NASA Glenn Research Center, based on the Generalized Method of Cells micromechanics method, has the potential to meet this need. Utilizing MAC/GMC, the effective stiffness properties, proportional limit stress and ultimate strength can be predicted based on the properties and response of the individual constituents. In this paper, the effective stiffness and strength properties for a representative laminated ceramic matrix composite with a large diameter fiber are predicted for a variety of fiber orientation angles and laminate orientations. As part of the analytical study, methods to determine the in-situ stiffness and strength properties of the constituents required to appropriately simulate the effective composite response are developed. The stiffness properties of the representative composite have been adequately predicted for all of the fiber orientations and laminate configurations examined in this study. The proportional limit stresses and strains and ultimate stresses and strains were predicted with varying levels of accuracy, depending on the laminate orientation. However, for the cases where the predictions did not have the desired level of accuracy, the specific issues related to the micromechanics theory were identified which could lead to difficulties that were encountered that could be addressed in future work.

Microstructural evolution and mechanical properties of a low alloy high strength Ni-Cr-Mo-V steel during heat treatment process

NASA Astrophysics Data System (ADS)

Wu, C.; Han, S.

2018-05-01

In order to obtain an optimal heat treatment for a low alloy high strength Ni-Cr-Mo-V steel, the microstructural evolution and mechanical properties of the material were studied. For this purpose, a series of quenching and temper experiments were carried out. The results showed that the effects of tempering temperature, time, original microstructure on the microstructural evolution and final properties were significant. The martensite can be completely transformed into the tempered lath structure. The width and length of the lath became wider and shorter, respectively with increasing temperature and time. The amount and size of the precipitates increased with temperature and time. The yield strength (YS), ultimate tensile strength (UTS) and hardness decreased with temperature and time, but the reduction in area (Z), elongation (E) and impact toughness displayed an opposite trend, which was related to the morphological evolution of the lath tempered structure.

An investigation of the compressive strength of Kevlar 49/epoxy composites

NASA Technical Reports Server (NTRS)

Kulkarni, S. V.; Rosen, B. W.; Rice, J. S.

1975-01-01

Tests were performed to evaluate the effect of a wide range of variables including matrix properties, interface properties, fiber prestressing, secondary reinforcement, and others on the ultimate compressive strength of Kevlar 49/epoxy composites. Scanning electron microscopy is used to assess the resulting failure surfaces. In addition, a theoretical study is conducted to determine the influence of fiber anisotropy and lack of perfect bond between fiber and matrix on the shear mode microbuckling. The experimental evaluation of the effect of various constituent and process characteristics on the behavior of these unidirectional composites in compression did not reveal any substantial increase in strength. However, theoretical evaluations indicate that the high degree of fiber anisotropy results in a significant drop in the predicted stress level for internal instability. Scanning electron microscope data analysis suggests that internal fiber failure and smooth surface debonding could be responsible for the measured low compressive strengths.

The Effect of Scale Dependent Discretization on the Progressive Failure of Composite Materials Using Multiscale Analyses

NASA Technical Reports Server (NTRS)

Ricks, Trenton M.; Lacy, Thomas E., Jr.; Pineda, Evan J.; Bednarcyk, Brett A.; Arnold, Steven M.

2013-01-01

A multiscale modeling methodology, which incorporates a statistical distribution of fiber strengths into coupled micromechanics/ finite element analyses, is applied to unidirectional polymer matrix composites (PMCs) to analyze the effect of mesh discretization both at the micro- and macroscales on the predicted ultimate tensile (UTS) strength and failure behavior. The NASA code FEAMAC and the ABAQUS finite element solver were used to analyze the progressive failure of a PMC tensile specimen that initiates at the repeating unit cell (RUC) level. Three different finite element mesh densities were employed and each coupled with an appropriate RUC. Multiple simulations were performed in order to assess the effect of a statistical distribution of fiber strengths on the bulk composite failure and predicted strength. The coupled effects of both the micro- and macroscale discretizations were found to have a noticeable effect on the predicted UTS and computational efficiency of the simulations.

New high-strength, high-conductivity Cu-Ag alloy sheets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sakai, Y.; Inoue, K.; Maeda, H.

1995-04-01

A sheet-conductor fabrication method has been developed for Cu-Ag alloys containing 6--24 wt% Ag in which high-strength and high-conductivity are obtained by coldworking combined with intermediate heat treatments. The intermediate heat treatments were repeated three times at 400--450 C for 1--2 h at appropriate stages of cold-rolling. The optimized Cu-24 wt% Ag alloy sheet with a 96% reduction ratio shows an ultimate tensile strength of 1,050 MPa and an electrical conductivity of 75% IACS at room temperature. Anisotropy in the strength with respect to the rolling direction is less than 10%, and no anisotropy in the electrical conductivity occurs. Themore » authors demonstrated the ability to manufacture the Cu-Ag sheets for Bitter magnet on a commercial basis. The sheets fabricated by this method are promising as conductors for high-field Bitter magnet coils.« less

Rating the strength of coal mine roof rocks. Information circular/1996

DOE Office of Scientific and Technical Information (OSTI.GOV)

Molinda, G.M.; Mark, C.

1996-05-01

The Ferm pictoral classification of coal measure rocks is widely utilized in coalfield exploration. Although extremely useful as an alternative to conventional geologic description, no material properties are provided that would be suitable for engineering solutions. To remedy this problem, the USBM has tested over 30 common coal measure roof rock types for axial and bedding strength. More than 1,300 individual point load tests have been conducted on core from 8 different coal mines representing the full range of common coal measure rocks. The USBM core and roof exposure properties database has been merged with the picture classification to provide,more » for the first time, a simple, clear guide from field identification of core to the associated mechanical strength of the rock. For 33 of the most common roof rocks, the axial and diametral point load strength, as well as the ultimate unit rating, is overprinted onto the photograph.« less

Optimizing the coupled effects of Hall-Petch and precipitation strengthening in a Al 0.3 CoCrFeNi high entropy alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gwalani, B.; Soni, Vishal; Lee, Michael

2017-05-01

A successful demonstration of applying integrated strengthening using Hall-Petch strengthening (grains size effect) and precipitation strengthening is shown in the fcc based high entropy alloy (HEA) Al0.3CoCrFeNi, leading to quantitative determinations of the Hall-Petch coefficients for both hardness and tensile yield strength, aswell as the enhancements in the yield strength fromtwo distinct types of ordered precipitates, L12 and B2. An excellent combination of yield strength (~490MPa), ultimate tensile strength (~850MPa), and ductility (~45% elongation) was achieved by optimizing and coupling both strengtheningmechanisms, resulting from a refined grain size as well as both L12 and B2 ordered precipitates. This opens upmore » new avenues for the future development of HEAs, with the appropriate balance of properties required for engineering applications.« less

Screen-Based Sedentary Behavior, Physical Activity, and Muscle Strength in the English Longitudinal Study of Ageing

PubMed Central

Hamer, Mark; Stamatakis, Emmanuel

2013-01-01

Background Sarcopenia is associated with loss of independence and ill-health in the elderly although the causes remain poorly understood. We examined the association between two screen-based leisure time sedentary activities (daily TV viewing time and internet use) and muscle strength. Methods and Results We studied 6228 men and women (aged 64.9±9.1 yrs) from wave 4 (2008-09) of the English Longitudinal Study of Ageing, a prospective study of community dwelling older adults. Muscle strength was assessed by a hand grip test and the time required to complete five chair rises. TV viewing and internet usage were inversely associated with one another. Participants viewing TV ≥6hrs/d had lower grip strength (Men, B = −1.20 kg, 95% CI, −2.26, −0.14; Women, −0.75 kg, 95% CI, −1.48, −0.03) in comparison to <2hrs/d TV, after adjustment for age, physical activity, smoking, alcohol, chronic disease, disability, depressive symptoms, social status, and body mass index. In contrast, internet use was associated with higher grip strength (Men, B = 2.43 kg, 95% CI, 1.74, 3.12; Women, 0.76 kg, 95% CI, 0.32, 1.20). These associations persisted after mutual adjustment for both types of sedentary behaviour. Conclusions In older adults, the association between sedentary activities and physical function is context specific (TV viewing vs. computer use). Adverse effects of TV viewing might reflect the prolonged sedentary nature of this behavior. PMID:23755302

Dietary Variety and Decline in Lean Mass and Physical Performance in Community-Dwelling Older Japanese: A 4-year Follow-Up Study.

PubMed

Yokoyama, Y; Nishi, M; Murayama, H; Amano, H; Taniguchi, Y; Nofuji, Y; Narita, M; Matsuo, E; Seino, S; Kawano, Y; Shinkai, S

2017-01-01

To examine associations of dietary variety with changes in lean mass and physical performance during a 4-year period in an elderly Japanese population. Four-year prospective study. The Hatoyama Cohort Study and Kusatsu Longitudinal Study, Japan. 935 community-dwelling Japanese aged 65 years or older. Dietary variety was assessed using a 10-item food frequency questionnaire. Body composition was determined by multifrequency bioelectrical impedance analysis, and physical performance (grip strength and usual gait speed) was measured in surveys at baseline and 4 years later. Longitudinal analysis included only participants who were originally in the upper three quartiles of lean body mass, appendicular lean mass, grip strength, and usual gait speed. The outcome measures were decline in lean body mass, appendicular lean mass, grip strength, and usual gait speed, defined as a decrease to the lowest baseline quartile level at the 4-year follow-up survey. Associations of dietary variety with the outcome measures were examined by logistic regression analysis adjusted for potential confounders. In the fully adjusted model, the odds ratios for decline in grip strength and usual gait speed were 0.43 (95% confidence interval, 0.19-0.99) and 0.43 (confidence interval, 0.19-0.99), respectively, for participants in the highest category of dietary variety score as compared with those in the lowest category. Dietary variety was not significantly associated with changes in lean body mass or appendicular lean mass. Among older adults, greater dietary variety may help maintain physical performance, such as grip strength and usual gait speed, but not lean mass.

Planar-focusing cathodes.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lewellen, J. W.; Noonan, J.; Accelerator Systems Division

2005-01-01

Conventional {pi}-mode rf photoinjectors typically use magnetic solenoids for emittance compensation. This provides independent focusing strength but can complicate rf power feed placement, introduce asymmetries (due to coil crossovers), and greatly increase the cost of the photoinjector. Cathode-region focusing can also provide for a form of emittance compensation. Typically this method strongly couples focusing strength to the field gradient on the cathode, however, and usually requires altering the longitudinal position of the cathode to change the focusing. We propose a new method for achieving cathode-region variable-strength focusing for emittance compensation. The new method reduces the coupling to the gradient onmore » the cathode and does not require a change in the longitudinal position of the cathode. Expected performance for an S-band system is similar to conventional solenoid-based designs. This paper presents the results of rf cavity and beam dynamics simulations of the new design. We have proposed a method for performing emittance compensation using a cathode-region focusing scheme. This technique allows the focusing strength to be adjusted somewhat independently of the on-axis field strength. Beam dynamics calculations indicate performance should be comparable to presently in-use emittance compensation schemes, with a simpler configuration and fewer possibilities for emittance degradation due to the focusing optics. There are several potential difficulties with this approach, including cathode material selection, cathode heating, and peak fields in the gun. We hope to begin experimenting with a cathode of this type in the near future, and several possibilities exist for reducing the peak gradients to more acceptable levels.« less

Data-driven regions of interest for longitudinal change in frontotemporal lobar degeneration.

PubMed

Pankov, Aleksandr; Binney, Richard J; Staffaroni, Adam M; Kornak, John; Attygalle, Suneth; Schuff, Norbert; Weiner, Michael W; Kramer, Joel H; Dickerson, Bradford C; Miller, Bruce L; Rosen, Howard J

2016-01-01

Current research is investigating the potential utility of longitudinal measurement of brain structure as a marker of drug effect in clinical trials for neurodegenerative disease. Recent studies in Alzheimer's disease (AD) have shown that measurement of change in empirically derived regions of interest (ROIs) allows more reliable measurement of change over time compared with regions chosen a-priori based on known effects of AD on brain anatomy. Frontotemporal lobar degeneration (FTLD) is a devastating neurodegenerative disorder for which there are no approved treatments. The goal of this study was to identify an empirical ROI that maximizes the effect size for the annual rate of brain atrophy in FTLD compared with healthy age matched controls, and to estimate the effect size and associated power estimates for a theoretical study that would use change within this ROI as an outcome measure. Eighty six patients with FTLD were studied, including 43 who were imaged twice at 1.5 T and 43 at 3 T, along with 105 controls (37 imaged at 1.5 T and 67 at 3 T). Empirically-derived maps of change were generated separately for each field strength and included the bilateral insula, dorsolateral, medial and orbital frontal, basal ganglia and lateral and inferior temporal regions. The extent of regions included in the 3 T map was larger than that in the 1.5 T map. At both field strengths, the effect sizes for imaging were larger than for any clinical measures. At 3 T, the effect size for longitudinal change measured within the empirically derived ROI was larger than the effect sizes derived from frontal lobe, temporal lobe or whole brain ROIs. The effect size derived from the data-driven 1.5 T map was smaller than at 3 T, and was not larger than the effect size derived from a-priori ROIs. It was estimated that measurement of longitudinal change using 1.5 T MR systems requires approximately a 3-fold increase in sample size to obtain effect sizes equivalent to those seen at 3 T. While the results should be confirmed in additional datasets, these results indicate that empirically derived ROIs can reduce the number of subjects needed for a longitudinal study of drug effects in FTLD compared with a-priori ROIs. Field strength may have a significant impact on the utility of imaging for measuring longitudinal change.

Sarcopenia, dynapenia, and the impact of advancing age on human skeletal muscle size and strength; a quantitative review.

PubMed

Mitchell, W Kyle; Williams, John; Atherton, Philip; Larvin, Mike; Lund, John; Narici, Marco

2012-01-01

Changing demographics make it ever more important to understand the modifiable risk factors for disability and loss of independence with advancing age. For more than two decades there has been increasing interest in the role of sarcopenia, the age-related loss of muscle or lean mass, in curtailing active and healthy aging. There is now evidence to suggest that lack of strength, or dynapenia, is a more constant factor in compromised wellbeing in old age and it is apparent that the decline in muscle mass and the decline in strength can take quite different trajectories. This demands recognition of the concept of muscle quality; that is the force generating per capacity per unit cross-sectional area (CSA). An understanding of the impact of aging on skeletal muscle will require attention to both the changes in muscle size and the changes in muscle quality. The aim of this review is to present current knowledge of the decline in human muscle mass and strength with advancing age and the associated risk to health and survival and to review the underlying changes in muscle characteristics and the etiology of sarcopenia. Cross-sectional studies comparing young (18-45 years) and old (>65 years) samples show dramatic variation based on the technique used and population studied. The median of values of rate of loss reported across studies is 0.47% per year in men and 0.37% per year in women. Longitudinal studies show that in people aged 75 years, muscle mass is lost at a rate of 0.64-0.70% per year in women and 0.80-00.98% per year in men. Strength is lost more rapidly. Longitudinal studies show that at age 75 years, strength is lost at a rate of 3-4% per year in men and 2.5-3% per year in women. Studies that assessed changes in mass and strength in the same sample report a loss of strength 2-5 times faster than loss of mass. Loss of strength is a more consistent risk for disability and death than is loss of muscle mass.

[Comparative study on the strength of different mechanisms of operation of multidirectionally angle-stable distal radius plates].

PubMed

Rausch, S; Hoffmeier, K; Gueorguiev, B G; Klos, K; Gras, F; Hofmann, G O; Mückley, T

2011-12-01

Polyaxial angle-stable plating is thought to be particularly beneficial in the management of complex intra-articular fractures of the distal radius. The present study was performed to investigate the strength of polyaxial locking interfaces of distal radius plates. We tested the polyaxial interfaces of 3 different distal radius plates (2.4 mm Variable Angle LCP Two-Column Volar Distal Radius Plate, Synthes, Palmar Classic, Königsee Implantate and VariAx Plate Stryker). The strength of 0° and 10° screw locking angle was obtained during static loading. The strength of Palmar Classic with a 0° locking angle is significantly the best of all tested systems. With a 10° locking angle there is no significant difference between Palmar Classic, Two column Plate and VariAx Plate. The strength of polyaxial interfaces differs between the tested systems. A reduction of ultimate strength is due to increases of screw locking angle. The design of polyaxial locking interfaces should be investigated in human bone models. © Georg Thieme Verlag KG Stuttgart · New York.

Study of strength properties of semi-finished products from economically alloyed high-strength aluminium-scandium alloys for application in automobile transport and shipbuilding

NASA Astrophysics Data System (ADS)

Baranov, Vladimir; Sidelnikov, Sergey; Zenkin, Evgeny; Frolov, Viktor; Voroshilov, Denis; Yakivyuk, Olga; Konstantinov, Igor; Sokolov, Ruslan; Belokonova, Irina

2018-04-01

The results of a study on the strength of rolled products from aluminium alloys doped with scandium under various processing conditions of hot and cold rolling are presented. The regularities of metal flow and the level of strength of deformed semi-finished products from aluminum-scandium alloys are established, depending on the total degree of deformation and the various modes of single reduction during rolling. It is shown that when using one heating of a cast billet to obtain high-quality semi-finished products, the temperature during the rolling process should not be lower than 350-370°, and the total degree of deformation does not exceed 50-60%. It was found that the semi-finished products from alloys with a content of scandium in the range 0.11-0.12% in the deformed state had elevated values of ultimate tensile strength and yield strength of the metal, which allows them to be recommended for industrial production of sheet metal products.

Effect of Brake Forming on the Strength of 24S-T Aluminum-alloy Sheet

NASA Technical Reports Server (NTRS)

Heimerl, George J; Woods, Walter

1946-01-01

Tests were made to determine the effect of brake forming on the strength of 24S-T aluminum alloy sheet that had been formed to an inside bend radius of three times the sheet thickness. The results for both directions of the grain of the material showed that the compressive yield stresses were appreciably increased, that the tensile yield stresses were moderately increased, that the ultimate tensile stresses were only slightly increased, that the elongations were considerably reduced, and that the shapes of the tensile and compressive stress-strain curves were markedly changed.

Moving Aerospace Structural Design Practice to a Load and Resistance Factor Approach

NASA Technical Reports Server (NTRS)

Larsen, Curtis E.; Raju, Ivatury S.

2016-01-01

Aerospace structures are traditionally designed using the factor of safety (FOS) approach. The limit load on the structure is determined and the structure is then designed for FOS times the limit load - the ultimate load. Probabilistic approaches utilize distributions for loads and strengths. Failures are predicted to occur in the region of intersection of the two distributions. The load and resistance factor design (LRFD) approach judiciously combines these two approaches by intensive calibration studies on loads and strength to result in structures that are efficient and reliable. This paper discusses these three approaches.

LIFESPAN: A tool for the computer-aided design of longitudinal studies

PubMed Central

Brandmaier, Andreas M.; von Oertzen, Timo; Ghisletta, Paolo; Hertzog, Christopher; Lindenberger, Ulman

2015-01-01

Researchers planning a longitudinal study typically search, more or less informally, a multivariate space of possible study designs that include dimensions such as the hypothesized true variance in change, indicator reliability, the number and spacing of measurement occasions, total study time, and sample size. The main search goal is to select a research design that best addresses the guiding questions and hypotheses of the planned study while heeding applicable external conditions and constraints, including time, money, feasibility, and ethical considerations. Because longitudinal study selection ultimately requires optimization under constraints, it is amenable to the general operating principles of optimization in computer-aided design. Based on power equivalence theory (MacCallum et al., 2010; von Oertzen, 2010), we propose a computational framework to promote more systematic searches within the study design space. Starting with an initial design, the proposed framework generates a set of alternative models with equal statistical power to detect hypothesized effects, and delineates trade-off relations among relevant parameters, such as total study time and the number of measurement occasions. We present LIFESPAN (Longitudinal Interactive Front End Study Planner), which implements this framework. LIFESPAN boosts the efficiency, breadth, and precision of the search for optimal longitudinal designs. Its initial version, which is freely available at http://www.brandmaier.de/lifespan, is geared toward the power to detect variance in change as specified in a linear latent growth curve model. PMID:25852596

Penalized maximum likelihood simultaneous longitudinal PET image reconstruction with difference-image priors.

PubMed

Ellis, Sam; Reader, Andrew J

2018-04-26

Many clinical contexts require the acquisition of multiple positron emission tomography (PET) scans of a single subject, for example, to observe and quantitate changes in functional behaviour in tumors after treatment in oncology. Typically, the datasets from each of these scans are reconstructed individually, without exploiting the similarities between them. We have recently shown that sharing information between longitudinal PET datasets by penalizing voxel-wise differences during image reconstruction can improve reconstructed images by reducing background noise and increasing the contrast-to-noise ratio of high-activity lesions. Here, we present two additional novel longitudinal difference-image priors and evaluate their performance using two-dimesional (2D) simulation studies and a three-dimensional (3D) real dataset case study. We have previously proposed a simultaneous difference-image-based penalized maximum likelihood (PML) longitudinal image reconstruction method that encourages sparse difference images (DS-PML), and in this work we propose two further novel prior terms. The priors are designed to encourage longitudinal images with corresponding differences which have (a) low entropy (DE-PML), and (b) high sparsity in their spatial gradients (DTV-PML). These two new priors and the originally proposed longitudinal prior were applied to 2D-simulated treatment response [ 18 F]fluorodeoxyglucose (FDG) brain tumor datasets and compared to standard maximum likelihood expectation-maximization (MLEM) reconstructions. These 2D simulation studies explored the effects of penalty strengths, tumor behaviour, and interscan coupling on reconstructed images. Finally, a real two-scan longitudinal data series acquired from a head and neck cancer patient was reconstructed with the proposed methods and the results compared to standard reconstruction methods. Using any of the three priors with an appropriate penalty strength produced images with noise levels equivalent to those seen when using standard reconstructions with increased counts levels. In tumor regions, each method produces subtly different results in terms of preservation of tumor quantitation and reconstruction root mean-squared error (RMSE). In particular, in the two-scan simulations, the DE-PML method produced tumor means in close agreement with MLEM reconstructions, while the DTV-PML method produced the lowest errors due to noise reduction within the tumor. Across a range of tumor responses and different numbers of scans, similar results were observed, with DTV-PML producing the lowest errors of the three priors and DE-PML producing the lowest bias. Similar improvements were observed in the reconstructions of the real longitudinal datasets, although imperfect alignment of the two PET images resulted in additional changes in the difference image that affected the performance of the proposed methods. Reconstruction of longitudinal datasets by penalizing difference images between pairs of scans from a data series allows for noise reduction in all reconstructed images. An appropriate choice of penalty term and penalty strength allows for this noise reduction to be achieved while maintaining reconstruction performance in regions of change, either in terms of quantitation of mean intensity via DE-PML, or in terms of tumor RMSE via DTV-PML. Overall, improving the image quality of longitudinal datasets via simultaneous reconstruction has the potential to improve upon currently used methods, allow dose reduction, or reduce scan time while maintaining image quality at current levels. © 2018 The Authors. Medical Physics published by Wiley Periodicals, Inc. on behalf of American Association of Physicists in Medicine.

Interface reactions between silicon carbide and interlayers in silicon carbide copper metal matrix composites

NASA Astrophysics Data System (ADS)

Köck, T.; Brendel, A.; Bolt, H.

2007-05-01

Novel copper matrix composites reinforced with silicon carbide fibres are considered as a new generation of heat sink materials for the divertor of future fusion reactors. The divertor is exposed to intense particle bombardment and heat loads of up to 15 MW m-2. This component consists of the plasma-facing material which is bonded to the actively cooled heat sink. Due to its high thermal conductivity of about 400 W m-1 K-1 copper is a promising material for the heat sink. To increase the mechanical properties of copper at working temperature (823 K), silicon carbide fibres with a diameter of 140 μm are used to reinforce the interface area between the plasma-facing material and the heat sink. Push-out tests show that the adhesion between SiC fibre and Cu matrix without any interlayer is very low. To increase the fibre-matrix bonding the fibres are coated with Cr and W with a thickness of 300-400 nm before Cu deposition by magnetron sputtering. Push-out tests on these modified fibres show a significant increase in adhesion compared to the fibres without interlayer. XRD investigations after a heat treatment at 923 K show a chromium carbide (Cr23C6, Cr3C2) formation and the absence of chromium silicides. In the case of a W interlayer a W2C formation is detected and also no tungsten silicides. Single-fibre tensile tests were performed to investigate the influence of the reaction zone on the ultimate tensile strength of the fibres. The ultimate tensile strength for fibres without interlayer remains constant at about 2200 MPa after annealing at 923 K. The fibres with chromium and tungsten interlayers, respectively, show a decrease of about 30% of the ultimate tensile strength after the heat treatment at 923 K.

A Longitudinal Study into Indicators of Mental Health, Strengths and Difficulties Reported by Boarding Students as They Transition from Primary School to Secondary Boarding Schools in Perth, Western Australia

ERIC Educational Resources Information Center

Mander, David J.; Lester, Leanne

2017-01-01

This study examined indicators of mental health, as well as strengths and difficulties, as reported by same-age boarding and non-boarding students spanning four time points over a 2-year period as they transitioned from primary to boarding school in Western Australia (i.e., at the end of Grade 7, beginning of Grade 8, end of Grade 8, and end of…

Realizing a Circuit Analog of an Optomechanical System with Longitudinally Coupled Superconducting Resonators

NASA Astrophysics Data System (ADS)

Eichler, C.; Petta, J. R.

2018-06-01

We realize a superconducting circuit analog of the generic cavity-optomechanical Hamiltonian by longitudinally coupling two superconducting resonators, which are an order of magnitude different in frequency. We achieve longitudinal coupling by embedding a superconducting quantum interference device into a high frequency resonator, making its resonance frequency depend on the zero point current fluctuations of a nearby low frequency L C resonator. By applying sideband drive fields we enhance the intrinsic coupling strength of about 15 kHz up to 280 kHz by controlling the amplitude of the drive field. Our results pave the way towards the exploration of optomechanical effects in a fully superconducting platform and could enable quantum optics experiments with photons in the yet unexplored radio frequency band.

The effect of ultrasonics on the strength properties of carbon steel processed by cold plastic deformation

NASA Technical Reports Server (NTRS)

Atanasiu, N.; Dragan, O.; Atanasiu, Z.

1974-01-01

A study was made of the influence of ultrasounds on the mechanical properties of OLT 35 carbon steel tubes cold-drawn on a plug ultrasonically activated by longitudinal waves. Experimental results indicate that: 1. The reduction in the values of the flow limit and tensile strength is proportional to the increase in acoustic energy introduced into the material subjected to deformation. 2. The diminution in influence of ultrasounds on tensile strength and flow rate that is due to an increased degree of deformation is explained by a reduction in specific density of the acoustic energy at the focus of deformation. 3. The relations calculated on the basis of the variation in the flow limit and tensile strength as a function of acoustic energy intensity was verified experimentally.

Design loads and uncertainties for the transverse strength of ships

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pittaluga, A.

1995-12-31

Rational design of ship structures is becoming a reality, and a reliability based approach for the longitudinal strength assessment of ship hulls is close to implementation. Transverse strength of ships is a step behind, mainly due to the complexity of the collapse modes associated with transverse strength. Nevertheless, some investigations are being made and the importance of an acceptable stochastic model for the environmental demand on the transverse structures is widely recognized. In the paper, the problem of the determination of the sea loads on a transverse section of a ship is discussed. The problem of extrapolating the calculated results,more » which are relevant to the submerged portion of the hull, to areas which are only occasionally wet in extreme conditions is also addressed.« less

Simulated Data for High Temperature Composite Design

NASA Technical Reports Server (NTRS)

Chamis, Christos C.; Abumeri, Galib H.

2006-01-01

The paper describes an effective formal method that can be used to simulate design properties for composites that is inclusive of all the effects that influence those properties. This effective simulation method is integrated computer codes that include composite micromechanics, composite macromechanics, laminate theory, structural analysis, and multi-factor interaction model. Demonstration of the method includes sample examples for static, thermal, and fracture reliability for a unidirectional metal matrix composite as well as rupture strength and fatigue strength for a high temperature super alloy. Typical results obtained for a unidirectional composite show that the thermal properties are more sensitive to internal local damage, the longitudinal properties degrade slowly with temperature, the transverse and shear properties degrade rapidly with temperature as do rupture strength and fatigue strength for super alloys.

Effect of bending on the room-temperature tensile strengths of structural ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jenkins, M.G.

1992-01-01

Results for nearly fifty, room-temperature tensile tests conducted on two advanced, monolithic silicon nitride ceramics are evaluated for the effects of bending and application of various Weibull statistical analyses. Two specimen gripping systems (straight collet and tapered collet) were evaluated for both success in producing gage section failures and tendency to minimize bending at failure. Specimen fabrication and grinding technique consderations are briefly reviewed and related to their effects on successful tensile tests. Ultimate tensile strengths are related to the bending measured at specimen failure and the effects of the gripping system on bending are discussed. Finally, comparisons are mademore » between the use of censored and uncensored data sample sets for determining the maximum likelihood estimates of the Weibull parameters from the tensile strength distributions.« less

Effect of bending on the room-temperature tensile strengths of structural ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jenkins, M.G.

1992-07-01

Results for nearly fifty, room-temperature tensile tests conducted on two advanced, monolithic silicon nitride ceramics are evaluated for the effects of bending and application of various Weibull statistical analyses. Two specimen gripping systems (straight collet and tapered collet) were evaluated for both success in producing gage section failures and tendency to minimize bending at failure. Specimen fabrication and grinding technique consderations are briefly reviewed and related to their effects on successful tensile tests. Ultimate tensile strengths are related to the bending measured at specimen failure and the effects of the gripping system on bending are discussed. Finally, comparisons are mademore » between the use of censored and uncensored data sample sets for determining the maximum likelihood estimates of the Weibull parameters from the tensile strength distributions.« less

Tensile behavior of the L(1)2 compound Al67Ti25Cr8

NASA Technical Reports Server (NTRS)

Kumar, K. S.; Brown, S. A.

1992-01-01

Temperature-related variations in tensile yield strength and ductility were studied on cast, homogenized and isothermally forged Al67Ti25Cr8. Yield strength dropped discontinuously between 623 K and 773 K and then decreased gradually with increasing temperature. Below 623 K, fracture occurred prior to macroscopic yielding. Ductility decreased from 0.2 percent at 623 K to zero at 773 K, but increased again at higher temperatures. At 1073 K, an elongation of 19 percent was obtainable, and ultimate tensile strength and localized necking were observed. Fracture surfaces and deformed microstructures were examined. The 1073 K tensile specimen that exhibited 19 percent elongation showed grain boundary serrations and some evidence of recrystallization (likely dynamic) although fracture occurred predominantly via an intergranular mode.

Evaluation of the interfacial bond properties between carbon phenolic and glass phenolic composites

NASA Technical Reports Server (NTRS)

Jordan, K.; Clinton, R.; Jeelani, S.

1991-01-01

The effects of moisture and surface finish on the mechanical and physical properties of the interfacial bond between carbon/phenolic (C/P) and glass/phenolic (G/P) composite materials have been studied. Test results indicate that moisture substantially degrades the integrity of the interfacial bond between C/P and G/P materials. The apparent effect of the autoclave curing of the C/P material reduces the ultimate interlaminar shear length of the C/P material by 20 percent compared to the hydroclave curing of the C/P material. The variation in applied surface finishes is found to have no appreciable effect on the ultimate interlaminar shear strength of the interface in the wet laminate.

Characterization of a Ultra-high Temperature Ceramic Composite

NASA Technical Reports Server (NTRS)

Levine, Stanley R.; Opila, Elizabeth J.; Robinson, Raymond C.; Lorincz, Jonathan A.

2003-01-01

Ultra-high temperature ceramics (UHTC) are of interest for hypersonic vehicle leading edge applications. Monolithic UHTCs are of concern because of their low fracture toughness and brittle behavior. UHTC composites (UHTCC) are being investigated as a possible approach to overcome these deficiencies. In this study a small sample of a UHTCC was evaluated by limited mechanical property tests, furnace oxidation exposures, and oxidation exposures in a flowing environment. The composite was prepared from a carbon fiber perform using ceramic particulates and a preceramic polymer. The as-received composite plate was non-uniform from front to back surface. Plate dimensions were 150 x 150 x 6 mm. The back surface had a fibrous, uniform appearance; XRD analysis revealed the presence of Sic and C. The front surface was smooth and non-uniform in appearance with evidence of a coarse grain structure produced by a liquid phase; XRD analysis revealed the presence of HfB2. Microcracks were present throughout the thickness as one might expect from a carbon fiber reinforced composite with attendant large thermal expansion mismatch between the matrix phases and the fibers. The HfB2 phase on the front surface was comparable in thickness to a fiber ply or about 0.6 mm, and surface microcracks were evident. Limited four point flexural tests were carried out at span to depth ratios of approximately 14 and 16 with markedly different results. Tests were run with the front or the back surface in tension. At the shorter span to depth failures occurred under a loading pin for both orientations. At a span to depth of 16 failures occurred in the center of the span with fracture clearly initiating from a tensile failure. Ultimate flexural strength, strain at ultimate stress, stress and strain at deviation from linear elastic behavior are reported. Strains at ultimate stress ranged from about 0.6 to 0.7 % for the back surface in tension, and 0.4 to 0.6 for the front surface in tension. At constant span to depth the strain at ultimate stress was about 0.2% greater for the back surface in tension and the ultimate strength was also higher. Strengths were in line with predictions from theory. Furnace oxidation studies were carried out at 1627 and 1927OC in a static furnace environment using ten minute cycles and one, five, and ten cycles. Limited oxidation studies were also carried out in a flowing oxyacetylene torch environment. Specimens were photographed, and weight and dimensional changes were determined. XRD and SEM characterizations were performed. Weight losses were attributed primarily to carbon fiber oxidation. The composite survived the torch test with little visible distress. Further details will be determined once metallographic studies are completed.

49 CFR 173.247 - Bulk packaging for certain elevated temperature materials.

Code of Federal Regulations, 2012 CFR

2012-10-01

... constructed of carbon steel which is in elevated temperature material service is excepted from § 178.345-7(d... constructed such that the stress in the packaging does not exceed one fourth (0.25) of the ultimate strength... kettle tires; CG height is measured perpendicular from the road surface). (2) High stability kettles. (i...

46 CFR 54.25-10 - Low temperature operation-ferritic steels (replaces UCS-65 through UCS-67).

Code of Federal Regulations, 2013 CFR

2013-10-01

... the following additional requirements: Note: For high alloy steels refer to § 54.25-15. For heat... tempered steels. The ultimate and yield strengths shall be as shown in the applicable specification and... 46 Shipping 2 2013-10-01 2013-10-01 false Low temperature operation-ferritic steels (replaces UCS...

46 CFR 54.25-10 - Low temperature operation-ferritic steels (replaces UCS-65 through UCS-67).

Code of Federal Regulations, 2014 CFR

2014-10-01

... the following additional requirements: Note: For high alloy steels refer to § 54.25-15. For heat... tempered steels. The ultimate and yield strengths shall be as shown in the applicable specification and... 46 Shipping 2 2014-10-01 2014-10-01 false Low temperature operation-ferritic steels (replaces UCS...

46 CFR 54.25-10 - Low temperature operation-ferritic steels (replaces UCS-65 through UCS-67).

Code of Federal Regulations, 2012 CFR

2012-10-01

... the following additional requirements: Note: For high alloy steels refer to § 54.25-15. For heat... tempered steels. The ultimate and yield strengths shall be as shown in the applicable specification and... 46 Shipping 2 2012-10-01 2012-10-01 false Low temperature operation-ferritic steels (replaces UCS...

46 CFR 199.150 - Survival craft launching and recovery arrangements; general.

Code of Federal Regulations, 2013 CFR

2013-10-01

... approval series 160.163. (b) Unless expressly provided otherwise in this part, each survival craft must be... attachment to the vessel must be designed, based on the ultimate strength of the construction material, to be at least 4.5 times the load imparted on the attachment by the launching appliance and its fully...

Installation and use of epoxy-grouted rock anchors for skyline logging in southeast Alaska.

Treesearch

W.L. Schroeder; D.N. Swanston

1992-01-01

Field tests of the load-carrying capacity of epoxy-grouted rock anchors in poor quality bedrock on Wrangel Island in southeast Alaska demonstrated the effectiveness of rock anchors as substitutes for stump anchors for logging system guylines. Ultimate capacity depends mainly on rock hardness or strength and length of the imbedded anchor.

49 CFR 238.419 - Truck-to-car-body and truck component attachment.

Code of Federal Regulations, 2014 CFR

2014-10-01

... 49 Transportation 4 2014-10-01 2014-10-01 false Truck-to-car-body and truck component attachment... Specific Requirements for Tier II Passenger Equipment § 238.419 Truck-to-car-body and truck component attachment. (a) The ultimate strength of the truck-to-car-body attachment for each unit in a train shall be...

49 CFR 238.419 - Truck-to-car-body and truck component attachment.

Code of Federal Regulations, 2010 CFR

2010-10-01

... 49 Transportation 4 2010-10-01 2010-10-01 false Truck-to-car-body and truck component attachment... Specific Requirements for Tier II Passenger Equipment § 238.419 Truck-to-car-body and truck component attachment. (a) The ultimate strength of the truck-to-car-body attachment for each unit in a train shall be...

Modeling Field-Scale Phosphorus Transfer: Model Strengths and Weaknesses, Gaps in Knowledge, and the Role for Scientists

USDA-ARS?s Scientific Manuscript database

The ultimate goal of applied research of phosphorus (P) transfer from agricultural fields to surface waters should arguably be to develop and apply mathematical models. There are two primary reasons for this assertion: 1) models formalize our understanding of P transfer and force us to test that und...

49 CFR 238.419 - Truck-to-car-body and truck component attachment.

Code of Federal Regulations, 2011 CFR

2011-10-01

... 49 Transportation 4 2011-10-01 2011-10-01 false Truck-to-car-body and truck component attachment... Specific Requirements for Tier II Passenger Equipment § 238.419 Truck-to-car-body and truck component attachment. (a) The ultimate strength of the truck-to-car-body attachment for each unit in a train shall be...

The polymethyl methacrylate cervical cage for treatment of cervical disk disease Part III. Biomechanical properties.

PubMed

Chen, Jyi-Feng; Lee, Shih-Tseng

2006-10-01

In a previous article, we used the PMMA cervical cage in the treatment of single-level cervical disk disease and the preliminary clinical results were satisfactory. However, the mechanical properties of the PMMA cage were not clear. Therefore, we designed a comparative in vitro biomechanical study to determine the mechanical properties of the PMMA cage. The PMMA cervical cage and the Solis PEEK cervical cage were compressed in a materials testing machine to determine the mechanical properties. The compressive yield strength of the PMMA cage (7030 +/- 637 N) was less than that of the Solis polymer cervical cage (8100 +/- 572 N). The ultimate compressive strength of the PMMA cage (8160 +/- 724 N) was less than that of the Solis cage (9100 +/- 634 N). The stiffness of the PMMA cervical cage (8106 +/- 817 N/mm) was greater than that of the Solis cage (6486 +/- 530 N/mm). The elastic modulus of the PMMA cage (623 +/- 57 MPa) was greater than that of the Solis cage (510 +/- 42 MPa). The elongation of PMMA cage (43.5 +/- 5.7%) was larger than that of the Solis cage (36.1 +/- 4.3%). Although the compressive yield strength and ultimate compressive strength of the PMMA cervical cage were less than those of the Solis polymer cage, the mechanical properties are better than those of the cervical vertebral body. The PMMA cage is strong and safe for use as a spacer for cervical interbody fusion. Compared with other cage materials, the PMMA cage has many advantages and no obvious failings at present. However, the PMMA cervical cage warrants further long-term clinical study.

Wear, strength, modulus and hardness of CAD/CAM restorative materials.

PubMed

Lawson, Nathaniel C; Bansal, Ritika; Burgess, John O

2016-11-01

To measure the mechanical properties of several CAD/CAM materials, including lithium disilicate (e.max CAD), lithium silicate/zirconia (Celtra Duo), 3 resin composites (Cerasmart, Lava Ultimate, Paradigm MZ100), and a polymer infiltrated ceramic (Enamic). CAD/CAM blocks were sectioned into 2.5mm×2.5mm×16mm bars for flexural strength and elastic modulus testing and 4mm thick blocks for hardness and wear testing. E.max CAD and half the Celtra Duo specimens were treated in a furnace. Flexural strength specimens (n=10) were tested in a three-point bending fixture. Vickers microhardness (n=2, 5 readings per specimen) was measured with a 1kg load and 15s dwell time. The CAD/CAM materials as well as labial surfaces of human incisors were mounted in the UAB wear device. Cusps of human premolars were mounted as antagonists. Specimens were tested for 400,000 cycles at 20N force, 2mm sliding distance, 1Hz frequency, 24°C, and 33% glycerin lubrication. Volumetric wear and opposing enamel wear were measured with non-contact profilometry. Data were analyzed with 1-way ANOVA and Tukey post-hoc analysis (alpha=0.05). Specimens were observed with SEM. Properties were different for each material (p<0.01). E.max CAD and Celtra Duo were generally stronger, stiffer, and harder than the other materials. E.max CAD, Celtra Duo, Enamic, and enamel demonstrated signs of abrasive wear, whereas Cerasmart, Lava Ultimate, Paradigm MZ100 demonstrated signs of fatigue. Resin composite and resin infiltrated ceramic materials have demonstrated adequate wear resistance for load bearing restorations, however, they will require at least similar material thickness as lithium disilicate restorations due to their strength. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

The strength of aversive and appetitive associations and maladaptive behaviors.

PubMed

Itzhak, Yossef; Perez-Lanza, Daniel; Liddie, Shervin

2014-08-01

Certain maladaptive behaviors are thought to be acquired through classical Pavlovian conditioning. Exaggerated fear response, which can develop through Pavlovian conditioning, is associated with acquired anxiety disorders such as post-traumatic stress disorders (PTSDs). Inflated reward-seeking behavior, which develops through Pavlovian conditioning, underlies some types of addictive behavior (e.g., addiction to drugs, food, and gambling). These maladaptive behaviors are dependent on associative learning and the development of long-term memory (LTM). In animal models, an aversive reinforcer (fear conditioning) encodes an aversive contextual and cued LTM. On the other hand, an appetitive reinforcer results in conditioned place preference (CPP) that encodes an appetitive contextual LTM. The literature on weak and strong associative learning pertaining to the development of aversive and appetitive LTM is relatively scarce; thus, this review is particularly focused on the strength of associative learning. The strength of associative learning is dependent on the valence of the reinforcer and the salience of the conditioned stimulus that ultimately sways the strength of the memory trace. Our studies suggest that labile (weak) aversive and appetitive LTM may share similar signaling pathways, whereas stable (strong) aversive and appetitive LTM is mediated through different pathways. In addition, we provide some evidence suggesting that extinction of aversive fear memory and appetitive drug memory is likely to be mediated through different signaling molecules. We put forward the importance of studies aimed to investigate the molecular mechanisms underlying the development of weak and strong memories (aversive and appetitive), which would ultimately help in the development of targeted pharmacotherapies for the management of maladaptive behaviors that arise from classical Pavlovian conditioning. © 2014 International Union of Biochemistry and Molecular Biology.

Intermediate Temperature Stress Rupture of a Woven Hi-Nicalon, BN-Interphase, SiC Matric Composite in Air

NASA Technical Reports Server (NTRS)

Morscher, Gregory N.; Hurst, Janet; Brewer, David

1999-01-01

Woven Hi-Nicalon (TM) reinforced melt-infiltrated SiC matrix composites were tested under tensile stress-rupture conditions in air at intermediate temperatures. A comprehensive examination of the damage state and the fiber properties at failure was performed. Modal acoustic emission analysis was used to monitor damage during the experiment. Extensive microscopy of the composite fracture surfaces and the individual fiber fracture surfaces was used to determine the mechanisms leading to ultimate failure. The rupture properties of these composites were significantly worse than expected compared to the fiber properties under similar conditions. This was due to the oxidation of the BN interphase. Oxidation occurred through the matrix cracks that intersected the surface or edge of a tensile bar. These oxidation reactions resulted in minor degradation to fiber strength and strong bonding of the fibers to one another at regions of near fiber-to-fiber contact. It was found that two regimes for rupture exist for this material: a high stress regime where rupture occurs at a fast rate and a low stress regime where rupture occurs at a slower rate. For the high stress regime, the matrix damage state consisted of through thickness cracks. The average fracture strength of fibers that were pulled-out (the final fibers to break before ultimate failure) was controlled by the slow-crack growth rupture criterion in the literature for individual Hi-Nicalon (TM) fibers. For the low stress regime, the matrix damage state consisted of microcracks which grew during the rupture test. The average fracture strength of fibers that were pulled-out in this regime was the same as the average fracture strength of individual fibers pulled out in as-produced composites tested at room temperature.

The Effects of Magnetic-Field Geometry on Longitudinal Oscillations of Solar Prominences: Cross-Sectional Area Variation for Thin Tubes

NASA Technical Reports Server (NTRS)

Luna, M.; Diaz, A. J.; Oliver, R.; Terradas, J.; Karpen, J.

2016-01-01

Solar prominences are subject to both field-aligned (longitudinal) and transverse oscillatory motions, as evidenced by an increasing number of observations. Large-amplitude longitudinal motions provide valuable information on the geometry of the filament channel magnetic structure that supports the cool prominence plasma against gravity. Our pendulum model, in which the restoring force is the gravity projected along the dipped field lines of the magnetic structure, best explains these oscillations. However, several factors can influence the longitudinal oscillations, potentially invalidating the pendulum model. Aims. The aim of this work is to study the influence of large-scale variations in the magnetic field strength along the field lines, i.e., variations of the cross-sectional area along the flux tubes supporting prominence threads. Methods. We studied the normal modes of several flux tube configurations, using linear perturbation analysis, to assess the influence of different geometrical parameters on the oscillation properties. Results. We found that the influence of the symmetric and asymmetric expansion factors on longitudinal oscillations is small.Conclusions. We conclude that the longitudinal oscillations are not significantly influenced by variations of the cross-section of the flux tubes, validating the pendulum model in this context.

Investigation of rectangular concrete columns reinforced or prestressed with fiber reinforced polymer (FRP) bars or tendons

NASA Astrophysics Data System (ADS)

Choo, Ching Chiaw

Fiber reinforced polymer (FRP) composites have been increasingly used in concrete construction. This research focused on the behavior of concrete columns reinforced with FRP bars, or prestressed with FRP tendons. The methodology was based the ultimate strength approach where stress and strain compatibility conditions and material constitutive laws were applied. Axial strength-moment (P-M) interaction relations of reinforced or prestressed concrete columns with FRP, a linearly-elastic material, were examined. The analytical results identified the possibility of premature compression and/or brittle-tension failure occurring in FRP reinforced and prestressed concrete columns where sudden and explosive type failures were expected. These failures were related to the rupture of FRP rebars or tendons in compression and/or in tension prior to concrete reaching its ultimate strain and strength. The study also concluded that brittle-tension failure was more likely to occur due to the low ultimate tensile strain of FRP bars or tendons as compared to steel. In addition, the failures were more prevalent when long term effects such as creep and shrinkage of concrete, and creep rupture of FRP were considered. Barring FRP failure, concrete columns reinforced with FRP, in some instances, gained significant moment resistance. As expected the strength interaction of slender steel or FRP reinforced concrete columns were dependent more on column length rather than material differences between steel and FRP. Current ACI minimum reinforcement ratio for steel (rhomin) reinforced concrete columns may not be adequate for use in FRP reinforced concrete columns. Design aids were developed in this study to determine the minimum reinforcement ratio (rhof,min) required for rectangular reinforced concrete columns by averting brittle-tension failure to a failure controlled by concrete crushing which in nature was a less catastrophic and more gradual type failure. The proposed method using rhof,min enabled the analysis of FRP reinforced concrete columns to be carried out in a manner similar to steel reinforced concrete columns since similar provisions in ACI 318 were consistently used in developing these aids. The design aids produced accurate estimates of rhof,min. When creep and shrinkage effects of concrete were considered, conservative rhof,min values were obtained in order to preserve an adequate margin of safety due to their unpredictability.

Investigation on mechanical properties of basalt composite fabrics (experiment study)

NASA Astrophysics Data System (ADS)

Talebi Mazraehshahi, H.; Zamani, H.

2010-06-01

To fully appreciate the role and application of composite materials to structures, correct understanding of mechanical behaviors required for selection of optimum material. Fabric reinforced composites are composed of a matrix that is reinforced with pliable fabric, glass fabric is most popular reinforcement for different application specially in aircraft structure, although other fabric material are also used. At this study new fabric material called basalt with epoxy resin introduced and mechanical behaviors of this material investigated from view point of testing. For this study two type of fabric with different thickness used. Comparison between this composite reinforcement with popular reinforcement as carbon, glass, kevlar performed. To determine mechanical properties of epoxy based basalt fabric following test procedure performed : 1). Tensile testing according to ASTM D3039 in 0° and 90° direction to find ultimate strength in tension and shear, modulus of elasticity, elangation and ultimate strain. 2). Compression testing according to EN 2850 ultimate compression strength and maximum deformation under compression loading. 3). Shear testing according to ASTM D3518-94 to find in plane shear response of polymer matrix composites materials. 4). Predict flexural properties of sandwich construction which manufactured from basalt facing with PVC foam core according to ASTM C393-94. Material strength properties must be based on enough tests of material to meet the test procedure specifications [1]. For this reason six specimens were manufactured for testing and the tests were performed on them using an INSTRON machine model 5582. In the study, the effect of percent of resin in basalt reinforced composite was investigated. Also the weights of the ballast based composites with different percent of resin were measured with conventional composites. As the weight is an important parameter in aerospace industry when the designer wants to replace one material with another, the effect of weight must be considered. Weight measurement showed that the replacement of glass fabric reinforcement with basalt fabric has little effect on weight. Investigation also shows that mechanical behavior of basalt fabric is higher than glass fabric. This is due to the excellent mechanical properties of the ballast fabric such as Young modulus and strength in compare with the glass fabric. Figure1 shows the samples which used for tensile testing in warp direction.

Child Characteristics and Parental Educational Expectations: Evidence for Transmission with Transaction

PubMed Central

Briley, Daniel A.; Harden, K. Paige; Tucker-Drob, Elliot M.

2014-01-01

Parents’ expectations for their children’s ultimate educational attainment have been hypothesized to play an instrumental role in socializing academically-relevant child behaviors, beliefs, and abilities. In addition to social transmission of educationally relevant values from parents to children, parental expectations and child characteristics may transact bidirectionally. We explore this hypothesis using both longitudinal and genetically informative twin data from the Early Childhood Longitudinal Study –Birth and Kindergarten cohorts. Our behavior genetic results indicate that parental expectations partly reflect child genetic variation, even as early as 4 years of age. Two classes of child characteristics were hypothesized to contribute to these child-to-parent effects: behavioral tendencies (approaches toward learning and problem behaviors) and achievement (math and reading). Using behavior genetic models, we find within-twin-pair associations between these child characteristics and parental expectations. Using longitudinal cross-lagged models, we find that initial variation in child characteristics predicts future educational expectations above and beyond previous educational expectations. These results are consistent with transactional frameworks in which parent-to-child and child-to-parent effects co-occur. PMID:25285965

Child characteristics and parental educational expectations: evidence for transmission with transaction.

PubMed

Briley, Daniel A; Harden, K Paige; Tucker-Drob, Elliot M

2014-12-01

Parents' expectations for their children's ultimate educational attainment have been hypothesized to play an instrumental role in socializing academically relevant child behaviors, beliefs, and abilities. In addition to social transmission of educationally relevant values from parents to children, parental expectations and child characteristics may transact bidirectionally. We explore this hypothesis using both longitudinal and genetically informative twin data from the Early Childhood Longitudinal Study-Birth and Kindergarten cohorts. Our behavior genetic results indicate that parental expectations partly reflect child genetic variation, even as early as 4 years of age. Two classes of child characteristics were hypothesized to contribute to these child-to-parent effects: behavioral tendencies (approaches toward learning and problem behaviors) and achievement (math and reading). Using behavior genetic models, we find within-twin-pair associations between these child characteristics and parental expectations. Using longitudinal cross-lagged models, we find that initial variation in child characteristics predicts future educational expectations above and beyond previous educational expectations. These results are consistent with transactional frameworks in which parent-to-child and child-to-parent effects co-occur. PsycINFO Database Record (c) 2014 APA, all rights reserved.

Influence of physical fitness on cardio-metabolic risk factors in European children. The IDEFICS study.

PubMed

Zaqout, M; Michels, N; Bammann, K; Ahrens, W; Sprengeler, O; Molnar, D; Hadjigeorgiou, C; Eiben, G; Konstabel, K; Russo, P; Jiménez-Pavón, D; Moreno, L A; De Henauw, S

2016-07-01

The aim of the study was to assess the associations of individual and combined physical fitness components with single and clustering of cardio-metabolic risk factors in children. This 2-year longitudinal study included a total of 1635 European children aged 6-11 years. The test battery included cardio-respiratory fitness (20-m shuttle run test), upper-limb strength (handgrip test), lower-limb strength (standing long jump test), balance (flamingo test), flexibility (back-saver sit-and-reach) and speed (40-m sprint test). Metabolic risk was assessed through z-score standardization using four components: waist circumference, blood pressure (systolic and diastolic), blood lipids (triglycerides and high-density lipoprotein) and insulin resistance (homeostasis model assessment). Mixed model regression analyses were adjusted for sex, age, parental education, sugar and fat intake, and body mass index. Physical fitness was inversely associated with clustered metabolic risk (P<0.001). All coefficients showed a higher clustered metabolic risk with lower physical fitness, except for upper-limb strength (β=0.057; P=0.002) where the opposite association was found. Cardio-respiratory fitness (β=-0.124; P<0.001) and lower-limb strength (β=-0.076; P=0.002) were the most important longitudinal determinants. The effects of cardio-respiratory fitness were even independent of the amount of vigorous-to-moderate activity (β=-0.059; P=0.029). Among all the metabolic risk components, blood pressure seemed not well predicted by physical fitness, while waist circumference, blood lipids and insulin resistance all seemed significantly predicted by physical fitness. Poor physical fitness in children is associated with the development of cardio-metabolic risk factors. Based on our results, this risk might be modified by improving mainly cardio-respiratory fitness and lower-limb muscular strength.

Macroscopic anisotropic bone material properties in children with severe osteogenesis imperfecta.

PubMed

Albert, Carolyne; Jameson, John; Tarima, Sergey; Smith, Peter; Harris, Gerald

2017-11-07

Children with severe osteogenesis imperfecta (OI) typically experience numerous fractures and progressive skeletal deformities over their lifetime. Recent studies proposed finite element models to assess fracture risk and guide clinicians in determining appropriate intervention in children with OI, but lack of appropriate material property inputs remains a challenge. This study aimed to characterize macroscopic anisotropic cortical bone material properties and investigate relationships with bone density measures in children with severe OI. Specimens were obtained from tibial or femoral shafts of nine children with severe OI and five controls. The specimens were cut into beams, characterized in bending, and imaged by synchrotron radiation X-ray micro-computed tomography. Longitudinal modulus of elasticity, yield strength, and bending strength were 32-65% lower in the OI group (p<0.001). Yield strain did not differ between groups (p≥0.197). In both groups, modulus and strength were lower in the transverse direction (p≤0.009), but anisotropy was less pronounced in the OI group. Intracortical vascular porosity was almost six times higher in the OI group (p<0.001), but no differences were observed in osteocyte lacunar porosity between the groups (p=0.086). Volumetric bone mineral density was lower in the OI group (p<0.001), but volumetric tissue mineral density was not (p=0.770). Longitudinal OI bone modulus and strength were correlated with volumetric bone mineral density (p≤0.024) but not volumetric tissue mineral density (p≥0.099). Results indicate that cortical bone in children with severe OI yields at the same strain as normal bone, and that their decreased bone material strength is associated with reduced volumetric bone mineral density. These results will enable the advancement of fracture risk assessment capability in children with severe OI. Copyright © 2017 Elsevier Ltd. All rights reserved.