Exploratory Solid-State Synthesis of Uranium Chalcogenides and Mixed Anion Uranium Chalcogenides

NASA Astrophysics Data System (ADS)

Ward, Matthew David

Several uranium chalcogenides and mixed anion uranium chalcogenides have been synthesized by solid-state synthetic methods. Structural determinations were carried out via single-crystal X-ray diffraction. Some of these compounds have been further characterized by magnetic measurements, optical properties measurements, Raman spectroscopy, resistivity measurements, XANES and XPS. Eight compounds of the composition MU8Q17 were synthesized and characterized by single-crystal X-ray diffraction. All of these compounds crystallize in the CrU8S17 structure type. XANES measurements indicate that ScU8S17 contains Sc3+ and must be charge balanced with some amount of U 3+. Two compounds of the composition ATiU3Te9 crystallize as black rectangular plates. From single-crystal magnetic measurements, CsTiU 3Te9 is consistent with antiferromagnetic coupling between magnetic U atoms. The uranium chalcogenide compounds NiUS3 and Cr4US 8 were synthesized from reaction of the elements in various fluxes. NiUS3 crystallizes in the GdFeO3 structure type. Cr 4US8 crystallizes in the orthorhombic space group D - Pnma and its structure is related to that of Li4UF 8. The compounds Rh2U6S15, Cs 2Ti2U6Se15, and Cs2Cr 2U6Se15 crystallize as black prisms in the cubic space group O-Im3m. Magnetic measurements on Cs 2Cr2U6Se15 give a value for the Weiss temperature, θWeiss, of 57.59 K, indicative of ferromagnetic coupling. Black plates of CsScU(Se2)Se3 were synthesized from the reaction of the elements in a CsCl flux. CsScU(Se2)Se 3 crystallizes in the orthorhombic space group D- Cmcm . Magnetic susceptibility measurements on CsScU(Se2)Se 3 indicate three regions of magnetic response. The uranium double salt Cs5[U2(μ-S 2)2Cl8]I crystallizes as red plates. Cs 5[U2(μ-S2)2Cl 8]I displays optical anisotropy with band gap energies of 1.99 eV and 2.08 eV along the [001] and [100] polarizations. The uranium oxychalcogenides U7O2Se12 and Na2Ba2(UO2)S4 were synthesized by intentional oxygen contamination. The structure of U7O 2Se12 is related to the previously reported U7Q 12. Na2Ba2(UO2)S4 contains isolated uranyl polyhedra in which each uranium atom may be assigned an oxidation state of +6. The four uranium(IV) chlorophosphates, UCl4(POCl3), [U2Cl9][PCl4], UCl3(PO2Cl 2), and U2Cl8(POCl3) were synthesized in an effort to synthesize new novel uranyl sulfides. All are unstable, but UCl4(POCl3) is the thermodynamically favorable phase.

Oxidation and crystal field effects in uranium

NASA Astrophysics Data System (ADS)

Tobin, J. G.; Yu, S.-W.; Booth, C. H.; Tyliszczak, T.; Shuh, D. K.; van der Laan, G.; Sokaras, D.; Nordlund, D.; Weng, T.-C.; Bagus, P. S.

2015-07-01

An extensive investigation of oxidation in uranium has been pursued. This includes the utilization of soft x-ray absorption spectroscopy, hard x-ray absorption near-edge structure, resonant (hard) x-ray emission spectroscopy, cluster calculations, and a branching ratio analysis founded on atomic theory. The samples utilized were uranium dioxide (U O2) , uranium trioxide (U O3) , and uranium tetrafluoride (U F4) . A discussion of the role of nonspherical perturbations, i.e., crystal or ligand field effects, will be presented.

Direct observation of pure pentavalent uranium in U2O5 thin films by high resolution photoemission spectroscopy.

PubMed

Gouder, T; Eloirdi, R; Caciuffo, R

2018-05-29

Thin films of the elusive intermediate uranium oxide U 2 O 5 have been prepared by exposing UO 3 precursor multilayers to atomic hydrogen. Electron photoemission spectra measured about the uranium 4f core-level doublet contain sharp satellites separated by 7.9(1) eV from the 4f main lines, whilst satellites characteristics of the U(IV) and U(VI) oxidation states, expected respectively at 6.9(1) and 9.7(1) eV from the main 4f lines, are absent. This shows that uranium ions in the films are in a pure pentavalent oxidation state, in contrast to previous investigations of binary oxides claiming that U(V) occurs only as a metastable intermediate state coexisting with U(IV) and U(VI) species. The ratio between the 5f valence band and 4f core-level uranium photoemission intensities decreases by about 50% from UO 2 to U 2 O 5 , which is consistent with the 5f  2 (UO 2 ) and 5f  1 (U 2 O 5 ) electronic configurations of the initial state. Our studies conclusively establish the stability of uranium pentoxide.

On some factors affecting the nonstoichiometry in U 3O 8

NASA Astrophysics Data System (ADS)

Fujino, Takeo; Tagawa, Hiroaki; Adachi, Takeo

1981-03-01

The nonstoichiometry of U 3O 8 was studied under various conditions. The {O}/{U} atom ratios obtained by the oxidation of uranium metal in air followed by cooling with moderate rates (method 1) are 2.67 ± 0.01 in the temperature range 700 900°C and 2.662 ± 0.005 at 1000°C and are generally larger than the ratio by thermogravimetry. If the oxidation was carried out in a crucible with a lid, a compositional peak was observed at 900 950°C, which did not appear for the U 3O 8 samples from UO 2. The U 3O 8 made from UO 2 by method 1 have {O}/{U} ratios 2.655 ± 0.005 (700° C), 2.653 ± 0.004 (800° C), 2.648 ± 0.004 (900° C) and 2.645 ± 0.003 (1000° C). Differences were observed in the O/U ratios of heating and cooling series. X-ray diffraction analysis showed several additional peaks other than those of α-U 3O 8 for the samples which exhibited the compositional peak.

Thermochemistry of rare earth doped uranium oxides LnxU1-xO2-0.5x+y (Ln = La, Y, Nd)

NASA Astrophysics Data System (ADS)

Zhang, Lei; Navrotsky, Alexandra

2015-10-01

Lanthanum, yttrium, and neodymium doped uranium dioxide samples in the fluorite structure have been synthesized, characterized in terms of metal ratio and oxygen content, and their enthalpies of formation measured by high temperature oxide melt solution calorimetry. For oxides doped with 10-50 mol % rare earth (Ln) cations, the formation enthalpies from constituent oxides (LnO1.5, UO2 and UO3 in a reaction not involving oxidation or reduction) become increasingly exothermic with increasing rare earth content, while showing no significant dependence on the varying uranium oxidation state. The oxidation enthalpy of LnxU1-xO2-0.5x+y is similar to that of UO2 to UO3 for all three rare earth doped systems. Though this may suggest that the oxidized uranium in these systems is energetically similar to that in the hexavalent state, thermochemical data alone can not constrain whether the uranium is present as U5+, U6+, or a mixture of oxidation states. The formation enthalpies from elements calculated from the calorimetric data are generally consistent with those from free energy measurements.

Review of the NURE assessment of the U.S. Gulf Coast Uranium Province

USGS Publications Warehouse

Hall, Susan M.

2013-01-01

Historic exploration and development were used to evaluate the reliability of domestic uranium reserves and potential resources estimated by the U.S. Department of Energy national uranium resource evaluation (NURE) program in the U.S. Gulf Coast Uranium Province. NURE estimated 87 million pounds of reserves in the $30/lb U3O8 cost category in the Coast Plain uranium resource region, most in the Gulf Coast Uranium Province. Since NURE, 40 million pounds of reserves have been mined, and 38 million pounds are estimated to remain in place as of 2012, accounting for all but 9 million pounds of U3O8 in the reserve or production categories in the NURE estimate. Considering the complexities and uncertainties of the analysis, this study indicates that the NURE reserve estimates for the province were accurate. An unconditional potential resource of 1.4 billion pounds of U3O8, 600 million pounds of U3O8 in the forward cost category of $30/lb U3O8 (1980 prices), was estimated in 106 favorable areas by the NURE program in the province. Removing potential resources from the non-productive Houston embayment, and those reserves estimated below historic and current mining depths reduces the unconditional potential resource 33% to about 930 million pounds of U3O8, and that in the $30/lb cost category 34% to 399 million pounds of U3O8. Based on production records and reserve estimates tabulated for the region, most of the production since 1980 is likely from the reserves identified by NURE. The potential resource predicted by NURE has not been developed, likely due to a variety of factors related to the low uranium prices that have prevailed since 1980.

Uranium extremophily is an adaptive, rather than intrinsic, feature for extremely thermoacidophilic Metallosphaera species

PubMed Central

Mukherjee, Arpan; Wheaton, Garrett H.; Blum, Paul H.; Kelly, Robert M.

2012-01-01

Thermoacidophilic archaea are found in heavy metal-rich environments, and, in some cases, these microorganisms are causative agents of metal mobilization through cellular processes related to their bioenergetics. Given the nature of their habitats, these microorganisms must deal with the potentially toxic effect of heavy metals. Here, we show that two thermoacidophilic Metallosphaera species with nearly identical (99.99%) genomes differed significantly in their sensitivity and reactivity to uranium (U). Metallosphaera prunae, isolated from a smoldering heap on a uranium mine in Thüringen, Germany, could be viewed as a “spontaneous mutant” of Metallosphaera sedula, an isolate from Pisciarelli Solfatara near Naples. Metallosphaera prunae tolerated triuranium octaoxide (U3O8) and soluble uranium [U(VI)] to a much greater extent than M. sedula. Within 15 min following exposure to “U(VI) shock,” M. sedula, and not M. prunae, exhibited transcriptomic features associated with severe stress response. Furthermore, within 15 min post-U(VI) shock, M. prunae, and not M. sedula, showed evidence of substantial degradation of cellular RNA, suggesting that transcriptional and translational processes were aborted as a dynamic mechanism for resisting U toxicity; by 60 min post-U(VI) shock, RNA integrity in M. prunae recovered, and known modes for heavy metal resistance were activated. In addition, M. sedula rapidly oxidized solid U3O8 to soluble U(VI) for bioenergetic purposes, a chemolithoautotrophic feature not previously reported. M. prunae, however, did not solubilize solid U3O8 to any significant extent, thereby not exacerbating U(VI) toxicity. These results point to uranium extremophily as an adaptive, rather than intrinsic, feature for Metallosphaera species, driven by environmental factors. PMID:23010932

Uranium in granitic magmas: Part 2. Experimental determination of uranium solubility and fluid-melt partition coefficients in the uranium oxide-haplogranite-H 2O-NaX (X = Cl, F) system at 770°C, 2 kbar

NASA Astrophysics Data System (ADS)

Peiffert, Chantal; nguyen-Trung, Chinh; Cuney, Michel

1996-05-01

The solubility of uranium oxide was investigated in both aqueous halide (Cl, F) fluid and granitic melt in equilibrium in the system uranium oxide-haplogranite-H 2O-NaCl (0.1-5.0 molal), NaF (0.1-0.5 molal) at 770°C, 2 kbar, and fO 2 conditions controlled by Ni-NiO, Fe 3O 4-Fe 2O 3, and Cu 2O- CuO buffers. Three distinct uranium oxides UO (2+ x) with x = 0.01 ± 0.01; 0.12 ± 0.02; and 0.28 ± 0.02, respec- tively, were obtained in both chloride and fluoride systems, under the three fO 2 conditions cited above. Changes in the composition of aqueous solutions and silicate melt were observed after the runs. These changes were more pronounced for the fluoride-bearing experiments. Quench pH decreased from 5.9 to 2.1 with increasing chloride molality from 0.085-4.38 molal. For fluoride solutions, the decrease of pH from 5.4 to 3.4 corresponded to the increase of fluoride molality from 0.02-0.23 molal. The U solubility in chloride solutions was in the range 10-967 ppm. For the same molality, fluoride solutions appeared to dissolve up to twenty times more uranium than chloride solutions. The increase of halide molality and oxidation led to increase the U solubility. The U solubility in silicate glasses was in the range 10-1.8 × 10 4 ppm and increased with increasing oxidation and halide concentration. In addition, increasing agpaicity also increased U solubility in the chloride system. This effect was not observed in the fluoride system. The chloride concentration in the silicate melt increased from 100-790 ppm with increasing initial aqueous chloride concentration from 0.1-5.0 m. The fluoride concentration in the silicate melt increased from 2.8 × 10 3 to 1.1 × 10 4 ppm with increasing initial fluoride concentra- tion from 0.1-0.5 m. In the chloride system, the partition coefficient of U (log D)(U) fluid/melt) increased from -1.2-0 with increasing agpaicity from 0.92-1.36, for increasing chloride concentration from 0.085-4.38 molal and for increasing fO 2 from 10 -15 to 10 -4 bar. In the fluoride system, a linear correlation was established between the partition coefficient of U and the log fO 2. In F-rich system, D(U) fluid/melt values was in the range 2.4 × 10 -2-4.2 × 10 -2 for increasing fluoride concentration from 0.02-0.22 molal and for the same increasing of fO 2. In the chloride system, the partition coefficients of Na ( D (Na) fluid/melt) and K ( D) (K) fluid/melt) are in good agreement up to 1.0 m NaCl with the two linear equations established by Holland (1972) : D (Na) fluid/melt = 0.46 × (Cl)(m) (1) and D(Na) fluid/melt = 0.34 × (Cl)(m) (2). However, in initial 5.0 m NaCl, slopes of Eqns. 1 and 2 decreased to 0.41 and 0.16, respectively. Data obtained in the present study provide useful information for the understanding of the behaviour of U in the fractionation processes of halide rich magmas. Fluid/melt partition coefficients higher than one, favorable for the genesis of magmatic U mineralization, can be reached for peraluminous leucogran- ites in equilibrium with chloride-rich solutions.

A series of uranium (IV, V, VI) tritylimido complexes, their molecular and electronic structures and reactivity with CO2.

PubMed

Schmidt, Anna-Corina; Heinemann, Frank W; Maron, Laurent; Meyer, Karsten

2014-12-15

A series of uranium tritylimido complexes with structural continuity across complexes in different oxidation states, namely U(IV), U(V), and U(VI), is reported. This series was successfully synthesized by employing the trivalent uranium precursor, [(((nP,Me)ArO)3tacn)U(III)] (1) (where ((nP,Me)ArO)3tacn(3-) = trianion of 1,4,7-tris(2-hydroxy-5-methyl-3-neopentylbenzyl)-1,4,7-triazacyclononane), with the organic azides Me3SiN3, Me3SnN3, and Ph3CN3 (tritylazide). While the reaction with Me3SiN3 yields an inseparable mixture of both the azido and imido uranium complexes, applying the heavier Sn homologue yields the bis-μ-azido complex [{(((nP,Me)ArO)3tacn)U(IV)}2(μ-N3)2] (2) exclusively. In contrast to this one-electron redox chemistry, the reaction of precursor 1 with tritylazide solely leads to the two-electron oxidized U(V) imido [(((nP,Me)ArO)3tacn)U(V)(N-CPh3)] (3). Oxidation and reduction of 3 yield the corresponding U(VI) and U(IV) complexes [(((nP,Me)ArO)3tacn)U(VI)(N-CPh3)][B(C6F5)4] (4) and K[(((nP,Me)ArO)3tacn)U(IV)(N-CPh3)] (5), respectively. In addition, the U(V) imido 3 engages in a H atom abstraction reaction with toluene to yield the closely related amido complex [(((nP,Me)ArO)3tacn)U(IV)(N(H)-CPh3)] (6). Complex 6 and the three tritylimido complexes 3, 4, and 5, with oxidation states ranging from +IV to +VI and homologous core structures, were investigated by X-ray diffraction analyses and magnetochemical and spectroscopic studies as well as density functional theory (DFT) computational analysis. The series of structurally very similar imido complexes provides a unique opportunity to study electronic properties and to probe the uranium imido reactivity solely as a function of electron count of the metal-imido entity. Evidence for the U-N bond covalency and f-orbital participation in complexes 3-6 was drawn from the in-depth and comparative DFT study. The reactivity of the imido and amido complexes with CO2 was probed, and conclusions about the influence of the formal oxidation state are reported.

Oxidative Uranium Release from Anoxic Sediments under Diffusion-Limited Conditions.

PubMed

Bone, Sharon E; Cahill, Melanie R; Jones, Morris E; Fendorf, Scott; Davis, James; Williams, Kenneth H; Bargar, John R

2017-10-03

Uranium (U) contamination occurs as a result of mining and ore processing; often in alluvial aquifers that contain organic-rich, reduced sediments that accumulate tetravalent U, U(IV). Uranium(IV) is sparingly soluble, but may be mobilized upon exposure to nitrate (NO 3 - ) and oxygen (O 2 ), which become elevated in groundwater due to seasonal fluctuations in the water table. The extent to which oxidative U mobilization can occur depends upon the transport properties of the sediments, the rate of U(IV) oxidation, and the availability of inorganic reductants and organic electron donors that consume oxidants. We investigated the processes governing U release upon exposure of reduced sediments to artificial groundwater containing O 2 or NO 3 - under diffusion-limited conditions. Little U was mobilized during the 85-day reaction, despite rapid diffusion of groundwater within the sediments and the presence of nonuraninite U(IV) species. The production of ferrous iron and sulfide in conjunction with rapid oxidant consumption suggested that the sediments harbored large concentrations of bioavailable organic carbon that fueled anaerobic microbial respiration and stabilized U(IV). Our results suggest that seasonal influxes of O 2 and NO 3 - may cause only localized mobilization of U without leading to export of U from the reducing sediments when ample organic carbon is present.

Review of the NURE Assessment of the U.S. Gulf Coast Uranium Province

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hall, Susan M., E-mail: SusanHall@usgs.gov

2013-09-15

Historic exploration and development were used to evaluate the reliability of domestic uranium reserves and potential resources estimated by the U.S. Department of Energy national uranium resource evaluation (NURE) program in the U.S. Gulf Coast Uranium Province. NURE estimated 87 million pounds of reserves in themore » $$30/lb U{sub 3}O{sub 8} cost category in the Coast Plain uranium resource region, most in the Gulf Coast Uranium Province. Since NURE, 40 million pounds of reserves have been mined, and 38 million pounds are estimated to remain in place as of 2012, accounting for all but 9 million pounds of U{sub 3}O{sub 8} in the reserve or production categories in the NURE estimate. Considering the complexities and uncertainties of the analysis, this study indicates that the NURE reserve estimates for the province were accurate. An unconditional potential resource of 1.4 billion pounds of U{sub 3}O{sub 8}, 600 million pounds of U{sub 3}O{sub 8} in the forward cost category of $$30/lb U{sub 3}O{sub 8} (1980 prices), was estimated in 106 favorable areas by the NURE program in the province. Removing potential resources from the non-productive Houston embayment, and those reserves estimated below historic and current mining depths reduces the unconditional potential resource 33% to about 930 million pounds of U{sub 3}O{sub 8}, and that in the $30/lb cost category 34% to 399 million pounds of U{sub 3}O{sub 8}. Based on production records and reserve estimates tabulated for the region, most of the production since 1980 is likely from the reserves identified by NURE. The potential resource predicted by NURE has not been developed, likely due to a variety of factors related to the low uranium prices that have prevailed since 1980.« less

PROCESS FOR PRODUCING URANIUM HALIDES

DOEpatents

Murphree, E.V.

1957-10-29

A process amd associated apparatus for producing UF/sub 4/ from U/sub 3/ O/sub 8/ by a fluidized'' technique are reported. The U/sub 3/O/sub 8/ is first reduced to UO/sub 2/ by reaction with hydrogen, and the lower oxide of uranium is then reacted with gaseous HF to produce UF/sub 4/. In each case the reactant gas is used, alone or in combination with inert gases, to fluidize'' the finely divided reactant solid. The complete setup of the plant equipment including bins, reactor and the associated piping and valving, is described. An auxiliary fluorination reactor allows for the direct production of UF/sub 6/ from UF/sub 4/ and fluorine gas, or if desired, UF/sub 4/ may be collected as the product.

Oxidation of U-20 at% Zr alloy in air at 423 1063 K

NASA Astrophysics Data System (ADS)

Matsui, Tsuneo; Yamada, Takanobu; Ikai, Yasushi; Naito, Keiji

1993-01-01

The oxidation behavior of U 0.80Zr 0.20 alloy (two-phase mixture of U and UZr 2 below 878 K and single solid solution above 1008 K) was studied by thermogravimetry in the temperature range from 423 to 1063 K in air. During oxidation in the low temperature region (423-503 K), the sample kept its initial shape (a rectangular rod) and the surface of the sample was covered by a black thin adherent UO2 + x oxide layer. On the other hand, by oxidation in the middle temperature region, the sample broke to several pieces of thin plates and blocks, and fine powder at 643-723 K and entirely to fine powder at 775-878 K, all of which were analyzed to be a mixture of U 3O 8 and ZrO 2. By oxidation in the high temperature region (1008-1063 K) the sample broke to very fine powder, which consisted of U 3O 8 and ZrO 2. Based on the sample shape, the oxide phase identified after oxidation and the slope value of the bilogarithmic plots of the weight gain against time, the oxidation kinetics was analyzed with a paralinear equation in the low temperature region below 503 K and a linear equation in the middle and high temperature regions above 643 K. Oxidation rates of U 0.80Zr 0.20 (two-phase mixture) in the low and middle temperature regions were smaller than those of uranium metal. A discontinuity in the plot of the linear oxidation rate constant versus reciprocal temperature was found to be present between 723 and 838 K, similarly to the case of uranium metal previously reported. The linear rate constants of single-phase solid solution in the high temperature region above 1008 K seemed to be a little smaller than those estimated by the extrapolation of the values in the middle temperature region.

Nuclear forensic analysis of uranium oxide powders interdicted in Victoria, Australia

DOE PAGES

Kristo, Michael Joseph; Keegan, Elizabeth; Colella, Michael; ...

2015-04-13

Nuclear forensic analysis was conducted on two uranium samples confiscated during a police investigation in Victoria, Australia. The first sample, designated NSR-F-270409-1, was a depleted uranium powder of moderate purity (~1000 μg/g total elemental impurities). The chemical form of the uranium was a compound similar to K 2(UO 2) 3O 4·4H 2O. While aliquoting NSR-F-270409-1 for analysis, the body and head of a Tineid moth was discovered in the sample. The second sample, designated NSR-F-270409-2, was also a depleted uranium powder. It was of reasonably high purity (~380 μg/g total elemental impurities). The chemical form of the uranium was primarilymore » UO 3·2H 2O, with minor phases of U 3O 8 and UO 2. While aliquoting NSR-F-270409-2 for analysis, a metal staple of unknown origin was discovered in the sample. The presence of 236U and 232U in both samples indicates that the uranium feed stocks for these samples experienced a neutron flux at some point in their history. The reactor burn-up calculated from the isotopic composition of the uranium is consistent with that of spent fuel from natural uranium (NU) fueled Pu production. These nuclear forensic conclusions allow us to categorically exclude Australia as the origin of the material and greatly reduce the number of candidate sources.« less

PROGRESS REPORT ON GEOLOGIC STUDIES OF THE RANGER OREBODIES, NORTHERN TERRITORY, AUSTRALIA.

USGS Publications Warehouse

Nash, J. Thomas; Frishman, David; ,

1985-01-01

The Ranger No. 1 and No. 3 orebodies contain about 124,000 tonnes U//3O//8 in highly chloritized metasediments of the lower Proterozoic Cahill Formation within about 500 m of the projected sub-Kombolgie Formation unconformity. In both orebodies, oxidized and reduced uranium minerals occur chiefly in quartzose schists that have highly variable amounts of muscovite, sericite, and chlorite. The effects of several periods of alteration are pervasive in the vicinity of orebodies where biotite and garnet are altered to chlorite, and feldspars to white mica or chlorite. Oxidized uranium minerals, associated with earthy iron oxides, occur from the surface to a depth of about 60 m. Below the oxidized zone, uranium occurs chiefly as uraninite and pitchblende disseminated through thick sections of quartz-chlorite-muscovite schist and has no apparent association with graphite or sulphides. The geologic age(s) of uranium emplacement are obscure because there are few age criteria. Reduced uranium minerals are younger than 1. 8-b. y. -old granite dykes, and some occur locally in 1. 65-b. y. -old Kombolgie Formation.

LOW-TEMPERATURE MAGNETIC PROPERTIES OF SOME URANIUM OXIDES

DOE Office of Scientific and Technical Information (OSTI.GOV)

Leask, M.J.M.; Roberts, L.E.J.; Walter, A.J.

1963-10-01

The magnetic susceptibilities of UO/sub 2/, UO/sub 2.1/, U/sub 4/O/sub 9/ , U/s ub 3/O/sub 7/, and U/sub 3/O/sub 8/ at temperatures between 1.5 and 44 deg K were determined using an a-c inductance method. The susceptibility Of U/sub 3/ O/sub 8/ rises to a sharp maximum at 4.2 deg K, with smaller effects at 8 and at 25.3 deg K. The susceptibility of UO/sub 2/ reaches a maximum at 29 deg K and remains constant between 25 and 2 deg K. A maximum in the susceptibility- temperature plot for U/sub 4/O/sub 9/ at 6.4 deg K occurs also-in themore » plots for UO/sub 2.1/ an d U/sub 3/O/sub 7/ and appears to be primarily due to the inclusion of interstitial oxygen ions in the UO/sub 2/ lattice, independent of the precise nature of subsequent ordering effects. (auth)« less

Density functional theory calculations of UO2 oxidation: evolution of UO(2+x), U4O(9-y), U3O7, and U3O8.

PubMed

Andersson, D A; Baldinozzi, G; Desgranges, L; Conradson, D R; Conradson, S D

2013-03-04

Formation of hyperstoichiometric uranium dioxide, UO2+x, derived from the fluorite structure was investigated by means of density functional theory (DFT) calculations. Oxidation was modeled by adding oxygen atoms to UO2 fluorite supercells. For each compound ab initio molecular dynamics simulations were performed to allow the ions to optimize their local geometry. A similar approach was used for studying the reduction of U3O8. In agreement with the experimental phase diagram we identify stable line compounds at the U4O9-y and U3O7 stoichiometries. Although the transition from fluorite to the layered U3O8 structure occurs at U3O7 (UO2.333) or U3O7.333 (UO2.444), our calculated low temperature phase diagram indicates that the fluorite derived compounds are favored up to UO2.5, that is, as long as the charge-compensation for adding oxygen atoms occurs via formation of U(5+) ions, after which the U3O8-y phase becomes more stable. The most stable fluorite UO2+x phases at low temperature (0 K) are based on ordering of split quad-interstitial oxygen clusters. Most existing crystallographic models of U4O9 and U3O7, however, apply the cuboctahedral cluster. To better understand these discrepancies, the new structural models are analyzed in terms of existing neutron diffraction data. DFT calculations were also performed on the experimental cuboctahedral based U4O9-y structure, which enable comparisons between the properties of this phase with the quad-interstitial ones in detail.

EXTRACTION OF URANIUM

DOEpatents

Kesler, R.D.; Rabb, D.D.

1959-07-28

An improved process is presented for recovering uranium from a carnotite ore. In the improved process U/sub 2/O/sub 5/ is added to the comminuted ore along with the usual amount of NaCl prior to roasting. The amount of U/sub 2/O/ sub 5/ is dependent on the amount of free calcium oxide and the uranium in the ore. Specifically, the desirable amount of U/sub 2/O/sub 5/ is 3.2% for each 1% of CaO, and 5 to 6% for each 1% of uranium. The mixture is roasted at about 1560 deg C for about 30 min and then leached with a 3 to 9% aqueous solution of sodium carbonate.

In vitro dissolution of uranium oxide by baboon alveolar macrophages.

PubMed Central

Poncy, J L; Metivier, H; Dhilly, M; Verry, M; Masse, R

1992-01-01

In vitro cellular dissolution tests for insoluble forms of uranium oxide are technically difficult with conventional methodology using adherent alveolar macrophages. The limited number of cells per flask and the slow dissolution rate in a large volume of nutritive medium are obvious restricting factors. Macrophages in suspension cannot be substituted because they represent different and poorly reproducible functional subtypes with regard to activation and enzyme secretion. Preliminary results on the dissolution of uranium oxide using immobilized alveolar macrophages are promising because large numbers of highly functional macrophages can be cultured in a limited volume. Cells were obtained by bronchoalveolar lavages performed on baboons (Papio papio) and then immobilized after the phagocytosis of uranium octoxide (U3O8) particles in alginate beads linked with Ca2+. The dissolution rate expressed as percentage of initial uranium content in cells was 0.039 +/- 0.016%/day for particles with a count median geometric diameter of 3.84 microns(sigma g = 1.84). A 2-fold increase in the dissolution rate was observed when the same number of particles was immobilized without macrophages. These results, obtained in vitro, suggest that the U3O8 preparation investigated should be assigned to inhalation class Y as recommended by the International Commission on Radiological Protection. Future experiments are intended to clarify this preliminary work and to examine the dissolution characteristics of other particles such as uranium dioxide. It is recommended that the dissolution rate should be measured over an interval of 3 weeks, which is compatible with the survival time of immobilized cells in culture and may reveal transformation states occurring with aging of the particles. PMID:1396447

Method of preparing uranium nitride or uranium carbonitride bodies

DOEpatents

Wilhelm, Harley A.; McClusky, James K.

1976-04-27

Sintered uranium nitride or uranium carbonitride bodies having a controlled final carbon-to-uranium ratio are prepared, in an essentially continuous process, from U.sub.3 O.sub.8 and carbon by varying the weight ratio of carbon to U.sub.3 O.sub.8 in the feed mixture, which is compressed into a green body and sintered in a continuous heating process under various controlled atmospheric conditions to prepare the sintered bodies.

Morphology of U 3O 8 materials following storage under controlled conditions of temperature and relative humidity

DOE PAGES

Tamasi, Alison L.; Cash, Leigh J.; Mullen, William Tyler; ...

2016-07-05

Changes in the visual characteristics of uranium oxide surfaces and morphology following storage under different conditions of temperature and relative humidity may provide insight into the history of an unknown sample. Sub-samples of three α-U 3O 8 materials—one that was phase-pure and two that were phase-impure—were stored under controlled conditions for two years. We used scanning electron microscopy to image the oxides before and after storage, and a morphology lexicon was used to characterize the images. Finally, temporal changes in morphology were observed in some sub-samples, and changes were greatest following exposure to high relative humidity.

Extended study on oxidation behaviors of UN0.68 and UN1.66 by XPS

NASA Astrophysics Data System (ADS)

Luo, Lizhu; Hu, Yin; Pan, Qifa; Long, Zhong; Lu, Lei; Liu, Kezhao; Wang, Xiaolin

2018-04-01

The surface oxidation behaviors of UN0.68 and UN1.66 thin films are investigated by X-ray photoelectron spectroscopy (XPS), and the traditional U4f/N1s, O1s, valence band spectra as well as the unconventional U4d and U5d spectra are collected for the understanding of their oxidation behavior in-depth. Similar asymmetrical peak shape of the U4f spectra to uranium is observed for both uranium nitrides, despite of a slight shift to higher energy side for UN1.66 clean surface. However, significant difference among the corresponding spectra of UN0.68 and UN1.66 during oxidation reveals the distinctive properties of each own. The coexistence of UO2-x, UO2 and UO2-x.Ny on UN0.68 surface results in the peculiar features of U4f spectra as well as the others within the XPS energy scale, where peaks of the oxidized species firstly shift to higher energy side compared to the clean surface, and then return closely towards those of stoichiometric UO2. For UN1.66, the generation of U-N-O ternary compounds on the surface is identified with the symmetrical U4f peaks at 379.9eV and 390.8 eV, which locate intermediate between UO2 and UN1.66, and gradually expanding to higher energy side during the progressive oxidation. Furthermore, the formation of N-O species on UN1.66 surface is also detected as an oxidation product. The metallic character of UN1.66 is identified by the intense signal at Fermi level, which is greatly suppressed by the increasing oxygen exposure and implies the weakening metallic properties of the as-generated U-N-O compounds. Higher uranium oxides, such as UO3 and U4O9, are deduced to be the final oxidation products, and a multistage mechanism for UN1.66 following the exposure to oxygen is discussed.

Uranium-mediated electrocatalytic dihydrogen production from water

NASA Astrophysics Data System (ADS)

Halter, Dominik P.; Heinemann, Frank W.; Bachmann, Julien; Meyer, Karsten

2016-02-01

Depleted uranium is a mildly radioactive waste product that is stockpiled worldwide. The chemical reactivity of uranium complexes is well documented, including the stoichiometric activation of small molecules of biological and industrial interest such as H2O, CO2, CO, or N2 (refs 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11), but catalytic transformations with actinides remain underexplored in comparison to transition-metal catalysis. For reduction of water to H2, complexes of low-valent uranium show the highest potential, but are known to react violently and uncontrollably forming stable bridging oxo or uranyl species. As a result, only a few oxidations of uranium with water have been reported so far; all stoichiometric. Catalytic H2 production, however, requires the reductive recovery of the catalyst via a challenging cleavage of the uranium-bound oxygen-containing ligand. Here we report the electrocatalytic water reduction observed with a trisaryloxide U(III) complex [((Ad,MeArO)3mes)U] (refs 18 and 19)—the first homogeneous uranium catalyst for H2 production from H2O. The catalytic cycle involves rare terminal U(IV)-OH and U(V)=O complexes, which have been isolated, characterized, and proven to be integral parts of the catalytic mechanism. The recognition of uranium compounds as potentially useful catalysts suggests new applications for such light actinides. The development of uranium-based catalysts provides new perspectives on nuclear waste management strategies, by suggesting that mildly radioactive depleted uranium—an abundant waste product of the nuclear power industry—could be a valuable resource.

Structure and thermodynamics of uranium-containing iron garnets

NASA Astrophysics Data System (ADS)

Guo, Xiaofeng; Navrotsky, Alexandra; Kukkadapu, Ravi K.; Engelhard, Mark H.; Lanzirotti, Antonio; Newville, Matthew; Ilton, Eugene S.; Sutton, Stephen R.; Xu, Hongwu

2016-09-01

Use of crystalline garnet as a waste form phase appears to be advantageous for accommodating actinides from nuclear waste. Previous studies show that large amounts of uranium (U) and its analogues such as cerium (Ce) and thorium (Th) can be incorporated into the garnet structure. In this study, we synthesized U loaded garnet phases, Ca3UxZr2-xFe3O12 (x = 0.5-0.7), along with the endmember phase, Ca3(Zr2)SiFe3+2O12, for comparison. The oxidation states of U were determined by X-ray photoelectron and absorption spectroscopies, revealing the presence of mixed pentavalent and hexavalent uranium in the phases with x = 0.6 and 0.7. The oxidation states and coordination environments of Fe were measured using transmission 57Fe-Mössbauer spectroscopy, which shows that all iron is tetrahedrally coordinated Fe3+. U substitution had a significant effect on local environments, the extent of U substitution within this range had a minimal effect on the structure, and unlike in the x = 0 sample, Fe exists in two different environments in the substituted garnets. The enthalpies of formation of garnet phases from constituent oxides and elements were first time determined by high temperature oxide melt solution calorimetry. The results indicate that these substituted garnets are thermodynamically stable under reducing conditions. Our structural and thermodynamic analysis further provides explanation for the formation of natural uranium garnet, elbrusite-(Zr), and supports the potential use of Ca3UxZr2-xFe3O12 as viable waste form phases for U and other actinides.

Structure and thermodynamics of uranium-containing iron garnets

DOE PAGES

Guo, Xiaofeng; Navrotsky, Alexandra; Kukkadapu, Ravi K.; ...

2016-09-15

Use of crystalline garnet as a waste form phase appears to be advantageous for accommodating actinides from nuclear waste. Previous studies show that large amounts of uranium (U) and its analogues such as cerium (Ce) and thorium (Th) can be incorporated into the garnet structure. In this study, we synthesized U loaded garnet phases, Ca 3U xZr 2–xFe 3O 12 (x = 0.5–0.7), along with the endmember phase, Ca 3(Zr 2)SiFe 3+ 2O 12, for comparison. The oxidation states of U were determined by X-ray photoelectron and absorption spectroscopies, revealing the presence of mixed pentavalent and hexavalent uranium in themore » phases with x = 0.6 and 0.7. The oxidation states and coordination environments of Fe were measured using transmission 57Fe-Mössbauer spectroscopy, which shows that all iron is tetrahedrally coordinated Fe 3+. U substitution had a significant effect on local environments, the extent of U substitution within this range had a minimal effect on the structure, and unlike in the x = 0 sample, Fe exists in two different environments in the substituted garnets. The enthalpies of formation of garnet phases from constituent oxides and elements were first time determined by high temperature oxide melt solution calorimetry. The results indicate that these substituted garnets are thermodynamically stable under reducing conditions. Furthermore, our structural and thermodynamic analysis further provides explanation for the formation of natural uranium garnet, elbrusite-(Zr), and supports the potential use of Ca 3U xZr 2–xFe 3O 12 as viable waste form phases for U and other actinides.« less

Uranium Isotopic Ratio Measurements of U3O8 Reference Materials by Atom Probe Tomography

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fahey, Albert J.; Perea, Daniel E.; Bartrand, Jonah AG

2016-01-01

We report results of measurements of isotopic ratios obtained with atom probe tomography on U3O8 reference materials certified for their isotopic abundances of uranium. The results show good agreement with the certified values. High backgrounds due to tails from adjacent peaks complicate the measurement of the integrated peak areas as well as the fact that only oxides of uranium appear in the spectrum, the most intense of which is doubly charged. In addition, lack of knowledge of other instrumental parameters, such as the dead time, may bias the results. Isotopic ratio measurements can be performed at the nanometer-scale with themore » expectation of sensible results. The abundance sensitivity and mass resolving power of the mass spectrometer are not sufficient to compete with magnetic-sector instruments but are not far from measurements made by ToF-SIMS of other isotopic systems. The agreement of the major isotope ratios is more than sufficient to distinguish most anthropogenic compositions from natural.« less

Thermal properties of nonstoichiometry uranium dioxide

NASA Astrophysics Data System (ADS)

Kavazauri, R.; Pokrovskiy, S. A.; Baranov, V. G.; Tenishev, A. V.

2016-04-01

In this paper, was developed a method of oxidation pure uranium dioxide to a predetermined deviation from the stoichiometry. Oxidation was carried out using the thermogravimetric method on NETZSCH STA 409 CD with a solid electrolyte galvanic cell for controlling the oxygen potential of the environment. 4 samples uranium oxide were obtained with a different ratio of oxygen-to-metal: O / U = 2.002, O / U = 2.005, O / U = 2.015, O / U = 2.033. For the obtained samples were determined basic thermal characteristics of the heat capacity, thermal diffusivity, thermal conductivity. The error of heat capacity determination is equal to 5%. Thermal diffusivity and thermal conductivity of the samples decreased with increasing deviation from stoichiometry. For the sample with O / M = 2.033, difference of both values with those of stoichiometric uranium dioxide is close to 50%.

Structure and thermodynamic stability of UTa 3 O 10 , a U( v )-bearing compound

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guo, Xiaofeng; Lipp, Christian; Tiferet, Eitan

Heating a mixture of uranyl(VI) nitrate and tantalum(V) oxide in the molar ratio of 2 : 3 to 1400 °C resulted in the formation of a new compound, UTa 3O 10. The honey colored to yellow brown crystals of UTa 3O 10 crystallize in an orthorhombic structure with the space group Fddd (no. 70), lattice parameters a = 7.3947(1), b = 12.7599(2), c = 15.8156(2) Å, and Z = 8. Vertex sharing [TaO 6] 7- octahedra of two crystallographically distinct Ta cations form a three dimensional tantalate framework. Within this framework, six membered rings of [TaO 6] 7- octahedra aremore » formed within the (001) plane. The center of these rings is occupied by the uranyl cations [UO 2] +, with an oxidation state of +5 for uranium. The pentavalence of U and Ta was confirmed by X-ray photoelectron spectroscopy and X-ray adsorption spectroscopy. The enthalpy of formation of UTa 3O 10 from Ta 2O 5, β-U 3O 7, and U 3O 8 has been determined to be 13.1 ± 18.1 kJ mol -1 using high temperature oxide melt solution calorimetry with sodium molybdate as the solvent at 700 °C. The close to zero enthalpy of formation of UTa 3O 10 can be explained by closely balanced structural stabilizing and destabilizing factors, which may also apply to other UM 3O 10 compounds.« less

Uranium mineralization in the Wilson Creek and Cranberry Gneisses and the Grandfather Mountain Formation, North Carolina and Tennessee. National Uranium Resource Evaluation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wagener, H.D.; McHone, J.G.

1982-10-01

Detailed petrologic investigations were conducted at 74 anomalies that have surface radioactivities of 5 to 300 times background in the Grandfather Mountain region of North Carolina and Tennessee. One or more specimens of radioactive rock and one specimen of nonanomalous (barren) rock were taken for chemical analysis from each of the 74 sites. The specimens were analyzed fluorometrically for uranium (U/sub 3/O/sub 8/) and for 29 other elements by emission spectroscopy. Of the radioactive specimens, 23 contained less than 100 ppM U/sub 3/O/sub 8/ and were either depleted in uranium because of leaching or were rich in thorium; 25 containedmore » more than 500 ppM U/sub 3/O/sub 8/, with a maximum of 33,000 ppM. Specimens collected as barren contained up to 65 ppM U/sub 3/O/sub 8/. The more uraniferous rocks of the region tend to contain the larger concentrations of trace amounts of base metals.« less

THE ANALYSIS OF URANIUM-ZIRCONIUM ALLOYS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Milner, G.W.C.; Skewies, A.F.

1953-03-01

A satisfactory procedure is described for the analysis of uranium-zirconium alloys containing up to 25% zirconium. It is based on the separation of the zirconium from the uranium by dissolving the cupferron complex of the former element into chloroform. After the evaporation of the solvent from the combined organic extracts, the residue is ignited to zirconium oxide. The latter is then re-dissolved and zirconium is separated from other elements co-extracted in the solvent extraction procedure by precipitation with mandelic acid. The zirconium mandelate is finally ignited to oxide at 960 deg C. The uranium is separated from the aqueous solutionmore » remaining from the cupferron extraction by precipitating with tannin at a pH of 8; the precipitate being removed by filtration and then ignited a t 800 deg C. The residue is dissolved in nitric acid and the uranium is finally determined by precipitating as ammonium diuranate and then igniting to U{sub 3}O{sub 8}. (auth)« less

Physicochemical characterization of Capstone depleted uranium aerosols III: morphologic and chemical oxide analyses.

PubMed

Krupka, Kenneth M; Parkhurst, Mary Ann; Gold, Kenneth; Arey, Bruce W; Jenson, Evan D; Guilmette, Raymond A

2009-03-01

The impact of depleted uranium (DU) penetrators against an armored target causes erosion and fragmentation of the penetrators, the extent of which is dependent on the thickness and material composition of the target. Vigorous oxidation of the DU particles and fragments creates an aerosol of DU oxide particles and DU particle agglomerations combined with target materials. Aerosols from the Capstone DU aerosol study, in which vehicles were perforated by DU penetrators, were evaluated for their oxidation states using x-ray diffraction (XRD), and particle morphologies were examined using scanning electron microscopy/energy dispersive spectroscopy (SEM/EDS). The oxidation state of a DU aerosol is important as it offers a clue to its solubility in lung fluids. The XRD analysis showed that the aerosols evaluated were a combination primarily of U3O8 (insoluble) and UO3 (relatively more soluble) phases, though intermediate phases resembling U4O9 and other oxides were prominent in some samples. Analysis of particle residues in the micrometer-size range by SEM/EDS provided microstructural information such as phase composition and distribution, fracture morphology, size distribution, and material homogeneity. Observations from SEM analysis show a wide variability in the shapes of the DU particles. Some of the larger particles were spherical, occasionally with dendritic or lobed surface structures. Others appear to have fractures that perhaps resulted from abrasion and comminution, or shear bands that developed from plastic deformation of the DU material. Amorphous conglomerates containing metals other than uranium were also common, especially with the smallest particle sizes. A few samples seemed to contain small bits of nearly pure uranium metal, which were verified by EDS to have a higher uranium content exceeding that expected for uranium oxides. Results of the XRD and SEM/EDS analyses were used in other studies described in this issue of Health Physics to interpret the results of lung solubility studies and in selecting input parameters for dose assessments.

Physicochemical Characterization of Capstone Depleted Uranium Aerosols III: Morphologic and Chemical Oxide Analyses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Krupka, Kenneth M.; Parkhurst, MaryAnn; Gold, Kenneth

2009-03-01

The impact of depleted uranium (DU) penetrators against an armored target causes erosion and fragmentation of the penetrators, the extent of which is dependent on the thickness and material composition of the target. Vigorous oxidation of the DU particles and fragments creates an aerosol of DU oxide particles and DU particle agglomerations combined with target materials. Aerosols from the Capstone DU aerosol study, in which vehicles were perforated by DU penetrators, were evaluated for their oxidation states using X-ray diffraction (XRD) and particle morphologies using scanning electron microscopy/energy dispersive spectrometry (SEM/EDS). The oxidation state of a DU aerosol is importantmore » as it offers a clue to its solubility in lung fluids. The XRD analysis showed that the aerosols evaluated were a combination primarily of U3O8 (insoluble) and UO3 (relatively more soluble) phases, though intermediate phases resembling U4O9 and other oxides were prominent in some samples. Analysis of particle residues in the micrometer-size range by SEM/EDS provided microstructural information such as phase composition and distribution, fracture morphology, size distribution, and material homogeneity. Observations from SEM analysis show a wide variability in the shapes of the DU particles. Some of the larger particles appear to have been fractured (perhaps as a result of abrasion and comminution); others were spherical, occasionally with dendritic or lobed surface structures. Amorphous conglomerates containing metals other than uranium were also common, especially with the smallest particle sizes. A few samples seemed to contain small chunks of nearly pure uranium metal, which were verified by EDS to have a higher uranium content exceeding that expected for uranium oxides. Results of the XRD and SEM/EDS analyses were used in other studies described in this issue of The Journal of Health Physics to interpret the results of lung solubility studies and in selecting input parameters for dose assessments.« less

Potential uranium supply from phosphoric acid: A U.S. analysis comparing solvent extraction and Ion exchange recovery

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Haeyeon; G. Eggert, Roderick; W. Carlsen, Brett

Phosphate rock contains significant amounts of uranium, although in low concentrations. Recovery of uranium as a by-product from phosphoric acid, an intermediate product produced during the recovery of phosphorus from phosphate rock, is not unprecedented. Phosphoric acid plants ceased to produce uranium as a by-product in the early 1990s with the fall of uranium prices. In the last decade, this topic has regained attention due to higher uranium prices and expected increase in demand for uranium. Our study revisits the topic and estimates how much uranium might be recoverable from current phosphoric acid production in the United States and whatmore » the associated costs might be considering two different recovery processes: solvent extraction and ion exchange. Based on U.S. phosphoric acid production in 2014, 5.5 million pounds of U 3O 8 could have been recovered, more than domestic U.S. mine production of uranium in the same year. Annualized costs for a hypothetical uranium recovery plant are US$48-66 per pound U 3O 8 for solvent extraction, the process used historically in the United States to recover uranium from phosphoric acid. For ion exchange, not yet proven at a commercial scale for uranium recovery, the estimated costs are US$33-54 per pound U 3O 8. Our results suggest that it is technically possible for the United States to recover significant quantities of uranium from current phosphoric acid production. And for this type of uranium production to be economically attractive on a large scale, either recovery costs must fall or uranium prices rise.« less

Potential uranium supply from phosphoric acid: A U.S. analysis comparing solvent extraction and Ion exchange recovery

DOE PAGES

Kim, Haeyeon; G. Eggert, Roderick; W. Carlsen, Brett; ...

2016-06-16

Phosphate rock contains significant amounts of uranium, although in low concentrations. Recovery of uranium as a by-product from phosphoric acid, an intermediate product produced during the recovery of phosphorus from phosphate rock, is not unprecedented. Phosphoric acid plants ceased to produce uranium as a by-product in the early 1990s with the fall of uranium prices. In the last decade, this topic has regained attention due to higher uranium prices and expected increase in demand for uranium. Our study revisits the topic and estimates how much uranium might be recoverable from current phosphoric acid production in the United States and whatmore » the associated costs might be considering two different recovery processes: solvent extraction and ion exchange. Based on U.S. phosphoric acid production in 2014, 5.5 million pounds of U 3O 8 could have been recovered, more than domestic U.S. mine production of uranium in the same year. Annualized costs for a hypothetical uranium recovery plant are US$48-66 per pound U 3O 8 for solvent extraction, the process used historically in the United States to recover uranium from phosphoric acid. For ion exchange, not yet proven at a commercial scale for uranium recovery, the estimated costs are US$33-54 per pound U 3O 8. Our results suggest that it is technically possible for the United States to recover significant quantities of uranium from current phosphoric acid production. And for this type of uranium production to be economically attractive on a large scale, either recovery costs must fall or uranium prices rise.« less

Structure and thermodynamic stability of UTa 3O 10, aU(v)-bearing compound

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guo, Xiaofeng; Lipp, Christian; Tiferet, Eitan

Heating a mixture of uranyl (VI) nitrate and tantalum (V) oxide in the molar ratio of 2 : 3 to 1400 °C resulted in the formation of a new compound, UTa 3O 10. The honey colored to yellow brown crystals of UTa 3O 10 crystallize in an orthorhombic structure with the space group Fddd (no. 70), lattice parameters a = 7.3947(1), b = 12.7599(2), c = 15.8156(2) Å, and Z = 8. Vertex sharing [TaO 6] 7– octahedra of two crystallographically distinct Ta cations form a three dimensional tantalate framework. Within this framework, six membered rings of [TaO 6] 7–more » octahedra are formed within the (001) plane. The center of these rings is occupied by the uranyl cations [UO 2]+, with an oxidation state of +5 for uranium. The pentavalence of U and Ta was confirmed by X-ray photoelectron spectroscopy and X-ray adsorption spectroscopy. The enthalpy of formation of UTa 3O 10 from Ta 2O 5, β-U 3O 7, and U3O8 has been determined to be 13.1 ± 18.1 kJ mol–1 using high temperature oxide melt solution calorimetry with sodium molybdate as the solvent at 700 °C. As a result, the close to zero enthalpy of formation of UTa 3O 10 can be explained by closely balanced structural stabilizing and destabilizing factors, which may also apply to other UM 3O 10 compounds.« less

Structure and thermodynamic stability of UTa 3O 10, aU(v)-bearing compound

DOE PAGES

Guo, Xiaofeng; Lipp, Christian; Tiferet, Eitan; ...

2016-09-09

Heating a mixture of uranyl (VI) nitrate and tantalum (V) oxide in the molar ratio of 2 : 3 to 1400 °C resulted in the formation of a new compound, UTa 3O 10. The honey colored to yellow brown crystals of UTa 3O 10 crystallize in an orthorhombic structure with the space group Fddd (no. 70), lattice parameters a = 7.3947(1), b = 12.7599(2), c = 15.8156(2) Å, and Z = 8. Vertex sharing [TaO 6] 7– octahedra of two crystallographically distinct Ta cations form a three dimensional tantalate framework. Within this framework, six membered rings of [TaO 6] 7–more » octahedra are formed within the (001) plane. The center of these rings is occupied by the uranyl cations [UO 2]+, with an oxidation state of +5 for uranium. The pentavalence of U and Ta was confirmed by X-ray photoelectron spectroscopy and X-ray adsorption spectroscopy. The enthalpy of formation of UTa 3O 10 from Ta 2O 5, β-U 3O 7, and U3O8 has been determined to be 13.1 ± 18.1 kJ mol–1 using high temperature oxide melt solution calorimetry with sodium molybdate as the solvent at 700 °C. As a result, the close to zero enthalpy of formation of UTa 3O 10 can be explained by closely balanced structural stabilizing and destabilizing factors, which may also apply to other UM 3O 10 compounds.« less

Measurement of the Auger parameter and Wagner plot for uranium compounds

DOE Office of Scientific and Technical Information (OSTI.GOV)

Holliday, Kiel S.; Siekhaus, Wigbert; Nelson, Art J.

2013-05-15

In this study, the photoemission from the U 4f{sub 7/2} and 4d{sub 5/2} states and the U N{sub 6}O{sub 45}O{sub 45} and N{sub 67}O{sub 45}V x-ray excited Auger transitions were measured for a range of uranium compounds. The data are presented in Wagner plots and the Auger parameter is calculated to determine the utility of this technique in the analysis of uranium materials. It was demonstrated that the equal core-level shift assumption holds for uranium. It was therefore possible to quantify the relative relaxation energies, and uranium was found to have localized core-hole shielding. The position of compounds within themore » Wagner plot made it possible to infer information on bonding character and local electron density. The relative ionicity of the uranium compounds studied follows the trend UF{sub 4} > UO{sub 3} > U{sub 3}O{sub 8} > U{sub 4}O{sub 9}/U{sub 3}O{sub 7} Almost-Equal-To UO{sub 2} > URu{sub 2}Si{sub 2}.« less

Carbothermic reduction of uranium oxides into solvent metallic baths

NASA Astrophysics Data System (ADS)

Guisard Restivo, Thomaz A.; Capocchi, José D. T.

2004-09-01

The carbothermic reduction of UO 2 and U 3O 8 is studied employing tin and silicon solvent metallic baths in thermal analysis equipment, under Ar inert and N 2 reactive atmospheres. The metallic solvents are expected to lower the U activity by several orders of magnitude owing to strong interactions among the metals. The reduction products are composed of the solvent metal matrix and intermetallic U compounds. Silicon is more effective in driving the reduction since there is no residual UO 2 after the reaction. The gaseous product detected by mass spectrometer (MS) during the reduction is CO. A kinetic study for the Si case was accomplished by the stepwise isothermal analysis (SAI) method, leading to the identification of the controlling mechanisms as chemical reaction at the surface and nucleation, for UO 2 and U 3O 8 charges, respectively. One example for another system containing Al 2O 3 is also shown.

Structural and electronic properties of U{sub n}O{sub m} (n=1-3,m=1-3n) clusters: A theoretical study using screened hybrid density functional theory

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, Yu; Liu, Haitao; Zhang, Ping, E-mail: zhang-ping@iapcm.ac.cn

The structural and electronic properties of small uranium oxide clusters U{sub n}O{sub m} (n=1-3, m=1-3n) are systematically studied within the screened hybrid density functional theory. It is found that the formation of U–O–U bondings and isolated U–O bonds are energetically more stable than U–U bondings. As a result, no uranium cores are observed. Through fragmentation studies, we find that the U{sub n}O{sub m} clusters with the m/n ratio between 2 and 2.5 are very stable, hinting that UO{sub 2+x} hyperoxides are energetically stable. Electronically, we find that the O-2p states always distribute in the deep energy range, and the U-5fmore » states always distribute at the two sides of the Fermi level. The U-6d states mainly hybridize with the U-5f states in U-rich clusters, while hybridizing with O-2p states in O-rich clusters. Our work is the first one on the screened hybrid density functional theory level studying the atomic and electronic properties of the actinide oxide clusters.« less

Uranium deposits of Brazil

DOE Office of Scientific and Technical Information (OSTI.GOV)

NONE

Brazil is a country of vast natural resources, including numerous uranium deposits. In support of the country`s nuclear power program, Brazil has developed the most active uranium industry in South America. Brazil has one operating reactor (Angra 1, a 626-MWe PWR), and two under construction. The country`s economic challenges have slowed the progress of its nuclear program. At present, the Pocos de Caldas district is the only active uranium production. In 1990, the Cercado open-pit mine produced approximately 45 metric tons (MT) U{sub 3}O{sub 8} (100 thousand pounds). Brazil`s state-owned uranium production and processing company, Uranio do Brasil, announced itmore » has decided to begin shifting its production from the high-cost and nearly depleted deposits at Pocos de Caldas, to lower-cost reserves at Lagoa Real. Production at Lagoa Real is schedules to begin by 1993. In addition to these two districts, Brazil has many other known uranium deposits, and as a whole, it is estimated that Brazil has over 275,000 MT U{sub 3}O{sub 8} (600 million pounds U{sub 3}O{sub 8}) in reserves.« less

Selection of Nuclear Fuel for TREAT: UO 2 vs U 3O 8

DOE Office of Scientific and Technical Information (OSTI.GOV)

Glazoff, Michael Vasily; Van Rooyen, Isabella Johanna; Coryell, Benjamin David

The Transient Reactor Test (TREAT) that resides at the Materials and Fuels Complex (MFC) at Idaho National Laboratory (INL), first achieved criticality in 1959, and successfully performed many transient tests on nuclear fuel until 1994 when its operations were suspended. Resumption of operations at TREAT was approved in February 2014 to meet the U.S. Department of Energy (DOE) Office of Nuclear Energy’s objectives in transient testing of nuclear fuels. The National Nuclear Security Administration’s is converting TREAT from its existing highly enriched uranium (HEU) core to a new core containing low enriched uranium (LEU) (i.e., U-235< 20% by weight). Themore » TREAT Conversion project is currently progressing with conceptual design phase activities. Dimensional stability of the fuel element assemblies, predictable fuel can oxidation and sufficient heat conductivity by the fuel blocks are some of the critical performance requirements of the new LEU fuel. Furthermore, to enable the design team to design fuel block and can specifications, it is amongst the objectives to evaluate TREAT LEU fuel and cladding material’s chemical interaction. This information is important to understand the viability of Zr-based alloys and fuel characteristics for the fabrication of the TREAT LEU fuel and cladding. Also, it is very important to make the right decision on what type of nuclear fuel will be used at TREAT. In particular, one has to consider different oxides of uranium, and most importantly, UO 2 vs U 3O 8. In this report, the results are documented pertaining to the choice mentioned above (UO 2 vs U 3O 8). The conclusion in favor of using UO 2 was made based on the analysis of historical data, up-to-date literature, and self-consistent calculations of phase equilibria and thermodynamic properties in the U-O and U-O-C systems. The report is organized as follows. First, the criteria that were used to make the choice are analyzed. Secondly, existing historical data and current literature were reviewed. This analysis was supplemented by the construction and examination of the U-O and U-O-C phase diagrams at pressure close to negligent, thereby mimicking the conditions in which nuclear fuel is supposed to function inside the zirconium-based cladding in the reactor. Finally, our conclusion in favor of the UO 2 down selection was summarized and explained in the last Section of this document.« less

Analysis of oxygen potential of (U 0.7Pu 0.3)O 2±x and (U 0.8Pu 0.2)O 2±x based on point defect chemistry

NASA Astrophysics Data System (ADS)

Kato, Masato; Konashi, Kenji; Nakae, Nobuo

2009-06-01

Stoichiometries in (U 0.7Pu 0.3)O 2±x and (U 0.8Pu 0.2)O 2±x were analyzed with the experimental data of oxygen potential based on point defect chemistry. The relationship between the deviation x of stoichiometric composition and the oxygen partial pressure P was evaluated using a Kröger-Vink diagram. The concentrations of the point defects in uranium and plutonium mixed oxide (MOX) were estimated from the measurement data of oxygen potentials as functions of temperature and P. The analysis results showed that x was proportional to PO2±1/2 near the stoichiometric region of both (U 0.7Pu 0.3)O 2±x and (U 0.8Pu 0.2)O 2±x, which suggested that intrinsic ionization was the dominant defect. A model to calculate oxygen potential was derived and it represented the experimental data accurately. Further, the model estimated the thermodynamic data, ΔH and ΔS, of stoichiometric (U 0.7Pu 0.3)O 2.00 and (U 0.8Pu 0.2)O 2.00 as -552.5 kJ·mol -1 and -149.7 J·mol -1, and -674.0 kJ · mol -1 and -219.4 J · mol -1, respectively.

Thiocyanate complexes of uranium in multiple oxidation states: a combined structural, magnetic, spectroscopic, spectroelectrochemical, and theoretical study.

PubMed

Hashem, Emtithal; Platts, James A; Hartl, František; Lorusso, Giulia; Evangelisti, Marco; Schulzke, Carola; Baker, Robert J

2014-08-18

A comprehensive study of the complexes A4[U(NCS)8] (A = Cs, Et4N, (n)Bu4N) and A3[UO2(NCS)5] (A = Cs, Et4N) is described, with the crystal structures of [(n)Bu4N]4[U(NCS)8]·2MeCN and Cs3[UO2(NCS)5]·O0.5 reported. The magnetic properties of square antiprismatic Cs4[U(NCS)8] and cubic [Et4N]4[U(NCS)8] have been probed by SQUID magnetometry. The geometry has an important impact on the low-temperature magnetic moments: at 2 K, μeff = 1.21 μB and 0.53 μB, respectively. Electronic absorption and photoluminescence spectra of the uranium(IV) compounds have been measured. The redox chemistry of [Et4N]4[U(NCS)8] has been explored using IR and UV-vis spectroelectrochemical methods. Reversible 1-electron oxidation of one of the coordinated thiocyanate ligands occurs at +0.22 V vs Fc/Fc(+), followed by an irreversible oxidation to form dithiocyanogen (NCS)2 which upon back reduction regenerates thiocyanate anions coordinating to UO2(2+). NBO calculations agree with the experimental spectra, suggesting that the initial electron loss of [U(NCS)8](4-) is delocalized over all NCS(-) ligands. Reduction of the uranyl(VI) complex [Et4N]3[UO2(NCS)5] to uranyl(V) is accompanied by immediate disproportionation and has only been studied by DFT methods. The bonding in [An(NCS)8](4-) (An = Th, U) and [UO2(NCS)5](3-) has been explored by a combination of DFT and QTAIM analysis, and the U-N bonds are predominantly ionic, with the uranyl(V) species more ionic that the uranyl(VI) ion. Additionally, the U(IV)-NCS ion is more ionic than what was found for U(IV)-Cl complexes.

Evaluation of phases in Pu-C-O and (U, Pu)-C-O systems by X-ray diffractometry and chemical analysis

NASA Astrophysics Data System (ADS)

Jain, G. C.; Ganguly, C.

1993-12-01

Preparation and characterisation of the carbides of uranium, plutonium and mixed uranium and plutonium form a part of advanced fuel development programs for fast breeder reactors. In the present study, the compositions of the phases of Pu-C-O and (U.Pu)-C-O systems have been determined by chemical analysis and lattice parameter measurement. The carbide samples have been prepared by vacuum carbothermic synthesis of tabletted oxide-graphite powder mixture. Dependence of stoichiometry of Pu 2C 3 phase on the oxygen content of Pu(C,O) phase in Pu(C,O) + Pu 2C 3 phase mixture has been evaluated. Stoichiometry and oxygen solubility of (U 0.3Pu 0.7)(C,O) phase in multiple phase mixture have been determined. Segregation of plutonium in (U,Pu) 2C 3 phase of (U,Pu)(C,O) + (U,Pu) 2C 3 phase mixture and its dependence on the oxygen content of (U,Pu)(C,O) phase have also been determined from the measurement of the lattice parameter of (U,Pu) 2C 3 phase.

The role of lead and excess oxygen in uranite

USGS Publications Warehouse

Berman, Robert Morris

1957-01-01

Analysed samples of uraninite were x-rayed, annealed by heating to 550° and 900° for various times in a nitrogen atmosphere, and x-rayed again. A decrease in unit cell size was generally observed. Calculations on the basis of Vegard's Law showed that the ordering of the interstitial oxygen ions could account for the decrease in cell size on annealing. The interstitial oxygens are not necessarily completely disordered before annealing. The degree of original disorder is dependent on the Rare Earth/ThO2 ratio; for high ThO2 and low rare earths, the interstitial oxygens are completely random. The degree of disorder apparently depends solely on the composition, and not on the past history of the sample; this implies that the oxygens are being continuously disordered, perhaps by alpha particles, to the equilibrium point determined by the R.E./ThO2 ratio. The degree of ordering of the interstitial oxygens also accounts for the difference in cell size between vein pitchblendes and those from the sediments of the Colorado Plateau. A study was also made of the degree of oxidation of uraninites. Although the uranium in many pegmatitic uraninites is more oxidized than can be obtained with the cubic UO2 phase in the laboratory, if the atoms proxying for uranium are calculated into the structural formula, and the lead is assumed to be radiogenic and calculated as original uranium, almost all pegmatitic uraninites fall into the range of interstitial oxygen content obtainable in the laboratory. This fact supports the auto-oxidation hypothesis. Many of the vein and sedimentary pitchblendes have compositions close to U3O8, although they are cubic. They may gave crystallized as U3O8, the decomposed to the cubic phase and a amorphous phase. This suggests that the stability range of U3O8 includes only very exceptional natural conditions. Vegard's Law calculations, studies of zoning in crystals, differential leaching, polished section textures, and other lines of evidence indicate that lead, including radiogenic lead, is exsolved from uraninite. A study of x-ray line intensities indicates that it exsolves as oriented monomolecular layers of orthohombic PbO (massicot) along cube planes in the uraninite, separating the uraninite crystallites so that the x-ray reflections interfere destructively to different degrees for different reflections.

URANIUM OXIDE-CONTAINING FUEL ELEMENT COMPOSITION AND METHOD OF MAKING SAME

DOEpatents

Handwerk, J.H.; Noland, R.A.; Walker, D.E.

1957-09-10

In the past, bodies formed of a mixture of uranium dioxide and aluminum powder have been used in fuel elements; however, these mixtures were found not to be suitable when exposed to temperatures of about 600 deg C, because at such high temperatures the fuel elements were distorted. If uranosic oxide, U/sub 3/O/sub 8/, is substituted for UO/sub 2/, the mechanical properties are not impaired when these materials are used at about 600 deg C and no distortion takes place. The uranosic oxide and aluminum, both in powder form, are first mixed, and after a homogeneous mixture has been obtained, are shaped into fuel elements by extrusion at elevated temperature. Magnesium powder may be used in place of the aluminum.

Actinide Oxidation State and O/M Ratio in Hypostoichiometric Uranium-Plutonium-Americium U0.750Pu0.246Am0.004O2-x Mixed Oxides.

PubMed

Vauchy, Romain; Belin, Renaud C; Robisson, Anne-Charlotte; Lebreton, Florent; Aufore, Laurence; Scheinost, Andreas C; Martin, Philippe M

2016-03-07

Innovative americium-bearing uranium-plutonium mixed oxides U1-yPuyO2-x are envisioned as nuclear fuel for sodium-cooled fast neutron reactors (SFRs). The oxygen-to-metal (O/M) ratio, directly related to the oxidation state of cations, affects many of the fuel properties. Thus, a thorough knowledge of its variation with the sintering conditions is essential. The aim of this work is to follow the oxidation state of uranium, plutonium, and americium, and so the O/M ratio, in U0.750Pu0.246Am0.004O2-x samples sintered for 4 h at 2023 K in various Ar + 5% H2 + z vpm H2O (z = ∼ 15, ∼ 90, and ∼ 200) gas mixtures. The O/M ratios were determined by gravimetry, XAS, and XRD and evidenced a partial oxidation of the samples at room temperature. Finally, by comparing XANES and EXAFS results to that of a previous study, we demonstrate that the presence of uranium does not influence the interactions between americium and plutonium and that the differences in the O/M ratio between the investigated conditions is controlled by the reduction of plutonium. We also discuss the role of the homogeneity of cation distribution, as determined by EPMA, on the mechanisms involved in the reduction process.

Reoxidation of uranium metal immersed in a Li2O-LiCl molten salt after electrolytic reduction of uranium oxide

NASA Astrophysics Data System (ADS)

Choi, Eun-Young; Jeon, Min Ku; Lee, Jeong; Kim, Sung-Wook; Lee, Sang Kwon; Lee, Sung-Jai; Heo, Dong Hyun; Kang, Hyun Woo; Jeon, Sang-Chae; Hur, Jin-Mok

2017-03-01

We present our findings that uranium (U) metal prepared by using the electrolytic reduction process for U oxide (UO2) in a Li2O-LiCl salt can be reoxidized into UO2 through the reaction between the U metal and Li2O in LiCl. Two salt types were used for immersion of the U metal: one was the salt used for electrolytic reduction, and the other was applied to the unused LiCl salts with various concentrations of Li2O and Li metal. Our results revealed that the degree of reoxidation increases with the increasing Li2O concentration in LiCl and that the presence of the Li metal in LiCl suppresses the reoxidation of the U metal.

Preparation of porous magnesium oxide foam and study on its enrichment of uranium

NASA Astrophysics Data System (ADS)

Wang, Yunsheng; Chen, Yuantao; Liu, Chen; Yu, Fang

2018-06-01

Herein, we prepared porous magnesium oxide (MP-MgO) by in situ carbonization and using Mg(NO3)2 as precursor along with P123 as soft template. The BET surface area, and total pore volume of MP-MgO were found to be 14.76 m2 g, 0.15 cm3 g-1, respectively. The adsorption behavior of U (Ⅵ) by the porous MgO was studied by static adsorption experiments, and also the effects of adsorption time, pH of wastewater and U (Ⅵ) concentration were discussed. The results indicated that the optimum pH for MP-MgO was 3.0-4.5, the removal of uranium in this case was mainly due to surface complexation. Through the study, we found that the adsorption capacity of MP-MgO for uranium was more than 2500 mg g-1, the adsorption equilibrium time was about 150 min. Moreover, the kinetic study showed that the process followed the pseudo-first-order model, and the adsorption process was spontaneous and endothermic.

A review of the high temperature oxidation of uranium oxides in molten salts and in the solid state to form alkali metal uranates, and their composition and properties

NASA Astrophysics Data System (ADS)

Griffiths, Trevor R.; Volkovich, Vladimir A.

An extensive review of the literature on the high temperature reactions (both in melts and in the solid state) of uranium oxides (UO 2, U 3O 8 and UO 3) resulting in the formation of insoluble alkali metal (Li to Cs) uranates is presented. Their uranate(VI) and uranate(V) compounds are examined, together with mixed and oxygen-deficient uranates. The reactions of uranium oxides with carbonates, oxides, per- and superoxides, chlorides, sulfates, nitrates and nitrites under both oxidising and non-oxidising conditions are critically examined and systematised, and the established compositions of a range of uranate(VI) and (V) compounds formed are discussed. Alkali metal uranates(VI) are examined in detail and their structural, physical, thermodynamic and spectroscopic properties considered. Chemical properties of alkali metal uranates(VI), including various methods for their reduction, are also reported. Errors in the current theoretical treatment of uranate(VI) spectra are identified and the need to develop routes for the preparation of single crystals is stressed.

Structure and Reactivity of X-ray Amorphous Uranyl Peroxide, U 2O 7

DOE PAGES

Odoh, Samuel O.; Shamblin, Jacob; Colla, Christopher A.; ...

2016-03-14

Recent accidents resulting in worker injury and radioactive contamination occurred due to pressurization of uranium yellowcake drums produced in the western USA. The drums contained an unexpected X-ray amorphous reactive form of uranium oxide, U 2O7. Heating hydrated uranyl peroxides produced during in situ mining unintentionally produced U 2O 7. It is a hygroscopic anhydrous uranyl peroxide that reacts rapidly with water to release O 2 gas and form metaschoepite, a uranyl-oxide hydrate. Quantum chemical calculations indicate that the most stable U 2O 7 conformer consists of two bent (UO 2) 2+ uranyl ions bridged by a peroxide group bidentatemore » and parallel to each uranyl ion, and a μ2-O atom, resulting in charge neutrality. A pair distribution function from neutron total scattering supports this structural model. The reactivity of U 2O 7 in water and with water in air is much higher than other uranium oxides, and this can be both hazardous and potentially advantageous in the nuclear fuel cycle.« less

Quantifying Morphological Features of α-U3O8 with Image Analysis for Nuclear Forensics.

PubMed

Olsen, Adam M; Richards, Bryony; Schwerdt, Ian; Heffernan, Sean; Lusk, Robert; Smith, Braxton; Jurrus, Elizabeth; Ruggiero, Christy; McDonald, Luther W

2017-03-07

Morphological changes in U 3 O 8 based on calcination temperature have been quantified enabling a morphological feature to serve as a signature of processing history in nuclear forensics. Five separate calcination temperatures were used to synthesize α-U 3 O 8 , and each sample was characterized using powder X-ray diffraction (p-XRD) and scanning electron microscopy (SEM). The p-XRD spectra were used to evaluate the purity of the synthesized U-oxide; the morphological analysis for materials (MAMA) software was utilized to quantitatively characterize the particle shape and size as indicated by the SEM images. Analysis comparing the particle attributes, such as particle area at each of the temperatures, was completed using the Kolmogorov-Smirnov two sample test (K-S test). These results illustrate a distinct statistical difference between each calcination temperature. To provide a framework for forensic analysis of an unknown sample, the sample distributions at each temperature were compared to randomly selected distributions (100, 250, 500, and 750 particles) from each synthesized temperature to determine if they were statistically different. It was found that 750 particles were required to differentiate between all of the synthesized temperatures with a confidence interval of 99.0%. Results from this study provide the first quantitative morphological study of U-oxides, and reveals the potential strength of morphological particle analysis in nuclear forensics by providing a framework for a more rapid characterization of interdicted uranium oxide samples.

RECOVERY OF URANIUM VALUES FROM URANIUM BEARING RAW MATERIALS

DOEpatents

Michal, E.J.; Porter, R.R.

1959-06-16

Uranium leaching from ground uranium-bearing raw materials using MnO/sub 2/ in H/sub 2/SO/sub 4/ is described. The MnO/sub 2/ oxidizes U to the leachable hexavalent state. The MnO/sub 2/ does not replace Fe normally added, because the Fe complexes P and catalyzes the MnO/sub 2/ reaction. Three examples of continuous processes are given, but batch operation is also possible. The use of MnO/sub 2/ makes possible recovery of very low U values. (T.R.H.)

Radiolytic Effects on Fluoride Impurities in a U{sub 3}O{sub 8} Matrix

DOE Office of Scientific and Technical Information (OSTI.GOV)

Icenhour, A.S.

2000-05-01

The safe handling and storage of radioactive materials require an understanding of the effects of radiolysis on those materials. Radiolysis may result in the production of gases (e.g., corrosives) or pressures that are deleterious to storage containers. A study has been performed to address these concerns as they relate to the radiolysis of residual fluoride compounds in uranium oxides.

Analysis of a Uranium Oxide Sample Interdicted in Slovakia (FSC 12-3-1)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Borg, Lars E.; Dai, Zurong; Eppich, Gary R.

2014-01-17

We provide a concise summary of analyses of a natural uranium sample seized in Slovakia in November 2007. Results are presented for compound identification, water content, U assay, trace element abundances, trace organic compounds, isotope compositions for U, Pb, Sr and O, and age determination using the 234U – 230Th and 235U – 231Pa chronometers. The sample is a mixture of two common uranium compounds - schoepite and uraninite. The uranium isotope composition is indistinguishable from natural; 236U was not detected. The O, Sr and Pb isotope compositions and trace element abundances are unremarkable. The 234U – 230Th chronometer givesmore » an age of 15.5 years relative to the date of analysis, indicating the sample was produced in January 1997. A comparison of the data for this sample with data in the Uranium Sourcing database failed to find a match, indicating the sample was not produced at a facility represented in the database.« less

RECOVERY OF URANIUM FROM LOW GRADE URANIUM BEARING ORES

DOEpatents

Rhodes, H.B.; Pesold, W.F.; Hirshon, J.M.

1959-06-01

Recovery of U, Fe, and Al from Chattanooga shale is described. Ground shale (-4 to +325 mesh) is roasted to remove organic and volatile matter. The heated shale is then reacted with a chlorinating agent (CCl/sub 4/, COCl/sub 2/, Cl, and SCl) at 600 to 1000 C. The metal chloride vapor is separated from entrained solids and then contacted with a liquid alkali metal chloride which removes U. The U is reeovered by cooling and dissolving the bath followed by acidification and solvent extraction. A condensed phase of Al, Fe, and K chlorides is treated to separate Al as alumina by passing through a Fe/sub 2/O/ sub 3/ bed. The remaining FeCl/sub 3/ is oxidized by O/sub 2/ at 1000 C to form Fe/sub 2/O/sub 3/ and Cl/sub 2/. Alternatively, vapor from the U separation step may be passed to a liquid KCl bath at 500 to 650 C. The resulting mixture is oxidized to form Cl/sub 2/ and Fe/sub 2/O/sub 3/ + Al/sub 2/O/sub 3/. The Al and Fe are separated by reaction with NaOH at high temperatures and pressures. (T.R.H.)

PROCESS FOR PRODUCING URANIUM HEXAFLUORIDE

DOEpatents

Fowler, R.D.

1957-10-22

A process for the production of uranium hexafluoride from the oxides of uranium is reported. In accordance with the method the higher oxides of uranium may be reduced to uranium dioxide (UO/sub 2/), the latter converted into uranium tetrafluoride by reaction with hydrogen fluoride, and the UF/sub 4/ convented to UF/sub 6/ by reaction with a fluorinating agent. The UO/sub 3/ or U/sub 3/O/sub 8/ is placed in a reaction chamber in a copper boat or tray enclosed in a copper oven, and heated to 500 to 650 deg C while hydrogen gas is passed through the oven. The oven is then swept clean of hydrogen and the water vapor formed by means of nitrogen and then while continuing to maintain the temperature between 400 and 600 deg C, anhydrous hydrogen fluoride is passed through. After completion of the conversion to uranium tetrafluoride, the temperature of the reaction chamber is lowered to ahout 400 deg C, and elemental fluorine is used as the fluorinating agent for the conversion of UF/sub 4/ into UF/sub 6/. The fluorine gas is passed into the chamber, and the UF/sub 6/ formed passes out and is delivered to a condenser.

Selective recovery of uranium from Ca-Mg uranates by chlorination

NASA Astrophysics Data System (ADS)

Pomiro, Federico J.; Gaviría, Juan P.; Quinteros, Raúl D.; Bohé, Ana E.

2017-07-01

A chlorination process is proposed for the uranium extraction and separation using Calciumsbnd Magnesium uranates such as starting reactants which were obtained by precipitation from uranyl nitrate solutions with calcium hydroxide. The study is based on thermodynamic and reaction analysis using chlorine gas as chlorination agent. The results showed that the chlorination reaction of Ca uranate is more feasible to occur than the Mg uranate. The products obtained after chlorination reactions were washed with deionized water to remove the chlorides produced and analyzed. The XRD patterns of the washed products indicated that the chlorination between 400 and 500 °C result in a single phase of calcium uranate (CaUO4) as reaction product. The formation of U3O8 and MgU3O10 was observed at temperatures between 600 °C and 700 °C for 8 hs. The optimal conditions to recover uranium were 3 l h-1 of chlorine and 10 hs of reaction at 700 °C being U3O8 the single uranium product obtained.

Competing retention pathways of uranium upon reaction with Fe(II)

NASA Astrophysics Data System (ADS)

Massey, Michael S.; Lezama-Pacheco, Juan S.; Jones, Morris E.; Ilton, Eugene S.; Cerrato, José M.; Bargar, John R.; Fendorf, Scott

2014-10-01

Biogeochemical retention processes, including adsorption, reductive precipitation, and incorporation into host minerals, are important in contaminant transport, remediation, and geologic deposition of uranium. Recent work has shown that U can become incorporated into iron (hydr)oxide minerals, with a key pathway arising from Fe(II)-induced transformation of ferrihydrite, (Fe(OH)3·nH2O) to goethite (α-FeO(OH)); this is a possible U retention mechanism in soils and sediments. Several key questions, however, remain unanswered regarding U incorporation into iron (hydr)oxides and this pathway's contribution to U retention, including: (i) the competitiveness of U incorporation versus reduction to U(IV) and subsequent precipitation of UO2; (ii) the oxidation state of incorporated U; (iii) the effects of uranyl aqueous speciation on U incorporation; and, (iv) the mechanism of U incorporation. Here we use a series of batch reactions conducted at pH ∼7, [U(VI)] from 1 to 170 μM, [Fe(II)] from 0 to 3 mM, and [Ca] at 0 or 4 mM coupled with spectroscopic examination of reaction products of Fe(II)-induced ferrihydrite transformation to address these outstanding questions. Uranium retention pathways were identified and quantified using extended X-ray absorption fine structure (EXAFS) spectroscopy, X-ray powder diffraction, X-ray photoelectron spectroscopy, and transmission electron microscopy. Analysis of EXAFS spectra showed that 14-89% of total U was incorporated into goethite, upon reaction with Fe(II) and ferrihydrite. Uranium incorporation was a particularly dominant retention pathway at U concentrations ⩽50 μM when either uranyl-carbonato or calcium-uranyl-carbonato complexes were dominant, accounting for 64-89% of total U. With increasing U(VI) and Fe(II) concentrations, U(VI) reduction to U(IV) became more prevalent, but U incorporation remained a functioning retention pathway. These findings highlight the potential importance of U(V) incorporation within iron oxides as a retention process of U across a wide range of biogeochemical environments and the sensitivity of uranium retention processes to operative (bio)geochemical conditions.

Competing retention pathways of uranium upon reaction with Fe(II)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Massey, Michael S.; Lezama Pacheco, Juan S.; Jones, Morris

Biogeochemical retention processes, including adsorption, reductive precipitation, and incorporation into host minerals, are important in contaminant transport, remediation, and geologic deposition of uranium. Recent work has shown that U can become incorporated into iron (hydr)oxide minerals, with a key pathway arising from Fe(II)-induced transformation of ferrihydrite, (Fe(OH)3•nH2O) to goethite (α-FeO(OH)); this is a possible U retention mechanism in soils and sediments. Several key questions, however, remain unanswered regarding U incorporation into iron (hydr)oxides and this pathway’s contribution to U retention, including: (i) the competitiveness of U incorporation versus reduction to U(IV) and subsequent precipitation of UO2; (ii) the oxidation statemore » of incorporated U; (iii) the effects of uranyl aqueous speciation on U incorporation; and, (iv) the mechanism of U incorporation. Here we use a series of batch reactions conducted at pH ~7, [U(VI)] from 1 to 170 μM, [Fe(II)] from 0 to 3 mM, and [Ca] at 0 or 4 mM) coupled with spectroscopic examination of reaction products of Fe(II)-induced ferrihydrite transformation to address these outstanding questions. Uranium retention pathways were identified and quantified using extended x-ray absorption fine structure (EXAFS) spectroscopy, x-ray powder diffraction, x-ray photoelectron spectroscopy, and transmission electron microscopy. Analysis of EXAFS spectra showed that 14 to 89% of total U was incorporated into goethite, upon reaction with Fe(II) and ferrihydrite. Uranium incorporation was a particularly dominant retention pathway at U concentrations ≤ 50 μM when either uranyl-carbonato or calcium-uranyl-carbonato complexes were dominant, accounting for 64 to 89% of total U. With increasing U(VI) and Fe(II) concentrations, U(VI) reduction to U(IV) became more prevalent, but U incorporation remained a functioning retention pathway. These findings highlight the potential importance of U(V) incorporation within iron oxides as a retention process of U across a wide range of biogeochemical environments and the sensitivity of uranium retention processes to operative (bio)geochemical conditions.« less

Uranium (III)-Plutonium (III) co-precipitation in molten chloride

NASA Astrophysics Data System (ADS)

Vigier, Jean-François; Laplace, Annabelle; Renard, Catherine; Miguirditchian, Manuel; Abraham, Francis

2018-02-01

Co-management of the actinides in an integrated closed fuel cycle by a pyrochemical process is studied at the laboratory scale in France in the CEA-ATALANTE facility. In this context the co-precipitation of U(III) and Pu(III) by wet argon sparging in LiCl-CaCl2 (30-70 mol%) molten salt at 705 °C is studied. Pu(III) is prepared in situ in the molten salt by carbochlorination of PuO2 and U(III) is then introduced as UCl3 after chlorine purge by argon to avoid any oxidation of uranium up to U(VI) by Cl2. The oxide conversion yield through wet argon sparging is quantitative. However, the preferential oxidation of U(III) in comparison to Pu(III) is responsible for a successive conversion of the two actinides, giving a mixture of UO2 and PuO2 oxides. Surprisingly, the conversion of sole Pu(III) in the same conditions leads to a mixture of PuO2 and PuOCl, characteristic of a partial oxidation of Pu(III) to Pu(IV). This is in contrast with coconversion of U(III)-Pu(III) mixtures but in agreement with the conversion of Ce(III).

Syntheses and structures of [UO2( L)5](ClO4)2 and [U( L')4(H2O)4](ClO4)4 ( L is dimethylformamide, L' is N,N-dimethylcarbamide)

NASA Astrophysics Data System (ADS)

Serezhkin, V. N.; Vologzhanina, A. V.; Pushkin, D. V.; Astashkina, D. A.; Savchenkov, A. V.; Serezhkina, L. B.

2017-09-01

The reaction of aqueous solutions of uranyl perchlorate with selected organic amides was studied in the dark and under the sunlight. The complexes [UVIO2(C3H7NO)5](ClO4)2 ( I) and [UIV(C3H8N2O)4(H2O)4](ClO4)4 ( II), where C3H7NO is N,N-dimethylformamide ( Dmfa) and C3H8N2O is N,N-dimethylcarbamide ( a-Dmur), were studied by X-ray diffraction. Complex II and the complex UIV( s-Dmur)4(H2O)4(ClO4)4 ( III), where s-Dmur is N,N'-dimethylcarbamide, were studied by IR spectroscopy. Crystals I and II are composed of mononuclear [UO2( Dmfa)5]2+ and [U( Dmur)4(H2O)4]4+ groups as uranium-containing structural units belonging to the crystal-chemical groups AM 7 1 ( A = UVI, M 1 = O2- and Dmfa) and AM 8 1 ( A = UIV, M 1 = Dmur and H2O) of uranium complexes, respectively. The mononuclear uranium- containing complexes in the crystals of U(IV) and U(VI) perchlorates were found to obey the 14 neighbors rule.

Separation of uranium from (Th,U)O.sub.2 solid solutions

DOEpatents

Chiotti, Premo; Jha, Mahesh Chandra

1976-09-28

Uranium is separated from mixed oxides of thorium and uranium by a pyrometallurgical process in which the oxides are mixed with a molten chloride salt containing thorium tetrachloride and thorium metal which reduces the uranium oxide to uranium metal which can then be recovered from the molten salt. The process is particularly useful for the recovery of uranium from generally insoluble high-density sol-gel thoria-urania nuclear reactor fuel pellets.

Top Ten Reasons for DEOX as a Front End to Pyroprocessing

DOE Office of Scientific and Technical Information (OSTI.GOV)

B.R. Westphal; K.J. Bateman; S.D. Herrmann

A front end step is being considered to augment chopping during the treatment of spent oxide fuel by pyroprocessing. The front end step, termed DEOX for its emphasis on decladding via oxidation, employs high temperatures to promote the oxidation of UO2 to U3O8 via an oxygen carrier gas. During oxidation, the spent fuel experiences a 30% increase in lattice structure volume resulting in the separation of fuel from cladding with a reduced particle size. A potential added benefit of DEOX is the removal of fission products, either via direct release from the broken fuel structure or via oxidation and volatilizationmore » by the high temperature process. Fuel element chopping is the baseline operation to prepare spent oxide fuel for an electrolytic reduction step. Typical chopping lengths range from 1 to 5 mm for both individual elements and entire assemblies. During electrolytic reduction, uranium oxide is reduced to metallic uranium via a lithium molten salt. An electrorefining step is then performed to separate a majority of the fission products from the recoverable uranium. Although DEOX is based on a low temperature oxidation cycle near 500oC, additional conditions have been tested to distinguish their effects on the process.[1] Both oxygen and air have been utilized during the oxidation portion followed by vacuum conditions to temperatures as high as 1200oC. In addition, the effects of cladding on fission product removal have also been investigated with released fuel to temperatures greater than 500oC.« less

Neutronics Benchmarks for the Utilization of Mixed-Oxide Fuel: Joint U.S./ Russian Progress Report for Fiscal Year 1997, Volume 4, Part 8 - Neutron Poison Plates in Assemblies Containing Homogeneous Mixtures of Polystyrene-Moderated Plutonium and Uranium Oxides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yavuz, M.

1999-05-01

In the 1970s at the Battelle Pacific Northwest Laboratory (PNL), a series of critical experiments using a remotely operated Split-Table Machine was performed with homogeneous mixtures of (Pu-U)O{sub 2}-polystyrene fuels in the form of square compacts having different heights. The experiments determined the critical geometric configurations of MOX fuel assemblies with and without neutron poison plates. With respect to PuO{sub 2} content and moderation [H/(Pu+U)atomic] ratio (MR), two different homogeneous (Pu-U) O{sub 2}-polystyrene mixtures were considered: Mixture (1) 14.62 wt% PuO{sub 2} with 30.6 MR, and Mixture (2) 30.3 wt% PuO{sub 2} with 2.8 MR. In all mixtures, the uraniummore » was depleted to about O.151 wt% U{sup 235}. Assemblies contained copper, copper-cadmium or aluminum neutron poison plates having thicknesses up to {approximately}2.5 cm. This evaluation contains 22 experiments for Mixture 1, and 10 for Mixture 2 compacts. For Mixture 1, there are 10 configurations with copper plates, 6 with aluminum, and 5 with copper-cadmium. One experiment contained no poison plate. For Mixture 2 compacts, there are 3 configurations with copper, 3 with aluminum, and 3 with copper-cadmium poison plates. One experiment contained no poison plate.« less

A preliminary report on the geology of the Dennison-Bunn uranium claim, Sandoval County, New Mexico

USGS Publications Warehouse

Ridgley, Jennie L.

1978-01-01

Uranium at the Dennison-Bunn claim, south of Cuba, N. Mex., along the east margin of the San Juan Basin, occurs in unoxidized gray, fluvial channel sandstone of the Westwater Canyon Member of the Upper Jurassic Morrison Formation. The uranium-bearing sandstone is bounded on the north and south by a variable zone of buff and orange sandstone. Within the mineralized zone, the uranium has been remobilized and reconcentrated along the margins of numerous smaller tongues of oxidized rock in a configuration similar to that found in roll-type uranium deposits. In cross section, these small-scale features are zoned; they have an inner, pale orange, oxidized core, a mineralized redox rim cemented with hematite(?), and an outer-shell of -gray, slightly to moderately mineralized rock. The uranium content in the mineralized rock ranges from 0.001 to 0.07 percent U3O8. The uranium, at this locality, is believed to have originated within the Westwater Canyon Member or to have been derived from the overlying Brushy Basin Member. Based on observed outcrop relations, two hypotheses are proposed for explaining the origin of the occurrence. Briefly these hypotheses are: (1) the mineralized zone represents the remnant of an original roll-type uranium deposit, formed during early Eocene time, which has undergone subsequent oxidation with remobilization and redeposition of uranium around the margins of smaller tongues of oxidized rock; and (2) the mineralized zone represents the remnant of an original tabular deposit which has undergone subsequent oxidation with remobilization and redeposition of uranium around the margins of smaller tongues of oxidized rock.

Predicting equilibrium uranium isotope fractionation in crystals and solution

NASA Astrophysics Data System (ADS)

Schauble, E. A.

2015-12-01

Despite the rapidly growing interest in using 238U/235U measurements as a proxy for changes in oxygen abundance in surface and near-surface environments, the present theoretical understanding of uranium isotope fractionation is limited to a few simple gas-phase molecules and analogues of dissolved species (e.g., 1,2,3). Understanding uranium isotope fractionation behavior in more complicated species, such as crystals and adsorption complexes, will help in the design and interpretation of experiments and field studies, and may suggest other uses for 38U/235U measurements. In this study, a recently developed first-principles method for estimating the nuclear volume component of field shift fractionation in crystals and complex molecular species (4) is combined with mass-dependent fractionation theory to predict equilibrium 38U/235U fractionations in aqueous and crystalline uranium compounds, including uraninite (UO2). The nuclear field shift effect, caused by the interaction of electrons with the finite volume of the positive charge distribution in uranium nuclei, is estimated using Density Functional Theory and the Projector Augmented Wave method (DFT-PAW). Tests against relativistic electronic structure calculations and Mössbauer isomer shift data indicate that the DFT-PAW method is reasonably accurate, while being much better suited to models of complex and crystalline species. Initial results confirm previous predictions that the nuclear volume effect overwhelms mass depdendent fractionation in U(VI)-U(IV) exchange reactions, leading to higher 238U/235U in U(IV) species (i.e., for UO2 xtal vs. UO22+aq, ln αNV ≈ +1.8‰ , ln αMD ≈ -0.8‰, ln αTotal ≈ +1.0‰ at 25ºC). UO2 and U(H2O)94+, are within ~0.4‰ of each other, while U(VI) species appear to be more variable. This suggests that speciation is likely to significantly affect natural uranium isotope fractionations, in addition to oxidation state. Tentatively, it appears that uranyl-type (UO22+-bearing) structures will tend to have higher 238U/235U than uranate-type structures that lack strong U=O bonds. References: 1. Bigeleisen (1996) JACS 118:3676; 2. Schauble (2006) Eos 87:V21B-0570; 3. Abe et al. (2008) J Chem Phys 128:144309, 129:164309, & Abe et al. (2010) J Chem Phys 133:044309; 4. Schauble (2013) PNAS 110:17714.

PRODUCTION OF URANIUM HEXAFLUORIDE

DOEpatents

Fowler, R.D.

1957-08-27

A process for the production of uranium hexafluoride from the oxides of uranium is reported. In accordance with the method, the higher oxides of uranium may be reduced to uranium dioxide (UO/sub 2/), the latter converted into uranium tetrafluoride by reaction with hydrogen fluoride, and the UF/sub 4/ converted to UF/sub 6/ by reaction with a fluorinating agent, such as CoF/sub 3/. The UO/sub 3/ or U/sub 3/O/sub 8/ is placed in a reac tion chamber in a copper boat or tray enclosed in a copper oven, and heated to 500 to 650 deg C while hydrogen gas is passed through the oven. After nitrogen gas is used to sweep out the hydrogen and the water vapor formed, and while continuing to inaintain the temperature between 400 deg C and 600 deg C, anhydrous hydrogen fluoride is passed through. After completion of the conversion of UO/sub 2/ to UF/sub 4/ the temperature of the reaction chamber is lowered to about 400 deg C or less, the UF/sub 4/ is mixed with the requisite quantity of CoF/sub 3/, and after evacuating the chamber, the mixture is heated to 300 to 400 deg C, and the resulting UF/sub 6/ is led off and delivered to a condenser.

Separation of uranium from (U, Th)O 2 and (U, Pu)O 2 by solid state reactions route

NASA Astrophysics Data System (ADS)

Keskar, Meera; Mudher, K. D. Singh; Venugopal, V.

2005-01-01

Solid state reactions of UO 2, ThO 2, PuO 2 and their mixed oxides (U, Th)O 2 and (U, Pu)O 2 were carried out with sodium nitrate upto 900 °C, to study the formation of various phases at different temperatures, which are amenable for easy dissolution and separation of the actinide elements in dilute acid. Products formed by reacting unsintered as well as sintered UO 2 with NaNO 3 above 500 °C were readily soluble in 2 M HNO 3, whereas ThO 2 and PuO 2 did not react with NaNO 3 to form any soluble products. Thus reactions of mixed oxides (U, Th)O 2 and (U, Pu)O 2 with NaNO 3 were carried out to study the quantitative separation of U from (U, Th)O 2 and (U, Pu)O 2. X-ray diffraction, X-ray fluorescence, thermal analysis and chemical analysis techniques were used for the characterization of the products formed during the reactions.

XPS and SIMS study of the surface and interface of aged C + implanted uranium

DOE PAGES

Donald, Scott B.; Siekhaus, Wigbert J.; Nelson, Art J.

2016-09-08

X-ray photoelectron spectroscopy in combination with secondary ion mass spectrometry depth profiling were used to investigate the surface and interfacial chemistry of C + ion implanted polycrystalline uranium subsequently oxidized in air for over 10 years at ambient temperature. The original implantation of 33 keV C + ions into U 238 with a dose of 4.3 × 10 17 cm –3 produced a physically and chemically modified surface layer that was characterized and shown to initially prevent air oxidation and corrosion of the uranium after 1 year in air at ambient temperature. The aging of the surface and interfacial layersmore » were examined by using the chemical shift of the U 4f, C 1s, and O 1s photoelectron lines. In addition, valence band spectra were used to explore the electronic structure of the aged carbide surface and interface layer. Moreover, the time-of-flight secondary ion mass spectrometry depth profiling results for the aged sample confirmed an oxidized uranium carbide layer over the carbide layer/U metal interface.« less

Retention and chemical speciation of uranium in an oxidized wetland sediment from the Savannah River Site.

PubMed

Li, Dien; Seaman, John C; Chang, Hyun-Shik; Jaffe, Peter R; Koster van Groos, Paul; Jiang, De-Tong; Chen, Ning; Lin, Jinru; Arthur, Zachary; Pan, Yuanming; Scheckel, Kirk G; Newville, Matthew; Lanzirotti, Antonio; Kaplan, Daniel I

2014-05-01

Uranium speciation and retention mechanisms onto Savannah River Site (SRS) wetland sediments was studied using batch (ad)sorption experiments, sequential extraction, U L3-edge X-ray absorption near-edge structure (XANES) spectroscopy, fluorescence mapping and μ-XANES. Under oxidized conditions, U was highly retained by the SRS wetland sediments. In contrast to other similar but much lower natural organic matter (NOM) sediments, significant sorption of U onto the SRS sediments was observed at pH < 4 and pH > 8. Sequential extraction indicated that the U species were primarily associated with the acid soluble fraction (weak acetic acid extractable) and organic fraction (Na-pyrophosphate extractable). Uranium L3-edge XANES spectra of the U-bound sediments were nearly identical to that of uranyl acetate. Based on fluorescence mapping, U and Fe distributions in the sediment were poorly correlated, U was distributed throughout the sample and did not appear as isolated U mineral phases. The primary oxidation state of U in these oxidized sediments was U(VI), and there was little evidence that the high sorptive capacity of the sediments could be ascribed to abiotic or biotic reduction to the less soluble U(IV) species or to secondary mineral formation. Collectively, this study suggests that U may be strongly bound to wetland sediments, not only under reducing conditions by reductive precipitation, but also under oxidizing conditions through NOM-uranium bonding. Published by Elsevier Ltd.

Uranium-mediated electrocatalytic dihydrogen production from water.

PubMed

Halter, Dominik P; Heinemann, Frank W; Bachmann, Julien; Meyer, Karsten

2016-02-18

Depleted uranium is a mildly radioactive waste product that is stockpiled worldwide. The chemical reactivity of uranium complexes is well documented, including the stoichiometric activation of small molecules of biological and industrial interest such as H2O, CO2, CO, or N2 (refs 1 - 11), but catalytic transformations with actinides remain underexplored in comparison to transition-metal catalysis. For reduction of water to H2, complexes of low-valent uranium show the highest potential, but are known to react violently and uncontrollably forming stable bridging oxo or uranyl species. As a result, only a few oxidations of uranium with water have been reported so far; all stoichiometric. Catalytic H2 production, however, requires the reductive recovery of the catalyst via a challenging cleavage of the uranium-bound oxygen-containing ligand. Here we report the electrocatalytic water reduction observed with a trisaryloxide U(III) complex [(((Ad,Me)ArO)3mes)U] (refs 18 and 19)--the first homogeneous uranium catalyst for H2 production from H2O. The catalytic cycle involves rare terminal U(IV)-OH and U(V)=O complexes, which have been isolated, characterized, and proven to be integral parts of the catalytic mechanism. The recognition of uranium compounds as potentially useful catalysts suggests new applications for such light actinides. The development of uranium-based catalysts provides new perspectives on nuclear waste management strategies, by suggesting that mildly radioactive depleted uranium--an abundant waste product of the nuclear power industry--could be a valuable resource.

Functionalization of carbon dioxide and carbon disulfide using a stable uranium(III) alkyl complex.

PubMed

Matson, Ellen M; Forrest, William P; Fanwick, Phillip E; Bart, Suzanne C

2011-04-06

A rare uranium(III) alkyl complex, Tp*(2)U(CH(2)Ph) (2) (Tp* = hydrotris(3,5-dimethylpyrazolyl)borate), was synthesized by salt metathesis from Tp*(2)UI (1) and KCH(2)Ph and fully characterized using (1)H NMR, infrared, and electronic absorption spectroscopies as well as X-ray crystallography. This complex has a uranium-carbon distance of 2.57(2) Å, which is comparable to other uranium alkyls reported. Treating this compound with either carbon dioxide or carbon disulfide results in insertion into the uranium-carbon bond to generate Tp*(2)U(κ(2)-O(2)CCH(2)Ph) (3) and Tp*(2)U(SC(S)CH(2)Ph) (4), respectively. These species, characterized spectroscopically and by X-ray crystallography, feature new carboxylate and dithiocarboxylate ligands. Analysis by electronic absorption spectroscopy supports the trivalent oxidation state of the uranium center in both of these derivatives. Addition of trimethylsilylhalides (Me(3)SiX; X = Cl, I) to 3 results in the release of the free silyl ester, Me(3)SiOC(O)CH(2)Ph, forming the initial uranium monohalide species, Tp*(2)UX, which can then be used over multiple cycles for the functionalization of carbon dioxide. © 2011 American Chemical Society

DOE Office of Scientific and Technical Information (OSTI.GOV)

Donald, Scott B.; Siekhaus, Wigbert J.; Nelson, Art J.

X-ray photoelectron spectroscopy in combination with secondary ion mass spectrometry depth profiling were used to investigate the surface and interfacial chemistry of C + ion implanted polycrystalline uranium subsequently oxidized in air for over 10 years at ambient temperature. The original implantation of 33 keV C + ions into U 238 with a dose of 4.3 × 10 17 cm –3 produced a physically and chemically modified surface layer that was characterized and shown to initially prevent air oxidation and corrosion of the uranium after 1 year in air at ambient temperature. The aging of the surface and interfacial layersmore » were examined by using the chemical shift of the U 4f, C 1s, and O 1s photoelectron lines. In addition, valence band spectra were used to explore the electronic structure of the aged carbide surface and interface layer. Moreover, the time-of-flight secondary ion mass spectrometry depth profiling results for the aged sample confirmed an oxidized uranium carbide layer over the carbide layer/U metal interface.« less

Dissolution of Uranium(IV) Oxide in Solutions of Ammonium Carbonate and Hydrogen Peroxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Smith, Steven C.; Peper, Shane M.; Douglas, Matthew

2009-09-12

Understanding the dissolution characteristics of uranium oxides is of fundamental scientific interest. Bench scale experiments were conducted to determine the optimal dissolution parameters of uranium(IV) oxide (UO2) powder in solutions of ammonium carbonate [(NH4)2CO3] and hydrogen peroxide (H2O2). Experimental parameters included variable peroxide and carbonate concentrations, and temperature. Results indicate the dissolution rate of UO2 in 1 M (NH4)2CO3 increases linearly with peroxide concentration ranging from 0.05 – 2 M (1:1 to 40:1 mol ratio H2O2:U), with no apparent maximum rate reached under the limited conditions used in our study. Temperature ranging studies show the dissolution rate of UO2 inmore » 1 M (NH4)2CO3 and 0.1 M H2O2 (2:1 mol ratio H2O2:U) increases linearly from 15 °C to 60 °C, again with no apparent maximum rate reached. Dissolution of UO2 in solutions with constant [H2O2] and [(NH4)2CO3] ranging from 0.5 to 2 M showed no difference in rate; however dissolution was significantly reduced in 0.05 M (NH4)2CO3 solution. The results of this study demonstrate the influence of [H2O2], [(NH4)2CO3], and temperature on the dissolution of UO2 in peroxide-containing (NH4)2CO3 solutions. Future studies are planned to elucidate the solution and solid state complexes in these systems.« less

Exploration for uranium-vanadium deposits by the U.S. Geological Survey in the Club Mesa area, Uravan district, Montrose County, Colorado

USGS Publications Warehouse

Boardman, R.L.; Litsey, L.R.; Bowers, H.E.

1958-01-01

Club Mesa is one of the most productive areas for uranium-vanadium ore in southwestern Colorago. The average grade of this ore has ranged from about 0.25 to 1.50 percent U3O8 and 1.5 to 5.0 percent V2O5.

Americium characterization by X-ray fluorescence and absorption spectroscopy in plutonium uranium mixed oxide

NASA Astrophysics Data System (ADS)

Degueldre, Claude; Cozzo, Cedric; Martin, Matthias; Grolimund, Daniel; Mieszczynski, Cyprian

2013-06-01

Plutonium uranium mixed oxide (MOX) fuels are currently used in nuclear reactors. The actinides in these fuels need to be analyzed after irradiation for assessing their behaviour with regard to their environment and the coolant. In this work the study of the atomic structure and next-neighbour environment of Am in the (Pu,U)O2 lattice in an irradiated (60 MW d kg-1) MOX sample was performed employing micro-X-ray fluorescence (µ-XRF) and micro-X-ray absorption fine structure (µ-XAFS) spectroscopy. The chemical bonds, valences and stoichiometry of Am (˜0.66 wt%) are determined from the experimental data gained for the irradiated fuel material examined in its peripheral zone (rim) of the fuel. In the irradiated sample Am builds up as Am3+ species within an [AmO8]13- coordination environment (e.g. >90%) and no (<10%) Am(IV) or (V) can be detected in the rim zone. The occurrence of americium dioxide is avoided by the redox buffering activity of the uranium dioxide matrix.

Isolation and characterization of a uranium(VI)-nitride triple bond

NASA Astrophysics Data System (ADS)

King, David M.; Tuna, Floriana; McInnes, Eric J. L.; McMaster, Jonathan; Lewis, William; Blake, Alexander J.; Liddle, Stephen T.

2013-06-01

The nature and extent of covalency in uranium bonding is still unclear compared with that of transition metals, and there is great interest in studying uranium-ligand multiple bonds. Although U=O and U=NR double bonds (where R is an alkyl group) are well-known analogues to transition-metal oxo and imido complexes, the uranium(VI)-nitride triple bond has long remained a synthetic target in actinide chemistry. Here, we report the preparation of a uranium(VI)-nitride triple bond. We highlight the importance of (1) ancillary ligand design, (2) employing mild redox reactions instead of harsh photochemical methods that decompose transiently formed uranium(VI) nitrides, (3) an electrostatically stabilizing sodium ion during nitride installation, (4) selecting the right sodium sequestering reagent, (5) inner versus outer sphere oxidation and (6) stability with respect to the uranium oxidation state. Computational analyses suggest covalent contributions to U≡N triple bonds that are surprisingly comparable to those of their group 6 transition-metal nitride counterparts.

Effect of cooling rate on achieving thermodynamic equilibrium in uranium-plutonium mixed oxides

NASA Astrophysics Data System (ADS)

Vauchy, Romain; Belin, Renaud C.; Robisson, Anne-Charlotte; Hodaj, Fiqiri

2016-02-01

In situ X-ray diffraction was used to study the structural changes occurring in uranium-plutonium mixed oxides U1-yPuyO2-x with y = 0.15; 0.28 and 0.45 during cooling from 1773 K to room-temperature under He + 5% H2 atmosphere. We compare the fastest and slowest cooling rates allowed by our apparatus i.e. 2 K s-1 and 0.005 K s-1, respectively. The promptly cooled samples evidenced a phase separation whereas samples cooled slowly did not due to their complete oxidation in contact with the atmosphere during cooling. Besides the composition of the annealing gas mixture, the cooling rate plays a major role on the control of the Oxygen/Metal ratio (O/M) and then on the crystallographic properties of the U1-yPuyO2-x uranium-plutonium mixed oxides.

Pentavalent uranium trans-dihalides and -pseudohalides.

PubMed

Lewis, Andrew J; Nakamaru-Ogiso, Eiko; Kikkawa, James M; Carroll, Patrick J; Schelter, Eric J

2012-05-21

Pentavalent uranium complexes of the formula U(V)X(2)[N(SiMe(3))(2)](3) (X = F(-), Cl(-), Br(-), N(3)(-), NCS(-)) are accessible from the oxidation of U(III)[N(SiMe(3))(2)](3) through two sequential, one-electron oxidation reactions (halides) and substitution through salt metathesis (pseudohalides). Uranium(v) mixed-halides are also synthesized by successive one-electron oxidation reactions.

Adsorption of uranium(VI) to manganese oxides: X-ray absorption spectroscopy and surface complexation modeling.

PubMed

Wang, Zimeng; Lee, Sung-Woo; Catalano, Jeffrey G; Lezama-Pacheco, Juan S; Bargar, John R; Tebo, Bradley M; Giammar, Daniel E

2013-01-15

The mobility of hexavalent uranium in soil and groundwater is strongly governed by adsorption to mineral surfaces. As strong naturally occurring adsorbents, manganese oxides may significantly influence the fate and transport of uranium. Models for U(VI) adsorption over a broad range of chemical conditions can improve predictive capabilities for uranium transport in the subsurface. This study integrated batch experiments of U(VI) adsorption to synthetic and biogenic MnO(2), surface complexation modeling, ζ-potential analysis, and molecular-scale characterization of adsorbed U(VI) with extended X-ray absorption fine structure (EXAFS) spectroscopy. The surface complexation model included inner-sphere monodentate and bidentate surface complexes and a ternary uranyl-carbonato surface complex, which was consistent with the EXAFS analysis. The model could successfully simulate adsorption results over a broad range of pH and dissolved inorganic carbon concentrations. U(VI) adsorption to synthetic δ-MnO(2) appears to be stronger than to biogenic MnO(2), and the differences in adsorption affinity and capacity are not associated with any substantial difference in U(VI) coordination.

High-pressure synthesis and characterization of new actinide borates, AnB4O8 (An=Th, U).

PubMed

Hinteregger, Ernst; Hofer, Thomas S; Heymann, Gunter; Perfler, Lukas; Kraus, Florian; Huppertz, Hubert

2013-11-18

New actinide borates ThB4O8 and UB4O8 were synthesized under high-pressure, high-temperature conditions (5.5 GPa/1100 °C for thorium borate, 10.5 GPa/1100 °C for the isotypic uranium borate) in a Walker-type multianvil apparatus from their corresponding actinide oxide and boron oxide. The crystal structure was determined on basis of single-crystal X-ray diffraction data that were collected at room temperature. Both compounds crystallized in the monoclinic space group C2/c (Z=4). Lattice parameters for ThB4O8: a=1611.3(3), b=419.86(8), c=730.6(2) pm; β=114.70(3)°; V=449.0(2) Å(3); R1=0.0255, wR2=0.0653 (all data). Lattice parameters for UB4O8: a=1589.7(3), b=422.14(8), c=723.4(2) pm; β=114.13(3)°; V=443.1(2) Å(3); R1=0.0227, wR2=0.0372 (all data). The new AnB4O8 (An=Th, U) structure type is constructed from corner-sharing BO4 tetrahedra, which form layers in the bc plane. One of the four independent oxygen atoms is threefold-coordinated. The actinide cations are located between the boron-oxygen layers. In addition to Raman spectroscopic investigations, DFT calculations were performed to support the assignment of the vibrational bands. © 2013 The Authors. Published by Wiley-VCH Verlag GmbH & Co. KGaA. This isan open access article under the terms of the Creative Commons AttributionLicense, which permits use, distribution and reproduction in any medium,provided the original work is properly cited.

Surface characterization of U(AlxSi1-x)3 alloy and its interaction with O2 and H2O, at room temperature

NASA Astrophysics Data System (ADS)

Matmor, M.; Cohen, S.; Rafailov, G.; Vaknin, M.; Shamir, N.; Gouder, T.; Zalkind, S.

2018-02-01

Surface characterization and the interactions of U(AlxSi1-x)3 alloy (x = 0.57) with oxygen and water vapor were studied, utilizing X-Ray Photoelectron Spectroscopy and Direct Recoil Spectrometry, at room temperature. The U 4f spectrum of U(AlxSi1-x)3 alloy exhibits weak correlation satellites, suggesting an itinerant description of the U 5f states for this compound. The Al and Si 2p lines are chemically shifted to lower binding energies. Exposing the alloy to oxygen and water vapor results in oxidation of mainly the uranium and aluminum components, while silicon is only slightly oxidized. Oxygen was found to be a stronger oxidizer than water vapor and the trend is consistent with the more negative enthalpies of formation of metal oxides produced by the O2 reaction, as compared to H2O. During oxygen exposure, fast oxidation occurs by oxide islands nucleation and lateral growth, followed by oxidation of the sub-surface, up to ∼4 nm, at 1000 L exposure. Water initially reacts with the surface by full dissociation and oxide islands formation, which is then covered by hydroxides. Only a minor increase in the oxide thickness of up to ∼2.5 nm, was observed after coalescence.

Effects of calcium and phosphate on uranium(IV) oxidation: Comparison between nanoparticulate uraninite and amorphous U IV–phosphate

DOE PAGES

Latta, Drew E.; Kemner, Kenneth M.; Mishra, Bhoopesh; ...

2015-11-17

The mobility of uranium in subsurface environments depends strongly on its redox state, with U IV phases being significantly less soluble than U VI minerals. This study compares the oxidation kinetics and mechanisms of two potential products of U VI reduction in natural systems, a nanoparticulate UO 2 phase and an amorphous U IV–Ca–PO 4 analog to ningyoite (CaU IV(PO 4) 2·1–2H 2O). The valence of U was tracked by X-ray absorption near-edge spectroscopy (XANES), showing similar oxidation rate constants for U IVO 2 and U IV–phosphate in solutions equilibrated with atmospheric O 2 and CO 2 at pH 7.0more » (k obs,UO2 = 0.17 ± 0.075 h -1 vs. k obs,U IV PO4 = 0.30 ± 0.25 h -1). Addition of up to 400 μM Ca and PO 4 decreased the oxidation rate constant by an order of magnitude for both UO 2 and U IV–phosphate. The intermediates and products of oxidation were tracked by electron microscopy, powder X-ray diffraction (pXRD), and extended X-ray absorption fine-structure spectroscopy (EXAFS). In the absence of Ca or PO 4, the product of UO 2 oxidation is Na–uranyl oxyhydroxide (under environmentally relevant concentrations of sodium, 15 mM NaClO 4 and low carbonate concentration), resulting in low concentrations of dissolved U VI (<2.5 × 10 -7 M). Oxidation of U IV–phosphate produced a Na-autunite phase (Na 2(UO 2)PO 4·xH 2O), resulting in similarly low dissolved U concentrations (<7.3 × 10 -8 M). When Ca and PO 4 are present in the solution, the EXAFS data and the solubility of the UVI phase resulting from oxidation of UO 2 and UIV–phosphate are consistent with the precipitation of Na-autunite. Bicarbonate extractions and Ca K-edge X-ray absorption spectroscopy of oxidized solids indicate the formation of a Ca–UVI–PO 4 layer on the UO 2 surface and suggest a passivation layer mechanism for the decreased rate of UO 2 oxidation in the presence of Ca and PO 4. Interestingly, the extractions were unable to remove all of the oxidized U from partially oxidized UO 2 solids, suggesting that oxidized U is distributed between the interior of the UO 2 nanoparticles and the labile surface layer. Accounting for the entire pool of oxidized U by XANES is the likely reason for the higher UO 2 oxidation rate constants determined here relative to prior studies. In conclusion, our results suggest that the natural presence or addition of Ca and PO 4 in groundwater could slow the rates of U IV oxidation, but that the rates are still fast enough to cause complete oxidation of U IV within days under fully oxygenated conditions.« less

CHEMICAL DIFFERENCES BETWEEN SLUDGE SOLIDS AT THE F AND H AREA TANK FARMS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reboul, S.

2012-08-29

The primary source of waste solids received into the F Area Tank Farm (FTF) was from PUREX processing performed to recover uranium and plutonium from irradiated depleted uranium targets. In contrast, two primary sources of waste solids were received into the H Area Tank Farm (HTF): a) waste from PUREX processing; and b) waste from H-modified (HM) processing performed to recover uranium and neptunium from burned enriched uranium fuel. Due to the differences between the irradiated depleted uranium targets and the burned enriched uranium fuel, the average compositions of the F and H Area wastes are markedly different from onemore » another. Both F and H Area wastes contain significant amounts of iron and aluminum compounds. However, because the iron content of PUREX waste is higher than that of HM waste, and the aluminum content of PUREX waste is lower than that of HM waste, the iron to aluminum ratios of typical FTF waste solids are appreciably higher than those of typical HTF waste solids. Other constituents present at significantly higher concentrations in the typical FTF waste solids include uranium, nickel, ruthenium, zinc, silver, cobalt and copper. In contrast, constituents present at significantly higher concentrations in the typical HTF waste solids include mercury, thorium, oxalate, and radionuclides U-233, U-234, U-235, U-236, Pu-238, Pu-242, Cm-244, and Cm-245. Because of the higher concentrations of Pu-238 in HTF, the long-term concentrations of Th-230 and Ra-226 (from Pu-238 decay) will also be higher in HTF. The uranium and plutonium distributions of the average FTF waste were found to be consistent with depleted uranium and weapons grade plutonium, respectively (U-235 comprised 0.3 wt% of the FTF uranium, and Pu-240 comprised 6 wt% of the FTF plutonium). In contrast, at HTF, U-235 comprised 5 wt% of the uranium, and Pu-240 comprised 17 wt% of the plutonium, consistent with enriched uranium and high burn-up plutonium. X-ray diffraction analyses of various FTF and HTF samples indicated that the primary crystalline compounds of iron in sludge solids are Fe{sub 2}O{sub 3}, Fe{sub 3}O{sub 4}, and FeO(OH), and the primary crystalline compounds of aluminum are Al(OH){sub 3} and AlO(OH). Also identified were carbonate compounds of calcium, magnesium, and sodium; a nitrated sodium aluminosilicate; and various uranium compounds. Consistent with expectations, oxalate compounds were identified in solids associated with oxalic acid cleaning operations. The most likely oxidation states and chemical forms of technetium are assessed in the context of solubility, since technetium-99 is a key risk driver from an environmental fate and transport perspective. The primary oxidation state of technetium in SRS sludge solids is expected to be Tc(IV). In salt waste, the primary oxidation state is expected to be Tc(VII). The primary form of technetium in sludge is expected to be a hydrated technetium dioxide, TcO{sub 2} {center_dot} xH{sub 2}O, which is relatively insoluble and likely co-precipitated with iron. In salt waste solutions, the primary form of technetium is expected to be the very soluble pertechnetate anion, TcO{sub 4}{sup -}. The relative differences between the F and H Tank Farm waste provide a basis for anticipating differences that will occur as constituents of FTF and HTF waste residue enter the environment over the long-term future. If a constituent is significantly more dominant in one of the Tank Farms, its long-term environmental contribution will likely be commensurately higher, assuming the environmental transport conditions of the two Tank Farms share some commonality. It is in this vein that the information cited in this document is provided - for use during the generation, assessment, and validation of Performance Assessment modeling results.« less

Thermal expansion of the nuclear fuel-sodium reaction product Na3(U0.84(2),Na0.16(2))O4 - Structural mechanism and comparison with related sodium-metal ternary oxides

NASA Astrophysics Data System (ADS)

Illy, Marie-Claire; Smith, Anna L.; Wallez, Gilles; Raison, Philippe E.; Caciuffo, Roberto; Konings, Rudy J. M.

2017-07-01

Na3.16(2)UV,VI0.84(2)O4 is obtained from the reaction of sodium with uranium dioxide under oxygen potential conditions typical of a sodium-cooled fast nuclear reactor. In the event of a breach of the steel cladding, it would be the dominant reaction product forming at the rim of the mixed (U,Pu)O2 fuel pellets. High-temperature X-ray diffraction measurements show that a distortion of the uranium environment in Na3.16(2)UV,VI0.84(2)O4 results in a strongly anisotropic thermal expansion. A comparison with several related sodium metallates Nan-2Mn+On-1 - including Na3SbO4 and Na3TaO4, whose crystal structures are reported for the first time - has allowed us to assess the role played in the lattice expansion by the Mn+ cation radius and the Na/M ratio. On this basis, the thermomechanical behavior of the title compound is discussed, along with those of several related double oxides of sodium and actinide elements, surrogate elements, or fission products.

High temperature heat capacity of (U, Am)O2±x

NASA Astrophysics Data System (ADS)

Epifano, E.; Beneš, O.; Vălu, O. S.; Zappey, J.; Lebreton, F.; Martin, P. M.; Guéneau, C.; Konings, R. J. M.

2017-10-01

Mixed uranium and americium dioxides (U, Am)O2±x are candidates as possible transmutation targets for generation IV reactors. In this work, the enthalpy increments of this solid solution were measured in the 470-1750 K temperature range by drop calorimetry for Am/(Am + U) ratios equal to 0.32, 0.39, 0.49, 0.58 and 0.68. Then, the heat capacity functions were obtained by derivation of the enthalpy data. The results of this work were compared to the heat capacity and enthalpy functions reported in the literature for the UO2 [1] and AmO2 [2] binary oxides and for the U0.9Am0.1O2±x, U0.8Am0.2O2±x mixed oxides [3]. From the obtained trend, it was found out that an excess contribution to the enthalpy increment appears for T > 1100 K in the compositions with Am/(Am + U)≥0.4 and a possible explanation attributing this effect to oxygen hypostoichiometry is provided. Finally, to verify the hypothesis, thermodynamic computations based on the CALPHAD method were performed for AmO2-x under air and the results confirmed that the source of the excess contribution is the formation of oxygen vacancies.

Preparation of graphene oxide-manganese dioxide for highly efficient adsorption and separation of Th(IV)/U(VI).

PubMed

Pan, Ning; Li, Long; Ding, Jie; Li, Shengke; Wang, Ruibing; Jin, Yongdong; Wang, Xiangke; Xia, Chuanqin

2016-05-15

Manganese dioxide decorated graphene oxide (GOM) was prepared via fixation of crystallographic MnO2 (α, γ) on the surface of graphene oxide (GO) and was explored as an adsorbent material for simultaneous removal of thorium/uranium ions from aqueous solutions. In single component systems (Th(IV) or U(VI)), the α-GOM2 (the weight ratio of GO/α-MnO2 of 2) exhibited higher maximum adsorption capacities toward both Th(IV) (497.5mg/g) and U(VI) (185.2 mg/g) than those of GO. In the binary component system (Th(IV)/U(VI)), the saturated adsorption capacity of Th(IV) (408.8 mg/g)/U(VI) (66.8 mg/g) on α-GOM2 was also higher than those on GO. Based on the analysis of various data, it was proposed that the adsorption process may involve four types of molecular interactions including coordination, electrostatic interaction, cation-pi interaction, and Lewis acid-base interaction between Th(IV)/U(VI) and α-GOM2. Finally, the Th(IV)/U(VI) ions on α-GOM2 can be separated by a two-stage desorption process with Na2CO3/EDTA. Those results displayed that the α-GOM2 may be utilized as an potential adsorbent for removing and separating Th(IV)/U(VI) ions from aqueous solutions. Copyright © 2016 Elsevier B.V. All rights reserved.

Newly recognized hosts for uranium in the Hanford Site vadose zone

USGS Publications Warehouse

Stubbs, J.E.; Veblen, L.A.; Elbert, D.C.; Zachara, J.M.; Davis, J.A.; Veblen, D.R.

2009-01-01

Uranium contaminated sediments from the U.S. Department of Energy's Hanford Site have been investigated using electron microscopy. Six classes of solid hosts for uranium were identified. Preliminary sediment characterization was carried out using optical petrography, and electron microprobe analysis (EMPA) was used to locate materials that host uranium. All of the hosts are fine-grained and intergrown with other materials at spatial scales smaller than the analytical volume of the electron microprobe. A focused ion beam (FIB) was used to prepare electron-transparent specimens of each host for the transmission electron microscope (TEM). The hosts were identified as: (1) metatorbernite [Cu(UO2)2(PO4)2??8H2O]; (2) coatings on sediment clasts comprised mainly of phyllosilicates; (3) an amorphous zirconium (oxyhydr)oxide found in clast coatings; (4) amorphous and poorly crystalline materials that line voids within basalt lithic fragments; (5) amorphous palagonite surrounding fragments of basaltic glass; and (6) Fe- and Mn-oxides. These findings demonstrate the effectiveness of combining EMPA, FIB, and TEM to identify solid-phase contaminant hosts. Furthermore, they highlight the complexity of U geochemistry in the Hanford vadose zone, and illustrate the importance of microscopic transport in controlling the fate of contaminant metals in the environment. ?? 2008 Elsevier Ltd.

Exploiting the Reactivity of Actinide Fluoride Bonds for the Synthesis of a New Class of Bis(azide) Uranium Complexes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Erickson, Karla A.; Lichtscheidl, Alejandro G.; Monreal, Marisa Jennifer

The terminal actinide fluoride bonds in (C 5Me 5) 2ThF 2(py) (py = pyridine) and (C 5Me 5) 2UF 2(O=PR 3) (R = Me, Ph) react with two equivalents of Me 3SiN 3 in toluene to form the polymeric thorium bis(azide), [(C 5Me 5) 2Th(N 3)2] ∞, and a new class of monometallic uranium bis(azide) complexes, (C 5Me 5) 2U(N 3)2(O=PR 3), respectively. Full characterization of the novel complexes (C 5Me 5) 2ThF 2(py) and (C 5Me 5) 2UF 2(O=PR 3) are reported, including the solid-state structures of (C 5Me 5) 2ThF 2(py) and (C 5Me 5) 2U(N 3) 2(O=PPhmore » 3). Lastly, electronic absorption spectral data are also reported for (C 5Me 5) 2AnF 2(py) (An = Th, U) and (C 5Me 5) 2U(N 3) 2(O=PR 3) to confirm metal oxidation state and enable elucidation of the fluoride and azide ligand bonding in these complexes.« less

Exploiting the Reactivity of Actinide Fluoride Bonds for the Synthesis of a New Class of Bis(azide) Uranium Complexes

DOE PAGES

Erickson, Karla A.; Lichtscheidl, Alejandro G.; Monreal, Marisa Jennifer; ...

2017-11-04

The terminal actinide fluoride bonds in (C 5Me 5) 2ThF 2(py) (py = pyridine) and (C 5Me 5) 2UF 2(O=PR 3) (R = Me, Ph) react with two equivalents of Me 3SiN 3 in toluene to form the polymeric thorium bis(azide), [(C 5Me 5) 2Th(N 3)2] ∞, and a new class of monometallic uranium bis(azide) complexes, (C 5Me 5) 2U(N 3)2(O=PR 3), respectively. Full characterization of the novel complexes (C 5Me 5) 2ThF 2(py) and (C 5Me 5) 2UF 2(O=PR 3) are reported, including the solid-state structures of (C 5Me 5) 2ThF 2(py) and (C 5Me 5) 2U(N 3) 2(O=PPhmore » 3). Lastly, electronic absorption spectral data are also reported for (C 5Me 5) 2AnF 2(py) (An = Th, U) and (C 5Me 5) 2U(N 3) 2(O=PR 3) to confirm metal oxidation state and enable elucidation of the fluoride and azide ligand bonding in these complexes.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kristo, Michael Joseph; Keegan, Elizabeth; Colella, Michael

Nuclear forensic analysis was conducted on two uranium samples confiscated during a police investigation in Victoria, Australia. The first sample, designated NSR-F-270409-1, was a depleted uranium powder of moderate purity (~1000 μg/g total elemental impurities). The chemical form of the uranium was a compound similar to K 2(UO 2) 3O 4·4H 2O. While aliquoting NSR-F-270409-1 for analysis, the body and head of a Tineid moth was discovered in the sample. The second sample, designated NSR-F-270409-2, was also a depleted uranium powder. It was of reasonably high purity (~380 μg/g total elemental impurities). The chemical form of the uranium was primarilymore » UO 3·2H 2O, with minor phases of U 3O 8 and UO 2. While aliquoting NSR-F-270409-2 for analysis, a metal staple of unknown origin was discovered in the sample. The presence of 236U and 232U in both samples indicates that the uranium feed stocks for these samples experienced a neutron flux at some point in their history. The reactor burn-up calculated from the isotopic composition of the uranium is consistent with that of spent fuel from natural uranium (NU) fueled Pu production. These nuclear forensic conclusions allow us to categorically exclude Australia as the origin of the material and greatly reduce the number of candidate sources.« less

Crystal chemistry and thermal behavior of La doped (U, Th)O2

NASA Astrophysics Data System (ADS)

Keskar, Meera; Shelke, Geeta P.; Shafeeq, Muhammed; Krishnan, K.; Sali, S. K.; Kannan, S.

2017-12-01

X-ray diffraction, chemical and thermal studies of [(U0.2Th0.8)1-yLay]O2+x (LUTL) and [(U0.3Th0.7)1-yLay]O2+x (UTL); compounds (where y ≤ 0.4) were carried out. These compounds were synthesized by gel combustion method followed by heating in reduced atmospheres at 1673 K. To co-relate lattice parameters with metal and oxygen concentrations, reduced oxides were heated in Ar, CO2 and air atmospheres. Retention of FCC phase was confirmed in all mixed oxides with y ≤ 0.4. The cubic lattice parameters could be expressed in a linear equation of x and y as: a (Ǻ) = 5.5709 - 0.187 x + 0.032 y; [x < 0 and 0 ≤ y ≤ 0.40] for LUTL and a (Ǻ) = 5.5580 - 0.26 x + 0.015 y; [x < 0 and 0 ≤ y ≤ 0.36] for UTL. Oxidation studies and simple ionic model calculations suggested that uranium is predominantly present as a mixture of +5 and + 6 states when La/U ratio ∼2. Oxidation kinetics of mixed oxides was studied by non-isothermal method using thermogravimetry and was found to be a diffusion controlled reaction. High temperature X-ray diffraction studies of LUTL and UTL mixed oxides showed positive thermal expansion in the temperature range of 298-1273 K and % expansion increases with La concentration.

A XAS study of the local environments of cations in (U, Ce)O 2

NASA Astrophysics Data System (ADS)

Martin, Philippe; Ripert, Michel; Petit, Thierry; Reich, Tobias; Hennig, Christoph; D'Acapito, Francesco; Hazemann, Jean Louis; Proux, Olivier

2003-01-01

Mixed oxide (MOX) fuel is usually considered as a solid solution formed by uranium and plutonium dioxides. Nevertheless, some physico-chemical properties of (U 1- y, Pu y)O 2 samples manufactured under industrial conditions showed anomalies in the domain of plutonium contents ranging between 3 and 15 at.%. Cerium is commonly used as an inactive analogue of plutonium in preliminary studies on MOX fuels. Extended X-ray Absorption Fine Structure (EXAFS) measurements performed at the European Synchrotron Radiation Facility (ESRF) at the cerium and uranium edges on (U 1- y, Ce y)O 2 samples are presented and discussed. They confirmed on an atomic scale the formation of an ideal solid solution for cerium concentrations ranging between 0 and 50 at.%.

Studies on supercritical hydrothermal syntheses of uranium and lanthanide oxide particles and their reaction mechanisms

NASA Astrophysics Data System (ADS)

Hwang, DongKi; Tsukahara, Takehiko; Tanaka, Kosuke; Osaka, Masahiko; Ikeda, Yasuhisa

2015-11-01

In order to develop preparation method of raw metal oxide particles for low decontaminated MOX fuels by supercritical hydrothermal (SH) treatments, we have investigated behavior of aqueous solutions dissolving U(VI), Ln(III) (Ln: lanthanide = Ce, Pr, Nd, Sm, Tb), Cs(I), and Sr(II) nitrate or chloride compounds under SH conditions (temperature = 400-500 °C, pressure = 30-40 MPa). As a result, it was found that Ln(NO3)3 (Ln = Ce, Pr, Tb) compounds produce LnO2, that Ln(NO3)3 (Ln = Nd, Sm) compounds are hardly converted to their oxides, and that LnCl3 (Ln = Ce, Pr, Nd, Sm, Tb), CsNO3, and Sr(NO3)2 do not form their oxide compounds. Furthermore, HNO2 species were detected in the liquid phase obtained after treating HNO3 aqueous solutions containing Ln(NO3)3 (Ln = Ce, Pr, Tb) under SH conditions, and also NO2 and NO compounds were found to be produced by decomposition of HNO3. From these results, it was proposed that the Ln oxide (LnO2) particles are directly formed with oxidation of Ln(III) to Ln(IV) by HNO3 and HNO2 species in the SH systems. Moreover, the uranyl ions were found to form U3O8 and UO3 depending on the concentration of HNO3. From these results, it is expected that the raw metal oxide particles for low decontaminated MOX fuels are efficiently prepared by the SH method.

Geology of the Midnite uranium mine, Stevens County, Washington; a preliminary report

USGS Publications Warehouse

Nash, J. Thomas; Lehrman, Norman J.

1975-01-01

The Midnite mine is one of only two mines in the United States currently producing uranium from discordant deposits in crystalline host rocks. Ore bodies are in metamorphosed steeply dipping Precambrian pelitic and calcareous rocks of a roof pendant adjacent to a Cretaceous(?) porphyritic quartz monzonite pluton. Production during 14 years, of operation has been about 8 million pounds of U3O8 from oxidized and reduced ores averaging 0.23 percent U3O8. Uranium deposits are generally tabular in form and dimensions range up to 380 m long, 210 m wide, and 50 m thick. Deposits are bounded on at least one side by unmineralized intrusive ribs of granitic rock, and thickest mineralized zones invariably occur at depressions in the intrusive contact. Upper limits of some deposits are nearly horizontal, and upper elevations of adjacent mineralized zones separated by ribs of granite are similar. Near surface ore is predominantly autunite, but ore at depth consists of pitchblende and coffinite with abundant pyrite and marcasite. Uranium minerals occur as .disseminations along foliation, replacements, and stockwork fracture-fillings. No stratigraphic controls on ore deposition are recognized. Rather, mineralized zones cut across lithologic boundaries if permeability is adequate. Most ore is in muscovite schist and mica phyllite, but important deposits occur in calc-silicate hornfels. Amphibolite sills and mid-Tertiary dacite dikes locally, carry ore where intensely fractured. High content of iron and sulfur, contained chiefly in FeS2, appear to be an important feature of favorable host rocks. Geometry of deposits, structural, and geochemical features suggest that uranium minerals were deposited over a span of time from late Cretaceous to late Tertiary. Ore occurs in but is not offset by a shear zone that displaces mid-Tertiary rocks.. Economic zones of uranium are interpreted to have been secondarily enriched in late Tertiary time by downward and lateral migration of uranium into permeable zones where deposition was influenced by ground water controls and minerals that could reduce or neutralize uranium-bearing solutions.

Kinetic study of the thermal decomposition of uranium metaphosphate, U(PO3)4, into uranium pyrophosphate, UP2O7

NASA Astrophysics Data System (ADS)

Yang, Hee-Chul; Kim, Hyung-Ju; Lee, Si-Young; Yang, In-Hwan; Chung, Dong-Yong

2017-06-01

The thermochemical properties of uranium compounds have attracted much interest in relation to thermochemical treatments and the safe disposal of radioactive waste bearing uranium compounds. The characteristics of the thermal decomposition of uranium metaphosphate, U(PO3)4, into uranium pyrophosphate, UP2O7, have been studied from the view point of reaction kinetics and acting mechanisms. A mixture of U(PO3)4 and UP2O7 was prepared from the pyrolysis residue of uranium-bearing spent TBP. A kinetic analysis of the reaction of U(PO3)4 into UP2O7 was conducted using an isoconversional method and a master plot method on the basis of data from a non-isothermal thermogravimetric analysis. The thermal decomposition of U(PO3)4 into UP2O7 followed a single-step reaction with an activation energy of 175.29 ± 1.58 kJ mol-1. The most probable kinetic model was determined as a type of nucleation and nuclei-growth models, the Avrami-Erofeev model (A3), which describes that there are certain restrictions on nuclei growth of UP2O7 during the solid-state decomposition of U(PO3)4.

Photocatalytic decomposition of Rhodamine B on uranium-doped mesoporous titanium dioxide

DOE PAGES

Liu, Yi; Becker, Blake; Burdine, Brandon; ...

2017-04-13

Mesoporous uranium-doped TiO 2 anatase materials were studied to determine the influence of U-doping on the photocatalytic properties for Rhodamine B (RhB) degradation. The physico-chemical properties of the samples were characterized and the results of X-ray diffraction, transmission electron microscopy, and Raman spectroscopy demonstrate homogeneous incorporation of uranium into the anatase lattice. X-ray photoelectron spectroscopy of the doped anatase confirmed the dominance of the U 4+ species and an increasing proportion of U 6+ species as the uranium doping was increased. The absorption thresholds of the uranium-doped anatase extended into the visible light region. A synergistic effect of the bandmore » gap energy and oxidation state of the dopant contribute to an enhanced photocatalytic capability for RhB degradation by U-doped TiO 2.« less

Photocatalytic decomposition of Rhodamine B on uranium-doped mesoporous titanium dioxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Yi; Becker, Blake; Burdine, Brandon

Mesoporous uranium-doped TiO 2 anatase materials were studied to determine the influence of U-doping on the photocatalytic properties for Rhodamine B (RhB) degradation. The physico-chemical properties of the samples were characterized and the results of X-ray diffraction, transmission electron microscopy, and Raman spectroscopy demonstrate homogeneous incorporation of uranium into the anatase lattice. X-ray photoelectron spectroscopy of the doped anatase confirmed the dominance of the U 4+ species and an increasing proportion of U 6+ species as the uranium doping was increased. The absorption thresholds of the uranium-doped anatase extended into the visible light region. A synergistic effect of the bandmore » gap energy and oxidation state of the dopant contribute to an enhanced photocatalytic capability for RhB degradation by U-doped TiO 2.« less

METHOD FOR PURIFYING URANIUM

DOEpatents

Kennedy, J.W.; Segre, E.G.

1958-08-26

A method is presented for obtaining a compound of uranium in an extremely pure state and in such a condition that it can be used in determinations of the isotopic composition of uranium. Uranium deposited in calutron receivers is removed therefrom by washing with cold nitric acid and the resulting solution, coataining uranium and trace amounts of various impurities, such as Fe, Ag, Zn, Pb, and Ni, is then subjected to various analytical manipulations to obtain an impurity-free uranium containing solution. This solution is then evaporated on a platinum disk and the residue is ignited converting it to U2/sub 3//sub 8/. The platinum disk having such a thin film of pure U/sub 2/O/sub 8/ is suitable for use with isotopic determination techaiques.

Development of a reactive zone technology for simultaneous in situ immobilisation of radium and uranium

NASA Astrophysics Data System (ADS)

Burghardt, D.; Kassahun, A.

2005-12-01

Simultaneous in situ immobilisation of uranium (U) and radium (226Ra) by injectible amounts of grey cast iron (gcFe), nano-scale iron (naFe) and a gcFe/MnO2 mixture (1:1) was studied in batch and column tests. Both 0.5 g/L naFe and gcFe are effective in 226Ra and U removal from mine water, whereas MnO2 addition clearly increased the efficiency of gcFe for 226Ra and U immobilisation. In a column test with 0.6 wt% gcFe/MnO2 mixture (1:1), neither 226Ra nor U was detected in the effluent after replacement of 45 pore volumes. A sequential extraction under flow condition revealed 226Ra to be mostly occluded in manganese oxides. Uranium was mostly sorbed onto poorly crystalline iron hydroxides, but a significant part was found to be occluded in manganese oxides also. The results of this study suggest that MnO2 promotes iron hydroxide formation under slightly reducing environmental conditions resulting in an increased pollutant retention capacity.

Adsorption of uranium composites onto saltrock oxides - experimental and theoretical study.

PubMed

Ivanova, Bojidarka; Spiteller, Michael

2014-09-01

The study encompassed experimental mass spectrometric and theoretical quantum chemical studies on adsorption of uranium species in different oxidation states of the metal ion, and oxides of UxOy(n+) type, where x = 1 or 3, y = 2 or 8, and n = 0, 1 or 2 onto nanosize-particles of saltrock oxides MO (M = Mg(II), Ca(II), Ni(II), Co(II), Sr(II) or Ba(II)), M2Oy (M = Au(III) or Ag(I), y = 3 or 1) silicates 3Al2O3.2SiO2, natural kaolinite (Al2O2·2SiO2·2H2O), illite (K0.78Ca0.02Na0.02(Mg0.34Al1.69Fe(III)0.02)[Si3.35Al0.65]O10(OH)2·nH2O), CaSiO3, 3MgO·4SiO2,H2O, and M(1)M(2)(SiO4)X2 (M(1) = M(2) = Al or M(1) = K, M(2) = Al, X = F or Cl), respectively. The UV-MALDI-Orbitrap mass spectrometry was utilized in solid-state and semi-liquid colloidal state, involving the laser ablation at λex = 337.2 nm. The theoretical modeling and experimental design was based on chemical-, physico-chemical, physical and biological processes involving uranium species under environmental conditions. Therefore, the results reported are crucial for quality control and monitoring programs for assessment of radionuclide migration. They impact significantly the methodology for evaluation of human health risk from radioactive contamination. The study has importance for understanding the coordination and red-ox chemistry of uranium compounds as well. Due to the double nature of uranium between rare element and superconductivity like materials as well as variety of oxidation states ∈ (+1)-(+6), the there remain challenging areas for theoretical and experimental research, which are of significant importance for management of nuclear fuel cycles and waste storage. Copyright © 2014 Elsevier Ltd. All rights reserved.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Campbell, Keri R.; Judge, Elizabeth J.; Barefield, James E.

We show the analysis of light water reactor simulated used nuclear fuel using laser-induced breakdown spectroscopy (LIBS) is explored using a simplified version of the main oxide phase. The main oxide phase consists of the actinides, lanthanides, and zirconium. The purpose of this study is to develop a rapid, quantitative technique for measuring zirconium in a uranium dioxide matrix without the need to dissolve the material. A second set of materials including cerium oxide is also analyzed to determine precision and limit of detection (LOD) using LIBS in a complex matrix. Two types of samples are used in this study:more » binary and ternary oxide pellets. The ternary oxide, (U,Zr,Ce)O 2 pellets used in this study are a simplified version the main oxide phase of used nuclear fuel. The binary oxides, (U,Ce)O 2 and (U,Zr)O 2 are also examined to determine spectral emission lines for Ce and Zr, potential spectral interferences with uranium and baseline LOD values for Ce and Zr in a UO 2 matrix. In the spectral range of 200 to 800 nm, 33 cerium lines and 25 zirconium lines were identified and shown to have linear correlation values (R 2) > 0.97 for both the binary and ternary oxides. The cerium LOD in the (U,Ce)O 2 matrix ranged from 0.34 to 1.08 wt% and 0.94 to 1.22 wt% in (U,Ce,Zr)O 2 for 33 of Ce emission lines. The zirconium limit of detection in the (U,Zr)O 2 matrix ranged from 0.84 to 1.15 wt% and 0.99 to 1.10 wt% in (U,Ce,Zr)O 2 for 25 Zr lines. Finally, the effect of multiple elements in the plasma and the impact on the LOD is discussed.« less

Modelling of the dissolution and reprecipitation of uranium under oxidising conditions in the zone of shallow groundwater circulation.

PubMed

Dutova, Ekaterina M; Nikitenkov, Aleksei N; Pokrovskiy, Vitaly D; Banks, David; Frengstad, Bjørn S; Parnachev, Valerii P

2017-11-01

Generic hydrochemical modelling of a grantoid-groundwater system, using the Russian software "HydroGeo", has been carried out with an emphasis on simulating the accumulation of uranium in the aqueous phase. The baseline model run simulates shallow granitoid aquifers (U content 5 ppm) under conditions broadly representative of southern Norway and southwestern Siberia: i.e. temperature 10 °C, equilibrated with a soil gas partial CO 2 pressure (P CO2 , open system) of 10 -2.5 atm. and a mildly oxidising redox environment (Eh = +50 mV). Modelling indicates that aqueous uranium accumulates in parallel with total dissolved solids (or groundwater mineralisation M - regarded as an indicator of degree of hydrochemical evolution), accumulating most rapidly when M = 550-1000 mg L -1 . Accumulation slows at the onset of saturation and precipitation of secondary uranium minerals at M = c. 1000 mg L -1 (which, under baseline modelling conditions, also corresponds approximately to calcite saturation and transition to Na-HCO 3 hydrofacies). The secondary minerals are typically "black" uranium oxides of mixed oxidation state (e.g. U 3 O 7 and U 4 O 9 ). For rock U content of 5-50 ppm, it is possible to generate a wide variety of aqueous uranium concentrations, up to a maximum of just over 1 mg L -1 , but with typical concentrations of up to 10 μg L -1 for modest degrees of hydrochemical maturity (as indicated by M). These observations correspond extremely well with real groundwater analyses from the Altai-Sayan region of Russia and Norwegian crystalline bedrock aquifers. The timing (with respect to M) and degree of aqueous uranium accumulation are also sensitive to Eh (greater mobilisation at higher Eh), uranium content of rocks (aqueous concentration increases as rock content increases) and P CO2 (low P CO2 favours higher pH, rapid accumulation of aqueous U and earlier saturation with respect to uranium minerals). Copyright © 2017 Elsevier Ltd. All rights reserved.

Characterisation and dissolution of depleted uranium aerosols produced during impacts of kinetic energy penetrators against a tank.

PubMed

Chazel, V; Gerasimo, P; Dabouis, V; Laroche, P; Paquet, F

2003-01-01

Aerosols produced during impacts of depleted uranium (DU) penetrators against the glacis (sloping armour) and the turret of a tank were sampled. The concentration and size distribution were determined. Activity median aerodynamic diameters were 1 microm (geometric standard deviation, sigma(g) = 3.7) and 2 microm (sigma(g) = 2.5), respectively, for glacis and turret. The mean air concentration was 120 Bq m(-3), i.e. 8.5 mg m(-3) of DU. Filters analysed by scanning electron microscopy (SEM) and X ray diffraction showed two types of particles (fine particles and large molten particles) composed mainly of a mixture of uranium and aluminium. The uranium oxides were mostly U3O8, UO2.25 and probably UO3.01 and a mixed compound of U and Al. The kinetics of dissolution in three media (HCO3-, HCl and Gamble's solution) were determined using in-vitro tests. The slow dissolution rates were respectively slow, and intermediate between slow and moderate, and the rapid dissolution fractions were mostly intermediate between moderate and fast. According to the in-vitro results for Gamble's solution, and based on a hypothetical single acute inhalation of 90 Bq, effective doses integrated up to 1 y after incorporation were 0.54 and 0.56 mSv, respectively, for aerosols from glacis and turret. In comparison, the ICRP limits are 20 mSv y(-1) for workers and 1 mSv y(-1) for members of the public. A kidney concentration of approximately 0.1 microg U g(-1) was predicted and should not, in this case, lead to kidney damage.

Uranium(VI) interactions with mackinawite in the presence and absence of bicarbonate and oxygen.

PubMed

Gallegos, Tanya J; Fuller, Christopher C; Webb, Samuel M; Betterton, William

2013-07-02

Mackinawite, Fe(II)S, samples loaded with uranium (10(-5), 10(-4), and 10(-3) mol U/g FeS) at pH 5, 7, and 9, were characterized using X-ray absorption spectroscopy and X-ray diffraction to determine the effects of pH, bicarbonate, and oxidation on uptake. Under anoxic conditions, a 5 g/L suspension of mackinawite lowered 5 × 10(-5) M uranium(VI) to below 30 ppb (1.26 × 10(-7) M) U. Between 82 and 88% of the uranium removed from solution by mackinawite was U(IV) and was nearly completely reduced to U(IV) when 0.012 M bicarbonate was added. Near-neighbor coordination consisting of uranium-oxygen and uranium-uranium distances indicates the formation of uraninite in the presence and absence of bicarbonate, suggesting reductive precipitation as the dominant removal mechanism. Following equilibration in air, mackinawite was oxidized to mainly goethite and sulfur and about 76% of U(IV) was reoxidized to U(VI) with coordination of uranium to axial and equatorial oxygen, similar to uranyl. Additionally, uranium-iron distances, typical of coprecipitation of uranium with iron oxides, and uranium-sulfur distances indicating bidentate coordination of U(VI) to sulfate were evident. The affinity of mackinawite and its oxidation products for U(VI) provides impetus for further study of mackinawite as a potential reactive medium for remediation of uranium-contaminated water.

Uranium metallogenesis of the peraluminous leucogranite from the Pontivy-Rostrenen magmatic complex (French Armorican Variscan belt): the result of long-term oxidized hydrothermal alteration during strike-slip deformation

NASA Astrophysics Data System (ADS)

Ballouard, C.; Poujol, M.; Mercadier, J.; Deloule, E.; Boulvais, P.; Baele, J. M.; Cuney, M.; Cathelineau, M.

2018-06-01

In the French Armorican Variscan belt, most of the economically significant hydrothermal U deposits are spatially associated with peraluminous leucogranites emplaced along the south Armorican shear zone (SASZ), a dextral lithospheric scale wrench fault that recorded ductile deformation from ca. 315 to 300 Ma. In the Pontivy-Rostrenen complex, a composite intrusion, the U mineralization is spatially associated with brittle structures related to deformation along the SASZ. In contrast to monzogranite and quartz monzodiorite (3 < U < 9 ppm; Th/U > 3), the leucogranite samples are characterized by highly variable U contents ( 3 to 27 ppm) and Th/U ratios ( 0.1 to 5) suggesting that the crystallization of magmatic uranium oxide in the more evolved facies was followed by uranium oxide leaching during hydrothermal alteration and/or surface weathering. U-Pb dating of uranium oxides from the deposits reveals that they mostly formed between ca. 300 and 270 Ma. In monzogranite and quartz monzodiorite, apatite grains display magmatic textures and provide U-Pb ages of ca. 315 Ma reflecting the time of emplacement of the intrusions. In contrast, apatite grains from the leucogranite display textural, geochemical, and geochronological evidences for interaction with U-rich oxidized hydrothermal fluids contemporaneously with U mineralizing events. From 300 to 270 Ma, infiltration of surface-derived oxidized fluids leached magmatic uranium oxide from fertile leucogranite and formed U deposits. This phenomenon was sustained by brittle deformation and by the persistence of thermal anomalies associated with U-rich granitic bodies.

Environmental modeling of uranium interstitial compositions of non-stoichiometric oxides: experimental and theoretical analysis.

PubMed

Ivanova, Bojidarka

2016-10-01

Study of uranium interstitial compositions of non-stoichiometric oxides UO2+x (x ∈ 0.1-0.02) in gas and condense phases has been presented, using various soft-ionization mass spectrometric methods such as ESI-, APCI-, and MALDI-MS at a wide dynamic temperature gradient (∈ 25-300 °C). Linearly polarized vibrational spectroscopy has been utilized in order to assign unambiguously, the vibrational frequencies of uranium non-stoichiometric oxides. Experimental design has involved xUO2.66·yUO2.33, xUO2.66·yUO2.33/SiO2, xUO2.66·yUO2.33/SiO2 (NaOH) and SiO2/x'NaOH·y'UO2(NO3)2·6H2O, multicomponent systems (x = 1, y ∈ 0.1-1.0 and x' = 1, y' ∈ 0.1-0.6) as well as phase transitions UO2(NO3)2·6H2O → {U4O9(UO2.25)} → U3O7(UO2.33) → U3O8(UO2.66) → {UO3}, thus ensuring a maximal representativeness to real environmental conditions, where diverse chemical, geochemical and biochemical reactions, including complexation and sorption onto minerals have occurred. Experimental factors such as UV-irradiation, pH, temperature, concentration levels, solvent types and ion strength have been taken into consideration, too. As far as uranium speciation represents a challenging analytical task in terms of chemical identification diverse coordination species, mechanistic aspects relating incorporation of oxygen into UO 2+x form the shown full methods validation significantly impacts the field of environmental radioanalytical chemistry. UO2 is the most commonly used fuel in nuclear reactors around the globe; however, a large non-stoichiometric range ∈ UO1.65-UO2.25 has occurred due to radiolysis of water on UO2 surface yielding to H2O2, OH(·), and more. Each of those compositions has different oxygen diffusion. And in this respect enormous effort has been concentrated to study the potential impact of hazardous radionuclide on the environment, encompassing from the reprocessing to the disposal stages of the fuel waste, including the waste itself, the processes in the waste containers, the clay around the containers, and geological processes. In a broader sense, thereby, this study contributes to field of environmental analysis highlighting the great ability of various soft-ionization MS methods, particularly, MALDI-MS one, for direct assay of complex multicomponent heterogeneous mixtures at fmol-attomol concentration ranges, along with it the great instrumental features allowing, not only meaningful quantitative, but also structural information of the analytes, thus making the method indispensable for environmental speciation of radionuclides, generally.

Uranium speciation in acid waste-weathered sediments: The role of aging and phosphate amendments

DOE PAGES

Perdrial, Nicolas; Vázquez-Ortega, Angélica; Wang, Guohui; ...

2017-12-05

Uranium speciation and lability are strongly coupled to mineral transformations in silicate sediments, particularly for sediments subjected to weathering in acidic, high-level radioactive waste, as occurred at the Department of Energy's Hanford (WA) site. Here, uncontaminated Hanford sediments were reacted for 365 days with acidic (pH 3), uranium-bearing waste solutions, with and without phosphate in batch experiments, prior to detailed characterizations using electron microscopy, x-ray diffraction and x-ray absorption spectroscopy. In PO 4-reactant free systems, uranium speciation was controlled initially by precipitation of compreignacite [K 2(UO 2) 6O 4(OH) 6·8H 2O]- and becquerelite [Ca(UO 2) 6O 4(OH) 6·8H 2O]-like species.more » Subsequent further removal of uranium coincided with that of Si and accumulation of boltwoodite, [(K, Na)(UO 2) 2O 4(HSiO 4) 2•0.5(H 2O)]-like species of uranium at 180 and 365 days. When present, PO 4 exerted a direct and strong control over U speciation. Furthermore, the detection of meta-ankoleite, [K 2(UO 2) 2O 4(PO 4) 2·6H 2O] at all reaction times when U was present emphasizes the importance of dissolved phosphate as a control on U speciation. Here, meta-ankoleite appears well crystallized and when it occurs as the principal product of sediment weathering, its low solubility is expected to limit dissolved U(VI) concentrations in groundwater. Although boltwoodite solubility is also low, it is formed more slowly (and only when PO 4 is absent), after initial precipitation of more soluble, less crystalline uranyl hydroxides. In the context of Hanford crib waste our results suggest that with PO 4 present, nearly all uranium would have precipitated in the upper soil.« less

Uranium speciation in acid waste-weathered sediments: The role of aging and phosphate amendments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Perdrial, Nicolas; Vázquez-Ortega, Angélica; Wang, Guohui

Uranium speciation and lability are strongly coupled to mineral transformations in silicate sediments, particularly for sediments subjected to weathering in acidic, high-level radioactive waste, as occurred at the Department of Energy's Hanford (WA) site. In this study, uncontaminated Hanford sediments were reacted for 365 days with acidic (pH 3), uranium-bearing waste solutions, with and without phosphate in batch experiments, prior to detailed characterizations using electron microscopy, x-ray diffraction and x-ray absorption spectroscopy. In PO(4)(-)reactant free systems, uranium speciation was controlled initially by precipitation of compreignacite [K-2(UO2)(6)O-4(OH)(6)center dot 8H(2)O]-and becquerelite [Ca(UO2)(6)O-4(OH)(6)center dot 8H(2)O]-like species. Subsequent further removal of uranium coincided withmore » that of Si and accumulation of boltwoodite, [(K, Na)(UO2)(2)O-4(HSiO4)(2)center dot 0.5(H2O)]-like species of uranium at 180 and 365 days. When present, PO4 exerted a direct and strong control over U speciation. The detection of meta-ankoleite, [K-2(UO2)(2)O-4(PO4)(2)center dot 6H(2)O] at all reaction times when U was present emphasizes the importance of dissolved phosphate as a control on U speciation. Here, meta-ankoleite appears well crystallized and when it occurs as the principal product of sediment weathering, its low solubility is expected to limit dissolved U(VI) concentrations in groundwater. Although boltwoodite solubility is also low, it is formed more slowly (and only when PO4 is absent), after initial precipitation of more soluble, less crystalline uranyl hydroxides. In the context of Hanford crib waste our results suggest that with PO4 present, nearly all uranium would have precipitated in the upper soil.« less

Uranium speciation in acid waste-weathered sediments: The role of aging and phosphate amendments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Perdrial, Nicolas; Vázquez-Ortega, Angélica; Wang, Guohui

Uranium speciation and lability are strongly coupled to mineral transformations in silicate sediments, particularly for sediments subjected to weathering in acidic, high-level radioactive waste, as occurred at the Department of Energy's Hanford (WA) site. Here, uncontaminated Hanford sediments were reacted for 365 days with acidic (pH 3), uranium-bearing waste solutions, with and without phosphate in batch experiments, prior to detailed characterizations using electron microscopy, x-ray diffraction and x-ray absorption spectroscopy. In PO 4-reactant free systems, uranium speciation was controlled initially by precipitation of compreignacite [K 2(UO 2) 6O 4(OH) 6·8H 2O]- and becquerelite [Ca(UO 2) 6O 4(OH) 6·8H 2O]-like species.more » Subsequent further removal of uranium coincided with that of Si and accumulation of boltwoodite, [(K, Na)(UO 2) 2O 4(HSiO 4) 2•0.5(H 2O)]-like species of uranium at 180 and 365 days. When present, PO 4 exerted a direct and strong control over U speciation. Furthermore, the detection of meta-ankoleite, [K 2(UO 2) 2O 4(PO 4) 2·6H 2O] at all reaction times when U was present emphasizes the importance of dissolved phosphate as a control on U speciation. Here, meta-ankoleite appears well crystallized and when it occurs as the principal product of sediment weathering, its low solubility is expected to limit dissolved U(VI) concentrations in groundwater. Although boltwoodite solubility is also low, it is formed more slowly (and only when PO 4 is absent), after initial precipitation of more soluble, less crystalline uranyl hydroxides. In the context of Hanford crib waste our results suggest that with PO 4 present, nearly all uranium would have precipitated in the upper soil.« less

The effect of fission products on the rate of U3O8 formation in SIMFUEL oxidized in air at 250°C

NASA Astrophysics Data System (ADS)

Choi, Jong-Won; McEachern, Rod J.; Taylor, Peter; Wood, Donald D.

1996-06-01

The effect of fission products on the rate of U3O8 formation was investigated by oxidizing UO2-based SIMFUEL (simulated high burnup nuclear fuel) and unirradiated UO2 fuel specimens in air at 250°C for different times (1-317 days). The progress of oxidation was monitored by X-ray diffraction, revealing that the rate of U3O8 formation declines with increasing burnup. An expression was derived to describe quantitatively the time for U3O8 powder formation as a function of simulated burnup. These findings were supported by additional isochronal oxidation experiments conducted between 200 and 300°C.

Influence of uranyl speciation and iron oxides on uranium biogeochemical redox reactions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stewart, B.D.; Amos, R.T.; Nico, P.S.

2010-03-15

Uranium is a pollutant of concern to both human and ecosystem health. Uranium's redox state often dictates its partitioning between the aqueous- and solid-phases, and thus controls its dissolved concentration and, coupled with groundwater flow, its migration within the environment. In anaerobic environments, the more oxidized and mobile form of uranium (UO{sub 2}{sup 2+} and associated species) may be reduced, directly or indirectly, by microorganisms to U(IV) with subsequent precipitation of UO{sub 2}. However, various factors within soils and sediments may limit biological reduction of U(VI), inclusive of alterations in U(VI) speciation and competitive electron acceptors. Here we elucidate themore » impact of U(VI) speciation on the extent and rate of reduction with specific emphasis on speciation changes induced by dissolved Ca, and we examine the impact of Fe(III) (hydr)oxides (ferrihydrite, goethite and hematite) varying in free energies of formation on U reduction. The amount of uranium removed from solution during 100 h of incubation with S. putrefaciens was 77% with no Ca or ferrihydrite present but only 24% (with ferrihydrite) and 14% (no ferrihydrite) were removed for systems with 0.8 mM Ca. Imparting an important criterion on uranium reduction, goethite and hematite decrease the dissolved concentration of calcium through adsorption and thus tend to diminish the effect of calcium on uranium reduction. Dissimilatory reduction of Fe(III) and U(VI) can proceed through different enzyme pathways, even within a single organism, thus providing a potential second means by which Fe(III) bearing minerals may impact U(VI) reduction. We quantify rate coefficients for simultaneous dissimilatory reduction of Fe(III) and U(VI) in systems varying in Ca concentration (0 to 0.8 mM), and using a mathematical construct implemented with the reactive transport code MIN3P, we reveal the predominant influence of uranyl speciation, specifically the formation of uranyl-calcium-carbonato complexes, and ferrihydrite on the rate and extent of uranium reduction in complex geochemical systems.« less

Uranium(VI) interactions with mackinawite in the presence and absence of bicarbonate and oxygen

USGS Publications Warehouse

Gallegos, Tanya J.; Fuller, Christopher C.; Webb, Samuel M.; Betterton, William J.

2013-01-01

Mackinawite, Fe(II)S, samples loaded with uranium (10-5, 10-4, and 10-3 mol U/g FeS) at pH 5, 7, and 9, were characterized using X-ray absorption spectroscopy and X-ray diffraction to determine the effects of pH, bicarbonate, and oxidation on uptake. Under anoxic conditions, a 5 g/L suspension of mackinawite lowered 5 × 10-5 M uranium(VI) to below 30 ppb (1.26 × 10-7 M) U. Between 82 and 88% of the uranium removed from solution by mackinawite was U(IV) and was nearly completely reduced to U(IV) when 0.012 M bicarbonate was added. Near-neighbor coordination consisting of uranium–oxygen and uranium-uranium distances indicates the formation of uraninite in the presence and absence of bicarbonate, suggesting reductive precipitation as the dominant removal mechanism. Following equilibration in air, mackinawite was oxidized to mainly goethite and sulfur and about 76% of U(IV) was reoxidized to U(VI) with coordination of uranium to axial and equatorial oxygen, similar to uranyl. Additionally, uranium-iron distances, typical of coprecipitation of uranium with iron oxides, and uranium-sulfur distances indicating bidentate coordination of U(VI) to sulfate were evident. The affinity of mackinawite and its oxidation products for U(VI) provides impetus for further study of mackinawite as a potential reactive medium for remediation of uranium-contaminated water.

Uranium in foraminiferal calcite as a recorder of seawater uranium concentrations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Russell, A.D.; Emerson, S.; Nelson, B.K.

The authors present results of an investigation of uranium/calcium ratios in cleaned foraminiferal calcite as a recorder of seawater uranium concentrations. For accurate reconstruction of past seawater uranium content, shell calcite must incorporate uranium in proportion to seawater concentration and must preserve its original uranium composition over time. Laboratory culture experiments with live benthic (Amphistegina lobifera) and live planktonic (Globigerinell calida) foraminifera show that the U/Ca ratio of cleaned calcite tests is proportional to the concentration of uranium in solution. After correcting results for the presence of initial calcite, the apparent distribution coefficient D = (U/Ca[sub calcite])/(U/Ca)[sub solution] = 10.6more » [+-] 0.3 (x10[sup [minus]3]) for A. lobifera and D = 7.9 [+-] 0.1 (x10[sup [minus]3]) for G. calida. U/Ca ratios in planktonic foraminifera from core tops collected above 3900 m in the equatorial Atlantic and above 2100 m in the Pacific Ocean show no significant difference among the species analyzed. D estimated form core top samples ranges from 7.6 [+-] 0.4 (x10[sup [minus]3]) for O. universa to 8.4 [+-] 0.5 (x10[sup [minus]3]) for G. ruber. In benthic species C. wuellerstorfi, D = 7.0 [+-] 0.8 (x10[sup [minus]3]). U/Ca and Mg/Ca in G. tumida and G. sacculifer from core tops taken near and below the regional lysocline decrease with water depth. Smaller decreases in U/Ca and Mg/Ca with depth were observed in C. wuellerstorfi. In the planktonic species, the authors believe that U/CA and Mg/Ca are lower in the more dissolution-resistant fraction of calcite, leading to lower U/Ca in more highly dissolved samples.« less

Optimization of a bioremediation system of soluble uranium based on the biostimulation of an indigenous bacterial community.

PubMed

Maleke, Maleke; Williams, Peter; Castillo, Julio; Botes, Elsabe; Ojo, Abidemi; DeFlaun, Mary; van Heerden, Esta

2015-06-01

High concentrations of uranium(VI) in the Witwatersrand Basin, South Africa from mining leachate is a serious environmental concern. Treatment systems are often ineffective. Therefore, optimization of a bioremediation system that facilitates the bioreduction of U(VI) based on biostimulation of indigenous bacterial communities can be a viable alternative. Tolerance of the indigenous bacteria to high concentrations of U and the amount of citric acid required for U removal was optimized. Two bioreactor studies which showed effective U(VI) removal more than 99 % from low (0.0037 mg L(-1)) and high (10 mg L(-1)) concentrations of U to below the limit allowed by South African National Standards for drinking water (0.0015 mg L(-1)). The second bioreactor was able to successfully adapt even with increasing levels of U(VI) feed water up to 10 mg L(-1), provided that enough electron donor was available. Molecular biology analyses identified Desulfovibrio sp. and Geobacter sp. among known species, which are known to reduce U(VI). The mineralogical analysis determined that part of the uranium precipitated intracellularly, which meant that the remaining U(VI) was precipitated as U(IV) oxides and TEM-EDS also confirmed this analysis. This was predicted with the geochemical model from the chemical data, which demonstrated that the treated drainage was supersaturated with respect to uraninite > U4O9 > U3O8 > UO2(am). Therefore, the tolerance of the indigenous bacterial community could be optimized to remediate up to 10 mg L(-1), and the system can thus be upscaled and employed for remediation of U(VI) impacted sites.

Forms of uranium associated to silica in the environment of the Nopal deposit (Mexico)

NASA Astrophysics Data System (ADS)

Allard, T.; Othmane, G.; Menguy, N.; Vercouter, T.; Morin, G.; Calas, G.; Fayek, M.

2011-12-01

The understanding of the processes that control the transfers of uranium in the environment is necessary for the safety assessement of nuclear waste repositories. In particular, several poorly ordered phases (e.g. Fe oxihydroxides) are expected to play an important role in trapping uranium from surface waters. Among them, natural systems containing amorphous silica are poorly documented. A former study from the environment of the Peny mine (France) showed the importance of silica in uranium speciation [1]. The Nopal uranium deposit is located in volcanic tuff from tertiary period. It hosted several hydrothermal alteration episodes responsible for clay minerals formation. A primary uranium mineralisation occurred in a breccia pipe, consisting in uraninite, subsequently altered in secondary uranium minerals among which several silicates. Eventually, opal was formed and coated uranyl silicates such as uranophane and weeksite [2], [3]. Opals also contain minor amounts of uranium. The Nopal deposit is still considered as a natural analogue of high level nuclear waste repository located in volcanic tuff. It may be used to reveal the low temperature conditions of trapping of uranium in systems devoid of iron oxides such as silica-containing ones. The aim of this study is then to determine the uranium speciation, and its possible complexity, associated to these opals that represent a late trapping episode. It will provide insights ranging from the micrometer scale of electron microscopies to the molecular scale provided by fluorescence spectroscopy. Three samples of green or yellow opals have been analysed by a combination of complementary tools including scanning electron microscopy (SEM) on cross-sections, transmission electron microscopy (TEM) on focused ion beam (FIB) films, cathodoluminescence and time-resolved laser fluorescence spectroscopy (TRLFS). Uranium speciation was found to be complex. We first evidence U-bearing microparticles of beta-uranophane Ca[(UO2)(SiO3OH)]2(H2O)5 and apatite Ca5(PO4)3(OH,Cl,F) containing minor amounts of uranium. Uranophane was formed prior to opal and coated by it. However the major part of uranium is concentrated in Ca-U-enriched zones with a Ca:U ratio of 1:1 and displaying botryoidal features. The exact nature of Ca-U species in these zones was not specified but TEM, cathodoluminescence and TRLFS analyses suggest the presence of Cam-(UO2)m-(O/OH/H2O)n complexes adsorbed or incorporated in opal. These results will be discussed in terms of chemical conditions that prevailed during U incorporation and compared to other known U-Si environmental systems, including the Peny system (France). [1] Allard, T. et al. (1999) Chem. Geol., 158, 81-103 [2] Calas, G. et al. (2008) Terra Nova, 20, 206-212. [3] Schindler, M. et al. (2010) Geochim. Cosmochim. Ac, 74, 187-202.

Visualizing different uranium oxidation states during the surface alteration of uraninite and uranium tetrachloride.

PubMed

Grossmann, Kay; Arnold, Thuro; Steudtner, Robin; Weiss, Stefan; Bernhard, Gert

2009-08-01

Low-temperature alteration reactions on uranium phases may lead to the mobilization of uranium and thereby poses a potential threat to humans living close to uranium-contaminated sites. In this study, the surface alteration of uraninite (UO(2)) and uranium tetrachloride (UCl(4)) in air atmosphere was studied by confocal laser scanning microscopy (CLSM) and laser-induced fluorescence spectroscopy using an excitation wavelength of 408 nm. It was found that within minutes the oxidation state on the surface of the uraninite and the uranium tetrachloride changed. During the surface alteration process U(IV) atoms on the uraninite and uranium tetrachloride surface became stepwise oxidized by a one-electron step at first to U(V) and then further to U(VI). These observed changes in the oxidation states of the uraninite surface were microscopically visualized and spectroscopically identified on the basis of their fluorescence emission signal. A fluorescence signal in the wavelength range of 415-475 nm was indicative for metastable uranium(V), and a fluorescence signal in the range of 480-560 nm was identified as uranium(VI). In addition, the oxidation process of tetravalent uranium in aqueous solution at pH 0.3 was visualized by CLSM and U(V) was fluorescence spectroscopically identified. The combination of microscopy and fluorescence spectroscopy provided a very convincing visualization of the brief presence of U(V) as a metastable reaction intermediate and of the simultaneous coexistence of the three states U(IV), U(V), and U(VI). These results have a significant importance for fundamental uranium redox chemistry and should contribute to a better understanding of the geochemical behavior of uranium in nature.

Formation and reduction behaviors of zirconium oxide compounds in LiCl-Li2O melt at 923 K

NASA Astrophysics Data System (ADS)

Sakamura, Yoshiharu; Iizuka, Masatoshi; Kitawaki, Shinichi; Nakayoshi, Akira; Kofuji, Hirohide

2015-11-01

The reduction behaviors of ZrO2, Li2ZrO3 and (U,Pu,Zr)O2 in a LiCl-Li2O salt bath at 923 K were investigated. This study was conducted as part of a feasibility study on the pyrochemical treatment of damaged fuel debris generated by severe accidents at light water reactors. It was demonstrated in electrolytic reduction tests that the uranium in synthetic corium specimens of (U,Pu,Zr)O2 with various ZrO2 contents could be reduced to the metallic form and that part of the zirconium was converted to Li2ZrO3. Zirconium metal and Li2ZrO3 were obtained by the reduction of ZrO2. The reduction of Li2ZrO3 did not proceed even in LiCl containing no Li2O. Moreover, the stable chemical forms of the ZrO2-Li2O complex oxide were investigated as a function of the Li2O concentration in LiCl. ZrO2 was converted to Li2ZrO3 at a Li2O concentration of 0.018 wt%. As the Li2O concentration was increased, Li2ZrO3 was converted to Li6Zr2O7 and then to Li8ZrO6. It is suggested that the removal of Li2ZrO3 from the reduction product is a key point in the pyrochemical treatment of corium.

Uranium(iii) complexes supported by hydrobis(mercaptoimidazolyl)borates: synthesis and oxidation chemistry.

PubMed

Maria, Leonor; Santos, Isabel C; Santos, Isabel

2018-05-23

The reaction of [UI3(thf)4] with the sodium or lithium salts of hydrobis(2-mercapto-1-methylimidazolyl)borate ligands ([H(R)B(timMe)2]-) in a 1 : 2 ratio, in tetrahydrofuran, gave the U(iii) complexes [UI{κ3-H,S,S'-H(R)B(timMe)2}2(thf)2] (R = H (1), Ph (2)) in good yields. Crystals of [UI{κ3-H,S,S'-H(Ph)B(timMe)2}2(thf)2] (2) were obtained by recrystallization from a tetrahydrofuran/acetonitrile solution, and the ion-separated uranium complex [U{κ3-H,S,S'-H(Ph)B(timMe)2}2(CH3CN)3][I] (3-I) was obtained by dissolution of 2 in acetonitrile followed by recrystallization. One-electron oxidation of 2 with AgBPh4 or I2 resulted in the formation of the cationic U(iv) complexes [U{κ3-H,S,S'-H(Ph)B(timMe)2}3][X] (X = BPh4 (6-BPh4), I (6-I)), due to a ligand redistribution process. These complexes are the first examples of homoleptic poly(azolyl)borate U(iv) complexes. Treatment of complex 2 with azobenzene led to the isolation of crystals of the U(iv) compound [UI{κ3-H(Ph)B(timMe)2}2(κ2-timMe)] (7). Treatment of 2 with pyridine-N oxide (pyNO) led to the formation of the uranyl complex [UO2{κ2-S,S'-H(Ph)B(timMe)2}2] (8) and of complex 6-I, while from the reaction of [U{κ3-H(Ph)B(timMe)2}2(thf)3][BPh4] (5) with pyNO, the oxo-bridged U(iv) complex [{U{κ3-H(Ph)B(timMe)2}2(pyNO)}2(μ-O)][BPh4]2 (9) was also obtained. In the U(iii) and U(iv) complexes, the bis(azolyl)borate ligands bind to the uranium center in a κ3-H,S,S' coordination mode, while in the U(vi) complex the ligands bind to the metal in a κ2-S,S' mode. The presence of UH-B interactions in the solid-state, for the nine-coordinate complexes 1, 2, 3, 6 and 7 and for the eight-coordinate complex 9, was supported by IR spectroscopy and/or X-ray diffraction analysis.

Uranium Conversion & Enrichment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Karpius, Peter Joseph

2017-02-06

The isotopes of uranium that are found in nature, and hence in ‘fresh’ Yellowcake’, are not in relative proportions that are suitable for power or weapons applications. The goal of conversion then is to transform the U 3O 8 yellowcake into UF 6. Conversion and enrichment of uranium is usually required to obtain material with enough 235U to be usable as fuel in a reactor or weapon. The cost, size, and complexity of practical conversion and enrichment facilities aid in nonproliferation by design.

Uranium(VI) Scavenging by Amorphous Iron Phosphate Encrusting Sphaerotilus natans Filaments.

PubMed

Seder-Colomina, Marina; Morin, Guillaume; Brest, Jessica; Ona-Nguema, Georges; Gordien, Nilka; Pernelle, Jean-Jacques; Banerjee, Dipanjan; Mathon, Olivier; Esposito, Giovanni; van Hullebusch, Eric D

2015-12-15

U(VI) sorption to iron oxyhydroxides, precipitation of phosphate minerals, as well as biosorption on bacterial biomass are among the most reported processes able to scavenge U(VI) under oxidizing conditions. Although phosphates significantly influence bacterially mediated as well as iron oxyhydroxide mediated scavenging of uranium, the sorption or coprecipitation of U(VI) with poorly crystalline nanosized iron phosphates has been scarcely documented, especially in the presence of microorganisms. Here we show that dissolved U(VI) can be bound to amorphous iron phosphate during their deposition on Sphaerotilus natans filamentous bacteria. Uranium LIII-edge EXAFS analysis reveals that the adsorbed uranyl ions share an equatorial oxygen atom with a phosphate tetrahedron of the amorphous iron phosphate, with a characteristic U-P distance of 3.6 Å. In addition, the uranyl ions are connected to FeO6 octahedra with U-Fe distances at ~3.4 Å and at ~4.0 Å. The shortest U-Fe distance corresponds to a bidentate edge-sharing complex often reported for uranyl adsorption onto iron oxyhydroxides, whereas the longest U-Fe and U-P distances can be interpreted as a bidentate corner-sharing complex, in which two adjacent equatorial oxygen atoms are shared with the vertices of a FeO6 octahedron and of a phosphate tetrahedron. Furthermore, based on these sorption reactions, we demonstrate the ability of an attached S. natans biofilm to remove uranium from solution without any filtration step.

Thermodynamic and kinetic aspects of UO 2 fuel oxidation in air at 400-2000 K

NASA Astrophysics Data System (ADS)

Taylor, Peter

2005-09-01

Most nuclear fuel oxidation research has addressed either low-temperature (<700 K) air oxidation related to fuel storage or high-temperature (>1500 K) steam oxidation linked to reactor safety. This paper attempts to unify modelling for air oxidation of UO 2 fuel over a wide range of temperature, and thus to assist future improvement of the ASTEC code, co-developed by IRSN and GRS. Phenomenological correlations for different temperature ranges distinguish between oxidation on the scale of individual grains to U 3O 7 and U 3O 8 below ˜700 K and individual fragments to U 3O 8 via UO 2+ x and/or U 4O 9 above ˜1200 K. Between about 700 and 1200 K, empirical oxidation rates slowly decline as the U 3O 8 product becomes coarser-grained and more coherent, and fragment-scale processes become important. A more mechanistic approach to high-temperature oxidation addresses questions of oxygen supply, surface reaction kinetics, thermodynamic properties, and solid-state oxygen diffusion. Experimental data are scarce, however, especially at low oxygen partial pressures and high temperatures.

Laser-induced breakdown spectroscopy of light water reactor simulated used nuclear fuel: Main oxide phase

DOE PAGES

Campbell, Keri R.; Judge, Elizabeth J.; Barefield, James E.; ...

2017-04-22

We show the analysis of light water reactor simulated used nuclear fuel using laser-induced breakdown spectroscopy (LIBS) is explored using a simplified version of the main oxide phase. The main oxide phase consists of the actinides, lanthanides, and zirconium. The purpose of this study is to develop a rapid, quantitative technique for measuring zirconium in a uranium dioxide matrix without the need to dissolve the material. A second set of materials including cerium oxide is also analyzed to determine precision and limit of detection (LOD) using LIBS in a complex matrix. Two types of samples are used in this study:more » binary and ternary oxide pellets. The ternary oxide, (U,Zr,Ce)O 2 pellets used in this study are a simplified version the main oxide phase of used nuclear fuel. The binary oxides, (U,Ce)O 2 and (U,Zr)O 2 are also examined to determine spectral emission lines for Ce and Zr, potential spectral interferences with uranium and baseline LOD values for Ce and Zr in a UO 2 matrix. In the spectral range of 200 to 800 nm, 33 cerium lines and 25 zirconium lines were identified and shown to have linear correlation values (R 2) > 0.97 for both the binary and ternary oxides. The cerium LOD in the (U,Ce)O 2 matrix ranged from 0.34 to 1.08 wt% and 0.94 to 1.22 wt% in (U,Ce,Zr)O 2 for 33 of Ce emission lines. The zirconium limit of detection in the (U,Zr)O 2 matrix ranged from 0.84 to 1.15 wt% and 0.99 to 1.10 wt% in (U,Ce,Zr)O 2 for 25 Zr lines. Finally, the effect of multiple elements in the plasma and the impact on the LOD is discussed.« less

The discovery and character of Pleistocene calcrete uranium deposits in the Southern High Plains of west Texas, United States

USGS Publications Warehouse

Van Gosen, Bradley S.; Hall, Susan M.

2017-12-18

This report describes the discovery and geology of two near-surface uranium deposits within calcareous lacustrine strata of Pleistocene age in west Texas, United States. Calcrete uranium deposits have not been previously reported in the United States. The west Texas uranium deposits share characteristics with some calcrete uranium deposits in Western Australia—uranium-vanadium minerals hosted by nonpedogenic calcretes deposited in saline lacustrine environments.In the mid-1970s, Kerr-McGee Corporation conducted a regional uranium exploration program in the Southern High Plains province of the United States, which led to the discovery of two shallow uranium deposits (that were not publicly reported). With extensive drilling, Kerr-McGee delineated one deposit of about 2.1 million metric tons of ore with an average grade of 0.037 percent U3O8 and another deposit of about 0.93 million metric tons of ore averaging 0.047 percent U3O8.The west-Texas calcrete uranium-vanadium deposits occur in calcareous, fine-grained sediments interpreted to be deposited in saline lakes formed during dry interglacial periods of the Pleistocene. The lakes were associated with drainages upstream of a large Pleistocene lake. Age determinations of tephra in strata adjacent to one deposit indicate the host strata is middle Pleistocene in age.Examination of the uranium-vanadium mineralization by scanning-electron microscopy indicated at least two generations of uranium-vanadium deposition in the lacustrine strata identified as carnotite and a strontium-uranium-vanadium mineral. Preliminary uranium-series results indicate a two-component system in the host calcrete, with early lacustrine carbonate that was deposited (or recrystallized) about 190 kilo-annum, followed much later by carnotite-rich crusts and strontium-uranium-vanadium mineralization in the Holocene (about 5 kilo-annum). Differences in initial 234U/238U activity ratios indicate two separate, distinct fluid sources.

Thermodynamic and experimental study of UC powders ignition

NASA Astrophysics Data System (ADS)

Le Guyadec, F.; Rado, C.; Joffre, S.; Coullomb, S.; Chatillon, C.; Blanquet, E.

2009-09-01

Mixed plutonium and uranium carbide (UPuC) is considered as a possible fuel material for future nuclear reactors. However, UPuC is pyrophoric and fine powders of UPuC are subject to temperature increase due to oxidation with air and possible ignition during conditioning and handling. In a first approach and to allow easier experimental conditions, this study was undertaken on uranium monocarbide (UC) with the aim to determine safe handling conditions for the production and reprocessing of uranium carbide fuels. The reactivity of uranium monocarbide in oxidizing atmosphere was studied in order to analyze the ignition process. Experimental thermogravimetric analysis (TGA) and differential thermal analysis (DTA) revealed that UC powder obtained by arc melting and milling is highly reactive in air at about 200 °C. The phases formed at the various observed stages of the oxidation process were analyzed by X-ray diffraction. At the same time, ignition was analyzed thermodynamically along isothermal sections of the U-C-O ternary diagram and the pressure of the gas produced by the UC + O 2 reaction was calculated. Two possible oxidation schemes were identified on the U-C-O phase diagram and assumptions are proposed concerning the overall oxidation and ignition paths. It is particularly important to understand the mechanisms involved since temperatures as high as 2500 °C could be reached, leading to CO(g) production and possibly to a blast effect.

Utilization of non-weapons-grade plutonium and highly enriched uranium with breeding of the 233U isotope in the VVER reactors using thorium and heavy water

NASA Astrophysics Data System (ADS)

Marshalkin, V. E.; Povyshev, V. M.

2015-12-01

A method for joint utilization of non-weapons-grade plutonium and highly enriched uranium in the thorium-uranium—plutonium oxide fuel of a water-moderated reactor with a varying water composition (D2O, H2O) is proposed. The method is characterized by efficient breeding of the 233U isotope and safe reactor operation and is comparatively simple to implement.

Oxygen diffusion model of the mixed (U,Pu)O2 ± x: Assessment and application

NASA Astrophysics Data System (ADS)

Moore, Emily; Guéneau, Christine; Crocombette, Jean-Paul

2017-03-01

The uranium-plutonium (U,Pu)O2 ± x mixed oxide (MOX) is used as a nuclear fuel in some light water reactors and considered for future reactor generations. To gain insight into fuel restructuring, which occurs during the fuel lifetime as well as possible accident scenarios understanding of the thermodynamic and kinetic behavior is crucial. A comprehensive evaluation of thermo-kinetic properties is incorporated in a computational CALPHAD type model. The present DICTRA based model describes oxygen diffusion across the whole range of plutonium, uranium and oxygen compositions and temperatures by incorporating vacancy and interstitial migration pathways for oxygen. The self and chemical diffusion coefficients are assessed for the binary UO2 ± x and PuO2 - x systems and the description is extended to the ternary mixed oxide (U,Pu)O2 ± x by extrapolation. A simulation to validate the applicability of this model is considered.

Optimization of Uranium-Doped Americium Oxide Synthesis for Space Application.

PubMed

Vigier, Jean-François; Freis, Daniel; Pöml, Philipp; Prieur, Damien; Lajarge, Patrick; Gardeur, Sébastien; Guiot, Antony; Bouëxière, Daniel; Konings, Rudy J M

2018-04-16

Americium 241 is a potential alternative to plutonium 238 as an energy source for missions into deep space or to the dark side of planetary bodies. In order to use the 241 Am isotope for radioisotope thermoelectric generator or radioisotope heating unit (RHU) production, americium materials need to be developed. This study focuses on the stabilization of a cubic americium oxide phase using uranium as the dopant. After optimization of the material preparation, (Am 0.80 U 0.12 Np 0.06 Pu 0.02 )O 1.8 has been successfully synthesized to prepare a 2.96 g pellet containing 2.13 g of 241 Am for fabrication of a small scale RHU prototype. Compared to the use of pure americium oxide, the use of uranium-doped americium oxide leads to a number of improvements from a material properties and safety point of view, such as good behavior under sintering conditions or under alpha self-irradiation. The mixed oxide is a good host for neptunium (i.e., the 241 Am daughter element), and it has improved safety against radioactive material dispersion in the case of accidental conditions.

REFRACTORY ARTICLE AND PROCESS OF MANUFACTURING SAME

DOEpatents

Hamilton, N.E.

1957-12-10

A method is described for fabricating improved uranium oxide crucibles. In the past, such crucibles have lacked mechanical strength due to the poor cohesion of the uranium oxide particles. This difficulty has now been overcome by admixing with the uranium oxide a quantity of a refractory oxide binder, and dry pressing and sintering the resulting mixture into the desired shape. Suitable as binders are BeO, CaO, Al/sub 2/C/sub 3/, and ThO/sub 2/ among others.

Use of spectroscopic techniques for uranium(VI)/montmorillonite interaction modeling.

PubMed

Kowal-Fouchard, A; Drot, R; Simoni, E; Ehrhardt, J J

2004-03-01

To experimentally identify both clay sorption sites and sorption equilibria and to understand the retention mechanisms at a molecular level, we have characterized the structure of hexavalent uranium surface complexes resulting from the interaction between the uranyl ions and the surface retention groups of a montmorillonite clay. We have performed laser-induced fluorescence spectroscopy (LIFS) and X-ray photoelectron spectroscopy (XPS) on uranyl ion loaded montmorillonite. These structural results were then compared to those obtained from the study of uranyl ions sorbed onto an alumina and also from U(VI) sorbed on an amorphous silica. This experimental approach allowed for a clear determination of the reactive surface sites of montmorillonite for U(VI) sorption. The lifetime values and the U4f XPS spectra of uranium(VI) sorbed on montmorillonite have shown that this ion is sorbed on both exchange and edge sites. The comparison of U(VI)/clay and U(VI)/oxide systems has determined that the interaction between uranyl ions and montmorillonite edge sites occurs via both [triple bond]AlOH and [triple bond]SiOH surface groups and involves three distinct surface complexes. The surface complexation modeling of the U(VI)/montmorillonite sorption edges was determined using the constant capacitance model and the above experimental constraints. The following equilibria were found to account for the uranyl sorption mechanisms onto montmorillonite for metal concentrations ranged from 10(-6) to 10(-3) M and two ionic strengths (0.1 and 0.5 M): 2[triple bond]XNa + UO2(2+) <==> ([triple bond]X)2UO2 + 2Na+, log K0(exch) = 3.0; [triple bond]Al(OH)2 + UO2(2+) <==> [triple bond]Al(OH)2UO2(2+), log K0(Al) = 14.9; [triple bond]Si(OH)2 + UO2(2+) <==> [triple bond]SiO2UO2 + 2H+, log K0(Si1) = -3.8; and [triple bond]Si(OH)2 + 3UO2(2+) + 5H2O <==> [triple bond]SiO2(UO2)3(OH)5- + 7H+, log K0(Si2) = -20.0.

Utilization of non-weapons-grade plutonium and highly enriched uranium with breeding of the {sup 233}U isotope in the VVER reactors using thorium and heavy water

DOE Office of Scientific and Technical Information (OSTI.GOV)

Marshalkin, V. E., E-mail: marshalkin@vniief.ru; Povyshev, V. M.

A method for joint utilization of non-weapons-grade plutonium and highly enriched uranium in the thorium–uranium—plutonium oxide fuel of a water-moderated reactor with a varying water composition (D{sub 2}O, H{sub 2}O) is proposed. The method is characterized by efficient breeding of the {sup 233}U isotope and safe reactor operation and is comparatively simple to implement.

The short-term reduction of uranium by nanoscale zero-valent iron (nZVI): role of oxide shell, reduction mechanism and the formation of U( v )-carbonate phases

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tsarev, Sergey; Collins, Richard N.; Ilton, Eugene S.

Nanoscale zero-valent iron (nZVI) is a potential remediation agent for uranium-contaminated groundwaters, however, a complete mechanistic understanding of the processes that lead to uranium immobilization has yet to be achieved. In this study, the short-term anoxic reaction of U(VI) with fresh, (anoxic) aged and corroded nZVI particles was investigated under aqueous conditions conducive to the formation of thermodynamically stable U(VI)-Ca-CO3 ternary aqueous complexes. The first stage of the reaction between U(VI) and nZVI was assigned to sorption processes with the formation of surface U(VI)-carbonate complexes. Aged nZVI removed U(VI) faster than either fresh or corroded nZVI and it is hypothesizedmore » that U reduction initially occurs through the transfer of one electron from Fe(II) in the nZVI surface oxide layer. Evidence for reduction to U(V) was obtained through X-ray photoelectron spectroscopy and by determination of U-O bond distances of ~2.05 Å and 2.27 Å by U LIII-edge X-ray absorption spectroscopy detection of U-O bond distances at ~2.05 Å and 2.27 Å with these distances , similar to thoseat observed for the U(V) site in the mixed U(V)/U(VI) carbonate mineral wyartite. Scanning transmission electron microscopy also demonstrated that U was present as a nanoparticulate phase after one day of reaction, rather than a surface complex. Further reduction to U(IV), as observed in previous studies, would appear to be rate-limiting and coincident with the transformation of this meta-stable U-carbonate phase to uraninite (UO2).« less

Remote fabrication and irradiation test of recycled nuclear fuel prepared by the oxidation and reduction of spent oxide fuel

NASA Astrophysics Data System (ADS)

Jin Ryu, Ho; Chan Song, Kee; Il Park, Geun; Won Lee, Jung; Seung Yang, Myung

2005-02-01

A direct dry recycling process was developed in order to reuse spent pressurized light water reactor (LWR) nuclear fuel in CANDU reactors without the separation of sensitive nuclear materials such as plutonium. The benefits of the dry recycling process are the saving of uranium resources and the reduction of spent fuel accumulation as well as a higher proliferation resistance. In the process of direct dry recycling, fuel pellets separated from spent LWR fuel rods are oxidized from UO2 to U3O8 at 500 °C in an air atmosphere and reduced into UO2 at 700 °C in a hydrogen atmosphere, which is called OREOX (oxidation and reduction of oxide fuel). The pellets are pulverized during the oxidation and reduction processes due to the phase transformation between cubic UO2 and orthorhombic U3O8. Using the oxide powder prepared from the OREOX process, the compaction and sintering processes are performed in a remote manner in a shielded hot cell due to the high radioactivity of the spent fuel. Most of the fission gas and volatile fission products are removed during the OREOX and sintering processes. The mini-elements fabricated by the direct dry recycling process are irradiated in the HANARO research reactor for the performance evaluation of the recycled fuel pellets. Post-irradiation examination of the irradiated fuel showed that microstructural evolution and fission gas release behavior of the dry-recycled fuel were similar to high burnup UO2 fuel.

Synchrotron X-ray characterization of mackinawite and uraninite relevant to bio-remediation of groundwater contaminated with uranium

NASA Astrophysics Data System (ADS)

Carpenter, J.; Hyun, S.; Hayes, K. F.

2010-12-01

Uranium (U) originating from mining operations for weapon manufacturing and nuclear energy production is a significant radionuclide contaminant in groundwater local to uranium mining, uranium milling, and uranium mill tailing (UMT) storage sites. In the USA, the Department of Energy (DOE) is currently overseeing approximately 24 Uranium Mill Tailing Remediation Action (UMTRA) sites which have collectively processed over 27 million tons of uranium ore1,2. In-Situ microbial bio-reduction of the highly mobile U6+ ion into the dramatically less mobile U4+ ion has been demonstrated as an effective remedial process to inhibit uranium migration in the aqueous phase3. The resistance of this process to oxidization and possible remobilization of U when bioremediation stops (and oxidants such as oxygen from the air or nitrate in water diffuse into the formation) in the long term is not known. UMTRA site studies3 have shown that iron sulfide solids are produced by sulfate reducing bacteria (SRB) during U bioremediation, and some forms of these iron sulfide solids are known to be effective oxidant scavengers, potentially protecting against re-oxidation and thus remobilization of U. This work is investigating the role of iron sulfide solids in the long-term immobilization of reduced U compounds after bioremediation is completed in groundwater local to UMTRA sites. Re-oxidation tests are being performed in packed media columns loaded with both FeS and U solids. High quality mackinawite (FeS), and uraninite (UO2) have been synthesized in our laboratory via a wet chemistry approach. These synthetic materials are expected to mimic the naturally occurring and biogenic materials present in biologically stimulated UMTRA sites. In order to establish the initial conditions of the prepared experimental columns and to compare synthetic and biogenic FeS and UO2, these synthesized materials have been characterized with synchrotron radiation at the Stanford Synchrotron Radiation Lightsource using synchrotron x-ray powder diffraction (SXRD) and extended x-ray absorption fine structure (EXAFS). SXRD data were collected and analyzed with profile fitting to determine lattice parameters and crystallite size for comparison with published values for both biogenic and synthetic materials. This is particularly of interest for UO2, as there is very little information on particle size and lattice parameters for synthetic UO2 in the literature. Profile fitting of the SXRD data for FeS gives lattice parameters of a = b = 3.668 and a mean crystallite size of 5 to 8 nm. Both of these values are in good agreement with published values. For fresh UO2, lattice parameters were determined as a = b = c = 5.4 nm for both freshly synthesized and aged (3 months) UO2 and particle size was determined to be 3.5 nm for fresh UO2 and 5.83 nm for aged UO2. This suggests a growth mechanism for crystallites over time, and an inferred decrease in reactivity.

Breeding of 233U in the thorium-uranium fuel cycle in VVER reactors using heavy water

NASA Astrophysics Data System (ADS)

Marshalkin, V. E.; Povyshev, V. M.

2015-12-01

A method is proposed for achieving optimal neutron kinetics and efficient isotope transmutation in the 233U-232Th oxide fuel of water-moderated reactors with variable water composition (D2O, H2O) that ensures breeding of the 233U and 235U isotopes. The method is comparatively simple to implement.

Uranium-bearing breccia pipes of northwestern Arizona - an overview

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chenoweth, W.L.

During the 1950s and 1960s, the uranium deposits in breccia pipes of the Grand Canyon region were regarded as geologic curiosities. Today this area is the site of numerous exploration projects for ore-bearing pipes. The classic example of the older mines is the Orphan Lode, a patented claim within Grand Canyon National Park. Between 1956 and 1969, this deposit produced 4.26 million lb U/sub 3/O/sub 8/. Exploration since the mid-1970s has developed numerous new deposits in the Grand Canyon region. The Hack 1, 2, and 3, Pigeon, Kanab North, Canyon, and Pinenut deposits are, or will be, mined. The pipesmore » are circular and originated by dissolution of the Mississippian Redwall Limestone and collapse of the overlying strata. Uraninite ore occurs in both the pipe fill and in association with the peripheral shear zone. The principal host rocks are the Coconino Sandstone, Hermit Shale, and Esplanade Sandstone. Although small (3 to 5 million lb U/sub 3/O/sub 8/), the high grade (60 to 70% U/sub 3/O/sub 8/) of the deposits makes the pipes attractive exploration targets.« less

Selective Extraction of Uranium from Liquid or Supercritical Carbon Dioxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Farawila, Anne F.; O'Hara, Matthew J.; Wai, Chien M.

2012-07-31

Current liquid-liquid extraction processes used in recycling irradiated nuclear fuel rely on (1) strong nitric acid to dissolve uranium oxide fuel, and (2) the use of aliphatic hydrocarbons as a diluent in formulating the solvent used to extract uranium. The nitric acid dissolution process is not selective. It dissolves virtually the entire fuel meat which complicates the uranium extraction process. In addition, a solvent washing process is used to remove TBP degradation products, which adds complexity to the recycling plant and increases the overall plant footprint and cost. A liquid or supercritical carbon dioxide (l/sc -CO2) system was designed tomore » mitigate these problems. Indeed, TBP nitric acid complexes are highly soluble in l/sc -CO2 and are capable of extracting uranium directly from UO2, UO3 and U3O8 powders. This eliminates the need for total acid dissolution of the irradiated fuel. Furthermore, since CO2 is easily recycled by evaporation at room temperature and pressure, it eliminates the complex solvent washing process. In this report, we demonstrate: (1) A reprocessing scheme starting with the selective extraction of uranium from solid uranium oxides into a TBP-HNO3 loaded Sc-CO2 phase, (2) Back extraction of uranium into an aqueous phase, and (3) Conversion of recovered purified uranium into uranium oxide. The purified uranium product from step 3 can be disposed of as low level waste, or mixed with enriched uranium for use in a reactor for another fuel cycle. After an introduction on the concept and properties of supercritical fluids, we first report the characterization of the different oxides used for this project. Our extraction system and our online monitoring capability using UV-Vis absorbance spectroscopy directly in sc-CO2 is then presented. Next, the uranium extraction efficiencies and kinetics is demonstrated for different oxides and under different physical and chemical conditions: l/sc -CO2 pressure and temperature, TBP/HNO3 complex used, reductant or complexant used for selectivity, and ionic liquids used as supportive media. To complete the extraction and recovery cycle, we then demonstrate uranium back extraction from the TBP loaded sc-CO2 phase into an aqueous phase and the characterization of the uranium complex formed at the end of this process. Another aspect of this project was to limit proliferation risks by either co-extracting uranium and plutonium, or by leaving plutonium behind by selectively extracting uranium. We report that the former is easily achieved, since plutonium is in the tetravalent or hexavalent oxidation state in the oxidizing environment created by the TBP-nitric acid complex, and is therefore co-extracted. The latter is more challenging, as a reductant or complexant to plutonium has to be used to selectively extract uranium. After undertaking experiments on different reducing or complexing systems (e.g., AcetoHydroxamic Acid (AHA), Fe(II), ascorbic acid), oxalic acid was chosen as it can complex tetravalent actinides (Pu, Np, Th) in the aqueous phase while allowing the extraction of hexavalent uranium in the sc-CO2 phase. Finally, we show results using an alternative media to commonly used aqueous phases: ionic liquids. We show the dissolution of uranium in ionic liquids and its extraction using sc-CO2 with and without the presence of AHA. The possible separation of trivalent actinides from uranium is also demonstrated in ionic liquids using neodymium as a surrogate and diglycolamides as the extractant.« less

Variations of uranium concentrations in a multi-aquifer system under the impact of surface water-groundwater interaction

NASA Astrophysics Data System (ADS)

Wu, Ya; Li, Junxia; Wang, Yanxin; Xie, Xianjun

2018-04-01

Understanding uranium (U) mobility is vital to minimizing its concentrations in potential drinking water sources. In this study, we report spatial-seasonal variations in U speciation and concentrations in a multi-aquifer system under the impact of Sanggan River in Datong basin, northern China. Hydrochemical and H, O, Sr isotopic data, thermodynamic calculations, and geochemical modeling are used to investigate the mechanisms of surface water-groundwater mixing-induced mobilization and natural attenuation of U. In the study site, groundwater U concentrations are up to 30.2 μg/L, and exhibit strong spatial-seasonal variations that are related to pH and Eh values, as well as dissolved Ca2+, HCO3-, and Fe(III) concentrations. For the alkaline aquifers of this site (pH 7.02-8.44), U mobilization is due to the formation and desorption of Ca2UO2(CO3)30 and CaUO2(CO3)32- caused by groundwater Ca2+ elevation via mineral weathering and Na-Ca exchange, incorporated U(VI) release from calcite, and U(IV) oxidation by Fe(OH)3. U immobilization is linked to the adsorption of CaUO2(CO3)32- and UO2(CO3)34- shifted from Ca2UO2(CO3)30 because of HCO3- elevation and Ca2+ depletion, U(VI) co-precipitation with calcite, and U(VI) reduction by adsorbed Fe2+ and FeS. Those results are of great significance for the groundwater resource management of this and similar other surface water-groundwater interaction zones.

Effect of uranium(VI) speciation on simultaneous microbial reduction of uranium(VI) and iron(III).

PubMed

Stewart, Brandy D; Amos, Richard T; Fendorf, Scott

2011-01-01

Uranium is a pollutant of concern to both human and ecosystem health. Uranium's redox state often dictates whether it will reside in the aqueous or solid phase and thus plays an integral role in the mobility of uranium within the environment. In anaerobic environments, the more oxidized and mobile form of uranium (UO2(2+) and associated species) may be reduced, directly or indirectly, by microorganisms to U(IV) with subsequent precipitation of UO. However, various factors within soils and sediments, such as U(VI) speciation and the presence of competitive electron acceptors, may limit biological reduction of U(VI). Here we examine simultaneous dissimilatory reduction of Fe(III) and U(VI) in batch systems containing dissolved uranyl acetate and ferrihydrite-coated sand. Varying amounts of calcium were added to induce changes in aqueous U(VI) speciation. The amount of uranium removed from solution during 100 h of incubation with S. putrefaciens was 77% in absence of Ca or ferrihydrite, but only 24% (with ferrihydrite) and 14% (without ferrihydrite) were removed for systems with 0.8 mM Ca. Dissimilatory reduction of Fe(III) and U(VI) proceed through different enzyme pathways within one type of organism. We quantified the rate coefficients for simultaneous dissimilatory reduction of Fe(III) and U(VI) in systems varying in Ca concecentration (0-0.8 mM). The mathematical construct, implemented with the reactive transport code MIN3P, reveals predominant factors controlling rates and extent of uranium reduction in complex geochemical systems.

Uranium Bio-accumulation and Cycling as revealed by Uranium Isotopes in Naturally Reduced Sediments from the Upper Colorado River Basin

NASA Astrophysics Data System (ADS)

Lefebvre, Pierre; Noël, Vincent; Jemison, Noah; Weaver, Karrie; Bargar, John; Maher, Kate

2016-04-01

Uranium (U) groundwater contamination following oxidized U(VI) releases from weathering of mine tailings is a major concern at numerous sites across the Upper Colorado River Basin (CRB), USA. Uranium(IV)-bearing solids accumulated within naturally reduced zones (NRZs) characterized by elevated organic carbon and iron sulfide compounds. Subsequent re-oxidation of U(IV)solid to U(VI)aqueous then controls the release to groundwater and surface water, resulting in plume persistence and raising public health concerns. Thus, understanding the extent of uranium oxidation and reduction within NRZs is critical for assessing the persistence of the groundwater contamination. In this study, we measured solid-phase uranium isotope fractionation (δ238/235U) of sedimentary core samples from four study sites (Shiprock, NM, Grand Junction, Rifle and Naturita, CO) using a multi-collector inductively coupled plasma mass spectrometer (MC-ICP-MS). We observe a strong correlation between U accumulation and the extent of isotopic fractionation, with Δ238U up to +1.8 ‰ between uranium-enriched and low concentration zones. The enrichment in the heavy isotopes within the NRZs appears to be especially important in the vadose zone, which is subject to variations in water table depth. According to previous studies, this isotopic signature is consistent with biotic reduction processes associated with metal-reducing bacteria. Positive correlations between the amount of iron sulfides and the accumulation of reduced uranium underline the importance of sulfate-reducing conditions for U(IV) retention. Furthermore, the positive fractionation associated with U reduction observed across all sites despite some variations in magnitude due to site characteristics, shows a regional trend across the Colorado River Basin. The maximum extent of 238U enrichment observed in the NRZ proximal to the water table further suggests that the redox cycling of uranium, with net release of U(VI) to the groundwater by non-fractionating oxidation, is occurring within this zone. Thus, release of uranium from the NRZs may play a critical role in the persistence of groundwater contamination at these sites.

Hydrothermal synthesis of (C6N2H14)2(UVI2UIVO4F12), a mixed-valent one-dimensional uranium oxyfluoride.

PubMed

Allen, S; Barlow, S; Halasyamani, P S; Mosselmans, J F; O'Hare, D; Walker, S M; Walton, R I

2000-08-21

A new hybrid organic-inorganic mixed-valent uranium oxyfluoride, (C6N2H14)2(U3O4F12), UFO-17, has been synthesized under hydrothermal conditions using uranium dioxide as the uranium source, hydrofluoric acid as mineralizer, and 1,4-diazabicyclo[2.2.2]octane as template. The single-crystal X-ray structure was determined. Crystals of UFO-17 belonged to the orthorhombic space group Cmcm (no. 63), with a = 14.2660(15) A, b = 24.5130(10) A, c = 7.201(2) A, and Z = 4. The structure reveals parallel uranium-containing chains of two types: one type is composed of edge-sharing UO2F5 units; the other has a backbone of edge-sharing UF8 units, each sharing an edge with a pendant UO2F5 unit. Bond-valence calculations suggest the UF8 groups contain UIV, while the UO2F5 groups contain UVI. EXAFS data give results consistent with the single-crystal X-ray structure determination, while comparison of the uranium LIII-edge XANES of UFO-17 with that of related UIV and UVI compounds supports the oxidation-state assignment. Variable-temperature magnetic susceptibility measurements on UFO-17 and a range of related hybrid organic-inorganic uranium(IV) and uranium(VI) fluorides and oxyfluorides further support the formulation of UFO-17 as a mixed-valent UIV/UVI compound.

Uranium chloride extraction of transuranium elements from LWR fuel

DOEpatents

Miller, W.E.; Ackerman, J.P.; Battles, J.E.; Johnson, T.R.; Pierce, R.D.

1992-08-25

A process of separating transuranium actinide values from uranium values present in spent nuclear oxide fuels containing rare earth and noble metal fission products as well as other fission products is disclosed. The oxide fuel is reduced with Ca metal in the presence of Ca chloride and a U-Fe alloy which is liquid at about 800 C to dissolve uranium metal and the noble metal fission product metals and transuranium actinide metals and rare earth fission product metals leaving Ca chloride having CaO and fission products of alkali metals and the alkali earth metals and iodine dissolved therein. The Ca chloride and CaO and the fission products contained therein are separated from the U-Fe alloy and the metal values dissolved therein. The U-Fe alloy having dissolved therein reduced metals from the spent nuclear fuel is contacted with a mixture of one or more alkali metal or alkaline earth metal halides selected from the class consisting of alkali metal or alkaline earth metal and Fe or U halide or a combination thereof to transfer transuranium actinide metals and rare earth metals to the halide salt leaving the uranium and some noble metal fission products in the U-Fe alloy and thereafter separating the halide salt and the transuranium metals dissolved therein from the U-Fe alloy and the metals dissolved therein. 1 figure.

Uranium chloride extraction of transuranium elements from LWR fuel

DOEpatents

Miller, William E.; Ackerman, John P.; Battles, James E.; Johnson, Terry R.; Pierce, R. Dean

1992-01-01

A process of separating transuranium actinide values from uranium values present in spent nuclear oxide fuels containing rare earth and noble metal fission products as well as other fission products is disclosed. The oxide fuel is reduced with Ca metal in the presence of Ca chloride and a U-Fe alloy which is liquid at about 800.degree. C. to dissolve uranium metal and the noble metal fission product metals and transuranium actinide metals and rare earth fission product metals leaving Ca chloride having CaO and fission products of alkali metals and the alkali earth metals and iodine dissolved therein. The Ca chloride and CaO and the fission products contained therein are separated from the U-Fe alloy and the metal values dissolved therein. The U-Fe alloy having dissolved therein reduced metals from the spent nuclear fuel is contacted with a mixture of one or more alkali metal or alkaline earth metal halides selected from the class consisting of alkali metal or alkaline earth metal and Fe or U halide or a combination thereof to transfer transuranium actinide metals and rare earth metals to the halide salt leaving the uranium and some noble metal fission products in the U-Fe alloy and thereafter separating the halide salt and the transuranium metals dissolved therein from the U-Fe alloy and the metals dissolved therein.

Phase separation of metal-added corium and its effect on a steam explosion

NASA Astrophysics Data System (ADS)

Min, B. T.; Kim, J. H.; Hong, S. W.; Hong, S. H.; Park, I. K.; Song, J. H.; Kim, H. D.

2008-07-01

To simulate a relocation of molten core material and its interaction phenomenon with water during a severe accident in a nuclear reactor, a typical corium of UO 2/ZrO 2/Zr/Stainless steel mixed at a 62 wt%, 15 wt%, 12 wt% and 11 wt%, respectively, was melted and then cooled down to become a solidified ingot. It was shown that the molten corium was separated into two layers, of which the upper layer was oxide mixtures and the lower layer was metal alloys. The upper layer was UO 2 and ZrO 2 and the lower layer mostly consisted of metal mixtures such as uranium, zirconium and stainless steel. Iron content varied with the positions and about a half of it existed as an alloy such as Fe 2U. Uranium metal was produced by reduction of UO 2 by zirconium metal. The average densities of the upper oxide layer and the lower metal layer were 8.802 and 9.411 g/cm 3, respectively. In another test, metal-added molten corium was poured into water and it showed that a steam explosion could occur by applying an external trigger.

Effects of calcium and phosphate on uranium(IV) oxidation: Comparison between nanoparticulate uraninite and amorphous UIV-phosphate

NASA Astrophysics Data System (ADS)

Latta, Drew E.; Kemner, Kenneth M.; Mishra, Bhoopesh; Boyanov, Maxim I.

2016-02-01

The mobility of uranium in subsurface environments depends strongly on its redox state, with UIV phases being significantly less soluble than UVI minerals. This study compares the oxidation kinetics and mechanisms of two potential products of UVI reduction in natural systems, a nanoparticulate UO2 phase and an amorphous UIV-Ca-PO4 analog to ningyoite (CaUIV(PO4)2·1-2H2O). The valence of U was tracked by X-ray absorption near-edge spectroscopy (XANES), showing similar oxidation rate constants for UIVO2 and UIV-phosphate in solutions equilibrated with atmospheric O2 and CO2 at pH 7.0 (kobs,UO2 = 0.17 ± 0.075 h-1 vs. kobs,UIVPO4 = 0.30 ± 0.25 h-1). Addition of up to 400 μM Ca and PO4 decreased the oxidation rate constant by an order of magnitude for both UO2 and UIV-phosphate. The intermediates and products of oxidation were tracked by electron microscopy, powder X-ray diffraction (pXRD), and extended X-ray absorption fine-structure spectroscopy (EXAFS). In the absence of Ca or PO4, the product of UO2 oxidation is Na-uranyl oxyhydroxide (under environmentally relevant concentrations of sodium, 15 mM NaClO4 and low carbonate concentration), resulting in low concentrations of dissolved UVI (<2.5 × 10-7 M). Oxidation of UIV-phosphate produced a Na-autunite phase (Na2(UO2)PO4·xH2O), resulting in similarly low dissolved U concentrations (<7.3 × 10-8 M). When Ca and PO4 are present in the solution, the EXAFS data and the solubility of the UVI phase resulting from oxidation of UO2 and UIV-phosphate are consistent with the precipitation of Na-autunite. Bicarbonate extractions and Ca K-edge X-ray absorption spectroscopy of oxidized solids indicate the formation of a Ca-UVI-PO4 layer on the UO2 surface and suggest a passivation layer mechanism for the decreased rate of UO2 oxidation in the presence of Ca and PO4. Interestingly, the extractions were unable to remove all of the oxidized U from partially oxidized UO2 solids, suggesting that oxidized U is distributed between the interior of the UO2 nanoparticles and the labile surface layer. Accounting for the entire pool of oxidized U by XANES is the likely reason for the higher UO2 oxidation rate constants determined here relative to prior studies. Our results suggest that the natural presence or addition of Ca and PO4 in groundwater could slow the rates of UIV oxidation, but that the rates are still fast enough to cause complete oxidation of UIV within days under fully oxygenated conditions.

Rapid removal of uranium from aqueous solutions using magnetic Fe3O4@SiO2 composite particles.

PubMed

Fan, Fang-Li; Qin, Zhi; Bai, Jing; Rong, Wei-Dong; Fan, Fu-You; Tian, Wei; Wu, Xiao-Lei; Wang, Yang; Zhao, Liang

2012-04-01

Rapid removal of U(VI) from aqueous solutions was investigated using magnetic Fe(3)O(4)@SiO(2) composite particles as the novel adsorbent. Batch experiments were conducted to study the effects of initial pH, amount of adsorbent, shaking time and initial U(VI) concentrations on uranium sorption efficiency as well as the desorbing of U(VI). The sorption of uranium on Fe(3)O(4)@SiO(2) composite particles was pH-dependent, and the optimal pH was 6.0. In kinetics studies, the sorption equilibrium can be reached within 180 min, and the experimental data were well fitted by the pseudo-second-order model, and the equilibrium sorption capacities calculated by the model were almost the same as those determined by experiments. The Langmuir sorption isotherm model correlates well with the uranium sorption equilibrium data for the concentration range of 20-200 mg/L. The maximum uranium sorption capacity onto magnetic Fe(3)O(4)@SiO(2) composite particles was estimated to be about 52 mg/g at 25 °C. The highest values of uranium desorption (98%) was achieved using 0.01 M HCl as the desorbing agent. Fe(3)O(4)@SiO(2) composite particles showed a good selectivity for uranium from aqueous solution with other interfering cation ions. Present study suggested that magnetic Fe(3)O(4)@SiO(2) composite particles can be used as a potential adsorbent for sorption uranium and also provided a simple, fast separation method for removal of heavy metal ion from aqueous solution. Copyright © 2011 Elsevier Ltd. All rights reserved.

Structural evolution of the double perovskites Sr{sub 2}B'UO{sub 6} (B' = Mn, Fe, Co, Ni, Zn) upon reduction: Magnetic behavior of the uranium cations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pinacca, R.M., E-mail: rmp@unsl.edu.ar; Viola, M.C.; Pedregosa, J.C.

2011-11-15

Highlights: {yields} Evolution of the double perovskites Sr{sub 2}B'UO{sub 6} upon reduction were studied by XRPD. {yields} Orthorhombic (Pnma) disordered perovskites SrB'{sub 0.5-x}U{sub 0.5+x}O{sub 3} were obtained at 900 {sup o}C. {yields} U{sup 5+/4+} and Zn{sup 2+} cations are distributed at random over the octahedral positions. {yields} AFM ordering for the perovskite with B' = Zn appears below 30 K. -- Abstract: We describe the preparation of five perovskite oxides obtained upon reduction of Sr{sub 2}B'UO{sub 6} (B' = Mn, Fe, Co, Ni, Zn) with H{sub 2}/N{sub 2} (5%/95%) at 900 {sup o}C during 8 h, and their structural characterizationmore » by X-ray powder diffraction (XRPD). During the reduction process there is a partial segregation of the elemental metal when B' = Co, Ni, Fe, and the corresponding B'O oxide when B' = Mn, Zn. Whereas the parent, oxygen stoichiometric double perovskites Sr{sub 2}B'UO{sub 6} are long-range ordered concerning B' and U cations. The crystal structures of the reduced phases, SrB'{sub 0.5-x}U{sub 0.5+x}O{sub 3} with 0.37 < x < 0.27, correspond to simple, disordered perovskites; they are orthorhombic, space group Pnma (No. 62), with a full cationic disorder at the B site. Magnetic measurements performed on the phase with B' = Zn, indicate uncompensated antiferromagnetic ordering of the U{sup 5+}/U{sup 4+} sublattice below 30 K.« less

Volcanogenic Uranium Deposits: Geology, Geochemical Processes, and Criteria for Resource Assessment

USGS Publications Warehouse

Nash, J. Thomas

2010-01-01

Felsic volcanic rocks have long been considered a primary source of uranium for many kinds of uranium deposits, but volcanogenic uranium deposits themselves have generally not been important resources. Until the past few years, resource summaries for the United States or the world generally include volcanogenic in the broad category of 'other deposits' because they comprised less than 0.5 percent of past production or estimated resources. Exploration in the United States from the 1940s through 1982 discovered hundreds of prospects in volcanic rocks, of which fewer than 20 had some recorded production. Intensive exploration in the late 1970s found some large deposits, but low grades (less than about 0.10 percent U3O8) discouraged economic development. A few deposits in the world, drilled in the 1980s and 1990s, are now known to contain large resources (>20,000 tonnes U3O8). However, research on ore-forming processes and exploration for volcanogenic deposits has lagged behind other kinds of uranium deposits and has not utilized advances in understanding of geology, geochemistry, and paleohydrology of ore deposits in general and epithermal deposits in particular. This review outlines new ways to explore and assess for volcanogenic deposits, using new concepts of convection, fluid mixing, and high heat flow to mobilize uranium from volcanic source rocks and form deposits that are postulated to be large. Much can also be learned from studies of epithermal metal deposits, such as the important roles of extensional tectonics, bimodal volcanism, and fracture-flow systems related to resurgent calderas. Regional resource assessment is helped by genetic concepts, but hampered by limited information on frontier areas and undiscovered districts. Diagnostic data used to define ore deposit genesis, such as stable isotopic data, are rarely available for frontier areas. A volcanic environment classification, with three classes (proximal, distal, and pre-volcanic structures), permits use of geologic features on 1:500,000 to 1:100,000 scale maps. Geochemical databases for volcanic rocks are postulated to be more effective than databases for stream sediments or surface radioactivity, both of which tend to be inconsistent because of variable leaching of uranium from soils. Based on empirical associations, spatial associations with areas of wet paleoclimate, adjacent oil and gas fields, or evaporite beds are deemed positive. Most difficult to estimate is the location of depositional traps and reduction zones, in part because they are mere points at regional scale. Grade and tonnage data are reviewed and discussed for 32 deposits in the world. Experience of mining engineers and geologists in Asia suggests that tonnages could be higher than presently known in the Western Hemisphere. Geological analysis, and new data from Asia, suggest a typical or median deposit tonnage of about 5,000 tonnes U3O8, and an optimistic forecast of discoveries in the range of 5,000 to 20,000 tonnes U3O8. The likely grade of undiscovered deposits could be about 0.15 percent U3O8 , based on both western and eastern examples. Volcanic terrane is under-explored, relative to other kinds of uranium deposits, and is considered a favorable frontier area for new discoveries.

The effect of hydrogen peroxide on uranium oxide films on 316L stainless steel

NASA Astrophysics Data System (ADS)

Wilbraham, Richard J.; Boxall, Colin; Goddard, David T.; Taylor, Robin J.; Woodbury, Simon E.

2015-09-01

For the first time the effect of hydrogen peroxide on the dissolution of electrodeposited uranium oxide films on 316L stainless steel planchets (acting as simulant uranium-contaminated metal surfaces) has been studied. Analysis of the H2O2-mediated film dissolution processes via open circuit potentiometry, alpha counting and SEM/EDX imaging has shown that in near-neutral solutions of pH 6.1 and at [H2O2] ⩽ 100 μmol dm-3 the electrodeposited uranium oxide layer is freely dissolving, the associated rate of film dissolution being significantly increased over leaching of similar films in pH 6.1 peroxide-free water. At H2O2 concentrations between 1 mmol dm-3 and 0.1 mol dm-3, formation of an insoluble studtite product layer occurs at the surface of the uranium oxide film. In analogy to corrosion processes on common metal substrates such as steel, the studtite layer effectively passivates the underlying uranium oxide layer against subsequent dissolution. Finally, at [H2O2] > 0.1 mol dm-3 the uranium oxide film, again in analogy to common corrosion processes, behaves as if in a transpassive state and begins to dissolve. This transition from passive to transpassive behaviour in the effect of peroxide concentration on UO2 films has not hitherto been observed or explored, either in terms of corrosion processes or otherwise. Through consideration of thermodynamic solubility product and complex formation constant data, we attribute the transition to the formation of soluble uranyl-peroxide complexes under mildly alkaline, high [H2O2] conditions - a conclusion that has implications for the design of both acid minimal, metal ion oxidant-free decontamination strategies with low secondary waste arisings, and single step processes for spent nuclear fuel dissolution such as the Carbonate-based Oxidative Leaching (COL) process.

Volumetric determination of uranium using titanous sulfate as reductant before oxidimetric titration

USGS Publications Warehouse

Wahlberg, James S.; Skinner, Dwight L.; Rader, Lewis F.

1956-01-01

A new method for determining uranium in samples containing 0.05 percent or more U3O8, using titanous sulfate as reducing agent, is much shorter, faster, and has fewer interferences than conventional methods using reductor columns. The sample is dissolved with sulfuric, nitric, perchloric, and hydrofluoric acids. Elements that would otherwise form insoluble fluorides are kept in solution by complexing the fluoride ion with boric acid. A precipitation is made with cupferron to remove interfering elements. The solution is filtered to remove the precipitated cupferrates instead of extracting them with chloroform as is usually done. Filtration is preferred to extraction because any niobium that may be in solution forms an insoluble cupferrate that may be removed by filtering but is very difficult to extract with chloroform. Excess cupferron is destroyed by oxidizing with nitric and perchloric acids, and evaporating to dense fumes of sulfuric acid. The uranium is reduced to U(IV) by the addition of titanous sulfate, with cupric sulfate used as an indicator of the completeness of the reduction. Metallic copper is formed when all the uranium is reduced. The reduced copper is then reoxidized by the addition of mercuric perchlorate, an excess of ferric sulfate added, and the solution titrated immediately with standard ceric sulfate with ferroin as an indicator. Precision of the method compared favorable with methods in common use, both for uranium ores and for most types of uranium-rich materials.

Magnesium transport extraction of transuranium elements from LWR fuel

DOEpatents

Ackerman, John P.; Battles, James E.; Johnson, Terry R.; Miller, William E.; Pierce, R. Dean

1992-01-01

A process of separating transuranium actinide values from uranium values present in spent nuclear oxide fuels which contain rare earth and noble metal fission products. The oxide fuel is reduced with Ca metal in the presence of CaCl.sub.2 and a U-Fe alloy containing not less than about 84% by weight uranium at a temperature in the range of from about 800.degree. C. to about 850.degree. C. to produce additional uranium metal which dissolves in the U-Fe alloy raising the uranium concentration and having transuranium actinide metals and rare earth fission product metals and the noble metal fission products dissolved therein. The CaCl.sub.2 having CaO and fission products of alkali metals and the alkali earth metals and iodine dissolved therein is separated and electrolytically treated with a carbon electrode to reduce the CaO to Ca metal while converting the carbon electrode to CO and CO.sub.2. The Ca metal and CaCl.sub.2 is recycled to reduce additional oxide fuel. The U-Fe alloy having transuranium actinide metals and rare earth fission product metals and the noble metal fission products dissolved therein is contacted with Mg metal which takes up the actinide and rare earth fission product metals. The U-Fe alloy retains the noble metal fission products and is stored while the Mg is distilled and recycled leaving the transuranium actinide and rare earth fission products isolated.

Solid state reactions of CeO 2, PuO 2, (U,Ce)O 2 and (U,Pu)O 2 with K 2S 2O 8

NASA Astrophysics Data System (ADS)

Keskar, Meera; Kasar, U. M.; Mudher, K. D. Singh; Venugopal, V.

2004-09-01

Solid state reactions of CeO 2, PuO 2 and mixed oxides (U,Ce)O 2 and (U,Pu)O 2 containing different mol.% of Ce and Pu, were carried out with K 2S 2O 8 at different temperatures to identify the formation of various products and to investigate their dissolution behaviour. X-ray, chemical and thermal analysis methods were used to characterise the products formed at various temperatures. The products obtained by heating two moles of K 2S 2O 8 with one mole each of CeO 2, PuO 2, (U,Ce)O 2 and (U,Pu)O 2 at 400 °C were identified as K 4Ce(SO 4) 4, K 4Pu(SO 4) 4, K 4(U,Ce)(SO 4) 4 and K 4(U,Pu)(SO 4) 4, respectively. K 4Ce(SO 4) 4 further decomposed to form K 4Ce(SO 4) 3.5 at 600 °C and mixture of K 2SO 4 and CeO 2 at 950 °C. Thus the products formed during the reaction of 2K 2S 2O 8 + CeO 2 show that cerium undergoes changes in oxidation state from +4 to +3 and again to +4. XRD data of K 4Ce(SO 4) 4 and K 4Ce(SO 4) 3.5 were indexed on triclinic and monoclinic system, respectively. PuO 2 + 2K 2S 2O 8 reacts at 400 °C to form K 4Pu(SO 4) 4 which was stable upto 750 °C and further decomposes to form K 2SO 4 + PuO 2 at 1000 °C. The products formed at 400 °C during the reactions of the oxides and mixed oxides were found to be readily soluble in 1-2 M HNO 3.

Single crystal structures and theoretical calculations of uranium endohedral metallofullerenes (U@C2n , 2n = 74, 82) show cage isomer dependent oxidation states for U.

PubMed

Cai, Wenting; Morales-Martínez, Roser; Zhang, Xingxing; Najera, Daniel; Romero, Elkin L; Metta-Magaña, Alejandro; Rodríguez-Fortea, Antonio; Fortier, Skye; Chen, Ning; Poblet, Josep M; Echegoyen, Luis

2017-08-01

Charge transfer is a general phenomenon observed for all endohedral mono-metallofullerenes. Since the detection of the first endohedral metallofullerene (EMF), La@C 82 , in 1991, it has always been observed that the oxidation state of a given encapsulated metal is always the same, regardless of the cage size. No crystallographic data exist for any early actinide endohedrals and little is known about the oxidation states for the few compounds that have been reported. Here we report the X-ray structures of three uranium metallofullerenes, U@ D 3h -C 74 , U@ C 2 (5)-C 82 and U@ C 2v (9)-C 82 , and provide theoretical evidence for cage isomer dependent charge transfer states for U. Results from DFT calculations show that U@ D 3h -C 74 and U@ C 2 (5)-C 82 have tetravalent electronic configurations corresponding to U 4+ @ D 3h -C 74 4- and U 4+ @ C 2 (5)-C 82 4- . Surprisingly, the isomeric U@ C 2v (9)-C 82 has a trivalent electronic configuration corresponding to U 3+ @ C 2v (9)-C 82 3- . These are the first X-ray crystallographic structures of uranium EMFs and this is first observation of metal oxidation state dependence on carbon cage isomerism for mono-EMFs.

Preparation of UO2, ThO2 and (Th,U)O2 pellets from photochemically-prepared nano-powders

NASA Astrophysics Data System (ADS)

Pavelková, Tereza; Čuba, Václav; de Visser-Týnová, Eva; Ekberg, Christian; Persson, Ingmar

2016-02-01

Photochemically-induced preparation of nano-powders of crystalline uranium and/or thorium oxides and their subsequent pelletizing has been investigated. The preparative method was based on the photochemically induced formation of amorphous solid precursors in aqueous solution containing uranyl and/or thorium nitrate and ammonium formate. The EXAFS analyses of the precursors shown that photon irradiation of thorium containing solutions yields a compound with little long-range order but likely "ThO2 like" and the irradiation of uranium containing solutions yields the mixture of U(IV) and U(VI) compounds. The U-containing precursors were carbon free, thus allowing direct heat treatment in reducing atmosphere without pre-treatment in the air. Subsequent heat treatment of amorphous solid precursors at 300-550 °C yielded nano-crystalline UO2, ThO2 or solid (Th,U)O2 solutions with high purity, well-developed crystals with linear crystallite size <15 nm. The prepared nano-powders of crystalline oxides were pelletized without any binder (pressure 500 MPa), the green pellets were subsequently sintered at 1300 °C under an Ar:H2 (20:1) mixture (UO2 and (Th,U)O2 pellets) or at 1600 °C in ambient air (ThO2 pellets). The theoretical density of the sintered pellets varied from 91 to 97%.

Field Testing of Downgradient Uranium Mobility at an In-Situ Recovery Uranium Mine

NASA Astrophysics Data System (ADS)

Reimus, P. W.; Clay, J. T.; Rearick, M.; Perkins, G.; Brown, S. T.; Basu, A.; Chamberlain, K.

2015-12-01

In-situ recovery (ISR) mining of uranium involves the injection of O2 and CO2 (or NaHCO3) into saturated roll-front deposits to oxidize and solubilize the uranium, which is then removed by ion exchange at the surface and processed into U3O8. While ISR is economical and environmentally-friendly relative to conventional mining, one of the challenges of extracting uranium by this process is that it leaves behind a geochemically-altered aquifer that is exceedingly difficult to restore to pre-mining geochemical conditions, a regulatory objective. In this research, we evaluated the ability of the aquifer downgradient of an ISR mining area to attenuate the transport of uranium and other problem constituents that are mobilized by the mining process. Such an evaluation can help inform both regulators and the mining industry as to how much restoration of the mined ore zone is necessary to achieve regulatory compliance at various distances downgradient of the mining zone even if complete restoration of the ore zone proves to be difficult or impossible. Three single-well push-pull tests and one cross-well test were conducted in which water from an unrestored, previously-mined ore zone was injected into an unmined ore zone that served as a geochemical proxy for the downgradient aquifer. In all tests, non-reactive tracers were injected with the previously-mined ore zone water to allow the transport of uranium and other constituents to be compared to that of the nonreactive species. In the single-well tests, it was shown that the recovery of uranium relative to the nonreactive tracers ranged from 12-25%, suggesting significant attenuation capacity of the aquifer. In the cross-well test, selenate, molybdate and metavanadate were injected with the unrestored water to provide information on the transport of these potentially-problematic anionic constituents. In addition to the species-specific transport information, this test provided valuable constraints on redox conditions within the system, as redox couples involving these species collectively bracket the predicted transition redox potential for the U(VI)/U(IV) couple. Reduction should provide much longer-lasting immobilization of constituents than adsorption, especially given the inherent reducing characteristics of roll-front systems.

Theoretical investigations of geometry, electronic structure and stability of UO(6): octahedral uranium hexoxide and its isomers.

PubMed

Xiao, Hai; Hu, Han-Shi; Schwarz, W H Eugen; Li, Jun

2010-08-26

The existence of a novel octahedral UO(6) complex had been suggested by Pyykko et al. [Pyykko, P.; Runeberg, N.; Straka, M.; Dyall, K. G. Chem. Phys. Lett. 2000, 328, 415]. We have now investigated the stability, the geometric and electronic structures, and the vibrations of various UO(6) molecules, using spin-orbit density functional and scalar-relativistic coupled-cluster approaches. We find four different (meta-)stable species, namely (3)D(2h)-UO(2)(eta(2)-O(2)(*))(2) at lowest energy, (3)C(2v)-UO(4)(*)(eta(2)-O(2)(*)) and (1)D(3)-U(eta(2)-O(2))(3) at medium energies, and (1)O(h)-UO(6) at highest energy. The decay of O(h)-UO(6) occurs via an activated spin-flip mechanism. The UO(6) species correspond to local minima on singlet and triplet energy surfaces and might be trapped in noble gas matrices. Experimentally, the four species might be identified through their vibrational spectra. Uranium is best described as coordinated by oxygen atoms in various oxidation states as oxo O(2-), oxido(1) O(*-), peroxido O(2)(2-), and superoxido O(2)(*-) ligands. The occurrence of monovalent oxygen is remarkable. The resulting characterization of the central ion as U(VI) in all four cases does not fully reflect the electronic differences, nor the "valence-activity" of the U-6p(6) semicore shell.

Depleted uranium dust from fired munitions: physical, chemical and biological properties.

PubMed

Mitchel, R E J; Sunder, S

2004-07-01

This paper reports physical, chemical and biological analyses of samples of dust resulting from munitions containing depleted uranium (DU) that had been live-fired and had impacted an armored target. Mass spectroscopic analysis indicated that the average atom% of U was 0.198 +/- 0.10, consistent with depleted uranium. Other major elements present were iron, aluminum, and silicon. About 47% of the total mass was particles with diameters <300 microm, of which about 14% was <10 microm. X-ray diffraction analysis indicated that the uranium was present in the sample as uranium oxides-mainly U3O7 (47%), U3O8 (44%) and UO2 (9%). Depleted uranium dust, instilled into the lungs or implanted into the muscle of rats, contained a rapidly soluble uranium component and a more slowly soluble uranium component. The fraction that underwent dissolution in 7 d declined exponentially with increasing initial burden. At the lower lung burdens tested (<15 microg DU dust/lung) about 14% of the uranium appeared in urine within 7 d. At the higher lung burdens tested (~80-200 microg DU dust/lung) about 5% of the DU appeared in urine within 7 d. In both cases about 50% of that total appeared in urine within the first day. DU implanted in muscle similarly showed that about half of the total excreted within 7 d appeared in the first day. At the lower muscle burdens tested (<15 microg DU dust/injection site) about 9% was solubilized within 7 d. At muscle burdens >35 microg DU dust/injection site about 2% appeared in urine within 7 d. Natural uranium (NU) ore dust was instilled into rat lungs for comparison. The fraction dissolving in lung showed a pattern of exponential decline with increasing initial burden similar to DU. However, the decline was less steep, with about 14% appearing in urine for lung burdens up to about 200 microg NU dust/lung and 5% at lung burdens >1,100 microg NU dust/lung. NU also showed both a fast and a more slowly dissolving component. At the higher lung burdens of both DU and NU that showed lowered urine excretion rates, histological evidence of kidney damage was seen. Kidney damage was not seen with the muscle burdens tested. DU dust produced kidney damage at lower lung burdens and lower urine uranium levels than NU dust, suggesting that other toxic metals in DU dust may contribute to the damage.

Effects of organic carbon supply rates on uranium mobility in a previously bioreduced contaminated sediment.

PubMed

Wan, Jiamin; Tokunaga, Tetsu K; Kim, Yongman; Brodie, Eoin; Daly, Rebecca; Hazen, Terry C; Firestone, Mary K

2008-10-15

Bioreduction-based strategies for remediating uranium (U)-contaminated sediments face the challenge of maintaining the reduced status of U for long times. Because groundwater influxes continuously bring in oxidizing terminal electron acceptors (O2, NO3(-)), it is necessary to continue supplying organic carbon (OC) to maintain the reducing environment after U bioreduction is achieved. We tested the influence of OC supply rates on mobility of previously microbial reduced uranium U(IV) in contaminated sediments. We found that high degrees of U mobilization occurred when OC supply rates were high, and when the sediment still contained abundant Fe(III). Although 900 days with low levels of OC supply minimized U mobilization, the sediment redox potential increased with time as did extractable U(VI) fractions. Molecular analyses of total microbial activity demonstrated a positive correlation with OC supply and analyses of Geobacteraceae activity (RT-qPCR of 16S rRNA) indicated continued activity even when the effluent Fe(II) became undetectable. These data support our hypothesis on the mechanisms responsible for remobilization of U under reducing conditions; that microbial respiration caused increased (bi)carbonate concentration and formation of stable uranyl carbonate complexes, thereby shifted U(IV)/U(VI) equilibrium to more reducing potentials. The data also suggested that low OC concentrations could not sustain the reducing condition of the sediment for much longer time. Bioreduced U(IV) is not sustainable in an oxidizing environment for a very long time.

Kinetics of triscarbonato uranyl reduction by aqueous ferrous iron: a theoretical study.

PubMed

Wander, Matthew C F; Kerisit, Sebastien; Rosso, Kevin M; Schoonen, Martin A A

2006-08-10

Uranium is a pollutant whose mobility is strongly dependent on its oxidation state. While U(VI) in the form of the uranyl cation is readily reduced by a range of natural reductants, by contrast complexation of uranyl by carbonate greatly reduces its reduction potential and imposes increased electron transfer (ET) distances. Very little is known about the elementary processes involved in uranium reduction from U(VI) to U(V) to U(IV) in general. In this study, we examine the theoretical kinetics of ET from ferrous iron to triscarbonato uranyl in aqueous solution. A combination of molecular dynamics (MD) simulations and density functional theory (DFT) electronic structure calculations is employed to compute the parameters that enter into Marcus' ET model, including the thermodynamic driving forces, reorganization energies, and electronic coupling matrix elements. MD simulations predict that two ferrous iron atoms will bind in an inner-sphere fashion to the three-membered carbonate ring of triscarbonato uranyl, forming the charge-neutral ternary Fe(2)UO(2)(CO(3))(3)(H(2)O)(8) complex. Through a sequential proton-coupled electron-transfer mechanism (PCET), the first ET step converting U(VI) to U(V) is predicted by DFT to occur with an electronic barrier that corresponds to a rate on the order of approximately 1 s(-1). The second ET step converting U(V) to U(IV) is predicted to be significantly endergonic. Therefore, U(V) is a stabilized end product in this ET system, in agreement with experiment.

The chemical state of defective uranium-plutonium oxide fuel pins irradiated in sodium cooled reactors

NASA Astrophysics Data System (ADS)

Kleykamp, H.

1997-09-01

Steady-state irradiation experiments were conducted in the sodium loop of the Siloe reactor on artificially failed mixed oxide pins that had been pre-irradiated in fast reactors up to 11.5% burnup. The formation of the predominant reaction product Na 3(U,Pu)O 4 starts on the fuel surface and is terminated when a lower O/(U + Pu) threshold of the fuel is attained. The axial extent of the reaction product depends on the size of the initial cladding defect. The occurrence of secondary cracks is possible. Na(U,Pu)O 3 forms at higher fuel temperatures. The existence of Na 3U 1- xPu xO 4 is shown in pre-irradiated blanket pins after artificial defect formation. Caesium in the oxocompounds is reduced to the metallic state and is dissolved in the coolant. Evidence of a very low chemical potential of oxygen in defective fuel pins is sustained by the occurrence of actinide-platinum metal phases formed by coupled reduction of hypostoichiometric fuel with ɛ-(Mo,Tc,Ru,Rh,Pd) precipitates. Continued operation of defective pins is not hazardous by easy precautions.

Using 238U/235U ratios to understand the formation and oxidation of reduced uranium solids in naturally reduced zones

NASA Astrophysics Data System (ADS)

Jemison, N.; Johnson, T. M.; Druhan, J. L.; Davis, J. A.

2016-12-01

Uranium occurs in groundwater primarily as soluble and mobile U(VI), which can be reduced to immobile U(IV), often observed in sediments as uraninite. Numerous U(VI)-contaminated sites, such as the DOE field site in Rifle, CO, contain naturally reduced zones (NRZ's) that have relatively high concentrations of organic matter. Reduction of heavy metals occurs within NRZ's, producing elevated concentrations of iron sulfides and U(IV). Slow, natural oxidation of U(IV) from NRZ's may prolong U(VI) contamination of groundwater. The reduction of U(VI) produces U(IV) with a higher 238U/235U ratio. Samples from two NRZ sediment cores recovered from the Rifle site revealed that the outer fringes of the NRZ contain U(IV) with a high 238U/235U ratio, while lower values are observed in the center . We suggest that as aqueous U(VI) was reduced in the NRZ, it was driven to lower 238U/235U values, such that U(IV) formed in the core of the NRZ reflects a lower 238U/235U. Two oxidation experiments were conducted by injecting groundwater containing between 14.9 and 21.2 mg/L dissolved O2 as an oxidant into the NRZ. The oxidation of U(IV) from this NRZ increased aqueous U(VI) concentrations and caused a shift to higher 238U/235U in groundwater as U(IV) was oxidized primarily on the outer fringes of the NRZ. In total these observations suggest that the stability of solid phase uranium is governed by coupled reaction and transport processes. To better understand various reactive transport scenarios we developed a model for the formation and oxidation of NRZ's utilizing the reactive transport software CrunchTope. These simulations suggest that the development of isotopically heterogeneous U(IV) within NRZ's is largely controlled by permeability of the NRZ and the U(VI) reduction rate. Oxidation of U(IV) from the NRZ's is constrained by the oxidation rate of U(IV) as well as iron sulfides, which can prevent oxidation of U(IV) by scavenging dissolved oxygen.

Incorporation mechanisms of actinide elements into the structures of U 6+ phases formed during the oxidation of spent nuclear fuel

NASA Astrophysics Data System (ADS)

Burns, Peter C.; Ewing, Rodney C.; Miller, Mark L.

1997-05-01

Uranyl oxide hydrate and uranyl silicate phases will form due to the corrosion and alteration of spent nuclear fuel under oxidizing conditions in silica-bearing solution. The actinide elements in the spent fuel may be incorporated into the structures of these secondary U6+ phases during the long-term corrosion of the UO 2 in spent fuel. The incorporation of actinide elements into the crystal structures of the alteration products may decrease actinide mobility. The crystal chemistry of the various oxidation states of the actinide elements of environmental concern is examined to identify possible incorporation mechanisms. The substitutions Pu 6+U 6+ and (Pu 5+, Np 5+)U 6+ should readily occur in many U 6+ structures, although structural modification may be required to satisfy local bond-valence requirements. Crystal-chemical characteristics of the U 6+ phases indicate that An 4+ (An: actinide)U 6+ substitution is likely to occur in the sheets of uranyl polyhedra that occur in the structures of the minerals schoepite, [(UO 2) 8O 2(OH) 12](H 2O) 12, ianthinite, [U 24+ (UO 2) 4O 6(OH) 4(H 2O) 4](H 2O) 5, becquerelite, Ca[(UO 2) 3O 2(OH) 3] 2(H 2O) 8, compreignacite, K 2[(UO 2) 3O 2(OH) 3] 2(H 2O) 8, α-uranophane, Ca[(UO 2)(SiO 3OH)] 2(H 2O) 5, and boltwoodite, K(H 2O)[(UO 2)(SiO 4)], all of which are likely to form due to the oxidation and alteration of the UO 2 in spent fuel. The incorporation of An 3+ into the sheets of the structures of α-uranophane and boltwoodite, as well as interlayer sites of various uranyl phases, may occur.

Uranium passivation by C + implantation: A photoemission and secondary ion mass spectrometry study

NASA Astrophysics Data System (ADS)

Nelson, A. J.; Felter, T. E.; Wu, K. J.; Evans, C.; Ferreira, J. L.; Siekhaus, W. J.; McLean, W.

2006-03-01

Implantation of 33 keV C + ions into polycrystalline U 238 with a dose of 4.3 × 10 17 cm -2 produces a physically and chemically modified surface layer that prevents further air oxidation and corrosion. X-ray photoelectron spectroscopy and secondary ion mass spectrometry were used to investigate the surface chemistry and electronic structure of this C + ion implanted polycrystalline uranium and a non-implanted region of the sample, both regions exposed to air for more than a year. In addition, scanning electron microscopy was used to examine and compare the surface morphology of the two regions. The U 4f, O 1s and C 1s core-level and valence band spectra clearly indicate carbide formation in the modified surface layer. The time-of-flight secondary ion mass spectrometry depth profiling results reveal an oxy-carbide surface layer over an approximately 200 nm thick UC layer with little or no residual oxidation at the carbide layer/U metal transitional interface.

Anodic behavior of uranium in AlCl3-1-ethyl-3-methyl-imidazolium chloride ionic liquid

NASA Astrophysics Data System (ADS)

Jiang, Yidong; Luo, Lizhu; Wang, Shaofei; Bin, Ren; Zhang, Guikai; Wang, Xiaolin

2018-01-01

The oxidation state of metals unambiguously affects its anodic behavior in ionic liquid. We systematically investigated the anodic behavior of uranium with different surface oxidation states by electrochemical measurements, spectroscopic methods and surface analysis techniques. In the anodic process, metal uranium can be oxidized to U3+. The corresponding products accumulated on the metal/ILs interface will form a viscous layer. The anodic behavior of uranium is also strongly dependent upon the surface oxide states including thickness and homogeneity of the oxide film. With an increase in the thickness of oxide film, it will be breached at potentials in excess of a critical value. A uniform oxide on uranium surface can be breached evenly, and then the underlying metal starts to dissolve forming a viscous layer which can facilitate uniformly stripping of oxide, thus giving an oxide-free surface. Otherwise, a nonuniform oxide can result in a severe pitted surface with residue oxygen.

Pyroprocessing of oxidized sodium-bonded fast reactor fuel - An experimental study of treatment options for degraded EBR-II fuel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hermann, S.D.; Gese, N.J.; Wurth, L.A.

An experimental study was conducted to assess pyrochemical treatment options for degraded EBR-II fuel. As oxidized material, the degraded fuel would need to be converted back to metal to enable electrorefining within an existing electro-metallurgical treatment process. A lithium-based electrolytic reduction process was studied to assess the efficacy of converting oxide materials to metal with a particular focus on the impact of zirconium oxide and sodium oxide on this process. Bench-scale electrolytic reduction experiments were performed in LiCl-Li{sub 2}O at 650 C. degrees with combinations of manganese oxide (used as a surrogate for uranium oxide), zirconium oxide, and sodium oxide.more » In the absence of zirconium or sodium oxide, the electrolytic reduction of MnO showed nearly complete conversion to metal. The electrolytic reduction of a blend of MnO-ZrO{sub 2} in LiCl - 1 wt% Li{sub 2}O showed substantial reduction of manganese, but only 8.5% of the zirconium was found in the metal phase. The electrolytic reduction of the same blend of MnO-ZrO{sub 2} in LiCl - 1 wt% Li{sub 2}O - 6.2 wt% Na{sub 2}O showed substantial reduction of manganese, but zirconium reduction was even less at 2.4%. This study concluded that ZrO{sub 2} cannot be substantially reduced to metal in an electrolytic reduction system with LiCl - 1 wt% Li{sub 2}O at 650 C. degrees due to the perceived preferential formation of lithium zirconate. This study also identified a possible interference that sodium oxide may have on the same system by introducing a parasitic and cyclic reaction of dissolved sodium metal between oxidation at the anode and reduction at the cathode. When applied to oxidized sodium-bonded EBR-II fuel (e.g., U-10Zr), the prescribed electrolytic reduction system would not be expected to substantially reduce zirconium oxide, and the accumulation of sodium in the electrolyte could interfere with the reduction of uranium oxide, or at least render it less efficient.« less

Breeding of {sup 233}U in the thorium–uranium fuel cycle in VVER reactors using heavy water

DOE Office of Scientific and Technical Information (OSTI.GOV)

Marshalkin, V. E., E-mail: marshalkin@vniief.ru; Povyshev, V. M.

A method is proposed for achieving optimal neutron kinetics and efficient isotope transmutation in the {sup 233}U–{sup 232}Th oxide fuel of water-moderated reactors with variable water composition (D{sub 2}O, H{sub 2}O) that ensures breeding of the {sup 233}U and {sup 235}U isotopes. The method is comparatively simple to implement.

The effect of Si and Al concentrations on the removal of U(VI) in the alkaline conditions created by NH3 gas

DOE Office of Scientific and Technical Information (OSTI.GOV)

Katsenovich, Yelena P.; Cardona, Claudia; Lapierre, Robert

2016-10-01

Remediation of uranium in the deep unsaturated zone is a challenging task, especially in the presence of oxygenated, high-carbonate alkalinity soil and pore water composition typical for arid and semi-arid environments of the western regions of the U.S. This study evaluates the effect of various pore water constituencies on changes of uranium concentrations in alkaline conditions, created in the presence of reactive gases such as NH3 to effectively mitigate uranium contamination in the vadose zone sediments. This contaminant is a potential source for groundwater pollution through slow infiltration of soluble and highly mobile uranium species towards the water table. Themore » objective of this research was to evaluate uranium sequestration efficiencies in the alkaline synthetic pore water solutions prepared in a broad range of Si, Al, and bicarbonate concentrations typically present in field systems of the western U.S. regions and identify solid uranium-bearing phases that result from ammonia gas treatment. In previous studies (Szecsody et al. 2012; Zhong et al. 2015), although uranium mobility was greatly decreased, solid phases could not be identified at the low uranium concentrations in field-contaminated sediments. The chemical composition of the synthetic pore water used in the experiments varied for silica (5–250 mM), Al3+ (2.8 or 5 mM), HCO3- (0–100 mM) and U(VI) (0.0021–0.0084 mM) in the solution mixture. Experiment results suggested that solutions with Si concentrations higher than 50 mM exhibited greater removal efficiencies of U(VI). Solutions with higher concentrations of bicarbonate also exhibited greater removal efficiencies for Si, Al, and U(VI). Overall, the silica polymerization reaction leading to the formation of Si gel correlated with the removal of U(VI), Si, and Al from the solution. If no Si polymerization was observed, there was no U removal from the supernatant solution. Speciation modeling indicated that the dominant uranium species in the presence of bicarbonate were anionic uranyl carbonate complexes (UO2(CO3)2-2 and UO2(CO3)3-4) and in the absence of bicarbonate in the solution, U(VI) major species appeared as uranyl-hydroxide (UO2(OH)3- and UO2(OH)4-2) species. The model also predicted the formation of uranium solid phases. Uranyl carbonates as rutherfordine [UO2CO3], cejkaite [Na4(UO2)(CO3)3] and hydrated uranyl silicate phases as Na-boltwoodite [Na(UO2)(SiO4)·1.5H2O] were anticipated for most of the synthetic pore water compositions amended from medium (2.9 mM) to high (100 mM) bicarbonate concentrations.« less

High-resolution mineralogical characterization and biogeochemical modeling of uranium reaction pathways at the FRC

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen Zhu

2006-06-15

High-Resolution Mineralogical Characterization and Biogeochemical Modeling of Uranium Reduction Pathways at the Oak Ridge Field-Research Center (FRC) Chen Zhu, Indiana University, David R. Veblen, Johns Hopkins University We have successfully completed a proof-of-concept, one-year grant on a three-year proposal from the former NABIR program, and here we seek additional two-year funding to complete and publish the research. Using a state-of-the-art 300-kV, atomic resolution, Field Emission Gun Transmission Electron Microscope (TEM), we have successfully identified three categories of mineral hosts for uranium in contaminated soils: (1) iron oxides; (2) mixed manganese-iron oxides; and (3) uranium phosphates. Method development using parallel electronmore » energy loss spectroscopy (EELS) associated with the TEM shows great promise for characterizing the valence states of immobilized U during bioremediation. We have also collected 27 groundwater samples from two push-pull field biostimulation tests, which form two time series from zero to approximately 600 hours. The temporal evolution in major cations, anions, trace elements, and the stable isotopes 34S, 18O in sulfate, 15N in nitrate, and 13C in dissolved inorganic carbon (DIC) clearly show that biostimulation resulted in reduction of nitrate, Mn(IV), Fe(III), U(VI), sulfate, and Tc(VII), and these reduction reactions were intimately coupled with a complex network of inorganic reactions evident from alkalinity, pH, Na, K, Mg, and Ca concentrations. From these temporal trends, apparent zero order rates were regressed. However, our extensive suite of chemical and isotopic data sets, perhaps the first and only comprehensive data set available at the FRC, show that the derived rates from these field biostimulation experiments are composite and lump-sum rates. There were several reactions that were occurring at the same time but were masked by these pseudo-zero order rates. A reaction-path model comprising a total of nine redox couples (NO3–/NH4+, MnO2(s)/Mn2+, Fe(OH)3(s) /Fe2+, TcO4–/TcO2(s), UO22+/UO2(s), SO42–/HS–, CO2/CH4, ethanol/acetate, and H+/H2.) is used to simulate the temporal biogeochemical evolution observed in the field tests. Preliminary results show that the models based on thermodynamics and more complex rate laws can generate the apparent zero order rates when several concurrent or competing reactions occur. Professor Alex Halliday of Oxford University, UK, and his postdoctoral associates are measuring the uranium isotopes in our groundwater samples. Newly developed state-of-the-art analytical techniques in measuring variability in 235U/238U offer the potential to distinguish biotic and abiotic uranium reductive mechanisms.« less

Reactivity of uranium(iii) with H2E (E = S, Se, Te): synthesis of a series of mononuclear and dinuclear uranium(iv) hydrochalcogenido complexes.

PubMed

Franke, Sebastian M; Rosenzweig, Michael W; Heinemann, Frank W; Meyer, Karsten

2015-01-01

We report the syntheses, electronic properties, and molecular structures of a series of mono- and dinuclear uranium(iv) hydrochalcogenido complexes supported by the sterically demanding but very flexible, single N-anchored tris(aryloxide) ligand ( Ad ArO) 3 N) 3- . The mononuclear complexes [(( Ad ArO) 3 N)U(DME)(EH)] (E = S, Se, Te) can be obtained from the reaction of the uranium(iii) starting material [(( Ad ArO) 3 N)U III (DME)] in DME via reduction of H 2 E and the elimination of 0.5 equivalents of H 2 . The dinuclear complexes [{(( Ad ArO) 3 N)U} 2 (μ-EH) 2 ] can be obtained by dissolving their mononuclear counterparts in non-coordinating solvents such as benzene. In order to facilitate the work with the highly toxic gases, we created concentrated THF solutions that can be handled using simple glovebox techniques and can be stored at -35 °C for several weeks.

Pyrochlore-rich titanate ceramics for the immobilization of plutonium: redox effects on phase equilibria in cerium- and thorium- substituted analogs

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ryerson, F J; Ebbinghaus, B

2000-05-25

Three compositions representing plutonium-free analogs of a proposed Ca-Ti-Gd-Hf-U-PU oxide ceramic for the immobilization of plutonium were equilibrated at 1 atm, 1350 C over a range of oxygen fugacities between air and that equivalent to the iron-wuestite buffer. The cerium analog replaces Pu on a mole-per-mole basic with Ce; the thorium analog replaces Pu with Th. A third material has 10 wt% Al{sub 2}O{sub 3} added to the cerium analog to encourage the formation of a Hf-analog of, CaHfTi{sub 2}O{sub 7}, zirconolite, which is referred to as hafnolite. The predominant phase produced in each formulation under all conditions is pyrochlore,more » A{sub 2}T{sub 2}O{sub 7}, where the T site is filled by Ti, and Ca, the lanthanides, Hf, U and Pu are accommodated on the A-site. Other lanthanide and uranium-bearing phases encountered include brannerite (UTi{sub 2}O{sub 6}), hafnolite (CaHfTi{sub 2}O{sub 7}), perovskite (CaTiO{sub 3}) and a calcium-lanthanide aluminotitanate with nominal stoichiometry (Ca,Ln)Ti{sub 2}Al{sub 9}O{sub 19}, where Ln is a lanthanide. The phase compositions show progressive shifts with decreasing oxygen fugacity. All of the phases observed have previously been identified in titanate-based high-level radioactive waste ceramics and demonstrate the flexibility of these ceramics to variations in processing parameters. The main variation is an increase in the uranium concentrations of pyrochlore and brannerite which must be accommodated by variations in modal abundance. Pyrochlore compositions are consistent with existing spectroscopic data suggesting that uranium is predominantly pentavalent in samples synthesized in air. A simple model based on ideal stoichiometry suggests the U{sup +4}/{Sigma}U varies linearly with log fO{sub 2} and that all of the uranium is quadravalent at the iron-wuestite buffer.« less

Uranium bioprecipitation mediated by yeasts utilizing organic phosphorus substrates.

PubMed

Liang, Xinjin; Csetenyi, Laszlo; Gadd, Geoffrey Michael

2016-06-01

In this research, we have demonstrated the ability of several yeast species to mediate U(VI) biomineralization through uranium phosphate biomineral formation when utilizing an organic source of phosphorus (glycerol 2-phosphate disodium salt hydrate (C3H7Na2O6P·xH2O (G2P)) or phytic acid sodium salt hydrate (C6H18O24P6·xNa(+)·yH2O (PyA))) in the presence of soluble UO2(NO3)2. The formation of meta-ankoleite (K2(UO2)2(PO4)2·6(H2O)), chernikovite ((H3O)2(UO2)2(PO4)2·6(H2O)), bassetite (Fe(++)(UO2)2(PO4)2·8(H2O)), and uramphite ((NH4)(UO2)(PO4)·3(H2O)) on cell surfaces was confirmed by X-ray diffraction in yeasts grown in a defined liquid medium amended with uranium and an organic phosphorus source, as well as in yeasts pre-grown in organic phosphorus-containing media and then subsequently exposed to UO2(NO3)2. The resulting minerals depended on the yeast species as well as physico-chemical conditions. The results obtained in this study demonstrate that phosphatase-mediated uranium biomineralization can occur in yeasts supplied with an organic phosphate substrate as sole source of phosphorus. Further understanding of yeast interactions with uranium may be relevant to development of potential treatment methods for uranium waste and utilization of organic phosphate sources and for prediction of microbial impacts on the fate of uranium in the environment.

Anaerobic U(IV) Bio-oxidation and the Resultant Remobilization of Uranium in Contaminated Sediments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Coates, John D.

2005-06-01

A proposed strategy for the remediation of uranium (U) contaminated sites is based on immobilizing U by reducing the oxidized soluble U, U(VI), to form a reduced insoluble end product, U(IV). Due to the use of nitric acid in the processing of nuclear fuels, nitrate is often a co-contaminant found in many of the environments contaminated with uranium. Recent studies indicate that nitrate inhibits U(VI) reduction in sediment slurries. However, the mechanism responsible for the apparent inhibition of U(VI) reduction is unknown, i.e. preferential utilization of nitrate as an electron acceptor, direct biological oxidation of U(IV) coupled to nitrate reduction,more » and/or abiotic oxidation by intermediates of nitrate reduction. Recent studies indicates that direct biological oxidation of U(IV) coupled to nitrate reduction may exist in situ, however, to date no organisms have been identified that can grow by this metabolism. In an effort to evaluate the potential for nitrate-dependent bio-oxidation of U(IV) in anaerobic sedimentary environments, we have initiated the enumeration of nitrate-dependent U(IV) oxidizing bacteria. Sediments, soils, and groundwater from uranium (U) contaminated sites, including subsurface sediments from the NABIR Field Research Center (FRC), as well as uncontaminated sites, including subsurface sediments from the NABIR FRC and Longhorn Army Ammunition Plant, Texas, lake sediments, and agricultural field soil, sites served as the inoculum source. Enumeration of the nitrate-dependent U(IV) oxidizing microbial population in sedimentary environments by most probable number technique have revealed sedimentary microbial populations ranging from 9.3 x 101 - 2.4 x 103 cells (g sediment)-1 in both contaminated and uncontaminated sites. Interestingly uncontaminated subsurface sediments (NABIR FRC Background core FB618 and Longhorn Texas Core BH2-18) both harbored the most numerous nitrate-dependent U(IV) oxidizing population 2.4 x 103 cells (g sediment)-1. The nitrate-dependent U(IV) oxidizing microbial population in groundwaters is less numerous ranging from 0 cells mL-1 (Well FW300, Uncontaminated Background NABIR FRC) to 4.3 x 102 cells mL-1 (Well TPB16, Contaminated Area 2 NABIR FRC). The presence of nitrate-dependent U(IV) oxidizing bacteria supports our hypothesis that bacteria capable of anaerobic U(IV) oxidation are ubiquitous and indigenous to sedimentary and groundwater environments.« less

A model of early formation of uranium molecular oxides in laser-ablated plasmas

NASA Astrophysics Data System (ADS)

Finko, Mikhail S.; Curreli, Davide; Weisz, David G.; Crowhurst, Jonathan C.; Rose, Timothy P.; Koroglu, Batikan; Radousky, Harry B.; Armstrong, Michael R.

2017-12-01

In this work, we present a newly constructed U x O y reaction mechanism that consists of 30 reaction channels (21 of which are reversible channels) for 11 uranium molecular species (including ions). Both the selection of reaction channels and calculation of corresponding rate coefficients is accomplished via a comprehensive literature review and application of basic reaction rate theory. The reaction mechanism is supplemented by a detailed description of oxygen plasma chemistry (19 species and 142 reaction channels) and is used to model an atmospheric laser ablated uranium plume via a 0D (global) model. The global model is used to analyze the evolution of key uranium molecular species predicted by the reaction mechanism, and the initial stage of formation of uranium oxide species.

Rare-Earth Oxide Ion (Tm3+, Ho3+, and U3+) Doped Glasses and Fibres for 1.8 to 4 Micrometer Coherent and Broadband Sources

DTIC Science & Technology

2006-07-24

oxide ( TeO2 ) , fluorine- containing silicate (SiOF2) and germanate (GeOF2) glass hosts for each dopant by characterising the spectroscopic properties...Earth Oxide Ion (Tm3+, Ho3+, And U3+) Doped Glasses And Fibres For 1.8 To 4 Micrometer Coherent And Broadband Sources 5c. PROGRAM ELEMENT NUMBER 5d...Rare-earth oxide ion (Tm3+, Ho3+, and U3+) doped glasses and fibres for 1.8 to 4 micrometer coherent and broadband sources Report prepared

Determination of trace levels of uranium and thorium in high purity gadolinium sulfate using the ICP-MS with solid-phase chromatographic extraction resin

NASA Astrophysics Data System (ADS)

Ito, S.; Takaku, Y.; Ikeda, M.; Kishimoto, Y.

2017-11-01

The new Super-Kamiokande-Gadolinium (SK-Gd) project is an upgrade of the Super-Kamiokande (SK) detector. In the SK-Gd project, 0.2% Gd_2(SO_4)_3 is loaded into the 50 kton water tank of the SK. One of the main purposes of the project is to discover supernova relic neutrinos. Neutrino measurements and proton decay searches will also be performed in the SK-Gd. In order to measure solar neutrinos with a low energy threshold of ˜3.5 MeV in the SK-Gd, the main radioactive contaminations, ^{238}U and ^{232}Th, in Gd_2(SO_4)_3{\\cdot}8H_2O, should be minimized before loading. Our maximum levels for U and Th are 5 mBq (U)/kg (Gd_2(SO_4)_3{\\cdot}8H_2O) and 0.05 mBq (Th)/kg (Gd_2(SO_4)_3{\\cdot}8H_2O). In order to measure such low concentrations of U and Th in Gd_2(SO_4)_3{\\cdot}8H_2O, we developed the solid-phase extraction technique. Using this method, about 90% or more U and Th could be efficiently extracted while Gd was reduced by a factor of about 104. This allowed these radioactivity contaminations to be measured precisely as 0.04 mBq/kg (Gd_2(SO_4)_3{\\cdot}8H_2O) for U and 0.01 mBq/kg (Gd_2(SO_4)_3{\\cdot}8H_2O) for Th. We measured three pure Gd_2(SO_4)_3{\\cdot}8H_2O samples using this method and estimated that the purest one contained <0.04 mBq (U)/kg (Gd_2(SO_4)_3{\\cdot}8H_2O) and 0.06 ± 0.01 mBq (Th)/kg (Gd_2(SO_4)_3{\\cdot}8H_2O) by the ICP-MS.

Uranium resources in the Silver Reef (Harrisburg) district, Washington County, Utah

USGS Publications Warehouse

Stugard, Frederick

1951-01-01

The Silver Reef district is near Leeds, about 16 miles north of St. George, Utah. The major structural feature of the district is the Virgin anticline, a fold extending southwestward toward St. George. The anticline has been breached by erosion, and sandstone hogbacks or 'reefs' are carved from the Shinarump conglomerate mud sandstone members of the Chinle formation, both of Triassic age. Thirteen occurrences of uranium-vanadium minerals, all within the Tecumseh sandstone, which is the upper part of the Silver Reef sandstone member of the Chinle formation, have been examined over an area about 1.75 miles wide and 3 miles long. Two shipments of uranium-vanadium ore have been produced from the Chloride Chief and Silver Point claims. Samples from the deposits contain as much as 0.94 percent U3O8. The ore contains several times as much vanadium oxide as uranium, some copper, and traces of silver. It occurs in thinly bedded cross-bedded shales and sandstones within the fluviatile Tecumseh sandstone member of the Chinle formation. The ore beds are lenticular and are localized 2 near the base, center, and top of this sandstone member. The uranium-vanadium ore contains several yellow and green minerals not yet identified; the occurrences are similar to, but not associated with, the cerargyrite ore that made the district famous from 1879 to 1909.

The coprecipitation of Pu and other radionuclides with CaCO[sub 3

DOE Office of Scientific and Technical Information (OSTI.GOV)

Meece, D.E.; Benninger, L.K.

1993-04-01

The record of fallout plutonium concentrations in annual bands of corals is strikingly similar to the record of atmospheric deposition of [sup 90]Sr. This similarity implies that corals may incorporate Pu from seawater with a constant partition coefficient (constant discrimination). To investigate physicochemical aspects of Pu incorporation, the following have been coprecipitated with CaCO[sub 3] (calcite and aragonite): oxidized and reduced Pu; americium, thorium, and uranium as analogs to Pu oxidation states (III, IV, VI), respectively; and [sup 210]Pb as a particle-reactive nuclide which may be incorporated by corals with constant discrimination. Americium, thorium, and lead adsorb onto both calcitemore » and aragonite, with more than 99% of the recovered activity found associated with the solids. Uranium exhibits a behavior consistent with lattice substitution. Partition coefficients for U in aragonite range from 1.8 to 9.8 and vary inversely with pH and/or rate of precipitation. The partition coefficient for U in calcite is less than 0.2 and may be as low as 0.046. Reduced Pu sorbs with 3 to 4% remaining in solution. Oxidized Pu may both sorb and coprecipitate. The coral record for Pb and U results primarily from biological, rather than physicochemical, effects; it is likely that the PU coral record also reflects biological discrimination. 50 refs., 4 figs., 5 tabs.« less

PROPERTIES OF URANIUM MONOCARBIDE

DOE Office of Scientific and Technical Information (OSTI.GOV)

Brown, D.J.; Stobo, J.J.

1963-02-01

Some of the properties of UC relevant to its use as a fuel for either thermal or fast reactors were evaluated. The oxidation resistance of cast UC is shown to be superior to that of U metal above about 550 deg C in CO/sub 2/, and above about 200 deg C in air containing 1 wt% H/sub 2/O. In CO/sub 2/ at 800 deg C, even porous sintered UC is more resistant than U. Good compatibility with liquid Na (containing 10 ppm O) is reported, after 8 weeks at 800 and at 750 deg C. Hot-hardness values drop from 700more » VPN at 300 deg C to 50 VPN at 1000 deg C. (auth)« less

In situ mobility of uranium in the presence of nitrate following sulfate-reducing conditions.

PubMed

Paradis, Charles J; Jagadamma, Sindhu; Watson, David B; McKay, Larry D; Hazen, Terry C; Park, Melora; Istok, Jonathan D

2016-04-01

Reoxidation and mobilization of previously reduced and immobilized uranium by dissolved-phase oxidants poses a significant challenge for remediating uranium-contaminated groundwater. Preferential oxidation of reduced sulfur-bearing species, as opposed to reduced uranium-bearing species, has been demonstrated to limit the mobility of uranium at the laboratory scale yet field-scale investigations are lacking. In this study, the mobility of uranium in the presence of nitrate oxidant was investigated in a shallow groundwater system after establishing conditions conducive to uranium reduction and the formation of reduced sulfur-bearing species. A series of three injections of groundwater (200 L) containing U(VI) (5 μM) and amended with ethanol (40 mM) and sulfate (20 mM) were conducted in ten test wells in order to stimulate microbial-mediated reduction of uranium and the formation of reduced sulfur-bearing species. Simultaneous push-pull tests were then conducted in triplicate well clusters to investigate the mobility of U(VI) under three conditions: 1) high nitrate (120 mM), 2) high nitrate (120 mM) with ethanol (30 mM), and 3) low nitrate (2 mM) with ethanol (30 mM). Dilution-adjusted breakthrough curves of ethanol, nitrate, nitrite, sulfate, and U(VI) suggested that nitrate reduction was predominantly coupled to the oxidation of reduced-sulfur bearing species, as opposed to the reoxidation of U(IV), under all three conditions for the duration of the 36-day tests. The amount of sulfate, but not U(VI), recovered during the push-pull tests was substantially more than injected, relative to bromide tracer, under all three conditions and further suggested that reduced sulfur-bearing species were preferentially oxidized under nitrate-reducing conditions. However, some reoxidation of U(IV) was observed under nitrate-reducing conditions and in the absence of detectable nitrate and/or nitrite. This suggested that reduced sulfur-bearing species may not be fully effective at limiting the mobility of uranium in the presence of dissolved and/or solid-phase oxidants. The results of this field study confirmed those of previous laboratory studies which suggested that reoxidation of uranium under nitrate-reducing conditions can be substantially limited by preferential oxidation of reduced sulfur-bearing species. Copyright © 2016 The Authors. Published by Elsevier B.V. All rights reserved.

In situ mobility of uranium in the presence of nitrate following sulfate-reducing conditions

DOE PAGES

Paradis, Charles J.; Jagadamma, Sindhu; Watson, David B.; ...

2016-02-11

Reoxidation and mobilization of previously reduced and immobilized uranium by dissolved phase oxidants poses a significant challenge for remediating uranium-contaminated groundwater. Preferential oxidation of reduced sulfur-bearing species, as opposed to reduced uranium bearing species, has been demonstrated to limit the mobility of uranium at the laboratory scale yet field-scale investigations are lacking. Here in this study, the mobility of uranium in the presence of nitrate oxidant was investigated in a shallow groundwater system after establishing conditions conducive to uranium reduction and the formation of reduced sulfur-bearing species. A series of three injections of groundwater (200 L) containing U(VI) (5 μM)more » and amended with ethanol (40 mM) and sulfate (20 mM) were conducted in ten test wells in order to stimulate microbial mediated reduction of uranium and the formation of reduced sulfur-bearing species. Simultaneous push-pull tests were then conducted in triplicate well clusters to investigate the mobility of U(VI) under three conditions: 1) high nitrate (120 mM), 2) high nitrate (120 mM) with ethanol (30 mM), and 3) low nitrate (2 mM) with ethanol (30 mM). Dilution-adjusted breakthrough curves of ethanol, nitrate, nitrite, sulfate, and U(VI) suggested that nitrate reduction was predominantly coupled to the oxidation of reduced-sulfur bearing species, as opposed to the reoxidation of U(IV), under all three conditions for the duration of the 36-day tests. The amount of sulfate, but not U(VI), recovered during the push-pull tests was substantially more than injected, relative to bromide tracer, under all three conditions and further suggested that reduced sulfur-bearing species were preferentially oxidized under nitrate-reducing conditions. However, some reoxidation of U(IV) was observed under nitrate-reducing conditions and in the absence of detectable nitrate and/or nitrite. This suggested that reduced sulfur-bearing species may not be fully effective at limiting the mobility of uranium in the presence of dissolved and/or solid-phase oxidants. Lastly, the results of this field study confirmed those of previous laboratory studies which suggested that reoxidation of uranium under nitrate-reducing conditions can be substantially limited by preferential oxidation of reduced sulfur-bearing species.« less

238U and 235U isotope fractionation upon oxidation of uranium-bearing rocks by fracture waters

NASA Astrophysics Data System (ADS)

Chernyshev, I. V.; Golubev, V. N.; Chugaev, A. V.; Mandzhieva, G. V.

2016-10-01

The variations in 238U/235U values accompanying mobilization of U by fracture waters from uranium-bearing rocks, in which U occurs as a fine impregnation of oxides and silicates, were studied by the high-precision (±0.07‰) MC-ICP-MS method. Transition of U into the aqueous phase in the oxidized state U(VI) is accompanied by its isotope fractionation with enrichment of dissolved U(VI) in the heavy isotope 238U up to 0.32‰ in relation to the composition of the solid phases. According to the sign, this effect is consistent with the tendency of the behavior of 238U and 235U upon interaction of river waters with rocks of the catchment areas [11] and with the effect observed during oxidation of uraninite by the oxygen-bearing NaHCO3 solution [12].

Solid state speciation of uranium and its local structure in Sr2CeO4 using photoluminescence spectroscopy.

PubMed

Sahu, M; Gupta, Santosh K; Jain, D; Saxena, M K; Kadam, R M

2018-04-15

An effort was taken to carry our speciation study of uranium ion in technologically important cerate host Sr 2 CeO 4 using time resolved photoluminescence spectroscopy. Such studies are not relevant only to nuclear industry but can give rich insight into fundamentals of 5f electron chemistry in solid state systems. In this work both undoped and varied amount of uranium doped Sr 2 CeO 4 compound is synthesized using complex polymerization method and is characterized systematically using X-ray diffraction (XRD), Raman spectroscopy, impedance spectroscopy and scanning electron microscopy (SEM). Both XRD and Raman spectroscopy confirmed the formation of pure Sr 2 CeO 4 which has tendency to decompose peritectically to SrCeO 3 and SrO at higher temperature. Uranium doping is confirmed by XRD. Uranium exhibits a rich chemistry owing to its variable oxidation state from +3 to +6. Each of them exhibits distinct luminescence properties either due to f-f transitions or ligand to metal charge transfer (LMCT). We have taken Sr 2 CeO 4 as a model host lattice to understand the photophysical characteristics of uranium ion in it. Emission spectroscopy revealed the stabilization of uranium as U (VI) in the form of UO 6 6- (octahedral uranate) in Sr 2 CeO 4 . Emission kinetics study reflects that uranate ions are not homogeneously distributed in Sr 2 CeO 4 and it has two different environments due to its stabilization at both Sr 2+ as well as Ce 4+ site. The lifetime population analysis interestingly pinpointed that majority of uranate ion resided at Ce 4+ site. The critical energy-transfer distance between the uranate ion was determined based on which the concentration quenching mechanism was attributed to electric multipolar interaction. These studies are very important in designing Sr 2 CeO 4 based optoelectronic material as well exploring it for actinides studies. Copyright © 2018 Elsevier B.V. All rights reserved.

Solid state speciation of uranium and its local structure in Sr2CeO4 using photoluminescence spectroscopy

NASA Astrophysics Data System (ADS)

Sahu, M.; Gupta, Santosh K.; Jain, D.; Saxena, M. K.; Kadam, R. M.

2018-04-01

An effort was taken to carry our speciation study of uranium ion in technologically important cerate host Sr2CeO4 using time resolved photoluminescence spectroscopy. Such studies are not relevant only to nuclear industry but can give rich insight into fundamentals of 5f electron chemistry in solid state systems. In this work both undoped and varied amount of uranium doped Sr2CeO4 compound is synthesized using complex polymerization method and is characterized systematically using X-ray diffraction (XRD), Raman spectroscopy, photoluminescence spectroscopy and scanning electron microscopy (SEM). Both XRD and Raman spectroscopy confirmed the formation of pure Sr2CeO4 which has tendency to decompose peritectically to SrCeO3 and SrO at higher temperature. Uranium doping is confirmed by XRD. Uranium exhibits a rich chemistry owing to its variable oxidation state from +3 to +6. Each of them exhibits distinct luminescence properties either due to f-f transitions or ligand to metal charge transfer (LMCT). We have taken Sr2CeO4 as a model host lattice to understand the photophysical characteristics of uranium ion in it. Emission spectroscopy revealed the stabilization of uranium as U (VI) in the form of UO66- (octahedral uranate) in Sr2CeO4. Emission kinetics study reflects that uranate ions are not homogeneously distributed in Sr2CeO4 and it has two different environments due to its stabilization at both Sr2+ as well as Ce4+ site. The lifetime population analysis interestingly pinpointed that majority of uranate ion resided at Ce4+ site. The critical energy-transfer distance between the uranate ion was determined based on which the concentration quenching mechanism was attributed to electric multipolar interaction. These studies are very important in designing Sr2CeO4 based optoelectronic material as well exploring it for actinides studies.

Bis(hydroxylamino)triazines: High Selectivity and Hydrolytic Stability of Hydroxylamine-Based Ligands for Uranyl Compared to Vanadium(V) and Iron(III).

PubMed

Hadjithoma, Sofia; Papanikolaou, Michael G; Leontidis, Epameinondas; Kabanos, Themistoklis A; Keramidas, Anastasios D

2018-06-08

The development of ligands with high selectivity and affinity for uranium is critical in the extraction of uranium from human body, radioactive waste, and seawater. A scientific challenge is the improvement of the selectivity of chelators for uranium over other heavy metals, including iron and vanadium. Flat ligands with hard donor atoms that satisfy the geometric and electronic requirements of the U VI O 2 2+ exhibit high selectivity for the uranyl moiety. The bis(hydroxylamino)(triazine) ligand, 2,6-bis[hydroxy(methyl)amino]-4-morpholino-1,3,5-triazine (H 2 bihyat), a strong binder for hard metal ions (Fe III , Ti IV , V V , and Mo VI ), reacted with [U VI O 2 (NO 3 ) 2 (H 2 O) 2 ]·4H 2 O in aqueous solution and resulted in the isolation of the complexes [U VI O 2 (bihyat)(H 2 O)], [U VI O 2 (bihyat) 2 ] 2- , and {[U VI O 2 (bihyat)(μ-OH)]} 2 2- . These three species are in equilibrium in aqueous solution, and their abundance varies with the concentration of H 2 bihyat and the pH. Reaction of H 2 bihyat with [U VI O 2 (NO 3 ) 2 (H 2 O) 2 ]·4H 2 O in CH 3 CN gave the trinuclear complex [U VI 3 O 6 (bihyat) 2 (μ-bihyat) 2 ] 2- , which is the major species in organic solvents. The dynamics between the U VI O 2 2+ and the free ligand H 2 bihyat in aqueous and dimethyl sulfoxide solutions; the metal binding ability of the H 2 bihyat over pyridine-2,6-dicarboxylic acid (H 2 dipic) or glutarimidedioxime for U VI O 2 2+ , and the selectivity of the H 2 bihyat to bind U VI O 2 2+ in comparison to V V O 4 3- and Fe III in either U VI O 2 2+ /V V O 4 3- or U VI O 2 2+ /Fe III solutions were examined by NMR and UV-vis spectroscopies. The results revealed that H 2 bihyat is a superior ligand for U VI O 2 2+ with high selectivity compared to Fe III and V V O 4 3- , which increases at higher pHs. Thus, this type of ligand might find applications in the extraction of uranium from the sea and its removal from the environment and the human body.

Uranium Redox Transformations after U(VI) Coprecipitation with Magnetite Nanoparticles.

PubMed

Pidchenko, Ivan; Kvashnina, Kristina O; Yokosawa, Tadahiro; Finck, Nicolas; Bahl, Sebastian; Schild, Dieter; Polly, Robert; Bohnert, Elke; Rossberg, André; Göttlicher, Jörg; Dardenne, Kathy; Rothe, Jörg; Schäfer, Thorsten; Geckeis, Horst; Vitova, Tonya

2017-02-21

Uranium redox states and speciation in magnetite nanoparticles coprecipitated with U(VI) for uranium loadings varying from 1000 to 10 000 ppm are investigated by X-ray absorption spectroscopy (XAS). It is demonstrated that the U M 4 high energy resolution X-ray absorption near edge structure (HR-XANES) method is capable to clearly characterize U(IV), U(V), and U(VI) existing simultaneously in the same sample. The contributions of the three different uranium redox states are quantified with the iterative transformation factor analysis (ITFA) method. U L 3 XAS and transmission electron microscopy (TEM) reveal that initially sorbed U(VI) species recrystallize to nonstoichiometric UO 2+x nanoparticles within 147 days when stored under anoxic conditions. These U(IV) species oxidize again when exposed to air. U M 4 HR-XANES data demonstrate strong contribution of U(V) at day 10 and that U(V) remains stable over 142 days under ambient conditions as shown for magnetite nanoparticles containing 1000 ppm U. U L 3 XAS indicates that this U(V) species is protected from oxidation likely incorporated into octahedral magnetite sites. XAS results are supported by density functional theory (DFT) calculations. Further characterization of the samples include powder X-ray diffraction (pXRD), scanning electron microscopy (SEM) and Fe 2p X-ray photoelectron spectroscopy (XPS).

Formation and Geological Sequestration of Uranium Nanoparticles in Deep Granitic Aquifer

PubMed Central

Suzuki, Yohey; Mukai, Hiroki; Ishimura, Toyoho; Yokoyama, Takaomi D.; Sakata, Shuhei; Hirata, Takafumi; Iwatsuki, Teruki; Mizuno, Takashi

2016-01-01

The stimulation of bacterial activities that convert hexavalent uranium, U(VI), to tetravalent uranium, U(IV), appears to be feasible for cost-effective remediation of contaminated aquifers. However, U(VI) reduction typically results in the precipitation of U(IV) particles less than 5 nanometers in diameter, except for environmental conditions enriched with iron. Because these tiny particles are mobile and susceptible to oxidative dissolution after the termination of nutrient injection, in situ bioremediation remains to be impractical. Here we show that U(IV) nanoparticles of coffinite (U(SiO4)1−x(OH)4x) formed in fracture-filling calcium carbonate in a granitic aquifer. In situ U-Pb isotope dating demonstrates that U(IV) nanoparticles have been sequestered in the calcium carbonate for at least 1 million years. As the microbiologically induced precipitation of calcium carbonate in aquifer systems worldwide is extremely common, we anticipate simultaneous stimulation of microbial activities for precipitation reactions of calcium carbonate and U(IV) nanoparticles, which leads to long-term sequestration of uranium and other radionuclides in contaminated aquifers and deep geological repositories. PMID:26948389

Formation and Geological Sequestration of Uranium Nanoparticles in Deep Granitic Aquifer.

PubMed

Suzuki, Yohey; Mukai, Hiroki; Ishimura, Toyoho; Yokoyama, Takaomi D; Sakata, Shuhei; Hirata, Takafumi; Iwatsuki, Teruki; Mizuno, Takashi

2016-03-07

The stimulation of bacterial activities that convert hexavalent uranium, U(VI), to tetravalent uranium, U(IV), appears to be feasible for cost-effective remediation of contaminated aquifers. However, U(VI) reduction typically results in the precipitation of U(IV) particles less than 5 nanometers in diameter, except for environmental conditions enriched with iron. Because these tiny particles are mobile and susceptible to oxidative dissolution after the termination of nutrient injection, in situ bioremediation remains to be impractical. Here we show that U(IV) nanoparticles of coffinite (U(SiO4)1-x(OH)4x) formed in fracture-filling calcium carbonate in a granitic aquifer. In situ U-Pb isotope dating demonstrates that U(IV) nanoparticles have been sequestered in the calcium carbonate for at least 1 million years. As the microbiologically induced precipitation of calcium carbonate in aquifer systems worldwide is extremely common, we anticipate simultaneous stimulation of microbial activities for precipitation reactions of calcium carbonate and U(IV) nanoparticles, which leads to long-term sequestration of uranium and other radionuclides in contaminated aquifers and deep geological repositories.

U-Zr alloy: XPS and TEM study of surface passivation

NASA Astrophysics Data System (ADS)

Paukov, M.; Tkach, I.; Huber, F.; Gouder, T.; Cieslar, M.; Drozdenko, D.; Minarik, P.; Havela, L.

2018-05-01

Surface reactivity of Uranium metal is an important factor limiting its practical applications. Bcc alloys of U with various transition metals are much less reactive than pure Uranium. So as to specify the mechanism of surface protection, we have been studying the U-20 at.% Zr alloy by photoelectron spectroscopy and transmission electron microscopy. The surface was studied in as-obtained state, in various stages of surface cleaning, and during an isochronal annealing cycle. The analysis based on U-4f, Zr-3p, and O-1 s spectra shows that a Zr-rich phase segregates at the surface at temperatures exceeding 550 K, which provides a self-assembled coating. The comparison of oxygen exposure of the stoichiometric and coated surfaces shows that the coating is efficiently preventing the oxidation of uranium even at elevated temperatures. The coating can be associated with the UZr2+x phase. TEM study indicated that the coating is about 20 nm thick. For the clean state, the U-4f core-level lines of the bcc alloy are practically identical to those of α-U, revealing similar delocalization of the 5f electronic states.

A model of early formation of uranium molecular oxides in laser-ablated plasmas

DOE Office of Scientific and Technical Information (OSTI.GOV)

Finko, Mikhail S.; Curreli, Davide; Weisz, David G.

Here, in this work, we present a newly constructed U xO y reaction mechanism that consists of 30 reaction channels (21 of which are reversible channels) for 11 uranium molecular species (including ions). Both the selection of reaction channels and calculation of corresponding rate coefficients is accomplished via a comprehensive literature review and application of basic reaction rate theory. The reaction mechanism is supplemented by a detailed description of oxygen plasma chemistry (19 species and 142 reaction channels) and is used to model an atmospheric laser ablated uranium plume via a 0D (global) model. Finally, the global model is usedmore » to analyze the evolution of key uranium molecular species predicted by the reaction mechanism, and the initial stage of formation of uranium oxide species.« less

A model of early formation of uranium molecular oxides in laser-ablated plasmas

DOE PAGES

Finko, Mikhail S.; Curreli, Davide; Weisz, David G.; ...

2017-10-12

Here, in this work, we present a newly constructed U xO y reaction mechanism that consists of 30 reaction channels (21 of which are reversible channels) for 11 uranium molecular species (including ions). Both the selection of reaction channels and calculation of corresponding rate coefficients is accomplished via a comprehensive literature review and application of basic reaction rate theory. The reaction mechanism is supplemented by a detailed description of oxygen plasma chemistry (19 species and 142 reaction channels) and is used to model an atmospheric laser ablated uranium plume via a 0D (global) model. Finally, the global model is usedmore » to analyze the evolution of key uranium molecular species predicted by the reaction mechanism, and the initial stage of formation of uranium oxide species.« less

Electrochemical separation of uranium in the molten system LiF-NaF-KF-UF4

NASA Astrophysics Data System (ADS)

Korenko, M.; Straka, M.; Szatmáry, L.; Ambrová, M.; Uhlíř, J.

2013-09-01

This article is focused on the electrochemical investigation (cyclic voltammetry and related studies) of possible reduction of U4+ ions to metal uranium in the molten system LiF-NaF-KF(eut.)-UF4 that can provide basis for the electrochemical extraction of uranium from molten salts. Two-step reduction mechanism for U4+ ions involving one electron exchange in soluble/soluble U4+/U3+ system and three electrons exchange in the second step were found on the nickel working electrode. Both steps were found to be reversible and diffusion controlled. Based on cyclic voltammetry, the diffusion coefficients of uranium ions at 530 °C were found to be D(U4+) = 1.64 × 10-5 cm2 s-1 and D(U3+) 1.76 × 10-5 cm2 s-1. Usage of the nickel spiral electrode for electrorefining of uranium showed fairly good feasibility of its extraction. However some oxidant present during the process of electrorefining caused that the solid deposits contained different uranium species such as UF3, UO2 and K3UO2F5.

Oxygen potential of (U 0.88Pu 0.12)O 2±x and (U 0.7Pu 0.3)O 2±x at high temperatures of 1673-1873 K

NASA Astrophysics Data System (ADS)

Kato, M.; Takeuchi, K.; Uchida, T.; Sunaoshi, T.; Konashi, K.

2011-07-01

The oxygen potential of (U 0.88Pu 0.12)O 2±x (-0.0119 < x < 0.0408) and (U 0.7Pu 0.3)O 2±x (-0.0363 < x < 0.0288) was measured at high temperatures of 1673-1873 K using gas equilibrium method with thermo gravimeter. The measured data were analyzed by a defect chemistry model. Expressions were derived to represent the oxygen potential based on defect chemistry as functions of temperature and oxygen-to-metal ratio. The thermodynamic data, ΔG, ΔH and ΔS, at stoichiometric composition were obtained. The expressions can be used for in situ determination of the oxygen-to-metal ratio by the gas-equilibration method. The calculation results were consistent with measured data. It was estimated that addition of 1 wt.% Pu content increased oxygen potential of uranium and plutonium mixed oxide by 2-5 kJ/mol.

High frequency EMI sensing for estimating depleted uranium radiation levels in soil

NASA Astrophysics Data System (ADS)

Shubitidze, Fridon; Barrowes, Benjamin E.; Ballard, John; Unz, Ron; Randle, Adam; Larson, Steve L.; O'Neill, Kevin A.

2018-04-01

This paper studies high (100 kHz up to 15 MHz) frequency electromagnetic responses (HFEMI) for DU metallic pieces and DU contaminated soils and derives a simple empirical expression from the measured HFEMI data for estimating DU contamination levels in soil. Depleted uranium (DU) is the byproduct of uranium enrichment and contains 33% less radioactive isotopes than natural uranium. There are at least thirty facilities at fourteen separate locations in the US, where munitions containing DU have been evaluated or used for training. At these sites, which vary in size, evaluation studies have been conducted with and without catch boxes. In addition, the DoD used DU at open firing ranges as large as thousands of acres (hundreds of hectares), for both artillery and aircraft training. These activities have left a legacy of DU contamination. Currently at military sites where DU munitions have been or are being used, cleanup activities mainly are done by excavating and shipping large volumes of site soil and berm materials to a hazardous material radiation disposal site. This approach is very time consuming, costly, and associated with the potential for exposure of personnel performing excavation and transportation. It also limits range use during the operation. So, there is an urgent need for technologies for rapid surveying of large areas to detect, locate, and removal of DU contaminants at test sites. Additionally, the technologies are needed to detect material at a depth of at least 30 cm as well as discriminate between DU metals and oxides from natural uranium and from other conductive metals such as natural and man-made range clutter. One of the potential technologies for estimating DU radiation levels in soils is HFEMI sensing. In this paper, HFEMI signals are collected for DU metal pieces, sodium diunarate (Na2U2 O3) and tri-uranium octoxide (U3O8). The EMI signal's sensitivity with respect to DU material composition and conditions are illustrated and analyzed. A new scheme for extracting near-surface soil's EM parameters is formulated.

Expanding the Chemistry of Actinide Metallocene Bromides. Synthesis, Properties and Molecular Structures of the Tetravalent and Trivalent Uranium Bromide Complexes: (C 5Me 4R) 2UBr 2, (C 5Me 4R) 2U(O-2,6- iPr 2C 6H 3)(Br), and [K(THF)][(C 5Me 4R) 2UBr 2] (R = Me, Et)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lichtscheidl, Alejandro Gaston; Pagano, Justin K.; Scott, Brian Lindley

The organometallic uranium species (C 5Me 4R) 2UBr 2 (R = Me, Et) were obtained by treating their chloride analogues (C 5Me 4R) 2UCl 2 (R = Me, Et) with Me 3SiBr. Treatment of (C 5Me 4R) 2UCl 2 and (C 5Me 4R) 2UBr 2 (R = Me, Et) with K(O-2,6- iPr 2C 6H 3) afforded the halide aryloxide mixed-ligand complexes (C 5Me 4R) 2U(O-2,6- iPr 2C 6H 3)(X) (R = Me, Et; X = Cl, Br). Complexes (C 5Me 4R) 2U(O-2,6- iPr 2C 6H 3)(Br) (R = Me, Et) can also be synthesized by treating (C 5Me 4R) 2U(O-2,6-more » iPr 2C 6H 3)(Cl) (R = Me, Et) with Me 3SiBr, respectively. Reduction of (C 5Me 4R) 2UCl 2 and (C 5Me 4R) 2UBr 2 (R = Me, Et) with KC 8 led to isolation of uranium(III) “ate” species [K(THF)][(C 5Me 5) 2UX 2] (X = Cl, Br) and [K(THF) 0.5][(C 5Me 4Et) 2UX 2] (X = Cl, Br), which can be converted to the neutral complexes (C 5Me 4R) 2U[N(SiMe 3) 2] (R = Me, Et). Analyses by nuclear magnetic resonance spectroscopy, X-ray crystallography, and elemental analysis are also presented.« less

Expanding the Chemistry of Actinide Metallocene Bromides. Synthesis, Properties and Molecular Structures of the Tetravalent and Trivalent Uranium Bromide Complexes: (C 5Me 4R) 2UBr 2, (C 5Me 4R) 2U(O-2,6- iPr 2C 6H 3)(Br), and [K(THF)][(C 5Me 4R) 2UBr 2] (R = Me, Et)

DOE PAGES

Lichtscheidl, Alejandro Gaston; Pagano, Justin K.; Scott, Brian Lindley; ...

2016-01-06

The organometallic uranium species (C 5Me 4R) 2UBr 2 (R = Me, Et) were obtained by treating their chloride analogues (C 5Me 4R) 2UCl 2 (R = Me, Et) with Me 3SiBr. Treatment of (C 5Me 4R) 2UCl 2 and (C 5Me 4R) 2UBr 2 (R = Me, Et) with K(O-2,6- iPr 2C 6H 3) afforded the halide aryloxide mixed-ligand complexes (C 5Me 4R) 2U(O-2,6- iPr 2C 6H 3)(X) (R = Me, Et; X = Cl, Br). Complexes (C 5Me 4R) 2U(O-2,6- iPr 2C 6H 3)(Br) (R = Me, Et) can also be synthesized by treating (C 5Me 4R) 2U(O-2,6-more » iPr 2C 6H 3)(Cl) (R = Me, Et) with Me 3SiBr, respectively. Reduction of (C 5Me 4R) 2UCl 2 and (C 5Me 4R) 2UBr 2 (R = Me, Et) with KC 8 led to isolation of uranium(III) “ate” species [K(THF)][(C 5Me 5) 2UX 2] (X = Cl, Br) and [K(THF) 0.5][(C 5Me 4Et) 2UX 2] (X = Cl, Br), which can be converted to the neutral complexes (C 5Me 4R) 2U[N(SiMe 3) 2] (R = Me, Et). Analyses by nuclear magnetic resonance spectroscopy, X-ray crystallography, and elemental analysis are also presented.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bi, G.; Liu, C.; Si, S.

This paper was focused on core design, neutronics evaluation and fuel cycle analysis for Thorium-Uranium Breeding Recycle in current PWRs, without any major change to the fuel lattice and the core internals, but substituting the UOX pellet with Thorium-based pellet. The fuel cycle analysis indicates that Thorium-Uranium Breeding Recycle is technically feasible in current PWRs. A 4-loop, 193-assembly PWR core utilizing 17 x 17 fuel assemblies (FAs) was taken as the model core. Two mixed cores were investigated respectively loaded with mixed reactor grade Plutonium-Thorium (PuThOX) FAs and mixed reactor grade {sup 233}U-Thorium (U{sub 3}ThOX) FAs on the basis ofmore » reference full Uranium oxide (UOX) equilibrium-cycle core. The UOX/PuThOX mixed core consists of 121 UOX FAs and 72 PuThOX FAs. The reactor grade {sup 233}U extracted from burnt PuThOX fuel was used to fabrication of U{sub 3}ThOX for starting Thorium-. Uranium breeding recycle. In UOX/U{sub 3}ThOX mixed core, the well designed U{sub 3}ThOX FAs with 1.94 w/o fissile uranium (mainly {sup 233}U) were located on the periphery of core as a blanket region. U{sub 3}ThOX FAs remained in-core for 6 cycles with the discharged burnup achieving 28 GWD/tHM. Compared with initially loading, the fissile material inventory in U{sub 3}ThOX fuel has increased by 7% via 1-year cooling after discharge. 157 UOX fuel assemblies were located in the inner of UOX/U{sub 3}ThOX mixed core refueling with 64 FAs at each cycle. The designed UOX/PuThOX and UOX/U{sub 3}ThOX mixed core satisfied related nuclear design criteria. The full core performance analyses have shown that mixed core with PuThOX loading has similar impacts as MOX on several neutronic characteristic parameters, such as reduced differential boron worth, higher critical boron concentration, more negative moderator temperature coefficient, reduced control rod worth, reduced shutdown margin, etc.; while mixed core with U{sub 3}ThOX loading on the periphery of core has no visible impacts on neutronic characteristics compared with reference full UOX core. The fuel cycle analysis has shown that {sup 233}U mono-recycling with U{sub 3}ThOX fuel could save 13% of natural uranium resource compared with UOX once through fuel cycle, slightly more than that of Plutonium single-recycling with MOX fuel. If {sup 233}U multi-recycling with U{sub 3}ThOX fuel is implemented, more natural uranium resource would be saved. (authors)« less

Trace metal assay of U(3)O(8) powder by electrothermal AAS.

PubMed

Page, A G; Godbole, S V; Kulkarni, M J; Porwal, N K; Shelar, S S; Joshi, B D

1983-10-01

Methods have been developed for the direct determination of Ag, Ca, K., Li, Mg, Na, Pb, Sn and Zn in U(3)O(8) powder samples by electrothermal AAS. Nanogram and lower amounts of these elements have been determined with a relative standard deviation of 6-16% in mg amounts of sample (either alone or mixed with an equal weight of graphite). The results for NBL reference samples were in reasonable agreement with the certified values. X-Ray diffraction studies on the residues left from the graphite mixtures after the atomization cycle, confirmed the formation of uranium carbide (UC(2)).

Direct electrochemical reduction of solid uranium oxide in molten fluoride salts

NASA Astrophysics Data System (ADS)

Gibilaro, Mathieu; Cassayre, Laurent; Lemoine, Olivier; Massot, Laurent; Dugne, Olivier; Malmbeck, Rikard; Chamelot, Pierre

2011-07-01

The direct electrochemical reduction of UO 2 solid pellets was carried out in LiF-CaF 2 (+2 mass.% Li 2O) at 850 °C. An inert gold anode was used instead of the usual reactive sacrificial carbon anode. In this case, oxidation of oxide ions present in the melt yields O 2 gas evolution on the anode. Electrochemical characterisations of UO 2 pellets were performed by linear sweep voltammetry at 10 mV/s and reduction waves associated to oxide direct reduction were observed at a potential 150 mV more positive in comparison to the solvent reduction. Subsequent, galvanostatic electrolyses runs were carried out and products were characterised by SEM-EDX, EPMA/WDS, XRD and microhardness measurements. In one of the runs, uranium oxide was partially reduced and three phases were observed: nonreduced UO 2 in the centre, pure metallic uranium on the external layer and an intermediate phase representing the initial stage of reduction taking place at the grain boundaries. In another run, the UO 2 sample was fully reduced. Due to oxygen removal, the U matrix had a typical coral-like structure which is characteristic of the pattern observed after the electroreduction of solid oxides.

Redox behavior of uranium at the nanoporous aluminum oxide-water interface: implications for uranium remediation.

PubMed

Jung, Hun Bok; Boyanov, Maxim I; Konishi, Hiromi; Sun, Yubing; Mishra, Bhoopesh; Kemner, Kenneth M; Roden, Eric E; Xu, Huifang

2012-07-03

Sorption-desorption experiments show that the majority (ca. 80-90%) of U(VI) presorbed to mesoporous and nanoporous alumina could not be released by extended (2 week) extraction with 50 mM NaHCO(3) in contrast with non-nanoporous α alumina. The extent of reduction of U(VI) presorbed to aluminum oxides was semiquantitatively estimated by comparing the percentages of uranium desorbed by anoxic sodium bicarbonate between AH(2)DS-reacted and unreacted control samples. X-ray absorption spectroscopy confirmed that U(VI) presorbed to non-nanoporous alumina was rapidly and completely reduced to nanoparticulate uraninite by AH(2)DS, whereas reduction of U(VI) presorbed to nanoporous alumina was slow and incomplete (<5% reduction after 1 week). The observed nanopore size-dependent redox behavior of U has important implications in developing efficient remediation techniques for the subsurface uranium contamination because the efficiency of in situ bioremediation depends on how effectively and rapidly U(VI) bound to sediment or soil can be converted to an immobile phase.

Paleontological analysis of a lacustrine carbonaceous uranium deposit at the Anderson mine, Date Creek basin, west-central Arizona (U.S.A.)

USGS Publications Warehouse

Otton, J.K.; Bradbury, J.P.; Forester, R.M.; Hanley, J.H.

1990-01-01

The Tertiary sedimentary sequence of the Date Creek basin area of Arizona is composed principally of intertonguing alluvial-fan and lacustrine deposits. The lacustrine rocks contain large intermediate- to, locally, high-grade uranium deposits that form one of the largest uranium resources in the United States (an estimated 670,000 tons of U3O8 at an average grade of 0.023% is indicated by drilling to date). At the Anderson mine, about 50,000 tons of U3O8 occurs in lacustrine carbonaceous siltstones and mudstones (using a cutoff grade of 0.01%). The Anderson mine constitutes a new class of ore deposit, a lacustrine carbonaceous uranium deposit. Floral and faunal remains at the Anderson mine played a critical role in creating and documenting conditions necessary for uranium mineralization. Organic-rich, uraniferous rocks at the Anderson mine contain plant remains and ostracodes having remarkably detailed preservation of internal features because of infilling by opaline silica. This preservation suggests that the alkaline lake waters in the mine area contained high concentrations of dissolved silica and that silicification occurred rapidly, before compaction or cementation of the enclosing sediment. Uranium coprecipitated with the silica. Thinly laminated, dark-colored, siliceous beds contain centric diatoms preserved with carbonaceous material suggesting that lake waters at the mine were locally deep and anoxic. These alkaline, silica-charged waters and a stagnant, anoxic environment in parts of the lake were necessary conditions for the precipitation of large amounts of uranium in the lake-bottom sediments. Sediments at the Anderson mine contain plant remains and pollen that were derived from diverse vegetative zones suggesting about 1500 m of relief in the area at the time of deposition. The pollen suggests that the valley floor was semiarid and subtropical, whereas nearby mountains supported temperate deciduous forests. ?? 1990.

DISPERSION HARDENING OF URANIUM METAL

DOEpatents

Arbiter, W.

1963-01-15

A method of hardening U metal involves the forming of a fine dispersion of UO/sub 2/. This method consists of first hydriding the U to form a finely divided powder and then exposing the powder to a very dilute O gas in an inert atmosphere under such pressure and temperature conditions as to cause a thin oxide film to coat each particle of the U hydride, The oxide skin prevents agglomeration of the particles as the remaining H is removed, thus preserving the small particle size. The oxide skin coatings remain as an oxide dispersion. The resulting product may be workhardened to improve its physical characteristics. (AEC)

Microbially catalyzed nitrate-dependent metal/radionuclide oxidation in shallow subsurface sediments

NASA Astrophysics Data System (ADS)

Weber, K.; Healy, O.; Spanbauer, T. L.; Snow, D. D.

2011-12-01

Anaerobic, microbially catalyzed nitrate-dependent metal/radionuclide oxidation has been demonstrated in a variety of sediments, soils, and groundwater. To date, studies evaluating U bio-oxidation and mobilization have primarily focused on anthropogenically U contaminated sites. In the Platte River Basin U originating from weathering of uranium-rich igneous rocks in the Rocky Mountains was deposited in shallow alluvial sediments as insoluble reduced uranium minerals. These reduced U minerals are subject to reoxidation by available oxidants, such nitrate, in situ. Soluble uranium (U) from natural sources is a recognized contaminant in public water supplies throughout the state of Nebraska and Colorado. Here we evaluate the potential of anaerobic, nitrate-dependent microbially catalyzed metal/radionuclide oxidation in subsurface sediments near Alda, NE. Subsurface sediments and groundwater (20-64ft.) were collected from a shallow aquifer containing nitrate (from fertilizer) and natural iron and uranium. The reduction potential revealed a reduced environment and was confirmed by the presence of Fe(II) and U(IV) in sediments. Although sediments were reduced, nitrate persisted in the groundwater. Nitrate concentrations decreased, 38 mg/L to 30 mg/L, with increasing concentrations of Fe(II) and U(IV). Dissolved U, primarily as U(VI), increased with depth, 30.3 μg/L to 302 μg/L. Analysis of sequentially extracted U(VI) and U(IV) revealed that virtually all U in sediments existed as U(IV). The presence of U(IV) is consistent with reduced Fe (Fe(II)) and low reduction potential. The increase in aqueous U concentrations with depth suggests active U cycling may occur at this site. Tetravalent U (U(IV)) phases are stable in reduced environments, however the input of an oxidant such as oxygen or nitrate into these systems would result in oxidation. Thus co-occurrence of nitrate suggests that nitrate could be used by bacteria as a U(IV) oxidant. Most probable number enumeration of nitrate-dependent U(IV) oxidizing microorganisms demonstrated an abundant community ranging from 1.61x104 to 2.74x104 cells g-1 sediment. Enrichments initiated verified microbial U reduction and U oxidation coupled to nitrate reduction. Sediment slurries were serially diluted and incubated over a period of eight weeks and compared to uninoculated controls. Oxidation (0-4,554 μg/L) and reduction (0-55 μg/L) of U exceeded uninoculated controls further providing evidence of a U biogeochemical cycling in these subsurface sediments. The oxidation of U(IV) could contribute to U mobilization in the groundwater and result in decreased water quality. Not only could nitrate serve as an oxidant, but Fe(III) could also contribute to U mobilization. Nitrate-dependent Fe(II) oxidation is an environmentally ubiquitous process facilitated by a diversity of microorganisms. Additional research is necessary in order to establish a role of biogenic Fe(III) oxides in U geochemical cycling at this site. These microbially mediated processes could also have a confounding effect on uranium mobility in subsurface environments.

In-situ evidence for uranium immobilization and remobilization

USGS Publications Warehouse

Senko, John M.; Istok, Jonathan D.; Suflita, Joseph M.; Krumholz, Lee R.

2002-01-01

The in-situ microbial reduction and immobilization of uranium was assessed as a means of preventing the migration of this element in the terrestrial subsurface. Uranium immobilization (putatively identified as reduction) and microbial respiratory activities were evaluated in the presence of exogenous electron donors and acceptors with field push−pull tests using wells installed in an anoxic aquifer contaminated with landfill leachate. Uranium(VI) amended at 1.5 μM was reduced to less than 1 nM in groundwater in less than 8 d during all field experiments. Amendments of 0.5 mM sulfate or 5 mM nitrate slowed U(VI) immobilization and allowed for the recovery of 10% and 54% of the injected element, respectively, as compared to 4% in the unamended treatment. Laboratory incubations confirmed the field tests and showed that the majority of the U(VI) immobilized was due to microbial reduction. In these tests, nitrate treatment (7.5 mM) inhibited U(VI) reduction, and nitrite was transiently produced. Further push−pull tests were performed in which either 1 or 5 mM nitrate was added with 1.0 μM U(VI) to sediments that already contained immobilized uranium. After an initial loss of the amendments, the concentration of soluble U(VI) increased and eventually exceeded the injected concentration, indicating that previously immobilized uranium was remobilized as nitrate was reduced. Laboratory experiments using heat-inactivated sediment slurries suggested that the intermediates of dissimilatory nitrate reduction (denitrification or dissimilatory nitrate reduction to ammonia), nitrite, nitrous oxide, and nitric oxide were all capable of oxidizing and mobilizing U(IV). These findings indicate that in-situ subsurface U(VI) immobilization can be expected to take place under anaerobic conditions, but the permanence of the approach can be impaired by disimilatory nitrate reduction intermediates that can mobilize previously reduced uranium.

Investigating microstructural evolution during the electroreduction of UO2 to U in LiCl-KCl eutectic using focused ion beam tomography

NASA Astrophysics Data System (ADS)

Brown, L. D.; Abdulaziz, R.; Tjaden, B.; Inman, D.; Brett, D. J. L.; Shearing, P. R.

2016-11-01

Reprocessing of spent nuclear fuels using molten salt media is an attractive alternative to liquid-liquid extraction techniques. Pyroelectrochemical processing utilizes direct, selective, electrochemical reduction of uranium dioxide, followed by selective electroplating of a uranium metal. Thermodynamic prediction of the electrochemical reduction of UO2 to U in LiCl-KCl eutectic has shown to be a function of the oxide ion activity. The pO2- of the salt may be affected by the microstructure of the UO2 electrode. A uranium dioxide filled "micro-bucket" electrode has been partially electroreduced to uranium metal in molten lithium chloride-potassium chloride eutectic. This partial electroreduction resulted in two distinct microstructures: a dense UO2 and a porous U metal structure were characterised by energy dispersive X-ray spectroscopy. Focused ion beam tomography was performed on five regions of this electrode which revealed an overall porosity ranging from 17.36% at the outer edge to 3.91% towards the centre, commensurate with the expected extent of reaction in each location. The pore connectivity was also seen to reduce from 88.32% to 17.86% in the same regions and the tortuosity through the sample was modelled along the axis of propagation of the electroreduction, which was seen to increase from a value of 4.42 to a value of infinity (disconnected pores). These microstructural characteristics could impede the transport of O2- ions resulting in a change in the local pO2- which could result in the inability to perform the electroreduction.

Assessment of solid/liquid equilibria in the (U, Zr)O2+y system

NASA Astrophysics Data System (ADS)

Mastromarino, S.; Seibert, A.; Hashem, E.; Ciccioli, A.; Prieur, D.; Scheinost, A.; Stohr, S.; Lajarge, P.; Boshoven, J.; Robba, D.; Ernstberger, M.; Bottomley, D.; Manara, D.

2017-10-01

Solid/liquid equilibria in the system UO2sbnd ZrO2 are revisited in this work by laser heating coupled with fast optical thermometry. Phase transition points newly measured under inert gas are in fair agreement with the early measurements performed by Wisnyi et al., in 1957, the only study available in the literature on the whole pseudo-binary system. In addition, a minimum melting point is identified here for compositions near (U0.6Zr0.4)O2+y, around 2800 K. The solidus line is rather flat on a broad range of compositions around the minimum. It increases for compositions closer to the pure end members, up to the melting point of pure UO2 (3130 K) on one side and pure ZrO2 (2970 K) on the other. Solid state phase transitions (cubic-tetragonal-monoclinic) have also been observed in the ZrO2-rich compositions X-ray diffraction. Investigations under 0.3 MPa air (0.063 MPa O2) revealed a significant decrease in the melting points down to 2500 K-2600 K for increasing uranium content (x(UO2)> 0.2). This was found to be related to further oxidation of uranium dioxide, confirmed by X-ray absorption spectroscopy. For example, a typical oxidised corium composition U0.6Zr0.4O2.13 was observed to solidify at a temperature as low as 2493 K. The current results are important for assessing the thermal stability of the system fuel - cladding in an oxide based nuclear reactor, and for simulating the system behaviour during a hypothetical severe accident.

Immobilization of uranium into magnetite from aqueous solution by electrodepositing approach.

PubMed

Lu, Bing-Qing; Li, Mi; Zhang, Xiao-Wen; Huang, Chun-Mei; Wu, Xiao-Yan; Fang, Qi

2018-02-05

Immobilization of uranium into magnetite (Fe 3 O 4 ), which was generated from metallic iron by electrochemical method, was proposed to rapidly remove uranium from aqueous solution. The effects of electrochemical parameters such as electrode materials, voltage, electrode gap, reaction time and pH value on the crystallization of Fe 3 O 4 and uranium removal efficiencies were investigated. More than 90% uranium in the solution was precipitated with Fe 3 O 4 under laboratory conditions when uranium concentration range from 0.5mg/L to 10mg/L. The Fe 3 O 4 crystallization mechanism and immobilization of uranium was proved by XPS, XRD, TEM, FTIR and VSM methods. The results indicated that the cationic (including Fe 2+ , Fe 3+ and U(VI)) migrate to cathode side under the electric field and the uranium was incorporated or adsorbed by Fe 3 O 4 which was generated at cathode while the pH ranges between 2-7. The uranium-containing precipitate of Fe 3 O 4 can exist stably at the acid concentration below 60g/L. Furthermore, the precipitate may be used as valuable resources for uranium or iron recycling, which resulted in no secondary pollution in the removal of uranium from aqueous solution. Copyright © 2017. Published by Elsevier B.V.

Fabrication of (U,Am)O2 pellet with controlled porosity from oxide microspheres

NASA Astrophysics Data System (ADS)

Ramond, Laure; Coste, Philippe; Picart, Sébastien; Gauthé, Aurélie; Bataillea, Marc

2017-08-01

U1-xAmxO2±δ mixed-oxides are considered as promising compounds for americium heterogeneous transmutation in Sodium Fast Neutron Reactor. Porous microstructure is envisaged in order to facilitate helium and fission gas release and to reduce pellet swelling during irradiation and under self-irradiation. In this study, the porosity is created by reducing (U,Am)3O8 microspheres into (U,Am)O2 during the sintering. This reduction is accompanied by a decrease of the lattice volume that leads to the creation of open porosity. Finally, an (U0.90Am0.10)O2 porous ceramic pellet (D∼89% of the theoretical density TD) with controlled porosity (≥8% open porosity) was obtained from mixed-oxide microspheres obtained by the Weak Acid Resin (WAR) process.

Oxidation of UC: An in situ high temperature environmental scanning electron microscopy study

NASA Astrophysics Data System (ADS)

Gasparrini, Claudia; Podor, Renaud; Horlait, Denis; Rushton, Michael J. D.; Fiquet, Olivier; Lee, William Edward

2017-10-01

In situ HT-ESEM oxidation of sintered UC fragments revealed the morphological changes occurring during the transformation between UC to UO2 and UO2 to U3O8 at 723-848 K and in an atmosphere of 10-100 Pa O2. Two main oxidation pathways were revealed. Oxidation at 723 K in atmospheres ≤25 Pa O2 showed the transformation from UC to UO2+x, as confirmed by post mortem HRTEM analysis. This oxidation pathway was comprised of three steps: (i) an induction period, where only surface UC particles oxidised, (ii) a sample area expansion accompanied by crack formation and propagation, (iii) a stabilisation of the total crack length inferring that crack propagation had stopped. Samples oxidised under 50 Pa O2 at 723 K and at 773-848 K for 10-100 Pa O2 showed an "explosive" oxidation pathway: (i) sample area expansion occurred as soon as oxygen was inserted into the chamber and crack propagation and crack length followed an exponential law; (ii) cracks propagated as a network and the oxide layer fragmented, (iii) an "explosion" occurred causing a popcorn-like transformation, typical for oxidation from UO2 to U3O8. HRTEM characterisation revealed U3O8 preferentially grow in the [001] direction. The explosive growth, triggered by ignition of UC, proceeded as a self-propagating high-temperature synthesis reaction, with a propagation speed of 150-500 ± 50 μm/s.

Reduction of uranium by cytochrome c3 of Desulfovibrio vulgaris

USGS Publications Warehouse

Lovley, D.R.; Widman, P.K.; Woodward, J.C.; Phillips, E.J.P.

1993-01-01

The mechanism for U(VI) reduction by Desulfovibrio vulgaris (Hildenborough) was investigated. The H2-dependent U(VI) reductase activity in the soluble fraction of the cells was lost when the soluble fraction was passed over a cationic exchange column which extracted cytochrome c3. Addition of cytochrome c3 back to the soluble fraction that had been passed over the cationic exchange column restored the U(VI)-reducing capacity. Reduced cytochrome c3 was oxidized by U(VI), as was a c-type cytochrome(s) in whole-cell suspensions. When cytochrome c3 was combined with hydrogenase, its physiological electron donor, U(VI) was reduced in the presence of H2. Hydrogenase alone could not reduce U(VI). Rapid U(VI) reduction was followed by a subsequent slow precipitation of the U(IV) mineral uraninite. Cytochrome c3 reduced U(VI) in a uranium-contaminated surface water and groundwater. Cytochrome c3 provides the first enzyme model for the reduction and biomineralization of uranium in sedimentary environments. Furthermore, the finding that cytochrome c3 can catalyze the reductive precipitation of uranium may aid in the development of fixed-enzyme reactors and/or organisms with enhanced U(VI)-reducing capacity for the bioremediation of uranium- contaminated waters and waste streams.

Spectroscopic Evidence of Uranium Immobilization in Acidic ...

EPA Pesticide Factsheets

Biogeochemistry of uranium in wetlands plays important roles in U immobilization in storage ponds of U mining and processing facilities but has not been well understood. The objective of this work was to study molecular mechanisms responsible for high U retention by Savannah River Site (SRS) wetland sediments under varying redox and acidic (pH = 2.6-5.8) conditions using U L3-edge X-ray absorption spectroscopy. Uranium in the SRS wetland sediments existed primarily as U(VI) bonded as a bidentate to carboxylic sites (U-C bond distance at ~2.88 Å), rather than phenolic or other sites of natural organic matter (NOM). In microcosms simulating the SRS wetland process, U immobilization on roots was 2 orders of magnitude higher than on the adjacent brown or more distant white sands in which U was U(VI). Uranium on the roots were both U(IV) and U(VI), which were bonded as a bidentate to carbon, but the U(VI) may also form a U phosphate mineral. After 140 days of air exposure, all U(IV) was reoxidized to U(VI) but remained as a bidentate bonding to carbon. This study demonstrated NOM and plant roots can highly immobilize U(VI) in the SRS acidic sediments, which has significant implication on the long-term stewardship of U-contaminated wetlands. There were several former U processing facilities at the Savannah River Site (SRS), Aiken, SC. As a result of their operations, uranium has entered the surrounding environments. For example, approximately 45,000 kg o

Morphological Comparison of U3O8 Ore Concentrates from Canada Key Lake and Namibia Sources

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schwartz, Daniel S.; Tandon, Lav; Martinez, Patrick Thomas

Uranium ore concentrates from two different sources were examined using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The ore powders are referred to as Namibia (id. no. 90036, LIMS id. no. 18775) and Canada Key Lake (id. no. 90019, LIMS id. no. 18774). Earlier work identified the ores as the U₃O₈ phase of uranium oxide using x-ray diffraction. Both sets of powders were in the form of dark brown to black powder fines. However, the Canada Key Lake concentrates contained larger chunks of material on the millimeter scale that were easily visible to the unaided eye. The powdersmore » were mounted for SEM examination by hand dispersing a small amount onto conductive sticky tape. Two types of applicators were used and compared: a fine-tipped spatula and a foam-tipped applicator. The sticky tape was on a standard SEM “tee” mount, which was tapped to remove loose contamination before being inserted into the SEM.« less

Human exposure to natural uranium: A case history and analytical results from some postmortem tissues

PubMed Central

Donoghue, J. K.; Dyson, E. D.; Hislop, J. S.; Leach, A. M.; Spoor, N. L.

1972-01-01

Donoghue, J. K., Dyson, E. D., Hislop, J. S., Leach, A. M., and Spoor, N. L. (1972).Brit. J. industr. Med.,29, 81-89. Human exposure to natural uranium: a case history and analytical results from some postmortem tissues. After the collapse and sudden death of an employee who had worked for 10 years in a natural uranium workshop, in which the airborne uranium was largely U3O8 with an Activity Median Aerodynamic Diameter in the range 3·5-6·0 μm and average concentration of 300 μg/m3, his internal organs were analysed for uranium. The tissues examined included lungs (1041 g), pulmonary lymph nodes (12 g), sternum (114 g), and kidneys (217 g). Uranium was estimated by neutron activation analysis, using irradiated tissue ash, and counting the delayed neutrons from uranium-235. The concentrations of uranium (μg U/g wet tissue) in the lungs, lymph nodes, sternum, and kidneys were 1·2, 1·8, 0·09, and 0·14 respectively. The weights deposited in the lungs and lymph nodes are less than 1% of the amounts calculated from the environmental data using the parameters currently applied in radiological protection. The figures are compatible with those reported by Quigley, heartherton, and Ziegler in 1958 and by Meichen in 1962. The relation between these results, the environmental exposure data, and biological monitoring data is discussed in the context of current views on the metabolism of inhaled insoluble uranium. PMID:5060250

U(IV) chalcogenolates synthesized via oxidation of uranium metal by dichalcogenides.

PubMed

Gaunt, Andrew J; Scott, Brian L; Neu, Mary P

2006-09-04

Treatment of uranium metal with dichalcogenides in the presence of a catalytic amount of iodine in pyridine affords molecular U(IV) chalcogenolates that do not require stabilizing ancillary ligands. Oxidation of U(0) by PhEEPh yields monomeric seven-coordinate U(EPh)4(py)3 (E = S(1), Se(2)). The dimeric eight-coordinate complexes [U(EPh)2(mu2-EPh)2(CH3CN)2]2 (E = S(3), Se(4)) are obtained by crystallization from solutions of 1 and 2 dissolved in acetonitrile. Oxidation of U(0) by pySSpy and crystallization from thf yields nine-coordinate U(Spy)4(thf) (5). Incorporation of elemental selenium into the oxidation of U(0) by PhSeSePh results in the isolation of [U(py)2(SePh)(mu3-Se)(mu2-SePh)]4.4py (6), a tetrameric cluster in which each U(IV) ion is eight-coordinate and the U4Se4 core forms a distorted cube. The compounds were analyzed spectroscopically and the single-crystal X-ray structures of 1 and 3-6 were determined. The isolation of 1-6 represents six new examples of actinide chalcogenolates and allows insight into the nature of "hard" actinide ion-"soft" chalcogen donor interactions.

Synthesis and characterisation of the uranium pyrochlore betafite [(Ca,U)₂(Ti,Nb,Ta)₂O₇].

PubMed

McMaster, Scott A; Ram, Rahul; Charalambous, Fiona; Pownceby, Mark I; Tardio, James; Bhargava, Suresh K

2014-09-15

Betafite of composition [(Ca,U)2(Ti,Nb,Ta)2O7] was prepared via a solid state synthesis route. The synthesis was shown to be sensitive to initial reactant ratios, the atmosphere used (oxidising, neutral, reducing) and time. The optimum conditions for the synthesis of betafite were found to be heating the reactants required at 1150°C for 48 h under an inert gas atmosphere. XRD characterisation revealed that the synthesised betafite contained minor impurities. EPMA analysis of a sectioned surface showed very small regions of Ca-free betafite on grain boundaries as well as minor rutile impurities. Some heterogeneity between the Nb:Ta ratio was observed by quantitative EPMA but was generally within the nomenclature requirements stated for betafite. SEM analysis revealed the synthesised betafite was comprised mostly of hexaoctohedral crystals of ∼ 3 μm in diameter. XPS analysis of the sample showed that the uranium in the synthesised betafite was predominately present in the U(5+) oxidation state. A minor amount of U(6+) was also detected which was possibly due to surface oxidation. Copyright © 2014 Elsevier B.V. All rights reserved.

Theoretical Estimate of Maximum Possible Nuclear Explosion

DOE R&D Accomplishments Database

Bethe, H. A.

1950-01-31

The maximum nuclear accident which could occur in a Na-cooled, Be moderated, Pu and power producing reactor is estimated theoretically. (T.R.H.) 2O82 Results of nuclear calculations for a variety of compositions of fast, heterogeneous, sodium-cooled, U-235-fueled, plutonium- and power-producing reactors are reported. Core compositions typical of plate-, pin-, or wire-type fuel elements and with uranium as metal, alloy, and oxide were considered. These compositions included atom ratios in the following range: U-23B to U-235 from 2 to 8; sodium to U-235 from 1.5 to 12; iron to U-235 from 5 to 18; and vanadium to U-235 from 11 to 33. Calculations were performed to determine the effect of lead and iron reflectors between the core and blanket. Both natural and depleted uranium were evaluated as the blanket fertile material. Reactors were compared on a basis of conversion ratio, specific power, and the product of both. The calculated results are in general agreement with the experimental results from fast reactor assemblies. An analysis of the effect of new cross-section values as they became available is included. (auth)

Managing the Nuclear Fuel Cycle: Policy Implications of Expanding Global Access to Nuclear Power

DTIC Science & Technology

2008-01-20

critical aspect of the nuclear fuel cycle for the United States, where longstanding nonproliferation policy discouraged commercial nuclear fuel...have U.S. government officials. However, the case of Iran raises perhaps the most critical question in this decade for strengthening the nuclear...slight difference in atomic mass between 235U and 238U. The typical enrichment process requires about 10 lbs of uranium U3O8 to produce 1 lb of low

A procedure for quantitation of total oxidized uranium for bioremediation studies

USGS Publications Warehouse

Elias, Dwayne A.; Senko, John M.; Krumholz, Lee R.

2003-01-01

A procedure was developed for the quantitation of complexed U(VI) during studies on U(VI) bioremediation. These studies typically involve conversion of soluble or complexed U(VI) (oxidized) to U(IV) (the reduced form which is much less soluble). Since U(VI) freely exchanges between material adsorbed to the solid phase and the dissolved phase, uranium bioremediation experiments require a mass balance of U in both its soluble and adsorbed forms as well as in the reduced sediment bound phase. We set out to optimize a procedure for extraction and quantitation of sediment bound U(VI). Various extractant volumes to sediment ratios were tested and it was found that between 1:1 to 8:1 ratios (v/w) there was a steady increase in U(VI) recovered, but no change with further increases in v/w ratio.Various strengths of NaHCO3, Na-EDTA, and Na-citrate were used to evaluate complexed U(VI) recovery, while the efficiency of a single versus repeated extraction steps was compared with synthesized uranyl-phosphate and uranyl-hydroxide. Total recovery with 1 M NaHCO3 was 95.7% and 97.9% from uranyl-phosphate and uranyl-hydroxide, respectively, compared to 80.7% and 89.9% using 450 mM NaHCO3. Performing the procedure once yielded an efficiency of 81.1% and 92.3% for uranyl-phosphate and uranyl-hydroxide, respectively, as compared to three times. All other extractants yielded 7.9–82.0% in both experiments.

Infrared spectroscopy of extreme coordination: the carbonyls of U(+) and UO(2)(+).

PubMed

Ricks, Allen M; Gagliardi, Laura; Duncan, Michael A

2010-11-17

Uranium and uranium dioxide carbonyl cations produced by laser vaporization are studied with mass-selected ion infrared spectroscopy in the C-O stretching region. Dissociation patterns, spectra, and quantum chemical calculations establish that the fully coordinated ions are U(CO)(8)(+) and UO(2)(CO)(5)(+), with D(4d) square antiprism and D(5h) pentagonal bipyramid structures. Back-bonding in U(CO)(8)(+) causes a red-shifted CO stretch, but back-donation is inefficient for UO(2)(CO)(5)(+), producing a blue-shifted CO stretch characteristic of nonclassical carbonyls.

Uranium and radon in ground water in the lower Illinois River basin

USGS Publications Warehouse

Morrow, William S.

2001-01-01

Uranium and radon are present in ground water throughout the United States, along with other naturally occurring radionuclides. The occurrence and distribution of uranium and radon are of concern because these radionuclides are carcinogens that can be ingested through drinking water. As part of the U.S. Geological Survey (USGS) National Water-Quality Assessment (NAWQA) program, water samples were collected and analyzed for uranium and radon from 117 wells in four aquifers in the lower Illinois River Basin (LIRB) from 1996 to 1997. The aquifers were the shallow glacial drift deposits of the Bloomington Ridged Plain (BRP) not overlying a buried bedrock valley (BRP N/O BV), shallow glacial drift deposits of the BRP overlying the Mahomet Buried Bedrock Valley (BRP O/L MBBV), shallow glacial drift deposits of the Galesburg/Springfield Plain not overlying a buried bedrock valley (GSP N/O BV), and the deep glacial drift deposits of the Mahomet Buried Bedrock Valley (MBBV). Uranium was detected in water samples from all aquifers except the MBBV and ranged in concentration from less than 1 microgram per liter ( ? g/L) to 17 ? g/L. Uranium concentrations did not exceed 20 ? g/L, the proposed U.S. Environmental Protection Agency (USEPA) Maximum Contaminant Level (MCL) at the time of sampling (1996?97). The current (2001) promulgated MCL is 30 ? g/L (U.S. Environmental Protection Agency, 2000). The highest median uranium concentration (2.0 ? g/L) among the four aquifers was in the BRP N/O BV. Uranium most often occurred in oxidizing and sulfate-rich water. Radon was detected in water samples from all aquifers in the LIRB. Radon concentrations in all aquifers ranged from less than 80 picocuries per liter (pCi/L) to 1,300 pCi/L. Of 117 samples, radon concentrations exceeded 300 pCi/L (the proposed USEPA MCL) in 34 percent of the samples. Radon concentrations exceeded 300 pCi/L in more than one-half of the samples from the GSP N/O BV and the BRP O/L MBBV. No sample exceeded the proposed Alternative Maximum Contaminant Level (AMCL) of 4,000 pCi/L. Concentrations of uranium and radon were not correlated.

Oxygen potential of uranium--plutonium oxide as determined by controlled- atmosphere thermogravimetry

DOE Office of Scientific and Technical Information (OSTI.GOV)

Swanson, Gerald C.

1975-10-01

The oxygen-to-metal atom ratio, or O/M, of solid solution uranium- plutonium oxide reactor fuel is a measure of the concentration of crystal defects in the oxide which affect many fuel properties, particularly, fuel oxygen potential. Fabrication of a high-temperature oxygen electrode, employing an electro-active tip of oxygen-deficient solid-state electrolyte, intended to confirm gaseous oxygen potentials is described. Uranium oxide and plutonium oxide O/M reference materials were prepared by in situ oxidation of high purity metals in the thermobalance. A solid solution uranium-plutonium oxide O/M reference material was prepared by alloying the uranium and plutonium metals in a yttrium oxide cruciblemore » at 1200°C and oxidizing with moist He at 250°C. The individual and solid solution oxides were isothermally equilibrated with controlled oxygen potentials between 800 and 1300°C and the equilibrated O/ M ratios calculated with corrections for impurities and buoyancy effects. Use of a reference oxygen potential of -100 kcal/mol to produce an O/M of 2.000 is confirmed by these results. However, because of the lengthy equilibration times required for all oxides, use of the O/M reference materials rather than a reference oxygen potential is recommended for O/M analysis methods calibrations.« less

Early Jurassic mafic dykes from the Aigao uranium ore deposit in South China: Geochronology, petrogenesis and relationship with uranium mineralization

NASA Astrophysics Data System (ADS)

Zhang, Di; Zhao, Kui-Dong; Chen, Wei; Jiang, Shao-Yong

2018-05-01

Mafic dykes are abundant and widely distributed in many granite-hosted uranium ore deposits in South China. However, their geochronology, petrogenesis and relationship with uranium mineralization were poorly constrained. In this study, apatite U-Pb dating, whole-rock major and trace element and Sr-Nd-Pb isotope analysis were conducted for the dolerite dykes from the Aigao uranium ore deposit. Apatite U-Pb isotopic data indicate that the mafic dykes were emplaced at Early Jurassic (189 ± 4 Ma), which provides new evidence for the rarely identified Early Jurassic magmatism in South China. Pyroxene from the dykes is mainly augite, and plagioclase belongs to albite. The dolerite samples have relatively low SiO2 contents (45.33-46.79 wt%), relatively high total alkali contents (K2O + Na2O = 4.11-4.58 wt%) and Al2O3 contents (13.39-13.80 wt%), and medium MgO contents (4.29-5.16 wt%). They are enriched in Nb, Ta, Ti, rare earth elements and depleted in Rb, K, Sr, Th, showing the typical OIB-like geochemical affinity. All the dolerite samples show homogeneous Sr-Nd-Pb isotopic compositions, with (87Sr/86Sr)i varying from 0.706049 to 0.707137, εNd(t) from +4.6 to +5.2, 206Pb/204Pb from 19.032 to 19.126 and 207Pb/204Pb from 15.641 to 15.653. The mafic dykes in the Aigao deposit should be derived from the partial melting of the asthenospheric mantle and formed in a within-plate extensional environment. The emplacement age of the mafic dykes is older than the uranium mineralization age. Therefore, CO2 in ore-forming fluids couldn't originate from the basaltic magma as suggested by previous studies. The dolerite dykes might only provide a favorable reducing environment to promote the precipitation of uraninite from oxidize hydrothermal fluids.

Performance of the MTR core with MOX fuel using the MCNP4C2 code.

PubMed

Shaaban, Ismail; Albarhoum, Mohamad

2016-08-01

The MCNP4C2 code was used to simulate the MTR-22 MW research reactor and perform the neutronic analysis for a new fuel namely: a MOX (U3O8&PuO2) fuel dispersed in an Al matrix for One Neutronic Trap (ONT) and Three Neutronic Traps (TNTs) in its core. Its new characteristics were compared to its original characteristics based on the U3O8-Al fuel. Experimental data for the neutronic parameters including criticality relative to the MTR-22 MW reactor for the original U3O8-Al fuel at nominal power were used to validate the calculated values and were found acceptable. The achieved results seem to confirm that the use of MOX fuel in the MTR-22 MW will not degrade the safe operational conditions of the reactor. In addition, the use of MOX fuel in the MTR-22 MW core leads to reduce the uranium fuel enrichment with (235)U and the amount of loaded (235)U in the core by about 34.84% and 15.21% for the ONT and TNTs cases, respectively. Copyright © 2016 Elsevier Ltd. All rights reserved.

Seasonal uranium distributions in the coastal waters off the Amazon and Mississippi Rivers

USGS Publications Warehouse

Swarzenski, P.W.; McKee, B.A.

1998-01-01

The chemical reactivity of uranium was investigated across estuarine gradients from two of the world's largest river systems: the Amazon and Mississippi. Concentrations of dissolved (<0.45 ??m) uranium (U) were measured in surface waters of the Amazon shelf during rising (March 1990), flood (June 1990) and low (November 1991) discharge regimes. The dissolved U content was also examined in surface waters collected across estuarine gradients of the Mississippi outflow region during April 1992, August 1993, and November (1993). All water samples were analyzed for U by isotope dilution inductively coupled plasma mass spectrometry (ICP-MS). In Amazon shelf surface waters uranium increased nonconservatively from about 0.01 ??g l-1 at the river's mouth to over 3 ??g l-1 at the distal site, irrespective of river discharge stage. Observed large-scale U removal at salinities generally less than 15 implies a) that riverine dissolved U was extensively adsorbed by freshly-precipitated hydrous metal oxides (e.g., FeOOH, MnO2) as a result of flocculation and aggregation, and b) that energetic resuspension and reworking of shelf sediments and fluid muds on the Amazon shelf released a chemically reactive particle/colloid to the water column which can further scavenge dissolved U across much of the estuarine gradient. In contrast, the estuarine chemistry of U is inconclusive within surface waters of the Mississippi shelf-break region. U behavior is most likely controlled less by traditional sorption and/or desorption reactions involving metal oxides or colloids than by the river's variable discharge regime (e.g., water parcel residence time during estuarine mixing, nature of particulates, sediment storage and resuspension in the confined lower river), and plume dispersal. Mixing of the thin freshwater lens into ambient seawater is largely defined by wind-driven rather than physical processes. As a consequence, in the Mississippi outflow region uranium predominantly displays ConserVative behavior; removal is evident only during anomalous river discharge regimes. 'Products-approach' mixing experiments conducted during the Flood of 1993 suggest the importance of small particles and/or colloids in defining a depleted U versus salinity distribution.

Uranium biogeochemistry across the redox transition zone of a permanently stratified fjord: Framvaren, Norway

USGS Publications Warehouse

Swarzenski, P.W.; McKee, B.A.; Skei, J.M.; Todd, J.F.

1999-01-01

During August 1995, the vertical concentration profile of dissolved and particulate uranium exhibited strong non-conservative characteristics in the upper 30 m of Framvaren Fjord. There was a pronounced peak in both particulate (> 0.2 ??m; 1.09 nM) and dissolved (< 0.2 ??m; 17.06 nM) uranium in the finely stratified waters at the O2/H2S interface which is positioned well within the euphotic zone at about 20-21 m. Such concentration maxima at the redox boundary are also observed for dissolved organic carbon (DEC), Sr and Ba. Dissolved U levels seen in the water column from 18 m down to 30 m exceeded the high salinity (salinity = 35) U concentrations (13.63 ?? 0.84 nM; Chen, J.H., Edwards, R.L., Wasserburg, G.L., 1986. 238U, 234U and 232Th in seawater. Earth Planet Sci. Lett. 80, 241-251.) observed uniformly in the open ocean. A prolific population of S microbes (e.g., Chromatium, Chlorobium sp.) flourishes at the O2/H2S interface. The source of elevated U at the redox boundary must be due to microbial uptake and subsequent release processes rather than dilution from oceanic uranium. Uranium oxidation state determinations in waters from 1, 22 and 30 m depth reveal that reduced U(IV) is not present in significant abundance, and that the chemical and/or biological reduction of hexavalent uranium is largely inhibited. Our results suggest that U and other trace constituents such as DOC, Sr, Ba, Fe(II), Mn(II) are greatly modified by direct and indirect microbial transformation reactions which are most concentrated across the redox transition zone in Framvaren Fjord.

Progress report on geologic studies of the Ranger orebodies, Northern Territory, Australia

USGS Publications Warehouse

Nash, J.T.; Frishman, David

1982-01-01

The Ranger No. 1 and No. 3 orebodies contain about 124,000 tonnes U3O8 in highly chloritized metasediments of the lower Proterozoic Cahill Formation within about 500 m of the projected sub-Kombolgie Formation unconformity. In both orebodies, oxidized and reduced uranium minerals occur chiefly in quartzose schists that have highly variable amounts of muscovite, sericite, and chlorite. The effects of several periods of alteration are pervasive in the vicinity of orebodies where biotite and garnet are altered to chlorite, and feldspars to white mica or chlorite. Oxidized uranium minerals, associated with earthy iron oxides, occur from the surface to a depth of about 60 m. Below the oxidized zone, uranium occurs chiefly as uraninite and pitchblende disseminated through thick sections of quartz-chlorite-muscovite schist and has no apparent association with graphite or sulfides. In fact, graphite is rare and sulfides are generally low in abundance (<0.5 percent). Higher ore grades occur in disrupted zones a few centimeters thick and in some quartz-chlorite vein-like zones of uncertain origin. Uranium correlates strongly with chlorite, but not all of the many ages of chlorite have associated uranium. At least five textural varieties of chlorite are present and represent at least 3 ages. Preliminary microprobe analyses suggest that Mg-Fe-Al contents are relatively uniform. Apatite commonly occurs with chlorite. Uranium is not common in carbonate rocks and seems to occur only in disrupted zones that have chlorite alteration. Chloritization and silicification are more widespread and intense in the No. 1 orebody than in the No. 3. In both orebodies, hematite occurs tens to hundreds of meters below the weathered zone, in both altered and largely unaltered rocks, with and without uranium. The structure of the orebodies is outwardly simple, particularly in No. 3; dips are less than 40? on most lithologic contacts. The No. 1 orebody is in a basin-like structure about 400 m wide that probably formed in part by progressive removal of carbonate rocks that are as much as 200 m thick adjacent to the No. 1 orebody and below the No. 3 orebody. Quartz-chlorite breccias have formed in the zone of carbonate thinning; uranium is spotty and low grade in these breccias. Chloritized and uraniferous broken and sheared zones, a few centimeters to a few meters thick, have an unknown attitude but must have small displacement. Blocks of altered Kombolgie sandstone are downfaulted into the No. 3 orebody and locally contain reduced uranium minerals. One or more shear zones 5-30 m thick of crushed and smeared fine to coarse rock fragments occur below the orebodies, and other low-angle shears probably occur in the orebodies. The shear zone dips about 40 o and displacement on it is not known. The footwall rocks generally are less retrograded than those in the hanging wall (orebody) and consist of quartz-biotite-feldspar schists and gneisses flanking the Nanambu Complex. A few scattered fractures in the footwall sequence contain pitchblende of unknown age and origin. Major element chemical analyses confirm the lithologic observations of large changes in composition during multiple stages of alteration. Granitic dikes and pelitic schists have gained Fe and Mg and lost Si, Ca, Na, and K during chloritization. Marbles have gained Si, Al, Fe, and P, and lost Mg, Ca, and K during jasperoid-chlorite alteration. Total net chemical gains and losses in the Ranger No. 1 orebody were huge: equal to about 37 percent of the mass of the ore-bearing rock that will be mined. There were net gains in Si and P and net losses in Al, Fe, Mg, Ca, K, and Na. The geologic age(s) of uranium emplacement are obscure because there are few age criteria. Reduced uranium minerals are younger than 1.8-b.y.-old granite dikes, and some occur locally in 1.65-b.y.-old Kombolgie Formation. Diabase dikes (age not known) are thoroughly chloritized and contain sparse ore minerals. Oxidized ura

Facile Reductive Silylation of UO22+ to Uranium(IV) Chloride.

PubMed

Kiernicki, John J; Zeller, Matthias; Bart, Suzanne C

2017-01-19

General reductive silylation of the UO 2 2+ cation occurs readily in a one-pot, two-step stoichiometric reaction at room temperature to form uranium(IV) siloxides. Addition of two equivalents of an alkylating reagent to UO 2 X 2 (L) 2 (X=Cl, Br, I, OTf; L=triphenylphosphine oxide, 2,2'-bipyridyl) followed by two equivalents of a silyl (pseudo)halide, R 3 Si-X (R=aryl, alkyl, H; X=Cl, Br, I, OTf, SPh), cleanly affords (R 3 SiO) 2 UX 2 (L) 2 in high yields. Support is included for the key step in the process, reduction of U VI to U V . This procedure is applicable to a wide range of commercially available uranyl salts, silyl halides, and alkylating reagents. Under this protocol, one equivalent of SiCl 4 or two equivalents of Me 2 SiCl 2 results in direct conversion of the uranyl to uranium(IV) tetrachloride. Full spectroscopic and structural characterization of the siloxide products is reported. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Incorporation of oxidized uranium into Fe (hydr)oxides during Fe(II) catalyzed remineralization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nico, Peter S.; Stewart, Brandy D.; Fendorf, Scott

2009-07-01

The form of solid phase U after Fe(II) induced anaerobic remineralization of ferrihydrite in the presence of aqueous and absorbed U(VI) was investigated under both abiotic batch and biotic flow conditions. Experiments were conducted with synthetic ground waters containing 0.168 mM U(VI), 3.8 mM carbonate, and 3.0 mM Ca{sup 2+}. In spite of the high solubility of U(VI) under these conditions, appreciable removal of U(VI) from solution was observed in both the abiotic and biotic systems. The majority of the removed U was determined to be substituted as oxidized U (U(VI) or U(V)) into the octahedral position of the goethitemore » and magnetite formed during ferrihydrite remineralization. It is estimated that between 3% and 6% of octahedral Fe(III) centers in the new Fe minerals were occupied by U(VI). This site specific substitution is distinct from the non-specific U co-precipitation processes in which uranyl compounds, e.g. uranyl hydroxide or carbonate, are entrapped with newly formed Fe oxides. The prevalence of site specific U incorporation under both abiotic and biotic conditions and the fact that the produced solids were shown to be resistant to both extraction (30 mM KHCO{sub 3}) and oxidation (air for 5 days) suggest the potential importance of sequestration in Fe oxides as a stable and immobile form of U in the environment.« less

Thermionic System Evaluation Test: Ya-21U System Topaz International Program

DTIC Science & Technology

1996-07-01

by enriched uranium dioxide (U02) fuel pellets, as illustrated by Figure 5. The work section of the converter contained 34 TFEs that provided power...power system. This feature permitted transportation of the highly enriched uranium oxide fuel in separate containers from the space power system and...by Figure 8. The radial reflector contained three safety and nine control drums. Each drum contained a section of boron carbide (B4C) neutron poison

Efficacy of a solution-based approach for making sodalite waste forms for an oxide reduction salt utilized in the reprocessing of used uranium oxide fuel

NASA Astrophysics Data System (ADS)

Riley, Brian J.; Pierce, David A.; Frank, Steven M.; Matyáš, Josef; Burns, Carolyne A.

2015-04-01

This paper describes the various approaches evaluated for making solution-derived sodalite with a LiCl-Li2O oxide reduction salt selected to dissolve used uranium oxide fuel so the uranium can be recovered and recycled. The approaches include modified sol-gel and solution-based synthesis processes. As-made products were mixed with 5 and 10 mass% of a Na2O-B2O3-SiO2 glass binder and these, along with product without a binder, were heated using either a cold-press-and-sinter method or hot uniaxial pressing. The results demonstrate the limitation of sodalite yield due to the fast intermediate reactions between Na+ and Cl- to form halite in solution and Li2O and SiO2 to form lithium silicates (e.g., Li2SiO3 or Li2Si2O5) in the calcined and sintered pellets. The results show that pellets can be made with high sodalite fractions in the crystalline product (∼92 mass%) and low porosities using a solution-based approach and this LiCl-Li2O salt but that the incorporation of Li into the sodalite is low.

Efficacy of a solution-based approach for making sodalite waste forms for an oxide reduction salt utilized in the reprocessing of used uranium oxide fuel

DOE PAGES

Riley, Brian J.; Pierce, David A.; Frank, Steven M.; ...

2015-04-01

This paper describes the various approaches attempted to make solution-derived sodalite with a LiCl-Li 2O oxide reduction salt used to dissolve used uranium oxide fuel so the uranium can be recovered and recycled. The approaches include modified sol-gel and solutionbased synthesis processes. As-made products were mixed with 5 and 10 mass% of a Na 2O-B 2O 3- SiO 2 glass binder and these, along with product without a binder, were heated using either a cold-press-and-sinter method or hot uniaxial pressing. The results demonstrate the limitation of sodalite yield due to the fast intermediate reactions between Na+ and Cl- to formmore » halite in solution and Li 2O and SiO 2 to form lithium silicates (e.g., Li 2SiO 3 or Li 2Si 2O 5) in the calcined and sintered pellets. The results show that pellets can be made with high sodalite fractions in the crystalline product (~92 mass%) and low porosities using a solution-based approach and this LiCl-Li 2O salt but that the incorporation of Li into the sodalite is low.« less

Uranium Sequestration During Biostimulated Reduction and In Response to the Return of Oxic Conditions In Shallow Aquifers

USGS Publications Warehouse

Fuller, Christopher C.; Johnson, Kelly J.; Akstin, Katherine; Singer, David M.; Yabusaki, Steven B.; Fang, Yilin; Fuhrmann, M.

2015-01-01

A proposed approach for groundwater remediation of uranium contamination is to generate reducing conditions by stimulating the growth of microbial populations through injection of electron donor compounds into the subsurface. Sufficiently reducing conditions will result in reduction of soluble hexavalent uranium, U(VI), and precipitation of the less soluble +4 oxidation state uranium, U(IV). This process is termed biostimulated reduction. A key issue in the remediation of uranium (U) contamination in aquifers by biostimulated reduction is the long term stability of the sequestered uranium. Three flow-through column experiments using aquifer sediment were used to evaluate the remobilization of bioreduced U sequestered under conditions in which biostimulation extended well into sulfate reduction to enhance precipitation of reduced sulfur phases such as iron sulfides. One column received added ferrous iron, Fe(II), increasing production of iron sulfides, to test their effect on remobilization of the sequestered uranium, either by serving as a redox buffer by competing for dissolved oxygen, or by armoring the reduced uranium. During biostimulation of the ambient microbial population with acetate, dissolved uranium was lowered by a factor of 2.5 or more with continued removal for over 110 days of biostimulation, well after the onset of sulfate reduction at ~30 days. Sequestered uranium was essentially all U(IV) resulting from the formation of nano-particulate uraninite that coated sediment grains to a thickness of a few 10’s of microns, sometimes in association with S and Fe. A multicomponent biogeochemical reactive transport model simulation of column effluents during biostimulation was generally able to describe the acetate oxidation, iron, sulfate, and uranium reduction for all three columns using parameters derived from simulations of field scale biostimulation experiments. Columns were eluted with artificial groundwater at equilibrium with atmospheric oxygen to simulate the upper limit of dissolved oxygen in recharge water. Overall about 9% of total uranium removed from solution during biostimulation was remobilized. Release of U during oxic elution was a continuous process over 140 days with dissolved uranium concentrations about 0.2 and 0.8 aM for columns with and without ferrous iron addition, respectively. Uranium remaining on the sediment was in the reduced form. The prolonged period of biostimulation and concomitant sulfate reduction appears to limit the rate of U(IV) oxidative remobilization in contrast to a large release observed for columns in previous studies that did not undergo sulfate reduction. Although continued sulfate reduction may cause decreased permeability from precipitation of iron sulfide, the greater apparent stability of the sequestered U(IV) provided by the sustained biostimulation should be considered in design of field scale remediation efforts. Remobilization of uranium following biostimulated reduction should be tested further at the field scale.

Enthalpies of formation of U-, Th-, Ce-brannerite: implications for plutonium immobilization

NASA Astrophysics Data System (ADS)

Helean, K. B.; Navrotsky, A.; Lumpkin, G. R.; Colella, M.; Lian, J.; Ewing, R. C.; Ebbinghaus, B.; Catalano, J. G.

2003-08-01

Brannerite, ideally MTi 2O 6, (M=actinides, lanthanides and Ca) occurs in titanate-based ceramics proposed for the immobilization of plutonium. Standard enthalpies of formation, Δ H0f at 298 K, for three brannerite compositions (kJ/mol): CeTi 2O 6 (-2948.8 ± 4.3), U 0.97Ti 2.03O 6 (-2977.9 ± 3.5) and ThTi 2O 6 (-3096.5 ± 4.3) were determined by high temperature oxide melt drop solution calorimetry at 975 K using 3Na 2O · 4MoO 3 solvent. The enthalpies of formation were also calculated from an oxide phase assemblage (Δ H0f-ox at 298 K): MO 2 + 2TiO 2=MTi 2O 6. Only UTi 2O 6 is energetically stable with respect to an oxide assemblage: U 0.97Ti 2.03O 6 (Δ H0f-ox=-7.7±2.8 kJ/mol). Both CeTi 2O 6 and ThTi 2O 6 are higher in enthalpy with respect to their oxide assemblages with (Δ H0f-ox=+29.4±3.6 kJ/mol) and (Δ H0f-ox=+19.4±1.6 kJ/mol) respectively. Thus, Ce- and Th-brannerite are entropy stabilized and are thermodynamically stable only at high temperature.

Vaporization chemistry of hypo-stoichiometric (U,Pu)O 2

NASA Astrophysics Data System (ADS)

Viswanathan, R.; Krishnaiah, M. V.

2001-04-01

Calculations were performed on hypo-stoichiometric uranium plutonium di-oxide to examine its vaporization behavior as a function of O/ M ( M= U+ Pu) ratio and plutonium content. The phase U (1- y) Pu yO z was treated as an ideal solid solution of (1- y)UO 2+ yPuO (2- x) such that x=(2- z)/ y. Oxygen potentials for different desired values of y, z, and temperature were used as the primary input to calculate the corresponding partial pressures of various O-, U-, and Pu-bearing gaseous species. Relevant thermodynamic data for the solid phases UO 2 and PuO (2- x) , and the gaseous species were taken from the literature. Total vapor pressure varies with O/M and goes through a minimum. This minimum does not indicate a congruently vaporizing composition. Vaporization behavior of this system can at best be quasi-congruent. Two quasi-congruently vaporizing compositions (QCVCs) exist, representing the equalities (O/M) vapor=(O/M) mixed-oxide and (U/Pu) vapor=(U/Pu) mixed-oxide, respectively. The (O/M) corresponding to QCVC1 is lower than that corresponding to QCVC2, but very close to the value where vapor pressure minimum occurs. The O/M values of both QCVCs increase with decrease in plutonium content. The vaporization chemistry of this system, on continuous vaporization under dynamic condition, is discussed.

Managing the Nuclear Fuel Cycle: Policy Implications of Expanding Global Access to Nuclear Power

DTIC Science & Technology

2009-07-01

inalienable right and, by and large, neither have U.S. government officials. However, the case of Iran raises perhaps the most critical question in this...slight difference in atomic mass between 235U and 238U. The typical enrichment process requires about 10 lbs of uranium U3O8 to produce 1 lb of low...thermal neutrons but can induce fission in all actinides , including all plutonium isotopes. Therefore, nuclear fuel for a fast reactor must have a

URANIUM SEPARATION PROCESS

DOEpatents

Lyon, W.L.

1962-04-17

A method of separating uranium oxides from PuO/sub 2/, ThO/sub 2/, and other actinide oxides is described. The oxide mixture is suspended in a fused salt melt and a chlorinating agent such as chlorine gas or phosgene is sparged through the suspension. Uranium oxides are selectively chlorinated and dissolve in the melt, which may then be filtered to remove the unchlorinated oxides of the other actinides. (AEC)

Irradiation performance of HTGR fuel rods in HFIR experiments HRB-7 and -8

DOE Office of Scientific and Technical Information (OSTI.GOV)

Valentine, K.H.; Homan, F.J.; Long, E.L. Jr.

1977-05-01

The HRB-7 and -8 experiments were designed as a comprehensive test of mixed thorium-uranium oxide fissile particles with Th:U ratios from 0 to 8 for HTGR recycle application. In addition, fissile particles derived from Weak-Acid Resin (WAR) were tested as a potential backup type of fissile particle for HTGR recycle. These experiments were conducted at two temperatures (1250 and 1500/sup 0/C) to determine the influence of operating temperature on the performance parameters studied. The minor objectives were comparison of advanced coating designs where ZrC replaced SiC in the Triso design, testing of fuel coated in laboratory-scale equipment with fuel coatedmore » in production-scale coaters, comparison of the performance of /sup 233/U-bearing particles with that of /sup 235/U-bearing particles, comparison of the performance of Biso coatings with Triso coatings for particles containing the same type of kernel, and testing of multijunction tungsten-rhenium thermocouples. All objectives were accomplished. As a result of these experiments the mixed thorium-uranium oxide fissile kernel was replaced by a WAR-derived particle in the reference recycle design. A tentative decision to make this change had been reached before the HRB-7 and -8 capsules were examined, and the results of the examination confirmed the accuracy of the previous decision. Even maximum dilution (Th/U approximately equal to 8) of the mixed thorium-uranium oxide kernel was insufficient to prevent amoeba of the kernels at rates that are unacceptable in a large HTGR. Other results showed the performance of /sup 233/U-bearing particles to be identical to that of /sup 235/U-bearing particles, the performance of fuel coated in production-scale equipment to be at least as good as that of fuel coated in laboratory-scale coaters, the performance of ZrC coatings to be very promising, and Biso coatings to be inferior to Triso coatings relative to fission product retention.« less

Assessing and Minimizing Adversarial Risk in a Nuclear Material Transportation Network

DTIC Science & Technology

2013-09-01

0704-0188) Washington DC 20503. 1. AGENCY USE ONLY (Leave Blank) 2. REPORT DATE 09-27-2013 3. REPORT TYPE AND DATES COVERED Master’s Thesis 4. TITLE AND...U.S. as of July 2013. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 6 Figure A.1 Google Earth routing from Areva to Arkansas Nuclear...Uranium ore is mined or removed from the earth in a leaching process. 2. Conversion (1). Triuranium octoxide (U3O8, “yellowcake”) is converted into ura

Molten uranium dioxide structure and dynamics

DOE PAGES

Skinner, L. B.; Parise, J. B.; Benmore, C. J.; ...

2014-11-21

Uranium dioxide (UO 2) is the major nuclear fuel component of fission power reactors. A key concern during severe accidents is the melting and leakage of radioactive UO 2 as it corrodes through its zirconium cladding and steel containment. Yet, the very high temperatures (>3140 kelvin) and chemical reactivity of molten UO 2 have prevented structural studies. In this work, we combine laser heating, sample levitation, and synchrotron x-rays to obtain pair distribution function measurements of hot solid and molten UO 2. The hot solid shows a substantial increase in oxygen disorder around the lambda transition (2670 K) but negligiblemore » U-O coordination change. On melting, the average U-O coordination drops from 8 to 6.7 ± 0.5. Molecular dynamics models refined to this structure predict higher U-U mobility than 8-coordinated melts.« less

Trivalent uranium phenylchalcogenide complexes: exploring the bonding and reactivity with CS2 in the Tp*2UEPh series (E = O, S, Se, Te).

PubMed

Matson, Ellen M; Breshears, Andrew T; Kiernicki, John J; Newell, Brian S; Fanwick, Phillip E; Shores, Matthew P; Walensky, Justin R; Bart, Suzanne C

2014-12-15

The trivalent uranium phenylchalcogenide series, Tp*2UEPh (Tp* = hydrotris(3,5-dimethylpyrazolyl)borate, E = O (1), S (2), Se (3), Te (4)), has been synthesized to investigate the nature of the U-E bond. All compounds have been characterized by (1)H NMR, infrared and electronic absorption spectroscopies, and in the case of 4, X-ray crystallography. Compound 4 was also studied by SQUID magnetometry. Computational studies establish Mulliken spin densities for the uranium centers ranging from 3.005 to 3.027 (B3LYP), consistent for uranium-chalcogenide bonds that are primarily ionic in nature, with a small covalent contribution. The reactivity of 2-4 toward carbon disulfide was also investigated and showed reversible CS2 insertion into the U(III)-E bond, forming Tp*2U(κ(2)-S2CEPh) (E = S (5), Se (6), Te (7)). Compound 5 was characterized crystallographically.

Melting behavior of mixed U-Pu oxides under oxidizing conditions

NASA Astrophysics Data System (ADS)

Strach, Michal; Manara, Dario; Belin, Renaud C.; Rogez, Jacques

2016-05-01

In order to use mixed U-Pu oxide ceramics in present and future nuclear reactors, their physical and chemical properties need to be well determined. The behavior of stoichiometric (U,Pu)O2 compounds is relatively well understood, but the effects of oxygen stoichiometry on the fuel performance and stability are often still obscure. In the present work, a series of laser melting experiments were carried out to determine the impact of an oxidizing atmosphere, and in consequence the departure from a stoichiometric composition on the melting behavior of six mixed uranium plutonium oxides with Pu content ranging from 14 to 62 wt%. The starting materials were disks cut from sintered stoichiometric pellets. For each composition we have performed two laser melting experiments in pressurized air, each consisting of four shots of different duration and intensity. During the experiments we recorded the temperature at the surface of the sample with a pyrometer. Phase transitions were qualitatively identified with the help of a reflected blue laser. The observed phase transitions occur at a systematically lower temperature, the lower the Pu content of the studied sample. It is consistent with the fact that uranium dioxide is easily oxidized at elevated temperatures, forming chemical species rich in oxygen, which melt at a lower temperature and are more volatile. To our knowledge this campaign is a first attempt to quantitatively determine the effect of O/M on the melting temperature of MOX.

Glutathione oxidation in response to intracellular H2O2: Key but overlapping roles for dehydroascorbate reductases.

PubMed

Rahantaniaina, Marie-Sylviane; Li, Shengchun; Chatel-Innocenti, Gilles; Tuzet, Andrée; Mhamdi, Amna; Vanacker, Hélène; Noctor, Graham

2017-08-03

Glutathione is a pivotal molecule in oxidative stress, during which it is potentially oxidized by several pathways linked to H 2 O 2 detoxification. We have investigated the response and functional importance of 3 potential routes for glutathione oxidation pathways mediated by glutathione S-transferases (GST), glutaredoxin-dependent peroxiredoxins (PRXII), and dehydroascorbate reductases (DHAR) in Arabidopsis during oxidative stress. Loss-of-function gstU8, gstU24, gstF8, prxIIE and prxIIF mutants as well as double gstU8 gstU24, gstU8 gstF8, gstU24 gstF8, prxIIE prxIIF mutants were obtained. No mutant lines showed marked changes in their phenotype and glutathione profiles in comparison to the wild-type plants in either optimal conditions or oxidative stress triggered by catalase inhibition. By contrast, multiple loss of DHAR functions markedly decreased glutathione oxidation triggered by catalase deficiency. To assess whether this effect was mediated directly by loss of DHAR enzyme activity, or more indirectly by upregulation of other enzymes involved in glutathione and ascorbate recycling, we measured expression of glutathione reductase (GR) and expression and activity of monodehydroascorbate reductases (MDHAR). No evidence was obtained that either GRs or MDHARs were upregulated in plants lacking DHAR function. Hence, interplay between different DHARs appears to be necessary to couple ascorbate and glutathione pools and to allow glutathione-related signaling during enhanced H 2 O 2 metabolism.

Investigation of molybdate melts as an alternative method of reprocessing used nuclear fuel

DOE PAGES

Hames, Amber L.; Tkac, Peter; Paulenova, Alena; ...

2017-01-17

Here, an investigation of molybdate melts containing sodium molybdate (Na 2MoO 4) and molybdenum trioxide (MoO 3) to achieve the separation of uranium from fission products by crystallization has been performed. The separation is based on the difference in solubility of the fission product metal oxides compared to the uranium oxide or molybdate in the molybdate melt. The molybdate melt dissolves uranium dioxide at high temperatures, and upon cooling, uranium precipitates as uranium dioxide or molybdate, whereas the fission product metals remain soluble in the melt. Small-scale experiments using gram quantities of uranium dioxide have been performed to investigate themore » feasibility of UO 2 purification from the fission products. The composition of the uranium precipitate as well as data for partitioning of several fission product surrogates between the uranium precipitate and molybdate melt for various melt compositions are presented and discussed. The fission products Cs, Sr, Ru and Rh all displayed very large distribution ratios. The fission products Zr, Pd, and the lanthanides also displayed good distribution ratios (D > 10). A melt consisting of 20 wt% MoO 3-50 wt% Na 2MoO 4-30 wt% UO 2 heated to 1313 K and cooled to 1123 K for the physical separation of the UO 2 product from the melt, and washed once with Na 2MoO 4 displays optimum conditions for separation of the UO 2 from the fission products.« less

Webinar on the Removal of Uranium from Drinking Water by Small System Treatment Technology

EPA Science Inventory

Abstract: Radionuclides, such as uranium (U), occur naturally as trace elements in rocks and soils and thus can be found in dissolved forms in ground waters. Uranium has four oxidation states (+3, +4, +5, and +6) and is a very reactive element forming a variety of stable complexe...

Cs(2)K(UO)(2)Si(4)O(12): a mixed-valence uranium(IV,V) silicate.

PubMed

Lee, Cheng-Shiuan; Wang, Sue-Lein; Lii, Kwang-Hwa

2009-10-28

The first mixed-valence uranium(IV,V) silicate is synthesized under high-temperature, high-pressure hydrothermal conditions. The structure contains chains of corner-sharing U(IV,V)O(6) octahedra which are interconnected by Si(4)O(12) four-membered rings to form a 3-D framework. XPS and XANES spectra were measured to identify the valence state of uranium.

Geologic report on the Sand Wash Drilling Project, Moffat and Routt Counties, Colorado

DOE Office of Scientific and Technical Information (OSTI.GOV)

Carter, T.E.; Wayland, T.E.

1981-09-01

The Sand Wash Basin Drilling Project comprises twenty-seven (27) drill holes located in Moffat and Routt Counties, northwest Colorado, having an aggregate depth of 26,107.5 feet (7957.6 m). The holes penetrate the Browns Park Formation of Miocene age, which is a tuffaceous continental sandstone deposited in fluvial, eolian, and lacustrine environments. Partly based on project drilling results, uranium potential resource estimates for this formation in the $50/lb U/sub 3/O/sub 8/ forward-cost category have been increased by 34,476 tons U/sub 3/O/sub 8/ (35,036 metric tons). Three areas between Maybell and Craig, Colorado, considered favorable for uranium occurrences were verified as favorablemore » by project drilling, and a fourth favorable area northwest of Maybell has been expanded. In addition, project drilling results indicate two new favorable areas, one north and northwest and one south of Steamboat Springs, Colorado. Anomalous radioactivity was detected in drill holes in all six study areas of the project. The most important factor in concentrating significant amounts of uranium in the target formation appears to be the availability of gaseous or liquid hydrocarbons and/or hydrogen sulfide gas as reductants. Where subjacent formations supply these reductants to the Browns Park Formation, project drilling encountered 0.05 percent to 0.01 percent uranium concentrations. Potential, though unproven, sources of these reductants are believed to underlie parts of all six project study areas.« less

Behaviour of the pH Adjustment, Ion Exchange and Concentrate Precipitation Stages in the Acid Leaching of Uranium Phosphate Ores; TRATAMIENTO DE DISOLUCIONES DE LIXIVIACION DE MINERALES DE URANIO EN PRESENCIA DE FOSFATOS. COMPORTAMIENTO EN LAS ETAPAS DE AJUSTE DE PH, CAMBIO DE ION Y PRECIPITACION DE CONCENTRADOS (in Spanish)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aguilar, J.E.; Hueda, A.U.

Recovery of U from acid leach solutions of phosphate ore was studied. It was found that predictions can be made concerning solids removal and U recovery in the pH adjustment stage, resin U capacity, eluating agent suitability, ion exchange stage eluation velocity and eluate U concentration, and composition of the precipitate formed in the concentration stage. The results are valid in the concentration range 0.3 to 0. 8 g U/sub 3/O/sub 8//1. (J.R.D.)

Electrochemical and Spectroscopic Evidence on the One-Electron Reduction of U(VI) to U(V) on Magnetite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yuan, Ke; Ilton, Eugene S.; Antonio, Mark R.

2015-05-19

Reduction of U(VI) to U(VI) on mineral surfaces is often considered a one-step two-electron process. However, stabilized U(V), with no evidence of U(IV), found in recent studies Indicates U(VI) can undergo a one-electron reduction to U(V) without further progression to U(VI),. We investigated reduction pathways of uranium by reducing U(VI) electrochemically on a, magnetite electrode at,pH 3.4. Cyclic voltammetry confirms the one-electron reduction of U(VI) . Formation of nanosize uranium precipitates on the magnetite surface at reducing potentials and dissolution of the solids at oxidizing potentials are observed by in situ electrochemical atomic force microscopy. XPS, analysis Of the magnetitemore » electrodes polarized in uranium solutions at voltages - from -0.1 to -0.9 V (E-U(VI)/U(V)(0)= -0.135 V vs Ag/AgCl) show the presence of, only U(V) and U(VI). The sample with the highest U(V)/U(VI) ratio was prepared at -0.7 V, where the longest average U-O-axial distance of 2.05 + 0.01 A was evident in the same sample revealed by extended X-ray absorption fine structure analysis. The results demonstrate that the electrochemical reduction of U(VI) On magnetite only yields,U(V), even at a potential of -0.9 V, which favors the one-electron reduction mechanism, U(V) does not disproportionate but stabilizes on magnetite through precipitation Of mixed-valence state -U(V)/U(VI) solids.« less

Zircon U-Pb geochronology and geochemistry of granites in the Zhuguangshan complex, South China: Implications for uranium mineralization

NASA Astrophysics Data System (ADS)

Zhang, Long; Chen, Zhenyu; Li, Xiaofeng; Li, Shengrong; Santosh, M.; Huang, Guolong

2018-05-01

The Zhuguangshan complex, composed of Caledonian, Indosinian, and Yanshanian granites, and Cretaceous mafic dykes, is one of the most important granite-hosted uranium producers in South China. Here we present LA-ICP-MS zircon U-Pb and hornblende 40Ar/39Ar geochronology and whole-rock and biotite geochemistry for the granites in this complex to evaluate the magmatism and its constraints on uranium mineralization. Samples collected from the Fuxi, Youdong, Longhuashan, Chikeng, Qiling, and Sanjiangkou intrusions yield zircon weighted 206Pb/238U ages of 426.7 ± 5.4 Ma, 226.4 ± 3.5 Ma, 225.0 ± 2.7 Ma, 152.2 ± 3.0 Ma, 153.9 ± 2.1 Ma, and 155.2 ± 2.1 Ma, respectively. A new Ar-Ar dating of the hornblende of the diabase from the Changjiang uranium ore field yields a plateau age of 145.1 ± 1.5 Ma. These results coupled with published geochronological data indicate that six major magmatic events occurred in the study area at 420-435 Ma, 225-240 Ma, 150-165 Ma, 140 Ma, 105 Ma, and 90 Ma. Both U-bearing and barren granites occur in this complex, and they display differences in whole-rock and biotite geochemistry. The barren granites show higher Al2O3, CaO, TFMM, Rb, Zr, Ba, SI, Mg#, (La/Yb)N, and Eu/Eu*, but lower SiO2, ALK, Rb, DI, Rb/Sr, and TiO2/MgO than those of the U-bearing granites. Biotites in the U-bearing granites are close to the Fe-rich siderophyllite-annite end member with Fe/(Fe + Mg) ratios higher than 0.66, whereas those in the barren granites are relatively close to the Mg-rich eastonite-phlogopite end member with Fe/(Fe + Mg) ratios <0.66. The U-bearing granites were mainly derived from the partial melting of pelitic sedimentary source, whereas the psammitic source generated the barren granites. In addition, the barren granites show higher TFMM, Ba, and Eu/Eu* but lower SiO2, Rb/Sr and Al2O3/TiO2 ratios with higher zircon saturation temperatures relative to the U-bearing granites. These results indicate that the geochemical compositions of the U-bearing and barren granites are dictated not only by the compositions of source rocks but also the physicochemical conditions of partial melting. Our study suggests that these two factors are also the major factors that control uranium ore potential of the granites in the Zhuguangshan complex. The geochemical variations of U-bearing and barren granites can serve as a potential detector for granite-hosted uranium deposits.

Regularities of spatial association of major endogenous uranium deposits and kimberlitic dykes in the uranium ore regions of the Ukrainian Shield

NASA Astrophysics Data System (ADS)

Kalashnyk, Anna

2015-04-01

During exploration works we discovered the spatial association and proximity time formation of kimberlite dykes (ages are 1,815 and 1,900 Ga for phlogopite) and major industrial uranium deposits in carbonate-sodium metasomatites (age of the main uranium ore of an albititic formation is 1,85-1,70 Ga according to U-Pb method) in Kirovogradsky, Krivorozhsky and Alekseevsko-Lysogorskiy uranium ore regions of the Ukrainian Shield (UkrSh) [1]. In kimberlites of Kirovogradsky ore region uranium content reaches 18-20 g/t. Carbon dioxide is a major component in the formation of hydrothermal uranium deposits and the formation of the sodium in the process of generating the spectrum of alkaline ultrabasic magmas in the range from picritic to kimberlite and this is the connection between these disparate geochemical processes. For industrial uranium deposits in carbonate-sodium metasomatitics of the Kirovogradsky and Krivorozhsky uranium ore regions are characteristic of uranyl carbonate introduction of uranium, which causes correlation between CO2 content and U in range of "poor - ordinary - rich" uranium ore. In productive areas of uranium-ore fields of the Kirovogradsky ore region for phlogopite-carbonate veinlets of uranium ore albitites deep δ13C values (from -7.9 to -6.9o/oo) are characteristic. Isotope-geochemical investigation of albitites from Novokonstantynovskoe, Dokuchaevskoe, Partyzanskoe uranium deposits allowed obtaining direct evidence of the involvement of mantle material during formation of uranium albitites in Kirovogradsky ore region [2]. Petrological characteristics of kimberlites from uranium ore regions of the UkrSh (presence of nodules of dunite and harzburgite garnet in kimberlites, diamonds of peridotite paragenesis, chemical composition of indicator minerals of kimberlite, in particular Gruzskoy areas pyropes (Cr2O3 = 6,1-7,1%, MgO = 19,33-20,01%, CaO = 4,14-4,38 %, the content of knorringite component of most grains > 50mol%), chromites (Cr2O3 = 45,32-62,17%, MgO = 7,3-12,5%) allow us to estimate the depth of generation of kimberlite magmas more than 170-200 km. Ilmenites show two groups according to MgO, Cr2O3 and TiO2 content. Reconstructions of the mantle sections show also two intervals of pressures divided at 4.5 GPa, the upper part is highly metasomatized This high degree metasomatism is determined for almost all mantle columns. It is suggested that large-scale of uranium-bearing mantle fluids may be associated with the ancient degasation during the subduction which is highly enriched in U component . Analysis of the reasons for the marked association kimberlitic dykes and major industrial uranium deposits in carbonate-sodium metasomatic in the UkrSh led to the conclusion that hydrothermal uranium deposits are confined to the supply mantle fluid systems of mantle fault zones exercising brings sodium carbonate solutions enriched uranium from mantle sources. References: 1. Kalashnik A.A. New prognostic-evaluation criteria in technology prognosis of forming industrial endogenous uranium deposits of the Ukrainian Shield, 2014. Scientific proceedings of UkrSGRI, № 2, p. 27-54 (in Russian) 2. Stepanjuk L.M., Bondarenko S.V., Somka V.O. and other, 2012. Source of uranium and uranium-bearing sodium albitites for example of Dokuchaievskogo field of the Ingulsky megablock of the UkrSh: Abstracts of scientific conference "Theoretical issues and research practice metasomatic rocks and ores" (Kyiv, 14-16 March 2012), IGMOF, p.78-80. (in Ukrainian)

Oxidation kinetics for conversion of U 3O 8 to ε-UO 3 with NO 2

DOE PAGES

Johnson, J. A.; Rawn, C. J.; Spencer, B. B.; ...

2017-04-04

The oxidation kinetics of U 3O 8 powder to ε-UO 3 in an NO 2 environment was measured by in situ x-ray diffraction (XRD). Experiments were performed at temperatures of 195, 210, 235, and 250°C using a custom designed and fabricated sample isolation stage. Data were refined to quantify phase fractions using a newly proposed structure for the ε-UO 3 polymorph. The kinetics data were modeled using a shrinking core approach. A proposed two-step reaction process is presented based on the developed models.

In situ characterization of uranium and americium oxide solid solution formation for CRMP process: first combination of in situ XRD and XANES measurements.

PubMed

Caisso, Marie; Picart, Sébastien; Belin, Renaud C; Lebreton, Florent; Martin, Philippe M; Dardenne, Kathy; Rothe, Jörg; Neuville, Daniel R; Delahaye, Thibaud; Ayral, André

2015-04-14

Transmutation of americium in heterogeneous mode through the use of U1-xAmxO2±δ ceramic pellets, also known as Americium Bearing Blankets (AmBB), has become a major research axis. Nevertheless, in order to consider future large-scale deployment, the processes involved in AmBB fabrication have to minimize fine particle dissemination, due to the presence of americium, which considerably increases the risk of contamination. New synthesis routes avoiding the use of pulverulent precursors are thus currently under development, such as the Calcined Resin Microsphere Pelletization (CRMP) process. It is based on the use of weak-acid resin (WAR) microspheres as precursors, loaded with actinide cations. After two specific calcinations under controlled atmospheres, resin microspheres are converted into oxide microspheres composed of a monophasic U1-xAmxO2±δ phase. Understanding the different mechanisms during thermal conversion, that lead to the release of organic matter and the formation of a solid solution, appear essential. By combining in situ techniques such as XRD and XAS, it has become possible to identify the key temperatures for oxide formation, and the corresponding oxidation states taken by uranium and americium during mineralization. This paper thus presents the first results on the mineralization of (U,Am) loaded resin microspheres into a solid solution, through in situ XAS analysis correlated with HT-XRD.

Depleted and enriched uranium exposure quantified in former factory workers and local residents of NL Industries, Colonie, NY USA

DOE Office of Scientific and Technical Information (OSTI.GOV)

Arnason, John G.

Background: Between 1958 and 1982, NL Industries manufactured components of enriched (EU) and depleted uranium (DU) at a factory in Colonie NY, USA. More than 5 metric tons of DU was deposited as microscopic DU oxide particles on the plant site and surrounding residential community. A prior study involving a small number of individuals (n=23) indicated some residents were exposed to DU and former workers to both DU and EU, most probably through inhalation of aerosol particles. Objectives: Our aim was to measure total uranium [U] and the uranium isotope ratios: {sup 234}U/{sup 238}U; {sup 235}U/{sup 238}U; and {sup 236}U/{supmore » 238}U, in the urine of a cohort of former workers and nearby residents of the NLI factory, to characterize individual exposure to natural uranium (NU), DU, and EU more than 3 decades after production ceased. Methods: We conducted a biomonitoring study in a larger cohort of 32 former workers and 99 residents, who may have been exposed during its period of operation, by measuring Total U, NU, DU, and EU in urine using Sector Field Inductively Coupled Plasma - Mass Spectrometry (SF-ICP-MS). Results: Among workers, 84% were exposed to DU, 9% to EU and DU, and 6% to natural uranium (NU) only. For those exposed to DU, urinary isotopic and [U] compositions result from binary mixing of NU and the DU plant feedstock. Among residents, 8% show evidence of DU exposure, whereas none shows evidence of EU exposure. For residents, the [U] geometric mean is significantly below the value reported for NHANES. There is no significant difference in [U] between exposed and unexposed residents, suggesting that [U] alone is not a reliable indicator of exposure to DU in this group. Conclusions: Ninety four percent of workers tested showed evidence of exposure to DU, EU or both, and were still excreting DU and EU decades after leaving the workforce. The study demonstrates the advantage of measuring multiple isotopic ratios (e.g., {sup 236}U/{sup 238}U and {sup 235}U/{sup 238}U) over a single ratio ({sup 235}U/{sup 238}U) in determining sources of uranium exposure. - Highlights: • Biomonitoring study of residents and former workers exposed to DU in Colonie NY. • Urine (99 residents+32 former workers) analyzed for depleted uranium (DU). • DU detected in 84% of workers and 8% of residents >30 years after plant closed. • Enriched uranium detected in 6% of former workers based on isotope ratios.« less

Epithermal uranium deposits in a volcanogenic context: the example of Nopal 1 deposit, Sierra de Pena Blanca, Mexico

NASA Astrophysics Data System (ADS)

Calas, G.; Angiboust, S.; Fayek, M.; Camacho, A.; Allard, T.; Agrinier, P.

2009-12-01

The Peña Blanca molybdenum-uranium field (Chihuahua, Mexico) exhibits over 100 airborne anomalies hosted in tertiary ignimbritic ash-flow tuffs (44 Ma) overlying the Pozos conglomerate and a sequence of Cretaceous carbonate rocks. Uranium occurrences are associated with breccia zones at the intersection of two or more fault systems. Periodic reactivation of these structures associated with Basin and Range and Rio Grande tectonic events resulted in the mobilization of U and other elements by meteoric fluids heated by geothermal activity. Trace element geochemistry (U, Th, REE) provides evidence for local mobilization of uranium under oxidizing conditions. In addition, O- and H-isotope geochemistry of kaolinite, smectite, opal and calcite suggests that argillic alteration proceeded at shallow depth with meteoric water at 25-75 °C. Focussed along breccia zones, fluids precipitated several generations of pyrite and uraninite together with kaolinite, as in the Nopal 1 mine, indicating that mineralization and hydrothermal alteration of volcanic tuffs are contemporaneous. Low δ34S values (~ -24.5 ‰) of pyrites intimately associated with uraninite suggest that the reducing conditions at the origin of the U-mineralization arise from biological activity. Later, the uplift of Sierra Pena Blanca resulted in oxidation and remobilization of uranium, as confirmed by the spatial distribution of radiation-induced defect centers in kaolinites. These data show that tectonism and biogenic reducing conditions can play a major role in the formation and remobilization of uranium in epithermal deposits. By comparison with the other uranium deposits at Sierra Pena Blanca and nearby Sierra de Gomez, Nopal 1 deposit is one of the few deposits having retained a reduced uranium mineralization.

The phase state at high temperatures in the MOX-SiO 2 system

NASA Astrophysics Data System (ADS)

Nakamichi, S.; Kato, M.; Sunaoshi, T.; Uchida, T.; Morimoto, K.; Kashimura, M.; Kihara, Y.

2009-06-01

Influence of impurity Si on microstructure in a plutonium and uranium mixed oxide (MOX), which is used for fast breeder reactor fuel, was investigated, and phase state in 25% SiO 2 - (U 0.7Pu 0.3)O 2 was observed as a function of oxygen chemical potential. Compounds composed of Pu and Si with other elements were observed at grain boundaries of the MOX parent phase in the specimens after annealing. These compounds were not observed in the grain interior and the MOX phase was not affected significantly by impurity Si. It was found that the compounds tended to form more observably with decreasing O/M ratio and with increasing annealing temperatures.

Depleted and enriched uranium exposure quantified in former factory workers and local residents of NL Industries, Colonie, NY USA.

PubMed

Arnason, John G; Pellegri, Christine N; Moore, June L; Lewis-Michl, Elizabeth L; Parsons, Patrick J

2016-10-01

Between 1958 and 1982, NL Industries manufactured components of enriched (EU) and depleted uranium (DU) at a factory in Colonie NY, USA. More than 5 metric tons of DU was deposited as microscopic DU oxide particles on the plant site and surrounding residential community. A prior study involving a small number of individuals (n=23) indicated some residents were exposed to DU and former workers to both DU and EU, most probably through inhalation of aerosol particles. Our aim was to measure total uranium [U] and the uranium isotope ratios: (234)U/(238)U; (235)U/(238)U; and (236)U/(238)U, in the urine of a cohort of former workers and nearby residents of the NLI factory, to characterize individual exposure to natural uranium (NU), DU, and EU more than 3 decades after production ceased. We conducted a biomonitoring study in a larger cohort of 32 former workers and 99 residents, who may have been exposed during its period of operation, by measuring Total U, NU, DU, and EU in urine using Sector Field Inductively Coupled Plasma - Mass Spectrometry (SF-ICP-MS). Among workers, 84% were exposed to DU, 9% to EU and DU, and 6% to natural uranium (NU) only. For those exposed to DU, urinary isotopic and [U] compositions result from binary mixing of NU and the DU plant feedstock. Among residents, 8% show evidence of DU exposure, whereas none shows evidence of EU exposure. For residents, the [U] geometric mean is significantly below the value reported for NHANES. There is no significant difference in [U] between exposed and unexposed residents, suggesting that [U] alone is not a reliable indicator of exposure to DU in this group. Ninety four percent of workers tested showed evidence of exposure to DU, EU or both, and were still excreting DU and EU decades after leaving the workforce. The study demonstrates the advantage of measuring multiple isotopic ratios (e.g., (236)U/(238)U and (235)U/(238)U) over a single ratio ((235)U/(238)U) in determining sources of uranium exposure. Copyright © 2016 Elsevier Inc. All rights reserved.

Nuclear waste viewed in a new light; a synchrotron study of uranium encapsulated in grout.

PubMed

Stitt, C A; Hart, M; Harker, N J; Hallam, K R; MacFarlane, J; Banos, A; Paraskevoulakos, C; Butcher, E; Padovani, C; Scott, T B

2015-03-21

How do you characterise the contents of a sealed nuclear waste package without breaking it open? This question is important when the contained corrosion products are potentially reactive with air and radioactive. Synchrotron X-rays have been used to perform micro-scale in-situ observation and characterisation of uranium encapsulated in grout; a simulation for a typical intermediate level waste storage packet. X-ray tomography and X-ray powder diffraction generated both qualitative and quantitative data from a grout-encapsulated uranium sample before, and after, deliberately constrained H2 corrosion. Tomographic reconstructions provided a means of assessing the extent, rates and character of the corrosion reactions by comparing the relative densities between the materials and the volume of reaction products. The oxidation of uranium in grout was found to follow the anoxic U+H2O oxidation regime, and the pore network within the grout was observed to influence the growth of uranium hydride sites across the metal surface. Powder diffraction analysis identified the corrosion products as UO2 and UH3, and permitted measurement of corrosion-induced strain. Together, X-ray tomography and diffraction provide means of accurately determining the types and extent of uranium corrosion occurring, thereby offering a future tool for isolating and studying the reactions occurring in real full-scale waste package systems. Copyright © 2014 Elsevier B.V. All rights reserved.

Formation of 238U16O and 238U18O observed by time-resolved emission spectroscopy subsequent to laser ablation

NASA Astrophysics Data System (ADS)

Weisz, David G.; Crowhurst, Jonathan C.; Siekhaus, Wigbert J.; Rose, Timothy P.; Koroglu, Batikan; Radousky, Harry B.; Zaug, Joseph M.; Armstrong, Michael R.; Isselhardt, Brett H.; Savina, Michael R.; Azer, Magdi; Finko, Mikhail S.; Curreli, Davide

2017-07-01

We have measured vibronic emission spectra of an oxide of uranium formed after laser ablation of the metal in gaseous oxygen. Specifically, we have measured the time-dependent relative intensity of a band located at approximately 593.6 nm in 16O2. This band grew in intensity relative to neighboring atomic features as a function time in an oxygen environment but was relatively invariant with time in argon. In addition, we have measured the spectral shift of this band in an 18O2 atmosphere. Based on this shift, and by comparison with earlier results obtained from free-jet expansion and laser excitation, we can confirm that the oxide in question is UO, consistent with recent reports based on laser ablation in 16O2 only.

Use of boiled hexamethylenetetramine and urea to increase the porosity of cerium dioxide microspheres formed in the internal gelation process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hunt, R. D.; Collins, J. L.; Cowell, B. S.

Cerium dioxide (CeO 2) is a commonly used simulant for plutonium dioxide and for plutonium (Pu) in a mixed uranium (U) and Pu oxide [(U, Pu)O 2] in nuclear fuel development. This effort developed CeO 2 microspheres with different porosities and diameters for use in a crush-strength study. The internal gelation technique has produced CeO 2 microspheres with limited initial porosity. When an equal molar solution of urea and hexamethylenetetramine (HMTA) is gently boiling for 1 hr and used in the gelation process, the crystallite size and porosity of mixed U and thorium oxide microspheres and the (U, Pu)O 2more » microspheres increased significantly. In this study with cerium, the combination of ammonium cerium nitrate and 1-h boiled HMTA-urea failed to produce a stable feed broth. However, when the 1-h heated HMTA-urea was combined with unheated HMTA-urea in 1 to 3 volume ratio or the boiling time of the HMTA-urea was reduced to 15-20 min, a stable solution of HMTA, urea, and Ce was formed at 273 K. This new Ce solution produced CeO 2 microspheres with much higher initial porosities. Intermediate porosities were possible when the heated HMTA/urea was aged prior to use.« less

Use of boiled hexamethylenetetramine and urea to increase the porosity of cerium dioxide microspheres formed in the internal gelation process

DOE PAGES

Hunt, R. D.; Collins, J. L.; Cowell, B. S.

2017-05-13

Cerium dioxide (CeO 2) is a commonly used simulant for plutonium dioxide and for plutonium (Pu) in a mixed uranium (U) and Pu oxide [(U, Pu)O 2] in nuclear fuel development. This effort developed CeO 2 microspheres with different porosities and diameters for use in a crush-strength study. The internal gelation technique has produced CeO 2 microspheres with limited initial porosity. When an equal molar solution of urea and hexamethylenetetramine (HMTA) is gently boiling for 1 hr and used in the gelation process, the crystallite size and porosity of mixed U and thorium oxide microspheres and the (U, Pu)O 2more » microspheres increased significantly. In this study with cerium, the combination of ammonium cerium nitrate and 1-h boiled HMTA-urea failed to produce a stable feed broth. However, when the 1-h heated HMTA-urea was combined with unheated HMTA-urea in 1 to 3 volume ratio or the boiling time of the HMTA-urea was reduced to 15-20 min, a stable solution of HMTA, urea, and Ce was formed at 273 K. This new Ce solution produced CeO 2 microspheres with much higher initial porosities. Intermediate porosities were possible when the heated HMTA/urea was aged prior to use.« less

The distribution and mobility of uranium in glassy and zeolitized tuff, Keg Mountain area, Utah, U.S.A.

USGS Publications Warehouse

Zielinski, R.A.; Lindsey, D.A.; Rosholt, J.N.

1980-01-01

The distribution and mobility of uranium in a diagenetically altered, 8 Ma old tuff in the Keg Mountain area, Utah, are modelled in this study. The modelling represents an improvement over similar earlier studies in that it: (1) considers a large number of samples (76) collected with good geologic control and exhibiting a wide range of alteration; (2) includes radiometric data for Th, K and RaeU (radium equivalent uranium) as well as U; (3) considers mineralogic and trace-element data for the same samples; and (4) analyzes the mineral and chemical covariation by multivariate statistical methods. The variation of U in the tuff is controlled mainly by its primary abundance in glass and by the relative abundance of non-uraniferous detritus and uraniferous accessory minerals. Alteration of glass to zeolite, even though extensive, caused no large or systematic change in the bulk concentration of U in the tuff. Some redistribution of U during diagenesis is indicated by association of U with minor alteration products such as opal and hydrous Fe-Mn oxide minerals. Isotopic studies indicate that the zeolitized tuff has been open to migration of U decay products during the last 0.8 Ma. The tuff of Keg Mountain has not lost a statistically detectable fraction of its original U, even though it has a high (??? 9 ppm) trace U content and has been extensively altered to zeolite. Similar studies in a variety of geological environments are required in order to identify the particular combination of conditions most favorable for liberation and migration of U from tuffs. ?? 1980.

Quantifying Uranium Isotope Ratios Using Resonance Ionization Mass Spectrometry: The Influence of Laser Parameters on Relative Ionization Probability

DOE Office of Scientific and Technical Information (OSTI.GOV)

Isselhardt, Brett H.

2011-09-01

Resonance Ionization Mass Spectrometry (RIMS) has been developed as a method to measure relative uranium isotope abundances. In this approach, RIMS is used as an element-selective ionization process to provide a distinction between uranium atoms and potential isobars without the aid of chemical purification and separation. We explore the laser parameters critical to the ionization process and their effects on the measured isotope ratio. Specifically, the use of broad bandwidth lasers with automated feedback control of wavelength was applied to the measurement of 235U/ 238U ratios to decrease laser-induced isotopic fractionation. By broadening the bandwidth of the first laser inmore » a 3-color, 3-photon ionization process from a bandwidth of 1.8 GHz to about 10 GHz, the variation in sequential relative isotope abundance measurements decreased from >10% to less than 0.5%. This procedure was demonstrated for the direct interrogation of uranium oxide targets with essentially no sample preparation. A rate equation model for predicting the relative ionization probability has been developed to study the effect of variation in laser parameters on the measured isotope ratio. This work demonstrates that RIMS can be used for the robust measurement of uranium isotope ratios.« less

Sandstone type uranium deposits in the Ordos Basin, Northwest China: A case study and an overview

NASA Astrophysics Data System (ADS)

Akhtar, Shamim; Yang, Xiaoyong; Pirajno, Franco

2017-09-01

This paper provides a comprehensive review on studies of sandstone type uranium deposits in the Ordos Basin, Northwest China. As the second largest sedimentary basin, the Ordos Basin has great potential for targeting sandstone type U mineralization. The newly found and explored Dongsheng and Diantou sandstone type uranium deposits are hosted in the Middle Jurassic Zhilou Formation. A large number of investigations have been conducted to trace the source rock compositions and relationship between lithic subarkose sandstone host rock and uranium mineralization. An optical microscopy study reveals two types of alteration associated with the U mineralization: chloritization and sericitization. Some unusual mineral structures, with compositional similarity to coffinite, have been identified in a secondary pyrite by SEM These mineral phases are proposed to be of bacterial origin, following high resolution mapping of uranium minerals and trace element determinations in situ. Moreover, geochemical studies of REE and trace elements constrained the mechanism of uranium enrichment, displaying LREE enrichment relative to HREE. Trace elements such as Pb, Mo and Ba have a direct relationship with uranium enrichment and can be used as index for mineralization. The source of uranium ore forming fluids and related geological processes have been studied using H, O and C isotope systematics of fluid inclusions in quartz veins and the calcite cement of sandstone rocks hosting U mineralization. Both H and O isotopic compositions of fluid inclusions reveal that ore forming fluids are a mixture of meteoric water and magmatic water. The C and S isotopes of the cementing material of sandstone suggest organic origin and bacterial sulfate reduction (BSR), providing an important clue for U mineralization. Discussion of the ore genesis shows that the greenish gray sandstone plays a crucial role during processes leading to uranium mineralization. Consequently, an oxidation-reduction model for sandstone-type uranium deposit is proposed, which can elucidate the source of uranium in the deposits of the Ordos Basin, based on the role of organic materials and sulfate reducing bacteria. We discuss the mechanism of uranium deposition responsible for the genesis of these large sandstone type uranium deposits in this unique sedimentary basin.

Subsurface Conditions Controlling Uranium Incorporation in Iron Oxides: A Redox Stable Sink

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fendorf, Scott

2016-04-05

Toxic metals and radionuclides throughout the U.S. Department of Energy Complex pose a serious threat to ecosystems and to human health. Of particular concern is the redox-sensitive radionuclide uranium, which is classified as a priority pollutant in soils and groundwaters at most DOE sites owing to its large inventory, its health risks, and its mobility with respect to primary waste sources. The goal of this research was to contribute to the long-term mission of the Subsurface Biogeochemistry Program by determining reactions of uranium with iron (hydr)oxides that lead to long-term stabilization of this pervasive contaminant. The research objectives of thismore » project were thus to (1) identify the (bio)geochemical conditions, including those of the solid-phase, promoting uranium incorporation in Fe (hydr)oxides, (2) determine the magnitude of uranium incorporation under a variety of relevant subsurface conditions in order to quantify the importance of this pathway when in competition with reduction or adsorption; (3) identify the mechanism(s) of U(VI/V) incorporation in Fe (hydr)oxides; and (4) determine the stability of these phases under different biogeochemical (inclusive of redox) conditions. Our research demonstrates that redox transformations are capable of achieving U incorporation into goethite at ambient temperatures, and that this transformation occurs within days at U and Fe(II) concentrations that are common in subsurface geochemical environments with natural ferrihydrites—inclusive of those with natural impurities. Increasing Fe(II) or U concentration, or initial pH, made U(VI) reduction to U(IV) a more competitive sequestration pathway in this system, presumably by increasing the relative rate of U reduction. Uranium concentrations commonly found in contaminated subsurface environments are often on the order of 1-10 μM, and groundwater Fe(II) concentrations can reach exceed 1 mM in reduced zones of the subsurface. The redox-driven U(V) incorporation mechanism may help to explain U retention in some geologic materials, improving our understanding of U-based geochronology and the redox status of ancient geochemical environments. Additionally, U(VI) may be incorporated within silicate minerals though encapsulation of U-bearing iron oxides, leading to a redox stable solid. Our research detailing previously unrecognized mechanism of U incorporation within sediment minerals may even lead to new approaches for in situ contamination remediation techniques, and will help refine models of U fate and transport in reduced subsurface zones.« less

Oxidative Corrosion of the UO 2 (001) Surface by Nonclassical Diffusion

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stubbs, Joanne E.; Biwer, Craig A.; Chaka, Anne M.

Uranium oxide is central to every stage of the nuclear fuel cycle, from mining through fuel fabrication and use, to waste disposal and environmental cleanup. Its chemical and mechanical stability are intricately linked to the concentration of interstitial O atoms within the structure and the oxidation state of U. We have previously shown that during corrosion of the UO2 (111) surface under either 1 atm O2 gas or oxygenated water at room temperature, oxygen interstitials diffuse into the substrate to form a superlattice with three-layer periodicity. In the current study, we present results from surface x-ray scattering that reveal themore » structure of the oxygen diffusion profile beneath the (001) surface. The first few layers below the surface oscillate strongly in their surface-normal lattice parameters, suggesting preferential interstitial occupation of every other layer below the surface, which is geometrically consistent with the interstitial network that forms below the oxidized (111) surface. Deeper layers are heavily contracted and indicate that the oxidation front penetrates ~52 Å below the (001) surface after 21 days of dry O2 gas exposure at ambient pressure and temperature. X-ray photoelectron spectroscopy indicates U is present as U(IV), U(V), and U(VI).« less

Theoretical modeling of the uranium 4f XPS for U(VI) and U(IV) oxides

NASA Astrophysics Data System (ADS)

Bagus, Paul S.; Nelin, Connie J.; Ilton, Eugene S.

2013-12-01

A rigorous study is presented of the physical processes related to X-Ray photoelectron spectroscopy, XPS, in the 4f level of U oxides, which, as well as being of physical interest in themselves, are representative of XPS in heavy metal oxides. In particular, we present compelling evidence for a new view of the screening of core-holes that extends prior understandings. Our analysis of the screening focuses on the covalent mixing of high lying U and O orbitals as opposed to the, more common, use of orbitals that are nominally pure U or pure O. It is shown that this covalent mixing is quite different for the initial and final, core-hole, configurations and that this difference is directly related to the XPS satellite intensity. Furthermore, we show that the high-lying U d orbitals as well as the U(5f) orbital may both contribute to the core-hole screening, in contrast with previous work that has only considered screening through the U(5f) shell. The role of modifying the U-O interaction by changing the U-O distance has been investigated and an unexpected correlation between U-O distance and XPS satellite intensity has been discovered. The role of flourite and octahedral crystal structures for U(IV) oxides has been examined and relationships established between XPS features and the covalent interactions in the different structures. The physical views of XPS satellites as arising from shake processes or as arising from ligand to metal charge transfers are contrasted; our analysis provides strong support that shake processes give a more fundamental physical understanding than charge transfer. Our theoretical studies are based on rigorous, strictly ab initio determinations of the electronic structure of embedded cluster models of U oxides with formal U(VI) and U(IV) oxidation states. Our results provide a foundation that makes it possible to establish quantitative relationships between features of the XPS spectra and materials properties.

Effects of nitrate on the stability of uranium in a bioreduced region of the subsurface.

PubMed

Wu, Wei-Min; Carley, Jack; Green, Stefan J; Luo, Jian; Kelly, Shelly D; Van Nostrand, Joy; Lowe, Kenneth; Mehlhorn, Tonia; Carroll, Sue; Boonchayanant, Benjaporn; Löfller, Frank E; Watson, David; Kemner, Kenneth M; Zhou, Jizhong; Kitanidis, Peter K; Kostka, Joel E; Jardine, Philip M; Criddle, Craig S

2010-07-01

The effects of nitrate on the stability of reduced, immobilized uranium were evaluated in field experiments at a U.S. Department of Energy site in Oak Ridge, TN. Nitrate (2.0 mM) was injected into a reduced region of the subsurface containing high levels of previously immobilized U(IV). The nitrate was reduced to nitrite, ammonium, and nitrogen gas; sulfide levels decreased; and Fe(II) levels increased then deceased. Uranium remobilization occurred concomitant with nitrite formation, suggesting nitrate-dependent, iron-accelerated oxidation of U(IV). Bromide tracer results indicated changes in subsurface flowpaths likely due to gas formation and/or precipitate. Desorption-adsorption of uranium by the iron-rich sediment impacted uranium mobilization and sequestration. After rereduction of the subsurface through ethanol additions, background groundwater containing high levels of nitrate was allowed to enter the reduced test zone. Aqueous uranium concentrations increased then decreased. Clone library analyses of sediment samples revealed the presence of denitrifying bacteria that can oxidize elemental sulfur, H(2)S, Fe(II), and U(IV) (e.g., Thiobacillus spp.), and a decrease in relative abundance of bacteria that can reduce Fe(III) and sulfate. XANES analyses of sediment samples confirmed changes in uranium oxidation state. Addition of ethanol restored reduced conditions and triggered a short-term increase in Fe(II) and aqueous uranium, likely due to reductive dissolution of Fe(III) oxides and release of sorbed U(VI). After two months of intermittent ethanol addition, sulfide levels increased, and aqueous uranium concentrations gradually decreased to <0.1 microM.

Efficacy of a Solution-Based Approach for Making Sodalite Waste Forms for an Oxide Reduction Salt Utilized in the Reprocessing of Used Uranium Oxide Fuel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Riley, Brian J.; Pierce, David A.; Frank, Steven M.

2015-04-01

This paper describes various approaches for making sodalite with a LiCl-Li2O oxide reduction salt used to recover uranium from used oxide fuel. The approaches include sol-gel and solution-based synthesis processes. As-made products were mixed with 5 and 10 mass% of a Na2O-B2O3-SiO2 glass binder and these, along with product without a binder, were heated using either a cold-press-and-sinter method or hot uniaxial pressing. The results demonstrate the limitation of sodalite yield due to the fast intermediate reactions between Na+ and Cl- to form halite in solution and Li2O and SiO2 to form lithium silicates (e.g., Li2SiO3 or Li2Si2O5) in themore » calcined and sintered pellets. The results show that pellets can be made with high sodalite fractions (~92 mass%) and low porosities using a solution-based approach and this LiCl-Li2O salt.« less

Chemical composition of phosphorites of the Phosphoria Formation

USGS Publications Warehouse

Gulbrandsen, R.A.

1966-01-01

The chemical composition, both major and minor constituents, of 60 samples of phosphorite from the Phosphoria Formation was determined. Major constituents of the average phosphorite are, by weight per cent: SiO2, 11??9; Al2O3, 1??7; Fe2O3,1??1; MgO, 0??3; CaO, 44??0; Na2O, 0??6; K2O, 0??5; total H2O, 2??2; H2O-, 0??6; TiO2, 0??1; P2O5, 30??5; CO2, 2??2; SO3, 1??8; F, 3??1; organic matter, 2??1; and oil, 0??2. Uranium averages 0??009 per cent. The phosphate mineral is basically apatite, Ca5(PO4)3F, with small but significant and variable substitutions-Na, Sr, U and Th for Ca, and CO3 and SO4 for PO4. Rare metals not associated with apatite are associated principally with the organic-matter component of the rocks. This group includes As, Ag, Cd, Cr, Cu, Mo, Ni, Sb, Se, V and Zn. Chromium is the most abundant, having a modal abundance of 0??1 per cent and a maximum concentration of 0??3 per cent. The average phosphorite is composed of approximately 80 per cent apatite, 10 per cent quartz, 5 per cent muscovite-illite, 2 per cent organic matter, 1 per cent dolomite-calcite, 1 per cent iron oxide, and 1 per cent other components. It is texturally a medium-grained pellet phosphorite. ?? 1966.

Decontamination of TCE- and U-rich waters by granular iron: Role of sorbed Fe(II)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Charlet, L.; Liger, E.; Gerasimo, P.

1998-01-01

Uranium (UO{sub 2}{sup 2+}) and chlorinated aliphatics [tetrachloroethane (PCE) and trichloroethane (TCE)] can be reduced and thus immobilized or degraded, respectively, by the same abiotic mechanism. In this mechanism the reduction reaction is coupled to the oxidation of Fe(II) sorbed on iron corrosion products such as hematite. This is indicated by the equilibrium E{sub h} values measured during uranium immobilization and PCE degradation reactions of zerovalent iron. These values fit closely with those measured in the Fe(II)-{alpha}Fe{sub 2}O{sub 3}-H{sub 2}O system (in the absence of U or PCE), not those of the Fe(o)/Fe(II) or H{sub 2}(g)/H{sub 2}O couples. Because ironmore » (II) is very unstable in environments that are not strictly anaerobic, Fe(o) serves as a source of Fe(II). The reduction kinetic rate, analyzed in detail for the reduction of U(VI), is found to be a function of the concentration of OH{sup {minus}}, Fe{sup 2+} and reactive surface sites, and is given in terms of sorbed species concentrations by {l_brace}d[U(VI)]{sub ads}{r_brace}/dt = {l_brace}{minus}k{prime}[{triple_bond}FeOFeOH{sup 0}][U(VI)]{sub ads}{r_brace}. This rate law applies to organic pollutants as well, as long as they can be reduced by surface Fe(II): {l_brace}d[Pollutant]{r_brace}/dt = {l_brace}{minus}k{prime}[{triple_bond}FeOFeOH{sup 0}][Pollutant]{r_brace}. This mechanism suggests new possibilities for the improvement of low-cost decontamination techniques for U- and chlorinated aliphatic-rich waters.« less

Nouvelle serie d'oxydes derives de la structure de α-U 3U 8: MIIUMo 4O 16

NASA Astrophysics Data System (ADS)

Lee, M. R.; Jaulmes, S.

1987-04-01

A new family of isotypical oxides MIIUMo 4O 16 ( MII = Mg,Mn,Cd,Ca,Hg,Sr,Pb) is identified. The structure of the compound with Ca was determined by X-ray diffraction. It is triclinic, space group P overline1 with a = 13.239(5) Å, b = 6.651(2) Å, c = 8.236(3) Å, α = 90°00(4), β = 90°38(4), γ = 120°16(3), Z = 2. The final index and the weighted Rw index are 0.049 and 0.040, respectively. The cell is related to the orthorhombic one of α-U 3O 8: a = 2 a0, b = -( a0 + b0)/2, c = 2 c0. The structure, reminiscent of that of α-U 3O 8, consists of chains of [Ca,U]O 7 pentagonal bipyramids and MoO 6 octahedra, running parallel to the c axis. The UO distances along the UOCaO chains are shortened to 1.77(1) Å. The uranyl ion was characterized by its IR spectrum.

Effect of Al(OH)3 on the sintering of UO2-Gd2O3 fuel pellets with addition of U3O8 from recycle

NASA Astrophysics Data System (ADS)

dos Santos, Lauro Roberto; Durazzo, Michelangelo; Urano de Carvalho, Elita Fontenele; Riella, Humberto Gracher

2017-09-01

The incorporation of gadolinium as burnable poison directly into nuclear fuel is important for reactivity compensation, which enables longer fuel cycles. The function of the burnable poison fuel is to control the neutron population in the reactor core during its startup and the beginning of the fuel burning cycle to extend the use of the fuel. The implementation of UO2-Gd2O3 poisoned fuel in Brazil has been proposed according to the future requirements established for the Angra-2 nuclear power plant. The UO2 powder used is produced from the Ammonium Uranyl Carbonate (AUC). The incorporation of Gd2O3 powder directly into the AUC-derived UO2 powder by dry mechanical blending is the most attractive process, because of its simplicity. Nevertheless, processing by this method leads to difficulties while obtaining sintered pellets with the minimum required density. The cause of the low densities is the bad sintering behavior of the UO2-Gd2O3 mixed fuel, which shows a blockage in the sintering process that hinders the densification. This effect has been overcome by microdoping of the fuel with small quantities of aluminum. The process for manufacturing the fuel inevitably generates uranium-rich scraps from various sources. This residue is reincorporated into the production process in the form of U3O8 powder additions. The addition of U3O8 also hinders densification in sintering. This study was carried out to investigate the influence of both aluminum and U3O8 additives on the density of fuel pellets after sintering. As the effects of these additives are counterposed, this work studied the combined effect thereof, seeking to find an applicable composition for the production process. The experimental results demonstrated the effectiveness of aluminum, in the form of Al(OH)3, as an additive to promote increase in the densification of the (U,Gd)O2 pellets during sintering, even with high additions of U3O8 recycled from the manufacturing process.

Theoretical analysis of uranium-doped thorium dioxide: Introduction of a thoria force field with explicit polarization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shields, A. E.; Ruiz Hernandez, S. E.; Leeuw, N. H. de, E-mail: DeLeeuwN@Cardiff.ac.uk

2015-08-15

Thorium dioxide is used industrially in high temperature applications, but more insight is needed into the behavior of the material as part of a mixed-oxide (MOX) nuclear fuel, incorporating uranium. We have developed a new interatomic potential model including polarizability via a shell model, and commensurate with a prominent existing UO{sub 2} potential, to conduct configurational analyses and to investigate the thermophysical properties of uranium-doped ThO{sub 2}. Using the GULP and Site Occupancy Disorder (SOD) computational codes, we have analyzed the distribution of low concentrations of uranium in the bulk material, where we have not observed the formation of uraniummore » clusters or the dominance of a single preferred configuration. We have calculated thermophysical properties of pure thorium dioxide and Th{sub (1−x)}U{sub x}O{sub 2} which generated values in very good agreement with experimental data.« less

The structure of liquid UO2-x in reducing gas atmospheres

NASA Astrophysics Data System (ADS)

Alderman, O. L. G.; Benmore, C. J.; Weber, J. K. R.; Skinner, L. B.; Tamalonis, A. J.; Sendelbach, S.; Hebden, A.; Williamson, M. A.

2017-02-01

High energy X-ray diffraction experiments performed on hypostoichiometric UO2-x liquids in reducing gas mixtures of 95%Ar:5%CO and 95%Ar:5%H2 are compared to that conducted in a pure Ar atmosphere [Skinner et al., Science 346, 984 (2014)]. The measurements are pertinent to severe accident scenarios at nuclear reactors, where core melts can encounter reducing conditions and further shed light on the oxide chemistry of the low valence states of uranium, particularly U(III), which become stable only at very high temperatures and low oxygen potentials. The radioactive samples were melted by floating small spheres of material using an aerodynamic levitator and heating with a laser beam. In the more reducing environments, a 1.7% shift to lower Q-values is observed in the position of the principal peak of the measured X-ray structure factors, compared to the more oxidizing Ar environment. This corresponds to an equivalent elongation in the U-U nearest neighbor distances and the U-U periodicity. The U-O peak (modal) bond-length, as measured from the real-space total correlation functions, is also observed to expand by 0.9-1.6% under reducing conditions, consistent with the presence of 15-27% U3+ cations, assuming constant U-O coordination number. The slightly larger U-U elongation, as compared to the U-O elongation, is interpreted as a slight increase in U-O-U bond angles. Difficulties concerning the determination of the hypostoichiometry, x, are discussed, along with the future directions for related research.

The structure of liquid UO 2-x in reducing gas atmospheres

DOE PAGES

Alderman, O. L. G.; Benmore, C. J.; Weber, J. K. R.; ...

2017-02-22

High energy X-ray diffraction experiments performed on hypostoichiometric UO 2-x liquids in reducing gas mixtures of 95%Ar:5%CO and 95%Ar:5%H 2 are compared to that conducted in a pure Ar atmosphere [Skinner et al., Science 346, 984 (2014)]. The measurements are pertinent to severe accident scenarios at nuclear reactors, where core melts can encounter reducing conditions and further shed light on the oxide chemistry of the low valence states of uranium, particularly U(III), which become stable only at very high temperatures and low oxygen potentials. The radioactive samples were melted by floating small spheres of material using an aerodynamic levitator andmore » heating with a laser beam. In the more reducing environments, a 1.7% shift to lower Q-values is observed in the position of the principal peak of the measured X-ray structure factors, compared to the more oxidizing Ar environment. This corresponds to an equivalent elongation in the U-U nearest neighbor distances and the U-U periodicity. The U-O peak (modal) bond-length, as measured from the real-space total correlation functions, is also observed to expand by 0.9–1.6% under reducing conditions, consistent with the presence of 15–27% U 3+ cations, assuming constant U-O coordination number. The slightly larger U-U elongation, as compared to the U-O elongation, is interpreted as a slight increase in U-O-U bond angles. Difficulties concerning the determination of the hypostoichiometry, x, are discussed, along with the future directions for related research.« less

Spectroscopic evidence for uranium bearing precipitates in vadose zone sediments at the Hanford 300-area site

USGS Publications Warehouse

Arai, Y.; Marcus, M.A.; Tamura, N.; Davis, J.A.; Zachara, J.M.

2007-01-01

Uranium (U) solid-state speciation in vadose zone sediments collected beneath the former North Process Pond (NPP) in the 300 Area of the Hanford site (Washington) was investigated using multi-scale techniques. In 30 day batch experiments, only a small fraction of total U (???7.4%) was released to artificial groundwater solutions equilibrated with 1% pCO2. Synchrotron-based micro-X-ray fluorescence spectroscopy analyses showed that U was distributed among at least two types of species: (i) U discrete grains associated with Cu and (ii) areas with intermediate U concentrations on grains and grain coatings. Metatorbernite (Cu[UO2]2[PO 4]2??8H2O) and uranophane (Ca[UO 2]2[SiO3(OH)]2?? 5H 2O) at some U discrete grains, and muscovite at U intermediate concentration areas, were identified in synchrotron-based micro-X-ray diffraction. Scanning electron microscopy/energy dispersive X-ray analyses revealed 8-10 ??m size metatorbernite particles that were embedded in C-, Al-, and Si-rich coatings on quartz and albite grains. In ??- and bulk-X-ray absorption structure (??-XAS and XAS) spectroscopy analyses, the structure of metatorbernite with additional U-C and U-U coordination environments was consistently observed at U discrete grains with high U concentrations. The consistency of the ??- and bulk-XAS analyses suggests that metatorbernite may comprise a significant fraction of the total U in the sample. The entrapped, micrometer-sized metatorbernite particles in C-, Al-, and Si-rich coatings, along with the more soluble precipitated uranyl carbonates and uranophane, likely control the long-term release of U to water associated with the vadose zone sediments. ?? 2007 American Chemical Society.

Anaerobic bioremediation of hexavalent uranium in groundwater by reductive precipitation with methanogenic granular sludge.

PubMed

Tapia-Rodriguez, Aida; Luna-Velasco, Antonia; Field, Jim A; Sierra-Alvarez, Reyes

2010-04-01

Uranium has been responsible for extensive contamination of groundwater due to releases from mill tailings and other uranium processing waste. Past evidence has confirmed that certain bacteria can enzymatically reduce soluble hexavalent uranium (U(VI)) to insoluble tetravalent uranium (U(IV)) under anaerobic conditions in the presence of appropriate electron donors. This paper focuses on the evaluation of anaerobic granular sludge as a source of inoculum for the bioremediation of uranium in water. Batch experiments were performed with several methanogenic anaerobic granular sludge samples and different electron donors. Abiotic controls consisting of heat-killed inoculum and non-inoculated treatments confirmed the biological removal process. In this study, unadapted anaerobic granular sludge immediately reduced U(VI), suggesting an intrinsic capacity of the sludge to support this process. The high biodiversity of anaerobic granular sludge most likely accounts for the presence of specific microorganisms capable of reducing U(VI). Oxidation by O(2) was shown to resolubilize the uranium. This observation combined with X-ray diffraction evidence of uraninite confirmed that the removal during anaerobic treatment was due to reductive precipitation. The anaerobic removal activity could be sustained after several respikes of U(VI). The U(VI) removal was feasible without addition of electron donors, indicating that the decay of endogenous biomass substrates was contributing electron equivalents to the process. Addition of electron donors, such as H(2) stimulated the removal of U(VI) to varying degrees. The stimulation was greater in sludge samples with lower endogenous substrate levels. The present work reveals the potential application of anaerobic granular sludge for continuous bioremediation schemes to treat uranium-contaminated water. Copyright (c) 2009 Elsevier Ltd. All rights reserved.

Statistical sampling of the distribution of uranium deposits using geologic/geographic clusters

USGS Publications Warehouse

Finch, W.I.; Grundy, W.D.; Pierson, C.T.

1992-01-01

The concept of geologic/geographic clusters was developed particularly to study grade and tonnage models for sandstone-type uranium deposits. A cluster is a grouping of mined as well as unmined uranium occurrences within an arbitrary area about 8 km across. A cluster is a statistical sample that will reflect accurately the distribution of uranium in large regions relative to various geologic and geographic features. The example of the Colorado Plateau Uranium Province reveals that only 3 percent of the total number of clusters is in the largest tonnage-size category, greater than 10,000 short tons U3O8, and that 80 percent of the clusters are hosted by Triassic and Jurassic rocks. The distributions of grade and tonnage for clusters in the Powder River Basin show a wide variation; the grade distribution is highly variable, reflecting a difference between roll-front deposits and concretionary deposits, and the Basin contains about half the number in the greater-than-10,000 tonnage-size class as does the Colorado Plateau, even though it is much smaller. The grade and tonnage models should prove useful in finding the richest and largest uranium deposits. ?? 1992 Oxford University Press.

A study on recovery of uranium in the anode basket residues delivered from the pyrochemical process of used nuclear fuel

NASA Astrophysics Data System (ADS)

Eun, H. C.; Kim, T. J.; Jang, J. H.; Kim, G. Y.; Park, S. B.; Yoon, D. S.; Kim, S. H.; Paek, S. W.; Lee, S. J.

2018-04-01

In this study, the chlorination of uranium oxide (UO2) using ammonium chloride and zirconium as chemical agents was conducted to recover the uranium in the anode basket residues from the pyrochemical process of used nuclear fuel. The chlorination of UO2 was predicted using thermodynamic equilibrium calculations. The experimental conditions for the chlorination were determined using a chlorination test with cerium oxide (CeO2). In the chlorination test, it was confirmed that UO2 was chlorinated into UCl3 at 320 °C, some UO2 remained without changes in the chemical form, and ZrO2, Zr2O, and ZrCl2 were generated as byproducts.

Radiation damage and nanocrystal formation in uranium-niobium titanates

NASA Astrophysics Data System (ADS)

Lian, J.; Wang, S. X.; Wang, L. M.; Ewing, R. C.

2001-07-01

Two uranium-niobium titanates, U 2.25Nb 1.90Ti 0.32O 9.8 and Nb 2.75U 1.20Ti 0.36O 10, formed during the synthesis of brannnerite (UTi 2O 6), a minor phase in titanate-based ceramics investigated for plutonium immobilization. These uranium titanates were subjected to 800 keV Kr 2+ irradiation from 30 to 973 K. The critical amorphization dose of the U-rich and Nb-rich titanates at room temperature were 4.72×10 17 and 5×10 17 ions/ m2, respectively. At elevated temperature, the critical amorphization dose increases due to dynamic thermal annealing. The critical amorphization temperature for both Nb-rich and U-rich titanates is ˜933 K under a 800 keV Kr 2+ irradiation. Above the critical amorphization temperature, nanocrystals with an average size of ˜15 nm were observed. The formation of nanocrystals is due to epitaxial recrystallization. At higher temperatures, an ion irradiation-induced nucleation-growth mechanism also contributes to the formation of nanocrystals.

Depleted uranium dioxide melting in cold crucible melter and production of granules from the melt for use in casks for spent nuclear fuel and radioactive wastes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gotovchikov, V.T.; Seredenko, V.A.; Shatalov, V.V.

2007-07-01

This paper describes the results of a joint research program between the Russian Research Institute of Chemical Technology and Oak Ridge National Laboratory in the United States to develop new radiation shielding materials for use in the construction of casks for spent nuclear fuel (SNF) and radioactive wastes. Research and development is underway to develop SNF storage, transport, and disposal casks using shielding made with two new depleted uranium dioxide (DUO{sub 2}) materials: a DUO{sub 2}-steel cermet, and, DUCRETE with DUAGG (DUO{sub 2} aggregate). Melting the DUO{sub 2} and allowing it to freeze will produce a near 100% theoretical densitymore » product and assures that the product produces no volatile materials upon subsequent heating. Induction cold-crucible melters (ICCM) are being developed for this specific application. An ICCM is, potentially, a high throughput low-cost process. Schematics of a pilot facility were developed for the production of molten DUO{sub 2} from DU{sub 3}O{sub 8} to produce granules <1 mm in diameter in a continuous mode of operation. Thermodynamic analysis was conducted for uranium-oxygen system in the temperature range from 300 to 4000 K in various gas mediums. Temperature limits of stability for various uranium oxides were determined. Experiments on melting DUO{sub 2} were carried out in a high frequency ICCM in a cold crucible with a 120 mm in diameter. The microstructure of molten DUO{sub 2} was studied and lattice parameters were determined. It was experimentally proved, and validated by X-ray analysis, that an opportunity exists to produce molten DUO{sub 2} from mixed oxides (primarily DU{sub 3}O{sub 8}) by reduction melting in ICCM. This will allow using DU{sub 3}O{sub 8} directly to make DUO{sub 2}-a separate unit operation to produce UO{sub 2} feed material is not needed. Experiments were conducted concerning the addition of alloying components, gadolinium et al. oxides, into the DUO{sub 2} melt while in the crucible. These additives improve neutron and gamma radiation shielding and operation properties of the final solids. Cermet samples of 50 wt % DUO{sub 2} were produced. (authors)« less

Conceptual Core Analysis of Long Life PWR Utilizing Thorium-Uranium Fuel Cycle

NASA Astrophysics Data System (ADS)

Rouf; Su'ud, Zaki

2016-08-01

Conceptual core analysis of long life PWR utilizing thorium-uranium based fuel has conducted. The purpose of this study is to evaluate neutronic behavior of reactor core using combined thorium and enriched uranium fuel. Based on this fuel composition, reactor core have higher conversion ratio rather than conventional fuel which could give longer operation length. This simulation performed using SRAC Code System based on library SRACLIB-JDL32. The calculation carried out for (Th-U)O2 and (Th-U)C fuel with uranium composition 30 - 40% and gadolinium (Gd2O3) as burnable poison 0,0125%. The fuel composition adjusted to obtain burn up length 10 - 15 years under thermal power 600 - 1000 MWt. The key properties such as uranium enrichment, fuel volume fraction, percentage of uranium are evaluated. Core calculation on this study adopted R-Z geometry divided by 3 region, each region have different uranium enrichment. The result show multiplication factor every burn up step for 15 years operation length, power distribution behavior, power peaking factor, and conversion ratio. The optimum core design achieved when thermal power 600 MWt, percentage of uranium 35%, U-235 enrichment 11 - 13%, with 14 years operation length, axial and radial power peaking factor about 1.5 and 1.2 respectively.

Calibration of the Lawrence Livermore National Laboratory Passive-Active Neutron Drum Shuffler for Measurement of Highly Enriched Uranium in Oxides within DOE-STD-3013-2000 Containers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mount, M E; O'Connell, W J

2005-06-03

Lawrence Livermore National Laboratory (LLNL) uses the LLNL passive-active neutron drum (PAN) shuffler (Canberra Model JCC-92) for accountability measurement of highly enriched uranium (HEU) oxide and HEU in mixed uranium-plutonium (U-Pu) oxide. In June 2002, at the 43rd Annual Meeting of the Institute of Nuclear Material Management, LLNL reported on an extensive effort to calibrate this shuffler, based on standards measurements and extensive simulations, for HEU oxides and mixed U-Pu oxides in thin-walled primary and secondary containers. In August 2002, LLNL began to also use DOE-STD-3013-2000 containers for HEU oxide and mixed U-Pu oxide. These DOE-STD-3013-2000 containers are comprised ofmore » a stainless steel convenience can enclosed in welded stainless steel primary and secondary containers. Compared to the double thin-walled containers, the DOE-STD-3013-2000 containers have substantially thicker walls, and the density of materials in these containers was found to extend over a greater range (1.35 g/cm{sup 3} to 4.62 g/cm{sup 3}) than foreseen for the double thin-walled containers. Further, the DOE-STD-3013-2000 Standard allows for oxides containing at least 30 wt% Pu plus U whereas the calibration algorithms for thin-walled containers were derived for virtually pure HEU or mixed U-Pu oxides. An initial series of Monte Carlo simulations of the PAN shuffler response to given quantities of HEU oxide and mixed U-Pu oxide in DOE-STD-3013-2000 containers was generated and compared with the response predicted by the calibration algorithms for thin-walled containers. Results showed a decrease on the order of 10% in the count rate, and hence a decrease in the calculated U mass for measured unknowns, with some varying trends versus U mass. Therefore a decision was made to develop a calibration algorithm for the PAN shuffler unique to the DOE-STD-3013-2000 container. This paper describes that effort and selected unknown item measurement results.« less

UTa{sub 2}O(S{sub 2}){sub 3}Cl{sub 6}: A ribbon structure containing a heterobimetallic 5d-5f M{sub 3} cluster

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wells, Daniel M.; Chan, George H.; Ellis, Donald E.

2010-02-15

A new solid-state compound containing a heterobimetallic cluster of U and Ta, UTa{sub 2}O(S{sub 2}){sub 3}Cl{sub 6}, has been synthesized and its structure has been characterized by single-crystal X-ray diffraction methods. UTa{sub 2}O(S{sub 2}){sub 3}Cl{sub 6} was synthesized from UCl{sub 4} and Ta{sub 1.2}S{sub 2} at 883 K. The O is believed to have originated in the Ta{sub 1.2}S{sub 2} reactant. The compound crystallizes in the space group P1-bar of the triclinic system. The structure comprises a UTa{sub 2} unit bridged by mu{sub 2}-S{sub 2} and mu{sub 3}-O groups. Each Ta atom bonds to two mu{sub 2}-S{sub 2}, the mu{submore » 3}-O, and two terminal Cl atoms. Each U atom bonds to two mu{sub 2}-S{sub 2}, the mu{sub 3}-O, and four Cl atoms. The Cl atoms bridge in pairs to neighboring U atoms to form a ribbon structure. The bond distances are normal and are consistent with formal oxidation states of +IV/+V/-II/-I/-I for U/Ta/O/S/Cl, respectively. The optical absorbance spectrum displays characteristic transition peaks near the absorption edge. Density functional theory was used to assign these peaks to transitions between S{sup 1-} valence-band states and empty U 5f-6d hybrid bands. Density-of-states analysis shows overlap between Ta 5d and U bands, consistent with metal-metal interactions. - The UTa2O(S2)3Cl6 cluster with completed coordination sphere around uranium« less

Surface reactions of ethanol over UO 2(100) thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

S. D. Senanayake; Mudiyanselage, K.; Burrell, A. K.

2015-10-08

The study of the reactions of oxygenates on well-defined oxide surfaces is important for the fundamental understanding of heterogeneous chemical pathways that are influenced by atomic geometry, electronic structure, and chemical composition. In this work, an ordered uranium oxide thin film surface terminated in the (100) orientation is prepared on a LaAlO 3 substrate and studied for its reactivity with a C-2 oxygenate, ethanol (CH 3CH 2OH). With the use of synchrotron X-ray photoelectron spectroscopy (XPS), we have probed the adsorption and desorption processes observed in the valence band, C 1s, O 1s, and U 4f to investigate the bondingmore » mode, surface composition, electronic structure, and probable chemical changes to the stoichiometric-UO 2(100) [smooth-UO 2(100)] and Ar +-sputtered UO 2(100) [rough-UO 2(100)] surfaces. Unlike UO 2(111) single crystal and UO 2 thin film, Ar-ion-sputtering of this UO 2(100) did not result in noticeable reduction of U cations. Upon ethanol adsorption (saturation occurred at 0.5 ML), only the ethoxy (CH 3CH 2O –) species is formed on smooth-UO 2(100) whereas initially formed ethoxy species are partially oxidized to surface acetate (CH3COO–) on the Ar +-sputtered UO 2(100) surface. Furthermore, all ethoxy and acetate species are removed from the surface between 600 and 700 K.« less

Extraction of uranium from tailings by sulfuric acid leaching with oxidants

NASA Astrophysics Data System (ADS)

Huang, Jing; Li, Mi; Zhang, Xiaowen; Huang, Chunmei; Wu, Xiaoyan

2017-06-01

Recovery of uranium have been performed by leaching uranium-containing tailings in sulfuric acid system with the assistance of HF, HClO4, H2O2 and MnO2. The effect of reagent dosage, sulfuric acid concentration, Liquid/solid ratio, reaction temperature and particle size on the leaching of uranium were investigated. The results show that addiction of HF, HClO4, H2O2 and MnO2 significantly increased the extraction of uranium under 1M sulphuric acid condition and under the optimum reaction conditions a dissolution fraction of 85% by HClO4, 90% by HF, 95% by H2O2 can be reached respectively. The variation of technological mineralogy properites of tailings during leaching process show that the assistants can break gangue effectively. These observations suggest that optimum oxidants could potentially influence the extraction of uranium from tailings even under dilute acid condition.

Effect of pH and Fe/U ratio on the U(VI) removal rate by the synergistic effect of Fe(II) and O2

NASA Astrophysics Data System (ADS)

Fu, Yukui; Luo, Yingfeng; Fang, Qi; Xie, Yanpei; Wang, Zhihong; Zhu, Xiangyu

2018-02-01

As for the decommissioned uranium deposits of acid in-situ leaching, both of the concentrations of U(VI) and Fe(II) are relatively high in groundwater. In the presence of O2, the oxidation of Fe(II) into Fe(III) that forms Fe-hydroxides could effectively remove U(VI) in the forms of sorption or co-precipitation. In this process, pH condition and Fe content will have a significant effect on the U(VI) removal rate by the synergistic effect of Fe(II) and O2. In the present work, a series of batch experiments were carried out to investigate the effect of pH values and Fe/U mass ratio on the U(VI) removal rate by the synergistic effect of Fe(II) and O2. Experiment results show that the removal rate of U(VI) is mainly controlled by pH and secondly by Fe/U mass ratio. In the neutral conditions with pH at 7 and 8, the removal rate of U(VI) reaches up to 90% for all solutions with different initial Fe(II) concentrations. The optimal pH for the removal rate of U(VI) is above 7. In the acidic conditions with pH below 6, the effect of Fe/U mass ratio on the removal rate of U(VI) becomes more obvious and the optimal Fe/U mass ratio for U(VI) removal is 1:2.

Density functional study of H2O molecule adsorption on α-U(001) surface.

PubMed

Huang, Shanqisong; Zeng, Xiu-Lin; Zhao, Feng-Qi; Ju, Xuehai

2016-04-01

Periodic density functional theory (DFT) calculations were performed to investigate the adsorption of H2O on U(001) surface. The metallic nature of uranium atom and different adsorption sites of U(001) surface play key roles in the H2O molecular dissociate reaction. The long-bridge site is the most favorable site of H2O-U(001) adsorption configuration. The triangle-center site of the H atom is the most favorable site of HOH-U(001) adsorption configuration. The interaction between H2O and U surface is more evident on the first layer than that on any other two sub-layers. The dissociation energy of one hydrogen atom from H2O is -1.994 to -2.215 eV on U(001) surface, while the dissociating energy decreases to -3.351 to -3.394 eV with two hydrogen atoms dissociating from H2O. These phenomena also indicate that the Oads can promote the dehydrogenation of H2O. A significant charge transfer from the first layer of the uranium surface to the H and O atoms is also found to occur, making the bonding partly ionic.

Synthesis and Characterization of an f-Block Terminal Parent Imido [U=NH] Complex: A Masked Uranium(IV) Nitride

PubMed Central

2014-01-01

Deprotonation of [U(TrenTIPS)(NH2)] (1) [TrenTIPS = N(CH2CH2NSiPri3)3] with organoalkali metal reagents MR (M = Li, R = But; M = Na–Cs, R = CH2C6H5) afforded the imido-bridged dimers [{U(TrenTIPS)(μ-N[H]M)}2] [M = Li–Cs (2a–e)]. Treatment of 2c (M = K) with 2 equiv of 15-crown-5 ether (15C5) afforded the uranium terminal parent imido complex [U(TrenTIPS)(NH)][K(15C5)2] (3c), which can also be viewed as a masked uranium(IV) nitride. The uranium–imido linkage was found to be essentially linear, and theoretical calculations suggested σ2π4 polarized U–N multiple bonding. Attempts to oxidize 3c to afford the neutral uranium terminal parent imido complex [U(TrenTIPS)(NH)] (4) resulted in spontaneous disproportionation to give 1 and the uranium–nitride complex [U(TrenTIPS)(N)] (5); this reaction is a new way to prepare the terminal uranium–nitride linkage and was calculated to be exothermic by −3.25 kcal mol–1. PMID:24697157

U redox fronts and kaolinisation in basement-hosted unconformity-related U ores of the Athabasca Basin (Canada): late U remobilisation by meteoric fluids

NASA Astrophysics Data System (ADS)

Mercadier, Julien; Cuney, Michel; Cathelineau, Michel; Lacorde, Mathieu

2011-02-01

Proterozoic basement-hosted unconformity-related uranium deposits of the Athabasca Basin (Saskatchewan, Canada) were affected by significant uranium redistribution along oxidation-reduction redox fronts related to cold and late meteoric fluid infiltration. These redox fronts exhibit the same mineralogical and geochemical features as the well-studied uranium roll-front deposits in siliclastic rocks. The primary hydrothermal uranium mineralisation (1.6-1.3 Ga) of basement-hosted deposits is strongly reworked to new disseminated ores comprising three distinctly coloured zones: a white-green zone corresponding to the previous clay-rich alteration halo contemporaneous with hydrothermal ores, a uranium front corresponding to the uranium deposition zone of the redox front (brownish zone, rich in goethite) and a hematite-rich red zone marking the front progression. The three zones directly reflect the mineralogical zonation related to uranium oxides (pitchblende), sulphides, iron minerals (hematite and goethite) and alumino-phosphate-sulphate (APS) minerals. The zoning can be explained by processes of dissolution-precipitation along a redox interface and was produced by the infiltration of cold (<50°C) meteoric fluids to the hydrothermally altered areas. U, Fe, Ca, Pb, S, REE, V, Y, W, Mo and Se were the main mobile elements in this process, and their distribution within the three zones was, for most of them, directly dependent on their redox potential. The elements concentrated in the redox fronts were sourced by the alteration of previously crystallised hydrothermal minerals, such as uranium oxides and light rare earth element (LREE)-rich APS. The uranium oxides from the redox front are characterised by LREE-enriched patterns, which differ from those of unconformity-related ores and clearly demonstrate their distinct conditions of formation. Uranium redox front formation is thought to be linked to fluid circulation episodes initiated during the 400-300 Ma period during uplift and erosion of the Athabasca Basin when it was near the Equator and to have been still active during the last million years. A major kaolinisation event was caused by changes in the fluid circulation regime, reworking the primary uranium redox fronts and causing the redistribution of elements originally concentrated in the uranium-enriched meteoric-related redox fronts.

U.sup.+4 generation in HTER

DOEpatents

Miller, William E [Naperville, IL; Gay, Eddie C [Park Forest, IL; Tomczuk, Zygmunt [Homer Glen, IL

2006-03-14

A improved device and process for recycling spent nuclear fuels, in particular uranium metal, that facilitates the refinement and recovery of uranium metal from spent metallic nuclear fuels. The electrorefiner device comprises two anodes in predetermined spatial relation to a cathode. The anodese have separate current and voltage controls. A much higher voltage than normal for the electrorefining process is applied to the second anode, thereby facilitating oxidization of uranium (III), U.sup.+, to uranium (IV), U.sup.+4. The current path from the second anode to the cathode is physically shorter than the similar current path from the second anode to the spent nuclear fuel contained in a first anode shaped as a basket. The resulting U.sup.+4 oxidizes and solubilizes rough uranium deposited on the surface of the cathode. A softer uranium metal surface is left on the cathode and is more readily removed by a scraper.

Formation of 238U 16O and 238U 18O observed by time-resolved emission spectroscopy subsequent to laser ablation

DOE PAGES

Weisz, David G.; Crowhurst, Jonathan C.; Siekhaus, Wigbert J.; ...

2017-07-17

Here, we have measured vibronic emission spectra of an oxide of uranium formed after laser ablation of the metal in gaseous oxygen. Specifically, we have measured the time-dependent relative intensity of a band located at approximately 593.6 nm in 16O 2. This band grew in intensity relative to neighboring atomic features as a function time in an oxygen environment but was relatively invariant with time in argon. In addition, we have measured the spectral shift of this band in an 18O 2 atmosphere. Based on this shift, and by comparison with earlier results obtained from free-jet expansion and laser excitation,more » we can confirm that the oxide in question is UO, consistent with recent reports based on laser ablation in 16O 2 only.« less

Formation of 238U 16O and 238U 18O observed by time-resolved emission spectroscopy subsequent to laser ablation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weisz, David G.; Crowhurst, Jonathan C.; Siekhaus, Wigbert J.

Here, we have measured vibronic emission spectra of an oxide of uranium formed after laser ablation of the metal in gaseous oxygen. Specifically, we have measured the time-dependent relative intensity of a band located at approximately 593.6 nm in 16O 2. This band grew in intensity relative to neighboring atomic features as a function time in an oxygen environment but was relatively invariant with time in argon. In addition, we have measured the spectral shift of this band in an 18O 2 atmosphere. Based on this shift, and by comparison with earlier results obtained from free-jet expansion and laser excitation,more » we can confirm that the oxide in question is UO, consistent with recent reports based on laser ablation in 16O 2 only.« less

Isotopic signature and nano-texture of cesium-rich micro-particles: Release of uranium and fission products from the Fukushima Daiichi Nuclear Power Plant.

PubMed

Imoto, Junpei; Ochiai, Asumi; Furuki, Genki; Suetake, Mizuki; Ikehara, Ryohei; Horie, Kenji; Takehara, Mami; Yamasaki, Shinya; Nanba, Kenji; Ohnuki, Toshihiko; Law, Gareth T W; Grambow, Bernd; Ewing, Rodney C; Utsunomiya, Satoshi

2017-07-14

Highly radioactive cesium-rich microparticles (CsMPs) released from the Fukushima Daiichi Nuclear Power Plant (FDNPP) provide nano-scale chemical fingerprints of the 2011 tragedy. U, Cs, Ba, Rb, K, and Ca isotopic ratios were determined on three CsMPs (3.79-780 Bq) collected within ~10 km from the FDNPP to determine the CsMPs' origin and mechanism of formation. Apart from crystalline Fe-pollucite, CsFeSi 2 O 6  · nH 2 O, CsMPs are comprised mainly of Zn-Fe-oxide nanoparticles in a SiO 2 glass matrix (up to ~30 wt% of Cs and ~1 wt% of U mainly associated with Zn-Fe-oxide). The 235 U/ 238 U values in two CsMPs: 0.030 (±0.005) and 0.029 (±0.003), are consistent with that of enriched nuclear fuel. The values are higher than the average burnup estimated by the ORIGEN code and lower than non-irradiated fuel, suggesting non-uniform volatilization of U from melted fuels with different levels of burnup, followed by sorption onto Zn-Fe-oxides. The nano-scale texture and isotopic analyses provide a partial record of the chemical reactions that occurred in the fuel during meltdown. Also, the CsMPs were an important medium of transport for the released radionuclides in a respirable form.

Current status of U{sub 3}Si{sub 2} fuel element fabrication in Brazil

DOE Office of Scientific and Technical Information (OSTI.GOV)

Durazzo, M.; Carvalho, E.F. Urano de; Saliba-Silva, A.M.

2008-07-15

IPEN has been working for increasing radioisotope production in order to supply the expanding demand for radiopharmaceutical medicines requested by the Brazilian welfare. To reach this objective, the IEA-R1 research reactor power capacity was recently increased from 2 MW to 4 MW. Since 1988 IPEN has been manufacturing its own fuel element, initially based on U{sub 3}O{sub 8}-Al dispersion fuel plates with 2.3 gU/cm{sup 3}. To support the reactor power increase, higher uranium density in the fuel plate meat had to be achieved for better irradiation flux and also to minimize the irradiated fuel elements to be stored. Uranium silicidemore » was the chosen option and the fuel fabrication development started with the support of the IAEA BRA/4/047 Technical Cooperation Project. This paper describes the results of this program and the current status of silicide fuel fabrication and its qualification. (author)« less

Uranium speciation as a function of depth in contaminated hanford sediments--a micro-XRF, micro-XRD, and micro- and bulk-XAFS study.

PubMed

Singer, David M; Zachara, John M; Brown, Gordon E

2009-02-01

The distribution and speciation of U and Cu in contaminated vadose zone and aquifer sediments from the U.S. DOE Hanford site (300 Area) were determined using a combination of synchrotron-based micro-X-ray fluorescence (microXRF) imaging, micro-X-ray absorption near edge structure (microXANES) spectroscopy, and micro-X-ray diffraction (microXRD) techniques combined with bulk U LIII-edge X-ray absorption fine structure (XAFS) spectroscopy. Samples were collected from within the inactive North Process Pond (NPP2) at 8 ft (2.4 m, NPP2-8) depth and 12 ft (3.7 m, NPP2-12) depth in the vadose zone, and fines were isolated from turbid groundwater just below the water Table (12-14 ft, approximately 4 m, NPP2-GW). microXRF imaging, microXRD, and microXANES spectroscopy revealed two major U occurrences within the vadose and groundwater zones: (1) low to moderate concentrations of U(VI) associated with fine-textured grain coatings that were consistently found to contain clinochlore (referred to here as chlorite) observed in all three samples, and (2) U(VI)-Cu(II) hotspots consisting of micrometer-sized particles associated with surface coatings on grains of muscovite and chlorite observed in samples NPP2-8' and NPP2-GW. In the aquifer fines (NPP2-GW), these particles were identified as cuprosklodowskite (cps: Cu[(UO2)(SiO2OH)]2 x 6H2O) and metatorbernite (mtb: Cu(UO2)2(PO4)2 x 8H2O). In contrast, the U-Cu-containing particles in the vadose zone were X-ray amorphous. Analyses of U LIII-edge XAFS spectra by linear-combination fitting indicated that U speciation consisted of (1) approximately 75% uranyl sorbed to chlorite and approximately 25% mtb-like X-ray amorphous U-Cu-phosphates (8 ft depth), (2) nearly 100% sorbed uranyl (12 ft depth), and (3) approximately 70% uranyl sorbed to chlorite and approximately 30% cps/mtb (groundwater zone). These findings suggest that dissolution of U(VI)-Cu(II)-bearing solids as well as desorption of U(VI), mainly from phyllosilicates, are important persistent sources of U(VI) to the associated uranium groundwater plume in Hanford Area 300.

Behavior of Colorado Plateau uranium minerals during oxidation

USGS Publications Warehouse

Garrels, Robert Minard; Christ, C.L.

1956-01-01

Uranium occurs as U(VI) and U(IV) in minerals of the Colorado Plateau ores. The number of species containing U(VI) is large, but only two U(IV) minerals are known from the Plateau: uraninite, and oxide, and coffinite, a hydroxy-silicate. These oxidize to yield U(VI) before reacting significantly with other mineral constituents. Crystal-structure analysis has shown that U(VI) invariable occurs as uranyl ion, UO2+2. Uranyl ion may form complex carbonate or sulfate ions with resulting soluble compounds, but only in the absence of quinquevalent vanadium, arsenic, or phosphorous. In the presence of these elements in the +5 valence state, the uranyl ion is fixed in insoluble layer compounds formed by union of uranyl ion with orthovanadate, orthophosphate, or orthoarsenate. Under favorable conditions UO2+2 may react to form the relatively insoluble rutherfordine, UO2CO3, or hydrated uranyl hydroxides. These are rarely found on the Colorado Plateau as opposed to their excellent development in other uraniferous areas, a condition which is apparently related to the semiarid climate and low water table of the Plateau. Uranium may also be fixed as uranyl silicate, but little is known about minerals of this kind. In the present study emphasis has been placed on a detailing of the chemical and crystal structural changes which occur in the oxidation paragenetic sequence.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weydert, M.; Brennan, J.G.; Andersen, R.A.

Reaction of (MeC{sub 5}H{sub 4}){sub 3}UX (X = Cl, MeC{sub 5}H{sub 4}) with t-BuLi affords the tertiary alkyl complex (MeC{sub 5}H{sub 4}){sub 3}U(t-Bu). Despite uranium(IV) generally being the preferred oxidation state in organometallic systems, (MeC{sub 5}H{sub 4}){sub 3}U(t-Bu) reacts with Lewis bases (L = PMe{sub 3}, THF, RCN, RNC) to yield the reduced uranium(III) base adducts (MeC{sub 5}H{sub 4}){sub 3}U(L). Carbon monoxide undergoes migratory insertion into the metal tertiary alkyl bond. The resulting acyl derivative decomposes at 90{degree}C to yield insoluble uranium-containing products and a mixture of tert-butyltoluenes by ring expansion of a methylcyclopentadienyl ligand. Ethylene also undergoes migratory insertionmore » into the metal tertiary alkyl bond. No subsequent insertion of ethylene into the metal carbon bond takes place after the first equivalent has inserted. In marked contrast, reaction of various (MeC{sub 5}H{sub 4}){sub 3}ThX (X = Cl, I, MeC{sub 5}H{sub 4}, O-2,6-Me{sub 2}C{sub 6}H{sub 3}, OTs) compounds with t-BuLi gave intractable materials. However, reaction of the cationic species [(RC{sub 5}H{sub 4}){sub 3}Th](BPh{sub 4}) (R = Me{sub 3}Si, t-Bu) with t-BuLi yields the new thorium hydrides (RC{sub 5}H{sub 4}){sub 3}ThH. 40 refs., 2 figs.« less

Characterization of the Kinetics of NF3-Fluorination of NpO2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Casella, Andrew M.; Scheele, Randall D.; McNamara, Bruce K.

2015-12-23

The exploitation of selected actinide and fission product fluoride volatilities has long been considered as a potentially attractive compact method for recycling used nuclear fuels to avoid generating the large volumes of radioactive waste arising from aqueous reprocessing [1-7]. The most developed process uses the aggressive and hazardous fluorinating agents hydrogen fluoride (HF) and/or molecular fluorine (F2) at high temperatures to volatilize the greatest fraction of the used nuclear fuel into a single gas stream. The volatilized fluorides are subsequently separated using a series of fractionation and condensation columns to recover the valuable fuel constituents and fission products. In pursuitmore » of a safer and less complicated approach, we investigated an alternative fluoride volatility-based process using the less hazardous fluorinating agent nitrogen trifluoride (NF3) and leveraging its less aggressive nature to selectively evolve fission product and actinide fluorides from the solid phase based on their reaction temperatures into a single recycle stream [8-15]. In this approach, successive isothermal treatments using NF3 will first evolve the more thermally susceptible used nuclear fuel constituents leaving the other constituents in the residual solids until subsequent isothermal temperature treatments cause these others to volatilize. During investigation of this process, individual neat used fuel components were treated with isothermal NF3 in an attempt to characterize the kinetics of each fluorination reaction to provide input into the design of a new volatile fluoride separations approach. In these directed investigations, complex behavior was observed between NF3 and certain solid reactants such as the actinide oxides of uranium, plutonium, and neptunium. Given the similar thermal reaction susceptibilities of neptunium oxide (NpO2) and uranium dioxide (UO2) and the importance of Np and U, we initially focused our efforts on determining the reaction kinetic parameters for NpO2. Characterizing the NF3 fluorination of NpO2 using established models for gas-solid reactions [16] proved unsuccessful so we developed a series of successive fundamental reaction mechanisms to characterize the observed successive fluorination reactions leading to production of the volatile neptunium hexafluoride (NpF6).« less

Effect of bicarbonate on aging and reactivity of nanoscale zerovalent iron (nZVI) toward uranium removal.

PubMed

Hua, Yilong; Wang, Wei; Huang, Xiaoyue; Gu, Tianhang; Ding, Dexin; Ling, Lan; Zhang, Wei-Xian

2018-06-01

Bicarbonate, ubiquitous in natural and waste waters is an important factor regulating the rate and efficiency of pollutant separation and transformation. For example, it can form complexes with U(VI) in the aqueous phase and at the solid-water interface. In this work, we investigated the effect of bicarbonate on the aging of nanoscale zero-valent (nZVI) in the context of U(VI) reduction and removal from wastewater. For fresh nZVI, over 99% aqueous uranium was separated in less than 10 min, of which 83% was reduced from U(VI) to U(IV). When nZVI was aged in water, its activity for U(VI) sequestration and reduction was significantly reduced. Batch experiments showed that for nZVI aged in the presence of 10 mM bicarbonate, only 20.3% uranium was reduced to U(IV) after 6 h reactions. Characterizations of the iron nanoparticles with spherical aberration corrected scanning transmission electron microscopy (Cs-STEM) suggest that in fresh nZVI, uranium was concentrated at the nanoparticle center; whereas in nZVI aged in bicarbonate, uranium was largely deposited on the outer surface of the nanoparticles. Furthermore, aged nZVI without bicarbonate contained more lepidocrocite (γ-FeOOH) while aged nZVI in the presence of bicarbonate had more magnetite/maghemite (Fe 3 O 4 /γ-Fe 2 O 3 ). This could be attributed to the formation of carbonate green rust and pH buffer effect of . Primary mechanisms for U(VI) removal with nZVI include reduction, sorption and/or precipitation. Results demonstrate that bicarbonate alter the aging products of nZVI, and reduces the separation efficiency and reduction capability for uranium removal. Copyright © 2018. Published by Elsevier Ltd.

Uranium Isotope Ratios in Modern and Precambrian Soils

NASA Astrophysics Data System (ADS)

DeCorte, B.; Planavsky, N.; Wang, X.; Auerbach, D. J.; Knudsen, A. C.

2015-12-01

Uranium isotopes (δ238U values) are an emerging paleoredox proxy that can help to better understand the redox evolution of Earth's surface environment. Recently, uranium isotopes have been used to reconstruct ocean and atmospheric redox conditions (Montoya-Pino et al., 2010; Brennecka et al., 2011; Kendall et al., 2013; Dahl et al., 2014). However, to date, there have not been studies on paleosols, despite that paleosols are, arguably better suited to directly tracking the redox conditions of the atmosphere. Sedimentary δ238U variability requires the formation of the soluble, oxidized form of U, U(VI). The formation of U(VI) is generally thought to require oxygen levels orders of magnitude higher than prebiotic levels. Without significant U mobility, it would have been impossible to develop isotopically distinct pools of uranium in ancient Earth environments. Conversely, an active U redox cycle leads to significant variability in δ238U values. Here we present a temporally and geographically expansive uranium isotope record from paleosols and modern soils to better constrain atmospheric oxygen levels during the Precambrian. Preliminary U isotope measurements of paleosols are unfractionated (relative to igneous rocks), possibly because of limited fractionation during oxidation (e.g., {Wang, 2015 #478}) or insufficient atmospheric oxygen levels to oxidize U(IV)-bearing minerals in the bedrock. Further U isotope measurements of paleosols with comparison to modern soils will resolve this issue.

238U, and its decay products, in grasses from an abandoned uranium mine

NASA Astrophysics Data System (ADS)

Childs, Edgar; Maskall, John; Millward, Geoffrey

2016-04-01

Bioaccumulation of radioactive contaminants by plants is of concern particularly where the sward is an essential part of the diet of ruminants. The abandoned South Terras uranium mine, south west England, had primary deposits of uraninite (UO2) and pitchblende (U3O8), which contained up to 30% uranium. When the mine was active uranium and radium were extracted but following closure it was abandoned without remediation. Waste rock and gangue, consisting of inefficiently processed minerals, were spread around the site, including a field where ruminants are grazed. Here we report the activity concentrations of 238U, 235U 214,210Pb, and the concentrations of selected metals in the soils, roots and leaves of grasses taken from the contaminated field. Soil samples were collected at the surface, and at 30 cm depth, using an auger along a 10-point transect in the field from the foot of a waste heap. Whole, individual grass plants were removed with a spade, ensuring that their roots were intact. The soils and roots and grass leaves were freeze-dried. Activity concentrations of the radionuclides were determined by gamma spectroscopy, following 30 days incubation for development of secular equilibrium. Dried soils, roots and grasses were also digested in aqua regia and the concentrations of elements determined by ICP techniques. Maximum activity concentrations of 238U, 235U, 214Pb and 210Pb surface soils were 63,300, 4,510, 23,300 and 49,400 Bq kg-1, respectively. The mean 238U:235U ratio was 11.8 ± 1.8, an order of magnitude lower than the natural value of 138, indicating disequilibrium within the decay chain due to mineral processing. Radionuclides in the roots had 5 times lower concentration and only grass leaves in the vicinity of the waste heap had measureable values. The mean soil to root transfer factor for 238U was 36%, the mean root to leaf was 3% and overall only 0.7% of 238U was transferred from the soil to the leaves. The roots contained 0.8% iron, possibly as iron plaque acting to mediate 238U transfer within the plants. The results are discussed in the context of remediation of grazing land contaminated with radionuclides.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Yingjie, E-mail: yzx@ansto.gov.au; Bhadbhade, Mohan; Karatchevtseva, Inna

Three new coordination polymers of uranium(VI) with pyromellitic acid (H{sub 4}btca) have been synthesized and structurally characterized. (ED)[(UO{sub 2})(btca)]·(DMSO)·3H{sub 2}O (1) (ED=ethylenediammonium; DMSO=dimethylsulfoxide) has a lamellar structure with intercalation of ED and DMSO. (NH{sub 4}){sub 2}[(UO{sub 2}){sub 6}O{sub 2}(OH){sub 6}(btca)]·~6H{sub 2}O (2) has a 3D framework built from 7-fold coordinated uranyl trinuclear units and btca ligands with 1D diamond-shaped channels (~8.5 Å×~8.6 Å). [(UO{sub 2}){sub 2}(H{sub 2}O)(btca)]·4H{sub 2}O (3) has a 3D network constructed by two types of 7-fold coordinated uranium polyhedron. The unique μ{sub 5}-coordination mode of btca in 3 enables the formation of 1D olive-shaped large channels (~4.5more » Å×~19 Å). Vibrational modes, thermal stabilities and fluorescence properties have been investigated. - Graphical abstract: Table of content: three new uranium(VI) coordination polymers with pyromellitic acid (H{sub 4}btca) have been synthesized via room temperature and hydrothermal synthesis methods, and structurally characterized. Two to three dimensional (3D) frameworks are revealed. All 3D frameworks have unique 1D large channels. Their vibrational modes, thermal stabilities and photoluminescence properties have been investigated. - Highlights: • Three new coordination polymers of U(VI) with pyromellitic acid (H{sub 4}btca). • Structures from a 2D layer to 3D frameworks with unique 1D channels. • Unusual µ{sub 5}-(η{sub 1}:η{sub 2}:η{sub 1}:η{sub 2:}η{sub 1}) coordination mode of btca ligand. • Vibrational modes, thermal stabilities and luminescent properties reported.« less

Characterization of cores from an in-situ recovery mined uranium deposit in Wyoming: Implications for post-mining restoration

DOE Office of Scientific and Technical Information (OSTI.GOV)

WoldeGabriel, G.; Boukhalfa, H.; Ware, S. D.

In-situ recovery (ISR) of uranium (U) from sandstone-type roll-front deposits is a technology that involves the injection of solutions that consist of ground water fortified with oxygen and carbonate to promote the oxidative dissolution of U, which is pumped to recovery facilities located at the surface that capture the dissolved U and recycle the treated water. The ISR process alters the geochemical conditions in the subsurface creating conditions that are more favorable to the migration of uranium and other metals associated with the uranium deposit. There is a lack of clear understanding of the impact of ISR mining on themore » aquifer and host rocks of the post-mined site and the fate of residual U and other metals within the mined ore zone. We performed detailed petrographic, mineralogical, and geochemical analyses of several samples taken from about 7 m of core of the formerly the ISR-mined Smith Ranch–Highland uranium deposit in Wyoming. We show that previously mined cores contain significant residual uranium (U) present as coatings on pyrite and carbonaceous fragments. Coffinite was identified in three samples. Core samples with higher organic (> 1 wt.%) and clay (> 6–17 wt.%) contents yielded higher 234U/ 238U activity ratios (1.0–1.48) than those with lower organic and clay fractions. The ISR mining was inefficient in mobilizing U from the carbonaceous materials, which retained considerable U concentrations (374–11,534 ppm). This is in contrast with the deeper part of the ore zone, which was highly depleted in U and had very low 234U/ 238U activity ratios. This probably is due to greater contact with the lixiviant (leaching solution) during ISR mining. EXAFS analyses performed on grains with the highest U and Fe concentrations reveal that Fe is present in a reduced form as pyrite and U occurs mostly as U(IV) complexed by organic matter or as U(IV) phases of carbonate complexes. Moreover, U–O distances of ~ 2.05 Å were noted, indicating the potential formation of other poorly defined U(IV/VI) species. We also noted a small contribution from Udouble bond; length as m-dashO at 1.79 Å, which indicates that U is partially oxidized. There is no apparent U–S or U–Fe interaction in any of the U spectra analyzed. However, SEM analysis of thin sections prepared from the same core material reveals surficial U associated with pyrite which is probably a minor fraction of the total U present as thin coatings on the surface of pyrite. Our data show the presence of different structurally variable uranium forms associated with the mined cores. U associated with carbonaceous materials is probably from the original U mobilization that accumulated in the organic matter-rich areas under reducing conditions during shallow burial diagenesis. U associated with pyrite represents a small fraction of the total U and was likely deposited as a result of chemical reduction by pyrite. Our data suggest that areas rich in carbonaceous materials had limited exposure to the lixiviant solution, continue to be reducing, and still hold significant U resources. Because of their limited access to fluid flow, these areas might not contribute significantly to post-mining U release or attenuation. Areas with pyrite that are accessible to fluids seem to be more reactive and could act as reductants and facilitate U reduction and accumulation, limiting its migration.« less

Characterization of cores from an in-situ recovery mined uranium deposit in Wyoming: Implications for post-mining restoration

DOE PAGES

WoldeGabriel, G.; Boukhalfa, H.; Ware, S. D.; ...

2014-10-08

In-situ recovery (ISR) of uranium (U) from sandstone-type roll-front deposits is a technology that involves the injection of solutions that consist of ground water fortified with oxygen and carbonate to promote the oxidative dissolution of U, which is pumped to recovery facilities located at the surface that capture the dissolved U and recycle the treated water. The ISR process alters the geochemical conditions in the subsurface creating conditions that are more favorable to the migration of uranium and other metals associated with the uranium deposit. There is a lack of clear understanding of the impact of ISR mining on themore » aquifer and host rocks of the post-mined site and the fate of residual U and other metals within the mined ore zone. We performed detailed petrographic, mineralogical, and geochemical analyses of several samples taken from about 7 m of core of the formerly the ISR-mined Smith Ranch–Highland uranium deposit in Wyoming. We show that previously mined cores contain significant residual uranium (U) present as coatings on pyrite and carbonaceous fragments. Coffinite was identified in three samples. Core samples with higher organic (> 1 wt.%) and clay (> 6–17 wt.%) contents yielded higher 234U/ 238U activity ratios (1.0–1.48) than those with lower organic and clay fractions. The ISR mining was inefficient in mobilizing U from the carbonaceous materials, which retained considerable U concentrations (374–11,534 ppm). This is in contrast with the deeper part of the ore zone, which was highly depleted in U and had very low 234U/ 238U activity ratios. This probably is due to greater contact with the lixiviant (leaching solution) during ISR mining. EXAFS analyses performed on grains with the highest U and Fe concentrations reveal that Fe is present in a reduced form as pyrite and U occurs mostly as U(IV) complexed by organic matter or as U(IV) phases of carbonate complexes. Moreover, U–O distances of ~ 2.05 Å were noted, indicating the potential formation of other poorly defined U(IV/VI) species. We also noted a small contribution from Udouble bond; length as m-dashO at 1.79 Å, which indicates that U is partially oxidized. There is no apparent U–S or U–Fe interaction in any of the U spectra analyzed. However, SEM analysis of thin sections prepared from the same core material reveals surficial U associated with pyrite which is probably a minor fraction of the total U present as thin coatings on the surface of pyrite. Our data show the presence of different structurally variable uranium forms associated with the mined cores. U associated with carbonaceous materials is probably from the original U mobilization that accumulated in the organic matter-rich areas under reducing conditions during shallow burial diagenesis. U associated with pyrite represents a small fraction of the total U and was likely deposited as a result of chemical reduction by pyrite. Our data suggest that areas rich in carbonaceous materials had limited exposure to the lixiviant solution, continue to be reducing, and still hold significant U resources. Because of their limited access to fluid flow, these areas might not contribute significantly to post-mining U release or attenuation. Areas with pyrite that are accessible to fluids seem to be more reactive and could act as reductants and facilitate U reduction and accumulation, limiting its migration.« less

Corrosion Experiments Using Spherical Uranium Powders

DOE Office of Scientific and Technical Information (OSTI.GOV)

Powell, G. L.; Siekhaus, W. J.; Teslich, N. E.

2017-02-01

Corrosion experiments using spherical U powders are continuing with scanning electron microscopy (SEM) showing that the particles are highly textured, 5 m to 25 m diameters with 4% larger particles that are fused smaller particles. This U has a high specific surface area with no corners or back-sides, is well annealed with no machining work, and coated with a coherent oxide film, 30 nm to 300 nm thick. Exposure of this powder to low vapor pressure H 2O in the absence of O 2, i.e., a vacuum desiccator, resulted in a coherent oxide film growth of ~1 m/y, ~ 10Xmore » the growth rate in ambient air, displaying fracture along the growth plane at ~300 nm.« less

Geochemical investigations by the U.S. Geological Survey on uranium mining, milling, and environmental restoration

USGS Publications Warehouse

Landa, Edward R.; Cravotta, Charles A.; Naftz, David L.; Verplanck, Philip L.; Nordstrom, D. Kirk; Zielinski, Robert A.

2000-01-01

Recent research by the U.S. Geological Survey has characterized contaminant sources and identified important geochemical processes that influence transport of radionuclides from uranium mining and milling wastes. 1) Selective extraction studies indicated that alkaline earth sulfates and hydrous ferric oxides are important hosts of 226Ra in uranium mill tailings. The action of sulfate-reducing and ironreducing bacteria on these phases was shown to enhance release of radium, and this adverse result may temper decisions to dispose of uranium mill tailings in anaerobic environments. 2) Field studies have shown that although surface-applied sewage sludge/wood chip amendments aid in revegetating pyritic spoil, the nitrogen in sludge leachate can enhance pyrite oxidation, acidification of groundwater, and the consequent mobilization of metals and radionuclides. 3) In a U.S. Environmental Protection Agencyfunded study, three permeable reactive barriers consisting of phosphate-rich material, zero-valent iron, or amorphous ferric oxyhydroxide have been installed at an abandoned uranium upgrader facility near Fry Canyon, UT. Preliminary results indicate that each of the permeable reactive barriers is removing the majority of the uranium from the groundwater. 4) Studies on the geochemistry of rare earth elements as analogues for actinides such as uranium and thorium in acid mine drainage environments indicate high mobility under acid-weathering conditions but measurable attenuation associated with iron and aluminum colloid formation. Mass balances from field and laboratory studies are being used to quantify the amount of attenuation. 5) A field study in Colorado demonstrated the use of 234U/238U isotopic ratio measurements to evaluate contamination of shallow groundwater with uranium mill effluent.

Multiscale structural characterizations of mixed U(iv)-An(iii) oxalates (An(iii) = Pu or Am) combining XAS and XRD measurements.

PubMed

Arab-Chapelet, B; Martin, P M; Costenoble, S; Delahaye, T; Scheinost, A C; Grandjean, S; Abraham, F

2016-04-28

Mixed actinide(III,IV) oxalates of the general formula M2.2UAn(C2O4)5·nH2O (An = Pu or Am and M = H3O(+) and N2H5(+)) have been quantitatively precipitated by oxalic precipitation in nitric acid medium (yield >99%). Thorough multiscale structural characterization using XRD and XAS measurements confirmed the existence of mixed actinide oxalate solid solutions. The XANES analysis confirmed that the oxidation states of the metallic cations, tetravalent for uranium and trivalent for plutonium and americium, are maintained during the precipitation step. EXAFS measurements show that the local environments around U(+IV), Pu(+III) and Am(+III) are comparable, and the actinides are surrounded by ten oxygen atoms from five bidentate oxalate anions. The mean metal-oxygen distances obtained by XAS measurements are in agreement with those calculated from XRD lattice parameters.

Uranium speciation and stability after reductive immobilization in aquifer sediments

NASA Astrophysics Data System (ADS)

Sharp, Jonathan O.; Lezama-Pacheco, Juan S.; Schofield, Eleanor J.; Junier, Pilar; Ulrich, Kai-Uwe; Chinni, Satya; Veeramani, Harish; Margot-Roquier, Camille; Webb, Samuel M.; Tebo, Bradley M.; Giammar, Daniel E.; Bargar, John R.; Bernier-Latmani, Rizlan

2011-11-01

It has generally been assumed that the bioreduction of hexavalent uranium in groundwater systems will result in the precipitation of immobile uraninite (UO 2). In order to explore the form and stability of uranium immobilized under these conditions, we introduced lactate (15 mM for 3 months) into flow-through columns containing sediments derived from a former uranium-processing site at Old Rifle, CO. This resulted in metal-reducing conditions as evidenced by concurrent uranium uptake and iron release. Despite initial augmentation with Shewanella oneidensis, bacteria belonging to the phylum Firmicutes dominated the biostimulated columns. The immobilization of uranium (˜1 mmol U per kg sediment) enabled analysis by X-ray absorption spectroscopy (XAS). Tetravalent uranium associated with these sediments did not have spectroscopic signatures representative of U-U shells or crystalline UO 2. Analysis by microfocused XAS revealed concentrated micrometer regions of solid U(IV) that had spectroscopic signatures consistent with bulk analyses and a poor proximal correlation (μm scale resolution) between U and Fe. A plausible explanation, supported by biogeochemical conditions and spectral interpretations, is uranium association with phosphoryl moieties found in biomass; hence implicating direct enzymatic uranium reduction. After the immobilization phase, two months of in situ exposure to oxic influent did not result in substantial uranium remobilization. Ex situ flow-through experiments demonstrated more rapid uranium mobilization than observed in column oxidation studies and indicated that sediment-associated U(IV) is more mobile than biogenic UO 2. This work suggests that in situ uranium bioimmobilization studies and subsurface modeling parameters should be expanded to account for non-uraninite U(IV) species associated with biomass.

Tuning the Oxidation State, Nuclearity, and Chemistry of Uranium Hydrides with Phenylsilane and Temperature: The Case of the Classic Uranium(III) Hydride Complex [(C 5 Me 5) 2U(μ-H)] 2

DOE PAGES

Pagano, Justin K.; Dorhout, Jacquelyn M.; Czerwinski, Kenneth R.; ...

2016-03-18

Here, this work demonstrates that the oxidation state and chemistry of uranium hydrides can be tuned with temperature and the stoichiometry of phenylsilane. The trivalent uranium hydride [(C 5Me 5) 2U–H] x (5) was found to be comprised of an equilibrium mixture of U(III) hydrides in solution at ambient temperature. A single U(III) species can be selectively prepared by treating (C 5Me5)2UMe2 (4) with 2 equiv of phenylsilane at 50 °C. The U(III) system is a potent reducing agent and displayed chemistry distinct from the U(IV) system [(C 5Me 5) 2U(H)(μ-H)] 2 (2), which was harnessed to prepare a varietymore » of organometallic complexes, including (C 5Me 5) 2U(dmpe)(H) (6), and the novel uranium(IV) metallacyclopentadiene complex (C 5Me 5) 2U(C 4Me 4) (11).« less

Uranium extraction from TRISO-coated fuel particles using supercritical CO2 containing tri-n-butyl phosphate.

PubMed

Zhu, Liyang; Duan, Wuhua; Xu, Jingming; Zhu, Yongjun

2012-11-30

High-temperature gas-cooled reactors (HTGRs) are advanced nuclear systems that will receive heavy use in the future. It is important to develop spent nuclear fuel reprocessing technologies for HTGR. A new method for recovering uranium from tristructural-isotropic (TRISO-) coated fuel particles with supercritical CO(2) containing tri-n-butyl phosphate (TBP) as a complexing agent was investigated. TRISO-coated fuel particles from HTGR fuel elements were first crushed to expose UO(2) pellet fuel kernels. The crushed TRISO-coated fuel particles were then treated under O(2) stream at 750°C, resulting in a mixture of U(3)O(8) powder and SiC shells. The conversion of U(3)O(8) into solid uranyl nitrate by its reaction with liquid N(2)O(4) in the presence of a small amount of water was carried out. Complete conversion was achieved after 60 min of reaction at 80°C, whereas the SiC shells were not converted by N(2)O(4). Uranyl nitrate in the converted mixture was extracted with supercritical CO(2) containing TBP. The cumulative extraction efficiency was above 98% after 20 min of online extraction at 50°C and 25 MPa, whereas the SiC shells were not extracted by TBP. The results suggest an attractive strategy for reprocessing spent nuclear fuel from HTGR to minimize the generation of secondary radioactive waste. Copyright © 2012 Elsevier B.V. All rights reserved.

Spectroscopic evidence of uranium immobilization in acidic wetlands by natural organic matter and plant roots

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Dien; Kaplan, Daniel I.; Chang, Hyun-Shik

Biogeochemistry of uranium in wetlands plays important roles in U immobilization in storage ponds of U mining and processing facilities but has not been well understood. The objective of this work was to study molecular mechanisms responsible for high U retention by Savannah River Site (SRS) wetland sediments under varying redox and acidic (pH = 2.6–5.8) conditions using U L₃-edge X-ray absorption spectroscopy. Uranium in the SRS wetland sediments existed primarily as U(VI) bonded as a bidentate to carboxylic sites (U–C bond distance at ~2.88 Å), rather than phenolic or other sites of natural organic matter (NOM). In microcosms simulatingmore » the SRS wetland processes, U immobilization on roots was two orders of magnitude higher than on the adjacent brown or more distant white sands in which U was U(VI). Uranium on the roots were both U(IV) and U(VI), which were bonded as a bidentate to carbon, but the U(VI) may also form a U phosphate mineral. After 140 days of air exposure, all U(IV) was re-oxidized to U(VI) but remained as a bidentate bonding to carbon. This study demonstrated NOM and plant roots can highly immobilize U(VI) in the SRS acidic sediments, which has significant implication for the long-term stewardship of U-contaminated wetlands.« less

Spectroscopic evidence of uranium immobilization in acidic wetlands by natural organic matter and plant roots

DOE PAGES

Li, Dien; Kaplan, Daniel I.; Chang, Hyun-Shik; ...

2015-03-03

Biogeochemistry of uranium in wetlands plays important roles in U immobilization in storage ponds of U mining and processing facilities but has not been well understood. The objective of this work was to study molecular mechanisms responsible for high U retention by Savannah River Site (SRS) wetland sediments under varying redox and acidic (pH = 2.6–5.8) conditions using U L₃-edge X-ray absorption spectroscopy. Uranium in the SRS wetland sediments existed primarily as U(VI) bonded as a bidentate to carboxylic sites (U–C bond distance at ~2.88 Å), rather than phenolic or other sites of natural organic matter (NOM). In microcosms simulatingmore » the SRS wetland processes, U immobilization on roots was two orders of magnitude higher than on the adjacent brown or more distant white sands in which U was U(VI). Uranium on the roots were both U(IV) and U(VI), which were bonded as a bidentate to carbon, but the U(VI) may also form a U phosphate mineral. After 140 days of air exposure, all U(IV) was re-oxidized to U(VI) but remained as a bidentate bonding to carbon. This study demonstrated NOM and plant roots can highly immobilize U(VI) in the SRS acidic sediments, which has significant implication for the long-term stewardship of U-contaminated wetlands.« less

Impact of the cation distribution homogeneity on the americium oxidation state in the U0.54Pu0.45Am0.01O2-x mixed oxide

NASA Astrophysics Data System (ADS)

Vauchy, Romain; Robisson, Anne-Charlotte; Martin, Philippe M.; Belin, Renaud C.; Aufore, Laurence; Scheinost, Andreas C.; Hodaj, Fiqiri

2015-01-01

The impact of the cation distribution homogeneity of the U0.54Pu0.45Am0.01O2-x mixed oxide on the americium oxidation state was studied by coupling X-ray diffraction (XRD), electron probe micro analysis (EPMA) and X-ray absorption spectroscopy (XAS). Oxygen-hypostoichiometric Am-bearing uranium-plutonium mixed oxide pellets were fabricated by two different co-milling based processes in order to obtain different cation distribution homogeneities. The americium was generated from β- decay of 241Pu. The XRD analysis of the obtained compounds did not reveal any structural difference between the samples. EPMA, however, revealed a high homogeneity in the cation distribution for one sample, and substantial heterogeneity of the U-Pu (so Am) distribution for the other. The difference in cation distribution was linked to a difference in Am chemistry as investigated by XAS, with Am being present at mixed +III/+IV oxidation state in the heterogeneous compound, whereas only Am(IV) was observed in the homogeneous compound. Previously reported discrepancies on Am oxidation states can hence be explained by cation distribution homogeneity effects.

Richland five-year O2 R and D Program. Integrated site operation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1966-07-11

The technical feasibility of using an electrolytic reduction process to reduce metal scrap and oxide to usable uranium metal is being studied. The incentives for using electrolytic reduction at Richland may be summarized as follows: (1) reduce the unit and total costs of producing plutonium; (2) increase the flexibility of the Richland reactors for producing isotopes, particularly U-236; and (3) simplify the present fuel cycle complex. The scope of the mission is limited to the evaluation of hollow extruded I and E cores, the evaluation of electro-reduced uranium, an investigation of the solution rate of UO{sub 2} in the electrolyte,more » and small-scale irradiations of UO{sub 2} fuels in the N and K Reactors. Progress during FY 1966 is summarized.« less

Attenuation and Transport Mechanisms of Depleted Uranium in Groundwater at Lawrence Livermore National Laboratory Site 300

NASA Astrophysics Data System (ADS)

Danny, K. R.; Taffet, M. J.; Brusseau, M. L. L.; Chorover, J.

2015-12-01

Lawrence Livermore National Laboratory (LLNL) Site 300 was established in 1955 to support weapons research and development. Depleted uranium was used as a proxy for fissile uranium-235 (235U) in open-air explosives tests conducted at Building 812. As a result, oxidized depleted uranium was deposited on the ground, eventually migrating to the underlying sandstone aquifer. Uranium (U) groundwater concentrations exceed the California and Federal Maximum Contaminant Level of 20 pCi L-1 (30 ug L-1). However, the groundwater plume appears to attenuate within 60 m of the source, beyond which no depleted U is detected. This study will determine the relative contribution of physical (e.g. dilution), chemical (e.g. surface adsorption, mineral precipitation), and biological (e.g. biotransformation) processes that contribute to the apparent attenuation of U, which exists as uranyl (UO22+) complexes, at the site. Methods of investigation include evaluating 15 yr of hydrogeologic and chemical data, creating a site conceptual model, and applying equilibrium (e.g. aqueous species complexation, mineral saturation indices) and reactive transport models using Geochemist's WorkbenchTM. Reactive transport results are constrained by direct field observations, including U major ion, and dissolved O2 concentrations, pH, and others, under varying chemical and hydraulic conditions. Aqueous speciation calculations indicate that U primarily exists as anionic CaUO2(CO3)32- or neutral Ca2UO2(CO3)30 species. Additionally, nucleation and growth of Ca/Mg uranyl carbonate solids are predicted to affect attenuation. Initial reactive transport results suggest surface adsorption (e.g. ion exchange, surface complexation) to layer silicate clays is limited under the aqueous geochemical conditions of the site. Current and future work includes XRD analysis of aquifer solids to constrain iron and aluminum (oxy)hydroxides, and coupling advective-dispersive transport with the chemical and physical processes. This work performed under the auspices of the U.S. Department of Energy by Lawrence Livermore National Laboratory under Contract DE-AC52-07NA27344. LLNL-ABS-675707.

Oxidation of naturally reduced uranium in aquifer sediments by dissolved oxygen and its potential significance to uranium plume persistence

NASA Astrophysics Data System (ADS)

Davis, J. A.; Smith, R. L.; Bohlke, J. K.; Jemison, N.; Xiang, H.; Repert, D. A.; Yuan, X.; Williams, K. H.

2015-12-01

The occurrence of naturally reduced zones is common in alluvial aquifers in the western U.S.A. due to the burial of woody debris in flood plains. Such reduced zones are usually heterogeneously dispersed in these aquifers and characterized by high concentrations of organic carbon, reduced mineral phases, and reduced forms of metals, including uranium(IV). The persistence of high concentrations of dissolved uranium(VI) at uranium-contaminated aquifers on the Colorado Plateau has been attributed to slow oxidation of insoluble uranium(IV) mineral phases found in association with these reducing zones, although there is little understanding of the relative importance of various potential oxidants. Four field experiments were conducted within an alluvial aquifer adjacent to the Colorado River near Rifle, CO, wherein groundwater associated with the naturally reduced zones was pumped into a gas-impermeable tank, mixed with a conservative tracer (Br-), bubbled with a gas phase composed of 97% O2 and 3% CO2, and then returned to the subsurface in the same well from which it was withdrawn. Within minutes of re-injection of the oxygenated groundwater, dissolved uranium(VI) concentrations increased from less than 1 μM to greater than 2.5 μM, demonstrating that oxygen can be an important oxidant for uranium in such field systems if supplied to the naturally reduced zones. Dissolved Fe(II) concentrations decreased to the detection limit, but increases in sulfate could not be detected due to high background concentrations. Changes in nitrogen species concentrations were variable. The results contrast with other laboratory and field results in which oxygen was introduced to systems containing high concentrations of mackinawite (FeS), rather than the more crystalline iron sulfides found in aged, naturally reduced zones. The flux of oxygen to the naturally reduced zones in the alluvial aquifers occurs mainly through interactions between groundwater and gas phases at the water table. Seasonal variations of the water table at the Rifle, CO site may play an important role in introducing oxygen into the system. Although oxygen was introduced directly to the naturally reduced zones in these experiments, delivery of oxidants to the system may also be controlled by other oxidative pathways in which oxygen plays an indirect role.

Electronic structures of C u 2 O , C u 4 O 3 , and CuO: A joint experimental and theoretical study

DOE PAGES

Wang, Y.; Lany, S.; Ghanbaja, J.; ...

2016-12-14

We present a joint experimental and theoretical study for the electronic structures of copper oxides including Cu 2O, CuO, and the metastable mixed-valence oxide Cu 4O 3. The optical band gap is determined by experimental optical absorption coefficient, and the electronic structure in valence and conduction bands is probed by photoemission and electron energy loss spectroscopies, respectively. Furthermore, we compare our experimental results with many-body GW calculations utilizing an additional on-site potential for d-orbital energies that facilitates tractable and predictive computations. The side-by-side comparison between the three oxides, including a band insulator (Cu2O) and two Mott/charge-transfer insulators (CuO, Cu 4Omore » 3) leads to a consistent picture for the optical and band-structure properties of the Cu oxides, strongly supporting indirect band gaps of about 1.2 and 0.8 eV in CuO and Cu 4O 3, respectively. This comparison also points towards surface oxidation and reduction effects that can complicate the interpretation of the photoemission spectra.« less

PREPARATION OF UO$sub 2$ FOR NUCLEAR REACTOR FUEL PELLETS

DOEpatents

Googin, J.M.

1962-06-01

A method is given for preparing high-density UO/sub 2/ compacts. An aqueous uranyl fluoride solution is contacted with an aqueous ammonium hydroxide solution at an ammonium to-uranium ratio of 25: 1 to 30:1 to form a precipitate. The precipitate is separated from the- mother liquor, dried, and contacted with steam at a uniform temperature within the range of 400 to 650 deg C to produce U/ sub 3/O/sub 8/. The U/sub 3/O/sub 8/ is red uced to UO/sub 2/ with hydrogen at a uniform temperature within the range of 550 to 600 deg C. The UO/sub 2/ is then compressed into compacts and sintered. High-density compacts are fabricated to close tolerances without use of a binder and without machining or grinding. (AEC)

[Determination of 235U/238U isotope ratios in camphor tree bark samples by MC-ICP-MS after separation of uranium from matrix elements].

PubMed

Wang, Xiao-Ping; Zhang, Ji-Long

2007-07-01

Twelve camphor (cinnamomum camphora) tree bark samples were collected from Hiroshima and Kyoto, and the matrix element composition and morphology of the outer surface of these camphor tree bark samples were studied by EDXS and SEM respectively. After a dry decomposition, DOWEX 1-X8 anion exchange resin was used to separate uranium from matrix elements in these camphor tree bark samples. Finally, 235U/238 U isotope ratios in purified uranium solutions were determined by MC-ICP-MS. It was demonstrated that the outer surface of these camphor tree bark samples is porous and rough, with Al, Ca, Fe, K, Mg, Si, C, O and S as its matrix element composition. Uranium in these camphor tree bark samples can be efficiently separated and quantitatively recovered from the matrix element composition. Compared with those collected from Kyoto, the camphor tree bark samples collected from Hiroshima have significantly higher uranium contents, which may be due to the increased aerosol mass concentration during the city reconstruction. Moreover, the 235 U/23.U isotope ratios in a few camphor tree bark samples collected from Hiroshima are slightly higher than 0.007 25.

Oxidative dissolution of biogenic uraninite in groundwater at Old Rifle, CO

USGS Publications Warehouse

Campbell, Kate M.; Veeramani, Harish; Ulrich, Kai-Uwe; Blue, Lisa Y.; Giammar, Dianiel E.; Bernier-Latmani, Rizlan; Stubbs, Joanne E.; Suvorova, Elena; Yabusaki, Steve; Lezama-Pacheco, Juan S.; Mehta, Apurva; Long, Philip E.; Bargar, John R.

2011-01-01

Reductive bioremediation is currently being explored as a possible strategy for uranium-contaminated aquifers such as the Old Rifle site (Colorado). The stability of U(IV) phases under oxidizing conditions is key to the performance of this procedure. An in situ method was developed to study oxidative dissolution of biogenic uraninite (UO2), a desirable U(VI) bioreduction product, in the Old Rifle, CO, aquifer under different variable oxygen conditions. Overall uranium loss rates were 50–100 times slower than laboratory rates. After accounting for molecular diffusion through the sample holders, a reactive transport model using laboratory dissolution rates was able to predict overall uranium loss. The presence of biomass further retarded diffusion and oxidation rates. These results confirm the importance of diffusion in controlling in-aquifer U(IV) oxidation rates. Upon retrieval, uraninite was found to be free of U(VI), indicating dissolution occurred via oxidation and removal of surface atoms. Interaction of groundwater solutes such as Ca2+ or silicate with uraninite surfaces also may retard in-aquifer U loss rates. These results indicate that the prolonged stability of U(IV) species in aquifers is strongly influenced by permeability, the presence of bacterial cells and cell exudates, and groundwater geochemistry.

Leaching under Oxygen Pressure with Carbonate Solution Reduction by Hydrogen; LIXIVIATION OXYDANTE DES PECHBLENDES ET PRECIPITATION DE L'URANIUM PAR L'HYDROGENE. APPLICATION AUX MINERAIS PAUVRES FRANCAIS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Balaceanu, J.C.; Coussemant, F.; Mouret, P.

1959-10-31

A study was made of the basic characteristics of the leaching with carbonate solution under oxygen pressure and of the catalytic hydrogen reduction of low-grade French ores. Pure U/sub 3/O/sub 8/ was used in the investigations on leaching. The effects of oxygen pressure, temperature, initial surface of the oxide, surfuce during the course of the reaction, and concentration of the carbonate solution were determined. It was shown that the heterogeneous reactions involve a constant surface and two steps. A pilot plant experiment was made on a number of low-grade French ores. With ores the leaching is not sensitive to oxygenmore » pressure. Dilute solutions of sodium uranyl carbonate are obtained from the leaching. The uranium can be precipitated as an oxide of a lower valent state by catalytic reduction with hydrogen. The study of this step was made on pure solutions of sodium uranyl carbonate in the presence of nickel and platinum catalysts. The reaction is strongly modified by the presence of even low concentrations of sodium bicarbonate. The reaction velocity increases with hydrogen pressure up to 5 atm, but then becomes independent of the pressure. The precipitation is accelerated by an increase in temperature. (J.S.R.)« less

Comparative investigation of the solution species [U(CO3)5]6- and the crystal structure of Na6[U(CO3)5].12H2O.

PubMed

Hennig, Christoph; Ikeda-Ohno, Atsushi; Emmerling, Fanziska; Kraus, Werner; Bernhard, Gert

2010-04-21

The limiting U(IV) carbonate species in aqueous solution was investigated by comparing its structure parameters with those of the complex preserved in a crystal structure. The solution species prevails in aqueous solution of 0.05 M U(IV) and 1 M NaHCO(3) at pH 8.3. Single crystals of Na(6)[U(CO(3))(5)].12H(2)O were obtained directly from this mother solution. The U(IV) carbonate complex in the crystal structure was identified as a monomeric [U(CO(3))(5)](6-) anionic complex. The interatomic distances around the U(IV) coordination polyhedron show average distances of U-O = 2.461(8) A, U-C = 2.912(4) A and U-O(dist) = 4.164(6) A. U L(3)-edge EXAFS spectra were collected from the solid Na(6)[U(CO(3))(5)].12H(2)O and the corresponding solution. The first shell of the Fourier transforms (FTs) revealed, in both samples, a coordination of ten oxygen atoms at an average U-O distance of 2.45 +/- 0.02 A, the second shell originates from five carbon atoms with a U-C distance of 2.91 +/- 0.02 A, and the third shell was fit with single and multiple scattering paths of the distal oxygen at 4.17 +/- 0.02 A. These data indicate the identity of the [U(CO(3))(5)](6-) complex in solid and solution state. The high negative charge of the [U(CO(3))(5)](6-) anion is compensated by Na(+) cations. In solid state the Na(+) cations form a bridging network between the [U(CO(3))(5)](6-) units, while in liquid state the Na(+) cations seem to be located close to the anionic complex. The average metal-oxygen distances of the coordination polyhedron show a linear correlation to the radius contraction of the neighbouring actinide(IV) ions and indicate the equivalence of the [An(CO(3))(5)](6-) coordination within the series of thorium, uranium, neptunium and plutonium.

Direct Compositional Characterization of (U,Th)O2 Powders, Microspheres, and Pellets Using TXRF.

PubMed

Dhara, Sangita; Prabhat, Parimal; Misra, N L

2015-10-20

A total reflection X-ray fluorescence (TXRF) analysis method for direct compositional characterization of sintered and green (U,Th)O2 samples in different forms (e.g., pellets, powders, and microspheres) without sample dissolution has been developed for the first time. The methodology involves transfer of only a few nanograms of the sample on the TXRF sample support by gently rubbing the samples on supports or taking their tiny uniform slurry in collodion on the sample support, drying them to make thin film, and measuring the TXRF spectra of the specimens thus prepared. This approach minimizes the matrix effects. Uranium determinations from the TXRF spectra of such specimens were made with respect to thorium, considering it as an internal standard. Samples having uranium atom percent (at%) from 0 to 100 in (U,Th)O2 were analyzed for uranium in comparison to thorium. The results showed an average precision of 2.6% (RSD, 2σ, n = 8). The TXRF-determined results deviated from expected values within 5%. The TXRF results were compared with those of biamperometry with good agreement. The lattice parameters of the solid solutions were calculated using their XRD patterns. A good correlation between lattice parameters and TXRF-determined U at% and between TXRF-determined U at% and expected U at%, calculated on the basis of preparation of (U,Th)O2 solid solutions, was obtained. The developed method is capable of analyzing (U,Th)O2 samples directly with almost negligible sample preparation and is well suited for radioactive samples. The present study suggests that this method can be extended for the determination of U,Th and Pu in other nuclear fuel materials (e.g., nitrides, carbides, etc.) in the form of pellets, powders, and microspheres after suitable modifications in sample handling procedure.

Oxidation behavior of U-Si compounds in air from 25 to 1000 C

NASA Astrophysics Data System (ADS)

Sooby Wood, E.; White, J. T.; Nelson, A. T.

2017-02-01

The air oxidation behavior of U3Si2, USi, and U3Si5 is studied from room temperature to 1000 C. The onsets of breakaway oxidation for each compound are identified during synthetic air ramps to 1000 C using thermogravimetric analysis. Isothermal air oxidation tests are performed below and above the breakaway oxidation onset to discern the oxidation kinetic behavior of these candidate accident tolerant fuel forms. Uranium metal is tested in the same manner to provide a reference for the oxidation behavior. Thermogravimetric, x-ray diffraction, and scanning electron microscopy analysis are presented here along with a discussion of the oxidation behavior of these materials and the impact of the lack of oxidation resistance to their deployment as accident tolerant nuclear fuels.

High temperature redox reactions with uranium: Synthesis and characterization of Cs(UO{sub 2})Cl(SeO{sub 3}), Rb{sub 2}(UO{sub 2}){sub 3}O{sub 2}(SeO{sub 3}){sub 2}, and RbNa{sub 5}U{sub 2}(SO{sub 4}){sub 7}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Babo, Jean-Marie; Department of Civil and Environmental Engineering and Earth Sciences and Department of Chemistry and Biochemistry, University of Notre Dame, Notre Dame, IN 46556; Albrecht-Schmitt, Thomas E., E-mail: talbrechtschmitt@gmail.com

2013-10-15

Cs(UO{sub 2})Cl(SeO{sub 3}) (1), Rb{sub 2}(UO{sub 2}){sub 3}O{sub 2}(SeO{sub 3}){sub 3} (2), and RbNa{sub 5}U{sub 2}(SO{sub 4}){sub 7} (3) single crystals were synthesized using CsCl, RbCl, and a CuCl/NaCl eutectic mixture as fluxes, respectively. Their lattice parameters and space groups are as follows: P2{sub 1}/n (a=6.548(1) Å, b=11.052(2) Å, c=10.666(2) Å and β=93.897(3)°), P1{sup ¯} (a=7.051(2) Å, b=7.198(2) Å, c=8.314(2) Å, α=107.897(3)°, β=102.687(3)° and γ=100.564(3)°) and C2/c (a=17.862(4) Å, b=6.931(1) Å, c=20.133(4) Å and β=109.737(6)°. The small anionic building units found in these compounds are SeO{sub 3}{sup 2−} and SO{sub 4}{sup 2−} tetrahedra, oxide, and chloride. The crystal structure ofmore » the first compound is composed of [(UO{sub 2}){sub 2}Cl{sub 2}(SeO{sub 3}){sub 2}]{sup 2−} chains separated by Cs{sup +} cations. The structure of (2) is constructed from [(UO{sub 2}){sub 3}O{sub 11}]{sup 16−} chains further connected through selenite units into layers stacked perpendicularly to the [0 1 0] direction, with Rb{sup +} cations intercalating between them. The structure of compound (3) is made of uranyl sulfate layers formed by edge and vertex connections between dimeric [U{sub 2}O{sub 16}] and [SO{sub 4}] polyhedra. These layers contain unusual sulfate–metal connectivity as well as large voids. - Graphical abstract: A new family of uranyl selenites and sulfates has been prepared by high-temperature redox reactions. This compounds display new bonding motifs. Display Omitted - Highlights: • Low-dimensional Uranyl Oxoanion compounds. • Conversion of U(IV) to U(VI) at high temperatures. • Dimensional reduction by both halides and stereochemically active lone-pairs.« less

Uranium and cadmium provoke different oxidative stress responses in Lemna minor L.

PubMed

Horemans, N; Van Hees, M; Van Hoeck, A; Saenen, E; De Meutter, T; Nauts, R; Blust, R; Vandenhove, H

2015-01-01

Common duckweed (Lemna minor L.) is ideally suited to test the impact of metals on freshwater vascular plants. Literature on cadmium (Cd) and uranium (U) oxidative responses in L. minor are sparse or, for U, non-existent. It was hypothesised that both metals impose concentration-dependent oxidative stress and growth retardation on L. minor. Using a standardised 7-day growth inhibition test, the adverse impact of these metals on L. minor growth was confirmed, with EC50 values for Cd and U of 24.1 ± 2.8 and 29.5 ± 1.9 μm, respectively, and EC10 values of 1.5 ± 0.2 and 6.5 ± 0.9 μm, respectively. The metal-induced oxidative stress response was compared through assessing the activity of different antioxidative enzymes [catalase, glutathione reductase, superoxide dismutase (SOD), ascorbate peroxidase (APOD), guaiacol peroxidase (GPOD) and syringaldizyne peroxidase (SPOD)]. Significant changes in almost all antioxidative enzymes indicated their importance in counteracting the U- and Cd-imposed oxidative burden. However, some striking differences were also observed. For activity of APODs and SODs, a biphasic but opposite response at low Cd compared to U concentrations was found. In addition, Cd (0.5-20 μm) strongly enhanced plant GPOD activity, whereas U inhibited it. Finally, in contrast to Cd, U up to 10 μm increased the level of chlorophyll a and b and carotenoids. In conclusion, although U and Cd induce similar growth arrest in L. minor, the U-induced oxidative stress responses, studied here for the first time, differ greatly from those of Cd. © 2014 German Botanical Society and The Royal Botanical Society of the Netherlands.

29 CFR 1926.55 - Gases, vapors, fumes, dusts, and mists.

Code of Federal Regulations, 2013 CFR

2013-07-01

... Nitrous oxide 10024-97-2 E Octachloronaphthalene 2234-13-1 — 0.1 X Octane 111-65-9 400 1900 — Oil mist... — Uranium (as U) 7440-61-1 Soluble compounds — 0.2 — Insoluble compounds — 0.2 — Vanadium 1314-62-1 Respirable dust (as V2 O5) — (C)0.5 — Fume (as V2 O5) — (C)0.1 — Vegetable oil mist Total dust — — Respirable...

29 CFR 1926.55 - Gases, vapors, fumes, dusts, and mists.

Code of Federal Regulations, 2014 CFR

2014-07-01

... Nitrous oxide 10024-97-2 E Octachloronaphthalene 2234-13-1 — 0.1 X Octane 111-65-9 400 1900 — Oil mist... — Uranium (as U) 7440-61-1 Soluble compounds — 0.2 — Insoluble compounds — 0.2 — Vanadium 1314-62-1 Respirable dust (as V2 O5) — (C)0.5 — Fume (as V2 O5) — (C)0.1 — Vegetable oil mist Total dust — — Respirable...

29 CFR 1926.55 - Gases, vapors, fumes, dusts, and mists.

Code of Federal Regulations, 2012 CFR

2012-07-01

... Nitrous oxide 10024-97-2 E Octachloronaphthalene 2234-13-1 — 0.1 X Octane 111-65-9 400 1900 — Oil mist... — Uranium (as U) 7440-61-1 Soluble compounds — 0.2 — Insoluble compounds — 0.2 — Vanadium 1314-62-1 Respirable dust (as V2 O5) — (C)0.5 — Fume (as V2 O5) — (C)0.1 — Vegetable oil mist Total dust — — Respirable...

U(VI) adsorption on aquifer sediments at the Hanford Site.

PubMed

Um, Wooyong; Serne, R Jeffrey; Brown, Christopher F; Last, George V

2007-08-15

Aquifer sediments collected via split-spoon sampling in two new groundwater wells in the 200-UP-1 operable unit at the Hanford Site were characterized and showed typical Ringold Unit E Formation properties dominated by gravel and sand. High iron-oxide content in Fe oxide/clay coatings caused the highest U(VI) adsorption as quantified by batch K(d) values, indicating iron oxides are the key solid adsorbent in the 200-UP-1 sediments that affect U(VI) fate and mobility. Even though U(VI) adsorption on the gravel-sized fraction of the sediments is considered to be negligible, careful characterization should be conducted to determine U(VI) adsorption on gravel, because of presence of Fe oxides coatings and diffusion-controlled adsorption into the gravel particles' interior surfaces. A linear adsorption isotherm was observed up to 10(-6) M (238 microg/L) of total U(VI) concentration in batch U(VI) adsorption tests with varying total U(VI) concentrations in spiked groundwater. U(VI) adsorption decreased with increasing concentrations of dissolved carbonate, because strong anionic aqueous uranium-carbonate complexes formed at high pH and high alkalinity conditions. Noticeable uranium desorption hysteresis was observed in a flow-through column experiment, suggesting that desorption K(d) values for aged uranium-contaminated sediments at the Hanford Site can be larger than adsorption K(d) values determined in short-term laboratory experiments and slow uranium release from contaminated sediments into the groundwater is expected.

The importance of colloids and mires for the transport of uranium isotopes through the Kalix River watershed and Baltic Sea

DOE Office of Scientific and Technical Information (OSTI.GOV)

Porcelli, D.; Wasserburg, G.J.; Andersson, P.S.

The importance of colloids and organic deposits for the transport of uranium isotopes from continental source regions and through the estuarine environment was investigated in the mire-rich Kalix River drainage basin in northern Sweden and the Baltic Sea. Ultrafiltration techniques were used to separate uranium and other elements associated with colloids > 10 kD and >3 kD from {open_quotes}solute{close_quotes} uranium and provided consistent results and high recovery rates for uranium as well as for other elements from large volume samples. Uranium concentrations in 0.45 {mu}m-filtered Kalix River water samples increased by a factor of 3 from near the headwaters inmore » the Caledonides to the river mouth while major cation concentrations were relatively constant. {sup 234}U {sup 238}U ratios were high ({delta}{sup 234}U = 770-1500) throughout the basin, without showing any simple pattern, and required a supply of {sup 234}U-rich water. Throughout the Kalix River, a large fraction (30-90%) of the uranium is carried by >10 kD colloids, which is compatible with uranium complexation with humic acids. No isotopic differences were found between colloid-associated and solute uranium. Within the Baltic Sea, about half of the uranium is removed at low salinities. The proportion that is lost is equivalent to that of river-derived colloid-bound uranium, suggesting that while solute uranium behaves conservatively during estuarine mixing, colloid-bound uranium is lost due to rapid flocculation of colloidal material. The association of uranium with colloids therefore may be an important parameter in determining uranium estuarine behavior. Mire peats in the Kalix River highly concentrate uranium and are potentially a significant source of recoil {sup 234}U to the mirewaters and river waters. However, mirewater data clearly demonstrate that only small {sup 234}U/{sup 238}U shifts are generated relative to inflowing groundwater. 63 refs., 8 figs., 3 tabs.« less

XRD monitoring of α self-irradiation in uranium-americium mixed oxides.

PubMed

Horlait, Denis; Lebreton, Florent; Roussel, Pascal; Delahaye, Thibaud

2013-12-16

The structural evolution under (241)Am self-irradiation of U(1-x)Am(x)O(2±δ) transmutation fuels (with x ≤ 0.5) was studied by X-ray diffraction (XRD). Samples first underwent a preliminary heat treatment performed under a reducing atmosphere (Ar/H2(4%)) aiming to recover the previously accumulated structural defects. Over all measurements (carried out over up to a full year and for integrated doses up to 1.5 × 10(18) α-decay events·g(-1)), only fluorite U(1-x)Am(x)O(2±δ) solid solutions were observed. Within a few days after the end of the heat treatment, each of the five studied samples was slowly oxidized as a consequence of their move to air atmosphere, which is evidenced by XRD by an initial sharp decrease of the unit cell parameter. For the compounds with x ≤ 0.15, this oxidation occurred without any phase transitions, but for U0.6Am0.4O(2±δ) and U0.5Am0.5O(2±δ), this process is accompanied by a transition from a first fluorite solid solution to a second oxidized one, as the latter is thermodynamically stable in ambient conditions. In the meantime and after the oxidation process, (241)Am α self-irradiation caused a structural swelling up to ∼0.8 vol %, independently of the sample composition. The kinetic constants of swelling were also determined by regression of experimental data and are, as expected, dependent on x and thus on the dose rate. The normalization of these kinetic constants by sample α-activity, however, leads to very close swelling rates among the samples. Finally, evolutions of microstrain and crystallite size were also monitored, but for the considered dose rates and cumulated doses, α self-irradiation was found, within the limits of the diffractometer used, to have almost no impact on these characteristics. Microstrain was found to be influenced instead by the americium content in the materials (i.e., by the impurities associated with americium starting material and the increase of cationic charge heterogeneity with increasing americium content).

Oxidation behavior of U-Si compounds in air from 25 to 1000 C

DOE PAGES

Wood, E. Sooby; White, J. T.; Nelson, A. T.

2016-12-18

The air oxidation behavior of U 3Si 2, USi, and U 3Si 5 is studied from room temperature to 1000 C. Moreover, the onsets of breakaway oxidation for each compound are identified during synthetic air ramps to 1000 C using thermogravimetric analysis. Isothermal air oxidation tests are performed below and above the breakaway oxidation onset to discern the oxidation kinetic behavior of these candidate accident tolerant fuel forms. Uranium metal is tested in the same manner to provide a reference for the oxidation behavior. We present thermogravimetric, x-ray diffraction, and scanning electron microscopy analysis here along with a discussion ofmore » the oxidation behavior of these materials and the impact of the lack of oxidation resistance to their deployment as accident tolerant nuclear fuels.« less

Biosorption and Biomineralization of U(VI) by the Marine Bacterium Idiomarina loihiensis MAH1: Effect of Background Electrolyte and pH

PubMed Central

Morcillo, Fernando; González-Muñoz, María T.; Reitz, Thomas; Romero-González, María E.; Arias, José M.; Merroun, Mohamed L.

2014-01-01

The main goal of this study is to compare the effects of pH, uranium concentration, and background electrolyte (seawater and NaClO4 solution) on the speciation of uranium(VI) associated with the marine bacterium Idiomarina loihiensis MAH1. This was done at the molecular level using a multidisciplinary approach combining X-ray Absorption Spectroscopy (XAS), Time-Resolved Laser-Induced Fluorescence Spectroscopy (TRLFS), and High Resolution Transmission Electron Microscopy (HRTEM). We showed that the U(VI)/bacterium interaction mechanism is highly dependent upon pH but also the nature of the used background electrolyte played a role. At neutral conditions and a U concentration ranging from 5·10−4 to 10−5 M (environmentally relevant concentrations), XAS analysis revealed that uranyl phosphate mineral phases, structurally resembling meta-autunite [Ca(UO2)2(PO4)2 2–6H2O] are precipitated at the cell surfaces of the strain MAH1. The formation of this mineral phase is independent of the background solution but U(VI) luminescence lifetime analyses demonstrated that the U(VI) speciation in seawater samples is more intricate, i.e., different complexes were formed under natural conditions. At acidic conditions, pH 2, 3 and 4.3 ([U] = 5·10−4 M, background electrolyte  = 0.1 M NaClO4), the removal of U from solution was due to biosorption to Extracellular Polysaccharides (EPS) and cell wall components as evident from TEM analysis. The L III-edge XAS and TRLFS studies showed that the biosorption process observed is dependent of pH. The bacterial cell forms a complex with U through organic phosphate groups at pH 2 and via phosphate and carboxyl groups at pH 3 and 4.3, respectively. The differences in the complexes formed between uranium and bacteria on seawater compared to NaClO4 solution demonstrates that the actinide/microbe interactions are influenced by the three studied factors, i.e., the pH, the uranium concentration and the chemical composition of the solution. PMID:24618567

Duttonite, a new quadrivalent vanadium oxide from the Peanut mine, Montrose County, Colorado

USGS Publications Warehouse

Thompson, Mary Eleanor; Roach, Carl Houston; Meyrowitz, Robert

1956-01-01

Duttonite, a new quadrivalent vanadium oxide from the Peanut mine, Montrose County, Colo., has the formula VO(OH)2. The mineral occurs as crusts and coatings of pale-brown transparent platy crystals, as one of the first oxidation products of montroseite ore. It is associated with melanovanadite and abundant crystals of hexagonal native selenium. Duttonite is biaxial positive, 2V is about 60°, dispersion is r v, moderate; X = a, pale pinkish brown; Y = c, pale yellow-brown; Z = b, pale brown; α = 1.810 ± 0.003, β = 1.900 ± 0.003, γ > 2.01. The hardness is about 2.5; the calculated specific gravity is 3.24. The chemical analysis shows, in percent: V2o3 2.6, V2O4 75.3, FeO 0.4, H2O 18.1, insoluble 4.2, total 100.6. Duttonite is monoclinic, ao = 8.80 ± 0.02A, bo - 3.95 ± 0.01A, co - 5.96 ± 0.02A, β = 90°401 ± 51. The space group is I2/c, (C62h); the cell contents are 4[VO(OH)2]. The crystals are strongly pseudo-orthorhombic, and the structure departs only slightly from the space group Imcm. Duttonite is named for Captain Clarence Edward Dutton (1841-1912). A detailed study of the geology, geochemistry, and mineralogy of the vanadium-uranium ore at the Peanut mine, Montrose County, Colo., was begun early in 1954 by Carl H. Roach of the U. S. Geological Survey. A number of rare and new minerals were found in the ore and the study of these samples was undertaken by Mary E. Thompson. Duttonite is the first new vanadium mineral to be described from the Peanut mine. It is named for Captain Clarence Edward Dutton (1841-1912), who was one of the first geologists to work in the Colorado Plateau region and who was a member of the U. s. Geological Survey from 1879-91. We are indebted to the following members of the Geological Surbey: K. E. Valentine for spectrographic analyses of duttonite, and M. E. Mrose and H. T. Evans, Jr., for measurement of the unit cell constants. This work is part of a program being conducted by the U. S. Geological Survey on behalf of the Division of Raw Materials of the U. S. Atomic Energy Commission.

Radionuclide sorption in Yucca Mountain tuffs with J-13 well water: Neptunium, uranium, and plutonium. Yucca Mountain site characterization program milestone 3338

DOE Office of Scientific and Technical Information (OSTI.GOV)

Triay, I.R.; Cotter, C.R.; Kraus, S.M.

1996-08-01

We studied the retardation of actinides (neptunium, uranium, and plutonium) by sorption as a function of radionuclide concentration in water from Well J-13 and of tuffs from Yucca Mountain. Three major tuff types were examined: devitrified, vitric, and zeolitic. To identify the sorbing minerals in the tuffs, we conducted batch sorption experiments with pure mineral separates. These experiments were performed with water from Well J-13 (a sodium bicarbonate groundwater) under oxidizing conditions in the pH range from 7 to 8.5. The results indicate that all actinides studied sorb strongly to synthetic hematite and also that Np(V) and U(VI) do notmore » sorb appreciably to devitrified or vitric tuffs, albite, or quartz. The sorption of neptunium onto clinoptilolite-rich tuffs and pure clinoptilolite can be fitted with a sorption distribution coefficient in the concentration range from 1 X 10{sup -7} to 3 X 10{sup -5} M. The sorption of uranium onto clinoptilolite-rich tuffs and pure clinoptilolite is not linear in the concentration range from 8 X 10{sup -8} to 1 X 10{sup -4} M, and it can be fitted with nonlinear isotherm models (such as the Langmuir or the Freundlich Isotherms). The sorption of neptunium and uranium onto clinoptilolite in J-13 well water increases with decreasing pH in the range from 7 to 8.5. The sorption of plutonium (initially in the Pu(V) oxidation state) onto tuffs and pure mineral separates in J-13 well water at pH 7 is significant. Plutonium sorption decreases as a function of tuff type in the order: zeolitic > vitric > devitrified; and as a function of mineralogy in the order: hematite > clinoptilolite > albite > quartz.« less

Removal of Trace Elements by Cupric Oxide Nanoparticles from Uranium In Situ Recovery Bleed Water and Its Effect on Cell Viability

PubMed Central

Schilz, Jodi R.; Reddy, K. J.; Nair, Sreejayan; Johnson, Thomas E.; Tjalkens, Ronald B.; Krueger, Kem P.; Clark, Suzanne

2015-01-01

In situ recovery (ISR) is the predominant method of uranium extraction in the United States. During ISR, uranium is leached from an ore body and extracted through ion exchange. The resultant production bleed water (PBW) contains contaminants such as arsenic and other heavy metals. Samples of PBW from an active ISR uranium facility were treated with cupric oxide nanoparticles (CuO-NPs). CuO-NP treatment of PBW reduced priority contaminants, including arsenic, selenium, uranium, and vanadium. Untreated and CuO-NP treated PBW was used as the liquid component of the cell growth media and changes in viability were determined by the MTT (3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) assay in human embryonic kidney (HEK 293) and human hepatocellular carcinoma (Hep G2) cells. CuO-NP treatment was associated with improved HEK and HEP cell viability. Limitations of this method include dilution of the PBW by growth media components and during osmolality adjustment as well as necessary pH adjustment. This method is limited in its wider context due to dilution effects and changes in the pH of the PBW which is traditionally slightly acidic however; this method could have a broader use assessing CuO-NP treatment in more neutral waters. PMID:26132311

Study of uranium oxidation states in geological material.

PubMed

Pidchenko, I; Salminen-Paatero, S; Rothe, J; Suksi, J

2013-10-01

A wet chemical method to determine uranium (U) oxidation states in geological material has been developed and tested. The problem faced in oxidation state determinations with wet chemical methods is that U redox state may change when extracted from the sample material, thereby leading to erroneous results. In order to quantify and monitor U redox behavior during the acidic extraction in the procedure, an analysis of added isotopic redox tracers, (236)U(VI) and (232)U(IV), and of variations in natural uranium isotope ratio ((234)U/(238)U) of indigenous U(IV) and U(VI) fractions was performed. Two sample materials with varying redox activity, U bearing rock and U-rich clayey lignite sediment, were used for the tests. The Fe(II)/Fe(III) redox-pair of the mineral phases was postulated as a potentially disturbing redox agent. The impact of Fe(III) on U was studied by reducing Fe(III) with ascorbic acid, which was added to the extraction solution. We observed that ascorbic acid protected most of the U from oxidation. The measured (234)U/(238)U ratio in U(IV) and U(VI) fractions in the sediment samples provided a unique tool to quantify U oxidation caused by Fe(III). Annealing (sample heating) to temperatures above 500 °C was supposed to heal ionizing radiation induced defects in the material that can disturb U redox state during extraction. Good agreement between two independent methods was obtained for DL-1a material: an average 38% of U(IV) determined by redox tracer corrected wet chemistry and 45% for XANES. Copyright © 2013 Elsevier Ltd. All rights reserved.

Dissolution of synthetic uranium dibutyl phosphate deposits in oxidizing and reducing chemical formulations.

PubMed

Rufus, A L; Sathyaseelan, V S; Narasimhan, S V; Velmurugan, S

2013-06-15

Permanganate and nitrilotriacetic acid (NTA) based dilute chemical formulations were evaluated for the dissolution of uranium dibutyl phosphate (U-DBP), a compound that deposits over the surfaces of nuclear reprocessing plants and waste storage tanks. A combination of an acidic, oxidizing treatment (nitric acid with permanganate) followed by reducing treatment (NTA based formulation) efficiently dissolved the U-DBP deposits. The dissolution isotherm of U-DBP in its as precipitated form followed a logarithmic fit. The same chemical treatment was also effective in dissolving U-DBP coated on the surface of 304-stainless steel, while resulting in minimal corrosion of the stainless steel substrate material. Investigation of uranium recovery from the resulting decontamination solutions by ion exchange with a bed of mixed anion and cation resins showed quantitative removal of uranium. Copyright © 2013 Elsevier B.V. All rights reserved.

Determination of irradiated reactor uranium in soil samples in Belarus using 236U as irradiated uranium tracer.

PubMed

Mironov, Vladislav P; Matusevich, Janna L; Kudrjashov, Vladimir P; Boulyga, Sergei F; Becker, J Sabine

2002-12-01

This work presents experimental results on the distribution of irradiated reactor uranium from fallout after the accident at Chernobyl Nuclear Power Plant (NPP) in comparison to natural uranium distribution in different soil types. Oxidation processes and vertical migration of irradiated uranium in soils typical of the 30 km relocation area around Chernobyl NPP were studied using 236U as the tracer for irradiated reactor uranium and inductively coupled plasma mass spectrometry as the analytical method for uranium isotope ratio measurements. Measurements of natural uranium yielded significant variations of its concentration in upper soil layers from 2 x 10(-7) g g(-1) to 3.4 x 10(-6) g g(-1). Concentrations of irradiated uranium in the upper 0-10 cm soil layers at the investigated sampling sites varied from 5 x 10(-12) g g(-1) to 2 x 10(-6) g g(-1) depending on the distance from Chernobyl NPP. In the majority of investigated soil profiles 78% to 97% of irradiated "Chernobyl" uranium is still contained in the upper 0-10 cm soil layers. The physical and chemical characteristics of the soil do not have any significant influence on processes of fuel particle destruction. Results obtained using carbonate leaching of 236U confirmed that more than 60% of irradiated "Chernobyl" uranium is still in a tetravalent form, ie. it is included in the fuel matrix (non-oxidized fuel UO2). The average value of the destruction rate of fuel particles determined for the Western radioactive trace (k = 0.030 +/- 0.005 yr(-1)) and for the Northern radioactive trace (k = 0.035 + 0.009 yr(-1)) coincide within experimental errors. Use of leaching of fission products in comparison to leaching of uranium for study of the destruction rate of fuel particles yielded poor coincidence due to the fact that use of fission products does not take into account differences in the chemical properties of fission products and fuel matrix (uranium).

Oxidative elemental cycling under the low O2 Eoarchean atmosphere

PubMed Central

Frei, Robert; Crowe, Sean A.; Bau, Michael; Polat, Ali; Fowle, David A.; Døssing, Lasse N.

2016-01-01

The Great Oxidation Event signals the first large-scale oxygenation of the atmosphere roughly 2.4 Gyr ago. Geochemical signals diagnostic of oxidative weathering, however, extend as far back as 3.3–2.9 Gyr ago. 3.8–3.7 Gyr old rocks from Isua, Greenland stand as a deep time outpost, recording information on Earth’s earliest surface chemistry and the low oxygen primordial biosphere. Here we find fractionated Cr isotopes, relative to the igneous silicate Earth reservoir, in metamorphosed banded iron formations (BIFs) from Isua that indicate oxidative Cr cycling 3.8–3.7 Gyr ago. Elevated U/Th ratios in these BIFs relative to the contemporary crust, also signal oxidative mobilization of U. We suggest that reactive oxygen species were present in the Eoarchean surface environment, under a very low oxygen atmosphere, inducing oxidative elemental cycling during the deposition of the Isua BIFs and possibly supporting early aerobic biology. PMID:26864443

Synthesis of Actinide Fluoride Complexes Using Trimethyltin Fluoride as a Mild and Selective Fluorinating Reagent

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kagan, Benjamin D.; Lichtscheidl, Alejandro G.; Erickson, Karla A.

Trimethyltin fluoride (Me₃SnF) is a mild and selective reagent for the installation of actinide fluoride bonds as demonstrated by the room temperature synthesis of a variety of organometallic and inorganic thorium(IV), uranium(IV), and uranium(V) fluoride complexes ((1,2,4-tBu₃C₅H₂)₂ThF₂, (C₅Me₅)₂U(F)(O-2,6-iPr₂C₆H₃), U(F)(O-2,6-tBu₂C₆H₃)₃, U(F)[N(SiMe₃)₂]₃ (C₅Me₅)₂UF₂(L) (L = O=PMe₃, O=PPh₃, O=PCy₃), and (C₅Me₅)₂U(F)(=N-2,6-iPr₂C₆H₃)) from their corresponding chloride, bromide, and iodide analogues. From these reactions, the new (C₅Me₅)₂UF₂(L) (L = O=PPh₃, O=PCy₃) uranium fluoride complexes were isolated and characterized by NMR spectroscopy and X-ray crystallography.

Synthesis of Actinide Fluoride Complexes Using Trimethyltin Fluoride as a Mild and Selective Fluorinating Reagent

DOE PAGES

Kagan, Benjamin D.; Lichtscheidl, Alejandro G.; Erickson, Karla A.; ...

2017-11-07

Trimethyltin fluoride (Me₃SnF) is a mild and selective reagent for the installation of actinide fluoride bonds as demonstrated by the room temperature synthesis of a variety of organometallic and inorganic thorium(IV), uranium(IV), and uranium(V) fluoride complexes ((1,2,4-tBu₃C₅H₂)₂ThF₂, (C₅Me₅)₂U(F)(O-2,6-iPr₂C₆H₃), U(F)(O-2,6-tBu₂C₆H₃)₃, U(F)[N(SiMe₃)₂]₃ (C₅Me₅)₂UF₂(L) (L = O=PMe₃, O=PPh₃, O=PCy₃), and (C₅Me₅)₂U(F)(=N-2,6-iPr₂C₆H₃)) from their corresponding chloride, bromide, and iodide analogues. From these reactions, the new (C₅Me₅)₂UF₂(L) (L = O=PPh₃, O=PCy₃) uranium fluoride complexes were isolated and characterized by NMR spectroscopy and X-ray crystallography.

Radium and uranium concentrations and associated hydrogeochemistry in ground water in southwestern Pueblo County, Colorado

USGS Publications Warehouse

Felmlee, J. Karen; Cadigan, Robert Allen

1979-01-01

Radium and uranium concentrations in water from 37 wells tapping the aquifer system of the Dakota Sandstone and Purgatoire Formation in southwestern Pueblo County, Colorado, have a wide range of values and define several areas of high radioactivity in the ground water. Radium ranges from 0.3 to 420 picocuries per liter and has a median value of 8.8, and uranium ranges from 0.02 to 180 micrograms per liter and has a median value of 2.4. Radon concentrations, measured in 32 of the 37 wells, range from less than 100 picocuries per liter to as much as 27,000 and have a median value of 580. Relationships among the radioactive elements and 28 other geochemical parameters were studied by using correlation coefficients and R-mode factor analysis. Five factor groups were determined to represent major influences on water chemistry: (1) short-term solution reactions, (2) oxidation reactions, (3) hydrolysis reactions, (4) uranium distribution, and (5) long-term solution reactions. Uranium concentrations are most strongly influenced by oxidation reactions but also are affected by solution reactions and distribution of uranium in the rocks of the aquifer system. Radon and radium concentrations are mostly controlled by uranium distribution; radium also shows a moderate negative relationship with oxidation. To explain the statistical and spatial relationships among the parameters, a model was developed involving the selective leaching of uranium-bearing phases and metal sulfides which occur in discontinuous zones in sandstone and shale. When reducing conditions prevail, uranium is immobile, but radium can be taken into solution. When faults and associated fractured rocks allow oxidizing conditions to dominate, uranium can be taken into solution; radium can also be taken into solution, or it may become immobilized by coprecipitation with iron and manganese oxides or with barite. Several areas within the study area are discussed in terms of the model.

A Comparison of Naturally-Occurring and Artificially Stimulated Uranium(VI) Bioreduction in Sediment from a Field-scale Experiment in Rifle, CO

NASA Astrophysics Data System (ADS)

Campbell, K. M.; Williams, K. H.; Lesher, E.; Davis, J. A.; Long, P. E.

2007-12-01

Long-term remediation of uranium (U)-contaminated groundwater poses one of the greatest challenges in the clean-up of impacted sites. One solution is to reduce dissolved U(VI) to insoluble U(IV) precipitates by stimulating indigenous metal reducing bacterial populations in situ. Contamination from a former U mine tailings repository (Rifle, CO) provides a research site to study the efficacy of biostimulated U(VI) reduction at the field scale. Several cores were drilled in June 2007 across a region of naturally-occurring U(VI) bioreduction. The cores represent a cross section of sediment that ranges from minimally reducing to highly reducing. Anaerobic sediment samples from the cores were analyzed for labile U(VI) content by carbonate extraction in anoxic conditions (pH 9.4, 14 mM NaHCO3, 2.8 mM Na2CO¬3). A subset of the same core sections were dried and oxidized by exposure to air for 2 weeks. The carbonate extraction was repeated, and the amount of U(IV) present in the anaerobic sample was calculated by difference between the anoxic and oxidized extractions. An acid extraction was also performed on the oxidized sediments to compare the carbonate extractable and the acid extractable U fractions. The highest U concentrations were found in the highly bioreduced sediment, with the majority of U present as U(IV) (66-92%). The regions of highest bioreduction also correspond to elevated concentrations of solid phase organic carbon, suggesting that natural bioreduction is stimulated by zones of increased organic carbon content. The same field site was then used for an artificially stimulated bioreduction experiment, where the indigenous bacterial community was stimulated by injecting acetate upgradient of the core collection location. Carbonate and acid extractions were performed on core samples taken after the completion of the acetate injection. This work evaluates the composition of the sediment before and after biostimulation as a way of directly comparing the extent of natural U(VI) bioreduction to acetate-stimulated bioreduction in order to facilitate the design of a more effective bioremediation strategy for this site.

230Th-234U Model-Ages of Some Uranium Standard Reference Materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Williams, R W; Gaffney, A M; Kristo, M J

The 'age' of a sample of uranium is an important aspect of a nuclear forensic investigation and of the attribution of the material to its source. To the extent that the sample obeys the standard rules of radiochronometry, then the production ages of even very recent material can be determined using the {sup 230}Th-{sup 234}U chronometer. These standard rules may be summarized as (a) the daughter/parent ratio at time=zero must be known, and (b) there has been no daughter/parent fractionation since production. For most samples of uranium, the 'ages' determined using this chronometer are semantically 'model-ages' because (a) some assumptionmore » of the initial {sup 230}Th content in the sample is required and (b) closed-system behavior is assumed. The uranium standard reference materials originally prepared and distributed by the former US National Bureau of Standards and now distributed by New Brunswick Laboratory as certified reference materials (NBS SRM = NBL CRM) are good candidates for samples where both rules are met. The U isotopic standards have known purification and production dates, and closed-system behavior in the solid form (U{sub 3}O{sub 8}) may be assumed with confidence. We present here {sup 230}Th-{sup 234}U model-ages for several of these standards, determined by isotope dilution mass spectrometry using a multicollector ICP-MS, and compare these ages with their known production history.« less

Room temperature electrodeposition of actinides from ionic solutions

DOEpatents

Hatchett, David W.; Czerwinski, Kenneth R.; Droessler, Janelle; Kinyanjui, John

2017-04-25

Uranic and transuranic metals and metal oxides are first dissolved in ozone compositions. The resulting solution in ozone can be further dissolved in ionic liquids to form a second solution. The metals in the second solution are then electrochemically deposited from the second solutions as room temperature ionic liquid (RTIL), tri-methyl-n-butyl ammonium n-bis(trifluoromethansulfonylimide) [Me.sub.3N.sup.nBu][TFSI] providing an alternative non-aqueous system for the extraction and reclamation of actinides from reprocessed fuel materials. Deposition of U metal is achieved using TFSI complexes of U(III) and U(IV) containing the anion common to the RTIL. TFSI complexes of uranium were produced to ensure solubility of the species in the ionic liquid. The methods provide a first measure of the thermodynamic properties of U metal deposition using Uranium complexes with different oxidation states from RTIL solution at room temperature.

The association of uranium with organic matter in Holocene peat: An experimental leaching study

USGS Publications Warehouse

Zielinski, R.A.; Meier, A.L.

1988-01-01

Uraniferous peat was sampled from surface layers of a Holocene U deposit in northeastern Washington State. Dried, sized, and homogenized peat that contained 5980 ??307 ppm U was subjected to a variety of leaching conditions to determine the nature and strength of U-organic bonding in recently accumulated organic matter. The results complement previous experimental studies of U uptake on peat and suggest some natural or anthropogenic disturbances that are favorable for remobilizing U. The fraction of U leached in 24 h experiments at 25??C ranged from 0 to 95%. The most effective leach solutions contained anions capable of forming stable dissolved complexes with uranyl (UO2+2) cation. These included H2SO4 (pH = 1.5) and concentrated (>0.01 M) solutions of sodium bicarbonate-carbonate (pH = 7.0-10.0), or sodium pyrophosphate (pH = 10). Effective leaching by carbonate and pyrophosphate in the absence of added oxidant, and the insignificant effect of added oxidant (as pressurized O2) strongly suggest that U is initially fixed on organic matter as an oxidized U(VI) species. Uranium is more strongly bound than some other polyvalent cations, based on its resistance to exchange in the presence of large excesses of dissolved Ca2+ and Cu2+. Measurements of the rate of U leaching indicate faster rates in acid solution compared to carbonate solution, and are consisten with simultaneous attack of sites with different affinities for U. Sulfuric acid appears a good choice for commercial extraction of U from mined peat. In situ disturbances such as overliming of peat soils, addition of fertilizers containing pyrophosphate, or incursions of natural carbonate-rich waters could produce significant remobilization of U, and possibly compromise the quality of local domestic water supplies. ?? 1988.

Interaction between U/UO2 bilayers and hydrogen studied by in-situ X-ray diffraction

NASA Astrophysics Data System (ADS)

Darnbrough, J. E.; Harker, R. M.; Griffiths, I.; Wermeille, D.; Lander, G. H.; Springell, R.

2018-04-01

This paper reports experiments investigating the reaction of H2 with uranium metal-oxide bilayers. The bilayers consist of ≤ 100 nm of epitaxial α-U (grown on a Nb buffer deposited on sapphire) with a UO2 overlayer of thicknesses of between 20 and 80 nm. The oxides were made either by depositing via reactive magnetron sputtering, or allowing the uranium metal to oxidise in air at room temperature. The bilayers were exposed to hydrogen, with sample temperatures between 80 and 200 C, and monitored via in-situ x-ray diffraction and complimentary experiments conducted using Scanning Transmission Electron Microscopy - Electron Energy Loss Spectroscopy (STEM-EELS). Small partial pressures of H2 caused rapid consumption of the U metal and lead to changes in the intensity and position of the diffraction peaks from both the UO2 overlayers and the U metal. There is an orientational dependence in the rate of U consumption. From changes in the lattice parameter we deduce that hydrogen enters both the oxide and metal layers, contracting the oxide and expanding the metal. The air-grown oxide overlayers appear to hinder the H2-reaction up to a threshold dose, but then on heating from 80 to 140 C the consumption is more rapid than for the as-deposited overlayers. STEM-EELS establishes that the U-hydride layer lies at the oxide-metal interface, and that the initial formation is at defects or grain boundaries, and involves the formation of amorphous and/or nanocrystalline UH3. This explains why no diffraction peaks from UH3 are observed.

Evaluating chemical extraction techniques for the determination of uranium oxidation state in reduced aquifer sediments.

PubMed

Stoliker, Deborah L; Campbell, Kate M; Fox, Patricia M; Singer, David M; Kaviani, Nazila; Carey, Minna; Peck, Nicole E; Bargar, John R; Kent, Douglas B; Davis, James A

2013-08-20

Extraction techniques utilizing high pH and (bi)carbonate concentrations were evaluated for their efficacy in determining the oxidation state of uranium (U) in reduced sediments collected from Rifle, CO. Differences in dissolved concentrations between oxic and anoxic extractions have been proposed as a means to quantify the U(VI) and U(IV) content of sediments. An additional step was added to anoxic extractions using a strong anion exchange resin to separate dissolved U(IV) and U(VI). X-ray spectroscopy showed that U(IV) in the sediments was present as polymerized precipitates similar to uraninite and/or less ordered U(IV), referred to as non-uraninite U(IV) species associated with biomass (NUSAB). Extractions of sediment containing both uraninite and NUSAB displayed higher dissolved uranium concentrations under oxic than anoxic conditions while extractions of sediment dominated by NUSAB resulted in identical dissolved U concentrations. Dissolved U(IV) was rapidly oxidized under anoxic conditions in all experiments. Uraninite reacted minimally under anoxic conditions but thermodynamic calculations show that its propensity to oxidize is sensitive to solution chemistry and sediment mineralogy. A universal method for quantification of U(IV) and U(VI) in sediments has not yet been developed but the chemical extractions, when combined with solid-phase characterization, have a narrow range of applicability for sediments without U(VI).

Evaluating chemical extraction techniques for the determination of uranium oxidation state in reduced aquifer sediments

USGS Publications Warehouse

Stoliker, Deborah L.; Campbell, Kate M.; Fox, Patricia M.; Singer, David M.; Kaviani, Nazila; Carey, Minna; Peck, Nicole E.; Barger, John R.; Kent, Douglas B.; Davis, James A.

2013-01-01

Extraction techniques utilizing high pH and (bi)carbonate concentrations were evaluated for their efficacy in determining the oxidation state of uranium (U) in reduced sediments collected from Rifle, CO. Differences in dissolved concentrations between oxic and anoxic extractions have been proposed as a means to quantify the U(VI) and U(IV) content of sediments. An additional step was added to anoxic extractions using a strong anion exchange resin to separate dissolved U(IV) and U(VI). X-ray spectroscopy showed that U(IV) in the sediments was present as polymerized precipitates similar to uraninite and/or less ordered U(IV), referred to as non-uraninite U(IV) species associated with biomass (NUSAB). Extractions of sediment containing both uraninite and NUSAB displayed higher dissolved uranium concentrations under oxic than anoxic conditions while extractions of sediment dominated by NUSAB resulted in identical dissolved U concentrations. Dissolved U(IV) was rapidly oxidized under anoxic conditions in all experiments. Uraninite reacted minimally under anoxic conditions but thermodynamic calculations show that its propensity to oxidize is sensitive to solution chemistry and sediment mineralogy. A universal method for quantification of U(IV) and U(VI) in sediments has not yet been developed but the chemical extractions, when combined with solid-phase characterization, have a narrow range of applicability for sediments without U(VI).

Investigation of uranium geochemistry along groundwater flow path in the Continental Intercalaire aquifer (Southern Tunisia).

PubMed

Dhaoui, Z; Chkir, N; Zouari, K; Ammar, F Hadj; Agoune, A

2016-06-01

Environmental tracers ((2)H, (18)O, isotopes of Uranium) and geochemical processes occurring within groundwaters from the Continental Intercalaire (CI) in Southern Tunisia were used to understand the hydrodynamics and the recharge conditions of this aquifer. This study investigates the chemical and isotopic compositions of the CI groundwater. The water types are dominated by Na(+), SO4(2-), Cl(-) throughout most of the basin with a general increase in total dissolved solids from the Saharan Platform margins towards the Chotts region. Large scale groundwater flow paths are toward the Chotts region. The stable isotopes composition of the analyzed groundwater ranges from -8.8 to -6‰ vs V-SMOW for δ(18)O and from -67 to -40‰ vs V-SMOW for δ(2)H. The relatively enriched stable isotopes contents suggest the contribution of the Dahar sandstones outcrops in the current recharge of the CI aquifer in an arid context. However, the most depleted values in heavy isotopes indicate a paleorecharge of the aquifer under wetter conditions revealing a long residence time of groundwaters. The results from water samples using alpha spectrometry method indicate a range in (238)U concentrations and (234)U/(238)U activity ratios (AR) of 0.044-1.285 μg kg(-1) and 1.2 to 8.84 respectively. The geochemistry of uranium isotopes in groundwater is controlled by many factors, essentially, the influence of water rock interactions, the preferential dissolution of (234)U relative to (238)U due to alpha recoil and the mixing processes between different waters with distinct AR as well as (238)U concentrations. Copyright © 2016 Elsevier Ltd. All rights reserved.

Manufacturing Methods for the Production of Field Effect Electron Emitters from Oxide-Metal Composites.

DTIC Science & Technology

1977-12-01

Internal Zone Melting, Oxide-Metal Eutectic Structures ABSTRACT (Continue X reverae elde II neceaetrry end Identity by block nwbor* -^>This report...To- Uranium (0/U) Ratio B. Storage of "As-Received" Powders C. Moisture Content D. Oxidation Properties E. Sintering Properties F. Particle Size... Nickel - Vanadium 3.3 Nickel -Al203 3.4 Nickel -Tungsten 3.5 Copper-410 Stainless Steel C. Etching 1. Chemical Etching 2. Thermal Annealing 3. Ion

Fate of Uranium in Wetlands: Impact of Drought Followed by Re-flooding

NASA Astrophysics Data System (ADS)

Gilson, E.; Huang, S.; Koster van Groos, P. G.; Scheckel, K.; Peacock, A. D.; Kaplan, D. I.; Jaffe, P. R.

2014-12-01

Uranium contamination in groundwater can be mitigated in anoxic zones by iron-reducing bacteria that reduce soluble U(VI) to insoluble U(IV) and by uranium immobilization through complexation and sorption. Wetlands often link ground and surface-waters, making them strategic systems for potentially limiting migration of uranium contamination. Little is known about how drought periods that result in the drying of wetland soils, and consequent redox changes, affect uranium fate and transport in wetlands. In order to better understand the fate and stability of immobilized uranium in wetland soils, and how dry periods affect the uranium stability, we dosed saturated wetland mesocosms planted with Scirpus acutus with low levels of uranyl-acetate for 5 months before imposing a 9-day drying period followed by a 13-day rewetting period. Concentrations of uranium in mesocosm effluent increased after rewetting, but the cumulative amount of uranium released in the 13 days following the drying constituted less than 1% of the uranium immobilized in the soil during the 5 months prior to the drought. This low level of remobilization suggests that the uranium immobilized in these soils was not primarily bioreduced U(IV), which could have been oxidized to soluble U(VI) during the drought and released in the effluent during the subsequent flood. XANES analyses confirm that most of the uranium immobilized in the mesocosms was U(VI) sorbed to iron oxides. Compared to mesocosms that did not experience drying or rewetting, mesocosms that were sacrificed immediately after drying and after 13 days of rewetting had less uranium in soil near roots and more uranium on root surfaces. Metal-reducing bacteria only dominated the bacterial community after 13 days of rewetting and not immediately after drying, indicating that these bacteria are not responsible for this redistribution of uranium after the drying and rewetting. Results show that short periods of drought conditions in a wetland may impact uranium distribution, but these conditions may not cause large losses of immobilized uranium from the wetland.

Periodic trends in hexanuclear actinide clusters.

PubMed

Diwu, Juan; Wang, Shuao; Albrecht-Schmitt, Thomas E

2012-04-02

Four new Th(IV), U(IV), and Np(IV) hexanuclear clusters with 1,2-phenylenediphosphonate as the bridging ligand have been prepared by self-assembly at room temperature. The structures of Th(6)Tl(3)[C(6)H(4)(PO(3))(PO(3)H)](6)(NO(3))(7)(H(2)O)(6)·(NO(3))(2)·4H(2)O (Th6-3), (NH(4))(8.11)Np(12)Rb(3.89)[C(6)H(4)(PO(3))(PO(3)H)](12)(NO(3))(24)·15H(2)O (Np6-1), (NH(4))(4)U(12)Cs(8)[C(6)H(4)(PO(3))(PO(3)H)](12)(NO(3))(24)·18H(2)O (U6-1), and (NH(4))(4)U(12)Cs(2)[C(6)H(4)(PO(3))(PO(3)H)](12)(NO(3))(18)·40H(2)O (U6-2) are described and compared with other clusters of containing An(IV) or Ce(IV). All of the clusters share the common formula M(6)(H(2)O)(m)[C(6)H(3)(PO(3))(PO(3)H)](6)(NO(3))(n)((6-n)) (M = Ce, Th, U, Np, Pu). The metal centers are normally nine-coordinate, with five oxygen atoms from the ligand and an additional four either occupied by NO(3)(-) or H(2)O. It was found that the Ce, U, and Pu clusters favor both C(3i) and C(i) point groups, while Th only yields in C(i), and Np only C(3i). In the C(3i) clusters, there are two NO(3)(-) anions bonded to the metal centers. In the C(i) clusters, the number of NO(3)(-) anions varies from 0 to 2. The change in the ionic radius of the actinide ions tunes the cavity size of the clusters. The thorium clusters were found to accept larger ions including Cs(+) and Tl(+), whereas with uranium and later elements, only NH(4)(+) and/or Rb(+) reside in the center of the clusters.

Physico-Chemical Heterogeneity of Organic-Rich Sediments in the Rifle Aquifer, CO: Impact on Uranium Biogeochemistry.

PubMed

Janot, Noémie; Lezama Pacheco, Juan S; Pham, Don Q; O'Brien, Timothy M; Hausladen, Debra; Noël, Vincent; Lallier, Florent; Maher, Kate; Fendorf, Scott; Williams, Kenneth H; Long, Philip E; Bargar, John R

2016-01-05

The Rifle alluvial aquifer along the Colorado River in west central Colorado contains fine-grained, diffusion-limited sediment lenses that are substantially enriched in organic carbon and sulfides, as well as uranium, from previous milling operations. These naturally reduced zones (NRZs) coincide spatially with a persistent uranium groundwater plume. There is concern that uranium release from NRZs is contributing to plume persistence or will do so in the future. To better define the physical extent, heterogeneity and biogeochemistry of these NRZs, we investigated sediment cores from five neighboring wells. The main NRZ body exhibited uranium concentrations up to 100 mg/kg U as U(IV) and contains ca. 286 g of U in total. Uranium accumulated only in areas where organic carbon and reduced sulfur (as iron sulfides) were present, emphasizing the importance of sulfate-reducing conditions to uranium retention and the essential role of organic matter. NRZs further exhibited centimeter-scale variations in both redox status and particle size. Mackinawite, greigite, pyrite and sulfate coexist in the sediments, indicating that dynamic redox cycling occurs within NRZs and that their internal portions can be seasonally oxidized. We show that oxidative U(VI) release to the aquifer has the potential to sustain a groundwater contaminant plume for centuries. NRZs, known to exist in other uranium-contaminated aquifers, may be regionally important to uranium persistence.

Weathering processes and dating of soil profiles from São Paulo State, Brazil, by U-isotopes disequilibria.

PubMed

Bonotto, Daniel Marcos; Jiménez-Rueda, Jairo Roberto; Fagundes, Isabella Cruz; Filho, Carlos Roberto Alves Fonseca

2017-01-01

This study reports the use of the U-series radionuclides 238 U and 234 U for dating two soil profiles. The soil horizons developed over sandstones from Tatuí and Pirambóia formations at the Paraná sedimentary basin, São Paulo State, Brazil. Chemical data in conjunction with the 234 U/ 238 U activity ratios (AR's) of the soil horizons allowed investigating the U-isotopes mobility in the shallow oxidizing environment. Kaolinization and laterization processes are taking place in the profiles sampled, as they are especially common in regions characterized by a wet and dry tropical climate and a water table that is close to the surface. These processes are implied by inverse significant correlations between silica and iron in both soil profiles. Iron oxides were also very important to retain uranium in the two sites investigated, helping on the understanding of the weathering processes acting there. 238 U and its progeny 234 U permitted evaluating the processes of physical and chemical alteration, allowing the suggestion of a possible timescale corresponding to the Middle Pleistocene for the development of the more superficial soil horizons. Copyright © 2016 Elsevier Ltd. All rights reserved.

The Influence of Oxygen and Sulfur on Uranium Partitioning Into the Core

NASA Astrophysics Data System (ADS)

Moore, R. D., Jr.; Van Orman, J. A.; Hauck, S. A., II

2017-12-01

Uranium, along with K and Th, may provide substantial long-term heating in planetary cores, depending on the magnitude of their partitioning into the metal during differentiation. In general, non-metallic light elements are known to have a large influence on the partitioning of trace elements, and the presence of sulfur is known to enhance the partitioning of uranium into the metal. Data from the steelmaking literature indicate that oxygen also enhances the solubility of oxygen in liquid iron alloys. Here we present experimental data on the partitioning of U between immiscible liquids in the Fe-S-O system, and use these data along with published metal-silicate partitioning data to calibrate a quantitative activity model for U in the metal. We also determined partition coefficients for Th, K, Nb, Nd, Sm, and Yb, but were unable to fully constrain activity models for these elements with available data. A Monte Carlo fitting routine was used to calculate U-S, U-O, and U-S-O interaction coefficients, and their associated uncertainties. We find that the combined interaction of uranium with sulfur and oxygen is predominant, with S and O together enhancing the solubility of uranium to a far greater degree than either element in isolation. This suggests that uranium complexes with sulfite or sulfate species in the metal. For a model Mars core composition containing 14 at% S and 5 at% O, the metal/silicate partition coefficient for U is predicted to be an order of magnitude larger than for a pure Fe-Ni core.

Mild hydrothermal crystal growth of new uranium(IV) fluorides, Na3.13Mg1.43U6F30 and Na2.50Mn1.75U6F30: Structures, optical and magnetic properties

NASA Astrophysics Data System (ADS)

Yeon, Jeongho; Smith, Mark D.; Tapp, Joshua; Möller, Angela; zur Loye, Hans-Conrad

2016-04-01

Two new uranium(IV) fluorides, Na3.13Mg1.43U6F30 (1) and Na2.50Mn1.75U6F30 (2), were synthesized through an in situ mild hydrothermal route, and were structurally characterized by single crystal X-ray diffraction. The compounds exhibit complex crystal structures composed of corner- or edge-shared UF9 and MF6 (M=Mg, Mn) polyhedra, forming hexagonal channels in the three-dimensional framework, in which ordered or disordered divalent metal and sodium atoms reside. The large hexagonal voids contain the nearly regular M(II)F6 octahedra and sodium ions, whereas the small hexagonal cavities include M(II) and sodium ions on a mixed-occupied site. Magnetic susceptibility measurements yielded effective magnetic moments of 8.36 and 11.6 μB for 1 and 2, respectively, confirming the presence and oxidation states of U(IV) and Mn(II). The large negative Weiss constants indicate the spin gap between a triplet and a singlet state in the U(IV). Magnetization data as a function of applied fields revealed that 2 exhibits paramagnetic behavior due to the nonmagnetic singlet ground state of U(IV) at low temperature. UV-vis diffuse reflectance and X-ray photoelectron spectroscopy data were also analyzed.

Synthesis and characterization of a new and electronically unusual uranium metallacyclocumulene, (C 5Me 5) 2U(η 4-1,2,3,4-PhC 4Ph)

DOE PAGES

Pagano, Justin K.; Erickson, Karla A.; Scott, Brian L.; ...

2016-10-22

A new uranium metallacyclocumulene, (C 5Me 5) 2U(η 4-1,2,3,4-PhC 4Ph), was synthesized by both reaction of (C 5Me 5) 2UCl 2 with 1,4-diphenylbutadiyne in the presence of KC 8 and by ligand exchange between (C 5Me 5) 2U(η 2-Me 3SiC 2SiMe 3) and 1,4-diphenylbutadiyne. Lastly, full characterization of (C 5Me 5) 2U(η 4-1,2,3,4-PhC 4Ph) is reported, including the solid-state structure. (C 5Me 5) 2U(η 4-1,2,3,4-PhC 4Ph) displays an unusually detailed UV–visible spectrum, which is rare for uranium(IV) metallocene complexes.

Synthesis and characterization of a new and electronically unusual uranium metallacyclocumulene, (C 5Me 5) 2U(η 4-1,2,3,4-PhC 4Ph)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pagano, Justin K.; Erickson, Karla A.; Scott, Brian L.

A new uranium metallacyclocumulene, (C 5Me 5) 2U(η 4-1,2,3,4-PhC 4Ph), was synthesized by both reaction of (C 5Me 5) 2UCl 2 with 1,4-diphenylbutadiyne in the presence of KC 8 and by ligand exchange between (C 5Me 5) 2U(η 2-Me 3SiC 2SiMe 3) and 1,4-diphenylbutadiyne. Lastly, full characterization of (C 5Me 5) 2U(η 4-1,2,3,4-PhC 4Ph) is reported, including the solid-state structure. (C 5Me 5) 2U(η 4-1,2,3,4-PhC 4Ph) displays an unusually detailed UV–visible spectrum, which is rare for uranium(IV) metallocene complexes.

Uranium delivery and uptake in a montane wetland, north-central Colorado, USA

USGS Publications Warehouse

Schumann, R. Randall; Zielinski, Robert A.; Otton, James K.; Pantea, Michael P.; Orem, William H.

2017-01-01

Comprehensive sampling of peat, underlying lakebed sediments, and coexisting waters of a naturally uraniferous montane wetland are combined with hydrologic measurements to define the important controls on uranium (U) supply and uptake. The major source of U to the wetland is groundwater flowing through locally fractured and faulted granite gneiss of Proterozoic age. Dissolved U concentrations in four springs and one seep ranged from 20 to 83 ppb (μg/l). Maximum U concentrations are ∼300 ppm (mg/kg) in lakebed sediments and >3000 ppm in peat. Uranium in lakebed sediments is primarily stratabound in the more organic-rich layers, but samples of similar organic content display variable U concentrations. Post-depositional modifications include variable additions of U delivered by groundwater. Uranium distribution in peat is heterogeneous and primarily controlled by proximity to groundwater-fed springs and seeps that act as local point sources of U, and by proximity to groundwater directed along the peat/lakebeds contact. Uranium is initially sorbed on various organic components of peat as oxidized U(VI) present in groundwater. Selective extractions indicate that the majority of sorbed U remains as the oxidized species despite reducing conditions that should favor formation of U(IV). Possible explanations are kinetic hindrances related to strong complex formation between uranyl and humic substances, inhibition of anaerobic bacterial activity by low supply of dissolved iron and sulfate, and by cold temperatures.

In situ bioremediation of uranium with emulsified vegetable oil as the electron donor.

PubMed

Watson, David B; Wu, Wei-Min; Mehlhorn, Tonia; Tang, Guoping; Earles, Jennifer; Lowe, Kenneth; Gihring, Thomas M; Zhang, Gengxin; Phillips, Jana; Boyanov, Maxim I; Spalding, Brian P; Schadt, Christopher; Kemner, Kenneth M; Criddle, Craig S; Jardine, Philip M; Brooks, Scott C

2013-06-18

A field test with a one-time emulsified vegetable oil (EVO) injection was conducted to assess the capacity of EVO to sustain uranium bioreduction in a high-permeability gravel layer with groundwater concentrations of (mM) U, 0.0055; Ca, 2.98; NO3(-), 0.11; HCO3(-), 5.07; and SO4(2-), 1.23. Comparison of bromide and EVO migration and distribution indicated that a majority of the injected EVO was retained in the subsurface from the injection wells to 50 m downgradient. Nitrate, uranium, and sulfate were sequentially removed from the groundwater within 1-2 weeks, accompanied by an increase in acetate, Mn, Fe, and methane concentrations. Due to the slow release and degradation of EVO with time, reducing conditions were sustained for approximately one year, and daily U discharge to a creek, located approximately 50 m from the injection wells, decreased by 80% within 100 days. Total U discharge was reduced by 50% over the one-year period. Reduction of U(VI) to U(IV) was confirmed by synchrotron analysis of recovered aquifer solids. Oxidants (e.g., dissolved oxygen, nitrate) flowing in from upgradient appeared to reoxidize and remobilize uranium after the EVO was exhausted as evidenced by a transient increase of U concentration above ambient values. Occasional (e.g., annual) EVO injection into a permeable Ca and bicarbonate-containing aquifer can sustain uranium bioreduction/immobilization and decrease U migration/discharge.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Eppich, Gary R.; Williams, Ross W.; Gaffney, Amy M.

Here, age dating of nuclear material can provide insight into source and suspected use in nuclear forensic investigations. We report here a method for the determination of the date of most recent chemical purification for uranium materials using the 235U- 231Pa chronometer. Protactinium is separated from uranium and neptunium matrices using anion exchange resin, followed by sorption of Pa to an SiO 2 medium. The concentration of 231Pa is measured by isotope dilution mass spectrometry using 233Pa spikes prepared from an aliquot of 237Np and calibrated in-house using the rock standard Table Mountain Latite and the uranium isotopic standard U100.more » Combined uncertainties of age dates using this method are 1.5 to 3.5 %, an improvement over alpha spectrometry measurement methods. Model ages of five uranium standard reference materials are presented; all standards have concordant 235U- 231Pa and 234U- 230Th model ages.« less

Fast Oxidation Processes in a Naturally Reduced Aquifer Zone Caused by Dissolved Oxygen

NASA Astrophysics Data System (ADS)

Davis, J. A.; Jemison, N. E.; Williams, K. H.; Hobson, C.; Bush, R. P.

2014-12-01

The occurrence of naturally reduced zones is quite common in alluvial aquifers in the western U.S.A. due to the burial of woody debris in flood plains. The naturally reduced zones are heterogeneously dispersed in such aquifers and are characterized by high concentrations of organic carbon and reduced phases, including iron sulfides and reduced forms of metals, including uranium(IV). The persistence of high concentrations of dissolved uranium(VI) at uranium-contaminated aquifers on the Colorado Plateau has been attributed to slow oxidation of insoluble uranium(IV) mineral phases that are found in association with these natural reducing zones, although there is little understanding of the relative importance of various potential oxidants. Three field experiments were conducted within an alluvial aquifer adjacent to the Colorado River near Rifle, CO wherein groundwater associated with naturally reduced zones was pumped into a gas-impermeable tank, mixed with a conservative tracer (Br-), bubbled with a gas phase composed of 97% O2 and 3% CO2, and then returned to the subsurface in the same well from which it was withdrawn. Within minutes of re-injection of the oxygenated groundwater, dissolved uranium(VI) concentrations increased from less than 1 μM to greater than 2.5 μM, demonstrating that oxygen can be an important oxidant for uranium in these field systems if supplied to the naturally reduced zones. Small concentrations of nitrate were also observed in the previously nitrate-free groundwater, and Fe(II) decreased to the detection limit. These results contrast with other laboratory and field results in which oxygen was introduced to systems containing high concentrations of mackinawite (FeS) rather than the more crystalline iron sulfides found in aged, naturally reduced zones. The flux of oxygen to the naturally reduced zones in the alluvial aquifers occurs mainly through interactions between groundwater and gas phases at the water table, and seasonal variations of the water table at the Rifle, CO site may play an important role in introducing oxygen into the system. Although oxygen was introduced directly to the naturally reduced zones in these experiments, delivery of oxidants to the system may normally be controlled by other oxidative pathways in which oxygen plays an indirect role.

The crystal structure of ianthinite, [U 24+(UO 2) 4O 6(OH) 4(H 2O) 4](H 2O) 5: a possible phase for Pu 4+ incorporation during the oxidation of spent nuclear fuel

NASA Astrophysics Data System (ADS)

Burns, Peter C.; Finch, Robert J.; Hawthorne, Frank C.; Miller, Mark L.; Ewing, Rodney C.

1997-10-01

Ianthinite, [U 24+(UO 2) 4O 6(OH) 4(H 2O) 4](H 2O) 5, is the only known uranyl oxide hydrate mineral that contains U 4+, and it has been proposed that ianthinite may be an important Pu 4+-bearing phase during the oxidative dissolution of spent nuclear fuel. The crystal structure of ianthinite, orthorhombic, a = 0.7178(2), b = 1.1473(2), c = 3.039(1) nm, V = 2.5027 nm 3Z = 4, space group P2 1cn, has been solved by direct methods and refined by least-squares methods to an R index of 9.7% and a wR index of 12.6% using 888 unique observed [| F| ≥ 5 σ | F|] reflections. The structure contains both U 4+. The U 6+ cations are present as roughly linear (U 6+O 2) 2+ uranyl ion (Ur) that are in turn coordinated by five O 2- and OH - located at the equatorial positions of pentagonal bipyramids. The U 4+ cations are coordinated by O 2-, OH - and H 2O in a distorted octahedral arrangement. The Ur φ5and U 4+| 6 (φ: O 2-, OH -, H 2O) polyhedra l sharing edges to for two symmetrically distinct sheets at z ≈ 0.0 and z ≈ 0.25 that are parallel to (001). The sheets have the β-U 3O 8 sheet anion-topology. There are five symmetrically distinct H 2O groips located at z ≈ 0.125 between the sheets of U φn polyhedra, and the sheets of U φn polyhedra are linked together only by hydrogen bonding to the intersheet H 2O groups. The crystal-chemical requirements of U 4+ and Pu 4+ are very similar, suggesting that extensive Pu 4+ ↔ U 4+ substitution may occur within the sheets of U φn polyhedra in trh structure of ianthinine.

Interdiffusion behavior of U3Si2 with FeCrAl via diffusion couple studies

NASA Astrophysics Data System (ADS)

Hoggan, Rita E.; He, Lingfeng; Harp, Jason M.

2018-04-01

Uranium silicide (U3Si2) is a candidate to replace uranium oxide (UO2) as light water reactor (LWR) fuel because of its higher thermal conductivity and higher fissile density relative to the current standard, UO2. A class of Fe, Cr, Al alloys collectively known as FeCrAl alloys that have superior mechanical and oxidation resistance are being considered as an alternative to the standard Zirconium based LWR cladding. The interdiffusion behavior between FeCrAl and U3Si2 is investigated in this study. Commercially available FeCrAl, along with U3Si2 pellets were placed in diffusion couples. Individual tests were ran at temperatures ranging from 500 °C to 1000 °C for 30 h and 100 h. The interdiffusion was analyzed with an optical microscope, scanning electron microscope, and transmission electron microscope. Uniform and planar interdiffusion layers along the material interface were illustrated with backscatter electron micrographs and energy-dispersive X-ray spectroscopy. Electron diffraction was used to validate phases present in the system, including distinct U2Fe3Si/UFe2 and UFeSi layers at the material interface. U and Fe diffused far into the FeCrAl and U3Si2 matrix, respectively, in the higher temperature tests. No interaction was observed at 500 °C for 30 h.

Uranium silicide pellet fabrication by powder metallurgy for accident tolerant fuel evaluation and irradiation

DOE PAGES

Harp, Jason Michael; Lessing, Paul Alan; Hoggan, Rita Elaine

2015-06-21

In collaboration with industry, Idaho National Laboratory is investigating uranium silicide for use in future light water reactor fuels as a more accident resistant alternative to uranium oxide base fuels. Specifically this project was focused on producing uranium silicide (U 3Si 2) pellets by conventional powder metallurgy with a density greater than 94% of the theoretical density. This work has produced a process to consistently produce pellets with the desired density through careful optimization of the process. Milling of the U 3Si 2 has been optimized and high phase purity U 3Si 2 has been successfully produced. Results are presentedmore » from sintering studies and microstructural examinations that illustrate the need for a finely ground reproducible particle size distribution in the source powder. The optimized process was used to produce pellets for the Accident Tolerant Fuel-1 irradiation experiment. The average density of these pellets was 11.54 ±0.06 g/cm 3. Additional characterization of the pellets by scaning electron microscopy and X-ray diffraction has also been performed. As a result, pellets produced in this work have been encapsulated for irradiation, and irradiation in the Advanced Test Reactor is expected soon.« less

Uranium silicide pellet fabrication by powder metallurgy for accident tolerant fuel evaluation and irradiation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Harp, Jason Michael; Lessing, Paul Alan; Hoggan, Rita Elaine

In collaboration with industry, Idaho National Laboratory is investigating uranium silicide for use in future light water reactor fuels as a more accident resistant alternative to uranium oxide base fuels. Specifically this project was focused on producing uranium silicide (U 3Si 2) pellets by conventional powder metallurgy with a density greater than 94% of the theoretical density. This work has produced a process to consistently produce pellets with the desired density through careful optimization of the process. Milling of the U 3Si 2 has been optimized and high phase purity U 3Si 2 has been successfully produced. Results are presentedmore » from sintering studies and microstructural examinations that illustrate the need for a finely ground reproducible particle size distribution in the source powder. The optimized process was used to produce pellets for the Accident Tolerant Fuel-1 irradiation experiment. The average density of these pellets was 11.54 ±0.06 g/cm 3. Additional characterization of the pellets by scaning electron microscopy and X-ray diffraction has also been performed. As a result, pellets produced in this work have been encapsulated for irradiation, and irradiation in the Advanced Test Reactor is expected soon.« less

The measurement of U(VI) and Np(IV) mass transfer in a single stage centrifugal contactor

NASA Astrophysics Data System (ADS)

May, I.; Birkett, E. J.; Denniss, I. S.; Gaubert, E. T.; Jobson, M.

2000-07-01

BNFL currently operates two reprocessing plants for the conversion of spent nuclear fuel into uranium and plutonium products for fabrication into uranium oxide and mixed uranium and plutonium oxide (MOX) fuels. To safeguard the future commercial viability of this process, BNFL is developing novel single cycle flowsheets that can be operated in conjunction with intensified centrifugal contactors.

An aerosol particle containing enriched uranium encountered in the remote upper troposphere.

PubMed

Murphy, D M; Froyd, K D; Apel, E; Blake, D; Blake, N; Evangeliou, N; Hornbrook, R S; Peischl, J; Ray, E; Ryerson, T B; Thompson, C; Stohl, A

2018-04-01

We describe a submicron aerosol particle sampled at an altitude of 7 km near the Aleutian Islands that contained a small percentage of enriched uranium oxide. 235 U was 3.1 ± 0.5% of 238 U. During twenty years of aircraft sampling of millions of particles in the global atmosphere, we have rarely encountered a particle with a similarly high content of 238 U and never a particle with enriched 235 U. The bulk of the particle consisted of material consistent with combustion of heavy fuel oil. Analysis of wind trajectories and particle dispersion model results show that the particle could have originated from a variety of areas across Asia. The source of such a particle is unclear, and the particle is described here in case it indicates a novel source where enriched uranium was dispersed. Published by Elsevier Ltd.

Biological reduction of uranium coupled with oxidation of ammonium by Acidimicrobiaceae bacterium A6 under iron reducing conditions.

PubMed

Gilson, Emily R; Huang, Shan; Jaffé, Peter R

2015-11-01

This study investigated the possibility of links between the biological immobilization of uranium (U) and ammonium oxidation under iron (Fe) reducing conditions. The recently-identified Acidimicrobiaceae bacterium A6 (ATCC, PTA-122488) derives energy from ammonium oxidation coupled with Fe reduction. This bacterium has been found in various soil and wetland environments, including U-contaminated wetland sediments. Incubations of Acidimicrobiaceae bacteria A6 with nontronite, an Fe(III)-rich clay, and approximately 10 µM U indicate that these bacteria can use U(VI) in addition to Fe(III) as an electron acceptor in the presence of ammonium. Measurements of Fe(II) production and ammonium oxidation support this interpretation. Concentrations of approximately 100 µM U were found to entirely inhibit Acidimicrobiaceae bacteria A6 activity. These results suggest that natural sites of active ammonium oxidation under Fe reducing conditions by Acidimicrobiaceae bacteria A6 could be hotspots of U immobilization by bioreduction. This is the first report of biological U reduction that is not coupled to carbon oxidation.

Studies of the kinetics and mechanism of the oxidation of uranium by dry and moist air A model for determining the oxidation rate over a wide range of temperatures and water vapour pressures

NASA Astrophysics Data System (ADS)

McGillivray, G. W.; Geeson, D. A.; Greenwood, R. C.

1994-01-01

The rate of oxidation of uranium metal by moist air has been measured at temperatures from 115 to 350°C and water vapour pressures from 0 to 47 kPa (350 Torr). From this and from previously reported data, a model has been developed which allows the rate of uranium oxidation to be calculated at any particular combination of temperature and water vapour pressure of interest, in the range 0-350°C and 0-101.3 kPa (760 Torr). The model is based on the assumption that the surface concentration of water determines the rate of reaction and that the adsorption of water onto the oxide follows a Langmuir type isotherm. Theoretical plots of rate as a function of water vapour pressure and Arrhenius plots derived from the model have been shown to be in good agreement with experimental data. The model assumes separate contributions to the overall observed rate from oxygen and water vapour. Surface studies have been carried out using SIMS (secondary ion mass spectrometry). Depth profiling of the oxide produced by isotopically labelled reagents ( 18O 2 and H 218O), has shown that oxygen from both reactants is incorporated into the oxide layer in the ratio predicted by the kinetic model. This supports a mechanism in which oxygen and water vapour produce separate diffusing species (possibly O 2- and OH -).

Luminescence of powdered uranium glasses

NASA Technical Reports Server (NTRS)

Eubanks, A. G.; Mcgarrity, J. M.; Silverman, J.

1974-01-01

Measurement of cathodoluminescence and photoluminescence efficiencies in powdered borosilicate glasses having different particle size and different uranium content. Excitation with 100 to 350 keV electrons and with 253.7 nm light was found to produce identical absolute radiant exitance spectra in powdered samples. The most efficient glass was one containing 29.4 wt% B2O3, 58.8 wt% SiO2, 9.8 wt% Na2O and 2.0 wt% UO2.

Uptake and speciation of uranium in synthetic gypsum (CaSO4•2H2O): Applications to radioactive mine tailings.

PubMed

Lin, Jinru; Sun, Wei; Desmarais, Jacques; Chen, Ning; Feng, Renfei; Zhang, Patrick; Li, Dien; Lieu, Arthur; Tse, John S; Pan, Yuanming

2018-01-01

Phosphogypsum formed from the production of phosphoric acid represents by far the biggest accumulation of gypsum-rich wastes in the world and commonly contains elevated radionuclides, including uranium, as well as other heavy metals and metalloids. Therefore, billions-of-tons of phosphogypsum stockpiled worldwide not only possess serious environmental problems but also represent a potential uranium resource. Gypsum is also a major solid constituent in many other types of radioactive mine tailings, which stems from the common usage of sulfuric acid in extraction processes. Therefore, management and remediation of radioactive mine tailings as well as future beneficiation of uranium from phosphogysum all require detailed knowledge about the nature and behavior of uranium in gypsum. However, little is known about the uptake mechanism or speciation of uranium in gypsum. In this study, synthesis experiments suggest an apparent pH control on the uptake of uranium in gypsum at ambient conditions: increase in U from 16 μg/g at pH = 6.5 to 339 μg/g at pH = 9.5. Uranium L 3 -edge synchrotron X-ray absorption spectroscopic analyses of synthetic gypsum show that uranyl (UO 2 ) 2+ at the Ca site is the dominant species. The EXAFS fitting results also indicate that uranyl in synthetic gypsum occurs most likely as carbonate complexes and yields an average U-O distance ∼0.25 Å shorter than the average Ca-O distance, signifying a marked local structural distortion. Applications to phosphogypsum from the New Wales phosphoric acid plant (Florida, USA) and uranium mine tailings from the Key Lake mill (Saskatchewan, Canada) show that gypsum is an important carrier of uranium over a wide range of pH and controls the fate of this radionuclide in mine tailings. Also, development of new technologies for recovering U from phosphogypsum in the future must consider lattice-bound uranyl in gypsum. Copyright © 2017 Elsevier Ltd. All rights reserved.

Uranium and minor-element partitioning in Fe-Ti oxides and zircon from partially melted granodiorite, Crater Lake, Oregon

USGS Publications Warehouse

Tourrette, T.Z.L.; Burnett, D.S.; Bacon, C.R.

1991-01-01

Crystal-liquid partitioning in Fe-Ti oxides and zircon was studied in partially melted granodiorite blocks ejected during the climactic eruption of Mt. Mazama (Crater Lake), Oregon. The blocks, which contain up to 33% rhyolite glass (75 wt% SiO2), are interpreted to be portions of the magma chamber walls that were torn off during eruption. The glass is clear and well homogenized for all measured elements except Zr. Results for Fe-Ti oxides give DUoxide/liq ??? 0.1. Partitioning of Mg, Mn, Al, Si, V, and Cr in Fe-Ti oxides indicates that grains surrounded by glass are moderately well equilibrated with the melt for many of the minor elements, while those that are inclusions in relict plagioclase are not. Uranium and ytterbium inhomogeneities in zircons indicate that the zircons have only partially equilibrated with the melt and that uranium appears to have been diffusing out of the zircons faster than the zircons were dissolving. Minimum U, Y, and P concentrations in zircons give maximum DUzrc/liq = 13,DYzrc/liq = 23, and DPzrc/liq = 1, but these are considerably lower than reported by other workers for U and Y. Based on our measurements and given their low abundances in most rocks, Fe-Ti oxides probably do not play a major role in U-Th fractionation during partial melting. The partial melts were undersaturated with zircon and apatite, but both phases are present in our samples. This demonstrates an actual case of non-equilibrium source retention of accessory phases, which in general could be an important trace-element fractionation mechanism. Our results do not support the hypothesis that liquid structure is the dominant factor controlling trace-element partitioning in high-silica rhyolites. Rough calculations based on Zr gradients in the glass indicate that the samples could have been partially molten for 800 to 8000 years. ?? 1991.

The effect of calcium on aqueous uranium(VI) speciation and adsorption to ferrihydrite and quartz

USGS Publications Warehouse

Fox, P.M.; Davis, J.A.; Zachara, J.M.

2006-01-01

Recent studies of uranium(VI) geochemistry have focused on the potentially important role of the aqueous species, CaUO2 (CO3)32- and Ca2 UO2(CO3)30(aq), on inhibition of microbial reduction and uranium(VI) aqueous speciation in contaminated groundwater. However, to our knowledge, there have been no direct studies of the effects of these species on U(VI) adsorption by mineral phases. The sorption of U(VI) on quartz and ferrihydrite was investigated in NaNO3 solutions equilibrated with either ambient air (430 ppm CO2) or 2% CO2 in the presence of 0, 1.8, or 8.9 mM Ca2+. Under conditions where the Ca2UO2(CO3)30 (aq) species predominates U(VI) aqueous speciation, the presence of Ca in solution lowered U(VI) adsorption on quartz from 77% in the absence of Ca to 42% and 10% at Ca concentrations of 1.8 and 8.9 mM, respectively. U(VI) adsorption to ferrihydrite decreased from 83% in the absence of Ca to 57% in the presence of 1.8 mM Ca. Surface complexation model predictions that included the formation constant for aqueous Ca2UO2(CO3)30(aq) accurately simulated the effect of Ca2+ on U(VI) sorption onto quartz and ferrihydrite within the thermodynamic uncertainty of the stability constant value. This study confirms that Ca2+ can have a significant impact on the aqueous speciation of U(VI), and consequently, on the sorption and mobility of U(VI) in aquifers. ?? 2005 Elsevier Inc. All rights reserved.

Excision of uranium oxide chains and ribbons in the novel one-dimensional uranyl iodates K(2)[(UO(2))3(IO(3))(4)O(2)] and Ba[(UO(2)2(IO(3))(2)O(2)](H(2)O).

PubMed

Bean, A C; Ruf, M; Albrecht-Schmitt, T E

2001-07-30

The alkali metal and alkaline-earth metal uranyl iodates K(2)[(UO(2))(3)(IO(3))(4)O(2)] and Ba[(UO(2))(2)(IO(3))(2)O(2)](H(2)O) have been prepared from the hydrothermal reactions of KCl or BaCl(2) with UO(3) and I(2)O(5) at 425 and 180 degrees C, respectively. While K(2)[(UO(2))(3)(IO(3))(4)O(2)] can be synthesized under both mild and supercritical conditions, the yield increases from <5% to 73% as the temperature is raised from 180 to 425 degrees C. Ba[(UO(2))(2)(IO(3))(2)O(2)](H(2)O), however, has only been isolated from reactions performed in the mild temperature regime. Thermal measurements (DSC) indicate that K(2)[(UO(2))(3)(IO(3))(4)O(2)] is more stable than Ba[(UO(2))(2)(IO(3))(2)O(2)](H(2)O) and that both compounds decompose through thermal disproportionation at 579 and 575 degrees C, respectively. The difference in the thermal behavior of these compounds provides a basis for the divergence of their preparation temperatures. The structure of K(2)[(UO(2))(3)(IO(3))(4)O(2)] is composed of [(UO(2))(3)(IO(3))(4)O(2)](2)(-) chains built from the edge-sharing UO(7) pentagonal bipyramids and UO(6) octahedra. Ba[(UO(2))(2)(IO(3))(2)O(2)](H(2)O) consists of one-dimensional [(UO(2))(2)(IO(3))(2)O(2)](2)(-) ribbons formed from the edge sharing of distorted UO(7) pentagonal bipyramids. In both compounds the iodate groups occur in both bridging and monodentate binding modes and further serve to terminate the edges of the uranium oxide chains. The K(+) or Ba(2+) cations separate the chains or ribbons in these compounds forming bonds with terminal oxygen atoms from the iodate ligands. Crystallographic data: K(2)[(UO(2))(3)(IO(3))(4)O(2)], triclinic, space group P_1, a = 7.0372(5) A, b = 7.7727(5) A, c = 8.9851(6) A, alpha = 93.386(1) degrees, beta = 105.668(1) degrees, gamma = 91.339(1) degrees, Z = 1; Ba[(UO(2))(2)(IO(3))(2)O(2)](H(2)O), monoclinic, space group P2(1)/c, a = 8.062(4) A, b = 6.940(3) A, c = 21.67(1), beta= 98.05(1) degrees, Z = 4.

Genetic and grade and tonnage models for sandstone-hosted roll-type uranium deposits, Texas Coastal Plain, USA

USGS Publications Warehouse

Hall, Susan M.; Mihalasky, Mark J.; Tureck, Kathleen; Hammarstrom, Jane M.; Hannon, Mark

2017-01-01

The coincidence of a number of geologic and climatic factors combined to create conditions favorable for the development of mineable concentrations of uranium hosted by Eocene through Pliocene sandstones in the Texas Coastal Plain. Here 254 uranium occurrences, including 169 deposits, 73 prospects, 6 showings and 4 anomalies, have been identified. About 80 million pounds of U3O8 have been produced and about 60 million pounds of identified producible U3O8 remain in place. The development of economic roll-type uranium deposits requires a source, large-scale transport of uranium in groundwater, and deposition in reducing zones within a sedimentary sequence. The weight of the evidence supports a source from thick sequences of volcanic ash and volcaniclastic sediment derived mostly from the Trans-Pecos volcanic field and Sierra Madre Occidental that lie west of the region. The thickest accumulations of source material were deposited and preserved south and west of the San Marcos arch in the Catahoula Formation. By the early Oligocene, a formerly uniformly subtropical climate along the Gulf Coast transitioned to a zoned climate in which the southwestern portion of Texas Coastal Plain was dry, and the eastern portion humid. The more arid climate in the southwestern area supported weathering of volcanic ash source rocks during pedogenesis and early diagenesis, concentration of uranium in groundwater and movement through host sediments. During the middle Tertiary Era, abundant clastic sediments were deposited in thick sequences by bed-load dominated fluvial systems in long-lived channel complexes that provided transmissive conduits favoring transport of uranium-rich groundwater. Groundwater transported uranium through permeable sandstones that were hydrologically connected with source rocks, commonly across formation boundaries driven by isostatic loading and eustatic sea level changes. Uranium roll fronts formed as a result of the interaction of uranium-rich groundwater with either (1) organic-rich debris adjacent to large long-lived fluvial channels and barrier–bar sequences or (2) extrinsic reductants entrained in formation water or discrete gas that migrated into host units via faults and along the flanks of salt domes and shale diapirs. The southwestern portion of the region, the Rio Grande embayment, contains all the necessary factors required for roll-type uranium deposits. However, the eastern portion of the region, the Houston embayment, is challenged by a humid environment and a lack of source rock and transmissive units, which may combine to preclude the deposition of economic deposits. A grade and tonnage model for the Texas Coastal Plain shows that the Texas deposits represent a lower tonnage subset of roll-type deposits that occur around the world, and required aggregation of production centers into deposits based on geologic interpretation for the purpose of conducting a quantitative mineral resource assessment.

Oxygen potentials of mixed oxide fuels for fast reactors

NASA Astrophysics Data System (ADS)

Kato, M.; Tamura, T.; Konashi, K.

2009-03-01

Oxygen potentials of homogenous (Pu0.2U0.8)O2-x and (Am0.02Pu0.30Np0.02U0.66)O2-x which have been developed as fuels for fast breeder reactors were measured at temperatures of 1473-1623 K by a gas equilibrium method using an (Ar, H2, H2O) gas mixture. The measured oxygen potentials of (Pu0.2U0.8)O2-x were about 25 kJ mol-1 lower than those of (Pu0.3U0.7)O2-x measured previously and were consistent with the values calculated by Besmann and Lindemer's model. The measured oxygen potentials of (Am0.02Pu0.30Np0.02U0.66)O2-x were slightly higher than those of MOX without minor actinides. No fuel-cladding chemical interaction is affected significantly by adding their minor actinides.

Extracellular reduction of uranium via Geobacter conductive pili as a protective cellular mechanism.

PubMed

Cologgi, Dena L; Lampa-Pastirk, Sanela; Speers, Allison M; Kelly, Shelly D; Reguera, Gemma

2011-09-13

The in situ stimulation of Fe(III) oxide reduction by Geobacter bacteria leads to the concomitant precipitation of hexavalent uranium [U(VI)] from groundwater. Despite its promise for the bioremediation of uranium contaminants, the biological mechanism behind this reaction remains elusive. Because Fe(III) oxide reduction requires the expression of Geobacter's conductive pili, we evaluated their contribution to uranium reduction in Geobacter sulfurreducens grown under pili-inducing or noninducing conditions. A pilin-deficient mutant and a genetically complemented strain with reduced outer membrane c-cytochrome content were used as controls. Pili expression significantly enhanced the rate and extent of uranium immobilization per cell and prevented periplasmic mineralization. As a result, pili expression also preserved the vital respiratory activities of the cell envelope and the cell's viability. Uranium preferentially precipitated along the pili and, to a lesser extent, on outer membrane redox-active foci. In contrast, the pilus-defective strains had different degrees of periplasmic mineralization matching well with their outer membrane c-cytochrome content. X-ray absorption spectroscopy analyses demonstrated the extracellular reduction of U(VI) by the pili to mononuclear tetravalent uranium U(IV) complexed by carbon-containing ligands, consistent with a biological reduction. In contrast, the U(IV) in the pilin-deficient mutant cells also required an additional phosphorous ligand, in agreement with the predominantly periplasmic mineralization of uranium observed in this strain. These findings demonstrate a previously unrecognized role for Geobacter conductive pili in the extracellular reduction of uranium, and highlight its essential function as a catalytic and protective cellular mechanism that is of interest for the bioremediation of uranium-contaminated groundwater.

A charge-optimized many-body potential for the U-UO2-O2 system

NASA Astrophysics Data System (ADS)

Li, Yangzhong; Liang, Tao; Sinnott, Susan B.; Phillpot, Simon R.

2013-12-01

Building on previous charge-optimized many-body (COMB) potentials for metallic α-U and gaseous O2, we have developed a new potential for UO2, which also allows the simulation of U-UO2-O2 systems. The UO2 lattice parameter, elastic constants and formation energies of stoichiometric and non-stoichiometric intrinsic defects are well reproduced. Moreover, this is the first rigid-ion potential that produces the correct deviation of the Cauchy relation, as well as the first classical interatomic potential that is able to determine the defect energies of non-stoichiometric intrinsic point defects in UO2 with an appropriate reference state. The oxygen molecule interstitial in the α-U structure is shown to decompose, with some U-O bonds approaching the natural bond length of perfect UO2. Finally, we demonstrate the capability of this COMB potential to simulate a complex system by performing a simulation of the α-U + O2 → UO2 phase transformation. We also identify a possible mechanism for uranium oxidation and the orientation of the resulting fluorite UO2 structure relative to the coordinate system of orthorhombic α-U.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bromfield, C.S.; Grauch, R.I.; Otton, J.K.

The Richfield Quadrangle in west-central Utah was evaluated to identify areas favorable for the occurrence of uranium deposits known or likely to contain 100 tons of uranium with an average grade of not less than 100 ppM U/sub 3/O/sub 8/. Geologic reconnaissance was made of all known environments thought to be favorable for uranium deposits, and a representative selection of uranium occurrences reported in the literature was visited. Geochemical analyses from rock and limited water samples were used in the evaluation. Preliminary and incomplete aeroradiometric data and hydrogeochemical and stream-sediment analyses arrived too late in the program to be field-checkedmore » or to be adequately analyzed for this report. Two areas favorable for uranium deposits were delineated: (1) volcanogenic deposits (class 500 to 599) in association with Miocene Mount Belknap rhyolite, and acidic plutons in the Marysvale Volcanic Field in the Antelope Range and Tushar Mountains; and (2) volcanogenic (class 500 to 599) and/or magmatic hydrothermal deposits (class 330) associated with Miocene high-silica high-alkali rhyolite tuffs, flows, and hypabyssal intrusives in volcanic or subvolcanic environments in the southern Wah Wah Mountains.« less

Crystal chemistry of pyrochlore from the Mesozoic Panda Hill carbonatite deposit, western Tanzania

NASA Astrophysics Data System (ADS)

Boniface, Nelson

2017-02-01

The Mesozoic Panda Hill carbonatite deposit in western Tanzania hosts pyrochlore, an ore and source of niobium. This study was conducted to establish the contents of radioactive elements (uranium and thorium) in pyrochlore along with the concentration of niobium in the ore. The pyrochlore is mainly hosted in sövite and is structurally controlled by NW-SE (SW dipping) or NE-SW (NW dipping) magmatic flow bands with dip angles of between 60° and 90°. Higher concentrations of pyrochlore are associated with magnetite, apatite and/or phlogopite rich flow bands. Electron microprobe analyses on single crystals of pyrochlore yield very low UO2 concentrations that range between 0 and 0.09 wt% (equivalent to 0 atoms per formula unit: a.p.f.u.) and ThO2 between 0.55 and 1.05 wt% (equivalent to 0.1 a.p.f.u.). The analyses reveal high concentrations of Nb2O5 (ranging between 57.13 and 65.50 wt%, equivalent to a.p.f.u. ranging between 1.33 and 1.43) and therefore the Panda Hill Nb-oxide is classified as pyrochlore sensu stricto. These data point to a non radioactive pyrochlore and a deposit rich in Nb at Panda Hill. The Panda Hill pyrochlore has low concentrations of REEs as displayed by La2O3 that range between 0.10 and 0.49 wt% (equivalent to a.p.f.u. ranging between 0 and 0.01) and Ce2O3 ranging between 0.86 and 1.80 wt% (equivalent to a.p.f.u. ranging between 0.02 and 0.03), Pr2O3 concentrations range between 0 and 0.23 wt% (equivalent to 0 a.p.f.u.), and Y2O3 is 0 wt% (equivalent to 0 a.p.f.u.). The abundance of the REEs in pyroclore at the Panda Hill Carbonatite deposit is of no economic significance.

Actinide Foil Production for MPACT Research

DOE Office of Scientific and Technical Information (OSTI.GOV)

Beller, Denis

Sensitive fast-neutron detectors are required for use in lead slowing down spectrometry (LSDS), an active interrogation technique for used nuclear fuel assay for Materials Protection, Accounting, and Controls Technologies (MPACT). During the past several years UNLV sponsored a research project at RPI to investigate LSDS; began development of fission chamber detectors for use in LSDS experiments in collaboration with INL, LANL, and Oregon State U.; and participated in a LSDS experiment at LANL. In the LSDS technique, research has demonstrated that these fission chamber detectors must be sensitive to fission energy neutrons but insensitive to thermal-energy neutrons. Because most systemsmore » are highly sensitive to large thermal neutron populations due to the well-known large thermal cross section of 235U, even a miniscule amount of this isotope in a fission chamber will overwhelm the small population of higher-energy neutrons. Thus, fast-fission chamber detectors must be fabricated with highly depleted uranium (DU) or ultra-pure thorium (Th), which is about half as efficient as DU. Previous research conducted at RPI demonstrated that the required purity of DU for assay of used nuclear fuel using LSDS is less than 4 ppm 235U, material that until recently was not available in the U.S. In 2009 the PI purchased 3 grams of ultra-depleted uranium (uDU, 99.99998% 238U with just 0.2 ± 0.1 ppm 235U) from VNIIEF in Sarov, Russia. We received the material in the form of U3O8 powder in August of 2009, and verified its purity and depletion in a FY10 MPACT collaboration project. In addition, chemical processing for use in FC R&D was initiated, fission chamber detectors and a scanning alpha-particle spectrometer were developed, and foils were used in a preliminary LSDS experiment at a LANL/LANSCE in Sept. of 2010. The as-received U3O8 powder must be chemically processed to convert it to another chemical form while maintaining its purity, which then must be used to electro-deposit U or UO2 in extremely thin layers (1 to 2 mg/cm2) on various media such as films, foils, or discs. After many months of investigation and trials in FY10 and 11, UNLV researchers developed a new method to produce pure UO2 deposits on foils using a unique approach, which has never been demonstrated, that involves dissolution of U3O8 directly into room temperature ionic liquid (RTIL) followed by electrodeposition from the RTIL-uDU solution (Th deposition from RTIL had been previously demonstrated). The high-purity dissolution of the U3O8 permits the use of RTIL solutions for deposition of U on metal foils in layers without introducing contamination. In FY10 and early FY11 a natural U surrogate for the uDU was used to investigate this and other techniques. In this research project UNLV will deposit directly from RTIL to produce uDU and Th foils devoid of possible contaminants. After these layers have been deposited, they will be examined for purity and uniformity. UNLV will complete the development and demonstration of the RTIL technology/ methodology to prepare uDU and Th samples for use in constructing fast-neutron detectors. Although this material was purchased for use in research using fast-fission chamber detectors for active inspection techniques for MPACT, it could also contribute to R&D for other applications, such as cross section measurements or neutron spectroscopy for national security« less

Understanding Uranium Behavior in a Reduced Aquifer

NASA Astrophysics Data System (ADS)

Janot, N.; Lezama-Pacheco, J. S.; Williams, K. H.; Bernier-Latmani, R.; Long, P. E.; Davis, J. A.; Fox, P. M.; Yang, L.; Giammar, D.; Cerrato, J. M.; Bargar, J.

2012-12-01

Uranium contamination of groundwater is a concern at several US Department of Energy sites, such Old Rifle, CO. Uranium transport in the environment is mainly controlled by its oxidation state, since oxidized U(VI) is relatively mobile, whereas U(IV) is relatively insoluble. Bio-remediation of contaminated aquifers aims at immobilizing uranium in a reduced form. Previous laboratory and field studies have shown that adding electron donor (lactate, acetate, ethanol) to groundwater stimulates the activity of metal- and sulfate-reducing bacteria, which promotes U(VI) reduction in contaminated aquifers. However, obtaining information on chemical and physical forms of U, Fe and S species for sediments biostimulated in the field, as well as kinetic parameters such as U(VI) reduction rate, is challenging due to the low concentration of uranium in the aquifers (typically < 10 ppm) and the expense of collecting large number of cores. An in-situ technique has been developed for studying uranium, iron and sulfur reduction dynamics during such bioremediation episodes. This technique uses in-well columns to obtain direct access to chemical and physical forms of U(IV) produced in the aquifer, evolving microbial communities, and trace and major ion groundwater constituents. While several studies have explored bioreduction of uranium under sulfate-reducing conditions, less attention has been paid to the initial iron-reducing phase, noted as being of particular importance to uranium removal. The aim of this work was to assess the formation of U(IV) during the early stages of a bio-remediation experiment at the Old Rifle site, CO, from early iron-reducing conditions to the transition to sulfate-reducing conditions. Several in-well chromatographic columns packed with sediment were deployed and were sampled at different days after the start of bio-reduction. X-ray absorption spectroscopy and X-ray microscopy were used to obtain information on Fe, S and U speciation and distribution. Chemical extractions of the reduced sediments have also been performed, to determine the rate of Fe(II) and U(IV) accumulation.

Examination of U valence states in the brannerite structure by near-infrared diffuse reflectance and X-ray photoelectron spectroscopies

NASA Astrophysics Data System (ADS)

Finnie, Kim S.; Zhang, Zhaoming; Vance, Eric R.; Carter, Melody L.

2003-04-01

The valence state of uranium doped into a f 0 thorium analog of brannerite (i.e., thorutite) has been examined using near-infrared (NIR) diffuse reflectance (DRS) and X-ray photoelectron (XPS) spectroscopies. NIR transitions of U 4+, which are not observed in spectra of brannerite, have been detected in the samples of U xTh 1- xTi 2O 6, and we propose that strong specular reflectance is responsible for the lack of U 4+ features in UTi 2O 6. Characteristic U 5+ bands have been identified in samples in which sufficient Ca 2+ has been added to nominally effect complete oxidation to U 5+. XPS results support the assignments of U 4+ and U 5+ by DRS. The presence of residual U 4+ bands in the spectra of the Ca-doped samples is consistent with segregation of Ca 2+ to the grain boundaries during high temperature sintering.

National Uranium Resource Evaluation: Lewistown Quadrangle, Montana

DOE Office of Scientific and Technical Information (OSTI.GOV)

Culver, J.C.

1982-09-01

Uranium resources in the Lewistown Quadrangle, Montana, were evaluated to a depth of 1500 m (5000 ft). All existing geologic data were considered, including geologic surveys, literature, theses, radiometric surveys, oil- and water-well logs. Additional data were generated during the course of two field seasons, including the collection of more than 350 water, rock, crude oil and panned concentrate samples for analyses, sedimentary facies maps, structural geology and isopach maps, and field examination of reported areas of anomalous radioactivity. Three environments with potential for the occurrence of a minimum of 100 t of 0.01% U/sub 3/O/sub 8/ were delineated. Themore » most favorable environment is located in the southeastern portion of the quadrangle; here, Tertiary felsic dikes intrude four potential sandstone host rocks in the Kootenai Formation and the Colorado Shale. Structural-chemical traps for allogenic uranium are provided by the juxtaposition of oil-bearing domes. A second potential environment is located in the Eagle Sandstone in the northwestern and western portions of the quadrangle; here, anomalous water samples were obtained downtip from oxidized outcrops that are structurally related to Tertiary intrusive rocks of the Bearpaw and Highwood Mountains. Lignitic lenses and carbonaceous sandstones deposited in a near-shore lagoonal and deltaic environment provide potential reductants for hexavalent uranium in this environment. A third environment, in the Judith River Formation, was selected as favorable on the basis of water-well and gamma-ray log anomalies and their structural relationship with the Bearpaw Mountains. Organic materials are present in the Judith River Formation as potential reductants. They were deposited in a near-shore fluvial and lagoonal system similar to the depositional environment of the Jackson Group of the Texas Gulf Coast.« less

Chemical aspects of uranium behavior in soils: A review

NASA Astrophysics Data System (ADS)

Vodyanitskii, Yu. N.

2011-08-01

Uranium has varying degrees of oxidation (+4 and +6) and is responsive to changes in the redox potential of the environment. It is deposited at the reduction barrier with the participation of biota and at the sorption barrier under oxidative conditions. Iron (hydr)oxides are the strongest sorbents of uranium. Uranium, being an element of medium biological absorption, can accumulate (relative to thorium) in the humus horizons of some soils. The high content of uranium in uncontaminated soils is most frequently inherited from the parent rocks in the regions of positive U anomalies: in the soils developed on oil shales and in the marginal zone of bogs at the reduction barrier. The development of nuclear and coal-fired power engineering resulted in the environmental contamination with uranium. The immobilization of anthropogenic uranium at artificial geochemical barriers is based on two preconditions: the stimulation of on-site metal-reducing bacteria or the introduction of strong mineral reducers, e.g., Fe at low degrees of oxidation.

Phanerozoic extensional faulting and alteration control on uranium mineralization in trachytes of the Central Eastern Desert of Egypt

NASA Astrophysics Data System (ADS)

Hamdy, Mohamed M.; Waheeb, Anton G.; Aly, Samir M.; Farag, Nagdy M.; Sadek, Adel F.

2017-12-01

The Gabal Nasb El Atshan Upper Carboniferous-Lower Permian altered trachytes include uranium up to 3165 ppm. The paleostress and resolved shear stress analyses of the deformation systems in Gabal Nasb El Atshan area indicate that the trachyte was subjected to WNW-ESE to E-W tensile shear stress directed extensional regimes. The low-stress regions in the vicinity of extensional faults and their associated joints were favorable locations for fluid flow and the consequence alteration and U-mineralization. This occurred more extensively along the contacts between the sills of trachyte and the Hammamat sedimentary rocks; where the latter acted as a physical barrier for the alteration fluids migration outward. Alteration styles include albitization, aegirinization, arfvedsonization, chloritization and ferruginisation. The albitization is the most common sodic metasomatism, giving sanidine from Or98.8Ab0.7 to Or62.3Ab37.6, anorthoclase from Or51.4Ab48.0 to Or12.2Ab87.6 and albite from Or11.0Ab89.0 to Or0.8Ab99.2. Aegirine and arfvedsonite formed due to decreasing sodium activity in the metasomatic fluids. Sodic metasomatism may be the source of uranium-enrichment, taking place during the late magmatic to deuteric processes. This was followed by a retrograde alteration of chloritization between 175 and 42 °C toward precipitation of Fe-oxides and alteration of primary uranium. Surficial low-temperature alteration remobilized and redistributed the produced uranylhydroxides and ferruginisation caused the reduction and adsorption of U forming betafite, uranophane, soddyite, umohoite, uranotile and uranopilite.

Preliminary report of the uranium favorability of shear zones in the crystalline rocks of the southern Appalachians

DOE Office of Scientific and Technical Information (OSTI.GOV)

Penley, H.M.; Schot, E.H.; Sewell, J.M.

1978-11-01

Three sheared areas in the crystalline Piedmont and Blue Ridge provinces, from which uranium occurrences or anomalous radioactivity have been reported, were studied to determine their favorability for uranium mineralization. The study, which involved a literature review, geologic reconnaissance, ground radiometric surveys, and sampling of rock outcrops for petrographic and chemical analyses, indicates that more-detailed investigations of these and similar areas are warranted. In each area, surface leaching and deep residual cover make it difficult to assess the potential for uranium mineralization on the basis of results from chemical analyses for U/sub 3/O/sub 8/ and the radiometric surveys. Although anomalousmore » radioactivity and anomalous chemical uranium values were noted in only a few rock exposures and samples from the shear zones, the potential for uranium mineralization at depth could be much greater than indicated by these surface data. The study indicates that shear zones within Precambiran granitic basement complexes (such as the Wilson Creek Gneiss of western North Carolina, the Cranberry Gneiss of eastern Tennessee, and the Toxaway Gneiss of western South Carolina) are favorable as hosts for uranium and may contain subsurface deposits. Mylonitized graphitic schists immediately north of the Towaliga fault in Alabama and Georgia may be favorable host rocks for uranium.« less

Microbial reduction of uranium

USGS Publications Warehouse

Lovley, D.R.; Phillips, E.J.P.; Gorby, Y.A.; Landa, E.R.

1991-01-01

REDUCTION of the soluble, oxidized form of uranium, U(VI), to insoluble U(IV) is an important mechanism for the immobilization of uranium in aquatic sediments and for the formation of some uranium ores1-10. U(VI) reduction has generally been regarded as an abiological reaction in which sulphide, molecular hydrogen or organic compounds function as the reductant1,2,5,11. Microbial involvement in U(VI) reduction has been considered to be limited to indirect effects, such as microbial metabolism providing the reduced compounds for abiological U(VI) reduction and microbial cell walls providing a surface to stimulate abiological U(VI) reduction1,12,13. We report here, however, that dissimilatory Fe(III)-reducing microorganisms can obtain energy for growth by electron transport to U(VI). This novel form of microbial metabolism can be much faster than commonly cited abiological mechanisms for U(VI) reduction. Not only do these findings expand the known potential terminal electron acceptors for microbial energy transduction, they offer a likely explanation for the deposition of uranium in aquatic sediments and aquifers, and suggest a method for biological remediation of environments contaminated with uranium.

Formation of unprecedented actinidecarbon triple bonds in uranium methylidyne molecules

PubMed Central

Lyon, Jonathan T.; Hu, Han-Shi; Andrews, Lester; Li, Jun

2007-01-01

Chemistry of the actinide elements represents a challenging yet vital scientific frontier. Development of actinide chemistry requires fundamental understanding of the relative roles of actinide valence-region orbitals and the nature of their chemical bonding. We report here an experimental and theoretical investigation of the uranium methylidyne molecules X3UCH (X = F, Cl, Br), F2ClUCH, and F3UCF formed through reactions of laser-ablated uranium atoms and trihalomethanes or carbon tetrafluoride in excess argon. By using matrix infrared spectroscopy and relativistic quantum chemistry calculations, we have shown that these actinide complexes possess relatively strong UC triple bonds between the U 6d-5f hybrid orbitals and carbon 2s-2p orbitals. Electron-withdrawing ligands are critical in stabilizing the U(VI) oxidation state and sustaining the formation of uranium multiple bonds. These unique UC-bearing molecules are examples of the long-sought actinide-alkylidynes. This discovery opens the door to the rational synthesis of triple-bonded actinidecarbon compounds. PMID:18024591

Quantitative determination of environmental levels of uranium, thorium and plutonium in bone by solvent extraction and alpha spectrometry

NASA Astrophysics Data System (ADS)

Singh, Narayani P.; Zimmerman, Carol J.; Lewis, Laura L.; Wrenn, McDonald E.

1984-06-01

Solvent extraction and alpha-spectrometry have been emplyed in the quantitative simultaneous determination of uranium. thorium and plutonium. The bone specimens, spiked with 232U, 229Th and 242Pu tracers, are wet ashed with HNO 3 followed by alternate additions of a new drops of HNO 3 and H 2O 2. Uranium is reduced to the tetravalent state with 200 mg SnCl 2 and 25 ml HI. Uranium, thorium and plutonium are then coprecipitated with calcium as oxalate, heated to 550°C, dissolved in 50 ml HCl, and the acidity adjusted to 10 M. Uranium and plutonium are extracted into a 20% tri-lauryl amine (TLA) solution in xylene, leaving thorium in the aqueous phase. Plutonium is first back-extracted from the TLA phase by shaking with a 1:1.5 volume of 0.05 M NH 4I in 8 M HCl, which reduces Pu(IV) to Pu(III). Uranium is then back-extracted with an equal volume of 0.1 M HCl. Thorium, which was left in the aqueous phase, is evaporated to dryness, dissolved in 4 M HNO 3, and the acidity adjusted to 4 M. Thorium is then extracted into 20% TLA solution in xylene pre-equilibrated with 4 M HNO 3, and back-extracted with 10 M HCl. Uranium, thorium, and plutonium are then electrodeposited separately onto platinum discs and counted by an alpha-spectrometer with a multi-channel analyzer and surface barrier silicon diodes. The mean recoveries of uranium, thorium, and plutonium in bovine, dog, and human bones were over 70%.

High density dispersion fuel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hofman, G.L.

1996-09-01

A fuel development campaign that results in an aluminum plate-type fuel of unlimited LEU burnup capability with an uranium loading of 9 grams per cm{sup 3} of meat should be considered an unqualified success. The current worldwide approved and accepted highest loading is 4.8 g cm{sup {minus}3} with U{sub 3}Si{sub 2} as fuel. High-density uranium compounds offer no real density advantage over U{sub 3}Si{sub 2} and have less desirable fabrication and performance characteristics as well. Of the higher-density compounds, U{sub 3}Si has approximately a 30% higher uranium density but the density of the U{sub 6}X compounds would yield the factormore » 1.5 needed to achieve 9 g cm{sup {minus}3} uranium loading. Unfortunately, irradiation tests proved these peritectic compounds have poor swelling behavior. It is for this reason that the authors are turning to uranium alloys. The reason pure uranium was not seriously considered as a dispersion fuel is mainly due to its high rate of growth and swelling at low temperatures. This problem was solved at least for relatively low burnup application in non-dispersion fuel elements with small additions of Si, Fe, and Al. This so called adjusted uranium has nearly the same density as pure {alpha}-uranium and it seems prudent to reconsider this alloy as a dispersant. Further modifications of uranium metal to achieve higher burnup swelling stability involve stabilization of the cubic {gamma} phase at low temperatures where normally {alpha} phase exists. Several low neutron capture cross section elements such as Zr, Nb, Ti and Mo accomplish this in various degrees. The challenge is to produce a suitable form of fuel powder and develop a plate fabrication procedure, as well as obtain high burnup capability through irradiation testing.« less

Energy dependence of the trapping of uranium atoms by aluminum oxide surfaces

NASA Technical Reports Server (NTRS)

Librecht, K. G.

1979-01-01

The energy dependence of the trapping probability for sputtered U-235 atoms striking an oxidized aluminum collector surface at energies between 1 eV and 184 eV was measured. At the lowest energies, approximately 10% of the uranium atoms are not trapped, while above 10 eV essentially all of them stick. Trapping probabilities averaged over the sputtered energy distribution for uranium incident on gold and mica are also presented.

Geochemistry of vanadium in an epigenetic, sandstone-hosted vanadium- uranium deposit, Henry Basin, Utah

USGS Publications Warehouse

Wanty, R.B.; Goldhaber, M.B.; Northrop, H.R.

1990-01-01

The epigenetic Tony M vanadium-uranium orebody in south-central Utah is hosted in fluvial sandstones of the Morrison Formation (Upper Jurassic). Measurements of the relative amounts of V+3 and V +4 in ore minerals show that V+3 is more abundant. Thermodynamic calculations show that vanadium was more likely transported to the site of mineralization as V+4. The ore formed as V+4 was reduced by hydrogen sulfide, followed by hydrolysis and precipitation of V+3 in oxide minerals or chlorite. Uranium was transported as uranyl ion (U+6), or some complex thereof, and reduced by hydrogen sulfide, forming coffinite. Detrital organic matter in the rocks served as the carbon source for sulfate-reducing bacteria. Vanadium most likely was derived from the dissolution of iron-titanium oxides. Uranium probably was derived from the overlying Brushy Basin Member of the Morrison Formation. Previous studies have shown that the ore formed at the density-stratified interface between a basinal brine and dilute meteoric water. The mineralization processes described above occurred within the mixing zone between these two fluids. -from Authors

Uranyl-Peroxide Clusters Incorporating Iron Trimers and Bridging by Bisphosphonate- and Carboxylate-Containing Ligands.

PubMed

Qiu, Jie; Dong, Sining; Szymanowski, Jennifer E S; Dobrowolska, Malgorzata; Burns, Peter C

2017-04-03

A hybrid uranium-iron cage nanocluster, [(UO 2 ) 24 (FeOH) 24 (O 2 ) 24 (PO 4 ) 8 (CH(COO)(PO 3 ) 2 ) 24 ] 96- (U 24 Fe 24 ), was synthesized using bridging ligands containing bisphosphonate and carboxylate groups. U 24 Fe 24 contains six tetramers of uranyl hexagonal bipyramids and eight iron trimers, each of which consists of three corner-sharing Fe 3+ octahedra and is stabilized by in situ formed phosphate and 2,2-bis(phosphonato)acetate (C 2 P 2 ) groups. Tetramers and trimers are bridged by 24 C 2 P 2 groups into a cage cluster. Crystals of U 24 Fe 24 present a paramagnetic-like behavior. X-ray scattering showed that U 24 Fe 24 forms in the reactant solution prior to crystallization and is stable upon dissolution in water.

Uranium isotope composition of a laterite profile during extreme weathering of basalt in Guangdong, South China

NASA Astrophysics Data System (ADS)

Huang, J.; Zhou, Z.; Gong, Y.; Lundstrom, C.; Huang, F.

2015-12-01

Rock weathering and soil formation in the critical zone are important for material cycle from the solid Earth to superficial system. Laterite is a major type of soil in South China forming at hot-humid climate, which has strong effect on the global uranium cycle. Uranium is closely related to the environmental redox condition because U is stable at U(Ⅳ) in anoxic condition and U(Ⅵ) as soluble uranyl ion (UO22+) under oxic circumstance. In order to understand the behavior of U isotopes during crust weathering, here we report uranium isotopic compositions of soil and base rock samples from a laterite profile originated from extreme weathering of basalt in Guangdong, South China. The uranium isotopic data were measured on a Nu Plasma MC-ICP-MS at the University of Illinois at Urbana-Champaign using the double spike method. The δ238U of BCR-1 is -0.29±0.03‰ (relative to the international standard CRM-112A), corresponding to a 238U/235U ratio of 137.911±0.004. Our result of BCR-1 agrees with previous analyses (e.g., -0.28‰ in Weyer et al. 2008) [1]. U contents of the laterite profile decrease from 1.9 ppm to 0.9 ppm with depth, and peak at 160 - 170 cm (2.3 ppm), much higher than the U content of base rocks (~0.5 ppm). In contrary, U/Th of laterites is lower than that of base rock (0.27) except the peak at the depth of 160-170 cm (0.38), indicating significant U loss during weathering. Notably, U isotope compositions of soils show a small variation from -0.38 to -0.28‰, consistent with the base rock within analytical error (0.05‰ to 0.08‰, 2sd). Such small variation can be explained by a "rind effect" (Wang et al., 2015) [2], by which U(Ⅳ) can be completely oxidized to U(VI) layer by layer during basalt weathering by dissolved oxygen. Therefore, our study indicates that U loss during basalt weathering at the hot-humid climate does not change U isotope composition of superficial water system. [1] Weyer S. et al. (2008) Natural fractionation of 238U/235U. GCA 72,345-359 [2] Wang X. et al. (2015) Isotope fractionation during oxidation of tetravalent uranium by dissolved oxygen. GCA 150, 160-170

Characterization of U(VI)-carbonato ternary complexes on hematite: EXAFS and electrophoretic mobility measurements

USGS Publications Warehouse

Bargar, John R.; Reitmeyer, Rebecca; Lenhart, John J.; Davis, James A.

2000-01-01

We have measured U(VI) adsorption on hematite using EXAFS spectroscopy and electrophoresis under conditions relevant to surface waters and aquifers (0.01 to 10 μM dissolved uranium concentrations, in equilibrium with air, pH 4.5 to 8.5). Both techniques suggest the existence of anionic U(VI)-carbonato ternary complexes. Fits to EXAFS spectra indicate that U(VI) is simultaneously coordinated to surface FeO6 octahedra and carbonate (or bicarbonate) ligands in bidentate fashions, leading to the conclusion that the ternary complexes have an inner-sphere metal bridging (hematite-U(VI)-carbonato) structure. Greater than or equal to 50% of adsorbed U(VI) was comprised of monomeric hematite-U(VI)-carbonato ternary complexes, even at pH 4.5. Multimeric U(VI) species were observed at pH ≥ 6.5 and aqueous U(VI) concentrations approximately an order of magnitude more dilute than the solubility of crystalline β-UO2(OH)2. Based on structural constraints, these complexes were interpreted as dimeric hematite-U(VI)-carbonato ternary complexes. These results suggest that Fe-oxide-U(VI)-carbonato complexes are likely to be important transport-limiting species in oxic aquifers throughout a wide range of pH values.

Quantum mechanical calculation of aqueuous uranium complexes: carbonate, phosphate, organic and biomolecular species

PubMed Central

Kubicki, James D; Halada, Gary P; Jha, Prashant; Phillips, Brian L

2009-01-01

Background Quantum mechanical calculations were performed on a variety of uranium species representing U(VI), U(V), U(IV), U-carbonates, U-phosphates, U-oxalates, U-catecholates, U-phosphodiesters, U-phosphorylated N-acetyl-glucosamine (NAG), and U-2-Keto-3-doxyoctanoate (KDO) with explicit solvation by H2O molecules. These models represent major U species in natural waters and complexes on bacterial surfaces. The model results are compared to observed EXAFS, IR, Raman and NMR spectra. Results Agreement between experiment and theory is acceptable in most cases, and the reasons for discrepancies are discussed. Calculated Gibbs free energies are used to constrain which configurations are most likely to be stable under circumneutral pH conditions. Reduction of U(VI) to U(IV) is examined for the U-carbonate and U-catechol complexes. Conclusion Results on the potential energy differences between U(V)- and U(IV)-carbonate complexes suggest that the cause of slower disproportionation in this system is electrostatic repulsion between UO2 [CO3]35- ions that must approach one another to form U(VI) and U(IV) rather than a change in thermodynamic stability. Calculations on U-catechol species are consistent with the observation that UO22+ can oxidize catechol and form quinone-like species. In addition, outer-sphere complexation is predicted to be the most stable for U-catechol interactions based on calculated energies and comparison to 13C NMR spectra. Outer-sphere complexes (i.e., ion pairs bridged by water molecules) are predicted to be comparable in Gibbs free energy to inner-sphere complexes for a model carboxylic acid. Complexation of uranyl to phosphorus-containing groups in extracellular polymeric substances is predicted to favor phosphonate groups, such as that found in phosphorylated NAG, rather than phosphodiesters, such as those in nucleic acids. PMID:19689800

An unusual temperature dependence in the oxidation of oxycarbide layers on uranium

NASA Astrophysics Data System (ADS)

Ellis, Walton P.

1981-09-01

An anomalous temperature dependence has been observed for the oxidation kinetics of outermost oxycarbide layers on polycrystalline uranium metal. Normally, oxidation or corrosion reactions are expected to proceed more rapidly as the temperature is elevated. Thus, it came as a surprise when we observed that the removal of the outermost atomic layers of carbon from uranium oxycarbide by O 2 reproducibly proceeds at a much faster rate at 25°C than at 280°C.

An unusual temperature dependence in the oxidation of oxycarbide layers on uranium

NASA Astrophysics Data System (ADS)

Ellis, Walton P.

An anomalous temperature dependence has been observed for the oxidation kinetics of outermost oxycarbide layers on polycrystalline uranium metal. Normally, oxidation or corrosion reactions are expected to proceed more rapidly as the temperature is elevated. Thus, it came as a surprise when we observed that the removal of the outermost atomic layers of carbon from uranium oxycarbide by O 2 reproducibly proceeds at a much faster rate at 25°C than at 280°C.

Development of Novel Porous Sorbents for Extraction of Uranium from Seawater

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lin, Wenbin

Climate disruption is one of the greatest crises the global community faces in the 21st century. Alarming increases in CO 2, NO, SO 2 and particulate matter levels will have catastrophic consequences on the environment, food supplies, and human health if no action is taken to lessen their worldwide prevalence. Nuclear energy remains the only mature technology capable of continuous base-load power generation with ultralow carbon dioxide, nitric oxide, and sulfur dioxide emissions. Over the lifetime of the technology, nuclear energy outputs less than 1.5% the carbon dioxide emissions per gigawatt hour relative to coal—about as much as onshore windmore » power.1 However, in order for nuclear energy to be considered a viable option in the future, a stable supply of uranium must be secured. Current estimates suggest there is less than 100 years’ worth of uranium left in terrestrial ores (6.3 million tons) if current consumption levels remain unchanged.2 It is likely, however, that demand for nuclear fuel will rise as a direct consequence of the ratification of global climate accords. The oceans, containing approximately 4.5 billion tons of uranium (U) at a uniform concentration of ~3 ppb, represent a virtually limitless supply of this resource.3 Development of technologies to recover uranium from seawater would greatly improve the U resource availability, providing a U price ceiling for the current generation and sustaining the nuclear fuel supply for future generations. Several methods have been previously evaluated for uranium sequestration including solvent extraction, ion exchange, flotation, biomass collection, and adsorption; however, none have been found to be suitable for reasons including cost effectiveness, long term stability, and selectivity.4,5 While polymer beads and fibers have been functionalized with amidoxime functional groups to afford U adsorption capacities as high as 1.5 g U/kg,6 further discoveries are needed to make uranium extraction from seawater economically feasible.« less

Characterization of Uranium Ore Concentrate Chemical Composition via Raman Spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Su, Yin-Fong; Tonkyn, Russell G.; Sweet, Lucas E.

Uranium Ore Concentrate (UOC, often called yellowcake) is a generic term that describes the initial product resulting from the mining and subsequent milling of uranium ores en route to production of the U-compounds used in the fuel cycle. Depending on the mine, the ore, the chemical process, and the treatment parameters, UOC composition can vary greatly. With the recent advent of handheld spectrometers, we have chosen to investigate whether either commercial off-the-shelf (COTS) handheld devices or laboratory-grade Raman instruments might be able to i) identify UOC materials, and ii) differentiate UOC samples based on chemical composition and thus suggest themore » mining or milling process. Twenty-eight UOC samples were analyzed via FT-Raman spectroscopy using both 1064 nm and 785 nm excitation wavelengths. These data were also compared with results from a newly developed handheld COTS Raman spectrometer using a technique that lowers background fluorescence signal. Initial chemometric analysis was able to differentiate UOC samples based on mine location. Additional compositional information was obtained from the samples by performing XRD analysis on a subset of samples. The compositional information was integrated with chemometric analysis of the spectroscopic dataset allowing confirmation that class identification is possible based on compositional differences between the UOC samples, typically involving species such as U3O8, α-UO2(OH)2, UO4•2H2O (metastudtite), K(UO2)2O3, etc. While there are clearly excitation λ sensitivities, especially for dark samples, Raman analysis coupled with chemometric data treatment can nicely differentiate UOC samples based on composition and even mine origin.« less

Physico-chemical properties of Moringa oleifera seed oil enzymatically interesterified with palm stearin and palm kernel oil and its potential application in food.

PubMed

Dollah, Sarafhana; Abdulkarim, Sabo Mohammed; Ahmad, Siti Hajar; Khoramnia, Anahita; Mohd Ghazali, Hasanah

2016-08-01

High oleic acid Moringa oleifera seed oil (MoO) has been rarely applied in food products due to the low melting point and lack of plasticity. Enzymatic interesterification (EIE) of MoO with palm stearin (PS) and palm kernel oil (PKO) could yield harder fat stocks that may impart desirable nutritional and physical properties. Blends of MoO and PS or PKO were examined for triacylglycerol (TAG) composition, thermal properties and solid fat content (SFC). EIE caused rearrangement of TAGs, reduction of U3 and increase of U2 S in MoO/PS blends while reduction of U3 and S3 following increase of S2 U and U2 S in MoO/PKO blends (U, unsaturated and S, saturated fatty acids). SFC measurements revealed a wide range of plasticity, enhancements of spreadability, mouthfeel and cooling effect for interesterified MoO/PS, indicating the possible application of these blends in margarines. However, interesterified MoO/PKO was not suitable in margarine application, while ice-cream may be formulated from these blends. A soft margarine formulated from MoO/PS 70:30 revealed high oxidative stability during 8 weeks storage with no significant changes in peroxide and p-anisidine values. EIE of fats with MoO allowed nutritional and oxidative stable plastic fats to be obtained, suitable for possible use in industrial food applications. © 2015 Society of Chemical Industry. © 2015 Society of Chemical Industry.

Uranium Isotope Fractionation during Oxidation of Dissolved U(iv) and Synthetic Solid UO2

NASA Astrophysics Data System (ADS)

Wang, X.; Johnson, T. M.; Lundstrom, C. C.

2013-12-01

U isotopes (238U/235U) show promise as a tool for environmental monitoring of U contamination as well as a proxy for paleo-redox conditions. However, the isotopic fractionation mechanisms of U are still poorly understood. In groundwater systems, U(VI), a mobile contaminant, can be reduced to immobile U(IV) and thus remediated. Previous work shows that 238U/235U of the remaining U(VI) changes with the extent of reduction. Therefore, U(VI) isotope composition in groundwater can potentially be used to detect and perhaps quantify the extent of reduction. However, knowing if isotopic fractionation occurs during U(IV) oxidation is equally important. First, the reduced U(IV) (either solid or as dissolved organic complexes) potentially can be reoxidized to U(VI). If isotope fractionation occurs during oxidation, it would complicate the use of U isotope composition as a monitoring technique. Further, in natural weathering processes, U(IV) minerals are oxidized to form dissolved U(VI), which is carried to rivers and eventually to the ocean and deposited in marine sediments. The weathering cycle is thus sensitive to redox conditions, meaning the sedimentary U isotope record may serve as a paleoredox indicator, provided U isotope fractionation during oxidation and reduction are well known. We conducted experiments oxidizing 2 different U(IV) species by O2 and measuring isotopic fractionation factors. In one experiment, dissolved U(IV) in 0.1 N HCl (pH 1) was oxidized by entrained air. As oxidation proceeds at pH 1, the remaining dissolved U(IV) becomes progressively enriched in 238U in a linear trend, while the product U(VI) paralleled, but was offset to 1.0‰ lighter in 238U/235U. This linear progression of both remaining reactant and product suggests equilibrium fractionation during oxidation of dissolved U(IV) by O2. A second experiment oxidized synthetic, solid UO2 (in 20 mM NaHCO3, pH 7) with entrained air. The oxidative fractionation is very weak in this case with product U(VI) ~0.1‰ heavier than the remaining UO2. We attribute the lack of strong fractionation during oxidation of solid UO2 to a 'rind effect', where the surface layer must be completely oxidized before the next layer is exposed to oxidant. Hence, nearly complete, congruent conversion of each layer of U(IV) to U(VI) results in minimal isotope fractionation. A small amount of transient fractionation probably occurs initially, but this is quickly negated as the surface becomes isotopically fractionated. Interestingly, our measured ~0.1‰ U isotope fractionation during oxidation of solid U(IV) agrees with the natural observation that 238U/235U ratios in river water (mainly U(VI)) are ~0.1‰ greater than those in fresh continental rocks (primarily U(IV) minerals). Application of these results to natural settings should be done with caution, however. Oxidation of natural uraninite in continental rocks is a much slower process. If the U(VI) product and the U(IV) reactant remain in contact for long periods of time (e.g., months), they may evolve toward isotopic equilibrium. Measurements of 238U/235U in various natural weathering environments should be undertaken to examine this idea.

Analysis Of 2H-Evaporator Scale Pot Bottom Sample [HTF-13-11-28H

DOE Office of Scientific and Technical Information (OSTI.GOV)

Oji, L. N.

2013-07-15

Savannah River Remediation (SRR) is planning to remove a buildup of sodium aluminosilicate scale from the 2H-evaporator pot by loading and soaking the pot with heated 1.5 M nitric acid solution. Sampling and analysis of the scale material from the 2H evaporator has been performed so that the evaporator can be chemically cleaned beginning July of 2013. Historically, since the operation of the Defense Waste Processing Facility (DWPF), silicon in the DWPF recycle stream combines with aluminum in the typical tank farm supernate to form sodium aluminosilicate scale mineral deposits in the 2H-evaporator pot and gravity drain line. The 2H-evaporatormore » scale samples analyzed by Savannah River National Laboratory (SRNL) came from the bottom cone sections of the 2H-evaporator pot. The sample holder from the 2H-evaporator wall was virtually empty and was not included in the analysis. It is worth noting that after the delivery of these 2H-evaporator scale samples to SRNL for the analyses, the plant customer determined that the 2H evaporator could be operated for additional period prior to requiring cleaning. Therefore, there was no need for expedited sample analysis as was presented in the Technical Task Request. However, a second set of 2H evaporator scale samples were expected in May of 2013, which would need expedited sample analysis. X-ray diffraction analysis (XRD) confirmed the bottom cone section sample from the 2H-evaporator pot consisted of nitrated cancrinite, (a crystalline sodium aluminosilicate solid), clarkeite and uranium oxide. There were also mercury compound XRD peaks which could not be matched and further X-ray fluorescence (XRF) analysis of the sample confirmed the existence of elemental mercury or mercuric oxide. On ''as received'' basis, the scale contained an average of 7.09E+00 wt % total uranium (n = 3; st.dev. = 8.31E-01 wt %) with a U-235 enrichment of 5.80E-01 % (n = 3; st.dev. = 3.96E-02 %). The measured U-238 concentration was 7.05E+00 wt % (n=3, st. dev. = 8.25E-01 wt %). Analyses results for Pu-238 and Pu-239, and Pu-241 are 7.06E-05 {+-} 7.63E-06 wt %, 9.45E-04 {+-} 3.52E-05 wt %, and <2.24E-06 wt %, respectively. These results are provided so that SRR can calculate the equivalent uranium-235 concentrations for the NCSA. Because this 2H evaporator pot bottom scale sample contained a significant amount of elemental mercury (11.7 wt % average), it is recommended that analysis for mercury be included in future Technical Task Requests on 2H evaporator sample analysis at SRNL. Results confirm that the uranium contained in the scale remains depleted with respect to natural uranium. SRNL did not calculate an equivalent U-235 enrichment, which takes into account other fissionable isotopes U-233, Pu-239 and Pu-241.« less

'Pincer' dicarbene complexes of some early transition metals and uranium.

PubMed

Pugh, David; Wright, Joseph A; Freeman, Sandra; Danopoulos, Andreas A

2006-02-14

The complexes [(C-N-C)MX(n)(thf)(m)] with the 'pincer' 2,6-bis(imidazolylidene)pyridine, (C-N-C) = 2,6-bis(arylimidazol-2-ylidene)pyridine, aryl = 2,6-Pr(i)2C6H3, M = V, X = Cl, n = 2, m = 1 1a; M = Cr, X = Cl, n = 2, m = 0, 2a, X = Br, 2b; M = Mn, X = Br, n = 2, m = 0, 3; M = Nb, X = Cl, n = 3, m = 0, 4; and M = U, X = Cl, n = 4, m = 0, 5, were synthesised by (a) substitution of labile tmed (1a), thf (2a, 3, 5) or dme (4) by free (C-N-C) or by (b) reaction of the bisimidazolium salt (CH-N-CH)Br2 with {Cr[N(SiMe3)2]2(thf)2} followed by amine elimination (2b). Attempted alkylation of 1a, 2, 3a and 4 with Grignard or alkyl lithiums gave intractable mixtures, and in one case [reaction of 1a with (mesityl)MgBr] resulted in exchange of Cl by Br (1b). Oxidation of 1a or [(C-N-C)VCl3] with 4-methylmorpholine N-oxide afforded the trans-V(C-N-C)(=O)Cl2, 6, which by reaction with AgBF4 in MeCN gave trans-[V(C-N-C)(=O)(MeCN)2][BF4]2, 7. Reaction of 1a with p-tolyl azide gave trans-V(C-N-C)(=N-p-tolyl)Cl2 8. The complex trans-Ti(C-N-C)(=NBu(t))Cl2, 9, was prepared by substitution of the pyridine ligands in Ti(NBu(t))Cl2(py)3 by C-N-C.

New Technique for Speciation of Uranium in Sediments Following Acetate-Stimulated Bioremediation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

2011-06-22

Acetate-stimulated bioremediation is a promising new technique for sequestering toxic uranium contamination from groundwater. The speciation of uranium in sediments after such bioremediation attempts remains unknown as a result of low uranium concentration, and is important to analyzing the stability of sequestered uranium. A new technique was developed for investigating the oxidation state and local molecular structure of uranium from field site sediments using X-Ray Absorption Spectroscopy (XAS), and was implemented at the site of a former uranium mill in Rifle, CO. Glass columns filled with bioactive Rifle sediments were deployed in wells in the contaminated Rifle aquifer and amendedmore » with a hexavalent uranium (U(VI)) stock solution to increase uranium concentration while maintaining field conditions. This sediment was harvested and XAS was utilized to analyze the oxidation state and local molecular structure of the uranium in sediment samples. Extended X-Ray Absorption Fine Structure (EXAFS) data was collected and compared to known uranium spectra to determine the local molecular structure of the uranium in the sediment. Fitting was used to determine that the field site sediments did not contain uraninite (UO{sub 2}), indicating that models based on bioreduction using pure bacterial cultures are not accurate for bioremediation in the field. Stability tests on the monomeric tetravalent uranium (U(IV)) produced by bioremediation are needed in order to assess the efficacy of acetate-stimulation bioremediation.« less

Experimental studies of thermal and chemical interactions between oxide and silicide nuclear fuels with water

DOE Office of Scientific and Technical Information (OSTI.GOV)

farahani, A.A.; Corradini, M.L.

Given some transient power/cooling mismatch is a nuclear reactor and its inability to establish the necessary core cooling, energetic fuel-coolant interactions (FCI`s commonly called `vapor explosions`) could occur as a result of the core melting and coolant contact. Although a large number of studies have been done on energetic FCI`s, very few experiments have been performed with the actual fuel materials postulated to be produced in severe accidents. Because of the scarcity of well-characterized FCI data for uranium allows in noncommercial reactors (cermet and silicide fuels), we have conducted a series of experiments to provide a data base for themore » foregoing materials. An existing 1-D shock-tube facility was modified to handle depleted radioactive materials (U{sub 3}O{sub 8}-Al, and U{sub 3}Si{sub 2}-Al). Our objectives have been to determine the effects of the initial fuel composition and temperature and the driving pressure (triggering) on the explosion work output, dynamic pressures, transient temperatures, and the hydrogen production. Experimental results indicate limited energetics, mainly thermal interactions, for these fuel materials as compared to aluminum where more chemical reactions occur between the molten aluminum and water.« less

A novel sequential process for remediating rare-earth wastewater.

PubMed

Cui, Mingcan; Jang, Min; Kang, Kyounglim; Kim, Dukmin; Snyder, Shane A; Khim, Jeehyeong

2016-02-01

A novel and economic sequential process consisting of precipitation, adsorption, and oxidation was developed to remediate actual rare-earth (RE) wastewater containing various toxic pollutants, including radioactive species. In the precipitation step, porous air stones (PAS) containing waste oyster shell (WOS), PASWOS, was prepared and used to precipitate most heavy metals with >97% removal efficiencies. The SEM-EDS analysis revealed that PAS plays a key role in preventing the surface coating of precipitants on the surface of WOS and in releasing the dissolved species of WOS successively. For the adsorption step, a polyurethane (PU) impregnated by coal mine drainage sludge (CMDS), PUCMDS, was synthesized and applied to deplete fluoride (F), arsenic (As), uranium (U), and thorium (Th) that remained after precipitation. The continuous-mode sequential process using PAS(WOS), PU(CMDS), and ozone (O3) had 99.9-100% removal efficiencies of heavy metals, 99.3-99.9% of F and As, 95.8-99.4% of U and Th, and 92.4% of COD(Cr) for 100 days. The sequential process can treat RE wastewater economically and effectively without stirred-tank reactors, pH controller, continuous injection of chemicals, and significant sludge generation, as well as the quality of the outlet met the EPA recommended limits. Copyright © 2015 Elsevier Ltd. All rights reserved.

Réduction des nitrates et de l'uranium par les bactéries indigènes

NASA Astrophysics Data System (ADS)

Abdelouas, Abdesselam; Lutze, Werner; Nuttall, Eric

1998-07-01

A bioremediation concept has been developed to clean up ground water contaminated with nitrate (1200 mg·L -1) and uranium (0.25 mg·L -1). We studied the Tuba City mill tailings site, Arizona, USA. Indigenous bacteria capable of catalyzing the reduction of NO 3- and U(VI) were identified in the ground water and in the host rock, the Navajo sandstone. After complete reduction of O 2 and NO 3- within one week, U(VI) was reduced and precipitated as uraninite. Final uranium concentrations < 15 μg·L -1 were reached after a few weeks at 24 °C. Iron sulfide also precipitated as a result of reduction of Fe(III) on the sand surface and sulfate in the ground water. U(VI) was not reduced by sulfide. It was found that enzymatic reduction of U(VI) is faster than abiotic reduction under the conditions given by the composition of the ground water.

The Effect of Si and Al Concentration Ratios on the Removal of U(VI) under Hanford Site 200 Area Conditions-12115

DOE Office of Scientific and Technical Information (OSTI.GOV)

Katsenovich, Yelena; Gonzalez, Nathan; Moreno-Pastor, Carol

2012-07-01

Injection of reactive gases, such as NH{sub 3}, is an innovative technique to mitigate uranium contamination in soil for a vadose zone (VZ) contaminated with radionuclides. A series of experiments were conducted to examine the effect of the concentration ratio of silicon to aluminum in the presence of various bicarbonate concentrations on the coprecipitation process of U(VI). The concentration of Al in all tests remained unchanged at 2.8 mM. Experiments showed that the removal efficiency of uranium was not significantly affected by the different bicarbonate and U(VI) concentrations tested. For the lower Si:Al molar ratios of 2:1 and 18:1, themore » removal efficiency of uranium was relatively low (≤ 8%). For the Si:Al molar ratio of 35:1, the removal efficiency of uranium was increased to an average of ∼82% for all bicarbonate concentrations tested. At higher Si:Al molar ratios (53:1 and above), a relatively high removal efficiency of U(VI), approximately 85% and higher, was observed. These results demonstrate that the U(VI) removal efficiency is more affected by the Si:Al molar ratio than by the bicarbonate concentration in solution. The results of this experiment are promising for the potential implementation of NH{sub 3} gas injection for the remediation of U(VI) -contaminated VZ. (authors)« less

Carnotite resources of the Spud Patch area, San Miguel County, Colorado

USGS Publications Warehouse

Bell, Henry

1953-01-01

The Spud Patch area comprises about 8 square in T. 43 M., R. 18 and 19 W., San Miguel County, Colo., and is about 4 miles northeast of Egnar, Colo. Claims of the United States Vanadium Co. and the Vanadium Corp. of America cover about half the area. Claims of other owners, public land, and patented agricultural land, comprise the remainder of the area. The area is about 38 miles from the Government mill at Montecello, Utah, and 55 miles from the Vanadium Corp. of America mill at Naturita, Colo.Between 1940 and 1951, the Spud Patch area yielded about 24,000 short tons of carnotite ore that probably averaged 0.21 percent U3O8 and 2.2 percent V2O5.The deposits are in a broad sandstone lens near the top of the Salt Wash member of the Jurassic Morrison formation. Although the deposits mined have been mainly impregnations of sandstone by carnotite and gray vanadium-bearing clay minerals, some of the richer deposits found by Geological Survey drilling have a finely disseminated black uranium mineral but no carnotite. The deposits commonly are thin irregular tabular layers, which locally thicken to form elongate masses called "rolls". These rolls have a dominant northeasterly trend. Geologic features found to be most useful as guides to ore are listed.From November 1949 to May 1952, the U.S. Geological Survey drilled 415 diamond-drill holes totaling 67,215 feet in the Spud Patch area. The purpose of this drilling was to find deposits that would make new mines and to appraise the reserves in the unexplored area.As a result of Geological Survey drilling, indicated and inferred reserves computed at the cutoff of 1 foot or more thick and 0.10 percent U3O8 or 1.0 percent V2O5 total 20,500 short tons, averaging 0.28 percent U3O8 and 2.1 percent V2O5. These reserves and those computed at a lower grade cutoff of 0.05 percent U3O8 or 0.50 percent V2O5 and the pounds of contained metal are summarized in table 1.Potential reserves, whose existence is based on geologic evidence alone, are predicted to total about 42,000 short tons, averaging 0.25 percent U3O8 and 2.0 percent V2O5.No additional exploratory-type drilling by the Geological Survey is planned in the Spud Patch area. Recommendations are offered for additional development-type drilling, preferably by claim owners or lessees in specific areas in the vicinity of deposits discovered by Geological Survey drilling.

Highly Efficient Interception and Precipitation of Uranium(VI) from Aqueous Solution by Iron-Electrocoagulation Combined with Cooperative Chelation by Organic Ligands.

PubMed

Li, Peng; Zhun, Bao; Wang, Xuegang; Liao, PingPing; Wang, Guanghui; Wang, Lizhang; Guo, Yadan; Zhang, Weimin

2017-12-19

A new strategy combining iron-electrocoagulation and organic ligands (OGLs) cooperative chelation was proposed to screen and precipitate low concentrations (0-18.52 μmol/L) of uranium contaminant in aqueous solution. We hypothesized that OGLs with amino, hydroxyl, and carboxyl groups hydrophobically/hydrophilically would realize precuring of uranyl ion at pH < 3.0, and the following iron-electrocoagulation would achieve faster and more efficient uranium precipitation. Experimentally, the strategy demonstrated highly efficient uranium(VI) precipitation efficiency, especially with hydrophilic macromolecular OGLs. The uranium removal efficiency at optimized experimental condition reached 99.65%. The decrease of zeta potential and the lattice enwrapping between U-OGLs chelates and flocculation precursor were ascribed to the enhanced uranium precipitation activity. Uranium was precipitated as oxides of U(VI) or higher valences that were easily captured in aggregated micelles under low operation current potential. The actual uranium tailing wastewater was treated, and a satisfied uranium removal efficiency of 99.02% was discovered. After elution of the precipitated flocs, a concentrated uranium solution (up to 106.52 μmol/L) with very few other metallic impurities was obtained. Therefore, the proposed strategy could remove uranium and concentrate it concurrently. This work could provide new insights into the purification and recovery of uranium from aqueous solutions in a cost-effective and environmentally friendly process.

Tris(phosphinoamide)-supported uranium-cobalt heterobimetallic complexes featuring Co → U dative interactions.

PubMed

Napoline, J Wesley; Kraft, Steven J; Matson, Ellen M; Fanwick, Phillip E; Bart, Suzanne C; Thomas, Christine M

2013-10-21

A series of tris- and tetrakis(phosphinoamide) U/Co complexes has been synthesized. The uranium precursors, (η(2)-Ph2PN(i)Pr)4U (1), (η(2)-(i)Pr2PNMes)4U (2), (η(2)-Ph2PN(i)Pr)3UCl (3), and (η(2)-(i)Pr2PNMes)3UI (4), were easily accessed via addition of the appropriate stoichiometric equivalents of [Ph2PN(i)Pr]K or [(i)Pr2PNMes]K to UCl4 or UI4(dioxane)2. Although the phosphinoamide ligands in 1 and 4 have been shown to coordinate to U in an η(2)-fashion in the solid state, the phosphines are sufficiently labile in solution to coordinate cobalt upon addition of CoI2, generating the heterobimetallic Co/U complexes ICo(Ph2PN(i)Pr)3U[η(2)-Ph2PN(i)Pr] (5), ICo((i)Pr2PNMes)3U[η(2)-((i)Pr2PNMes)] (6), ICo(Ph2PN(i)Pr)3UI (7), and ICo((i)Pr2PNMes)3UI (8). Structural characterization of complexes 5 and 7 reveals reasonably short Co-U interatomic distances, with 7 exhibiting the shortest transition metal-uranium distance ever reported (2.874(3) Å). Complexes 7 and 8 were studied by cyclic voltammetry to examine the influence of the metal-metal interaction on the redox properties compared with both monometallic Co and heterobimetallic Co/Zr complexes. Theoretical studies are used to further elucidate the nature of the transition metal-actinide interaction.

Composition, stability, and measurement of reduced uranium phases for groundwater bioremediation at Old Rifle, CO

DOE Office of Scientific and Technical Information (OSTI.GOV)

Campbell, K. M.; Davis, J. A.; Bargar, J.

2011-10-15

Reductive biostimulation is currently being explored as a possible remediation strategy for uranium (U) contaminated groundwater, and is currently being investigated at a field site in Rifle, CO, USA. The long-term stability of the resulting U(IV) phases is a key component of the overall performance and depends upon a variety of factors, including rate and mechanism of reduction, mineral associations in the subsurface, and propensity for oxidation. To address these factors, several approaches were used to evaluate the redox sensitivity of U: measurement of the rate of oxidative dissolution of biogenic uraninite (UO{sub 2(s)}) deployed in groundwater at Rifle, characterizationmore » of a zone of natural bioreduction exhibiting relevant reduced mineral phases, and laboratory studies of the oxidative capacity of Fe(III) and reductive capacity of Fe(II) with regard to U(IV) and U(VI), respectively.« less

Radical anionic versus neutral 2,2'-bipyridyl coordination in uranium complexes supported by amide and ketimide ligands.

PubMed

Diaconescu, Paula L; Cummins, Christopher C

2015-02-14

The synthesis and characterization of (bipy)(2)U(N[t-Bu]Ar)(2) (1-(bipy)(2), bipy = 2,2'-bipyridyl, Ar = 3,5-C(6)H(3)Me(2)), (bipy)U(N[(1)Ad]Ar)(3) (2-bipy), (bipy)(2)U(NC[t-Bu]Mes)(3) (3-(bipy)(2), Mes = 2,4,6-C(6)H(2)Me(3)), and IU(bipy)(NC[t-Bu]Mes)(3) (3-I-bipy) are reported. X-ray crystallography studies indicate that bipy coordinates as a radical anion in 1-(bipy)(2) and 2-bipy, and as a neutral ligand in 3-I-bipy. In 3-(bipy)(2), one of the bipy ligands is best viewed as a radical anion, the other as a neutral ligand. The electronic structure assignments are supported by NMR spectroscopy studies of exchange experiments with 4,4'-dimethyl-2,2'-bipyridyl and also by optical spectroscopy. In all complexes, uranium was assigned a +4 formal oxidation state.

Synthesis of functional materials in combustion reactions

NASA Astrophysics Data System (ADS)

Zhuravlev, V. D.; Bamburov, V. G.; Ermakova, L. V.; Lobachevskaya, N. I.

2015-12-01

The conditions for obtaining oxide compounds in combustion reactions of nitrates of metals with organic chelating-reducing agents such as amino acids, urea, and polyvinyl alcohol are reviewed. Changing the nature of internal fuels and the reducing agent-to-oxidizing agent ratio makes possible to modify the thermal regime of the process, fractal dimensionality, morphology, and dispersion of synthesized functional materials. This method can be used to synthesize simple and complex oxides, composites, and metal powders, as well as ceramics and coatings. The possibilities of synthesis in combustion reactions are illustrated by examples of αand γ-Al2O3, YSZ composites, uranium oxides, nickel powder, NiO and NiO: YSZ composite, TiO2, and manganites, cobaltites, and aluminates of rare earth elements.

Removal of Radioactive Materials from Groundwater Using Porous Iron Composite Media

NASA Astrophysics Data System (ADS)

Dorward, E.; Thomas, R.; Cochran, J. P.; Chang, H. S.; Tandukar, M.; Coutelot, F.; Seaman, J. C.

2017-12-01

Uranium (U) is a concern in aqueous environments because of its toxicity. Reducing the mobile U(VI) to the relatively immobile U(IV) can decrease soluble U concentrations. Zero valent iron (ZVI) has been demonstrated as an effective reducing agent for U(VI) as well as other frequently occurring co-contaminants, such as nitrate (NO3-). However, the ability of ZVI to chemically reduce and immobilize U and other associated contaminants in more complex systems containing many alternate electron acceptors and non-ideal chemical conditions remains a concern. Porous iron composite (PIC) materials were evaluated for their ability to address these concerns in both batch and column experiments. We created an artificial groundwater surrogate containing ≈ 100 mg L-1 NO3-, 200 mg L-1 alkalinity, 100 µg L-1 U(VI) as uranyl (UO2+2), 100 µg L-1 rhenium (Re) as perrhenate (ReO4-), and 50 µg L-1 arsenic (As). In batch, we reacted 5 grams of PIC material with 200 mL groundwater surrogate under two different atmospheric conditions to evaluate the impact of O2. At specific time intervals, 5 mL aliquots from each batch treatment were removed for chemical analysis (i.e., U, Re, As, Fe, NO3, etc.) and the pH and ORP of the remaining suspension was measured. The PIC was effective at fully reducing NO3- levels over the extended reaction time despite rapid pH increase (> 8) during equilibration. Soluble levels of U and Re, a chemical surrogate for 99Tc, decreased in a similar fashion to NO3- in both the presence and absence of O2. Soluble As levels decreased more rapidly than other contaminants, but remained at ≈ 1 µg L-1. Very little nitrite (NO2-) was detected in the batch tests, with NH4+ levels consistent with the amount of NO3- reduced. Similar rates of immobilization for U, Re, and As were observed in the presence and absence of NO3-. Subsequent leaching tests corresponding to residence times ranging from 120 to 7.5 minutes demonstrated the ability of the PIC to reduce NO3- to NH4+, with no persistence of NO2-. Uranium and As were readily immobilized regardless of flow velocity. A strong kinetic component was observed for Re leaching behavior in the column tests. These results indicate the strong ability of PIC material to reduce U, NO3-, and other species under conditions that frequently inhibit conventional ZVI effectiveness.

Preparation and benchmarking of ANSL-V cross sections for advanced neutron source reactor studies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Arwood, J.W.; Ford, W.E. III; Greene, N.M.

1987-01-01

Validity of selected data from the fine-group neutron library was satisfactorily tested in performance parameter calculations for the BAPL-1, TRX-1, and ZEEP-1 thermal lattice benchmarks. BAPL-2 is an H/sub 2/O moderated, uranium oxide lattice; TRX-1 is an H/sub 2/O moderated, 1.31 weight percent enriched uranium metal lattice; ZEEP-1 is a D/sub 2/O-moderated, natural uranium lattice. 26 refs., 1 tab.

Uranium Isotope Systematic in Saanich Inlet

NASA Astrophysics Data System (ADS)

Amini, M.; Holmden, C.; Francois, R.

2008-12-01

As a redox-sensitive element Uranium has become the focus of stable isotope studies. Based on the nuclear field shift effect [1], U isotope fractionation was predicted as a function of U(IV)-U(VI) exchange reactions with the insoluble reduced U(IV) species being heavier than the soluble oxidized U(VI) species. Recently, variations in 238U/235U were reported in low temperature aqueous and sedimentary environments [2,3] indicating that U deposited in well-oxygenated environments is characterized by light isotopic composition, whereas suboxic and anoxic deposits tend towards a heavy isotopic signature. U isotope fractionation has been hence proposed as a promising new paleo-redox proxy. In order to test the efficacy of U isotope fractionation to record oxidation states in marine systems, we are investigating sediment samples deposited over a range of redox conditions in the seasonally anoxic Saanich Inlet, on the east coast of Vancouver Island. We have also made δ238U measurements for water samples from above and below the redoxcline. The measurements were carried out by MC-ICPMS using 233U/236U-double spike technique. The data are reported as δ238U relative to NBL 112a with a 238U/235U ratio of 137.88 (2sd). External precision is better than 0.10 permil (2sd). Eleven analyses of seawater performed over the course of this work yielded δ238U of -0.41±0.07 permil (2sd). No clear difference in δ238U values has been found, thus far, in water samples collected at 10m (O2~380μM) and 200m (O2~1μM) depths from a single location in the middle of the inlet. The mean of two measurements of the deepwater sample yielded -0.43±0.01 permil (2sd). Two measurements of the shallow water sample yielded a mean value of -0.38±0.03 permil (2sd). The δ238U values for HF-HNO3 digestions of the organic rich sediments, one taken in the middle of the basin (3.11% organic carbon) below seasonally anoxic bottom waters (-0.22±0.01 permil, n=2), and the other taken from the sill (1.29% organic carbon) below well-oxygenated bottom waters (-0.22 permil, n=1) are identical. The δ238U value matches previously reported values for suboxic sediments from the Peru margin [3], but is lighter than organic rich sediments from the Black Sea [3], where the bottom waters are strongly euxinic. The consistency in δ238U vaues between previously investigated suboxic sediment samples [3] and our two sediment samples indicates that the magnitude of the U isotopic fractionation is identical between seawater and sediments deposited under a range of bottom water oxygen conditions from oxygenated to anoxic. However, differences between the U isotope compositions in Saanich Inlet and those from the Black Sea remain to be explained, if U isotope fractionation is be used as a quantitative proxy for paleoredox in ancient oceans. [1] Schauble (2007) GCA 71, 2170- 2189. [2] Stirling et al. (2007) EPSL 264, 208-225. [3] Weyer et al. (2007) GCA 72, 345-399.

Surface spectroscopy studies of the oxidation behavior of uranium

NASA Astrophysics Data System (ADS)

Bloch, J.; Atzmony, U.; Dariel, M. P.; Mintz, M. H.; Shamir, N.

1982-02-01

Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) techniques were utilized to study the oxidation behavior of clean uranium surfaces, at very low pressures of various atmospheres (UHV, H 2, O 2, and CO 2), at room temperature. Both for O 2 and CO 2, a precursor chemisorbed oxygen species has been identified at the very initial stage of the oxidation reaction. This chemisorbed oxygen transforms to the oxide form at a rate which depends on the pressure of the oxidizing atmosphere. Residual gaseous carbon compounds which are present even under UHV conditions result in the simultaneous formation of surface carbide which accompanies the initial stage of oxidation. This carbide however decomposes later as oxidation proceeds. Adventitious hydrocarbon adsorption occurs on the formed oxide layer.

U.S.-Australia Civilian Nuclear Cooperation: Issues for Congress

DTIC Science & Technology

2010-09-30

7 Uranium Mining and Milling ................................................................................................8...cycle begins with mining uranium ore and upgrading it to yellowcake. Because naturally occurring uranium lacks sufficient fissile 235U to make fuel for...enrichment, and finally fabrication into fuel elements. Australia exports its uranium after the mining and milling stage. Commercial enrichment services

Determination of interstitial oxygen atom position in U2N3+xOy by near edge structure study

NASA Astrophysics Data System (ADS)

Jiang, A. K.; Zhao, Y. W.; Long, Z.; Hu, Y.; Wang, X. F.; Yang, R. L.; Bao, H. L.; Zeng, R. G.; Liu, K. Z.

2018-06-01

The determination of interstitial oxygen atom site in U2N3+xOy film could facilitate the understanding of the oxidation mechanism of α-U2N3 and the effect of U2N3+xOy on anti-oxidation. By comparing the similarities and variances between N K edge and O K edge electron energy loss spectra (EELS) for oxidized α-U2N3 and UO2, the present work looks at the local structure of nitrogen and oxygen atoms in U2N3+xOy film, identifying the most possible position of interstitial O atom.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Catalano, Jeffrey G.; Giammar, Daniel E.; Wang, Zheming

Phosphate addition is an in situ remediation approach that may enhance the sequestration of uranium without requiring sustained reducing conditions. However, the geochemical factors that determine the dominant immobilization mechanisms upon phosphate addition are insufficiently understood to design efficient remediation strategies or accurately predict U(VI) transport. The overall objective of our project is to determine the dominant mechanisms of U(VI)-phosphate reactions in subsurface environments. Our research approach seeks to determine the U(VI)-phosphate solid that form in the presence of different groundwater cations, characterize the effects of phosphate on U(VI) adsorption and precipitation on smectite and iron oxide minerals, examples ofmore » two major reactive mineral phases in contaminated sediments, and investigate how phosphate affects U(VI) speciation and fate during water flow through sediments from contaminated sites. The research activities conducted for this project have generated a series of major findings. U(VI) phosphate solids from the autunite mineral family are the sole phases to form during precipitation, with uranyl orthophosphate not occurring despite its predicted greater stability. Calcium phosphates may take up substantial quantities of U(VI) through three different removal processes (adsorption, coprecipitation, and precipitation) but the dominance of each process varies with the pathway of reaction. Phosphate co-adsorbs with U(VI) onto smectite mineral surfaces, forming a mixed uranium-phosphate surface complex over a wide range of conditions. However, this molecular-scale association of uranium and phosphate has not effect on the overall extent of uptake. In contrast, phosphate enhanced U(VI) adsorption to iron oxide minerals at acidic pH conditions but suppresses such adsorption at neutral and alkaline pH, despite forming mixed uranium-phosphate surface complexes during adsorption. Nucleation barriers exist that inhibit U(VI) phosphate solids from precipitating in the presence of smectite and iron oxide minerals as well as sediments from contaminated sites. Phosphate addition enhances retention of U(VI) by sediments from the Rifle, CO and Hanford, WA field research sites, areas containing substantial uranium contamination of groundwater. This enhanced retention is through adsorption processes. Both fast and slow uptake and release behavior is observed, indicating that diffusion of uranium between sediment grains has a substantial effect of U(VI) fate in flowing groundwater systems. This project has revealed the complexity of U(VI)-phosphate reactions in subsurface systems. Distinct chemical processes occur in acidic and alkaline groundwater systems. For the latter, calcium phosphate formation, solution complexation, and competition between phosphate and uranium for adsorption sites may serve to either enhance or inhibit U(VI) removal from groundwater. Under the groundwater conditions present at many contaminated sites in the U.S., phosphate appears to general enhance U(VI) retention and limit transport. However, formation of low-solubility uranium phosphate solids does not occur under field-relevant conditions, despite this being the desired product of phosphate-based remediation approaches. In addition, simple equilibrium approaches fail to well-predict uranium fate in contaminated sediments amended with phosphate, with reactive transport models that include reaction rates and mass transport through occluded domains needed to properly describe the system. Phosphate addition faces challenges to being effective as a stand-alone groundwater treatment approach but would prove beneficial as an add-on to other treatment methods that will further limit uranium migration in the subsurface.« less

Recommended Values of the Thermophysical Properties of Eight Alloys, Major Constituents and Their Oxides

DTIC Science & Technology

1966-01-01

V & 1? MATERIALS 732 e a ja o 8 i 1* •ŗ •3V h Q £ u HO > HS MSB Q »H ELEMENTS...CO e - « « s M u I 2 H t- xti CO in eo N i o 7 o T-S T-1110 ""A ’ityAnonpuoo iBttueqx -•-■-■-- - ■ - ^ H.^’.^" V ...IO CO M i-t •O COCS O tr- lO CON I s e IO 05 w O Ü o Ü I g E 1_5I ,_uio JJBM ’AiAnonpuoo iBrajaqi i V

The interaction of molecular hydrogen with α-radiolytic oxidants on a (U,Pu)O2 surface

NASA Astrophysics Data System (ADS)

Bauhn, Lovisa; Hansson, Niklas; Ekberg, Christian; Fors, Patrik; Delville, Rémi; Spahiu, Kastriot

2018-07-01

In order to assess the impact of α-radiolysis of water on the oxidative dissolution of spent fuel, an un-irradiated, annealed MOX fuel pellet with high content of Pu (∼24 wt%), and a specific α-activity of 4.96 GBq/gMOX, was leached in carbonate-containing solutions of low ionic strength. The high Pu content in the pellet stabilizes the (U,Pu)O2(s) matrix towards oxidative dissolution, whereas the α-decays emitted from the surface are expected to produce ∼3.6 × 10-7 mol H2O2/day, contributing to the oxidative dissolution of the pellet. Two sets of leaching tests were conducted under different redox conditions: Ar gas atmosphere and deuterium gas atmosphere. A relatively slow increase of the U and Pu concentrations was observed in the Ar case, with U concentrations increasing from 1·10-6 M after 1 h to ∼7 × 10-5 M after 58 days. Leaching under an atmosphere starting at 1 MPa deuterium gas was undertaken in order to evaluate any effect of dissolved hydrogen on the radiolytic dissolution of the pellet, as well as to investigate any potential recombination of the α-radiolytic products with dissolved deuterium. For the latter purpose, isotopic analysis of the D/H content was carried out on solution samples taken during the leaching. Despite the continuous production of radiolytic oxidants, the concentrations of U and Pu remained quite constant at the level of ∼3 × 10-8 M during the first 30 days, i.e. as long as the deuterium pressure remained higher than 0.8 MPa. These data rule out any oxidative dissolution of the pellet during the first month. The un-irradiated MOX fuel does not contain metallic ε-particles, hence it is mainly the interaction of radiolytic oxidants and dissolved deuterium with the surface of the mixed actinide oxide that causes the neutralization of the oxidants. This conclusion is supported by the steadily increasing levels of HDO measured in the leachate samples.

Bioreduction of U(VI)-Phthalate to a Polymeric U(IV)-Phthalate Colloid

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vazquez, G.; Dodge, C; Francis, A

2009-01-01

Phthalic acid, a ubiquitous organic ligand, formed soluble mono- and biligand complexes with a uranyl ion that was then reduced to a U(IV)-phthalate by a Clostridium species under anaerobic conditions. We confirmed the reduction of the hexavalent uranium to the tetravalent oxidation state by UV-vis absorption and X-ray absorption near edge structure spectroscopy. Sequential micro- and ultrafiltration of the solution revealed that the bioreduced uranium was present as a colloid with particles between 0.03 and 0.45 {mu}m. Analysis with extended X-ray absorption fine structure revealed the association of the reduced uranium with the phthalic acid as a repeating biligand 1:2more » U(IV):phthalic acid polymer. This is the first report of the formation of a U(IV) complexed to two phthalic acid molecules in the form of a polymeric colloid. Although it was proposed that the bioreduction and the precipitation of uranium might be an invaluable strategy to immobilize uranium in contaminated environments, our results suggest that the organic ligands present there might hinder the precipitation of the bioreduced uranium under anaerobic conditions and, thereby, enhance its environmental mobility as uranium organic complexes or colloids.« less

Subsurface Nitrogen-Cycling Microbial Communities at Uranium Contaminated Sites in the Colorado River Basin

NASA Astrophysics Data System (ADS)

Cardarelli, E.; Bargar, J.; Williams, K. H.; Dam, W. L.; Francis, C.

2015-12-01

Throughout the Colorado River Basin (CRB), uranium (U) persists as a relic contaminant of former ore processing activities. Elevated solid-phase U levels exist in fine-grained, naturally-reduced zone (NRZ) sediments intermittently found within the subsurface floodplain alluvium of the following Department of Energy-Legacy Management sites: Rifle, CO; Naturita, CO; and Grand Junction, CO. Coupled with groundwater fluctuations that alter the subsurface redox conditions, previous evidence from Rifle, CO suggests this resupply of U may be controlled by microbially-produced nitrite and nitrate. Nitrification, the two-step process of archaeal and bacterial ammonia-oxidation followed by bacterial nitrite oxidation, generates nitrate under oxic conditions. Our hypothesis is that when elevated groundwater levels recede and the subsurface system becomes anoxic, the nitrate diffuses into the reduced interiors of the NRZ and stimulates denitrification, the stepwise anaerobic reduction of nitrate/nitrite to dinitrogen gas. Denitrification may then be coupled to the oxidation of sediment-bound U(IV) forming mobile U(VI), allowing it to resupply U into local groundwater supplies. A key step in substantiating this hypothesis is to demonstrate the presence of nitrogen-cycling organisms in U-contaminated, NRZ sediments from the upper CRB. Here we investigate how the diversity and abundances of nitrifying and denitrifying microbial populations change throughout the NRZs of the subsurface by using functional gene markers for ammonia-oxidation (amoA, encoding the α-subunit of ammonia monooxygenase) and denitrification (nirK, nirS, encoding nitrite reductase). Microbial diversity has been assessed via clone libraries, while abundances have been determined through quantitative polymerase chain reaction (qPCR), elucidating how relative numbers of nitrifiers (amoA) and denitrifiers (nirK, nirS) vary with depth, vary with location, and relate to uranium release within NRZs in sediment cores spanning the upper CRB. Early findings from Rifle, CO indicate elevated abundances of ammonia-oxidizers seem to correlate with elevated uranium concentrations emphasizing the critical need to understand how nitrogen-cycling organisms influence subsurface U redox chemistry and mobility.

Neutronic performance of high-density LEU fuels in water-moderated and water-reflected research reactors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bretscher, M.M.; Matos, J.E.

At the Reduced Enrichment for Research and Test Reactors (RERTR) meeting in September 1994, Durand reported that the maximum uranium loading attainable with U{sub 3}Si{sub 2} fuel is about 6.0 g U/cm{sup 3}. The French Commissariat a l`Energie Atomique (CEA) plan to perform irradiation tests with 5 plates at this loading. Compagnie pour L`Etude et La Realisation de Combustibles Atomiques (CERCA) has also fabricated a few uranium nitride (UN) plates with a uranium density in the fuel meat of 7.0 g/cm{sup 3} and found that UN is compatible with the aluminum matrix at temperatures below 500 C. High density dispersionmore » fuels proposed for development include U-Zr(4 wt%)-Nb(2 wt%), U-Mo(5 wt%), and U-Mo(9 wt%). The purpose of this note is to examine the relative neutronic behavior of these high density fuels in a typical light water-reflected and water-moderated MTR-type research reactor. The results show that a dispersion of the U-Zr-Nb alloy has the most favorable neutronic properties and offers the potential for uranium densities greater than 8.0 g/cm{sup 3}. On the other hand, UN is the least reactive fuel because of the relatively large {sup 14}N(n,p) cross section. For a fixed value of k{sub eff}, the required {sup 235}U loading per fuel element is least for the U-Zr-Nb fuel and steadily increases for the U-Mo(5%), U-Mo(9%), and UN fuels. Because of volume fraction limitations, the UO{sub 2} dispersions are only useful for uranium densities below 5.0 g/cm{sup 3}. In this density range, however, UO{sub 2} is more reactive than U{sub 3}Si{sub 2}.« less

234U/238U as a ground-water tracer, SW Nevada-SE California

USGS Publications Warehouse

Ludwig, K. R.; Peterman, Z.E.; Simmons, K.R.; Gutentag, E.D.

1993-01-01

The 234U/238U ratio of uranium in oxidizing ground waters is potentially an excellent ground-water tracer because of its high solubility and insensitivity to chemical reactions. Moreover, recent advances in analytical capability have made possible very precise uranium-isotopic analyses on modest (approx.100 ml) amounts of normal ground water. Preliminary results on waters from SW Nevada/Se California indicate two main mixing trends, but in detail indicate significant complexity requiring three or more main components.

The Earth's Thorium and Uranium Abundance and Distribution

NASA Astrophysics Data System (ADS)

McDonough, W. F.; Guo, M.; Wipperfurth, S. A.

2017-12-01

The abundance and distribution of thorium (Th) and uranium (U) and its Th/U value have been assessed for the bulk silicate Earth (BSE), core, modern mantle and continental crust. These heat producing elements power the Earth's engine and are recorders of atmospheric oxidation and biologically mediated processes. More than 50,000 measured Th/U values (Kappa) and a couple of thousand Kappa-Pb values, the time-integrated Pb isotopic values from the decay of Th and U, are evaluated for the BSE, continental crust (CC) and modern mantle (MM), with the latter represented by mid-ocean ridge basalts (MORB) and ocean island basalt (OIB). The Kappa-Pb values for these complementary enriched and depleted domains of the BSE (i.e., CC_Kappa-Pb = 4.1 +/- 0.2 and MM_Kappa-Pb = 3.8 +/- 0.1, respectively) narrowly bracket the solar system initial (SSi_Kappa-Pb = 3.88 +/- 0.02) with an uncertainty of +/-5%) and demonstrate that negligible Th/U fractionation accompanied accretion, core formation, and crust - mantle differentiation. Experimental studies find marked differences in the partitioning of U and Th during core formation and thus, the BSE_Kappa-Pb = of 3.9 +/- 0.2 dictates that Th and U were excluded from the core. The <4% differences between the CC_Kappa-Pb and MM_Kappa-Pb reveals that U6+ recycling back into the mantle has either been a relatively recent process or that its recycling following atmospheric oxygenation at 2.4 Ga was limited and evolved slowly with time. Recent data from geoneutrino flux measurements at KamLAND observes a Th/U of 4.1 (+5.5, -3.3); although these uncertainties are large, future experiments, with annual count rates that are 10 to 40 times greater than that at KamLAND, will provide greater statistics, a critical measure of the planetary Th/U ratio, and an assessment of the assumption of chondritic ratio for the Earth.

XPS studies of UO 2 oxidation by alpha radiolysis of water at 100°C

NASA Astrophysics Data System (ADS)

Sunder, S.; Boyer, G. D.; Miller, N. H.

1990-12-01

The effect of alpha radiolysis of water on the oxidation and dissolution of UO 2 was studied at 100°C as a function of alpha-field strength and water chemistry using X-ray photoelectron spectroscopy. In N 2-purged solutions the oxidation of UO 2 increases with the strength of the alpha flux; an alpha flux greater than or equal to that from a 250-μ Ci americium-241 source leads to oxidation of UO 2 beyond the UO 2.33 (U 3O 7) stage, and an alpha flux equal to that from a 5-μ Ci source does not result in UO 2 oxidation beyond the UO 2.33 stage. The presence of dissolved H 2 in water, at a concentration ≥ 1.6 × 10 -4moldm-3, reduces the oxidation and dissolution of UO 2 due to alpha radiolysis at temperatures ≥ 100° C. It is concluded that the radiolysis of groundwater at ~ 100°C, due to the alpha flux associated with used CANDU fuel, is unlikely to make a significant contribution to its oxidative dissolution in the geological disposal vault planned in the Canadian Nuclear Fuel Waste Management Program. CANada Deuterium Uranium. Registered trademark.

The geometric structures, vibrational frequencies and redox properties of the actinyl coordination complexes ([AnO2(L)n](m); An = U, Pu, Np; L = H2O, Cl-, CO3(2-), CH3CO2(-), OH-) in aqueous solution, studied by density functional theory methods.

PubMed

Austin, Jonathan P; Sundararajan, Mahesh; Vincent, Mark A; Hillier, Ian H

2009-08-14

The geometric and electronic structures of the aqua, chloro, acetato, hydroxo and carbonato complexes of U, Np and Pu in both their (VI) and (V) oxidation states, and in an aqueous environment, have been studied using density functional theory methods. We have obtained micro-solvated structures derived from molecular dynamics simulations and included the bulk solvent using a continuum model. We find that two different hydrogen bonding patterns involving the axial actinyl oxygen atoms are sometimes possible, and may give rise to different An-O bond lengths and vibrational frequencies. These alternative structures are reflected in the experimental An-O bond lengths of the aqua and carbonato complexes. The variation of the redox potential of the uranyl complexes with the different ligands has been studied using both BP86 and B3LYP functionals. The relative values for the four uranium complexes having anionic ligands are in surprisingly good agreement with experiment, although the absolute values are in error by approximately 1 eV. The absolute error for the aqua species is much less, leading to an incorrect order of the redox potentials of the aqua and chloro species.

Fractionation of Oxygen Isotopes by Thermal Ionization Mass Spectrometry Inferred from Simultaneous Measurement of (17)O/(16)O and (18)O/(16)O Ratios and Implications for the (182)Hf-(182)W Systematics.

PubMed

Trinquier, Anne

2016-06-07

Accurate (182)Hf-(182)W chronology of early planetary differentiation relies on highly precise and accurate tungsten isotope measurements. WO3(-) analysis by negative thermal ionization mass spectrometry requires W(17)O(16)O2(-), W(17)O2(16)O(-), W(18)O(16)O2(-), W(17)O3(-), W(17)O(18)O(16)O(-), and W(18)O2(16)O(-) isotopologue interference corrections on W(16)O3(-) species ( Harper et al. Geochim. Cosmochim. Acta 1996 , 60 , 1131 ; Quitté et al. Geostandard. Newslett. 2002 , 26 , 149 ; Trinquier et al. Anal. Chem. 2016 , 88 , 1542 ; Touboul et al. Nature 2015 , 520 , 530 ; Touboul et al. Int. J. Mass Spectrom. 2012 , 309 , 109 ). In addition, low ion beam intensity counting statistics combined with Faraday cup detection noise limit the precision on the determination of (18)O/(16)O and (17)O/(16)O relative abundances. Mass dependent variability of (18)O/(16)O over the course of an analysis and between different analyses calls for oxide interference correction on a per integration basis, based on the in-run monitoring of the (18)O/(16)O ratio ( Harper et al. Geochim. Cosmochim. Acta 1996 , 60 , 1131 ; Quitté et al. Geostandard. Newslett. 2002 , 26 , 149 ; Trinquier et al. Anal. Chem. 2016 , 88 , 1542 ). Yet, the (17)O/(16)O variation is normally not being monitored and, instead, inferred from the measured (18)O/(16)O variation, assuming a δ(17)O-δ(18)O Terrestrial Fractionation Line ( Trinquier et al. Anal. Chem. 2016 , 88 , 1542 ). The purpose of the present study is to verify the validity of this assumption. Using high resistivity amplifiers, (238)U(17)O2 and (238)U(18)O2 ion beams down to 1.6 fA have been monitored simultaneously with (235,238)U(16)O2 species in a uranium certified reference material. This leads to a characterization of O isotope fractionation by thermal ionization mass spectrometry in variable loading and running conditions (additive-to-sample ratio, PO2 pressure, presence of ionized metal and oxide species). Proper determination of O isotope composition based on the simultaneous analysis of the (18)O/(16)O and (17)O/(16)O ratios could prevent tens of ppm bias or more on the (182)W/(184)W and (183)W/(184)W ratios.

Margaritasite: a new mineral of hydrothermal origin from the Pena Blanca uranium district, Mexico.

USGS Publications Warehouse

Wenrich, K.J.; Modreski, P.J.; Zielinski, R.A.; Seeley, J.L.

1982-01-01

Margaritasite, (Cs,K,H3O)2(UO2)2V2O8.nH2O (where Cs > K, H3O and n approx 1), a 10.514, b 8.425, c 7.25 A, beta 106.01o, P21/a, Z = 2, is a newly recognized uranium ore mineral named for the Margaritas deposit, Pena Blanca uranium district, Chihuahua, Mexico, at which it was discovered. A Cs-rich analogue of carnotite, margaritasite is the natural equivalent of synthetic Cs-uranyl vanadate (A.M. 43- 799, 50-825). A fine-grained yellow mineral, it is most easily distinguished from carnotite by XRD; X-ray powder patterns (CuKalpha radiation) show that the (001) reflection of margaritasite lies at 12.7o (2theta ), while that of carnotite is found at 13.8o (2theta ). The shift of the (001) reflection in margaritasite reflects the structural changes caused when Cs occupies the sites filled by K in carnotite. Synthesis experiments indicate that margaritasite also differs from carnotite in a higher-T hydrothermal origin. Chemical analyses and XRD data for margaritasite and synthetic Cs- carnotite, and chemical analyses for rocks from Sierra Pena Blanca and vicinity, are tabulated.-J.A.Z.

Unraveling uranium induced oxidative stress related responses in Arabidopsis thaliana seedlings. Part I: responses in the roots.

PubMed

Vanhoudt, Nathalie; Vandenhove, Hildegarde; Horemans, Nele; Remans, Tony; Opdenakker, Kelly; Smeets, Karen; Bello, Daniel Martinez; Wannijn, Jean; Van Hees, May; Vangronsveld, Jaco; Cuypers, Ann

2011-06-01

When aiming to evaluate the environmental impact of uranium contamination, it is important to unravel the mechanisms by which plants respond to uranium stress. As oxidative stress seems an important modulator under other heavy metal stress, this study aimed to investigate oxidative stress related responses in Arabidopsis thaliana exposed to uranium concentrations ranging from 0.1 to 100 μM for 1, 3 and 7 days. Besides analyzing relevant reactive oxygen species-producing and -scavenging enzymes at protein and transcriptional level, the importance of the ascorbate-glutathione cycle under uranium stress was investigated. These results are reported separately for roots and leaves in two papers: Part I dealing with responses in the roots and Part II unraveling responses in the leaves and presenting general conclusions. Results of Part I indicate that oxidative stress related responses in the roots were only triggered following exposure to the highest uranium concentration of 100 μM. A fast oxidative burst was suggested based on the observed enhancement of lipoxygenase (LOX1) and respiratory burst oxydase homolog (RBOHD) transcript levels already after 1 day. The first line of defense was attributed to superoxide dismutase (SOD), also triggered from the first day. The enhanced SOD-capacity observed at protein level corresponded with an enhanced expression of iron SOD (FSD1) located in the plastids. For the detoxification of H(2)O(2), an early increase in catalase (CAT1) transcript levels was observed while peroxidase capacities were enhanced at the later stage of 3 days. Although the ascorbate peroxidase capacity and gene expression (APX1) increased, the ascorbate/dehydroascorbate redox balance was completely disrupted and shifted toward the oxidized form. This disrupted balance could not be inverted by the glutathione part of the cycle although the glutathione redox balance could be maintained. Copyright © 2011 Elsevier Ltd. All rights reserved.

Heat-induced redistribution of surface oxide in uranium

NASA Astrophysics Data System (ADS)

Swissa, Eli; Shamir, Noah; Mintz, Moshe H.; Bloch, Joseph

1990-09-01

The redistribution of oxygen and uranium metal at the vicinity of the metal-oxide interface of native and grown oxides due to vacuum thermal annealing was studied for uranium and uranium-chromium alloy using Auger depth profiling and metallographic techniques. It was found that uranium metal is segregating out through the uranium oxide layer for annealing temperatures above 450°C. At the same time the oxide is redistributed in the metal below the oxide-metal interface in a diffusion like process. By applying a diffusion equation of a finite source, the diffusion coefficients for the process were obtained from the oxygen depth profiles measured for different annealing times. An Arrhenius like behavior was found for the diffusion coefficient between 400 and 800°C. The activation energy obtained was Ea = 15.4 ± 1.9 kcal/mole and the pre-exponential factor, D0 = 1.1 × 10 -8cm2/ s. An internal oxidation mechanism is proposed to explain the results.

Structural study of (N{sub 2}H{sub 5},H){sub 2.9}U{sub 1.1}Ce{sub 0.9}(C{sub 2}O{sub 4}){sub 5}·10H{sub 2}O from a conventional X-ray diffraction diagram obtained on a powder synthesized by a fast vortex process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Brackx, E., E-mail: Emmanuelle.brackx@cea.fr; Laval, J.P.; Dugne, O.

2015-01-15

In the context of research on U/minor actinides for nuclear fuel reprocessing in the transmutation process, developments are first studied with surrogates containing uranium and lanthanides to facilitate testing. The tests consist of precipitating and calcining a hydrazinium uranium/cerium oxalate. The structure of this oxalate had not been previously determined, but was necessary to validate the physicochemical mechanisms involved. The present study, firstly demonstrates the structural similarity of the U/Ce oxalate phase (N{sub 2}H{sub 5},H){sub 2.9}U{sub 1.1}Ce{sub 0.9}(C{sub 2}O{sub 4}){sub 5}·10H{sub 2}O, synthesized using a vortex precipitator for continuous synthesis of actinide oxalates, with previously known oxalates, crystallizing in P6{submore » 3}/mmc symmetry, obtained by more classical methods. This fast precipitation process induces massive nucleation of fine powders. Their structural and microstructural determination confirms that the raw and dried phases belong to the same structural family as (NH{sub 4}){sub 2}U{sub 2}(C{sub 2}O{sub 4}){sub 5}·0.7H{sub 2}O whose structure was described by Chapelet-Arab in P6{sub 3}/mmc symmetry, using single crystal data. However, they present an extended disorder inside the tunnels of the structure, even after drying at 100 °C, between water and hydrazinium ions. This disorder is directly related to the fast vortex method. This structure determination can be used as a basis for further semi-quantitative analysis on the U/minor actinides products formed under various experimental conditions. - Highlights: • Uranium cerium oxalate precipitate characterization by X-ray powder diffraction. • Morphology characterization by SEM analysis. • Structure determination by unit cell Rietveld refinement.« less

Synthesis of functional materials in combustion reactions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhuravlev, V. D., E-mail: zhvd@ihim.uran.ru; Bamburov, V. G.; Ermakova, L. V.

2015-12-15

The conditions for obtaining oxide compounds in combustion reactions of nitrates of metals with organic chelating–reducing agents such as amino acids, urea, and polyvinyl alcohol are reviewed. Changing the nature of internal fuels and the reducing agent-to-oxidizing agent ratio makes possible to modify the thermal regime of the process, fractal dimensionality, morphology, and dispersion of synthesized functional materials. This method can be used to synthesize simple and complex oxides, composites, and metal powders, as well as ceramics and coatings. The possibilities of synthesis in combustion reactions are illustrated by examples of αand γ-Al{sub 2}O{sub 3}, YSZ composites, uranium oxides, nickelmore » powder, NiO and NiO: YSZ composite, TiO{sub 2}, and manganites, cobaltites, and aluminates of rare earth elements.« less

Fretting Wear Damage Mechanism of Uranium under Various Atmosphere and Vacuum Conditions

PubMed Central

Li, Zhengyang; Wu, Yanping; Meng, Xiandong; Zhang, Dongxu

2018-01-01

A fretting wear experiment with uranium has been performed on a linear reciprocating tribometer with ball-on-disk contact. This study focused on the fretting behavior of the uranium under different atmospheres (Ar, Air (21% O2 + 78% N2), and O2) and vacuum conditions (1.05 and 1 × 10−4 Pa). Evolution of friction was assessed by coefficient of friction (COF) and friction-dissipated energy. The oxide of the wear surface was evaluated by Raman spectroscopy. The result shows that fretting wear behavior presents strong atmosphere and vacuum condition dependence. With increasing oxygen content, the COF decreases due to abrasive wear and formation of oxide film. The COF in the oxygen condition is at least 0.335, and it has a maximum wear volume of about 1.48 × 107 μm3. However, the COF in a high vacuum condition is maximum about 1.104, and the wear volume is 1.64 × 106 μm3. The COF in the low vacuum condition is very different: it firstly increased and then decreased rapidly to a steady value. It is caused by slight abrasive wear and the formation of tribofilm after thousands of cycles. PMID:29659484

Compositional changes at the interface between thorium-doped uranium dioxide and zirconium due to high-temperature annealing

NASA Astrophysics Data System (ADS)

Youn, Young-Sang; Lee, Jeongmook; Kim, Jandee; Kim, Jong-Yun

2018-06-01

Compositional changes at the interface between thorium-doped uranium dioxide (U0.97Th0.03O2) and Zr before and after annealing at 1700 °C for 18 h were studied by X-ray photoelectron spectroscopy, X-ray diffraction, and Raman spectroscopy. At room temperature, the U0.97Th0.03O2 pellet consisted of hyperstoichiometric UO2+x with UO2 and ThO2, and the Zr sample contained Zr with ZrO2. After annealing, the former contained stoichiometric UO2 with ThO2 and the latter consisted of ZrO2 along with ZrO2·2H2O.

Uranium levels in the diet of São Paulo City residents.

PubMed

Garcia, F; Barioni, A; Arruda-Neto, J D T; Deppman, A; Milian, F; Mesa, J; Rodriguez, O

2006-07-01

Natural levels of uranium in the diet of São Paulo City residents were studied, and radionuclide concentrations were measured by the fission track method on samples of typical adult food items. This information was used to evaluate the daily intake of uranium in individuals living in São Paulo City which is, according to our findings, around 0.97 microg U/day. Using the ICRP Uranium-model, we estimated the uranium accumulation and committed doses in some tissues and organs, as function of time. We compared the output of the ICRP uranium biokinetic model, tailored for the conditions prevailing in São Paulo, with experimental data from other localities. Such comparison was possible by means of a simple method we developed, which allows normalization among experimental results from different regions where distinct values of chronic daily intake are observed.

Potential aquifer vulnerability in regions down-gradient from uranium in situ recovery (ISR) sites.

PubMed

Saunders, James A; Pivetz, Bruce E; Voorhies, Nathan; Wilkin, Richard T

2016-12-01

Sandstone-hosted roll-front uranium ore deposits originate when U(VI) dissolved in groundwater is reduced and precipitated as insoluble U(IV) minerals. Groundwater redox geochemistry, aqueous complexation, and solute migration are important in leaching uranium from source rocks and transporting it in low concentrations to a chemical redox interface where it is deposited in an ore zone typically containing the uranium minerals uraninite, pitchblende, and/or coffinite; various iron sulfides; native selenium; clays; and calcite. In situ recovery (ISR) of uranium ores is a process of contacting the uranium mineral deposit with leaching and oxidizing (lixiviant) fluids via injection of the lixiviant into wells drilled into the subsurface aquifer that hosts uranium ore, while other extraction wells pump the dissolved uranium after dissolution of the uranium minerals. Environmental concerns during and after ISR include water quality degradation from: 1) potential excursions of leaching solutions away from the injection zone into down-gradient, underlying, or overlying aquifers; 2) potential migration of uranium and its decay products (e.g., Ra, Rn, Pb); and, 3) potential mobilization and migration of redox-sensitive trace metals (e.g., Fe, Mn, Mo, Se, V), metalloids (e.g., As), and anions (e.g., sulfate). This review describes the geochemical processes that control roll-front uranium transport and fate in groundwater systems, identifies potential aquifer vulnerabilities to ISR operations, identifies data gaps in mitigating these vulnerabilities, and discusses the hydrogeological characterization involved in developing a monitoring program. Published by Elsevier Ltd.

Optimization of ISOCS Parameters for Quantitative Non-Destructive Analysis of Uranium in Bulk Form

NASA Astrophysics Data System (ADS)

Kutniy, D.; Vanzha, S.; Mikhaylov, V.; Belkin, F.

2011-12-01

Quantitative calculation of the isotopic masses of fissionable U and Pu is important for forensic analysis of nuclear materials. γ-spectrometry is the most commonly applied tool for qualitative detection and analysis of key radionuclides in nuclear materials. Relative isotopic measurement of U and Pu may be obtained from γ-spectra through application of special software such as MGAU (Multi-Group Analysis for Uranium, LLNL) or FRAM (Fixed-Energy Response Function Analysis with Multiple Efficiency, LANL). If the concentration of U/Pu in the matrix is unknown, however, isotopic masses cannot be calculated. At present, active neutron interrogation is the only practical alternative for non-destructive quantification of fissionable isotopes of U and Pu. An active well coincidence counter (AWCC), an alternative for analyses of uranium materials, has the following disadvantages: 1) The detection of small quantities (≤100 g) of 235U is not possible in many models; 2) Representative standards that capture the geometry, density and chemical composition of the analyzed unknown are required for precise analysis; and 3) Specimen size is severely restricted by the size of the measuring chamber. These problems may be addressed using modified γ-spectrometry techniques based on a coaxial HPGe-detector and ISOCS software (In Situ Object Counting System software, Canberra). We present data testing a new gamma-spectrometry method uniting actinide detection with commonly utilized software, modified for application in determining the masses of the fissionable isotopes in unknown samples of nuclear materials. The ISOCS software, widely used in radiation monitoring, calculates the detector efficiency curve in a specified geometry and range of photon energies. In describing the geometry of the source-detector, it is necessary to clearly describe the distance between the source and the detector, the material and the thickness of the walls of the container, as well as material, density and chemical composition of the matrix of the specimen. Obviously, not all parameters can be characterized when measuring samples of unknown composition or uranium in bulk form. Because of this, and especially for uranium materials, the IAEA developed an ISOCS optimization procedure. The target values for the optimization are Μmatrixfixed, the matrix mass determined by weighing with a known mass container, and Εfixed, the 235U enrichment, determined by MGAU. Target values are fitted by varying the matrix density (ρ), and the concentration of uranium in the matrix of the unknown (w). For each (ρi, wi), an efficiency curve is generated, and the masses of uranium isotopes, Μ235Ui and Μ238Ui, determined using spectral activity data and known specific activities for U. Finally, fitted parameters are obtained for Μmatrixi = Μmatrixfixed ± 1σ, Εi = Εfixed ± 1σ, as well as important parameters (ρi, wi, Μ235Ui, Μ238Ui, ΜUi). We examined multiple forms of uranium (powdered, pressed, and scrap UO2 and U3O8) to test this method for its utility in accurately identifying the mass and enrichment of uranium materials, and will present the results of this research.

Electron transfer at the cell-uranium interface in Geobacter spp.

PubMed

Reguera, Gemma

2012-12-01

The in situ stimulation of Fe(III) oxide reduction in the subsurface stimulates the growth of Geobacter spp. and the precipitation of U(VI) from groundwater. As with Fe(III) oxide reduction, the reduction of uranium by Geobacter spp. requires the expression of their conductive pili. The pili bind the soluble uranium and catalyse its extracellular reductive precipitation along the pili filaments as a mononuclear U(IV) complexed by carbon-containing ligands. Although most of the uranium is immobilized by the pili, some uranium deposits are also observed in discreet regions of the outer membrane, consistent with the participation of redox-active foci, presumably c-type cytochromes, in the extracellular reduction of uranium. It is unlikely that cytochromes released from the outer membrane could associate with the pili and contribute to the catalysis, because scanning tunnelling microscopy spectroscopy did not reveal any haem-specific electronic features in the pili, but, rather, showed topographic and electronic features intrinsic to the pilus shaft. Pili not only enhance the rate and extent of uranium reduction per cell, but also prevent the uranium from traversing the outer membrane and mineralizing the cell envelope. As a result, pili expression preserves the essential respiratory activities of the cell envelope and the cell's viability. Hence the results support a model in which the conductive pili function as the primary mechanism for the reduction of uranium and cellular protection in Geobacter spp.

The geochemistry of water near a surficial organic-rich uranium deposit, northeastern Washington State, U.S.A.

USGS Publications Warehouse

Zielinski, R.A.; Otton, J.K.; Wanty, R.B.; Pierson, C.T.

1987-01-01

The chemistry of three stream, three spring and six near-surface waters in the vicinity of a Holocene organic-rich uranium deposit is described, with particular emphasis on the chemistry of U. Results characterize the solution behavior of uranium as U-bearing water interacts with relatively undecomposed, surficial organic matter. Of the measured major and trace chemical species, only U is consistently highly enriched (17-318 ppb) relative to reported values for regional waters, or to literature values for waters in largely granitic terrains. R-mode factor analysis of the chemical data suggests that most U is present in a soluble form, but that some U is also associated with fine suspended particulates of clay, organic matter, or hydrous oxides. Calculations that apply thermodynamic data to predict U speciation in solution indicate the relative importance of uranyl carbonate and uranyl phosphate complexes. Analysis of more finely filtered samples (0.05 ??m vs. 0.45 ??m), and direct radiographic observations using fission-track detectors suspended in the waters indicate the presence of some uraniferous particulate matter. Application of existing thermodynamic data for uranous- and uranyl-bearing minerals indicates that all waters are undersaturated with U minerals as long as ambient Eh ??? +0.1 v. If coexisting surface and near-surface waters are sufficiently oxidizing, initial fixation of U in the deposit should be by a mechanism of adsorption. Alternatively, more reducing conditions may prevail in deeper pore waters of the organic-rich host sediments, perhaps leading to direct precipitation or diagenetic formation of U4+ minerals. A 234U 238U alpha activity ratio of 1.08 ?? 0.02 in a spring issuing from a hillslope above the deposit suggests a relatively soluble source of U. In contrast, higher activity ratios of 234U 238U (??? 1.3) in waters in contact with the uraniferous valley-fill sediments suggest differences in the nature of interaction between groundwater and the local, U-rich source rocks. ?? 1987.

ZPR-6 assembly 7 high {sup 240} PU core : a cylindrical assemby with mixed (PU, U)-oxide fuel and a central high {sup 240} PU zone.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lell, R. M.; Schaefer, R. W.; McKnight, R. D.

Over a period of 30 years more than a hundred Zero Power Reactor (ZPR) critical assemblies were constructed at Argonne National Laboratory. The ZPR facilities, ZPR-3, ZPR-6, ZPR-9 and ZPPR, were all fast critical assembly facilities. The ZPR critical assemblies were constructed to support fast reactor development, but data from some of these assemblies are also well suited to form the basis for criticality safety benchmarks. Of the three classes of ZPR assemblies, engineering mockups, engineering benchmarks and physics benchmarks, the last group tends to be most useful for criticality safety. Because physics benchmarks were designed to test fast reactormore » physics data and methods, they were as simple as possible in geometry and composition. The principal fissile species was {sup 235}U or {sup 239}Pu. Fuel enrichments ranged from 9% to 95%. Often there were only one or two main core diluent materials, such as aluminum, graphite, iron, sodium or stainless steel. The cores were reflected (and insulated from room return effects) by one or two layers of materials such as depleted uranium, lead or stainless steel. Despite their more complex nature, a small number of assemblies from the other two classes would make useful criticality safety benchmarks because they have features related to criticality safety issues, such as reflection by soil-like material. The term 'benchmark' in a ZPR program connotes a particularly simple loading aimed at gaining basic reactor physics insight, as opposed to studying a reactor design. In fact, the ZPR-6/7 Benchmark Assembly (Reference 1) had a very simple core unit cell assembled from plates of depleted uranium, sodium, iron oxide, U3O8, and plutonium. The ZPR-6/7 core cell-average composition is typical of the interior region of liquid-metal fast breeder reactors (LMFBRs) of the era. It was one part of the Demonstration Reactor Benchmark Program,a which provided integral experiments characterizing the important features of demonstration-size LMFBRs. As a benchmark, ZPR-6/7 was devoid of many 'real' reactor features, such as simulated control rods and multiple enrichment zones, in its reference form. Those kinds of features were investigated experimentally in variants of the reference ZPR-6/7 or in other critical assemblies in the Demonstration Reactor Benchmark Program.« less

Heptavalent Neptunium in a Gas-Phase Complex: (Np VIIO 3 +)(NO 3 –) 2

DOE PAGES

Dau, Phuong D.; Maurice, Remi; Renault, Eric; ...

2016-09-15

A central goal of chemistry is to achieve ultimate oxidation states, including in gas-phase complexes with no condensed phase perturbations. In the case of the actinide elements, the highest established oxidation states are labile Pu(VII) and somewhat more stable Np(VII). We have synthesized and characterized gas-phase AnO 3(NO 3) 2- complexes for An = U, Np, and Pu by endothermic NO 2 elimination from AnO 2(NO 3) 3-. It was previously demonstrated that the PuO 3+ core of PuO 3(NO 3) 2- has a Pu—O• radical bond such that the oxidation state is Pu(VI); it follows that in UO 3(NOmore » 3) 2- it is the stable U(VI) oxidation state. On the basis of the relatively more facile synthesis of NpO 3(NO 3) 2-, a Np(VII) oxidation state is inferred. This interpretation is substantiated by reactivity of the three complexes: NO 2 spontaneously adds to UO 3(NO 3) 2- and PuO 3(NO 3) 2- but not to NpO 3(NO 3) 2-. This unreactive character is attributed to a Np(VII)O 3+ core with three stable Np=O bonds, this in contrast to reactive U—O• and Pu—O• radical bonds. The computed structures and reaction energies for the three AnO 3(NO 3) 2- support the conclusion that the oxidation states are U(VI), Np(VII), and Pu(VI). These results establish the extreme Np(VII) oxidation state in a gas-phase complex, and demonstrate the inherently greater stability of Np(VII) versus Pu(VII).« less

Multielement statistical evidence for uraniferous hydrothermal activity in sandstones overlying the Phoenix uranium deposit, Athabasca Basin, Canada

NASA Astrophysics Data System (ADS)

Chen, Shishi; Hattori, Keiko; Grunsky, Eric C.

2018-04-01

The Phoenix U deposit, with indicated resources of 70.2 M lb U3O8, occurs along the unconformity between the Proterozoic Athabasca Group sandstones and the crystalline basement rocks. Principal component analysis (PCA) is applied to the compositions of sandstones overlying the deposit. Among PCs, PC1 accounts for the largest variability of U and shows a positive association of U with rare earth elements (REEs) + Y + Cu + B + Na + Mg + Ni + Be. The evidence suggests that U was dispersed into sandstones together with these elements during the uraniferous hydrothermal activity. Uranium shows an inverse association with Zr, Hf, Th, Fe, and Ti. Since they are common in detrital heavy minerals, such heavy minerals are not the major host of U. The elements positively associated with U are high in concentrations above the deposit, forming a "chimney-like" or "hump-like" distribution in a vertical section. Their enrichment patterns are explained by the ascent of basement fluids through faults to sandstones and the circulation of basinal fluids around the deposit. The Pb isotope compositions of whole rocks are similar to expected values calculated from the concentrations of U, Th, and Pb except for sandstones close to the deposit. The data suggest that in situ decay of U and Th is responsible for the Pb isotope compositions of most sandstones and that highly radiogenic Pb dispersed from the deposit to the proximal sandstones long after the mineralization. This secondary dispersion is captured in PC8, which has low eigenvalue. The data suggests that the secondary dispersion has minor effect on the overall lithogeochemistry of sandstones.

The thermal conductivity of mixed fuel U xPu 1-xO 2: molecular dynamics simulations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Xiang-Yang; Cooper, Michael William Donald; Stanek, Christopher Richard

2015-10-16

Mixed oxides (MOX), in the context of nuclear fuels, are a mixture of the oxides of heavy actinide elements such as uranium, plutonium and thorium. The interest in the UO 2-PuO 2 system arises from the fact that these oxides are used both in fast breeder reactors (FBRs) as well as in pressurized water reactors (PWRs). The thermal conductivity of UO 2 fuel is an important material property that affects fuel performance since it is the key parameter determining the temperature distribution in the fuel, thus governing, e.g., dimensional changes due to thermal expansion, fission gas release rates, etc. Formore » this reason it is important to understand the thermal conductivity of MOX fuel and how it differs from UO 2. Here, molecular dynamics (MD) simulations are carried out to determine quantitatively, the effect of mixing on the thermal conductivity of U xPu 1-xO 2, as a function of PuO 2 concentrations, for a range of temperatures, 300 – 1500 K. The results will be used to develop enhanced continuum thermal conductivity models for MARMOT and BISON by INL. These models express the thermal conductivity as a function of microstructure state-variables, thus enabling thermal conductivity models with closer connection to the physical state of the fuel.« less

Surface reactions kinetics between nanocrystalline magnetite and uranyl.

PubMed

Missana, Tiziana; Maffiotte, César; García-Gutiérrez, Miguel

2003-05-01

Magnetite is the most important end member of iron corrosion products under reducing environment, which is the condition expected in a deep geological high level radioactive waste disposal. Nanocrystalline magnetite was synthesized in the laboratory and its physicochemical properties were analyzed in detail. The kinetics of the adsorption of U(VI) and the kinetics of the actinide reduction to a lower oxidation state, in presence of the oxide, were studied by means of batch sorption techniques and X-ray photoelectron spectroscopy (XPS) analysis. The results showed that the uranium sorption and reduction processes on the magnetite surface have very fast kinetics (hours), the reduction process being triggered by sorption. XPS measurements showed that the speciation of uranium at the surface does not show significant changes with time (from 1 day to 3 months), as well as the quantity of uranium detected at the surface. The surface speciation depended on the initial pH of the contact solution. Considering that the Eh of equilibrium between magnetite and the solution, under our experimental conditions, is slightly positive (50-100 mV), the uranium reduction would also be thermodynamically possible within the liquid phase. However, the kinetics of reduction in the liquid occur at a much slower rate which, in turn, has to depend on the attainment of the magnetite/solution equilibrium. The decrease of uranium in solution, observed after the uranyl adsorption stage, and particularly at acidic pH, is most probably due to the precipitation of U(IV) formed in the solution.

Inclusions and Substructures in Uranium of Nuclear Purity. Report No. 51; INCLUSIONES Y SUBESTRUCTURAS EN URANIO DE PUREZA NUCLEAR. INFORME NO. 51

DOE Office of Scientific and Technical Information (OSTI.GOV)

Biloni, H.; Lindenvald, N.; Sabato, J.A.

1961-01-01

The inclusions in uranium of nuclear purity (UC, UH/sub 3/, UO/sub 2/, UO, UN, and the complexes which include the intersolubility of U with C and N or with C, N, and O) were . analyzed metallographically, and the results reported by other authors were discussed critically. The existence of the fine precipitate reticular substructure, sensitive to thermal treatments, which generally appears in uraniunn was analyzed. Its origins were discussed in accordance with bibliographic data. Complementary data for its comprehension are given from the metallographic analysis of U--Al and U-- Fe alloys with low Al and Fe concentrations. (tr-auth)

Investigations Into the Reusability of Amidoxime-Based Polymeric Uranium Adsorbents

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kuo, Li-Jung; Gill, Gary A.; Strivens, Jonathan E.

Significant advancements in amidoxime-based polymeric adsorbents to extract uranium from seawater are achieved in recent years. The success of uranium adsorbent development can help provide a sustainable supply of fuel for nuclear reactors. To bring down the production cost of this new technology, in addition to the development of novel adsorbents with high uranium capacity and manufacture cost, the development of adsorbent re-using technique is critical because it can further reduce the cost of the adsorbent manufacture. In our last report, the use of high concentrations of bicarbonate solution (3M KHCO3) was identified as a cost-effective, environmental friendly method tomore » strip uranium from amidoxime-based polymeric adsorbents. This study aims to further improve the method for high recovery of uranium capacity in re-uses and to evaluate the performance of adsorbents after multiple re-use cycles. Adsorption of dissolved organic matter (DOM) on the uranium adsorbents during seawater exposure can hinder the uranium adsorption and slow down the adsorption rate. An additional NaOH rinse (0.5 M NaOH, room temperature) was applied after the 3 M KHCO3 elution to remove natural organic matter from adsorbents. The combination of 3 M KHCO3 elution and 0.5 M NaOH rinse significantly improves the recovery of uranium adsorption capacity in the re-used adsorbents. In the first re-use, most ORNL adsorbents tested achieve ~100% recovery by using 3 M KHCO3 elution + 0.5 M NaOH rinse approach, in comparison to 54% recovery when only 3 M KHCO3 elution was applied. A significant drop in capacity was observed when the adsorbents went through more than one re-use. FTIR spectra revealed that degradation of amidoxime ligands occurs during seawater exposure, and is more significant the longer the exposure time. Significantly elevated ratios of Ca/U and Mg/U in re-used adsorbents support the decrease in abundance of amidoxime ligands and increase carboxylate group from FT-IR analysis. The impact of the length of seawater exposure cycle in adsorbent re-use was evaluated by comparing the adsorption capacity for a common adsorbent formulation (ORNL AI8 formulation) under different exposure cycle (28 days and 42 days). Adsorbents with a 28 days seawater exposure cycle had higher recovery of uranium capacity than adsorbent with 42 days of seawater exposure. Under different cumulative seawater exposure time, the adsorbent with 28 days seawater exposure cycle also had less amidoxime ligands degradation than the adsorbent with 42 days seawater exposure cycle. These observations support the negative impact of prolonged seawater exposure on amidoxime ligands stability. Recovery of uranium capacity in re-uses also varies across different adsorbent formulations. Among three different ORNL adsorbents tested (AI8, AF8, AF1-DMSO), AI8 had the best recovery in each re-use, followed by AF8 and then AF1-DMSO. This demonstrates that continuing efforts on developing new adsorbents with high capacity and stability is critical. The overall performance of adsorbents in multiple re-use cycles can be evaluated by calculation total harvestable uranium, the summation of adsorbed uranium from each seawater exposure cycle. In this assessment, the ORNL AI8 braid with 28 days seawater exposure cycle can reach total harvestable uranium 10g Uranium/kg adsorbent in ~140 days; while the same type of braid but with 42 days seawater exposure cycle reach the same level in ~170 days. Notably, the performance of total harvestable uranium also varies among different adsorbent formulations (AI8 > AF1-DMSO > AF8). Short seawater exposure cycle is associated with high re-use frequency. The development of low-cost offshore adsorbent deployment/extraction is essential for high frequency reuse operation. This study also highlights the importance to examine the re-use performance of newly developed uranium adsorbents for selection of optimal adsorbents for ocean deployment.« less

High-Resolution Mineralogical Characterization and Biogeochemical Modeling of Uranium Reduction Pathways at the NABIR Field-Research Center

DOE Office of Scientific and Technical Information (OSTI.GOV)

David R. Veblen; Chen Zhu; Lee Krumholz

The effectiveness and feasibility of bioremediation at the field scale cannot be fully assessed until the mechanisms of immobilization and U speciation in the solid matrix are resolved. However, characterization of the immobilized U and its valence states is extremely difficult, because microbially mediated mineral precipitates are generally nanometer (nm)-sized, poorly crystalline, or amorphous. We are developing combined field emission gun--scanning electron microscopy (FEG-SEM, at Indiana University) and FEG transmission electron microscopy (TEM, at Hopkins) to detect and isolate uranium containing phases; (1) method developments for TEM sample preparations and parallel electron energy loss spectroscopy (EELS) determination of uranium valence;more » and (2) to determine the speciation, fate, reactivity, valence states of immobilized uranium, using the state-of-the-art 300-kV, FEG-TEM. We have obtained preliminary results on contaminated sediments from Area 3 at the Oak Ridge Field Research Center (FRC). TEM results show that the sediments contain numerous minerals, including quartz, mica/clay (muscovite and/or illite), rutile, ilmenite, zircon, and an Al-Sr-Ce-Ca phosphate mineral, none of which contain uranium above the EDS detection limit. Substantial U (up to {approx}2 wt.%) is, however, clearly associated with two materials: (1) the Fe oxyhydroxide and (2) clots of a chemically complex material that is likely a mixture of several nm-scale phases. The Fe oxyhydroxide was identified as goethite from its polycrystalline SAED pattern and EDS analysis showing it to be very Fe-rich; the aggregate also displays one of several morphologies that are common for goethite. U is strongly sorbed to goethite in the FRC sediment, and the ubiquitous association with phosphorous suggests that complexes containing both U and P may play an important role in that sorption. Results from bulk analysis and SEM had previously demonstrated the association of U with Fe and thus suggested that U may be sorbed by Fe oxide or oxyhydroxide (Dr. Roh, image presented by David Watson). However, rigorous identification of the host minerals for U requires TEM results such as these involving imaging, electron diffraction, and spectroscopic analysis. An even higher concentration of U occurs in the chemically complex material noted above. These ''clots'' are high in Fe but also contain C, O, Mg, Al, Si, P, S, Cl, K, Ca, Mn, and U. This chemical complexity strongly suggests that they consist of aggregates of carbonate, silicate, phosphate, and sulfate phases, and TEM images also suggest that they may be intergrowths of numerous exceedingly small nanoparticles. EELS and EFTEM studies should be able to resolve these various components and identify precisely where the uranium is in these complex materials. From the results, it is clear that the FEG-SEM and FEG-TEM can readily detect uranium in the FRC samples. The FEG-SEM allows a wide field of view of the samples and can detect U-rich aggregates as small as 20-30 nm. The FEG-TEM can then focus on these aggregates and use SAED, EDS, EFTEM, and PEELS techniques to determine the valence states, structures, and compositional data for these aggregates. This research will provide a crucial component for a complete understanding of the efficacy of uranium bioremediation.« less

Characterization and Testing of Amidoxime-Based Adsorbent Materials to Extract Uranium from Natural Seawater

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kuo, Li-Jung; Janke, Christopher J.; Wood, Jordana R.

Extraction of uranium (U) from seawater for use as a nuclear fuel is a significant challenge due to the low concentration of U in seawater (~3.3 ppb) and difficulties to selectively extract U from the background of major and trace elements in seawater. The Pacific Northwest National Laboratory (PNNL)’s Marine Sciences Laboratory (MSL) has been serving as a marine test site for determining performance characteristics (adsorption capacity, adsorption kinetics, and selectivity) of novel amidoxime-based polymeric adsorbents developed at Oak Ridge National Laboratory (ORNL) under natural seawater exposure conditions. This manuscript describes the performance of three formulations (38H, AF1, AI8) ofmore » amidoxime-based polymeric adsorbents produced at ORNL in MSL’s ambient seawater testing facility. The adsorbents were produced in two forms, fibrous material (40-100 mg samples) and braided material (5-10 g samples), and exposed to natural seawater using flow-through columns and recirculating flumes. All three formulations demonstrated high 56 day uranium adsorption capacity (>3 g U/kg adsorbent). The AF1 formulation had the best uranium adsorption performance, with a 56 day capacity of 3.9 g U/ kg adsorbent, a saturation capacity of 5.4 g U/kg adsorbent, and ~25 days half-saturation time. The two exposure methods, flowthrough columns and flumes, were demonstrated to produce similar performance results, providing confidence that the test methods were reliable, that scaling up from 10’s of mg quantities of exposure in flow-through columns to gram quantities in flumes produced similar results, and confirm that the manufacturing process produces a homogeneous adsorbent. Adsorption kinetics appear to be element specific, with half-saturation times ranging from minutes for the major cations in seawater, to 8-10 weeks for V and Fe. Reducing the exposure time provides a potential pathway to improve the adsorption capacity of U by reducing the V/U ratio on the adsorbent.« less

Characterization and testing of amidoxime-based adsorbent materials to extract uranium from natural seawater

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kuo, Li-Jung; Janke, Christopher James; Wood, Jordana

Extraction of uranium (U) from seawater for use as a nuclear fuel is a significant challenge due to the low concentration of U in seawater (~3.3 ppb) and difficulties to selectively extract U from the background of major and trace elements in seawater. The Pacific Northwest National Laboratory (PNNL) s Marine Sciences Laboratory (MSL) has been serving as a marine test site for determining performance characteristics (adsorption capacity, adsorption kinetics, and selectivity) of novel amidoxime-based polymeric adsorbents developed at Oak Ridge National Laboratory (ORNL) under natural seawater exposure conditions. This report describes the performance of three formulations (38H, AF1, AI8)more » of amidoxime-based polymeric adsorbent produced at ORNL in MSL s ambient seawater testing facility. The adsorbents were produced in two forms, fibrous material (40-100 mg samples) and braided material (5-10 g samples), exposed to natural seawater using flow-through columns and recirculating flumes. All three formulations demonstrated high 56 day uranium adsorption capacity (>3 gU/kg adsorbent). The AF1 formulation had the best uranium adsorption performance, with 56-day capacity of 3.9 g U/kg adsorbent, saturation capacity of 5.4 g U/kg adsorbent, and ~25 days half-saturation time. The two exposure methods, flow-through columns and flumes were demonstrated to produce similar performance results, providing confidence that the test methods were reliable, that scaling up from 10 s of mg quantities of exposure in flow-through columns to gram quantities in flumes produced similar results, and that the manufacturing process produces a homogenous adsorbent. Adsorption kinetics appear to be element specific, with half-saturation times ranging from minutes for the major cations in seawater to 8-10weeks for V and Fe. Reducing the exposure time provides a potential pathway to improve the adsorption capacity of U by reducing the V/U ratio on the adsorbent.« less

Characterization and testing of amidoxime-based adsorbent materials to extract uranium from natural seawater

DOE PAGES

Kuo, Li-Jung; Janke, Christopher James; Wood, Jordana; ...

2015-11-19

Extraction of uranium (U) from seawater for use as a nuclear fuel is a significant challenge due to the low concentration of U in seawater (~3.3 ppb) and difficulties to selectively extract U from the background of major and trace elements in seawater. The Pacific Northwest National Laboratory (PNNL) s Marine Sciences Laboratory (MSL) has been serving as a marine test site for determining performance characteristics (adsorption capacity, adsorption kinetics, and selectivity) of novel amidoxime-based polymeric adsorbents developed at Oak Ridge National Laboratory (ORNL) under natural seawater exposure conditions. This report describes the performance of three formulations (38H, AF1, AI8)more » of amidoxime-based polymeric adsorbent produced at ORNL in MSL s ambient seawater testing facility. The adsorbents were produced in two forms, fibrous material (40-100 mg samples) and braided material (5-10 g samples), exposed to natural seawater using flow-through columns and recirculating flumes. All three formulations demonstrated high 56 day uranium adsorption capacity (>3 gU/kg adsorbent). The AF1 formulation had the best uranium adsorption performance, with 56-day capacity of 3.9 g U/kg adsorbent, saturation capacity of 5.4 g U/kg adsorbent, and ~25 days half-saturation time. The two exposure methods, flow-through columns and flumes were demonstrated to produce similar performance results, providing confidence that the test methods were reliable, that scaling up from 10 s of mg quantities of exposure in flow-through columns to gram quantities in flumes produced similar results, and that the manufacturing process produces a homogenous adsorbent. Adsorption kinetics appear to be element specific, with half-saturation times ranging from minutes for the major cations in seawater to 8-10weeks for V and Fe. Reducing the exposure time provides a potential pathway to improve the adsorption capacity of U by reducing the V/U ratio on the adsorbent.« less

Uranium Release from Acidic Weathered Hanford Sediments: Single-Pass Flow-Through and Column Experiments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Guohui; Um, Wooyong; Wang, Zheming

The reaction of acidic radioactive waste with sediments can induce mineral transformation reactions that, in turn, control contaminant fate. Here, sediment weathering by synthetic uranium-containing acid solutions was investigated using bench-scale experiments to simulate waste disposal conditions at Hanford’s cribs, USA. During acid weathering, the presence of phosphate exerted a strong influence over uranium mineralogy and a rapidly precipitated, crystalline uranium phosphate phase (meta-ankoleite [K(UO2)(PO4)·3H2O]) was identified using spectroscopic and diffraction-based techniques. In phosphate-free system, uranium oxyhydroxide minerals such as K-compreignacite [K2(UO2)6O4(OH)6·7H2O] were formed. Single-pass flow-through (SPFT) and column leaching experiments using synthetic Hanford pore water showed that uranium precipitatedmore » as meta-ankoleite during acid weathering was strongly retained in the sediments, with an average release rate of 2.67E-12 mol g-1 s-1. In the absence of phosphate, uranium release was controlled by dissolution of uranium oxyhydroxide (compreignacite-type) mineral with a release rate of 1.05-2.42E-10 mol g-1 s-1. The uranium mineralogy and release rates determined for both systems in this study support the development of accurate U-release models for prediction of contaminant transport. These results suggest that phosphate minerals may be a good candidate for uranium remediation approaches at contaminated sites.« less

Uranium Release from Acidic Weathered Hanford Sediments: Single-Pass Flow-Through and Column Experiments.

PubMed

Wang, Guohui; Um, Wooyong; Wang, Zheming; Reinoso-Maset, Estela; Washton, Nancy M; Mueller, Karl T; Perdrial, Nicolas; O'Day, Peggy A; Chorover, Jon

2017-10-03

The reaction of acidic radioactive waste with sediments can induce mineral transformation reactions that, in turn, control contaminant fate. Here, sediment weathering by synthetic uranium-containing acid solutions was investigated using bench-scale experiments to simulate waste disposal conditions at Hanford's cribs (Hanford, WA). During acid weathering, the presence of phosphate exerted a strong influence over uranium mineralogy and a rapidly precipitated, crystalline uranium phosphate phase (meta-ankoleite [K(UO 2 )(PO 4 )·3H 2 O]) was identified using spectroscopic and diffraction-based techniques. In phosphate-free system, uranium oxyhydroxide minerals such as K-compreignacite [K 2 (UO 2 ) 6 O 4 (OH) 6 ·7H 2 O] were formed. Single-pass flow-through (SPFT) and column leaching experiments using synthetic Hanford pore water showed that uranium precipitated as meta-ankoleite during acid weathering was strongly retained in the sediments, with an average release rate of 2.67 × 10 -12 mol g -1 s -1 . In the absence of phosphate, uranium release was controlled by dissolution of uranium oxyhydroxide (compreignacite-type) mineral with a release rate of 1.05-2.42 × 10 -10 mol g -1 s -1 . The uranium mineralogy and release rates determined for both systems in this study support the development of accurate U-release models for the prediction of contaminant transport. These results suggest that phosphate minerals may be a good candidate for uranium remediation approaches at contaminated sites.

Electrochemical and spectroscopic evidence on the one-electron reduction of U(VI) to U(V) on magnetite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yuan, Ke; Ilton, Eugene S.; Antonio, Mark R.

2015-05-19

Reduction of U(VI) to U(IV) on mineral surfaces has been considered as a one-step two electron process. However, stabilized U(V), with no evidence of U(IV), found in recent studies indicates U(VI) can undergo a one electron reduction to U(V) without further progression to U(IV). We investigated the mechanisms of uranium reduction by reducing U(VI) electrochemically on a magnetite electrode at pH 3.4 . The one electron reduction of U(VI) was first confirmed using the cyclic voltammetry method. Formation of nano-size uranium precipitates on the surface of magnetite at reducing potentials and dissolution of the solids at oxidizing potentials were observedmore » by in situ electrochemical AFM. XPS analysis of the magnetite electrodes polarized in uranium solutions at voltages from 0.1 ~ 0.9 V (vs. Ag/AgCl) showed the presence of only U(V) and U(VI). The highest amount of U(V) relative to U(VI) was prepared at 0.7 V, where the longest average U–Oaxial distance of 2.05 ± 0.01 Å was evident in the same sample revealed by EXAFS analysis. The results demonstrate that the electrochemical reduction of U(VI) on magnetite only yields U(V), even at a potential of 0.9 V, which favors the one-electron reduction mechanism. U(V) did not disproportionate but stabilized on magnetite through precipitation of mixed-valence state U(VI)/U(V) solids.« less

Identification of Uranium Minerals in Natural U-Bearing Rocks Using Infrared Reflectance Spectroscopy.

PubMed

Beiswenger, Toya N; Gallagher, Neal B; Myers, Tanya L; Szecsody, James E; Tonkyn, Russell G; Su, Yin-Fong; Sweet, Lucas E; Lewallen, Tricia A; Johnson, Timothy J

2018-02-01

The identification of minerals, including uranium-bearing species, is often a labor-intensive process using X-ray diffraction (XRD), fluorescence, or other solid-phase or wet chemical techniques. While handheld XRD and fluorescence instruments can aid in field applications, handheld infrared (IR) reflectance spectrometers can now also be used in industrial or field environments, with rapid, nondestructive identification possible via analysis of the solid's reflectance spectrum providing information not found in other techniques. In this paper, we report the use of laboratory methods that measure the IR hemispherical reflectance of solids using an integrating sphere and have applied it to the identification of mineral mixtures (i.e., rocks), with widely varying percentages of uranium mineral content. We then apply classical least squares (CLS) and multivariate curve resolution (MCR) methods to better discriminate the minerals (along with two pure uranium chemicals U 3 O 8 and UO 2 ) against many common natural and anthropogenic background materials (e.g., silica sand, asphalt, calcite, K-feldspar) with good success. Ground truth as to mineral content was attained primarily by XRD. Identification is facile and specific, both for samples that are pure or are partially composed of uranium (e.g., boltwoodite, tyuyamunite, etc.) or non-uranium minerals. The characteristic IR bands generate unique (or class-specific) bands, typically arising from similar chemical moieties or functional groups in the minerals: uranyls, phosphates, silicates, etc. In some cases, the chemical groups that provide spectral discrimination in the longwave IR reflectance by generating upward-going (reststrahlen) bands can provide discrimination in the midwave and shortwave IR via downward-going absorption features, i.e., weaker overtone or combination bands arising from the same chemical moieties.

XANES and EXAFS investigation of uranium incorporation on nZVI in the presence of phosphate.

PubMed

Qiu, Muqing; Wang, Min; Zhao, Qingzhou; Hu, Baowei; Zhu, Yuling

2018-06-01

Effect of phosphate on the reduction of U(VI) on nZVI was determined by batch, XPS, XANES and EXAFS techniques. The batch experiments showed that nZVI was quite effective for the removal of uranium under the anaerobic conditions, whereas the addition of phosphate enhanced uranium removal over wide pH range. At low pH, the reduction of U(VI) to U(IV) significantly decreased with increasing phosphate concentration by XPS and XANES analysis. According to EXAFS analysis, the occurrence of UU shell at 10 mg/L phosphate and pH 4.0 was similar to that of U (IV) O 2 (s), whereas the UP and UFe shells were observed at 50 mg/L phosphate, revealing that reductive co-precipitate (U (IV) O 2 (s)) and precipitation of uranyl-phosphate were observed at low and high phosphate, respectively. The findings are crucial for the prediction of the effect of phosphate on the speciation and binding of uranium by nZVI at low pH, which is significant in controlling the mobility of U(VI) in contaminated environments. Copyright © 2018 Elsevier Ltd. All rights reserved.

Igneous rocks of the East Pacific Rise

USGS Publications Warehouse

Engel, A.E.J.; Engel, C.G.

1964-01-01

The apical parts of large volcanoes along the East Pacific Rise (islands and seamounts) are encrusted with rocks of the alkali volcanic suite (alkali basalt, andesine- and oligoclase-andesite, and trachyte). In contrast, the more submerged parts of the Rise are largely composed of a tholeiitic basalt which has low concentrations of K, P, U, Th, Pb, and Ti. This tholeiitic basalt is either the predominant or the only magma generated in the earth's mantle under oceanic ridges and rises. It is at least 1000-fold more abundant than the alkali suite, which is probably derived from tholeiitic basalt by magmatic differentiation in and immediately below the larger volcanoes. Distinction of oceanic tholeiites from almost all continental tholeiites is possible on the simple basis of total potassium content, with the discontinuity at 0.3 to 0.5 percent K2O by weight. Oceanic tholeiites also are readily distinguished from some 19 out of 20 basalts of oceanic islands and seamount cappings by having less than 0.3 percent K2O by weight and more than 48 percent SiO2. Deep drilling into oceanic volcanoes should, however, core basalts transitional between the oceanic tholeiites and the presumed derivative alkali basalts.The composition of the oceanic tholeiites suggests that the mantle under the East Pacific Rise contains less than 0.10 percent potassium oxide by weight; 0.1 part per million of uranium and 0.4 part of thorium; a potassium:rubidium ratio of about 1200 and a potassium: uranium ratio of about 104.

31 CFR 540.315 - Uranium-235 (U235).

Code of Federal Regulations, 2013 CFR

2013-07-01

... 31 Money and Finance:Treasury 3 2013-07-01 2013-07-01 false Uranium-235 (U235). 540.315 Section... FOREIGN ASSETS CONTROL, DEPARTMENT OF THE TREASURY HIGHLY ENRICHED URANIUM (HEU) AGREEMENT ASSETS CONTROL REGULATIONS General Definitions § 540.315 Uranium-235 (U235). The term uranium-235 or U235 means the fissile...

31 CFR 540.315 - Uranium-235 (U235).

Code of Federal Regulations, 2012 CFR

2012-07-01

... 31 Money and Finance:Treasury 3 2012-07-01 2012-07-01 false Uranium-235 (U235). 540.315 Section... FOREIGN ASSETS CONTROL, DEPARTMENT OF THE TREASURY HIGHLY ENRICHED URANIUM (HEU) AGREEMENT ASSETS CONTROL REGULATIONS General Definitions § 540.315 Uranium-235 (U235). The term uranium-235 or U235 means the fissile...

31 CFR 540.315 - Uranium-235 (U235).

Code of Federal Regulations, 2014 CFR

2014-07-01

... 31 Money and Finance:Treasury 3 2014-07-01 2014-07-01 false Uranium-235 (U235). 540.315 Section... FOREIGN ASSETS CONTROL, DEPARTMENT OF THE TREASURY HIGHLY ENRICHED URANIUM (HEU) AGREEMENT ASSETS CONTROL REGULATIONS General Definitions § 540.315 Uranium-235 (U235). The term uranium-235 or U235 means the fissile...

31 CFR 540.315 - Uranium-235 (U235).

Code of Federal Regulations, 2011 CFR

2011-07-01

... 31 Money and Finance:Treasury 3 2011-07-01 2011-07-01 false Uranium-235 (U235). 540.315 Section... FOREIGN ASSETS CONTROL, DEPARTMENT OF THE TREASURY HIGHLY ENRICHED URANIUM (HEU) AGREEMENT ASSETS CONTROL REGULATIONS General Definitions § 540.315 Uranium-235 (U235). The term uranium-235 or U235 means the fissile...

31 CFR 540.315 - Uranium-235 (U235).

Code of Federal Regulations, 2010 CFR

2010-07-01

... 31 Money and Finance: Treasury 3 2010-07-01 2010-07-01 false Uranium-235 (U235). 540.315 Section... FOREIGN ASSETS CONTROL, DEPARTMENT OF THE TREASURY HIGHLY ENRICHED URANIUM (HEU) AGREEMENT ASSETS CONTROL REGULATIONS General Definitions § 540.315 Uranium-235 (U235). The term uranium-235 or U235 means the fissile...

Geophysical interpretation of U, Th, and rare earth element mineralization of the Bokan Mountain peralkaline granite complex, Prince of Wales Island, southeast Alaska

USGS Publications Warehouse

McCafferty, Anne E.; Stoeser, Douglas B.; Van Gosen, Bradley S.

2014-01-01

A prospectivity map for rare earth element (REE) mineralization at the Bokan Mountain peralkaline granite complex, Prince of Wales Island, southeastern Alaska, was calculated from high-resolution airborne gamma-ray data. The map displays areas with similar radioelement concentrations as those over the Dotson REE-vein-dike system, which is characterized by moderately high %K, eU, and eTh (%K, percent potassium; eU, equivalent parts per million uranium; and eTh, equivalent parts per million thorium). Gamma-ray concentrations of rocks that share a similar range as those over the Dotson zone are inferred to locate high concentrations of REE-bearing minerals. An approximately 1300-m-long prospective tract corresponds to shallowly exposed locations of the Dotson zone. Prospective areas of REE mineralization also occur in continuous swaths along the outer edge of the pluton, over known but undeveloped REE occurrences, and within discrete regions in the older Paleozoic country rocks. Detailed mineralogical examinations of samples from the Dotson zone provide a means to understand the possible causes of the airborne Th and U anomalies and their relation to REE minerals. Thorium is sited primarily in thorite. Uranium also occurs in thorite and in a complex suite of ±Ti±Nb±Y oxide minerals, which include fergusonite, polycrase, and aeschynite. These oxides, along with Y-silicates, are the chief heavy REE (HREE)-bearing minerals. Hence, the eU anomalies, in particular, may indicate other occurrences of similar HREE-enrichment. Uranium and Th chemistry along the Dotson zone showed elevated U and total REEs east of the Camp Creek fault, which suggested the potential for increased HREEs based on their association with U-oxide minerals. A uranium prospectivity map, based on signatures present over the Ross-Adams mine area, was characterized by extremely high radioelement values. Known uranium deposits were identified in the U-prospectivity map, but the largest tract occurs over a radioelement-rich granite phase within the pluton that is likely not related to mineralization. Neither mineralization type displays a well-defined airborne magnetic signature.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

Statistical data on energy production and consumption and supporting information were obtained from US Bureau of Mines records supplemented by additional data obtained in Portugal. Geologic descriptions and analysis of known areas and of areas having possible future potential have been prepared by the US Geological Survey. Portugal lacks sufficient indigenous supplies of organic fuels to meet its energy demands, and so must import large quantities of petroleum and coal. Approximately 80% of Portugal's electric energy is produced by hydroelectric stations; thermal stations produce the other 20%. Portugal has produced no crude oil, natural gas, or condensate; no resources ormore » reserves in these categories are listed for Portugal in the 1976 World Energy Conference report. Until the last year or so (1980), no significant onshore petroleum exploration had been done in Portugal since 1963. Production of coal in Portugal has declined steadily to the present annual yield of about 200,000 metric tons. On the basis of estimates in only three coal fields, resources of coal of all ranks in Portugal total at least 76 million (10/sup 6/) metric tons. Uranium is mined near Viseu and Guarda in the northern part of Portugal; the Nisa mine in east-central Portugal will begin producing uranium ore in 1985 after installation of a processing plant. Portugal produced 95 metric tons of uranium oxide (U/sub 3/O/sub 8/) from ore stocks in each year from 1972 through 1974; production is assumed to have continued at the same rate since then. Geothermal energy has not been developed in mainland Portugal; however, hot springs that may have geothermal energy potential are known in the Minho district in the northwest. Geothermal energy resources exist in the Azores and a program of evaluation and exploration with technical assistance from the USGS is presently in progress there.« less

Crystal structure of the pyrochlore oxide superconductor KOs{sub 2}O{sub 6}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yamaura, Jun-Ichi; Yonezawa, Shigeki; Muraoka, Yuji

2006-01-15

We report the single-crystal X-ray analysis of the structure of the pyrochlore oxide superconductor KOs{sub 2}O{sub 6}. The structure was identified as the {beta}-pyrochlore structure with space group Fd3-bar m and lattice constant a=10.089(2)A at 300K: the K atom is located at the 8b site, not at the 16d site as in conventional pyrochlore oxides. We found an anomalously large atomic displacement parameter U{sub iso}=0.0735(8)A{sup 2} at 300K for the K cation, which suggests that the K cation weakly bound to an oversized Os{sub 12}O{sub 18} cage exhibits intensive rattling, as recently observed for clathrate compounds. The rattling of Amore » cations is a common feature in the series of {beta}-pyrochlore oxide superconductors AOs{sub 2}O{sub 6} (A=Cs, Rb and K), and is greatest for the smallest K cation.« less

Spatial distribution of environmental risk associated to a uranium abandoned mine (Central Portugal)

NASA Astrophysics Data System (ADS)

Antunes, I. M.; Ribeiro, A. F.

2012-04-01

The abandoned uranium mine of Canto do Lagar is located at Arcozelo da Serra, central Portugal. The mine was exploited in an open pit and produced about 12430Kg of uranium oxide (U3O8), between 1987 and 1988. The dominant geological unit is the porphyritic coarse-grained two-mica granite, with biotite>muscovite. The uranium deposit consists of two gaps crushing, parallel to the coarse-grained porphyritic granite, with average direction N30°E, silicified, sericitized and reddish jasperized, with a width of approximately 10 meters. These gaps are accompanied by two thin veins of white quartz, 70°-80° WNW, ferruginous and jasperized with chalcedony, red jasper and opal. These veins are about 6 meters away from each other. They contain secondary U-phosphates phases such as autunite and torbernite. Rejected materials (1000000ton) were deposited on two dumps and a lake was formed in the open pit. To assess the environmental risk of the abandoned uranium mine of Canto do Lagar, were collected and analysed 70 samples on stream sediments, soils and mine tailings materials. The relation between samples composition were tested using the Principal Components Analysis (PCA) (multivariate analysis) and spatial distribution using Kriging Indicator. The spatial distribution of stream sediments shows that the probability of expression for principal component 1 (explaining Y, Zr, Nb, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Hf, Th and U contents), decreases along SE-NW direction. This component is explained by the samples located inside mine influence. The probability of expression for principal component 2 (explaining Be, Na, Al, Si, P, K, Ca, Ti, Mn, Fe, Co, Ni, Cu, As, Rb, Sr, Mo, Cs, Ba, Tl and Bi contents), increases to middle stream line. This component is explained by the samples located outside mine influence. The spatial distribution of soils, shows that the probability of expression for principal component 1 (explaining Mg, P, Ca, Ge, Sr, Y, Zr, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Hf, W, Th and U contents) decreases along SE direction and increases along NE and SW directions. The probability of expression for principal component 2 (explaining pH, K, Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Sr and Pb contents), decreases from central points (inside mine influence) to peripheral points (outside mine influence) and gradually increases along N and SW directions. The spatial distribution of tailing materials did not allowed a consistent spatial distribution. In general, the stream sediments are classified as unpolluted and not polluted or moderately polluted, according to geoaccumulation Müller index with exception of local samples, located inside mine influence. The soils cannot be used for public, private or residential uses according to the Canadian soil legislation. However, almost samples can be used for commercial or industrial occupation. According to the target values and intervention values for soils remediation, these soils need intervention. Tailing materials samples are much polluted in thorium (Th) and uranium (U) and they cannot be used for public, private or residential uses.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mehta, Vrajesh; Maillot, Fabien; Wang, Zheming

Uranyl phosphate solids are often found with uranium ores, and their low solubility makes them promising target phases for in situ remediation of uranium-contaminated subsurface environments. The products and solubility of uranium(VI) precipitated with phosphate can be affected by the pH, dissolved inorganic carbon (DIC) concentration, and co-solute composition (e.g. Na+/Ca2+) of the groundwater. Batch experiments were performed to study the effect of these parameters on the products and extent of uranium precipitation induced by phosphate addition. In the absence of co-solute cations, chernikovite [H3O(UO2)(PO4)•3H2O] precipitated despite uranyl orthophosphate [(UO2)3(PO4)2•4H2O] being thermodynamically more favorable under certain conditions. As determined usingmore » X-ray diffraction, electron microscopy, and laser induced fluorescence spectroscopy, the presence of Na+ or Ca2+ as a co-solute led to the precipitation of sodium autunite ([Na2(UO2)2(PO4)2] and autunite [Ca(UO2)2(PO4)2]), which are structurally similar to chernikovite. In the presence of sodium, the dissolved U(VI) concentrations were generally in agreement with equilibrium predictions of sodium autunite solubility. However, in the calcium-containing systems, the observed concentrations were below the predicted solubility of autunite, suggesting the possibility of uranium adsorption to or incorporation in a calcium phosphate precipitate in addition to the precipitation of autunite.« less

Early breakthrough of molybdenum and uranium in a permeable reactive barrier.

PubMed

Morrison, Stan J; Mushovic, Paul S; Niesen, Preston L

2006-03-15

A permeable reactive barrier (PRB) using zerovalent iron (ZVI) was installed at a site near Cañon City, CO, to treat molybdenum (Mo) and uranium (U) in groundwater. The PRB initially decreased Mo concentrations from about 4.8 to less than 0.1 mg/L; however, Mo concentrations in the ZVI increased to 2.0 mg/L after about 250 days and continued to increase until concentrations in the ZVI were about 4 times higherthan in the influent groundwater. Concentrations of U were reduced from 1.0 to less than 0.02 mg/L during the same period. Investigations of solid-phase samples indicate that (1) calcium carbonate, iron oxide, and sulfide minerals had precipitated in pores of the ZVI; (2) U and Mo were concentrated in the upgradient 5.1 cm of the ZVI; and (3) calcium was present throughout the ZVI accounting for up to 20.5% of the initial porosity. Results of a column test indicated that the ZVI from the PRB was still reactive for removing Mo and that removal rates were dependenton residence time and pH. The chemical evolution of the PRB is explained in four stages that present a progression from porous media flow through preferential flow and, finally, complete bypass of the ZVI.

Facile CO Cleavage by a Multimetallic CsU2 Nitride Complex.

PubMed

Falcone, Marta; Kefalidis, Christos E; Scopelliti, Rosario; Maron, Laurent; Mazzanti, Marinella

2016-09-26

Uranium nitrides are important materials with potential for application as fuels for nuclear power generation, and as highly active catalysts. Molecular nitride compounds could provide important insight into the nature of the uranium-nitride bond, but currently little is known about their reactivity. In this study, we found that a complex containing a nitride bridging two uranium centers and a cesium cation readily cleaved the C≡O bond (one of the strongest bonds in nature) under ambient conditions. The product formed has a [CsU2 (μ-CN)(μ-O)] core, thus indicating that the three cations cooperate to cleave CO. Moreover, the addition of MeOTf to the nitride complex led to an exceptional valence disproportionation of the CsU(IV) -N-U(IV) core to yield CsU(III) (OTf) and [MeN=U(V) ] fragments. The important role of multimetallic cooperativity in both reactions is illustrated by the computed reaction mechanisms. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Quantification of kinetic rate law parameters for the dissolution of natural autunite in the presence of aqueous bicarbonate ions at high concentrations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gudavalli, Ravi; Katsenovich, Yelena; Wellman, Dawn

Uranium is a key contaminant of concern in the groundwater at 91 waste sites at 18 U.S. Department of Energy (DOE) facilities within the United States and is a potential source of groundwater contamination and a risk to human health and the environment through discharges to surface water. Dissolved inorganic carbon (bicarbonate/carbonate) has a high affinity for complexing with uranium that is present as sorbed or unique uranium-bearing mineral phases within the sedimentary matrix. This process can result in the formation of soluble uranyl carbonate aqueous species, which are mobile under circumneutral pH conditions. This study was conducted to quantifymore » the rate of release of uranium from the autunite mineral, (Ca[(UO 2)(PO 4)] 2∙3H 2O), that was formed during polyphosphate injection to remediate uranium; the dissolution of uranium was studied as a function of the aqueous bicarbonate concentration, ranging from 25 to 100 mM. Experiments were carried out in the pH range from 7 to 11 in the temperature range of 23-90°C via single-pass flow-through testing. Consistent with the results of previous studies (Gudavalli et al., 2013 a, b), the rate of uranium release from autunite exhibited minimal dependency on temperature, but was strongly dependent on pH and increasing concentrations of bicarbonate in the solution. Data obtained during these experiments were compared with results of previous experiments conducted using a low-concentration range of bicarbonate solutions (0.5-3.0 mM). An 8- to 30 fold increase in the rate of uranium release was observed in the presence of high bicarbonate concentrations at pH 7-8 compared to low bicarbonate values, while at pH 9-11, there was only a 5-fold increase in uranium rate of release with an increase in bicarbonate concentrations. The rate of uranium release was calculated to be between 5.18 x 10 -8 and 1.69 x 10 -7 mol m -2 s -1. The activation energy values at high and low bicarbonate concentrations were similar, with ratio values in the range of 0.6-1.0.« less