[Mechanical property of tooth-like yttria-stabilized tetragonal zirconia polycrystal by adding rare earth oxide].

PubMed

Gao, Yan; Zhang, Fuqiang; Gao, Jianhua

2012-02-01

To evaluate the influence of mechanical property of tooth-like yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) by adding rare earth oxide as colorants. Six kinds of tooth-like Y-TZP were made by introducing internal coloration technology. The colorants included rare earth oxide (Pr6O11, CeO2, Er2O3) and transition element oxide (MnO2). Mechanical properties (flexural strength, vickers hardness and fracture toughness) were tested. Microstructure was examined by scanning electron microscope(SEM), and the fracture model was analyzed. The range of flexural strength of the six kinds of tooth-like Y-TZP were (792 +/- 20)-(960 +/- 17) MPa, the fracture toughness were (4.72 +/- 0.31)-(5.64 +/- 0.38) MPam(1/2), and the vickers hardness were (1332 +/- 19)-(1380 +/- 17) MPa. SEM observation on the cross section of the six kinds of sintered composites showed a relatively dense polycrystal structure, and the fracture models was mixed type. Tooth-like Y-TZP is acquired with better mechanical properties (fracture toughness and vickers hardness) by adding rare earth oxide as colorants. It is available for clinical application.

The effect of heat treatments applied to superstructure porcelain on the mechanical properties and microstructure of lithium disilicate glass ceramics.

PubMed

Özdemir, Hatice; Özdoğan, Alper

2018-01-30

The aim of this study was to investigate that heat treatments with different numbers applied to superstructure porcelain whether effects microstructure and mechanical properties of lithium disilicate ceramic (LDC). Eighty disc-shaped specimens were fabricated from IPS e.max Press. Specimens were fired at heating values of porcelain in different numbers and divided four groups (n=5). Initial Vickers hardness were measured and X-ray diffraction (XRD) analysis was performed. Different surface treatment were applied and then Vickers hardness, surface roughness and environmental scanning electron microscopy (ESEM) analysis were performed. Data were analyzed with Varyans analysis and Tukey HSD test (α=0.05). Initial hardness among groups was no significant different (p>0.05), but hardness and surface roughness after surface treatments were significant different (p<0.05). Lithium disilicate (LD) peaks decrease depended on firing numbers. ESEM observations showed that firing number and surface treatments effect microstructure of LDC. Increasing firing numbers and surface treatments effect the microstructure of LDC.

Surface martensitization of Carbon steel using Arc Plasma Sintering

NASA Astrophysics Data System (ADS)

Wahyudi, Haris; Dimyati, Arbi; Sebayang, Darwin

2018-03-01

In this paper new technology of surface structure modification of steel by short plasma exposure in Arc Plasma Sintering (APS) device is presented. APS is an apparatus working based on plasma generated by DC pulsed current originally used for synthesizing materials via sintering and melting. Plasma exposure in APS was applied into the specimens for 1 and 3 seconds which generate temperature approximately about 1300-1500°C. The SUP9, pearlitic carbon steel samples were used. The hardness, hardening depth and microstructure of the specimens have been investigated by Vickers micro hardness test and Scanning Electron Microscopy (SEM) supported by Energy Dispersive X-Ray Spectroscopy (EDX). The results have showed that the mechanical property was significantly improved due to the formation of single martensitic structures as identified by SEM. The hardness of treated surface evaluated by Vickers hardness test showed significant improvement nearly three time from 190 VHN before to 524 VHN after treatment. Furthermore, EDX confirmed that the formation of martensite layer occurred without altering its composition. The APS also produced uniform hardened layer up to 250 μm. The experiment has demonstrated that arc plasma process was successfully improved the mechanical properties of steel in relatively very short time.

Preparation of graphite dispersed copper composite with intruding graphite particles in copper plate

NASA Astrophysics Data System (ADS)

Noor, Abdul Muizz Mohd; Ishikawa, Yoshikazu; Yokoyama, Seiji

2017-01-01

In this study, it was attempted that copper-graphite composite was prepared locally on the surface of a copper plate with using a spot welding machine. Experiments were carried out with changing the compressive load, the repetition number of the compression and the electrical current in order to study the effect of them on carbon content and Vickers hardness on the copper plate surface. When the graphite was pushed into copper plate only with the compressive load, the composite was mainly hardened by the work hardening. The Vickers hardness increased linearly with an increase in the carbon content. When an electrical current was energized through the composite at the compression, the copper around the graphite particles were heated to the temperature above approximately 2100 K and melted. The graphite particles partially or entirely dissolved into the melt. The graphite particles were precipitated from the melt under solidification. In addition, this high temperature caused the improvement of wetting of copper to graphite. This high temperature caused the annealing, and reduced the Vickers hardness. Even in this case, the Vickers hardness increased with an increase in the carbon content. This resulted from the dispersion hardening.

Influence of artificial saliva on abrasive wear and microhardness of dental composites filled with nanoparticles.

PubMed

Mayworm, Camila D; Camargo, Sérgio S; Bastian, Fernando L

2008-09-01

The aim of this study is to compare the wear resistance and hardness of two dental nanohybrid composites and to evaluate the influence of artificial saliva storage on those properties. Specimens were made from two commercial nanohybrid dental composites (Esthet-X-Dentsply and Filtek Supreme-3M). Abrasion tests were carried out in a ball-cratering machine (three body abrasion) and microscopic analysis of the wear surfaces was made using optical and scanning electron microscopy; hardness was quantified by Vickers hardness test. Those tests were repeated on specimens stored in artificial saliva. Results show that the wear rate of the studied materials is within 10(-7)mm(3)/Nmm range, one of the composites presenting wear rate twice as large as the other. After storage in artificial saliva, the wear resistance increases for both materials. Microhardness of the composites is around 52 and 64HV, Esthet-X presents higher hardness values than Filtek Supreme. After storage in artificial saliva, the microhardness of both materials decreases. Data were analyzed using ANOVA test, p < or = 0.05. Artificial saliva storage increases the materials' wear resistance, suggesting that in both materials bulk post-cure takes place and saliva absorption occurs only on the surface of the composites. This effect was confirmed by comparing the Vickers hardness before and after artificial saliva treatment and FTIR analyses. Surface microhardness of the composites decreases after storage in artificial saliva whereas bulk microhardness of the materials increases.

Microstructural characterization and strengthening behavior of nanometer sized carbides in Ti–Mo microalloyed steels during continuous cooling process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Chih-Yuan, E-mail: chen6563@gmail.com; Department of Materials Science and Engineering, National Taiwan University, Taipei 10617, Taiwan; Yang, Jer-Ren, E-mail: jryang@ntu.edu.tw

Nanometer-sized carbides that precipitated in a Ti–Mo bearing steel after interrupted continuous cooling in a temperature range of 620–700 °C with or without hot deformation were investigated by field-emission-gun transmission electron microscopy. The nanometer-sized carbides were identified as randomly homogeneous precipitation carbides and interphase precipitation carbides coexisting in the ferrite matrix. It is found that this dual precipitation morphology of carbides in the steel leads to the non-uniform mechanical properties of individual ferrite grains. Vickers hardness data mainly revealed that, in the specimens cooled at a rate of 0.5 °C/s without hot deformation, the range of Vickers hardness distribution wasmore » 230–340 HV 0.1 when cooling was interrupted at 680 °C, and 220–360 HV 0.1 when cooling was interrupted at 650 °C. For the specimens cooled at a rate of 0.5 °C/s with hot deformation, the range of Vickers hardness distribution was 290–360 HV 0.1 when cooling was interrupted at 680 °C, and 280–340 HV 0.1 when cooling was interrupted at 650 °C. Therefore, a narrower range of hardness distribution occurred in the specimens that underwent hot deformation and were then cooled with a lower interrupted cooling temperature. The uniform precipitation status in each ferrite grain can lead to ferrite grains with a narrower Vickers hardness distribution. On the other hand, interrupted cooling produced a maximum Vickers hardness of 320–330 HV 0.1 for the hot deformed specimens and 290–310 HV 0.1 for the non-deformed specimens with cooling interrupted in the temperature range of 660–670 °C. The maximum Vickers hardness obtained in such a temperature range can be ascribed to the full precipitation of the microalloying elements in the supersaturated ferrite matrix with a tiny size (~ 4–7 nm). - Highlight: • The interrupted continuous cooling temperatures were 620 °C to 700 °C. • Precipitation carbides with dual dispersed morphology coexisted in the matrix. • Heavy hot deformation narrowed the range of hardness distribution. • Full precipitation of nano-sized carbides achieved maximum hardening.« less

Tungsten tetraboride, an inexpensive superhard material

PubMed Central

Mohammadi, Reza; Lech, Andrew T.; Xie, Miao; Weaver, Beth E.; Yeung, Michael T.; Tolbert, Sarah H.; Kaner, Richard B.

2011-01-01

Tungsten tetraboride (WB4) is an interesting candidate as a less expensive member of the growing group of superhard transition metal borides. WB4 was successfully synthesized by arc melting from the elements. Characterization using powder X-ray diffraction (XRD) and energy-dispersive X-ray spectroscopy (EDX) indicates that the as-synthesized material is phase pure. The zero-pressure bulk modulus, as measured by high-pressure X-ray diffraction for WB4, is 339 GPa. Mechanical testing using microindentation gives a Vickers hardness of 43.3 ± 2.9 GPa under an applied load of 0.49 N. Various ratios of rhenium were added to WB4 in an attempt to increase hardness. With the addition of 1 at.% Re, the Vickers hardness increased to approximately 50 GPa at 0.49 N. Powders of tungsten tetraboride with and without 1 at.% Re addition are thermally stable up to approximately 400 °C in air as measured by thermal gravimetric analysis. PMID:21690363

Final report on COOMET Vickers PTB/VNIIFTRI key comparison (COOMET.M.H-K1.b and COOMET.M.H-K1.c)

NASA Astrophysics Data System (ADS)

Aslanyan, E.; Herrmann, K.

2013-01-01

This report describes a COOMET key comparison on Vickers hardness scales of two National Metrology Institutes—PTB and VNIIFTRI. The pilot laboratory was PTB, which was the linking institute with the key comparison reference values of CCM.H-K1. In the key comparison two sets of hardness reference blocks for the Vickers hardness scales HV1 and HV30, each consisting of three hardness reference blocks with the hardness levels 240 HV, 540 HV and 840 HV, are used. The same hardness reference blocks were used previously in the key comparison CCM.H-K1. The measurement results and uncertainty assessments, announced by VNIIFTRI, are in good agreement with the key comparison reference values of CCM.H-K1. Main text. To reach the main text of this paper, click on Final Report. Note that this text is that which appears in Appendix B of the BIPM key comparison database kcdb.bipm.org/. The final report has been peer-reviewed and approved for publication by the CCM, according to the provisions of the CIPM Mutual Recognition Arrangement (CIPM MRA).

Characterization of the Interface of an Alloy 625 Overlay on Steels Using Nanoindentation

NASA Astrophysics Data System (ADS)

Dai, Tao; Lippold, John

2018-06-01

Industry standards require postweld heat treatment (PWHT) to reduce the heat-affected zone hardness of steels such as F22 (2.25Cr-1Mo) and AISI 8630 overlaid (clad) with Alloy 625 weld metal. PWHT results in carbon diffusion and accumulation at the interface between the steel and overlay. The accumulation of carbon in a planar solidification growth zone adjacent to the fusion boundary results in high hardness and the potential for hydrogen-assisted cracking. The planar growth zone (PGZ) is so narrow that normal Vickers hardness testing cannot fully reveal the hardness distribution in this zone. This study focused on the application of nanoindentation to characterize the hardness in the narrow microstructural regions adjacent to the fusion boundary. The development of nanohardness maps revealed that the PGZ is not necessarily the region that exhibits peak hardness after PWHT. The highest hardness values were associated with clusters of M7C3 carbides in specific subregions in the PGZ and also in the partially-mixed zone adjacent to the fusion boundary or in steel "swirl" structures. It was also confirmed in this study that nanohardness has a linear correlation with Vickers hardness values. The results presented here provide new insight into the role of carbon diffusion during PWHT and its effect on interface embrittlement associated with Alloy 625 overlays on steel.

Applications of NTNU/SINTEF Drillability Indices in Hard Rock Tunneling

NASA Astrophysics Data System (ADS)

Zare, S.; Bruland, A.

2013-01-01

Drillability indices, i.e., the Drilling Rate Index™ (DRI), Bit Wear Index™ (BWI), Cutter Life Index™ (CLI), and Vickers Hardness Number Rock (VHNR), are indirect measures of rock drillability. These indices are recognized as providing practical characterization of rock properties used in the Norwegian University of Science and Technology (NTNU) time and cost prediction models available for hard rock tunneling and surface excavation. The tests form the foundation of various hard rock equipment capacity and performance prediction methods. In this paper, application of the tests for tunnel boring machine (TBM) and drill and blast (D&B) tunneling is investigated and the impact of the indices on excavation time and costs is presented.

Effect of Substrate Bias on Friction Coefficient, Adhesion Strength and Hardness of TiN-COATED Tool Steel

NASA Astrophysics Data System (ADS)

Hamzah, Esah; Ali, Mubarak; Toff, Mohd Radzi Hj. Mohd

In the present study, TiN coatings have been deposited on D2 tool steel substrates by using cathodic arc physical vapor deposition technique. The objective of this research work is to determine the usefulness of TiN coatings in order to improve the micro-Vickers hardness and friction coefficient of TiN coating deposited on D2 tool steel, which is widely used in tooling applications. A Pin-on-Disc test was carried out to study the coefficient of friction versus sliding distance of TiN coating deposited at various substrate biases. The standard deviation parameter during tribo-test result showed that the coating deposited at substrate bias of -75 V was the most stable coating. A significant increase in micro-Vickers hardness was recorded, when substrate bias was reduced from -150 V to zero. Scratch tester was used to compare the critical loads for coatings deposited at different bias voltages and the adhesion achievable was demonstrated with relevance to the various modes, scratch macroscopic analysis, critical load, acoustic emission and penetration depth. A considerable improvement in TiN coatings was observed as a function of various substrate bias voltages.

Physical properties and comparative strength of a bioactive luting cement.

PubMed

Jefferies, Steven; Lööf, Jesper; Pameijer, Cornelis H; Boston, Daniel; Galbraith, Colin; Hermansson, Leif

2013-01-01

New dental cement formulations require testing to determine physical and mechanical laboratory properties. To test an experimental calcium aluminate/glass-ionomer cement, Ceramir C and B (CC and B), regarding compressive strength (CS), film thickness (FT), net setting time (ST) and Vickers hardness. An additional test to evaluate potential dimensional change/expansion properties of this cement was also conducted. CS was measured according to a slightly modified ISO 9917:2003 for the CC and B specimens. The samples were not clamped while being exposed to relative humidity of great than 90 percent at 37 degrees C for 10 minutes before being stored in phosphate-buffered saline at 37 degrees C. For the CS, four groups were tested: Group 1-CC and B; Group 2-RelyX Luting Cement; Group 3-Fuji Plus; and Group 4-RelyX Unicem. Samples from all groups were stored for 24 hours before testing. Only CCandB was tested for ST and FT according to ISO 9917:2003. The FT was tested 2 minutes after mixing. Vickers hardness was evaluated using the CSM Microhardness Indentation Tester using zinc phosphate cement as a comparison material. Expansion testing included evaluating potential cracks in feldspathic porcelain jacket crowns (PJCs). The mean and standard deviation after 24 hours were expressed in MPa: Group 1 equals 160 plus or equal to 27; Group 2 equals 96 plus or equal to 10; Group 3 equals 138 plus or equal to 15; Group 4 equals 157 plus or equal to 10. A single-factor ANOVA demonstrated statistically significant differences between the groups (P less than 0.001). Pair-wise statistical comparison demonstrated a statistically significant difference between Groups 1 and 2. No statistically significant differences were found between other groups. The FT was 16.8 plus or equal to 0.9 and the ST was 4.8 plus or equal to 0.1 min. Vickers hardness for Ceramir C and B was 68.3 plus or equal to 17.2 and was statistically significantly higher (P less than 0.05) than Fleck's Zinc Phosphate cement at Vickers hardness of 51.4 plus or equal to 10. There was no evidence of cracks due to radial expansion in PJCs by the Ceramir C and B cement. All luting cements tested demonstrated compressive strengths well in excess of the ISO requirement for water-based cements of no less than 50 MPa. Ceramir C and B showed significantly higher CS than RelyX Luting Cement after 24 hours, but was not significantly higher than either Fuji Plus or RelyX Unicem. The ST and FT values of CC and B conform to and are within the boundaries of the requirements of the standard. Surface hardness was statistically higher than and comparable to zinc phosphate cement. There was no evidence of potentially clinically significant and deleterious expansion behavior by this cement. All cements tested demonstrated acceptable strength properties. Within the limits of this study, Ceramir C and B is deemed to possess physical properties suitable for a dental luting cement.

Theoretical Conversions of Different Hardness and Tensile Strength for Ductile Materials Based on Stress-Strain Curves

NASA Astrophysics Data System (ADS)

Chen, Hui; Cai, Li-Xun

2018-04-01

Based on the power-law stress-strain relation and equivalent energy principle, theoretical equations for converting between Brinell hardness (HB), Rockwell hardness (HR), and Vickers hardness (HV) were established. Combining the pre-existing relation between the tensile strength ( σ b ) and Hollomon parameters ( K, N), theoretical conversions between hardness (HB/HR/HV) and tensile strength ( σ b ) were obtained as well. In addition, to confirm the pre-existing σ b -( K, N) relation, a large number of uniaxial tensile tests were conducted in various ductile materials. Finally, to verify the theoretical conversions, plenty of statistical data listed in ASTM and ISO standards were adopted to test the robustness of the converting equations with various hardness and tensile strength. The results show that both hardness conversions and hardness-strength conversions calculated from the theoretical equations accord well with the standard data.

Processing and Testing Re2Si207 Matrix Composites (Preprint)

DTIC Science & Technology

2012-07-01

using the Archimedes method. 2.3. Indentation and Characterization The hardnesses of the sintered pellets were measured by Vickers indentation at...J. Mechanical Properties and Atomistic Deformation Mechanism of g-Y2Si2O7 from First- Principles Investigations. Acta mat. 55, 6019-6026 (2007). 10

Enamel microhardness and bond strengths of self-etching primer adhesives.

PubMed

Adebayo, Olabisi A; Burrow, Michael F; Tyas, Martin J; Adams, Geoffrey G; Collins, Marnie L

2010-04-01

The aim of this study was to determine the relationship between enamel surface microhardness and microshear bond strength (microSBS). Buccal and lingual mid-coronal enamel sections were prepared from 22 permanent human molars and divided into two groups, each comprising the buccal and lingual enamel from 11 teeth, to analyze two self-etching primer adhesives (Clearfil SE Bond and Tokuyama Bond Force). One-half of each enamel surface was tested using the Vickers hardness test with 10 indentations at 1 N and a 15-s dwell time. A hybrid resin composite was bonded to the other half of the enamel surface with the adhesive system assigned to the group. After 24 h of water storage of specimens at 37 degrees C, the microSBS test was carried out on a universal testing machine at a crosshead speed of 1 mm min(-1) until bond failure occurred. The mean microSBS was regressed on the mean Vickers hardness number (VHN) using a weighted regression analysis in order to explore the relationship between enamel hardness and microSBS. The weights used were the inverse of the variance of the microSBS means. Neither separate correlation analyses for each adhesive nor combined regression analyses showed a significant correlation between the VHN and the microSBS. These results suggest that the microSBS of the self-etch adhesive systems are not influenced by enamel surface microhardness.

Hardness - Yield Strength Relation of Al-Mg-Si Alloys

NASA Astrophysics Data System (ADS)

Praveen Sekhar, Aluru; Nandy, Supriya; Ray, Kalyan Kumar; Das, Debdulal

2018-03-01

Assessing the mechanical properties of materials through indentation hardness test is an attractive method, rather than obtaining the properties through destructive approach like tensile testing. The present work emphasizes on the relation between hardness and yield strength of Al-Mg-Si alloys considering Tabor type equations. Al-0.5Mg-0.4Si alloy has been artificially aged at various temperatures (100 to 250 °C) for different time durations (0.083 to 1000 h) and the ageing response has been assessed by measuring the Vickers hardness and yield strength. Correlations of the existing data from the open literature have also been reviewed. Lastly, it has been explained that the deviation in obtained relation from Tabor’s equation is owing to the dislocation accumulation during indentation.

Thermomechanical Properties of Sb2O3-TeO2-V2O5 Glassy Systems: Thermal Stability, Glass Forming Tendency and Vickers Hardness

NASA Astrophysics Data System (ADS)

Souri, Dariush; Torkashvand, Ziba

2017-04-01

Three-component 40TeO2-(60- x)V2O5- xSb2O3 glasses with 0 ≤ x ≤ 10 (in mol.%) were obtained by the rapid melt-quenching method. These glasses were studied with respect to some mechanical properties with the goal of obtaining information about their structure. The Vickers hardness test was employed to obtain Vickers micro-hardness ( H V) at two different loads, which was within the range of 13.187-17.557 GPa for a typical 0.1 HV (0.9807 N) load. In addition, theoretical micro-hardness ( H) was investigated and compared with experimental H V, showing the elevating trend with increase of Sb2O3 content, as for H V. Furthermore, differential scanning calorimetry (DSC) was employed within the range of 150-500°C at heating rates of φ = 3 K/min, 6 K/min, 9 K/min, 10 K/min, and 13 K/min. In this work, thermal stability ( T s = T cr - T x) and glass forming tendency ( K gl) were measured and reported for these glasses to determine the relationship between the chemical composition and the thermal stability, in order to interpret the structure of glass. Generally, from the ascertained outputs [analysis of mechanical data, titration study, the values of reduced fraction of vanadium ions ( C V) and oxygen molar volume ( V_{{O}}^{*} )], it was found that the micro-hardness had an increasing trend with increasing the Sb2O3 content. Among the studied glasses, the sample with x = 8 had a higher average micro-hardness value, the highest average thermal stability and glass forming tendency with respect to the other samples, which makes it a useful material (owning very good resistance against thermal attacks) for device manufacturing.

Good Biocompatibility and Sintering Properties of Zirconia Nanoparticles Synthesized via Vapor-phase Hydrolysis

PubMed Central

Wang, Jigang; Yin, Wenyan; He, Xiao; Wang, Qiang; Guo, Ming; Chen, Shaowei

2016-01-01

ZrO2 nanoparticles were synthesized by a vapor-phase hydrolysis process, and characterized in terms of crystalline structures, hardness and microstructures by X-ray diffraction, Vickers hardness test method, and atomic force microscopy (AFM) measurements. Moreover, in vitro cytotoxicity evaluation and hemolysis assay showed that the nanoparticles possessed good biocompatibility. Hardness investigations and AFM measurements indicated that both the sintering temperature and compression force played an important role in determining the physical behaviors (hardness, roughness and density) of flakes of the ZrO2 nanoparticles. When ZrO2 nanoparticles synthesized at 500 °C were pressed into flakes under 6 MPa and sintered at 1400 °C, the resulting flakes exhibited an optimal combination of hardness (534.58 gf·mm−2), roughness (0.07 μm) and density (4.41 g·cm−3). As the Vickers hardness value of human bones is of 315~535 gf·mm−2 and the density of adult femuris about 1.3~1.7 g·cm−3, the experimental results showed that the ZrO2 flakes were comparable to human bones with a higher density. As a result, the synthesized ZrO2 NPs may be useful for biomedical applications, especially for bone repair and replacement in future. PMID:27725744

Assessment of the hardness of different orthodontic wires and brackets produced by metal injection molding and conventional methods

PubMed Central

Alavi, Shiva; Kachuie, Marzie

2017-01-01

Background: This study was conducted to assess the hardness of orthodontic brackets produced by metal injection molding (MIM) and conventional methods and different orthodontic wires (stainless steel, nickel-titanium [Ni-Ti], and beta-titanium alloys) for better clinical results. Materials and Methods: A total of 15 specimens from each brand of orthodontic brackets and wires were examined. The brackets (Elite Opti-Mim which is produced by MIM process and Ultratrimm which is produced by conventional brazing method) and the wires (stainless steel, Ni-Ti, and beta-titanium) were embedded in epoxy resin, followed by grinding, polishing, and coating. Then, X-ray energy dispersive spectroscopy (EDS) microanalysis was applied to assess their elemental composition. The same specimen surfaces were repolished and used for Vickers microhardness assessment. Hardness was statistically analyzed with Kruskal–Wallis test, followed by Mann–Whitney test at the 0.05 level of significance. Results: The X-ray EDS analysis revealed different ferrous or co-based alloys in each bracket. The maximum mean hardness values of the wires were achieved for stainless steel (SS) (529.85 Vickers hardness [VHN]) versus the minimum values for beta-titanium (334.65 VHN). Among the brackets, Elite Opti-Mim exhibited significantly higher VHN values (262.66 VHN) compared to Ultratrimm (206.59 VHN). VHN values of wire alloys were significantly higher than those of the brackets. Conclusion: MIM orthodontic brackets exhibited hardness values much lower than those of SS orthodontic archwires and were more compatible with NiTi and beta-titanium archwires. A wide range of microhardness values has been reported for conventional orthodontic brackets and it should be considered that the manufacturing method might be only one of the factors affecting the mechanical properties of orthodontic brackets including hardness. PMID:28928783

Assessment of the hardness of different orthodontic wires and brackets produced by metal injection molding and conventional methods.

PubMed

Alavi, Shiva; Kachuie, Marzie

2017-01-01

This study was conducted to assess the hardness of orthodontic brackets produced by metal injection molding (MIM) and conventional methods and different orthodontic wires (stainless steel, nickel-titanium [Ni-Ti], and beta-titanium alloys) for better clinical results. A total of 15 specimens from each brand of orthodontic brackets and wires were examined. The brackets (Elite Opti-Mim which is produced by MIM process and Ultratrimm which is produced by conventional brazing method) and the wires (stainless steel, Ni-Ti, and beta-titanium) were embedded in epoxy resin, followed by grinding, polishing, and coating. Then, X-ray energy dispersive spectroscopy (EDS) microanalysis was applied to assess their elemental composition. The same specimen surfaces were repolished and used for Vickers microhardness assessment. Hardness was statistically analyzed with Kruskal-Wallis test, followed by Mann-Whitney test at the 0.05 level of significance. The X-ray EDS analysis revealed different ferrous or co-based alloys in each bracket. The maximum mean hardness values of the wires were achieved for stainless steel (SS) (529.85 Vickers hardness [VHN]) versus the minimum values for beta-titanium (334.65 VHN). Among the brackets, Elite Opti-Mim exhibited significantly higher VHN values (262.66 VHN) compared to Ultratrimm (206.59 VHN). VHN values of wire alloys were significantly higher than those of the brackets. MIM orthodontic brackets exhibited hardness values much lower than those of SS orthodontic archwires and were more compatible with NiTi and beta-titanium archwires. A wide range of microhardness values has been reported for conventional orthodontic brackets and it should be considered that the manufacturing method might be only one of the factors affecting the mechanical properties of orthodontic brackets including hardness.

Enhancement of the wear resistance and microhardness of aluminum alloy by Nd:YaG laser treatment.

PubMed

Hussein, Haitham T; Kadhim, Abdulhadi; Al-Amiery, Ahmed A; Kadhum, Abdul Amir H; Mohamad, Abu Bakar

2014-01-01

Influence of laser treatment on mechanical properties, wear resistance, and Vickers hardness of aluminum alloy was studied. The specimens were treated by using Nd:YaG laser of energy 780 mj, wavelength 512 nm, and duration time 8 ns. The wear behavior of the specimens was studied for all specimens before and after treatment by Nd:YaG laser and the dry wear experiments were carried out by sing pinon-disc technique. The specimens were machined as a disk with diameter of 25 mm and circular groove in depth of 3 mm. All specimens were conducted by scanning electron microscopy (SEM), energy-dispersive X-ray fluorescence analysis (EDS), optical microscopy, and Vickers hardness. The results showed that the dry wear rate was decreased after laser hardening and increased Vickers hardness values by ratio of 2.4:1. The results showed that the values of wear rate for samples having circular grooves are less than samples without grooves after laser treatment.

[The design of Co-Cr-Mo alloy combining the framework with porcelain fused to metal restorations and determination of the mechanical properties].

PubMed

Chao, Yong-lie; Lui, Chang-hong; Li, Ning; Yang, Xiao-yu

2005-02-01

To investigate a kind of Co-Cr-Mo alloys used for both porcelain fused to metal (PFM) restorations and casting framework of removable partial dentures. The Co-Cr-Mo alloy underwent the design for elementary compositions of the alloys and the production from the raw materials by means of a vacuum melt furnace. The strength, hardness, plasticity and casting ability of the alloy were examined with metal tensile test. Vickers hardness test and grid casting were examined respectively. The microstructure of the Co-Cr-Mo alloy was also inspected by scanning electron microscope and X-ray diffraction analysis. The elementary composition of DA9-4 alloy mainly consisted of Co 54%-67%, Cr 21%-26%, Mo 5%-8%, W 5%-8%, Si 1%-3%, Mn 0.1%-0.25% and trace elements. The yield strength of the alloy was 584 MPa, while the tensile strength was 736 MPa. The coefficient of expansion was 15.0%, the Vickers hardness reached 322, and the casting ratio exibited 100%. The DA9-4 Co-Cr-Mo alloy used for PFM and framework shown in this paper can meet the clinical demands and have reached the objects of the experiment plan.

Evaluation of pristine and Eu ₂O₃-added MgB ₂ ceramics for medical applications: hardness, corrosion resistance, cytotoxicity and antibacterial activity.

PubMed

Batalu, Dan; Stanciuc, Ana Maria; Moldovan, Lucia; Aldica, Gheorghe; Badica, Petre

2014-09-01

Nano- or micropowders of Eu2O3 were added to MgB2, resulting in a composition of (MgB2)0.975(EuO1.5)0.025. Pristine and doped samples were prepared using spark plasma sintering and tested for (i) Vickers hardness, (ii) pH evolution in phosphate-buffered saline solution, (iii) corrosion resistance (Tafel polarization curves), (iv) cytotoxicity (in vitro tests), and (v) antibacterial activity. Eu2O3 addition influenced the investigated properties. Solutions of MgB2-based samples show a relatively high saturation pH of 8.5. This value is lower than that of solutions incubated with Mg or other Mg-based biodegradable alloys reported in the literature. MgB2-based samples have lower electro-corrosion rates than Mg. Their Vickers hardness is 6.8-10.2GPa, and these values are higher than those of biodegradable Mg-based alloys. MgB2 has low in vitro biocompatibility, good antibacterial activity against Escherichia coli, and mild activity against Staphylococcus aureus. Our results suggest that MgB2-based materials deserve attention in biomedical applications, such as implants or sterile medical instruments. Copyright © 2014 Elsevier B.V. All rights reserved.

Y-TZP ceramic processing from coprecipitated powders: a comparative study with three commercial dental ceramics.

PubMed

Lazar, Dolores R R; Bottino, Marco C; Ozcan, Mutlu; Valandro, Luiz Felipe; Amaral, Regina; Ussui, Valter; Bressiani, Ana H A

2008-12-01

(1) To synthesize 3mol% yttria-stabilized zirconia (3Y-TZP) powders via coprecipitation route, (2) to obtain zirconia ceramic specimens, analyze surface characteristics, and mechanical properties, and (3) to compare the processed material with three reinforced dental ceramics. A coprecipitation route was used to synthesize a 3mol% yttria-stabilized zirconia ceramic processed by uniaxial compaction and pressureless sintering. Commercially available alumina or alumina/zirconia ceramics, namely Procera AllCeram (PA), In-Ceram Zirconia Block (CAZ) and In-Ceram Zirconia (IZ) were chosen for comparison. All specimens (6mmx5mmx5mm) were polished and ultrasonically cleaned. Qualitative phase analysis was performed by XRD and apparent densities were measured on the basis of Archimedes principle. Ceramics were also characterized using SEM, TEM and EDS. The hardness measurements were made employing Vickers hardness test. Fracture toughness (K(IC)) was calculated. Data were analyzed using one-way analysis of variance (ANOVA) and Tukey's test (alpha=0.05). ANOVA revealed that the Vickers hardness (p<0.0001) and fracture toughness (p<0.0001) were affected by the ceramic materials composition. It was confirmed that the PA ceramic was constituted of a rhombohedral alumina matrix, so-called alpha-alumina. Both CAZ and IZ ceramics presented tetragonal zirconia and alpha-alumina mixture of phases. The SEM/EDS analysis confirmed the presence of aluminum in PA ceramic. In the IZ and CAZ ceramics aluminum, zirconium and cerium in grains involved by a second phase containing aluminum, silicon and lanthanum were identified. PA showed significantly higher mean Vickers hardness values (H(V)) (18.4+/-0.5GPa) compared to vitreous CAZ (10.3+/-0.2GPa) and IZ (10.6+/-0.4GPa) ceramics. Experimental Y-TZP showed significantly lower results than that of the other monophased ceramic (PA) (p<0.05) but it showed significantly higher fracture toughness (6.0+/-0.2MPam(1/2)) values when compared to the other tested ceramics (p<0.05). The coprecipitation method used to synthesize zirconia powders and the adopted ceramic processing conditions led to ceramics with mechanical properties comparable to commercially available reinforced ceramic materials.

Metallographic structure and hardness of titanium orthodontic brackets.

PubMed

Zinelis, Spiros; Annousaki, Olga; Eliades, Theodore; Makou, Margarita

2003-11-01

To determine the elemental composition, microstructure, and hardness of two different brands of titanium (Ti) orthodontic brackets. Four specimens of each brand were embedded in epoxy resin and, after metallographic grinding and polishing, were studied under a metallographic microscope. The bonding base morphology of each bracket was studied in as-received brackets by scanning electron microscopy. Energy dispersive x-ray microanalysis (EDS) was used on polished specimens to assess the elemental composition of base and wing bracket components, and the brackets were subjected to metallographic etching to reveal the metallurgical structure. The same specimen surfaces were used for assessment of the Vickers hardness. The results were statistically analyzed by two-way analysis of variance (ANOVA) with the bracket brand and bracket region (base, wing) serving as discriminating variables, whilst further group differences were investigated with Tukey's multiple comparison test at the alpha = 0.05 level of significance. Metallographic imaging revealed that the Orthos2 brackets (Ormco, Glendora, CA, USA) consist of two parts joined together by laser welding, with large gaps along the base wing interface, whereas Rematitan brackets (Dentaurum, Ispringen, Germany) are single-piece appliances. Ti was the only element identified in Rematitan and Orthos2 base materials, while aluminium (Al) and vanadium (V) were also found in the Orthos2 wing component. Metallographic analysis showed the presence of a + b phase for Orthos2 and plate-like grains for Rematitan. The results of the Vickers hardness testing were: Orthos2 (wing): 371 +/- 22, Rematitan (wing): 272 +/- 4, Rematitan (base): 271 +/- 16, Orthos2 (base): 165 +/- 2. The findings of the present study suggest that there are significant differences in composition, microstructure and hardness between the two commercial types of Ti brackets tested; the clinical implications of the findings are discussed.

Changes in Vickers hardness during the decomposition of bone: Possibilities for forensic anthropology.

PubMed

Walden, Steven J; Evans, Sam L; Mulville, Jacqui

2017-01-01

The purpose of this study was to determine how the Vickers hardness (HV) of bone varies during soft tissue putrefaction. This has possible forensic applications, notably for determining the postmortem interval. Experimental porcine bone samples were decomposed in surface and burial deposition scenarios over a period of 6 months. Although the Vickers hardness varied widely, it was found that when transverse axial hardness was subtracted from longitudinal axial hardness, the difference showed correlations with three distinct phases of soft tissue putrefaction. The ratio of transverse axial hardness to longitudinal axial hardness showed a similar correlation. A difference of 10 or greater in HV with soft tissue present and signs of minimal decomposition, was associated with a decomposition period of 250 cumulative cooling degree days or less. A difference of 10 (+/- standard error of mean at a 95% confidence interval) or greater in HV associated with marked decomposition indicated a decomposition period of 1450 cumulative cooling degree days or more. A difference of -7 to +8 (+/- standard error of mean at a 95% confidence interval) was thus associated with 250 to 1450 cumulative cooling degree days' decomposition. The ratio of transverse axial HV to longitudinal HV, ranging from 2.42 to 1.54, is a more reliable indicator in this context and is preferable to using negative integers These differences may have potential as an indicator of postmortem interval and thus the time of body deposition in the forensic context. Crown Copyright © 2016. Published by Elsevier Ltd. All rights reserved.

Effect of five commercial mouth rinses on the microhardness of a nanofilled resin composite restorative material: An in vitro study

PubMed Central

Jyothi, KN; Crasta, Shanol; Venugopal, P

2012-01-01

Aim and Objectives: This in vitro study was designed to comparatively evaluate the effect of five commercial mouth rinses on the micro hardness of a nanofilled resin based restorative material. Materials and Methods: Fifty specimens of resin composite material (Filtek Z350XT, 3M ESPE, St.Paul, MN USA) were prepared and immersed in artificial saliva for 24 h. The base line micro hardness of specimens was recorded using Vicker's micro hardness tester (MMT – X7 Matsuzawa, Japan). The specimens were randomly distributed into five groups, each containing 10 specimens (n=10) as follows – Group I Listerine (alcohol based), Group II Periogard (alcohol based), Group III Colgate plax (alcohol based), Group IV C- prev (alcohol free), Group V Hiora(alcohol free). The specimens were immersed in 20 ml of mouth rinses and incubated for 24 h at 37°C. The post immersion micro hardness values of the specimens were recorded and the data was tabulated for statistical analysis. Kruskal–Wallis test was used for inter group comparison followed by pair wise comparison of groups using Mann–Whitney U test. The level of significance was set at P=0.05. Results: Significant reduction in the mean VHN (Vicker's micro hardness number) was observed in all the groups after exposure to the tested mouth rinses (P<0.01) and the reduction in mean VHN values were as follows: Group I 12.09, Group II 3.42, Group II 1.51, Group IV 1.03, Group V 0.57. Inter group comparison showed statistically significant reduction in micro hardness in Groups I and II compared to all other groups with P<0.001. There was no significant difference between Groups III, IV and V. Conclusion: All the mouth rinses showed a reduction in the microhardness of nanofilled resin composite material with listerine (Group I) containing maximum amount of alcohol, showing highest reduction in micro hardness value. PMID:22876004

Effect of Three Clinical Curing Treatments on Fluoride Release and Surface Hardness of Glass-Ionomer Cements.

PubMed

Dionysopoulos, Dimitrios; Tolidis, Kosmas; Gerasimou, Paris; Sfeikos, Thrasyvoulos

The purpose of this study was to investigate the effect of radiant heat, ultrasonic treatment, and 42.7 wt% CaCl₂ solution on fluoride release and surface hardness in three conventional glass-ionomer cements (GICs). The fluoride release patterns of each GIC were evaluated during a 28-day period using a fluoride ion-selective electrode. The surface hardness of the tested GICs was evaluated 24 hours after preparation of the specimens using Vickers hardness test. Statistical analysis of the data was made using analysis of variance and Bonferroni post hoc test (α = .05). Radiant heat, ultrasonic, and CaCl₂ solution treatments reduced fluoride release and increased the surface hardness of the tested GICs (P < .05). Among the tested GICs, differences in fluoride release and surface hardness were observed (P < .05). The clinical treatments investigated may be effective methods for improving the setting reaction of GICs and may achieve sufficient initial mechanical properties earlier. Although a reduction in fluoride release occurs after the treatments, anticariogenic properties of the GICs may not be significantly affected.

Estimation of Vickers hardness uncertainty for a heterogeneous welded joint (S235JR+AR and X2CrNiMo17-12-2)

NASA Astrophysics Data System (ADS)

Dijmărescu, M. C.; Dijmărescu, M. R.

2017-08-01

When talking about tests that include measurements, the uncertainty of measurement is an essential element because it is important to know the limits within the obtained results may be assumed to lie and the influence the measurement technological system elements have on these results. The research presented in this paper focuses on the estimation of the Vickers hardness uncertainty of measurement for the heterogeneous welded joint between S235JR+AR and X2CrNiMo17-12-2 materials in order to establish the results relevance and the quality assessment of this joint. The paper contents are structured in three main parts. In the first part, the initial data necessary for the experiment is presented in terms of the welded joint and technological means characterisation. The second part presents the physical experiment development and its results and in the third part the uncertainty of the measurements is calculated and a results discussion is undertaken.

Enhancement of the Wear Resistance and Microhardness of Aluminum Alloy by Nd:YaG Laser Treatment

PubMed Central

Hussein, Haitham T.; Kadhim, Abdulhadi; Al-Amiery, Ahmed A.; Kadhum, Abdul Amir H.; Mohamad, Abu Bakar

2014-01-01

Influence of laser treatment on mechanical properties, wear resistance, and Vickers hardness of aluminum alloy was studied. The specimens were treated by using Nd:YaG laser of energy 780 mj, wavelength 512 nm, and duration time 8 ns. The wear behavior of the specimens was studied for all specimens before and after treatment by Nd:YaG laser and the dry wear experiments were carried out by sing pinon-disc technique. The specimens were machined as a disk with diameter of 25 mm and circular groove in depth of 3 mm. All specimens were conducted by scanning electron microscopy (SEM), energy-dispersive X-ray florescence analysis (EDS), optical microscopy, and Vickers hardness. The results showed that the dry wear rate was decreased after laser hardening and increased Vickers hardness values by ratio of 2.4 : 1. The results showed that the values of wear rate for samples having circular grooves are less than samples without grooves after laser treatment. PMID:25136694

Sintering Behavior of Spark Plasma Sintered SiC with Si-SiC Composite Nanoparticles Prepared by Thermal DC Plasma Process

NASA Astrophysics Data System (ADS)

Yu, Yeon-Tae; Naik, Gautam Kumar; Lim, Young-Bin; Yoon, Jeong-Mo

2017-11-01

The Si-coated SiC (Si-SiC) composite nanoparticle was prepared by non-transferred arc thermal plasma processing of solid-state synthesized SiC powder and was used as a sintering additive for SiC ceramic formation. Sintered SiC pellet was prepared by spark plasma sintering (SPS) process, and the effect of nano-sized Si-SiC composite particles on the sintering behavior of micron-sized SiC powder was investigated. The mixing ratio of Si-SiC composite nanoparticle to micron-sized SiC was optimized to 10 wt%. Vicker's hardness and relative density was increased with increasing sintering temperature and holding time. The relative density and Vicker's hardness was further increased by reaction bonding using additional activated carbon to the mixture of micron-sized SiC and nano-sized Si-SiC. The maximum relative density (97.1%) and Vicker's hardness (31.4 GPa) were recorded at 1800 °C sintering temperature for 1 min holding time, when 0.2 wt% additional activated carbon was added to the mixture of SiC/Si-SiC.

Metrological Characterization of the Vickers Hardness Primary Standard Machine Established at CSIR-NPL

NASA Astrophysics Data System (ADS)

Titus, S. Seelakumar; Vikram; Girish; Jain, Sushil Kumar

2018-06-01

CSIR-National Physical Laboratory (CSIR-NPL) is the National Metrological Institute (NMI) of India, which has the mandate for the realization of SI units of measurements and dissemination of the same to the user organizations. CSIR-NPL has established a hardness standardizing machine for realizing the Vickers hardness scale as per ISO 6507-3 standard for providing national traceability in hardness measurement. Direct verification of the machine has been carried out by measuring the uncertainty in the generated force, the indenter geometry and the indentation measuring system. From these measurements, it is found that the machine exhibits a calibration and measurement capability (CMC) of ±1.5% for HV1-HV3 scales and ±1.0% for HV5-HV50 scales and ±0.8% for HV100 scale.

A comparative evaluation of effect of modern-curing lights and curing modes on conventional and novel-resin monomers

PubMed Central

Roy, Konda Karthik; Kumar, Kanumuru Pavan; John, Gijo; Sooraparaju, Sujatha Gopal; Nujella, Surya Kumari; Sowmya, Kyatham

2018-01-01

Aim: The aim of this study is to compare and to evaluate effect of curing light and curing modes on the nanohybrid composite resins with conventional Bis-GMA and novel tricyclodecane (TCD) monomers. Methodology: Two nanohybrid composites, IPS empress direct and charisma diamond were used in this study. Light-emitting diode (LED)-curing unit and quartz-tungsten-halogen (QTH)-curing unit which were operated into two different modes: continuous and soft start. Based on the composite resin, curing lights, and mode of curing used, the samples were divided into 8 groups. After polymerization, the samples were stored for 48 h in complete darkness at 37°C and 100% humidity. The Vickers hardness (VK) of the surface was determined with Vickers indenter by the application of 200 g for 15 s. Three VK readings were recorded for each sample surface both on top and bottom surfaces. For all the specimens, the three hardness values for each surface were averaged and reported as a single value. The mean VK and hardness ratio were calculated. The depth of cure was assessed based on the hardness ratio. Results: Comparison of mean hardness values and hardness ratios was done using ANOVA with post hoc Tukey's test. Conclusion: Both QTH- and LED-curing units had shown the adequate depth of cure. Soft-start-curing mode in both QTH- and LED-curing lights had effectively increased microhardness than the continuous mode of curing. TCD monomer had shown higher hardness values compared with conventional Bis-GMA-containing resin. PMID:29628651

Mechanical properties of Al-Cu alloy-SiC composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Anggara, B. S., E-mail: anggorobs1960@yahoo.com; Handoko, E.; Soegijono, B.

The synthesis of aluminum (Al) alloys, Al-Cu, from mixture 96.2 % Al and 3.8 % Cu has been prepared by melting process at a temperature of 1200°C. The adding 12.5 wt% up to 20 wt% of SiC on Al-Cu alloys samples has been investigated. The structure analyses were examined by X-Ray Diffractometer (XRD) and scanning electron microscope (SEM). Moreover, the morphology of Al-Cu alloys has been seen as structure in micrometer range. The hardness was measured by hardness Vickers method. According to the results, it can be assumed that the 15 wt% of SiC content is prefer content to getmore » better quality of back to back hardness Vickers of Al-Cu alloys.« less

Mechanical properties of Al-Cu alloy-SiC composites

NASA Astrophysics Data System (ADS)

Anggara, B. S.; Handoko, E.; Soegijono, B.

2014-09-01

The synthesis of aluminum (Al) alloys, Al-Cu, from mixture 96.2 % Al and 3.8 % Cu has been prepared by melting process at a temperature of 1200°C. The adding 12.5 wt% up to 20 wt% of SiC on Al-Cu alloys samples has been investigated. The structure analyses were examined by X-Ray Diffractometer (XRD) and scanning electron microscope (SEM). Moreover, the morphology of Al-Cu alloys has been seen as structure in micrometer range. The hardness was measured by hardness Vickers method. According to the results, it can be assumed that the 15 wt% of SiC content is prefer content to get better quality of back to back hardness Vickers of Al-Cu alloys.

Preparation and characterization of Al{sub 2}O{sub 3}-Ti{sub 3}SiC{sub 2} composites and its functionally graded materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Luo Yongming; Li Shuqin; Chen Jian

2003-01-01

Alumina/titanium silicon carbide (Al{sub 2}O{sub 3}-Ti{sub 3}SiC{sub 2}) composites and its functionally graded materials (FGMs) were fabricated by a powder metallurgy processes and their microstructure and properties were investigated, respectively. The experimental results showed that the Vickers hardness of composites decreased with increasing Ti{sub 3}SiC{sub 2} content while the fracture toughness and strength exhibited the opposite trend. Minimum Vickers hardness (4 GPa), maximum strength (598 MPa) and maximum toughness (11.24 MPa m{sup 1/2}) were reached in the pure Ti{sub 3}SiC{sub 2} material. Strength and hardness of FGMs were evaluated. Observation using an scanning electron microscope (SEM) indicated that the presencemore » of Ti{sub 3}SiC{sub 2} of FGMs inhibited the growth of alumina grains through a pinning mechanism. The study shows that the combination of the layered Ti{sub 3}SiC{sub 2} structure and the fine alumina grains can result in a Al{sub 2}O{sub 3}-Ti{sub 3}SiC{sub 2} composites possessing a high toughness and low Vickers hardness without a sacrifice in the strength.« less

Mechanical Properties of Calcium Fluoride-Based Composite Materials

PubMed Central

Kleczewska, Joanna; Pryliński, Mariusz; Podlewska, Magdalena; Sokołowski, Jerzy; Łapińska, Barbara

2016-01-01

Aim of the study was to evaluate mechanical properties of light-curing composite materials modified with the addition of calcium fluoride. The study used one experimental light-curing composite material (ECM) and one commercially available flowable light-curing composite material (FA) that were modified with 0.5–5.0 wt% anhydrous calcium fluoride. Morphology of the samples and uniformity of CaF2 distribution were analyzed using Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS). Mechanical properties were tested after 24-hour storage of specimens in dry or wet conditions. Stored dry ECM enriched with 0.5–1.0 wt% CaF2 showed higher tensile strength values, while water storage of all modified ECM specimens decreased their tensile strength. The highest Vickers hardness tested after dry storage was observed for 2.5 wt% CaF2 content in ECM. The addition of 2.0–5.0 wt% CaF2 to FA caused significant decrease in tensile strength after dry storage and overall tensile strength decrease of modified FA specimens after water storage. The content of 2.0 wt% CaF2 in FA resulted in the highest Vickers hardness tested after wet storage. Commercially available composite material (FA), unmodified with fluoride addition, demonstrated overall significantly higher mechanical properties. PMID:28004001

Evaluation of Polymerization Efficacy in Composite Resins via FT-IR Spectroscopy and Vickers Microhardness Test.

PubMed

Jafarzadeh, Tahereh-Sadat; Erfan, Mohammad; Behroozibakhsh, Marjan; Fatemi, Mostafa; Masaeli, Reza; Rezaei, Yashar; Bagheri, Hossein; Erfan, Yasaman

2015-01-01

Background and aims. Polymerization efficacy affects the properties and performance of composite resin restorations.The purpose of this study was to evaluate the effectiveness of polymerization of two micro-hybrid, two nano-hybrid and one nano-filled ormocer-based composite resins, cured by two different light-curing systems, using Fourier transformation infrared (FT-IR) spectroscopy and Vickers microhardness testing at two different depths (top surface, 2 mm). Materials and methods. For FT-IR spectrometry, five cylindrical specimens (5mm in diameter × 2 mm in length) were prepared from each composite resin using Teflon molds and polymerized for 20 seconds. Then, 70-μm wafers were sectioned at the top surface and at2mm from the top surface. The degree of conversion for each sample was calculated using FT-IR spectroscopy. For Vickers micro-hardness testing, three cylindrical specimens were prepared from each composite resin and polymerized for 20 seconds. The Vickers microhardness test (Shimadzu, Type M, Japan) was performed at the top and bottom (depth=2 mm) surfaces of each specimen. Three-way ANOVA with independent variables and Tukey tests were performed at 95% significance level. Results. No significant differences were detected in degree of conversion and microhardness between LED and QTH light-curing units except for the ormocer-based specimen, CeramX, which exhibited significantly higher DC by LED. All the composite resins showed a significantly higher degree of conversion at the surface. Microhardness was not significantly affected by depth, except for Herculite XRV Ultra and CeramX, which showed higher values at the surface. Conclusion. Composite resins containing nano-particles generally exhibited more variations in degree of conversion and microhardness.

Evaluation of Polymerization Efficacy in Composite Resins via FT-IR Spectroscopy and Vickers Microhardness Test

PubMed Central

Jafarzadeh, Tahereh-Sadat; Erfan, Mohammad; Behroozibakhsh, Marjan; Fatemi, Mostafa; Masaeli, Reza; Rezaei, Yashar; Bagheri, Hossein; Erfan, Yasaman

2015-01-01

Background and aims. Polymerization efficacy affects the properties and performance of composite resin restorations.The purpose of this study was to evaluate the effectiveness of polymerization of two micro-hybrid, two nano-hybrid and one nano-filled ormocer-based composite resins, cured by two different light-curing systems, using Fourier transformation infrared (FT-IR) spectroscopy and Vickers microhardness testing at two different depths (top surface, 2 mm). Materials and methods. For FT-IR spectrometry, five cylindrical specimens (5mm in diameter × 2 mm in length) were prepared from each composite resin using Teflon molds and polymerized for 20 seconds. Then, 70-μm wafers were sectioned at the top surface and at2mm from the top surface. The degree of conversion for each sample was calculated using FT-IR spectroscopy. For Vickers micro-hardness testing, three cylindrical specimens were prepared from each composite resin and polymerized for 20 seconds. The Vickers microhardness test (Shimadzu, Type M, Japan) was performed at the top and bottom (depth=2 mm) surfaces of each specimen. Three-way ANOVA with independent variables and Tukey tests were performed at 95% significance level. Results. No significant differences were detected in degree of conversion and microhardness between LED and QTH light-curing units except for the ormocer-based specimen, CeramX, which exhibited significantly higher DC by LED. All the composite resins showed a significantly higher degree of conversion at the surface. Microhardness was not significantly affected by depth, except for Herculite XRV Ultra and CeramX, which showed higher values at the surface. Conclusion. Composite resins containing nano-particles generally exhibited more variations in degree of conversion and microhardness. PMID:26889359

Depth of cure of resin composites: is the ISO 4049 method suitable for bulk fill materials?

PubMed

Flury, Simon; Hayoz, Stefanie; Peutzfeldt, Anne; Hüsler, Jürg; Lussi, Adrian

2012-05-01

To evaluate if depth of cure D(ISO) determined by the ISO 4049 method is accurately reflected with bulk fill materials when compared to depth of cure D(new) determined by Vickers microhardness profiles. D(ISO) was determined according to "ISO 4049; Depth of cure" and resin composite specimens (n=6 per group) were prepared of two control materials (Filtek Supreme Plus, Filtek Silorane) and four bulk fill materials (Surefil SDR, Venus Bulk Fill, Quixfil, Tetric EvoCeram Bulk Fill) and light-cured for either 10s or 20s. For D(new), a mold was filled with one of the six resin composites and light-cured for either 10 s or 20 s (n=22 per group). The mold was placed under a microhardness indentation device and hardness measurements (Vickers hardness, VHN) were made at defined distances, beginning at the resin composite that had been closest to the light-curing unit (i.e. at the "top") and proceeding toward the uncured resin composite (i.e. toward the "bottom"). On the basis of the VHN measurements, Vickers hardness profiles were generated for each group. D(ISO) varied between 1.76 and 6.49 mm with the bulk fill materials showing the highest D(ISO). D(new) varied between 0.2 and 4.0 mm. D(new) was smaller than D(ISO) for all resin composites except Filtek Silorane. For bulk fill materials the ISO 4049 method overestimated depth of cure compared to depth of cure determined by Vickers hardness profiles. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of polymerization technique and glass fiber addition on the surface roughness and hardness of PMMA denture base material.

PubMed

Gad, Mohammed M; Rahoma, Ahmed; Al-Thobity, Ahmad M

2018-06-20

The current study evaluated the effects of autoclave polymerization both with and without glass fiber (GF) reinforcement on the surface roughness and hardness of acrylic denture base material. Ninety disc specimens (30×2.5 mm) were prepared from Vertex resin and divided according to polymerization techniques into a water bath, short and long autoclave polymerization groups. Tested groups were divided into three subgroups according to the GF concentration (0, 2.5, and 5 wt%). Profilometer and Vickers hardness tests were performed to measure surface roughness and hardness. ANOVA and Tukey-Kramer multiple comparison tests analyzed the results, and p≤0.05 was considered statistically significant. Autoclave polymerization significantly decreased the surface roughness and increased the hardness of acrylic resin without GF reinforcement (p<0.05). However, 5 wt% GF addition significantly increased surface roughness and decreased hardness of the autoclave polymerized denture base resin (p<0.05). Surface properties of Polymethyl methacrylate (PMMA) denture base material improved with autoclave polymerization and negatively affected with GFs addition.

Low temperature method for the production of calcium phosphate fillers

PubMed Central

Calafiori, Anna Rita; Marotta, Marcello; Nastro, Alfonso; Martino, Guglielmo

2004-01-01

Background Calcium phosphate manufactured samples, prepared with hydroxyapatite, are used as either spacers or fillers in orthopedic surgery, but these implants have never been used under conditions of mechanical stress. Similar conditions also apply with cements. Many authors have postulated that cements are a useful substitute material when implanted in vivo. The aim of this research is to develop a low cristalline material similar to bone in porosity and cristallinity. Methods Commercial hydroxyapatite (HAp) and monetite (M) powders are mixed with water and compacted to produce cylindrical samples. The material is processed at a temperature of 37–120 degrees C in saturated steam to obtain samples that are osteoconductive. The samples are studied by X-ray powder diffraction (XRD), Vickers hardness test (HV), scanning electron microscopy (SEM), and porosity evaluation. Results The X-ray diffractions of powders from the samples show patterns typical of HAp and M powders. After thermal treatment, no new crystal phase is formed and no increase of the relative intensity of the peaks is obtained. Vicker hardness data do not show any relationship with treatment temperature. The total porosity decreases by 50–60% according to the specific thermal treatment. Scanning electron microscopy of the surfaces of the samples with either HAp 80%-M 20% (c) or Hap 50%-M 50% (f), show cohesion of the powder grains. Conclusions The dissolution-reprecipitation process is more intesive in manufactured samples (c) and (f), according to Vickers hardness data. The process occurs in a steam saturated environment between 37 degrees and 120 degrees C. (c) (f) manufactured samples show pore dimension distributions useful to cellular repopulation in living tissues. PMID:15035671

Sintering Behavior of Spark Plasma Sintered SiC with Si-SiC Composite Nanoparticles Prepared by Thermal DC Plasma Process.

PubMed

Yu, Yeon-Tae; Naik, Gautam Kumar; Lim, Young-Bin; Yoon, Jeong-Mo

2017-11-25

The Si-coated SiC (Si-SiC) composite nanoparticle was prepared by non-transferred arc thermal plasma processing of solid-state synthesized SiC powder and was used as a sintering additive for SiC ceramic formation. Sintered SiC pellet was prepared by spark plasma sintering (SPS) process, and the effect of nano-sized Si-SiC composite particles on the sintering behavior of micron-sized SiC powder was investigated. The mixing ratio of Si-SiC composite nanoparticle to micron-sized SiC was optimized to 10 wt%. Vicker's hardness and relative density was increased with increasing sintering temperature and holding time. The relative density and Vicker's hardness was further increased by reaction bonding using additional activated carbon to the mixture of micron-sized SiC and nano-sized Si-SiC. The maximum relative density (97.1%) and Vicker's hardness (31.4 GPa) were recorded at 1800 °C sintering temperature for 1 min holding time, when 0.2 wt% additional activated carbon was added to the mixture of SiC/Si-SiC.

Microhardness of light- and dual-polymerizable luting resins polymerized through 7.5-mm-thick endocrowns.

PubMed

Gregor, Ladislav; Bouillaguet, Serge; Onisor, Ioana; Ardu, Stefano; Krejci, Ivo; Rocca, Giovanni Tommaso

2014-10-01

The complete polymerization of luting resins through thick indirect restorations is still questioned. The purpose of this study was to evaluate the degree of polymerization of light- and dual-polymerizable luting resins under thick indirect composite resin and ceramic endocrowns by means of Vickers microhardness measurements. The Vickers microhardness measurements of a light-polymerizable microhybrid composite resin and a dual-polymerizable luting cement directly polymerized in a natural tooth mold for 40 seconds with a high-power light-emitting diode lamp (control) were compared with measurements after indirect irradiation through 7.5-mm-thick composite resin and ceramic endocrowns for 3 × 90 seconds. A test-to-control microhardness values ratio of 0.80 at a depth of 0.5 mm below the surface was assumed as the criterion for adequate conversion. For the Vickers microhardness measurements of a dual-polymerizable luting cement, no differences (P>.05) were found between Vickers microhardness control values and values reported after polymerization through composite resin and ceramic endocrowns. For The Vickers microhardness measurements (±SD) of a light-polymerizable microhybrid composite resin, control values were significantly (P<.05) higher (111 ±3.3) than those reported after polymerization through composite resin (100.5 ±3.8) and ceramic (99.7 ±2.3) endocrowns. However, the hardness values of The Vickers microhardness measurements of a light-polymerizable microhybrid composite resin polymerized through the endocrowns were approximately 10% to 12% lower than those of the control values. Two-way ANOVA showed the influence of the luting material on the Vickers microhardness values (P<.05). The effect of endocrown material was not significant (P>.05). Under the conditions of this in vitro study, Vickers microhardness values of the dual-polymerizable resin cement and the light-polymerizable restorative composite resin irradiated for 3 × 90 seconds with a high irradiance light-emitting diode lamp through 7.5-mm-thick endocrowns reached at least 80% of the control Vickers microhardness values, which means that both materials can be adequately polymerized when they are used for luting thick indirect restorations. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

A new technique to make transparent teeth without decalcifying: description of the methodology and micro-hardness assessment.

PubMed

Malentacca, Augusto; Lajolo, Carlo

2015-01-01

Diaphanisation and other in vitro endodontic models (i.e., plastic blocks, micro-CT reconstruction, computerised models) do not recreate real root canal working conditions: a more realistic endodontic model is essential for testing endodontic devices and teaching purposes. The aim of this study was to describe a new technique to construct transparent teeth without decalcifying and evaluate the micro-hardness of so treated teeth. Thirty freshly extracted teeth were randomly divided into three groups as follows: 10 non-treated teeth (4 molars, 3 premolars, 3 incisors; control group - G1), 10 teeth were diaphanised (4 molars, 4 premolars, 2 incisors - G2) and 10 teeth were treated with the new proposed technique (2 molars, 6 premolars, 2 incisors - G3). Vickers hardness tester (MHT-4 and AxioVision microscope, Carl Zeiss, 37030 Gottingen, Germany - load=50 g, dwell time=20s, slope=5, 50× magnification) was used to determine microhardness (Vickers Hardness Number - VHN). Statistical analysis was performed using the Intercooled Stata 8.0 software (Stata Corporation, College Station, TX, USA). Only groups 1 and 3 could be tested for hardness because diaphanised teeth were too tender and elastic. Differences in enamel VHN were observed between G1 (mean 304.29; DS=10.44; range 283-321) and G3 (mean 318.51; DS=14.36; range 295.5-339.2) - (p<0.05); differences in dentine VHN were observed between G1 (mean 74.73; DS=6.62; range 63.9-88.1) and G3 (mean 64.54; DS=5.55; range 51.2-72.3) - (p<0.05). G3 teeth presented a slightly lower VHN compared to G1, probably due to some little structural differences among groups, and were dramatically harder than the diaphanised teeth. The described technique, thus, can be considered ideal for testing endodontic instruments and for teaching purposes. Copyright © 2014 Elsevier GmbH. All rights reserved.

Optimization of process parameters in welding of dissimilar steels using robot TIG welding

NASA Astrophysics Data System (ADS)

Navaneeswar Reddy, G.; VenkataRamana, M.

2018-03-01

Robot TIG welding is a modern technique used for joining two work pieces with high precision. Design of Experiments is used to conduct experiments by varying weld parameters like current, wire feed and travelling speed. The welding parameters play important role in joining of dissimilar stainless steel SS 304L and SS430. In this work, influences of welding parameter on Robot TIG Welded specimens are investigated using Response Surface Methodology. The Micro Vickers hardness tests of the weldments are measured. The process parameters are optimized to maximize the hardness of the weldments.

Effect of laser irradiation on surface hardness and structural parameters of 7178 aluminium alloy

NASA Astrophysics Data System (ADS)

Maryam, Siddra; Bashir, Farooq

2018-04-01

Aluminium 7178 samples were prepared and irradiated with Nd:YAG laser. The surfaces of exposed samples were investigated using optical microscopy, which revealed that the surface morphology of the samples is changed drastically as a function of laser shots. It is revealed from the micrographs that the laser heat effected area increases with the increase in the number of the laser pulses. Furthermore morphological and mechanical properties were studied using XRD and Vickers hardness testing. XRD study shows an increasing trend in Grain size with the increasing number of laser shots. And the hardness of the samples as a function of the laser shots shows that the hardness first increases and then it decreases gradually. It was observed that the grain size has no pronouncing effect on the hardness. Hardness profile has a decreasing trend with the increase in linear distance from the boundary of the laser heat affected area.

Traceability in hardness measurements: from the definition to industry

NASA Astrophysics Data System (ADS)

Germak, Alessandro; Herrmann, Konrad; Low, Samuel

2010-04-01

The measurement of hardness has been and continues to be of significant importance to many of the world's manufacturing industries. Conventional hardness testing is the most commonly used method for acceptance testing and production quality control of metals and metallic products. Instrumented indentation is one of the few techniques available for obtaining various property values for coatings and electronic products in the micrometre and nanometre dimensional scales. For these industries to be successful, it is critical that measurements made by suppliers and customers agree within some practical limits. To help assure this measurement agreement, a traceability chain for hardness measurement traceability from the hardness definition to industry has developed and evolved over the past 100 years, but its development has been complicated. A hardness measurement value not only requires traceability of force, length and time measurements but also requires traceability of the hardness values measured by the hardness machine. These multiple traceability paths are needed because a hardness measurement is affected by other influence parameters that are often difficult to identify, quantify and correct. This paper describes the current situation of hardness measurement traceability that exists for the conventional hardness methods (i.e. Rockwell, Brinell, Vickers and Knoop hardness) and for special-application hardness and indentation methods (i.e. elastomer, dynamic, portables and instrumented indentation).

Elemental, microstructural, and mechanical characterization of high gold orthodontic brackets after intraoral aging.

PubMed

Hersche, Sepp; Sifakakis, Iosif; Zinelis, Spiros; Eliades, Theodore

2017-02-01

The purpose of the present study was to investigate the elemental composition, the microstructure, and the selected mechanical properties of high gold orthodontic brackets after intraoral aging. Thirty Incognito™ (3M Unitek, Bad Essen, Germany) lingual brackets were studied, 15 brackets as received (control group) and 15 brackets retrieved from different patients after orthodontic treatment. The surface of the wing area was examined by scanning electron microscopy (SEM). Backscattered electron imaging (BEI) was performed, and the elemental composition was determined by X-ray EDS analysis (EDX). After appropriate metallographic preparation, the mechanical properties tested were Martens hardness (HM), indentation modulus (EIT), elastic index (ηIT), and Vickers hardness (HV). These properties were determined employing instrumented indentation testing (IIT) with a Vickers indenter. The results were statistically analyzed by unpaired t-test (α=0.05). There were no statistically significant differences evidenced in surface morphology and elemental content between the control and the experimental group. These two groups of brackets showed no statistically significant difference in surface morphology. Moreover, the mean values of HM, EIT, ηIT, and HV did not reach statistical significance between the groups (p>0.05). Under the limitations of this study, it may be concluded that the surface elemental content and microstructure as well as the evaluated mechanical properties of the Incognito™ lingual brackets remain unaffected by intraoral aging.

Crack-resistant Al2O3-SiO2 glasses.

PubMed

Rosales-Sosa, Gustavo A; Masuno, Atsunobu; Higo, Yuji; Inoue, Hiroyuki

2016-04-07

Obtaining "hard" and "crack-resistant" glasses have always been of great important in glass science and glass technology. However, in most commercial glasses both properties are not compatible. In this work, colorless and transparent xAl2O3-(100-x)SiO2 glasses (30 ≤ x ≤ 60) were fabricated by the aerodynamic levitation technique. The elastic moduli and Vickers hardness monotonically increased with an increase in the atomic packing density as the Al2O3 content increased. Although a higher atomic packing density generally enhances crack formation in conventional oxide glasses, the indentation cracking resistance increased by approximately seven times with an increase in atomic packing density in binary Al2O3-SiO2 glasses. In particular, the composition of 60Al2O3 • 40SiO2 glass, which is identical to that of mullite, has extraordinary high cracking resistance with high elastic moduli and Vickers hardness. The results indicate that there exist aluminosilicate compositions that can produce hard and damage-tolerant glasses.

The effect of case hardening treatment on aluminum 7075 toward its hardness and tensile strength

NASA Astrophysics Data System (ADS)

Darsono, Febri Budi; Triyono, Teguh; Surojo, Eko

2018-02-01

This research was aimed at figuring out the effect of case hardening treatment on aluminum 7075 toward its hardness and tensile strength. Pack carburizing was the method used in this process. It was conducted in 2 hours of holding time in various solution heat treatment (SHT): 350°C, 400°C, 450°C, and 500° C using smoergen oven, which was then followed by quenching. Several tests to see the effect of the treatment were done before and after the treatment, namely: Vickers hardness test using HWMMT-X7, tensile test ASTM B557-84 using SANS UTM, XRD test using Rigaku Benchtop, and SEM-EDS test using JEOL JSM-6510 LA. The result showed that the hardness and tensile of aluminum 7075 before treatment were 59.1 VHN and 235.7 Mpa. After treatment, its hardness values were 94.0, 120.7, 141.3, and 145.9 VHN and the tensile strengths were 321.7, 410.0, 480.0, and 538.3 Mpa. The result showed that SHT temperature rise in pack carburizing process increased the tensile strength, while the increase of the hardness value is due to the formation of Al4C3 phase on the aluminum surface.

Manufacturing Feasibility and Forming Properties of Cu-4Sn in Selective Laser Melting.

PubMed

Mao, Zhongfa; Zhang, David Z; Wei, Peitang; Zhang, Kaifei

2017-03-24

Copper alloys, combined with selective laser melting (SLM) technology, have attracted increasing attention in aerospace engineering, automobile, and medical fields. However, there are some difficulties in SLM forming owing to low laser absorption and excellent thermal conductivity. It is, therefore, necessary to explore a copper alloy in SLM. In this research, manufacturing feasibility and forming properties of Cu-4Sn in SLM were investigated through a systematic experimental approach. Single-track experiments were used to narrow down processing parameter windows. A Greco-Latin square design with orthogonal parameter arrays was employed to control forming qualities of specimens. Analysis of variance was applied to establish statistical relationships, which described the effects of different processing parameters (i.e., laser power, scanning speed, and hatch space) on relative density (RD) and Vickers hardness of specimens. It was found that Cu-4Sn specimens were successfully manufactured by SLM for the first time and both its RD and Vickers hardness were mainly determined by the laser power. The maximum value of RD exceeded 93% theoretical density and the maximum value of Vickers hardness reached 118 HV 0.3/5. The best tensile strength of 316-320 MPa is inferior to that of pressure-processed Cu-4Sn and can be improved further by reducing defects.

Mechanical properties of 8Cr-2WVTa steel aged for 30 000 h

NASA Astrophysics Data System (ADS)

Tamura, M.; Shinozuka, K.; Esaka, H.; Sugimoto, S.; Ishizawa, K.; Masamura, K.

2000-12-01

A mill production plate of a reduced activation ferritic steel was thermally aged for up to 30 000 h at 400-650°C. Charpy impact tests, creep rupture tests and hardness tests were conducted. Both Vickers hardness number and creep strength decrease with aging at 650°C. The ductile-brittle transition temperature (DBTT) increases with both aging time and aging temperature. However, the DBTT does not exceed +20°C even after aging at 650°C for 30 000 h. Extracted residues and extraction replicas were analyzed metallurgically. The increase in DBTT is related mainly to the precipitation of Laves phase on the prior austenite grain boundaries. The rather low DBTT after aging is caused by the fine prior austenitic grain size.

Light energy transmission and Vickers hardness ratio of bulk-fill resin based composites at different thicknesses cured by a dual-wave or a single-wave light curing unit.

PubMed

Santini, Ario; Naaman, Reem Khalil; Aldossary, Mohammed Saeed

2017-04-01

To quantify light energy transmission through two bulk-fill resin-based composites and to measure the top to bottom surface Vickers hardness ratio (VHratio) of samples of various incremental thicknesses, using either a single-wave or dual-wave light curing unit (LCU). Tetric EvoCeram Bulk Fill (TECBF) and SonicFill (SF) were studied. Using MARC-RC, the irradiance delivered to the top surface of the samples 2, 3, 4 and 5 mm thick (n= 5 for each thickness) was adjusted to 800 mW/cm2 for 20 seconds (16 J/cm2) using either a single-wave, Bluephase or a dual-wave, Bluephase G2 LCUs. Light energy transmission through to the bottom surface of the specimens was measured at real time using MARC-RC. The Vickers hardness (VH) was determined using Vickers micro hardness tester and the VHratio was calculated. Data were analyzed using a general linear model in Minitab 16; α= 0.05. TECBF was more translucent than SF (P< 0.05). The mean VHratio was higher than 80% in 2, 3 and 4 mm increment thickness for both materials (except for 4 mm TECBF when cured with the dual-wave Bluephase G2). SF showed significantly higher VH ratio than TECBF at all different thickness levels (P< 0.05), except at the 2 mm level (P> 0.05). TECBF showed significantly greater VH ratio when cured with the single-wave Bluephase than when using the dual-wave Bluephase G2 (P< 0.05). The transmission of light energy through to the bottom surface and the VHratio are material dependent. Although TECBF is more translucent than SF, it showed lower VHratio compared to SF when cured with dual-wave Bluephase G2.

Effect of Heating Time on Hardness Properties of Laser Clad Gray Cast Iron Surface

NASA Astrophysics Data System (ADS)

Norhafzan, B.; Aqida, S. N.; Mifthal, F.; Zulhishamuddin, A. R.; Ismail, I.

2018-03-01

This paper presents effect of heating time on cladded gray cast iron. In this study, the effect of heating time on cladded gray cast iron and melted gray cast iron were analysed. The gray cast iron sample were added with mixed Mo-Cr powder using laser cladding technique. The mixed Mo and Cr powder was pre-placed on gray cast iron surface. Modified layer were sectioned using diamond blade cutter and polish using SiC abrasive paper before heated. Sample was heated in furnace for 15, 30 and 45 minutes at 650 °C and cool down in room temperature. Metallographic study was conduct using inverted microscope while surface hardness properties were tested using Wilson hardness test with Vickers scale. Results for metallographic study showed graphite flakes within matrix of pearlite. The surface hardness for modified layer decreased when increased heating time process. These findings are significant to structure stability of laser cladded gray cast iron with different heating times.

Effect of post weld impact treatment (PWIT) on mechanical properties of spot-welded joint

NASA Astrophysics Data System (ADS)

Ghazali, F. A.; Salleh, Z.; Hyie, K. M.; Rozlin, N. M. Nik; Hamidi, S. H. Ahmad; Padzi, M. M.

2017-12-01

This paper focuses on the study of improvement for spot welding on the tensile shear and hardness by applying post weld impact treatment (PWIT) on the welded joint. The main objective of the research is to characterize and improve the mechanical properties of the joint. The method of PWIT used on the welded joint was Pneumatic Impact Treatment (PIT). The concept of PIT on spot welding is that it improves the mechanical properties of the welded zone. The working sample was undergoing a resistance spot welding of joining two similar in dimension and material of a steel plate before treated. The dimension of both plate are 110 mm × 45 mm × 1.2 mm and the material used were low carbon steel (LCS). All the welded samples were tested for its mechanical properties by performing the tensile-shear and hardness test. Tensile-shear test was conducted on the spot welded, both treated and as-welded samples using crosshead speed of 2 mm/min, while hardness test was performed using 1kgf load via Vickers hardness indenter. The effects of PIT on tensile-shear properties and hardness were evaluated and found that the implementation of PIT has increased tensile shear and hardness significantly.

Comparisons of nanoindentation, 3-point bending, and tension tests for orthodontic wires.

PubMed

Iijima, Masahiro; Muguruma, Takeshi; Brantley, William A; Mizoguchi, Itaru

2011-07-01

The purposes of this study were to obtain information about mechanical properties with the nanoindentation test for representative wire alloys and compare the results with conventional mechanical tests. Archwires having 0.016 × 0.022-in cross sections were obtained of 1 stainless steel, 1 cobalt-chromium-nickel, 1 beta-titanium alloy, and 2 nickel-titanium products. Specimens of as-received wires were subjected to nanoindentation testing along the external surfaces and over polished cross sections to obtain values of hardness and elastic modulus. Other specimens of as-received wires were subjected to Vickers hardness, 3-point bending, and tension tests. All testing was performed at 25°C. Differences were found in hardness and elastic modulus obtained with the nanoindentation test at the external and cross-sectioned surfaces and with the conventional mechanical-property tests. Mechanical properties obtained with the nanoindentation test generally varied with indentation depth. The 3 testing methods did not yield identical values of hardness and elastic modulus, although the order among the 5 wire products was the same. Variations in results for the nanoindentation and conventional mechanical property tests can be attributed to the different material volumes sampled, different work-hardening levels, and an oxide layer on the wire surface. Copyright © 2011 American Association of Orthodontists. Published by Mosby, Inc. All rights reserved.

Metallurgical characterization of new palladium-containing cobalt chromium and nickel chromium alloys

NASA Astrophysics Data System (ADS)

Puri, Raghav

Recently introduced to the market has been an entirely new subclass of casting alloy composition whereby palladium (˜25 wt%) is added to traditional base metal alloys such as CoCr and NiCr. Objectives. The purpose of this study was to evaluate the microstructure and Vickers hardness of two new CoPdCr and one new NiPdCr alloy and compare them to traditional CoCr and NiCr alloys. Methods. The casting alloys investigated were: CoPdCr-A (Noble Crown NF, The Argen Corporation), CoPdCr-I (Callisto CP+, Ivoclar Vivadent), NiPdCr (Noble Crown, Argen), CoCr (Argeloy N.P. Special, Argen), and NiCr (Argeloy N.P. Star, Argen). As-cast cylindrical alloy specimens were mounted in epoxy resin and prepared with standard metallographic procedures, i.e. grinding with successive grades of SiC paper and polishing with alumina suspensions. The alloys were examined with an optical microscope, SEM/EPMA, and XRD to gain insight into their microstructure, composition, and crystal structure. Vickers hardness (VHN) was measured and statistically analyzed by one way ANOVA and Tukey's HSD test (alpha=0.05). Results. Optical microscopy showed a dendritic microstructure for all alloys. The Pd-containing alloys appear to possess a more complex microstructure. SEM/EPMA showed Cr to be rather uniformly distributed in the matrix with palladium tending to be segregated apart from Mo and Ni or Co. Areas of different composition may explain the poor electrochemical results noted in previous studies. XRD suggested the main phase in the Ni-containing solutions was a face centered cubic Ni solid solution, whereas the CoCr exhibited a hexagonal crystal structure that was altered to face centered cubic when Pd was included in the composition. For Vickers hardness, the Co-containing alloys possessed a greater hardness than the Ni-containing alloys. However, the incorporation of Pd in CoCr and NiCr had only a slight effect on microhardness. Conclusion. Overall, the inclusion of palladium increases the microstructural complexity of NiCr and CoCr alloys.

Metallurgical characterization of experimental Ag-based soldering alloys.

PubMed

Ntasi, Argyro; Al Jabbari, Youssef S; Silikas, Nick; Al Taweel, Sara M; Zinelis, Spiros

2014-10-01

To characterize microstructure, hardness and thermal properties of experimental Ag-based soldering alloys for dental applications. Ag12Ga (AgGa) and Ag10Ga5Sn (AgGaSn) were fabricated by induction melting. Six samples were prepared for each alloy and microstructure, hardness and their melting range were determined by, scanning electron microscopy, energy dispersive X-ray (EDX) microanalysis, X-ray diffraction (XRD), Vickers hardness testing and differential scanning calorimetry (DSC). Both alloys demonstrated a gross dendritic microstructure while according to XRD results both materials consisted predominately of a Ag-rich face centered cubic phase The hardness of AgGa (61 ± 2) was statistically lower than that of AgGaSn (84 ± 2) while the alloys tested showed similar melting range of 627-762 °C for AgGa and 631-756 °C for AgGaSn. The experimental alloys tested demonstrated similar microstructures and melting ranges. Ga and Sn might be used as alternative to Cu and Zn to modify the selected properties of Ag based soldering alloys.

Metallurgical characterization of experimental Ag-based soldering alloys

PubMed Central

Ntasi, Argyro; Al Jabbari, Youssef S.; Silikas, Nick; Al Taweel, Sara M.; Zinelis, Spiros

2014-01-01

Aim To characterize microstructure, hardness and thermal properties of experimental Ag-based soldering alloys for dental applications. Materials and methods Ag12Ga (AgGa) and Ag10Ga5Sn (AgGaSn) were fabricated by induction melting. Six samples were prepared for each alloy and microstructure, hardness and their melting range were determined by, scanning electron microscopy, energy dispersive X-ray (EDX) microanalysis, X-ray diffraction (XRD), Vickers hardness testing and differential scanning calorimetry (DSC). Results Both alloys demonstrated a gross dendritic microstructure while according to XRD results both materials consisted predominately of a Ag-rich face centered cubic phase The hardness of AgGa (61 ± 2) was statistically lower than that of AgGaSn (84 ± 2) while the alloys tested showed similar melting range of 627–762 °C for AgGa and 631–756 °C for AgGaSn. Conclusion The experimental alloys tested demonstrated similar microstructures and melting ranges. Ga and Sn might be used as alternative to Cu and Zn to modify the selected properties of Ag based soldering alloys. PMID:25382945

Metallurgical characterization of orthodontic brackets produced by Metal Injection Molding (MIM).

PubMed

Zinelis, Spiros; Annousaki, Olga; Makou, Margarita; Eliades, Theodore

2005-11-01

The aim of this study was to investigate the bonding base surface morphology, alloy type, microstructure, and hardness of four types of orthodontic brackets produced by Metal Injection Molding technology (Discovery, Extremo, Freedom, and Topic). The bonding base morphology of the brackets was evaluated by scanning electron microscopy (SEM). Brackets from each manufacturer were embedded in epoxy resin, and after metallographic grinding, polishing and coating were analyzed by x-ray energy-dispersive spectroscopic (EDS) microanalysis to assess their elemental composition. Then, the brackets were subjected to metallographic etching to reveal their metallurgical structure. The same specimen surfaces were repolished and used for Vickers microhardness measurements. The results were statistically analyzed with one-way analysis of variance and Student-Newman-Keuls multiple comparison test at the 0.05 level of significance. The findings of SEM observations showed a great variability in the base morphology design among the brackets tested. The x-ray EDS analysis demonstrated that each bracket was manufactured from different ferrous or Co-based alloys. Metallographic analysis showed the presence of a large grain size for the Discovery, Freedom, and Topic brackets and a much finer grain size for the Extremo bracket. Vickers hardness showed great variations among the brackets (Topic: 287 +/- 16, Freedom: 248 +/- 13, Discovery: 214 +/- 12, and Extremo: 154 +/- 9). The results of this study showed that there are significant differences in the base morphology, composition, microstructure, and microhardness among the brackets tested, which may anticipate significant clinical implications.

Mapping residual stress fields from Vickers hardness indents using Raman microprobe spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sparks, R.G.; Enloe, W.S.; Paesler, M.A.

Micro-Raman spectroscopy is used to map the residual stress fields in the vicinity of Vickers hardness indents. Both 514.5 and 488.0 nm, light is used to excite the effect and the resulting shifted and broadened Raman peaks are analyzed using computer deconvolution. Half-wave plates are used to vary the orientation of the incident later light`s polarization state with respect to crystal orientation. The Raman scattered light is then analyzed for polarization dependences which are indicative of the various components of the Raman scattering tensor. Such studies can yield valuable information about the orientation of stress components in a well knownmore » stress field. The results can then be applied to the determination of stress components in machined semiconductor materials.« less

Effect of gloss and heat on the mechanical behaviour of a glass carbomer cement.

PubMed

Menne-Happ, Ulrike; Ilie, Nicoleta

2013-03-01

The effect of gloss and heat on the mechanical behaviour of a recently launched glass carbomer cement (GCP, GCP dental) was evaluated and compared with resin-modified glass ionomer cements (Fuji II LC, GC and Photac Fil Quick Aplicap, 3M ESPE). 120bar-shaped specimens (n=20) were produced, maintained in distilled water at 37°C and tested after one week. The GCP specimens were cured with and without heat application and with and without gloss. The flexural strength and modulus of elasticity in flexural test as well as the micro-mechanical properties (Vickers Hardness, indentation modulus, creep) of the top and bottom surface were evaluated. The amount and size of the fillers, voids and cracks were compared using a light and a scanning electron microscope. In the flexural test, the resin-modified glass ionomer cements performed significantly better than GCP. Fuji II LC and Photac Fil (Weibull parameter: 17.7 and 14.3) proved superior reliability in the flexural test compared to GCP (1.4-2.6). The highest Vickers Hardness and lowest creep were achieved by GCP, whereas Fuji II LC reached the highest indentation modulus. The results of this study proved that relationships exist between the compositions, microstructures and mechanical properties of the cements. Heat treatment and gloss application did not influence the mechanical properties of GCP. The mechanical properties were basically influenced by the type of cement and its microstructure. Considering the measured mechanical properties, there is no need of using gloss or heat when restoring teeth with GCP. Copyright © 2012 Elsevier Ltd. All rights reserved.

Comparison of time-dependent changes in the surface hardness of different composite resins

PubMed Central

Ozcan, Suat; Yikilgan, Ihsan; Uctasli, Mine Betul; Bala, Oya; Kurklu, Zeliha Gonca Bek

2013-01-01

Objective: The aim of this study was to evaluate the change in surface hardness of silorane-based composite resin (Filtek Silorane) in time and compare the results with the surface hardness of two methacrylate-based resins (Filtek Supreme and Majesty Posterior). Materials and Methods: From each composite material, 18 wheel-shaped samples (5-mm diameter and 2-mm depth) were prepared. Top and bottom surface hardness of these samples was measured using a Vicker's hardness tester. The samples were then stored at 37°C and 100% humidity. After 24 h and 7, 30 and 90 days, the top and bottom surface hardness of the samples was measured. In each measurement, the rate between the hardness of the top and bottom surfaces were recorded as the hardness rate. Statistical analysis was performed by one-way analysis of variance, multiple comparisons by Tukey's test and binary comparisons by t-test with a significance level of P = 0.05. Results: The highest hardness values were obtained from each two surfaces of Majesty Posterior and the lowest from Filtek Silorane. Both the top and bottom surface hardness of the methacrylate based composite resins was high and there was a statistically significant difference between the top and bottom hardness values of only the silorane-based composite, Filtek Silorane (P < 0.05). The lowest was obtained with Filtek Silorane. The hardness values of all test groups increased after 24 h (P < 0.05). Conclusion: Although silorane-based composite resin Filtek Silorane showed adequate hardness ratio, the use of incremental technic during application is more important than methacrylate based composites. PMID:24966724

U 3Si 2 Fabrication and Testing for Implementation into the BISON Fuel Performance Code

DOE Office of Scientific and Technical Information (OSTI.GOV)

Knight, Travis W.

A creep test stand was designed and constructed for compressive creep testing of U 3Si 2 pellets. This is described in Chapter 3. Creep testing of U 3Si 2 pellets was completed. In total, 13 compressive creep tests of U 3Si 2 pellets was successfully completed. This is reported in Chapter 3. Secondary creep model of U 3Si 2 was developed and implemented in BISON. This is described in Chapter 4. Properties of U 3Si 2 were implemented in BISON. This is described in Chapter 4. A resonant frequency and damping analyzer (RFDA) using impulse excitation technique (IET) was setup,more » tested, and used to analyze U 3Si 2 samples to measure Young’s and Shear Moduli which were then used to calculate the Poisson ratio for U 3Si 2. This is described in Chapter 5. Characterization of U 3Si 2 samples was completed. Samples were prepared and analyzed by XRD, SEM, and optical microscopy. Grain size analysis was conducted on images. SEM with EDS was used to analyze second phase precipitates. Impulse excitation technique was used to determine the Young’s and Shear Moduli of a tile specimen which allowed for the determination of the Poisson ratio. Helium pycnometry and mercury intrusion porosimetry was performed and used with image analysis to determine porosity size distribution. Vickers microindentation characterization method was used to evaluate the mechanical properties of U 3Si 2 including toughness, hardness, and Vickers hardness. Electrical resistivity measurement was done using the four-point probe method. This is reported in Chapter 5.« less

Microhardness and morphological changes induced by Nd:Yag laser on dental enamel: an in vitro study.

PubMed

Bedini, Rossella; Manzon, Licia; Fratto, Giovanni; Pecci, Raffaella

2010-01-01

The aim of this work was a scanning electron microscopy (SEM) evaluation of the hardness and morphological changes of enamel irradiated by neodymium: yttrium aluminium garnet (Nd:YAG) laser with different energy levels. Twenty-eight human teeth samples were divided into 4 groups: control, where enamel surface was not lased, and 3 test treated with 3 different levels of energy power 0.6, 1.2 and 2.4 Watt, respectively. In each group, 5 samples underwent Vickers micro-hardness test and 2 samples were processed for SEM. No significant differences between treated and non treated samples were found by micro-hardness test. However, by SEM, test samples showed a rougher enamel surface than control. Specifically, the 0.6 Watt treated samples showed vertical scratches and glass-like areas, while in the other 2 groups enamel surface was covered by craters and cracks. These findings suggest that enamel should be lased at a low energy level to preserve its integrity and reduce demineralization, and thus for dental caries prevention purposes; while high energy level creates a retentive surface suitable for sealant or composite anchorage.

Prediction of the Vickers Microhardness and Ultimate Tensile Strength of AA5754 H111 Friction Stir Welding Butt Joints Using Artificial Neural Network.

PubMed

De Filippis, Luigi Alberto Ciro; Serio, Livia Maria; Facchini, Francesco; Mummolo, Giovanni; Ludovico, Antonio Domenico

2016-11-10

A simulation model was developed for the monitoring, controlling and optimization of the Friction Stir Welding (FSW) process. This approach, using the FSW technique, allows identifying the correlation between the process parameters (input variable) and the mechanical properties (output responses) of the welded AA5754 H111 aluminum plates. The optimization of technological parameters is a basic requirement for increasing the seam quality, since it promotes a stable and defect-free process. Both the tool rotation and the travel speed, the position of the samples extracted from the weld bead and the thermal data, detected with thermographic techniques for on-line control of the joints, were varied to build the experimental plans. The quality of joints was evaluated through destructive and non-destructive tests (visual tests, macro graphic analysis, tensile tests, indentation Vickers hardness tests and t thermographic controls). The simulation model was based on the adoption of the Artificial Neural Networks (ANNs) characterized by back-propagation learning algorithm with different types of architecture, which were able to predict with good reliability the FSW process parameters for the welding of the AA5754 H111 aluminum plates in Butt-Joint configuration.

Correction of the post -- necking true stress -- strain data using instrumented nanoindentation

NASA Astrophysics Data System (ADS)

Romero Fonseca, Ivan Dario

The study of large plastic deformations has been the focus of numerous studies particularly in the metal forming processes and fracture mechanics fields. A good understanding of the plastic flow properties of metallic alloys and the true stresses and true strains induced during plastic deformation is crucial to optimize the aforementioned processes, and to predict ductile failure in fracture mechanics analyzes. Knowledge of stresses and strains is extracted from the true stress-strain curve of the material from the uniaxial tensile test. In addition, stress triaxiality is manifested by the neck developed during the last stage of a tensile test performed on a ductile material. This necking phenomenon is the factor responsible for deviating from uniaxial state into a triaxial one, then, providing an inaccurate description of the material's behavior after the onset of necking. The research of this dissertation is aimed at the development of a correction method for the nonuniform plastic deformation (post-necking) portion of the true stress-strain curve. The correction proposed is based on the well-known relationship between hardness and flow (yield) stress, except that instrumented nanoindentation hardness is utilized rather than conventional macro or micro hardness. Three metals with different combinations of strain hardening behavior and crystal structure were subjected to quasi-static tensile tests: power-law strain hardening low carbon G10180 steel (BCC) and electrolytic tough pitch copper C11000 (FCC), and linear strain hardening austenitic stainless steel S30400 (FCC). Nanoindentation hardness values, measured on the broken tensile specimen, were converted into flow stress values by means of the constraint factor C from Tabor's, the representative plastic strainepsilonr and the post-test true plastic strains measured. Micro Vickers hardness testing was carried out on the sample as well. The constraint factors were 5.5, 4.5 and 4.5 and the representative plastic strains were 0.028, 0.062 and 0.061 for G101800, C11000 and S30400 respectively. The established corrected curves relating post-necking flow stress to true plastic strain turned out to be well represented by a power-law function. Experimental results dictated that a unique single value for C and for epsilonr is not appropriate to describe materials with different plastic behaviors. Therefore, Tabor's equation, along with the representative plastic strain concept, has been misused in the past. The studied materials exhibited different nanohardness and plastic strain distributions due to their inherently distinct elasto-plastic response. The proposed post-necking correction separates out the effect of triaxiality on the uniaxial true stress-strain curve provided that the nanohardness-flow stress relationship is based on uniaxial values of stress. Some type of size effect, due to the microvoids at the tip of the neck, influenced nanohardness measurements. The instrumented nanoindentation technique proved to be a very suitable method to probe elasto-plastic properties of materials such as nanohardness, elastic modulus, and quasi-static strain rate sensitivity among others. Care should be taken when converting nanohardness to Vickers and vice versa due to their different area definition used. Nanohardness to Vickers ratio oscillated between 1.01 and 1.17.

Reverse-Martensitic Hardening of Austenitic Stainless Steel upon Up-quenching

NASA Astrophysics Data System (ADS)

Sato, Kiminori; Guo, Defeng; Li, Xiaohong; Zhang, Xiangyi

2016-08-01

Reverse-martensitic transformation utilizing up-quenching was demonstrated for austenitic stainless steel. Up-quenching was done following the stress-induced phase modification to martensite and then enrichment of the body-centered-cubic ferrite. Transmission-electron-microscopy observation and Vickers hardness test revealed that the reverse-martensitic transformation yields quench hardening owing to an introduction of highly-concentrated dislocation. It is furthermore found that Cr precipitation on grain boundaries caused by isothermal aging is largely suppressed in the present approach.

Effect of γ-IRRADIATION on the Mechanical Properties of Al-Cu Alloy

NASA Astrophysics Data System (ADS)

Abo-Elsoud, M.; Ismail, H.; Sobhy, Maged S.

SEM observations and Vickers hardness tests were performed to identify the irradiation effects. γ-irradiation effect during the aging hardening process can be explained depending on the composition of the alloy and is used to derive quantitative information on the kinetics of the transformation precipitates. Increasing the Cu content of an Al-Cu alloy can improve the aging hardness. The present results of the hardness behavior, with SEM observations of surveillance specimens at different doses, suggest that the radiation-induced defects are probably complex valence-solute clusters. These clusters act as nuclei for the precipitation of θ-Al2Cu type. This can be effectively utilized to study the systematics of nucleation of precipitates at vacancy-type defects. γ-irradiation probably plays the key role in defects responsible for material strengthening and embrittlement.

Wear Resistance of Austempered Ductile Iron with Nanosized Additives

NASA Astrophysics Data System (ADS)

Kaleicheva, J. K.; Mishev, V.

2018-01-01

The wear resistance, microstructure and mechanical properties of austempered ductile iron (ADI) with nanosized additives of cubic boron nitride cBN are investigated. Samples of ductile iron are put under austhempering at the following conditions: heating at 900°С, 1 h and isothermal retention at 280оС, 2 h and 380°С, 2 h with the aim to achieve a lower bainitic structure and an upper bainitic structure. The experimental wear testing of austempered ductile irons is performed in friction conditions of a fixed abrasive by a cinematic scheme „pin - disc” using an accelerated testing method and device. The microstructure of the ADI is investigated by metallographic and X-Ray analyses. The Vickers hardness testing and impact strength examination are carried out. The influence of the nanosized additives of cBN on the wear resistance, microstructure, impact strength and hardness of the ADI is investigated.

Construction of continuous cooling transformation (CCT) diagram using Gleeble for coarse grained heat affected zone of SA106 grade B steel

NASA Astrophysics Data System (ADS)

Vimalan, G.; Muthupandi, V.; Ravichandran, G.

2018-05-01

A continuous cooling transformation diagram is constructed for simulated coarse grain heat affected zone (CGHAZ) of SA106 grade B carbon steel. Samples are heated to a peak temperature of 1200°C in the Gleeble thermo mechanical simulator and then cooled at different cooling rates varying from 0.1°C/s to 100°C/s. Microstructure of the specimens simulated at different cooling rates were characterised by optical microscopy and hardness was assessed by Vicker's hardness test and micro-hardness test. Transformation temperatures and the corresponding phase fields were identified from dilatometric curves and the same could be confirmed by correlating with the microstructures at room temperature. These data were used to construct the CCT diagram. Phase fields were found to have ferrite, pearlite, bainite and martensite or their combinations. With the help of this CCT diagram it is possible to predict the microstructure and hardness of coarse grain HAZ experiencing different cooling rates. The constructed CCT diagram becomes an important tool in evaluating the weldability of SA106 grade B carbon steel.

Quench hardening of Sb0.2 Bi1.8Te3, Bi2Te2.8Se0.2 and Sn0.2 Bi1.8Te3 single crystals

NASA Astrophysics Data System (ADS)

Soni, P. H.

2018-02-01

The V2-VI3 intermetallics are narrow band gap semiconductors and well known for their thermoelectric properties. They therefore offer a convenient route to tune band gap for manipulating thermoelectric parameters. The V group element Sb can be fruitfully used to substitute Bi in various proportions thus forming a psuedobinary solid solution. The electronic in general and the thermoelectric properties in particular of this psuedobinary have been amply reported. However there are no reports found on mechanical properties. I have used Sb0.2 Bi1.8Te3, Bi2Te2.8Se0.2 and Sn0.2 Bi1.8Te3single crystals grown using Bridgman technique for the quenching treatment followed by hardness testing. Vickers hardness tests were conducted on the cleavage planes of the crystals quenched from various high temperatures and the quench hardenening coefficient values have been determined. The hardness tests were carried out at various applied loads also to explore load dependence of the measured hardness. The results are reported in the paper.

Mechanical and wear properties of aluminum coating prepared by cold spraying

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yusof, Siti Nurul Akmal, E-mail: em-leo277@yahoo.com; Manap, Abreeza, E-mail: Abreeza@uniten.edu.my; Afandi, Nurfanizan Mohd

In this study, aluminum (Al) powders were deposited onto Al substrates using cold spray to form a coating. The main objective is to investigate and compare the microstructure, mechanical and wear properties of Al coating to that of the Al substrate. The microstructure of the coating and substrate were observed using Scanning Electron Microscope (SEM). Hardness was evaluated using the Vickers Hardness test and wear properties were investigated using a pin-on-disk wear test machine. The elemental composition of the coating and substrate was determined using Energy-dispersive X-ray spectroscopy (EDX). Results showed that the friction coefficient and specific wear rate decreasedmore » while wear rate increased linearly with increasing load. It was found that the coating exhibit slightly better mechanical and wear properties compared to the substrate.« less

Evaluation to determine the caries remineralization potential of three dentifrices: An in vitro study

PubMed Central

Balakrishnan, Arun; Jonathan, R; Benin, P; Kuumar, Arvind

2013-01-01

Aim: The aim of this study was to evaluate the remineralizing potential of three different remineralizing agents (GC tooth Mousse, Clinpro tooth crθme and SHY-NM) on demineralized tooth surfaces using micro CT and microhardness. Materials and Methods: Forty five freshly extracted mandibular premolars were collected and enamel specimens were prepared. The samples were assigned to three groups with fifteen specimens in each group. The specimens were then demineralized using McInne's demineralizing solution in two cycles. After that, remineralization was carried out in two cycles for 30 days using Casein phosphopeptide - Amorphous calcium phosphate (CPP - ACP), 0.21% sodium fluoride - Tricalcium phosphate (f-TCP) and Calcium Sodium Phosphosilicate (CSP) containing tooth pastes for groups I, II, III respectively. The specimens were evaluated for Linear attenuation co-efficient using micro CT (Scanco™) and Vicker's Micro Hardness (Schimadzu™) testing at different time periods. The results were tabulated and statistically analysed. Results: It was observed that all the three remineralizing agents used in the study significantly increased the Linear Attenuation Co-efficient and Vicker's hardness number values of the enamel specimens following 15 days and 30 days application. Conclusion: CPP – ACP showed the better remineralizing potential than the other two agents and there was no statistical significant difference between f-TCP and CSP groups. PMID:23956545

Effect of Heat Input on Microstructure Evolution and Mechanical Properties in the Weld Heat-Affected Zone of 9Cr-2W-VTa Reduced Activation Ferritic-Martensitic Steel for Fusion Reactor

NASA Astrophysics Data System (ADS)

Moon, Joonoh; Lee, Chang-Hoon; Lee, Tae-Ho; Kim, Hyoung Chan

2015-01-01

The phase transformation and mechanical properties in the weld heat-affected zone (HAZ) of a reduced activation ferritic/martensitic steel were explored. The samples for HAZs were prepared using a Gleeble simulator at different heat inputs. The base steel consisted of tempered martensite and carbides through quenching and tempering treatment, whereas the HAZs consisted of martensite, δ-ferrite, and a small volume of autotempered martensite. The prior austenite grain size, lath width of martensite, and δ-ferrite fraction in the HAZs increased with increase in the heat input. The mechanical properties were evaluated using Vickers hardness and Charpy V-notch impact test. The Vickers hardness in the HAZs was higher than that in the base steel but did not change noticeably with increase in the heat input. The HAZs showed poor impact property due to the formation of martensite and δ-ferrite as compared to the base steel. In addition, the impact property of the HAZs deteriorated more with the increase in the heat input. Post weld heat treatment contributed to improve the impact property of the HAZs through the formation of tempered martensite, but the impact property of the HAZs remained lower than that of base steel.

Effect of incorporation of zinc oxide nanoparticles on mechanical properties of conventional glass ionomer cements.

PubMed

Panahandeh, Narges; Torabzadeh, Hassan; Aghaee, Mohammadamin; Hasani, Elham; Safa, Saeed

2018-01-01

The aim of this study is to investigate the physical properties of conventional and resin-modified glass ionomer cements (GICs) compared to GICs supplemented with zinc oxide (ZnO) nanofiller particles at 5% (w/w). In this in vitro study, ZnO nanoparticles of different morphologies (nanospherical, nanorod, and nanoflower) were incorporated to glass ionomer powder. The samples were subjected to the flexural strength ( n = 20) and surface hardness test ( n = 12) using a universal testing machine and a Vickers hardness machine, respectively. Surface analysis and crystal structure of samples were performed with scanning electron microscope and X-radiation diffraction, respectively. The data were analyzed using one-way ANOVA, Shapiro-Wilk, and Tukey's tests ( P < 0.05). Flexural strength of glass ionomer containing nanoparticles was not significantly different from the control group ( P > 0.05). The surface hardness of the glass ionomer containing nanospherical or nanoflower ZnO was significantly lower than the control group ( P < 0.05). However, the surface hardness of glass ionomer containing nanorod ZnO was not significantly different from the control group ( P = 0.868). Incorporation of nanospherical and nanoflower ZnO to glass ionomer decreased their surface hardness, without any changes on their flexural strength. Incorporation of nanorod ZnO particles caused no effect on the mechanical properties.

Effects of thermal cycling on surface roughness, hardness and flexural strength of polymethylmethacrylate and polyamide denture base resins.

PubMed

Ayaz, Elif Aydoğan; Bağış, Bora; Turgut, Sedanur

2015-10-16

The purpose of this study was to evaluate the effects of thermal cycling on the surface roughness, hardness and flexural strength of denture resins. Polyamide (PA; Deflex and Valplast) and polymethylmethacrylate (PMMA; QC-20 and Acron MC) denture materials were selected. A total of 180 specimens were fabricated and then divided into 3 groups. The first group (group 1) acted as a control and was not thermocycled. The second group (group 2) was subjected to thermocycling for 10,000 cycles in artificial saliva and 5,000 cycles in distilled water. The last group (group 3) was thermocycled for 20,000 cycles in artificial saliva and 10,000 cycles in distilled water. The surface roughness were measured with a profilometer. The hardness of the resins were measured with a Vickers Hardness Tester using a 100-gf load. The flexural strength test was performed using the universal test machine with a crosshead speed of 5 mm/min. Data were analyzed using statistical software. The results of the measurements in the 3 different tests were analyzed by Kruskal-Wallis test with Bonferroni correction. Multiple comparisons were made by Conover and Wilcoxon tests. There was a significant difference between the PMMA and PA groups in terms of surface roughness, hardness and transverse strength before and after thermal cycling (p<0.001). Thermal cycling did not change the surface roughness, hardness and flexural strength values of either the PMMA or PA group (p>0.001).

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hallerman, G.; Gray, R.J.

The design and testing procedures of two elevatedtemperature hardness testers are described. One device uses a Rockwell tester with a large vertical capacity and a load range of 15 to 150 kg. The tester is equipped with a 900 deg C heating chamber which maintains an argon atmosphere over the specimen and can be laterally displaced by a cross-feed mechanism to allow repeated hardness readings to be made on the same specimen. The second instrument is a microindentation hardness tester for hardness determinations to a maximum temperature of 1000 deg C in vacuum of 10/sup -4/ to 10/sup -5/ torr.more » A deadweight loading system with a 136-deg diamond pyramid (Vickers) indenter, capable of delivering static loads between 0.150 and 3 kg, is contained within the vacuum chamber to avoid calibration problems that arise when loads are applied from outside the vacuum system. The microindentation hardness tester allows up to 100 determinations to be made on a single specimen without opening the test chamber. The applicability of the testers is illustrated by elevatedtemperature hardness measurements on several commercial alloys, a group of niobium-vanadium alloys, and by the changes in hardness occurring at the transformation temperatures of iron and steel. Hardness values of Haynes alloy No. 25 were determined at the temperatures of aging and are shown to be different from those obtained with the customary method of investigating age hardening. The testing is currently being used to aid and accelerate the development of alloys with desirable high-temperature properties. (auth)« less

Mechanical properties of titanium-hydroxyapatite (Ti-HA) composite coating on stainless steel prepared by thermal spraying

NASA Astrophysics Data System (ADS)

Rosmamuhamadani, R.; Azhar, N. H.; Talari, M. K.; Yahaya, Sabrina M.; Sulaiman, S.; Ismail, M. I. S.

2017-09-01

Addition of hydroxyapatite (HA) can enhance the bioactivity of the common metallic implant due to its similarity with natural bones and teeth. In this investigation, high velocity oxy-fuel (HVOFT) technique was used to deposit titanium-hydroxyapatite (Ti-HA) composite on stainless steel substrate plate with different percentage of HA for biomedical applications. The aim of this research is to investigate the mechanical properties of Ti-HA coating such as hardness, adhesion strength and wear behaviour. The hardness and strength was determined by using SHIMADZU-microhardness Vickers tester and PosiTest AT portable adhesion tester respectively. The wear test was performed by using pin-on-disk equipment and field emission scanning electron microscope (FESEM) used to determine the extent of surface damage. From the results obtained, mechanical properties such as hardness and adhesion strength of titanium (Ti) coating decreased with the increased of HA contents. Meanwhile, the coefficient of friction of Ti-10% HA coating shows the highest value compare to others as three-body abrasion had occurred during the test.

Effect of Loading Rate Upon Conventional Ceramic Microindentation Hardness

PubMed Central

Quinn, George D.; Patel, Parimal J.; Lloyd, Isabel

2002-01-01

The world standards for conventional ceramic hardness have varying requirements for control of loading rate during the indentation cycle. A literature review suggests that loading rate may affect measured hardness in some instances. In view of the uncertainty over this issue, new experiments over a range of indentation loading rates were performed on a steel, sintered silicon carbide, and an aluminum oxynitride. There was negligible effect upon Vickers hardness when loading rate was varied by almost four orders of magnitude from approximately 0.03 N/s to 10 N/s. PMID:27446732

Microstructure, Mechanical Properties, and Two-Body Abrasive Wear Behavior of Cold-Sprayed 20 vol.% Cubic BN-NiCrAl Nanocomposite Coating

NASA Astrophysics Data System (ADS)

Luo, Xiao-Tao; Yang, Er-Juan; Shang, Fu-Lin; Yang, Guan-Jun; Li, Chen-Xin; Li, Chang-Jiu

2014-10-01

20 vol.% cubic boron nitride (cBN) dispersoid reinforced NiCrAl matrix nanocomposite coating was prepared by cold spray using mechanically alloyed nanostructured composite powders. The as-sprayed nanocomposite coating was annealed at a temperature of 750 °C to enhance the inter-particle bonding. Microstructure of spray powders and coatings was characterized. Vickers microhardness of the coatings was measured. Two-body abrasive wear behavior of the coatings was examined on a pin-on-disk test. It was found that, in mechanically alloyed composite powders, nano-sized and submicro-sized cBN particles are uniformly distributed in nanocrystalline NiCrAl matrix. Dense coating was deposited by cold spray at a gas temperature of 650 °C with the same phases and grain size as those of the starting powder. Vickers hardness test yielded a hardness of 1063 HV for the as-sprayed 20 vol.% cBN-NiCrAl coating. After annealed at 750 °C for 5 h, unbonded inter-particle boundaries were partially healed and evident grain growth of nanocrystalline NiCrAl was avoided. Wear resistance of the as-sprayed 20 vol.% cBN-NiCrAl nanocomposite coating was comparable to the HVOF-sprayed WC-12Co coating. Annealing of the nanocomposite coating resulted in the improvement of wear resistance by a factor of ~33% owing to the enhanced inter-particle bonding. Main material removal mechanisms during the abrasive wear are also discussed.

Comparison Study on Additive Manufacturing (AM) and Powder Metallurgy (PM) AlSi10Mg Alloys

NASA Astrophysics Data System (ADS)

Chen, B.; Moon, S. K.; Yao, X.; Bi, G.; Shen, J.; Umeda, J.; Kondoh, K.

2018-02-01

The microstructural and mechanical properties of AlSi10Mg alloys fabricated by additive manufacturing (AM) and powder metallurgy (PM) routes were investigated and compared. The microstructures were examined by scanning electron microscopy assisted with electron-dispersive spectroscopy. The crystalline features were studied by x-ray diffraction and electron backscatter diffraction. Room-temperature tensile tests and Vickers hardness measurements were performed to characterize the mechanical properties. It was found that the AM alloy had coarser Al grains but much finer Si precipitates compared with the PM alloy. Consequently, the AM alloy showed more than 100% increment in strength and hardness compared with the PM alloy due to the presence of ultrafine forms of Si, while exhibiting moderate ductility.

Hardness and surface roughness of enamel and base layers of resin denture teeth after long-term repeated chemical disinfection.

PubMed

Neppelenbroek, Karin Hermana; Kurokawa, Luciana Ayumi; Procópio, Andréa Lemos Falcão; Pegoraro, Thiago Amadei; Hotta, Juliana; Mello Lima, Jozely Francisca; Urban, Vanessa Migliorini

2015-01-01

To evaluate the effect of successive cycles of disinfection in different denture cleansers on the surface roughness and the Vickers hardness of two layers of acrylic resin (base-BL and enamel-EL) of two commercial cross-linked artificial teeth. The occlusal surfaces of 60 acrylic resin denture posterior teeth (Trilux-TLX and SR Orthosit PE-SRO) embedded in autopolymerizing acrylic resin were ground fat with 1200-grit silicon carbide paper. Specimens were stored in distilled water at 37°C and then submitted to the microhardness (VHN) and roughness (μm) tests. Specimens were stored in distilled water at 37°C for 90 days and submitted to 720 disinfection cycles in sodium hypochlorite at 0.5%, 30% vinegar solution or distilled water (control). Afterward, micro-hardness and roughness tests were again performed. Data were analyzed using two-way ANOVA and Tukey's test (α=0.05). Hypochlorite immersion decreased the hardness of BL and EL of SRO teeth, with an average reduction of 10.11% (p<0.008). TLX teeth demonstrated a hardness reduction of 28.96% of both layers for all solutions including water (p<0.0000). The roughness of both teeth was not affected by denture cleansers (p>0.37). Hypochlorite promoted deleterious effects on the hardness of both layers of the artificial teeth tested. Immersion in vinegar and water also resulted in reduction of hardness of TLX teeth. The surface hardness of the different layers of cross-linked artificial teeth can be altered by daily disinfection in denture cleansers commonly indicated for removable dentures.

Evaluation of remineralization capacity of casein phosphopeptide-amorphous calcium phosphate on the carbamide peroxide treated enamel

PubMed Central

Penumatsa, Narendra Varma; Kaminedi, Raja Rajeswari; Baroudi, Kusai; Barakath, Ola

2015-01-01

Objective: The aim of this study was to evaluate the potential of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) in remineralizing the bleached enamel surface using micro-hardness. Materials and Methods: Thirty human enamel slabs were randomly divided into three groups (n = 10). Groups A and B were exposed to 20% carbamide peroxide and 35% carbamide peroxide gel, respectively. After the exposure to the bleaching agent, the slabs were kept in artificial saliva for 1-week. Group C (control group) were kept in artificial saliva for 1-week. Vickers micro-hardness test was performed by Leica VMHT-Mot micro-hardness tester. CPP-ACP (Gc Tooth Mousse, Melbourne, Australia) was then applied to specimens of Groups A and B for 3 min for 2 weeks. Micro-hardness values of postbleach Group A (Ar) and Group B (Br) were recorded and statistically analyzed by paired t-test and one-way analysis of variance at the significance level of α =0.05. Results: There was a significant decrease in micro-hardness of enamel in carbamide peroxide bleached groups. However, there was a significant increase in micro-hardness after the remineralization by CPP-ACP and the extent of remineralization is more for the Group B. Conclusions: That bleaching agents reduced enamel micro-hardness and the use of CPP-ACP after bleaching can significantly enhance the micro-hardness of bleached enamel. PMID:26538923

Evaluation of degree of conversion and hardness of dental composites photo-activated with different light guide tips.

PubMed

Galvão, Marília Regalado; Caldas, Sergei Godeiro Fernandes Rabelo; Bagnato, Vanderlei Salvador; de Souza Rastelli, Alessandra Nara; de Andrade, Marcelo Ferrarezi

2013-01-01

The aim of this study was to evaluate the degree of conversion and hardness of different composite resins, photo-activated for 40 s with two different light guide tips, fiber optic and polymer. Five specimens were made for each group evaluated. The percentage of unreacted carbon double bonds (% C═C) was determined from the ratio of absorbance intensities of aliphatic C═C (peak at 1637 cm(-1)) against internal standard before and after curing of the specimen: aromatic C-C (peak at 1610 cm(-1)). The Vickers hardness measurements were performed in a universal testing machine. A 50 gf load was used and the indenter with a dwell time of 30 seconds. The degree of conversion and hardness mean values were analyzed separately by ANOVA and Tukey's test, with a significance level set at 5%. The mean values of degree of conversion for the polymer and fiber optic light guide tip were statistically different (P<.001). The hardness mean values were statistically different among the light guide tips (P<.001), but also there was difference between top and bottom surfaces (P<.001). The results showed that the resins photo-activated with the fiber optic light guide tip promoted higher values for degree of conversion and hardness.

Evaluation of degree of conversion and hardness of dental composites photo-activated with different light guide tips

PubMed Central

Galvão, Marília Regalado; Caldas, Sergei Godeiro Fernandes Rabelo; Bagnato, Vanderlei Salvador; de Souza Rastelli, Alessandra Nara; de Andrade, Marcelo Ferrarezi

2013-01-01

Objective: The aim of this study was to evaluate the degree of conversion and hardness of different composite resins, photo-activated for 40 s with two different light guide tips, fiber optic and polymer. Methods: Five specimens were made for each group evaluated. The percentage of unreacted carbon double bonds (% C═C) was determined from the ratio of absorbance intensities of aliphatic C═C (peak at 1637 cm−1) against internal standard before and after curing of the specimen: aromatic C-C (peak at 1610 cm−1). The Vickers hardness measurements were performed in a universal testing machine. A 50 gf load was used and the indenter with a dwell time of 30 seconds. The degree of conversion and hardness mean values were analyzed separately by ANOVA and Tukey’s test, with a significance level set at 5%. Results: The mean values of degree of conversion for the polymer and fiber optic light guide tip were statistically different (P<.001). The hardness mean values were statistically different among the light guide tips (P<.001), but also there was difference between top and bottom surfaces (P<.001). Conclusions: The results showed that the resins photo-activated with the fiber optic light guide tip promoted higher values for degree of conversion and hardness. PMID:23407620

An in vitro investigation of wear resistance and hardness of composite resins.

PubMed

Cao, Liqun; Zhao, Xinyi; Gong, Xu; Zhao, Shouliang

2013-01-01

The aim of the present study was to investigate the wear resistance and hardness of five kinds of composite resins. Sixty-five specimens were fabricated with one nano-hybrid (Charisma Diamond), two micro-hybrid (3MZ250, Clearfil AP-X) and two packable (3MP60, Surefil) composite resins, according to a randomized complete block design (n=13, 8 for wear test; 5 for hardness test). The composites were filled in a rectangular mold, and light polymerization. After storage in 37°C deionized water for 24h, all specimens were tested with a custom-made toothbrush machine with a stainless-steel ball as antagonist (3N loads, 1Hz, 6×10(5) cycles) immersed in calcium fluoride slurry. Wear volume, hardness and surface structure of each tested material was examined by a three-dimensional non-contact optical profilometer, Vickers indentation technique and scanning electron microscope. The volume loss ranked from least to most as follows: Charisma Diamond, P60, Z250, Clearfil AP-X and Surefil. Regarding hardness, the rank from highest to lowest as follows: Clearfil AP-X, P60, Surefil, Z250, Charisma Diamond. The interactions between wear resistance and microhardness were not significant. The custom-made machine is considered suitable to simulate sliding of an antagonist cusp on an opposing occlusal composite restoration. Nanofilled composite may have superior wear compared to other composite resins.

Effect of G-Coat Plus on the mechanical properties of glass-ionomer cements.

PubMed

Bagheri, R; Taha, N A; Azar, M R; Burrow, M F

2013-12-01

Although various mechanical properties of tooth-coloured materials have been described, little data have been published on the effect of ageing and G-Coat Plus on the hardness and strength of the glass-ionomer cements (GICs). Specimens were prepared from one polyacid-modified resin composite (PAMRC; Freedom, SDI), one resin-modified glass-ionomer cement; (RM-GIC; Fuji II LC, GC), and one conventional glass-ionomer cement; (GIC; Fuji IX, GC). GIC and RM-GIC were tested both with and without applying G-Coat Plus (GC). Specimens were conditioned in 37 °C distilled water for either 24 hours, four and eight weeks. Half the specimens were subjected to a shear punch test using a universal testing machine; the remaining half was subjected to Vickers Hardness test. Data analysis showed that the hardness and shear punch values were material dependent. The hardness and shear punch of the PAMRC was the highest and GIC the lowest. Applying the G-Coat Plus was associated with a significant decrease in the hardness of the materials but increase in the shear punch strength after four and eight weeks. The mechanical properties of the restorative materials were affected by applying G-Coat Plus and distilled water immersion over time. The PAMRC was significantly stronger and harder than the RM-GIC or GIC. © 2013 Australian Dental Association.

A study on hardness behavior of geopolymer paste in different condition

NASA Astrophysics Data System (ADS)

Zainal, Farah Farhana; Hussin, Kamarudin; Rahmat, Azmi; Abdullah, Mohd Mustafa Al Bakri; Shamsudin, Shaiful Rizam

2016-07-01

This study has been conducted to understand the hardness behavior of geopolymer paste in different conditions; with and without being immersed in water. Geopolymer paste has been used nowadays as an alternative way to reduce global warming pollution by carbon dioxide (CO2) released to the air caused from the production of Ordinary Portland Cement (OPC). Geopolymer has many advantages such as high compressive strength, lower water absorption and lower porosity. Geopolymer paste in this study was made from a mixture of fly ash and alkaline activators. The alkaline activators that have been used were sodium hydroxide (NaOH) solution and sodium silicate (Na2SiO3) solution. Then the mixture was allowed to harden for 24hrs at ambient temperature and then placed in the oven for 24hrs with 60°C for the curing process. The hardness testing was conducted after a few months when the samples already achieved the optimum design. The samples were divided to two conditions; without immersion which was placed at ambient temperature (S1) and immersed in water for one week (S2). The samples then are divided into two at the center and testing was conducted into 4 parts which are part 1, part 2, part 3 and part 4. Various methods of non-destructively testing concrete and mortar have been in use for many years such as Vickers hardness test, Rockwell hardness test, Brinell hardness test and many more. The Rockwell hardness test method as defined in ASTM E-18 is the most commonly used hardness test method which is also used in this study. From the results, S1 has higher hardness value than S2 for all parts with the maximum value of S1 is 118.6 and the minimum value is 71.8. The maximum value of S2 is 114.4 and the minimum value is 0. The central part of the geopolymer paste also showed greater hardness values than the edge area of the samples.

Mechanical properties and three-body wear of dental restoratives and their comparative flowable materials.

PubMed

Schultz, Sabine; Rosentritt, Martin; Behr, Michael; Handel, Gerhard

2010-01-01

To compare wear performance and resistance to crack propagation (K1C) of commercial restorative materials and their flowable variations. A potential correlation between three-body wear and fracture toughness, modulus of elasticity, fracture work, Vickers hardness, and filler content was investigated. Seven restoratives (five composites, one ormocer, and one compomer) and their corresponding flowable materials were used to determine and compare the three-body wear with a bolus of millet-seed shells and rice food (Willytec). The wear characteristics were measured by profilometry after 50,000, 100,000, 150,000, and 200,000 loading cycles. The fracture toughness value, K1C (MPam1/2), for each single-edged notched specimen was measured in a three-point bending test (universal testing machine 1446, Zwick). Fracture work and modulus of elasticity were calculated from the load curves. Vickers hardness was measured (HV hardness tester, Zwick) according to DIN 50133. The veneering composite Sinfony (3M ESPE) was used as a reference material. Heavily filled composites experienced less wear than their flowable variations. The nanofiller composites revealed better wear results than hybrid composites, compomers, and ormocers. After 200,000 load cycles, the lowest wear rates were detected for Grandio (14 microm; Voco), and the highest mean values were found for Dyract AP (104 microm; Dentsply DeTrey). The values for fracture toughness (K1C) ranged from 0.82 to 3.64 MPam1/2. Highest K1C data was exhibited by the nanocomposite Nanopaq (Schutz Dental). All tested restorative materials exhibited higher fracture toughness than their low-viscosity variations. The wear resistance of the newer generation composites with incorporated nanofiller or microfiller particles increased to a high extent. Flowables show less resistance against wear and crack propagation because of their lower filler content. The reduced mechanical properties limit their use as a restorative to small noncontact, low-stress clinical situations.

Measure of microhardness, fracture toughness and flexural strength of N-vinylcaprolactam (NVC)-containing glass-ionomer dental cements.

PubMed

Moshaverinia, Alireza; Brantley, William A; Chee, Winston W L; Rohpour, Nima; Ansari, Sahar; Zheng, Fengyuan; Heshmati, Reza H; Darr, Jawwad A; Schricker, Scott R; Rehman, Ihtesham U

2010-12-01

To investigate the effects of N-vinylcaprolactam (NVC)-containing terpolymers on the fracture toughness, microhardness, and flexural strength of conventional glass-ionomer cements (GIC). The terpolymer of acrylic acid (AA)-itaconic acid (IA)-N-vinylcaprolactam (NVC) with 8:1:1 (AA:IA:NVC) molar ratio was synthesized by free radical polymerization and characterized using (1)H NMR and FTIR. Experimental GIC samples were made from a 50% solution of the synthesized terpolymer with Fuji IX powder in a 3.6:1 P/L ratio. Specimens were mixed and fabricated at room temperature. Plane strain fracture toughness (K(Ic)) was measured in accordance with ASTM Standard 399-05. Vickers hardness was determined using a microhardness tester. Flexural strength was measured using samples with dimensions of 2 mm×2 mm×20 mm. For all mechanical property tests, specimens were first conditioned in distilled water at 37°C for 1 day or 1 week. Fracture toughness and flexural strength tests were conducted on a screw-driven universal testing machine using a crosshead speed of 0.5mm/min. Values of mechanical properties for the experimental GIC were compared with the control group (Fuji IX GIC), using one-way ANOVA and the Tukey multiple range test at α=0.05. The NVC-modified GIC exhibited significantly higher fracture toughness compared to the commercially available Fuji IX GIC, along with higher mean values of flexural strength and Vickers hardness, which were not significantly different. It was concluded that NVC-containing polymers are capable of enhancing clinically relevant properties for GICs. This new modified glass-ionomer is a promising restorative dental material. Copyright © 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of Thickness on Light Transmission and Vickers Hardness of Five Bulk-fill Resin-based Composites Using Polywave and Single-peak Light-emitting Diode Curing Lights.

PubMed

Maghaireh, G A; Price, R B; Abdo, N; Taha, N A; Alzraikat, H

2018-06-28

This study compared light transmission through different thicknesses of bulk-fill resin-based composites (RBCs) using a polywave and a single-peak light-emitting diode light-curing unit (LCU). The effect on the surface hardness was also evaluated. Five bulk-fill RBCs were tested. Specimens (n=5) of 1-, 2-, 4-, or 6-mm thickness were photopolymerized for 10 seconds from the top using a polywave (Bluephase Style) or single-peak (Elipar S10) LCU, while a spectrophotometer monitored in real time the transmitted irradiance and radiant exposure reaching the bottom of the specimen. After 24 hours of storage in distilled water at 37°C, the Vickers microhardness (VH) was measured at top and bottom. Results were analyzed using multiple-way analysis of variance, Tukey post hoc tests, and multivariate analysis (α=0.05). The choice of LCU had no significant effect on the total amount of light transmitted through the five bulk-fill RBCs at each thickness. There was a significant decrease in the amount of light transmitted as the thickness increased for all RBCs tested with both LCUs ( p<0.001). Effect of LCU on VH was minimal (η p 2 =0.010). The 1-, 2-, and 4-mm-thick specimens of SDR, X-tra Fill, and Filtek Bulk Restorative achieved a VH bottom/top ratio of approximately 80% when either LCU was used. The total amount of light transmitted through the five bulk-fill RBCs was similar at the different thicknesses using either LCU. The polywave LCU used in this study did not enhance the polymerization of the tested bulk-fill RBCs when compared with the single-peak LCU.

Metallurgical effects on titanium by laser welding on dental stone.

PubMed

Fujioka, Sonosuke; Kakimoto, Kazutoshi; Inoue, Taro; Okazaki, Joji; Komasa, Yutaka

2003-12-01

It is not known for certain that dental stone components influence titanium welding. In this study, we investigated metallurgical problems caused by laser welding on dental stones using wrought commercial pure (CP) titanium. A pulsed Nd:YAG laser irradiated a number of specimens' surfaces which were fixed on either a dental hard stone or a titanium plate. The metallurgical properties of the weld were evaluated using the Vickers hardness test, microstructure observation, fractured surface observation and quantitative analysis of oxygen and hydrogen. In the weld formed on the dental stone there was an increase in hardness, the existence of an acicular structure and a brittle fractured surface, and an increase in the oxygen and hydrogen concentrations compared with base metal. In the weld formed on the titanium plate, these changes were not observed. Therefore, it was demonstrated that laser welding on dental stones made the welds brittle.

Microstructure and properties of 17-4PH steel plasma nitrocarburized with a carrier gas containing rare earth elements

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, R.L., E-mail: ruiliangliu@126.com; Yan, M.F., E-mail: yanmufu@hit.edu.cn; Wu, Y.Q.

2010-01-15

The effect of rare earth addition in the carrier gas on plasma nitrocarburizing of 17-4PH steel was studied. The microstructure and crystallographically of the phases in the surface layer as well as surface morphology of the nitrocarburized specimens were characterized by optical microscope, X-ray diffraction and scanning tunneling microscope, respectively. The hardness of the surface layer was measured by using a Vickers hardness test. The results show that the incorporation of rare earth elements in the carrier gas can increase the nitrocarburized layer thickness up to 55%, change the phase proportion in the nitrocarburized layer, refine the nitrides in surfacemore » layer, and increase the layer hardness above 100HV. The higher surface hardening effect after rare earth addition is caused by improvement in microstructure and change in the phase proportion of the nitrocarburized layer.« less

Study of the mechanical properties of hybrid composite basalt / alumina / shells for brake lining pads

NASA Astrophysics Data System (ADS)

Adi Atmika, I. K.; Ary Subagia, IDG.; Surata, I. W.; Sutantra, I. N.

2017-05-01

Brake lining pad as one of the active safety components in motor vehicles has been studied thoroughly. Asbestos is the main material forming the brake in addition to other alloy materials that have a negative impact on health and the environment. This paper explain the behavior of hybrid composites phenolic resin with basalt/alumina/clamshell powder reinforced on brake lining pad. This materials has been manufactured use compaction and sintering process through any steps, that an emphasis of 2,000 kg for 30 minutes at a constant temperature of 150° C. The research aims to investigate hardness characteristic of hybrid composite that test using the vickers according to standard ASTM E-384. The reinforced materials and phenolic resin composition is 60%: 40%. The results show for the average hardness VHN to 24.18, 25.11, 26.34, 27.21 and 28.83. The average hardness hybrid composite shows the hardness harder than asbestos materials.

Influence of microstructure on hardness of plasma sprayed Al2O3-TiO2-MgO coatings with interface diffusion by heat treatment

NASA Astrophysics Data System (ADS)

Chen, Kunlun; Song, Peng; Li, Chao; Lu, Jiansheng

2017-12-01

The effect of heat treatment on the microstructure and mechanical properties of Al2O3-TiO2 coatings doped with 5 wt% MgO was investigated in this paper. The composite coatings were prepared by atmospheric plasma spraying (APS) and heat treated at 1000 °C for 24 h in Ar. The coatings were analyzed using scanning electron microscopy with electron probe x-ray microanalysis and x-ray diffraction. The hardness was determined using a Vickers hardness test on the as-sprayed coatings and after heat treatment. The results showed that the interface diffusion between the Al-rich and Ti-rich layers resulted in mutual pinning within the coating during the heat treatment. The newly formed MgAl2O4 phase promoted cracking-healing behavior within the coating. We conclude that increase of the hardness of the coatings was mainly caused by the mutual pinning interface and crack healing.

Metallurgical and electrochemical characterization of contemporary silver-based soldering alloys.

PubMed

Ntasi, Argyro; Al Jabbari, Youssef; Mueller, Wolf Dieter; Eliades, George; Zinelis, Spiros

2014-05-01

To investigate the microstructure, hardness, and electrochemical behavior of four contemporary Ag-based soldering alloys used for manufacturing orthodontic appliances. The Ag-based alloys tested were Dentaurum Universal Silver Solder (DEN), Orthodontic Solders (LEO), Ortho Dental Universal Solder (NOB), and Silver Solder (ORT). Five disk-shaped specimens were produced for each alloy, and after metallographic preparation their microstructural features, elemental composition, and hardness were determined by scanning electron microscopy with energy-dispersive X-ray (EDX) microanalysis, X-ray diffraction (XRD) analysis, and Vickers hardness testing. The electrochemical properties were evaluated by anodic potentiodynamic scanning in 0.9% NaCl and Ringer's solutions. Hardness, corrosion current (Icorr), and corrosion potential (Ecorr) were statistically analyzed by one-way analysis of variance and Tukey test (α=.05). EDX analysis showed that all materials belong to the Ag-Zn-Cu ternary system. Three different mean atomic contrast phases were identified for LEO and ORT and two for DEN and NOB. According to XRD analysis, all materials consisted of Ag-rich and Cu-rich face-centered cubic phases. Hardness testing classified the materials in descending order as follows: DEN, 155±3; NOB, 149±3; ORT, 141±4; and LEO, 136±8. Significant differences were found for Icorr of NOB in Ringer's solution and Ecorr of DEN in 0.9% NaCl solution. Ag-based soldering alloys demonstrate great diversity in their elemental composition, phase size and distribution, hardness, and electrochemical properties. These differences may anticipate variations in their clinical performance.

Improvement in hardness of soda-lime-silica glass

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chakraborty, Riya; De, Moumita; Roy, Sudakshina

2012-06-05

Hardness is a key design parameter for structural application of brittle solids like glass. Here we report for the first time the significant improvement of about 10% in Vicker's hardness of a soda-lime-silica glass with loading rate in the range of 0.1-10 N.s{sup -1}. Corroborative dark field optical and scanning electron microscopy provided clue to this improvement through evidence of variations in spatial density of shear deformation band formation as a function of loading rate.

Anti-scratch AlMgB14 Gorilla® Glass coating

NASA Astrophysics Data System (ADS)

Putrolaynen, V. V.; Grishin, A. M.; Rigoev, I. V.

2017-10-01

Hard aluminum-magnesium boride (BAM) films were fabricated onto Corning® Gorilla® Glass by radio-frequency magnetron sputtering of a single stoichiometric AlMgB14 target. BAM films exhibit a Vickers hardness from 10 to 30 GPa and a Young's modulus from 80 to 160 GPa depending on applied loading forces. Deposited hard coating increases the critical load at which glass substrate cracks. The adhesion energy of BAM films on Gorilla® Glass is 6.4 J/m2.

Crack-resistant Al2O3–SiO2 glasses

PubMed Central

Rosales-Sosa, Gustavo A.; Masuno, Atsunobu; Higo, Yuji; Inoue, Hiroyuki

2016-01-01

Obtaining “hard” and “crack-resistant” glasses have always been of great important in glass science and glass technology. However, in most commercial glasses both properties are not compatible. In this work, colorless and transparent xAl2O3–(100–x)SiO2 glasses (30 ≤ x ≤ 60) were fabricated by the aerodynamic levitation technique. The elastic moduli and Vickers hardness monotonically increased with an increase in the atomic packing density as the Al2O3 content increased. Although a higher atomic packing density generally enhances crack formation in conventional oxide glasses, the indentation cracking resistance increased by approximately seven times with an increase in atomic packing density in binary Al2O3–SiO2 glasses. In particular, the composition of 60Al2O3•40SiO2 glass, which is identical to that of mullite, has extraordinary high cracking resistance with high elastic moduli and Vickers hardness. The results indicate that there exist aluminosilicate compositions that can produce hard and damage-tolerant glasses. PMID:27053006

Crack-resistant Al2O3-SiO2 glasses

NASA Astrophysics Data System (ADS)

Rosales-Sosa, Gustavo A.; Masuno, Atsunobu; Higo, Yuji; Inoue, Hiroyuki

2016-04-01

Obtaining “hard” and “crack-resistant” glasses have always been of great important in glass science and glass technology. However, in most commercial glasses both properties are not compatible. In this work, colorless and transparent xAl2O3-(100-x)SiO2 glasses (30 ≤ x ≤ 60) were fabricated by the aerodynamic levitation technique. The elastic moduli and Vickers hardness monotonically increased with an increase in the atomic packing density as the Al2O3 content increased. Although a higher atomic packing density generally enhances crack formation in conventional oxide glasses, the indentation cracking resistance increased by approximately seven times with an increase in atomic packing density in binary Al2O3-SiO2 glasses. In particular, the composition of 60Al2O3•40SiO2 glass, which is identical to that of mullite, has extraordinary high cracking resistance with high elastic moduli and Vickers hardness. The results indicate that there exist aluminosilicate compositions that can produce hard and damage-tolerant glasses.

Boronization and Carburization of Superplastic Stainless Steel and Titanium-Based Alloys

PubMed Central

Matsushita, Masafumi

2011-01-01

Bronization and carburization of fine-grain superplastic stainless steel is reviewed, and new experimental results for fine grain Ti88.5Al4.5V3Fe2Mo2 are reported. In superplastic duplex stainless steel, the diffusion of carbon and boron is faster than in non-superplastic duplex stainless steel. Further, diffusion is activated by uniaxial compressive stress. Moreover, non-superplastic duplex stainless steel shows typical grain boundary diffusion; however, inner grain diffusion is confirmed in superplastic stainless steel. The presence of Fe and Cr carbides or borides is confirmed by X-ray diffraction, which indicates that the diffused carbon and boron react with the Fe and Cr in superplastic stainless steel. The Vickers hardness of the carburized and boronized layers is similar to that achieved with other surface treatments such as electro-deposition. Diffusion of boron into the superplastic Ti88.5Al4.5V3Fe2Mo2 alloy was investigated. The hardness of the surface exposed to boron powder can be increased by annealing above the superplastic temperature. However, the Vickers hardness is lower than that of Ti boride. PMID:28824144

Nanoclay-Reinforced Glass-Ionomer Cements: In Vitro Wear Evaluation and Comparison by Two Wear-Test Methods

PubMed Central

Fareed, Muhammad A.; Stamboulis, Artemis

2017-01-01

Glass ionomer cement (GIC) represents a major transformation in restorative dentistry. Wear of dental restoratives is a common phenomenon and the determination of the wear resistance of direct-restorative materials is a challenging task. The aim of this paper was to evaluate the wear resistance of novel glass ionomer cement by two wear-test methods and to compare the two wear methods.The wear resistance of a conventional glass ionomer cement (HiFi Advanced Health Care Kent, UK) and cements modified by including various percentages of nanoclays (1, 2 and 4 wt %) was measured by a reciprocating wear test (ball-on-flat) and Oregon Health and Sciences University’s (OHSU) wear simulator. The OHSU wear simulation subjected the cement specimens to three wear mechanisms, namely abrasion, three-body abrasion and attrition using a steatite antagonist. The abrasion wear resulted in material loss from GIC specimen as the steatite antagonist forced through the exposed glass particles when it travelled along the sliding path.The hardness of specimens was measured by the Vickers hardness test. The results of reciprocation wear test showed that HiFi-1 resulted in the lowest wear volume 4.90 (0.60) mm3 (p < 0.05), but there was no significant difference (p > 0.05) in the wear volume in comparison to HiFi, HiFi-2 and HiFi-4. Similarly, the results of OHSU wear simulator showed that the total wear volume of HiFi-4 1.49 (0.24) was higher than HiFi-1 and HiFi-2. However, no significant difference (p > 0.05) was found in the OHSU total wear volume in GICs after nanoclay incorporation. The Vickers hardness (HV) of the nanoclay-reinforced cements was measured between 62 and 89 HV. Nanoclay addition at a higher concentration (4%) resulted in higher wear volume and wear depth. The total wear volumes were less dependent upon abrasion volume and attrition volume. The total wear depths were strongly influenced by attrition depth and to some extent by abrasion depth. The addition of nanoclay in higher wt % to HiFi did not result in significant improvement in wear resistance and hardness. Nonetheless, wear is a very complex phenomenon because it is sensitive to a wide number of factors that do not necessarily act in the same way when compared using different parameters. PMID:29563434

Thermal Shock and Ablation Behavior of Tungsten Nozzle Produced by Plasma Spray Forming and Hot Isostatic Pressing

NASA Astrophysics Data System (ADS)

Wang, Y. M.; Xiong, X.; Zhao, Z. W.; Xie, L.; Min, X. B.; Yan, J. H.; Xia, G. M.; Zheng, F.

2015-08-01

Tungsten nozzle was produced by plasma spray forming (PSF, relative density of 86 ± 2%) followed by hot isostatic pressing (HIPing, 97 ± 2%) at 2000 °C and 180 MPa for 180 min. Scanning electron microscope, x-ray diffractometer, Archimedes method, Vickers hardness, and tensile tests have been employed to study microstructure, phase composition, density, micro-hardness, and mechanical properties of the parts. Resistance of thermal shock and ablation behavior of W nozzle were investigated by hot-firing test on solid rocket motor (SRM). Comparing with PSF nozzle, less damage was observed for HIPed sample after SRM test. Linear ablation rate of nozzle made by PSF was (0.120 ± 0.048) mm/s, while that after HIPing reduced to (0.0075 ± 0.0025) mm/s. Three types of ablation mechanisms including mechanical erosion, thermophysical erosion, and thermochemical ablation took place during hot-firing test. The order of degree of ablation was nozzle throat > convergence > dilation inside W nozzle.

Green synthesis and characterization of Ag nanoparticles from Mangifera indica leaves for dental restoration and antibacterial applications.

PubMed

Sundeep, Dola; Vijaya Kumar, T; Rao, P S Subba; Ravikumar, R V S S N; Gopala Krishna, A

2017-05-01

Green synthesis has gained a wide recognition as clean synthesis technique in the recent years. In the present investigation, silver nanoparticles were prepared by a novel green synthesis technique using Mangifera indica (Mango leaves) and found to be successfully used in dental applications. The prepared samples were spectroscopically characterized by XRD, PSA, SEM with EDS, and UV-Vis spectroscopy. The crystalline size and lattice strain were analyzed from the XRD data which were counter-verified by W-H plots and particle size analyzer. The XRD peaks revealed that average crystalline size of the as-synthesized Ag nanoparticles was of 32.4 nm with face-centered cubic structure. This was counter-verified by particle size analyzer and Williamson-Hall plots and found to be 31.7 and 33.21 nm in the former and latter, and the crystalline size of Ag NPs could be concluded as 32 ± 2 nm. The morphological structure of the prepared sample was studied through SEM images and the chemical composition was analyzed by the EDS data. The band energy was calculated as 393 nm from UV-Vis, which confirmed the synthesized sample as Ag nanoparticles. To improve the mechanical bonding and hardness of the dentally used glass ionomer cement (GIC), the synthesized silver nanoparticles were incorporated into GIC in 2% weight ratio. The morphology of the prepared specimens was studied using optical microscope images. Vickers microhardness and Monsanto hardness tests were performed on GIC, GIC reinforced with microsilver particles and GIC reinforced with nanosilver particles and the latter derived a promising results. The results of the Monsanto tests confirmed the increase in hardness of the GIC reinforced with AgNps as 14.2 kg/cm 2 compared to conventional GIC and GIC reinforced with silver microparticle as 11.7 and 9.5 kg/cm 2 . Similarly the Vickers hardness results exhibited the enhanced hardness of GIC-reinforced AgNps as 82 VHN compared to GIC as 54 and GIC-reinforced silver microparticles as 61 VHN. The antibacterial activity of AgNPs was tested by a well-diffusion method on Escherichia coli and Staphylococcus aureus bacteria, and the obtained results exhibited a promising antibacterial activity of the as-synthesized nanoparticles.

Ceramic tools insert assesment based on vickers indentation methodology

NASA Astrophysics Data System (ADS)

Husni; Rizal, Muhammad; Aziz M, M.; Wahyu, M.

2018-05-01

In the interrupted cutting process, the risk of tool chipping or fracture is higher than continues cutting. Therefore, the selection of suitable ceramic tools for interrupted cutting application become an important issue to assure that the cutting process is running effectively. At present, the performance of ceramics tools is assessed by conducting some cutting tests, which is required time and cost consuming. In this study, the performance of ceramic tools evaluated using hardness tester machine. The technique, in general, has a certain advantage compare with the more conventional methods; the experimental is straightforward involving minimal specimen preparation and the amount of material needed is small. Three types of ceramic tools AS10, CC650 and K090 have been used, each tool was polished then Vickers indentation test were performed with the load were 0.2, 0.5, 1, 2.5, 5 and 10 kgf. The results revealed that among the load used in the tests, the indentation loads of 5 kgf always produce well cracks as compared with others. Among the cutting tool used in the tests, AS10 has produced the shortest crack length and follow by CC 670, and K090. It is indicated that the shortest crack length of AS10 reflected that the tool has a highest dynamic load resistance among others insert.

Prediction of the Vickers Microhardness and Ultimate Tensile Strength of AA5754 H111 Friction Stir Welding Butt Joints Using Artificial Neural Network

PubMed Central

De Filippis, Luigi Alberto Ciro; Serio, Livia Maria; Facchini, Francesco; Mummolo, Giovanni; Ludovico, Antonio Domenico

2016-01-01

A simulation model was developed for the monitoring, controlling and optimization of the Friction Stir Welding (FSW) process. This approach, using the FSW technique, allows identifying the correlation between the process parameters (input variable) and the mechanical properties (output responses) of the welded AA5754 H111 aluminum plates. The optimization of technological parameters is a basic requirement for increasing the seam quality, since it promotes a stable and defect-free process. Both the tool rotation and the travel speed, the position of the samples extracted from the weld bead and the thermal data, detected with thermographic techniques for on-line control of the joints, were varied to build the experimental plans. The quality of joints was evaluated through destructive and non-destructive tests (visual tests, macro graphic analysis, tensile tests, indentation Vickers hardness tests and t thermographic controls). The simulation model was based on the adoption of the Artificial Neural Networks (ANNs) characterized by back-propagation learning algorithm with different types of architecture, which were able to predict with good reliability the FSW process parameters for the welding of the AA5754 H111 aluminum plates in Butt-Joint configuration. PMID:28774035

Influence of Size on the Microstructure and Mechanical Properties of an AISI 304L Stainless Steel—A Comparison between Bulk and Fibers

PubMed Central

Baldenebro-Lopez, Francisco J.; Gomez-Esparza, Cynthia D.; Corral-Higuera, Ramon; Arredondo-Rea, Susana P.; Pellegrini-Cervantes, Manuel J.; Ledezma-Sillas, Jose E.; Martinez-Sanchez, Roberto; Herrera-Ramirez, Jose M.

2015-01-01

In this work, the mechanical properties and microstructural features of an AISI 304L stainless steel in two presentations, bulk and fibers, were systematically studied in order to establish the relationship among microstructure, mechanical properties, manufacturing process and effect on sample size. The microstructure was analyzed by XRD, SEM and TEM techniques. The strength, Young’s modulus and elongation of the samples were determined by tensile tests, while the hardness was measured by Vickers microhardness and nanoindentation tests. The materials have been observed to possess different mechanical and microstructural properties, which are compared and discussed. PMID:28787949

Effects of environment on microhardness of magnesium oxide

NASA Technical Reports Server (NTRS)

Ishigaki, H.; Buckley, D. H.

1982-01-01

Micro-Vickers hardness measurements of magnesium oxide single crystals were conducted in various environments. These environments included air, nitrogen gas, water, mineral oil with or without various additives, and aqueous solutions with various pH values. Indentations were made on the (100) plane with the diagonals of the indentation in the (100) direction. The results indicate that a sulfur containing additve in mineral oil increased hardness, a chlorine containing additive in mineral oil decreased hardness, and aqueous solutions of hydrogen chloride decreased hardness. Other environments were found to have little effect on hardness. Mechanically polished surfaces showed larger indentation creep than did as-cleaved surfaces.

[Evaluation of mechanical properties of four kinds of composite resins for inlay].

PubMed

Jiang, Ling-ling; Liu, Hong; Wang, Jin-rui

2011-04-01

To evaluate the compressive strength, wear resistance, hardness, and soaking fatigue of four composite resins for inlay, which were Ceramage, Surefil, Solitaire 2, and Filtek(TM) Z350. Scanning electron microscope (SEM) was used to analyze the microstructures of the wear surface of the samples. The samples for the compression test, hardness test and wear were prepared. The samples were respectively immersed in the artificial saliva for 2 months for immersed test. The electronic universal testing machine was used to test the compression strength. Hardness was quantified by micro-Vickers hardness test. The wear tester was used for the wear test. SEM was used to analyze the microstructures of the wear surface of samples. All the data was analyzed by using SPSS17.0 software package. The compressive strength of Surefil was the biggest which was significantly higher than the other three resins before soaking (P<0.05). After soaking, there was no significant difference between the composite resins (P>0.05). The hardness of Surefil was the best, and significant difference was found between the hardness of the materials before soaking (P<0.05). After soaking, no significant difference was obtained between the hardness of Surefil and Filtek(TM) Z350 (P>0.05).The compressive strength and hardness of 4 materials decreased after soaking in artificial saliva. But only the compressive strength of Filtek(TM) Z350 had no significant change after immersion (P>0.05). Except Filtek(TM) Z350, there was significant difference between the other three materials (P<0.05). Significant relationship was observed between wear and hardness of three materials (P<0.05). According to SEM observation, abrasive wear occurred in four materials. In addition to Ceramage, other composite resins had adhesive wear. The mechanical property of Surefil is the best, and it is suitable for fabrication of posterior inlay. Filtek(TM) Z350's ability to resist fatigue is the best.

Enhancement of as-sputtered silver-tantalum oxide thin film coating on biomaterial stainless steel by surface thermal treatment

NASA Astrophysics Data System (ADS)

Alias, Rodianah; Mahmoodian, Reza; Shukor, Mohd Hamdi Abd; Yew, Been Seok; Muhamad, Martini

2018-04-01

Stainless steel 316L (SS316L) is extensively used as surgical/clinical tools due to its low carbon content and excellent mechanical characteristic. The fabrication of metal ceramic based on this metallic biomaterial favor its biofunctionality properties. However, instability phase of amorphous thin film lead to degradation, corrosion and oxidation. Thus, thin film coating requires elevated adhesion strength and higher surface hardness to meet clinical tools criteria. In this study, the SS316L was deposited with micron thickness of Ag-TaO thin film by using magnetron sputtering. The microstructure, elemental analysis and phase identification of Ag-TaO thin film were characterized by using FESEM, EDX and XRD, respectively; whereas the micro scratch test and micro hardness test were performed by using Micro Scratch Testing System and Vickers Micro Hardness Tester, respectively. It was found that the coating thin film's adhesion and hardness strength were improved from 672 to 2749 mN and 142 to 158 Hv respectively. It was found that the as-deposited surface were treated at 500 °C of temperatures with 2 °C/min ramping rate enhance 4.1 times of the adhesion strength value. Furthermore, FESEM characterization revealed coarsening structure of the thin film coating which can provide high durability service.

Synthesis and Characterization of Low-Cost Superhard Transition-Metal Borides

NASA Astrophysics Data System (ADS)

Kaner, Richard

2013-06-01

The increasing demand for high-performance cutting and forming tools, along with the shortcomings of traditional tool materials such as diamond (unable to cut ferrous materials), cubic boron nitride (expensive) and tungsten carbide (relatively-low hardness), has motivated the search for new superhard materials for these applications. This has led us to a new class of superhard materials, dense refractory transition-metal borides, which promise to address some of the existing problems of conventional superhard materials. For example, we have synthesized rhenium diboride (ReB2) using arc melting at ambient pressure. This superhard material has demonstrated an excellent electrical conductivity and superior mechanical properties, including a Vickers hardness of 48.0 GPa (under an applied load of 0.49 N). To further increase the hardness and lower the materials costs, we have begun exploring high boron content metal borides including tungsten tetraboride (WB4) . We have synthesized WB4 by arc melting and studied its hardness and high-pressure behavior. With a similar Vickers hardness (43.3 GPa under a load of 0.49 N) and bulk modulus (326-339 GPa) to ReB2, WB4 offers a lower cost alternative and has the potential to be used in cutting tools. To further enhance the hardness of this superhard metal, we have created the binary and ternary solid solutions of WB4 with Cr, Mn and Ta, the results of which show a hardness increase of up to 20 percent. As with other metals, these metallic borides can be readily cut and shaped using electric discharge machining (EDM).

Microstructure and Mechanical Behaviors of Titanium Matrix Composites Containing In Situ Whiskers Synthesized via Plasma Activated Sintering.

PubMed

Sun, Yi; Zhang, Jian; Luo, Guoqiang; Shen, Qiang; Zhang, Lianmeng

2018-04-02

In this paper, titanium matrix composites with in situ TiB whiskers were synthesized by the plasma activated sintering technique; crystalline boron and amorphous boron were used as reactants for in situ reactions, respectively. The influence of the sintering process and the crystallography type of boron on the microstructure and mechanical properties of composites were studied and compared. The densities were evaluated using Archimedes' principle. The microstructure and mechanical properties were characterized by SEM, XRD, EBSD, TEM, a universal testing machine, and a Vickers hardness tester. The prepared composite material showed a high density and excellent comprehensive performance under the PAS condition of 20 MPa at 1000 °C for 3 min. Amorphous boron had a higher reaction efficiency than crystalline boron, and it completely reacted with the titanium matrix to generate TiB whiskers, while there was still a certain amount of residual crystalline boron combining well with the titanium matrix at 1100 °C. The composite samples with a relative density of 98.33%, Vickers hardness of 389.75 HV, compression yield strength of up to 1190 MPa, and an ultimate compressive strength of up to 1710 MPa were obtained. Compared with the matrix material, the compressive strength of TC4 titanium alloy containing crystalline boron and amorphous boron was increased by 7.64% and 15.50%, respectively.

Microstructure and Mechanical Behaviors of Titanium Matrix Composites Containing In Situ Whiskers Synthesized via Plasma Activated Sintering

PubMed Central

Luo, Guoqiang; Shen, Qiang; Zhang, Lianmeng

2018-01-01

In this paper, titanium matrix composites with in situ TiB whiskers were synthesized by the plasma activated sintering technique; crystalline boron and amorphous boron were used as reactants for in situ reactions, respectively. The influence of the sintering process and the crystallography type of boron on the microstructure and mechanical properties of composites were studied and compared. The densities were evaluated using Archimedes’ principle. The microstructure and mechanical properties were characterized by SEM, XRD, EBSD, TEM, a universal testing machine, and a Vickers hardness tester. The prepared composite material showed a high density and excellent comprehensive performance under the PAS condition of 20 MPa at 1000 °C for 3 min. Amorphous boron had a higher reaction efficiency than crystalline boron, and it completely reacted with the titanium matrix to generate TiB whiskers, while there was still a certain amount of residual crystalline boron combining well with the titanium matrix at 1100 °C. The composite samples with a relative density of 98.33%, Vickers hardness of 389.75 HV, compression yield strength of up to 1190 MPa, and an ultimate compressive strength of up to 1710 MPa were obtained. Compared with the matrix material, the compressive strength of TC4 titanium alloy containing crystalline boron and amorphous boron was increased by 7.64% and 15.50%, respectively. PMID:29614842

A comparison of the wear resistance and hardness of indirect composite resins.

PubMed

Mandikos, M N; McGivney, G P; Davis, E; Bush, P J; Carter, J M

2001-04-01

Various new, second-generation indirect composites have been developed with claimed advantages over existing tooth-colored restorative materials. To date, little independent research has been published on these materials, and the properties specified in the advertising materials are largely derived from in-house or contracted testing. Four second-generation indirect composites (Artglass, belleGlass, Sculpture, and Targis) were tested for wear resistance and hardness against 2 control materials with well-documented clinical application. Human enamel was also tested for comparison. Twelve specimens of each material were fabricated according to the manufacturers' directions and subjected to accelerated wear in a 3-body abrasion, toothbrushing apparatus. Vickers hardness was measured for each of the tested materials, and energy dispersive x-ray (EDX) spectroscopy was performed to determine the elemental composition of the composite fillers. The statistical tests used for wear and hardness were the Kruskal-Wallis 1-way ANOVA test with Mann-Whitney tests and 1-way ANOVA with multiple comparisons (Tukey HSD). The Pearson correlation coefficient was used to determine the existence of a relationship between the hardness of the materials and the degree to which they had worn. The level of statistical significance chosen was alpha=.05. The control material Concept was superior to the other composites in wear resistance and hardness and had the lowest surface roughness. Significant relationships were observed between depth of wear and hardness and between depth of wear and average surface roughness. Enamel specimens were harder and more wear resistant than any of the composites. EDX spectroscopy revealed that the elemental composition of the fillers of the 4 new composites was almost identical, as was the composition of the 2 control composites. The differences in wear, hardness, and average surface roughness may have been due to differences in the chemistry or method of polymerization of the composites. Further research in this area should be encouraged. It was also apparent that the filler present in the tested composites did not exactly fit the manufacturers' descriptions.

Fretting Fatigue Experiment and Analysis of AlSi9Cu2Mg Alloy

PubMed Central

Wang, Jun; Xu, Hong; Su, Tiexiong; Zhang, Yi; Guo, Zhen; Mao, Huping; Zhang, Yangang

2016-01-01

An investigation was carried out in order to study the fretting fatigue behavior of an AlSi9Cu2Mg aluminum alloy. The fretting fatigue tests of AlSi9Cu2Mg were performed using a specially designed testing machine. The failure mechanism of fretting fatigue was explored by studying the fracture surfaces, fretting scars, fretting debris, and micro-hardness of fretting fatigue specimens using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and micro Vickers hardness test techniques. The experimental results show that the fretting fatigue limit (42 MPa) is significantly reduced to approximately 47% of the plain fatigue limit (89 MPa) under 62.5 MPa contact pressure. Furthermore, the fretting fatigue life decreases with increasing alternating stress and increasing contact pressure. The examination results suggest that the stress concentrates induced by oxidation-assisted wear on the contact interface led to the earlier initiation and propagation of crack under the fretting condition. PMID:28774103

Fretting Fatigue Experiment and Analysis of AlSi9Cu2Mg Alloy.

PubMed

Wang, Jun; Xu, Hong; Su, Tiexiong; Zhang, Yi; Guo, Zhen; Mao, Huping; Zhang, Yangang

2016-12-05

An investigation was carried out in order to study the fretting fatigue behavior of an AlSi9Cu2Mg aluminum alloy. The fretting fatigue tests of AlSi9Cu2Mg were performed using a specially designed testing machine. The failure mechanism of fretting fatigue was explored by studying the fracture surfaces, fretting scars, fretting debris, and micro-hardness of fretting fatigue specimens using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and micro Vickers hardness test techniques. The experimental results show that the fretting fatigue limit (42 MPa) is significantly reduced to approximately 47% of the plain fatigue limit (89 MPa) under 62.5 MPa contact pressure. Furthermore, the fretting fatigue life decreases with increasing alternating stress and increasing contact pressure. The examination results suggest that the stress concentrates induced by oxidation-assisted wear on the contact interface led to the earlier initiation and propagation of crack under the fretting condition.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Overman, Nicole R.; Toloczko, Mychailo B.; Olszta, Matthew J.

High chromium, nickel-base Alloy 690 exhibits an increased resistance to stress corrosion cracking (SCC) in pressurized water reactor (PWR) primary water environments over lower chromium alloy 600. As a result, Alloy 690 has been used to replace Alloy 600 for steam generator tubing, reactor pressure vessel nozzles and other pressure boundary components. However, recent laboratory crack-growth testing has revealed that heavily cold-worked Alloy 690 materials can become susceptible to SCC. To evaluate reasons for this increased SCC susceptibility, detailed characterizations have been performed on as-received and cold-worked Alloy 690 materials using electron backscatter diffraction (EBSD) and Vickers hardness measurements. Examinationsmore » were performed on cross sections of compact tension specimens that were used for SCC crack growth rate testing in simulated PWR primary water. Hardness and the EBSD integrated misorientation density could both be related to the degree of cold work for materials of similar grain size. However, a microstructural dependence was observed for strain correlations using EBSD and hardness which should be considered if this technique is to be used for gaining insight on SCC growth rates« less

An in vitro investigation of wear resistance and hardness of composite resins

PubMed Central

Cao, Liqun; Zhao, Xinyi; Gong, Xu; Zhao, Shouliang

2013-01-01

Purpose: The aim of the present study was to investigate the wear resistance and hardness of five kinds of composite resins. Materials and Methods: Sixty-five specimens were fabricated with one nano-hybrid (Charisma Diamond), two micro-hybrid (3MZ250, Clearfil AP-X) and two packable (3MP60, Surefil) composite resins, according to a randomized complete block design (n=13, 8 for wear test; 5 for hardness test). The composites were filled in a rectangular mold, and light polymerization. After storage in 37°C deionized water for 24h, all specimens were tested with a custom-made toothbrush machine with a stainless-steel ball as antagonist (3N loads, 1Hz, 6×105 cycles) immersed in calcium fluoride slurry. Wear volume, hardness and surface structure of each tested material was examined by a three-dimensional non-contact optical profilometer, Vickers indentation technique and scanning electron microscope. Results: The volume loss ranked from least to most as follows: Charisma Diamond, P60, Z250, Clearfil AP-X and Surefil. Regarding hardness, the rank from highest to lowest as follows: Clearfil AP-X, P60, Surefil, Z250, Charisma Diamond. The interactions between wear resistance and microhardness were not significant. Conclusions: The custom-made machine is considered suitable to simulate sliding of an antagonist cusp on an opposing occlusal composite restoration. Nanofilled composite may have superior wear compared to other composite resins. PMID:23844265

Wear resistance of a modified polymethyl methacrylate artificial tooth compared to five commercially available artificial tooth materials.

PubMed

Kamonwanon, Pranithida; Yodmongkol, Sirasa; Chantarachindawong, Rojcharin; Thaweeboon, Sroisiri; Thaweeboon, Boonyanit; Srikhirin, Toemsak

2015-08-01

Wear resistance is a limitation of artificial denture teeth. Improving the wear resistance of conventional artificial denture teeth is of value to prosthodontic patients. The purpose of this in vitro study was to evaluate the wear resistance and hardness of modified polymethyl methacrylate artificial denture teeth compared to 5 commercially available artificial tooth materials. This study evaluated 180 artificial denture teeth (6 groups) that included 3 groups of conventional artificial teeth (MajorDent, Cosmo HXL, and Gnathostar), 2 groups of composite resin artificial teeth (Endura and SR Orthosit PE), and 1 group of modified surface artificial teeth. The flattened buccal surface of each tooth (n=15) was prepared for investigation with the Vickers hardness test and the elucidate wear test (n=15) by using a brushing machine. Each group was loaded for 18,000 cycles, at 2 N, and 150 rpm. The wear value was identified with a profilometer. The data were statistically analyzed by using 1-way ANOVA and post hoc Turkey honestly significant difference tests (α=.001). The tribologies were observed under a scanning electron microscope, and the cytotoxicities were evaluated by MTT assay. The Vickers hardnesses ranged from 28.48 to 39.36. The wear depths and worn surface area values ranged from 1.12 to 10.79 μm and from 6.74 to 161.95 μm(2). The data revealed that the modified artificial denture teeth were significantly harder and exhibited significantly higher wear resistance than did the conventional artificial teeth (P<.001). The scanning electron microscopic images revealed cross sections of the conventional artificial denture teeth with intensively worn surface areas after brushing. The cytotoxicity test revealed 97.85% cell viability, which indicates the nontoxicity of the modified surface of this material. Within the limitations of this study, the polymethyl methacrylate modified surface artificial denture teeth was not significantly different from that of the composite resin artificial denture teeth, with the exceptions that the surface was harder and more wear resistant. Copyright © 2015 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Layered Manufacturing of Dental Ceramics: Fracture Mechanics, Microstructure, and Elemental Composition of Lithography-Sintered Ceramic.

PubMed

Uçar, Yurdanur; Aysan Meriç, İpek; Ekren, Orhun

2018-02-11

To compare the fracture mechanics, microstructure, and elemental composition of lithography-based ceramic manufacturing with pressing and CAD/CAM. Disc-shaped specimens (16 mm diameter, 1.2 mm thick) were used for mechanical testing (n = 10/group). Biaxial flexural strength of three groups (In-Ceram alumina [ICA], lithography-based alumina, ZirkonZahn) were determined using the "piston on 3-ball" technique as suggested in test Standard ISO-6872. Vickers hardness test was performed. Fracture toughness was calculated using fractography. Results were statistically analyzed using Kruskal-Wallis test followed by Dunnett T3 (α = 0.05). Weibull analysis was conducted. Polished and fracture surface characterization was made using scanning electron microscope (SEM). Energy dispersive spectroscopy (EDS) was used for elemental analysis. Biaxial flexural strength of ICA, LCM alumina (LCMA), and ZirkonZahn were 147 ± 43 MPa, 490 ± 44 MPa, and 709 ± 94 MPa, respectively, and were statistically different (P ≤ 0.05). The Vickers hardness number of ICA was 850 ± 41, whereas hardness values for LCMA and ZirkonZahn were 1581 ± 144 and 1249 ± 57, respectively, and were statistically different (P ≤ 0.05). A statistically significant difference was found between fracture toughness of ICA (2 ± 0.4 MPa⋅m 1/2 ), LCMA (6.5 ± 1.5 MPa⋅m 1/2 ), and ZirkonZahn (7.7 ± 1 MPa⋅m 1/2 ) (P ≤ 0.05). Weibull modulus was highest for LCMA (m = 11.43) followed by ZirkonZahn (m = 8.16) and ICA (m = 5.21). Unlike LCMA and ZirkonZahn groups, a homogeneous microstructure was not observed for ICA. EDS results supported the SEM images. Within the limitations of this in vitro study, it can be concluded that LCM seems to be a promising technique for final ceramic object manufacturing in dental applications. Both the manufacturing method and the material used should be improved. © 2018 by the American College of Prosthodontists.

The effect of aqueous media on the mechanical properties of fluorapatite-mullite glass-ceramics.

PubMed

Mollazadeh, S; Ajalli, Siamak; Kashi, Tahereh S Jafarzadeh; Yekta, Bijan Eftekhai; Javadpour, Jafar; Jafari, S; Youssefi, Abbas; Fazel, Akbar

2015-11-01

To verify the effects of alternating thermal changes in aqueous media and chemical composition on mechanical properties of apatite-mullite glass-ceramics and to investigate concentration of ions eluted from glass-ceramics in aqueous media. The glass compositions were from SiO2Al2O3P2O5CaOTiO2BaOZrO2CaF2 system. Glass-ceramics were prepared by heat-treating at 1100°C for 3h samples alternately immersed in water at 5 and 60°C. The 3-point bending strength (n=10) were determined using 3×4×25mm/bar and a universal testing machine, at a cross-head speed of 0.1mm/min. Vickers micro hardness were evaluated by applying a total of 15-20 indentations under a 100g load for 30s. Concentrations of ions eluted from glass-ceramics immersed in 60±5°C double distilled water were determined by ion chromatography. The toxicity of glass-ceramics was assessed by seeding the osteosarcoma cells (MG63) on powder for different days and their cell proliferation assessment was investigated by MTT assay. The data were analyzed using one way analysis of variance and the means were compared by Tukey's test (5% significance level). The highest flexural strength and hardness values after thermal changes belonged to TiO2 and ZrO2 containing glass-ceramics which contained lower amount of released ions. BaO containing glass-ceramic and sample with extra amount of silica showed the highest amount of reduction in their mechanical strength values. These additives enhanced the concentration of eluted ions in aqueous media. MTT results showed that glass-ceramics were almost equivalent concerning their in-vitro biological behavior. Thermal changes and chemical compositions had significant effects on flexural strength and Vickers micro-hardness values. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of gamma irradiation on high temperature hardness of low-density polyethylene

NASA Astrophysics Data System (ADS)

Chen, Pei-Yun; Yang, Fuqian; Lee, Sanboh

2015-11-01

Gamma irradiation can cause the change of microstructure and molecular structure of polymer, resulting in the change of mechanical properties of polymers. Using the hardness measurement, the effect of gamma irradiation on the high temperature hardness of low-density polyethylene (LDPE) was investigated. The gamma irradiation caused the increase in the melting point, the enthalpy of fusion, and the portion of crystallinity of LDPE. The Vickers hardness of the irradiated LDPE increases with increasing the irradiation dose, annealing temperature, and annealing time. The activation energy for the rate process controlling the reaction between defects linearly decreases with the irradiation dose. The process controlling the hardness evolution in LDPE is endothermic because LDPE is semi-crystalline.

Fabrication and Properties of Novel NiWFeB Amorphous Alloys

NASA Astrophysics Data System (ADS)

Zhang, Jiajia; Liu, Wensheng; Ma, Yunzhu; Ye, Xiaoshan; Wu, Yayu

2017-09-01

In this work, we reported the successful synthesis of four quaternary NiWFeB amorphous alloys (Ni53.9W4.3Fe24.2B17.6, Ni49.7W9.7Fe22.3B18.3, Ni46.2W14.1Fe20.8B18.9 and Ni42.2W19.2Fe18.9B19.7 in at.%) via melt spinning method. The synthesized amorphous alloys are characterized by x-ray diffraction, transmission electron microscopy, differential scanning calorimeter, scanning electron microscopy and Vickers indenters. The results showed that the crystallization temperatures T x1 of four amorphous alloys with increased W contents, derived from the exothermic peaks in DSC, were 705, 715, 851, and 965 K, respectively. The Vickers hardness ( H v) of the corresponding four amorphous alloys at room temperature was 8.5, 9.8, 10.3, and 11.4 GPa, respectively. The much finer shear bands in the deformation region underneath the Vickers indenter were observed as the tungsten content increases. All the results showed a tendency that the higher the tungsten content, the greater the thermal stability and hardness. The results indicated the NiWFeB amorphous alloys could be easier fabricated by continuing to increase the tungsten content, and those NiWFeB amorphous alloys would have a promising application in nuclear energies and military defenses.

Composition, microstructure, Vickers hardness and activation energies of Co-Cu alloys fabricated by arc melting technique

NASA Astrophysics Data System (ADS)

Mebed, A. M.; Abd-Elnaiem, Alaa M.; Asafa, Tesleem B.; Gaffar, M. A.

2012-12-01

We have determined the phase transition for the Co-20 and -30 at.% Cu alloys fabricated by arc melting technique, from the binodal to the two phases α + L as well as the peritectic transitions, using differential thermal analysis (DTA). We equally studied the effects of aging treatment, ranging from 3 to 35 h, on the alloy samples using scanning electron microscopy (SEM) and Vickers hardness (HV). The activation energies of these alloys are equally determined using five established models. Our results show that for aging time up to 15 h, within the spinodal region at 773 K, the hardness value for Co-20 and -30 at.% Cu alloys oscillates reaching a local maximum at the aging time of 8.5 ± 0.5 h. After 20 h of heat treatment, the HV for Co-20 at.% Cu alloy diminishes significantly while that of Co-30 at.% Cu effectively stabilizes at 241 MPa. The activation energies for the peritectic transformation based on Ozawa model are estimated to be 2465 and 2680 kJ mol-1 for Co-20 and -30 at.% Cu, respectively. On leave for: Al-Jouf University, Skaka-2014, KSA.

Phase formation kinetics, hardness and magnetocaloric effect of sub-rapidly solidified LaFe11.6Si1.4 plates during isothermal annealing

NASA Astrophysics Data System (ADS)

Dai, Yuting; Xu, Zhishuai; Luo, Zhiping; Han, Ke; Zhai, Qijie; Zheng, Hongxing

2018-05-01

High-temperature phase transition behavior and intrinsic brittleness of NaZn13-type τ1 phase in La-Fe-Si magnetocaloric materials are two key problems from the viewpoint of materials production and practical applications. In the present work, the Johnson-Mehl-Avrami-Kolmogorov (JMAK) equation was introduced to quantitatively characterize the formation kinetics of τ1 phase in sub-rapidly solidified LaFe11.6Si1.4 plates during the isothermal annealing process. Avrami index was estimated to be 0.43 (∼0.5), which suggests that the formation of τ1 phase is in a diffusion-controlled one-dimensional growth mode. Meanwhile, it is found that the Vickers hardness as a function of annealing time for sub-rapidly solidified plates also agrees well with the JMAK equation. The Vickers hardness of τ1 phase was estimated to be about 754. Under a magnetic field change of 30 kOe, the maximum magnetic entropy change was about 22.31 J/(kg·K) for plates annealed at 1323 K for 48 h, and the effective magnetic refrigeration capacity reached 191 J/kg.

The influence of mineralogical, chemical and physical properties on grindability of commercial clinkers with high MgO level

DOE Office of Scientific and Technical Information (OSTI.GOV)

Souza, Vladia Cristina G. de; Koppe, Jair Carlos; Costa, Joao F.C.L.

2008-08-15

This research investigates various methods able to identify possible mineralogical, physical and chemical influences on the grindability of commercial clinkers with high MgO level. The aim of the study is to evaluate the hardness and elastic modulus of the clinker mineral phases and their fracture strength during the comminution processes, comparing samples from clinkers with low MgO level (0.5%) and clinkers with elevated MgO levels (> 5.0%). The study of the influence of mineralogical, chemical and physical properties was carried out using several analytical techniques, such as: optical microscopy, X-ray diffraction with Rietveld refinement (XRD) and X-ray fluorescence (XRF). Thesemore » techniques were useful in qualifying the different clinker samples. The drop weight test (DWT) and the Bond ball mill grindability test were performed to characterize the mechanical properties of clinkers. Nanoindentation tests were also carried out. Results from the Bond ball mill grindability test were found to be related to the hardness of the mineral phase and to mineralogical characteristics, such as type and amount of inclusions in silicates, belite and alite crystals shape, or microcracked alites. In contrast, the results obtained by the DWT were associated to the macro characteristics of clinkers, such as porosity, as well as to the hardness and mineralogical characteristics of belite crystals in clusters. Hardness instrumented tests helped to determine the Vickers hardness and elastic modulus from the mineral phases in commercial clinkers and produced different values for the pure phases compared to previous publications.« less

Repulsive Interaction of Sulfide Layers on Compressor Impeller Blades Remanufactured Through Plasma Spray Welding

NASA Astrophysics Data System (ADS)

Chang, Y.; Zhou, D.; Wang, Y. L.; Huang, H. H.

2016-12-01

This study investigated the repulsive interaction of sulfide layers on compressor impeller blades remanufactured through plasma spray welding (PSW). Sulfide layers on the blades made of FV(520)B steel were prepared through multifarious corrosion experiments, and PSW was utilized to remanufacture blade specimens. The specimens were evaluated through optical microscopy, scanning electron microscopy, energy-dispersive spectroscopy, 3D surface topography, x-ray diffraction, ImageJ software analysis, Vicker's micro-hardness test and tensile tests. Results showed a large number of sulfide inclusions in the fusion zone generated by sulfide layers embodied into the molten pool during PSW. These sulfide inclusions seriously degraded the mechanical performance of the blades remanufactured through PSW.

Identification of a novel FAM83H mutation and microhardness of an affected molar in autosomal dominant hypocalcified amelogenesis imperfecta.

PubMed

Hyun, H-K; Lee, S-K; Lee, K-E; Kang, H-Y; Kim, E-J; Choung, P-H; Kim, J-W

2009-11-01

To determine the underlying molecular genetic aetiology of a family with the hypocalcified form of amelogenesis imperfecta and to investigate the hardness of the enamel and dentine of a known FAM83H mutation. Mutational screening of the FAM83H on the basis of candidate gene approach was performed. All exons and exon-intron boundaries was amplified and sequenced. A microhardness test was performed to measure the Vickers microhardness value. A novel nonsense mutation (c.1354C>T, p.Q452X) was identified in the last exon of FAM83H, which resulted in soft, uncalcified enamel. The affected enamel was extremely soft (about 17% of the normal control), but the underlying dentine was as hard as the normal control. Mutational analysis revealed a novel mutation in FAM83H gene. Hardness of dentine was not affected by the mutation, whilst the enamel was extremely soft.

Effects of multiple firings on the microstructure of zirconia and veneering ceramics.

PubMed

Alkurt, Murat; Yeşil Duymus, Zeynep; Gundogdu, Mustafa

2016-01-01

The aim of study was to evaluate the effects of multiple firings on the microstructures of zirconia and two ceramics. Vita VM9 (VMZ) and Cerabien ZR (C-Z) ceramics on a zirconia framework and zirconia without veneering ceramic (WO-Z) were evaluated. Firing methods included firing two, five, and ten times (n=10). The effects of multiple firings on the surface hardness of the materials were evaluated using a Vickers hardness (HV) tester. Data were analyzed by two-way ANOVA and Tukey's test (α=0.05). After firing five and ten times, the hardness of VM-Z and C-Z increased significantly (p<0.001). The HVs of the Cerabien ZR and Vita VM9 veneering ceramics were similar (p>0.05). In the XRD analysis, zirconia had similar tetragonal (t)-monoclinic (m) phase transformations of Y-TZP after the different firing times. Clinically, multiple firings did not affect the microstructure of zirconia, but the structures of the two ceramics were affected.

Microstructural features of friction stir welded dissimilar Aluminium alloys AA2219-AA7475

NASA Astrophysics Data System (ADS)

Zaman Khan, Noor; Ubaid, Mohammed; Siddiquee, Arshad Noor; Khan, Zahid A.; Al-Ahmari, Abdulrahman; Chen, Xizhang; Haider Abidi, Mustufa

2018-05-01

High strength, good corrosion resistance, light weight make aluminium alloys a material of choice in many industrial sectors like aerospace, marine etc. Problems associated with welding of these alloys by fusion welding processes restricted their use in various industries. Friction stir welding (FSW), a clean solid-state joining process, easily overcomes various difficulties encountered during conventional fusion welding processes. In the present work, the effect of rotational speed (710 rpm, 900 rpm and 1120 rpm) on micro-hardness distribution and microstructure of FSWed dissimilar aluminium alloy joints were analyzed. Plates of AA7475-T761 and AA2219-O having thickness of 2.5 mm were welded by fixing AA7475 on retreating side (RS) and AA2219 on advancing side (AS). Welded joints were characterized by Vickers micro-hardness testing, scanning electron microscopy (SEM) and optical microscopy (OM). Results revealed that rotational speed significantly affects the micro-hardness due to increase in grain size, coarsening and dissolution of strengthening precipitates and re-precipitation. Higher micro-hardness values were observed in stir zone due to grain refinement and re-precipitation. Minimum micro-hardness value was observed at the TMAZ/HAZ of advancing side due to thermal softening.

Surface hardness evaluation of different composite resin materials: influence of sports and energy drinks immersion after a short-term period

PubMed Central

ERDEMİR, Ugur; YİLDİZ, Esra; EREN, Meltem Mert; OZEL, Sevda

2013-01-01

Objectives: This study evaluated the effect of sports and energy drinks on the surface hardness of different composite resin restorative materials over a 1-month period. Material and Methods: A total of 168 specimens: Compoglass F, Filtek Z250, Filtek Supreme, and Premise were prepared using a customized cylindrical metal mould and they were divided into six groups (N=42; n=7 per group). For the control groups, the specimens were stored in distilled water for 24 hours at 37º C and the water was renewed daily. For the experimental groups, the specimens were immersed in 5 mL of one of the following test solutions: Powerade, Gatorade, X-IR, Burn, and Red Bull, for two minutes daily for up to a 1-month test period and all the solutions were refreshed daily. Surface hardness was measured using a Vickers hardness measuring instrument at baseline, after 1-week and 1-month. Data were statistically analyzed using Multivariate repeated measure ANOVA and Bonferroni's multiple comparison tests (α=0.05). Results: Multivariate repeated measures ANOVA revealed that there were statistically significant differences in the hardness of the restorative materials in different immersion times (p<0.001) in different solutions (p<0.001). The effect of different solutions on the surface hardness values of the restorative materials was tested using Bonferroni's multiple comparison tests, and it was observed that specimens stored in distilled water demonstrated statistically significant lower mean surface hardness reductions when compared to the specimens immersed in sports and energy drinks after a 1-month evaluation period (p<0.001). The compomer was the most affected by an acidic environment, whereas the composite resin materials were the least affected materials. Conclusions: The effect of sports and energy drinks on the surface hardness of a restorative material depends on the duration of exposure time, and the composition of the material. PMID:23739850

Indentation fracture toughness and dynamic elastic moduli for commercial feldspathic dental porcelain materials.

PubMed

Rizkalla, Amin S; Jones, Derek W

2004-02-01

The purpose of this study was to evaluate and compare the indentation fracture toughness, true hardness and dynamic elastic moduli for 14 commercial dental porcelain materials. The specimens were fired according to manufacturer instructions. The density of the specimens (n=3) was measured by means of the water displacement technique. Dynamic Young's shear and bulk moduli and Poisson's ratio (n=3) were measured using a non-destructive ultrasonic technique using 10 MHz lithium niobate crystals. The true hardness (n=3) was measured using a Knoop indenter and the fracture toughness (n=3) was determined using a Vickers indenter and a Tukon hardness tester. Statistical analysis of the data was conducted using ANOVA and a Student-Newman-Keuls (SNK) rank order multiple comparative test. The SNK rank test analysis for the mean dynamic Young's modulus and fracture toughness was able to separate 14 dental porcelain materials into seven and nine groups, respectively, at p=0.05. The elastic moduli, true hardness and indentation fracture toughness for opaque porcelains were significantly higher than incisal; and body materials at p=0.05. The indentation fracture toughness and the ultrasonic test methods exhibit lower coefficient of variation compared to conventional methods and have considerable advantage for ceramic dental materials in that only small specimens are required to produce an acceptable number of data for statistical analysis.

Distortion control in 20MnCr5 bevel gears after liquid nitriding process to maintain precision dimensions

NASA Astrophysics Data System (ADS)

Mahendiran, M.; Kavitha, M.

2018-02-01

Robotic and automotive gears are generally very high precision components with limitations in tolerances. Bevel gears are more widely used and dimensionally very close tolerance components that need stability without any backlash or distortion for smooth and trouble free functions. Nitriding is carried out to enhance wear resistance of the surface. The aim of this paper is to reduce the distortion in liquid nitriding process, though plasma nitriding is preferred for high precision components. Various trials were conducted to optimize the process parameters, considering pre dimensional setting for nominal nitriding layer growth. Surface cleaning, suitable fixtures and stress relieving operations were also done to optimize the process. Micro structural analysis and Vickers hardness testing were carried out for analyzing the phase changes, variation in surface hardness and case depth. CNC gear testing machine was used for determining the distortion level. The presence of white layer was found for about 10-15μm in the case depth of 250± 3.5μm showing an average surface hardness of 670 HV. Hence the economical liquid nitriding process was successfully used for producing high hardness and wear resistant coating over 20MnCr5 material with less distortion and reduced secondary grinding process for dimensional control.

Dry sliding behavior of aluminum alloy 8011 with 12% fly ash composites

NASA Astrophysics Data System (ADS)

Magibalan, S.; Senthilkumar, P.; Palanivelu, R.; Senthilkumar, C.; Shivasankaran, N.; Prabu, M.

2018-05-01

This research focused on the fabrication of aluminum alloy 8011 with 12% fly ash (FA) composite (AA8011%–12% FA) using the stir casting method. A three-level central composite design experiment was developed using response surface methodology with various parameters such as load, time, and sliding velocity varied in the range of 5 to 15 N, 5 to 15 min, and 1.5 to 4.5 m.s‑1, respectively. Dry sliding wear tests were performed as per the experimental design using a pin on disc at room temperature. The obtained regression result indicated that the developed model performed well in relating the wear process parameters and predicted the wear behavior of the composite. The surface plot showed that the wear rate increases with increase in load, time, and sliding velocity. Hardness was evaluated by Vickers hardness testing machine. Moreover, the surface morphology of the worn-out composite was examined using a scanning electron microscope.

Microstructure and phase analysis of Zirconia-ODS (Oxide Dispersion Strengthen) alloy sintered by APS with milling time variation

NASA Astrophysics Data System (ADS)

Sugeng, Bambang; Bandriyana, B.; Sugeng, Bambang; Salam, Rohmad; Sumariyo; Sujatno, Agus; Dimyati, Arbi

2018-03-01

Investigation on the relationship between the process conditions of milling time and the microstructure on the synthesis of the zirconia-ODS steel alloy has been performed. The elemental composition of the alloy was determined on 20 wt% Cr and zirconia dispersoid of 0.50 wt%. The synthesis was carried out by powder metallurgy method with milling time of 3, 5 and 7 hours, static compression of 20 Ton and sintering process for 4 minutes using the APS (Arc Plasma Sintering) equipment. SEM-EDX and XRD test was carried out to characterize the phase and morphology of the alloy and the effect to the mechanical properties was evaluated by the Vickers Hardness testing. The synthesis produced sample of ODS steel with good dense and very little porous with the Fe-Cr phase that clearly observed in the XRD peak pattern. In addition milling time increased the homogeneously of Fe-Cr phase formulation, enhanced the grain refinement of the structure and increase the hardness of the alloy.

Mechanical properties of polymer-infiltrated-ceramic (sodium aluminum silicate) composites for dental restoration.

PubMed

Cui, Bencang; Li, Jing; Wang, Huining; Lin, Yuanhua; Shen, Yang; Li, Ming; Deng, Xuliang; Nan, Cewen

2017-07-01

To fabricate indirect restorative composites for CAD/CAM applications and evaluate the mechanical properties. Polymer-infiltrated-ceramic composites were prepared through infiltrating polymer into partially sintered sodium aluminum silicate ceramic blocks and curing. The corresponding samples were fabricated according to standard ISO-4049 using for mechanical properties measurement. The flexural strength and fracture toughness were measured using a mechanical property testing machine. The Vickers hardness and elastic modulus were calculated from the results of nano-indentation. The microstructures were investigated using secondary electron detector. The density of the porous ceramic blocks was obtained through TG-DTA. The conversion degrees were calculated from the results of mid-infrared spectroscopy. The obtained polymer infiltrated composites have a maximum flexural strength value of 214±6.5MPa, Vickers hardness of 1.76-2.30GPa, elastic modulus of 22.63-27.31GPa, fracture toughness of 1.76-2.35MPam 1/2 and brittleness index of 0.75-1.32μm -1/2 . These results were compared with those of commercial CAD/CAM blocks. Our results suggest that these materials with good mechanical properties are comparable to two commercial CAD/CAM blocks. The sintering temperature could dramatically influence the mechanical properties. Restorative composites with superior mechanical properties were produced. These materials mimic the properties of natural dentin and could be a promising candidate for CAD/CAM applications. Copyright © 2017 Elsevier Ltd. All rights reserved.

Characterization of the Mineral Trioxide Aggregate–Resin Modified Glass Ionomer Cement Interface in Different Setting Conditions

PubMed Central

Eid, Ashraf A.; Komabayashi, Takashi; Watanabe, Etsuko; Shiraishi, Takanobu; Watanabe, Ikuya

2012-01-01

Introduction Mineral trioxide aggregate (MTA) has been used successfully for perforation repair, vital pulpotomies, and direct pulp capping. However, little is known about the interactions between MTA and glass ionomer cement (GIC) in final restorations. In this study, 2 null hypotheses were tested: (1) GIC placement time does not affect the MTA-GIC structural interface and hardness and (2) moisture does not affect the MTA-GIC structural interface and hardness. Methods Fifty cylinders were half filled with MTA and divided into 5 groups. The other half was filled with resin-modified GIC either immediately after MTA placement or after 1 or 7 days of temporization in the presence or absence of a wet cotton pellet. The specimens were then sectioned, carbon coated, and examined using a scanning electron microscope and an electron probe micro-analyzer (SEM-EPMA) for interfacial adaptation, gap formation, and elemental analysis. The Vickers hardness numbers of the interfacial MTA were recorded 24 hours after GIC placement and 8 days after MTA placement and analyzed using the analysis of variance test. Results Hardness testing 24 hours after GIC placement revealed a significant increase in hardness with an increase of temporization time but not with a change of moisture conditions (P < .05). Hardness testing 8 days after MTA placement indicated no significant differences among groups. SEM-EPMA showed interfacial adaptation to improve with temporization time and moisture. Observed changes were limited to the outermost layer of MTA. The 2 null hypotheses were not rejected. Conclusions GIC can be applied over freshly mixed MTA with minimal effects on the MTA, which seemed to decrease with time. PMID:22794220

Grinding efficiency of abutment tooth with both dentin and core composite resin on axial plane.

PubMed

Miho, Otoaki; Sato, Toru; Matsukubo, Takashi

2015-01-01

The purpose of this study was to evaluate grinding efficiency in abutment teeth comprising both dentin and core composite resin in the axial plane. Grinding was performed over 5 runs at two loads (0.5 or 0.25 N) and two feed rates (1 or 2 mm/sec). The grinding surface was observed with a 3-D laser microscope. Tomographic images of the grinding surfaces captured perpendicular to the feed direction were also analyzed. Using a non-ground surface as a reference, areas comprising only dentin, both dentin and core composite resin, or only core composite resin were analyzed to determine the angle of the grinding surface. Composite resins were subjected to the Vickers hardness test and scanning electron microscopy. Data were statistically analyzed using a one-way analysis of variance and multiple comparison tests. Multiple regression analysis was performed for load, feed rate, and Vickers hardness of the build-up material depending on number of runs. When grinding was performed at a constant load and feed rate, a greater grinding angle was observed in areas comprising both dentin and composite resin or only composite resin than in areas consisting of dentin alone. A correlation was found between machinability and load or feed rate in areas comprising both dentin and composite resin or composite resin alone, with a particularly high correlation being observed between machinability and load. These results suggest that great caution should be exercised in a clinical setting when the boundary between the dentin and composite resin is to be ground, as the angle of the grinding surface changes when the rotating diamond point begins grinding the composite resin.

Evaluation of mechanical properties of some glycine complexes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nagaraju, D.; Raja Shekar, P. V., E-mail: pvrsleo@gmail.com; Chandra, Ch. Sateesh

2014-04-24

The variation of Vickers hardness with load for (101) glycine zinc chloride (GZC), (001) glycine lithium sulphate (GLS), (001) triglycine sulphate (TGS) and (010) glycine phosphite (GPI) crystals was studied. From the cracks initiated along the corners of the indentation impression, crack lengths were measured and the fracture toughness value and brittle index number were determined. The hardness related parameters viz. yield strength and Young’s modulus were also estimated. The anisotropic nature of the crystals was studied using Knoop indentation technique.

Effects of minor Cu and Si additions on glass forming ability and mechanical properties of Co-Fe-Ta-B Bulk metallic glass

NASA Astrophysics Data System (ADS)

Yazici, Ziya Ozgur; Hitit, Aytekin; Yalcin, Yilmaz; Ozgul, Metin

2016-01-01

Effect of Cu and Si substitutions for Co and B on the glass forming ability (GFA) of Co(43-x)CuxFe20Ta5.5B(31.5-x)Siy (x=0-1.5 and y=5-10) were systematically investigated by X-ray diffraction, optical microscopy, scanning electron microscopy, and differential scanning calorimetry. In order to evaluate the contribution of copper and silicon, appropriate amounts of copper and silicon were individually introduced to the base alloy composition. By using the effects of copper and silicon together, significant enhancement was obtained and the critical casting thickness (CCT) of the base alloy was increased three times from 2 mm to 6 mm. Moreover, mechanical properties of the alloys were examined by compression tests and Vickers hardness measurements. The compression test results revealed that the glassy alloys having enhanced GFA shows high strength of about 3500-4000 MPa. In addition, existence of (Co,Fe)2B and (Co,Fe)20.82Ta2.18B6 crystalline phases in glassy matrix influences the hardnesses of the alloys compared to monolitic glassy structure having hardness of about 1200 Hv.

Formation of high heat resistant coatings by using gas tunnel type plasma spraying.

PubMed

Kobayashi, A; Ando, Y; Kurokawa, K

2012-06-01

Zirconia sprayed coatings are widely used as thermal barrier coatings (TBC) for high temperature protection of metallic structures. However, their use in diesel engine combustion chamber components has the long run durability problems, such as the spallation at the interface between the coating and substrate due to the interface oxidation. Although zirconia coatings have been used in many applications, the interface spallation problem is still waiting to be solved under the critical conditions such as high temperature and high corrosion environment. The gas tunnel type plasma spraying developed by the author can make high quality ceramic coatings such as Al2O3 and ZrO2 coating compared to other plasma spraying method. A high hardness ceramic coating such as Al2O3 coating by the gas tunnel type plasma spraying, were investigated in the previous study. The Vickers hardness of the zirconia (ZrO2) coating increased with decreasing spraying distance, and a higher Vickers hardness of about Hv = 1200 could be obtained at a shorter spraying distance of L = 30 mm. ZrO2 coating formed has a high hardness layer at the surface side, which shows the graded functionality of hardness. In this study, ZrO2 composite coatings (TBCs) with Al2O3 were deposited on SS304 substrates by gas tunnel type plasma spraying. The performance such as the mechanical properties, thermal behavior and high temperature oxidation resistance of the functionally graded TBCs was investigated and discussed. The resultant coating samples with different spraying powders and thickness are compared in their corrosion resistance with coating thickness as variables. Corrosion potential was measured and analyzed corresponding to the microstructure of the coatings. High Heat Resistant Coatings, Gas Tunnel Type Plasma Spraying, Hardness,

Fracture behaviour of WC-Co hardmetals with WC partially substituted by titanium carbide

NASA Astrophysics Data System (ADS)

Szutkowska, M.; Boniecki, M.; Cygan, S.; Kalinka, A.; Grilli, M. L.; Balos, S.

2018-03-01

The addition of various amounts of TiC0.9 phase in the range from 5wt.% to 20wt.% substituting WC phase was applied in WC-Co hardmetals with 9.5 wt.% bonding cobalt phase. The hardmetals were consolidated using Hot Isostatic Pressing (HIP) method at temperature of 1573K and pressure of 1500 atm. The plain strain fracture toughness has been determined from 3PB test on a precracking single edge notched beam (SENB) specimen. The indentation fracture toughness with Vickers cracks for comparison was also measured, which changed from 12 to 9.0 MPa·m1/2. The amount of the TiC0.9 phase affected the mechanical and physical properties: Vickers hardness from 12.5 to 14.0 GPa, Young’s modulus from 550 to 460 GPa, density from 13.1 to 9.6 g/cm3, friction coefficient from 0.24 to 0.45, fracture toughness from 16.8 to 11.0 MPa·m1/2. Scanning electron microscopy (SEM), X-ray and electron diffraction phase analysis were used to examine the WC-Co hardmetal with addition of the TiC0.9 phase. For comparison, physical and mechanical properties of the WC-Co hardmetals before modification were tested.

Effects of the bleaching procedures on enamel micro-hardness: Plasma Arc and diode laser comparison.

PubMed

Nematianaraki, Saeid; Fekrazad, Reza; Naghibi, Nasim; Kalhori, Katayoun Am; Junior, Aldo Brugnera

2015-10-02

One of the major side effects of vital bleaching is the reduction of enamel micro-hardness. The purpose of this study was to evaluate the influence of two different bleaching systems, Plasma Arc and GaAlAs laser, on the enamel micro-hardness. 15 freshly extracted human third molars were sectioned to prepare 30 enamel blocks (5×5 mm). These samples were then randomly divided into 2 groups of 15 each (n=15): a plasma arc bleaching group (: 350-700 nm) + 35% Hydrogen Peroxide whitening gel and a laser bleaching group (GaAlAs laser, λ: 810 nm, P: 10 W, CW, Special Tip) + 35% Hydrogen Peroxide whitening gel. Samples were subjected to the Vickers micro-hardness test (VHN) at a load of 50 g for 15s before and after treatment. Data were statistically analyzed by a Mann-Whitney test (p≤0.05). In the GaAlAs laser group, the enamel micro-hardness was 618.2 before and was reduced to 544.6 after bleaching procedures. In the plasma arc group, the enamel micro-hardness was 644.8 before and 498.9 after bleaching. Although both techniques significantly reduced VHN, plasma arc bleaching resulted in a 22.62% reduction in VHN for enamel micro-hardness, whereas an 11.89% reduction in VHN was observed for laser bleaching; this difference is statistically significant (p<0.001). Both bleaching techniques reduced enamel micro-hardness, although the reduction is much less significant with the GaAlAs laser than with the plasma arc. Therefore GaAlAs laser bleaching has fewer harmful effects than plasma arc in respect to enamel micro-hardness reduction.

Influences of multiple firings and aging on surface roughness, strength and hardness of veneering ceramics for zirconia frameworks.

PubMed

Tang, Xuehua; Luo, Huinan; Bai, Yang; Tang, Hui; Nakamura, Takashi; Yatani, Hirofumi

2015-09-01

To evaluate the effects of multiple firings and aging on surface roughness, strength, and hardness of veneering ceramics for zirconia frameworks. Five different veneering ceramics for zirconia frameworks were used: Vintage ZR (ZR), Cerabien ZR (CZR), VitaVM9 (VM9), Cercon ceram KISS (KISS), and IPS e.max ceram (e.max). Specimens were fired 2 or 10 times in order to accelerate aging. Surface roughness was evaluated using laser profilometry. Flexural strength and Vickers hardness were also measured. Surface topography was observed using scanning electron microscopy. After accelerated aging, the surface roughness of all specimens fired 10 times was significantly lower than that of the same specimens fired 2 times (P=0.000). Except for VM9, the flexural strength of all specimens fired 10 times was greater than that of the same specimens fired 2 times, and the differences were significant for ZR and CZR (P<0.01). The flexural strength of VM9 fired 10 times was significantly lower than that of VM9 fired 2 times (P=0.034). The Vickers hardness of ZR and VM9 fired 10 times was significantly higher than that of the same specimens fired 2 times (P<0.05), but that of KISS fired 10 times was significantly lower than that of KISS fired 2 times (P=0.000). Multiple firings had a positive effect on the surface roughness of all aged veneering ceramics used for zirconia restorations and on the strength and hardness of many aged veneering ceramics used for zirconia restorations. Copyright © 2015 Elsevier Ltd. All rights reserved.

Extracorporeal shockwave enhanced regeneration of fibrocartilage in a delayed tendon-bone insertion repair model.

PubMed

Chow, Dick Ho Kiu; Suen, Pui Kit; Huang, Le; Cheung, Wing-Hoi; Leung, Kwok-Sui; Ng, Chun; Shi, San Qiang; Wong, Margaret Wan Nar; Qin, Ling

2014-04-01

Fibrous tissue is often formed in delayed healing of tendon bone insertion (TBI) instead of fibrocartilage. Extracorporeal shockwave (ESW) provides mechanical cues and upregulates expression of fibrocartilage-related makers and cytokines. We hypothesized that ESW would accelerate fibrocartilage regeneration at the healing interface in a delayed TBI healing model. Partial patellectomy with shielding at the TBI interface was performed on 32 female New Zealand White Rabbits for establishing this delayed TBI healing model. The rabbits were separated into the control and ESW group for evaluations at postoperative week 8 and 12. Shielding was removed at week 4 and a single ESW treatment was applied at week 6. Fibrocartilage regeneration was evaluated histomorphologically and immunohistochemically. Vickers hardness of the TBI matrix was measured by micro-indentation. ESW group showed higher fibrocartilage area, thickness, and proteoglycan deposition than the control in week 8 and 12. ESW increased expression of SOX9 and collagen II significantly in week 8 and 12, respectively. ESW group showed a gradual transition of hardness from bone to fibrocartilage to tendon, and had a higher Vickers hardness than the control group at week 12. In conclusion, ESW enhanced fibrocartilage regeneration at the healing interface in a delayed TBI healing model. © 2013 Orthopaedic Research Society. Published by Wiley Periodicals, Inc.

An Investigation of the Microstructure of an Intermetallic Layer in Welding Aluminum Alloys to Steel by MIG Process

PubMed Central

Nguyen, Quoc Manh; Huang, Shyh-Chour

2015-01-01

Butt joints of A5052 aluminum alloy and SS400 steel, with a new type of chamfered edge, are welded by means of metal inert gas welding and ER4043 Al-Si filler metal. The microhardness and microstructure of the joint are investigated. An intermetallic layer is found on the surface of the welding seam and SS400 steel sheet. The hardness of the intermetallic layer is examined using the Vickers hardness test. The average hardness values at the Intermetallic (IMC) layer zone and without the IMC layer zone were higher than that of the welding wire ER4043. The tensile strength test showed a fracture at the intermetallic layer when the tensile strength is 225.9 MPa. The tensile value test indicated the average of welds was equivalent to the 85% tensile strength of the A5052 aluminum alloy. The thickness of the intermetallic layers is non-uniform at different positions with the ranges from 1.95 to 5 μm. The quality of the butt joint is better if the intermetallic layer is minimized. The Si crystals which appeared at the welding seam, indicating that this element participated actively during the welding process, also contributed to the IMC layer’s formation. PMID:28793708

Research on microstructure properties of the TiC/Ni-Fe-Al coating prepared by laser cladding technology

NASA Astrophysics Data System (ADS)

Jiao, Junke; Xu, Zifa; Zan, Shaoping; Zhang, Wenwu; Sheng, Liyuan

2017-10-01

In this paper, the laser cladding method was used to preparation the TiC reinforced Ni-Fe-Al coating on the Ni base superalloy. The Ti/Ni-Fe-Al powder was preset on the Ni base superalloy and the powder layer thickness is 0.5mm. A fiber laser was used the melting Ti/Ni-Fe-Al powder in an inert gas environment. The shape of the cladding layer was tested using laser scanning confocal microscope (LSCM) under different cladding parameters such as the laser power, the melting velocity and the defocused amount. The microstructure, the micro-hardness was tested by LSCM, SEM, Vickers hardness tester. The test result showed that the TiC particles was distributed uniformly in the cladding layer and hardness of the cladding layer was improved from 180HV to 320HV compared with the Ni-Fe-Al cladding layer without TiC powder reinforced, and a metallurgical bonding was produced between the cladding layer and the base metal. The TiC powder could make the Ni-Fe-Al cladding layer grain refining, and the more TiC powder added in the Ni-Fe-Al powder, the smaller grain size was in the cladding layer.

An Investigation of the Microstructure of an Intermetallic Layer in Welding Aluminum Alloys to Steel by MIG Process.

PubMed

Nguyen, Quoc Manh; Huang, Shyh-Chour

2015-12-02

Butt joints of A5052 aluminum alloy and SS400 steel, with a new type of chamfered edge, are welded by means of metal inert gas welding and ER4043 Al-Si filler metal. The microhardness and microstructure of the joint are investigated. An intermetallic layer is found on the surface of the welding seam and SS400 steel sheet. The hardness of the intermetallic layer is examined using the Vickers hardness test. The average hardness values at the Intermetallic (IMC) layer zone and without the IMC layer zone were higher than that of the welding wire ER4043. The tensile strength test showed a fracture at the intermetallic layer when the tensile strength is 225.9 MPa. The tensile value test indicated the average of welds was equivalent to the 85% tensile strength of the A5052 aluminum alloy. The thickness of the intermetallic layers is non-uniform at different positions with the ranges from 1.95 to 5 μm. The quality of the butt joint is better if the intermetallic layer is minimized. The Si crystals which appeared at the welding seam, indicating that this element participated actively during the welding process, also contributed to the IMC layer's formation.

Characteristic of Low Temperature Carburized Austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Istiroyah; Pamungkas, M. A.; Saroja, G.; Ghufron, M.; Juwono, A. M.

2018-01-01

Low temperature carburizing process has been carried out on austenitic stainless steel (ASS) type AISI 316L, that contain chromium in above 12 at%. Therefore, conventional heat treatment processes that are usually carried out at high temperatures are not applicable. The sensitization process due to chromium migration from the grain boundary will lead to stress corrosion crack and decrease the corrosion resistance of the steel. In this study, the carburizing process was carried out at low temperatures below 500 °C. Surface morphology and mechanical properties of carburized specimens were investigated using optical microscopy, non destructive profilometer, and Vicker microhardness. The surface roughness analysis show the carburising process improves the roughness of ASS surface. This improvement is due to the adsorption of carbon atoms on the surface of the specimen. Likewise, the hardness test results indicate the carburising process increases the hardness of ASS.

Microstructure and antibacterial properties of microwave plasma nitrided layers on biomedical stainless steels

NASA Astrophysics Data System (ADS)

Lin, Li-Hsiang; Chen, Shih-Chung; Wu, Ching-Zong; Hung, Jing-Ming; Ou, Keng-Liang

2011-06-01

Nitriding of AISI 303 austenitic stainless steel using microwave plasma system at various temperatures was conducted in the present study. The nitrided layers were characterized via scanning electron microscopy, glancing angle X-ray diffraction, transmission electron microscopy and Vickers microhardness tester. The antibacterial properties of this nitrided layer were evaluated. During nitriding treatment between 350 °C and 550 °C, the phase transformation sequence on the nitrided layers of the alloys was found to be γ → (γ + γ N) → (γ + α + CrN). The analytical results revealed that the surface hardness of AISI 303 stainless steel could be enhanced with the formation of γ N phase in nitriding process. Antibacterial test also demonstrated the nitrided layer processed the excellent antibacterial properties. The enhanced surface hardness and antibacterial properties make the nitrided AISI 303 austenitic stainless steel to be one of the essential materials in the biomedical applications.

Influence of the bracket on bonding and physical behavior of orthodontic resin cements.

PubMed

Bolaños-Carmona, Victoria; Zein, Bilal; Menéndez-Núñez, Mario; Sánchez-Sánchez, Purificación; Ceballos-García, Laura; González-López, Santiago

2015-01-01

The aim of the study is to determine the influence of the type of bracket, on bond strength, microhardness and conversion degree (CD) of four resin orthodontic cements. Micro-tensile bond strength (µTBS) test between the bracket base and the cement was carried out on glass-hour-shaped specimens (n=20). Vickers Hardness Number (VHN) and micro-Raman spectra were recorded in situ under the bracket base. Weibull distribution, ANOVA and non-parametric test were applied for data analysis (p<0.05). The highest values of ή as well as the β Weibull parameter were obtained for metallic brackets with Transbond™ plastic brackets with the self-curing cement showing the worst performance. The CD was from 80% to 62.5%.

Zirconia toughened mica glass ceramics for dental restorations.

PubMed

Gali, Sivaranjani; K, Ravikumar; Murthy, B V S; Basu, Bikramjit

2018-03-01

The objective of the present study is to understand the role of yttria stabilized zirconia (YSZ) in achieving the desired spectrum of clinically relevant mechanical properties (hardness, elastic modulus, fracture toughness and brittleness index) and chemical solubility of mica glass ceramics. The glass-zirconia mixtures with varying amounts of YSZ (0, 5, 10, 15 and 20wt.%) were ball milled, compacted and sintered to obtain pellets of glass ceramic-YSZ composites. Phase analysis was carried out using X-ray diffraction and microstructural characterization with SEM revealed the crystal morphology of the composites. Mechanical properties such as Vickers hardness, elastic modulus, indentation fracture toughness and chemical solubility were assessed. Phase analysis of sintered pellets of glass ceramic-YSZ composites revealed the characteristic peaks of fluorophlogopite (FPP) and tetragonal zirconia. Microstructural investigation showed plate and lath-like interlocking mica crystals with embedded zirconia. Vickers hardness of 9.2GPa, elastic modulus of 125GPa, indentation toughness of 3.6MPa·m 1/2 , and chemical solubility of 30μg/cm 2 (well below the permissible limit) were recorded with mica glass ceramics containing 20wt.% YSZ. An increase in hardness and toughness of the glass ceramic-YSZ composites with no compromise on their brittleness index and chemical solubility has been observed. Such spectrum of properties can be utilised for developing a machinable ceramic for low stress bearing inlays, onlays and veneers. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

[Effect of sintering temperature on mechanical properties of dental zirconia toughened alumina ceramics].

PubMed

Fan, Jiang-Yuan; Lin, Ting-Ting; Hu, Fang-Xuan; Zheng, Rui-Bin; Fan, Fan; Ma, Jian-Feng

2017-04-01

To investigate the effect of sintering temperature on mechanical properties of dental zirconia toughened alumina (ZTA) ceramics prepared by gel-casting technique. The samples prepared by gel-casting were sintered at 1100, 1200, 1250, 1300 and 1400degrees centigrade for each group. The flexural strength, fracture toughness, Vickers hardness and brittleness index were obtained and microscopic morphology of each group was observed under scanning electron microscope (SEM). The data were statistically analyzed using SPSS 19.0 software package. The flexural strength, fracture toughness and Vickers hardness increased with the increasing sintering temperature during 1100~1400degrees centigrade. The lowest brittleness index (0.74±0.16) μm -1/2 was observed in group sintered at 1200degrees centigrade and the highest (2.76±0.14) μm -1/2 was at 1400degrees centigrade (P<0.05), while the flexural strength of these two groups was (46.89±3.24) MPa and (349.64±54.72) MPa, respectively. The ZTA dental ceramics exhibit good machinability with proper sintering temperature (1200degrees centigrade) and the strength meets the requirement of clinical application.

Determination of 200 °C Isothermal Section of Al-Ag-Ga Phase Diagram by Microanalysis, X-ray Diffraction, Hardness and Electrical Conductivity Measurements

NASA Astrophysics Data System (ADS)

Premović, Milena; Tomović, Milica; Minić, Duško; Manasijević, Dragan; Živković, Dragana; Ćosović, Vladan; Grković, Vladan; Đorđević, Aleksandar

2017-04-01

Ternary Al-Ag-Ga system at 200 °C was experimentally and thermodynamically assessed. Isothermal section was extrapolated using optimized thermodynamic parameters for constitutive binary systems. Microstructure and phase composition of the selected alloy samples were analyzed using light microscopy, scanning electron microscopy combined with energy-dispersive spectrometry and x-ray powder diffraction technique. The obtained experimental results were found to be in a close agreement with the predicted phase equilibria. Hardness and electrical conductivity of the alloy samples from four vertical sections Al-Ag80Ga20, Al-Ag60Ga40, Ag-Al80Ga20 and Ag-Al60Ga40 of the ternary Al-Ag-Ga system at 200 °C were experimentally determined using Brinell method and eddy current measurements. Additionally, hardness of the individual phases present in the microstructure of the studied alloy samples was determined using Vickers microhardness test. Based on experimentally obtained results, isolines of Brinell hardness and electrical conductivity were calculated for the alloys from isothermal section of the ternary Al-Ag-Ga system at 200 °C.

Laser-assisted generation of periodic structures on a steel surface: A method for increasing microhardness

NASA Astrophysics Data System (ADS)

Razi, Sepehr; Ghasemi, Fatemeh

2018-02-01

Stainless steel grade 316L is a commonly used metal in various industrial applications because of its excellent resistance to corrosion and great welding and biocompatibility characteristics. Here, the laser-induced micro/nanostructures generation on the steel surface is investigated. A femtosecond ultrashort pulsed laser is selected in this regard, and various irradiation circumstances are considered for two groups of specimens possessing different initial roughness. It turns out that regular periodic ripples with spatial periodicities less than the laser wavelength are generated on both groups at irradiation fluences ≤ 2 J/cm2. Furthermore, it figures out that each ripple is composed of the closely created nano dimension structures. Vickers micro-hardness test is also utilized to examine the alterations of the surface hardness features. Moreover, variations of the surface chemistry are studied and discussions related to the most effective factors in surface hardness raise/decrease are presented. Results reveal the potential benefits of the femtosecond laser technique, such as its flexibility and ease of implementation in controlled modification of the surface features. Thus, it might be of interest to manufacturers looking for precise surface morphology, chemistry and hardness alterations.

Surface properties of multilayered, acrylic resin artificial teeth after immersion in staining beverages

PubMed Central

NEPPELENBROEK, Karin Hermana; KUROISHI, Eduardo; HOTTA, Juliana; MARQUES, Vinicius Rizzo; MOFFA, Eduardo Buozi; SOARES, Simone; URBAN, Vanessa Migliorini

2015-01-01

Objective To evaluate the effect of staining beverages (coffee, orange juice, and red wine) on the Vickers hardness and surface roughness of the base (BL) and enamel (EL) layers of improved artificial teeth (Vivodent and Trilux). Material and Methods Specimens (n=8) were stored in distilled water at 37°C for 24 h and then submitted to the tests. Afterwards, specimens were immersed in one of the staining solutions or distilled water (control) at 37°C, and the tests were also performed after 15 and 30 days of immersion. Data were analyzed using 3-way ANOVA and Tukey’s test (α=0.05). Results Vivodent teeth exhibited a continuous decrease (p<0.0005) in hardness of both layers for up to 30 days of immersion in all solutions. For Trilux teeth, similar results were found for the EL (p<0.004), and the BL showed a decrease in hardness after 15 days of immersion (p<0.01). At the end of 30 days, this reduction was not observed for coffee and water (p>0.15), but red wine and orange juice continuously reduced hardness values (p<0.0004). Red wine caused the most significant hardness changes, followed by orange juice, coffee, and water (p<0.006). No significant differences in roughness were observed for both layers of the teeth during the immersion period, despite the beverage (p>0.06). Conclusions Hardness of the two brands of acrylic teeth was reduced by all staining beverages, mainly for red wine. Roughness of both layers of the teeth was not affected by long-term immersion in the beverages. PMID:26398509

Mechanical properties of commercial high strength ceramic core materials.

PubMed

Rizkalla, A S; Jones, D W

2004-02-01

The objective of the present study is to evaluate and compare the flexural strength, dynamic elastic moduli and true hardness (H(o)) values of commercial Vita In-Ceram alumina core and Vita In-Ceram matrix glass with the standard aluminous porcelain (Hi-Ceram and Vitadur), Vitadur N and Dicor glass and glass-ceramic. The flexural strength was evaluated (n=5) using 3-point loading and a servo hydraulic Instron testing machine at a cross head speed of 0.5 mm/min. The density of the specimens (n=3) was measured by means of the water displacement technique. Dynamic Young's shear and bulk moduli and Poisson's ratio (n=3) were measured using a non-destructive ultrasonic technique using 10 MHz lithium niobate crystals. The true hardness (n=3) was measured using a Knoop indenter and the fracture toughness (n=3) was determined using a Vickers indenter and a Tukon hardness tester. Statistical analysis of the data was conducted using ANOVA and a Student-Newman-Keuls (SNK) rank order multiple comparative test. The SNK rank order test analysis of the mean flexural strength was able to separate five commercial core materials into three significant groups at p=0.05. Vita In-Ceram alumina and IPS Empress 2 exhibited significantly higher flexural strength than aluminous porcelains and IPS Empress at p=0.05. The dynamic elastic moduli and true hardness of Vita In-Ceram alumina core were significantly higher than the rest of the commercial ceramic core materials at p=0.05. The ultrasonic test method is a valuable mechanical characterization tool and was able to statistically discriminate between the chemical and structural differences within dental ceramic materials. Significant correlation was obtained between the dynamic Young's modulus and true hardness, p=0.05.

Development of 2024 AA-Yttrium composites by Spark Plasma Sintering

NASA Astrophysics Data System (ADS)

Vidyasagar, CH S.; Karunakar, D. B.

2018-04-01

The method of fabrication of MMNCs is quite a challenge, which includes advanced processing techniques like Spark Plasma Sintering (SPS), etc. The objective of the present work is to fabricate aluminium based MMNCs with the addition of small amounts of yttrium using Spark Plasma Sintering and to evaluate their mechanical and microstructure properties. Samples of 2024 AA with yttrium ranging from 0.1% to 0.5 wt% are fabricated by Spark Plasma Sintering (SPS). Hardness of the samples is determined using Vickers hardness testing machine. The metallurgical characterization of the samples is evaluated by Optical Microscopy (OM), Field Emission Scanning Electron Microscopy (FE-SEM). Unreinforced 2024 AA sample is also fabricated as a benchmark to compare its properties with those of the composite developed. It is found that the yttrium addition increases the above mentioned properties by altering the precipitation kinetics and intermetallic formation to some extent and then decreases gradually when yttrium wt% increases beyond 0.3 wt%. High density (˂ 99.75) is achieved in the samples and highest hardness achieved is 114 Hv, fabricated by spark plasma sintering and uniform distribution of yttrium is observed.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Malik, Hitendra K., E-mail: hkmalik@physics.iitd.ac.in; Singh, Omveer; Dahiya, Raj P.

We have established a hot cathode arc discharge plasma system, where different stainless steel samples can be treated by monitoring the plasma parameters and nitriding parameters independently. In the present work, a mixture of 70% N{sub 2} and 30% H{sub 2} gases was fed into the plasma chamber and the treatment time and substrate temperature were optimized for treating 304L Stainless Steel samples. Various physical techniques such as x-ray diffraction, energy dispersive x-ray spectroscopy and micro-vickers hardness tester were employed to determine the structural, surface composition and surface hardness of the treated samples.

The effect of McInnes solution on enamel and the effect of Tooth mousse on bleached enamel: An in vitro study

PubMed Central

Darshan, H E; Shashikiran, N D

2008-01-01

Aims: To evaluate the effect of McInnes bleaching agent on the micro hardness of enamel before and after bleaching and to evaluate the effect of G C Tooth Mousse on the bleached enamel surface for its microhardness. Materials and Methods: McInnes bleaching solution, Casein phosphopeptide-amorphous calcium phosphate CCP-ACP (G C Tooth mousse) artificial saliva (Dept of Oral Pathology, College of Dental Sciences, Davengere), deionized water, Vickers Micro Hardness tester (Zwick/ZHV, Germany), freshly extracted teeth, cold cure acrylic, Diamond disc (Horico - PFINGST New jersey USA, KAVO- Germany), straight handpiece (kavo peca reta) and plastic moulds (6.5 × 2 mm). The purpose of this study was to evaluate and compare microhardness of the sound enamel surface by Vickers Hardness Number before and after bleaching with McInnes solution, and to evaluate the effect of casein phosphopeptide amorphous calcium phosphate (G C Tooth Mousse) on the bleached enamel surface for its microhardness. Statistical analysis: The data obtained from the test were subjected for statistical analysis and are presented as range, mean and standard deviation. P value of 0.05 or less was considered for statistical significance. The changes in microhardness at different times of assessment were analyzed using the paired ‘t’ test Results: All the samples showed decrease in the microhardness after two cycles of bleaching, though immediately after bleaching the decrease in the microhardness was not significant (P = 0.34). However, after the second cycles, it showed a significant decrease (P<0.01) in the microhardness. After application of remineralization solution (GC Tooth mousse), the samples showed a marginal increase in the microhardness (P<0.05) after seven days and a marked increase after fourteen days (P<0.001). Conclusion: McInnes bleaching agent does decrease the microhardness of enamel by causing enamel demineralization and GC Tooth mousse used in the study causes an increase in the microhardness of bleached enamel by maintaining a high gradient of calcium and phosphate ions at the enamel subsurface. PMID:20142891

Mechanical optimization of the composite biomaterial based on the tricalcium phosphate, titania and magnesium fluoride.

PubMed

Ayadi, Ibticem; Ayed, Foued Ben

2016-07-01

The microstructure, the densification and the mechanical properties of the tricalcium phosphate - titania - MgF2 composites were investigated. The effect of MgF2 addition on the performances of the tricalcium phosphate - 40wt% titania composites is discussed. The mechanical properties were investigated by Brazilian test, Vickers indentation and the ultrasound techniques. The mechanical properties of the tricalcium phosphate - 40wt% titania composites reached optimum performances after the sintering process at 1200°C for one hour with 4wt% MgF2. Thus, the highest values of the rupture strength, Vickers hardness, Young׳s and the shear modulus reached 27MPa, 360Hv, 51GPa and 20GPa, respectively. The increase of the mechanical properties of the composites is due to the presence of the liquid phase and the formation of a new compound. Thus, the microstructure of the composites reveals the presence of a new lamella form relative to the Mg2(PO4)F. Beyond 4wt% MgF2, the performances of the composites are hindered by the exaggerated grain growth and the formation of the bubbles. Copyright © 2016 Elsevier Ltd. All rights reserved.

Hardness of model dental composites - the effect of filler volume fraction and silanation.

PubMed

McCabe, J F; Wassell, R W

1999-05-01

The relationship between structure and mechanical properties for dental composites has often proved difficult to determine due to the use of commercially available materials having a number of differences in composition i.e. different type of resin, different type of filler, etc. This makes a scientific study of any one variable such as filler content difficult if not impossible. In the current study it was the aim to test the hypothesis that hardness measurements of dental composites could be used to monitor the status of the resin-filler interface and to determine the efficacy of any particle silanation process. Ten model composites formulated from a single batch of resin and containing a common type of glass filler were formulated to contain varying amounts of filler. Some materials contained silanated filler, others contained unsilanated filler. Specimens were prepared and stored in water and hardness (Vickers') was determined at 24 h using loads of 50, 100, 200 and 300 g. Composites containing silanated fillers were significantly harder than materials containing unsilanated fillers. For unsilanated products hardness was independent of applied load and in this respect they behaved like homogeneous materials. For composites containing silanated fillers there was a marked increase in measured hardness as applied load was increased. This suggests that the hardness-load profile could be used to monitor the status of the resin-filler interface. Copyright 1999 Kluwer Academic Publishers

Effect of conventional and sugar free pediatric syrup formulations on primary tooth enamel hardness: An in vitro study.

PubMed

Mali, Gaurao Vasant; Dodamani, Arun Suresh; Karibasappa, Gundabaktha Nagappa; Kumar, Prashanth Vishwakarma; Jain, Vardhaman Mulchand

2015-01-01

To assess and compare the effect of conventional and sugar free pediatric syrup formulations on primary tooth enamel hardness over a period of 14 days. An in vitro study was done on 40 noncarious deciduous teeth. 10 teeth in each group were dipped in 4 pediatric medicinal syrups (1 sugarfree and 3 conventional) for 1 min thrice daily for 14 days and the enamel surface micro hardness was checked at baseline, 7 th day and 14 th day by Vickers hardness testing machine. The pH, titratable acidity and buffering capacity of the syrups were assessed. The pH of syrups were above critical pH for demineralization of the tooth but tiratable acidity and buffering capacity differed. ANOVA test indicated that the reduction in mean micro hardness was maximum in Group D (Conventional Analgesic syrup) and least in Group A (Sugarfree cough syrup) on 7 th and 14 th day. On intergroup comparison there was no difference (P > 0.05) in micro hardness between Group B (Conventional Cough syrup) and Group C (Conventional Antibiotic). However, highly significant (P < 0.01) difference between the either pair of Group B with Group D, and Group C with Group D on 14 th day. The percentage reduction in micro hardness on 14 th day was maximum for Group D (24.4 ± 2.2) and minimum for Group A (14.0 ± 1.3) which was statistically significant (P < 0.01). Sugar free pediatric medicines can be effective in reducing dental erosion and efforts should be made to incorporate sugar substitutes in formulation of pediatric medicines.

Growth and characterization of Cadmium Thiosemicarbazide Bromide crystals for antibacterial and nonlinear optical applications

NASA Astrophysics Data System (ADS)

Thomas Joseph Prakash, J.; Martin Sam Gnanaraj, J.

2015-01-01

Semiorganic nonlinear optical crystals of Cadmium Thiosemicarbazide Bromide was grown by slow evaporation solution growth technique. The unit cell parameters were estimated by subjecting the crystals to single crystal X-ray diffraction. The grown crystals were subjected to Powder X-ray diffraction for analyzing the crystalline nature of the sample. FTIR studies reveal the functional groups and the optical characters were analyzed by UV-Vis spectral studies. Mechanical stability of the sample was assessed by Vicker's micro hardness test. The presence of surface dislocations was identified by chemical etching technique. Antibacterial study was carried out against ACDP declared harmful pathogens. SHG efficiency of CTSB crystal was tested using Nd: YAG laser and it was found to be ∼1.8 times that of potassium dihydrogen phosphate.

Effect of four over-the-counter tooth-whitening products on enamel microhardness.

PubMed

Majeed, A; Grobler, S R; Moola, M H; Oberholzer, T G

2011-10-01

This in vitro study evaluated the effect of four over-the-counter tooth-whitening products on enamel microhardness. Fifty enamel blocks were prepared from extracted human molar teeth. The enamel surfaces were polished up to 1200 grit fineness and the specimens randomly divided into five groups. Enamel blocks were exposed to: Rapid White (n=10); Absolute White (n=10); Speed White (n=10) and White Glo (n=10) whitening products, according to the manufacturers' instructions. As control, ten enamel blocks were kept in artificial saliva at 37 degrees C without any treatment. Microhardness values were obtained before exposure (baseline) and after 1, 7 and 14-day treatment periods using a digital hardness tester with a Vickers diamond indenter. Data were analysed using Wilcoxon Signed Rank Sum Test, one-way ANOVA and Tukey-Kramer Multiple Comparison Test (p<0.05). Both Rapid White and Absolute White reduced enamel microhardness. Speed White increased the microhardness of enamel, while White Glo and artificial saliva had no effect on hardness. Over-the-counter tooth-whitening products might decrease enamel microhardness depending on the type of product.

Bearing assembly and the like for use in corrosive and non-corrosive atmospheres

DOEpatents

Mashburn, Douglas N.; Woodall, Harold C.; Wright, Ralph R.

1979-01-01

This invention relates to a novel machine element characterized by mutually rubbing surfaces which are composed of dissimilar materials having high hardness, a low coefficient of friction, and resistance to corrosion by halogen-containing atmospheres. As exemplified by the preferred embodiment for use in gaseous UF.sub.6, the rubbing surfaces are chemically deposited nickel and anodized aluminum. These surfaces permit jam-free operation despite long-term exposure to UF.sub.6. Preferably, both surfaces have a hardness of at least about 500 HV.sub.100 on the Vickers hardness scale, and preferably the anodized-aluminum surface is of a type having comparatively little tendency to sorb uranium hexafluoride.

[A new machinability test machine and the machinability of composite resins for core built-up].

PubMed

Iwasaki, N

2001-06-01

A new machinability test machine especially for dental materials was contrived. The purpose of this study was to evaluate the effects of grinding conditions on machinability of core built-up resins using this machine, and to confirm the relationship between machinability and other properties of composite resins. The experimental machinability test machine consisted of a dental air-turbine handpiece, a control weight unit, a driving unit of the stage fixing the test specimen, and so on. The machinability was evaluated as the change in volume after grinding using a diamond point. Five kinds of core built-up resins and human teeth were used in this study. The machinabilities of these composite resins increased with an increasing load during grinding, and decreased with repeated grinding. There was no obvious correlation between the machinability and Vickers' hardness; however, a negative correlation was observed between machinability and scratch width.

Erosive effects of common beverages on extracted premolar teeth.

PubMed

Seow, W K; Thong, K M

2005-09-01

Dental erosion is highly prevalent today, and acidic drinks are thought to be an important cause. The aim of the present investigation was to determine the erosive potential of a range of common beverages on extracted human teeth. The beverages were tested for their individual pHs using a pH meter. The clinical effects of the most erosive beverages were determined by the degree of etching and Vickers microhardness of enamel. The results showed that many common beverages have pHs sufficiently low to cause enamel erosion. Lime juice concentrate (pH 2.1) had the lowest pH, followed by Coca-cola and Pepsi (both with pH 2.3) and Lucozade (pH 2.5). The erosive potential of these beverages was demonstrated by the deep etching of the enamel after five minutes. The Vickers Hardness of enamel was reduced by about 50 per cent in the case of lime juice (p < 0.001) and 24 per cent in the case of Coca-cola (p < 0.004). Addition of saliva to 50 per cent (v/v) of Coca-cola completely reversed the erosive effects on the enamel. Although only a few of the beverages with the lowest pHs were tested, the present study showed that the most acidic drinks had the greatest erosive effects on enamel. While saliva was protective against erosion, relatively large volumes were required to neutralize the acidity.

Micro-scale abrasive wear behavior of medical implant material Ti-25Nb-3Mo-3Zr-2Sn alloy on various friction pairs.

PubMed

Wang, Zhenguo; Huang, Weijiu; Ma, Yanlong

2014-09-01

The micro-scale abrasion behaviors of surgical implant materials have often been reported in the literature. However, little work has been reported on the micro-scale abrasive wear behavior of Ti-25Nb-3Mo-3Zr-2Sn (TLM) titanium alloy in simulated body fluids, especially with respect to friction pairs. Therefore, a TE66 Micro-Scale Abrasion Tester was used to study the micro-scale abrasive wear behavior of the TLM alloy. This study covers the friction coefficient and wear loss of the TLM alloy induced by various friction pairs. Different friction pairs comprised of ZrO2, Si3N4 and Al2O3 ceramic balls with 25.4mm diameters were employed. The micro-scale abrasive wear mechanisms and synergistic effect between corrosion and micro-abrasion of the TLM alloy were investigated under various wear-corrosion conditions employing an abrasive, comprised of SiC (3.5 ± 0.5 μm), in two test solutions, Hanks' solution and distilled water. Before the test, the specimens were heat treated at 760°C/1.0/AC+550°C/6.0/AC. It was discovered that the friction coefficient values of the TLM alloy are larger than those in distilled water regardless of friction pairs used, because of the corrosive Hanks' solution. It was also found that the value of the friction coefficient was volatile at the beginning of wear testing, and it became more stable with further experiments. Because the ceramic balls have different properties, especially with respect to the Vickers hardness (Hv), the wear loss of the TLM alloy increased as the ball hardness increased. In addition, the wear loss of the TLM alloy in Hanks' solution was greater than that in distilled water, and this was due to the synergistic effect of micro-abrasion and corrosion, and this micro-abrasion played a leading role in the wear process. The micro-scale abrasive wear mechanism of the TLM alloy gradually changed from two-body to mixed abrasion and then to three-body abrasion as the Vickers hardness of the balls increased. Copyright © 2014 Elsevier B.V. All rights reserved.

Thermal, mechanical, optical and dielectric properties of piperazinium hydrogen phosphite monohydrate NLO single crystal

NASA Astrophysics Data System (ADS)

Rajkumar, R.; Praveen Kumar, P.

2018-05-01

Optical transparent crystal of piperazinium hydrogen phosphite monohydrate (PHPM) was grown by slow evaporation method. The grown crystal was characterized by single crystal X-ray diffraction analysis and the crystal belongs to monoclinic system. The functional groups present in PHPM crystal were confirmed by FTIR analysis. UV-Visible spectrum shows that the PHPM crystal is transparent in the visible region. The mechanical behavior of PHPM crystal was characterized by Vickers hardness test. Thermal stability of PHPM crystal was analyzed by thermogravimetric analysis. Dielectric studies were also carried out for the grown crystal. The third-order nonlinear parameters such as nonlinear refractive index and nonlinear absorption coefficient have been calculated using Z scan technique.

High-Temperature Microindentation Tests on Olivine and Clinopyroxene

NASA Astrophysics Data System (ADS)

Dorner, D.; Schellewald, M.; Stöckhert, B.

2001-12-01

The perspectives of microindentation techniques for the investigation of the mechanical behaviour of minerals at high temperatures are explored. The technique offers the following advantages: (1) natural specimens with small grain size can be used, (2) preparation is simple, (3) a reasonable number of experiments can be performed within a short period of time. The strength of single crystals as a function of orientation and the activated glide systems are studied using scanning electron microscopy (SEM) combined with electron backscatter diffraction (EBSD) facilities. Furthermore, the effects of compositional variations on the flow strength of solid solutions are explored. The indentation hardness tests are performed on selected grains within natural polycrystalline aggregates. The surface of the specimen is polished mechanically and chemically. The orientation of the crystals is determined using EBSD. The indentation tests are performed with a diamond pyramid (Vickers indenter) at temperatures of 25 ° C to 900 ° C. Loading is done with a constant displacement rate up to a force of 0.5 N, followed by a creep period of 10 s at constant load. SEM is used to measure the size of the indents and to examine their morphology in detail. The microhardness obtained for olivine depends on crystal and indenter orientation and decreases slightly with temperature. Slip steps are observed on the surface around the indents. Their orientation with respect to the crystal orientation indicates that the predominant glide system activated in the indentation process is \\{110\\}[001]. The Schmid factors for this glide system correlate with the observed orientation dependence of the hardness. Indentation hardness of clinopyroxene solid solutions depends on composition with jadeite being stronger than diopside. This is inverse to what is expected for dislocation creep. The high yield stresses inferred from the hardness data and the weak dependence of hardness on temperature are consistent with plasticity being the deformation regime explored in indentation hardness tests.

Why do nickel-titanium archwires fracture intraorally? Fractographic analysis and failure mechanism of in-vivo fractured wires.

PubMed

Zinelis, Spiros; Eliades, Theodore; Pandis, Nikolaos; Eliades, George; Bourauel, Christoph

2007-07-01

The aim of this study was to characterize intraorally fractured nickel-titanium (Ni-Ti) archwires, determine the type of fracture, assess changes in the alloy's hardness and structure, and propose a mechanism of failure. Eleven Ni-Ti SE 200 and 19 copper-Ni-Ti (both, Ormco, Glendora, Calif) intraorally fractured archwires were collected. The location of fracture (anterior or posterior), wire type, cross section, and period of service before fracture were recorded. The retrieved wires and brand-, type-, and size-matched specimens of unused wires were subjected to scanning electron microscopy to assess the fracture type and morphological variation of fracture site of retrieved specimens, and to Vickers hardness (HV200) testing to investigate the hardness of as-received and in-vivo fractured specimens. Fracture site distribution was statistically analyzed with the chi-square test (alpha = 0.05), whereas the results of the hardness testing were analyzed with 2-way ANOVA with state (control vs in-vivo fractured) and composition (Ni-Ti SE vs copper-Ni-Ti) serving as discriminating variables and the Student-Newman-Keuls test at the 95% confidence level. The fracture site distribution showed a preferential location at the midspan between the premolar and the molar, suggesting that masticatory forces and complex loading during engagement of the wire to the bracket slot and potential intraoral aging might account for fracture incidence. All retrieved wires had the distinct features of brittle fracture without plastic deformation or crack propagation, whereas no increase in hardness was observed for the retrieved specimens. Most fractures sites were in the posterior region of the arch, probably because of the high-magnitude masticatory forces. Brittle fracture without plastic deformation was observed in most Ni-Ti wires regardless of archwire composition. There was no increase in the hardness of the intraorally exposed specimens regardless of wire type. This contradicts previous in-vitro studies and rules out hydrogen embrittlement as the cause of fracture.

Evaluation of microhardness, surface roughness, and wear behavior of different types of resin composites polymerized with two different light sources.

PubMed

Topcu, Fulya Toksoy; Erdemir, Ugur; Sahinkesen, Gunes; Yildiz, Esra; Uslan, Ibrahim; Acikel, Cengizhan

2010-02-01

The microhardness, surface roughness and wear resistance of different types of resin composites, polymerized by a Quartz Tungsten Halogen (QTH) or Light Emitting Diode (LED) light curing units (LCU) were evaluated in this in vitro study. Cylindrical blocks were prepared from composites (8 mm in diameter, and 2 mm in thickness) and polymerized by a LED or a QTH LCU. Vickers hardness was measured on the top and bottom surfaces of the specimens. Surface roughness was measured with a surface profilometer on the top of the specimens. For the wear test, specimens were tested in a conventional pin-on-disc tribology machine under 15 N loads. The statistical analyses were performed by one-way analysis of variance (ANOVA) and t-tests, including the Bonferroni correction. Nanocomposite material Clearfil Majesty Posterior showed the highest hardness values in all polymerization types at the top and bottom surfaces (p < 0.05). Microhybrid Clearfil APX and hybrid Quixfil composites demonstrated the greatest surface roughness. Wear resistance of Clearfil Majesty Posterior was found to be the highest among the other tested resin composites. The results indicated that Clearfil Majesty Posterior demonstrated higher microhardness, less surface roughness, and higher wear resistance when compared with the other tested materials for both polymerization types.

In Vitro Comparative Study of Two Different Bleaching Agents on Micro-hardness Dental Enamel.

PubMed

Fatima, Nazish; Ali Abidi, Syed Yawar; Meo, Ashraf Ali

2016-02-01

To evaluate the effect of home-use bleaching agent containing 16% Carbamide Peroxide (CP) and in-office bleaching agent containing 38% Hydrogen Peroxide (HP) on enamel micro-hardness. An in vitroexperimental study. Department of Operative Dentistry and Science of Dental Materials at Dr. Ishrat-ul-Ebad Khan Institute of Oral Health Sciences, Dow University of Health Sciences and Material Engineering Department of NED University of Engineering and Technology, Karachi, from July to December 2014. Atotal of 90 enamel slabs from 45 sound human 3rd molar were randomly divided into 3 groups. Each group contained 30 specimens (n=30). Group 1 was kept in artificial saliva at 37°C in incubator during the whole experiment. However, Groups 2 and 3 were treated with power whitening gel and tooth whitening pen respectively. After bleaching session, specimens were thoroughly rinsed with deionized water again for 10 seconds and then stored in artificial saliva at 37°C in incubator. Artificial saliva was changed after every 2 days. The Vickers hardness tester (Wolpert 402 MVD, Germany) was adjusted to a load of 0.1 kg (100 gm) and dwell time of 5 seconds. Three Vickers were performed on each specimen using a hardness tester according to the ISO 6507-3:1998 specification. Micro-hardness measurements were performed before and after bleaching at day 1, 7 and 14. In the control group, the baseline micro-hardness was 181.1 ±9.3 which was reduced after the storage on day 1, 7 and 14 (p = 0.104). In Group 2, baseline micro-hardness was 180.4 ±10.1 which was reduced to 179.79 ±10.0 units after day 1. Whereas, on day 7 and 14, the values of micro-hardness were 179.8 ±10 and 179.7 ±10.29, respectively (p=0.091). Furthermore, the baseline micro-hardness in Group 3 was 174.0 ±22.9 units which was reduced to 173 ±23 on day 1, 170 ±30 on day 7 and 173 ±23 on day 14 (p = 0.256). The statistically insignificant difference was found among micro-hardness values of different bleaching agents (p = 0.118). Bleaching with 38% Hydrogen Peroxide (HP) and 16% Carbamide Peroxide (CP) resulted in insignificant effect on surface micro-hardness of enamel.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tan, Yi, E-mail: tanyi@dlut.edu.cn; You, Xiaogang; You, Qifan

Electron beam smelting (EBS) has been used to fabricate the Inconel 740 superalloy. Microstructures, hardness, and deformation characteristics of the alloy are studied. It is observed that carbides and fine secondary phase nuclei are distributed in the hot worked EBS 740 superalloy. The Ostwald ripening occurs during solution treatment and leads to aggregation of the γ′ precipitates, the size of γ′ precipitates varies from several nanometers to more than one hundred nanometers as a result. The average size of the secondary phase is < 30 nm after aging treatment and the average Vickers hardness is measured to be about 370.more » The critical shear stress is calculated to be 0.627 GPa with governing mechanism of shearing, causing a stronger strengthening effect than the traditionally prepared Inconel 740 superalloy. The compression behavior indicates that the EBS 740 superalloy shows higher flow stress than 740H at low Zener-Hollomon parameter, which may arise from the undissolved γ′ precipitates and higher activation energy Q. The tensile results show that the fracture surface exhibits a ductile fracture pattern, in contrast to no obvious plastic deformation on the macroscopic fracture. Crack propagation proceeds in a transgranular fracture mode with facets and voids presented on the fracture surface. - Graphical abstract: Electron beam smelting (EBS) has been used to fabricate the Inconel 740 superalloy. Microstructures, hardness, and deformation characteristics of the alloy are studied. The average size of the secondary phase is < 30 nm after aging treatment and the average Vickers hardness is measured to be about 370. The critical shear stress is calculated to be 0.627 GPa with governing mechanism of shearing, causing a stronger strengthening effect than the traditionally prepared Inconel 740 superalloy. The EBS 740 superalloy shows higher flow stress than 740H at low Zener-Hollomon parameter, which may arise from the undissolved γ′ precipitates and higher activation energy Q. The EBS technology shows encouraging potential in preparation of nickel-based superalloys. Morphologies of γ′ precipitates and Vickers hardness as well as hot compression curves for electron beam smelting 740 superalloy. - Highlights: • Electron beam smelting, a novel method, was used to prepare the Inconel 740 superalloy. • The average size of the γ′ precipitates after aging treatment is < 30 nm. • The shearing mode generates a stronger strengthening effect than the traditional 740. • At low Zener-Hollomon parameter, the EBS 740 shows higher flow stress than 740H.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Greve, L., E-mail: lars.greve@volkswagen.de; Medricky, M., E-mail: miloslav.medricky@volkswagen.de; Andres, M., E-mail: miloslav.medricky@volkswagen.de

A comprehensive strain hardening and fracture characterization of different grades of boron steel blanks has been performed, providing the foundation for the implementation into the modular material model (MMM) framework developed by Volkswagen Group Research for an explicit crash code. Due to the introduction of hardness-based interpolation rules for the characterized main grades, the hardening and fracture behavior is solely described by the underlying Vickers hardness. In other words, knowledge of the hardness distribution within a hot-formed component is enough to set up the newly developed computational model. The hardness distribution can be easily introduced via an experimentally measured hardnessmore » curve or via hardness mapping from a corresponding hot-forming simulation. For industrial application using rather coarse and computationally inexpensive shell element meshes, the user material model has been extended by a necking/post-necking model with reduced mesh-dependency as an additional failure mode. The present paper mainly addresses the necking/post-necking model.« less

Influence of Ultrasonic Surface Rolling on Microstructure and Wear Behavior of Selective Laser Melted Ti-6Al-4V Alloy

PubMed Central

Wang, Zhen; Xiao, Zhiyu; Huang, Chuanshou; Wen, Liping; Zhang, Weiwen

2017-01-01

The present article studied the effect of ultrasonic surface rolling process (USRP) on the microstructure and wear behavior of a selective laser melted Ti-6Al-4V alloy. Surface characteristics were investigated using optical microscope, nano-indentation, scanning electron microscope, transmission electron microscope and laser scanning confocal microscope. Results indicated that the thickness of pore-free surfaces increased to 100~200 μm with the increasing ultrasonic surface rolling numbers. Severe work hardening occurred in the densified layer, resulting in the formation of refined grains, dislocation walls and deformation twins. After 1000 N 6 passes, about 15.5% and 14.1% increment in surficial Nano-hardness and Vickers-hardness was obtained, respectively. The hardness decreased gradually from the top surface to the substrate. Wear tests revealed that the friction coefficient declined from 0.74 (polished surface) to 0.64 (USRP treated surface) and the wear volume reduced from 0.205 mm−3 to 0.195 mm−3. The difference in wear volume between USRP treated and polished samples increased with sliding time. The enhanced wear resistance was concluded to be associated with the improvement of hardness and shear resistance and also the inhibition of delamination initiation. PMID:29048344

Degree of conversion and hardness of two different systems of the Vitrebond™ glass ionomer cement light cured with blue LED.

PubMed

Calixto, Luiz Rafael; Tonetto, Mateus Rodrigues; Pinto, Shelon Cristina Souza; Barros, Erico Damasceno; Borges, Alvaro Henrique; Lima, Fabricio Viana Pereira; de Andrade, Marcelo Ferrarezi; Bandéca, Matheus Coelho

2013-03-01

This study investigated the physicochemical properties of the new formulation of the glass ionomer cements through hardness test and degree of conversion by infrared spectroscopy (FTIR). Forty specimens (n = 40) were made in a metallic mold (4 mm diameter x 2 mm thickness) with two resin-modified glass ionomer cements, Vitrebond™ and Vitrebond™ Plus (3M/ ESPE). Each specimen was light cured with blue LED with power density of 500 mW/cm(2) during 30 s. Immediately after light curing, 24h, 48h and 7 days the hardness and degree of conversion was determined. The Vickers hardness was performed by the MMT-3 microhardness tester using load of 50 gm force for 30 seconds. For degree of conversion, the specimens were pulverized, pressed with KBr and analyzed with FT-IR (Nexus 470). The statistical analysis of the data by ANOVA showed that the Vitrebond™ and Vitrebond™ Plus were no difference significant between the same storage times (p > 0.05). For degree of conversion, the Vitrebond™ and Vitrebond™ Plus were statistically different in all storage times after light curing. The Vitrebond™ showed higher values than Vitrebond™ Plus (p < 0.05). The performance of Vitrebond™ had greater results for degree of conversion than Vitrebond™ Plus. The correlation between hardness and degree of conversion was no evidence in this study.

Laser cladding of tungsten carbides (Spherotene ®) hardfacing alloys for the mining and mineral industry

NASA Astrophysics Data System (ADS)

Amado, J. M.; Tobar, M. J.; Alvarez, J. C.; Lamas, J.; Yáñez, A.

2009-03-01

The abrasive nature of the mechanical processes involved in mining and mineral industry often causes significant wear to the associated equipment and derives non-negligible economic costs. One of the possible strategies to improve the wear resistance of the various components is the deposition of hardfacing layers on the bulk parts. The use of high power lasers for hardfacing (laser cladding) has attracted a great attention in the last decade as an alternative to other more standard methods (arc welding, oxy-fuel gas welding, thermal spraying). In laser cladding the hardfacing material is used in powder form. For high hardness applications Ni-, Co- or Fe-based alloys containing hard phase carbides at different ratios are commonly used. Tungsten carbides (WC) can provide coating hardness well above 1000 HV (Vickers). In this respect, commercially available WC powders normally contain spherical micro-particles consisting of crushed WC agglomerates. Some years ago, Spherotene ® powders consisting of spherical-fused monocrystaline WC particles, being extremely hard, between 1800 and 3000 HV, were patented. Very recently, mixtures of Ni-based alloy with Spherotene powders optimized for laser processing were presented (Technolase ®). These mixtures have been used in our study. Laser cladding tests with these powders were performed on low carbon steel (C25) substrates, and results in terms of microstructure and hardness will be discussed.

Evaluation of consolidation method on mechanical and structural properties of ODS RAF steel

NASA Astrophysics Data System (ADS)

Frelek-Kozak, M.; Kurpaska, L.; Wyszkowska, E.; Jagielski, J.; Jozwik, I.; Chmielewski, M.

2018-07-01

In the present work, the effects of the fabrication method on mechanical and structural properties of 12%Cr, 2%W, 0.25%Ti, 0.25%Y2O3 steels were investigated. Materials obtained by Spark Plasma Sintering (SPS), Hot Isostatic Pressing (HIP) and Hot Extrusion (HE) methods were studied. The microstructure was characterized by using Scanning Electron Microscopy (SEM) and Electron Backscatter Diffraction analysis (EBSD). Mechanical properties of the studied samples were evaluated by using Vickers micro hardness HV0.1, Small Punch Test (SPT) and nanoindentation (NI) methods. The analysis revealed that samples manufactured via HIP and SPS processes exhibit very similar properties, whereas SPS method produces material with slightly lower hardness. In addition, significantly lower mechanical properties of the specimens after HE process were observed. The study described in this article addresses also the problems of mechanical parameters measured in micro- and nano-scale experiments and aims to identify possible pitfalls related to the use of various manufacturing technologies.

Effect of target-fixture geometry on shock-wave compacted copper powders

NASA Astrophysics Data System (ADS)

Kim, Wooyeol; Ahn, Dong-Hyun; Yoon, Jae Ik; Park, Lee Ju; Kim, Hyoung Seop

2018-01-01

In shock compaction with a single gas gun system, a target fixture is used to safely recover a powder compact processed by shock-wave dynamic impact. However, no standard fixture geometry exists, and its effect on the processed compact is not well studied. In this study, two types of fixture are used for the dynamic compaction of hydrogen-reduced copper powders, and the mechanical properties and microstructures are investigated using the Vickers microhardness test and electron backscatter diffraction, respectively. With the assistance of finite element method simulations, we analyze several shock parameters that are experimentally hard to control. The results of the simulations indicate that the target geometry clearly affects the characteristics of incident and reflected shock waves. The hardness distribution and the microstructure of the compacts also show their dependence on the geometry. With the results of the simulations and the experiment, it is concluded that the target geometry affects the shock wave propagation and wave interaction in the specimen.

Properties of zirconia-toughened-alumina prepared via powder processing and colloidal processing routes.

PubMed

Rafferty, A; Alsebaie, A M; Olabi, A G; Prescott, T

2009-01-15

Alumina-zirconia composites were prepared by two routes: powder processing, and colloidal processing. Unstabilised zirconia powder was added to alumina in 5 wt%, 10 wt% and 20 wt% quantities. For the colloidal method, zirconium(IV) propoxide solution was added to alumina powder, also in 5 wt%, 10 wt% and 20 wt% quantities. Additions of glacial acetic acid were needed to form stable suspensions. Suspension stability was verified by pH measurements and sedimentation testing. For the powder processed samples Vickers hardness decreased indefinitely with increasing ZrO(2) additions, but for colloidal samples the hardness at first decreased but then increased again above >10 wt% ZrO(2). Elastic modulus (E) values decreased with ZrO(2) additions. However, samples containing 20 wt% zirconia prepared via a colloidal method exhibited a much higher modulus than the powder processed equivalent. This was due to the homogeneous dispersion of zirconia yielding a sample which was less prone to microcracking.

Microstructure Evolution and Mechanical Properties of Mg-14%Li-1%Al Alloy During the High-Pressure Torsion

NASA Astrophysics Data System (ADS)

Tian, Chenguang; Lu, Huimin; Zhao, Liyuan

The super-light LA141 (Mg-14%Li-1%Al) alloy was produced and processed by high-pressure torsion (HPT) under the imposed pressure of 3 GPa and different shear strains γ through 3, 6, 9 and 12 turns at room temperature (RT). The microstructure evolution of the alloy during the HPT treatment was investigated by transmission electron microscope (TEM) and optical microscope (OM). It turned out that the grains were substantially refined, and the optical microscope revealed that the grains of HPT processed samples at the edge of the disc were finer by comparison with the ones near the center of the disc. Later, Vickers indentation analysis was used to evaluate the micro-hardness of deformed samples, and tension test was employed to obtain the strength and elongation at room temperature. The results indicated that the micro-hardness and tensile strength had increased to a certain extent, and the elongation had been significantly improved.

Reduced tissue hardness of trabecular bone is associated with severe osteoarthritis.

PubMed

Dall'Ara, Enrico; Ohman, Caroline; Baleani, Massimiliano; Viceconti, Marco

2011-05-17

This study investigated whether changes in hardness of human trabecular bone are associated with osteoarthritis. Twenty femoral heads extracted from subjects without musculoskeletal diseases (subject age: 49-83 years) and twenty femoral heads extracted from osteoarthritic subjects (subject age: 42-85 years) were tested. Sixty indentations were performed along the main trabecular direction of each sample at a fixed relative distance. Two microstructures were found on the indenting locations: packs of parallel-lamellae (PL) and secondary osteons (SO). A 25gf load was applied for 15s and the Vickers Hardness (HV) was assessed. Trabecular tissue extracted from osteoarthritic subjects was found to be about 13% less hard compared to tissue extracted from non-pathologic subjects. However, tissue hardness was not significantly affected by gender or age. The SO was 10% less hard than the PL for both pathologic and non-pathologic tissues. A hardness of 34.1HV for PL and 30.8HV for SO was found for the non-pathologic tissue. For osteoarthritic tissue, the hardness was 30.2HV for PL and 27.1HV for SO. In the bone tissue extracted from osteoarthritic subjects the occurrence of indenting a SO (28%) was higher than that observed in the non-pathological tissue (15%). Osteoarthritis is associated with reduced tissue hardness and alterations in microstructure of the trabecular bone tissue. Gender does not significantly affect trabecular bone hardness either in non-pathological or osteoarthritic subjects. A similar conclusion can be drawn for age, although a larger donor sample size would be necessary to definitively exclude the existence of a slight effect. Copyright © 2011. Published by Elsevier Ltd.

Synthesis, characterization and bioactivity of a calcium-phosphate glass-ceramics obtained by the sol-gel processing method.

PubMed

Jmal, Nouha; Bouaziz, Jamel

2017-02-01

In this work, a calcium-phosphate glass-ceramics was successfully obtained by heat treatment of a mixture of 26.52 in wt.% of fluorapatite (Fap) and 73.48 in wt.% of 77S (77 SiO 2 14 CaO9 P 2 O 5 in wt.%) gel. The calcium phosphate-glass-ceramics was prepared by sol-gel process with tetraethyl orthosilicate (TEOS), triethyl phosphate (TEP), calcium nitrate and fluorapatite. The synthesized powders were characterized by some commonly used tools such as X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), 31 P magic angle spinning nuclear magnetic resonance (MAS-NMR), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and thin-film X-ray diffraction (TF-XRD). The obtained results seemed to confirm the nucleation and growth of hydroxyapatite (Hap) nano-phase in the glass. Moreover, an in-vitro evaluation of the glass-ceramic was performed. In addition, to assess its bioactive capacity, it was soaked in simulated body fluid (SBF) at different time intervals. The SEM, EDS and TF-XRD analyses showed the deposition of hydroxyapatite on the surface of the specimens after three days of immersion in SBF solution. The mechanical properties of the obtained material such as rupture strength, Vickers hardness and elastic modulus were measured. In addition, the friction coefficient of calcium phosphate-glass-ceramics was tested. The values of the composite of rupture strength (24MPa), Vickers hardness (214Hv), Young's modulus (52.3GPa), shear modulus (19GPa) and friction coefficient (0.327) were obtained. This glass-ceramics can have useful applications in dental prostheses. Indeed, this material may have promising applications for implants because of its content of fluorine, the effective protector against dental caries. Copyright © 2016 Elsevier B.V. All rights reserved.

X-ray and optical crystallographic parameters investigations of high frequency induction melted Al-(alpha-Al(2)O(3)) alloys.

PubMed

Bourbia, A; Draissia, M; Bedboudi, H; Boulkhessaim, S; Debili, M Y

2010-01-01

This article deals with the microstructural strengthening mechanisms of aluminium by means of hard alpha-Al(2)O(3) alumina fine particles. A broad of understanding views covering materials preparations, elaboration process, characterization techniques and associated microstructural characteristic parameters measurements is given. In order to investigate the microstructural characteristic parameters and the mechanical strengthening mechanisms of pure aluminium by hard fine particles, a set of Al-(alpha-Al(2)O(3)) alloys samples were made under vacuum by high fusion temperature melting, the high frequency (HF) process, and rapidly solidified under ambient temperature from a mixture of cold-compacted high-pure fine Al and alpha-Al(2)O(3) powders. The as-solidified Al-(alpha-Al(2)O(3)) alloys were characterized by means of X-ray diffraction (XRD) analyses, optical microscopy observations and Vickers microhardness tests in both brut and heat-treated states. It was found that the as-solidified HF Al-(alpha-Al(2)O(3)) alloys with compositions below 4 wt.% (alpha-Al(2)O(3)) are single-phase microstructures of the solid solution FCC Al phase and over two-phase microstructures of the solid solution FCC Al and the Rhombohedral alpha-Al(2)O(3) phases. The optical micrographs reveal the presence of a grain size refinement in these alloys. Vickers microhardness of the as-solidified Al-(alpha-Al(2)O(3)) is increased by means of pure fine alpha-Al(2)O(3) alumina particles. These combined effects of strengthening and grain size refinement observed in the as-solidified Al-(alpha-Al(2)O(3)) alloys are essentially due to a strengthening of Al by the alpha-Al(2)O(3) alumina particles insertion in the (HF) melted and rapidly solidified alloys.

Mechanical properties of Mo-Si-B alloys fabricated by using core-shell powder with dispersion of yttria nanoparticles

NASA Astrophysics Data System (ADS)

Byun, Jong Min; Bang, Su-Ryong; Choi, Won June; Kim, Min Sang; Noh, Goo Won; Kim, Young Do

2017-01-01

In recent years, refractory materials with excellent high-temperature properties have been in the spotlight as a next generation's high-temperature materials. Among these, Mo-Si-B alloys composed of two intermetallic compound phases (Mo5SiB2 and Mo3Si) and a ductile α-Mo phase have shown an outstanding thermal properties. However, due to the brittleness of the intermetallic compound phases, Mo-Si-B alloys were restricted to apply for the structural materials. So, to enhance the mechanical properties of Mo-Si-B alloys, many efforts to add rare-earth oxide particles in the Mo-Si-B alloy were performed to induce the improvement of strength and fracture toughness. In this study, to investigate the effect of adding nano-sized Y2O3 particles in Mo-Si-B alloy, a core-shell powder consisting of intermetallic compound phases as the core and nano-sized α-Mo and Y2O3 particles surrounding the core was fabricated. Then pressureless sintering was carried out at 1400 °C for 3 h, and the mechanical properties of sintered bodies with different amounts of Y2O3 particles were evaluated by Vickers hardness and 3-point bending test. Vickers hardness was improved by dispersed Y2O3 particles in the Mo-Si-B alloy. Especially, Mo-3Si-1B-1.5Y2O3 alloy had the highest value, 589 Hv. The fracture toughness was measured using Mo-3Si-1B-1.5Y2O3 alloy and the value indicated as 13.5 MPa·√m.

Effect of Er,Cr:YSGG laser irradiation on bovine enamel surface during in-office tooth bleaching ex vivo.

PubMed

Dionysopoulos, Dimitrios; Strakas, Dimitrios; Koliniotou-Koumpia, Eugenia; Koumpia, Effimia

2017-07-01

The aim of this in vitro study was to evaluate the effect of using Er,Cr:YSGG laser during in-office tooth bleaching on bovine enamel surface to evaluate the safety of this therapy on tooth tissues. Thirty-six enamel specimens were prepared from bovine incisors and divided into three groups: Group 1 specimens (control) received no bleaching treatment; Group 2 received a conventional in-office bleaching treatment (40 % H 2 O 2 ); Group 3 received laser-assisted bleaching procedure (40 % H 2 O 2 ) utilizing an Er,Cr:YSGG laser. The specimens were stored for 10 days after the bleaching treatment in artificial saliva. Vickers hardness was determined using a microhardness tester, and measurements for surface roughness were done using a VSI microscope. Three specimens for each experimental group were examined under SEM and mineral composition of the specimens was evaluated using EDS. Data were statistically analyzed using one-way ANOVA, Tukey's post hoc, Wilcoxon signed rank and Kruskal-Wallis tests (a = 0.05). The Vickers hardness of the enamel was reduced after in-office bleaching procedures (p < 0.05), and changes in surface morphology of the enamel were observed. However, the surface roughness of the enamel was not influenced (p > 0.05), and no changes in mineral composition of the enamel were detected after in-office bleaching procedures (p > 0.05). The laser-assisted bleaching treatment with Er,Cr:YSGG laser did not influence the enamel surface compared to the conventional bleaching technique. The safety of the use of Er,Cr:YSGG laser during in-office tooth bleaching regarding the surface properties of the enamel was confirmed under in vitro conditions.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Moraes, Paulo E.L., E-mail: pauloeduardo.leitedemoraes@gmail.com; Contieri, Rodrigo J., E-mail: contieri@fem.unicamp.br; Lopes, Eder S.N., E-mail: ederlopes@fem.unicamp.br

Ti and Ti alloys are widely used in restorative surgery because of their good biocompatibility, enhanced mechanical behavior and high corrosion resistance in physiological media. The corrosion resistance of Ti-based materials is due to the spontaneous formation of the TiO{sub 2} oxide film on their surface, which exhibits elevated stability in biological fluids. Ti–Nb alloys, depending on the composition and the processing routes to which the alloys are subjected, have high mechanical strength combined with low elastic modulus. The addition of Sn to Ti–Nb alloys allows the phase transformations to be controlled, particularly the precipitation of ω phase. The aimmore » of this study is to discuss the microstructure, mechanical properties and corrosion behavior of cast Ti–Nb alloys to which Sn has been added. Samples were centrifugally cast in a copper mold, and the microstructure was characterized using optical microscopy, scanning electron microscopy and X-ray diffractometry. Mechanical behavior evaluation was performed using Berkovich nanoindentation, Vickers hardness and compression tests. The corrosion behavior was evaluated in Ringer's solution at room temperature using electrochemical techniques. The results obtained suggested that the physical, mechanical and chemical behaviors of the Ti–Nb–Sn alloys are directly dependent on the Sn content. - Graphical abstract: Effects of Sn addition to the Ti–30Nb alloy on the elastic modulus. - Highlights: • Sn addition causes reduction of the ω phase precipitation. • Minimum Vickers hardness and elastic modulus occurred for 6 wt.% Sn content. • Addition of 6 wt.% Sn resulted in maximum ductility and minimum compression strength. • All Ti–30Nb–XSn (X = 0, 2, 4, 6, 8 and 10%) alloys are passive in Ringer's solution. • Highest corrosion resistance was observed for 6 wt.% Sn content.« less

Protection of Tempered Aluminum Alloy in Contact with the Environment

NASA Astrophysics Data System (ADS)

Araoyinbo, A. O.; Salleh, M. A. A. Mohd; Rahmat, A.; Azmi, A. I.; Rahim, W. M. F. Wan Abd; Perju, M. C.; Jin, T. S.

2018-06-01

In many service applications an increasing temperature or inadequate protections often give rise to localized forms of corrosion in an initially free and unprotected system. This research understudy the corrosion chemistry, the effect of chromium as the inhibitor, Vickers hardness test, and weight loss on tempered aluminium alloy 7075 in corrosive mediums. The tempers of the aluminium alloy used are T6 and T73 where obtained by solution heat treatment at 470°C and quenched before immersion test in acidic (pH3), and slightly alkaline (pH7.5) solutions. The results obtained were characterized by conventional weight loss process and morphology observation with a microscope. The surface morphology shows exfoliation form of corrosion and the weight loss analysis shows the as received sample experience more weight loss when compared with the other heat treated samples.

Physicochemical analysis of urinary stones from Dharmapuri district

NASA Astrophysics Data System (ADS)

Aslin Shamema, A.; Thanigai Arul, K.; Senthil Kumar, R.; Narayana Kalkura, S.

2015-01-01

Nephrolithiasis is a common disease caused by the multifactorial components such as geographical location, bacterial infection, low urine volume, and low intake of water. This disease induces severe metabolic abnormalities in the human body. As the prevalence of this disease was high in Dharmapuri district located in Tamil Nadu, urinary stones removed from the patients pertaining to this district were collected and to identify the toxic elements present in the stones. The presence of functional groups and phases of the stones were analyzed using X-ray diffraction (XRD), Fourier transform Raman spectroscopy and Fourier transform infrared spectroscopy (FT-IR). The majority of stones were found to be calcium oxalate monohydrate (COM) and mixed stones having minor existence of struvite and uric acid. Hexagonal shaped COM crystals, needle shaped uric acid crystals and layered arrangement of struvite crystals in the core region were revealed by Scanning Electron Microscopy (SEM). Thermo Gravimetric Analysis (TGA) was used to determine the thermal stability and the hardness of the stone which was measured using Vickers hardness (HV). The presence of toxic elements in stones such as zirconium and mercury was identified using Energy Dispersive X-ray Spectroscopy (EDS). The EDS analysis showed higher concentration of zirconium in the core region compared to the periphery. The percentage of zirconium was relatively high compared to other toxic elements in the stones. The Vickers hardness results indicated that high HV values in the core region than the periphery and this might be due to the presence of zirconium.

Effects of a low-shrinkage methacrylate monomer and monoacylphosphine oxide photoinitiator on curing efficiency and mechanical properties of experimental resin-based composites.

PubMed

Manojlovic, Dragica; Dramićanin, Miroslav D; Milosevic, Milos; Zeković, Ivana; Cvijović-Alagić, Ivana; Mitrovic, Nenad; Miletic, Vesna

2016-01-01

This study investigated the degree of conversion, depth of cure, Vickers hardness, flexural strength, flexural modulus and volumetric shrinkage of experimental composite containing a low shrinkage monomer FIT-852 (FIT; Esstech Inc.) and photoinitiator 2,4,6-trimethylbenzoyldiphenylphosphine oxide (TPO; Sigma Aldrich) compared to conventional composite containing Bisphenol A-glycidyl methacrylate (BisGMA) and camphorquinone-amine photoinitiator system. The degree of conversion was generally higher in FIT-based composites (45-64% range) than in BisGMA-based composites (34-58% range). Vickers hardness, flexural strength and modulus were higher in BisGMA-based composites. A polywave light-curing unit was generally more efficient in terms of conversion and hardness of experimental composites than a monowave unit. FIT-based composite containing TPO showed the depth of cure below 2mm irrespective of the curing light. The depth of cure of FIT-based composite containing CQ and BisGMA-based composites with either photoinitiator was in the range of 2.8-3.0mm. Volumetric shrinkage of FIT-based composite (0.9-5.7% range) was lower than that of BisGMA-based composite (2.2-12% range). FIT may be used as a shrinkage reducing monomer compatible with the conventional CQ-amine system as well as the alternative TPO photoinitiator. However, the depth of cure of FIT_TPO composite requires boosting to achieve clinically recommended thickness of 2mm. Copyright © 2015 Elsevier B.V. All rights reserved.

The characterization of ceramic alumina prepared by using additive glass beads

NASA Astrophysics Data System (ADS)

Suprapedi; Muljadi; Sardjono, Priyo

2018-01-01

The ceramic alumina has been made by using additive glass bead (5 and 10 % wt.). There are two kinds of materials, such as : gamma Alumina and glass bead. Synthesis of alumina was done by ball milling for 24 hours, then the mixed powder was dried in drying oven at 100 °C for 6 hours. Furthermore, the dried powder was mixed by using 2 % of PVA and continued with compacted to form a pellet with pressure of 50 MPA. The next step is sintering process with variation temperature of 1150, 1200, 1250, 1300 and 1400 °C and holding time for 2 hours. The characterization conducted are consist of test density, hardness, shrinkage, and microstructure. The results show that ceramic alumina with addition of 10 % wt. glass bead has the higher value of density, hardness and shrinkage than addition of 5% wt. glass bead. The highest characterization of ceramic alumina with addition 10 % glass bead was achieved at sintering temperature of 1400 °C with density 3.68 g/cm3, hardness vickers 780.40 Hv and shrinkage 15.23 %. The XRD results show that it was founds a corrundum (alpha Alumina) as dominant phase and mullite as minor phase.

Microstructures and Hardness of the High Chromium Oxide Dispersion Strengthened Alloy Fe-25Cr-Y2O3Sintered by the Arc Plasma Sintering (APS)

NASA Astrophysics Data System (ADS)

Bandriyana; Dimyati, Arbi; Sujatno, Agus; Salam, Rohmad; Sumaryo; Untoro, Pudji; Suharno, Bambang

2018-03-01

High chromium ODS alloy has been developed for application as structural material in high temperature nuclear reactor. In the present study, Fe-25Cr-Y2O3 with dispersed 0.5 wt.% Ytria (Y2O3) were synthesized and characterized by means of various techniques as a function of milling time 1, 2 and 3 hours. The alloy synthesis was carried out by the Mechanical Alloying (MA) process and subsequent sintering by means the new plasma technique using the APS apparatus. Scaning Electron Microscopy (SEM) and X-ray diffraction (XRD) were conducted for morphology and phase analysis. Evaluation of the mechanical properties was studied based on the Vickers hardness measurement. SEM examination revealed that the sample after sintering by APS method at different milling duration exhibited some particle aglomeration and homogenized oxide dispersion that obviously strengthened the alloy. The XRD test, however, proved the formation of the main phase Fe-Cr. The alloy showed exceptionally high hardness of 193 VHR which is mainly due to the grain refining that increase by the increasing of the milling time.

Ethanol postpolymerization treatment for improving the biocompatibility of acrylic reline resins.

PubMed

Neves, Cristina B; Lopes, Luís P; Ferrão, Helena F; Miranda, Joana P; Castro, Matilde F; Bettencourt, Ana F

2013-01-01

To evaluate the effect of postpolymerization treatment based on ethanol-aqueous solutions on the residual monomer (RM) content, flexural strength, microhardness, and cytotoxicity of hard chairside reline resins (Kooliner, Ufi Gel Hard). After polymerization, specimens were immersed in water, 20%, 50%, or 70% ethanol solutions at 23°C or 55°C for 10 minutes. Controls were left untreated. HPLC was used for the determination of RM content. Specimens were submitted to Vickers microhardness and 3-point loading flexural strength tests. Cytotoxicity of resin eluates was determined on human fibroblasts by assessing cellular mitochondrial function and lactate dehydrogenase release. Higher concentrations of ethanol promoted lower RM content at 55°C in both materials. The mechanical properties were maintained after 50% and 20% ethanol treatments in Kooliner and Ufi Gel Hard, respectively. Specimens submitted to those treatments showed significant reduction on cytotoxicity compared to immersion in hot water, the treatment of choice in the recent literature. Immersion of relined dentures in specific ethanol solutions at 55°C for 10 minutes can be considered an effective postpolymerization treatment contributing to increase materials biocompatibility. The proposed protocol is expeditious and easy to achieve with simple equipment in a dental office.

Synthesis and characterization of magnesium aluminate (MgAl2O4) spinel (MAS) thin films

NASA Astrophysics Data System (ADS)

Ahmad, Syed Muhammad; Hussain, Tousif; Ahmad, Riaz; Siddiqui, Jamil; Ali, Dilawar

2018-01-01

In a quest to identify more economic routes for synthesis of magnesium aluminate (MgAl2O4) spinel (MAS) thin films, dense plasma focus device was used with multiple plasma focus shots. Structural, bonding between composite films, surface morphological, compositional and hardness properties of MAS thin films were investigated by using x-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive x-rays (EDX) analysis and Vickers micro hardness test respectively. In XRD graph, the presence of MgAl2O4 diffraction peaks in crystallographic orientations (222), (400) and (622) pointed out the successful formation of polycrystalline thin films of MgAl2O4 with face centered cubic structure. The FTIR spectrums showed a major common transmittance band at 697.95 cm-1 which belongs to MgAl2O4. SEM micrographs illustrated a mesh type, granular and multi layers microstructures with significant melting effects. EDX spectrum confirmed the existence of magnesium, oxygen and aluminum in MAS films. A common increasing behavior in micro-hardness of composite MgAl2O4 films by increasing number of plasma focus shots was found.

Effect of sintering atmosphere on the hardness of ThO2

NASA Astrophysics Data System (ADS)

Baena, Angela; Cardinaels, Thomas; Van Eyken, Jelle; Puzzolante, Jean Louis; Binnemans, Koen; Verwerft, Marc

2016-08-01

The hardness and toughness of ThO2 sintered under reducing and oxidizing conditions has been investigated and, quite unexpectedly, a significant difference in hardness was observed for the entire range of porosities studied. Reducing conditions systematically yielded higher hardness values than oxidizing conditions. Extrapolated to zero porosity, the hardness for ThO2 is H0 = 10.5 ± 0.3 GPa for oxidizing conditions and H0 = 12.4 ± 0.7 GPa for reducing conditions. Toughness values have been derived from Vickers indentations; differences in toughness were insignificant and only a single value is proposed: KIC = 0.97 ± 0.12 MPa √m. The difference in hardness is attributed to the presence of point defects, also acting as color centers and causing grey coloration of ThO2 sintered under reducing conditions. Furthermore, and of interest for nuclear fuel production, is the finding that ThO2 sintered under reducing conditions is significantly easier to grind compared to material sintered under oxidizing conditions.

Corrosion behavior of sensitized duplex stainless steel.

PubMed

Torres, F J; Panyayong, W; Rogers, W; Velasquez-Plata, D; Oshida, Y; Moore, B K

1998-01-01

The present work investigates the corrosion behavior of 2205 duplex stainless steel in 0.9% NaCl solution after various heat-treatments, and compares it to that of 316L austenitic stainless steel. Both stainless steels were heat-treated at 500, 650, and 800 degrees C in air for 1 h, followed by furnace cooling. Each heat-treated sample was examined for their microstructures and Vickers micro-hardness, and subjected to the X-ray diffraction for the phase identification. Using potentiostatic polarization method, each heat-treated sample was corrosion-tested in 37 degrees C 0.9% NaCl solution to estimate its corrosion rate. It was found that simulated sensitization showed an adverse influence on both steels, indicating that corrosion rates increased by increasing the sensitization temperatures.

Effect of graphenenano-platelets on the mechanical properties of Mg/3wt%Al alloy-nanocomposite

NASA Astrophysics Data System (ADS)

Kumar, Pravir; Kujur, MilliSuchita; Mallick, Ashis; Sandar Tun, Khin; Gupta, Manoj

2018-04-01

The bulk Mg/3%Al/0.1%GNP alloy-nano composite was fabricated using powder metallurgy route assisted with microwave sintering and followed by hot extrusion. The microstructural and Raman spectroscopy studies were performed to characterize the graphene nano-platelet(GNP).EDX tests confirmed the presence and the homogeneous distribution of Al and graphene nano-platelets in the magnesium alloy-nanocomposite. The addition of 3 wt% Al and 0.1wt%GNP to the Mg changed Vicker hardness, ultimate tensile strength and failure strain by +46.15%,+17.6% and -5% respectively. The fabricated composite offers higher resistance to the local deformation than monolithic Mg and Mg/3%Al alloy, revealed by the load/unload-indentation depth curve.

Growth and properties of benzil doped benzimidazole (BMZ) single crystals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Babu, R. Ramesh, E-mail: rampap2k@yahoo.co.in; Crystal Growth and Crystallography Section, National Physical Laboratory, Krishnan Marg, New Delhi 110 012; Sukumar, M.

2010-09-15

In the present work, we have made an attempt to study the effect of benzil doping on the properties of benzimidazole single crystals. For this purpose we have grown pure and benzil doped benzimidazole single crystals by vertical Bridgman technique. The grown crystals were characterized by various characterization techniques. The presence of dopants confirmed by powder X-ray diffraction (XRD). Crystalline perfection of the grown crystals has been analysed by high-resolution X-ray diffraction (HRXRD). The transmittance, electrical property and mechanical strength have been analysed using UV-vis-NIR spectroscopic, dielectric and Vicker's hardness studies. The relative second harmonic generation efficiency of pure andmore » doped benzimidazole crystals measured using Kurtz powder test.« less

Hardness properties and microscopic investigation of crack- crystal interaction in SiO(2)-MgO-Al(2)O(3)-K(2)O-B(2)O(3)-F glass ceramic system.

PubMed

Roy, Shibayan; Basu, Bikramjit

2010-01-01

In view of the potential engineering applications requiring machinability and wear resistance, the present work focuses to evaluate hardness property and to understand the damage behavior of some selected glass-ceramics having different crystal morphologies with SiO(2)-MgO-Al(2)O(3)-K(2)O-B(2)O(3)-F composition, using static micro-indentation tests as well as dynamic scratch tests, respectively. Vickers hardness of up to 5.5 GPa has been measured in glass-ceramics containing plate like mica crystals. Scratch tests at a high load of 50 Nin artificial saliva were carried out in order to simulate the crack-microstructure interaction during real-time abrasion wear and machining operation. The experimental observations indicate that the novel "spherulitic-dendritic shaped "crystals, similar to the plate like crystals, have the potential to hinder the scratching induced crack propagation. In particular, such potential of the 'spherulitic-dendritic' crystals become more effective due to the larger interfacial area with the glass matrix as well as the dendritic structure of each mica plate, which helps in crack deflection and crack blunting, to a larger extent.While modest damage tolerant behavior is observed in case of 'spherulitic-dendritic' crystal containing material, severe brittle fracture of plate like crystals were noted, when both were scratched at 50 N load.

Effects of soldering and laser welding on bond strength of ceramic to metal.

PubMed

Aladağ, Akin; Cömlekoğlu, M Erhan; Dündar, Mine; Güngör, M Ali; Artunç, Celal

2011-01-01

Welding or soldering of metal frameworks negatively affects the overall bond strength between the veneering ceramic and metal. The purpose of this study was to evaluate the effect of soldering and laser-welding procedures on the bond strength between ceramic and metal. Thirty Ni-based metal specimens (Wiron 99) (8 × 4 × 4 mm) were fabricated and divided into 3 groups; soldered (S), laser welded (L), and control (untreated cast alloy) (n=10). In S and L specimens, a notch (1 × 1.5 mm) was prepared longitudinally on the surface of each specimen and filled with compatible alloy (Wiron soldering rods and Wiroweld NC, respectively). Vickers hardness measurements were made after polishing the surfaces with a metallographic polishing kit. A veneering ceramic (VITA VMK 95) was vibrated, condensed in a mold, and fired on the metal frameworks. The specimens were sectioned in 2 axes to obtain nontrimmed bar specimens with a bonding area of approximately 1 mm². Forty bars per block were obtained. Each bar was subjected to microtensile bond strength (μTBS) testing with a crosshead speed of 1 mm/min. The μTBS data (MPa) were recorded, and SEM was used for failure analysis of the tested bars. The measurements were statistically analyzed using a 1-way ANOVA and Tamhane tests (α=.05). The mean differences in μTBS of veneering ceramic to soldered (10.4 ±2.4 MPa) and laser-welded (11.7 ±1.3 MPa) metal surfaces were not significantly different and were significantly lower than that of the cast alloy (25.4 ±3.6 MPa) (P<.05). The mean Vickers hardness of cast alloy was significantly higher (236 ±17 HV) than soldered (114 ±9 HV) and laser-welded groups (129 ±11 HV) (P<.05). Soldering and laser welding significantly decreased the μTBS of a veneering ceramic to a base metal alloy. Copyright © 2011 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Comparative Effect of Different Polymerization Techniques on the Flexural and Surface Properties of Acrylic Denture Bases.

PubMed

Gad, Mohammed M; Fouda, Shaimaa M; ArRejaie, Aws S; Al-Thobity, Ahmad M

2017-05-22

Polymerization techniques have been modified to improve physical and mechanical properties of polymethylmethacrylate (PMMA) denture base, as have the laboratory procedures that facilitate denture construction techniques. The purpose of the present study was to investigate the effect of autoclave polymerization on flexural strength, elastic modulus, surface roughness, and the hardness of PMMA denture base resins. Major Base and Vertex Implacryl heat-polymerized acrylic resins were used to fabricate 180 specimens. According to the polymerization technique, tested groups were divided into: group I (water-bath polymerization), group II (short autoclave polymerization cycle, 60°C for 30 minutes, then 130°C for 10 minutes), and group III (long autoclave polymerization cycle, 60°C for 30 minutes, then 130°C for 20 minutes). Each group was divided into two subgroups based on the materials used. Flexural strength and elastic modulus were determined by a three-point bending test. Surface roughness and hardness were evaluated with a profilometer and Vickers hardness (VH) test, respectively. One-way ANOVA and the Tukey-Kramer multiple-comparison test were used for results analysis, which were statistically significant at p ≤ 0.05. Autoclave polymerization showed a significant increase in flexural strength and hardness of the two resins (p < 0.05). The elastic modulus showed a significant increase in the major base resin, while a significant decrease was seen for Vertex Implacryl in all groups (p < 0.05); however, there was no significant difference in surface roughness between autoclave polymerization and water-bath polymerization (p > 0.05). Autoclave polymerization significantly increased the flexural properties and hardness of PMMA denture bases, while the surface roughness was within acceptable clinical limits. For a long autoclave polymerization cycle, it could be used as an alternative to water-bath polymerization. © 2017 by the American College of Prosthodontists.

The Effect of Lucite Glass Reinforcement on the Properties of Conventional Glass-Ionomer Filling Materials

PubMed Central

Kazemi Yazdi, Haleh; Van Noort, Richard; Mansouri, Mona

2016-01-01

Statement of the Problem: The usage of glass ionomer cements (GICs) restorative materials are very limited due to lack of flexural strength and toughness. Purpose: The aim of this study was to investigate the effect of using a leucite glass on a range of mechanical and optical properties of commercially available conventional glass ionomer cement. Materials and Method: Ball milled 45μm leucite glass particles were incorporated into commercial conventional GIC, Ketac-Molar Easymix (KMEm). The characteristics of the powder particles were observed under scanning electron microscopy. The samples were made for each experimental group; KMEm and lucite- modified Ketac-Molar easy Mix (LMKMEm) according to manufacturer’s instruction then were collected in damp tissue and stored in incubator for 1 hour. The samples were divided into two groups, one stored in distilled water for 24 hours and the others for 1 week.10 samples were made for testing biaxial flexural strength after 1 day and 1 week, with a crosshead speed of 1mm/min, calculated in MPa. The hardness (Vickers hardness tester) of each experimental group was also tested. To evaluate optical properties, 3 samples were made for each experimental group and evaluated with a spectrophotometer. The setting time of modified GIC was measured with Gillmore machine. Result: The setting time in LMKMEm was 8 minutes. The mean biaxial flexural strength was LMKMEm/ 1day: 24.13±4.14 MPa, LMKMEm/ 1 week: 24.22±4.87 MPa KMEm/1day:28.87±6.31 MPa and KMEm/1 week: 26.65±5.82 MPa which were not statistically different from each other. The mean Vickers hardness was LMKMEm: 403±66 Mpa and KMEm: 358±22 MPa; though not statistically different from each other. The mean total transmittance (Tt) was LMKMEm: 15.9±0.7, KMEm: 22.3±1.2, the mean diffuse transmittance (Td) was LMKMEm: 12.2±0.5, KMEm: 18.0±0.5 which were statistically different from each other. Conclusion: Leucite glass can be incorporated with a conventional GIC without interfering with setting time. Yet, it did not improve the mechanical and optical properties of the GIC. PMID:27942546

The Effects of Metallurgical Factors on PWSCC Crack Growth Rates in TT Alloy 690 in Simulated PWR Primary Water

NASA Astrophysics Data System (ADS)

Yonezawa, Toshio; Watanabe, Masashi; Hashimoto, Atsushi

2015-06-01

Primary water stress corrosion cracking growth rates (PWSCCGRs) in highly cold-worked thermally treated (TT) Alloy 690 have been recently reported as exhibiting significant heat-to-heat variability. Authors hypothesized that these significant differences could be due to the metallurgical characteristics of each heat. In order to confirm this hypothesis, the effect of fundamental metallurgical characteristics on PWSCCGR measurements in cold-worked TT Alloy 690 has been investigated. The following new observations were made in this study: (1) Microcracks and voids were observed in or near eutectic crystals of grain boundary (GB) M23C6 carbides (primary carbides) after cold rolling, but were not observed before cold rolling. These primary carbides with microcracks and voids were observed in both lightly forged and as-cast and cold-rolled TT Alloy 690 (heat A) as well as in a cold-rolled TT Alloy 690 (heat Y) that simulated the chemical composition and carbide banded structure of the material previously tested by Paraventi and Moshier. However, this was not observed in precipitated (secondary) M23C6 GB carbides in heavily forged and cold-rolled TT Alloy 690 heat A and a cold-rolled commercial TT Alloy 690. (2) From microstructural analyses carried out on the various TT Alloy 690 test materials before and after cold rolling, the amount of eutectic crystals (primary carbides and nitrides) M23C6 and TiN depended on the chemical composition. In particular, the amount of M23C6 depended on the fabrication process. Microcracks and voids in or near the M23C6 and TiN precipitates were generated by the cold rolling process. (3) The PWSCCGRs observed in TT Alloy 690 were different for each heat and fabrication process. The PWSCCGR decreased with increasing Vickers hardness of each heat. However, for the same heats and fabrication processes, the PWSCCGR increased with increasing Vickers hardness due to cold work. Thus, the PWSCCGR must be affected not only by hardness (or equivalently the cold working ratio) but also by grain size, microcracks, and voids of primary M23C6 carbides, etc., which in turn depend on chemical composition and the fabrication process.

Effects of heat input on mechanical properties of metal inert gas welded 1.6 mm thick galvanized steel sheet

NASA Astrophysics Data System (ADS)

Rafiqul, M. I.; Ishak, M.; Rahman, M. M.

2012-09-01

It is usually a lot easier and less expensive to galvanize steel before it is welded into useful products. Galvanizing afterwards is almost impossible. In this research work, Galvanized Steel was welded by using the ER 308L stainless steel filler material. This work was done to find out an alternative way of welding and investigate the effects of heat input on the mechanical properties of butt welded joints of Galvanized Steel. A 13.7 kW maximum capacity MIG welding machine was used to join 1.6 mm thick sheet of galvanized steel with V groove and no gap between mm. Heat inputs was gradually increased from 21.06 to 25.07 joules/mm in this study. The result shows almost macro defects free welding and with increasing heat input the ultimate tensile strength and welding efficiency decrease. The Vickers hardness also decreases at HAZ with increasing heat input and for each individual specimen; hardness was lowest in heat affected zone (HAZ), intermediate in base metal and maximum in welded zone. The fracture for all specimens was in the heat affected zone while testing in the universal testing machine.

Application of Various NDT Methods for the Evaluation of Building Steel Structures for Reuse

PubMed Central

Fujita, Masanori; Masuda, Tomoya

2014-01-01

The reuse system proposed by the authors is an overall business system for realizing a cyclic reuse flow through the processes of design, fabrication, construction, maintenance, demolition and storage. The reuse system is one of the methods to reduce the environmental burden in the field of building steel structures. These buildings are assumed to be demolished within approximately 30 years or more for physical, architectural, economic and social reasons in Japan. In this paper, focusing on building steel structures used for plants, warehouses and offices without fire protection, the performance of steel structural members for reuse is evaluated by a non-destructive test. First, performance evaluation procedures for a non-destructive test, such as mechanical properties, chemical compositions, dimension and degradation, are shown. Tensile strengths are estimated using Vickers hardness measured by a portable ultrasonic hardness tester, and chemical compositions are measured by a portable optical emission spectrometer. The weldability of steel structural members is estimated by carbon equivalent and weld crack sensitivity composition using chemical compositions. Finally, the material grade of structural members of the building steel structure for reuse is estimated based on the proposed procedures. PMID:28788237

Microstructures and Mechanical Properties of Weld Metal and Heat-Affected Zone of Electron Beam-Welded Joints of HG785D Steel

NASA Astrophysics Data System (ADS)

Zhang, Qiang; Han, Jianmin; Tan, Caiwang; Yang, Zhiyong; Wang, Junqiang

2016-12-01

Vacuum electron beam welding (EBW) process was employed to butt weld 10-mm-thick HG785D high-strength steels. The penetration into the steel was adjusted by beam current. Microstructures at weld metal and heat-affected zone (HAZ) regions were comparatively observed. Mechanical properties of the EBWed joints including Vickers hardness, tensile and Charpy impact tests were evaluated. The results indicated that microstructures at the weld metal consisted of coarse lath martensite and a small amount of acicular martensite, while that in the HAZ was tempered sorbite and martensite. The grain size in the weld metal was found to be larger than that in the HAZ, and its proportion in weld metal was higher. The hardness in the weld metal was higher than the HAZ and base metal. The tensile strength and impact toughness in the HAZ was higher than that in the weld metal. All the behaviors were related to microstructure evolution caused by higher cooling rates and state of base metal. The fracture surfaces of tensile and impact tests on the optimized joint were characterized by uniform and ductile dimples. The results differed significantly from that obtained using arc welding process.

Application of Various NDT Methods for the Evaluation of Building Steel Structures for Reuse.

PubMed

Fujita, Masanori; Masuda, Tomoya

2014-10-22

The reuse system proposed by the authors is an overall business system for realizing a cyclic reuse flow through the processes of design, fabrication, construction, maintenance, demolition and storage. The reuse system is one of the methods to reduce the environmental burden in the field of building steel structures. These buildings are assumed to be demolished within approximately 30 years or more for physical, architectural, economic and social reasons in Japan. In this paper, focusing on building steel structures used for plants, warehouses and offices without fire protection, the performance of steel structural members for reuse is evaluated by a non-destructive test. First, performance evaluation procedures for a non-destructive test, such as mechanical properties, chemical compositions, dimension and degradation, are shown. Tensile strengths are estimated using Vickers hardness measured by a portable ultrasonic hardness tester, and chemical compositions are measured by a portable optical emission spectrometer. The weldability of steel structural members is estimated by carbon equivalent and weld crack sensitivity composition using chemical compositions. Finally, the material grade of structural members of the building steel structure for reuse is estimated based on the proposed procedures.

A hard oxide semiconductor with a direct and narrow bandgap and switchable p-n electrical conduction.

PubMed

Ovsyannikov, Sergey V; Karkin, Alexander E; Morozova, Natalia V; Shchennikov, Vladimir V; Bykova, Elena; Abakumov, Artem M; Tsirlin, Alexander A; Glazyrin, Konstantin V; Dubrovinsky, Leonid

2014-12-23

An oxide semiconductor (perovskite-type Mn2 O3 ) is reported which has a narrow and direct bandgap of 0.45 eV and a high Vickers hardness of 15 GPa. All the known materials with similar electronic band structures (e.g., InSb, PbTe, PbSe, PbS, and InAs) play crucial roles in the semiconductor industry. The perovskite-type Mn2 O3 described is much stronger than the above semiconductors and may find useful applications in different semiconductor devices, e.g., in IR detectors. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Hardness and Second Phase Percentage of Ni-Ti-Hf Compounds After Heat Treatment at 700C

NASA Technical Reports Server (NTRS)

Stanford, Malcolm K.

2017-01-01

The Vickers hardness and second phase precipitation of three ternary intermetallic Ni-Ti-Hf compounds containing either 1, 3 or 5 at.% Hf were compared to 60-Nitinol (55 at.% Ni - 45 at.% Ti). Heat treatment either at 700 C or with a subsequent aging step, hardened the 3 and 5 at.% Hf-containing ternaries to approximately 620 HV (56 HRC). Heat treatment increased the hardness of the 1 at.% Hf compound by more than 25 percent. Average hardness of the 3 and 5 at.% Hf ternaries, though higher than that of the binary Ni-Ti or the Ni-Ti-Hf compound containing 1 at.% Hf, appeared to be fairly insensitive to the different heat treatments. There was a drastic reduction of fatigue-enhancing second phase precipitates for the 5 at.% Hf ternaries compared to the other compounds. These results should guide materials selection for development of aerospace componentry.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hu, Xunxiang; Koyanagi, Takaaki; Fukuda, Makoto

In this paper, pure tungsten samples have been neutron irradiated in HFIR at 90–850 °C to 0.03–2.2 dpa. A dispersed barrier hardening model informed by the available microstructure data has been used to predict the hardness. Comparison of the model predictions and the measured Vickers hardness reveals the dominant hardening contribution at various irradiation conditions. For tungsten samples irradiated in HFIR, the results indicate that voids and dislocation loops contributed to the hardness increase in the low dose region (<0.3 dpa), while the formation of intermetallic second phase precipitation, resulting from transmutation, dominates the radiation-induced strengthening beginning with a relativelymore » modest dose (>0.6 dpa). Finally, the precipitate contribution is most pronounced for the HFIR irradiations, whereas the radiation-induced defect cluster microstructure can rationalize the entirety of the hardness increase observed in tungsten irradiated in the fast neutron spectrum of Joyo and the mixed neutron spectrum of JMTR.« less

Gradient microstructure and microhardness in a nitrided 18CrNiMo7-6 gear steel

NASA Astrophysics Data System (ADS)

Yang, R.; Wu, G. L.; Zhang, X.; Fu, W. T.; Huang, X.

2017-07-01

A commercial gear steel (18CrNiMo7-6) containing a tempered martensite structure was nitrided using a pressurized gas nitriding process under a pressure of 5 atm at 530 °C for 5 hours. The mechanical properties and microstructure of the nitrided sample were characterized by Vickers hardness measurements, X-ray diffraction, and backscatter electron imaging in a scanning electron microscope. A micro-hardness gradient was identified over a distance of 500 μm with hardness values of 900 HV at the top surface and 300 HV in the core. This micro-hardness gradient corresponds to a gradient in the microstructure that changes from a nitride compound layer at the top surface (∼ 20 μm thick) to a diffusion zone with a decreasing nitrogen concentration and precipitate density with distance from the surface, finally reaching the core matrix layer with a recovered martensite structure.

Effects of nitrogen ion implantation time on tungsten films deposited by DC magnetron sputtering on AISI 410 martensitic stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Malau, Viktor, E-mail: malau@ugm.ac.id; Ilman, Mochammad Noer, E-mail: noer-ilman@yahoo.com; Iswanto, Priyo Tri, E-mail: priyatri@yahoo.com

Nitrogen ion implantation time on tungsten thin film deposited on surface of AISI 410 steel has been performed. Tungsten thin film produced by dc magnetron sputtering method was deposited on AISI 410 martensitic stainless steel substrates, and then the nitrogen ions were implanted on tungsten thin film. The objective of this research is to investigate the effects of implantation deposition time on surface roughness, microhardness, specific wear and corrosion rate of nitrogen implanted on tungsten film. Magnetron sputtering process was performed by using plasma gas of argon (Ar) to bombardier tungsten target (W) in a vacuum chamber with a pressuremore » of 7.6 x 10{sup −2} torr, a voltage of 300 V, a sputter current of 80 mA for sputtered time of 10 minutes. Nitrogen implantation on tungsten film was done with an initial pressure of 3x10{sup −6} mbar, a fluence of 2 x 10{sup 17} ions/cm{sup 2}, an energy of 100 keV and implantation deposition times of 0, 20, 30 and 40 minutes. The surface roughness, microhardness, specific wear and corrosion rate of the films were evaluated by surfcorder test, Vickers microhardness test, wear test and potentiostat (galvanostat) test respectively. The results show that the nitrogen ions implanted deposition time on tungsten film can modify the surface roughness, microhardness, specific wear and corrosion rate. The minimum surface roughness, specific wear and corrosion rate can be obtained for implantation time of 20 minutes and the maximum microhardness of the film is 329 VHN (Vickers Hardness Number) for implantation time of 30 minutes. The specific wear and corrosion rate of the film depend directly on the surface roughness.« less

Indentation Behavior and Mechanical Properties of Tungsten/Chromium co-Doped Bismuth Titanate Ceramics Sintered at Different Temperatures

PubMed Central

Xu, Jiageng; Chen, Yu; Tan, Zhi; Nie, Rui; Wang, Qingyuan; Zhu, Jianguo

2018-01-01

A sort of tungsten/chromium(W/Cr) co-doped bismuth titanate (BIT) ceramics (Bi4Ti2.95W0.05O12.05 + 0.2 wt % Cr2O3, abbreviate to BTWC) are ordinarily sintered between 1050 and 1150 °C, and the indentation behavior and mechanical properties of ceramics sintered at different temperatures have been investigated by both nanoindentation and microindentation technology. Firstly, more or less Bi2Ti2O7 grains as the second phase were found in BTWC ceramics, and the grain size of ceramics increased with increase of sintering temperatures. A nanoindentation test for BTWC ceramics reveals that the testing hardness of ceramics decreased with increase of sintering temperatures, which could be explained by the Hall–Petch equation, and the true hardness could be calculated according to the pressure-state-response (PSR) model considering the indentation size effect, where the value of hardness depends on the magnitude of load. While, under the application of microsized Vickers, the sample sintered at a lower temperature (1050 °C) gained four linearly propagating cracks, however, they were observed to shorten in the sample sintered at a higher temperature (1125 °C). Moreover, both the crack deflection and the crack branching existed in the latter. The hardness and the fracture toughness of BTWC ceramics presented a contrary variational tendency with increase of sintering temperatures. A high sintering tends to get a lower hardness and a higher fracture toughness, which could be attributed to the easier plastic deformation and the stronger crack inhibition of coarse grains, respectively, as well as the toughening effect coming from the second phase. PMID:29584677

Hardness Evaluation of Composite Resins Cured with QTH and LED

PubMed Central

Esmaeili, Behnaz; Safarcherati, Hengameh; Vaezi, Assila

2014-01-01

Background and aims. Today light cured composites are widely used. Physical and mechanical properties of composites are related to the degree of conversion. Light curing unit (LCU) is an important factor for composite polymerization. Aim of this study is evaluation of composite resins hardness using halogen and LED light curing units. Materials and methods. In this study, 30 samples of Filtek Z250 and C-Fill composite resins were provided. Samples were light cured with Ultralume2, Valo and Astralis7. Vickers hardness number (VHN) was measured in 0, 1, 2 mm depth. Statistical analysis used: Data were analysed by SPSS software and compared with each other by T-test, one-way and two-way ANOVA and Post-hoc Tukey test. Results. In Filtek Z250, at top surface, VHN of Ultralume2 was higher than VHN of Valo (P = 0.02) and Astralis7 (P =0.04), but in depth of 1, 2 mm, VHN of Ultralume2 and Astralis7 were almost the same and both LCUs were more than Valo which the difference between Ultralume2 and Valo was significant in depth of 1mm (0.05) and 2mm (0.02). In C-Fill composite, at top surface, Astralis7 showed higher VHN, but in depth of 2 mm, performance of all devices were rather simi-lar. Conclusion. In Z250, which contains camphorquinone initiator, light cure LED Ultra-lume2 with narrow wavelength showed higher hardness number than Valo. In C-fill, in top surface, Astralis7 with more exposure time, resulted higher VHN. But In depth of 2 mm, various light curing devices had rather similar hardness number. PMID:25024838

Fabrication and characterization of Si3N4 ceramics without additives by high pressure hot pressing

NASA Technical Reports Server (NTRS)

Shimada, M.; Tanaka, A.; Yamada, T.; Koizumi, M.

1984-01-01

High pressure hot-pressing of Si3N4 without additives was performed using various kinds of Si3N4 powder as starting materials, and the relation between densification and alpha-beta phase transformation was studied. The temperature dependences of Vickers microhardness and fracture toughness were also examined. Densification of Si3N4 was divided into three stages, and it was found that densification and phase transformation of Si3N4 under pressure were closely associated. The results of the temperature dependence of Vickers microhardness indicated that the high-temperature hardness was strongly influenced not only by the density and microstructure of sintered body but also by the purity of starting powder. The fracture toughness values of Si3N4 bodies without additives were 3.29-4.39 MN/m to the 3/2 power and independent of temperature up to 1400 C.

Effects of applying anchovy (Stolephorus insularis) substrates on the microhardness of tooth enamel in Sprague-Dawley rats

NASA Astrophysics Data System (ADS)

Hendrik, Y. C.; Puspitawati, R.; Gunawan, H. A.

2017-08-01

Anchovies (Stolephorus insularis) contain high levels of fluor in the form of CaF2. The aim of this study is to analyze changes in tooth enamel microhardness after application of anchovy substrates by feeding or as a topical fluoridation material. An in vivo study of the lower left incisors of nine Sprague-Dawley rats was conducted. The sample was comprised of baseline and treatment groups, including feeding application, topical application, negative control feeding, and negative control topical groups. The treatment groups were given 5% anchovy substrates through feeding and topical applications. After treatment, tooth samples were extracted from each of the rats for examination, and statistical analyses were performed after determining hardness numbers for enamel surfaces using Vickers microhardness tester. Vickers hardness numbers (VHNs) for anchovy substrate application and consumption by feeding (440.3 ± 24.72) were higher than for the negative control (315.80 ± 17.51). VHNs for the topical application group were higher than for the negative control (347.28 ± 28.56) and for the feeding group. The use of anchovy as a fluoridation material in form of topical application is potentially an effective method for increasing the microhardness of the tooth enamel surface

Compatibility of martensitic/austenitic steel welds with liquid lead bismuth eutectic environment

NASA Astrophysics Data System (ADS)

Van den Bosch, J.; Almazouzi, A.

2009-04-01

The high-chromium ferritic/martensitic steel T91 and the austenitic stainless steel 316L are to be used in contact with liquid lead-bismuth eutectic (LBE), under high irradiation doses. Both tungsten inert gas (TIG) and electron beam (EB) T91/316L welds have been examined by means of metallography, scanning electron microscopy (SEM-EDX), Vickers hardness measurements and tensile testing both in inert gas and in LBE. Although the T91/316L TIG weld has very good mechanical properties when tested in air, its properties decline sharply when tested in LBE. This degradation in mechanical properties is attributed to the liquid metal embrittlement of the 309 buttering used in TIG welding of T91/316L welds. In contrast to mixed T91/316L TIG welding, the mixed T91/316L EB weld was performed without buttering. The mechanical behaviour of the T91/316L EB weld was very good in air after post weld heat treatment but deteriorated when tested in LBE.

Deformation Microstructures Near Vickers Indentations in SNO2/SI Coated Systems

NASA Astrophysics Data System (ADS)

Daria, G.; Evghenii, H.; Olga, S.; Zinaida, D.; Iana, M.; Victor, Z.

The micromechanical properties (hardness and brittleness) of the hard-on-hard SnO2 / Si-coated system (CS) and their modification depending the on load value has been studied. A nonmonotonic changing of microhardness with load growth was detected. The brittle/plastic behavior of the rigid/hard-on-hard SnO2 / Si CS and its response to concentrated load action explains it.A specific evolution of the indentation-deformed zone vs. load value attributed to the change in the internal stress redistribution between film and substrate was detected. It results in a brittleness indentation size effect (BISE) of the SnO2 / Si CS revealed in this experiment.It was shown that the greater portion of internal stresses under indentation is concentrated in the coating layer at small loads. This fact causes a strong elastic-plastic relaxation in the film and its delamination from substrate. The increase of brittle failure in the indentation-deformed zone with a decrease of indentation load was revealed.

On the Corrosion Performance of Monel 400 in Molten LiCl-Li2O-Li at 923 K

NASA Astrophysics Data System (ADS)

Phillips, William; Merwin, Augustus; Chidambaram, Dev

2018-06-01

The corrosion resistance of a Ni-Cu alloy, Monel 400, in molten LiCl-Li2O-Li at 923 K (650 °C) was investigated. Exposure testing of Monel 400 samples submerged in molten LiCl-2 wt pct Li2O solutions with Li concentrations between zero and 1 wt pct was performed at 923 K (650°C) for 20 hours. Post exposure surface analysis was performed using X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy, optical microscopy, micro-Vickers hardness testing, and X-ray photoelectron spectroscopy, while inductively coupled plasma optical emission spectroscopy was used to quantify the rate of material leaching. The extent of material degradation was observed to be strongly correlated to the concentration of metallic Li in the molten LiCl-Li2O system.

Hydroxyapatite Coatings on High Nitrogen Stainless Steel by Laser Rapid Manufacturing

NASA Astrophysics Data System (ADS)

Das, Ashish; Shukla, Mukul

2017-11-01

In this research, the laser rapid manufacturing (LRM) additive manufacturing process was used to deposit multifunctional hydroxyapatite (HAP) coatings on high nitrogen stainless steel. LRM overcomes the limitations of conventional coating processes by producing coatings with metallurgical bond, osseointegration, and infection inhibition properties. The microstructure, microhardness, antibacterial efficacy, and bioactivity of the coatings were investigated. The microstructure studies established that the coatings consist of austenite dendrites with HAP and some reaction products primarily occurring in the inter-dendritic regions. A Vickers microhardness test confirmed the hardness values of deposited HAP coatings to be higher than those of the bare 254SS samples, while a fluorescence activated cell sorting test confirmed their superior antibacterial properties as compared with pristine samples. The coated samples immersed in simulated body fluid showed rapid apatite forming ability. The results obtained in this research signify the potential application of the LRM process in synthesizing multifunctional orthopaedic coatings.

Effect of Various Heat Treatment Processes on Fatigue Behavior of Tool Steel for Cold Forging Die

NASA Astrophysics Data System (ADS)

Jin, S. U.; Kim, S. S.; Lee, Y. S.; Kwon, Y. N.; Lee, J. H.

Effects of various heat treatment processes, including "Q/T (quenching and tempering)", "Q/CT/T (Quenching, cryogenic treatment and tempering)", "Q/T (quenching and tempering) + Ti-nitriding" and "Q/CT/T (Cryogenic treatment and tempering) + Ti-nitriding", on S-N fatigue behavior of AISI D2 tool steel were investigated. The optical micrographs and Vicker's hardness values at near surface and core area were examined for each specimen. Uniaxial fatigue tests were performed by using an electro-magnetic resonance fatigue testing machine at a frequency of 80 Hz and an R ratio of -1. The overall resistance to fatigue tends to decrease significantly with Ti-nitriding treatment compared to those for the general Q/T and Q/CT/T specimens. The reduced resistance to fatigue with Ti-nitriding is discussed based on the microstructural and fractographic analyses.

Effects of N-vinylcaprolactam containing polyelectrolytes on hardness, fluoride release and water sorption of conventional glass ionomers.

PubMed

Moshaverinia, Alireza; Ansari, Sahar; Roohpour, Nima; Reshad, Mamaly; Schricker, Scott R; Chee, Winston Wl

2011-05-01

N-vinylcaprolactam (NVC) containing glass ionomers are promising dental restorative materials with improved mechanical properties; however, little information is available on other physical properties of this type of modified glass ionomer, especially their water sorption, fluoride releasing properties and microhardness. The purpose of this study was to investigate the effects of NVC-containing polyelectrolytes on microhardness, fluoride release and water sorption of conventional glass ionomer cements (GIC). The terpolymer of acrylic acid (AA), itaconic acid (IA) and N-vinylcaprolactam (NVC) with 8:1:1 and 7:1:2 (AA: IA: NVC) molar ratios was synthesized by free radical polymerization and characterized using 1H-NMR and FTIR. Experimental GIC specimens were made from a 50% solution of the synthesized terpolymer with Fuji IX powder in a 3.6:1 P/L ratio. Specimens were mixed and fabricated at room temperature. Vickers hardness was determined using a microhardness tester. Water sorption and fluoride releasing properties were also investigated. Commercial Fuji IX was used as the control group. All specimens were first conditioned in distilled water at 37°C for 1 day up to 1 month. Results for the experimental GIC were compared with the control group, using 1-way and 2-way ANOVA and the Tukey multiple range test (α=.05). The NVC-modified GIC exhibited higher mean values of Vickers hardness numbers (VHN). However, the data exhibited no statistically significant differences between the experimental and control groups. The experimental cement (TP2) absorbed significantly more water than the control group (P<.034). Additionally, NVC-containing specimens showed comparable fluoride releasing properties with almost the same fluoride burst and continued fluoride release from the bulk of the material. It was concluded that a hydrophilic monomer such as NVC might be able to increase the water sorption and decrease the amount of initial fluoride release of the glass ionomers. Hydrophilic monomer such as NVC might be able to increase the water sorption and decrease the amount of initial fluoride release of the glass ionomers. Copyright © 2011 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Effect of heat treatment on mechanical properties of age-hardenable gold alloy at intraoral temperature.

PubMed

Watanabe, I; Watanabe, E; Cai, Z; Okabe, T; Atsuta, M

2001-09-01

The aim of this study was to investigate the effect of various heat treatments on the mechanical properties of gold alloys capable of age-hardening at intraoral temperature. Dumbbell-shaped patterns (ISO 6871) were cast with three gold alloys (Sofard; NC Type-IV; Aurum Cast, NihombashiTokuriki Co.). The Sofard alloy is age-hardenable at intraoral temperature. The castings underwent various heat treatments [as-cast (AC); solution treatment (ST); high-temperature aging (HA); intraoral aging (IA)]. After these heat treatments, ultimate tensile strength (UTS), 0.2% offset yield strength (YS), and elongation (EL) were measured at a strain rate of 1.7x10(-4)/s. Fracture surfaces of the specimens after tensile testing were observed using SEM. Vickers hardness was also measured after heat treating. After IA, the hardness values of the Sofard alloy increased and reached values similar to the hardness of the Sofard specimens aged at high temperature (HA). The hardness values of the NC Type-IV and Aurum Cast specimens slightly increased after IA, but did not reach the values of the specimens after HA. All the Sofard, NC Type-IV and Aurum Cast specimens showed significantly (P<0.05) greater hardness values after HA, compared with the values after any other heat treatments (AC, ST and IA). The UTS and YS of the specimens indicated a tendency similar to the results obtained for hardness. The Sofard specimens with ST showed the greatest elongation compared to the corresponding NC Type-IV and Aurum Cast specimens. However, the elongation of the Sofard specimens was abruptly reduced after intraoral aging. Intraoral aging significantly improved the mechanical properties and hardness of the Sofard alloy.

Elastic and mechanical softening in boron-doped diamond

PubMed Central

Liu, Xiaobing; Chang, Yun-Yuan; Tkachev, Sergey N.; Bina, Craig R.; Jacobsen, Steven D.

2017-01-01

Alternative approaches to evaluating the hardness and elastic properties of materials exhibiting physical properties comparable to pure diamond have recently become necessary. The classic linear relationship between shear modulus (G) and Vickers hardness (HV), along with more recent non-linear formulations based on Pugh’s modulus extending into the superhard region (HV > 40 GPa) have guided synthesis and identification of novel superabrasives. These schemes rely on accurately quantifying HV of diamond-like materials approaching or potentially exceeding the hardness of the diamond indenter, leading to debate about methodology and the very definition of hardness. Elasticity measurements on such materials are equally challenging. Here we used a high-precision, GHz-ultrasonic interferometer in conjunction with a newly developed optical contact micrometer and 3D optical microscopy of indentations to evaluate elasticity-hardness relations in the ultrahard range (HV > 80 GPa) by examining single-crystal boron-doped diamond (BDD) with boron contents ranging from 50–3000 ppm. We observe a drastic elastic-mechanical softening in highly doped BDD relative to the trends observed for superhard materials, providing insight into elasticity-hardness relations for ultrahard materials. PMID:28233808

Elastic and mechanical softening in boron-doped diamond

NASA Astrophysics Data System (ADS)

Liu, Xiaobing; Chang, Yun-Yuan; Tkachev, Sergey N.; Bina, Craig R.; Jacobsen, Steven D.

2017-02-01

Alternative approaches to evaluating the hardness and elastic properties of materials exhibiting physical properties comparable to pure diamond have recently become necessary. The classic linear relationship between shear modulus (G) and Vickers hardness (HV), along with more recent non-linear formulations based on Pugh’s modulus extending into the superhard region (HV > 40 GPa) have guided synthesis and identification of novel superabrasives. These schemes rely on accurately quantifying HV of diamond-like materials approaching or potentially exceeding the hardness of the diamond indenter, leading to debate about methodology and the very definition of hardness. Elasticity measurements on such materials are equally challenging. Here we used a high-precision, GHz-ultrasonic interferometer in conjunction with a newly developed optical contact micrometer and 3D optical microscopy of indentations to evaluate elasticity-hardness relations in the ultrahard range (HV > 80 GPa) by examining single-crystal boron-doped diamond (BDD) with boron contents ranging from 50-3000 ppm. We observe a drastic elastic-mechanical softening in highly doped BDD relative to the trends observed for superhard materials, providing insight into elasticity-hardness relations for ultrahard materials.

Preparation of anti-adhesion surfaces on aluminium substrates of rubber plastic moulds using a coupling method of liquid plasma and electrochemical machining

NASA Astrophysics Data System (ADS)

Meng, Jianbing; Dong, Xiaojuan; Wei, Xiuting; Yin, Zhanmin

2014-03-01

Hard anti-adhesion surfaces, with low roughness and wear resistance, on aluminium substrates of rubber plastic moulds were fabricated via a new coupling method of liquid plasma and electrochemical machining. With the aid of liquid plasma thermal polishing and electrochemical anodic dissolution, micro/nano-scale binary structures were prepared as the base of the anti-adhesion surfaces. The anti-adhesion behaviours of the resulting aluminium surfaces were analysed by a surface roughness measuring instrument, a scanning electron microscope (SEM), a Fourier-transform infrared spectrophotometer (FTIR), an X-ray diffractometer (XRD), an optical contact angle meter, a digital Vickers micro-hardness (Hv) tester, and electronic universal testing. The results show that, after the liquid plasma and electrochemical machining, micro/nano-scale binary structures composed of micro-scale pits and nano-scale elongated boss structures were present on the sample surfaces. As a result, the anti-adhesion surfaces fabricated by the above coupling method have good anti-adhesion properties, better wear resistance and lower roughness.

Preparation of anti-adhesion surfaces on aluminium substrates of rubber plastic moulds using a coupling method of liquid plasma and electrochemical machining

DOE Office of Scientific and Technical Information (OSTI.GOV)

Meng, Jianbing, E-mail: jianbingmeng@126.com; Dong, Xiaojuan; Wei, Xiuting

Hard anti-adhesion surfaces, with low roughness and wear resistance, on aluminium substrates of rubber plastic moulds were fabricated via a new coupling method of liquid plasma and electrochemical machining. With the aid of liquid plasma thermal polishing and electrochemical anodic dissolution, micro/nano-scale binary structures were prepared as the base of the anti-adhesion surfaces. The anti-adhesion behaviours of the resulting aluminium surfaces were analysed by a surface roughness measuring instrument, a scanning electron microscope (SEM), a Fourier-transform infrared spectrophotometer (FTIR), an X-ray diffractometer (XRD), an optical contact angle meter, a digital Vickers micro-hardness (Hv) tester, and electronic universal testing. The resultsmore » show that, after the liquid plasma and electrochemical machining, micro/nano-scale binary structures composed of micro-scale pits and nano-scale elongated boss structures were present on the sample surfaces. As a result, the anti-adhesion surfaces fabricated by the above coupling method have good anti-adhesion properties, better wear resistance and lower roughness.« less

Correlation between some thermo-mechanical and physico-chemical properties in multi-component glasses of Se-Te-Sn-Cd system

NASA Astrophysics Data System (ADS)

Kumar, Amit; Mehta, Neeraj

2017-06-01

The glass transition phenomenon is guided by the swift cooling of a melt (glass-forming liquid). Consequently, the glass as a final product consists of a considerable number of micro-voids having the size of the order of atomic and/or molecular sizes. The model of free volume fluctuation helps in describing the diverse physico-chemical properties of amorphous materials (like glasses and polymers). This theory is based on the fraction of fluctuation free frozen at the glass transition temperature and it forms a basis for determination of various significant thermo-mechanical properties. In the present work, Vickers hardness test method is employed that provides useful information concerning the mechanical behavior of brittle solids. The present work emphasizes the results of micro-indentation measurements on recently synthesized novel Se78- x Te20Sn2Cd x glassy system. Basic thermo-mechanical parameters such as micro-hardness, volume ( V h), formation energy ( E h) of micro-voids in the glassy network and modulus of elasticity ( E) have been determined and their variation with glass composition has been investigated.

Mechanical and thermodynamic properties of AlX (X = N, P, As) compounds

NASA Astrophysics Data System (ADS)

Xu, Lifang; Bu, Wei

2017-09-01

The Vickers hardness of various AlX (X = N, P, As) compound polymorphs were calculated with the bond resistance model. Thermodynamic properties, such as vibrational entropy, constant volume specific heat and Debye temperatures, were calculated using phonon dispersion relations and phonon density of states (DOS). The calculated values are in good agreement with the previous experimental and theoretical data. For the same structure of AlX (X = N, P, As) compounds, their hardness and Debye temperatures both decrease with the X atomic number. The wurtzite (wz) and zincblende (zb) structures of the same compounds AlX share an almost identical hardness, but have different Debye temperatures. The difference between wz and zb structures increases as the atomic number of X increases. The thermodynamic properties reveal that the constant volume specific heat approaches the Dulong-Petit rule at high temperatures.

Surface characteristics changes in polymeric material by swift ion beam

NASA Astrophysics Data System (ADS)

Abdul-Kader, A. M.; El-Gendy, Y. A.

2018-03-01

In this work, polyethylene (PE) samples were subjected to 9 MeV Cl+2 ions with fluences ranging from 1 × 1013 to 5 × 1014 ion/cm2. Rutherford back scattering spectrometry (RBS), X-ray diffraction (XRD), ultraviolet-visible (UV-vis) spectroscopy and Vicker's micro-hardness (Hv) techniques were used to investigate the compositional transformation, changes in the structure, optical and surface hardness of bombarded samples. The adhesion parameters were analyzed using the contact angle measurements. The obtained results showed that the ion irradiation caused a decrease in the crystallinity of polyethylene and increase in absorption of oxygen on the polymer surface as well. The absorption edge shifted towards the red shift as Cl-ion fluence increases. It was found that the hardness and adhesion parameters increase with increasing the ion beam fluence.

Characterization of a Viking Blade Fabricated by Traditional Forging Techniques

NASA Astrophysics Data System (ADS)

Vo, H.; Frazer, D.; Bailey, N.; Traylor, R.; Austin, J.; Pringle, J.; Bickel, J.; Connick, R.; Connick, W.; Hosemann, P.

2016-12-01

A team of students from the University of California, Berkeley, participated in a blade-smithing competition hosted by the Minerals, Metals, and Materials Society at the TMS 2015 144th annual meeting and exhibition. Motivated by ancient forging methods, the UC Berkeley team chose to fabricate our blade from historical smithing techniques utilizing naturally-occurring deposits of iron ore. This approach resulted in receiving the "Best Example of a Traditional Blade Process/Ore Smelting Technique" award for our blade named "Berkelium." First, iron-enriched sand was collected from local beaches. Magnetite (Fe3O4) was then extracted from the sand and smelted into individual high- and low-carbon steel ingots. Layers of high- and low-carbon steels were forge-welded together, predominantly by hand, to form a composite material. Optical microscopy, energy dispersive spectroscopy, and Vickers hardness mechanical testing were conducted at different stages throughout the blade-making process to evaluate the microstructure and hardness evolution during formation. It was found that the pre-heat-treated blade microstructure was composed of ferrite and pearlite, and contained many nonmetallic inclusions. A final heat treatment was performed, which caused the average hardness of the blade edge to increase by more than a factor of two, indicating a martensitic transformation.

Mechanical Properties of ZnSe for the FEANICS Module

NASA Technical Reports Server (NTRS)

Salem, Jon

2006-01-01

Mechanical and physical properties of ZnSe windows to be used with the FEANICS (Flow Enclosure Accommodating Novel Investigations in Combustion of Solids) experiments were measured in order to determine design allowables. In addition, the literature on crack growth properties was summarized. The average Young's modulus, Poisson's ratio, equibiaxial fracture strength, flaw size, grain size, Knoop hardness, Vicker's hardness, and branching constant were 74.3 +/- 0.1 GPa, 0.31, 57.8 +/- 6.5 MPa, 21 4 mm, 43 +/- 9 micron, 0.97 +/- 0.02 GPa, 0.97 +/- 0.02 GPa, and 1.0 +/- 0.1 MPam(exp 0.5), respectively. The properties of current ZnSe made by chemical vapor deposition are in good agreement with those measured in the 1970's. The hardness of CVD ZnSe windows is about one twentieth of the sapphire window being replaced, and about one-sixth of that of window glass. Thus the ZnSe window must be handled with great care. The large grain size relative to the inherent crack size implies the need to use single crystal crack growth properties in the design process. In order to determine the local failure stresses in one of the test specimens, a solution for the stresses between the support ring and the edge of a circular plate load between concentric rings was derived.

Synthesis, Hardness, and Electronic Properties of Stoichiometric VN and CrN

DOE PAGES

Wang, Shanmin; Yu, Xiaohui; Zhang, Jianzhong; ...

2015-11-09

Here, we report synthesis of single-crystal VN and CrN through high-pressure ionexchange reaction routes. The final products are stoichiometric and have crystallite sizes in the range of 50-120 mu m. We also prepared VN and TiN crystals using high-pressure sintering of nitride powders. On the basis of single-crystal indentation testing, the determined asymptotic Vickers hardness for TiN, VN, and CrN is 18 (1), 10 (1), and 16 (1) GPa, respectively. Moreover, the relatively low hardness in VN indicates that the metallic bonding prevails due to the overfilled metallic a bonds, although the cation-anion covalent hybridization in this compound is muchmore » stronger than that in TiN and CrN. All three nitrides are intrinsically excellent metals at ambient pressure. In particular, VN exhibits superconducting transition at T-c approximate to 7.8 K, which is slightly lower than the reported values for nitrogen-deficient or crystallinedisordered samples due to unsuppressed "spin fluctuation" in the well-crystallized stoichiometric VN. The magnetostructural transition in CrN correlates with a metal metal transition at T-N = 240(5) K and is accompanied by a similar to 40% drop in electrical resistivity. Additionally, more detailed electronic properties are presented with new insights into these nitrides.« less

Ethanol Postpolymerization Treatment for Improving the Biocompatibility of Acrylic Reline Resins

PubMed Central

Neves, Cristina B.; Lopes, Luís P.; Ferrão, Helena F.; Miranda, Joana P.; Castro, Matilde F.; Bettencourt, Ana F.

2013-01-01

Objective. To evaluate the effect of postpolymerization treatment based on ethanol-aqueous solutions on the residual monomer (RM) content, flexural strength, microhardness, and cytotoxicity of hard chairside reline resins (Kooliner, Ufi Gel Hard). Methods. After polymerization, specimens were immersed in water, 20%, 50%, or 70% ethanol solutions at 23°C or 55°C for 10 minutes. Controls were left untreated. HPLC was used for the determination of RM content. Specimens were submitted to Vickers microhardness and 3-point loading flexural strength tests. Cytotoxicity of resin eluates was determined on human fibroblasts by assessing cellular mitochondrial function and lactate dehydrogenase release. Results. Higher concentrations of ethanol promoted lower RM content at 55°C in both materials. The mechanical properties were maintained after 50% and 20% ethanol treatments in Kooliner and Ufi Gel Hard, respectively. Specimens submitted to those treatments showed significant reduction on cytotoxicity compared to immersion in hot water, the treatment of choice in the recent literature. Significance. Immersion of relined dentures in specific ethanol solutions at 55°C for 10 minutes can be considered an effective postpolymerization treatment contributing to increase materials biocompatibility. The proposed protocol is expeditious and easy to achieve with simple equipment in a dental office. PMID:23971038

Microstructural Evolution and Local Mechanical Properties of Friction Stir Processed Mg-3Gd-1Zn Cast Alloy

NASA Astrophysics Data System (ADS)

Sabbaghian, M.; Mahmudi, R.

2016-05-01

Microstructural evolution, hardness, and shear strength of the cast plates of GZ31 magnesium alloy were investigated after friction stir processing (FSP). Due to severe plastic deformation and dynamic recrystallization, FSP breaks the dendrites and results in a fine homogenous structure in the stirred zone (SZ) having average grain sizes of about 4.0 and 2.5 μm in the one and two-pass FSPed plates, respectively. As a novel approach, strength of the processed plates was examined by shear punch testing in three regions of the SZ on the surface layer, namely, center line (CL), retreating side (RS), and advancing side (AS). FSP showed great potential in the enhancement of SZ ultimate shear strength from 114 to about 152 and 155 MPa in the one and two-pass FSPed materials, respectively. The same trend was observed in hardness values of the SZ, where the average hardness of the base material increased from 41 to 60 and 68 Vickers after one and two passes of FSP, respectively. The variations in the shear strength of the CL, RS, and AS zones of the SZ were about 5% for the first pass of FSP, the effect which was decreased to less than 2% after two passes of FSP.

Cut marks on bone surfaces: influences on variation in the form of traces of ancient behaviour

PubMed Central

Braun, David R.; Pante, Michael; Archer, William

2016-01-01

Although we know that our lineage has been producing sharp-edged tools for over 2.6 Myr, our knowledge of what they were doing with these tools is far less complete. Studies of these sharp-edged stone tools show that they were most probably used as cutting implements. However, the only substantial evidence of this is the presence of cut marks on the bones of animals found in association with stone tools in ancient deposits. Numerous studies have aimed to quantify the frequency and placement of these marks. At present there is little consensus on the meaning of these marks and how the frequency relates to specific behaviours in the past. Here we investigate the possibility that mechanical properties associated with edges of stone tools as well as the properties of bones themselves may contribute to the overall morphology of these marks and ultimately their placement in the archaeological record. Standardized tests of rock mechanics (Young's modulus and Vickers hardness) indicate that the hardness of tool edges significantly affects cut-mark morphology. In addition, we show that indentation hardness of bones also impacts the overall morphology of cut marks. Our results show that rock type and bone portions influence the shape and prevalence of cut marks on animal bones. PMID:27274806

Hardness, elastic, and electronic properties of chromium monoboride

DOE PAGES

Han, Lei; Wang, Shanmin; Zhu, Jinlong; ...

2015-06-03

Here, we report high-pressure synthesis of chromium monoboride (CrB) at 6 GPa and 1400 K. The elastic and plastic behaviors have been investigated by hydrostatic compression experiment and micro-indentation measurement. CrB is elastically incompressible with a high bulk modulus of 269.0 (5.9) GPa and exhibits a high Vickers hardness of 19.6 (0.7) GPa under the load of 1 kg force. Based on first principles calculations, the observed mechanical properties are attributed to the polar covalent Cr-B bonds interconnected with strong zigzag B-B covalent bonding network. The presence of metallic Cr bilayers is presumably responsible for the weakest paths in shearmore » deformation.« less

The Effect of Tempering Process on Microstructural Characteristics and Mechanical Properties of Induction Bend Pipe

NASA Astrophysics Data System (ADS)

Yu, Hao; Zhou, Tao

The heat treatment during manufacturing process of induction bend pipe had been simulated. The evolutions of ferrite, M/A island and substructure after tempering at 500 700 °C were characterized by means of optical microscopy, positron annihilation technique, SEM, TEM, XRD and EBSD. The mechanical performance was evaluated by tensile test, Charpy V-notch impact test (-20 °C) and Vickers hardness test (10 kgf). Microstructure observations showed that fine and homogenous M/A islands as well as dislocation packages in quasi-polygonal ferrite matrix after tempering at 600 650 °C generated optimal combination of strength and toughness. After tempering at 700 °C, the yield strength decreased dramatically. EBSD analysis indicated that the effective grain size diminished with the tempering temperature increasing. It could cause more energy cost during microcrack propagation process with subsequent improvement in impact toughness. Dislocation analysis suggested that the decrease and pile-up of dislocation benefited the combination of strength and toughness.

Mechanical Characteristics of Submerged Arc Weldment in API Gas Pipeline Steel of Grade X65

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hashemi, S. H.; Mohammadyani, D.

The mechanical properties of submerged arc weldment (SAW) in gas transportation pipeline steel of grade API X65 (65 ksi yield strength) were investigated. This steel is produced by thermo mechanical control rolled (TMC), and is largely used in Iran gas piping systems and networks. The results from laboratory study on three different regions; i.e. base metal (BM), fusion zone (FZ) and heat affected zone (HAZ) were used to compare weldment mechanical characteristics with those specified by API 5L (revision 2004) standard code. Different laboratory experiments were conducted on test specimens taken from 48 inch outside diameter and 14.3 mm wallmore » thickness gas pipeline. The test results showed a gradient of microstructure and Vickers hardness data from the centerline of FZ towards the unaffected MB. Similarly, lower Charpy absorbed energy (compared to BM) was observed in the FZ impact specimens. Despite this, the API specifications were fulfilled in three tested zones, ensuring pipeline structural integrity under working conditions.« less

Effect of pre-strain on precipitation and exfoliation corrosion resistance in an Al-Zn-Mg alloy

NASA Astrophysics Data System (ADS)

Lu, Xianghan; Du, Zhiwei; Han, Xiaolei; Li, Ting; Wang, Guojun; Lu, Liying; Bai, Xiaoxia; Zhou, Tietao

2017-12-01

To investigate the effect of pre-strain on behaviors in a specially developed Al-4.5Zn-1.2Mg alloy, transmission electron microscopy (TEM) bright field (BF) imaging combined with select area electron diffraction (SAED), Vickers-hardness tests and electrical conductivity tests was conducted for insight into precipitation in aluminum (Al) matrix during two step ageing, and standard exfoliation corrosion (EXCO) test combined with high-angle angular dark field scanning transmission electron microscopy (HAADF-STEM) and scanning electron microscopy (SEM) was carried out for corrosion behavior. Results showed that pre-strain accelerated precipitation during two step ageing as the sequence of: (i) supersaturated solid solution (SSS), GPI zones precipitations, GPI dissolution; (ii) SSS, fcc precipitates, η’ phases or η phases. And the precipitation hardening of the fcc precipitates was not effective as GPI zones. Pre-strain also accelerated EXCO developing, which was mainly attributed to the coverage ratio of η phases on high-angle grain boundaries (HAGBs) increasing as pre-strain increase.

CHIPPING FRACTURE RESISTANCE OF DENTURE TOOTH MATERIALS

PubMed Central

Quinn, G. D.; Giuseppetti, A. A.; Hoffman, K. H.

2014-01-01

Objective The applicability of the edge chipping method to denture tooth materials was assessed. These are softer materials than those usually tested by edge chipping. The edge chipping fracture resistances of polymethylmethacrylate (PMMA) based and two filled resin composite denture tooth materials were compared. Methods An edge chipping machine was used to chip rectangular blocks and flattened anterior denture teeth. Force versus edge distance data were collected over a broad range of forces and distances. Between 20 and 65 chips were made per condition depending upon the material, the scatter, and the indenter type. Different indenter types were used including Rockwell C, sharp conical 120°, Knoop, and Vickers. The edge toughness, Te, was evaluated for different indenter types. Results The edge chipping data collected on the blocks matched the data collected from flattened teeth. High scatter, particularly at large distances and loads, meant that many tests (up to 64) were necessary to compare the denture tooth materials and to ascertain the appropriate data trends. A linear force – distance trend analysis was adequate for comparing these materials. A power law trend might be more appropriate, but the large scatter obscured the definitive determination of the precise trend. Different indenters produce different linear trends, with the ranking of: sharp conical 120°, Rockwell C, and Knoop, from lowest to highest edge toughness. Vickers indenter data were extremely scattered and a sensible trend could not be obtained. Edge toughness was inversely correlated to hardness. Significance Edge chipping data collected either from simple laboratory scale test blocks or from actual denture teeth may be used to evaluate denture materials. The edge chipping method’s applicability has been extended to another class of restorative materials. PMID:24674342

Effects of delayed finishing/polishing on surface roughness, hardness and gloss of tooth-coloured restorative materials.

PubMed

Yazici, A Ruya; Tuncer, Duygu; Antonson, Sibel; Onen, Alev; Kilinc, Evren

2010-01-01

The aim of this study was to investigate the effect of delayed finishing/polishing on the surface roughness, hardness and gloss of tooth-coloured restorative materials. Four different tooth-coloured restoratives: a flowable resin composite- Tetric Flow, a hybrid resin composite- Venus, a nanohybrid resin composite- Grandio, and a polyacid modified resin composite- Dyract Extra were used. 30 specimens were made for each material and randomly assigned into three groups. The first group was finished/polished immediately and the second group was finished/polished after 24 hours. The remaining 10 specimens served as control. The surface roughness of each sample was recorded using a laser profilometer. Gloss measurements were performed using a small-area glossmeter. Vickers microhardness measurements were performed from three locations on each specimen surface under 100g load and 10s dwell time. Data for surface roughness and hardness were analyzed by Kruskal Wallis test and data for gloss were subjected to one-way ANOVA and Tukey test (P <.05). The smoothest surfaces were obtained under Mylar strip for all materials. While there were no significant differences in surface roughness of immediate and delayed finished/polished Dyract Extra samples, immediately finished/polished Venus and Grandio samples showed significantly higher roughness than the delayed polished samples (P <.05). In Tetric Flow samples, immediately finishing/polishing provided smoother surface than delayed finishing/polishing (P <.05). The highest gloss values were recorded under Mylar strip for all materials. While delayed finishing/polishing resulted in a significantly higher gloss compared to immediate finishing/polishing in Venus samples (P <.05), no differences were observed between delayed or immediate finishing/polishing for the other materials (P>.05). The lowest hardness values were found under Mylar strip. Delayed finishing/polishing significantly increased the hardness of all materials. The effect of delayed finishing/polishing on surface roughness, gloss and hardness appears to be material dependent.

Mechanical properties of β-HMX.

PubMed

Gallagher, Hugh G; Miller, John C; Sheen, David B; Sherwood, John N; Vrcelj, Ranko M

2015-01-01

For a full understanding of the mechanical properties of a material, it is essential to understand the defect structures and associated properties and microhardness indentation is a technique that can aid this understanding. The Vickers hardness on (010), {011} and {110} faces lay in the range of 304-363 MPa. The Knoop Hardnesses on the same faces lay in the range 314-482 MPa. From etching of three indented surfaces, the preferred slip planes have been identified as (001) and (101). For a dislocation glide, the most likely configuration for dislocation movement on the (001) planes is (001) [100] (|b| = 0.65 nm) and for the (101) plane as (101) [Formula: see text] (|b| = 1.084 nm) although (101) [010] (|b| = 1.105 nm) is possible. Tensile testing showed that at a stress value of 2.3 MPa primary twinning occurred and grew with increasing stress. When the stress was relaxed, the twins decreased in size, but did not disappear. The twinning shear strain was calculated to be 0.353 for the (101) twin plane. HMX is considered to be brittle, compared to other secondary explosives. Comparing HMX with a range of organic solids, the values for hardness numbers are similar to those of other brittle systems. Under the conditions developed beneath a pyramidal indenter, dislocation slip plays a major part in accommodating the local deformation stresses. Graphical abstractHMX undergoing tensile testing.

Static and fatigue mechanical behavior of three dental CAD/CAM ceramics.

PubMed

Homaei, Ehsan; Farhangdoost, Khalil; Tsoi, James Kit Hon; Matinlinna, Jukka Pekka; Pow, Edmond Ho Nang

2016-06-01

The aim of this study was to measure the mechanical properties and fatigue behavior of three contemporary used dental ceramics, zirconia Cercon(®) (ZC), lithium disilicate e.max(®) CAD (LD), and polymer-infiltrated ceramic Enamic(®) (PIC). Flexural strength of each CAD/CAM ceramic was measured by three point bending (n=15) followed by Weibull analysis. Elastic modulus was calculated from the load-displacement curve. For cyclic fatigue loading, sinusoidal loading with a frequency of 8Hz with minimum load 3N were applied to these ceramics (n=24) using three point bending from 10(3) to 10(6) cycles. Fatigue limits of these ceramics were predicted with S-N fatigue diagram. Fracture toughness and Vickers hardness of the ceramics were measured respectively by single edge V-notch beam (SEVNB) and microindentation (Hv 0.2) methods. Chemical compositions of the materials׳ surfaces were analyzed by EDS, and microstructural analysis was conducted on the fracture surfaces by SEM. One-way ANOVA was performed and the level of significance was set at 0.05 to analyze the numerical results. The mean flexural strength of ZC, LD, and PIC was respectively 886.9, 356.7, and 135.8MPa. However, the highest Weibull modulus belonged to PIC with 19.7 and the lowest was found in LD with 7.0. The fatigue limit of maximum load for one million cycles of ZC, LD, and PIC was estimated to be 500.1, 168.4, and 73.8GPa. The mean fracture toughness of ZC, LD, and PIC was found to be respectively 6.6, 2.8, and 1.4MPam(1/2), while the mean Vickers hardness was 1641.7, 676.7, and 261.7Hv. Fracture surfaces followed fatigue loading appeared to be smoother than that after monotonic loading. Mechanical properties of ZC were substantially superior to the two other tested ceramics, but the scattering of data was the least in PIC. The fatigue limit was found to be approximately half of the mean flexural strength for all tested ceramics. Copyright © 2016 Elsevier Ltd. All rights reserved.

Effect of a common diet and regular beverage on enamel erosion in various temperatures: an in-vitro study.

PubMed

Khamverdi, Zahra; Vahedi, Mohammad; Abdollahzadeh, Shermin; Ghambari, Mohammad Hosein

2013-09-01

This study compared diet and regular Coca-Cola on enamel erosion in cold and room temperatures. Seventy five enamel specimens were prepared and divided into 5 equal groups (N=15) as follows: Group 1: regular beverage at room temperature, Group 2: regular beverage at refri-gerator temperature, Group 3: diet beverage at room and Group 4: diet beverage at refrige-rator temperature. The specimens were immersed in the regular or diet beverage (Coca-Cola, trade mark regd. Khoshgovar Co., Tehran, Iran) at room (20°C) or refrigerator (2°C) temperatures for 20 minutes, 3 times per day for 7 days. Specimens in the control subjects (group 5) were placed in synthetic saliva at room temperature for 7 days. The hardness of specimens was tested using Vickers test under 500 gr loads for 5 seconds. The data were analyzed using two-way ANOVA and Tukey tests. The mean and standard deviations of micro-hardness values of the studied groups were as follow: G1: 304.26±29.71, G2: 285.53±42.14, G3: 279.06±39.52, G4: 266.80±23.98 and G5: 319± 30.79. There was a significant difference in the beverage type as the main factor (p<0.05), but temperature factor and their interaction effect on enamel hardness showed no significant difference (p>0.05). Tukey tests showed that there were significant differences between control and diet groups as well as regular and diet groups. Diet Coca-Cola is more erosive than the regular type and the temperature of the beverages used had no significant influence on enamel erosion.

Effect of a Common Diet and Regular Beverage on Enamel Erosion in Various Temperatures: An In-Vitro Study

PubMed Central

Khamverdi, Zahra; Vahedi, Mohammad; Abdollahzadeh, Shermin; Ghambari, Mohammad Hosein

2013-01-01

Objective: This study compared diet and regular Coca-Cola on enamel erosion in cold and room temperatures. Materials and Methods: Seventy five enamel specimens were prepared and divided into 5 equal groups (N=15) as follows: Group 1: regular beverage at room temperature, Group 2: regular beverage at refri-gerator temperature, Group 3: diet beverage at room and Group 4: diet beverage at refrige-rator temperature. The specimens were immersed in the regular or diet beverage (Coca-Cola, trade mark regd. Khoshgovar Co., Tehran, Iran) at room (20°C) or refrigerator (2°C) temperatures for 20 minutes, 3 times per day for 7 days. Specimens in the control subjects (group 5) were placed in synthetic saliva at room temperature for 7 days. The hardness of specimens was tested using Vickers test under 500 gr loads for 5 seconds. The data were analyzed using two-way ANOVA and Tukey tests. Results: The mean and standard deviations of micro-hardness values of the studied groups were as follow: G1: 304.26±29.71, G2: 285.53±42.14, G3: 279.06±39.52, G4: 266.80±23.98 and G5: 319± 30.79. There was a significant difference in the beverage type as the main factor (p<0.05), but temperature factor and their interaction effect on enamel hardness showed no significant difference (p>0.05). Tukey tests showed that there were significant differences between control and diet groups as well as regular and diet groups. Conclusion: Diet Coca-Cola is more erosive than the regular type and the temperature of the beverages used had no significant influence on enamel erosion. PMID:24910648

Comparison of enamel remineralization potential after application of titanium tetra fluoride and carbon dioxide laser

PubMed Central

Fekrazad, Reza; Najafi, Ahmad; Mahfar, Ramona; Namdari, Mahshid

2017-01-01

Background and Aims The aim was comparison of enamel remineralization after application of APF, TiF4 and CO2 laser alone or in combination. Materials and Methods Enamel blocks were prepared from human third molars. The initial surface hardness was determined by Vicker's hardness tester. The samples underwent a demineralization regimen for 7 days to produce artificial initial caries. The hardness of enamel blocks with white spot lesions was measured, and the samples which had the mean hardness change of 65–90%, were selected, and randomly divided into 5 groups (N=15): G1: control; G2: APF 1.23%; G3: TiF4 4%; G4: TiF4 4% followed by CO2 laser (10.6 µm wavelength, 1 W peak power, 10 ms pulse duration, 500 ms repeat time, 0.2 mm beam spot size, 2 cm distance); G5: CO2 laser (same parameters) followed by TiF4 4%. Surface hardness recovery was measured after the treatments. Three samples in each group were observed under scanning electron microscope at ×1,000 magnification. Data were analyzed by repeated measure ANOVA and Bonferrouni tests. Significance level was set at 0.05. Results G2, G3, G4 indicated significant differences with control and G5 (p<0.05). Surface hardness in G5 was not significantly different from control (p=0.7) in enamel hardness test. There was not a significant difference between G2 & G3, G2 & G4, and G3 & G4 (p=1). The SEM results indicated globules of calcium fluoride on the surface in G2, and a smooth glaze-like surface layer in G3 and G4. In G5, some micro-cracks without any glaze-like layer were observed. Conclusions APF, TiF4 and TiF4 before CO2 laser irradiation significantly increased the micro-hardness of initially demineralized enamel surfaces. CO2 laser irradiation before TiF4 application could not remineralize the white-spot lesions. PMID:28785131

Room Temperature Elastic Moduli and Vickers Hardness of Hot-Pressed LLZO Cubic Garnet

DTIC Science & Technology

2012-01-01

polishing compounds, Leco, St. Joseph, MI). X - ray diffraction and scanning electron microscopy (SEM) The microstructure of the hot-pressed specimens...was examined on uncoated fracture surfaces by SEM with an accelerating voltage of 1 and 3 kV. Phase purity was evaluated from X - ray diffraction data...the micro- structure appeared to be homogenous for the two hot- pressed LLZO specimens included in this study (Fig. 1). X - ray diffraction confirmed that

The effect of nitrogen gas flow rate on heat treatment of AISI SS-430: Study of microstructure and hardness

NASA Astrophysics Data System (ADS)

Sebayang, Perdamean; Darmawan, Bobby Aditya; Simbolon, Silviana; Alfirano, Sudiro, Toto; Aryanto, Didik

2018-05-01

The aim of this research was to obtain the austenite phase from ferritic stainless steel through sample heat treatment. The AISI 430 ferritic steel with the thickness of about 0.4 mm was used. The heat treatment was conducted in a tube furnace at elevated temperature of 1150, 1200, 1250 °C and nitrogen gas flow rate of 0.57 and 0.73 l/s. The samples were then rapidly quenched in water bath. An optical microscope, XRD, SEM-EDS and micro vickers hardness tester were used to characterize the sample before and after het treatment. The presence of anneal twins indicated the formation of austenite phase in the sample. Its fraction was varied from 10.89 wt% to 35.10 wt%. In addition, the heat treatment temperature strongly affected the sample hardness. The optimum hardness obtained was about 542.69 HV. According to the results, this material can be considered for biomedical applications.

Enhanced properties of nanostructured TiO2-graphene composites by rapid sintering

NASA Astrophysics Data System (ADS)

Shon, In-Jin; Yoon, Jin-Kook; Hong, Kyung-Tae

2018-01-01

Despite of many attractive properties of TiO2, the drawback of TiO2 ceramic is low fracture toughness for widely industrial application. The method to improve the fracture toughness and hardness has been reported by addition of reinforcing phase to fabricate a nanostructured composite. In this regard, graphene has been evaluated as an ideal second phase in ceramics. Nearly full density of nanostructured TiO2-graphene composite was achieved within one min using pulsed current activated sintering. The effect of graphene on microstructure, fracture toughness and hardness of TiO2-graphene composite was evaluated using Vickers hardness tester and field emission scanning electron microscopy. The grain size of TiO2 in the TiO2-x vol% (x = 0, 1, 3, and 5) graphene composite was greatly reduced with increase in addition of graphene. Both hardness and fracture toughness of TiO2-graphene composites simultaneously increased in the addition of graphene.

Irradiation hardening of pure tungsten exposed to neutron irradiation

DOE PAGES

Hu, Xunxiang; Koyanagi, Takaaki; Fukuda, Makoto; ...

2016-08-26

In this paper, pure tungsten samples have been neutron irradiated in HFIR at 90–850 °C to 0.03–2.2 dpa. A dispersed barrier hardening model informed by the available microstructure data has been used to predict the hardness. Comparison of the model predictions and the measured Vickers hardness reveals the dominant hardening contribution at various irradiation conditions. For tungsten samples irradiated in HFIR, the results indicate that voids and dislocation loops contributed to the hardness increase in the low dose region (<0.3 dpa), while the formation of intermetallic second phase precipitation, resulting from transmutation, dominates the radiation-induced strengthening beginning with a relativelymore » modest dose (>0.6 dpa). Finally, the precipitate contribution is most pronounced for the HFIR irradiations, whereas the radiation-induced defect cluster microstructure can rationalize the entirety of the hardness increase observed in tungsten irradiated in the fast neutron spectrum of Joyo and the mixed neutron spectrum of JMTR.« less

The effect of condensation pressure on selected physical properties of mineral trioxide aggregate.

PubMed

Nekoofar, M H; Adusei, G; Sheykhrezae, M S; Hayes, S J; Bryant, S T; Dummer, P M H

2007-06-01

To examine the effect of condensation pressure on surface hardness, microstructure and compressive strength of mineral trioxide aggregate (MTA). White ProRoot MTA (Dentsply Tulsa Dental, Johnson City, TN, USA) was mixed and packed into cylindrical polycarbonate tubes. Six groups each of 10 specimens were subjected to pressures of 0.06, 0.44, 1.68, 3.22, 4.46 and 8.88 MPa respectively. The surface hardness of each specimen was measured using Vickers microhardness. Cylindrical specimens of 4 mm in diameter and 6 mm in height were prepared in polycarbonate cylindrical moulds for testing the compressive strength. Five groups of 10 specimens were prepared using pressures of 0.06, 0.44, 1.68, 3.22 or 4.46 MPa. Data were subjected to one-way anova. The microstructure was analysed using a scanning electron microscope (SEM) after sectioning specimens with a scalpel. A trend was observed for higher condensation pressures to produce lower surface hardness values. A condensation pressure of 8.88 MPa produced specimens with significantly lower values in terms of surface hardness than other groups (P<0.001). A condensation pressure of 1.68 MPa conferred the maximum compressive strength; however, it was not statistically different. Higher condensation pressures resulted in fewer voids and microchannels when analysed with SEM. In specimens prepared with lower condensation pressures distinctive crystalline structures were observed. They tended to appear around microchannels. Condensation pressure may affect the strength and hardness of MTA. Use of controlled condensation pressure in sample preparation for future studies is suggested.

Processing of AlCoCrFeNiTi high entropy alloy by atmospheric plasma spraying

NASA Astrophysics Data System (ADS)

Löbel, M.; Lindner, T.; Kohrt, C.; Lampke, T.

2017-03-01

High Entropy Alloys (HEA) are gaining increasing interest due to their unique combination of properties. Especially the combination of high mechanical strength and hardness with distinct ductility makes them attractive for numerous applications. One interesting alloy system that exhibits excellent properties in bulk state is AlCoCrFeNiTi. A high strength, wear resistance and high-temperature resistance are the necessary requirements for the application in surface engineering. The suitability of blended, mechanically ball milled and inert gas atomized feedstock powders for the development of atmospheric plasma sprayed (APS) coatings is investigated in this study. The ball milled and inert gas atomized powders were characterized regarding their particle morphology, phase composition, chemical composition and powder size distribution. The microstructure and phase composition of the thermal spray coatings produced with different feedstock materials was investigated and compared with the feedstock material. Furthermore, the Vickers hardness (HV) was measured and the wear behavior under different tribological conditions was tested in ball-on-disk, oscillating wear and scratch tests. The results show that all produced feedstock materials and coatings exhibit a multiphase composition. The coatings produced with inert gas atomized feedstock material provide the best wear resistance and the highest degree of homogeneity.

Growth and characterization of novel organic 3-Hydroxy Benzaldehyde-N-methyl 4 Stilbazolium Tosylate crystals for NLO applications.

PubMed

Jagannathan, K; Umarani, P; Ratchagar, V; Ramesh, V; Kalainathan, S

2016-01-15

The 3-Hydroxy Benzaldehyde-N-methyl 4-Stilbazolium Tosylate (3- HBST) is a new organic NLO crystal and it is a new derivative in stilbazolium tosylate family. In this work we have synthesized 3-HBST and the single crystal was grown by conventional slow cooling method. The structure and lattice parameters of the grown crystal were determined by the single crystal X-ray diffraction (XRD) technique and it is exhibiting good crystalline nature which is observed from the powder XRD. In order to check the crystalline quality the rocking curve was recorded using multi crystal X-ray diffractometer. The functional groups were identified from both FTIR and NMR spectral analyses. The π-π* and n-π* optical transition energy levels were estimated from the absorption peaks. The NLO property was confirmed by measuring relative SHG efficiency by Kurtz powder test; it shows 24 times higher SHG efficiency than that of urea. In order to test the mechanical stability the Vickers and Knoop micro hardness measurement were carried out and found that the micro hardness number decreases with increasing load. The melting point was determined from Differential Scanning Colorimetry (DSC). Copyright © 2015 Elsevier B.V. All rights reserved.

High pressure infiltration sintering behavior of WC-Co alloys

NASA Astrophysics Data System (ADS)

Fan, Xiaoqin; He, Duanwei; Wang, Pei; Li, Dong; Liu, Yinjuan; Ma, Dejiang; Du, Yanchun; Gao, Shangpan; Kou, Zili

2016-10-01

In this paper, two average tungsten carbide particle sizes of 2, 0.5 μm are placed respectively, in contact with a WC-16Co substrate, pressed at the pressure of 4.5-5.5 GPa, and heated to temperatures ranging from 1350°C to 1500°C in a large-volume cubic press. During the process Co was forced out of the WC-16Co substrate into the compressed powder. The resulting infiltrated samples were characterized using X-ray diffraction (XRD), scanning electron microscope (SEM), Vickers hardness and cutting performance tests. The results of XRD confirmed that the sintered bulks have WC and Co phases. The scanning electron microscopy (SEM) analysis reveals that the WC grains in well-sintered alloys are round in shape and cobalt with lower content is uniformly dispersed in the WC grain boundaries. The sintered sub-micron WC-Co alloy with a cobalt content of 3.8 wt% exhibits a prominent combination of high hardness value of 23.1 GPa and a large fracture toughness value of 8.6 MPa m½. The high-speed cutting tests indicating its cutting performance is significantly superior to the commercial YG6X (WC-6 wt%Co with WC grain size of 0.5 μm).

Evaluation of fracture toughness of ZrO 2 and Si 3N 4 engineering ceramics following CO 2 and fibre laser surface treatment

NASA Astrophysics Data System (ADS)

Shukla, P. P.; Lawrence, J.

2011-02-01

The fracture toughness property ( K1C) of Si 3N 4 and ZrO 2 engineering ceramics was investigated by means of CO 2 and a fibre laser surface treatment. Near surface modifications in the hardness were investigated by employing the Vickers indentation method. Crack lengths and the crack geometry were then measured by using the optical microscopy. A co-ordinate measuring machine was used to investigate the diamond indentations and to measure the lengths of the cracks. Thereafter, computational and analytical methods were employed to determine the K1C. An increase in the K1C of both ceramics was found by the CO 2 and the fibre laser surface treatment in comparison to the as-received surfaces. The K1C of the CO 2 laser radiated surface of the Si 3N 4 was over 3% higher in comparison to that of the fibre laser treated surface. This was by softening of the near surface layer of the Si 3N 4 which comprised of lowering of hardness, which in turn increased the crack resistance. The effects were not similar in ZrO 2 ceramic to that of the Si 3N 4 as the fibre laser radiation in this case had produced an increase of 34% compared to that of the CO 2 laser radiation. This occurred due to propagation of lower crack resulting from the Vickers indentation test during the fibre laser surface treatment which inherently affected the end K1C through an induced compressive stress layer. The K1C modification of the two ceramics treated by the CO 2 and the fibre laser was also believed to be influenced by the different laser wavelength and its absorption co-efficient, the beam delivery system as well as the differences in the brightness of the two lasers used.

On the scaling behavior of hardness with ligament diameter of nanoporous-Au: Constrained motion of dislocations along the ligaments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Viswanath, R. N.; Polaki, S. R.; Rajaraman, R.

The scaling behavior of hardness with ligament diameter and vacancy defect concentration in nanoporous Au (np-Au) has been investigated using a combination of Vickers Hardness, Scanning electron microscopy, and positron lifetime measurements. It is shown that for np-Au, the hardness scales with the ligament diameter with an exponent of −0.3, that is, at variance with the conventional Hall-Petch exponent of −0.5 for bulk systems, as seen in the controlled experiments on cold worked Au with varying grain size. The hardness of np-Au correlates with the vacancy concentration C{sub V} within the ligaments, as estimated from positron lifetime experiments, and scalesmore » as C{sub V}{sup 1/2}, pointing to the interaction of dislocations with vacancies. The distinctive Hall-Petch exponent of −0.3 seen for np-Au, with ligament diameters in the range of 5–150 nm, is rationalized by invoking the constrained motion of dislocations along the ligaments.« less

Comparative characterization of a novel cad-cam polymer-infiltrated-ceramic-network

PubMed Central

Pascual, Agustín; Camps, Isabel; Grau-Benitez, María

2015-01-01

Background The field of dental ceramics for CAD-CAM is enriched with a new innovative material composition having a porous three-dimensional structure of feldspathic ceramic infiltrated with acrylic resins.The aim of this study is to determine the mechanical properties of Polymer-Infiltrated-Ceramic-Network (PICN) and compare its performance with other ceramics and a nano-ceramic resin available for CAD-CAM systems. Material and Methods In this study a total of five different materials for CAD-CAM were investigated. A polymer-infiltrated ceramic (Vita Enamic), a nano-ceramic resin (Lava Ultimate), a feldspathic ceramic (Mark II), a lithium disilicate ceramic (IPS-e max CAD) and finally a Leucite based ceramic (Empress - CAD). From CAD-CAM blocks, 120 bars (30 for each material cited above) were cut to measure the flexural strength with a three-point-bending test. Strain at failure, fracture stress and Weibull modulus was calculated. Vickers hardness of each material was also measured. Results IPS-EMAX presents mechanical properties significantly better from the other materials studied. Its strain at failure, flexural strength and hardness exhibited significantly higher values in comparison with the others. VITA ENAMIC and LAVA ULTIMATE stand out as the next most resistant materials. Conclusions The flexural strength, elastic modulus similar to a tooth as well as having less hardness than ceramics make PICN materials an option to consider as a restorative material. Key words:Ceramic infiltrated with resin, CAD-CAM, Weibull modulus, flexural strength, micro hardness. PMID:26535096

Evaluation of five CAD/CAM materials by microstructural characterization and mechanical tests: a comparative in vitro study.

PubMed

Sonmez, Nesrin; Gultekin, Pinar; Turp, Volkan; Akgungor, Gokhan; Sen, Deniz; Mijiritsky, Eitan

2018-01-08

Polymer infiltrated ceramics and nano-ceramic resins are the new restorative materials which have been developed in order to enhance the adverse properties of glass-matrix ceramics and resin composites. The aim of the present in vitro study was to evaluate the characteristics of various CAD/CAM materials through mechanical, microstructural, and SEM analysis. Five test groups (n = 22) were formed by using the indicated CAD/CAM blocks: VITA Enamic (VITA Zahnfabrik), Lava Ultimate (3 M ESPE), IPS e.max CAD (Ivoclar Vivadent), IPS Empress CAD (Ivoclar Vivadent), and VITA Mark II (VITA Zahnfabrik). Two specimens from each test group were used for XRD and EDS analysis. Remaining samples were divided into two subgroups (n = 10). One subgroup specimens were thermocycled (5 °C to 55 °C, 30s, 10,000 cycles) whereas the other were not. All of the specimens were evaluated in terms of flexural strength, Vickers hardness, and fracture toughness. Results were statistically analyzed using two-way ANOVA, one-way ANOVA, Tukey's HSD, and Student's t tests (α = .05). Fractured specimens were evaluated using SEM. The highest Vickers microhardness value was found for VITA Mark II (p < .001), however flexural strength and fracture toughness results were lowest conversely (p < .05). IPS e.max CAD was found to have the highest flexural strength (p < .001). Fracture toughness of IPS e.max CAD was also higher than other tested block materials (p < .001). Lava Ultimate and VITA Enamic's mechanical properties were affected negatively from thermocycling (p < .05). Microhardness, flexural strength, and fracture toughness values of Lava Ultimate and VITA Enamic were found to be similar to VITA Mark II and IPS Empress CAD groups. It should be realised that simulated aging process seem to affect ceramic-polymer composite materials more significantly than glass ceramics.

Electrical and mechanical properties of Sn-5wt.%Sb alloy with annealing temperature

NASA Astrophysics Data System (ADS)

Said Gouda, El; Ahmed, E. M.; Saad Allah, F. A.

2009-01-01

A binary Sn-5wt.%Sb solder alloy was chosen as a potential alternative to Sn-Pb solder alloy to be subjected to many studies. It was casted from the liquid state, cold drawn into wires of 1 mm diameters. The study includes the structure, electrical resistivity, tensile strength, hardness and indentation creep behavior using XRD, four probes electrical circuit, conventional tensile testing machine, Vickers microhardness tester, respectively. These properties were carried out for the cold worked alloy and after annealing at 393 and 473 K for 60 min. It was found that annealed samples exhibit more precipitations of the intermetallic compounds SnSb, higher lattice parameters and higher crystallite size, while have lower lattice-strain induced due to the cold working process. These structural changes greatly affect the electrical resistivity and mechanical properties of this alloy.

Pressure variation of developed lapping tool on surface roughness

NASA Astrophysics Data System (ADS)

Hussain, A. K.; Lee, K. Q.; Aung, L. M.; Abu, A.; Tan, L. K.; Kang, H. S.

2018-01-01

Improving the surface roughness is always one of the major concerns in the development of lapping process as high precision machining caters a great demand in manufacturing process. This paper aims to investigate the performance of a newly designed lapping tool in term of surface roughness. Polypropylene is used as the lapping tool head. The lapping tool is tested for different pressure to identify the optimum working pressure for lapping process. The theoretical surface roughness is also calculated using Vickers Hardness. The present study shows that polypropylene is able to produce good quality and smooth surface roughness. The optimum lapping pressure in the present study is found to be 45 MPa. By comparing the theoretical and experimental values, the present study shows that the newly designed lapping tool is capable to produce finer surface roughness.

Characterization of irradiated AISI 316L stainless steel disks removed from the Spallation Neutron Source

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vevera, Bradley J; Hyres, James W; McClintock, David A

2014-01-01

Irradiated AISI 316L stainless steel disks were removed from the Spallation Neutron Source (SNS) for post-irradiation examination (PIE) to assess mechanical property changes due to radiation damage and erosion of the target vessel. Topics reviewed include high-resolution photography of the disk specimens, cleaning to remove mercury (Hg) residue and surface oxides, profile mapping of cavitation pits using high frequency ultrasonic testing (UT), high-resolution surface replication, and machining of test specimens using wire electrical discharge machining (EDM), tensile testing, Rockwell Superficial hardness testing, Vickers microhardness testing, scanning electron microscopy (SEM), and energy dispersive spectroscopy (EDS). The effectiveness of the cleaning proceduremore » was evident in the pre- and post-cleaning photography and permitted accurate placement of the test specimens on the disks. Due to the limited amount of material available and the unique geometry of the disks, machine fixturing and test specimen design were critical aspects of this work. Multiple designs were considered and refined during mock-up test runs on unirradiated disks. The techniques used to successfully machine and test the various specimens will be presented along with a summary of important findings from the laboratory examinations.« less

Tribological behavior of DLC films deposited on nitrided and post-oxidized stainless steel by PACVD

NASA Astrophysics Data System (ADS)

Dalibon, E. L.; Brühl, S. P.; Heim, D.

2012-06-01

In this work, the tribological behavior and adhesion of DLC films deposited by PACVD on AISI 420 martensitic stainless steel was evaluated. Prior to DLC deposition, the samples were nitrided and some of them also post-oxidized. The films were characterized by Raman and EDS, microhardness was assessed with Vickers indenter and the microstructure was analyzed by OM, SEM, FIB. Fretting and linear reciprocating sliding tests were performed using a WC ball as counterpart, and the adhesion of the DLC films was characterized using the Scratch Test and Rockwell C indentation. Corrosion behavior was evaluated by the Salt Spray Fog Test. The film showed a hardness of only about 1500 HV but it was about 15-20 microns thick. The results of the mechanical tests showed that pre-treatments (nitriding and oxidizing) of the substrate did not have a big influence in the tribological behavior of the coating. However, the nitriding treatment before the DLC coating process reduced the interface stress and enhanced the adhesion. Additionally, all the films evidenced good corrosion resistance in a saline environment, better than the AISI 420 itself.

Properties of a proline-containing glass ionomer dental cement.

PubMed

Ansari, Sahar; Moshaverinia, Maryam; Roohpour, Nima; Chee, Winston W L; Schricker, Scott R; Moshaverinia, Alireza

2013-11-01

Proline-containing glass ionomers are promising fast-set dental restorative materials with superior mechanical properties; however, little information is available on other physical properties of this type of glass ionomer. The objectives of this study were to synthesize and characterize a polyacrylic acid terpolymer containing proline derivative (PD) and to investigate the physical properties of this glass ionomer cement (GIC) and its cytotoxicity in vitro. A terpolymer of AA (acrylic acid), IA (itaconic acid), and proline derivative (MP) with an 8:1:1 molar ratio was synthesized and characterized. Experimental GIC specimens were made from the synthetized terpolymer with Fuji IX (GC America, Alsip, Ill) commercial glass ionomer powder as recommended by the manufacturer. Specimens were mixed and fabricated at room temperature and were conditioned in distilled water at 37°C for 1 day and 1 week. Vickers hardness was determined with a microhardness tester. The water sorption characteristics and fluoride releasing properties of the specimens were investigated. The in vitro cytotoxicity of the experimental glass ionomer was assessed by evaluating the C2C12 cell metabolism with methyltetrazolium (MTT) assay. Commercial Fuji IX was used as a control for comparison. The data obtained for the experimental GIC (PD) were compared with the control group by using 1- and 2-way ANOVA and the Tukey multiple range test at α=.05. Proline-modified GIC (PD) exhibited significantly higher surface hardness values (Vickers hardness number [VHN] 58 ±6.1) in comparison to Fuji IX GIC (VHN 47 ±5.3) after 1 week of maturation. Statistical analysis of data showed that the water sorption properties of the experimental cement (PD) were significantly greater than those of the control group (P<.05). The experimental GIC showed a significant increase in the amounts of initial fluoride release (P<.05) with continued fluoride release from the bulk of the material. The experimental group showed slightly reduced cell metabolism and cell number in comparison to the control group. However, the results were not statistically different (P>.05). An amino acid-containing GIC had better surface hardness properties than commercial Fuji IX GIC. This formulation of fast-set glass ionomer showed increased water sorption without adversely affecting the amount of fluoride release. Considering its biocompatibility, this material shows promise not only as a dental restorative material but also as a bone cement with low cytotoxicity. Copyright © 2013 Editorial Council for the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Investigation of Plasma Facing Components in Plasma Focus Operation

NASA Astrophysics Data System (ADS)

Roshan, M. V.; Babazadeh, A. R.; Kiai, S. M. Sadat; Habibi, H.; Mamarzadeh, M.

2007-09-01

Both aspects of the plasma-wall interactions, counter effect of plasma and materials, have been considered in our experiments. The AEOI plasma focus, Dena, has Filippov-type electrodes. The experimental results verify that neutron production increases using tungsten as an anode insert material, compared to the copper one. The experiments show decrement of the hardness of Aluminum targets outward the sides, from 135 to 78 in Vickers scale. The sputtering yield is about 0.0065 for deuteron energy of 50 keV.

Physical and Mechanical Characterization of a Nano Carbon Infused Aluminum-Matrix Composite

DTIC Science & Technology

2011-10-01

n (EBSD) a results are s f hardness correlation Vickers ha condition, opy and Im clusions in son 6061 ma num specim s and appe , which are... extrusi perties to po inum in the ference poin wever no s view of a ha ly a carbon image in ations of am rticular hea Electron B and covetic unted...as a n the were point ased veals rbon No atter ere metallogr significan grains in having g distributi area cov grains un

Report of Research at Technische Universitaet Darmstadt on Ultrahard Materials in the B-C-N-Si System

DTIC Science & Technology

2015-06-01

structure at the micro- and nanoscale. In other words, development of nanocomposites, multilayers, and superlattices via appropriate design and control of...C-B and C-N bonds as C-C and B-N bonds. Later, the same research group , based on first-principles total-energy, and dynamic phonon calculations...Vickers hardness values.7 Another research group employed an ab initio evolutionary algorithm42 to resolve the crystal structure of the observed

Novel Synthesis of Calcium Oxide-Aluminum Oxide Glasses

NASA Astrophysics Data System (ADS)

Weber, J. K. Richard; Tangeman, Jean A.; Key, Thomas S.; Hiera, Kirsten J.; Paradis, Paul-Francois; Ishikawa, Takehiko; Yu, Jianding; Yoda, Shinichi

2002-05-01

Binary Al2O3:CaO glasses containing 36-50 mole% Al2O3 were synthesized by containerless processing of liquids in nitrogen using aerodynamic and a pressurized electrostatic-aerodynamic levitator. The critical cooling rate for glass formation RC under containerless conditions was ca. 70 K/s. The Vickers hardness of the glasses was 775-785; and the infrared transmission extended to approximately 5500 nm. The work function of the 36 mole% Al2O3 composition was 3.7 eV at 1100 K.

Titanium orthodontic brackets: structure, composition, hardness and ionic release.

PubMed

Gioka, Christiana; Bourauel, Christoph; Zinelis, Spiros; Eliades, Theodore; Silikas, Nikolaos; Eliades, George

2004-09-01

The aim of the present study was to investigate the composition, morphology, bulk structure and ionic release of two brands of titanium orthodontic brackets: Orthos2 (Ormco, USA) and Rematitan (Dentaurum, Germany). Five specimens of each group were examined with computerized X-ray microtomography, to reveal the morphology and structure of brackets, whilst resin-embedded and metallographically polished specimens were subjected to SEM/EDS analysis and Vickers microhardness measurements. Brackets were also maintained in 0.9% saline for 2 months and the ionic release in the immersion medium was determined with Inductively Coupled Plasma Atomic Emission Spectroscopy. The results of the hardness and ionic release measurements were statistically analyzed with two-way ANOVA and Tukey's test (alpha = 0.05). Orthos2 brackets consisted of two parts, the base (commercially pure Ti grade II) and the wing (Ti-6Al-4V alloy), joined together by laser welding, producing large gaps along the base-wing interface. The base was of lower hardness (Hv = 145), than the wing (Hv = 392) and incorporated a standard foil base-mesh pad. Rematitan brackets consisted of commercially pure Ti grade IV, with a single-piece manufacturing pattern of virtually identical hardness (p > 0.05) at the base and wings, featuring a laser-etched base-mesh pad. The hardness of the Rematitan brackets was significantly lower than the hardness of the Orthos2 wings, but double the hardness of the Orthos2 base. Released Ti levels were below the threshold level (1 ng/ml) of analysis for both materials, whilst traces of Al (3 ppm) and V (2 ppm) were found in the immersion media for Ti-6Al-4V alloy. The structural and hardness differences found may influence the torque transfer characteristics from activated archwires to the brackets and the crevice corrosion potential at the base-wing interface (Orthos2). The detection of Al and V in the immersion medium (Orthos2) may imply a different biological response from the two types of Ti brackets.

Mechanical Characterization of ZnSe Windows for Use With the Flow Enclosure Accommodating Novel Investigations in Combustion of Solids (FEANICS) Module

NASA Technical Reports Server (NTRS)

Salem, Jonathan A.

2006-01-01

Mechanical and physical properties of ZnSe windows to be used with the FEANICS (Flow Enclosure Accommodating Novel Investigations in Combustion of Solids) experiments were measured in order to determine design allowables. The average Young s modulus, Poisson's ratio, equibiaxial fracture strength, flaw size, grain size, Knoop hardness, Vicker s hardness, and branching constant were 74.3 +/- 0.1 GPa, 0.31, 57.8 +/- 6.5 MPa, 21 +/- 4 mm, 43 +/- 9 microns, 0.97 +/- 0.02 GPa, 0.97 +/- 0.02 GPa, and 1.0 +/- 0.1 MPa(square root of)m, respectively. The properties of current ZnSe made by chemical vapor deposition are in good agreement with those measured in the 1970 s. The hardness of CVD ZnSe windows is about one-twentieth of the sapphire window being replaced, and about one-sixth of that of window glass. Thus the ZnSe window must be handled with great care. The large grain size relative to the inherent crack size implies the need to use single crystal crack growth properties in the design process. In order to determine the local failure stresses in one of the test specimens, a solution for the stresses between the support ring and the edge of a circular plate load between concentric rings was derived

The antimicrobial potential of stevia in an in vitro microbial caries model.

PubMed

Kishta-; Derani, Maryam; Neiva, Gisele F; Boynton, James R; Kim, Youngjoo E; Fontana, Margherita

2016-04-01

To determine the effect of stevia on caries development when incorporated into a cariogenic diet in a controlled microbial caries model. 56 bovine tooth specimens (4 x 4 mm) were divided into four groups, each secured in a caries-forming vessel. All vessels were placed on an electric stirrer inside a 37°C incubator. The specimens were inoculated with Streptococcus mutans, and exposed for 4 days to circulating cycles of tryptic soy broth supplemented with 5% sucrose-TSBS (three x/day), and a mineral wash solution. Between TSBS cycles (three x/day), each group received one of four experimental solutions: phosphate buffer (PBS-negative control), 0.5% stevia solution, 5% stevia solution, or 5% xylitol solution. Development of caries lesions was analyzed using enamel surface hardness. Difference in Vickers Hardness between pre and post-treatment was calculated to determine caries development. Plaque was dislodged from six specimens per group, and the CFU/ml calculated. Data were analyzed using ANOVA at 95% confidence level, and individual group differences calculated using Tukey's test. 5% xylitol resulted in significantly less plaque at the end of the study compared to PBS and 5% stevia, but not significantly different than 0.5% stevia. 5% stevia had significantly softer lesions than the other groups, while there was no significant difference in hardness scores between 5% xylitol, 0.5% stevia and PBS.

Influence of sodium content on the properties of bioactive glasses for use in air abrasion.

PubMed

Farooq, Imran; Tylkowski, Maxi; Müller, Steffen; Janicki, Tomasz; Brauer, Delia S; Hill, Robert G

2013-12-01

Air abrasion is used in minimally invasive dentistry for preparing cavities, while removing no or little sound dentine or enamel, and the use of bioactive glass (rather than alumina) as an abrasive could aid in tooth remineralization. Melt-derived bioactive glasses (SiO2-P2O5-CaO-CaF2-Na2O) with low sodium content (0 to 10 mol% Na2O in exchange for CaO) for increased hardness, high phosphate content for high bioactivity and fluoride content for release of fluoride and formation of fluorapatite were produced, and particles between 38 and 80 µm in size were used for cutting soda-lime silicate glass microscope slides and human enamel. Vickers hardness increased with decreasing Na2O content, owing to a more compact silicate network in low sodium content glasses, resulting in shorter cutting times. Cutting times using bioactive glass were significantly longer than using the alumina control (29 µm) when tested on microscope slides; however, glasses showed more comparable results when cutting human enamel. The bioactive glasses formed apatite in Tris buffer within 6 h, which was significantly faster than Bioglass® 45S5 (24 h), suggesting that the hardness of the glasses makes them suitable for air abrasion application, while their high bioactivity and fluoride content make them of interest for tooth remineralization.

Neutron energy spectrum influence on irradiation hardening and microstructural development of tungsten

DOE PAGES

Fukuda, Makoto; Kiran Kumar, N. A. P.; Koyanagi, Takaaki; ...

2016-07-02

We performed a neutron irradiation to single crystal pure tungsten in the mixed spectrum High Flux Isotope Reactor (HFIR). In order to investigate the influences of neutron energy spectrum, the microstructure and irradiation hardening were compared with previous data obtained from the irradiation campaigns in the mixed spectrum Japan Material Testing Reactor (JMTR) and the sodium-cooled fast reactor Joyo. The irradiation temperatures were in the range of ~90–~800 °C and fast neutron fluences were 0.02–9.00 × 10 25 n/m 2 (E > 0.1 MeV). Post irradiation evaluation included Vickers hardness measurements and transmission electron microscopy. Moreover, the hardness and microstructuremore » changes exhibited a clear dependence on the neutron energy spectrum. The hardness appeared to increase with increasing thermal neutron flux when fast fluence exceeds 1 × 10 25 n/m 2 (E > 0.1 MeV). Finally, irradiation induced precipitates considered to be χ- and σ-phases were observed in samples irradiated to >1 × 10 25 n/m 2 (E > 0.1 MeV), which were pronounced at high dose and due to the very high thermal neutron flux of HFIR. Although the irradiation hardening mainly caused by defects clusters in a low dose regime, the transmutation-induced precipitation appeared to impose additional significant hardening of the tungsten.« less

Neutron energy spectrum influence on irradiation hardening and microstructural development of tungsten

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fukuda, Makoto; Kiran Kumar, N. A. P.; Koyanagi, Takaaki

We performed a neutron irradiation to single crystal pure tungsten in the mixed spectrum High Flux Isotope Reactor (HFIR). In order to investigate the influences of neutron energy spectrum, the microstructure and irradiation hardening were compared with previous data obtained from the irradiation campaigns in the mixed spectrum Japan Material Testing Reactor (JMTR) and the sodium-cooled fast reactor Joyo. The irradiation temperatures were in the range of ~90–~800 °C and fast neutron fluences were 0.02–9.00 × 10 25 n/m 2 (E > 0.1 MeV). Post irradiation evaluation included Vickers hardness measurements and transmission electron microscopy. Moreover, the hardness and microstructuremore » changes exhibited a clear dependence on the neutron energy spectrum. The hardness appeared to increase with increasing thermal neutron flux when fast fluence exceeds 1 × 10 25 n/m 2 (E > 0.1 MeV). Finally, irradiation induced precipitates considered to be χ- and σ-phases were observed in samples irradiated to >1 × 10 25 n/m 2 (E > 0.1 MeV), which were pronounced at high dose and due to the very high thermal neutron flux of HFIR. Although the irradiation hardening mainly caused by defects clusters in a low dose regime, the transmutation-induced precipitation appeared to impose additional significant hardening of the tungsten.« less

Growth, spectral, thermal, laser damage threshold, microhardness, dielectric, linear and nonlinear optical properties of an organic single crystal: L-phenylalanine DL-mandelic acid

NASA Astrophysics Data System (ADS)

Jayaprakash, P.; Peer Mohamed, M.; Krishnan, P.; Nageshwari, M.; Mani, G.; Lydia Caroline, M.

2016-12-01

Single crystals of L-phenylalanine dl-mandelic acid [C9H11NO2. C8H8O3], have been grown by the slow evaporation technique at room temperature using aqueous solution. The single crystal XRD study confirms monoclinic system for the grown crystal. The functional groups present in the grown crystal have been identified by FTIR and FT-Raman analyses. The optical absorption studies show that the crystal is transparent in the visible region with a lower cut-off wavelength of 257 nm and the optical band gap energy Eg is determined to be 4.62 eV. The Kurtz powder second harmonic generation was confirmed using Nd:YAG laser with fundamental wavelength of 1064 nm. Further, the thermal studies confirmed no weight loss up to 150°C for the as-grown crystal. The photoluminescence spectrum exhibited three peaks (414 nm, 519 nm, 568 nm) due to the donation of protons from carboxylic acid to amino group. Laser damage threshold value was found to be 4.98 GW/cm2. The Vickers microhardness test was carried out on the grown crystals and there by Vickers hardness number (Hv), work hardening coefficient (n), yield strength (σy), stiffness constant C11 were evaluated. The dielectric behavior of the crystal has been determined in the frequency range 50 Hz-5 MHz at various temperatures.

Tribological and mechanical performance evaluation of metal prosthesis components manufactured via metal injection molding.

PubMed

Melli, Virginia; Juszczyk, Mateusz; Sandrini, Enrico; Bolelli, Giovanni; Bonferroni, Benedetta; Lusvarghi, Luca; Cigada, Alberto; Manfredini, Tiziano; De Nardo, Luigi

2015-01-01

The increasing number of total joint replacements, in particular for the knee joint, has a growing impact on the healthcare system costs. New cost-saving manufacturing technologies are being explored nowadays. Metal injection molding (MIM) has already demonstrated its suitability for the production of CoCrMo alloy tibial trays, with a significant reduction in production costs, by holding both corrosion resistance and biocompatibility. In this work, mechanical and tribological properties were evaluated on tibial trays obtained via MIM and conventional investment casting. Surface hardness and wear properties were evaluated through Vickers hardness, scratch and pin on disk tests. The MIM and cast finished tibial trays were then subjected to a fatigue test campaign in order to obtain their fatigue load limit at 5 millions cycles following ISO 14879-1 directions. CoCrMo cast alloy exhibited 514 HV hardness compared to 335 HV of MIM alloy, furthermore it developed narrower scratches with a higher tendency towards microploughing than microcutting, in comparison to MIM CoCrMo. The observed fatigue limits were (1,766 ± 52) N for cast tibial trays and (1,625 ± 44) N for MIM ones. Fracture morphologies pointed out to a more brittle behavior of MIM microstructure. These aspects were attributed to the absence of a fine toughening and surface hardening carbide dispersion in MIM grains. Nevertheless, MIM tibial trays exhibited a fatigue limit far beyond the 900 N of maximum load prescribed by ISO and ASTM standards for the clinical application of these devices.

Effect of Manufacturing Process on the Biocompatibility and Mechanical Properties of Ti-30Ta Alloy

NASA Astrophysics Data System (ADS)

Gill, P.; Munroe, N.; Pulletikurthi, C.; Pandya, S.; Haider, W.

2011-07-01

Ti alloys have been widely used in the aerospace, chemical, and biomedical industries for their high strength/weight ratio and corrosion resistance. However, Nitinol's usage in the latter industry has been fraught with concerns of allergic and toxic effects of Ni released from implants. Recently, much attention has been placed on the development of Ni-free Ti-Ta alloys, which are considered prime candidates for applications such as metal-on-metal spinal disk replacements, orthopedic implants, cardiovascular stents, dental posts, and guide wires. In this research, the biocompatibility of Ti-30Ta alloys manufactured by powder metallurgy (PM) and arc melting (ARC) were investigated. The corrosion resistance of each alloy was determined in accordance with ASTM F 2129-08 in phosphate buffered saline (PBS) and PBS with amino acids at 37 °C. The concentration of metal ions released during corrosion was measured by Inductively Coupled Plasma Mass Spectroscopy (ICP-MS). Scanning Electron Microscopy (SEM) was used to assess the morphology of the alloys before and after corrosion. Vicker's hardness tests were performed to compare the hardness and tensile strength of the alloys. Human osteoblast cells were successfully grown on the surface of both alloys.

Effect of pulsed laser parameters on in-situ TiC synthesis in laser surface treatment

NASA Astrophysics Data System (ADS)

Hamedi, M. J.; Torkamany, M. J.; Sabbaghzadeh, J.

2011-04-01

Commercial titanium sheets pre-coated with 300-μm thick graphite layer were treated by employing a pulsed Nd:YAG laser in order to enhance surface properties such as wear and erosion resistance. Laser in-situ alloying method produced a composite layer by melting the titanium substrate and dissolution of graphite in the melt pool. Correlations between pulsed laser parameters, microstructure and microhardness of the synthesized composite coatings were investigated. Effects of pulse duration and overlapping factor on the microstructure and hardness of the alloyed layer were deduced from Vickers micro-indentation tests, XRD, SEM and metallographic analyses of cross sections of the generated layer. Results show that the composite cladding layer was constituted with TiC intermetallic phase between the titanium matrix in particle and dendrite forms. The dendritic morphology of composite layer was changed to cellular grain structure by increasing laser pulse duration and irradiated energy. High values of the measured hardness indicate that deposited titanium carbide increases in the conditions with more pulse duration and low process speed. This occurs due to more dissolution of carbon into liquid Ti by heat input increasing and positive influence of the Marangoni flow in the melted zone.

[The influence of polymerization time on physicochemical properties of the acrylic resin Vertex RS].

PubMed

Fraczak, Bogumiła; Sobolewska, Ewa; Ey-Chmielewska, Halina; Skowronek, Maria; Błazewicz, Stanisław

2009-01-01

A good denture can only be produced through proper actions during the clinical and laboratory stages of the production process. The aim of this study was to determine if a change in polymerization time affects the physicochemical properties of polymethacrylate material used for dentures. We examined the acrylic resin Vertex R.S. polymerized for 15, 25, 40, or 60 minutes. Palapress Vario was taken as reference material. Static bending, microhardness, surface wettability, and susceptibility to abrasion were determined. The microhardness test showed that most of the samples had similar Vickers hardness (VS) values, except for the sample polymerized for 25 min. which demonstrated a significantly higher value. Grindability was affected by a change in polymerization time. Mass loss was greatest for samples polymerized for 15, 25, and 60 min. and smallest for Vertex 40 and Palapress Vario. We also observed differences in the wetting angle. Vertex 40 and 60 had a relatively low wetting angle signifying that longer polymerization time results in lower hydrophobicity of the material. The present study has demonstrated that polymerization time has a significant effect on the hardness and some mechanical properties of the acrylic resin.

An electron back-scattered diffraction study on the microstructure evolution of severely deformed aluminum AI6061 alloy

NASA Astrophysics Data System (ADS)

Vaseghi, M.; Karimi Taheri, A.; Kim, H. S.

2014-08-01

In this paper dynamic strain ageing behavior in an Al-Mg-Si alloy related to equal channel angular pressing (ECAP) was investigated. In order to examine the combined plastic deformation and ageing effects on microstructure evolutions and strengthening characteristics, the Al6061 alloy were subjected to phi=90° ECAP die for up to 4 passes via route Bc at high temperatures. For investigating the effects of ageing temperature and strain rate in ECAP, Vickers hardness tests were performed. The combination of the ECAP process with dynamic ageing at higher temperatures resulted in a significant increase in hardness. The microstructural evolution of the samples was studied using electron back-scattering diffraction (EBSD). The grains of Al6061 aluminum alloy were refined significantly at 100 and 150 °C with greater pass numbers and the distributions of grain size tended to be more uniform with pass number increasing. Frequency of sub-boundaries and low angle grain boundaries (LAGBs) increased at initial stage of deformation, and sub-boundaries and LAGBs evolved into highangle grain boundaries (HAGBs) with further deformation, which resulted in the high frequency of HAGBs in the alloy after ECAP 4 passes.

Properties of boride-added powder metallurgy magnesium alloys

NASA Astrophysics Data System (ADS)

Tanaka, Atsushi; Yoshimura, Syota; Fujima, Takuya; Takagi, Ken-ichi

2009-06-01

Magnesium alloys with metallic borides, magnesium diboride (MgB2) or aluminum diboride (AlB2), were investigated regarding their mechanical properties, transverse rupture strength (TRS) and micro Vickers hardness (HV). The alloys were made from pure Mg, Al and B powders by mechanical alloying and hot pressing to have boride content of between 2.0 and 20 vol%. The alloy with AlB2 exhibited an obvious improvement of HV around a boride content of 6 vol% though the other alloy, with MgB2, did not. TRS showed moderate maxima around the same boride content region for the both alloys. X-ray diffraction measurements indicated an intermetallic compound, Mg17Al12, formed in the alloy with AlB2, which was consistent with its higher hardness.

Effect of heat treatment on corrosion behavior of duplex stainless steel in orthodontic applications

NASA Astrophysics Data System (ADS)

Sabea Hammood, Ali; Faraj Noor, Ahmed; Talib Alkhafagy, Mohammed

2017-12-01

Heat treatment is necessary for duplex stainless steel (DSS) to remove or dissolve intermetallic phases, to remove segregation and to relieve any residual thermal stress in DSS, which may be formed during production processes. In the present study, the corrosion resistance of a DSS in artificial saliva was studied by potentiodynamic measurements. The microstructure was investigated by scanning electron microscopy (SEM),x-ray diffraction (XRD) and Vickers hardness (HV). The properties were tested in as-received and in thermally treated conditions (800-900 °C, 2-8 min). The research aims to evaluate the capability of DSS for orthodontic applications, in order to substitute the austenitic grades. The results indicate that the corrosion resistance is mainly affected by the ferrite/austenite ratio. The best result was obtained with a treatment at 900 °C for 2 min.

Microstructure of directionally solidified Ti-Fe eutectic alloy with low interstitial and high mechanical strength

NASA Astrophysics Data System (ADS)

Contieri, R. J.; Lopes, E. S. N.; Taquire de La Cruz, M.; Costa, A. M.; Afonso, C. R. M.; Caram, R.

2011-10-01

The performance of Ti alloys can be considerably enhanced by combining Ti and other elements, causing an eutectic transformation and thereby producing composites in situ from the liquid phase. This paper reports on the processing and characterization of a directionally solidified Ti-Fe eutectic alloy. Directional solidification at different growth rates was carried out in a setup that employs a water-cooled copper crucible combined with a voltaic electric arc moving through the sample. The results obtained show that a regular fiber-like eutectic structure was produced and the interphase spacing was found to be a function of the growth rate. Mechanical properties were measured using compression, microindentation and nanoindentation tests to determine the Vickers hardness, compressive strength and elastic modulus. Directionally solidified eutectic samples presented high values of compressive strength in the range of 1844-3000 MPa and ductility between 21.6 and 25.2%.

Characterization of Hydrogen Embrittled Zircaloy-4 by Using a Van de Graaff Particle Accelerator

NASA Astrophysics Data System (ADS)

Budd, John

2013-04-01

On-site, dry cask storage was originally by the intended to be a short-term solution for holding spent nuclear fuel. Due to the lack of a permanent storage facility, the nuclear power industry seeks to assess the effective lifetime of the casks. One issue which could compromise cask integrity is Hydrogen embrittlement. This phenomenon occurs in the Zircaloy-4 fuel-rod cladding and is caused by the formation of Zirconium hydrides. Over time, thermal stresses caused by the heat from reactions of the stored nuclear fuel could result in significant breaches of the cladding. Our group at Texas A&M University- Kingsville is conducting experiments to aid in determining when such breaches will occur. We will irradiate samples of the alloy with protons of energies up to 400 keV using a Van de Graaff particle accelerator. Once irradiated, their properties will be characterized using scanning electron microscopy and Vickers hardness tests.

Material testing of reconditioned orthodontic brackets.

PubMed

Reimann, S; Rewari, A; Keilig, L; Widu, F; Jäger, A; Bourauel, C

2012-12-01

While all manufacturers of orthodontic brackets label these products for single use, there are commercial providers offering bracket reconditioning (or "recycling"). We conducted this study to investigate the effects of different recycling techniques on material-related parameters in orthodontic brackets, aiming to derive indications for clinical use and conclusions about the biocompatibility, longevity, and application of recycled brackets. New metal brackets (equilibrium(®); Dentaurum, Ispringen, Germany) were compared to brackets recycled by different techniques, including direct flaming with a Bunsen burner, chemical reconditioning in an acid bath, a commercial unit (Big Jane; Esmadent, IL, USA), and outsourcing to a company (Ortho Clean, Dellstedt, Germany). Material-related examinations included the following: (1) corrosion behavior by static immersion testing and use of a mass spectrometer to determine nickel-ion concentrations in the corrosive medium, (2) surface features in scanning electron micrographs before and after corrosion testing, (3) Vickers hardness using a hardness testing machine, (4) shear bond strength as defined in DIN 13990-1, (5) dimensional stability of the bracket slots by light microscopy, and (6) frictional loss as assessed by an orthodontic measurement and simulation system (OMSS). Each examination was performed on ten brackets. Student's t-test was used for statistical analysis. Compared to the new brackets, those recycled in an acid bath or by a commercial provider revealed significant dimensional changes (p<0.05). Corrosion on the recycled brackets varied according to the recycling techniques employed. The group of brackets recycled by one company revealed hardness values that differed from those of all the other groups. No significant differences were observed in nickel-ion release, frictional loss, and shear bond strength. Recycling was found to significantly reduce the corrosion resistance and dimensional stability of orthodontic brackets. As the savings generated by recycling do not justify the risks involved, the practice of labeling orthodontic brackets for single use remains a responsible precaution that safeguards patients and orthodontists against definite risks.

Microstructural Modification of Sn-0.7Cu Solder Alloys by Fe/Bi-Addition for Achieving High Mechanical Performance

NASA Astrophysics Data System (ADS)

Ali, Bakhtiar; Sabri, Mohd Faizul Mohd; Said, Suhana Mohd; Mahdavifard, Mohammad Hossein; Sukiman, Nazatul Liana; Jauhari, Iswadi

2017-08-01

In this work, we studied the Fe/Bi-bearing tin-copper (Sn-0.7Cu) solders for their microstructural and mechanical properties. The microstructure was studied using field emission scanning electron microscopy (FESEM) with a backscattered electron (BSE) detector, x-ray diffraction (XRD) analysis, and energy-dispersive x-ray spectroscopy (EDX). The microstructure study showed that Fe forms very few FeSn2 intermetallic compounds (IMCs) and does not significantly alter the microstructure of Sn-0.7Cu, whereas Bi controls the size of inter-dendritic regions containing Cu6Sn5 and Ag3Sn IMCs of the alloy, as well as significantly refines its primary β-Sn dendrites. Moreover, Bi atoms dissolve in β-Sn matrix, which in turn strengthen the solder by the Bi solid solution strengthening mechanism. Such microstructural modification leads to significant improvements in various mechanical properties of the alloy, including shear strength, impact toughness, and hardness values. Shear tests were performed with a 0.25 mm/min shear speed. The results showed that shear strength improves from 16.57 MPa to 38.36 MPa with the addition of Fe/Bi to Sn-0.7Cu, raising by about 130%. The energy absorbed during impact tests was measured for samples with the help of a Charpy impact testing machine with a 5.4 m/s impact speed. The results revealed that the addition of Fe/Bi to Sn-0.7Cu improves its impact absorbed energy by over 35%, increasing it from 7.5 J to 10.3 J. Vickers hardness tests were carried out for the test samples with a 245.2 mN applied load and 10 s dwell time. The results showed that the hardness number improves from 9.89 to 24.13 with Fe/Bi to Sn-0.7Cu, increasing by about 140%.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Miao; Du, Yonghui; Gao, Lili

A recent experimental study reported the successful synthesis of an orthorhombic FeB{sub 4} with a high hardness of 62(5) GPa [H. Gou et al., Phys. Rev. Lett. 111, 157002 (2013)], which has reignited extensive interests on whether transition-metal borides compounds will become superhard materials. However, it is contradicted with some theoretical studies suggesting transition-metal boron compounds are unlikely to become superhard materials. Here, we examined structural and electronic properties of FeB{sub 4} using density functional theory. The electronic calculations show the good metallicity and covalent Fe–B bonding. Meanwhile, we extensively investigated stress-strain relations of FeB{sub 4} under various tensile andmore » shear loading directions. The calculated weakest tensile and shear stresses are 40 GPa and 25 GPa, respectively. Further simulations (e.g., electron localization function and bond length along the weakest loading direction) on FeB{sub 4} show the weak Fe–B bonding is responsible for this low hardness. Moreover, these results are consistent with the value of Vickers hardness (11.7–32.3 GPa) by employing different empirical hardness models and below the superhardness threshold of 40 GPa. Our current results suggest FeB{sub 4} is a hard material and unlikely to become superhard (>40 GPa)« less

Bcl-2 expression is essential for development and normal physiological properties of tooth hard tissue and saliva production.

PubMed

Saghiri, Mohammad Ali; Asatourian, Armen; Gurel, Zafer; Sorenson, Christine M; Sheibani, Nader

2017-09-15

Apoptosis plays a fundamental role in appropriate tissue development and function. Although expression of Bcl-2 has been reported during tooth and submandibular gland (SMG) development, the physiological role Bcl-2 plays during these processes has not been addressed. This study was performed to evaluate the impact of Bcl-2 expression on the formation and properties of tooth hard tissue, and saliva production. Twenty-four mice (12 males and 12 females) were divided into three groups of eight (n=8): group A (Bcl-2 +/+), group B (Bcl-2 +/-), and group C (Bcl-2 -/-) and subjected to micro-CT analyses. The mineral content of first molars was analyzed by X-Ray diffraction (XRD) and scanning electron microscopy (SEM) color dot map. The surface microhardness was determined by Vickers test on labial surfaces of incisors. Saliva was collected from different groups of mice after subcutaneous injection of pilocarpine. Samples from Bcl-2 -/- mice showed significantly smaller micro-CT values, lower and poor crystallinity of hydroxyapatite (HA), and lowest surface micro hardness. SMG from Bcl-2 -/- mice showed remarkable reduction in size, consistent with reduced saliva accumulation. The absence of Bcl-2 expression in SMG did not affect the expression of other Bcl-2 family members. Thus, Bcl-2 expression influence on the formation and properties of tooth hard tissue, and saliva accumulation. Bcl-2 expression has a significant impact on the mineralogical content of enamel crystals of tooth structure. Lack of Bcl-2 expression led to impaired production of enamel ACP crystals. Copyright © 2017 Elsevier Inc. All rights reserved.

Mechanical Properties and Wear Characteristics Al-ZrO2-SiCp and Graphite Hybrid Metal Matrix Composites

NASA Astrophysics Data System (ADS)

Nayak, S. K.; Mahanta, T.; Sahoo, J. K.; Mishra, A.

2018-03-01

Development of Aluminum Metal Matrix Co mposites (AMMCs) has been one of the major requirements in engineering applicat ions due to their excellent mechanical properties, light weight and high strength. In the present investigation, Stir casting technique has been used for fabrication of co mposites, taking Alu miniu m as parent metal, Silicon Carbide (SiCp) of 7 vol. % of 220 mesh size and 1.75 vol. % of graphite as reinforcements. The Zirconia content was varied as 2.75, 4.5 and 6 vol. % to fabricate three d ifferent types of hybrid composites. The tensile strength and hardness were measured in UTM and Vickers hardness tester respectively and the wear characteristics were studied in a pin on disc friction monitor under dry sliding condition against steel counter face. The tensile strength was found to be 90 MPa, 120 MPa, 130 MPa and hardness 80.25 VHN, 103.22 VHN, 103.77 VHN for 2.75, 4.5 and 6vol. % of Zirconia respectively. Fro m the above investigation, it is recommended that composition with Al, 7 %-SiCp, 1.75 % -Gr and 6 vol %-ZrO2 showed better mechanical p roperties i.e . h igh tensile strength (130MPa) and reasonably good hardness (103.77 VHN) . The co mposite with Al, 7 % - SiCp, 1.75 % -Gr and 6 %-ZrO2 is good for short run frictional applicat ion and the composite with Al, 7 %- SiCp, 1.75 % -Gr and 4.5 %- ZrO2 may be used for long run frictional applicat ions after testing.

Effect of powder reactivity on fabrication and properties of NiAl/Al2O3 composite coated on cast iron using spark plasma sintering

NASA Astrophysics Data System (ADS)

Beyhaghi, Maryam; Kiani-Rashid, Ali-Reza; Kashefi, Mehrdad; Khaki, Jalil Vahdati; Jonsson, Stefan

2015-07-01

Powder mixtures of Ni, NiO and Al are ball milled for 1 and 10 h. X-ray diffractometry and differential thermal analysis show that while ball milling for 1 h produced mechanically activated powder; 10 h ball milling produced NiAl and Al2O3 phases. Dense NiAl/Al2O3 composite coatings are formed on gray cast iron substrate by spark plasma sintering (SPS) technique. The effect of powder reactivity on microstructure, hardness and scratch hardness of NiAl/Al2O3 coatings after SPS is discussed. Results show that in the coating sample made of mechanically activated powder in situ synthesis of NiAl/Al2O3 composite coating is fulfilled and a thicker well-formed diffusion bond layer at the interface between coating and substrate is observed. The diffusion of elements across the bond layers and phase evolution in the bond layers were investigated. No pores or cracks were observed at the interface between coating layer and substrate in any of samples. Higher Vickers hardness and scratch hardness values in coating made of 10 h ball milled powder than in coating fabricated from 1 h ball milled powder are attributed to better dispersion of Al2O3 reinforcement particles in NiAl matrix and nano-crystalline structure of NiAl matrix. Scratched surface of coatings did not reveal any cracking or spallation at coating-substrate interface indicating their good adherence at test conditions.

Effect of Cryogenic Treatment on Microstructure and Mechanical Properties of 0Cr12Mn5Ni4Mo3Al Steel

NASA Astrophysics Data System (ADS)

Bai, Xue; Zheng, Linbin; Cui, Jinyan; Wu, Sujun; Song, Ruokang; Xie, Di; Wang, Dawei; Li, Haisheng

2017-10-01

This paper systematically investigated the effect of cryogenic temperature and soaking time on the 0Cr12Mn5Ni4Mo3Al steel. Microstructure observation and mechanical tests were performed on the specimens by scanning electron microscopy, x-ray diffraction, Vickers hardness tests and tensile tests. Cryogenic treatments were carried out at different temperatures of -73, -120, -160 and -196 °C for a given soaking time of 4 h and at a specific temperature of -73 °C for different soaking time of 8, 12, 21 and 32 h, followed by the subsequent tempering treatment. The results showed that the volume fraction of martensite in this steel has significantly increased and the size of martensite lath has decreased after cryogenic treatment, which leads to the improvement of the mechanical properties of the steel. The cryogenic treatment affected the microstructure by promoting the transformation of retained austenite to martensite and the formation of reversed austenite in the steel. The optimal hardness and strength of this steel were obtained by cryogenic treatment at -73 °C for 8 h. It has been found that the soaking time is a critical parameter for the mechanical properties of 0Cr12Mn5Ni4Mo3Al steel. When the cryogenic temperature is lower than -73 °C, there is no further improvement of the mechanical properties.

Finite element analysis of stresses in Berkovich, Vickers and Knoop indentation for densifying and non-densifying glasses

NASA Astrophysics Data System (ADS)

Chen, Kanghua

2002-08-01

A constitutive law for fused silica accounting for its permanent densification under large compressive stresses is presented. The implementation of the constitutive equations in the general-purpose finite element code ABAQUS via user subroutine is proposed and carefully verified. The three-dimensional indentation mechanics under Berkovich, Vickers and Knoop indenters is extensively investigated based on the proposed constitutive relation. The results of stress distribution and plastic zone for both densifying and non-densifying optical glasses are systematically compared. These numerical results are in good agreement with the experimental observations of optical manufacturing. That is, fused silica shows lower material removal rate, smaller surface roughness and subsurface damage in contrast to non-densifying optical glasses under the same grinding condition. Material densification of fused silica is thoroughly studied through numerical simulations of indentation mechanics. The exact amount of densification and shear strain of fused silica under Berkovich indentation is calculated to show the deformation mechanism of glass materials under three-dimensional indentations. The surface profiles show the material "pile-up" around the indenter tip for non-densifying glasses and "sink-in" for fused silica after the indentation load is removed. An important inverse problem is studied: estimation of abrasive size and indentation load through the examination of residual indentation footprints. A series of 2D axisymmetric spherical indentation simulations generate a wide range of relationships among the indentation load, indenter size, residual indentation depth and size of residual indentation zone for the five selected brittle materials: glass fused silica (FS), BK7, semiconductor Si, laser glass LHG8, and optical crystal CaF2.. The application of the inverse problem is verified by the good agreement between the estimated abrasive size and the actual abrasive size found during a material removal experiment of magnetorheological finishing (MRF) of fused silica. The explanation of indentation size effect (ISE) is attempted using numerical indentation simulations. Vickers indentation simulations on the five selected brittle materials (FS, BK7, Si, LHG8 and CaF2.) show no size dependence of Vickers hardness when the material is modeled as elastic-perfectly plastic (with or without densification). The simulation results on axisymmetric conical indentation also indicate that the bluntness of the indenter tip is not the reason for the indentation size effect. A new constitutive model accounting for the material length scale is needed in order to explain the well-observed indentation size effect during indentation tests.

Assessment of elemental composition, microstructure, and hardness of stainless steel endodontic files and reamers.

PubMed

Darabara, Myrsini; Bourithis, Lefteris; Zinelis, Spiros; Papadimitriou, George D

2004-07-01

The purpose of this study was to determine the elemental composition, microstructure, and hardness of commercially available reamers, K files, and H files. Five instruments of each type from different manufacturers (Antaeos, FKG, Maillefer, Mani, and Micromega) were embedded in epoxy resin along their longitudinal axis. After metallographic grinding and polishing, the specimens were chemically etched and their microstructure investigated under an incident light microscope. The specimens were studied under a scanning electron microscope, and their elemental compositions were determined by energy dispersive X-ray microanalysis. The same surfaces were repolished and X-ray diffraction was performed. The same specimen surface was used for the assessment of the Vickers hardness (HV200) by using a microhardness tester with a 200-g load and 20-s contact time. The hardness results were statistically analyzed with two-way ANOVA and Tukey's test (a = 0.05). All files demonstrated extensively elongated grains parallel to longitudinal file axis because of cold drawing. The elemental composition of Maillefer and Mani reamers, Antaeos K files, and Mani H files were found in the range of AISI 303 SS, whereas all the rest were determined as AISI 304 SS. Two different phases (austenite SSt and martensite SSt) were identified with X-ray diffraction for all files tested. The results of hardness classified reamers in the following decreasing order (HMV200): Micromega = 673 +/- 29, Mani = 662 +/- 24, Maillefer = 601 +/- 34, Antaeos = 586 +/- 18, FKG = 557 +/- 19, and the K files (HV200): FKG = 673 +/- 16, Mani = 647 +/- 19, Maillefer = 603 +/- 41, Antaeos = 566 +/- 21, Micromega = 555 +/- 15, and the H files (HMV200): Mani = 640 +/- 12, FKG = 583 +/- 31, Maillefer = 581 +/- 5, Antaeos = 573 +/- 3, Micromega = 546 +/- 14. Although only two stainless steel alloys were used for the production of endodontic files, the differences in hardness are independent to the alloys used, implying that other factors, such as the production method or the thermomechanical history of the alloys, play an important role on the mechanical properties of endodontic files.

The variation in surface morphology and hardness of human deciduous teeth samples after laser irradiation

NASA Astrophysics Data System (ADS)

Khalid, Arooj; Bashir, Shazia; Akram, Mahreen; Salman Ahmed, Qazi

2017-11-01

The variation in surface morphology and hardness of human deciduous teeth samples has been investigated after laser irradiation at different wavelengths and energies. Nd:YAG was employed as a source of irradiation for IR (1064 nm) and visible (532 nm) radiation, whereas an excimer laser was used as the source of UV (248 nm) radiation. Scanning electron microscope (SEM) analysis was carried out to reveal the surface morphological evolution of teeth samples. Vickers microhardness tester was employed to investigate the modifications in the hardness of the laser-treated samples. It is observed from SEM analysis that IR wavelength is responsible for ablation of collagen matrix and intertubular dentine. For visible radiation, the ablation of collagen along with hydroxypatite is observed. With UV radiation, the ablation of peritubular dentine is dominant and is responsible for the sealing of tubules. The decrease in hardness at lower energy for both wavelengths is due to the evaporation of carbon content. With increasing energy, evaporation of water along with carbon content, and resolidification and re-organization of inorganic content causes the increase in hardness of the treated dentine. SEM as well as microhardness analyses reveal that laser wavelengths and energy of laser radiation significantly influence the surface morphology and hardness of samples.

Manganese mono-boride, an inexpensive room temperature ferromagnetic hard material

PubMed Central

Ma, Shuailing; Bao, Kuo; Tao, Qiang; Zhu, Pinwen; Ma, Teng; Liu, Bo; Liu, Yazhou; Cui, Tian

2017-01-01

We synthesized orthorhombic FeB-type MnB (space group: Pnma) with high pressure and high temperature method. MnB is a promising soft magnetic material, which is ferromagnetic with Curie temperature as high as 546.3 K, and high magnetization value up to 155.5 emu/g, and comparatively low coercive field. The strong room temperature ferromagnetic properties stem from the positive exchange-correlation between manganese atoms and the large number of unpaired Mn 3d electrons. The asymptotic Vickers hardness (AVH) is 15.7 GPa which is far higher than that of traditional ferromagnetic materials. The high hardness is ascribed to the zigzag boron chains running through manganese lattice, as unraveled by X-ray photoelectron spectroscopy result and first principle calculations. This exploration opens a new class of materials with the integration of superior mechanical properties, lower cost, electrical conductivity, and fantastic soft magnetic properties which will be significant for scientific research and industrial application as advanced structural and functional materials. PMID:28262805

Comparative study on microstructure and martensitic transformation of aged Ni-rich NiTi and NiTiCo shape memory alloys

NASA Astrophysics Data System (ADS)

El-Bagoury, Nader

2016-05-01

In this article the influence of aging heat treatment conditions of 250, 350, 450 and 550 °C for 3 h on the microstructure, martensitic transformation temperatures and mechanical properties of Ni51Ti49Co0 and Ni47 Ti49Co4 shape memory alloys was investigated. This comparative study was carried out using X-ray diffraction analysis, scanning electron microscope, energy dispersive spectrometer, differential scanning calorimeter and Vickers hardness tester. The results show that the microstructure of both aged alloys contains martensite phase and Ti2Ni in addition to some other precipitates. The martensitic transformation temperature was increased steadily by increasing the ageing temperature and lowering the value of valence electron number (ev/a) and concentration. Moreover, the hardness measurements were gradually increased at first by increasing the aging temperature from 250 to 350 °C. Further elevating in aging temperature to 450 and 550 °C decreases the hardness value.

Phase formation in selected surface-roughened plasma-nitrided 304 austenite stainless steel.

PubMed

Singh, Gajendra Prasad; Joseph, Alphonsa; Raole, Prakash Manohar; Barhai, Prema Kanta; Mukherjee, Subroto

2008-04-01

Direct current (DC) glow discharge plasma nitriding was carried out on three selected surface-roughened AISI 304 stainless steel samples at 833 K under 4 mbar pressures for 24 h in the presence of N 2 :H 2 gas mixtures of 50 : 50 ratios. After plasma nitriding, the phase formation, case depth, surface roughness, and microhardness of a plasma-nitrided layer were evaluated by glancing angle x-ray diffractogram, optical microscope, stylus profilometer, and Vickers microhardness tester techniques. The case depth, surface hardness, and phase formation variations were observed with a variation in initial surface roughness. The diffraction patterns of the plasma-nitrided samples showed the modified intensities of the α and γ phases along with those of the CrN, Fe 4 N, and Fe 3 N phases. Hardness and case depth variations were observed with a variation in surface roughness. A maximum hardness of 1058 Hv and a case depth of 95 μm were achieved in least surface-roughened samples.

Machinable glass-ceramics forming as a restorative dental material.

PubMed

Chaysuwan, Duangrudee; Sirinukunwattana, Krongkarn; Kanchanatawewat, Kanchana; Heness, Greg; Yamashita, Kimihiro

2011-01-01

MgO, SiO(2), Al(2)O(3), MgF(2), CaF(2), CaCO(3), SrCO(3), and P(2)O(5) were used to prepare glass-ceramics for restorative dental materials. Thermal properties, phases, microstructures and hardness were characterized by DTA, XRD, SEM and Vickers microhardness. Three-point bending strength and fracture toughness were applied by UTM according to ISO 6872: 1997(E). XRD showed that the glass crystallized at 892°C (second crystallization temperature+20°C) for 3 hrs consisted mainly of calcium-mica and fluorapatite crystalline phases. Average hardness (3.70 GPa) closely matched human enamel (3.20 GPa). The higher fracture toughness (2.04 MPa√m) combined with the hardness to give a lower brittleness index (1.81 µm(-1/2)) which indicates that they have exceptional machinability. Bending strength results (176.61 MPa) were analyzed by Weibull analysis to determine modulus value (m=17.80). Machinability of the calcium mica-fluorapatite glass-ceramic was demonstrated by fabricating with CAD/CAM.

Multielemental analysis of prehistoric animal teeth by laser-induced breakdown spectroscopy and laser ablation inductively coupled plasma mass spectrometry

DOE Office of Scientific and Technical Information (OSTI.GOV)

Galiova, Michaela; Kaiser, Jozef; Fortes, Francisco J.

2010-05-01

Laser-induced breakdown spectroscopy (LIBS) and laser ablation (LA) inductively coupled plasma (ICP) mass spectrometry (MS) were utilized for microspatial analyses of a prehistoric bear (Ursus arctos) tooth dentine. The distribution of selected trace elements (Sr, Ba, Fe) was measured on a 26 mmx15 mm large and 3 mm thick transverse cross section of a canine tooth. The Na and Mg content together with the distribution of matrix elements (Ca, P) was also monitored within this area. The depth of the LIBS craters was measured with an optical profilometer. As shown, both LIBS and LA-ICP-MS can be successfully used for themore » fast, spatially resolved analysis of prehistoric teeth samples. In addition to microchemical analysis, the sample hardness was calculated using LIBS plasma ionic-to-atomic line intensity ratios of Mg (or Ca). To validate the sample hardness calculations, the hardness was also measured with a Vickers microhardness tester.« less

Enhancing the Hardness of Sintered SS 17-4PH Using Nitriding Process for Bracket Orthodontic Application

NASA Astrophysics Data System (ADS)

Suharno, B.; Supriadi, S.; Ayuningtyas, S. T.; Widjaya, T.; Baek, E. R.

2018-01-01

Brackets orthodontic create teeth movement by applying force from wire to bracket then transferred to teeth. However, emergence of friction between brackets and wires reduces load for teeth movement towards desired area. In order to overcome these problem, surface treatment like nitriding chosen as a process which could escalate efficiency of transferred force by improving material hardness since hard materials have low friction levels. This work investigated nitriding treatment to form nitride layer which affecting hardness of sintered SS 17-4PH. The nitride layers produced after nitriding process at various temperature i.e. 470°C, 500°C, 530°C with 8hr holding time under 50% NH3 atmosphere. Optical metallography was conducted to compare microstructure of base and surface metal while the increasing of surface hardness then observed using vickers microhardness tester. Hardened surface layer was obtained after gaseous nitriding process because of nitride layer that contains Fe4N, CrN and Fe-αN formed. Hardness layers can achieved value 1051 HV associated with varies thickness from 53 to 119 μm. The presence of a precipitation process occurring in conjunction with nitriding process can lead to a decrease in hardness due to nitrogen content diminishing in solid solution phase. This problem causes weakening of nitrogen expansion in martensite lattice.

Use of variations in unit cell length, reflectance and hardness for determining the origin of Fe disulphides in sedimentary rocks

NASA Astrophysics Data System (ADS)

Dill, H. G.; Eberhard, E.; Hartmann, B.

1997-01-01

Fe disulphides are common opaque accessories in sedimentary rocks. Both marcasite and pyrite may shed some light on the depositional environment and help determine the diagenesis of their host rocks. Quantitative ore microscopy (reflectance measurements, Vickers hardness numbers) and X-ray diffraction methods, supplemented with scanning electron microscopy and chemical analyses, were applied to pyrite (and some marcasite) hosted by sedimentary rocks spanning the interval from the Devonian to the Pliocene, and formed in various marine and continental environments. Quantitative ore microscopy of pyrites of sedimentary origin does not seem to be an efficient tool for analyzing the environment owing to the inhomogeneous nature of sulphide aggregates when viewed under the ore microscope, and the variable amounts of minor elements (e.g., As, Ni, and Co) that control the reflectance values (RV) and Vickers hardness numbers (VHN) of the host sulphides. However, such parameters as crystal habit and unit cell length of pyrite, which correlate with FeS x, are useful for environmental analysis. The redox conditions and the presence of organic remains during formation are the main factors determining these crystallographic parameters. Differences in these parameters from those of pure, ideal FeS 2 can be related to substitution of, e.g., wustite in the pyrite lattice, reflecting moderate oxidation (i.e. in the microenvironment). As far as crystal habit and length of the cell edge are concerned, late stage diagenesis is obviously less important than the microenvironment attending initial formation. The environment of deposition (i.e. the macroenvironment) of pyrite-bearing rocks has no influence on the crystal morphology or the length of the unit cell of Fe disulphide. X-ray diffraction measurements demonstrate that this method provides useful evidence on the microenvironment of sulphide precipitation around a single, equant pyrite, as well as around pyritized fossils.

The influences of accelerated aging on mechanical properties of veneering ceramics used for zirconia restorations.

PubMed

Luo, Huinan; Tang, Xuehua; Dong, Zhen; Tang, Hui; Nakamura, Takashi; Yatani, Hirofumi

2016-01-01

This study evaluated the influences of accelerated aging on the mechanical properties of veneering ceramics used for zirconia frameworks. Five different veneering ceramics for zirconia frameworks were used. Twenty specimens were fabricated for each veneering ceramic. All specimens were divided into two groups. One was subjected to accelerated aging and the other was used as a control. Accelerated aging was performed in distilled water for 5 h at 200ºC and 2 atm. The density, open porosity, surface roughness, three-point flexural strength, and Vickers hardness were measured. The results showed that the density, open porosity, and surface roughness of all examined veneering ceramics were changed by the accelerated aging process. Accelerated aging was also found to have a positive effect on strength and a negative effect on the hardness.

Optimization Study of Pulsed DC Nitrogen-Hydrogen Plasma in the Presence of an Active Screen Cage

NASA Astrophysics Data System (ADS)

Saeed, A.; W. Khan, A.; F., Jan; U. Shah, H.; Abrar, M.; Zaka-Ul-Islam, M.; Khalid, M.; Zakaullah, M.

2014-05-01

A glow discharge plasma nitriding reactor in the presence of an active screen cage is optimized in terms of current density, filling pressure and hydrogen concentrations using optical emission spectroscopy (OES). The samples of AISI 304 are nitrided for different treatment times under optimum conditions. The treated samples were analyzed by X-ray diffraction (XRD) to explore the changes induced in the crystallographic structure. The XRD pattern confirmed the formation of iron and chromium nitrides arising from incorporation of nitrogen as an interstitial solid solution in the iron lattice. A Vickers microhardness tester was used to evaluate the surface hardness as a function of treatment time (h). The results showed clear evidence of improved surface hardness and a substantial amount of decrease in the treatment time compared with the previous work.

Evaluation of crystalline changes and resistance to demineralization of the surface of human dental enamel treated with Er:YAG laser and fluoride using x-ray diffraction analysis and Vickers microhardness

NASA Astrophysics Data System (ADS)

Behroozibakhsh, Marjan; Shahabi, Sima; Ghavami-Lahiji, Mehrsima; Sadeghian, Safura; Sadat Faal Nazari, Neda

2018-06-01

This study aimed to investigate the changes in crystalline structure and resistance to demineralization of human dental surface enamel treated with erbium-doped yttrium aluminium garnet laser (Er:YAG) laser and fluoride. The enamel surfaces were divided into four groups according to the treatment process including, (L): irradiated with Er:YAG; (F): treated with acidulated phosphate fluoride gel (LF): Pre-irradiated surfaces with Er:YAG subjected to acidulated phosphate fluoride gel and (FL): laser irradiation was performed on the fluoridated enamel surface. Before and after the treatment procedure, the samples were evaluated using X-ray diffraction, scanning electron microscope (SEM) and the Vickers microhardness test. The surface microhardness values also were measured after a pH-cycling regime and acid challenge. The a-axis of all lased groups was contracted after treatment procedure. Measurement of the area under the peaks showed the highest crysallinity in the FL group. The hardness values of all laser treated samples significantly reduced after treatment procedure compared to the F group (p  ⩽  0.001). The morphological observations showed remarkable changes on the lased enamel surfaces including cracks, craters and exposed prisms. These findings suggest, irradiation of the Er:YAG laser accompanying with fluoride application can induce some beneficial crystalline changes regarding the acid-resistance properties of enamel, however, the craters and cracks produced by laser irradiation can promote enamel demineralization and consequently the positive effects of the Er:YAG laser will be eliminated.

Effect of PWHT on Microstructure, Mechanical and Corrosion Behaviour of Gas Tungsten Arc Welds of IN718 Superalloys

NASA Astrophysics Data System (ADS)

Dilkush; Mohammed, Raffi; Madhusudhan Reddy, G.; Srinivasa Rao, K.

2018-03-01

The present work aims to improve corrosion resistance and mechanical behavior of the welds with suitable post weld heat treatment i.e. direct aging and solutionizing treatments (980STA, 1080STA). Gas tungsten arc welding (GTAW) has been performed on Inconel 718 (IN718) nickel based super alloy plates with 3mm thickness. The structural –property relationship of the post weld heat treated samples is judged by correlating the microstructural changes with observed mechanical behavior and pitting corrosion resistance of the welds As-recevied, direct aging (DA), 980STA,1080STA were studied. Welds were characterized for microstructure changes with scanning electron microscopy (SEM) and optical microscopy (OM).Vickers micro- hardness tester was used to measure the hardness of the weldments. Potential-dynamic polarization testing was carried out to study the pitting corrosion resistance in 3.5%NaCl (Sodium chloride) solution at 30°C.Results of the present study established that post weld heat treatments resulted in promoting the element segregation diffusion and resolve them from brittle laves particles in the matrix. Increased precipitation of strengthening phases lead to a significant increase in fusion zone hardness of 1080STA post weld heat treated condition compared to as welded, direct aged, 980STA conditions. Due to significant changes in the microstructural behavior of 1080STA condition resulted in superior pitting corrosion resistance than 980STA, direct aged and as- recevied conditions of IN718 GTA welds

The In vitro Evaluation of the effect of xyliwhite, probiotic, and the conventional toothpastes on the enamel roughness and microhardness.

PubMed

Maden, E Arat; Altun, C; Polat, G Guven; Basak, F

2018-03-01

The aim of this study was to evaluate the effect of fluoride, Xylitol, Probiotic, and Whitening toothpastes on the permanent teeth enamel roughness and microhardness. One hundred and twenty teeth were randomly divided into 2 groups, each group having 60 samples. G1: The group in which enamel roughness was examined (n = 60). G2: The group in which enamel microhardness was examined (n = 60). Then, these groups were randomly divided into 4 groups among themselves (n = 15). Each group was brushed using four different toothpastes for 1 week with a battery-powered toothbrush in the morning and evening for 2 min. Vicker's hardness tester was used to measure the changes in microhardness, and the profilometer was used to measure the changes in surface roughness. No statistically significant differences were found on surface roughness and microhardness values measured after tooth brushing process in group brushed with Colgate MaxFresh toothpaste (P > 0.01). Statistically significant decrease was observed on Vicker's hardness values measured after tooth brushing process in groups brushed with Ipana White Power Carbonate toothpaste, Xyliwhite Toothpaste Gel, and Periobiotic Probiotic Toothpaste (P < 0.01). Statistically significant increase was observed on surface roughness values in groups brushed with Ipana White Power Carbonate toothpaste, Xyliwhite Toothpaste Gel, Periobiotic Probiotic Toothpaste (P < 0.01). As a result, Colgate MaxFresh abrasive-free toothpaste with fluoride has no effect on permanent tooth enamel surface roughness and microhardness. Xyliwhite, Periobiotic, and Ipana White Power Carbonate-containing abrasive toothpastes led to changes negatively on permanent tooth enamel surface roughness and microhardness.

Light energy attenuation through orthodontic ceramic brackets at different irradiation times.

PubMed

Santini, Ario; Tiu, Szu Hui; McGuinness, Niall J P; Aldossary, Mohammed Saeed

2016-09-01

To evaluate the total light energy (TLE) transmission through three types of ceramic brackets with, bracket alone and with the addition of orthodontic adhesive, at different exposure durations, and to compare the microhardness of the cured adhesive. Three different makes of ceramic brackets, Pure Sapphire(M), Clarity™ ADVANCED(P) and Dual Ceramic(P) were used. Eighteen specimens of each make were prepared and allocated to three groups (n = 6). MARC(®)-resin calibrator was used to determine the light curing unit (LCU) tip irradiance (mW/cm(2)) and TLE (J/cm(2)) transmitted through the ceramic brackets, and through ceramic bracket plus Transbond™ XT Light Cure Adhesive, for 5, 10 and 20 s. Vickers-hardness values at the bottom of the cured adhesive were determined. Statistical analysis used one-way analysis of variance (ANOVA); P = 0.05. TLE transmission rose significantly among all samples with increasing exposure durations. TLE reaching the adhesive- enamel interface was less than 10 J/cm(2), and through monocrystalline and polycrystalline ceramic brackets was significantly different (P < 0.05). Pure Sapphire(M) showed the highest amount of TLE transmission and Vickers-hardness values for 5, 10 and 20 s. Following manufacturer's recommendations, insufficient TLE may be delivered to the adhesive: increasing the exposure durations may be required when adhesive is cured through ceramic brackets. Clinicians are advised to measure the tip irradiance of their LCUs and increase curing time beyond 5 s. Orthodontic clinicians should understand the type of light curing device and the orthodontic adhesive used in their practice.

Effects of HfB2 and HfN Additions on the Microstructures and Mechanical Properties of TiB2-Based Ceramic Tool Materials

PubMed Central

An, Jing; Song, Jinpeng; Liang, Guoxing; Gao, Jiaojiao; Xie, Juncai; Cao, Lei; Wang, Shiying; Lv, Ming

2017-01-01

The effects of HfB2 and HfN additions on the microstructures and mechanical properties of TiB2-based ceramic tool materials were investigated. The results showed that the HfB2 additive not only can inhibit the TiB2 grain growth but can also change the morphology of some TiB2 grains from bigger polygons to smaller polygons or longer ovals that are advantageous for forming a relatively fine microstructure, and that the HfN additive had a tendency toward agglomeration. The improvement of flexural strength and Vickers hardness of the TiB2-HfB2 ceramics was due to the relatively fine microstructure; the decrease of fracture toughness was ascribed to the formation of a weaker grain boundary strength due to the brittle rim phase and the poor wettability between HfB2 and Ni. The decrease of the flexural strength and Vickers hardness of the TiB2-HfN ceramics was due to the increase of defects such as TiB2 coarse grains and HfN agglomeration; the enhancement of fracture toughness was mainly attributed to the decrease of the pore number and the increase of the rim phase and TiB2 coarse grains. The toughening mechanisms of TiB2-HfB2 ceramics mainly included crack bridging and transgranular fracture, while the toughening mechanisms of TiB2-HfN ceramics mainly included crack deflection, crack bridging, transgranular fracture, and the core-rim structure. PMID:28772821

Synthesis Oxide Dispersion Strengthening Stainless Steel doped with Nano Zirconia by Mechanical Alloying

NASA Astrophysics Data System (ADS)

Pawawoi; Widiansyah, Irfan; Hadi Prajitno, Djoko

2017-01-01

The oxide dispersion strengthening stainless steel of Fe-11.5wt%Cr and Fe-11.5wt%Cr-1%ZrO2 alloy by mechanical alloying method were synthesized by planetary ball milling. The methods employed for study were designing of Fe-11.5wt%Cr and Fe-11.5wt%Cr-1%ZrO2 proportion of composition alloy which is plotted to Schaffler diagram to get ferritic/martensitic stainless steel. After MA the ODS powders were compaction with pressure 80kg/mm2 and followed by sintering at the temperature of 900,1000 and 1100º C under high purity argon atmosphere for 1 hour. Characterization by XRD is used to examination phase present. Optical microscopy and SEM is used to get image microstructures. XRD analysis resulting the ferritic and martensitic is a major and minor phase respectively. There are not significant differences in the microstructure between Fe-11.5wt%Cr and Fe-11.5wt%Cr-1wt%ZrO2. An increase in the sintering temperature shift the microstructure from dendritic to equaxed. EDS examination showed that zirconia exit in the alloy Fe-11.5wt%Cr-1wt%ZrO2.The addition of 1 % nano-zirconia (ZrO2) into Fe-Cr alloy while milling process was resulted a higher Hardness Vickers Values rather than without zirconia addition. Average value of Hardness Vickers values was resulted 135.5 HV for Fe-11.5wt%Cr whereas 138.4 HV for Fe-11.5wt%Cr-1wt%ZrO2.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Shanmin; Yu, Xiaohui; Zhang, Jianzhong

Here, we report synthesis of single-crystal VN and CrN through high-pressure ionexchange reaction routes. The final products are stoichiometric and have crystallite sizes in the range of 50-120 mu m. We also prepared VN and TiN crystals using high-pressure sintering of nitride powders. On the basis of single-crystal indentation testing, the determined asymptotic Vickers hardness for TiN, VN, and CrN is 18 (1), 10 (1), and 16 (1) GPa, respectively. Moreover, the relatively low hardness in VN indicates that the metallic bonding prevails due to the overfilled metallic a bonds, although the cation-anion covalent hybridization in this compound is muchmore » stronger than that in TiN and CrN. All three nitrides are intrinsically excellent metals at ambient pressure. In particular, VN exhibits superconducting transition at T-c approximate to 7.8 K, which is slightly lower than the reported values for nitrogen-deficient or crystallinedisordered samples due to unsuppressed "spin fluctuation" in the well-crystallized stoichiometric VN. The magnetostructural transition in CrN correlates with a metal metal transition at T-N = 240(5) K and is accompanied by a similar to 40% drop in electrical resistivity. Additionally, more detailed electronic properties are presented with new insights into these nitrides.« less

Solid State Reaction Synthesis of Si-HA as Potential Biomedical Material: An Endeavor to Enhance the Added Value of Indonesian Mineral Resources

NASA Astrophysics Data System (ADS)

Hartatiek; Yudyanto; Ratnasari, S. D.; Windari, R. Y.; Hidayat, N.

2017-05-01

In recent years, one of the most prominently investigated materials is hydroxyapatite (HA). It is because of its excellent properties for medical applications, essentially related to orthopedic. Also, the introduction of other materials to HA becomes another research focus of many leading scientists. In this present study, silicon with various concentrations was introduced, by means of solid state reaction route, to HA forming Si-HA. The crystal structure properties of the as-prepared samples were evaluated by X-ray diffractometer (XRD). Fourier Transform Infra Red (FTIR) spectroscopy data collection and analysis were done to investigate the functional groups within the samples. The microstructural characteristics as well as elemental mapping of the samples were captured by scanning electron microscopy and energy dispersive x-ray spectroscopy (SEM-EDX). Vickers hardness test was also conducted to investigate the hardness properties of the samples. Furthermore, in vitro characterization-based bio resorbability of the samples in a simulated body fluid were also described. This study revealed that Indonesian limestone can be utilized as the raw material for synthesizing HA. The silicon has been successfully incorporated into phosphate site of the HA crystal. Conclusively, the Si-HA reported in this study shows good bioresorbability characteristic.

Cracking Problems and Mechanical Characteristics of PME and BME Ceramic Capacitors

NASA Technical Reports Server (NTRS)

Teverovsky, Alexander

2018-01-01

Most failures in MLCCs are caused by cracking that create shorts between opposite electrodes of the parts. A use of manual soldering makes this problem especially serious for space industry. Experience shows that different lots of ceramic capacitors might have different susceptibility to cracking under manual soldering conditions. This simulates a search of techniques that would allow revealing capacitors that are most robust to soldering-induced stresses. Currently, base metal electrode (BME) capacitors are introduced to high-reliability applications as a replacement of precious metal electrode (PME) parts. Understanding the difference in the susceptibility to cracking between PME and BME capacitors would facilitate this process. This presentation gives a review of mechanical characteristics measured in-situ on MLCCs that includes flexural strength, Vickers hardness, indentation fracture toughness, and the board flex testing and compare characteristics of BME and PME capacitors. A history case related to cracking in PME capacitors that caused flight system malfunctions and mechanisms of failure are considered. Possible qualification tests that would allow evaluation of the resistance of MLCCs to manual soldering are suggested and perspectives related to introduction of BME capacitors discussed.

Microstructure control for high strength 9Cr ferritic-martensitic steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tan, Lizhen; Hoelzer, David T; Busby, Jeremy T

2012-01-01

Ferritic-martensitic (F-M) steels with 9 wt.%Cr are important structural materials for use in advanced nuclear reactors. Alloying composition adjustment, guided by computational thermodynamics, and thermomechanical treatment (TMT) were employed to develop high strength 9Cr F-M steels. Samples of four heats with controlled compositions were subjected to normalization and tempering (N&T) and TMT, respectively. Their mechanical properties were assessed by Vickers hardness and tensile testing. Ta-alloying showed significant strengthening effect. The TMT samples showed strength superior to the N&T samples with similar ductility. All the samples showed greater strength than NF616, which was either comparable to or greater than the literaturemore » data of the PM2000 oxide-dispersion-strengthened (ODS) steel at temperatures up to 650 C without noticeable reduction in ductility. A variety of microstructural analyses together with computational thermodynamics provided rational interpretations on the strength enhancement. Creep tests are being initiated because the increased yield strength of the TMT samples is not able to deduce their long-term creep behavior.« less

PWSCC Susceptibility in Heat Affected Zones of Alloy 600

NASA Astrophysics Data System (ADS)

Couvant, Thierry; Brossier, Thomas; Cossange, Christian

The recent field experience and several experimental results have shown the possible deleterious effect of a heat affected zone (HAZ) induced by welding on the susceptibility to the stress corrosion cracking (SCC) of Alloy 600 of bottom penetrations exposed to primary water of PWRs. This work tried to quantify the increasing susceptibility to initiation and crack propagation in 600/182 HAZ. The rolled plate did not exhibit any susceptibility to SCC except for a cold work higher than 10% typically. By contrast, the weld metal was well known for its high susceptibility to SCC. Metallurgical and mechanical characterizations of the HAZ indicated a slight gradient of Vickers micro hardness close to the fusion line (up to few mm) and a lack of intergranular precipitates up to 500 µm from the fusion line. SCC tests clearly demonstrated that a non-susceptible plate may exhibit a significant susceptibility to SCC propagation in the HAZ. Results of initiation tests did not allow to observe any SCC in the base metal, due to the high susceptibility to SCC of the weld.

Comparison of mechanical and microstructural properties of conventional and severe plastic deformation processes

NASA Astrophysics Data System (ADS)

Szombathelyi, V.; Krallics, Gy

2014-08-01

The effect of the deformation processes on yield stress, Vickers microhardness and dislocation density were investigated using commercial purity (A1050) and alloyed aluminum (Al 6082). For the evolution of the dislocation density X-ray line profile analysis was used. In the large plastic strain range the variation of mechanical and microstructure evolution of A1050 and of Al 6082 processed by equal channel angular pressing are investigated using route BC and route C. In the plastic strain range up to 3 plane strain compression test was used to evaluate mechanical properties. The hardness and the yield stress showed a sharp increase after the first pass. In the case of A1050 it was found that the two examined routes has not resulted difference in the flow stress. In the case of Al 6082 the effect of the routes on the yield stress is significant. The present results showed that in the comparable plastic strain range higher yield stress values can be achieved by plane strain compression test than by ECAP.

Investigation of stand-off distance effect on structure, adhesion and hardness of copper coatings obtained by the APS technique

NASA Astrophysics Data System (ADS)

Masoumeh, Goudarzi; Shahrooz, Saviz; Mahmood, Ghoranneviss; Ahmad, Salar Elahi

2018-03-01

The outbreak of the disease and infection in the hospital environment and medical equipment is one of the concerns of modern life. One of the effective ways for preventing and reducing the complications of infections is modification of the surface. Here, the handmade atmospheric plasma spray system is used for accumulating copper as an antibacterial agent on the 316L stainless steel substrate, which applies to hospital environment and medical equipment. As a durable coating with proper adhesion is needed on the substrate, the effect of stand-off distance (SOD) which is an important parameter of the spray on the microstructure, the hardness and adhesion of the copper coating on the 316L stainless steel were investigated. The structure and phase composition of copper depositions were investigated using scanning electron microscopy and X-ray diffraction. The adhesion and hardness of depositions are evidenced using the cross cut tester and Vickers hardness tester, respectively. The findings confirm that the voids in the coatings increase with increasing SOD, which leads to decreasing the hardness of coatings and also the adhesion strength between depositions and substrate. In addition, by increasing the SOD, the oxygen content and the size of grains in the lamellae (fine structure) of coatings also increase.

Comparison of Microstructures and Mechanical Properties for Solid and Mesh Cobalt-Base Alloy Prototypes Fabricated by Electron Beam Melting

NASA Astrophysics Data System (ADS)

Gaytan, S. M.; Murr, L. E.; Martinez, E.; Martinez, J. L.; Machado, B. I.; Ramirez, D. A.; Medina, F.; Collins, S.; Wicker, R. B.

2010-12-01

The microstructures and mechanical behavior of simple, as-fabricated, solid geometries (with a density of 8.4 g/cm3), as-fabricated and fabricated and annealed femoral (knee) prototypes, and reticulated mesh components (with a density of 1.5 g/cm3) all produced by additive manufacturing (AM) using electron beam melting (EBM) of Co-26Cr-6Mo-0.2C powder are examined and compared in this study. Microstructures and microstructural issues are examined by optical metallography (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectrometry (EDS), and X-ray diffraction (XRD), while mechanical properties included selective specimen tensile testing and Vickers microindentation hardness (HV) and Rockwell C-scale hardness (HRC) measurements. Orthogonal (X-Y) melt scanning of the electron beam during AM produced unique, orthogonal and related Cr23C6 carbide (precipitate) arrays (a controlled microstructural architecture) with dimensions of 2 μm in the build plane perpendicular to the build direction, while connected carbide columns were formed in the vertical plane, parallel to the build direction, with microindentation hardnesses ranging from 4.4 to 5.9 GPa, corresponding to a yield stress and ultimate tensile strength (UTS) of 0.51 and 1.45 GPa with elongations ranging from 1.9 to 5.3 pct. Annealing produced an equiaxed fcc grain structure with some grain boundary carbides, frequent annealing twins, and often a high density of intrinsic {111} stacking faults within the grains. The reticulated mesh strut microstructure consisted of dense carbide arrays producing an average microindentation hardness of 6.2 GPa or roughly 25 pct higher than the fully dense components.

Effects of Ceramic Density and Sintering Temperature on the Mechanical Properties of a Novel Polymer-Infiltrated Ceramic-Network Zirconia Dental Restorative (Filling) Material.

PubMed

Li, Weiyan; Sun, Jian

2018-05-10

BACKGROUND Polymer-infiltrated ceramic-network (PICN) dental material is a new and practical development in orthodontics. Sintering is the process of forming a stable solid mass from a powder by heating without melting. The aim of this study was to evaluate the effects of sintering temperature on the mechanical properties of a PICN zirconia dental material. MATERIAL AND METHODS A dense zirconia ceramic and four PICN zirconia dental materials, with varying porosities, were sintered at three different temperatures; 12 PICN zirconia dental materials based on these porous ceramics were prepared, as well as a pure polymer. After the specimen preparation, flexural strength and elastic modulus values were measured using the three-point bending test, and fracture toughness were determined by the single-edge notched beam (SENB) method. The Vickers hardness test method was used with an indentation strength (IS) test. Scanning electron microscopy (SEM) was used to examine the microstructure of the ceramic surface and the fracture surface. RESULTS Mechanical properties of the PICN dental materials, including flexural strength, elastic modulus, fracture toughness, and hardness, were more similar to the properties of natural teeth when compared with traditional dental ceramic materials, and were affected by the density and sintering temperature. SEM showed that the porous ceramic network became cohesive and that the length of cracks in the PICN dental material was reduced. CONCLUSIONS PICN zirconia dental materials were characterized by similar mechanical properties to natural dental tissues, but further studies are required continue to improve the similarities with natural human enamel and dentin.

Effects of Ceramic Density and Sintering Temperature on the Mechanical Properties of a Novel Polymer-Infiltrated Ceramic-Network Zirconia Dental Restorative (Filling) Material

PubMed Central

Li, Weiyan

2018-01-01

Background Polymer-infiltrated ceramic-network (PICN) dental material is a new and practical development in orthodontics. Sintering is the process of forming a stable solid mass from a powder by heating without melting. The aim of this study was to evaluate the effects of sintering temperature on the mechanical properties of a PICN zirconia dental material. Material/Methods A dense zirconia ceramic and four PICN zirconia dental materials, with varying porosities, were sintered at three different temperatures; 12 PICN zirconia dental materials based on these porous ceramics were prepared, as well as a pure polymer. After the specimen preparation, flexural strength and elastic modulus values were measured using the three-point bending test, and fracture toughness were determined by the single-edge notched beam (SENB) method. The Vickers hardness test method was used with an indentation strength (IS) test. Scanning electron microscopy (SEM) was used to examine the microstructure of the ceramic surface and the fracture surface. Results Mechanical properties of the PICN dental materials, including flexural strength, elastic modulus, fracture toughness, and hardness, were more similar to the properties of natural teeth when compared with traditional dental ceramic materials, and were affected by the density and sintering temperature. SEM showed that the porous ceramic network became cohesive and that the length of cracks in the PICN dental material was reduced. Conclusions PICN zirconia dental materials were characterized by similar mechanical properties to natural dental tissues, but further studies are required continue to improve the similarities with natural human enamel and dentin. PMID:29746449

Growth, structural, optical, thermal and mechanical properties of ammonium pentaborate single crystal.

PubMed

Balakrishnan, T; Bhagavannarayana, G; Ramamurthi, K

2008-11-15

Nonlinear optical single crystals of ammonium pentaborate (APB) were grown by the slow cooling method from aqueous solution. Grown crystal was characterized by powder X-ray diffraction (PXRD) and FT-IR spectral analysis. Perfection of the grown crystal was evaluated by high-resolution X-ray diffractometry (HRXRD). The effect of nylon threading on the perfection of the grown bigger crystal was also studied by HRXRD. The range and percentage of optical transmission was ascertained by recording UV-vis-NIR spectrum. Thermal properties were investigated by TG-DTA and DSC analyses. Its mechanical hardness was estimated by Vickers microhardness tester.

Obtaining and Mechanical Properties of Ti-Mo-Zr-Ta Alloys

NASA Astrophysics Data System (ADS)

Bălţatu, M. S.; Vizureanu, P.; Geantă, V.; Nejneru, C.; Țugui, C. A.; Focşăneanu, S. C.

2017-06-01

Ti-based alloys are successfully used in the area of orthopedic biomaterials for their enhanced biocompatibility, good corrosion and mechanical properties. The most suitable metals as an alloying element for orthopedic biomaterials are zirconium, molybdenum and tantalum because are non toxic and have good properties. The paper purpose development of two alloys of Ti-Mo-Zr-Ta (TMZT) prepared by arc-melting with several mechanical properties determined by microindentation. The mechanical properties analyzed was Vickers hardness and dynamic elasticity modulus. The investigated alloys presents a low Young’s modulus, an important condition of biomaterials for preventing stress shielding phenomenon.

Mechanical properties of multilayered films using different nanoindenters.

PubMed

Fang, Te-Hua; Wang, Tong Hong; Wu, Jia-Hung

2010-07-01

The effects of interface, contact hardness, deformation, and adhesion of Al/Ni multilayered films under nanoindentation were investigated using molecular dynamics (MD) simulations. The results show that the indentation force of the sphere indenter is the largest among nanoindentations using sphere, cone, Vickers, or Berkovich type indenters at the same penetration depth. Force increasing, relaxation and adhesion took place during loading, holding depth and unloading, respectively. The interface occurred along the {111} (110) slip systems and the maximum width of the glide bands was about 1 nm. The reaction force and plastic energy of the indented films are also discussed.

The densification, crystallization and mechanical properties of allylhydridopolycarbosilane-derived silicon carbide

NASA Astrophysics Data System (ADS)

Moraes, Kevin V.

Allylhydridopolycarbosilane is a precursor of growing importance in the fabrication of silicon carbide ceramics. However, prior to this study few details were available about the processing-structure-property relationships for this material. In Part 1 of this study the processes of densification and microstructural transformation of the partially pyrolysed amorphous AHPCS-SiC was investigated in the temperature region of 800°C to 1600°C. In Part 2 of this study, mechanical properties, specifically fracture toughness (K1c) and Vickers hardness, were measured on bulk specimens in the temperature range of 1000°C to 1600°C. A combination of X-Ray diffraction (XRD), Transmission Electron Microscopy (TEM), 29Si Nuclear Magnetic Resonance (NMR) and micro Raman spectroscopy, along with simultaneous Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TGA) were used to follow the structural transformation of the partially pyrolysed AHPCS-SiC on several length scales between the temperature of 800 to 1600°C. It was determined that the rate of densification of amorphous AHPCS-SiC, partially pyrolysed to 600°C, depends on the surface to volume ratio. Calculations were preformed that suggested that nucleation of the SiC crystals should occur preferentially on the surface of the powder particles rather than in the bulk. However, TEM on samples heat-treated to 1600°C did not show a preponderance of crystals on the surface of the particles compared to their bulk. Crystallization of beta-SiC occurs at ca. 1250°C, as determined by DSC and supported by NMR and electron diffraction. The average size of the beta-SiC crystallites, as determined by XRD, was ca. 5 nm at 1600°C. Prior to the crystallization of beta-SiC, Raman spectroscopy indicates the presence of carbon clusters in the otherwise amorphous matrix. These carbon clusters have predominantly sp3 bonding at 1100°C that gradually converts to predominantly sp 2 bonded carbon at higher temperatures, with average basal plane sizes of 20--25 A between 1100 in addition to 1600°C. The amorphous structure formed at temperatures below the crystallization temperature is unstable. It is seen from DSC that amorphous AHPCS-SiC undergoes two distinct exothermic events: a broad, irreversible, exotherm that corresponds to structural relaxation and chemical condensation and a second, much sharper, exotherm that corresponds to crystallization. Fracture toughness values measured on cold-pressed and infiltrated AHPCS-SiC samples were in the range of 1.4 to 1.67 MPam1/2. It appears that toughness increases with increasing heat treatment temperature. The Vickers hardness at 10 N was ca. 8.7 to 12.6 MPa. The Vickers hardness does not appear to vary significantly with the heat-treatment temperature.

[Influence of different ultrasonic irrigation solutions after root canal preparation with ProTaper by machine on micro-hardness of root canal dentin].

PubMed

Guo, Jiang-li; Zhang, Yan; Zhen, Lei

2015-08-01

To develope the influence of different ultrasonic irrigations after root canal preparation with nickel titanium ProTaper on micro-hardness of root canal dentin. Sixty of maxillary anterior teeth with single-canal were collected and randomly divided into 6 groups. Group A was control group, group B was prepared to F3 with nickel titanium ProTaper by machine, group C was ultrasonic irrigated with 3% hydrogen peroxide solution for 1 minute after preparation, group D was ultrasonic irrigated with koutai mouthwash for 1 minute after preparation, group E was ultrasonic irrigated with 17% EDTA solution for 1 minute after preparation, group F was ultrasonic irrigated with distilled water for 1 minute after preparation. The roots were then sectioned horizontally into 3 parts, split longitudinally into halves and examined under a micro Vickers hardness test machine. The data was analyzed by one-way ANOVA and t test with SPSS 17.0 software package. The micro-hardness of group A was (52.66 ± 1.64) HV,(52.08 ± 1.53) HV and (51.47 ± 2.53) HV. There was no significant difference in all parts of the root canal in group A (P>0.05). The micro-hardness of the apical third of root canal was lower than that of the cervical and middle of root canal in the other groups (P<0.05). In the cervical and middle third of the root canals, the micro-hardness of group E was (44.65 ± 1.33) HV and(42.55 ± 1.12) HV, and there were statistical significances between group E and the other groups (P<0.05). In the apical third of root canal,the micro-hardness of group E was (37.82 ± 1.60) HV, and group C was (44.14±1.73) HV, both of the comparative differences with other groups were statistically significant (P<0.05). There was no significant difference among group B, group D and group F (P>0.05). Root canal preparation to F3 with nickel titanium ProTaper by machine can make the micro-hardness of the apical third of root canal decrease. Ultrasonic irrigation with 17% EDTA solution for 1 minute can make the micro-hardness of the root canal decrease ultrasonic irrigation with. Ultrasonic irrigation with 3% hydrogen peroxide can make the micro-hardness of the apical third of root canal decrease. Ultrasonic irrigation with Koutai mouthwash and distilled water for 1 minute have no influence on the micro-hardness of root canal.

Comparative Studies on microstructure, mechanical and corrosion behaviour of DMR 249A Steel and its welds

NASA Astrophysics Data System (ADS)

Mohammed, Raffi; Dilkush; Madhusudhan Reddy, G.; Srinivasa Rao, K.

2018-03-01

DMR249A Medium strength (low carbon) Low-alloy steels are used as structural components in naval applications due to its low cost and high availability. An attempt has been made to weld the DMR 249A steel plates of 8mm thickness using shielded metal arc welding (SMAW) and gas tungsten arc welding (GTAW). Welds were characterized for metallography to carry out the microstructural changes, mechanical properties were evaluated using vickers hardness tester and universal testing machine. Potentio-dynamic polarization tests were carried out to determine the pitting corrosion behaviour. Constant load type Stress corrosion cracking (SCC) testing was done to observe the cracking tendency of the joints in a 3.5%NaCl solution. Results of the present study established that SMA welds resulted in formation of relatively higher amount of martensite in ferrite matrix when compared to gas tungsten arc welding (GTAW). It is attributed to faster cooling rates achieved due to high thermal efficiency. Improved mechanical properties were observed for the SMA welds and are due to higher amount of martensite. Pitting corrosion and stress corrosion cracking resistance of SMA welds were poor when compared to GTA welds.

Evaluation of Giga-cycle Fatigue Properties of Austenitic Stainless Steels Using Ultrasonic Fatigue Test

NASA Astrophysics Data System (ADS)

Takahashi, Kyouhei; Ogawa, Takeshi

Ultrasonic fatigue tests have been performed in austenitic stainless steel, SUS316NG, in order to investigate giga-cycle fatigue strength of pre-strained materials, i.e. 5, 10 and 20% tensile pre-strains and -20% compressive pre-strain. The pre-strains were applied before specimen machining. The austenitic stainless steels are known to exhibit remarkable self-heating during the fatigue experiment. Therefore, heat radiation method was established by setting fatigue specimens in a low temperature chamber at about -100°C. The self-heating was controlled by intermittent loading condition, which enabled us to maintain the test section of the specimens at about room temperature. The results revealed that the fatigue strength increased with increasing pre-strain levels. Fish-eye fracture was observed for -20% pre-strained specimen fractured at 4.11×107 cycles, while the other specimens exhibited ordinary fatigue fracture surface originated from stage I facet on the specimen surface. The increase in fatigue limit was predicted by Vickers hardness, HV, which depended on the size of indented region. The prediction was successful using HV values obtained by the size of the indented region similar to those of the stage I facets.

Metallurgy and mechanical properties variation with heat input,during dissimilar metal welding between stainless and carbon steel

NASA Astrophysics Data System (ADS)

Ramdan, RD; Koswara, AL; Surasno; Wirawan, R.; Faturohman, F.; Widyanto, B.; Suratman, R.

2018-02-01

The present research focus on the metallurgy and mechanical aspect of dissimilar metal welding.One of the common parameters that significantly contribute to the metallurgical aspect on the metal during welding is heat input. Regarding this point, in the present research, voltage, current and the welding speed has been varied in order to observe the effect of heat input on the metallurgical and mechanical aspect of both welded metals. Welding was conducted by Gas Metal Arc Welding (GMAW) on stainless and carbon steel with filler metal of ER 309. After welding, hardness test (micro-Vickers), tensile test, macro and micro-structure characterization and Energy Dispersive Spectroscopy (EDS) characterization were performed. It was observed no brittle martensite observed at HAZ of carbon steel, whereas sensitization was observed at the HAZ of stainless steel for all heat input variation at the present research. Generally, both HAZ at carbon steel and stainless steel did not affect tensile test result, however the formation of chromium carbide at the grain boundary of HAZ structure (sensitization) of stainless steel, indicate that better process and control of welding is required for dissimilar metal welding, especially to overcome this issue.

The effect of filler loading and morphology on the mechanical properties of contemporary composites.

PubMed

Kim, Kyo-Han; Ong, Joo L; Okuno, Osamu

2002-06-01

Little information exists regarding the filler morphology and loading of composites with respect to their effects on selected mechanical properties and fracture toughness. The objectives of this study were to: (1) classify commercial composites according to filler morphology, (2) evaluate the influence of filler morphology on filler loading, and (3) evaluate the effect of filler morphology and loading on the hardness, flexural strength, flexural modulus, and fracture toughness of contemporary composites. Field emission scanning electron microscopy/energy dispersive spectroscopy was used to classify 3 specimens from each of 14 commercial composites into 4 groups according to filler morphology. The specimens (each 5 x 2.5 x 15 mm) were derived from the fractured remnants after the fracture toughness test. Filler weight content was determined by the standard ash method, and the volume content was calculated using the weight percentage and density of the filler and matrix components. Microhardness was measured with a Vickers hardness tester, and flexural strength and modulus were measured with a universal testing machine. A 3-point bending test (ASTM E-399) was used to determine the fracture toughness of each composite. Data were compared with analysis of variance followed by Duncan's multiple range test, both at the P<.05 level of significance. The composites were classified into 4 categories according to filler morphology: prepolymerized, irregular-shaped, both prepolymerized and irregular-shaped, and round particles. Filler loading was influenced by filler morphology. Composites containing prepolymerized filler particles had the lowest filler content (25% to 51% of filler volume), whereas composites containing round particles had the highest filler content (59% to 60% of filler volume). The mechanical properties of the composites were related to their filler content. Composites with the highest filler by volume exhibited the highest flexural strength (120 to 129 MPa), flexural modulus (12 to 15 GPa), and hardness (101 to 117 VHN). Fracture toughness was also affected by filler volume, but maximum toughness was found at a threshold level of approximately 55% filler volume. Within the limitations of this study, the commercial composites tested could be classified by their filler morphology. This property influenced filler loading. Both filler morphology and filler loading influenced flexural strength, flexural modulus, hardness, and fracture toughness.

Influence of different staining beverages on color stability, surface roughness and microhardness of silorane and methacrylate-based composite resins.

PubMed

Karaman, Emel; Tuncer, Duygu; Firat, Esra; Ozdemir, Oguz Suleyman; Karahan, Sevilay

2014-05-01

To investigate the influence of different staining beverages on color stability, surface roughness and microhardness of silorane and methacrylate-based composite resins. Three different composite resins (Filtek Silorane, Filtek P60, Filtek Supreme XT) were tested. Thirty cylindrical specimens (10 × 2 mm) per material were prepared and polished with a series of aluminum-oxide polishing disks. Each group was then randomly subdivided into three groups according to the test beverages: distilled water (control), cola and coffee. The samples were immersed into different beverages for 15 days. Color, surface roughness and microhardness values were measured by a spectrophotometer, prophylometer and Vickers hardness device respectively, at baseline and after 15 days. The data were subjected to statistical analysis. Immersion in coffee resulted in a significant discoloration for all the composites tested, although the color change was lower in Filtek Silorane than that of MBCs (p < 0.05). All the composites tested showed similar surface roughness changes after immersion in different beverages (p > 0.05). Besides coffee caused more roughness change than others. Immersion in coffee caused highest microhardness change in Filtek Supreme XT (p < 0.05). Cola and coffee altered, to some degree, the color, surface roughness and/or microhardness of the tested resin composites, depending on the characteristics of the materials.

Superthermostability of nanoscale TIC-reinforced copper alloys manufactured by a two-step ball-milling process

NASA Astrophysics Data System (ADS)

Wang, Fenglin; Li, Yunping; Xu, Xiandong; Koizumi, Yuichiro; Yamanaka, Kenta; Bian, Huakang; Chiba, Akihiko

2015-12-01

A Cu-TiC alloy, with nanoscale TiC particles highly dispersed in the submicron-grained Cu matrix, was manufactured by a self-developed two-step ball-milling process on Cu, Ti and C powders. The thermostability of the composite was evaluated by high-temperature isothermal annealing treatments, with temperatures ranging from 727 to 1273 K. The semicoherent nanoscale TiC particles with Cu matrix, mainly located along the grain boundaries, were found to exhibit the promising trait of blocking grain boundary migrations, which leads to a super-stabilized microstructures up to approximately the melting point of copper (1223 K). Furthermore, the Cu-TiC alloys after annealing at 1323 K showed a slight decrease in Vickers hardness as well as the duplex microstructure due to selective grain growth, which were discussed in terms of hardness contributions from various mechanisms.

The effect of boriding on wear resistance of cold work tool steel

NASA Astrophysics Data System (ADS)

Anzawa, Y.; Koyama, S.; Shohji, I.

2017-05-01

Recently, boriding has attracted extensive attention as surface stiffening processing of plain steel. In this research, the influence of processing time on the formation layer of cold work tool steel (KD11MAX) by Al added fused salt bath was examined. In addition, in order to improve the abrasion resistance of KD11MAX, the effect of the treatment of boronization on the formation layer has been investigated. Boriding were performed in molten borax which contained about 10 mass% Al at processing time of 1.8 ~ 7.2 ks (processing temperature of 1303 K). As a result of the examination, the hardness of the boriding layer becomes about 1900 HV when the processing time of 3.6 ks. Also the abrasion resistance has improved remarkably. Furthermore, it was revealed that the formation layer was boronized iron from the Vickers hardness and analysis of the X-ray diffraction measurement.

Superstrong micro-grained polycrystalline diamond compact through work hardening under high pressure

NASA Astrophysics Data System (ADS)

Liu, Jin; Zhan, Guodong; Wang, Qiang; Yan, Xiaozhi; Liu, Fangming; Wang, Pei; Lei, Li; Peng, Fang; Kou, Zili; He, Duanwei

2018-02-01

We report an approach to strengthen micro-grained polycrystalline diamond (MPD) compact through work hardening under high pressure and high temperature, in which both hardness and fracture toughness are simultaneously boosted. Micro-sized diamond powders are treated without any additives under a high pressure of 14 GPa and temperatures ranging from 1000 °C to 2000 °C. It was found that the high pressure and high temperature environments could constrain the brittle feature and cause a severe plastic deformation of starting diamond grains to form a mutual bonded diamond network. The relative density is increased with temperature to nearly fully dense at 1600 °C. The Vickers hardness of the well-prepared MPD bulks at 14 GPa and 1900 °C reaches the top limit of the single crystal diamond of 120 GPa, and the near-metallic fracture toughness of the sample is as high as 18.7 MPa m1/2.

New multifunctional tungsten nitride with energetic N6 and extreme hardness predicted from first principles

NASA Astrophysics Data System (ADS)

Li, Qian; Sha, Lei; Zhu, Chunye; Yao, Yansun

2017-05-01

We report a new member to the family of tungsten nitrides, WN6, predicted from the structure search. Ground-state convex hull calculation reveals that crystalline WN6 is thermodynamically stable at pressures above 16 GPa, but remains dynamically stable at ambient conditions. The predicted high-pressure WN6 structure contains chaired \\text{cyclo-N}6{6-} rings isoelectronic to cyclo-hexasulfur (S6), which is unprecedented in nitrogen. In the \\text{cyclo-N}6{6-} unit all nitrogen atoms are singly bonded and therefore contain a high energy density. By means of efficiently packing the covalent-bonded species, WN6 is estimated to have extremely high Vickers hardness greater than 40 GPa at ambient conditions, placing it as one of the hardest materials. The present results reveal that WN6 may be used as a superhard material but simultaneously maintaining other desirable properties, which represents an interesting example of multifunctional materials.

Effect of Laser Power on Metallurgical, Mechanical and Tribological Characteristics of Hardfaced Surfaces of Nickel-Based Alloy

NASA Astrophysics Data System (ADS)

Gnanasekaran, S.; Padmanaban, G.; Balasubramanian, V.

2017-12-01

In this present work, nickel based alloy was deposited on 316 LN austenitic stainless steel (ASS) by a laser hardfacing technique to investigate the influence of laser power on macrostructure, microstructure, microhardness, dilution and wear characteristics. The laser power varied from 1.1 to 1.9 kW. The phase constitution, microstructure and microhardness were examined by optical microscope, scanning electron microscopy, energy dispersion spectroscopy and Vickers microhardness tester. The wear characteristics of the hardfaced surfaces and substrate were evaluated at room temperature (RT) under dry sliding wear condition (pin-on-disc). The outcome demonstrates that as the laser power increases, dilution increases and hardness of the deposit decreases. This is because excess heat melts more volume of substrate material and increases the dilution; subsequently it decreases the hardness of the deposit. The microstructure of the deposit is characterized by Ni-rich carbide, boride and silicide.

Cold Sprayability of Mixed Commercial Purity Ti Plus Ti6Al4V Metal Powders

NASA Astrophysics Data System (ADS)

Aydin, Huseyin; Alomair, Mashael; Wong, Wilson; Vo, Phuong; Yue, Stephen

2017-02-01

In the present work, metallic composite coatings of commercial purity Ti plus Ti6Al4V were produced by cold spraying to explore the effect of mixing on porosity and mechanical properties of the coatings. The coatings were deposited using N2 gas at 800 °C and 4 MPa pressure on 1020 steel substrate. Coating characteristics were studied by examining porosity percentages and Vickers's hardness. The microstructure was examined using optical and electron microscopy techniques. It was observed that mixing metal powders can lead to improvements in cold sprayability, specifically decreases in the porosity of the `matrix' powder. It is shown that a critical addition can significantly influence porosity, but above this critical level, there is a little change in porosity. Hardness differences between the two powders are considered to be the first-order influence, but differences in particle sizes and morphology may also be contributing factors.

Effects of the iodine incorporation on the structure and physical properties of Ge-Sb-Se chalcogenide glasses

NASA Astrophysics Data System (ADS)

Wang, Yaling; Xu, Junfeng; Cheng, Hu; Chang, Fang'e.; Jian, Zengyun

2018-01-01

(100-x)(Ge23Se67Sb10)-xI (x = 0, 3, 5, 7, 10 wt%) chalcohalide glasses were prepared by the traditional melt-quenched method. The structure and physical properties were analyzed by using XRD, TMA, FTIR and Vickers hardness tester. It was found that the glass structure trends to crystallization with increase of iodine content. The values of infrared transmittance decrease from 62% to 35% in the range of 2.5-16 μm with increasing iodine content. The density decreases from 4.62 ± 0.3 g cm-3 to 4.31 ± 0.3 g cm-3, the hardness decreases from 164.9 ± 0.5 kg mm-2 to 154.6 ± 0.5 kg mm-2. The glass transition point Tg decreases from 267 °C to 205 °C, while the thermal expansion coefficient increases with iodine content.

Wear, strength, modulus and hardness of CAD/CAM restorative materials.

PubMed

Lawson, Nathaniel C; Bansal, Ritika; Burgess, John O

2016-11-01

To measure the mechanical properties of several CAD/CAM materials, including lithium disilicate (e.max CAD), lithium silicate/zirconia (Celtra Duo), 3 resin composites (Cerasmart, Lava Ultimate, Paradigm MZ100), and a polymer infiltrated ceramic (Enamic). CAD/CAM blocks were sectioned into 2.5mm×2.5mm×16mm bars for flexural strength and elastic modulus testing and 4mm thick blocks for hardness and wear testing. E.max CAD and half the Celtra Duo specimens were treated in a furnace. Flexural strength specimens (n=10) were tested in a three-point bending fixture. Vickers microhardness (n=2, 5 readings per specimen) was measured with a 1kg load and 15s dwell time. The CAD/CAM materials as well as labial surfaces of human incisors were mounted in the UAB wear device. Cusps of human premolars were mounted as antagonists. Specimens were tested for 400,000 cycles at 20N force, 2mm sliding distance, 1Hz frequency, 24°C, and 33% glycerin lubrication. Volumetric wear and opposing enamel wear were measured with non-contact profilometry. Data were analyzed with 1-way ANOVA and Tukey post-hoc analysis (alpha=0.05). Specimens were observed with SEM. Properties were different for each material (p<0.01). E.max CAD and Celtra Duo were generally stronger, stiffer, and harder than the other materials. E.max CAD, Celtra Duo, Enamic, and enamel demonstrated signs of abrasive wear, whereas Cerasmart, Lava Ultimate, Paradigm MZ100 demonstrated signs of fatigue. Resin composite and resin infiltrated ceramic materials have demonstrated adequate wear resistance for load bearing restorations, however, they will require at least similar material thickness as lithium disilicate restorations due to their strength. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Synergistic methods for the production of high-strength and low-cost boron carbide

NASA Astrophysics Data System (ADS)

Wiley, Charles Schenck

2011-12-01

Boron carbide (B4C) is a non-oxide ceramic in the same class of nonmetallic hard materials as silicon carbide and diamond. The high hardness, high elastic modulus and low density of B4C make it a nearly ideal material for personnel and vehicular armor. B4C plates formed via hot-pressing are currently issued to U.S. soldiers and have exhibited excellent performance; however, hot-pressed articles contain inherent processing defects and are limited to simple geometries such as low-curvature plates. Recent advances in the pressureless sintering of B4C have produced theoretically-dense and complex-shape articles that also exhibit superior ballistic performance. However, the cost of this material is currently high due to the powder shape, size, and size distribution that are required, which limits the economic feasibility of producing such a product. Additionally, the low fracture toughness of pure boron carbide may have resulted in historically lower transition velocities (the projectile velocity range at which armor begins to fail) than competing silicon carbide ceramics in high-velocity long-rod tungsten penetrator tests. Lower fracture toughness also limits multi-hit protection capability. Consequently, these requirements motivated research into methods for improving the densification and fracture toughness of inexpensive boron carbide composites that could result in the development of a superior armor material that would also be cost-competitive with other high-performance ceramics. The primary objective of this research was to study the effect of titanium and carbon additives on the sintering and mechanical properties of inexpensive B4C powders. The boron carbide powder examined in this study was a sub-micron (0.6 mum median particle size) boron carbide powder produced by H.C. Starck GmbH via a jet milling process. A carbon source in the form of phenolic resin, and titanium additives in the form of 32 nm and 0.9 mum TiO2 powders were selected. Parametric studies of sintering behavior were performed via high-temperature dilatometry in order to measure the in-situ sample contraction and thereby measure the influence of the additives and their amounts on the overall densification rate. Additionally, broad composition and sintering/post-HIPing studies followed by characterization and mechanical testing elucidated the effects of these additives on sample densification, microstructure de- velopment, and mechanical properties such as Vickers hardness and microindentation fracture toughness. Based upon this research, a process has been developed for the sintering of boron carbide that yielded end products with high relative densities (i.e., 100%, or theoretical density), microstructures with a fine (˜2-3 mum) grain size, and high Vickers microindentation hardness values. In addition to possessing these improved physical properties, the costs of producing this material were substantially lower (by a factor of 5 or more) than recently patented work on the pressureless sintering and post-HIPing of phase-pure boron carbide powder. This recently patented work developed out of our laboratory utilized an optimized powder distribution and yielded samples with high relative densities and high hardness values. The current work employed the use of titanium and carbon additives in specific ratios to activate the sintering of boron carbide powder possessing an approximately mono-modal particle size distribution. Upon heating to high temperatures, these additives produced fine-scale TiB2 and graphite inclusions that served to hinder grain growth and substantially improve overall sintered and post-HIPed densities when added in sufficient concentrations. The fine boron carbide grain size manifested as a result of these second phase inclusions caused a substantial increase in hardness; the highest hardness specimen yielded a hardness value (2884.5 kg/mm2) approaching that of phase-pure and theoretically-dense boron carbide (2939 kg/mm2). Additionally, the same high-hardness composition exhibited a noticeably higher fracture toughness (3.04 MPa˙m1/2) compared to phase-pure boron carbide (2.42 MPa˙m1/2), representing a 25.6% improvement. A potential consequence of this study would be the development of a superior armor material that is sufficiently affordable, allowing it to be incorporated into the general soldier's armor chassis.

Fiber laser welding of dual-phase galvanized sheet steel (DP590): traditional analysis and new quality assessment techniques

NASA Astrophysics Data System (ADS)

Miller, Stephanie; Pfeif, Erik; Kazakov, Andrei; Baumann, Esther; Dowell, Marla

2016-03-01

Laser welding has many advantages over traditional joining methods, yet remains underutilized. NIST has undertaken an ambitious initiative to improve predictions of weldability, reliability, and performance of laser welds. This study investigates butt welding of galvanized and ungalvanized dual-phase automotive sheet steels (DP 590) using a 10 kW commercial fiber laser system. Parameter development work, hardness profiles, microstructural characterization, and optical profilometry results are presented. Sound welding was accomplished in a laser power range of 2.0 kW to 4.5 kW and travel speed of 2000 mm/min to 5000 mm/min. Vickers hardness ranged from approximately 2 GPa to 4 GPa across the welds, with limited evidence of heat affected zone softening. Decreased hardness across the heat affected zone directly correlated to the appearance of ferrite. A technique was developed to non-destructively evaluate weld quality based on geometrical criteria. Weld face profilometry data were compared between light optical, metallographic sample, and frequency-modulated continuous-wave laser detection and ranging (FMCW LADAR) methods.

Structural, chemical and physical properties of pure and La3+ doped L-Threonine acetate crystals

NASA Astrophysics Data System (ADS)

Senthamizhan, A.; Sambathkumar, K.; Nithiyanantham, S.; Venkatachalapathy, M.; Rajkamal, N.

2017-12-01

The pure and La3+ doped L- Threonine crystals can be grown by slow evaporation techniques. The crystal structure were examined through X-Ray diffraction (XRD) analysis, confirmed the P212121 system. The quantitative nature of dopant can be analyzed with Inductively Coupled Plasma (ICP) study. The Fourier Transform Infra-Red (FTIR) and Fourier Transform (FT- Raman) investigations yields the possible stretching/bonding with their functional groups and the qualitative/quantitative nature of both crystals is analyzed. The optical behavior of crystals can be studied through Ultra Violet (UV) - Visible spectrometer. The mechanical, thermal and decomposition studies can be carried out through Vickers hardness test, Thermo Gravometric Analysis (TGA) and Differential Thermal Analysis (DTA). The Non Linear Optical (NLO) properties are found more than Potassium Phosphate (KDP) through Kurtz powders technique. The dielectric and optical absorption studies for both pure and L-doped crystals were studied and interpreted all the properties. The La3+ dopant increases the properties are investigated.

Microhardness evaluations of CAD/CAM ceramics irradiated with CO2 or Nd:YAP laser

PubMed Central

Rocca, Jean Paul; Fornaini, Carlo; Medioni, Etienne; Brulat-Bouchard, Nathalie

2017-01-01

Background and aims The aim of this study was to measure the microhardness values of irradiated computer-aided design/computer-aided manufacturing (CAD/CAM) ceramics surfaces before and after thermal treatment. Materials and Methods Sixty CAD/CAM ceramic discs were prepared and grouped by material, i.e. lithium disilicate ceramic (Emax CAD) and zirconia ceramic (Emax ZirCAD). Laser irradiation at the material surface was performed with a carbon dioxide laser at 5 Watt (W) or 10 W power in continuous mode (CW mode), or with a neodymium:yttrium aluminum perovskite (Nd:YAP) laser at 10 W on graphite and non-graphite surfaces. Vickers hardness was tested at 0.3 kgf for lithium disilicate and 1 kgf for zirconia. Results Emax CAD irradiated with CO2 at 5 W increased microhardness by 6.32 GPa whereas Emax ZirCAD irradiated with Nd:YAP decreased microhardness by 17.46 GPa. Conclusion CO2 laser effectively increases the microhardness of lithium disilicate ceramics (Emax CAD). PMID:28740324

Structural, optical, mechanical and dielectric studies of pure and doped L-Prolinium trichloroacetate single crystals.

PubMed

Renuka, N; Ramesh Babu, R; Vijayan, N; Vasanthakumar, Geetha; Krishna, Anuj; Ramamurthi, K

2015-02-25

In the present work, pure and metal substituted L-Prolinium trichloroacetate (LPTCA) single crystals were grown by slow evaporation method. The grown crystals were subjected to single crystal X-ray diffraction (XRD), powder X-ray diffraction, FTIR, UV-Visible-NIR, hardness, photoluminescence and dielectric studies. The dopant concentration in the crystals was measured by inductively coupled plasma (ICP) analysis. Single crystal X-ray diffraction studies of the pure and metal substituted LPTCA revealed that the grown crystals belong to the trigonal system. Ni(2+) and Co(2+) doping slightly altered the lattice parameters of LPTCA without affecting the basic structure of the crystal. FTIR spectral analysis confirms the presence of various functional groups in the grown crystals. The mechanical behavior of pure and doped crystals was analyzed by Vickers's microhardness test. The optical transmittance, dielectric and photoluminescence properties of the pure and doped crystals were analyzed. Copyright © 2014 Elsevier B.V. All rights reserved.

Validity of "sputtering and re-condensation" model in active screen cage plasma nitriding process

NASA Astrophysics Data System (ADS)

Saeed, A.; Khan, A. W.; Jan, F.; Abrar, M.; Khalid, M.; Zakaullah, M.

2013-05-01

The validity of "sputtering and re-condensation" model in active screen plasma nitriding for nitrogen mass transfer mechanism is investigated. The dominant species including NH, Fe-I, N2+, N-I and N2 along with Hα and Hβ lines are observed in the optical emission spectroscopy (OES) analysis. Active screen cage and dc plasma nitriding of AISI 316 stainless steel as function of treatment time is also investigated. The structure and phases composition of the nitrided layer is studied by X-ray diffraction (XRD). Surface morphology is studied by scanning electron microscopy (SEM) and hardness profile is obtained by Vicker's microhardness tester. Increasing trend in microhardness is observed in both cases but the increase in active screen plasma nitriding is about 3 times greater than that achieved by dc plasma nitriding. On the basis of metallurgical and OES observations the use of "sputtering and re-condensation" model in active screen plasma nitriding is tested.

Comparisons between TiO2- and SiO2-flux assisted TIG welding processes.

PubMed

Tseng, Kuang-Hung; Chen, Kuan-Lung

2012-08-01

This study investigates the effects of flux compounds on the weld shape, ferrite content, and hardness profile in the tungsten inert gas (TIG) welding of 6 mm-thick austenitic 316 L stainless steel plates, using TiO2 and SiO2 powders as the activated fluxes. The metallurgical characterizations of weld metal produced with the oxide powders were evaluated using ferritoscope, optical microscopy, and Vickers microhardness test. Under the same welding parameters, the penetration capability of TIG welding with TiO2 and SiO2 fluxes was approximately 240% and 292%, respectively. A plasma column made with SiO2 flux exhibited greater constriction than that made with TiO2 flux. In addition, an anode root made with SiO2 flux exhibited more condensation than that made with TiO2 flux. Results indicate that energy density of SiO2-flux assisted TIG welding is higher than that of TiO2-flux assisted TIG welding.

The effect of long-term disinfection procedures on hardness property of resin denture teeth.

PubMed

Campanha, Nara Hellen; Pavarina, Ana Cláudia; Jorge, Janaina Habib; Vergani, Carlos Eduardo; Machado, Ana Lucia; Giampaolo, Eunice Teresinha

2012-06-01

The aim of the study was to evaluate the effect of long-term disinfection procedures on the Vickers hardness (VHN) of acrylic resin denture teeth. Five acrylic resin denture teeth (Vipi Dent Plus-V, Trilux-T, Biolux-B, Postaris-P and Artiplus-A) and one composite resin denture teeth (SR-Orthosit-O) were embedded in heat-polymerised acrylic resin within polyvinylchloride tubes. Specimens were stored in distilled water at 37°C for 48 h. Measurements of hardness were taken after the following disinfection procedures: immersion for 7 days in 4% chlorhexidine gluconate or in 1% sodium hypochlorite (CIm and HIm group, respectively) and seven daily cycles of microwave sterilisation at 650 W for 6 min (MwS group). In the WIm group, specimens were maintained in water during the time used to perform the disinfection procedures (7 days). Data were analysed with anova followed by the Bonferroni procedure (α = 0.01). Microwave disinfection decreased the hardness of all acrylic resin denture teeth (p < 0.001). Immersion for 7 days in 4% chlorhexidine gluconate or distilled water had significant effect on the hardness of the acrylic resin denture teeth A (p < 0.01), and 1% sodium hypochlorite on teeth T (p < 0.01). All disinfection procedures decrease the hardness of the composite resin denture teeth (p < 0.01). Teeth O exhibited the highest and teeth V the lowest hardness values in the control group (p < 0.01). Disinfection procedures changed the hardness of resin denture teeth. © 2011 The Gerodontology Society and John Wiley & Sons A/S.

Mechanical properties of ZrB2- and HfB2-based ultra-high temperature ceramics fabricated by spark plasma sintering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zapata-Solvas, E.; Jayaseelan, D.; Lin, Hua-Tay

2013-01-01

Flexural strengths at room temperature, at 1400 C in air and at room temperature after 1 h oxidation at 1400 C were determined for ZrB2- and HfB2-based ultra-high temperature ceramics (UHTCs). Defects caused by electrical discharge machining (EDM) lowered measured strengths significantly and were used to calculate fracture toughness via a fracture mechanics approach. ZrB2 with 20 vol.% SiC had room temperature strength of 700 90 MPa, fracture toughness of 6.4 0.6 MPa, Vickers hardness at 9.8 N load of 21.1 0.6 GPa, 1400 C strength of 400 30 MPa and room temperature strength after 1 h oxidation at 1400more » C of 678 15 MPa with an oxide layer thickness of 45 5 m. HfB2 with 20 vol.% SiC showed room temperature strength of 620 50 MPa, fracture toughness of 5.0 0.4 MPa, Vickers hardness at 9.8 N load of 27.0 0.6 GPa, 1400 C strength of 590 150 MPa and room temperature strength after 1 h oxidation at 1400 C of 660 25 MPa with an oxide layer thickness of 12 1 m. 2 wt.% La2O3 addition to UHTCs slightly reduced mechanical performance while increasing tolerance to property degradation after oxidation and effectively aided internal stress relaxation during spark plasma sintering (SPS) cooling, as quantified by X-ray diffraction (XRD). Slow crack growth was suggested as the failure mechanism at high temperatures as a consequence of sharp cracks formation during oxidation.« less

A strategic approach to physico-chemical analysis of bis (thiourea) lead chloride - A reliable semi-organic nonlinear optical crystal

NASA Astrophysics Data System (ADS)

Rajagopalan, N. R.; Krishnamoorthy, P.; Jayamoorthy, K.

2017-03-01

Good quality crystals of bis thiourea lead chloride (BTLC) have been grown by slow evaporation method from aqueous solution. Orthorhombic structure and Pna21 space group of the crystals have been identified by single crystal X-ray diffraction. Studies on nucleation kinetics of grown BTLC has been carried out from which meta-stable zone width, induction period, free energy change, critical radius, critical number and growth rate have been calculated. The experimental values of interfacial surface energy for the crystal growth process have been compared with theoretical models. Ultra violet transmittance studies resulted in a high transmittance and wide band gap energy suggested the required optical transparency of the crystal. The second harmonic generation (SHG) and phase matching nature of the crystal have been justified by Kurtz-Perry method. The SHG nature of the crystal has been further attested by the higher values of theoretical hyper polarizability. The dielectric nature of the crystals at different temperatures with varying frequencies has been thoroughly studied. The activation energy values of the electrical process have been calculated from ac conductivity study. Solid state parameters including valence electron plasma energy, Penn gap, Fermi energy and polarisability have been unveiled by theoretical approach and correlated with the crystal's SHG efficiency. The values of hardness number, elastic stiffness constant, Meyer's Index, minimum level of indentation load, load dependent constant, fracture toughness, brittleness index and corrected hardness obtained from Vicker's hardness test clearly showed that the BTLC crystal has good mechanical stability required for NLO device fabrication.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Han, Lei; Wang, Shanmin; Zhu, Jinlong

Here, we report high-pressure synthesis of chromium monoboride (CrB) at 6 GPa and 1400 K. The elastic and plastic behaviors have been investigated by hydrostatic compression experiment and micro-indentation measurement. CrB is elastically incompressible with a high bulk modulus of 269.0 (5.9) GPa and exhibits a high Vickers hardness of 19.6 (0.7) GPa under the load of 1 kg force. Based on first principles calculations, the observed mechanical properties are attributed to the polar covalent Cr-B bonds interconnected with strong zigzag B-B covalent bonding network. The presence of metallic Cr bilayers is presumably responsible for the weakest paths in shearmore » deformation.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Han, Lei; College of Construction Engineering, Jilin University, Changchun, Jilin 130061; Wang, Shanmin

We report high-pressure synthesis of chromium monoboride (CrB) at 6 GPa and 1400 K. The elastic and plastic behaviors have been investigated by hydrostatic compression experiment and micro-indentation measurement. CrB is elastically incompressible with a high bulk modulus of 269.0 (5.9) GPa and exhibits a high Vickers hardness of 19.6 (0.7) GPa under the load of 1 kg force. Based on first principles calculations, the observed mechanical properties are attributed to the polar covalent Cr-B bonds interconnected with strong zigzag B-B covalent bonding network. The presence of metallic Cr bilayers is presumably responsible for the weakest paths in shear deformation.

Microhardness study of the nonlinear optical crystal L-arginine hydrochloride monohydrate

NASA Astrophysics Data System (ADS)

Mukerji, Sudeshna; Kar, Tanusree

2000-12-01

The results of measurement of the Vickers microhardness ( H v ) of the (100), (010), and (001) faces of the nonlinear optical (NLO) crystal L-arginine hydrochloride monohydrate (LAHCl) have been reported. It was observed that the microhardnesses of the three crystal planes decrease with the increase of applied load, and the hardness profile is different for different planes. The proportional specimen-resistance (PSR) model of Li and Bradt is used to explain the microhardness behavior of LAHCl. The indentation work-hardening coefficients ( n) for three planes were found to be greater than 1.8, and this indicates that LAHCl is a soft crystal.

Microstructure and Mechanical Properties of a Tempered High Cr Martensitic Steel

NASA Astrophysics Data System (ADS)

Guerra-Fuentes, L.; Hernandez-Rodriguez, M. A. L.; Zambrano-Robledo, P.; Salinas-Rodriguez, A.; Garcia-Sanchez, E.

2017-07-01

Microstructural and mechanical studies have been performed in a high Cr martensitic steel Firth-Vickers (FV535) to analyze the tempering of martensite. Nanoindentation technique was used to determine the hardness and elastic modulus through systematic measurements on martensite and tempered martensite. On the other hand, microscopic studies were carried out to analyze the material in the same condition as received and subsequently observe the microstructural modifications after heat treatment. The precipitation presented in the last stage of tempering was observed by transmission electron microscopy. The results showed the effect of the martensite decomposition on the mechanical and nanomechanical properties of FV535.

Bulk superhard B-C-N nanocomposite compact and method for preparing thereof

DOEpatents

Zhao, Yusheng; He, Duanwei

2004-07-06

Bulk, superhard, B-C-N nanocomposite compact and method for preparing thereof. The bulk, superhard, nanocomposite compact is a well-sintered compact and includes nanocrystalline grains of at least one high-pressure phase of B-C-N surrounded by amorphous diamond-like carbon grain boundaries. The bulk compact has a Vicker's hardness of about 41-68 GPa. It is prepared by ball milling a mixture of graphite and hexagonal boron nitride, encapsulating the ball-milled mixture, and sintering the encapsulated ball-milled mixture at a pressure of about 5-25 GPa and at a temperature of about 1000-2500 K.

Resolving the structure and properties of τ1-Cr-Ni-Al for high temperature protective applications

NASA Astrophysics Data System (ADS)

Simonson, J. W.; Nicasio, J. E.; Ilyas, H.; Pabla, J.; Horvat, K.; Misuraca, J. C.

Increasing the temperature of the steam in turbine power plants enhances thermal efficiency while reducing CO2 emissions. Exposed steel components, however, must be coated to withstand the harsh environments present in next-generation advanced ultra-supercritical plants. Proposed coating materials must exhibit low density, high hardness, high toughness, excellent oxidation resistance, and low thermal conductivity. With an eye towards satisfying this diverse array of requirements, we report the properties of the so-called τ1 phase of Cr-Ni-Al. We resolve the previously controversial composition and crystal structure of this material. The complex structure is composed of distorted icosahedra and octahedra of Al, with nearest-neighbor transition metal-Al bond lengths as short as 2.4 Å, far shorter than typical distances in Ni-Al and Cr-Al binaries. Accordingly, Vickers hardness is 6 . 88 +/- 0 . 13 GPa, as hard as extra-high-hardness armor plating at only 45% the density. We discuss these properties in light of the result of transport and oxidation resistance measurements. The apparent dependencies of these properties on crystal structure suggests new criteria for materials research. Acknowledgment is made to the Donors of the American Chemical Society Petroleum Research Fund, for support of this research under contract 56764-UNI10.

Effects of Sterilization Cycles on PEEK for Medical Device Application

PubMed Central

Yap, Wai Teng; Foo, Soo Leong; Lee, Teck Kheng

2018-01-01

The effects of the sterilization process have been studied on medical grade thermoplastic polyetheretherketone (PEEK). For a reusable medical device, material reliability is an important parameter to decide its lifetime, as it will be subjected to the continuous steam sterilization process. A spring nature, clip component was selected out of a newly designed medical device (patented) to perform this reliability study. This clip component was sterilized for a predetermined number of cycles (2, 4, 6, 8, 10, 20…100) at 121 °C for 30 min. A significant decrease of ~20% in the compression force of the spring was observed after 30 cycles, and a ~6% decrease in the lateral dimension of the clip was observed after 50 cycles. No further significant change in the compression force or dimension was observed for the subsequent sterilization cycles. Vickers hardness and differential scanning calorimetry (DSC) techniques were used to characterize the effects of sterilization. DSC results exhibited no significant change in the degree of cure and melting behavior of PEEK before and after the sterilization. Hardness measurement exhibited an increase of ~49% in hardness after just 20 cycles. When an unsterilized sample was heated for repetitive cycles without the presence of moisture (121 °C, 10 and 20 cycles), only ~7% of the maximum change in hardness was observed. PMID:29466289

Tribological Characteristics of Submicron SiC(p)-GR(p)/Zn-35Al-1Mg Composites in Semisolidification Casting process

NASA Astrophysics Data System (ADS)

Liu, S.; Fang, Z. W.; Li, L. X.

2018-05-01

Uniform SiC(p)-GR(p)/Zn-35Al-1Mg composites were prepared by powder pressing and semisolidification stirring-casting process by adding submicron silicon carbide and graphite reinforcement particles in an aluminum-zinc alloy matrix. Micro Vickers hardness and microstructures of the novel composites were studied, and their wear properties and wear temperature were measured for different load and friction conditions. The results show that silicon carbide and graphite particles homogeneously mix in the matrix, while contained silicon carbide particles improve the matrix hardness to 8.4%, graphite improves the matrix hardness to 16.8%, but two of them, combined, reduce the matrix hardness to 7.6%; the rate of temperature rise of the zinc-aluminum matrix alloy is the highest than the other three composites and is up to 48.5° C/s at 1.69MPa. At 0.56MPa and sliding 26.4km, the graphite composite anti-wear effect is optimal, while at 1.13MPa, the wear resistance of silicon carbide and graphite compound particles is the best; in the other case of only silicon carbide particles, the wear resistance is increased to 35% at 1.69MPa and 26.4km, and its anti-wear effects are excellent.

Effects of Sterilization Cycles on PEEK for Medical Device Application.

PubMed

Kumar, Amit; Yap, Wai Teng; Foo, Soo Leong; Lee, Teck Kheng

2018-02-21

The effects of the sterilization process have been studied on medical grade thermoplastic polyetheretherketone (PEEK). For a reusable medical device, material reliability is an important parameter to decide its lifetime, as it will be subjected to the continuous steam sterilization process. A spring nature, clip component was selected out of a newly designed medical device (patented) to perform this reliability study. This clip component was sterilized for a predetermined number of cycles (2, 4, 6, 8, 10, 20…100) at 121 °C for 30 min. A significant decrease of ~20% in the compression force of the spring was observed after 30 cycles, and a ~6% decrease in the lateral dimension of the clip was observed after 50 cycles. No further significant change in the compression force or dimension was observed for the subsequent sterilization cycles. Vickers hardness and differential scanning calorimetry (DSC) techniques were used to characterize the effects of sterilization. DSC results exhibited no significant change in the degree of cure and melting behavior of PEEK before and after the sterilization. Hardness measurement exhibited an increase of ~49% in hardness after just 20 cycles. When an unsterilized sample was heated for repetitive cycles without the presence of moisture (121 °C, 10 and 20 cycles), only ~7% of the maximum change in hardness was observed.

Mechanical properties and internal fit of 4 CAD-CAM block materials.

PubMed

Goujat, Alexis; Abouelleil, Hazem; Colon, Pierre; Jeannin, Christophe; Pradelle, Nelly; Seux, Dominique; Grosgogeat, Brigitte

2018-03-01

Recent polymer-based computer-assisted design and computer-assisted manufacturing (CAD-CAM) materials have been commercialized for inlay restorations, a polymer-infiltrated ceramic-network (PICN) and composite resin nanoceramics. Little independent evidence regarding their mechanical properties exists. Internal adaptation is an important factor for the clinical success and longevity of a restoration, and data concerning this parameter for inlays made with these blocks are scarce. The purpose of this in vitro study was to evaluate and compare the mechanical properties (flexural strength, flexural modulus, Vickers hardness, fracture toughness) and the internal adaptation of these recent polymer-based blocks with a lithium disilicate glass-ceramic block. The materials tested in this study were a PICN material (Vita Enamic), 2 composite resin nanoceramics (Lava Ultimate; 3M ESPE and Cerasmart; GCDental Products), and a lithium disilicate glass-ceramic (IPS e.max CAD). Mechanical properties were evaluated according to ISO norm DIS 6872:2013. Bar-shaped specimens (18×3×3 mm) were prepared and submitted to a 3-point bend test using a universal testing machine at a cross-head speed of 0.5 mm/min. In addition, identical cavities were prepared in 60 human mandibular extracted molars (n=15) and optically scanned to receive mesioocclusodistal inlays milled with the 4 materials tested in a CEREC Inlab milling machine. The replica technique and a stereomicroscope (×20) were used to measure the internal fit of the inlays at 9 preselected locations. All data were statistically analyzed using 1-way ANOVA and the post hoc Tukey multiple comparison or Games-Howell test (α=.05). The mean flexural strength of the tested blocks ranged from 148.7 ±9.5 MPa (Vita Enamic) to 216.5 ±28.3 MPa (Cerasmart). The mean flexural modulus ranged from 23.3 ±6.4 GPa (Vita Enamic) to 52.8 ±10.5 GPa (IPS e.max CAD). The mean Vickers hardness ranged from 0.66 ±0.02 GPa (Cerasmart) to 5.98 ±0.69 GPa (IPS e.max CAD). The mean fracture toughness ranged from 1.2 ±0.17 MPa.m 1/2 (Cerasmart) to 1.8 ±0.29 MPa.m 1/2 (IPS e.max CAD). The values for internal discrepancy ranged from 119 ±55 μm to 234 ±51 μm. The mean internal discrepancy was significantly higher for Lava Ultimate (P<.05) than IPS e.max CAD and Cerasmart but not for Vita Enamic. The factor ''material'' was statistically significant in relation to the mechanical properties evaluated in this study (P<.05). The Pearson correlation was negative between the flexural strength results and the internal discrepancy of the materials tested (R 2 =0.941; P<.05). The mechanical properties of the CAD-CAM block materials tested were within the acceptable range for fabrication of single restorations according to the ISO standard for ceramics (ISO 6872:2008). IPS e.max CAD and Cerasmart were observed to have superior flexural strength and better internal fit. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Synthesis and statistical modelling of dry sliding wear of Al 8011/6 vol.% AlB2 in situ composite

NASA Astrophysics Data System (ADS)

Kumar, Narendra; Singh, Sandeep Kumar; Gautam, Gaurav; Padap, Aditya Kumar; Mohan, Anita; Mohan, Sunil

2017-10-01

The present study has used response surface methodology (RSM) and central composite design (CCD) for modelling, using wear parameters to predict the wear performance of an Al 8011/6.0 vol.% AlB2 composite. The effect of applied load and sliding velocity was studied at five levels for a fixed sliding distance. To understand wear behaviour, sliding wear tests were planned according to CCD and performed on a pin-on-disc apparatus at ambient temperature. An analysis of variance (ANOVA) was conducted to show the relative significance of the parameters. A second-order regression model was developed to predict the wear loss and to establish the relationships between wear parameters. Response surface and contour plots were drawn to analyse the wear results. Worn surfaces were examined under scanning electron microscope (SEM), and energy dispersive spectroscopy (EDS) was used to interpret the operative wear mechanisms. Validation tests results show good agreement between experimental and predicted data. As an initial step of this study, AlB2 particles were reinforced in Al 8011 alloy by an in situ technique to synthesise an Al 8011/6.0 vol.% AlB2 composite. During synthesis an in situ reaction takes place between molten alloy and inorganic salt KBF4 at 850 °C, which leads to the formation of AlB2 particles. The composite was analysed by x-ray diffractometer (XRD) to detect the phases present, while optical and scanning electron microscopy (OM & SEM) were carried out to ascertain morphology and particle distribution. Hardness was evaluated by a Vickers hardness testing machine.

Effect of Metal Ion Etching on the Tribological, Mechanical and Microstructural Properties of TiN-COATED d2 Tool Steel Using Cae Pvd Technique

NASA Astrophysics Data System (ADS)

Ali, Mubarak; Hamzah, Esah Binti; Hj. Mohd Toff, Mohd Radzi

A study has been made on TiN coatings deposited on D2 tool steel substrates by using commercially available cathodic arc evaporation, physical vapor deposition technique. The goal of this work is to determine the usefulness of TiN coatings in order to improve the micro-Vickers hardness, coefficient of friction and surface roughness of TiN coating deposited on tool steel, which is vastly use in tool industry for various applications. A pin-on-disc test was carried out to study the coefficient of friction versus sliding distance of TiN coating at various ion etching rates. The tribo-test showed that the minimum value recorded for friction coefficient was 0.386 and 0.472 with standard deviation of 0.056 and 0.036 for the coatings deposited at zero and 16 min ion etching. The differences in friction coefficient and surface roughness was mainly associated with the macrodroplets, which was produced during etching stage. The coating deposited for 16 min metal ion etching showed the maximum hardness, i.e., about five times higher than uncoated one and 1.24 times to the coating deposited at zero ion etching. After friction test, the wear track was observed by using field emission scanning electron microscope. The coating deposited for zero ion etching showed small amounts of macrodroplets as compared to the coating deposited for 16 min ion etching. The elemental composition on the wear scar were investigated by means of energy dispersive X-ray, indicate no further TiN coating on wear track. A considerable improvement in TiN coatings was recorded as a function of various ion etching rates.

Light weight and high strength materials made of recycled steel and aluminum

NASA Astrophysics Data System (ADS)

Nounezi, Thomas

Recycling has proven not only to address today's economical, environmental and social issues, but also to be imperative for the sustainability of human technology. The current thesis has investigated the feasibility of a new philosophy for Recycling (Alloying-Recycling) using steel 1020 and aluminum 6061T6. The study was limited to the metallurgical aspects only and has highlighted the potential of recycled alloys made of recycled aluminum and steel to exhibit substantially increased wear resistance and strength-to-weight ratio as compared to initial primary materials. Three alloy-mixtures are considered: TN3 (5wt% 1020 +95wt% 6061T6); TN5 (0.7wt% 1020 + 99.3wt% 6061T6); and TN4 (10wt% 6061T6 + 90wt% 1020). A Tucker induction power supply system (3kW; 135-400 kHz) is used to melt the alloy mixtures for casting in graphite crucibles. Heat treatment of the cast samples is done using a radiation box furnace. Microscopy, Vickers hardness and pin-on-disc abrasive wear tests are performed. Casting destroyed the initial microstructures of the alloys leading to a hardness reduction in the as-cast and solution heat-treated aluminum rich samples to 60 Hv from 140 Hv. Ageing slightly increased the hardness of the cast samples and provided a wear resistance two times higher than that of the initial 6061T6 material. On the steel rich side, the hardness of the as-cast TN4 was 480 Hv, which is more than twice as high as the initial hardness of steel 1020 of 202 Hv; this hints to strong internal and residual stress, probably martensite formation during fast cooling following casting. Solution heat treatment lowered the hardness to the original value of steel 1020, but provided about ten (10) times higher wear resistance; this suggests higher ductility and toughness of normalised TN4 as compared to 1020. In addition, TN4 exhibits about 25% weight reduction as compared to 1020. The actual recycling process and the effect of non-metallic impurities shall be investigated in future works. Also, the casting and heat treatment processes need to be improved.

Structure-property relationships of iron-hydroxyapatite ceramic matrix nanocomposite fabricated using mechanosynthesis method.

PubMed

Nordin, Jamillah Amer; Prajitno, Djoko Hadi; Saidin, Syafiqah; Nur, Hadi; Hermawan, Hendra

2015-06-01

Hydroxyapatite (HAp) is an attractive bioceramics due to its similar composition to bone mineral and its ability to promote bone-implant interaction. However, its low strength has limited its application as load bearing implants. This paper presented a work focusing on the improvement of HAp mechanical property by synthesizing iron (Fe)-reinforced bovine HAp nanocomposite powders via mechanosynthesis method. The synthesis process was performed using high energy milling at varied milling time (3, 6, 9, and 12h). The samples were characterized by X-ray diffraction (XRD), Fourier transform infrared (FT-IR), and scanning electron microscopy (SEM). Its mechanical properties were investigated by micro-Vicker's hardness and compression tests. Results showed that milling time directly influenced the characteristics of the nanocomposite powders. Amorphous BHAp was formed after 9 and 12h milling in the presence of HPO4(2-) ions. Continuous milling has improved the crystallinity of Fe without changing the HAp lattice structure. The nanocomposite powders were found in spherical shape, agglomerated and dense after longer milling time. The hardness and Young's modulus of the nanocomposites were also increased at 69% and 66%, respectively, as the milling time was prolonged from 3 to 12h. Therefore, the improvement of the mechanical properties of nanocomposite was attributed to high Fe crystallinity and homogenous, dense structure produced by mechanosynthesis. Copyright © 2015 Elsevier B.V. All rights reserved.

Fabrication of optical element from unidirectional grown imidazole-imidazolium picrate monohydrate (IIP) organic crystals for nonlinear optical applications

NASA Astrophysics Data System (ADS)

Vivek, P.; Murugakoothan, P.

2014-12-01

Nonlinear optical bulk single crystal of Imidazole-imidazolium picrate monohydrate (IIP) has been grown by Sankaranarayanan-Ramasamy (SR) method using acetonitrile as solvent. First time we report the bulk growth of IIP crystal by SR method. The transparent IIP single crystal of maximum diameter 21 mm and length 46 mm was obtained by employing SR method. The grown crystal was subjected to high resolution X-ray diffraction, UV-vis-NIR transmittance, refractive index, hardness, dielectric and laser damage threshold studies. The crystalline perfection of the grown crystal was analyzed using HRXRD. Cut off wavelength and optical transmission window of the crystal was assessed by UV-vis-NIR and the refractive index of the crystal was found. The mechanical property of the crystal was estimated by Vicker's hardness test. The dielectric property of the crystal was measured as a function of frequency. The laser damage threshold value was determined. The particle size dependent second harmonic generation efficiency for IIP was evaluated with standard reference material potassium dihydrogen phosphate (KDP) by Kurtz-Perry powder method using Nd:YAG laser, which established the existence of phase matching. The second harmonic generation (SHG) of IIP crystal was investigated by the SHG Maker fringes technique. The mechanism of growth is revealed by carrying out chemical etching using acetonitrile as etchant.

Constitutive model of friction stir weld with consideration of its inhomogeneous mechanical properties

NASA Astrophysics Data System (ADS)

Zhang, Ling; Min, Junying; Wang, Bin; Lin, Jianping; Li, Fangfang; Liu, Jing

2016-03-01

In practical engineering, finite element(FE) modeling for weld seam is commonly simplified by neglecting its inhomogeneous mechanical properties. This will cause a significant loss in accuracy of FE forming analysis, in particular, for friction stir welded(FSW) blanks due to the large width and good formability of its weld seam. The inhomogeneous mechanical properties across weld seam need to be well characterized for an accurate FE analysis. Based on a similar AA5182 FSW blank, the metallographic observation and micro-Vickers hardness analysis upon the weld cross-section are performed to identify the interfaces of different sub-zones, i.e., heat affected zone(HAZ), thermal-mechanically affected zone(TMAZ) and weld nugget(WN). Based on the rule of mixture and hardness distribution, a constitutive model is established for each sub-zone to characterize the inhomogeneous mechanical properties across the weld seam. Uniaxial tensile tests of the AA5182 FSW blank are performed with the aid of digital image correlation(DIC) techniques. Experimental local stress-strain curves are obtained for different weld sub-zones. The experimental results show good agreement with those derived from the constitutive models, which demonstrates the feasibility and accuracy of these models. The proposed research gives an accurate characterization of inhomogeneous mechanical properties across the weld seam produced by FSW, which provides solutions for improving the FE simulation accuracy of FSW sheet forming.

Friction and wear properties of high-velocity oxygen fuel sprayed WC-17Co coating under rotational fretting conditions

NASA Astrophysics Data System (ADS)

Luo, Jun; Cai, Zhenbing; Mo, Jiliang; Peng, Jinfang; Zhu, Minhao

2016-05-01

Rotational fretting which exist in many engineering applications has incurred enormous economic loss. Thus, accessible methods are urgently needed to alleviate or eliminate damage by rotational fretting. Surface engineering is an effective approach that is successfully adopted to enhance the ability of components to resist the fretting damage. In this paper, using a high-velocity oxygen fuel sprayed (HVOF) technique WC-17Co coating is deposited on an LZ50 steel surface to study its properties through Vickers hardness testing, scanning electric microscope (SEM), energy dispersive X-ray spectroscopy (EDX), and X-ray diffractrometry (XRD). Rotational fretting wear tests are conducted under normal load varied from 10 N to 50 N, and angular displacement amplitudes vary from 0.125° to 1°. Wear scars are examined using SEM, EDX, optical microscopy (OM), and surface topography. The experimental results reveal that the WC-17Co coating adjusted the boundary between the partial slip regime (PSR) and the slip regime (SR) to the direction of smaller amplitude displacement. As a result, the coefficients of friction are consistently lower than the substrate's coefficients of friction both in the PSR and SR. The damage to the coating in the PSR is very slight. In the SR, the coating exhibits higher debris removal efficiency and load-carrying capacity. The bulge is not found for the coating due to the coating's higher hardness to restrain plastic flow. This research could provide experimental bases for promoting industrial application of WC-17Co coating in prevention of rotational fretting wear.

Laser beam welding of Waspaloy: Characterization and corrosion behavior evaluation

NASA Astrophysics Data System (ADS)

Shoja Razavi, Reza

2016-08-01

In this work, a study on Nd:YAG laser welding of Waspaloy sheets has been made. Microstructures, phase changes and hardness of the laser joint were investigated using optical microscopy, scanning electron microscopy (SEM), field emission scanning electron microscopy (FESEM), energy dispersive spectroscopy (EDS), X-ray diffraction analysis (XRD) and vickers microhardness (HV0.3). Corrosion behavior of the weldment at low temperature in 3.5%wt NaCl solution at room temperature was also investigated using open circuit potential and cyclic potentiodynamic polarization tests. Hot corrosion studies were conducted on samples in the molten salt environment (Na2SO4-60%V2O5) at 900 °C for 50 h. Results indicated that the microstructure of weld zone was mainly dendritic grown epitaxially in the direction perpendicular to the weld boundary and heat transfer. Moreover, the Ti-Mo carbide particles were observed in the structure of the weld zone and base metal. The average size of carbides formed in the base metal (2.97±0.5 μm) was larger than that of the weld zone (0.95±0.2 μm). XRD patterns of the weld zone and base metal showed that the laser welding did not alter the phase structure of the weld zone, being in γ-Ni(Cr) single phase. Microhardness profile showed that the hardness values of the weld zone (210-261 HV) were lower than that of the base metal (323-330 HV). Electrochemical and hot corrosion tests indicated that the corrosion resistance of the weld metal was greater than the base metal in both room and high temperatures.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bandriyana,, E-mail: bandri@batan.go.id; Ismoyo, Agus Hadi; Dimyati, A.

Surface treatment by implantation with nitrogen-ion was performed on the commercial feritic high strength steel AISI 410 which is termed for high temperature applications. The aim of this research was focused on the surface modification to improve its high temperature oxidation property in the early stages. Ion implantation was carried out at acceleration energy of 100 KeV and ion current 10 mA for 30, 60 and 90 minutes. The samples were subjected to the high temperature oxidation test by means of thermogravimetry in a magnetic suspension balance (MSB) at 500 °C for 5 hours. The scanning electron microscopy (SEM), X-ray diffractionmore » spectrometry (XRD) and Vickers Hardness measurement were used for sample characterization. The formation of ferro-nitride phase after implantation did not occur, however a thin layer considered to contain nitrogen interstitials was detected. The oxidation of both samples before and after implantation followed parabolic kinetics indicating inward growth of oxide scale characteristically due to diffusion of oxygen anions towards matrix surface. After oxidation test relativelly stable oxide scales were observed. Oxidation rates decreased proportionally with the increasing of implantation time due to the formation of oxide layer which is considered to be effectiv inhibitor for the oxygen diffusion.« less

Characterization and study of mechanical and tribological properties on titanium di oxide (TiO2) coated 304L stainless steel

NASA Astrophysics Data System (ADS)

Ghanaraja, S.; Ali, Syed Imran; Ravikumar, K. S.; Likith, P.

2018-04-01

In the present investigation Atmospheric Plasma Spraying (APS) method is selected for coating the materials on 304L Stainless Steel as a substrate material, also called as substrate of Thermal Barrier Coating (TBC) system developed in the present work. Commercially available Ni-Cr metal powder is selected for bond coat and TiO2 powder is selected for Top Coat. The thickness of bond coat is taken as 75 µm where as the top coat thickness is varied as 100 µm, 200 µm and 300 µm. In plasma sprayed coating more attention is given to obtain uniform thickness on the given substrate. The various surface texture parameters of each sample is tested, morphology and coating thickness of above TBC system are studied with the help of SEM and X-Ray Diffraction for phase analysis. Micro-hardness of each layer of coating is measured by using Vicker's diamond indentation and the abrasive wear resistance of each system has been investigated through Pin-on-disc test, at room temperature by using wear and friction tribometer. The coating system possesses good wear resistance and can be used in various applications.

The effect of different beverages on surface hardness of nanohybrid resin composite and giomer.

PubMed

Tanthanuch, Saijai; Kukiattrakoon, Boonlert; Siriporananon, Chantima; Ornprasert, Nawanda; Mettasitthikorn, Wathu; Likhitpreeda, Salinla; Waewsanga, Sulawan

2014-05-01

To investigate the effects of five beverages (apple cider, orange juice, Coca-Cola, coffee, and beer) on microhardness and surface characteristic changes of nanohybrid resin composite and giomer. Ninety-three specimens of each resin composite and giomer were prepared. Before immersion, baseline data of Vicker's microhardness was recorded and surface characteristics were examined using scanning electron microscopy (SEM). Five groups of discs (n = 18) were alternately immersed in 25 mL of each beverage for 5 s and in 25 mL of artificial saliva for 5 s for 10 cycles. Specimens were then stored in artificial saliva for 24 h. This process was repeated for 28 days. After immersion, specimens were evaluated and data were analyzed by two-way repeated analysis of variance (ANOVA), Tukey's honestly significant difference (HSD), and a t-test (α = 0.05). Microhardness of all groups significantly decreased after being immersed in the tested beverages (P < 0.05). SEM photomicrographs presented surface degradation of all groups. The effect of these beverages on the surface of both restorative materials also depended upon the exposure time and chemical composition of the restorative materials and beverages.

The effect of different beverages on surface hardness of nanohybrid resin composite and giomer

PubMed Central

Tanthanuch, Saijai; Kukiattrakoon, Boonlert; Siriporananon, Chantima; Ornprasert, Nawanda; Mettasitthikorn, Wathu; Likhitpreeda, Salinla; Waewsanga, Sulawan

2014-01-01

Aims: To investigate the effects of five beverages (apple cider, orange juice, Coca-Cola, coffee, and beer) on microhardness and surface characteristic changes of nanohybrid resin composite and giomer. Materials and Methods: Ninety-three specimens of each resin composite and giomer were prepared. Before immersion, baseline data of Vicker's microhardness was recorded and surface characteristics were examined using scanning electron microscopy (SEM). Five groups of discs (n = 18) were alternately immersed in 25 mL of each beverage for 5 s and in 25 mL of artificial saliva for 5 s for 10 cycles. Specimens were then stored in artificial saliva for 24 h. This process was repeated for 28 days. After immersion, specimens were evaluated and data were analyzed by two-way repeated analysis of variance (ANOVA), Tukey's honestly significant difference (HSD), and a t-test (α = 0.05). Results: Microhardness of all groups significantly decreased after being immersed in the tested beverages (P < 0.05). SEM photomicrographs presented surface degradation of all groups. Conclusions: The effect of these beverages on the surface of both restorative materials also depended upon the exposure time and chemical composition of the restorative materials and beverages. PMID:24944451

In vivo rehardening of enamel eroded by a cola drink.

PubMed

Kim, J W; Jang, K T; Lee, S H; Kim, C C; Hahn, S H; García-Godoy, F

2001-01-01

There are many concerns about the erosive effects of acidic beverages. In this study, the effects of Pepsi-Cola (pH 2.41) on bovine enamel and the rehardening effect resulting from intraoral exposure of the teeth were determined by microhardness testing (Vicker's Hardness Number). Bovine enamel specimens (VHN 380.00 +/- 12.74) were immersed in 100 ml of Pepsi-Cola for five minutes and subsequently exposed to human intraoral environment through the use of a removable resin plate. Microhardness testing was performed on specimens after one hour, twenty-four hours and forty-eight hours of exposure to an intraoral environment. The microhardness value was significantly (p < 0.05) reduced by the cola beverage (VHN 262.13 +/- 20.34), and significantly (p < 0.05) increased after intraoral exposure for one hour (VHN 299.75 +/- 26.86) and twenty-four hours (VHN 328.00 +/- 18.70). The difference in the microhardness between the twenty-four-hour group and the forty-eight-hour group (VHN 333.50 +/- 15.13) was not significant (p > 0.05). The microhardness value of the forty-eight-hour group was significantly less than the values recorded during the initial pre-study measurements p < 0.05).

In vivo surface analysis of titanium and stainless steel miniplates and screws.

PubMed

Matthew, I R; Frame, J W; Browne, R M; Millar, B G

1996-12-01

This study was undertaken to characterize the surfaces of Champy titanium and stainless steel miniplates and screws that had been used to stabilize fractures of the mandible in an animal model. Miniplates and screws were retrieved at 4, 12, and 24 weeks after surgery. Low-vacuum scanning electron microscopy (SEM) of autoclaved unused (control) and test miniplates from the same production batches was undertaken. Energy-dispersive X-ray (EDX) analysis was used to identify compositional variations of the miniplate surface, and Vickers hardness testing was performed. At autopsy, clinical healing of all fractures was noted. SEM analysis indicated no perceptible difference in the surface characteristics of the miniplates at all time intervals. Aluminium and silicon deposits were identified by EDX analysis over the flat surfaces. There was extensive damage to some screw heads. It is concluded that there were no significant changes in the surface characteristics of miniplates retrieved up to 24 weeks after implantation in comparison with controls. Damage to the screws during insertion due to softness of the materials may render their removal difficult. There was no evidence to support the routine removal of titanium or stainless steel miniplates because of surface corrosion up to 6 months after implantation.

Analyses of the Erosive Effect of Dietary Substances and Medications on Deciduous Teeth

PubMed Central

Lussi, Adrian; Carvalho, Thiago Saads

2015-01-01

This study aimed at analysing the erosive potential of 30 substances (drinks, candies, and medicaments) on deciduous enamel, and analyse the associated chemical factors with enamel dissolution. We analysed the initial pH, titratable acidity (TA) to pH 5.5, calcium (Ca), inorganic phosphate (Pi), and fluoride (F) concentration, and degree of saturation ((pK -pI)HAP, (pK -pI)FAP, and (pK−pI)CaF2) of all substances. Then, we randomly distributed 300 specimens of human deciduous enamel into 30 groups (n = 10 for each of the substances tested. We also prepared 20 specimens of permanent enamel for the sake of comparison between the two types of teeth, and we tested them in mineral water and Coca-Cola®. In all specimens, we measured surface hardness (VHN: Vickers hardness numbers) and surface reflection intensity (SRI) at baseline (SHbaseline and SRIbaseline), after a total of 2 min (SH2min) and after 4 min (SH4min and SRI4min) erosive challenges (60 ml of substance for 6 enamel samples; 30°C, under constant agitation at 95 rpm). There was no significant difference in SHbaseline between deciduous and permanent enamel. Comparing both teeth, we observed that after the first erosive challenge with Coca-Cola®, a significantly greater hardness loss was seen in deciduous (−90.2±11.3 VHN) than in permanent enamel (−44.3±12.2 VHN; p = 0.007), but no differences between the two types of teeth were observed after two challenges (SH4min). After both erosive challenges, all substances except for mineral water caused a significant loss in relative surface reflectivity intensity, and most substances caused a significant loss in surface hardness. Multiple regression analyses showed that pH, TA and Ca concentration play a significant role in initial erosion of deciduous enamel. We conclude that drinks, foodstuffs and medications commonly consumed by children can cause erosion of deciduous teeth and erosion is mainly associated with pH, titratable acidity and calcium concentration in the solution. PMID:26700481

Analyses of the Erosive Effect of Dietary Substances and Medications on Deciduous Teeth.

PubMed

Lussi, Adrian; Carvalho, Thiago Saads

2015-01-01

This study aimed at analysing the erosive potential of 30 substances (drinks, candies, and medicaments) on deciduous enamel, and analyse the associated chemical factors with enamel dissolution. We analysed the initial pH, titratable acidity (TA) to pH 5.5, calcium (Ca), inorganic phosphate (Pi), and fluoride (F) concentration, and degree of saturation ((pK -pI)HAP, (pK -pI)FAP, and (pK-pI)CaF2) of all substances. Then, we randomly distributed 300 specimens of human deciduous enamel into 30 groups (n = 10 for each of the substances tested. We also prepared 20 specimens of permanent enamel for the sake of comparison between the two types of teeth, and we tested them in mineral water and Coca-Cola®. In all specimens, we measured surface hardness (VHN: Vickers hardness numbers) and surface reflection intensity (SRI) at baseline (SH baseline and SRI baseline), after a total of 2 min (SH2 min) and after 4 min (SH4 min and SRI4 min) erosive challenges (60 ml of substance for 6 enamel samples; 30°C, under constant agitation at 95 rpm). There was no significant difference in SH baseline between deciduous and permanent enamel. Comparing both teeth, we observed that after the first erosive challenge with Coca-Cola®, a significantly greater hardness loss was seen in deciduous (-90.2 ± 11.3 VHN) than in permanent enamel (-44.3 ± 12.2 VHN; p = 0.007), but no differences between the two types of teeth were observed after two challenges (SH4 min). After both erosive challenges, all substances except for mineral water caused a significant loss in relative surface reflectivity intensity, and most substances caused a significant loss in surface hardness. Multiple regression analyses showed that pH, TA and Ca concentration play a significant role in initial erosion of deciduous enamel. We conclude that drinks, foodstuffs and medications commonly consumed by children can cause erosion of deciduous teeth and erosion is mainly associated with pH, titratable acidity and calcium concentration in the solution.

Influence of M-TIG and A-TIG Welding Process on Microstructure and Mechanical Behavior of 409 Ferritic Stainless Steel

NASA Astrophysics Data System (ADS)

Vidyarthy, R. S.; Dwivedi, D. K.; Vasudevan, M.

2017-03-01

The current study investigates the effects of activating flux tungsten inert gas welding (A-TIG) and multipass tungsten inert gas welding (M-TIG) on the weld morphology, angular distortion, microstructures and mechanical properties when welding 8-mm-thick 409 ferritic stainless steel (FSS). SiO2 was used as activating flux for A-TIG welding, while SUPERTIG ER309L was used as filler for M-TIG welding. Bead-on-plate weld trials were carried out to obtain the full penetration by using different combinations of flux coating density, welding speed and welding current. An optical microscope, field emission scanning microscope (FESEM), and x-ray diffractometer were used for the metallurgical characterizations. Vickers hardness, tensile test, Charpy toughness test, and creep behavior test were carried out to evaluate the mechanical properties of the base and weld metals. Experimental results indicate that the A-TIG process can increase the joint penetration and tends to reduce the angular distortion of the 409 FSS weldment. The A-TIG welded joint also exhibited greater mechanical strength. However, a critically low Charpy toughness was measured for the A-TIG weld fusion zone, which was later sufficiently improved after post weld heat treatment (PWHT). It was concluded that PWHT is mandatory for A-TIG welded 409 FSS.

Wear Behavior and Microstructure of Mg-Sn Alloy Processed by Equal Channel Angular Extrusion

PubMed Central

Chen, Jung-Hsuan; Shen, Yen-Chen; Chao, Chuen-Guang; Liu, Tzeng-Feng

2017-01-01

Mg-5wt.% Sn alloy is often used in portable electronic devices and automobiles. In this study, mechanical properties of Mg-5wt.% Sn alloy processed by Equal Channel Angular Extrusion (ECAE) were characterized. More precisely, its hardness and wear behavior were measured using Vickers hardness test and a pin-on-disc wear test. The microstructures of ECAE-processed Mg-Sn alloys were investigated by scanning electron microscope and X-ray diffraction. ECAE process refined the grain sizes of the Mg-Sn alloy from 117.6 μm (as-cast) to 88.0 μm (one pass), 49.5 μm (two passes) and 24.4 μm (four passes), respectively. Meanwhile, the hardness of the alloy improved significantly. The maximum wear resistance achieved in the present work was around 73.77 m/mm3, which was obtained from the Mg-Sn alloy treated with a one-pass ECAE process with a grain size of 88.0 μm. The wear resistance improvement was caused by the grain size refinement and the precipitate of the second phase, Mg2Sn against the oxidation of the processed alloy. The as-cast Mg-Sn alloy with the larger grain size, i.e., 117.6 μm, underwent wear mechanisms, mainly adhesive wear and abrasive wear. In ECAE-processed Mg-Sn alloy, high internal energy occurred due to the high dislocation density and the stress field produced by the plastic deformation, which led to an increased oxidation rate of the processed alloy during sliding. Therefore, the oxidative wear and a three-body abrasive wear in which the oxide debris acted as the three-body abrasive components became the dominant factors in the wear behavior, and as a result, reduced the wear resistance in the multi-pass ECAE-processed alloy. PMID:29144414

Explosive Shock-Wave Consolidation of Aluminum Powder/Carbon Nanotube Aggregate Mixtures: Optical and Electron Metallography

NASA Astrophysics Data System (ADS)

Salas, W.; Alba-Baena, N. G.; Murr, L. E.

2007-12-01

The formation of conventional metal-matrix composites reinforced with carbon nanotubes (CNTs) has proven difficult because of the agglomeration and inability of CNTs to disperse. We have explored the explosive consolidation of 150- μm aluminum powder/multiwalled carbon nanotube (MWCNT) aggregates (including multiconcentric fullerenes) at volume percentages of 2 and 5 pct. These consolidated mixtures formed two-phase, monolithic systems (TPSs) with the MWCNT aggregate material spreading along the Al grains and forming carbon phases mainly at the Al particle triple points. The Al powder particle (or grain) hardness increased from HRE 22 to HRE 40 for the consolidated Al, while the two-phase system hardness dropped from HRE 40 to HRE 39 and 33, respectively, for 2 and 5 vol pct MWCNT aggregate additions. Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) observations illustrate a laminate-like structure of the consolidated MWCNT aggregate material, which is easily delaminated, causing intergranular (Al) failure. The Al grains exhibited a shock-induced dislocation substructure (0.5 to 3 μm) and recrystallized subgrains, which increased the individual particle/grain Vickers hardness from 24 to 43 HV.

Characterization of a wollastonite glass-ceramic material prepared using sugar cane bagasse ash (SCBA) as one of the raw materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Teixeira, Silvio R., E-mail: rainho@fct.unesp.br; Souza, Agda E.; Carvalho, Claudio L.

Glass-ceramic material prepared with sugar cane bagasse ash as one of the raw materials was characterized to determine some important properties for its application as a coating material. X-ray diffraction patterns showed that wollastonite-2M (CaSiO{sub 3}) was the major glass-ceramic phase. The Rietveld method was used to quantify the crystalline (60 wt.%) and vitreous (40 wt.%) phases in the glass-ceramic. The microstructure (determined by scanning electron microscopy) of this material had a marble appearance, showing a microporous network of elongated crystals with some areas with dendritic, feather-like ordering. Microhardness data gave a mean hardness value of 564.4 HV (Vickers-hardness), andmore » light microscopy disclosed a greenish brown colored material with a vitreous luster. - Highlights: • We studied the properties of a glass-ceramic material obtained from sugarcane ash. • This material has the appearance and hardness of natural stones. • A refining method gave information about its amorphous and crystalline phases. • This material has potential to be used as coating plates for buildings.« less

Effect of Co doping on structural and mechanical properties of CeO2

NASA Astrophysics Data System (ADS)

Tiwari, Saurabh; Balasubramanian, Nivedha; Biring, Sajal; Sen, Somaditya

2018-05-01

Sol-gel synthesized nanocrystalline Co doped CeO2 powders [(Ce1-xCoxO2; x=0, 0.03)] were made into cylindrical discs by uniaxial pressing and sintered at 1500°C for 24h to measure mechanical properties. The pure phase formation of undoped and Co doped samples were confirmed by X-ray diffraction and Raman analysis. The scanning electron microscopy (SEM) was used for observing the microstructure of sintered samples to investigate density, porosity, and grain size. The grains size observed for 1500°C sintered samples 5-8 µm. Vickers indentation method used for investigating the micro-hardness. For undoped CeO2 micro-hardness was found 6.2 GPa which decreased with Co doping. It was found that samples follow indentation size effect (ISE) and follow elastic than plastic deformation. Enhanced ductile nature with Co doping in CeO2 made it more promising material for optoelectronic device applications.

Effect of sintering process on the magnetic and mechanical properties of sintered Nd-Fe-B magnets

NASA Astrophysics Data System (ADS)

Hu, Z. H.; Qu, H. J.; Zhao, J. Q.; Yan, C. J.; Liu, X. M.

2014-11-01

The magnetic and mechanical properties of sintered Nd-Fe-B magnets prepared by different sintering processes were investigated. The results showed that the intrinsic coercivity and fracture toughness of sintered Nd-Fe-B magnets first increased, and then declined with increasing annealing temperature. The optimum magnetic properties and fracture toughness of sintered Nd-Fe-B magnets were obtained at the annealing temperature of 540 °C. Sintering temperature increasing from 1047 °C to 1071 °C had hardly effect on the magnetic properties of sintered Nd-Fe-B magnets. The variation of Vickers hardness and fracture toughness was not the same with increasing sintering temperature, and the effect of sintering temperature on the mechanical properties was complex and irregular. The reasons for the variation on magnetic and mechanical properties were analyzed, and we presumed that the effect of microstructure on the mechanical properties was more sensitive than the magnetic properties through analyzing the microstructure of sintered Nd-Fe-B magnets.

A Novel Approach to Enhance the Mechanical Strength and Electrical and Thermal Conductivity of Cu-GNP Nanocomposites

NASA Astrophysics Data System (ADS)

Saboori, Abdollah; Pavese, Matteo; Badini, Claudio; Fino, Paolo

2018-01-01

Copper/graphene nanoplatelet (GNP) nanocomposites were produced by a wet mixing method followed by a classical powder metallurgy technique. A qualitative evaluation of the structure of graphene after mixing indicated that wet mixing is an appropriate dispersion method. Thereafter, the effects of two post-processing techniques such as repressing-annealing and hot isostatic pressing (HIP) on density, interfacial bonding, hardness, and thermal and electrical conductivity of the nanocomposites were analyzed. Density evaluations showed that the relative density of specimens increased after the post-processing steps so that after HIPing almost full densification was achieved. The Vickers hardness of specimens increased considerably after the post-processing techniques. The thermal conductivity of pure copper was very low in the case of the as-sintered samples containing 2 to 3 pct porosity and increased considerably to a maximum value in the case of HIPed samples which contained only 0.1 to 0.2 pct porosity. Electrical conductivity measurements showed that by increasing the graphene content electrical conductivity decreased.

High-Speed Friction Stir Welding of AA7075-T6 Sheet: Microstructure, Mechanical Properties, Micro-texture, and Thermal History

NASA Astrophysics Data System (ADS)

Zhang, Jingyi; Upadhyay, Piyush; Hovanski, Yuri; Field, David P.

2018-01-01

Friction stir welding (FSW) is a cost-effective and high-quality joining process for aluminum alloys (especially heat-treatable alloys) that is historically operated at lower joining speeds (up to hundreds of millimeters per minute). In this study, we present a microstructural analysis of friction stir welded AA7075-T6 blanks with high welding speeds up to 3 M/min. Textures, microstructures, mechanical properties, and weld quality are analyzed using TEM, EBSD, metallographic imaging, and Vickers hardness. The higher welding speed results in narrower, stronger heat-affected zones (HAZs) and also higher hardness in the nugget zones. The material flow direction in the nugget zone is found to be leaning towards the welding direction as the welding speed increases. Results are coupled with welding parameters and thermal history to aid in the understanding of the complex material flow and texture gradients within the welds in an effort to optimize welding parameters for high-speed processing.

The effect of surface nanocrystallization on plasma nitriding behaviour of AISI 4140 steel

NASA Astrophysics Data System (ADS)

Li, Yang; Wang, Liang; Zhang, Dandan; Shen, Lie

2010-11-01

A plastic deformation surface layer with nanocrystalline grains was produced on AISI 4140 steel by means of surface mechanical attrition treatment (SMAT). Plasma nitriding of SMAT and un-SMAT AISI 4140 steel was carried out by a low-frequency pulse excited plasma unit. A series of nitriding experiments has been conducted at temperatures ranging from 380 to 500 °C for 8 h in an NH 3 gas. The samples were characterized using X-ray diffraction, scanning electron microscopy, optical microscopy and Vickers microhardness tester. The results showed that a much thicker compound layer with higher hardness was obtained for the SMAT samples when compared with un-SMAT samples after nitriding at the low temperature. In particular, plasma nitriding SMAT AISI 4140 steel at 380 °C for 8 h can produced a compound layer of 2.5 μm thickness with very high hardness on the surface, which is similar to un-SMAT samples were plasma nitrided at approximately 430 °C within the same time.

Strengthening Effect of Incremental Shear Deformation on Ti Alloy Clad Plate with a Ni-Based Alloy Laser-Clad Layer

NASA Astrophysics Data System (ADS)

Zhao, W.; Zha, G. C.; Kong, F. X.; Wu, M. L.; Feng, X.; Gao, S. Y.

2017-05-01

A Ti-6Al-4V alloy clad plate with a Tribaloy 700 alloy laser-clad layer is subjected to incremental shear deformation, and we evaluate the structural evolution and mechanical properties of the specimens. Results indicate the significance of the incremental shear deformation on the strengthening effect. The wear resistance and Vickers hardness of the laser-clad layer are enhanced due to increased dislocation density. The incremental shear deformation can increase the bonding strength of the laser-clad layer and the corresponding substrate and can break the columnar crystals in the laser-clad layer near the interface. These phenomena suggest that shear deformation eliminates the defects on the interface of the laser-clad layer and the substrate. Substrate hardness is evidently improved, and the strengthening effect is caused by the increased dislocation density and shear deformation. This deformation can then transform the α- and β-phases in the substrate into a high-intensity ω-phase.

Effects of metal binder on the microstructure and mechanical properties of Al2O3-based micro-nanocomposite ceramic tool material

NASA Astrophysics Data System (ADS)

Ni, Xiu-ying; Zhao, Jun; Sun, Jia-lin; Gong, Feng; Li, Zuo-li

2017-07-01

The Al2O3-(W,Ti)C composites with Ni and Mo additions varying from 0vol% to 12vol% were prepared via hot pressing sintering under 30 MPa. The microstructure was investigated via X-ray diffraction (XRD) and scanning electron microscopy (SEM) equipped with energy dispersive spectrometry (EDS). Mechanical properties such as flexural strength, fracture toughness, and Vickers hardness were also measured. Results show that the main phases A12O3 and (W,Ti)C were detected by XRD. Compound MoNi also existed in sintered nanocomposites. The fracture modes of the nanocomposites were both intergranular and transgranular fractures. The plastic deformation of metal particles and crack bridging were the main toughening mechanisms. The maximum flexural strength and fracture toughness were obtained for 9vol% and 12vol% additions of Ni and Mo, respectively. The hardness of the composites reduced gradually with increasing content of metals Ni and Mo.

Microstructural and Mechanical Characterization of Ti-12Mo-6Zr Biomaterials Fabricated by Spark Plasma Sintering

NASA Astrophysics Data System (ADS)

Daoush, Walid Mohamed Rashad Mohamed; Park, Hee Sup; Inam, Fawad; Lim, Byung Kyu; Hong, Soon Hyung

2015-03-01

Ti-12Mo-6Zr/Al2O3 (titanium biomaterial) was prepared by a powder metallurgy route using Spark Plasma Sintering (SPS). Ti, Mo, and Zr powders were mixed by wet milling with different content of alumina nanoparticles (up to 5 wt pct) as an oxide dispersion strengthening phase. Composite powder mixtures were SPSed at 1273 K (1000 °C) followed by heat treatment and quenching. Composite powders, sintered materials, and heat-treated materials were examined using optical and high-resolution electronic microscopy (scanning and transmission) and X-ray diffraction to characterize particle size, surface morphology, and phase identifications for each composition. All sintered materials were evaluated by measuring density, Vickers hardness, and tensile properties. Fully dense sintered materials were produced by SPS and mechanical properties were found to be improved by subsequent heat treatment. The tensile properties as well as the hardness were increased by increasing the content of Al2O3 nanoparticles in the Ti-12Mo-6Zr matrix.

Synthesis and studies on microhardness of alkali zinc borate glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Subhashini,, E-mail: subhashini.p.p@gmail.com; Bhattacharya, Soumalya, E-mail: subhashini.p.p@gmail.com; Shashikala, H. D., E-mail: subhashini.p.p@gmail.com

2014-04-24

The mixed alkali effect on zinc borate glasses have been reported. The glass systems of nominal composition 10Zn+xLi{sub 2}O+yNa{sub 2}O+80B{sub 2}O{sub 3} (x = y = 0, 5, 10, 15 mol%) were prepared using standard melt quenching method. The structural, physical and mechanical properties of the samples have been studied using X-ray diffraction(XRD), density measurement and Vickers hardness measurement, respectively. A consistent increase in the density was observed, which explains the role of the modifiers (Li{sub 2}O and Na{sub 2}O) in the network modification of borate structure. The molar volume is decreasing linearly with the alkali concentration, which is attributedmore » to the conversion of tetrahedral boron (BO{sub 4/2}){sup −} into (BO{sub 3/2}){sup −}. The microhardness studies reveals the anisotropy nature of the material. It further confirms that the samples belong to hard glass category.« less

Growth, spectral and optical characterization of a novel nonlinear optical organic material: D-Alanine DL-Mandelic acid single crystal

NASA Astrophysics Data System (ADS)

Jayaprakash, P.; Mohamed, M. Peer; Caroline, M. Lydia

2017-04-01

An organic nonlinear optical single crystal, D-alanine DL-mandelic acid was synthesized and successfully grown by slow evaporation solution growth technique at ambient temperature using solvent of aqueous solution. The unit cell parameters were assessed from single crystal X-ray diffraction analysis. The presence of diverse functional groups and vibrational modes were identified using Fourier Transform Infra Red and Fourier Transform Raman spectral analyses. The chemical structure of grown crystal has been identified by Nuclear Magnetic Resonance spectroscopic study. Ultraviolet-visible spectral analysis reveal that the crystal has lower cut-off wavelength down to 259 nm, is a key factor to exhibit second harmonic generation signal. The electronic optical band gap and Urbach energy is calculated as 5.31 eV and 0.2425 eV respectively from the UV absorption profile. The diverse optical properties such as, extinction coefficient, reflectance, linear refractive index, optical conductivity was calculated using UV-visible data. The relative second harmonic efficiency of the compound is found to be 0.81 times greater than that of KH2PO4 (KDP). The thermal stability of the grown crystal was studied by thermogravimetric analysis and differential thermal analysis techniques. The luminescence spectrum exhibited two peaks (520 nm, 564 nm) due to the donation of protons from carboxylic acid to amino group. The Vickers microhardness test was carried out employing one of the as-grown hard crystal and there by hardness number (Hv), Meyer's index (n), yield strength (σy), elastic stiffness constant (C11) and Knoop hardness number (HK) were assessed. The dielectric behaviour of the as-grown crystal was analyzed for different temperatures (313 K, 333 K, 353 K, and 373 K) at different frequencies.

Effect of etch-and-rinse and self-etching adhesive systems on hardness uniformity of resin cements after glass fiber post cementation

PubMed Central

Grande da Cruz, Fernanda Zander; Grande, Christiana Zander; Roderjan, Douglas Augusto; Galvão Arrais, César Augusto; Bührer Samra, Adriana Postiglione; Calixto, Abraham Lincoln

2012-01-01

Objective To evaluate the effects of etch-and-rinse and self-etching adhesive systems on Vickers hardness (VHN) uniformity of dual-cured resin cements after fiber post cementation. Methods: Fifty glass fiber posts were cemented into bovine roots using the following cementing systems: Prime&Bond 2.1 Dual Cure and Enforce with light-activation (PBDC-LCEN); Prime&Bond 2.1 and Enforce with light-activation (PB-CLEN); Prime&Bond 2.1 Dual Cure and Enforce without light exposure (PBDC-SCEN); ED Primer and Panavia 21 (ED-SCPN); and Clearfil SE Bond and Panavia 21 (CF-SCPN). The roots were stored in distilled water for 72 h and transversely sectioned into thirds (coronal, medium, and apical). The VHN values of the resin cement layers were measured close to the post and to the dentin wall on the transversely sectioned flat surfaces. The results were analyzed by three-way repeated measures analysis of variance (ANOVA) and Tukey’s post-hoc test (pre-set alpha of 5%). Results: Most resin cements presented higher VHN values near the post than near the dentin wall. The ED-SCPN group showed the highest VHN values regardless of the root third, while the self-cured group PBDC-SCEN exhibited the lowest values. The resin cements from the light-activated groups PBDC-LCEN and PB-LCEN showed lower VHN values at the apical third than at the coronal third. The VHN values were not influenced by the root third in self-cured groups PBDC-SCEN, ED-SCPN, and ED-SCPN. Conclusion: Depending on the product, bonding agents might promote changes in hardness uniformity of resin cements after post cementation. PMID:22904652

Wear Resistance Properties Reinforcement Using Nano-Al/Cu Composite Coating in Sliding Bearing Maintenance.

PubMed

Liu, Hongtao; Li, Zhixiong; Wang, Jianmei; Sheng, Chenxing; Liu, Wanli

2018-03-01

Sliding bearing maintenance is crucial for reducing the cost and extending the service life. An efficient and practical solution is to coat a restorative agent onto the worn/damaged bearings. Traditional pure-copper (Cu) coating results in a soft surface and poor abrasion resistance. To address this issue, this paper presents a nano-composite repairing coating method. A series of nano-Al/Cu coatings were prepared on the surface of 45 steel by composite electro-brush plating (EBP). Their micro-hardness was examined by a MHV-2000 Vickers hardness tester, and tribological properties by a UMT-2M Micro-friction tester, 3D profiler and SEM. Then, the influence of processing parameters such as nano-particle concentration and coating thickness on the micro-hardness of nano-Al/Cu coating was analyzed. The experimental analysis results demonstrate that, when the nano-Al particle concentration in electrolyte was 10 g/L, the micro-hardness of the composite coating was 1.1 times as much as that of pure-Cu coating. When the Al nano-particle concentration in electrolyte was 20 g/L, the micro-hardness of the composite coating reached its maximum value (i.e., 231.6 HV). Compared with the pure-Cu coating, the hardness and wear resistance of the nano-composite coating were increased, and the friction coefficient and wear volume were decreased, because of the grain strengthening and dispersion strengthening. The development in this work may provide a feasible and effective nano-composite EBP method for sliding bearing repair.

Processing and characterization of laser sintered hybrid B4C/cBN reinforced Ti-based metal matrix composite

NASA Astrophysics Data System (ADS)

Gupta, Ankit; Hussain, Manowar; Misra, Saurav; Das, Alok Kumar; Mandal, Amitava

2018-06-01

The purpose of this study is to make a boron carbide (B4C) and cubic boron nitride (cBN) reinforced Ti6Al4V metal matrix composites (MMC's) by direct metal laser sintering (DMLS) technique using the continuous wave (CW) SPI fiber laser and to check the feasibility of the formation of three dimensional objects by this process. For this study, the process parameters like laser power density (3.528-5.172 W/cm2 (×104), scanning speed (3500-4500 mm/min), composition of the reinforced materials B4C (5-25% by volume) and cBN (3% by volume) were taken as input variables and hatching gap (0.2 mm), spot diameter (0.4 mm), layer thickness (0.4 mm) were taken as constant. It was analyzed that surface characteristic, density and the mechanical properties of sintered samples were greatly influenced by varying the input process parameters. Field emission scanning electron microscopy (FESEM), Energy dispersive X-ray spectroscopy (EDX) and X-Ray diffraction (XRD) were performed for microstructural analysis, elemental analysis, and recognition of intermetallic compounds respectively. Mechanical properties like micro-hardness & wear rate were examined by Vickers micro-hardness tester & pin on disc arrangement respectively. From hardness tests, it was observed that hardness property of the sintered specimens was increased as compared to the parent material. The XRD results show that there is a good affinity between Ti6Al4V-B4C-cBN to produce various intermetallic compounds which themselves enhance the mechanical properties of the samples. From FESEM analysis, we can conclude that there is a uniform distribution of reinforcements in the titanium alloy matrix. Furthermore, the coefficient of friction (COF) was characterized by the irregular pattern and it tends to decrease with an increase in the volume % of reinforcement. The results obtained in this work may be useful in preparing the MMC's with improved mechanical properties and overall characteristics.

The effect of Coca-Cola and fruit juices on the surface hardness of glass-ionomers and 'compomers'.

PubMed

Aliping-McKenzie, M; Linden, R W A; Nicholson, J W

2004-11-01

The interaction of tooth-coloured dental restorative materials (a conventional glass-ionomer, two resin-modified glass-ionomers and two compomers) with acidic beverages has been studied with the aim of investigating how long-term contact affects solution pH and specimen surface hardness. For each material (ChemFil Superior, ChemFlex, Vitremer Core Build-Up/Restorative, Fuji II LC, Dyract AP and F2000) disc-shaped specimens were prepared and stored in sets of six in the following storage media: 0.9% NaCl (control), Coca-Cola, apple juice and orange juice. After time intervals of 1 day, 1 week, 1 month, 3 months, 4 months, 6 months and 1 year, solution pH and Vickers Hardness Number were determined for each individual specimen. Differences were analysed by anova followed by Student-Newman-Keuls post hoc analysis. All materials were found to reduce the pH of the 0.9% NaCl, but to increase the pH of the acidic beverages. The conventional glass-ionomers dissolved completely in apple juice and orange juice, but survived in Coca-Cola, albeit with a significantly reduced hardness after 1 year. The other materials survived in apple juice and orange juice, but showed greater reductions in surface hardness in these beverages than in Coca-Cola. Fruit juices were thus shown to pose a greater erosive threat to tooth coloured materials than Coca-Cola, a finding which is similar to those concerning dentine and enamel towards these drinks.

A new superhard carbon allotrope: Orthorhombic C20

NASA Astrophysics Data System (ADS)

Wei, Qun; Zhao, Chenyang; Zhang, Meiguang; Yan, Haiyan; Zhou, Yingjiao; Yao, Ronghui

2018-06-01

A new superhard carbon orthorhombic allotrope oC20 is proposed, which exhibits distinct topologies including C4, C3 and two types of C6 carbon rings. The calculated elastic constants and phonon spectra reveal that oC20 is mechanically and dynamically stable at ambient pressure. The calculated electronic band structure of oC20 shows that it is an indirect band gap semiconductor with a band gap of 4.46 eV. The Vickers hardness of oC20 is 75 GPa. The calculated tensile and shear strength indicate that the weakest tensile strength is 64 GPa and the weakest shear strength is 48 GPa, which means oC20 is a potential superhard material.

Flexibility and hardness of dental stainless steel wrought wires used in Thailand.

PubMed

Benjakul, P; Cheunarrom, C; Ongthiemsak, C

2001-03-01

Stainless steel wrought wires used as clasp arms for removable partial dentures in Thailand were compared with those used in some other countries (in the as-received condition) in terms of flexibility, Vickers microhardness and composition. The results showed that there were significant differences (P< or =0.05) among the wires. A Japanese stainless steel wire (SK) was obviously different from the others. It had the lowest proportional limit and microhardness, but its flexibility was almost the same. The chemical composition of each wire was not greatly different. The wires were about 18-20 wt% chromium and 8-9 wt% nickel, except for the SK wire, which had about 12 wt% nickel.

The fracture toughness of borides formed on boronized cold work tool steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sen, Ugur; Sen, Saduman

2003-06-15

In this study, the fracture toughness of boride layers of two borided cold work tool steels have been investigated. Boriding was carried out in a salt bath consisting of borax, boric acid, ferro-silicon and aluminum. Boriding was performed at 850 and 950 deg. C for 2 to 7 h. The presence of boride phases were determined by X-ray diffraction (XRD) analysis. Hardness and fracture toughness of borides were measured via Vickers indenter. Increasing of boriding time and temperature leads to reduction of fracture toughness of borides. Metallographic examination showed that boride layer formed on cold work tool steels was compactmore » and smooth.« less

Glass formation, properties, and structure of soda-yttria-silicate glasses

NASA Technical Reports Server (NTRS)

Angel, Paul W.; Hann, Raiford E.

1991-01-01

The glass formation region of the soda yttria silicate system was determined. The glasses within this region were measured to have a density of 2.4 to 3.1 g/cu cm, a refractive index of 1.50 to 1.60, a coefficient of thermal expansion of 7 x 10(exp -6)/C, softening temperatures between 500 and 780 C, and Vickers hardness values of 3.7 to 5.8 GPa. Aqueous chemical durability measurements were made on select glass compositions while infrared transmission spectra were used to study the glass structure and its effect on glass properties. A compositional region was identified which exhibited high thermal expansion, high softening temperatures, and good chemical durability.

Preparation of bulk superhard B-C-N nanocomposite compact

DOEpatents

Zhao, Yusheng [Los Alamos, NM; He, Duanwei [Sichuan, CN

2011-05-10

Bulk, superhard, B--C--N nanocomposite compacts were prepared by ball milling a mixture of graphite and hexagonal boron nitride, encapsulating the ball-milled mixture at a pressure in a range of from about 15 GPa to about 25 GPa, and sintering the pressurized encapsulated ball-milled mixture at a temperature in a range of from about 1800-2500 K. The product bulk, superhard, nanocomposite compacts were well sintered compacts with nanocrystalline grains of at least one high-pressure phase of B--C--N surrounded by amorphous diamond-like carbon grain boundaries. The bulk compacts had a measured Vicker's hardness in a range of from about 41 GPa to about 68 GPa.

Physical properties of root cementum: Part I. A new method for 3-dimensional evaluation.

PubMed

Malek, S; Darendeliler, M A; Swain, M V

2001-08-01

Cementum is a nonuniform connective tissue that covers the roots of human teeth. Investigation of the physical properties of cementum may help in understanding or evaluating any possible connection to root resorption. A variety of engineering tests are available to investigate these properties. However, the thickness of the cementum layer varies, and this limits the applicability of these techniques in determining the physical properties of cementum. Hardness testing with Knoop and Vickers indentations overcame some of these limitations, but they prohibited the retrieval and retesting of the sample and therefore the testing was restricted to one area or section of the tooth. Another limiting factor with the existing techniques was the risk of artifacts related to the embedding material such as acrylic. A new method to investigate the physical properties of human premolar cementum was developed to obtain a 3-dimensional map of these properties with the Ultra Micro Indentation System (UMIS-2000; Commonwealth Scientific and Industrial Research Organization, Campbell, Australia). UMIS-2000 is a nano-indentation instrument for investigation of the properties of the near-surface region of materials. Premolars were harvested from orthodontic patients requiring extractions and then mounted on a newly designed surveyor that allowed sample retrieval and 3-dimensional rotation. This novel method enabled the quantitative testing of root surface cementum, on all 4 root surfaces, extending from the apex to the cementoenamel junction at 60 different sites.

Effects of Power-Law Plasticity on Deformation Fields underneath Vickers Indenter

NASA Astrophysics Data System (ADS)

Chollacoop, Nuwong; Srikant, Gollapudi; Ramamurty, Upadrasta

The effects of power-law plasticity (yield strength σy and strain hardening exponent n) on the plastic strain distribution underneath a Vickers indenter was explicitly investigated by recourse to macro- and micro-indentation experiments on heat-treated Al-Zn-Mg alloy. With carefully designed aging profile, Al alloy can achieve similar σy with different n, and vice versa. Using the Vickers tip, the samples were macro-indented, sectioned and micro-indented to construct the sub-surface strain distribution. Thus, the effects of σy and n on stain distribution underneath Vickers indenter were revealed.

Tribological characterization of the drill pipe tool joints reconditioned by using welding technologies

NASA Astrophysics Data System (ADS)

Caltaru, M.; Badicioiu, M.; Ripeanu, R. G.; Dinita, A.; Minescu, M.; Laudacescu, E.

2018-01-01

Drill pipe is a seamless steel pipe with upset ends fitted with special threaded ends that are known as tool joints. During drilling operations, the wall thickness of the drill pipe and the outside diameter of the tool joints will be gradually reduced due to wear. The present research work investigate the possibility of reconditioning the drill pipe tool joints by hardbanding with a new metal-cored coppered flux cored wire, Cr-Mo alloyed, using the gas metal active welding process, taking into considerations two different hardbanding technologies, consisting in: hardbanding drill pipe tool joints after removing the old hardbanding material and surface reconstruction with a compensation material (case A), and hardbanding tool joint drill pipe, without removing the old hardbanding material (case B). The present paper brings forward the experimental researches regarding the tribological characterization of the reconditioned drill pipe tool joint by performing macroscopic analyses, metallographic analyses, Vickers hardness measurement, chemical composition measurement and wear tests conducted on ball on disk friction couples, in order to certify the quality of the hardbanding obtained by different technological approaches, to validate the optimum technology.

Synthesis and physicochemical properties of bis(L-asparaginato) zinc(II): A promising new semiorganic crystal with high laser damage threshold for shorter wavelength generation

NASA Astrophysics Data System (ADS)

Subhashini, R.; Arjunan, S.

2018-05-01

An exceedingly apparent nonlinear semiorganic optical crystals of bis(L-asparaginato)zinc(II) [BLAZ], was synthesized by a traditional slow evaporation solution growth technique. The cell parameters were estimated from single crystal X-ray diffraction analysis. Spectroscopic study substantiates the presence of functional groups. The UV spectrum shows the sustenance of wide transparency window and several optical constants, such as extinction coefficient (K), refractive index, optical conductivity and electric susceptibility with real and imaginary parts of dielectric constant were calculated using the transmittance data. The fluorescence emission spectrum of the crystal pronounces red emission. The laser induced surface damage threshold of the crystal was measured using Nd:YAG laser. The output intensity of second harmonic generation was estimated using the Kurtz and Perry powder method. The hardness stability was investigated by Vickers microhardness test. The decomposition and thermal stability of the compound were scrutinized by TGA-DSC studies. Dielectric studies were carried out to anatomize the electrical properties of the crystal. SEM analysis reveals the existence of minute crystallites on the growth surface.

Wear properties of 10 vol.% silicon carbide particulate-reinforced aluminum composite fabricated by powder injection molding

NASA Astrophysics Data System (ADS)

Patcharawit, T.; Ngeekoh, A.; Chuankrekkul, N.

2017-09-01

Wear properties of aluminum matrix composites reinforced with silicon carbide particulate of 10 vol.% addition was investigated in as-sintered and heat-treated conditions under varying loads at -5, -25, -45 and -65N using a ball on flat type of wear test. The composite was fabricated by powder injection molding and sintering at 650 °C for 3 hours. Solution treatment was carried out at 550 °C for 2 hours followed by age-hardening at 160 °C for 6 hours. SEM and XRD results indicated Al and SiCp are present as matrix and reinforcement, while AlN, Al2Cu and Mg2Si were also detected. Further precipitation of Al2Cu and Mg2Si in heat-treated samples promoted maximum macro and micro Vickers hardness values, which were achieved at 161 and 157 Hv respectively. Wear weight loss increased with increasing minus load level. The coefficient of friction was found in the range of 0.042-0.048. Wear mechanisms were determined as the combination of abrasive, adhesion and oxidation.

Effect of Annealing Treatments on the Microstructure, Mechanical Properties and Corrosion Behavior of Direct Metal Laser Sintered Ti-6Al-4V

NASA Astrophysics Data System (ADS)

Xu, Yangzi; Lu, Yuan; Sundberg, Kristin L.; Liang, Jianyu; Sisson, Richard D.

2017-05-01

An experimental investigation on the effects of post-annealing treatments on the microstructure, mechanical properties and corrosion behavior of direct metal laser sintered Ti-6Al-4V alloys has been conducted. The microstructure and phase evolution as affected by annealing treatment temperature were examined through scanning electron microscopy and x-ray diffraction. The tensile properties and Vickers hardness were measured and compared to the commercial Grade 5 Ti-6Al-4V alloy. Corrosion behavior of the parts was analyzed electrochemically in simulated body fluid at 37 °C. It was found out that the as-printed parts mainly composed of non-equilibrium α' phase. Annealing treatment allowed the transformation from α' to α phase and the development of β phase. The tensile test results indicated that post-annealing treatment could improve the ductility and decrease the strength. The as-printed Ti-6Al-4V part exhibits inferior corrosion resistance compared to the commercial alloy, and post-annealing treatment can reduce its susceptibility to corrosion by reducing the two-phase interface area.

Structure and Properties of the Aluminide Coatings on the Inconel 625 Superalloy

NASA Astrophysics Data System (ADS)

Adamiak, Stanisław; Bochnowski, Wojciech; Dziedzic, Andrzej; Filip, Ryszard; Szeregij, Eugeniusz

2016-01-01

The research samples used in this study were based on the Inconel 625 alloy; the examined samples were coated with aluminide films deposited in a low-activity chemical vapor deposition (CVD) process. The samples' microstructure was investigated with optical and electron microscopy and energy dispersive X-ray spectroscopy analysis. Hardness measurements were performed using Vickers and Berkovich test methods. The adhesion of the aluminide coating was determined by fractography. It was shown that the fracture mechanism was different for the respective zones of the aluminide coating and the substrate material. The outer zone of the aluminide coating is characterized by an intercrystalline fracture, with a small contribution of transcrystalline fracture within individual grains (large crystallites in the bottom of the zone, composed of smaller crystallites, also show an intercrystalline fracture). The substrate material exhibited a ductile intercrystalline fracture. Based on this investigation, an increase of the microhardness of the material occurring at loads below 0.2 N was observed. When determining microhardness of aluminide coating it is necessary to take into account the optimal choice of the indentation tip.

Deformation During Friction Stir Welding

NASA Technical Reports Server (NTRS)

White, Henry J.

2002-01-01

Friction Stir Welding (FSW) is a solid state welding process that exhibits characteristics similar to traditional metal cutting processes. The plastic deformation that occurs during friction stir welding is due to the superposition of three flow fields: a primary rotation of a radially symmetric solid plug of metal surrounding the pin tool, a secondary uniform translation, and a tertiary ring vortex flow (smoke rings) surrounding the tool. If the metal sticks to the tool, the plug surface extends down into the metal from the outer edge of the tool shoulder, decreases in diameter like a funnel, and closes up beneath the pin. Since its invention, ten years have gone by and still very little is known about the physics of the friction stir welding process. In this experiment, an H13 steel weld tool (shoulder diameter, 0.797 in; pin diameter, 0.312 in; and pin length, 0.2506 in) was used to weld three 0.255 in thick plates. The deformation behavior during friction stir welding was investigated by metallographically preparing a plan view sections of the weldment and taking Vickers hardness test in the key-hole region.

Effects of Laser Remelting and Oxidation on NiCrAlY/8Y2O3-ZrO2 Thermal Barrier Coatings

NASA Astrophysics Data System (ADS)

Xu, S. Q.; Zhu, C.; Zhang, Y.

2018-02-01

In this study, three groups of thermal barrier coatings (TBCs) samples were remelted by CO2 laser with different laser energy densities (1, 5 and 10 J/mm2) to seal the surface of yttria-stabilized zirconia (YSZ) coatings. Microscopic observations showed that the cracks size and the remelted depth in YSZ coatings increased. A 50-μm-thick dense layer was formed on the surface of YSZ coating in samples with 1 J/mm2 energy density. Microindentation tests showed that the Vickers hardness of YSZ coatings increases with the increase in laser energy density. After isothermal oxidation at 1200 °C for 200 h, thinner thermally growth oxides were found in laser remelted YSZ samples under energy density of 1 J/mm2 (6.32 ± 0.28 μm). Cyclic oxidation results showed that the weight gain per unit area of low energy density laser remelted TBCs was smaller than that of the high energy density laser remelted and as-sprayed TBCs.

Phase transition of AISI type 304L stainless steel induced by severe plastic deformation via cryo-rolling

NASA Astrophysics Data System (ADS)

Shit, Gopinath; Bhaskar, Pragna; Ningshen, S.; Dasgupta, A.; Mudali, U. Kamachi; Bhaduri, A. Kumar

2017-05-01

The phase transition induced by Severe Plastic Deformation (SPD) was confirmed in metastable AISI type 304L austenitic stainless steel (SS). SPD via cryo-rolling in liquid nitrogen (L-N2) temperature is the adopted route for correlating the phase transition and corrosion resistance. The thickness of the annealed AISI type 304L SS at 1050°C sheet was reduced step by step from 15% to 50% of its initial thickness. The phase changes and phase transformation are qualitatively analyzed by X-Ray Diffraction (XRD) method. During the process, the XRD of each Cryo-Rolled and annealed sample was analyzed and different phases and phase transitions are measured. The investigated AISI type 304L SS by SPD reveals a microstructure of γ-austenite; α'-marternsite and ɛ-martensite formation depending on the percentage of cryo-rolling. The Vickers hardness (HV) of the samples is also measured. The corrosion rate of the annealed sheet and cryo rolled sample was estimated in boiling nitric acid as per ASTM A-262 practice-C test.

Tribo-Mechanical Properties of HVOF Deposited Fe3Al Coatings Reinforced with TiB2 Particles for Wear-Resistant Applications

PubMed Central

Amiriyan, Mahdi; Blais, Carl; Savoie, Sylvio; Schulz, Robert; Gariépy, Mario; Alamdari, Houshang

2016-01-01

This study reveals the effect of TiB2 particles on the mechanical and tribological properties of Fe3Al-TiB2 composite coatings against an alumina counterpart. The feedstock was produced by milling Fe3Al and TiB2 powders in a high energy ball mill. The high-velocity oxy-fuel (HVOF) technique was used to deposit the feedstock powder on a steel substrate. The effect of TiB2 addition on mechanical properties and dry sliding wear rates of the coatings at sliding speeds ranging from 0.04 to 0.8 m·s−1 and loads of 3, 5 and 7 N was studied. Coatings made from unreinforced Fe3Al exhibited a relatively high wear rate. The Vickers hardness, elastic modulus and wear resistance of the coatings increased with increasing TiB2 content in the Fe3Al matrix. The wear mechanisms strongly depended on the sliding speed and the presence of TiB2 particles but were less dependent on the applied load. This study reveals the effect of TiB2 particles on the mechanical and tribological properties of Fe3Al-TiB2 composite coatings against an alumina counterpart. The feedstock was produced by milling Fe3Al and TiB2 powders in a high energy ball mill. The high-velocity oxy-fuel (HVOF) technique was used to deposit the feedstock powder on a steel substrate. The effect of TiB2 addition on mechanical properties and dry sliding wear rates of the coatings at sliding speeds ranging from 0.04 to 0.8 m·s−1 and loads of 3, 5 and 7 N was studied. Coatings made from unreinforced Fe3Al exhibited a relatively high wear rate. The Vickers hardness, elastic modulus and wear resistance of the coatings increased with increasing TiB2 content in the Fe3Al matrix. The wear mechanisms strongly depended on the sliding speed and the presence of TiB2 particles but were less dependent on the applied load. This study reveals the effect of TiB2 particles on the mechanical and tribological properties of Fe3Al-TiB2 composite coatings against an alumina counterpart. The feedstock was produced by milling Fe3Al and TiB2 powders in a high energy ball mill. The high-velocity oxy-fuel (HVOF) technique was used to deposit the feedstock powder on a steel substrate. The effect of TiB2 addition on mechanical properties and dry sliding wear rates of the coatings at sliding speeds ranging from 0.04 to 0.8 m·s−1 and loads of 3, 5 and 7 N was studied. Coatings made from unreinforced Fe3Al exhibited a relatively high wear rate. The Vickers hardness, elastic modulus and wear resistance of the coatings increased with increasing TiB2 content in the Fe3Al matrix. The wear mechanisms strongly depended on the sliding speed and the presence of TiB2 particles but were less dependent on the applied load. This study reveals the effect of TiB2 particles on the mechanical and tribological properties of Fe3Al-TiB2 composite coatings against an alumina counterpart. The feedstock was produced by milling Fe3Al and TiB2 powders in a high energy ball mill. The high-velocity oxy-fuel (HVOF) technique was used to deposit the feedstock powder on a steel substrate. The effect of TiB2 addition on mechanical properties and dry sliding wear rates of the coatings at sliding speeds ranging from 0.04 to 0.8 m·s−1 and loads of 3, 5 and 7 N was studied. Coatings made from unreinforced Fe3Al exhibited a relatively high wear rate. The Vickers hardness, elastic modulus and wear resistance of the coatings increased with increasing TiB2 content in the Fe3Al matrix. The wear mechanisms strongly depended on the sliding speed and the presence of TiB2 particles but were less dependent on the applied load. This study reveals the effect of TiB2 particles on the mechanical and tribological properties of Fe3Al-TiB2 composite coatings against an alumina counterpart. The feedstock was produced by milling Fe3Al and TiB2 powders in a high energy ball mill. The high-velocity oxy-fuel (HVOF) technique was used to deposit the feedstock powder on a steel substrate. The effect of TiB2 addition on mechanical properties and dry sliding wear rates of the coatings at sliding speeds ranging from 0.04 to 0.8 m·s−1 and loads of 3, 5 and 7 N was studied. Coatings made from unreinforced Fe3Al exhibited a relatively high wear rate. The Vickers hardness, elastic modulus and wear resistance of the coatings increased with increasing TiB2 content in the Fe3Al matrix. The wear mechanisms strongly depended on the sliding speed and the presence of TiB2 particles but were less dependent on the applied load. This study reveals the effect of TiB2 particles on the mechanical and tribological properties of Fe3Al-TiB2 composite coatings against an alumina counterpart. The feedstock was produced by milling Fe3Al and TiB2 powders in a high energy ball mill. The high-velocity oxy-fuel (HVOF) technique was used to deposit the feedstock powder on a steel substrate. The effect of TiB2 addition on mechanical properties and dry sliding wear rates of the coatings at sliding speeds ranging from 0.04 to 0.8 m·s−1 and loads of 3, 5 and 7 N was studied. Coatings made from unreinforced Fe3Al exhibited a relatively high wear rate. The Vickers hardness, elastic modulus and wear resistance of the coatings increased with increasing TiB2 content in the Fe3Al matrix. The wear mechanisms strongly depended on the sliding speed and the presence of TiB2 particles but were less dependent on the applied load. PMID:28787917

Interfacial reactions and wetting in Al-Mg sintered by powder metallurgy process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Faisal, Heny, E-mail: faisal@physics.its.ac.id; Darminto,; Triwikantoro,

2016-04-19

Was conducted to analyze the effect of temperature variation on the bonding interface sintered composite Al-Mg and analyze the effect of variations of the density and hardness sinter. Research carried out by the base material powders of Al, Mg powder and solvent n-butanol. The method used in this study is a powder metallurgy, with a composition of 60% volume fraction of Al - 40% Mg. Al-Mg mixing with n-butanol for 1 hour at 500 rpm. Then the emphasis (cold comression) with a size of 1.4 cm in diameter dies and height of 2.8 cm, is pressed with a force of 20 MPa and heldmore » for 15 minutes. After the sample into pellets, then sintered at various temperatures 300 °C, 350 °C, 400 °C and 450 °C. Characterization is done by using the testing green density, sintered density, X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), vickers microhardness, and press test. XRD data analysis done by using X’Pert High Score Plus (HSP) to determine whether there is a new phase is formed. Test results show that the sintered density increasing sintering temperature, the resulting density is also increasing (shrinkage). However, at a temperature of 450 °C decreased (swelling). With the increased sinter density, interfacial bonding getting Kuta and more compact so that its hardness is also increased. From the test results of SEM / EDX, there Mg into Al in the border area. At temperatures of 300 °C, 350 °C, 400 °C, the phase formed is Al, Mg and MgO. While phase is formed at a temperature of 450 °C is aluminum magnesium (Al{sub 3}Mg{sub 2}), Aluminum Magnesium Zinc (AlMg{sub 2}Zn).« less

Abrasive Wear Resistance of Tool Steels Evaluated by the Pin-on-Disc Testing

NASA Astrophysics Data System (ADS)

Bressan, José Divo; Schopf, Roberto Alexandre

2011-05-01

Present work examines tool steels abrasion wear resistance and the abrasion mechanisms which are one main contributor to failure of tooling in metal forming industry. Tooling used in cutting and metal forming processes without lubrication fails due to this type of wear. In the workshop and engineering practice, it is common to relate wear resistance as function of material hardness only. However, there are others parameters which influences wear such as: fracture toughness, type of crystalline structure and the occurrence of hard precipitate in the metallic matrix and also its nature. In the present investigation, the wear mechanisms acting in tool steels were analyzed and, by normalized tests, wear resistance performance of nine different types of tool steels were evaluated by pin-on-disc testing. Conventional tool steels commonly used in tooling such as AISI H13 and AISI A2 were compared in relation to tool steels fabricated by sintering process such as Crucible CPM 3V, CPM 9V and M4 steels. Friction and wear testing were carried out in a pin-on-disc automated equipment which pin was tool steel and the counter-face was a abrasive disc of silicon carbide. Normal load of 5 N, sliding velocity of 0.45 m/s, total sliding distance of 3000 m and room temperature were employed. The wear rate was calculated by the Archard's equation and from the plotted graphs of pin cumulated volume loss versus sliding distance. Specimens were appropriately heat treated by quenching and three tempering cycles. Percentage of alloying elements, metallographic analyses of microstructure and Vickers microhardness of specimens were performed, analyzed and correlated with wear rate. The work is concluded by the presentation of a rank of tool steel wear rate, comparing the different tool steel abrasion wear resistance: the best tool steel wear resistance evaluated was the Crucible CPM 9V steel.

Clinical Performance of a New Biomimetic Double Network Material

PubMed Central

Dirxen, Christine; Blunck, Uwe; Preissner, Saskia

2013-01-01

Background: The development of ceramics during the last years was overwhelming. However, the focus was laid on the hardness and the strength of the restorative materials, resulting in high antagonistic tooth wear. This is critical for patients with bruxism. Objectives: The purpose of this study was to evaluate the clinical performance of the new double hybrid material for non-invasive treatment approaches. Material and Methods: The new approach of the material tested, was to modify ceramics to create a biomimetic material that has similar physical properties like dentin and enamel and is still as strong as conventional ceramics. Results: The produced crowns had a thickness ranging from 0.5 to 1.5 mm. To evaluate the clinical performance and durability of the crowns, the patient was examined half a year later. The crowns were still intact and soft tissues appeared healthy and this was achieved without any loss of tooth structure. Conclusions: The material can be milled to thin layers, but is still strong enough to prevent cracks which are stopped by the interpenetrating polymer within the network. Depending on the clinical situation, minimally- up to non-invasive restorations can be milled. Clinical Relevance: Dentistry aims in preservation of tooth structure. Patients suffering from loss of tooth structure (dental erosion, Amelogenesis imperfecta) or even young patients could benefit from minimally-invasive crowns. Due to a Vickers hardness between dentin and enamel, antagonistic tooth wear is very low. This might be interesting for treating patients with bruxism. PMID:24167534

The Influence of Plasma-Based Nitriding and Oxidizing Treatments on the Mechanical and Corrosion Properties of CoCrMo Biomedical Alloy

NASA Astrophysics Data System (ADS)

Noli, Fotini; Pichon, Luc; Öztürk, Orhan

2018-04-01

Plasma-based nitriding and/or oxidizing treatments were applied to CoCrMo alloy to improve its surface mechanical properties and corrosion resistance for biomedical applications. Three treatments were performed. A set of CoCrMo samples has been subjected to nitriding at moderate temperatures ( 400 °C). A second set of CoCrMo samples was oxidized at 395 °C in pure O2. The last set of CoCrMo samples was nitrided and subsequently oxidized under the experimental conditions of previous sets (double treatment). The microstructure and morphology of the layers formed on the CoCrMo alloy were investigated by X-ray diffraction, Atomic Force Microscopy, and Scanning Electron Microscopy. In addition, nitrogen and oxygen profiles were determined by Glow Discharge Optical Emission Spectroscopy, Rutherford Backscattering Spectroscopy, Energy-Dispersive X-ray, and Nuclear Reaction Analysis. Significant improvement of the Vickers hardness of the CoCrMo samples after plasma nitriding was observed due to the supersaturated nitrogen solution and the formation of an expanded FCC γ N phase and CrN precipitates. In the case of the oxidized samples, Vickers hardness improvement was minimal. The corrosion behavior of the samples was investigated in simulated body fluid (0.9 pct NaCl solution at 37 °C) using electrochemical techniques (potentiodynamic polarization and cyclic voltammetry). The concentration of metal ions released from the CoCrMo surfaces was determined by Instrumental Neutron Activation Analysis. The experimental results clearly indicate that the CoCrMo surface subjected to the double surface treatment consisting in plasma nitriding and plasma oxidizing exhibited lower deterioration and better resistance to corrosion compared to the nitrided, oxidized, and untreated samples. This enhancement is believed to be due to the formation of a thicker and more stable layer.

A Comparative Study of Structural Stability and Mechanical and Optical Properties of Fluorapatite (Ca5(PO4)3F) and Lithium Disilicate (Li2Si2O5) Components Forming Dental Glass-Ceramics: First Principles Study

NASA Astrophysics Data System (ADS)

Biskri, Z. E.; Rached, H.; Bouchear, M.; Rached, D.; Aida, M. S.

2016-10-01

The aim of this paper is a comparative study of structural stability and mechanical and optical properties of fluorapatite (FA) (Ca5(PO4)3F) and lithium disilicate (LD) (Li2Si2O5), using the first principles pseudopotential method based on density functional theory (DFT) within the generalized gradient approximation (GGA). The stability of fluorapatite and lithium disilicate compounds has been evaluated on the basis of their formation enthalpies. The results show that fluorapatite is more energetically stable than lithium disilicate. The independent elastic constants and related mechanical properties, including bulk modulus ( B), shear modulus ( G), Young's modulus ( E) and Poisson's ratio ( ν) as well as the Vickers hardness ( H v), have been calculated for fluorapatite compound and compared with other theoretical and experimental results. The obtained values of the shear modulus, Young's modulus and Vickers hardness are smaller in comparison with those of lithium disilicate compound, implying that lithium disilicate is more rigid than fluorapatite. The brittle and ductile properties were also discussed using B/ G ratio and Poisson's ratio. Optical properties such as refractive index n( ω), extinction coefficient k( ω), absorption coefficient α( ω) and optical reflectivity R( ω) have been determined from the calculations of the complex dielectric function ɛ( ω), and interpreted on the basis of the electronic structures of both compounds. The calculated values of static dielectric constant ɛ 1(0) and static refractive index n(0) show that the Li2Si2O5 compound has larger values compared to those of the Ca5(PO4)3F compound. The results of the extinction coefficient show that Li2Si2O5 compound exhibits a much stronger ultraviolet absorption. According to the absorption and reflectivity spectra, we inferred that both compounds are theoretically the best visible and infrared transparent materials.

Study of the radiation damage effect on Titanium metastable beta alloy by high intensity proton beam

DOE PAGES

Ishida, Taku; Wakai, E.; Hagiwara, M.; ...

2018-04-26

Here, a foil of a metastable β Titanium alloy Ti-15V-3Cr-3Sn-3Al was irradiated at the J-PARC neutrino experimental facility with 1.4 × 10 20 30 GeV protons at low temperature (100–130°C at most), and microstructural characterization and hardness testing were conducted as an initial study on the radiation damage effects of Titanium alloy by the high energy proton beam exposure. Expected radiation damage at the beam center is about 0.06–0.12 displacement per atom. A high density (> 10 23 m –3) of a nanometer-sized precipitate was observed by TEM studies, which would be identified as martensite α-phase and athermal ω-phase formedmore » during the solution-treatment process to fabricate metastable β alloy. They did not appear to change substantially after irradiation with protons. In the irradiated specimen, we could not identify an obvious signature of radiation damage distributed along the proton beam profile. Very small, nanometer-scale black dots were present at a low density in the most highly irradiated region, and may be small dislocation loops formed during irradiation. The micro-indentation test indicated that the radiation exposure led to tiny increase in Vickers micro-hardness of ΔH V= 20 at beam center. Atom probe tomography reveals compositional fluctuations that reach a maximum amplitude of 10 at% Ti within a space of < 5 nm both before and after irradiation, which may also indicate presence of rich precipitates. These experimental results suggest this specific β alloy may exhibit radiation damage resistance due to the existence of a high density of nano-scale precipitates, but further studies with higher exposure are required to explore this possibility.« less

Effect of pressure difference on the quality of titanium casting.

PubMed

Watanabe, I; Watkins, J H; Nakajima, H; Atsuta, M; Okabe, T

1997-03-01

In casting titanium using a two-compartment casting machine, Herø et al. (1993) reported that the pressure difference between the melting chamber and the mold chamber affected the soundness of the castings. This study tested the hypothesis that differences in pressure produce castings with various amounts of porosity and different mechanical properties values. Plastic dumbbell-shaped patterns were invested with an alumina-based, phosphate-bonded investment material. Both chambers of the casting machine were evacuated to 6 x 10(-2) torr; the argon pressure difference was then adjusted to either 50, 150, 300, or 450 torr. The porosity of the cast specimens was determined by x-ray radiography and quantitative image analysis. Tensile strength and elongation were measured by means of a universal testing machine at a strain rate of 1.7 x 10(-4)/s. The fractured surfaces were examined by SEM. Changes in Vickers hardness with depth from the cast surface were measured on polished cross-sections of the specimens. Raising the argon pressure difference to 300 and 450 torr caused a significant increase in internal porosity and a resultant decrease in the engineering tensile strength and elongation. The highest tensile strength (approximately 540 MPa), elongation (approximately 10%), bulk hardness (HV50g 209), and lowest porosity level (approximately 0.8%) occurred in the specimens cast at 150 torr. Turbulence of the metal during casting was thought to be responsible for the increase in porosity levels with the increase in argon pressure difference. By choosing an argon pressure difference (around 150 torr) suitable for this geometry, we could produce castings which have adequate mechanical properties and low porosity levels.

Study of the radiation damage effect on Titanium metastable beta alloy by high intensity proton beam

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ishida, Taku; Wakai, E.; Hagiwara, M.

Here, a foil of a metastable β Titanium alloy Ti-15V-3Cr-3Sn-3Al was irradiated at the J-PARC neutrino experimental facility with 1.4 × 10 20 30 GeV protons at low temperature (100–130°C at most), and microstructural characterization and hardness testing were conducted as an initial study on the radiation damage effects of Titanium alloy by the high energy proton beam exposure. Expected radiation damage at the beam center is about 0.06–0.12 displacement per atom. A high density (> 10 23 m –3) of a nanometer-sized precipitate was observed by TEM studies, which would be identified as martensite α-phase and athermal ω-phase formedmore » during the solution-treatment process to fabricate metastable β alloy. They did not appear to change substantially after irradiation with protons. In the irradiated specimen, we could not identify an obvious signature of radiation damage distributed along the proton beam profile. Very small, nanometer-scale black dots were present at a low density in the most highly irradiated region, and may be small dislocation loops formed during irradiation. The micro-indentation test indicated that the radiation exposure led to tiny increase in Vickers micro-hardness of ΔH V= 20 at beam center. Atom probe tomography reveals compositional fluctuations that reach a maximum amplitude of 10 at% Ti within a space of < 5 nm both before and after irradiation, which may also indicate presence of rich precipitates. These experimental results suggest this specific β alloy may exhibit radiation damage resistance due to the existence of a high density of nano-scale precipitates, but further studies with higher exposure are required to explore this possibility.« less

Effect of polyvinyl siloxane impression material on the polymerization of composite resin.

PubMed

Chen, Liang; Kleverlaan, Cornelis Johannes; Liang, Kunneng; Yang, Deqin

2017-04-01

Polyvinyl siloxane impression material has been widely used as a lingual matrix for rebuilding missing tooth structure with composite resin. The composite resin is light polymerized in contact with the polyvinyl siloxane impression material. However, polyvinyl siloxane impression material has been shown to interact with other dental materials. The purpose of this study was to assess the effect of polyvinyl siloxane impression materials on the polymerization of composite resins by assessing the Vickers microhardness and degree of conversion of polyvinyl siloxane. The composite resins were light polymerized in contact with 3 polyvinyl siloxane impression materials (Flexitime Easy Putty; President Light Body; Xantopren L Blue) (n=8) and in contact with a matrix strip as the control group (n=8). Vickers microhardness and degree of conversion on contact surfaces were measured to evaluate the polymerization of composite resins. The depth of the effect was assessed by Vickers microhardness on section surfaces and observed with scanning electron microscopy. The results were analyzed by 1-way analysis of variance and the post hoc Tukey honest significant differences test (α=.05). The Vickers microhardness and degree of conversion values on the contact surfaces of the experiment groups were significantly lower than those of the control group (P<.05); the Vickers microhardness values on the section surfaces indicated that there was no significant difference at the same depth of different groups (P>.05). The scanning electron microscope observation showed that an approximately 10-μm deep unpolymerized layer was found in the experimental group. Polyvinyl siloxane impression materials have an inhibitory effect on the polymerization of the composite resins, but just limited to within approximately 10 μm from the surface in contact with the impression material. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Effect of bismuth oxide on white mineral trioxide aggregate: chemical characterization and physical properties.

PubMed

Grazziotin-Soares, R; Nekoofar, M H; Davies, T E; Bafail, A; Alhaddar, E; Hübler, R; Busato, A L S; Dummer, P M H

2014-06-01

To assess the effect of bismuth oxide (Bi2 O3 ) on the chemical characterization and physical properties of White mineral trioxide aggregate (MTA) Angelus. Commercially available White MTA Angelus and White MTA Angelus without Bi2 O3 provided by the manufacturer especially for this study were subjected to the following tests: Rietveld X-ray diffraction analysis (XRD), energy-dispersive X-ray analysis (EDX), scanning electron microscopy (SEM), compressive strength, Vickers microhardness test and setting time. Chemical analysis data were reported descriptively, and physical properties were expressed as means and standard deviations. Data were analysed using Student's t-test and Mann-Whitney U test (P = 0.05). Calcium silicate peaks were reduced in the diffractograms of both hydrated materials. Bismuth particles were found on the surface of White MTA Angelus, and a greater amount of particles characterized as calcium hydroxide was observed by visual examination on White MTA without Bi2 O3 . The material without Bi2 O3 had the shortest final setting time (38.33 min, P = 0.002), the highest Vickers microhardness mean value (72.35 MPa, P = 0.000) and similar compressive strength results (P = 0.329) when compared with the commercially available White MTA Angelus containing Bi2 O3 . The lack of Bi2 O3 was associated with an increase in Vickers microhardness, a reduction in final setting time, absence of Bi2 O3 peaks in diffractograms, as well as a large amount of calcium and a morphology characteristic of calcium hydroxide in EDX/SEM analysis. © 2013 International Endodontic Journal. Published by John Wiley & Sons Ltd.

Growth, spectral, optical, thermal, and mechanical behaviour of an organic single crystal: Quinolinium 2-carboxy 6-nitrophthalate monohydrate

NASA Astrophysics Data System (ADS)

Mohana, J.; Ahila, G.; Bharathi, M. Divya; Anbalagan, G.

2016-09-01

Organic single crystals of quinolinium 2-carboxy 6-nitrophthalate monohydrate (QN) were grown by slow evaporation solution growth technique using ethanol and water as a mixed solvent. X-ray powder diffraction analysis revealed that the crystal belongs to the monoclinic crystal system with space group of P21/c. The functional groups present in the crystallized material confirmed its molecular structure. The optical transparency range and the lower cutoff wavelength were identified from the UV-vis spectrum. The optical constants were determined by UV-visible transmission spectrum at normal incidence, measured over the 200-700 nm spectral range. The dispersion of the refractive index was discussed in terms of the single-oscillator Wemple and DiDomenico model. The calculated HOMO and LUMO energies show that the charge transfer occur within the molecule. Electronic excitation properties were discussed within the framework of two level model on the basis of an orbital analysis. The nonlinear optical absorption coefficient (β) and nonlinear refraction (n2) of QN was measured by Z-scan technique and reported here. Thermal stability of QN was determined using TGA/DSC curves. Vicker's microhardness studies were carried out on the (1 1 ̅0) plane to understand the mechanical properties of the grown crystal. The microhardness measurements showed a Vickers hardness value as 18.4 kg/mm2 which is comparable to well-known organic crystal, urea.

Experimental and numerical study on plasma nitriding of AISI P20 mold steel

NASA Astrophysics Data System (ADS)

Nayebpashaee, N.; Vafaeenezhad, H.; Kheirandish, Sh.; Soltanieh, M.

2016-09-01

In this study, plasma nitriding was used to fabricate a hard protective layer on AISI P20 steel, at three process temperatures (450°C, 500°C, and 550°C) and over a range of time periods (2.5, 5, 7.5, and 10 h), and at a fixed gas N2:H2 ratio of 75vol%:25vol%. The morphology of samples was studied using optical microscopy and scanning electron microscopy, and the formed phase of each sample was determined by X-ray diffraction. The elemental depth profile was measured by energy dispersive X-ray spectroscopy, wavelength dispersive spectroscopy, and glow dispersive spectroscopy. The hardness profile of the samples was identified, and the microhardness profile from the surface to the sample center was recorded. The results show that ɛ-nitride is the dominant species after carrying out plasma nitriding in all strategies and that the plasma nitriding process improves the hardness up to more than three times. It is found that as the time and temperature of the process increase, the hardness and hardness depth of the diffusion zone considerably increase. Furthermore, artificial neural networks were used to predict the effects of operational parameters on the mechanical properties of plastic mold steel. The plasma temperature, running time of imposition, and target distance to the sample surface were all used as network inputs; Vickers hardness measurements were given as the output of the model. The model accurately reproduced the experimental outcomes under different operational conditions; therefore, it can be used in the effective simulation of the plasma nitriding process in AISI P20 steel.

Influence of nitrogen immersion on the mechanical properties of (NiO)x(Bi1.6 Pb0.4)Sr2Ca2Cu3O10-δ composite

NASA Astrophysics Data System (ADS)

Rahal, H. T.; Awad, R.; Abdel-Gaber, A. M.

2018-05-01

(NiO)x(Bi1.6 Pb0.4)Sr2Ca2Cu3O10-δ composite, where 0.0 ≤ x ≤ 0.2 wt%., were prepared using solid state reaction method. The prepared samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) as well as transmission electron microscopy (TEM). Vickers microhardness measurements (HV) were carried out at room temperature under different applied loads varying from 0.49 to 9.8 N, and dwell times (40 and 59 s). It was noted that dwell time and Vickers microhardness were inversely proportional. HV values increase as x increases up to 0.1 wt%, and then they decrease with further increases in x. All samples exhibit indentation size effect (ISE) with normal trend, as Vickers microhardness decreases by increasing the applied loads. Also, Vickers microhardness measurements of the prepared samples were done during both loading forces up to 9.8 N and unloading downwards to 0.49 N. It was noted that unloading values of Vickers microhardness are slightly greater than loading values. The elastic/plastic deformation model (EPD) was used to interpret the loading and unloading Vickers microhardness results. It is clearly noted that values of do, the added elastic component the measured plastic indentation semi-diagonal (d),in the unloading results are much higher than those for loading data. The effect of liquid nitrogen immersion for 16 h on Vickers microhardness values was examined. A significant improvement in the Vickers microhardness of (Bi, Pb)-2223 samples immersed in liquid nitrogen was observed. Such behavior is attributed to the fact that nitrogen immersion increases the volume contraction of the superconductor matrix, causing the shrink of the pores and voids present in the samples. Different models were used to analyze the obtained results such as Meyer's law, Hays-Kendall (HK) approach, elastic/plastic deformation (EPD) model, and modified proportional specimen resistance (MPSR) model. The experimental results of Vickers microhardness of both samples without and with liquid nitrogen immersion are well fitted according to the MPSR model.

Influences of Light-emitting Diode Illumination Bleaching Technique on Nanohardness of Computer-aided Design and Computer-aided Manufacturing Ceramic Restorative Materials.

PubMed

Juntavee, Niwut; Juntavee, Apa; Saensutthawijit, Phuwiwat

2018-02-01

This study evaluated the effect of light-emitting diode (LED) illumination bleaching technique on the surface nanohardness of various computer-aided design and computer-aided manufacturing (CAD/CAM) ceramic materials. Twenty disk-shaped samples (width, length, and thickness = 10, 15, and 2 mm) were prepared from each of the ceramic materials for CAD/CAM, including Lava™ Ultimate (L V ), Vita Enamic® (E n ) IPS e.max® CAD (M e ), inCoris® TZI (I C ), and Prettau® zirconia (P r ). The samples from each type of ceramic were randomly divided into two groups based on the different bleaching techniques to be used on them, using 35% hydrogen peroxide with and without LED illumination. The ceramic disk samples were bleached according to the manufacturer's instruction. Surface hardness test was performed before and after bleaching using nanohardness tester with a Berkovich diamond indenter. The respective Vickers hardness number upon no bleaching and bleaching without or with LED illumination [mean ± standard deviation (SD)] for each type of ceramic were as follows: 102.52 ± 2.09, 101.04 ± 1.18, and 98.17 ± 1.15 for L V groups; 274.96 ± 5.41, 271.29 ± 5.94, and 268.20 ± 7.02 for E n groups; 640.74 ± 31.02, 631.70 ± 22.38, and 582.32 ± 33.88 for M e groups; 1,442.09 ± 35.07, 1,431.32 ± 28.80, and 1,336.51 ± 34.03 for I C groups; and 1,383.82 ± 33.87, 1,343.51 ± 38.75, and 1,295.96 ± 31.29 for P r groups. The results indicated surface hardness reduction following the bleaching procedure of varying degrees for different ceramic materials. Analysis of variance (ANOVA) revealed a significant reduction in surface hardness due to the effect of bleaching technique, ceramic material, and the interaction between bleaching technique and ceramic material (p < 0.05). Bleaching resulted in a diminution of the surface hardness of dental ceramic for CAD/CAM. Using 35% hydrogen peroxide bleaching agent with LED illumination exhibited more reduction in surface hardness of dental ceramic than what was observed without LED illumination. Clinicians should consider protection of the existing restoration while bleaching.

Preliminary study of the biomechanical behavior and physical characteristics of tantalum (Ta)-coated prostheses.

PubMed

Duan, Yonghong; Liu, Lie; Wang, Ling; Guo, Fei; Li, Haoping; Shi, Lei; Li, Mao; Yin, Dayu; Jiang, Chi; Zhu, Qingsheng

2012-03-01

Use of Ta biomaterials in medicine started in the middle of the last century. The good biocompatibility and chemical stability, and the unique physical characteristics of Ta metal have resulted in many possible developments of Ta biomaterials. In this study, histopathological observation, histomorphometric analysis, scanning electron microscope (SEM) observation, energy-dispersive X-ray spectroscopy (EDX) analysis, biomechanical testing, and examination of the coating's mechanical strength have been used to evaluate the value of clinical application of Ta-coated prostheses prepared by a plasma-spraying process. Histopathological observation has demonstrated that the periprosthetic new bone tissues tightly and stably adhere to the Ta coating after the implantation, with no signs of loosening. Early after implantation, there is no significant difference in periprosthetic bone volume and ultimate shear strength between Ta-coated and Ti-coated prostheses (P > 0.05). EDX analysis suggests that the ultimate shear stress does not damage Ta coating. Mechanical strength testing shows that the adhesive strength and Vicker's surface hardness (HV) of the Ta coating are significantly higher than those of the Ti coating (P < 0.01). Ta coating has good stability and bone biocompatibility; the extraordinary physical characteristics of Ta coating have great significance in maintaining prosthetic stability and surface porosity after implantation.

Effect of Microstructure on Stress Corrosion Cracking Behaviour of High Nitrogen Stainless Steel Gas Tungsten Arc Welds

NASA Astrophysics Data System (ADS)

Mohammed, Raffi; Srinivasa Rao, K.; Madhusudhan Reddy, G.

2018-03-01

Present work is aimed to improve stress corrosion cracking resistance of high nitrogen steel and its welds. An attempt to weld high nitrogen steel of 5 mm thick plate using gas tungsten arc welding (GTAW) with three high strength age hardenable fillers i.e., 11-10 PH filler, PH 13- 8Mo and maraging grade of MDN 250 filler is made. Welds were characterized by optical microscopy and scanning electron microscopy. Vickers hardness testing of the welds was carried out to study the mechanical behaviour of welds. Potentio-dynamic polarization studies were done to determine pitting corrosion resistance in aerated 3.5% NaCl solution. Stress corrosion cracking (SCC) testing was carried out using constant load type machine with applied stress of 50% yield strength and in 45% MgCl2 solution boiling at 155°C. The results of the present investigation established that improvement in resistance to stress corrosion cracking was observed for PH 13- 8Mo GTA welds when compared to 11-10 PH and MDN 250 GTA welds. However, All GTA welds failed in the weld interface region. This may be attributed to relatively lower pitting potential in weld interface which acts as active site and the initiation source of pitting.

The Effect of Irradiation Distance on Microhardness of Resin Composites Cured with Different Light Curing Units

PubMed Central

Cekic-Nagas, Isil; Egilmez, Ferhan; Ergun, Gulfem

2010-01-01

Objectives: The aim of this study was to compare the microhardness of five different resin composites at different irradiation distances (2 mm and 9 mm) by using three light curing units (quartz tungsten halogen, light emitting diodes and plasma arc). Methods: A total of 210 disc-shaped samples (2 mm height and 6 mm diameter) were prepared from different resin composites (Simile, Aelite Aesthetic Enamel, Clearfil AP-X, Grandio caps and Filtek Z250). Photoactivation was performed by using quartz tungsten halogen, light emitting diode and plasma arc curing units at two irradiation distances (2 mm and 9 mm). Then the samples (n=7/per group) were stored dry in dark at 37°C for 24 h. The Vickers hardness test was performed on the resin composite layer with a microhardness tester (Shimadzu HMV). Data were statistically analyzed using nonparametric Kruskal Wallis and Mann-Whitney U tests. Results: Statistical analysis revealed that the resin composite groups, the type of the light curing units and the irradiation distances have significant effects on the microhardness values (P<.05). Conclusions: Light curing unit and irradiation distance are important factors to be considered for obtaining adequate microhardness of different resin composite groups. PMID:20922164

Integrated experimental and theoretical approach for corrosion and wear evaluation of laser surface nitrided, Ti-6Al-4V biomaterial in physiological solution.

PubMed

Vora, Hitesh D; Shanker Rajamure, Ravi; Dahotre, Sanket N; Ho, Yee-Hsien; Banerjee, Rajarshi; Dahotre, Narendra B

2014-09-01

A laser based surface nitriding process was adopted to further enhance the osseo-integration, corrosion resistance, and tribological properties of the commonly used bioimplant alloy, Ti-6Al-4V. Earlier preliminary osteoblast, electrochemical, and corrosive wear studies of laser nitrided titanium in simulated body fluid clearly revealed improvement of cell adhesion as well as enhancement in corrosion and wear resistance but mostly lacked the in-depth fundamental understanding behind these improvements. Therefore, a novel integrated experimental and theoretical approach were implemented to understand the physical phenomena behind the improvements and establish the property-structure-processing correlation of nitrided surface. The first principle and thermodynamic calculations were employed to understand the thermodynamic, electronic, and elastic properties of TiN for enthalpy of formation, Gibbs free energy, density of states, and elastic properties of TiN were investigated. Additionally, open circuit potential and cyclic potentio-dynamic polarization tests were carried out in simulated body fluid to evaluate the corrosion resistance that in turn linked with the experimentally measured and computationally predicted surface energies of TiN. From these results, it is concluded that the enhancement in the corrosion resistance after laser nitriding is mainly attributed to the presence of covalent bonding via hybridization among Ti (p) and N (d) orbitals. Furthermore, mechanical properties, such as, Poisson׳s ratio, stiffness, Pugh׳s ductility criteria, and Vicker׳s hardness, predicted from first principle calculations were also correlated to the increase in wear resistance of TiN. All the above factors together seem to have contributed to significant improvement in both wear and corrosion performance of nitride surface compared to the bare Ti-6Al-4V in physiological environment indicating its suitability for bioimplant applications. Copyright © 2014 Elsevier Ltd. All rights reserved.

Experimental Study on Thermal Conductivity and Hardness of Cu and Ni Nanoparticle Packed Bed for Thermoelectric Application

NASA Astrophysics Data System (ADS)

Lin, Zi-Zhen; Huang, Cong-Liang; Zhen, Wen-Kai; Feng, Yan-Hui; Zhang, Xin-Xin; Wang, Ge

2017-03-01

The hot-wire method is applied in this paper to probe the thermal conductivity (TC) of Cu and Ni nanoparticle packed beds (NPBs). A different decrease tendency of TC versus porosity than that currently known is discovered. The relationship between the porosity and nanostructure is investigated to explain this unusual phenomenon. It is found that the porosity dominates the TC of the NPB in large porosities, while the TC depends on the contact area between nanoparticles in small porosities. Meanwhile, the Vickers hardness (HV) of NPBs is also measured. It turns out that the enlarged contact area between nanoparticles is responsible for the rapid increase of HV in large porosity, and the saturated nanoparticle deformation is responsible for the small increase of HV in low porosity. With both TC and HV considered, it can be pointed out that a structure of NPB with a porosity of 0.25 is preferable as a thermoelectric material because of the low TC and the higher hardness. Although Cu and Ni are not good thermoelectric materials, this study is supposed to provide an effective way to optimize thermoelectric figure of merit (ZT) and HV of nanoporous materials prepared by the cold-pressing method.

Effects of various light curing methods on the leachability of uncured substances and hardness of a composite resin.

PubMed

Moon, H-J; Lee, Y-K; Lim, B-S; Kim, C-W

2004-03-01

The purpose of this study was to evaluate the effect of the various light curing units (plasma arc, halogen and light-emitting diodes) and irradiation methods (one-step, two-step and pulse) using different light energy densities on the leachability of unreacted monomers (Bis-GMA and UDMA) and the surface hardness of a composite resin (Z250, 3M). Leachability of the specimens immersed for 7 days in ethanol was analysed by HPLC. Vicker's hardness number (VHN) was measured immediately after curing (IC) and after immersion in ethanol for 7 days. Various irradiation methods with three curing units resulted in differences in the amount of leached monomers and VHN of IC when light energy density was lower than 17.0 J cm(-2) (P = 0.05). However, regardless of curing units and irradiation methods, these results were not different when the time or light energy density increased. When similar light energy density was irradiated (15.6-17.7 J cm(-2)), the efficiency of irradiation methods was different by the following order: one-step > or = two-step > pulse. These results suggest that the amount of leached monomers and VHN were influenced by forming polymer structure in activation and initiation stages of polymerization process with different light source energies and curing times.

Fabrication methods and anisotropic properties of graphite matrix compacts for use in HTGR

NASA Astrophysics Data System (ADS)

Yeo, Sunghwan; Yun, Jihae; Kim, Sungok; Cho, Moon Sung; Lee, Young-Woo

2018-02-01

This study investigated the anisotropic microstructural, mechanical, and thermal properties of fabricated graphite matrix prismatic compacts for High Temperature Gas Cooled Reactor (HTGR) fuel. When the observed alignment of graphite grains and the coke derived from phenolic resin is in the transverse direction, the result is severely anisotropic thermal properties. Compacts with such orientation in the transverse direction exhibited increases of thermal expansion and conductivity up to 5.8 times and 4.82 times, respectively, more than those in the axial direction. The formation of pores due to the pyrolysis of phenolic resin was observed predominantly on upper region of the fabricated compacts. This anisotropic pore formation created anisotropic Vickers hardness on the planes with different directions.

Comparative examination of the microstructure and high temperature oxidation performance of NiCrBSi flame sprayed and pack cementation coatings

NASA Astrophysics Data System (ADS)

Chaliampalias, D.; Vourlias, G.; Pavlidou, E.; Skolianos, S.; Chrissafis, K.; Stergioudis, G.

2009-01-01

Coatings formed from NiCrBSi powder were deposited by thermal spray and pack cementation processes on low carbon steel. The microstructure and morphology of the coatings were studied by scanning electron microscopy (SEM) and X-ray diffraction analysis (XRD). Flame sprayed coatings exhibited high porosity and were mechanically bonded to the substrate while pack cementation coatings were more compact and chemically bonded to the substrate. The microhardness and the high temperature oxidation resistance of the coated samples were evaluated by a Vickers microhardness tester and by thermogravimetric measurements (TG), respectively. Pack cementation coatings showed higher hardness and were more protective to high temperature environments than the flame sprayed coatings.

Cold spray NDE for porosity and other process anomalies

NASA Astrophysics Data System (ADS)

Glass, S. W.; Larche, M. R.; Prowant, M. S.; Suter, J. D.; Lareau, J. P.; Jiang, X.; Ross, K. A.

2018-04-01

This paper describes a technology review of nondestructive evaluation (NDE) methods that can be applied to cold spray coatings. Cold spray is a process for depositing metal powder at high velocity so that it bonds to the substrate metal without significant heating that would be likely to cause additional residual tensile stresses. Coatings in the range from millimeters to centimeters are possible at relatively high deposition rates. Cold spray coatings that may be used for hydroelectric components that are subject to erosion, corrosion, wear, and cavitation damage are of interest. The topic of cold spray NDE is treated generally, however, but may be considered applicable to virtually any cold spray application except where there are constraints of the hydroelectric component application that bear special consideration. Optical profilometry, eddy current, ultrasound, and hardness tests are shown for one set of good, fair, and poor nickel-chrome (NiCr) on 304 stainless steel (304SS) cold spray samples to demonstrate inspection possibilities. The primary indicator of cold spray quality is the cold spray porosity that is most directly measured with witness-sample destructive examinations (DE)—mostly photo-micrographs. These DE-generated porosity values are correlated with optical profilometry, eddy current, ultrasound, and hardness test NDE methods to infer the porosity and other information of interest. These parameters of interest primarily include: • Porosity primarily caused by improper process conditions (temperature, gas velocity, spray standoff, spray angle, powder size, condition, surface cleanliness, surface oxide, etc.) • Presence/absence of the cold spray coating including possible over-sprayed voids • Coating thicknessOptical profilometry measurements of surface roughness trended with porosity plus, if compared with a reference measurement or reference drawing, would provide information on the coating thickness. Ultrasound could provide similar surface profile information plus attenuation measurements trended with porosity. The ultrasound measurements, however, may be limited to geometries where the substrate back-wall is normal to the cold spray surface and not too thick. Eddy current showed a strong correlation with porosity. Eddy currents can also be sensitive to cracks and do not need fluid coupling to make measurements, but are not sensitive to coating thicknesses in most cases. Vickers hardness measurements also tracked well with porosity; however, these types of hardness measurements are also not sensitive to coating thickness. An NDE program may include multiple measurements.

Effect of Heat and Laser Treatment on Cu2S Thin Film Sprayed on Polyimide Substrate

NASA Astrophysics Data System (ADS)

Magdy, Wafaa; Mahmoud, Fawzy A.; Nassar, Amira H.

2018-02-01

Three samples of copper sulfide Cu2S thin film were deposited on polyimide substrate by spray pyrolysis using deposition temperature of 400°C and deposition time of about 45 min. One of the samples was left as deposited, another was heat treated, while the third was laser treated. The structural, surface morphological, optical, mechanical, and electrical properties of the films were investigated. X-ray diffraction (XRD) analysis showed that the copper sulfide films were close to copper-rich phase (Cu2S). Increased crystallite size after heat and laser treatment was confirmed by XRD analysis and scanning electron microscopy. Vickers hardness measurements showed that the samples' hardness values were enhanced with increasing crystallite size, representing an inverse Hall-Petch (H-P) effect. The calculated optical bandgap of the treated films was lower than that of the deposited film. Finally, it was found that both heat and laser treatment enhanced the physical properties of the sprayed Cu2S films on polyimide substrate for use in solar energy applications.

Effects of hydrostatic pressure and biaxial strains on the elastic and electronic properties of t-C8B2N2

NASA Astrophysics Data System (ADS)

Zhu, Haiyan; Shi, Liwei; Li, Shuaiqi; Duan, Yifeng; Zhang, Shaobo; Xia, Wangsuo

2018-04-01

The effects of hydrostatic pressure and biaxial strains on the elastic and electronic properties of a superhard material t-C8B2N2 have been studied using first-principles calculations. The structure is proven to be mechanically and dynamically stable under the applied external forces. All the elastic constants (except C66) and elastic modulus increase (decrease) with increasing pressure and compressive (tensile) biaxial strain ɛxx. A microscopic model is used to calculate the Vicker's hardness of every single bond as well as the crystal. The hardness of t-C8B2N2 (64.7 GPa) exceeds that of c-BN (62 GPa) and increases obviously by employing pressure and compressive ɛxx. Furthermore, the Debye temperature and anisotropy of sound velocities for t-C8B2N2 have been discussed. t-C8B2N2 undergoes an indirect to direct bandgap transition when ɛxx > 2%; however, the indirect bandgap character of the material remains under pressure.

Microstructure and Mechanical Property of 12Cr Oxide Dispersion Strengthened Steel

NASA Astrophysics Data System (ADS)

Xu, Haijian; Lu, Zheng; Jia, Chunyan; Gao, Hao; Liu, Chunming

2016-03-01

Nanostructured oxide dispersion strengthened (ODS) steels with nominal compositions (wt%): Fe-12Cr-2W-0.3Ti-0.3Y2O3 were produced by mechanical alloying and hot isostatic pressing. The microstructure was characterized by means of electron microscopy (EBSD, TEM and HRTEM) and the hardness and the tensile properties at different temperatures were measured. The results showed that the ultimate tensile strength of the fabricated 12Cr-ODS steel reached nearly 1,100 MPa at room temperature and maintained around 340 MPa at 700°C. Nano-oxide particles with size ranging from several nm to 30 nm and the number density was 3.6 × 1020/m3 were observed by TEM. Following heat treatment, including normalizing at 1,100°C for 1 h and tempering at 750°C for 2 h, the average grain size was a little decreased. The number of nano-oxide particles increased and the number density was 8.9 × 1020/m3. Specimens showed much higher ductility and there was a slight increase of ultimate tensile strength and Vickers hardness at the same time.

Growth, structural, thermal, dielectric and nonlinear optical properties of potassium hexachloro cadmate (IV) a novel single crystal

NASA Astrophysics Data System (ADS)

Umarani, P.; Jagannathan, K.

2018-02-01

The Potassium hexachloro cadmate (IV) (PHC) single crystal was grown from the aqueous of the solution by a controlled evaporation method. Single crystal XRD solved the structure. FTIR is used to identify the functional groups of grown crystal. The UV-Vis-NIR spectrometer was used to find out the UV cut off region and to calculate the optical band gap of the Potassium hexachloro cadmate (IV) single crystal. The EDAX spectrum has been used to identify the compounds present in title compound. The TG-DTA profile shows the thermal stability of the grown crystal of Potassium hexachloro cadmate (IV). The Vicker's hardness measurement was used to calculate the material hardness of the title compound. The dielectric loss and constant varied with frequencies and activation energy is also calculated. The solid state parameters like plasma energy, Penn gap, Fermi energy, electronic polarizability using Penn analysis and Clausius-Mossotti equation were also calculated for the title compound. The Z-scan technique is used to calculate the third order nonlinear susceptibility of a real and imaginary part.

Effectiveness of anchovy substrate application on decreasing acid solubility of Sprague Dawley rats’ tooth enamel (in vivo)

NASA Astrophysics Data System (ADS)

Triputra, F.; Puspitawati, R.; Gunawan, H. A.

2017-08-01

Anchovies (Stolephorus insularis), a natural resource of Indonesia, contain fluoride in the form of CaF2 and can function as a fluoridation material to prevent dental caries. The aim of this study is to study the effectiveness of anchovy substrate, through food or topical application, in decreasing the acid solubility of tooth enamel. This research used 14 Sprague Dawley rats as subjects divided into the following 5 groups: baseline, experimental feeding, experimental smearing, and their negative controls. After 15 days of anchovy substrate application, lower incisors were extracted and the acid solubility of enamel was analyzed qualitatively and quantitatively using a stereo microscope and a Micro-Vickers Hardness Tester. Analysis of enamel surface destruction and enamel surface microscopic hardness shifting after a 60 sec application of H2PO4 (50% concentration) resulted in a decrease in acid solubility of enamel treated with anchovy substrate. This result can be seen with both the chewing and smearing method. S. insularis can be used as an alternative material for fluoridation.

Hardening of Metallic Materials Using Plasma Immersion Ion Implantation (PIII)

NASA Astrophysics Data System (ADS)

Xu, Yufan; Clark, Mike; Flanagan, Ken; Milhone, Jason; Nonn, Paul; Forest, Cary

2016-10-01

A new approach of Plasma Immersion Ion Implantation (PIII) has been developed with the Plasma Couette Experiment Upgrade (PCX-U). The new approach efficiently reduces the duty cycle under the same average power for PIII. The experiment uses a Nitrogen plasma at a relatively high density of 1010 1011 cm-3 with ion temperatures of < 2 eV and electron temperature of 5 10 eV. The pulser for this PIII experiment has a maximum negative bias greater than 20kV, with 60Hz frequency and a 8 μs on-time in one working cycle. The samples (Alloy Steel 9310) are analyzed by a Vicker Hardness Tester to study the hardness and X-ray Photoelectron Spectroscopy (XPS) to study implantation density and depth. Different magnetic fields are also applied on samples to reduce the energy loss and secondary emission. Higher efficiency of implantation is expected from this experiment and the results will be presented. Hilldale Undergraduate/Faculty Research Fellowship of University of Wisconsin-Madison; Professor Cary Forest's Kellett Mid-Career Faculty Award.

Microscopic observation of laser glazed yttria-stabilized zirconia coatings

NASA Astrophysics Data System (ADS)

Morks, M. F.; Berndt, C. C.; Durandet, Y.; Brandt, M.; Wang, J.

2010-08-01

Thermal barrier coatings (TBCs) are frequently used as insulation system for hot components in gas-turbine, combustors and power plant industries. The corrosive gases which come from combustion of low grade fuels can penetrate into the TBCs and reach the metallic components and bond coat and cause hot corrosion and erosion damage. Glazing the top coat by laser beam is advanced approach to seal TBCs surface. The laser beam has the advantage of forming a dense thin layer composed of micrograins. Plasma-sprayed yttria-stabilized zirconia (YSZ) coating was glazed with Nd-YAG laser at different operating conditions. The surface morphologies, before and after laser treatment, were investigated by scanning electron microscopy. Laser beam assisted the densification of the surface by remelting a thin layer of the exposed surface. The laser glazing converted the rough surface of TBCs into smooth micron-size grains with size of 2-9 μm and narrow grain boundaries. The glazed surfaces showed higher Vickers hardness compared to as-sprayed coatings. The results revealed that the hardness increases as the grain size decreases.

Nitride alloy layer formation of duplex stainless steel using nitriding process

NASA Astrophysics Data System (ADS)

Maleque, M. A.; Lailatul, P. H.; Fathaen, A. A.; Norinsan, K.; Haider, J.

2018-01-01

Duplex stainless steel (DSS) shows a good corrosion resistance as well as the mechanical properties. However, DSS performance decrease as it works under aggressive environment and at high temperature. At the mentioned environment, the DSS become susceptible to wear failure. Surface modification is the favourable technique to widen the application of duplex stainless steel and improve the wear resistance and its hardness properties. Therefore, the main aim of this work is to nitride alloy layer on the surface of duplex stainless steel by the nitriding process temperature of 400°C and 450°C at different time and ammonia composition using a horizontal tube furnace. The scanning electron microscopy and x-ray diffraction analyzer are used to analyse the morphology, composition and the nitrided alloy layer for treated DSS. The micro hardnesss Vickers tester was used to measure hardness on cross-sectional area of nitrided DSS. After nitriding, it was observed that the hardness performance increased until 1100 Hv0.5kgf compared to substrate material of 250 Hv0.5kgf. The thickness layer of nitride alloy also increased from 5μm until 100μm due to diffusion of nitrogen on the surface of DSS. The x-ray diffraction results showed that the nitride layer consists of iron nitride, expanded austenite and chromium nitride. It can be concluded that nitride alloy layer can be produced via nitriding process using tube furnace with significant improvement of microstructural and hardness properties.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stulikova, Ivana, E-mail: ivana.stulikova@mff.cuni.cz; Smola, Bohumil; Vlach, Martin

Solution treated MgTb3Nd2 alloy (nominal composition in wt.%) (ST) and the alloy prepared by hot extrusion of isostatically pressed powder (PM) were isochronally heat treated and studied by electrical resistivity and hardness measurements and by differential scanning calorimetry. Microstructure development was investigated in transmission electron microscopy. Successive precipitation of transient phases in the sequence β″ (D0{sub 19} plates) → β′(cbco) → β{sub 1} (Mg{sub 3}Gd type, fcc) → β (Mg{sub 5}Gd type, fcc) known from the ST alloy was identified also in the PM alloy. The early precipitation stage (D0{sub 19} clusters) revealed in the ST alloy as well asmore » precipitation of equilibrium β{sub e} phase Mg{sub 41}(Tb,Nd){sub 5} manifest themselves only slightly in the PM alloy. Powder metallurgy route does not change the values of activation energies but shifts the temperature ranges of these processes. Vickers hardness of the as prepared state is higher in the PM alloy and is very resistant against the heat treatment up to 510 °C. Contrary to the ST alloy precipitation due to isochronal annealing does not lead to pronounced hardness changes in the PM alloy. - Highlights: • Powder metallurgy (PM) does not change precipitation sequence in MgTbNd alloy. • Temperature ranges of transient phase precipitations are shifted in PM alloy. • Hardness is resistant against isochronal heat treatment up to 510 °C in the PM alloy. • PM procedure does not change activation energies of precipitation.« less

Evaluation of the effects of the solution used for electrochemical dissolution of nickel-titanium endodontic files on dentine structure, microhardness and cell viability.

PubMed

Amaral, C C F; Ormiga, F; Boldrini, L C; Miranda, P G; Mendonça, T A; Granjeiro, J M; Gomes, J A C P

2018-05-15

To evaluate the effects of the [NaF 12 g/L + NaCl 1 g/L] solution used in the electrochemical dissolution process of fractured endodontic files, as well as its NiTi-containing product, on dentine hardness, topography and human fibroblast viability. Sixty single-rooted human teeth were evaluated for dentine microhardness using the Vickers hardness test and the area and number of dentinal tubules by scanning electron microscopy. The samples were divided according to the dentine surface treatment: distilled water; 17% EDTA; [NaF 12 g/L + NaCl 1 g/L]; and 17% EDTA + [NaF 12 g/L + NaCl 1 g/L]. Thirty-six single-rooted human teeth were divided according to the irrigation protocol: Dulbecco's Modified Eagle's Medium + 10% fetal bovine serum; 5.25% NaOCl; [NaF 12 g/L + NaCl 1 g/L]; and [NaF 12 g/L + NaCl 1 g/L+NiTi]. The extracts in contact with the apical foramen were used in the MTT assay to evaluate human fibroblast viability, with dilutions of 100, 50, 25 and 12.5%. Statistical tests used were paired t-tests, one-way ANOVA, Tukey's test, Kruskal-Wallis test and Dunn's post-test. The [NaF 12 g/L + NaCl 1 g/L] solution did not modify the dentine microhardness or the average dentinal tubule area. However, the EDTA induced changes in the dentine structure and microhardness (p<0.05). The [NaF 12 g/L + NaCl 1 g/L] solution and its NiTi-containing product had lower cytotoxicity than NaOCl at dilutions of 25% and 50% (p<0.01). The [NaF 12 g/L + NaCl 1 g/L] solution did not alter dentine microhardness or damage the dentine structure. It also demonstrated lower cytotoxicity than NaOCl. This article is protected by copyright. All rights reserved. This article is protected by copyright. All rights reserved.

Microhardness evaluation of enamel adjacent to an improved GIC sealant after different enamel pre-treatment procedures.

PubMed

Haznedaroglu, E; Sozkes, S; Mentes, A R

2014-12-01

This in vitro study was carried out to evaluate the microhardness of enamel adjacent to a glass ionomer cement (GIC) with high fluoride content used as a sealant (Fuji Triage, GC Corp., Japan) after laser, bur or air abrasion treatment procedures. 200 freshly extracted non-carious human molars were divided into 10 experimental groups according to the enamel pre-treatment method: A air abrasion (Mach 4.1 Kreativ Inc., USA); AP, Air abrasion + conditioning with 20% polyacrylic acid (GC cavity conditioner); L, Er,Cr:YSGG laser application (Waterlase, Biolase Technology, Inc., San Clemente, USA); LP, Er,Cr:YSGG laser application and fissure conditioning; B, ameloplasty carried out with a diamond bur especially designed for preparing fissures (Komet #8833); BP, ameloplasty + fissure conditioning; P, application of 20% polyacrylic acid and all fissures sealed with GIC; C, no fissure treatment, the material was applied directly to the fissures (control); R, application of 37% orthophosphoric acid and fissures sealed with a resin-based sealant (Fissurit; Voco, Germany) (control); N, no treatment (control). Half of each group of teeth were left in artificial saliva for one month and the rest for three months. The teeth were then sectioned and microhardness was measured using a Vickers test apparatus. Kruskal-Wallis, Mann-Whitney U and Dunn's multiple comparison tests were carried out (5% significance). After one month results regarding hardness at the base and lateral walls of fissures were significantly higher in groups A, AP, L, LP, B, BP, P and C than in groups R and N (p<0.01), but no difference was seen between the treatment procedures. The results after three months produced similar findings with evenly increased values for all groups. The results of this study showed that the tested GIC with a higher fluoride content seemed to improve the enamel hardness of the fissure enamel and could be regarded as an alternative material in cases where resin sealant applications are questionable.

Mechanical behavior of M-Wire and conventional NiTi wire used to manufacture rotary endodontic instruments.

PubMed

Pereira, Erika S J; Gomes, Renata O; Leroy, Agnès M F; Singh, Rupinderpal; Peters, Ove A; Bahia, Maria G A; Buono, Vicente T L

2013-12-01

Comparison of physical and mechanical properties of one conventional and a new NiTi wire, which had received an additional thermomechanical treatment. Specimens of both conventional (NiTi) and the new type of wire, called M-Wire (MW), were subjected to tensile and three-point bending tests, Vickers microhardness measurements, and to rotating-bending fatigue tests at a strain-controlled level of 6%. Fracture surfaces were observed by scanning electron microscopy and the non-deformed microstructures by transmission electron microscopy. The thermomechanical treatment applied to produce the M-Wire apparently increased the tensile strength and Vickers microhardness of the material, but its apparent Young modulus was smaller than that of conventionally treated NiTi. The three-point bending tests showed a higher flexibility for MW which also exhibited a significantly higher number of cycles to failure. M-Wire presented mechanical properties that can render endodontic instruments more flexible and fatigue resistant than those made with conventionally processed NiTi wires. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of storage solutions on microhardness of crown enamel and dentin.

PubMed

Aydın, Berdan; Pamir, Tijen; Baltaci, Aysun; Orman, Mehmet N; Turk, Tugba

2015-01-01

The aim of this study was to determine alterations in microhardness of crown dentin and enamel, after 2 and 12-month storage in de-ionized water, 0.2% glutaraldehyde, Hanks' Balanced Salt Solution (HBSS), 0.1% sodium hypochlorite (NaOCl) or 0.1% thymol. Freshly extracted, nonsterile 60 intact human premolars were distributed to five groups. Six teeth from each group were evaluated after two, and other six teeth were evaluated after 12 months storage. After grinding and polishing of teeth, Vickers hardness was evaluated with making indentations on enamel and dentin, using a pyramid diamond indenter tip exerting 100 g load for 15 s. After 2 months storage in solutions, range of the hardness values (HV) of enamel and dentin were in between 315-357 and 64-67, respectively. However, 12 months storage of the teeth resulted in a statistically significant decrease in microhardness when compared to microhardness of teeth stored for 2 months (P = 0.001). Although the differences were not significant regarding solutions, all solutions decreased the microhardness both in enamel and dentin (P > 0.05). However, decrease in microhardness was relatively less in de-ionized water and thymol solutions while glutaraldehyde decreased microhardness the most: 63% for enamel and 53% for dentin. Microhardness of enamel and dentin was in an acceptable range when teeth were stored for 2 months in de-ionized water, glutaraldehyde, HBSS, NaOCl or in thymol; thus, teeth kept up to 2 months in these solutions can be used for mechanical in vitro tests. However, 12 months storage significantly decreased the microhardness of enamel and dentin.

Characterization of retrieved orthodontic miniscrew implants.

PubMed

Eliades, Theodore; Zinelis, Spiros; Papadopoulos, Moschos A; Eliades, George

2009-01-01

The purposes of this study were to characterize the morphologic, structural, and compositional alterations and to assess any hardness changes in used orthodontic miniscrew implants. Eleven miniscrew implants (Aarhus Anchorage System, Medicon eG, Tuttlingen, Germany) placed in 5 patients were retrieved after successful service of 3.5 to 17.5 months; none showed signs of mobility or failure. These implants, and brand-, type-, and size-matched specimens as controls, were subjected to multi-technique characterization. Optical microscopy indicated loss of gloss with variable discoloration. Scanning electron microscopy and x-ray microanalysis showed morphologic alteration of the miniscrew implant surfaces with integuments formed on the surface. The materials precipitated on the surfaces were sodium, potassium, chlorine, iron, calcium, and phosphorus from the contact of the implant with biologic fluids such as blood and exudates, forming sodium chloride, potassium chloride, and calcium-phosphorus precipitates. The composition of the implant was similar to that of a titanium alloy. X-ray microtomography analysis showed no bulk structure alterations. Vickers microhardness testing showed no increased bulk or surface hardness of the retrieved specimens compared with the controls, excluding the possibility of strain-hardening phenomena as a result of self-tapping and self-drilling placement and related loading conditions. Used titanium-alloy miniscrew implants have morphologic and surface structural alterations including adsorption of an integument that is calcified as a result of contact of the implants with biologic fluids. Randomly organized osseointegration islets on these smooth titanium-alloy miniscrew surfaces might be enhanced by the extended period of retention in alveolar bone in spite of the smooth surface and immediate loading pattern of these implants.

Microstructural Evaluation of Inductively Sintered Aluminum Matrix Nanocomposites Reinforced with Silicon Carbide and/or Graphene Nanoplatelets for Tribological Applications

NASA Astrophysics Data System (ADS)

Islam, Mohammad; Khalid, Yasir; Ahmad, Iftikhar; Almajid, Abdulhakim A.; Achour, Amine; Dunn, Theresa J.; Akram, Aftab; Anwar, Saqib

2018-04-01

Silicon carbide (SiC) nanoparticles (NP) and/or graphene nanoplatelets (GNP) were incorporated into the aluminum matrix through colloidal dispersion and mixing of the powders, followed by consolidation using a high-frequency induction heat sintering process. All the nanocomposite samples exhibited high densification (> 96 pct) with a maximum increase in Vickers microhardness by 92 pct relative to that of pure aluminum. The tribological properties of the samples were determined at the normal frictional forces of 10 and 50 N. At relatively low load of 10 N, the adhesive wear was found to be the predominant wear mechanism, whereas in the case of a 50 N normal load, there was significant contribution from abrasive wear possibly by hard SiC NP. From wear tests, the values for the coefficient of friction (COF) and the normalized wear rate were determined. The improvement in hardness and wear resistance may be attributed to multiple factors, including high relative density, uniform SiC and GNP dispersion in the aluminum matrix, grain refinement through GNP pinning, as well as inhibition of dislocation movement by SiC NP. The nanocomposite sample containing 10 SiC and 0.5 GNP (by wt pct) yielded the maximum wear resistance at 10 N normal load. Microstructural characterization of the nanocomposite surfaces and wear debris was performed using scanning electron microscope (SEM) and transmission electron microscope (TEM). The synergistic effect of the GNP and SiC nanostructures accounts for superior wear resistance in the aluminum matrix nanocomposites.

Microstructural Evaluation of Inductively Sintered Aluminum Matrix Nanocomposites Reinforced with Silicon Carbide and/or Graphene Nanoplatelets for Tribological Applications

NASA Astrophysics Data System (ADS)

Islam, Mohammad; Khalid, Yasir; Ahmad, Iftikhar; Almajid, Abdulhakim A.; Achour, Amine; Dunn, Theresa J.; Akram, Aftab; Anwar, Saqib

2018-07-01

Silicon carbide (SiC) nanoparticles (NP) and/or graphene nanoplatelets (GNP) were incorporated into the aluminum matrix through colloidal dispersion and mixing of the powders, followed by consolidation using a high-frequency induction heat sintering process. All the nanocomposite samples exhibited high densification (> 96 pct) with a maximum increase in Vickers microhardness by 92 pct relative to that of pure aluminum. The tribological properties of the samples were determined at the normal frictional forces of 10 and 50 N. At relatively low load of 10 N, the adhesive wear was found to be the predominant wear mechanism, whereas in the case of a 50 N normal load, there was significant contribution from abrasive wear possibly by hard SiC NP. From wear tests, the values for the coefficient of friction (COF) and the normalized wear rate were determined. The improvement in hardness and wear resistance may be attributed to multiple factors, including high relative density, uniform SiC and GNP dispersion in the aluminum matrix, grain refinement through GNP pinning, as well as inhibition of dislocation movement by SiC NP. The nanocomposite sample containing 10 SiC and 0.5 GNP (by wt pct) yielded the maximum wear resistance at 10 N normal load. Microstructural characterization of the nanocomposite surfaces and wear debris was performed using scanning electron microscope (SEM) and transmission electron microscope (TEM). The synergistic effect of the GNP and SiC nanostructures accounts for superior wear resistance in the aluminum matrix nanocomposites.

Effect of flaw size and temperature on the matrix cracking behavior of a brittle ceramic matrix composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Anandakumar, U.; Webb, J.E.; Singh, R.N.

The matrix cracking behavior of a zircon matrix - uniaxial SCS 6 fiber composite was studied as a function of initial flaw size and temperature. The composites were fabricated by a tape casting and hot pressing technique. Surface flaws of controlled size were introduced using a vicker`s indenter. The composite samples were tested in three point flexure at three different temperatures to study the non steady state and steady state matrix cracking behavior. The composite samples exhibited steady state and non steady matrix cracking behavior at all temperatures. The steady state matrix cracking stress and steady state crack size increasedmore » with increasing temperature. The results of the study correlated well with the results predicted by the matrix cracking models.« less

Effect of cobalt on microstructure and properties of AlCr1.5CuFeNi2Cox high-entropy alloys

NASA Astrophysics Data System (ADS)

Kukshal, Vikas; Patnaik, Amar; Bhat, I. K.

2018-04-01

The present paper investigates the effect of Co addition on the alloying behaviour, microstructure and the resulting properties of cast AlCr1.5CuFeNi2Cox high-entropy alloys intended to be used for high temperature applications. The elements Al, Cr, Cu, Fe, Ni and Co (Purity > 99) weighing approximately 800 g was melted in a high temperature vacuum induction furnace. The microstructure, phase transformation, density, microhardness and compressive strength of the samples were analysed using x-ray diffraction (XRD), scanning electron microscopes (SEM), Vickers microhardness tester and universal Testing machine. The crystalline structure of the alloys exhibits simple FCC and BCC phases. The microstructures investigation of the alloys shows the segregation of copper in the interdendritic region resulting in Cu-rich FCC phase. The addition of Co further enhances the formation of FCC phase resulting in the decrease in micro hardness value of the alloys, which varies from 471 HV to 364 HV with increase in the cobalt content from x = 0 to x = 1 (molar ratio). The similar decreasing trend is also observed for the compressive strength of the alloys.

Characterization of AISI 4140 borided steels

NASA Astrophysics Data System (ADS)

Campos-Silva, I.; Ortiz-Domínguez, M.; López-Perrusquia, N.; Meneses-Amador, A.; Escobar-Galindo, R.; Martínez-Trinidad, J.

2010-02-01

The present study characterizes the surface of AISI 4140 steels exposed to the paste-boriding process. The formation of Fe 2B hard coatings was obtained in the temperature range 1123-1273 K with different exposure times, using a 4 mm thick layer of boron carbide paste over the material surface. First, the growth kinetics of boride layers at the surface of AISI 4140 steels was evaluated. Second, the presence and distribution of alloying elements on the Fe 2B phase was measured using the Glow Discharge Optical Emission Spectrometry (GDOES) technique. Further, thermal residual stresses produced on the borided phase were evaluated by X-ray diffraction (XRD) analysis. The fracture toughness of the iron boride layer of the AISI 4140 borided steels was estimated using a Vickers microindentation induced-fracture testing at a constant distance of 25 μm from the surface. The force criterion of fracture toughness was determined from the extent of brittle cracks, both parallel and perpendicular to the surface, originating at the tips of an indenter impression. The fracture toughness values obtained by the Palmqvist crack model are expressed in the form KC( π/2) > KC > KC(0) for the different applied loads and experimental parameters of the boriding process.

Surface improvement and biocompatibility of TiAl 24Nb 10 intermetallic alloy using rf plasma nitriding

NASA Astrophysics Data System (ADS)

Abd El-Rahman, A. M.; Maitz, M. F.; Kassem, M. A.; El-Hossary, F. M.; Prokert, F.; Reuther, H.; Pham, M. T.; Richter, E.

2007-09-01

The present work describes the surface improvement and biocompatibility of TiAl 24Nb 10 intermetallic alloy using rf plasma nitriding. The nitriding process was carried out at different plasma power from 400 W to 650 W where the other plasma conditions were fixed. Grazing incidence X-ray diffractometry (GIXRD), Auger electron spectroscopy (AES), tribometer and a nanohardness tester were employed to characterize the nitrided layer. Further potentiodynamic polarization method was used to describe the corrosion behavior of the un-nitrided and nitrided alloy. It has been found that the Vickers hardness (HV) and corrosion resistance values of the nitrided layers increase with increasing plasma power while the wear rates of the nitrided layers reduce by two orders of magnitude as compared to those of the un-nitrided layer. This improvement in surface properties of the intermetallic alloy is due to formation of a thin modified layer which is composed of titanium nitride in the alloy surface. Moreover, all modified layers were tested for their sustainability as a biocompatible material. Concerning the application area of biocompatibility, the present treated alloy show good surface properties especially for the nitrided alloy at low plasma power of 400 W.

SPS Fabrication of Tungsten-Rhenium Alloys in Support of NTR Fuels Development

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jonathan A. Webb; Indrajit Charit; Cory Sparks

Abstract. Tungsten metal slugs were fabricated via Spark Plasma Sintering (SPS) of powdered metals at temperatures ranging from 1575 K to 1975 K and hold times of 5 minutes to 30 minutes, using powders with an average diameter of 7.8 ?m. Sintered tungsten specimens were found to have relative densities ranging from 83 % to 94 % of the theoretical density for tungsten. Consolidated specimens were also tested for their Vickers Hardness Number (VHN), which was fitted as a function of relative density; the fully consolidated VHN was extrapolated to be 381.45 kg/mm2. Concurrently, tungsten and rhenium powders with averagemore » respective diameters of 0.5 ?m and 13.3 ?m were pre-processed either by High-Energy-Ball-Milling (HEBM) or by homogeneous mixing to yield W-25at.%Re mixtures. The powder batches were sintered at temperatures of 1975 K and 2175 K for hold times ranging from 0 minutes to 60 minutes yielding relative densities ranging from 94% to 97%. The combination of HEBM and sintering showed a significant decrease in the inter-metallic phases compared to that of the homogenous mixing and sintering.« less

Structure, mechanical and thermal behaviour of mixtures of polyester resin and dental ceramic waste

NASA Astrophysics Data System (ADS)

Peña Rodríguez, G.; Martínez Maldonado, L.; Dulce Moreno, H. J.

2016-02-01

The tensile strength and bending strength, structure and thermal behaviour of mixtures of polyester resin (P-2000) and powders (ASTM sieve 200, <75μm) of dental ceramic wastes (dentals impressions, alginate and gypsum) was reported. The samples consisted of mixtures with percentage weights of 50-50%, 60-40%, 70-30%, 80-20%, 90-10%, where the resin was the majority phase, the Mekc (4% wt) was used as catalyst. The structure was studied using SEM and XRD, the thermal behaviour using DSC, TGA and DMA, while the mechanical strength was tested using standards ASTM D790 and D638. Irregular morphology and presence of small agglomerations was observed, with particle sizes between 29.63 and 38.67μm, the presence of different phases of calcium sulphate was found, and that to the increasing the concentration of the powder, the materials becomes more crystalline, increasing its density. An average service temperature of 69.15±4.60°C was found. Vickers hardness values are reported in ranges from 18.65 to 27.96. Considering the elastic modules was established that the materials become more rigid by having more powder concentration.

Mechanical characterization of hydroxyapatite, thermoelectric materials and doped ceria

NASA Astrophysics Data System (ADS)

Fan, Xiaofeng

For a variety of applications of brittle ceramic materials, porosity plays a critical role structurally and/or functionally, such as in engineered bone scaffolds, thermoelectric materials and in solid oxide fuel cells. The presence of porosity will affect the mechanical properties, which are essential to the design and application of porous brittle materials. In this study, the mechanical property versus microstructure relations for bioceramics, thermoelectric (TE) materials and solid oxide fuel cells were investigated. For the bioceramic material hydroxyapatite (HA), the Young's modulus was measured using resonant ultrasound spectroscopy (RUS) as a function of (i) porosity and (ii) microcracking damage state. The fracture strength was measured as a function of porosity using biaxial flexure testing, and the distribution of the fracture strength was studied by Weibull analysis. For the natural mineral tetrahedrite based solid solution thermoelectric material (Cu10Zn2As4S13 - Cu 12Sb4S13), the elastic moduli, hardness and fracture toughness were studied as a function of (i) composition and (ii) ball milling time. For ZiNiSn, a thermoelectric half-Heusler compound, the elastic modulus---porosity and hardness---porosity relations were examined. For the solid oxide fuel cell material, gadolina doped ceria (GDC), the elastic moduli including Young's modulus, shear modulus, bulk modulus and Poisson's ratio were measured by RUS as a function of porosity. The hardness was evaluated by Vickers indentation technique as a function of porosity. The results of the mechanical property versus microstructure relations obtained in this study are of great importance for the design and fabrication of reliable components with service life and a safety factor. The Weibull modulus, which is a measure of the scatter in fracture strength, is the gauge of the mechanical reliability. The elastic moduli and Poisson's ratio are needed in analytical or numerical models of the thermal and mechanical stresses arising from in-service thermal gradients, thermal transients and/or mechanical loading. Hardness is related to a material's wear resistance and machinability, which are two essential considerations in fabrication and application.

Direct laser metal deposition of WC/Co/Cr powder by means of the functionally graded materials strategy

NASA Astrophysics Data System (ADS)

Angelastro, A.; Campanelli, S. L.

2017-12-01

One of the many applications of direct laser metal deposition (DLMD) is the realization of multilayer thick coatings having particular mechanical characteristics, such as high hardness. The objective of this work was to obtain a thick, very hard and wear resistant coating, containing a high percentage of tungsten carbide (WC), on an AISI 304 stainless steel substrate. In order to achieve this result, a tungsten carbide-cobalt-chrome (WC/Co/Cr) powder was processed by the DLMD method. WC/Co/Cr is a composite widely used as a wear-resistant material for cutting tools, molds, coatings and other severe applications. Because of its high hardness, poor ductility and low thermal expansion coefficient, depositing this material directly on the stainless steel substrate is very difficult. In order to overcome this problem, the strategy of functionally graded materials (FGM) was used. Colmonoy 227-F nickel alloy was chosen for this purpose in order to generate a mixture with the WC/Co/Cr powder. Four different materials were deposited, layer by layer, by mixing Colmonoy 227-F with an increasing amount of WC/Co/Cr powders, until obtaining a thick surface coating with a maximum amount of WC of 77.4 wt%. For each powder mixture, a mathematical model was applied to calculate optimal values of translation speed and overlap percentages. A metallographic examination was performed in order to detect macro- and micro-structures of the different materials. Finally, Vickers micro-hardness was measured at various locations along the transverse section to appreciate the gradual increase of the FGM hardness, starting from the substrate and culminating at the top surface of the last deposited material.

The Structure and Mechanical Properties of High-Strength Bulk Ultrafine-Grained Cobalt Prepared Using High-Energy Ball Milling in Combination with Spark Plasma Sintering

PubMed Central

Marek, Ivo; Vojtěch, Dalibor; Michalcová, Alena; Kubatík, Tomáš František

2016-01-01

In this study, bulk ultrafine-grained and micro-crystalline cobalt was prepared using a combination of high-energy ball milling and subsequent spark plasma sintering. The average grain sizes of the ultrafine-grained and micro-crystalline materials were 200 nm and 1 μm, respectively. Mechanical properties such as the compressive yield strength, the ultimate compressive strength, the maximum compressive deformation and the Vickers hardness were studied and compared with those of a coarse-grained as-cast cobalt reference sample. The bulk ultrafine-grained sample showed an ultra-high compressive yield strength that was greater than 1 GPa, which is discussed with respect to the preparation technique and a structural investigation. PMID:28773514

Ultrasonically set novel NVC-containing glass-ionomer cements for applications in restorative dentistry.

PubMed

Moshaverinia, Alireza; Ansari, Sahar; Moshaverinia, Maryam; Schricker, Scott R; Chee, Winston W L

2011-09-01

The objective of this study is to investigate the effects of application of ultrasound on the physical properties of a novel NVC (N-vinylcaprolactam)-containing conventional glass-ionomer cement (GIC). Experimental GIC (EXP) samples were made from the acrylic acid (AA)-itaconic acid (IA)-NVC synthesized terpolymer with Fuji IX powder in a 3.6:1 P/L ratio as recommended by the manufacturer. Specimens were mixed and fabricated at room temperature and were conditioned in distilled water at 37°C for 1 day up to 4 week. Ultrasound (US) was applied 20 s after mixing by placing the dental scaler tip on the top of the cement and applying light hand pressure to ensure the tip remained in contact with cement without causing any deformation. Vickers hardness was determined using a microhardness tester. The working and setting times were determined using a Gillmore needle. Water sorption was also investigated. Commercial Fuji IX was used as control for comparison (CON). The data obtained for the EXP GIC set through conventional set (CS) and ultrasonically set (US) were compared with the CON group, using one-way ANOVA and the Tukey multiple range test at α = 0.05. Not only ultrasonic (US) application accelerated the curing process of both EXP cement and CON group but also improved the surface hardness of all the specimens. US set samples showed significantly lower water sorption values (P < 0.05) due to improved acid-base reaction within the GIC matrix and accelerated maturation process. According to the statistical analysis of data, significant increase was observed in the surface hardness properties of CS and US specimens both in EXP samples and the CON groups. It was concluded that it is possible to command set GICs by the application of ultrasound, leading to GICs with enhanced physical and handling properties. US application might be a potential way to broaden the clinical applications of conventional GICs in restorative dentistry for procedures such as class V cavity restorations.

The relationship between vickers microhardness and compressive strength of functional surface geopolymers

NASA Astrophysics Data System (ADS)

Subaer, Ekaputri, Januari Jaya; Fansuri, Hamzah; Abdullah, Mustafa Al Bakri

2017-09-01

An experimental study to investigate the relationship between Vickers microhardness and compressive strength of geopolymers made from metakaolin has been conducted. Samples were prepared by using metakaolin activated with a sodium silicate solution at a different ratio of Si to Al and Na to Al and cured at 70oC for one hour. The resulting geopolymers were stored in an open air for 28 days before conducting any measurement. Bulk density and apparent porosity of the samples were measured by using Archimedes's method. Vickers microhardness measurements were performed on a polished surface of geopolymers with a load ranging from 0.3 - 1.0 kg. The topographic of indented samples were examined by using scanning electron microscopy (SEM). Compressive strength of the resulting geopolymers was measured on the cylindrical samples with a ratio of height to the diameter was 2:1. The results showed that the molar ratios of geopolymers compositions play important roles in the magnitude of bulk density, porosity, Vickers's microhardness as well as the compressive strength. The porosity reduced exponentially the magnitude of the strength of geopolymers. It was found that the relationship between Vickers microhardness and compressive strength was linear. At the request of all authors and with the approval of the proceedings editor, article 020188 titled, "The relationship between vickers microhardness and compressive strength of functional surface geopolymers," is being retracted from the public record due to the fact that it is a duplication of article 020170 published in the same volume.

Structural, thermal, laser damage, photoconductivity, NLO and mechanical properties of modified vertical Bridgman method grown AgGa0.5In0.5Se2 single crystal

NASA Astrophysics Data System (ADS)

Vijayakumar, P.; Ramasamy, P.

2016-08-01

AgGa0.5In0.5Se2 single crystal was grown using modified vertical Bridgman method. The structural perfection of the AgGa0.5In0.5Se2 single crystal has been analyzed by high-resolution X-ray diffraction rocking curve measurements. The structural and compositional uniformities of AgGa0.5In0.5Se2 were studied using Raman scattering spectroscopy at room temperature. The FWHM of the Γ1 (W1) and Γ5L (Γ15) measured at different regions of the crystal confirms that the composition throughout its length is fairly uniform. Thermal properties of the as-grown crystal, including specific heat, thermal diffusivity and thermal conductivity have been investigated. The multiple shot surface laser damage threshold value was measured using Nd:YAG laser. Photoconductivity measurements with different temperatures have confirmed the positive photoconducting behavior. Second harmonic generation (SHG) on powder samples has been measured using the Kurtz and Perry technique and the results display that AgGa0.5In0.5Se2 is a phase-matchable NLO material. The hardness behavior has been measured using Vickers micro hardness measurement and the indentation size effect has been observed. The classical Meyer's law, propositional resistance model and modified propositional resistance model have been used to analyse the micro hardness behavior.

Fabrication of modified GIC: GIC-nanoSiO2-HA-ZrO2 using two different mixing methods

NASA Astrophysics Data System (ADS)

Ghazali, Nor Ainon Maziah; Bakar, Wan Zaripah Wan; Rahman, Ismail Ab; Masudi, Sam'an Malik

2017-12-01

Conventional glass ionomer cement (GIC) is among the mostly used material in dentistry but some modifications were needed due to its deficiencies such as low mechanical strength and opacity. In this study, a new nanocomposite, GIC-nanoSiO2-HA-ZrO2 was fabricated whereby zirconia is added to improve the hardness. The nanocomposite of SiO2-HA-ZrO2 was synthesized using two different mixing methods which are one pot and spatulation methods. One pot method involved the addition of zirconia nanopowder during the one pot synthesis of nanoSiO2-HA and spatulation method involved the addition of zirconia nanopowder by controlled grinding process using mortar and pestle. Different weight percentage from 1-20 % of nanoSiO2-HA-ZrO2 was added to GIC and the hardness was analyzed using Vickers Tester. The one pot method recorded the highest and significant hardness value at 3 % addition which is ˜75.27 HV (± 2.48) compared to spatulation method ˜69.53 HV (± 7.78) at p < 0.05. Scanning Electron Microscope image from one pot method showed less agglomeration of the nanopowder and nanozirconia is uniformly distributed. Within the limitation of this study, one pot method produced better GIC-nanoSiO2-HA-ZrO2 composite.

High Elastic Moduli of a 54Al2O3-46Ta2O5 Glass Fabricated via Containerless Processing

PubMed Central

Rosales-Sosa, Gustavo A.; Masuno, Atsunobu; Higo, Yuji; Inoue, Hiroyuki; Yanaba, Yutaka; Mizoguchi, Teruyasu; Umada, Takumi; Okamura, Kohei; Kato, Katsuyoshi; Watanabe, Yasuhiro

2015-01-01

Glasses with high elastic moduli have been in demand for many years because the thickness of such glasses can be reduced while maintaining its strength. Moreover, thinner and lighter glasses are desired for the fabrication of windows in buildings and cars, cover glasses for smart-phones and substrates in Thin-Film Transistor (TFT) displays. In this work, we report a 54Al2O3-46Ta2O5 glass fabricated by aerodynamic levitation which possesses one of the highest elastic moduli and hardness for oxide glasses also displaying excellent optical properties. The glass was colorless and transparent in the visible region, and its refractive index nd was as high as 1.94. The measured Young’s modulus and Vickers hardness were 158.3 GPa and 9.1 GPa, respectively, which are comparable to the previously reported highest values for oxide glasses. Analysis made using 27Al Magic Angle Spinning Nuclear Magnetic Resonance (MAS NMR) spectroscopy revealed the presence of a significantly large fraction of high-coordinated Al in addition to four-coordinated Al in the glass. The high elastic modulus and hardness are attributed to both the large cationic field strength of Ta5+ ions and the large dissociation energies per unit volume of Al2O3 and Ta2O5. PMID:26468639

Novel Zirconia Surface Treatments for Enhanced Osseointegration: Laboratory Characterization

PubMed Central

Ewais, Ola H.; Al Abbassy, Fayza; Ghoneim, Mona M.; Aboushelib, Moustafa N.

2014-01-01

Purpose. The aim of this study was to evaluate three novel surface treatments intended to improve osseointegration of zirconia implants: selective infiltration etching treatment (SIE), fusion sputtering (FS), and low pressure particle abrasion (LPPA). The effects of surface treatments on roughness, topography, hardness, and porosity of implants were also assessed. Materials and Methods. 45 zirconia discs (19 mm in diameter × 3 mm in thickness) received 3 different surface treatments: selective infiltration etching, low pressure particle abrasion with 30 µm alumina, and fusion sputtering while nontreated surface served as control. Surface roughness was evaluated quantitatively using profilometery, porosity was evaluated using mercury prosimetry, and Vickers microhardness was used to assess surface hardness. Surface topography was analyzed using scanning and atomic force microscopy (α = 0.05). Results. There were significant differences between all groups regarding surface roughness (F = 1678, P < 0.001), porosity (F = 3278, P < 0.001), and hardness (F = 1106.158, P < 0.001). Scanning and atomic force microscopy revealed a nanoporous surface characteristic of SIE, and FS resulted in the creation of surface microbeads, while LPPA resulted in limited abrasion of the surface. Conclusion. Within the limitations of the study, changes in surface characteristics and topography of zirconia implants have been observed after different surface treatment approaches. Thus possibilities for enhanced osseointegration could be additionally offered. PMID:25349610

The relationship between Vickers microhardness and compressive strength of functional surface geopolymers

NASA Astrophysics Data System (ADS)

Subaer, Ekaputri, Januari Jaya; Fansuri, Hamzah; Abdullah, Mustafa Al Bakri

2017-09-01

An experimental study to investigate the relationship between Vickers microhardness and compressive strength of geopolymers made from metakaolin has been conducted. Samples were prepared by using metakaolin activated with a sodium silicate solution at a different ratio of Si to Al and Na to Al and cured at 70°C for one hour. The resulting geopolymers were stored in an open air for 28 days before conducting any measurement. Bulk density and apparent porosity of the samples were measured by using Archimedes's method. Vickers microhardness measurements were performed on a polished surface of geopolymers with a load ranging from 0.3 - 1.0 kg. The topographic of indented samples were examined by using scanning electron microscopy (SEM). Compressive strength of the resulting geopolymers was measured on the cylindrical samples with a ratio of height to the diameter was 2:1. The results showed that the molar ratios of geopolymers compositions play important roles in the magnitude of bulk density, porosity, Vickers's microhardness as well as the compressive strength. The porosity reduced exponentially the magnitude of the strength of geopolymers. It was found that the relationship between Vickers microhardness and compressive strength was linear.

Microshear bond strength and finite element analysis of resin composite adhesion to press-on-metal ceramic for repair actions after various conditioning methods.

PubMed

Kanat, Burcu; Cömlekoğlu, M Erhan; Cömlekoğlu, Mine Dündar; Culha, Osman; Ozcan, Mutlu; Güngör, Mehmet Ali

2014-02-01

This study evaluated the repair bond strength of differently surface-conditioned press-on-metal ceramic to repair composites and determined the location of the accumulated stresses by finite element analysis. Press-on-metal ceramic disks (IPS InLine PoM, Ivoclar Vivadent) (N = 45, diameter: 3 mm, height: 2 mm) were randomly divided into 3 groups (n = 15 per group) and conditioned with one of the following methods: 9.5% hydrofluoric acid (HF) (Porcelain etch), tribochemical silica coating (TS) (CoJet), and an unconditioned group acted as the control (C). Each group was divided into three subgroups depending on the repair composite resins: a) Arabesk Top (V, a microhybrid; VOCO), b) Filtek Z250 (F, a hybrid;3M ESPE); c) Tetric EvoCeram (T, a nanohybrid; Ivoclar Vivadent) (n = 5 per subgroup). Repair composites disks (diameter: 1 mm, height: 1 mm) were photopolymerized on each ceramic block. Microshear bond strength (MSB) tests were performed (1 mm/min) and the obtained data were statistically analyzed using 2-way ANOVA and Tukey's post-hoc test (α = 0.05). Failure types were analyzed under SEM. Vickers indentation hardness, Young's modulus, and finite element analysis (FEA) were performed complementary to MSB tests to determine stress accumulation areas. MSB results were significantly affected by the surface conditioning methods (p = 0.0001), whereas the repair composite types did not show a significant effect (p = 0.108). The interaction terms between the repair composite and surface conditioning method were also statistically significant (p = 0.0001). The lowest MSB values (MPa ± SD) were obtained in the control group (V = 4 ± 0.8; F = 3.9 ± 0.7; T = 4.1 ± 0.7) (p < 0.05). While the group treated with T composite resulted in significantly lower MSB values for the HF group (T= 4.1 ± 0.8) compared to those of other composites (V = 8.1 ± 2.6; F = 7.6 ± 2.2) (p < 0.05), there were no significant differences when TS was used as a conditioning method (V = 5 ± 1.7; F = 4.7 ± 1; T = 6.2 ± 0.8) (p > 0.05). The control group presented exclusively adhesive failures. Cohesive failures in composite followed by mixed failure types were more common in HF and TS conditioned groups. Elasticity modulus of the composites were 22.9, 12.09, and 10.41 GPa for F, T, and V, respectively. Vickers hardness of the composites were 223, 232, and 375 HV for V, T, and F, respectively. Von Mises stresses in the FEA analysis for the V and T composites spread over a large area due to the low elastic modulus of the composite, whereas the F composite material accumulated more stresses at the bonded interface. Press-on-metal ceramic could best be repaired using tribochemical silica coating followed by silanization, regardless of the repair composite type in combination with their corresponding adhesive resins, providing that no cohesive ceramic failure was observed.

Ni-Al phase transformation of dual layer coating prepared by pack cementation and electrodeposition

NASA Astrophysics Data System (ADS)

Afandi, A.; Sugiarti, E.; Ekaputra, R.; Sudiro, T.; Thosin, K. A. Z.

2018-03-01

In this work, Fe-Cr alloys were coated via Aluminum (Al) pack cementation, followed by Nickel (Ni) electrodeposition. The process of pack cementation was done with mixing powders of Al, Al203 and NH4Cl with weight percentage of 15%, 85%, and 5% respectively. To control successful Al diffusion to the substrate, pack cementation was conducted for 7 hours with two holding temperatures treatment at 400 °C for 4 hours, and 800 ° C hours for 2 hours. Subsequently, the electrodeposition of Ni was applied with the solution consisting of NiSO4, H3BO3, and NiCl2. The samples were placed in the cathode, and then dipped in the solutions, while Ni plate used as anode. Successfully the samples were coated by dual Al-Ni layers, the samples were slowly heat treated at 900 °C for 10 hours. The inter-diffusion of Al and Ni were characterized with SEM/EDX to investigate the distribution of the elements. Mechanical properties of the coated substrates were analyzed with Hardness Vickers (HV). It was found the hardness of the substrate increased significantly, from originally 255 HV to the 1177 HV after pack cementation. The hardness of the substrates has decreased to 641 HV after Ni plating, but subsequent heat treatment has been able to increase the hardness to 842 HV. This phenomenon can be correlated to the inward Al diffusion, and outward Fe, Cr diffusion. The formation of intermetallic compounds due to Al inward and Fe, Cr outward diffusion were discussed in details.

The effect of annealing on structure and hardness of (Fe-Cr)-50 at.% Al coatings synthesized by mechanical alloying

NASA Astrophysics Data System (ADS)

Ciswandi, Aryanto, Didik; Irmaniar, Tjahjono, Arif; Sudiro, Toto

2018-05-01

In this research, the deposition of (Fe-Cr)-50at.% Al coatings on low carbon steel was carried out by a mechanical alloying (MA) technique. The MA was performed in a shaker mill for 4 hours. Two types of Fe-Cr powders as starting material were used, high purity Fe-Cr powders: (Fe-12.5Cr)-50Al and (Fe-25Cr)-50Al, and Fe-Cr lump powder: (50FeCr)-50Al (in at.%). The coated samples were then annealed in a vacuum furnace at 700°C for 1h. The characterizations of coating structure before and after annealing were studied by XRD and SEM-EDX, while the coating hardness was measured by micro-Vickers hardness tester. Before annealing, all of coating composition were composed mainly of (Fe,Cr)Al phase. After annealing, the FeAl and Fe0.99Cr0.02Al0.99 intermetallic phases was formed in the (Fe-12.5Cr)-50Al and (Fe-25Cr)-50Al coatings. In addition, Fe2CrAlwas also found in the (Fe-25Cr)-50Al coating. Whilethe AlCr2 intermetallic phase was detected as the main phase of (50FeCr)-50Al coating. The cross-sectional microstructure showed that the (Fe-12.5Cr)-50Al and (Fe-25Cr)-50Al coatings have a smoother structure compared to (50FeCr)-50Al coating. The annealing led to intermetallic phase formation and an increasing coating hardness.

Effects of Sn Addition on the Microstructures and Mechanical Properties of Mg-6Zn-3Cu- xSn Magnesium Alloys

NASA Astrophysics Data System (ADS)

Zhang, Tao; Shen, Jun; Sang, Jia-Xin; Li, Yang; He, Pei-Pei

2015-08-01

In this paper, Mg-6Zn-3Cu- xSn (ZC63- xSn) magnesium alloys with different Sn contents (0, 1, 2, 4 wt pct) were fabricated and subjected to different heat treatments. The microstructures and mechanical properties of the obtained ZC63- xSn samples were investigated by optical microscopy, X-ray diffraction, scanning electron microscopy, Vickers hardness testing, and tensile testing. It was found that the As-cast Mg-6Zn-3Cu (ZC63) magnesium alloy mainly contained α-Mg grains and Mg(Zn,Cu) particles. Sn dissolved in α-Mg grains when Sn content was below 2 wt pct while Mg2Sn phase forms in the case of Sn content was above 4 wt pct. Addition of Sn refined both α-Mg grains and Mg(Zn,Cu) particles, and increased the volume fraction of Mg(Zn,Cu) particles. Compared with the Sn-free alloy, the microhardness of Sn-containing alloys increased greatly and that of As-extrude ZC63-4Sn sample achieved the highest value. The strength of ZC63 magnesium alloy was significantly enhanced because of Sn addition, which was attributed to grain refinement strengthening, solid solution strengthening, and precipitation strengthening. Furthermore, the ultimate yield stress, yield strength, and elongation of ZC63- xSn magnesium alloys were increased owing to the deceasing grain size induced by extrusion process.

B2 Grain Growth Behavior of a Ti-22Al-25Nb Alloy Fabricated by Hot Pressing Sintering

NASA Astrophysics Data System (ADS)

Jia, Jianbo; Liu, Wenchao; Xu, Yan; Chen, Chen; Yang, Yue; Luo, Junting; Zhang, Kaifeng

2018-05-01

Grain growth behavior of a powder metallurgy (P/M) Ti-22Al-25Nb alloy was investigated by applying a series of isothermal treatment tests over a wide range of temperatures and holding times. An isothermal treatment scheme was conducted in the B2 phase region (1070-1110 °C) and α 2 + B2 phase region (1010-1050 °C) at holding times of 10, 30 min, 1, 2, and 3 h, respectively. The effects of temperature and holding time on the microstructure evolution and microhardness of the P/M Ti-22Al-25Nb alloy at elevated temperatures were evaluated using optical microscope, scanning electron microscope, x-ray diffraction, and Vickers hardness test techniques. The results revealed that the alloy's treated microstructure was closely linked to temperature and holding time, respectively. The change law of B2 grain growth with holding time and temperature can be well interpreted by the Beck equation and Hillert equation, respectively. The B2 grain growth exponent n and activation energy Q were acquired based on experimental data in the α 2 + B2 and B2 phase regions. In addition, the grain growth contour map for the P/M Ti-22Al-25Nb alloy was constructed to depict variations in B2 grain size based on holding time and temperature.

Microstructure, Wear Resistance and Oxidation Behavior of Ni-Ti-Si Coatings Fabricated on Ti6Al4V by Laser Cladding.

PubMed

Zhuang, Qiaoqiao; Zhang, Peilei; Li, Mingchuan; Yan, Hua; Yu, Zhishui; Lu, Qinghua

2017-10-30

The Ni-Ti-Si composite coatings were successfully fabricated on Ti6Al4V by laser cladding. The microstructure were studied by SEM (scanning electron microscopy) and EDS (energy dispersive spectrometer). It has been found that Ti₂Ni and Ti₅Si₃ phases exist in all coatings, and some samples have TiSi₂ phases. Moreover, due to the existence of these phases, coatings presented relatively higher microhardness than that of the substrate (826 HV (Vickers hardness)) and the microhardness value of coating 3 is about twice larger than that of the substrate. During the dry sliding friction and wear test, due to the distribution of the relatively ductile phase of Ti₂Ni and reinforcement phases of Ti₅Si₃ and TiSi₂, the coatings performed good wear resistance. The oxidation process contains two stages: the rapid oxidation and slow oxidation by high temperature oxidation test at 800 °C for 50 h. Meanwhile, the value of the oxidation weight gain of the substrate is approximately three times larger than that of the coating 4. During the oxidation process, the oxidation film formed on the coating is mainly consisted of TiO₂, Al₂O₃ and SiO₂. Phases Ti₂Ni, Ti₅Si₃, TiSi₂ and TiSi were still found and it could be responsible for the improvement in oxidation resistance of the coatings by laser cladding.

Catalase and sodium fluoride mediated rehabilitation of enamel bleached with 37% hydrogen peroxide.

PubMed

Thakur, Ruchi; Shigli, Anand L; Sharma, Divya; Thakur, Gagan

2015-01-01

Bleaching agents bring about a range of unwanted changes in the physical structure of enamel which needs to be restored qualitatively and timely. Catalase being an antioxidant ensures the effective removal of free radicals and improvement in fluoride mediated remineralization from the enamel microstructure which if retained may harm the integrity and affect the hardness of enamel. Thirty freshly extracted incisors were sectioned to 6 slabs which were divided into 5 groups: Group A, control; Group B, treatment with 37% hydrogen peroxide (HP); Group C, treatment with 37% HP and catalase, Group D, treatment with 37% HP and 5% sodium fluoride application, Group E, treatment with 37% HP followed by catalase and 5% sodium fluoride. Scanning electron microscope and microhardness analysis were done for all slabs. One-way ANOVA test was applied among different groups. Vicker's microhardness number (VHN) of Group B and C was significantly lower. No significant difference between VHN of Group B and C. VHN of Group D was significantly higher than Group A, B, and C; but significantly lower than Group E. VHN of Group E was significantly higher than any other experimental group. One-way ANOVA revealed a highly significant P value (P = 0.0001) and so Tukey's post-hoc Test for the group comparisons was employed. Subsequent treatment of bleached enamel with catalase and fluoride varnish separately results in repairing and significantly increasing the microhardness.

Study of variation in surface morphology, chemical composition, crystallinity and hardness of laser irradiated silver in dry and wet environments

NASA Astrophysics Data System (ADS)

Ali, Nisar; Bashir, Shazia; Umm-i-Kalsoom; Begum, Narjis; Hussain, Tousif

2017-07-01

Variation in surface morphology, chemical composition, crystallinity and hardness of laser irradiated silver in dry and wet ambient environments has been investigated. For this purpose, the silver targets were exposed for various number of laser pulses in ambient environment of air, ethanol and de-ionized water for various number of laser pulses i.e. 500, 1000, 1500 and 2000. Scanning Electron Microscope (SEM) was employed to investigate the surface morphology of irradiated silver. SEM analysis reveals significant surface variations for both dry and wet ambient environments. For lower number of pulses, in air environment significant mass removal is observed but in case of ethanol no significant change in surface morphology is observed. In case of de-ionized water small sized cavities are observed with formation of protrusions with spherical top ends. For higher number of laser pulses, refilling of cavities by shock liquefied material, globules and protrusions are observed in case of dry ablation. For ablation in ethanol porous and coarse periodic ripples are observed whereas, for de-ionized water increasing density of protrusions is observed for higher number of pulses. EDS analysis exhibits the variation in chemical composition along with an enhanced diffusion of oxygen under both ambient conditions. The crystal structure of the exposed targets were explored by X-ray Diffraction (XRD) technique. XRD results support the EDS results. Formation of Ag2O in case of air and ethanol whereas, Ag2O and Ag3O in case of de-ionized water confirms the diffusion of oxygen into the silver surface after irradiation. Vickers Hardness tester was employed to measure the hardness of laser treated targets. Enhanced hardness is observed after irradiation in both dry and wet ambient environments. Initial decrease and then increase in hardness is observed with increase in number of laser pulses in air environment. In case of ethanol, increase in number of laser pulses results in continuous decrease in hardness. Whereas, in case of de-ionized water hardness increases with increase in number of laser pulses.

Fabrication of naturel pumice/hydroxyapatite composite for biomedical engineering.

PubMed

Komur, Baran; Lohse, Tim; Can, Hatice Merve; Khalilova, Gulnar; Geçimli, Zeynep Nur; Aydoğdu, Mehmet Onur; Kalkandelen, Cevriye; Stan, George E; Sahin, Yesim Muge; Sengil, Ahmed Zeki; Suleymanoglu, Mediha; Kuruca, Serap Erdem; Oktar, Faik Nuzhet; Salman, Serdar; Ekren, Nazmi; Ficai, Anton; Gunduz, Oguzhan

2016-07-07

We evaluated the Bovine hydroxyapatite (BHA) structure. BHA powder was admixed with 5 and 10 wt% natural pumice (NP). Compression strength, Vickers micro hardness, Fourier transform infrared spectroscopy, scanning electron microscopy (SEM) and X-ray diffraction studies were performed on the final NP-BHA composite products. The cells proliferation was investigated by MTT assay and SEM. Furthermore, the antimicrobial activity of NP-BHA samples was interrogated. Variances in the sintering temperature (for 5 wt% NP composites) between 1000 and 1300 °C, reveal about 700 % increase in the microhardness (~100 and 775 HV, respectively). Composites prepared at 1300 °C demonstrate the greatest compression strength with comparable result for 5 wt% NP content (87 MPa), which are significantly better than those for 10 wt% and those that do not include any NP (below 60 MPa, respectively). The results suggested the optimal parameters for the preparation of NP-BHA composites with increased mechanical properties and biocompatibility. Changes in micro-hardness and compression strength can be tailored by the tuning the NP concentration and sintering temperature. NP-BHA composites have demonstrated a remarkable potential for biomedical engineering applications such as bone graft and implant.

Evaluation of thermal stress in hydroxyapatite film fabricated by powder jet deposition.

PubMed

Akatsuka, Ryo; Matsumura, Ken; Noji, Miyoko; Kuriyagawa, Tsunemoto; Sasaki, Keiichi

2013-10-01

This study aimed to create a thick hydroxyapatite (HA) film on the surface of a human tooth via a powder jet deposition (PJD) device for dental handpieces, and to examine the microstructural and mechanical properties of the HA film. In particular, the effects of thermal stress on this film were evaluated. The HA film was created by blasting 3.18-μm HA particles, calcinated at 1,200°C, onto the enamel substrate at room temperature and atmospheric pressure. An HA film with an area of 3 mm × 3 mm was prepared and polished. The following HA film parameters were evaluated from the three-dimensional surface profile: surface roughness, Vickers hardness, and bonding strength before and after artificial aging induced by 500 cycles of thermal cycling (5-55°C). The HA particles in the deposited film were densely packed, and the surface of the HA film was unchanged after thermal cycling. There were also no significant differences in the hardness and the bonding strength of the HA film before and after thermal cycling. The HA film created in this study demonstrated excellent microstructural and mechanical properties, even after the application of thermal stress. © 2013 Eur J Oral Sci.

XRD investigation of the Effect of MgO Additives on ZTA-TiO2 Ceramic Composites

NASA Astrophysics Data System (ADS)

Azhar, Ahmad Zahirani Ahmad; Manshor, Hanisah; Ali, Afifah Mohd

2018-01-01

Alumina (Al2O3) based ceramics possess good mechanical properties and suitable for the application of cutting inserts. However, this monolithic ceramics suffer from lack of toughness. Hence, there are some modification were made such as the addition of yttria stabilized zirconia (YSZ) to the Al2O3 helps in increasing the toughness of the Al2O3 ceramics. Some additives such as MgO and TiO2 were used to further improve the mechanical properties of ZTA. In this study, high purity raw materials which consist of ZTA-TiO2 were mixed with different amount of MgO (0.0 - 1.0 wt %). The mixture of materials was going through wet mixing, compaction and pressureless sintering at 1600°C for one hour. The samples were characterized for phase analysis, microstructure, shrinkage rate, bulk density, Vickers hardness and fracture toughness. Based on the XRD analysis results, the secondary phase (MgAl2O4) was detected in the sample with 0.5 wt% of MgO onwards which leads to grains refinement, thus improve the density and hardness of ZTA-TiO2-MgO ceramics composites.

Effects of Wet and Dry Finishing and Polishing on Surface Roughness and Microhardness of Composite Resins

PubMed Central

Nasoohi, Negin; Hoorizad, Maryam

2017-01-01

Objectives: This study aimed to assess the effect of wet and dry finishing and polishing on microhardness and roughness of microhybrid and nanohybrid composites. Materials and Methods: Thirty samples were fabricated of each of the Polofil Supra and Aelite Aesthetic All-Purpose Body microhybrid and Grandio and Aelite Aesthetic Enamel nanohybrid composite resins. Each group (n=30) was divided into three subgroups of D, W and C (n=10). Finishing and polishing were performed dry in group D and under water coolant in group W. Group C served as the control group and did not receive finishing and polishing. Surface roughness of samples was measured by a profilometer and their hardness was measured by a Vickers hardness tester. Data were analyzed using two-way ANOVA (P<0.05). Results: The smoothest surfaces with the lowest microhardness were obtained under Mylar strip without finishing/polishing for all composites (P<0.0001). The highest surface roughness was recorded for dry finishing/polishing for all composites (P<0.0001). Dry finishing/polishing increased the microhardness of all composites (P<0.0001). Conclusions: Dry finishing and polishing increases the microhardness and surface roughness of microhybrid and nanohybrid composite resins. PMID:29104597

Characterization and Surface Treatment of Materials Used in MADEAL S.A. Industry Productive Process of Rims by Plasma Assisted Repetitive Pulsed Arcs Technique

NASA Astrophysics Data System (ADS)

Jiménez, H.; Salazar, V. H.; Devia, A.; Jaramillo, S.; Velez, G.

2006-12-01

A study of materials used in the molds production to aluminium rims manufacture in the MADEAL S.A. factory was carried out for apply a plasma assisted surface treatment consists in growing TiAlN hard coatings that it protects this molds in the productive process. This coating resists high oxidation temperatures, of the other of 800 °C, high hardness (2800 Vickers) and low friction coefficient. A plasma assisted repetitive pulsed arcs mono-evaporator system was used in the grow of the TiAlN coatings, the TiAlN target is a sinterized 50% Ti and 50% Al, in the substrate they were used two types of steel that compose the molds injection pieces for the rims production. These materials were subjected to linear and fluctuating thermal changes in the Bruker axs X-Ray diffractometer temperature chamber, what simulated the molds thermal variation in the rims production process and they were compared with TiAlN coatings subjected to same thermal changes. The Materials characterization, before and later of thermal process, was carried out using XRD, SPM and EDS techniques, to analyze the crystallographic, topographic and chemical surface structure behaviours.

Investigation on synthesis, growth and characterization of CdIn2S2Se2 single crystal grown by vertical Bridgman method

NASA Astrophysics Data System (ADS)

Vijayakumar, P.; Ramasamy, P.

2017-06-01

CdIn2S2Se2 polycrystalline material has been synthesized by melt oscillation method. Vertical Bridgman method was used to grow a good quality CdIn2S2Se2 single crystal. The crystalline phase and growth orientation were confirmed by powder X-ray diffraction pattern and unit cell parameters were determined by single crystal X-ray diffraction analysis. The structural uniformity of CdIn2S2Se2 was studied using Raman scattering spectroscopy at room temperature. The stoichiometric composition variation along the CdIn2S2Se2 was measured using energy dispersive spectrometry. The transmission spectra of CdIn2S2Se2 single crystal gave 42% transmission in the NIR region. Thermal property of CdIn2S2Se2 has been studied using differential thermal analysis. Thermal diffusivity, specific heat capacity and thermal conductivity were also measured. Electrical property was measured using Hall Effect measurement and it confirms the n-type semiconducting nature. The hardness behavior has been measured using Vickers micro hardness measurement and the indentation size effect has been observed.