Sample records for x80 steel pipe

  1. Welding needs specified for X-80 offshore line pipe

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Price, J.C.

    1993-12-20

    High-quality, defect-free welds can be deposited in API Grade 5L X-80 line pipe with pulsed gas-metal-arc welding (GMAW) and shielded metal-arc welding (SMAW) processes. The newly developed Grade X-80 combines higher yield-strength pipe with thinner walls to reduce fabrication costs and improve some projects' economics. Use of X-80 pipe can yield as much as 7.5% cost savings over construction with X-65 steel. Increased demand of natural gas has prompted development of large gas fields which will require large-diameter pipelines at higher operating pressures. API 5L X-80 line pipe could, therefore, become commonplace by the end of the decade if weldingmore » technology can be developed to match mechanical properties without affecting productivity. The paper discusses large-diameter projects, welding processes, GMAW shielding gas, SMAW filler wires, hardness and weldability, toughness and corrosion resistance, economics, and what's been learned.« less

  2. Effect of Pipe Body Alloy on Weldability of X80 Steel

    NASA Astrophysics Data System (ADS)

    Kong, Xianglei; Huang, Guojian; Fu, Kuijun; Liu, Fangfang; Huang, Minghao; Zhang, Yinghui

    Effect of Mo, Ni, and Cr on impact property of pipe seam and heat-affected zone (HAZ) of X80 steel was investigated by thermal simulation test and butt welding test. The results showed that, there was an obvious relationship between strip's composition and the toughness of weld and HAZ, the more content of Mo, Ni and less of Cr in the strip matrix, the better of impact toughness of weld and HAZ. Metallographic microscope was used to compare microstructures of welding specimens, every welded seam microstructure was mainly acicular ferrite (AF) and a little volume of proeutectoid ferrite (PF), and with some granular precipitations on original austenite grain boundary, the difference was that there were more PF and less precipitations of the specimen with more content of Mo, Ni and less of Cr in the strip matrix. Because of the high price of Mo and Ni, alloy design must be considered comprehensively with the cost and property requirements in the production.

  3. Precipitation and Dislocation Strengthening Behaviour of Grade X80 Steel for Pipeline with Strain Based Design

    NASA Astrophysics Data System (ADS)

    Sun, Weihua; Hu, Shu-e.; Li, Guobao; Yu, Hao

    This paper analyzes precipitation and dislocation strengthening behaviors of a 27mm thick Niobium-bearing Grade X80 steel plate for strain based design line pipe manufacture. The steel is produced by thermal-mechanical processing (TMCP) and is characterized with granular bainite and polygonal ferrite microstructure. Mechanical properties of both the steel and the UOE pipe are briefly introduced. Transmission electron microscope (TEM) is used to investigate the fine grain structure, distribution of the precipitates and dislocations in the steel. Precipitate morphologies, volume fractions of M(C,N), M3C, CaS, AlN and Cu are extensively studied respectively by Electrolytic Chemical Phase Analysis (ECPA) and X-ray Small Angle Diffraction (X-ray SAD). Dislocations in the steel are characterized with Positron Annihilation analysis. The results prove that precipitation hardening reveal a 58.1MPa strengthening contribution by the precipitates less than 20nm in size. Dislocation hardening is approximately 176MPa to the present studied steel and 198MPa to the pipe.

  4. Characterization of X80 and X100 Microalloyed Pipeline Steel Using Quantitative X-ray Diffraction

    NASA Astrophysics Data System (ADS)

    Wiskel, J. B.; Li, X.; Ivey, D. G.; Henein, H.

    2018-06-01

    Quantitative X-ray diffraction characterization of four (4) X80 and three (3) X100 microalloyed steels was undertaken. The effect of through-thickness position, processing parameters, and composition on the measured crystallite size, microstrain, and J index (relative magnitude of crystallographic texture) was determined. Microstructure analysis using optical microscopy, scanning electron microscopy, transmission electron microscopy, and electron-backscattered diffraction was also undertaken. The measured value of microstrain increased with increasing alloy content and decreasing cooling interrupt temperature. Microstructural features corresponding to crystallite size in the X80 steels were both above and below the detection limit for quantitative X-ray diffraction. The X100 steels consistently exhibited microstructure features below the crystallite size detection limit. The yield stress of each steel increased with increasing microstrain. The increase in microstrain from X80 to X100 is also associated with a change in microstructure from predominantly polygonal ferrite to bainitic ferrite.

  5. Characterization of Mechanical Properties and Residual Stress in API 5L X80 Steel Welded Joints

    NASA Astrophysics Data System (ADS)

    de Sousa Lins, Amilton; de Souza, Luís Felipe Guimarães; Fonseca, Maria Cindra

    2018-01-01

    The use of high-strength and low-alloy steels, high design factors and increasingly stringent safety requirements have increased the operating pressure levels and, consequently, the need for further studies to avoid and prevent premature pipe failure. To evaluate the possibility of improving productivity in manual arc welding of this type of steel, this work characterizes the mechanical properties and residual stresses in API 5L X80 steel welded joints using the SMAW and FCAW processes. The residual stresses were analyzed using x-ray diffraction with the sin2 ψ method at the top and root of the welded joints in the longitudinal and transverse directions of the weld bead. The mechanical properties of the welded joints by both processes were characterized in terms of tensile strength, impact toughness and Vickers microhardness in the welded and shot peening conditions. A predominantly compressive residual stress was found, and shot peening increased the tensile strength and impact toughness in both welded joints.

  6. Corrosion effect of Bacillus cereus on X80 pipeline steel in a Beijing soil environment.

    PubMed

    Wan, Hongxia; Song, Dongdong; Zhang, Dawei; Du, Cuiwei; Xu, Dake; Liu, Zhiyong; Ding, De; Li, Xiaogang

    2018-06-01

    The corrosion of X80 pipeline steel in the presence of Bacillus cereus (B. cereus) was studied through electrochemical and surface analyses and live/dead staining. Scanning electron microscopy and live/dead straining results showed that a number of B. cereus adhered to the X80 steel. Electrochemical impedance spectroscopy showed that B. cereus could accelerate the corrosion of X80 steel. In addition, surface morphology observations indicated that B. cereus could accelerate pitting corrosion in X80 steel. The depth of the largest pits due to B. cereus was approximately 11.23μm. Many pits were found on the U-shaped bents and cracks formed under stress after 60days of immersion in the presence of B. cereus. These indicate that pitting corrosion can be accelerated by B. cereus. X-ray photoelectron spectroscopy results revealed that NH 4 + existed on the surface of X80 steel. B. cereus is a type of nitrate-reducing bacteria and hence the corrosion mechanism of B. cereus may involve nitrate reduction on the X80 steel. Copyright © 2018 Elsevier B.V. All rights reserved.

  7. Procedures, considerations for welding X-80 line pipe established

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Hillenbrand, H.G.; Niederhoff, K.A.; Hauck, G.

    1997-09-15

    The possibility of manufacturing and laying high-strength Grade X-80 (GRS 550) linepipe has been proven in large projects that have already been implemented. Two welding methods for pipeline construction are well established: manual deposition of root and hot passes with cellulosic electrodes and of filler and cap passes with basic vertical-down electrodes (combined-electrode welding) and mechanized-gas-metal arc welding (GMAW). This is also true for the welding consumables, which have been well-tuned to match the pipe material in strength. The pipe material is suitable for unrestricted use in onshore and offshore applications. The paper discusses higher grades, composition, weldability, welding methods,more » and economics.« less

  8. Elevated temperature mechanical properties of line pipe steels

    NASA Astrophysics Data System (ADS)

    Jacobs, Taylor Roth

    The effects of test temperature on the tensile properties of four line pipe steels were evaluated. The four materials include a ferrite-pearlite line pipe steel with a yield strength specification of 359 MPa (52 ksi) and three 485 MPa (70 ksi) yield strength acicular ferrite line pipe steels. Deformation behavior, ductility, strength, strain hardening rate, strain rate sensitivity, and fracture behavior were characterized at room temperature and in the temperature range of 200--350 °C, the potential operating range for steels used in oil production by the steam assisted gravity drainage process. Elevated temperature tensile testing was conducted on commercially produced as-received plates at engineering strain rates of 1.67 x 10 -4, 8.33 x 10-4, and 1.67 x 10-3 s-1. The acicular ferrite (X70) line pipe steels were also tested at elevated temperatures after aging at 200, 275, and 350 °C for 100 h under a tensile load of 419 MPa. The presence of serrated yielding depended on temperature and strain rate, and the upper bound of the temperature range where serrated yielding was observed was independent of microstructure between the ferrite-pearlite (X52) steel and the X70 steels. Serrated yielding was observed at intermediate temperatures and continuous plastic deformation was observed at room temperature and high temperatures. All steels exhibited a minimum in ductility as a function of temperature at testing conditions where serrated yielding was observed. At the higher temperatures (>275 °C) the X52 steel exhibited an increase in ductility with an increase in temperature and the X70 steels exhibited a maximum in ductility as a function of temperature. All steels exhibited a maximum in flow strength and average strain hardening rate as a function of temperature. The X52 steel exhibited maxima in flow strength and average strain hardening rate at lower temperatures than observed for the X70 steels. For all steels, the temperature where the maximum in both flow

  9. Steel Fibers Reinforced Concrete Pipes - Experimental Tests and Numerical Simulation

    NASA Astrophysics Data System (ADS)

    Doru, Zdrenghea

    2017-10-01

    The paper presents in the first part a state of the art review of reinforced concrete pipes used in micro tunnelling realised through pipes jacking method and design methods for steel fibres reinforced concrete. In part two experimental tests are presented on inner pipes with diameters of 1410mm and 2200mm, and specimens (100x100x500mm) of reinforced concrete with metal fibres (35 kg / m3). In part two experimental tests are presented on pipes with inner diameters of 1410mm and 2200mm, and specimens (100x100x500mm) of reinforced concrete with steel fibres (35 kg / m3). The results obtained are analysed and are calculated residual flexural tensile strengths which characterise the post-cracking behaviour of steel fibres reinforced concrete. In the third part are presented numerical simulations of the tests of pipes and specimens. The model adopted for the pipes test was a three-dimensional model and loads considered were those obtained in experimental tests at reaching breaking forces. Tensile stresses determined were compared with mean flexural tensile strength. To validate tensile parameters of steel fibres reinforced concrete, experimental tests of the specimens were modelled with MIDAS program to reproduce the flexural breaking behaviour. To simulate post - cracking behaviour was used the method σ — ε based on the relationship stress - strain, according to RILEM TC 162-TDF. For the specimens tested were plotted F — δ diagrams, which have been superimposed for comparison with the similar diagrams of experimental tests. The comparison of experimental results with those obtained from numerical simulation leads to the following conclusions: - the maximum forces obtained by numerical calculation have higher values than the experimental values for the same tensile stresses; - forces corresponding of residual strengths have very similar values between the experimental and numerical calculations; - generally the numerical model estimates a breaking force greater

  10. Stress Corrosion Cracking Behavior of X80 Pipeline Steel in Acid Soil Environment with SRB

    NASA Astrophysics Data System (ADS)

    Wang, Dan; Xie, Fei; Wu, Ming; Liu, Guangxin; Zong, Yue; Li, Xue

    2017-06-01

    Self-designed experimental device was adopted to ensure the normal growth of sulphate-reducing bacteria (SRB) in sterile simulated Yingtan soil solution. Stress corrosion cracking (SCC) behavior of X80 pipeline steel in simulated acid soil environment was investigated by electrochemical impedance spectroscopy, slow strain rate test, and scanning electron microscope. Results show that the presence of SRB could promote stress corrosion cracking susceptibility. In a growth cycle, polarization resistance first presents a decrease and subsequently an increase, which is inversely proportional to the quantities of SRB. At 8 days of growth, SRB reach their largest quantity of 1.42 × 103 cells/g. The corrosion behavior is most serious at this time point, and the SCC mechanism is hydrogen embrittlement. In other SRB growth stages, the SCC mechanism of X80 steel is anodic dissolution. With the increasing SRB quantities, X80 steel is largely prone to SCC behavior, and the effect of hydrogen is considerably obvious.

  11. Residual Stress Analysis in Girth-welded Ferritic and Austenitic Steel Pipes Using Neutron and X-Ray Diffraction

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Hempel, Nico; Bunn, Jeffrey R; Nitschke-Pagel, Thomas

    This paper is dedicated to the thorough experimental analysis of the residual stresses in the vicinity of tubular welds and the mechanisms involved in their formation. Pipes made of a ferritic-pearlitic structural steel and an austenitic stainless steel are investigated in this study. The pipes feature a similar geometry and are MAG welded with two passes and comparable parameters. Residual strain mappings are carried out using X-ray and neutron diffraction. The combined use of both techniques permits both near-surface and through-wall analyses of the residual stresses. The findings allow for a consistent interpretation of the mechanisms accounting for the formationmore » of the residual stress fields due to the welding process. Since the results are similar for both materials, it can be concluded that residual stresses induced by phase transformations, which can occur in the structural steel, play a minor role in this regard.« less

  12. 49 CFR 192.105 - Design formula for steel pipe.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 49 Transportation 3 2010-10-01 2010-10-01 false Design formula for steel pipe. 192.105 Section 192... for steel pipe. (a) The design pressure for steel pipe is determined in accordance with the following... § 192.113. T=Temperature derating factor determined in accordance with § 192.115. (b) If steel pipe that...

  13. 49 CFR 192.105 - Design formula for steel pipe.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 3 2014-10-01 2014-10-01 false Design formula for steel pipe. 192.105 Section 192... for steel pipe. (a) The design pressure for steel pipe is determined in accordance with the following... § 192.113. T=Temperature derating factor determined in accordance with § 192.115. (b) If steel pipe that...

  14. 49 CFR 192.105 - Design formula for steel pipe.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 49 Transportation 3 2013-10-01 2013-10-01 false Design formula for steel pipe. 192.105 Section 192... for steel pipe. (a) The design pressure for steel pipe is determined in accordance with the following... § 192.113. T=Temperature derating factor determined in accordance with § 192.115. (b) If steel pipe that...

  15. 49 CFR 192.105 - Design formula for steel pipe.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 49 Transportation 3 2011-10-01 2011-10-01 false Design formula for steel pipe. 192.105 Section 192... for steel pipe. (a) The design pressure for steel pipe is determined in accordance with the following... § 192.113. T=Temperature derating factor determined in accordance with § 192.115. (b) If steel pipe that...

  16. 49 CFR 192.105 - Design formula for steel pipe.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 3 2012-10-01 2012-10-01 false Design formula for steel pipe. 192.105 Section 192... for steel pipe. (a) The design pressure for steel pipe is determined in accordance with the following... § 192.113. T=Temperature derating factor determined in accordance with § 192.115. (b) If steel pipe that...

  17. 49 CFR 192.55 - Steel pipe.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... Other Regulations Relating to Transportation (Continued) PIPELINE AND HAZARDOUS MATERIALS SAFETY ADMINISTRATION, DEPARTMENT OF TRANSPORTATION (CONTINUED) PIPELINE SAFETY TRANSPORTATION OF NATURAL AND OTHER GAS BY PIPELINE: MINIMUM FEDERAL SAFETY STANDARDS Materials § 192.55 Steel pipe. (a) New steel pipe is...

  18. 49 CFR 192.309 - Repair of steel pipe.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 49 Transportation 3 2011-10-01 2011-10-01 false Repair of steel pipe. 192.309 Section 192.309... Lines and Mains § 192.309 Repair of steel pipe. (a) Each imperfection or damage that impairs the serviceability of a length of steel pipe must be repaired or removed. If a repair is made by grinding, the...

  19. 49 CFR 192.309 - Repair of steel pipe.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 3 2014-10-01 2014-10-01 false Repair of steel pipe. 192.309 Section 192.309... Lines and Mains § 192.309 Repair of steel pipe. (a) Each imperfection or damage that impairs the serviceability of a length of steel pipe must be repaired or removed. If a repair is made by grinding, the...

  20. 49 CFR 192.309 - Repair of steel pipe.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 49 Transportation 3 2013-10-01 2013-10-01 false Repair of steel pipe. 192.309 Section 192.309... Lines and Mains § 192.309 Repair of steel pipe. (a) Each imperfection or damage that impairs the serviceability of a length of steel pipe must be repaired or removed. If a repair is made by grinding, the...

  1. 49 CFR 192.309 - Repair of steel pipe.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 3 2012-10-01 2012-10-01 false Repair of steel pipe. 192.309 Section 192.309... Lines and Mains § 192.309 Repair of steel pipe. (a) Each imperfection or damage that impairs the serviceability of a length of steel pipe must be repaired or removed. If a repair is made by grinding, the...

  2. 49 CFR 192.315 - Wrinkle bends in steel pipe.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 49 Transportation 3 2010-10-01 2010-10-01 false Wrinkle bends in steel pipe. 192.315 Section 192... Transmission Lines and Mains § 192.315 Wrinkle bends in steel pipe. (a) A wrinkle bend may not be made on steel... wrinkle bend on steel pipe must comply with the following: (1) The bend must not have any sharp kinks. (2...

  3. 49 CFR 192.315 - Wrinkle bends in steel pipe.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 49 Transportation 3 2013-10-01 2013-10-01 false Wrinkle bends in steel pipe. 192.315 Section 192... Transmission Lines and Mains § 192.315 Wrinkle bends in steel pipe. (a) A wrinkle bend may not be made on steel... wrinkle bend on steel pipe must comply with the following: (1) The bend must not have any sharp kinks. (2...

  4. 49 CFR 192.315 - Wrinkle bends in steel pipe.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 49 Transportation 3 2011-10-01 2011-10-01 false Wrinkle bends in steel pipe. 192.315 Section 192... Transmission Lines and Mains § 192.315 Wrinkle bends in steel pipe. (a) A wrinkle bend may not be made on steel... wrinkle bend on steel pipe must comply with the following: (1) The bend must not have any sharp kinks. (2...

  5. 49 CFR 192.315 - Wrinkle bends in steel pipe.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 3 2014-10-01 2014-10-01 false Wrinkle bends in steel pipe. 192.315 Section 192... Transmission Lines and Mains § 192.315 Wrinkle bends in steel pipe. (a) A wrinkle bend may not be made on steel... wrinkle bend on steel pipe must comply with the following: (1) The bend must not have any sharp kinks. (2...

  6. 49 CFR 192.315 - Wrinkle bends in steel pipe.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 3 2012-10-01 2012-10-01 false Wrinkle bends in steel pipe. 192.315 Section 192... Transmission Lines and Mains § 192.315 Wrinkle bends in steel pipe. (a) A wrinkle bend may not be made on steel... wrinkle bend on steel pipe must comply with the following: (1) The bend must not have any sharp kinks. (2...

  7. Window type: 4x4 multipaned steel window flanked by 1x4 multipaned ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Window type: 4x4 multipaned steel window flanked by 1x4 multipaned steel, casements. Concrete stoop, entry overhang and pipe rail detail also illustrated. Building 36, facing northwest - Harbor Hills Housing Project, 26607 Western Avenue, Lomita, Los Angeles County, CA

  8. Research and Development of Ultra-High Strength X100 Welded Pipe

    NASA Astrophysics Data System (ADS)

    Chuanguo, Zhang; Lei, Zheng; Ping, Hu; Bei, Zhang; Kougen, Wu; Weifeng, Huang

    Ultra-high strength X100 welded pipe can be used in the construction of long distance oil and gas pipeline to improve transmission capacity and reduce operation cost. By using the way of thermo-simulation and pilot rolling, the CCT (Continuous Cooling Transformation) diagram and the relationship between ACC (Accelerated Cooling) parameters, microstructure and mechanical properties were studied for the designed X100 pipeline steel with low carbon, high manganese and niobium micro-alloyed composition in lab. The analysis of CCT diagram indicates that the suitable hardness and microstructure can be obtained in the cooling rate of 20 80°C/sec. The pilot rolling results show that the ACC cooling start temperature below Ar3 phase transformation point is beneficial to increase uniform elongation, and the cooling stop temperature of 150 350°C is helpful to obtain high strength and toughness combination. Based on the research conclusions, the X100 plate and UOE pipe with dimension in O.D.1219×W.T.14.8mm, O.D.1219×W.T.17.8mm, designed for the natural gas transmission pipeline, were trial produced. The manufactured pipe body impact absorbed energy at -10°C is over 250J. The DWTT shear area ratio at 0°C is over 85%. The transverse strength meets the X100 grade requirement, and uniform elongation is over 4%. The X100 plate and UOE pipe with dimension in O.D.711×W.T.20.0mm, O.D.711×W.T.12.5mm, designed for an offshore engineering, were also trial produced. The average impact absorbed energy of pipe body at -30°C is over 200J. The average impact absorbed energy of HAZ (Heat-affected zone) and WM (Welded Seam) at -30°C is over 100J. And the good pipe shapes were obtained

  9. S-N Fatigue and Fatigue Crack Propagation Behaviors of X80 Steel at Room and Low Temperatures

    NASA Astrophysics Data System (ADS)

    Jung, Dae-Ho; Kwon, Jae-Ki; Woo, Nam-Sub; Kim, Young-Ju; Goto, Masahiro; Kim, Sangshik

    2014-02-01

    In the present study, the S-N fatigue and the fatigue crack propagation (FCP) behaviors of American Petroleum Institute X80 steel were examined in the different locations of the base metal (BM), weld metal (WM), and heat-affected zone (HAZ) at 298 K, 223 K, and 193 K (25 °C, -50 °C, and -80 °C). The resistance to S-N fatigue of X80 BM specimen increased greatly with decreasing temperature from 298 K to 193 K (25 °C to -80 °C) and showed a strong dependency on the flow strength (½(yield strength + tensile strength)). The FCP rates of X80 BM specimen were substantially reduced with decreasing temperature from 298 K to 223 K (25 °C to -50 °C) over the entire ∆ K regime, while further reduction in FCP rates was not significant with temperature from 223 K to 193 K (-50 °C to -80 °C). The FCP rates of the X80 BM and the WM specimens were comparable with each other, while the HAZ specimen showed slightly better FCP resistance than the BM and the WM specimens over the entire ∆K regime at 298 K (25 °C). Despite the varying microstructural characteristics of each weld location, the residual stress appeared to be a controlling factor to determine the FCP behavior. The FCP behaviors of high strength X80 steel were discussed based on the microstructural and the fractographic observations.

  10. Corrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment

    PubMed Central

    Li, Zhong; Li, Caiyu; Qian, Hongchang; Li, Jun; Huang, Liang; Du, Cuiwei

    2017-01-01

    The corrosion behavior of X80 steel in the presence of coupled coating defects was simulated and studied under the interference of alternating current (AC) in an alkaline environment. The results from electrochemical measurements showed that the electrode potential of the coating defect with the smaller exposed area was lower than that with the larger area, which indicated that the steel with the smaller coating defect was more prone to corrosion. The result of weight loss tests also showed that the smaller coating defect had induced a higher corrosion rate. However, the corrosion rate of X80 steel at the larger coating defect decreased gradually with the increase of the larger defect area at a constant smaller defect area. The corrosion morphology images showed that the coating defects with smaller areas suffered from more severe pitting corrosion. PMID:28773078

  11. Hydrogen accelerated fatigue crack growth of friction stir welded X52 steel pipe

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Ronevich, Joseph Allen; Somerday, Brian P.; Feng, Zhili

    Friction stir welded steel pipelines were tested in high pressure hydrogen gas to examine the effects of hydrogen accelerated fatigue crack growth. Fatigue crack growth rate (da/dN) vs. stress-intensity factor range (ΔK) relationships were measured for an X52 friction stir welded pipe tested in 21 MPa hydrogen gas at a frequency of 1 Hz and R = 0.5. Tests were performed on three regions: base metal (BM), center of friction stir weld (FSW), and 15 mm off-center of the weld. For all three material regions, tests in hydrogen exhibited accelerated fatigue crack growth rates that exceeded an order of magnitudemore » compared to companion tests in air. Among tests in hydrogen, fatigue crack growth rates were modestly higher in the FSW than the BM and 15 mm off-center tests. Select regions of the fracture surfaces associated with specified ΔK levels were examined which revealed intergranular fracture in the BM and 15 mm off-center specimens but an absence of intergranular features in the FSW specimens. In conclusion, the X52 friction stir weld and base metal tested in hydrogen exhibited fatigue crack growth rate relationships that are comparable to those for conventional arc welded steel pipeline of similar strength found in the literature.« less

  12. Hydrogen accelerated fatigue crack growth of friction stir welded X52 steel pipe

    DOE PAGES

    Ronevich, Joseph Allen; Somerday, Brian P.; Feng, Zhili

    2016-11-17

    Friction stir welded steel pipelines were tested in high pressure hydrogen gas to examine the effects of hydrogen accelerated fatigue crack growth. Fatigue crack growth rate (da/dN) vs. stress-intensity factor range (ΔK) relationships were measured for an X52 friction stir welded pipe tested in 21 MPa hydrogen gas at a frequency of 1 Hz and R = 0.5. Tests were performed on three regions: base metal (BM), center of friction stir weld (FSW), and 15 mm off-center of the weld. For all three material regions, tests in hydrogen exhibited accelerated fatigue crack growth rates that exceeded an order of magnitudemore » compared to companion tests in air. Among tests in hydrogen, fatigue crack growth rates were modestly higher in the FSW than the BM and 15 mm off-center tests. Select regions of the fracture surfaces associated with specified ΔK levels were examined which revealed intergranular fracture in the BM and 15 mm off-center specimens but an absence of intergranular features in the FSW specimens. In conclusion, the X52 friction stir weld and base metal tested in hydrogen exhibited fatigue crack growth rate relationships that are comparable to those for conventional arc welded steel pipeline of similar strength found in the literature.« less

  13. Influence of Heat Input on Microstructure and Toughness Properties in Simulated CGHAZ of X80 Steel Manufactured Using High-Temperature Processing

    NASA Astrophysics Data System (ADS)

    Zhu, Zhixiong; Han, Jian; Li, Huijun

    2015-11-01

    To determine and demonstrate the weldability of high-Nb high-temperature processed (HTP) steels and provide extremely valuable information for future line pipe steel design and general steel manufacture, in the current study the toughness in simulated coarse-grained heat-affected zone (CGHAZ) of an X80 grade steel manufactured using HTP was evaluated. The simulated CGHAZs subjected to thermal cycles with various heat inputs (HIs) (0.8 to 5.0 kJ/mm) were produced using a Gleeble 3500 simulator. The microstructures and corresponding mechanical properties were investigated by means of optical microscopy, scanning electron microscopy, electron backscatter diffraction, hardness testing, and Charpy V-notch (CVN) testing. The microstructural examination shows that the simulated CGHAZs consisted of a bainite-dominant microstructure and relatively low amount (<2 pct) of martensite-austenite (M-A) constituent. The prior austenite grain size was controlled to be 45 to 55 µm at HIs of 0.8 to 3.5 kJ/mm, and remarkably increased to 85 µm at an HI of 5 kJ/mm. The results of CVN testing suggest that superior toughness can be achieved in the studied range of HIs (0.8 to 5 kJ/mm). This is thought to be associated with the combined effects of bainitic microstructure and low M-A fraction as well as comparatively fine austenite grain size in the studied CGHAZs.

  14. 49 CFR 192.111 - Design factor (F) for steel pipe.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 3 2012-10-01 2012-10-01 false Design factor (F) for steel pipe. 192.111 Section...) for steel pipe. (a) Except as otherwise provided in paragraphs (b), (c), and (d) of this section, the... less must be used in the design formula in § 192.105 for steel pipe in Class 1 locations that: (1...

  15. 49 CFR 192.111 - Design factor (F) for steel pipe.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 49 Transportation 3 2013-10-01 2013-10-01 false Design factor (F) for steel pipe. 192.111 Section...) for steel pipe. (a) Except as otherwise provided in paragraphs (b), (c), and (d) of this section, the... less must be used in the design formula in § 192.105 for steel pipe in Class 1 locations that: (1...

  16. 49 CFR 192.111 - Design factor (F) for steel pipe.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 3 2014-10-01 2014-10-01 false Design factor (F) for steel pipe. 192.111 Section...) for steel pipe. (a) Except as otherwise provided in paragraphs (b), (c), and (d) of this section, the... less must be used in the design formula in § 192.105 for steel pipe in Class 1 locations that: (1...

  17. 49 CFR 192.111 - Design factor (F) for steel pipe.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 49 Transportation 3 2011-10-01 2011-10-01 false Design factor (F) for steel pipe. 192.111 Section...) for steel pipe. (a) Except as otherwise provided in paragraphs (b), (c), and (d) of this section, the... less must be used in the design formula in § 192.105 for steel pipe in Class 1 locations that: (1...

  18. 49 CFR 192.109 - Nominal wall thickness (t) for steel pipe.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 49 Transportation 3 2011-10-01 2011-10-01 false Nominal wall thickness (t) for steel pipe. 192.109 Section 192.109 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND... Nominal wall thickness (t) for steel pipe. (a) If the nominal wall thickness for steel pipe is not known...

  19. 49 CFR 192.109 - Nominal wall thickness (t) for steel pipe.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 3 2014-10-01 2014-10-01 false Nominal wall thickness (t) for steel pipe. 192.109 Section 192.109 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND... Nominal wall thickness (t) for steel pipe. (a) If the nominal wall thickness for steel pipe is not known...

  20. 49 CFR 192.109 - Nominal wall thickness (t) for steel pipe.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 49 Transportation 3 2013-10-01 2013-10-01 false Nominal wall thickness (t) for steel pipe. 192.109 Section 192.109 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND... Nominal wall thickness (t) for steel pipe. (a) If the nominal wall thickness for steel pipe is not known...

  1. 49 CFR 192.109 - Nominal wall thickness (t) for steel pipe.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 49 Transportation 3 2010-10-01 2010-10-01 false Nominal wall thickness (t) for steel pipe. 192.109 Section 192.109 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND... Nominal wall thickness (t) for steel pipe. (a) If the nominal wall thickness for steel pipe is not known...

  2. 49 CFR 192.109 - Nominal wall thickness (t) for steel pipe.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 3 2012-10-01 2012-10-01 false Nominal wall thickness (t) for steel pipe. 192.109 Section 192.109 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND... Nominal wall thickness (t) for steel pipe. (a) If the nominal wall thickness for steel pipe is not known...

  3. Research on Buckling State of Prestressed Fiber-Strengthened Steel Pipes

    NASA Astrophysics Data System (ADS)

    Wang, Ruheng; Lan, Kunchang

    2018-01-01

    The main restorative methods of damaged oil and gas pipelines include welding reinforcement, fixture reinforcement and fiber material reinforcement. Owing to the severe corrosion problems of pipes in practical use, the research on renovation and consolidation techniques of damaged pipes gains extensive attention by experts and scholars both at home and abroad. The analysis of mechanical behaviors of reinforced pressure pipelines and further studies focusing on “the critical buckling” and intensity of pressure pipeline failure are conducted in this paper, providing theoretical basis to restressed fiber-strengthened steel pipes. Deformation coordination equations and buckling control equations of steel pipes under the effect of prestress is deduced by using Rayleigh Ritz method, which is an approximation method based on potential energy stationary value theory and minimum potential energy principle. According to the deformation of prestressed steel pipes, the deflection differential equation of prestressed steel pipes is established, and the critical value of buckling under prestress is obtained.

  4. Fracture-Toughness Analysis in Transition-Temperature Region of Three American Petroleum Institute X70 and X80 Pipeline Steels

    NASA Astrophysics Data System (ADS)

    Shin, Sang Yong; Woo, Kuk Je; Hwang, Byoungchul; Kim, Sangho; Lee, Sunghak

    2009-04-01

    The fracture toughness in the transition-temperature region of three American Petroleum Institute (API) X70 and X80 pipeline steels was analyzed in accordance with the American Society for Testing and Materials (ASTM) E1921-05 standard test method. The elastic-plastic cleavage fracture toughness ( K Jc ) was determined by three-point bend tests, using precracked Charpy V-notch (PCVN) specimens; the measured K Jc values were then interpreted by the three-parameter Weibull distribution. The fracture-toughness test results indicated that the master curve and the 98 pct confidence curves explained the variation in the measured fracture toughness well. The reference temperatures obtained from the fracture-toughness test and index temperatures obtained from the Charpy impact test were lowest in the X70 steel rolled in the two-phase region, because this steel had smaller effective grains and the lowest volume fraction of hard phases. In this steel, few hard phases led to a higher resistance to cleavage crack initiation, and the smaller effective grain size led to a higher possibility of crack arrest, thereby resulting in the best overall fracture properties. Measured reference temperatures were then comparatively analyzed with the index temperatures obtained from the Charpy impact test, and the effects of microstructures on these temperatures were discussed.

  5. 49 CFR 192.107 - Yield strength (S) for steel pipe.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 49 Transportation 3 2013-10-01 2013-10-01 false Yield strength (S) for steel pipe. 192.107 Section 192.107 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND HAZARDOUS... (S) for steel pipe. (a) For pipe that is manufactured in accordance with a specification listed in...

  6. 49 CFR 192.107 - Yield strength (S) for steel pipe.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 3 2014-10-01 2014-10-01 false Yield strength (S) for steel pipe. 192.107 Section 192.107 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND HAZARDOUS... (S) for steel pipe. (a) For pipe that is manufactured in accordance with a specification listed in...

  7. 49 CFR 192.107 - Yield strength (S) for steel pipe.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 3 2012-10-01 2012-10-01 false Yield strength (S) for steel pipe. 192.107 Section 192.107 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND HAZARDOUS... (S) for steel pipe. (a) For pipe that is manufactured in accordance with a specification listed in...

  8. 49 CFR 192.107 - Yield strength (S) for steel pipe.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 49 Transportation 3 2010-10-01 2010-10-01 false Yield strength (S) for steel pipe. 192.107 Section 192.107 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND HAZARDOUS... (S) for steel pipe. (a) For pipe that is manufactured in accordance with a specification listed in...

  9. 49 CFR 192.107 - Yield strength (S) for steel pipe.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 49 Transportation 3 2011-10-01 2011-10-01 false Yield strength (S) for steel pipe. 192.107 Section 192.107 Transportation Other Regulations Relating to Transportation (Continued) PIPELINE AND HAZARDOUS... (S) for steel pipe. (a) For pipe that is manufactured in accordance with a specification listed in...

  10. Effect of Alternating Current on the Cathodic Protection and Interface Structure of X80 Steel.

    PubMed

    Wang, Huiru; Du, Cuiwei; Liu, Zhiyong; Wang, Luntao; Ding, De

    2017-07-25

    This study employs potential-monitoring techniques, cyclic voltammetry tests, alternating current (AC) voltammetry methods, and surface characterization to investigate the AC corrosion of cathodically protected X80 pipeline steel. In a non-passive neutral solution at pH 7.2, a sufficiently negative potential completely protects steel at an AC current density of 100 A/m². In an alkaline solution at pH 9.6, more serious AC corrosion occurs at more negative cathodic protection (CP) potential, whereas without CP the steel suffers negligible corrosion. In addition, the interface capacitance increases with AC amplitude. Based on these results, the AC corrosion mechanisms that function under various conditions are analyzed and described.

  11. Effect of Alternating Current on the Cathodic Protection and Interface Structure of X80 Steel

    PubMed Central

    Wang, Huiru; Du, Cuiwei; Liu, Zhiyong; Wang, Luntao; Ding, De

    2017-01-01

    This study employs potential-monitoring techniques, cyclic voltammetry tests, alternating current (AC) voltammetry methods, and surface characterization to investigate the AC corrosion of cathodically protected X80 pipeline steel. In a non-passive neutral solution at pH 7.2, a sufficiently negative potential completely protects steel at an AC current density of 100 A/m2. In an alkaline solution at pH 9.6, more serious AC corrosion occurs at more negative cathodic protection (CP) potential, whereas without CP the steel suffers negligible corrosion. In addition, the interface capacitance increases with AC amplitude. Based on these results, the AC corrosion mechanisms that function under various conditions are analyzed and described. PMID:28773211

  12. Characterization of a carbon fiber reinforced polymer repair system for structurally deficient steel piping

    NASA Astrophysics Data System (ADS)

    Wilson, Jeffrey M.

    This Dissertation investigates a carbon fiber reinforced polymer repair system for structurally deficient steel piping. Numerous techniques exist for the repair of high-pressure steel piping. One repair technology that is widely gaining acceptance is composite over-wraps. Thermal analytical evaluations of the epoxy matrix material produced glass transition temperature results, a cure kinetic model, and a workability chart. These results indicate a maximum glass transition temperature of 80°C (176°F) when cured in ambient conditions. Post-curing the epoxy, however, resulted in higher glass-transition temperatures. The accuracy of cure kinetic model presented is temperature dependent; its accuracy improves with increased cure temperatures. Cathodic disbondment evaluations of the composite over-wrap show the epoxy does not breakdown when subjected to a constant voltage of -1.5V and the epoxy does not allow corrosion to form under the wrap from permeation. Combustion analysis of the composite over-wrap system revealed the epoxy is flammable when in direct contact with fire. To prevent combustion, an intumescent coating was developed to be applied on the composite over-wrap. Results indicate that damaged pipes repaired with the carbon fiber composite over-wrap withstand substantially higher static pressures and exhibit better fatigue characteristics than pipes lacking repair. For loss up to 80 percent of the original pipe wall thickness, the composite over-wrap achieved failure pressures above the pipe's specified minimum yield stress during monotonic evaluations and reached the pipe's practical fatigue limit during cyclical pressure testing. Numerous repairs were made to circular, thru-wall defects and monotonic pressure tests revealed containment up to the pipe's specified minimum yield strength for small diameter defects. The energy release rate of the composite over-wrap/steel interface was obtained from these full-scale, leaking pipe evaluations and results

  13. 76 FR 76437 - Certain Welded Stainless Steel Pipe From Korea and Taiwan

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-12-07

    ... Welded Stainless Steel Pipe From Korea and Taiwan Determination On the basis of the record \\1\\ developed... antidumping duty orders on certain welded stainless steel pipe from Korea and Taiwan would be likely to lead... 2011), entitled Certain Welded Stainless Steel Pipe from Korea and Taiwan, Investigation Nos. 731-TA...

  14. [Effect of chloramines disinfection for biofilm formation control on copper and stainless steel pipe materials].

    PubMed

    Zhou, Ling-ling; Zhang, Yong-ji; Li, Xing; Li, Gui-bai

    2008-12-01

    Two rotating annular bioreactors (RABs) with copper and stainless steel pipe materials were adopted in the study, the effects of these two pipe materials and chloramines disinfection on biofilms formation in drinking water distribution system were evaluated. The maximum viable bacterial number in biofilm of copper and stainless steel reached 5.5 x 10(3) CFU/cm2 and 2.5 x 10(5) CFU/cm2 at 18th and 21st day without chloramines, and the viable bacterial number at the apparent steady state was 1.0 x 10(3) CFU/cm2 and 1.3 x 10(5) CFU/cm2 respectively. It was obvious that the biomass on copper materials was lower than that of the stainless steel. The maximum viable bacterial on copper and stainless steel under chloramines was 5.0 x 10(2) CFU/cm2 and 5.0 x 10(4) CFU/cm2, which was one order of magnitude lower than that of without chloramines, and its number was 10 CFU/cm2 and 3.5 x 10(4) CFU/cm2 at the steady state. These results illustrated that chloramines had apparent ability in controlling biomass when the biofilm was on steady states, especially for copper material. There was exponential relationship between biomass in biofilm and residue chloramines, which meant less biomass with more chloramines, synergistic effects were observed between chloramines and copper materials on biomass in biofilms inactivation.

  15. Investigation on size tolerance of pore defect of girth weld pipe.

    PubMed

    Li, Yan; Shuai, Jian; Xu, Kui

    2018-01-01

    Welding quality control is an important parameter for safe operation of oil and gas pipes, especially for high-strength steel pipes. Size control of welding defect is a bottleneck problem for current pipe construction. As a key part of construction procedure for butt-welding of pipes, pore defects in girth weld is difficult to ignore. A three-dimensional non-linear finite element numerical model is established to study applicability of size control indices based on groove shape and softening phenomenon of material in heat-affected zone of practical pipe girth weld. Taking design criteria of pipe as the basis, basic tensile, extremely tensile and extremely compressive loading conditions are determined for pipe stress analysis, and failure criteria based on flow stress is employed to perform stress analysis for pipe girth weld with pore defect. Results show that pipe girth welding stresses of pores at various radial locations are similar. Whereas, stress for pores of different sharpness varied significantly. Besides, tolerance capability of API 5L X90 grade pipe to pore defect of girth weld is lower than that of API 5L X80 grade pipe, and size control index of 3 mm related to pore defect in current standards is applicable to API 5L X80 and X90 grade girth welded pipes with radially non-sharp pore defects.

  16. Investigation on size tolerance of pore defect of girth weld pipe

    PubMed Central

    Shuai, Jian; Xu, Kui

    2018-01-01

    Welding quality control is an important parameter for safe operation of oil and gas pipes, especially for high-strength steel pipes. Size control of welding defect is a bottleneck problem for current pipe construction. As a key part of construction procedure for butt-welding of pipes, pore defects in girth weld is difficult to ignore. A three-dimensional non-linear finite element numerical model is established to study applicability of size control indices based on groove shape and softening phenomenon of material in heat-affected zone of practical pipe girth weld. Taking design criteria of pipe as the basis, basic tensile, extremely tensile and extremely compressive loading conditions are determined for pipe stress analysis, and failure criteria based on flow stress is employed to perform stress analysis for pipe girth weld with pore defect. Results show that pipe girth welding stresses of pores at various radial locations are similar. Whereas, stress for pores of different sharpness varied significantly. Besides, tolerance capability of API 5L X90 grade pipe to pore defect of girth weld is lower than that of API 5L X80 grade pipe, and size control index of 3 mm related to pore defect in current standards is applicable to API 5L X80 and X90 grade girth welded pipes with radially non-sharp pore defects. PMID:29364986

  17. Automated GMA welding of austenitic stainless steel pipe

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Tahash, G.J.

    1996-12-31

    The study focused on reducing weld cycle times of rotatable subassemblies (spools) using automated welding equipment. A unique automatic Gas Metal Arc Welding (GMAW) system was used to produce a series of pipe to pipe welds on 141 mm (5 in.) schedule 80 seamless stainless steel pipe. After manual tack welding, the adaptive control system welded the root pass of the argon gas backed open vee groove circumferential butt joints in the IG rotated position with short circuiting transfer GMAW. The fill and cover passes were welded automatically with spray transfer GMAW. Automatic welding cycle times were found to bemore » 50--80 percent shorter than the current techniques of roll welding with Shielded Metal Arc Welding and manual Gas Tungsten Arc Welding. Weld costs ({Brit_pounds}/m), including amortization, for the various systems were compared. The cost of automated GMA welds was virtually equivalent to the most competitive methods while depositing 75% more filler metal per year. Also investigated were metallurgical effects generated by weld thermal cycling, and the associated effects on mechanical properties of the weld joint. Mechanical properties of the welds met or exceeded those of the base metal. Sensitization of the pipe did not occur in the heat affected zone (HAZ), based on the absence of evidence of intergranular attack in modified Strauss corrosion tests and despite the fact of interpass temperatures well above recommended maximums. Cooling rates of 3--5 C/s in the heat affected zone of the four pass welds were measured by thermocouple technique and found to be within the non-sensitizing range for this alloy.« less

  18. Concrete filled steel pipe inspection using electro magnetic acoustic transducer (EMAT)

    NASA Astrophysics Data System (ADS)

    Na, Won-Bae; Kundu, Tribikram; Ryu, Yeon-Sun; Kim, Jeong-Tae

    2005-05-01

    Concrete-filled steel pipes are usually exposed in hostile environments such as seawater and deicing materials. The outside corrosion of the steel pipe can reduce the wall thickness and the corrosion-induced delamination of internal concrete can increase internal volume or pressure. In addition, the void that can possibly exist in the pipe reduces the bending resistance. To avoid structural failure due to this type of deterioration, appropriate inspection and repair techniques are to be developed. Guided wave techniques have strong potentials for this kind of inspection because of long-distance inspection capability. Among different transducer-coupling mechanism, electro-magnetic acoustic transducers (EMATs) give relatively consistent results in comparison to piezoelectric transducers since they do not need any couplant. In this study EMATs are used for transmitting and receiving cylindrical guided waves through concrete-filled steel pipes. Through time history curves and wavelet transform, it is shown that EMAT-generated cylindrical guided wave techniques have good potential for the interface inspection of concrete-filled steel pipes.

  19. 77 FR 64468 - Circular Welded Carbon-Quality Steel Pipe From India: Final Affirmative Countervailing Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-10-22

    ...-Quality Steel Pipe From India: Final Affirmative Countervailing Duty Determination AGENCY: Import... exporters of circular welded carbon-quality steel pipe (``circular welded pipe'') from India. For... determination.\\1\\ \\1\\ See Circular Welded Carbon-Quality Steel Pipe From India: Preliminary Affirmative...

  20. Experimental Verification of Steel Pipe Collapse under Vacuum Pressure Conditions

    NASA Astrophysics Data System (ADS)

    Autrique, R.; Rodal, E.

    2016-11-01

    Steel pipes are used widely in hydroelectric systems and in pumping systems. Both systems are subject to hydraulic transient effects caused by changes in boundary conditions, such as sudden valve closures, pump failures, or accidents. Water column separation, and its associated vaporization pressure inside the pipe, can cause the collapse of thin walled steel pipes subject to atmospheric pressure, as happened during the well known Oigawa Power Plant accident in Japan, in 1950. The conditions under which thin walled pipes subject to external pressure can collapse have been studied mathematically since the second half of the XIX century, with classical authors Southwell and Von Mises obtaining definitive equations for long and short pipes in the second decade of the XX century, in which the fundamental variables are the diameter to thickness ratio D/t and the length to diameter ratio L/D. In this paper, the predicted critical D/t ratio for steel pipe collapse is verified experimentally, in a physical model able to reproduce hydraulic transients, generating vacuum pressures through rapid upstream valve closures.

  1. The Role of Hydrogen-Enhanced Strain-Induced Lattice Defects on Hydrogen Embrittlement Susceptibility of X80 Pipeline Steel

    NASA Astrophysics Data System (ADS)

    Hattori, M.; Suzuki, H.; Seko, Y.; Takai, K.

    2017-08-01

    Studies to date have not completely determined the factors influencing hydrogen embrittlement of ferrite/bainite X80 pipeline steel. Hydrogen embrittlement susceptibility was evaluated based on fracture strain in tensile testing. We conducted a thermal desorption analysis to measure the amount of tracer hydrogen corresponding to that of lattice defects. Hydrogen embrittlement susceptibility and the amount of tracer hydrogen significantly increased with decreasing crosshead speed. Additionally, a significant increase in the formation of hydrogen-enhanced strain-induced lattice defects was observed immediately before the final fracture. In contrast to hydrogen-free specimens, the fracture surface of the hydrogen-charged specimens exhibited shallower dimples without nuclei, such as secondary phase particles. These findings indicate that the presence of hydrogen enhanced the formation of lattice defects, particularly just prior to the occurrence of final fracture. This in turn enhanced the formation of shallower dimples, thereby potentially causing premature fracture of X80 pipeline steel at lower crosshead speeds.

  2. Phase constitution characteristics of the Fe-Al alloy layer in the HAZ of calorized steel pipe

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Li Yajiang; Zou Zengda; Wei Xing

    1997-09-01

    Mechanical properties of the welding region and phase constitution characteristics in the iron-aluminum (Fe-Al) alloy layer of calorized steel pipes were researched by means of metallography, which included the use of scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron probe microanalysis (EPMA) and an X-ray diffractometer. Experimental results indicated that the Fe-Al alloy layer of calorized steel pipe was mainly composed of an FeAl phase, an Fe{sub 3}Al phase and an {alpha}-Fe(Al) solid solution, and the microhardness in the Fe-Al coating was 600--310 HM from the surface layer to the inside. There were no higher aluminum content phases, suchmore » as brittle FeAl{sub 2}, Fe{sub 2}Al{sub 5} and FeAl{sub 3}. By controlling the aluminizing process parameters, the ability to bear deformation and weld-ability of the calorized steel pipe were remarkably improved.« less

  3. 49 CFR 192.115 - Temperature derating factor (T) for steel pipe.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 49 Transportation 3 2013-10-01 2013-10-01 false Temperature derating factor (T) for steel pipe. 192.115 Section 192.115 Transportation Other Regulations Relating to Transportation (Continued... § 192.115 Temperature derating factor (T) for steel pipe. The temperature derating factor to be used in...

  4. 49 CFR 192.115 - Temperature derating factor (T) for steel pipe.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 3 2014-10-01 2014-10-01 false Temperature derating factor (T) for steel pipe. 192.115 Section 192.115 Transportation Other Regulations Relating to Transportation (Continued... § 192.115 Temperature derating factor (T) for steel pipe. The temperature derating factor to be used in...

  5. 49 CFR 192.115 - Temperature derating factor (T) for steel pipe.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 3 2012-10-01 2012-10-01 false Temperature derating factor (T) for steel pipe. 192.115 Section 192.115 Transportation Other Regulations Relating to Transportation (Continued... § 192.115 Temperature derating factor (T) for steel pipe. The temperature derating factor to be used in...

  6. 49 CFR 192.115 - Temperature derating factor (T) for steel pipe.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 49 Transportation 3 2011-10-01 2011-10-01 false Temperature derating factor (T) for steel pipe. 192.115 Section 192.115 Transportation Other Regulations Relating to Transportation (Continued... § 192.115 Temperature derating factor (T) for steel pipe. The temperature derating factor to be used in...

  7. 49 CFR 192.115 - Temperature derating factor (T) for steel pipe.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 49 Transportation 3 2010-10-01 2010-10-01 false Temperature derating factor (T) for steel pipe. 192.115 Section 192.115 Transportation Other Regulations Relating to Transportation (Continued... § 192.115 Temperature derating factor (T) for steel pipe. The temperature derating factor to be used in...

  8. 78 FR 45271 - Welded Stainless Steel Pressure Pipe From Malaysia, Thailand, and Vietnam

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-07-26

    ... Stainless Steel Pressure Pipe From Malaysia, Thailand, and Vietnam Determination On the basis of the record... reason of imports from Malaysia, Thailand, and Vietnam of welded stainless steel pressure pipe, provided... pipe from Malaysia, Thailand, and Vietnam. Accordingly, effective May 16, 2013, the Commission...

  9. 75 FR 20342 - Certain Circular Welded Non-Alloy Steel Pipe From Mexico: Final Results of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-04-19

    ...-Alloy Steel Pipe From Mexico: Final Results of Antidumping Duty Administrative Review and Rescission of...- alloy steel pipe from Mexico. See Certain Circular Welded Non-Alloy Steel Pipe From Mexico; Preliminary... remaining three respondents. See Certain Circular Welded Non-Alloy Steel Pipe from Mexico: Notice of Partial...

  10. Development of cryogenic thermal control heat pipes. [of stainless steels

    NASA Technical Reports Server (NTRS)

    1978-01-01

    The development of thermal control heat pipes that are applicable to the low temperature to cryogenic range was investigated. A previous effort demonstrated that stainless steel axially grooved tubing which met performance requirements could be fabricated. Three heat pipe designs utilizing stainless steel axially grooved tubing were fabricated and tested. One is a liquid trap diode heat pipe which conforms to the configuration and performance requirements of the Heat Pipe Experiment Package (HEPP). The HEPP is scheduled for flight aboard the Long Duration Flight Exposure Facility (LDEF). Another is a thermal switch heat pipe which is designed to permit energy transfer at the cooler of the two identical legs. The third thermal component is a hybrid variable conductance heat pipe (VCHP). The design incorporates both a conventional VCHP system and a liquid trap diode. The design, fabrication and thermal testing of these heat pipes is described. The demonstrated heat pipe behavior including start-up, forward mode transport, recovery after evaporator dry-out, diode performance and variable conductance control are discussed.

  11. 78 FR 5170 - Circular Welded Carbon Quality Steel Pipe From the People's Republic of China: Rescission of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-01-24

    ... Steel Tube Manufacturing Co., Ltd., Huludao City Steel Pipe Industrial, Jiangsu Changbao Steel Tube Co... Quality Steel Pipe From the People's Republic of China: Rescission of Antidumping Duty Administrative... of the antidumping duty order on circular welded carbon quality steel pipe from the People's Republic...

  12. 49 CFR 192.113 - Longitudinal joint factor (E) for steel pipe.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 49 Transportation 3 2013-10-01 2013-10-01 false Longitudinal joint factor (E) for steel pipe. 192... § 192.113 Longitudinal joint factor (E) for steel pipe. The longitudinal joint factor to be used in the... class Longitudinal joint factor (E) ASTM A 53/A53M Seamless 1.00 Electric resistance welded 1.00 Furnace...

  13. 49 CFR 192.113 - Longitudinal joint factor (E) for steel pipe.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 3 2012-10-01 2012-10-01 false Longitudinal joint factor (E) for steel pipe. 192... § 192.113 Longitudinal joint factor (E) for steel pipe. The longitudinal joint factor to be used in the... class Longitudinal joint factor (E) ASTM A 53/A53M Seamless 1.00 Electric resistance welded 1.00 Furnace...

  14. 49 CFR 192.113 - Longitudinal joint factor (E) for steel pipe.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 3 2014-10-01 2014-10-01 false Longitudinal joint factor (E) for steel pipe. 192... § 192.113 Longitudinal joint factor (E) for steel pipe. The longitudinal joint factor to be used in the... class Longitudinal joint factor (E) ASTM A 53/A53M Seamless 1.00 Electric resistance welded 1.00 Furnace...

  15. 49 CFR 192.113 - Longitudinal joint factor (E) for steel pipe.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 49 Transportation 3 2011-10-01 2011-10-01 false Longitudinal joint factor (E) for steel pipe. 192... § 192.113 Longitudinal joint factor (E) for steel pipe. The longitudinal joint factor to be used in the... class Longitudinal joint factor (E) ASTM A 53/A53M Seamless 1.00 Electric resistance welded 1.00 Furnace...

  16. 75 FR 69052 - Certain Seamless Carbon and Alloy Steel Standard, Line, and Pressure Pipe From the People's...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-11-10

    ... seamless carbon and alloy steel standard, line, and pressure pipe (``seamless pipe'') from the People's... seamless pipe from the PRC. See Certain Seamless Carbon and Alloy Steel Standard, Line, and Pressure Pipe..., and its negative determination of critical circumstances. See Certain Seamless Carbon and Alloy Steel...

  17. 77 FR 41967 - Certain Circular Welded Carbon Steel Pipes and Tubes From India, Thailand, and Turkey; Certain...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-07-17

    ... Pipes and Tubes From India, Thailand, and Turkey; Certain Circular Welded Non-Alloy Steel Pipe From... on (1) certain circular welded carbon steel pipes and tubes from India, Thailand, and Turkey; (2... circular welded carbon steel pipes and tubes from Turkey would likely lead to continuation or recurrence of...

  18. 78 FR 9676 - Circular Welded Carbon Quality Steel Pipe From the People's Republic of China: Rescission of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-02-11

    ... Tube Manufacturing Co., Ltd.; Huludao City Steel Pipe Industrial; Jiangsu Changbao Steel Tube Co., Ltd... Quality Steel Pipe From the People's Republic of China: Rescission of Countervailing Duty Administrative... countervailing duty order on circular welded carbon quality steel pipe from the People's Republic of China (``PRC...

  19. 77 FR 36256 - Circular Welded Carbon-Quality Steel Pipe From India: Postponement of Final Determination of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-06-18

    ...-Quality Steel Pipe From India: Postponement of Final Determination of Antidumping Duty Investigation...- quality steel pipe from India.\\1\\ On June 1, 2012, the Department published its preliminary determination... is currently due on August 6, 2012. \\1\\ See Circular Welded Carbon-Quality Steel Pipe from India, the...

  20. 75 FR 69626 - Certain Welded Carbon Steel Standard Pipes and Tubes From India: Final Results of Antidumping...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-11-15

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-533-502] Certain Welded Carbon Steel... order on certain welded carbon steel standard pipes and tubes from India. The period of review is May 1... carbon steel standard pipes and tubes from India. See Certain Welded Carbon Steel Standard Pipes and...

  1. Drop Weight Impact Behavior of Al-Si-Cu Alloy Foam-Filled Thin-Walled Steel Pipe Fabricated by Friction Stir Back Extrusion

    NASA Astrophysics Data System (ADS)

    Hangai, Yoshihiko; Nakano, Yukiko; Utsunomiya, Takao; Kuwazuru, Osamu; Yoshikawa, Nobuhiro

    2017-02-01

    In this study, Al-Si-Cu alloy ADC12 foam-filled thin-walled stainless steel pipes, which exhibit metal bonding between the ADC12 foam and steel pipe, were fabricated by friction stir back extrusion. Drop weight impact tests were conducted to investigate the deformation behavior and mechanical properties of the foam-filled pipes during dynamic compression tests, which were compared with the results of static compression tests. From x-ray computed tomography observation, it was confirmed that the fabricated foam-filled pipes had almost uniform porosity and pore size distributions. It was found that no scattering of the fragments of collapsed ADC12 foam occurred for the foam-filled pipes owing to the existence of the pipe surrounding the ADC12 foam. Preventing the scattering of the ADC12 foam decreases the drop in stress during dynamic compression tests and therefore improves the energy absorption properties of the foam.

  2. Numerical simulation of X90 UOE pipe forming process

    NASA Astrophysics Data System (ADS)

    Zou, Tianxia; Ren, Qiang; Peng, Yinghong; Li, Dayong; Tang, Ding; Han, Jianzeng; Li, Xinwen; Wang, Xiaoxiu

    2013-12-01

    The UOE process is an important technique to manufacture large-diameter welding pipes which are increasingly applied in oil pipelines and offshore platforms. The forming process of UOE mainly consists of five successive operations: crimping, U-forming, O-forming, welding and mechanical expansion, through which a blank is formed into a pipe in a UOE pipe mill. The blank with an appropriate edge bevel is bent into a cylindrical shape by crimping (C-forming), U-forming and O-forming successively. After the O-forming, there is an open-seam between two ends of the plate. Then, the blank is welded by automatic four-electrode submerged arc welding technique. Subsequently, the welded pipe is expanded with a mechanical expander to get a high precision circular shape. The multiple operations in the UOE mill make it difficult to control the quality of the formed pipe. Therefore, process design mainly relies on experience in practical production. In this study, the UOE forming of an API X90 pipe is studied by using finite element simulation. The mechanical properties tests are performed on the API X90 pipeline steel blank. A two-dimensional finite element model under the hypothesis of plane strain condition is developed to simulate the UOE process according to data coming from the workshop. A kinematic hardening model is used in the simulation to take the Bauschinger effect into account. The deformation characteristics of the blank during the forming processes are analyzed. The simulation results show a significant coherence in the geometric configurations comparing with the practical manufacturing.

  3. 76 FR 76944 - Circular Welded Carbon Quality Steel Pipe From the People's Republic of China: Rescission of the...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-12-09

    ... Zhongyuan Steel Pipe Manufacturer (``Hebei Zhongyuan''), Hefei Zijin Steel Tube Manufacturing Co., Ltd... Quality Steel Pipe From the People's Republic of China: Rescission of the 2010-2011 Antidumping Duty... antidumping duty order on circular welded carbon quality steel pipe (``CWP'') from the People's Republic of...

  4. Welding High Strength Modern Line Pipe Steel

    NASA Astrophysics Data System (ADS)

    Goodall, Graeme Robertson

    The effect of modern mechanized girth welding on high strength line pipe has been investigated. The single cycle grain coarsened heat affected zone in three grade 690 line pipe steels and a grade 550 steel has been simulated using a Gleeble thermo-mechanical simulator. The continuous cooling transformation diagrams applicable to the grain coarsened heat affected zone resulting from a range of heat inputs applicable to modern mechanized welding have been established by dilatometry and metallography. The coarse grained heat affected zone was found to transform to lath martensite, bainite, and granular bainite depending on the cooling rate. The impact toughness of the steels was measured using Charpy impact toughness and compared to the toughness of the grain coarsened heat affected zone corresponding to a welding thermal cycle. The ductile to brittle transition temperature was found to be lowest for the steel with the highest hardenability. The toughness resulting from three different thermal cycles including a novel interrupted intercritically reheated grain coarsened (NTR ICR GC HAZ) that can result from dual torch welding at fast travel speed and close torch spacing have been investigated. All of the thermally HAZ regions showed reduced toughness that was attributed to bainitic microstructure and large effective grain sizes. Continuous cooling transformation diagrams for five weld metal chemistries applicable to mechanized pulsed gas metal arc welding of modern high strength pipe steel (SMYS>550 MPa) have been constructed. Welds at heat inputs of 1.5 kJmm-1 and 0.5 kJmm-1 have been created for simulation and analysis. Dilatometric analysis was performed on weld metal specimens cut from single pass 1.5 kJmm-1 as deposited beads. The resulting microstructures were found to range from martensite to polygonal ferrite. There is excellent agreement between the simulated and as deposited weld metal regions. Toughness testing indicates improved energy absorption at -20

  5. 76 FR 76939 - Certain Welded Carbon Steel Pipe and Tube From Turkey: Notice of Final Results of Antidumping...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-12-09

    ... Pipe and Tube From Turkey: Notice of Final Results of Antidumping Duty Administrative Review AGENCY... antidumping duty administrative review of certain welded carbon steel pipe and tube from Turkey. The... carbon steel pipe and tube from Turkey. See Certain Welded Carbon Steel Pipe and Tube from Turkey; Notice...

  6. 75 FR 13255 - Certain Seamless Carbon and Alloy Steel Standard, Line, and Pressure Pipe from the People's...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-03-19

    ... seamless carbon and alloy steel standard, line, and pressure pipe (``seamless pipe'') from the People's... countervailing duty investigations of seamless pipe from the PRC. See Certain Seamless Carbon and Alloy Steel... Investigation, 74 FR 52744 (October 14, 2009) and Certain Seamless Carbon and Alloy Steel Standard, Line, and...

  7. 76 FR 66893 - Certain Circular Welded Carbon Steel Pipes and Tubes From India, Thailand, and Turkey; Final...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-10-28

    ...] Certain Circular Welded Carbon Steel Pipes and Tubes From India, Thailand, and Turkey; Final Results of... circular welded carbon steel pipes and tubes from India, Thailand, and Turkey, pursuant to section 751(c..., Thailand, and Turkey. See Antidumping Duty Order; Certain Welded Carbon Steel Standard Pipes and Tubes from...

  8. 76 FR 31940 - Circular Welded Non-Alloy Steel Pipe From Taiwan: Notice of Rescission of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-06-02

    ... Steel Pipe From Taiwan: Notice of Rescission of Antidumping Duty Administrative Review AGENCY: Import... review of the antidumping duty order on circular welded non-alloy steel pipe from Taiwan. The period of... review of the antidumping duty order on circular welded non-alloy steel pipe from Taiwan. See Antidumping...

  9. 77 FR 64483 - Circular Welded Carbon-Quality Steel Pipe from the Socialist Republic of Vietnam: Notice of Final...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-10-22

    ... Pipe from the Socialist Republic of Vietnam;'' ``Verification of the Sales Response of Midwest Air... Steel Joint Stock Company.... Sun Steel Joint Stock 4.57 Company. Huu Lien Asia Corporation........ Huu Lien Asia 4.57 Corporation. Hoa Phat Steel Pipe Co Hoa Phat Steel Pipe Co.. 4.57 Vietnam-Wide Rate \\13...

  10. 77 FR 65712 - Circular Welded Carbon-Quality Steel Pipe From Vietnam; Termination of Investigation

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-10-30

    ... INTERNATIONAL TRADE COMMISSION [Investigation No. 701-TA-485 (Final)] Circular Welded Carbon-Quality Steel Pipe From Vietnam; Termination of Investigation AGENCY: United States International Trade... carbon-quality steel pipe from Vietnam (investigation No. 701-TA-485 (Final)) is terminated. DATES...

  11. 78 FR 21105 - Circular Welded Carbon Steel Pipes and Tubes From Thailand: Preliminary Results of Antidumping...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-04-09

    ... Pipes and Tubes From Thailand: Preliminary Results of Antidumping Duty Administrative Review; 2011- 2012... on circular welded carbon steel pipes and tubes from Thailand. This review covers two producers... welded carbon steel pipes and tubes from Thailand.\\1\\ The merchandise is classifiable under the...

  12. Finite element residual stress analysis of induction heating bended ferritic steel piping

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Kima, Jong Sung; Kim, Kyoung-Soo; Oh, Young-Jin

    2014-10-06

    Recently, there is a trend to apply the piping bended by induction heating process to nuclear power plants. Residual stress can be generated due to thermo-mechanical mechanism during the induction heating bending process. It is well-known that the residual stress has important effect on crack initiation and growth. The previous studies have focused on the thickness variation. In part, some studies were performed for residual stress evaluation of the austenitic stainless steel piping bended by induction heating. It is difficult to find the residual stresses of the ferritic steel piping bended by the induction heating. The study assessed the residualmore » stresses of induction heating bended ferriticsteel piping via finite element analysis. As a result, it was identified that high residual stresses are generated on local outersurface region of the induction heating bended ferritic piping.« less

  13. 75 FR 28557 - Circular Welded Carbon Steel Pipes and Tubes From Thailand: Extension of Time Limit for Final...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-05-21

    ... Steel Pipes and Tubes From Thailand: Extension of Time Limit for Final Results of Antidumping Duty... carbon steel pipes and tubes from Thailand. See Circular Welded Carbon Steel Pipes and Tubes from Thailand: Preliminary Results and Rescission, in Part, of Antidumping Duty Administrative Review, 75 FR...

  14. 75 FR 18788 - Circular Welded Carbon Steel Pipes and Tubes from Thailand: Preliminary Results and Rescission...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-04-13

    ... Pipes and Tubes from Thailand: Preliminary Results and Rescission, in Part, of Antidumping Duty... review of the antidumping duty order on circular welded carbon steel pipes and tubes from Thailand, in... welded carbon steel pipes and tubes from Thailand. See Antidumping Duty Order: Circular Welded Carbon...

  15. 77 FR 24459 - Stainless Steel Butt-Weld Pipe Fittings From Italy: Final Results of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-04-24

    ... CR, of wrought austenitic stainless steel fittings of seamless and welded construction covered by the... DEPARTMENT OF COMMERCE International Trade Administration [A-475-828] Stainless Steel Butt-Weld... administrative review of the antidumping duty order on stainless steel butt-weld pipe fittings (SSBW pipe...

  16. 77 FR 42697 - Stainless Steel Butt-Weld Pipe Fittings From Italy, Malaysia, and the Philippines: Continuation...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-07-20

    ...] Stainless Steel Butt-Weld Pipe Fittings From Italy, Malaysia, and the Philippines: Continuation of.... International Trade Commission that revocation of the antidumping duty orders on stainless steel butt-weld pipe... from Italy, Malaysia, and the Philippines.\\2\\ \\1\\ See Antidumping Duty Orders: Stainless Steel Butt...

  17. 75 FR 76025 - Stainless Steel Butt-Weld Pipe Fittings From Japan, Korea, and Taiwan

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-12-07

    ... INTERNATIONAL TRADE COMMISSION [Investigation Nos. 731-TA-376 and 563-564 (Third Review)] Stainless Steel Butt-Weld Pipe Fittings From Japan, Korea, and Taiwan AGENCY: United States International... steel butt-weld pipe fittings from Japan, Korea, and Taiwan would be likely to lead to continuation or...

  18. 77 FR 43806 - Seamless Carbon and Alloy Steel Standard, Line, and Pressure Pipe From the People's Republic of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-07-26

    ... duty order on seamless carbon and alloy steel standard, line, and pressure pipe from the People's... the antidumping duty order on seamless carbon and alloy steel standard, line, and pressure pipe from... Making Co., Ltd.; Wuxi Seamless Special Pipe Co., Ltd.; Wuxi Sifang Steel Tube Co., Ltd.; Wuxi Zhenda...

  19. 78 FR 31574 - Welded Stainless Steel Pressure Pipe From Malaysia, Thailand, and Vietnam; Institution of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-05-24

    ... INTERNATIONAL TRADE COMMISSION [Investigation Nos. 731-TA-1210-1212 (Preliminary)] Welded Stainless Steel Pressure Pipe From Malaysia, Thailand, and Vietnam; Institution of Antidumping Duty..., by reason of imports from Malaysia, Thailand, and Vietnam of welded stainless steel pressure pipe...

  20. 49 CFR 192.328 - Additional construction requirements for steel pipe using alternative maximum allowable operating...

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 3 2012-10-01 2012-10-01 false Additional construction requirements for steel pipe using alternative maximum allowable operating pressure. 192.328 Section 192.328 Transportation... Lines and Mains § 192.328 Additional construction requirements for steel pipe using alternative maximum...

  1. 49 CFR 192.328 - Additional construction requirements for steel pipe using alternative maximum allowable operating...

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 3 2014-10-01 2014-10-01 false Additional construction requirements for steel pipe using alternative maximum allowable operating pressure. 192.328 Section 192.328 Transportation... Lines and Mains § 192.328 Additional construction requirements for steel pipe using alternative maximum...

  2. 77 FR 39735 - Stainless Steel Butt-Weld Pipe Fittings From Italy, Malaysia, and the Philippines

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-07-05

    ... revocation of the antidumping duty orders on stainless steel butt-weld pipe fittings From Italy, Malaysia... INTERNATIONAL TRADE COMMISSION [Investigation Nos. 731-TA-865-867 (Second Review)] Stainless Steel Butt-Weld Pipe Fittings From Italy, Malaysia, and the Philippines Determination On the basis of the...

  3. 78 FR 72863 - Circular Welded Carbon-Quality Steel Pipe From the People's Republic of China: Continuation of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-12-04

    ...-Quality Steel Pipe From the People's Republic of China: Continuation of Antidumping Duty Order AGENCY... circular welded carbon-quality steel pipe (``circular welded pipe'') from the People's Republic of China...\\ See Initiation of Five-Year (``Sunset'') Review, 78 FR 33063 (June 3, 2013). \\2\\ See Circular Welded...

  4. 75 FR 64250 - Certain Welded Carbon Steel Pipe and Tube From Turkey: Notice of Final Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-10-19

    ... Pipe and Tube From Turkey: Notice of Final Antidumping Duty Administrative Review AGENCY: Import... administrative review of certain welded carbon steel pipe and tube from Turkey. This review covers four producers... Administrative Review of Certain Welded Carbon Steel Pipe and Tube from Turkey: Selection of Respondents for...

  5. Corrugated steel culvert pipe deterioration : final report, August 2009.

    DOT National Transportation Integrated Search

    2009-08-01

    This research provides the basis for developing a comprehensive plan for inspection, cleaning, condition assessment and : prediction of remaining service life of CSCP (Corrugated Steel Culvert Pipe). Inspection frequency guidelines were developed : t...

  6. 76 FR 27987 - Circular Welded Carbon Steel Pipes and Tubes From Thailand: Amended Final Results of Antidumping...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-05-13

    ... Pipes and Tubes From Thailand: Amended Final Results of Antidumping Duty Administrative Review Pursuant... tubes from Thailand, which covered Saha Thai Steel Pipe (Public) Co., Ltd. (Saha Thai) and the period March 1, 2006, through February 28, 2007. See Circular Welded Carbon Steel Pipes and Tubes from Thailand...

  7. 78 FR 286 - Circular Welded Carbon Steel Pipes and Tubes From Turkey; Amended Final Results of Antidumping...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-01-03

    ... Pipes and Tubes From Turkey; Amended Final Results of Antidumping Duty Administrative Review; 2010 to... administrative review of the antidumping duty order on circular welded carbon steel pipes and tubes from Turkey... Act). \\1\\ See Circular Welded Carbon Steel Pipes and Tubes from Turkey; Final Results of Antidumping...

  8. 76 FR 78886 - Certain Welded Carbon Steel Standard Pipe and Tube From Turkey: Intent To Rescind Countervailing...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-12-20

    ... Standard Pipe and Tube From Turkey: Intent To Rescind Countervailing Duty Administrative Review, in Part... certain welded carbon steel pipe and tube from Turkey. See Antidumping or Countervailing Duty Order... Certain Welded Carbon Steel Standard Pipe from Turkey,'' (October 27, 2011). A Type 3 entry is an entry of...

  9. Characterization of corrosion scale formed on stainless steel delivery pipe for reclaimed water treatment.

    PubMed

    Cui, Yong; Liu, Shuming; Smith, Kate; Yu, Kanghua; Hu, Hongying; Jiang, Wei; Li, Yuhong

    2016-01-01

    To reveal corrosion behavior of stainless steel delivery pipe used in reclaimed water treatment, this research focused on the morphological, mineralogical and chemical characteristics of stainless steel corrosion scale and corroded passive film. Corrosion scale and coupon samples were taken from a type 304 pipe delivering reclaimed water to a clear well in service for more than 12 years. Stainless steel corrosion scales and four representative pipe coupons were investigated using mineralogy and material science research methods. The results showed corrosion scale was predominantly composed of goethite, lepidocrocite, hematite, magnetite, ferrous oxide, siderite, chrome green and chromite, the same as that of corroded pipe coupons. Hence, corrosion scale can be identified as podiform chromite deposit. The loss of chromium in passive film is a critical phenomenon when stainless steel passive film is damaged by localized corrosion. This may provide key insights toward improving a better comprehension of the formation of stainless steel corrosion scale and the process of localized corrosion. The localized corrosion behavior of stainless steel is directly connected with reclaimed water quality parameters such as residual chlorine, DO, Cl(-) and SO4(2-). In particular, when a certain amount of residual chlorine in reclaimed water is present as an oxidant, ferric iron is the main chemical state of iron minerals. Copyright © 2015 Elsevier Ltd. All rights reserved.

  10. On the impact bending test technique for high-strength pipe steels

    NASA Astrophysics Data System (ADS)

    Arsenkin, A. M.; Odesskii, P. D.; Shabalov, I. P.; Likhachev, M. V.

    2015-10-01

    It is shown that the impact toughness (KCV-40 = 250 J/cm2) accepted for pipe steels of strength class K65 (σy ≥ 550 MPa) intended for large-diameter gas line pipes is ineffective to classify steels in fracture strength. The results obtained upon testing of specimens with a fatigue crack and additional sharp lateral grooves seem to be more effective. In energy consumption, a macrorelief with splits is found to be intermediate between ductile fracture and crystalline brittle fracture. A split formation mechanism is considered and a scheme is proposed for split formation.

  11. Use of Nitrocarburizing for Strengthening Threaded Joints of Drill Pipes from Medium-Carbon Alloy Steels

    NASA Astrophysics Data System (ADS)

    Priymak, E. Yu.; Stepanchukova, A. V.; Yakovleva, I. L.; Tereshchenko, N. A.

    2015-05-01

    Nitrocarburizing is tested at the Drill Equipment Plant for reinforcing threaded joints of drill pipes for units with retrievable core receiver (RCR). The effect of the nitrocarburizing on the mechanical properties of steels of different alloying systems is considered. Steels for the production of threaded joints of drill pipes are recommended.

  12. Structural Repair of Steel Piping by In-Situ Sleeving of Nanostructured Materials

    DOT National Transportation Integrated Search

    2009-06-03

    The focus of Task 1 is to demonstrate the repair of degraded pipeline steel using patches of high strength nanocrystalline metal. As mentioned in Bi-Monthly Research Progress Report #2, the cracking caused by corrosion damage in the steel pipe sectio...

  13. 75 FR 2487 - Circular Welded Carbon Steel Pipes and Tubes from Thailand: Court Decision Not in Harmony with...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-01-15

    ... Pipes and Tubes from Thailand: Court Decision Not in Harmony with Final Results of Administrative Review... welded carbon steel pipes and tubes from Thailand covering the period March 1, 2006 through February 28, 2007. Circular Welded Carbon Steel Pipes and Tubes from Thailand: Final Results of Antidumping Duty...

  14. 76 FR 72173 - Circular Welded Carbon-Quality Steel Pipe From India, the Sultanate of Oman, the United Arab...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-11-22

    ...-552-810] Circular Welded Carbon-Quality Steel Pipe From India, the Sultanate of Oman, the United Arab... Steel Pipe from India, Oman, the United Arab Emirates, and Vietnam, dated October 26, 2011 (hereinafter... pipe from India, the Sultanate of Oman (``Oman''), the United Arab Emirates (``the UAE''), and the...

  15. 77 FR 6542 - Certain Welded Carbon Steel Standard Pipe and Tube From Turkey: Notice of Final Rescission of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-02-08

    ... Standard Pipe and Tube From Turkey: Notice of Final Rescission of Countervailing Duty Administrative Review...) order on certain welded carbon steel pipe and tube from Turkey for the period of review (POR) of January... of Certain Welded Carbon Steel Standard Pipe from Turkey,'' (October 27, 2011). We reviewed the...

  16. 76 FR 21331 - Certain Carbon Steel Butt-Weld Pipe Fittings From Brazil, Japan, Taiwan, Thailand, and the People...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-04-15

    ...-807, A-570-814] Certain Carbon Steel Butt-Weld Pipe Fittings From Brazil, Japan, Taiwan, Thailand, and... butt-weld pipe fittings from Brazil, Japan, Taiwan, Thailand, and the People's Republic of China (PRC... duty orders on carbon steel butt-weld pipe fittings from Brazil, Japan, Taiwan, Thailand, and the PRC...

  17. Study on the residual stress relaxation in girth-welded steel pipes under bending load using diffraction methods

    DOE PAGES

    Hempel, Nico; Bunn, Jeffrey R.; Nitschke-Pagel, Thomas; ...

    2017-02-02

    This research is dedicated to the experimental investigation of the residual stress relaxation in girth-welded pipes due to quasi-static bending loads. Ferritic-pearlitic steel pipes are welded with two passes, resulting in a characteristic residual stress state with high tensile residual stresses at the weld root. Also, four-point bending is applied to generate axial load stress causing changes in the residual stress state. These are determined both on the outer and inner surfaces of the pipes, as well as in the pipe wall, using X-ray and neutron diffraction. Focusing on the effect of tensile load stress, it is revealed that notmore » only the tensile residual stresses are reduced due to exceeding the yield stress, but also the compressive residual stresses for equilibrium reasons. Furthermore, residual stress relaxation occurs both parallel and perpendicular to the applied load stress.« less

  18. Study on the residual stress relaxation in girth-welded steel pipes under bending load using diffraction methods

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Hempel, Nico; Bunn, Jeffrey R.; Nitschke-Pagel, Thomas

    This research is dedicated to the experimental investigation of the residual stress relaxation in girth-welded pipes due to quasi-static bending loads. Ferritic-pearlitic steel pipes are welded with two passes, resulting in a characteristic residual stress state with high tensile residual stresses at the weld root. Also, four-point bending is applied to generate axial load stress causing changes in the residual stress state. These are determined both on the outer and inner surfaces of the pipes, as well as in the pipe wall, using X-ray and neutron diffraction. Focusing on the effect of tensile load stress, it is revealed that notmore » only the tensile residual stresses are reduced due to exceeding the yield stress, but also the compressive residual stresses for equilibrium reasons. Furthermore, residual stress relaxation occurs both parallel and perpendicular to the applied load stress.« less

  19. 77 FR 21968 - Seamless Carbon and Alloy Steel Standard, Line, and Pressure Pipe From the People's Republic of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-04-12

    ... countervailing duty order on seamless carbon and alloy steel standard, line, and pressure pipe from the People's... administrative review of the countervailing duty order on seamless carbon and alloy steel standard, line, and... Making Co., Ltd., Wuxi Seamless Special Pipe Co., Ltd., Wuxi Sifang Steel Tube Co., Ltd., Wuxi Zhenda...

  20. 77 FR 32552 - Circular Welded Carbon-Quality Steel Pipe From the Socialist Republic of Vietnam: Preliminary...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-06-01

    ... obtain separate-rate status in non-market economy (NME) investigations such as this investigation.\\3\\ \\2... Welded Non-Alloy Steel Pipe from Brazil, Mexico, the Republic of Korea, and Taiwan; and Certain Circular... Steel Pipe from the People's Republic of China, 73 FR 31970 (June 5, 2008), and accompanying Issues and...

  1. 46 CFR 56.80-15 - Heat treatment of bends and formed components.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 2 2010-10-01 2010-10-01 false Heat treatment of bends and formed components. 56.80-15... PIPING SYSTEMS AND APPURTENANCES Bending and Forming § 56.80-15 Heat treatment of bends and formed... forming requires no subsequent heat treatment. (b) Ferritic alloy steel piping which has been heated for...

  2. 46 CFR 56.80-15 - Heat treatment of bends and formed components.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 2 2011-10-01 2011-10-01 false Heat treatment of bends and formed components. 56.80-15... PIPING SYSTEMS AND APPURTENANCES Bending and Forming § 56.80-15 Heat treatment of bends and formed... forming requires no subsequent heat treatment. (b) Ferritic alloy steel piping which has been heated for...

  3. 46 CFR 56.80-15 - Heat treatment of bends and formed components.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 2 2014-10-01 2014-10-01 false Heat treatment of bends and formed components. 56.80-15... PIPING SYSTEMS AND APPURTENANCES Bending and Forming § 56.80-15 Heat treatment of bends and formed... forming requires no subsequent heat treatment. (b) Ferritic alloy steel piping which has been heated for...

  4. 46 CFR 56.80-15 - Heat treatment of bends and formed components.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 2 2012-10-01 2012-10-01 false Heat treatment of bends and formed components. 56.80-15... PIPING SYSTEMS AND APPURTENANCES Bending and Forming § 56.80-15 Heat treatment of bends and formed... forming requires no subsequent heat treatment. (b) Ferritic alloy steel piping which has been heated for...

  5. 46 CFR 56.80-15 - Heat treatment of bends and formed components.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 2 2013-10-01 2013-10-01 false Heat treatment of bends and formed components. 56.80-15... PIPING SYSTEMS AND APPURTENANCES Bending and Forming § 56.80-15 Heat treatment of bends and formed... forming requires no subsequent heat treatment. (b) Ferritic alloy steel piping which has been heated for...

  6. 75 FR 9163 - Certain Seamless Carbon and Alloy Steel Standard, Line, and Pressure Pipe From the People's...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-03-01

    ... Alloy Steel Standard, Line, and Pressure Pipe From the People's Republic of China: Preliminary... the People's Republic of China. For information on the estimated subsidy rates, see the ``Suspension... Carbon and Alloy Steel Standard, Line, and Pressure Pipe from the People's Republic of China: Initiation...

  7. 75 FR 26273 - Certain Seamless Carbon and Alloy Steel Standard, Line, and Pressure Pipe From China

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-05-11

    ... certain seamless carbon and alloy steel standard, line, and pressure pipe (``seamless SLP pipe... China of seamless SLP pipe, and that such products are being sold in the United States at less than fair...

  8. 76 FR 68208 - Circular Welded Carbon-Quality Steel Pipe From India, Oman, United Arab Emirates, and Vietnam...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-11-03

    ... (Preliminary)] Circular Welded Carbon-Quality Steel Pipe From India, Oman, United Arab Emirates, and Vietnam... carbon-quality steel pipe from India, Oman, United Arab Emirates, and Vietnam, provided for in... Governments of India, Oman, United Arab Emirates, and Vietnam. Unless the Department of Commerce extends the...

  9. 77 FR 48965 - Certain Carbon Steel Butt-Weld Pipe Fittings From the People's Republic of China: Notice of Court...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-08-15

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-570-814] Certain Carbon Steel Butt... scope of the Order \\1\\ as excluding carbon steel butt-weld pipe fittings from the People's Republic of... Carbon Steel Butt-Weld Pipe Fittings From the People's Republic of China, 57 FR 29702 (July 6, 1992...

  10. 76 FR 56395 - Certain Welded Carbon Steel Pipe and Tube From Turkey: Notice of Extension of Time Limit for...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-09-13

    ... Pipe and Tube From Turkey: Notice of Extension of Time Limit for Final Results of Antidumping Duty... antidumping order on certain welded carbon steel pipe and tube from Turkey for the period May 1, 2009, through April 30, 2010. See Certain Welded Carbon Steel Pipe and Tube From Turkey; Notice of Preliminary Results...

  11. Heat Transfer Modeling of an Annular On-Line Spray Water Cooling Process for Electric-Resistance-Welded Steel Pipe

    PubMed Central

    Chen, Zejun; Han, Huiquan; Ren, Wei; Huang, Guangjie

    2015-01-01

    On-line spray water cooling (OSWC) of electric-resistance-welded (ERW) steel pipes can replace the conventional off-line heat treatment process and become an important and critical procedure. The OSWC process improves production efficiency, decreases costs, and enhances the mechanical properties of ERW steel pipe, especially the impact properties of the weld joint. In this paper, an annular OSWC process is investigated based on an experimental simulation platform that can obtain precise real-time measurements of the temperature of the pipe, the water pressure and flux, etc. The effects of the modes of annular spray water cooling and related cooling parameters on the mechanical properties of the pipe are investigated. The temperature evolutions of the inner and outer walls of the pipe are measured during the spray water cooling process, and the uniformity of mechanical properties along the circumferential and longitudinal directions is investigated. A heat transfer coefficient model of spray water cooling is developed based on measured temperature data in conjunction with simulation using the finite element method. Industrial tests prove the validity of the heat transfer model of a steel pipe undergoing spray water cooling. The research results can provide a basis for the industrial application of the OSWC process in the production of ERW steel pipes. PMID:26201073

  12. Heat Transfer Modeling of an Annular On-Line Spray Water Cooling Process for Electric-Resistance-Welded Steel Pipe.

    PubMed

    Chen, Zejun; Han, Huiquan; Ren, Wei; Huang, Guangjie

    2015-01-01

    On-line spray water cooling (OSWC) of electric-resistance-welded (ERW) steel pipes can replace the conventional off-line heat treatment process and become an important and critical procedure. The OSWC process improves production efficiency, decreases costs, and enhances the mechanical properties of ERW steel pipe, especially the impact properties of the weld joint. In this paper, an annular OSWC process is investigated based on an experimental simulation platform that can obtain precise real-time measurements of the temperature of the pipe, the water pressure and flux, etc. The effects of the modes of annular spray water cooling and related cooling parameters on the mechanical properties of the pipe are investigated. The temperature evolutions of the inner and outer walls of the pipe are measured during the spray water cooling process, and the uniformity of mechanical properties along the circumferential and longitudinal directions is investigated. A heat transfer coefficient model of spray water cooling is developed based on measured temperature data in conjunction with simulation using the finite element method. Industrial tests prove the validity of the heat transfer model of a steel pipe undergoing spray water cooling. The research results can provide a basis for the industrial application of the OSWC process in the production of ERW steel pipes.

  13. Control of Microstructures and the Practical Properties of API X80 Grade Heavy-Wall High-Frequency Electric Resistance-Welded Pipe with Excellent Low-Temperature Toughness

    NASA Astrophysics Data System (ADS)

    Goto, Sota; Nakata, Hiroshi; Toyoda, Shunsuke; Okabe, Takatoshi; Inoue, Tomohiro

    2017-10-01

    This paper describes development of heavy-walled API X80 grade high-frequency electric resistance-welded (HFW) line pipes and conductor-casing pipes with wall thicknesses up to 20.6 mm. A fine bainitic-ferrite microstructure, which is preferable for low-temperature toughness, was obtained by optimizing the carbon content and applying the thermomechanical controlled hot-rolling process. As a result, the Charpy ductile-brittle transition temperature (DBTT) was well below 227 K (-46 °C) in the base metal of the HFW line pipe. When the controlled hot-rolling ratio (CR) was increased from 23 to 48 pct, the area average grain size decreased from 15 to 8 μm. The dependence of CTOD properties on CR was caused by the largest grain which is represented by the area average grain size. No texture development due to the increase of CR from 23 to 48 pct was observed. In addition, because controlled in-line heat treatment of the longitudinal weld seam also produced the fine bainitic-ferrite microstructure at the weld seam, DBTT was lower than 227 K (-46 °C) at the weld portion. The developed pipes showed good girth weldability without preheat treatment, and fracture in the tensile test initiated from the base metal in all cases.

  14. Arrangement for connecting a fiber-reinforced plastic pipe to a stainless steel flange

    DOEpatents

    Allais, Arnaud [D-30625 Hannover, DE; Hoffmann, Ernst [D-30855 Langenhagen, DE

    2008-02-05

    Arrangement for connecting a fiber-reinforced plastic pipe (18) to a stainless steel flange (12, 16), in which the end of the fiber-reinforced plastic pipe (18) is accommodated in a ring-shaped groove (12a, 16a) in the flange (12, 16), the groove conforming to the dimensions of the fiber-reinforced plastic pipe (18), where the gap remaining between the end of the fiber-reinforced plastic pipe (18) and the ring-shaped groove (12a, 16a) is filled with a sealant (19).

  15. 78 FR 33809 - Seamless Carbon and Alloy Steel Standard, Line, and Pressure Pipe From the People's Republic of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-06-05

    ... review of the antidumping duty order on seamless carbon and alloy steel standard, line, and pressure pipe... seamless carbon and alloy steel standard, line, and pressure pipe from the People's Republic of China... DEPARTMENT OF COMMERCE International Trade Administration [A-570-956] Seamless Carbon and Alloy...

  16. 77 FR 2511 - Certain Welded Carbon Steel Pipe and Tube From Turkey: Extension of Time Limit for Preliminary...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-01-18

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-489-501] Certain Welded Carbon Steel Pipe and Tube From Turkey: Extension of Time Limit for Preliminary Results of Antidumping Duty... certain welded carbon steel pipe and tube from Turkey covering the period May 1, 2010, through April 30...

  17. 76 FR 3083 - Certain Welded Carbon Steel Pipe and Tube From Turkey: Extension of Time Limit for Preliminary...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-01-19

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-489-501] Certain Welded Carbon Steel Pipe and Tube From Turkey: Extension of Time Limit for Preliminary Results of Antidumping Duty... welded carbon steel pipe and tube from Turkey covering the period May 1, 2009, through April 30, 2010...

  18. 75 FR 3896 - Certain Welded Carbon Steel Pipe and Tube from Turkey: Extension of Time Limit for Preliminary...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-01-25

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-489-501] Certain Welded Carbon Steel Pipe and Tube from Turkey: Extension of Time Limit for Preliminary Results of Antidumping Duty... antidumping duty order on certain welded carbon steel pipe and tube from Turkey covering the period May 1...

  19. 77 FR 73674 - Circular Welded Carbon-Quality Steel Pipe From India, Oman, The United Arab Emirates, and Vietnam

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-12-11

    ...)] Circular Welded Carbon-Quality Steel Pipe From India, Oman, The United Arab Emirates, and Vietnam... welded carbon-quality steel pipe from India, Oman, the United Arab Emirates, and Vietnam, provided for in... from India, Oman, the United Arab Emirates, and Vietnam were subsidized and/or dumped within the...

  20. 76 FR 78313 - Circular Welded Carbon-Quality Steel Pipe From India, Oman, the United Arab Emirates, and Vietnam

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-12-16

    ... (Preliminary)] Circular Welded Carbon-Quality Steel Pipe From India, Oman, the United Arab Emirates, and... India, Oman, the United Arab Emirates, and Vietnam of circular welded carbon- quality steel pipe... the Governments of India, Oman, the United Arab Emirates, and Vietnam.\\2\\ \\1\\ The record is defined in...

  1. 75 FR 44763 - Certain Circular Welded Non-Alloy Steel Pipe From Mexico; Extension of Time Limit for Preliminary...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-07-29

    ...-Alloy Steel Pipe From Mexico; Extension of Time Limit for Preliminary Results of Antidumping Duty... review of the antidumping duty order on certain circular welded non- alloy steel pipe from Mexico. We... preliminary results of this review within the original time frame because we require additional time with...

  2. 77 FR 37711 - Circular Welded Carbon-Quality Steel Pipe From India, Oman, the United Arab Emirates, and Vietnam...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-06-22

    ...)] Circular Welded Carbon-Quality Steel Pipe From India, Oman, the United Arab Emirates, and Vietnam...-fair-value imports from India, Oman, the United Arab Emirates, and Vietnam of circular welded carbon... respect to circular welded carbon-quality steel pipe from Oman and the United Arab Emirates being sold in...

  3. 77 FR 15718 - Circular Welded Carbon-Quality Steel Pipe From India, the Sultanate of Oman, the United Arab...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-03-16

    ...-811] Circular Welded Carbon-Quality Steel Pipe From India, the Sultanate of Oman, the United Arab... Oman (Oman), the United Arab Emirates (UAE), and the Socialist Republic of Vietnam (Vietnam). See Circular Welded Carbon-Quality Steel Pipe From India, the Sultanate of Oman, the United Arab Emirates, and...

  4. 46 CFR 98.25-80 - Cargo hose.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... Cargo hose. (a) Cargo hose fabricated of seamless steel pipe with swivel joints, wire braided armored rubber or other hose material acceptable to the Commandant, shall be fitted to the liquid or vapor lines... 46 Shipping 4 2013-10-01 2013-10-01 false Cargo hose. 98.25-80 Section 98.25-80 Shipping COAST...

  5. 46 CFR 98.25-80 - Cargo hose.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... Cargo hose. (a) Cargo hose fabricated of seamless steel pipe with swivel joints, wire braided armored rubber or other hose material acceptable to the Commandant, shall be fitted to the liquid or vapor lines... 46 Shipping 4 2010-10-01 2010-10-01 false Cargo hose. 98.25-80 Section 98.25-80 Shipping COAST...

  6. 46 CFR 98.25-80 - Cargo hose.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... Cargo hose. (a) Cargo hose fabricated of seamless steel pipe with swivel joints, wire braided armored rubber or other hose material acceptable to the Commandant, shall be fitted to the liquid or vapor lines... 46 Shipping 4 2012-10-01 2012-10-01 false Cargo hose. 98.25-80 Section 98.25-80 Shipping COAST...

  7. 46 CFR 98.25-80 - Cargo hose.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... Cargo hose. (a) Cargo hose fabricated of seamless steel pipe with swivel joints, wire braided armored rubber or other hose material acceptable to the Commandant, shall be fitted to the liquid or vapor lines... 46 Shipping 4 2011-10-01 2011-10-01 false Cargo hose. 98.25-80 Section 98.25-80 Shipping COAST...

  8. 46 CFR 98.25-80 - Cargo hose.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... Cargo hose. (a) Cargo hose fabricated of seamless steel pipe with swivel joints, wire braided armored rubber or other hose material acceptable to the Commandant, shall be fitted to the liquid or vapor lines... 46 Shipping 4 2014-10-01 2014-10-01 false Cargo hose. 98.25-80 Section 98.25-80 Shipping COAST...

  9. APPLICATION OF STEEL PIPE PILE LOADING TESTS TO DESIGN VERIFICATION OF FOUNDATION OF THE TOKYO GATE BRIDGE

    NASA Astrophysics Data System (ADS)

    Saitou, Yutaka; Kikuchi, Yoshiaki; Kusakabe, Osamu; Kiyomiya, Osamu; Yoneyama, Haruo; Kawakami, Taiji

    Steel sheet pipe pile foundations with large diameter steel pipe sheet pile were used for the foundation of the main pier of the Tokyo Gateway bridge. However, as for the large diameter steel pipe pile, the bearing mechanism including a pile tip plugging effect is still unclear due to lack of the practical examinations even though loading tests are performed on Trans-Tokyo Bay Highway. In the light of the foregoing problems, static pile loading tests both vertical and horizontal directions, a dynamic loading test, and cone penetration tests we re conducted for determining proper design parameters of the ground for the foundations. Design parameters were determined rationally based on the tests results. Rational design verification was obtained from this research.

  10. Effect of Structure Factor on High-Temperature Ductility of Pipe Steels

    NASA Astrophysics Data System (ADS)

    Kolbasnikov, N. G.; Matveev, M. A.; Mishnev, P. A.

    2016-05-01

    Effects of various factors such as the grain size, the morphology of nonmetallic inclusions, and joint microalloying with boron and titanium on the high-temperature ductility of pipe steels are studied. Physical modeling of the conditions of cooling of the skin of a continuous-cast preform in the zone of secondary cooling in a Gleeble facility is performed. Technical recommendations are given for raising the hot ductility of steels under industrial conditions.

  11. 76 FR 7151 - Certain Carbon Steel Butt-Weld Pipe Fittings From Brazil, Japan, Taiwan, Thailand, and the People...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-02-09

    ...-807, A-570-814] Certain Carbon Steel Butt-Weld Pipe Fittings From Brazil, Japan, Taiwan, Thailand, and..., Thailand, and the People's Republic of China (PRC), pursuant to section 751(c) of the Tariff Act of 1930... antidumping duty orders \\1\\ on carbon steel butt-weld pipe fittings from Brazil, Japan, Taiwan, Thailand, and...

  12. 76 FR 64900 - Welded Carbon Steel Pipe and Tube From Turkey: Final Results of Expedited Sunset Review of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-10-19

    ... Tube From Turkey: Final Results of Expedited Sunset Review of Countervailing Duty Order AGENCY: Import... welded carbon steel pipe and tube from Turkey pursuant to section 751(c) of the Tariff Act of 1930, as... INFORMATION: Background The CVD order on welded carbon steel pipe and tube from Turkey was published in the...

  13. 78 FR 79665 - Welded Carbon Steel Standard Pipe and Tube Products From Turkey: Final Results of Antidumping...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-12-31

    ... Pipe and Tube Products From Turkey: Final Results of Antidumping Duty Administrative Review; 2011-2012... pipe and tube products (welded pipe and tube) from Turkey.\\1\\ The period of review (POR) is May 1, 2011... during the POR.\\2\\ \\1\\ See Welded Carbon Steel Standard Pipe and Tube Products from Turkey: Preliminary...

  14. 78 FR 34340 - Welded Carbon Steel Standard Pipe and Tube Products From Turkey: Preliminary Results of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-06-07

    ... Pipe and Tube Products From Turkey: Preliminary Results of Antidumping Duty Administrative Review; 2011... tube products (welded pipe and tube) from Turkey.\\2\\ The period of review is May 1, 2011, to April 30... order. See Antidumping Duty Order; Welded Carbon Steel Standard Pipe and Tube Products from Turkey, 51...

  15. 78 FR 49255 - Certain Circular Welded Carbon Steel Pipes and Tubes From Taiwan: Partial Rescission of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-08-13

    ... Co., Ltd., Tension Steel Industries Co., Ltd., and Yieh Phui Enterprise Co., Ltd. Petitioner... Steel Industries Co., Ltd.; and (5) Yieh Phui Enterprise Co., Ltd. This review will continue with... Carbon Steel Pipes and Tubes From Taiwan: Partial Rescission of Antidumping Duty Administrative Review...

  16. 76 FR 77480 - Certain Circular Welded Carbon Steel Pipes and Tubes From Taiwan: Notice of Rescission of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-12-13

    ... Kao Hsiung Chang Iron & Steel Corp.); and (6) Tension Steel Industries Co. Ltd. The Department... Carbon Steel Pipes and Tubes From Taiwan: Notice of Rescission of Antidumping Duty Administrative Review... response to a request from United States Steel Corporation, an interested party, the Department of Commerce...

  17. 75 FR 64696 - Circular Welded Carbon Steel Pipes and Tubes From Thailand: Final Results of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-10-20

    ... Pipes and Tubes From Thailand: Final Results of Antidumping Duty Administrative Review AGENCY: Import... Thailand. The review was requested by Allied Tube and Conduit Corporation (Allied Tube), by Wheatland Tube... antidumping duty order on pipes and tubes from Thailand. See Circular Welded Carbon Steel Pipes and Tubes from...

  18. 75 FR 62366 - Circular Welded Carbon Steel Pipes and Tubes From Taiwan: Final Results of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-10-08

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-583-008] Circular Welded Carbon Steel... antidumping duty order on circular welded carbon steel pipes and tubes from Taiwan. See Preliminary Results of Antidumping Duty Administrative Review: Circular Welded Carbon Steel [[Page 62367

  19. 78 FR 70069 - Circular Welded Carbon-Quality Steel Pipe From China

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-11-22

    ... INTERNATIONAL TRADE COMMISSION [Investigation Nos. 701-TA-447 and 731-TA-1116 (Review)] Circular Welded Carbon-Quality Steel Pipe From China Determination On the basis of the record \\1\\ developed in the subject five-year reviews, the United States International Trade Commission (Commission) determines...

  20. Microbiological corrosion of ASTM SA105 carbon steel pipe for industrial fire water usage

    NASA Astrophysics Data System (ADS)

    Chidambaram, S.; Ashok, K.; Karthik, V.; Venkatakrishnan, P. G.

    2018-02-01

    The large number of metallic systems developed for last few decades against both general uniform corrosion and localized corrosion. Among all microbiological induced corrosion (MIC) is attractive, multidisciplinary and complex in nature. Many chemical processing industries utilizes fresh water for fire service to nullify major/minor fire. One such fire water service line pipe attacked by micro-organisms leads to leakage which is industrially important from safety point of view. Also large numbers of leakage reported in similar fire water service of nearby food processing plant, paper & pulp plant, steel plant, electricity board etc…In present investigation one such industrial fire water service line failure analysis of carbon steel line pipe was analyzed to determine the cause of failure. The water sample subjected to various chemical and bacterial analyses. Turbidity, pH, calcium hardness, free chlorine, oxidation reduction potential, fungi, yeasts, sulphide reducing bacteria (SRB) and total bacteria (TB) were measured on water sample analysis. The corrosion rate was measured on steel samples and corrosion coupon measurements were installed in fire water for validating non flow assisted localized corrosion. The sulphide reducing bacteria (SRB) presents in fire water causes a localized micro biological corrosion attack of line pipe.

  1. 75 FR 44766 - Certain Welded Carbon Steel Standard Pipe from Turkey: Final Results of Countervailing Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-07-29

    ... Standard Pipe from Turkey: Final Results of Countervailing Duty Administrative Review AGENCY: Import... Department of Commerce (the Department) published in the Federal Register its preliminary results of... Carbon Steel Standard Pipe From Turkey: Preliminary Results of Countervailing Duty Administrative Review...

  2. 75 FR 13729 - Circular Welded Non-Alloy Steel Pipe from the Republic of Korea: Extension of Time Limit for the...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-03-23

    ... Steel Pipe from the Republic of Korea: Extension of Time Limit for the Final Results and Rescission in Part of the Antidumping Duty Administrative Review AGENCY: Import Administration, International Trade... Welded Non-Alloy Steel Pipe from the Republic of Korea: Preliminary Results and Rescission in Part of the...

  3. 75 FR 4529 - Circular Welded Carbon Steel Pipes and Tubes From Thailand: Final Results of Antidumping Duty New...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-01-28

    ... Pipes and Tubes From Thailand: Final Results of Antidumping Duty New Shipper Review AGENCY: Import... Thailand. See Circular Welded Carbon Steel Pipes and Tubes from Thailand: Preliminary Results of... review under the antidumping duty order covering pipes and tubes from Thailand. See Preliminary Results...

  4. 75 FR 36635 - Circular Welded Carbon Steel Pipes and Tubes From Thailand: Rescission of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-06-28

    ... Pipes and Tubes From Thailand: Rescission of Antidumping Duty Administrative Review AGENCY: Import... tubes from Thailand. See Antidumping or Countervailing Duty Order, Finding, or Suspended Investigation... the antidumping duty order on circular welded carbon steel pipes and tubes from Thailand for the...

  5. Effects of Microstructure on Tensile, Charpy Impact, and Crack Tip Opening Displacement Properties of Two API X80 Pipeline Steels

    NASA Astrophysics Data System (ADS)

    Shin, Sang Yong

    2013-06-01

    The effects of microstructure on tensile, Charpy impact, and crack tip opening displacement (CTOD) properties of two API X80 pipeline steels were investigated in this study. Two API X80 pipeline steels consisting of acicular ferrite and granular bainite, and a small amount of hard phases such as martensite and secondary phases have elongated grains along the rolling direction, so that they show different mechanical properties as the specimens' directions change. The 90 deg specimens have high tensile strength due to the low stress concentration on the fine hard phases and the high loads for the deformation of the elongated grains. In contrast, the 30 deg specimens have less elongated grains and larger hard phases such as martensite, with the size of about 3 μm, than the 90 deg specimens. Hence, the 30 deg specimens have low tensile strength because of the high stress concentration on the large hard phases and the low loads to deform grains. In the 90 deg specimen, brittle crack propagation surfaces are even since cracks propagate in a straight line along the elongated grain structure. In the 30 deg specimen, however, brittle crack propagation surfaces are uneven, and secondary cracks are observed, because of the zigzag brittle crack propagation path. In the CTOD properties, the 90 deg specimens have maximum forces of higher magnitude than the 30 deg specimens, because of the elongated grain structure. However, CTODs of the 90 deg specimens are lower than those of the 30 deg specimens because of the low plastic deformation areas by the elongated grains in the 90 deg specimens.

  6. Modification of the Stress-Strain Curve for High-Strength Line Pipe Steel

    NASA Astrophysics Data System (ADS)

    Jonsson, Katherine

    2013-01-01

    This thesis presents work performed to improve the work hardening behaviour of an X80 microalloyed steel through various Interrupted Thermal Treatments (ITT). The aim of this work was to determine the relationships between thermal history, microstructure and mechanical properties through both qualitative and quantitative measures. Prior to the ITT experiments, a continuous cooling transformation (CCT) diagram was constructed under no-strain conditions to identify the transformation temperatures and products that are achievable in X80 steel. The thermal treatments were applied using a Gleeble thermal-mechanical simulator to generate a variety of microstructures in various fractions and morphologies. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to investigate and quantify the microstructures in terms of phase fraction and grain size. The ITT experiments successfully generated microstructures comprised of ferrite, bainitic ferrite, martensite and martensite-austenite (M-A) without the addition of strain. The effect of cooling rates, interrupt temperature, re-heat temperature and hold times were investigated and the mechanical performance was correlated with the quantified microstructures. Although the ITT experiments did not improve the strength relative to a continuously cooled sample, the work hardening coefficient was increased as a result of the interrupted thermal treatments.

  7. 78 FR 61335 - Circular Welded Carbon-Quality Steel Pipe From the People's Republic of China: Final Results of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-10-03

    ... identical in content. Final Results of Sunset Review: The Department determines that revocation of the... Pipes 45.35 Co., Ltd. Shanghai Metals & Minerals Huludao Steel Pipe 45.35 Import & Export Corp. Industrial Co. Shanghai Metals & Minerals Benxi Northern Pipes 45.35 Import & Export Corp. Co., Ltd. Huludao...

  8. Characterization of bond line discontinuities in a high-Mn TWIP steel pipe welded by HF-ERW

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Park, Gitae; Kim, Bongyoon; Kang, Yongjoon

    In this work, the microstructure and defects in a high-frequency electrical resistance welded (HF-ERW) pipe of high-Mn twinning-induced plasticity (TWIP) steel were characterized. The microstructure of the base metal and the bond line were examined using both optical microscopy and scanning electron microscopy. The features of the bond line were similar to those of conventional steel. Simultaneously, the circumferential ductility was evaluated via a flaring test. It was concluded that the deterioration of the circumferential ductility in a high-Mn TWIP steel pipe was caused by irregular shaped oxide defects and a penetrator that had been formed during welding. Specifically, themore » penetrator, which is composed of MnO and Mn{sub 2}SiO{sub 4}, was found to be the most influential on the circumferential ductility of the welded pipe. The penetrator was analyzed using both an electron probe micro analyzer and transmission electron microscopy, and the formation sequence of the penetrator was evaluated. - Highlights: •This study focused on applying the HF-ERW process to the seam welding of expandable pipe using TWIP steels. •For improvement of the circumferential ductility, deterioration factors were characterized. •Penetrator which would mainly deteriorate the circumferential ductility consisted of round MnO and Mn{sub 2}SiO{sub 4}. •Metallurgical evidence of existing theory regarding the mechanism of defect formation during the HF-ERW was characterized.« less

  9. 77 FR 14002 - Stainless Steel Butt-Weld Pipe Fittings From Italy, Malaysia, and the Philippines: Final Results...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-03-08

    ... steel fittings of seamless and welded construction covered by the latest revision of ANSI B16.9, ANSI...] Stainless Steel Butt-Weld Pipe Fittings From Italy, Malaysia, and the Philippines: Final Results of the... Commerce (the Department) initiated sunset reviews of the antidumping duty orders on stainless steel butt...

  10. 76 FR 19788 - Carbon Steel Butt-Weld Pipe Fittings From Brazil, China, Japan, Taiwan, and Thailand

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-04-08

    ...)] Carbon Steel Butt-Weld Pipe Fittings From Brazil, China, Japan, Taiwan, and Thailand Determinations On... fittings from Brazil, China, Japan, Taiwan, and Thailand would be likely to lead to continuation or... Pipe Fittings from Brazil, China, Japan, Taiwan, and Thailand: Investigation Nos. 731-TA-308-310 and...

  11. 49 CFR Appendix B to Part 192 - Qualification of Pipe

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ...—Steel pipe, “Standard Specification for Seamless Carbon Steel Pipe for High Temperature Service... pipe, “Standard Specification for Metal-Arc-Welded Steel Pipe for Use with High-Pressure Transmission...). ASTM A672—Steel pipe, “Standard Specification for Electric-Fusion-Welded Steel Pipe for High-Pressure...

  12. 49 CFR Appendix B to Part 192 - Qualification of Pipe

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ...—Steel pipe, “Standard Specification for Seamless Carbon Steel Pipe for High Temperature Service... pipe, “Standard Specification for Metal-Arc-Welded Steel Pipe for Use with High-Pressure Transmission...). ASTM A672—Steel pipe, “Standard Specification for Electric-Fusion-Welded Steel Pipe for High-Pressure...

  13. 49 CFR Appendix B to Part 192 - Qualification of Pipe

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ...—Steel pipe, “Standard Specification for Seamless Carbon Steel Pipe for High Temperature Service... pipe, “Standard Specification for Metal-Arc-Welded Steel Pipe for Use with High-Pressure Transmission...). ASTM A672—Steel pipe, “Standard Specification for Electric-Fusion-Welded Steel Pipe for High-Pressure...

  14. 49 CFR 192.112 - Additional design requirements for steel pipe using alternative maximum allowable operating...

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ..., fully killed, continuously cast steel with calcium treatment. (2) The carbon equivalents of the steel... under this section. (b) Fracture control (1) The toughness properties for pipe must address the... specification level 2 or ASME B31.8 (incorporated by reference, see § 192.7). (2) Fracture control must: (i...

  15. 49 CFR 192.112 - Additional design requirements for steel pipe using alternative maximum allowable operating...

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ..., fully killed, continuously cast steel with calcium treatment. (2) The carbon equivalents of the steel... under this section. (b) Fracture control (1) The toughness properties for pipe must address the... specification level 2 or ASME B31.8 (incorporated by reference, see § 192.7). (2) Fracture control must: (i...

  16. 49 CFR 192.112 - Additional design requirements for steel pipe using alternative maximum allowable operating...

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ..., fully killed, continuously cast steel with calcium treatment. (2) The carbon equivalents of the steel... under this section. (b) Fracture control (1) The toughness properties for pipe must address the... specification level 2 or ASME B31.8 (incorporated by reference, see § 192.7). (2) Fracture control must: (i...

  17. 49 CFR 192.112 - Additional design requirements for steel pipe using alternative maximum allowable operating...

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ..., fully killed, continuously cast steel with calcium treatment. (2) The carbon equivalents of the steel... under this section. (b) Fracture control (1) The toughness properties for pipe must address the... specification level 2 or ASME B31.8 (incorporated by reference, see § 192.7). (2) Fracture control must: (i...

  18. 49 CFR 192.112 - Additional design requirements for steel pipe using alternative maximum allowable operating...

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ..., fully killed, continuously cast steel with calcium treatment. (2) The carbon equivalents of the steel... under this section. (b) Fracture control (1) The toughness properties for pipe must address the... specification level 2 or ASME B31.8 (incorporated by reference, see § 192.7). (2) Fracture control must: (i...

  19. Fibre Laser Welding of HY-80 Steel: Procedure Development and Testing

    DTIC Science & Technology

    2010-09-01

    2 Welding The material used in this study was quenched and tempered martensitic HY80 steel which conforms to MIL-S-1621 [2]. The testing...Journal, 1977. [4] AWS, D1.6 in Structural Welding Code Stainless Steel . 2007, American Welding Society: Miami Florida. [5] DefStan, 02-770 Part 2...Canada Fibre Laser Welding of HY-80 Steel Proceedure Development and Testing Christopher Bayley DLP Neil Aucoin DLP Xinjin Cao NRC IAR AMTC Technical

  20. 24 CFR 3280.706 - Oil piping systems.

    Code of Federal Regulations, 2013 CFR

    2013-04-01

    ... described in § 3280.706(b) (1) through (4). (1) Steel or wrought-iron pipe shall comply with ANSI B 36.10-1979, Welded and Seamless Wrought Steel Pipe. Threaded copper or brass pipe in iron pipe sizes may be used. (2) Fittings for oil piping shall be wrought-iron, malleable iron, steel, or brass (containing...

  1. 24 CFR 3280.706 - Oil piping systems.

    Code of Federal Regulations, 2012 CFR

    2012-04-01

    ... described in § 3280.706(b) (1) through (4). (1) Steel or wrought-iron pipe shall comply with ANSI B 36.10-1979, Welded and Seamless Wrought Steel Pipe. Threaded copper or brass pipe in iron pipe sizes may be used. (2) Fittings for oil piping shall be wrought-iron, malleable iron, steel, or brass (containing...

  2. Experimental use of Line-X coated steel pipe piles, Clay Hill Bridge (#2157) replacement project over the Mousam River, Route 9/Western Avenue, Kennebunk, Maine.

    DOT National Transportation Integrated Search

    2013-02-01

    Steel pipe piles used by MaineDOT for bridge construction are typically coated with a fusion-bonded epoxy (FBE). FBE is a powder-based coating with properties similar to traditional : epoxies. Its name is derived from the process by which it adheres ...

  3. Effects of Mo, Cr, and V Additions on Tensile and Charpy Impact Properties of API X80 Pipeline Steels

    NASA Astrophysics Data System (ADS)

    Han, Seung Youb; Shin, Sang Yong; Seo, Chang-Hyo; Lee, Hakcheol; Bae, Jin-Ho; Kim, Kisoo; Lee, Sunghak; Kim, Nack J.

    2009-08-01

    In this study, four API X80 pipeline steels were fabricated by varying Mo, Cr, and V additions, and their microstructures and crystallographic orientations were analyzed to investigate the effects of their alloying compositions on tensile properties and Charpy impact properties. Because additions of Mo and V promoted the formation of fine acicular ferrite (AF) and granular bainite (GB) while prohibiting the formation of coarse GB, they increased the strength and upper-shelf energy (USE) and decreased the energy transition temperature (ETT). The addition of Cr promoted the formation of coarse GB and hard secondary phases, thereby leading to an increased effective grain size, ETT, and strength, and a decreased USE. The addition of V resulted in a higher strength, a higher USE, a smaller effective grain size, and a lower ETT, because it promoted the formation of fine and homogeneous of AF and GB. The steel that contains 0.3 wt pct Mo and 0.06 wt pct V without Cr had the highest USE and the lowest ETT, because its microstructure was composed of fine AF and GB while its maintained excellent tensile properties.

  4. 75 FR 73033 - Circular Welded Carbon Steel Pipes and Tubes from Thailand: Amended Final Results of Antidumping...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-11-29

    ... Pipes and Tubes from Thailand: Amended Final Results of Antidumping Duty Administrative Review AGENCY... Thailand, covering the period March 1, 2008 through February 28, 2009. The final results were subsequently... Circular Welded Carbon Steel Pipes and Tubes From Thailand: Final Results of Antidumping Duty...

  5. Feasibility of Underwater Friction Stir Welding of HY-80 Steel

    DTIC Science & Technology

    2011-03-01

    UNDERWATER FRICTION STIR WELDING OF HY-80 STEEL by William C. Stewart March 2011 Thesis Advisor: Terry McNelley Second Reader: Sarath Menon...Master’s Thesis 4. TITLE AND SUBTITLE Feasibility of Underwater Friction Stir Welding of HY-80 Steel 5. FUNDING NUMBERS 6. AUTHOR(S) William...DISTRIBUTION CODE A 13. ABSTRACT (maximum 200 words) The purpose of this thesis is to determine the feasibility of underwater friction stir welding

  6. Arc Welding-Pipe, 3-25. Military Curriculum Materials for Vocational and Technical Education.

    ERIC Educational Resources Information Center

    Ohio State Univ., Columbus. National Center for Research in Vocational Education.

    This instructor guide and text for a secondary-postsecondary level course in arc welding-pipe comprise one of a number of military-developed curriculum packages selected for adaptation to vocational instruction and curriculum development in a civilian setting. Purpose of the course is to teach students to weld 5-inch mild steel schedule 80 pipe,…

  7. 78 FR 65272 - Circular Welded Carbon Steel Pipes and Tubes From Thailand: Final Results of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-10-31

    ... Pipes and Tubes From Thailand: Final Results of Antidumping Duty Administrative Review; 2011-2012 AGENCY... and tubes from Thailand. This review covers two producers and/or exporters of the subject merchandise... duty order on circular welded carbon steel pipes and tubes from Thailand.\\1\\ We invited interested...

  8. 76 FR 63902 - Circular Welded Carbon Steel Pipes and Tubes From Taiwan: Final Results of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-10-14

    ... Pipes and Tubes From Taiwan: Final Results of Antidumping Duty Administrative Review AGENCY: Import... Department of Commerce (the Department) published the preliminary results of the administrative review of the antidumping duty order on circular welded carbon steel pipes and tubes from Taiwan. See Preliminary Results of...

  9. 77 FR 10773 - Stainless Steel Butt-Weld Pipe Fittings From Italy, Malaysia, and the Philippines; Scheduling of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-02-23

    ... Butt-Weld Pipe Fittings From Italy, Malaysia, and the Philippines; Scheduling of Expedited Five-Year... orders on stainless steel butt-weld pipe fittings from Italy, Malaysia, and the Philippines would be... certificate of service. Determination.--The Commission has determined to exercise its authority to extend the...

  10. 76 FR 65179 - Certain Welded Carbon Steel Standard Pipe From Turkey: Extension of Time for Preliminary Results...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-10-20

    ... Standard Pipe From Turkey: Extension of Time for Preliminary Results of Countervailing Duty Administrative... carbon steel standard pipe from Turkey covering the period of review January 1, 2010, through December 31... Republic of Turkey. There are 14 programs under review in addition to several newly alleged subsidies...

  11. 77 FR 72818 - Circular Welded Carbon Steel Pipes and Tubes From Turkey; Final Results of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-12-06

    ... Pipes and Tubes From Turkey; Final Results of Antidumping Duty Administrative Review; 2010 to 2011... tubes from Turkey.\\1\\ This review covers four producers and exporters of subject merchandise: Borusan....'' \\1\\ See Circular Welded Carbon Steel Pipes and Tubes From Turkey: Notice of Preliminary Results of...

  12. 24 CFR 3280.706 - Oil piping systems.

    Code of Federal Regulations, 2014 CFR

    2014-04-01

    ...) through (4). (1) Steel or wrought-iron pipe shall comply with ANSI B 36.10-1979, Welded and Seamless Wrought Steel Pipe. Threaded copper or brass pipe in iron pipe sizes may be used. (2) Fittings for oil... Seamless Copper Tube for Air Conditioning and Refrigeration Field Service. (4) Steel tubing shall have a...

  13. Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions

    PubMed Central

    Yang, Yuanfeng; Joshi, Gaurav R.; Akid, Robert

    2015-01-01

    The aim of this research was to investigate the influence of metallurgy on the corrosion behaviour of separate weld zone (WZ) and parent plate (PP) regions of X65 pipeline steel in a solution of deionised water saturated with CO2, at two different temperatures (55 °C and 80 °C) and at initial pH~4.0. In addition, a non-electrochemical immersion experiment was also performed at 80 °C in CO2, on a sample portion of X65 pipeline containing part of a weld section, together with adjacent heat affected zones (HAZ) and parent material. Electrochemical impedance spectroscopy (EIS) was used to evaluate the corrosion behaviour of the separate weld and parent plate samples. This study seeks to understand the significance of the different microstructures within the different zones of the welded X65 pipe in CO2 environments on corrosion performance; with particular attention given to the formation of surface scales; and their composition/significance. The results obtained from grazing incidence X-ray diffraction (GIXRD) measurements suggest that, post immersion, the parent plate substrate is scale free, with only features arising from ferrite (α-Fe) and cementite (Fe3C) apparent. In contrast, at 80 °C, GIXRD from the weld zone substrate, and weld zone/heat affected zone of the non-electrochemical sample indicates the presence of siderite (FeCO3) and chukanovite (Fe2CO3(OH)2) phases. Scanning Electron Microscopy (SEM) on this surface confirmed the presence of characteristic discrete cube-shaped crystallites of siderite together with plate-like clusters of chukanovite.

  14. Corrosion-Fatigue Cracking in HY-80 and HY-130 Steels

    DTIC Science & Technology

    2015-01-22

    Naval Research Laboratory Washington, DC 20375-5320 NRL/MR/6355--15-9584 Corrosion- Fatigue Cracking in HY-80 and HY-130 Steels January 22, 2015 P.S...RESPONSIBLE PERSON 19b. TELEPHONE NUMBER (include area code) b. ABSTRACT c. THIS PAGE 18. NUMBER OF PAGES 17. LIMITATION OF ABSTRACT Corrosion- Fatigue ...including [NaCl] concentration) and load ratio on fatigue crack growth kinetics of HY-80 and HY-130 steels. Fracture mechanics wedge-opening-load

  15. Electrolytic etching of fine stainless-steel pipes patterned by laser-scan lithography

    NASA Astrophysics Data System (ADS)

    Takahashi, Hiroshi; Sagara, Tomoya; Horiuchi, Toshiyuki

    2017-07-01

    Recently, it is required to develop a method for fabricating cylindrical micro-components in the field of measurement and medical engineering. Here, electrolytic etching of fine stainless-steel pipes patterned by laser-scan lithography was researched. The pipe diameter was 100 μm. At first, a pipe coated with 3-7 μm thick positive resist (tok, PMER P LA-900) was exposed to a violet laser beam with a wavelength of 408 nm (Neoark,TC20-4030-45). The laser beam was reshaped in a circle by placing a pinhole, and irradiated on the pipe by reducing the size in 1/20 using a reduction projection optics. Linearly arrayed 22 slit patterns with a width of 25 μm and a length of 175 μm were delineated in every 90-degree circumferential direction. That is, 88 slits in total were delineated at an exposure speed of 110 μm/s. In the axial direction, patterns were delineated at intervals of 90 μm. Following the pattern delineation, the pipe masked by the resist patterns was electrolytically etched. The pipe was used as an anode and an aluminum cylinder was set as a cathode around the pipe. As the electrolyte, aqueous solution of NaCl and NH4Cl was used. After etching the pipe, the resist was removed by ultrasonic cleaning in acetone. Although feasibility for fabricating multi-slit pipes was demonstrated, sizes of the etched slits were enlarged being caused by the undercut, and the shapes were partially deformed, and all the pipes were snapped at the chuck side.

  16. Effects of Cooling Conditions on Tensile and Charpy Impact Properties of API X80 Linepipe Steels

    NASA Astrophysics Data System (ADS)

    Han, Seung Youb; Shin, Sang Yong; Lee, Sunghak; Kim, Nack J.; Bae, Jin-Ho; Kim, Kisoo

    2010-02-01

    In this study, four API X80 linepipe steel specimens were fabricated by varying the cooling rate and finish cooling temperature, and their microstructures and crystallographic orientations were analyzed to investigate the effects of the cooling conditions on the tensile and Charpy impact properties. All the specimens consisted of acicular ferrite (AF), granular bainite (GB), and martensite-austenite (MA) constituents. The volume fraction of MA increased with an increasing cooling rate, and the volume fraction and size of MA tended to decrease with an increasing finish cooling temperature. According to the crystallographic orientation analysis data, the effective grain size and unit crack path decreased as fine ACs having a large amount of high-angle grain boundaries were homogeneously formed, thereby leading to the improvement in the Charpy impact properties. The specimen fabricated with the higher cooling rate and lower finish cooling temperature had the highest upper-shelf energy (USE) and the lowest energy transition temperature (ETT), because it contained a large amount of MA homogeneously distributed inside fine AFs, while its tensile properties remained excellent.

  17. 75 FR 22372 - Certain Seamless Carbon and Alloy Steel Standard, Line, and Pressure Pipe From the People's...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-04-28

    ... Alloy Steel Standard, Line, and Pressure Pipe From the People's Republic of China: Preliminary..., line, and pressure pipe from the People's Republic of China (``PRC'') is being, or is likely to be...'s Republic of China, dated September 16, 2009 (``Petition''). On September 28, 2009, TMK IPSCO and...

  18. Demonstration and Validation of Stainless Steel Materials for Critical Above Grade Piping in Highly Corrosive Locations

    DTIC Science & Technology

    2017-05-01

    Protecting And Bonding Reinforcing Steel In Cement -Based Composites, Corrosion 2009, Atlanta, GA, 22-26 March 2009. 7. Hock, V., O. Marshall, S...ER D C/ CE RL T R- 17 -1 3 DoD Corrosion Prevention and Control Program Demonstration and Validation of Stainless Steel Materials for...ERDC/CERL TR-17-13 May 2017 Demonstration and Validation of Stainless Steel Materials for Critical Above-Grade Piping in Highly Corrosive

  19. 75 FR 6183 - Certain Seamless Carbon and Alloy Steel Standard, Line, and Pressure Pipe from the People's...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-02-08

    ... antidumping duty investigation on certain seamless carbon and alloy steel standard, line, and pressure pipe from the People's Republic of China. See Certain Seamless Carbon and Alloy Steel Standard, Line, and... DEPARTMENT OF COMMERCE INTERNATIONAL TRADE ADMINISTRATION (A-570-956) Certain Seamless Carbon and...

  20. The Effect of Ultrasonic Peening on Service Life of the Butt-Welded High-Temperature Steel Pipes

    NASA Astrophysics Data System (ADS)

    Daavari, Morteza; Vanini, Seyed Ali Sadough

    2015-09-01

    Residual stresses introduced by manufacturing processes such as casting, forming, machining, and welding have harmful effects on the mechanical behavior of the structures. In addition to the residual stresses, weld toe stress concentration can play a determining effect. There are several methods to improve the mechanical properties such as fatigue behavior of the welded structures. In this paper, the effects of ultrasonic peening on the fatigue life of the high-temperature seamless steel pipes, used in the petrochemical environment, have been investigated. These welded pipes are fatigued due to thermal and mechanical loads caused by the cycle of cooling, heating, and internal pressure fluctuations. Residual stress measurements, weld geometry estimation, electrochemical evaluations, and metallography investigations were done as supplementary examinations. Results showed that application of ultrasonic impact treatment has led to increased fatigue life, fatigue strength, and corrosion resistance of A106-B welded steel pipes in petrochemical corrosive environment.

  1. 76 FR 67146 - Stainless Steel Butt-Weld Pipe Fittings From Italy; Extension of Time Limit for Preliminary...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-10-31

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-475-828] Stainless Steel Butt-Weld... antidumping duty order on stainless steel butt-weld pipe fittings from Italy in the Federal Register. See... preliminary results of this review within the original time frame because it needs to obtain additional...

  2. 24 CFR 3280.705 - Gas piping systems.

    Code of Federal Regulations, 2013 CFR

    2013-04-01

    ... § 3280.705(b) (1) through (4). (1) Steel or wrought-iron pipe shall comply with ANSI Standard B36.10-1979, Welded and Seamless Wrought Steel Pipe. Threaded brass pipe in iron pipe sizes may be used. Threaded brass pipe shall comply with ASTM B43-91, Standard Specification for Seamless Red Brass Pipe, Standard...

  3. 24 CFR 3280.705 - Gas piping systems.

    Code of Federal Regulations, 2012 CFR

    2012-04-01

    ... § 3280.705(b) (1) through (4). (1) Steel or wrought-iron pipe shall comply with ANSI Standard B36.10-1979, Welded and Seamless Wrought Steel Pipe. Threaded brass pipe in iron pipe sizes may be used. Threaded brass pipe shall comply with ASTM B43-91, Standard Specification for Seamless Red Brass Pipe, Standard...

  4. 24 CFR 3280.705 - Gas piping systems.

    Code of Federal Regulations, 2010 CFR

    2010-04-01

    ... § 3280.705(b) (1) through (4). (1) Steel or wrought-iron pipe shall comply with ANSI Standard B36.10-1979, Welded and Seamless Wrought Steel Pipe. Threaded brass pipe in iron pipe sizes may be used. Threaded brass pipe shall comply with ASTM B43-91, Standard Specification for Seamless Red Brass Pipe, Standard...

  5. 24 CFR 3280.705 - Gas piping systems.

    Code of Federal Regulations, 2011 CFR

    2011-04-01

    ... § 3280.705(b) (1) through (4). (1) Steel or wrought-iron pipe shall comply with ANSI Standard B36.10-1979, Welded and Seamless Wrought Steel Pipe. Threaded brass pipe in iron pipe sizes may be used. Threaded brass pipe shall comply with ASTM B43-91, Standard Specification for Seamless Red Brass Pipe, Standard...

  6. 49 CFR 195.112 - New pipe.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... with the following: (a) The pipe must be made of steel of the carbon, low alloy-high strength, or alloy... sets forth the chemical requirements for the pipe steel and mechanical tests for the pipe to provide... made, the specified minimum yield strength or grade, and the pipe size. The marking must be applied in...

  7. 49 CFR 195.112 - New pipe.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... with the following: (a) The pipe must be made of steel of the carbon, low alloy-high strength, or alloy... sets forth the chemical requirements for the pipe steel and mechanical tests for the pipe to provide... made, the specified minimum yield strength or grade, and the pipe size. The marking must be applied in...

  8. 49 CFR 195.112 - New pipe.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... with the following: (a) The pipe must be made of steel of the carbon, low alloy-high strength, or alloy... sets forth the chemical requirements for the pipe steel and mechanical tests for the pipe to provide... made, the specified minimum yield strength or grade, and the pipe size. The marking must be applied in...

  9. 49 CFR 195.112 - New pipe.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... with the following: (a) The pipe must be made of steel of the carbon, low alloy-high strength, or alloy... sets forth the chemical requirements for the pipe steel and mechanical tests for the pipe to provide... made, the specified minimum yield strength or grade, and the pipe size. The marking must be applied in...

  10. 49 CFR 195.112 - New pipe.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... with the following: (a) The pipe must be made of steel of the carbon, low alloy-high strength, or alloy... sets forth the chemical requirements for the pipe steel and mechanical tests for the pipe to provide... made, the specified minimum yield strength or grade, and the pipe size. The marking must be applied in...

  11. 75 FR 63439 - Certain Welded Carbon Steel Standard Pipes and Tubes From India: Extension of the Final Results...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-10-15

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-533-502] Certain Welded Carbon Steel... or (202) 482-1690, respectively. SUPPLEMENTARY INFORMATION: Background On June 14, 2010, the... antidumping duty order on certain welded carbon steel standard pipes and tubes from India. See Certain Welded...

  12. 76 FR 3612 - Circular Welded Carbon Steel Pipes and Tubes From Taiwan; Extension of Time Limit for Preliminary...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-01-20

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-583-008] Circular Welded Carbon Steel... Steel Pipes and Tubes From Taiwan: Notice of Partial Rescission of Antidumping Duty Administrative... complete the preliminary results of this review within the original time frame because we require...

  13. Special Features of Structure Formation in Pipes from Medium-Carbon Low-Alloy Steel 32G2F Under Heat Treatment

    NASA Astrophysics Data System (ADS)

    Stepanov, A. I.; Belikov, S. V.; Musikhin, S. A.; Burmasov, S. P.; Popov, A. A.

    2017-03-01

    Special features of formation of structure and properties of seamless pipes from medium-carbon low-alloy steel for oil and gas applications are considered and associated with chemical inhomogeneity of the metal of the pipes.

  14. Determination of ac conductor and pipe loss in pipe-type cable systems. Final report

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Silver, D.A.; Seman, G.W.

    1982-02-01

    The results are presented of investigations into the determination of the ac/dc resistance ratios of high and extra high voltage pipe-type cables with conventional and large size segmental conductors in carbon steel, stainless steel and aluminum pipes in three cable per pipe and single cable per pipe configurations. The measurements included 115 through 765 kV cables with copper, enamel coated copper, and aluminum conductors in sizes of 2000 kcmil (1015 mm/sup 2/), 3250 kcmil (1650 mm/sup 2/), and 3500 kcmil (1776 mm/sup 2/). Calculations using presently available techniques were employed to provide correlation between measured and calculated values in bothmore » magnetic and non-magnetic pipes. In addition, a number of new techniques in conductor construction, pipe material and pipe liners and cable wraps were investigated as means of decreasing the ac/dc resistance ratios of pipe-type cables. Finally, the various systems studied were compared on the basis of system MVA rating and by evaluation of installed and overall operating costs as compared to conventional three cable per pipe systems installed in carbon steel pipes.« less

  15. Transient Response to Rapid Cooling of a Stainless Steel Sodium Heat Pipe

    NASA Technical Reports Server (NTRS)

    Mireles, Omar R.; Houts, Michael G.

    2011-01-01

    Compact fission power systems are under consideration for use in long duration space exploration missions. Power demands on the order of 500 W, to 5 kW, will be required for up to 15 years of continuous service. One such small reactor design consists of a fast spectrum reactor cooled with an array of in-core alkali metal heat pipes coupled to thermoelectric or Stirling power conversion systems. Heat pipes advantageous attributes include a simplistic design, lack of moving parts, and well understood behavior. Concerns over reactor transients induced by heat pipe instability as a function of extreme thermal transients require experimental investigations. One particular concern is rapid cooling of the heat pipe condenser that would propagate to cool the evaporator. Rapid cooling of the reactor core beyond acceptable design limits could possibly induce unintended reactor control issues. This paper discusses a series of experimental demonstrations where a heat pipe operating at near prototypic conditions experienced rapid cooling of the condenser. The condenser section of a stainless steel sodium heat pipe was enclosed within a heat exchanger. The heat pipe - heat exchanger assembly was housed within a vacuum chamber held at a pressure of 50 Torr of helium. The heat pipe was brought to steady state operating conditions using graphite resistance heaters then cooled by a high flow of gaseous nitrogen through the heat exchanger. Subsequent thermal transient behavior was characterized by performing an energy balance using temperature, pressure and flow rate data obtained throughout the tests. Results indicate the degree of temperature change that results from a rapid cooling scenario will not significantly influence thermal stability of an operating heat pipe, even under extreme condenser cooling conditions.

  16. Stainless Steel to Titanium Bimetallic Transitions

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Kaluzny, J. A.; Grimm, C.; Passarelli, D.

    In order to use stainless steel piping in an LCLS-II (Linac Coherent Light Source Upgrade) cryomodule, stainless steel to titanium bimetallic transitions are needed to connect the stainless steel piping to the titanium cavity helium vessel. Explosion bonded stainless steel to titanium transition pieces and bimetallic transition material samples have been tested. A sample transition tube was subjected to tests and x-ray examinations between tests. Samples of the bonded joint material were impact and tensile tested at room temperature as well as liquid helium temperature. The joint has been used successfully in horizontal tests of LCLS-II cavity helium vessels andmore » is planned to be used in LCLS-II cryomodules. Results of material sample and transition tube tests will be presented.« less

  17. Effects of microstructure banding on hydrogen assisted fatigue crack growth in X65 pipeline steels

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Ronevich, Joseph A.; Somerday, Brian P.; San Marchi, Chris W.

    Banded ferrite-pearlite X65 pipeline steel was tested in high pressure hydrogen gas to evaluate the effects of oriented pearlite on hydrogen assisted fatigue crack growth. Test specimens were oriented in the steel pipe such that cracks propagated either parallel or perpendicular to the banded pearlite. The ferrite-pearlite microstructure exhibited orientation dependent behavior in which fatigue crack growth rates were significantly lower for cracks oriented perpendicular to the banded pearlite compared to cracks oriented parallel to the bands. Thus the reduction of hydrogen assisted fatigue crack growth across the banded pearlite is attributed to a combination of crack-tip branching and impededmore » hydrogen diffusion across the banded pearlite.« less

  18. Effects of microstructure banding on hydrogen assisted fatigue crack growth in X65 pipeline steels

    DOE PAGES

    Ronevich, Joseph A.; Somerday, Brian P.; San Marchi, Chris W.

    2015-09-10

    Banded ferrite-pearlite X65 pipeline steel was tested in high pressure hydrogen gas to evaluate the effects of oriented pearlite on hydrogen assisted fatigue crack growth. Test specimens were oriented in the steel pipe such that cracks propagated either parallel or perpendicular to the banded pearlite. The ferrite-pearlite microstructure exhibited orientation dependent behavior in which fatigue crack growth rates were significantly lower for cracks oriented perpendicular to the banded pearlite compared to cracks oriented parallel to the bands. Thus the reduction of hydrogen assisted fatigue crack growth across the banded pearlite is attributed to a combination of crack-tip branching and impededmore » hydrogen diffusion across the banded pearlite.« less

  19. Long-term strength and allowable stresses of grade 10Kh9MFB and X10CrMoVNb9-1 (T91/P91) chromium heat-resistant steels

    NASA Astrophysics Data System (ADS)

    Skorobogatykh, V. N.; Danyushevskiy, I. A.; Schenkova, I. A.; Prudnikov, D. A.

    2015-04-01

    Currently, grade X10CrMoVNb9-1 (T91, P91) and 10Kh9MFB (10Kh9MFB-Sh) chromium steels are widely applied in equipment manufacturing for thermal power plants in Russia and abroad. Compilation and comparison of tensile, impact, and long-term strength tests results accumulated for many years of investigations of foreign grade X10CrMoVNb9-1, T91, P91, and domestic grade 10Kh9MFB (10Kh9MFB-Sh) steels is carried out. The property identity of metals investigated is established. High strength and plastic properties of steels, from which pipes and other products are made, for operation under creep conditions are confirmed. Design characteristics of long-term strength on the basis of tests with more than one million of hour-samples are determined ( and at temperatures of 500-650°C). The table of recommended allowable stresses for grade 10Kh9MFB, 10Kh9MFB-SH, X10CrMoVNb9-1, T91, and P91 steels is developed. The long-time properties of pipe welded joints of grade 10Kh9MFB+10Kh9MFB, 10Kh9MFB-Sh+10Kh9MFB-Sh, X10CrMoVNb9-1+X10CrMoVNb9-1, P91+P91, T91+T91, 10Kh9MFB (10Kh9MFB-Sh)+X10CrMoVNb9-1(T/P91) steels is researched. The welded joint reduction factor is experimentally determined.

  20. Evaluation of Delamination of X80 Pipeline Steel Coating Under Alternating Stray Current Via Scanning Electrochemical Microscopy

    NASA Astrophysics Data System (ADS)

    Wang, Xinhua; Liu, Qiang; Chun, Yingchun; Li, Yingchao; Wang, Zuquan

    2018-04-01

    The delamination of epoxy coating on X80 pipeline steel was evaluated under various stray alternating current (AC) interferences (0-300 A/m2). Qualitative and quantitative analyses were carried out using scanning electrochemical microscopy (SECM), electrochemical impedance spectroscopy (EIS), and three-dimensional digital microscopy. The results show that the SECM current is directly proportional to the soaking time and applied current density. The variation in SECM current curve shape indicates the delamination distance of epoxy coatings at the defect area. The depths of corrosion pits at 50, 100, and 300 A/m2 stray currents were 140, 160, and 240 μm, respectively. The corrosion pits also became wider with increasing current densities. With increasing stray AC densities, both the coating delamination and pit depth became more severe at the same soaking time. The EIS results show that the change in impedance was not significant without stray current, whereas the impedance first decreased and then increased when stray current was applied. These results are consistent with the SECM measurements.

  1. 75 FR 1335 - Circular Welded Carbon Steel Pipes and Tubes from Taiwan; Extension of Time Limit for Preliminary...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-01-11

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-583-008] Circular Welded Carbon Steel... review of the antidumping duty order on circular welded carbon steel pipes and tubes from Taiwan.\\1\\ On... review within the original time frame because we require additional time to obtain information from the...

  2. 46 CFR 105.20-5 - Piping systems.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... that seamless steel pipe or tubing which provides equivalent safety may be used for diesel cargo... that steel or nodular iron may be used in cargo systems utilizing steel pipe or tubing. (c) Aluminium...

  3. 46 CFR 105.20-5 - Piping systems.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... that seamless steel pipe or tubing which provides equivalent safety may be used for diesel cargo... that steel or nodular iron may be used in cargo systems utilizing steel pipe or tubing. (c) Aluminium...

  4. 46 CFR 105.20-5 - Piping systems.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... that seamless steel pipe or tubing which provides equivalent safety may be used for diesel cargo... that steel or nodular iron may be used in cargo systems utilizing steel pipe or tubing. (c) Aluminium...

  5. 46 CFR 105.20-5 - Piping systems.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... that seamless steel pipe or tubing which provides equivalent safety may be used for diesel cargo... that steel or nodular iron may be used in cargo systems utilizing steel pipe or tubing. (c) Aluminium...

  6. Multiple Restart Testing of a Stainless Steel Sodium Heat Pipe Module

    NASA Technical Reports Server (NTRS)

    Martin, James; Mireles, Omar; Reid, Robert

    2005-01-01

    A heat pipe cooled reactor is one of several candidate reactor cores being considered for space power and propulsion systems to support future space exploration activities. Long life heat pipe modules. with designs verified through a combination of theoretical analysis and experimental evaluations. would be necessary to establish the viability of this option. A hardware-based program was initiated to begin experimental testing of components to verify compliance of proposed designs. To this end, a number of stainless steel/sodium heat pipe modules have been designed and fabricated to support experimental testing of a Safe Affordable Fission Engine (SAFE) project, a 100-kWt core design pursued jointly by the Marshall Space Flight Center and the Los Alamos National Laboratory. One of the SAFE heat pipe modules was successfully subjected to over 200 restarts. examining the behavior of multiple passive freeze/thaw operations. Typical operation included a 1-hour startup to an average evaporator temperature of 1000 K followed by a 15 minute hold at temperature. Nominal maximum input power during the hold period was 1.9 kW. Between heating cycles the module was cooled to less than 325 K, returning the sodium to a frozen state in preparation fop the next startup cycle.

  7. 46 CFR 105.20-5 - Piping systems.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... that seamless steel pipe or tubing which provides equivalent safety may be used for diesel cargo... that steel or nodular iron may be used in cargo systems utilizing steel pipe or tubing. (c) Aluminum or...

  8. Establishing a design procedure for buried steel-reinforced high-density polyethylene pipes : a field study.

    DOT National Transportation Integrated Search

    2015-11-01

    Two field tests were conducted to investigate the field performance of steel-reinforced high-density polyethylene : (SRHDPE) pipes during installation and under traffic loading. One test site was located on E 1000 road in Lawrence, KS, which is : clo...

  9. 46 CFR 182.455 - Fuel piping.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... piping of other materials, such as seamless steel pipe or tubing, which provide equivalent safety may be... shock. Fuel filters fitted with bowls of other than steel construction must be approved by the Commandant and be protected from mechanical damage. Approval of bowls of other than steel construction will...

  10. 46 CFR 182.455 - Fuel piping.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... piping of other materials, such as seamless steel pipe or tubing, which provide equivalent safety may be... shock. Fuel filters fitted with bowls of other than steel construction must be approved by the Commandant and be protected from mechanical damage. Approval of bowls of other than steel construction will...

  11. 46 CFR 182.455 - Fuel piping.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... piping of other materials, such as seamless steel pipe or tubing, which provide equivalent safety may be... shock. Fuel filters fitted with bowls of other than steel construction must be approved by the Commandant and be protected from mechanical damage. Approval of bowls of other than steel construction will...

  12. 46 CFR 182.455 - Fuel piping.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... piping of other materials, such as seamless steel pipe or tubing, which provide equivalent safety may be... shock. Fuel filters fitted with bowls of other than steel construction must be approved by the Commandant and be protected from mechanical damage. Approval of bowls of other than steel construction will...

  13. Heat Pipe Materials Compatibility

    NASA Technical Reports Server (NTRS)

    Eninger, J. E.; Fleischman, G. L.; Luedke, E. E.

    1976-01-01

    An experimental program to evaluate noncondensable gas generation in ammonia heat pipes was completed. A total of 37 heat pipes made of aluminum, stainless steel and combinations of these materials were processed by various techniques, operated at different temperatures and tested at low temperature to quantitatively determine gas generation rates. In order of increasing stability are aluminum/stainless combination, all aluminum and all stainless heat pipes. One interesting result is the identification of intentionally introduced water in the ammonia during a reflux step as a means of surface passivation to reduce gas generation in stainless-steel/aluminum heat pipes.

  14. 24 CFR 3280.705 - Gas piping systems.

    Code of Federal Regulations, 2014 CFR

    2014-04-01

    ... consist of one or more of the materials described in § 3280.705(b) (1) through (4). (1) Steel or wrought-iron pipe shall comply with ANSI Standard B36.10-1979, Welded and Seamless Wrought Steel Pipe. Threaded... Specification for Seamless Red Brass Pipe, Standard Sizes. (2) Fittings for gas piping shall be wrought iron...

  15. Numerical simulation of micro-crack occurring in pipe made of stainless steel

    NASA Astrophysics Data System (ADS)

    Wotzka, Daria

    2017-10-01

    Research works carried out regard to studies aiming at determination of the effect of cumulative duty operation on the development of micro-cracks in pipelines for transport of chemical substances. This paper presents results of computer simulations of a pipeline made of stainless steel. The model was investigated using the COMSOL Multiphysics environment. The object under study was divided into sub areas and then discretized according to the FEM method. The physico-chemical parameters of individual areas were defined based on measurement data. The main aim of research works was the modeling of acoustic emission wave, which is emitted in the vicinity of the tip of micro-crack as a result of its development. In order to solve the task, heterogeneity in the structure of the material, referred to damage/micro-crack, causing local stresses was assumed. The local stresses give rise to elastic waves, which propagate in the material in all directions. When the emission waves reach the boundaries of the pipe they are then transferred into acoustic waves and propagate in the surround air, until their natural attenuation. The numerical model takes into account the effect of high pressure (3.6 MPa) and negative temperature (-100°C) of the gas, transported inside the pipe. The influence of changes of these values in the range of ± 20% on the obtained results was investigated. The main contribution of the works is the multiphysical simulation model of transportation pipe made of steel, coupling structural mechanics, thermal conductivity and acoustic waves.

  16. Multiple Restart Testing of a Stainless Steel Sodium Heat Pipe Module

    NASA Astrophysics Data System (ADS)

    Martin, James; Mireles, Omar; Reid, Robert

    2005-02-01

    A heat pipe cooled reactor is one of several candidate reactor concepts being considered for space power and propulsion systems to support future space exploration activities. Long life heat pipe modules, with concepts verified through a combination of theoretical analysis and experimental evaluations, would be necessary to establish the viability of this option. A number of stainless steel/sodium heat pipe modules have been designed and fabricated to support experimental testing of a Safe Affordable Fission Engine (SAFE) project, a 100-kWt core design pursued jointly by the Marshall Space Flight Center and the Los Alamos National Laboratory. One of the SAFE heat pipe modules was successfully subjected to over 200 restarts, examining the behavior of multiple passive freeze/thaw operations. Typical operation included a 1-hour startup to an average evaporator temperature of 1000 K followed by a 15-minute hold at temperature. Nominal maximum input power to the evaporator (measured at the power supply) during the hold period was 1.9 kW, with approximately 1.6 kW calculated as the axial power transfer to the condenser (the 300W difference was lost to environment at the evaporator surface). Between heating cycles the module was cooled to less than 325 K, returning the sodium to a frozen state in preparation for the next startup cycle.

  17. Electron Cloud in Steel Beam Pipe vs Titanium Nitride Coated and Amorphous Carbon Coated Beam Pipes in Fermilab's Main Injector

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Backfish, Michael

    This paper documents the use of four retarding field analyzers (RFAs) to measure electron cloud signals created in Fermilab’s Main Injector during 120 GeV operations. The first data set was taken from September 11, 2009 to July 4, 2010. This data set is used to compare two different types of beam pipe that were installed in the accelerator. Two RFAs were installed in a normal steel beam pipe like the rest of the Main Injector while another two were installed in a one meter section of beam pipe that was coated on the inside with titanium nitride (TiN). A secondmore » data run started on August 23, 2010 and ended on January 10, 2011 when Main Injector beam intensities were reduced thus eliminating the electron cloud. This second run uses the same RFA setup but the TiN coated beam pipe was replaced by a one meter section coated with amorphous carbon (aC). This section of beam pipe was provided by CERN in an effort to better understand how an aC coating will perform over time in an accelerator. The research consists of three basic parts: (a) continuously monitoring the conditioning of the three different types of beam pipe over both time and absorbed electrons (b) measurement of the characteristics of the surrounding magnetic fields in the Main Injector in order to better relate actual data observed in the Main Injector with that of simulations (c) measurement of the energy spectrum of the electron cloud signals using retarding field analyzers in all three types of beam pipe.« less

  18. 77 FR 32539 - Circular Welded Carbon-Quality Steel Pipe From the United Arab Emirates: Preliminary...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-06-01

    ... Investigations; Request for Comment, 73 FR 26371 (May 9, 2008). A. Targeted Dumping Test We conducted customer..., 2011, the Department initiated the antidumping duty investigations on certain steel pipe from India... the Socialist Republic of Vietnam: Initiation of Antidumping Duty Investigations, 76 FR 72164...

  19. 75 FR 78216 - Certain Circular Welded Non-Alloy Steel Pipe From Mexico: Preliminary Results of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-12-15

    ... Non-Alloy Steel Pipe from Brazil, the Republic of Korea (Korea), Mexico, and Venezuela and Amendment..., Director, Office 7 to Michael Walsh, Director, AD/CVD Revenue Policy & Programs, U.S. Customs and Border...

  20. Seam-weld quality of modern ERW/HFI line pipe

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Groeneveld, T.P.; Barnes, C.R.

    1991-09-01

    This study was undertaken to determine whether the seam-weld quality of modern ERW (electric resistance-welded)/HFI (high-frequency induction) welded pipe has been improved and justifies more widespread use of this type of pipe in critical applications. Wider use of ERW/HFI line pipe in gas-transmission lines would be expected to reduce construction costs. Five recently produced, heavy wall pipes fabricated using high-frequency electric-resistance welding (ERW) processes to make the seam weld and one pipe fabricated using the high-frequency induction (HFI) welding process to make the seam weld were studied. Four of the pipes were Grade X-60, one was Grade X-65, and onemore » was Grade X-70. All of the pipes were produced from microalloyed, controlled-rolled steels, and the weld zones were post-weld normalized. Ultrasonic inspection of the seam welds in the six pipe sections evaluated revealed no indications of defects. The tensile properties of all of the weld zones exceeded the minimum specified yield strengths for the respective grades of pipe and all of the pipes exhibited ductile failures either in the weld zone or in the base metal. Five of the six pipes exhibited ductile failures either in the weld zone or in the base metal. Five of the six pipes exhibited relatively low 85% shear area transition temperatures and relatively high upper-shelf energy absorptions as determined with Charpy V-notch specimens. In addition, for two of the three joints of pipe for which the properties were determined at both ends of the pipe, the tensile and impact properties showed little variation from end-to-end. However, for the other joint of pipe, the impact properties varied substantially from one end to the other.« less

  1. 77 FR 18266 - Stainless Steel Butt-Weld Pipe Fittings From Italy, Malaysia, and the Philippines; Revised...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-03-27

    ... INTERNATIONAL TRADE COMMISSION [Investigation Nos. 731-TA-865-867 (Second Review)] Stainless Steel Butt-Weld Pipe Fittings From Italy, Malaysia, and the Philippines; Revised Schedule for the Subject Reviews AGENCY: United States International Trade Commission. ACTION: Notice. DATES: Effective Date: March...

  2. Research and Development of Heavy Gauge X80 Pipeline Plate Utilizing Optimized Rolling and Cooling Process

    NASA Astrophysics Data System (ADS)

    Li, Shaopo; Li, Jiading; Ding, Wenhua; Zhang, Hai

    This paper reports on the experience with the production of 27/33 mm X80 heavy wall thicknesses, large OD (48") in Shouqin Steel Co., Ltd. (SQS). Considering the technology capability of the plate mill in SQS, a optimized rolling and cooling process was developed to achieve stable heavy gauge X80 mechanical properties. The importance of the slab reheating process and rolling schedule will be discussed in the paper. In addition, the per pass reductions logic used during recrystallized rough rolling, and special emphasis on the reduction of the final roughing pass prior to the intermediate holding resulting in a fine uniform prior austenite microstructure will be discussed. The optimized cooling process application after finish rolling guarantees the steady control of the final bainitic microstructure with optimum M/A phase for heavy gauge X80 plates. The plates produced by this process achieved good flatness and excellent mechanical properties. SQS has produced 10000 tons 27mm X80 for the Middle Asia C Line Project and 1000 tons 33mm X80 for the 3rd West-to-East Natural Gas Transmission Pipeline Project in 2013-2014. The products utilizing optimized rolling and cooling process showed extremely excellent low temperature toughness.

  3. X-ray attenuation properties of stainless steel (u)

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Wang, Lily L; Berry, Phillip C

    2009-01-01

    Stainless steel vessels are used to enclose solid materials for studying x-ray radiolysis that involves gas release from the materials. Commercially available stainless steel components are easily adapted to form a static or a dynamic condition to monitor the gas evolved from the solid materials during and after the x-ray irradiation. Experimental data published on the x-ray attenuation properties of stainless steel, however, are very scarce, especially over a wide range of x-ray energies. The objective of this work was to obtain experimental data that will be used to determine how a poly-energetic x-ray beam is attenuated by the stainlessmore » steel container wall. The data will also be used in conjunction with MCNP (Monte Carlos Nuclear Particle) modeling to develop an accurate method for determining energy absorbed in known solid samples contained in stainless steel vessels. In this study, experiments to measure the attenuation properties of stainless steel were performed for a range of bremsstrahlung x-ray beams with a maximum energy ranging from 150 keV to 10 MeV. Bremsstrahlung x-ray beams of these energies are commonly used in radiography of engineering and weapon components. The weapon surveillance community has a great interest in understanding how the x-rays in radiography affect short-term and long-term properties of weapon materials.« less

  4. Health safety of main water pipe materials supplied in China market.

    PubMed

    Lu, Kai; Ding, Liang; Wang, Hong-Wei; Jing, Hai-Ning; Zhao, Xiao-Ning; Lin, Shao-Bin; Li, Ya-Dong; Jin, Yin-Long; Liu, Feng-Mao; Jiang, Shu-Ren

    2006-04-01

    To assess the health safety of copper, steel and plastic water pipes by field water quality investigations. Four consumers were randomly selected for each type of water pipes. Two consumers of every type of the water pipes had used the water pipes for more than 1 year and the other 2 consumers had used the water pipes for less than 3 months. The terminal volume of tap water in copper and steel water pipes should be not less than 0.1 liter, whereas that in plastic water pipes should be not less than 1 liter. The mean values of the experimental results in the second field water quality investigation of the copper and steel water pipes met the Sanitary Standards for Drinking Water Quality. The items of water sample of the plastic water pipes met the requirements of the Sanitary Standards for Drinking Water Quality. Copper, steel, and plastic pipes can be used as drinking water pipes.

  5. Response of reinforced concrete and corrugated steel pipes to surface load

    NASA Astrophysics Data System (ADS)

    Lay, Geoff R.

    Full-scale simulated live load tests were conducted in a controlled laboratory setting using a single-axle frame on 600-mm-inner-diameter reinforced concrete pipe (RCP) and corrugated steel pipe (CSP) when buried in dense, well-graded sand and gravel. Measurements of the RCP at nominal and working forces and beyond are reported for 0.3, 0.6 and 0.9 m of soil cover above the pipe crown. The RCP experienced no cracking when buried at 0.3 m under nominal and working CL-625 and CL-800 single-axle design loads. At these loads, the vertical contraction of the pipe diameter was less than 0.08 and 0.10 mm and the largest tensile strains in the pipe were 75 and 100 muepsilon (50-60% of the cracking strain), respectively. A 0.15 (+/-0.05)-mm-wide axial crack developed at the inner crown in the presence of a 6 kNm/m circumferential bending moment (70% of the theoretical ultimate moment capacity) at the fully factored CL-625 load. This crack did not propagate or widen from 3 series of cyclic load-unload tests. At 1300 kN of applied load the change in pipe diameter was less than 3.5 mm. Increasing soil cover from 0.3 to 0.6 to 0.9 m reduced the circumferential crown bending moment from 6.0 to 3.9 to 2.1 kNm/m, respectively, at 400 kN of axle load. A 1.6- and a 2.8-mm-thick CSP were also subjected to axle loading. No yielding or limit states occurred in the 1.6-mm-thick CSP when buried 0.9-m-deep. However, at 0.6 m of cover a 300 kN axle load caused local yielding at the pipe crown. Increasing soil cover from 0.6 to 0.9 m decreased the vertical diameter change from -3.0 to -1.2 mm and the crown bending moment from 0.7 to 0.2 kNm/m (75% and 20% of the yield moment), respectively, at a 250 kN axle load. Deflections of the thicker CSP were less than the thinner pipe below the CL-625 single-axle load, however further increases in applied load produced a greater response in the thicker pipe, likely due to a haunch support issue. Shallow axle loading produced a greater 3-dimensional

  6. Inclusion Characteristics and Acicular Ferrite Nucleation in Ti-Containing Weld Metals of X80 Pipeline Steel

    NASA Astrophysics Data System (ADS)

    Wang, Bingxin; Liu, Xianghua; Wang, Guodong

    2018-06-01

    X80 steel weld metals with Ti contents of 0.003 to 0.13 pct were prepared by the single-pass submerged-arc welding process. The effects of Ti content in weld metals on the constituent phases of inclusions and chemical compositions of the constituent phases, as well as the potency of acicular ferrite (AF) nucleation on the inclusions were investigated. Moreover, the crystallographic orientation relationship between the AF and inclusion was examined. The results show that with an increase in Ti content, the primary constituent phases of the inclusions change from the (Mn-Al-Si-O) compound to a mixture of spinel and pseudobrookite solid solutions, and eventually to pseudobrookite. The spinel solid solution is characterized by the MnTi2O4 constituent. Compared to pseudobrookite, spinel has a lower Ti concentration, but a significantly higher Mn content. In the case of the presence of a considerable amount of spinel, the Mn element is enriched strongly in the inclusions, resulting in the development of a Mn-depleted zone (MDZ) in the matrix around the inclusions, which enhances the driving force for AF formation. AF shows the Baker-Nutting orientation relationship with MnTi2O4. The formation of MDZ and the presence of the Baker-Nutting orientation relationship promote the ability of inclusions to nucleate the intragranular AF.

  7. Inclusion Characteristics and Acicular Ferrite Nucleation in Ti-Containing Weld Metals of X80 Pipeline Steel

    NASA Astrophysics Data System (ADS)

    Wang, Bingxin; Liu, Xianghua; Wang, Guodong

    2018-03-01

    X80 steel weld metals with Ti contents of 0.003 to 0.13 pct were prepared by the single-pass submerged-arc welding process. The effects of Ti content in weld metals on the constituent phases of inclusions and chemical compositions of the constituent phases, as well as the potency of acicular ferrite (AF) nucleation on the inclusions were investigated. Moreover, the crystallographic orientation relationship between the AF and inclusion was examined. The results show that with an increase in Ti content, the primary constituent phases of the inclusions change from the (Mn-Al-Si-O) compound to a mixture of spinel and pseudobrookite solid solutions, and eventually to pseudobrookite. The spinel solid solution is characterized by the MnTi2O4 constituent. Compared to pseudobrookite, spinel has a lower Ti concentration, but a significantly higher Mn content. In the case of the presence of a considerable amount of spinel, the Mn element is enriched strongly in the inclusions, resulting in the development of a Mn-depleted zone (MDZ) in the matrix around the inclusions, which enhances the driving force for AF formation. AF shows the Baker-Nutting orientation relationship with MnTi2O4. The formation of MDZ and the presence of the Baker-Nutting orientation relationship promote the ability of inclusions to nucleate the intragranular AF.

  8. J-R fracture characteristics of ferritic steels for RPVs and RCS piping of nuclear power plants

    NASA Astrophysics Data System (ADS)

    Yoon, Ji-Hyun; Lee, Bong-Sang; Hong, Jun-Hwa

    2001-10-01

    J-R fracture resistance tests have been performed on 3 heats of SA508-Gr.3 nuclear reactor pressure vessel (RPV) steel as well as 2 heats of SA516-Gr.70 and a heat of SA508-Gr.1a steels for nuclear reactor coolant system (RCS) piping. For the latter two steels, dynamic in addition to static J-R fracture resistances were investigated. From the test results of the SA508-Gr.3 steels, the J-R fracture resistance was superior in the following order: Si-killing steel, modified VCD steel and VCD steel. Microstructural analyses were carried out to correlate J-R fracture resistances with microstructural characteristics. According to the test results for SA508-Gr.1a and SA516-Gr.70 steels, all of the tested steels showed steep drops in fracture resistance at certain temperature and loading rate combinations. One heat of SA516-Gr.70 steel was very sensitive to dynamic strain aging and its fracture resistance was significantly low. It was concluded that microstructural and chemical factors affect the J-R fracture and DSA characteristics of SA516-Gr.70 steels.

  9. 77 FR 54926 - Certain Seamless Carbon and Alloy Steel; Standard, Line, and Pressure Pipe From Germany

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-09-06

    ... INTERNATIONAL TRADE COMMISSION [Investigation No. 731-TA-709 (Third Review)] Certain Seamless Carbon and Alloy Steel; Standard, Line, and Pressure Pipe From Germany Determination On the basis of the record \\1\\ developed in the subject five-year review, the United States International Trade Commission...

  10. 77 FR 32531 - Circular Welded Carbon-Quality Steel Pipe From the Sultanate of Oman: Preliminary Determination...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-06-01

    ... antidumping duty investigation on certain steel pipe from India, Oman, the UAE, and Vietnam.\\2\\ The Department... the Socialist Republic of Vietnam: Initiation of Antidumping Duty Investigations, 76 FR 72164... notified all interested parties of its intent to select mandatory respondents for this investigation based...

  11. Nondestructive Technique To Assess Embrittlement In Steels

    NASA Technical Reports Server (NTRS)

    Allison, Sidney G.; Yost, William T.; Cantrell, John H.

    1990-01-01

    Recent research at NASA Langley Research Center led to identification of nondestructive technique for detection of temper embrittlement in HY80 steel. Measures magnetoacoustic emission associated with reversible motion of domain walls at low magnetic fields. Of interest to engineers responsible for reliability and safety of various dynamically loaded and/or thermally cycled steel parts. Applications include testing of landing gears, naval vessels, and parts subjected to heat, such as those found in steam-pipe fittings, boilers, turbine rotors, and nuclear pressure vessels.

  12. 76 FR 5205 - Carbon Steel Butt-Weld Pipe Fittings from Brazil, China, Japan, Taiwan, and Thailand

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-01-28

    ...)] Carbon Steel Butt-Weld Pipe Fittings from Brazil, China, Japan, Taiwan, and Thailand AGENCY: United... Thailand. SUMMARY: The Commission hereby gives notice of the scheduling of expedited reviews pursuant to..., Taiwan, and Thailand would be likely to lead to continuation or recurrence of material injury within a...

  13. 77 FR 19623 - Certain Welded Carbon Steel Standard Pipe from Turkey: Preliminary Results of Countervailing Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-04-02

    ... International Financial Statistics, a publication of the International Monetary Fund (IMF). For Euro-denominated... The Social Security Institution of the GOT administers the incentive for the Employer's Share in... certain welded carbon steel standard pipe from Turkey for the period January 1, 2010, through December 31...

  14. 77 FR 64473 - Circular Welded Carbon-Quality Steel Pipe From the Sultanate of Oman: Final Affirmative...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-10-22

    ...-Quality Steel Pipe From the Sultanate of Oman: Final Affirmative Countervailing Duty Determination AGENCY... Sultanate of Oman (``Oman''). DATES: Effective Date: October 22, 2012. FOR FURTHER INFORMATION CONTACT... Sultanate of Oman (``GSO'') on April 5, April 20, and May 10, 2012. We received the GSO's responses...

  15. New portable pipe wall thickness measuring technique

    NASA Astrophysics Data System (ADS)

    Pascente, Joseph E.

    1998-03-01

    One of the biggest inspection challenges facing many of the process industries; namely the petrochemical, refining, fossil power, and pulp and paper industries is: How to effectively examine their insulated piping? While there are a number of failure mechanisms involved in various process piping systems, piping degradation through corrosion and erosion are by far the most prevalent. This degradation can be in the form of external corrosion under insulation, internal corrosion through a variety of mechanisms, and internal erosion caused by the flow of the product through the pipe. Refineries, chemical plants and electrical power plants have MANY thousands of miles of pipe that are insulated to prevent heat loss or heat absorption. This insulation is often made up of several materials, with calcium based material being the most dense. The insulating material is usually wrapped with an aluminum or stainless steel outer wrap. Verification of wall thickness of these pipes can be accomplished by removing the insulation and doing an ultrasound inspection or by taking x- rays at a tangent to the edge of the pipe through the insulation. Both of these processes are slow and expensive. The time required to obtain data is measured in hours per meter. The ultrasound method requires that the insulation be plugged after the inspection. The surface needs to be cleaned or the resulting data will not be accurate. The tangent x-ray only shows two thicknesses and requires that the area be roped off because of radiation safety.

  16. Neutron Irradiation Effects on the Mechanical Properties of HY-80 Steel

    DTIC Science & Technology

    1986-12-01

    compared to trends established by NRL and by Carpenter (Ref. (18]) ....................... 57 Figure 27 Charpy V-notch ductility characteristics of...59 Figure 28 Charpy V-notch ductility characteristics of three steels of different strength levels after simultaneous irradiations at 550-F...as determined by Charpy V (30 Ft.Lb.) (Ref. [14]) ....... 49 Table 4 Tensile properties of HY-80 steel (Ref. [3,17) .............................. 51

  17. 76 FR 78887 - Circular Welded Carbon Quality Steel Pipe From the People's Republic of China: Rescission of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-12-20

    ... DEPARTMENT OF COMMERCE International Trade Administration [C-570-911] Circular Welded Carbon Quality Steel Pipe From the People's Republic of China: Rescission of Countervailing Duty Administrative Review AGENCY: Import Administration, International Trade Administration, Department of Commerce. DATES: Effective Date: December 20, 2011. FOR...

  18. 75 FR 71672 - Circular Welded Carbon Quality Steel Pipe From the People's Republic of China: Rescission of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-11-24

    ... DEPARTMENT OF COMMERCE International Trade Administration [C-570-911] Circular Welded Carbon Quality Steel Pipe From the People's Republic of China: Rescission of Countervailing Duty Administrative Review AGENCY: Import Administration, International Trade Administration, Department of Commerce. DATES: Effective Date: November 24, 2010. FOR...

  19. 76 FR 77770 - Certain Circular Welded Non-Alloy Steel Pipe From Mexico: Final Results of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-12-14

    ...-Alloy Steel Pipe From Mexico: Final Results of Antidumping Duty Administrative Review AGENCY: Import... Department of Commerce (the Department) published the preliminary results of the administrative review of the...: Preliminary Results of Antidumping Duty Administrative Review, 76 FR 49437 (August 10, 2011) (Preliminary...

  20. 76 FR 71938 - Circular Welded Carbon Steel Pipes and Tubes From Thailand: Extension of Time Limit for...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-11-21

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-549-502] Circular Welded Carbon Steel Pipes and Tubes From Thailand: Extension of Time Limit for Preliminary Results of Antidumping Duty... and tubes from Thailand for the period March 1, 2010, through February 28, 2011. See Initiation of...

  1. 76 FR 49437 - Certain Circular Welded Non-Alloy Steel Pipe From Mexico: Preliminary Results of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-08-10

    ... Non-Alloy Steel Pipe from Brazil, the Republic of Korea (Korea), Mexico, and Venezuela and Amendment... 23954 (May 6, 2003) (Assessment Policy Notice). Because ``as entered'' liquidation instructions do not... assessment'' regulation on May 6, 2003. See Assessment Policy Notice. This clarification will apply to POR...

  2. CAP/WAP-based correlations for estimating the static axial capacity of open-ended steel pipe piles in Alaska.

    DOT National Transportation Integrated Search

    2012-12-01

    CAPWAP analyses of open-ended steel pipe piles at 32 bridge sites in Alaska have been compiled with geotechnical and construction : information for 12- to 48-inch diameter piles embedded in predominantly cohesionless soils to maximum depths of 161-fe...

  3. 76 FR 4633 - Carbon Steel Butt-Weld Pipe Fittings From the People's Republic of China: Notice of Court...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-01-26

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-570-814] Carbon Steel Butt-Weld Pipe..., International Trade Administration, Department of Commerce. SUMMARY: On January 6, 2011, the United States Court of International Trade (``CIT'') sustained the Department of Commerce's (``the Department'') results...

  4. The Effects of an Unexpected Ceramic Coating Phase at the Head of a Pipe on Joining and Postprocessing of a Ceramic-Lined Composite Pipe

    NASA Astrophysics Data System (ADS)

    Mahmoodian, R.; Rahbari, R. G.; Hamdi, M.; Hassan, M. A.; Sparham, Mahdi

    2013-01-01

    Produced ceramic-lined steel pipe using the self-propagating high-temperature synthesis (SHS) method has found uses in many applications. A SHS-centrifugal machine was designed to produce a ceramic-lined steel pipe from ferric oxide and aluminum powder (thermite mixture) under high centrifugal acceleration. The obtained products are expected to be Al2O3 ceramic in the innermost layer and a Fe layer in a region between the outer steel pipes. In the present work, specific regions of a pipe was particularly observed to investigate the stuck (dead) spaces at the pipe head because of its importance in further processes (joining, welding, etc.) which may affect the quality of the next operations. In this article, the product's composition, phase separation, microhardness, and surface finish were studied on three zones of the pipe.

  5. 75 FR 54912 - Drill Pipe and Drill Collars From China

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-09-09

    ...)] Drill Pipe and Drill Collars From China AGENCY: United States International Trade Commission. ACTION... retarded, by reason of subsidized and less-than-fair-value imports from China of drill pipe and drill... defined the subject merchandise as steel drill pipe, and steel drill collars, whether or not conforming to...

  6. 78 FR 72863 - Circular Welded Carbon Quality Steel Pipe From the People's Republic of China: Continuation of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-12-04

    ... Quality Steel Pipe From the People's Republic of China: Continuation of Countervailing Duty Order AGENCY...) from the People's Republic of China (PRC) would likely lead to continuation or recurrence of net... reasonably foreseeable time.\\3\\ \\1\\ See Initiation of Five-Year (``Sunset'') Review, 78 FR 33063 (June 3...

  7. 76 FR 78615 - Circular Welded Carbon-Quality Steel Pipe From India, the Sultanate of Oman, the United Arab...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-12-19

    ...-810] Circular Welded Carbon-Quality Steel Pipe From India, the Sultanate of Oman, the United Arab..., the Sultanate of Oman (``Oman''), The United Arab Emirates (``the UAE''), and the Socialist Republic... Oman, the United Arab Emirates, and the Socialist Republic of Vietnam: Initiation of Countervailing...

  8. 78 FR 34342 - Certain Circular Welded Non-Alloy Steel Pipe From Mexico: Final Results and Partial Rescission of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-06-07

    ... Welded Non-Alloy Steel Pipe from Brazil, the Republic of Korea (Korea), Mexico, and Venezuela and... Proceedings: Assessment of Antidumping Duties, 68 FR 23954 (May 6, 2003) (reseller policy). This clarification... antidumping duties in accordance with the reseller policy. Cash Deposit Requirements The following cash...

  9. 46 CFR 45.133 - Air pipes.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 2 2012-10-01 2012-10-01 false Air pipes. 45.133 Section 45.133 Shipping COAST GUARD....133 Air pipes. (a) Where an air pipe to any tank extends above the freeboard or superstructure deck— (1) The exposed part of the air pipe must be made of steel and of sufficient thickness to avoid...

  10. 46 CFR 45.133 - Air pipes.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 2 2013-10-01 2013-10-01 false Air pipes. 45.133 Section 45.133 Shipping COAST GUARD....133 Air pipes. (a) Where an air pipe to any tank extends above the freeboard or superstructure deck— (1) The exposed part of the air pipe must be made of steel and of sufficient thickness to avoid...

  11. 46 CFR 45.133 - Air pipes.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 2 2014-10-01 2014-10-01 false Air pipes. 45.133 Section 45.133 Shipping COAST GUARD....133 Air pipes. (a) Where an air pipe to any tank extends above the freeboard or superstructure deck— (1) The exposed part of the air pipe must be made of steel and of sufficient thickness to avoid...

  12. 46 CFR 45.133 - Air pipes.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 2 2010-10-01 2010-10-01 false Air pipes. 45.133 Section 45.133 Shipping COAST GUARD....133 Air pipes. (a) Where an air pipe to any tank extends above the freeboard or superstructure deck— (1) The exposed part of the air pipe must be made of steel and of sufficient thickness to avoid...

  13. 46 CFR 45.133 - Air pipes.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 2 2011-10-01 2011-10-01 false Air pipes. 45.133 Section 45.133 Shipping COAST GUARD....133 Air pipes. (a) Where an air pipe to any tank extends above the freeboard or superstructure deck— (1) The exposed part of the air pipe must be made of steel and of sufficient thickness to avoid...

  14. Performance of steel pipe pile-to-concrete bent cap connections subject to seismic or high transverse loading : Phase II

    DOT National Transportation Integrated Search

    2005-02-01

    The response of a concrete filled, steel pipe pile-to-concrete pile cap connection subjected to extreme lateral loads : was experimentally and analytically investigated in this project. This connection is part of a bridge support system : used by the...

  15. Mechanical Characteristics of Submerged Arc Weldment in API Gas Pipeline Steel of Grade X65

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Hashemi, S. H.; Mohammadyani, D.

    The mechanical properties of submerged arc weldment (SAW) in gas transportation pipeline steel of grade API X65 (65 ksi yield strength) were investigated. This steel is produced by thermo mechanical control rolled (TMC), and is largely used in Iran gas piping systems and networks. The results from laboratory study on three different regions; i.e. base metal (BM), fusion zone (FZ) and heat affected zone (HAZ) were used to compare weldment mechanical characteristics with those specified by API 5L (revision 2004) standard code. Different laboratory experiments were conducted on test specimens taken from 48 inch outside diameter and 14.3 mm wallmore » thickness gas pipeline. The test results showed a gradient of microstructure and Vickers hardness data from the centerline of FZ towards the unaffected MB. Similarly, lower Charpy absorbed energy (compared to BM) was observed in the FZ impact specimens. Despite this, the API specifications were fulfilled in three tested zones, ensuring pipeline structural integrity under working conditions.« less

  16. The rotating heat pipe - Implementation as a uniform-temperature heat source

    NASA Astrophysics Data System (ADS)

    Limoges, R. F.

    1981-11-01

    A wickless rotating heat pipe, if properly controlled, is a uniform heat source. The data presented are based on work done with 12.7 cm diameter x 76 cm long rotating heat pipes operating between 120 and 140 C. The major areas reviewed are: materials of fabrication, working fluids, sealing, temperature control, heaters, and safety. The optimum rotating heat pipe defined by these studies is fabricated of type 304 stainless steel, uses water as the working fluid, is sealed with welded joints, and utilizes a pressure switch and a fast-response quartz lamp for temperature control. Surface-temperature control of + or - 0.15 C and temperature uniformity within 0.8 C are obtained. Results of experiments designed to study the effects of hydrogen in the enclosed volume of the heat pipe are presented.

  17. Development of Low-Carbon, Copper-Strengthened HSLA Steel Plate for Naval Ship Construction

    DTIC Science & Technology

    1990-06-01

    steel plate microstructures, 2% nital etch . ...................................................... 13 2. Charpy V-notch impact energy transition for...met a minimum yield strength requirement of 80 ksi yield strength through 3/4 inch gage, had high Charpy V-notch impact energy at low tempera- tures...tempered HSLA line-pipe steels, which typically could not meet the minimum Charpy V-notch impact toughness requirement of 35 ft-lb at -1 200 F. In 1984

  18. Friction Stir Welding of Line-Pipe Steels

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Sanderson, Samuel; Mahoney, Murray; Feng, Zhili

    Friction stir welding (FSW) offers both economic and technical advantages over conventional fusion welding practices for welding line-pipe. For offshore line-pipe construction, the economic savings has been shown to be considerable, approaching a calculated 25%. Offshore pipe is relatively small diameter but heavy wall compared to onshore pipe. One concern is the ability to achieve consistent full weld penetration in an on-site offshore FSW operation, e.g., on a lay-barge. In addition, depending on the size and morphology of the unwelded zone, lack of penetration at the weld root can be difficult if not impossible to detect by conventional NDE methods.more » Thus, an approach to assure consistent full penetration via process control is required for offshore line-pipe construction using FSW. For offshore construction, an internal structural mandrel can be used offering the opportunity to use a sacrificial anvil FSW approach. With this approach, a small volume of sacrificial material can be inserted into the structural anvil. The FSW tool penetrates into the sacrificial anvil, beyond the inner diameter of the pipe wall, thus assuring full penetration. The sacrificial material is subsequently removed from the pipe inner wall. In the work presented herein, FSW studies were completed on both 6 mm and 12 mm wall thickness line-pipe. Lastly, post-FSW evaluations including radiography, root-bend tests, and metallography demonstrated the merits of the sacrificial anvil approach to achieve consistent full penetration.« less

  19. Window type: 2x3 fixed multipaned steel window flanked by 1x3 ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Window type: 2x3 fixed multipaned steel window flanked by 1x3 multipaned steel casements. Concrete sill and spandrel also illustrated. Building 43, facing east - Harbor Hills Housing Project, 26607 Western Avenue, Lomita, Los Angeles County, CA

  20. Manufacture of mold of polymeric composite water pipe reinforced charcoal

    NASA Astrophysics Data System (ADS)

    Zulfikar; Misdawati; Idris, M.; Nasution, F. K.; Harahap, U. N.; Simanjuntak, R. K.; Jufrizal; Pranoto, S.

    2018-03-01

    In general, household wastewater pipelines currently use thermoplastic pipes of Polyvinyl Chloride (PVC). This material is known to be not high heat resistant, contains hazardous chemicals (toxins), relatively inhospitable, and relatively more expensive. Therefore, researchers make innovations utilizing natural materials in the form of wood charcoal as the basic material of making the water pipe. Making this pipe requires a simple mold design that can be worked in the scale of household and intermediate industries. This research aims to produce water pipe mold with simple design, easy to do, and making time relatively short. Some considerations for molding materials are weight of mold, ease of raw material, strong, sturdy, and able to cast. Pipe molds are grouped into 4 (four) main parts, including: outer diameter pipe molding, pipe inside diameter, pipe holder, and pipe alignment control. Some materials have been tested as raw materials for outer diameter of pipes, such as wood, iron / steel, cement, and thermoset. The best results are obtained on thermoset material, where the process of disassembling is easier and the resulting mold weight is relatively lighter. For the inside diameter of the pipe is used stainless steel, because in addition to be resistant to chemical processes that occur, in this part of the mold must hold the press load due to shrinkage of raw materials of the pipe during the process of hardening (polymerization). Therefore, it needs high pressure resistant material and does not blend with the raw material of the pipe. The base of the mold is made of stainless steel material because it must be resistant to corrosion due to chemical processes. As for the adjustment of the pipe is made of ST 37 carbon steel, because its function is only as a regulator of the alignment of the pipe structure.

  1. 76 FR 37320 - Certain Welded Stainless Steel Pipes From the Republic of Korea: Notice of Court Decision Not in...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-06-27

    ... Steel Pipes From the Republic of Korea: Notice of Court Decision Not in Harmony With Final Results of Administrative Review and Amended Final Results AGENCY: Import Administration, International Trade Administration...) sustained the Department of Commerce's (the Department's) results of redetermination as applied to...

  2. Experimental and numerical analysis on aluminum/steel pipe using magnetic pulse welding

    NASA Astrophysics Data System (ADS)

    Shim, J. Y.; Kim, I. S.; Lee, K. J.; Kang, B. Y.

    2011-12-01

    Recently, there has been a trend in the automotive industry to focus on the improvement of lightweight materials, such as aluminum and magnesium because the welding of dissimilar metals causes many welding defects. Magnetic pulse welding (MPW), one of the solid state welding technologies, uses electromagnetic force from current discharged through a working coil which develops a repulsive force between the induced currents flowing parallel and in the opposite direction in the tube to be welded. The objective of this paper is to develop a numerical model for analysis of the interaction between the outer pipe and the working coil using a finite element method (FEM) in the MPW process. Four Maxwell equations are solved using a general electromagnetic mechanics computer program, ANSYS/EMAG code. Experiments were also carried out with a W-MPW60 machine manufactured by WELMATE CO., LTD. with the Al1070 and SM45C for Al pipe and steel bar respectively. The calculated and measured results were compared to verify the proposed model.

  3. Effect of Low-Temperature Environment on Stress Corrosion Cracking Behavior of X80 Pipeline Steel in Simulated Alkaline Soil Solution

    NASA Astrophysics Data System (ADS)

    Xie, Fei; Wang, Dan; Wu, Ming; Yu, Chengxiang; Sun, Dongxu; Yang, Xu; Xu, Changhao

    2018-04-01

    The stress corrosion cracking (SCC) of X80 pipeline steel in simulated alkaline soil solution under different temperatures was investigated by slow-strain-rate testing, scanning electron microscopy and energy-dispersive spectroscopy. Results showed that the fracture was transgranular and brittle at 273 K to 278 K (0 °C to 5 °C), and the metal surface was dissolved by a large number of chloride ions. Furthermore, hydrogen embrittlement was caused by the hydrogen atom extended to the high-stress region. The fracture process was controlled by hydrogen-induced cracking, and SCC was highly sensitive at this stage. At 288 K to 298 K (15 °C to 25 °C), the fracture morphology was attributed to the mixed mode of ductile and brittle fractures, the fracture process was controlled by the mechanism of hydrogen-induced cracking and anodic dissolution, and the susceptibility to SCC decreased. When the temperature reached 308 K to 318 K (35 °C to 45 °C), the fracture was mainly intergranular and ductile, the fracture process was controlled by anodic dissolution, and SCC sensitivity was the smallest in this temperature range.

  4. Microalloyed HSLA (High Strength Low Alloy) Steels: Proceedings of Microalloying 󈨜 Held in Conjunction with the 1988 World Materials Congress, Chicago, Illinois, USA, 24-30 September 1988

    DTIC Science & Technology

    1988-01-01

    steels. The high quality linepipe steels are During the last few years, a large scale conducted. During the last few years, API X52 of efforts has been...with satisfied results. mass production of API X52 steels in production line will be demonstrated. The mass production of line pipe steels in the plate...mill of China Steel Corporation has also been conducted. More than eighty Procedures thousand tons of API X52 has been manufactured during the last 2

  5. Window type: paired 3x2 multipaned steel window flanked by 1x3 ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Window type: paired 3x2 multipaned steel window flanked by 1x3 multipaned steel casements, breaking building corner. Broad overhanging eave also illustrated. Second story detail. Building 13, facing east - Harbor Hills Housing Project, 26607 Western Avenue, Lomita, Los Angeles County, CA

  6. Use of Carbon Steel for Construction of Post-combustion CO 2 Capture Facilities: A Pilot-Scale Corrosion Study

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Li, Wei; Landon, James; Irvin, Bradley

    Corrosion studies were carried out on metal coated and noncoated carbon steel as well as stainless steel in a pilot-scale post-combustion CO 2 capture process. Aqueous 30 wt % monoethanolamine (MEA) solvent was used without any chemical additive for antioxidation to examine a worst-case scenario where corrosion is not mitigated. The corrosion rate of all carbon steels was almost zero in the absorber column and CO 2 lean amine piping except for Ni-coated carbon steel (<1.8 mm/yr). Ni 2Al 3/Al 2O 3 precoated carbon steels showed initial protection but lost their integrity in the stripping column and CO 2 richmore » amine piping, and severe corrosion was eventually observed for all carbon steels at these two locations. Stainless steel was found to be stable and corrosion resistant in all of the sampling locations throughout the experiment. This study provides an initial framework for the use of carbon steel as a potential construction material for process units with relatively mild operating conditions (temperature less than 80 °C), such as the absorber and CO 2 lean amine piping of a post-combustion CO 2 capture process. As a result, it also warrants further investigation of using carbon steel with more effective corrosion mitigation strategies for process units where harsh environments are expected (such as temperatures greater than 100 °C).« less

  7. Use of Carbon Steel for Construction of Post-combustion CO 2 Capture Facilities: A Pilot-Scale Corrosion Study

    DOE PAGES

    Li, Wei; Landon, James; Irvin, Bradley; ...

    2017-04-13

    Corrosion studies were carried out on metal coated and noncoated carbon steel as well as stainless steel in a pilot-scale post-combustion CO 2 capture process. Aqueous 30 wt % monoethanolamine (MEA) solvent was used without any chemical additive for antioxidation to examine a worst-case scenario where corrosion is not mitigated. The corrosion rate of all carbon steels was almost zero in the absorber column and CO 2 lean amine piping except for Ni-coated carbon steel (<1.8 mm/yr). Ni 2Al 3/Al 2O 3 precoated carbon steels showed initial protection but lost their integrity in the stripping column and CO 2 richmore » amine piping, and severe corrosion was eventually observed for all carbon steels at these two locations. Stainless steel was found to be stable and corrosion resistant in all of the sampling locations throughout the experiment. This study provides an initial framework for the use of carbon steel as a potential construction material for process units with relatively mild operating conditions (temperature less than 80 °C), such as the absorber and CO 2 lean amine piping of a post-combustion CO 2 capture process. As a result, it also warrants further investigation of using carbon steel with more effective corrosion mitigation strategies for process units where harsh environments are expected (such as temperatures greater than 100 °C).« less

  8. 76 FR 1971 - Drill Pipe From the People's Republic of China: Final Affirmative Countervailing Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-01-11

    ... Group). Xigang Seamless Steel Tube Co., Ltd. (Xigang) and Wuxi Seamless Pipe Co., Ltd. (WSP) were also.... (SPM), Jiangyin Liangda Drill Pipe Co., Ltd. (Liangda), Jiangyin Sanliang Steel Pipe Trading Co., Ltd... investigation are VAM Drilling USA, Inc., Texas Steel Conversion, Inc., Rotary Drilling Tools, TMK IPSCO, and...

  9. Window type: paired 2x4 multipaned steel windows flanked by 1x4 ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Window type: paired 2x4 multipaned steel windows flanked by 1x4 multipaned steel casements, breaking building corner. Raised panel door front entry also illustrated. Ground floor detail Building 19, facing north - Harbor Hills Housing Project, 26607 Western Avenue, Lomita, Los Angeles County, CA

  10. Corrosion of Spiral Rib Aluminized Pipe

    DOT National Transportation Integrated Search

    2012-08-01

    Large diameter, corrugated steel pipes are a common sight in the culverts that run alongside many Florida roads. Spiral-ribbed aluminized pipe (SRAP) has been widely specified by the Florida Department of Transportation (FDOT) for runoff drainage. Th...

  11. Occurrence of nonylphenol and bisphenol A in household water pipes made of different materials.

    PubMed

    Cheng, Yang-Chen; Chen, Huei-Wen; Chen, Wen-Ling; Chen, Chia-Yang; Wang, Gen-Shuh

    2015-10-01

    We assessed the occurrence of nonylphenol (NP) and bisphenol A (BPA) in tap water supplied through polyvinyl chloride (PVC), stainless steel, and galvanized pipes. Water samples were collected from selected households in Taipei and Kaohsiung (Northern and Southern Taiwan, respectively) in different seasons to elucidate the effects of pipeline materials and ambient temperatures on NP and BPA concentrations in tap water. We detected higher concentrations of NP in tap water from households using PVC pipes (64-195 ng/L) than from those using stainless steel pipes (17-44 ng/L) and galvanized pipes (27-96 ng/L). To verify that water can absorb NP and BPA from PVC pipes, we sealed Milli-Q and tap water in PVC and stainless steel pipes to assess the potential release of NP and BPA from the pipes into the water. Both NP and BPA concentrations initially increased with contact time in the PVC pipes, and the concentration profiles during the retention appeared to be more strongly affected by ambient temperatures. Concentration variations in the stainless steel pipes were smaller than those in the PVC pipes.

  12. Study of the structure and properties of metal of the major steam lines of a CCGT-420 unit made from high-chromium X10CrMoVNb9-1 (P91) steel

    NASA Astrophysics Data System (ADS)

    Grin', E. A.; Anokhov, A. E.; Pchelintsev, A. V.; Krüger, E.-T.

    2016-07-01

    The technology of manufacture of live steam lines and hot reheat lines at FINOW Rohrsysteme GmbH are discussed. These pipelines are designed for high-performance CCGT units and are made from high-chromium martensitic steel X10CrMoVNb9-1 (P91). The principles of certification and evaluation of conformance of thermal and mechanical equipment made from new construction materials with the TRCU 032-2013 technical regulation of the Customs Union are detailed. The requirements outlined in Russian and international regulatory documents regarding the manufacture of pipes and semifinished products for pipeline systems are compared. The characteristic features of high-chromium martensitic steel, which define the requirements for its heat treatment and welding, are outlined. The methodology and the results of a comprehensive analysis of metal of pipes, fittings, and weld joints of steam lines are presented. It is demonstrated that the short-term mechanical properties of metal (P91 steel) of pipes, bends, and weld joints meet the requirements of European standards and Russian technical specifications. The experimental data on long-term strength of metal of pipes from a live steam line virtually match the corresponding reference curve from the European standard, while certain experimental points for metal of bends of this steam line and metal of pipes and bends from a hot reheat line lie below the reference curve, but they definitely stay within the qualifying (20%) interval of the scatter band. The presence of a weakened layer in the heat-affected zone of weld joints of steel P91 is established. It is shown that the properties of this zone govern the short-term and long-term strength of weld joints in general. The results of synthesis and analysis of research data support the notion that the certification testing of steam lines and other equipment made from chromium steels should necessarily involve the determination of long-term strength parameters.

  13. MODEL TESTS AND 3D ELASTIC FINITE ELEMENT ANALYSIS FOR STEEL PIPE PILES WITH WINGS IN STALLED IN SOIL CEMENT COLUMN

    NASA Astrophysics Data System (ADS)

    Tamai, Toshiyuki; Teramoto, Shuntarou; Kimura, Makoto

    Steel pipe piles with wings installed in soil cement column is a composite foundation of pile consisting of soil improvement with cement and steel pipe with wings. This type of pile shows higher vertical bearing capacity when compared to steel pipe piles that are installed without soil cement. It is thought the wings contribute to higher bearing capacity of this type of piles. The wings are also thought to play the role of structural unification of pile foundations and load transfer. In this study, model test and 3D elastic finite element analysis was carried out in order to elucidate the effect of wings on the structural unification of pile foundation and the load transfer mechanism. Firstly, the model test was carried out in order to grasp the influence of pile with and without wings, the shape of wings of the pile and the unconfined compression strength of the soil cement on the structural unification of the pile foundation. The numerical analysis of the model test was then carried out on the intermediate part of the pile foundation with wings and mathematical model developed. Finally load tran sfer mechanism was checked for the entire length of the pile through this mathematical model and the load sharing ratio of the wings and stress distribution occurring in the soil cement clarified. In addition, the effect of the wing interval on the structural unification of the pile foundation and load transfer was also checked and clarified.

  14. Strain limits for concrete filled steel tubes in AASHTO seismic provisions.

    DOT National Transportation Integrated Search

    2013-08-01

    Reinforced concrete filled steel tubes (RCFSTs) are commonly used as bridge pipe piles in high seismic regions. The pipe piles in high : seismic regions. The pipe-piles consist of reinforced concrete encased in a steel tube. The steel tube is used as...

  15. UOE Pipe Numerical Model: Manufacturing Process And Von Mises Residual Stresses Resulted After Each Technological Step

    NASA Astrophysics Data System (ADS)

    Delistoian, Dmitri; Chirchor, Mihael

    2017-12-01

    Fluid transportation from production areas to final customer is effectuated by pipelines. For oil and gas industry, pipeline safety and reliability represents a priority. From this reason, pipe quality guarantee directly influence pipeline designed life, but first of all protects environment. A significant number of longitudinally welded pipes, for onshore/offshore pipelines, are manufactured by UOE method. This method is based on cold forming. In present study, using finite element method is modeled UOE pipe manufacturing process and is obtained von Mises stresses for each step. Numerical simulation is performed for L415 MB (X60) steel plate with 7,9 mm thickness, length 30 mm and width 1250mm, as result it is obtained a DN 400 pipe.

  16. Pipe overpack container for trasuranic waste storage and shipment

    DOEpatents

    Geinitz, Richard R.; Thorp, Donald T.; Rivera, Michael A.

    1999-01-01

    A Pipe Overpack Container for transuranic waste storage and shipment. The system consists of a vented pipe component which is positioned in a vented, insulated 55 gallon steel drum. Both the vented pipe component and the insulated drum are capable of being secured to prevent the contents from leaving the vessel. The vented pipe component is constructed of 1/4 inch stainless steel to provide radiation shielding. Thus, allowing shipment having high Americium-241 content. Several Pipe Overpack Containers are then positioned in a type B, Nuclear Regulatory Commission (NRC) approved, container. In the current embodiment, a TRUPACT-II container was employed and a maximum of fourteen Pipe Overpack Containers were placed in the TRUPACT-II. The combination received NRC approval for the shipment and storage of transuranic waste.

  17. Light as a key driver of freshwater biofouling surface roughness in an experimental hydrocanal pipe rig.

    PubMed

    Ravizza, Matilde; Giosio, Dean; Henderson, Alan; Hovenden, Mark; Hudson, Monica; Salleh, Sazlina; Sargison, Jane; Shaw, Jennifer L; Walker, Jessica; Hallegraeff, Gustaaf

    2016-07-01

    Biofouling in canals and pipelines used for hydroelectric power generation decreases the flow capacity of conduits. A pipeline rig was designed consisting of test sections of varying substrata (PVC, painted steel) and light levels (transparent, frosted, opaque). Stalk-forming diatoms were abundant in both the frosted and transparent PVC pipes but negligible in the painted steel and opaque PVC pipes. Fungi were slightly more abundant in the painted steel pipe but equally present in all the other pipes while bacterial diversity was similar in all pipes. Photosynthetically functional biofouling (mainly diatoms) was able to develop in near darkness. Different biological fouling compositions generated differing friction factors. The highest friction factor was observed in the transparent pipe (densest diatom fouling), the lowest peak friction for the opaque PVC pipe (lowest fouling biomass), and with the painted steel pipe (high fouling biomass, but composed of fungal and bacterial crusts) being intermediate between the opaque and frosted PVC pipes.

  18. 76 FR 8345 - Certain Carbon Steel Butt-Weld Pipe Fittings From Brazil, Japan, Taiwan, Thailand, and the People...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-02-14

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-351-602, A-588-602, A-583-605, A-549-807, A-570-814] Certain Carbon Steel Butt-Weld Pipe Fittings From Brazil, Japan, Taiwan, Thailand, and the People's Republic of China: Final Results of the Expedited Sunset Reviews of the Antidumping Duty Orders Correction In notice document 2011...

  19. 46 CFR 119.455 - Fuel piping.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ..., such as seamless steel pipe or tubing, which provide equivalent safety may be used; (ii) Diesel fuel... bowls of other than steel construction must be approved by the Commandant and be protected from mechanical damage. Approval of bowls of other than steel construction will specify if a flame shield is...

  20. 46 CFR 119.455 - Fuel piping.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ..., such as seamless steel pipe or tubing, which provide equivalent safety may be used; (ii) Diesel fuel... bowls of other than steel construction must be approved by the Commandant and be protected from mechanical damage. Approval of bowls of other than steel construction will specify if a flame shield is...

  1. 46 CFR 119.455 - Fuel piping.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ..., such as seamless steel pipe or tubing, which provide equivalent safety may be used; (ii) Diesel fuel... bowls of other than steel construction must be approved by the Commandant and be protected from mechanical damage. Approval of bowls of other than steel construction will specify if a flame shield is...

  2. 46 CFR 119.455 - Fuel piping.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ..., such as seamless steel pipe or tubing, which provide equivalent safety may be used; (ii) Diesel fuel... bowls of other than steel construction must be approved by the Commandant and be protected from mechanical damage. Approval of bowls of other than steel construction will specify if a flame shield is...

  3. Performance of steel pipe pile-to-concrete bent cap connections subject to seismic or high transverse loading - Phase I : Preliminary investigation

    DOT National Transportation Integrated Search

    1998-06-01

    The response of a concrete filled, steel pipe pile-to-concrete pile cap connection subjected to extreme lateral loads was experimentally and analytically investigated in this project. This connection is part of a bridge support system used by the Mon...

  4. Cryogenic thermal diode heat pipes

    NASA Technical Reports Server (NTRS)

    Alario, J.

    1979-01-01

    The development of spiral artery cryogenic thermal diode heat pipes was continued. Ethane was the working fluid and stainless steel the heat pipe material in all cases. The major tasks included: (1) building a liquid blockage (blocking orifice) thermal diode suitable for the HEPP space flight experiment; (2) building a liquid trap thermal diode engineering model; (3) retesting the original liquid blockage engineering model, and (4) investigating the startup dynamics of artery cryogenic thermal diodes. An experimental investigation was also conducted into the wetting characteristics of ethane/stainless steel systems using a specially constructed chamber that permitted in situ observations.

  5. Pipe overpack container for transuranic waste storage and shipment

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Geinitz, R.R.; Thorp, D.T.; Rivera, M.A.

    1999-12-07

    A Pipe Overpack Container is described for transuranic waste storage and shipment. The system consists of a vented pipe component which is positioned in a vented, insulated 55 gallon steel drum. Both the vented pipe component and the insulated drum are capable of being secured to prevent the contents from leaving the vessel. The vented pipe component is constructed of 1/4 inch stainless steel to provide radiation shielding, thus allowing shipment having high Americium-241 content. Several Pipe Overpack Containers are then positioned in a type B, Nuclear Regulatory Commission (NRC) approved, container. In the current embodiment, a TRUPACT-II container wasmore » employed and a maximum of fourteen Pipe Overpack Containers were placed in the TRUPACT-II. The combination received NRC approval for the shipment and storage of transuranic waste.« less

  6. 77 FR 64478 - Circular Welded Carbon-Quality Steel Pipe From India: Final Determination of Sales at Less Than...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-10-22

    ....D. and 0.165 inch wall thickness (gage 8) 4.000 inch O.D. and 0.148 inch wall thickness (gage 9) 4.000 inch O.D. and 0.165 inch wall thickness (gage 8) 4.500 inch O.D. and 0.203 inch wall thickness... investigation is Zenith Birla (India) Limited (previously known as Zenith Steel Pipes and Industries Ltd...

  7. 76 FR 6762 - Drill Pipe From the People's Republic of China: Amended Final Determination of Critical...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-02-08

    ... the specific chemistry of the steel (i.e., carbon, stainless steel, or other alloy steel), and without... collar green tubes) and unfinished drill pipe (including drill pipe green tubes, which are tubes meeting...

  8. The Development of Boiler Pipes Used for 700°C A-USC-PP in China

    NASA Astrophysics Data System (ADS)

    Liu, Zhengdong; Bao, Hansheng; Xu, Songqian; Wang, Qijiang; Yang, Yujun; Zhang, Peng; Lei, Bingwang

    This paper introduces the progress of boiler pipes used for the manufacturing of 700°C advanced ultra-super-critical (A-USC) fossil fuel power plants (PP) in China, with the emphasis on the detailed advancements of G115 and CN617 pipes, including technical exploration, industrial production and microstructure-property investigation. G115 is a novel ferritic heat resistant steels developed by CISRI, which is an impressive candidate material to make pipes for the temperature up to 650°C. CN617 is a recent modification of Inconel617B and the CN617 pipe with the dimension of Φ 460 × 80 mm was successfully manufactured in China. Some newly available data associated with above materials will be released. G115 and CN617 are imposing candidate materials for the manufacturing of 700°C advanced ultra-super-critical (A-USC) fossil fuel power plants (PP) in China.

  9. Corrosion of Spiral Rib Aluminized Pipe : [Summary

    DOT National Transportation Integrated Search

    2012-01-01

    Large diameter, corrugated steel pipes are a common sight in the culverts that run alongside many Florida roads. Spiral-ribbed aluminized pipe (SRAP) has been widely specified by the Florida Department of Transportation (FDOT) for runoff drainage. Th...

  10. Strain-Based Design Methodology of Large Diameter Grade X80 Linepipe

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Lower, Mark D.

    2014-04-01

    Continuous growth in energy demand is driving oil and natural gas production to areas that are often located far from major markets where the terrain is prone to earthquakes, landslides, and other types of ground motion. Transmission pipelines that cross this type of terrain can experience large longitudinal strains and plastic circumferential elongation as the pipeline experiences alignment changes resulting from differential ground movement. Such displacements can potentially impact pipeline safety by adversely affecting structural capacity and leak tight integrity of the linepipe steel. Planning for new long-distance transmission pipelines usually involves consideration of higher strength linepipe steels because theirmore » use allows pipeline operators to reduce the overall cost of pipeline construction and increase pipeline throughput by increasing the operating pressure. The design trend for new pipelines in areas prone to ground movement has evolved over the last 10 years from a stress-based design approach to a strain-based design (SBD) approach to further realize the cost benefits from using higher strength linepipe steels. This report presents an overview of SBD for pipelines subjected to large longitudinal strain and high internal pressure with emphasis on the tensile strain capacity of high-strength microalloyed linepipe steel. The technical basis for this report involved engineering analysis and examination of the mechanical behavior of Grade X80 linepipe steel in both the longitudinal and circumferential directions. Testing was conducted to assess effects on material processing including as-rolled, expanded, and heat treatment processing intended to simulate coating application. Elastic-plastic and low-cycle fatigue analyses were also performed with varying internal pressures. Proposed SBD models discussed in this report are based on classical plasticity theory and account for material anisotropy, triaxial strain, and microstructural damage effects

  11. 49 CFR Appendix B to Part 192 - Qualification of Pipe

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... specification listed in section I of this appendix: (1) Physical (mechanical) properties of pipe, including...). II. Steel pipe of unknown or unlisted specification. A. Bending Properties. For pipe 2 inches (51... impair the strength or tightness of the pipe. D. Tensile Properties. If the tensile properties of the...

  12. 49 CFR Appendix B to Part 192 - Qualification of Pipe

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... specification listed in section I of this appendix: (1) Physical (mechanical) properties of pipe, including...). II. Steel pipe of unknown or unlisted specification. A. Bending Properties. For pipe 2 inches (51... impair the strength or tightness of the pipe. D. Tensile Properties. If the tensile properties of the...

  13. Crack Resistance of Welded Joints of Pipe Steels of Strength Class K60 of Different Alloying Systems

    NASA Astrophysics Data System (ADS)

    Tabatchikova, T. I.; Tereshchenko, N. A.; Yakovleva, I. L.; Makovetskii, A. N.; Shander, S. V.

    2018-03-01

    The crack resistance of welded joints of pipe steels of strength class K60 and different alloying systems is studied. The parameter of the crack tip opening displacement (CTOD) is shown to be dependent on the size of the austenite grains and on the morphology of bainite in the superheated region of the heat-affected zone of the weld. The crack resistance is shown to be controllable due to optimization of the alloying system.

  14. Simplified pipe gun

    NASA Astrophysics Data System (ADS)

    Sørensen, H.; Nordskov, A.; Sass, B.; Visler, T.

    1987-12-01

    A simplified version of a deuterium pellet gun based on the pipe gun principle is described. The pipe gun is made from a continuous tube of stainless steel and gas is fed in from the muzzle end only. It is indicated that the pellet length is determined by the temperature gradient along the barrel right outside the freezing cell. Velocities of around 1000 m/s with a scatter of ±2% are obtained with a propellant gas pressure of 40 bar.

  15. 46 CFR 45.153 - Through-hull piping: General.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 2 2010-10-01 2010-10-01 false Through-hull piping: General. 45.153 Section 45.153... Conditions of Assignment § 45.153 Through-hull piping: General. (a) All through-hull pipes required by this subpart must be made of steel or material equivalent to the hull in strength and fatigue resistance. (b...

  16. 75 FR 38989 - Welded Large Diameter Line Pipe From Japan: Notice of Rescission of Antidumping Duty...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-07-07

    ... Pipe From Japan: Notice of Rescission of Antidumping Duty Administrative Review AGENCY: Import... antidumping duty order on welded large diameter line pipe from Japan. The review covers 4 producers/exporters of welded large diameter line pipe from Japan, which are, JFE Steel Corporation, Nippon Steel...

  17. 1/50 Scale Model Of The 80x120 Foot Wind Tunnel Model (NFAC) In The Test Section Of The 40x80 Wind Tunnel.

    NASA Image and Video Library

    1996-06-27

    (03/12/1976) 1/50 scale model of the 80x120 foot wind tunnel model (NFAC) in the test section of the 40x80 wind tunnel. Model viewed from the west, mounted on a rotating ground board designed for this test. Ramp leading to ground board includes a generic building placed in front of the 80x120 inlet.

  18. Influence of structure on static cracking resistance and fracture of welded joints of pipe steels of strength class K60

    NASA Astrophysics Data System (ADS)

    Tereshchenko, N. A.; Tabatchikova, T. I.; Yakovleva, I. L.; Makovetskii, A. N.; Shander, S. V.

    2017-07-01

    The static cracking resistance of a number of welded joints made from pipe steels of K60 strength class has been determined. It has been established that the deformation parameter CTOD varies significantly at identical parameters of weldability of steels. The character of fracture has been investigated and the zone of local brittleness of welded joints has been studied. It has been shown that the ability of a metal to resist cracking is determined by the austenite grain size and by the bainite morphology in the region of overheating in the heat-affected zone of a welded joint.

  19. Solar dynamic heat rejection technology. Task 2: Heat pipe radiator development

    NASA Technical Reports Server (NTRS)

    League, Mark; Alario, Joe

    1988-01-01

    This report covers the design, fabrication, and test of several dual slot heat pipe engineering development units. The following dual-slot heat pipes were fabricated and tested: two 6-ft. aluminum heat pipes; a 20-ft. aluminum heat pipe; and a 20-ft. aluminum heat pipe with a four-leg evaporator section. The test results of all four test articles are presented and compared to the performance predicted by the design software. Test results from the four-leg article are incomplete. The methodology for fabricating stainless steel dual slot heat pipes was also studied by performing a tool life test with different single point cutters, and these results are also presented. Although the dual-slot heat pipe has demonstrated the potential to meet the requirements for a high capacity radiator system, uncertainties with the design still exist. The startup difficulties with the aluminum test articles must be solved, and a stainless steel/methanol heat pipe should be built and tested.

  20. Heat pipe manufacturing study

    NASA Technical Reports Server (NTRS)

    Edelstein, F.

    1974-01-01

    Heat pipe manufacturing methods are examined with the goal of establishing cost effective procedures that will ultimately result in cheaper more reliable heat pipes. Those methods which are commonly used by all heat pipe manufacturers have been considered, including: (1) envelope and wick cleaning, (2) end closure and welding, (3) mechanical verification, (4) evacuation and charging, (5) working fluid purity, and (6) charge tube pinch off. The study is limited to moderate temperature aluminum and stainless steel heat pipes with ammonia, Freon-21 and methanol working fluids. Review and evaluation of available manufacturers techniques and procedures together with the results of specific manufacturing oriented tests have yielded a set of recommended cost-effective specifications which can be used by all manufacturers.

  1. DSTO Landmine Detection Test Targets

    DTIC Science & Technology

    2005-06-01

    cm diameter, 10 cm high. x x GS 32D50 Galvanised steel, pipe, hollow, 32 cm diameter, 50 cm long, ends capped x x GS 45D50 Galvanised Steel, pipe...hollow, 45 cm diameter, 50 cm long, ends capped x x GS 75D50 Galvanised Steel, pipe, hollow, 75 cm diameter, 50 cm long, ends capped x x

  2. UOE Pipe Manufacturing Process Simulation: Equipment Designing and Construction

    NASA Astrophysics Data System (ADS)

    Delistoian, Dmitri; Chirchor, Mihael

    2017-12-01

    UOE pipe manufacturing process influence directly on pipeline resilience and operation capacity. At present most spreaded pipe manufacturing method is UOE. This method is based on cold forming. After each technological step appears a certain stress and strain level. For pipe stress strain study is designed and constructed special equipment that simulate entire technological process.UOE pipe equipment is dedicated for manufacturing of longitudinally submerged arc welded DN 400 (16 inch) steel pipe.

  3. Effect of Thermal Shock During Legionella Bacteria Removal on the Corrosion Properties of Zinc-Coated Steel Pipes

    NASA Astrophysics Data System (ADS)

    Orlikowski, Juliusz; Ryl, Jacek; Jazdzewska, Agata; Krakowiak, Stefan

    2016-07-01

    The purpose of this investigation was to conduct the failure analysis of a water-supply system made from zinc-coated steel. The observed corrosion process had an intense and complex character. The brownish deposits and perforations were present after 2-3 years of exploitation. The electrochemical study based on the Tafel polarization, corrosion potential monitoring, and electrochemical impedance spectroscopy together with microscopic analysis via SEM and EDX were performed in order to identify the cause of such intense corrosion. The performed measurements allowed us to determine that thermal shock was the source of polarity-reversal phenomenon. This process had begun the corrosion of steel which later led to the formation of deposits and perforations in the pipes. The work includes appropriate action in order to efficiently identify the described corrosion threat.

  4. Impact of Stainless Steel Exposure on the Oxidation of Polysorbate 80 in Histidine Placebo and Active Monoclonal Antibody Formulation.

    PubMed

    Gopalrathnam, Ganapathy; Sharma, Anant Navanithan; Dodd, Steven Witt; Huang, Lihua

    2018-01-01

    Rapid oxidation of polysorbate 80 in histidine buffer was observed upon brief exposure to stainless steel. Liquid chromatography-mass spectrometry analysis indicates degradation of both polyoxyethylene sorbitan and polyoxyethylene head groups and unsaturated fatty acid chains, with further confirmation by reversed-phase high-performance liquid chromatography data. Both Fe 2+ and Fe 3+ were shown to induce polysorbate 80 oxidation. The degree of oxidation in polysorbate 20 and polysorbate 80 are comparable for the head groups and saturated fatty acid esters. However, the same phenomenon was not observed with placebo or monoclonal antibody at a threshold protein concentration, formulated in sodium citrate, in combination with histidine and sodium citrate, or with Na 2 ethylenediaminetetraacetic acid (EDTA). Further, polysorbate 80 oxidation was not observed with Lilly's antibody containing the active ingredient LY2951742, at or above a threshold concentration. Finally, no major polysorbate 80 degradation was observed in histidine buffer, with or without protein, in containers composed of glass or plastic, or when stainless steel exposure was otherwise completely absent. Finally, the 2-oxo oxidation form of histidine was not observed, but the other oxidation products and modifications of histidine were identified. LAY ABSTRACT: Rapid oxidation of polysorbate 80 in histidine buffer was observed upon brief exposure to stainless steel. The degree of oxidation in polysorbate 80 and polysorbate 20 were comparable. However, the same phenomenon was not observed with placebo when formulated in sodium citrate, in combination with histidine and sodium citrate, or with Na 2 ethylenediaminetetraacetic acid (EDTA). Polysorbate 80 oxidation was not observed with Lilly's antibody containing the active ingredient, LY2951742, at or above a threshold concentration. No major polysorbate 80 degradation in histidine buffer was observed when stainless steel contact was completely absent.

  5. Cryogenic piping material selection for the Component Test Facility (CTF)

    NASA Technical Reports Server (NTRS)

    St. Cyr, William W.

    1991-01-01

    The anticipated high cost of the 8500 psi cryogenic and 15,000 psi gas piping systems used in the CTF at NASA's John C. Stennis Space Center led to the consideration of high-strength materials for these piping systems. Based on years of satisfactory service using austenitic stainless steels in cryogenic applications, particularly for hydrogen service, consideration was limited to the austenitic stainless steels. Attention was focused on alternatives to the 304/304L grades of stainless steel traditionally used in these applications. This paper discusses the various considerations that resulted in the decision to continue using 304/304L for the cryogenic piping and the selection of the nitrogen-strengthened 21Cr-6Ni-9Mn alloy (UNS S21903) for the high-pressure gas systems at the CTF.

  6. Steel Optimization and Substitution for 1980 Oldsmobile Omega X-Body Car.

    DOT National Transportation Integrated Search

    1981-07-01

    This report studies the potential of weight reduction for a 1980 Oldsmobile Omega X-body four-door sedan through steel optimization and substitution of newer steels. The study shows that 74 pounds can be removed from this vehicle using current steel ...

  7. 46 CFR 56.80-5 - Bending.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 2 2010-10-01 2010-10-01 false Bending. 56.80-5 Section 56.80-5 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PIPING SYSTEMS AND APPURTENANCES Bending and Forming § 56.80-5 Bending. Pipe may be bent by any hot or cold method and to any radius which will result...

  8. 46 CFR 56.80-5 - Bending.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 2 2011-10-01 2011-10-01 false Bending. 56.80-5 Section 56.80-5 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PIPING SYSTEMS AND APPURTENANCES Bending and Forming § 56.80-5 Bending. Pipe may be bent by any hot or cold method and to any radius which will result...

  9. Northwest view of steel plate "cans" in bay 7 of ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Northwest view of steel plate "cans" in bay 7 of the main pipe mill building. Historian for scale. - U.S. Steel National Tube Works, Main Pipe Mill Building, Along Monongahela River, McKeesport, Allegheny County, PA

  10. Measurement of defect thickness of the wall thinning defect pipes by lock-in infrared thermography technique

    NASA Astrophysics Data System (ADS)

    Kim, Kyeongsuk; Kim, Kyungsu; Jung, Hyunchul; Chang, Hosub

    2010-03-01

    Mostly piping which is using for the nuclear power plants are made up of carbon steel pipes. The wall thinning defects occurs by the effect of the flow accelerated corrosion of fluid that flows in carbon steel pipes. The defects could be found on the welding part and anywhere in the pipes. The infrared thermography technique which is one of the non-destructive testing method has used for detecting the defects of various kinds of materials over the years. There is a limitation for measuring the defect of metals that have a big coefficient of thermal diffusion. However, a technique using lock-in method gets over the difficulty. Consequently, the lock-in infrared thermography technique has been applied to the various industry fields. In this paper, the defect thickness of the straight pipe which has an artificial defect the inside of the pipes was measured by using the lock-in infrared thermography technique and the result could be utilized in detecting defects of carbon steel pipes.

  11. 46 CFR 38.10-10 - Cargo piping-TB/ALL.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... pressure shall be seamless drawn steel or electric resistance welded steel. Pipe used in refrigerated tank systems shall be of a material which is suitable for the minimum service temperature to which it may be...

  12. 46 CFR 38.10-10 - Cargo piping-TB/ALL.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... pressure shall be seamless drawn steel or electric resistance welded steel. Pipe used in refrigerated tank systems shall be of a material which is suitable for the minimum service temperature to which it may be...

  13. 46 CFR 38.10-10 - Cargo piping-TB/ALL.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... pressure shall be seamless drawn steel or electric resistance welded steel. Pipe used in refrigerated tank systems shall be of a material which is suitable for the minimum service temperature to which it may be...

  14. 46 CFR 38.10-10 - Cargo piping-TB/ALL.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... pressure shall be seamless drawn steel or electric resistance welded steel. Pipe used in refrigerated tank systems shall be of a material which is suitable for the minimum service temperature to which it may be...

  15. Microstructural characterization of pipe bomb fragments

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Gregory, Otto, E-mail: gregory@egr.uri.edu; Oxley, Jimmie; Smith, James

    2010-03-15

    Recovered pipe bomb fragments, exploded under controlled conditions, have been characterized using scanning electron microscopy, optical microscopy and microhardness. Specifically, this paper examines the microstructural changes in plain carbon-steel fragments collected after the controlled explosion of galvanized, schedule 40, continuously welded, steel pipes filled with various smokeless powders. A number of microstructural changes were observed in the recovered pipe fragments: deformation of the soft alpha-ferrite grains, deformation of pearlite colonies, twin formation, bands of distorted pearlite colonies, slip bands, and cross-slip bands. These microstructural changes were correlated with the relative energy of the smokeless powder fillers. The energy of themore » smokeless powder was reflected in a reduction in thickness of the pipe fragments (due to plastic strain prior to fracture) and an increase in microhardness. Moreover, within fragments from a single pipe, there was a radial variation in microhardness, with the microhardness at the outer wall being greater than that at the inner wall. These findings were consistent with the premise that, with the high energy fillers, extensive plastic deformation and wall thinning occurred prior to pipe fracture. Ultimately, the information collected from this investigation will be used to develop a database, where the fragment microstructure and microhardness will be correlated with type of explosive filler and bomb design. Some analyses, specifically wall thinning and microhardness, may aid in field characterization of explosive devices.« less

  16. Detection of surface cracking in steel pipes based on vibration data using a multi-class support vector machine classifier

    NASA Astrophysics Data System (ADS)

    Mustapha, S.; Braytee, A.; Ye, L.

    2017-04-01

    In this study, we focused at the development and verification of a robust framework for surface crack detection in steel pipes using measured vibration responses; with the presence of multiple progressive damage occurring in different locations within the structure. Feature selection, dimensionality reduction, and multi-class support vector machine were established for this purpose. Nine damage cases, at different locations, orientations and length, were introduced into the pipe structure. The pipe was impacted 300 times using an impact hammer, after each damage case, the vibration data were collected using 3 PZT wafers which were installed on the outer surface of the pipe. At first, damage sensitive features were extracted using the frequency response function approach followed by recursive feature elimination for dimensionality reduction. Then, a multi-class support vector machine learning algorithm was employed to train the data and generate a statistical model. Once the model is established, decision values and distances from the hyper-plane were generated for the new collected data using the trained model. This process was repeated on the data collected from each sensor. Overall, using a single sensor for training and testing led to a very high accuracy reaching 98% in the assessment of the 9 damage cases used in this study.

  17. An Overview of Long Duration Sodium Heat Pipe Tests

    NASA Astrophysics Data System (ADS)

    Rosenfeld, John H.; Ernst, Donald M.; Lindemuth, James E.; Sanzi, James L.; Geng, Steven M.; Zuo, Jon

    2004-02-01

    High temperature heat pipes are being evaluated for use in energy conversion applications such as fuel cells, gas turbine re-combustors, and Stirling cycle heat sources; with the resurgence of space nuclear power, additional applications include reactor heat removal elements and radiator elements. Long operating life and reliable performance are critical requirements for these applications. Accordingly long-term materials compatibility is being evaluated through the use of high temperature life test heat pipes. Thermacore, Inc. has carried out several sodium heat pipe life tests to establish long term operating reliability. Four sodium heat pipes have recently demonstrated favorable materials compatibility and heat transport characteristics at high operating temperatures in air over long time periods. A 316L stainless steel heat pipe with a sintered porous nickel wick structure and an integral brazed cartridge heater has successfully operated at 650C to 700C for over 115,000 hours without signs of failure. A second 316L stainless steel heat pipe with a specially-designed Inconel 601 rupture disk and a sintered nickel powder wick has demonstrated over 83,000 hours at 600C to 650C with similar success. A representative one-tenth segment Stirling Space Power Converter heat pipe with an Inconel 718 envelope and a stainless steel screen wick has operated for over 41,000 hours at nearly 700C. A hybrid (i.e. gas-fired and solar) heat pipe with a Haynes 230 envelope and a sintered porous nickel wick structure was operated for about 20,000 hours at nearly 700C without signs of degradation. These life test results collectively have demonstrated the potential for high temperature heat pipes to serve as reliable energy conversion system components for power applications that require long operating lifetime with high reliability. Detailed design specifications, operating history, and test results are described for each of these sodium heat pipes. Lessons learned and future life

  18. An Overview of Long Duration Sodium Heat Pipe Tests

    NASA Technical Reports Server (NTRS)

    Rosenfeld, John H.; Ernst, Donald M.; Lindemuth, James E.; Sanzi, James L.; Geng, Steven M.; Zuo, Jon

    2004-01-01

    High temperature heat pipes are being evaluated for use in energy conversion applications such as fuel cells, gas turbine re-combustors, and Stirling cycle heat sources; with the resurgence of space nuclear power, additional applications include reactor heat removal elements and radiator elements. Long operating life and reliable performance are critical requirements for these applications. Accordingly long-term materials compatibility is being evaluated through the use of high temperature life test heat pipes. Thermacore International, Inc., has carried out several sodium heat pipe life tests to establish long term operating reliability. Four sodium heat pipes have recently demonstrated favorable materials compatibility and heat transport characteristics at high operating temperatures in air over long time periods. A 3l6L stainless steel heat pipe with a sintered porous nickel wick structure and an integral brazed cartridge heater has successfully operated at 650 to 700 C for over 115,000 hours without signs of failure. A second 3l6L stainless steel heat pipe with a specially-designed Inconel 60 I rupture disk and a sintered nickel powder wick has demonstrated over 83,000 hours at 600 to 650 C with similar success. A representative one-tenth segment Stirling Space Power Converter heat pipe with an Inconel 718 envelope and a stainless steel screen wick has operated for over 41 ,000 hours at nearly 700 0c. A hybrid (i.e. gas-fired and solar) heat pipe with a Haynes 230 envelope and a sintered porous nickel wick structure was operated for about 20,000 hours at nearly 700 C without signs of degradation. These life test results collectively have demonstrated the potential for high temperature heat pipes to serve as reliable energy conversion system components for power applications that require long operating lifetime with high reliability, Detailed design specifications, operating hi story, and test results are described for each of these sodium heat pipes. Lessons

  19. Flexible ocean upwelling pipe

    DOEpatents

    Person, Abraham

    1980-01-01

    In an ocean thermal energy conversion facility, a cold water riser pipe is releasably supported at its upper end by the hull of the floating facility. The pipe is substantially vertical and has its lower end far below the hull above the ocean floor. The pipe is defined essentially entirely of a material which has a modulus of elasticity substantially less than that of steel, e.g., high density polyethylene, so that the pipe is flexible and compliant to rather than resistant to applied bending moments. The position of the lower end of the pipe relative to the hull is stabilized by a weight suspended below the lower end of the pipe on a flexible line. The pipe, apart from the weight, is positively buoyant. If support of the upper end of the pipe is released, the pipe sinks to the ocean floor, but is not damaged as the length of the line between the pipe and the weight is sufficient to allow the buoyant pipe to come to a stop within the line length after the weight contacts the ocean floor, and thereafter to float submerged above the ocean floor while moored to the ocean floor by the weight. The upper end of the pipe, while supported by the hull, communicates to a sump in the hull in which the water level is maintained below the ambient water level. The sump volume is sufficient to keep the pipe full during heaving of the hull, thereby preventing collapse of the pipe.

  20. Modification of the Structure of Low-Carbon Pipe Steel by Helical Rolling, and the Increase in Its Strength and Cold Resistance

    NASA Astrophysics Data System (ADS)

    Derevyagina, L. S.; Gordienko, A. I.; Pochivalov, Yu. I.; Smirnova, A. S.

    2018-01-01

    The paper reports the investigation results on the microstructure and mechanical properties of low-carbon pipe steel after helical rolling. The processing of the steel leads to the refinement of ferritic grains from 12 (for the coarse-grained state) to 5 μm, to the strengthening of ferrite by carbide particles, a decrease in the total fraction of perlite grains, a more uniform alternation of ferrite and perlite, and the formation of regions with bainitic structure. The mechanical properties of the steel have been determined in the conditions of static and dynamic loading in the range of test temperatures from +20 to-70°C. As a result of processing, the ultimate tensile strength increases (from 650 to 770 MPa at a rolling temperature from 920°C) and the viscoplastic properties at negative temperatures are improved significantly. The ductile-brittle transition temperature of the rolled steel decreases from-32 to-55°C and the impact toughness at the test temperature-40°C increases eight times compared to the initial state of the steel.

  1. 6. VIEW OF SHOWING DOWNSTREAM OUTLET PIPE AND COLLAR (12' ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    6. VIEW OF SHOWING DOWNSTREAM OUTLET PIPE AND COLLAR (12' DIAMETER CORRUGATED STEEL PIPE ENCASED IN 6' CONCRETE), LOOKING NORTH - High Mountain Dams in Bonneville Unit, Island Lake Dam, Wasatch National Forest, Kamas, Summit County, UT

  2. 34. THESE INGOT MOLDS OF STEEL 32' X 83' ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    34. THESE INGOT MOLDS OF STEEL - 32' X 83' IN SIZE - ARE READY TO BE TAKEN TO THE STRIPPER, WHERE THE MOLDS WILL BE REMOVED. INGOTS WILL NEXT BE PLACED INTO A 'SOAKING PIT,' WHERE THEY ARE HEATED TO A UNIFORM TEMPERATURE PRIOR TO ROLLING. - Corrigan, McKinney Steel Company, 3100 East Forty-fifth Street, Cleveland, Cuyahoga County, OH

  3. Characterization of Anisotropic Behavior for High Grade Pipes

    NASA Astrophysics Data System (ADS)

    Yang, Kun; Huo, Chunyong; Ji, Lingkang; Li, Yang; Zhang, Jiming; Ma, Qiurong

    With the developing requirement of nature gas, the property needs of steel for pipe line are higher and higher, especially in strength and toughness. It is necessary to improve the steel grade in order to ensure economic demand and safety. However, with the rise of steel grade, the differences on properties in different orientations (anisotropic behaviors) become more and more obvious after the process of hot rolling, which may affect the prediction of fracture for the pipes seriously (Thinking of isotropic mechanical properties for material in traditional predict way). In order to get the reason for anisotropic mechanics, a series of tests are carried out for high grade steel pipes, including not only mechanical properties but also microstructures. Result indicates that there are obviously anisotropic behaviors for high grade steel pipes in two orientations (rolling orientation and transverse orientation). Strength is better in T orientation because Rm is higher and Rt 0.5 rises more in T orientation, and toughness is better in L orientation because of the higher Akv and SA in L orientation under a same temperature. Banded structures are formed in T orientation, and the spatial distribution of inclusion and precipitated phases are different in T, L and S orientation. The anisotropic arrangement for the matrix in space (banded structures), which is formed after the process of hot rolling, may affect the mechanical properties in different orientation. Moreover, the elasticity modulus of particles is different from the elasticity modulus of matrix, deformation between particles and matrix may cause stress concentration, and damage forms in this place. Because of the different distribution of particles in space, the level of damage is anisotropic in different orientations, and the anisotropic mechanical properties occur finally. Therefore, the anisotropic mechanical properties are determined by the anisotropic microstructures, both the anisotropic of matrix and the

  4. Thermo-Mechanical Analysis of a Single-Pass Weld Overlay and Girth Welding in Lined Pipe

    NASA Astrophysics Data System (ADS)

    Obeid, Obeid; Alfano, Giulio; Bahai, Hamid

    2017-08-01

    The paper presents a nonlinear heat-transfer and mechanical finite-element (FE) analyses of a two-pass welding process of two segments of lined pipe made of a SUS304 stainless steel liner and a C-Mn steel pipe. The two passes consist of the single-pass overlay welding (inner lap weld) of the liner with the C-Mn steel pipe for each segment and the single-pass girth welding (outer butt weld) of the two segments. A distributed power density of the moving welding torch and a nonlinear heat-transfer coefficient accounting for both radiation and convection have been used in the analysis and implemented in user subroutines for the FE code ABAQUS. The modeling procedure has been validated against previously published experimental results for stainless steel and carbon steel welding separately. The model has been then used to determine the isotherms induced by the weld overlay and the girth welding and to clarify their influence on the transient temperature field and residual stress in the lined pipe. Furthermore, the influence of the cooling time between weld overlay and girth welding and of the welding speed have been examined thermally and mechanically as they are key factors that can affect the quality of lined pipe welding.

  5. Flow accelerated corrosion of carbon steel feeder pipes from pressurized heavy water reactors

    NASA Astrophysics Data System (ADS)

    Singh, J. L.; Kumar, Umesh; Kumawat, N.; Kumar, Sunil; Kain, Vivekanand; Anantharaman, S.; Sinha, A. K.

    2012-10-01

    Detailed investigation of a number of feeder pipes received from Rajasthan Atomic Power Station Unit 2 (RAPS#2) after en-masse feeder pipe replacement after 15.67 Effective Full Power Years (EFPYs) was carried out. Investigations included ultrasonic thickness measurement by ultrasonic testing, optical microscopy, scanning electron microscopy, chemical analysis and X-ray Diffraction (XRD). Results showed that maximum thickness reduction of the feeder had occurred downstream and close to the weld in 32 NB (1.25″/32.75 mm ID) elbows. Rate of Flow Accelerated Corrosion (FAC) was measured to be higher in the lower diameter feeder pipes due to high flow velocity and turbulence. Weld regions had thinned to a lower extent than the parent material due to higher chromium content in the weld. A weld protrusion has been shown to add to the thinning due to FAC and lead to faster thinning rate at localized regions. Surface morphology of inner surface of feeder had shown different size scallop pattern over the weld and parent material. Inter-granular cracks were also observed along the weld fusion line and in the parent material in 32 NB outlet feeder elbow.

  6. Fabrication and development of several heat pipe honeycomb sandwich panel concepts. [airframe integrated scramjet engine

    NASA Technical Reports Server (NTRS)

    Tanzer, H. J.

    1982-01-01

    The feasibility of fabricating and processing liquid metal heat pipes in a low mass honeycomb sandwich panel configuration for application on the NASA Langley airframe-integrated Scramjet engine was investigated. A variety of honeycomb panel facesheet and core-ribbon wick concepts was evaluated within constraints dictated by existing manufacturing technology and equipment. The chosen design consists of an all-stainless steel structure, sintered screen facesheets, and two types of core-ribbon; a diffusion bonded wire mesh and a foil-screen composite. Cleaning, fluid charging, processing, and process port sealing techniques were established. The liquid metals potassium, sodium and cesium were used as working fluids. Eleven honeycomb panels 15.24 cm X 15.24 cm X 2.94 cm were delivered to NASA Langley for extensive performance testing and evaluation; nine panels were processed as heat pipes, and two panels were left unprocessed.

  7. Comparison of carbon footprints of steel versus concrete pipelines for water transmission.

    PubMed

    Chilana, Lalit; Bhatt, Arpita H; Najafi, Mohammad; Sattler, Melanie

    2016-05-01

    The global demand for water transmission and service pipelines is expected to more than double between 2012 and 2022. This study compared the carbon footprint of the two most common materials used for large-diameter water transmission pipelines, steel pipe (SP) and prestressed concrete cylinder pipe (PCCP). A planned water transmission pipeline in Texas was used as a case study. Four life-cycle phases for each material were considered: material production and pipeline fabrication, pipe transportation to the job site, pipe installation in the trench, and operation of the pipeline. In each phase, the energy consumed and the CO2-equivalent emissions were quantified. It was found that pipe manufacturing consumed a large amount of energy, and thus contributed more than 90% of life cycle carbon emissions for both kinds of pipe. Steel pipe had 64% larger CO2-eq emissions from manufacturing compared to PCCP. For the transportation phase, PCCP consumed more fuel due to its heavy weight, and therefore had larger CO2-eq emissions. Fuel consumption by construction equipment for installation of pipe was found to be similar for steel pipe and PCCP. Overall, steel had a 32% larger footprint due to greater energy used during manufacturing. This study compared the carbon footprint of two large-diameter water transmission pipeline materials, steel and prestressed concrete cylinder, considering four life-cycle phases for each. The study provides information that project managers can incorporate into their decision-making process concerning pipeline materials. It also provides information concerning the most important phases of the pipeline life cycle to target for emission reductions.

  8. Assessment of Ductile-to-Brittle Transition Behavior of Localized Microstructural Regions in a Friction-Stir Welded X80 Pipeline Steel with Miniaturized Charpy V-Notch Testing

    NASA Astrophysics Data System (ADS)

    Avila, Julian A.; Lucon, Enrico; Sowards, Jeffrey; Mei, Paulo Roberto; Ramirez, Antonio J.

    2016-06-01

    Friction-stir welding (FSW) is an alternative welding process for pipelines. This technology offers sound welds, good repeatability, and excellent mechanical properties. However, it is of paramount importance to determine the toughness of the welds at low temperatures in order to establish the limits of this technology. Ductile-to-brittle transition curves were generated in the present study by using a small-scale instrumented Charpy machine and miniaturized V-notch specimens (Kleinstprobe, KLST); notches were located in base metal, heat-affected, stirred, and hard zones within a FSW joint of API-5L X80 Pipeline Steel. Specimens were tested at temperatures between 77 K (-196 °C) and 298 K (25 °C). Based on the results obtained, the transition temperatures for the base material and heat-affected zone were below 173 K (-100 °C); conversely, for the stirred and hard zones, it was located around 213 K (-60 °C). Fracture surfaces were characterized and showed a ductile fracture mechanism at high impact energies and a mixture of ductile and brittle mechanisms at low impact energies.

  9. [Study on pipe material's influence on chlorine dioxide drinking water disinfection].

    PubMed

    He, Tao; Yue, Yinling; Ling, Bo; Zhang, Lan

    2010-09-01

    To study the pipe material's influence on chlorine dioxide drinking water disinfection. 0.8 mg/L chlorine dioxide solution was injected into 5 kinds of pipes respectively, PPR, PVC-U, Steel with Zinc coating, copper and PE pipes. Dipped free from light for 48 hours and the concentrations of chlorine dioxide, chlorite and chlorate were tested from samples taken from each kind of pipe at 1, 2, 3, 4, 5, 6, 12, 24 and 48 hours respectively. Chlorine dioxides decay rates in the water dipping the pipes increase as the dipping time increases and the decay of chlorine dioxide mainly occurs within 6 hours after the dipping. But for different pipe, the influence of decay differs. The consumption of chlorine dioxide of the metal pipes is more than that of the plastic pipes. And with 2 hours after the dipping experiment begins, the concentrations of the chlorite of the copper pipe and of the steel with zinc coating pipe increase quickly and reach the maximum concentration. But then the chlorite concentration decreases greatly. After dipped 24 hours, the chlorite in the water in the pipe can not be detected. For other plastic piples, all the chlorite concentrations in the dipping water increase as the dipping time increase. Compared with the start of the dipping experiment, the chlorate concentration in the dipping water of each pipe has no obvious change. The material of the water transportation pipe does have influence on chlorine dioxide drinking water disinfection.

  10. View looking east in the main pipe mill building at ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    View looking east in the main pipe mill building at the operators pulpit of the east-west reelers, no. 2 seamless line. - U.S. Steel National Tube Works, Main Pipe Mill Building, Along Monongahela River, McKeesport, Allegheny County, PA

  11. 49 CFR 192.55 - Steel pipe.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... in a hoop stress of less than 6,000 p.s.i. (41 MPa) where no close coiling or close bending is to be done, if visual examination indicates that the pipe is in good condition and that it is free of split...

  12. 49 CFR 192.55 - Steel pipe.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... in a hoop stress of less than 6,000 p.s.i. (41 MPa) where no close coiling or close bending is to be done, if visual examination indicates that the pipe is in good condition and that it is free of split...

  13. 49 CFR 192.55 - Steel pipe.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... in a hoop stress of less than 6,000 p.s.i. (41 MPa) where no close coiling or close bending is to be done, if visual examination indicates that the pipe is in good condition and that it is free of split...

  14. 49 CFR 192.55 - Steel pipe.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... in a hoop stress of less than 6,000 p.s.i. (41 MPa) where no close coiling or close bending is to be done, if visual examination indicates that the pipe is in good condition and that it is free of split...

  15. Hydrogen assisted cracking and CO2 corrosion behaviors of low-alloy steel with high strength used for armor layer of flexible pipe

    NASA Astrophysics Data System (ADS)

    Liu, Zhenguang; Gao, Xiuhua; Du, Linxiu; Li, Jianping; Zhou, Xiaowei; Wang, Xiaonan; Wang, Yuxin; Liu, Chuan; Xu, Guoxiang; Misra, R. D. K.

    2018-05-01

    In this study, hydrogen induced cracking (HIC), sulfide stress corrosion cracking (SSCC) and hydrogen embrittlement (HE) were carried out to study hydrogen assisted cracking behavior (HIC, SSCC and HE) of high strength pipeline steel used for armor layer of flexible pipe in ocean. The CO2 corrosion behavior of designed steel with high strength was studied by using immersion experiment. The experimental results demonstrate that the corrosion resistance of designed steel with tempered martensite to HIC, SSCC and HE is excellent according to specific standards, which contributes to the low concentration of dislocation and vacancies previously formed in cold rolling process. The corrosion mechanism of hydrogen induced cracking of designed steel, which involves in producing process, microstructure and cracking behavior, is proposed. The designed steel with tempered martensite shows excellent corrosion resistance to CO2 corrosion. Cr-rich compound was first formed on the coupon surface exposed to CO2-saturated brine condition and chlorine, one of the corrosion ions in solution, was rich in the inner layer of corrosion products.

  16. Evaluation of commercially-available spacecraft-type heat pipes

    NASA Technical Reports Server (NTRS)

    Kaufman, W. B.; Tower, L. K.

    1978-01-01

    As part of an effort to develop reliable, cost effective spacecraft thermal control heat pipes, life tests on 30 commercially available heat pipes in 10 groups of different design and material combinations were conducted. Results for seven groups were reported herein. Materials are aluminum and stainless steel, and working fluids are methanol and ammonia. The formation of noncondensible gas was observed for times exceeding 11,000 hours. The heat transport capacities of the pipes were also determined.

  17. Beam loss reduction by magnetic shielding using beam pipes and bellows of soft magnetic materials

    NASA Astrophysics Data System (ADS)

    Kamiya, J.; Ogiwara, N.; Hotchi, H.; Hayashi, N.; Kinsho, M.

    2014-11-01

    One of the main sources of beam loss in high power accelerators is unwanted stray magnetic fields from magnets near the beam line, which can distort the beam orbit. The most effective way to shield such magnetic fields is to perfectly surround the beam region without any gaps with a soft magnetic high permeability material. This leads to the manufacture of vacuum chambers (beam pipes and bellows) with soft magnetic materials. A Ni-Fe alloy (permalloy) was selected for the material of the pipe parts and outer bellows parts, while a ferritic stainless steel was selected for the flanges. An austenitic stainless steel, which is non-magnetic material, was used for the inner bellows for vacuum tightness. To achieve good magnetic shielding and vacuum performances, a heat treatment under high vacuum was applied during the manufacturing process of the vacuum chambers. Using this heat treatment, the ratio of the integrated magnetic flux density along the beam orbit between the inside and outside of the beam pipe and bellows became small enough to suppress beam orbit distortion. The outgassing rate of the materials with this heat treatment was reduced by one order magnitude compared to that without heat treatment. By installing the beam pipes and bellows of soft magnetic materials as part of the Japan Proton Accelerator Research Complex 3 GeV rapid cycling synchrotron beam line, the closed orbit distortion (COD) was reduced by more than 80%. In addition, a 95.5% beam survival ratio was achieved by this COD improvement.

  18. Guided Wave Sensing In a Carbon Steel Pipe Using a Laser Vibrometer System

    NASA Astrophysics Data System (ADS)

    Ruíz Toledo, Abelardo; Salazar Soler, Jordi; Chávez Domínguez, Juan Antonio; García Hernández, Miguel Jesús; Turó Peroy, Antoni

    2010-05-01

    Non-Destructive Evaluation (NDE) techniques have achieved a great development during the last decades as a valuable tool for material characterization, manufacturing control and structural integrity tests. Among these tools, the guided wave technology has been rapidly extended because it reduces inspection time and costs compared to the ordinary point by point testing in large structures, as well as because of the possibility of inspecting under insulation and coating conditions. This fast development has motivated the creation of several inspection and material characterization systems including different technologies which can be combined with this technique. Different measurements systems based on laser techniques have been presented in order to inspect pipes, plates and diverse structures. Many of them are experimental systems of high cost and complexity which combine the employment of a laser for generation of waves in the structure and an interferometer for detection. Some of them employ air-coupled ultrasound generation transducers, with high losses in air and which demand high energy for exciting waves in materials of high stiffness. The combined employment of a commercial vibrometer system for Lamb wave sensing in plates has been successfully shown in the literature. In this paper we present a measurement system based on the combined employment of a piezoelectric wedge transducer and a laser vibrometer to sense guided acoustic waves in carbon steel pipes. The measurement system here presented is mainly compounded of an angular wedge transducer, employed to generate the guided wave and a commercial laser vibrometer used in the detection process. The wedge transducer is excited by means of a signal function generator whose output signal has been amplified with a power signal amplifier. A high precision positioning system is employed to place the laser beam at different points through the pipe surface. The signal detected by the laser vibrometer system is

  19. Autogenous Metallic Pipe Leak Repair in Potable Water Systems.

    PubMed

    Tang, Min; Triantafyllidou, Simoni; Edwards, Marc A

    2015-07-21

    Copper and iron pipes have a remarkable capability for autogenous repair (self-repair) of leaks in potable water systems. Field studies revealed exemplars that metallic pipe leaks caused by nails, rocks, and erosion corrosion autogenously repaired, as confirmed in the laboratory experiments. This work demonstrated that 100% (N = 26) of 150 μm leaks contacting representative bulk potable water in copper pipes sealed autogenously via formation of corrosion precipitates at 20-40 psi, pH 3.0-11.0, and with upward and downward leak orientations. Similar leaks in carbon steel pipes at 20 psi self-repaired at pH 5.5 and 8.5, but two leaks did not self-repair permanently at pH 11.0 suggesting that water chemistry may control the durability of materials that seal the leaks and therefore the permanence of repair. Larger 400 μm holes in copper pipes had much lower (0-33%) success of self-repair at pH 3.0-11.0, whereas all 400 μm holes in carbon steel pipes at 20 psi self-repaired at pH 4.0-11.0. Pressure tests indicated that some of the repairs created at 20-40 psi ambient pressure could withstand more than 100 psi without failure. Autogenous repair has implications for understanding patterns of pipe failures, extending the lifetime of decaying infrastructure, and developing new plumbing materials.

  20. 49 CFR 179.400-17 - Inner tank piping.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... vapor space of the inner tank to facilitate unloading the liquid lading must be approved. [Amdt. 179-32... Liquid Tank Car Tanks and Seamless Steel Tanks (Classes DOT-113 and 107A) § 179.400-17 Inner tank piping. (a) Product lines. The piping system for vapor and liquid phase transfer and venting must be made for...

  1. 49 CFR 179.400-17 - Inner tank piping.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... vapor space of the inner tank to facilitate unloading the liquid lading must be approved. [Amdt. 179-32... Liquid Tank Car Tanks and Seamless Steel Tanks (Classes DOT-113 and 107A) § 179.400-17 Inner tank piping. (a) Product lines. The piping system for vapor and liquid phase transfer and venting must be made for...

  2. 49 CFR 179.400-17 - Inner tank piping.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... vapor space of the inner tank to facilitate unloading the liquid lading must be approved. [Amdt. 179-32... Liquid Tank Car Tanks and Seamless Steel Tanks (Classes DOT-113 and 107A) § 179.400-17 Inner tank piping. (a) Product lines. The piping system for vapor and liquid phase transfer and venting must be made for...

  3. Design characteristics of a heat pipe test chamber

    NASA Technical Reports Server (NTRS)

    Baker, Karl W.; Jang, J. Hoon; Yu, Juin S.

    1992-01-01

    LeRC has designed a heat pipe test facility which will be used to provide data for validating heat pipe computer codes. A heat pipe test chamber that uses helium gas for enhancing heat transfer was investigated. The conceptual design employs the technique of guarded heating and guarded cooling to facilitate accurate measurements of heat transfer rates to the evaporator and from the condenser. The design parameters are selected for a baseline heat pipe made of stainless steel with an inner diameter of 38.10 mm and a wall thickness of 1.016 mm. The heat pipe operates at a design temperature of 1000 K with an evaporator radial heat flux of 53 W/sq. cm.

  4. Effects of phosphate addition on biofilm bacterial communities and water quality in annular reactors equipped with stainless steel and ductile cast iron pipes.

    PubMed

    Jang, Hyun-Jung; Choi, Young-June; Ro, Hee-Myong; Ka, Jong-Ok

    2012-02-01

    The impact of orthophosphate addition on biofilm formation and water quality was studied in corrosion-resistant stainless steel (STS) pipe and corrosion-susceptible ductile cast iron (DCI) pipe using cultivation and culture-independent approaches. Sample coupons of DCI pipe and STS pipe were installed in annular reactors, which were operated for 9 months under hydraulic conditions similar to a domestic plumbing system. Addition of 5 mg/L of phosphate to the plumbing systems, under low residual chlorine conditions, promoted a more significant growth of biofilm and led to a greater rate reduction of disinfection by-products in DCI pipe than in STS pipe. While the level of THMs (trihalomethanes) increased under conditions of low biofilm concentration, the levels of HAAs (halo acetic acids) and CH (chloral hydrate) decreased in all cases in proportion to the amount of biofilm. It was also observed that chloroform, the main species of THM, was not readily decomposed biologically and decomposition was not proportional to the biofilm concentration; however, it was easily biodegraded after the addition of phosphate. Analysis of the 16S rDNA sequences of 102 biofilm isolates revealed that Proteobacteria (50%) was the most frequently detected phylum, followed by Firmicutes (10%) and Actinobacteria (2%), with 37% of the bacteria unclassified. Bradyrhizobium was the dominant genus on corroded DCI pipe, while Sphingomonas was predominant on non-corroded STS pipe. Methylobacterium and Afipia were detected only in the reactor without added phosphate. PCR-DGGE analysis showed that the diversity of species in biofilm tended to increase when phosphate was added regardless of the pipe material, indicating that phosphate addition upset the biological stability in the plumbing systems.

  5. Repair of Corrosion in Air Supply Piping at the NASA Glenn Research Center's 1 by 1 Foot Supersonic Wind Tunnel

    NASA Technical Reports Server (NTRS)

    Henry, Michael

    2000-01-01

    During a test at the NASA Glenn Research Center's 1 x 1 Supersonic Wing Tunnel, it was discovered that particles entrained in the air flow were damaging the pressure sensitive paint on a test article. An investigation found the source of the entrained particles to be rust on the internal surfaces of the air supply piping. To remedy the situation, the air supply line components made from carbon steel were either refurbished or replaced with new stainless steel components. The refurbishment process included various combinations of chemical cleaning, bead blasting, painting and plating.

  6. Effect of the Initial State of a Steel 38KhN3MFA Billet on the Microstructure and the Mechanical Properties of Seamless Pipes

    NASA Astrophysics Data System (ADS)

    Vorob'ev, R. A.; Dubinskii, V. N.; Sorokina, S. A.

    2017-11-01

    The effect of the initial structure of 38KhN3MFA steel on the mechanical properties of heattreated seamless pipes is studied. It is found that satisfactory macrostructure, strength, and plastic characteristics are insufficient to achieve the required set of service properties of the end product in the presence of a structural heterogeneity in tubular billets. A banded structure can cause a substantial scatter of the mechanical properties of the end product and a decrease in the impact toughness of the steel. It is shown that, in the presence of a banded structure, the required mechanical properties of the end product made of 38KhN3MFA steel can be achieved by correcting the final heat treatment conditions.

  7. Polarization effects associated with thermal processing of HY-80 structural steel using high-power laser diode array

    NASA Astrophysics Data System (ADS)

    Wu, Sheldon S. Q.; Baker, Bradford W.; Rotter, Mark D.; Rubenchik, Alexander M.; Wiechec, Maxwell E.; Brown, Zachary M.; Beach, Raymond J.; Matthews, Manyalibo J.

    2017-12-01

    Localized heating of roughened steel surfaces using highly divergent laser light emitted from high-power laser diode arrays was experimentally demonstrated and compared with theoretical predictions. Polarization dependence was analyzed using Fresnel coefficients to understand the laser-induced temperature rise of HY-80 steel plates under 383- to 612-W laser irradiation. Laser-induced, transient temperature distributions were directly measured using bulk thermocouple probes and thermal imaging. Finite-element analysis yielded quantitative assessment of energy deposition and heat transport in HY-80 steel using absorptivity as a tuning parameter. The extracted absorptivity values ranged from 0.62 to 0.75 for S-polarized and 0.63 to 0.85 for P-polarized light, in agreement with partially oxidized iron surfaces. Microstructural analysis using electron backscatter diffraction revealed a heat affected zone for the highest temperature conditions (612 W, P-polarized) as evidence of rapid quenching and an austenite to martensite transformation. The efficient use of diode arrays for laser-assisted advanced manufacturing technologies, such as hybrid friction stir welding, is discussed.

  8. Evolution of weld metal microstructure in shielded metal arc welding of X70 HSLA steel with cellulosic electrodes: A case study

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Ghomashchi, Reza, E-mail: reza.ghomashchi@adelaide.edu.au; Costin, Walter; Kurji, Rahim

    2015-09-15

    The microstructure of weld joint in X70 line pipe steel resulted from shielded metal arc welding with E6010 cellulosic electrodes is characterized using optical and electron microscopy. A range of ferritic morphologies have been identified ranging from polygonal inter- and intra-prior austenite grains allotriomorphic, idiomorphic ferrites to Widmanstätten, acicular and bainitic ferrites. Electron Backscatter Diffraction (EBSD) analysis using Image Quality (IQ) and Inverse Pole Figure (IPF) maps through superimposition of IQ and IPF maps and measurement of percentages of high and low angle grain boundaries was identified to assist in differentiation of acicular ferrite from Widmanstätten and bainitic ferrite morphologies.more » In addition two types of pearlitic structures were identified. There was no martensite detected in this weld structure. The morphology, size and chemistry of non-metallic inclusions are also discussed briefly. - Highlights: • Application of EBSD reveals orientation relationships in a range of phases for shielded metal arc welding of HSLA steel. • Nucleation sites of various ferrite morphologies identified • Formation of upper and lower bainite and their morphologies.« less

  9. 46 CFR 56.80-10 - Forming (reproduces 129.2).

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 2 2010-10-01 2010-10-01 false Forming (reproduces 129.2). 56.80-10 Section 56.80-10 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PIPING SYSTEMS AND APPURTENANCES Bending and Forming § 56.80-10 Forming (reproduces 129.2). (a) Piping components may be formed...

  10. 46 CFR 56.80-10 - Forming (reproduces 129.2).

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 2 2011-10-01 2011-10-01 false Forming (reproduces 129.2). 56.80-10 Section 56.80-10 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PIPING SYSTEMS AND APPURTENANCES Bending and Forming § 56.80-10 Forming (reproduces 129.2). (a) Piping components may be formed...

  11. Tests on a pilot plant for reheating desulfurized flue gases with the help of heat pipes

    NASA Astrophysics Data System (ADS)

    Schug, W.

    1982-02-01

    Desulfurized flue gases were reheated with a heat pipe heat exchanger. Finned heat pipes, with a coating or made of high quality steel were subjected to different operating conditions for 1000 hr. The coating proved to be unsuitable for heat transfer because it swells and detaches itself from the background material. The high quality steels showed pitting and surface corrosion. The possibilities of cleaning were also studied to prevent deposits forming on the heat pipes, but no solution was found.

  12. Heat pipe radiator technology for space power systems

    NASA Technical Reports Server (NTRS)

    Carlson, A. W.; Gustafson, E.; Ercegovic, B. A.

    1986-01-01

    High-reliability high-performance deployable monogroove and dual-slot heat pipe radiator systems to meet the requirements for electric power in future space missions, such as the 300-kW(e) electric powder demand projected for NASA's Space Station, are discussed. Analytical model trade studies of various configurations show the advantages of the dual-slot heat pipe radiator for high temperature applications as well as its weight reduction potential over the 50-350 F temperature range. The ammonia-aluminum monogroove heat pipe, limited to below-180 F operating temperatures, is under development, and can employ methanol-stainless steel heat pipes to achieve operating temperatures in excess of 300 F. Dual-slot heat pipe configuration proof-of-concept testing was begun in 1985.

  13. High temperature thermal energy storage in steel and sand

    NASA Technical Reports Server (NTRS)

    Turner, R. H.

    1979-01-01

    The technical and economic potential for high temperature (343 C, 650 F) thermal energy storage in hollow steel ingots, pipes embedded in concrete, and for pipes buried in sand was evaluated. Because it was determined that concrete would separate from pipes due to thermal stresses, concrete was replaced by sand, which is free from thermal stresses. Variations of the steel ingot concept were not cost effective compared to the sand-pipe approach, therefore, the sand-pipe thermal storage unit (TSU) was evaluated in depth to assess the approximate tube spacing requirements consistent with different system performance characteristics and also attendant system costs. For large TSUs which do not require fast response times, the sand-pipe approach offers attractive possibilities. A pipe diameter about 9 cm (3.5 in) and pipe spacing of approximately 25 cm (10 in), with sand filling the interspaces, appears appropriate. Such a TSU system designed for 8 hours charge/discharge cycle has an energy unit storage cost (CE) of $2.63/kWhr-t and a power unit storage cost (Cp) of $42/kW-t (in 1977 dollars).

  14. Study of Mechanical Properties and Characterization of Pipe Steel welded by Hybrid (Friction Stir Weld + Root Arc Weld) Approach

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Lim, Yong Chae; Sanderson, Samuel; Mahoney, Murray

    Friction stir welding (FSW) has recently attracted attention as an alternative construction process for gas/oil transportation applications due to advantages compared to fusion welding techniques. A significant advantage is the ability of FSW to weld the entire or nearly the entire wall thickness in a single pass, while fusion welding requires multiple passes. However, when FSW is applied to a pipe or tube geometry, an internal back support anvil is required to resist the plunging forces exerted during FSW. Unfortunately, it may not be convenient or economical to use internal backing support due to limited access for some applications. Tomore » overcome this issue, ExxonMobil recently developed a new concept, combining root arc welding and FSW. That is, a root arc weld is made prior to FSW that supports the normal loads associated with FSW. In the present work, mechanical properties of a FSW + root arc welded pipe steel are reported including microstructure and microhardness.« less

  15. DRAFT One Year Extension of the Short-Term National Product Waiver for Stainless Steel Nuts and Bolts used in Pipe Couplings, Restraints, Joints, Flanges and Saddles for State Revolving Fund Projects

    EPA Pesticide Factsheets

    DRAFT one year extension of the short-term national product waiver for stainless steel nuts and bolts used in pipe couplings, restraints, joints, flanges and saddles for State Revolving Fund projects.

  16. Experimental investigations on sodium-filled heat pipes

    NASA Technical Reports Server (NTRS)

    Dorner, S.; Reiss, F.; Schretzmann, K.

    1977-01-01

    The possibilities of producing heat pipes and, especially, the necessary capillary structures are discussed. Several types of heat pipes were made from stainless steel and tested at temperatures between 400 and 1055 deg C. The thermal power was determined by a calorimeter. Results indicate: bubble-free evaporation of sodium from rectangular open chennels is possible with a heat flux of more than 1,940 W/sq cm at 1055 C. The temperature drop along the tube could be measured only at low temperatures. A subdivided heat pipe worked against the gravitational field. A heat pipe with a capillary structure made of a rolled screen was supported by rings and bars operated at 250 W/sq cm heat flux in the evaporating region.

  17. Effect of preliminary thermal treatment on decomposition kinetics of austenite in low-alloyed pipe steel in intercritical temperature interval

    NASA Astrophysics Data System (ADS)

    Makovetskii, A. N.; Tabatchikova, T. I.; Yakovleva, I. L.; Tereshchenko, N. A.; Mirzaev, D. A.

    2013-06-01

    The decomposition kinetics of austenite that appears in the 13KhFA low-alloyed pipe steel upon heating the samples in an intercritical temperature interval (ICI) and exposure for 5 or 30 min has been studied by the method of high-speed dilatometry. The results of dilatometry are supplemented by the microstructure analysis. Thermokinetic diagrams of the decomposition of the γ phase are represented. The conclusion has been drawn that an increase in the duration of exposure in the intercritical interval leads to a significant increase in the stability of the γ phase.

  18. 76 FR 11757 - Drill Pipe From the People's Republic of China: Antidumping Duty Order

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-03-03

    ... are finished drill pipe and drill collars without regard to the specific chemistry of the steel (i.e... included are unfinished drill collars (including all drill collar green tubes) and unfinished drill pipe (including drill pipe green tubes, which are tubes meeting the following description: seamless tubes with an...

  19. Study on pipe deflection by using numerical method

    NASA Astrophysics Data System (ADS)

    Husaini; Zaki Mubarak, Amir; Agustiar, Rizki

    2018-05-01

    Piping systems are widely used in a refinery or oil and gas industry. The piping system must be properly designed to avoid failure or leakage. Pipe stress analysis is conducted to analyze the loads and critical stress occurred, so that the failure of the pipe can be avoided. In this research, it is analyzed the deflection of a pipe by using Finite Element Method. The pipe is made of A358 / 304SS SCH10S Stainless Steel. It is 16 inches in size with the distance between supports is 10 meters. The fluid flown is Liquid Natural Gas (LNG) with the range of temperature of -120 ° C to -170 ° C, and a density of 461.1 kg / m 3. The flow of LNG causes deflection of the pipe. The pipe deflection must be within the permissible tolerable range. The objective is to analyze the deflection occurred in the piping system. Based on the calculation and simulation, the deflection is 4.4983 mm, which is below the maximum limit of deflection allowed, which is 20.3 mm.

  20. Smart manufacturing of complex shaped pipe components

    NASA Astrophysics Data System (ADS)

    Salchak, Y. A.; Kotelnikov, A. A.; Sednev, D. A.; Borikov, V. N.

    2018-03-01

    Manufacturing industry is constantly improving. Nowadays the most relevant trend is widespread automation and optimization of the production process. This paper represents a novel approach for smart manufacturing of steel pipe valves. The system includes two main parts: mechanical treatment and quality assurance units. Mechanical treatment is performed by application of the milling machine with implementation of computerized numerical control, whilst the quality assurance unit contains three testing modules for different tasks, such as X-ray testing, optical scanning and ultrasound testing modules. The advances of each of them provide reliable results that contain information about any failures of the technological process, any deviations of geometrical parameters of the valves. The system also allows detecting defects on the surface or in the inner structure of the component.

  1. 1/50 Scale Model Of The 80X120 Foot Wind Tunnel Model (NFAC) In The Test Section Of The 40X80 Wind Tunnel At Nasa Ames.

    NASA Image and Video Library

    1976-03-12

    (03/12/1976) Overhead view of 1/50 scale model of the 80x120 foot wind tunnel model (NFAC) in the test section of the 40x80 wind tunnel at NASA Ames. Model mounted on a rotating ground board designed for this test.

  2. The Collection of Ice in Jet A-1 Fuel Pipes

    NASA Astrophysics Data System (ADS)

    Maloney, Thomas C.

    ® and there was a lack of a preferential accumulation region downstream of a pipe bend. A greater heat transfer from the pipe increased ice accumulation for aluminum that was made rough with 80 grit sand paper, and for Teflon®. Water was shown to collect in the pipe system as the number of tests increased and the freeze temperature of either the hard or soft ice was about 0 °C. Finally, results of "stage I" tests showed that stainless steel pipe welds were a preferred sight for ice to accumulate. Repeatability was done first in stage II and the normalized pressure increase for two 3/42 un-insulated pipe tests were within 7%. Normalized pressure increase across a pipe was shown to increase as Reynolds number decreased. A 50% increase in Reynolds number led to a 40% decrease in characteristic normalized pressure increase (CNPI). Tests were done at three temperatures and ice accumulated the most at -11 °C. The CNPI at -11 °C was about three times greater than the CNPI at -7.4 °C and about sixty times greater than the CNPI at -19.4 C. A greater heat transfer from the fuel pipe increased ice accumulation. For the amount of time that the tests ran, the total normalized pressure increase was about .9 greater for an un-insulated pipe than for an insulated pipe. Contamination in the fuel increased the amount of soft ice that collected in the system. The CNPI for the more contaminated fuel was more than double the case with less contaminated fuel. Possible solutions for the prevention or decrease of ice accumulation in aircraft fuel systems based on the results of this study are insulated pipes, a change in the type of pipe material, a higher fuel flow rate and cleaner fuel. The fuel temperature could also be altered to avoid temperatures where the most ice accumulates.

  3. Construction of the 40x80 Foot Wind Tunnel at Ames.

    NASA Image and Video Library

    1943-07-07

    Looking South from inside the diffuser of the 40x80 foot wind tunnel at NACA's Ames Research Center. Construction began in late 1941, the mammoth construction task sorely taxing the resources of the new center. Two and a half years later, in dune 1944, the 40 x 80-foot full-scale tunnel went into operation.

  4. 75 FR 49891 - Drill Pipe from the People's Republic of China: Notice of Preliminary Affirmative Determination...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-08-16

    ... non-API specifications, whether finished or unfinished (including green tubes suitable for drill pipe), without regard to the specific chemistry of the steel (i.e., carbon, stainless steel, or other alloy steel...

  5. Latest Development and Application of Nb-Bearing High Strength Pipeline Steels

    NASA Astrophysics Data System (ADS)

    Zhang, Yongqing; Shang, Chengjia; Guo, Aimin; Zheng, Lei; Niu, Tao; Han, Xiulin

    In order to solve the pollution problem emerging in China recently, China's central government is making great efforts to raise the percentage of natural gas consumption in the China's primary energy mix, which needs to construct big pipelines to transport natural gas from the nation's resource-rich western regions to the energy-starved east, as well as import from the Central Asia and Russia. With this mainstream trend, high strength, high toughness, heavy gauge, and large diameter pipeline steels are needed to improve the transportation efficiency. This paper describes the latest progresses in Nb-bearing high strength pipeline steels with regard to metallurgical design, development and application, including X80 coil with a thickness up to 22.0mm, X80 plate with a diameter as much as 1422mm, X80 plate with low-temperature requirements and low-Mn sour service X65 for harsh sour service environments. Moreover, based on widely accepted TMCP and HTP practices with low carbon and Nb micro-alloying design, this paper also investigated some new metallurgical phenomena based on powerful rolling mills and heavy ACC equipment.

  6. Cold Test and Performance Evaluation of Prototype Cryoline-X

    NASA Astrophysics Data System (ADS)

    Shah, N.; Choukekar, K.; Kapoor, H.; Muralidhara, S.; Garg, A.; Kumar, U.; Jadon, M.; Dash, B.; Bhattachrya, R.; Badgujar, S.; Billot, V.; Bravais, P.; Cadeau, P.

    2017-12-01

    The multi-process pipe vacuum jacketed cryolines for the ITER project are probably world’s most complex cryolines in terms of layout, load cases, quality, safety and regulatory requirements. As a risk mitigation plan, design, manufacturing and testing of prototype cryoline (PTCL) was planned before the approval of final design of ITER cryolines. The 29 meter long PTCL consist of 6 process pipes encased by thermal shield inside Outer Vacuum Jacket of DN 600 size and carries cold helium at 4.5 K and 80 K. The global heat load limit was defined as 1.2 W/m at 4.5 K and 4.5 W/m at 80 K. The PTCL-X (PTCL for Group-X cryolines) was specified in detail by ITER-India and designed as well as manufactured by Air Liquide. PTCL-X was installed and tested at cryogenic temperature at ITER-India Cryogenic Laboratory in 2016. The heat load at 4.5 K and 80 K, estimated using enthalpy difference method, was found to be approximately 0.8 W/m at 4.5 K, 4.2 W/m at 80 K, which is well within the defined limits. Thermal shield temperature profile was also found to be satisfactory. Paper summarizes the cold test results of PTCL-X

  7. Heat pipe wick with structural enhancement

    DOEpatents

    Andraka, Charles E.; Adkins, Douglas R.; Moreno, James B.; Rawlinson, K. Scott; Showalter, Steven K.; Moss, Timothy A.

    2003-11-18

    Heat pipe wick structure wherein a stout sheet of perforated material overlays a high performance wick material such as stainless steel felt affixed to a substrate. The inventive structure provides a good flow path for working fluid while maintaining durability and structural stability independent of the structure (or lack of structure) associated with the wick material. In one described embodiment, a wick of randomly laid .about.8 micron thickness stainless steel fibers is sintered to a metal substrate and a perforated metal overlay.

  8. Analysis of High-Power Diode Laser Heating Effects on HY-80 Steel for Laser Assisted Friction Stir Welding Applications

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Wiechec, Maxwell; Baker, Brad; McNelley, Terry

    In this research, several conditions of high power diode laser heated HY-80 steel were characterized to determine the viability of using such lasers as a preheating source before friction stir welding in order to reduce frictional forces thereby reducing tool wear and increasing welding speeds. Differences in microstructures within heat affected zones were identified at specific laser powers and traverse speeds. Vickers hardness values were recorded and analyzed to validate the formation of additional martensite in diode laser heated regions of HY-80 steel. Conditions that produced little to no additional martensite were identified and relationships among high power diode lasermore » power, traverse speed, and martensite formation were determined. The development of heat affected zones, change in grain structure, and creation of additional martensite in HY-80 can be prevented through the optimization of laser amperage and transverse speed.« less

  9. The resistance of high frequency inductive welded pipe to grooving corrosion in salt water

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Duran, C.; Triess, E.; Herbsleb, G.

    1986-09-01

    When exposed to neutral, salt-containing waters, electric resistant welded pipe in carbon and low alloy steels with increased sulfur contents may suffer preferential corrosion attack in the weld area. Because of its appearance, this type of corrosion is called grooving corrosion. The susceptibility to grooving corrosion may be determined and quantitatively described by means of an accelerated potentiostatic exposure test. The importance of type, concentration, and temperature of the electrolytic solution; potential; test duration; and the sulfur content of the steel in the accelerated corrosion test and the susceptibility of steels to grooving corrosion are described. Line pipe in highmore » frequency inductive (HFI) welded carbon and low alloy steels are resistant to grooving corrosion particularly because of their low sulfur content.« less

  10. Flexible metallic ultrasonic transducers for structural health monitoring of pipes at high temperatures.

    PubMed

    Shih, Jeanne-Louise; Kobayashi, Makiko; Jen, Cheng-Kuei

    2010-09-01

    Piezoelectric films have been deposited by a sol-gel spray technique onto 75-μm-thick titanium and stainless steel (SS) membranes and have been fabricated into flexible ultrasonic transducers (FUTs). FUTs using titanium membranes were glued and those using SS membranes brazed onto steel pipes, procedures that serve as on-site installation techniques for the purpose of offering continuous thickness monitoring capabilities at up to 490 °C. At 150 °C, the thickness measurement accuracy of a pipe with an outer diameter of 26.6 mm and a wall thickness of 2.5 mm was estimated to be 26 μm and the center frequency of the FUT was 10.8 MHz. It is demonstrated that the frequency bandwidth of the FUTs and SNR of signals using glue or brazing materials as high-temperature couplant for FUTs are sufficient to inspect the steel pipes even with a 2.5 mm wall thickness.

  11. 37. REDUCTION PLANT DRYER Stainless steel screen cylinder, encased ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    37. REDUCTION PLANT - DRYER Stainless steel screen cylinder, encased within an outer steel shell (top half missing). As fish were tumbled by the rotating screen, they were cooked and dried by live steam piped into the dryer through overhead pipes. The dryer is mounted on a slight angle, aiding the process by moving the drying fish towards the exhaust end of the dryer. - Hovden Cannery, 886 Cannery Row, Monterey, Monterey County, CA

  12. Speed of Sound in Metal Pipes: An Inexpensive Lab

    ERIC Educational Resources Information Center

    Huggins, Elisha

    2008-01-01

    Our favorite demonstration for sound waves is to set up a compressional pulse on a horizontally stretched Slinky[TM]. One can easily watch the pulse move back and forth at a speed of the order of one meter per second. Watching this demonstration, it occurred to us that the same thing might happen in a steel pipe if you hit the end of the pipe with…

  13. High Temperature Properties Test and Research of 9Cr1Mo (P9) Seamless Pipe Used in Petrochemical Industry

    NASA Astrophysics Data System (ADS)

    Wang, Qijiang; Zhou, Yedong; Zhang, Qinglian

    Production technical process of BaoSteel-produced 9Cr1Mo (P9) seamless pipe is presented, and creep property of isothermal annealed state of that steel is studied under the temperatures of 550 °C, 600 °C, 650 °C, 700 °C. Also, isothermal extrapolation method and Larson-Miller method are employed to extrapolate creep rupture strength of the steel at the creep time of 20000h, 40000h, 60000h and 100000h. The results show that high temperature properties of BaoSteel-produced 9Cr1Mo (P9) seamless pipe meets the API 530 standard of USA and the SH/T3037 standard of China's petrochemical industry, and the steel can be used in large scale petroleum cracking equipment. Meantime, the comparison of creep properties at 650 °C and transient elevated temperature properties at different temperatures between isothermal annealed state and normalized + tempered state of 9Cr1Mo (P9) seamless pipe as well as the microstructure analysis show that the normalized + tempered 9Cr1Mo (P9) seamless pipe presents better high temperature properties.

  14. 77 FR 10722 - Drill Pipe From the People's Republic of China: Termination of Anti-Circumvention Inquiry

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-02-23

    ... response to a request from VAM Drilling U.S.A., Texas Steel Conversion Inc. and Rotary Drilling Tools... products covered by the orders are steel drill pipe, and steel drill collars, whether or not conforming to... drill collars without regard to the specific chemistry of the steel (i.e., carbon, stainless steel, or...

  15. Study of fatigue behavior of longitudinal welded pipes

    NASA Astrophysics Data System (ADS)

    Simion, P.; Dia, V.; Istrate, B.; Hrituleac, G.; Hrituleac, I.; Munteanu, C.

    2016-08-01

    During transport and storage of the various fluids, welded pipes are subjected to cyclic loading due to pressure fluctuations that often exceed the prescribed values for normal operation. These cyclic loading can significantly reduce the life of the pipes; as a result the design should be based on the fatigue strength not only on static resistance. In general the fatigue strength of pipes is dependent by strength, pipe geometry and surface quality. In case of the electric longitudinal welded pipes, the fatigue strength is significantly limited by concentration of residual stress and the size of existing defects in the weld seam. This paper presents the fatigue behaviour of the electric welded pipes by high frequency, under conditions that simulate real operating conditions pipes. Fatigue testing was performed on welded pipes made of micro alloyed carbon steels. Some of these pipes were previously subjected to a heat treatment of normalization, in order to also determine the influence of heat treatment on the fatigue strength of welded pipes. To determine and correlate the different factors affecting the fatigue strength, welded pipes were also subjected to various tests: tensile tests, impact tests, measurement of micro hardness, microstructural analysis by optical microscopy and scanning electron microscopy.

  16. 46 CFR 56.50-65 - Burner fuel-oil service systems.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... service systems. (a) All discharge piping from the fuel oil service pumps to burners must be seamless steel with a thickness of at least Schedule 80. If required by § 56.07-10(e) of this part or paragraph... than Schedule 80. Short lengths of steel, or annealed copper nickel, nickel copper, or copper pipe and...

  17. 46 CFR 56.50-65 - Burner fuel-oil service systems.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... service systems. (a) All discharge piping from the fuel oil service pumps to burners must be seamless steel with a thickness of at least Schedule 80. If required by § 56.07-10(e) of this part or paragraph... than Schedule 80. Short lengths of steel, or annealed copper nickel, nickel copper, or copper pipe and...

  18. 46 CFR 56.50-65 - Burner fuel-oil service systems.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... service systems. (a) All discharge piping from the fuel oil service pumps to burners must be seamless steel with a thickness of at least Schedule 80. If required by § 56.07-10(e) of this part or paragraph... than Schedule 80. Short lengths of steel, or annealed copper nickel, nickel copper, or copper pipe and...

  19. 46 CFR 56.50-65 - Burner fuel-oil service systems.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... service systems. (a) All discharge piping from the fuel oil service pumps to burners must be seamless steel with a thickness of at least Schedule 80. If required by § 56.07-10(e) of this part or paragraph... than Schedule 80. Short lengths of steel, or annealed copper nickel, nickel copper, or copper pipe and...

  20. 46 CFR 56.50-65 - Burner fuel-oil service systems.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... service systems. (a) All discharge piping from the fuel oil service pumps to burners must be seamless steel with a thickness of at least Schedule 80. If required by § 56.07-10(e) of this part or paragraph... than Schedule 80. Short lengths of steel, or annealed copper nickel, nickel copper, or copper pipe and...

  1. A simple heat-pipe cell for X-ray absorption spectrometry of potassium vapor

    NASA Astrophysics Data System (ADS)

    Pres̆eren, R.; Kodre, A.; Arc̆on, I.; Padez̆nik Gomils̆ek, J.; Hribar, M.

    1999-01-01

    The construction and operation of a simple high-temperature X-ray absorption cell for potassium vapor is described. The principle of "spectroscopic heat pipe" is exploited to separate kapton windows, indispensable for good transmission in the low-energy region, from the hot and aggressive vapor. High-resolution spectrum of the K-edge region of atomic potassium reveals fingerprints of multielectron photoexcitations.

  2. An X-ray investigation of the unusual supernova remnant CTB 80

    NASA Technical Reports Server (NTRS)

    Wang, Z. R.; Seward, F. D.

    1984-01-01

    The X-ray properties of SNR CTB 80 (G68.8 + 2.8) are discussed based on both low- and high-resolution images from the Einstein satellite. The X-ray maps show a point source coinciding with the region of maximum radio emission. Diffuse X-ray emission is evident mainly along the radio lobe extending about 8 arcmin east of the point source and aligned with the projected magnetic field lines. The observed X-ray luminosity is 3.2 x 10 to the 34th ergs/s with 1.0 x 10 to the 3th ergs/s from the point source (assuming a distance of 3 kpc). There is also faint, diffuse, X-ray emission south of the point source, where radio emission is absent. The unusual radio and X-ray morphologies are interpreted as a result of relativistic jets energized by the central object, and the possible association of CTB 80 with SN 1408 as recorded by Chinese observers is discussed.

  3. A76-0634. 1/50 Scale Model Of The 80X120 Foot Wind Tunnel Model (Nfac) In The Test Section Of The 40X80 Foot Wind Tunnel.

    NASA Image and Video Library

    1996-06-27

    (03/12/1976) 1/50 scale model of the 80x120 foot wind tunnel model (NFAC) in the test section of the 40x80 foot wind tunnel. Model mounted on a rotating ground board designed for this test, viewed from the west, oriented for North wind.

  4. xPIPE--Reception of DICOM Data from any Sender via the Internet.

    PubMed

    Czwoydzinski, J; Eßeling, R; Meier, N; Heindel, W; Lenzen, H

    2015-05-01

    Various technologies have been established for DICOM data exchange in radiology. In addition to the patient CD, online transfers via VPN (virtual private network) or DICOM email are common practice. However, dedicated network solutions are generally not appropriate for data exchange with occasional and spontaneous partners due to missing infrastructure at the partner institutions and/or complex setup procedures. The purpose was to develop a practical solution to complement the established technologies to allow users worldwide to transfer images without registration. The development of the xPIPE system is based on Java and various software libraries. A client hosted on a website enables sending DICOM data to a receiving system of the hospital. The new xPIPE system creates a gateway to a receiving hospital which is accessible from any point worldwide, giving other hospitals, clinics and patients a simple and secure method to transmit DICOM data without intermediate storage on external servers. The system was deployed at the University Hospital Münster and subsequently widely used even without information events and training. Data protection during transfer is ensured by the use of signatures and encryption. From the user's perspective the system has only minor technical requirements and can be used with minimal setup effort. © Georg Thieme Verlag KG Stuttgart · New York.

  5. A Stainless-Steel Mandrel for Slumping Glass X-ray Mirrors

    NASA Technical Reports Server (NTRS)

    Gubarev, Mikhail V.; O'Dell, Stephen L.; Jones, William D.; Kester, Thomas J.; Griffith, Charles W.; Zhang, William W.; Saha, Timo T.; Chan, Kai-Wing

    2009-01-01

    We have fabricated a precision full-cylinder stainless-steel mandrel at Marshall Space Flight Center. The mandrel is figured for a 30-cm diameter primary (paraboloid) mirror of an 840-cm focal-length Wolter-1 telescope. We have developed this mandrel for experiments in slumping.thermal forming at about 600 C.of glass mirror segments at Goddard Space Flight Center, in support of NASA's participation in the International X-ray Observatory (IXO). Precision turning of stainless-steel mandrels may offer a low-cost alternative to conventional figuring of fused-silica or other glassy forming mandrels. We report on the fabrication, metrology, and performance of this first mandrel; then we discuss plans and goals for stainless-steel mandrel technology.

  6. A Stainless-Steel Mandrel for Slumping Glass X-Ray Mirrors

    NASA Technical Reports Server (NTRS)

    ODell, Stephen L.; Gubarev, Mikhail V.; Jones, William D.; Kester, Thomas J.; Griffith, Charles W.; Zhang, William W.; Saha, Timo T.; Chan, Kai-Wing

    2008-01-01

    We have fabricated a precision full -cylinder stainless-steel mandrel at Marshall Space Flight Center. The mandrel is figured for a 30-cm-diameter primary (paraboloid) mirror of an 840-cm focal-lengthWolter-1 telescope. We have developed this mandrel for experiments in slumping.thermal forming at about 600 C-of glass mirror segments at Goddard Space Flight Center, in support of NASA fs participation in the International X -ray Observatory (IXO). Precision turning of stainless ]steel mandrels may offer a lowcost alternative to conventional figuring of fused -silica or other glassy forming mandrels. We report on the fabrication, metrology, and performance of this first mandrel; then we discuss plans and goals for stainless-steel mandrel technology.

  7. Effects of C and Si on strain aging of strain-based API X60 pipeline steels

    NASA Astrophysics Data System (ADS)

    Sung, Hyo Kyung; Lee, Dong Ho; Lee, Sunghak; Lee, Byeong-Joo; Hong, Seung-Pyo; Kim, Young-Woon; Yoo, Jang Yong; Hwang, Byoungchul; Shin, Sang Yong

    2017-05-01

    Four types of strain-based API X60 pipeline steels were fabricated by varying the C and Si contents, and the effects of C and Si on strain aging were investigated. The 0.05 wt% C steels consisted mainly of polygonal ferrite (PF), whereas the 0.08 wt% C steels consisted of acicular ferrite (AF). The volume fraction of AF increased with increasing C content because C is an austenite stabilizer element. The volume fractions of bainitic ferrite (BF) of the 0.15 wt% Si steels were higher than those of the 0.25 wt% Si steels, whereas the volume fractions of the secondary phases were lower. From the tensile properties before and after the aging process of the strainbased API X60 pipeline steels, the yield strength increased and the uniform and total elongation decreased, which is the strain aging effect. The strain aging effect in the strain-based API X60 pipeline steels was minimized when the volume fraction of AF was increased and secondary phases were distributed uniformly. On the other hand, an excessively high C content formed fine precipitates, and the strain aging effect occurred because of the interactions among dislocations and fine precipitates.

  8. Summary of Structural Evaluation and Design Support for the Underground Nuclear Test Program.

    DTIC Science & Technology

    1979-07-01

    consider using API -5LX pipe as this pipe has been shown to have high ductility (better than A36). This pipe comes in several grades (X42, X46, X52 , X56, X60...X65, X70) with the grade number representing the yield strength (ksi) of the steel. Grades X42 and X52 are readily available while the higher yield...strength steels are less readily available. I believe X52 has certainly a high enough yield strength (52,000 psi) for your application and that even

  9. 78 FR 54864 - Light-Walled Rectangular Pipe and Tube From Mexico: Preliminary Results and Partial Rescission of...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-09-06

    ... DEPARTMENT OF COMMERCE International Trade Administration [A-201-836] Light-Walled Rectangular... the antidumping duty order on light-walled rectangular pipe and tube (LWR pipe and tube) from Mexico... The merchandise subject to the order is certain welded carbon- quality light-walled steel pipe and...

  10. 78 FR 62583 - Welded Stainless Pressure Pipe From Malaysia, Thailand, and the Socialist Republic of Vietnam...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-10-22

    ... Pressure Pipe From Malaysia: Request for Extension of Preliminary Determination,'' ``Welded Stainless Steel... Stainless Pressure Pipe From Malaysia, Thailand, and the Socialist Republic of Vietnam: Postponement of...: Charles Riggle (Malaysia), Brandon [[Page 62584

  11. A Thermodynamic Model to Estimate the Formation of Complex Nitrides of Al x Mg(1- x)N in Silicon Steel

    NASA Astrophysics Data System (ADS)

    Luo, Yan; Zhang, Lifeng; Li, Ming; Sridhar, Seetharaman

    2018-06-01

    A complex nitride of Al x Mg(1- x)N was observed in silicon steels. A thermodynamic model was developed to predict the ferrite/nitride equilibrium in the Fe-Al-Mg-N alloy system, using published binary solubility products for stoichiometric phases. The model was used to estimate the solubility product of nitride compound, equilibrium ferrite, and nitride compositions, and the amounts of each phase, as a function of steel composition and temperature. In the current model, the molar ratio Al/(Al + Mg) in the complex nitride was great due to the low dissolved magnesium in steel. For a steel containing 0.52 wt pct Als, 10 ppm T.Mg., and 20 ppm T.N. at 1100 K (827 °C), the complex nitride was expressed by Al0.99496Mg0.00504N and the solubility product of this complex nitride was 2.95 × 10-7. In addition, the solution temperature of the complex nitride increased with increasing the nitrogen and aluminum in steel. The good agreement between the prediction and the detected precipitate compositions validated the current model.

  12. The effects of insulation defects on the corrosion of sub-sea super duplex stainless steel process pipes

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Francis, R.; Irwin, J.; Byrne, G.

    1995-10-01

    There is an increasing use of CRAs (corrosion resistant alloys) for subsea flowlines. These pipes carry corrosive fluids at high temperatures and pressures, and insulation is usually, applied to prevent excessive cooling of the process fluids. The present tests were undertaken to investigate the effect of insulation defects on the susceptibility to localized corrosion of a super duplex stainless steel at different internal temperatures. Four different commercial coating systems were tested, Neoprene, EPDM, Polyurethane and Polyurethane foam. The results show that pitting occurred at an average temperature of 55 C for neoprene and EPDM, and at lower temperatures for themore » other two coatings. The reasons for this are discussed, and the implications for service applications.« less

  13. Impact of saline aquifer water on surface and shallow pit corrosion of martensitic stainless steels during exposure to CO2 environment (CCS)

    NASA Astrophysics Data System (ADS)

    Pfennig, Anja; Kranzmann, Axel

    2018-05-01

    Pipe steels suitable for carbon capture and storage technology (CCS) require resistance against the corrosive environment of a potential CCS-site, e.g. heat, pressure, salinity of the aquifer, CO2-partial pressure. Samples of different mild and high alloyed stainless injection-pipe steels partially heat treated: 42CrMo4, X20Cr13, X46Cr13, X35CrMo4 as well as X5CrNiCuNb16-4 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CO2-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. Main corrosion products are FeCO3 and FeOOH. Corrosion rates obtained at 100 bar are generally much lower than those measured at ambient pressure. Highest surface corrosion rates are 0.8 mm/year for 42CrMo4 and lowest 0.01 mm/year for X5CrNiCuNb16-4 in the vapour phase at ambient pressure. At 100 bar the highest corrosion rates are 0.01 mm/year for 42CrMo4, X20Cr13 (liquid phase), X46Cr13 and less than 0.01 mm/year for X35CrMo4 and X5CrNiCuNb16-4 after 8000 h of exposure with no regard to atmosphere. Martensitic microstructure offers good corrosion resistance.

  14. Experimental study of plastic responses of pipe elbows

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Greenstreet, W.L.

    Load-deflection responses were determined experimentally for sixteen 152.4-mm (6-in.) (nominal) commercial carbon steel pipe elbows and four 152.4-mm (6-in.) stainless steel elbows. Each specimen was loaded with an external force of sufficient magnitude to produce predominantly plastic response. The influences of bend radius and wall thickness were studied, as well as the effect of internal prssure on load-deflection behavior. Comparisons of results from stainless steel and from carbon steel elbows indicate differences in responses attributable to material differences. The results were interpreted in terms of limit analysis concepts, and collapse loads were determined. Trends given by the collapse loads aremore » identified and discussed.« less

  15. Friction loss in straight pipes of unplasticized polyvinyl chloride.

    PubMed

    Iwasaki, T; Ojima, J

    1996-01-01

    In order to design proper ductwork for a local exhaust system, airflow characteristics were investigated in straight pipes of unplasticized polyvinyl chloride (PVC). A linear decrease in static pressure was observed downstream at points from the opening of the VU pipes (JIS K 6741) located at distances greater than 10 times the pipe diameter, for velocities ranging between 10.18-36.91 m/s. Roughness inside pipes with small diameters was found to be 0.0042-0.0056 mm and the friction factor was calculated on the basis of Colebrook's equation for an airflow transition zone. An extended friction chart was then constructed on the basis of the roughness value and the friction factor. This chart can be applied when designing a local exhaust system with the ducts of diameters ranging from 40 to 900 mm. The friction loss of the PVC pipe was found to be approximately 2/3 of that of a galvanized steel pipe.

  16. Study of MA Effect on Yield Strength and Ductility of X80 Linepipe Steels Weld

    NASA Astrophysics Data System (ADS)

    Huda, Nazmul; Lazor, Robert; Gerlich, Adrian P.

    2017-09-01

    Multipass GMAW (Gas Metal Arc Welding) welding was used to join X80 linepipe materials using two weld metals of slightly different compositions. Welding wires with diameters of 0.984 and 0.909 mm were used while applying the same heat input in each pass. The slight difference in the wire diameters resulted in different HAZ microstructures. The microstructures in the doubly reheated HAZ of both welds were found to contain bainite-ferrite. However, etching also revealed a difference in martensite-austenite (MA) fraction in these reheated zones. The MA exhibited twice the hardness of ferrite when measured by nanoindentation. Tensile testing from the reheated zone of both welds revealed a difference in yield strength, tensile strength and elongation of the transverse weld specimens. In the reheated zone of weld A, (produced with a 0.984 mm wire) a higher fraction of MA was observed, which resulted in higher strength but lower elongation compared to weld B. The ductility of weld A was found severely impaired (to nearly half of weld B) due to formation of closely spaced voids around the MA, along with debonding of MA from the matrix, which occurs just above the yield stress.

  17. 20. DETAILED OBLIQUE VIEW SOUTHWEST FURNACE 2, SHOWING STEEL FRAME ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    20. DETAILED OBLIQUE VIEW SOUTHWEST FURNACE 2, SHOWING STEEL FRAME BOXES FOR COUNTERWEIGHTS, AND FURNACE HEATING PIPES AT RIGHT. - Vulcan Crucible Steel Company, Building No. 3, 100 First Street, Aliquippa, Beaver County, PA

  18. PHOTOCOPY OF STANDARD USDA/USFS PLAN FOR 13' X 13' STEEL ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    PHOTOCOPY OF STANDARD USDA/USFS PLAN FOR 13' X 13' STEEL LOOKOUT HOUSE (CAB); ELEVATIONS, SECTIONS, MISC. DETAILS; DATED 1961 - North Mountain Lookout, Stanislaus National Forest, Groveland, Tuolumne County, CA

  19. 46 CFR 76.15-15 - Piping.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... pressure of not less than 6,000 p.s.i. (b) All piping, in nominal sizes not over 3/4 inch, shall be at least Schedule 40 (standard weight), and in nominal sizes over 3/4 inch, shall be at least Schedule 80 (extra heavy). (c) All piping, valves, and fittings of ferrous materials shall be protected inside and...

  20. Heat Pipes

    NASA Astrophysics Data System (ADS)

    1990-01-01

    Bobs Candies, Inc. produces some 24 million pounds of candy a year, much of it 'Christmas candy.' To meet Christmas demand, it must produce year-round. Thousands of cases of candy must be stored a good part of the year in two huge warehouses. The candy is very sensitive to temperature. The warehouses must be maintained at temperatures of 78-80 degrees Fahrenheit with relative humidities of 38- 42 percent. Such precise climate control of enormous buildings can be very expensive. In 1985, energy costs for the single warehouse ran to more than 57,000 for the year. NASA and the Florida Solar Energy Center (FSEC) were adapting heat pipe technology to control humidity in building environments. The heat pipes handle the jobs of precooling and reheating without using energy. The company contacted a FSEC systems engineer and from that contact eventually emerged a cooperative test project to install a heat pipe system at Bobs' warehouses, operate it for a period of time to determine accurately the cost benefits, and gather data applicable to development of future heat pipe systems. Installation was completed in mid-1987 and data collection is still in progress. In 1989, total energy cost for two warehouses, with the heat pipes complementing the air conditioning system was 28,706, and that figures out to a cost reduction.

  1. Heat Pipes

    NASA Technical Reports Server (NTRS)

    1990-01-01

    Bobs Candies, Inc. produces some 24 million pounds of candy a year, much of it 'Christmas candy.' To meet Christmas demand, it must produce year-round. Thousands of cases of candy must be stored a good part of the year in two huge warehouses. The candy is very sensitive to temperature. The warehouses must be maintained at temperatures of 78-80 degrees Fahrenheit with relative humidities of 38- 42 percent. Such precise climate control of enormous buildings can be very expensive. In 1985, energy costs for the single warehouse ran to more than $57,000 for the year. NASA and the Florida Solar Energy Center (FSEC) were adapting heat pipe technology to control humidity in building environments. The heat pipes handle the jobs of precooling and reheating without using energy. The company contacted a FSEC systems engineer and from that contact eventually emerged a cooperative test project to install a heat pipe system at Bobs' warehouses, operate it for a period of time to determine accurately the cost benefits, and gather data applicable to development of future heat pipe systems. Installation was completed in mid-1987 and data collection is still in progress. In 1989, total energy cost for two warehouses, with the heat pipes complementing the air conditioning system was $28,706, and that figures out to a cost reduction.

  2. Pitting Initiation and Propagation of X70 Pipeline Steel Exposed to Chloride-Containing Environments

    PubMed Central

    Yang, Zixuan; Kan, Bo; Li, Jinxu; Su, Yanjing; Qiao, Lijie; Volinsky, Alex A.

    2017-01-01

    Inclusion-induced pitting initiation mechanisms in X70 steel were investigated by scanning electron microscopy, scanning Kelvin probe force microscopy (SKPFM), immersion and electrochemical polarization tests in chloride-containing ion solutions. There are three inclusion types in the X70 steel. Corrosion test results indicated that pitting corrosion resistance of type A inclusion < type C inclusion < type B inclusion, i.e., (Mn, Ca)S < matrix < (Al, Ca)O. SKPFM test results show that the type A inclusion exhibited both lower and higher potentials than the matrix, while the type B inclusion exhibited higher potential than the matrix. The corrosion test and the SKPFM potential test results are consistent. Potentiodynamic polarization results indicate that the type A and C are active inclusions, while the type B is an inactive inclusion. Three kinds of possible mechanisms of inclusion-induced pitting corrosion are established for the X70 steel. PMID:28902156

  3. Sodium Heat Pipe Module Processing For the SAFE-100 Reactor Concept

    NASA Technical Reports Server (NTRS)

    Martin, James; Salvail, Pat

    2003-01-01

    To support development and hardware-based testing of various space reactor concepts, the Early Flight Fission-Test Facility (EFF-TF) team established a specialized glove box unit with ancillary systems to handle/process alkali metals. Recently, these systems have been commissioned with sodium supporting the fill of stainless steel heat pipe modules for use with a 100 kW thermal heat pipe reactor design. As part of this effort, procedures were developed and refined to govern each segment of the process covering: fill, leak check, vacuum processing, weld closeout, and final "wet in". A series of 316 stainless steel modules, used as precursors to the actual 321 stainless steel modules, were filled with 35 +/- 1 grams of sodium using a known volume canister to control the dispensed mass. Each module was leak checked to less than10(exp -10) std cc/sec helium and vacuum conditioned at 250 C to assist in the removal of trapped gases. A welding procedure was developed to close out the fill stem preventing external gases from entering the evacuated module. Finally the completed modules were vacuum fired at 750 C allowing the sodium to fully wet the internal surface and wick structure of the heat pipe module.

  4. Sodium Heat Pipe Module Processing For the SAFE-100 Reactor Concept

    NASA Astrophysics Data System (ADS)

    Martin, James; Salvail, Pat

    2004-02-01

    To support development and hardware-based testing of various space reactor concepts, the Early Flight Fission-Test Facility (EFF-TF) team established a specialized glove box unit with ancillary systems to handle/process alkali metals. Recently, these systems have been commissioned with sodium supporting the fill of stainless steel heat pipe modules for use with a 100 kW thermal heat pipe reactor design. As part of this effort, procedures were developed and refined to govern each segment of the process covering: fill, leak check, vacuum processing, weld closeout, and final ``wet in''. A series of 316 stainless steel modules, used as precursors to the actual 321 stainless steel modules, were filled with 35 +/-1 grams of sodium using a known volume canister to control the dispensed mass. Each module was leak checked to <10-10 std cc/sec helium and vacuum conditioned at 250 °C to assist in the removal of trapped gases. A welding procedure was developed to close out the fill stem preventing external gases from entering the evacuated module. Finally the completed modules were vacuum fired at 750 °C allowing the sodium to fully wet the internal surface and wick structure of the heat pipe module.

  5. Small, Untethered, Mobile Robots for Inspecting Gas Pipes

    NASA Technical Reports Server (NTRS)

    Wilcox, Brian

    2003-01-01

    Small, untethered mobile robots denoted gas-pipe explorers (GPEXs) have been proposed for inspecting the interiors of pipes used in the local distribution natural gas. The United States has network of gas-distribution pipes with a total length of approximately 109 m. These pipes are often made of iron and steel and some are more than 100 years old. As this network ages, there is a need to locate weaknesses that necessitate repair and/or preventive maintenance. The most common weaknesses are leaks and reductions in thickness, which are caused mostly by chemical reactions between the iron in the pipes and various substances in soil and groundwater. At present, mobile robots called pigs are used to inspect and clean the interiors of gas-transmission pipelines. Some carry magnetic-flux-leakage (MFL) sensors for measuring average wall thicknesses, some capture images, and some measure sizes and physical conditions. The operating ranges of pigs are limited to fairly straight sections of wide transmission- type (as distinguished from distribution- type) pipes: pigs are too large to negotiate such obstacles as bends with radii comparable to or smaller than pipe diameters, intrusions of other pipes at branch connections, and reductions in diameter at valves and meters. The GPEXs would be smaller and would be able to negotiate sharp bends and other obstacles that typically occur in gas-distribution pipes.

  6. 78 FR 41366 - Certain Large Diameter Carbon and Alloy Seamless Standard, Line, and Pressure Pipe (Over 4 1/2

    Federal Register 2010, 2011, 2012, 2013, 2014

    2013-07-10

    ... Carbon and Alloy Seamless Standard, Line, and Pressure Pipe (Over 4 \\1/2\\ Inches) From Japan: Preliminary... seamless standard, line, and pressure pipe (over 4 \\1/2\\ inches) (large diameter seamless pipe) from Japan.../exporters of subject merchandise, Canadian Natural Resources Limited (CNRL), JFE Steel Corporation (JFE...

  7. Thermostructural applications of heat pipes

    NASA Technical Reports Server (NTRS)

    Peeples, M. E.; Reeder, J. C.; Sontag, K. E.

    1979-01-01

    The feasibility of integrating heat pipes in high temperature structure to reduce local hot spot temperature was evaluated for a variety of hypersonic aerospace vehicles. From an initial list of twenty-two potential applications, the single stage to orbit wing leading edge showed the greatest promise and was selected for preliminary design of an integrated heat pipe thermostructural system. The design consisted of a Hastelloy X assembly with sodium heat pipe passages aligned normal to the wing leading edge. A d-shaped heat pipe cross section was determined to be optimum from the standpoint of structural weight.

  8. Measurements of void fraction distribution in cavitating pipe flow using x-ray CT

    NASA Astrophysics Data System (ADS)

    Bauer, D.; Chaves, H.; Arcoumanis, C.

    2012-05-01

    Measuring the void fraction distribution is still one of the greatest challenges in cavitation research. In this paper, a measurement technique for the quantitative void fraction characterization in a cavitating pipe flow is presented. While it is almost impossible to visualize the inside of the cavitation region with visible light, it is shown that with x-ray computed tomography (CT) it is possible to capture the time-averaged void fraction distribution in a quasi-steady pipe flow. Different types of cavitation have been investigated including cloud-like cavitation, bubble cavitation and film cavitation at very high flow rates. A specially designed nozzle was employed to induce very stable quasi-steady cavitation. The obtained results demonstrate the advantages of the measurement technique compared to other ones; for example, structures were observed inside the cavitation region that could not be visualized by photographic images. Furthermore, photographic images and pressure measurements were used to allow comparisons to be made and to prove the superiority of the CT measurement technique.

  9. Toughness of 2,25Cr-1Mo steel and weld metal

    NASA Astrophysics Data System (ADS)

    Acarer, Mustafa; Arici, Gökhan; Acar, Filiz Kumdali; Keskinkilic, Selcuk; Kabakci, Fikret

    2017-09-01

    2,25Cr-1Mo steel is extensively used at elevated temperature structural applications in fossil fire power plants for steam pipes, nozzle chambers and petrochemical industry for hydrocracking unit due to its excellent creep resistance and good redundant to oxidation. Also they should have acceptable weldability and toughness. The steels are supplied in quenched and tempered condition and their welded components are subjected to post-weld heat treatment (PWHT). Tempering process is carried out at 690-710°C to improve toughness properties. However they are sensitive to reheat cracking and temper embrittlement. To measure temper embrittlement of the steels and their weld metal, temper embrittlement factor and formula (J factor - Watanabe and X formula- Bruscato) are used. Step cooling heat treatment is also applied to determine temper embrittlement. In this study, toughness properties of Cr Mo (W) steels were reviewed. Also transition temperature curves of 2,25Cr-1Mo steel and its weld metal were constructed before and after step cool heat treatment as experimental study. While 2,25Cr-1Mo steel as base metal was supplied, all weld metal samples were produced in Gedik Welding Company. Hardness measurements and microstructure evaluation were also carried out.

  10. Sodium Based Heat Pipe Modules for Space Reactor Concepts: Stainless Steel SAFE-100 Core

    NASA Technical Reports Server (NTRS)

    Martin, James J.; Reid, Robert S.

    2004-01-01

    A heat pipe cooled reactor is one of several candidate reactor cores being considered for advanced space power and propulsion systems to support future space exploration applications. Long life heat pipe modules, with designs verified through a combination of theoretical analysis and experimental lifetime evaluations, would be necessary to establish the viability of any of these candidates, including the heat pipe reactor option. A hardware-based program was initiated to establish the infrastructure necessary to build heat pipe modules. This effort, initiated by Los Alamos National Laboratory and referred to as the Safe Affordable Fission Engine (SAFE) project, set out to fabricate and perform non-nuclear testing on a modular heat pipe reactor prototype that can provide 100 kilowatt from the core to an energy conversion system at 700 C. Prototypic heat pipe hardware was designed, fabricated, filled, closed-out and acceptance tested.

  11. Procedures for testing and evaluating spacecraft-type heat pipes

    NASA Astrophysics Data System (ADS)

    Tower, L. K.; Kaufman, W. B.

    1984-04-01

    This report describes part of an effort to develop dependable, cost effective spacecraft thermal control heat pipes. In the program the reliability and performance of 30 commercially available heat pipes were assessed. The pipes comprised 10 groups of varying design, with aluminum and stainless steel as structural materials, and methanol and ammonia as working fluids. The factors studied were noncondensible gas accumulation and heat transfer capability in one g. The present report supplements a brief earlier report by describing in detail the procedures required to conduct a comprehensive evaluation of heat pipes for thermal control. It discusses the test facilities and testing procedures. The manner in which data may be taken for estimating useful life and comparing performance is described. Some of the pitfalls in making such judgments are illustrated. Originator supplied keywords include: heat transfer, and corrosion.

  12. Porphyrins as Corrosion Inhibitors for N80 Steel in 3.5% NaCl Solution: Electrochemical, Quantum Chemical, QSAR and Monte Carlo Simulations Studies.

    PubMed

    Singh, Ambrish; Lin, Yuanhua; Quraishi, Mumtaz A; Olasunkanmi, Lukman O; Fayemi, Omolola E; Sasikumar, Yesudass; Ramaganthan, Baskar; Bahadur, Indra; Obot, Ime B; Adekunle, Abolanle S; Kabanda, Mwadham M; Ebenso, Eno E

    2015-08-18

    The inhibition of the corrosion of N80 steel in 3.5 wt. % NaCl solution saturated with CO2 by four porphyrins, namely 5,10,15,20-tetrakis(4-hydroxyphenyl)-21H,23H-porphyrin (HPTB), 5,10,15,20-tetra(4-pyridyl)-21H,23H-porphyrin (T4PP), 4,4',4″,4‴-(porphyrin-5,10,15,20-tetrayl)tetrakis(benzoic acid) (THP) and 5,10,15,20-tetraphenyl-21H,23H-porphyrin (TPP) was studied using electrochemical impedance spectroscopy (EIS), potentiodynamic polarization, scanning electrochemical microscopy (SECM) and scanning electron microscopy (SEM) techniques. The results showed that the inhibition efficiency, η% increases with increasing concentration of the inhibitors. The EIS results revealed that the N80 steel surface with adsorbed porphyrins exhibited non-ideal capacitive behaviour with reduced charge transfer activity. Potentiodynamic polarization measurements indicated that the studied porphyrins acted as mixed type inhibitors. The SECM results confirmed the adsorption of the porphyrins on N80 steel thereby forming a relatively insulated surface. The SEM also confirmed the formation of protective films of the porphyrins on N80 steel surface thereby protecting the surface from direct acid attack. Quantum chemical calculations, quantitative structure activity relationship (QSAR) were also carried out on the studied porphyrins and the results showed that the corrosion inhibition performances of the porphyrins could be related to their EHOMO, ELUMO, ω, and μ values. Monte Carlo simulation studies showed that THP has the highest adsorption energy, while T4PP has the least adsorption energy in agreement with the values of σ from quantum chemical calculations.

  13. Sodium alginate: A promising biopolymer for corrosion protection of API X60 high strength carbon steel in saline medium.

    PubMed

    Obot, I B; Onyeachu, Ikenna B; Kumar, A Madhan

    2017-12-15

    Sodium alginate (SA), a polysaccharide biopolymer, has been studied as an effective inhibitor against the corrosion of API X60 steel in neutral 3.5% NaCl using gravimetric and electrochemical techniques (OCP, EIS and EFM). The inhibition efficiency of the SA increased with concentration but was lower at higher temperature (70°C). Electrochemical measurements showed that the SA shifted the steel corrosion potential to more positive value and reduced the kinetics of corrosion by forming an adsorbed layer which mitigated the steel surface wetting, based on contact angle measurement. SEM-EDAX was used to confirm the inhibition of SA on API X60 steel surfaces. The SA adsorbs on the steel surface through a physisorption mechanism using its carboxylate oxygen according to UV-vis and ATR-IR measurements, respectively. This phenomena result in decreased localized pitting corrosion of the API X60 steel in 3.5% NaCl solution. Theoretical results using quantum chemical calculations and Monte Carlo simulations provide further atomic level insights into the interaction of SA with steel surface. Copyright © 2017 Elsevier Ltd. All rights reserved.

  14. Advanced radiator concepts utilizing honeycomb panel heat pipes (stainless steel)

    NASA Technical Reports Server (NTRS)

    Fleischman, G. L.; Tanzer, H. J.

    1985-01-01

    The feasibility of fabricating and processing moderate temperature range heat pipes in a low mass honeycomb sandwich panel configuration for highly efficient radiator fins for the NASA space station was investigated. A variety of honeycomb panel facesheet and core-ribbon wick concepts were evaluated within constraints dictated by existing manufacturing technology and equipment. Concepts evaluated include: type of material, material and panel thicknesses, wick type and manufacturability, liquid and vapor communication among honeycomb cells, and liquid flow return from condenser to evaporator facesheet areas. In addition, the overall performance of the honeycomb panel heat pipe was evaluated analytically.

  15. Design of dual energy x-ray detector for conveyor belt with steel wire ropes

    NASA Astrophysics Data System (ADS)

    Dai, Yue; Miao, Changyun; Rong, Feng

    2009-07-01

    A dual energy X-ray detector for conveyor belt with steel wire ropes is researched in the paper. Conveyor belt with steel wire ropes is one of primary transfer equipments in modern production. The traditional test methods like electromagnetic induction principle could not display inner image of steel wire ropes directly. So X-ray detection technology has used to detect the conveyor belt. However the image was not so clear by the interference of the rubber belt. Therefore, the dualenergy X-ray detection technology with subtraction method is developed to numerically remove the rubber belt from radiograph, thus improving the definition of the ropes image. The purpose of this research is to design a dual energy Xray detector that could make the operator easier to found the faulty of the belt. This detection system is composed of Xray source, detector controlled by FPGA chip, PC for running image processing system and so on. With the result of the simulating, this design really improved the capability of the staff to test the conveyor belt.

  16. Simulation of Targets Feeding Pipe Rupture in Wendelstein 7-X Facility Using RELAP5 and COCOSYS Codes

    NASA Astrophysics Data System (ADS)

    Kaliatka, T.; Povilaitis, M.; Kaliatka, A.; Urbonavicius, E.

    2012-10-01

    Wendelstein nuclear fusion device W7-X is a stellarator type experimental device, developed by Max Planck Institute of plasma physics. Rupture of one of the 40 mm inner diameter coolant pipes providing water for the divertor targets during the "baking" regime of the facility operation is considered to be the most severe accident in terms of the plasma vessel pressurization. "Baking" regime is the regime of the facility operation during which plasma vessel structures are heated to the temperature acceptable for the plasma ignition in the vessel. This paper presents the model of W7-X cooling system (pumps, valves, pipes, hydro-accumulators, and heat exchangers), developed using thermal-hydraulic state-of-the-art RELAP5 Mod3.3 code, and model of plasma vessel, developed by employing the lumped-parameter code COCOSYS. Using both models the numerical simulation of processes in W7-X cooling system and plasma vessel has been performed. The results of simulation showed, that the automatic valve closure time 1 s is the most acceptable (no water hammer effect occurs) and selected area of the burst disk is sufficient to prevent pressure in the plasma vessel.

  17. Investigating pitting in X65 carbon steel using potentiostatic polarisation

    NASA Astrophysics Data System (ADS)

    Mohammed, Sikiru; Hua, Yong; Barker, R.; Neville, A.

    2017-11-01

    Although pitting corrosion in passive materials is generally well understood, the growth of surface pits in actively-corroding materials has received much less attention to date and remains poorly understood. One of the key challenges which exists is repeatedly and reliably generating surface pits in a practical time-frame in the absence of deformation and/or residual stress so that studies on pit propagation and healing can be performed. Another pertinent issue is how to evaluate pitting while addressing general corrosion in low carbon steel. In this work, potentiostatic polarisation was employed to induce corrosion pits (free from deformation or residual stress) on actively corroding X65 carbon steel. The influence of applied potential (50 mV, 100 mV and 150 mV vs open circuit potential) was investigated over 24 h in a CO2-saturated, 3.5 wt.% NaCl solution at 30 °C and pH 3.8. Scanning electron microscopy (SEM) was utilised to examine pits, while surface profilometry was conducted to measure pit depth as a function of applied potential over the range considered. Analyses of light pitting (up to 120 μm) revealed that pit depth increased linearly with increase in applied potential. This paper relates total pit volume (measured using white light interferometry) to dissipated charge or total mass loss (using the current response for potentiostatic polarisation in conjunction with Faraday's law). By controlling the potential of the surface (anodic) the extent of pitting and general corrosion could be controlled. This allowed pits to be evaluated for their ability to continue to propagate after the potentiostatic technique was employed. Linear growth from a depth of 70 μm at pH 3.8, 80 °C was demonstrated. The technique offers promise for the study of inhibition of pitting.

  18. 46 CFR 154.1125 - Pipes, fittings, and valves.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ..., fitting, and valve for the water spray system must be made of fire resistant and corrosion resistant materials, such as galvanized steel or galvanized iron pipe. (e) Each water spray system must have a means of drainage to prevent corrosion of the system and freezing of accumulated water in subfreezing...

  19. 46 CFR 154.1125 - Pipes, fittings, and valves.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ..., fitting, and valve for the water spray system must be made of fire resistant and corrosion resistant materials, such as galvanized steel or galvanized iron pipe. (e) Each water spray system must have a means of drainage to prevent corrosion of the system and freezing of accumulated water in subfreezing...

  20. Piping Inelastic Fracture Mechanics Analysis.

    DTIC Science & Technology

    1980-06-30

    LOCATIONd THERM4AL SLEEVE REPAIR WELD TYPE 310 STAINLESS TEL C FVICt AREA SPO PCE Fig. 3.1-Duane Arnold recirculation-inlet-nozzle safe end configuration...Environment The most commonly used materials in the LWR piping system are Types 304 and 316 austenitic stainless steel ( cast /wrought). However, for various...seismic and water hammering), the contribu- tion of the residual stress due to the welding plays a very important role in initiation and propagation

  1. 49 CFR 192.620 - Alternative maximum allowable operating pressure for certain steel pipelines.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... for certain steel pipelines. 192.620 Section 192.620 Transportation Other Regulations Relating to... STANDARDS Operations § 192.620 Alternative maximum allowable operating pressure for certain steel pipelines..., 2, or 3 location; (2) The pipeline segment is constructed of steel pipe meeting the additional...

  2. Pulsed Eddy Current Sensing for Critical Pipe Condition Assessment

    PubMed Central

    2017-01-01

    Pulsed Eddy Current (PEC) sensing is used for Non-Destructive Evaluation (NDE) of the structural integrity of metallic structures in the aircraft, railway, oil and gas sectors. Urban water utilities also have extensive large ferromagnetic structures in the form of critical pressure pipe systems made of grey cast iron, ductile cast iron and mild steel. The associated material properties render NDE of these pipes by means of electromagnetic sensing a necessity. In recent years PEC sensing has established itself as a state-of-the-art NDE technique in the critical water pipe sector. This paper presents advancements to PEC inspection in view of the specific information demanded from water utilities along with the challenges encountered in this sector. Operating principles of the sensor architecture suitable for application on critical pipes are presented with the associated sensor design and calibration strategy. A Gaussian process-based approach is applied to model a functional relationship between a PEC signal feature and critical pipe wall thickness. A case study demonstrates the sensor’s behaviour on a grey cast iron pipe and discusses the implications of the observed results and challenges relating to this application. PMID:28954392

  3. Pulsed Eddy Current Sensing for Critical Pipe Condition Assessment.

    PubMed

    Ulapane, Nalika; Alempijevic, Alen; Vidal Calleja, Teresa; Valls Miro, Jaime

    2017-09-26

    Pulsed Eddy Current (PEC) sensing is used for Non-Destructive Evaluation (NDE) of the structural integrity of metallic structures in the aircraft, railway, oil and gas sectors. Urban water utilities also have extensive large ferromagnetic structures in the form of critical pressure pipe systems made of grey cast iron, ductile cast iron and mild steel. The associated material properties render NDE of these pipes by means of electromagnetic sensing a necessity. In recent years PEC sensing has established itself as a state-of-the-art NDE technique in the critical water pipe sector. This paper presents advancements to PEC inspection in view of the specific information demanded from water utilities along with the challenges encountered in this sector. Operating principles of the sensor architecture suitable for application on critical pipes are presented with the associated sensor design and calibration strategy. A Gaussian process-based approach is applied to model a functional relationship between a PEC signal feature and critical pipe wall thickness. A case study demonstrates the sensor's behaviour on a grey cast iron pipe and discusses the implications of the observed results and challenges relating to this application.

  4. Time Reversal Method for Pipe Inspection with Guided Wave

    NASA Astrophysics Data System (ADS)

    Deng, Fei; He, Cunfu; Wu, Bin

    2008-02-01

    The temporal-spatial focusing effect of the time reversal method on the guided wave inspection in pipes is investigated. A steel pipe model with outer diameter of 70 mm and wall thickness of 3.5 mm is numerically built to analyse the reflection coefficient of L(0,2) mode when the time reversal method is applied in the model. According to the calculated results, it is shown that a synthetic time reversal array method is effective to improve the signal-to-noise ratio of a guided wave inspection system. As an intercepting window is widened, more energy can be included in a re-emitted signal, which leads to a large reflection coefficient of L(0,2) mode. It is also shown that when a time reversed signal is reapplied in the pipe model, by analysing the motion of the time reversed wave propagating along the pipe model, a defect can be identified. Therefore, it is demonstrated that the time reversal method can be used to locate the circumferential position of a defect in a pipe. Finally, through an experiment corresponding with the pipe model, the experimental result shows that the above-mentioned method can be valid in the inspection of a pipe.

  5. Establishing a design procedure for buried steel-reinforced high density polyethylene (SRHDPE) pipes.

    DOT National Transportation Integrated Search

    2013-11-01

    Metal and plastic pipes have been used extensively as storm sewers and buried drainage structures in transportation projects. Metal pipes have : high strength and stiffness but are susceptible to corrosion from wastewaters containing acid, and from a...

  6. Field investigation on structural performance of the buried UPVC pipes with and without geogrid reinforcement

    NASA Astrophysics Data System (ADS)

    Teja, Akkineni Surya; Rajkumar, R.; Gokula Krishnan, B.; Aravindh, R.

    2018-02-01

    Buried pipes are used mainly for water supply and drainage besides many other applications such as oil, liquefied natural gas, coal slurries and mine tailings. The pipes used may be rigid (reinforced concrete, vitrified clay and ductile iron) or flexible (Steel, UPVC, aluminium, Fiber glass and High-density polyethylene) although the distinction between them is blurring. Flexible pipe design is governed by deflection or buckling. UPVC pipes are preferred due to light weight, long term chemical stability and cost efficiency. This project aims to study the load deformation behaviour of the buried pipe and stress variation across the cross section of the pipe under static loading along with the influence of depth of embedment, density of backfill on the deformation and stresses in pipe and the deformation behaviour of buried pipe when soil is reinforced with geogrid reinforcement and evaluate the structural performance of the pipe.

  7. In Situ Corrosion and Heat Loss Assessment of Two Nonstandard Underground Heat Distribution System Piping Designs

    DTIC Science & Technology

    2011-06-01

    of this specific design consists of a carrier pipe, carrier pipe insulation ( mineral wool ), an annular air space, steel casing, a layer of exterior...excavation site agree with Perma-Pipe “Multi-Therm 500” nominal specs for 10” carrier with 2” mineral wool insulation. 3. Conduit Temperature: Supply...the ASHRAE calculation method or by manufacturer performance claims. MEC is reasonably certain that the mineral wool insulation used by the

  8. Modeling the GPR response of leaking, buried pipes

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Powers, M.H.; Olhoeft, G.R.

    1996-11-01

    Using a 2.5D, dispersive, full waveform GPR modeling program that generates complete GPR response profiles in minutes on a Pentium PC, the effects of leaking versus non-leaking buried pipes are examined. The program accounts for the dispersive, lossy nature of subsurface materials to GPR wave propagation, and accepts complex functions of dielectric permittivity and magnetic permeability versus frequency through Cole-Cole parameters fit to laboratory data. Steel and plastic pipes containing a DNAPL chlorinated solvent, an LNAPL hydrocarbon, and natural gas are modeled in a surrounding medium of wet, moist, and dry sand. Leaking fluids are found to be more detectablemore » when the sand around the pipes is fully water saturated. The short runtimes of the modeling program and its execution on a PC make it a useful tool for exploring various subsurface models.« less

  9. Research of x-ray nondestructive detector for high-speed running conveyor belt with steel wire ropes

    NASA Astrophysics Data System (ADS)

    Wang, Junfeng; Miao, Changyun; Wang, Wei; Lu, Xiaocui

    2008-03-01

    An X-ray nondestructive detector for high-speed running conveyor belt with steel wire ropes is researched in the paper. The principle of X-ray nondestructive testing (NDT) is analyzed, the general scheme of the X-ray nondestructive testing system is proposed, and the nondestructive detector for high-speed running conveyor belt with steel wire ropes is developed. The hardware of system is designed with Xilinx's VIRTEX-4 FPGA that embeds PowerPC and MAC IP core, and its network communication software based on TCP/IP protocol is programmed by loading LwIP to PowerPC. The nondestructive testing of high-speed conveyor belt with steel wire ropes and network transfer function are implemented. It is a strong real-time system with rapid scanning speed, high reliability and remotely nondestructive testing function. The nondestructive detector can be applied to the detection of product line in industry.

  10. 33 CFR 157.122 - Piping, valves, and fittings.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... OIL IN BULK Crude Oil Washing (COW) System on Tank Vessels Design, Equipment, and Installation § 157..., valves, and fittings of each COW system must: (1) Meet 46 CFR part 56; and (2) Be of steel or an equivalent material accepted by the Commandant. (b) The piping of each COW system must be permanently...

  11. 77 FR 67336 - Certain Small Diameter Carbon and Alloy Seamless Standard, Line and Pressure Pipe From Romania...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-11-09

    ... products subject to the order are small diameter seamless carbon and alloy (other than stainless) steel... Carbon and Alloy Seamless Standard, Line and Pressure Pipe From Romania: Final Results of Antidumping... alloy seamless standard, line and pressure pipe from Romania. The period of review is August 1, 2010...

  12. 76 FR 65748 - Certain Pipe and Tube From Brazil, India, Korea, Mexico, Taiwan, Thailand, and Turkey; Commission...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2011-10-24

    ...-534, and 536 (Third Review)] Certain Pipe and Tube From Brazil, India, Korea, Mexico, Taiwan, Thailand... Turkey, the antidumping duty orders on welded carbon steel pipe and tube from India, Thailand, and Turkey... group responses with respect to Mexico, Thailand, and Turkey were adequate, and decided to conduct full...

  13. Effect of Acidified Feronia elephantum Leaf Extract on the Corrosion Behavior of Mild Steel

    NASA Astrophysics Data System (ADS)

    Muthukrishnan, Pitchaipillai; Prakash, Periakaruppan; Ilayaraja, Murugan; Jeyaprabha, Balasubramanian; Shankar, Karikalan

    2015-03-01

    Mild steel is used as a structural material for pipes, tank, reaction vessels, etc. which are known to corrode invariably in contact with various solvents. From the view point of a nation's economy and financial implications of corrosion hazard, it is necessary to adopt appropriate means and ways to reduce the losses due to corrosion. The use of eco-friendly corrosion inhibitors are increasing day by day. Feronia elephantum leaf extract (FELE) has been tested as eco-friendly corrosion inhibitor for A262 mild steel in 1 M H2SO4 and 1 M HCl solutions using non-electrochemical (Gravimetric, X-ray diffraction analysis, scanning electron microscopy, and Fourier transform infrared spectroscopy) and electrochemical techniques (open circuit potential, potentiostatic polarization, and electrochemical impedance measurements). The protection efficiency is found to increase with increase in FELE concentration but decrease with temperature, which is suggestive of physical adsorption mechanism. The adsorption of FELE on mild steel surface obeys the Langmuir adsorption isotherm. SEM results confirm the formation of a protective layer by FELE over mild steel surface.

  14. Demonstration and Validation of Corrosion-Mitigation Technologies for Mechanical Room Utility Piping and Cooling-Tower Pumps

    DTIC Science & Technology

    2015-05-01

    Infrastructure, Task 2.1” ERDC/CERL TR-15-5 ii Abstract Two critical infrastructure corrosion issues at Fort Bragg, NC, are the cor- rosion of steel utility...piping union joints in mechanical rooms and the cor- rosion of steel pump housings in cooling tower systems. Reliable operation of these components...pump 5 incorporating 316 stainless steel housing. .................................... 19 Figure 13. New pump 5 being installed

  15. AC-Induced Bias Potential Effect on Corrosion of Steels

    DTIC Science & Technology

    2009-02-05

    induction, variable conduction Experimental Setup Super- martensitic stainless steel composition Analysis: C Mn Si Cr Ni Mo Cu N Typical 13 Cr ɘ.01 0.6... stainless steel used in pipelines. •Low carbon (ɘ.01): allows the formation of a “soft” martensite that is more resistant than standard martensitic ...Proposed AC Corrosion Models  AC Simulated Corrosion testing  Stainless steel pipe and coating  Cathodic protection  Experimental Setup  Preliminary

  16. Conceptual design study: Cold water pipe systems for self-mounted OTEC powerplants

    NASA Astrophysics Data System (ADS)

    1981-02-01

    The conceptual design and installation aspects of cold water pipes (CWP) systems for shelf mounted OTEC power plants in Puerto Rico and Hawaii are considered. The CWP systems using Fiberglass Reinforced Plastic (FRP) and steel were designed; the FRP, can be controlled by varying the core thickness; and steel is used as a structural material in offshore applications. A marine railway approach was chosen for installation of the CWP. Two methods for pulling the track for the railway down the pipe fairway to its final location are presented. The track is permanently fastened to the sloping seabed with piles installed by a remotely controlled cart that rides on the track itself. Both the marine railway and the shelf mounted platform that houses the OTEC power plant require an anodic or equivalent corrosion protection system.

  17. Method of manufacturing a heat pipe wick with structural enhancement

    DOEpatents

    Andraka, Charles E [Albuquerque, NM; Adkins, Douglas R [Albuquerque, NM; Moreno, James B [Albuquerque, NM; Rawlinson, K Scott [Albuquerque, NM; Showalter, Steven K [Albuquerque, NM; Moss, Timothy A [Albuquerque, NM

    2006-10-24

    Heat pipe wick structure wherein a stout sheet of perforated material overlays a high performance wick material such as stainless steel felt affixed to a substrate. The inventive structure provides a good flow path for working fluid while maintaining durability and structural stability independent of the structure (or lack of structure) associated with the wick material. In one described embodiment, a wick of randomly laid .about.8 micron thickness stainless steel fibers is sintered to a metal substrate and a perforated metal overlay.

  18. 75 FR 69125 - Certain Seamless Carbon and Alloy Steel Standard, Line, and Pressure Pipe From China

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-11-10

    ... standard, line, and pressure pipe (``seamless SLP pipe''), provided for in subheadings 7304.19.10, 7304.19... Charlotte R. Lane determines that the domestic seamless SLP pipe industry is materially injured by reason of... notification of preliminary determinations by Commerce that imports of seamless SLP pipe from China were...

  19. 75 FR 11119 - Certain Large Diameter Carbon and Alloy Seamless Standard, Line, and Pressure Pipe From Japan...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-03-10

    ... Carbon and Alloy Seamless Standard, Line, and Pressure Pipe From Japan: Extension of Time Limit for... review of the antidumping duty order on certain large diameter carbon and alloy seamless standard, line... manufacturers/exporters: JFE Steel Corporation; Nippon Steel Corporation; NKK Tubes; and Sumitomo Metal...

  20. 77 FR 21734 - Certain Small Diameter Carbon and Alloy Seamless Standard, Line, and Pressure Pipe From Romania...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2012-04-11

    ... Carbon and Alloy Seamless Standard, Line, and Pressure Pipe From Romania: Extension of Time Limit for... diameter carbon and alloy seamless standard, line and pressure pipe from Romania for the period August 1... investigation based upon the allegation of the petitioner, U.S. Steel. See the memorandum to Susan Kuhbach dated...

  1. The effect of various deformation processes on the corrosion behavior of casing and tubing carbon steels in sweet environment

    NASA Astrophysics Data System (ADS)

    Elramady, Alyaa Gamal

    The aim of this research project is to correlate the plastic deformation and mechanical instability of casing steel materials with corrosion behavior and surface change, in order to identify a tolerable degree of deformation for casing steel materials. While the corrosion of pipeline and casing steels has been investigated extensively, corrosion of these steels in sweet environments with respect to plastic deformation due to bending, rolling, autofrettage, or handling needs more investigation. Downhole tubular expansion of pipes (casings) is becoming standard practice in the petroleum industry to repair damaged casings, shutdown perforations, and ultimately achieve mono-diameter wells. Tubular expansion is a cold-drawing metal forming process, which consists of running conical mandrels through casings either mechanically using a piston or hydraulically by applying a back pressure. This mechanism subjects the pipes to large radial plastic deformations of up to 30 pct. of the inner diameter. It is known that cold-working is a way of strengthening materials such as low carbon steel, but given that this material will be subjected to corrosive environments, susceptibility to stress corrosion cracking (SCC) should be investigated. This research studies the effect of cold-work, in the form of cold-rolling and cold-expansion, on the surface behavior of API 5CT steels when it is exposed to a CO2-containing environment. Cold-work has a pronounced influence on the corrosion behavior of both API 5CT K55 and P110 grade steels. The lowest strength grade steel, API 5CT K55, performed poorly in a corrosive environment in the slow strain rate test. The ductile material exhibited the highest loss in strength and highest susceptibility to stress corrosion cracking in a CO 2-containing environment. The loss in strength declined with cold-rolling, which can be ascribed to the surface compressive stresses induced by cold-work. On the other hand, API 5CT P110 grade steels showed higher

  2. Fatigue crack growth of 316NG austenitic stainless steel welds at 325 °C

    NASA Astrophysics Data System (ADS)

    Li, Y. F.; Xiao, J.; Chen, Y.; Zhou, J.; Qiu, S. Y.; Xu, Q.

    2018-02-01

    316NG austenitic stainless steel is a commonly-used material for primary coolant pipes of pressurized water reactor systems. These pipes are usually joined together by automated narrow gap welding process. In this study, welds were prepared by narrow gap welding on 316NG austenitic stainless steel pipes, and its microstructure of the welds was characterized. Then, fatigue crack growth tests were conducted at 325 °C. Precipitates enriched with Mn and Si were found in the fusion zone. The fatigue crack path was out of plane and secondary cracks initiated from the precipitate/matrix interface. A moderate acceleration of crack growth was also observed at 325°Cair and water (DO = ∼10 ppb) with f = 2 Hz.

  3. Thermal Analysis of Heat Pipe Radiators with A Rectangular Groove Wick Structure

    DTIC Science & Technology

    1990-06-01

    heat pipe inside radius r, .... heat pipe vapor core radius R ..... radiosity R, . Reynolds number of vapor flow Rf .... reduction factor t ..... one...The radiosity of the fin element, R(x), consists of the emission from the surface of the fin element plus the reflected irradiation from both...the radiosity received from both heat pipe condensers, i.e., heat pipe condenser 1 and condenser 2. It can 2-12 be expressed as I(x)wedx = l R(O2)Fi

  4. Process research into metallic pipe wear of hot chamber die casting machines and methods ofincreasing wear resistance

    NASA Astrophysics Data System (ADS)

    Mukhametzyanova, G. F.; Kolesnikov, MS; Mukhametzyanov, I. R.; Astatshenko, V. I.

    2017-09-01

    The kinetics and reasons for metallic pipe wear of hot chamberzinc alloy die casting machines are established.Increasing metallic pipe wear components wear resistance is being achieved by means of die steelДИ - 22 with electroslag remelting modification and electron-beamremelting modification and after the processes of nitriding and boriding besides.

  5. 49 CFR 192.111 - Design factor (F) for steel pipe.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... NATURAL AND OTHER GAS BY PIPELINE: MINIMUM FEDERAL SAFETY STANDARDS Pipe Design § 192.111 Design factor (F... street, or a railroad; (3) Is supported by a vehicular, pedestrian, railroad, or pipeline bridge; or (4...

  6. Inspecting Pipe Radiographically Through Asbestos Insulation

    NASA Technical Reports Server (NTRS)

    Gianettino, David P.

    1994-01-01

    Welds between sections of insulated steampipe located and inspected radiographically. Unless need to repair defective weld, one avoids cost, time, and hazard of removing asbestos insulation. Enables inspectors to locate and evaluate nondestructively any weld in pipe system, without shutting down steam. Hidden weld joints first located by use of low-power fluoroscope, moved along pipe while technician observes fluoroscopic image. Low-energy x rays from fluoroscope penetrate insulation but not pipe. Weld bead appears in silhouette on fluoroscope screen. Technician then accurately marks weld sites on insulation for later inspection.

  7. Residual stress determination in an overlay dissimilar welded pipe by neutron diffraction

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Woo, Wan Chuck; Em, Vyacheslav; Hubbard, Camden R

    2011-01-01

    Residual stresses were determined through the thickness of a dissimilar weld overlay pipe using neutron diffraction. The specimen has a complex joining structure consisting of a ferritic steel (SA508), austenitic steel (F316L), Ni-based consumable (Alloy 182), and overlay of Ni-base superalloy (Alloy 52M). It simulates pressurized nozzle components, which have been a critical issue under the severe crack condition of nuclear power reactors. Two neutron diffractometers with different spatial resolutions have been utilized on the identical specimen for comparison. The macroscopic 'stress-free' lattice spacing (d{sub o}) was also obtained from both using a 2-mm width comb-like coupon. The results showmore » significant changes in residual stresses from tension (300-400 MPa) to compression (-600 MPa) through the thickness of the dissimilar weld overlay pipe specimen.« less

  8. Fracture Behavior of Ultra-Low-Carbon Steel Plate and Heat-Affected-Zone.

    DTIC Science & Technology

    1990-12-01

    ferrite . This effect on the transformation kinetics of steel is shown in Fig. 2. This alloying addition, however, has experienced...V-notch ITT of -76’F (-600C). The design philo.ophy used for this alloy required that the steel be low carbon with a nearly 100% acicular ferrite ...line pipe fitting steel by International Nickel Company and was called IN 787. It is a low carbon-manganese steel strengthened with a fine precipitate

  9. Stainless Steel Vacuum Chamber for Scanning Transmission X-ray Microsopy

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Kilcoyne, Arthur L.

    The stainless steel chamber was specifically conceived and designed for housing an interferometer controlled scanning transmission x-ray microscope (STXM). The construction of the chamber is such that internal components of the microscope rest within the chamber and are fixed to a 4 inch stainless steel belly band. The integral and most important part of the chamber is the belly band, which serves to isolate high frequency vibrations (e.g., floor surroundings, people traffic) from the sensitive measurements performed using the microscope. In addition, the chamber effectively acts as a sound barrier to the nanometer measurements conducted within. The assembled chamber (andmore » microscope) are readily adjustable at the micron level using strut members external to the chamber but fixed to the belly band and a stand made of polymer concreate.« less

  10. Effective grain size and charpy impact properties of high-toughness X70 pipeline steels

    NASA Astrophysics Data System (ADS)

    Hwang, Byoungchul; Kim, Yang Gon; Lee, Sunghak; Kim, Young Min; Kim, Nack J.; Yoo, Jang Yong

    2005-08-01

    The correlation of microstructure and Charpy V-notch (CVN) impact properties of a high-toughness API X70 pipeline steel was investigated in this study. Six kinds of steel were fabricated by varying the hot-rolling conditions, and their microstructures, effective grain sizes, and CVN impact properties were analyzed. The CVN impact test results indicated that the steels rolled in the single-phase region had higher upper-shelf energies (USEs) and lower energy-transition temperatures (ETTs) than the steels rolled in the two-phase region because their microstructures were composed of acicular ferrite (AF) and fine polygonal ferrite (PF). The decreased ETT in the steels rolled in the single-phase region could be explained by the decrease in the overall effective grain size due to the presence of AF having a smaller effective grain size. On the other hand, the absorbed energy of the steels rolled in the two-phase region was considerably lower because a large amount of dislocations were generated inside PFs during rolling. It was further decreased when coarse martensite or cementite was formed during the cooling process.

  11. Structural damping results from vibration tests of straight piping sections

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Ware, A.G.; Thinnes, G.L.

    EG and G Idaho is assisting the USNRC and the Pressure Vessel Research Committee in supporting a final position on revised damping values for structural analyses of nuclear piping systems. As part of this program, a series of vibrational tests on 76-mm and 203-mm (3-in. amd 8-in.) Schedule 40 carbon steel piping was conducted to determine the changes in structural damping due to various parametric effects. The 10-m (33-ft) straight sections of piping were rigidly supported at the ends. Spring, rod, and constant force hangers, as well as a sway brace and snubbers were included as intermediate supports. Excitation wasmore » provided by low-force level hammer inpacts, a hydraulic shaker, and a 445-kN (50-ton) overhead crane. Data was recorded using acceleration, strain, and displacement time histories. This paper presents results from the testing showing the effect of stress level and type of supports on structural damping in piping.« less

  12. COST AND PERFORMANCE REPORT: INNOVATIVE ACOUSTIC SENSOR TECHNOLOGIES FOR LEAK DETECTION IN CHALLENGING PIPE TYPES

    DTIC Science & Technology

    2016-12-30

    Operational Variable LeakFinderRT Equipment Logistics Portable Case Pipe Material Pit Cast Iron, Spun Cast Iron, Steel , Ductile Iron, Asbestos Cement ...AND ACRONYMS AC asbestos cement AMI advanced metering infrastructure AWWA American Water Works Association CI cast iron DI ductile iron DoD...assessing their ability to detect and accurately locate leaks in challenging pipe types such as polyvinyl chloride (PVC), asbestos cement (AC), and

  13. X-ray fractography on fatigue fractured surface of austenitic stainless steel

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Yajima, Zenjiro; Tokuyama, Hideki; Kibayashi, Yasuo

    1995-12-31

    X-ray diffraction observation of the material internal structure beneath fracture surfaces provide fracture analysis with useful information to investigate the conditions and mechanisms of fracture. X-ray fractography is a generic name given to this technique. In the present study, X-ray fractography was applied to fatigue fracture surfaces of austenitic stainless steel (AISI 304) which consisted of solution treatment. The fatigue tests were carried out on compact tension (CT) specimens. The plastic strain on the fracture surface was estimated from measuring the line broadening of X-ray diffraction profiles. The line broadening of X-ray diffraction profiles was measured on and beneath fatiguemore » fracture surfaces. The depth of the plastic zone left on fracture surfaces was evaluated from the line broadening. The results are discussed on the basis of fracture mechanics.« less

  14. Quality assurance in the production of pipe fittings by automatic laser-based material identification

    NASA Astrophysics Data System (ADS)

    Moench, Ingo; Peter, Laszlo; Priem, Roland; Sturm, Volker; Noll, Reinhard

    1999-09-01

    In plants of the chemical, nuclear and off-shore industry, application specific high-alloyed steels are used for pipe fittings. Mixing of different steel grades can lead to corrosion with severe consequential damages. Growing quality requirements and environmental responsibilities demand a 100% material control in the production of the pipe fittings. Therefore, LIFT, an automatic inspection machine, was developed to insure against any mix of material grades. LIFT is able to identify more than 30 different steel grades. The inspection method is based on Laser-Induced Breakdown Spectrometry (LIBS). An expert system, which can be easily trained and recalibrated, was developed for the data evaluation. The result of the material inspection is transferred to an external handling system via a PLC interface. The duration of the inspection process is 2 seconds. The graphical user interface was developed with respect to the requirements of an unskilled operator. The software is based on a realtime operating system and provides a safe and reliable operation. An interface for the remote maintenance by modem enables a fast operational support. Logged data are retrieved and evaluated. This is the basis for an adaptive improvement of the configuration of LIFT with respect to changing requirements in the production line. Within the first six months of routine operation, about 50000 pipe fittings were inspected.

  15. Heavy-section steel technology program. Semiannual progress report for period ending February 28, 1973

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    None

    1974-02-01

    The materials investigations under the HSST program are divided into studies of unirradiated materials and studies of irradiation effects. The studies of unirradiated materials, which include inspection, characterization, metallurgy, variability determinations, transition temperature investigations, fracture mechanics studies, and fatigue-crack propagation tests, are discussed. The investigations of irradiated materials include studies of radiation effects on A-533-B steel. Results of studies on thick pressure vessels and pipes of ASTM A508 steel are also reported along with results of studies on Mode III crack extension in reactor piping. (JRD)

  16. Inhibition of calcium carbonate deposition on stainless steel using olive leaf extract as a green inhibitor.

    PubMed

    Aidoud, Roumaissa; Kahoul, Abdelkrim; Naamoune, Farid

    2017-01-01

    The antiscale properties of the aqueous extract of olive (Olea europaea L.) leaves as a natural scale inhibitor for stainless steel surface in Hammam raw water were investigated using chronoamperometry (CA) and electrochemical impedance spectroscopy techniques in conjunction with a microscopic examination. The X-ray diffraction analysis reveals that the scale deposited over the pipe walls consists of pure CaCO 3 calcite. The CA, in accordance with electrochemical impedance spectra and scanning electron microscopy, shows that the inhibition efficiency increases with increasing extract concentration. This efficiency is considerably reduced as the temperature is increased.

  17. Characterization of a cold-rolled 2101 lean duplex stainless steel.

    PubMed

    Bassani, Paola; Breda, Marco; Brunelli, Katya; Mészáros, Istvan; Passaretti, Francesca; Zanellato, Michela; Calliari, Irene

    2013-08-01

    Duplex stainless steels (DSS) may be defined as a category of steels with a two-phase ferritic-austenitic microstructure, which combines good mechanical and corrosion properties. However, these steels can undergo significant microstructural modification as a consequence of either thermo-mechanical treatments (ferrite decomposition, which causes σ- and χ-phase formation and nitride precipitation) or plastic deformation at room temperature [austenite transformation into strain-induced martensite (SIM)]. These secondary phases noticeably affect the properties of DSS, and therefore are of huge industrial interest. In the present work, SIM formation was investigated in a 2101 lean DSS. The material was subjected to cold rolling at various degrees of deformation (from 10 to 80% thickness reduction) and the microstructure developed after plastic deformation was investigated by electron backscattered diffraction, X-ray diffraction measurements, and hardness and magnetic tests. It was observed that SIM formed as a consequence of deformations higher than ~20% and residual austenite was still observed at 80% of thickness reduction. Furthermore, a direct relationship was found between microstructure and magnetic properties.

  18. Fatigue strength of socket welded pipe joint

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Higuchi, Makoto; Hayashi, Makoto; Yamauchi, Takayoshi

    1995-12-01

    Fully reversed four point bending fatigue tests were carried out on small diameter socket welded joints made of carbon steels. Experimental parameters were pipe diameter, thicknesses of pipe and socket wall, throat depth and shape of fillet welds, slip-on and diametral gaps in the socket welding, lack of penetration at the root of fillet welds, and peening of fillet welds. In most cases a fatigue crack started from the root of the fillet, but in the case of higher stress amplitude, it tended to start from the toe of fillet. The standard socket welded joint for a pipe with amore » 50 mm nominal diameter showed a relatively low fatigue strength of 46 MPa in stress amplitude at the 10{sup 7} cycles failure life. This value corresponds to about 1/5 of that for the smoothed base metal specimens in axial fatigue. The fatigue strength decreased with increasing pipe diameter, and increased with increasing thickness of the pipe and socket wall. The effects of throat depth and shape of fillet welds on fatigue strength were not significant. Contrary to expectation, the fatigue strength of a socket welded joint without slip-on gap is Higher than that of the joint with a normal gap. A lack of penetration at the root deleteriously reduced fatigue strength, showing 14 MPa in stress amplitude at the 10{sup 7} cycles failure life for the 50 mm diameter socket joint.« less

  19. Study made of pneumatic high pressure piping materials /10,000 psi/

    NASA Technical Reports Server (NTRS)

    Loeb, M. B.; Smith, J. C.

    1967-01-01

    Evaluations of five types of steel for use in high pressure pneumatic piping systems include tests for impact strength, tensile and yield strengths, elongation and reduction in area, field weldability, and cost. One type, AISI 4615, was selected as most advantageous for extensive use in future flight vehicles.

  20. Long Duration Exposure Facility (LDEF) low-temperature Heat Pipe Experiment Package (HEPP) flight results

    NASA Technical Reports Server (NTRS)

    Mcintosh, Roy; Mccreight, Craig; Brennan, Patrick J.

    1992-01-01

    The Low Temperature Heat Pipe Flight Experiment (HEPP) is a fairly complicated thermal control experiment that was designed to evaluate the performance of two different low temperature ethane heat pipes and a n-Heptane Phase Change Material (PCM) canister. A total of 388 days of continuous operation with an axially grooved aluminum fixed conductance heat pipe of axially grooved stainless steel heat pipe diode was demonstrated before the EDS batteries lost power. The inability of the HEPP's radiator to cool below 190 K in flight prevented freezing of the PCM and the opportunity to conduct transport tests with the heat pipes. Post flight tests showed that the heat pipes and the PCM are still functioning. This paper presents a summary of the flight data analysis for the HEPP and its related support systems. Pre and post-flight thermal vacuum tests results are presented for the HEPP thermal control system along with individual heat pipe performance and PCM behavior. Appropriate SIG related systems data will also be included along with a 'lessons learned' summary.

  1. Aerial View Of The Site From The 40x80 Foot Wind Tunnel At Nasa Ames Research Center.

    NASA Image and Video Library

    1943-03-12

    (03/12/1943) Aerial view of the site from the 40x80 wind tunnel At NASA Ames Research Center. Site includes the 16 foot and 7x10 wind tunnels in the background. Building 200 also under construction. Framing for the drive fans of the 40x80 in scene.

  2. Thermal Aging Phenomena in Cast Duplex Stainless Steels

    DOE PAGES

    Byun, T. S.; Yang, Y.; Overman, N. R.; ...

    2015-11-12

    We used cast stainless steels (CASSs)for the large components of light water reactor (LWR) power plants such as primary coolant piping and pump casing. The thermal embrittlement of CASS components is one of the most serious concerns related to the extended-term operation of nuclear power plants. Many past researches have concluded that the formation of Cr-rich alpha-phase by Spinodal decomposition of delta-ferrite phase is the primary mechanism for the thermal embrittlement. Cracking mechanism in the thermally-embrittled duplex stainless steels consists of the formation of cleavage at ferrite and its propagation via separation of ferrite-austenite interphase. This article intends to providemore » an introductory overview on the thermal aging phenomena in LWR-relevant conditions. Firstly, the thermal aging effect on toughness is discussed in terms of the cause of embrittlement and influential parameters. Moreover, an approximate analysis of thermal reaction using Arrhenius equation was carried out to scope the aging temperatures for the accelerated aging experiments to simulate the 60 and 80 years of services. Further, an equilibrium precipitation calculation was performed for model CASS alloys using the CALPHAD program, and the results are used to describe the precipitation behaviors in duplex stainless steels. Our results are also to be used to guide an on-going research aiming to provide knowledge-based conclusive prediction for the integrity of the CASS components of LWR power plants during the service life extended up to and beyond 60 years.« less

  3. Thermal Aging Phenomena in Cast Duplex Stainless Steels

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Byun, T. S.; Yang, Y.; Overman, N. R.

    Cast stainless steels (CASSs) have been extensively used for the large components of light water reactor (LWR) power plants such as primary coolant piping and pump casing. The thermal embrittlement of CASS components is one of the most serious concerns related to the extended-term operation of nuclear power plants. Many past researches have concluded that the formation of Cr–rich α'-phase by Spinodal decomposition of δ-ferrite phase is the primary mechanism for the thermal embrittlement. Cracking mechanism in the thermally-embrittled duplex stainless steels consists of the formation of cleavage at ferrite and its propagation via separation of ferrite-austenite interphase. This articlemore » intends to provide an introductory overview on the thermal aging phenomena in LWR relevant conditions. Firstly, the thermal aging effect on toughness is discussed in terms of the cause of embrittlement and influential parameters. An approximate analysis of thermal reaction using Arrhenius equation was carried out to scope the aging temperatures for the accelerated aging experiments to simulate the 60 and 80 years of services. Further, equilibrium precipitation calculation was performed for model CASS alloys using the CALPHAD program and the results are used to describe the precipitation behaviors in duplex stainless steels. These results are also to be used to guide an on-going research aiming to provide knowledge-based conclusive prediction for the integrity of the CASS components of LWR power plants during the service life extended up to and beyond 60 years.« less

  4. Heat pipe fatigue test specimen: Metallurgical evaluation

    NASA Technical Reports Server (NTRS)

    Walak, Steven E.; Cronin, Michael J.; Grobstein, Toni

    1992-01-01

    An innovative creep/fatigue test was run to simulate the temperature, mechanical load, and sodium corrosion conditions expected in a heat pipe designed to supply thermal energy to a Stirling cycle power converter. A sodium-charged Inconel 718 heat pipe with a Nickel 200 screen wick was operated for 1090 hr at temperatures between 950 K (1250 F) and 1050 K (1430 F) while being subjected to creep and fatigue loads in a servo-hydraulic testing machine. After testing, the heat pipe was sectioned and examined using optical microscopy, scanning electron microscopy, and electron microprobe analysis with wavelength dispersive x-ray spectroscopy. The analysis concentrated on evaluating topographic, microstructural, and chemical changes in the sodium exposed surfaces of the heat pipe wall and wick. Surface changes in the evaporator, condenser, and adiabatic sections of the heat pipe were examined in an effort to correlate the changes with the expected sodium environment in the heat pipe. This report describes the setup, operating conditions, and analytical results of the sodium heat pipe fatigue test.

  5. Liquid metal micro heat pipes for space radiator applications

    NASA Technical Reports Server (NTRS)

    Gerner, F. M.; Henderson, H. T.

    1995-01-01

    Micromachining is a chemical means of etching three-dimensional structures, typically in single-crystalline silicon. These techniques are leading toward what is coming to be referred to as MEMS (micro electro mechanical systems), where in addition to the ordinary two dimensional (planar) microelectronics, it is possible to build three-dimensional micromotors, electrically-actuated microvalves, hydraulic systems, and much more on the same microchip. These techniques become possible because of differential etching rates of various crystallographic planes and materials used for semiconductor microfabrication. The University of Cincinnati group in collaboration with NASA Lewis formed micro heat pipes in silicon by the above techniques. Work is ongoing at a modest level, but several essential bonding and packaging techniques have been recently developed. Currently, we have constructed and filled water/silicon micro heat pipes. Preliminary thermal tests of arrays of 125 micro heat pipes etched in a 1 inch x 1 inch x 250 micron silicon wafer have been completed. These pipes are instrumented with extremely small P-N junctions to measure their effective conductivity and their maximum operating power. A relatively simple one-dimensional model has been developed in order to predict micro heat pipes' operating characteristics. This information can be used to optimize micro heat pipe design with respect to length, hydraulic diameter, and number of pipes. Work is progressing on the fabrication of liquid-metal micro heat pipes. In order to be compatible with liquid metal (sodium or potassium), the inside of the micro heat pipes will be coated with a refractory metal (such as tungsten, molybdenum, or titanium).

  6. Establishing a design procedure for buried steel-reinforced high-density polyethylene pipes : a field study, [technical summary].

    DOT National Transportation Integrated Search

    2015-11-01

    Several national standards and specification have been developed for design, installation, : and materials for precast concrete pipe, corrugated metal pipe, and HDPE pipes. However, : no national accepted installation standard or design method is ava...

  7. Tribological characterization of the drill pipe tool joints reconditioned by using welding technologies

    NASA Astrophysics Data System (ADS)

    Caltaru, M.; Badicioiu, M.; Ripeanu, R. G.; Dinita, A.; Minescu, M.; Laudacescu, E.

    2018-01-01

    Drill pipe is a seamless steel pipe with upset ends fitted with special threaded ends that are known as tool joints. During drilling operations, the wall thickness of the drill pipe and the outside diameter of the tool joints will be gradually reduced due to wear. The present research work investigate the possibility of reconditioning the drill pipe tool joints by hardbanding with a new metal-cored coppered flux cored wire, Cr-Mo alloyed, using the gas metal active welding process, taking into considerations two different hardbanding technologies, consisting in: hardbanding drill pipe tool joints after removing the old hardbanding material and surface reconstruction with a compensation material (case A), and hardbanding tool joint drill pipe, without removing the old hardbanding material (case B). The present paper brings forward the experimental researches regarding the tribological characterization of the reconditioned drill pipe tool joint by performing macroscopic analyses, metallographic analyses, Vickers hardness measurement, chemical composition measurement and wear tests conducted on ball on disk friction couples, in order to certify the quality of the hardbanding obtained by different technological approaches, to validate the optimum technology.

  8. Development and Application of Alloy TDJ-028 Seamless Pipe for Sour Oil and Gas Wells

    NASA Astrophysics Data System (ADS)

    Zhengzhou, Li; Cheng, Su; Baoshun, Wang; Peiming, Lu; Jie, Zhang

    The new frontier of oil and gas exploration will be with deep wells. Deep wells generally have higher temperature and pressure. Wells are categorized as being either sweet or sour. Sweet wells are only mildly corrosive, while sour wells are very corrosive. Thus, material selection is especially critical for deep sour wells which contain high concentration of hydrogen sulfide, carbon dioxide, elemental sulfur and chlorides. As these conditions become more severe, tubular material selection goes from stainless steel used for sweet wells, to duplex stainless steel, to nickel based alloy such as UNS N08028, UNS N06985 and UNS N08825, for sour well service. In this paper, Alloy TDJ-028 (UNS N08028) seamless pipe used for OCTG's has been developed using hot extrusion and cold worked processing. The mechanical tests show that the minimum yield strength grade of TDJ-028 alloy pipe was higher than 110KSI. The hardness, flattening and impact properties of the pipe and coupling stock were very good. Furthermore, the corrosion data is also presented to show the performance of the Alloy TDJ-028 in sour well environment using SCC, SSC tests. The properties of Alloy TDJ-028 pipe met the specification of ISO 13680 and NACE MR0175. So far, Jiuli has the ability to produce massive Alloy TDJ-028 OCTG's for sour oil and gas wells and the production diameter of the pipe can reach 8 inch.

  9. Monitoring of hot pipes at the power plant Neurath using guided waves

    NASA Astrophysics Data System (ADS)

    Weihnacht, Bianca; Klesse, Thomas; Neubeck, Robert; Schubert, Lars

    2013-04-01

    In order to reduce the CO2-emissions and to increase the energy efficiency, the operating temperatures of power plants will be increased up to 720°C. This demands for novel high-performance steels in the piping systems. Higher temperatures lead to a higher risk of damage and have a direct impact on the structure stability and the deposition structure. Adequately trusted results for the prediction of the residual service life of those high strength steels are not available so far. To overcome these problems the implementation of an online monitoring system in addition to periodic testing is needed. RWE operates the lignite power plant Neurath. All test and research activities have to be checked regarding their safety and have to be coordinated with the business operation of the plant. An extra bypass was established for this research and made the investigations independent from the power plant operating. In order to protect the actuators and sensors from the heat radiated from the pipe, waveguides were welded to the bypass. The data was evaluated regarding their dependencies on the environmental influences like temperature and correction algorithms were developed. Furthermore, damages were introduced into the pipe with diameters of 8 mm to 10 mm and successfully detected by the acoustic method.

  10. Post-Test Analysis of a 10-Year Sodium Heat Pipe Life Test

    NASA Technical Reports Server (NTRS)

    Rosenfeld, John H.; Locci, Ivan E.; Sanzi, James L.; Hull, David R.; Geng, Steven M.

    2011-01-01

    High-temperature heat pipes are being evaluated for use in energy conversion applications such as fuel cells, gas turbine re-combustors, Stirling cycle heat sources; and with the resurgence of space nuclear power both as reactor heat removal elements and as radiator elements. Long operating life and reliable performance are critical requirements for these applications. Accordingly, long-term materials compatibility is being evaluated through the use of high-temperature life test heat pipes. Thermacore, Inc., has carried out a sodium heat pipe 10-year life test to establish long-term operating reliability. Sodium heat pipes have demonstrated favorable materials compatibility and heat transport characteristics at high operating temperatures in air over long time periods. A representative one-tenth segment Stirling Space Power Converter heat pipe with an Inconel 718 envelope and a stainless steel screen wick has operated for over 87,000 hr (10 years) at nearly 700 C. These life test results have demonstrated the potential for high-temperature heat pipes to serve as reliable energy conversion system components for power applications that require long operating lifetime with high reliability. Detailed design specifications, operating history, and post-test analysis of the heat pipe and sodium working fluid are described. Lessons learned and future life test plans are also discussed.

  11. Ultrasonic Device Would Open Pipe Bombs

    NASA Technical Reports Server (NTRS)

    El-Raheb, Michael S.; Adams, Marc A.; Zwissler, James G.

    1991-01-01

    Piezoelectric ultrasonic transducer, energized by frequency generator and power supply, vibrates shell of pipe bomb while hardly disturbing explosive inner material. Frequency-control circuitry senses resonance in shell and holds generator at that frequency to induce fatigue cracking in threads of end cap. In addition to disarming bombs, ultrasonically induced fatigue may have other applications. In manufacturing, replaces some machining and cutting operations. In repair of equipment, cleanly and quickly disassembles corroded parts. In demolition of buildings used to dismember steel framework safely and controllably.

  12. Establishing a design procedure for buried steel-reinforced high density polyethylene (SRHDPE) pipes : [technical summary].

    DOT National Transportation Integrated Search

    2013-11-01

    Metal and plastic pipes have been used extensively as storm sewers and buried drainage structures in transportation projects. Metal pipes have high strength and stiffness but are susceptible to corrosion from wastewaters containing acid, and from agg...

  13. OTEC Cold Water Pipe-Platform Subsystem Dynamic Interaction Validation

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Varley, Robert; Halkyard, John; Johnson, Peter

    A commercial floating 100-megawatt (MW) ocean thermal energy conversion (OTEC) power plant will require a cold water pipe (CWP) with a diameter of 10-meter (m) and length of up to 1,000 m. The mass of the cold water pipe, including entrained water, can exceed the mass of the platform supporting it. The offshore industry uses software-modeling tools to develop platform and riser (pipe) designs to survive the offshore environment. These tools are typically validated by scale model tests in facilities able to replicate real at-sea meteorological and ocean (metocean) conditions to provide the understanding and confidence to proceed to finalmore » design and full-scale fabrication. However, today’s offshore platforms (similar to and usually larger than those needed for OTEC applications) incorporate risers (or pipes) with diameters well under one meter. Secondly, the preferred construction method for large diameter OTEC CWPs is the use of composite materials, primarily a form of fiber-reinforced plastic (FRP). The use of these material results in relatively low pipe stiffness and large strains compared to steel construction. These factors suggest the need for further validation of offshore industry software tools. The purpose of this project was to validate the ability to model numerically the dynamic interaction between a large cold water-filled fiberglass pipe and a floating OTEC platform excited by metocean weather conditions using measurements from a scale model tested in an ocean basin test facility.« less

  14. 75 FR 68324 - Certain Stainless Steel Butt-Weld Pipe Fittings From Japan, South Korea and Taiwan; Final Results...

    Federal Register 2010, 2011, 2012, 2013, 2014

    2010-11-05

    .... SUPPLEMENTARY INFORMATION: Scope of the Orders Japan The products covered by this order include certain... designing the piping system: (1) Corrosion of the piping system will occur if material other than stainless... designing the piping system: (1) Corrosion of the piping system will occur if material other than stainless...

  15. R&D and Applications of V-N Microalloyed Steels in China

    NASA Astrophysics Data System (ADS)

    Yang, Caifu

    This paper reviews the recent development of V-N microalloying technologies and its applications in HSLA steels in China. Enhanced-nitrogen in V-containing steels promotes precipitation of fine V(C,N) particles, and improves markedly precipitation strengthening effectiveness of V(C,N), therefore, there is a significant saving of V addition in a given strength requirement. V-N microalloying can be used effectively for ferrite grain refinement as well by the nucleation of intra-granular ferrite promoted by VN precipitates in Austenite in V-N steels. V-N microalloying process is a cost-effective way which has been widely used for high strength rebars, section steels, forging steels, seamless pipes, and CSP strip steels in China.

  16. Mechanical and Microstructural Effects of Thermal Aging on Cast Duplex Stainless Steels by Experiment and Finite Element Method

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Schwarm, Samuel C.; Mburu, Sarah N.; Kolli, Ratna P.

    Cast duplex stainless steel piping in light water nuclear reactors expe- rience thermal aging embrittlement during operational service. Interest in extending the operational life to 80 years requires an increased understanding of the microstructural evolution and corresponding changes in mechanical behavior. We analyze the evolution of the microstructure during thermal aging of cast CF-3 and CF-8 stainless steels using electron microscopy and atom probe tomography. The evolution of the mechanical properties is measured concurrently by mechanical methods such as tensile tests, Charpy V-notch tests, and instrumented nanoinden- tation. A microstructure-based finite element method model is developed and uti- lized inmore » conjunction with the characterization results in order to correlate the local stress-strain effects in the microstructure with the bulk measurements. This work is supported by the DOE Nuclear Energy University Programs (NEUP), contract number DE-NE0000724.« less

  17. Lockheed XFV-1 model in the 40x80 foot wind tunnel at NASA Ames Research Center

    NASA Image and Video Library

    1952-05-16

    Wide shot of 40x 80 wind tunnel settling chamber with Lockheed XFV-1 model. Project engineer Mark Kelly (not shown). Remote controlled model flown in the settling chamber of the 40x80 wind tunnel. Electric motors in the model, controlled the counter-rotating propellers to test vertical takeoff. Test no. 71

  18. Corrosion of Advanced Steels: Challenges in the Oil and Gas Industry

    NASA Astrophysics Data System (ADS)

    Mishra, Brajendra; Apelian, Diran

    Drill pipe steels are in contact with CO2 and H2S environments, depending on the oil and gas field. These steels have to be resistant to various in-service conditions including aggressive environments containing CO2, H2S, O2, and chlorides, in addition to static and dynamic mechanical stresses. In this respect stress corrosion cracking susceptibility of two grades of drill pipe steel in CO2 environment have been studied simulating the bottom hole oil and gas well conditions. SSRT results show that SCC susceptibility or loss of ductility changes with temperature and increasing temperature increases the loss of ductility. No FeCO3 is observed below 100 °C, and density of FeCO3 is higher in grip section than gauge length and this is due to strain disturbance of growth of iron carbonate crystals. Material selection for down hole in CO2 containing environments needs has been reviewed and probability of SCC occurrence in higher temperatures has been included.

  19. Reactor Materials Program - Baseline Material Property Handbook - Mechanical Properties of 1950's Vintage Stainless Steel Weldment Components, Task Number 89-23-A-1

    DOE Office of Scientific and Technical Information (OSTI.GOV)

    Stoner, K.J.

    1999-11-05

    The Process Water System (primary coolant) piping of the nuclear production reactors constructed in the 1950''s at Savannah River Site is comprised primarily of Type 304 stainless steel with Type 308 stainless steel weld filler. A program to measure the mechanical properties of archival PWS piping and weld materials (having approximately six years of service at temperatures between 25 and 100 degrees C) has been completed. The results from the mechanical testing has been synthesized to provide a mechanical properties database for structural analyses of the SRS piping.

  20. A high performance cocurrent-flow heat pipe for heat recovery applications

    NASA Technical Reports Server (NTRS)

    Saaski, E. W.; Hartl, J. C.

    1980-01-01

    By the introduction of a plate-and-tube separator assembly into a heat pipe vapor core, it has been demonstrated that axial transport capacity in reflux mode can be improved by up to a factor of 10. This improvement is largely the result of eliminating the countercurrent shear that commonly limits reflux heat pipe axial capacity. With benzene, axial heat fluxes up to 1800 W/sq cm were obtained in the temperature range 40 to 80 C, while heat flux densities up to 3000 W/sq cm were obtained with R-11 over the temperature range 40 to 80 C. These very high axial capacities compare favorably with liquid metal limits; the sonic limit for liquid sodium, for example, is 3000 W/sq cm at 657 C. Computational models developed for these cocurrent flow heat pipes agreed with experimental data within + or - 25%.

Some links on this page may take you to non-federal websites. Their policies may differ from this site.