Composition and microstructure of MTA and Aureoseal Plus: XRF, EDS, XRD and FESEM evaluation.

PubMed

Cianconi, L; Palopoli, P; Campanella, V; Mancini, M

2016-12-01

The aim of this study was to determine the chemical composition and the phases' microstructure of Aureoseal Plus (OGNA, Italy) and ProRoot MTA (Dentsply Tulsa Dental, USA) and to compare their characteristics. Study Design: Comparing Aureoseal Plus and ProRoot MTA microstructure by means of several analyses type. The chemical analysis of the two cements was assessed following the UNI EN ISO 196-2 norm. X-Ray fluorescence (XRF) was used to determine the element composition. The crystalline structure was analysed quantitatively using x-ray diffraction (XRD). Powders morphology was evaluated using a scanning electron microscope (SEM) with backscattering detectors, and a field emission scanning electron microscope (FESEM). Elemental analysis was performed by energy dispersive x-ray analysis (EDS). The semi-quantitative XRF analysis showed the presence of heavy metal oxides in both cements. The XRD spectra of the two cements reported the presence of dicalcium silicate, tricalcium silicate, tricalcium aluminate, tetracalcium aluminoferrite, bismuth oxide and gypsum. SEM analysis showed that ProRoot MTA powder is less coarse and more homogeneous than Aureoseal. Both powders are formed by particles of different shapes: round, prismatic and oblong. The EDS analysis showed that some ProRoot MTA particles, differently from Aureoseal, contain Ca, Si, Al and Fe. Oblong particles in ProRoot and Aureoseal are rich of bismuth. The strong interest in developing new Portland cement-based endodontic sealers will create materials with increased handling characteristics and physicochemical properties. A thorough investigation on two cement powders was carried out by using XRF, XRD, SEM and EDS analysis. To date there was a lack of studies on Aureoseal Plus. This cement is similar in composition to ProRoot MTA. Despite that it has distinctive elements that could improve its characteristics, resulting in a good alternative to MTA.

Combined In-Situ XRD and In-Situ XANES Studies on the Reduction Behavior of a Rhenium Promoted Cobalt Catalyst

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Nitin; Payzant, E Andrew; Jothimurugesan, K

2011-01-01

A 10% Co 4% Re/(2% Zr/SiO2) catalyst was prepared by co-impregnation using a silica support modified by 2% Zr. The catalyst was characterized by temperature programmed reduction (TPR), in situ XRD and in situ XANES analysis where it was simultaneously exposed to H2 using a temperature programmed ramp. The results showed the two step reduction of large crystalline Co3O4 with CoO as an intermediate. TPR results showed that the reduction of highly dispersed Co3O4 was facilitated by reduced rhenium by a H2-spillover mechanism. In situ XRD results showed the presence of both, Co-hcp and Co-fcc phases in the reduced catalystmore » at 400 C. However, the Co-hcp phase was more abundant, which is thought to be the more active phase as compared to the Co-fcc phase for CO hydrogenation. CO hydrogenation at 270 C and 5 bar pressure produces no detectable change in the phases during the time of experiment. In situ XANES results showed a decrease in the metallic cobalt in the presence of H2/CO, which can be attributed due to oxidation of the catalyst by reaction under these conditions.« less

Thermoluminescence (TL) properties and x-ray diffraction (XRD) analysis of high purity CaSO4:Dy TL material

NASA Astrophysics Data System (ADS)

Kamarudin, Nadira; Abdullah, Wan Saffiey Wan; Hamid, Muhammad Azmi Abdul; Dollah, Mohd Taufik

2014-09-01

This paper presents the characterization and TL properties of dysprosium (Dy) doped calcium sulfate (CaSO4) TL material produced by co-precipitation technique with 0.5mol% concentration of dopant. The morphology of the produced TL material was studied using scanning electron microscope (SEM) and the micrograph shows that rectangular parallelepiped shaped crystal with the average of 150 μm in length were produced. The crystallinity of the produced powder was studied using x-ray powder diffraction (XRD). The XRD spectra show that the TL material produced is high purity anhydrite CaSO4 with average crystallite size of 74 nm with orthorhombic crystal system. The TL behavior of produced CaSO4:Dy was studied using a TLD reader after exposure to gamma ray by Co60 source with the doses of 1,5 and 10 Gy. The glow curve shows linear response with glow peak around 230°C which is desired development in the field of radiation dosimetry.

Remote In-Situ Quantitative Mineralogical Analysis Using XRD/XRF

NASA Technical Reports Server (NTRS)

Blake, D. F.; Bish, D.; Vaniman, D.; Chipera, S.; Sarrazin, P.; Collins, S. A.; Elliott, S. T.

2001-01-01

X-Ray Diffraction (XRD) is the most direct and accurate method for determining mineralogy. The CHEMIN XRD/XRF instrument has shown promising results on a variety of mineral and rock samples. Additional information is contained in the original extended abstract.

FTIR, XRD and DSC studies of nanochitosan, cellulose acetate and polyethylene glycol blend ultrafiltration membranes.

PubMed

Vinodhini, P Angelin; K, Sangeetha; Thandapani, Gomathi; P N, Sudha; Jayachandran, Venkatesan; Sukumaran, Anil

2017-11-01

In the present work, a series of novel nanochitosan/cellulose acetate/polyethylene glycol (NCS/CA/PEG) blend flat sheet membranes were fabricated in different ratios (1:1:1, 1:1:2, 2:1:1, 2:1:2, 1:2:1, 2:2:1) in a polar solvent of N,N'-dimethylformamide (DMF) using the most popular phase inversion method. Nanochitosan was prepared by the ionotropic gelation method and its average particle size has been analyzed using Dynamic Light Scattering (DLS) method. The effect of blending of the three polymers was investigated using FTIR and XRD studies. FTIR results confirmed the formation of well-blended membranes and the XRD analysis revealed enhanced amorphous nature of the membrane ratio 2:1:2. DSC study was conducted to find out the thermal behavior of the blend membranes and the results clearly indicated good thermal stability and single glass transition temperature (T g ) of all the prepared membranes. Asymmetric nature and rough surface morphology was confirmed using SEM analysis. From the results it was evident that the blending of the polymers with higher concentration of nanochitosan can alter the nature of the resulting membranes to a greater extent and thus amorphous membranes were obtained with good miscibility and compatibility. Copyright © 2017 Elsevier B.V. All rights reserved.

[Research on characteristics of soil clay mineral evolution in paddy field and dry land by XRD spectrum].

PubMed

Zhang, Zhi-dan; Li, Qiao; Luo, Xiang-li; Jiang, Hai-chao; Zheng, Qing-fu; Zhao, Lan-po; Wang, Ji-hong

2014-08-01

The present paper took the typical saline-alkali soil in Jilin province as study object, and determinated the soil clay mineral composition characteristics of soil in paddy field and dry land. Then XRD spectrum was used to analyze the evolutionary mechanism of clay mineral in the two kinds of soil. The results showed that the physical and chemical properties of soil in paddy field were better than those in dry land, and paddy field would promote the weathering of mineral particles in saline-alkali soil and enhance the silt content. Paddy field soil showed a strong potassium-removal process, with a higher degree of clay mineral hydration and lower degree of illite crystallinity. Analysis of XRD spectrum showed that the clay mineral composition was similar in two kinds of soil, while the intensity and position of diffraction peak showed difference. The evolution process of clay mineral in dry land was S/I mixture-->vermiculite, while in paddy field it was S/I mixture-->vermiculite-->kaolinite. One kind of hydroxylated 'chlorite' mineral would appear in saline-alkali soil in long-term cultivated paddy field. Taking into account that the physical and chemical properties of soil in paddy field were better then those in dry land, we could know that paddy field could help much improve soil structure, cultivate high-fertility soil and improve saline-alkali soil. This paper used XRD spectrum to determine the characteristics of clay minerals comprehensively, and analyzed two'kinds of land use comparatively, and was a new perspective of soil minerals study.

Mineralogical composition of the meteorite El Pozo (Mexico): a Raman, infrared and XRD study.

PubMed

Ostrooumov, Mikhail; Hernández-Bernal, Maria del Sol

2011-12-01

The Raman (RMP), infrared (IR) and XRD analysis have been applied to the examination of mineralogical composition of El Pozo meteorite (an ordinary chondrite L5 type; village Valle of Allende, founded in State of Chihuahua, Mexico: 26°56'N and 105°24'W, 1998). RMP measurements in the range of 100-3500 cm(-1) revealed principal characteristic bands of the major minerals: olivine, two polymorph modifications of pyroxene (OPx and CPx) and plagioclase. Some bands of the minor minerals (hematite and goethite) were also identified. All these minerals were clearly distinguished using IR and XRD techniques. XRD technique has shown the presence of some metallic phases such as kamacite and taenite as well as troilite and chromite. These minerals do not have characteristic Raman spectra because Fe-Ni metals have no active modes for Raman spectroscopy and troilite is a weak Raman scatterer. Raman mapping microspectroscopy was a key part in the investigation of El Pozo meteorite's spatial distribution of the main minerals because these samples are structurally and chemically complex and heterogeneous. The mineral mapping by Raman spectroscopy has provided information for a certain spatial region on which a spatial distribution coexists of the three typical mineral assemblages: olivine; olivine+orthopyroxene; and orthopyroxene. Copyright © 2011 Elsevier B.V. All rights reserved.

Multivariate analysis of DSC-XRD simultaneous measurement data: a study of multistage crystalline structure changes in a linear poly(ethylene imine) thin film.

PubMed

Kakuda, Hiroyuki; Okada, Tetsuo; Otsuka, Makoto; Katsumoto, Yukiteru; Hasegawa, Takeshi

2009-01-01

A multivariate analytical technique has been applied to the analysis of simultaneous measurement data from differential scanning calorimetry (DSC) and X-ray diffraction (XRD) in order to study thermal changes in crystalline structure of a linear poly(ethylene imine) (LPEI) film. A large number of XRD patterns generated from the simultaneous measurements were subjected to an augmented alternative least-squares (ALS) regression analysis, and the XRD patterns were readily decomposed into chemically independent XRD patterns and their thermal profiles were also obtained at the same time. The decomposed XRD patterns and the profiles were useful in discussing the minute peaks in the DSC. The analytical results revealed the following changes of polymorphisms in detail: An LPEI film prepared by casting an aqueous solution was composed of sesquihydrate and hemihydrate crystals. The sesquihydrate one was lost at an early stage of heating, and the film changed into an amorphous state. Once the sesquihydrate was lost by heating, it was not recovered even when it was cooled back to room temperature. When the sample was heated again, structural changes were found between the hemihydrate and the amorphous components. In this manner, the simultaneous DSC-XRD measurements combined with ALS analysis proved to be powerful for obtaining a better understanding of the thermally induced changes of the crystalline structure in a polymer film.

XRD and EBSD analysis of anisotropic microstructure development in cold rolled F138 stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

De Vincentis, N.S., E-mail: devincentis@ifir-conic

The microstructural characteristics of deformation-processed materials highly influence their mechanical properties. For a complete characterization of a microstructure both local and global information must be gathered, which requires the combination of different analysis techniques. X-ray and Electron Backscatter Diffraction were used in the present paper to characterize the deformation induced in a cold rolled F138 austenitic stainless steel sample. The results obtained using laboratory and synchrotron X-ray sources were compared and combined with EBSD quantitative results, allowing the global and local characterization and orientation dependence of the deformation microstructure. A particular behavior was observed in the XRD data corresponding tomore » the planes with < 220 >∥ ND, likely due to a smaller amount of defects accumulated in the crystals with that particular orientation. EBSD was used to separate the scans data into partitions and to calculate misorientation variables and parameters, showing that this behavior can be attributed to a combination of larger grain sizes, lower local boundary misorientations and dislocation densities for crystals having < 220 >∥ ND. Several conclusions, of general validity for the evaluation of microstructure anisotropy, can be extracted from the results. - Highlights: •Combined XRD and EBSD for studying microstructure gave a superb insight on anisotropic accumulation of defects. •W-H and CMWP methods were applied for checking consistency of results. •XRD showed that a smaller accumulation of defects occurred in crystals with < 220 >∥ ND. •High brilliance X-ray beam allowed to study the anisotropy of defect accumulation.« less

The high - low-p clinoenstatite transition: in situ xrd and ultrasonic study

NASA Astrophysics Data System (ADS)

Müller, H. J.; Wunder, B.; Lathe, C.; Schilling, F. R.

2003-04-01

Using single-crystal X-ray diffraction analyses in a diamond anvil cell Angel et al. (1992) published the transformation of MgSiO_3 from LCEn to a C2/c-polymorph (HCEn) at around 5.5 - 8.0 GPa and room-T (RT)conditions. This LCEn - HCEn-transition is not quenchable. However, the knowledge of the exact phase boundary positions for the MgSiO_3-transitions is essential as pyroxene is an important component of the Earth's mantle and will significantly influence elastic properties (e.g. v_p, v_s) of the mantle. We determined the HCEn - LCEn-transition by in-situ XRD experiments under high P, T using the multi-anvil appar atus MAX80 at the synchrotron facility HASYLAB, Hamburg. Our preliminary results only represent the minimum P-conditions of the HCEn - LCEn phase boundary, which is approximated by equation P (GPa) = 0.0021T (/C) + 6.06. Nevertheless, our results are in good agreement to data published by Angel & Hugh-Jones (1994). The invariant point defined by the intersection of the HCEn - LCEn equilibrium determined within this study and the OEn - LCEn reaction after Angel &Hugh-Jones (1994) lies at about 7.9 GPa and 875/C. This is in contrast to earlier experimental results of Kanzaki (1991) and Ulmer &Stalder (2001). The samples for the ultrasonic interferometry experiments were prepared by hot-isostatic pressing also using the MAX80. Adjacent XRD ruled out any phase transition during the hip-process. For the ultrasonic measurements one of the six anvils of MAX80 were exchanged by an anvil equipped with lithium niobate p- and s-wave transducers of 33.3 MHz natural frequency (Mueller et al., 2002). Corresponding to the XRD experiments HCEn was formed by increasing the pressure at RT. The velocities of elastic compressional and shear waves were measured under in situ conditions using the classical digital sweep technique. After the phase transition to LCEn as a result of rising the temperature at given pressure the measurements were repeated. The newly developed

Quantitative XRD analysis of {110} twin density in biotic aragonites.

PubMed

Suzuki, Michio; Kim, Hyejin; Mukai, Hiroki; Nagasawa, Hiromichi; Kogure, Toshihiro

2012-12-01

{110} Twin densities in biotic aragonite have been estimated quantitatively from the peak widths of specific reflections in powder X-ray diffraction (XRD) patterns, as well as direct confirmation of the twins using transmission electron microscopy (TEM). Influence of the twin density on the peak widths in the XRD pattern was simulated using DIFFaX program, regarding (110) twin as interstratification of two types of aragonite unit layers with mirrored relationship. The simulation suggested that the twin density can be estimated from the difference of the peak widths between 111 and 021, or between 221 and 211 reflections. Biotic aragonite in the crossed-lamellar microstructure (three species) and nacreous microstructure (four species) of molluscan shells, fish otoliths (two species), and a coral were investigated. The XRD analyses indicated that aragonite crystals in the crossed-lamellar microstructure of the three species contain high density of the twins, which is consistent with the TEM examination. On the other hand, aragonite in the nacre of the four species showed almost no difference of the peak widths between the paired reflections, indicating low twin densities. The results for the fish otoliths were varied between the species. Such variation of the twin density in biotic aragonites may reflect different schemes of crystal growth in biomineralization. Copyright © 2012 Elsevier Inc. All rights reserved.

Ultrasonic-assisted synthesis of nano lead(II) coordination polymer as precursors for preparation of lead(II) oxide nano-structures: Thermal, optical properties and XRD studies.

PubMed

Ghavidelaghdam, Elham; Shahverdizadeh, Gholam Hossein; Motameni Tabatabai, Javad; Mirtamizdoust, Babak

2018-04-01

Nano structure of a lead (II) coordination polymer [Pb 2 (C 2 Cl 3 O 2 ) 2 (NO 3 ) 2 (C l2 H 8 N 2 ) 2 ] n (1), has been synthesized by a sonochemical method in different concentrations. The nano particles were characterized by scanning electron microscopy (SEM) X-ray powder diffraction (XRD), FT-IR spectroscopy and elemental analyses. The thermal stability of nano structure is closely investigated via thermal gravimetric (TGA), and compared with crystalline structure. The compounds are then heated to 600 °C to produce PbO nano particles. The resulting PbO is characterized through XRD and SEM analyses. Concentration of initial reagents effects on size and morphology of nano-structured compound 1 have been studied and show that low concentrations of initial reagents decreased particles size and leaded to uniform nano particles morphology. The photoluminescence properties of the prepared compound, as crystalline and as nanoparticles, have been investigated. The result showed a good correlation between the size and emission wavelength. Copyright © 2017. Published by Elsevier B.V.

[Identification of Dens Draconis and Os Draconis by XRD method].

PubMed

Chen, Guang-Yun; Wu, Qi-Nan; Shen, Bei; Chen, Rong

2012-04-01

To establish an XRD method for evaluating the quality of Os Draconis and Dens Draconis and applying in judgement of the counterfeit. Dens Draconis, Os Draconis and the counterfeit of Os Draconis were analyzed by XRD. Their diffraction patterns were clustered analysis and evaluated their similarity degree. Established the analytical method of Dens Draconis and Os Draconis basing the features fingerprint information of the 10 common peaks by XRD pattern. Obtained the XRD pattern of the counterfeit of Os Draconis. The similarity degree of separate sources of Dens Draconis was high,while the similarity degree of separate sources of Os Draconis was significant different from each other. This method can be used for identification and evaluation of Os Draconis and Dens Draconis. It also can be used for identification the counterfeit of Os Draconis effectively.

Mössbauer and XRD study of novel quaternary Sn-Fe-Co-Ni electroplated alloy

NASA Astrophysics Data System (ADS)

Kuzmann, E.; Sziráki, L.; Stichleutner, S.; Homonnay, Z.; Lak, G. B.; El-Sharif, M.; Chisholm, C. U.

2017-11-01

Constant current electrochemical deposition technique was used to obtain quaternary alloys of Sn-Fe-Co-Ni from a gluconate electrolyte, which to date have not been reported in the literature. For the characterization of electroplated alloys, 57Fe and 119Sn Conversion Electron Mössbauer Spectroscopy (CEMS), XRD and SEM/EDAX were used. XRD revealed the amorphous character of the novel Sn-Fe-Co-Ni electrodeposited alloys. 57Fe Mössbauer spectrum of quaternary deposit with composition of 37.0 at% Sn, 38.8 at% Fe, 16.8 at% Co and 7.4 at% Ni displayed a magnetically split sextet (B = 28.9T) with broad lines typical of iron bearing ferromagnetic amorphous alloys. Magnetically split 119Sn spectra reflecting a transferred hyperfine field (B = 2.3T) were also observed. New quaternary Sn-Fe-Co-Ni alloys were successfully prepared.

Synchronizing flash-melting in a diamond cell with synchrotron X ray diffraction (XRD)

NASA Astrophysics Data System (ADS)

Karandikar, Amol; Boehler, Reinhard; Meng, Yue; Rod, Eric; Shen, Guoyin

2013-06-01

The major challenges in measuring melting temperatures in laser heated diamond cells are sample instability, thermal runaway and chemical reactions. To circumvent these problems, we developed a ``flash heating'' method using a modulated CW fiber laser and fast X ray detection capability at APS (Pilatus 1M detector). As an example, Pt spheres of 5 micron diameter were loaded in a single crystal sapphire encapsulation in the diamond cell at 65 GPa and heated in a single flash heating event for 20 ms to reach a desired temperature. A CCD spectrometer and the Pilatus were synchronized to measure the temperature and the XRD signal, respectively, when the sample reached the thermal steady state. Each successive flash heating was done at a higher temperature. The integrated XRD pattern, collected during and after (300 K) each heating, showed no chemical reaction up to 3639 K, the highest temperature reached in the experiment. Pt111 and 200 peak intensity variation showed gradual recrystalization and complete diminishing at about 3600 K, indicating melting. Thus, synchronized flash heating with novel sample encapsulation circumvents previous notorious problems and enables accurate melting temperature measurement in the diamond cell using synchrotron XRD probe. Affiliation 2: Geowissenschaeften, Goethe-Universitaet, Altenhoeferallee 1, D-60438 Frankfurt a.M., Germany.

Leonardo da Vinci's drapery studies: characterization of lead white pigments by µ-XRD and 2D scanning XRF

NASA Astrophysics Data System (ADS)

Gonzalez, Victor; Calligaro, Thomas; Pichon, Laurent; Wallez, Gilles; Mottin, Bruno

2015-11-01

This work focuses on the composition and microstructure of the lead white pigment employed in a set of paintworks, using a combination of µ-XRD and 2D scanning XRF, directly applied on five drapery studies attributed to Leonardo da Vinci (1452-1519) and conserved in the Département des Arts Graphiques, Musée du Louvre and in the Musée des Beaux- Arts de Rennes. Trace elements present in the composition as well as in the lead white highlights were imaged by 2D scanning XRF. Mineral phases were determined in a fully noninvasive way using a special µ-XRD diffractometer. Phase proportions were estimated by Rietveld refinement. The analytical results obtained will contribute to differentiate lead white qualities and to highlight the artist's technique.

Some critical aspects of FT-IR, TGA, powder XRD, EDAX and SEM studies of calcium oxalate urinary calculi.

PubMed

Joshi, Vimal S; Vasant, Sonal R; Bhatt, J G; Joshi, Mihir J

2014-06-01

Urinary calculi constitute one of the oldest afflictions of humans as well as animals, which are occurring globally. The calculi vary in shape, size and composition, which influence their clinical course. They are usually of the mixed-type with varying percentages of the ingredients. In medical management of urinary calculi, either the nature of calculi is to be known or the exact composition of calculi is required. In the present study, two selected calculi were recovered after surgery from two different patients for detailed examination and investigated by using Fourier-Transform infrared spectroscopy (FT-IR), thermo-gravimetric analysis (TGA), powder X-ray diffraction (XRD), scanning electron microscopy and energy dispersive analysis of X-rays (EDAX) techniques. The study demonstrated that the nature of urinary calculi and presence of major phase in mixed calculi could be identified by FT-IR, TGA and powder XRD, however, the exact content of various elements could be found by EDAX only.

Thermoluminescence (TL) properties and x-ray diffraction (XRD) analysis of high purity CaSO{sub 4}:Dy TL material

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kamarudin, Nadira; Abdullah, Wan Saffiey Wan; Dollah, Mohd Taufik

2014-09-03

This paper presents the characterization and TL properties of dysprosium (Dy) doped calcium sulfate (CaSO{sub 4}) TL material produced by co-precipitation technique with 0.5mol% concentration of dopant. The morphology of the produced TL material was studied using scanning electron microscope (SEM) and the micrograph shows that rectangular parallelepiped shaped crystal with the average of 150 μm in length were produced. The crystallinity of the produced powder was studied using x-ray powder diffraction (XRD). The XRD spectra show that the TL material produced is high purity anhydrite CaSO{sub 4} with average crystallite size of 74 nm with orthorhombic crystal system. Themore » TL behavior of produced CaSO{sub 4}:Dy was studied using a TLD reader after exposure to gamma ray by Co{sup 60} source with the doses of 1,5 and 10 Gy. The glow curve shows linear response with glow peak around 230°C which is desired development in the field of radiation dosimetry.« less

Mineralogical Composition of the Mexican Ordinary Chondrite Type Meteorite: A Raman, Infrared and XRD Study

NASA Astrophysics Data System (ADS)

Ostrooumov, M.

2016-08-01

The Raman microprobe (RMP), infrared (IR) and XRD analysis have been applied to the examination of mineralogical composition of seven mexican meteorites: Aldama, Cosina, El Pozo, Escalon, Nuevo Mercurio,Pacula, Zapotitlan Salinas.

Spectral studies of 2-pyrazoline derivatives: structural elucidation through single crystal XRD and DFT calculations.

PubMed

Chinnaraja, D; Rajalakshmi, R; Srinivasan, T; Velmurugan, D; Jayabharathi, J

2014-04-24

A series of biologically active N-thiocarbamoyl pyrazoline derivatives have been synthesized using anhydrous potassium carbonate as the catalyst. All the synthesized compounds were characterized by FT-IR, (1)H NMR, (13)C NMR spectral studies, LCMS, CHN Analysis and X-ray diffraction analysis (compound 7). In order to supplement the XRD parameters, molecular modelling was carried out by Gaussian 03W. From the optimized structure, the energy, dipolemoment and HOMO-LUMO energies of all the systems were calculated. Copyright © 2014 Elsevier B.V. All rights reserved.

Different β-alanine dimeric forms in trifluoromethanesulfonic acid salts. XRD and vibrational studies.

PubMed

Wołoszyn, Łukasz; Ilczyszyn, Maria M

2018-03-15

Two new crystalline salts: β-alaninium trifluoromethanesulfonate (β-AlaOTf) and bis(β-alanine) trifluoromethanesulfonate (β-2AlaOTf) were obtained. The former one contains diprotonated β-alanine dimer, the latter one monoprotonated β-alanine dimer. Both compounds were studied by single crystal XRD, vibrational (IR and Raman) spectroscopy and calorimetric method. The quantum-mechanical calculations (DFT/B3LYP/6-311++G(2d,2p)) for the diprotonated dimer were carried out. The β-AlaOTf salt crystallizes in the P1¯ space group of triclinic system (Z=2), the β-2AlaOTf in the P2 1 /m space group of monoclinic system (Z=2). The vibrational data for the studied compounds are discussed in relation to their crystal structure, and provide insight into the character of hydrogen bonds and β-alanine protonation. The studied crystals do not exhibit phase transitions in the solid state. Copyright © 2017 Elsevier B.V. All rights reserved.

Novel Sample-handling Approach for XRD Analysis with Minimal Sample Preparation

NASA Technical Reports Server (NTRS)

Sarrazin, P.; Chipera, S.; Bish, D.; Blake, D.; Feldman, S.; Vaniman, D.; Bryson, C.

2004-01-01

Sample preparation and sample handling are among the most critical operations associated with X-ray diffraction (XRD) analysis. These operations require attention in a laboratory environment, but they become a major constraint in the deployment of XRD instruments for robotic planetary exploration. We are developing a novel sample handling system that dramatically relaxes the constraints on sample preparation by allowing characterization of coarse-grained material that would normally be impossible to analyze with conventional powder-XRD techniques.

Powder XRD, TEM, FTIR and thermal studies of strontium tartrate nano particles

NASA Astrophysics Data System (ADS)

Lathiya, U. M.; Jethva, H. O.; Joshi, M. J.; Vyas, P. M.

2017-05-01

Strontium tartrate finds several applications, e.g., as non-linear optical and dielectric material, in tracer composition and ammunition unit, in treating structural integrity of bone. The growth of single crystals of strontium tartrate in silica gel has been widely reported. In the present study, strontium tartrate nano particles were synthesized by wet chemical method using strontium chloride, tartaric acid and sodium meta-silicate solutions in the presence of Triton X -100 surfactant. It was found that the presence of sodium meta-silicate facilitated the reaction for strontium tartrate product. The powder XRD study of strontium tartrate nano-particles suggested monoclinic crystal system and the average crystallite size was found to be 40 nm determined by applying Scherrer's formula. The TEM analysis indicated that the nano particles were spherical in nature. The FTIR spectrum confirmed the presence of various functional groups such as O-H,C-H, and C=O stretching mode. The thermal analysis was carried out by using TGA and DTA studies. The nano-particles were found to be stable up to 175°C and then decomposed through various stages. The results are compared with the bulk crystalline material available in the literature.

Synthesis of metal complexes involving Schiff base ligand with methylenedioxy moiety: spectral, thermal, XRD and antimicrobial studies.

PubMed

Sundararajan, M L; Jeyakumar, T; Anandakumaran, J; Karpanai Selvan, B

2014-10-15

Metal complexes of Zn(II), Cd(II), Ni(II), Cu(II), Fe(III), Co(II), Mn(II) Hg(II), and Ag(I) have been synthesized from Schiff base ligand, prepared by the condensation of 3,4-(methylenedioxy)aniline and 5-bromo salicylaldehyde. All the compounds have been characterized by using elemental analysis, molar conductance, FT-IR, UV-Vis, (1)H NMR, (13)C NMR, mass spectra, powder XRD and thermal analysis (TG/DTA) technique. The elemental analysis suggests the stoichiometry to be 1:1 (metal:ligand). The FT-IR, (1)H NMR, (13)C NMR and UV-Vis spectral data suggest that the ligand coordinate to the metal atom by imino nitrogen and phenolic oxygen as bidentate manner. Mass spectral data further support the molecular mass of the compounds and their structure. Powder XRD indicates the crystalline state and morphology of the ligand and its metal complexes. The thermal behaviors of the complexes prove the presence of lattice as well as coordinated water molecules in the complexes. Melting point supports the thermal stability of all the compounds. The in vitro antimicrobial effects of the synthesized compounds were tested against five bacterial and three fungal species by well diffusion method. Antioxidant activities have also been performed for all the compounds. Metal complexes show more biological activity than the Schiff base. Copyright © 2014 Elsevier B.V. All rights reserved.

XRD, SEM and infrared study into the intercalation of sodium hexadecyl sulfate (SHS) into hydrocalumite.

PubMed

Zhang, Ping; Wang, Tianqi; Zhang, Longlong; Wu, Daishe; Frost, Ray L

2015-12-05

Hydrocalumite (CaAl-LDH-Cl) interacted with a natural anionic surfactant, sodium hexadecyl sulfate (SHS), was performed using an intercalation method. To understand the intercalation behavior and characterize the resulting products, powder X-ray diffraction (XRD), scan electron microscopy (SEM) and mid-infrared (MIR) spectroscopy combined with near-infrared (NIR) spectroscopy technique were used. The XRD analysis indicated that SHS was intercalated into CaAl-LDH-Cl successfully, resulting in an expansion of the interlayer (from 0.78 nm to 2.74 nm). The bands of C-H stretching vibrations of SHS were observed in the near-infrared spectra, which indicated that the resulting products were indeed CaAl-LDH-SHS. In addition, the bands of water stretching vibrations and OH groups shifted to higher wavenumbers when SHS was intercalated into CaAl-LDH-Cl interlayer space. Copyright © 2015 Elsevier B.V. All rights reserved.

Dynamic XRD, Shock and Static Compression of CaF2

NASA Astrophysics Data System (ADS)

Kalita, Patricia; Specht, Paul; Root, Seth; Sinclair, Nicholas; Schuman, Adam; White, Melanie; Cornelius, Andrew; Smith, Jesse; Sinogeikin, Stanislav

2017-06-01

The high-pressure behavior of CaF2 is probed with x-ray diffraction (XRD) combined with both dynamic compression, using a two-stage light gas gun, and static compression, using diamond anvil cells. We use XRD to follow the unfolding of a shock-driven, fluorite to cotunnite phase transition, on the timescale of nanoseconds. The dynamic behavior of CaF2 under shock loading is contrasted with that under static compression. This work leverages experimental capabilities at the Advanced Photon Source: dynamic XRD and shock experiments at the Dynamic Compression Sector, as well as XRD and static compression in diamond anvil cell at the High-Pressure Collaborative Access Team. These experiments and cross-platform comparisons, open the door to an unprecedented understanding of equations of state and phase transitions at the microstructural level and at different time scales and will ultimately improve our capability to simulate the behavior of materials at extreme conditions. Sandia National Laboratories is a multi-mission laboratory managed and operated by Sandia Corporation, a wholly owned subsidiary of Lockheed Martin Corporation, for the U.S. Department of Energy's National Nuclear Security Administration under contract DE-AC04-94AL85000.

Crystal imperfection studies of pure and silicon substituted hydroxyapatite using Raman and XRD.

PubMed

Zou, Shuo; Huang, Jie; Best, Serena; Bonfield, William

2005-12-01

Hydroxyapatite (HA) is important in biomedical applications because of its chemical similarity to the mineral content of bone and its consequent bioactivity. Silicon substitution into the hydroxyapatite crystal lattice was found to enhance its bioactivity both in vitro and in vivo [1, 2]. However, the mechanism for the enhancement is still not well understood. In this paper, the crystal imperfections introduced by silicon substitution were studied using XRD and Raman spectroscopy. It was found that silicon substitution did not introduce microstrain, but deceased the crystal size in the hk0 direction. Three new vibration modes and peak broadening were observed in Raman spectra following silicon incorporation. The imperfections introduced by silicon substitution may play a role in enhancing bioactivity. A phenomenological relationship between the width of the PO4 v1 peak and crystal size was established.

Structural investigations in helium charged titanium films using grazing incidence XRD and EXAFS spectroscopy

NASA Astrophysics Data System (ADS)

Wan, Chubin; Zhou, Xiaosong; Wang, Yuting; Li, Shina; Ju, Xin; Peng, Shuming

2014-01-01

The crystal structure and local atomic arrangements surrounding Ti atoms were determined for He-charged hexagonal close-packed (hcp) Ti films and measured at glancing angles by synchrotron radiation X-ray diffraction (XRD) and extended X-ray absorption fine structure (EXAFS) spectroscopy, respectively. The charged specimens were prepared by direct current magnetron sputtering with a He/Ar mixture. He atoms with a relatively medium concentration (He/Ti atomic ratio as high as 17 at.%) were incorporated evenly in the deposited films. XRD results showed the changes in the peak intensities in Ti films with different He contents. EXAFS Fourier Transform analysis indicated that the average Ti-Ti distance decreased significantly, and proved the existence of phase transition.

MultiLaue: A Technique to Extract d-spacings from Laue XRD

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gainsforth, Zack; Marcus, Matthew A.; Tamura, Nobumichi

We present that broad spectrum X-ray Diffraction (XRD) is named Laue after Max von Laue, and is the original XRD technique. Today, monochromatic XRD is more common because Bragg's equation allows determination of d-spacings where Laue does not. Laue still remains in use for single crystal systems because it can be used to make very accurate unit cell determinations as well as for strain and orientation mapping. Lastly, a Laue technique which could provide unambiguous determination of lattice spacings, a la Bragg's equation would be a huge leap forward, especially for multiphase samples such as meteorites, interplanetary dust particles andmore » some geological specimens.« less

MultiLaue: A Technique to Extract d-spacings from Laue XRD

DOE PAGES

Gainsforth, Zack; Marcus, Matthew A.; Tamura, Nobumichi; ...

2016-07-25

We present that broad spectrum X-ray Diffraction (XRD) is named Laue after Max von Laue, and is the original XRD technique. Today, monochromatic XRD is more common because Bragg's equation allows determination of d-spacings where Laue does not. Laue still remains in use for single crystal systems because it can be used to make very accurate unit cell determinations as well as for strain and orientation mapping. Lastly, a Laue technique which could provide unambiguous determination of lattice spacings, a la Bragg's equation would be a huge leap forward, especially for multiphase samples such as meteorites, interplanetary dust particles andmore » some geological specimens.« less

Comparative investigation of Fourier transform infrared (FT-IR) spectroscopy and X-ray diffraction (XRD) in the determination of cotton fiber crystallinity.

PubMed

Liu, Yongliang; Thibodeaux, Devron; Gamble, Gary; Bauer, Philip; VanDerveer, Don

2012-08-01

Despite considerable efforts in developing curve-fitting protocols to evaluate the crystallinity index (CI) from X-ray diffraction (XRD) measurements, in its present state XRD can only provide a qualitative or semi-quantitative assessment of the amounts of crystalline or amorphous fraction in a sample. The greatest barrier to establishing quantitative XRD is the lack of appropriate cellulose standards, which are needed to calibrate the XRD measurements. In practice, samples with known CI are very difficult to prepare or determine. In a previous study, we reported the development of a simple algorithm for determining fiber crystallinity information from Fourier transform infrared (FT-IR) spectroscopy. Hence, in this study we not only compared the fiber crystallinity information between FT-IR and XRD measurements, by developing a simple XRD algorithm in place of a time-consuming and subjective curve-fitting process, but we also suggested a direct way of determining cotton cellulose CI by calibrating XRD with the use of CI(IR) as references.

XRD, TEM, and thermal analysis of Arizona Ca-montmorillonites modified with didodecyldimethylammonium bromide.

PubMed

Sun, Zhiming; Park, Yuri; Zheng, Shuilin; Ayoko, Godwin A; Frost, Ray L

2013-10-15

An Arizona SAz-2 calcium montmorillonite was modified by a typical dialkyl cationic surfactant (didodecyldimethylammonium bromide, abbreviated to DDDMA) through direct ion exchange. The obtained organoclays were characterized by X-ray diffraction (XRD), high-resolution transmission electron microscopy (HR-TEM), high-resolution thermogravimetric analysis (HR-TG), and infrared emission spectroscopy (IES). The intercalation of surfactants greatly increased the basal spacing of the interlayers and the conformation arrangement of the loaded surfactant were assessed based on the XRD and TEM measurements. This work shows that the dialkyl surfactant can be directly intercalated into the montmorillonite without first undergoing Na(+) exchange. Moreover, the thermal stability of organoclays and the different arrangements of the surfactant molecules intercalated in the SAz-2 Ca-montmorillonite were determined by a combination of TG and IES techniques. The detailed conformational ordering of different intercalated surfactants under different conditions was also studied. The surfactant molecule DDDMA has proved to be thermally stable even at 400°C which indicates that the prepared organoclay is stable to significantly high temperatures. This study offers new insights into the structure and thermal stabilities of SAz-2 Ca-montmorillonite modified with DDDMA. The experimental results also confirm the potential applications of organic SAz-2 Ca-montmorillonites as adsorbents and polymer-clay nanocomposites. Copyright © 2013 Elsevier Inc. All rights reserved.

Influence of smectite suspension structure on sheet orientation in dry sediments: XRD and AFM applications.

PubMed

Zbik, Marek S; Frost, Ray L

2010-06-15

The structure-building phenomena within clay aggregates are governed by forces acting between clay particles. Measurements of such forces are important to understand in order to manipulate the aggregate structure for applications such as dewatering of mineral processing tailings. A parallel particle orientation is required when conducting XRD investigation on the oriented samples and conduct force measurements acting between basal planes of clay mineral platelets using atomic force microscopy (AFM). To investigate how smectite clay platelets were oriented on silicon wafer substrate when dried from suspension range of methods like SEM, XRD and AFM were employed. From these investigations, we conclude that high clay concentrations and larger particle diameters (up to 5 microm) in suspension result in random orientation of platelets in the substrate. The best possible laminar orientation in the clay dry film, represented in the XRD 001/020 intensity ratio of 47 was obtained by drying thin layers from 0.02 wt.% clay suspensions of the natural pH. Conducted AFM investigations show that smectite studied in water based electrolytes show very long-range repulsive forces lower in strength than electrostatic forces from double-layer repulsion. It was suggested that these forces may have structural nature. Smectite surface layers rehydrate in water environment forms surface gel with spongy and cellular texture which cushion approaching AFM probe. This structural effect can be measured in distances larger than 1000 nm from substrate surface and when probe penetrate this gel layer, structural linkages are forming between substrate and clay covered probe. These linkages prevent subsequently smooth detachments of AFM probe on way back when retrieval. This effect of tearing new formed structure apart involves larger adhesion-like forces measured in retrieval. It is also suggested that these effect may be enhanced by the nano-clay particles interaction. 2010 Elsevier Inc. All

SR-XRD and SR-FTIR study of the alteration of silver foils in medieval paintings.

PubMed

Salvadó, Nati; Butí, Salvador; Labrador, Ana; Cinque, Gianfelice; Emerich, Hermann; Pradell, Trinitat

2011-03-01

Altarpieces and polychrome carved wood from the fifteenth century AD usually exhibit golden and silvery areas by the application of a very thin foil of metal. The metal foils were normally protected from the atmosphere by a varnish or resin which maybe either preserved or absent. Moreover, they were glued to the background surface by adhesive substances (egg yolk, drying oil or animal glue). The high proportion of the glueing substances often renders the development of reaction compounds. With time, silver alters blacken or simply disappear completely. In this paper, we study the alterations to metal foils from a selection of fifteenth century artworks showing different glueing agents, organic coatings and several degrees of conservation of the organic coatings and metal leafs. The submillimetric layered structure and the high variability and low amount of most of the compounds present in the different layers, as well as their differing nature (organic and inorganic) make the use of micron-sensitive high-resolution techniques essential for their study. In particular, the high resolution, high brilliance and small footprint renders synchrotron radiation most adequate for their study. SR-XRD was performed to identify the reaction compounds formed in the different layers; μFTIR was used at to identify the silver protecting organic coatings, the metal foil glueing layers and the corresponding reaction compounds. The results obtained suggest that atmospheric corrosion is the dominant mechanism, and therefore that the degree of corrosion of the metal foils is mainly related to the conservation state of the protecting coatings.

XRD and FTIR crystallinity indices in sound human tooth enamel and synthetic hydroxyapatite.

PubMed

Reyes-Gasga, José; Martínez-Piñeiro, Esmeralda L; Rodríguez-Álvarez, Galois; Tiznado-Orozco, Gaby E; García-García, Ramiro; Brès, Etienne F

2013-12-01

The crystallinity index (CI) is a measure of the percentage of crystalline material in a given sample and it is also correlated to the degree of order within the crystals. In the literature two ways are reported to measure the CI: X-ray diffraction and infrared spectroscopy. Although the CI determined by these techniques has been adopted in the field of archeology as a structural order measure in the bone with the idea that it can help e.g. in the sequencing of the bones in chronological and/or stratigraphic order, some debate remains about the reliability of the CI values. To investigate similarities and differences between the two techniques, the CI of sound human tooth enamel and synthetic hydroxyapatite (HAP) was measured in this work by X-ray diffraction (XRD) and Fourier Transform Infrared spectroscopy (FTIR), at room temperature and after heat treatment. Although the (CI)XRD index is related to the crystal structure of the samples and the (CI)FTIR index is related to the vibration modes of the molecular bonds, both indices showed similar qualitative behavior for heat-treated samples. At room temperature, the (CI)XRD value indicated that enamel is more crystalline than synthetic HAP, while (CI)FTIR indicated the opposite. Scanning (SEM) and transmission (TEM) images were also used to corroborate the measured CI values. © 2013.

High temperature XRD of Cu2.1Zn0.9SnSe4

NASA Astrophysics Data System (ADS)

Chetty, Raju; Mallik, Ramesh Chandra

2014-04-01

Quaternary compound with chemical composition Cu2.1Zn0.9SnSe4 is prepared by solid state synthesis. High temperature XRD (X-Ray Diffraction) of this compound is used in studying the effect of temperature on lattice parameters and thermal expansion coefficients. Thermal expansion coefficient is one of the important quantities in evaluating the Grüneisen parameter which further useful in determining the lattice thermal conductivity of the material. The high temperature XRD of the material revealed that the lattice parameters as well as thermal expansion coefficients of the material increased with increase in temperature which confirms the presence of anharmonicty.

Spectroscopic, DFT, and XRD Studies of Hydrogen Bonds in N-Unsubstituted 2-Aminobenzamides.

PubMed

Mphahlele, Malose Jack; Maluleka, Marole Maria; Rhyman, Lydia; Ramasami, Ponnadurai; Mampa, Richard Mokome

2017-01-04

The structures of the mono- and the dihalogenated N -unsubstituted 2-aminobenzamides were characterized by means of the spectroscopic (¹H-NMR, UV-Vis, FT-IR, and FT-Raman) and X-ray crystallographic techniques complemented with a density functional theory (DFT) method. The hindered rotation of the C(O)-NH₂ single bond resulted in non-equivalence of the amide protons and therefore two distinct resonances of different chemical shift values in the ¹H-NMR spectra of these compounds were observed. 2-Amino-5-bromobenzamide ( ABB ) as a model confirmed the presence of strong intramolecular hydrogen bonds between oxygen and the amine hydrogen. However, intramolecular hydrogen bonding between the carbonyl oxygen and the amine protons was not observed in the solution phase due to a rapid exchange of these two protons with the solvent and fast rotation of the Ar-NH₂ single bond. XRD also revealed the ability of the amide unit of these compounds to function as a hydrogen bond donor and acceptor simultaneously to form strong intermolecular hydrogen bonding between oxygen of one molecule and the NH moiety of the amine or amide group of the other molecule and between the amine nitrogen and the amide hydrogen of different molecules. DFT calculations using the B3LYP/6-311++G(d,p) basis set revealed that the conformer ( A ) with oxygen and 2-amine on the same side predominates possibly due to the formation of a six-membered intramolecular ring, which is assisted by hydrogen bonding as observed in the single crystal XRD structure.

In Situ XAS and XRD Studies of Substituted Spinel Lithium Manganese Oxides in the 4-5 V Region

DOE Office of Scientific and Technical Information (OSTI.GOV)

McBreen, J.; Mukerjee, S.; Yang, X. Q.

Partial substitution of Mn in lithium manganese oxide spinel materials by Cu and Ni greatly affects the electrochemistry and the phase behavior of the cathode. Substitution with either metal or with a combination of both shortens the 4.2 V plateau and results in higher voltage plateaus. In situ x-ray absorption (XAS) studies indicate that the higher voltage plateaus are related to redox processes on the substituents. In situ x-ray diffraction (XRD) on LiCu{sub 0.5}Mn{sub 1.5}O{sub 4} shows single phase behavior during the charge and discharge process. Three phases are observed for LiNi{sub 0.5}Mn{sub 1.5}O{sub 4} and two phases are observedmore » in the case of LiNi{sub 0.25}Cu{sub 0.25}Mn{sub 1.5}O{sub 4}. The electrolyte stability is dependent on both the operating voltage and the cathode composition. Even though Ni substituted materials have lower voltages, the electrolyte is more stable in cells with the Cu substituted materials.« less

Investigation of composition and structure of spongy and hard bone tissue using FTIR spectroscopy, XRD and SEM

NASA Astrophysics Data System (ADS)

Al-Akhras, M.-Ali H.; Hasan Qaseer, M. K.; Albiss, B. A.; Alebrhim, M. Anwar; Gezawa, Umar S.

2018-02-01

Valuable structural and chemical features can be obtained for spongy and hard bone by infrared spectroscopy and X-ray diffraction. A better understanding of chemical and structural differences between spongy and hard bone is a very important contributor to bone quality. Our data according to IR data showed that the collagen cross-links occurred to be higher in spongy bone, and crystallinity was lower in spongy bone. Deconvolution of the infrared band near 870 cm-1 reveals evidence for A2-type carbonate substitution on hydroxyapatite of spongy bone in addition to the A and B type carbonate substitution that are also found in hard bone. IR and XRD data confirmed the results of each other since full width at half maximum of 002-apatite pattern of XRD showed that the crystallinity was lower in spongy bone. The microstructure was examined by using scanning electron microscope and the result showed that the lattice of thin threads in spongy bone and is less dense than hard bone.

Length-Scale-Dependent Phase Transformation of LiFePO4 : An In situ and Operando Study Using Micro-Raman Spectroscopy and XRD.

PubMed

Siddique, N A; Salehi, Amir; Wei, Zi; Liu, Dong; Sajjad, Syed D; Liu, Fuqiang

2015-08-03

The charge and discharge of lithium ion batteries are often accompanied by electrochemically driven phase-transformation processes. In this work, two in situ and operando methods, that is, micro-Raman spectroscopy and X-ray diffraction (XRD), have been combined to study the phase-transformation process in LiFePO4 at two distinct length scales, namely, particle-level scale (∼1 μm) and macroscopic scale (∼several cm). In situ Raman studies revealed a discrete mode of phase transformation at the particle level. Besides, the preferred electrochemical transport network, particularly the carbon content, was found to govern the sequence of phase transformation among particles. In contrast, at the macroscopic level, studies conducted at four different discharge rates showed a continuous but delayed phase transformation. These findings uncovered the intricate phase transformation in LiFePO4 and potentially offer valuable insights into optimizing the length-scale-dependent properties of battery materials. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

The Crystal Structure of Micro- and Nanopowders of ZnS Studied by EPR of Mn2+ and XRD.

PubMed

Nosenko, Valentyna; Vorona, Igor; Grachev, Valentyn; Ishchenko, Stanislav; Baran, Nikolai; Becherikov, Yurii; Zhuk, Anton; Polishchuk, Yuliya; Kladko, Vasyl; Selishchev, Alexander

2016-12-01

The crystal structure of micro- and nanopowders of ZnS doped with different impurities was analyzed by the electron paramagnetic resonance (EPR) of Mn 2+ and XRD methods. The powders of ZnS:Cu, ZnS:Mn, ZnS:Co, and ZnS:Eu with the particle sizes of 5-7 μm, 50-200 nm, 7-10 μm, and 5-7 nm, respectively, were studied. Manganese was incorporated in the crystal lattice of all the samples as uncontrolled impurity or by doping. The Mn 2+ ions were used as EPR structural probes. It is found that the ZnS:Cu has the cubic structure, the ZnS:Mn has the hexagonal structure with a rhombic distortion, the ZnS:Co is the mixture of the cubic and hexagonal phases in the ratio of 1:10, and the ZnS:Eu has the cubic structure and a distorted cubic structure with stacking defects in the ratio 3:1. The EPR technique is shown to be a powerful tool in the determination of the crystal structure for mixed-polytype ZnS powders and powders with small nanoparticles. It allows observation of the stacking defects, which is revealed in the XRD spectra.

A Combined XRD/XRF Instrument for Lunar Resource Assessment

NASA Technical Reports Server (NTRS)

Vaniman, D. T.; Bish, D. L.; Chipera, S. J.; Blacic, J. D.

1992-01-01

Robotic surface missions to the Moon should be capable of measuring mineral as well as chemical abundances in regolith samples. Although much is already known about the lunar regolith, our data are far from comprehensive. Most of the regolith samples returned to Earth for analysis had lost the upper surface, or it was intermixed with deeper regolith. This upper surface is the part of the regolith most recently exposed to the solar wind; as such it will be important to resource assessment. In addition, it may be far easier to mine and process the uppermost few centimeters of regolith over a broad area than to engage in deep excavation of a smaller area. The most direct means of analyzing the regolith surface will be by studies in situ. In addition, the analysis of the impact-origin regolith surfaces, the Fe-rich glasses of mare pyroclastic deposits, are of resource interest, but are inadequately known; none of the extensive surface-exposed pyroclastic deposits of the Moon have been systematically sampled, although we know something about such deposits from the Apollo 17 site. Because of the potential importance of pyroclastic deposits, methods to quantify glass as well as mineral abundances will be important to resource evaluation. Combined x ray diffraction (XRD) and x ray fluorescence (XRF) analysis will address many resource characterization problems on the Moon. XRF methods are valuable for obtaining full major-element abundances with high precision. Such data, collected in parallel with quantitative mineralogy, permit unambiguous determination of both mineral and chemical abundances where concentrations are high enough to be of resource grade. Collection of both XRD and XRF data from a single sample provides simultaneous chemical and mineralogic information. These data can be used to correlate quantitative chemistry and mineralogy as a set of simultaneous linear equations, the solution of which can lead to full characterization of the sample. The use of

Inhibitive effect of Pt on Pd-hydride formation of Pd@Pt core-shell electrocatalysts: An in situ EXAFS and XRD study

DOE PAGES

Wise, Anna M.; Richardson, Peter W.; Price, Stephen W. T.; ...

2017-12-27

In situ EXAFS and XRD have been used to study the electrochemical formation of hydride phases, H abs, in 0.5 M H 2SO 4 for a Pd/C catalyst and a series of Pd@Pt core-shell catalysts with varying Pt shell thickness, from 0.5 to 4 monolayers. Based on the XRD data a 3% lattice expansion is observed for the Pd/C core catalyst upon hydride formation at 0.0 V. In contrast, the expansion was ≤0.6% for all of the core-shell catalysts. The limited extent of the lattice expansion observed suggests that hydride formation, which may occur during periodic active surface area measurementsmore » conducting during accelerated aging tests or driven by H 2 crossover in PEM fuel cells, is unlikely to contribute significantly to the degradation of Pd@Pt core-shell electrocatalysts in contrast to the effects of oxide formation.« less

Inhibitive effect of Pt on Pd-hydride formation of Pd@Pt core-shell electrocatalysts: An in situ EXAFS and XRD study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wise, Anna M.; Richardson, Peter W.; Price, Stephen W. T.

In situ EXAFS and XRD have been used to study the electrochemical formation of hydride phases, H abs, in 0.5 M H 2SO 4 for a Pd/C catalyst and a series of Pd@Pt core-shell catalysts with varying Pt shell thickness, from 0.5 to 4 monolayers. Based on the XRD data a 3% lattice expansion is observed for the Pd/C core catalyst upon hydride formation at 0.0 V. In contrast, the expansion was ≤0.6% for all of the core-shell catalysts. The limited extent of the lattice expansion observed suggests that hydride formation, which may occur during periodic active surface area measurementsmore » conducting during accelerated aging tests or driven by H 2 crossover in PEM fuel cells, is unlikely to contribute significantly to the degradation of Pd@Pt core-shell electrocatalysts in contrast to the effects of oxide formation.« less

XRD and FTIR structural investigation of gadolinium-zinc-borate glass ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Borodi, G.; Pascuta, P.; Dan, V.

2013-11-13

X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy measurements have been employed to investigate the (Gd{sub 2}O{sub 3}){sub x}⋅(B{sub 2}O{sub 3}){sub (60−x)}⋅(ZnO){sub 40} glass ceramics system, with 0 ≤ x ≤ 15 mol%. After heat treatment applied at 860 °C for 2 h, some structural changes were observed and new crystalline phases appeared in the structure of the samples. In these glass ceramics four crystalline phases were identified using powder diffraction files (PDF 2), namely ZnB{sub 4}O{sub 7}, Zn{sub 4}O(B{sub 6}O{sub 12}), Zn{sub 3}(BO{sub 3}){sub 2} and GdBO{sub 3}. From the XRD data, the average unit-cell parameter and themore » quantitative ratio of the crystallographic phases in the studied samples were evaluated. FTIR data revealed that the BO{sub 3}, BO{sub 4} and ZnO{sub 4} are the main structural units of these glass ceramics network. The compositional dependence of the different structural units which appear in the studied samples was followed.« less

Insight into the Am-O Phase Equilibria: A Thermodynamic Study Coupling High-Temperature XRD and CALPHAD Modeling.

PubMed

Epifano, Enrica; Guéneau, Christine; Belin, Renaud C; Vauchy, Romain; Lebreton, Florent; Richaud, Jean-Christophe; Joly, Alexis; Valot, Christophe; Martin, Philippe M

2017-07-03

In the frame of minor actinide transmutation, americium can be diluted in UO 2 and (U, Pu)O 2 fuels burned in fast neutron reactors. The first mandatory step to foresee the influence of Am on the in-reactor behavior of transmutation targets or fuel is to have fundamental knowledge of the Am-O binary system and, in particular, of the AmO 2-x phase. In this study, we coupled HT-XRD (high-temperature X-ray diffraction) experiments with CALPHAD thermodynamic modeling to provide new insights into the structural properties and phase equilibria in the AmO 2-x -AmO 1.61+x -Am 2 O 3 domain. Because of this approach, we were able for the first time to assess the relationships between temperature, lattice parameter, and hypostoichiometry for fcc AmO 2-x . We showed the presence of a hyperstoichiometric existence domain for the bcc AmO 1.61+x phase and the absence of a miscibility gap in the fcc AmO 2-x phase, contrary to previous representations of the phase diagram. Finally, with the new experimental data, a new CALPHAD thermodynamic model of the Am-O system was developed, and an improved version of the phase diagram is presented.

Structure, Elastic Constants and XRD Spectra of Extended Solids under High Pressure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Batyrev, I. G.; Coleman, S. P.; Ciezak-Jenkins, J. A.

We present results of evolutionary simulations based on density functional calculations of a potentially new type of energetic materials called extended solids: P-N and N-H. High-density structures with covalent bonds generated using variable and fixed concentration methods were analysed in terms of thermo-dynamical stability and agreement with experimental X-ray diffraction (XRD) spectra. X-ray diffraction spectra were calculated using a virtual diffraction algorithm that computes kinematic diffraction intensity in three-dimensional reciprocal space before being reduced to a two-theta line profile. Calculated XRD patterns were used to search for the structure of extended solids present at experimental pressures by optimizing data accordingmore » to experimental XRD peak position, peak intensity and theoretically calculated enthalpy. Elastic constants has been calculated for thermodynamically stable structures of P-N system.« less

Hydrometallurgical Extraction of Zinc and Copper A 57Fe-Mössbauer and XRD Approach

NASA Astrophysics Data System (ADS)

Mulaba-Bafubiandi, A. F.; Waanders, F. B.

2005-02-01

The most commonly used route in the hydrometallurgical extraction of zinc and copper from a sulphide ore is the concentrate roast leach electro winning process. In the present investigation a zinc copper ore from the Maranda mine, located in the Murchison Greenstone Belt, South Africa, containing sphalerite (ZnS) and chalcopyrite (CuFeS2), was studied. The 57Fe-Mössbauer spectrum of the concentrate yielded pyrite, chalcopyrite and clinochlore, consistent with XRD data. Optimal roasting conditions were found to be 900°C for 3 h and the calcine produced contained according to X-ray diffractometry equal amounts of franklinite (ZnFe2O4) and zinc oxide (ZnO) and half the amount of willemite (Zn2SiO4). The Mössbauer spectrum showed predominantly franklinite (59%), hematite (6%) and other Zn- or Cu-depleted ferrites (35%). The latter could not be detected by XRD analyses as peak overlapping with other species occurred. Leaching was done with HCl, H2SO4 and HNO3, to determine which process would result in maximum recovery of Zn and Cu. More than 80% of both were recovered by using either one of the three techniques. From the residue of the leaching, the Fe-compounds were precipitated and <1% of the Zn and Cu was not recovered.

Mössbauer, TEM/SAED and XRD investigation on waste dumps of the Valea lui Stan gold mines

NASA Astrophysics Data System (ADS)

Constantinescu, Serban Grigore; Udubasa, Sorin S.; Udubasa, Gheorghe; Kuncser, Victor; Popescu-Pogrion, Nicoleta; Mercioniu, Ionel; Feder, Marcel

2012-03-01

The complementary investigation techniques, Mössbauer spectroscopy, transmission electron microscopy with selected area electron diffraction (TEM/SAED), X-ray diffraction (XRD) have been used to investigate the fate of the Valea lui Stan, Romania, gold-ore nanoscale-minerals during the long time of residence in the waste dumps. The preliminary investigations showed such waste dumps to contain significant amount of metals which cannot be identified by conventional methods. An intense research activity started up in order to evaluate the possibilities to recycle Valea lui Stan waste dumps and to recover metals by chemical or phytoextraction procedures. The waste dumps naturally show different mineral constituents with clay minerals as major phases, observed by XRD-technique. Although the waste dumps materials have whitish-yellowish colours, MÖSSBAUER technique evidences the presence of the finely dispersed iron bearing minerals. The authors are focusing to inspect and analyze Fe-compounds in the samples collected from Valea lui Stan's waste dumps in order to identify the magnetic phases by Mössbauer technique.

Transmission X-ray Diffraction (XRD) Patterns Relevant to the MSL Chemin Amorphous Component: Sulfates And Silicates

NASA Technical Reports Server (NTRS)

Morris, R. V.; Rampe, E. B.; Graff, T. G.; Archer, P. D., Jr.; Le, L.; Ming, D. W.; Sutter, B.

2015-01-01

The Mars Science Laboratory (MSL) CheMin instrument on the Curiosity rover is a transmission X-ray diffractometer (Co-Kalpha radiation source and a approx.5deg to approx.52deg 2theta range) where the analyzed powder samples are constrained to have discrete particle diameters <150 microns by a sieve. To date, diffraction patterns have been obtained for one basaltic soil (Rocknest (RN)) and four drill fines of coherent rock (John Klein (JK), Cumberland (CB), Windjana (WJ), and Confidence Hills (CH)). The CheMin instrument has detected and quantified the abundance of both primary igneous (e.g., feldspar, olivine, and pyroxene) and secondary (e.g., Ca-sulfates, hematite, akaganeite, and Fe-saponite) minerals. The diffraction patterns of all CheMin samples are also characterized by a broad diffraction band centered near 30deg 2theta and by increasing diffraction intensity (scattering continuum) from approx.15deg to approx.5deg, the 2theta minimum. Both the broad band and the scattering continuum are attributed to the presence of an XRD amorphous component. Estimates of amorphous component abundance, based on the XRD data itself and on mass-balance calculations using APXS data crystalline component chemistry derived from XRD data, martian meteorites, and/or stoichiometry [e.g., 6-9], range from approx.20 wt.% to approx.50 wt.% of bulk sample. The APXSbased calculations show that the amorphous component is rich in volatile elements (esp. SO3) and is not simply primary basaltic glass, which was used as a surrogate to model the broad band in the RN CheMin pattern. For RN, the entire volatile inventory (except minor anhydrite) is assigned to the amorphous component because no volatile-bearing crystalline phases were reported within detection limits [2]. For JK and CB, Fesaponite, basanite, and akaganeite are volatile-bearing crystalline components. Here we report transmission XRD patterns for sulfate and silicate phases relevant to interpretation of MSL-CheMin XRD amorphous

[NIR and XRD analysis of drill-hole samples from Zhamuaobao iron-graphite deposit, Inner Mongolia].

PubMed

Li, Ying-kui; Cao, Jian-jin; Wu, Zheng-quan; Dai, Dong-le; Lin, Zu-xu

2015-01-01

The author analyzed the 4202 drill-hole samples from Zhamuaobao iron-graphite deposit by using near infrared spectroscopy(NIR) and X-ray diffraction(XRD) measuring and testing techniques, and then compared and summarized the results of two kinds of testing technology. The results indicate that some difference of the mineral composition exists among different layers, the lithology from upper to deeper is the clay gravel layer of tertiary and quaternary, mudstone, mica quartz schist, quartz actinolite scarn, skarnization marble, iron ore deposits, graphite deposits and mica quartz schist. The petrogenesis in different depth also shows difference, which may indicate the geological characteristic to some extent. The samples had mainly undergone such processes as oxidization, carbonation, chloritization and skarn alteration. The research results can not only improve the geological feature of the mining area, but also have great importance in ore exploration, mining, mineral processing and so on. What's more, as XRD can provide preliminary information about the mineral composition, NIR can make further judgement on the existence of the minerals. The research integrated the advantages of both NIR and XRD measuring and testing techniques, put forward a method with two kinds of modern testing technology combined with each other, which may improve the accuracy of the mineral composition identification. In the meantime, the NIR will be more wildly used in geography on the basis of mineral spectroscopy.

Modeling and measurements of XRD spectra of extended solids under high pressure

NASA Astrophysics Data System (ADS)

Batyrev, I. G.; Coleman, S. P.; Stavrou, E.; Zaug, J. M.; Ciezak-Jenkins, J. A.

2017-06-01

We present results of evolutionary simulations based on density functional calculations of various extended solids: N-Si and N-H using variable and fixed concentration methods of USPEX. Predicted from the evolutionary simulations structures were analyzed in terms of thermo-dynamical stability and agreement with experimental X-ray diffraction spectra. Stability of the predicted system was estimated from convex-hull plots. X-ray diffraction spectra were calculated using a virtual diffraction algorithm which computes kinematic diffraction intensity in three-dimensional reciprocal space before being reduced to a two-theta line profile. Calculations of thousands of XRD spectra were used to search for a structure of extended solids at certain pressures with best fits to experimental data according to experimental XRD peak position, peak intensity and theoretically calculated enthalpy. Comparison of Raman and IR spectra calculated for best fitted structures with available experimental data shows reasonable agreement for certain vibration modes. Part of this work was performed by LLNL, Contract DE-AC52-07NA27344. We thank the Joint DoD / DOE Munitions Technology Development Program, the HE C-II research program at LLNL and Advanced Light Source, supported by BES DOE, Contract No. DE-AC02-05CH112.

Trace elemental analysis of Indian natural moonstone gems by PIXE and XRD techniques.

PubMed

Venkateswara Rao, R; Venkateswarulu, P; Kasipathi, C; Sivajyothi, S

2013-12-01

A selected number of Indian Eastern Ghats natural moonstone gems were studied with a powerful nuclear analytical and non-destructive Proton Induced X-ray Emission (PIXE) technique. Thirteen elements, including V, Co, Ni, Zn, Ga, Ba and Pb, were identified in these moonstones and may be useful in interpreting the various geochemical conditions and the probable cause of their inceptions in the moonstone gemstone matrix. Furthermore, preliminary XRD studies of different moonstone patterns were performed. The PIXE technique is a powerful method for quickly determining the elemental concentration of a substance. A 3MeV proton beam was employed to excite the samples. The chemical constituents of moonstones from parts of the Eastern Ghats geological formations of Andhra Pradesh, India were determined, and gemological studies were performed on those gems. The crystal structure and the lattice parameters of the moonstones were estimated using X-Ray Diffraction studies, trace and minor elements were determined using the PIXE technique, and major compositional elements were confirmed by XRD. In the present work, the usefulness and versatility of the PIXE technique for research in geo-scientific methodology is established. © 2013 Elsevier Ltd. All rights reserved.

XRD and 29Si MAS-NMR spectroscopy across the β-Lu 2Si 2O 7- β-Y 2Si 2O 7 solid solution

NASA Astrophysics Data System (ADS)

Becerro, Ana I.; Escudero, Alberto

2005-01-01

Samples in the system Lu 2-xY xSi 2O 7 (0⩽ x⩽2) have been synthesized following the sol-gel method and calcined to 1300 °C, a temperature at which the β-polymorph is known to be the stable phase for the end-members Lu 2Si 2O 7 and Y 2Si 2O 7. The XRD patterns of all the compositions studied are compatible with the structure of the β-polymorph. Unit cell parameters are calculated as a function of composition from XRD patterns. They show a linear change with increasing Y content, which indicates a solid solubility of β-Y 2Si 2O 7 in β-Lu 2Si 2O 7 at 1300 °C. 29Si MAS NMR spectra of the different members of the system agree with the XRD results, showing a linear decrease of the 29Si chemical shift with increasing Y content. Finally, a correlation reported in the literature to predict 29Si chemical shifts in silicates is applied here to obtain the theoretical variation in 29Si chemical shift values in the system Lu 2Si 2O 7-Y 2Si 2O 7 and the results compare favorably with the values obtained experimentally.

Morphological, chemical and structural characterisation of deciduous enamel: SEM, EDS, XRD, FTIR and XPS analysis.

PubMed

Zamudio-Ortega, C M; Contreras-Bulnes, R; Scougall-Vilchis, R J; Morales-Luckie, R A; Olea-Mejía, O F; Rodríguez-Vilchis, L E

2014-09-01

The purpose of this study was to characterise the enamel surface of sound deciduous teeth in terms of morphology, chemical composition, structure and crystalline phases. The enamel of 30 human deciduous teeth was examined by: Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray Spectroscopy (EDS), X-ray Powder Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), and X-ray Photoelectron Spectroscopy (XPS). Chemical differences between incisors and canines were statistically evaluated using the Mann-Whitney U test (p ≤ 0.05). Three enamel patterns were observed by SEM: 'mostly smooth with some groves', 'abundant microporosities' and 'exposed prisms'. The average Ca/P molar ratios were 1.37 and 1.03 by EDS and XPS, respectively. The crystallite size determined by XRD was 210.82 ± 16.78 Å. The mean ratio between Ca bonded to phosphate and Ca bonded to hydroxyl was approximately 10:1. The enamel of sound deciduous teeth showed two main patterns: 'mostly smooth with some groves' and 'abundant microporosities'. 'Exposed prisms' was a secondary pattern. There were slight variations among the Ca/P molar ratios found by EDS and XPS, suggesting differences in the mineral content from the enamel surface to the interior. The crystalline phases found in enamel were hydroxyapatite and carbonate apatite, with major type B than type A carbonate incorporation.

Analytical electron microscopy of Mg-SiO smokes - A comparison with infrared and XRD studies

NASA Technical Reports Server (NTRS)

Rietmeijer, F. J. M.; Nuth, J. A.; Mackinnon, I. D. R.

1986-01-01

Analytical electron microscopy conducted for Mg-SiO smokes (experimentally obtained from samples previously characterized by IR spectroscopy) indicates that the microcrystallinity content of unannealed smokes increases with increased annealing for up to 30 hr. The growth of forsterite microcrystallites in the initially nonstoichiometric smokes may give rise to the contemporaneous growth of the SiO polymorph tridymite and MgO; after 4 hr of annealing, these react to form enstatite. It is suggested that XRD analysis and IR spectroscopy should be conducted in conjunction with detailed analytical electron microscopy for the detection of emerging crystallinity in vapor-phase condensates.

High temperature XRD of Cu{sub 2.1}Zn{sub 0.9}SnSe{sub 4}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chetty, Raju, E-mail: rcmallik@physics.iisc.ernet.in; Mallik, Ramesh Chandra, E-mail: rcmallik@physics.iisc.ernet.in

2014-04-24

Quaternary compound with chemical composition Cu{sub 2.1}Zn{sub 0.9}SnSe{sub 4} is prepared by solid state synthesis. High temperature XRD (X-Ray Diffraction) of this compound is used in studying the effect of temperature on lattice parameters and thermal expansion coefficients. Thermal expansion coefficient is one of the important quantities in evaluating the Grüneisen parameter which further useful in determining the lattice thermal conductivity of the material. The high temperature XRD of the material revealed that the lattice parameters as well as thermal expansion coefficients of the material increased with increase in temperature which confirms the presence of anharmonicty.

XRD and mineralogical analysis of gypsum dunes at White Sands National Monument, New Mexico and applications to gypsum detection on Mars

NASA Astrophysics Data System (ADS)

Lafuente, B.; Bishop, J. L.; Fenton, L. K.; King, S. J.; Blake, D.; Sarrazin, P.; Downs, R.; Horgan, B. H.

2013-12-01

A field portable X-ray Diffraction (XRD) instrument was used at White Sands National Monument to perform in-situ measurements followed by laboratory analyses of the gypsum-rich dunes and to determine its modal mineralogy. The field instrument is a Terra XRD (Olympus NDT) based on the technology of the CheMin (Chemistry and Mineralogy) instrument onboard the Mars Science Laboratory (MSL) rover Curiosity which is providing the mineralogical and chemical composition of scooped soil samples and drilled rock powders collected at Gale Crater [1]. Using Terra at White Sands will contribute to 'ground truth' for gypsum-bearing environments on Mars. Together with data provided by VNIR spectra [2], this study clarifies our understanding of the origin and history of gypsum-rich sand dunes discovered near the northern polar region of Mars [3]. The results obtained from the field analyses performed by XRD and VNIR spectroscopy in four dunes at White Sands revealed the presence of quartz and dolomite. Their relative abundance has been estimated using the Reference Intensity Ratio (RIR) method. For this study, particulate samples of pure natural gypsum, quartz and dolomite were used to prepare calibration mixtures of gypsum-quartz and gypsum-dolomite with the 90-150μm size fractions. All single phases and mixtures were analyzed by XRD and RIR factors were calculated. Using this method, the relative abundance of quartz and dolomite has been estimated from the data collected in the field. Quartz appears to be present in low amounts (2-5 wt.%) while dolomite is present at percentages up to 80 wt.%. Samples from four dunes were collected and prepared for subsequent XRD analysis in the lab to estimate their composition and illustrate the changes in mineralogy with respect to location and grain size. Gypsum-dolomite mixtures: The dolomite XRD pattern is dominated by an intense diffraction peak at 2θ≈36 deg. which overlaps a peak of gypsum, This makes low concentrations of dolomite

A 4-(o-chlorophenyl)-2-aminothiazole: Microwave assisted synthesis, spectral, thermal, XRD and biological studies

NASA Astrophysics Data System (ADS)

Rajmane, S. V.; Ubale, V. P.; Lawand, A. S.; Nalawade, A. M.; Karale, N. N.; More, P. G.

2013-11-01

A 4-(o-chlorophenyl)-2-aminothiazole (CPAT) has been synthesized by reacting o-chloroacetophenone, iodine and thiourea under microwave irradiation as a green chemistry approach. The reactions proceed selectively and within a couple of minutes giving high yields of the products. The compound was characterized by elemental, spectral (UV-visible, IR, NMR and GC-MS), XRD and thermal analyses. The TG curve of the compound was analyzed to calculate various kinetic parameters (n, E, Z, ΔS and ΔG) by using Coats-Redfern (C.R.), MacCallum-Tanner (M.T.) and Horowitz-Metzger (H.M.) method. The compound was tested for the evaluation of antibacterial activity against B. subtilis and E. coli and antifungal activity against A. niger and C. albicans. The compound was evaluated for their in vitro nematicidal activity on plant parasitic nematode Meloidogyne javanica and molluscicidal activity on fresh water helminthiasis vector snail Lymnea auricularia. The compound is biologically active in very low concentration. X-ray diffraction study suggests a triclinic crystal system for the compound.

Interaction of selenite with reduced Fe and/or S species: An XRD and XAS study.

PubMed

Finck, Nicolas; Dardenne, Kathy

2016-05-01

In this study, we investigated the interaction between selenite and either Fe((II))aq or S((-II))aq in solution, and the results were used to investigate the interaction between Se((IV))aq and FeS in suspension. The reaction products were characterized by a combination of methods (SEM, XRD and XAS) and the reaction mechanisms were identified. In a first experiment, Se((IV))aq was reduced to Se((0)) by interaction with Fe((II))aq which was oxidized to Fe((III)), but the reaction was only partial. Subsequently, some Fe((III)) produced akaganeite (β-FeOOH) and the release of proton during that reaction decreased the pH. The pH decrease changed the Se speciation in solution which hindered further Se((IV)) reduction by Fe((II))aq. In a second experiment, Se((IV))aq was quantitatively reduced to Se((0)) by S((-II))aq and the reaction was fast. Two sulfide species were needed to reduce one Se((IV)), and the observed pH increase was due to a proton consumption. For both experiments, experimental results are consistent with expectations based on the oxidation reduction potential of the various species. Upon interaction with FeS, Se((IV))aq was reduced to Se((0)) and minute amounts of pyrite were detected, a consequence of partial mackinawite oxidation at surface sulfur sites. These results are of prime importance with respect to safe deep disposal of nuclear waste which contains the long-lived radionuclide (79)Se. This study shows that after release of (79)Se((IV)) upon nuclear waste matrix corrosion, selenite can be reduced in the near field to low soluble Se((0)) by interaction with Fe((II))aq and/or S((-II))aq species. Because the solubility of Se((0)) species is significantly lower than that of Se((IV)), selenium will become much less (bio)available and its migration out of deep HLW repositories may be drastically hindered. Copyright © 2016. Published by Elsevier B.V.

Response Time Measurements of the NIF DANTE XRD-31 X-Ray Diodes (Pre-print)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Don Pellinen and Michael Griffin

2009-01-23

The XRD-31 is a fast, windowless X-ray vacuum photodiode developed by EG&G. It is currently the primary fast X-ray detector used to diagnose the X-rays on NIF and OMEGA on the multichannel DANTE spectrometer. The XRD-31 has a dynamic range of less than 1e-12 amps to more than 10 amps. A technique is described to measure the impulse response of the diodes to a 150 fs pulse of 200 nm laser light and a method to calculate the “risetime” for a square pulse and compare it with the computed electron transit time from the photocathode to the anode. Measured responsemore » time for 5 XRD-31s assembled in early 2004 was 149.7 ps +-2.75 ps.« less

An Integrated XRF/XRD Instrument for Mars Exobiology and Geology Experiments

NASA Technical Reports Server (NTRS)

Koppel, L. N.; Franco, E. D.; Kerner, J. A.; Fonda, M. L.; Schwartz, D. E.; Marshall, J. R.

1993-01-01

By employing an integrated x-ray instrument on a future Mars mission, data obtained will greatly augment those returned by Viking; details characterizing the past and present environment on Mars and those relevant to the possibility of the origin and evolution of life will be acquired. A combined x-ray fluorescence/x-ray diffraction (XRF/XRD) instrument was breadboarded and demonstrated to accommodate important exobiology and geology experiment objectives outlined for MESUR and future Mars missions. Among others, primary objectives for the exploration of Mars include the intense study of local areas on Mars to establish the chemical, mineralogical, and petrological character of different components of the surface material; to determine the distribution, abundance, and sources and sinks of volatile materials, including an assessment of the biologic potential, now and during past epoches; and to establish the global chemical and physical characteristics of the Martian surface. The XRF/XRD breadboard instrument identifies and quantifies soil surface elemental, mineralogical, and petrological characteristics and acquires data necessary to address questions on volatile abundance and distribution. Additionally, the breadboard is able to characterize the biogenic element constituents of soil samples providing information on the biologic potential of the Mars environment. Preliminary breadboard experiments confirmed the fundamental instrument design approach and measurement performance.

Evaluation of Rock Powdering Methods to Obtain Fine-grained Samples for CHEMIN, a Combined XRD/XRF Instrument

NASA Technical Reports Server (NTRS)

Chipera, S. J.; Vaniman, D. T.; Bish, D. L.; Sarrazin, P.; Feldman, S.; Blake, D. F.; Bearman, G.; Bar-Cohen, Y.

2004-01-01

A miniature XRD/XRF (X-ray diffraction / X-ray fluorescence) instrument, CHEMIN, is currently being developed for definitive mineralogic analysis of soils and rocks on Mars. One of the technical issues that must be addressed to enable remote XRD analysis is how best to obtain a representative sample powder for analysis. For powder XRD analyses, it is beneficial to have a fine-grained sample to reduce preferred orientation effects and to provide a statistically significant number of crystallites to the X-ray beam. Although a two-dimensional detector as used in the CHEMIN instrument will produce good results even with poorly prepared powder, the quality of the data will improve and the time required for data collection will be reduced if the sample is fine-grained and randomly oriented. A variety of methods have been proposed for XRD sample preparation. Chipera et al. presented grain size distributions and XRD results from powders generated with an Ultrasonic/Sonic Driller/Corer (USDC) currently being developed at JPL. The USDC was shown to be an effective instrument for sampling rock to produce powder suitable for XRD. In this paper, we compare powder prepared using the USDC with powder obtained with a miniaturized rock crusher developed at JPL and with powder obtained with a rotary tungsten carbide bit to powders obtained from a laboratory bench-scale Retsch mill (provides benchmark mineralogical data). These comparisons will allow assessment of the suitability of these methods for analysis by an XRD/XRF instrument such as CHEMIN.

Effect of sample moisture content on XRD-estimated cellulose crystallinity index and crystallite size

Treesearch

Umesh P. Agarwal; Sally A. Ralph; Carlos Baez; Richard S. Reiner; Steve P. Verrill

2017-01-01

Although X-ray diffraction (XRD) has been the most widely used technique to investigate crystallinity index (CrI) and crystallite size (L200) of cellulose materials, there are not many studies that have taken into account the role of sample moisture on these measurements. The present investigation focuses on a variety of celluloses and cellulose...

Definitive Mineralogical Analysis of Mars Analog Rocks Using the CheMin XRD/XRF Instrument

NASA Technical Reports Server (NTRS)

Blake, D. F.; Sarrazin, P.; Bish, D. L.; Feldman, S.; Chipera, S. J.; Vaniman, D. T.; Collins, S.

2004-01-01

Mineral identification is a critical component of Mars Astrobiological missions. Chemical or elemental data alone are not definitive because a single elemental or chemical composition or even a single bonding type can represent a range of substances or mineral assemblages. Minerals are defined as unique structural and compositional phases that occur naturally. There are about 15,000 minerals that have been described on Earth, all uniquely identifiable via diffraction methods. There are likely many minerals yet undiscovered on Earth, and likewise on Mars. If an unknown phase is identified on Mars, it can be fully characterized by structural (X-ray Diffraction, XRD) and elemental analysis (X-ray Fluorescence, XRF) without recourse to other data because XRD relies on the principles of atomic arrangement for its determinations. XRD is the principal means of identification and characterization of minerals on Earth.

Characterization using XRD of puzzolanic materials from residual sludge from water treatment

NASA Astrophysics Data System (ADS)

Barón, G.; Montaño, A. M.; González, C. P.

2017-12-01

The goal of this work is to do mechanical and chemical characterization of puzzolanic materials using compressive strength measurements and X-Ray Diffraction (XRD). These materials are composed of red clay and aluminous sludge produced by the treatment of potable water at Planta Algodonal, Ocaña, Norte de Santander, Colombia. Ceramic bricks were sintered to 1100°C and ten were characterized in their physically, mechanically and chemically properties. The results showed that the relationships with which the Colombian standards according to NTC 4017 (100KGF/cm2) for non-structural bricks are maintained for those containing 10% (105Kgf/cm2) and 20% (102.9Kgf/cm2) of sludge with respect to clay.

Validation of enhanced stabilization of municipal solid waste under controlled leachate recirculation using FTIR and XRD.

PubMed

Sethi, Sapna; Kothiyal, N C; Nema, Arvind K

2012-07-01

Leachate recirculation at neutral PH accompanied with buffer/nutrients addition has been used successfully in earlier stabilization of municipal solid waste in bioreactor landfills. In the present study, efforts were made to enhance the stabilization rate of municipal solid waste (MSW) and organic solid waste (OSW) in simulated landfill bioreactors by controlling the pH of recirculated leachate towards slightly alkaline side in absence of additional buffer and nutrients addition. Enhanced stabilization in waste samples was monitored with the help of analytical tools like Fourier Transform Infrared Spectroscopy (FTIR) and X-Ray Diffraction (XRD). Predominance of bands assigned to inorganic compounds and comparatively lower intensities of bands for organic compounds in the FTIR spectra of waste samples degraded with leachate recirculation under controlled pH confirmed higher rate of biodegradation and mineralization of waste than the samples degraded without controlled leachate recirculation. XRD spectra also confirmed to a greater extent of mineralization in the waste samples degraded under leachate recirculation with controlled pH. Comparison of XRD spectra of two types of wastes pointed out higher degree of mineralization in organic solid waste as compared to municipal solid waste.

Structural investigations in helium implanted cubic zirconia using grazing incidence XRD and EXAFS spectroscopy

NASA Astrophysics Data System (ADS)

Kuri, G.; Degueldre, C.; Bertsch, J.; Döbeli, M.

2010-06-01

The crystal structure and local atom arrangements surrounding Zr atoms were determined for a helium implanted cubic stabilized zirconia (CSZ) using X-ray diffraction (XRD) and extended X-ray absorption fine structure (EXAFS) spectroscopy, respectively, measured at glancing angles. The implanted specimen was prepared at a helium fluence of 2 × 10 16 cm -2 using He + beams at two energies (2.54 and 2.74 MeV) passing through a 8.0 μm Al absorber foil. XRD results identified the formation of a new rhombohedral phase in the helium embedded layer, attributed to internal stress as a result of expansion of the CSZ-lattice. Zr K-edge EXAFS data suggested loss of crystallinity in the implanted lattice and disorder of the Zr atoms environment. EXAFS Fourier transforms analysis showed that the average first-shell radius of the Zr sbnd O pair in the implanted sample was slightly larger than that of the CSZ standard. Common general disorder features were explained by rhombohedral type short-range ordered clusters. The average structural parameters estimated from the EXAFS data of unimplanted and implanted CSZ are compared and discussed. Potential of EXAFS as a local probe of atomic-scale structural modifications induced by helium implantation in CSZ is demonstrated.

Effect of microwave treatment on structure of binders based on sodium carboxymethyl starch: FT-IR, FT-Raman and XRD investigations

NASA Astrophysics Data System (ADS)

Kaczmarska, Karolina; Grabowska, Beata; Spychaj, Tadeusz; Zdanowicz, Magdalena; Sitarz, Maciej; Bobrowski, Artur; Cukrowicz, Sylwia

2018-06-01

The paper deals with the influence of the microwave treatment on sodium carboxymethyl starch (CMS-Na) applied as a binder for moulding sands. The Fourier transformation infrared spectrometry (FT-IR), Raman spectroscopy (FT-Raman) and XRD analysis data of native potato starch and three different carboxymethyl starches (CMS-Na) with various degree of substitution (DS) before and after exposition to microwave radiation have been compared. FT-IR studies showed that polar groups present in CMS-Na structure take part in the formation of new hydrogen bonds network after water evaporation. However, these changes depend on DS value of the modified starch. The FT-Raman study confirmed that due to the impact on the samples by microwave, the changes of intensity in the characteristic bands associated with the crystalline regions in the sample were noticed. The X-ray diffraction data for microwave treated CMS-Na samples have been compared with the diffractograms of initial materials and analysis of XRD patterns confirmed that microwave-treated samples exhibit completely amorphous structure. Analysis of structural changes allows to state that the binding of sand grains in moulding sand with CMS-Na polymeric binder consists in the formation of hydrogen bonds networks (physical cross-linking).

Effect of microwave treatment on structure of binders based on sodium carboxymethyl starch: FT-IR, FT-Raman and XRD investigations.

PubMed

Kaczmarska, Karolina; Grabowska, Beata; Spychaj, Tadeusz; Zdanowicz, Magdalena; Sitarz, Maciej; Bobrowski, Artur; Cukrowicz, Sylwia

2018-06-15

The paper deals with the influence of the microwave treatment on sodium carboxymethyl starch (CMS-Na) applied as a binder for moulding sands. The Fourier transformation infrared spectrometry (FT-IR), Raman spectroscopy (FT-Raman) and XRD analysis data of native potato starch and three different carboxymethyl starches (CMS-Na) with various degree of substitution (DS) before and after exposition to microwave radiation have been compared. FT-IR studies showed that polar groups present in CMS-Na structure take part in the formation of new hydrogen bonds network after water evaporation. However, these changes depend on DS value of the modified starch. The FT-Raman study confirmed that due to the impact on the samples by microwave, the changes of intensity in the characteristic bands associated with the crystalline regions in the sample were noticed. The X-ray diffraction data for microwave treated CMS-Na samples have been compared with the diffractograms of initial materials and analysis of XRD patterns confirmed that microwave-treated samples exhibit completely amorphous structure. Analysis of structural changes allows to state that the binding of sand grains in moulding sand with CMS-Na polymeric binder consists in the formation of hydrogen bonds networks (physical cross-linking). Copyright © 2018 Elsevier B.V. All rights reserved.

Powder-XRD and (14) N magic angle-spinning solid-state NMR spectroscopy of some metal nitrides.

PubMed

Kempgens, Pierre; Britton, Jonathan

2016-05-01

Some metal nitrides (TiN, ZrN, InN, GaN, Ca3 N2 , Mg3 N2 , and Ge3 N4 ) have been studied by powder X-ray diffraction (XRD) and (14) N magic angle-spinning (MAS) solid-state NMR spectroscopy. For Ca3 N2 , Mg3 N2 , and Ge3 N4 , no (14) N NMR signal was observed. Low speed (νr  = 2 kHz for TiN, ZrN, and GaN; νr  = 1 kHz for InN) and 'high speed' (νr  = 15 kHz for TiN; νr  = 5 kHz for ZrN; νr  = 10 kHz for InN and GaN) MAS NMR experiments were performed. For TiN, ZrN, InN, and GaN, powder-XRD was used to identify the phases present in each sample. The number of peaks observed for each sample in their (14) N MAS solid-state NMR spectrum matches perfectly well with the number of nitrogen-containing phases identified by powder-XRD. The (14) N MAS solid-state NMR spectra are symmetric and dominated by the quadrupolar interaction. The envelopes of the spinning sidebands manifold are Lorentzian, and it is concluded that there is a distribution of the quadrupolar coupling constants Qcc 's arising from structural defects in the compounds studied. Copyright © 2015 John Wiley & Sons, Ltd.

Exploration of geo-mineral compounds in granite mining soils using XRD pattern data analysis

NASA Astrophysics Data System (ADS)

Koteswara Reddy, G.; Yarakkula, Kiran

2017-11-01

The purpose of the study was to investigate the major minerals present in granite mining waste and agricultural soils near and away from mining areas. The mineral exploration of representative sub-soil samples are identified by X-Ray Diffractometer (XRD) pattern data analysis. The morphological features and quantitative elementary analysis was performed by Scanning Electron Microscopy-Energy Dispersed Spectroscopy (SEM-EDS).The XRD pattern data revealed that the major minerals are identified as Quartz, Albite, Anorthite, K-Feldspars, Muscovite, Annite, Lepidolite, Illite, Enstatite and Ferrosilite in granite waste. However, in case of agricultural farm soils the major minerals are identified as Gypsum, Calcite, Magnetite, Hematite, Muscovite, K-Feldspars and Quartz. Moreover, the agricultural soils neighbouring mining areas, the minerals are found that, the enriched Mica group minerals (Lepidolite and Illite) the enriched Orthopyroxene group minerals (Ferrosilite and Enstatite). It is observed that the Mica and Orthopyroxene group minerals are present in agricultural farm soils neighbouring mining areas and absent in agricultural farm soils away from mining areas. The study demonstrated that the chemical migration takes place at agricultural farm lands in the vicinity of the granite mining areas.

Swelling induced by alpha decay in monazite and zirconolite ceramics: A XRD and TEM comparative study

NASA Astrophysics Data System (ADS)

Deschanels, X.; Seydoux-Guillaume, A. M.; Magnin, V.; Mesbah, A.; Tribet, M.; Moloney, M. P.; Serruys, Y.; Peuget, S.

2014-05-01

Zirconolite and monazite matrices are potential ceramics for the containment of actinides (Np, Cm, Am, Pu) which are produced over the reprocessing of spent nuclear fuel. Actinides decay mainly through the emission of alpha particles, which in turn causes most ceramics to undergo structural and textural changes (amorphization and/or swelling). In order to study the effects of alpha decays on the above mentioned ceramics two parallel approaches were set up. The first involved the use of an external irradiation source, Au, which allowed the deposited recoil energy to be simulated. The second was based on short-lived actinide doping with 238Pu, (i.e. an internal source), via the incorporation of plutonium oxide into both the monazite and zirconolite structures during synthesis. In both types of irradiation experiments, the zirconolite samples became amorphous at room temperature with damage close to 0.3 dpa; corresponding to a critical dose of 4 × 1018 α g-1 (i.e. ∼1.3 × 1021 keV cm-3). Both zirconolite samples also showed the same degree of macroscopic swelling at saturation (∼6%), with ballistic processes being the predominant damaging effect. In the case of the monazite however, the macroscopic swelling and amorphization were dependent on the nature of the irradiation. Externally, (Au), irradiated samples became amorphous while also demonstrating a saturation swelling of up to 8%. In contrast to this, the swelling of the 238Pu doped samples was much smaller at ∼1%. Also, unlike the externally (Au) irradiated monazite these 238Pu doped samples remained crystalline up to 7.5 × 1018 α g-1 (0.8 dpa). XRD, TEM and swelling measurements were used to fully characterize and interpret this behavior. The low swelling and the conservation of the crystalline state of 238Pu doped monazite samples indicates that alpha annealing took place within this material.

In-situ XRD vs ex-situ vacuum annealing of tantalum oxynitride thin films: Assessments on the structural evolution

NASA Astrophysics Data System (ADS)

Cunha, L.; Apreutesei, M.; Moura, C.; Alves, E.; Barradas, N. P.; Cristea, D.

2018-04-01

The purpose of this work is to discuss the main structural characteristics of a group of tantalum oxynitride (TaNxOy) thin films, with different compositions, prepared by magnetron sputtering, and to interpret and compare the structural changes, by X-ray diffraction (XRD), when the samples are vacuum annealed under two different conditions: i) annealing, followed by ex-situ XRD: one sample of each deposition run was annealed at a different temperature, until a maximum of 800 °C, and the XRD patterns were obtained, at room temperature, after each annealing process; ii) annealing with in-situ XRD: the diffraction patterns are obtained, at certain temperatures, during the annealing process, using always the same sample. In-situ XRD annealing could be an interesting process to perform annealing, and analysing the evolution of the structure with the temperature, when compared to the classical process. A higher structural stability was observed in some of the samples, particularly on those with highest oxygen content, but also on the sample with non-metal (O + N) to metal (Ta) ratio around 0.5.

Effect of H2O on the morphological changes of KNO3 formed on K2O/Al2O3 NOx storage materials: Fourier transform infra-red (FTIR) and time-resolved x-ray diffraction (TR-XRD) studies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Do Heui; Mudiyanselage, Kumudu K.; Szanyi, Janos

Based on combined FTIR and XRD studies, we report here that H2O induces a morphological change of KNO3 species formed on model K2O/Al2O3 NOx storage-reduction catalysts. Specifically as evidenced by FTIR, the contact of H2O with NO2 pre-adsorbed on K2O/Al2O3 promotes the transformation from bidentate (surface-like) KNO3 species to ionic (bulk-like) ones irrespective of K loadings. Once H2O is removed from the sample, a reversible transformation into bidentate KNO3 is observed, demonstrating a significant dependence of H2O on such morphological changes. TR-XRD results show the formation of two different types of bulk KNO3 phases (orthorhomobic and rhombohedral) in an as-impregnatedmore » sample. Once H2O begins to desorb above 400 K, the former is transformed into the latter, resulting in the existence of only the rhombohedral KNO3 phase. On the basis of consistent FTIR and TR-XRD results, we propose a model for the morphological changes of KNO3 species with respect to NO2 adsorption/desorption, H2O and/or heat treatments. Compared with the BaO/Al2O3 system, K2O/Al2O3 shows some similarities with respect to the formation of bulk nitrates upon H2O contact. However, there are significant differences that originate from the lower melting temperature of KNO3 relative to Ba(NO3)2.« less

Coupling XRD, EXAFS, and 13C NMR to study the effect of the carbon stoichiometry on the local structure of UC(1±x).

PubMed

Carvajal Nuñez, U; Martel, L; Prieur, D; Lopez Honorato, E; Eloirdi, R; Farnan, I; Vitova, T; Somers, J

2013-10-07

A series of uranium carbide samples, prepared by arc melting with a C/U ratio ranging from 0.96 to 1.04, has been studied by X-ray diffraction (XRD), (13)C nuclear magnetic resonance (NMR), and extended X-ray absorption fine structure (EXAFS). XRD determines phase uniqueness and the increase of the lattice parameter versus the carbon content. In contrast, (13)C NMR detects the different carbon environments in the lattice and in this study, clearly identifies the presence of discrete peaks for carbon in the octahedral lattice site in UC and an additional peak associated with excess carbon in hyperstoichiometric samples. Two peaks associated with different levels of carbon deficiency are detected for all hypostoichiometric compositions. More than one carbon environment is always detected by (13)C NMR. This exemplifies the difficulty in obtaining a perfect stoichiometric uranium monocarbide UC(1.00). The (13)C MAS spectra of uranium carbides exhibit the effects resulting from the carbon content on both the broadening of the peaks and on the Knight shift. An abrupt spectral change occurs between hypo- and hyperstoichiometric samples. The results obtained by EXAFS highlight subtle differences between the different stoichiometries, and in the hyperstoichiometric samples, the EXAFS results are consistent with the excess carbon atoms being in the tetrahedral interstitial position.

Real-Time XRD Studies of Li-O2 Electrochemical Reaction in Nonaqueous Lithium-Oxygen Battery.

PubMed

Lim, Hyunseob; Yilmaz, Eda; Byon, Hye Ryung

2012-11-01

Understanding of electrochemical process in rechargeable Li-O2 battery has suffered from lack of proper analytical tool, especially related to the identification of chemical species and number of electrons involved in the discharge/recharge process. Here we present a simple and straightforward analytical method for simultaneously attaining chemical and quantified information of Li2O2 (discharge product) and byproducts using in situ XRD measurement. By real-time monitoring of solid-state Li2O2 peak area, the accurate efficiency of Li2O2 formation and the number of electrons can be evaluated during full discharge. Furthermore, by observation of sequential area change of Li2O2 peak during recharge, we found nonlinearity of Li2O2 decomposition rate for the first time in ether-based electrolyte.

The XRD Amorphous Component in John Klein Drill Fines at Yellowknife Bay, Gale Crater, Mars

NASA Technical Reports Server (NTRS)

Morris, Richard V.; Ming,, Douglas W.; Blake, David; Vaniman, David; Bish, David L; Chipera, Steve; Downs, Robert; Morrison, Shaunna; Gellert, Ralf; Campbell, Iain;

Characterisation of 1,3-diammonium propylselenate monohydrate by XRD, FT-IR, FT-Raman, DSC and DFT studies

NASA Astrophysics Data System (ADS)

Thirunarayanan, S.; Arjunan, V.; Marchewka, M. K.; Mohan, S.; Atalay, Yusuf

2016-03-01

The crystals of 1,3-diammonium propylselenate monohydrate (DAPS) were prepared and characterised X-ray diffraction (XRD), FT-IR, FT-Raman spectroscopy, and DFT/B3LYP methods. It comprises protonated propyl ammonium moieties (diammonium propyl cations), selenate anions and water molecule which are held together by a number of hydrogen bonds and form infinite chains. The XRD data confirm the transfer of two protons from selenic acid to 1,3-diaminopropane molecule. The DAPS complex is stabilised by the presence of O-H···O and N-H···O hydrogen bonds and the electrostatic interactions as well. The N···O and O···O bond distances are 2.82-2.91 and 2.77 Å, respectively. The FT-IR and FT-Raman spectra of 1,3-diammonium propyl selenate monohydrate are recorded and the complete vibrational assignments have been discussed. The geometry is optimised by B3LYP method using 6-311G, 6-311+G and 6-311+G* basis sets and the energy, structural parameters, vibrational frequencies, IR and Raman intensities are determined. Differential scanning colorimetry (DSC) data were also presented to analyse the possibility of the phase transition. Complete natural bonding orbital (NBO) analysis is carried out to analyse the intramolecular electronic interactions and their stabilisation energies. The electrostatic potential of the complex lies in the range +1.902e × 10-2 to -1.902e × 10-2. The limits of total electron density of the complex is +8.43e × 10-2 to -8.43e × 10-2.

Operando XRD studies as a tool for determination of transport parameters of mobile ions in electrode materials

NASA Astrophysics Data System (ADS)

Kondracki, Łukasz; Kulka, Andrzej; Świerczek, Konrad; Ziąbka, Magdalena; Molenda, Janina

2017-11-01

In this work a detailed operando XRD investigations of structural properties of LixMn2O4 manganese spinel are shown to be a complementary, successful method of determination of diffusion coefficient D and surface exchange coefficient k in the working electrode. Kinetics of lithium ions transport are estimated on the basis of rate of structural changes of the cathode material during a relaxation stage after a high current charge, i.e. during structural relaxation of the material. The presented approach seems to be applicable as a complementary method of determination of transport coefficients for all intercalation-type electrode materials.

XRD and XAS structural study of CuAlO2 under high pressure.

PubMed

Pellicer-Porres, J; Segura, A; Ferrer-Roca, Ch; Polian, A; Munsch, P; Kim, D

2013-03-20

We present the results of x-ray diffraction and x-ray absorption spectroscopy experiments in CuAlO(2) under high pressure. We discuss the polarization dependence of the x-ray absorption near-edge structure at the Cu K-edge. XRD under high pressure evidences anisotropic compression, the a-axis being more compressible than the c-axis. EXAFS yields the copper-oxygen bond length, from which the only internal parameter of the delafossite structure is deduced. The combination of anisotropic compression and the internal parameter decrease results in a regularization of the AlO(6) octahedra. The anisotropic compression is related to the chemical trends observed in the lattice parameters when Al is substituted by other trivalent cations. Both experiments evidence the existence of an irreversible phase transition that clearly manifests at 35 ± 2 GPa. The structure of the high-pressure polymorph could not be determined, but it implies a change of the Cu environment, which remains anisotropic. Precursor effects are observed from the lowest pressures, which are possibly related to crystal breaking at a submicroscopic scale with partial reorientation of the crystallites.

XRD and XAS structural study of CuAlO2 under high pressure

NASA Astrophysics Data System (ADS)

Pellicer-Porres, J.; Segura, A.; Ferrer-Roca, Ch; Polian, A.; Munsch, P.; Kim, D.

2013-03-01

We present the results of x-ray diffraction and x-ray absorption spectroscopy experiments in CuAlO2 under high pressure. We discuss the polarization dependence of the x-ray absorption near-edge structure at the Cu K-edge. XRD under high pressure evidences anisotropic compression, the a-axis being more compressible than the c-axis. EXAFS yields the copper-oxygen bond length, from which the only internal parameter of the delafossite structure is deduced. The combination of anisotropic compression and the internal parameter decrease results in a regularization of the AlO6 octahedra. The anisotropic compression is related to the chemical trends observed in the lattice parameters when Al is substituted by other trivalent cations. Both experiments evidence the existence of an irreversible phase transition that clearly manifests at 35 ± 2 GPa. The structure of the high-pressure polymorph could not be determined, but it implies a change of the Cu environment, which remains anisotropic. Precursor effects are observed from the lowest pressures, which are possibly related to crystal breaking at a submicroscopic scale with partial reorientation of the crystallites.

Structural studies with the use of XRD and Mössbauer spectroscopy of new high Manganese steels

NASA Astrophysics Data System (ADS)

Jablonska, Magdalena Barbara

2014-04-01

New high-strength austenitic and austenitic-ferritic manganese steels represent a significant potential in applications for structural components in the automotive and railway industry due to the excellent combination of high mechanical properties and good plasticity. They belong to the group of steels called AHSS (Advanced High Strength Steels) and UHSS (Ultra High Strength Steels). Application of this combination of properties allows a reduction in the weight of vehicles by the use of reduced cross-section components, and thus to reduce fuel consumption. The development and implementation of industrial production of such interesting and promising steel and its use as construction material requires an improvement of their casting properties and susceptibility to deformation in plastic working conditions. In this work, XRD, Transmission Mössbauer Spectroscopy and Conversion Electron Mössbauer Spectroscopy were employed in a study of the new high-manganese steels with a austenite and austenite-ferrite structure. The influence of the plastic deformation parameters on the changes in the structure, distribution of ferrite and disclosure of the presence of carbides was determined. The analysis of phase transformations in various times using CEMS method made possible to reveal their fine details.

XRF, μ-XRD and μ-spectroscopic techniques for revealing the composition and structure of paint layers on polychrome sculptures after multiple restorations.

PubMed

Franquelo, M L; Duran, A; Castaing, J; Arquillo, D; Perez-Rodriguez, J L

2012-01-30

This paper presents the novel application of recently developed analytical techniques to the study of paint layers on sculptures that have been restored/repainted several times across centuries. Analyses were performed using portable XRF, μ-XRD and μ-Raman instruments. Other techniques, such as optical microscopy, SEM-EDX and μ-FTIR, were also used. Pigments and other materials including vermilion, minium, red lac, ivory black, lead white, barium white, zinc white (zincite), titanium white (rutile and anatase), lithopone, gold and brass were detected. Pigments from both ancient and modern times were found due to the different restorations/repaintings carried out. μ-Raman was very useful to characterise some pigments that were difficult to determine by μ-XRD. In some cases, pigments identification was only possible by combining results from the different analytical techniques used in this work. This work is the first article devoted to the study of sculpture cross-section samples using laboratory-made μ-XRD systems. Copyright © 2011 Elsevier B.V. All rights reserved.

The importance of XRD analysis in provenance and palaeoenvironmental studies of the Piedras de Afilar Formation, Neoproterozoic of Uruguay

NASA Astrophysics Data System (ADS)

Pamoukaghlian, K.; Poiré, D. G.; Gaucher, C.; Uriz, N.; Cingolani, C.; Frigeiro, P.

2009-04-01

The Piedras de Afilar Formation crops out in the southeast part of Uruguay, forming part of the Tandilia Terrane (sensu Bossi et al. 2005). Pamoukaghlian et al. (2006) and Gaucher et al. (2008) have published δ13C, δ18O and U/Pb SHRIMP results, which indicate a Neoproterozoic age for this formation. The palaeoenvironment has been defined as a shallow marine platform based on the presence of interference ripples, hummocky and mega-hummocky cross-stratification. X-ray diffraction (XRD) analyses help to better constrain the palaeoenvironment: the presence of chlorite/smectite found in black shales, suggest a reducing environment, and abundant illite indicates a cold to temperate climate. Provenance studies have been undertaken that utilise a combination of detailed palaeocurrent measurements, petrographic descriptions, XRD analyses, and geochemical isotopic analyses, including U/Pb SHRIMP determinations. Mineral compositional diagrams for sandstones suggest a stable cratonic provenance. Palaeocurrents are mainly from the NNE, indicating a provenance from the cratonic areas of the Tandilia Terrane. The illite crystal index indicates diagenetic to low-metamorphic conditions for the sequence; this is important to confirm that the identified minerals are authigenic. Clay minerals identified by XRD analysis of sandstones from the siliciclastic member are illite (80 - 90%), kaolinite (5 - 10%), and chlorite (5 - 10%). This is consistent with a provenance from the cratonic areas (quartz-feldspar dominated rock types). Isotopic analyses have been undertaken to provide better constraints on the tectonic setting. U/Pb SHRIMP ages for the youngest zircons are 990 Ma (Gaucher et al. 2008), and the basal granite (Granito de la Paz) is 2056 ± 11 Ma (Hartmann et al. 2001), suggesting a provenance from the Archaean basement for the Piedras de Afilar Formation, like its counterparts in the Rio de la Plata Craton. References Bossi, J., Piñeyro, D., Cingolani, C. (2005). El l

Mercury Retention and Accumulation by Plants at the Abandoned New Idria Mine Site - a Preliminary micro-XRF and micro-XRD Study

NASA Astrophysics Data System (ADS)

Siebner, H.; Webb, S. M.; Brown, G. E.

2008-12-01

Due to its high toxicity and increasing levels in ecosystems, Hg pollution has become a serious global problem. A lot of research has been conducted with regard to Hg biogeochemical cycles in aquatic systems. Much less is known about terrestrial Hg-cycles in general and in plants specifically. Plants play an important role in these cycles; they are known to be an important sink for both atmospheric and soil Hg, the vegetative cover significantly influences soil erosion and migration of contaminants into aquatic systems. However, the processes involved in the interactions of Hg with plants and plants products are poorly studied. Information concerning the interaction of Hg in plants at the molecular level is sparse. The present study is intended to provide new information on Hg retention, translocation, and accumulation in plants associated with mercury mine wastes in central California. We present here preliminary results of Hg distribution in root and leave samples, taken from different plant species, which have adapted to the hostile environment at the New Idria site. Samples were taken at two locations that differ in water acidity and flooding regime. The distribution of Hg appears to be affected by plant species, growing conditions, and development stage. Micro-XRF images of root sections show that Hg is mainly associated with Fe plaque at the outer surfaces and epidermis, but is distributed differently in roots of the two plants. Micro-XRD showed evidence for mineralogical changes in the plaque through the sections. Mercury in leaves was found to be highly diffuse in its distribution, and is not associated with Fe-rich particles attached to the outer surface of the leaf. This finding implies that Hg is assimilated in the leaf tissue. Further examination of Fe plaque characteristics and associated Hg, as well as Hg speciation in the different organs of these plants, is being conducted in our lab.

Multiscale structural characterizations of mixed U(iv)-An(iii) oxalates (An(iii) = Pu or Am) combining XAS and XRD measurements.

PubMed

Arab-Chapelet, B; Martin, P M; Costenoble, S; Delahaye, T; Scheinost, A C; Grandjean, S; Abraham, F

2016-04-28

Mixed actinide(III,IV) oxalates of the general formula M2.2UAn(C2O4)5·nH2O (An = Pu or Am and M = H3O(+) and N2H5(+)) have been quantitatively precipitated by oxalic precipitation in nitric acid medium (yield >99%). Thorough multiscale structural characterization using XRD and XAS measurements confirmed the existence of mixed actinide oxalate solid solutions. The XANES analysis confirmed that the oxidation states of the metallic cations, tetravalent for uranium and trivalent for plutonium and americium, are maintained during the precipitation step. EXAFS measurements show that the local environments around U(+IV), Pu(+III) and Am(+III) are comparable, and the actinides are surrounded by ten oxygen atoms from five bidentate oxalate anions. The mean metal-oxygen distances obtained by XAS measurements are in agreement with those calculated from XRD lattice parameters.

Heteropolyhedral silver compounds containing the polydentate ligand N,N,O-E-[6-(hydroxyimino)ethyl]-1,3,7-trimethyllumazine. Preparation, spectral and XRD structural study and AIM calculations.

PubMed

Jiménez-Pulido, Sonia B; Hueso-Ureña, Francisco; Fernández-Liencres, M Paz; Fernández-Gómez, Manuel; Moreno-Carretero, Miguel N

2013-01-14

The oxime derived from 6-acetyl-1,3,7-trimethyllumazine (1) ((E-6-(hydroxyimino)ethyl)-1,3,7-trimethylpteridine-2,4(1H,3H)-dione, DLMAceMox) has been prepared and its molecular and crystal structure determined from spectral and XRD data. The oxime ligand was reacted with silver nitrate, perchlorate, thiocyanate, trifluoromethylsulfonate and tetrafluoroborate to give complexes with formulas [Ag(2)(DLMAceMox)(2)(NO(3))(2)](n) (2), [Ag(2)(DLMAceMox)(2)(ClO(4))(2)](n) (3), [Ag(2)(DLMAceMox)(2)(SCN)(2)] (4), [Ag(2)(DLMAceMox)(2)(CF(3)SO(3))(2)(CH(3)CH(2)OH)]·CH(3)CH(2)OH (5) and [Ag(DLMAceMox)(2)]BF(4) (6). Single-crystal XRD studies show that the asymmetrical residual unit of complexes 2, 3 and 5 contains two quite different but connected silver centers (Ag1-Ag2, 2.9-3.2 Å). In addition to this, the Ag1 ion displays coordination with the N5 and O4 atoms from both lumazine moieties and a ligand (nitrato, perchlorato or ethanol) bridging to another disilver unit. The Ag2 ion is coordinated to the N61 oxime nitrogens, a monodentate and a (O,O)-bridging nitrato/perchlorato or two monodentate O-trifluoromethylsulfonato anions. The coordination polyhedra can be best described as a strongly distorted octahedron (around Ag1) and a square-based pyramid (around Ag2). The Ag-N and Ag-O bond lengths range between 2.22-2.41 and 2.40-2.67 Å, respectively. Although the structure of 4 cannot be resolved by XRD, it is likely to be similar to those described for 2, 3 and 5, containing Ag-Ag units with S-thiocyanato terminal ligands. Finally, the structure of the tetrafluoroborate compound 6 is mononuclear with a strongly distorted tetrahedral AgN(4) core (Ag-N, 2.27-2.43 Å). Always, the different Ag-N distances found clearly point to the more basic character of the oxime N61 nitrogen atom when compared with the pyrazine N5 one. A topological analysis of the electron density within the framework provided by the quantum theory of atoms in molecules (QTAIM) using DFT(M06L) levels of

Studies the alterations of biochemical and mineral contents in bone tissue of mus musculus due to aluminum toxicity and the protective action of desferrioxamine and deferiprone by FTIR, ICP-OES, SEM and XRD techniques.

PubMed

Sivakumar, S; Khatiwada, Chandra Prasad; Sivasubramanian, J

2014-05-21

The present study has attempt to analyze the changes in the biochemical and mineral contents of aluminum intoxicated bone and determine the protective action of desferrioxamine (DFO) and deferiprone (DFP) by using Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), inductively coupled plasma optical emission spectroscopy (ICP-OES), and scanning electron microscopy (SEM) techniques for four groups of animals such as control (Group I), aluminum intoxicated (Group II), Al+DFP (Group III) and Al+DFO+DFP (Group IV) treated groups respectively. The FTIR spectra of the aluminum intoxicated bone showed significant alteration in the biochemical constituents. The bands ratio at I1400/I877 significantly decreased from control to aluminum, but enhanced it by Al+DFP to Al+DFO+DFP treated bone tissue for treatments of 16 weeks. This result suggests that DFO and DFP are the carbonate inhibitor, recovered from chronic growth of bone diseases and pathologies. The alteration of proteins profile indicated by Amide I and Amide II, where peak area values decreased from control to aluminum respectively, but enhanced by treated with DFP (p.o.) and DFO+DFP (i.p.) respectively. The XRD analysis showed a decrease in crystallinity due to aluminum toxicity. Further, the Ca, Mg, and P contents of the aluminum exposed bone were less than those of the control group, and enhanced by treatments with DFO and DFP. The concentrations of trace elements were found by ICP-OES. Therefore, present study suggests that due to aluminum toxicity severe loss of bone minerals, decrease in the biochemical constituents and changes in the surface morphology. Copyright © 2014 Elsevier B.V. All rights reserved.

Nano Cu interaction with single amino acid tyrosine derived self-assemblies; study through XRD, AFM, confocal Raman microscopy, SERS and DFT methods

NASA Astrophysics Data System (ADS)

Govindhan, Raman; Karthikeyan, Balakrishnan

2017-12-01

3,5-Bis(trifluoromethyl)benzylamine derivatives of single amino acid tyrosine produced self-assembled nanotubes (BTTNTs) as simple Phe-Phe. It has been observed that tyrosine derivative gives exclusively micro and nano tubes irrespective of the concentration of the precursor monomer. However, the introduced xenobiotic trifluoromethyl group (TFM) present in key backbone positionsof the self assembly gives the specific therapeutic function has been highlighted. Herein this work study of such self assembled nanotubes were studied through experimental and theoretical methods. The interaction of nanocopper cluster with the nanotubes (Cu@BTTNTs) were extensively studied by various methods like XRD, AFM, confocal Raman microscopy, SERS and theoretical methods like Mulliken's atomic charge analysis. SERS reveals that the interactions of Cu cluster with NH2, OH, NH and phenyl ring π-electrons system of BTTNTs. DFT studies gave the total dipole moment values of Cu@BTTNTs and explained the nature of interaction.

Elucidation of reaction mechanism involved in the formation of LaNiO3 from XRD and TG analysis

NASA Astrophysics Data System (ADS)

Dharmadhikari, Dipti V.; Athawale, Anjali A.

2013-06-01

The present work is focused on the synthesis and elucidation of reaction mechanism involved in the formation of LaNiO3 with the help of X-ray diffraction (XRD) and thermogravimetric (TG) analysis. LaNiO3 was synthesized by hydrothermal method by heating at 160°C under autogenous pressure for 6h. Pure phase product was obtained after calcining the hydrothermally activated product for 6h at 700°C. The various phases of the product obtained after hydrothermal treatment and calcination followed by the formation of pure phase nanocrystalline lanthanum nickel oxide could be determined from XRD analysis of the samples. The reaction mechanism and phase formation temperature has been interpreted by thermogravimetric analysis of the hydrothermally synthesized product and XRD analysis.

XRD and solid state 13C-NMR evaluation of the crystallinity enhancement of 13C-labeled bacterial cellulose biosynthesized by Komagataeibacter xylinus under different stimuli: A comparative strategy of analyses.

PubMed

Meza-Contreras, Juan C; Manriquez-Gonzalez, Ricardo; Gutiérrez-Ortega, José A; Gonzalez-Garcia, Yolanda

2018-05-22

The production and crystallinity of 13 C bacterial cellulose (BC) was examined in static culture of Komagataeibacter xylinus with different chemical and physical stimuli: the addition of NaCl or cloramphenicol as well as exposure to a magnetic field or to UV light. Crystalline BC biosynthesized under each stimulus was studied by XRD and solid state 13 C NMR analyses. All treatments produced BC with enhanced crystallinity over 90% (XRD) and 80% (NMR) compared to the control (83 and 76%, respectively) or to Avicel (77 and 62%, respectively). The XRD data indicated that the crystallite size was 80-85 Å. Furthermore, changes on the allomorphs (I α and I β ) ratio tendency of BC samples addressed to the stimuli were estimated using the C4 signal from 13 C NMR data. These results showed a decrease of the allomorph I α (3%) when BC was biosynthesized with UV light and chloramphenicol compared to control (58.79%). In contrast, the BC obtained with NaCl increased up to 60.31% of the I α allomorph ratio. Copyright © 2018 Elsevier Ltd. All rights reserved.

A.C. impedance, XRD, DSC, SEM and charge/discharge studies on Al2O3, TiO2, SiO2 dispersoid LiPF6/PVC/PVdF-co-HFP composite polymer electrolytes by phase inversion

NASA Astrophysics Data System (ADS)

Vickraman, P.; Gopukumar, S.

2017-07-01

The PVC/PVdF-co-HFP composite polymer electrolyte membranes (CPEMs) by varying blend ratios 1:1, 1:2, and 2:1 with fixed content of Al2O3, TiO2 and SiO2 having soaked in 0.5 M LiPF6 in EC/DEC (1:1) v/v) have been prepared by phase inversion. CPEMs of higher ionic conductivity (not dependent on electrolyte uptake as observed in our study) ASA4 (3.61×10-4 Scm-1), TSA3 (1.53×10-4 Scm-1), and SSA3 (4.81×10-4 Scm-1) have been only chosen for XRD, DSC, SEM and electrochemical studies. In XRD, crystalline peaks (phases) of PVdF have been noted with/without change in intensity as well as FWHM which correspond to type of filler interaction with host matrix. In DSC, it is observed that shifts in baseline, melting endotherms, and area under the endotherms indicating the thermal hist ory of PVC (Tg = 82 ° C) and melting of VdF crystallites varied with nature of the filler dispersoid. In SEM, the coagulated fibrils of the polymer coiled with the sponge like structure has been mapped. The charge/discharge studies are carried out on these CPEMs at C/10 rate in the voltage range 2.8 V - 4.2 V, and it is noted that the TSA3 showed better cycling performance with good capacity retention i.e., 50 cycles with 66% capacity retention than ASA4 of 28 cycles with 65% and SSA3 of 5 cycles with 56%. In the present study Coulombic efficiency is concerned only for first cycle and it is noted that the TSA3 showed 71% than 66% and 62% respectively for SSA3 and ASA4.

Synthetic, XRD, non-covalent interactions and solvent dependent nonlinear optical studies of Sulfadiazine-Ortho-Vanillin Schiff base: (E)-4-((2-hydroxy-3-methoxy- benzylidene) amino)-N-(pyrimidin-2-yl)benzene-sulfonamide

NASA Astrophysics Data System (ADS)

Shahid, Muhammad; Salim, Muhammad; Khalid, Muhammad; Tahir, Muhammad Nawaz; Khan, Muhammad Usman; Braga, Ataualpa Albert Carmo

2018-06-01

In this study, Sulfadiazine-Ortho-Vanillin Schiff base namely (E)-4-((2-hydroxy-3-methoxybenzylidene)amino)sbnd N-(pyrimidin-2-yl)benzene-sulfonamide (BS) was synthesized. Chemical characterization and computational studies using different techniques like XRD, FT-IR, UV-Vis, NBO, FMO, and MEP have been employed. Density functional theory (DFT) calculations have been performed at M06-2X/6-311 + G(d,p) level of theory to obtain optimized geometry and vibrational wave numbers for (E)-4-((2-hydroxy-3-methoxybenzylidene)amino)sbnd N-(pyrimidin-2-yl)benzene-sulfonamide (BS). The DFT optimized geometry supports the experimental XRD parameters. Frontier molecular orbital (FMO) energies and molecular electrostatic potential (MEP) surfaces have been executed at M06-2X/6-311 + G(d,p) level of theory. NBO analysis has been carried out at M06-2X/6-311 + G(d,p) level which not only discovered the hyper conjugative interactions and stability in title molecule but also reconfirmed the existence of Nsbnd H⋯N hydrogen bonds between the dimer. The findings of small EHOMO-ELUMO gap shows less hardness and larger softness values which suggested the bioactiveness of the title molecule. Finally, the effect of solvent on nonlinear optical (NLO) properties has been executed using M06-2X level of theory and 6-311 + G (d,p) basis set. The solvent polarity enhanced the NLO response from 3.62 × 10-30 esu to 4.66 × 10-30 esu indicating the considerable NLO character hence in general may have potential applications in the development of non-linear optical materials.

Laboratory Detection and Analysis of Organic Compounds in Rocks Using HPLC and XRD Methods

NASA Technical Reports Server (NTRS)

Dragoi, D.; Kanik, I.; Bar-Cohen, Y.; Sherrit, S.; Tsapin, A.; Kulleck, J.

2004-01-01

In this work we describe an analytical method for determining the presence of organic compounds in rocks, limestone, and other composite materials. Our preliminary laboratory experiments on different rocks/limestone show that the organic component in mineralogical matrices is a minor phase on order of hundreds of ppm and can be better detected using high precision liquid chromatography (HPLC). The matrix, which is the major phase, plays an important role in embedding and protecting the organic molecules from the harsh Martian environment. Some rocks bear significant amounts of amino acids therefore, it is possible to identify these phases using powder x-ray diffraction (XRD) by crystallizing the organic. The method of detection/analysis of organics, in particular amino acids, that have been associated with life will be shown in the next section.

EPR, SEM and XRD investigation of ornamental limestone and marbles from some renowned Romanian quarries.

NASA Astrophysics Data System (ADS)

Covaci, D.; Costea, C.; Dumitras, D.; Duliu, O. G.

2012-04-01

Ornamental limestone and marble samples were collected and analysed by means of Electron Paramagnetic Resonance (EPR), Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD), in order to evidence any systematic peculiarities able to be used in further provenance studies as well as to get more detailed information regarding geochemistry and mineralogy of three of the most important deposits from Romania. In this respect, 20 samples of limestone (Arnota quarry, Capatani Mountains and Mateias South quarry, Iezer Mountains) and 9 of calci-dolomitic marble (Porumbacu de Sus quarry, Fagaras Mountains) were collected over a significant sampling area. EPR spectroscopy, primarily used to asset the degree of homogeneity of considered samples, evidenced, for both Arnota and Mateias South limestone, the presence of a typical six hyperfine lines spectrum of Mn2+ ions in calcite but no traces of Fe ferromagnetic clusters. A more careful investigation has showed that although within the same quarry, there were no significant differences regarding EPR spectra, the resonance lines were systematic narrower in the case of Mateias South samples which suggested a lower content of divalent manganese ions. The Porumbacu calci-dolomitic marble, presented a more intricate Mn2+ spectrum, consisting of a superposition of typical dolomitic and calcitic spectra. Again, the EPR spectra were almost identical, attesting, as in the previous cases, a relative uniform distribution of paramagnetic Mn2+ ions within quarry. In the case of SEM, scattered, back scattered and absorbed electron modes were used to visualise the mineral formations on the sample surfaces while an EDAX quantitative analysis was used to determine the content of the most abundant elements. Although, at a first inspection, both groups of limestone looked almost similar, displaying a great variety of randomly orientated micro-crystalline agglomeration, only in the case of Arnota samples, we have noticed the presence of

Investigation of structural resorption behavior of biphasic bioceramics with help of gravimetry, μCT, SEM, and XRD.

PubMed

de Wild, Michael; Amacher, Fabienne; Bradbury, Christopher R; Molenberg, Aart

2016-04-01

Resorbable bone substitute materials are widely used for bone augmentation after tumor resection, parallel to implant placement, or in critical size bone defects. In this study, the structural dissolution of a biphasic calcium phosphate bone substitute material with a hydroxyapatite (HA)/tricalcium phosphate (β-TCP) ratio of 60/40 was investigated by repeatedly placing porous blocks in EDTA solution at 37 °C. At several time points, the blocks were investigated by SEM, µCT, and gravimetry. It was found that always complete 2-3 µm sized grains were removed from the structure and that the β-TCP is dissolved more rapidly. This selective dissolution of the β-TCP grains was confirmed by XRD measurements. The blocks were eroded from the outside toward the center. The structure remained mechanically stable because the central part showed a delayed degradation and because the slower dissolving HA grains preserved the integrity of the structure. © 2015 Wiley Periodicals, Inc.

Comparative investigation of Fourier Transform Infrared (FT-IR) spectroscopy and X-ray Diffraction (XRD) in the determination of cotton fiber crystallinity

USDA-ARS?s Scientific Manuscript database

Despite considerable efforts in developing the curve-fitting protocol to evaluate the crystallinity index (CI) from the X-ray diffraction (XRD) measurement, in its present state XRD procedure can only provide a qualitative or semi-quantitative assessment of the amounts of crystalline or amorphous po...

XRD monitoring of α self-irradiation in uranium-americium mixed oxides.

PubMed

Horlait, Denis; Lebreton, Florent; Roussel, Pascal; Delahaye, Thibaud

2013-12-16

The structural evolution under (241)Am self-irradiation of U(1-x)Am(x)O(2±δ) transmutation fuels (with x ≤ 0.5) was studied by X-ray diffraction (XRD). Samples first underwent a preliminary heat treatment performed under a reducing atmosphere (Ar/H2(4%)) aiming to recover the previously accumulated structural defects. Over all measurements (carried out over up to a full year and for integrated doses up to 1.5 × 10(18) α-decay events·g(-1)), only fluorite U(1-x)Am(x)O(2±δ) solid solutions were observed. Within a few days after the end of the heat treatment, each of the five studied samples was slowly oxidized as a consequence of their move to air atmosphere, which is evidenced by XRD by an initial sharp decrease of the unit cell parameter. For the compounds with x ≤ 0.15, this oxidation occurred without any phase transitions, but for U0.6Am0.4O(2±δ) and U0.5Am0.5O(2±δ), this process is accompanied by a transition from a first fluorite solid solution to a second oxidized one, as the latter is thermodynamically stable in ambient conditions. In the meantime and after the oxidation process, (241)Am α self-irradiation caused a structural swelling up to ∼0.8 vol %, independently of the sample composition. The kinetic constants of swelling were also determined by regression of experimental data and are, as expected, dependent on x and thus on the dose rate. The normalization of these kinetic constants by sample α-activity, however, leads to very close swelling rates among the samples. Finally, evolutions of microstrain and crystallite size were also monitored, but for the considered dose rates and cumulated doses, α self-irradiation was found, within the limits of the diffractometer used, to have almost no impact on these characteristics. Microstrain was found to be influenced instead by the americium content in the materials (i.e., by the impurities associated with americium starting material and the increase of cationic charge heterogeneity with

A MS, SEM-EDX and XRD study of Ti or Cu-doped zinc ferrites as regenerable sorbents for hot coal gas desulfurization

NASA Astrophysics Data System (ADS)

Ahmed, M. A.; García, E.; Alonso, L.; Palacios, J. M.

2000-02-01

Kinetic studies in thermobalance carried out by several authors previously have shown that small concentrations of TiO 2 or CuO can increase substantially the overall sulfidation rate of zinc ferrites, as regenerable sorbents for hot coal gas desulfurization. These oxides modify the textural properties of both the fresh or regenerated and the sulfided sorbent, modifying consequently the sulfidation rate because it is a partially diffusion-controlled process. However, by using grain models it is shown that most of the observed changes are due to changes in the intrinsic reactivity of the sorbent. Detailed studies of characterization in previous papers using different techniques have failed in revealing differential chemical changes that could be associated with a different behavior. In fact, the only significant changes observed in these studies were an apparent disappearance in fresh sorbents calcined at very high temperatures of the Raman effect, and a slight shift of the XPS binding energy of Fe levels, indicating a probable site migration and/or a change of the oxidation state. These characterization results, however, were not completely conclusive and additional efforts should be undertaken. In this paper more sensitive techniques such as Mössbauer spectroscopy (MS), powder X-ray diffraction (XRD) and scanning electron microscopy (SEM-EDX), have been used for the characterization of fresh, regenerated and sulfided sorbents. The study shows that the addition of TiO 2 or CuO induce substantial structural changes in zinc ferrites that can explain their apparent enhancing effect on the overall sulfidation reactivity. Additionally, this effect is decreased as the number of sulfidation-regeneration cycles increases, probably explaining the performance decay exhibited by these sorbents in multicycle tests in a fixed bed reactor.

XRD measurement of mean crystallite thickness of illite and illite/smectite: Reappraisal of the Kubler index and the Scherrer equation

USGS Publications Warehouse

Drits, Victor A.; Środoń, Jan; Eberl, D.D.

1997-01-01

The standard form of the Scherrer equation, which has been used to calculate the mean thickness of the coherent scattering domain (CSD) of illite crystals from X-ray diffraction (XRD) full width data at half maximum (FWHM) intensity, employs a constant, Ksh, of 0.89. Use of this constant is unjustified, even if swelling has no effect on peak broadening, because this constant is valid only if all CSDs have a single thickness. For different thickness distributions, the Scherrer “constant” has very different values.Analysis of fundamental particle thickness data (transmission electron microscopy, TEM) for samples of authigenic illite and illite/smectite from diagenetically altered pyroclastics and filamentous illites from sandstones reveals a unique family of lognormal thickness distributions for these clays. Experimental relations between the distributions' lognormal parameters and mean thicknesses are established. These relations then are used to calculate the mean thickness of CSDs for illitic samples from XRD FWHM, or from integral XRD peak widths (integrated intensity/maximum intensity).For mixed-layer illite/smectite, the measured thickness of the CSD corresponds to the mean thickness of the mixed-layer crystal. Using this measurement, the mean thickness of the fundamental particles that compose the mixed-layer crystals can be calculated after XRD determination of percent smectitic interlayers. The effect of mixed layering (swelling) on XRD peak width for these samples is eliminated by using the 003 reflection for glycolated samples, and the 001, 002 or 003 reflection for dehydrated, K-saturated samples. If this technique is applied to the 001 reflection of air-dried samples (Kubler index measurement), mean CSD thicknesses are underestimated due to the mixed-layering effect.The technique was calibrated using NEW MOD©-simulated XRD profiles of illite, and then tested on well-characterized illite and illite/smectite samples. The XRD measurements are in good

FTIR spectroscopic, thermal and XRD characterization of hydroxyapatite from new natural sources

NASA Astrophysics Data System (ADS)

Shaltout, Abdallah A.; Allam, Moussa A.; Moharram, Mohamed A.

2011-12-01

The inorganic constituents of 5 different plants (leaves and stalks) were investigated by using Fourier transformer infrared spectroscopy (FTIR), X-ray diffraction (XRD) and thermal analysis including thermal gravimetric analysis (TGA), derivative thermogravimetry (DTG) and differential scanning calorimetry (DSC). These plants are Catha edulis (Khat), basil, mint, green tea and trifolium. The absorption bands of carbonate ions CO 32- was exhibited at 1446 cm -1, and the phosphate ions PO 43- was assigned at 1105 and 1035 cm -1. At high temperatures (600, 700 and 600 °C) further absorption bands of the phosphate ions PO 43- was assigned at the frequencies 572, 617, 962, 1043 and 1110 cm -1 and the vibrational absorption band of the carbonate ions CO 32- was assigned at 871, 1416 and 1461 cm -1. X-ray diffraction and thermal analysis confirm the obtained results of FITR. Results showed that the main inorganic constituents of C. edulis and basil leaves are hydroxyapatite whereas the hydroxyapatite content in the other plant samples is less than that in case of C. edulis and basil plant leaves.

Capacity Fading Mechanism of the Commercial 18650 LiFePO4-Based Lithium-Ion Batteries: An in Situ Time-Resolved High-Energy Synchrotron XRD Study.

PubMed

Liu, Qi; Liu, Yadong; Yang, Fan; He, Hao; Xiao, Xianghui; Ren, Yang; Lu, Wenquan; Stach, Eric; Xie, Jian

2018-02-07

In situ high-energy synchrotron XRD studies were carried out on commercial 18650 LiFePO 4 cells at different cycles to track and investigate the dynamic, chemical, and structural changes in the course of long-term cycling to elucidate the capacity fading mechanism. The results indicate that the crystalline structural deterioration of the LiFePO 4 cathode and the graphite anode is unlikely to happen before capacity fades below 80% of the initial capacity. Rather, the loss of the active lithium source is the primary cause for the capacity fade, which leads to the appearance of inactive FePO 4 that is proportional to the absence of the lithium source. Our in situ HESXRD studies further show that the lithium-ion insertion and deinsertion behavior of LiFePO 4 continuously changed with cycling. For a fresh cell, the LiFePO 4 experienced a dual-phase solid-solution behavior, whereas with increasing cycle numbers, the dynamic change, which is characteristic of the continuous decay of solid solution behavior, is obvious. The unpredicted dynamic change may result from the morphology evolution of LiFePO 4 particles and the loss of the lithium source, which may be the cause of the decreased rate capability of LiFePO 4 cells after long-term cycling.

Multielemental analyses of isomorphous Indian garnet gemstones by XRD and external pixe techniques.

PubMed

Venkateswarulu, P; Srinivasa Rao, K; Kasipathi, C; Ramakrishna, Y

2012-12-01

Garnet gemstones were collected from parts of Eastern Ghats geological formations of Andhra Pradesh, India and their gemological studies were carried out. Their study of chemistry is not possible as they represent mixtures of isomorphism nature, and none of the individual specimens indicate independent chemistry. Hence, non-destructive instrumental methodology of external PIXE technique was employed to understand their chemistry and identity. A 3 MeV proton beam was employed to excite the samples. In the present study geochemical characteristics of garnet gemstones were studied by proton induced X-ray emission. Almandine variety of garnet is found to be abundant in the present study by means of their chemical contents. The crystal structure and the lattice parameters were estimated using X-Ray Diffraction studies. The trace and minor elements are estimated using PIXE technique and major compositional elements are confirmed by XRD studies. The technique is found very useful in characterizing the garnet gemstones. The present work, thus establishes usefulness and versatility of the PIXE technique with external beam for research in Geo-scientific methodology. Copyright © 2012 Elsevier Ltd. All rights reserved.

Studies on the self-catalyzed Knoevenagel condensation, characterization, DPPH radical scavenging activity, cytotoxicity, and molecular properties of 5-arylidene-2,2-dimethyl-1,3-dioxane-4,6-diones using single crystal XRD and DFT techniques

NASA Astrophysics Data System (ADS)

Suresh Kumar, G. S.; Antony Muthu Prabhu, A.; Bhuvanesh, N.

2014-10-01

We have studied the self-catalyzed Knoevenagel condensation, spectral characterization, DPPH radical scavenging activity, cytotoxicity, and molecular properties of 5-arylidene-2,2-dimethyl-1,3-dioxane-4,6-diones using single crystal XRD and DFT techniques. In the absence of any catalyst, a series of novel 5-arylidene-2,2-dimethyl-1,3-dioxane-4,6-diones were synthesized using Meldrum’s acid and formylphenoxyaliphatic acid(s) in water. These molecules are arranged in the dimer form through intermolecular H-bonding in the single crystal XRD structure. Compounds have better DPPH radical scavenging activity and cytotoxicity against A431 cancer cell line. The optimized molecular structure, natural bond orbital analysis, electrostatic potential map, HOMO-LUMO energies, molecular properties, and atomic charges of these molecules have been studied by performing DFT/B3LYP/3-21G(*) level of theory in gas phase.

Effects of uniformities of deposition of respirable particles on filters on determining their quartz contents by using the direct on-filter X-ray diffraction (DOF XRD) method.

PubMed

Chen, Ching-Hwa; Tsaia, Perng-Jy; Lai, Chane-Yu; Peng, Ya-Lian; Soo, Jhy-Charm; Chen, Cheng-Yao; Shih, Tung-Sheng

2010-04-15

In this study, field samplings were conducted in three workplaces of a foundry plant, including the molding, demolding, and bead blasting, respectively. Three respirable aerosol samplers (including a 25-mm aluminum cyclone, nylon cyclone, and IOSH cyclone) were used side-by-side to collect samples from each selected workplace. For each collected sample, the uniformity of the deposition of respirable dusts on the filter was measured and its free silica content was determined by both the DOF XRD method and NIOSH 7500 XRD method (i.e., the reference method). A same trend in measured uniformities can be found in all selected workplaces: 25-mm aluminum cyclone>nylon cyclone>IOSH cyclone. Even for samples collected by the sampler with the highest uniformity (i.e., 25-mm aluminum cyclone), the use of the DOF XRD method would lead to the measured free silica concentrations 1.15-2.89 times in magnitude higher than that of the reference method. A new filter holder should be developed with the minimum uniformity comparable to that of NIOSH 7500 XRD method (=0.78) in the future. The use of conversion factors for correcting quartz concentrations obtained from the DOF XRD method based on the measured uniformities could be suitable for the foundry industry at this stage. 2009 Elsevier B.V. All rights reserved.

The inconsistency in adsorption properties and powder XRD data of MOF-5 is rationalized by framework interpenetration and the presence of organic and inorganic species in the nanocavities.

PubMed

Hafizovic, Jasmina; Bjørgen, Morten; Olsbye, Unni; Dietzel, Pascal D C; Bordiga, Silvia; Prestipino, Carmelo; Lamberti, Carlo; Lillerud, Karl Petter

2007-03-28

MOF-5 is the archetype metal-organic framework and has been subjected to numerous studies the past few years. The focal point of this report is the pitfalls related to the MOF-5 phase identification based on powder XRD data. A broad set of conditions and procedures have been reported for MOF-5 synthesis. These variations have led to materials with substantially different adsorption properties (specific surface areas in the range 700 to 3400 m(2)/g). The relatively low weight loss observed for some as synthesized samples upon solvent removal is also indicative of a low pore volume. Regrettably, these materials have all been described as MOF-5 without any further comments. Furthermore, the reported powder XRD patterns hint at structural differences: The variations in surface area are accompanied by peak splitting phenomena and rather pronounced changes in the relative peak intensities in the powder XRD patterns. In this work, we use single-crystal XRD to investigate structural differences between low and high surface area MOF-5. The low surface area MOF-5 sample had two different classes of crystals. For the dominant phase, Zn(OH)2 species partly occupied the cavities. The presence of Zn species makes the hosting cavity and possibly also adjacent cavities inaccessible and thus efficiently reduces the pore volume of the material. Furthermore, the minor phase consisted of doubly interpenetrated MOF-5 networks, which lowers the adsorption capacity. The presence of Zn species and lattice interpenetration changes the symmetry from cubic to trigonal and explains the peak splitting observed in the powder XRD patterns. Pore-filling effects from the Zn species (and partly the solvent molecules) are also responsible for the pronounced variations in powder XRD peak intensities. This latter conclusion is particularly useful for predicting the adsorption properties of a MOF-5-type material from powder XRD.

X-Ray Diffraction (XRD) Characterization Methods for Sigma=3 Twin Defects in Cubic Semiconductor (100) Wafers

NASA Technical Reports Server (NTRS)

Park, Yeonjoon (Inventor); Kim, Hyun Jung (Inventor); Skuza, Jonathan R. (Inventor); Lee, Kunik (Inventor); Choi, Sang Hyouk (Inventor); King, Glen C. (Inventor)

2017-01-01

An X-ray defraction (XRD) characterization method for sigma=3 twin defects in cubic semiconductor (100) wafers includes a concentration measurement method and a wafer mapping method for any cubic tetrahedral semiconductor wafers including GaAs (100) wafers and Si (100) wafers. The methods use the cubic semiconductor's (004) pole figure in order to detect sigma=3/{111} twin defects. The XRD methods are applicable to any (100) wafers of tetrahedral cubic semiconductors in the diamond structure (Si, Ge, C) and cubic zinc-blend structure (InP, InGaAs, CdTe, ZnSe, and so on) with various growth methods such as Liquid Encapsulated Czochralski (LEC) growth, Molecular Beam Epitaxy (MBE), Organometallic Vapor Phase Epitaxy (OMVPE), Czochralski growth and Metal Organic Chemical Vapor Deposition (MOCVD) growth.

Synthesis, molecular structure, FT-IR and XRD investigations of 2-(4-chlorophenyl)-2-oxoethyl 2-chlorobenzoate: a comparative DFT study.

PubMed

Chidan Kumar, C S; Fun, Hoong Kun; Tursun, Mahir; Ooi, Chin Wei; Chandraju, Siddegowda; Quah, Ching Kheng; Parlak, Cemal

2014-04-24

2-(4-Chlorophenyl)-2-oxoethyl 2-chlorobenzoate has been synthesized, its structural and vibrational properties have been reported using FT-IR and single-crystal X-ray diffraction (XRD) studies. The conformational analysis, optimized geometric parameters, normal mode frequencies and corresponding vibrational assignments of the synthesized compound (C15H10Cl2O3) have been examined by means of Becke-3-Lee-Yang-Parr (B3LYP) density functional theory (DFT) method together with 6-31++G(d,p) basis set. Furthermore, reliable conformational investigation and vibrational assignments have been made by the potential energy surface (PES) and potential energy distribution (PED) analyses, respectively. Calculations are performed with two possible conformations. The title compound crystallizes in orthorhombic space group Pbca with the unit cell dimensions a=12.312(5) Å, b=8.103(3) Å, c=27.565(11) Å, V=2750.0(19) Å(3). B3LYP method provides satisfactory evidence for the prediction of vibrational wavenumbers and structural parameters. Copyright © 2014 Elsevier B.V. All rights reserved.

Effect of annealing temperature on optical properties of binary zinc tin oxide nano-composite prepared by sol-gel route using simple precursors: structural and optical studies by DRS, FT-IR, XRD, FESEM investigations.

PubMed

Habibi, Mohammad Hossein; Mardani, Maryam

2015-02-25

Binary zinc tin oxide nano-composite was synthesized by a facile sol-gel method using simple precursors from the solutions consisting of zinc acetate, tin(IV) chloride and ethanol. Effect of annealing temperature on optical and structural properties was investigated using X-ray diffraction (XRD), diffuse reflectance spectra (DRS), field emission scanning electron microscopy (FESEM) and Fourier transform infrared spectroscopy (FTIR). XRD results revealed the existence of the ZnO and SnO2 phases. FESEM results showed that binary zinc tin oxide nano-composites ranges from 56 to 60 nm in diameter at 400°C and 500°C annealing temperatures respectively. The optical band gap was increased from 2.72 eV to 3.11 eV with the increasing of the annealing temperature. FTIR results confirmed the presence of zinc oxide and tin oxide and the broad absorption peaks at 3426 and 1602 cm(-1) can be ascribed to the vibration of absorptive water, and the absorption peaks at 546, 1038 and 1410 cm(-1) are due to the vibration of Zn-O or Sn-O groups in binary zinc tin oxide. Copyright © 2014 Elsevier B.V. All rights reserved.

High temperature XRD of Cu2GeSe3

NASA Astrophysics Data System (ADS)

Premkumar D., S.; Chetty, Raju; Malar, P.; Mallik, Ramesh Chandra

2015-06-01

The Cu2GeSe3 is prepared by solid state synthesis method. The high temperature XRD has been done at different temperature from 30 °C to 450 °C. The reitveld refinement confirms Cu2GeSe3 phase and orthorhombic crystal structure. The lattice constants are increasing with increase in the temperature and their rate of increase with respect to temperature are used for finding the thermal expansion coefficient. The calculation of the linear and volume coefficient of thermal expansion is done from 30 °C to 400 °C. Decrease in the values of linear expansion coefficients with temperature are observed along a and c axis. Since thermal expansion coefficient is the consequence of the distortion of atoms in the lattice; this can be further used to find the minimum lattice thermal conductivity at given temperature.

Synchrotron Radiation XRD Analysis of Indialite in Y-82094 Ungrouped Carbonaceous Chondrite

NASA Technical Reports Server (NTRS)

Mikouchi, T.; Hagiya, K.; Sawa, N.; Kimura, M.; Ohsumi, K.; Komatsu, M.; Zolensky, M.

2016-01-01

Y-82094 is an ungrouped type 3.2 carbonaceous chondrite, with abundant chondrules making 78 vol.% of the rock. Among these chondrules, an unusual porphyritic Al-rich magnesian chondrule is reported that consists of a cordierite-like phase, Al-rich orthopyroxene, cristobalite, and spinel surrounded by an anorthitic mesostasis. The reported chemical formula of the cordierite-like phase is Na(0.19)Mg(1.95)Fe(0.02)Al(3.66)Si(5.19)O18, which is close to stoichiometric cordierite (Mg2Al3[AlSi5O18]). Although cordierite can be present in Al-rich chondrules, it has a high temperature polymorph (indialite) and it is therefore necessary to determine whether it is cordierite or indialite in order to better constrain its formation conditions. In this abstract we report on our synchrotron radiation X-ray diffraction (SR-XRD) study of the cordierite-like phase in Y-82094.

Understanding changes in cellulose crystalline structure of lignocellulosic biomass during ionic liquid pretreatment by XRD.

PubMed

Zhang, Jiafu; Wang, Yixun; Zhang, Liye; Zhang, Ruihong; Liu, Guangqing; Cheng, Gang

2014-01-01

X-ray diffraction (XRD) was used to understand the interactions of cellulose in lignocellulosic biomass with ionic liquids (ILs). The experiment was designed in such a way that the process of swelling and solubilization of crystalline cellulose in plant cell walls was followed by XRD. Three different feedstocks, switchgrass, corn stover and rice husk, were pretreated using 1-butyl-3-methylimidazolium acetate ([C4mim][OAc]) at temperatures of 50-130°C for 6h. At a 5 wt.% biomass loading, increasing pretreatment temperature led to a drop in biomass crystallinity index (CrI), which was due to swelling of crystalline cellulose. After most of the crystalline cellulose was swollen with IL molecules, a low-order structure was found in the pretreated samples. Upon further increasing temperature, cellulose II structure started to form in the pretreated biomass samples as a result of solubilization of cellulose in [C4mim][OAc] and subsequent regeneration. Copyright © 2013 Elsevier Ltd. All rights reserved.

Copper(II) complex with 6-methylpyridine-2-carboxyclic acid: Experimental and computational study on the XRD, FT-IR and UV-Vis spectra, refractive index, band gap and NLO parameters

NASA Astrophysics Data System (ADS)

Altürk, Sümeyye; Avcı, Davut; Başoğlu, Adil; Tamer, Ömer; Atalay, Yusuf; Dege, Necmi

2018-02-01

Crystal structure of the synthesized copper(II) complex with 6-methylpyridine-2-carboxylic acid, [Cu(6-Mepic)2·H2O]·H2O, was determined by XRD, FT-IR and UV-Vis spectroscopic techniques. Furthermore, the geometry optimization, harmonic vibration frequencies for the Cu(II) complex were carried out by using Density Functional Theory calculations with HSEh1PBE/6-311G(d,p)/LanL2DZ level. Electronic absorption wavelengths were obtained by using TD-DFT/HSEh1PBE/6-311G(d,p)/LanL2DZ level with CPCM model and major contributions were determined via Swizard/Chemissian program. Additionally, the refractive index, linear optical (LO) and non-nonlinear optical (NLO) parameters of the Cu(II) complex were calculated at HSEh1PBE/6-311G(d,p) level. The experimental and computed small energy gap shows the charge transfer in the Cu(II) complex. Finally, the hyperconjugative interactions and intramolecular charge transfer (ICT) were studied by performing of natural bond orbital (NBO) analysis.

Copper(II) complex with 6-methylpyridine-2-carboxyclic acid: Experimental and computational study on the XRD, FT-IR and UV-Vis spectra, refractive index, band gap and NLO parameters.

PubMed

Altürk, Sümeyye; Avcı, Davut; Başoğlu, Adil; Tamer, Ömer; Atalay, Yusuf; Dege, Necmi

2018-02-05

Crystal structure of the synthesized copper(II) complex with 6-methylpyridine-2-carboxylic acid, [Cu(6-Mepic) 2 ·H 2 O]·H 2 O, was determined by XRD, FT-IR and UV-Vis spectroscopic techniques. Furthermore, the geometry optimization, harmonic vibration frequencies for the Cu(II) complex were carried out by using Density Functional Theory calculations with HSEh1PBE/6-311G(d,p)/LanL2DZ level. Electronic absorption wavelengths were obtained by using TD-DFT/HSEh1PBE/6-311G(d,p)/LanL2DZ level with CPCM model and major contributions were determined via Swizard/Chemissian program. Additionally, the refractive index, linear optical (LO) and non-nonlinear optical (NLO) parameters of the Cu(II) complex were calculated at HSEh1PBE/6-311G(d,p) level. The experimental and computed small energy gap shows the charge transfer in the Cu(II) complex. Finally, the hyperconjugative interactions and intramolecular charge transfer (ICT) were studied by performing of natural bond orbital (NBO) analysis. Copyright © 2017 Elsevier B.V. All rights reserved.

[X-ray diffraction (XRD) and near infrared spectrum (NIR) analysis of the soil overlying the Bairendaba deposit of the Inner Mongolia Grassland].

PubMed

Luo, Song-ying; Cao, Jian-jin; Wu, Zheng-quan

2014-08-01

The soil samples uniformly overlying the Bairendaba deposit of the Inner Mongolia grassland were collected, and ana- lyzed with X-ray diffraction (XRD) and near infrared spectrum (NIR), for exploring the origins of the soil from the, grassland mining area and the relationship with the underground rock. The results show that the samp]s consist of quartz, graphite, carbonate, hornblende, mica, chlorite, montmorillonite, illite, berlinite, diaspore, azurite, hen tite, etc. These indicate that the soil samples were not only from the weathering products of the surface rock, but also from the underground rock mass and the alteration of the wall rock. The azurite and the hematite contained in the soil, mainly coming from the oxidation zone of the orebodies, can be used as the prospecting marks. The alteration mineral assemblage is mainly chlorite-illite-montmorillonite and it experienced the alteration process of potassic alteration-->silicification-->carbonatization-->silk greisenization-->clayization. Also, the wall rock alteration and the physical weathering processes can be accurately restored by analyzing the combination of the alteration minerals, which can provide important reference information for the deep ore prospecting and the ore deposit genesis study, improving the rate of the prospecting. The XRD and NIR with the characteristics of the economy and quickness can be used for the identification of mineral composition of soil, and in the study of mineral and mineral deposits. Especially, NIR has its unique superiority, that is, its sample request is low, and it can analyze a batch of samples quickly. With the development of INR, it will be more and more widely applied in geological field, and can play an important role in the ore exploration.

Bone matrix calcification during embryonic and postembryonic rat calvarial development assessed by SEM-EDX spectroscopy, XRD, and FTIR spectroscopy.

PubMed

Henmi, Akiko; Okata, Hiroshi; Anada, Takahisa; Yoshinari, Mariko; Mikami, Yasuto; Suzuki, Osamu; Sasano, Yasuyuki

2016-01-01

Bone mineral is constituted of biological hydroxyapatite crystals. In developing bone, the mineral crystal matures and the Ca/P ratio increases. However, how an increase in the Ca/P ratio is involved in maturation of the crystal is not known. The relationships among organic components and mineral changes are also unclear. The study was designed to investigate the process of calcification during rat calvarial bone development. Calcification was evaluated by analyzing the atomic distribution and concentration of Ca, P, and C with scanning electron microscopy (SEM)-energy-dispersive X-ray (EDX) spectroscopy and changes in the crystal structure with X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. Histological analysis showed that rat calvarial bone formation started around embryonic day 16. The areas of Ca and P expanded, matching the region of the developing bone matrix, whereas the area of C became localized around bone. X-ray diffraction and FTIR analysis showed that the amorphous-like structure of the minerals at embryonic day 16 gradually transformed into poorly crystalline hydroxyapatite, whereas the proportion of mineral to protein increased until postnatal week 6. FTIR analysis also showed that crystallization of hydroxyapatite started around embryonic day 20, by which time SEM-EDX spectroscopy showed that the Ca/P ratio had increased and the C/Ca and C/P ratios had decreased significantly. The study suggests that the Ca/P molar ratio increases and the proportion of organic components such as proteins of the bone matrix decreases during the early stage of calcification, whereas crystal maturation continues throughout embryonic and postembryonic bone development.

XRD measurement of mean thickness, thickness distribution and strain for illite and illite-smectite crystallites by the Bertaut-Warren-Averbach technique

USGS Publications Warehouse

Drits, Victor A.; Eberl, Dennis D.; Środoń, Jan

1998-01-01

A modified version of the Bertaut-Warren-Averbach (BWA) technique (Bertaut 1949, 1950; Warren and Averbach 1950) has been developed to measure coherent scattering domain (CSD) sizes and strains in minerals by analysis of X-ray diffraction (XRD) data. This method is used to measure CSD thickness distributions for calculated and experimental XRD patterns of illites and illite-smectites (I-S). The method almost exactly recovers CSD thickness distributions for calculated illite XRD patterns. Natural I-S samples contain swelling layers that lead to nonperiodic structures in the c* direction and to XRD peaks that are broadened and made asymmetric by mixed layering. Therefore, these peaks cannot be analyzed by the BWA method. These difficulties are overcome by K-saturation and heating prior to X-ray analysis in order to form 10-Å periodic structures. BWA analysis yields the thickness distribution of mixed-layer crystals (coherently diffracting stacks of fundamental illite particles). For most I-S samples, CSD thickness distributions can be approximated by lognormal functions. Mixed-layer crystal mean thickness and expandability then can be used to calculate fundamental illite particle mean thickness. Analyses of the dehydrated, K-saturated samples indicate that basal XRD reflections are broadened by symmetrical strain that may be related to local variations in smectite interlayers caused by dehydration, and that the standard deviation of the strain increases regularly with expandability. The 001 and 002 reflections are affected only slightly by this strain and therefore are suited for CSD thickness analysis. Mean mixed-layer crystal thicknesses for dehydrated I-S measured by the BWA method are very close to those measured by an integral peak width method.

In situ synchrotron XRD analysis of the kinetics of spodumene phase transitions.

PubMed

L Moore, Radhika; Mann, Jason P; Montoya, Alejandro; Haynes, Brian S

2018-04-25

The phase transition by thermal activation of natural α-spodumene was followed by in situ synchrotron XRD in the temperature range 896 to 940 °C. We observed both β- and γ-spodumene as primary products in approximately equal proportions. The rate of the α-spodumene inversion is first order and highly sensitive to temperature (apparent activation energy ∼800 kJ mol-1). The γ-spodumene product is itself metastable, forming β-spodumene, with the total product mass fraction ratio fγ/fβ decreasing as the conversion of α-spodumene continues. We found the relationship between the product yields and the degree of conversion of α-spodumene to be the same at all temperatures in the range studied. A model incorporating first order kinetics of the α- and γ-phase inversions with invariant rate constant ratio describes the results accurately. Theoretical phonon analysis of the three phases indicates that the γ phase contains crystallographic instabilities, whilst the α and β phases do not.

Use of tourmaline as a potential petrogenetic indicator in the determination of host magma: CRS, XRD and PED-XRF methods

NASA Astrophysics Data System (ADS)

Gullu, Bahattin; Kadioglu, Yusuf Kagan

2017-08-01

Tourmaline defines a group of complex borosilicate forms as accessory mineral in igneous and metamorphic rocks and they act an important role in the interpretation of the chemical composition changes of the composition of the host fluid of the magma. The variety of tourmaline can be identified by using optical microscopy, X-Ray Diffraction (XRD) and by determining its chemical composition through Polarized Energy Dispersive X-Ray Fluorescence (PED-XRF) methods. However, microscopic investigations and XRD analyses are not quite adequate for detailed determination of tourmaline sub-groups. In addition, the use of chemical composition of tourmaline as a strict indicator of geochemical processes might be a misleading method. In this study, variable tourmaline crystals were collected from three different pegmatitic occurrences in Behrekdag, Yozgat and Karakaya granitic bodies of Central Anatolia to identify their chemical properties through Confocal Raman Spectroscopy (CRS), PED-XRF and XRD analyses. The confocal Raman spectrometry of collected tourmalines from the Behrekdag, Yozgat and Karakaya granites are in the compositions of schorl, schorl and elbaite respectively. The dominant compositional groups of these tourmalines are in the form of schorl. Raman shift values of tourmalines revealed four bands centered at almost 1050, 750, 400 and 300 cm- 1. The first group of the band arises from SiO stretching, the second from Bsbnd O stretching and the other two belong to bending modes of Osbnd Bsbnd O and Bsbnd Osbnd Al with symmetrical deformation of Sisbnd Osbnd Si. The strongest spectra near 360 cm- 1 should belong to the bonding of Alsbnd O. As a result, the confocal Raman studies are more sensitive for identification of tourmaline subgroup compositions and have a quite important in the explaining source of the magma.

Use of tourmaline as a potential petrogenetic indicator in the determination of host magma: CRS, XRD and PED-XRF methods.

PubMed

Gullu, Bahattin; Kadioglu, Yusuf Kagan

2017-08-05

Tourmaline defines a group of complex borosilicate forms as accessory mineral in igneous and metamorphic rocks and they act an important role in the interpretation of the chemical composition changes of the composition of the host fluid of the magma. The variety of tourmaline can be identified by using optical microscopy, X-Ray Diffraction (XRD) and by determining its chemical composition through Polarized Energy Dispersive X-Ray Fluorescence (PED-XRF) methods. However, microscopic investigations and XRD analyses are not quite adequate for detailed determination of tourmaline sub-groups. In addition, the use of chemical composition of tourmaline as a strict indicator of geochemical processes might be a misleading method. In this study, variable tourmaline crystals were collected from three different pegmatitic occurrences in Behrekdag, Yozgat and Karakaya granitic bodies of Central Anatolia to identify their chemical properties through Confocal Raman Spectroscopy (CRS), PED-XRF and XRD analyses. The confocal Raman spectrometry of collected tourmalines from the Behrekdag, Yozgat and Karakaya granites are in the compositions of schorl, schorl and elbaite respectively. The dominant compositional groups of these tourmalines are in the form of schorl. Raman shift values of tourmalines revealed four bands centered at almost 1050, 750, 400 and 300cm -1 . The first group of the band arises from SiO stretching, the second from BO stretching and the other two belong to bending modes of OBO and BOAl with symmetrical deformation of SiOSi. The strongest spectra near 360cm -1 should belong to the bonding of AlO. As a result, the confocal Raman studies are more sensitive for identification of tourmaline subgroup compositions and have a quite important in the explaining source of the magma. Copyright © 2017 Elsevier B.V. All rights reserved.

Mineralogical In-situ Investigation of Acid-Sulfate Samples from the Rio Tinto River, Spain, with a Portable XRD/XRF Instrument

NASA Technical Reports Server (NTRS)

Sarrazin, P.; Ming, D. W.; Morris, R. V.; Fernandez-Remolar, D.; Amils, R.; Arvidson, R. E.; Blake, D.; Bish, D. L.

2007-01-01

A field campaign was organized in September 2006 by Centro de Astobiologica (Spain) and Washington University (St Louis, USA) for the geological study of the Rio Tinto river bed sediments using a suite of in-situ instruments comprising an ASD reflectance spectrometer, an emission spectrometer, panoramic and close-up color imaging cameras, a life detection system and NASA's CheMin 4 XRD/XRF prototype. The primary objectives of the field campaign were to study the geology of the site and test the potential of the instrument suite in an astrobiological investigation context for future Mars surface robotic missions. The results of the overall campaign will be presented elsewhere. This paper focuses on the results of the XRD/XRF instrument deployment. The specific objectives of the CheMin 4 prototype in Rio Tinto were to 1) characterize the mineralogy of efflorescent salts in their native environments; 2) analyze the mineralogy of salts and oxides from the modern environment to terraces formed earlier as part of the Rio Tinto evaporative system; and 3) map the transition from hematite-dominated terraces to the mixed goethite/salt-bearing terraces where biosignatures are best preserved.

Cobalt ferrite nano-composite coated on glass by Doctor Blade method for photo-catalytic degradation of an azo textile dye Reactive Red 4: XRD, FESEM and DRS investigations.

PubMed

Habibi, Mohammad Hossein; Parhizkar, Janan

2015-11-05

Cobalt ferrite nano-composite was prepared by hydrothermal route using cobalt nitrate, iron nitrate and ethylene glycol as chelating agent. The nano-composite was coated on glass by Doctor Blade method and annealed at 300 °C. The structural, optical, and photocatalytic properties have been studied by powder X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and UV-visible spectroscopy (UV-Vis DRS). Powder XRD analysis confirmed formation of CoFe2O4 spinel phase. The estimated particle size from FESEM data was 50 nm. The calculated energy band gaps, obtained by Tauc relation from UV-Vis absorption spectra was 1.3 eV. Photocatalytic degradation of Reactive Red 4 as an azo textile was investigated in aqueous solution under irradiation showed 68.0% degradation of the dye within 100 min. The experimental enhanced activity compare to pure Fe2O3 can be ascribed to the formation of composite, which was mainly attributable to the transfer of electron and hole to the surface of composite and hinder the electron hole recombination. Copyright © 2015 Elsevier B.V. All rights reserved.

Synchrotron-based XRD from rat bone of different age groups.

PubMed

Rao, D V; Gigante, G E; Cesareo, R; Brunetti, A; Schiavon, N; Akatsuka, T; Yuasa, T; Takeda, T

2017-05-01

Synchrotron-based XRD spectra from rat bone of different age groups (w, 56 w and 78w), lumber vertebra at early stages of bone formation, Calcium hydroxyapatite (HAp) [Ca 10 (PO 4 ) 6 (OH) 2 ] bone fill with varying composition (60% and 70%) and bone cream (35-48%), has been acquired with 15keV synchrotron X-rays. Experiments were performed at Desy, Hamburg, Germany, utilizing the Resonant and Diffraction beamline (P9), with 15keV X-rays (λ=0.82666 A 0 ). Diffraction data were quantitatively analyzed using the Rietveld refinement approach, which allowed us to characterize the structure of these samples in their early stages. Hydroxyapatite, received considerable attention in medical and materials sciences, since these materials are the hard tissues, such as bone and teeth. Higher bioactivity of these samples gained reasonable interest for biological application and for bone tissue repair in oral surgery and orthopedics. The results obtained from these samples, such as phase data, crystalline size of the phases, as well as the degree of crystallinity, confirm the apatite family crystallizing in a hexagonal system, space group P6 3 /m with the lattice parameters of a=9.4328Å and c=6.8842Å (JCPDS card #09-0432). Synchrotron-based XRD patterns are relatively sharp and well resolved and can be attributed to the hexagonal crystal form of hydroxyapatite. All the samples were examined with scanning electron microscope at an accelerating voltage of 15kV. The presence of large globules of different sizes is observed, in small age groups of the rat bone (8w) and lumber vertebra (LV), as distinguished from, large age groups (56 and 78w) in all samples with different magnification, reflects an amorphous phase without significant traces of crystalline phases. Scanning electron microscopy (SEM) was used to characterize the morphology and crystalline properties of Hap, for all the samples, from 2 to 100μm resolution. Copyright © 2017 Elsevier B.V. All rights reserved.

Synthesis, spectroscopic (UV-Vis, FT-IR and NMR), single crystal XRD of 3,5-diethyl -2,6-di(thiophen-2-yl)piperidin-4-on-1-ium picrate: A comprehensive experimental and computational study

NASA Astrophysics Data System (ADS)

Arockia doss, M.; Rajarajan, G.; Thanikachalam, V.; Selvanayagam, S.; Sridhar, B.

2017-01-01

A piperidin-4-one containing picrate 3,5-diethyl -2,6-di(thiophen-2-yl)piperidin-4-on-1-ium picrate [3,5-DPPP] was synthesized. The molecular structure of 3,5-DPPP was confirmed by FT-IR, NMR, Uv-Vis, single crystal XRD analysis and DFT and HF methods with 6-31G(d,p) basis set. The XRD data confirm the transfer of protons from picric acid (O2) to piperidin-4-one ring (N1). The 3,5-DPPP compound is stabilized by the presence of intermolecular and intramolecular hydrogen bonds (N-H⋯O, C-H⋯S and C-H⋯O). Density functional theory and HF calculations have been used widely for calculating a wide variety of molecular properties such as optimized structure, FT-IR and Uv-Vis spectra, and provided reliable results which are in agreement with experimental data. The charge density data have been used to understand the properties of molecular systems. Furthermore, several quantum chemical insights have been obtained in the form of the total and partial density of states, the HOMO-LUMO energy gap and electrostatic potential map etc. In addition, the polarizability and first hyperpolarizability were calculated to show the potential applications of 3,5-DPPP in nonlinear optics.

Chemical and morphological characterization of TSP and PM2.5 by SEM-EDS, XPS and XRD collected in the metropolitan area of Monterrey, Mexico

NASA Astrophysics Data System (ADS)

González, Lucy T.; Rodríguez, F. E. Longoria; Sánchez-Domínguez, M.; Leyva-Porras, C.; Silva-Vidaurri, L. G.; Acuna-Askar, Karim; Kharisov, B. I.; Villarreal Chiu, J. F.; Alfaro Barbosa, J. M.

2016-10-01

Total suspended particles (TSP) and particles smaller than 2.5 μm (PM2.5) were collected at four sites in the metropolitan area of Monterrey (MAM) in Mexico. The samples were characterized by X-ray Diffraction (XRD), X-ray Photoelectron Spectroscopy (XPS), and Scanning Electron Microscopy (SEM). In order to determine the possible sources of emissions of atmospheric particulate matter, a principal component analysis (PCA) was performed. The XRD results showed that the major crystalline compounds found in the TPS were CaCO3 and SiO2; while in the PM2.5 CaSO4 was found. The XPS analysis showed that the main elements found on the surface of the particles were C, O, Si, Ca, S, and N. The deconvolution carried out on the high-resolution spectra for C1s, S2p and N1s, showed that the aromatics, sulfates and pyrrolic-amides were the main groups contributing to the signal of these elements, respectively. The C-rich particles presented a spherical morphology, while the Ca- and Si-based particles mostly showed a prismatic shape. The PCA analysis together with the results obtained from the characterization techniques, suggested that the main contributors to the CaCO3 particles collected in the PM were most probably produced and emitted into the atmosphere by local construction industries and exploitation of rich-deposits of calcite. Meanwhile, the SiO2 found in the MAM originated from the suspension of geological material abundant in the region, and the carbon particles were mainly produced by the combustion of fossil fuels.

XRD and spectral dataset of the UV-A stable nanotubes of 3,5-bis(trifluoromethyl)benzylamine derivative of tyrosine.

PubMed

Govindhan, R; Karthikeyan, B

2017-10-01

The data presented in this article are related to the research entitled of UV-A stable nanotubes. The nanotubes have been prepared from 3,5-bis(trifluoromethyl)benzylamine derivative of tyrosine (BTTP). XRD data reveals the size of the nanotubes. As-synthesized nanotubes (BTTPNTs) are characterized by UV-vis optical absorption studies [1] and photo physical degradation kinetics. The resulted dataset is made available to enable critical or extended analyzes of the BTTPNTs as an excellent light resistive materials.

Following the movement of Cu ions in a SSZ-13 zeolite during dehydration, reduction and adsorption: a combined in situ TP-XRD, XANES/DRIFTS study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kwak, Ja Hun; Varga, Tamas; Peden, Charles HF

2014-05-05

Cu-SSZ-13 has been shown to possess high activity and superior N2 formation selectivity in the selective catalytic reduction of NOx under oxygen rich conditions. Here, a combination of synchrotron-based (XRD and XANES) and vibrational (DRIFTS) spectroscopy tools have been used to follow the changes in the location and coordination environment of copper ions in a Cu-SSZ-13 zeolite during calcinations, reduction with CO, and adsorption of CO and H2O. XANES spectra collected during these procedures provides critical information not only on the variation in the oxidation state of the copper species in the zeolite structure, but also on the changes inmore » the coordination environment around these ions as they interact with the framework, and with different adsorbates (H2O and CO). Time-resolved XRD data indicate the movement of copper ions and the consequent variation of the unit cell parameters during dehydration. DRIFT spectra provide information about the adsorbed species present in the zeolite, as well as the oxidation states of and coordination environment around the copper ions. A careful analysis of the asymmetric T-O-T vibrations of the CHA framework perturbed by copper ions in different coordination environments proved to be especially informative. The results of this study will aid the identification of the location, coordination and oxidation states of copper ions obtained during in operando catalytic studies. Financial support was provided by the US Department of Energy (DOE), Office of Energy Efficiency and Renewable Energy, Vehicle Technologies Program. Part of this work (sample preparation) was performed in the Environmental Molecular Sciences Laboratory (EMSL) at Pacific Northwest National Laboratory (PNNL). The EMSL is a national scientific user facility supported by the US DOE, Office of Biological and Environmental Research. PNNL is a multi-program national laboratory operated for the US DOE by Battelle. All of the spectroscopy work reported here

Structural changes and thermal stability of charged LiNixMnyCozO₂ cathode materials studied by combined in situ time-resolved XRD and mass spectroscopy.

PubMed

Bak, Seong-Min; Hu, Enyuan; Zhou, Yongning; Yu, Xiqian; Senanayake, Sanjaya D; Cho, Sung-Jin; Kim, Kwang-Bum; Chung, Kyung Yoon; Yang, Xiao-Qing; Nam, Kyung-Wan

2014-12-24

Thermal stability of charged LiNixMnyCozO2 (NMC, with x + y + z = 1, x:y:z = 4:3:3 (NMC433), 5:3:2 (NMC532), 6:2:2 (NMC622), and 8:1:1 (NMC811)) cathode materials is systematically studied using combined in situ time-resolved X-ray diffraction and mass spectroscopy (TR-XRD/MS) techniques upon heating up to 600 °C. The TR-XRD/MS results indicate that the content of Ni, Co, and Mn significantly affects both the structural changes and the oxygen release features during heating: the more Ni and less Co and Mn, the lower the onset temperature of the phase transition (i.e., thermal decomposition) and the larger amount of oxygen release. Interestingly, the NMC532 seems to be the optimized composition to maintain a reasonably good thermal stability, comparable to the low-nickel-content materials (e.g., NMC333 and NMC433), while having a high capacity close to the high-nickel-content materials (e.g., NMC811 and NMC622). The origin of the thermal decomposition of NMC cathode materials was elucidated by the changes in the oxidation states of each transition metal (TM) cations (i.e., Ni, Co, and Mn) and their site preferences during thermal decomposition. It is revealed that Mn ions mainly occupy the 3a octahedral sites of a layered structure (R3̅m) but Co ions prefer to migrate to the 8a tetrahedral sites of a spinel structure (Fd3̅m) during the thermal decomposition. Such element-dependent cation migration plays a very important role in the thermal stability of NMC cathode materials. The reasonably good thermal stability and high capacity characteristics of the NMC532 composition is originated from the well-balanced ratio of nickel content to manganese and cobalt contents. This systematic study provides insight into the rational design of NMC-based cathode materials with a desired balance between thermal stability and high energy density.

An exploratory method to detect tephras from quantitative XRD scans: Examples from Iceland and east Greenland marine sediments

USGS Publications Warehouse

Andrews, John T.; Eberl, D.D.; Kristjansdottir, G.B.

2006-01-01

Tephras, mainly from Iceland, are becoming increasingly important in interpreting leads and lags in the Holocene climate system across NW Europe. Here we demonstrate that Quantitative Phase Analysis of x-ray diffractograms of the 150 um fraction and identify these same peaks in XRD scans - two of these correlate geochemically and chronologically with Hekla 1104 and 3. At a distal site to the WNW of Iceland, on the East Greenland margin (core MD99-2317), the weight% of volcanic glass reaches values of 11% at about the time of the Saksunarvatn tephra. The XRD method identifies the presence of volcanic glass but not its elemental composition; hence it will assist in focusing attention on specific sections of sediment cores for subsequent geochemical fingerprinting of tephras. ?? 2006 SAGE Publications.

Mossbauer and XRD characterization of the phase transformations in a Fe-Mn-Al-C-Mo-Si-Cu as cast alloy during tribology test

NASA Astrophysics Data System (ADS)

Ramos, J.; Piamba, J. F.; Sánchez, H.; Alcazar, G. A. Pérez

2015-06-01

In present study Fe-29.0Mn-6Al-0.9C-1.8Mo-1.6Si-0.4Cu (%w) alloy was obtained after melted in an induction furnace, and then molded as an ingot. From the as cast ingot it were cut samples for the different characterization measurements. The microstructure of the as-cast sample is of dendritic type and its XRD pattern was refined with the lines of the austenite, with a big volumetric fraction, and the lines of the martensite, with small volumetric fraction. The Mössbauer spectrum of the sample was fitted with a broad singlet which corresponds to disordered austenite. After the tribology test, its XRD pattern was refined with the lines of two austenite phases, one similar to the previous one and other with bigger lattice parameter. The total volumetric fraction of the austenite is smaller than that obtained for sample without wear. It was added the lines of the martensite phase with bigger volumetric fraction than that of the previous sample. The Mössbauer spectrum of the weared sample was fitted with two paramagnetic sites which correspond to the two Fe austenite phases and a hyperfine magnetic field distribution which is associated to the disordered original martensite and the new one which appears in the surface as a consequence of the wear process. These results show that during wear process the original austenite phase is transformed in martensite and in a new austenite phase. The increases of the martensitic phase improves mechanical properties and wear behavior.

Army Study Shows Decline In Behavioral Health Stigma

DTIC Science & Technology

2012-01-01

Army Study Shows Decline in Behavioral Health Stigma By Rob McIlvaine Army News Service WASHINGTON, Jan. 20, 2012 - A newly released Army study on...conference yesterday. The three-year study outlines the problem of suicide in the Army and related issues of substance abuse, spouse abuse and child abuse...REPORT TYPE 3. DATES COVERED 00-00-2012 to 00-00-2012 4. TITLE AND SUBTITLE Army Study Shows Decline In Behavioral Health Stigma 5a. CONTRACT

Investigation of synthetic spider silk crystallinity and alignment via electrothermal, pyroelectric, literature XRD, and tensile techniques.

PubMed

Munro, Troy; Putzeys, Tristan; Copeland, Cameron G; Xing, Changhu; Lewis, Randolph V; Ban, Heng; Glorieux, Christ; Wubbenhorst, Michael

2017-04-01

The processes used to create synthetic spider silk greatly affect the properties of the produced fibers. This paper investigates the effect of process variations during artificial spinning on the thermal and mechanical properties of the produced silk. Property values are also compared to the ones of the natural dragline silk of the N. clavipes spider, and to unprocessed (as-spun) synthetic silk. Structural characterization by scanning pyroelectric microscopy is employed to provide insight into the axial orientation of the crystalline regions of the fiber and is supported by XRD data. The results show that stretching and passage through liquid baths induce crystal formation and axial alignment in synthetic fibers, but with different structural organization than natural silks. Furthermore, an increase in thermal diffusivity and elastic modulus is observed with decreasing fiber diameter, trending towards properties of natural fiber. This effect seems to be related to silk fibers being subjected to a radial gradient during production.

Investigation of synthetic spider silk crystallinity and alignment via electrothermal, pyroelectric, literature XRD, and tensile techniques

PubMed Central

Munro, Troy; Putzeys, Tristan; Copeland, Cameron G.; Xing, Changhu; Lewis, Randolph V; Ban, Heng; Glorieux, Christ; Wubbenhorst, Michael

2018-01-01

The processes used to create synthetic spider silk greatly affect the properties of the produced fibers. This paper investigates the effect of process variations during artificial spinning on the thermal and mechanical properties of the produced silk. Property values are also compared to the ones of the natural dragline silk of the N. clavipes spider, and to unprocessed (as-spun) synthetic silk. Structural characterization by scanning pyroelectric microscopy is employed to provide insight into the axial orientation of the crystalline regions of the fiber and is supported by XRD data. The results show that stretching and passage through liquid baths induce crystal formation and axial alignment in synthetic fibers, but with different structural organization than natural silks. Furthermore, an increase in thermal diffusivity and elastic modulus is observed with decreasing fiber diameter, trending towards properties of natural fiber. This effect seems to be related to silk fibers being subjected to a radial gradient during production. PMID:29430211

Volcanic glass in Cretaceous dacites and rhyolites of the Paraná Magmatic Province, southern Brazil: Characterization and quantification by XRD-Rietveld

NASA Astrophysics Data System (ADS)

Andrade, Fábio Ramos Dias de; Polo, Liza Angélica; Janasi, Valdecir de Assis; Carvalho, Flávio Machado de Souza

2018-04-01

Acidic rocks are a significant component of the Cretaceous Paraná Magmatic Province, occurring in different stratigraphic positions, and often forming deposits of complex and as yet poorly defined architecture. Vitrophyric varieties are surprisingly abundant for a volcanic sequence of this age, and are composed of predominant glass plus plagioclase (labradorite-andesine), pyroxenes (augite ± pigeonite and orthopyroxene), Ti-rich magnetite, and traces of apatite. Hypocrystalline rocks, largely derived from devitrification, additionally contain sanidine, cristobalite, and quartz. The negative correlation between the abundance of these minerals and the amount of glass suggests that these latter phases formed by devitrification. Modal analysis using a combined XRD Rietveld-RIR method detected glass contents between 0 and 85 wt% % in a set of representative samples of Palmas-type acidic rocks from southern Brazil with dacite to rhyolite composition. Modal compositions determined by XRD and by scanning electron microscope are in good agreement with each other, and were checked against whole-rock XRF chemical data. Water contents up to 4 wt% show a positive linear correlation with the amount of glass, and are inferred to be mostly secondary, as original (pre-eruptive) H2O dissolved in melts is inferred to have been < 1.5 wt% in all rocks. Glass is the only water bearing phase in the studied samples, which lack low temperature hydrated phases. Water loss during devitrification appears to have occurred along fractures, and was accompanied by Na loss and, in some samples, also Ca, Rb and Sr loss. The rapid and inexpensive method of modal analyses of glassy rocks developed here may be a useful tool for mapping acidic volcanic rocks in southern Paraná Magmatic Province, and also to identify the architecture of these deposits.

Combined use of FE-SEM+EDS, ToF-SIMS, XPS, XRD and OM for the study of ancient gilded artefacts

NASA Astrophysics Data System (ADS)

Ingo, G. M.; Riccucci, C.; Pascucci, M.; Messina, E.; Giuliani, C.; Biocca, P.; Tortora, L.; Fierro, G.; Di Carlo, G.

2018-07-01

Gilded brooches dating back to 16th-17th centuries CE were investigated by means of integrated and complementary analytical techniques such as high spatial resolution field emission scanning electron microscopy coupled with energy dispersive X-ray spectrometry (FE-SEM+EDS), time of flight secondary ion mass spectrometry (ToF-SIMS), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and optical microscopy (OM). The results reveal in detail the surface and subsurface morphology and the chemical features of the micrometric decorative Au layer that has been deposited by means of the so-called fire-gilding technique based on the use of an amalgam. Moreover, the results allow to recognise chlorine, sulphur and phosphorous species as the main degradation agents and to identify the corrosion products naturally formed during the long-term interaction with the burial soil constituents. The findings show also that the galvanic coupling between the two dissimilar metals, i.e. Cu and Au, lead to enhancement of corrosion phenomena causing the spalling of the gold thin film and the disfigurement of the object. From a conservation point of view, the results suggest a targeted use of low-toxic inhibitors to hinder the detrimental role of chlorine as possible responsible of future further severe degradation phenomena. In conclusions, the micro and nano-chemical, structural and morphological investigations in a depth range from a few nanometers to micrometers have revealed the complex nature of corroded surface of ancient gold coated artefacts, highlighting some specific aspects related to their peculiar degradation mechanisms thus extending the scientific relevance of the tailored use of complementary and integrated surface and subsurface analytical techniques for the investigation of ancient coated artefacts.

Use of an Ultrasonic/Sonic Driller/Corer to Obtain Sample Powder for CHEMIN, a Combined XRD/XRF Instrument

NASA Technical Reports Server (NTRS)

Chipera, S. J.; Bish, D. L.; Vaniman, D. T.; Sherrit, S.; Bar-Cohen, Y.; Sarrazin, P.; Blake, D. F.

2003-01-01

A miniature CHEMIN XRD/XRF (X-Ray Diffraction/X-Ray Fluourescence) instrument is currently being developed for definitive mineralogic analysis of soils and rocks on Mars. One of the technical issues that must be addressed in order to enable XRD analysis on an extraterrestrial body is how best to obtain a representative sample powder for analysis. For XRD powder diffraction analyses, it is beneficial to have a fine-grained sample to reduce preferred orientation effects and to provide a statistically significant number of crystallites to the X-ray beam. Although a 2-dimensional detector as used in the CHEMIN instrument will produce good results with poorly prepared powders, the quality of the data will improve if the sample is fine-grained and randomly oriented. An Ultrasonic/Sonic Driller/Corer (USDC) currently being developed at JPL is an effective mechanism of sampling rock to produce cores and powdered cuttings. It requires low axial load (< 5N) and thus offers significant advantages for operation from lightweight platforms and in low gravity environments. The USDC is lightweight (<0.5kg), and can be driven at low power (<5W) using duty cycling. It consists of an actuator with a piezoelectric stack, ultrasonic horn, free-mass, and drill bit. The stack is driven with a 20 kHz AC voltage at resonance. The strain generated by the piezoelectric is amplified by the horn by a factor of up to 10 times the displacement amplitude. The tip impacts the free-mass and drives it into the drill bit in a hammering action. The free-mass rebounds to interact with the horn tip leading to a cyclic rebound at frequencies in the range of 60-1000 Hz. It does not require lubricants, drilling fluid or bit sharpening and it has the potential to operate at high and low temperatures using a suitable choice of piezoelectric material. To assess whether the powder from an ultrasonic drill would be adequate for analyses by an XRD/XRF spectrometer such as CHEMIN, powders obtained from the JPL

Quantitative assessment of alkali-reactive aggregate mineral content through XRD using polished sections as a supplementary tool to RILEM AAR-1 (petrographic method)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Castro, Nelia, E-mail: nelia.castro@ntnu.no; Sorensen, Bjorn E.; Broekmans, Maarten A.T.M.

The mineral content of 5 aggregate samples from 4 different countries, including reactive and non-reactive aggregate types, was assessed quantitatively by X-ray diffraction (XRD) using polished sections. Additionally, electron probe microanalyzer (EPMA) mapping and cathodoluminescence (CL) were used to characterize the opal-CT identified in one of the aggregate samples. Critical review of results from polished sections against traditionally powdered specimen has demonstrated that for fine-grained rocks without preferred orientation the assessment of mineral content by XRD using polished sections may represent an advantage over traditional powder specimens. Comparison of data on mineral content and silica speciation with expansion data frommore » PARTNER project confirmed that the presence of opal-CT plays an important role in the reactivity of one of the studied aggregates. Used as a complementary tool to RILEM AAR-1, the methodology suggested in this paper has the potential to improve the strength of the petrographic method.« less

Identification of a deleterious phase in photocatalyst based on Cd1 - xZnxS/Zn(OH)2 by simulated XRD patterns.

PubMed

Cherepanova, Svetlana; Markovskaya, Dina; Kozlova, Ekaterina

2017-06-01

The X-ray diffraction (XRD) pattern of a deleterious phase in the photocatalyst based on Cd 1 - x Zn x S/Zn(OH) 2 contains two relatively intense asymmetric peaks with d-spacings of 2.72 and 1.56 Å. Very small diffraction peaks with interplanar distances of (d) ≃ 8.01, 5.40, 4.09, 3.15, 2.49 and 1.35 Å are characteristic of this phase but not always observed. To identify this phase, the XRD patterns for sheet-like hydroxide β-Zn(OH) 2 and sheet-like hydrozincite Zn 5 (CO 3 ) 2 (OH) 6 as well as for turbostratic hydrozincite were simulated. It is shown that the XRD pattern calculated on the basis of the last model gives the best correspondence with experimental data. Distances between layers in the turbostratically disordered hydrozincite fluctuate around d ≃ 8.01 Å. This average layer-to-layer distance is significantly higher than the interlayer distance 6.77 Å in the ordered Zn 5 (CO 3 ) 2 (OH) 6 probably due to a deficiency of CO 3 2- anions, excess OH - and the presence of water molecules in the interlayers. It is shown by variable-temperature XRD and thermogravimetric analysis (TGA) that the nanocrystalline turbostratic nonstoichiometric hydrozincite-like phase is quite thermostable. It decomposes into ZnO in air above 473 K.

Evaluating mineralogy at terrestrial analogs for early Mars: Detection and characterization of clays with XRD and investigation of iron substitution in natroalunite

NASA Astrophysics Data System (ADS)

Beckerman, Laura Grace

The Mars Science Laboratory (MSL) Curiosity rover is equipped with CheMin, the first x-ray diffraction (XRD) instrument on Mars, for in situ mineralogy as part of its mission to seek evidence of past habitability at Gale Crater. Detection and characterization of hydrated minerals like clays and sulfates provides crucial insight into Mars' early geochemistry. For example, clays are often interpreted as having formed in lacustrine environments at neutral pHs, while sulfates such as jarosite are evidence of acid sulfate alteration. However, CheMin's inability to remove non-clay minerals and to preferentially orient samples may pose significant challenges to clay detection and characterization at Gale Crater. To evaluate the effect of particle size separation (<0.2 microm), removal of non-clay minerals, preferred orientation, and ethylene glycol solvation on XRD analyses of clays, we used both a CheMin analog instrument and a traditional laboratory XRD to identify clays in acid sulfate altered basalt from Mars analog sites in Costa Rica. We detected kaolinite in four of the fourteen samples studied, one of which also contained montmorillonite. Kaolinite was not detected in two samples with the analog instrument prior to clay isolation. These results suggest that CheMin may miss detection of some clays at Gale Crater, which could affect interpretations of early Mars' habitability. Mistaking iron-rich natroalunite (Na[Al,Fe]3(SO4) 2(OH)6) for jarosite (KFe3(SO4) 2(OH)6) could also impact interpretations of early Mars, as natroalunite can form over a broader range of pH, water:rock ratios, and redox conditions than can jarosite. To determine if iron-rich natroalunite is a common alteration product at Mars analog sites, we assessed iron content in natroalunite from Costa Rica. We detected up to 30% iron substitution in natroalunite at diverse geochemical settings. We also evaluated the feasibility of using XRD or Raman spectroscopy for in situ iron-rich natroalunite

XRD- and infrared-probed anisotropic thermal expansion properties of an organic semiconducting single crystal.

PubMed

Mohanraj, J; Capria, E; Benevoli, L; Perucchi, A; Demitri, N; Fraleoni-Morgera, A

2018-01-17

The anisotropic thermal expansion properties of an organic semiconducting single crystal constituted by 4-hydroxycyanobenzene (4HCB) have been probed by XRD in the range 120-300 K. The anisotropic thermal expansion coefficients for the three crystallographic axes and for the crystal volume have been determined. A careful analysis of the crystal structure revealed that the two different H-bonds stemming from the two independent, differently oriented 4HCB molecules composing the unit cell have different rearrangement patterns upon temperature variations, in terms of both bond length and bond angle. Linearly Polarized Mid InfraRed (LP-MIR) measurements carried out in the same temperature range, focused on the O-H bond spectral region, confirm this finding. The same LP-MIR measurements, on the basis of a semi-empirical relation and of geometrical considerations and assumptions, allowed calculation of the -CNH-O- hydrogen bond length along the a and b axes of the crystal. In turn, the so-calculated -CNH-O- bond lengths were used to derive the thermal expansion coefficients along the corresponding crystal axes, as well as the volumetric one, using just the LP-MIR data. Reasonable to good agreement with the same values obtained from XRD measurements was obtained. This proof-of-principle opens interesting perspectives about the possible development of a rapid, low cost and industry-friendly assessment of the thermal expansion properties of organic semiconducting single crystals (OSSCs) involving hydrogen bonds.

Synthesis, dynamic NMR characterization and XRD studies of novel N,N'-substituted piperazines for bioorthogonal labeling.

PubMed

Mamat, Constantin; Pretze, Marc; Gott, Matthew; Köckerling, Martin

2016-01-01

Novel, functionalized piperazine derivatives were successfully synthesized and fully characterized by 1 H/ 13 C/ 19 F NMR, MS, elemental analysis and lipophilicity. All piperazine compounds occur as conformers resulting from the partial amide double bond. Furthermore, a second conformational shape was observed for all nitro derivatives due to the limited change of the piperazine chair conformation. Therefore, two coalescence points were determined and their resulting activation energy barriers were calculated using 1 H NMR. To support this result, single crystals of 1-(4-nitrobenzoyl)piperazine ( 3a , monoclinic, space group C 2/ c , a = 24.587(2), b = 7.0726(6), c = 14.171(1) Å, β = 119.257(8)°, V = 2149.9(4) Å 3 , Z = 4, D obs = 1.454 g/cm 3 ) and the alkyne derivative 4-(but-3-yn-1-yl)-1-(4-fluorobenzoyl)piperazine ( 4b , monoclinic, space group P 2 1 / n , a = 10.5982(2), b = 8.4705(1), c = 14.8929(3) Å, β = 97.430(1)°, V = 1325.74(4) Å 3 , Z = 4, D obs = 1.304 g/cm 3 ) were obtained from a saturated ethyl acetate solution. The rotational conformation of these compounds was also verified by XRD. As proof of concept for future labeling purposes, both nitropiperazines were reacted with [ 18 F]F - . To test the applicability of these compounds as possible 18 F-building blocks, two biomolecules were modified and chosen for conjugation either using the Huisgen-click reaction or the traceless Staudinger ligation.

Sol-gel synthesis, phase composition, morphological and structural characterization of Ca10(PO4)6(OH)2: XRD, FTIR, SEM, 3D SEM and solid-state NMR studies

NASA Astrophysics Data System (ADS)

Kareiva, Simonas; Klimavicius, Vytautas; Momot, Aleksandr; Kausteklis, Jonas; Prichodko, Aleksandra; Dagys, Laurynas; Ivanauskas, Feliksas; Sakirzanovas, Simas; Balevicius, Vytautas; Kareiva, Aivaras

2016-09-01

Aqueous sol-gel chemistry route based on ammonium-hydrogen phosphate as the phosphorus precursor, calcium acetate monohydrate as source of calcium ions, and 1,2-ethylendiaminetetraacetic acid (EDTA), or 1,2-diaminocyclohexanetetracetic acid (DCTA), or tartaric acid (TA), or ethylene glycol (EG), or glycerol (GL) as complexing agents have been used to prepare calcium hydroxyapatite (Ca10(PO4)6(OH)2, CHAp). The phase transformations, composition, and structural changes in the polycrystalline samples were studied by infrared spectroscopy (FTIR), X-ray powder diffraction analysis (XRD), and scanning electron microscopy (SEM). The local short-range (nano- and mezo-) scale effects in CHAp were studied using solid-state NMR spectroscopy. The spatial 3D data from the SEM images of CHAp samples obtained by TA, EG and GL sol-gel routes were recovered for the first time to our knowledge.

Data from the Mars Science Laboratory CheMin XRD/XRF Instrument

NASA Technical Reports Server (NTRS)

Vaniman, David; Blake, David; Bristow, Tom; DesMarais, David; Achilles, Cherie; Anderson, Robert; Crips, Joy; Morookian, John Michael; Spanovich, Nicole; Vasavada, Ashwin;

XRD, Electron Microscopy and Vibrational Spectroscopy Characterization of Simulated SB6 HLW Glasses - 13028

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stefanovsky, S.V.; Institute of Physical Chemistry and Electrochemistry RAS, Leninskii av. 31, Moscow 119991; Nikonov, B.S.

2013-07-01

Sample glasses have been made using SB6 high level waste (HLW) simulant (high in both Al and Fe) with 12 different frit compositions at a constant waste loading of 36 wt.%. As follows from X-ray diffraction (XRD) and optical and scanning electron microscopy (SEM) data, all the samples are composed of primarily glass and minor concentration of spinel phases which form both isometric grains and fine cubic (∼1 μm) crystals. Infrared spectroscopy (IR) spectra of all the glasses within the range of 400-1600 cm{sup -1} consist of the bands due to stretching and bending modes in silicon-oxygen, boron-oxygen, aluminum-oxygen andmore » iron-oxygen structural groups. Raman spectra showed that for the spectra of all the glasses within the range of 850-1200 cm{sup -1} the best fit is achieved by suggestion of overlapping of three major components with maxima at 911-936 cm{sup -1}, 988-996 cm{sup -1} and 1020-1045 cm{sup -1}. The structural network is primarily composed of metasilicate chains and rings with embedded AlO{sub 4} and FeO{sub 4} tetrahedra. Major BO{sub 4} tetrahedra and BO{sub 3} triangles form complex borate units and are present as separate constituents. (authors)« less

High temperature XRD of Cu{sub 2}GeSe{sub 3}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Premkumar, D. S.; Malar, P.; Chetty, Raju

2015-06-24

The Cu{sub 2}GeSe{sub 3} is prepared by solid state synthesis method. The high temperature XRD has been done at different temperature from 30 °C to 450 °C. The reitveld refinement confirms Cu{sub 2}GeSe{sub 3} phase and orthorhombic crystal structure. The lattice constants are increasing with increase in the temperature and their rate of increase with respect to temperature are used for finding the thermal expansion coefficient. The calculation of the linear and volume coefficient of thermal expansion is done from 30 °C to 400 °C. Decrease in the values of linear expansion coefficients with temperature are observed along a andmore » c axis. Since thermal expansion coefficient is the consequence of the distortion of atoms in the lattice; this can be further used to find the minimum lattice thermal conductivity at given temperature.« less

An azodye-rhodamine-based fluorescent and colorimetric probe specific for the detection of Pd(2+) in aqueous ethanolic solution: synthesis, XRD characterization, computational studies and imaging in live cells.

PubMed

Mahapatra, Ajit Kumar; Manna, Saikat Kumar; Maiti, Kalipada; Mondal, Sanchita; Maji, Rajkishor; Mandal, Debasish; Mandal, Sukhendu; Uddin, Md Raihan; Goswami, Shyamaprosad; Quah, Ching Kheng; Fun, Hoong-Kun

2015-02-21

Azodye-rhodamine hybrid colorimetric fluorescent probe (L) has been designed and synthesized. The structure of L has been established based on single crystal XRD. It has been shown to act as a selective turn-on fluorescent chemosensor for Pd(2+) with >40 fold enhancement by exhibiting red emission among the other 27 cations studied in aqueous ethanol. The coordination features of the species of recognition have been computationally evaluated by DFT methods and found to have a distorted tetrahedral Pd(2+) center in the binding core. The probe (L) has been shown to detect Pd up to 0.45 μM at pH 7.4. Furthermore, the probe can be used to image Pd(2+) in living cells.

Characterizing the Phyllosilicates and Amorphous Phases Found by MSL Using Laboratory XRD and EGA Measurements of Natural and Synthetic Materials

NASA Technical Reports Server (NTRS)

Rampe, Elizabeth B.; Morris, Richard V.; Chipera, Steve; Bish, David L.; Bristow, Thomas; Archer, Paul Douglas; Blake, David; Achilles, Cherie; Ming, Douglas W.; Vaniman, David;

Investigation of Physically and Chemically Ionic Liquid Confinement in Nanoporous Materials by a Combination of SANS, Contrast-Matching SANS, XRD and Nitrogen Adsorption

NASA Astrophysics Data System (ADS)

Romanos, G. E.; Stefanopoulos, K. L.; Vangeli, O. C.; Mergia, K.; Beltsios, K. G.; Kanellopoulos, N. K.; Lairez, D.

2012-02-01

In the present study, [bmim][PF6] ionic liquid (IL) was introduced into the pores of two ordered mesoporous silicas (MCM-41 and SBA-15) having different pore sizes by means of two different processes: a) with physical imbibition from a methanol solution under high vacuum and b) by chemically immobilising the IL with silanisation of the pore surface followed by reaction with butyl-methyl imidazolium chloride and anion exchange with PF6, the process termed as the "grafting to" method. Both the extent of IL entrapment and the structural properties of the IL phase under confinement were investigated by SANS, contrast-matching SANS, XRD and nitrogen adsorption measurements. The results show that the pores of chemically prepared samples are not totally filled by IL and also suggest for ordering of the silylated IL phase. On the other hand, the physically prepared samples are almost or totally filled with IL whereas no evidence for ordering of the confined IL phase was observed.

Regional and National Grid Integration Studies Consistently Show Higher

Science.gov Websites

Levels of Renewables Are Possible | Energy Analysis | NREL Regional and National Grid Integration Studies Consistently Show Higher Levels of Renewables Are Possible Regional and National Grid Integration Studies Consistently Show Higher Levels of Renewables Are Possible Analysis Insights: April 2015

Characterizing the Phyllosilicate Component of the Sheepbed Mudstone in Gale Crater, Mars Using Laboratory XRD and EGA

NASA Technical Reports Server (NTRS)

Rampe, E. B.; Morris, R. V.; Ming, D. W.; Archer, P. D.; Bish, D. L.; Chipera, S. J.; Vaniman, D. T.; Blake, D. F.; Bristow, T. F.; Sutter, B.;

In-situ investigation of stress conditions during expansion of bare metal stents and PLLA-coated stents using the XRD sin(2)ψ-technique.

PubMed

Kowalski, Wolfgang; Dammer, Markus; Bakczewitz, Frank; Schmitz, Klaus-Peter; Grabow, Niels; Kessler, Olaf

2015-09-01

Drug eluting stents (DES) consist of platform, coating and drug. The platform often is a balloon-expandable bare metal stent made of the CoCr alloy L-605 or stainless steel 316 L. The function of the coating, typically a permanent polymer, is to hold and release the drug, which should improve therapeutic outcome. Before implantation, DES are compressed (crimped) to allow implantation in the human body. During implantation, DES are expanded by balloon inflation. Crimping, as well as expansion, causes high stresses and high strains locally in the DES struts, as well as in the polymer coating. These stresses and strains are important design criteria of DES. Usually, they are calculated numerically by finite element analysis (FEA), but experimental results for validation are hardly available. In this work, the X-ray diffraction (XRD) sin(2)ψ-technique is applied to in-situ determination of stress conditions of bare metal L-605 stents, and Poly-(L-lactide) (PLLA) coated stents. This provides a realistic characterization of the near-surface stress state and a validation option of the numerical FEA. XRD-results from terminal stent struts of the bare metal stent show an increasing compressive load stress in tangential direction with increasing stent expansion. These findings correlate with numerical FEA results. The PLLA-coating also bears increasing compressive load stress during expansion. Copyright © 2015 Elsevier Ltd. All rights reserved.

Quantitative shock stage assessment in olivine and pyroxene bearing meteorites via in situ micro-XRD

NASA Astrophysics Data System (ADS)

McCausland, P. J.; Flemming, R. L.; Izawa, M. R.

2010-12-01

Shock metamorphism is observed in most meteorites and impact structures [1]. Qualitative petrographic observations underpin a shock classification system [1-3] based on the deformation features in common silicates and on textural relations such as the development of maskelynite from feldspars, mobility of sulphides and metal in veins and local Fe-reduction in silicates. Shock deformation of minerals produces streaks (mosaicity) rather than discrete spots in 2D X-ray diffraction patterns, representing the progressive disruption of the crystal lattice into a mosaic of rotated domains [4,5]. Here we use in situ micro-XRD [5,6] to measure the mosaicity of olivine and pyroxene in ordinary chondrites of increasing shock stages S1 to S5 and then apply the method to achondrites with qualitatively low to high shock. X-ray diffraction data were collected in situ on polished thin sections and slab cut surfaces using a Bruker D8 Discover micro X-ray diffractometer [5], operated using CuKα radiation generated at 40 kV and 40 mA with a beam diameter of 500 μm. Diffracted X-rays were recorded with a 2D detector, giving images with information in both the 2-theta and chi dimensions, in which each lattice plane (hkl) will have a diffraction spot or streak lying along an arc in chi of radius 2-theta (hkl). Individual reflections can be indexed and then integrated as a function of chi angle, allowing examination of the peak shape and quantitative analysis of the mosaic peak FWHM along chi. We find that both forsterite and enstatite exhibit greater mosaicity in chi with increasing shock stage: Forsterite chi ranges from <1° for S1 to >6° for S5. Enstatite chi values from the same meteorites show a more subdued growth of streak length with shock state, from ~1° to ~4°. A slab of the olivine shergottite DaG 476 exhibits forsterite mosaicity of 6.9°+/-1.1°, indicating that it has experienced shock stage S5, with shock pressures 30-45 GPa [1,4], consistent with the 40-45 GPa shock

Synthesis, structural, spectroscopic, anti-cancer and molecular docking studies on novel 2-[(Anthracene-9-ylmethylene)amino]-2-methylpropane-1,3-diol using XRD, FTIR, NMR, UV-Vis spectra and DFT

NASA Astrophysics Data System (ADS)

Pavitha, P.; Prashanth, J.; Ramu, G.; Ramesh, G.; Mamatha, K.; Venkatram Reddy, Byru

2017-11-01

The novel titled compound 2-[(Anthracene-9-ylmethylene)amino]-2-methylpropane-1,3-diol (AMD) has been synthesized by slow evaporation technique from mixed solvent system of methanol with anthracene-9-carbaldehyde and 2-amino-2-methylpropane-1,3-diol. The synthesized molecule AMD was characterized experimentally by single crystal XRD, FTIR, NMR and UV-Vis spectra and density functional theory (DFT) computations. The structure of the crystal has been determined as orthorhombic system with space group P 21 21 21 and the cell parameters are obtained using XRD data. The optimized ground state geometry of the molecule is determined by evaluating torsional potentials as a function of angle of free rotation around Csbnd C bonds of functional groups by DFT method employing B3LYP functional with 6-311++G(d,p) basis set. All the fundamental vibrations of the molecule are assigned unambiguously using potential energy distribution (PED) obtained in the DFT computations. The rms error between the observed and scaled frequencies is 6.20 cm-1. The values of dipole moment, polarizability and hyperpolarizability are evaluated to study the NLO behavior of the molecule. The HOMO-LUMO energies and thermodynamic parameters are also determined. The molecular electrostatic surface potential (MESP) is mapped to obtain the charge density distribution. The 1H and 13C NMR chemical shifts of the molecule are calculated by the gauge independent atomic orbital (GIAO) method and compared with experimental results. UV-visible spectrum of the compound is also recorded in the region 200-800 nm to know the type of electronic transitions involved. The anti-cancer activity of AMD is determined against human breast cancer cell line MCF-7 and human prostate cancer cell line PC-3 and correlated the results with study of molecular docking against pharmacological protein IDO-1 receptor.

Ion-pairing in aqueous CaCl 2 and RbBr solutions. Simultaneous structural refinement of XAFS and XRD data

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pham, Thai V.; Fulton, John L.

2013-01-22

We present a new methodology involving the simultaneous refinement of both x-ray absorption and x-ray diffraction spectra (X-ray Absorption/Diffraction Structural Refinement,XADSR), to study hydration and ion pair structure of CaCl 2 and RbBr salts in concentrated aqueous solutions. The XADSR analysis includes the XAFS spectra analysis of both the cation and anion as a probe of their short-range structure with an XRD spectral analysis as a probe of the global structural. Together they deliver a comprehensive picture of the cation and anion hydration, the contact ion pair (CIP) structure and the solvent-separated ion pair (SSIP) structure. XADSR analysis of 6.0more » m aqueous CaCl 2 reveals that there are an insignificant number of Ca 2+-Cl- CIP’s, but there are approximately 3.4 SSIP’s separated by about 4.99 Å. In contrast XADSR analysis of aqueous RbBr yields about 0.7 pair CIP at a bond length 3.51 Å. The present work demonstrates a new approach for a direct co-refinement of XRD and XAFS spectra in a simple and reliable fashion, opening new opportunities for analysis in various disordered and crystalline systems. This work was supported by the U.S. Department of Energy (DOE), Office of Basic Energy Sciences, Division of Chemical Sciences, Geosciences and Biosciences. Pacific Northwest National Laboratory (PNNL) is operated for the U.S. Department of Energy by Battelle.« less

Landed XRD/XRF analysis of prime targets in the search for past or present Martian life.

PubMed

Vaniman, D; Bish, D; Blake, D; Elliott, S T; Sarrazin, P; Collins, S A; Chipera, S

1998-12-25

Mars landers seeking evidence for past or present life will be guided by information from orbital mapping and from previous surface exploration. Several target options have been proposed, including sites that may harbor extant life and sites most likely to preserve evidence of past life These sites have specific mineralogic characteristics. Extant life might be gathered around the sinters and associated mineral deposits of rare active fumaroles, or held within brine pockets and inclusions in a few evaporite-mineral deposits. Possibilities for fossilization include deltaic and lake-bottom sediments of once-flooded craters, sinters formed by ancient hot-spring deposits, and the carbonate deposits associated with some evaporite systems. However, the highly varied mineralogy of fossil occurrences on Earth leads to the inference that Mars, an equally complex planet, could host a broad variety of potential fossilizing deposits. The abundance of volcanic systems on Mars and evidence for close associations between volcanism and water release suggest possibilities of organism entrapment and mineralization in volcaniclastic deposits, as found in some instances on Earth. Thus the targets being considered for exploration include a wide variety of unique deposits that would be characterized by silica or various nonsilicate minerals. Beyond these "special" deposits and in the most general case, an ability to distinguish mineralized from uncemented volcanic detritus may be the key to success in finding possible fossil-bearing authigenic mineralogies. A prototype miniaturized X ray diffraction/X ray fluorescence (XRD/XRF) instrument has been evaluated with silica, carbonate, and sulfate minerals and with a basalt, to examine the capabilities of this tool in mineralogic and petrologic exploration for exobiological goals. This instrument. CHEMIN (chemical and mineralogical analyzer), is based on an innovative low-power X ray tube, transmission geometry, and CCD collection and

Structural, morphological and optical studies of F doped SnO2 thin films

NASA Astrophysics Data System (ADS)

Chandel, Tarun; Thakur, Vikas; Dwivedi, Shailendra Kumar; Zaman, M. Burhanuz; Rajaram, Poolla

2018-05-01

Highly conducting and transparent FTO (flourine doped tin Oxide) thin films were grown on the glass substrates using a low cost spray pyrolysis technique. The films were characterized for their structural, morphological and optical studies using XRD, SEM and UV-Vis spectroscopy. XRD studies show that the FTO films crystallize in Tetragonal cassiterite structure. Morphological analysis using SEM show that the films are uniformly covered with spherical grains albeit high in surface roughness. The average optical transmission greater than 80% in the visible region along with the appearance of interference fringes in the transmission curves confirms the high quality of the films. Electrical studies show that the films exhibit sheet resistance below 10 Ω ϒ-1.

Using Instruments as Applied Science, Multipurpose Tools During Human Exploration: An XRD/XRF Demonstration Strategy for the Deep Space Gateway

NASA Astrophysics Data System (ADS)

Bleacher, J. E.; Gendreau, K.; Arzoumanian, Z.; Young, K. E.; McAdam, A.

2018-02-01

Science instruments to be used during human exploration should be designed to serve as multipurpose tools that are of use throughout a mission. Here we discuss a multipurpose tool approach to using contact XRD/XRF onboard the Deep Space Gateway.

MICROSCANNING XRF, XANES, AND XRD STUDIES OF THEDECORATED SURFACE OF ROMAN TERRA SIGILLATA CERAMICS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mirguet, C.; Sciau, P.; Goudeau, P.

Different microscanning synchrotron techniques were used to better understand the elaboration process and origins of Terra Sigillata potteries from the Roman period. A mixture Gallic slip sample cross-section showing red and yellow colors was studied. The small (micron) size of the X-ray beam available at Stanford Synchrotron Radiation Laboratory (SSRL) and Advanced Light Source (ALS) synchrotron sources, coupled with the use of a sample scanning stage allowed us to spatially resolve the distribution of the constitutive mineral phases related to the chemical composition. Results show that red color is a result of iron-rich hematite crystals and the yellow part ismore » a result of the presence of Ti-rich rutile-type phase (brookite). Volcanic-type clay is at the origin of these marble Terra Sigillata.« less

Seismicity triggered by the olivine-spinel transition: New insights from combined XRD and acoustic emission monitoring during deformation experiments in Mg2GeO4

NASA Astrophysics Data System (ADS)

Schubnel, A. J.; Hilairet, N.; Gasc, J.; Héripré, E.; Brunet, F.; Wang, Y.

2010-12-01

Polycrystalline Mg2GeO4-olivine has been deformed (strain rates from 2.10-4/s to 10-5/s) in the deformation-DIA in 13-BM-D at GSECARS (Advanced Photon Source) at ca. 2 GPa confining pressure for temperatures between 973 and 1573 K (i.e., in the Mg2GeO4-ringwoodite field). Stress, advancement of transformation, and strain were measured in-situ using X-ray diffraction (XRD) and imaging, and acoustic emissions (AE) full waveforms were recorded simultaneously. When differential stress is applied (ca. 1- to 2 GPa) and temperature is increased, the very beginning of the transformation to the ringwoodite structure (as evidenced by in situ XRD) is accompanied by AE bursts which locate within the sample. At high strain rates (>10-4/s) and low temperatures (800-900 degrees C), the number of AEs is comparable, if not larger, to that observed during the cold compression of quartz grains. The largest events always occur at a temperature slightly below that of appearance of the ringwoodite-structure phase on the XRD images patterns. This suggests that AEs are generated while the transition is still nucleation controlled (pseudo-martensitic stage). During stress-relaxation periods, the rate of AE triggering decreases, but does not completely vanish. The AE production rate increases again as soon as deformation is started again. Importantly, we still observed very large AEs at strain rates as low as approx. 10-5/ s. At these early stages of the transformation, the samples did not show any macroscopic rheological weakening. Focal mechanism analysis of the largest AEs showed that they are all of shear type, some being even pure double couple. They radiate about the same amount of energy as typically recorded during fast crack propagation in amorphous glass material. This suggests that they cannot only originate from the martensitic nucleation of oriented spinel-lamellae within a single germanium olivine crystal. Preliminary microstructural analysis (SEM and EBSD) highlights the

Structural changes and thermal stability of charged LiNi xMn yCo zO 2 cathode materials studied by combined in situ time-resolved XRD and mass spectroscopy

DOE PAGES

Bak, Seong -Min; Hu, Enyuan; Zhou, Yongning; ...

2014-11-24

Thermal stability of charged LiNi xMn yCo zO 2 (NMC, with x + y + z = 1, x:y:z = 4:3:3 (NMC433), 5:3:2 (NMC532), 6:2:2 (NMC622), and 8:1:1 (NMC811)) cathode materials is systematically studied using combined in situ time- resolved X-ray diffraction and mass spectroscopy (TR-XRD/MS) techniques upon heating up to 600 °C. The TR-XRD/MS results indicate that the content of Ni, Co, and Mn significantly affects both the structural changes and the oxygen release features during heating: the more Ni and less Co and Mn, the lower the onset temperature of the phase transition (i.e., thermal decomposition) and themore » larger amount of oxygen release. Interestingly, the NMC532 seems to be the optimized composition to maintain a reasonably good thermal stability, comparable to the low-nickel-content materials (e.g., NMC333 and NMC433), while having a high capacity close to the high-nickel-content materials (e.g., NMC811 and NMC622). The origin of the thermal decomposition of NMC cathode materials was elucidated by the changes in the oxidation states of each transition metal (TM) cations (i.e., Ni, Co, and Mn) and their site preferences during thermal decomposition. It is revealed that Mn ions mainly occupy the 3a octahedral sites of a layered structure (R3¯m) but Co ions prefer to migrate to the 8a tetrahedral sites of a spinel structure (Fd3¯m) during the thermal decomposition. Such element-dependent cation migration plays a very important role in the thermal stability of NMC cathode materials. The reasonably good thermal stability and high capacity characteristics of the NMC532 composition is originated from the well-balanced ratio of nickel content to manganese and cobalt contents. As a result, this systematic study provides insight into the rational design of NMC-based cathode materials with a desired balance between thermal stability and high energy density.« less

Uranium speciation as a function of depth in contaminated hanford sediments--a micro-XRF, micro-XRD, and micro- and bulk-XAFS study.

PubMed

Singer, David M; Zachara, John M; Brown, Gordon E

2009-02-01

The distribution and speciation of U and Cu in contaminated vadose zone and aquifer sediments from the U.S. DOE Hanford site (300 Area) were determined using a combination of synchrotron-based micro-X-ray fluorescence (microXRF) imaging, micro-X-ray absorption near edge structure (microXANES) spectroscopy, and micro-X-ray diffraction (microXRD) techniques combined with bulk U LIII-edge X-ray absorption fine structure (XAFS) spectroscopy. Samples were collected from within the inactive North Process Pond (NPP2) at 8 ft (2.4 m, NPP2-8) depth and 12 ft (3.7 m, NPP2-12) depth in the vadose zone, and fines were isolated from turbid groundwater just below the water Table (12-14 ft, approximately 4 m, NPP2-GW). microXRF imaging, microXRD, and microXANES spectroscopy revealed two major U occurrences within the vadose and groundwater zones: (1) low to moderate concentrations of U(VI) associated with fine-textured grain coatings that were consistently found to contain clinochlore (referred to here as chlorite) observed in all three samples, and (2) U(VI)-Cu(II) hotspots consisting of micrometer-sized particles associated with surface coatings on grains of muscovite and chlorite observed in samples NPP2-8' and NPP2-GW. In the aquifer fines (NPP2-GW), these particles were identified as cuprosklodowskite (cps: Cu[(UO2)(SiO2OH)]2 x 6H2O) and metatorbernite (mtb: Cu(UO2)2(PO4)2 x 8H2O). In contrast, the U-Cu-containing particles in the vadose zone were X-ray amorphous. Analyses of U LIII-edge XAFS spectra by linear-combination fitting indicated that U speciation consisted of (1) approximately 75% uranyl sorbed to chlorite and approximately 25% mtb-like X-ray amorphous U-Cu-phosphates (8 ft depth), (2) nearly 100% sorbed uranyl (12 ft depth), and (3) approximately 70% uranyl sorbed to chlorite and approximately 30% cps/mtb (groundwater zone). These findings suggest that dissolution of U(VI)-Cu(II)-bearing solids as well as desorption of U(VI), mainly from phyllosilicates, are

Characterization of minerals in air dust particles in the state of Tamilnadu, India through FTIR, XRD and SEM analyses

NASA Astrophysics Data System (ADS)

Senthil Kumar, R.; Rajkumar, P.

2014-11-01

The abstract of this paper explains the presence of minerals in air which causes great concern regarding public health issues. The spectroscopic investigation of air dust particles of several samples in various locations in the state of Tamilnadu, India is reported. Qualitative analyses were carried out to determine the major and minor constituent minerals present in the samples based on the FTIR, XRD absorption peaks. This study also identified the minerals like quartz, asbestos, kaolinite, calcite, hematite, montmorillonite, nacrite and several other trace minerals in the air dust particles. The presents of quartz is mainly found in all the samples invariably. Hence the percentage of quartz and its crystalline nature were determined with the help of extinction co-efficient and crystallinity index respectively. The shape and size of the particulates are studied with SEM analysis.

Thermal decomposition of dolomite under CO2: insights from TGA and in situ XRD analysis.

PubMed

Valverde, Jose Manuel; Perejon, Antonio; Medina, Santiago; Perez-Maqueda, Luis A

2015-11-28

Thermal decomposition of dolomite in the presence of CO2 in a calcination environment is investigated by means of in situ X-ray diffraction (XRD) and thermogravimetric analysis (TGA). The in situ XRD results suggest that dolomite decomposes directly at a temperature around 700 °C into MgO and CaO. Immediate carbonation of nascent CaO crystals leads to the formation of calcite as an intermediate product of decomposition. Subsequently, decarbonation of this poorly crystalline calcite occurs when the reaction is thermodynamically favorable and sufficiently fast at a temperature depending on the CO2 partial pressure in the calcination atmosphere. Decarbonation of this dolomitic calcite occurs at a lower temperature than limestone decarbonation due to the relatively low crystallinity of the former. Full decomposition of dolomite leads also to a relatively low crystalline CaO, which exhibits a high reactivity as compared to limestone derived CaO. Under CO2 capture conditions in the Calcium-Looping (CaL) process, MgO grains remain inert yet favor the carbonation reactivity of dolomitic CaO especially in the solid-state diffusion controlled phase. The fundamental mechanism that drives the crystallographic transformation of dolomite in the presence of CO2 is thus responsible for its fast calcination kinetics and the high carbonation reactivity of dolomitic CaO, which makes natural dolomite a potentially advantageous alternative to limestone for CO2 capture in the CaL technology as well as SO2in situ removal in oxy-combustion fluidized bed reactors.

XRD, vibrational spectra and quantum chemical studies of an anticancer drug: 6-Mercaptopurine.

PubMed

Kumar, S Suresh; Athimoolam, S; Sridhar, B

2015-07-05

The single crystal of the hydrated anticancer drug, 6-Mercaptopurine (6-MP), has been grown by slow evaporation technique under room temperature. The structure was determined by single crystal X-ray diffraction. The vibrational spectral analysis was carried out using Laser Raman and FT-IR spectroscopy in the range of 3300-100 and 4000-400 cm(-1). The single crystal X-ray studies shows that the crystal packing is dominated by N-H⋯O and O-H⋯N classical hydrogen bonds leading to a hydrogen bonded ensemble. This classical hydrogen bonds were further connected through O-H⋯S hydrogen bond to form two primary ring R4(4)(16) and R4(4)(12) motifs. These two primary ring motifs are interlinked with each other to build a ladder like structure. These ladders are connected through N-H⋯N hydrogen bond along c-axis of the unit cell through chain C(5) motifs. Further, the strength of the hydrogen bonds is studied through vibrational spectral measurements. The shifting of bands due to the intermolecular interactions was also analyzed in the solid crystalline state. Geometrical optimizations of the drug molecule were done by Density Functional Theory (DFT) using the B3LYP function and Hartree-Fock (HF) level with 6-311++G(d,p) basis set. The optimized molecular geometry and computed vibrational spectra are compared with experimental results which show significant agreement. The natural bond orbital (NBO) analysis was carried out to interpret hyperconjugative interaction and intramolecular charge transfer (ICT). The chemical hardness, electro-negativity and chemical potential of the molecule are carried out by HOMO-LUMO plot. In which, the frontier orbitals has lower band gap value indicating the possible pharmaceutical activity of the molecule. Copyright © 2015 Elsevier B.V. All rights reserved.

Adsorption of Lysine on Na-Montmorillonite and Competition with Ca(2+): A Combined XRD and ATR-FTIR Study.

PubMed

Yang, Yanli; Wang, Shengrui; Liu, Jingyang; Xu, Yisheng; Zhou, Xiaoyun

2016-05-17

Lysine adsorption at clay/aqueous interfaces plays an important role in the mobility, bioavailability, and degradation of amino acids in the environment. Knowledge of these interfacial interactions facilitates our full understanding of the fate and transport of amino acids. Here, X-ray diffraction (XRD) and attenuated total reflectance Fourier-transform infrared spectroscopy (ATR-FTIR) measurements were used to explore the dynamic process of lysine adsorption on montmorillonite and the competition with Ca(2+) at the molecular level. Density functional theory (DFT) calculations were employed to determine the peak assignments of dissolved lysine in the solution phase. Three surface complexes, including dicationic, cationic, and zwitterionic structures, were observed to attach to the clay edge sites and penetrate the interlayer space. The increased surface coverage and Ca(2+) competition did not affect the interfacial lysine structures at a certain pH, whereas an elevated lysine concentration contributed to zwitterionic-type coordination at pH 10. Moreover, clay dissolution at pH 4 could be inhibited at a higher surface coverage with 5 and 10 mM lysine, whereas the inhibition effect was inconspicuous or undetected at pH 7 and 10. The presence of Ca(2+) not only could remove a part of the adsorbed lysine but also could facilitate the readsorption of dissolved Si(4+) and Al(3+) and surface protonation. Our results provide new insights into the process of lysine adsorption and its effects on montmorillonite surface sites.

A study of silver species on silver-exchanged ETS-10 and mordenite by XRD, SEM and solid-state 109Ag, 29Si and 27AI NMR spectroscopy.

PubMed

Liu, Yan; Chen, Fu; Wasylishen, Roderick E; Xu, Zhenghe; Sawada, James; Kuznicki, Steven M

2012-08-01

Silver zeolites, especially Ag-ETS-10 and Ag-mordenite, actively bind xenon and iodine, two prime contaminants common to nuclear accidents. The evolution of silver species on silver exchanged ETS-10 (Ag/ETS-10) and mordenite (Ag/Mor) has been investigated by exposing the materials to a series of activation conditions in Ar, air and H2. The samples were characterized by XRD, SEM and solid-state 109Ag, 29Si and 27AI MAS NMR. The silver reduction and structural evolution have been illustrated by those techniques. The effectiveness of one sample of each type of sieve was tested for its ability to trap mercury from a gas stream. However, the results from this study demonstrate that the adsorption characteristics of silver-loaded sieves cannot necessarily be predicted using a full complement of structural characterization techniques, which highlights the importance of understanding the formation and nature of silver species on molecular sieves.

Process monitoring and control with CHEMIN, a miniaturized CCD-based instrument for simultaneous XRD/XRF analysis

NASA Astrophysics Data System (ADS)

Vaniman, David T.; Bish, D.; Guthrie, G.; Chipera, S.; Blake, David E.; Collins, S. Andy; Elliott, S. T.; Sarrazin, P.

1999-10-01

There is a large variety of mining and manufacturing operations where process monitoring and control can benefit from on-site analysis of both chemical and mineralogic constituents. CHEMIN is a CCD-based instrument capable of both X-ray fluorescence (XRF; chemical) and X-ray diffraction (XRD; mineralogic) analysis. Monitoring and control with an instrument like CHEMIN can be applied to feedstocks, intermediate materials, and final products to optimize production. Examples include control of cement feedstock, of ore for smelting, and of minerals that pose inhalation hazards in the workplace. The combined XRD/XRF capability of CHEMIN can be used wherever a desired commodity is associated with unwanted constituents that may be similar in chemistry or structure but not both (e.g., Ca in both gypsum and feldspar, where only the gypsum is desired to make wallboard). In the mining industry, CHEMIN can determine mineral abundances on the spot and enable more economical mining by providing the means to assay when is being mined, quickly and frequently, at minimal cost. In manufacturing, CHEMIN could be used to spot-check the chemical composition and crystalline makeup of a product at any stage of production. Analysis by CHEMIN can be used as feedback in manufacturing processes where rates of heating, process temperature, mixture of feedstocks, and other variables must be adjusted in real time to correct structure and/or chemistry of the product (e.g., prevention of periclase and alkali sulfate coproduction in cement manufacture).

Characterisation of mineralogical forms of barium and trace heavy metal impurities in commercial barytes by EPMA, XRD and ICP-MS.

PubMed

Ansari, T M; Marr, I L; Coats, A M

2001-02-01

This study was carried out to characterise the mineralogical forms of barium and the trace heavy metal impurities in commercial barytes of different origins using electron probe microanalysis (EPMA), X-ray diffraction (XRD) and inductively coupled plasma mass spectrometry (ICP-MS). Qualitative EPMA results show the presence of typically eight different minerals in commercial barytes including barite (BaSO4), barium feldspar, galena (PbS), pyrite (FeS2), sphalerite (ZnS), quartz (SiO2), and silicates, etc. Quantitative EPMA confirms that the barite crystals in the barytes contain some strontium and a little calcium, whereas trace heavy metals occur in the associated minerals. Analysis of aqua regia extracts of barytes samples by ICP-MS has shown the presence of a large number of elements in the associated minerals. Arsenic, copper and zinc concentrations correlate closely in all 10 samples. The findings suggest that barytes is not, as traditionally thought, an inert mineral, but is a potentially toxic substance due to its associated heavy metal impurities, which can be determined by an aqua regia digest without the need for complete dissolution of the barite itself. X-ray powder diffraction was not informative as the complex barite pattern masks the very weak lines from the small amounts of associated minerals.

Study of structural and magnetic properties of cobalt ferrite nanoparticles sintered at different temperature

NASA Astrophysics Data System (ADS)

Kumari, Mukesh; Bhatnagar, Mukesh Chander

2018-05-01

Cobalt ferrite (CFO) has been synthesized in the form of nanoparticles (NPs) through sol-gel auto-combustion method. The prepared NPs of CFO were sintered for four hours at various temperatures from 300°C to 900°C. The physical properties of the sintered samples have been optimized using X-ray diffraction (XRD), Raman spectroscopy and physical properties measurement system (PPMS). The XRD and Raman studies have confirmed the cubic spinel phase formation of CFO NPs. XRD results showed that as we increase the sintering temperature the crystallite size of particles increases. Whereas the magnetic studies revealed that the saturation magnetization (MS) increases while the coercivity (HC) of nanoparticles decreases with increase of sintering temperature.

Size distribution of magnetic iron oxide nanoparticles using Warren-Averbach XRD analysis

NASA Astrophysics Data System (ADS)

Mahadevan, S.; Behera, S. P.; Gnanaprakash, G.; Jayakumar, T.; Philip, J.; Rao, B. P. C.

2012-07-01

We use the Fourier transform based Warren-Averbach (WA) analysis to separate the contributions of X-ray diffraction (XRD) profile broadening due to crystallite size and microstrain for magnetic iron oxide nanoparticles. The profile shape of the column length distribution, obtained from WA analysis, is used to analyze the shape of the magnetic iron oxide nanoparticles. From the column length distribution, the crystallite size and its distribution are estimated for these nanoparticles which are compared with size distribution obtained from dynamic light scattering measurements. The crystallite size and size distribution of crystallites obtained from WA analysis are explained based on the experimental parameters employed in preparation of these magnetic iron oxide nanoparticles. The variation of volume weighted diameter (Dv, from WA analysis) with saturation magnetization (Ms) fits well to a core shell model wherein it is known that Ms=Mbulk(1-6g/Dv) with Mbulk as bulk magnetization of iron oxide and g as magnetic shell disorder thickness.

Combining µXANES and µXRD mapping to analyse the heterogeneity in calcium carbonate granules excreted by the earthworm Lumbricus terrestris

PubMed Central

Brinza, Loredana; Schofield, Paul F.; Hodson, Mark E.; Weller, Sophie; Ignatyev, Konstantin; Geraki, Kalotina; Quinn, Paul D.; Mosselmans, J. Frederick W.

2014-01-01

The use of fluorescence full spectral micro-X-ray absorption near-edge structure (µXANES) mapping is becoming more widespread in the hard energy regime. This experimental method using the Ca K-edge combined with micro-X-ray diffraction (µXRD) mapping of the same sample has been enabled on beamline I18 at Diamond Light Source. This combined approach has been used to probe both long- and short-range order in calcium carbonate granules produced by the earthworm Lumbricus terrestris. In granules produced by earthworms cultured in a control artificial soil, calcite and vaterite are observed in the granules. However, granules produced by earthworms cultivated in the same artificial soil amended with 500 p.p.m. Mg also contain an aragonite. The two techniques, µXRD and µXANES, probe different sample volumes but there is good agreement in the phase maps produced. PMID:24365942

Gun Shows and Gun Violence: Fatally Flawed Study Yields Misleading Results

PubMed Central

Hemenway, David; Webster, Daniel; Pierce, Glenn; Braga, Anthony A.

2010-01-01

A widely publicized but unpublished study of the relationship between gun shows and gun violence is being cited in debates about the regulation of gun shows and gun commerce. We believe the study is fatally flawed. A working paper entitled “The Effect of Gun Shows on Gun-Related Deaths: Evidence from California and Texas” outlined this study, which found no association between gun shows and gun-related deaths. We believe the study reflects a limited understanding of gun shows and gun markets and is not statistically powered to detect even an implausibly large effect of gun shows on gun violence. In addition, the research contains serious ascertainment and classification errors, produces results that are sensitive to minor specification changes in key variables and in some cases have no face validity, and is contradicted by 1 of its own authors’ prior research. The study should not be used as evidence in formulating gun policy. PMID:20724672

Gun shows and gun violence: fatally flawed study yields misleading results.

PubMed

Wintemute, Garen J; Hemenway, David; Webster, Daniel; Pierce, Glenn; Braga, Anthony A

2010-10-01

A widely publicized but unpublished study of the relationship between gun shows and gun violence is being cited in debates about the regulation of gun shows and gun commerce. We believe the study is fatally flawed. A working paper entitled "The Effect of Gun Shows on Gun-Related Deaths: Evidence from California and Texas" outlined this study, which found no association between gun shows and gun-related deaths. We believe the study reflects a limited understanding of gun shows and gun markets and is not statistically powered to detect even an implausibly large effect of gun shows on gun violence. In addition, the research contains serious ascertainment and classification errors, produces results that are sensitive to minor specification changes in key variables and in some cases have no face validity, and is contradicted by 1 of its own authors' prior research. The study should not be used as evidence in formulating gun policy.

PyXRD v0.6.7: a free and open-source program to quantify disordered phyllosilicates using multi-specimen X-ray diffraction profile fitting

NASA Astrophysics Data System (ADS)

Dumon, M.; Van Ranst, E.

2016-01-01

This paper presents a free and open-source program called PyXRD (short for Python X-ray diffraction) to improve the quantification of complex, poly-phasic mixed-layer phyllosilicate assemblages. The validity of the program was checked by comparing its output with Sybilla v2.2.2, which shares the same mathematical formalism. The novelty of this program is the ab initio incorporation of the multi-specimen method, making it possible to share phases and (a selection of) their parameters across multiple specimens. PyXRD thus allows for modelling multiple specimens side by side, and this approach speeds up the manual refinement process significantly. To check the hypothesis that this multi-specimen set-up - as it effectively reduces the number of parameters and increases the number of observations - can also improve automatic parameter refinements, we calculated X-ray diffraction patterns for four theoretical mineral assemblages. These patterns were then used as input for one refinement employing the multi-specimen set-up and one employing the single-pattern set-ups. For all of the assemblages, PyXRD was able to reproduce or approximate the input parameters with the multi-specimen approach. Diverging solutions only occurred in single-pattern set-ups, which do not contain enough information to discern all minerals present (e.g. patterns of heated samples). Assuming a correct qualitative interpretation was made and a single pattern exists in which all phases are sufficiently discernible, the obtained results indicate a good quantification can often be obtained with just that pattern. However, these results from theoretical experiments cannot automatically be extrapolated to all real-life experiments. In any case, PyXRD has proven to be useful when X-ray diffraction patterns are modelled for complex mineral assemblages containing mixed-layer phyllosilicates with a multi-specimen approach.

High resolution HH-XRF scanning and XRD modelling as a tool in sedimentological analysis - A case study from the Enreca-3 core, Bach Long Vi Island, Vietnam

NASA Astrophysics Data System (ADS)

Rizzi, Malgorzata; Hemmingsen Schovsbo, Niels; Korte, Christoph; Bryld Wessel Fyhn, Michael

2017-04-01

To improve the understanding and interpretation of the depositional environment of a late Oligocene lacustrine organic rich oil-prone source rock succession, 2464 hand held (HH)-XRF measurements were made systematically on the 500 m long, continuous core from the fully cored Enreca-3 well. This core, drilled on the remote Bach Long Vi Island, northern Gulf of Tonkin, offshore Vietnam, represents a deep lake succession alternating between lacustrine pelagic dominated sediments interrupted by hyperpycnal turbidites, high density turbidites and debris flows [1, 2]. From a combined HH-XRF-XRD data set, multivariate data analysis and regression models are used to type the rock and to predict the XRD mineral composition based on HH-XRF composition. The rock types and the modelled mineral composition highlight the geochemical variations of the sediment and allows for direct comparison with sedimentological processes and facies changes. The modeling also depicts the cyclic alteration of rock types that are present on many different scales ranging from centimeters to hundreds of meters [1, 2]. The sedimentological and geochemical variations observed throughout the cored section reflects fluctuating paleoclimate, tectonism and hinterland condition controlling the depositional setting, which may provide a deeper understanding of the deposition of this and similar Paleogene syn-rift succession in the South China Sea region. It allows furthermore the development of a more generalized depositional model relevant for other deep-lacustrine syn-rift basins. [1] Petersen et al. (2014) Journal of Petroleum Geology, 37: 373-389. [2] Hovikoski et al. (2016) Journal of Sedimentary Research, 86(8): 982-1007.

Design and characterization of a mapping device optimized to collect XRD patterns from highly inhomogeneous and low density powder samples

NASA Astrophysics Data System (ADS)

D'Elia, A.; Cibin, G.; Robbins, P. E.; Maggi, V.; Marcelli, A.

2017-11-01

We report on the development of a device designed to improve X-ray Powder Diffraction data acquisition through mapping coupled to a rotational motion of the sample. The device and procedures developed aim at overcoming the experimental issues that accompany the analysis of inhomogeneous samples, such as powders, dust or aerosols deposited on a flat substrate. Introducing the mapping of the substrate on which powders are deposited and at the same time the rotation, we may overcome drawbacks associated to inhomogeneous distributions such as ring-like patterns due to the coffee stain effect generated by the evaporation of a solution. Experimental data have been collected from powders of a NIST standard soil sample (11 μg) and from an airborne dust extracted from deep ice cores in Antarctica (9.6 μg). Both particulate samples have been deposited on polycarbonate membranes from ultra-dilute solutions. Data show that this approach makes possible to collect XRD patterns useful to identify mineral fractions present in these low density samples.

In Operando XRD and TXM Study on the Metastable Structure Change of NaNi 1/3Fe 1/3Mn 1/3O 2 under Electrochemical Sodium-Ion Intercalation

DOE PAGES

Xie, Yingying; Wang, Hong; Xu, Guiliang; ...

2016-09-02

In operando XRD and TXM-XANES approaches demonstrate that structure evolution in NaNi 1/3Fe 1/3Mn 1/3O 2 during cycling follows a continuous change, and the formation of a nonequilibrium solid solution phase in the existence of two phases. Here, an O3' and P3' monoclinic phase occur, and redox couples of Ni 3+/Ni 4+ and Fe 3+/Fe 4+ are mainly responsible in the charge voltage range from 4.0 to 4.3 V.

A combined experimental and computational study of 3-bromo-5-(2,5-difluorophenyl) pyridine and 3,5-bis(naphthalen-1-yl)pyridine: Insight into the synthesis, spectroscopic, single crystal XRD, electronic, nonlinear optical and biological properties

NASA Astrophysics Data System (ADS)

Ghiasuddin; Akram, Muhammad; Adeel, Muhammad; Khalid, Muhammad; Tahir, Muhammad Nawaz; Khan, Muhammad Usman; Asghar, Muhammad Adnan; Ullah, Malik Aman; Iqbal, Muhammad

2018-05-01

Carbon-carbon coupling play a vital role in the synthetic field of organic chemistry. Two novel pyridine derivatives: 3-bromo-5-(2,5-difluorophenyl)pyridine (1) and 3,5-bis(naphthalen-1-yl)pyridine (2) were synthesized via carbon-carbon coupling, characterized by XRD, spectroscopic techniques and also investigated by using density functional theory (DFT). XRD data and optimized DFT studies are found to be in good correspondence with each other. The UV-Vis analysis of compounds under study i.e. (1) and (2) was obtained by using "TD-DFT/B3LYP/6-311 + G(d,p)" level of theory to explain the vertical transitions. Calculated FT-IR and UV-Vis results are found to be in good agreement with experimental FT-IR and UV-Vis findings. Natural bond orbital (NBO) study was performed using B3LYP/6-311 + G(d,p) level to find the most stable molecular structure of the compounds. Frontier molecular orbital (FMO) analysis were performed at B3LYP/6-311 + G(d,p) level of theory, which indicates that the molecules might be bioactive. Moreover, the bioactivity of compounds (1) and (2) have been confirmed by the experimental activity in terms of zones of inhibition against bacteria and fungus. Chemical reactivity of compounds (1) and (2) was indicated by mapping molecular electrostatic potential (MEP) over the entire stabilized geometries of the compounds under study. The nonlinear optical properties were computed with B3LYP/6-311 + G(d,p) level of theory which are found greater than the value of urea due to conjugation effect. Two state model has been further employed to explain the nonlinear optical properties of compounds under investigation.

Kinetics and structural changes of Li-rich layered oxide 0.5Li2MnO3·0.5LiNi(0.292)Co(0.375)Mn(0.333)O2 material investigated by a novel technique combining in situ XRD and a multipotential step.

PubMed

Shen, Chong-Heng; Huang, Ling; Lin, Zhou; Shen, Shou-Yu; Wang, Qin; Su, Hang; Fu, Fang; Zheng, Xiao-Mei

2014-08-13

Li-rich layered oxide 0.5Li2MnO3·0.5LiNi0.292Co0.375Mn0.333O2 was prepared by an aqueous solution-evaporation route. X-ray powder diffraction (XRD) showed that the as-synthesized material was a solid solution consisting of layered α-NaFeO2-type LiMO2 (M = Ni, Co, Mn) and monoclinic Li2MnO3. The superlattice spots in the selected area electron diffraction pattern indicated the ordering of lithium ions with transition metal (TM) ions in TM layers in this Li-rich layered oxide. Electrochemical performance testing showed that the as-synthesized material could deliver an initial discharge capacity of 267.7 mAh/g, with a capacity retention of 88.5% after 33 cycles. A new combination technique, multipotential step in situ XRD (MPS in situ XRD) measurement, was applied for the first time to investigate the Li-rich layered oxide. Using this approach, the relationships between kinetics and structural variations can be obtained simutaneously. In situ XRD results showed that the c parameter decreased from 3.70 to 4.30 V and increased from 4.30 to 4.70 V, whereas the a parameter underwent a decrease above 4.30 V during the first charge process. Below 3.90 V during the first discharge process, a slight decrease in the c parameter was found along with an increase in the a parameter. During the first charge process, the value of the coefficient of diffusion for lithium ions (DLi+) decreased to its mininum at 4.55 V, which might be associated with Ni(2+) migration, as indicated by both Ni occupancy in 3b sites (Ni3b%) in the Li(+) layers and complicated chemical reactions. Remarkably, a lattice distortion might occur within the local domain in the host stucture during the first discharge process, indicated by a slight splitting of the (003) diffraction peak at 3.20 V.

Microanalysis (micro-XRF, micro-XANES, and micro-XRD) of a tertiary sediment using microfocused synchrotron radiation.

PubMed

Denecke, Melissa A; Somogyi, Andrea; Janssens, Koen; Simon, Rolf; Dardenne, Kathy; Noseck, Ulrich

2007-06-01

Micro-focused synchrotron radiation techniques to investigate actinide elements in geological samples are becoming an increasingly used tool in nuclear waste disposal research. In this article, results using mu-focus techniques are presented from a bore core section of a U-rich tertiary sediment collected from Ruprechtov, Czech Republic, a natural analog to nuclear waste repository scenarios in deep geological formations. Different methods are applied to obtain various, complementary information. Elemental and element chemical state distributions are obtained from micro-XRF measurements, oxidation states of As determined from micro-XANES, and the crystalline structure of selected regions are studied by means of micro-XRD. We find that preparation of the thin section created an As oxidation state artifact; it apparently changed the As valence in some regions of the sample. Results support our previously proposed hypothesis of the mechanism for U-enrichment in the sediment. AsFeS coating on framboid Fe nodules in the sediment reduced mobile groundwater-dissolved U(VI) to less-soluble U(IV), thereby immobilizing the uranium in the sediment.

Study Shows Philippine Power System Can Achieve 30% and 50% Renewable

Science.gov Websites

Energy by 2030 | News | NREL Study Shows Philippine Power System Can Achieve 30% and 50 % Renewable Energy by 2030 Study Shows Philippine Power System Can Achieve 30% and 50% Renewable Energy by of the Philippines (NGCP), and the Philippine Electricity Market Association produced the study

Structure analysis and spectroscopic characterization of 2-Fluoro-3-Methylpyridine-5-Boronic Acid with experimental (FT-IR, Raman, NMR and XRD) techniques and quantum chemical calculations

NASA Astrophysics Data System (ADS)

Alver, Özgür; Dikmen, Gökhan

2016-03-01

Possible stable conformers, geometrical molecular structures, vibrational properties as well as band assignments, nuclear magnetic shielding tensors of 2-Fluoro-3-Methylpyridine-5-Boronic Acid (2F3MP5BA) were studied experimentally and theoretically using FT-IR, Raman, (CP/MAS) NMR and XRD spectroscopic methods. FT-IR and Raman spectra were evaluated in the region of 3500-400 cm-1, and 3200-400 cm-1, respectively. The optimized geometric structures, vibrational wavenumbers and nuclear magnetic shielding tensors were examined using Becke-3-Lee-Yang-Parr (B3LYP) hybrid density functional theory method with 6-311++G(d, p) basis set. 1H, 13C NMR chemical shifts were calculated using the gauge invariant atomic orbital (GIAO) method. 1H, 13C, APT and HETCOR NMR experiments of title molecule were carried out in DMSO solution. 13C CP/MAS NMR measurement was done with 4 mm zirconium rotor and glycine was used as an external standard. Single crystal of 2F3MP5BA was also prepared for XRD measurements. Assignments of vibrational wavenumbers were also strengthened by calculating the total energy distribution (TED) values using scaled quantum mechanical (SQM) method.

Synthesis and characterization of 64SiO2-26CaO-5P2O5-5CuO bioactive composition for the growth of hydroxyapatite layer by XRD, Raman and pH studies

NASA Astrophysics Data System (ADS)

Kaur, Pardeep; Singh, K. J.

2016-05-01

Bioactive sample with the nominal composition of 64SiO2-26CaO-5P2O5-5CuO has been prepared in the laboratory by using the sol-gel technique. The bioactivity of the prepared sample has been analyzed by using the Tris Simulated Body Fluid which has also been prepared in the laboratory. XRD and Raman techniques have been employedto probe the formation of hydroxyapatite layer. pH studies has also been undertaken to check the acidic/non-acidic behavior of sample. Growth of hydroxyapatite layer has been observed after one day on the surface of the sample. Moreover, sample has been observed to be non-acidic in nature.

Study by NOAA and Partners Shows Some Gulf Dolphins Severely Ill | NOAA

Science.gov Websites

Publications Press Releases Story Archive Home Study by NOAA and Partners Shows Some Gulf Dolphins Severely Ill Study by NOAA and Partners Shows Some Gulf Dolphins Severely Ill Aug 2011: Veterinarians collect samples of 2011, preliminary results show that many of the dolphins in the study are underweight, anemic

Astrobiological Significance of Definitive Mineralogical Analysis of Martian Surface Samples Using the CheMin XRD/XRF Instrument

NASA Technical Reports Server (NTRS)

Feldman, S. M.; Blake, D. F.; Sarrazin, P.; Bish, D. L.; Chipera, S. J.; Vaniman, D. T.; Collins, S.

2004-01-01

The search for evidence of habitability, or of extant or extinct life on Mars, will initially be a search for evidence of past or present conditions supportive of life. The three key requirements for the emergence of life are thought to be liquid water; a suitable energy source; and chemical building blocks. CheMin is a miniaturized XRD/XRF (X-Ray diffraction / X-ray fluorescence) instrument which has been developed for definitive mineralogic analysis of soils and rocks on the Martian surface. The CheMin instrument can provide information that is highly relevant to each of these habitability requirements as summarized below.

Synthesis, XRD single crystal structure analysis, vibrational spectral analysis, molecular dynamics and molecular docking studies of 2-(3-methoxy-4-hydroxyphenyl) benzothiazole

NASA Astrophysics Data System (ADS)

Sarau Devi, A.; Aswathy, V. V.; Sheena Mary, Y.; Yohannan Panicker, C.; Armaković, Stevan; Armaković, Sanja J.; Ravindran, Reena; Van Alsenoy, C.

2017-11-01

The vibrational spectra and corresponding vibrational assignments of 2-(3-methoxy-4-hydroxyphenyl)benzothiazole is reported. Single crystal XRD data of the title compound is reported and the orientation of methoxy group is cis to nitrogen atom of the thiazole ring. The phenyl ring breathing modes of the title compound are assigned at 1042 and 731 cm-1 theoretically. The charge transfer within the molecule is studied using frontier molecular orbital analysis. The chemical reactivity descriptors are calculated theoretically. The NMR spectral data predicted theoretically are in good agreement with the experimental data. The strong negative region spread over the phenyl rings, nitrogen atom and oxygen atom of the hydroxyl group in the MEP plot is due to the immense conjugative and hyper conjugative resonance charge delocalization of π-electrons. Molecule sites prone to electrophilic attacks have been determined by analysis of ALIE surfaces, while Fukui functions provided further insight into the local reactivity properties of title molecule. Autoxidation properties have been investigated by calculation of bond dissociation energies (BDEs) of hydrogen abstraction, while BDEs of the rest of the single acyclic bonds were valuable for the further investigation of degradation properties. Calculation of radial distribution functions was performed in order to determine which atoms of the title molecule have pronounced interactions with water molecules. The title compound forms a stable complex with aryl hydrocarbon receptor and can be a lead compound for developing new anti-tumor drug. Antimicrobial properties of the title compound was screened against one bacterial culture Escherchia coli and four fungal cultures viz., Aspergillus niger, Pencillum chrysogenum, Saccharomyces cerevisiae and Rhyzopus stolonifer.

Interactions between 2,4-bis-pteridine-1,5-benzodiazepine and group 12 dihalides: synthesis, spectral and XRD structural studies and theoretical calculations.

PubMed

Illán-Cabeza, Nuria A; Jiménez-Pulido, Sonia B; Hueso-Ureña, Francisco; Peña-Ruiz, Tomás; Quirós-Olozábal, Miguel; Moreno-Carretero, Miguel N

2016-11-28

2,4-Bis(1,3,7-trimethyl-pteridine-2,4(1H,3H)-dione-6-yl)-2,3-dihydro-2-methyl-1H-1,5-benzodiazepine (DLMBZD) has been prepared and its molecular and crystal structures have been determined from spectral and XRD data. The benzodiazepine ligand was reacted with zinc(ii), cadmium(ii) and mercury(ii) chloride, bromide and iodide to give complexes with general formula [M(DLMBZD)X 2 ]. The complexes have been synthesized and characterized by IR, NMR and elemental analysis. The structure of seven complexes has been obtained by single crystal X-ray diffraction. In all the cases, the metal is (2 + 2 + 1)-five-coordinated by two halide ligands, two nitrogen atoms from pyrazine and diazepine rings and a carbonyl oxygen from a pteridine ring. The coordinated-metal environment is a square-based pyramid, with increasing trigonality from Hg(ii) to Zn(ii) complexes. To coordinate the metals, the ligand folds itself, establishing four intramolecular σ-π interactions with the pyrimidine and pyrazine rings. A topological analysis of the electron density using the Quantum Theory of Atoms in Molecules and the complexes stability has been performed.

3-Iodobenzaldehyde: XRD, FT-IR, Raman and DFT studies.

PubMed

Kumar, Chandraju Sadolalu Chidan; Parlak, Cemal; Tursun, Mahir; Fun, Hoong-Kun; Rhyman, Lydia; Ramasami, Ponnadurai; Alswaidan, Ibrahim A; Keşan, Gürkan; Chandraju, Siddegowda; Quah, Ching Kheng

2015-06-15

The structure of 3-iodobenzaldehyde (3IB) was characterized by FT-IR, Raman and single-crystal X-ray diffraction techniques. The conformational isomers, optimized geometric parameters, normal mode frequencies and corresponding vibrational assignments of 3IB were examined using density functional theory (DFT) method, with the Becke-3-Lee-Yang-Parr (B3LYP) functional and the 6-311+G(3df,p) basis set for all atoms except for iodine. The LANL2DZ effective core basis set was used for iodine. Potential energy distribution (PED) analysis of normal modes was performed to identify characteristic frequencies. 3IB crystallizes in monoclinic space group P21/c with the O-trans form. There is a good agreement between the theoretically predicted structural parameters, and vibrational frequencies and those obtained experimentally. In order to understand halogen effect, 3-halogenobenzaldehyde [XC6H4CHO; X=F, Cl and Br] was also studied theoretically. The free energy difference between the isomers is small but the rotational barrier is about 8kcal/mol. An atypical behavior of fluorine affecting conformational preference is observed. Copyright © 2015 Elsevier B.V. All rights reserved.

The Mineralogy of Martian Dust: Design and Analysis Considerations for an X-Ray Diffraction/X-Ray Fluorescence (XRD/XRF) Instrument for Exobiological Studies

NASA Technical Reports Server (NTRS)

Blake, David; Vaniman, David; Bish, David; Morrison, David (Technical Monitor)

1994-01-01

A principal objective of Mars exploration is the search for evidence of past life which may have existed during an earlier clement period of Mars history. We would like to investigate the history of surface water activity (which is a requirement for all known forms of life) by identifying and documenting the distribution of minerals which require water for their formation or distribution. A knowledge of the mineralogy of the present Martian surface would help to identify areas which, due to the early activity of water, might have harbored ancient life. It would be desirable to establish the presence and characterize the distribution of hydrated minerals such as clays, and of minerals which are primarily of sedimentary origin such as carbonates, silica and evaporites. Mineralogy, which is more critical to exobiological exploration than is simple chemical analysis (absent the detection of organics), will remain unknown or will at best be imprecisely constrained unless a technique sensitive to mineral structure such as powder X-ray diffraction (XRD) is employed. Additional information is contained in the original extended abstract.

Proton transfer and hydrogen bonding in the organic solid state: a combined XRD/XPS/ssNMR study of 17 organic acid-base complexes.

PubMed

Stevens, Joanna S; Byard, Stephen J; Seaton, Colin C; Sadiq, Ghazala; Davey, Roger J; Schroeder, Sven L M

2014-01-21

The properties of nitrogen centres acting either as hydrogen-bond or Brønsted acceptors in solid molecular acid-base complexes have been probed by N 1s X-ray photoelectron spectroscopy (XPS) as well as (15)N solid-state nuclear magnetic resonance (ssNMR) spectroscopy and are interpreted with reference to local crystallographic structure information provided by X-ray diffraction (XRD). We have previously shown that the strong chemical shift of the N 1s binding energy associated with the protonation of nitrogen centres unequivocally distinguishes protonated (salt) from hydrogen-bonded (co-crystal) nitrogen species. This result is further supported by significant ssNMR shifts to low frequency, which occur with proton transfer from the acid to the base component. Generally, only minor chemical shifts occur upon co-crystal formation, unless a strong hydrogen bond is formed. CASTEP density functional theory (DFT) calculations of (15)N ssNMR isotropic chemical shifts correlate well with the experimental data, confirming that computational predictions of H-bond strengths and associated ssNMR chemical shifts allow the identification of salt and co-crystal structures (NMR crystallography). The excellent agreement between the conclusions drawn by XPS and the combined CASTEP/ssNMR investigations opens up a reliable avenue for local structure characterization in molecular systems even in the absence of crystal structure information, for example for non-crystalline or amorphous matter. The range of 17 different systems investigated in this study demonstrates the generic nature of this approach, which will be applicable to many other molecular materials in organic, physical, and materials chemistry.

Free volume in ionic liquids: a connection of experimentally accessible observables from PALS and PVT experiments with the molecular structure from XRD data.

PubMed

Beichel, Witali; Yu, Yang; Dlubek, Günter; Krause-Rehberg, Reinhard; Pionteck, Jürgen; Pfefferkorn, Dirk; Bulut, Safak; Bejan, Dana; Friedrich, Christian; Krossing, Ingo

2013-06-14

In the current work, free volume concepts, primarily applied to glass formers in the literature, were transferred to ionic liquids (ILs). A series of 1-butyl-3-methylimidazolium ([C4MIM](+)) based ILs was investigated by Positron Annihilation Lifetime Spectroscopy (PALS). The phase transition and dynamic properties of the ILs [C4MIM][X] with [X](-) = [Cl](-), [BF4](-), [PF6](-), [OTf](-), [NTf2](-) and [B(hfip)4](-) were reported recently (Yu et al., Phys. Chem. Chem. Phys., 2012, 14, 6856-6868). In this subsequent work, attention was paid to the connection of the free volume from PALS (here the mean hole volume, ) with the molecular structure, represented by volumes derived from X-ray diffraction (XRD) data. These were the scaled molecular volume Vm,scaled and the van der Waals volume V(vdw). Linear correlations of at the "knee" temperature ((T(k))) with V(m,scaled) and V(vdw) gave good results for the [C4MIM](+) series. Further relationships between volumes from XRD data with the occupied volume Vocc determined from PALS/PVT (Pressure Volume Temperature) measurements and from Sanchez-Lacombe Equation of State (SL-EOS) fits were elaborated (V(occ)(SL-EOS) ≈ 1.63 V(vdw), R(2) = 0.981 and V(occ)(SL-EOS) ≈ 1.12 V(m,scaled), R(2) = 0.980). Finally, the usability of V(m,scaled) was justified in terms of the Cohen-Turnbull (CT) free volume theory. Empirical CT type plots of viscosity and electrical conductivity showed a systematic increase in the critical free volume with molecular size. Such correlations allow descriptions of IL properties with the easily accessible quantity V(m,scaled) within the context of the free volume.

Phase study and surface morphology of beta-alumina

NASA Astrophysics Data System (ADS)

Tak, S. K.

2018-05-01

Beta alumina ceramic is well known as a polycrystalline ceramic material. The characteristic crystal structure of beta-alumina makes it useful as a separator in sodium sulphur batteries and other electrochemical devices requiring the passage of sodium ions. β"-alumina powders for this study were prepared by zeta process. The pellets were sintered at different microwave power levels and power schedule to optimize the sintering conditions to obtain preferred β" phase with improved microstructure. Phase identification was studied by X-ray diffraction (XRD). XRD analysis shows increase in β'' phase as the sintering temperature was increased from 1400°C to 1600°C. Surface morphology of the pellets was carried out by Scanning Electron microscopy (SEM). SEM studies revealed the formation and growth of platelet grains with interconnected porosity.

XRD investigation of the Effect of MgO Additives on ZTA-TiO2 Ceramic Composites

NASA Astrophysics Data System (ADS)

Azhar, Ahmad Zahirani Ahmad; Manshor, Hanisah; Ali, Afifah Mohd

2018-01-01

Alumina (Al2O3) based ceramics possess good mechanical properties and suitable for the application of cutting inserts. However, this monolithic ceramics suffer from lack of toughness. Hence, there are some modification were made such as the addition of yttria stabilized zirconia (YSZ) to the Al2O3 helps in increasing the toughness of the Al2O3 ceramics. Some additives such as MgO and TiO2 were used to further improve the mechanical properties of ZTA. In this study, high purity raw materials which consist of ZTA-TiO2 were mixed with different amount of MgO (0.0 - 1.0 wt %). The mixture of materials was going through wet mixing, compaction and pressureless sintering at 1600°C for one hour. The samples were characterized for phase analysis, microstructure, shrinkage rate, bulk density, Vickers hardness and fracture toughness. Based on the XRD analysis results, the secondary phase (MgAl2O4) was detected in the sample with 0.5 wt% of MgO onwards which leads to grains refinement, thus improve the density and hardness of ZTA-TiO2-MgO ceramics composites.

A comparative study: Effect of plasma on V2O5 nanostructured thin films

NASA Astrophysics Data System (ADS)

Singh, Megha; Kumar, Prabhat; Sharma, Rabindar K.; Reddy, G. B.

2016-05-01

Vanadium pentoxide nanostructured thin films (NSTs) have been studied to analyze the effect of plasma on nanostructures grown and morphology of films deposited using sublimation process. Nanostructured thin films were deposited on glass substrates, one in presence of oxygen plasma and other in oxygen environment (absence of plasma). Films were characterized using XRD, Raman spectroscopy, SEM and HRTEM. XRD studies revealed α-V2O5 films (orthorhombic phase) with good crystallinity. However, film deposited in presence of plasma have higher peak intensities as compared to those deposited in absence of plasma. Raman studies also support these finding following same trends of considerable increase in intensity in case of film deposited in presence of plasma. SEM micrographs makes the difference more visible, as film deposited in plasma have well defined plate like structures whereas other film have not-clearly-defined petal-like structures. HRTEM results show orthorhombic phase with 0.39 nm interplanar spacing, as reported by XRD. Results are hereby in good agreement with each other.

Physiochemical Characterization and Release Rate Studies of SolidDispersions of Ketoconazole with Pluronic F127 and PVP K-30

PubMed Central

Kumar, Pankaj; Mohan, Chander; KanamSrinivasan Uma Shankar, Mara; Gulati, Monica

2011-01-01

In the present study solid dispersions of the antifungal drug Ketoconazole were prepared with Pluronic F-127 and PVP K-30 with an intention to improve its dissolution properties. Investigations of the properties of the dispersions were performed using release studies, Differential scanning calorimetery (DSC), X-ray powder diffraction (XRD) and Fourier transform infrared (FTIR). The results obtained showed that the rate of dissolution of Ketoconazole was considerably improved when formulated in solid dispersions with PVP K-30 and Pluronic F-127 as compared with pure drug and physical mixtures. The results from DSC and XRD studies showed the transition of crystalline nature of drug to amorphous form, while FTIR studies demonstrated the absence of drug-carriers interaction. PMID:24250403

Study Shows India Can Integrate 175 GW of Renewable Energy into Its

Science.gov Websites

Electricity Grid | News | News | NREL Study Shows India Can Integrate 175 GW of Renewable Energy into Its Electricity Grid News Release: Study Shows India Can Integrate 175 GW of Renewable Energy Corporation, Ltd. (POSOCO); and Lawrence Berkeley National Laboratory (LBNL) produced the study Greening the

Facile synthesis of the Li-rich layered oxide Li1.23Ni0.09Co0.12Mn0.56O2 with superior lithium storage performance and new insights into structural transformation of the layered oxide material during charge-discharge cycle: in situ XRD characterization.

PubMed

Shen, Chong-Heng; Wang, Qin; Fu, Fang; Huang, Ling; Lin, Zhou; Shen, Shou-Yu; Su, Hang; Zheng, Xiao-Mei; Xu, Bin-Bin; Li, Jun-Tao; Sun, Shi-Gang

2014-04-23

In this work, the Li-rich oxide Li1.23Ni0.09Co0.12Mn0.56O2 was synthesized through a facile route called aqueous solution-evaporation route that is simple and without waste water. The as-prepared Li1.23Ni0.09Co0.12Mn0.56O2 oxide was confirmed to be a layered LiMO2-Li2MnO3 solid solution through ex situ X-ray diffraction (ex situ XRD) and transmission electron microscopy (TEM). Electrochemical results showed that the Li-rich oxide Li1.23Ni0.09Co0.12Mn0.56O2 material can deliver a discharge capacity of 250.8 mAhg(-1) in the 1st cycle at 0.1 C and capacity retention of 86.0% in 81 cycles. In situ X-ray diffraction technique (in situ XRD) and ex situ TEM were applied to study structural changes of the Li-rich oxide Li1.23Ni0.09Co0.12Mn0.56O2 material during charge-discharge cycles. The study allowed observing experimentally, for the first time, the existence of β-MnO2 phase that is appeared near 4.54 V in the first charge process, and a phase transformation of the β-MnO2 to layered Li0.9MnO2 is occurred in the initial discharge process by evidence of in situ XRD pattrens and selected area electron diffraction (SAED) patterns at different states of the initial charge and discharge process. The results illustrated also that the variation of the in situ X-ray reflections during charge-discharge cycling are clearly related to the changes of lattice parameters of the as-prepared Li-rich oxide during the charge-discharge cycles.

DSC and Raman studies of silver borotellurite glasses

NASA Astrophysics Data System (ADS)

Kaur, Amandeep; Khanna, Atul; Gonzàlez, Fernando

2016-05-01

Silver borotellurite glasses of composition: xAg2O-yB2O3-(100-x-y)TeO2 (x=20-mol%, y = 0, 10, 20 and 30-mol%) were prepared and characterized by density, X-ray diffraction (XRD), differential scanning calorimetry, and Raman spectroscopy. XRD confirmed the amorphous structure of all samples. Density of glasses decreases while the glass transition temperature increases with increase in B2O3 content from 10 to 30-mol%. Raman study shows that coordination number of Te with oxygen decreases steadily from 3.42 to 3.18 on adding B2O3 due to the transformation of TeO4 into TeO3 units.

CO2 study shows effects on scrub oak environment

NASA Technical Reports Server (NTRS)

2000-01-01

CO2 study site manager and plant physiologist Graham Hymus (left) examines scrub oak foliage while project engineer David Johnson (right) looks on. The life sciences study is showing that rising levels of carbon dioxide in our atmosphere, caused by the burning of fossil fuels, could spur plant growth globally. The site of KSC's study is a natural scrub oak area near the Vehicle Assembly Building. Twelve-foot areas of scrub oak have been enclosed in 16 open-top test chambers into which CO2 has been blown. Five scientists from NASA and the Smithsonian Environmental Research Center in Edgewater, Md., work at the site to monitor experiments and keep the site running. Scientists hope to continue the study another five to 10 years. More information on this study can be found in Release No. 57- 00.

Measurement and characterization of external oil in the fried waxy maize starch granules using ATR-FTIR and XRD.

PubMed

Chen, Long; Tian, Yaoqi; Sun, Binghua; Cai, Canxin; Ma, Rongrong; Jin, Zhengyu

2018-03-01

Concerns regarding increased dietary oil uptake have prompted efforts to investigate the oil absorption and distribution in fried starchy foods. In the present study, attenuated total reflection Fourier transform infrared (ATR-FTIR) spectroscopy, together with a chloroform-methanol method, was used to analyze the external and internal oil contents in fried starchy samples. The micromorphology of fried starchy samples was further investigated using scanning electron microscope (SEM), polarized light microscope (PLM) and confocal laser scanning microscopy (CLSM). The results indicated that large amounts of oil were absorbed in or within waxy maize starch, but the majority of oil was located near the surface layer of the starch granules. After defatting, the internal oil was thoroughly removed, while a small amount of external oil remained. As evidenced by the changes of the crystalline characteristics with the help of X-ray diffraction (XRD), the interaction between starch and lipids on the surface was confirmed to form V-type complex compounds during frying at high moisture. Copyright © 2017 Elsevier Ltd. All rights reserved.

Non-convergent ordering and displacive phase transition in pigeonite: in situ HT XRD study

NASA Astrophysics Data System (ADS)

Cámara, F.; Carpenter, M. A.; Domeneghetti, M. C.; Tazzoli, V.

A natural Ca-rich pigeonite (En47Fs43Wo10), free of augite exsolution products, was studied by in situ high-temperature single-crystal X-ray diffraction. The sample, monoclinic P21/c (a=9.719(7) Å, b=8.947(9) Å, c=5.251(3) Å, β=108.49(5), V=433.0(6) Å3), was annealed up to 1000 °C to induce a phase transition from P21/c to C2/c symmetry. Complete single-crystal X-ray diffraction data collections were carried out in situ at 650, 750, 850 and 950 °C after the crystal had reached equilibrium for the Fe-Mg intracrystalline exchange reaction at each temperature. The variation, with increasing temperature, of lattice parameters, of intensity of hkl reflections with h + k=2n + 1 (which vanish at high temperature) and of some geometrical parameters from structure refinement, showed that the displacive phase transition P21/cC2/c was continuous in character. This contrasts with the first-order character for the HT phase transition in pigeonite containing significantly less calcium.

Identification of the silver state in the framework of Ag-containing zeolite by XRD, FTIR, photoluminescence, 109Ag NMR, EPR, DR UV-vis, TEM and XPS investigations.

PubMed

Popovych, Nataliia; Kyriienko, Pavlo; Soloviev, Sergiy; Baran, Rafal; Millot, Yannick; Dzwigaj, Stanislaw

2016-10-26

Silver has been identified in the framework of Ag x SiBEA zeolites (where x = 3-6 Ag wt%) by the combined use of XRD, 109 Ag MAS NMR, FTIR, diffuse reflectance UV-visible, EPR and XPS spectroscopy. The incorporation of Ag ions into the framework of SiBEA zeolite has been evidenced by XRD. The consumption of OH groups as a result of their reaction with the silver precursor has been monitored by FTIR and photoluminescence spectroscopy. The changes in the silver state as a function of Ag content and thermal and hydrogen treatment at 573 K have been identified by 109 Ag MAS NMR, EPR, DR UV-visible, TEM and XPS investigations. The acidity of AgSiBEA has been investigated by FTIR spectroscopy of adsorbed CO and pyridine used as probe molecules.

XRD, TEM, IR, Raman and NMR Spectroscopy of In Situ Crystallization of Lithium Disilicate Glass

NASA Technical Reports Server (NTRS)

Fuss, T.; Mogus-Milankovic, A.; Ray, C. S.; Lesher, C. E.; Youngman, R.; Day, D. E.

2006-01-01

The structure of a Li2O-2SiO2 (LS2) glass was investigated as a function of pressure and temperature up to 6 GPa and 750 C respectively, using XRD, TEM, IR, Raman and NMR spectroscopy. Glass densified at 6 GPa has an average Si-O-Si bond angle approx.7deg lower than that found in glass processed at 4.5 GPa. At 4.5 GPa, lithium disilicate crystallizes from the glass, while at 6 GPa a new high pressure form of lithium metasilicate crystallizes. The new phase, while having lithium metasilicate crystal symmetry, contains at least 4 different Si sites. NMR results for 6 GPa sample indicate the presence of Q4 species with (Q(sup 4))Si-O-Si(Q(sup 4)) bond angles of approx.157deg. This is the first reported occurrence of Q(sup 4) species with such large bond angles in alumina free alkali silicate glass. No five- or six- coordinated Si are found.

Analysis of quantitative data obtained from toxicity studies showing non-normal distribution.

PubMed

Kobayashi, Katsumi

2005-05-01

The data obtained from toxicity studies are examined for homogeneity of variance, but, usually, they are not examined for normal distribution. In this study I examined the measured items of a carcinogenicity/chronic toxicity study with rats for both homogeneity of variance and normal distribution. It was observed that a lot of hematology and biochemistry items showed non-normal distribution. For testing normal distribution of the data obtained from toxicity studies, the data of the concurrent control group may be examined, and for the data that show a non-normal distribution, non-parametric tests with robustness may be applied.

Synthesis, structural and vibrational investigation on 2-phenyl-N-(pyrazin-2-yl)acetamide combining XRD diffraction, FT-IR and NMR spectroscopies with DFT calculations.

PubMed

Lukose, Jilu; Yohannan Panicker, C; Nayak, Prakash S; Narayana, B; Sarojini, B K; Van Alsenoy, C; Al-Saadi, Abdulaziz A

2015-01-25

The optimized molecular structure, vibrational frequencies, corresponding vibrational assignments of 2-phenyl-N-(pyrazin-2-yl)acetamide have been investigated experimentally and theoretically using Gaussian09 software package. The title compound was optimized by using the HF/6-31G(6D,7F) and B3LYP/6-31G(6D,7F) calculations. The geometrical parameters are in agreement with the XRD data. The stability of the molecule arising from hyper-conjugative interaction and charge delocalization has been analyzed using NBO analysis. Gauge-including atomic orbital (1)H-NMR chemical shifts calculations were carried out and compared with experimental data. The HOMO and LUMO analysis is used to determine the charge transfer within the molecule. Molecular electrostatic potential was performed by the DFT method. First hyperpolarizability is calculated in order to find its role in non linear optics. From the XRD data, in the crystal, molecules are held together by strong C-H⋯O and N-H⋯O intermolecular interactions. Copyright © 2014 Elsevier B.V. All rights reserved.

DSC and Raman studies of silver borotellurite glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kaur, Amandeep; Khanna, Atul, E-mail: atul.phy@gndu.ac.in; Gonzàlez, Fernando

2016-05-23

Silver borotellurite glasses of composition: xAg{sub 2}O-yB{sub 2}O{sub 3}-(100-x-y)TeO{sub 2} (x=20-mol%, y = 0, 10, 20 and 30-mol%) were prepared and characterized by density, X-ray diffraction (XRD), differential scanning calorimetry, and Raman spectroscopy. XRD confirmed the amorphous structure of all samples. Density of glasses decreases while the glass transition temperature increases with increase in B{sub 2}O{sub 3} content from 10 to 30-mol%. Raman study shows that coordination number of Te with oxygen decreases steadily from 3.42 to 3.18 on adding B{sub 2}O{sub 3} due to the transformation of TeO{sub 4} into TeO{sub 3} units.

Studies on thermal reactions and sintering behaviour of red clays by irreversible dilatometry

NASA Astrophysics Data System (ADS)

Anil, Asha; Misra, S. N.; Misra, N. M.

2018-05-01

Thermal behavior of clays strongly influences that of ceramic bodies made thereof and hence, its study is must for assessing its utility in ceramic products as well as to set the body composition. Irreversible dilatometry is an effective thermal analysis tool for evaluating thermal reactions as well as sintering behavior of clays or clay based ceramic bodies. In this study, irreversible dilatometry of four red clay samples (S, M, R and G) of Gujarat region, which vary in their chemical and mineralogical compositions was carried out using a Dilatometer and compared. Chemical analysis and XRD of red clays were carried out. XRD showed that major clay minerals in S, M and R clays are kaolinite. However, clay marked R and G showed presence of both kaolinite and illite and /muscovite. Presence of non-clay minerals such as hematite, quartz, anatase were also observed in all clays. XRD results were in agreement with chemical analyses results. Rational analyses showed variation in amount of clay and non-clay minerals in red clay samples. Evaluation of dilatometric curves showed that clay marked as S, M and R exhibit patterns typical for kaolinitic clays. Variation in linear expansion (up to 550°C) and shrinkage (above 550°C) between these three clays was found to be related to difference in amount of quartz and kaolinite respectively. However, dilatometric curve of G exhibit a pattern similar to that for an illitic clay. This study confirmed that sintering of investigated kaolinitic and illitic and / muscovitic red clays initiates at above 1060°C and 860°C respectively and this behaviour strongly depends upon type and amount of minerals and their chemical compositions.

Surface morphology and electrochemical studies on polyaniline/CuO nano composites

NASA Astrophysics Data System (ADS)

Ashokkumar, S. P.; Vijeth, H.; Yesappa, L.; Niranjana, M.; Vandana, M.; Basappa, M.; Devendrappa, H.

2018-05-01

An electrochemically synthesized Polyaniline (PANI) and Polyaniline/copper oxide (PCN) nano composite have studied the morphology and electrochemical properties. The composite is characterized by X-ray diffraction (XRD) and surface morphology was studied using FESEM and electrochemical behavior is studied using cyclic voltammetry (CV) technique. The CV curves shows rectangular shaped curve and they have contribution to electrical double layer capacitance (EDCL).

X-ray diffraction study of the mineralogy of microinclusions in fibrous diamond

NASA Astrophysics Data System (ADS)

Smith, Evan; Kopylova, Maya; Dubrovinksy, Leonid

2010-05-01

Fibrous diamond, occurring both as cuboids and as coatings over non-fibrous diamond nuclei, is translucent due to the presence of millions of sub-micron-sized mineral and fluid inclusions. Diamond is strong and relatively inert, making it an excellent vessel to preserve trapped materials. These microinclusions represent direct samples of natural diamond-forming mantle fluids, and are critical for our understanding of diamond genesis. Traditionally, infrared spectroscopy, Raman spectroscopy, secondary ion mass spectrometry, electron microprobe, and FIB-TEM techniques have proven to be effective for the study of microinclusions in diamond. The abundance and random orientation of included minerals in fibrous diamond make them amenable to a powder-type X-ray diffraction (XRD) technique. This technique provides an accurate way to identify included minerals. It also has the advantage of analyzing thousands of inclusions simultaneously, rather than analyzing one inclusion at a time, as with common FIB-TEM techniques. XRD provides a bulk analysis, giving a superior measure of relative abundances of included minerals, as well as potentially accounting for small quantities of minerals that might otherwise be overlooked. We studied fibrous cuboid diamonds with microinclusions from the Democratic Republic of Congo (DRC) (23 samples), Brazil (4 samples), Jericho (1 sample), and Wawa conglomerates (9 samples). XRD analysis was performed at the Bayerisches Geoinstitut (BGI), University of Bayreuth, Germany. The unique XRD setup consists of a RIGAKU FR-D high-brilliance source, OSMIC Inc. Confocal Max-Flux optics, and a SMART APEX 4K CCD area detector. Preliminary XRD studies of microinclusions 8 fibrous diamonds from the DRC showed a prevalence of silicates with structural and coordinated H2O. Sheet silicates constituted 9 out of 13 detected minerals, with phlogopite-biotite micas being present in 4 out of 8 samples. Other detected minerals were 2 chlorite minerals, 2 clay

Weathering and hydrothermal alteration of basalts in Iceland: mineralogy from VNIR, TIR, XRD, and implications for Mars

NASA Astrophysics Data System (ADS)

Ehlmann, B. L.; Mustard, J. F.; Bish, D. L.

2009-12-01

Recent orbital investigations have revealed that aqueous alteration on early Mars took place in diverse alteration environments indicated by distinctive assemblages of minerals (Murchie et al., 2009, JGR). There is growing evidence for past diagenetic or low-temperature/pressure hydrothermal activity on Mars at neutral to alkaline pH, indicated by the presence of Fe/Mg smectites, chlorite, prehnite, serpentine, opaline silica, and zeolites such as analcime in Noachian terrains (Ehlmann et al., 2009, JGR). In recent investigations of terrestrial Mars analog sites, neutral to alkaline pH alteration of basalt, both pedogenic and hydrothermal, has been understudied in favor of sulfur-rich, acidic systems including those at the Hawaiian volcanoes and Rio Tinto, Spain. We began study of the alteration of basalt lava flows in Iceland as a geochemical analog for Noachian Mars. Because the basaltic bedrock is recently formed (<16Ma) with few localities of more highly evolved composition and has poorly formed soils and spare vegetation, the ground and surface waters are broadly similar to those which might have existed on Noachian Mars. Iceland has a variety of geothermal spring systems--low T, low S; low T, high S; and high T, high S--each of which creates distinctive mineralogic assemblages. Here we examine rocks of the Hvalfjordur peninsula, collected from basalt flows that were in some places altered at the surface by pedogenesis and in other locations were hydrothermally altered by non-sulfurous groundwater circulation (low T, low S) following the emplacement of a later hot basalt flow. Rock samples were surveyed in the field using a portable VNIR spectrometer. Altered and unaltered rocks that were typical for the locality were collected as were altered rocks whose spectra were most similar to those measured by CRISM from Mars orbit. Ten rocks were ultimately selected for detailed laboratory analyses: zeolitized basaltic rocks bearing minerals including analcime and

Electrochemical lithiation/delithiation of SnP₂O₇ observed by in situ XRD and ex situ⁷Li/³¹P NMR, and ¹¹⁹Sn Mössbauer spectroscopy.

PubMed

Bezza, Ilham; Kaus, Maximilian; Riekehr, Lars; Pfaffmann, Lukas; Doyle, Stephen; Indris, Sylvio; Ehrenberg, Helmut; Solhy, Abderrahim; Saadoune, Ismael

2016-04-21

SnP2O7 was prepared by a sol-gel route. The structural changes of tin pyrophosphate during the electrochemical lithiation were followed by using in situ XRD measurements that reveal the existence of a crystalline phase at the beginning of the discharge process. Nevertheless, it becomes amorphous after the full discharge as a result of a conversion reaction leading to the formation of LixSny alloys. The electrochemical tests show a high capacity with high retention upon cycling. To better understand the reaction mechanism of SnP2O7 with Li, several techniques were applied, such as ex situ(119)Sn Mössbauer and ex situ(7)Li and (31)P NMR spectroscopies with which we can follow the changes in the local environment of each element during cycling.

Fe K-Edge X-ray absorption near-edge spectroscopy (XANES) and X-ray diffraction (XRD) analyses of LiFePO4 and its base materials

NASA Astrophysics Data System (ADS)

Latif, C.; Negara, V. S. I.; Wongtepa, W.; Thamatkeng, P.; Zainuri, M.; Pratapa, S.

2018-03-01

XANES analysis has been performed with the aim of knowing the Fe oxidation state in a synthesized LiFePO4 and its base materials. XANES measurements were performed at SLRI on energy around Fe K-edge. An XRD analysis has also been performed with the aim of knowing the phase composition, lattice parameters and crystallite size of the LiFePO4 as well as the base materials. From the XRD analysis, it was found that the dominating phase in the iron sand sample was Fe3O4 and the only phase found after calcination was LiFePO4. The latter phase exhibited crystallite size of 100 nm and lattice parameters a = 10.169916 Å, b = 5.919674 Å, c = 4.627893 Å. Qualitative analysis of XANES data revealed that the oxidation number of Fe in the sample before calcination was greater than that after calcination and Fe in the natural iron sand, indicated by the E0 values of 7129.2 eV, 7120.6 eV and 7124.4 eV respectively.

X-radiography, XRD and Ultrasonic Data Transfer Function Technique - Simultaneous Measurements Under Simulated Mantle Conditions in a Multi-Anvil Device

NASA Astrophysics Data System (ADS)

Mueller, H. J.; Schilling, F. R.; Lathe, C.

2004-05-01

The interpretation of seismic data from the Earth's deep interior requires measurements of the physical properties of Earth materials under experimental simulated mantle conditions. Elastic wave velocity measurement is an important tool for the determination of the elastic properties. Ultrasonic interferometry allows the highly precise travel time measurement at a sample enclosed in a high-pressure multi-anvil device. But the calculation of wave velocities requires the exact sample length under in situ conditions. There are two options - scanning the interfaces of the sample by XRD (Mueller et al., 2003) and X-radiography (Li et al., 2001). The multi-anvil apparatus MAX80 is equipped for both methods. Only the X-radiography is fast enough for transient measurements. Contrary to XRD measurements, imaging the sample by X-rays requires a beam diameter larger than the sample length. Therefore the fixed primary slits of Max80 were exchanged by 4-blade high precision slits of Advanced Design Consulting, Inc. A Ce-YAG-crystal converts the X-ray image to an optical one, redirected by a mirror and captured by a CCD-camera. To derive the sample length, the different brightness of sample, buffer rod and reflector at the electronic image is evaluated. Classical ultrasonic interferometry is very time consuming, because the ultrasonic waves of the frequency range under study are generated and detected one after another with a given step rate. A 60 MHz frequency sweep with 100 kHz steps lasts for more than 30 minutes. This is a serious limitation for all transient measurements, but also limits the data collection at elevated temperatures to prevent the pressure transmitting boron epoxy cubes and the anvils from overheating. The ultrasonic transfer function technique (UTF), first described by Li et al. (2002), generates all the frequencies simultaneously. Related to the results and experiences of Li the UTF-technique was developed independently at GFZ. This version allows to

Preparation, characterization and conductivity study of nitro-mercurated styrene butadiene rubber/silver doped zinc oxide nanocomposites

NASA Astrophysics Data System (ADS)

Anilkumar, T.; Naik, Adarsh Ajith; Ramesan, M. T.

2017-06-01

Here we report the preparation of nitromercurated styrene butadiene rubber (NMSBR)/silver doped zinc oxide nanocomposite by inexpensive and ecofriendly two roll mill mixing. The composites were characterized by UV, FTIR, XRD, SEM, TGA and conductivity measurements. UV and FTIR spectrum indicated the interfacial interaction between the polymer and nanoparticles.XRD and SEM images showed the uniform arrangement of nanoparticles within the macromolecular chain. TGA study indicated the better thermal resistance of the composite. The dielectric properties and AC conductivity ofnanocomposites were much greater than nitromercurated SBR and they may be used as multifunctional materials for nanoelectronic devices.

Pharmacologically significant complexes of Mn(II), Co(II), Ni(II), Cu(II) and Zn(II) of novel Schiff base ligand, (E)-N-(furan-2-yl methylene) quinolin-8-amine: Synthesis, spectral, XRD, SEM, antimicrobial, antioxidant and in vitro cytotoxic studies

NASA Astrophysics Data System (ADS)

Shakir, M.; Hanif, Summaiya; Sherwani, Mohd. Asif; Mohammad, Owais; Al-Resayes, Saud I.

2015-07-01

A novel series of metal complexes of the types, [ML2(H2O)2]Cl2 and [ML2]Cl2 [M = Mn(II), 1; Co(II), 2; Ni(II), 3; Cu(II), 4; and Zn(II), 5] were synthesized by the interaction of ligand, L (E)-N-(furan-2-yl methylene) quinolin-8-amine, derived from the condensation of 2-furaldehyde and 8-aminoquinoline. The synthesized ligand and its metal complexes were characterized on the basis of results obtained from elemental analysis, ESI-MS, XRD, SEM, TGA/DTA, FT-IR, UV-Vis, magnetic moment and 1H and 13C NMR spectroscopic studies. EPR parameters were recorded in case of complex 4. The comparative in-vitro antimicrobial activities against various pathogens with reference to known antibiotics and antioxidant activity against standard control at variable concentrations revealed that the metal complexes show enhanced antimicrobial and free radical scavenging activities in general as compared to free ligand. However, the complexes 1 and 5 have shown best antioxidant activity among all the metal complexes. Furthermore, comparative in-vitro antiproliferative activity on ligand and its metal chelates performed on MDA-MB-231 (breast carcinoma), KCL22 (blood lymphoid carcinoma), HeLa (cervical carcinoma) cell lines and normal cells (PBMC) revealed that metal chelates show moderate to good activity as compared to ligand where as complex 1 seems to be the most promising one possessing a broad spectrum of activity against all the selected cancer cell lines with IC50 < 2.10 μM.

Synthesis and structural studies of Mg doped LiNi0.5Mn0.5O2 cathode materials for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Murali, N.; Margarette, S. J.; Madhuri Sailaja, J.; Kondala Rao, V.; Himakar, P.; Kishore Babu, B.; Veeraiah, V.

2018-02-01

Layered Mg doped LiNi0.5Mn0.5O2 materials have been synthesized by sol-gel method. The physical properties of these materials were examined by XRD, FESEM and FT-IR studies. From XRD patterns, the phase formation of α-NaFeO2 layered structure with R\\bar 3m space group is confirmed. The surface morphology of the synthesized materials has been examined by FESEM analysis in which the average particle size is found to be about 2 - 2.5 µm. These materials show some changes in the local ion environment, as examined by FT-IR studies.

XRD analysis of undoped and Fe doped TiO{sub 2} nanoparticles by Williamson Hall method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bharti, Bandna; Barman, P. B.; Kumar, Rajesh, E-mail: rajesh.kumar@juit.ac.in

2015-08-28

Undoped and Fe doped titanium dioxide (TiO{sub 2}) nanoparticles were synthesized by sol-gel method at room temperature. The synthesized samples were annealed at 500°C. For structural analysis, the prepared samples were characterized by X-ray diffraction (XRD). The crystallite size of TiO{sub 2} and Fe doped TiO{sub 2} nanoparticles were calculated by Scherer’s formula, and was found to be 15 nm and 11 nm, respectively. Reduction in crystallite size of TiO{sub 2} with Fe doping was observed. The anatase phase of Fe-doped TiO{sub 2} nanoparticles was also confirmed by X-ray diffraction. By using Williamson-Hall method, lattice strain and crystallite size weremore » also calculated. Williamson–Hall plot indicates the presence of compressive strain for TiO{sub 2} and tensile strain for Fe-TiO{sub 2} nanoparticles annealed at 500°C.« less

Preparation of biocompatible magnetite-carboxymethyl cellulose nanocomposite: characterization of nanocomposite by FTIR, XRD, FESEM and TEM.

PubMed

Habibi, Neda

2014-10-15

The preparation and characterization of magnetite-carboxymethyl cellulose nano-composite (M-CMC) material is described. Magnetite nano-particles were synthesized by a modified co-precipitation method using ferrous chloride tetrahydrate and ferric chloride hexahydrate in ammonium hydroxide solution. The M-CMC nano-composite particles were synthesized by embedding the magnetite nanoparticles inside carboxymethyl cellulose (CMC) using a freshly prepared mixture of Fe3O4 with CMC precursor. Morphology, particle size, and structural properties of magnetite-carboxymethyl cellulose nano-composite was accomplished using X-ray powder diffraction (XRD), transmission electron microscopy (TEM), Fourier transformed infrared (FTIR) and field emission scanning electron microscopy (FESEM) analysis. As a result, magnetite nano-particles with an average size of 35nm were obtained. The biocompatible Fe3O4-carboxymethyl cellulose nano-composite particles obtained from the natural CMC polymers have a potential range of application in biomedical field. Copyright © 2014 Elsevier B.V. All rights reserved.

Structural, XPS and magnetic studies of pulsed laser deposited Fe doped Eu{sub 2}O{sub 3} thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Sandeep; Prakash, Ram, E-mail: rpgiuc@gmail.com; Choudhary, R.J.

2015-10-15

Highlights: • Growth of Fe doped Eu{sub 2}O{sub 3} thin films by PLD. • XRD and Raman’s spectroscopy used for structure confirmation. • The electronic states of Eu and Fe are confirmed by XPS. • Magnetic properties reveals room temperature magnetic ordering in deposited film. - Abstract: Fe (4 at.%) doped europium (III) oxide thin film was deposited on silicon (1 0 0) substrate by pulsed laser deposition technique. Structural, spectral and magnetic properties were studied by X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS) and magnetization measurements. XRD and Raman spectroscopy reveal that the grown film is singlemore » phased and belongs to the cubic structure of Eu{sub 2}O{sub 3}. XPS study of the Eu{sub 1.92}Fe{sub 0.08}O{sub 3} film shows that Fe exists in Fe{sup 3+} ionic state in the film. The film exhibits magnetic ordering at room temperature.« less

Preparation and study of (1 - x)CuFe2O4-xBaTiO3 (x = 0, 0.1 and 1) composite multiferroics

NASA Astrophysics Data System (ADS)

Murtaza, Tahir; Ali, Javid; Khan, M. S.

2018-07-01

The parent and mixed spinel-perovskite composite of (1 - x)CuFe2O4-xBaTiO3 (x = 0, 0.1 and 1) has been prepared by solid-state reaction method and studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), Mössbauer spectroscopy, magnetometry and P-E lope tracer. The XRD results showed the formation of single phase tetragonal spinel CuFe2O4 and tetragonal perovskite BaTiO3 at room temperature, further XRD of composite 0.1CuFe2O4-0.9BaTiO3 reflects the two crystallographic phases with 1:9 ratio. The SEM micrographs show the homogeneous and uniform formation of the samples. Through EDAX analysis, the chemical composition of the sample is found to be same as the nominal composition. The high field Mossbauer data of CuFe2O4 sample shows the ferrimagnetic ordering in the sample. The observed M-H and P-E loops of the composite 0.1CuFe2O4-0.9BaTiO3 sample show the presence of spontaneous magnetization and spontaneous electric polarization indicating the multiferroic nature of the sample.

Interaction of atomic oxygen with thin film and bulk copper: An XPS, AES, XRD, and profilometer study

NASA Technical Reports Server (NTRS)

Raikar, Genesh N.; Gregory, John C.; Christl, Ligia C.; Peters, Palmer N.

1992-01-01

The University of Alabama in Huntsville (UAH) experiment A-0114 was designed primarily to study degradation of material surfaces due to low earth orbital (LEO) atmospheric oxygen. The experiment contained 128 one inch circular samples: metals, polymers, carbons, and semiconductors. Among metal samples, copper has shown some interesting new results. Two types of copper samples, a film sputter coated on fused silica and a bulk piece of OFHC copper, were characterized employing a variety of techniques such as X-ray and Auger electron spectroscopies, X-ray diffraction, and high resolution profilometry. Cu 2p core level spectra were used to characterize the presence of Cu2O and CuO in addition to Cu Auger LMM lines. These results are supported by our recent X-ray diffraction studies which clearly establish the presence of Cu oxides which we were unable to prove in our earlier work. Profilometry showed an increase in thickness of the film sample where exposed to 106.7 +/- 0.5 nm from an initial thickness of 74.2 +/- 1.1 nm. Further studies with SEM and ellipsometry are underway.

The new insight into the structure-activity relation of Pd/CeO2-ZrO2-Nd2O3 catalysts by Raman, in situ DRIFTS and XRD Rietveld analysis.

PubMed

Yang, X; Yang, L; Lin, J; Zhou, R

2016-01-28

Pd/CeO2-ZrO2-Nd2O3 (CZN) catalysts with different CeO2/ZrO2 molar ratios were synthesized and have been characterized by multiple techniques, e.g. XRD in combination with Rietveld refinement, UV-Raman, XPS and in situ DRIFTS. The XRD pattern of CZN with CeO2/ZrO2 molar ratios ≥1/2 can be indexed satisfactorily to the fluorite structure with a space group Fm3̄m, while the XRD patterns of CZ12 only display diffraction peaks of the tetragonal phase (S.G. P42/nmc). Nd addition can effectively stabilize the cubic structure of the CZN support and increase the enrichment of defect sites on the surface, which may be related to the better catalytic activity of Pd/CZN12 catalysts compared with Pd/CZ12. The presence of moderate ZrO2 can increase the concentration of O* active species, leading to accelerate the formation of nitrate species and thus enhance the catalytic activity of NOx and HC elimination. The Pd-dispersion decreases with the increasing Zr content, leading to the decreased CO catalytic activity, especially for the aged catalysts. The change regularity of the OSC value is almost the same with the in situ dynamic operational window, demonstrating that the in situ dynamic operational window is basically affected by the OSC value.

XRD Analysis of Cement Paste Samples Exposed to the Simulated Environment of a Deep Repository - 12239

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ferreira, Eduardo G.A.; Marumo, Julio T.; Vicente, Roberto

2012-07-01

Portland cement materials are widely used as engineered barriers in repositories for radioactive waste. The capacity of such barriers to avoid the disposed of radionuclides to entering the biosphere in the long-term depends on the service life of those materials. Thus, the performance assessment of structural materials under a series of environmental conditions prevailing at the environs of repositories is a matter of interest. The durability of cement paste foreseen as backfill in a deep borehole for disposal of disused sealed radioactive sources is investigated in the development of the repository concept. Results are intended to be part of themore » body of evidence in the safety case of the proposed disposal technology. This paper presents the results of X-Ray Diffraction (XRD) Analysis of cement paste exposed to varying temperatures and simulated groundwater after samples received the radiation dose that the cement paste will accumulate until complete decay of the radioactive sources. The XRD analysis of cement paste samples realized in this work allowed observing some differences in the results of cement paste specimens that were submitted to different treatments. The cluster analysis of results was able to group tested samples according to the applied treatments. Mineralogical differences, however, are tenuous and, apart from ettringite, are hardly observed. The absence of ettringite in all the seven specimens that were kept in dry storage at high temperature had hardly occurred by natural variations in the composition of hydrated cement paste because ettringite is observed in all tested except the seven specimens. Therefore this absence is certainly the result of the treatments and could be explained by the decomposition of ettringite. Although the temperature of decomposition is about 110-120 deg. C, it may be initially decomposed to meta-ettringite, an amorphous compound, above 50 deg. C in the absence of water. Influence of irradiation on the

Preparation, characterization, dielectric properties and diffusion studies of styrene butadiene rubber (SBR)/manganous tungstate (MnWO4) nanocomposites

NASA Astrophysics Data System (ADS)

Jasna, V. C.; Ramesan, M. T.

2017-06-01

Nanocomposites based on SBR with different content of manganous tungstate nanoparticles were prepared and characterized by FTIR, UV-visible spectroscopy, XRD, SEM, TGA, DSC and impedance analysis. The interaction between nanoparticles and the elastomer was clear from the shift in peaks of UV and FTIR. XRD and SEM analysis showed the uniform arrangement of nanoparticles in SBR matrix. Glass transition temperature, thermal stability and dielectric properties of composites were enhanced by the addition of nanoparticles. Sorption studies of nanocomposites were done in aromatic solvents at different temperature. Sorption data obtained were used to estimate the thermodynamic properties.

Structural and morphological study of chemically synthesized CdSe thin films

NASA Astrophysics Data System (ADS)

Agrawal, P.; Singh, Randhir; Sharma, Jeewan; Sachdeva, M.; Singh, Anupinder; Bhargava, A.

2018-05-01

Nanocrystalline CdSe thin films were prepared by Chemical Bath Deposition (CBD) method using potassium nitrilo-triacetic acid cadmium complex and sodium selenosulphite. The as deposited films were red in color, uniform and well adherent to the glass substrate. These films were strongly dependent on the deposition parameters such as bath composition, deposition temperature and time. Films were annealed at 350 °C for four hours. The morphological, structural and optical properties were studied using X-ray diffraction (XRD), UV-VIS spectrophotometer measurements, scanning electron microscopy and atomic force microscopy. The XRD analysis confirmed that films are predominantly in hexagonal phase. Scanning electron micrograph shows that the grains are uniformly spread all over the film and each grain contains many nanocrystals with spherical shapes.

Probing Titanium Disulfide-Sulfur Composite Materials for Li-S Batteries via In Situ X-ray Diffraction (XRD)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Q.; Bock, D.; Takeuchi, K. J.

Development of Li-S batteries is hindered by sluggish kinetics resulting from the intrinsic poor conductivity of sulfur and capacity degradation due to solubility of intermediate lithium polysulfides (LiPS). A strategy for overcoming these issues is to use TiS 2, which is a good electrical conductor and LiPS absorbant, as an additive to sulfur electrodes. Furthemore, from a structural perspective, we probed TiS 2-S composite materials during electrochemical discharge and charge reactions in propylene-oxide based glyme (DPGDME) electrolyte using in-situ XRD, revealing the synergistic effects of TiS 2 and S in the composites. TiS 2 was found to function effectively asmore » a conductive additive and improve the utilization of sulfur. Intercalation of Li + into TiS 2 takes place simultaneously with the sulfur-lithium reaction, and contributes favorably to the total realized capacity.« less

Probing Titanium Disulfide-Sulfur Composite Materials for Li-S Batteries via In Situ X-ray Diffraction (XRD)

DOE PAGES

Zhang, Q.; Bock, D.; Takeuchi, K. J.; ...

2017-03-01

Development of Li-S batteries is hindered by sluggish kinetics resulting from the intrinsic poor conductivity of sulfur and capacity degradation due to solubility of intermediate lithium polysulfides (LiPS). A strategy for overcoming these issues is to use TiS 2, which is a good electrical conductor and LiPS absorbant, as an additive to sulfur electrodes. Furthemore, from a structural perspective, we probed TiS 2-S composite materials during electrochemical discharge and charge reactions in propylene-oxide based glyme (DPGDME) electrolyte using in-situ XRD, revealing the synergistic effects of TiS 2 and S in the composites. TiS 2 was found to function effectively asmore » a conductive additive and improve the utilization of sulfur. Intercalation of Li + into TiS 2 takes place simultaneously with the sulfur-lithium reaction, and contributes favorably to the total realized capacity.« less

Structural studies of zirconium doped Ba{sub 0.70}Sr{sub 0.30}TiO{sub 3} lead free ferroelectric thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sharma, Sarita, E-mail: sss.sharmasarita@gmail.com; Ram, Mast; Thakur, Shilpa

2016-05-06

Ba{sub 0.7}Sr{sub 0.3}(Zr{sub x}Ti{sub 1-x})O{sub 3}(BSZT, x=0,0.05,0.10,0.15,0.20) thin films were prepared by using sol gel method. Structural and microstructural properties were studied by using XRD, Raman Spectroscopy and atomic force microscopy (AFM) respectively. XRD and Raman Spectroscopy show the presence of tetragonal phase in multilayer BSZT thin film. The experimental results demonstrate that structural and microstructural properties of BSZT thin film were significantly dependent on variation of Zr content.

In situ characterization of uranium and americium oxide solid solution formation for CRMP process: first combination of in situ XRD and XANES measurements.

PubMed

Caisso, Marie; Picart, Sébastien; Belin, Renaud C; Lebreton, Florent; Martin, Philippe M; Dardenne, Kathy; Rothe, Jörg; Neuville, Daniel R; Delahaye, Thibaud; Ayral, André

2015-04-14

Transmutation of americium in heterogeneous mode through the use of U1-xAmxO2±δ ceramic pellets, also known as Americium Bearing Blankets (AmBB), has become a major research axis. Nevertheless, in order to consider future large-scale deployment, the processes involved in AmBB fabrication have to minimize fine particle dissemination, due to the presence of americium, which considerably increases the risk of contamination. New synthesis routes avoiding the use of pulverulent precursors are thus currently under development, such as the Calcined Resin Microsphere Pelletization (CRMP) process. It is based on the use of weak-acid resin (WAR) microspheres as precursors, loaded with actinide cations. After two specific calcinations under controlled atmospheres, resin microspheres are converted into oxide microspheres composed of a monophasic U1-xAmxO2±δ phase. Understanding the different mechanisms during thermal conversion, that lead to the release of organic matter and the formation of a solid solution, appear essential. By combining in situ techniques such as XRD and XAS, it has become possible to identify the key temperatures for oxide formation, and the corresponding oxidation states taken by uranium and americium during mineralization. This paper thus presents the first results on the mineralization of (U,Am) loaded resin microspheres into a solid solution, through in situ XAS analysis correlated with HT-XRD.

Surfactant-free bio-synthesised Tio2 nanorods from Turbinaria conoides-a study on photocatalytic and anti-bacterial activity

NASA Astrophysics Data System (ADS)

Subhapriya, S.; Gomathipriya, P.

2018-06-01

In this study, Titania nanorods were synthesised from aqueous extract of Turbinaria conoides (brown seaweeds) (TiO2NRs-TC) under surfactant free medium. The photocatalytic activity of the synthesised nanorods was tested towards the photocatalytic decolourization using simulated dye wastewater containing Navy Blue HER (NBHER). The synthesised Titania nanorods were characterized by using x-ray diffraction (XRD), UV–visible spectroscopy (UV–vis), Scanning Electron Microscopy (SEM), Energy Dispersive Spectrophotometer (EDS) and Transmission Electron Microscopy (TEM). XRD pattern confirms the anatase phase formation and HR-SEM micrograph shows the presence of rod like structure with the size of about 50 nm. TEM analysis proves the rod like structure with a size of 45–50 nm which was in agreement with the XRD analysis and HR-SEM images. EDS and XDS confirmed the formation of Titania nanoparticles. The formation of TiO2NRs-TC has a beneficial influence on the dye Navy blue HER photodegradation. TiO2-TC nano rods also show superior photocatalytic ability in hydrogen generation (2.1 mmol/h‑1g‑1). The antibacterial activity of the synthesised nanoparticles was examined using disc diffusion method which showed diverse susceptibility of microorganisms to the Titania nanoparticles.

Morphology and thermal studies of zinc sulfide and cadmium sulfide nanoparticles in polyvinyl alcohol matrix

NASA Astrophysics Data System (ADS)

Osuntokun, Jejenija; Ajibade, Peter A.

2016-09-01

Zn(II) and Cd(II) metal complexes of 1-cyano-1-carboethoxyethylene-2,2-dithiolato-κS,S'-bis(N,N-dimethylthiourea-κS) have been synthesized and characterized with analytical and spectroscopic techniques. The complexes were thermolysed in hexadecylamine at 200 °C to prepare ZnS and CdS nanoparticles. The nanoparticles were characterized with scanning electron microscope (SEM), transmission electron microscope (TEM), and powder X-ray diffraction (p-XRD). TEM images showed spherically shaped nanoparticles, whose sizes are in the range 4.33-7.21 nm for ZnS and 4.95-7.7 nm CdS respectively and XRD confirmed cubic crystalline phases for the nanoparticles. The optical band gap energy evaluated from the absorption spectra are 2.88 eV (430 nm) and 2.81 eV (440 nm) for the ZnS and CdS nanoparticles respectively. The as-prepared metal sulfide nanoparticles were further incorporated into polyvinyl alcohol (PVA) to give ZnS/PVA and CdS/PVA composites. The polymer nanocomposites were studied to investigate their morphology and thermal properties relative to the pure PVA. XRD diffractions indicated that the crystalline phases of the nanoparticles and the sizes in PVA matrices remained unaltered. Infra-red spectra studies revealed interactions between the PVA and the metal sulfide nanoparticles and TGA studies show that the ZnS/PVA and CdS/PVA nanocomposites exhibit better thermal stability than the pure PVA.

Structural morphology study of Cd2+ induced Langmuir Blodgett multilayer films of arachidic acid

NASA Astrophysics Data System (ADS)

Roy, Dhrubojyoti; Das, Nayan Mani; Gupta, P. S.

2013-04-01

The organization and headgroup co-ordination of Cadmium Arachidate (CdAA) molecule in Langmuir-Blodgett (LB) multilayer films deposited on hydrophilic Glass (SiO2) and Silicon (100) substrate at normal subphase pH (6.8) are studied. X-ray diffraction (XRD) and X-ray reflectivity (XRR) study reveals ordered layer by layer organization with uniform packing of CdAA molecules, and with a small tilt angle of alkyl chain of CdAA molecule equal to 6.8° ± 1.75°. Electron density profiles (EDPs) shows that the coverage of films remains almost constant with increase in bilayer thickness which indicate very little presence of pinhole defects. AFM study for 25 ML shows that coverage of the film remain intact upto 22nd ML and then decreases sharply due to presence of pinhole defects. Fourier transform infrared spectroscopy (FTIR) study is also consistent with XRD and XRR study of ordered deposition of CdAA molecule. FTIR and X-ray photoelectron spectroscopy (XPS) study indicates the formation of unidentate bridging metal-carboxylate coordination type headgroups consistent with one cadmium metal ion between two carboxylate (COO) groups in each headgroup structure.

Study of Initial Stages of Ball-Milling of Cu Powder Using X-ray Diffraction

NASA Astrophysics Data System (ADS)

Gayathri, N.; Mukherjee, Paramita

2018-04-01

The initial stage of size refinement of Cu powder is studied using detailed X-ray diffraction (XRD) analysis to understand the mechanism of formation of nanomaterials during the ball-milling process. The study was restricted to samples obtained for milling time up to 240 min to understand the deformation mechanism at the early stages of ball milling. Various model based approaches for the analysis of the XRD were used to study the evolution of the microstructural parameters such as domain size and microstrain along the different crystallographic planes. It was seen that the domain size saturates at a low value along the (311) plane whereas the size along the (220) and (200) plane is still higher. The r.m.s microstrain showed a non-monotonic change along the different crystallographic directions up to the milling time of 240 min.

Simulation study of an X-ray diffraction system for breast tumor detection

NASA Astrophysics Data System (ADS)

Marticke, F.; Montémont, G.; Paulus, C.; Michel, O.; Mars, J. I.; Verger, L.

2017-09-01

X-ray diffraction (XRD) is a powerful technique used to determine the molecular structure of biological tissues. In breast tissues for example, the scattering signatures of dense fibroglandular tissue and carcinoma have been shown to be significantly different. In this study, XRD was used as a second control level when conventional mammography results were unclear, for instance because of overly high breast density. A system optimized for this issue, called multifocal XRD, was developed combining energy dispersive spectral information at different scattering angles. This system allows depth-imaging in one go but needs an x,y-direction scan to image the region conventional mammography identified as suspect. The scan-time for about 10 cm3 with an incident flux of about 4 . 8 ṡ 107 photons per second would be around 2 s. For this study, breast phantoms with and without cancerous nodule were simulated to assess the separation power of the method and to determine the radiation dose required to obtain nearly ideal separation. For tumors situated in the center of the breast, the required dose was only about 0.3 mGy, even for breasts with high density. The tumor position was shown to have a low impact on detectability provided it remained in a zone where the system was sufficiently sensitive. The influence of incident spectrum maximum energy was also studied. The required dose remained very low with any of the incident spectra tested. Finally, an image slice was reconstructed in the x-direction and showed that the system can detect the presence of a small tumor (4 mm). Hence, XRD is a very promising tool to reduce the number of unnecessary invasive breast biopsies.

Phosphorus Sorption Characteristics in Aluminum-based Water Treatment Residuals Reacted with Dairy Wastewater: 1. Isotherms, XRD, and SEM-EDS Analysis.

PubMed

Zohar, Iris; Massey, Michael S; Ippolito, James A; Litaor, M Iggy

2018-05-01

We examined P sorption characteristics in Al-based water treatment residuals (Al-WTR) generated from slightly alkaline surface water and in an organic residual composite (WW-Al/O-WTR), produced by using the Al-WTR to treat organic-rich and high P concentration dairy wastewater. Solids from both residuals were examined using scanning electron microscopy-energy dispersive spectroscopy (SEM-EDS) and X-ray diffraction (XRD), and exposed to P additions of 0 to 4000 mg L in a sorption experiment. The Al-WTR removed ∼97% of the added P, whereas WW-Al/O-WTR removed only 78% of the added P in the addition range of 0 to 100 mg P L. With P additions of ≥100 mg L, the removal rate declined to <38% by Al-WTR and to 16% by WW-Al/O-WTR, possibly implying a change in sorption mechanisms. Analysis by XRD indicated that the major mineral was calcite, with some silica and poorly crystalline Al hydroxides. Analysis by SEM-EDS, which used three-element overlay maps of the residual surfaces, indicated that P was sparsely sorbed on both calcic and Al (hydr)oxide surfaces, along with a few clusters, even at low P concentrations of the treated waters. Ternary clusters of P, Al, and Ca were more abundant on the WW-Al/O-WTR. Carbon distribution suggested that organic substances covered Al surfaces. Sorption of P onto WW-Al/O-WTR may be reversible due to relatively weak Ca-P and Al-P bonds induced by the slight alkaline nature and in the presence of organic moieties, enhancing the WW-Al/O-WTR potential to act as a P source, rather than a P sink, in agricultural applications. Copyright © by the American Society of Agronomy, Crop Science Society of America, and Soil Science Society of America, Inc.

Operando Synchrotron XRD Investigation of Silver Metal Formation upon Electrochemical Reduction of Silver Iron Pyrophosphate (Ag 7Fe 3(P 2O 7) 4)

DOE PAGES

Zhang, Yiman; Kirshenbaum, Kevin C.; Marschilok, Amy C.; ...

2017-05-11

The formation of conductive metallic silver upon electrochemical reduction and lithiation of Ag 7Fe 3(P 2O 7) 4 is investigated. Alternating current impedance spectroscopy measurements show a 34% decrease in charge transfer resistance upon one electron equivalent (ee) of reduction, which is coincident with the formation of a Ag metal conductive network evidenced by both ex situ and operando X-ray diffraction. Quantitative assessment of Ag metal formation derived from operando XRD shows that only Ag + ions are reduced during the first 3ee, followed by simultaneous reduction of Ag + and Fe 3+ reduction for the next 5ee (3ee tomore » 8ee), culminating in reduction of the remaining Ag +. Scanning electron microscopy images show smaller Ag metal crystallite size and shorter nearest neighbor distance between and among Ag particles with higher depth of discharge. A high rate intermittent pulsatile discharge test is conducted where the cell delivers 12 total pulses during full discharge to probe the effect of Ag metal formation on the Li/Ag 7Fe 3(P 2O 7) 4 cell electrochemistry. The Ohmic resistance is derived from the voltage drop of each pulse. The resistance is 65 Ω initially, reaches its minimum of 26 Ω at 4.5 ee discharge, and levels off at 35 Ω after 7.0 ee reduction. In conclusion, the initial Ag reduction is more significant for the conductive network formation indicated by the decrease of both R ct and Ohmic resistance, which facilitates the high power output of the cell.« less

Operando Synchrotron XRD Investigation of Silver Metal Formation upon Electrochemical Reduction of Silver Iron Pyrophosphate (Ag 7Fe 3(P 2O 7) 4)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Yiman; Kirshenbaum, Kevin C.; Marschilok, Amy C.

The formation of conductive metallic silver upon electrochemical reduction and lithiation of Ag 7Fe 3(P 2O 7) 4 is investigated. Alternating current impedance spectroscopy measurements show a 34% decrease in charge transfer resistance upon one electron equivalent (ee) of reduction, which is coincident with the formation of a Ag metal conductive network evidenced by both ex situ and operando X-ray diffraction. Quantitative assessment of Ag metal formation derived from operando XRD shows that only Ag + ions are reduced during the first 3ee, followed by simultaneous reduction of Ag + and Fe 3+ reduction for the next 5ee (3ee tomore » 8ee), culminating in reduction of the remaining Ag +. Scanning electron microscopy images show smaller Ag metal crystallite size and shorter nearest neighbor distance between and among Ag particles with higher depth of discharge. A high rate intermittent pulsatile discharge test is conducted where the cell delivers 12 total pulses during full discharge to probe the effect of Ag metal formation on the Li/Ag 7Fe 3(P 2O 7) 4 cell electrochemistry. The Ohmic resistance is derived from the voltage drop of each pulse. The resistance is 65 Ω initially, reaches its minimum of 26 Ω at 4.5 ee discharge, and levels off at 35 Ω after 7.0 ee reduction. In conclusion, the initial Ag reduction is more significant for the conductive network formation indicated by the decrease of both R ct and Ohmic resistance, which facilitates the high power output of the cell.« less

Synthesis of kaolinite-filled EPDM rubber composites by solution intercalation: structural characterization and studies on mechanical properties

NASA Astrophysics Data System (ADS)

Ginil Mon, S.; Jaya Vinse Ruban, Y.; Vetha Roy, D.

2011-09-01

In the large field of nanotechnology, polymer matrix-based nanocomposites have become a prominent area of current research and development. Exfoliated clay-based nanocomposites have dominated the polymer world with excellent characteristics. EPDM rubber composites have been synthesized by solution-intercalation using the easily available kaolinite as filler. The composite structure has been elucidated by X-ray diffraction (XRD), Fourier transform IR, and scanning electron microscope studies. The molecular level dispersion of clay layers has been verified by the disappearance of basal XRD peak of kaolinite in the EPDM/kaolinite composites. The mechanical properties showed significant improvement of EPDM/kaolinite composites with respect to neat EPDM.

Solid-state one-way photoisomerisation of Z,E,Z-1,6-(4,4'-diphenyl)hexa-1,3,5-triene dicarboxylate examined using higher-order derivative spectra and powder XRD patterns.

PubMed

Sonoda, Yoriko; Goto, Midori; Ichimura, Kunihiro

2018-03-14

Higher order derivative spectra were applied at first to one-way ZEZ-to-EEE photoisomerisation of dimethyl ester (ZEZ-DPH1) of the titled compound in a methylcyclohexane solution. Many common crossing points emerged in UV-induced derivative-spectral changes to reveal the direct ZEZ-to-EEE photoisomerisation without the transient formation of an intermediate to suggest the bicycle-pedal mechanism. The solid-state photoisomerisation was subsequently monitored by tracing changes in the fourth-order derivatives of absorption spectra of a thin crystalline layer of ZEZ-DPH1 prepared by the drop-casting method, because the distortion of absorption spectra due to light scattering is cancelled. It was suggested that the solid-state photochemical event consists of three steps: fast ZEZ-to-EEE photoisomerisation, a subsequent slow ZEZ-to-EEE photoisomerisation and very slow disappearance of the EEE-isomer. Studies on powder XRD were also carried out for a drop-cast solid layer of ZEZ-DPH1 to disclose the coexistence of a crystal form other than the original one, and the former exhibited faster ZEZ-to-EEE photoisomerisation when compared with the original crystal form. The results revealed by XRD analysis are in line with those obtained by higher-order derivative spectra, confirming the solid-state one-way photoisomerisation to take place through the bicycle-pedal process.

The observation of the physicochemical change of rock under freeze-thawing experiment: CLSM, XRD and ICP analysis

NASA Astrophysics Data System (ADS)

Choi, J.; Chae, B.; Chon, C.; Jeong, J.

2013-12-01

Abstract : In order to understand the progress of the physical weathering of rock sample, we managed freeze-thawing experiment at temperature of up to 40C from -20C taking into account of South Korea. In this study, the time was held by two hours the temperature of the maximum (40C) and minimum (-20C) and the experiments were carried out at intervals of one hour rising and falling. We have run the experiment about 120 cycle with the cycle of -20C from 40C experiment. We measured the physical properties of rock samples after each 20 cycle has elapsed by using confocal laser scanning microscope (CLSM) and observed changes in roughness of rock samples surface. We also analyzed the mineral of rock sample using the XRD analysis and observing the change in chemical composition of solution used in the experiment by using ICP analysis. Through the above process, we observed physico-chemical changes in the rock sample due to freeze-thaw cycles. To analysis of the line roughness parameter we used set by the 10 vertical and horizontal cross section line on the surface and surface roughness parameter was analyzed by using the area on the surface. Through such a process, while the freeze-thawing experiment is advanced, it was studied how the physical roughness and chemical composition were changed. As a result, it was possible to observe a change in the mineral component of the particular dissolved in the solution and it was able to observe the characteristic changes of the parameters of the roughness of the lines and surfaces.

Cyanidation Study of Slag Rich in Silver

NASA Astrophysics Data System (ADS)

Pérez-Labra, Miguel; Romero-Serrano, J. Antonio; Ávila-Davila, E. O.; Reyes-Pérez, M.; Barrientos-Hernández, F. R.; Hernández, I. A. Lira

Slag from smelting reduction processes were characterized by chemical analysis, XRD, SEM-EDS and XRF. The results revealed Ag concentrations of 362 g/t of slag, the slag mineralogical characterization by XRD and SEM-EDS showed mineralogical species oxidized complex containing Pb, Zn, Ca, Si, Fe, As, S in its structure, silver was found in globules associated lead in the slag and the furutobeite specie. The leaching study was conducted to evaluate process variables such as NaCN concentration: from 7.8×10-3M - 1.26×10-1M, temperature: 25-50°C, particle size: +140 mesh to -400 mesh, stirring speed of 750 rpm - 900 rpm. All studies were performed with a NaOH concentration of 0.2 M. The optimal values of silver recovery encountered in conditions of 7.8×10-3M NaCN, agitation rate of 750 rpm, temperature of 35°C and with a treatment time of 240 min. We also observed that a particle size -400 mesh will have optimum recoveries compared to +140 mesh, +200, +270 and +325.

Dynamics of Polymorphic Transformations in Palm Oil, Palm Stearin and Palm Kernel Oil Characterized by Coupled Powder XRD-DSC.

PubMed

Zaliha, Omar; Elina, Hishamuddin; Sivaruby, Kanagaratnam; Norizzah, Abd Rashid; Marangoni, Alejandro G

2018-06-01

The in situ polymorphic forms and thermal transitions of refined, bleached and deodorized palm oil (RBDPO), palm stearin (RBDPS) and palm kernel oil (RBDPKO) were investigated using coupled X-ray diffraction (XRD) and differential scanning calorimetry (DSC). Results indicated that the DSC onset crystallisation temperature of RBDPO was at 22.6°C, with a single reflection at 4.2Å started to appear from 23.4 to 17.1°C, and were followed by two prominent exothermic peaks at 20.1°C and 8.5°C respectively. Further cooling to -40°C leads to the further formation of a β'polymorph. Upon heating, a of β'→βtransformation was observed between 32.1 to 40.8°C, before the sample was completely melted at 43.0°C. The crystallization onset temperature of RBDPS was 44.1°C, with the appearance of the α polymorph at the same temperature as the appearance of the first sharp DSC exothermic peak. This quickly changed from α→β´ in the range 25 to 21.7°C, along with the formation of a small β peak at -40°C. Upon heating, a small XRD peak for the β polymorph was observed between 32.2 to 36.0°C, becoming a mixture of (β´+ β) between 44.0 to 52.5°C. Only the β polymorph survived further heating to 59.8°C. For RBDPKO, the crystallization onset temperature was 11.6°C, with the formation of a single sharp exothermic peak at 6.5°C corresponding to the β' polymorphic form until the temperature reached -40°C. No transformation of the polymorphic form was observed during the melting process of RBDPKO, before being completely melted at 33.2°C. This work has demonstrated the detailed dynamics of polymorphic transformations of PKO and PS, two commercially important hardstocks used widely by industry and will contribute to a greater understanding of their crystallization and melting dynamics.

Structural and optical studies of CuO nanostructures

NASA Astrophysics Data System (ADS)

Chand, Prakash; Gaur, Anurag; Kumar, Ashavani

2014-04-01

In the present study, copper oxide (CuO) nanostructures have been synthesized at 140 °C for different aging periods, 1, 24, 48 and 96 hrs by hydrothermal method to investigate their effects on structural and optical properties. The X-ray diffractometer (XRD) pattern indicates the pure phase formation of CuO and the particle size, calculated from XRD data, has been found to be increasing from 21 to 36 nm for the samples synthesized at different aging periods. Field emission scanning electron microscope (FESEM) analysis also shows that the average diameter and length of these rectangular nano flakes increases with increasing the aging periods. Moreover Raman spectrums also confirm the phase formation of CuO. The optical band gaps calculated through UV-visible spectroscopy are found to be decreasing from 2.92 to 2.69 eV with increase in aging periods, 1 to 96 hrs, respectively.

Fluorine-doped NiO nanostructures: Structural, morphological and spectroscopic studies

NASA Astrophysics Data System (ADS)

Singh, Kulwinder; Kumar, Manjeet; Singh, Dilpreet; Singh, Manjinder; Singh, Paviter; Singh, Bikramjeet; Kaur, Gurpreet; Bala, Rajni; Thakur, Anup; Kumar, Akshay

2018-05-01

Nanostructured NiO has been prepared by co-precipitation method. In this study, the effect of fluorine doping (1, 3 and 5 wt. %) on the structural, morphological as well as optical properties of NiO nanostructures has been studied. X-ray diffraction (XRD) has employed for studying the structural properties. Cubic crystal structure of NiO was confirmed by the XRD analysis. Crystallite size increased with increase in doping concentration. Nelson-Riley factor (NRF) analysis indicated the presence of defect states in the synthesized samples. Field emission scanning electron microscopy showed the spherical morphology of the synthesized samples and also revealed that the particle size varied with dopant content. The optical properties were studied using UV-Visible Spectroscopy. The results indicated that the band gap energy of the synthesized nanostructures decreased with increase in doping concentration upto 3% but increased as the doping concentration was further raised to 5%. This can be ascribed to the defect states variations in the synthesized samples. The results suggested that the synthesized nanostructures are promising candidate for optoelectronic as well as gas sensing applications.

Investigation of irradiation effects induced by self-ion in 6H-SiC combining RBS/C, Raman and XRD

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chaabane, Nihed; Debelle, Aurelien; Sattonnay, Gael

2012-01-01

Single crystals of 6H-SiC were irradiated at room temperature and 670 K with 4 MeV C ions at two fluences: 1015 and 1016 cm2 (0.16 and 1.6 dpa at the damage peak). Damage accumulation was studied by a combination of X-ray diffraction (XRD), Raman spectroscopy and Rutherford backscattering spectrometry in channelling geometry (RBS/C) along the [0001] direction. The irradiated layer is found to be composed of a low damage region up to 1.5 lm followed by a region where the disorder level is higher, consistent with SRIM predictions. At room temperature and low fluence, typically 1015 cm2, the strain depthmore » profile follows the dpa depth distribution (with a maximum value of 2%). The disorder is most likely due to small defect clusters. When increasing the fluence up to 1016 cm2, a buried amorphous layer forms, as indicated by e.g. Raman results where the Si C bands become broader or even disappear. At a higher irradiation temperature of 670 K, amorphization is not observed at the same fluence, revealing a dynamic annealing process. However, results tend to suggest that the irradiated layer is highly heterogeneous and composed of different types of defects.« less

The effect of chemical modification on the physico-chemical characteristics of halloysite: FTIR, XRF, and XRD studies

NASA Astrophysics Data System (ADS)

Szczepanik, Beata; Słomkiewicz, Piotr; Garnuszek, Magdalena; Czech, Kamil; Banaś, Dariusz; Kubala-Kukuś, Aldona; Stabrawa, Ilona

2015-03-01

The effect of chemical modification of halloysite from a Polish strip mine "Dunino" on the chemical composition and structure of this clay mineral was studied using infrared spectroscopy (ATR FT-IR), wavelength dispersive X-ray fluorescence (WDXRF), and X-ray powder diffraction (XRPD) methods. The results obtained by the WDXRF technique confirm that the content of silica and alumina was the highest for bleached halloysite samples and the lowest for acid-treated halloysite. A higher content of Fe2O3 in comparison to halloysite samples coming from other countries was observed for raw halloysite samples. XRPD diffraction pattern obtained for raw halloysite confirmed the presence of halloysite, kaolinite, hematite, and calcite minerals in the sample. Bleaching the halloysite removes (or significantly reduces) the content of other minerals present in the raw halloysite. The FT-IR spectra of the studied halloysite samples show in the 3700-3600 cm-1 region well-defined hydroxyl stretching bands characteristic for the kaolin-group minerals and bands associated with the vibrations of the aluminium-silicon skeleton in the 1400-1000 cm-1 region. Modifying halloysite with 4-chloro-aniline causes successive incorporation of amine into the BH sample.

Cooperative use of VCD and XRD for the determination of tetrahydrobenzoisoquinolines absolute configuration: a reliable proof of memory of chirality and retention of configuration in enediyne rearrangements.

PubMed

Mondal, Shovan; Naubron, Jean-Valère; Campolo, Damien; Giorgi, Michel; Bertrand, Michéle P; Nechab, Malek

2013-12-01

The absolute configurations (AC) of azaheterocylic compounds resulting from the cascade rearrangement of enediynes involving only light atoms were unambiguously assigned by the joint use of vibrational circular dichroism (VCD) and copper radiation single crystal X-ray diffraction (XRD). These AC determinations proved that the rearrangements of enediynes proceeded with memory of chirality and retention of configuration. © 2013 Wiley Periodicals, Inc.

Chemical bath deposited and dip coating deposited CuS thin films - Structure, Raman spectroscopy and surface study

NASA Astrophysics Data System (ADS)

Tailor, Jiten P.; Khimani, Ankurkumar J.; Chaki, Sunil H.

2018-05-01

The crystal structure, Raman spectroscopy and surface microtopography study on as-deposited CuS thin films were carried out. Thin films deposited by two techniques of solution growth were studied. The thin films used in the present study were deposited by chemical bath deposition (CBD) and dip coating deposition techniques. The X-ray diffraction (XRD) analysis of both the as-deposited thin films showed that both the films possess covellite phase of CuS and hexagonal unit cell structure. The determined lattice parameters of both the films are in agreement with the standard JCPDS as well as reported data. The crystallite size determined by Scherrer's equation and Hall-Williamsons relation using XRD data for both the as-deposited thin films showed that the respective values were in agreement with each other. The ambient Raman spectroscopy of both the as-deposited thin films showed major emission peaks at 474 cm-1 and a minor emmision peaks at 265 cm-1. The observed Raman peaks matched with the covellite phase of CuS. The atomic force microscopy of both the as-deposited thin films surfaces showed dip coating thin film to be less rough compared to CBD deposited thin film. All the obtained results are presented and deliberated in details.

Proton irradiation studies on Al and Al5083 alloy

NASA Astrophysics Data System (ADS)

Bhattacharyya, P.; Gayathri, N.; Bhattacharya, M.; Gupta, A. Dutta; Sarkar, Apu; Dhar, S.; Mitra, M. K.; Mukherjee, P.

2017-10-01

The change in the microstructural parameters and microhardness values in 6.5 MeV proton irradiated pure Al and Al5083 alloy samples have been evaluated using different model based techniques of X-ray diffraction Line Profile Analysis (XRD) and microindendation techniques. The detailed line profile analysis of the XRD data showed that the domain size increases and saturates with irradiation dose both in the case of Al and Al5083 alloy. The corresponding microstrain values did not show any change with irradiation dose in the case of the pure Al but showed an increase at higher irradiation doses in the case of Al5083 alloy. The microindendation results showed that unirradiated Al5083 alloy has higher hardness value compared to that of unirradiated pure Al. The hardness increased marginally with irradiation dose in the case of Al5083, whereas for pure Al, there was no significant change with dose.

Study on electrochemically deposited Mg metal

NASA Astrophysics Data System (ADS)

Matsui, Masaki

An electrodeposition process of magnesium metal from Grignard reagent based electrolyte was studied by comparing with lithium. The electrodeposition of magnesium was performed at various current densities. The obtained magnesium deposits did not show dendritic morphologies while all the lithium deposits showed dendritic products. Two different crystal growth modes in the electrodeposition process of magnesium metal were confirmed by an observation using scanning electron micro scope (SEM) and a crystallographic analysis using X-ray diffraction (XRD). An electrochemical study of the deposition/dissolution process of the magnesium showed a remarkable dependency of the overpotential of magnesium deposition on the electrolyte concentration compared with lithium. This result suggests that the dependency of the overpotential on the electrolyte concentration prevent the locally concentrated current resulting to form very uniform deposits.

Effect of interparticle interactions on size determination of zirconia and silica based systems – A comparison of SAXS, DLS, BET, XRD and TEM

PubMed Central

Pabisch, Silvia; Feichtenschlager, Bernhard; Kickelbick, Guido; Peterlik, Herwig

2012-01-01

The aim of this work is a systematic comparison of size characterisation methods for two completely different model systems of oxide nanoparticles, i.e. amorphous spherical silica and anisotropic facet-shaped crystalline zirconia. Size and/or size distribution were determined in a wide range from 5 to 70 nm using small-angle X-ray scattering (SAXS), dynamic light scattering (DLS), nitrogen sorption (BET), X-ray diffraction (XRD) and transmission electron microscopy (TEM). A nearly perfect coincidence was observed only for SAXS and TEM for both types of particles. For zirconia nanoparticles considerable differences between different measurement methods were observed. PMID:22347721

A study on the structural and mechanical properties of nanocrystalline CuS thin films grown by chemical bath deposition technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mukherjee, Nillohit; Sinha, Arijit; Khan, Gobinda Gopal

2011-01-15

We report a chemical route for the deposition of nanocrystalline thin films of CuS, using aqueous solutions of Cu(CH{sub 3}COO){sub 2}, SC(NH{sub 2}){sub 2} and N(CH{sub 2}CH{sub 2}OH){sub 3} [triethanolamine, i.e. TEA] in proper concentrations and ratios. The films were structurally characterized using X-ray diffraction technique (XRD), field emission scanning electron microscopy (FESEM) and optical analysis [both photo luminescence (PL) and ultraviolet-visible (UV-vis)]. Optical studies showed a large blue shift in the band gap energy of the films due to quantum confinement effect exerted by the nanocrystals. From both XRD and FESEM analyses, formation of CuS nanocrystals with sizes withinmore » 10-15 nm was evident. A study on the mechanical properties was carried out using nanoindentation and nanoscratch techniques, which showed good mechanical stability and high adherence of the films with the bottom substrate. Such study on the mechanical properties of the CuS thin films is being reported here for the first time. Current-voltage (I-V) measurements were also carried out for the films, which showed p-type conductivity.« less

Study on structural, morphological, optical and thermal properties of guanidine carbonate doped nickel sulfate hexahydrate crystal.

PubMed

Silambarasan, A; Rajesh, P; Ramasamy, P

2015-01-05

The single crystal of guanidine carbonate doped nickel sulfate hexahydrate was grown from solution for ultraviolet filters. The single crystal XRD confirms that the grown single crystal belongs to the tetragonal system with the space group of P4₁2₁2. The crystallinity of the grown crystal was estimated by powder X-ray diffraction studies. The optical transmission and thermal stability of as-grown guanidine carbonate doped nickel sulfate single crystals have been studied. The optical transmission spectrum demonstrates the characteristics of ultraviolet filters. The TG/DTA studies confirm the thermal properties of grown crystals. Thermo-gravimetric analysis showed that the dehydration temperature of the guanidine carbonate doped nickel sulfate crystal is about 100 °C, which is much higher than that of pure nickel sulfate hexahydrate (NSH) crystals which is 72 °C. The growth behaviors and dislocation density were detected under the high resolution XRD and etching studies respectively. Copyright © 2014 Elsevier B.V. All rights reserved.

Ab initio random structure searching of organic molecular solids: assessment and validation against experimental data† †Electronic supplementary information (ESI) available: Results of similarity analysis between the 11 structures of lowest energy obtained in the AIRSS calculations and the reported structures of form III and form IV of m-ABA; unit cell parameters and volumes for all structures considered; comparison of 2θ values derived from the unit cell parameters of different structural models representing form III of m-ABA; Le Bail fitting of the experimental powder XRD pattern of form IV of m-ABA recorded at 70 K using, as the initial structural model, the reported crystal structure following geometry optimization; table of calculated (GIPAW) absolute isotropic NMR shieldings; simulated powder XRD data for the considered structures after precise geometry optimization; experimental 1H MAS NMR spectra of forms III and IV. (pdf) The calculated and experimental data for this study are provided as a supporting dataset from WRAP, the Warwick Research Archive Portal at http://wrap.warwick.ac.uk/91884. See DOI: 10.1039/c7cp04186a

PubMed Central

Zilka, Miri; Dudenko, Dmytro V.; Hughes, Colan E.; Williams, P. Andrew; Sturniolo, Simone; Franks, W. Trent; Pickard, Chris J.

2017-01-01

This paper explores the capability of using the DFT-D ab initio random structure searching (AIRSS) method to generate crystal structures of organic molecular materials, focusing on a system (m-aminobenzoic acid; m-ABA) that is known from experimental studies to exhibit abundant polymorphism. Within the structural constraints selected for the AIRSS calculations (specifically, centrosymmetric structures with Z = 4 for zwitterionic m-ABA molecules), the method is shown to successfully generate the two known polymorphs of m-ABA (form III and form IV) that have these structural features. We highlight various issues that are encountered in comparing crystal structures generated by AIRSS to experimental powder X-ray diffraction (XRD) data and solid-state magic-angle spinning (MAS) NMR data, demonstrating successful fitting for some of the lowest energy structures from the AIRSS calculations against experimental low-temperature powder XRD data for known polymorphs of m-ABA, and showing that comparison of computed and experimental solid-state NMR parameters allows different hydrogen-bonding motifs to be discriminated. PMID:28944393

Chemical induced demineralization study in cortical bone

NASA Astrophysics Data System (ADS)

Sales, E.; da Silva, C. E. R.; Letichevsky, S.; dos Santos, R.; Leitao, R.; dos Santos, C. T.; de Oliveira, L. F.; de Avillez, R.; Monteiro, M.; Costa-Felix, R.; Paciornik, S.; dos Anjos, M.

2018-05-01

In this work we present a study of demineralization in bovine cortical bone. We selected 9 fresh cortical bone samples from 2 diaphyseal femurs for analysis. Samples were demineralized for 24 h, 48 h, 72 h and 96 h using two concentrations of EDTA with different pH: EDTA 0.1 M (pH 10, alkaline) and EDTA 0.5 M (pH 7.4, neutral). We have employed μ-X-ray fluorescence (μ-XRF) and X-ray diffraction (XRD) to assess the degree of demineralization. EDTA solutions were analyzed for Calcium (Ca) and Phosphorous (P) extractions by Atomic Absorption Spectrophotometry (AAS) and Ion Chromatography (IC), respectively. Results from AAS and IC showed that EDTA 0.5 M (pH 7.4) removed two times more Ca and 3 times more P than EDTA 0.1 M (pH 10) in the first 24 hours. μ-XRF results presented that EDTA has a high capacity to bind Calcium and Phosphorus. On the other hand, despite the differences in concentration and pH, EDTA did not bind Zn and Sr. Results from XRD showed that EDTA with high concentration had a greater impact to the samples' crystallinity causing a severe damage.

Endophytic fungal isolate mediated biosynthesis of silver nanoparticles and their free radical scavenging activity and anti microbial studies.

PubMed

Netala, Vasudeva Reddy; Kotakadi, Venkata Subbaiah; Bobbu, Pushpalatha; Gaddam, Susmila Aparna; Tartte, Vijaya

2016-12-01

The present study reports that the biosynthesis of AgNPs using an endophytic fungus isolated from the ethnomedicinal plant Centella asiatica. The endophytic fungus was identified as Aspergillus versicolor ENT7 based on 18S rRNA gene sequencing (NCBI Accession number KF493864). The AgNPs synthesized were characterized by UV-visible spectroscopy, Fourier transform infra-red spectroscopy (FTIR), transmission electron microscopy (TEM), X-ray diffraction (XRD), particle size analyzer, and zeta potential measurements. The UV-Vis absorption spectra showed the peak at 429 nm which confirmed the synthesis of AgNPs. TEM analysis revealed that the AgNPs were spherical in shape with 3-40 nm in size; similar results were also obtained by Horiba particle size analyzer with 5-40 nm in size. The synthesized AgNPs were highly stable due to their high negative zeta potential value of -38.2 mV. XRD studies showed (111), (200), (220), (311), and (222) planes of the face-centered cubic (FCC) lattice, indicating the crystalline nature of the AgNPs. Selected area electron diffraction (SAED) pattern of the AgNPs showed five circular fringes which were in accordance with XRD data and confirmed the formation of high crystalline nature of AgNPs. FTIR measurements indicated the peaks at 3273, 2925, 1629, 1320, and 1020 cm -1 corresponding to different functional groups possibly involved in the synthesis and stabilization of AgNPs. The synthesized AgNPs exhibited effective free radical scavenging activity with the IC50 value of 60.64 µg/ml. The synthesized AgNPs were found to be highly toxic against both gram-positive and gram-negative bacteria and also showed a very good antifungal activity.

A Preliminary Study on Black Colored Potsherds from Taiwan

NASA Astrophysics Data System (ADS)

Liou, Y. S.; Yi-Chang, L.

2016-12-01

Black colored potsherds from the archaeological sites of late Neolithic (3500-2000 BP) and Iron Age (1400-800 BP) exhibit the minor phase in the number of antiques, however, they represent a specific symbol on the religious rites and social stratum in the archaeological and cultural contents of Taiwan. A lot of efforts focused on morphological and decorative styles of the black pottery have been made in previous archaeological works. In this study, multiple analytical techniques including micro-Raman spectroscopy, X-ray diffraction analysis (XRD), and micro X-ray florescence spectroscopy (μXRF) were applied to 11 potsherds found at eleven archaeological sites across Taiwan to understand the raw materials, production techniques, and the possible interactions and exchange system among ancient societies. Ten mineral phases including α-quartz, amorphous carbon, anatase, plagioclase, etc., were identified from Raman spectra. The presence of amorphous carbon indicates that pottery was fired under reducing conditions. Pyroxene minerals were present in some potsherds, suggesting that raw materials were not sourced locally, and perhaps further indicating trading or people migration activities in ancient periods. XRD measurements and μXRF analyses were used as complementary techniques to obtain mineral and chemical compositions. XRD measurements show that quartz, albite, biotite, and gypsum were present in potsherds. Chemically, SiO2, Al2O3, Na2O, K2O, Fe2O3, and CaO are the main constituents. The correlation plots of these main compositions show that pottery raw material can subdivide into three group which were related to different areas and ages. However, it need more detailed investigation to decipher this issue.

1-Formyl-3-phenyl-5-(4-isopropylphenyl)-2-pyrazoline: Synthesis, characterization, antimicrobial activity and DFT studies

NASA Astrophysics Data System (ADS)

Sid, Assia; Messai, Amel; Parlak, Cemal; Kazancı, Nadide; Luneau, Dominique; Keşan, Gürkan; Rhyman, Lydia; Alswaidan, Ibrahim A.; Ramasami, Ponnadurai

2016-10-01

The structure of 1-formyl-3-phenyl-5-(4-isopropylphenyl)-2-pyrazoline synthesized as single crystal was investigated by FTIR, NMR, XRD. Experimental data were complemented by quantum mechanical calculations. XRD data show that the compound crystallizes in the triclinic system (P-1) via trans isomer (a = 6.4267(4) Å, b = 10.9259(12) Å, c = 12.4628(9) Å and α = 102.894(8)°, β = 102.535(6)°, γ = 101.633(7)°). Anti-microbial screening results indicate that the compound shows promising activity. The theoretically predicted and experimentally obtained parameters reveal further insight into pyrazoline systems.

Composite uranium carbide targets at TRIUMF: Development and characterization with SEM, XRD, XRF and L-edge densitometry

NASA Astrophysics Data System (ADS)

Kunz, Peter; Bricault, Pierre; Dombsky, Marik; Erdmann, Nicole; Hanemaayer, Vicky; Wong, John; Lützenkirchen, Klaus

2013-09-01

The production of radioactive ion beams (RIB) from spallation targets by irradiation with a continuous 500 MeV proton beam, has been routine at TRIUMF for several years. Based on the experience with composite refractory carbide targets a procedure for the fabrication of UC2/C targets was developed. It includes the preparation of UC2 by carbothermal reduction of UO2, the slip-casting of fine-grained UC2/C slurry on graphite foil under inert gas atmosphere and the cutting of composite target discs which are stacked up to a lamellar structure. The thermal properties of such an arrangement are adequate to withstand the high power deposition of an intense, continuous proton beam and also beneficial for the fast release of short-lived radioactive isotopes. Molecular structure, particle size and the impact of sintering of the target discs were investigated via XRD and SEM. Thickness and mass distribution were measured with position-sensitive LIII-edge densitometry. The results confirm that the properties of the UC2/C target material are well suited for RIB production at TRIUMF while there is still room for improvement with regard to uniformity of mass distribution in target disc thickness.

YAlO3:Ce3+ powders: Synthesis, characterization, thermoluminescence and optical studies

NASA Astrophysics Data System (ADS)

Parganiha, Yogita; Kaur, Jagjeet; Dubey, Vikas; Shrivastava, Ravi

2015-09-01

Yttrium aluminum perovskite (YAP) is a promising high temperature ceramic material, known for its mechanical, structural and optical properties. YAP's also known as an ideal host material for solid-state lasers and phosphors. In this work, Ce3+ doped YAlO3 phosphors were synthesized by solid state reaction method, which is very suitable technique for large scale production. A prepared phosphor was characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Scanning electron microscopy (SEM), Photoluminescence spectra and Thermoluminescence (TL) glow curve study. The starting reagents used for sample preparation are Y2O3, Al2O3 and CeO2, boric acid used as a flux. Ratio of Y:Al was 1:1 which shows perovskite structure confirmed by the X-ray diffraction (XRD) study. The entire prepared sample was studied by PL excitation and emission spectra. Prominent peak at 446 nm (blue emission) which shows broad emission spectra of photoluminescence. It proves that prepared phosphor can act as a single host for blue emission of light and can be used for display applications. Commission Internationale de I'Eclairage (CIE) techniques proves the blue emission of light (x = .148, y = .117). TL glow curve analysis of prepared phosphor shows the prominent peak at 189 °C for the variable UV exposure time and high temperature peak shows the more stability and less fading in the prepared phosphor. Kinetic data of prepared phosphor were evaluated by peak shape method for variable UV exposure time (5-25 min).

Structural and magnetic studies of nanocrystalline Y{sub 2}Ir{sub 2}O{sub 7}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dwivedi, Vinod Kumar, E-mail: vinodd@iitk.ac.in; Mukhopadhyay, Soumik

2015-06-24

In this paper, we discuss synthesis of Y{sub 2}Ir{sub 2}O{sub 7} nanoparticles via chemical solution process. Structural analysis shows single cubic phase with Fd-3m space group symmetry. The particle size and distribution were studied by Transmission Electron Microscopy experiments. The average particle size turns out to be 50nm, which is in good agreement with the XRD results. Magnetic characterization shows no evidence of long range ordering even in presence of strong correlations.

High-resolution Measurement of Contact Ion-pair Structures in Aqueous RbCl Solutions from the Simultaneous Corefinement of their Rb and Cl K-edge XAFS and XRD Spectra

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pham, Van-Thai; Fulton, John L.

2016-06-21

In concentrated solutions of aqueous RbCl, all of the Rb+ and Cl- ions exist as contact ion pairs. This full structural assessment is derived from the refinement of three independent experimental measurements: the Rb and Cl K-edge x-ray absorption fine structure (XAFS) and the x-ray diffraction spectra (XRD). This simultaneous refinement of the XAFS and XRD data provides high accuracy since each method probes the structure of different local regions about the ions with high sensitivity. At high RbCl concentration (6 m (mol/kg )) the solution is dominated by Rb+ - Cl- contact ion pairs yielding an average of 1.5more » pairs at an Rb-Cl distance of 3.24 Å. Upon formation of these ion pairs, approximately 1.1 waters molecules are displaced from the Rb+ and 1.4 water molecules from Cl-. The hydration shells about both the cation and anion are also determined. These results greatly improve the understanding of monovalent ions and provide a basis for testing the Rb+-Cl- interaction potentials used in molecular dynamics (MD) simulation. This research was supported by the US Department of Energy, Office of Science, Office of Basic Energy Sciences, Division of Chemical Sciences, Geosciences, and Biosciences.« less

Talk Show Science.

ERIC Educational Resources Information Center

Moore, Mitzi Ruth

1992-01-01

Proposes having students perform skits in which they play the roles of the science concepts they are trying to understand. Provides the dialog for a skit in which hot and cold gas molecules are interviewed on a talk show to study how these properties affect wind, rain, and other weather phenomena. (MDH)

The theoretical and experimental study on dicalcium phosphate dehydrate loading with protocatechuic aldehyde.

PubMed

Guo, Yuehua; Qu, Shuxin; Lu, Xiong; Xie, Haodong; Zhang, Hongping; Weng, Jie

2010-07-01

The aim of this study is to investigate the interaction between dicalcium phosphate dihydrate (CaHPO(4) x 2H(2)O, DCPD) and Protocatechuic aldehyde (C(7)H(6)O(3), Pca), which is the water-soluble constituents of Chinese Medicine, Salvia Miltiorrhiza Bunge (SMB), by calculating the absorption energy through molecular dynamics simulation. Furthermore, the effects of functional groups of Pca and temperature on Pca adsorbed by DCPD are calculated respectively. DCPD/Pca and DCPD were analyzed by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TG). The simulation results showed that Pca mostly absorbed on the (0 2 0) surface of DCPD. The aldehyde group of Pca played a moren important role on the adsorption of Pca on DCPD than hydroxyl did, while temperature had no distinct effects on the adsorption. XRD results indicated that Pca induced the preferential growth of (0 2 0) crystal surface in DCPC/Pca whereas it had no influence on the crystal structure, the crystallinity and grain size of DCPD. FTIR and TG results showed that the characteristic peak of Pca was at 1295 cm(-1) and the content of Pca in DCPD was 16%, respectively. The present results show that molecular dynamics simulation is a very effective and complementary method to study the interaction between materials and medicine.

A study of tantalum pentoxide Ta 2O 5 structures up to 28 GPa

DOE PAGES

Stavrou, Elissaios; Zaug, Joseph M.; Bastea, Sorin; ...

2017-05-02

In this study, tantalum pentoxide Ta 2O 5 with the orthorhombic L-Ta 2O 5 structure has been experimentally studied up to 28.3 GPa (at ambient temperature) using synchrotron angle-dispersive powder X-ray diffraction (XRD). The ambient pressure phase remains stable up to 25 GPa where with increased pressure a crystalline to amorphous phase transition occurs. A detailed equation of state (EOS), including pressure dependent lattice parameters, is reported. The results of this study were compared with a previous high-pressure XRD study by Li et al. A clear discrepancy between the ambient-pressure crystal structures and, consequently, the reported EOSs between the twomore » studies was revealed. Finally, he origin of this discrepancy is attributed to two different crystal structures used to index the XRD patterns.« less

X-ray diffraction study of low-temperature phase transformations in nickel-titanium orthodontic wires.

PubMed

Iijima, M; Brantley, W A; Guo, W H; Clark, W A T; Yuasa, T; Mizoguchi, I

2008-11-01

Employ conventional X-ray diffraction (XRD) to analyze three clinically important nickel-titanium orthodontic wire alloys over a range of temperatures between 25 and -110 degrees C, for comparison with previous results from temperature-modulated differential scanning calorimetry (TMDSC) studies. The archwires selected were 35 degrees C Copper Ni-Ti (Ormco), Neo Sentalloy (GAC International), and Nitinol SE (3M Unitek). Neo Sentalloy, which exhibits superelastic behavior, is marketed as having shape memory in the oral environment, and Nitinol SE and 35 degrees C Copper Ni-Ti also exhibit superelastic behavior. All archwires had dimensions of 0.016in.x0.022in. (0.41 mm x 0.56 mm). Straight segments cut with a water-cooled diamond saw were placed side-by-side to yield a 1 cm x 1cm test sample of each wire product for XRD analysis (Rint-Ultima(+), Rigaku) over a 2theta range from 30 degrees to 130 degrees and at successive temperatures of 25, -110, -60, -20, 0 and 25 degrees C. The phases revealed by XRD at the different analysis temperatures were in good agreement with those found in previous TMDSC studies of transformations in these alloys, in particular verifying the presence of R-phase at 25 degrees C. Precise comparisons are not possible because of the approximate nature of the transformation temperatures determined by TMDSC and the preferred crystallographic orientation present in the wires. New XRD peaks appear to result from low-temperature transformation in martensite, which a recent transmission electron microscopy (TEM) study has shown to arise from twinning. While XRD is a useful technique to study phases in nickel-titanium orthodontic wires and their transformations as a function of temperature, optimum insight is obtained when XRD analyses are combined with complementary TMDSC and TEM study of the wires.

Study of benzotriazole as corrosion inhibitors of carbon steel in chloride solution containing hydrogen sulfide using electrochemical impedance spectroscopy (EIS)

NASA Astrophysics Data System (ADS)

Solehudin, Agus; Nurdin, Isdiriayani

2014-03-01

Corrosion and inhibition studies on API 5LX65 carbon steel in chloride solution containing various concentrations of benzotriazole has been conducted at temperature of 70°C using Electrochemical Impedance Spectroscopy (EIS). Corroded carbon steel surface with and without inhibitor have been observed using X-ray Diffraction (XRD), Scanning Electron Microscope (SEM), and Energy Dispersive Spectroscopy (EDS). The objectives of this research are to study the performance of benzotriazole as corrosion inhibitors. The experimental results of carbon steel corrosion in 3.5% NaCl solution containing 500 mg/l H2S at different BTAH concentrations showed that corrosion rate of carbon steel decreases with increasing of BTAH concentrations from 0 to 10 mmol/l. The inhibition efficiency of BTAH was found to be affected by its concentration. The optimum efficiency obtained of BTAH is 93% at concentration of 5 mmol/l. The result of XRD and EDS analysis reveal the iron sulfide (FeS) formation on corroded carbon steel surface without inhibitor. The EDS spectrum show the Nitrogen (N) bond on carbon steel surface inhibited by BTAH.

Spectroscopic studies on sidewall carboxylic acid functionalization of multi-walled carbon nanotubes with valine.

PubMed

Deborah, M; Jawahar, A; Mathavan, T; Dhas, M Kumara; Benial, A Milton Franklin

2015-03-15

The valine functionalized multi-walled carbon nanotubes (MWCNTS) were prepared and characterized by using XRD, UV-Vis, FT-IR, EPR, SEM, and EDX, spectroscopic techniques. The enhanced XRD peak (002) intensity was observed for valine functionalized MWCNTs compared with oxidized MWCNTs, which is likely due to sample purification by acid washing. UV-Vis study shows the formation of valine functionalized MWCNTs. FT-IR study confirms the presence of functional groups of oxidized MWCNTs and valine functionalized MWCNTs. The ESR line shape analysis indicates that the observed EPR line shape is a Gaussian line shape. The g-values indicate that the systems are isotropic in nature. The morphology study was carried out for oxidized MWCNTs and valine functionalized MWCNTs by using SEM. The EDX spectra revealed that the high purity of oxidized MWCNTs and valine functionalized MWCNTs. The functionalization has been chosen because, functionalization of CNTs with amino acids makes them soluble and biocompatible. Thus, they have potential applications in the field of biosensors and targeted drug delivery. Copyright © 2014 Elsevier B.V. All rights reserved.

Spectroscopic studies on sidewall carboxylic acid functionalization of multi-walled carbon nanotubes with valine

NASA Astrophysics Data System (ADS)

Deborah, M.; Jawahar, A.; Mathavan, T.; Dhas, M. Kumara; Benial, A. Milton Franklin

2015-03-01

The valine functionalized multi-walled carbon nanotubes (MWCNTS) were prepared and characterized by using XRD, UV-Vis, FT-IR, EPR, SEM, and EDX, spectroscopic techniques. The enhanced XRD peak (0 0 2) intensity was observed for valine functionalized MWCNTs compared with oxidized MWCNTs, which is likely due to sample purification by acid washing. UV-Vis study shows the formation of valine functionalized MWCNTs. FT-IR study confirms the presence of functional groups of oxidized MWCNTs and valine functionalized MWCNTs. The ESR line shape analysis indicates that the observed EPR line shape is a Gaussian line shape. The g-values indicate that the systems are isotropic in nature. The morphology study was carried out for oxidized MWCNTs and valine functionalized MWCNTs by using SEM. The EDX spectra revealed that the high purity of oxidized MWCNTs and valine functionalized MWCNTs. The functionalization has been chosen because, functionalization of CNTs with amino acids makes them soluble and biocompatible. Thus, they have potential applications in the field of biosensors and targeted drug delivery.

Conservation of Moroccan manuscript papers aged 150, 200 and 800 years. Analysis by infrared spectroscopy (ATR-FTIR), X-ray diffraction (XRD), and scanning electron microscopy energy dispersive spectrometry (SEM-EDS).

PubMed

Hajji, Latifa; Boukir, Abdellatif; Assouik, Jamal; Lakhiari, Hamid; Kerbal, Abdelali; Doumenq, Pierre; Mille, Gilbert; De Carvalho, Maria Luisa

2015-02-05

The preservation of manuscripts and archive materials is a serious problem for librarians and restorers. Paper manuscript is subjected to numerous degradation factors affecting their conservation state. This research represents an attempt to evaluate the conservation restoration process applied in Moroccan libraries, especially the alkaline treatment for strengthening weakened paper. In this study, we focused on six samples of degraded and restored paper taken from three different Moroccan manuscripts aged 150, 200 and 800 years. In addition, the Japanese paper used in restoration has been characterized. A modern paper was also analyzed as reference. A three-step analytical methodology based on infrared spectroscopy (ATR-FTIR), X-ray diffraction (XRD) and scanning electron microscopy coupled to energy dispersive spectrometry (SEM-EDS) analysis was developed before and after restoration in order to determine the effect of the consolidation treatment on the paper structure. The results obtained by XRD and ATR-FTIR disclosed the presence of barium sulfate (BaSO4) in all restored paper manuscripts. The presence of calcium carbonate (CaCO3) in all considered samples was confirmed by FTIR spectroscopy. The application of de-acidification treatment causes significant changes connected with the increase of intensity mostly in the region 1426 cm(-1), assigned to the asymmetric and symmetric CO stretching mode of calcite, indicating the effectiveness of de-acidification procedure proved by the rise of the alkaline reserve content allowing the long term preservation of paper. Observations performed by SEM magnify the typical paper morphology and the structure of fibbers, highlighting the effect of the restoration process, manifested by the reduction of impurities. Copyright © 2014 Elsevier B.V. All rights reserved.

Honored Teacher Shows Commitment.

ERIC Educational Resources Information Center

Ratte, Kathy

1987-01-01

Part of the acceptance speech of the 1985 National Council for the Social Studies Teacher of the Year, this article describes the censorship experience of this honored social studies teacher. The incident involved the showing of a videotape version of the feature film entitled "The Seduction of Joe Tynan." (JDH)

Study of chloride ion transport of composite by using cement and starch as a binder

DOE Office of Scientific and Technical Information (OSTI.GOV)

Armynah, Bidayatul; Halide, Halmar; Zahrawani,

This study presents the chemical bonding and the structural properties of composites from accelerator chloride test migration (ACTM). The volume fractions between binder (cement and starch) and charcoal in composites are 20:80 and 60:40. The effect of the binder to the chemical composition, chemical bonding, and structural properties before and after chloride ion passing through the composites was determined by X-ray fluorescence (XRF), by Fourier transform infra-red (FTIR), and x-ray diffraction (XRD), respectively. From the XRD data, XRF data, and the FTIR data shows the amount of chemical composition, the type of binding, and the structure of composites are dependingmore » on the type of binder. The amount of chloride migration using starch as binder is higher than that of cement as a binder due to the density effects.« less

Structural and optical studies of hydrothermally synthesized MoS{sub 2} nanostructures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chacko, Levna; Swetha, A. K.; Aneesh, P. M., E-mail: aneeshpm@cukerala.ac.in

2016-05-06

Transition-metal dichalcogenides like molybdenum disulphide have intrigued intensive interest as two-dimensional (2D) materials beyond extensively studied graphene due to their unique electronic and optical properties. Here we report the hydrothermal synthesis of MoS{sub 2} nanostructures without the addition of any surfactants. The structural and optical properties of the synthesized samples were characterized by various techniques, including X-ray diffraction (XRD), UV-Vis absorption, photoluminescence (PL), and Raman analysis. XRD and Raman spectroscopic studies confirm the formation of hexagonal phase and well ordered stacking of S-Mo-S layers. The increased lattice parameters of MoS{sub 2} samples are due to the stress or strain inducedmore » bending and folding of the layers. The synthesized MoS{sub 2} nanostructures shows a large optical absorption in 300-700 nm region and strong luminescence at 640 nm. In addition, the optical results demonstrates the quantum confinement in layered d-electron material MoS{sub 2} that can lead to engineer its various properties for electronic and optoelectronic applications.« less

Phase transition studies in bismuth ferrite thin films synthesized via spray pyrolysis technique

NASA Astrophysics Data System (ADS)

Goyal, Ankit; Lakhotia, Harish

2013-06-01

Multiferroic are the materials, which combine two or more "ferroic" properties, ferromagnetism, ferroelectricity or ferroelasticity. BiFeO3 is the only single phase multiferroic material which possesses a high Curie temperature (TC ˜ 1103 K), and a high Neel temperature (TN ˜ 643 K) at room temperature. Normally sophisticated methods are being used to deposit thin films but here we have tried a different method Low cost Spray Pyrolysis Method to deposit BiFeO3 thin film of Glass Substrate with rhombohedral crystal structure and R3c space group. Bismuth Ferrite thin films are synthesized using Bismuth Nitrate and Iron Nitrate as precursor solutions. X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) were used to study structural analysis of prepared thin films. XRD pattern shows phase formation of BiFeO3 and SEM analysis shows formation of nanocrystals of 200 nm. High Temperature Resistivity measurements were done by using Keithley Electrometer (Two Probe system). Abrupt behavior in temperature range (313 K - 400K) has been observed in resistance studies which more likely suggests that in this transition the structure is tetragonal rather than rhombohedral. BiFeO3 is the potential active material in the next generation of ferroelectric memory devices.

Doping effect on the structural properties of Cu1-x(Ni, Zn, Al and Fe)xO samples (0study

NASA Astrophysics Data System (ADS)

Amaral, J. B.; Araujo, R. M.; Pedra, P. P.; Meneses, C. T.; Duque, J. G. S.; dos S. Rezende, M. V.

2016-09-01

In this work, the effect of insertion of transition metal, TM (=Ni, Zn, Al and Fe), ions in Cu1-xTMxO samples (0studied through experimental and computational methods. The analyses of X-ray diffraction (XRD) patterns using Rietveld refinement show that i) at x=0, all samples present a monoclinic crystal system with space group C2/c and ii) for increasing the TM-doping, Ni and Zn-doped samples show a small amount of spurious phases for concentrations above x=0.05. Based on these results, a defect disorder study for using atomistic computational simulations which is based on the lattice energy minimization technique is employed to predict the location of the dopant ions in the structure. In agreement with XRD data, our computational results indicate that the trivalent (Al and Fe ions) are more favorable to be incorporated into CuO matrix than the divalent (Ni and Zn ions).

New Study Shows 59 Percent of Americans Will Develop Kidney Disease in Their Lifetime

MedlinePlus

... Patients Organ Donation & Transplantation Professionals Events Advocacy Donate NEW STUDY SHOWS 59 PERCENT OF AMERICANS WILL DEVELOP ... Urine Screening for All Americans Over Age 60 New York, NY (August 1, 2013) – Nearly six of ...

In-vitro antibacterial study of zinc oxide nanostructures on Streptococcus sobrinus

NASA Astrophysics Data System (ADS)

Bakhori, Siti Khadijah Mohd; Mahmud, Shahrom; Ann, Ling Chuo; Sirelkhatim, Amna; Hasan, Habsah; Mohamad, Dasmawati; Masudi, Sam'an Malik; Seeni, Azman; Rahman, Rosliza Abd

2014-10-01

Zinc oxide nanostructures were prepared using a pilot plant of zinc oxide boiling furnace. Generally, it produced two types of nanostructures different in morphology; one is rod-like shaped (ZnO-1) and a plate-like shape (ZnO-2). The properties of ZnO were studied by structural, optical and morphological using XRD, PL and FESEM respectively. The XRD patterns confirmed the wurtzite structures of ZnO with the calculated crystallite size of 41 nm (ZnO-1) and 42 nm (ZnO-2) using Scherrer formula. The NBE peaks were determined by photoluminescence spectra which reveal peak at 3.25 eV and 3.23 eV for ZnO-1 and ZnO-2 respectively. Prior to that, the morphologies for both ZnO-1 and ZnO-2 were demonstrated from FESEM micrographs. Subsequently the antibacterial study was conducted using in-vitro broth dilution technique towards a gram positive bacterium Streptococcus sobrinus (ATCC 33478) to investigate the level of antibacterial effect of zinc oxide nanostructures as antibacterial agent. Gradual increment of ZnO concentrations from 10-20 mM affected the inhibition level after twenty four hours of incubation. In conjunction with concentration increment of ZnO, the percentage inhibition towards Streptococcus sobrinus was also increased accordingly. The highest inhibition occurred at 20 mM of ZnO-1 and ZnO-2 for 98% and 77% respectively. It showed that ZnO has good properties as antibacterial agent and relevancy with data presented by XRD, PL and FESEM were determined.

Setup for in situ x-ray diffraction study of swift heavy ion irradiated materials.

PubMed

Kulriya, P K; Singh, F; Tripathi, A; Ahuja, R; Kothari, A; Dutt, R N; Mishra, Y K; Kumar, Amit; Avasthi, D K

2007-11-01

An in situ x-ray diffraction (XRD) setup is designed and installed in the materials science beam line of the Pelletron accelerator at the Inter-University Accelerator Centre for in situ studies of phase change in swift heavy ion irradiated materials. A high vacuum chamber with suitable windows for incident and diffracted X-rays is integrated with the goniometer and the beamline. Indigenously made liquid nitrogen (LN2) temperature sample cooling unit is installed. The snapshots of growth of particles with fluence of 90 MeV Ni ions were recorded using in situ XRD experiment, illustrating the potential of this in situ facility. A thin film of C60 was used to test the sample cooling unit. It shows that the phase of the C60 film transforms from a cubic lattice (at room temperature) to a fcc lattice at around T=255 K.

Setup for in situ x-ray diffraction study of swift heavy ion irradiated materials

NASA Astrophysics Data System (ADS)

Kulriya, P. K.; Singh, F.; Tripathi, A.; Ahuja, R.; Kothari, A.; Dutt, R. N.; Mishra, Y. K.; Kumar, Amit; Avasthi, D. K.

2007-11-01

An in situ x-ray diffraction (XRD) setup is designed and installed in the materials science beam line of the Pelletron accelerator at the Inter-University Accelerator Centre for in situ studies of phase change in swift heavy ion irradiated materials. A high vacuum chamber with suitable windows for incident and diffracted X-rays is integrated with the goniometer and the beamline. Indigenously made liquid nitrogen (LN2) temperature sample cooling unit is installed. The snapshots of growth of particles with fluence of 90MeV Ni ions were recorded using in situ XRD experiment, illustrating the potential of this in situ facility. A thin film of C60 was used to test the sample cooling unit. It shows that the phase of the C60 film transforms from a cubic lattice (at room temperature) to a fcc lattice at around T =255K.

Study Shows Administrative Shortage.

ERIC Educational Resources Information Center

Sullivan, John R., Jr.

1989-01-01

Summarizes "Administrative Shortage in New England: The Evidence, the Causes, the Recommendations." High pressure, long hours, low salaries, and high housing costs are among the reasons cited for the shortage. Recommendations are centered on role identity, staff support, training, and recruitment. (SI)

Hey Teacher, Your Personality's Showing!

ERIC Educational Resources Information Center

Paulsen, James R.

1977-01-01

A study of 30 fourth, fifth, and sixth grade teachers and 300 of their students showed that a teacher's age, sex, and years of experience did not relate to students' mathematics achievement, but that more effective teachers showed greater "freedom from defensive behavior" than did less effective teachers. (DT)

Study on Sumbawa gold recovery using centrifuge

NASA Astrophysics Data System (ADS)

Ferdana, A. D.; Petrus, H. T. B. M.; Bendiyasa, I. M.; Prijambada, I. D.; Hamada, F.; Sachiko, T.

2018-01-01

The Artisanal Small Gold Mining in Sumbawa has been processing gold with mercury (Hg), which poses a serious threat to the mining and global environment. One method of gold processing that does not use mercury is by gravity method. Before processing the ore first performed an analysis of Mineragraphy and analysis of compound with XRD. Mineragraphy results show that gold is associated with chalcopyrite and covelite and is a single particle (native) on size 58.8 μm, 117 μm up to 294 μm. characterization with XRD shows that the Sumbawa Gold Ore is composed of quartz, pyrite, pyroxene, and sericite compounds. Sentrifugation is one of separation equipment of gravity method to increase concentrate based on difference of specific gravity. The optimum concentration result is influenced by several variables, such as water flow rate and particle size. In this present research, the range of flow rate is 5 lpm and 10 lpm, the particle size - 100 + 200 mesh and -200 +300 mesh. Gold concentration in concentrate is measured by EDX. The result shows that the optimum condition is obtained at a separation with flow rate 5 lpm and a particle size of -100 + 200 mesh.

Synthesis, Characterization and Comparative Luminescence Studies of Rare-Earth-Doped Gd2O3 Nanoparticles

NASA Astrophysics Data System (ADS)

Pyngrope, D.; Singh, L. R.; Prasad, A. I.; Bora, A.

2018-04-01

A facile direct precipitation method was used for the synthesis of luminescence nanomaterial. Gd2O3 doped with rare earth element Eu3+ is synthesized by polyol route. The synthesized nanoparticles show their characteristic red emission. The nanoparticles are characterized by x-ray diffractometer (XRD), Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM) and photoluminescence (PL) study. The synthesized nanoparticles are spherical particles with 30 nm size. The photoluminescence studies show the characteristic Eu3+ red emission. The PL study shows the intensity of the magnetic dipole transition ( 5 D0 \\to 7 F1 ) at 592 nm compared to that of the electronic dipole transition ( 5 D0 \\to 7 F2 ) at 615 nm. The nanomaterials can show significant application in various display devices and biomedical applications for tracking.

Phase identification and morphology study of hematite (Fe2O3) with sintering time varitions

NASA Astrophysics Data System (ADS)

Yazirin, Cepi; Puspitasari, Poppy; Sasongko, Muhammad Ilman Nur; Tsamroh, Dewi Izzatus; Risdanareni, Puput

2017-09-01

Iron oxide has been the interest of many studies due to its applications in various scientific and industrial fields including in environment, corrosion, soil science, and exhaust emissions. Iron oxide (Fe2O3) has potential applications in catalytic reactions in electronic devices such as semiconductors, paint formulations, and lithium rechargeable batteries. Fe2O3 can be synthesized through the process of stirring, decomposition of organic iron, sol-gel, combustion, and evaporating solvents. Most of the methods used involve several steps and take a long time. The aim of this research was to investigate the phase and morphology characterization of iron oxide (Fe2O3) powder with solvent ethylene glycol after being sintered for 1 hour, 2 hours and 3 hours. The characterization tools utilized were XRD, SEM-EDX, and FTIR. The results of XRD analysis showed that the Fe2O3 sintered for 1 hour had the smallest crystallite size with a diameter of 21.05 nm. In the XRD test, the beam of X-ray was shot directly at the grain being tested. The results of SEM analysis showed thatthe Fe2O3 sintered for 1 hour produced the best result due to its crystallite size of 12.36 nm and hada shape of homogeneous nanosphere; the duration of sintering indeed had a great influence on the grain size of iron oxide (Fe2O3). In addition, the results of the elemental composition analysis indicate that the longer the sintering process, the higher the concentration of O but the lower the Fe.

Photoluminescence studies on holmium (III) and praseodymium (III) doped calcium borophosphate (CBP) phosphors

NASA Astrophysics Data System (ADS)

Reddy Prasad, V.; Damodaraiah, S.; Devara, S. N.; Ratnakaram, Y. C.

2018-05-01

Using solid state reaction method, Ho3+ and Pr3+ doped calcium borophosphate (CBP) phosphors were prepared. These phosphors were characterized using XRD, SEM, FT-IR, 31P solid state NMR, photoluminescence (PL) and decay profiles. Structural details were discussed from XRD and FT-IR spectra. From 31P NMR spectra of these phosphors, mono-phosphate complexes Q0-(PO43-) were observed. Photoluminescence spectra were measured for both Ho3+ and Pr3+ doped calcium borophosphate phosphors and the spectra were studied for different concentrations. Decay curves were obtained for the excited level, 5F4+5S2 of Ho3+ and 1D2 level of Pr3+ in these calcium borophosphate phosphors and lifetimes were measured. CIE color chromaticity diagrams are drawn for these two rare earth ions in calcium borophosphate phosphors. Results show that Ho3+ and Pr3+ doped CBP phosphors might be served as green and red luminescence materials.

Study on structure and morphology (Boehmeria nivea) in the irregular and regular parts of the fiber after biodegumming

NASA Astrophysics Data System (ADS)

Wulandari, A. P.; Septarini, D.; Zainuddin, A.

2017-05-01

Ramie is a natural fiber that is very potential to be developed in Indonesia. Decorticated-fiber which has been known as china grass produce different structures irregular part but shows a long straight section in the middle. This study aims to determine differences in chemical components, morphology and microstructure of two different parties after biodegumming process. China grass has been processed to remove gum using pectinolytic fungus. The microstructure of the treated was further tested by Fourier Transform InfraRed (FTIR), X-Ray Diffraction (XRD), and Scanning Electron Microscope (SEM). The FTIR study indicated that during the biodegumming process, chemical bonding of non-cellulose components most removed by the activity of pectinase from the fungus. XRD analysis reflects an increase in the crystallinity of the fiber after biodegumming. Scanning electron microscopy (SEM) was used to confirm a reduction in the size of the fiber after biodegumming either in the irregular and regular part of the fiber after biodegumming.

Contesting the "Nature" Of Conformity: what Milgram and Zimbardo's studies really show.

PubMed

Haslam, S Alexander; Reicher, Stephen D

2012-01-01

Understanding of the psychology of tyranny is dominated by classic studies from the 1960s and 1970s: Milgram's research on obedience to authority and Zimbardo's Stanford Prison Experiment. Supporting popular notions of the banality of evil, this research has been taken to show that people conform passively and unthinkingly to both the instructions and the roles that authorities provide, however malevolent these may be. Recently, though, this consensus has been challenged by empirical work informed by social identity theorizing. This suggests that individuals' willingness to follow authorities is conditional on identification with the authority in question and an associated belief that the authority is right.

Stabilization of collagen with EDC/NHS in the presence of L-lysine: a comprehensive study.

PubMed

Usha, R; Sreeram, K J; Rajaram, A

2012-02-01

This paper reports the effect of L-lysine on the conformational, rheological, and thermal properties of 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide (EDC) and N-hydroxysuccinimide (NHS) cross linked collagen and investigates the influence of l-lysine on the self assembly processes of collagen. In the absence of L-lysine, the rheological characterization of collagen cross linked with EDC/NHS showed an increase in shearing stress with shearing speed indicating that the collagen chains become rigid and the molecules are reluctant to flow. On the other hand, the increase in shearing stress with shearing speed is comparatively much less in the presence of L-lysine indicating a greater flexibility of the collagen molecules. The self assembly processes of collagen treated with EDC/NHS in the absence and presence of L-lysine were characterized using powder XRD, FT-IR, polarizing optical microscopy and kinetic studies. XRD studies show an increase in peak intensity and sharpness in the presence of L-lysine indicating the enhancement of crystallinity of collagen nano-fibrils. FT-IR results suggest that the incorporation of L-lysine in the EDC/NHS cross linking favors the molecular stability of collagen. From the present study, it is possible to conclude that the pre-treatment of collagen with L-lysine enhances EDC/NHS cross linking and can be used for biomaterial applications. Copyright © 2011 Elsevier B.V. All rights reserved.

The graphene oxide membrane immersing in the aqueous solution studied by electrochemical impedance spectroscopy

NASA Astrophysics Data System (ADS)

Zhang, Yongjing; Chen, Zhe; Yao, Lei; Wang, Xiao; Fu, Ping; Lin, Zhidong

2018-04-01

The interlayer spacing of graphene oxide (GO) is a key property for GO membrane. To probe the variation of interlayer spacing of the GO membrane immersing in KCl aqueous solution, electrochemical impedance spectroscopy (EIS), x-ray diffraction (XRD) and computational calculation was utilized in this study. The XRD patterns show that soaking in KCl aqueous solution leads to an increase of interlayer spacing of GO membrane. And the EIS results indicate that during the immersing process, the charge transfer resistance of GO membrane decreases first and then increases. Computational calculation confirms that intercalated water molecules can result in an increase of interlayer spacing of GO membrane, while the permeation of K+ ions would lead to a decrease of interlayer spacing. All the results are in agreement with each other. It suggests that during the immersing process, the interlayer spacing of GO enlarges first and then decreases. EIS can be a promisingly online method for examining the interlayer spacing of GO in the aqueous solution.

Epitaxial growth of the zinc oxide nanorods, their characterization and in vitro biocompatibility studies.

PubMed

Gopikrishnan, Ramya; Zhang, Kai; Ravichandran, Prabakaran; Biradar, Santhoshkumar; Ramesh, Vani; Goornavar, Virupaxi; Jeffers, Robert B; Pradhan, Aswini; Hall, Joseph C; Baluchamy, Sudhakar; Ramesh, Govindarajan T

2011-10-01

Here, we have synthesized Zinc Oxide (ZnO) nanorods at room temperature using zinc acetate and hexamethylenetetramine as precursors followed by characterization using X-ray diffraction (XRD), fourier transform infra red spectroscopy, scanning electron microscopy (SEM) and transmission electron microscopy. The growth of the synthesized ZnO was found to be very close to its hexagonal nature, which is confirmed by XRD. The nanorods were grown perpendicular to the long-axis and grew along the [001] direction, which is the nature of ZnO growth. The morphology of the synthesized ZnO nanorods was also confirmed by SEM. The size of the nanorod was estimated to be around 20-25 nm in diameter and approximately 50-60 nm in length. Our biocompatibility studies using synthesized ZnO showed no significant dose- or time-dependent increase in the formation of free radicals, accumulation of peroxidative products, antioxidant depletion or loss of cell viability on lung epithelial cells.

Study of benzotriazole as corrosion inhibitors of carbon steel in chloride solution containing hydrogen sulfide using electrochemical impedance spectroscopy (EIS)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Solehudin, Agus, E-mail: asolehudin@upi.edu; Nurdin, Isdiriayani

2014-03-24

Corrosion and inhibition studies on API 5LX65 carbon steel in chloride solution containing various concentrations of benzotriazole has been conducted at temperature of 70°C using Electrochemical Impedance Spectroscopy (EIS). Corroded carbon steel surface with and without inhibitor have been observed using X-ray Diffraction (XRD), Scanning Electron Microscope (SEM), and Energy Dispersive Spectroscopy (EDS). The objectives of this research are to study the performance of benzotriazole as corrosion inhibitors. The experimental results of carbon steel corrosion in 3.5% NaCl solution containing 500 mg/l H{sub 2}S at different BTAH concentrations showed that corrosion rate of carbon steel decreases with increasing of BTAHmore » concentrations from 0 to 10 mmol/l. The inhibition efficiency of BTAH was found to be affected by its concentration. The optimum efficiency obtained of BTAH is 93% at concentration of 5 mmol/l. The result of XRD and EDS analysis reveal the iron sulfide (FeS) formation on corroded carbon steel surface without inhibitor. The EDS spectrum show the Nitrogen (N) bond on carbon steel surface inhibited by BTAH.« less

A study on micro-structural and optical parameters of InxSe1-x thin film

NASA Astrophysics Data System (ADS)

Patel, P. B.; Desai, H. N.; Dhimmar, J. M.; Modi, B. P.

2018-04-01

Thin film of Indium Selenide (InSe) has been deposited by thermal evaporation technique onto pre cleaned glass substrate under high vacuum condition. The micro-structural and optical properties of InxSe1-x (x = 0.6, 1-x = 0.4) thin film have been characterized by X-ray diffractrometer (XRD) and UV-Visible spectrophotometer. The XRD spectra showed that InSe thin film has single phase hexagonal structure with preferred orientation along (1 1 0) direction. The micro-structural parameters (crystallite size, lattice strain, dislocation density, domain population) for InSe thin film have been calculated using XRD spectra. The optical parameters (absorption, transmittance, reflectance, energy band gap, Urbach energy) of InSe thin film have been evaluated from absorption spectra. The direct energy band gap and Urbach energy of InSe thin film is found to be 1.90 eV and 235 meV respectively.

XRD and FTIR studies the effect of heat treatment and doping the transition metal oxide on LiNbO3 and LiNb3O8 nano-crystallite phases in lithium borate glass system.

PubMed

Kashif, Ismail; Soliman, Ashia A; Sakr, Elham M; Ratep, Asmaa

2013-09-01

Glasses of various compositions in the system 90 Li2B4O7-10 Nb2O5 mixed with T.M ions (where T.M is the transition metal) were prepared by quenching technique. Heat-treatment of the parent glasses was performed at 540, 570 and 620 °C, for 5 and 16 h. The glass structure evolution during the controlled crystallization was examined by XRD and FT-IR spectroscopy analysis. The crystalline phases present in the glass ceramics were identified via X-ray diffraction as a function of heat treatment. The FT-IR data propose for these glasses and heat-treated glass network structures mainly built by: di-, tri-, tetra-, penta-and ortho-borate groups. It was found that the quantitative evolution of these various borate species in the glass structures is influenced by the transition metal. A detailed discussion relating to the N4 evolution with the T.M content was made. Copyright © 2013 Elsevier B.V. All rights reserved.

In-state and interstate associations between gun shows and firearm deaths and injuries: A quasi-experimental study

PubMed Central

Matthay, Ellicott C.; Galin, Jessica; Rudolph, Kara E.; Farkas, Kriszta; Wintemute, Garen; Ahern, Jennifer

2018-01-01

Background Gun shows are an important source of firearms, but no adequately powered studies have examined whether these events are associated with increases in firearm injuries. Objective To determine whether gun shows are associated with short-term increases in locally occurring firearm injuries and whether this association differs by the state in which the gun show occurs. Design Quasi-experimental. Setting California. Study Population Individuals in California within driving distance of gun shows. Measurements Gun shows in California and Nevada between 2005 and 2013 (n = 915 shows) and rates of firearm-related deaths, emergency department visits, and inpatient hospitalizations in California. Results Compared to the two weeks before gun shows occurred, post-show firearm injury rates remained stable in regions near California gun shows but increased from 0.67 (95% CI, 0.55 to 0.80) to 1.14 (95% CI, 0.97 to 1.30) per 100,000 in regions near Nevada shows. After adjustment for seasonality and clustering, California shows were not associated with increases in local firearm injuries (RR, 0.99 [95% CI, 0.97 to 1.02]), but Nevada shows were associated with increases in injuries occurring in California (RR, 1.69 [95% CI, 1.16 to 2.45]). The pre-post difference was significantly higher for Nevada shows compared to California shows (Ratio of RRs, 1.70 [95% CI, 1.17 to 2.47]). The Nevada association was driven by significant increases in interpersonal violence firearm injuries (RR, 2.23 [95% CI, 1.01 to 4.89), but corresponded to a small increase in absolute numbers. Non-firearm injuries served as a negative control and were not associated with California or Nevada gun shows. Results were robust to sensitivity analyses. Limitation We only examined firearm injuries in California, and gun show occurrence was not randomized. Conclusion Gun shows occurring in Nevada, but not California, are associated with local, short-term increases in firearm injuries in California. Differing

Tandem transmission/reflection mode XRD instrument including XRF for in situ measurement of Martian rocks and soils

NASA Astrophysics Data System (ADS)

Delhez, Robert; Van der Gaast, S. J.; Wielders, Arno; de Boer, J. L.; Helmholdt, R. B.; van Mechelen, J.; Reiss, C.; Woning, L.; Schenk, H.

2003-02-01

The mineralogy of the surface material of Mars is the key to disclose its present and past life and climates. Clay mineral species, carbonates, and ice (water and CO2) are and/or contain their witnesses. X-ray powder diffraction (XRPD) is the most powerful analytical method to identify and quantitatively characterize minerals in complex mixtures. This paper discusses the development of a working model of an instrument consisting of a reflection mode diffractometer and a transmission mode CCD-XRPD instrument, combined with an XRF module. The CCD-XRD/XRF instrument is analogous to the instrument for Mars missions developed by Sarrazin et al. (1998). This part of the tandem instrument enables "quick and dirty" analysis of powdered (!) matter to monitor semi-quantitatively the presence of clay minerals as a group, carbonates, and ices and yields semi-quantitative chemical information from X-ray fluorescence (XRF). The reflection mode instrument (i) enables in-situ measurements of rocks and soils and quantitative information on the compounds identified, (ii) has a high resolution and reveals large spacings for accurate identification, in particular of clay mineral species, and (iii) the shape of the line profiles observed reveals the kind and approximate amounts of lattice imperfections present. It will be shown that the information obtained with the reflection mode diffractometer is crucial for finding signs of life and changes in the climate on Mars. Obviously this instrument can also be used for other extra-terrestrial research.

Potentiodynamic Polarization Studies and Surface Chemical Composition of Bismuth Titanate (BixTiyOz) Films Produced through Radiofrequency Magnetron Sputtering

PubMed Central

Alfonso, José E.; Olaya, Jhon J.; Pinzón, Manuel J.; Marco, José F.

2013-01-01

The applications of Bismuth Titanate (BixTiyOz) materials have been focused on their electronic and optical properties, but with respect to the use of these compounds in applications like corrosion resistance, have been very few or nonexistent. For this reason, in the present investigation BixTiyOz thin films were deposited using RF magnetron sputtering onto silicon wafers, stainless steel 316L, and titanium alloy (Ti6Al4V) substrates, in order to carry out a study of the corrosion behavior of this compound. The structural properties of the coatings were studied through X-ray diffraction (XRD), the morphology was determined using Scanning Electron Microscopy (SEM), the corrosion resistance behavior of the coated and uncoated substrates was evaluated via the Potentiodynamic Polarization technique, and surface chemical composition was evaluated through X-ray photoelectron spectroscopy (XPS). The XRD results indicated that the films were amorphous. The SEM micrographs showed that the deposited films were homogeneous, but in some cases there were cracks. The potentiodynamic polarization technique showed that the corrosion current in the coated substrates decreased by an order of two magnitudes with respect to the uncoated substrates, but in both cases the corrosion mechanism was pitting due to the pores in the film. The XPS analysis shows that the deposited films contain both Bi3+ and Ti4+. PMID:28788338

Activity and Stability of (Pr 1-xNd x) 2NiO 4 as Cathodes for Solid Oxide Fuel Cells: Part V. In Situ Studies of Phase Evolution

DOE PAGES

Dogdibegovic, Emir; Alabri, Nawf S.; Wright, Christopher J.; ...

2017-08-12

This study is to complement an early report (the manuscript is attached for review purpose) on the role of interlayer on activity and performance stability in praseodymium nickelates. The aforementioned report showed a remarkable 48% increase in power density while switching from common GDC interlayer to a new interlayer chemistry (PGCO). Furthermore, a stable long-term performance was linked with suppressed reaction between the cathode and PGCO interlayer. In this article, we report in situ studies of the phase evolution. The high energy XRD studies at a synchrotron source showed fully suppressed phase transition in praseodymium nickelates with PGCO interlayer, whilemore » the electrodes on the GDC interlayer undergo substantial phase transformation. Furthermore, in operando and post-test XRD analyses shown fully suppressed structural changes in electrodes operated in full cells at 750°C and 0.80 V for 500 hours. SEM-EDS analysis showed that the formation of PrO x at the cathode-interlayer interface may play a role in a decrease of mechanical integrity of the interfaces, due to thermal expansion mismatch, leading to a local stress between the two phases. Furthermore, phase evolution at a narrow interface may propagate toward the electrode bulk, leading to structural changes Q1 and performance degradation.« less

Activity and Stability of (Pr 1-xNd x) 2NiO 4 as Cathodes for Solid Oxide Fuel Cells: Part V. In Situ Studies of Phase Evolution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dogdibegovic, Emir; Alabri, Nawf S.; Wright, Christopher J.

This study is to complement an early report (the manuscript is attached for review purpose) on the role of interlayer on activity and performance stability in praseodymium nickelates. The aforementioned report showed a remarkable 48% increase in power density while switching from common GDC interlayer to a new interlayer chemistry (PGCO). Furthermore, a stable long-term performance was linked with suppressed reaction between the cathode and PGCO interlayer. In this article, we report in situ studies of the phase evolution. The high energy XRD studies at a synchrotron source showed fully suppressed phase transition in praseodymium nickelates with PGCO interlayer, whilemore » the electrodes on the GDC interlayer undergo substantial phase transformation. Furthermore, in operando and post-test XRD analyses shown fully suppressed structural changes in electrodes operated in full cells at 750°C and 0.80 V for 500 hours. SEM-EDS analysis showed that the formation of PrO x at the cathode-interlayer interface may play a role in a decrease of mechanical integrity of the interfaces, due to thermal expansion mismatch, leading to a local stress between the two phases. Furthermore, phase evolution at a narrow interface may propagate toward the electrode bulk, leading to structural changes Q1 and performance degradation.« less

Hydrothermal Synthesis and Biocompatibility Study of Highly Crystalline Carbonated Hydroxyapatite Nanorods

NASA Astrophysics Data System (ADS)

Xue, Caibao; Chen, Yingzhi; Huang, Yongzhuo; Zhu, Peizhi

2015-08-01

Highly crystalline carbonated hydroxyapatite (CHA) nanorods with different carbonate contents were synthesized by a novel hydrothermal method. The crystallinity and chemical structure of synthesized nanorods were studied by Fourier transform infrared spectroscopy (FTIR), X-ray photo-electronic spectroscopy (XPS), X-ray diffraction (XRD), Raman spectroscopy, and transmission electron microscopy (TEM). The biocompatibility of synthesized CHA nanorods was evaluated by cell viability and alkaline phosphatase (ALP) activity of MG-63 cell line. The biocompatibility evaluation results show that these CHA nanorods are biologically active apatites and potentially promising bone-substitute biomaterials for orthopedic application.

Luminescence properties of rare earth doped metal oxide nanostructures: A case of Eu-ZnO

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sahu, D.; Acharya, B. S.; Panda, N. R., E-mail: nihar@iitbbs.ac.in

2016-05-06

The present study reports the growth and luminescence properties of Eu doped ZnO nanostructures. The experiment has been carried out by synthesizing the materials by simple wet-chemical method. X-ray diffraction (XRD) studies show expansion of ZnO lattice with the incorporation of Eu ions which has been confirmed from the appearance of Eu{sub 2}O{sub 3} as a minor phase in the XRD pattern. The estimation of crystallite size from XRD results matches closely with the results obtained from transmission electron microscopy. Further, these results show the formation of nanosized Eu-ZnO particles of average size around 60 nm stacked on each other. FTIRmore » studies show the presence of both Zn-O and Eu-O modes in the spectra supporting the results obtained from XRD. The interesting results obtained from photoluminescence (PL) measurements show the presence of both band edge emission in UV region and the defect emissions in violet, blue and green region. The appearance of {sup 5}D{sub 0}→{sup 7}F{sub J} transitions of Eu{sup 3+} ions in red region clearly suggests the possible occurrence of energy transfer between the energy states of ZnO host and Eu{sup 3+} ions.« less

An effective approach to study the biocompatibility of Fe3O4 nanoparticles, graphene and their nanohybrid composite

NASA Astrophysics Data System (ADS)

Singh, Ashwani Kumar; Singh, Pallavi; Verma, Rajiv Kumar; Yadav, Suresh; Singh, Kedar; Srivastava, Amit

2018-02-01

The present manuscript describes a simple, facile and effective solvothermal route to synthesize Fe3O4 nanoparticles (Fe3O4 NPs), reduced graphene oxide nanosheets (rGO NSs) and Fe3O4/reduced graphene oxide nanohybrid composite (Fe3O4/rGO nanohybrid composite) and subsequently examines their comparative biocompatibilities. The as-obtained Fe3O4 NPs, rGO NSs and Fe3O4/rGO nanohybrid composite have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Raman spectroscopy. The XRD studies and scanning electron microscope confirmed the proper phase formation and the surface morphology of the as-synthesized products, respectively. The Raman spectra of Fe3O4 NPs show the strongest peak at 673 cm-1 which can be assigned to A1g peak of bare Fe3O4 NPs and it complements the XRD studies. Furthermore, the increment in the I D/I G ratio in the Fe3O4/rGO nanohybrid composite suggests the creation of defects in graphene sheets due to strain caused by Fe3O4 NPs. The biocompatibility of these samples has been tested using Lung cancer cell line H1299 through MTT assay. The MTT assay reveals that the nanohybrid composite endows more biocompatible and effectiveness than rGO NSs and Fe3O4 NPs individually, as anti-proliferative agent for cancer treatment.

Best in show but not best shape: a photographic assessment of show dog body condition.

PubMed

Such, Z R; German, A J

2015-08-01

Previous studies suggest that owners often wrongly perceive overweight dogs to be in normal condition. The body shape of dogs attending shows might influence owners' perceptions, with online images of overweight show winners having a negative effect. This was an observational in silico study of canine body condition. 14 obese-prone breeds and 14 matched non-obese-probe breeds were first selected, and one operator then used an online search engine to identify 40 images, per breed, of dogs that had appeared at a major national UK show (Crufts). After images were anonymised and coded, a second observer subjectively assessed body condition, in a single sitting, using a previously validated method. Of 1120 photographs initially identified, 960 were suitable for assessing body condition, with all unsuitable images being from longhaired breeds. None of the dogs (0 per cent) were underweight, 708 (74 per cent) were in ideal condition and 252 (26 per cent) were overweight. Pugs, basset hounds and Labrador retrievers were most likely to be overweight, while standard poodles, Rhodesian ridgebacks, Hungarian vizslas and Dobermanns were least likely to be overweight. Given the proportion of show dogs from some breeds that are overweight, breed standards should be redefined to be consistent with a dog in optimal body condition. British Veterinary Association.

Synchrotron WAXS and XANES studies of silica (SiO2) powders synthesized from Indonesian natural sands

NASA Astrophysics Data System (ADS)

Muchlis, Khairanissa; Aini Fauziyah, Nur; Soontaranon, Siriwat; Limpirat, Wanwisa; Pratapa, Suminar

2017-01-01

In this study, we have investigated polymorphic silica (SiO2) powders using, Wide Angle X-ray Scattering (WAXS) and X-Ray Absorption Near Edge Spectroscopy (XANES), laboratory X-Ray Diffraction (XRD) instruments. The WAXS and XANES spectra were collected using synchrotron radiation at Synchrotron Light Research Institute (SLRI), Nakhon Ratchasima, Thailand. The silica powders were obtained by processing silica sand from Tanah Laut, South Kalimantan, Indonesia. Purification process of silica sand was done by magnetic separation and immersion with HCl. The purification step was needed to reduce impurity or undesirable non Si elements. Three polymorphs of silica were produced, i.e. amorphous phase (A), quartz (B), and cristobalite (C). WAXS profile for each phase was presented in terms of intensity vs. 2θ prior to analyses. Both XRD (λCuKα=1.54056 Å) and WAXS (λ=1.09 Å) patttern show that (1) A sample contains no crystallites, (2) B sample is monophasic, contains only quartz, and (3) C sample contains cristobalite and trydimite. XRD quantitative analysis using Rietica gave 98,8 wt% cristobalite, while the associated WAXS data provided 98.7 wt% cristobalite. Si K-edge XANES spectra were measured at energy range 1840 to 1920 eV. Qualitatively, the pre-edge and edge features for all phases are similar, but their main peaks in the post-edge region are different.

Studies on Electrical and Magnetic Properties of Mg-Substituted Nickel Ferrites

NASA Astrophysics Data System (ADS)

Chavan, Pradeep; Naik, L. R.; Belavi, P. B.; Chavan, Geeta; Ramesha, C. K.; Kotnala, R. K.

2017-01-01

The semiconducting polycrystalline ferrite materials with the general formula Ni1- x Mg x Fe2O4 were synthesized by using the solid state reaction method. X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectrographs, and atomic force microscopy techniques were utilized to study the structural parameters. XRD confirms the formation of single phase cubic spinel structure of the ferrites. The crystallite sizes of ferrites determined using the Debye-Scherer formula ranges from 0.963 μm to 1.069 μm. The cation distribution of ferrite shows that Mg2+ ions occupy a tetrahedral site ( A-site) and the Ni2+ ion occupy an octahedral site ( B-site) whereas Fe3+ ions occupies an octahedral as well as a tetrahedral site. The study of elastic parameters such as the longitudinal modulus, rigidity modulus, Young's modulus, bulk modulus, and Debye temperature were estimated using the FTIR technique. The decrease of direct current (DC) resistivity with increase in temperature indicates the semiconducting nature of ferrites. The dielectric constant as well as loss tangent decreases with increase in frequency, and at still higher frequencies, they are almost constant. This shows usual dielectric dispersion behavior attributed to the Maxwell-Wagner type of interfacial polarization and is in accordance with Koop's phenomenological theory. The linear increase of alternating current conductivity with increase of frequency shows the small polaron hopping type of conduction mechanism in all the ferrites. The magnetic properties such as saturation magnetization ( M s ), magnetic moment, coercivity, remnant magnetization ( M r ), and the ratio of M r /M s was estimated using the M-H loop.

Obesity in show cats.

PubMed

Corbee, R J

2014-12-01

Obesity is an important disease with a high prevalence in cats. Because obesity is related to several other diseases, it is important to identify the population at risk. Several risk factors for obesity have been described in the literature. A higher incidence of obesity in certain cat breeds has been suggested. The aim of this study was to determine whether obesity occurs more often in certain breeds. The second aim was to relate the increased prevalence of obesity in certain breeds to the official standards of that breed. To this end, 268 cats of 22 different breeds investigated by determining their body condition score (BCS) on a nine-point scale by inspection and palpation, at two different cat shows. Overall, 45.5% of the show cats had a BCS > 5, and 4.5% of the show cats had a BCS > 7. There were significant differences between breeds, which could be related to the breed standards. Most overweight and obese cats were in the neutered group. It warrants firm discussions with breeders and cat show judges to come to different interpretations of the standards in order to prevent overweight conditions in certain breeds from being the standard of beauty. Neutering predisposes for obesity and requires early nutritional intervention to prevent obese conditions. Journal of Animal Physiology and Animal Nutrition © 2014 Blackwell Verlag GmbH.

Title: Studies on drug switchability showed heterogeneity in methodological approaches: a scoping review.

PubMed

Belleudi, Valeria; Trotta, Francesco; Vecchi, Simona; Amato, Laura; Addis, Antonio; Davoli, Marina

2018-05-16

Several drugs share the same therapeutic indication, including those undergoing patent expiration. Concerns on the interchangeability are frequent in clinical practice, challenging the evaluation of switchability through observational research. To conduct a scoping review of observational studies on drug switchability to identify methodological strategies adopted to deal with bias and confounding. We searched PubMed, EMBASE, and Web of Science (updated 1/31/2017) to identify studies evaluating switchability in terms of effectiveness/safety outcomes or compliance. Three reviewers independently screened studies extracting all characteristics. Strategies to address confounding, particularly, previous drug use and switching reasons were considered. All findings were summarized in descriptive analyses. Thirty-two studies, published in the last 10 years, met the inclusion criteria. Epilepsy, cardiovascular and rheumatology were the most frequently represented clinical areas. 75% of the studies reported data on effectiveness/safety outcomes. The most frequent study design was cohort (65.6%) followed by case-control (21.9%) and self-controlled (12.5%). Case-control and case-crossover studies showed homogeneous methodological strategies to deal with bias and confounding. Among cohort studies, the confounding associated with previous drug use was addressed introducing variables in multivariate model (47.3%) or selecting only adherent patients (14.3%). Around 30% of cohort studies did not report reasons for switching. In the remaining 70%, clinical parameters or previous occurrence of outcomes were measured to identify switching connected with lack of effectiveness or adverse events. This study represents a starting point for researchers and administrators who are approaching the investigation and assessment of issues related to interchangeability of drugs. Copyright © 2018. Published by Elsevier Inc.

The study of the changes in the biochemical and mineral contents of bones of Catla catla due to lead intoxication.

PubMed

Palaniappan, P L R M; Krishnakumar, N; Vadivelu, M; Vijayasundaram, V

2010-02-01

In the present study, an attempt has been made to analyze the changes in the biochemical and mineral contents of lead-intoxicated bones of Catla catla at subchronic (15.5 ppm) exposure, and also to determine whether the effects of Pb intoxication can be reversed with the chelating agent meso 2, 3-dimercaptosuccinic acid (DMSA) on the bones of freshwater fingerlings Catla catla by using Fourier transform infrared (FT-IR) spectroscopy, X-ray diffraction (XRD), and atomic absorption spectrophotometer techniques. The FT-IR spectra of the lead-exposed bones show significant alteration in the biochemical constituents. The XRD analysis showed a decrease in crystallinity due to lead exposure. Further, the Ca, Mg, and P contents of the lead-exposed bones were less than those of the control group, and there was an increase in the mineral contents of the bones after DMSA treatment. In conclusion, the present study suggests that the subchronic lead exposure results in severe loss of bone minerals. The overall decrease in the FT-IR band intensity of Pb-exposed bones relative to the control indicates a decrease in the biochemical constituents like proteins and lipids. The increase in the band intensity after treatment with chelating agent DMSA indicates increased biochemical constituents, showing that the subchronic effects of lead can be reversed by DMSA. The amide I bands observed at 1654 cm(-1) in the present study suggest that the protein is dominated by alpha-helical structure.

Synthesis of BiFeO3 thin films by chemical solution deposition - Structural and magnetic studies

NASA Astrophysics Data System (ADS)

Angappane, S.; Kambhala, Nagaiah

2012-06-01

BiFeO3 thin films were deposited on Si (100) substrates by chemical solution deposition. A precursor solution of bismuth acetate and iron acetylacetonate dissolved in distilled water and acetic acid was spin coated on to silicon substrates at ambient conditions, followed by drying and annealing at 650 °C. The films were characterized by XRD and FESEM to study structural properties and morphology. The magnetic properties studied by SQUID magnetometer shows the ferromagnetic nature of the chemical solution deposited BiFeO3 films which are crucial for low cost device applications.

Structural and Electronic Properties Study of Colombian Aurifer Soils by Mössbauer Spectroscopy and X-ray Diffraction

NASA Astrophysics Data System (ADS)

Bustos Rodríguez, H.; Rojas Martínez, Y.; Oyola Lozano, D.; Pérez Alcázar, G. A.; Fajardo, M.; Mojica, J.; Molano, Y. J. C.

2005-02-01

In this work a study on gold mineral samples is reported, using optical microscopy, X-ray diffraction (XRD) and Mössbauer spectroscopy (MS). The auriferous samples are from the El Diamante mine, located in Guachavez-Nariño (Colombia) and were prepared by means of polished thin sections. The petrography analysis registered the presence, in different percentages that depend on the sample, of pyrite, quartz, arsenopyirite, sphalerite, chalcopyrite and galena. The XRD analysis confirmed these findings through the calculated cell parameters. One typical Rietveld analysis showed the following weight percent of phases: 85.0% quartz, 14.5% pyrite and 0.5% sphalerite. In this sample, MS demonstrated the presence of two types of pyrite whose hyperfine parameters are δ 1 = 0.280 ± 0.002 mm/s and Δ 1 = 0.642 ± 0.002 mm/s, δ 2 = 0.379 ± 0.002 mm/s and Δ 2 = 0.613 ± 0.002 mm/s.

Enhanced room temperature ferromagnetism in Ni doped SnO2 nanoparticles: A comprehensive study

NASA Astrophysics Data System (ADS)

Ahmed, Ateeq; Ali, T.; Naseem Siddique, M.; Ahmad, Abid; Tripathi, P.

2017-08-01

We emphasized on a detailed investigation of the structural, optical, and magnetic properties of pure and Ni-doped SnO2 nanoparticles (NPs) synthesized by a sol-gel process. An extensive structural study has been carried out using various characterization techniques. The X-ray Diffraction (XRD) spectra show the formation of the single phase tetragonal structure of pure and Ni-doped SnO2 NPs without any noticeable impurity phase such as NiO. XRD results indicate that the crystallite size of SnO2 is found to be decreased with Ni doping, which has also been confirmed by the Field Emission Scanning Electron Microscopy study. X-ray Photoelectron Spectroscopy (XPS) measurements displayed a clear sign for Ni2+ ions occupying the lattice sites of Sn4+ in the SnO2 host which also gives clear evidence for the formation of single phase Sn1-xNixO2 NPs. The optical analysis shows a significant decrease in the energy gap of SnO2, i.e., (from 3.71 eV to 3.28 eV) as Ni concentration increases which may be correlated with the core level valence band XPS analysis. Photoluminescence studies show that Ni doping creates oxygen vacancies due to dissimilar ionic radii of Ni2+ and Sn4+. Superconducting quantum interference device measurements revealed that the Ni doped SnO2 NPs exhibit strong ferromagnetic behavior at room temperature and this analysis has been well fitted with a simple relationship to find out magnetic parameters proposed by Stearns and Cheng et al. Hence, our results demonstrate that Ni-doping has strong impact on the structural, optical, and magnetic properties.

In situ Studies of Phase Evolution in (Pr1-xNdx)2NiO4 Electrodes with Various Interlayer Chemistries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dogdibegovic, Emir; Alabri, Nawf S.; Wright, Christopher J.

2017-07-24

The interest in Pr2NiO4 (PNO) electrode stems from the necessity to develop active and stable oxygen electrodes (1-6) for solid oxide fuel cells (SOFCs) (7-9). PNO is known for its highly active nature (7,8,10), originating from its superior oxygen ion diffusion, surface exchange coefficient (2,7,9-11) and structural flexibility over a wide temperature region (from 500 to 900oC) (3,12). PNO electrode, however, does undergo structural evolution to form a higher order phase (Pr3Ni2O7) and Pr6O11 (PrOx) (8). The structural change has been a major concern because it possibly links with the performance degradation over long-term operation (7,8) Conventional x-ray diffraction (XRD)more » has been extensively used to investigate the structural evolution in nickelates in the form of powders or planar electrodes (8,10). This method has two major limitations due to its low flux and low resolution: (1) it might overlook the presence of additional phases in the system, which is especially true for praseodymium nickelates where XRD diffraction patterns of higher order phase(s) (e.g. Pr3Ni2O7) may overlap with the parent PNO phase, making quantification challenging (8); and (2) the quantification of phase evolution in electrochemically operated PNO electrode may show major structural change with almost 100% of the parent phase transition from the conventional XRD analysis, while the transmission electron microscopy (TEM) studies clearly show the regions of preserved PNO phase (7).« less

Studies of tin-transition metal-carbon and tin-cobalt-transition metal-carbon negative electrode materials prepared by mechanical attrition

NASA Astrophysics Data System (ADS)

Ferguson, P. P.; Martine, M. L.; George, A. E.; Dahn, J. R.

Samples of Sn 30TM 30C 40 and of Sn 30Co 15TM 15C 40, with TM = 3d transition metals, were prepared by vertical-axis attritor milling. The structure and performance of these samples were studied by X-ray diffraction (XRD) and by electrochemical testing. The XRD patterns of Sn 30TM 30C 40 show an amorphous-like diffraction pattern only for the sample with TM = Co. The other prepared samples show broadened Bragg peaks of their main starting material, along with an amorphous-like background, even after 32 h of milling. Samples with TM = Co and TM = Ni show stable differential capacity versus potential plots and stable cycling for at least 100 cycles with reversible capacities of 425 and 250 mAh g -1, respectively. All samples prepared with 15 at.% Co show good capacity retention for at least 100 cycles ranging from 270 mAh g -1 for samples with TM = Ni to 500 mAh g -1 for samples with TM = Ti. The differential capacity versus potential plots for all the prepared Sn 30Co 15TM 15C 40 samples show similar structure to that of Sn 30Co 30C 40 except when TM = Cu. This shows the possibility of preparing tin-based negative electrode materials using a combination of cobalt and TM, especially if one looks to reduce the cobalt content.

Synthesis of polyimides from α,αʹ-bis(3-aminophenoxy)-p-xylene: Spectroscopic, single crystal XRD and thermal studies

NASA Astrophysics Data System (ADS)

Ashraf, Ahmad Raza; Akhter, Zareen; Simon, Leonardo C.; McKee, Vickie; Castel, Charles Dal

2018-05-01

The meta-catenated ether-based diamine monomer α,αʹ-bis(3-aminophenoxy)-p-xylene (3APX) was synthesized from dinitro precursor α,αʹ-bis(3-nitrophenoxy)-p-xylene (3NPX). FTIR, 1H and 13C NMR spectroscopic studies accompanied by elemental analysis were performed for structural elucidations of 3NPX and 3APX. The spatial orientations of 3APX were explored by single crystal X-ray diffraction analysis. Its crystal system was found to be monoclinic, adopting the space group P21/c. The synthesized diamine monomer (3APX) was used for preparation of new series of polyimides by reacting with three different dianhydrides (BTDA, ODPA, 6FDA). The relevant copolyimides were developed via incorporation of 4,4ʹ-methylenedianiline (MDA) in the backbone of afore-synthesized polyimides. The structures of polyimides and copolyimides were verified by FTIR and 1H NMR spectroscopic techniques. Their properties were evaluated by dynamic and isothermal TGA (nitrogen and air atmospheres) and WAXRD studies. Polyimides displayed significantly high thermal stability as their degradation started around 400 °C and it was improved further by execution of copolymerization strategy with MDA. The 5% weight loss temperature (T5) of polyimides under nitrogen atmosphere was in the range of 425-460 °C while for copolyimides it increased to 454-498 °C. Thermal decomposition in air was slower than nitrogen between 400 and 550 °C however it was accelerated above 550 °C. Isothermal TGA disclosed that copolyimides have the ability to endure elevated temperatures for extended period. WAXRD analysis showed the amorphous nature of polyimides and copolyimides.

A study of structural and mechanical properties of nano-crystalline tungsten nitride film synthesis by plasma focus

NASA Astrophysics Data System (ADS)

Hussnain, Ali; Singh Rawat, Rajdeep; Ahmad, Riaz; Hussain, Tousif; Umar, Z. A.; Ikhlaq, Uzma; Chen, Zhong; Shen, Lu

2015-02-01

Nano-crystalline tungsten nitride thin films are synthesized on AISI-304 steel at room temperature using Mather-type plasma focus system. The surface properties of the exposed substrate against different deposition shots are examined for crystal structure, surface morphology and mechanical properties using X-ray diffraction (XRD), atomic force microscope, field emission scanning electron microscope and nano-indenter. The XRD results show the growth of WN and WN2 phases and the development of strain/stress in the deposited films by varying the number of deposition shots. Morphology of deposited films shows the significant change in the surface structure with different ion energy doses (number of deposition shots). Due to the effect of different ion energy doses, the strain/stress developed in the deposited film leads to an improvement of hardness of deposited films.

Laboratory study of fungal bioreceptivity of different fractions of composite flooring tiles showing efflorescence.

PubMed

Masaphy, Segula; Lavi, Ido; Sultz, Stephan; Zabari, Limor

2014-06-01

Fungi can grow in extreme habitats, such as natural stone and mineral building materials, sometimes causing deterioration. Efflorescence-concentrated salt deposits-results from water movement through building material; it can damage masonry materials and other bricks. Fungal isolate KUR1, capable of growth on, and dissolution of stone chips composing terrazzo-type floor tiles, was isolated from such tiles showing fiber-like crystalline efflorescence. The isolate's ribosomal DNA sequences were 100 % identical to those of Nigrospora sphaerica. The ability of KUR1 to colonize and degrade the different stone chips composing the tiles was studied in axenic culture experiments. When exposed to each of the different mineral chip types composed of dolomite, calcite, or calcite-apatite mineral in low-nutrition medium, the fungus showed selective nutrient consumption, and different growth and stone mineral dissolution rates. Micromorphological examination of the fungus-colonized chips by electron microscopy showed the production of a fungal biofilm with thin films around the hyphae on the surface of the examined chips and disintegration of the calcite-apatite fraction. More than 70 % dissolution of the introduced powdered (<1 mm particle size) mineral was obtained within 10 days of incubation for the soft calcite-apatite fraction.

Rietveld-refinement and optical study of the Fe doped ZnO thin film by RF magnetron sputtering

NASA Astrophysics Data System (ADS)

Kumar, Arun; Dhiman, Pooja; Singh, M.

2017-05-01

Fe Doped ZnO Dilute Magnetic Semiconductor thin film prepared by RF magnetron sputtering on glass substrate and Influence of 3% Fe-doping on structural and Optical properties has been studied. The Rietveld-refinement analysis shows that Fe doping has a significant effect on crystalline structure, grain size and strain in the thin film. Two dimensional and three-dimensional atom probe tomography of the thin film shows that Fe ions are randomly distributed which is supported by Xray Diffraction (XRD). Fe-doping is found to effectively modify the band gap energy up to 3.5 eV.

In Situ XRD Studies of the Process Dynamics During Annealing in Cold-Rolled Copper

NASA Astrophysics Data System (ADS)

Dey, Santu; Gayathri, N.; Bhattacharya, M.; Mukherjee, P.

2016-12-01

The dynamics of the release of stored energy during annealing along two different crystallographic planes, i.e., {111} and {220}, in deformed copper have been investigated using in situ X-ray diffraction measurements at 458 K and 473 K (185 °C and 200 °C). The study has been carried out on 50 and 80 pct cold-rolled Cu sheets. The microstructures of the rolled samples have been characterized using optical microscopy and electron backscattered diffraction measurements. The microstructural parameters were evaluated from the X-ray diffractogram using the Scherrer equation and the modified Rietveld method. The stored energy along different planes was determined using the modified Stibitz formula from the X-ray peak broadening, and the bulk stored energy was evaluated using differential scanning calorimetry. The process dynamics of recovery and recrystallization as observed through the release of stored energy have been modeled as the second-order and first-order processes, respectively.

Contesting the “Nature” Of Conformity: What Milgram and Zimbardo's Studies Really Show

PubMed Central

Haslam, S. Alexander; Reicher, Stephen. D.

2012-01-01

Understanding of the psychology of tyranny is dominated by classic studies from the 1960s and 1970s: Milgram's research on obedience to authority and Zimbardo's Stanford Prison Experiment. Supporting popular notions of the banality of evil, this research has been taken to show that people conform passively and unthinkingly to both the instructions and the roles that authorities provide, however malevolent these may be. Recently, though, this consensus has been challenged by empirical work informed by social identity theorizing. This suggests that individuals' willingness to follow authorities is conditional on identification with the authority in question and an associated belief that the authority is right. PMID:23185132

10. INTERIOR VIEW SHOWING MOUNTINGS FROM TUNING DEVICE. VIEW SHOWS ...

Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

10. INTERIOR VIEW SHOWING MOUNTINGS FROM TUNING DEVICE. VIEW SHOWS COPPER SHEETING ON WALLS. - Chollas Heights Naval Radio Transmitting Facility, Helix House, 6410 Zero Road, San Diego, San Diego County, CA

Potentiodynamic Polarization Studies and Surface Chemical Composition of Bismuth Titanate (Bi x Ti y O z ) Films Produced through Radiofrequency Magnetron Sputtering.

PubMed

Alfonso, José E; Olaya, Jhon J; Pinzón, Manuel J; Marco, José F

2013-10-08

The applications of Bismuth Titanate (Bi x Ti y O z ) materials have been focused on their electronic and optical properties, but with respect to the use of these compounds in applications like corrosion resistance, have been very few or nonexistent. For this reason, in the present investigation Bi x Ti y O z thin films were deposited using RF magnetron sputtering onto silicon wafers, stainless steel 316L, and titanium alloy (Ti₆Al₄V) substrates, in order to carry out a study of the corrosion behavior of this compound. The structural properties of the coatings were studied through X-ray diffraction (XRD), the morphology was determined using Scanning Electron Microscopy (SEM), the corrosion resistance behavior of the coated and uncoated substrates was evaluated via the Potentiodynamic Polarization technique, and surface chemical composition was evaluated through X-ray photoelectron spectroscopy (XPS). The XRD results indicated that the films were amorphous. The SEM micrographs showed that the deposited films were homogeneous, but in some cases there were cracks. The potentiodynamic polarization technique showed that the corrosion current in the coated substrates decreased by an order of two magnitudes with respect to the uncoated substrates, but in both cases the corrosion mechanism was pitting due to the pores in the film. The XPS analysis shows that the deposited films contain both Bi 3+ and Ti 4+ .

A pilot study in non-human primates shows no adverse response to intravenous injection of quantum dots.

PubMed

Ye, Ling; Yong, Ken-Tye; Liu, Liwei; Roy, Indrajit; Hu, Rui; Zhu, Jing; Cai, Hongxing; Law, Wing-Cheung; Liu, Jianwei; Wang, Kai; Liu, Jing; Liu, Yaqian; Hu, Yazhuo; Zhang, Xihe; Swihart, Mark T; Prasad, Paras N

2012-05-20

Quantum dots have been used in biomedical research for imaging, diagnostics and sensing purposes. However, concerns over the cytotoxicity of their heavy metal constituents and conflicting results from in vitro and small animal toxicity studies have limited their translation towards clinical applications. Here, we show in a pilot study that rhesus macaques injected with phospholipid micelle-encapsulated CdSe/CdS/ZnS quantum dots do not exhibit evidence of toxicity. Blood and biochemical markers remained within normal ranges following treatment, and histology of major organs after 90 days showed no abnormalities. Our results show that acute toxicity of these quantum dots in vivo can be minimal. However, chemical analysis revealed that most of the initial dose of cadmium remained in the liver, spleen and kidneys after 90 days. This means that the breakdown and clearance of quantum dots is quite slow, suggesting that longer-term studies will be required to determine the ultimate fate of these heavy metals and the impact of their persistence in primates.

Mössbauer and XRD characterization of the effect of heat treatment and the tribological test on the physical and mechanical properties of a Fe-Mn-Al-C alloy

NASA Astrophysics Data System (ADS)

Ramos, J.; Piamba, J. F.; Sanchez, H.; Pérez Alcazar, G. A.

2017-11-01

In this study, a Fe-29.0Mn-6.0Al-0.9C-1.8Mo-1.6Si-0.4Cu (Wt. %) alloy was prepared in an induction furnace. The as-cast sample was submitted to homogenization at 1050 °C over 8 hours, which was followed by quenching, and an aging heat treatment at 500 °C for 12 h. Wear tests were performed by using a Pin on Disk Tribometer (ASTM G99) at room temperature to evaluate the mass loss. Optical Microscopy, X-Ray Diffraction, and Transmission Mossbauer Spectroscopy were used to characterize the microstructure and structural properties of the samples. The obtained microstructure of the heat-treated samples was of the austenitic type, and their XRD patterns were refined with the lines of the austenite, martensite, galaxite, and FeO structures. Mössbauer spectra of powders, obtained from the surface of the samples, showed the presence of a broad doublet, which corresponded to the disordered austenite; and a small hyperfine magnetic field distribution associated with the disordered and ferromagnetic martensite. After the tribology test, the surface of the sample was examined, and it was obderved that the austenite, martensite, and galaxite phases were present. The martensite quantity increased and, those of galaxite and austenite decreased, but that of austenite appeared to have larger lattice parameter. The decrease in the galaxite content was a direct consequence of the wear test, which removed matter from the sample surface. The appearance of additional martensite was due to the transformation of the austenite by mechanical work. The additional presence of a new austenite with a bigger lattice parameter and of the Fe oxide was the consequence of the heating process of the sample during the tribological test. The Mossbauer spectrum of this sample confirms the increase of the martensite content. The mechanical properties increased with the heat treatment.

A study of optical, mechanical and electrical properties of poly(methacrylic acid)/TiO2 nanocomposite

NASA Astrophysics Data System (ADS)

AL-Baradi, Ateyyah M.; Al-Shehri, Samar F.; Badawi, Ali; Merazga, Amar; Atta, A. A.

2018-06-01

This work is concerned with the study of the effect of titanium dioxide (TiO2) nanofillers on the optical, mechanical and electrical properties of poly(methacrylic acid) (PMAA) networks as a function of TiO2 concentration and crosslink density. The structure of the prepared samples was investigated by X-ray diffractometry (XRD) and Transmittance Electron Microscope (TEM). XRD results showed a single phase for the nanocomposites indicating that no large TiO2 aggregates in the polymer matrix. The optical properties of the prepared samples including the absorption, transmittance, energy band gap and refractive index were explored using Spectrophotometer. These measurements showed that there is a red-shift in the absorption caused by the increase of TiO2 concentration. However, the crosslink density in the polymer plays no role in changing the absorption. The energy band gap (Eg) decreases with increasing the concentration of TiO2 in the polymer matrix; whereas Eg increases with increasing the crosslink density. Moreover, the mechanical properties of PMAA/TiO2 nanocomposites by Dynamic Mechanical Analysis (DMA) showed that the viscoelasticity of PMAA decreases with adding TiO2 nanoparticles and the glass transition temperature (Tg) was also found to drop from 130 °C to 114 °C. Finally, the DC conductivity of the obtained systems was found to increase with increasing TiO2 nanoparticles in the matrix.

In situ Studies of Phase Evolution in (Pr 1-x Nd x) 2 NiO 4 Electrodes with Various Interlayer Chemistries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dogdibegovic, Emir; Alabri, Nawf Saif; Wright, Christopher J.

The interest in Pr2NiO4 (PNO) electrode stems from the necessity to develop active and stable oxygen electrodes (1-6) for solid oxide fuel cells (SOFCs) (7-9). PNO is known for its highly active nature (7,8,10), originating from its superior oxygen ion diffusion, surface exchange coefficient (2,7,9-11) and structural flexibility over a wide temperature region (from 500 to 900oC) (3,12). PNO electrode, however, does undergo structural evolution to form a higher order phase (Pr3Ni2O7) and Pr6O11 (PrOx) (8). The structural change has been a major concern because it possibly links with the performance degradation over long-term operation (7,8) Conventional x-ray diffraction (XRD)more » has been extensively used to investigate the structural evolution in nickelates in the form of powders or planar electrodes (8,10). This method has two major limitations due to its low flux and low resolution: (1) it might overlook the presence of additional phases in the system, which is especially true for praseodymium nickelates where XRD diffraction patterns of higher order phase(s) (e.g. Pr3Ni2O7) may overlap with the parent PNO phase, making quantification challenging (8); and (2) the quantification of phase evolution in electrochemically operated PNO electrode may show major structural change with almost 100% of the parent phase transition from the conventional XRD analysis, while the transmission electron microscopy (TEM) studies clearly show the regions of preserved PNO phase (7).« less

Microstructure of hydrogenated Mg2Ni studied by SANS

NASA Astrophysics Data System (ADS)

Mori, K.; Sugiyama, M.; Iwase, K.; Kawabe, S.; Onodera, Y.; Itoh, K.; Otomo, T.; Fukunaga, T.

2010-10-01

X-ray powder diffraction (XRD) and small-angle neutron scattering (SANS) experiments were carried out for the hydrogenated and duterated Mg2Ni, respectively. According to the results of XRD experiments, both of them coexisted with unhydrogenated (or undeuterated) Mg2Ni in the hydrogen absorbing cycle. Furthermore, in the SANS experiments, a slope of SANS curve, I(Q), was roughly evaluated by using the following power law: I(Q) propto Q-m, where Q is the magnitude of the scattering vector, and m can be equated with a fractal dimensionality, DS (= 6 - m). In conclusion, the hydrogenated and duterated Mg2Ni showed DS~ 3 and ~ 2, respectively. The significant difference between DS's can be understood by considering the scattering length densities, ρ, of Mg2Ni, Mg2NiH4, and Mg2NiD4.

X-ray diffraction, Raman, and photoacoustic studies of ZnTe nanocrystals

NASA Astrophysics Data System (ADS)

Ersching, K.; Campos, C. E. M.; de Lima, J. C.; Grandi, T. A.; Souza, S. M.; da Silva, D. L.; Pizani, P. S.

2009-06-01

Nanocrystalline ZnTe was prepared by mechanical alloying. X-ray diffraction (XRD), energy dispersive spectroscopy, Raman spectroscopy, and photoacoustic absorption spectroscopy techniques were used to study the structural, chemical, optical, and thermal properties of the as-milled powder. An annealing of the mechanical alloyed sample at 590 °C for 6 h was done to investigate the optical properties in a defect-free sample (close to bulk form). The main crystalline phase formed was the zinc-blende ZnTe, but residual trigonal tellurium and hexagonal ZnO phases were also observed for both as-milled and annealed samples. The structural parameters, phase fractions, average crystallite sizes, and microstrains of all crystalline phases were obtained from Rietveld analyses of the X-ray patterns. Raman results corroborate the XRD results, showing the longitudinal optical phonons of ZnTe (even at third order) and those modes of trigonal Te. Nonradiative surface recombination and thermal bending heat transfer mechanisms were proposed from photoacoustic analysis. An increase in effective thermal diffusivity coefficient was observed after annealing and the carrier diffusion coefficient, the surface recombination velocity, and the recombination time parameters remained the same.

Watching a food-related television show and caloric intake. A laboratory study.

PubMed

Bodenlos, Jamie S; Wormuth, Bernadette M

2013-02-01

Television watching has been positively associated with overeating and obesity. How popular food-related television shows affects eating behavior has not been examined. An experimental study was conducted to examine how exposure to a food-related television program affects amount and type of food consumed in adults (N=80). Participants were randomized to watch a cooking or nature television program and were then presented with 800 total calories of chocolate covered candies, cheese curls, and carrots. Food was weighed before and after the ad libitum eating session to determine amount consumed. After controlling for dietary restraint, hunger and food preference, significantly more chocolate covered candies were consumed among individuals who watched the cooking program compared to the nature program. No significant differences between conditions were found for overall caloric intake or for cheese curl or carrot consumption. Findings suggest that watching food-related television programs may affect eating behavior and has implications for obesity prevention and intervention efforts. Copyright © 2012 Elsevier Ltd. All rights reserved.

Encapsulation of boswellic acid with β- and hydroxypropyl-β-cyclodextrin: Synthesis, characterization, in vitro drug release and molecular modelling studies

NASA Astrophysics Data System (ADS)

Tambe, Amruta; Pandita, Nancy; Kharkar, Prashant; Sahu, Niteshkumar

2018-02-01

Boswellic acids (BAs) are a group of pentacyclic triterpenes present in gum-resin of Boswellia serrata. They are well known for their anti-inflammatory, hypolipidemic, immunomodulatory and anti-tumor activity, but they have poor aqueous solubility and limited bioavailability. In order to enhance their aqueous solubility, inclusion complexes of BAs with β-cyclodextrin (β-CD) and hydroxypropyl-β-cyclodextrin (HP-β-CD) were synthesized and their drug release profiles were studied. Molecular associations of β-CD and HP-β-CD with BAs were investigated by phase solubility studies. The stability constants were found to be 380.2 and 145.9 M-1 for BA: β-CD and BA: HP-β-CD inclusion complexes, respectively with AN- type curve. BA: β-CD and BA: HP-β-CD inclusion complexes were synthesized using kneading (KN), co-precipitation (CP) and solvent evaporation (SE) methods in 1:1 as well as 1:2 ratios. Further these were characterized by Fourier transform infrared (FTIR) spectrophotometry, Powder X-ray Diffraction (P-XRD) and Differential scanning calorimetric (DSC) analysis. FTIR analysis showed shifting of frequencies in complexes as compared to CDs and BAs. P-XRD data obtained for BA: β-CD complexes synthesized by CP and SE methods showed amorphous pattern. Also, DSC analysis showed a change in thermal behaviour for synthesized complexes. In vitro drug release studies of BA: β-CD complexes showed enhanced release with 1:2 complexes than 1:1 complexes at pH 1.2 and pH 6.8. Similarly, drug release enhancement was observed more with BA: HP-β-CD complexes in 1:2 ratio than 1:1. To understand the interaction of BAs with CD cavity molecular modelling studies were performed which favored 1:2 complex formation over 1:1 complexes. The study thus highlights that CDs can be used for solubility and dissolution enhancement of BAs.

Experimental study on the effect of calcination on the volcanic ash activity of diatomite

NASA Astrophysics Data System (ADS)

Xiao, Liguang; Pang, Bo

2017-09-01

The volcanic ash activity of diatomite was studied under the conditions of aerobic calcination and vacuum calcination by the combined water rate method, it was characterized by XRD, BET and SEM. The results showed that the volcanic ash activity of diatomite under vacuum conditions was higher than that of aerobic calcination, 600°C vacuum calcination 2h, the combined water rate of diatomite-Ca(OH)2-H2O system was increased from 6.24% to 71.43%, the volcanic ash activity reached the maximum value, the specific surface

28. MAP SHOWING LOCATION OF ARVFS FACILITY AS BUILT. SHOWS ...

Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

28. MAP SHOWING LOCATION OF ARVFS FACILITY AS BUILT. SHOWS LINCOLN BOULEVARD, BIG LOST RIVER, AND NAVAL REACTORS FACILITY. F.C. TORKELSON DRAWING NUMBER 842-ARVFS-101-2. DATED OCTOBER 12, 1965. INEL INDEX CODE NUMBER: 075 0101 851 151969. - Idaho National Engineering Laboratory, Advanced Reentry Vehicle Fusing System, Scoville, Butte County, ID

Synthesis, structural, DFT studies, docking and antibacterial activity of a xanthene based hydrazone ligand

NASA Astrophysics Data System (ADS)

Naseem, Saira; Khalid, Muhammad; Tahir, Muhammad Nawaz; Halim, Mohammad A.; Braga, Ataualpa A. C.; Naseer, Muhammad Moazzam; Shafiq, Zahid

2017-09-01

Herein, we present the synthesis of novel xanthene-based hydrazone (1). The chemical structure of 1 was resolved using spectroscopic techniques such as NMR, FT-IR, UV-VIS and X-ray crystallographic approaches. X-ray diffraction analysis shows that the compound (1) crystallizes in triclinic crystal lattice with the Pbar1 space group and diffused to form multi-layered structure due to non-covalent interactions such as intramolecular hydrogen bonding (H.B). In addition to experimental investigation, density functional theory (DFT) calculation with M06-2X/6-31G(d,p) and B3LYP/6-31G(d,p) level of theories was performed on compound (1) to obtain optimized geometry, spectroscopic and electronic properties. DFT optimized geometry shows good agreement with the experimental XRD structure. The hyper conjugative interactions and hydrogen bonding network are responsible for the stability of compound (1) as revealed by natural bond orbital (NBO) calculation. Moreover, hydrogen bonding network in the dimer is confirmed by FT-IR and thermodynamic studies showing excellent agreement with XRD and NBO findings. TD-DFT/UV-VIS analysis provides insight that maximum excitation is found in 1 which shows good agreement with experimental UV-VIS result. The global reactivity parameters are calculated using the energies of frontier molecular orbitals also disclosed that the compound is more stable might be due to hydrogen bonding network. Experimental and molecular docking studies indicated that this compound has anti-bacterial and anti-diabetic properties. The binding affinity of this compound against the multidrug efflux pump subunit AcrB OS=Escherichia coli (strain K12) and Human Pancreatic Alpha-Amylase is -9.2 and -10.00 kcal/mol which are higher than the control drugs. Pi-Pi, Pi-anaion, amide-pi and pi-alkyl bonds play key role in drug-protein complexes.

Properties of Gd{sub 2}O{sub 3} nanoparticles studied by hyperfine interactions and magnetization measurements

DOE Office of Scientific and Technical Information (OSTI.GOV)

Correa, E. L., E-mail: eduardo.correa@usp.br; Bosch-Santos, B.; Cavalcante, F. H. M.

2016-05-15

The magnetic behavior of Gd{sub 2}O{sub 3} nanoparticles, produced by thermal decomposition method and subsequently annealed at different temperatures, was investigated by magnetization measurements and, at an atomic level, by perturbed γ − γ angular correlation (PAC) spectroscopy measuring hyperfine interactions at {sup 111}In({sup 111}Cd) probe nuclei. Nanoparticle structure, size and shape were characterized by X-ray diffraction (XRD) and Transmission Electron Microscopy (TEM). Magnetization measurements were carried out to characterize the paramagnetic behavior of the samples. XRD results show that all samples crystallize in the cubic-C form of the bixbyite structure with space group Ia3. TEM images showed that particlesmore » annealed at 873 K present particles with highly homogeneous sizes in the range from 5 nm to 10 nm and those annealed at 1273 K show particles with quite different sizes from 5 nm to 100 nm, with a wide size distribution. PAC and magnetization results show that samples annealed at 873 and 1273 K are paramagnetic. Magnetization measurements show no indication of blocking temperatures for all samples down to 2 K and the presence of antiferromagnetic correlations.« less

Structural, morphological and gas sensing study of zinc doped tin oxide nanoparticles synthesized via hydrothermal technique

NASA Astrophysics Data System (ADS)

Singh, Davender; Kundu, Virender Singh; Maan, A. S.

2016-07-01

The pure and Zn-doped SnO2 nanoparticles were prepared successfully by hydrothermal route on large scale having different doping concentration of zinc from 0 to 0.20%. The calcined nanoparticles were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM) for structural and morphological studies. XRD analyses reveal that the nanoparticles of these doping concentrations are polycrystalline in nature and existed as tetragonal rutile structure, SEM study of images confirms the existence of very small, homogeneously distributed, and spherical nanoparticles. The particles size of the nanoparticles was calculated by Scherrer formula and was found in the range of 9-21 nm. The presence of dopant (i.e. zinc) and formation of Sn-O phase and hydrous nature of Zn-doped SnO2 nanoparticles are confirmed by EDX and FTIR study. The gas sensing properties of pure and Zn-doped SnO2 nanoparticles were investigated for various concentrations of methanol, ethanol and acetone at different operating temperatures and it has been found that with doping concentration of zinc (x = 0.20%) shows the maximum response 78% to methanol, 65% to ethanol and 62% to acetone respectively at different operating temperature within the measurement limit for a concentration of 100 ppm of each gases.

Material rhetoric: spreading stones and showing bones in the study of prehistory.

PubMed

Van Reybrouck, David; de Bont, Raf; Rock, Jan

2009-06-01

Since the linguistic turn, the role of rhetoric in the circulation and the popular representation of knowledge has been widely accepted in science studies. This article aims to analyze not a textual form of scientific rhetoric, but the crucial role of materiality in scientific debates. It introduces the concept of material rhetoric to understand the promotional regimes in which material objects play an essential argumentative role. It analyzes the phenomenon by looking at two students of prehistory from nineteenth-century Belgium. In the study of human prehistory and evolution, material data are either fairly abundant stone tools or very scarce fossil bones. These two types of material data stand for two different strategies in material rhetoric. In this article, the first strategy is exemplified by Aimé Rutot, who gathered great masses of eoliths (crudely chipped stones which he believed to be prehistoric tools). The second strategy is typified by the example of Julien Fraipont, who based his scientific career on only two Neanderthal skeletons. Rutot sent his "artifacts" to a very wide audience, while Fraipont showed his skeletons to only a few selected scholars. Unlike Rutot, however, Fraipont was able to monitor his audience's interpretation of the finds by means of personal contacts. What an archaeologist gains in reach, he or she apparently loses in control. In this article we argue that only those scholars who find the right balance between the extremes of reach and control will prove to be successful.

Spectroscopic characterization approach to study surfactants effect on ZnO 2 nanoparticles synthesis by laser ablation process

NASA Astrophysics Data System (ADS)

Drmosh, Q. A.; Gondal, M. A.; Yamani, Z. H.; Saleh, T. A.

2010-05-01

Zinc peroxide nanoparticles having grain size less than 5 nm were synthesized using pulsed laser ablation in aqueous solution in the presence of different surfactants and solid zinc target in 3% H 2O 2. The effect of surfactants on the optical and structure of ZnO 2 was studied by applying different spectroscopic techniques. Structural properties and grain size of the synthesized nanoparticles were studied using XRD method. The presence of the cubic phase of zinc peroxide in all samples was confirmed with XRD, and the grain sizes were 4.7, 3.7, 3.3 and 2.8 nm in pure H 2O 2, and H 2O 2 mixed with SDS, CTAB and OGM respectively. For optical characterization, FTIR transmittance spectra of ZnO 2 nanoparticles prepared with and without surfactants show a characteristic ZnO 2 absorption at 435-445 cm -1. FTIR spectrum revealed that the adsorbed surfactants on zinc peroxide disappeared in case of CTAB and OGM while it appears in case of SDS. This could be due to high critical micelles SDS concentration comparing with others which is attributed to the adsorption anionic nature of this surfactant. Both FTIR and UV-vis spectra show a red shift in the presence of SDS and blue shift in the presence of CTAB and OGM. The blue shift in the absorption edge indicates the quantum confinement property of nanoparticles. The zinc peroxide nanoparticles prepared in additives-free media was also characterized by Raman spectra which show the characteristic peaks at 830-840 and 420-440 cm -1.

Microstructural studies of nanocrystalline α-alumina powder produced from Al13-cluster

NASA Astrophysics Data System (ADS)

Harun Al Rashid Megat Ahmad, Megat; Aziz Mohamed, Abdul; Ibrahim, Azmi; Seman Mahmood, Che; Giri Rachman Putra, Edy; Jamro, Rafhayudi; Kasim, Razali; Rawi Muhammad Zin, Muhammad

2007-12-01

Nanocrystalline alumina powder was produced from calcinations of Al13-oxalate precipitates at 1100 °C. A nearly normal distribution of agglomerated alumina powder was obtained with an average particle size of about 1 μm. XRD measurement confirmed that the alumina produced was of high purity and crystalline α-phase. Microstructural features of both the precipitates and alumina obtained were studied using the small angle neutron scattering (SANS) technique. SANS examinations show the formation of microstructures in the alumina powder of mass fractals type with dimension of ˜2.8 indicative of low intra-granular porosity.

COMPARATIVE STUDY OF RADON AND THORON MEASUREMENTS IN FOUR ROMANIAN SHOW CAVES.

PubMed

Burghele, B D; Cucos, A; Papp, B; Dicu, T; Pressyanov, D; Dimitrov, D; Dimitrova, I; Constantin, S

2017-11-01

Measurements have been carried out using four types of passive detectors in four of the most popular show caves in Romania. Three types of detectors (RSKS, RadTrak and CD) were used for radon measurements and two (Raduet and CD) for thoron measurement. Activity concentrations in air were measured in the same locations for two seasons, autumn and winter. Measured values for the different caves varied between below detection limit (5 Bq m-3) and 4024 Bq m-3 for radon and from below 10 to 583 Bq m-3 for thoron. The results indicate a very good correlation between RSKS and RadTrak detectors (r = 0.96). The most significant difference between radon concentrations measured with different types of detectors (RSKS and CD) was higher than 150%. The study suggests that the activity concentration of radon in caves, measured using track detectors, could not be influenced by the type of detector used if the microclimate factor is acknowledged. © The Author 2017. Published by Oxford University Press. All rights reserved. For Permissions, please email: journals.permissions@oup.com.

Neural Correlates of Empathy with Pain Show Habituation Effects. An fMRI Study

PubMed Central

Preis, Mira A.; Kröner-Herwig, Birgit; Schmidt-Samoa, Carsten; Dechent, Peter; Barke, Antonia

2015-01-01

Background Neuroimaging studies have demonstrated that the actual experience of pain and the perception of another person in pain share common neural substrates, including the bilateral anterior insular cortex and the anterior midcingulate cortex. As many fMRI studies include the exposure of participants to repeated, similar stimuli, we examined whether empathic neural responses were affected by habituation and whether the participants' prior pain experience influenced these habituation effects. Method In 128 trials (four runs), 62 participants (31 women, 23.0 ± 4.2 years) were shown pictures of hands exposed to painful pressure (pain pictures) and unexposed (neutral pictures). After each trial, the participants rated the pain of the model. Prior to the experiment, participants were either exposed to the same pain stimulus (pain exposure group) or not (touch exposure group). In order to assess possible habituation effects, linear changes in the strength of the BOLD response to the pain pictures (relative to the neutral pictures) and in the ratings of the model’s pain were evaluated across the four runs. Results Although the ratings of the model’s pain remained constant over time, we found neural habituation in the bilateral anterior/midinsular cortex, the posterior midcingulate extending to dorsal posterior cingulate cortex, the supplementary motor area, the cerebellum, the right inferior parietal lobule, and the left superior frontal gyrus, stretching to the pregenual anterior cingulate cortex. The participant’s prior pain experience did neither affect their ratings of the model’s pain nor their maintenance of BOLD activity in areas associated with empathy. Interestingly, participants with high trait personal distress and fantasy tended to show less habituation in the anterior insula. Conclusion Neural structures showed a decrease of the BOLD signal, indicating habituation over the course of 45 minutes. This can be interpreted as a neuronal mechanism

A Pilot Study of Reasons and Risk Factors for "No-Shows" in a Pediatric Neurology Clinic.

PubMed

Guzek, Lindsay M; Fadel, William F; Golomb, Meredith R

2015-09-01

Missed clinic appointments lead to decreased patient access, worse patient outcomes, and increased healthcare costs. The goal of this pilot study was to identify reasons for and risk factors associated with missed pediatric neurology outpatient appointments ("no-shows"). This was a prospective cohort study of patients scheduled for 1 week of clinic. Data on patient clinical and demographic information were collected by record review; data on reasons for missed appointments were collected by phone interviews. Univariate and multivariate analyses were conducted using chi-square tests and multiple logistic regression to assess risk factors for missed appointments. Fifty-nine (25%) of 236 scheduled patients were no-shows. Scheduling conflicts (25.9%) and forgetting (20.4%) were the most common reasons for missed appointments. When controlling for confounding factors in the logistic regression, Medicaid (odds ratio 2.36), distance from clinic, and time since appointment was scheduled were associated with missed appointments. Further work in this area is needed. © The Author(s) 2014.

Obesity in show dogs.

PubMed

Corbee, R J

2013-10-01

Obesity is an important disease with a growing incidence. Because obesity is related to several other diseases, and decreases life span, it is important to identify the population at risk. Several risk factors for obesity have been described in the literature. A higher incidence of obesity in certain breeds is often suggested. The aim of this study was to determine whether obesity occurs more often in certain breeds. The second aim was to relate the increased prevalence of obesity in certain breeds to the official standards of that breed. To this end, we investigated 1379 dogs of 128 different breeds by determining their body condition score (BCS). Overall, 18.6% of the show dogs had a BCS >5, and 1.1% of the show dogs had a BCS>7. There were significant differences between breeds, which could be correlated to the breed standards. It warrants firm discussions with breeders and judges in order to come to different interpretations of the standards to prevent overweight conditions from being the standard of beauty. © 2012 Blackwell Verlag GmbH.

In-State and Interstate Associations Between Gun Shows and Firearm Deaths and Injuries: A Quasi-experimental Study.

PubMed

Matthay, Ellicott C; Galin, Jessica; Rudolph, Kara E; Farkas, Kriszta; Wintemute, Garen J; Ahern, Jennifer

2017-12-19

Gun shows are an important source of firearms, but no adequately powered studies have examined whether they are associated with increases in firearm injuries. To determine whether gun shows are associated with short-term increases in local firearm injuries and whether this association differs by the state in which the gun show is held. Quasi-experimental. California. Persons in California within driving distance of gun shows. Gun shows in California and Nevada between 2005 and 2013 (n = 915 shows) and rates of firearm-related deaths, emergency department visits, and inpatient hospitalizations in California. Compared with the 2 weeks before, postshow firearm injury rates remained stable in regions near California gun shows but increased from 0.67 injuries (95% CI, 0.55 to 0.80 injuries) to 1.14 injuries (CI, 0.97 to 1.30 injuries) per 100 000 persons in regions near Nevada shows. After adjustment for seasonality and clustering, California shows were not associated with increases in local firearm injuries (rate ratio [RR], 0.99 [CI, 0.97 to 1.02]) but Nevada shows were associated with increased injuries in California (RR, 1.69 [CI, 1.16 to 2.45]). The pre-post difference was significantly higher for Nevada shows than California shows (ratio of RRs, 1.70 [CI, 1.17 to 2.47]). The Nevada association was driven by significant increases in firearm injuries from interpersonal violence (RR, 2.23 [CI, 1.01 to 4.89]) but corresponded to a small increase in absolute numbers. Nonfirearm injuries served as a negative control and were not associated with California or Nevada gun shows. Results were robust to sensitivity analyses. Firearm injuries were examined only in California, and gun show occurrence was not randomized. Gun shows in Nevada, but not California, were associated with local, short-term increases in firearm injuries in California. Differing associations for California versus Nevada gun shows may be due to California's stricter firearm regulations. National

X-ray diffraction and X-ray K absorption near edge studies of copper (II) complexes with amino acids

NASA Astrophysics Data System (ADS)

Sharma, P. K.; Mishra, Ashutosh; Malviya, Varsha; Kame, Rashmi; Malviya, P. K.

2017-05-01

Synthesis of copper (II) complexes [CuL1L2X].nH2O, where n=1, 2,3 (X=Cl,Br,NO3) (L1is 2,2’-bipyridine and L2 is L-tyrosine) by the chemical root method. The XRD data for the samples have been recorded. EXAFS spectra have also been recorded at the K-edge of Cu using the dispersive beam line BL-8 at 2.5 Gev Indus-2 Synchrotron radiation source at RRCAT, Indore, India. XRD and EXAFS data have been analysed using the computer software. X-ray diffraction studies of all complexes indicate their crystalline nature. Lattice parameter, bond length, particle size have been determined from XRD data.

Characterization of Serpentine Samples from the Coast Range Ophiolite Microbial Observatory with μ-FTIR and XRD. ­­

NASA Astrophysics Data System (ADS)

Sousa, A.; Cardace, D.

2017-12-01

Serpentinizing systems hold much promise as potentially habitable environments in diverse planetary settings. They involve abundant and simple ingredients (i.e., the mineral olivine, liquid water), support subsurface microbial communities on Earth (Crespo-Medina et al. 2014; Suzuki et al. 2014; Kelley et al. 2005) and are thought to occur elsewhere in our solar system such as Mars (Schulte et al. 2006; Ehlmann et al. 2010)and possibly ocean worlds (Waite et al. 2017; Vance 2009). Although geochemical and microbial data collection continues in serpentinizing systems, the identification and resolution of potential biosignatures in serpentinites are not yet clear. Specifically, the micro-scale mineralogical contexts in which cell fragments or biofilm residues may be formed and preserved is lacking. Here we report preliminary transmission and reflection mode μ-FTIR spectral maps and XRD diffractograms, obtained with instruments relevant to robotic exploration missions (Blake et al. 2012; Igisu et al. 2009; Leroi et al. 2009). Samples analyzed include ultramafic rock and constituent mineral standards (e.g., olivine) and rocks collected from near surface sites associated with the NASA Astrobiology Institute-funded initiative, the Coast Range Ophiolite Microbial Observatory (CROMO), in Lower Lake, CA (Cardace et al. 2013). These new results provide co-registered, complementary data on astrobiologically important rock and mineral phases related to serpentinization (Crespo-Medina et al. 2014; Twing et al. 2017). Future work will leverage this data set in microbial colonization experiments aimed at parsing background organic loads in serpentinites from surficial/fracture-localized modern biofilm signatures.

Preparation and crystalline studies of PVDF hybrid composites

NASA Astrophysics Data System (ADS)

Chethan P., B.; Renukappa, N. M.; Sanjeev, Ganesh

2018-04-01

The conducting polymer composites have become increasingly important for electrical and electronic applications due to their flexibility, easy of processing, high strength and low cost. A flexible conducting polymer hybrid composite was prepared by melt mixing of nickel coated multi-walled carbon nanotubes (Ni-MWNT) and graphitized carbon nanofibres (GCNF) in Polyvinylidene fluoride (PVDF) matrix. The crystalline structures of the nano composites were studied by X-ray diffraction (XRD) method and showed characteristic peaks at 17.7°, 18.5°, 20° and 26.7° of 2θ. The β phase crystalline nature of the composite films, degree of crystallinity, melting temperature and crystallization behavior of the hybrid composites were studied using appropriate characterization techniques. The filler in the insulating polymer matrix plays crucial role to improve the crystallinity of the composites.

Synthesis of nanostructured iron oxides dispersed in carbon materials and in situ XRD study of the changes caused by thermal treatment

NASA Astrophysics Data System (ADS)

Gonçalves, Gustavo R.; Schettino, Miguel A.; Morigaki, Milton K.; Nunes, Evaristo; Cunha, Alfredo G.; Emmerich, Francisco G.; Passamani, Edson C.; Baggio-Saitovitch, Elisa; Freitas, Jair C. C.

2015-07-01

Carbon-based magnetic nanocomposites are of large interest for applications in catalysis, magnetic separation, water cleaning, and magnetic resonance imaging, among others. This work describes the synthesis of nanocomposites consisting of iron oxides dispersed into a char (obtained from the carbonization at 700 °C of a lignocellulosic precursor) and the study of the thermal transformations occurring in these materials as a consequence of heat treatments. The materials were prepared by impregnation of the char with iron nitrate in the presence of ammonium hydroxide in aqueous suspension. X-ray diffraction experiments performed using synchrotron radiation and Mössbauer spectroscopy showed that the as-prepared material was composed of amorphous Fe3+ oxides. Scanning electron microscopy images combined with energy-dispersive X-ray spectrometry indicated a homogeneous dispersion of iron oxides and of silica particles (naturally present in the lignocellulosic precursor) throughout the char. X-ray diffractograms recorded in situ during the heat treatment of the as-prepared material showed the presence of small hematite crystallites (average size 22 nm) starting from ca. 300 °C. Further heating caused a progressive growth of the hematite crystallites up to ca. 500 °C, when the conversion to magnetite (Fe3O4) started to take place. At higher temperatures, wüstite (Fe1-xO) was detected as an intermediate phase and austenitic iron (γ-Fe) became the dominant phase at temperatures from 900 °C. A steep weight loss was observed in the TG curve accompanying this last reduction stage; upon cooling, γ-Fe was converted into α-Fe (ferrite), which was the dominant phase at room temperature in this heat-treated sample.

Green synthesis, characterization and catalytic degradation studies of gold nanoparticles against congo red and methyl orange.

PubMed

Umamaheswari, C; Lakshmanan, A; Nagarajan, N S

2018-01-01

The present study reports, novel and greener method for synthesis of gold nanoparticles (AuNPs) using 5,7-dihydroxy-6-metoxy-3 ' ,4 ' methylenedioxyisoflavone (Dalspinin), isolated from the roots of Dalbergia coromandeliana was carried out for the first time. The synthesized gold nanoparticles were characterized by UV-Vis spectroscopy, high resolution transmission electron microscopy (HR-TEM), selected area electron diffraction (SAED), Fourier transform infrared spectroscopy (FT-IR) and X-ray diffraction (XRD). The observed surface plasmon resonance (SPR) at 532nm in the UV-Vis absorption spectrum indicates the formation of gold nanoparticles. The powder XRD and SAED pattern for synthesized gold nanoparticles confirms crystalline nature. The HR-TEM images showed that the AuNPs formed were small in size, highly monodispersed and spherical in shape. The average particle sizes of the AuNPs are found to be ~10.5nm. The prepared AuNPs were found to be stable for more than 5months without any aggregation. The catalytic degradation studies of the synthesized AuNPs towards degradation of congo red and methyl orange, showed good catalytic in the complete degradation of both the dyes. The reduction catalyzed by gold nanoparticles followed the pseudo-first order kinetics, with a rate constant of 4.5×10 -3 s -1 (R 2 =0.9959) and 1.7×10 -3 s -1 (R 2 =0.9918) for congo red (CR) and methyl orange (MO), respectively. Copyright © 2017. Published by Elsevier B.V.

Deposition of dual-layer coating on Ti6Al4V

NASA Astrophysics Data System (ADS)

Hussain Din, Sajad; Shah, M. A.; Sheikh, N. A.

2017-03-01

Dual-layer diamond coatings were deposited on titanium alloy (Ti6Al4V) using a hot filament chemical vapour deposition technique with the anticipation of studying the structural and morphology properties of the alloy. The coated diamond films were characterized using scanning electron microscope, x-ray diffraction (XRD), and Raman spectroscopy. The XRD studies reveal that the deposited films are highly crystalline in nature, whereas morphological studies show that the films have a cauliflower structure. XRD analysis was used to calculate the structural parameters of the Ti6Al4V and CVD-coated Ti6Al4V. Raman spectroscopy was used to determine the nature and magnitude of the residual stress of the coatings.

Preparation, characterization and electroluminescence studies of ZnO nanorods for optoelectronic device applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Anju, E-mail: singh-nk24@yahoo.com; Vishwakarma, H. L., E-mail: horilal5@yahoo.com

2015-07-31

In this work, ZnO nanorods were achieved by a simple chemical precipitation method in the presence of capping agent Poly Vinyl Pyrrolidone (PVP) at room temperature. X-Ray Diffraction (XRD) result indicates that the synthesized undoped ZnO nanorods have wurtzite hexagonal structure without any impurities. It has been seen that the growth orientation of the prepared ZnO nanorods were (101). XRD analysis revealed that the nanorods having the crystallite size 49 nm. The Scanning Electron Microscopy (SEM) image confirmed the size and shape of these nanorods. The diameter of nanorods has been found that 1.52 µm to 1.61 µm and the lengthmore » of about 4.89 µm. It has also been found that at room temperature Ultra Violet Visible (UV-VIS) absorption band is around 355 nm (blue shifted as compared to bulk). Electroluminescence (EL) studies show that emission of light is possible at very small threshold voltage and increases rapidly with increasing applied voltage. It is seen that smaller ZnO nanoparticles give higher electroluminescence brightness starting at lower threshold voltage. The brightness is also affected by increasing the frequency of AC signal.« less

The CPP-ACP relieved enamel erosion from a carbonated soft beverage: an in vitro AFM and XRD study.

PubMed

Wang, C P; Huang, S B; Liu, Y; Li, J Y; Yu, H Y

2014-03-01

To investigate the CPP-ACP's effect on enamel against carbonated beverage erosion and explore the potential mechanism. A total of 30 enamel samples were prepared from sound bovine incisors, divided into 3 groups. Samples in the control group were kept in artificial saliva. Specimens' surfaces were smeared with a CPP-ACP agent (Tooth Mousse, TM) for 3 min, rinsed with distilled water for 10s, merged into cola (Coca Cola, CC) for 4 intervals of 2 min, rinsed again for the TM+CC group. In the CC group, specimens were treated solely with cola for 4 intervals (2 min each). The cycles were applied at 0, 12, 24, 36, 48 and 60 h. The surface microhardness (SMH) alterations were measured using a microhardness tester, the surface profiles were analyzed using the atomic force microscope, and the surface crystalline amount (I%) and crystallinity (FWHM) were analyzed using X-ray diffractometer. The SMH were significantly decreased in CC group, showing the largest SMH alteration; the reduction of SMH in TM+CC group was lower than that in CC group, still larger than control. After cycles, the TM+CC group showed rougher surfaces than control, while the CC group had the roughest surfaces. The TM+CC had an I% higher than the CC, and lower than the control. The TM+CC group had a FWHM lower than CC, higher than control. CPP-ACP was able to relieve the erosion on enamel from carbonated beverage. Copyright © 2013 Elsevier Ltd. All rights reserved.

In-field X-ray and neutron diffraction studies of re-entrant charge-ordering and field induced metastability in La0.175Pr0.45Ca0.375MnO3-δ

NASA Astrophysics Data System (ADS)

Sharma, Shivani; Shahee, Aga; Yadav, Poonam; da Silva, Ivan; Lalla, N. P.

2017-11-01

Low-temperature high-magnetic field (2 K, 8 T) (LTHM) powder X-ray diffraction (XRD) and time of flight powder neutron diffraction (NPD), low-temperature transmission electron microscopic (TEM), and resistivity and magnetization measurements have been carried out to investigate the re-entrant charge ordering (CO), field induced structural phase transitions, and metastability in phase-separated La0.175Pr0.45Ca0.375MnO3-δ (LPCMO). Low-temperature TEM and XRD studies reveal that on cooling under zero-field, paramagnetic Pnma phase transforms to P21/m CO antiferromagnetic (AFM) insulating phase below ˜233 K. Unlike reported literature, no structural signature of CO AFM P21/m to ferromagnetic (FM) Pnma phase-transition during cooling down to 2 K under zero-field was observed. However, the CO phase was found to undergo a re-entrant transition at ˜40 K. Neutron diffraction studies revealed a pseudo CE type spin arrangement of the observed CO phase. The low-temperature resistance, while cooled under zero-field, shows insulator to metal like transition below ˜105 K with minima at ˜25 K. On application of field, the CO P21/m phase was found to undergo field-induced transition to FM Pnma phase, which shows irreversibility on field removal below ˜40 K. Zero-field warming XRD and NPD studies reveal that field-induced FM Pnma phase is a metastable phase, which arise due to the arrest of kinetics of the first-order phase transition of FM Pnma to CO-AFM P21/m phase, below 40 K. Thus, a strong magneto-structural coupling is observed for this system. A field-temperature (H-T) phase-diagram has been constructed based on the LTHM-XRD, which matches very nicely with the reported H-T phase-diagram constructed based on magnetic measurements. Due to the occurrence of gradual growth of the re-entrant CO phase and the absence of a clear structural signature of phase-separation of CO-AFM P21/m and FM Pnma phases, the H-T minima in the phase-diagram of the present LPCMO sample has been

A comparative study of the effectiveness of "Star Show" vs. "Participatory Oriented Planetarium" lessons in a middle school Starlab setting

NASA Astrophysics Data System (ADS)

Platco, Nicholas L.., Jr.

2005-06-01

The purpose of this study was to compare the effectiveness of "Star Show" and the "Participatory Oriented Planetarium" (POP) instructional programs in a middle school Starlab setting. The Star Show is a planetarium program that relies heavily on an audiovisual/lecture format to impart information, while the POP method of instruction is an inquiry, activity-based approach to teaching astronomy. All Star Show and POP lessons were conducted in a Starlab planetarium. This study examined the effectiveness of the two methods on the attainment of astronomy knowledge, changes in student attitudes toward astronomy, retention of knowledge, and gender differences. A pilot study (N = 69) was conducted at a middle school near King of Prussia, Pennsylvania. The main study (N = 295) was conducted at a middle school near Reading, Pennsylvania. All students were pretested and posttested in both studies. The testing instruments included a 60-question paper-and-pencil content test and a 22-item Likert-style science attitude test. The content test was judged to be valid and reliable by a panel of science educators. The attitude test is a field-tested attitude survey developed by Michael Zeilik. The topics included in the Star Show and POP lessons were seasons, moon phases, eclipses, stars, and constellations. The Star Show programs used in this study are professionally prepared planetarium programs from Jeff Bowen Productions. Several planetarium educators who have been involved with planetarium training workshops throughout the United States developed the POP lessons used in this study. The Star Show was clearly the more effective method for improving student knowledge in both the pilot and main studies. Both methods were equally effective for improving student attitudes toward astronomy. The POP method was the more effective method of instruction when retention of knowledge was examined four weeks after the treatments ended. Gender did not have any significant effect on this study

The formation and structure of mechano-synthesized nanocrystalline Sr{sub 3}Fe{sub 2}O{sub 6.4}: XRD Rietveld, Mössabuer and XPS analyses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Al-Rawas, A.D., E-mail: arawas@squ.edu.om; Widatallah, H.M.; Al-Harthi, S.H.

2015-05-15

Highlights: • The formation of mechano-synthesized nanocrystalline Sr{sub 3}Fe{sub 2}O{sub 7−δ} is investigated. • Pre-milling the reactants substantially lowers the formation temperature. • The core and surface structures were studied. • XRD and {sup 57}Fe Mössbauer spectroscopic analyses indicate the δ-value to be 0.60. • XPS shows a complex surface structure for the mechanosynthesized Sr{sub 3}Fe{sub 2}O{sub 7−δ} nanoparticles. - Abstract: The influence of ball milling and subsequent sintering of a 3:1 molar mixture of SrCO{sub 3} and α-Fe{sub 2}O{sub 3} on the formation of Sr{sub 3}Fe{sub 2}O{sub 7−δ} double perovskite is investigated with different analytical techniques. Milling the mixturemore » for 110 h leads to the formation of SrCO{sub 3}-α-Fe{sub 2}O{sub 3} nanocomposites and the structural deformation of α-Fe{sub 2}O{sub 3} via the incorporation of Sr{sup 2+} ions. Subsequent sintering of the pre-milled reactants’ mixture has led to the partial formation of an SrFeO{sub 3} perovskite-related phase in the temperature range 400–600 °C. This was followed by the progressive development of an Sr{sub 3}Fe{sub 2}O{sub 7−δ} phase that continued to increase with increasing sintering temperature until a single-phased nanocrystalline Sr{sub 3}Fe{sub 2}O{sub 7−δ} phase was attained at 950 °C (12 h). This temperature is ∼350 °C lower than the temperature at which the material is prepared conventionally using the ceramic method. The evolution of different structural phases during the reaction process is discussed. Rietveld refinement of the X-ray diffraction data shows a value of 0.60 for the oxygen deficiency δ, in consistency with the Fe{sup 3+}/Fe{sup 4+} ratio derived from the {sup 57}Fe Mössbauer data recorded at both 300 K and 78 K. The Mössbauer data suggests that the Sr{sub 3}Fe{sub 2}O{sub 6.4} nanoparticles are superparamagnetic with blocking temperatures below 78 K. The surfaces of the Sr{sub 3}Fe{sub 2}O{sub 6

Thermal behaviour and microanalysis of coal subbituminus

NASA Astrophysics Data System (ADS)

Heriyanti; Prendika, W.; Ashyar, R.; Sutrisno

2018-04-01

Differential scanning calorimetry (DSC) and X-ray powder diffraction (XRD) is used to study the thermal behaviour of sub-bituminous coal. The DSC experiment was performed in air atmosphere up to 125 °C at a heating rate of 25 °C min1. The DSC curve showed that the distinct transitional stages in the coal samples studied. Thermal heating temperature intervals, peak and dissociation energy of the coal samples were also determined. The XRD analysis was used to evaluate the diffraction pattern and crystal structure of the compounds in the coal sample at various temperatures (25-350 °C). The XRD analysis of various temperatures obtained compounds from the coal sample, dominated by quartz (SiO2) and corundum (Al2O3). The increase in temperature of the thermal treatment showed a better crystal formation.

Study on the Structural, Morphological and Optical Properties of RF-Sputtered Dysprosium-Doped Barium Tungstate Thin Films

NASA Astrophysics Data System (ADS)

Hridya, S.; Kavitha, V. S.; Chalana, S. R.; Reshmi Krishnan, R.; Sreeja Sreedharan, R.; Suresh, S.; Nampoori, V. P. N.; Sankararaman, S.; Prabhu, Radhakrishna; Mahadevan Pillai, V. P.

2017-11-01

Barium tungstate films with different Dy3+ doping concentrations, namely 0 wt.%, 1 wt.%, 3 wt.% and 5 wt.%, are deposited on cleaned quartz substrate by radio frequency magnetron sputtering technique and the prepared films are annealed at a temperature of 700°C. The structural, morphological and optical properties of the annealed films are studied using techniques such as x-ray diffraction (XRD), micro-Raman spectroscopy, field emission scanning electron microscopy, atomic force microscopy and photoluminescence spectroscopy. XRD analysis shows that all the films are well-crystallized in nature with a monoclinic barium tungstate phase. The presence of characteristic modes of the tungstate group in the Raman spectra supports the formation of the barium tungstate phase in the films. Scanning electron microscopic images of the films present a uniform dense distribution of well-defined grains with different sizes. All the doped films present a broad emission in the 390-500 nm region and its intensity increases up to 3 wt.% and thereafter decreases due to usual concentration quenching.

Long-term integrated studies show complex and surprising effects of climate change in northern hardwood forests

Treesearch

Peter M. Groffman; Lindsey Rustad; Pamela H. Templer; John Campbell; Lynn M. Christenson; Nina K. Lany; Anne M. Socci; Matthew A. Vadeboncoeur; Paul Schaberg; Geoffrey F. Wilson; Charles T. Driscoll; Timothy J. Fahey; Melany C. Fisk; Christine L. Goodale; Mark B. Green; Steven P. Hamburg; Chris E. Johnson; Myron J. Mitchell; Jennifer L. Morse; Linda H. Pardo; Nicholas L. Rodenhouse

2012-01-01

Evaluations of the local effects of global change are often confounded by the interactions of natural and anthropogenic factors that overshadow the effects of climate changes on ecosystems. Long-term watershed and natural elevation gradient studies at the Hubbard Brook Experimental Forest and in the surrounding region show surprising results demonstrating the effects...

Structural and mechanical study of concrete made from cementitious materials of low environmental impact

NASA Astrophysics Data System (ADS)

González, A. K.; Montaño, A. M.; González, C. P.; Santos, A.

2017-12-01

This work shows the results obtained by replacing Type I Portland®, by cementitious geopolymers materials, derived from minerals, in concrete mixtures. Synthesis of both geopolymers through alkaline activation of two alluminosilicates: Bentonite and Pumice with sodium silicate (Na2SiO3). XRD, SEM and XRDE are used to structural study of new geopolymers. Concrete mixtures with replacement of Portland have 10% and 30% of geopolymer. Finally, concrete mortars formed were mechanically analysed according to ICONTEC 220 at 7, 14, 28, 41, 90 and 120 days of cure. Results shows that compressive strength of concrete from Bentonite and Pumice are almost the same for the standard concrete at 28 days of cure. At 90 days of cure, compression resistance of concrete from Pumice at 10% is even higher than those that standard concrete shows.

Study on the Growth Mechanism of K2Ti4O9 Crystal

NASA Astrophysics Data System (ADS)

Zhou, Xuesong; Fan, Jing; Wei, Xiaoli; Shen, Yi; Meng, Yanzhi

2018-04-01

Potassium hexatitanate (K2Ti4O9) whiskers were prepared by the kneading-drying-calcination method. After the preparation of products under different calcination temperatures and holding times, their morphology and structure were characterized by thermogravimetric and differential thermal, X-ray diffraction (XRD), scanning electron microscopy and transmission electron microscopy. The XRD analysis showed that the reaction mixture was completely converted to K2Ti4O9 crystals at 800 °C when the T/K ratio was 3. Based on the analysis of LS (liquid-solid) growth mechanism, the corresponding transformation reaction mechanism during the roasting was elucidated. K2Ti4O9 whiskers grow mainly through the parallel action at a low temperature. With the increase in temperature, the series effect is obvious.

Effect of intrinsic zinc oxide coating on the properties of Al-doped zinc oxide nanorod arrays

NASA Astrophysics Data System (ADS)

Saidi, S. A.; Mamat, M. H.; Ismail, A. S.; Malek, M. F.; Yusoff, M. M.; Sin, N. D. Md.; Zoolfakar, A. S.; Khusaimi, Z.; Rusop, M.

2018-05-01

The aim of this study was to explore the influence of intrinsic zinc oxide (ZnO) coating fabricated by a simple immersion method. X-ray powder diffraction (XRD) analysis indicated that the Al-doped ZnO nanorod arrays films had a hexagonal wurtzite structure, similar to that of an intrinsic ZnO coating. Structural properties of the samples were characterised using field emission scanning electron microscopy (FESEM; JEOL JSM-7600F) and optical properties using X-ray diffraction (XRD). The XRD results showed that all films were crystallized under hexagonal wurtzite structure and presented a preferential orientation along the c-axis (002) was obtained. The XRD results showed that the intrinsic ZnO coating material had a strong orientation, whereas the ZnO was randomly oriented. Overall these results indicate that intrinsic ZnO coating are pontetial for the creation of functional materials such as barrier protection, optoelectronic devices, humidity sensor and ultraviolet photoconductive sensor.

Synthesis and detection the oxidization of Co cores of Co@SiO2 core-shell nanoparticles by in situ XRD and EXAFS.

PubMed

Zhang, Kunhao; Zhao, Ziyan; Wu, Zhonghua; Zhou, Ying

2015-01-01

In this paper, the Co@SiO2 core-shell nanoparticles were prepared by the sol-gel method. The oxidization of Co core nanoparticles was studied by the synchrotron radiation-based techniques including in situ X-ray diffraction (XRD) and X-ray absorption fine structure (XAFS) up to 800°C in air and N2 protection conditions, respectively. It was found that the oxidization of Co cores is undergoing three steps regardless of being in air or in N2 protection condition. In the first step ranging from room temperature to 200°C, the Co cores were dominated by Co(0) state as well as small amount of Co(2+) ions. When temperature was above 300°C, the interface between Co cores and SiO2 shells was gradually oxidized into Co(2+), and the CoO layer was observed. As the temperature increasing to 800°C, the Co cores were oxidized to Co3O4 or Co3O4/CoO. Nevertheless, the oxidization kinetics of Co cores is different for the Co@SiO2 in air and N2 gas conditions. Generally, the O2 in the air could get through the SiO2 shells easily onto the Co core surface and induce the oxidization of the Co cores due to the mesoporous nature of the SiO2 shells. However, in N2 gas condition, the O atoms can only be from the SiO2 shells, so the diffusion effect of O atoms in the interface between Co core and SiO2 shell plays a key role.

In vitro and in vivo studies on a novel solid dispersion of repaglinide using polyvinylpyrrolidone as the carrier.

PubMed

Yin, Li-Fang; Huang, Shi-Jing; Zhu, Chun-Li; Zhang, Shu-Hui; Zhang, Qiang; Chen, Xi-Jing; Liu, Qing-Wang

2012-11-01

In order to improve the dissolution and absorption of the water insoluble drug repaglinide, a solid dispersion was developed by solvent method using polyvinylpyrrolidone K30 (PVP K30) as the hydrophilic carrier for the first time. Studies indicated that both solubility and the dissolution rate of repaglinide were significantly increased in the solid dispersion system compared with that of repaglinide raw material or physical mixtures. The repaglinide solid dispersions with PVP K30 solid state was characterized by polarizing microscopy, differential scanning calorimetry (DSC), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT-IR). DSC and XRD studies indicated that repaglinide existed in an amorphous form in the solid dispersion. FT-IR analysis demonstrated the presence of intermolecular hydrogen bonding between repaglinide and PVP K30 in the solid dispersion. In the in situ gastrointestinal perfusion experiment, solid dispersion was shown to remarkably enhance the absorption of repaglinide in stomach and all segments of intestine. In vivo pharmacokinetic study in rats showed that immediate and complete release of repaglinide from the solid dispersion resulted in rapid absorption that significantly increased the bioavailability and the maximum plasma concentration over repaglinide raw material. These results demonstrated PVP K30 was an appropriate carrier for solid dispersion of repaglinide, with increased dissolution and oral absorption.

Study of sintering temperature on the structure of silicon carbide membrane

NASA Astrophysics Data System (ADS)

Sadighzadeh, A.; Mashayekhan, Sh.; Nedaie, B.; Ghorashi, A. H.

2014-09-01

Study of the microstructure of silicon carbide (SiC) membrane as a function of sintering temperature and the percentage amount of additive kaolin is the outcome of the experimental fabrications presented in this paper. The SEM micrographs are used to investigate the impact of above parameters on the porosity of membrane. The experimental results show that the rise in the temperature causes more sintering of powder particles, growing granules, augmentation of the number of pores and consequently increasing the total porosity of membrane. Using XRD analyses, it is found that SiC amorphous phase is highly sensitive to the temperature and its crystallization physically grows with temperature increase.

Study of Crystallinity Index (CrI) of Oil Palm Frond Pretreatment using Aqueous [EMIM][OAc] in a Closed System

NASA Astrophysics Data System (ADS)

Abu Darim, R.; Azizan, A.; Salihon, J.

2018-05-01

The objective of this preliminary study is to identify the Crystalinity Index (CrI) of Oil Palm Frond (OPF) pretreated with 40% concentration of 1-ethyl-3-methylimidazolium acetate ionic liquid ([EMIM][OAc]) in a closed system. The morphology and structural changes of the pretreated OPF were examined by using Fourier Transform Infrared Spectrometer (FTIR) and X-Ray Diffraction (XRD). The pretreatment process was carried out in triplicates by loading 40% of [EMIM][OAc] concentration with 10 wt% of OPF loading in the Bio-ionic liquid-reactor. The pretreatment process was conducted for 3 hours with working volume of 70 mL and temperature of 110°C. A Bio-ionic liquid reactor was purposely designed for the lignocellulosic pretreatment by using aqueous ionic liquid at high temperature (higher than boiling point of water). The CrI of OPF pretreated with 40% concentration of [EMM][OAc] in a closed system observed was 9% lower from the untreated OPF and the result showed significant difference with 95% confidence level. Further examination of the untreated and pretreated OPF by using XRD showed that the diffraction pattern of the pretreated OPF samples was decreasing compared to the untreated OPF. The characteristic of the FTIR spectra of the pretreated OPF showed the presence of the cellulose I and occurrence of amorphous cellulosic in the samples. The findings from this study are expected to improve knowledge on pretreatment of OPF by using aqueous [EMIM][OAc] as a green economically viable process for future renewable energy.

[Study on Hydrothermal Preparation and Luminescence Properties of Luminescent Material BaSrMg(PO₄)₂:Eu³⁺].

PubMed

Hu, Qing-song; Zhu, Cheng-jing; Xia, Yue-yi; Wang, Li-li; Liu, Wen-han; Pan, Zai-fa

2016-02-01

Eu³⁺ doped BaSrMg (PO₄)₂ were prepared by a hydrothermal method. The crystal structure and morphology of BaSrMg(PO₄)₂:Eu³⁺ phosphor were characterized by X-ray powder diffraction (XRD) and field emission scanning electron microscopy (FESEM). The effects of different pH values (5, 6, 7 and 8) and different reaction temperatures (120, 140, 160, 180 and 200 °C) on the crystal structure and morphology of BaSrMg(PO₄)₂:Eu³⁺ phosphor were studied in this paper. The results of XRD indicate that diffraction peaks are sharp and strong only when pH value is 6, meanwhile the FESEM shows the morphology is regular-shaped. The XRD patterns show amorphous halos superimposed with several weak sharp peaks for the samples preparing under the pH values of 5, 7 and 8. It indicates that these three samples are solid solution or mixed phases, which are in accord with the results of FESEM. From the fluorescence spectra, the peaks in the excitation spectra were assigned to the transition from ⁷F₀ to ⁵D₄, ⁵L₈, ⁵L₆ and ⁵D₂, while the peaks of emission spectra corresponding to the transition of ⁵D₁ --> ⁷F₁ and ⁵D₀-->⁷Fj (J = 0, 1, 2, 3 and 4). The strongest emission peak of the optimized phosphor located at 613 nm (⁵D0--> ⁷F₂), excited by the main excitation peak with wavelength of 394 nm. The splitting of the emission peaks changes depends on pH values and temperatures, which indicating that luminescence properties is closely related to the crystal structure and morphology of particles.

Structural studies of ZnO nanostructures by varying the deposition parameters

NASA Astrophysics Data System (ADS)

Yunus, S. H. A.; Sahdan, M. Z.; Ichimura, M.; Supee, A.; Rahim, S.

2017-01-01

The effect of Zinc Oxide (ZnO) thin film on the growth of ZnO nanorods (NRs) was investigated. The structures of ZnO NRs were synthesized by chemical bath deposition (CBD) method in aqueous solution of N2O6Zn.6H2O and C6H12N4 at 90°C of deposition temperature. One of the ZnO NRs samples was deposited on a ZnO seed layer coated on a glass substrate to investigate the properties of ZnO NRs without receiving effect of other materials. Next, for diode application, the ZnO NRs was deposited on tin monosulfide (SnS) coated on indium-tin-oxide (ITO) coated glass substrate (SnS/ITO). The next, the ZnO structural properties were studied from surface morphology, X-ray diffractometer (XRD) spectra, and chemical composition by using field emission scanning electron microscope (FESEM), XRD and energy dispersive X-ray Spectroscopy (EDX). The growth of ZnO NRs on ZnO seed layer was investigated by ZnO seed layer condition while the growth of ZnO NRs on SnS/ITO was investigated by deposition time and deposition temperature parameters. From FESEM images, aligned ZnO NRs were obtained, and the diameters of ZnO NRs were 0.024-3.94 µm. The SnS thin film was affected by the diameter of ZnO NRs which are the ZnO NRs grow on SnS thin films has a larger diameter compared to ZnO NRs grow on ZnO seed layer. Besides that, all of ZnO peaks observed from XRD corresponding to the wurzite structure and preferentially oriented along the c-axis. In addition, EDX shows a high composition of zinc (Zn) and oxygen (O) signals, which indicated that the NRs are indeed made up of Zn and O.

Component analyses of urinary nanocrystallites of uric acid stone formers by combination of high-resolution transmission electron microscopy, fast Fourier transformation, energy dispersive X-ray spectroscopy, X-ray diffraction and Fourier transform infrared spectroscopy.

PubMed

Sun, Xin-Yuan; Xue, Jun-Fa; Xia, Zhi-Yue; Ouyang, Jian-Ming

2015-06-01

This study aimed to analyse the components of nanocrystallites in urines of patients with uric acid (UA) stones. X-ray diffraction (XRD), Fourier transform infrared spectroscopy, high-resolution transmission electron microscopy (HRTEM), fast Fourier transformation (FFT) of HRTEM, and energy dispersive X-ray spectroscopy (EDS) were performed to analyse the components of these nanocrystallites. XRD and FFT showed that the main component of urinary nanocrystallites was UA, which contains a small amount of calcium oxalate monohydrate and phosphates. EDS showed the characteristic absorption peaks of C, O, Ca and P. The formation of UA stones was closely related to a large number of UA nanocrystallites in urine. A combination of HRTEM, FFT, EDS and XRD analyses could be performed accurately to analyse the components of urinary nanocrystallites.

Synthesis, characterization and antimicrobial studies of Schiff base complexes

NASA Astrophysics Data System (ADS)

Zafar, Hina; Ahmad, Anis; Khan, Asad U.; Khan, Tahir Ali

2015-10-01

The Schiff base complexes, MLCl2 [M = Fe(II), Co(II), Ni(II), Cu(II) and Zn(II)] have been synthesized by the template reaction of respective metal ions with 2-acetylpyrrole and 1,3-diaminopropane in 1:2:1 M ratio. The complexes have been characterized by elemental analyses, ESI - mass, NMR (1H and 13C), IR, XRD, electronic and EPR spectral studies, magnetic susceptibility and molar conductance measurements. These studies show that all the complexes have octahedral arrangement around the metal ions. The molar conductance measurements of all the complexes in DMSO indicate their non-electrolytic nature. The complexes were screened for their antibacterial activity in vitro against Gram-positive (Streptococcus pyogenes) and Gram-negative (Klebsiella pneumoniae) bacteria. Among the metal complexes studied the copper complex [CuLCl2], showed highest antibacterial activity nearly equal to standard drug ciprofloxacin. Other complexes also showed considerable antibacterial activity. The relative order of activity against S. Pyogenes is as Cu(II) > Zn(II) > Co(II) = Fe(II) > Ni(II) and with K. Pneumonia is as Cu(II) > Co(II) > Zn(II) > Fe(II) > Ni(II).

Spectral, thermal, XRD and SEM studies of charge-transfer complexation of hexamethylenediamine and three types of acceptors: π-, σ- and vacant orbital acceptors that include quinol, picric acid, bromine, iodine, SnCl4 and ZnCl2 acceptors

NASA Astrophysics Data System (ADS)

Adam, Abdel Majid A.; Refat, Moamen S.; Saad, Hosam A.

2013-11-01

In this work, structural, thermal, morphological and pharmacological characterization was performed on the interactions between a hexamethylenediamine (HMDA) donor and three types of acceptors to understand the complexation behavior of diamines. The three types of acceptors include π-acceptors (i.e., quinol (QL) and picric acid (PA)), σ-acceptors (i.e., bromine and iodine) and vacant orbital acceptors (i.e., tin(IV) tetrachloride (SnCl4) and zinc chloride (ZnCl2)). The characterization of the obtained CT complexes was performed using elemental analysis, infrared (IR), Raman, 1H NMR and electronic absorption spectroscopy, powder X-ray diffraction (XRD) and thermogravimetric (TG) analysis. Their morphologies were studied using scanning electron microscopy with energy-dispersive X-ray analysis (SEM-EDX). The biological activities of the obtained CT complexes were tested for their antibacterial activities. The complex containing the QL acceptor exhibited a remarkable electronic spectrum with a strong, broad absorption band, which had an observed λmax that was at a much longer wavelength than those of the free reactants. In addition, this complex exhibited strong antimicrobial activities against various bacterial and fungal strains compared to standard drugs. The complexes containing the PA, iodine, Sn(IV) and Zn(II) acceptors exhibited good thermal stability up to 240, 330, 275 and 295 °C, respectively. The complexes containing bromine, Sn(IV) and Zn(II) acceptors exhibited good crystallinity. In addition to its good crystallinity properties, the complex containing the bromine acceptor exhibits a remarkable morphology feature.

Reversible photo-induced trap formation in mixed-halide hybrid perovskites for photovoltaics† †Electronic supplementary information (ESI) available: Experimental details, PL, PDS spectra and XRD patterns. See DOI: 10.1039/c4sc03141e Click here for additional data file.

PubMed Central

Hoke, Eric T.; Slotcavage, Daniel J.; Dohner, Emma R.; Bowring, Andrea R.

2015-01-01

We report on reversible, light-induced transformations in (CH3NH3)Pb(BrxI1–x)3. Photoluminescence (PL) spectra of these perovskites develop a new, red-shifted peak at 1.68 eV that grows in intensity under constant, 1-sun illumination in less than a minute. This is accompanied by an increase in sub-bandgap absorption at ∼1.7 eV, indicating the formation of luminescent trap states. Light soaking causes a splitting of X-ray diffraction (XRD) peaks, suggesting segregation into two crystalline phases. Surprisingly, these photo-induced changes are fully reversible; the XRD patterns and the PL and absorption spectra revert to their initial states after the materials are left for a few minutes in the dark. We speculate that photoexcitation may cause halide segregation into iodide-rich minority and bromide-enriched majority domains, the former acting as a recombination center trap. This instability may limit achievable voltages from some mixed-halide perovskite solar cells and could have implications for the photostability of halide perovskites used in optoelectronics. PMID:28706629

Study on the removal of iron impurities in methanesulfonic acid tin plating bath

NASA Astrophysics Data System (ADS)

Hou-li, LIU; Jian-Jun, CHEN; Hong-Liang, PAN

2018-03-01

This thesis investigated the the influence of sodium sulfite as reducing agent on the recovery rate of tin ion. The approach is that HZ016 type cation exchange resin was used to adsorb Sn2+ and Fe2+ in electroplated tin solution first. After adsorption, the resin was removed by sulfuric acid, which was added with NaOH to adjust pH value to form precipitation and separate tin. X-ray diffraction (XRD) and energy spectrum (EDS) method were used to analyze the composition of the precipitates adjusted by pH. The results show that when the mass ratio of resin to bath is 1:2, the adsorption efficiency of resin reaches 98.3% and 97.1% respectively, and the elution efficiency of tin and iron reaches 95.1% and 94% respectively when the mass ratio of resin to eluent sulfuric acid is 1:4. Sodium sulfite was added to increase the efficiency of tin recovery by 8.1%. EDS and XRD atlas showed that after pH regulation, the main composition of the filtration precipitation was the hydroxides of tin.

Comparative study of hydrogen storage on metal doped mesoporous materials

NASA Astrophysics Data System (ADS)

Carraro, P. M.; Sapag, K.; Oliva, M. I.; Eimer, G. A.

2018-06-01

The hydrogen adsorption capacity of mesoporous materials MCM-41 modified with Co, Fe, Ti, Mg and Ni at 77 K and 10 bar was investigated. Various techniques including XRD, N2 adsorption and DRUV-vis were employed for the materials characterization. The results showed that a low nickel loading on MCM-41 support promoted the presence of hydrogen-favorable sites, increasing the hydrogen storage capacity.

A comparative study on the properties of graphene oxide and activated carbon based sustainable wood starch composites.

PubMed

Baishya, Prasanta; Maji, Tarun Kumar

2018-08-01

Activated carbon (AC) prepared from Jatropha curcas and graphene oxide (GO) were employed in the preparation of natural polymer based wood starch composites (WSC) through the solution blending technique using water as a solvent. In this study, methyl methacrylate (MMA) was grafted onto the starch polymer and this MMA grafted starch (MMA-g-starch) was cross-linked with the cheap soft wood flour using the citric acid as cross-linker and water as a solvent in the whole process. The prepared GO and AC were characterized through Fourier transform infrared spectroscopy (FTIR), X-ray diffractometry (XRD), thermogravimetric analysis (TGA) and Raman study. The interaction of GO and AC, with MMA-g-starch, citric acid and wood were studied by FTIR, XRD and SEM analysis. The GO and AC treated composites exhibited outstanding mechanical properties, thermal stability and fire resistance properties. The tensile strength of the composites increased by 178% and 200% with addition of 2 phr AC and GO respectively compared to untreated composites. A significant enhancement in water resistance properties of GO and AC treated composites was also attained. The study showed that the properties of the composites containing AC prepared from the seeds of Jatropha curcas was quite comparable with the composites reinforced with GO. Copyright © 2018 Elsevier B.V. All rights reserved.

Physical and optical studies of BaO-TeO2-TiO2-B2O3 glasses containing Cu2+ transition metal ion

NASA Astrophysics Data System (ADS)

Srinivas, B.; Kumar, R. Vijaya; Hameed, Abdul; Sagar, D. Karuna; Chary, M. Narasimha; Shareefuddin, Md.

2018-05-01

Glasses with the composition xBaO-(30-x) TeO2-10TiO2-59B2O3-1CuO (where x = 10, 15, 20 and 25 mole %) were prepared by melt quenching technique. The XRD studies were made on these glass samples at room temperature. The amorphous nature of the glass samples was confirmed from the XRD patterns. The physical parameters such as density (ρ), molar volume (Vm), average boron-boron separation (dB-B) and oxygen packing density (OPD) were calculated. The change in density and molar volume has been investigated in terms of the variation of BaO in the glass composition. The optical absorption spectra have been recorded at room temperature. The values of optical band gap have been estimated from the ASF and Tauc's methods. Both Tauc's and ASF methods have been showing progressively increasing indirect optical band gap values with the increase of BaO concentrations.

Comparative study of Ni and Cu doped ZnO nanoparticles: Structural and optical properties

NASA Astrophysics Data System (ADS)

Thakur, Shaveta; Thakur, Samita; Sharma, Jyoti; Kumar, Sanjay

2018-05-01

Nanoparticles of undoped and doped (0.1 M Ni2+ and Cu2+) ZnO are synthesized using chemical precipitation method. The crystallite size, morphology, chemical bonding and optical properties of as prepared nanoparticles are determined by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy and UV-visible spectra. XRD analysis shows that the prepared samples are single phase and have hexagonal wurtzite structure. The crystallite size of the doped and undoped nanoparticles is determined using Scherrer method. The crystallite size is found to be increased with concentration of nickel and copper. All stretching and vibrational bands are observed at their specific positions through FTIR. The increase in band gap can be attributed to the different chemical nature of dopant and host cation.

Electron microscopy study of microbial mat in the North Fiji basin hydrothermal vent

NASA Astrophysics Data System (ADS)

Park, H.; Kim, J. W.; Lee, J. W.

2017-12-01

Hydrothermal vent systems consisting of hydrothermal vent, hydrothermal sediment and microbial mat are widely spread around the ocean, particularly spreading axis, continental margin and back-arc basin. Scientists have perceived that the hydrothermal systems, which reflect the primeval earth environment, are one of the best places to reveal the origin of life and extensive biogeochemical process of microbe-mineral interaction. In the present study multiline of analytical methods (X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM)) were utilized to investigate the mineralogy/chemistry of microbe-mineral interaction in hydrothermal microbial mat. Microbial mat samples were recovered by Canadian scientific submersible ROPOS on South Pacific North Fiji basin KIOST hydrothermal vent expedition 1602. XRD analysis showed that red-colored microbial mat contains Fe-oxides and Fe-oxyhydroxides. Various morphologies of minerals in the red-colored microbial mat observed by SEM are mainly showed sheath shaped, resembled with Leptothrix microbial structure, stalks shaped, similar with Marioprofundus microbial structure and globule shaped microbial structures. They are also detected with DNA analysis. The cross sectional observation of microbial structures encrusted with Fe-oxide and Fe-oxyhydroxide at a nano scale by Transmission Electron Microscopy (TEM) and Focused Ion Beam (FIB) technique was developed to verify the structural/biogeochemical properties in the microbe-mineral interaction. Systematic nano-scale measurements on the biomineralization in the microbial mat leads the understandings of biogeochemical environments around the hydrothermal vent.

The high-pressure behavior of spherocobaltite (CoCO3): a single crystal Raman spectroscopy and XRD study

NASA Astrophysics Data System (ADS)

Chariton, Stella; Cerantola, Valerio; Ismailova, Leyla; Bykova, Elena; Bykov, Maxim; Kupenko, Ilya; McCammon, Catherine; Dubrovinsky, Leonid

2018-01-01

Magnesite (MgCO3), calcite (CaCO3), dolomite [(Ca, Mg)CO3], and siderite (FeCO3) are among the best-studied carbonate minerals at high pressures and temperatures. Although they all exhibit the calcite-type structure ({R}\\bar{3}{c}) at ambient conditions, they display very different behavior at mantle pressures. To broaden the knowledge of the high-pressure crystal chemistry of carbonates, we studied spherocobaltite (CoCO3), which contains Co2+ with cation radius in between those of Ca2+ and Mg2+ in calcite and magnesite, respectively. We synthesized single crystals of pure spherocobaltite and studied them using Raman spectroscopy and X-ray diffraction in diamond anvil cells at pressures to over 55 GPa. Based on single crystal diffraction data, we found that the bulk modulus of spherocobaltite is 128 (2) GPa and K' = 4.28 (17). CoCO3 is stable in the calcite-type structure up to at least 56 GPa and 1200 K. At 57 GPa and after laser heating above 2000 K, CoCO3 partially decomposes and forms CoO. In comparison to previously studied carbonates, our results suggest that at lower mantle conditions carbonates can be stable in the calcite-type structure if the radius of the incorporated cation(s) is equal or smaller than that of Co2+ (i.e., 0.745 Å).

Time-resolved x-ray diffraction and Raman studies of the phase transition mechanisms of methane hydrate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hirai, Hisako, E-mail: hirai@sci.ehime-u.ac.jp; Kadobayashi, Hirokazu; Hirao, Naohisa

The mechanisms by which methane hydrate transforms from an sI to sH structure and from an sH to filled-ice Ih structure were examined using time-resolved X-ray diffractometry (XRD) and Raman spectroscopy in conjunction with charge-coupled device camera observation under fixed pressure conditions. The XRD data obtained for the sI–sH transition at 0.8 GPa revealed an inverse correlation between sI and sH, suggesting that the sI structure is replaced by sH. Meanwhile, the Raman analysis demonstrated that although the 12-hedra of sI are retained, the 14-hedra are replaced sequentially by additional 12-hedra, modified 12-hedra, and 20-hedra cages of sH. With themore » sH to filled-ice Ih transition at 1.8 GPa, both the XRD and Raman data showed that this occurs through a sudden collapse of the sH structure and subsequent release of solid and fluid methane that is gradually incorporated into the filled-ice Ih to complete its structure. This therefore represents a typical reconstructive transition mechanism.« less

Effect of substrate temperature in the synthesis of BN nanostructures

NASA Astrophysics Data System (ADS)

Sajjad, M.; Zhang, H. X.; Peng, X. Y.; Feng, P. X.

2011-06-01

Boron nitride (BN) nanostructures were grown on molybdenum discs at different substrate temperatures using the short-pulse laser plasma deposition technique. Large numbers of randomly oriented nanorods of fiber-like structures were obtained. The variation in the length and diameter of the nanorods as a function of the substrate temperature was systematically studied. The surface morphologies of the samples were studied using scanning electron microscopy. Energy dispersive x-ray spectroscopy confirmed that both the elements boron and nitrogen are dominant in the nanostructure. The x-ray diffraction (XRD) technique was used to analyse BN phases. The XRD peak that appeared at 26° showed the presence of hexagonal BN phase, whereas the peak at 44° was related to cubic BN content in the samples. Raman spectroscopic analysis showed vibrational modes of sp2- and sp3-type bonding in the sample. The Raman spectra agreed well with XRD results.

Limestone calcination under calcium-looping conditions for CO2 capture and thermochemical energy storage in the presence of H2O: an in situ XRD analysis.

PubMed

Valverde, Jose Manuel; Medina, Santiago

2017-03-15

This work reports an in situ XRD analysis of whether the calcination/carbonation behavior of natural limestone (CaCO 3 ) is affected by the addition of H 2 O to the calciner at a very low concentration under relevant Calcium-Looping (CaL) conditions for CO 2 capture in coal fired power plants (CFPP) and Thermochemical Energy Storage (TCES) in Concentrated Solar Power plants (CSP). Previous studies have demonstrated that the presence of steam in the calciner at a high concentration yields a significant increase in the reaction rate. However, a further undesired consequence is the serious deterioration of the CaO mechanical strength, which would lead to particle attrition and mass loss in any CaL process based on the use of circulating fluidized beds. The results presented in this manuscript on the time evolution of the wt% and crystallite size of the phases involved in the calcination/carbonation reactions indicate that the calcination rate is still notably increased by the presence of H 2 O at very low concentrations whereas the reactivity toward carbonation and crystal structure of the formed CaO are not essentially affected, which suggests that the CaO mechanical strength is not impaired. Thus, the benefit of using steam for calcination in the CaL process could be still retained while at the same time particle attrition would not be promoted.

Tilapia show immunization response against Ich

USDA-ARS?s Scientific Manuscript database

This study compares the immune response of Nile tilapia and red tilapia against parasite Ichthyophthirius multifiliis (Ich) using a cohabitation challenge model. Both Nile and red tilapia showed strong immune response post immunization with live Ich theronts by IP injection or immersion. Blood serum...

X-ray absorption fine structure and x-ray diffraction studies of crystallographic grains in nanocrystalline FePd:Cu thin films

NASA Astrophysics Data System (ADS)

Krupinski, M.; Perzanowski, M.; Polit, A.; Zabila, Y.; Zarzycki, A.; Dobrowolska, A.; Marszalek, M.

2011-03-01

FePd alloys have recently attracted considerable attention as candidates for ultrahigh density magnetic storage media. In this paper we investigate FePd thin alloy film with a copper admixture composed of nanometer-sized grains. [Fe(0.9 nm)/Pd(1.1 nm)/Cu(d nm)]×5 multilayers were prepared by thermal deposition at room temperature in UHV conditions on Si(100) substrates covered by 100 nm SiO2. The thickness of the copper layer has been changed from 0 to 0.4 nm. After deposition, the multilayers were rapidly annealed at 600 °C in a nitrogen atmosphere, which resulted in the creation of the FePd:Cu alloy. The structure of alloy films obtained this way was determined by x-ray diffraction (XRD), glancing angle x-ray diffraction, and x-ray absorption fine structure (EXAFS). The measurements clearly showed that the L10 FePd:Cu nanocrystalline phase has been formed during the annealing process for all investigated copper compositions. This paper concentrates on the crystallographic grain features of FePd:Cu alloys and illustrates that the EXAFS technique, supported by XRD measurements, can help to extend the information about grain size and grain shape of poorly crystallized materials. We show that, using an appropriate model of the FePd:Cu grains, the comparison of EXAFS and XRD results gives a reasonable agreement.

"The Show"

ERIC Educational Resources Information Center

Gehring, John

2004-01-01

For the past 16 years, the blue-collar city of Huntington, West Virginia, has rolled out the red carpet to welcome young wrestlers and their families as old friends. They have come to town chasing the same dream for a spot in what many of them call "The Show". For three days, under the lights of an arena packed with 5,000 fans, the…

Mechanisms governing brittle fault mechanics - a multi-scale study from the Permian Khao-Kwang fold-and-thrust belt, Thailand

NASA Astrophysics Data System (ADS)

von Hagke, Christoph; Morley, Chris; Kanitpanyacharoen, Waruntorn

2017-04-01

Despite our qualitative understanding of factors contributing to thrust and detachment weakness such as mineralogy, pore fluid pressure, or efficiency of structure localization, it is difficult to assess the contribution of the individual factors. Here we present multi-scale analysis of a mixed clay / carbonate high displacement (kms of heave) thrust zone, where it is possible to study structures formed within a similar temperature and pressure regime, and thus only varying due to lithological contrasts. We mapped the well-exposed thrust zone in a large quarry at outcrop scale in five separate sections present along a strike-distance of 1 km. The thrust zone shows considerable variations in structural style, as well as localization within different clay and limestone horizons. Zones of low and high strain have been identified. We investigate these changes in macroscopic deformation style using Virtual Polarizing Microscopy, and the combined methods of Broad Ion Beam milling and Scanning Electron Microscopy in addition with XRD analysis. We characterize structural and mineralogical variations in the thrust zone at all scales, from outcrop down to nano-meters. Results show strain localization is heterogeneous, with strong variations along strike. Within the clay package, strain localizes along zones rich in organic matter. Microstructures are complex, and show multiple deformation events, including crack-seal processes and reworking of vein material. Pressure solution is dominant. XRD analysis shows mineralogical differences between zones of high and low strain within the shale-dominated package. However, highest strain does not only occur in the clay units, but partly is accommodated in the surrounding limestone.

Zeta-potential and particle size studies of silver sulphide nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sharma, Vikash, E-mail: vikash@csr.res.in; Tarachand,; Ganesan, V.

Silver sulfide (Ag{sub 2}S) nanoparticles (NPs) were prepared successfully for the first time using diethylene glycol (DEG) as a surfactant. X-ray diffraction (XRD) data revealed single phase nature of the compound and energy-dispersive X-ray (EDX) confirmed its nominal composition. Their sizes were 43 nm from XRD, 50 nm from atomic force microscopy (AFM) and 19 nm & 213 nm from dynamic light scattering (DLS); their differences have been discussed. Autotitration study of zeta potential of these NPs in deionized water by DLS at different pH values confirmed an isoelectric point at pH = 5.14 and their very unstable nature in deionized water.

Ghana Fiasco Shows Risks of Faculty-Led Study Trips

ERIC Educational Resources Information Center

Fischer, Karin

2007-01-01

This article illustrates the importance of preparation for professors who take students overseas. A University of Washington study-abroad program in Ghana that was cut short last summer after the medical evacuation of half of its participants highlights the potential hazards associated with programs led by individual faculty members who may lack…

Debate over Social Studies Shows Little Sign of Abating

ERIC Educational Resources Information Center

Robelen, Erik W.

2010-01-01

The Texas board of education which consists of 15-member elected body drew national attention as a bloc of staunch conservatives largely succeeded in putting its stamp on a revised set of social studies standards. The debate was marked by tussles over such matters as the separation of church and state, the representation of minority figures and…

Studies Show Steps to More Success Planting Oak Forests

Treesearch

Robert L. Johnson

1986-01-01

As Ann Nestelroad observes in a preceding article, acorns sown 6 inches deep can germinate and produce seedlings. I believe, however, that the best oak establishment comes from acorns sown 1 to 2 inches deep in open areas. Deep sowing does not substantially reduce acorn depredation by rodents, but two ongoing studies at Stoneville, Mississippi, indicate that sowing in...

A study on the morphology of polystyrene-grafted poly(ethylene-alt-tetrafluoroethylene) (ETFE) films prepared using a simultaneous radiation grafting method

NASA Astrophysics Data System (ADS)

Song, Ju-Myung; Ko, Beom-Seok; Sohn, Joon-Yong; Nho, Young Chang; Shin, Junhwa

2014-04-01

The morphology of polystyrene-grafted poly(ethylene-alt-tetrafluoroethylene) (ETFE) films prepared using a simultaneous radiation grafting method was investigated using DMA, DSC, XRD, and SAXS instruments. The DMA study indicates that the ETFE amorphous phase and PS amorphous phase are mixed well in the PS-grafted ETFE films while the ETFE crystalline phase and the PS amorphous phase are separated, suggesting that the PS chains are grafted mainly on the ETFE amorphous regions. The DSC and XRD data showed that the natural crystalline structures of ETFE in the grafted ETFE films are not affected by the degree of grafting. The SAXS profiles displayed that the inter-crystalline distance of the ETFE films increases with an increasing degree of grafting, which further implies that the PS graft chains formed by the simultaneous irradiation has a significant impact on the amorphous morphology of the resulting grafted ETFE film. Thus, these results indicate that the styrene monomers are mainly grafted on the ETFE amorphous regions during the simultaneous radiation grafting process.

Physics Reality Show

NASA Astrophysics Data System (ADS)

Erukhimova, Tatiana

The attention span of K-12 students is very short; they are used to digesting information in short snippets through social media and TV. To get the students interested in physics, we created the Physics Reality Show: a series of staged short videos with duration no longer than a few minutes. Each video explains and illustrates one physics concept or law through a fast-paced sequence of physics demonstrations and experiments. The cast consists entirely of physics undergraduate students with artistic abilities and substantial experience in showing physics demonstrations at current outreach events run by the department: Physics Shows and Physics & Engineering Festival. Undergraduate students are of almost the same age as their high-school audience. They are in the best position to connect with kids and convey their fascination with physics. The PI and other faculty members who are involved in the outreach advise and coach the cast. They help students in staging the episodes and choosing the most exciting and relevant demonstrations. Supported by the APS mini-outreach Grant.

The effect of doped zinc on the structural properties of nano-crystalline (Se0.8Te0.2)100-xZnx

NASA Astrophysics Data System (ADS)

Kumar, Arun; Singh, Harkawal; Gill, P. S.; Goyal, Navdeep

2016-05-01

The effect of metallic zinc (Zn) on the structural properties of (Se0.8Te0.2)1-XZnX (x=0, 2, 6, 8, 10) samples analyzed by X-ray Diffraction (XRD). The presence of sharp peaks in XRD patterns confirmed the crystalline nature of the samples and is indexed in orthorhombic crystal structure. XRD studies predicts that the average particle size of all the samples are about 46.29 nm, which is less than 100 nm and hence have strong tendency of agglomeration. Williamson-Hall plot method was used to evaluate the lattice strain. The dislocation density and no. of unit cells of the samples were calculated which show the inverse relation with each other. Morphology index derived from FWHM of XRD data explains the direct relationship with the particle size.

Crystallization processes in Ge{sub 2}Sb{sub 2}Se{sub 4}Te glass

DOE Office of Scientific and Technical Information (OSTI.GOV)

Svoboda, Roman, E-mail: roman.svoboda@upce.cz; Bezdička, Petr; Gutwirth, Jan

2015-01-15

Highlights: • Crystallization kinetics of Ge{sub 2}Sb{sub 2}Se{sub 4}Te glass was studied in dependence on particle size by DSC. • All studied fractions were described in terms of the SB autocatalytic model. • Relatively high amount of Te enhances manifestation of bulk crystallization mechanisms. • XRD analysis of samples crystallized under different conditions showed correlation with DSC data. • XRD analysis revealed a new crystallization mechanism indistinguishable by DSC. - Abstract: Differential scanning calorimetry (DSC) and X-ray diffraction (XRD) analysis were used to study crystallization in Ge{sub 2}Sb{sub 2}Se{sub 4}Te glass under non-isothermal conditions as a function of the particlemore » size. The crystallization kinetics was described in terms of the autocatalytic Šesták–Berggren model. An extensive discussion of all aspects of a full-scale kinetic study of a crystallization process was undertaken. Dominance of the crystallization process originating from mechanically induced strains and heterogeneities was confirmed. Substitution of Se by Te was found to enhance the manifestation of the bulk crystallization mechanisms (at the expense of surface crystallization). The XRD analysis showed significant dependence of the crystalline structural parameters on the crystallization conditions (initial particle size of the glassy grains and applied heating rate). Based on this information, a new microstructural crystallization mechanism, indistinguishable by DSC, was proposed.« less

Optimization Study of Pulsed DC Nitrogen-Hydrogen Plasma in the Presence of an Active Screen Cage

NASA Astrophysics Data System (ADS)

Saeed, A.; W. Khan, A.; F., Jan; U. Shah, H.; Abrar, M.; Zaka-Ul-Islam, M.; Khalid, M.; Zakaullah, M.

2014-05-01

A glow discharge plasma nitriding reactor in the presence of an active screen cage is optimized in terms of current density, filling pressure and hydrogen concentrations using optical emission spectroscopy (OES). The samples of AISI 304 are nitrided for different treatment times under optimum conditions. The treated samples were analyzed by X-ray diffraction (XRD) to explore the changes induced in the crystallographic structure. The XRD pattern confirmed the formation of iron and chromium nitrides arising from incorporation of nitrogen as an interstitial solid solution in the iron lattice. A Vickers microhardness tester was used to evaluate the surface hardness as a function of treatment time (h). The results showed clear evidence of improved surface hardness and a substantial amount of decrease in the treatment time compared with the previous work.

Influence of gamma irradiation on the surface morphology, XRD and thermophysical properties of silicide hexoboride

NASA Astrophysics Data System (ADS)

Mirzayev, Matlab N.; Mehdiyeva, Ravan N.; Garibov, Ramin G.; Ismayilova, Narmin A.; Jabarov, Sakin H.

2018-05-01

In this study, compounds of B6Si were irradiated using a 60Co gamma source that have an energy line of 1.25 MeV at the absorbed dose rates from 14.6 kGy to 194.4 kGy. Surface morphology images of the sample obtained by Scanning Electron Microscope (SEM) show that the crystal structure at a high absorbed doses (D ≥ 145.8kGy) starts to be destroyed. X-ray diffraction studies revealed that with increasing radiation absorption dose, the spectrum intensity of the sample was decreased 1.96 times compared with the initial value. Thermal properties were studied by Differential scanning calorimetry (DSC) method in the temperature range of 30-1000∘C.

Feasibility study on cross-linked biopolymeric concrete encapsulating selenium glass wastes.

PubMed

Kim, Daeik; Park, Joon-Seok; Yen, Teh Fu

2012-08-01

Feasibility study was conducted to encapsulate the selenium (Se) contained in glass waste, using the biopolymer-modified concrete. Biopolymer has unique characteristics to provide the chemical sites to metals or toxic compounds through the three-dimensional cross-linked structure. Very minute amount of biopolymer enhanced the characteristics of cementitious material. The resulting biopolymeric composite with selenium glass waste showed 20% higher compressive strength than ordinary concrete and the lower leaching concentration than the equipment detection limit. For a qualitative measurement, X-ray diffraction (XRD; X-ray powder diffractogram) was used to characterize the biopolymeric concrete. The optimum waste content percentage with appropriate biopolymer concrete mixture ratio was identified for its possible commercial use.

Structure and luminescence properties of Tb3+-doped Lu3Al5O12 films prepared by Pechini sol-gel method

NASA Astrophysics Data System (ADS)

Wang, Jian; Shen, Siqing; Xie, Jianjun; Shi, Ying; Ai, Fei

2011-02-01

Tb3+-doped Lu3Al5O12(hereinafter referred to as LuAG:Tb) films were successfully prepared by Pechini sol-gel process and spin-coating technique on carefully cleaned (111) silicon wafer. The microstructure and optical properties of the LuAG:Tb films were studied by X-ray diffraction (XRD), atomic force microscopy(AFM), as well as photoluminescence (PL) spectra. The XRD results showed that the precursor films started to crystallize at about 900°C. All as-calcined LuAG:Tb films showed the Tb3+ characteristic emission bands.

Structure and luminescence properties of Tb3+-doped Lu3Al5O12 films prepared by Pechini sol-gel method

NASA Astrophysics Data System (ADS)

Wang, Jian; Shen, Siqing; Xie, Jianjun; Shi, Ying; Ai, Fei

2010-10-01

Tb3+-doped Lu3Al5O12(hereinafter referred to as LuAG:Tb) films were successfully prepared by Pechini sol-gel process and spin-coating technique on carefully cleaned (111) silicon wafer. The microstructure and optical properties of the LuAG:Tb films were studied by X-ray diffraction (XRD), atomic force microscopy(AFM), as well as photoluminescence (PL) spectra. The XRD results showed that the precursor films started to crystallize at about 900°C. All as-calcined LuAG:Tb films showed the Tb3+ characteristic emission bands.

Decreasing Ni, Cu, Cd, and Zn heavy metal magnetite-bentonite nanocomposites and adsorption isotherm study

NASA Astrophysics Data System (ADS)

Eskandari, M.; Zakeri Khatir, M.; Khodadadi Darban, A.; Meshkini, M.

2018-04-01

This present study was conducted to investigate the effect of magnetite-bentonite nanocomposite on heavy metal removal from an effluent. For this purpose, magnetite-bentonite nanocomposite was prepared through the chemical method and characterized using x-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques, followed by studying the effect of produced nanocomposite on the removal of Ni2+, Cu2+, Cd2+, and Zn2+ heavy metal ions. The results showed that adsorption capacity of magnetite-bentonite nanocomposites for the studied ions is in the order of Zn2+ > Cd2+ > Cu2+ > Ni2+. Adsorption isotherms were drawn for Ni2+, Cu2+, Cd2+, and Zn2+ cations and found that cations adsorption on nanocomposite fit into Langmuir model.

Zeta potential and Raman studies of PVP capped Bi2S3 nanoparticles synthesized by polyol method

NASA Astrophysics Data System (ADS)

Tarachand, Sathe, Vasant G.; Okram, Gunadhor S.

2018-05-01

Here we report the synthesis and characterisation of polyvinylpyrrolidone (PVP) capped Bi2S3 nanoparticles via one step catalyst-free polyol method. Raman spectroscopy, dynamic light scattering and zeta potential analysis were performed on it. Rietveld refinement of powder XRD of PVP capped samples confirmed the formation of single phase orthorhombic Bi2S3 for all PVP capped samples. The presence of eight obvious Raman modes further confirmed the formation of stoichiometric Bi2S3. Dynamic light scattering (DLS) studies show a clear increase in hydrodynamic diameter for samples made with increasing PVP concentration. Particle size obtained from DLS and XRD (using Scherrer's formula) combine with change in full width half maxima of Raman modes collectively suggest overall improvement in crystallinity and quality of product on introducing PVP. In zeta potential (ζ) measurement, steric hindrance of carbon chains plays very crucial role and a systematic reduction of ζ value is observed for samples made with decreasing PVP concentration. An isoelectric point is obtained for sample made with low PVP (1g). Present results are likely to open a window for its medical and catalytic applications.

Study of nanoparticles TiO2 thin films on p-type silicon substrate using different alcoholic solvents

NASA Astrophysics Data System (ADS)

Muaz, A. K. M.; Hashim, U.; Arshad, M. K. Md.; Ruslinda, A. R.; Ayub, R. M.; Gopinath, Subash C. B.; Voon, C. H.; Liu, Wei-Wen; Foo, K. L.

2016-07-01

In this paper, sol-gel method spin coating technique is adopted to prepare nanoparticles titanium dioxide (TiO2) thin films. The prepared TiO2 sol was synthesized using titanium butoxide act as a precursor and subjected to deposited on the p-type silicon oxide (p-SiO2) and glass slide substrates under room temperature. The effect of different alcoholic solvents of methanol and ethanol on the structural, morphological, optical and electrical properties were systematically investigated. The coated TiO2 thin films were annealed in furnace at 773 K for 1 h. The structural properties of the TiO2 films were examined with X-ray Diffraction (XRD). From the XRD analysis, both solvents showing good crystallinity with anatase phase were the predominant structure. Atomic Force Microscopy (AFM) was employed to study the morphological of the thin films. The optical properties were investigated by Ultraviolet-visible (UV-Vis) spectroscopy were found that ethanol as a solvent give a higher optical transmittance if compare to the methanol solvent. The electrical properties of the nanoparticles TiO2 thin films were measured using two-point-probe technique.

The Effect of Compaction Force on the Transition to Hydrate of Anhydrous Aripiprazole.

PubMed

Togo, Taichiro; Taniguchi, Toshiya; Nakata, Yoshitaka

2018-01-01

Aripiprazole (APZ) is used to treat schizophrenia and is administered as a tablet containing the anhydrous form of APZ. In this study, the effect of compaction force on the crystal form transition was investigated. The crystalline state was observed by X-ray diffraction (XRD). APZ Anhydrous Form II was compacted into tablets. The XRD intensity of anhydrous APZ became lower with higher compressive force. The degree of crystallinity decreased with the compaction force. The powder and the compacted tablets of anhydrous APZ were stored for one week under 60°C and 75% relative humidity. The powder showed no crystal form transition after storage. For the tablets, however, XRD peaks of APZ hydrate were observed after storage. The tablets compacted with higher force showed the higher XRD diffraction intensity of hydrate form. We concluded that the crystallinity reduction of APZ Anhydrous Form II by compaction caused and accelerated the transition to hydrate under high temperature and humidity conditions. In order to manufacture crystallographically stable tablets containing anhydrous APZ, it is important to prevent this crystallinity reduction during compaction.

Study on the structural, optical, and electrical properties of the yellow light-emitting diode grown on free-standing (0001) GaN substrate

NASA Astrophysics Data System (ADS)

Deng, Gaoqiang; Zhang, Yuantao; Yu, Ye; Yan, Long; Li, Pengchong; Han, Xu; Chen, Liang; Zhao, Degang; Du, Guotong

2018-04-01

In this paper, GaN-based yellow light-emitting diodes (LEDs) were homoepitaxially grown on free-standing (0001) GaN substrates by metal-organic chemical vapor deposition. X-ray diffraction (XRD), photoluminescence (PL), and electroluminescence (EL) measurements were conducted to investigate the structural, optical, and electrical properties of the yellow LED. The XRD measurement results showed that the InGaN/GaN multiple quantum wells (MQWs) in the LED structure have good periodicity because the distinct MQWs related higher order satellite peaks can be clearly observed from the profile of 2θ-ω XRD scan. The low temperature (10 K) and room temperature PL measurement results yield an internal quantum efficiency of 16% for the yellow LED. The EL spectra of the yellow LED present well Gaussian distribution with relatively low linewidth (47-55 nm), indicating the homogeneous In-content in the InGaN quantum well layers in the yellow LED structure. It is believed that this work will aid in the future development of GaN on GaN LEDs with long emission wavelength.

Study of free radicals in gamma irradiated cellulose of cultural heritage materials using Electron Paramagnetic Resonance

NASA Astrophysics Data System (ADS)

Kodama, Yasko; Rodrigues, Orlando, Jr.; Garcia, Rafael Henrique Lazzari; Santos, Paulo de Souza; Vasquez, Pablo A. S.

2016-07-01

Main subject of this article was to study room temperature stable radicals in Co-60 gamma irradiated contemporary paper using Electron Paramagnetic Resonance spectrometer (EPR). XRD was used to study the effect of ionizing radiation on the morphology of book paper. SEM images presented regions with cellulose fibers and regions with particles agglomeration on the cellulose fibers. Those agglomerations were rich in calcium, observed by EDS. XRD analysis confirmed presence of calcium carbonate diffraction peaks. The main objective of this study was to propose a method using conventional kinetics chemical reactions for the observed radical formed by ionizing radiation. Therefore, further analyses were made to study the half-life and the kinetics of the free radical created. This method can be suitably applied to study radicals on cultural heritage objects.

Spectral properties of Dy3+ doped ZnAl2O4 phosphor

NASA Astrophysics Data System (ADS)

Prakash, Ram; Kumar, Sandeep; Mahajan, Rubby; Khajuria, Pooja; Kumar, Vinay; Choudhary, R. J.; Phase, D. M.

2018-05-01

Herein, Dy3+ doped ZnAl2O4 phosphor was synthesized by the solution combustion method. The synthesized phosphor was characterized by X-ray diffraction (XRD), photoluminescence (PL) spectroscopy, UV-Vis spectroscopy and X-ray photoelectron spectroscopy (XPS). The phase purity of the phosphor was confirmed by the XRD studies that showed cubic symmetry of the synthesized phosphor. Under UV excitation (388 nm) the PL emission spectrum of the phosphor shows characteristic transition from the Dy3+ ion. A band gap of 5.2 eV was estimated from the diffused reflectance spectroscopy. The surface properties of the phosphor were studied using the X-ray photoelectron spectroscopy.

Comparative study of biogenic and abiotic iron-containing materials

NASA Astrophysics Data System (ADS)

Cherkezova-Zheleva, Z.; Shopska, M.; Paneva, D.; Kovacheva, D.; Kadinov, G.; Mitov, I.

2016-12-01

Series of iron-based biogenic materials prepared by cultivation of Leptothrix group of bacteria in different feeding media ( Sphaerotilus-Leptothrix group of bacteria isolation medium, Adler, Lieske and silicon-iron-glucose-peptone) were studied. Control samples were obtained in the same conditions and procedures but the nutrition media were not infected with bacteria, i.e. they were sterile. Room and low temperature Mössbauer spectroscopy, powder X-ray diffraction (XRD), and infrared spectroscopy (IRS) were used to reveal the composition and physicochemical properties of biomass and respective control samples. Comparative analysis showed differences in their composition and dispersity of present phases. Sample composition included different ratio of nanodimensional iron oxyhydroxide and oxide phases. Relaxation phenomena such as superparamagnetism or collective magnetic excitation behaviour were registered for some of them. The experimental data showed that the biogenic materials were enriched in oxyhydroxides of high dispersion. Catalytic behaviour of a selected biomass and abiotic material were studied in the reaction of CO oxidation. In situ diffuse-reflectance (DR) IRS was used to monitor the phase transformations in the biomass and CO conversion.

Inhibition and quenching effect on positronium formation in metal salt doped polymer blend

NASA Astrophysics Data System (ADS)

Praveena, S. D.; Ravindrachary, V.; Ismayil, Bhajantri, R. F.; Harisha, A.; Guruswamy, B.; Hegde, Shreedatta; Sagar, Rohan N.

2018-04-01

Sodium Bromide (NaBr) doped PVA/PVP (50:50) polymer blend composites were prepared using solution casting technique. Pure PVA/PVP blend and PVA/PVP:NaBr composites were studied using XRD and Positron Annihilation Lifetime Spectroscopy (PALS). XRD study shows increase in amorphous nature of the blend due to the NaBr dopant and PALS studies reveal that the o-Ps lifetime (τ3) and intensity (I3) decreases with increase in NaBr doping level. This shows chemical quenching and inhibition process of positronium (Ps) formation in the composite. Here the electron acceptor (Br-) acts as a strong chemical quencher for positronium formation and same is understood based on the spur model.

Dissemination of a Web-Based Tool for Supporting Health Insurance Plan Decisions (Show Me Health Plans): Cross-Sectional Observational Study.

PubMed

Zhao, Jingsong; Mir, Nageen; Ackermann, Nicole; Kaphingst, Kimberly A; Politi, Mary C

2018-06-20

The rate of uninsured people has decreased dramatically since the Affordable Care Act was passed. To make an informed decision, consumers need assistance to understand the advantages and disadvantages of health insurance plans. The Show Me Health Plans Web-based decision support tool was developed to improve the quality of health insurance selection. In response to the promising effectiveness of Show Me Health Plans in a randomized controlled trial (RCT) and the growing need for Web-based health insurance decision support, the study team used expert recommendations for dissemination and implementation, engaged external stakeholders, and made the Show Me Health Plans tool available to the public. The purpose of this study was to implement the public dissemination of the Show Me Health Plans tool in the state of Missouri and to evaluate its impact compared to the RCT. This study used a cross-sectional observational design. Dissemination phase users were compared with users in the RCT study across the same outcome measures. Time spent using the Show Me Health Plans tool, knowledge, importance rating of 9 health insurance features, and intended plan choice match with algorithm predictions were examined. During the dissemination phase (November 2016 to January 2017), 10,180 individuals visited the SMHP website, and the 1069 users who stayed on the tool for more than one second were included in our analyses. Dissemination phase users were more likely to live outside St. Louis City or County (P<.001), were less likely to be below the federal poverty level (P<.001), and had a higher income (P=.03). Overall, Show Me Health Plans users from St. Louis City or County spent more time on the Show Me Health Plans tool than those from other Missouri counties (P=.04); this association was not observed in the RCT. Total time spent on the tool was not correlated with knowledge scores, which were associated with lower poverty levels (P=.009). The users from the RCT phase were more

Structural and magnetic studies of half-metallic Heusler alloy Cr2CoSi nanoparticle synthesized by mechanical-alloying method

NASA Astrophysics Data System (ADS)

Saravanan, G.; Asvini, V.; Kalaiezhily, R. K.; Ravichandran, K.

2018-05-01

Heusler Alloy based Cr2CoSi nanoparticles were synthesized by using ball milling. X-ray diffractions studies were used to characterize the crystal structure of Cr2CoSi nanoparticles and magnetic properties were studied using VSM. XRD data analysis confirms the Heusler alloy phase showing the L21 structure. Magnetic properties are measured for synthesized samples having coercivity Hc = 389 Oe, with high saturation magnetization value Ms = 8.64 emu/g and remenance value Mr = 2.93 emu/g. Synthesized Heusler alloy Cr2CoSi nanoparticles can be potential materials for use in Spin polarized based spin sensors, spin devices, magnetic sensors and transducer applications.

Accessibility of Enzymatically Delignified Bambusa bambos for Efficient Hydrolysis at Minimum Cellulase Loading: An Optimization Study.

PubMed

Kuila, Arindam; Mukhopadhyay, Mainak; Tuli, D K; Banerjee, Rintu

2011-01-01

In the present investigation, Bambusa bambos was used for optimization of enzymatic pretreatment and saccharification. Maximum enzymatic delignification achieved was 84%, after 8 h of incubation time. Highest reducing sugar yield from enzyme-pretreated Bambusa bambos was 818.01 mg/g dry substrate after 8 h of incubation time at a low cellulase loading (endoglucanase, β-glucosidase, exoglucanase, and xylanase were 1.63 IU/mL, 1.28 IU/mL, 0.08 IU/mL, and 47.93 IU/mL, respectively). Enzyme-treated substrate of Bambusa bambos was characterized by analytical techniques such as Fourier transformed infrared spectroscopy (FTIR), X-ray diffraction (XRD), and scanning electron microscopy (SEM). The FTIR spectrum showed that the absorption peaks of several functional groups were decreased after enzymatic pretreatment. XRD analysis indicated that cellulose crystallinity of enzyme-treated samples was increased due to the removal of amorphous lignin and hemicelluloses. SEM image showed that surface structure of Bambusa bambos was distorted after enzymatic pretreatment.

Geothermal-retrofit study for the National Orange Show Facilities in San Bernardino, California

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1981-11-17

The cost and feasibility of retrofitting the National Orange Show Facilities to use geothermal heat instead of natural gas for heating are determined. Because of the limited usage of the smaller facilities the study was limited to the conversion of the six major buildings: Domed, Hobby, Citrus, Auditorium, Restaurant and Commercial. A major problem is that most of the buildings are used on a very limited basis. This drastically reduced the amount of savings that could be used to amortize the retrofit cost. Another problem is that the buildings are spread over a large area and so the below grademore » piping costs were high. Finally, all of the buildings except for the Auditorium have direct gas fired heaters that would require all new terminal heating systems. In order to limit the retrofit cost, the retrofit system was designed to handle less than the peak load. This seemed appropriate because the facility might not even be in operation when a peak load condition occurred. Also, the existing systems could be used to supplement the geothermal system if necessary. The calculated and design peak loads are summarized.« less

EUropean prospective cohort study on Enterobacteriaceae showing REsistance to CArbapenems (EURECA): a protocol of a European multicentre observational study.

PubMed

Gutiérrez-Gutiérrez, Belén; Sojo-Dorado, Jesús; Bravo-Ferrer, José; Cuperus, Nienke; de Kraker, Marlieke; Kostyanev, Tomislav; Raka, Lul; Daikos, George; Feifel, Jan; Folgori, Laura; Pascual, Alvaro; Goossens, Herman; O'Brien, Seamus; Bonten, Marc J M; Rodríguez-Baño, Jesús

2017-04-03

The rapid worldwide spread of carbapenem-resistant Enterobacteriaceae (CRE) constitutes a major challenge. The aim of the EUropean prospective cohort study on Enterobacteriaceae showing REsistance to CArbapenems (EURECA), which is part of the Innovative Medicines Initiative Joint Undertaking (IMI JU) funded COMBACTE-CARE project, is to investigate risk factors for and outcome determinants of CRE infections to inform randomised clinical trial designs and to provide a historical cohort that could eventually be used for future comparisons with new drugs targeting CRE. A multicentre (50 sites), multinational (11 European countries), analytical observational project was designed, comprising 3 studies. The aims of study 1 (a prospective cohort study) include characterising the features, clinical management and outcomes of hospitalised patients with intra-abdominal infection, pneumonia, complicated urinary tract infections and bloodstream infections caused by CRE (202 patients in each group). The main outcomes will be 30-day all-cause mortality and clinical response. Study 2 (a nested case-control study) will identify the risk factors for target infections caused by CRE; 248 selected patients from study 1 will be matched with patients with carbapenem-susceptible Enterobacteriaceae (1:1) and with hospitalised patients (1:3) and will provide a historical cohort of patients with CRE infections. Study 3 (a matched cohort study) will follow patients in study 2 in order to assess mortality, length of stay and hospital costs associated with CRE. All patients will be followed for 30 days. Different, up-to-date statistical methods will be applied to come to unbiased estimates for all 3 studies. Before-study sites will be initiated, approval will be sought from appropriate regulatory agencies and local Ethics Committees of Research or Institutional Review Boards (IRBs) to conduct the study in accordance with regulatory requirements. This is an observational study and therefore no

Study of nanoparticles TiO{sub 2} thin films on p-type silicon substrate using different alcoholic solvents

DOE Office of Scientific and Technical Information (OSTI.GOV)

Muaz, A. K. M.; Ruslinda, A. R.; Ayub, R. M.

2016-07-06

In this paper, sol-gel method spin coating technique is adopted to prepare nanoparticles titanium dioxide (TiO{sub 2}) thin films. The prepared TiO{sub 2} sol was synthesized using titanium butoxide act as a precursor and subjected to deposited on the p-type silicon oxide (p-SiO{sub 2}) and glass slide substrates under room temperature. The effect of different alcoholic solvents of methanol and ethanol on the structural, morphological, optical and electrical properties were systematically investigated. The coated TiO{sub 2} thin films were annealed in furnace at 773 K for 1 h. The structural properties of the TiO{sub 2} films were examined with X-raymore » Diffraction (XRD). From the XRD analysis, both solvents showing good crystallinity with anatase phase were the predominant structure. Atomic Force Microscopy (AFM) was employed to study the morphological of the thin films. The optical properties were investigated by Ultraviolet-visible (UV-Vis) spectroscopy were found that ethanol as a solvent give a higher optical transmittance if compare to the methanol solvent. The electrical properties of the nanoparticles TiO{sub 2} thin films were measured using two-point-probe technique.« less

Genotype-Phenotype Study of the Middle Gangetic Plain in India Shows Association of rs2470102 with Skin Pigmentation.

PubMed

Mishra, Anshuman; Nizammuddin, Sheikh; Mallick, Chandana Basu; Singh, Sakshi; Prakash, Satya; Siddiqui, Niyamat Ali; Rai, Niraj; Carlus, S Justin; Sudhakar, Digumarthi V S; Tripathi, Vishnu P; Möls, Märt; Kim-Howard, Xana; Dewangan, Hemlata; Mishra, Abhishek; Reddy, Alla G; Roy, Biswajit; Pandey, Krishna; Chaubey, Gyaneshwer; Das, Pradeep; Nath, Swapan K; Singh, Lalji; Thangaraj, Kumarasamy

2017-03-01

Our understanding of the genetics of skin pigmentation has been largely skewed towards populations of European ancestry, imparting less attention to South Asian populations, who behold huge pigmentation diversity. Here, we investigate skin pigmentation variation in a cohort of 1,167 individuals in the Middle Gangetic Plain of the Indian subcontinent. Our data confirm the association of rs1426654 with skin pigmentation among South Asians, consistent with previous studies, and also show association for rs2470102 single nucleotide polymorphism. Our haplotype analyses further help us delineate the haplotype distribution across social categories and skin color. Taken together, our findings suggest that the social structure defined by the caste system in India has a profound influence on the skin pigmentation patterns of the subcontinent. In particular, social category and associated single nucleotide polymorphisms explain about 32% and 6.4%, respectively, of the total phenotypic variance. Phylogeography of the associated single nucleotide polymorphisms studied across 52 diverse populations of the Indian subcontinent shows wide presence of the derived alleles, although their frequencies vary across populations. Our results show that both polymorphisms (rs1426654 and rs2470102) play an important role in the skin pigmentation diversity of South Asians. Copyright © 2016 The Authors. Published by Elsevier Inc. All rights reserved.

The structural and Raman spectral studies on Ni0.5Cu0.5Fe2O4 ferrite

NASA Astrophysics Data System (ADS)

Somani, M.; Saleem, M.

2018-05-01

Spinel ferrite Ni0.5Cu0.5Fe2O4 has been successfully prepared via solid state reaction. The crystal structure studies using XRD technique revealed cubic structure of the sample. The XRD spectra was further refined via Retvield Refinement and all the parameters regarding structure were obtained which confirmed cubic structure. The assigned space group was found to be Fd-3m. Particle size was calculated to be 56 nm. The Raman Spectra revealed five active Raman modes which confirmed spinel structure.

Adsorption studies of heavy metal ions on mesoporous aluminosilicate, novel cation exchanger.

PubMed

Sepehrian, H; Ahmadi, S J; Waqif-Husain, S; Faghihian, H; Alighanbari, H

2010-04-15

Mesoporous aluminosilicates, have been prepared with various mole ratios of Si/Al and Cethyltrimethylammonium bromide (CTAB). They have been characterized by XRD, nitrogen adsorption/desorption measurements, FT-IR and thermogravimetry. Adsorption behavior of heavy metal ions on this adsorbent have been studied and discussed. The results show that incorporation of aluminum ions in the framework of the mesoporous MCM-41 has transformed it into an effective cation exchanger. The K(d) values of several metal ions have been increased. Separation of Sr(II)-Ce(III), Sr(II)-U(VI) and Cd(II)-Ce(III) has been developed on columns of this novel mesoporous cation exchanger. 2009 Elsevier B.V. All rights reserved.

In vitro studies to show sequestration of matrix metalloproteinases by silver-containing wound care products.

PubMed

Walker, Michael; Bowler, Philip G; Cochrane, Christine A

2007-09-01

Excess or "uncontrolled" proteinase activity in the wound bed has been implicated as one factor that may delay or compromise wound healing. One proteinase group--matrix metalloproteinases--includes collagenases, elastase, and gelatinases and can be endogenous (cell) or exogenous (bacterial) in origin. A study was conducted to assess the ability of five silver-containing wound care products to reduce a known matrix metalloproteinase supernatant concentration in vitro. Four silver-containing wound dressings (a carboxy-methyl cellulose, a nanocrystalline, a hydro-alginate, and a collagen/oxidized regenerated cellulose composite dressing), along with a 0.5% aqueous silver nitrate [w/v] solution and controls for matrix metalloproteinase-2 and matrix metalloproteinase-9 sourced from ex vivo dermal tissue and blood monocytes, respectively, were used. Extracts were separated and purified using gelatine-Sepharose column chromatography and dialysis and polyacrylamide gel electrophoretic zymography was used to analyze specific matrix metalloproteinase activity. All dressings and the solution were shown to sequester both matrix metalloproteinases. The silver-containing carboxy-methyl cellulose dressing showed significantly greater sequestration for matrix metalloproteinase-2 at 6 and 24 hours (P< 0.001) compared to the other treatments. For matrix metalloproteinase-9, both the carboxy-methyl cellulose dressing and the oxidized regenerated cellulose dressing achieved significant sequestration when compared to the other treatments at 24 hours (P <0.001), which was maintained to 48 hours (P < 0.001). Results from this study show that silver-containing dressings are effective in sequestering matrix metalloproteinase-2 and -9 and that this can be achieved without a sacrificial protein (eg, collagen). Although the varying ability of wound dressings to sequester matrix metalloproteinases has been shown in vitro, further in vivo evidence is required to confirm these findings.

Structural, morphological and optical studies of ripple-structured ZnO thin films

NASA Astrophysics Data System (ADS)

Navin, Kumar; Kurchania, Rajnish

2015-11-01

Ripple-structured ZnO thin films were prepared on Si (100) substrate by sol-gel spin-coating method with different heating rates during preheating process and finally sintered at 500 °C for 2 h in ambient condition. The structural, morphological and photoluminescence (PL) properties of the nanostructured films were analyzed by X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM) and PL spectroscopy. XRD analysis revealed that films have hexagonal wurtzite structure and texture coefficient increases along (002) plane with preheating rate. The faster heating rate produced higher crystallization and larger average crystallite size. The AFM and SEM images indicate that all the films have uniformly distributed ripple structure with skeletal branches. The number of ripples increases, while the rms roughness, amplitude and correlation length of the ripple structure decrease with preheating rates. The PL spectra show the presence of different defects in the structure. The ultraviolet emission improved with the heating rate which indicates its better crystallinity.

Synthesis, characterization, bioactivity and antibacterial studies of silver doped calcium borosilicate glass-ceramics

NASA Astrophysics Data System (ADS)

Kumar, Alesh; Mariappan, C. R.

2018-04-01

Bioactive glass-ceramics 45.8 mol% SiO- 45.8 CaO - 8.4 B2O3 doped with Ag2O were synthesized by sol-gel method. The glass-ceramic nature of samples was confirmed by X-ray diffraction (XRD) and transmission electron microscopy (TEM) analysis. Fourier transform infrared (FT-IR) spectra reveal the probable stretching and bending vibration modes of silicate and borate groups. UV-Visible spectra reveal the presence of Ag+ ions and metallic Ag in the glass matrix for Ag2O doped ceramic sample. Biocompatibility of the glass nature of samples was studied by soaking of samples in Dulbecco's Modified Eagle's Medium (DMEM) with subsequent XRD studies. It was found that bone-like apatite formation on the glasses after soaked in DMEM. Antibacterial studies of glass ceramics powder against gram positive and negative microorganisms were carried out.

Temperature dependent and applied field strength dependent magnetic study of cobalt nickel ferrite nano particles: Synthesized by an environmentally benign method

NASA Astrophysics Data System (ADS)

Sontu, Uday Bhasker; G, Narsinga Rao; Chou, F. C.; M, V. Ramana Reddy

2018-04-01

Spinel ferrites have come a long way in their versatile applications. The ever growing applications of these materials demand detailed study of material properties and environmental considerations in their synthesis. In this article, we report the effect of temperature and applied magnetic field strength on the magnetic behavior of the cobalt nickel ferrite nano powder samples. Basic structural properties of spinel ferrite nano particles, that are synthesized by an environmentally benign method of auto combustion, are characterized through XRD, TEM, RAMAN spectroscopy. Diffuse Reflectance Spectroscopy (DRS) is done to understand the nickel substitution effect on the optical properties of cobalt ferrite nano particles. Thermo magnetic studies using SQUID in the temperature range 5 K to 400 K and room temperature (300 K) VSM studies are performed on these samples. Fields of 0Oe (no applied field: ZF), 1 kOe (for ZFC and FC curves), 5 kOe (0.5 T), 50 kOe (5T) (for M-H loop study) are used to study the magnetic behavior of these nano particles. The XRD,TEM analysis suggest 40 nm crystallites that show changes in the cation distribution and phase changes in the spinel structure with nickel substitution. Raman micrographs support phase purity changes and cation redistributions with nickel substitution. Diffuse reflectance study on powder samples suggests two band gap values for nickel rich compounds. The Magnetic study of these sample nano particles show varied magnetic properties from that of hard magnetic, positive multi axial anisotropy and single-magnetic-domain structures at 5 K temperature to soft magnetic core shell like structures at 300 K temperature. Nickel substitution effect is non monotonous. Blocking temperature of all the samples is found to be higher than the values suggested in the literature.

SORPTION OF LEAD ON A RUTHENIUM COMPOUND: A MACROSCOPIC AND MICROSCOPIC STUDY

EPA Science Inventory

The objective of this study was to elucidate the sorption mechanism of Pb on the high-affinity ruthenium compound with time at pH 6 employing batch methods and X-ray absorption fine structure (XAFS) and X-ray diffraction (XRD) spectroscopies. For the spectroscopic studies, Pb so...

Effects of graphene oxide concentration on optical properties of ZnO/RGO nanocomposites and their application to photocurrent generation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Azarang, Majid, E-mail: azarangmajid@gmail.com, E-mail: azarang@phys.usb.ac.ir; Department of Physics, University of Sistan and Baluchestan, 98135-674 Zahedan; Shuhaimi, Ahmad

2014-08-28

The effects of different concentrations of graphene oxide (GO) on the structure and optical properties of ZnO nanoparticles (NPs) were investigated. The nanocomposites were synthesized via the sol-gel method in a gelatin medium. X-ray diffraction patterns (XRD) and Fourier transform infrared spectroscopy indicated that the GO sheets were reduced and changed to reduced GO (RGO) during the calcination of the nanocomposites at 400 °C. In addition, the XRD patterns of the NPs indicated a hexagonal (wurtzite) structure for all the products. Microscopic studies showed that the NPs were decorated and dispersed on the RGO sheets very well. However, these studies revealedmore » that the RGO concentration had an effect on the crystal growth process for the ZnO NPs. Furthermore, these studies showed that the NPs could be grown with a single crystal quality in an optimum RGO concentration. According to the XRD results that were obtained from pure ZnO NPs, the calcinations temperature was decreased by the RGO. UV–vis and room temperature photoluminescence studies showed that the optical properties of the ZnO/RGO nanocomposite were affected by the RGO concentration. Finally, the obtained ZnO/RGO nanocomposite was used to generate a photocurrent. Observations showed that the photocurrent intensity of the nanocomposite was significantly increased by increasing the RGO, with an optimum RGO concentration.« less

Synthesis and photosensor study of as-grown CuZnO thin film by facile chemical bath deposition

NASA Astrophysics Data System (ADS)

Gubari, Ghamdan M. M.; Ibrahim Mohammed S., M.; Huse, Nanasaheb P.; Dive, Avinash S.; Sharma, Ramphal

2018-05-01

We have successfully deposited CuZnO thin film on a glass substrate by facile chemical bath deposition method at 85 °C for 1 hr. Structural, topographical, Optical and Electrical properties of the prepared Thin Films were investigated by XRD, Raman spectrum, AFM, UV-Visible Spectrophotometer and I-V Measurement System respectively. The X-ray diffraction (XRD) pattern confirmed the formation of the CuZnO composition when compared with standard JCPDS card (JCPDF # 75-0576 & # 36-1451). The Raman analysis shows a major peak at 458 cm-1 with E2 (High) vibrational mode. AFM images revealed uniform deposition over an entire glass substrate with 66.2 nm average roughness of the film. From the optical absorption spectrum, clear band edge around ˜407 nm was observed which results in a wide energy band gap of ˜3.04 eV. The electrical properties were measured at room temperature in the voltage range ±5 V, showed a drastic enhancement in current under light illumination with the highest photosensitivity of ˜99.9 % for 260 W.

Study the effect of nitrogen flow rate on tribological properties of tantalum nitride based coatings

NASA Astrophysics Data System (ADS)

Chauhan, Dharmesh B.; Chauhan, Kamlesh V.; Sonera, Akshay L.; Makwana, Nishant S.; Dave, Divyeshkumar P.; Rawal, Sushant K.

2018-05-01

Tantalum Nitride (TaN) based coatings are well-known for their high temperature stability and chemical inertness. We have studied the effect of nitrogen flow rate variation on the structural and tribological properties of TaN based coating deposited by RF magnetron sputtering process. The nitrogen flow rate was varied from 5 to 30 sccm. X-ray diffractometer (XRD) and Atomic Force Microscopy (AFM) were used to determine structure and surface topography of coating. Pin on disc tribometer was used to determine tribological properties of coating. TaN coated brass and mild steel substrates shows higher wear resistance compared to uncoated substrates of brass and mild steel.

Friedel's salt formation in sulfoaluminate cements: A combined XRD and {sup 27}Al MAS NMR study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Paul, G.; Boccaleri, E., E-mail: enrico.boccaleri@mfn.unipmn.it; Buzzi, L.

Four different binders based on calcium sulfoaluminate cements have been submitted to accelerated chlorination through ionic exchange on hydrated pastes, in order to investigate their ability to chemically bind chloride ions that might reduce chloride penetration. The composition of hydrated cements before and after the treatment was evaluated by means of an X-Ray Diffraction–{sup 27}Al Magic Angle Spinning Nuclear Magnetic Resonance Spectroscopy combined study, allowing to take into account even partially amorphous phases and to make quantitative assumption on the relative abundance of the different aluminium-containing phases. It was found that low SO{sub 3} Sulfoaluminate–Portland ternary systems are the mostmore » effective in binding chloride ions and the active role played by different members of the AFm family in chloride uptake was confirmed. Moreover, a peculiar behavior related to the formation of Friedel's salt in different pH conditions was also established for the different cements.« less

Hydrogen kinetics studies of MgH2-FeTi composites

NASA Astrophysics Data System (ADS)

Meena, Priyanka; Jangir, Mukesh; Singh, Ramvir; Sharma, V. K.; Jain, I. P.

2018-05-01

MgH2 + x wt% FeTi (x=10, 25, 50) nano composites were ball milled to get nano structured material and characterized for structural, morphological and thermal properties. XRD of the milled samples revealed the formation of MgH2, FeTi, Fe2Ti and H0.06FeTi phases. Morphological studies by SEM were undertaken to investigate the effect of hydrogenation of nanostructure alloy. EDX confirmed elemental composition of the as-prepared alloy. TGA studies showed higher desorption temperature for milled MgH2 compared to x wt% FeTi added MgH2. Activation energy for hydrogen desorption was found to be -177.90, -215.69, -162.46 and -87.93 kJ/mol for milled MgH2 and Mg2+x wt% FeTi (10, 25, 50), showing 89.97 kJ/ mol reduction in activation energy for 50 wt% alloy additives resulting in improved hydrogen storage capacity. DSC investigations were carried out to investigate the effect of alloy on hydrogen absorption behavior of MgH2.

Photocatalytic studies of electrochemically synthesized polysaccharide-functionalized ZnO nanoparticles

NASA Astrophysics Data System (ADS)

Kaur, Simranjeet; Kaur, Harpreet

2018-05-01

The present work reports the electrochemical synthesis of polysaccharide-functionalized ZnO nanoparticles using sodium hydroxide, starch, and zinc electrodes for the degradation of cationic dye (Rhodamine-B) under sunlight. Physiochemical properties of synthesized sample have been characterized by different techniques such as XRD, TEM, FESEM, EDS, IR, and UV-visible spectroscopic techniques. The influence of various factors such as effect of dye concentration, contact time, amount of photocatalyst, and pH has been studied. The results obtained from the photodegradation study showed that degradation rate of Rhodamine-B dye has been increased with increase of amount of photocatalyst and decreased with increase in initial dye concentration. Furthermore, the kinetics of the degradation has been investigated. It has been found that the photodegradation of Rhodamine-B dye follows pseudo-first-order kinetics and prepared photocatalyst can effectively degrade the cationic dye. Thus, this ecofriendly and efficient photocatalyst can be used for the treatment of dye-contaminated water. This catalyst also showed the antibacterial activity against Bacillus pumilus and Escherichia coli bacterial strains, so the synthesized nanoparticles also have the pharmaceutical properties.

Synthesis and structural studies of praseodymium doped silver borate glasses

NASA Astrophysics Data System (ADS)

Jagadeesha Gowda, G. V.; Eraiah, B.

2013-02-01

Praseodymium doped silver borate glasses with nominal composition xPr6O11-(25-x)Ag2O-75B2O3 (x=0, 1, 2, 3, 4, 5) were prepared by melt quench technique. XRD pattern shows that there is no sharp peak it confirms the amorphous nature of the present glasses. The glass transition temperature (Tg) of this glass system have been studied using the Matac MBS-8000 Digital Signal Processing and Conventional Thermal Analysis (DTA) method. The Tg of these glasses increases with increase in concentration of Pr6O11 except at 0.2 mol%, Tg value is lower. 11B MAS-NMR shows the presence of sharp peak around 0.306 ppm. Chemical shift of these glasses decreases with mol% of rare earth oxide. FTIR spectra recorded in the region of 400 to 4000 cm-1. This studies revealed that the progressive addition Ag2O and Pr6O11 leads to modification of B2O3 into BO4 groups. Raman measurements of these glasses support the proposed interpretations of the experimental results.

Morphological, structural and thermal studies of gallium nitride ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Indrakanti, Rajani; Rao, V. Brahmaji; Kiran, C. Udaya

2016-05-06

We report the synthesis and Characterization of III-V doped Nano ferrite Ga{sub (2x+2)}N Fe{sub 2(49-x)}O{sub 3} for x=1 and x=5 by Sol-Gel method. The Morphological, structural and Thermal characterisation studies are done by using Transmission Electron Microscopy, Energy Dispersive X-ray Analysis, Selected Area Electron Diffraction, Thermo-Gravimetric Analysis and Differential Thermal Analysis. Using the Sci-Finder software we could not trace any reports related to GaNFe{sub 2}O{sub 3} in the literature. It has been observed from our studies that the particles are in the Cylindrical and the Globular structure. The particle diameter values from the Histograms are in good agreement with themore » XRD values that were communicated by us earlier. The SAED and the EDAX studies reveal the confirmation of the composition and also that the synthesized Ferrite exhibits crystalline nature. The TG-DTA results show that the compound indicates constant sample weight.« less

Study of the thermal treatment of SiO2 aggregate

NASA Astrophysics Data System (ADS)

Tahiri, N.; Khouchaf, L.; Elaatmani, M.; Louarn, G.; Zegzouti, A.; Daoud, M.

2014-08-01

Crystalline quality and the silanoles defects (Si-OH) present within the structure of natural SiO2 play an important role in its reactivity. In this work, the relationship between the loss of silanoles and the crystallinity improvement upon heating between 450 °C and 650 °C was shown using X-Ray Diffraction (XRD) and Fourier Transform mid Infrared Spectroscopy in Attenuated Total Reflection (ATR). A shift of the principal band Si-O-Si from 1078 cm-1 to 1082 cm-1 and the decrease of the intensity of the Si-OH bands at 555cm-1and at 950cm-1 upon heating between 450 °C and 650 °C were shown. The reduction of the band is correlated to the loss of silanoles. In agreement with FT-IR results, the decrease of the FWHM of the XRD peaks shows that the crystalline quality is improved upon heating. This result leads to a decrease of the reactivity of SiO2 aggregate under chemical attacks.

Temperature-dependent vibrational spectroscopy to study order-disorder transitions in charge transfer complexes

NASA Astrophysics Data System (ADS)

Isaac, Rohan; Goetz, Katelyn P.; Roberts, Drew; Jurchescu, Oana D.; McNeil, L. E.

2018-02-01

Charge-transfer (CT) complexes are a promising class of materials for the semiconductor industry because of their versatile properties. This class of compounds shows a variety of phase transitions, which are of interest because of their potential impact on the electronic characteristics. Here temperature-dependent vibrational spectroscopy is used to study structural phase transitions in a set of organic CT complexes. Splitting and broadening of infrared-active phonons in the complex formed between pyrene and pyromellitic dianhydride (PMDA) confirm the structural transition is of the order-disorder type and complement previous x-ray diffraction (XRD) results. We show that this technique is a powerful tool to characterize transitions, and apply it to a range of binary CT complexes composed of polyaromatic hyrdocarbons (anthracene, perylene, phenanthrene, pyrene, and stilbene) and PMDA. We extend the understanding of transitions in perylene-PMDA and pyrene-PMDA, and show that there are no order-disorder transitions present in anthracene-PMDA, stilbene-PMDA and phenanthrene-PMDA in the temperature range investigated here.

Transformation of meta-stable calcium silicate hydrates to tobermorite: reaction kinetics and molecular structure from XRD and NMR spectroscopy

PubMed Central

2009-01-01

Understanding the integrity of well-bore systems that are lined with Portland-based cements is critical to the successful storage of sequestered CO2 in gas and oil reservoirs. As a first step, we investigate reaction rates and mechanistic pathways for cement mineral growth in the absence of CO2 by coupling water chemistry with XRD and NMR spectroscopic data. We find that semi-crystalline calcium (alumino-)silicate hydrate (Al-CSH) forms as a precursor solid to the cement mineral tobermorite. Rate constants for tobermorite growth were found to be k = 0.6 (± 0.1) × 10-5 s-1 for a solution:solid of 10:1 and 1.6 (± 0.8) × 10-4 s-1 for a solution:solid of 5:1 (batch mode; T = 150°C). This data indicates that reaction rates for tobermorite growth are faster when the solution volume is reduced by half, suggesting that rates are dependent on solution saturation and that the Gibbs free energy is the reaction driver. However, calculated solution saturation indexes for Al-CSH and tobermorite differ by less than one log unit, which is within the measured uncertainty. Based on this data, we consider both heterogeneous nucleation as the thermodynamic driver and internal restructuring as possible mechanistic pathways for growth. We also use NMR spectroscopy to characterize the site symmetry and bonding environment of Al and Si in a reacted tobermorite sample. We find two [4]Al coordination structures at δiso = 59.9 ppm and 66.3 ppm with quadrupolar product parameters (PQ) of 0.21 MHz and 0.10 MHz (± 0.08) from 27Al 3Q-MAS NMR and speculate on the Al occupancy of framework sites by probing the protonation environment of Al metal centers using 27Al{1H}CP-MAS NMR. PMID:19144195

Study of irradiation induced surface pattern and structural changes in Inconel 718 alloy

NASA Astrophysics Data System (ADS)

Wan, Hao; Si, Naichao; Zhao, Zhenjiang; Wang, Jian; Zhang, Yifei

2018-05-01

Helium ions irradiation induced surface pattern and structural changes of Inconel 718 alloy were studied with the combined utilization of atomic force microscopy (AFM), x-ray diffraction (XRD) and transmission electron microscopy (TEM). In addition, SRIM-2013 software was used to calculate the sputtering yield and detailed collision events. The result shows that, irradiation dose play an important role in altering the pattern of the surface. Enhanced irradiation aggravated the surface etching and increased the surface roughness. In ion irradiated layer, large amount of interstitials, vacancies and defect sinks were produced. Moreover, in samples with increasing dose irradiation, the dependence of interplanar spacing variation due to point defects clustering on sink density was discussed.

Molecular self-assembly in substituted alanine derivatives: XRD, Hirshfeld surfaces and DFT studies

NASA Astrophysics Data System (ADS)

Rajalakshmi, Periasamy; Srinivasan, Navaneethakrishnan; Sivaraman, Gandhi; Razak, Ibrahim Abdul; Rosli, Mohd Mustaqim; Krishnakumar, Rajaputi Venkatraman

2014-06-01

The molecular assemblage in the crystal structures of three modified chiral amino acids, two of which are isomeric D- and L-pairs boc-L-benzothienylalanine (BLA), boc-D-benzothienylalanine (BDA) and the other boc-D-naphthylalanine (NDA) differing from this pair very slightly in the chemical modification introduced, is accurately described. The aggregation of amino acid molecules is similar in all the crystals and may be described as a twisted double helical ladder in which two complementary long helical chains formed through O-H⋯O hydrogen bonds are interconnected through the characteristic head-to-tail N-H⋯O hydrogen bonds. Thus the molecular aggregation enabled through classical hydrogen bonds may be regarded as a mimic of the characteristic double helical structure of DNA. Also, precise structural information involving these amino acid molecules with lower symmetry exhibiting higher trigonal symmetry in their self-assembly is expected to throw light on the nature and strength of intermolecular interactions and their role in self-assembly of molecular aggregates, which are crucial in developing new or at least supplement existing crystal engineering strategies. Single crystal X-ray analysis and their electronic structures were calculated at the DFT level with a detailed analysis of Hirshfeld surfaces and fingerprint plots facilitating a comparison of intermolecular interactions in building different supramolecular architectures.

Spirocyclic character of ixazomib citrate revealed by comprehensive XRD, NMR and DFT study

NASA Astrophysics Data System (ADS)

Skorepova, Eliska; Čerňa, Igor; Vlasáková, Růžena; Zvoníček, Vít; Tkadlecová, Marcela; Dušek, Michal

2017-11-01

Ixazomib citrate is a very recently approved anti-cancer drug. Until now, to the best of our knowledge, no one has been able to solve any crystal structures of this compound. In this work, we present the crystal structures of two isostructural solvates of ixazomib citrate. In all currently available literature, the molecule is characterized as containing a single optically active carbon atom and a borate cycle formed when ixazomib is reacted with citric acid to form a stabilized ixazomib citrate that can be administered orally. However, the crystal structures revealed that none of the up-to-date presented structural formulas of ixazomib citrate are fully accurate. In addition to the citrate ring, another 5-membered ring is formed. These two rings are connected by the boron atom, making this compound a spirocyclic borate. By spirocyclization, the boron atom becomes tetrahedral and therefore optically active. In the crystal structures, ixazomib citrate was found to be in forms of two RR and RS stereoisomers. The results are supported by solid-state and solution NMR and DFT quantum mechanical calculations.

Synthesis, crystal growth, structural and physicochemical studies of novel binary organic complex: 4-chloroaniline-3-hydroxy-4-methoxybenzaldehyde

NASA Astrophysics Data System (ADS)

Sharma, K. P.; Reddi, R. S. B.; Bhattacharya, S.; Rai, R. N.

2012-06-01

The solid-state reaction, which is solvent free and green synthesis, has been adopted to explore the novel compound. The phase diagram of 4-chloroaniline (CA) and 3-hydroxy-4-methoxybenzaldehyde (HMB) system shows the formation of a novel 1:1 molecular complex, and two eutectics on either sides of complex. Thermochemical studies of complex and eutectics have been carried out for various properties such as heat of fusion, entropy of fusion, Jackson's parameters, interfacial energy and excess thermodynamic functions. The formation of molecular complex was also studied by IR, NMR, elemental analysis and UV-Vis absorption spectra. The single crystal of molecular complex was grown and its XRD study confirms the formation of complex and identifies the crystal structure and atomic packing of crystal of complex. Transmission spectra of grown crystal of the complex show 70% transmittance efficiency with cut off wavelength 412 nm. The band gap and refractive index of the crystal of complex have also been studied.

Synthesis, characterization, thermal and antimicrobial studies of diabetic drug models: Complexes of vanadyl(II) sulfate with ascorbic acid (vitamin C), riboflavin (vitamin B2) and nicotinamide (vitamin B3)

NASA Astrophysics Data System (ADS)

Refat, Moamen S.

2010-04-01

The oxovanadium(II) complexes of the different vitamins like ascorbic acid (vitamin C; Vit. C), riboflavin (vitamin B2; Vit. B2) and nicotinamide (vitamin B3; Vit. B3) were synthesized and characterized by elemental analysis, molar conductance, IR, electronic, magnetic measurements, thermal studies, XRD and SEM. Conductance measurements indicated that the vanadyl(II) complexes of Vit. B2 and Vit. B3 are 1:2 electrolytes except for [VO(Vit. C) 2(H 2O) 2] complex is non-electrolyte. IR data show that Vit. B2 is bidentate ligand against azomethine nitrogen of pyrazine ring and C dbnd O of pyrimidine-2,4-dione but Vit. B3 and Vit. C acts as a monodentate ligand through pyridine nitrogen and hydroxo oxygen of furan ring, respectively. Electronic spectral measurements indicated that all VO(II) complexes have a square-pyramidal geometry. Magnetic measurements for the new vanadyl(II) complexes are in a good agreement with the proposed formula. Thermal analyses (TG/DSC) of the studied complexes show that the decomposition process takes place in more than two steps. XRD refer that VO(II) complexes have an amorphous behavior. The surface morphology of the complexes was studied by SEM. The antimicrobial activities of the ligands and its complexes indicate that the vanadyl(II) complexes possess high antibacterial and antifungal activities towards the bacterial species and the fungal species than start ligands.

The photoluminescent properties of Y2O3:Bi3+, Eu3+, Dy3+ phosphors for white-light-emitting diodes.

PubMed

Han, Xiumei; Feng, Xu; Qi, Xiwei; Wang, Xiaoqiang; Li, Mingya

2014-05-01

Bi3+, Eu3+, Dy3+ activated Y2O3 phosphors were prepared through the sol-gel process. X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectra, and photoluminescence (PL) spectra were used to characterize the resulting phosphors. The XRD patterns show the refined crystal structure of Y2O3. The energy transfer processes of Bi(3+)-Eu3+ occurred in the host lattices. The thermal stability of Y2O3:Bi3+, Eu3+, Dy3+ phosphors was studied. Under short wavelength UV excitation, the phosphors show excellent characteristic red, blue, and yellow emission with medium intensity.

Electrochromic TiO2 Thin Film Prepared by Dip-Coating Technique

NASA Astrophysics Data System (ADS)

Suriani, S.; Kamisah, M. M.

2002-12-01

Titanium dioxide (TiO2) thin films were prepared by using sol-gel dip coating technique. The coating solutions were prepared by reacting titanium isopropoxide as precursors and ethanol as solvent. The films were formed on transparent ITO-coated glass by a dip coating technique and final dried at various temperatures up to 600 °C for 30 minutes. The films were characterized with the UV-Vis-NIR Spectrometer, Scanning Electron Microscopy (SEM) and X-ray diffractometer (XRD). XRD results show that the films dried at 600 °C form anatase structure. From the spectroscopic studies, the sample shows electrochromic property.

Studies of Niobium Thin Film Produced by Energetic Vacuum Deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Genfa Wu; Anne-Marie Valente; H. Phillips

2004-05-01

An energetic vacuum deposition system has been used to study deposition energy effects on the properties of niobium thin films on copper and sapphire substrates. The absence of working gas avoids the gaseous inclusions commonly seen with sputtering deposition. A biased substrate holder controls the deposition energy. Transition temperature and residual resistivity ratio of the niobium thin films at several deposition energies are obtained together with surface morphology and crystal orientation measurements by AFM inspection, XRD and TEM analysis. The results show that niobium thin films on sapphire substrate exhibit the best cryogenic properties at deposition energy around 123 eV.more » The TEM analysis revealed that epitaxial growth of film was evident when deposition energy reaches 163 eV for sapphire substrate. Similarly, niobium thin film on copper substrate shows that film grows more oriented with higher deposition energy and grain size reaches the scale of the film thickness at the deposition energy around 153 eV.« less

Preparation of Diatomite Supported Nano Zinc Oxide Composite Photocatalytic Material and Study on its Formaldehyde Degradation

NASA Astrophysics Data System (ADS)

Xiao, Liguang; Pang, Bo

2017-09-01

This experiment used zinc nitrate as precursor, ethanol as solvent and polyethylene glycol as dispersant, diatomite as carrier, diatomite loaded nano Zinc Oxide was prepared by sol-gel method, in addition, the formaldehyde degradation was studied by two kinds of experimental methods: preparation and loading, preparation and post loading, The samples were characterized by SEM, XRD, BET and IR. Experimental results showed that: Diatomite based nano Zinc Oxide had a continuous adsorption and degradation of formaldehyde, formaldehyde gas with initial concentration was 0.7mg/m3, after 36h degradation, the concentration reached 0.238mg/m3, the degradation rate reached to 66%.

Impedance and modulus spectroscopic study of nano hydroxyapatite

NASA Astrophysics Data System (ADS)

Jogiya, B. V.; Jethava, H. O.; Tank, K. P.; Raviya, V. R.; Joshi, M. J.

2016-05-01

Hydroxyapatite (Ca10 (PO4)6 (OH)2, HAP) is the main inorganic component of the hard tissues in bones and also important material for orthopedic and dental implant applications. Nano HAP is of great interest due to its various bio-medical applications. In the present work the nano HAP was synthesized by using surfactant mediated approach. Structure and morphology of the synthesized nano HAP was examined by the Powder XRD and TEM. Impedance study was carried out on pelletized sample in a frequency range of 100Hz to 20MHz at room temperature. The variation of dielectric constant, dielectric loss, and a.c. conductivity with frequency of applied field was studied. The Nyquist plot as well as modulus plot was drawn. The Nyquist plot showed two semicircle arcs, which indicated the presence of grain and grain boundary effect in the sample. The typical behavior of the Nyquist plot was represented by equivalent circuit having two parallel RC combinations in series.

Determinants for Tight and Selective Binding of a Medicinal Dicarbene Gold(I) Complex to a Telomeric DNA G-Quadruplex: a Joint ESI MS and XRD Investigation.

PubMed

Bazzicalupi, Carla; Ferraroni, Marta; Papi, Francesco; Massai, Lara; Bertrand, Benoît; Messori, Luigi; Gratteri, Paola; Casini, Angela

2016-03-18

The dicarbene gold(I) complex [Au(9-methylcaffein-8-ylidene)2 ]BF4 is an exceptional organometallic compound of profound interest as a prospective anticancer agent. This gold(I) complex was previously reported to be highly cytotoxic toward various cancer cell lines in vitro and behaves as a selective G-quadruplex stabilizer. Interactions of the gold complex with various telomeric DNA models have been analyzed by a combined ESI MS and X-ray diffraction (XRD) approach. ESI MS measurements confirmed formation of stable adducts between the intact gold(I) complex and Tel 23 DNA sequence. The crystal structure of the adduct formed between [Au(9-methylcaffein-8-ylidene)2 ](+) and Tel 23 DNA G-quadruplex was solved. Tel 23 maintains a characteristic propeller conformation while binding three gold(I) dicarbene moieties at two distinct sites. Stacking interactions appear to drive noncovalent binding of the gold(I) complex. The structural basis for tight gold(I) complex/G-quadruplex recognition and its selectivity are described. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Synthesis of nanocrystalline zirconia by amorphous citrate route: structural and thermal (HTXRD) studies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bhagwat, Mahesh; Ramaswamy, Veda

Nanocrystalline zirconia powder with a fairly narrow particle size distribution has been synthesized by the amorphous citrate route. The sample obtained has a high BET surface area of 89 m{sup 2} g{sup -1}. Rietveld refinement of the powder X-ray diffraction (XRD) profile of the zirconia sample confirms stabilization of zirconia in the tetragonal phase with around 8% monoclinic impurity. The data show the presence of both anionic as well as cationic vacancies in the lattice. Crystallite size determined from XRD is 8 nm and is in close agreement with the particle size determined by TEM. The in situ high temperature-X-raymore » diffraction (HTXRD) study revealed high thermal stability of the mixture till around 1023 K after which the transformation of tetragonal phase into the monoclinic phase has been seen as a function of temperature till 1473 K. This transformation is accompanied by an increase in the crystallite size of the sample from 8 to 55 nm. The thermal expansion coefficients are 9.14 x 10{sup -6} K{sup -1} along 'a'- and 15.8 x 10{sup -6} K{sup -1} along 'c'-axis. The lattice thermal expansion coefficient in the temperature range 298-1623 K is 34.6 x 10{sup -6} K{sup -1}.« less

Ellipsometric study of Si(0.5)Ge(0.5)/Si strained-layer superlattices

NASA Technical Reports Server (NTRS)

Sieg, R. M.; Alterovitz, S. A.; Croke, E. T.; Harrell, M. J.

1993-01-01

An ellipsometric study of two Si(0.5)Ge(0.5)/Si strained-layer super lattices grown by MBE at low temperature (500 C) is presented, and results are compared with x ray diffraction (XRD) estimates. Excellent agreement is obtained between target values, XRD, and ellipsometry when one of two available Si(x)Ge(1-x) databases is used. It is shown that ellipsometry can be used to nondestructively determine the number of superlattice periods, layer thicknesses, Si(x)Ge(1-x) composition, and oxide thickness without resorting to additional sources of information. It was also noted that we do not observe any strain effect on the E(sub 1) critical point.

Comparative study of hydroxyapatite from eggshells and synthetic hydroxyapatite for bone regeneration.

PubMed

Lee, Sang-Woon; Kim, Seong-Gon; Balázsi, Csaba; Chae, Weon-Sik; Lee, Hee-Ok

2012-03-01

The objective of this study was to evaluate the physical properties of synthetic hydroxyapatite (sHA) and hydroxyapatite from eggshells (eHA) by Fourier-transform infrared (FT-IR) and x-ray diffraction (XRD) and to compare the regenerative ability of the bone using sHA and eHA in a rabbit calvarial defect model. FT-IR and XRD were used to compare the physical properties of sHA and eHA. sHA was purchased from Sigma, and eHA was kindly donated from the Hungarian academy of science. Sixteen New Zealand white rabbits were used for the animal study. After the formation of a bilateral parietal bony defect (diameter 8.0 mm), either sHA or eHA was grafted into the defect. The defect in the control was left unfilled. Bone regeneration was evaluated by histomorphometry at 4 and 8 weeks after the operation. The peak broadening of the XRD experiments were in agreement with scanning electron microscope observation; the sHA had a smaller granule size than the eHA. The eHA had impurities phases of CaO (International Center for Diffraction Data (ICDD) 075-0264) and Ca(OH)(2) (ICDD 072-0156). Total new bone was 17.11 ± 10.24% in the control group, 28.81 ± 12.63% in sHA group, and 25.68 ± 10.89% in eHA group at 4 weeks after the operation. The difference was not statistically significant (P > .05). Total new bone at 8 weeks after the operation was 27.50 ± 10.89% in the control group, 38.62 ± 17.42% in sHA group, and 41.99 ± 8.44% in the eHA group. When comparing the sHA group to the control group, the difference was not statistically significant (P > .05). However, the eHA group was significantly different from the control group (P = .038). When comparing the eHA group to the sHA group, the difference was not statistically significant (P > .05). Both types of HA showed higher bone formation than the unfilled control. However, eHA had significantly higher bone formation than the unfilled control at 8 weeks after operation. Copyright © 2012 Elsevier Inc. All rights reserved.

A Fourier-Transform Infrared Study of Biochar Aging in Soils

PubMed Central

Singh, B.; Fang, Y.; Johnston, C.T.

2018-01-01

We used diffuse reflectance Fourier-transform infrared (DR-FTIR) spectroscopy, X-ray diffraction (XRD), and chemical and isotopic analyses to characterize the light fraction of four contrasting soils (control and biocharamended soils) to determine changes in biochar properties after aging. Two Eucalyptus saligna Sm. wood biochars, produced at 450°C (B450) and 550°C (B550), were incubated separately in each of the four soils for up to 12 mo at 20, 40, and 60°C. Total C and isotopic (δ13C) methods were used to quantify the amounts of biochar C and native C mineralized during incubation. The DR-FTIR spectra of the light fraction showed distinct absorption bands representing native soil organic C, biochar C, and mineral constituents present in the soils; the mineral bands were consistent with XRD data of the clay fraction of the four soils. Analysis of the DR-FTIR spectra in the ν(C–H) bands showed that the ratio of the aromatic ν(C–H) bands systematically increased relative to the aliphatic ν(C–H) bands with increasing mineralization of biochar C in the B550 amended soils, and this relationship was unique for each soil type. In contrast, this relationship was not observed for the B450 amended soils that contained a relatively smaller proportion of aromatic C. PMID:29657354

Structural and optical studies of Mg doped nanoparticles of chromium oxide (Cr2O3) synthesized by co-precipitation method

NASA Astrophysics Data System (ADS)

Singh, Jarnail; Verma, Vikram; Kumar, Ravi

2018-04-01

We present here the synthesization, structural and optical studies of Mg doped nanoparticles of Chromium oxide (Cr2O3) prepared using co-precipitation method. These samples were characterized using powder X-ray diffraction (XRD), Field emission scanning electron microscopy (FESEM), Raman spectroscopy and UV-Vis spectroscopy techniques. We have demonstrated that there is negligible change in optical band gap with the Mg doping. The prepared Cr2O3 nanoparticles are spherical in shape, but they are transformed into platelets when doped with Mg. The XRD studies reveal that the Mg doping in Cr2O3 doesn't affect the structure of Chromium oxide (Cr2O3).

Local symmetry breaking in SnO2 nanocrystals with cobalt doping and its effect on optical properties.

PubMed

Roy, S; Joshi, Amish G; Chatterjee, S; Ghosh, Anup K

2018-06-07

X-ray photoemission spectroscopy (XPS), X-ray diffraction (XRD) and transmission electron microscopy (TEM) have been used to study the structural and morphological characteristics of cobalt doped tin(iv) oxide (Sn1-xCoxO2; 0 ≤ x ≤ 0.04) nanocrystals synthesized by a chemical co-precipitation technique. Electronic structure analysis using X-ray photoemission spectroscopy (XPS) shows the formation of tin interstitials (Sni) and reduction of oxygen vacancies (VO) in the host lattice on Co doping and that the doped Co exists in mixed valence states of +2 and +3. Using XRD, the preferential position of the Sni and doped Co in the unit cell of the nanocrystals have been estimated. Rietveld refinement of XRD data shows that samples are of single phase and variation of lattice constants follows Vegard's law. XRD and TEM measurements show that the crystallite size of the nanocrystals decrease with increase in Co doping concentration. SAED patterns confirm the monocrystalline nature of the samples. The study of the lattice dynamics using Raman spectroscopy and Fourier transform infrared (FTIR) spectroscopy shows the existence of many disorder activated forbidden optical phonon modes, along with the corresponding classical modes, signifying Co induced local symmetry breaking in the nanocrystals. UV-Vis spectroscopy shows that the optical band gap has red shifted with increase in doping concentration. The study of Urbach energy confirms the increase in disorder in the nanocrystals with Co doping. Local symmetry breaking induced UV emission along with violet, blue and green luminescence has been observed from the PL study. The spectral contribution of UV emission decreases and green luminescence increases with increase in doping. Using PL, in conjunction with Raman spectroscopy, the type of oxygen vacancy induced in the nanocrystals on Co doping has been confirmed and the position of the defect levels in the forbidden zone (w.r.t. the optical band gap) has been studied.

Improving the Mechanical Performance and Thermal Stability of a PVA-Clay Nanocomposite by Electron Beam Irradiation

NASA Astrophysics Data System (ADS)

Shokuhi Rad, A.; Ebrahimi, D.

2017-07-01

The effects of electron beam irradiation and presence of clay on the mechanical properties and thermal stability of montmorillonite clay-modified polyvinyl alcohol nanocomposites were studied. By using the X-ray diffraction (XRD) and transmission electron microscopy (TEM), the microstructure of the nanocomposites was investigated. The results obtained from TEM and XRD tests showed that montmorillonite clay nanoparticles were located in the polyvinyl alcohol phase. The XRD analysis confirmed the formation of an exfoliated structure in nanocomposites samples. Increasing the amount of clay to 20 wt.% increased the tensile strength and modulus of the nanocomposite. Irradiation up to an absorbed dose of 100 kGy increased its mechanical properties and thermal stability, but at higher irradiation levels, the mechanical strength and thermal stability declined. The sample with 20 wt.% of the nanofiller, exposed to 100 kGy, showed the highest mechanical strength and thermal stability.

Characterization and growth mechanism of a peculiar nodular structure in shale: Comprehensive study over the Sitakund anticline, Bengal basin.

NASA Astrophysics Data System (ADS)

Gazi, M. Y.; Kabir, S. M. M.; Imam, M. B.

2017-12-01

Nodular shales commonly occur in comparatively older and silty shales near the axial (proximity to core) region of Sitakund Anticline (Study area), Sitapahar Anticline, Patharia Structure, Sylhet Anticline and Mirinja Anticline as observed. Stratigraphically, they are pronounced in the Surma group of Neogene succession. They are less abundant in limb portion. In many outcrop, they are found in the incompetent bed with the obliterated bedding bounded by well bedded competent beds. Their occurrence are sporadic rather than continuous along and across the strike of the bed. At some places huge number cluster of small and big nodular shales occur while in the other places, they occur as isolated mass in the highly disturbed or obliterated beds. The Surma group is the prime startigraphic unit in Bangladesh with major economic and academic importance. Yet there is a lack of comprehensive characterization of mudrocks of Surma group. This has prompted the present research to be undertaken. An initial field based study has been followed by detail textural, mineralogical, petrological and geochemical by using upscale laboratory techniques that include Thin Section Microscopy, Laser Particle Size Analyses, X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), and X-ray Florescence (XRF). From laser diffraction analysis, it is evident that nodular shales are silty in nature containing approximately 60% silt (Mainly quartz). XRD pattern shows that Nodular shale contains clay minerals, predominantly illite, Kaolinite, Chlorite and expandable mixed layer clay mineral. Detail geochemical analysis of some nodular shale samples shows that there are no significant variation from other samples in major and trace element concentration. Microcrack's within the quartz grains were observed in nodular shale. Projection of 15 nodular shale long axes in outcrop shows their orientation in NNW-SSE that is parallel to the fold axis. The study suggests a new name of conventionally called

Spectral characterization, thermal and biological activity studies of Schiff base complexes derived from 4,4‧-Methylenedianiline, ethanol amine and benzil

NASA Astrophysics Data System (ADS)

Emam, Sanaa Moustafa

2017-04-01

Some new metal(II) complexes of asymmetric Schiff base ligand were prepared by template technique. The shaped complexes are in binuclear structures and were explained through elemental analysis, molar conductivity, various spectroscopic methods (IR, U.V-Vis, XRD, ESR), thermal (TG) and magnetic moment measurements. The IR spectra were done demonstrating that the Schiff base ligand acts as neutral tetradentate moiety in all metal complexes. The electronic absorption spectra represented octahedral geometry for all complexes, while, the ESR spectra for Cu(II) complex showed axially symmetric g-tensor parameter with g׀׀ > g⊥ > 2.0023 indicating to 2B1g ground state with (dx2-y2)1 configuration. The nature of the solid residue created from TG estimations was affirmed utilizing IR and XRD spectra. The biological activity of the prepared complexes was studied against Land Snails. Additionally, the in vitro antitumor activity of the synthesized complexes with Hepatocellular Carcinoma cell (Hep-G2) was examined. It was observed that Zn(II) complex (5), exhibits a high inhibition of growth of the cell line with IC50 of 7.09 μg/mL.

Comparative study of nano-sized particles CoFe2O4 effects on superconducting properties of Y-123 and Y-358

NASA Astrophysics Data System (ADS)

Slimani, Y.; Hannachi, E.; Ben Salem, M. K.; Hamrita, A.; Varilci, A.; Dachraoui, W.; Ben Salem, M.; Ben Azzouz, F.

2014-10-01

The effects of nano-sized CoFe2O4 particles (10 nm) addition on the structural and the normal state resistivity of YBa2Cu3O7 (noted Y-123) and Y3Ba5Cu8O18 (noted Y-358) polycrystalline were systematically studied. Samples were synthesized in oxygen atmosphere using a standard solid state reaction technique by adding CoFe2O4 up to 2 wt%. Phases, microstructure and superconductivity have been systematically investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrical measurements ρ(T). XRD results reveal that the lattice parameters change for both Y-123 and Y-358 phases. SEM observations reveal that the grain size is reduced with increasing the content of CoFe2O4. The measurements for the resistivity dependence of temperature show that the depression in superconducting temperature is more pronounced for CoFe2O4 addition in Y-358 compound than in Y-123 one. These results may be attributed to the existence of much more disorder due to a greater number of Cu sites to be substituted by Fe and Co in Y-358 compared to Y-123.

Influence of Te and Se doping on ZnO films growth by SILAR method

NASA Astrophysics Data System (ADS)

Güney, Harun; Duman, Ćaǧlar

2016-04-01

The AIP Successive ionic layer adsorption and reaction (SILAR) is an economic and simple method to growth thin films. In this study, SILAR method is used to growth Selenium (Se) and Tellurium (Te) doped zinc oxide (ZnO) thin films with different doping rates. For characterization of the films X-ray diffraction (XRD), absorbance and scanning electron microscopy (SEM) are used. XRD results are showed well-defined strongly (002) oriented crystal structure for all samples. Also, absorbance measurements show, Te and Se concentration are proportional and inversely proportional with band gap energy, respectively. SEM measurements show that the surface morphology and thickness of the material varied with Se and/or Te and varying concentrations.

Influence of Te and Se doping on ZnO films growth by SILAR method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Güney, Harun, E-mail: harunguney25@hotmail.com; Duman, Çağlar, E-mail: caglarduman@erzurum.edu.tr

2016-04-18

The AIP Successive ionic layer adsorption and reaction (SILAR) is an economic and simple method to growth thin films. In this study, SILAR method is used to growth Selenium (Se) and Tellurium (Te) doped zinc oxide (ZnO) thin films with different doping rates. For characterization of the films X-ray diffraction (XRD), absorbance and scanning electron microscopy (SEM) are used. XRD results are showed well-defined strongly (002) oriented crystal structure for all samples. Also, absorbance measurements show, Te and Se concentration are proportional and inversely proportional with band gap energy, respectively. SEM measurements show that the surface morphology and thickness ofmore » the material varied with Se and/or Te and varying concentrations.« less

Solid-state reaction kinetics and optical studies of cadmium doped magnesium hydrogen phosphate crystals

NASA Astrophysics Data System (ADS)

Verma, Madhu; Gupta, Rashmi; Singh, Harjinder; Bamzai, K. K.

2018-04-01

The growth of cadmium doped magnesium hydrogen phosphate was successfully carried out by using room temperature solution technique i.e., gel encapsulation technique. Grown crystals were confirmed by single crystal X-ray diffraction (XRD). The structure of the grown crystal belongs to orthorhombic crystal system and crystallizes in centrosymmetric space group. Kinetics of the decomposition of the grown crystals were studied by non-isothermal analysis. Thermo gravimetric / differential thermo analytical (TG/DTA) studies revealed that the grown crystal is stable upto 119 °C. The various steps involved in the thermal decomposition of the material have been analysed using Horowitz-Metzger, Coats-Redfern and Piloyan-Novikova equations for evaluating various kinetic parameters. The optical studies shows that the grown crystals possess wide transmittance in the visible region and significant optical band gap of 5.5ev with cut off wavelength of 260 nm.

Noise exposure in movie theaters: a preliminary study of sound levels during the showing of 25 films.

PubMed

Warszawa, Anna; Sataloff, Robert T

2010-09-01

The harmful effects of noise exposure during leisure-time activities are beginning to receive some scrutiny. We conducted a preliminary study to investigate the noise levels during the showings of 25 different films. During each screening, various sound measurements were made with a dosimeter. The movies were classified on the basis of both their Motion Picture Association of America (MPAA) rating and their genre, and the size of the theater and the size of the audience were taken into consideration in the final analysis. Our findings suggest that the sound levels of many movies might be harmful to hearing, although we can draw no definitive conclusions. We did not discern any relationship between noise levels and either MPAA rating or genre. Further studies are recommended.

To study the effect of dopant NiO concentration and duration of calcinations on structural and optical properties of MgO-NiO nanocomposites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Rajesh, E-mail: rkkaushik06@gmail.com; Deptt. of Physics,Vaish College of Engineering, Rohtak-124001, Haryana; Praveen,

2016-05-06

In present work Magnesium oxide (MgO) samples were doped with different concentration of Transition metal Nickel Oxide(NiO) by using Chemical co-precipitation method. The doping levels were varied from NiO (5%, 10%, 15%) and all the samples were calcined at 600°C for 4hrs and 8hrs respectively. Structural analysis of these calcined materials is carried out by X-ray diffraction (XRD) techniques which reveals that average crystalline sizes are in nano region i.e. 21.77nm-31.13 nm and tabulated in table 1. The powder of calcined samples were also characterized by using various other techniques i.e. Scanning Electron Microscopy (SEM), Fourier Transformation Infrared Spectroscopy (FTIR), UV-Visiblemore » spectroscopy, Transmission Electron Microscopy (TEM) etc. The effects of dopant concentration, calcined temperature, calcinations duration on samples were studied and also investigate the effect of varying dopant concentration on morphology and optical properties of calcined nanomaterials. From results it was observed that the crystallite size of nanocomposites increases with increases dopant concentration or increases calcinations duration. The optical band gap decreases with increases sintering time and increase with increases dopant concentrations. TEM results coincide with XRD results and show that particles are polycrystalline in nature. FTIR spectra show that for all samples particles are pure in composition and transmission rate increases with calcinations duration.« less

Synthesis, spectroscopic characterization and structural investigations of new adduct compound of carbazole with picric acid: DNA binding and antimicrobial studies

NASA Astrophysics Data System (ADS)

Saravanabhavan, Munusamy; Sathya, Krishnan; Puranik, Vedavati G.; Sekar, Marimuthu

2014-01-01

Carbazole picrate (CP), a new organic compound has been synthesized, characterized by various analytical and spectroscopic technique such as FT-IR, UV-Vis, 1H and 13C NMR spectroscopy. An orthorhombic geometry was proposed based on single crystal XRD study. The thermal stability of the crystal was studied by using thermo-gravimetric and differential thermal analyses and found that it was stable up to 170 °C. Further, the newly synthesized title compound was tested for its in vitro antibacterial and antifungal activity against various bacterial and fungal species. Also, the compound was tested for its binding activity with Calf thymus (CT) DNA and the results show a considerable interaction between CP and CT-DNA.

Development of zinc oxide nanoparticle by sonochemical method and study of their physical and optical properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Khan, Samreen Heena, E-mail: samreen.heena.khan@gmail.com; Suriyaprabha, R.; Pathak, Bhawana, E-mail: bhawana.pathak@cug.ac.in

With the miniaturization of crystal size, the fraction of under-coordinated surface atoms becomes dominant, and hence, materials in the nano-regime behave very differently from the similar material in a bulk. Zinc oxide (ZnO), particularly, exhibits extraordinary properties such as a wide direct band gap (3.37 eV), large excitation binding energy (60 meV), low refractive index (1.9), stability to intense ultraviolet (UV) illumination, resistance to high-energy irradiation, and lower toxicity as compared to other semiconductors. This very property makes Zinc Oxide a potential candidate in many application fields, particularly as a prominent semiconductor. Zinc Oxide plays a significant role in manymore » technological advances with its application in semiconductor mediated photocatalytic processes and sensor, solar cells and others. In present study, Zinc Oxide (ZnO) has been synthesized using three different precursors by sonochemical method. Zinc Acetate Dihydrate, Zinc Nitrate Hexahydrate and Zinc Sulphate Heptahydrate used as a precursor for the synthesis process. The synthesized ZnO nanoparticle has been found under the range of ∼50 nm. Zinc oxide nanoparticles were characterized using different characterizing tools. The as-synthesized ZnO was characterized by Fourier Transform-Infrared Spectroscopy (FT-IR) for the determination of functional group; Scanning Electron Microscopy equipped with Energy Dispersive Spectroscopy (SEM-EDS) for Morphology and elemental detection respectively, Transmission Electron Microscopy for Particle size distribution and morphology and X-Ray Diffraction (XRD) for the confirmation of crystal structure of the nanomaterial. The optical properties of the ZnO were examined by UV-VIS spectroscopy equipped with Diffuse Reflectance spectroscopy (DRS) confirmed the optical band gap of ZnO-3 around 3.23 eV resembles with the band gap of bulk ZnO (3.37eV). The TEM micrograph of the as-synthesized material showed perfectly spherical

Computer Simulations to Study Diffraction Effects of Stacking Faults in Beta-SiC: II. Experimental Verification. 2; Experimental Verification

NASA Technical Reports Server (NTRS)

Pujar, Vijay V.; Cawley, James D.; Levine, S. (Technical Monitor)

2000-01-01

Earlier results from computer simulation studies suggest a correlation between the spatial distribution of stacking errors in the Beta-SiC structure and features observed in X-ray diffraction patterns of the material. Reported here are experimental results obtained from two types of nominally Beta-SiC specimens, which yield distinct XRD data. These samples were analyzed using high resolution transmission electron microscopy (HRTEM) and the stacking error distribution was directly determined. The HRTEM results compare well to those deduced by matching the XRD data with simulated spectra, confirming the hypothesis that the XRD data is indicative not only of the presence and density of stacking errors, but also that it can yield information regarding their distribution. In addition, the stacking error population in both specimens is related to their synthesis conditions and it appears that it is similar to the relation developed by others to explain the formation of the corresponding polytypes.

Showing and Telling Farming: Agricultural Shows and Re-Imaging British Agriculture

ERIC Educational Resources Information Center

Holloway, Lewis

2004-01-01

Some actors in the ''mainstream'' agricultural sector are beginning to engage in strategies of influencing public perceptions of farming, responding to public anxieties over industrialised agriculture and to a supposed separation of non-farming publics from food production. This paper focuses on agricultural shows as sites and events central to…