Comparing two tetraalkylammonium ionic liquids. II. Phase transitions.

PubMed

Lima, Thamires A; Paschoal, Vitor H; Faria, Luiz F O; Ribeiro, Mauro C C; Ferreira, Fabio F; Costa, Fanny N; Giles, Carlos

2016-06-14

Phase transitions of the ionic liquids n-butyl-trimethylammonium bis(trifluoromethanesulfonyl)imide, [N1114][NTf2], and methyl-tributylammonium bis(trifluoromethanesulfonyl)imide, [N1444][NTf2], were investigated by differential scanning calorimetry (DSC), X-ray diffraction (XRD) measurements, and Raman spectroscopy. XRD and Raman spectra were obtained as a function of temperature at atmospheric pressure, and also under high pressure at room temperature using a diamond anvil cell (DAC). [N1444][NTf2] experiences glass transition at low temperature, whereas [N1114][NTf2] crystallizes or not depending on the cooling rate. Both the ionic liquids exhibit glass transition under high pressure. XRD and low-frequency Raman spectra provide a consistent physical picture of structural ordering-disordering accompanying the thermal events of crystallization, glass transition, cold crystallization, pre-melting, and melting. Raman spectra in the high-frequency range of some specific cation and anion normal modes reveal conformational changes of the molecular structures along phase transitions.

Effect of substrate temperature in the synthesis of BN nanostructures

NASA Astrophysics Data System (ADS)

Sajjad, M.; Zhang, H. X.; Peng, X. Y.; Feng, P. X.

2011-06-01

Boron nitride (BN) nanostructures were grown on molybdenum discs at different substrate temperatures using the short-pulse laser plasma deposition technique. Large numbers of randomly oriented nanorods of fiber-like structures were obtained. The variation in the length and diameter of the nanorods as a function of the substrate temperature was systematically studied. The surface morphologies of the samples were studied using scanning electron microscopy. Energy dispersive x-ray spectroscopy confirmed that both the elements boron and nitrogen are dominant in the nanostructure. The x-ray diffraction (XRD) technique was used to analyse BN phases. The XRD peak that appeared at 26° showed the presence of hexagonal BN phase, whereas the peak at 44° was related to cubic BN content in the samples. Raman spectroscopic analysis showed vibrational modes of sp2- and sp3-type bonding in the sample. The Raman spectra agreed well with XRD results.

Synthesis and characterization of nanostructured titanium carbide for fuel cell applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Paviter; Singh, Harwinder; Singh, Bikramjeet

2016-04-13

Titanium carbide (TiC) nanoparticles have been successfully synthesized by carbo-thermic reaction of titanium and acetone at 800 °C. This method is relatively low temperature synthesis route. It can be used for large scale production of TiC. The synthesized nanoparticles have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and differential thermal analyzer (DTA) techniques. XRD analysis confirmed the formation of single phase TiC. XRD analysis confirmed that the particles are spherical in shape with an average particle size of 13 nm. DTA analysis shows that the phase is stable upto 900 °C and the material can be used formore » high temperature applications.« less

Sodium-promoted Pd/TiO2 for catalytic oxidation of formaldehyde at ambient temperature.

PubMed

Zhang, Changbin; Li, Yaobin; Wang, Yafei; He, Hong

2014-05-20

Catalytic oxidation of formaldehyde (HCHO) to CO2 at ambient conditions is of great interest for indoor HCHO purification. Here, we report that sodium-doped Pd/TiO2 is a highly effective catalyst for the catalytic oxidation of HCHO at room temperature. It was observed that Na doping has a dramatic promotion effect on the Pd/TiO2 catalyst and that nearly 100% HCHO conversion could be achieved over the 2Na-Pd/TiO2 catalyst at a GHSV of 95000 h(-1) and HCHO inlet concentration of 140 ppm at 25 °C. The mechanism of the Na-promotion effect was investigated by using Brunauer-Emmett-Teller (BET), X-ray diffraction (XRD), CO chemisorption, Temperature-programmed reduction by H2 (H2-TPR), X-ray photoelectron spectroscopy (XPS) and temperature-programmed desorption of O2 (O2-TPD) methods. The results showed that Na species addition can induce and further stabilize a negatively charged and well-dispersed Pd species, which then facilitates the activation of H2O and chemisorbed oxygen, therefore resulting in the high performance of the 2Na-Pd/TiO2 catalyst for the ambient HCHO destruction.

High temperature XRD of Cu2GeSe3

NASA Astrophysics Data System (ADS)

Premkumar D., S.; Chetty, Raju; Malar, P.; Mallik, Ramesh Chandra

2015-06-01

The Cu2GeSe3 is prepared by solid state synthesis method. The high temperature XRD has been done at different temperature from 30 °C to 450 °C. The reitveld refinement confirms Cu2GeSe3 phase and orthorhombic crystal structure. The lattice constants are increasing with increase in the temperature and their rate of increase with respect to temperature are used for finding the thermal expansion coefficient. The calculation of the linear and volume coefficient of thermal expansion is done from 30 °C to 400 °C. Decrease in the values of linear expansion coefficients with temperature are observed along a and c axis. Since thermal expansion coefficient is the consequence of the distortion of atoms in the lattice; this can be further used to find the minimum lattice thermal conductivity at given temperature.

Effects on structural, optical, and magnetic properties of pure and Sr-substituted MgFe2O4 nanoparticles at different calcination temperatures

NASA Astrophysics Data System (ADS)

Loganathan, A.; Kumar, K.

2016-06-01

In the present work, pure and Sr2+ ions substituted Mg ferrite nanoparticles (NPs) had been prepared by co-precipitation method and their structural, optical, and magnetic properties at different calcination temperatures were studied. On this purpose, thermo gravimetric and differential thermal analysis (TG-DTA), Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy, UV-Visible diffused reflectance spectroscopy, impedance spectroscopy, and vibrating sample magnetometer were carried out. The exo- and endothermic processes of synthesized precursors were investigated by TG-DTA measurements. The structural properties of the obtained products were examined by XRD analysis and show that the synthesized NPs are in the cubic spinel structure. The existence of two bands around 578-583 and 430-436 cm-1 in FT-IR spectrum also confirmed the formation of spinel-structured ferrite NPs. The lattice constants and particle size are estimated using XRD data and found to be strongly dependent on calcination temperatures. The optical, electrical, and magnetic properties of ferrite compositions also investigated and found to be strongly dependant on calcination temperatures.

A comparative study of the physical properties of Cu-Zn ferrites annealed under different atmospheres and temperatures: Magnetic enhancement of Cu0.5Zn0.5Fe2O4 nanoparticles by a reducing atmosphere

NASA Astrophysics Data System (ADS)

Gholizadeh, Ahmad

2018-04-01

In the present work, the influence of different sintering atmospheres and temperatures on physical properties of the Cu0.5Zn0.5Fe2O4 nanoparticles including the redistribution of Zn2+ and Fe3+ ions, the oxidation of Fe atoms in the lattice, crystallite sizes, IR bands, saturation magnetization and magnetic core sizes have been investigated. The fitting of XRD patterns by using Fullprof program and also FT-IR measurement show the formation of a cubic structure with no presence of impurity phase for all the samples. The unit cell parameter of the samples sintered at the air- and inert-ambient atmospheres trend to decrease with sintering temperature, but for the samples sintered under carbon monoxide-ambient atmosphere increase. The magnetization curves versus the applied magnetic field, indicate different behaviour for the samples sintered at 700 °C with the respect to the samples sintered at 300 °C. Also, the saturation magnetization increases with the sintering temperature and reach a maximum 61.68 emu/g in the sample sintered under reducing atmosphere at 600 °C. The magnetic particle size distributions of samples have been calculated by fitting the M-H curves with the size distributed Langevin function. The results obtained from the XRD and FTIR measurements suggest that the magnetic core size has the dominant effect in variation of the saturation magnetization of the samples.

Effect of 50 MeV Li3 + irradiation on structural and electrical properties of Mn-doped ZnO

NASA Astrophysics Data System (ADS)

Neogi, S. K.; Chattopadhyay, S.; Banerjee, Aritra; Bandyopadhyay, S.; Sarkar, A.; Kumar, Ravi

2011-05-01

The present work aims to study the effect of ion irradiation on structural and electrical properties and their correlation with the defects in the Zn1 - xMnxO-type system. Zn1 - xMnxO (x = 0.02, 0.04) samples have been synthesized by the solid-state reaction method and have been irradiated with 50 MeV Li3 + ions. The concomitant changes have been probed by x-ray diffraction (XRD), temperature-dependent electrical resistivity and positron annihilation lifetime (PAL) spectroscopy. The XRD result shows a single-phase wurtzite structure for Zn0.98Mn0.02O, whereas for the Zn0.96Mn0.04O sample an impurity phase has been found, apart from the usual peaks of ZnO. Ion irradiation removes this impurity peak. The grain size of the samples is found to be uniform. For Zn0.98Mn0.02O, the observed sharp decrease in room temperature resistivity (ρRT) with irradiation is consistent with the lowering of the full width at half maximum of the XRD peaks. However, for Zn0.96Mn0.04O, ρRT decreases for the initial fluence but increases for a further increase in fluence. All the irradiated Zn0.98Mn0.02O samples show a metal-semiconductor transition in temperature-dependent resistivity measurements at low temperature. But all the irradiated Zn0.96Mn0.04O samples show a semiconducting nature in the whole range of temperatures. Results of room temperature resistivity, XRD and PAL measurements are consistent with each other.

Effect of 50 MeV Li3+ irradiation on structural and electrical properties of Mn-doped ZnO.

PubMed

Neogi, S K; Chattopadhyay, S; Banerjee, Aritra; Bandyopadhyay, S; Sarkar, A; Kumar, Ravi

2011-05-25

The present work aims to study the effect of ion irradiation on structural and electrical properties and their correlation with the defects in the Zn(1 - x)Mn(x)O-type system. Zn(1 - x)Mn(x)O (x = 0.02, 0.04) samples have been synthesized by the solid-state reaction method and have been irradiated with 50 MeV Li(3+) ions. The concomitant changes have been probed by x-ray diffraction (XRD), temperature-dependent electrical resistivity and positron annihilation lifetime (PAL) spectroscopy. The XRD result shows a single-phase wurtzite structure for Zn(0.98)Mn(0.02)O, whereas for the Zn(0.96)Mn(0.04)O sample an impurity phase has been found, apart from the usual peaks of ZnO. Ion irradiation removes this impurity peak. The grain size of the samples is found to be uniform. For Zn(0.98)Mn(0.02)O, the observed sharp decrease in room temperature resistivity (ρ(RT)) with irradiation is consistent with the lowering of the full width at half maximum of the XRD peaks. However, for Zn(0.96)Mn(0.04)O, ρ(RT) decreases for the initial fluence but increases for a further increase in fluence. All the irradiated Zn(0.98)Mn(0.02)O samples show a metal-semiconductor transition in temperature-dependent resistivity measurements at low temperature. But all the irradiated Zn(0.96)Mn(0.04)O samples show a semiconducting nature in the whole range of temperatures. Results of room temperature resistivity, XRD and PAL measurements are consistent with each other.

High temperature XRD of Cu{sub 2}GeSe{sub 3}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Premkumar, D. S.; Malar, P.; Chetty, Raju

2015-06-24

The Cu{sub 2}GeSe{sub 3} is prepared by solid state synthesis method. The high temperature XRD has been done at different temperature from 30 °C to 450 °C. The reitveld refinement confirms Cu{sub 2}GeSe{sub 3} phase and orthorhombic crystal structure. The lattice constants are increasing with increase in the temperature and their rate of increase with respect to temperature are used for finding the thermal expansion coefficient. The calculation of the linear and volume coefficient of thermal expansion is done from 30 °C to 400 °C. Decrease in the values of linear expansion coefficients with temperature are observed along a andmore » c axis. Since thermal expansion coefficient is the consequence of the distortion of atoms in the lattice; this can be further used to find the minimum lattice thermal conductivity at given temperature.« less

Dielectric properties of A- and B-site doped BaTiO 3: Effect of La and Ga

NASA Astrophysics Data System (ADS)

Gulwade, Devidas; Gopalan, Prakash

2009-06-01

Extremely small amounts of La and Ga doping on the A- and B-site of BaTiO 3, respectively, resulting in a solid solution of the type Ba 1-3xLa 2xTi 1-3yGa 4yO 3 have been investigated. The present work dwells on the influence of the individual dopants, namely La and Ga, on the dielectric properties of BaTiO 3. The compositions have been prepared by solid-state reaction. X-ray diffraction (XRD) reveals the presence of tetragonal (P4/mmm) phase. The XRD data has been analyzed using FULLPROF, a Rietveld refinement package. The microstructure have been studied by orientation imaging microscopy (OIM). The compositions have been characterized by dielectric spectroscopy between room temperature and 250 °C. Further, the nature of phase transition has been studied using high temperature XRD. The resulting compounds exhibit high dielectric constant, enhanced diffuseness and low temperature coefficient of capacitance.

Comparing two tetraalkylammonium ionic liquids. II. Phase transitions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lima, Thamires A.; Paschoal, Vitor H.; Faria, Luiz F. O.

Phase transitions of the ionic liquids n-butyl-trimethylammonium bis(trifluoromethanesulfonyl)imide, [N{sub 1114}][NTf{sub 2}], and methyl-tributylammonium bis(trifluoromethanesulfonyl)imide, [N{sub 1444}][NTf{sub 2}], were investigated by differential scanning calorimetry (DSC), X-ray diffraction (XRD) measurements, and Raman spectroscopy. XRD and Raman spectra were obtained as a function of temperature at atmospheric pressure, and also under high pressure at room temperature using a diamond anvil cell (DAC). [N{sub 1444}][NTf{sub 2}] experiences glass transition at low temperature, whereas [N{sub 1114}][NTf{sub 2}] crystallizes or not depending on the cooling rate. Both the ionic liquids exhibit glass transition under high pressure. XRD and low-frequency Raman spectra provide a consistent physical picturemore » of structural ordering-disordering accompanying the thermal events of crystallization, glass transition, cold crystallization, pre-melting, and melting. Raman spectra in the high-frequency range of some specific cation and anion normal modes reveal conformational changes of the molecular structures along phase transitions.« less

Boron-doped diamond synthesized at high-pressure and high-temperature with metal catalyst

NASA Astrophysics Data System (ADS)

Shakhov, Fedor M.; Abyzov, Andrey M.; Kidalov, Sergey V.; Krasilin, Andrei A.; Lähderanta, Erkki; Lebedev, Vasiliy T.; Shamshur, Dmitriy V.; Takai, Kazuyuki

2017-04-01

The boron-doped diamond (BDD) powder consisting of 40-100 μm particles was synthesized at 5 GPa and 1500-1600 °C from a mixture of 50 wt% graphite and 50 wt% Ni-Mn catalyst with an addition of 1 wt% or 5 wt% boron powder. The size of crystal domains of doped and non-doped diamond was evaluated as a coherent scattering region by X-ray diffraction (XRD) and using small-angle neutron scattering (SANS), being ≥180 nm (XRD) and 100 nm (SANS). Magnetic impurities of NiMnx originating from the catalyst in the synthesis, which prevent superconductivity, were detected by magnetization measurements at 2-300 K. X-ray photoelectron spectroscopy, the temperature dependence of the resistivity, XRD, and Raman spectroscopy reveal that the concentration of electrically active boron is as high as (2±1)×1020 cm-3 (0.1 at%). To the best of our knowledge, this is the highest boron content for BDD synthesized in high-pressure high-temperature process with metal catalysts.

Understanding changes in cellulose crystalline structure of lignocellulosic biomass during ionic liquid pretreatment by XRD.

PubMed

Zhang, Jiafu; Wang, Yixun; Zhang, Liye; Zhang, Ruihong; Liu, Guangqing; Cheng, Gang

2014-01-01

X-ray diffraction (XRD) was used to understand the interactions of cellulose in lignocellulosic biomass with ionic liquids (ILs). The experiment was designed in such a way that the process of swelling and solubilization of crystalline cellulose in plant cell walls was followed by XRD. Three different feedstocks, switchgrass, corn stover and rice husk, were pretreated using 1-butyl-3-methylimidazolium acetate ([C4mim][OAc]) at temperatures of 50-130°C for 6h. At a 5 wt.% biomass loading, increasing pretreatment temperature led to a drop in biomass crystallinity index (CrI), which was due to swelling of crystalline cellulose. After most of the crystalline cellulose was swollen with IL molecules, a low-order structure was found in the pretreated samples. Upon further increasing temperature, cellulose II structure started to form in the pretreated biomass samples as a result of solubilization of cellulose in [C4mim][OAc] and subsequent regeneration. Copyright © 2013 Elsevier Ltd. All rights reserved.

Time dependence of carbon film deposition on SnO{sub 2}/Si using DC unbalanced magnetron sputtering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Alfiadi, H., E-mail: yudi@fi.itb.ac.id; Aji, A. S., E-mail: yudi@fi.itb.ac.id; Darma, Y., E-mail: yudi@fi.itb.ac.id

Carbon deposition on SnO{sub 2} layer has been demonstrated at low temperature using DC unbalanced magnetron-sputtering technique for various time depositions. Before carbon sputtering process, SnO{sub 2} thin layer is grown on silicon substrate by thermal evaporation method using high purity Sn wire and then fully oxidizes by dry O{sub 2} at 225°C. Carbon sputtering process was carried out at pressure of 4.6×10{sup −2} Torr by keeping the substrate temperature of 300 °C for sputtering deposition time of 1 to 4 hours. The properties of SnO{sub 2}/Si structure and carbon thin film on SnO{sub 2} is characterized using SEM, EDAX,more » XRD, FTIR, and Raman Spectra. SEM images and XRD spectra show that SnO2 thin film has uniformly growth on Si substrate and affected by annealing temperature. Raman and FTIR results confirm the formation of carbon-rich thin film on SnO{sub 2}. In addition, XRD spectra indicate that some structural change occur by increasing sputtering deposition time. Furthermore, the change of atomic structure due to the thermal annealing is analized by XRD spectra and Raman spectroscopy.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Saw, C K

To date a global kinetic rate law has not been written to accurately describe solid-solid phase transformations of HMX and TATB where contributions from grain size effects, binder contents, and impurity levels are explicitly defined. Our recent work presented at the 2001 SCCM topical APS meeting, Atlanta, GA, demonstrated one can not confidently use the second harmonic generation (SHG) diagnostic to study energetic material phase transitions where non-uniform grain size distributions are present. For example, in HMX, the early arrival of SHG before the XRD in the SHG/XRD simultaneous high temperature experiment clearly indicates the partial molecular conversion from centrosymmetricmore » to non-centrosymmetric without any structural changes as exhibit by the XRD pattern. This conversion is attributed to the changes of the surface molecules due to the differences in potential between the surface and the bulk. The present paper reports on accurate XRD measurements following changes of {beta}-HMX to {delta}-HMX at elevated temperature. The results are compared for sample with 2 different grain sizes for HMX. We report accurate temperature dependent lattice parameters and hence volume and linear thermal expansion coefficients along each crystallographic axis. We have also conducted kinetic studies of the behavior of 2 grain-sizes of HMX and concluded that their kinetics, are drastically different.« less

Hydrodeoxygenation of Guaiacol over Ceria-Zirconia Catalysts.

PubMed

Schimming, Sarah M; LaMont, Onaje D; König, Michael; Rogers, Allyson K; D'Amico, Andrew D; Yung, Matthew M; Sievers, Carsten

2015-06-22

The hydrodeoxygenation of guaiacol is investigated over bulk ceria and ceria-zirconia catalysts with different elemental compositions. The reactions are performed in a flow reactor at 1 atm and 275-400 °C. The primary products are phenol and catechol, whereas cresol and benzene are formed as secondary products. No products with hydrogenated rings are formed. The highest conversion of guaiacol is achieved over a catalyst containing 60 mol % CeO2 and 40 mol % ZrO2 . Pseudo-first-order activation energies of 97-114 kJ mol(-1) are observed over the mixed metal oxide catalysts. None of the catalysts show significant deactivation during 72 h on stream. The important physicochemical properties of the catalysts are characterized by X-ray diffraction (XRD), temperature-programmed reduction, titration of oxygen vacancies, and temperature-programmed desorption of ammonia. On the basis of these experimental results, the reasons for the observed reactivity trends are identified. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

n-Hexane hydro-isomerization over promoted Pd/HZSM-5 catalysts

NASA Astrophysics Data System (ADS)

Thoa Dao, Thi Kim; Loc Luu, Cam

2015-09-01

A series of Pd/HZSM-5 catalysts modified by various metallic species, including Co, Ni, Fe, Re, and Cu, was prepared by sequential impregnation. Contents of Pd and second metals in modified catalysts were 0.8 and 1.0 wt%, respectively. Physico-chemical characteristics of catalysts were investigated by nitrogen physi-sorption (BET), x-ray diffraction (XRD), transmission electron microscopy (TEM), ammonia temperature programmed desorption (NH3-TPD), temperature programmed reduction (TPR) and hydrogen pulse chemisorption (HPC). Coke formation was studied by the method of thermogravimetric analysis (TGA). The activities of catalysts in n-hexane isomerization were studied in a micro-flow reactor under atmospheric pressure at 250 °C, and molar ratio of H2: n-hexane of 5.92. It was found that Co, Ni, Fe, and Re additives exhibited geometric and electronic effects toward Pd/HZSM-5 catalyst, leading to an enhancement of its activity and stability. On the contrary, Cu additive caused Pd/HZSM-5 to become poorer in activity and stability.

Cordierite-supported metal oxide for non-methane hydrocarbon oxidation in cooking oil fumes.

PubMed

Huang, Yonghai; Yi, Honghong; Tang, Xiaolong; Zhao, Shunzheng; Gao, Fengyu; Wang, Jiangen; Yang, Zhongyu

2018-05-21

Cooking emission is an important reason for the air quality deterioration in the metropolitan area in China. Transition metal oxide and different loading of manganese oxide supported on cordierite were prepared by incipient wetness impregnation method and were used for non-methane hydrocarbon (NMHC) oxidation in cooking oil fumes (COFs). The effects of different calcination temperature and different Mn content were also studied. The SEM photographs and CO 2 temperature-programmed desorption revealed 5 wt% Mn/cordierite had the best pore structure and the largest number of the weak and moderate basic sites so it showed the best performance for NMHC oxidation. XRD analysis exhibited 5 wt% Mn/cordierite had the best dispersion of active phase and the active phase was MnO 2 when the calcination temperature was 400℃ which were good for the catalytic oxidation of NMHC.

Effect of rapid thermal annealing on the structural and electrical properties of RF sputtered CCTO thin film

NASA Astrophysics Data System (ADS)

Tripathy, N.; Das, K. C.; Ghosh, S. P.; Bose, G.; Kar, J. P.

2017-02-01

CaCu3Ti4O12 (CCTO) thin films have been deposited by RF magnetron sputtering on silicon substrates at room temperature. As-deposited thin films were subjected to rapid thermal annealing (RTA) at different temperatures ranging from 850°C to 1000°C. XRD and capacitance - voltage studies indicate that the structural and electrical properties of CCTO thin film strongly depend upon the annealing temperature. XRD pattern of CCTO thin film annealed at 950°C revealed the polycrystalline nature with evolutions of microstructures. Electrical properties of the dielectric films were investigated by fabricating Al/CCTO/Si metal oxide semiconductor structure. Electrical properties were found to be deteriorated with increasing in annealing temperature.

Annealing effect on the structural and dielectric properties of hematite nanoparticles

NASA Astrophysics Data System (ADS)

Kumar, Vijay; Chahal, Surjeet; Singh, Dharamvir; Kumar, Ashok; Kumar, Parmod; Asokan, K.

2018-05-01

In the present work, we have synthesized hematite (α-Fe2O3) nanoparticles by sol-gel method and sintered them at different temperatures (200 °C, 400 °C and 800 °C for six hours). The samples were then characterized using versatile characterization techniques such as X-ray diffraction (XRD), dielectric measurement and temperature dependent resistivity (RT) for their structural, dielectric and electrical properties. XRD measurements infer that intensity of peak increases with an increase in temperature resulting an increase in crystallite size. Temperature dependent resistivity also shows decrease in the resistivity of the samples. Furthermore, the dielectric measurements correspond to the increase in the dielectric constant. Based on these observations, it can be inferred that sintering temperature plays an important role in tailoring the various physical properties of hematite nanoparticles.

Does Z' equal 1 or 2? Enhanced powder NMR crystallography verification of a disordered room temperature crystal structure of a p38 inhibitor for chronic obstructive pulmonary disease.

PubMed

Widdifield, Cory M; Nilsson Lill, Sten O; Broo, Anders; Lindkvist, Maria; Pettersen, Anna; Svensk Ankarberg, Anna; Aldred, Peter; Schantz, Staffan; Emsley, Lyndon

2017-06-28

The crystal structure of the Form A polymorph of N-cyclopropyl-3-fluoro-4-methyl-5-[3-[[1-[2-[2-(methylamino)ethoxy]phenyl]cyclopropyl]amino]-2-oxo-pyrazin-1-yl]benzamide (i.e., AZD7624), determined using single-crystal X-ray diffraction (scXRD) at 100 K, contains two molecules in the asymmetric unit (Z' = 2) and has regions of local static disorder. This substance has been in phase IIa drug development trials for the treatment of chronic obstructive pulmonary disease, a disease which affects over 300 million people and contributes to nearly 3 million deaths annually. While attempting to verify the crystal structure using nuclear magnetic resonance crystallography (NMRX), we measured 13 C solid-state NMR (SSNMR) spectra at 295 K that appeared consistent with Z' = 1 rather than Z' = 2. To understand this surprising observation, we used multinuclear SSNMR ( 1 H, 13 C, 15 N), gauge-including projector augmented-wave density functional theory (GIPAW DFT) calculations, crystal structure prediction (CSP), and powder XRD (pXRD) to determine the room temperature crystal structure. Due to the large size of AZD7624 (ca. 500 amu, 54 distinct 13 C environments for Z' = 2), static disorder at 100 K, and (as we show) dynamic disorder at ambient temperatures, NMR spectral assignment was a challenge. We introduce a method to enhance confidence in NMR assignments by comparing experimental 13 C isotropic chemical shifts against site-specific DFT-calculated shift distributions established using CSP-generated crystal structures. The assignment and room temperature NMRX structure determination process also included measurements of 13 C shift tensors and the observation of residual dipolar coupling between 13 C and 14 N. CSP generated ca. 90 reasonable candidate structures (Z' = 1 and Z' = 2), which when coupled with GIPAW DFT results, room temperature pXRD, and the assigned SSNMR data, establish Z' = 2 at room temperature. We find that the polymorphic Form A of AZD7624 is maintained at room temperature, although dynamic disorder is present on the NMR timescale. Of the CSP-generated structures, 2 are found to be fully consistent with the SSNMR and pXRD data; within this pair, they are found to be structurally very similar (RMSD 16 = 0.30 Å). We establish that the CSP structure in best agreement with the NMR data possesses the highest degree of structural similarity with the scXRD-determined structure (RMSD 16 = 0.17 Å), and has the lowest DFT-calculated energy amongst all CSP-generated structures with Z' = 2.

In-situ XRD and EDS method study on the oxidation behaviour of Ni-Cu sulphide ore.

PubMed

Li, Guangshi; Cheng, Hongwei; Xiong, Xiaolu; Lu, Xionggang; Xu, Cong; Lu, Changyuan; Zou, Xingli; Xu, Qian

2017-06-12

The oxidation mechanism of sulfides is the key issue during the sulphide-metallurgy process. In this study, the phase transformation and element migration were clearly demonstrated by in-situ laboratory-based X-ray diffraction (XRD) and energy-dispersive X-ray spectroscopy (EDS), respectively. The reaction sequence and a four-step oxidation mechanism were proposed and identified. The elemental distribution demonstrated that at a low temperature, the Fe atoms diffused outward and the Ni/Cu atoms migrated toward the inner core, whereas the opposite diffusion processes were observed at a higher temperature. Importantly, the unique visual presentation of the oxidation behaviour provided by the combination of in-situ XRD and EDS might be useful for optimising the process parameters to improve the Ni/Cu extraction efficiency during Ni-Cu sulphide metallurgy.

Adsorption of vitamin E on mesoporous titania nanocrystals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shih, C.J., E-mail: cjshih@kmu.edu.tw; Lin, C.T.; Wu, S.M.

2010-07-15

Tri-block nonionic surfactant and titanium chloride were used as starting materials for the synthesis of mesoporous titania nanocrystallite powders. The main objective of the present study was to examine the synthesis of mesoporous titania nanocrystals and the adsorption of vitamin E on those nanocrystals using X-ray diffraction (XRD), transmission electron microscopy, and nitrogen adsorption and desorption isotherms. When the calcination temperature was increased to 300 {sup o}C, the reflection peaks in the XRD pattern indicated the presence of an anatase phase. The crystallinity of the nanocrystallites increased from 80% to 98.6% with increasing calcination temperature from 465 {sup o}C tomore » 500 {sup o}C. The N{sub 2} adsorption data and XRD data taken after vitamin E adsorption revealed that the vitamin E molecules were adsorbed in the mesopores of the titania nanocrystals.« less

Dependence of annealing temperature on microstructure and photoelectrical properties of vanadium oxide thin films prepared by DC reactive sputtering

NASA Astrophysics Data System (ADS)

Li, Yan; Zhang, Dongping; Wang, Bo; Liang, Guangxing; Zheng, Zhuanghao; Luo, Jingting; Cai, Xingmin; Fan, Ping

2013-12-01

Vanadium oxide thin films were prepared by DC reactive sputtering method, and the samples were annealed in Ar atmosphere under different temperature for 2 hours. The microstructure, optical and electrical properties of the as-grown and treated samples were characterized by XRD, spectrophotometer, and four-probe technique, respectively. XRD results investigated that the main content of the annealed sample are VO2 and V2O5. With annealing temperature increasing, the intensity of the VO2 phase diffraction peak strengthened. The electrical properties reveal that the annealed samples exhibit semiconductor-to-metal transition characteristic at about 40°C. Comparison of transmission spectra of the samples at room temperature and 100°C, a drastic drop in IR region is found.

Structural, microstructural, dielectric and ferroelectric properties of lead free Ba0.85Ca0.15Zr0.1Ti0.9O3 ceramic

NASA Astrophysics Data System (ADS)

Sharma, Sarita; Sharma, Hakikat; Negi, N. S.

2018-05-01

Lead free Ba0.85Ca0.15Zr0.1Ti0.9O3(BCTZ) ceramic has been synthesized by sol-gel method. Properties of material are studied at different sintering temperatures for 5 hours. Structural and microstructural properties are analyzed by using X-ray diffractrometer (XRD) and scanning electron microscopy (SEM) at annealing temperature of 850°C and 1050°C XRD pattern confirm the perovskite structure of the material without any unwanted phases crystalinity increased with increase of sintering temperature so as roughness and porosity is decreased as shown by SEM micrographs. There is large improvement in density with rise of sintering temperature which also leads to drastic change in ferroelectric and dielectric properties.

Sign reversal of transformation entropy change in Co{sub 2}Cr(Ga,Si) shape memory alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu, Xiao, E-mail: xu@material.tohoku.ac.jp; Omori, Toshihiro; Kainuma, Ryosuke

2015-11-02

In situ X-ray diffraction (XRD) measurements and compression tests were performed on Co{sub 2}Cr(Ga,Si) shape memory alloys. The reentrant martensitic transformation behavior was directly observed during the in situ XRD measurements. The high-temperature parent phase and low-temperature reentrant parent phase were found to have a continuous temperature dependence of lattice parameter, therefore suggesting that they are the same phase in nature. Moreover, compression tests were performed on a parent-phase single crystal sample; an evolution from normal to inverse temperature dependence of critical stress for martensitic transformation was directly observed. Based on the Clausius-Clapeyron analysis, a sign reversal of entropy changemore » can be expected on the same alloy.« less

Structural and surface properties of CuO-ZnO-Cr{sub 2}O{sub 3} catalysts and their relationship with selectivity to higher alcohol synthesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Campos-Martin, J.M.; Fierro, J.L.G.; Guerrero-Ruiz, A.

1995-10-01

A series of copper-zinc-chromium catalysts of different compositions and calcination temperatures has been prepared, characterized by several techniques (BET specific surface area, XRD, gravimetric TPR, TPD-CO, and XPS), and tested under high alcohol synthesis (HAS) conditions. CO hydrogenation was carried out at reaction temperatures of 523-598 K and 50 bar total pressure. The influence of catalyst composition, calcination temperature, and surface characteristics on the HAS selectivity was studied. The optimum HAS yields were found in the low Cr content region, but chromium was needed. Although chromium oxide does not seem to be involved in the catalytic site, its presence inmore » the catalyst composition is essential, owing to the larger specific surfaces and catalyst stability obtained at the highest reaction temperatures. For low Cr content composition, the temperature-programmed reduction (TPR) profiles were shifted to higher temperatures and simultaneously larger CO{sub 2} amounts were found in the temperature-programmed desorption profiles of adsorbed CO (TPD-CO). Photoelectron spectra (XPS) revealed that the oxidation state of copper is Cu{sup 2+} in the calcined catalysts and Cu{sup O} in the reduced ones; Cu{sup +} was only stabilized in a CuCr{sub 2}O{sub 4} spinel in the Cr-rich catalysts. These features derived from catalyst characterization are discussed in the framework of the catalytic behaviour for HAS synthesis. 53 refs., 7 figs., 4 tabs.« less

Is Tridymite at Gale Crater Evidence for Silicic Volcanism on Mars?

NASA Technical Reports Server (NTRS)

Morris, Richard V.; Vaniman, David T.; Ming, Douglas W.; Graff, Trevor G.; Downs, Robert T.; Fendrich, Kim; Mertzman, Stanley A.

2016-01-01

The X-ray diffraction (XRD) instrument (CheMin) onboard the MSL rover Curiosity detected 17 wt% of the SiO2 polymorph tridymite (relative to bulk sample) for the Buckskin drill sample (73 wt% SiO2) obtained from sedimentary rock in the Murray formation at Gale Crater, Mars. Other detected crystalline materials are plagioclase, sanidine, cristobalite, cation-deficient magnetite, and anhydrite. XRD amorphous material constitutes approx. 60 wt% of bulk sample, and the position of its broad diffraction peak near approx. 26 deg. 2-theta is consistent with opal-A. Tridymite is a lowpressure, high-temperature mineral (approx. 870 to 1670 deg. C) whose XRD-identified occurrence on the Earth is usually associated with silicic (e.g., rhyolitic) volcanism. High SiO2 deposits have been detected at Gale crater by remote sensing from martian orbit and interpreted as opal-A on the basis H2O and Si-OH spectral features. Proposed opal-A formation pathways include precipitation of silica from lake waters and high-SiO2 residues of acid-sulfate leaching. Tridymite is nominally anhydrous and would not exhibit these spectral features. We have chemically and spectrally analyzed rhyolitic samples from New Mexico and Iwodake volcano (Japan). The glassy (by XRD) NM samples have H2O spectral features similar to opal-A. The Iwodake sample, which has been subjected to high-temperature acid sulfate leaching, also has H2O spectral features similar to opal-A. The Iwodake sample has approx. 98 wt% SiO2 and 1% wt% TiO2 (by XRF), tridymite (>80 wt.% of crystalline material without detectable quartz by XRD), and H2O and Si-OH spectral features. These results open the working hypothesis that the opal-A-like high-SiO2 deposits at Gale crater detected from martian orbit are products of alteration associated with silicic volcanism. The presence or absence of tridymite will depend on lava crystallization temperatures (NM) and post crystallization alteration temperatures (Iwodake).

Influence of physicochemical treatments on iron-based spent catalyst for catalytic oxidation of toluene.

PubMed

Kim, Sang Chai; Shim, Wang Geun

2008-06-15

The catalytic oxidation of toluene was studied over an iron-based spent and regenerated catalysts. Air, hydrogen, or four different acid solutions (oxalic acid (C2H2O4), citric acid (C6H8O7), acetic acid (CH3COOH), and nitric acid (HNO3)) were employed to regenerate the spent catalyst. The properties of pretreated spent catalyst were characterized by the Brunauer Emmett Teller (BET), inductively coupled plasma (ICP), temperature programmed reduction (TPR), and X-ray diffraction (XRD) analyses. The air pretreatment significantly enhanced the catalytic activity of the spent catalyst in the pretreatment temperature range of 200-400 degrees C, but its catalytic activity diminished at the pretreatment temperature of 600 degrees C. The catalytic activity sequence with respect to the air pretreatment temperatures was 400 degrees C>200 degrees C>parent>600 degrees C. The TPR results indicated that the catalytic activity was correlated with both the oxygen mobility and the amount of available oxygen on the catalyst. In contrast, the hydrogen pretreatment had a negative effect on the catalytic activity, and toluene conversion decreased with increasing pretreatment temperatures (200-600 degrees C). The XRD and TPR results confirmed the formation of metallic iron which had a negative effect on the catalytic activity with increasing pretreatment temperature. The acid pretreatment improved the catalytic activity of the spent catalyst. The catalytic activity sequence with respect to different acids pretreatment was found to be oxalic acid>citric acid>acetic acid>or=nitric acid>parent. The TPR results of acid pretreated samples showed an increased amount of available oxygen which gave a positive effect on the catalytic activity. Accordingly, air or acid pretreatments were more promising methods of regenerating the iron-based spent catalyst. In particular, the oxalic acid pretreatment was found to be most effective in the formation of FeC2O4 species which contributed highly to the catalytic combustion of toluene.

[Study of the phase transformation of TiO2 with in-situ XRD in different gas].

PubMed

Ma, Li-Jing; Guo, Lie-Jin

2011-04-01

TiO2 sample was prepared by sol-gel method from chloride titanium. The phase transformation of the prepared TiO2 sample was studied by in-situ XRD and normal XRD in different gas. The experimental results showed that the phase transformation temperatures of TiO2 were different under in-situ or normal XRD in different kinds of gas. The transformation of amorphous TiO2 to anatase was controlled by kinetics before 500 degrees C. In-situ XRD showed that the growth of anatase was inhibited, but the transformation of anatase to rutile was accelerated under inactive nitrogen in contrast to air. Also better crystal was obtained under hydrogen than in argon. These all showed that external oxygen might accelerate the growth of TiO2, but reduced gas might partly counteract the negative influence of lack of external oxygen. The mechanism of phase transformation of TiO2 was studied by in-situ XRD in order to control the structure in situ.

Debye–Waller coefficient of heavily deformed nanocrystalline iron1

PubMed Central

Abdellatief, M.

2017-01-01

Synchrotron radiation X-ray diffraction (XRD) patterns from an extensively ball-milled iron alloy powder were collected at 100, 200 and 300 K. The results were analysed together with those using extended X-ray absorption fine structure, measured on the same sample at liquid nitrogen temperature (77 K) and at room temperature (300 K), to assess the contribution of static disorder to the Debye–Waller coefficient (B iso). Both techniques give an increase of ∼20% with respect to bulk reference iron, a noticeably smaller difference than reported by most of the literature for similar systems. Besides good quality XRD patterns, proper consideration of the temperature diffuse scattering seems to be the key to accurate values of the Debye–Waller coefficient. Molecular dynamics simulations of nanocrystalline iron aggregates, mapped on the evidence provided by XRD in terms of domain size distribution, shed light on the origin of the observed B iso increase. The main contribution to the static disorder is given by the grain boundary, while line and point defects have a much smaller effect. PMID:28381974

Debye–Waller coefficient of heavily deformed nanocrystalline iron

DOE Office of Scientific and Technical Information (OSTI.GOV)

Scardi, P.; Rebuffi, L.; Abdellatief, M.

2017-02-17

Synchrotron radiation X-ray diffraction (XRD) patterns from an extensively ball-milled iron alloy powder were collected at 100, 200 and 300 K. The results were analysed together with those using extended X-ray absorption fine structure, measured on the same sample at liquid nitrogen temperature (77 K) and at room temperature (300 K), to assess the contribution of static disorder to the Debye–Waller coefficient (B iso). Both techniques give an increase of ~20% with respect to bulk reference iron, a noticeably smaller difference than reported by most of the literature for similar systems. Besides good quality XRD patterns, proper consideration of themore » temperature diffuse scattering seems to be the key to accurate values of the Debye–Waller coefficient. Molecular dynamics simulations of nanocrystalline iron aggregates, mapped on the evidence provided by XRD in terms of domain size distribution, shed light on the origin of the observedB isoincrease. The main contribution to the static disorder is given by the grain boundary, while line and point defects have a much smaller effect.« less

Rietveld refinement, dielectric and magnetic properties of Nb modified Bi0.80Ba0.20FeO3 ceramic

NASA Astrophysics Data System (ADS)

Jangra, Sandhaya; Sanghi, Sujata; Agarwal, Ashish; Rangi, Manisha

2018-05-01

Bi0.80Ba0.20Fe0.95Nb0.05O3 ceramic has been prepared via conventional solid state reaction method. Structure analysis was carried out by X-ray diffraction (XRD) technique at room temperature. XRD pattern confirmed the crystalline nature of prepared sample. Rietveld analysis used for further structural investigations and confirmed the existence of rhombohedral symmetry (R3c space group). The dielectric response shows dispersion at lower frequency range and becomes frequency independent at high frequency. The approximation of conduction mechanism is determined by the temperature dependent behavior of frequency exponent `s'. Fitting results suggests the applicability of small polaron conduction mechanism at lower temperatures and CBH model at higher temperature. Room temperature magnetic measurements give the evidence of significant enhancement in magnetic properties with remanent magnetization (Mr = 0.1218 emu/g) and coercive field (Hc = 3.5342 kOe).

Simultaneous Femtosecond X-ray Spectroscopy and Diffraction of Photosystem II at Room Temperature

PubMed Central

Kern, Jan; Alonso-Mori, Roberto; Tran, Rosalie; Hattne, Johan; Gildea, Richard J.; Echols, Nathaniel; Glöckner, Carina; Hellmich, Julia; Laksmono, Hartawan; Sierra, Raymond G.; Lassalle-Kaiser, Benedikt; Koroidov, Sergey; Lampe, Alyssa; Han, Guangye; Gul, Sheraz; DiFiore, Dörte; Milathianaki, Despina; Fry, Alan R.; Miahnahri, Alan; Schafer, Donald W.; Messerschmidt, Marc; Seibert, M. Marvin; Koglin, Jason E.; Sokaras, Dimosthenis; Weng, Tsu-Chien; Sellberg, Jonas; Latimer, Matthew J.; Grosse-Kunstleve, Ralf W.; Zwart, Petrus H.; White, William E.; Glatzel, Pieter; Adams, Paul D.; Bogan, Michael J.; Williams, Garth J.; Boutet, Sébastien; Messinger, Johannes; Zouni, Athina; Sauter, Nicholas K.; Yachandra, Vittal K.; Bergmann, Uwe; Yano, Junko

2013-01-01

Intense femtosecond X-ray pulses produced at the Linac Coherent Light Source (LCLS) were used for simultaneous X-ray diffraction (XRD) and X-ray emission spectroscopy (XES) of microcrystals of Photosystem II (PS II) at room temperature. This method probes the overall protein structure and the electronic structure of the Mn4CaO5 cluster in the oxygen-evolving complex of PS II. XRD data are presented from both the dark state (S1) and the first illuminated state (S2) of PS II. Our simultaneous XRD/XES study shows that the PS II crystals are intact during our measurements at the LCLS, not only with respect to the structure of PS II, but also with regard to the electronic structure of the highly radiation sensitive Mn4CaO5 cluster, opening new directions for future dynamics studies. PMID:23413188

Simultaneous femtosecond X-ray spectroscopy and diffraction of photosystem II at room temperature.

PubMed

Kern, Jan; Alonso-Mori, Roberto; Tran, Rosalie; Hattne, Johan; Gildea, Richard J; Echols, Nathaniel; Glöckner, Carina; Hellmich, Julia; Laksmono, Hartawan; Sierra, Raymond G; Lassalle-Kaiser, Benedikt; Koroidov, Sergey; Lampe, Alyssa; Han, Guangye; Gul, Sheraz; Difiore, Dörte; Milathianaki, Despina; Fry, Alan R; Miahnahri, Alan; Schafer, Donald W; Messerschmidt, Marc; Seibert, M Marvin; Koglin, Jason E; Sokaras, Dimosthenis; Weng, Tsu-Chien; Sellberg, Jonas; Latimer, Matthew J; Grosse-Kunstleve, Ralf W; Zwart, Petrus H; White, William E; Glatzel, Pieter; Adams, Paul D; Bogan, Michael J; Williams, Garth J; Boutet, Sébastien; Messinger, Johannes; Zouni, Athina; Sauter, Nicholas K; Yachandra, Vittal K; Bergmann, Uwe; Yano, Junko

2013-04-26

Intense femtosecond x-ray pulses produced at the Linac Coherent Light Source (LCLS) were used for simultaneous x-ray diffraction (XRD) and x-ray emission spectroscopy (XES) of microcrystals of photosystem II (PS II) at room temperature. This method probes the overall protein structure and the electronic structure of the Mn4CaO5 cluster in the oxygen-evolving complex of PS II. XRD data are presented from both the dark state (S1) and the first illuminated state (S2) of PS II. Our simultaneous XRD-XES study shows that the PS II crystals are intact during our measurements at the LCLS, not only with respect to the structure of PS II, but also with regard to the electronic structure of the highly radiation-sensitive Mn4CaO5 cluster, opening new directions for future dynamics studies.

Nanoparticles of ZrPO4 for green catalytic applications

NASA Astrophysics Data System (ADS)

Sreenivasulu, Peta; Pendem, Chandrasekhar; Viswanadham, Nagabhatla

2014-11-01

Here we report the successful room temperature synthesis of zirconium phosphate nanoparticles (ZPNP) using the P123 tri-co-block polymer for the first time. The samples were characterized by SEM, TEM, XRD, TPD, and BET and were employed for fixation of CO2 on aniline to produce pharmaceutically important acetanilide under mild reaction conditions (150 °C and 150 Psi CO2 pressure).Here we report the successful room temperature synthesis of zirconium phosphate nanoparticles (ZPNP) using the P123 tri-co-block polymer for the first time. The samples were characterized by SEM, TEM, XRD, TPD, and BET and were employed for fixation of CO2 on aniline to produce pharmaceutically important acetanilide under mild reaction conditions (150 °C and 150 Psi CO2 pressure). Electronic supplementary information (ESI) available: Experimental details, wide angle XRD, EDX, IR spectra, GC data etc. See DOI: 10.1039/c4nr03209h

Facile synthesis of high surface area molybdenum nitride and carbide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Roy, Aaron; Serov, Alexey; Artyushkova, Kateryna

2015-08-15

The synthesis of high surface area γ-Mo{sub 2}N and α-Mo{sub 2}C is reported (116 and 120 m{sup 2}/g) without the temperature programmed reduction of MoO{sub 3}. γ-Mo{sub 2}N was prepared in an NH{sub 3}-free synthesis using forming gas (7 at% H{sub 2}, N{sub 2}-balance) as the reactive atmosphere. Three precursors were studied ((NH{sub 4}){sub 6}Mo{sub 7}O{sub 24}·4H{sub 2}O, (NH{sub 4}){sub 2} Mg(MoO{sub 4}){sub 2}, and MgMoO{sub 4}) along with the sacrificial support method (SSM) as a means of reducing the particle size of Mo{sub 2}N and Mo{sub 2}C. In situ X-ray diffraction (XRD) studies were carried out to identify reactionmore » intermediates, the temperature at which various intermediates form, and the average domain size of the Mo{sub 2}N products. Materials were synthesized in bulk and further characterized by XRD, HRTEM, XPS, and BET. - Highlights: • Facile synthesis of γ-Mo2N and α-Mo2C with surface area exceeding 100 m{sup 2}/g. • Sacrificial support method was used to achieve these high surface areas. • Materials can serve as catalysts or supports in (electro)chemical processes.« less

The Effects of Vanadium Pentoxide to Oxalic Acid Ratio and Different Atmospheres on the Formation of VO2 Nanopowders Synthesized via Sol-Gel Method

NASA Astrophysics Data System (ADS)

Vostakola, Mohsen Fallah; Yekta, Bijan Eftekhari; Mirkazemi, Seyed Mohammad

2017-11-01

Thermochromic VO2 nanopowders were synthesized via the sol-gel method through mixing oxalic acid and vanadium pentoxide in ethanol. We investigated the effect of oxalic acid to vanadium pentoxide ratio on the formation of final product and found that excessive oxalic acid reduced the final product from VO2 to V2O3. Because decreasing the oxalic acid to vanadium pentoxide ratio is a time-consuming process, oxygen was introduced by using a low-porosity alumina tube. The heat treatment was performed inside an electrical tube furnace and in a variety of atmospheres, including pure nitrogen (99.999% purity) and nitrogen containing 5 vol.%, 10 vol.%, and 15 vol.% hydrogen. According to x-ray diffraction (XRD) results, the appropriate atmosphere for synthesizing VO2 nanopowder was the one which contained 10 vol.% hydrogen. In order to decrease the transition temperature in VO2 from 63.5°C to room temperature, W6+ doping was done by adding different amounts of tungstic acid sol to vanadium sol precursor. Differential scanning calorimetry (DSC) results showed that W6+ reduced the transition temperature of VO2 approximately 23°C/wt.%. Lattice straining estimated from XRD results confirmed that VO2 was doped. XRD results at 25°C and 100°C along with DSC results indicated that VO2 was transformed from a low-temperature monoclinic phase to a high-temperature rutile one along this temperature interval.

Magnetic and dielectric behavior of chromium substituted Co-Mg ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Jadoun, Priya; Jyoti, Prashant, B. L.; Dolia, S. N.; Bhatnagar, D.; Saxena, V. K.

2016-05-01

The chromium doped Co-Mg ferrite with composition Co0.5Mg0.5Cr0.2Fe1.8O4 has been synthesized using sol-gel auto combustion method. The crystal structure has been analyzed by X-ray diffraction (XRD) technique. XRD pattern reveals the formation of single phase cubic spinel structure. The magnetic measurements show ferromagnetic behavior at room temperature and large coercivity is observed on cooling down the temperature to 20 K. Dielectric constant (ɛ') and dielectric loss tangent (tan δ) have been determined at room temperature as a function of frequency in the frequency range 75 kHz to 80 MHz. The decrease in dielectric constant with increasing frequency attributes to Maxwell Wagner model and conduction mechanism in ferrites.

Effect of Temperature, Precursor Type and Dripping Time on the Crystallite Size of Nano ZnO Obtained by One-Pot Synthesis: 2 k Full Factorial Design Analysis.

PubMed

Machado, Morgana de Medeiros; Savi, Bruna Martinello; Perucchi, Mariana Borges; Benedetti, Alessandro; Oliveira, Luis Felipe Silva; Bernardin, Adriano Michael

2018-06-01

The aim of this work was to determine the effect of temperature, precursor and dripping time on the crystallite size of ZnO nanoparticles synthesized by controlled precipitation according a 2k full factorial design. ZnCl2, Zn(NO3)2 and NaOH were used as precursors. After synthesis, the nano crystalline powder was characterized by XRD (Cu Kα), UV-Vis, and HR-TEM. The nano ZnO particles presented a crystallite size between 210 and 260 Å (HR-TEM and XRD). The results show that the crystallite size depends on the type of precursor and temperature of synthesis, but not on the dripping time.

Combustion synthesis and structural analysis of nanocrystalline nickel ferrite at low temperature regime

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shanmugavel, T., E-mail: gokulrajs@hotmail.com, E-mail: shanmugavelnano@gmail.com; Raj, S. Gokul, E-mail: gokulrajs@hotmail.com, E-mail: shanmugavelnano@gmail.com; Rajarajan, G.

2015-06-24

Combustion synthesis of single phase Nickel ferrite was successfully achieved at low temperature regime. The obtained powders were calcinated to increase the crystallinity and their characterization change due to calcinations is investigated in detail. Citric acid used as a chelating agent for the synthesis of nickel ferrite. Pure single phase nickel ferrites were found at this low temperature. The average crystalline sizes were measured by using powder XRD measurements. Surface morphology was investigated through Transmission Electron Microscope (TEM). Particle size calculated in XRD is compared with TEM results. Magnetic behaviour of the samples is analyzed by using Vibrating Sample Magnetometermore » (VSM). Saturation magnetization, coercivity and retentivity are measured and their results are discussed in detail.« less

A facile synthesis for cauliflower like CeO2 catalysts from Ce-BTC precursor and their catalytic performance for CO oxidation

NASA Astrophysics Data System (ADS)

Zhang, Xiaodong; Hou, Fulin; Yang, Yang; Wang, Yuxin; Liu, Ning; Chen, Dan; Yang, Yiqiong

2017-11-01

The paper presents a novel and facile method for preparing cauliflowerlike CeO2 through direct decomposition of cerium based metal-organic framework (MOF) Ce-BTC (BTC = 1,3,5-benzenetricarboxylic acid) straw in air. Several analytical tools such as Scanning electron microscopy (SEM), X-ray diffraction (XRD), Thermogravimetric (TG), N2 adsorption-desorption, Temperature programmed reduction (TPR), Raman, X-ray photoelectron spectroscopic (XPS) and Photoluminescence (PL) have been used to characterize Ce-BTC and CeO2. The Ce-BTC calcined at 500 °C (CeO2-500) maintains the morphology of its template ;Ce-BTC; and forms a special cauliflower-like structure. XRD patterns showed that the catalyst has a perfect CeO2 crystal structure and has a smaller particle size. The prepared CeO2 cauliflowers exhibit excellent catalytic activities, long-term stability, and cycling stability for CO oxidation. The improved catalytic activities could be attributed to porous nanorods of CeO2 cauliflowers, which provide more active sites and oxygen vacancy for CO oxidation.

Low temperature structural and transport studies of La{sub 0.175}Pr{sub 0.45}Ca{sub 0.375}MnO{sub 3-δ}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sharma, Shivani; Shahee, Aga; Singh, Kiran

2016-05-23

The temperature (T) dependent x-ray diffraction (XRD) and resistivity measurements of La{sub 0.175}Pr{sub 0.45}Ca{sub 0.375}MnO{sub 3-δ} (LPCMO) have been performed down to 2 K to understand the structural and transport properties. From room temperature down to 220 K, LPCMO exists in orthorhombic phase with Pnma structure and at T~220 K, it transforms to charge ordered (CO) monoclinic phase with P2{sub 1}/m structure and remains as it is down to 2 K. The CO phase is evident from the occurrence of weak but well defined superlattice peaks in the XRD pattern. This structural transformation is of first order in nature asmore » evident from the phase coexistence across the transition region. These results thus clearly illustrate that LPCMO undergoes a first order structural phase transition from charge disordered orthorhombic phase to CO monoclinic phase at ~220 K, consistent with temperature dependent resistivity results. Our structural analysis of T dependent XRD data using Rietveld refinement infers that below 220 K, LPCMO forms commensurate CO monoclinic P2{sub 1}/m structure with four times structural modulation.« less

Effect of annealing temperature on optical properties of binary zinc tin oxide nano-composite prepared by sol-gel route using simple precursors: structural and optical studies by DRS, FT-IR, XRD, FESEM investigations.

PubMed

Habibi, Mohammad Hossein; Mardani, Maryam

2015-02-25

Binary zinc tin oxide nano-composite was synthesized by a facile sol-gel method using simple precursors from the solutions consisting of zinc acetate, tin(IV) chloride and ethanol. Effect of annealing temperature on optical and structural properties was investigated using X-ray diffraction (XRD), diffuse reflectance spectra (DRS), field emission scanning electron microscopy (FESEM) and Fourier transform infrared spectroscopy (FTIR). XRD results revealed the existence of the ZnO and SnO2 phases. FESEM results showed that binary zinc tin oxide nano-composites ranges from 56 to 60 nm in diameter at 400°C and 500°C annealing temperatures respectively. The optical band gap was increased from 2.72 eV to 3.11 eV with the increasing of the annealing temperature. FTIR results confirmed the presence of zinc oxide and tin oxide and the broad absorption peaks at 3426 and 1602 cm(-1) can be ascribed to the vibration of absorptive water, and the absorption peaks at 546, 1038 and 1410 cm(-1) are due to the vibration of Zn-O or Sn-O groups in binary zinc tin oxide. Copyright © 2014 Elsevier B.V. All rights reserved.

Electrical properties of Mg doped ZnO nanostructure annealed at different temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mohamed, R., E-mail: ruziana12@gmail.com; Mamat, M. H., E-mail: hafiz-030@yahoo.com; Rusop, M., E-mail: nanouitm@gmail.com

In this work, ZincOxide (ZnO) nanostructures doped with Mg were successfully grown on the glass substrate. Magnesium (Mg) metal element was added in the ZnO host which acts as a doping agent. Different temperature in range of 250°C to 500°C was used in order to investigate the effect of annealing temperature of ZnO thin films. Field Emission Scanning Electron Microscopy (FESEM) was used to investigate the physical characteristic of ZnO thin films. FESEM results have revealed that ZnO nanorods were grown vertically aligned. The structural properties were determined by using X-Ray Diffraction (XRD) analysis. XRD results showed Mg doped ZnOmore » thin have highest crystalinnity at 500°C annealing temperature. The electrical properties were investigating by using Current-Voltage (I-V) measurement. I-V measurement showed the electrical properties were varied at different annealing temperature. The annealing temperature at 500°C has the highest electrical conductance properties.« less

Annealing Temperature Dependent Structural and Optical Properties of RF Sputtered ZnO Thin Films.

PubMed

Sharma, Shashikant; Varma, Tarun; Asokan, K; Periasamy, C; Boolchandani, Dharmendar

2017-01-01

This work investigates the effect of annealing temperature on structural and optical properties of ZnO thin films grown over Si 100 and glass substrates using RF sputtering technique. Annealing temperature has been varied from 300 °C to 600 °C in steps of 100, and different microstructural parameters such as grain size, dislocation density, lattice constant, stress and strain have been evaluated. The structural and surface morphological characterization has been done using X-ray Diffraction (XRD) and Scanning Electron Microscope (SEM). XRD analysis reveals that the peak intensity of 002 crystallographic orientation increases with increased annealing temperature. Optical characterization of deposited films have been done using UV-Vis-NIR spectroscopy and photoluminescence spectrometer. An increase in optical bandgap of deposited ZnO thin films with increasing annealing temperature has been observed. The average optical transmittance was found to be more than 85% for all deposited films. Photoluminiscense spectra (PL) suggest that the crystalline quality of deposited film has increased at higher annealing temperature.

Chemical characterization of hydroxyapatite obtained by wet chemistry in the presence of V, Co, and Cu ions.

PubMed

Moseke, Claus; Gelinsky, Michael; Groll, Jürgen; Gbureck, Uwe

2013-04-01

A model system for the precipitation of hydroxyapatite (HA) from saturated solutions at basic pH was utilized to investigate the effects of V, Co, and Cu ions on crystallography and stoichiometry of the produced apatites. X-ray diffraction (XRD) was applied to analyze phase composition and crystallinity of powders obtained with different metal ion concentrations and annealed at different sintering temperatures. This procedure used the temperature-dependent phase transitions and decompositions of calcium phosphates to analyze the particular influences of the metal ions on apatite mineralization. Comparative XRD measurements showed that all metal ion species reduced crystallinity and crystallite size of the produced apatites. Furthermore the transformation of amorphous calcium phosphate (ACP) to HA was partially inhibited, as was deduced from the formation of α-tricalcium phosphate (α-TCP) peaks in XRD patterns of the heated powders as well as from the reduced intensity of the OH stretch vibration in FTIR spectra. The thermally induced formation of β-TCP indicated a significantly reduced Ca/P ratio as compared to stoichiometric HA. This effect was more pronounced with rising metal ion content. In addition, the appearance of metal oxides in the XRD patterns of samples heated to higher temperatures indicated the incorporation of metal ions in the precipitated apatites. Peak shifts showed that both the apatitic as well as the β-TCP phase apparently had incorporated metal ions. Copyright © 2012 Elsevier B.V. All rights reserved.

Growth and characterization of hexamethylenetetramine crystals grown from solution

NASA Astrophysics Data System (ADS)

Babu, B.; Chandrasekaran, J.; Balaprabhakaran, S.

2014-06-01

Organic nonlinear optical single crystals of hexamethylenetetramine (HMT; 10 × 10 × 5 mm3) were prepared by crystallization from methanol solution. The grown crystals were subjected to various characterization techniques such as single crystal XRD, powder XRD, UV-Vis and electrical studies. Single crystal XRD analysis confirmed the crystalline structure of the grown crystals. Their crystalline nature was also confirmed by powder XRD technique. The optical transmittance property was identified from UV-Vis spectrum. Dielectric measurements were performed as a function of frequency at different temperatures. DC conductivity and photoconductivity studies were also carried out for the crystal. The powder second harmonic generation efficiency (SHG) of the crystal was measured using Nd:YAG laser and the efficiency was found to be two times greater than that of potassium dihydrogen phosphate (KDP).

Synthesis and characterization of nickel oxide particulate annealed at different temperatures

NASA Astrophysics Data System (ADS)

Sharma, Khem Raj; Thakur, Shilpa; Negi, N. S.

2018-04-01

Nickel oxide has been synthesized by solution combustion technique. The nickel oxide ceramic was annealed at 600°C and 1000°C for 2 hours. Structural, electrical, dielectric and magnetic properties were analyzed which are strongly dependent upon the synthesis method. Structural properties were examined by X-ray diffractometer (XRD), which confirmed the purity and cubic phase of nickel oxide. XRD data reveals the increase in crystallite size and decrease in full width half maximum (FWHM) as the annealing temperature increases. Electrical conductivity is found to increase from 10-6 to 10-5 (Ω-1cm-1) after annealing. Dielectric constant is observed to increase from 26 to 175 when the annealing temperature is increased from 600°C to 1000°C. Low value of coercive field is found which shows weak ferromagnetic behavior of NiO. It is observed that all the properties of NiO particulate improve with increasing annealing temperature.

Large scale synthesis of nanostructured zirconia-based compounds from freeze-dried precursors

NASA Astrophysics Data System (ADS)

Gómez, A.; Villanueva, R.; Vie, D.; Murcia-Mascaros, S.; Martínez, E.; Beltrán, A.; Sapiña, F.; Vicent, M.; Sánchez, E.

2013-01-01

Nanocrystalline zirconia powders have been obtained at the multigram scale by thermal decomposition of precursors resulting from the freeze-drying of aqueous acetic solutions. This technique has equally made possible to synthesize a variety of nanostructured yttria or scandia doped zirconia compositions. SEM images, as well as the analysis of the XRD patterns, show the nanoparticulated character of those solids obtained at low temperature, with typical particle size in the 10-15 nm range when prepared at 673 K. The presence of the monoclinic, the tetragonal or both phases depends on the temperature of the thermal treatment, the doping concentration and the nature of the dopant. In addition, Rietveld refinement of the XRD profiles of selected samples allows detecting the coexistence of the tetragonal and the cubic phases for high doping concentration and high thermal treatment temperatures. Raman experiments suggest the presence of both phases also at relatively low treatment temperatures.

Structure evolution of zinc oxide thin films deposited by unbalance DC magnetron sputtering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aryanto, Didik, E-mail: didi027@lipi.go.id; Materials Research Group, Physics Department, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah; Marwoto, Putut

Zinc oxide (ZnO) thin films are deposited on corning glass substrates using unbalanced DC magnetron sputtering. The effect of growth temperature on surface morphology and crystallographic orientation of ZnO thin film is studied using atomic force microscopy (AFM) and X-ray diffraction (XRD) techniques. The surface morphology and crystallographic orientation of ZnO thin film are transformed against the increasing of growth temperature. The mean grain size of film and the surface roughness are inversely and directly proportional towards the growth temperature from room temperature to 300 °C, respectively. The smaller grain size and finer roughness of ZnO thin film are obtainedmore » at growth temperature of 400 °C. The result of AFM analysis is in good agreement with the result of XRD analysis. ZnO thin films deposited in a series of growth temperatures have hexagonal wurtzite polycrystalline structures and they exhibit transformations in the crystallographic orientation. The results in this study reveal that the growth temperature strongly influences the surface morphology and crystallographic orientation of ZnO thin film.« less

Study on the Growth Mechanism of K2Ti4O9 Crystal

NASA Astrophysics Data System (ADS)

Zhou, Xuesong; Fan, Jing; Wei, Xiaoli; Shen, Yi; Meng, Yanzhi

2018-04-01

Potassium hexatitanate (K2Ti4O9) whiskers were prepared by the kneading-drying-calcination method. After the preparation of products under different calcination temperatures and holding times, their morphology and structure were characterized by thermogravimetric and differential thermal, X-ray diffraction (XRD), scanning electron microscopy and transmission electron microscopy. The XRD analysis showed that the reaction mixture was completely converted to K2Ti4O9 crystals at 800 °C when the T/K ratio was 3. Based on the analysis of LS (liquid-solid) growth mechanism, the corresponding transformation reaction mechanism during the roasting was elucidated. K2Ti4O9 whiskers grow mainly through the parallel action at a low temperature. With the increase in temperature, the series effect is obvious.

Mössbauer spectra of iron (III) sulfide particles

NASA Astrophysics Data System (ADS)

Kubono, I.; Nishida, N.; Kobayashi, Y.; Yamada, Y.

2017-11-01

Trivalent iron sulfide (Fe2 S 3) particles were synthesized using a modified polyol method. These particles exhibited a needle-like shape (diameter = 10-50 nm, length = 350-1000 nm) and generated a clear XRD pattern. Mössbauer spectra of the product showed a paramagnetic doublet at room temperature and distributed hyperfine magnetic splitting at low temperature. The Curie temperature of this material was determined to be approximately 60 K. The data suggest that the Fe2 S 3 had a structure similar to that of maghemite ( γ-Fe2 O 3) with a lattice constant of a = 10.6 Å. The XRD pattern calculated from this structure was in agreement with the experimental pattern and the calculated hyperfine magnetic field was also equivalent to that observed in the experimental Mössbauer spectrum.

Structural and thermal properties of vanadium tellurite glasses

NASA Astrophysics Data System (ADS)

Kaur, Rajinder; Kaur, Ramandeep; Khanna, Atul; González, Fernando

2018-04-01

V2O5-TeO2 glasses containing 10 to 50 mol% V2O5 were prepared by melt quenching and characterized by X-ray diffraction (XRD), density, Differential Scanning Calorimetry (DSC) and Raman studies.XRD confirmed the amorphous nature of vanadium tellurite samples. The density of the glasses decreases and the molar volume increases on increasing the concentration of V2O5. The thermal properties, such as glass transition temperature Tg, crystallization temperature Tc, and the melting temperature Tm were measured. Tg decreases from a value of 288°C to 232°C. The changes in Tg were correlated with the number of bonds per unit volume, and the average stretching force constant. Raman spectra were used to elucidate the short-range structure of vanadium tellurite glasses.

Preparation, characterization, dielectric properties and diffusion studies of styrene butadiene rubber (SBR)/manganous tungstate (MnWO4) nanocomposites

NASA Astrophysics Data System (ADS)

Jasna, V. C.; Ramesan, M. T.

2017-06-01

Nanocomposites based on SBR with different content of manganous tungstate nanoparticles were prepared and characterized by FTIR, UV-visible spectroscopy, XRD, SEM, TGA, DSC and impedance analysis. The interaction between nanoparticles and the elastomer was clear from the shift in peaks of UV and FTIR. XRD and SEM analysis showed the uniform arrangement of nanoparticles in SBR matrix. Glass transition temperature, thermal stability and dielectric properties of composites were enhanced by the addition of nanoparticles. Sorption studies of nanocomposites were done in aromatic solvents at different temperature. Sorption data obtained were used to estimate the thermodynamic properties.

Multiscale Design and Manufacturing of Hybrid DWCNT-Polymer Fibers

DTIC Science & Technology

2016-02-09

lower temperatures , but further increase of temperature produced insignificant structural changes. The latter effect shows promise for the control...elevated temperatures . Increase in crystallinity was confirmed by XRD experiments. Such nanofibers exhibited size effects for strength and modulus...Schatz group) study of the effects of higher carbonization temperatures . Some promising initial results are being now analyzed experimentally and

Surface Characteristics of Machined NiTi Shape Memory Alloy: The Effects of Cryogenic Cooling and Preheating Conditions

NASA Astrophysics Data System (ADS)

Kaynak, Y.; Huang, B.; Karaca, H. E.; Jawahir, I. S.

2017-07-01

This experimental study focuses on the phase state and phase transformation response of the surface and subsurface of machined NiTi alloys. X-ray diffraction (XRD) analysis and differential scanning calorimeter techniques were utilized to measure the phase state and the transformation response of machined specimens, respectively. Specimens were machined under dry machining at ambient temperature, preheated conditions, and cryogenic cooling conditions at various cutting speeds. The findings from this research demonstrate that cryogenic machining substantially alters austenite finish temperature of martensitic NiTi alloy. Austenite finish ( A f) temperature shows more than 25 percent increase resulting from cryogenic machining compared with austenite finish temperature of as-received NiTi. Dry and preheated conditions do not substantially alter austenite finish temperature. XRD analysis shows that distinctive transformation from martensite to austenite occurs during machining process in all three conditions. Complete transformation from martensite to austenite is observed in dry cutting at all selected cutting speeds.

Proxy-based accelerated discovery of Fischer–Tropsch catalysts† †Electronic supplementary information (ESI) available: Details of synthesis, analysis and testing, validation experiments for high-throughput XRD and gas treatment, details of statistical analysis and calculations, tabulation of synthesis parameters and XRD results, alternatives to Fig. 3 highlighting different data points, FTS testing results displayed graphically. See DOI: 10.1039/c4sc02116a Click here for additional data file.

PubMed Central

Boldrin, Paul; Gallagher, James R.; Combes, Gary B.; Enache, Dan I.; James, David; Ellis, Peter R.; Kelly, Gordon; Claridge, John B.

2015-01-01

Development of heterogeneous catalysts for complex reactions such as Fischer–Tropsch synthesis of fuels is hampered by difficult reaction conditions, slow characterisation techniques such as chemisorption and temperature-programmed reduction and the need for long term stability. High-throughput (HT) methods may help, but their use has until now focused on bespoke micro-reactors for direct measurements of activity and selectivity. These are specific to individual reactions and do not provide more fundamental information on the materials. Here we report using simpler HT characterisation techniques (XRD and TGA) along with ageing under Fischer–Tropsch reaction conditions to provide information analogous to metal surface area, degree of reduction and thousands of hours of stability testing time for hundreds of samples per month. The use of this method allowed the identification of a series of highly stable, high surface area catalysts promoted by Mg and Ru. In an advance over traditional multichannel HT reactors, the chemical and structural information we obtain on the materials allows us to identify the structural effects of the promoters and their effects on the modes of deactivation observed. PMID:29560180

Ultrafast visualization of crystallization and grain growth in shock-compressed SiO2

PubMed Central

Gleason, A. E.; Bolme, C. A.; Lee, H. J.; Nagler, B.; Galtier, E.; Milathianaki, D.; Hawreliak, J.; Kraus, R. G.; Eggert, J. H.; Fratanduono, D. E.; Collins, G. W.; Sandberg, R.; Yang, W.; Mao, W. L.

2015-01-01

Pressure- and temperature-induced phase transitions have been studied for more than a century but very little is known about the non-equilibrium processes by which the atoms rearrange. Shock compression generates a nearly instantaneous propagating high-pressure/temperature condition while in situ X-ray diffraction (XRD) probes the time-dependent atomic arrangement. Here we present in situ pump–probe XRD measurements on shock-compressed fused silica, revealing an amorphous to crystalline high-pressure stishovite phase transition. Using the size broadening of the diffraction peaks, the growth of nanocrystalline stishovite grains is resolved on the nanosecond timescale just after shock compression. At applied pressures above 18 GPa the nuclueation of stishovite appears to be kinetically limited to 1.4±0.4 ns. The functional form of this grain growth suggests homogeneous nucleation and attachment as the growth mechanism. These are the first observations of crystalline grain growth in the shock front between low- and high-pressure states via XRD. PMID:26337754

Structural, XPS and magnetic studies of pulsed laser deposited Fe doped Eu{sub 2}O{sub 3} thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Sandeep; Prakash, Ram, E-mail: rpgiuc@gmail.com; Choudhary, R.J.

2015-10-15

Highlights: • Growth of Fe doped Eu{sub 2}O{sub 3} thin films by PLD. • XRD and Raman’s spectroscopy used for structure confirmation. • The electronic states of Eu and Fe are confirmed by XPS. • Magnetic properties reveals room temperature magnetic ordering in deposited film. - Abstract: Fe (4 at.%) doped europium (III) oxide thin film was deposited on silicon (1 0 0) substrate by pulsed laser deposition technique. Structural, spectral and magnetic properties were studied by X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS) and magnetization measurements. XRD and Raman spectroscopy reveal that the grown film is singlemore » phased and belongs to the cubic structure of Eu{sub 2}O{sub 3}. XPS study of the Eu{sub 1.92}Fe{sub 0.08}O{sub 3} film shows that Fe exists in Fe{sup 3+} ionic state in the film. The film exhibits magnetic ordering at room temperature.« less

Ultrafast visualization of crystallization and grain growth in shock-compressed SiO 2

DOE PAGES

Gleason, A. E.; Bolme, C. A.; Lee, H. J.; ...

2015-09-04

Pressure- and temperature-induced phase transitions have been studied for more than a century but very little is known about the non-equilibrium processes by which the atoms rearrange. Shock compression generates a nearly instantaneous propagating high-pressure/temperature condition while in situ X-ray diffraction (XRD) probes the time-dependent atomic arrangement. Here we present in situ pump–probe XRD measurements on shock-compressed fused silica, revealing an amorphous to crystalline high-pressure stishovite phase transition. Using the size broadening of the diffraction peaks, the growth of nanocrystalline stishovite grains is resolved on the nanosecond timescale just after shock compression. At applied pressures above 18 GPa the nuclueationmore » of stishovite appears to be kinetically limited to 1.4 ± 0.4 ns. The functional form of this grain growth suggests homogeneous nucleation and attachment as the growth mechanism. As a result, these are the first observations of crystalline grain growth in the shock front between low- and high-pressure states via XRD.« less

Elucidation of reaction mechanism involved in the formation of LaNiO3 from XRD and TG analysis

NASA Astrophysics Data System (ADS)

Dharmadhikari, Dipti V.; Athawale, Anjali A.

2013-06-01

The present work is focused on the synthesis and elucidation of reaction mechanism involved in the formation of LaNiO3 with the help of X-ray diffraction (XRD) and thermogravimetric (TG) analysis. LaNiO3 was synthesized by hydrothermal method by heating at 160°C under autogenous pressure for 6h. Pure phase product was obtained after calcining the hydrothermally activated product for 6h at 700°C. The various phases of the product obtained after hydrothermal treatment and calcination followed by the formation of pure phase nanocrystalline lanthanum nickel oxide could be determined from XRD analysis of the samples. The reaction mechanism and phase formation temperature has been interpreted by thermogravimetric analysis of the hydrothermally synthesized product and XRD analysis.

An Investigation of the Interatomic Bonding Characteristics of a Ti - 51at.% Al Alloy by X-Ray Diffraction

DTIC Science & Technology

1991-06-01

GROUP SUBGROUP X-ray Diffraction, XRD, TiAI, titanium , aluminum, bonding characteristics, titanium aluminides , Debye-Waller temperature factor...XRD Powder Particles (575X) .............. 47 viii I. INTRODUCTION Titanium aluminides are recognized for their high specific strength, particularly at...bonding characteristics of binary titanium aluminides . Upon the introduction of a third element to the system, a rearrangement of the valence

Radiation-Induced Changes in Quartz, A Mineral Analog of Nuclear Power Plant Concrete Aggregates.

PubMed

Silva, Chinthaka M; Rosseel, Thomas M; Kirkegaard, Marie C

2018-03-19

Quartz single-crystal samples consisting of α-quartz crystal structure were neutron irradiated to fluences of 5 × 10 18 , 4 × 10 19 , and 2 × 10 20 n/cm 2 (E > 0.1 MeV) at two temperatures (52 and 95 °C). The changes in the α-quartz phase as a function of these two conditions (temperature and fluence) were studied using X-ray powder diffraction (XRD), Raman spectroscopy, and transmission electron microscopy (TEM), and the results acquired using these complementary techniques are presented in a single place for the first time. XRD studies showed that the lattice parameters of α-quartz increased with increasing neutron flux. The lattice growth was larger for the samples that were neutron irradiated at 52 °C than at 95 °C. Moreover, an amorphous content was determined in the quartz samples neutron irradiated at 4 × 10 19 n/cm 2 , with the greater amount being in the 52 °C irradiated sample. Complete amorphization of quartz was observed at a fluence of 2 × 10 20 n/cm 2 (E > 0.1 MeV) using XRD and confirmed by TEM characterization and Raman spectroscopic studies. The cause for α-quartz lattice expansion and sample amorphization was also explored using XRD and Raman spectroscopic studies.

Synthesis of nano-sized ZnO particles by co-precipitation method with variation of heating time

DOE Office of Scientific and Technical Information (OSTI.GOV)

Purwaningsih, S. Y., E-mail: sriyanisaputri@gmail.com; Pratapa, S.; Triwikantoro

Zinc oxide powders have been synthesized by a co-precipitation method at low temperature (85 °C), using zinc acetate dihydrate, ammonia, hydrochloric acid solutions as the reactants. A number of process parameters such as reaction temperature, solution basicity or pH and heating time are the main factors affecting the morphology and physical properties of the ZnO nanostructures. In this work the effect of heating time on the morphology and particles size were studied. The as-synthesized ZnO powders were characterized using transmission electron microscopy (TEM) and X-ray diffraction (XRD) techniques. The samples were also analyzed using Fourier transform infrared (FTIR). Rietveld refinementmore » of XRD data confirms that ZnO crystallizes in the hexagonal wurtzite structure with high degree of purity and the (101) plane predominant. The XRD results show that the average crystallite sizes were about 66, 27 and 12 nm for 3, 4 and 5 h of heating times, respectively. The XRD analysis indicated that a fraction of nano-sized ZnO powders were in the form of aggregates, which was also verified by TEM image. The TEM photograph demonstrated that the nano-sized ZnO particles were a pseudo-spherical shape.« less

PyXRD v0.6.7: a free and open-source program to quantify disordered phyllosilicates using multi-specimen X-ray diffraction profile fitting

NASA Astrophysics Data System (ADS)

Dumon, M.; Van Ranst, E.

2016-01-01

This paper presents a free and open-source program called PyXRD (short for Python X-ray diffraction) to improve the quantification of complex, poly-phasic mixed-layer phyllosilicate assemblages. The validity of the program was checked by comparing its output with Sybilla v2.2.2, which shares the same mathematical formalism. The novelty of this program is the ab initio incorporation of the multi-specimen method, making it possible to share phases and (a selection of) their parameters across multiple specimens. PyXRD thus allows for modelling multiple specimens side by side, and this approach speeds up the manual refinement process significantly. To check the hypothesis that this multi-specimen set-up - as it effectively reduces the number of parameters and increases the number of observations - can also improve automatic parameter refinements, we calculated X-ray diffraction patterns for four theoretical mineral assemblages. These patterns were then used as input for one refinement employing the multi-specimen set-up and one employing the single-pattern set-ups. For all of the assemblages, PyXRD was able to reproduce or approximate the input parameters with the multi-specimen approach. Diverging solutions only occurred in single-pattern set-ups, which do not contain enough information to discern all minerals present (e.g. patterns of heated samples). Assuming a correct qualitative interpretation was made and a single pattern exists in which all phases are sufficiently discernible, the obtained results indicate a good quantification can often be obtained with just that pattern. However, these results from theoretical experiments cannot automatically be extrapolated to all real-life experiments. In any case, PyXRD has proven to be useful when X-ray diffraction patterns are modelled for complex mineral assemblages containing mixed-layer phyllosilicates with a multi-specimen approach.

[Effects of annealing temperature on the structure and optical properties of ZnMgO films prepared by atom layer deposition].

PubMed

Sun, Dong-Xiao; Li, Jin-Hua; Fang, Xuan; Chen, Xin-Ying; Fang, Fang; Chu, Xue-Ying; Wei, Zhi-Peng; Wang, Xiao-Hua

2014-07-01

In the present paper, we report the research on the effects of annealing temperature on the crystal quality and optical properties of ZnMgO films deposited by atom layer deposition(ALD). ZnMgO films were prepared on quartz substrates by ALD and then some of the samples were treated in air ambient at different annealing temperature. The effects of annealing temperature on the crystal quality and optical properties of ZnMgO films were characterized by X-ray diffraction (XRD), photoluminescence (PL) and ultraviolet-visible (UV-Vis) absorption spectra. The XRD results showed that the crystal quality of ZnMgO films was significantly improved when the annealing temperature was 600 degrees C, meanwhile the intensity of(100) diffraction peak was the strongest. Combination of PL and UV-Vis absorption measurements showed that it can strongly promote the Mg content increasing in ZnMgO films and increase the band gap of films. So the results illustrate that suitable annealing temperature can effectively improve the crystal quality and optical properties of ZnMgO films.

Room temperature ferromagnetism in Mn-doped NiO nanoparticles

NASA Astrophysics Data System (ADS)

Layek, Samar; Verma, H. C.

2016-01-01

Mn-doped NiO nanoparticles of the series Ni1-xMnxO (x=0.00, 0.02, 0.04 and 0.06) are successfully synthesized using a low temperature hydrothermal method. Samples up to 6% Mn-doping are single phase in nature as observed from powder x-ray diffraction (XRD) studies. Rietveld refinement of the XRD data shows that all the single phase samples crystallize in the NaCl like fcc structure with space group Fm-3m. Unit cell volume decreases with increasing Mn-doping. Pure NiO nanoparticles show weak ferromagnetism, may be due to nanosize nature. Introduction of Mn within NiO lattice improves the magnetic properties significantly. Room temperature ferromagnetism is found in all the doped samples whereas the magnetization is highest for 2% Mn-doping and then decreases with further doping. The ZFC and FC branches in the temperature dependent magnetization separate well above 350 K indicating transition temperature well above room temperature for 2% Mn-doped NiO Nanoparticle. The ferromagnetic Curie temperature is found to be 653 K for the same sample as measured by temperature dependent magnetization study using vibrating sample magnetometer (VSM) in high vacuum.

In situ hydrogenation and decarboxylation of oleic acid into heptadecane over a Cu–Ni alloy catalyst using methanol as a hydrogen carrier

DOE PAGES

Zhang, Zihao; Yang, Qiwei; Chen, Hao; ...

2017-10-13

In this paper, supported Cu–Ni bimetallic catalysts were synthesized and evaluated for the in situ hydrogenation and decarboxylation of oleic acid using methanol as a hydrogen donor. The supported Cu–Ni alloy exhibited a significant improvement in both activity and selectivity towards the production of heptadecane in comparison with monometallic Cu and Ni based catalysts. The formation of the Cu–Ni alloy is demonstrated by high-angle annular dark-field scanning transmission electron microscopy (HADDF-STEM), energy dispersive X-ray spectroscopy (EDS-mapping), X-ray diffraction (XRD) and temperature programmed reduction (TPR). A partially oxidized Cu in the Cu–Ni alloy is revealed by diffuse reflectance infrared Fourier transformmore » spectroscopy (DRIFTS) following CO adsorption and X-ray photoelectron spectroscopy (XPS). The temperature programmed desorption of ethylene and propane (ethylene/propane-TPD) suggested that the formation of the Cu–Ni alloy inhibited the cracking of C–C bonds compared to Ni, and remarkably increased the selectivity to heptadecane. The temperature programmed desorption of acetic acid (acetic acid-TPD) indicated that the bimetallic Cu–Ni alloy and Ni catalysts had a stronger adsorption of acetic acid than that of the Cu catalyst. Finally, the formation of the Cu–Ni alloy and a partially oxidized Cu facilitates the decarboxylation reaction and inhibits the cracking reaction of C–C bonds, leading to enhanced catalytic activity and selectivity.« less

In situ hydrogenation and decarboxylation of oleic acid into heptadecane over a Cu–Ni alloy catalyst using methanol as a hydrogen carrier

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Zihao; Yang, Qiwei; Chen, Hao

In this paper, supported Cu–Ni bimetallic catalysts were synthesized and evaluated for the in situ hydrogenation and decarboxylation of oleic acid using methanol as a hydrogen donor. The supported Cu–Ni alloy exhibited a significant improvement in both activity and selectivity towards the production of heptadecane in comparison with monometallic Cu and Ni based catalysts. The formation of the Cu–Ni alloy is demonstrated by high-angle annular dark-field scanning transmission electron microscopy (HADDF-STEM), energy dispersive X-ray spectroscopy (EDS-mapping), X-ray diffraction (XRD) and temperature programmed reduction (TPR). A partially oxidized Cu in the Cu–Ni alloy is revealed by diffuse reflectance infrared Fourier transformmore » spectroscopy (DRIFTS) following CO adsorption and X-ray photoelectron spectroscopy (XPS). The temperature programmed desorption of ethylene and propane (ethylene/propane-TPD) suggested that the formation of the Cu–Ni alloy inhibited the cracking of C–C bonds compared to Ni, and remarkably increased the selectivity to heptadecane. The temperature programmed desorption of acetic acid (acetic acid-TPD) indicated that the bimetallic Cu–Ni alloy and Ni catalysts had a stronger adsorption of acetic acid than that of the Cu catalyst. Finally, the formation of the Cu–Ni alloy and a partially oxidized Cu facilitates the decarboxylation reaction and inhibits the cracking reaction of C–C bonds, leading to enhanced catalytic activity and selectivity.« less

Hierarchically porous LaFeO3 perovskite prepared from the pomelo peel bio-template for catalytic oxidation of NO

NASA Astrophysics Data System (ADS)

Zhao, Shaojun; Wang, Li; Wang, Ying; Li, Xing

2018-05-01

In this paper, pomelo peel was used as biological template to obtain hierarchically porous LaFeO3 perovskite for the catalytic oxidation of NO to NO2. In addition, X-ray diffraction (XRD), scanning electron microscopy (SEM), N2 adsorption-desorption analyses, X-ray photoelectron spectra (XPS), NO temperature-programmed desorption (NO-TPD), oxygen temperature-programmed desorption (O2-TPD) and hydrogen temperature-programmed reduction (H2-TPR) were used to investigate the micro-structure and the redox properties of the hierarchically porous LaFeO3 perovskite prepared from pomelo peel biological template and the LaFeO3 perovskite without the biological template. The results indicated that the hierarchically porous LaFeO3 perovskite successfully replicated the porous structure of pomelo peel with high specific surface area. Compared to the LaFeO3 perovskite prepared without the pomelo peel template, the hierarchically porous LaFeO3 perovskite showed better catalytic oxidization of NO to NO2 under the same conditions. The maximum NO conversions for LaFeO3 prepared with and without template were 90% at 305 °C and 76% at 313 °C, respectively. This is mainly attributed to the higher ratio of Fe4+/Fe3+, the hierarchically porous structure with more adsorbed oxygen species and higher surface area for the hierarchically porous LaFeO3 perovskite compared with the sample prepared without the pomelo peel template.

Low-temperature synthesis and structural properties of ferroelectric K 3WO 3F 3 elpasolite

NASA Astrophysics Data System (ADS)

Atuchin, V. V.; Gavrilova, T. A.; Kesler, V. G.; Molokeev, M. S.; Aleksandrov, K. S.

2010-06-01

Low-temperature ferroelectric G2 polymorph of K 3WO 3F 3 has been prepared by chemical synthesis. Structural and chemical properties of the final product have been evaluated with X-ray powder diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Structure parameters of G2-K 3WO 3F 3 are refined by the Rietveld method from XRD data measured at room temperature (space group Cm, Z = 2, a = 8.7350(3) Å, b = 8.6808(5) Å, c = 6.1581(3) Å, β = 135.124(3) Å, V = 329.46(3) Å 3; RB = 2.47%). Partial ordering of oxygen and fluorine atoms has been found over anion positions. Mechanism of ferroelectric phase transition in A 2BMO 3F 3 oxyfluorides is discussed.

Investigation on Structural and Optical Properties of Copper Telluride Thin Films with Different Annealing Temperature

NASA Astrophysics Data System (ADS)

Nishanthini, R.; Muthu Menaka, M.; Pandi, P.; Bahavan Palani, P.; Neyvasagam, K.

The copper telluride (Cu2Te) thin film of thickness 240nm was coated on a microscopic glass substrate by thermal evaporation technique. The prepared films were annealed at 150∘C and 250∘C for 1h. The annealing effect on Cu2Te thin films was examined with different characterization methods like X-ray Diffraction Spectroscopy (XRD), Scanning Electron Microscopy (SEM), Ultra Violet-Visible Spectroscopy (UV-VIS) and Photoluminescence (PL) Spectroscopy. The peak intensities of XRD spectra were increased while increasing annealing temperature from 150∘C to 250∘C. The improved crystallinity of the thin films was revealed. However, the prepared films are exposed complex structure with better compatibility. Moreover, the shift in band gap energy towards higher energies (blue shift) with increasing annealing temperature is observed from the optical studies.

Magnetic and dielectric behavior of chromium substituted Co-Mg ferrite nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jadoun, Priya, E-mail: priya4jadoun@gmail.com; Jyoti,; Prashant, B. L.

The chromium doped Co-Mg ferrite with composition Co{sub 0.5}Mg{sub 0.5}Cr{sub 0.2}Fe{sub 1.8}O{sub 4} has been synthesized using sol-gel auto combustion method. The crystal structure has been analyzed by X-ray diffraction (XRD) technique. XRD pattern reveals the formation of single phase cubic spinel structure. The magnetic measurements show ferromagnetic behavior at room temperature and large coercivity is observed on cooling down the temperature to 20 K. Dielectric constant (ε’) and dielectric loss tangent (tan δ) have been determined at room temperature as a function of frequency in the frequency range 75 kHz to 80 MHz. The decrease in dielectric constant with increasing frequency attributesmore » to Maxwell Wagner model and conduction mechanism in ferrites.« less

Dielectric and magnetic behavior of nanocrystalline Cu{sub 0.4}Co{sub 0.6}Fe{sub 2}O{sub 4} ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jadoun, Priya, E-mail: priya4jadoun@gmail.com; Sharma, Jyoti; Prashant, B. L.

2016-05-23

The mixed copper cobalt ferrite nanoparticles (Cu{sub 0.4}Co{sub 0.6}Fe{sub 2}O{sub 4}) have been synthesized by sol-gel auto combustion route with aqueous metal nitrates and citric acid as the precursor. The crystal structure has been analyzed by X-Ray diffraction (XRD) method. XRD reveals the formation of single phase cubic spinel structure. The Scanning Electron Microscopy (SEM) is used for morphological studies. The dielectric measurements at room temperature show the decrease in dielectric constant with increasing frequency which is attributed to Maxwell Wagner model and conduction mechanism in ferrites.The magnetic measurements show ferromagnetic behavior at room temperature and large coercivity is observedmore » on cooling down the temperature to 20 K.« less

Single step synthesis of nanostructured boron nitride for boron neutron capture therapy

NASA Astrophysics Data System (ADS)

Singh, Bikramjeet; Singh, Paviter; Kumar, Manjeet; Thakur, Anup; Kumar, Akshay

2015-05-01

Nanostructured Boron Nitride (BN) has been successfully synthesized by carbo-thermic reduction of Boric Acid (H3BO3). This method is a relatively low temperature synthesis route and it can be used for large scale production of nanostructured BN. The synthesized nanoparticles have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and differential thermal analyzer (DTA). XRD analysis confirmed the formation of single phase nanostructured Boron Nitride. SEM analysis showed that the particles are spherical in shape. DTA analysis showed that the phase is stable upto 900 °C and the material can be used for high temperature applications as well boron neutron capture therapy (BNCT).

DOE Office of Scientific and Technical Information (OSTI.GOV)

Winterrose, M.; Lucas, M; Yue, A

Synchrotron x-ray diffraction (XRD) measurements, nuclear forward scattering (NFS) measurements, and density functional theory (DFT) calculations were performed on L12-ordered Pd3Fe. Measurements were performed at 300 K at pressures up to 33 GPa, and at 7 GPa at temperatures up to 650 K. The NFS revealed a collapse of the 57Fe magnetic moment between 8.9 and 12.3 GPa at 300 K, coinciding with a transition in bulk modulus found by XRD. Heating the sample under a pressure of 7 GPa showed negligible thermal expansion from 300 to 523 K, demonstrating Invar behavior. Zero-temperature DFT calculations identified a ferromagnetic ground statemore » and showed several antiferromagnetic states had comparable energies at pressures above 20 GPa.« less

Temperature dependent surface and spectral modifications of nano V2O5 films

NASA Astrophysics Data System (ADS)

Manthrammel, M. Aslam; Fatehmulla, A.; Al-Dhafiri, A. M.; Alshammari, A. S.; Khan, Aslam

2017-03-01

Nanocrystalline V2O5 films have been deposited on glass substrates at 300°C substrate temperature using thermal evaporation technique and were subjected to thermal annealing at different temperatures 350, 400, and 550°C. X-ray diffraction (XRD) spectra exhibit sharper and broader characteristic peaks respectively indicating the rearrangement of nanocrystallite phases with annealing temperatures. Other phases of vanadium oxides started emerging with the rise in annealing temperature and the sample converted completely to VO2 (B) phase at 550°C annealing. FESEM images showed an increase in crystallite size with 350 and 400°C annealing temperatures followed by a decrease in crystallite size for the sample annealed at 550°C. Transmission spectra showed an initial redshift of the fundamental band edge with 350 and 400°C while a blue shift for the sample annealed at 550°C, which was in agreement with XRD and SEM results. The films exhibited smart window properties as well as nanorod growth at specific annealing temperatures. Apart from showing the PL and defect related peaks, PL studies also supported the observations made in the transmission spectra.

Effect of aging temperature on formation of sol-gel derived fluor-hydroxyapatite nanoparticles.

PubMed

Joughehdoust, S; Behnamghader, A; Jahandideh, R; Manafi, S

2010-04-01

Synthetic hydroxyapatite (HA) has been recognized as one of the most important bone substitute materials in orthopaedics and dentistry over past few decades because of its chemical and biological similarity to the mineral phase of human bone. One solution for reduction the solubility of HA in biological environments is replacing F- by OH in HA structure and forming fluor-hydroxyapatite (FHA) solid solution. In this paper, FHA nanoparticles were successfully synthesized by a sol-gel method. Also, the influence of aging temperature on formation of FHA powder was studied. Equimolar solutions of calcium nitrate tetrahydrate, triethyl phosphite and ammonium fluoride in ethanol were used as Ca, P and F precursors. After aging at different temperatures, the synthesized powders were heat treated at 550 degrees C. The powders were investigated with X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), selected area electron diffraction pattern (SAED), energy dispersive analysis of X-ray (EDAX) and zetasizer measurement. The results of XRD proved the presence of fluorapatite (FA) and HA in all samples. In addition, the formation of FHA was confirmed by FT-IR results. XRD studies also showed that the crystallites were in nanometric scale. At the same time, this result was in good agreement with the result of zetasizer analysis.

Influence of cobalt doping on structural and magnetic properties of BiFeO3 nanoparticles

NASA Astrophysics Data System (ADS)

Khan, U.; Adeela, N.; Javed, K.; Riaz, S.; Ali, H.; Iqbal, M.; Han, X. F.; Naseem, S.

2015-11-01

Nanocrystalline cobalt-doped bismuth ferrites with general formula of BiFe1- δ Co δ O3 (0 ≤ δ ≤ 0.1) have been synthesized using solution evaporation method. Structure and phase identification was performed with X-ray diffraction (XRD) technique. The results confirm the formation of rhombohedral-distorted Perovskite structure with R3c symmetry. A decrease in lattice parameters and an increase in X-ray density have been observed with increasing cobalt concentration in BiFeO3. Particle size determined by transmission electron microscope was in good agreement with XRD, i.e., 39 nm. Room-temperature coercivity and saturation magnetization of nanoparticles were increased up to 7.5 % of cobalt doping. Low-temperature magnetic measurements of selected sample showed increasing behavior in saturation magnetization, coercivity, effective magnetic moments, and anisotropy constant. An increase in coercivity with decrease in temperature followed theoretical model of Kneller's law, while modified Bloch's model was employed for saturation magnetization in temperature range of 5-300 K.

Characterization of pulsed laser deposition grown V2O3 converted VO2

NASA Astrophysics Data System (ADS)

Majid, Suhail; Shukla, D. K.; Rahman, F.; Gautam, Kamini; Sathe, V. G.; Choudhary, R. J.; Phase, D. M.

2016-10-01

Controllable tuning of Metal-insulator transition in VxOy thin film has been a field of extensive research. However controlled synthesis of desired Vanadium oxide phase is a challenging task. We have successfully achieved VO2 phase on Silicon substrate after post deposition annealing treatment to the PLD grown as deposited V2O3 thin films. The annealed thin film was characterized by x-ray diffraction (XRD), resistivity, Raman spectroscopy, X-ray absorption spectroscopy (XAS) and X-ray photoelectron spectroscopy (XPS) measurements. XRD confirms the crystalline nature and growth of VO2 phase in thin film. The characteristic MIT was observed from resistivity measurements and transition temperature appeared at lower value around 336 K, compared to bulk VO2. The structural transition accompanied with MIT from lower temperature monoclinic phase to higher temperature Rutile phase became evident from temperature dependent Raman measurements. Chemical state of vanadium was examined using XAS and XPS measurements which confirm the presence of +4 oxidation state of vanadium in thin film.

Multivariate analysis of DSC-XRD simultaneous measurement data: a study of multistage crystalline structure changes in a linear poly(ethylene imine) thin film.

PubMed

Kakuda, Hiroyuki; Okada, Tetsuo; Otsuka, Makoto; Katsumoto, Yukiteru; Hasegawa, Takeshi

2009-01-01

A multivariate analytical technique has been applied to the analysis of simultaneous measurement data from differential scanning calorimetry (DSC) and X-ray diffraction (XRD) in order to study thermal changes in crystalline structure of a linear poly(ethylene imine) (LPEI) film. A large number of XRD patterns generated from the simultaneous measurements were subjected to an augmented alternative least-squares (ALS) regression analysis, and the XRD patterns were readily decomposed into chemically independent XRD patterns and their thermal profiles were also obtained at the same time. The decomposed XRD patterns and the profiles were useful in discussing the minute peaks in the DSC. The analytical results revealed the following changes of polymorphisms in detail: An LPEI film prepared by casting an aqueous solution was composed of sesquihydrate and hemihydrate crystals. The sesquihydrate one was lost at an early stage of heating, and the film changed into an amorphous state. Once the sesquihydrate was lost by heating, it was not recovered even when it was cooled back to room temperature. When the sample was heated again, structural changes were found between the hemihydrate and the amorphous components. In this manner, the simultaneous DSC-XRD measurements combined with ALS analysis proved to be powerful for obtaining a better understanding of the thermally induced changes of the crystalline structure in a polymer film.

Heating-freezing effects on the orientation of kaolin clay particles

DOE PAGES

Jaradat, Karam A.; Darbari, Zubin; Elbakhshwan, Mohamed; ...

2017-09-29

The effects of temperature changes on the particle orientation of a consolidated kaolin are studied using XRD experiments. Here, two sets of equipment were utilized in this study: a benchtop equipment, and a synchrotron beamline at the National Synchrotron Light Source II (NSLS-II) at Brookhaven National Laboratory. The kaolin specimens tested in the benchtop XRD were subjected to elevated and freezing temperatures ex-situ, while those used for the NSLS-II experiment were exposed to the temperature changes in-situ. The temperatures considered in this study range from freezing (-10 °C) to elevated temperature below boiling (90 °C). The thermally-induced reorientation of claymore » mineral particles is highly dependent on the relative orientation of the clay mineral particles with respect to the applied thermal gradient. For example, kaolin samples with kaolinite particles oriented perpendicular to the thermal gradient, and to the expected thermally-induced pore water flow, experience much higher particles reorientations compared to samples with particles initially oriented parallel to the thermal gradient. Lastly, freezing kaolin preserved its microstructure as ice crystals form.« less

Heating-freezing effects on the orientation of kaolin clay particles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jaradat, Karam A.; Darbari, Zubin; Elbakhshwan, Mohamed

The effects of temperature changes on the particle orientation of a consolidated kaolin are studied using XRD experiments. Here, two sets of equipment were utilized in this study: a benchtop equipment, and a synchrotron beamline at the National Synchrotron Light Source II (NSLS-II) at Brookhaven National Laboratory. The kaolin specimens tested in the benchtop XRD were subjected to elevated and freezing temperatures ex-situ, while those used for the NSLS-II experiment were exposed to the temperature changes in-situ. The temperatures considered in this study range from freezing (-10 °C) to elevated temperature below boiling (90 °C). The thermally-induced reorientation of claymore » mineral particles is highly dependent on the relative orientation of the clay mineral particles with respect to the applied thermal gradient. For example, kaolin samples with kaolinite particles oriented perpendicular to the thermal gradient, and to the expected thermally-induced pore water flow, experience much higher particles reorientations compared to samples with particles initially oriented parallel to the thermal gradient. Lastly, freezing kaolin preserved its microstructure as ice crystals form.« less

Temperature characterization of dielectric permittivity and AC conductivity of nano copper oxide-doped polyaniline composite

NASA Astrophysics Data System (ADS)

Shubha, L. N.; Madhusudana Rao, P.

2016-06-01

The polyaniline/copper oxide (PANI/CuO) nanocomposite was prepared by mixing solutions of polyaniline and copper oxide nanoparticles in dimethyl sulfoxide (DMSO). The synthesized polymer nanocomposites were characterized by X-ray powder diffraction (XRD), scanning electron microscope (SEM) and UV-visible spectroscopy. The characteristic peaks in XRD and UV-visible spectra confirmed the presence of CuO in the polymer structure. SEM images indicated morphological changes in the composite matrix as compared to the pristine PANI. The DC conductivity measurements were performed using two-probe method for various temperatures. AC conductivity and dielectric response of the composites were investigated in the frequency range of 102-106Hz using LCR meter. Dielectric permittivity ɛ‧(w) and dielectric loss factor ɛ‧‧(w) were investigated. It was observed that ɛ‧(w) and ɛ‧‧(w) decrease with increase in frequency at all temperatures. At a particular frequency it is observed that both ɛ‧(w) and ɛ‧‧(w) increase with increase in temperature. It was also observed that AC conductivity increased with increase in frequency and temperature.

Solid state characterization of E2101, a novel antispastic drug.

PubMed

Kushida, Ikuo; Ashizawa, Kazuhide

2002-10-01

E2101, a novel antispastic drug, was found to exist in at least two polymorphs that were confirmed by X-ray powder diffraction (XRD). These two species are designated forms I and II. The physicochemical and thermodynamic properties of these polymorphs were characterized by variable temperature XRD, thermal analysis, hygroscopicity measurements, and dissolution studies. The transition temperature was also estimated from the solubilities determined at various temperatures. The E2101 polymorphs were anhydrous and adsorbed little moisture under high humidity conditions. The melting onsets and heats of fusion for form I were 148.1 +/- 0.2 degrees C and 38.2 +/- 1.0 kJ/mol, respectively, and for form II were 139.8 +/- 0.4 degrees C and 35.2 +/- 0.5 kJ/mol, respectively. The intrinsic dissolution rate of form II in JP 2 medium was 1.5-fold faster than that of form I, corresponding to the rank order of the aqueous solubility and the enthalpy of fusion. Accordingly, form I was thought to be thermodynamically more stable than form II and thus suitable for further development. According to the thermal analysis and variable temperature XRD results, the recrystallization of form I occurred at approximately 145 degrees C after form II melted, however, no crystal transition behavior was observed below the lower melting point. The DSC thermograms at various heating rates and van't Hoff plots from the solubility studies indicated that the polymorphic pair would be monotropic. Copyright 2002 Wiley-Liss Inc. and the American Pharmaceutical Association

Structural properties and gas sensing behavior of sol-gel grown nanostructured zinc oxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rajyaguru, Bhargav; Gadani, Keval; Kansara, S. B.

2016-05-06

In this communication, we report the results of the studies on structural properties and gas sensing behavior of nanostructured ZnO grown using acetone precursor based modified sol-gel technique. Final product of ZnO was sintered at different temperatures to vary the crystallite size while their structural properties have been studied using X-ray diffraction (XRD) measurement performed at room temperature. XRD results suggest the single phasic nature of all the samples and crystallite size increases from 11.53 to 20.96 nm with increase in sintering temperature. Gas sensing behavior has been studied for acetone gas which indicates that lower sintered samples are moremore » capable to sense the acetone gas and related mechanism has been discussed in the light of crystallite size, crystal boundary density, defect mechanism and possible chemical reaction between gas traces and various oxygen species.« less

Magnetic properties of M0.3Fe2.7O4 (M = Fe, Zn and Mn) ferrites nanoparticles

NASA Astrophysics Data System (ADS)

Modaresi, Nahid; Afzalzadeh, Reza; Aslibeiki, Bagher; Kameli, Parviz

2018-06-01

In the present article a comparative study on the structural and magnetic properties of nano-sized M0.3Fe0.7Fe2O4 (M = Fe, Zn and Mn) ferrites have been reported. The X-ray diffraction (XRD) patterns show that the crystallite size depends on the cation distribution. The Rietveld refinement of XRD patterns using MAUD software determines the distribution of cations and unit cell dimensions. The magnetic measurements show that the maximum and minimum value of saturation magnetization is obtained for Zn and Mn doped samples, respectively. The peak temperature of AC magnetic susceptibility of Zn and Fe doped samples below 300 K shows the superparamagnetic behavior in these samples at room temperature. the AC susceptibility results confirm the presence of strong interactions between the nanoparticles which leads to a superspin glass state in the samples at low temperatures.

Electrical properties of NiAs-type MnTe films with preferred crystallographic plane of (110)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, L.; Wang, Z. H., E-mail: zhwang@imr.ac.cn; Zhang, Z. D.

2016-01-28

NiAs-type manganese telluride (MnTe) films with preferred crystallographic plane of (110) were prepared on Si/SiO{sub 2} substrates by pulsed laser deposition. X-ray diffraction (XRD) of the films was studied at different temperatures. The XRD peak of MnTe (110) films shifts to higher angle with decreasing temperature, showing the decrease of the lattice parameter. Resistivity of the films was studied in the temperature range of 2–350 K. The bump between 150 and 250 K was observed in the films, which may be related to the special s-d and p-d overlaps induced by the compressed lattice. The magnon drag effect near its Néel temperaturemore » T{sub N} and enlarged magnetic-elastic coupling below 100 K were observed and analyzed in details.« less

Experimental investigation of nearly monodispersed ternary Mn_{0.5}Zn_{0.5}Fe_{2}O_{4} magnetic fluid

NASA Astrophysics Data System (ADS)

Parekh, K.; Upadhyay, R. V.; Mehta, R. V.; Aswal, V. K.

2008-03-01

The experimental investigations of a nearly monodispersed magnetic fluid, containing a ternary Mn_{0.5}Zn_{0.5}Fe_{2}O_{4} (MZ5) magnetic fluid, are carried out using XRD, TEM, Small Angle Neutron Scattering (SANS) and a SQUID magnetometer. The XRD and TEM measurements give the particle size to be 7.5 and 8.4 nm respectively, and confirms the single phase cubic spinel structure. The size distribution retrieved from TEM is found to be very narrow (<10{%}). Room temperature magnetic measurement fits with the Langevin's function modified for the particle size distribution as well as for the particle-particle interaction parameter. M(H)-measurements as a function of field for different temperatures show that the system is superparamagnetic at room temperature and develops coercivity at 5 K. Figs 4, Refs 12.

Influence of reaction time and synthesis temperature on the physical properties of ZnO nanoparticles synthesized by the hydrothermal method

NASA Astrophysics Data System (ADS)

Wasly, H. S.; El-Sadek, M. S. Abd; Henini, Mohamed

2018-01-01

Influence of synthesis temperature and reaction time on the structural and optical properties of ZnO nanoparticles synthesized by the hydrothermal method was investigated using X-ray diffraction (XRD), high resolution transmission electron microscopy (HR-TEM), energy-dispersive X-ray, Fourier transform infra-red spectroscopy, and UV-visible and fluorescence spectroscopy. The XRD pattern and HR-TEM images confirmed the presence of crystalline hexagonal wurtzite ZnO nanoparticles with average crystallite size in the range 30-40 nm. Their energy gap determined by fluorescence was found to depend on the synthesis temperature and reaction time with values in the range 2.90-3.78 eV. Thermal analysis, thermogravimetric and the differential scanning calorimetry were used to study the thermal reactions and weight loss with heat of the prepared ZnO nanoparticles.

Physicochemical characterization of point defects in fluorine doped tin oxide films

NASA Astrophysics Data System (ADS)

Akkad, Fikry El; Joseph, Sudeep

2012-07-01

The physical and chemical properties of spray deposited FTO films are studied using FESEM, x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS), electrical and optical measurements. The results of XRD measurements showed that the films are polycrystalline (grain size 20-50 nm) with Rutile structure and mixed preferred orientation along the (200) and (110) planes. An angular shift of the XRD peaks after F-doping is observed and interpreted as being due to the formation of substitutional fluorine defects (FO) in presence of high concentration of oxygen vacancies (VO) that are electrically neutral. The electrical neutrality of oxygen vacancies is supported by the observation that the electron concentration n is two orders of magnitude lower than the VO concentration calculated from chemical analyses using XPS measurements. It is shown that an agreement between XPS, XRD, and Hall effect results is possible provided that the degree of deviation from stoichiometry is calculated with the assumption that the major part of the bulk carbon content is involved in O-C bonds. High temperature thermal annealing is found to cause an increase in the FO concentration and a decrease in both n and VO concentrations with the increase of the annealing temperature. These results could be interpreted in terms of a high temperature chemical exchange reaction between the SnO2 matrix and a precipitated fluoride phase. In this reaction, fluorine is released to the matrix and Sn is trapped by the fluoride phase, thus creating substitutional fluorine FO and tin vacancy VSn defects. The enthalpy of this reaction is determined to be approximately 2.4 eV while the energy of formation of a VSn through the migration of SnSn host atom to the fluoride phase is approximately 0.45 eV.

XRD and FTIR crystallinity indices in sound human tooth enamel and synthetic hydroxyapatite.

PubMed

Reyes-Gasga, José; Martínez-Piñeiro, Esmeralda L; Rodríguez-Álvarez, Galois; Tiznado-Orozco, Gaby E; García-García, Ramiro; Brès, Etienne F

2013-12-01

The crystallinity index (CI) is a measure of the percentage of crystalline material in a given sample and it is also correlated to the degree of order within the crystals. In the literature two ways are reported to measure the CI: X-ray diffraction and infrared spectroscopy. Although the CI determined by these techniques has been adopted in the field of archeology as a structural order measure in the bone with the idea that it can help e.g. in the sequencing of the bones in chronological and/or stratigraphic order, some debate remains about the reliability of the CI values. To investigate similarities and differences between the two techniques, the CI of sound human tooth enamel and synthetic hydroxyapatite (HAP) was measured in this work by X-ray diffraction (XRD) and Fourier Transform Infrared spectroscopy (FTIR), at room temperature and after heat treatment. Although the (CI)XRD index is related to the crystal structure of the samples and the (CI)FTIR index is related to the vibration modes of the molecular bonds, both indices showed similar qualitative behavior for heat-treated samples. At room temperature, the (CI)XRD value indicated that enamel is more crystalline than synthetic HAP, while (CI)FTIR indicated the opposite. Scanning (SEM) and transmission (TEM) images were also used to corroborate the measured CI values. © 2013.

Radiation-Induced Changes in Quartz, A Mineral Analog of Nuclear Power Plant Concrete Aggregates

DOE Office of Scientific and Technical Information (OSTI.GOV)

Silva, Chinthaka M.; Rosseel, Thomas M.; Kirkegaard, Marie C.

Quartz single-crystal samples consisting of α-quartz crystal structure were neutron irradiated to fluences of 5 × 10 18, 4 × 10 19, and 2 × 10 20 n/cm 2 (E > 0.1 MeV) at two temperatures (52 and 95 °C). The changes in the α-quartz phase as a function of these two conditions (temperature and fluence) were studied using X-ray powder diffraction (XRD), Raman spectroscopy, and transmission electron microscopy (TEM), and the results acquired using these complementary techniques are presented in a single place for the first time. XRD studies showed that the lattice parameters of α-quartz increased with increasingmore » neutron flux. The lattice growth was larger for the samples that were neutron irradiated at 52 °C than at 95 °C. Moreover, an amorphous content was determined in the quartz samples neutron irradiated at 4 × 10 19 n/cm 2, with the greater amount being in the 52 °C irradiated sample. Complete amorphization of quartz was observed at a fluence of 2 × 10 20 n/cm 2 (E > 0.1 MeV) using XRD and confirmed by TEM characterization and Raman spectroscopic studies. In conclusion, the cause for α-quartz lattice expansion and sample amorphization was also explored using XRD and Raman spectroscopic studies.« less

Radiation-Induced Changes in Quartz, A Mineral Analog of Nuclear Power Plant Concrete Aggregates

DOE PAGES

Silva, Chinthaka M.; Rosseel, Thomas M.; Kirkegaard, Marie C.

2018-03-07

Quartz single-crystal samples consisting of α-quartz crystal structure were neutron irradiated to fluences of 5 × 10 18, 4 × 10 19, and 2 × 10 20 n/cm 2 (E > 0.1 MeV) at two temperatures (52 and 95 °C). The changes in the α-quartz phase as a function of these two conditions (temperature and fluence) were studied using X-ray powder diffraction (XRD), Raman spectroscopy, and transmission electron microscopy (TEM), and the results acquired using these complementary techniques are presented in a single place for the first time. XRD studies showed that the lattice parameters of α-quartz increased with increasingmore » neutron flux. The lattice growth was larger for the samples that were neutron irradiated at 52 °C than at 95 °C. Moreover, an amorphous content was determined in the quartz samples neutron irradiated at 4 × 10 19 n/cm 2, with the greater amount being in the 52 °C irradiated sample. Complete amorphization of quartz was observed at a fluence of 2 × 10 20 n/cm 2 (E > 0.1 MeV) using XRD and confirmed by TEM characterization and Raman spectroscopic studies. In conclusion, the cause for α-quartz lattice expansion and sample amorphization was also explored using XRD and Raman spectroscopic studies.« less

Study on the structural, optical, and electrical properties of the yellow light-emitting diode grown on free-standing (0001) GaN substrate

NASA Astrophysics Data System (ADS)

Deng, Gaoqiang; Zhang, Yuantao; Yu, Ye; Yan, Long; Li, Pengchong; Han, Xu; Chen, Liang; Zhao, Degang; Du, Guotong

2018-04-01

In this paper, GaN-based yellow light-emitting diodes (LEDs) were homoepitaxially grown on free-standing (0001) GaN substrates by metal-organic chemical vapor deposition. X-ray diffraction (XRD), photoluminescence (PL), and electroluminescence (EL) measurements were conducted to investigate the structural, optical, and electrical properties of the yellow LED. The XRD measurement results showed that the InGaN/GaN multiple quantum wells (MQWs) in the LED structure have good periodicity because the distinct MQWs related higher order satellite peaks can be clearly observed from the profile of 2θ-ω XRD scan. The low temperature (10 K) and room temperature PL measurement results yield an internal quantum efficiency of 16% for the yellow LED. The EL spectra of the yellow LED present well Gaussian distribution with relatively low linewidth (47-55 nm), indicating the homogeneous In-content in the InGaN quantum well layers in the yellow LED structure. It is believed that this work will aid in the future development of GaN on GaN LEDs with long emission wavelength.

[Spectral characteristics and implication of granite from pozaiying molybdenite deposits in west of Guangdong].

PubMed

An, Yan-Fei; Zhong, Li-li; Zhou, Yang-Zhang; Chen, Qing; Li, Xing-yuan

2014-06-01

Some granite samples from Pozaiying molybdenite deposits in the west of Guangdong were retrieved to characterize the spectral signature of XRD, FT-NIR and Raman. The results show that compared to the Porphyry granite and granite in the far zone, the signal of XRD and Raman of granite in near zone is weaker while the signal of FT-NIR is stronger. The authors' analyses indicate that the FWHM of quartz (101) peak in XRD, Sericite peak (4 529 cm(-1)) in FT-NIR and quartz peak in Raman shift from the latter are higher than those of former two. Those spectral characteristics indicate that compared with other samples, the content of petrogenetic mineral in samples from near zone is lower while the content of alteration mineral is higher, and its crystallinity and crystallization temperatures are both lower. The authors' studies suggest that there may be an alteration zone, embracing the granite-porphyry, which comprised low temperature mineral, and the quartz-porphyry which related to molybdenite mineralization belongs to the zone near Guanshanzhang mass.

Electrical Properties and Dipole Relaxation Behavior of Zinc-Substituted Cobalt Ferrite

NASA Astrophysics Data System (ADS)

Supriya, Sweety; Kumar, Sunil; Kar, Manoranjan

2017-12-01

Co1- x Zn x Fe2O4 ceramics with x = 0.00, 0.05, 0.10, 0.15 and 0.20 were synthesized by a modified citric acid sol-gel method. The crystalline phase of the samples was characterized by the powder x-ray diffraction technique (XRD) and the Rietveld analysis of the XRD patterns. The morphology and particle size were studied using field emission scanning electron microscopy. Fourier transform infrared spectroscopy studies were consistent with the XRD results. The impedance measurements were carried out from 100 Hz to 10 MHz at different temperatures from 40°C to 300°C. The frequency dispersion of dielectric was analyzed with a modified Debye equation. The activation energy derived from the dielectric constant and the impedance follows the Arrhenius law and are comparable with each other. The dielectric relaxation and impedance relaxation are correlated in terms of activation energy, show a good temperature stability of the dielectrics and are useful for their applications in microelectronic devices such as filters, capacitors, resonators, etc.

In situ SAXS study on size changes of platinum nanoparticles with temperature

NASA Astrophysics Data System (ADS)

Wang, W.; Chen, X.; Cai, Q.; Mo, G.; Jiang, L. S.; Zhang, K.; Chen, Z. J.; Wu, Z. H.; Pan, W.

2008-09-01

Poly(vinylpyrrolidone) (PVP)-coated platinum (Pt) nanoparticles were prepared in methanol-water reduction method. In situ small-angle X-ray scattering (SAXS) and X-ray diffraction (XRD) techniques were used to probe the size change of particles and crystallites with temperature. Tangent-by-tangent (TBT) method of SAXS data analysis was improved and used to get the particle size distribution (PSD) from SAXS intensity. Scherrer’s equation was used to derive the crystallite size from XRD pattern. Combining SAXS and XRD results, a step-like characteristic of the Pt nanoparticle growth has been found. Three stages (diffusion, aggregation, and agglomeration) can be used to describe the growth of the Pt nanoparticles and nanocrystallites. Aggregation was found to be the main growth mode of the Pt nanoparticles during heating. The maximum growth rates of Pt nanoparticles and Pt nanocrystallites, as well as the maximum aggregation degree of Pt nanocrystallites were found, respectively, at 250 °C, 350 °C and 300 °C. These results are helpful to understanding the growth mode of nanoparticles, as well as controlling the nanoparticle size.

The influence of calcination temperatures on the acid-based properties and catalytic activity for the 1,3-butadiene synthesis from ethanol/acetaldehyde mixture

NASA Astrophysics Data System (ADS)

Gao, Meixiang; Jiang, Haoxi; Zhang, Minhua

2018-05-01

The influences of the calcination temperature on the catalysts' acid-based properties and catalytic activity for the 1,3-butadiene synthesis from ethanol are investigated. The results show that the 2 wt% ZrO2/Nano-SiO2 calcined at 773 K shows the best performance with the selectivity of 93.18% and conversion of 58.52% when reacted at 593 K, a WHSV of 1.8 h-1 and 3.5:1 volume ratio ethanol-to-acetaldehyde in an atmospheric fixed-bed reactor. Prepared catalysts were characterized by N2 adsorption-desorption, XRD, temperature-programmed desorption of NH3 and CO2, FTIR spectroscopy of adsorbed pyridine and CO2. Based on the relationship between the catalyst activity and its properties, the fact can be presumed that the formation and strength of Zrsbnd Osbnd Si bond determines the acid-based properties of the catalyst. In addition, moderate-intensity weak acid-basic sites are more suitable for ethanol conversion to BD with the amount of acid and basic sites as close as possible.

Optical and dielectric properties of NiFe2O4 nanoparticles under different synthesized temperature

NASA Astrophysics Data System (ADS)

Parishani, Marziye; Nadafan, Marzieh; Dehghani, Zahra; Malekfar, Rasoul; Khorrami, G. H. H.

In this research, NiFe2O4 nanoparticles was prepared via the simple sol-gel route, using different sintering temperature. This nanoparticle was characterized via X-ray diffraction (XRD) pattern, scanning electron microscopy (SEM), and FTIR spectra. The XRD patterns show by increasing the synthesized temperature, the intensity, and broadening of peaks are decreased so the results are more crystallization and raising the size of nanoparticles. The size distribution in the histogram of the NiFe2O4 nanoparticles is 42, 96, and 315 nm at 750 °C, 850 °C, and 950 °C, respectively. The FTIR spectra were evaluated using Kramers-Kronig method. Results approved the existing of certain relations between sintering temperatures and grain size of nanoparticles. By raising the temperature from 750 °C to 950 °C, the grain size was increased from 70 nm to 300 nm and the optical constants of nanoparticles were strongly related to synthesizing temperature as well. Since by increasing temperature, both real/imaginary parts of the refractive index and dielectric function were decreased. Consequently, the transversal (TO) and longitudinal (LO) phonon frequencies are detected. The TO and LO frequencies have shifted to red frequencies by increasing reaction temperature.

High temperature electrical resistivity and Seebeck coefficient of Ge2Sb2Te5 thin films

NASA Astrophysics Data System (ADS)

Adnane, L.; Dirisaglik, F.; Cywar, A.; Cil, K.; Zhu, Y.; Lam, C.; Anwar, A. F. M.; Gokirmak, A.; Silva, H.

2017-09-01

High-temperature characterization of the thermoelectric properties of chalcogenide Ge2Sb2Te5 (GST) is critical for phase change memory devices, which utilize self-heating to quickly switch between amorphous and crystalline states and experience significant thermoelectric effects. In this work, the electrical resistivity and Seebeck coefficient are measured simultaneously as a function of temperature, from room temperature to 600 °C, on 50 nm and 200 nm GST thin films deposited on silicon dioxide. Multiple heating and cooling cycles with increasingly maximum temperature allow temperature-dependent characterization of the material at each crystalline state; this is in contrast to continuous measurements which return the combined effects of the temperature dependence and changes in the material. The results show p-type conduction (S > 0), linear S(T), and a positive Thomson coefficient (dS/dT) up to melting temperature. The results also reveal an interesting linearity between dS/dT and the conduction activation energy for mixed amorphous-fcc GST, which can be used to estimate one parameter from the other. A percolation model, together with effective medium theory, is adopted to correlate the conductivity of the material with average grain sizes obtained from XRD measurements. XRD diffraction measurements show plane-dependent thermal expansion for the cubic and hexagonal phases.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Winterrose, M.L.; Lucas, M.S.; Yue, A.F.

Synchrotron x-ray diffraction (XRD) measurements, nuclear forward scattering (NFS) measurements, and density functional theory (DFT) calculations were performed on L1{sub 2}-ordered Pd{sub 3}Fe. Measurements were performed at 300 K at pressures up to 33 GPa, and at 7 GPa at temperatures up to 650 K. The NFS revealed a collapse of the Fe57 magnetic moment between 8.9 and 12.3 GPa at 300 K, coinciding with a transition in bulk modulus found by XRD. Heating the sample under a pressure of 7 GPa showed negligible thermal expansion from 300 to 523 K, demonstrating Invar behavior. Zero-temperature DFT calculations identified a ferromagneticmore » ground state and showed several antiferromagnetic states had comparable energies at pressures above 20 GPa.« less

Structural and Optical properties of poly-crystalline BaTiO3 and SrTiO3 prepared via solid state route

NASA Astrophysics Data System (ADS)

Jarabana, Kanaka M.; Mishra, Ashutosh; Bisen, Supriya

2016-10-01

Polycrystalline BaTiO3 (BTO) and SrTiO3 (STO) were synthesized by solid state route method and properties of made polycrystalline were characterized by X-Ray diffraction (XRD), Raman Spectroscopy & FTIR Spectroscopy. XRD analysis shows that samples are crystalline in nature. In Raman Spectroscopy measurement, the experiment has been done with the help of JOBIN-YOVN HORIBA LABRAM HR800 single monochromator, which is coupled with a “peltier cooled” charge coupled device (CCD). Raman Spectroscopy at low temperature measurement shows the phase transition above & below the curie temperature in samples. Fourier transform Infrared spectroscopy was used to determine the Ti-O bond length position.

Single step synthesis of nanostructured boron nitride for boron neutron capture therapy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Bikramjeet; Singh, Paviter; Kumar, Akshay, E-mail: akshaykumar.tiet@gmail.com

2015-05-15

Nanostructured Boron Nitride (BN) has been successfully synthesized by carbo-thermic reduction of Boric Acid (H{sub 3}BO{sub 3}). This method is a relatively low temperature synthesis route and it can be used for large scale production of nanostructured BN. The synthesized nanoparticles have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and differential thermal analyzer (DTA). XRD analysis confirmed the formation of single phase nanostructured Boron Nitride. SEM analysis showed that the particles are spherical in shape. DTA analysis showed that the phase is stable upto 900 °C and the material can be used for high temperature applications asmore » well boron neutron capture therapy (BNCT)« less

Electro–optical properties of poly(vinyl acetate)/polyindole composite film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bhagat, D. J., E-mail: bhagatd@rediffmail.com; Dhokane, G. R.; Bajaj, N. S.

2016-05-06

In present work, electrical and optical properties of poly(vinyl acetate)/polyindole (PVAc/PIN) composite film are reported. The prepared composite was characterized via X–ray diffraction (XRD), UV–Vis spectroscopy and DC conductivity measurements. The polymer chain separation was determined using XRD analysis. An attempt has been made to study the temperature dependence of DC conductivity of PVAc/PIN composite in temperature range 308–373 K. The DC conductivity initially increases and reaches to 2.45×10–7 S/cm. The optical band gap value of composite is determined as 4.77 eV. The semiconducting nature of composite observed from electronic as well as optical band gap and Arrhenius behavior of DCmore » plot.« less

The phase diagram of ammonium nitrate.

PubMed

Chellappa, Raja S; Dattelbaum, Dana M; Velisavljevic, Nenad; Sheffield, Stephen

2012-08-14

The pressure-temperature (P-T) phase diagram of ammonium nitrate (AN) [NH(4)NO(3)] has been determined using synchrotron x-ray diffraction (XRD) and Raman spectroscopy measurements. Phase boundaries were established by characterizing phase transitions to the high temperature polymorphs during multiple P-T measurements using both XRD and Raman spectroscopy measurements. At room temperature, the ambient pressure orthorhombic (Pmmn) AN-IV phase was stable up to 45 GPa and no phase transitions were observed. AN-IV phase was also observed to be stable in a large P-T phase space. The phase boundaries are steep with a small phase stability regime for high temperature phases. A P-V-T equation of state based on a high temperature Birch-Murnaghan formalism was obtained by simultaneously fitting the P-V isotherms at 298, 325, 446, and 467 K, thermal expansion data at 1 bar, and volumes from P-T ramping experiments. Anomalous thermal expansion behavior of AN was observed at high pressure with a modest negative thermal expansion in the 3-11 GPa range for temperatures up to 467 K. The role of vibrational anharmonicity in this anomalous thermal expansion behavior has been established using high P-T Raman spectroscopy.

The phase diagram of ammonium nitrate

NASA Astrophysics Data System (ADS)

Chellappa, Raja S.; Dattelbaum, Dana M.; Velisavljevic, Nenad; Sheffield, Stephen

2012-08-01

The pressure-temperature (P-T) phase diagram of ammonium nitrate (AN) [NH4NO3] has been determined using synchrotron x-ray diffraction (XRD) and Raman spectroscopy measurements. Phase boundaries were established by characterizing phase transitions to the high temperature polymorphs during multiple P-T measurements using both XRD and Raman spectroscopy measurements. At room temperature, the ambient pressure orthorhombic (Pmmn) AN-IV phase was stable up to 45 GPa and no phase transitions were observed. AN-IV phase was also observed to be stable in a large P-T phase space. The phase boundaries are steep with a small phase stability regime for high temperature phases. A P-V-T equation of state based on a high temperature Birch-Murnaghan formalism was obtained by simultaneously fitting the P-V isotherms at 298, 325, 446, and 467 K, thermal expansion data at 1 bar, and volumes from P-T ramping experiments. Anomalous thermal expansion behavior of AN was observed at high pressure with a modest negative thermal expansion in the 3-11 GPa range for temperatures up to 467 K. The role of vibrational anharmonicity in this anomalous thermal expansion behavior has been established using high P-T Raman spectroscopy.

High-temperature investigation on morphology, phase and size of iron/iron-oxide core–shell nanoclusters for radiation nanodetector

NASA Astrophysics Data System (ADS)

Khanal, Lokendra Raj; Williams, Thomas; Qiang, You

2018-06-01

Iron/iron-oxide (Fe–Fe3O4) core–shell nanoclusters (NCs) synthesized by a cluster deposition technique were subjected to a study of their high temperature structural and morphological behavior. Annealing effects have been investigated up to 800 °C in vacuum, oxygen and argon environments. The ~18 nm average size of the as-prepared NCs increases slowly in temperatures up to 500 °C in all three environments. The size increases abruptly in the argon environment but slowly in vacuum and oxygen when annealed at 800 °C. The x-ray diffraction (XRD) studies have shown that the iron core remains in the core–shell NCs only when they were annealed in the vacuum. A dramatic change in the surface morphology, an island like structure and/or a network like pattern, was observed at the elevated temperature. The as-prepared and annealed samples were analyzed using XRD, scanning electron microscopy and imageJ software for a close inspection of the temperature aroused properties. This work presents the temperature induced size growth mechanism, oxidation kinetics and phase transformation of the NCs accompanied by cluster aggregation, particle coalescence, and diffusion.

The black rock series supported SCR catalyst for NO x removal.

PubMed

Xie, Bin; Luo, Hang; Tang, Qing; Du, Jun; Liu, Zuohua; Tao, Changyuan

2017-09-01

Black rock series (BRS) is of great potential for their plenty of valued oxides which include vanadium, iron, alumina and silica oxides, etc. BRS was used for directly preparing of selective catalytic reduction (SCR) catalyst by modifying its surface texture with SiO 2 -TiO 2 sols and regulating its catalytic active constituents with V 2 O 5 and MoO 3 . Consequently, 90% NO removal ratio was obtained within 300-400 °C over the BRS-based catalyst. The structure and properties of the BRS-based catalyst were characterized by the techniques of N 2 adsorption-desorption, X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), H 2 -temperature programmed reduction (H 2 -TPR), and NH 3 -temperature programmed desorption (NH 3 -TPD). The results revealed that the BRS-based catalyst possesses favorable properties for NO x removal, including highly dispersed active components, abundant surface-adsorbed oxygen O α , well redox property, and numerous Brønsted acid sites. Particularly, the BRS-based catalyst exhibited considerable anti-poisoning performance compared with commercial TiO 2 -based catalyst. The former catalyst shows a NO conversion surpassing 80% from 300 to 400 °C for potassium poisoning, and a durability of SO 2 and H 2 O exceeding 85% at temperatures from 300 to 450 °C.

Role of low-temperature AlGaN interlayers in thick GaN on silicon by metalorganic vapor phase epitaxy

NASA Astrophysics Data System (ADS)

Fritze, S.; Drechsel, P.; Stauss, P.; Rode, P.; Markurt, T.; Schulz, T.; Albrecht, M.; Bläsing, J.; Dadgar, A.; Krost, A.

2012-06-01

Thin AlGaN interlayers have been grown into a thick GaN stack on Si substrates to compensate tensile thermal stress and significantly improve the structural perfection of the GaN. In particular, thicker interlayers reduce the density in a-type dislocations as concluded from x-ray diffraction (XRD) measurements. Beyond an interlayer thickness of 28 nm plastic substrate deformation occurs. For a thick GaN stack, the first two interlayers serve as strain engineering layers to obtain a crack-free GaN structure, while a third strongly reduces the XRD ω-(0002)-FWHM. The vertical strain and quality profile determined by several XRD methods demonstrates the individual impact of each interlayer.

High-temperature X-ray diffraction study of crystallization and phase segregation on spinel-type lithium manganese oxides

NASA Astrophysics Data System (ADS)

Komaba, Shinichi; Yabuuchi, Naoaki; Ikemoto, Sachi

2010-01-01

To study crystallization process of spinel-type Li 1+xMn 2-xO 4, in-situ high-temperature X-ray diffraction technique (HT-XRD) was utilized for the mixture consisting of Li 2CO 3 and Mn 2O 3 as starting material in the temperature range of 25-700 °C. In-situ HT-XRD analysis directly revealed that crystallization process of Li 1+xMn 2-xO 4 was significantly affected by the difference in the Li/Mn molar ratio in the precursor. Single phase of stoichiometric LiMn 2O 4 formed at 700 °C. The formation of single phase of spinel was achieved at the lower temperature than the stoichiometric sample as Li/Mn molar ratio in the precursor increased. Lattice parameter of the stoichiometric LiMn 2O 4 at 25 °C was 8.24 Å and expanded to 8.31 Å at 700 °C, which corresponds to the approximately 3% expansion in the unit cell volume. From the slope of the lattice parameter change as a function of temperatures, linear thermal expansion coefficient of the stoichiometric LiMn 2O 4 was calculated to be 1.2×10 -5 °C -1 in this temperature range. When the Li/Mn molar ratio in Li 1+xMn 2-xO 4 increased ( x > 0.1), the spinel phase segregated into the Li 1+yMn 2-yO 4 ( x > y) and Li 2MnO 3 during heating, which involved the oxygen loss from the materials. During the cooling process from 700 °C, and the segregated phase merged into Li 1+xMn 2-xO 4 with oxygen incorporation. Such trend directly observed by in-situ HT-XRD was supported by thermal gravimetric analysis as reversible weight (oxygen) loss/gain at higher temperature (500-700 °C).

Mössbauer study of iron-based perovskite-type materials as potential catalysts for ethyl acetate oxidation

NASA Astrophysics Data System (ADS)

Paneva, D.; Dimitrov, M.; Velinov, N.; Kolev, H.; Kozhukharov, V.; Tsoncheva, T.; Mitov, I.

2010-03-01

La-Sr-Fe perovskite-type oxides were prepared by the nitrate-citrate method. The basic object of this study is layered Ruddlesden-Popper phase LaSr3Fe3O10. The phase composition and structural properties of the obtained materials are investigated by Mössbauer spectroscopy, X-ray diffraction (XRD), X-ray Photoelectron Spectroscopy (XPS) and temperature programmed reduction (TPR). The preliminary catalytic tests show a high potential of these materials for volatile organic compounds (VOCs) elimination as they possess high conversion ability and selectivity to total oxidation of ethyl acetate. Catalytic performance of LaSr3Fe3O10 is depended on the stability of structure and Fe4+-oxidation state.

Miscibility of amorphous ZrO2-Al2O3 binary alloy

NASA Astrophysics Data System (ADS)

Zhao, C.; Richard, O.; Bender, H.; Caymax, M.; De Gendt, S.; Heyns, M.; Young, E.; Roebben, G.; Van Der Biest, O.; Haukka, S.

2002-04-01

Miscibility is a key factor for maintaining the homogeneity of the amorphous structure in a ZrO2-Al2O3 binary alloy high-k dielectric layer. In the present work, a ZrO2/Al2O3 laminate thin layer has been prepared by atomic layer chemical vapor deposition on a Si (100) wafer. This layer, with artificially induced inhomogeneity (lamination), enables one to study the change in homogeneity of the amorphous phase in the ZrO2/Al2O3 system during annealing. High temperature grazing incidence x-ray diffraction (HT-XRD) was used to investigate the change in intensity of the constructive interference peak of the x-ray beams which are reflected from the interfaces of ZrO2/Al2O3 laminae. The HT-XRD spectra show that the intensity of the peak decreases with an increase in the anneal temperature, and at 800 °C, the peak disappears. The same samples were annealed by a rapid thermal process (RTP) at temperatures between 700 and 1000 °C for 60 s. Room temperature XRD of the RTP annealed samples shows a similar decrease in peak intensity. Transmission electronic microscope images confirm that the laminate structure is destroyed by RTP anneals and, just below the crystallization onset temperature, a homogeneous amorphous ZrAlxOy phase forms. The results demonstrate that the two artificially separated phases, ZrO2 and Al2O3 laminae, tend to mix into a homogeneous amorphous phase before crystallization. This observation indicates that the thermal stability of ZrO2-Al2O3 amorphous phase is suitable for high-k applications.

Thermal behavior of polyhalite: a high-temperature synchrotron XRD study

DOE PAGES

Xu, Hongwu; Guo, Xiaofeng; Bai, Jianming

2016-09-17

As an accessory mineral in marine evaporites, polyhalite, K 2MgCa 2(SO 4) 4·2H 2O, coexists with halite (NaCl) in salt formations, which have been considered as potential repositories for permanent storage of high-level nuclear wastes. However, because of the heat generated by radioactive decays in the wastes, polyhalite may dehydrate, and the released water will dissolve its neighboring salt, potentially affecting the repository integrity. Thus, studying the thermal behavior of polyhalite is important. In this paper, a polyhalite sample containing a small amount of halite was collected from the Salado formation at the WIPP site in Carlsbad, New Mexico. Tomore » determine its thermal behavior, in situ high-temperature synchrotron X-ray diffraction was conducted from room temperature to 1066 K with the sample powders sealed in a silica-glass capillary. At about 506 K, polyhalite started to decompose into water vapor, anhydrite (CaSO 4) and two langbeinite-type phases, K 2Ca x Mg 2-x (SO 4) 3, with different Ca/Mg ratios. XRD peaks of the minor halite disappeared, presumably due to its dissolution by water vapor. With further increasing temperature, the two langbeinite solid solution phases displayed complex variations in crystallinity, composition and their molar ratio and then were combined into the single-phase triple salt, K 2CaMg(SO 4) 3, at ~919 K. Rietveld analyses of the XRD data allowed determination of structural parameters of polyhalite and its decomposed anhydrite and langbeinite phases as a function of temperature. Finally, from the results, the thermal expansion coefficients of these phases have been derived, and the structural mechanisms of their thermal behavior been discussed.« less

Remote X-Ray Diffraction and X-Ray Fluorescence Analysis on Planetary Surfaces

NASA Technical Reports Server (NTRS)

Blake, David F.; DeVincenzi, D. (Technical Monitor)

1999-01-01

The legacy of planetary X-ray Diffraction (XRD) and X-ray Fluorescence (XRF) began in 1960 when W. Parish proposed an XRD instrument for deployment on the moon. The instrument was built and flight qualified, but the Lunar XRD program was cancelled shortly before the first human landing in 1969. XRF chemical data have been collected in situ by surface landers on Mars (Viking 1 & 2, Pathfinder) and Venus (Venera 13 & 14). These highly successful experiments provide critical constraints on our current understanding of surface processes and planetary evolution. However, the mineralogy, which is more critical to planetary surface science than simple chemical analysis, will remain unknown or will at best be imprecisely constrained until X-ray diffraction (XRD) data are collected. Recent progress in X-ray detector technology allows the consideration of simultaneous XRD (mineralogic analysis) and high-precision XRF (elemental analysis) in systems miniaturized to the point where they can be mounted on fixed landers or small robotic rovers. There is a variety of potential targets for XRD/XRF equipped landers within the solar system, the most compelling of which are the poles of the moon, the southern highlands of Mars and Europa.

Novel ultra-low temperature co-fired microwave dielectric ceramic at 400 degrees and its chemical compatibility with base metal

PubMed Central

Di, Zhou; Li-Xia, Pang; Ze-Ming, Qi; Biao-Bing, Jin; Xi, Yao

2014-01-01

A novel NaAgMoO4 material with spinel-like structure was synthesized by using the solid state reaction method and the ceramic sample was well densified at an extreme low sintering temperature about 400°C. Rietveld refinement of the crystal structure was performed using FULLPROF program and the cell parameters are a = b = c = 9.22039 Å with a space group F D −3 M (227). High performance microwave dielectric properties, with a permittivity ~7.9, a Qf value ~33,000 GHz and a temperature coefficient of resonant frequency ~−120 ppm/°C, were obtained. From X-ray diffraction (XRD) and Energy Dispersive Spectrometer (EDS) analysis of the co-fired sample, it was found that the NaAgMoO4 ceramic is chemically compatible with both silver and aluminum at the sintering temperature and this makes it a promising candidate for the ultra-low temperature co-fired ceramics technology. Analysis of infrared and THz spectra indicated that dielectric polarizability at microwave region of the NaAgMoO4 ceramic was equally contributed by ionic displasive and electronic polarizations. Its small microwave dielectric permittivity can also be explained well by the Shannon's additive rule. PMID:25099530

La-Sr-Ni-Co-O based perovskite-type solid solutions as catalyst precursors in the CO 2 reforming of methane

NASA Astrophysics Data System (ADS)

Valderrama, Gustavo; Kiennemann, Alain; Goldwasser, Mireya R.

La 1- xSr xNi 0.4Co 0.6O 3 and La 0.8Sr 0.2Ni 1- yCo yO 3 solid solutions with perovskite-type structure were synthesized by the sol-gel resin method and used as catalytic precursors in the dry reforming of methane with CO 2 to syngas, between 873 and 1073 K at atmospheric pressure under continuous flow of reactant gases with CH 4/CO 2 = 1 ratio. These quaternary oxides were characterized by X-ray diffraction (XRD), BET specific surface area and temperature-programmed reduction (TPR) techniques. XRD analyses of the more intense diffraction peaks and cell parameter measurements showed formation of La-Sr-Ni-Co-O solid solutions with La 0.9Sr 0.1CoO 3 and/or La 0.9Sr 0.1NiO 3 as the main crystallographic phases present on the solids depending on the degree of substitution. TPR analyses showed that Sr doping decreases the temperature of reduction via formation of intermediary species producing Ni 0, Co 0 with particle sizes in the range of nanometers over the SrO and La 2O 3 phases. These metallic nano particles highly dispersed in the solid matrix are responsible for the high activity shown during the reaction and avoid carbon formation. The presence of Sr in doping quantities also promotes the secondary reactions of carbon formation and water-gas shift in a very small extension during the dry reforming reaction.

The optimization functions of ICP discharge in preparation of Cu-Zn-Sn precursors and CZTS films by co-evaporation

NASA Astrophysics Data System (ADS)

Ye, Li; Junfang, Chen; Junhui, Ma; Lifen, Zhou

2016-02-01

Cu-Zn-Sn (CZT) precursors were successfully prepared on glass substrate with the introduction of the assistant technology ICP (inductively coupled plasma) based on the conventional co-evaporation process. The deposition was performed with the substrate temperature at 220 °C and the chamber pressure at 6.5 × 10-2 Pa. Argon plasma was investigated with a Langmuir probe. The plasma density and the electron temperature increased with the increasing of the discharge power. The impact of ICP discharge power on the structural and morphological properties of the CZT film were investigated with energy dispersive X-ray spectrometers (EDS), X-ray diffraction (XRD), and scanning electron microscopy (SEM). XRD and EDS were combined to investigate the structure of the film. The results show that Zn loss exists during the evaporation and the loss can be reduced by increasing the ICP discharge power. From the observation on the scanning electron microscope, the grain size becomes larger with argon plasma's assistance. The preparation of the Cu2ZnSnS4 (CZTS) film and the measured properties demonstrate that the ICP would optimize the growth of the film. Project supported by the Natural Science Foundation of Guangdong Province, China (No. S2013010012548), the Natural Science Foundation of Guangdong Province, China (No. 10151063101000048), the Key Program of the National Natural Science Foundation of China (No. 61072028), the Guangdong Provincial Natural Science Foundation of China (No. 2014A030313441), and the Guangdong Province and Chinese Ministry of Education Cooperation Project of Industry, Education and Academy (No. 2013B090600063).

Substrate temperature effects on the structure and properties of ZnMnO films prepared by pulsed laser deposition

NASA Astrophysics Data System (ADS)

Riascos, H.; Duque, J. S.; Orozco, S.

2017-01-01

ZnMnO thin films were grown on silicon substrates by pulsed laser deposition (PLD). Pulsed Nd:YAG laser was operated at a wavelength of 1064 nm and 100 mJ. ZnMnO thin films were deposited at the vacuum pressure of 10-5 Torr and with substrate temperature from room temperature to 600 °C. The effects of substrate temperature on the structural and Optical properties of ZnMnO thin films have been investigated by X-ray diffraction (XRD), Raman spectroscopy and Uv-vis spectroscopy. From XRD data of the samples, it can be showed that temperature substrate does not change the orientation of ZnMnO thin films. All the films prepared have a hexagonal wurtzite structure, with a dominant (002) peak around 2θ=34.44° and grow mainly along the c-axis orientation. The substrate temperature improved the crystallinity of the deposited films. Uv-vis analysis showed that, the thin films exhibit high transmittance and low absorbance in the visible region. It was found that the energy band to 300 ° C is 3.2 eV, whereas for other temperatures the values were lower. Raman reveals the crystal quality of ZnMnO thin films.

Alternative approaches used to assess structural changes of natural zircon caused by heat treatment

NASA Astrophysics Data System (ADS)

Huong, L. T. T.; Thuyet, N. T. M.; Phan, T. L.; Tran, N.; Toan, D. N.; Thang, P. D.; Huy, B. T.

2018-03-01

It is known that large changes in the crystal structure of zircon (ZrSiO4) can be assessed through the linewidth of the characteristic Raman mode (Δν3) at 1008 cm-1. However, the use of Δν3 to assess small changes caused by heat treatment at temperatures below its decomposition temperature of 1670 °C is difficult. The present work points out that the combination of X-ray diffraction (XRD) analyses, and photoluminescence (PL) and Raman (RS) measurements with different excitation wavelengths is an effective approach to solve the above problem. In this context, we have selected natural zircon containing some rare-earth (RE) impurities, and then studied the changes in its crystal structure caused by heat treatment at temperatures Tan=400-1600 °C. XRD analyses reveal that small modifications of the unit-cell parameters occur as Tan>600 °C. Taking the intensity ratios of the ν3 mode to RE-related emissions (Iν3/IRE) or the PL intensity ratios between RE-related emissions into consideration, the similar results in good agreement with the XRD analyses are also found. We believe that the small structural changes are related to the migration and redistribution of defects and impurities, and re-crystallization of zircon. This could be further confirmed though the relation between paramagnetic and ferromagnetic signals when Tan changes.

Quantitative analysis of tridymite and cristobalite crystallized in rice husk ash by heating.

PubMed

Shinohara, Yasushi; Kohyama, Norihiko

2004-04-01

The quantities of two forms of crystalline silica, tridymite and cristobalite, in heated rice husk ash (RHA) samples were determined by X-ray diffraction (XRD) and chemical methods. Two RHA samples, containing 93% SiO2 and 2-3% K2O, were prepared from charcoaled rice husk products and heated to above 900 degrees C. The crystalline silica made up over 60-80% of the total silica in the heated RHA samples based on the XRD analysis. The crystalline phases in the two samples were somewhat different: The sample heated in the temperature range of 900 to 1,200 degrees C contained 52-62% cristobalite and 10-17% tridymite, but the other sample heated at a comparable temperature, above 1,100 degrees C, contained 46-66% tridymite and 37-16% cristobalite. Based on a correlation of lower tridymite crystallization temperature with higher potassium content, it was concluded that higher potassium levels were responsible for this difference. The pyrophosphoric acid analysis did not give exact results in the evaluation of total crystalline silica content in these RHA samples. As the combustion of rice husk was considered to cover the demands for energy and silica resource in Asian countries, cristobalite and tridymite crystallized in RHA by burning of rice husk should be assessed precisely by XRD analysis and the airborne dust in relevant workplace be controlled.

Unusual effect of water vapor pressure on dehydration of dibasic calcium phosphate dihydrate.

PubMed

Kaushal, Aditya M; Vangala, Venu R; Suryanarayanan, Raj

2011-04-01

Dibasic calcium phosphate occurs as an anhydrate (DCPA; CaHPO₄) and as a dihydrate (DCPD; CaHPO₄•2H₂O). Our objective was to investigate the unusual behavior of these phases. Dibasic calcium phosphate dihydrate was dehydrated in a (i) differential scanning calorimeter (DSC) in different pan configurations; (ii) variable-temperature X-ray diffractometer (XRD) at atmospheric and under reduced pressure, and in sealed capillaries; and (iii) water vapor sorption analyzer at varying temperature and humidity conditions. Dehydration was complete by 210°C in an open DSC pan and under atmospheric pressure in the XRD. Unlike "conventional" hydrates, the dehydration of DCPD was facilitated in the presence of water vapor. Variable-temperature XRD in a sealed capillary and DSC in a hermetic pan with pinhole caused complete dehydration by 100°C and 140°C, respectively. Under reduced pressure, conversion to the anhydrate was incomplete even at 300°C. The increase in dehydration rate with increase in water vapor pressure has been explained by the Smith-Topley effect. Under "dry" conditions, a coating of poorly crystalline product is believed to form on the surface of particles and act as a barrier to further dehydration. However, in the presence of water vapor, recrystallization occurs, creating cracks and channels and facilitating continued dehydration. Copyright © 2010 Wiley-Liss, Inc.

Formation of Al15Mn3Si2 Phase During Solidification of a Novel Al-12%Si-4%Cu-1.2%Mn Heat-Resistant Alloy and Its Thermal Stability

NASA Astrophysics Data System (ADS)

Suo, Xiaojing; Liao, Hengcheng; Hu, Yiyun; Dixit, Uday S.; Petrov, Pavel

2018-02-01

The formation of Al15Mn3Si2 phase in Al-12Si-4Cu-1.2Mn (wt.%) alloy during solidification was investigated by adopting CALPHAD method and microstructural observation by optical microscopy, SEM-EDS, TEM-EDS/SAD and XRD analysis; SEM fixed-point observation method was applied to evaluate its thermal stability. As-cast microstructural observation consistently demonstrates the solidification sequence of the studied alloy predicted by phase diagram calculation. Based on the phase diagram calculation, SEM-EDS, TEM-EDS/SAD and XRD analysis, as well as evidences on Al-Si-Mn-Fe compounds from the literature, the primary and eutectic Mn-rich phases with different morphologies in the studied alloy are identified to be Al15Mn3Si2 that has a body-centered cubic (BCC) structure with a lattice constant of a = 1.352 nm. SEM fixed-point observation and XRD analysis indicate that Al15Mn3Si2 phase has more excellent thermal stability at high temperature than that of CuAl2 phase and can serve as the major strengthening phase in heat-resistant aluminum alloy that has to face a high-temperature working environment. Results of tension test show that addition of Mn can improve the strength of Al-Si-Cu alloy, especially at elevated temperature.

Facile synthesis of hollow Co3O4 microspheres and its use as a rapid responsive CL sensor of combustible gases.

PubMed

Teng, Fei; Yao, Wenqing; Zheng, Youfei; Ma, Yutao; Xu, Tongguang; Gao, Guizhi; Liang, Shuhui; Teng, Yang; Zhu, Yongfa

2008-09-15

The hollow Co(3)O(4) microspheres (HCMs) were prepared by the carbonaceous templates, which did not need the surface pretreatment. The chemiluminescence (CL) and catalytic properties for CO oxidation over these hollow samples were evaluated. The samples were characterized by scanning electron microscopy (SEM), energy disperse spectra (EDS), transmission electron microscopy (TEM), selected area electron diffraction (ED), X-ray diffraction (XRD), temperature-programmed desorption (TPD) and N(2) adsorption. The influences of filter' band length, flow rate of gas, test temperature, and particle structure on CL intensities were mainly investigated. It was found that compared with the solid Co(3)O(4) particles (SCPs), HCMs had a stronger CL intensity, which was ascribed to its hollow structure; and that CL properties of the catalysts were well correlated with their reaction activities. Moreover, HCMs were used to fabricate a highly sensitive gas detector, which is a rapid and effective method for the selection of catalysts or the detection of environmental deleterious gases.

Effect of content silver and heat treatment temperature on morphological, optical, and electrical properties of ITO films by sol-gel technique

NASA Astrophysics Data System (ADS)

Mirzaee, Majid; Dolati, Abolghasem

2014-09-01

Silver-doped indium tin oxide thin films were synthesized using sol-gel dip-coating technique. The influence of different silver-dopant contents and annealing temperature on the electrical, optical, structural, and morphological properties of the films were characterized by means of four-point probe, UV-Vis spectroscopy, X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and X-ray photoelectron spectroscope (XPS). XRD analysis confirmed the formation of cubic bixbyte structure of In2O3 with silver nanoparticles annealed at 350 °C. XPS analysis showed that divalent tin transformed to tetravalent tin through oxidization, and silver nanoparticles embedded into ITO matrix covered with silver oxide shell, resulting in high quality nanocomposite thin films. The embedment of polyvinylpyrrolidone inhibited the growth of silver nanoparticles and ITO annealed at 350 °C. Delafossite structure of tin-doped AgInO2 was found at higher annealing temperatures. XRD analysis and FESEM micrographs showed that the optimum temperature to prevent the formation of AgInO2 is 350 °C. The embedment of silver particles (5-10 nm) from reduction of silver ion in ITO thin films improved the electrical conductivity and optical transmittance of ITO nanolayers. The lowest stable sheet resistance of 1,952 Ω/Sq for a 321 nm thick and an average optical transmittance of 91.8 % in the visible region with a band gap of 3.43 eV were achieved for silver-doping content of 0.04 M.

Methanol incorporation in clathrate hydrates and the implications for oil and gas pipeline flow assurance and icy planetary bodies

PubMed Central

Shin, Kyuchul; Udachin, Konstantin A.; Moudrakovski, Igor L.; Leek, Donald M.; Alavi, Saman; Ratcliffe, Christopher I.; Ripmeester, John A.

2013-01-01

One of the best-known uses of methanol is as antifreeze. Methanol is used in large quantities in industrial applications to prevent methane clathrate hydrate blockages from forming in oil and gas pipelines. Methanol is also assigned a major role as antifreeze in giving icy planetary bodies (e.g., Titan) a liquid subsurface ocean and/or an atmosphere containing significant quantities of methane. In this work, we reveal a previously unverified role for methanol as a guest in clathrate hydrate cages. X-ray diffraction (XRD) and NMR experiments showed that at temperatures near 273 K, methanol is incorporated in the hydrate lattice along with other guest molecules. The amount of included methanol depends on the preparative method used. For instance, single-crystal XRD shows that at low temperatures, the methanol molecules are hydrogen-bonded in 4.4% of the small cages of tetrahydrofuran cubic structure II hydrate. At higher temperatures, NMR spectroscopy reveals a number of methanol species incorporated in hydrocarbon hydrate lattices. At temperatures characteristic of icy planetary bodies, vapor deposits of methanol, water, and methane or xenon show that the presence of methanol accelerates hydrate formation on annealing and that there is unusually complex phase behavior as revealed by powder XRD and NMR spectroscopy. The presence of cubic structure I hydrate was confirmed and a unique hydrate phase was postulated to account for the data. Molecular dynamics calculations confirmed the possibility of methanol incorporation into the hydrate lattice and show that methanol can favorably replace a number of methane guests. PMID:23661058

Methanol incorporation in clathrate hydrates and the implications for oil and gas pipeline flow assurance and icy planetary bodies.

PubMed

Shin, Kyuchul; Udachin, Konstantin A; Moudrakovski, Igor L; Leek, Donald M; Alavi, Saman; Ratcliffe, Christopher I; Ripmeester, John A

2013-05-21

One of the best-known uses of methanol is as antifreeze. Methanol is used in large quantities in industrial applications to prevent methane clathrate hydrate blockages from forming in oil and gas pipelines. Methanol is also assigned a major role as antifreeze in giving icy planetary bodies (e.g., Titan) a liquid subsurface ocean and/or an atmosphere containing significant quantities of methane. In this work, we reveal a previously unverified role for methanol as a guest in clathrate hydrate cages. X-ray diffraction (XRD) and NMR experiments showed that at temperatures near 273 K, methanol is incorporated in the hydrate lattice along with other guest molecules. The amount of included methanol depends on the preparative method used. For instance, single-crystal XRD shows that at low temperatures, the methanol molecules are hydrogen-bonded in 4.4% of the small cages of tetrahydrofuran cubic structure II hydrate. At higher temperatures, NMR spectroscopy reveals a number of methanol species incorporated in hydrocarbon hydrate lattices. At temperatures characteristic of icy planetary bodies, vapor deposits of methanol, water, and methane or xenon show that the presence of methanol accelerates hydrate formation on annealing and that there is unusually complex phase behavior as revealed by powder XRD and NMR spectroscopy. The presence of cubic structure I hydrate was confirmed and a unique hydrate phase was postulated to account for the data. Molecular dynamics calculations confirmed the possibility of methanol incorporation into the hydrate lattice and show that methanol can favorably replace a number of methane guests.

Fabrication and Characterization of CZTS Thin Films Prepared by the Sulfurization of RF-Sputtered Stacked Metal Precursors

NASA Astrophysics Data System (ADS)

Abusnina, Mohamed; Moutinho, Helio; Al-Jassim, Mowafak; DeHart, Clay; Matin, Mohammed

2014-09-01

In this work, Cu2ZnSnS4 (CZTS) thin films were prepared by the sulfurization of metal precursors deposited sequentially via radio frequency magnetron sputtering on Mo-coated soda-lime glass. The stack order of the precursors was Mo/Zn/Sn/Cu. Sputtered precursors were annealed in sulfur atmosphere with nine different conditions to study the impact of sulfurization time and substrate temperature on the structural, morphological, and optical properties of the final CZTS films. X-ray fluorescence was used to determine the elemental composition ratio of the metal precursors. Final CZTS films were characterized by x-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive spectroscopy (EDS). XRD and EDS were combined to investigate the films' structure and to identify the presence of secondary phases. XRD analysis indicated an improvement in film crystallinity with an increase of the substrate temperature and annealing times. Also indicated was the minimization and/or elimination of secondary phases when the films experienced longer annealing time. EDS revealed slight Sn loss in films sulfurized at 550°C; however, an increase of the sulfurization temperature to 600°C did not confirm these results. SEM study showed that films treated with higher temperatures exhibited dense morphology, indicating the completion of the sulfurization process. The estimated absorption coefficient was on the order of 104 cm-1 for all CZTS films, and the values obtained for the optical bandgap energy of the films were between 1.33 eV and 1.52 eV.

Efficient graphite ring heater suitable for diamond-anvil cells to 1300 K

DOE Office of Scientific and Technical Information (OSTI.GOV)

Du Zhixue; Amulele, George; Lee, Kanani K. M.

In order to generate homogeneous high temperatures at high pressures, a ring-shaped graphite heater has been developed to resistively heat diamond-anvil cell (DAC) samples up to 1300 K. By putting the heater in direct contact with the diamond anvils, this graphite heater design features the following advantages: (1) efficient heating: sample can be heated to 1300 K while the DAC body temperature remains less than 800 K, eliminating the requirement of a special alloy for the DAC; (2) compact design: the sample can be analyzed with in situ measurements, e.g., x-ray, optical, and electrical probes are possible. In particular, themore » side access of the heater allows for radial x-ray diffraction (XRD) measurements in addition to traditional axial XRD.« less

Synthesis and structural properties of Ba(1-x)LaxTiO3 perovskite nanoparticles fabricated by solvothermal synthesis route

NASA Astrophysics Data System (ADS)

Puli, Venkata Sreenivas; Adireddy, Shiva; Elupula, Ravinder; Molugu, Sudheer; Shipman, Josh; Chrisey, Douglas B.

2017-05-01

We report the successful synthesis and structural characterization of barium lanthanum titanate Ba(1-x)LaxTiO3 (x=0.003,0.006,0.010) nanoparticles. The colloidal nanoparticles were prepared with high yield by a solvothermal method at temperatures as low as 150°C for 24h. The as-prepared nanopowders were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), and Raman spectroscopy. The XRD studies revealed pseudo-cubic crystalline structure, with no impurity phases at room temperature. However ferroelectric tetragonal modes were clearly observed using Raman spectroscopy measurements. From TEM measurements, uniformly sized BLT nanoparticles were observed. Selected area diffraction TEM images revealed polycrystalline perovskite ring patterns, identified as corresponding to the tetragonal phase.

Synthesis and properties of selenium trihydride at high pressures

NASA Astrophysics Data System (ADS)

Zhang, Xiao; Xu, Wan; Wang, Yu; Jiang, Shuqing; Gorelli, Federico A.; Greenberg, Eran; Prakapenka, Vitali B.; Goncharov, Alexander F.

2018-02-01

The chemical reaction products of molecular hydrogen (H2) with selenium (Se) are studied by synchrotron x-ray diffraction (XRD) and Raman spectroscopy at high pressures. We find that a common H2Se is synthesized at 0.3 GPa using laser heating. Upon compression at 300 K, a crystal of the theoretically predicted Cccm H3Se has been grown at 4.6 GPa. At room temperature, H3Se shows a reversible phase decomposition after laser irradiation above 8.6 GPa, but remains stable up to 21 GPa. However, at 170 K Cccm H3Se persists up to 39.5 GPa based on XRD measurements, while low-temperature Raman spectra weaken and broaden above 23.1 GPa. At these conditions, the sample is visually nontransparent and shiny suggesting that metallization occurred.

Effects of the synthesis temperature on the crystalline structure and the magnetic properties of cobalt ferrite nanoparticles prepared via coprecipitation

NASA Astrophysics Data System (ADS)

Hutamaningtyas, Evangelin; Utari; Suharyana; Purnama, Budi; Wijayanta, Agung Tri

2016-08-01

The effects of the synthesis temperature on the crystalline structure and the magnetic properties of cobalt ferrite (CoFe2O4) nanoparticles prepared via coprecipitation are discussed. The synthesis was conducted at temperatures of 75 °C, 85 °C and 95 °C. Fourier transform infrared spectroscopy characterization related to a stretching vibration at a wavenumber of 590 cm-1 indicated the formation of a CoFe2O4 metal oxide. In addition, powder X ray diffraction (XRD) characterization proved that the metal oxide was CoFe2O4. Crystallite sizes calculated using the Scherer formula at the strongest peak of the XRD spectra of the samples synthesized at 75 °C, 85 °C and 95 °C were 32 nm, 43 nm and 50.4 nm, respectively. Finally, the results of the vibrating sample magnetometer characterization showed that the saturation magnetization decreased with increasing synthesis temperature, which is related to the dominant preference of Co2+ over Fe3+ cations at the octahedral sites.

Influence of Discharge Current on Phase Transition Properties of High Quality Polycrystalline VO2 Thin Film Fabricated by HiPIMS

PubMed Central

Lin, Tiegui; Wang, Jian; Liu, Gang; Wang, Langping; Wang, Xiaofeng; Zhang, Yufen

2017-01-01

To fabricate high-quality polycrystalline VO2 thin film with a metal–insulator transition (MIT) temperature less than 50 °C, high-power impulse magnetron sputtering with different discharge currents was employed in this study. The as-deposited VO2 films were characterized by a four-point probe resistivity measurement system, visible-near infrared (IR) transmittance spectra, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy. The resistivity results revealed that all the as-deposited films had a high resistance change in the phase transition process, and the MIT temperature decreased with the increased discharge current, where little deterioration in the phase transition properties, such as the resistance and transmittance changes, could be found. Additionally, XRD patterns at various temperatures exhibited that some reverse deformations that existed in the MIT process of the VO2 film, with a large amount of preferred crystalline orientations. The decrease of the MIT temperature with little deterioration on phase transition properties could be attributed to the reduction of the preferred grain orientations. PMID:28772990

Structural versus electrical properties of an organic-inorganic hybrid material based on sulfate

NASA Astrophysics Data System (ADS)

Ben Rached, Asma; Guionneau, Philippe; Lebraud, Eric; Mhiri, Tahar; Elaoud, Zakaria

2017-01-01

A new organo-sulfate compound is obtained by slow evaporation at room temperature and is characterized by powder and single-crystal X-ray diffraction (XRD) at variable temperatures. The benzylammonium monohydrogenosulfate of formula C6H5CH2NH3+. HSO4-, denoted (BAS), crystallizes in the monoclinic system P21/c space group with the following parameters at room temperature: a=5.623(5)Å, b=20.239(5) Å, c=8.188(5)Å, β=94.104(5)°. The crystal structure consists of infinite parallel two-dimensional planes built by HSO4- anions and C6H5CH2NH3+ cations interconnected by strong O-H….. O and N-H….. O hydrogen bonds. A phase transition is detected at 350 K by differential scanning calorimetry (DSC) and confirmed by powder XRD. Conductivity measurements using the impedance spectroscopy technique allow to determine the conductivity relaxation parameters associated with the H+ conduction from an analysis of the M"/M"max spectrum measured in a wide temperature range. Transport properties of this material appear to be due to an H+ ion hopping mechanism.

Hydrolysis of bamboo biomass by subcritical water treatment.

PubMed

Mohan, Mood; Banerjee, Tamal; Goud, Vaibhav V

2015-09-01

The aim of present study was to obtain total reducing sugars (TRS) from bamboo under subcritical water (SCW) treatment in a batch reactor at the temperature ranging from 170 °C to 220 °C and 40 min hydrolysis time. Experiments were performed to investigate the effects of temperature and time on TRS yield. The maximum TRS yield (42.21%) was obtained at lower temperature (180 °C), however longer reaction time (25 min). X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and scanning electron microscopy (SEM) analysis were used to characterise treated and untreated bamboo samples. The XRD profile revealed that crystallinity of bamboo increased to 71.90% with increase in temperature up to 210 °C and decreased thereafter to 70.92%. The first-order reaction kinetic model was used to fit the experimental data to obtain rate constants. From the Arrhenius plot, activation energy and pre-exponential factor at 25 min time were found to be 17.97 kJ mol(-1) and 0.154 min(-1), respectively. Copyright © 2015 Elsevier Ltd. All rights reserved.

Structure, Morphology, and Optical Properties of Amorphous and Nanocrystalline Gallium Oxide Thin Films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, S. Sampath; Rubio, E. J.; Noor-A-Alam, M.

Ga2O3 thin films were produced by sputter deposition by varying the substrate temperature (Ts) in a wide range (Ts=25-800 oC). The structural characteristics and optical properties of Ga2O3 films were evaluated using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectrometry (EDS), Rutherford backscattering spectrometry (RBS) and spectrophotometric measurements. The effect of growth temperature is significant on the chemistry, crystal structure and morphology of Ga2O3 films. XRD and SEM analyses indicate that the Ga2O3 films grown at lower temperatures were amorphous while those grown at Ts≥500 oC were nanocrystalline. RBS measurements indicate the well-maintained stoichiometry of Ga2O3 films atmore » Ts=300-700 oC. The spectral transmission of the films increased with increasing temperature. The band gap of the films varied from 4.96 eV to 5.17 eV for a variation in Ts in the range 25-800 oC. A relationship between microstructure and optical property is discussed.« less

Deposition of Nanostructured CdS Thin Films by Thermal Evaporation Method: Effect of Substrate Temperature

PubMed Central

Memarian, Nafiseh; Rozati, Seyeed Mohammad; Concina, Isabella

2017-01-01

Nanocrystalline CdS thin films were grown on glass substrates by a thermal evaporation method in a vacuum of about 2 × 10−5 Torr at substrate temperatures ranging between 25 °C and 250 °C. The physical properties of the layers were analyzed by transmittance spectra, XRD, SEM, and four-point probe measurements, and exhibited strong dependence on substrate temperature. The XRD patterns of the films indicated the presence of single-phase hexagonal CdS with (002) orientation. The structural parameters of CdS thin films (namely crystallite size, number of grains per unit area, dislocation density and the strain of the deposited films) were also calculated. The resistivity of the as-deposited films were found to vary in the range 3.11–2.2 × 104 Ω·cm, depending on the substrate temperature. The low resistivity with reasonable transmittance suggest that this is a reliable way to fine-tune the functional properties of CdS films according to the specific application. PMID:28773133

Pyrolysis of flax straw: Characterization of char, liquid, and gas as fuel

NASA Astrophysics Data System (ADS)

Tushar, Mohammad Shahed Hasan Khan

The demand for energy continues to outstrip its supply and necessitates the development of renewable energy options. Biomass has been recognized as a major renewable energy source to supplement the declining fossil fuel source of energy. It is the most popular form of renewable energy and, currently, biofuel production is becoming more promising. Being carbon neutral, readily available, and low in sulphur content makes biomass a very promising source of renewable energy. In the present research, both the isothermal and non-isothermal pressurized pyrolysis of flax straw is studied for the first time. In case of isothermal pyrolysis, the influence of pyrolysis temperature and reaction time on char yield and morphology was investigated. The applied pyrolysis temperature was varied between 300 and 500°C. The reaction time was varied from 15 to 60 min. The char yield was found to decrease as pyrolysis temperature and reaction time increased. The char structure and surface morphology were thoroughly investigated by means of x-ray diffraction (XRD), temperature-programmed oxidation (TPO), and scanning electron microscopy (SEM). The degree of porosity and graphitization increased as pyrolysis temperature and time increased. In fact, the experiment performed at 500°C for 1h duration did not yield any char; only residual ash could be obtained. The TPO studies on the char samples corroborated the XRD findings and showed the presence of two types of carbon, namely, amorphous filamentous carbon and graphitic carbon. A thermogravimetric analysis (TGA) of the char was performed to gain an understanding of combustion kinetics and reactivity. It implied that the reactivity of the char decreases as temperature increases, and this finding is well supported by the TPO, TGA, SEM, and XRD characterization data. Furthermore, an empirical global model was devised based on the power law to estimate activation energy and other kinetic parameters. For the non-isothermal pressurized pyrolysis of flax straw, the experiments were carried out at different pressures, ranging from 10 to 40 psig. The three types of products thus obtained (gas, liquid, char) were thoroughly quantified and analyzed. The yields of the products were found to be dependent on the experimental conditions. It was observed that 10 psig of pressure gave the maximum yield of bio-oil, while 20 psig pressure lead to maximum char yield. The gaseous products were analyzed using an online GC, while the bio-oils were characterized using an offline GC/MS. SEM studies were performed to study the char morphology and porosity. The main gaseous products observed were CO, H2, CO2, CH 4, and C3. The bio-oils were mainly composed of phenolic compounds, carboxylic acids, and furfural. The pH and density of the bio-oils was found to increase as pyrolysis pressure increased. SEM investigation gave insights into the porosity of chars; as pressure increased, an increase in the porosity of char was noted. XRD studies showed that amorphous hydrocarbon and graphitic carbons are the major constituents of char, which was supported by TPO experiments. A TGA study showed two reaction zones for char oxidation. The kinetic parameters of oxidation were estimated using a power law model, which was also used for isothermal pyrolysis and isothermal char oxidation kinetics. Based on the data generated, the pressure of 10 psig was found to be optimum for bio-oil production, while a pressure of 20 psig was optimum for char production. With the increase in pressure, the production of individual gas components increased within the pressure range studied. Finally, with the increase in reaction pressure, temperature and time, the produced chars became less reactive.

Alteration behavior of mineral structure and hazardous elements during combustion of coal from a power plant at Huainan, Anhui, China.

PubMed

Tang, Quan; Sheng, Wanqi; Li, Liyuan; Zheng, Liugen; Miao, Chunhui; Sun, Ruoyu

2018-08-01

The alteration behavior of minerals and hazardous elements during simulated combustion (100-1200 °C) of a raw coal collected from a power plant were studied. Thermogravimetric analysis indicated that there were mainly four alteration stages during coal combustion. The transformation behavior of mineral phases of raw coal, which were detected by X-ray polycrystalline diffraction (XRD) technique, mainly relied on the combustion temperature. A series of changes were derived from the intensities of mineral (e.g. clays) diffraction peaks when temperature surpassed 600 °C. Mineral phases tended to be simple and collapsed to amorphous glass when temperature reached up to 1200 °C. The characteristics of functional groups for raw coal and high-temperature (1200 °C) ash studied by Fourier transform infrared spectroscopy (FTIR) were in accordance with the result obtained from XRD analysis. The volatilization ratios of Co, Cr, Ni and V increased consistently with the increase of combustion temperature, suggesting these elements were gradually released from the organic matter and inorganic minerals of coal. Copyright © 2018 Elsevier Ltd. All rights reserved.

Annealing effect on thermal conductivity and microhardness of carbon nanotube containing Se80Te16Cu4 glassy composites

NASA Astrophysics Data System (ADS)

Upadhyay, A. N.; Tiwari, R. S.; Singh, Kedar

2018-02-01

This study deals with the effect of thermal annealing on structural/microstructural, thermal and mechanical behavior of pristine Se80Te16Cu4 and carbon nanotubes (CNTs) containing Se80Te16Cu4 glassy composites. Pristine Se80Te16Cu4, 3 and 5 wt%CNTs-Se80Te16Cu4 glassy composites are annealed in the vicinity of glass transition temperature to onset crystallization temperature (340-380 K). X-ray diffraction (XRD) pattern revealed formation of polycrystalline phases of hexagonal CuSe and trigonal selenium. The indexed d-values in XRD patterns are in well conformity with the d-values obtained after the indexing of the ring pattern of selected area electron diffraction pattern of TEM images. The SEM investigation exhibited that the grain size of the CNTs containing Se80Te16Cu4 glassy composites increased with increasing annealing temperature and decreased at further higher annealing temperature. Thermal conductivity, microhardness exhibited a substantial increase with increasing annealing temperature of 340-360 K and slightly decreases for 380 K. The variation of thermal conductivity and microhardness can be explained by cross-linking formation and voids reduction.

Room temperature ferromagnetism of nanocrystalline Nd1.90Ni0.10O3-δ

NASA Astrophysics Data System (ADS)

Sarkar, B. J.; Mandal, J.; Dalal, M.; Bandyopadhyay, A.; Chakrabarti, P. K.

2018-05-01

Nanocrystalline sample of Ni2+ doped neodymium oxide (Nd1.90Ni0.10O3-δ, NNO) is synthesized by co-precipitation method. Analysis of X-ray diffraction (XRD) pattern by Rietveld refinement method confirms the desired phase of NNO and complete substitution of Ni2+ ions in the Nd2O3 lattice. Analyses of transmission electron microscopy (TEM) and Raman spectroscopy of NNO recorded at room temperature (RT) also substantiate this fact. Besides, no traces of impurities are found in the analyses of XRD, TEM and Raman data. Room temperature hysteresis loop of NNO suggests the presence of weak ferromagnetism (FM) in low field region ( 600 mT), but in high field region paramagnetism of the host is more prominent. Magnetization vs. temperature ( M- T) curve in the entire temperature range (300-5 K) is analyzed successfully by a combined equation generated from three-dimensional (3D) spin wave model and Curie-Weiss law, which suggests the presence of mixed paramagnetic phase together with ferromagnetic phase in the doped sample. The onset of magnetic ordering is analyzed by oxygen vacancy mediated F-center exchange (FCE) coupling mechanism.

Structural properties and electrochemistry of α-LiFeO2

NASA Astrophysics Data System (ADS)

Abdel-Ghany, A. E.; Mauger, A.; Groult, H.; Zaghib, K.; Julien, C. M.

2012-01-01

In this work, we study the physico-chemistry and electrochemistry of lithium ferrite synthesized by solid-state reaction. Characterization included X-ray diffraction (XRD), scanning electronic microscopy (SEM), Raman scattering (RS), Fourier transform infrared spectroscopy (FTIR), and SQUID magnetometry. XRD peaks gradually sharpen with increasing firing temperature; all the diffraction peaks can be indexed to the cubic α-LiFeO2 phase (Fm3m space group) with the refined cell parameter a = 4.155 Å. RS and FTIR spectra show the vibrational modes due to covalent Fe-O bonds and the Li-cage mode at low-frequency. The electrochemical properties of Li/LiFeO2 are revisited along with the post-mortem analysis of the positive electrode material using XRD and Raman experiments.

Cascade Reductive Etherification of Bioderived Aldehydes over Zr-Based Catalysts.

PubMed

Shinde, Suhas; Rode, Chandrashekhar

2017-10-23

An efficient one-pot catalytic cascade sequence has been developed for the production of value-added ethers from bioderived aldehydes. Etherification of 5-(hydroxymethyl)furfural with different aliphatic alcohols over acidic Zr-montmorillonite (Zr-Mont) catalyst produced a mixture of 5-(alkoxymethyl)furfural and 2-(dialkoxymethyl)-5-(alkoxymethyl)furan. The latter was selectively converted back into 5-(alkoxymethyl)furfural by treating it with water over the same catalyst. The synthesis of 2,5-bis(alkoxymethyl)furan was achieved through a cascade sequence involving etherification, transfer hydrogenation, and re-etherification over a combination of acidic Zr-Mont and the charge-transfer hydrogenation catalyst [ZrO(OH) 2 ]. This catalyst combination was further explored for the cascade conversion of 2-furfuraldehyde into 2-(alkoxymethyl)furan. The scope of this strategy was then extended for the reductive etherification of lignin-derived arylaldehydes to obtain the respective benzyl ethers in >80 % yield. Additionally, the mixture of Zr-Mont and ZrO(OH) 2 does not undergo mutual destruction, which was proved by recycling experiments and XRD analysis. Both the catalysts were thoroughly characterized using BET, temperature-programmed desorption of NH 3 and CO 2 , pyridine-FTIR, XRD, inductively coupled plasma optical emission spectroscopy, and X-ray photoelectron spectroscopy techniques. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Carbon film deposition on SnO{sub 2}/Si(111) using DC unbalanced magnetron sputtering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aji, A. S.; Darma, Y.

In this paper, carbon deposition on SnO{sub 2} layer using DC unbalanced magnetron-sputtering technique at low temperature has been systematically studied. Sputtering process were carried out at pressure of 4.6×10{sup −2} Torr by keeping the substrate temperature at 300 °C. SnO{sub 2} were growth on silicon (111) substrate using thermal evaporation and continuing with dry oxidation of Sn at 225 °C. Thermal evaporation for high purity Sn was conducted by maintain the current source as high as 40 ampere. The quality of SnO{sub 2} on Si(111) and the characteristic of carbon thin film on SnO{sub 2} were analized by meanmore » XRD, FTIR and Raman spectra. XRD analysis shows that SnO{sub 2} film is growth uniformly on Si(111). FTIR and Raman spectra confirm the formation of thin film carbon on SnO{sub 2}. Additionally, thermal annealing for some sample series have been performed to study their structural stability. The change of atomic structure due to thermal annealing were analized by Raman and XRD spectra.« less

Graphene/semicrystalline-carbon derived from amylose films for supercapacitor application

NASA Astrophysics Data System (ADS)

Deraman, M.; Sazali, N. E. S.; Hanappi, M. F. Y. M.; Tajuddin, N. S. M.; Hamdan, E.; Suleman, M.; Othman, M. A. R.; Omar, R.; Hashim, M. A.; Basri, N. H.; Nor, N. S. M.; Dolah, B. N. M.; Noor, A. M.; Jasni, M. R. M.

2016-08-01

Graphene/semicrystalline-carbon in the form of carbon flakes is produced by carbonization up to 600, 700, 800, 900 and 1000°C, respectively, of the amylose films prepared by a casting method on copper foil substrate. The carbon flakes are characterized by X-ray diffraction (XRD) method to determine their microcrystallite interlayer spacing, width and stack-height; and Raman spectroscopy (RS) method to obtain structural information from the D-, D2- and G-bands peak-intensities. The XRD results show that increase in carbonization temperature lead to ~(1-3%), ~85% and ~30%increase in the microcrystallites interlayer spacing, width and stack-height, respectively, indicating that a larger growth of microcrytallite of carbon flakes occurs in the direction parallel to (001) plane or film planar surface. The specific surface area of carbon flakes estimated from the XRD results in decreases from ~4400 to ~3400 m2/g, corresponding to the specific capacitance between ~500 to ~400 F/g, which are well within the range of specific capacitance for typical electrodes carbon for supercapacitor application. The RS results show that the multilayer graphene co-exist with semicrystalline- carbon within the carbon flakes, with the multilayer graphene relative quantities increase with increasing carbonization temperature.

Structural, magnetic and electronic structural properties of Mn doped CeO2 nanoparticles

NASA Astrophysics Data System (ADS)

Kumari, Kavita; Vij, Ankush; Hashim, Mohd.; Chae, K. H.; Kumar, Shalendra

2018-05-01

Nanoparticles of Ce1-xMnxO2, (x=0.0, 0.01, and 0.05) have been synthesized by using co-precipitation method, and then characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), near edge x-ray absorption fine structure (NEXAFS) spectroscopy and dc magnetization measurements. XRD results clearly showed that the all the samples have single phase nature and exclude the presence of any secondary phase. The average particle size calculated using XRD TEM measurements found to decrease with increase in Mn doping in the range of 4.0 - 9.0 nm. The structural parameters such as strain, interplaner distance and lattice parameter is observed to decrease with increase in doping. The morphology of Ce1-xMnxO2 nanoparticles measured using TEM micrographs indicate that nanoparticle have spherical shape morphology. Magnetic hysteresis curve for Ce1-xMnxO2, (x = 0.0, 0.01, and 0.05) confirms the ferromagnetic ordering room temperature. The value of saturation magnetization is observed to decrease with increase in temperature from 10 K to 300 K. The NEXAFS spectra measured at Ce M4,5 edge reveals that Ce-ions are in +4 valance state.

Remarkable support effect on the reactivity of Pt/In2O3/MOx catalysts for methanol steam reforming

NASA Astrophysics Data System (ADS)

Liu, Xin; Men, Yong; Wang, Jinguo; He, Rong; Wang, Yuanqiang

2017-10-01

Effects of supports over Pt/In2O3/MOx catalysts with extremely low loading of Pt (1 wt%) and In2O3 loadings (3 wt%) are investigated for the hydrogen production of methanol steam reforming (MSR) in the temperature range of 250-400 °C. Under practical conditions without the pre-reduction, the 1Pt/3In2O3/CeO2 catalyst shows the highly efficient catalytic performance, achieving almost complete methanol conversion (98.7%) and very low CO selectivity of 2.6% at 325 °C. The supported Pt/In2O3 catalysts are characterized by means of Brunauer-Emmett-Teller (BET) surface area, X-ray diffraction (XRD), high-resolution transmission microscopy (HRTEM), temperature programmed reduction with hydrogen (H2-TPR), CO pulse chemisorption, temperature programmed desorption of methanol and water (CH3OH-TPD and H2O-TPD). These demonstrate that the nature of catalyst support of Pt/In2O3/MOx plays crucial roles in the Pt dispersion associated by the strong interaction among Pt, In2O3 and supporting materials and the surface redox properties at low temperature, and thus affects their capability to activate the reactants and determines the catalytic activity of methanol steam reforming. The superior 1Pt/3In2O3/CeO2 catalyst, exhibiting a remarkable reactivity and stability for 32 h on stream, demonstrates its potential for efficient hydrogen production of methanol steam reforming in mobile and de-centralized H2-fueled PEMFC systems.

The effect of sintering temperature on electrical characteristics of Fe2TiO5/Nb2O5 ceramics for NTC thermistor

NASA Astrophysics Data System (ADS)

Wiendartun, Risdiana, Fitrilawati, Siregar, R. E.

2016-02-01

A study on the fabrication of Iron Titanium Oxide (Fe2TiO5) ceramics for negative temperature coefficient (NTC) thermistors has been carried out, in order to know the effect of sintering temperature on the electrical characteristic of 1.0 % mole Nb2O5 doped Fe2TiO5 ceramics.These ceramics were made by mixing commercial powders of Fe2O3, TiO2 and Nb2O5 with proportional composition to produce Fe2TiO5 based ceramic. The raw pellet was sintered at 1000 °C, 1100 °C and 1200 °C temperature for 2 hours in air. Analysis of the microstructure and crystal structure were performed by using a scanning electron microscope (SEM) and x-ray diffraction (XRD) respectively. XRD spectra showed that the crystal structure of all ceramics of Fe2TiO5 made at various sintering temperatures are orthorhombic. The SEM images showed that the grain size of pellet ceramics increase with increasing sintering temperatures. From electrical resistances data that was measured at temperature 30-300 °C, it is found that the value of thermistor constant (B), activation energy (Ea), thermistor sensitivity (α) and room temperature resistance (RRT) decreases with respect to the increasing of sintering temperature. The fabricated Fe2TiO5 ceramics have thermistor constants (B = 6394-6959 K). This can be applied as temperature sensor, and will fulfill the market requirement.

Transformation Toughening of Composite Ceramics

DTIC Science & Technology

1992-12-31

Ca 2SiO 4 ) entiwickelt. Als Sili:ium-haltiger Prekursor i’urde has been well studied ’ 2 because of the considerable Siliziumdioxid veruiendet. Diese ...of carbon diffraction (XRD). This was after calcination for formed during the pyrolysis . The thermal decompo- I min at temperatures in the range...ques respectively. Some of the powders were also temperature for 1 min and cooled. At temperatures examined by SEM. below the pyrolysis stage the

Study on the surface sulfidization behavior of smithsonite at high temperature

NASA Astrophysics Data System (ADS)

Lv, Jin-fang; Tong, Xiong; Zheng, Yong-xing; Xie, Xian; Wang, Cong-bing

2018-04-01

Surface sulfidization behavior of smithsonite at high temperature was investigated by X-ray powder diffractometer (XRD) along with thermodynamic calculation, X-ray photoelectron spectroscopy (XPS) and electron probe microanalysis (EPMA). The XRD and thermodynamic analyses indicated that the smithsonite was decomposed into zincite at high temperatures. After introducing a small amount of pyrite, artificial sulfides were formed at surface of the obtained zincite. The XPS analyses revealed that the sulfide species including zinc sulfide and zinc disulfide were generated at the zincite surface. The EPMA analyses demonstrated that the film of sulfides was unevenly distributed at the zincite surface. The average concentration of elemental sulfur at the sample surface increased with increasing of pyrite dosage. A suitable mole ratio of FeS2 to ZnCO3 for the surface thermal modification was determined to be about 0.3. These findings can provide theoretical support for improving the process during which the zinc recovery from refractory zinc oxide ores is achieved by xanthate flotation.

Effect of heat treatment procedure on magnetic and magnetocaloric properties of Ni43Mn46In11 melt spun ribbons

NASA Astrophysics Data System (ADS)

Kaya, M.; Elerman, Y.; Dincer, I.

2018-07-01

The effect of heat treatment on the structural, magnetic and magnetocaloric properties of Ni43Mn46In11 melt-spun ribbons was systematically investigated using X-ray powder diffraction (XRD), scanning electron microscope (SEM), atomic force microscope (AFM), magnetic force microscope (MFM) and magnetic measurements. From the XRD studies, tetragonal and cubic phases were detected at room temperature for as-spun, quenched and slow-cooled ribbons. Furthermore, it was observed, upon annealing martensite transition temperatures increased when compared to the as-spun ribbon. To avoid magnetic hysteresis losses in the vicinity of the structural transition region, the magnetic entropy changes-ΔS m of the investigated ribbons were evaluated from temperature-dependent magnetisation-M(T) curves on cooling for different applied magnetic fields. The maximum ΔS m value was found to be 6.79 J kg-1 K-1 for the quenched ribbon in the vicinity of structural transition region for a magnetic field change of 50 kOe.

Cyclic Oxidation and Hot Corrosion Behavior of Nickel-Iron-Based Superalloy

NASA Astrophysics Data System (ADS)

Chellaganesh, D.; Adam Khan, M.; Winowlin Jappes, J. T.; Sathiyanarayanan, S.

2018-01-01

The high temperature oxidation and hot corrosion behavior of nickel-iron-based superalloy are studied at 900 ° and 1000 °C. The significant role of alloying elements with respect to the exposed medium is studied in detail. The mass change per unit area was catastrophic for the samples exposed at 1000 °C and gradual increase in mass change was observed at 900 °C for both the environments. The exposed samples were further investigated with SEM, EDS and XRD analysis to study the metallurgical characteristics. The surface morphology has expressed the in situ nature of the alloy and its affinity toward the environment. The EDS and XRD analysis has evidently proved the presence of protective oxides formation on prolonged exposure at elevated temperature. The predominant oxide formed during the exposure at high temperature has a major contribution toward the protection of the samples. The nickel-iron-based superalloy is less prone to oxidation and hot corrosion when compared to the existing alloy in gas turbine engine simulating marine environment.

In situ synchrotron XRD analysis of the kinetics of spodumene phase transitions.

PubMed

L Moore, Radhika; Mann, Jason P; Montoya, Alejandro; Haynes, Brian S

2018-04-25

The phase transition by thermal activation of natural α-spodumene was followed by in situ synchrotron XRD in the temperature range 896 to 940 °C. We observed both β- and γ-spodumene as primary products in approximately equal proportions. The rate of the α-spodumene inversion is first order and highly sensitive to temperature (apparent activation energy ∼800 kJ mol-1). The γ-spodumene product is itself metastable, forming β-spodumene, with the total product mass fraction ratio fγ/fβ decreasing as the conversion of α-spodumene continues. We found the relationship between the product yields and the degree of conversion of α-spodumene to be the same at all temperatures in the range studied. A model incorporating first order kinetics of the α- and γ-phase inversions with invariant rate constant ratio describes the results accurately. Theoretical phonon analysis of the three phases indicates that the γ phase contains crystallographic instabilities, whilst the α and β phases do not.

Annealing effect on structural and optical properties of chemical bath deposited MnS thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ulutas, Cemal, E-mail: cemalulutas@hakkari.edu.tr; Gumus, Cebrail

2016-03-25

MnS thin film was prepared by the chemical bath deposition (CBD) method on commercial microscope glass substrate deposited at 30 °C. The as-deposited film was given thermal annealing treatment in air atmosphere at various temperatures (150, 300 and 450 °C) for 1 h. The MnS thin film was characterized by using X-ray diffraction (XRD), UV-vis spectrophotometer and Hall effect measurement system. The effect of annealing temperature on the structural, electrical and optical properties such as optical constants of refractive index (n) and energy band gap (E{sub g}) of the film was determined. XRD measurements reveal that the film is crystallized inmore » the wurtzite phase and changed to tetragonal Mn{sub 3}O{sub 4} phase after being annealed at 300 °C. The energy band gap of film decreased from 3.69 eV to 3.21 eV based on the annealing temperature.« less

Effect of oxidizer to fuel molar ratio on particle size and DC conductivity of CeO{sub 2} nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Harish, B. M.; Rajeeva, M. P.; Naveen, C. S.

2016-05-06

Cerium oxide nanoparticles were synthesized by solution combustion method with varying the oxidizer (cerium nitrate hexa hydrate) to fuel (Glycine) molar ratio. The prepared samples were characterized by UV-visible spectrometer, X-ray diffractometer (XRD), Scanning electron microscope (SEM) and Energy dispersive X-Ray analysis (EDAX). XRD pattern reveals the formation of cubic fluorite structure of CeO{sub 2}. It was observed that finest crystallites were found at extreme fuel-deficient condition and it is good enough to produce favorable powder characteristics. The average crystallite size was found to be 14.46 nm to 21.57 nm. The temperature dependent dc conductivity was carried out using Keithleymore » source meter between the temperature range from 300 K to 573 K. From this study it was found that the conductivity increases with increase of temperature due to semiconducting behavior of CeO{sub 2} and it decreases with particle size due to increase in the energy band gap.« less

Structural and electrical properties of Li4Ti5O12 anode material for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Vikram Babu, B.; Vijaya Babu, K.; Tewodros Aregai, G.; Seeta Devi, L.; Madhavi Latha, B.; Sushma Reddi, M.; Samatha, K.; Veeraiah, V.

2018-06-01

In this work we investigate Li4Ti5O12 (LTO) anode material synthesized by conventional solid state reaction method calcined at 850 °C for 16 h. Thermal analysis reveals the temperature dependence of the material properties. The phase composition, micro-morphology and elemental analysis of the compound are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectra (EDS) respectively. The results of XRD pattern possessed cubic spinel structure with space group Fd-3m. The morphological features of the powder sample are in the range of 1.1 μm. The EDS spectra confirm the constituent elemental composition of the sample. Electrical conductivity measurement at different frequencies and temperatures had been carried out; and at room temperature it is found to be 5.96 × 10-7 S/cm. Besides, for the different frequencies applied, the activation energies were calculated and obtained to be in the range of 0.2-0.4 eV.

Structural and magnetic properties of morphotropic phase boundary involved Tb 1-xGd xFe 2 compounds

DOE Office of Scientific and Technical Information (OSTI.GOV)

Murtaza, Adil; Yang, Sen; Zhou, Chao

2016-09-01

In the present paper, structural, magnetic and magnetostrictive properties of Tb 1-xGd xFe 2 (0 <= x <= 1.0) were studied. Synchrotron x-ray diffraction (XRD) results show the non-cubic symmetry of Tb 1-xGd xFe 2 at room temperature and composition-induced crystallographic phase transition from rhombohedral phase to tetragonal phase. The Gd concentration dependent lattice parameters, lattice distortion and change of easy magnetic direction were detected by synchrotron XRD. With the Gd concentration increases, Curie temperature Tc increases while room temperature magnetization and magnetostriction coefficient lambda(111) and the anisotropy of TbFe 2 decrease. The decrease in spontaneous magnetostriction coefficient lambda(111) withmore » increasing Gd substitution can be understood on the basis of the single-ion model; the corresponding decrease of magnetostriction for Tb 1-xGd xFe 2, and the large magnetostriction value occurs on the Tb-rich side, are ascribed to decrease of lambda(111)« less

Laboratory Directed Research and Development Program: Annual report to the Department of Energy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ogeka, G.J.; Romano, A.J.

1994-12-01

Project program summaries are presented for: effect of bacterial spore protein on mutagenesis; cellular toxicity of coaine and cocaethylene; calcinfication in marine alga (global carbon cycling); advanced permanent magnet materials; a high flux neutron source; genetics of drug addiction; microdialysis; analysis of powder diffraction data; accelerator technology; nucleic acids and proteins and their interactions, by small-angle XRD; enhancement of microplanar beam radiation therapy of gliosarcoma; relaxographic and functional MRI; low-temperature infrared laser absorption spectroscopy; photodesorption of H{sub 2}; helical magnet for RHIC; novel microporous solids; chemistry and physics of stratospheric aerosols (ozone depletion); rf source for linear colliders; resonance Ramanmore » detection of VOCs; synthesis of plant fatty acids with unusual double bond positions; outer surface proteins of the Lyme disease spirochete; multiwire proportional chambers for collider muons; self-organized criticality; PCR-SSCP detection of genetic changes at single cell level; proton facility for cancer therapy; and visible free-electron laser experiment.« less

The structure and transformation of the nanomineral schwertmannite: a synthetic analog representative of field samples

NASA Astrophysics Data System (ADS)

French, Rebecca A.; Monsegue, Niven; Murayama, Mitsuhiro; Hochella, Michael F.

2014-04-01

The phase transformation of schwertmannite, an iron oxyhydroxide sulfate nanomineral synthesized at room temperature and at 75 °C using H2O2 to drive the precipitation of schwertmannite from ferrous sulfate (Regenspurg et al. in Geochim Cosmochim Acta 68:1185-1197, 2004), was studied using high-resolution transmission electron microscopy. The results of this study suggest that schwertmannite synthesized using this method should not be described as a single phase with a repeating unit cell, but as a polyphasic nanomineral with crystalline areas spanning less than a few nanometers in diameter, within a characteristic `pin-cushion'-like amorphous matrix. The difference in synthesis temperature affected the density of the needles on the schwertmannite surface. The needles on the higher-temperature schwertmannite displayed a dendritic morphology, whereas the needles on the room-temperature schwertmannite were more closely packed. Visible lattice fringes in the schwertmannite samples are consistent with the powder X-ray diffraction (XRD) pattern taken on the bulk schwertmannite and also matched d-spacings for goethite, indicating a close structural relationship between schwertmannite and goethite. The incomplete transformation from schwertmannite to goethite over 24 h at 75 °C was tracked using XRD and TEM. TEM images suggest that the sample collected after 24 h consists of aggregates of goethite nanocrystals. Comparing the synthetic schwertmannite in this study to a study on schwertmannite produced at 85 °C, which used ferric sulfate, reveals that synthesis conditions can result in significant differences in needle crystal structure. The bulk powder XRD patterns for the schwertmannite produced using these two samples were indistinguishable from one another. Future studies using synthetic schwertmannite should account for these differences when determining schwertmannite's structure, reactivity, and capacity to take up elements like arsenic. The schwertmannite synthesized by the Regenspurg et al. method produces a mineral that is consistent with the structure and morphology of natural schwertmannite observed in our previous study using XRD and TEM, making this an ideal synthetic method for laboratory-based mineralogical and geochemical studies that intend to be environmentally relevant.

In-field X-ray and neutron diffraction studies of re-entrant charge-ordering and field induced metastability in La0.175Pr0.45Ca0.375MnO3-δ

NASA Astrophysics Data System (ADS)

Sharma, Shivani; Shahee, Aga; Yadav, Poonam; da Silva, Ivan; Lalla, N. P.

2017-11-01

Low-temperature high-magnetic field (2 K, 8 T) (LTHM) powder X-ray diffraction (XRD) and time of flight powder neutron diffraction (NPD), low-temperature transmission electron microscopic (TEM), and resistivity and magnetization measurements have been carried out to investigate the re-entrant charge ordering (CO), field induced structural phase transitions, and metastability in phase-separated La0.175Pr0.45Ca0.375MnO3-δ (LPCMO). Low-temperature TEM and XRD studies reveal that on cooling under zero-field, paramagnetic Pnma phase transforms to P21/m CO antiferromagnetic (AFM) insulating phase below ˜233 K. Unlike reported literature, no structural signature of CO AFM P21/m to ferromagnetic (FM) Pnma phase-transition during cooling down to 2 K under zero-field was observed. However, the CO phase was found to undergo a re-entrant transition at ˜40 K. Neutron diffraction studies revealed a pseudo CE type spin arrangement of the observed CO phase. The low-temperature resistance, while cooled under zero-field, shows insulator to metal like transition below ˜105 K with minima at ˜25 K. On application of field, the CO P21/m phase was found to undergo field-induced transition to FM Pnma phase, which shows irreversibility on field removal below ˜40 K. Zero-field warming XRD and NPD studies reveal that field-induced FM Pnma phase is a metastable phase, which arise due to the arrest of kinetics of the first-order phase transition of FM Pnma to CO-AFM P21/m phase, below 40 K. Thus, a strong magneto-structural coupling is observed for this system. A field-temperature (H-T) phase-diagram has been constructed based on the LTHM-XRD, which matches very nicely with the reported H-T phase-diagram constructed based on magnetic measurements. Due to the occurrence of gradual growth of the re-entrant CO phase and the absence of a clear structural signature of phase-separation of CO-AFM P21/m and FM Pnma phases, the H-T minima in the phase-diagram of the present LPCMO sample has been attributed to the strengthening of AFM interaction during re-entrant CO transition and not to glass like "dynamic to frozen" transition.

Synthesis and Properties of Ortho-Nitro-Fe Complex

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mishra, A.; Mishra, Niyati; Sharma, R.

2011-07-15

Ortho-Nitro-Fe complex (Transition metal complex) has synthesized by chemical route method and properties of made complex has characterized by X-Ray diffraction (XRD), Moessbauer spectroscopy, Fourier transformation infra-red spectroscopy (FTIR) and X-Ray photoelectron spectroscopy (XPS). XRD analysis shows that sample is crystalline in nature and having particle size in the range of few nano meters. Moessbauer spectroscopy at room temperature shows the oxidation state of Iron (central metal ion) after complaxasion. FTIR spectra of the complex confirms the coordination of metal ion with ligand.

Using Variable Temperature Powder X-Ray Diffraction to Determine the Thermal Expansion Coefficient of Solid MgO

ERIC Educational Resources Information Center

Corsepius, Nicholas C.; DeVore, Thomas C.; Reisner, Barbara A.; Warnaar, Deborah L.

2007-01-01

A laboratory exercise was developed by using variable temperature powder X-ray diffraction (XRD) to determine [alpha] for MgO (periclase)and was tested in the Applied Physical Chemistry and Materials Characterization Laboratories at James Madison University. The experiment which was originally designed to provide undergraduate students with a…

Effect of annealing temperature on the properties of copper oxide films prepared by dip coating technique

NASA Astrophysics Data System (ADS)

Raship, N. A.; Sahdan, M. Z.; Adriyanto, F.; Nurfazliana, M. F.; Bakri, A. S.

2017-01-01

Copper oxide films were grown on silicon substrates by sol-gel dip coating method. In order to study the effects of annealing temperature on the properties of copper oxide films, the temperature was varied from 200 °C to 450 °C. In the process of dip coating, the substrate is withdrawn from the precursor solution with uniform velocity to obtain a uniform coating before undergoing an annealing process to make the copper oxide film polycrystalline. The physical properties of the copper oxide films were measured by an X-ray diffraction (XRD), a field emission scanning electron microscope (FESEM), an atomic force microscopy (AFM) and a four point probe instrument. From the XRD results, we found that pure cuprite (Cu2O) phase can be obtained by annealing the films annealed at 200 °C. Films annealed at 300 °C had a combination phase which consists of tenorite (CuO) and cuprite (Cu2O) phase while pure tenorite (CuO) phase can be obtained at 450 °C annealing temperature. The surface microstructure showed that the grains size is increased whereas the surface roughness is increased and then decreases by increasing in annealing temperature. The films showed that the resistivity decreased with increasing annealing temperature. Consequently, it was observed that annealing temperature has strong effects on the structural, morphological and electrical properties of copper oxide films.

Fabrication of Far Red Emission Phosphors Y3Al5O12:Eu(YAG:Eu) by Co-precipitation Method

NASA Astrophysics Data System (ADS)

Thu, L. D.; Trung, D. Q.; Lam, T. D.; Anh, T. X.

2016-05-01

Phosphors YAG:Eu (with seven molar percent of Eu to YAG) was synthesized by the co-precipitation method using NH3 solution as a precipitating agent. X-ray diffraction (XRD) patterns show that the samples are single phase, and the crystallinity starts forming at a sintering temperature of 1000°C. The crystallinity increases with the increasing sintered temperature. XRD studies followed by Rietveld refinement confirmed the body center cubic structure of the host lattice. The crystalline YAG:Eu showed four emission bands of europium ion with the force dipole transition ascribed to 5D0-7F4 located at 710 nm as the most dominating group (far-red emission—FR). The ratio of FR/OR (far-red/orange—red) is about 1.24 in all samples.

Hydrogenolysis of Glycerol to Propylene Glycol on Nanosized Cu-Zn-Al Catalysts Prepared Using Microwave Process.

PubMed

Kim, Dong Won; Ha, Sang Ho; Moon, Myung Jun; Lim, Kwon Taek; Ryu, Young Bok; Lee, Sun Do; Lee, Man Sig; Hong, Seong-Soo

2015-01-01

Cu-Zn-Al catalysts were prepared using microwave-assisted process and co-precipitation methods. The prepared catalysts were characterized by XRD, BET, XPS and TPD of ammonia and their catalytic activity for the hydrogenolysis of glycerol to propylene glycol was also examined. The XRD patterns of Cu/Zn/Al mixed catalysts show CuO and ZnO crystalline phase regardless of preparation method. The highest glycerol hydrogenolysis conversion is obtained with the catalyst having a Cu/Zn/Al ratio of 2:2:1. Hydrogen pre-reduction of catalysts significantly enhanced both glycerol conversions and selectivity to propylene glycol. The glycerol conversion increased with an increase of reaction temperature. However, the selectivity to propylene glycol increased with an increase of temperature, and then declined to 30.5% at 523 K.

Characterization of melt-quenched and milled amorphous solids of gatifloxacin.

PubMed

Hattori, Yusuke; Suzuki, Ayumi; Otsuka, Makoto

2016-11-01

The objectives of this study were to characterize and investigate the differences in amorphous states of gatifloxacin. We prepared two types of gatifloxacin amorphous solids coded as M and MQ using milling and melt-quenching methods, respectively. The amorphous solids were characterized via X-ray diffraction (XRD), nonisothermal differential scanning calorimetry (DSC) and time-resolved near-infrared (NIR) spectroscopy. Both the solids displayed halo XRD patterns, the characteristic of amorphous solids; however, in the non-isothermal DSC profiles, these amorphous solids were distinguished by their crystallization and melting temperatures. The Kissinger-Akahira-Sunose plots of non-isothermal crystallization temperatures at various heating rates indicated a lower activation energy of crystallization for the amorphous solid M than that of MQ. These results support the differentiation between two amorphous states with different physical and chemical properties.

Dielectric Relaxation Behavior and AC Electrical Conductivity Study of 2-(1,2-Dihydro-7-Methyl-2-Oxoquinoline-5-yl) Malononitrile (DMOQMN)

NASA Astrophysics Data System (ADS)

El-Nahass, M. M.; El-Zaidia, E. F. M.; Darwish, A. A. A.; Salem, G. F.

2017-02-01

Dielectric relaxation and alternative current conductivity of a new organic compound 2-(1,2-dihydro-7-methyl-2-oxoquinoline-5-yl) malononitrile (DMOQMN) have been investigated. X-ray diffraction (XRD) at room temperature reveals that DMOQMN samples have a polycrystalline structure of the triclinic system. The analysis of the dielectric constant and dielectric loss index suggested the dominant polarization is performed and the Maxwell-Wagner-Sillar type polarization is dominating at low frequency and high temperature. These results have been confirmed by the XRD and dielectric modulus. The estimated relaxation time and the activation energy are 9 × 10-13 s and 0.43 eV, respectively. Our results indicated that the conduction mechanism of DMOQMN is controlled by the correlation barrier hopping (CBH) model.

High-resolution transmission electron microscopy studies of graphite materials prepared by high-temperature treatment of unburned carbon concentrates from combustion fly ashes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Miguel Cabielles; Jean-Nol Rouzaud; Ana B. Garcia

2009-01-15

High-resolution transmission electron microscopy (HRTEM) has been used in this work to study the microstructural (structure and microtexture) changes occurring during the high-temperature treatment of the unburned carbon concentrates from coal combustion fly ashes. Emphasis was placed on two aspects: (i) the development of graphitic carbon structures and (ii) the disordered carbon forms remaining in the graphitized samples. In addition, by coupling HRTEM with energy-dispersive spectroscopy, the transformations with the temperature of the inorganic matter (mainly iron- and silicon-based phases) of the unburned carbon concentrates were evidenced. The HRTEM results were compared to the averaged structural order of the materialsmore » as evaluated by X-ray diffraction (XRD) and Raman spectroscopy. As indicated by XRD and Raman parameters, more-ordered materials were obtained from the unburned carbon concentrates with higher mineral/inorganic matter, thus inferring the catalytic effect of some of their components. However, the average character of the information provided by these instrumental techniques seems to be inconclusive in discriminating between carbon structures with different degrees of order (stricto sensu graphite, graphitic, turbostratic, etc.) in a given graphitized unburned carbon. Unlike XRD and Raman, HRTEM is a useful tool for imaging directly the profile of the polyaromatic layers (graphene planes), thus allowing the sample heterogeneity to be looked at, specifically the presence of disordered carbon phases. 49 refs., 9 figs., 3 tabs.« less

Effect of thermal annealing on the phase evolution of silver tungstate in Ag/WO₃ films.

PubMed

Bose, R Jolly; Sreedharan, R Sreeja; Krishnan, R Resmi; Reddy, V R; Gupta, Mukul; Ganesan, V; Sudheer, S K; Pillai, V P Mahadevan

2015-06-15

Silver/tungsten oxide multi-layer films are deposited over quartz substrates by RF magnetron sputtering technique and the films are annealed at temperatures 200, 400 and 600°C. The effect of thermal annealing on the phase evolution of silver tungstate phase in Ag/WO3 films is studied extensively using techniques like X-ray diffraction, micro-Raman analysis, atomic force microscopy and photoluminescence studies. The XRD pattern of the as-deposited film shows only the peaks of cubic phase of silver. The film annealed at 200°C shows the presence of XRD peaks corresponding to orthorhombic phase of Ag2WO4 and peaks corresponding to cubic phase of silver with reduced intensity. It is found that, as annealing temperature increases, the volume fraction of Ag decreases and that of Ag2WO4 phase increases and becomes highest at a temperature of 400°C. When the temperature increases beyond 400°C, the volume fraction of Ag2WO4 decreases, due to its decomposition into silver and oxygen deficient phase Ag2W4O13. The micro-Raman spectra of the annealed films show the characteristic bands of tungstate phase which is in agreement with XRD analysis. The surface morphology of the films studied by atomic force microscopy reveals that the particle size and r.m.s roughness are highest for the sample annealed at 400°C. In the photoluminescence study, the films with silver tungstate phase show an emission peak in blue region centered around the wavelength 441 nm (excitation wavelength 256 nm). Copyright © 2015 Elsevier B.V. All rights reserved.

Synthesis of waste cooking oil based biodiesel via ferric-manganese promoted molybdenum oxide / zirconia nanoparticle solid acid catalyst: influence of ferric and manganese dopants.

PubMed

Alhassan, Fatah H; Rashid, Umer; Taufiq-Yap, Yun Hin

2015-01-01

The utilization of ferric-manganese promoted molybdenum oxide/zirconia (Fe-Mn- MoO3/ZrO2) (FMMZ) solid acid catalyst for production of biodiesel was demonstrated. FMMZ is produced through impregnation reaction followed by calcination at 600°C for 3 h. The characterization of FMMZ had been done using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), thermal gravimetric analysis (TGA), temperature programmed desorption of NH3 (TPD-NH3), transmission electron microscopy(TEM) and Brunner-Emmett-Teller (BET) surface area measurement. The effect of waste cooking oil methyl esters (WCOME's) yield on the reactions variables such as reaction temperature, catalyst loading, molar ratio of methanol/oil and reusability were also assessed. The catalyst was used to convert the waste cooking oil into corresponding methyl esters (95.6%±0.15) within 5 h at 200℃ reaction temperature, 600 rpm stirring speed, 1:25 molar ratio of oil to alcohol and 4% w/w catalyst loading. The reported catalyst was successfully recycled in six connective experiments without loss in activity. Moreover, the fuel properties of WCOME's were also reported using ASTM D 6751 methods.

Anode-supported single-chamber solid oxide fuel cell based on cobalt-free composite cathode of Nd0.5Sr0.5Fe0.8Cu0.2O3-δ-Sm0.2Ce0.8O1.9 at intermediate temperatures

NASA Astrophysics Data System (ADS)

Yin, Jie-Wei; Zhang, Chunming; Yin, Yi-Mei; Shi, Huangang; Lin, Ye; Lu, Jun; Ma, Zi-Feng

2015-07-01

As a candidate of cathode material of single-chamber solid oxide fuel cell (SC-SOFC), cobalt-free mixed ionic electronic conductor (MIEC) Nd0.5Sr0.5Fe0.8Cu0.2O3-δ (NSFCu) is synthesized by sol-gel method with ethylene diamine tetraacetic acid and citric acid as co-complexing agents. The XRD shows NSFCu is stable after CO2 treatment and chemical compatible with SDC at high temperatures. CO2-TPD (CO2-temperature programmed desorption) demonstrates both CO2 adsorption and desorption phenomenon on NSFCu surface. However, the polarization resistances (Rp) of NSFCu and SDC (10:4 in weight) composite electrodes showed no decay in 5% CO2. Single cell using N2-O2-CH4 mixed gas (CH4 to O2 ratio = 1.5) as fuel shows maximum power density of 635 mW cm-2 at 700 °C. These results suggest that NSFCu-SDC is a promising composite cathode material for application in single-chamber solid oxide fuel cell.

A study of tantalum pentoxide Ta 2O 5 structures up to 28 GPa

DOE PAGES

Stavrou, Elissaios; Zaug, Joseph M.; Bastea, Sorin; ...

2017-05-02

In this study, tantalum pentoxide Ta 2O 5 with the orthorhombic L-Ta 2O 5 structure has been experimentally studied up to 28.3 GPa (at ambient temperature) using synchrotron angle-dispersive powder X-ray diffraction (XRD). The ambient pressure phase remains stable up to 25 GPa where with increased pressure a crystalline to amorphous phase transition occurs. A detailed equation of state (EOS), including pressure dependent lattice parameters, is reported. The results of this study were compared with a previous high-pressure XRD study by Li et al. A clear discrepancy between the ambient-pressure crystal structures and, consequently, the reported EOSs between the twomore » studies was revealed. Finally, he origin of this discrepancy is attributed to two different crystal structures used to index the XRD patterns.« less

Thermochemistry of amorphous and crystalline zirconium and hafnium silicates.

NASA Astrophysics Data System (ADS)

Ushakov, S.; Brown, C. E.; Navrotsky, Alexandra; Boatner, L. A.; Demkov, A. A.; Wang, C.; Nguyen, B.-Y.

2003-03-01

Calorimetric investigation of amorphous and crystalline zirconium and hafnium silicates was performed as part of a research program on thermochemistry of alternative gate dielectrics. Amorphous hafnium and zirconium silicates with varying SiO2 content were synthesized by a sol-gel process. Crystalline zirconium and hafnium silicates (zircon and hafnon) were synthesized by solid state reaction at 1450 °C from amorphous gels and grown as single crystals from flux. High temperature oxide melt solution calorimetry in lead borate (2PbO.B2O3) solvent at 800 oC was used to measure drop solution enthalpies for amorphous and crystalline zirconium and hafnium silicates and corresponding oxides. Applying appropriate thermochemical cycles, formation enthalpy of crystalline ZrSiO4 (zircon) from binary oxides (baddeleite and quartz) at 298 K was calculated as -23 +/-2 kJ/mol and enthalpy difference between amorphous and crystalline zirconium silicate (vitrification enthalpy) was found to be 61 +/-3 kJ/mol. Crystallization onset temperatures of amorphous zirconium and hafnium silicates, as measured by differential scanning calorimetry (DSC), increased with silica content. The resulting crystalline phases, as characterized by X-ray diffraction (XRD), were tetragonal HfO2 and ZrO2. Critical crystallite size for tetragonal to monoclinic transformation of HfO2 in the gel was estimated as 6 +/-2 nm from XRD data Crystallization enthalpies per mole of hafnia and zirconia in gels decrease slightly together with crystallite size with increasing silica content, for example from -22 to -15 +/-1 kJ per mol of HfO2 crystallized at 740 and 1006 °C from silicates with 10 and 70 mol Applications of thermal analyses and solution calorimetry techniques together with first-principles density functional calculations to estimate interface and surface energies are discussed.

Evaluation of Cation Migration in Lanthanum Strontium Cobalt Ferrite Solid Oxide Fuel Cell Cathodes via In-operando X-ray Diffraction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hardy, John S.; Coyle, Christopher A.; Bonnett, Jeff F.

2018-01-28

Anode-supported SOFCs with LSCF-6428 cathodes were operated at various temperatures for hundreds of hours in dry or humid (~3% water) cathode air with continuous cathode XRD. Additionally, one cell in dry air was held at OCV and another had 12% CO2 added to the humid air. Long cumulative XRD count times allowed identification of minor phases at <0.1 wt%. In humid air, performance improved during the first couple of hundred hours and Fe-rich Fe,Co spinel XRD peaks gradually shifted to lower angles while nano-nodules formed on LSCF surfaces. With 12% CO2 added, performance degraded after initial activation, unlike without CO2,more » where stability followed activation. In CO2, LSCF XRD peaks shifted indicating gradual decomposition. In dry air, fast initial degradation that decelerated over time occurred at constant current while the cell at OCV was stable. At OCV and 750°C or at constant current and 700°C in dry air, Fe-rich spinel XRD peaks shifted more slowly than in humid air tests; Co-rich Fe,Co spinel peaks shifted to higher angles; and SEM discovered smaller nano-nodules on LSCF than after humid air tests. At constant current at 750°C and 800°C in dry air, no nano-nodules or gradual changes in the XRD patterns were discovered.« less

Phase change of hydromagnesite, Mg5(CO3)4(OH)2 4H2O by thermal decomposition

NASA Astrophysics Data System (ADS)

Yamamoto, G. I.; Kyono, A.; Tamura, T.

2017-12-01

In recent years, the global warming is the most important environment problem, and thus attempts of CO2 geological storage have been made to remove carbon dioxide from the atmosphere all over the world (XUE and Nakao 2008). Regarding mineral CO2 sequestration, CO2 is chemically stored in solid carbonates by carbonation of minerals. Magnesium and calcium carbonates have long been known as a good CO2 storage. Hydrous magnesium carbonates can be, however, considered as much better candidates for CO2 storage because they precipitate easily from aqueous solutions. The typical hydrous magnesium carbonates are nesquehonite, MgCO3 3H2O and hydromagnesite, Mg5(CO3)4(OH)2 4H2O. Concerning their thermal properties, the former has been studied in detail, whereas, the latter is not enough. In this study, we performed in-site high-temperature X-ray diffraction (XRD) and thermogravimetric and differential thermal (TG-DTA) analyses to reveal the phase change of hydromagnesite at high temperature. The high-temperature XRD and TG-DTA were measured up to 320 oC and 550 oC, respectively. The results of in-site high-temperature XRD showed that, no significant change was observed up to 170 oC. With increasing temperature, the intensities of started to decrease at 200 oC, and all peaks disappeared at 290 oC. Above the temperature of the decomposition a few peaks corresponding to periclase appeared. The results of TG-DTA clearly showed that there were two weight loss steps in the temperature range of 200 to 340 oC and 340 to 500 oC, which correspond to the dehydration and decarbonation of hydromagnesite, respectively. These weight losses were accompanied by the endothermic maxima in the DTA. The dihydroxylation of hydromagnesite is spread over the two steps. Therefore, hydromagnesite decomposes into periclase, carbon dioxide, and water without passing through magnesite around 300 oC as following reaction: Mg5(CO3)4(OH)2 4H2O → 5MgO + 4CO2 + 5H2O.

The Effect of Compaction Force on the Transition to Hydrate of Anhydrous Aripiprazole.

PubMed

Togo, Taichiro; Taniguchi, Toshiya; Nakata, Yoshitaka

2018-01-01

Aripiprazole (APZ) is used to treat schizophrenia and is administered as a tablet containing the anhydrous form of APZ. In this study, the effect of compaction force on the crystal form transition was investigated. The crystalline state was observed by X-ray diffraction (XRD). APZ Anhydrous Form II was compacted into tablets. The XRD intensity of anhydrous APZ became lower with higher compressive force. The degree of crystallinity decreased with the compaction force. The powder and the compacted tablets of anhydrous APZ were stored for one week under 60°C and 75% relative humidity. The powder showed no crystal form transition after storage. For the tablets, however, XRD peaks of APZ hydrate were observed after storage. The tablets compacted with higher force showed the higher XRD diffraction intensity of hydrate form. We concluded that the crystallinity reduction of APZ Anhydrous Form II by compaction caused and accelerated the transition to hydrate under high temperature and humidity conditions. In order to manufacture crystallographically stable tablets containing anhydrous APZ, it is important to prevent this crystallinity reduction during compaction.

In-plane x-ray diffraction for characterization of monolayer and few-layer transition metal dichalcogenide films

NASA Astrophysics Data System (ADS)

Chubarov, Mikhail; Choudhury, Tanushree H.; Zhang, Xiaotian; Redwing, Joan M.

2018-02-01

There is significant interest in the growth of single crystal monolayer and few-layer films of transition metal dichalcogenides (TMD) and other 2D materials for scientific exploration and potential applications in optics, electronics, sensing, catalysis and others. The characterization of these materials is crucial in determining the properties and hence the applications. The ultra-thin nature of 2D layers presents a challenge to the use of x-ray diffraction (XRD) analysis with conventional Bragg-Brentano geometry in analyzing the crystallinity and epitaxial orientation of 2D films. To circumvent this problem, we demonstrate the use of in-plane XRD employing lab scale equipment which uses a standard Cu x-ray tube for the analysis of the crystallinity of TMD monolayer and few-layer films. The applicability of this technique is demonstrated in several examples for WSe2 and WS2 films grown by chemical vapor deposition on single crystal substrates. In-plane XRD was used to determine the epitaxial relation of WSe2 grown on c-plane sapphire and on SiC with an epitaxial graphene interlayer. The evolution of the crystal structure orientation of WS2 films on sapphire as a function of growth temperature was also examined. Finally, the epitaxial relation of a WS2/WSe2 vertical heterostructure deposited on sapphire substrate was determined. We observed that WSe2 grows epitaxially on both substrates employed in this work under all conditions studied while WS2 exhibits various preferred orientations on sapphire substrate which are temperature dependent. In contrast to the sapphire substrate, WS2 deposited on WSe2 exhibits only one preferred orientation which may provide a route to better control the orientation and crystal quality of WS2. In the case of epitaxial graphene on SiC, no graphene-related peaks were observed in in-plane XRD while its presence was confirmed using Raman spectroscopy. This demonstrates the limitation of the in-plane XRD technique for characterizing low electron density materials.

Preparation of highly active manganese oxides supported on functionalized MWNTs for low temperature NOx reduction with NH3

NASA Astrophysics Data System (ADS)

Pourkhalil, Mahnaz; Moghaddam, Abdolsamad Zarringhalam; Rashidi, Alimorad; Towfighi, Jafar; Mortazavi, Yadollah

2013-08-01

Manganese oxide catalysts (MnOx) supported on functionalized multi-walled carbon nanotubes (FMWNTs) for low temperature selective catalytic reduction (LTSCR) of nitrogen oxides (NOx) with NH3 in the presence of excess O2 were prepared by the incipient wetness impregnation method. These catalysts were characterized by N2 adsorption, Fourier transform infrared spectroscopy (FTIR), transmission electron microscope (TEM), X-ray diffraction (XRD), thermal gravimetric analysis (TGA) and H2-temperature programmed reduction (H2-TPR) methods. The effects of reaction temperature, MnOx loading, calcination temperature and calcination time were investigated. The presence of surface nitrate species under moderate calcination conditions may play a favorable role in the LTSCR of NOx with NH3. Under the reaction conditions of 200 °C, 1 bar, NO = NH3 = 900 ppm, O2 = 5 vol%, GHSV = 30,000 h-1 and 12 wt% MnOx, NOx conversion and N2 selectivity were 97% and 99.5%, respectively. The SCR activity was reduced in the presence of 100 ppm SO2 and 2.5 vol% H2O from 97% to 92% within 6 h at 200 °C, however such an effect was shown to be reversible by exposing the catalyst to a helium flow for 2 h at 350 °C due to thermal decomposition of ammonium sulphate salts.

Macro controlling of copper oxide deposition processes and spray mode by using home-made fully computerized spray pyrolysis system

NASA Astrophysics Data System (ADS)

Essa, Mohammed Sh.; Chiad, Bahaa T.; Shafeeq, Omer Sh.

2017-09-01

Thin Films of Copper Oxide (CuO) absorption layer have been deposited using home-made Fully Computerized Spray Pyrolysis Deposition system FCSPD on glass substrates, at the nozzle to substrate distance equal to 20,35 cm, and computerized spray mode (continues spray, macro-control spray). The substrate temperature has been kept at 450 °c with the optional user can enter temperature tolerance values ± 5 °C. Also that fixed molar concentration of 0.1 M, and 2D platform speed or deposition platform speed of 4mm/s. more than 1000 instruction program code, and specific design of graphical user interface GUI to fully control the deposition process and real-time monitoring and controlling the deposition temperature at every 200 ms. The changing in the temperature has been recorded during deposition processes, in addition to all deposition parameters. The films have been characterized to evaluate the thermal distribution over the X, Y movable hot plate, the structure and optical energy gap, thermal and temperature distribution exhibited a good and uniform distribution over 20 cm2 hot plate area, X-ray diffraction (XRD) measurement revealed that the films are polycrystalline in nature and can be assigned to monoclinic CuO structure. Optical band gap varies from 1.5-1.66 eV depending on deposition parameter.

An X-ray diffraction method for semiquantitative mineralogical analysis of Chilean nitrate ore

USGS Publications Warehouse

Jackson, J.C.; Ericksent, G.E.

1997-01-01

Computer analysis of X-ray diffraction (XRD) data provides a simple method for determining the semiquantitative mineralogical composition of naturally occurring mixtures of saline minerals. The method herein described was adapted from a computer program for the study of mixtures of naturally occurring clay minerals. The program evaluates the relative intensities of selected diagnostic peaks for the minerals in a given mixture, and then calculates the relative concentrations of these minerals. The method requires precise calibration of XRD data for the minerals to be studied and selection of diffraction peaks that minimize inter-compound interferences. The calculated relative abundances are sufficiently accurate for direct comparison with bulk chemical analyses of naturally occurring saline mineral assemblages.

An x-ray diffraction method for semiquantitative mineralogical analysis of chilean nitrate ore

USGS Publications Warehouse

John, C.; George, J.; Ericksen, E.

1997-01-01

Computer analysis of X-ray diffraction (XRD) data provides a simple method for determining the semiquantitative mineralogical composition of naturally occurring mixtures of saline minerals. The method herein described was adapted from a computer program for the study of mixtures of naturally occurring clay minerals. The program evaluates the relative intensities of selected diagnostic peaks for the minerals in a given mixture, and then calculates the relative concentrations of these minerals. The method requires precise calibration of XRD data for the minerals to be studied and selection of diffraction peaks that minimize inter-compound interferences. The calculated relative abundances are sufficiently accurate for direct comparison with bulk chemical analyses of naturally occurring saline mineral assemblages.

Influence of sulfurization temperature on Cu2ZnSnS4 absorber layer on flexible titanium substrates for thin film solar cells

NASA Astrophysics Data System (ADS)

Gokcen Buldu, Dilara; Cantas, Ayten; Turkoglu, Fulya; Gulsah Akca, Fatime; Meric, Ece; Ozdemir, Mehtap; Tarhan, Enver; Ozyuzer, Lutfi; Aygun, Gulnur

2018-02-01

In this study, the effect of sulfurization temperature on the morphology, composition and structure of Cu2ZnSnS4 (CZTS) thin films grown on titanium (Ti) substrates has been investigated. Since Ti foils are flexible, they were preferred as a substrate. As a result of their flexibility, they allow large area manufacturing and roll-to-roll processes. To understand the effects of sulfurization temperature on the CZTS formation on Ti foils, CZTS films fabricated with various sulfurization temperatures were investigated with several analyses including x-ray diffraction (XRD), scanning electron microscopy (SEM), x-ray photoelectron spectroscopy and Raman scattering. XRD measurements showed a sharp and intense peak coming from the (112) planes of the kesterite type lattice structure (KS), which is strong evidence for good crystallinity. The surface morphologies of our thin films were investigated using SEM. Electron dispersive spectroscopy was also used for the compositional analysis of the thin films. According to these analysis, it is observed that Ti foils were suitable as substrates for the growth of CZTS thin films with desired properties and the sulfurization temperature plays a crucial role for producing good quality CZTS thin films on Ti foil substrates.

Effect of calcination temperature on microstructure and magnetic properties of Ni{sub 0.5}Zn{sub 0.25}Cu{sub 0.25} Fe{sub 2}O{sub 4} nanoparticles synthesized by sol-gel method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pransisco, Prengki, E-mail: prengkipransisco@gmail.com, E-mail: afza@petronas.com.my; Shafie, Afza, E-mail: prengkipransisco@gmail.com, E-mail: afza@petronas.com.my; Guan, Beh Hoe, E-mail: beh.hoeguan@petronas.com.my

2014-10-24

This paper examines the effect of calcination process on the structural and magnetic properties material nanostructure composite of Ni{sub 0Ð}œ‡{sub 5}Zn{sub 0Ð}œ‡{sub 25}Cu{sub 0.25} Fe{sub 2}O{sub 4} ferrites. The samples were successfully prepared by sol-gel method at different calcination temperature, which are 600°C, 700°C, 800°C and 900°C. Morphological investigation, average crystallite size and microstructure of the material were examined by using X-ray diffraction (XRD) and confirmed by high resolution transmission electron microscope (HRTEM) and field emission scanning electron microscope (FESEM). The effects of calcination temperature on the magnetic properties were calculated by using vibrating sample magnetometer (VSM). The XRD resultmore » shows single-phase cubic spinel structure with interval average size 5.9-38 nm, and grain size microstructure of the material was increasing with temperature increases. The highest magnetization saturation was reached at a temperature 800°C with value 53.89 emu/g, and the value coercive force (Hc) was inversely with the grain size.« less

Effect of Bi substitution on the magnetic and magnetocaloric properties of Ni50Mn35In15-xBix Heusler alloys

NASA Astrophysics Data System (ADS)

Aryal, Anil; Quetz, Abdiel; Pandey, Sudip; Dubenko, Igor; Stadler, Shane; Ali, Naushad

2018-05-01

The structural, magnetic, magnetocaloric, and transport properties of Ni50Mn35In15-xBix (x = 0, 0.25, 0.5, 1, 1.5) compounds has been studied through X-ray diffraction (XRD), differential scanning calorimetry, and magnetization measurements. A mixture of high temperature austenite phase (AP) and low temperature martensitic phase (MP) was observed from the XRD at room temperature. The saturation magnetization MS at 10 K was found to decrease with increasing Bi content. A shift in the martensitic transition temperature (TM) relative to the parent compound was observed with a maximum shift of ˜ 36 K for x = 1.5. Abnormal shifts in TC and TM to higher temperatures were observed at high field for x ≥ 0.5. Large magnetic entropy changes (ΔSM) of about 40 J/kg K (x = 0) and 34 J/kg K (x = 0.25) were observed at TM with H = 5 T, which reduced significantly for higher Bi concentrations. The doping of small amounts of Bi in the In sites increased the peak width of the ΔSM curves at the second order transition, leading to larger values of relative cooling power. A significant magnetoresistance (-30%) was observed near TM with ΔH = 5T for x = 0.5.

Phase transition studies in bismuth ferrite thin films synthesized via spray pyrolysis technique

NASA Astrophysics Data System (ADS)

Goyal, Ankit; Lakhotia, Harish

2013-06-01

Multiferroic are the materials, which combine two or more "ferroic" properties, ferromagnetism, ferroelectricity or ferroelasticity. BiFeO3 is the only single phase multiferroic material which possesses a high Curie temperature (TC ˜ 1103 K), and a high Neel temperature (TN ˜ 643 K) at room temperature. Normally sophisticated methods are being used to deposit thin films but here we have tried a different method Low cost Spray Pyrolysis Method to deposit BiFeO3 thin film of Glass Substrate with rhombohedral crystal structure and R3c space group. Bismuth Ferrite thin films are synthesized using Bismuth Nitrate and Iron Nitrate as precursor solutions. X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) were used to study structural analysis of prepared thin films. XRD pattern shows phase formation of BiFeO3 and SEM analysis shows formation of nanocrystals of 200 nm. High Temperature Resistivity measurements were done by using Keithley Electrometer (Two Probe system). Abrupt behavior in temperature range (313 K - 400K) has been observed in resistance studies which more likely suggests that in this transition the structure is tetragonal rather than rhombohedral. BiFeO3 is the potential active material in the next generation of ferroelectric memory devices.

Green thermal-assisted synthesis and characterization of novel cellulose-Mg(OH)2 nanocomposite in PEG/NaOH solvent.

PubMed

Ponomarev, Nikolai; Repo, Eveliina; Srivastava, Varsha; Sillanpää, Mika

2017-11-15

Synthesis of nanocomposites was performed using microcrystalline cellulose (MCC), MgCl 2 in PEG/NaOH solvent by a thermal-assisted method at different temperatures by varying time and the amount of MCC. Results of XRD, FTIR, and EDS mapping showed that the materials consisted of only cellulose (CL) and magnesium hydroxide (MH). According to FTIR and XRD, it was found that crystallinity of MH in cellulose nanocomposites is increased with temperature and heating time and decreased with increasing of cellulose amount. The PEG/NaOH solvent has a significant effect on cellulose and Mg(OH) 2 morphology. BET and BJH results demonstrated the effects of temperature and cellulose amount on the pore size corresponding to mesoporous materials. TG and DTG analyses showed the increased thermal stability of cellulose nanocomposites with increasing temperature. TEM and SEM analyses showed an even distribution of MH nanostructures with various morphology in the cellulose matrix. The cellulose presented as the polymer matrix in the nanocomposites. It was supposed the possible interaction between cellulose and Mg(OH) 2 . The novel synthesis method used in this study is feasible, cost-efficient and environmentally friendly. Copyright © 2017 Elsevier Ltd. All rights reserved.

Structural, transport and magnetotransport properties of Ru-doped La0.5Sr0.5Mn1-xRuxO3 (x = 0.0 & 0.05) manganite

NASA Astrophysics Data System (ADS)

Jethva, Sadaf; Katba, Savan; Udeshi, Malay; Kuberkar, D. G.

2017-09-01

We report the results of the structural, transport and magnetotransport studies on polycrystalline La0.5Sr0.5Mn1-xRuxO3 (x = 0.0 and 0.05) manganite investigated using XRD and resistivity (with and without field) measurements. Rietveld refinement of XRD patterns confirms the single phasic tetragonal structure for both the samples crystalizing in I4/mcm space group (No. 140). Low-temperature resistivity and MR measurements with H = 0 T & 5 T field show thermal hysteresis which has been attributed to the first order phase transition. The increase in resistivity and decrease in metal - insulator transition temperature (TMI) with Ru - doping concentration in La0.5Sr0.5MnO3 (LSMO) has been understood in the context of superexchange interaction between Mn and Ru ions. The observed upturn in resistivity at low temperature under field has been explained using combined effect of electron - electron (e - e) interaction, Kondo-like spin-dependent scattering and electron - phonon interaction while the variation in resistivity at high temperature (T > Tp) has been explained using adiabatic small polaron hopping model.

Effects of sulfation level on the desulfation behavior of pre-sulfated Pt BaO/Al2O3 lean NOx trap catalysts: a combined H2 Temperature-Programmed Reaction, in-situ sulfur K-edge X-ray Absorption Near-Edge Spectroscopy, X-ray Photoelectron Spectroscopy, and Time-Resolved X-ray Diffraction Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Do Heui; Szanyi, Janos; Kwak, Ja Hun

2009-04-03

Desulfation by hydrogen of pre-sulfated Pt(2wt%) BaO(20wt%)/Al2O3 with various sulfur loading (S/Ba = 0.12, 0.31 and 0.62) were investigated by combining H2 temperature programmed reaction (TPRX), x-ray photoelectron spectroscopy (XPS), in-situ sulfur K-edge x-ray absorption near-edge spectroscopy (XANES), and synchrotron time-resolved x-ray diffraction (TR-XRD) techniques. We find that the amount of H2S desorbed during the desulfation in the H2 TPRX experiments is not proportional to the amount of initial sulfur loading. The results of both in-situ sulfur K-edge XANES and TR-XRD show that at low sulfur loadings, sulfates were transformed to a BaS phase and remained in the catalyst, rathermore » than being removed as H2S. On the other hand, when the deposited sulfur level exceeded a certain threshold (at least S/Ba = 0.31) sulfates were reduced to form H2S, and the relative amount of the residual sulfide species in the catalyst was much less than at low sulfur loading. Unlike samples with high sulfur loading (e.g., S/Ba = 0.62), H2O did not promote the desulfation for the sample with S/Ba of 0.12, implying that the formed BaS species originating from the reduction of sulfates at low sulfur loading are more stable to hydrolysis. The results of this combined spectroscopy investigation provide clear evidence to show that sulfates at low sulfur loadings are less likely to be removed as H2S and have a greater tendency to be transformed to BaS on the material, leading to the conclusion that desulfation behavior of Pt BaO/Al2O3 lean NOx trap catalysts is markedly dependent on the sulfation levels.« less

Effects of Sulfation Level on the Desulfation Behavior of Presulfated Pt-BaO/Al2O3 Lean NOx Trap Catalysts: A Combined H2 Temperature-Programmed Reaction, in Situ Sulfur K-Edge X-ray Absorption Near-Edge Spectroscopy, X-ray Photoelectron Spectroscopy, and Time-Resolved X-ray Diffraction Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, D.H.; Hanson, J.; Szanyi, J.

2009-04-30

Desulfation by hydrogen of presulfated Pt (2 wt %)-BaO(20 wt %)/Al{sub 2}O{sub 3} with various sulfur loading (S/Ba = 0.12, 0.31, and 0.62) were investigated by combining H{sub 2} temperature programmed reaction (TPRX), X-ray photoelectron spectroscopy (XPS), in situ sulfur K-edge X-ray absorption near-edge spectroscopy (XANES), and synchrotron time-resolved X-ray diffraction (TR-XRD) techniques. We find that the amount of H{sub 2}S desorbed during the desulfation in the H{sub 2} TPRX experiments is not proportional to the amount of initial sulfur loading. The results of both in situ sulfur K-edge XANES and TR-XRD show that at low sulfur loadings, sulfates weremore » transformed to a BaS phase and remained in the catalyst rather than being removed as H{sub 2}S. On the other hand, when the deposited sulfur level exceeded a certain threshold (at least S/Ba = 0.31) sulfates were reduced to form H{sub 2}S, and the relative amount of the residual sulfide species in the catalyst was much less than at low sulfur loading. Unlike samples with high sulfur loading (e.g., S/Ba = 0.62), H{sub 2}O did not promote the desulfation for the sample with S/Ba of 0.12, implying that the formed BaS species originating from the reduction of sulfates at low sulfur loading are more stable to hydrolysis. The results of this combined spectroscopy investigation provide clear evidence to show that sulfates at low sulfur loadings are less likely to be removed as H{sub 2}S and have a greater tendency to be transformed to BaS on the material, leading to the conclusion that desulfation behavior of Pt-BaO/Al{sub 2}O{sub 3} lean NO{sub x} trap catalysts is markedly dependent on the sulfation levels.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hamdi, S.; Ouni, S.; Chaker, H.

A new compound DySr{sub 5}Ni{sub 2.4}Cu{sub 0.6}O{sub 12-{delta}} has been prepared by sol gel method and annealed at 1473 K in 1 atm of Ar gas flow. The X-ray diffraction (XRD) is used for phase identification. The sample shows to adopt the K{sub 2}NiF{sub 4}-type structure based on tolerance factor calculation. XRD analysis using the Rietveld method was carried out and it was found that DySr{sub 5}Ni{sub 2.4}Cu{sub 0.6}O{sub 12-{delta}} (Dy{sub 0.33}Sr{sub 1.67}Ni{sub 0.8}Cu{sub 0.2}O{sub 4-{delta}}') compound crystallizes in tetragonal symmetry with space group I4/mmm (Z=2). The lattice parameters are found to be at room temperature a=3.7696(5) A and c=12.3747(2)more » A. The final reliability indices were: R{sub B}=5.219% and {chi}{sup 2}=3.47. Four probe electrical resistivity measurements were performed versus temperature in the range 294-579 K. A semiconducting behaviour over the whole range of temperature, with a conductivity maximum of 0.4 S cm{sup -1} is observed at 510 K. - Graphical abstract: DySr{sub 5}Ni{sub 2.4}Cu{sub 0.6}O{sub 12-{delta}} exhibits a semi-conducting behaviour over the whole temperature range 294-579 K with a conductivity maximum of 0.4 S cm{sup -1} at 510 K. Highlights: > We described our attempts to synthesize the pure compound DySr{sub 5}Ni{sub 2.4}Cu{sub 0.6}O{sub 12-{delta}}. > Product was characterized by XRD and electrical resistivity measurements. > Iodometric titration was used for the analysis of the oxygen nonstoichiometry. > Calculated tolerance factor was included in the tetragonal symmetry stability range. > Compound exhibits a semi-conducting behaviour over the whole temperature range 294-579 K.« less

Electron paramagnetic resonance in Cu-doped ZnO

NASA Astrophysics Data System (ADS)

Buchheit, R.; Acosta-Humánez, F.; Almanza, O.

2016-04-01

In this work, ZnO and Cu-doped ZnO nanoparticles (Zn1-xCuxO, x = 3%), with a calcination temperature of 500∘C were synthesized using the sol-gel method. The particles were analyzed using atomic absorption spectroscopy (AAS), X-ray diffraction (XRD) and electron paramagnetic resonance (EPR) at X-band, measurement in a temperature range from 90 K to room temperature. AAS confirmed a good correspondence between the experimental doping concentration and the theoretical value. XRD reveals the presence of ZnO phase in hexagonal wurtzite structure and a nanoparticle size for the samples synthesized. EPR spectroscopy shows the presence of point defects in both samples with g-values of g = 1.959 for shallow donors and g = 2.004 for ionized vacancies. It is important when these materials are required have been used as catalysts, as suggested that it is not necessary prepare them at higher temperature. A simulation of the Cu EPR signal using an anisotropic spin Hamiltonian was performed and showed good coincidence with the experimental spectra. It was shown that Cu2+ ions enter interstitial octahedral sites of orthorhombic symmetry in the wurtzite crystal structure. Temperature dependence of the EPR linewidth and signal intensity shows a paramagnetic behavior of the sample in the measurement range. A Néel temperature TN = 78 ± 19 K was determined.

Structural, magnetic and dielectric properties of polyaniline/MnCoFe2O4 nanocomposites

NASA Astrophysics Data System (ADS)

Chitra, Palanisamy; Muthusamy, Athianna; Jayaprakash, Rajan

2015-12-01

Ferromagnetic PANI containing MnCoFe2O4 nanocomposites were synthesized by in-situ chemical polymerization of aniline incorporated MnCoFe2O4 nanoparticles (20%, 10% w/w of fine powders) with and without ultrasonic treatment. The MnCoFe2O4 nanoparticles were synthesized by auto combustion method. The PANI/MnCoFe2O4 nanocomposites were characterized with Fourier transform infrared (FTIR), X-ray diffraction (XRD), Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The average particle size of the resulting PANI/MnCoFe2O4 nanocomposites was confirmed from the TEM and XRD analysis. The structure and morphology of the composites were confirmed by FT-IR spectroscopy, XRD and SEM. In addition, the electrical and magnetic properties of the nanocomposites were investigated. The PANI/MnCoFe2O4 nanocomposites under applied magnetic field exhibited the hysteresis loops of ferromagnetic nature at room temperature. The variation of Dielectric constant, Dielectric loss, and AC conductivity of PANI/MnCoFe2O4 nanocomposites at room temperature as a function of frequency in the range 50 Hz-5 MHz has been studied. Effect of ultrasonication on the PANI/MnCoFe2O4 nanocomposites was also investigated.

Effect of grain size on the magnetic properties of superparamagnetic Ni 0.5Zn 0.5Fe 2O 4 nanoparticles by co-precipitation process

NASA Astrophysics Data System (ADS)

Chen, D. G.; Tang, X. G.; Wu, J. B.; Zhang, W.; Liu, Q. X.; Jiang, Y. P.

2011-06-01

Ni 0.5Zn 0.5Fe 2O 4 (NZFO) spinel-type nanoparticles were directly fabricated by the chemical co-precipitation process using metal nitrate and acetate as precursors since nitrogen and carbon would be taken away in the forms of oxynitride and oxycarbide, respectively, after the precursors were annealed and then investigated in detail by employing X-ray diffraction (XRD), magnetic measurement and Raman spectroscopy. XRD analysis indicates that the as-prepared nanocrystals are all of a pure cubic spinel structure with their sizes ranging from 20.8 to 53.3 nm, as well as peaks of some samples shifting to lower angles due to lattice expansion. Calculations from the derived XRD data indicate that the activation energy is 30.83 kJ/mol. The magnetic measurements show that these samples are superparamagnetic. The saturation magnetization increases with annealing temperature, which may be explained by super-exchange interactions of Fe ions occurring at A- and B-sites. The variation of coercivity with particle size is interpreted on the basis of domain structure and crystal anisotropy. Furthermore, these nanoparticles exhibit a redshift phenomenon at lower temperatures seen in the Raman spectra, which could be related to ionic substitution.

Phase Evaluation in Al2O3 Fiber-Reinforced Ti2AlC During Sintering in the 1300 degrees C-1500 degrees C Temperature Range

DTIC Science & Technology

2011-01-01

composition: 97% Al2O3 and 3% SiO2] fibers. In both cases, the fibers were chopped with a razor blade into 5 cm lengths. Mixing of the powder and...the presence of XRD amorphous Ti- aluminides (see below) or other phases cannot be ruled out at this juncture. When the XRD spectrum of the as-received...not shown). No peaks belonging to any Ti- aluminide were found suggesting them to be amorphous or at most nano-crystalline. A typical TEM micrograph of

Preparation of Cu-doped nickel oxide thin films and their properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gowthami, V.; Meenakshi, M.; Anandhan, N.

2014-04-24

Copper doped Nickel oxide film was preferred on glass substrate by simple nebulizer technique keeping the substrate temperature at 350°C and characterized by X-ray diffraction (XRD), Photoluminescence (PL) and Four probe resistivity measurements. XRD studies indicated cubic structure and the crystallites are preferentially oriented along the [111] direction. Interesting results have been obtained from the study of PL spectra. A peak corresponding to 376nm in the emission spectra for 0%, 5% and 10% copper doped samples. The samples show sharp and strong UV emission corresponding to the near band edge emission under excitation of 275nm.

Influences of P doping on magnetic phase transition and structure in MnCoSi ribbon

NASA Astrophysics Data System (ADS)

Du, Qian-Heng; Chen, Guo-Fu; Yang, Wen-Yun; Hua, Mu-Xin; Du, Hong-Lin; Wang, Chang-Sheng; Liu, Shun-Quan; Hang, Jing-Zhi; Zhou, Dong; Zhang, Yan; Yan, Jin-Bo

2015-06-01

The structure and magnetic properties of MnCoSi1- x Px (x = 0.05-0.50) are systematically investigated. With P content increasing, the lattice parameter a increases monotonically while both b and c decrease. At the same time, the temperature of metamagnetic transition from a low-temperature non-collinear ferromagnetic state to a high-temperature ferromagnetic state decreases and a new magnetic transition from a higher-magnetization ferromagnetic state to a lower-magnetization ferromagnetic state is observed in each of these compounds for the first time. This is explained by the changes of crystal structure and distance between Mn and Si atoms with the increase of temperature according to the high-temperature XRD result. The metamagnetic transition is found to be a second-order magnetic transition accompanied by a low inversed magnetocaloric effect (1.0 J·kg-1·K-1 at 5 T) with a large temperature span (190 K at 5 T) compared with the scenario of MnCoSi. The changes in the order of metamagnetic transition and structure make P-doped MoCoSi compounds good candidates for the study of magnetoelastic coupling and the modulation of magnetic phase transition. Project supported by the National Natural Science Foundation of China (Grant No. 11275013), the Fund from the National Physics Laboratory, China Academy of Engineering Physics (Grant No. 2013DB01), and the National Key Basic Research Program of China (Grant No. 2010CB833104).

Setup for in situ x-ray diffraction study of swift heavy ion irradiated materials.

PubMed

Kulriya, P K; Singh, F; Tripathi, A; Ahuja, R; Kothari, A; Dutt, R N; Mishra, Y K; Kumar, Amit; Avasthi, D K

2007-11-01

An in situ x-ray diffraction (XRD) setup is designed and installed in the materials science beam line of the Pelletron accelerator at the Inter-University Accelerator Centre for in situ studies of phase change in swift heavy ion irradiated materials. A high vacuum chamber with suitable windows for incident and diffracted X-rays is integrated with the goniometer and the beamline. Indigenously made liquid nitrogen (LN2) temperature sample cooling unit is installed. The snapshots of growth of particles with fluence of 90 MeV Ni ions were recorded using in situ XRD experiment, illustrating the potential of this in situ facility. A thin film of C60 was used to test the sample cooling unit. It shows that the phase of the C60 film transforms from a cubic lattice (at room temperature) to a fcc lattice at around T=255 K.

Intermediate valence to Kondo behaviour in Ce(Pt1-xIrx)2Si2 (0≤x≤1)

NASA Astrophysics Data System (ADS)

Tchoula Tchokonté, M. B.; du Plessis, P. de V.; Kaczorowski, D.

2009-10-01

Measurements of X-ray diffraction (XRD), resistivity ( ρ(T)), magnetic susceptibility ( χ(T)) and magnetization ( σ(μ0H)) are reported for the polycrystalline Ce(Pt1-xIrx)2Si2 alloy system. The unit cell volume derived from the XRD results deviates from Vegard's rule around x=0.2-0.3. χ(T) measurements show a Curie-Weiss behaviour at high temperatures for the x= 0, 0.1 and 0.2 alloys whereas the alloys with x≥0.4 exhibit broad maxima in χ(T) at intermediate temperature (e.g. at 170 K for x=0.4). The latter behaviour due to valence fluctuations as described by Sales and Wohlleben. ρ(T) data indicate Kondo lattice behaviour for x≤0.2 and fluctuating valency for x≥0.3. σ(μ0H) data indicate metamagnetic behaviour for the x=0.4 alloy.

Hydrothermal formation of tobermorite studied by in situ X-ray diffraction under autoclave condition.

PubMed

Kikuma, Jun; Tsunashima, Masamichi; Ishikawa, Tetsuji; Matsuno, Shin-ya; Ogawa, Akihiro; Matsui, Kunio; Sato, Masugu

2009-09-01

Hydrothermal formation of tobermorite from a pre-cured cake has been investigated by transmission X-ray diffraction (XRD) using high-energy X-rays from a synchrotron radiation source in combination with a newly designed autoclave cell. The autoclave cell has a large and thin beryllium window for wide-angle X-ray diffraction; nevertheless, it withstands a steam pressure of more than 1.2 MPa, which enables in situ XRD measurements in a temperature range of 373 to 463 K under a saturated steam pressure. Formation and/or decomposition of several components has been successfully observed during 7.5 h of reaction time. From the intensity changes of the intermediate materials, namely non-crystalline C-S-H and hydroxylellestadite, two pathways for tobermorite formation have been confirmed. Thus, the newly developed autoclave cell can be used for the analyses of reaction mechanisms under specific atmospheres and temperatures.

Structural and Mössbauer analysis of pure and Ce-Dy doped cobalt ferrite nanoparticles

NASA Astrophysics Data System (ADS)

Hashim, Mohd.; Meena, Sher Singh; Kumar, Shalendra; Ahmed, Ateeq; Bhatt, Pramod

2018-05-01

Ce and Dy doped Cobalt ferrites with the chemical composition CoCexDyxFe2-2xO4 (x = 0.00 and 0.04) were synthesized via the chemical route using citrate-gel auto-combustion method. The structural analysis has been carried out with the help of x-ray diffraction (XRD). Formation of spinel cubic structure of the ferrites was confirmed by XRD analysis. Mössbauer spectra were recorded for both samples at room temperature. Presence of the well resolved sextet spectra corresponding to A and B sub-lattice clearly shows that both the samples have ferrimagnetic ordering at room temperature. Isomer shift observed from fitting of the Mössbauer spectra infers that Fe3+ ions are in high valence state. The decrease in the hyperfine field due to the doping of Ce and Dy clearly showed that magnetic interactions diluted due to the doping of Ce and Dy ions.

Growth of high quality and large-sized Rb 0.3MoO 3 single crystals by molten salt electrolysis method

NASA Astrophysics Data System (ADS)

Wang, Junfeng; Xiong, Rui; Yi, Fan; Yin, Di; Ke, Manzhu; Li, Changzhen; Liu, Zhengyou; Shi, Jing

2005-05-01

High quality and large-sized Rb 0.3MoO 3 single crystals were synthesized by molten salt electrolysis method. X-ray diffraction (XRD) patterns and rocking curves, as well as the white beam Laue diffraction of X-ray images show the crystals grown by this method have high quality. The lattice constants evaluated from XRD patterns are a0=1.87 nm, b0=0.75 nm, c0=1.00 nm, β=118.83∘. The in situ selected area electron diffraction (SAED) patterns along the [101¯], [11¯1¯] and [103¯] zone axes at room temperature indicate that the Rb 0.3MoO 3 crystal possess perfect C-centered symmetry. Temperature dependence of the resistivity shows this compound undergoes a metal to semiconductor transition at 183 K.

Rietveld analysis of the effect of annealing atmosphere on phase evolution of nanocrystalline TiO2 powders.

PubMed

Salari, M; Rezaee, M; Chidembo, A T; Konstantinov, K; Liu, H K

2012-06-01

The structural evolution of nanocrystalline TiO2 was studied by X-ray diffraction (XRD) and the Rietveld refinement method (RRM). TiO2 powders were prepared by the sol-gel technique. Post annealing of as-synthesized powders in the temperature range from 500 degrees C to 800 degrees C under air and argon atmospheres led to the formation of TiO2 nanoparticles with mean crystallite size in the range of 37-165 nm, based on the Rietveld refinement results. It was found that the phase structure, composition, and crystallite size of the resulting particles were dependent on not only the annealing temperature, but also the annealing atmosphere. Rietveld refinement of the XRD data showed that annealing the powders under argon atmosphere promoted the polymorphic phase transformation from anatase to rutile. Field emission scanning electron microscopy (FESEM) was employed to investigate the morphology and size of the annealed powders.

Effect of thickness on optoelectrical properties of Nb-doped indium tin oxide thin films deposited by RF magnetron sputtering

NASA Astrophysics Data System (ADS)

Li, Shi-na; Ma, Rui-xin; Ma, Chun-hong; Li, Dong-ran; Xiao, Yu-qin; He, Liang-wei; Zhu, Hong-min

2013-05-01

Niobium-doped indium tin oxide (ITO:Nb) thin films are prepared on glass substrates with various film thicknesses by radio frequency (RF) magnetron sputtering from one piece of ceramic target material. The effects of thickness (60-360 nm) on the structural, electrical and optical properties of ITO: Nb films are investigated by means of X-ray diffraction (XRD), ultraviolet (UV)-visible spectroscopy, and electrical measurements. XRD patterns show the highly oriented (400) direction. The lowest resistivity of the films without any heat treatment is 3.1×10-4Ω·cm-1, and the resistivity decreases with the increase of substrate temperature. The highest Hall mobility and carrier concentration are 17.6 N·S and 1.36×1021 cm-3, respectively. Band gap energy of the films depends on substrate temperature, which varies from 3.48 eV to 3.62 eV.

Formation of silicon nanocrystals in sapphire by ion implantation and the origin of visible photoluminescence

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yerci, S.; Serincan, U.; Dogan, I.

2006-10-01

Silicon nanocrystals, average sizes ranging between 3 and 7 nm, were formed in sapphire matrix by ion implantation and subsequent annealing. Evolution of the nanocrystals was detected by Raman spectroscopy and x-ray diffraction (XRD). Raman spectra display that clusters in the matrix start to form nanocrystalline structures at annealing temperatures as low as 800 deg. C in samples with high dose Si implantation. The onset temperature of crystallization increases with decreasing dose. Raman spectroscopy and XRD reveal gradual transformation of Si clusters into crystalline form. Visible photoluminescence band appears following implantation and its intensity increases with subsequent annealing process. Whilemore » the center of the peak does not shift, the intensity of the peak decreases with increasing dose. The origin of the observed photoluminescence is discussed in terms of radiation induced defects in the sapphire matrix.« less

Setup for in situ x-ray diffraction study of swift heavy ion irradiated materials

NASA Astrophysics Data System (ADS)

Kulriya, P. K.; Singh, F.; Tripathi, A.; Ahuja, R.; Kothari, A.; Dutt, R. N.; Mishra, Y. K.; Kumar, Amit; Avasthi, D. K.

2007-11-01

An in situ x-ray diffraction (XRD) setup is designed and installed in the materials science beam line of the Pelletron accelerator at the Inter-University Accelerator Centre for in situ studies of phase change in swift heavy ion irradiated materials. A high vacuum chamber with suitable windows for incident and diffracted X-rays is integrated with the goniometer and the beamline. Indigenously made liquid nitrogen (LN2) temperature sample cooling unit is installed. The snapshots of growth of particles with fluence of 90MeV Ni ions were recorded using in situ XRD experiment, illustrating the potential of this in situ facility. A thin film of C60 was used to test the sample cooling unit. It shows that the phase of the C60 film transforms from a cubic lattice (at room temperature) to a fcc lattice at around T =255K.

Characterization of mineral phases of agricultural soil samples of Colombian coffee using Mössbauer spectroscopy and X-ray diffraction

NASA Astrophysics Data System (ADS)

Rodríguez, Humberto Bustos; Lozano, Dagoberto Oyola; Martínez, Yebrayl Antonio Rojas; Pinilla, Marlene Rivera; Alcázar, German Antonio Pérez

2012-03-01

Soil chemical analysis, X-ray diffraction (XRD) and Mössbauer spectrometry (MS) of 57Fe were used to characterize mineral phases of samples taken from the productive layer (horizon A) of agricultural coffee soil from Tolima (Colombia). Chemical analysis shows the chemical and textural parameters of samples from two different regions of Tolima, i.e., Ibagué and Santa Isabel. By XRD phases like illite (I), andesine (A) and quartz (Q) in both samples were identified. The quantity of these phases is different for the two samples. The MS spectra taken at room temperature were adjusted by using five doublets, three of them associated to Fe + 3 type sites and the other two to Fe + 2 type sites. According to their isomer shift and quadrupole splitting the presence of phases like illite (detected by DRX), nontronite and biotite (not detected by XRD) can be postulated.

Development of Processing Techniques for Advanced Thermal Protection Materials

NASA Technical Reports Server (NTRS)

Selvaduray, Guna; Cox, Michael; Srinivasan, Vijayakumar

1997-01-01

Thermal Protection Materials Branch (TPMB) has been involved in various research programs to improve the properties and structural integrity of the existing aerospace high temperature materials. Specimens from various research programs were brought into the analytical laboratory for the purpose of obtaining and refining the material characterization. The analytical laboratory in TPMB has many different instruments which were utilized to determine the physical and chemical characteristics of materials. Some of the instruments that were utilized by the SJSU students are: Scanning Electron Microscopy (SEM), Energy Dispersive X-ray analysis (EDX), X-ray Diffraction Spectrometer (XRD), Fourier Transform-Infrared Spectroscopy (FTIR), Ultra Violet Spectroscopy/Visible Spectroscopy (UV/VIS), Particle Size Analyzer (PSA), and Inductively Coupled Plasma Atomic Emission Spectrometer (ICP-AES). The above mentioned analytical instruments were utilized in the material characterization process of the specimens from research programs such as: aerogel ceramics (I) and (II), X-33 Blankets, ARC-Jet specimens, QUICFIX specimens and gas permeability of lightweight ceramic ablators. In addition to analytical instruments in the analytical laboratory at TPMB, there are several on-going experiments. One particular experiment allows the measurement of permeability of ceramic ablators. From these measurements, physical characteristics of the ceramic ablators can be derived.

Co-Precipitation Synthesis and Characterization of SrBi2Ta2O9 Ceramic

NASA Astrophysics Data System (ADS)

Afqir, Mohamed; Tachafine, Amina; Fasquelle, Didier; Elaatmani, Mohamed; Carru, Jean-Claude; Zegzouti, Abdelouahad; Daoud, Mohamed

2018-04-01

Strontium bismuth tantalate (SrBi2Ta2O9) was synthesized by a co-precipitation method. The sample was characterized by x-ray powder diffraction patterns (XRD), Fourier-transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The results of the dielectric properties are reported at room temperature. No secondary phases were found while heating the powder at 850°C and the pure SrBi2Ta2O9 phase was formed, as revealed by XRD. The characteristic bands for SrBi2Ta2O9 were observed by FTIR at approximately 619 cm-1 and 810 cm-1. SEM micrographs for the sample displayed thin plate-like grains. The grain size was less than 1 μm and the crystallite size of about 24 nm. Dielectric response at room temperature shows that the SrBi2Ta2O9 ceramic has low loss values, and the flattening of the dielectric constant at higher frequencies. The observed Curie temperature is comparable with those reported in the literature.

Synthesis and characterization of FeSe1-xTex (x=0, 0.5, 1) superconductors

NASA Astrophysics Data System (ADS)

Zargar, Rayees A.; Hafiz, A. K.; Awana, V. P. S.

2015-08-01

In this study, FeTe1-xSex (x=0,0.5,1) samples were prepared by conventional solid state reaction method and investigated by powder XRD, SEM, Raman and resistivity measurement techniques to reveal the effect of tellurium (Te) substitution in FeSe matrix. Rietveld analysis was performed on room temperature recorded, X-ray diffraction (XRD) patterns of pure FeSe, FeTe and FeSe0.5Te0.5 which shows that all the compounds are crystallized in a tetragonal structure. SEM images show the dense surface morphology. Raman spectra recorded in the range from 100 to 700 cm-1 at ambient temperature has been interpreted by P4/nmm space group of the lattice. The variation in intensity and shift in peak positions of some phonon modes has been discussed on the basis of variation in crystalline field effect by substituting Te in FeSe lattice. The resistivity versus temperature curves reveals that FeSe becomes superconductor at 7 K and FeSe0.5Te0.5 shows superconductivity below 14 K while FeTe is non-superconducting compound.

Y 3-xMg 2AlSi 2O 12: Cex3+ phosphors - prospective for warm-white light emitting diodes

NASA Astrophysics Data System (ADS)

Katelnikovas, Arturas; Bareika, Tomas; Vitta, Pranciškus; Jüstel, Thomas; Winkler, Holger; Kareiva, Aivaras; Žukauskas, Artūras; Tamulaitis, Gintautas

2010-07-01

Y 3-xMg 2AlSi 2O 12: Cex3+ (YMASG:Ce) phosphors were synthesized by sol-gel combustion technique at different temperatures from 1400 to 1550 °C. Samples with x = 0.015, 0.03, 0.045, and 0.06 were fabricated and characterized using powder X-ray diffraction (XRD), photoluminescence spectroscopy, and fluorescence lifetime measurements in frequency domain. XRD patterns confirmed single-phase garnet crystal structure for all the samples independently of their substitutional level and annealing temperature. In respect to Y 3Al 5O 12:Ce 3+ (YAG:Ce) phosphor, which was synthesized for comparison by a different sol-gel procedure, the photoluminescence band of these garnets is red shifted, indicating a prospective for application of this novel phosphor in warm-white light emitting diodes (LEDs). The luminescence decays bi-exponentially. The main component has a characteristic decay time decreasing from 72 to of 50 ns with increasing sintering temperature and cerium content, while ˜2% of the excitation decays with a characteristic decay time of ˜8 ns.

Influence of Casting Section Thickness on Fatigue Strength of Austempered Ductile Iron

NASA Astrophysics Data System (ADS)

Olawale, J. O.; Ibitoye, S. A.

2017-10-01

The influence of casting section thickness on fatigue strength of austempered ductile iron was investigated in this study. ASTM A536 65-45-12 grade of ductile iron was produced, machined into round samples of 10, 15, 20 and 25 mm diameter, austenitized at a temperature of 820 °C, quenched into an austempering temperature (TA) of 300 and 375 °C and allowed to be isothermally transformed at these temperatures for a fixed period of 2 h. From the samples, fatigue test specimens were machined to conform to ASTM E-466. Scanning electron microscopy (SEM) and x-ray diffraction (XRD) methods were used to characterize microstructural morphology and phase distribution of heat-treated samples. The fatigue strength decreases as the section thickness increases. The SEM image and XRD patterns show a matrix of acicular ferrite and carbon-stabilized austenite with ferrite coarsening and volume fraction of austenite reducing as the section thickness increases. The study concluded that the higher the value of carbon-stabilized austenite the higher the fatigue strength while it decreases as the ausferrite structure becomes coarse.

Compaction and sintering behaviors of a Nd-Fe-B permanent magnet alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chin, T.; Hung, M.; Tsai, D.

1988-11-15

Extensive x-ray diffraction (XRD) and magnetic measurements were done on Nd/sub 15/ Fe/sub 77/ B/sub 8/ magnet alloy green compacts after cold isostatic pressing following a pulsed 2-T field (CIP) and die-pressing under a static 1.2-T perpendicular field (DP1) or parallel field (DP2), and on those after sintering. An alignment factor F, through the calculation of the integrated diffraction intensity ratio of the XRD patterns, was adopted as the effectiveness of magnetic alignment. At the green compact state, DP1 has the best alignment while CIP the worst. However, after sintering the alignment factor was such that CIP>DPI>DP2, the same ordermore » as the magnetic properties. Three mechanisms were proposed for the evolution of the alignment factor at different stages of sintering, i.e., that both the appearance of a liquid phase at low temperatures and preferred grain growth at high temperatures enhance F, while recrystallization at intermediate temperatures deteriorates F. CIP results in less-defect green compact, hence less recrystallization, leading to better resultant alignment« less

Facile Synthesis of Calcium Borate Nanoparticles and the Annealing Effect on Their Structure and Size

PubMed Central

Erfani, Maryam; Saion, Elias; Soltani, Nayereh; Hashim, Mansor; Wan Abdullah, Wan Saffiey B.; Navasery, Manizheh

2012-01-01

Calcium borate nanoparticles have been synthesized by a thermal treatment method via facile co-precipitation. Differences of annealing temperature and annealing time and their effects on crystal structure, particle size, size distribution and thermal stability of nanoparticles were investigated. The formation of calcium borate compound was characterized by X-ray diffraction (XRD) and Fourier Transform Infrared spectroscopy (FTIR), Transmission electron microscopy (TEM), and Thermogravimetry (TGA). The XRD patterns revealed that the co-precipitated samples annealed at 700 °C for 3 h annealing time formed an amorphous structure and the transformation into a crystalline structure only occurred after 5 h annealing time. It was found that the samples annealed at 900 °C are mostly metaborate (CaB2O4) nanoparticles and tetraborate (CaB4O7) nanoparticles only observed at 970 °C, which was confirmed by FTIR. The TEM images indicated that with increasing the annealing time and temperature, the average particle size increases. TGA analysis confirmed the thermal stability of the annealed samples at higher temperatures. PMID:23203073

Preparation, Structural and Dielectric Properties of Solution Grown Polyvinyl Alcohol(PVA) Film

NASA Astrophysics Data System (ADS)

Nangia, Rakhi; Shukla, Neeraj K.; Sharma, Ambika

2017-08-01

Flexible dielectrics with high permittivity have been investigated extensively due to their applications in electronic industry. In this work, structural and electrical characteristics of polymer based film have been analysed. Poly vinyl alcohol (PVA) film was prepared by solution casting method. X-ray diffraction (XRD) characterization technique is used to investigate the structural properties. The semi-crystalline nature has been determined by the analysis of the obtained XRD pattern. Electrical properties of the synthesized film have been analysed from the C-V and I-V curves obtained at various frequencies and temperatures. Low conductivity values confirm the insulating behaviour of the film. However, it is found that conductivity increases with temperature. Also, the dielectric permittivity is found to be higher at lower frequencies and higher temperatures, that proves PVA to be an excellent dielectric material which can be used in interface electronics. Dielectric behaviour of the film has been explained based on dipole orientations to slow and fast varying electric field. However further engineering can be done to modulate the structural, electrical properties of the film.

Phase separation in SiGe nanocrystals embedded in SiO{sub 2} matrix during high temperature annealing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mogaddam, N. A. P.; Turan, R.; Alagoz, A. S.

2008-12-15

SiGe nanocrystals have been formed in SiO{sub 2} matrix by cosputtering Si, Ge, and SiO{sub 2} independently on Si substrate. Effects of the annealing time and temperature on structural and compositional properties are studied by transmission electron microscopy, x-ray diffraction (XRD), and Raman spectroscopy measurements. It is observed that Ge-rich Si{sub (1-x)}Ge{sub x} nanocrystals do not hold their compositional uniformity when annealed at high temperatures for enough long time. A segregation process leading to separation of Ge and Si atoms from each other takes place. This process has been evidenced by a double peak formation in the XRD and Ramanmore » spectra. We attributed this phase separation to the differences in atomic size, surface energy, and surface diffusion disparity between Si and Ge atoms leading to the formation of nonhomogenous structure consist of a Si-rich SiGe core covered by a Ge-rich SiGe shell. This experimental observation is consistent with the result of reported theoretical and simulation methods.« less

Atomic-scale investigation and magnetic properties of Cu80Co20 nanowires

NASA Astrophysics Data System (ADS)

Hannour, A.; Lardé, R.; Jean, M.; Bran, J.; Pareige, P.; Le Breton, J. M.

2011-09-01

Cu80Co20 granular alloy nanowires were synthesized by electrodeposition method and investigated by x-ray diffraction (XRD), Laser Assisted Wide Angle Tomographic Atom Probe (LAWATAP), and SQUID magnetometry. XRD results reveal the existence of a fcc Cu matrix and fcc Co-rich nanograins, with a preferred orientation along the [200] direction (perpendicular to the substrate surface). The Co-rich nanograins could be coherent with the Cu matrix. 3D reconstructions of a nano-sized volume, obtained by LAWATAP, reveal the heterogeneous aspect of the Cu80Co20 nanowires: Co-rich nanoclusters with size between 2 and 10 nm are detected, and the presence of Cu and Co oxides is evidenced. Magnetization measurements indicate that the Co-rich nanoclusters are superparamagnetic, with a blocking temperature that extends up to, at least, room temperature. The presence of ferromagnetic domains at room temperature indicates that some Co-rich nanoclusters are correlated within a volume that corresponds to a so-called interacting superparamagnetic phase. As a matter of fact, by LAWATAP atomic-scale analysis, a very good correlation is obtained between microstructure and magnetic properties.

Surfactant Mediated Growth of Co on MgO(111)

NASA Astrophysics Data System (ADS)

Johnson-Steigelman, H. Trevor; Parihar, Somendra S.; Lyman, Paul F.

2010-03-01

Monolayer films of Co were deposited using an electrostatic electron-beam evaporator on single-crystal MgO(111)- √3 x√3 R 30^o substrates held at room temperature, with subsequent annealing of temperatures 400 C to 800 C. These films were characterized using low-energy electron diffraction (LEED), x-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and x-ray diffraction (XRD). After short anneals of 400 C, AFM, LEED, and XPS suggest that islanding has occurred at the surface. XPS and XRD indicate the presence of elemental Co. 1-2 ML films of Ag were examined as a potential surfactant to aid in the growth of smooth Co films. Despite the fact that Ag itself formed islands, it was found that the presence of Ag did have a surfactant effect upon the thin-film growth of Co on Ag/MgO(111)- √3 x√3 R 30^o. Co islands were still present, but much more smooth than islands formed without Ag. XPS and AFM suggest strongly that Ag floated to the top of these samples at temperatures above 400 ^oC.

Glass transition in ferroic glass K x (ND4)1-x D2PO4: a complete x-ray diffraction line shape analysis

NASA Astrophysics Data System (ADS)

Ranjan Choudhury, Rajul; Chitra, R.; Jayakrishnan, V. B.

2016-03-01

Quenching of dynamic disorder in glassy systems is termed as the glass transition. Ferroic glasses belong to the class of paracrystalline materials having crystallographic order in-between that of a perfect crystal and amorphous material, a classic example of ferroic glass is the solid solution of ferroelectric deuterated potassium dihydrogen phosphate and antiferroelectric deuterated ammonium dihydrogen phosphate. Lowering temperature of this ferroic glass can lead to a glass transition to a quenched disordered state. The subtle atomic rearrangement that takes place at such a glass transition can be revealed by careful examination of the temperature induced changes occurring in the x-ray powder diffraction (XRD) patterns of these materials. Hence we report here results of a complete diffraction line shape analysis of the XRD patterns recorded at different temperatures from deuterated mixed crystals DK x A1-x DP with mixing concentration x ranging as 0 < x < 1. Changes observed in diffraction peak shapes have been explained on the basis of structural rearrangements induced by changing O-D-O hydrogen bond dynamics in these paracrystals.

Polyaniline-Cadmium Ferrite Nanostructured Composite for Room-Temperature Liquefied Petroleum Gas Sensing

NASA Astrophysics Data System (ADS)

Kotresh, S.; Ravikiran, Y. T.; Tiwari, S. K.; Vijaya Kumari, S. C.

2017-08-01

We introduce polyaniline-cadmium ferrite (PANI-CdFe2O4) nanostructured composite as a room-temperature-operable liquefied petroleum gas (LPG) sensor. The structure of PANI and the composite prepared by chemical polymerization was characterized by Fourier-transform infrared (FT-IR) spectroscopy, x-ray diffraction (XRD) analysis, and field-emission scanning electron microscopy. Comparative XRD and FT-IR analysis confirmed CdFe2O4 embedded in PANI matrix with mutual interfacial interaction. The nanostructure of the composite was confirmed by transmission electron microscopy. A simple LPG sensor operable at room temperature, exclusively based on spin-coated PANI-CdFe2O4 nanocomposite, was fabricated with maximum sensing response of 50.83% at 1000 ppm LPG. The response and recovery time of the sensor were 50 s and 110 s, respectively, and it was stable over a period of 1 month with slight degradation of 4%. The sensing mechanism is discussed on the basis of the p- n heterojunction barrier formed at the interface of PANI and CdFe2O4.

Quantifying Morphological Features of α-U3O8 with Image Analysis for Nuclear Forensics.

PubMed

Olsen, Adam M; Richards, Bryony; Schwerdt, Ian; Heffernan, Sean; Lusk, Robert; Smith, Braxton; Jurrus, Elizabeth; Ruggiero, Christy; McDonald, Luther W

2017-03-07

Morphological changes in U 3 O 8 based on calcination temperature have been quantified enabling a morphological feature to serve as a signature of processing history in nuclear forensics. Five separate calcination temperatures were used to synthesize α-U 3 O 8 , and each sample was characterized using powder X-ray diffraction (p-XRD) and scanning electron microscopy (SEM). The p-XRD spectra were used to evaluate the purity of the synthesized U-oxide; the morphological analysis for materials (MAMA) software was utilized to quantitatively characterize the particle shape and size as indicated by the SEM images. Analysis comparing the particle attributes, such as particle area at each of the temperatures, was completed using the Kolmogorov-Smirnov two sample test (K-S test). These results illustrate a distinct statistical difference between each calcination temperature. To provide a framework for forensic analysis of an unknown sample, the sample distributions at each temperature were compared to randomly selected distributions (100, 250, 500, and 750 particles) from each synthesized temperature to determine if they were statistically different. It was found that 750 particles were required to differentiate between all of the synthesized temperatures with a confidence interval of 99.0%. Results from this study provide the first quantitative morphological study of U-oxides, and reveals the potential strength of morphological particle analysis in nuclear forensics by providing a framework for a more rapid characterization of interdicted uranium oxide samples.

Characterization of nanocrystalline ZnO:Al films by sol-gel spin coating method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gareso, P. L., E-mail: pgareso@gmail.com; Rauf, N., E-mail: pgareso@gmail.com; Juarlin, E., E-mail: pgareso@gmail.com

2014-09-25

Nanocrystalline ZnO films doped with aluminium by sol-gel spin coating method have been investigated using optical transmittance UV-Vis and X-ray diffraction (X-RD) measurements. ZnO films were prepared using zinc acetate dehydrate (Zn(CH{sub 3}COO){sub 2}@@‡2H{sub 2}O), ethanol, and diethanolamine (DEA) as a starting material, solvent, and stabilizer, respectively. For doped films, AlCl{sub 3} was added to the mixture. The ZnO:Al films were deposited on a transparent conductive oxide (TCO) substrate using spin coating technique at room temperature with a rate of 3000 rpm in 30 sec. The deposited films were annealed at various temperatures from 400°C to 600°C during 60 minutes.more » The transmittance UV-Vis measurement results showed that after annealing at 400°C, the energy band gap profile of nanocrystalline ZnO:Al film was a blue shift. This indicated that the band gap of ZnO:Al increased after annealing due to the increase of crystalline size. As the annealing temperature increased the bandgap energy was a constant. In addition to this, there was a small oscillation occurring after annealing compared to the as–grown samples. In the case of X-RD measurements, the crystalinity of the films were amorphous before annealing, and after annealing the crystalinity became enhance. Also, X-RD results showed that structure of nanocrystalline ZnO:Al films were hexagonal polycrystalline with lattice parameters are a = 3.290 Å and c = 5.2531 Å.« less

Thermal decomposition of dolomite under CO2: insights from TGA and in situ XRD analysis.

PubMed

Valverde, Jose Manuel; Perejon, Antonio; Medina, Santiago; Perez-Maqueda, Luis A

2015-11-28

Thermal decomposition of dolomite in the presence of CO2 in a calcination environment is investigated by means of in situ X-ray diffraction (XRD) and thermogravimetric analysis (TGA). The in situ XRD results suggest that dolomite decomposes directly at a temperature around 700 °C into MgO and CaO. Immediate carbonation of nascent CaO crystals leads to the formation of calcite as an intermediate product of decomposition. Subsequently, decarbonation of this poorly crystalline calcite occurs when the reaction is thermodynamically favorable and sufficiently fast at a temperature depending on the CO2 partial pressure in the calcination atmosphere. Decarbonation of this dolomitic calcite occurs at a lower temperature than limestone decarbonation due to the relatively low crystallinity of the former. Full decomposition of dolomite leads also to a relatively low crystalline CaO, which exhibits a high reactivity as compared to limestone derived CaO. Under CO2 capture conditions in the Calcium-Looping (CaL) process, MgO grains remain inert yet favor the carbonation reactivity of dolomitic CaO especially in the solid-state diffusion controlled phase. The fundamental mechanism that drives the crystallographic transformation of dolomite in the presence of CO2 is thus responsible for its fast calcination kinetics and the high carbonation reactivity of dolomitic CaO, which makes natural dolomite a potentially advantageous alternative to limestone for CO2 capture in the CaL technology as well as SO2in situ removal in oxy-combustion fluidized bed reactors.

Unpredictable adsorption and visible light induced decolorization of nano rutile for the treatment of crystal violet

NASA Astrophysics Data System (ADS)

Dong, Yanling; Liu, Yang; Lu, Dingze; Zheng, Feng; Fang, Pengfei; Zhang, Haining

2017-04-01

Photocatalysts containing different ratios of anatase and rutile are prepared via heat treatment of Degussa P-25 titania. X-ray diffraction (XRD), Bruuauer-Emmett-Teller (BET), ultraviolet-visible light diffuse reflectance spectra (DRS), Raman spectra (Raman), positron annihilation lifetime spectra (PAL) and temperature-programmed desorption (TPD) are applied to investigate the phase composition of the synthesized catalysts. Using crystal violet (CV) as the target pollutant, the unexpected visible light decolorization of rutile is observed. Despite the decreased specific surface area, the as-synthesized rutile samples exhibit much higher adsorption capability of CV than P-25 does, which in turn leads to improved photoreaction efficiency. Since the rutile samples can't absorb the visible light, the degradation under visible light irradiation is attributed to self-sensitization of CV on the surface of rutile.

Cobalt- and iron-based nanoparticles hosted in SBA-15 mesoporous silica and activated carbon from biomass: Effect of modification procedure

NASA Astrophysics Data System (ADS)

Tsoncheva, Tanya; Genova, Izabela; Paneva, Daniela; Dimitrov, Momtchil; Tsyntsarski, Boyko; Velinov, Nicolay; Ivanova, Radostina; Issa, Gloria; Kovacheva, Daniela; Budinova, Temenujka; Mitov, Ivan; Petrov, Narzislav

2015-10-01

Ordered mesoporous silica of SBA-15 type and activated carbon, prepared from waste biomass (peach stones), are used as host matrix of nanosized iron and cobalt particles. The effect of preparation procedure on the state of loaded nanoparticles is in the focus of investigation. The obtained materials are characterized by Boehm method, low temperature physisorption of nitrogen, XRD, UV-Vis, FTIR, Mossbauer spectroscopy and temperature programmed reduction with hydrogen. The catalytic behaviour of the samples is tested in methanol decomposition. The dispersion, oxidative state and catalytic behaviour of loaded cobalt and iron nanoparticles are successfully tuned both by the nature of porous support and the metal precursor used during the samples preparation. Facile effect of active phase deposition from aqueous solution of nitrate precursors is assumed for activated carbon support. For the silica based materials the catalytic activity could be significantly improved when cobalt acetylacetonate is used during the modification. The complex effect of pore topology and surface functionality of different supports on the active phase formation is discussed.

Synthesis of core-shell structured FAU/SBA-15 composite molecular sieves and their performance in catalytic cracking of polystyrene

NASA Astrophysics Data System (ADS)

Du, Jinlong; Shi, Chunwei; Wu, Wenyuan; Bian, Xue; Chen, Ping; Cui, Qingzhu; Cui, Zhixuan

2017-12-01

Composite molecular sieves, FAU/SBA-15, having core-shell structure were synthesized. The synthesized composite sieves were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDS), pyrolysis fourier transform infrared (Py-FTIR) spectroscopy, temperature programmed desorption spectra (NH3-TPD), UV Raman spectroscopy, nuclear magnetic resonance (NMR) and other techniques. XRD, SEM, TEM, N2 adsorption-desorption, mass spectrometry, NMR and EDS results showed that the composite molecular sieve contained two pore channels. Py-FTIR results showed that the addition of HY molecular sieves improved the acidity of the composite zeolite. The crystallization mechanism during the growth of FAU/SBA-15 shell was deduced from the influence of crystallization time on the synthesis of FAU/SBA-15 core-shell structured composite molecular sieve. HY dissociated partially in H2SO4 solution, and consisted of secondary structural units. This framework structure was more stable than its presence in the isolated form on the same ring or in the absence of Al. Thus it played a guiding role and connected with SBA-15 closely through the Si-O bond. This resulted in the gradual covering of the exterior surface of FAU phase by SBA-15 molecular sieves. The presence of SBA-15 restricted the formation of the other high mass components and increased the selectivity towards ethylbenzene.

In situ flow cell for combined X-ray absorption spectroscopy, X-ray diffraction, and mass spectrometry at high photon energies under solar thermochemical looping conditions

NASA Astrophysics Data System (ADS)

Rothensteiner, Matthäus; Jenni, Joel; Emerich, Hermann; Bonk, Alexander; Vogt, Ulrich F.; van Bokhoven, Jeroen A.

2017-08-01

An in situ/operando flow cell for transmission mode X-ray absorption spectroscopy (XAS), X-ray diffraction (XRD), and combined XAS/XRD measurements in a single experiment under the extreme conditions of two-step solar thermochemical looping for the dissociation of water and/or carbon dioxide was developed. The apparatus exposes materials to relevant conditions of both the auto-reduction and the oxidation sub-steps of the thermochemical cycle at ambient temperature up to 1773 K and enables determination of the composition of the effluent gases by online quadrupole mass spectrometry. The cell is based on a tube-in-tube design and is heated by means of a focusing infrared furnace. It was tested successfully for carbon dioxide splitting. In combined XAS/XRD experiments with an unfocused beam, XAS measurements were performed at the Ce K edge (40.4 keV) and XRD measurements at 64.8 keV and 55.9 keV. Furthermore, XRD measurements with a focused beam at 41.5 keV were carried out. Equimolar ceria-hafnia was auto-reduced in a flow of argon and chemically reduced in a flow of hydrogen/helium. Under reducing conditions, all cerium(iv) was converted to cerium(iii) and a cation-ordered pyrochlore-type structure was formed, which was not stable upon oxidation in a flow of carbon dioxide.

In situ flow cell for combined X-ray absorption spectroscopy, X-ray diffraction, and mass spectrometry at high photon energies under solar thermochemical looping conditions.

PubMed

Rothensteiner, Matthäus; Jenni, Joel; Emerich, Hermann; Bonk, Alexander; Vogt, Ulrich F; van Bokhoven, Jeroen A

2017-08-01

An in situ/operando flow cell for transmission mode X-ray absorption spectroscopy (XAS), X-ray diffraction (XRD), and combined XAS/XRD measurements in a single experiment under the extreme conditions of two-step solar thermochemical looping for the dissociation of water and/or carbon dioxide was developed. The apparatus exposes materials to relevant conditions of both the auto-reduction and the oxidation sub-steps of the thermochemical cycle at ambient temperature up to 1773 K and enables determination of the composition of the effluent gases by online quadrupole mass spectrometry. The cell is based on a tube-in-tube design and is heated by means of a focusing infrared furnace. It was tested successfully for carbon dioxide splitting. In combined XAS/XRD experiments with an unfocused beam, XAS measurements were performed at the Ce K edge (40.4 keV) and XRD measurements at 64.8 keV and 55.9 keV. Furthermore, XRD measurements with a focused beam at 41.5 keV were carried out. Equimolar ceria-hafnia was auto-reduced in a flow of argon and chemically reduced in a flow of hydrogen/helium. Under reducing conditions, all cerium(iv) was converted to cerium(iii) and a cation-ordered pyrochlore-type structure was formed, which was not stable upon oxidation in a flow of carbon dioxide.

Phase transition of aragonite in abalone nacre

NASA Astrophysics Data System (ADS)

An, Yuanlin; Liu, Zhiming; Wu, Wenjian

2013-04-01

Nacre is composed of about 95 vol.% aragonite and 5 vol.% biopolymer and famous for its "brick and mortar" microstructure. The phase transition temperature of aragonite in nacre is lower than the pure aragonite. In situ XRD was used to identify the phase transition temperature from aragonite to calcite in nacre, based on the analysis of TG-DSC of fresh nacre and demineralized nacre. The results indicate that the microstructure and biopolymer are the two main factors that influence the phase transition temperature of aragonite in nacre.

Structural, optical and magnetic investigation of Gd implanted CeO2 nanocrystals

NASA Astrophysics Data System (ADS)

Kaviyarasu, K.; Murmu, P. P.; Kennedy, J.; Thema, F. T.; Letsholathebe, Douglas; Kotsedi, L.; Maaza, M.

2017-10-01

Gadolinium implanted cerium oxide (Gd-CeO2) nanocomposites is an important candidate which have unique hexagonal structure and high K- dielectric constant. Gd-CeO2 nanoparticles were synthesized using hydrothermal method. X-ray diffraction (XRD) results showed that the peaks are consistent with pure phase cubic structure the XRD pattern also confirmed crystallinity and phase purity of the sample. Nanocrystals sizes were found to be up to 25 nm as revealed by XRD and SEM. It is suggested that Gd gives an affirmative effect on the ion influence behavior of Gd-CeO2. XRD patterns showed formation of new phases and SEM micrographs revealed hexagonal structure. Photoluminescence measurement (PL) reveals the systematic shift of the emission band towards lower wavelength thereby ascertaining the quantum confinement effect (QCE). The PL spectrum has wider broad peak ranging from 390 nm to 770 nm and a sharp one centered on at 451.30 nm which is in tune with Gd ions. In the Raman spectra showed intense band observed between 460 cm-1 and 470 cm-1 which is attributed to oxygen ions into CeO2. Room temperature ferromagnetism was observed in un-doped and Gd implanted and annealed CeO2 nanocrystals. In the recent studies, ceria based materials have been considered as one of the most promising electrolytes for reduced temperature SOFC (solid oxide fuel cell) system due to their high ionic conductivities allowing its use in stainless steel supported fuel cells. CeO2 having an optical bandgap 3.3 eV and n-type carrier density which make it a promising candidate for various technological application such as buffer layer on silicon on insulator devices.

Modeling and measurements of XRD spectra of extended solids under high pressure

NASA Astrophysics Data System (ADS)

Batyrev, I. G.; Coleman, S. P.; Stavrou, E.; Zaug, J. M.; Ciezak-Jenkins, J. A.

2017-06-01

We present results of evolutionary simulations based on density functional calculations of various extended solids: N-Si and N-H using variable and fixed concentration methods of USPEX. Predicted from the evolutionary simulations structures were analyzed in terms of thermo-dynamical stability and agreement with experimental X-ray diffraction spectra. Stability of the predicted system was estimated from convex-hull plots. X-ray diffraction spectra were calculated using a virtual diffraction algorithm which computes kinematic diffraction intensity in three-dimensional reciprocal space before being reduced to a two-theta line profile. Calculations of thousands of XRD spectra were used to search for a structure of extended solids at certain pressures with best fits to experimental data according to experimental XRD peak position, peak intensity and theoretically calculated enthalpy. Comparison of Raman and IR spectra calculated for best fitted structures with available experimental data shows reasonable agreement for certain vibration modes. Part of this work was performed by LLNL, Contract DE-AC52-07NA27344. We thank the Joint DoD / DOE Munitions Technology Development Program, the HE C-II research program at LLNL and Advanced Light Source, supported by BES DOE, Contract No. DE-AC02-05CH112.

Differences in the Nature of Active Sites for Methane Dry Reforming and Methane Steam Reforming over Nickel Aluminate Catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rogers, Jessica L.; Mangarella, Michael C.; D’Amico, Andrew D.

In this paper, the Pechini synthesis was used to prepare nickel aluminate catalysts with the compositions NiAl 4O 7, NiAl 2O 4, and Ni 2Al 2O 5. The samples have been characterized by N 2 physisorption, temperature-programmed reduction (TPR), temperature-programmed oxidation (TPO), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), and X-ray absorption spectroscopy (XAS). Characterization results indicate unique structural properties and excellent regeneration potential of nickel aluminates. Prepared samples were tested when unreduced and reduced prior to reaction for methane dry reforming and methane steam reforming reactivity. NiAl 2O 4 in the reduced and unreduced statemore » as well as NiAl 4O 7 in the reduced state are active and stable for methane dry reforming due to the presence of 4-fold coordinated oxidized nickel. The limited amount of metallic nickel in these samples minimizes carbon deposition. Finally, on the other hand, the presence of metallic nickel is required for methane steam reforming. Ni 2Al 2O 5 in the reduced and unreduced states and NiAl 2O 4 in the reduced state are found to be active for methane steam reforming due to the presence of sufficiently small nickel nanoparticles that catalyze the reaction without accumulating carbonaceous deposits.« less

Differences in the Nature of Active Sites for Methane Dry Reforming and Methane Steam Reforming over Nickel Aluminate Catalysts

DOE PAGES

Rogers, Jessica L.; Mangarella, Michael C.; D’Amico, Andrew D.; ...

2016-07-20

In this paper, the Pechini synthesis was used to prepare nickel aluminate catalysts with the compositions NiAl 4O 7, NiAl 2O 4, and Ni 2Al 2O 5. The samples have been characterized by N 2 physisorption, temperature-programmed reduction (TPR), temperature-programmed oxidation (TPO), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), and X-ray absorption spectroscopy (XAS). Characterization results indicate unique structural properties and excellent regeneration potential of nickel aluminates. Prepared samples were tested when unreduced and reduced prior to reaction for methane dry reforming and methane steam reforming reactivity. NiAl 2O 4 in the reduced and unreduced statemore » as well as NiAl 4O 7 in the reduced state are active and stable for methane dry reforming due to the presence of 4-fold coordinated oxidized nickel. The limited amount of metallic nickel in these samples minimizes carbon deposition. Finally, on the other hand, the presence of metallic nickel is required for methane steam reforming. Ni 2Al 2O 5 in the reduced and unreduced states and NiAl 2O 4 in the reduced state are found to be active for methane steam reforming due to the presence of sufficiently small nickel nanoparticles that catalyze the reaction without accumulating carbonaceous deposits.« less

ROLE OF TUNGSTEN IN THE AQUEOUS PHASE HYDRODEOXYGENATION OF ETHYLENE GLYCOL ON TUNGSTATED ZIRCONIA SUPPORTED PALLADIUM

DOE Office of Scientific and Technical Information (OSTI.GOV)

Marin-Flores, Oscar G.; Karim, Ayman M.; Wang, Yong

2014-11-15

The focus of the present work was specifically on the elucidation of the role played by tungsten on the catalytic activity and selectivity of tungstated zirconia supported palladium (Pd-mWZ) for the aqueous phase hydrodeoxygenation (APHDO) of ethylene glycol (EG). Zirconia supported palladium (Pd-mZ) was used as reference. The catalysts were prepared via incipient wet impregnation and characterized using X-ray diffraction (XRD), temperature-programmed reduction (TPR), CO pulse chemisorption, CO-DRIFTS, ammonia temperature-programmed desorption (NH3-TPD) and pyridine adsorption. The presence of W results in larger Pd particles on supported Pd catalysts, i.e., 0.9 and 6.1 nm Pd particles are for Pd-mZ and Pd-mWZ,more » respectively. For comparison purposes, the activity of the catalytic materials used in this work was obtained using a well-defined set of operating conditions. The catalytic activity measurements show that the overall intrinsic activity of Pd particles on mWZ is 1.9 times higher than on mZ. APHDO process appears to be highly favored on Pd-mWZ whereas Pd-mZ exhibits a higher selectivity for reforming. This difference in terms of selectivity seems to be related to the high concentration of Brønsted acid sites and electron-deficient Pd species present on Pd-mWZ.« less

The Evolution of Structural Order as a Measure of Thermal History of Coke in the Blast Furnace

NASA Astrophysics Data System (ADS)

Lundgren, Maria; Khanna, Rita; Ökvist, Lena Sundqvist; Sahajwalla, Veena; Björkman, Bo

2014-04-01

Investigations were carried out on cokes heat treated in the laboratory and on cokes extracted from the experimental blast furnace (EBF) raceway and hearth. X-ray diffraction (XRD) measurements were performed to investigate changes in structural order ( L c), chemical transformations in coke ash along with comparative thermodynamic equilibrium studies and the influence of melt. Three data processing approaches were used to compute L c values as a function of temperature and time and linear correlations were established between L c and heat treatment temperatures during laboratory investigations. These were used to estimate temperatures experienced by coke in various regions of EBF and estimated raceway temperatures were seen to follow the profile of combustion peak. The MgAl2O4 spinel was observed in coke submerged in slag during laboratory studies and in cokes found further into the raceway. Coke in contact with hot metal showed XRD peaks corresponding to presence of Fe3Si. The intensity of SiO2 peak in coke ash was seen to decrease with increasing temperature and disappeared at around 1770 K (1500 °C) due to the formation of SiC. This study has shown that the evolution of structural order and chemical transformations in coke could be used to estimate its thermal history in blast furnaces.

In vitro behavior of MC3T3-E1 preosteoblast with different annealing temperature titania nanotubes.

PubMed

Yu, W Q; Zhang, Y L; Jiang, X Q; Zhang, F Q

2010-10-01

Titanium oxide nanotube layers by anodization have excellent potential for dental implants because of good bone cell promotion. It is necessary to evaluate osteoblast behavior on different annealing temperature titania nanotubes for actual implant designs.  Scanning Electron Microscopy, X-Ray polycrystalline Diffractometer (XRD), X-ray photoelectron Spectroscope, and Atomic Force Microscopy (AFM) were used to characterize the different annealing temperature titania nanotubes. Confocal laser scanning microscopy, MTT, and Alizarin Red-S staining were used to evaluate the MC3T3-E1 preosteoblast behavior on different annealing temperature nanotubes.  The tubular morphology was constant when annealed at 450°C and 550°C, but collapsed when annealed at 650°C. XRD exhibited the crystal form of nanotubes after formation (amorphous), after annealing at 450°C (anatase), and after annealing at 550°C (anatase/rutile). Annealing led to the complete loss of fluorine on nanotubes at 550°C. Average surface roughness of different annealing temperature nanotubes showed no difference by AFM analysis. The proliferation and mineralization of preostoblasts cultured on anatase or anatase/rutile nanotube layers were shown to be significantly higher than smooth, amorphous nanotube layers.  Annealing can change the crystal form and composition of nanotubes. The nanotubes after annealing can promote osteoblast proliferation and mineralization in vitro. © 2010 John Wiley & Sons A/S.

Effect of sintering temperature on physical, structural and optical properties of wollastonite based glass-ceramic derived from waste soda lime silica glasses

NASA Astrophysics Data System (ADS)

Almasri, Karima Amer; Sidek, Hj. Ab Aziz; Matori, Khamirul Amin; Zaid, Mohd Hafiz Mohd

The impact of different sintering temperatures on physical, optical and structural properties of wollastonite (CaSiO3) based glass-ceramics were investigated for its potential application as a building material. Wollastonite based glass-ceramics was provided by a conventional melt-quenching method and followed by a controlled sintering process. In this work, soda lime silica glass waste was utilized as a source of silicon. The chemical composition and physical properties of glass were characterized by using Energy Dispersive X-ray Fluorescence (EDXRF) and Archimedes principle. The Archimedes measurement results show that the density increased with the increasing of sintering temperature. The generation of CaSiO3, morphology, size and crystal phase with increasing the heat-treatment temperature were examined by field emission scanning electron microscopy (FESEM), Fourier transforms infrared reflection spectroscopy (FTIR), and X-ray diffraction (XRD). The average calculated crystal size gained from XRD was found to be in the range 60 nm. The FESEM results show a uniform distribution of particles and the morphology of the wollastonite crystal is in relict shapes. The appearance of CaO, SiO2, and Ca-O-Si bands disclosed from FTIR which showed the formation of CaSiO3 crystal phase. In addition to the calculation of the energy band gap which found to be increased with increasing sintering temperature.

Temperature dependent dielectric relaxation and ac-conductivity of alkali niobate ceramics studied by impedance spectroscopy

NASA Astrophysics Data System (ADS)

Yadav, Abhinav; Mantry, Snigdha Paramita; Fahad, Mohd.; Sarun, P. M.

2018-05-01

Sodium niobate (NaNbO3) ceramics is prepared by conventional solid state reaction method at sintering temperature 1150 °C for 4 h. The structural information of the material has been investigated by X-ray diffraction (XRD) and Field emission scanning electron microscopy (FE-SEM). The XRD analysis of NaNbO3 ceramics shows an orthorhombic structure. The FE-SEM micrograph of NaNbO3 ceramics exhibit grains with grain sizes ranging between 1 μm to 5 μm. The surface coverage and average grain size of NaNbO3 ceramics are found to be 97.6 % and 2.5 μm, respectively. Frequency dependent electrical properties of NaNbO3 is investigated from room temperature to 500 °C in wide frequency range (100 Hz-5 MHz). Dielectric constant, ac-conductivity, impedance, modulus and Nyquist analysis are performed. The observed dielectric constant (1 kHz) at transition temperature (400 °C) are 975. From conductivity analysis, the estimated activation energy of NaNbO3 ceramics is 0.58 eV at 10 kHz. The result of Nyquist plot shows that the electrical behavior of NaNbO3 ceramics is contributed by grain and grain boundary responses. The impedance and modulus spectrum asserts that the negative temperature coefficient of resistance (NTCR) behavior and non-Debye type relaxation in NaNbO3.

Effect of Annealing Temperature on Structural and Optical Properties of Sol-Gel-Derived ZnO Thin Films

NASA Astrophysics Data System (ADS)

Arif, Mohd.; Sanger, Amit; Vilarinho, Paula M.; Singh, Arun

2018-04-01

Nanocrystalline ZnO thin films were deposited on glass substrate via sol-gel dip-coating technique then annealed at 300°C, 400°C, and 500°C for 1 h. Their optical, structural, and morphological properties were studied using ultraviolet-visible (UV-Vis) spectrophotometry, x-ray diffraction (XRD) analysis, and scanning electron microscopy (SEM). XRD diffraction revealed that the crystalline nature of the thin films increased with increasing annealing temperature. The c-axis orientation improved, and the grain size increased, as indicated by increased intensity of the (002) plane peak at 2θ = 34.42° corresponding to hexagonal ZnO crystal. The average crystallite size of the thin films ranged from 13 nm to 23 nm. Increasing the annealing temperature resulted in larger crystallite size and higher crystallinity with increased surface roughness. The grain size according to SEM analysis was in good agreement with the x-ray diffraction data. The optical bandgap of the thin films narrowed with increasing annealing temperature, lying in the range of 3.14 eV to 3.02 eV. The transmission of the thin films was as high as 94% within the visible region. The thickness of the thin films was 400 nm, as measured by ellipsometry, after annealing at the different temperatures of 300°C, 400°C, and 500°C.

Structural and magnetic properties of Ga-substituted Co 2 ‑W hexaferrites

NASA Astrophysics Data System (ADS)

Mahmood, Sami H.; Al Sheyab, Qusai; Bsoul, Ibrahim; Mohsen, Osama; Awadallah, Ahmad

2018-05-01

Precursor powders of BaMg2-xCoxFe16O27 with (x = 0.0, 1.0, and 2.0) were prepared using high-energy ball milling, and the effects of chemical composition and sintering temperature on the structural and magnetic properties were investigated using x-ray diffractometer (XRD), scanning electron microscopy (SEM), and vibrating sample magnetometry (VSM). XRD patterns of the prepared samples indicated that crystallization of pure BaW hexaferrite phase was achieved at sintering temperature of 1300{\\deg} C, while BaM and cubic spinel phase intermediate phases were obtained at lower sintering temperatures of 1100{\\deg} C and 1200{\\deg} C. SEM images revealed improvement of the crystallization of the structural phases, and growth of the particle size with increasing the sintering temperature. The magnetic data of the samples sintered at 1300{\\deg} C revealed an increase of the saturation magnetization from 59.44 emu/g to 72.56 emu/g with increasing Co concentration (x) from 0.0 to 2.0. The coercive field Hc decreased from 0.07 kOe at x = 0.0, to 0.03 kOe at x = 1.0, and then increases to 0.09 kOe at x = 2.0. The thermomagnetic curves of the samples sintered at 1300{\\deg} C confirmed the existence of the W-type phase, and revealed spin reorientation transitions above room temperature.

Center for Thin Film Studies

DTIC Science & Technology

1991-01-22

highly oriented pyrolitic graphite ( HOPG ) for detailed studies of nucleation and of the development of surface roughness. Using a shadowing technique, we...laser to a temperature of approximately 600’C, a polycrystalline film resulted, as indicated b x-ray diffraction ( XRD ) data shown in Fig. 4. vI Figure 4...stress level rose in films deposited at colder temperatures. Development of second harmonic generation as a technique for evaluation of anisotropy in

Biocompatibility and Surface Properties of TiO2 Thin Films Deposited by DC Magnetron Sputtering

PubMed Central

López-Huerta, Francisco; Cervantes, Blanca; González, Octavio; Hernández-Torres, Julián; García-González, Leandro; Vega, Rosario; Herrera-May, Agustín L.; Soto, Enrique

2014-01-01

We present the study of the biocompatibility and surface properties of titanium dioxide (TiO2) thin films deposited by direct current magnetron sputtering. These films are deposited on a quartz substrate at room temperature and annealed with different temperatures (100, 300, 500, 800 and 1100 °C). The biocompatibility of the TiO2 thin films is analyzed using primary cultures of dorsal root ganglion (DRG) of Wistar rats, whose neurons are incubated on the TiO2 thin films and on a control substrate during 18 to 24 h. These neurons are activated by electrical stimuli and its ionic currents and action potential activity recorded. Through X-ray diffraction (XRD), the surface of TiO2 thin films showed a good quality, homogeneity and roughness. The XRD results showed the anatase to rutile phase transition in TiO2 thin films at temperatures between 500 and 1100 °C. This phase had a grain size from 15 to 38 nm, which allowed a suitable structural and crystal phase stability of the TiO2 thin films for low and high temperature. The biocompatibility experiments of these films indicated that they were appropriated for culture of living neurons which displayed normal electrical behavior. PMID:28788667

Surface structural evolution of AuAg/TiO2 catalyst in the transformation of benzyl alcohol to sodium benzoate

NASA Astrophysics Data System (ADS)

Cui, Yuanyuan; Wang, Ying; Fan, Kangnian; Dai, Wei-Lin

2013-08-01

A series of AuAg/TiO2 catalysts calcined at different temperatures were used for single-pot, solvent-free synthesis of sodium benzoate and benzoic acid through the green oxidation of benzyl alcohol. The best catalytic performance, which produced a sodium benzoate yield of up to 85%, was obtained over the AuAg/TiO2 catalyst calcined at 623 K. Systematic characterizations including BET, XRD, TEM, XPS, and UV-vis DRS and ICP were carried out to investigate the influence of calcined temperature on the structural evolution of the bimetallic AuAg/TiO2 catalysts. TEM images showed that both low (473 K) and high calcinations temperatures (973 K) resulted in larger particles. The smallest particles (8.2 nm) were obtained at 623 K. This decrease in particle size may have been induced by the re-dispersion and interaction of the bimetallic species. XRD and XPS results showed that proper calcination temperature (623 K) could promote interactions between the bimetallic particles and the TiO2 support as well as the dispersion of active bimetallic species. The higher catalytic performance of the 623 K calcined catalyst could be attributed to the smaller particle size and the synergetic interaction between nano-bimetallic gold and silver species.

Yttria catalyzed microstructural modifications in oxide dispersion strengthened V-4Cr-4Ti alloys synthesized by field assisted sintering technique

NASA Astrophysics Data System (ADS)

Krishnan, Vinoadh Kumar; Sinnaeruvadi, Kumaran; Verma, Shailendra Kumar; Dash, Biswaranjan; Agrawal, Priyanka; Subramanian, Karthikeyan

2017-08-01

The present work deals with synthesis, characterisation and elevated temperature mechanical property evaluation of V-4Cr-4Ti and oxide (yttria = 0.3, 0.6 and 0.9 at%) dispersion strengthened V-4Cr-4Ti alloy processed by mechanical alloying and field-assisted sintering, under optimal conditions. Microstructural parameters of both powder and sintered samples were deduced by X-ray diffraction (XRD) and further confirmed with high resolution transmission electron microscopy. Powder diffraction and electron microscopy study show that ball milling of starting elemental powders (V-4Cr-4Ti) with and without yttria addition has resulted in single phase α-V (V-4Cr-4Ti) alloy. Wherein, XRD and electron microscopy images of sintered samples have revealed phase separation (viz., Cr-V and Ti-V) and domain size reduction, with yttria addition. The reasons behind phase separation and domain size reduction with yttria addition during sintering are extensively discussed. Microhardness and high temperature compression tests were done on sintered samples. Yttria addition (0.3 and 0.6 at.%) increases the elevated temperature compressive strength and strain hardening exponent of α-V alloys. High temperature compression test of 0.9 at% yttria dispersed α-V alloy reveals a glassy behaviour.

Thermal and temporal evolution of microstructure in polycrystalline ZnO

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kondal, Neha; Tiwari, Sanjiv Kumar, E-mail: sanjivkumar.tiwari@juit.ac.in

2016-05-06

Tug between electronics and spintronics has opened up new area of research named as dilute magnetic semiconductors (DMS), ZnO is one of the most reliable candidates for spintronic devices and DMS. Since, pure and transition metal doped polycrystalline ZnO shows room temperature ferromagnetism, therefore it is very important to gain insight into its microstructure (MS) evolution. We report thermal evolution of MS of pure ZnO on sintering it at 200 °C, 400 °C, 600 °C, and 800 °C in ambient atmosphere for two hours. Temporal evolution at fixed temperature was analyzed using mean field model of internal energy and entropy.more » Grain size of ZnO MS were analyzed using integral breadth method of X-ray diffraction (XRD) lines using Voigt profile fit,. XRD line corresponding to [101] plane shifts from 36.17° to 36.28° whereas grain size increases from 67.5 nm to 93.7 nm with increase of temperature from 23°C to 800°C respectively. Grain growth with increase of temperature show Arrhenius type behavior with activation energy of 30.77 kJ-mol{sup −1} and temporal growth shows diffusive behavior with exponent 0.5.« less

Synthesis of AuPd alloyed nanoparticles via room-temperature electron reduction with argon glow discharge as electron source.

PubMed

Yang, Manman; Wang, Zongyuan; Wang, Wei; Liu, Chang-Jun

2014-01-01

Argon glow discharge has been employed as a cheap, environmentally friendly, and convenient electron source for simultaneous reduction of HAuCl4 and PdCl2 on the anodic aluminum oxide (AAO) substrate. The thermal imaging confirms that the synthesis is operated at room temperature. The reduction is conducted with a short time (30 min) under the pressure of approximately 100 Pa. This room-temperature electron reduction operates in a dry way and requires neither hydrogen nor extra heating nor chemical reducing agent. The analyses using X-ray photoelectron spectroscopy (XPS) confirm all the metallic ions have been reduced. The characterization with X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) shows that AuPd alloyed nanoparticles are formed. There also exist some highly dispersed Au and Pd monometallic particles that cannot be detected by XRD and transmission electron microscopy (TEM) because of their small particle sizes. The observed AuPd alloyed nanoparticles are spherical with an average size of 14 nm. No core-shell structure can be observed. The room-temperature electron reduction can be operated in a larger scale. It is an easy way for the synthesis of AuPd alloyed nanoparticles.

XRD and SEM study of alumina silicate porcelain insulator

NASA Astrophysics Data System (ADS)

Duddi, Dharmender; Singh, G. P.; Kalra, Swati; Shekhawat, M. S.; Tak, S. K.

2018-05-01

Higher strength electrical porcelain is a requirement of industry. This will be achieved by a specific composition of raw materials, which is consisted of clays and feldspars. Water absorption, particle size and insulating properties are of special interest now a day. China clay, Ball clay and Quartz are widely used by ceramic industries in Bikaner district of Rajasthan. Sample for present study were prepared by mixing of above clay, feldspar with MnO2, then shrinkage is observed. Bar shaped samples were prepared and heated up to a temperature of about 1185° C to observe shrinkage. For phase study of XRD and SEM are observed.

Electrochromic TiO2 Thin Film Prepared by Dip-Coating Technique

NASA Astrophysics Data System (ADS)

Suriani, S.; Kamisah, M. M.

2002-12-01

Titanium dioxide (TiO2) thin films were prepared by using sol-gel dip coating technique. The coating solutions were prepared by reacting titanium isopropoxide as precursors and ethanol as solvent. The films were formed on transparent ITO-coated glass by a dip coating technique and final dried at various temperatures up to 600 °C for 30 minutes. The films were characterized with the UV-Vis-NIR Spectrometer, Scanning Electron Microscopy (SEM) and X-ray diffractometer (XRD). XRD results show that the films dried at 600 °C form anatase structure. From the spectroscopic studies, the sample shows electrochromic property.

Structural and magnetic analysis of Cu, Co substituted NiFe2O4 thin films

NASA Astrophysics Data System (ADS)

Sharma, Hakikat; Bala, Kanchan; Negi, N. S.

2016-05-01

In the present work we prepared NiFe2O4, Ni0.95Cu0.05Fe2O4 and Ni0.94Cu0.05Co0.01 Fe2O4 thin films by metallo-organic decomposition method (MOD) using spin coating technique. The thin films were analyzed by X-ray diffractometer (XRD) and Atomic force microscope (AFM) for structural studies. The XRD patterns confirmed the ferrite phase of thin films. From AFM, we analyzed surface morphology, calculated grain size (GS) and root mean square roughness (RMSR). Room temperature magnetic properties were investigated by vibrating sample magnetometer (VSM).

Polymethacrylic acid as a new precursor of CuO nanoparticles

NASA Astrophysics Data System (ADS)

Hosny, Nasser Mohammed; Zoromba, Mohamed Shafick

2012-11-01

Polymethacrylic acid and its copper complexes have been synthesized and characterized. These complexes have been used as precursors to produce CuO nanoparticles by thermal decomposition in air. The stages of decompositions and the calcination temperature of the precursors have been determined from thermal analyses (TGA). The obtained CuO nanoparticles have been characterized by X-ray diffraction (XRD), scanning tunneling microscopy (STM) and transmission electron microscopy (TEM). XRD showed a monoclinic structure with particle size 8-20 nm for the synthesized copper oxide nanoparticles. These nanoparticles are catalytically active in decomposing hydrogen peroxide and a mechanism of decomposition has been suggested.

Interplay of structural, optical and magnetic properties in Gd doped CeO{sub 2}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Soni, S.; Dalela, S., E-mail: sdphysics@rediffmail.com; Kumar, Sudish

In this research wok systematic investigation on the synthesis, characterization, optical and magnetic properties of Ce{sub 1-x}Gd{sub x}O{sub 2} (where x=0.02, 0.04, 0.06, and 0.10) synthesized using the Solid-state method. Structural, Optical and Magnetic properties of the samples were investigated by X-ray diffraction (XRD), UV-VIS-NIR spectroscopy and VSM. Fluorite structure is confirmed from the XRD measurement on Gd doped CeO{sub 2} samples. Magnetic studies showed that the Gd doped polycrystalline samples display room temperature ferromagnetism and the ferromagnetic ordering strengthens with the Gd concentration.

Synthesis and characterization of nanocrystalline graphite from coconut shell with heating process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wachid, Frischa M., E-mail: frischamw@yahoo.com, E-mail: adhiyudhaperkasa@yahoo.com, E-mail: afandisar@yahoo.com, E-mail: nurulrosyidah92@gmail.com, E-mail: darminto@physics.its.ac.id; Perkasa, Adhi Y., E-mail: frischamw@yahoo.com, E-mail: adhiyudhaperkasa@yahoo.com, E-mail: afandisar@yahoo.com, E-mail: nurulrosyidah92@gmail.com, E-mail: darminto@physics.its.ac.id; Prasetya, Fandi A., E-mail: frischamw@yahoo.com, E-mail: adhiyudhaperkasa@yahoo.com, E-mail: afandisar@yahoo.com, E-mail: nurulrosyidah92@gmail.com, E-mail: darminto@physics.its.ac.id

Graphite were synthesized and characterized by heating process of coconut shell with varying temperature (400, 800 and 1000°C) and holding time (3 and 5 hours). After heating process, the samples were characterized by X-ray diffraction (XRD) and analyzed by X'pert HighScore Plus Software, Scanning Electron Microcope-Energy Dispersive X-Ray (SEM-EDX) and Transmission Electron Microscope-Energy Dispersive X-Ray (TEM-EDX). Graphite and londsdaelite phase were analyzed by XRD. According to EDX analysis, the sample was heated in 1000°C got the highest content of carbon. The amorphous carbon and nanocrystalline graphite were observed by SEM-EDX and TEM-EDX.

Influence of incubation temperature on biofilm formation and corrosion of carbon steel by Serratia marcescens

NASA Astrophysics Data System (ADS)

Harimawan, Ardiyan; Devianto, Hary; Kurniawan, Ignatius Chandra; Utomo, Josephine Christine

2017-01-01

Microbial induced corrosion (MIC) or biocorrosion is one type of corrosion, directly or indirectly influenced by microbial activities, by forming biofilm and adhering on the metal surface. When forming biofilm, the microorganisms can produce extracellular products which influence the cathodic and anodic reactions on metal surfaces. This will result in electrochemical changes in the interface between the biofilm and the metal surface, leading to corrosion and deterioration of the metal. MIC might be caused by various types of microorganism which leads to different corrosion mechanism and reaction kinetics. Furthermore, this process will also be influenced by various environmental conditions, such as pH and temperature. This research is aimed to determine the effect of incubation temperature on corrosion of carbon steel caused by Serratia marcescens in a mixture solution of synthetic seawater with Luria Bertani medium with a ratio of 4:1. The incubation was performed for 19 days with incubation temperature of 30, 37, and 50°C. The analyses of biofilm were conducted by total plate count (TPC), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR). Biofilm was found to be evenly growth on the surface and increasing with increasing incubation temperature. It consists of functional group of alcohol, alkane, amine, nitro, sulfate, carboxylic acid, and polysulfide. The analyses of the corrosion were conducted by gravimetric and X-ray diffraction (XRD). Higher incubation temperature was found to increase the corrosion rate. However, the corrosion products were not detected by XRD analysis.

Temperature dependence of the crystalline quality of AlN layer grown on sapphire substrates by metalorganic chemical vapor deposition

NASA Astrophysics Data System (ADS)

Li, Xiao-Hang; Wei, Yong O.; Wang, Shuo; Xie, Hongen; Kao, Tsung-Ting; Satter, Md. Mahbub; Shen, Shyh-Chiang; Douglas Yoder, P.; Detchprohm, Theeradetch; Dupuis, Russell D.; Fischer, Alec M.; Ponce, Fernando A.

2015-03-01

We studied temperature dependence of crystalline quality of AlN layers at 1050-1250 °C with a fine increment step of around 18 °C. The AlN layers were grown on c-plane sapphire substrates by metalorganic chemical vapor deposition (MOCVD) and characterized by X-ray diffraction (XRD) ω-scans and atomic force microscopy (AFM). At 1050-1068 °C, the templates exhibited poor quality with surface pits and higher XRD (002) and (102) full-width at half-maximum (FWHM) because of insufficient Al atom mobility. At 1086 °C, the surface became smooth suggesting sufficient Al atom mobility. Above 1086 °C, the (102) FWHM and thus edge dislocation density increased with temperatures which may be attributed to the shorter growth mode transition from three-dimension (3D) to two-dimension (2D). Above 1212 °C, surface macro-steps were formed due to the longer diffusion length of Al atoms than the expected step terrace width. The edge dislocation density increased rapidly above 1212 °C, indicating this temperature may be a threshold above which the impact of the transition from 3D to 2D is more significant. The (002) FWHM and thus screw dislocation density were insensitive to the temperature change. This study suggests that high-quality AlN/sapphire templates may be potentially achieved at temperatures as low as 1086 °C which is accessible by most of the III-nitride MOCVD systems.

Study of sintering temperature on the structure of silicon carbide membrane

NASA Astrophysics Data System (ADS)

Sadighzadeh, A.; Mashayekhan, Sh.; Nedaie, B.; Ghorashi, A. H.

2014-09-01

Study of the microstructure of silicon carbide (SiC) membrane as a function of sintering temperature and the percentage amount of additive kaolin is the outcome of the experimental fabrications presented in this paper. The SEM micrographs are used to investigate the impact of above parameters on the porosity of membrane. The experimental results show that the rise in the temperature causes more sintering of powder particles, growing granules, augmentation of the number of pores and consequently increasing the total porosity of membrane. Using XRD analyses, it is found that SiC amorphous phase is highly sensitive to the temperature and its crystallization physically grows with temperature increase.

Structural properties of zirconia - in-situ high temperature XRD characterization

NASA Astrophysics Data System (ADS)

Kurpaska, Lukasz

2018-07-01

In this work, the effect of high temperature on structural properties of pure zirconium have been investigated. In-situ X-ray diffraction analysis of the oxide layer formed at temperature window 25-600 °C on pure zirconium were performed. Conducted experiment aimed at investigation of the zirconia phases developed on surface of the metallic substrate. Based on the conducted studies, possible stress state (during heating, continuous oxidation and cooling), cell parameters and HWHM factor were analyzed. A tetragonal and monoclinic phases peak shifts and intensities change were observed, suggesting that different phases react in different way upon temperature effect.

Low temperature synthesis of hexagonal ZnO nanorods and their hydrogen sensing properties

NASA Astrophysics Data System (ADS)

Qurashi, Ahsanulhaq; Faiz, M.; Tabet, N.; Alam, Mir Waqas

2011-08-01

The growth of hexagonal ZnO nanorods was demonstrated by low temperature chemical synthesis approach. X-ray diffraction (XRD) analysis revealed a wurtzite hexagonal structure of the ZnO nanorods. The optical properties were measured by UV-vis spectrophotometer at room temperature. X-ray photoelectron spectroscopy (XPS) confirmed high purity of the ZnO nanorods. The hydrogen sensor made of the ZnO nanorods showed reversible response. The hydrogen gas tests were carried out in presence of ambient air and the influence of operation temperature on the hydrogen gas sensing property of ZnO nanorods was also investigated.

Raman analysis of non stoichiometric Ni1-δO

NASA Astrophysics Data System (ADS)

Dubey, Paras; Choudhary, K. K.; Kaurav, Netram

2018-04-01

Thermal decomposition method was used to synthesize non-stoichiometric nickel oxide at different sintering temperatures upto 1100 °C. The structure of synthesized compounds were analyzed by X ray diffraction analysis (XRD) and magnetic ordering was studied with the help of Raman scattering spectroscopy for the samples sintered at different temperature. It was found that due to change in sintering temperature the stoichiometry of the sample changes and hence intensity of two magnon band changes. These results were interpreted as the decomposition temperature increases, which heals the defects present in the non-stoichiometric nickel oxide and antiferromagnetic spin correlation changes accordingly.

Effects of the Tempering and High-Pressure Torsion Temperatures on Microstructure of Ferritic/Martensitic Steel Grade 91

PubMed Central

Ganeev, Artur; Nikitina, Marina; Sitdikov, Vil; Islamgaliev, Rinat; Hoffman, Andrew; Wen, Haiming

2018-01-01

Grade 91 (9Cr-1Mo) steel was subjected to various heat treatments and then to high-pressure torsion (HPT) at different temperatures. Its microstructure was studied using transmission electron microscopy (TEM) and X-ray diffraction (XRD). Effects of the tempering temperature and the HPT temperature on the microstructural features and microhardness in the ultrafine-grained (UFG) Grade 91 steel were researched. The study of the UFG structure formation takes into account two different microstructures observed: before HPT in both samples containing martensite and in fully ferritic samples. PMID:29671761

Effects of annealing on the structure and magnetic properties of Fe80B20 magnetostrictive fibers.

PubMed

Zhu, Qianke; Zhang, Shuling; Geng, Guihong; Li, Qiushu; Zhang, Kewei; Zhang, Lin

2016-07-04

Fe80B20 amorphous alloys exhibit excellent soft magnetic properties, high abrasive resistance and outstanding corrosion resistance. In this work, Fe80B20 amorphous micro-fibers with HC of 3.33 Oe were firstly fabricated and the effects of annealing temperature on the structure and magnetic properties of the fibers were investigated. In this study, Fe80B20 amorphous fibers were prepared by the single roller melt-spinning method. The structures of as-spun and annealed fibers were investigated by X-ray diffractometer (XRD) (PANalytical X,Pert Power) using Cu Kα radiation. The morphology of the fibers was observed by scanning electron microscopy (SEM) (HITACHI-S4800). Differential scanning calorimetry (DSC) measurements of the fibers were performed on Mettler Toledo TGA/DSC1 device under N2 protection. Vibrating sample magnetometer (VSM, Versalab) was used to examine the magnetic properties of the fibers. The resonance behavior of the fibers was characterized by an impedance analyzer (Agilent 4294A) with a home-made copper coil. The X-ray diffusion (XRD) patterns show that the fibers remain amorphous structure until the annealing temperature reaches 500°C. The differential scanning calorimetry (DSC) results show that the crystallization temperature of the fibers is 449°C. The crystallization activation energy is calculated to be 221 kJ/mol using Kissinger formula. The scanning electron microscopy (SEM) images show that a few dendrites appear at the fiber surface after annealing. The result indicates that the coercivity HC (//) and HC (⊥) slightly increases with increasing annealing temperature until 400°C, and then dramatically increases with further increasing annealing temperature which is due to significant increase in magneto-crystalline anisotropy and magneto-elastic anisotropy. The Q value firstly increases slightly when the annealing temperature rises from room temperature (RT) to 300°C, then decreases until 400°C. Eventually, the value of Q increases to ~2000 at annealing temperature of 500°C. In this study, Fe80B20 amorphous fibers with the diameter of 60 μm were prepared by the single roller melt-spinning method and annealed at 200°C, 300°C, 400°C, and 500°C, respectively. XRD results indicate that the fiber structure remains amorphous when the annealing temperature is below 400°C. α-Fe phase and Fe3B phase appear when the annealing temperature rises to 500°C, which is above the crystallization temperature of 449°C. The recrystallization activation energy is calculated to be 221 kJ/mol. The coercivity increases with increasing annealing temperature, which attributes to the increase of total anisotropy. All the as-spun and annealed fibers exhibit good resonance behavior for magnetostrictive sensors.

Effects of graphene oxide concentration on optical properties of ZnO/RGO nanocomposites and their application to photocurrent generation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Azarang, Majid, E-mail: azarangmajid@gmail.com, E-mail: azarang@phys.usb.ac.ir; Department of Physics, University of Sistan and Baluchestan, 98135-674 Zahedan; Shuhaimi, Ahmad

2014-08-28

The effects of different concentrations of graphene oxide (GO) on the structure and optical properties of ZnO nanoparticles (NPs) were investigated. The nanocomposites were synthesized via the sol-gel method in a gelatin medium. X-ray diffraction patterns (XRD) and Fourier transform infrared spectroscopy indicated that the GO sheets were reduced and changed to reduced GO (RGO) during the calcination of the nanocomposites at 400 °C. In addition, the XRD patterns of the NPs indicated a hexagonal (wurtzite) structure for all the products. Microscopic studies showed that the NPs were decorated and dispersed on the RGO sheets very well. However, these studies revealedmore » that the RGO concentration had an effect on the crystal growth process for the ZnO NPs. Furthermore, these studies showed that the NPs could be grown with a single crystal quality in an optimum RGO concentration. According to the XRD results that were obtained from pure ZnO NPs, the calcinations temperature was decreased by the RGO. UV–vis and room temperature photoluminescence studies showed that the optical properties of the ZnO/RGO nanocomposite were affected by the RGO concentration. Finally, the obtained ZnO/RGO nanocomposite was used to generate a photocurrent. Observations showed that the photocurrent intensity of the nanocomposite was significantly increased by increasing the RGO, with an optimum RGO concentration.« less

Effect of bismuth doping on the structural and magnetic properties of zinc-ferrite nanoparticles prepared by a microwave combustion method

NASA Astrophysics Data System (ADS)

Shoushtari, Morteza Zargar; Emami, Akram; Ghahfarokhi, Seyed Ebrahim Mosavi

2016-12-01

In this study, we examine the bismuth doping effect on the structural, magnetic and microstructural properties of zinc-ferrite nanoparticles (ZnFe2-xBixO4 with x=0.0, 0.02, 0.04, 0.06, 0.1, 0.15) which have been prepared by a microwave combustion method. The structural, morphological and electromagnetic properties and also Curie temperature of the samples were examined by x-ray powder diffraction (XRD), field emission scanning electron microscope (FESEM), vibrating sample magnetometer (VSM), and LCR meter, respectively. In order to measure the energy band gap, the FTIR spectra of the samples were also considered. The XRD patterns of the samples revealed that all of them are ZnFe2O4 structure and no additional peak was observed in their patterns. This implied that the samples were single-phase up to bismuth solubility of 0.15 in Zinc-Ferrite. The results of XRD patterns also showed that the value lattice parameter increases with increasing the bismuth doping. The FESEM results revealed an ascending trend in the size of the nanoparticles. Also considering the VSM results characterized that an increasing the bismuth doping leads to lower the saturation magnetization. The Curie temperatures of the samples were reduced as a result of increasing the amount of bismuth.

Intracrystalline "geothermometry" assessed on clino and orthopyroxene bearing synthetic rocks

NASA Astrophysics Data System (ADS)

Murri, M.; Cámara, F.; Adam, J.; Domeneghetti, M. C.; Alvaro, M.

2018-04-01

Recent discussion on the application of intracrystalline "geothermometers" based on the Fe-Mg order-disorder reaction in pyroxene in natural rocks, indicates that the available calibration equations for clino and orthopyroxenes (cpx and opx), which express the equilibrium intracrystalline Fe-Mg distribution coefficient kD(Fe-Mg) as a function of temperature, require independent validation. In this paper, we tested the available experimental calibrations for clino and orthopyroxenes by determining the site occupancies of these minerals in synthetic samples grown from a hydrous nepheline basanite in a piston-cylinder apparatus at 1050 °C at 2.0 GPa to 1170 °C at 3.0 GPa, and quenched very rapidly by shutting off the power. The site occupancies were determined by single crystal X-ray diffraction (SC-XRD) and used to calculate the closure temperature, TC, of cation ordering using available calibrations of kD(Fe-Mg) vs. T. The calculated TC values of both clino and orthopyroxenes were found to be close to the temperatures at which they were quenched, in line with expected kinetic behavior, when calibrations for cpx (Murri et al., 2016) and opx (Stimpfl et al., 2005) based on SC-XRD structure refinements were used. In particular, the smallest discrepancy between calculated and actual temperature is of the order of a few degrees (12 °C for cpx and 4 °C for opx), and the largest is of the order of tens of degrees (22 °C for cpx and 55 °C for opx). On the other hand, much lower TCs were obtained when calibrations based on Mössbauer determination of site occupancies were used. These results confirm that the two methods (i.e. SC-XRD and Mössbauer) give inherently different site occupancy data and that the same methodology should thus be used for both calibration and natural samples in the determination of cooling rate of host rocks.

Austenite-martensite transformation in electrodeposited Fe70Pd30 NWs: a step towards making bio-nano-actuators tested on in vivo systems

NASA Astrophysics Data System (ADS)

Zuzek Rozman, K.; Pecko, D.; Trafela, S.; Samardzija, Z.; Spreitzer, M.; Jaglicic, Z.; Nadrah, P.; Zorko, M.; Bele, M.; Tisler, T.; Pintar, A.; Sturm, S.; Kostevsek, N.

2018-03-01

Fe69±3Pd31±3 nanowires (NWs) with lengths of a few microns and diameters of 200 nm were synthesized via template-assisted pulsed electrodeposition into alumina-based templates. The as-deposited Fe69±3Pd31±3 NWs exhibited α-Fe (bcc-solid solution of Fe, Pd) nanocrystalline structure as seen from the x-ray diffraction (XRD), that got confirmed by transmission electron microscopy (TEM) with some larger grains up 50 nm observed. Annealing of the as-deposited Fe69±3Pd31±3 NWs at 1173 K/45 min was followed by quenching in ice water and resulted in a transformation to the fcc crystal structure (XRD) with grain sizes up to 200 nm (TEM). To induce the austenite-to-martensite, i.e., fcc-to-fct phase transformation the fcc Fe69±3Pd31±3 NWs were cooled to 73 K. The XRD showed the disappearance of the (200) fcc reflection (at room temperature) and the appearance of the (200) fct reflection (at 73 K), confirming the fcc-to-fct transformation took place. The magnetic measurements revealed that the fcc Fe69±3Pd31±3 NWs measured at low temperatures (50 K) had a larger coercivity than at room temperature, which suggests the fct phase was present in the undercooled state, exhibiting a larger magnetocrystalline anisotropy than the fcc phase present at room temperature. As part of our interest in magnetic-shape-memory actuators, the as-deposited Fe69±3Pd31±3 NWs were tested for toxicity on zebrafish. In vivo tests showed no acute lethal or sub-lethal effects, which implies that the Fe69±3Pd31±3 NWs have the potential to be used as nano-actuators in biomedical applications.

The Effect of MnO2 Content and Sintering Atmosphere on The Electrical Properties of Iron Titanium Oxide NTC Thermistors using Yarosite

NASA Astrophysics Data System (ADS)

Wiendartun; Gustaman Syarif, Dani

2017-02-01

The effect of MnO2 content and sintering atmosphere on the characteristics of Fe2TiO5 ceramics for Negative Thermal Coefficient (NTC) thermistors by using Fe2O3 derived from yarosite has been studied. The ceramics were produced by pressing a homogeneous mixture of Fe2O3, TiO2 and MnO2 (0-2.0 w/o) powders in appropriate proportions to produce Fe2TiO5 based ceramics and sintering the pressed powder at 1100-1200°C for 3 hours in air, O2 and N2 gas. Electrical characterization was done by measuring electrical resistivity of the sintered ceramics at various temperatures from 30°C to 200°C. Microstructure and structural analyses were also carried out by using an scanning electron microscope (SEM) and x-ray diffraction (XRD). The XRD data showed that the pellets crystallize in orthorhombic. The presence of second phase could not be identified from the XRD analyses. The SEM images showed that the grain size of pellet ceramics increase with increasing of MnO2 addition, and the grains size of the ceramic sintered in oxygen gas is smaller than sintered in nitrogen gas. Electrical data showed that the value of room temperature resistance (RRT) tend to decrease with respect to the increasing of MnO2 addition and the pellet ceramics sintered in oxygen gas had the largest thermistor constant (B), activation energy (Ea), sensitivity (α) and room temperature resistance (RRT), compared to the sintered in nitrogen gas. From the electrical characteristics data, it was known that the electrical characteristics of the Fe2TiO5 pellet ceramics followed the NTC characteristic. The fabricated Fe2TiO5 ceramics have thermistor constants (B = 2207-7145K). This can be applied as temperature sensor, and will fulfill the market requirement.

The Introduction of substitutional and non-substitutional dopants into MgB2 in high pressure/Temperature or non-equilibrium regimes

NASA Astrophysics Data System (ADS)

Sumption, Mike

2013-03-01

In an attempt to study the effect of doping of MgB2 under conditions leading to efficient doping, we used both an high temperature/high pressure induction furnace to dope into MgB2 bulks at temperatures up to 1600 C and 1500 Psi, and thin film, PLD multilayer and mixed layer film fabrication. The high temperature/high pressure formation was used to explore the solubility at high temperatures of various dopants, and the thin film formation was an attempt to use non-equilibrium conditions to inject dopants more effectively. The dopants used were C, Ti, and Zr. C was seen to reach a maximal level at 4 at% C site substituted into MgB2, as evidenced by EPMA and XRD results. Zr, of interest as a possible Mg site substitution in MgB2 was not seen to enter into the MgB2 phase (instead segregating) in the bulk high temperature/high pressure experiments, but was seen to enter in during PLD, as evidenced by STEM and XRD results. Ti additions were attempted in the high pressures and temperature rig, with some evidence for dopant introduction. Critical field measurements on the Zr doped samples where seen to suppress Bc2 for all except very low levels of Ti addition, presumably associated with the much greater doping efficiency. This work was supported by the U.S. Department of Energy, High Energy Physics university Grant No. DE-FG02-95ER40900

Oxidation characteristics of MgF2 in air at high temperature

NASA Astrophysics Data System (ADS)

Chen, H. K.; Jie, Y. Y.; Chang, L.

2017-02-01

High temperature oxidation properties of MgF2 in air were studied. The changes of phase composition, macro surface morphology, weight and elemental composition of MgF2 samples with temperature were investigated by using XRD, EDS and gravimetric analyses. The results show that the oxidation reaction of MgF2 converted to MgO occurred at high temperature, and the reaction was accelerated by the increase of temperature and the presence of impurities. This result clarifies the understanding of the high temperature oxidation behavior of MgF2 in air, and provides a theoretical basis for the reasonable application of MgF2 in optical coating materials, electronic ceramic materials and magnesium melt protection.

Characterization of a Diamond Ground Y-TZP and Reversion of the Tetragonal to Monoclinic Transformation.

PubMed

Candido, L M; Fais, Lmg; Ferreira, E B; Antonio, S G; Pinelli, Lap

To characterize the surface of an yttria-stabilized zirconia (Y-TZP) ceramic after diamond grinding in terms of its crystalline phase, morphology, mean roughness (Ra), and wettability as well as to determine a thermal treatment to reverse the resulting tetragonal to monoclinic (t-m) transformation. Y-TZP specimens were distributed into different groups according to the actions (or no action) of grinding and irrigation. Grinding was accomplished using a diamond stone at a low speed. The samples were characterized by x-ray diffraction (XRD), scanning electron microscopy, goniometry, and profilometry. In situ high-temperature XRD was used to determine an annealing temperature to reverse the t-m transformation. Ra was submitted to the Kruskal-Wallis test, followed by the Dunn test (α=0.05). The volume fraction of the monoclinic phase and contact angle were submitted to one-way analysis of variance, followed by the Tukey test (α=0.05). Monoclinic zirconia was observed on the surface of samples after dry and wet grinding with a diamond stone. The volume fraction of the monoclinic phase was smaller on the dry ground samples (3.6%±0.3%) than on the wet ground samples (5.6%±0.3%). High-temperature XRD showed reversion of the t-m phase transformation, which started at 700°C and completed at 800°C in a conventional oven. Grinding with a diamond stone partially transformed the crystalline phase on the surface of a Y-TZP ceramic from tetragonal to monoclinic zirconia while simultaneously increasing the surface roughness and wettability. The t-m transformation could be reversed by heat treatment at 800°C or 900°C for 60 minutes or 1000°C for 30 minutes.

Structural and Magnetic Properties of {Eu}(3+) Eu 3 + -Doped {CdNb}_{2} {O}_{6} CdNb 2 O 6 Powders

NASA Astrophysics Data System (ADS)

Topkaya, Ramazan; Boyraz, Cihat; Ekmekçi, Mete Kaan

2018-03-01

Europium-doped CdNb2O6 powders with the molar concentration of Eu^{3+} (0.5, 3 and 6 mol%) were successfully prepared at 900°C by using molten salt synthesis method. The effect of europium (Eu) molar concentration on the structural and temperature-dependent magnetic properties of CdNb2O6 powders has been investigated by using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), vibrating sample magnetometer (VSM) and ferromagnetic resonance (FMR) techniques in the temperature range of 10-300 K. XRD results confirm that all the powders have orthorhombic crystal structure. It has been confirmed from VSM and FMR measurements that Eu^{3+}-doped CdNb2O6 powders have ferromagnetic behaviour for each Eu^{3+} molar concentration between 10 and 300 K. XRD and EDX analyses indicate that there is no magnetic impurity in Eu^{3+}-doped CdNb_2O_6 powders, supporting that the ferromagnetic behaviour of the powders arises from Eu^{3+} ions. The observed ferromagnetism was elucidated with the intrinsic exchange interactions between the magnetic moments associated with the unpaired 4 f electrons in Eu^{3+} ions. The saturation magnetization decreases with increasing Eu^{3+} molar concentration. The temperature-dependent magnetization behaviour was observed not to agree with Curie-Weiss law because europium obeys Van Vleck paramagnetism. Broad FMR spectra and a g-value higher than 2 were observed from FMR measurements, indicating the ferromagnetic behaviour of the powders. It was found that while the resonance field of FMR spectra decreases, the linewidth increases as a function of Eu^{3+} molar concentration.

Identification of a deleterious phase in photocatalyst based on Cd1 - xZnxS/Zn(OH)2 by simulated XRD patterns.

PubMed

Cherepanova, Svetlana; Markovskaya, Dina; Kozlova, Ekaterina

2017-06-01

The X-ray diffraction (XRD) pattern of a deleterious phase in the photocatalyst based on Cd 1 - x Zn x S/Zn(OH) 2 contains two relatively intense asymmetric peaks with d-spacings of 2.72 and 1.56 Å. Very small diffraction peaks with interplanar distances of (d) ≃ 8.01, 5.40, 4.09, 3.15, 2.49 and 1.35 Å are characteristic of this phase but not always observed. To identify this phase, the XRD patterns for sheet-like hydroxide β-Zn(OH) 2 and sheet-like hydrozincite Zn 5 (CO 3 ) 2 (OH) 6 as well as for turbostratic hydrozincite were simulated. It is shown that the XRD pattern calculated on the basis of the last model gives the best correspondence with experimental data. Distances between layers in the turbostratically disordered hydrozincite fluctuate around d ≃ 8.01 Å. This average layer-to-layer distance is significantly higher than the interlayer distance 6.77 Å in the ordered Zn 5 (CO 3 ) 2 (OH) 6 probably due to a deficiency of CO 3 2- anions, excess OH - and the presence of water molecules in the interlayers. It is shown by variable-temperature XRD and thermogravimetric analysis (TGA) that the nanocrystalline turbostratic nonstoichiometric hydrozincite-like phase is quite thermostable. It decomposes into ZnO in air above 473 K.

Thermal analysis of calcium sulfate dihydrate sources used to manufacture gypsum wallboard

DOE PAGES

Engbrecht, Dick C.; Hirschfeld, Deidre A.

2016-07-27

Gypsum wallboard has been used for over 100 years as a barrier to the spread of fire in residential and commercial structures. The gypsum molecule, CaSO 4·2H 2O, provides two crystalline waters that are released upon heating providing an endothermic effect. Manufacturers have recognized that the source of the gypsum ore is a factor that affects all aspects of its performance; thus, it is hypothesized that the impurities present in the gypsum ore are the causes of the performance differences. Differential Thermal Analysis/Thermogravimetric Analysis (DTA/TGA) and X-ray Diffraction (XRD) were used in this paper to compare and characterize samples ofmore » gypsum ore representing sources of natural, synthetic from a Flue Gas Desulfurization process (FGD) and blends thereof. The hemihydrate phase of representative natural, FGD, and reagent grade calcium sulfate were rehydrated with distilled water and evaluated by DTA/TGA. Analysis of the data shows distinct areas of similarity separated by the conversion to anhydrite ~250 °C. Compositional reconstructions based on DTA/TGA and XRD data were compared and although, the results were comparable, the DTA/TGA suggests thermally active compounds that were not detected by XRD. Anhydrite, silica and halite were reported by XRD but were not thermally reactive in the temperature range evaluated by DTA/TGA (ambient to 1050 °C). Finally, the presence of carbonate compounds (e.g., calcite and dolomite) were indicated by XRD and estimated from the thermal decomposition reaction ~700 °C.« less

Dynamics of Polymorphic Transformations in Palm Oil, Palm Stearin and Palm Kernel Oil Characterized by Coupled Powder XRD-DSC.

PubMed

Zaliha, Omar; Elina, Hishamuddin; Sivaruby, Kanagaratnam; Norizzah, Abd Rashid; Marangoni, Alejandro G

2018-06-01

The in situ polymorphic forms and thermal transitions of refined, bleached and deodorized palm oil (RBDPO), palm stearin (RBDPS) and palm kernel oil (RBDPKO) were investigated using coupled X-ray diffraction (XRD) and differential scanning calorimetry (DSC). Results indicated that the DSC onset crystallisation temperature of RBDPO was at 22.6°C, with a single reflection at 4.2Å started to appear from 23.4 to 17.1°C, and were followed by two prominent exothermic peaks at 20.1°C and 8.5°C respectively. Further cooling to -40°C leads to the further formation of a β'polymorph. Upon heating, a of β'→βtransformation was observed between 32.1 to 40.8°C, before the sample was completely melted at 43.0°C. The crystallization onset temperature of RBDPS was 44.1°C, with the appearance of the α polymorph at the same temperature as the appearance of the first sharp DSC exothermic peak. This quickly changed from α→β´ in the range 25 to 21.7°C, along with the formation of a small β peak at -40°C. Upon heating, a small XRD peak for the β polymorph was observed between 32.2 to 36.0°C, becoming a mixture of (β´+ β) between 44.0 to 52.5°C. Only the β polymorph survived further heating to 59.8°C. For RBDPKO, the crystallization onset temperature was 11.6°C, with the formation of a single sharp exothermic peak at 6.5°C corresponding to the β' polymorphic form until the temperature reached -40°C. No transformation of the polymorphic form was observed during the melting process of RBDPKO, before being completely melted at 33.2°C. This work has demonstrated the detailed dynamics of polymorphic transformations of PKO and PS, two commercially important hardstocks used widely by industry and will contribute to a greater understanding of their crystallization and melting dynamics.

Studies on temperature coefficient of resistivity of Cu2Se - V2O5 nanocomposite

NASA Astrophysics Data System (ADS)

Sairam, S.; Rai, Ranjan; Molli, Muralikrishna

2018-05-01

Nanocomposite of Copper Selenide in Vanadium Pentoxide (Cu2Se-V2O5) was prepared and characterized using XRD for phase analysis, SEM for morphology, and EDAX for elemental analysis. Electrical resistivity measurement was carried out using van der Pauw method as a function of temperature from 35 °C to 170 °C for 5 mol% Cu2Se - 95 mol%V2O5 composite. The temperature coefficient of resistivity was found to be -1.8% per °C.

Dielectric properties and activation behavior of gadolinium doped nanocrystalline yttrium chromite

NASA Astrophysics Data System (ADS)

Sinha, R.; Basu, S.; Meikap, A. K.

2018-04-01

Gadolinium doped Yttrium Chromite nanoparticles are synthesized following sol-gel method. The formation of the nanoparticles are confirmed by XRD and TEM measurements. Dielectric permittivity and dielectric loss are estimated within the temperature range 298K to 523K and in the frequency range 20 Hz to 1 MHz. Dielectric permittivity follows the power law ɛ'(f) ∝ Tm. It is observed that the temperature exponent m increases with the decreasing frequency. The temperature variation of resistivity shows that the samples have semiconducting behavior. The activation energy is also measured.

a Novel Catalyst for Reductive Dechlorination of Chlorobenzene in Subcritical Water:. Bifunctional Fe/ZrO2

NASA Astrophysics Data System (ADS)

Wei, Guang-Tao; Wei, Chao-Hai; He, Feng-Mei; Wu, Chao-Fei

Bifunctional Fe/ZrO2 was prepared by mechanical mixing method, and its bifunctional effect on reductive dechlorination of chlorobenzene in subcritical water was studied. Dechlorination efficiency increased with increasing iron content in catalyst and catalyst amount. Dechlorination efficiency slowed when the iron content in catalyst reached 30%; bifunctional catalyst of Fe/ZrO2 was more efficient in dechlorination of chlorobenzene than Fe alone. Catalyst of Fe (30%)/ZrO2 was characterized by means of X-ray diffraction (XRD), H2 temperature programmed desorption (H2-TPD), and N2 adsorption. The possible mechanism of dechlorination in subcritical water by this bifunctional catalyst was proposed. H+ produced in the water dissociation formed the highly reactive spillover hydrogen on the surface of catalyst, and then reacted with chlorobenzene adsorbed on the catalyst surface by ZrO2 to form benzene and chloride ions.

PET-modified red mud as catalysts for oxidative desulfurization reactions.

PubMed

do Prado, Nayara T; Heitmann, Ana P; Mansur, Herman S; Mansur, Alexandra A; Oliveira, Luiz C A; de Castro, Cinthia S

2017-07-01

This work describes the synthesis of catalysts based on red mud/polyethylene terephthalate (PET) composites and their subsequent heat treatment under N 2 atmosphere. The materials were characterized by scanning electron microscopy (SEM), temperature programmed reduction (TPR), Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), thermogravimetric (TG) analysis and N 2 adsorption/desorption. The catalysts were evaluated in the oxidative desulfurization reaction of dibenzothiophene (DBT) in a biphasic system. The results indicated that the PET impregnation on red mud increased the affinity of the catalyst with the nonpolar phase (fuel), in which the contaminant was dissolved, allowing a higher conversion (up to 80%) and selectivity to the corresponding dibenzothiophene sulfone. The sulfone compound is more polar than DBT and diffused into the polar solvent as indicated by the data obtained via gas chromatography-mass spectrometry (GC-MS). Copyright © 2017. Published by Elsevier B.V.

Mesoporous CeO2 nanoparticles synthesized by an inverse miniemulsion technique and their catalytic properties in methane oxidation

NASA Astrophysics Data System (ADS)

Nabih, Nermeen; Schiller, Renate; Lieberwirth, Ingo; Kockrick, Emanuel; Frind, Robert; Kaskel, Stefan; Weiss, Clemens K.; Landfester, Katharina

2011-04-01

Cerium(IV) oxide nanoparticles were synthesized using an inverse miniemulsion technique with cerium nitrate hexahydrate as precursor. The resulting nanocrystallites are as small as 5 nm with a specific surface area of 158 m2 g - 1 after calcination at 400 °C. With the addition of cetyltrimethylammonium bromide (CTAB) or (poly(ethylene oxide)-b-poly(propylene oxide)-b-poly(ethylene oxide)) triblock copolymers (PEO-PPO-PEO) as template in the miniemulsion droplets, the specific surface area can be increased up to 255 m2 g - 1. The miniemulsions were characterized by dynamic light scattering (DLS) and the obtained oxides were examined by x-ray diffraction (XRD), nitrogen sorption (BET and BJH), and transmission electron microscopy (TEM). The catalytic activity of the resulting ceria was investigated for the temperature-programmed oxidation (TPO) of methane.

Key factor affecting the structural and textural properties of ZSM-5/MCM-41 composite

NASA Astrophysics Data System (ADS)

Boukoussa, Bouhadjar; Aouad, Nafissa; Hamacha, Rachida; Bengueddach, Abdelkader

2015-03-01

ZSM-5/MCM-41 micro/mesoporous composite materials were synthesized by the hydrothermal technique with alkali-treated ZSM-5 zeolite as source of silica and aluminum and characterized by various physico-chemical techniques such as X-ray diffraction (XRD), nitrogen sorption at 77 K, transmission electronic microscopy (TEM), FTIR spectroscopy and NH3 temperature programmed desorption (TPD) techniques. The effect of concentration of CTAB in the synthesis of these solids has been investigated, the mesopore volume, surface area and surface acidity decrease with increasing the concentration of CTAB. Increasing the CTAB concentration causes the recrystallization of zeolite ZSM-5 and it disadvantage the formation of mesoporous materials MCM-41. The catalytic activity of ZSM-5/MCM-41 materials has been evaluated in the Friedel-Crafts acylation of anisole with benzoyl chloride as alkylating agent. The results revealed the reaction to be influenced by surface area, pore volume and surface acidity.

Thermal effects on domain orientation of tetragonal piezoelectrics

NASA Astrophysics Data System (ADS)

Chang, Wonyoung

Thermal effects on electrical poling or mechanical grinding induced texture in tetragonal lead zirconate titanate (PZT) and lead titanate (PT) have been investigated using ex situ and in situ X-ray diffraction (XRD) with an area detector. According to previous results using ex situ XRD, domain configurations of poled samples after heat-treatment at or higher than the Curie temperature (TC) are similar to that of unpoled samples showing random domain distributions. The texture parameter called multiples of a random distribution (MRD) gradually decreases with increasing depoling temperature. On the other hand, using in situ XRD measurements, it was found that the MRD maximum for soft PZT initially increases with temperature up to approximately 100°C and then falls to unity at temperatures approaching the TC, whereas the MRD of hard PZT and PT initially undergoes a smaller increase or no change. Mechanical strain energy has an apparent effect on domain wall mobility. In contrast with previous results on electrical poling, mechanically-ground PT and soft PZT materials retained strong ferroelastic textures during thermal cycling, even after excursions to temperatures slightly above the TC . For the ground PT, it was found that repeated cycling above T C results in changes in both peak intensity and peak position, whereas the ground soft PZT undergoes the decrease in intensity of the (002) reflection after the first cycle of heating. Residual stresses in the surface region from grinding resulted in domain wall motion and the retention of textures in annealed samples. The research in this thesis demonstrates that the magnitude of loading applied to the sample surface, the speed used for grinding, or the grit size, can greatly affect the grinding induced damage zone and the depoling behavior of piezoelectric ceramics. Among the possible effects of grinding conditions on surface textures, one of particular interest is the effect of mechanical stresses produced during grinding on the texture intensity in the ground surface region. Inhibited depoling of ground PT materials under different loading conditions investigated by in situ texture measurements between room temperature and approximately 100°C above the Curie temperature demonstrates the effects of residual stresses. For all the ground PT and soft PZT samples, there was little or no evidence of time dependence for domain reorientation at the whole annealing temperature range. In addition, both ground PT and soft PZT materials under lower loading conditions showed a gradual depoling behavior with increasing heat treatment temperature, whereas ground materials under higher loading conditions retained relatively strong ferroelastic texture up to temperatures around their respective TC, and then underwent a drastic change in MRD at temperatures above TC. Compared to the ground soft PZT materials, all the ground PT samples still maintained high MRD values after heat treatment above TC.

Structural and Magnetic Response in Bimetallic Core/Shell Magnetic Nanoparticles

PubMed Central

Nairan, Adeela; Khan, Usman; Iqbal, Munawar; Khan, Maaz; Javed, Khalid; Riaz, Saira; Naseem, Shahzad; Han, Xiufeng

2016-01-01

Bimagnetic monodisperse CoFe2O4/Fe3O4 core/shell nanoparticles have been prepared by solution evaporation route. To demonstrate preferential coating of iron oxide onto the surface of ferrite nanoparticles X-ray diffraction (XRD), High resolution transmission electron microscope (HR-TEM) and Raman spectroscopy have been performed. XRD analysis using Rietveld refinement technique confirms single phase nanoparticles with average seed size of about 18 nm and thickness of shell is 3 nm, which corroborates with transmission electron microscopy (TEM) analysis. Low temperature magnetic hysteresis loops showed interesting behavior. We have observed large coercivity 15.8 kOe at T = 5 K, whereas maximum saturation magnetization (125 emu/g) is attained at T = 100 K for CoFe2O4/Fe3O4 core/shell nanoparticles. Saturation magnetization decreases due to structural distortions at the surface of shell below 100 K. Zero field cooled (ZFC) and Field cooled (FC) plots show that synthesized nanoparticles are ferromagnetic till room temperature and it has been noticed that core/shell sample possess high blocking temperature than Cobalt Ferrite. Results indicate that presence of iron oxide shell significantly increases magnetic parameters as compared to the simple cobalt ferrite. PMID:28335200

Effect of Co doping on the magnetic and DC electrical properties of Mn-Zn nanoferrites

NASA Astrophysics Data System (ADS)

Khandan Fadafan, H.; Lotfi Orimi, R.; Nezhadeini, S.

2018-06-01

In this study, Cobalt-Manganese-Zinc nanoferrites with the formula CoxMn0.5-xZn0.5Fe2O4 with x = 0.0, 0.1, 0.3, and 0.5 prepared by chemical Co-precipitation method. Then the structure and morphology of the synthesized nanoparticles were characterized by X-ray diffraction (XRD) and transmitting electron microscopy (TEM), respectively. The XRD patterns indicated the formation of single-phased cubic structure of spinel ferrite in nanometer size with no minor phase. The TEM image showed the formation of nanoparticles with average size of about 40 nm and normal size distribution. The magnetic measurements of the nanoparticles were done at room temperature using a vibrating sample magnetometer (VSM). Results exhibited a super-paramagnetic like behavior for some of the samples. DC electrical resistivity measurements were carried out by two-probe technique from 25 to 250 °C and showed decreasing of the resistivity with temperature meanwhile passing a transition to form of a peak. The peaks values observed near the Curie temperatures of samples suggest that anomaly behavior can attributed to spin canting associated with the phase transition from para to ferromagnetic state at TC.

Effect of different conventional melt quenching technique on purity of lithium niobate (LiNbO3) nano crystal phase formed in lithium borate glass

NASA Astrophysics Data System (ADS)

Kashif, Ismail; Soliman, Ashia A.; Sakr, Elham M.; Ratep, Asmaa

2012-01-01

The glass system (45Li2O + 45B2O3 + 10Nb2O5) was fabricated by the conventional melt quenching technique poured in water, at air, between two hot plates and droplets at the cooled surface. The glass and glass ceramics were studied by differential thermal analysis (DTA) and X-ray diffraction (XRD). The as quenched samples poured in water and between two hot plates were amorphous. The samples poured at air and on cooled surface were crystalline as established via X-ray powder diffraction (XRD) studies. Differential thermal analysis was measured. The glass transition temperature (Tg) and the crystallization temperatures were calculated. Lithium niobate (LiNbO3) was the main phase in glass ceramic poured at air, droplets at the cooled surface and the heat treated glass sample at 500, 540 and 580 °C in addition to traces from LiNb3O8. Crystallite size of the main phases determined from the X-ray diffraction peaks is in the range of <100 nm. The fraction of crystalline (LiNbO3) phase decreases with increase in the heat treatment temperature.

Destruction of decabromodiphenyl ether (BDE-209) in a ternary carbonate molten salt reactor.

PubMed

Yao, Zhi-tong; Li, Jin-hui; Zhao, Xiang-yang

2013-09-30

Soil contamination by PBDEs has become a significant environmental concern and requires appropriate remediation technologies. In this study, the destruction of decabromodiphenyl ether (BDE-209) in a ternary molten salt (Li, Na, K)2 CO3 reactor was evaluated. The effects of reaction temperature, additive amount of BDE-209 and salt mixture, on off-gas species, were investigated. The salt mixture after reaction was characterized by XRD analysis and a reaction pathway proposed. The results showed that the amounts of C2H6, C2H4, C4H8 and CH4 in the off-gas decreased with increases in temperature, while the CO2 level increased. When the reaction temperature reached 750 °C, incomplete combustion products (PICs) were no longer detected. Increasing BDE-209 loading was not helpful for the reaction, as more PICs were produced. Larger amounts of salt mixture were helpful for the reaction and PICs were not observed with the mole ratio 1: 2000 of BDE-209 to carbonate melt. XRD analysis confirmed the capture of bromine in BDE-209 by the molten salt. Copyright © 2013 Elsevier Ltd. All rights reserved.

Characterization of bismuth selenide (Bi2Se3) thin films obtained by evaporating the hydrothermally synthesised nano-particles

NASA Astrophysics Data System (ADS)

Indirajith, R.; Rajalakshmi, M.; Gopalakrishnan, R.; Ramamurthi, K.

2016-03-01

Bismuth selenide (Bi2Se3) was synthesized by hydrothermal method at 200 °C and confirmed by powder X-ray diffraction (XRD) studies. The synthesized material was utilized to deposit bismuth selenide thin films at various substrate temperatures (Room Temperature-RT, 150 °C, 250 °C, 350 °C and 450 °C) by electron beam evaporation technique. XRD study confirmed the polycrystalline nature of the deposited Bi2Se3films. Optical transmittance spectra showed that the deposited (at RT) films acquire relatively high average transmittance of 60%in near infrared region (1500-2500 nm). An indirect allowed optical band gap calculated from the absorption edge for the deposited films is ranging from 0.62 to 0.8 eV. Scanning electron and atomic force microscopy analyses reveal the formation of nano-scale sized particles on the surface and that the nature of surface microstructures is influenced by the substrate temperature. Hall measurements showed improved electrical properties, for the films deposited at 350 °C which possess 2.8 times the mobility and 0.9 times the resistivity of the films deposited at RT.

Optical and superparamagnetic behavior of ZnFe2O4 nanoparticles

NASA Astrophysics Data System (ADS)

Lal, Ganesh; Punia, Khushboo; Dolia, S. N.; Kumar, Sudhish

2018-05-01

Nanoparticles of zinc ferrite have been synthesized using a low temperature citrate sol-gel route and characterized by powder X-ray diffraction (XRD), Raman & UV-Vis-NIR spectroscopic and SQUID magnetometry measurements. Analysis of XRD pattern and Raman spectrum confirmed that the synthesized ZnFe2O4 sample crystallizes in single phase fcc spinel ferrite structure and the average particle size of nanoparticles is estimated to 24nm. Optical absorption study shows that maximum photo absorption take place in the visible band and peaking in UV band at 206nm and the band gap energy is estimated to Eg = 2.1eV. Zero Field Cooled (ZFC) and Field Cooled (FC) modes of magnetization down to 5K and in fields up to 20kOe shows that ZnFe2O4 nanoparticles exhibits superparamagnetism with high magneto-crystalline anisotropy and high magnetization. Small difference of 9K between the separation temperature TS=˜30K and blocking temperature TB= 21K are suggestive of the formation of ferromagnetic clusters and a narrow particle size distribution of the nanoparticles in superparamagnetic ZnFe2O4 nanoparticles.

Preparation, quantitative surface analysis, intercalation characteristics and industrial implications of low temperature expandable graphite

NASA Astrophysics Data System (ADS)

Peng, Tiefeng; Liu, Bin; Gao, Xuechao; Luo, Liqun; Sun, Hongjuan

2018-06-01

Expandable graphite is widely used as a new functional carbon material, especially as fire-retardant; however, its practical application is limited due to the high expansion temperature. In this work, preparation process of low temperature and highly expandable graphite was studied, using natural flake graphite as raw material and KMnO4/HClO4/NH4NO3 as oxidative intercalations. The structure, morphology, functional groups and thermal properties were characterized during expanding process by Fourier transform infrared spectroscopy (FTIR), Raman spectra, thermo-gravimetry differential scanning calorimetry (TG-DSC), X-ray diffraction (XRD), and scanning electron microscope (SEM). The analysis showed that by oxidation intercalation, some oxygen-containing groups were grafted on the edge and within the graphite layer. The intercalation reagent entered the graphite layer to increase the interlayer spacing. After expansion, the original flaky expandable graphite was completely transformed into worm-like expanded graphite. The order of graphite intercalation compounds (GICs) was proposed and determined to be 3 for the prepared expandable graphite, based on quantitative XRD peak analysis. Meanwhile, the detailed intercalation mechanisms were also proposed. The comprehensive investigation paved a benchmark for the industrial application of such sulfur-free expanded graphite.

Optical, structural, and nuclear scientific studies of AlGaN with high Al composition

NASA Astrophysics Data System (ADS)

Lin, Tse Yang; Chung, Yee Ling; Li, Lin; Yao, Shude; Lee, Y. C.; Feng, Zhe Chuan; Ferguson, Ian T.; Lu, Weijie

2010-08-01

AlGaN epilayers with higher Al-compositions were grown by Metalorganic Chemical Vapor Deposition (MOCVD) on (0001) sapphire. Trimethylgallium (TMGa), trimethylaluminium (TMAl) and NH3 were used as the source precursors for Ga, Al, and N, respectively. A 25 nm AlN nucleation layer was first grown at low-temperature of 590 °C at 300 Torr. Followed, AlxGa1-xN layers were grown at 1080 °C on low-temperature AlN nucleation layers. The heterostructures were characterized by a series of techniques, including x-ray diffraction (XRD), Rutherford backscattering (RBS), photoluminescence (PL), scanning electron microscopy (SEM) and Raman scattering. Precise Al compositions were determined through XRD, RBS, and SEM combined measurements. Room Temperature Raman Scattering spectra shows three major bands from AlGaN alloys, which are AlN-like, A1 longitudinal optical (LO) phonon modes, and E2 transverse optical (TO) band, respectively, plus several peak comes from the substrate. Raman spectral line shape analysis lead to an optical determination of the electrical property free carrier concentration of AlGaN. The optical properties of AlGaN with high Al composition were presented here.

Low carrier semiconductor like behavior in Lu3Ir4Ge13 single crystal

NASA Astrophysics Data System (ADS)

Kumar, Anil; Matteppanavar, Shidaling; Thamizhavel, A.; Ramakrishnan, S.

2018-04-01

Single crystal of Lu3Ir4Ge13 crystallizing in the Yb3Rh4Sn13-type cubic crystal structure has been grown by Czochralski method in a tetra-arc furnace. In this paper we report on the crystal structure, magnetic and transport properties of Lu3Ir4Ge13. The analysis of the powder x-ray diffraction (XRD) studies revealed that Lu3Ir4Ge13 crystallizes in a cubic structure with the space group Pm-3n, no. 223. The lattice parameter was obtained from the Rietveld refinement of the room temperature XRD data which amounts to 8.904 (3) Å with low R factors. The temperature dependence of the resistivity exhibited semiconductor like behavior till 1.8 K, with a broad hump around 15 - 62 K. This hump was observed in both warming and cooling cycle with a very small hysteresis, it may be due to the existence of structural transition from high - low symmetry. The temperature dependent magnetization data shows the diamagnetic behavior with an anomaly around 70 K, which is well supported by the derivative of resistivity data.

Crystal structure and physicochemical characterization of ambazone monohydrate, anhydrous, and acetate salt solvate.

PubMed

Muresan-Pop, Marieta; Braga, Dario; Pop, Mihaela M; Borodi, Gheorghe; Kacso, Irina; Maini, Lucia

2014-11-01

The crystal structures of the monohydrate and anhydrous forms of ambazone were determined by single-crystal X-ray diffraction (SC-XRD). Ambazone monohydrate is characterized by an infinite three-dimensional network involving the water molecules, whereas anhydrous ambazone forms a two-dimensional network via hydrogen bonds. The reversible transformation between the monohydrate and anhydrous forms of ambazone was evidenced by thermal analysis, temperature-dependent X-ray powder diffraction and accelerated stability at elevated temperature, and relative humidity (RH). Additionally, a novel ambazone acetate salt solvate form was obtained and its nature was elucidated by SC-XRD. Powder dissolution measurements revealed a substantial solubility and dissolution rate improvement of acetate salt solvated form in water and physiological media compared with ambazone forms. Also, the acetate salt solvate displayed good thermal and solution stability but it transformed to the monohydrate on storage at elevated temperature and RH. Our study shows that despite the requirement for controlled storage conditions, the acetate salt solvated form could be an alternative to ambazone when solubility and bioavailability improvement is critical for the clinical efficacy of the drug product. © 2014 Wiley Periodicals, Inc. and the American Pharmacists Association.

Role of Ga particulates on the structure and optical properties of Y3(Al,Ga)5O12:Tb thin films prepared by PLD

NASA Astrophysics Data System (ADS)

Yousif, A.; Duvenhage, M. M.; Ntwaeaborwa, O. M.; Swart, H. C.

2018-04-01

Y3(Al,Ga)5O12:Tb thin films (70 nm) have been prepared by pulsed laser deposition on a Si (100) substrate at the substrate temperature of 300 °C. The effect of annealing time on the structural, morphological and luminescence properties of Y3(Al,Ga)5O12:Tb thin films at 800 °C were studied. The crystal structure of the samples was studied by X- ray diffraction (XRD) and showed shifts in the peak positions to lower diffraction angles for the annealed film compared to the XRD peak positions of the commercial Y3(Al,Ga)5O12:Tb powder. A new excitation band different from the original Y3(Al,Ga)5O12:Tb powder was also observed for the annealed films. The shift in the XRD pattern and the new excitation band for the annealed film suggested that the films were enriched with Ga after annealing.

Plasma Sprayed Hydroxyapatite Coatings: Influence of Spraying Power on Microstructure

NASA Astrophysics Data System (ADS)

Mohd, S. M.; Abd, M. Z.; Abd, A. N.

2010-03-01

The plasma sprayed hydroxyapatite (HA) coatings are used on metallic implants to enhance the bonding between the implant and bone in human body. The coating process was implemented at different spraying power for each spraying condition. The coatings formed from a rapid solidification of molten and partly molten particles that impact on the surface of substrate at high velocity and high temperature. The study was concentrated on different spraying power that is between 23 to 31 kW. The effect of different power on the coatings microstructure was investigated using scanning electron microscope (SEM) and phase composition was evaluated using X-ray diffraction (XRD) analysis. The coatings surface morphology showed distribution of molten, partially melted particles and some micro-cracks. The produced coatings were found to be porous as observed from the cross-sectional morphology. The coatings XRD results indicated the presence of crystalline phase of HA and each of the patterns was similar to the initial powder. Regardless of different spraying power, all the coatings were having similar XRD patterns.

A novel in situ synthesis of SiBCN-Zr composites prepared by a sol-gel process and spark plasma sintering.

PubMed

Miao, Yang; Yang, Zhihua; Liang, Bin; Li, Quan; Chen, Qingqing; Jia, Dechang; Cheng, Yi-Bing; Zhou, Yu

2016-08-09

In the work reported here, SiBCN amorphous powders were first prepared by a mechanical alloying technique, employing cubic silicon, graphite and hexagonal boron nitride powders as raw materials. Zirconia was then introduced via sol-gel methods. The resulting powder composite was then consolidated via SPS sintering. The SPS sintering sample was evaluated using XRD, SEM and TEM. XRD reveals a chemical transformation wherein amorphous BN(C) and ZrO2 form the primary ZrC and ZrB2 phases after SPS processing along with SiC and BN(C). Thereafter ZrC reacts with BN(C) completely to form ZrB2. The reaction starts at the temperature of 1500 °C and is complete at the temperature of 1900 °C. The fracture toughness of the sintered composites reaches 4.9 ± 0.2 MPa m(1/2) due to the presence of the laminated structure of the BN(C) phase.

Preparation and characterization of ultrafine nanoparticles of Cu doped lithium tetraborate

NASA Astrophysics Data System (ADS)

Khalilzadeh, Nasrin; Saion, Elias Bin; Mirabolghasemi, Hamed; Crouse, Karen A.; Shaari, Abdul Halim Bin; Hashim, Mansor Bin

This study details an innovative single-step thermal synthesis of nano-sized lithium tetraborate doped with 0.1 %wt copper and its characterization. The heating temperature for the synthesis of the nanoparticle material was optimized by variation between 200 and 850 °C. The optimum amount of polyvinyl pyrrolidone (PVP) the capping agent was determined to be 0.027 mol per 1 g LTB-Cu. The calcination time was 2 h. Characterization of the samples was carried out using Thermogravimetry Analysis (TGA), Derivative Thermogravimetry (DTG), Differential Scanning Calorimetry (DSC), Fourier Transform Infrared (FTIR) Spectroscopy, X-ray diffractometer (XRD), transmission electron microscopy (TEM) and Ultraviolet-Visible (UV-Vis) spectroscopy. The product was thermally stable above 450 °C. FTIR, XRD and TEM results confirmed the formation of pure nano-crystalline copper doped lithium tetraborate between 450 and 750 °C. The optical bandgap was estimated to be 5.02-6.05 eV in the presence of different amounts of PVP at various calcination temperatures.

Hydrogen Gas Sensing Characteristics of Nanostructured NiO Thin Films Synthesized by SILAR Method

NASA Astrophysics Data System (ADS)

Karaduman, Irmak; Çorlu, Tugba; Yıldırım, M. Ali; Ateş, Aytunç; Acar, Selim

2017-07-01

Nanostructured NiO thin films have been synthesized by a facile, low-cost successive ionic layer adsorption and reaction (SILAR) method, and the effects of the film thickness on their hydrogen gas sensing properties investigated. The samples were characterized by scanning electron microscopy (SEM), x-ray diffraction (XRD) analysis, and energy-dispersive x-ray analysis. The XRD results revealed that the crystallinity improved with increasing thickness, exhibiting polycrystalline structure. SEM studies showed that all the films covered the glass substrate well. According to optical absorption measurements, the optical bandgap decreased with increasing film thickness. The gas sensing properties of the nanostructured NiO thin films were studied as a function of operating temperature and gas concentration. The samples showed good sensing performance of H2 gas with high response. The maximum response was 75% at operating temperature of 200°C for hydrogen gas concentration of 40 ppm. These results demonstrate that nanostructured NiO thin films synthesized by the SILAR method have potential for application in hydrogen detection.

Alternating current response studies on nickel ferrite-niobium composite at room temperature

NASA Astrophysics Data System (ADS)

Reddy, L. P. Babu; Rajprakash, H. G.; Chethan, B.; Vijayakumari, S. C.; Ravikiran, Y. T.

2018-05-01

In the present research NDNF -Niobium Pentaxide doped Nickel Ferrite [NiFe2O4-Nb2O5-50%] composite was prepared by Mechano-Chemical mixing of NiFe2O4 [NF] with Nb2O5. NF and the NDNF were structurally characterized by four transform infrared spectroscopy [FTIR] and X-ray diffraction [XRD] techniques. The presence of characteristic absorption bands of NF and Nb2O5 in the FTIR spectrum of NDNF with small shift confirmed interfacial interaction of NF with Nb2O5. XRD studies also confirm interfacial interaction between NF and Nb2O5 in the composite and crystalline nature with an average crystallite size of 30nm. The Alternating Current (AC) response parameters of NF and the NDNF were comparatively studied in the frequency range 100Hz-1MHz at room temperature. Increase in AC conductivity of the NDNF has compared to NF was observed and discussed based on the electron hole exchange mechanism.

Sol-gel synthesis and characterizations of crystalline NaGd(WO4)2 powder for anisotropic transparent ceramic laser application

NASA Astrophysics Data System (ADS)

Durairajan, A.; Thangaraju, D.; Balaji, D.; Moorthy Babu, S.

2013-02-01

NaGd(WO4)2 powders were synthesized at different pH (3.5, 4.5, 5.5, 6.5 and 7.5) values by conventional Pechini method. Sodium and gadolinium nitrate salts and ammonium paratungstate are used as starting precursors. Metal cations were chelated by citric acid and individual citrates were bound together with ethylene glycol. Synthesized gel was analyzed using differential thermal analysis (DTA), thermo gravimetric (TG) and FT-IR spectroscopy to understand the degradation of gel and formation of metal citrates. Calcined powders (250, 600, 700 and 800 °C) were characterized by powder XRD, FT-IR, Raman and FE-SEM analysis. The temperature dependent phase formation was examined by powder XRD. The morphological changes at different pH derived powders were observed with FE-SEM micrographs. Stepwise organic liberation with respect to temperature and presence of carbon content in the pre-fired powder were analyzed using FT-IR analysis. Raman spectrum reveals disordered tungstate vibrations in the NGW matrix.

Effect of annealing on structure, morphology and optoelectronic properties of nanocrystalline CuO thin films

NASA Astrophysics Data System (ADS)

Jundale, D. M.; Pawar, S. G.; Patil, S. L.; Chougule, M. A.; Godse, P. R.; Patil, V. B.

2011-10-01

The nanocrystalline CuO thin films were prepared on glass substrates by the sol-gel method. The structural, morphological, electrical and optical properties of CuO thin films, submitted to an annealing treatment in the 400-700 °C ranges are studied by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), Four Probe Technique and UV-visible spectroscopic. XRD measurements show that all the films are crystallized in the monoclinic phase and present a random orientation. Four prominent peaks, corresponding to the (110) phase (2θ≈32.70°), (002) phase (2θ≈35.70°), (111) phase (2θ≈38.76°) and (202) phase (2θ≈49.06°) appear on the diffractograms. The crystallite size increases with increasing annealing temperature. These modifications influence the microstructure, electrical and optical properties. The optical band gap energy decreases with increasing annealing temperature. These mean that the optical quality of CuO films is improved by annealing.

Structural characteristics and properties of the regenerated silk fibroin prepared from formic acid.

PubMed

Um, I C; Kweon, H Y; Park, Y H; Hudson, S

2001-08-20

Structural characteristics and thermal and solution properties of the regenerated silk fibroin (SF) prepared from formic acid (FU) were compared with those of SF from water (AU). According to the turbidity and shear viscosity measurement, SF formic acid solution was stable and transparent, no molecular aggregations occurred. The sample FU exhibited the beta-sheet structure, while AU random coil conformation using Fourier transform infrared (FTIR), X-ray diffraction (XRD), and differential scanning calorimetry. The effects of methanol treatment on samples were also examined. According to the measurement of crystallinity (XRD) and crystallinity index (FTIR), the concept of long/short-range ordered structure formation was proposed. Long-range ordered crystallites are predominantly formed for methanol treated SF film while SF film cast from formic acid favors the formation of short-range ordered structure. The relaxation temperatures of SF films measured by dynamic thermomechanical analysis supported the above mechanism due to the sensitivity of relaxation temperature on the short-range order.

Study on defect properties of nanocrystalline TiO2 during phase transition by positron annihilation lifetime

NASA Astrophysics Data System (ADS)

Zheng, F.; Liu, Y.; Liu, Z.; Dai, Y.-Q.; Fang, P.-F.; Wang, S.-J.

2012-08-01

The defect properties of nanocrystalline TiO2 were investigated by positron annihilation lifetime spectroscopy (PALS) and X-ray diffraction (XRD) as a function of annealed temperature that ranged from 300 to 850 °C. Below 500 °C, the measured positron lifetimes of τ1 (200-206 ps) and τ2 (378-402 ps) revealed the existence of mono-vacancy and vacancy-clusters at grain surface and in the micro-void of intergranular region. Between 500 and 750 °C, the phase transition from anatase to rutile was probed by the variations of positron lifetime and XRD pattern. With the increasing temperature from 500 to 850 °C, the positron lifetime τ1, τ2 and its intensity I2 sharply decreased from 200 ps, 378 ps, and 60% to 135 ps, 274 ps, and 33%, respectively. The results clearly indicate that the mono-vacancy or vacancy-clusters at grain surface and micro-voids between the grains were annealed out during the phase transition.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Deus, R.C.; Cortés, J.A., E-mail: leandrosrr89@gmail.com; Ramirez, M.A.

Highlights: • CeO{sub 2} nanoparticles were obtained by microwave-hydrothermal method. • Rietveld refinement reveals a cubic structure. • KOH mineralizer agent exhibit weak agglomeration at low temperature and shorter time. - Abstract: The structural and photoluminescent properties at room temperature of CeO{sub 2} and La-doped CeO{sub 2} particles were undertaken. The obtained particles were synthesized by a microwave-assisted hydrothermal method (MAH) under different lanthanum contents. X-ray diffraction (XRD), Fourier transform infrared (FT-IR), Fourier transform Raman (FT-Raman), Ultra-violet spectroscopy (UV–vis) and photoluminescence (PL) measurements were carried out. XRD revealed that the powders are free of secondary phases and crystallize in themore » cubic structure. Raman data show that increasing La doping content increase oxygen vacancies due to lattice expansion. The UV/vis absorption spectroscopy suggested the presence of intermediate energy levels in the band gap of structurally ordered powders. Lanthanum addition creates oxygen vacancies and shifts the photoluminescence in the low energy range leading to intense PL emission.« less

Structural and electrical properties of different vanadium oxide phases in thin film form synthesized using pulsed laser deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Majid, S. S., E-mail: suhailphy276@gmail.com; Rahman, F.; Shukla, D. K.

2015-06-24

We present here the structural and electrical properties of the thin films of V{sub 2}O{sub 3} (Vanadium sesquioxide) and V{sub 5}O{sub 9}. Both these oxide phases, V{sub 2}O{sub 3} and V{sub 5}O{sub 9}, have beenachieved on (001) orientedSi substrate using the V{sub 2}O{sub 5} target by optimizing the deposition parameters using pulsed laser deposition technique (PLD).Deposited films were characterized by X-ray diffraction(XRD)and four probe temperature dependent resistivity measurements. XRD studies reveal the V{sub 2}O{sub 3} and V{sub 5}O{sub 9} phases and the amount of strain present in both these films. The temperature dependency of electrical resistivity confirmed the characteristic metal-insulatormore » transitions (MIT) for both the films, V{sub 2}O{sub 3} and V{sub 5}O{sub 9}.« less

[Synthesis and spectral characteristic of Ga-Fe3O4 at room temperature].

PubMed

Wang, Jing; Deng, Tong; Yang, Cai-Qin; Lin, Yu-Long; Wang, Wei; Wu, Hai-Yan

2008-03-01

Gallium bearing ferrites with different gallium content were synthesized by oxidation of ferrous and gallium ions under alkaline condition and room temperature. The samples were subjected to IR, XRD, Mossbauer spectral analysis and magnetization characterization. The results indicated that the green-rust intermediate phase would be produced during the procedure of Ga-Fe3O4 formation, and the green-rust intermediate phase was converted to ferrites with spinel structure during the drying under hot-N2 atmosphere. With the introduction of gallium into the spinel structure, the interplanar crystal spacing of the spinel structure decreased, as indicated from XRD spectra, and the lattice vibration of M(T)-O-M(o) moved to the high-frequency resulting from IR spectra. A small amount gallium introduction entered the tetrahedral sites preferentially rather than the octahedral sites, and increasing gallium introduction would enhance the occupation of octahedral sites. Furthermore, a small content of gallium in the initial solution could prevent the formation of non-magnetic Fe2O3.

Synthesis of ZnO nanopencils using wet chemical method and its investigation as LPG sensor

NASA Astrophysics Data System (ADS)

Shimpi, Navinchandra G.; Jain, Shilpa; Karmakar, Narayan; Shah, Akshara; Kothari, D. C.; Mishra, Satyendra

2016-12-01

ZnO nanopencils (NPCs) were prepared by a novel wet chemical process, using triethanolamine (TEA) as a mild base, which is relatively simple and cost effective method as compared to hydrothermal method. ZnO NPCs were characterized using powder X-ray diffraction (XRD), Fourier Transform Infra-Red (FTIR) spectroscopy in mid-IR and far-IR regions, X-ray Photoelectron Spectroscopy (XPS), UV-vis (UV-vis) absorption spectroscopy, room temperature Photoluminescence (PL) spectroscopy and Field Emission Scanning Electron Microscopy (FESEM). ZnO NPCs obtained, were highly pure, uniform and monodispersed.XRD pattern indicated hexagonal unit cell structure with preferred orientation along the c-axis. Sensing behaviour of ZnO NPCs was studied towards Liquefied Petroleum Gas (LPG) at different operating temperatures. The study shows that ZnO NPCs were most sensitive and promising candidate for detection of LPG at 250 °C with gas sensitivity > 60%. The high response towards LPG is due to high surface area of ZnO NPCs and their parallel alignment.

Thermal stability and electrochemical properties of PVP-protected Ru nanoparticles synthesized at room temperature

NASA Astrophysics Data System (ADS)

Kumar, Manish; Devi, Pooja; Shivling, V. D.

2017-08-01

Stable ruthenium nanoparticles (RuNPs) have been synthesized by the chemical reduction of ruthenium trichloride trihydrate (RuCl3 · 3H2O) using sodium borohydride (NaBH4) as a reductant and polyvinylpyrrolidone (PVP) as a protecting agent in the aqueous medium at room temperature. The nanoparticles thus prepared were characterized by their morphology and structural analysis from transmission electron microscopy (TEM), X-ray powder diffraction (XRD), UV-vis spectroscopy, Fourier transformation infrared and thermogravimetric analysis (TGA) techniques. The TEM image suggested a homogeneous distribution of PVP-protected RuNPs having a small average diameter of 2-4 nm with a chain-like network structure. The XRD pattern also confirmed that a crystallite size is around 2 nm of PVP-protected RuNPs having a single broad peak. The thermal stability studied using TGA, indicated good stability and the electrochemical properties of these nanoparticles revealed that saturation current increases for PVP-protected RuNPs/GC.

Physical and optical studies of BaO-TeO2-TiO2-B2O3 glasses containing Cu2+ transition metal ion

NASA Astrophysics Data System (ADS)

Srinivas, B.; Kumar, R. Vijaya; Hameed, Abdul; Sagar, D. Karuna; Chary, M. Narasimha; Shareefuddin, Md.

2018-05-01

Glasses with the composition xBaO-(30-x) TeO2-10TiO2-59B2O3-1CuO (where x = 10, 15, 20 and 25 mole %) were prepared by melt quenching technique. The XRD studies were made on these glass samples at room temperature. The amorphous nature of the glass samples was confirmed from the XRD patterns. The physical parameters such as density (ρ), molar volume (Vm), average boron-boron separation (dB-B) and oxygen packing density (OPD) were calculated. The change in density and molar volume has been investigated in terms of the variation of BaO in the glass composition. The optical absorption spectra have been recorded at room temperature. The values of optical band gap have been estimated from the ASF and Tauc's methods. Both Tauc's and ASF methods have been showing progressively increasing indirect optical band gap values with the increase of BaO concentrations.

Characteristics of a thick film ethanol gas sensor made of mechanically treated LaFeO3 powder

NASA Astrophysics Data System (ADS)

Suhendi, Endi; Witra, Hasanah, Lilik; Syarif, Dani Gustaman

2017-05-01

In this work, fabrication of LaFeO3 thick film ceramics for ethanol gas sensor made of mechanically treated (milling) powder was studied. The thick films were fabricated using screen printing technique from LaFeO3 powder treated by HEM (High Energy Milling). The films were baked at 800°C for one hour and analyzed using XRD and SEM. Sensitivity of the films was studied by measuring resistance of them at various temperatures in a chamber containing air with and without ethanol gas. Data of XRD showed that the thick film crystalizes in orthorombic structure with space group of Pn*a. SEM data showed that the films consisted of small grains with grain size of about 225 nm. According to the electrical data, the LaFeO3 thick films that produced in this work could be applied as ethanol gas with operating temperature of about 275°C.

Synthesis, structural and optical properties of PVP coated transition metal doped ZnS nanoparticles

NASA Astrophysics Data System (ADS)

Desai, N. V.; Shaikh, I. A.; Rawal, K. G.; Shah, D. V.

2018-05-01

The room temperature photoluminescence (PL) of transition metal doped ZnS nanoparticles is investigated in the present study. The PVP coated ZnS nanoparticles doped with transition metals are synthesized by facile wet chemical co-precipitation method with the concentration of impurity 1%. The UV-Vis absorbance spectra have a peak at 324nm which shifts slightly to 321nm upon introduction of the impurity. The incorporation of the transition metal as dopant is confirmed by X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS). The particle size and the morphology are characterized by scanning electron microscopy (SEM), XRD and UV-Vis spectroscopy. The average size of synthesized nanoparticles is about 2.6nm. The room temperature photoluminescence (PL) of undoped and doped ZnS nanoparticles show a strong and sharp peak at 782nm and 781.6nm respectively. The intensity of the PL changes with the type of doping having maximum for manganese (Mn).

Thermal characteristic of limonite ore upon calcination and reduction

NASA Astrophysics Data System (ADS)

Febriana, Eni; Manaf, Azwar; Prasetyo, A. B.; Mayangsari, W.

2018-05-01

Thermal characteristics of the limonite laterite ore types have been studied using TG / DTA. There are four endothermic peaks at 250, 646, 900, and 1023 °C with a total mass loss of 10.07wt%. These four peaks correspond to the XRD results on samples calcined at 600-1000 °C. Analysis of TG / DTA to the mixture of limonite and graphite showed two endothermic reaction peaks at 641 and 900 °C and an exothermic peak at 1180 °C. Reduction of the limonite-graphite mixture was done by heating at 800-1100 °C for 1 hour, and the reduced samples were analyzed using XRD. The results indicate that the reduction process proceed completely at higher temperatures, indicated by the increasing intensity of kamacite and Fe metal phase, and the decrease of peak intensity of carbon due to reaction with metal oxides. At 1100 °C, intensity of Fe-metal decreased due to sintering of Fe which may occur because the temperature was too high.

Reduced graphene oxide composites with water soluble copolymers having tailored lower critical solution temperatures and unique tube-like structure

NASA Astrophysics Data System (ADS)

Namvari, Mina; Biswas, Chandra S.; Galluzzi, Massimiliano; Wang, Qiao; Du, Bing; Stadler, Florian J.

2017-03-01

Nanohybrids of graphene with water soluble polymer were synthesized using ‘grafting from’ method. GO, prepared by modified Hummers’ method, was first reacted with sodium azide. Alkyne-terminated RAFT-CTA was synthesized by reaction of propargyl alcohol and S-1-dodecyl-S’-(α,α‘-dimethyl-α”-acetic acid) trithiocarbonate. RAFT-CTA was grafted onto the GO sheets by facile click-reaction and subsequently, N-isopropylacrylamide (NIPAM) and N-ethyleacrylamide (NEAM) were polymerized on graphene sheets via RAFT polymerization method. The respective copolymers with different ratios were also prepared. The nanohybrids were characterized by FTIR, XRD, TGA, Raman, SEM, and AFM. Both SEM and AFM clearly showed rod-like structures for rGO-PNEAM. XRD showed a small peak at 2θ = 19.21°, corresponding to d-spacing ≈ 4.6 Å. In addition, the nanohybrids showed a very broad temperature range for the LCST in water between ca. 30 and 70 °C.

Crystal Structure Variations of Sn Nanoparticles upon Heating

NASA Astrophysics Data System (ADS)

Mittal, Jagjiwan; Lin, Kwang-Lung

2018-04-01

Structural changes in Sn nanoparticles during heating below the melting point have been investigated using differential scanning calorimetry (DSC), x-ray diffraction (XRD) analysis, electron diffraction (ED), and high-resolution transmission electron microscopy (HRTEM). DSC revealed that the heat required to melt the nanoparticles (28.43 J/g) was about half compared with Sn metal (52.80 J/g), which was attributed to the large surface energy contribution for the nanoparticles. ED and XRD analyses of the Sn nanoparticles revealed increased intensity for crystal planes having large interplaner distances compared with regular crystal planes with increasing heat treatment temperature (HTT). HRTEM revealed an increase in interlayer spacing at the surface and near joints between nanoparticles with the HTT, leading to an amorphous structure of nanoparticles at the surface at 220°C. These results highlight the changes that occur in the morphology and crystal structure of Sn nanoparticles at the surface and in the interior with increase of the heat treatment temperature.

Effect of RE (Nd3+, Sm3+) oxide on structural, optical properties of Na2O-Li2O-ZnO-B2O3 glass system

NASA Astrophysics Data System (ADS)

Hivrekar, Mahesh M.; Bhoyar, D. N.; Mande, V. K.; Dhole, V. V.; Solunke, M. B.; Jadhav, K. M.

2018-05-01

Zinc borate glass activated with rare earth oxide (Nd2O3, Sm2O3) of Na2O-Li2O-ZnO-B2O3 quaternary system has been prepared successfully by melt quenching method. The nucleation and growth of RE oxide were controlled temperature range 950-1000° C and rapid cooling at room temperature. The physical, structural and optical properties were characterized by using X-ray diffraction (XRD), SEM, Ultraviolet-visible spectroscopy (UV-Vis). XRD and SEM studies confirmed the amorphous nature, surface morphology of prepared zinc borate glass. The physical parameters like density, molar volume, molar mass of Nd3+, Sm3+ doped borate glass are summarized in the present article. The optical absorption spectra along with tauc's plot are presented. The optical energy band gap increases due to the addition of rare earth oxide confirming the role of network modifier.

Magnetization and transport properties of silver-sheathed (Hg, Re)Ba2Ca2Cu3O8+delta tapes

NASA Astrophysics Data System (ADS)

Su, J. H.; Sastry, P. V. P. S. S.; Schwartz, J.

2003-10-01

(Hg, Re)Ba2Ca2Cu3O8+delta ((Hg, Re)-1223) samples have been fabricated by wrapping Re0.2Ba2Ca2Cu3Oy precursor powder within Ag foil and pressing or rolling. The Ag/precursor composite is then reacted with CaHgO2 in sealed reaction tubes. X-ray diffraction (XRD) patterns showed only one superconducting phase, (Hg, Re)-1223, in agreement with magnetization measurements showing an onset critical temperature (Tc) of 132 K. The magnetization properties were studied by dc magnetic measurements. The irreversibility line (Hirr), deduced from magnetization hysteresis loops, is approximated by a power law, Hirr ~ (1 - T/Tc)n, with n ~ 2.5, indicating moderate coupling between CuO2 layers compared to YBa2Cu3O7 (n ~ 1.5) and Bi/Tl-based superconductors (n ~ 5.5). The temperature dependence of the magnetization hysteresis loop width DeltaM showed three regimes, dominated by weak links at low temperature (regime I), thermally activated depinning of vortices at intermediate temperature (regime II) and giant flux creep at high temperature (regime III), respectively. Two field dependences were found in the intragrain critical current density (Jmagc) versus applied field at various temperatures: a weak one at lower temperature (leq50 K) and a stronger one at high temperature (geq65 K), indicating a transition from vortex lattice to vortex liquid in the tapes. The transport critical current density (Jtranc) of ~3 × 103 A cm-2 at 4.2 K and self-field was comparable to those for bulk Hg-based superconductors, indicating granular nature of the samples, which was confirmed further by XRD, scanning electron microscopy (SEM) and magneto-optical imaging (MOI).

Temperature driven structural-memory-effects in carbon nanotubes filled with Fe3C nano crystals

NASA Astrophysics Data System (ADS)

Boi, Filippo S.; Zhang, Xiaotian; Corrias, Anna

2018-02-01

We report the observation of novel temperature-driven structural-memory-effects in carbon nanotubes (CNTs) filled with Fe3C nano-crystals. These structural-transitions were measured by means of temperature (T) dependent x-ray diffraction (XRD) in the T-range from 298 K to 12 K. A clear reversible 2θ-shift in the 002-peak of the graphitic-CNTs-walls is found with the decrease of the temperature. As determined by Rietveld refinement, such 2θ-shift translates in a not previously reported decrease in the value of the CNT graphitic c-axis with the decrease of the temperature (from 298 K to 12 K). Also, a clear reversible 2θ-shift in the 031 and 131 diffraction-peaks of Fe3C is observed within the same T-range. Rietveld refinements confirm the existence of such memory-effect and also reveal a gradual decrease of the 010-axis of Fe3C with the decrease of the temperature. These observations imply that the observed structural-memory-effect is a characteristic of CNTs when Fe3C is the encapsulated ferromagnet. The generality of such memory-effects was further confirmed by additional measurements performed on other types of CNTs characterized by continuous Fe3C-filling. XRD measurements in the T-range from 298 K to 673 K revealed also an unusual reversible decrease of the Fe3C-peak intensities with the increase of the temperature. These observations can have important implications on the magnetic data recording applications of these nanostructures by helping in better understanding the unusual temperature-dependent magnetic instabilities of iron-based nano-crystals which have been recently reported in literature.

Synthesis of Nanocrystalline CaWO4 as Low-Temperature Co-fired Ceramic Material: Processing, Structural and Physical Properties

NASA Astrophysics Data System (ADS)

Vidya, S.; Solomon, Sam; Thomas, J. K.

2013-01-01

Nanocrystalline scheelite CaWO4, a promising material for low-temperature co-fired ceramic (LTCC) applications, has been successfully synthesized through a single-step autoignition combustion route. Structural analysis of the sample was performed by powder x-ray diffraction (XRD), Fourier-transform infrared spectroscopy, and Raman spectroscopy. The XRD analysis revealed that the as-prepared sample was single phase with scheelite tetragonal structure. The basic optical properties and optical constants of the CaWO4 nanopowder were studied using ultraviolet (UV)-visible absorption spectroscopy, which showed that the material was a wide-bandgap semiconductor with bandgap of 4.7 eV at room temperature. The sample showed poor transmittance in the ultraviolet region but maximum transmission in the visible/near-infrared regions. The photoluminescence spectra recorded at different temperatures showed intense emission in the green region. The particle size estimated from transmission electron microscopy was 23 nm. The feasibility of CaWO4 for LTCC applications was studied from its sintering behavior. The sample was sintered at a relatively low temperature of 810°C to high density, without using any sintering aid. The surface morphology of the sintered sample was analyzed by scanning electron microscopy. The dielectric constant and loss factor of the sample measured at 5 MHz were found to be 10.50 and 1.56 × 10-3 at room temperature. The temperature coefficient of the dielectric constant was -88.71 ppm/°C. The experimental results obtained in this work demonstrate the potential of nano-CaWO4 as a low-temperature co-fired ceramic as well as an excellent luminescent material.

OMVPE Growth of Quaternary (Al,Ga,In)N for UV Optoelectronics (title change from A)

DOE Office of Scientific and Technical Information (OSTI.GOV)

HAN,JUNG; FIGIEL,JEFFREY J.; PETERSEN,GARY A.

We report the growth and characterization of quaternary AlGaInN. A combination of photoluminescence (PL), high-resolution x-ray diffraction (XRD), and Rutherford backscattering spectrometry (RBS) characterizations enables us to explore the contours of constant PL peak energy and lattice parameter as functions of the quaternary compositions. The observation of room temperature PL emission at 351nm (with 20% Al and 5% In) renders initial evidence that the quaternary could be used to provide confinement for GaInN (and possibly GaN). AlGaInN/GrdnN MQW heterostructures have been grown; both XRD and PL measurements suggest the possibility of incorporating this quaternary into optoelectronic devices.

Structure of chitosan thermosensitive gels containing graphene oxide

NASA Astrophysics Data System (ADS)

Tylman, Michał; Pieklarz, Katarzyna; Owczarz, Piotr; Maniukiewicz, Waldemar; Modrzejewska, Zofia

2018-06-01

The supramolecular hydrogels of chitosan and graphene oxide (GO) have been prepared at temperature of the human body, by controlling the concentration of GO and ratio of chitosan to GO. During the preparation of gels the sodium β-glycerophosphate (Na-β-GP) was used as a neutralizing agent. The structure of obtained gels was determined on the basis of FTIR spectra and XRD diffraction patterns. The results of structural studies have been referenced to gels without graphene oxide. It was found that the gels crystalline structure after the addition of GO does not change. The XRD diffraction patterns are characterized by a number of peaks associated with precipitated NaCl during drying and presence of sodium β-glycerophosphate.

Fabrication of high-k dielectric Calcium Copper Titanate (CCTO) target by solid state route

NASA Astrophysics Data System (ADS)

Tripathy, N.; Das, K. C.; Ghosh, S. P.; Bose, G.; Kar, J. P.

2016-02-01

CaCu3Ti4O12 (CCTO) ceramic pellet of 10mm diameter has been synthesized by adopting solid state route. The structural and morphological characterization of the ceramics sample was carried out by X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. XRD pattern revealed the CCTO phase formation, where as SEM micrograph shows the sample consisting of well defined grain and grain boundaries. The room temperature dielectric constant of the sample was found to be ∼ 5000 at 1kHz. After successful preparation of CCTO pellet, a 2 inch diameter CCTO sputtering target is also fabricated in order to deposit CCTO thin films for microelectronic applications.

DSC and Raman studies of silver borotellurite glasses

NASA Astrophysics Data System (ADS)

Kaur, Amandeep; Khanna, Atul; Gonzàlez, Fernando

2016-05-01

Silver borotellurite glasses of composition: xAg2O-yB2O3-(100-x-y)TeO2 (x=20-mol%, y = 0, 10, 20 and 30-mol%) were prepared and characterized by density, X-ray diffraction (XRD), differential scanning calorimetry, and Raman spectroscopy. XRD confirmed the amorphous structure of all samples. Density of glasses decreases while the glass transition temperature increases with increase in B2O3 content from 10 to 30-mol%. Raman study shows that coordination number of Te with oxygen decreases steadily from 3.42 to 3.18 on adding B2O3 due to the transformation of TeO4 into TeO3 units.

Ellipsometric study of Si(0.5)Ge(0.5)/Si strained-layer superlattices

NASA Technical Reports Server (NTRS)

Sieg, R. M.; Alterovitz, S. A.; Croke, E. T.; Harrell, M. J.

1993-01-01

An ellipsometric study of two Si(0.5)Ge(0.5)/Si strained-layer super lattices grown by MBE at low temperature (500 C) is presented, and results are compared with x ray diffraction (XRD) estimates. Excellent agreement is obtained between target values, XRD, and ellipsometry when one of two available Si(x)Ge(1-x) databases is used. It is shown that ellipsometry can be used to nondestructively determine the number of superlattice periods, layer thicknesses, Si(x)Ge(1-x) composition, and oxide thickness without resorting to additional sources of information. It was also noted that we do not observe any strain effect on the E(sub 1) critical point.

Triggering Incipient Ferroelectricity in Calcium Copper Titanate (CaCu3Ti4O12) ceramics through partial B-site substitution with Te4+ ion

NASA Astrophysics Data System (ADS)

Barman, Nabadyuti; Varma, K. B. R.

Double perovskite structured dielectric ceramic CaCu3Ti4- x TexO12 (CCTTO) (x = 0, 0.05, 0.1, 0.15, 0.2) was fabricated from the powder obtained by conventional solid state synthetic route. The room temperature XRD patterns for the x = 0, 0.05, 0.075 modified samples were confirmed to possess a single phase with cubic space group Im3by Rietveld refinement. But, the Rietveld refinement performed on XRD patterns recorded for the compositions corresponding to x = 0.1, 0.15, 0.2 shows the coexistence of the cubic phase (space group Im3; a = 7.4065Å) and tetragonal phase (space group I4/mcm; a = 7.369 Å and c = 6.967 Å). The dielectric properties of these ceramics were studied over a wide frequency (40Hz-2MHz) and temperature range (30-400K). The Te4+ doped samples (CCTTO) exhibited dielectric permittivity (?r) value of ~23-33X103 which is more than twice that of undoped CCTO (~11x103) at 1kHz. A decreasing trend in dielectric permittivity with increasing temperature, a signature of incipient ferroelectricity, was observed for all the samples. Barrett's formula was invoked to rationalize the dielectric permittivity variation as a function of temperature. The incipient ferroelectric behavior is correlated with soft phonon mode observed in temperature dependent Raman Spectroscopic studies. .

Structural, magnetic and electrical properties of a new double-perovskite LaNaMnMoO6 material.

PubMed

Borchani, Sameh Megdiche; Koubaa, Wissem Cheikh-Rouhou; Megdiche, Makrem

2017-11-01

Structural, magnetic, magnetocaloric, electrical and magnetoresistance properties of an LaNaMnMoO 6 powder sample have been investigated by X-ray diffraction (XRD), magnetic and electrical measurements. Our sample has been synthesized using the ceramic method. Rietveld refinements of the XRD patterns show that our sample is single phase and it crystallizes in the orthorhombic structure with Pnma space group. Magnetization versus temperature in a magnetic applied field of 0.05 T shows that our sample exhibits a paramagnetic-ferromagnetic transition with decreasing temperature. The Curie temperature T C is found to be 320 K. Arrott plots show that all our double-perovskite oxides exhibit a second-order magnetic phase transition. From the measured magnetization data of an LaNaMnMoO 6 sample as a function of the magnetic applied field, the associated magnetic entropy change |-ΔSM| and the relative cooling power (RCP) have been determined. In the vicinity of T C , |-ΔSM| reached, in a magnetic applied field of 8 T, a maximum value of ∼4 J kg -1  K -1 . Our sample undergoes a large magnetocaloric effect at near-room temperature. Resistivity measurements reveal the presence of an insulating-metal transition at Tρ = 180 K. A magnetoresistance of 30% has been observed at room temperature for 6 T, significantly larger than that reported for the A 2 FeMoO 6 (A = Sr, Ba) double-perovskite system.

Thermotropic phase transitions in Pb{sub 1−x}Sr{sub x}(Al{sub 1/3}Nb{sub 2/3}){sub 0.1}(Zr{sub 0.52}Ti{sub 0.48}){sub 0.9}O{sub 3} ceramics: Temperature dependent dielectric permittivity and Raman scattering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, C. Q.; Peng, L.; Jiang, K.

2015-06-15

The phase transitions of Pb{sub 1−x}Sr{sub x}(Al{sub 1/3}Nb{sub 2/3}){sub 0.1}(Zr{sub 0.52}Ti{sub 0.48}){sub 0.9}O{sub 3} (Sr-modified PAN-PZT) ceramics with Sr compositions of x = 2%, 5%, 10% and 15% have been investigated using X-ray diffraction (XRD), temperature dependent dielectric permittivity and Raman scattering. The XRD analysis show that the phase transition occurs between Sr composition of 5% and 10%. Based on the broad dielectric peaks at 100 Hz, the diffused phase transition from tetragonal (T) to cubic (C) structure shifts to lower temperature with increasing Sr composition. The dramatic changes of wavenumber and full width at half-maximum (FWHM) for E(TO{sub 4})′more » softing mode can be observed at morphotropic phase boundary (MPB). Moreover, the MPB characteristic shows a wider and lower trend of temperature region with increasing Sr composition. It could be ascribed to the diminishment of the energy barrier and increment of A-cation entropy. Therefore, the Sr-modified PAN-PZT ceramics unambiguously undergo two successive structural transitions (rhombohedral-tetragonal-cubic phase) with temperature from 80 to 750 K. Correspondingly, the phase diagram of Sr-modified PAN-PZT ceramics can be well depicted.« less

Synthesis of core–shell structured FAU/SBA-15 composite molecular sieves and their performance in catalytic cracking of polystyrene

PubMed Central

Du, Jinlong; Shi, Chunwei; Wu, Wenyuan; Bian, Xue; Chen, Ping; Cui, Qingzhu; Cui, Zhixuan

2017-01-01

Abstract Composite molecular sieves, FAU/SBA-15, having core-shell structure were synthesized. The synthesized composite sieves were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDS), pyrolysis fourier transform infrared (Py-FTIR) spectroscopy, temperature programmed desorption spectra (NH3-TPD), UV Raman spectroscopy, nuclear magnetic resonance (NMR) and other techniques. XRD, SEM, TEM, N2 adsorption-desorption, mass spectrometry, NMR and EDS results showed that the composite molecular sieve contained two pore channels. Py-FTIR results showed that the addition of HY molecular sieves improved the acidity of the composite zeolite. The crystallization mechanism during the growth of FAU/SBA-15 shell was deduced from the influence of crystallization time on the synthesis of FAU/SBA-15 core-shell structured composite molecular sieve. HY dissociated partially in H2SO4 solution, and consisted of secondary structural units. This framework structure was more stable than its presence in the isolated form on the same ring or in the absence of Al. Thus it played a guiding role and connected with SBA-15 closely through the Si-O bond. This resulted in the gradual covering of the exterior surface of FAU phase by SBA-15 molecular sieves. The presence of SBA-15 restricted the formation of the other high mass components and increased the selectivity towards ethylbenzene. PMID:29383044

Effect of calcination temperature on phase transformation and crystallite size of copper oxide (CuO) powders

NASA Astrophysics Data System (ADS)

Ratnawulan, Fauzi, Ahmad; AE, Sukma Hayati

2017-08-01

Copper oxide powder was prepared from Copper iron from South Solok, Indonesia. The samples was dried and calcined for an hour at temperatures of 145°C, 300°C,850°C, 1000°C. Phase transformation and crystallite size of the calcined powders have been investigated as a function of calcination temperature by room-temperature X-ray diffraction (XRD). It was seen that the tenorite, CuO was successfully obtained. With increasing calcining temperature, CuO transformed from malachite Cu2(CO3)(OH)2 to tenorite phase (CuO) and crystallite size of prepared samples increased from 36 nm to 76 nm.

Maltodextrin: A consummate carrier for spray-drying of xylooligosaccharides.

PubMed

Zhang, Liangqing; Zeng, Xianhai; Fu, Nan; Tang, Xing; Sun, Yong; Lin, Lu

2018-04-01

The aim of this study was to evaluate the influence of spray-drying on the powder qualities and microstructures of prebiotic xylooligosaccharides (XOS). The relationships between glass transition temperature (T g ) and XOS retention, moisture content, drying yield as well as specific surface area under different inlet air temperatures and maltodextrin concentrations were investigated. Antioxidant activity retention, hygroscopicity, color attributes, X-ray diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FT-IR) of the spray-dried XOS product were also assessed. The results indicated that an increase in inlet air temperature decreased the moisture content, hence the T g value was increased. Higher maltodextrin concentration increased the T g value, and was attributed to the molecular weight increase. The wall deposition was a tendency to occur when the temperature beyond the T g , reduced the drying yield. Higher temperature and wall deposition promoted the decomposition of XOS into monosaccharide. The crust formation rate of droplets and stickiness of microparticles were affected by T g , and hence, influenced the specific surface area. The antioxidant activity retention of XOS exhibited a concentration-dependent behavior. The hygroscopicity of the microparticles could be reduced by both of the low inlet air temperature and high maltodextrin concentration. According to the results of color attributes, XRD and SEM, the particles were colorless and amorphous, and tended to become more spherical and scattered with the addition of maltodextrin. The FT-IR analysis confirmed that no chemical reaction occurred between XOS and agent, which indicated that maltodextrin is a promising carrier for producing bioactive XOS powder. Copyright © 2018 Elsevier Ltd. All rights reserved.

Effect of deposition temperature on thermal stabilities of copper-carbon films in barrier-less Cu metallization

NASA Astrophysics Data System (ADS)

Zhu, Huan; Fu, Zhiqiang; Xie, Qi; Yue, Wen; Wang, Chengbiao; Kang, Jiajie; Zhu, Lina

2018-01-01

Copper-carbon alloy films have been applied in barrier-less Cu metallization as seed layers for improving the thermal stabilities. The effect of the deposition temperature on the microstructure and properties of C-doped Cu films on Si substrates was investigated. The films were prepared by ion beam-assisted deposition at various deposition temperatures by co-sputtering of Cu and graphite targets. No inter-diffusion between Cu and Si was observed in Cu(C) films throughout this experiment, because XRD patterns corresponding to their deep-level reaction product, namely, Cu3Si, were not observed in XRD patterns and EDS results of Cu(C) films. Amorphous carbon layer and SiC layer were found in the interface of Cu(C) as-deposited films when deposition temperature rose to 100 °C by TEM, high-resolution image and Fourier transformation pattern. The Cu(C) films deposited at 100 °C had the best thermal stabilities and the lowest electrical resistivity of 4.44 μW cm after annealing at 400 °C for 1 h. Cu agglomeration was observed in Cu(C) alloy films with deposition temperatures of 200, 300 and 400 °C, and the most serious agglomeration occurred in Cu(C) films deposited at 200 °C. Undesired Cu agglomeration resulted in a sharp increase in the resistivity after annealing at 300 °C for 1 h. The deposition temperature of 100 °C reflected the superior thermal stabilities of Cu(C) seed layers compared with those of other layers.

Characteristics of silica rice husk ash from Mojogedang Karanganyar Indonesia

NASA Astrophysics Data System (ADS)

Suryana, R.; Iriani, Y.; Nurosyid, F.; Fasquelle, D.

2018-05-01

Indonesia is one of the countries in the world as the most abundant rice producer. Many researchers have demonstrated that the highest composition in the rice husk ash (RHA) is silica. Some of the advantages in utilizing silica as the raw material is the manufacture of ceramics, zeolite synthesis, fabrication of glass, electronic insulator materials, and as a catalyst. The amount of silica from rice husk ash is different for each region. Therefore, the study of silica from RHA is still promising, especially rice organic fertilizers. In this study, the rice came from Mojogedang Karanganyar Indonesia. Rice husk was dried under the solar radiation. Then the rice husk was heated in two steps: the first step at a temperature of 300°C and the second step at a temperature of 1200°C with a holding time at 2 h and 1 h, respectively. Furthermore, the temperature of the second step was varied at 1400 °C and 1600 °C. This heating process produced RHA. The content of RHA was observed on the EDAX spectrums while the morphology was observed from SEM images. The crystal structure of RHA was determined from XRD spectrums. The EDAX spectrums showed that RHA composition was dominated by elements Si and O for all the heating temperature. SEM images showed an agglomeration towards larger domains as heating temperatures increase. Analysis of XRD spectra is polycrystalline silica formed with the significant crystal orientation at 101, 102 and 200. The intensity of 101 increases significantly with increasing temperature. It is concluded that the crystal growth in the direction of 101 is preferred.

Atomic oxygen recombination on the ODS PM 1000 at high temperature under air plasma

NASA Astrophysics Data System (ADS)

Balat-Pichelin, M.; Bêche, E.

2010-06-01

High temperature materials are necessary for the design of primary heat shields for future reusable space vehicles re-entering atmospheric planet at hypersonic velocity. During the re-entry phase on earth, one of the most important phenomena occurring on the heat shield is the recombination of atomic oxygen and this phenomenon is more or less catalyzed by the material of the heat shield. PM 1000 is planned to be use on the EXPERT capsule to study in real conditions its catalycity. Before the flight, it is necessary to perform measurements on ground test facility. Experimental data of the recombination coefficient of atomic oxygen under air plasma flow were obtained in the diffusion reactor MESOX on pre-oxidized PM 1000, for two total pressures 300 and 1000 Pa in the temperature range (850-1650 K) using actinometry and optical emission spectroscopy. In this investigation, the evolution of the recombination coefficient is dependent of temperature, pressure level and also of the chemical composition of the surface leading to one order of magnitude for a given temperature. The recombination coefficient is increasing with temperature and also dependent on the static pressure. The surface change due to the plasma exposure is inspected with SEM, XRD and XPS. As chromium oxide is the main part of the oxide layer formed during the oxidation in air plasma conditions, a sintered Cr 2O 3 sample was elaborated from powders to compare the data of the recombination coefficient obtained on PM 1000. Pre- and post-test analyses on the several materials were carried out using SEM, WDS, XRD and XPS.

Room Temperature Magnetic Behavior In Nanocrystalline Ni-Doped Zro2 By Microwave-Assisted Polyol Synthesis

NASA Astrophysics Data System (ADS)

Parimita Rath, Pragyan; Parhi, Pankaj Kumar; Ranjan Panda, Sirish; Priyadarshini, Barsharani; Ranjan Sahoo, Tapas

2017-08-01

This article, deals with a microwave-assisted polyol method to demonstrate a low temperature route < 250°C, to prepare a high temperature cubic zirconia phase. Powder XRD pattern shows broad diffraction peaks suggesting nanometric size of the particles. Magnetic behavior of 1-5 at% Ni doped samples show a threshold for substitutional induced room temperature ferromagnetism up to 3 at% of Ni. TGA data reveals that Ni-doped ZrO2 polyol precursors decompose exothermically below 300°C. IR data confirms the reduction of Zr(OH)4 precipitates to ZrO2, in agreement with the conclusions drawn from the TGA analysis.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sun, Pei; Fang, Z. Zak; Koopman, Mark

Hydrogen has been investigated for decades as a temporary alloying element to refine the microstructure of Ti-6Al-4V, and is now being used in a novel powder metallurgy method known as "hydrogen sintering and phase transformation". Pseudo-binary phase diagrams of (Ti-6Al-4V)-xH have been studied and developed, but are not well established due to methodological limitations. In this paper, in situ studies of phase transformations during hydrogenation and dehydrogenation of (Ti-6Al-4V)-xH alloys were conducted using high-energy synchrotron X-ray diffraction (XRD), thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The eutectoid phase transformation of β ↔ α + δ was observed in themore » (Ti-6Al-4V)-xH alloy via in situ synchrotron XRD at 211 °C with a hydrogen concentration of 37.5 at.% (measured using TGA-DSC). The relationships of hydrogen composition to partial pressure and temperature were investigated in the temperature range 450-900°C. Based on these results, a partial pseudo-binary phase diagram of (Ti-6Al-4V)-xH is proposed for hydrogen compositions up to 60 at.% in the temperature range 100-900°C. Using the data collected in real time under controlled parameters of temperature, composition and hydrogen partial pressure, this work characterizes relevant phase transformations and microstructural evolution for practical titanium-hydrogen technologies of Ti-6Al-4V.« less

Point defects in Cu 2ZnSnSe 4(CZTSe): Resonant X-ray diffraction study of the low-temperature order/disorder transition

DOE PAGES

Schelhas, L. T.; Stone, K. H.; Harvey, S. P.; ...

2017-07-25

We report that the interest in Cu 2ZnSn(S,Se) 4 (CZTS) for photovoltaic applications is motivated by similarities to Cu(In,Ga)Se 2 while being comprised of non-toxic and earth abundant elements. However, CZTS suffers from a V oc deficit, where the V oc is much lower than expected based on the band gap, which may be the result of a high concentration of point-defects in the CZTS lattice. Recently, reports have observed a low-temperature order/disorder transition by Raman and optical spectroscopies in CZTS films and is reported to describe the ordering of Cu and Zn atoms in the CZTS crystal structure. Tomore » directly determine the level of Cu/Zn ordering, we have used resonant-XRD, a site, and element specific probe of long range order. We used CZTSe films annealed just below and quenched from just above the transition temperature; based on previous work, the Cu and Zn should be ordered and highly disordered, respectively. Our data show that there is some Cu/Zn ordering near the low temperature transition but significantly less than high chemical order expected from Raman. Finally, to understand both our resonant-XRD results and the Raman results, we present a structural model that involves antiphase domain boundaries and accommodates the excess Zn within the CZTS lattice.« less

Role of Oxides and Porosity on High-Temperature Oxidation of Liquid-Fueled HVOF Thermal-Sprayed Ni50Cr Coatings

NASA Astrophysics Data System (ADS)

Song, B.; Bai, M.; Voisey, K. T.; Hussain, T.

2017-02-01

High chromium content in Ni50Cr thermally sprayed coatings can generate a dense and protective scale at the surface of coating. Thus, the Ni50Cr coating is widely used in high-temperature oxidation and corrosion applications. A commercially available gas atomized Ni50Cr powder was sprayed onto a power plant steel (ASME P92) using a liquid-fueled high velocity oxy-fuel thermal spray with three processing parameters in this study. Microstructure of as-sprayed coatings was examined using oxygen content analysis, mercury intrusion porosimetry, scanning electron microscope (SEM), energy-dispersive x-ray spectroscopy (EDX) and x-ray diffraction (XRD). Short-term air oxidation tests (4 h) of freestanding coatings (without boiler steel substrate) in a thermogravimetric analyzer at 700 °C were performed to obtain the kinetics of oxidation of the as-sprayed coating. Long-term air oxidation tests (100 h) of the coated substrates were performed at same temperature to obtain the oxidation products for further characterization in detail using SEM/EDX and XRD. In all samples, oxides of various morphologies developed on top of the Ni50Cr coatings. Cr2O3 was the main oxidation product on the surface of all three coatings. The coating with medium porosity and medium oxygen content has the best high-temperature oxidation performance in this study.

Ion beam modification of structural and optical properties of GeO2 thin films deposited at various substrate temperatures using pulsed laser deposition

NASA Astrophysics Data System (ADS)

Rathore, Mahendra Singh; Vinod, Arun; Angalakurthi, Rambabu; Pathak, A. P.; Singh, Fouran; Thatikonda, Santhosh Kumar; Nelamarri, Srinivasa Rao

2017-11-01

High energy heavy ion irradiation-induced modification of high quality crystalline GeO2 thin films grown at different substrate temperatures ranging from 100 to 500 °C using pulsed laser deposition has been investigated. The pristine films were irradiated with 100 MeV Ag7+ ions at fixed fluence of 1 × 1013 ions/cm2. These pristine and irradiated films have been characterized using X-ray diffraction, atomic force microscopy, Raman spectroscopy, Fourier transform infrared and photoluminescence spectroscopy. The XRD and Raman results of pristine films confirm the formation of hexagonal structure of GeO2 films, whereas the irradiation eliminates all the peaks except major GeO2 peak of (101) plane. It is evident from the XRD results that crystallite size changes with substrate temperature and SHI irradiation. The surface morphology of films was studied by AFM. The functional group of pristine and irradiated films was investigated by IR transmission spectra. Pristine films exhibited strong photoluminescence around 342 and 470 nm due to oxygen defects and a red shift in the PL bands is observed after irradiation. Possible mechanism of tuning structural and optical properties of pristine as well as irradiated GeO2 films with substrate temperature and ion beam irradiation has been reported in detail.

Synthesis of multifunctional clustered nano-Fe3O4 chitosan nanocomposite for biomedical applications

NASA Astrophysics Data System (ADS)

Villamin, Maria Emma; Kitamoto, Yoshitaka

2018-01-01

Clustered iron oxide nanoparticles covered with chitosan hydrogel (FeOx/Ch NC) have multiple potential functionalities in biomedical applications such as pH-controlled drug release, magnetic hyperthermia, and magnetic non-contact pH sensing. In the present study, the synthesis and characterization of FeOx/Ch NC are demonstrated. Moreover, the heating capability of the nanocomposites is also explored for the potential magnetic hyperthermia application by measuring the temperature curves under different AC frequencies (900 kHz to 2500 kHz). Monodispersed FeOx NPs are first synthesized via thermal decomposition. Then, dried FeOx NPs are combined with chitosan using a homogenizer to form the clustered composites. Synthesized composites are then characterized using XRD, TEM, and FTIR. Temperature curves are measured via a custom-built hyperthermia setup. Results show successful synthesis of clustered Fe3O4-chitosan nanocomposite with XRD peaks corresponding to magnetite (Fe3O4) structure. FTIR results show the presence of functional groups of chitosan (N-H, C-O) and FeOx NPs (Fe-O). These confirms the successful fabrication of FeOx/Ch NC. The temperature curves show maximum temperature changes of about 2°C to 22°C depending on the AC frequency. The heating rate is found to increase with the frequency, which suggests that the resonance frequency is higher than 2500 kHz.

Synthesis of Carbon Nanotubes and Nanospheres from Coconut Fibre and the Role of Synthesis Temperature on Their Growth

NASA Astrophysics Data System (ADS)

Adewumi, Gloria A.; Inambao, Freddie; Eloka-Eboka, Andrew; Revaprasadu, Neerish

2018-07-01

Carbon nanotubes (CNT) and carbon nanospheres were successfully synthesized from coconut fibre-activated carbon. The biomass was first carbonized then physically activated, followed by treatment using ethanol vapor at 700°C to 1100°C at 100°C intervals. The effect of synthesis temperature on the formation of the nanomaterials was studied using scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive x-ray spectrometry, x-ray diffraction (XRD), Fourier transform infrared microscopy (FTIR) and thermogravimetric analysis. SEM analysis revealed that nanospheres were formed at higher temperatures of 1000°C and 1100°C, while lower temperatures of 800°C and 900°C favored the growth of CNT. At 700°C, however, no tubes or spheres were formed. TEM and FTIR were used to observe spectral features, such as the peak positions, intensity and bandwidth, which are linked to some structural properties of the samples investigated. All these observations provided facts on the nanosphere and nanotube dimensions, vibrational modes and the degree of purity of the obtained samples. The TEM results show spheres of diameter in the range 50 nm to 250 nm while the tubes had diameters between 50 nm to 100 nm. XRD analysis reveals the materials synthesized are amorphous in nature with a hexagonal graphite structure.

Synthesis and characterization of γ-Fe2O3 NPs on silicon substrate for power device application

NASA Astrophysics Data System (ADS)

Hussein Nurul Athirah, Abu; Bee Chin, Ang; Yew Hoong, Wong; Boon Hoong, Ong; Aainaa Aqilah, Baharuddin

2018-06-01

Maghemite nanoparticles (γ-Fe2O3 NPs) were synthesized using Massart procedure. The formation reaction were optimized by varying the concentration of ferric nitrate solution (Fe(NO3)3) (0.1, 0.3, 0.5, 0.7 and 1.0 M). All samples were characterized by means of x-ray Diffractometer (XRD), Raman Spectroscopy, Transmission Electron Microscope (TEM) and Alternating Gradient Magnetometer (AGM). The smallest size of the NPs were chosen to be deposited on Silicon (100) substrate by spin coating technique. Annealing process of the samples were performed in Argon ambient at different temperatures (600, 700, 800 and 900°) for 20 min. Metal-oxide-semiconductor capacitors were then fabricated by depositing Aluminium as the gate electrode. The effect of the annealing process on the structural and electrical properties of γ-Fe2O3 NPs thin film were investigated. The structural properties of the deposited thin film were evaluated by XRD analysis, Atomic Force Microscopy (AFM) and Raman Analysis. On the other hand, the electrical properties was conducted by current-voltage analysis. It was revealed that the difference in the annealing temperature affect the grain size, surface roughness, distribution of the nanoparticles as well as the electrical performance of the samples where low annealing temperature (600 °C) gives low leakage current while high annealing temperature (900 °C) gives high electrical breakdown.

Synthesis of Carbon Nanotubes and Nanospheres from Coconut Fibre and the Role of Synthesis Temperature on Their Growth

NASA Astrophysics Data System (ADS)

Adewumi, Gloria A.; Inambao, Freddie; Eloka-Eboka, Andrew; Revaprasadu, Neerish

2018-04-01

Carbon nanotubes (CNT) and carbon nanospheres were successfully synthesized from coconut fibre-activated carbon. The biomass was first carbonized then physically activated, followed by treatment using ethanol vapor at 700°C to 1100°C at 100°C intervals. The effect of synthesis temperature on the formation of the nanomaterials was studied using scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive x-ray spectrometry, x-ray diffraction (XRD), Fourier transform infrared microscopy (FTIR) and thermogravimetric analysis. SEM analysis revealed that nanospheres were formed at higher temperatures of 1000°C and 1100°C, while lower temperatures of 800°C and 900°C favored the growth of CNT. At 700°C, however, no tubes or spheres were formed. TEM and FTIR were used to observe spectral features, such as the peak positions, intensity and bandwidth, which are linked to some structural properties of the samples investigated. All these observations provided facts on the nanosphere and nanotube dimensions, vibrational modes and the degree of purity of the obtained samples. The TEM results show spheres of diameter in the range 50 nm to 250 nm while the tubes had diameters between 50 nm to 100 nm. XRD analysis reveals the materials synthesized are amorphous in nature with a hexagonal graphite structure.

In situ soft XAS study on nickel-based layered cathode material at elevated temperatures: A novel approach to study thermal stability

DOE PAGES

Yoon, Won -Sub; Yang, Xiao -Qing; Haas, Otto; ...

2014-10-29

Tracking thermally induced reactions has always been challenging for electrode materials of electrochemical battery systems. Traditionally, a variety of calorimetric techniques and in situ XRD at elevated temperatures has been used to evaluate the thermal stability of electrode materials. These techniques are capable of providing variations in heat capacity, mass and average bulk composition of materials only. Herein, we report investigation of thermal characteristics of Li 0.33Ni 0.8Co 0.15Al 0.05O 2 by using in situ soft XAS measurements in combination with XRD. Fluorescence yield and partial electron yield measurements are used simultaneously to obtain element selective surface and bulk information.more » Fluorescence yield measurements reveal no energy change of the absorption peak and thus no valence state change in the bulk. However, electron yield measurements indicate that NiO-type rock salt structure is formed at the surface at temperatures above 200°C while no evidence for a surface reaction near Co sites in investigated temperature range is found. These results clearly show that in situ soft XAS can give a unique understanding of the role of each element in the structural transformation under thermal abuse offering a useful guidance in developing new battery system with improved safety performance.« less

Gadolinia doped hafnia (Gd2O3- HfO 2) thermal barrier coatings for gas turbine applications

NASA Astrophysics Data System (ADS)

Gullapalli, Satya Kiran

Thermal efficiency of the gas turbines is influenced by the operating temperature of the hot gas path components. The material used for the hot gas path components can only withstand temperature up to a certain limit. Thermal barrier coatings (TBC) provide the additional thermal protection for these components and help the gas turbine achieve higher firing temperatures. Traditionally available yttria stabilized zirconia (YSZ) TBCs have a limitation up to 1200 C due to their phase transformation. The present work focuses on gadolinia based hafnia (GSH) TBCs to study their potential to replace the YSZ coatings. Different compositions of gadolinia doped hafnia coatings have been deposited using electron beam physical vapor deposition (EB-PVD) technique and characterized using x-ray diffraction (XRD) and scanning electron microscope (SEM). The crystal structure analysis performed using XRD confirmed the stabilization of the high temperature cubic phase of hafnia. Cross sectional analysis confirmed the presence of columnar structure in the coatings which is a signature of the EB-PVD coatings. Mechanical properties of the coatings were investigated using nanoindentation and nano impact testing at both room temperature and high temperature. Indentation tests indicate a reduction in hardness with an increase in temperature and gadolinia content in hafnia. Impact testing reveals the fracture resistance of the coatings as a function of stabilizer content and heat treatment. Thermal measurements and impedance testing was performed on the bulk material to study the effect of gadolinia content. Thermal cycling was performed to study the spallation behavior of the as deposited and aged samples. Finite element models were developed to study the interfacial stress development in the coatings subjected to thermal cycling.

Metallurgical characterization of controlled memory wire nickel-titanium rotary instruments.

PubMed

Shen, Ya; Zhou, Hui-Min; Zheng, Yu-Feng; Campbell, Les; Peng, Bin; Haapasalo, Markus

2011-11-01

To improve the fracture resistance of nickel-titanium (NiTi) files, manufacturers have introduced new alloys and developed new manufacturing processes for the fabrication of NiTi files. This study aimed to examine the phase transformation behavior and microstructure of NiTi instruments from a novel controlled memory NiTi wire (CM wire). Instruments of EndoSequence (ES), ProFile (PF), ProFile Vortex (Vortex), Twisted Files (TF), Typhoon (TYP), and Typhoon™ CM (TYP CM), all size 25/.04, were examined by differential scanning calorimetry (DSC) and x-ray diffraction (XRD). Microstructures of etched instruments were observed by optical microscopy and scanning electron microscopy with x-ray energy-dispersive spectrometric (EDS) analyses. The DSC analyses showed that each segment of the TYP CM and Vortex instruments had an austenite transformation completion or austenite-finish (A(f)) temperature exceeding 37°C, whereas the NiTi instruments made from conventional superelastic NiTi wire (ES, PF, and TYP) and TF had A(f) temperatures substantially below mouth temperature. The higher A(f) temperature of TYP CM instruments was consistent with a mixture of austenite and martensite structure, which was observed at room temperature with XRD. All NiTi instruments had room temperature martensite microstructures consisting of colonies of lenticular features with substantial twinning. EDS analysis indicated that the precipitates in all NiTi instruments were titanium-rich, with an approximate composition of Ti(2)Ni. The TYP CM and Vortex instruments with heat treatment contribute to increase austenite transformation temperature. The CM instrument has significant changes in the phase transformation behavior, compared with conventional superelastic NiTi instruments. Copyright © 2011 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Temperature dependent and applied field strength dependent magnetic study of cobalt nickel ferrite nano particles: Synthesized by an environmentally benign method

NASA Astrophysics Data System (ADS)

Sontu, Uday Bhasker; G, Narsinga Rao; Chou, F. C.; M, V. Ramana Reddy

2018-04-01

Spinel ferrites have come a long way in their versatile applications. The ever growing applications of these materials demand detailed study of material properties and environmental considerations in their synthesis. In this article, we report the effect of temperature and applied magnetic field strength on the magnetic behavior of the cobalt nickel ferrite nano powder samples. Basic structural properties of spinel ferrite nano particles, that are synthesized by an environmentally benign method of auto combustion, are characterized through XRD, TEM, RAMAN spectroscopy. Diffuse Reflectance Spectroscopy (DRS) is done to understand the nickel substitution effect on the optical properties of cobalt ferrite nano particles. Thermo magnetic studies using SQUID in the temperature range 5 K to 400 K and room temperature (300 K) VSM studies are performed on these samples. Fields of 0Oe (no applied field: ZF), 1 kOe (for ZFC and FC curves), 5 kOe (0.5 T), 50 kOe (5T) (for M-H loop study) are used to study the magnetic behavior of these nano particles. The XRD,TEM analysis suggest 40 nm crystallites that show changes in the cation distribution and phase changes in the spinel structure with nickel substitution. Raman micrographs support phase purity changes and cation redistributions with nickel substitution. Diffuse reflectance study on powder samples suggests two band gap values for nickel rich compounds. The Magnetic study of these sample nano particles show varied magnetic properties from that of hard magnetic, positive multi axial anisotropy and single-magnetic-domain structures at 5 K temperature to soft magnetic core shell like structures at 300 K temperature. Nickel substitution effect is non monotonous. Blocking temperature of all the samples is found to be higher than the values suggested in the literature.

Effects of graphene oxide doping on the structural and superconducting properties of YBa2Cu3O7-δ

NASA Astrophysics Data System (ADS)

Dadras, S.; Falahati, S.; Dehghani, S.

2018-05-01

In this research we reported the effects of graphene oxide (GO) doping on the structural and superconducting properties of YBa2Cu3O7-δ (YBCO) high temperature superconductors. We synthesized YBCO powder by sol-gel method. After calcination, the powder mixed with different weight percent (0, 0.1, 0.3, 0.7, 1 wt.%) of GO. Refinement of X-ray diffraction (XRD) was carried out by material analysis using diffraction (MAUD) program to obtain the structural parameters such as lattice parameters, site occupancy of different atoms and orthorhombicity value for the all samples. Results show that GO doping does not change the structure of YBCO compound, Cu (1), Cu (2) and oxygen sites occupancy. It seems that GO remains between the grains and can play the role of weak links. We found that GO addition to YBCO compound increases transition temperature (TC). The oxygen contents of the all GO-doped samples are increased with respect to the pure one. The strain (ɛ) of the samples obtained from Williamson-Hall method, varies with increasing of GO doping. The scanning electron microscopy (SEM) images of the samples show better YBCO grain connections by GO doping.

XRD- and infrared-probed anisotropic thermal expansion properties of an organic semiconducting single crystal.

PubMed

Mohanraj, J; Capria, E; Benevoli, L; Perucchi, A; Demitri, N; Fraleoni-Morgera, A

2018-01-17

The anisotropic thermal expansion properties of an organic semiconducting single crystal constituted by 4-hydroxycyanobenzene (4HCB) have been probed by XRD in the range 120-300 K. The anisotropic thermal expansion coefficients for the three crystallographic axes and for the crystal volume have been determined. A careful analysis of the crystal structure revealed that the two different H-bonds stemming from the two independent, differently oriented 4HCB molecules composing the unit cell have different rearrangement patterns upon temperature variations, in terms of both bond length and bond angle. Linearly Polarized Mid InfraRed (LP-MIR) measurements carried out in the same temperature range, focused on the O-H bond spectral region, confirm this finding. The same LP-MIR measurements, on the basis of a semi-empirical relation and of geometrical considerations and assumptions, allowed calculation of the -CNH-O- hydrogen bond length along the a and b axes of the crystal. In turn, the so-calculated -CNH-O- bond lengths were used to derive the thermal expansion coefficients along the corresponding crystal axes, as well as the volumetric one, using just the LP-MIR data. Reasonable to good agreement with the same values obtained from XRD measurements was obtained. This proof-of-principle opens interesting perspectives about the possible development of a rapid, low cost and industry-friendly assessment of the thermal expansion properties of organic semiconducting single crystals (OSSCs) involving hydrogen bonds.

Phase Compositions of Self Reinforcement Al2O3/CaAl12O19 Composite using X-ray Diffraction Data and Rietveld Technique

NASA Astrophysics Data System (ADS)

Asmi, D.; Low, I. M.; O'Connor, B.

2008-03-01

The analysis of x-ray diffraction (XRD) patterns by the Rietveld technique was tested to the quantitatively phase compositions of self reinforcement Al2O3/CaAl12O19 composite. Room-temperature XRD patterns revealed that α-Al2O3 was the only phase presence in the CA0 sample, whereas the α-Al2O3 and CaAl12O19 phases were found for CA5, CA15, CA30, and CA50 samples. The peak intensity of CA6 in the self reinforcement Al2O3/CaAl12O19 composites increased in proportion with increase in CaAl12O19 content in contrast to α-Al2O3. The diffraction patterns for CA100 sample shows minor traces of α-Al2O3 even in relatively low peak intensity. It is suggesting that the in-situ reaction sintering of raw materials were not react completely to form 100 wt% CaAl12O19 at temperature 1650 °C. Quantitative phase compositions of self reinforcement Al2O3/CaAl12O19 composites by Rietveld analysis with XRD data has been well demonstrated. The results showed that the GOF values are relatively low and the fluctuation in the difference plots shows a reasonable fit between the observed and the calculated plot.

Synchrotron X-ray measurement techniques for thermal barrier coated cylindrical samples under thermal gradients.

PubMed

Siddiqui, Sanna F; Knipe, Kevin; Manero, Albert; Meid, Carla; Wischek, Janine; Okasinski, John; Almer, Jonathan; Karlsson, Anette M; Bartsch, Marion; Raghavan, Seetha

2013-08-01

Measurement techniques to obtain accurate in situ synchrotron strain measurements of thermal barrier coating systems (TBCs) applied to hollow cylindrical specimens are presented in this work. The Electron Beam Physical Vapor Deposition coated specimens with internal cooling were designed to achieve realistic temperature gradients over the TBC coated material such as that occurring in the turbine blades of aeroengines. Effects of the circular cross section on the x-ray diffraction (XRD) measurements in the various layers, including the thermally grown oxide, are investigated using high-energy synchrotron x-rays. Multiple approaches for beam penetration including collection, tangential, and normal to the layers, along with variations in collection parameters are compared for their ability to attain high-resolution XRD data from the internal layers. This study displays the ability to monitor in situ, the response of the internal layers within the TBC, while implementing a thermal gradient across the thickness of the coated sample. The thermal setup maintained coating surface temperatures in the range of operating conditions, while monitoring the substrate cooling, for a controlled thermal gradient. Through variation in measurement location and beam parameters, sufficient intensities are obtained from the internal layers which can be used for depth resolved strain measurements. Results are used to establish the various techniques for obtaining XRD measurements through multi-layered coating systems and their outcomes will pave the way towards goals in achieving realistic in situ testing of these coatings.

Synchrotron X-ray measurement techniques for thermal barrier coated cylindrical samples under thermal gradients

NASA Astrophysics Data System (ADS)

Siddiqui, Sanna F.; Knipe, Kevin; Manero, Albert; Meid, Carla; Wischek, Janine; Okasinski, John; Almer, Jonathan; Karlsson, Anette M.; Bartsch, Marion; Raghavan, Seetha

2013-08-01

Measurement techniques to obtain accurate in situ synchrotron strain measurements of thermal barrier coating systems (TBCs) applied to hollow cylindrical specimens are presented in this work. The Electron Beam Physical Vapor Deposition coated specimens with internal cooling were designed to achieve realistic temperature gradients over the TBC coated material such as that occurring in the turbine blades of aeroengines. Effects of the circular cross section on the x-ray diffraction (XRD) measurements in the various layers, including the thermally grown oxide, are investigated using high-energy synchrotron x-rays. Multiple approaches for beam penetration including collection, tangential, and normal to the layers, along with variations in collection parameters are compared for their ability to attain high-resolution XRD data from the internal layers. This study displays the ability to monitor in situ, the response of the internal layers within the TBC, while implementing a thermal gradient across the thickness of the coated sample. The thermal setup maintained coating surface temperatures in the range of operating conditions, while monitoring the substrate cooling, for a controlled thermal gradient. Through variation in measurement location and beam parameters, sufficient intensities are obtained from the internal layers which can be used for depth resolved strain measurements. Results are used to establish the various techniques for obtaining XRD measurements through multi-layered coating systems and their outcomes will pave the way towards goals in achieving realistic in situ testing of these coatings.

Synthesis and characterization of barium hexaferrite with manganese (Mn) doping material as anti-radar

NASA Astrophysics Data System (ADS)

Susilawati, Doyan, Aris; Khalilurrahman

2017-01-01

Have been successfully synthesized barium powder doping Manganese hexaferrite with the expected potential as anti-radar material. Synthesis was done by using the co-precipitation method, the variation of the variable x concentrations used were 0; 0.2; 0.4; and 0.6 and calcined at temperatures of 400, 600 and 800°C. Characterization powders of hexaferrite have used XRD (X-Ray Diffraction), SEM (Scanning Electron Microscopy), TEM (Transmission Electron Microscopy), LCR (inductance, capacitance, and resistance) meter, and VSM (Vibrating Sample Magnetometer). The higher the concentration and temperature of calcinations given affect the color of the powder. The test results using XRD indicates that it has formed barium hexaferrite phase with a hexagonal crystal structure. Tests using SEM showed that all the constituent elements barium powder hexaferrite by doping Manganese powders have been spread evenly. XRD test results were confirmed by a test using a TEM showing the crystal structure and the powder was sized nano particles. The results from the LCR meter showed that the barium powder hexaferrite by doping Manganese that has been synthesized classified in semiconductor materials. The result from VSM showed that the value of coercivity magnetic powder doped barium hexaferrite Manganese is smaller when compared with barium hexaferrite without doping and belong to the soft magnetic. Based on the results of the synthesis and characterization, we can conclude that the barium powder heksaferrite by doping Manganese potential as a material anti-radar.

Effect of nano BiPb-2212 phase addition on BiPb-2223 phase properties

NASA Astrophysics Data System (ADS)

Mohammed, N. H.; Abou-Aly, A. I.; Barakat, M. Me.; Hassan, M. S.

2018-06-01

BiPb-2212 phase in nanoscale was added to BiPb-2223 phase with a general stoichiometry of (Bi1.7Pb0.4Sr2.1Ca1.1Cu2.1O8+δ)x/Bi1.8Pb0.4Sr2.0Ca2.0Cu3.2O10+δ, 0.0 ≤ x  ≤ 2.5 wt.%. All samples were prepared by the standard solid-state reaction method. The prepared nano BiPb-2212 phase was characterized by X-ray powder diffraction (XRD) and transmission electron microscope (TEM). The prepared samples were characterized by XRD and the scanning electron microscope (SEM). XRD analysis indicated that the sample with x = 1.5 wt.% has the highest relative volume fraction for BiPb-2223 phase. Samples were examined by electrical resistivity and I-V measurements. There is no significant change in the superconducting transition temperature Tc for all samples. The highest critical current density Jc was recorded for the sample with x = 1.5 wt.%. The normalized excess conductivity (Δσ/σroom) was calculated according to Aslamazov-Larkin (AL) model. Four different fluctuating regions were recorded as the temperature decreased. The coherence length along the c-axis at 0 K ξc(0), interlayer coupling strength s, Fermi velocity vF of the carriers and Fermi energy EF were calculated for both samples with x = 0.0 wt.% and 1.5 wt.%.

NH3-SCR denitration catalyst performance over vanadium-titanium with the addition of Ce and Sb.

PubMed

Xu, Chi; Liu, Jian; Zhao, Zhen; Yu, Fei; Cheng, Kai; Wei, Yuechang; Duan, Aijun; Jiang, Guiyuan

2015-05-01

Selective catalytic reduction technology using NH3 as a reducing agent (NH3-SCR) is an effective control method to remove nitrogen oxides. TiO2-supported vanadium oxide catalysts with different levels of Ce and Sb modification were prepared by an impregnation method and were characterized by X-ray diffractometer (XRD), Brunauer-Emmett-Teller (BET), Transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FT-IR), UV-Vis diffuse reflectance spectroscopy (UV-Vis DRS), Raman and Hydrogen temperature-programmed reduction (H2-TPR). The catalytic activities of V5CexSby/TiO2 catalysts for denitration were investigated in a fixed bed flow microreactor. The results showed that cerium, vanadium and antimony oxide as the active components were well dispersed on TiO2, and the catalysts exhibited a large number of d-d electronic transitions, which were helpful to strengthen SCR reactivity. The V5CexSby/TiO2 catalysts exhibited a good low temperature NH3-SCR catalytic activity. In the temperature range of 210 to 400°C, the V5CexSby/TiO2 catalysts gave NO conversion rates above 90%. For the best V5Ce35Sb2/TiO2 catalyst, at a reaction temperature of 210°C, the NO conversion rate had already reached 90%. The catalysts had different catalytic activity with different Ce loadings. With the increase of Ce loading, the NO conversion rate also increased. Copyright © 2015. Published by Elsevier B.V.

Evaluation of mechanical property and bioactivity of nano-bioglass 45S5 scaffold coated with poly-3-hydroxybutyrate.

PubMed

Montazeri, Mahbobeh; Karbasi, Saeed; Foroughi, Mohammad Reza; Monshi, Ahmad; Ebrahimi-Kahrizsangi, Reza

2015-02-01

One of the major challenges facing researchers of tissue engineering is scaffold design with desirable physical and mechanical properties for growth and proliferation of cells and tissue formation. In this research, firstly, nano-bioglass powder with grain sizes of 55-56 nm was prepared by melting method of industrial raw materials at 1,400 °C. Then the porous ceramic scaffold of bioglass with 30, 40 and 50 wt% was prepared by using the polyurethane sponge replication method. The scaffolds were coated with poly-3-hydroxybutyrate (P3HB) for 30 s and 1 min in order to increase the scaffold's mechanical properties. XRD, XRF, SEM, FE-SEM and FT-IR were used for phase and component studies, morphology, particle size and determination of functional groups, respectively. XRD and XRF results showed that the type of the produced bioglass was 45S5. The results of XRD and FT-IR showed that the best temperature to produce bioglass scaffold was 600 °C, in which Na2Ca2Si3O9 crystal is obtained. By coating the scaffolds with P3HB, a composite scaffold with optimal porosity of 80-87% in 200-600 μm and compression strength of 0.1-0.53 MPa was obtained. According to the results of compressive strength and porosity tests, the best kind of scaffold was produced with 30 wt% of bioglass immersed for 1 min in P3HB. To evaluate the bioactivity of the scaffold, the SBF solution was used. The selected scaffold (30 wt% bioglass/6 wt% P3HB) was maintained for up to 4 weeks in this solution at an incubation temperature of 37 °C. The XRD, SEM EDXA and AAS tests were indicative of hydroxyapatite formation on the surface of bioactive scaffold. This scaffold has some potential to use in bone tissue engineering.

Ceramic synthesis of 0.08BiGaO3-0.90BaTiO3-0.02LiNbO3 under high pressure and high temperature

NASA Astrophysics Data System (ADS)

Hui, Jin; Yong, Li; Mou-Sheng, Song; Lin, Chen; Xiao-Peng, Jia; Hong-An, Ma

2016-07-01

In this paper, the preparation of 0.08BiGaO3-0.90BaTiO3-0.02LiNbO3 is investigated at pressure 3.8 GPa and temperature 1100-1200 °C. Experimental results indicate that not only is the sintered rate more effective, but also the sintered temperature is lower under high pressure and high temperature than those of under normal pressure. It is thought that the adscititious pressure plays the key role in this process, which is discussed in detail. The composition and the structure of the as-prepared samples are recorded by XRD patterns. The result shows that the phases of BaTiO3, BaBiO2.77, and Ba2Bi4Ti5O18 with piezoelectric ceramic performance generate in the sintered samples. Furthermore, the surface morphology characteristics of the typical samples are also investigated using a scanning electron microscope. It indicates that the grain size and surface structure of the samples are closely related to the sintering temperature and sintering time. It is hoped that this study can provide a new train of thought for the preparation of lead-free piezoelectric ceramics with excellent performance. Project supported by the National Natural Science Foundation of China (Grant No. 51172089), the Natural Science Foundation of Education Department of Guizhou Province, China (Grant Nos. KY [2013]183 and LH [2015]7232), and the Research Fund for the Doctoral Program of Tongren University, China (Grant No. DS1302).

MOF-74 as an Efficient Catalyst for the Low-Temperature Selective Catalytic Reduction of NOx with NH3.

PubMed

Jiang, Haoxi; Wang, Qianyun; Wang, Huiqin; Chen, Yifei; Zhang, Minhua

2016-10-12

In this work, Mn-MOF-74 with hollow spherical structure and Co-MOF-74 with petal-like shape have been prepared successfully via the hydrothermal method. The catalysts were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), thermogravimetry-mass spectrum analysis (TG-MS), N 2 adsorption/desorption, scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). It is found that MOF-74(Mn, Co) exhibits the capability for selective catalytic reduction (SCR) of NO x at low temperatures. Both experimental (temperature-programmed desorption, TPD) and computational methods have shown that Co-MOF-74 and Mn-MOF-74 owned high adsorption and activation abilities for NO and NH 3 . The catalytic activities of Mn-MOF-74 and Co-MOF-74 for low-temperature denitrification (deNO x ) in the presence of NH 3 were 99% at 220 °C and 70% at 210 °C, respectively. It is found that the coordinatively unsaturated metal sites (CUSs) in M-MOF-74 (M = Mn and Co) played important roles in SCR reaction. M-MOF-74 (M = Mn and Co), especially Mn-MOF-74, showed excellent catalytic performance for low-temperature SCR. In addition, in the reaction process, NO conversion on Mn-MOF-74 decreased with the introduction of H 2 O and SO 2 and almost recovered when gas was cut off. However, for Co-MOF-74, SO 2 almost has no effect on the catalytic activity. This work showed that MOF-74 could be used prospectively as deNO x catalyst.

Temperature dependent growth of GaN nanowires using CVD technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Mukesh, E-mail: mukeshjihrnp@gmail.com; Singh, R.; Kumar, Vikram

2016-05-23

Growth of GaN nanowires have been carried out on sapphire substrates with Au as a catalyst using chemical vapour deposition technique. GaN nanowires growth have been studied with the experimental parameter as growth temperature. Diameter of grown GaN nanowires are in the range of 50 nm to 100 nm while the nanowire length depends on growth temperature. Morphology of the GaN nanowires have been studied by scanning electron microscopy. Crystalline nature has been observed by XRD patterns. Optical properties of grown GaN nanowires have been investigated by photoluminescence spectra.

Research on annealing and properties of TlBr crystals for radiation detector use

NASA Astrophysics Data System (ADS)

Zhiping, Zheng; Yongtao, Yu; Dongxiang, Zhou; Shuping, Gong; Qiuyun, Fu

2014-03-01

In this paper, annealing was carried out in air after cutting, polishing and etching to eliminate defects introduced by crystal and wafer preparation work. The effect of annealing temperature and time on the properties of TlBr crystals was investigated. The crystal quality was characterized by infrared (IR) transmittance spectrum, I-V measurement, XRD and energy response spectrum. In the annealing temperature range (100-320 °C) applied, it was found that higher temperature was more effective for improving quality. Furthermore, it is proved that an appropriate annealing time is vital for better crystal quality.

Metal-Insulator Transition in W-doped VO2 Nanowires

NASA Astrophysics Data System (ADS)

Long, Gen; Parry, James; Whittaker, Luisa; Banerjee, Sarbajit; Zeng, Hao

2010-03-01

We report a systematic study of the metal-insulator transition in W-doped VO2 nanowires. Magnetic susceptibility were measured for a bulk amount of VO2 nanowire powder. The susceptibility shows a sharp drop with decreasing temperature corresponding to the metal-insulator transition. The transition shows large temperature hysteresis for cooling and heating. With increasing doping concentration, the transition temperatures decreases systematically from 320 K to 275K. Charge transport measurements on the same nanowires showed similar behavior. XRD and TEM measurements were taken to further determine the structure of the materials in study.

Preparation and drug release behavior of temperature-responsive mesoporous carbons

NASA Astrophysics Data System (ADS)

Wang, Xiufang; Liu, Ping; Tian, Yong

2011-06-01

A temperature-responsive composite based on poly (N-isopropylacrylamide) (PNIPAAm) and ordered mesoporous carbons (OMCs) has been successfully prepared by a simple wetness impregnation technique. The structures and properties of the composite were characterized by infrared spectroscopy (IR), X-ray diffraction (XRD), transmission electron microscopy (TEM), N 2 sorption, thermogravimetric analysis (TG) and differential scanning calorimetry (DSC). The results showed that the inclusion of PNIPAAm had not greatly changed the basic ordered pore structure of the OMCs. Ibuprofen (IBU) was selected as model drug, and in vitro test of IBU release exhibited a temperature-responsive controlled release delivery.

Novel Montmorillonite/TiO₂/MnAl-Mixed Oxide Composites Prepared from Inverse Microemulsions as Combustion Catalysts.

PubMed

Napruszewska, Bogna D; Michalik-Zym, Alicja; Rogowska, Melania; Bielańska, Elżbieta; Rojek, Wojciech; Gaweł, Adam; Wójcik-Bania, Monika; Bahranowski, Krzysztof; Serwicka, Ewa M

2017-11-19

A novel design of combustion catalysts is proposed, in which clay/TiO₂/MnAl-mixed oxide composites are formed by intermixing exfoliated organo-montmorillonite with oxide precursors (hydrotalcite-like in the case of Mn-Al oxide) obtained by an inverse microemulsion method. In order to assess the catalysts' thermal stability, two calcination temperatures were employed: 450 and 600 °C. The composites were characterized with XRF (X-ray fluorescence), XRD (X-ray diffraction), HR SEM (high resolution scanning electron microscopy, N₂ adsorption/desorption at -196 °C, and H₂ TPR (temperature programmed reduction). Profound differences in structural, textural and redox properties of the materials were observed, depending on the presence of the TiO₂ component, the type of neutralization agent used in the titania nanoparticles preparation (NaOH or NH₃ (aq)), and the temperature of calcination. Catalytic tests of toluene combustion revealed that the clay/TiO₂/MnAl-mixed oxide composites prepared with the use of ammonia showed excellent activity, the composites obtained from MnAl hydrotalcite nanoparticles trapped between the organoclay layers were less active, but displayed spectacular thermal stability, while the clay/TiO₂/MnAl-mixed oxide materials obtained with the aid of NaOH were least active. The observed patterns of catalytic activity bear a direct relation to the materials' composition and their structural, textural, and redox properties.

Aqueous-Phase Hydrogenolysis of Glycerol over Re Promoted Ru Catalysts Encapuslated in Porous Silica Nanoparticles

PubMed Central

Li, Kuo-Tseng; Yen, Ruey-Hsiang

2018-01-01

Activity improvement of Ru-based catalysts is needed for efficient production of valuable chemicals from glycerol hydrogenolysis. In this work, a series of Re promoted Ru catalysts encapuslated in porous silica nanoparticles (denoted as Re-Ru@SiO2) were prepared by coating silica onto the surface of chemically reduced Ru-polyvinylpyrrolidone colloids, and were used to catalyze the conversion of glycerol to diols and alcohols in water. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), nitrogen adsorption, X-ray photoelectron spectroscopy (XPS) and temperature-programmed reduction (TPR) were used to characterize these nanoparticles. Effects of Ru/Si atomic ratio, Re addition, glycerol and catalyst concentrations, reaction time, temperature, and hydrogen pressure were investigated. Re addition retarded the reduction of ruthenium oxide, but increased the catalyst reactivity for glycerol hydrogenolysis. Due to its greater Ru content, Re-Ru@ SiO2 showed much better activity (reacted at much lower temperature) and more yields of 1,2-propanediol and overall liquid-phase products than Re-Ru/SiO2 (prepared by conventional impregnation method) reported before. The rate of glycerol disappearance exhibited first-order dependence on glycerol concentration and hydrogen pressure, with an activation energy of 107.8 kJ/mol. The rate constant increased linearly with increasing Ru/Si atomic ratio and catalyst amount. The yield of overall liquid-phase products correlated well with glycerol conversion. PMID:29522432

NH 3-SCR on Cu, Fe and Cu + Fe exchanged beta and SSZ-13 catalysts: Hydrothermal aging and propylene poisoning effects

DOE PAGES

Wang, Aiyong; Wang, Yilin; Walter, Eric D.; ...

2017-10-07

Cu, Fe and Cu + Fe ion exchanged Beta and SSZ-13 catalysts were prepared by solution ion exchange using commercial NH 4/Beta, and NH 4/SSZ-13 that was prepared in-house. To study hydrothermal aging effects, Beta supported catalysts were aged hydrothermally at 700 °C and SSZ-13 supported catalysts were aged at 750 °C. In order to reveal the effects of Fe addition in the co-exchanged catalysts, these catalysts were characterized by means of powder X-ray diffraction (XRD), N 2 adsorption-desorption, electron paramagnetic resonance (EPR), 27Al-nuclear magnetic resonance ( 27Al-NMR) and propylene coking followed with temperature programmed reaction (TPR), and further testedmore » with standard NH 3-SCR with and without the presence of propylene. Collectively, the catalyst characterizations and reaction testing indicated minor beneficial effects of Fe addition in Cu,Fe/Beta, where NH 3-SCR activity, N 2 selectivity and hydrothermal stability were all slightly improved. In contrast, Fe addition did not show apparent beneficial effects in low-temperature SCR for the Cu,Fe/SSZ-13 case. In conclusion, at elevated reaction temperatures, however, the presence of Fe indeed considerably improved NO conversion and N 2 selectivity for the hydrothermally aged Cu,Fe/SSZ-13 catalyst in the presence of propylene.« less

NH 3-SCR on Cu, Fe and Cu + Fe exchanged beta and SSZ-13 catalysts: Hydrothermal aging and propylene poisoning effects

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Aiyong; Wang, Yilin; Walter, Eric D.

Cu, Fe and Cu + Fe ion exchanged Beta and SSZ-13 catalysts were prepared by solution ion exchange using commercial NH 4/Beta, and NH 4/SSZ-13 that was prepared in-house. To study hydrothermal aging effects, Beta supported catalysts were aged hydrothermally at 700 °C and SSZ-13 supported catalysts were aged at 750 °C. In order to reveal the effects of Fe addition in the co-exchanged catalysts, these catalysts were characterized by means of powder X-ray diffraction (XRD), N 2 adsorption-desorption, electron paramagnetic resonance (EPR), 27Al-nuclear magnetic resonance ( 27Al-NMR) and propylene coking followed with temperature programmed reaction (TPR), and further testedmore » with standard NH 3-SCR with and without the presence of propylene. Collectively, the catalyst characterizations and reaction testing indicated minor beneficial effects of Fe addition in Cu,Fe/Beta, where NH 3-SCR activity, N 2 selectivity and hydrothermal stability were all slightly improved. In contrast, Fe addition did not show apparent beneficial effects in low-temperature SCR for the Cu,Fe/SSZ-13 case. In conclusion, at elevated reaction temperatures, however, the presence of Fe indeed considerably improved NO conversion and N 2 selectivity for the hydrothermally aged Cu,Fe/SSZ-13 catalyst in the presence of propylene.« less

Soot oxidation and NO{sub x} reduction over BaAl{sub 2}O{sub 4} catalyst

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lin, He; Li, Yingjie; Shangguan, Wenfeng

2009-11-15

This study addresses soot oxidation and NO{sub x} reduction over a BaAl{sub 2}O{sub 4} catalyst. By XRD analysis, the catalyst was shown to be of spinel structure. Temperature Programmed Oxidation (TPO) and Constant Temperature Oxidation (CTO) at 673 K show that the presence of O{sub 2} decreases the ignition temperature of soot, and it enhances the conversion of NO{sub x} to N{sub 2} and N{sub 2}O. The kinetic features of soot oxidation in the TPO test are similar to that in the TG-DTA analysis. Analysis by Diffuse Reflectance Fourier Infrared Transform Spectroscopy (DRIFTS) indicates that the nitrates formed from NO{submore » x} adsorption and the C(O) intermediates from soot oxidation are the key precursors of the redox process between soot and NO{sub x} over surfaces of the BaAl{sub 2}O{sub 4} catalyst. Moreover, DRIFTS tests suggest that nitrates act as the principal oxidants for C(O) oxidation, through which nitrates are reduced to N{sub 2} and N{sub 2}O. The O{sub 2} in the gas mixture presents a positive effect on the conversion of NO{sub x} to N{sub 2} and N{sub 2}O by promoting the oxidation of nitrites into nitrates species. (author)« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pan Qingtao; Huang Kai; Ni Shibing

Well-crystalline flower- and rod-like NiS nanostructures have been synthesized by an organic-free hydrothermal process at a low temperature of 200 deg. C. X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM) were employed to characterize the as-synthesized NiS nanostructures. The effects of temperature and reaction time on the morphology have been also investigated. The two-step flake-cracking mechanism for the formation of flower- and rod-like NiS nanostructures was discussed. The products were also investigated by photoluminescence (PL) spectroscopy.

The Influence of Growth Temperature on Sb Incorporation in InAsSb, and the Temperature-dependent Impact of Bi Surfactants

DTIC Science & Technology

2014-01-01

resolution X - ray diffraction (XRD) were collected for all samples, and reciprocal space maps (RSMs) were collected from selected samples. The complete data...exposure. The lines represent the model fit. 19 13 Figure 1. Triple axis x - ray diffraction from the bi-layered InAsSb structures grown on GaSb at...Applied Physics, Structural properties of bismuth‐bearing semiconductor alloys, 63 (1988) 107. 18 12 Figure Captions Figure 1. Triple axis x - ray

Room-temperature synthesis and photoluminescence of hexagonal CePO4 nanorods

NASA Astrophysics Data System (ADS)

Zhu, J.; Zhang, K.; Zhao, H. Y.

2018-01-01

Hexagonal CePO4 nanorods were synthesized via a simple chemical precipitation route at room-temperature without the presence of surfactants and then characterized by powder X-ray diffraction (XRD), energy-dispersive X-ray (EDX) spectrometry, scanning electron microscopy (SEM), transmission electron microscopy (TEM), ultraviolet-visible (UV-vis) absorption and photoluminescence (PL) spectroscopy. Hexagonal CePO4 nanorods exhibit strong ultraviolet absorption and ultraviolet luminescence, which correspond to the electronic transitions between 4f and 5d state of Ce3+ ions.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Skariah, Benoy, E-mail: skariahbenoy@yahoo.co.in, E-mail: dr.boben1@gmail.com; Thomas, Boben, E-mail: skariahbenoy@yahoo.co.in, E-mail: dr.boben1@gmail.com

For LPG sensing, boron doped (0.2 to 0.8 wt. %) polycrystalline tin oxide thin films are deposited by spray pyrolysis in the temperature range 325 - 430 °C. Sensor response of 56 % is achieved for 1000 ppm of LPG, at an operating temperature of 350 °C. The effects of ageing under ambient conditions on the sensor response are investigated for a storage period of six years. Ageing increases the film resistance but the gas response is lowered. XRD, SEM, FESEM, FTIR and XPS are utilized for structural, morphological and compositional charaterisations.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schelhas, L. T.; Stone, K. H.; Harvey, S. P.

We report that the interest in Cu 2ZnSn(S,Se) 4 (CZTS) for photovoltaic applications is motivated by similarities to Cu(In,Ga)Se 2 while being comprised of non-toxic and earth abundant elements. However, CZTS suffers from a V oc deficit, where the V oc is much lower than expected based on the band gap, which may be the result of a high concentration of point-defects in the CZTS lattice. Recently, reports have observed a low-temperature order/disorder transition by Raman and optical spectroscopies in CZTS films and is reported to describe the ordering of Cu and Zn atoms in the CZTS crystal structure. Tomore » directly determine the level of Cu/Zn ordering, we have used resonant-XRD, a site, and element specific probe of long range order. We used CZTSe films annealed just below and quenched from just above the transition temperature; based on previous work, the Cu and Zn should be ordered and highly disordered, respectively. Our data show that there is some Cu/Zn ordering near the low temperature transition but significantly less than high chemical order expected from Raman. Finally, to understand both our resonant-XRD results and the Raman results, we present a structural model that involves antiphase domain boundaries and accommodates the excess Zn within the CZTS lattice.« less

Magnetic and dielectric properties of Co doped nano crystalline Li ferrites by auto combustion method

NASA Astrophysics Data System (ADS)

Aravind, G.; Raghasudha, M.; Ravinder, D.; Kumar, R. Vijaya

2016-05-01

The ultra fine particles of the cobalt substituted lithium ferrites with the formula [Li0.5Fe0.5]1-xCoxFe2O4 (0.0≤x≤1.0) were synthesized by low temperature citrate-gel auto combustion method. Structural characterization of the samples was carried out using XRD studies and FESEM (Field Emission Scanning Electron Microscopy) analysis. XRD studies confirms the formation of single phased spinel structure with crystallite size in the range of 36-43 nm. The M-H loops have been traced using Vibrating Sample Magnetometer (VSM) for all the compositions at room temperature and hysteresis parameters were evaluated. The hysteresis loops of the prepared samples show clear saturation at an applied field of ±20 k Oe and the loops were highly symmetric in nature. The dielectric parameters such as dielectric constant (ε'), dielectric loss tangent (tan δ) of the samples were studied as a function of frequency in the range of 20 Hz to 2 MHz at room temperature using LCR Meter. The dielectric constant and loss tangent of the samples show a normal dielectric behavior with frequency which reveals that the dispersion is due to the Maxwell-Wagner type interfacial polarization and hopping of electrons between the Fe2+ and Fe3+ ions.

Investigation of irradiation effects induced by self-ion in 6H-SiC combining RBS/C, Raman and XRD

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chaabane, Nihed; Debelle, Aurelien; Sattonnay, Gael

2012-01-01

Single crystals of 6H-SiC were irradiated at room temperature and 670 K with 4 MeV C ions at two fluences: 1015 and 1016 cm2 (0.16 and 1.6 dpa at the damage peak). Damage accumulation was studied by a combination of X-ray diffraction (XRD), Raman spectroscopy and Rutherford backscattering spectrometry in channelling geometry (RBS/C) along the [0001] direction. The irradiated layer is found to be composed of a low damage region up to 1.5 lm followed by a region where the disorder level is higher, consistent with SRIM predictions. At room temperature and low fluence, typically 1015 cm2, the strain depthmore » profile follows the dpa depth distribution (with a maximum value of 2%). The disorder is most likely due to small defect clusters. When increasing the fluence up to 1016 cm2, a buried amorphous layer forms, as indicated by e.g. Raman results where the Si C bands become broader or even disappear. At a higher irradiation temperature of 670 K, amorphization is not observed at the same fluence, revealing a dynamic annealing process. However, results tend to suggest that the irradiated layer is highly heterogeneous and composed of different types of defects.« less

The effects of pore structure on the behavior of water in lignite coal and activated carbon.

PubMed

Nwaka, Daniel; Tahmasebi, Arash; Tian, Lu; Yu, Jianglong

2016-09-01

The effects of physical structure (pore structure) on behavior of water in lignite coal and activated carbon (AC) samples were investigated by using Differential Scanning Calorimetry (DSC) and low-temperature X-ray diffraction (XRD) techniques. AC samples with different pore structures were prepared at 800°C in steam and the results were compared with that of parent lignite coal. The DSC results confirmed the presence of two types of freezable water that freeze at -8°C (free water) and -42°C (freezable bound water). A shift in peak position of free water (FW) towards lower temperature was observed in AC samples compared to the lignite coal with decreasing water loading. The amount of free water (FW) increased with increasing gasification conversion. The amounts of free and freezable bound water (FBW) in AC samples were calculated and correlated to pore volume and average pore size. The amount of FW in AC samples is well correlated to the pore volume and average pore size of the samples, while an opposite trend was observed for FBW. The low-temperature XRD analysis confirmed the existence of non-freezable water (NFW) in coal and AC with the boundary between the freezable and non-freezable water (NFW) determined. Copyright © 2016 Elsevier Inc. All rights reserved.

Insight into the Am-O Phase Equilibria: A Thermodynamic Study Coupling High-Temperature XRD and CALPHAD Modeling.

PubMed

Epifano, Enrica; Guéneau, Christine; Belin, Renaud C; Vauchy, Romain; Lebreton, Florent; Richaud, Jean-Christophe; Joly, Alexis; Valot, Christophe; Martin, Philippe M

2017-07-03

In the frame of minor actinide transmutation, americium can be diluted in UO 2 and (U, Pu)O 2 fuels burned in fast neutron reactors. The first mandatory step to foresee the influence of Am on the in-reactor behavior of transmutation targets or fuel is to have fundamental knowledge of the Am-O binary system and, in particular, of the AmO 2-x phase. In this study, we coupled HT-XRD (high-temperature X-ray diffraction) experiments with CALPHAD thermodynamic modeling to provide new insights into the structural properties and phase equilibria in the AmO 2-x -AmO 1.61+x -Am 2 O 3 domain. Because of this approach, we were able for the first time to assess the relationships between temperature, lattice parameter, and hypostoichiometry for fcc AmO 2-x . We showed the presence of a hyperstoichiometric existence domain for the bcc AmO 1.61+x phase and the absence of a miscibility gap in the fcc AmO 2-x phase, contrary to previous representations of the phase diagram. Finally, with the new experimental data, a new CALPHAD thermodynamic model of the Am-O system was developed, and an improved version of the phase diagram is presented.

Microstructure and magnetic behavior of Mn doped GeTe chalcogenide semiconductors based phase change materials

NASA Astrophysics Data System (ADS)

Adam, Adam Abdalla Elbashir; Cheng, Xiaomin; Abuelhassan, Hassan H.; Miao, Xiang Shui

2017-06-01

Phase-change materials (PCMs) are the most promising candidates to be used as an active media in the universal data storage and spintronic devices, due to their large differences in physical properties of the amorphous-crystalline phase transition behavior. In the present study, the microstructure, magnetic and electrical behaviors of Ge0.94Mn0.06Te thin film were investigated. The crystallographic structure of Ge0.94Mn0.06Te thin film was studied sing X-ray diffractometer (XRD) and High Resolution Transmission Electron Microscope (HR-TEM). The XRD pattern showed that the crystallization structure of the film was rhombohedral phase for GeTe with a preference (202) orientation. The HR-TEM image of the crystalline Ge0.94Mn0.06Te thin film demonstrated that, there were two large crystallites and small amorphous areas. The magnetization as a function of the magnetic field analyses of both amorphous and crystalline states showed the ferromagnetic hysteretic behaviors. Then, the hole carriers concentration of the film was measured and it found to be greater than 1021 cm-3 at room temperature. Moreover, the anomalous of Hall Effect (AHE) was clearly observed for the measuring temperatures 5, 10 and 50 K. The results demonstrated that the magnitude of AHE decreased when the temperature was increasing.

Synthesis of nanocrystalline zirconia by amorphous citrate route: structural and thermal (HTXRD) studies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bhagwat, Mahesh; Ramaswamy, Veda

Nanocrystalline zirconia powder with a fairly narrow particle size distribution has been synthesized by the amorphous citrate route. The sample obtained has a high BET surface area of 89 m{sup 2} g{sup -1}. Rietveld refinement of the powder X-ray diffraction (XRD) profile of the zirconia sample confirms stabilization of zirconia in the tetragonal phase with around 8% monoclinic impurity. The data show the presence of both anionic as well as cationic vacancies in the lattice. Crystallite size determined from XRD is 8 nm and is in close agreement with the particle size determined by TEM. The in situ high temperature-X-raymore » diffraction (HTXRD) study revealed high thermal stability of the mixture till around 1023 K after which the transformation of tetragonal phase into the monoclinic phase has been seen as a function of temperature till 1473 K. This transformation is accompanied by an increase in the crystallite size of the sample from 8 to 55 nm. The thermal expansion coefficients are 9.14 x 10{sup -6} K{sup -1} along 'a'- and 15.8 x 10{sup -6} K{sup -1} along 'c'-axis. The lattice thermal expansion coefficient in the temperature range 298-1623 K is 34.6 x 10{sup -6} K{sup -1}.« less

In situ micro-Raman analysis and X-ray diffraction of nickel silicide thin films on silicon.

PubMed

Bhaskaran, M; Sriram, S; Perova, T S; Ermakov, V; Thorogood, G J; Short, K T; Holland, A S

2009-01-01

This article reports on the in situ analysis of nickel silicide (NiSi) thin films formed by thermal processing of nickel thin films deposited on silicon substrates. The in situ techniques employed for this study include micro-Raman spectroscopy (microRS) and X-ray diffraction (XRD); in both cases the variations for temperatures up to 350 degrees C has been studied. Nickel silicide thin films formed by vacuum annealing of nickel on silicon were used as a reference for these measurements. In situ analysis was carried out on nickel thin films on silicon, while the samples were heated from room temperature to 350 degrees C. Data was gathered at regular temperature intervals and other specific points of interest (such as 250 degrees C, where the reaction between nickel and silicon to form Ni(2)Si is expected). The transformations from the metallic state, through the intermediate reaction states, until the desired metal-silicon reaction product is attained, are discussed. The evolution of nickel silicide from the nickel film can be observed from both the microRS and XRD in situ studies. Variations in the evolution of silicide from metal for different silicon substrates are discussed, and these include (100) n-type, (100) p-type, and (110) p-type silicon substrates.

Gas sensing behaviour of Cr{sub 2}O{sub 3} and W{sup 6+}: Cr{sub 2}O{sub 3} nanoparticles towards acetone

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kohli, Nipin, E-mail: nipinkohli82@yahoo.com; Hastir, Anita; Singh, Ravi Chand

2016-05-23

This paper reports the acetone gas sensing properties of Cr{sub 2}O{sub 3} and 2% W{sup 6+} doped Cr{sub 2}O{sub 3} nanoparticles. The simple cost-effective hydrolysis assisted co-precipitation method was adopted. Synthesized samples were characterized by X-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM) techniques. XRD revealed that synthesized nanoparticles have corundum structure. The lattice parameters have been calculated by Rietveld refinement; and strain and crystallite size have been calculated by using the Williamson-Hall plots. For acetone gas sensing properties, the nanoparticles were applied as thick film onto alumina substrate and tested at different operating temperatures. The results showedmore » that the optimum operating temperature of both the gas sensors is 250°C. At optimum operating temperature, the response of Cr{sub 2}O{sub 3} and 2% W{sup 6+} doped Cr{sub 2}O{sub 3} gas sensor towards 100 ppm acetone was found to be 25.5 and 35.6 respectively. The investigations revealed that the addition of W{sup 6+} as a dopant enhanced the sensing response of Cr{sub 2}O{sub 3} nanoparticles appreciably.« less

Influence of Synthesis Temperature on the Growth and Surface Morphology of Co₃O₄ Nanocubes for Supercapacitor Applications.

PubMed

Samal, Rashmirekha; Dash, Barsha; Sarangi, Chinmaya Kumar; Sanjay, Kali; Subbaiah, Tondepu; Senanayake, Gamini; Minakshi, Manickam

2017-10-31

A facile hydrothermal route to control the crystal growth on the synthesis of Co₃O₄ nanostructures with cube-like morphologies has been reported and tested its suitability for supercapacitor applications. The chemical composition and morphologies of the as-prepared Co₃O₄ nanoparticles were extensively characterized using X-ray diffraction (XRD) and transmission electron microscopy (TEM). Varying the temperature caused considerable changes in the morphology, the electrochemical performance increased with rising temperature, and the redox reactions become more reversible. The results showed that the Co₃O₄ synthesized at a higher temperature (180 °C) demonstrated a high specific capacitance of 833 F/g. This is attributed to the optimal temperature and the controlled growth of nanocubes.

Nanoplate-like tungsten trioxide (hydrate) films prepared by crystal-seed-assisted hydrothermal reaction

NASA Astrophysics Data System (ADS)

Wang, P.; Yang, L.; Dai, B.; Yang, Z.; Guo, S.; Zhu, J.

2017-07-01

Vertically-aligned WO3 nanoplates on transparent conducting fluorine-doped tin oxide (FTO) glass were prepared by a facile template-free crystal-seed-assisted hydrothermal method. The effects of the hydrothermal temperature and reaction time on the crystal structure and morphology of the products were investigated by XRD and SEM. The XRD results showed that the as-prepared thin films obtained below 150∘C comprised orthorhombic WO3 ṡ H2O and completely converted to monoclinic WO3 at 180∘C. It was also noted that there was a phase transformation from orthorhombic to monoclinic by increasing the reaction time from 1 to 12 h. SEM analysis revealed that WO3 thin films are composed of plate-like nanostructures.

Reentrant behaviour in polyvinyl alcohol-borax hydrogels

NASA Astrophysics Data System (ADS)

Lawrence, Mathias B.; Desa, J. A. E.; Aswal, V. K.

2018-01-01

Polyvinyl alcohol (PVA) hydrogels, cross-linked with varying concentrations of borax, were studied with small angle neutron scattering (SANS), x-ray diffraction (XRD) and differential thermal analysis (DTA). The SANS data satisfy the Ornstein-Zernike approximation. The hydrogels are modelled as PVA chains bound by borate cross-links. Water occupies the spaces within the three-dimensional hydrogel network. The mesh size ξ indicates reentrant behaviour i.e. at first, ξ increases and later decreases as a function of borax concentration. The behaviour is explained on the basis of the balance between the charged di-diol cross-links and the shielding by free ions in the solvent. XRD and DTA show the molecular size of water in the solvent and the glass transition temperature commensurate with reentrant behaviour.

Structural and magnetic analysis of Cu, Co substituted NiFe{sub 2}O{sub 4} thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sharma, Hakikat; Bala, Kanchan; Negi, N. S.

2016-05-23

In the present work we prepared NiFe{sub 2}O{sub 4}, Ni{sub 0.95}Cu{sub 0.05}Fe{sub 2}O{sub 4} and Ni{sub 0.94}Cu{sub 0.05}Co{sub 0.01} Fe{sub 2}O{sub 4} thin films by metallo-organic decomposition method (MOD) using spin coating technique. The thin films were analyzed by X-ray diffractometer (XRD) and Atomic force microscope (AFM) for structural studies. The XRD patterns confirmed the ferrite phase of thin films. From AFM, we analyzed surface morphology, calculated grain size (GS) and root mean square roughness (RMSR). Room temperature magnetic properties were investigated by vibrating sample magnetometer (VSM).

Structural and morphological study of chemically synthesized CdSe thin films

NASA Astrophysics Data System (ADS)

Agrawal, P.; Singh, Randhir; Sharma, Jeewan; Sachdeva, M.; Singh, Anupinder; Bhargava, A.

2018-05-01

Nanocrystalline CdSe thin films were prepared by Chemical Bath Deposition (CBD) method using potassium nitrilo-triacetic acid cadmium complex and sodium selenosulphite. The as deposited films were red in color, uniform and well adherent to the glass substrate. These films were strongly dependent on the deposition parameters such as bath composition, deposition temperature and time. Films were annealed at 350 °C for four hours. The morphological, structural and optical properties were studied using X-ray diffraction (XRD), UV-VIS spectrophotometer measurements, scanning electron microscopy and atomic force microscopy. The XRD analysis confirmed that films are predominantly in hexagonal phase. Scanning electron micrograph shows that the grains are uniformly spread all over the film and each grain contains many nanocrystals with spherical shapes.

DSC and Raman studies of silver borotellurite glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kaur, Amandeep; Khanna, Atul, E-mail: atul.phy@gndu.ac.in; Gonzàlez, Fernando

2016-05-23

Silver borotellurite glasses of composition: xAg{sub 2}O-yB{sub 2}O{sub 3}-(100-x-y)TeO{sub 2} (x=20-mol%, y = 0, 10, 20 and 30-mol%) were prepared and characterized by density, X-ray diffraction (XRD), differential scanning calorimetry, and Raman spectroscopy. XRD confirmed the amorphous structure of all samples. Density of glasses decreases while the glass transition temperature increases with increase in B{sub 2}O{sub 3} content from 10 to 30-mol%. Raman study shows that coordination number of Te with oxygen decreases steadily from 3.42 to 3.18 on adding B{sub 2}O{sub 3} due to the transformation of TeO{sub 4} into TeO{sub 3} units.

Synthesis of TiN/a-Si3N4 thin film by using a Mather type dense plasma focus system

NASA Astrophysics Data System (ADS)

Hussain, T.; R., Ahmad; Khalid, N.; A. Umar, Z.; Hussnain, A.

2013-05-01

A 2.3 kJ Mather type pulsed plasma focus device was used for the synthesis of a TiN/a-Si3N4 thin film at room temperature. The film was characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and atomic force microscopy (AFM). The XRD pattern confirms the growth of polycrystalline TiN thin film. The XPS results indicate that the synthesized film is non-stoichiometric and contains titanium nitride, silicon nitride, and a phase of silicon oxy-nitride. The SEM and AFM results reveal that the surface of the synthesized film is quite smooth with 0.59 nm roughness (root-mean-square).

A Curved Image-Plate Detector System for High-Resolution Synchrotron X-ray Diffraction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sarin, P.; Haggerty, R; Yoon, W

2009-01-01

The developed curved image plate (CIP) is a one-dimensional detector which simultaneously records high-resolution X-ray diffraction (XRD) patterns over a 38.7 2{theta} range. In addition, an on-site reader enables rapid extraction, transfer and storage of X-ray intensity information in {le}30 s, and further qualifies this detector to study kinetic processes in materials science. The CIP detector can detect and store X-ray intensity information linearly proportional to the incident photon flux over a dynamical range of about five orders of magnitude. The linearity and uniformity of the CIP detector response is not compromised in the unsaturated regions of the image plate,more » regardless of saturation in another region. The speed of XRD data acquisition together with excellent resolution afforded by the CIP detector is unique and opens up wide possibilities in materials research accessible through X-ray diffraction. This article presents details of the basic features, operation and performance of the CIP detector along with some examples of applications, including high-temperature XRD.« less

Application of glucose as a green capping agent and reductant to fabricate CuI micro/nanostructures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tavakoli, Farnosh; Salavati-Niasari, Masoud, E-mail: salavati@kashanu.ac.ir; Ghanbari, Davood

Graphical abstract: - Highlights: • CuI nanostructures were prepared via a simple precipitation method. • Glucose as a green capping agent and reductant was applied. • The effect of glucose concentration on the morphology of CuI was investigated. • According to XRD results, pure cubic phase CuI have been formed by using glucose. - Abstract: In this work, CuI micro/nanostructures have been successfully prepared via a simple precipitation route at room temperature. By using glucose as a clean reducing agent with different concentrations, CuI micro/nanostructures with various morphologies were obtained. Besides glucose, Na{sub 2}SO{sub 3}, KBH{sub 4} and N{sub 2}H{submore » 4}·H{sub 2}O have been applied as reductant. X-ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence spectroscopy, X-ray energy dispersive spectroscopy (EDS) and Fourier transformed infrared (FT-IR) spectroscopy were used to characterize the as-produced CuI micro/nanostructures. According to the XRD results, it was found that pure cubic phase CuI have been formed by using glucose.« less

Synthesis and Characterization of Titanium Dioxide Thin Film for Sensor Applications

NASA Astrophysics Data System (ADS)

Latha, H. K. E.; Lalithamba, H. S.

2018-03-01

Titanium oxide (TiO2) nanoparticles (metal oxide semiconductor) are successfully synthesized using hydrothermal method for sensor application. Titanium dioxide and Sodium hydroxide are used as precursors. These reactants are mixed and calcinated at 400 °C to produce TiO2 nanoparticles. The crystalline structure, morphology of synthesized TiO2 nanoparticles are studied using x-ray diffraction (XRD), Fourier Transform Infrared (FTIR) analysis and scanning electron microscopy (SEM). XRD results revealed that the prepared TiO2 sample is highly crystalline, having Anatase crystal structure. FT-IR spectra peak at 475 cm‑1 indicated characteristic absorption bands of TiO2 nanoparticles. The XRD and FTIR result confirmed the formation of high purity of TiO2 nanoparticles. The SEM image shows that TiO2 nanoparticles prepared in this study are spherical in shape. Synthesized TiO2 nanoparticles are deposited on glass substrate at room temperature using E beam evaporation method to determine gauge factor and found to be 4.7. The deposited TiO2 thin films offer tremendous potential in the applications of electronic and magneto–electric devices.

Structural and magnetic properties of nanocomposite iron-containing SiCxNy films

NASA Astrophysics Data System (ADS)

Pushkarev, R. V.; Fainer, N. I.; Maurya, K. K.

2017-02-01

New ferromagnetic films with composition SiCxNyFez were synthesized using chemical vapor deposition technique. Films were deposited using ferrocene, 1,1,1,3,3,3-hexamethyldisilazane (HMDS) and hydrogen gaseous mixture. Chemical and phase composition of the films were studied by FTIR, Raman spectroscopy and X-ray diffraction with grazing incidence (GI-XRD). FTIR spectra analysis confirmed the existence of Si-C and Si-N bonds. Graphite inclusions and amorphous carbon were determined by Raman spectra analysis. The surface of the SiCxNyFez films studied by SEM is covered by nanocrystallites of iron oxide Fe3O4 phase. The main purpose of GI-XRD analysis is to describe the layered structure of the films in detail. It was shown by GI-XRD study, that phase composition of the SiCxNyFez films varies from iron oxide Fe3O4 to iron silicide Fe3Si and silicon carbide SiC with the deposition temperature growing. It was established, that SiCxNyFez films are perspective for application in the spintronic field.

Microwave Synthesis, Characterization, and Photoluminescence Properties of Nanocrystalline Zirconia

PubMed Central

Singh, A. K.; Nakate, Umesh T.

2014-01-01

We report synthesis of ZrO2 nanoparticles (NPs) using microwave assisted chemical method at 80°C temperature. Synthesized ZrO2 NPs were calcinated at 400°C under air atmosphere and characterized using FTIR, XRD, SEM, TEM, BET, and EDS for their formation, structure, morphology, size, and elemental composition. XRD results revealed the formation of mixed phase monoclinic and tetragonal ZrO2 phases having crystallite size of the order 8.8 nm from most intense XRD peak as obtained using Scherrer formula. Electron microscope analysis shows that the NPs were less than 10 nm and highly uniform in size having spherical morphology. BET surface area of ZrO2 NPs was found to be 65.85 m2/g with corresponding particle size of 16 nm. The band gap of synthesized NPs was found to be 2.49 eV and PL spectra of ZrO2 synthesized NPs showed strong peak at 414 nm, which corresponds to near band edge emission (UV emission) and a relatively weak peak at 475 and 562 nm. PMID:24578628

XRD and 29Si MAS-NMR spectroscopy across the β-Lu 2Si 2O 7- β-Y 2Si 2O 7 solid solution

NASA Astrophysics Data System (ADS)

Becerro, Ana I.; Escudero, Alberto

2005-01-01

Samples in the system Lu 2-xY xSi 2O 7 (0⩽ x⩽2) have been synthesized following the sol-gel method and calcined to 1300 °C, a temperature at which the β-polymorph is known to be the stable phase for the end-members Lu 2Si 2O 7 and Y 2Si 2O 7. The XRD patterns of all the compositions studied are compatible with the structure of the β-polymorph. Unit cell parameters are calculated as a function of composition from XRD patterns. They show a linear change with increasing Y content, which indicates a solid solubility of β-Y 2Si 2O 7 in β-Lu 2Si 2O 7 at 1300 °C. 29Si MAS NMR spectra of the different members of the system agree with the XRD results, showing a linear decrease of the 29Si chemical shift with increasing Y content. Finally, a correlation reported in the literature to predict 29Si chemical shifts in silicates is applied here to obtain the theoretical variation in 29Si chemical shift values in the system Lu 2Si 2O 7-Y 2Si 2O 7 and the results compare favorably with the values obtained experimentally.

HA/Bioglass composite films deposited by pulsed laser with different substrate temperature

NASA Astrophysics Data System (ADS)

Wang, D. G.; Chen, C. Z.; Jin, Q. P.; Li, H. C.; Pan, Y. K.

2014-03-01

In this experiment, the HA/Bioglass composite films on Ti-6Al-4V were deposited by a pulsed laser at Ar atmosphere, and the influence of substrate temperature on the morphology, phase constitutions, bonding configurations and adhesive strength of the films was studied. The obtained films were characterized by an electron probe microanalyzer (EPMA), scanning electron microscope (SEM), X-ray diffractometer (XRD), Fourier transform infrared spectrometer (FTIR), scratch apparatus, and so on. The results show that the amount of the droplets, the crystallinity, and the critical load of the deposited films all increase with the increase of the substrate temperature; however, the substrate temperature has little influence on the functional groups of the films.

Effects of Pressure and Temperature on the Kinetics of Iron-magnesite Redox Reaction: Implication for the Genesis of Ultradeep Diamonds

NASA Astrophysics Data System (ADS)

Zhu, F.; Li, J.; Liu, J.; Lai, X.; Chen, B.; Meng, Y.

2016-12-01

Diamonds may be the products of redox reaction between carbonates in the subducted slabs and iron metal in the mantle [1]. Given the relatively low temperatures of the subducted slabs, however, it remains to be shown that such reaction can occur at sufficiently fast rate. To examine the influence of pressure and temperature (P-T) on the kinetics of iron-carbonate redox reaction, we performed in-situ synchrotron X-ray diffraction (XRD) experiments at the Advanced Photon Source, Argonne National Laboratory, using laser-heated diamond anvil cells. The starting material consists of an iron foil sandwiched between two magnesite pellets. Data were collected between 1050 and 1800 K at 50-100 K intervals, at seven pressures between 12 and 40 GPa, corresponding the depths where most ultradeep diamonds originated [2]. We obtained constraints on the Fe-MgCO3reaction boundary, which was located between the estimated temperatures on the surface of cold slabs near 1400 K and inside their interiors near 1000 K, and it had a similar slope as the slab geotherm [3]. Furthermore, the experiments revealed a significant effect of pressure on the extent and rate of the reaction. The XRD patterns showed that below 15 GPa the initial reaction products were iron carbides, which reacted with magnesite to form diamonds when the reaction completed in 60 minutes at 1300 to 1500 K. Above 18 GPa only iron carbides were observed in the XRD patterns even when all the iron was consumed, and iron carbides still coexisted with magnesite after 100 to 160 minutes at 1600 to 1800 K. Our results suggest that diamonds can be produced from iron-carbonate redox reaction at slab-mantle boundary conditions at the deeper part of the upper mantle, but diamond growth through this reaction is slow or kinetically hindered in the lower mantle. References[1] Palyanov, Y. N. et al. (2013). Proc. Nat. Aca. Sci., 110(51), 20408-20413. [2] Stachel, T. et al. (2005). Elements, 1(2), 73-78. [3] Eberle et al. (2002). Phys. Earth Planet. Int., 134(3), 191-202.

Enhancement of ferromagnetic properties in composites of BaSnO3 and CoFe2O4

NASA Astrophysics Data System (ADS)

Manju, M. R.; Ajay, K. S.; D'Souza, Noel M.; Hunagund, Shivakumar; Hadimani, R. L.; Dayal, Vijaylakshmi

2018-04-01

In this paper, we report structural and magnetic properties of BaSnO3(BSO)(1-x)-CoFe2O4 (CFO)(x) composite (with x = 0%, 1% (C1), 2% (C2) and 5% (C3) in molar ratio) synthesized using nitrate precursor method. The X-ray diffraction (XRD) pattern of the composite powder confirmed presence of both BaSnO3 with the cubic perovskite structure and CoFe2O4 with the cubic spinel structure. No signature of any other phases in pure BaSnO3, CoFe2O4 and composites have been detected either in XRD or energy dispersive X-ray (EDS) analysis. The temperature dependent zero field cooled (ZFC) & field cooled (FC) magnetization and magnetic field dependence magnetization measurements have been carried at room temperature of the pure BaSnO3. We observe a weak ferromagnetic (FM) behavior at room temperature in pure BaSnO3 even though it is non-magnetic in nature. The room temperature Raman spectroscopy and electron spin resonance measurements of the sample confirm the presence of oxygen vacancy and formation of F-center, which is responsible for the FM behavior. The oxidation state and elemental analysis have been carried out using X-ray photoelectron spectroscopy (XPS). The magnetic field dependence of magnetization of the composite samples reveal increase of saturation magnetization (Ms), remanence magnetization (Mr) and coercivity (Hc) with increase in ferrite content in the composite. Significant enhancement in FM components is observed with lowering of temperature.

Effects of growth temperatures on the physical properties of Cu2ZnSnS4 thin films deposited through spray pyrolysis for solar cell applications

NASA Astrophysics Data System (ADS)

Fadavieslam, M. R.; Keshavarz, S.

2018-02-01

This paper reports the effects of substrate temperature on the structural, optical, and electrical properties of Cu2ZnSnS4 (CZTS) thin films deposited on soda lime glass through spray pyrolysis without sulfurization. Substrate temperatures ranged from 250 to 500 °C at a step of 50 °C, and a precursor solution was prepared by dissolving copper chloride, zinc acetate, zinc chloride, and thiourea in ethanol and di-ionized water. The films were characterized through X-ray diffraction (XRD), field emission scanning electron microscopy, ultraviolet-visible spectroscopy, and electrical resistance and Hall effect measurements, respectively, obtained by two-point probe and van der Pauw techniques. XRD revealed the formation of polycrystalline CZTS thin films and the appearance of relatively intense and sharp diffraction peaks at (112), (200), (220), and (312) of a kesterite phase with (112) preferential orientation, in which the crystalline degree increased as substrate temperature increased. Surface morphological analysis demonstrated the formation of a smooth, compact, and uniform CZTS surface. When substrate temperature increased from 250 to 500 °C, single-crystal grains increased from 6.38 to 28 nm, carrier concentration increased from 3.4 × 1017 to 2.36 × 1019 cm-3, Hall mobility increased from 30.96 to 68.52 cm2/V.S, optical band gap decreased from 1.74 to 1.14 eV, and resistivity decreased from 0.59 to 3.87 × 10-3 Ωcm. Hall effect analysis indicated that the films exhibited p-type conductivity.

Preparation of meta-stable phases of barium titanate by Sol-hydrothermal method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Selvaraj, Mahalakshmi; Department of Material Science, School of Chemistry, Madurai Kamaraj University, Tamilnadu Madurai-625 021; Venkatachalapathy, V.

2015-11-15

Two low-cost chemical methods of sol–gel and the hydrothermal process have been strategically combined to fabricate barium titanate (BaTiO{sub 3}) nanopowders. This method was tested for various synthesis temperatures (100 °C to 250 °C) employing barium dichloride (BaCl{sub 2}) and titanium tetrachloride (TiCl{sub 4}) as precursors and sodium hydroxide (NaOH) as mineralizer for synthesis of BaTiO{sub 3} nanopowders. The as-prepared BaTiO{sub 3} powders were investigated for structural characteristics using x-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The overall analysis indicates that the hydrothermal conditions create a gentle environment to promote the formation of crystalline phasemore » directly from amorphous phase at the very low processing temperatures investigated. XRD analysis showed phase transitions from cubic - tetragonal - orthorhombic - rhombohedral with increasing synthesis temperature and calculated grain sizes were 34 – 38 nm (using the Scherrer formula). SEM and TEM analysis verified that the BaTiO{sub 3} nanopowders synthesized by this method were spherical in shape and about 114 - 170 nm in size. The particle distribution in both SEM and TEM shows that as the reaction temperature increases from 100 °C to 250 °C, the particles agglomerate. Selective area electron diffraction (SAED) shows that the particles are crystalline in nature. The study shows that choosing suitable precursor and optimizing pressure and temperature; different meta-stable (ferroelectric) phases of undoped BaTiO{sub 3} nanopowders can be stabilized by the sol-hydrothermal method.« less

Characterization of bio char derived from tapioca skin

NASA Astrophysics Data System (ADS)

Hasnan, F. I.; Iamail, K. N.; Musa, M.; Jaapar, J.; Alwi, H.; Hamid, K. K. K.

2018-03-01

Pyrolysis of tapioca skin was conducted to produce bio chars in the range between 500°C–800°C. Surface modification treatment were performed on bio chars by using chemicals within 24 hours at 30°C and hot water within 1 hour to enhance the bio char’s adsorption properties according to surface area, pore volume, pore size, crystallinity structure and functional groups. The samples were characterized by using BET, XRD, FTIR and Methylene Blue adsorption. Based on BET result, it showed the surface area increased as the pyrolysis temperature increased followed by pore volume and pore size for S0. The optimum temperature for SNaOH, SHW and SMeOH was at 600°C, 700°C and 800°C with the surface area of 75.9874, 274.5066 and 351.5531 m2/g respectively compared to S0 while SP3HO4 has the worst result since it felt on macroporous structure. The percentage of MB adsorption was followed the size of bio chars surface area. Based on FTIR result, at temperature 500°C to 700°C, the bio chars still have functional groups while at 800°C, many functional groups were diminished due to high temperature struck on them. XRD result showed all the bio chars were amorphous. In conclusion, the best surface modification treatment was by Methanol followed by hot water and Sodium Hydroxide at temperature of 700°C and 800°C while Ortho-Phosphoric acid was the worst one and was not suitable for bio char’s surface modification for adsorption purpose.

Precipitate Evolution and Strengthening in Supersaturated Rapidly Solidified Al-Sc-Zr Alloys

NASA Astrophysics Data System (ADS)

Deane, Kyle; Kampe, S. L.; Swenson, Douglas; Sanders, P. G.

2017-04-01

Because of the low diffusivities of scandium and zirconium in aluminum, trialuminide precipitates containing these elements have been reported to possess excellent thermal stability at temperatures of 573 K (300 °C) and higher. However, the relatively low equilibrium solubilities of these elements in aluminum limit the achievable phase fraction and, in turn, strengthening contributions from these precipitates. One method of circumventing this limitation involves the use of rapid solidification techniques to suppress the initial formation of precipitates in alloys containing higher solute compositions. This work specifically discusses the fabrication of supersaturated Al-Sc, Al-Zr, and Al-Sc-Zr alloys via melt spinning, in which supersaturations of at least 0.55 at. pct Zr and 0.8 at. pct Sc are shown to be attainable through XRD analysis. The resulting ribbons were subjected to a multistep aging heat treatment in order to encourage a core-shell precipitate morphology, the precipitate evolution behavior was monitored with XRD and TEM, and the aging behavior was observed. While aging in these alloys is shown to follow similar trends to conventionally processed materials reported in literature, with phase fraction increasing until higher aging temperatures causing a competing dissolution effect, the onset of precipitation begins at lower temperatures than previously observed and the peak hardnesses occurred at higher temperature steps due to an increased aging time associated with increased solute concentration. Peaking in strength at a higher temperature doesn't necessarily mean an increase in thermal stability, but rather emphasizes the need for intelligently designed heat treatments to take full advantage of the potential strengthening of supersaturated Al-Sc-Zr alloys.

Structural, magnetic and electrical properties of a new double-perovskite LaNaMnMoO6 material

PubMed Central

Borchani, Sameh Megdiche; Koubaa, Wissem Cheikh-Rouhou; Megdiche, Makrem

2017-01-01

Structural, magnetic, magnetocaloric, electrical and magnetoresistance properties of an LaNaMnMoO6 powder sample have been investigated by X-ray diffraction (XRD), magnetic and electrical measurements. Our sample has been synthesized using the ceramic method. Rietveld refinements of the XRD patterns show that our sample is single phase and it crystallizes in the orthorhombic structure with Pnma space group. Magnetization versus temperature in a magnetic applied field of 0.05 T shows that our sample exhibits a paramagnetic–ferromagnetic transition with decreasing temperature. The Curie temperature TC is found to be 320 K. Arrott plots show that all our double-perovskite oxides exhibit a second-order magnetic phase transition. From the measured magnetization data of an LaNaMnMoO6 sample as a function of the magnetic applied field, the associated magnetic entropy change |−ΔSM| and the relative cooling power (RCP) have been determined. In the vicinity of TC, |−ΔSM| reached, in a magnetic applied field of 8 T, a maximum value of ∼4 J kg−1 K−1. Our sample undergoes a large magnetocaloric effect at near-room temperature. Resistivity measurements reveal the presence of an insulating-metal transition at Tρ = 180 K. A magnetoresistance of 30% has been observed at room temperature for 6 T, significantly larger than that reported for the A2FeMoO6 (A = Sr, Ba) double-perovskite system. PMID:29291087

OXIDATION OF METHANOL USING OZONE ON TITANIA-SUPPORTED VANADIUM CATALYST

EPA Science Inventory

Catalytic ozone decomposition of methanol has been conducted at mild temperatures of 100 to 250°C using V2O5/TiO2 catalyst prepared by either sol-gel or wet impregnation methods. The catalysts were characterized using XRD, surface area measurements, and desorption of CH3OH. Gas p...

Simple sol-gel synthesis and characterization of new CoTiO3/CoFe2O4 nanocomposite by using liquid glucose, maltose and starch as fuel, capping and reducing agents.

PubMed

Ansari, Fatemeh; Sobhani, Azam; Salavati-Niasari, Masoud

2018-03-15

The sol-gel auto-combustion technique is an effective method for the synthesis of the composites. In this research for the first time, CoTiO 3 /CoFe 2 O 4 nanocomposites are successfully synthesized via a new sol-gel auto-combustion technique. The glucose, maltose and starch are used as fuel, capping and reducing agents, also the optimal reducing agent is chosen. The effects of quantity of reducing agent, molar ratio of Ti:Co, calcination temperature and time on the morphology, particle size, magnetic property, purity and phase of the nanocomposites are investigated. XRD patterns show formation of CoTiO 3 /CoFe 2 O 4 spherical nanoparticles with nearly evenly distribution, when the molar ratio of Co/Ti is 1:1. EDS analysis confirm results of XRD. The magnetic behavior of the nanocomposites is studied by VSM. The nanocomposites exhibit a high coercivity at room temperature. Copyright © 2017 Elsevier Inc. All rights reserved.

Effect of swift heavy ion irradiation on structural and opto-electrical properties of bi-layer CdS-Bi2S3 thin films prepared by solution growth technique at room temperature

NASA Astrophysics Data System (ADS)

Shaikh, Shaheed U.; Siddiqui, Farha Y.; Desale, Deepali J.; Ghule, Anil V.; Singh, Fouran; Kulriya, Pawan K.; Sharma, Ramphal

2015-01-01

CdS-Bi2S3 bi-layer thin films have been deposited by chemical bath deposition method on Indium Tin Oxide glass substrate at room temperature. The as-deposited thin films were annealed at 250 °C in an air atmosphere for 1 h. An air annealed thin film was irradiated using Au9+ ions with the energy of 120 MeV at fluence 5×1012 ions/cm2 using tandem pelletron accelerator. The irradiation induced modifications were studied using X-ray diffraction (XRD), Atomic Force Microscopy (AFM), Raman spectroscopy, UV spectroscopy and I-V characteristics. XRD study reveals that the as-deposited thin films were nanocrystalline in nature. The decrease in crystallite size, increase in energy band gap and resistivity were observed after irradiation. Results are explained on the basis of energy deposited by the electronic loss after irradiation. The comparative results of as-deposited, air annealed and irradiated CdS-Bi2S3 bi-layer thin films are presented.

[Preparation and characterization of magnetic nano-particles with radiofrequency-induced hyperthermia for cancer treatment].

PubMed

Fan, Xiangshan; Zhang, Dongsheng; Zheng, Jie; Gu, Ning; Ding, Anwei; Jia, Xiupeng; Qing, Hongyun; Jin, Liqiang; Wan, Meiling; Li, Qunhui

2006-08-01

Mn0.5Zn0.5Fe2O4 nano-particles were prepared by the chemical co-precipitation, their characteristics were observed with transmission electron microscope (TEM), X-ray diffractometer (XRD) and thermal analysis system, and etc. The temperature changes of the nano-particles of Mn0.5Zn0.5Fe2O4 and its magnetic fluid explored in radiofrequency(RF,200 KHz, 4 KW) were measured. The proliferation ratio of L929 cells cultured in soak of Mn0.5Zn0.5Fe2O4 nano-particles were observed. The experiment indicates that the magnetic particles were about 40 nm diameter in average, round, had strong magnetism, and were proved to be consistent with the standard data of chart of XRD. Its magnetic fluid exposed to RF could be heated up to temperature range from 40 degrees C to 51 degrees C due to the amount of the magnetic nano-particles and intensity of the alternating magnetic field. Magnetic nano-particles were found to have no obvious cytotoxicity to L929 cells.

Current-voltage characteristics of n-AlMgZnO/p-GaN junction diodes

NASA Astrophysics Data System (ADS)

Hsueh, Kuang-Po; Cheng, Po-Wei; Cheng, Yi-Chang; Sheu, Jinn-Kong; Yeh, Yu-Hsiang; Chiu, Hsien-Chin; Wang, Hsiang-Chun

2013-03-01

This study investigates the temperature dependence of the current-voltage (I-V) characteristics of Al-doped MgxZn1-xO/p-GaN junction diodes. Specifically, this study reports the deposition of n-type Al-doped MgxZn1-xO (AMZO) films on p-GaN using a radio-frequency (RF) magnetron sputtering system followed by annealing at 700, 800, 900, and 1000 °C in a nitrogen ambient for 60 seconds, respectively. The AMZO/GaN films were thereafter analyzed using Hall measurement and the x-ray diffraction (XRD) patterns. The XRD results show that the diffraction angles of the annealed AMZO films remain the same as that of GaN without shifting. The n-AMZO/p-GaN diode with 900 °C annealing had the lowest leakage current in forward and reverse bias. However, the leakage current of the diodes did not change significantly with an increase in annealing temperatures. These findings show that the n-AMZO/p-GaN junction diode is feasible for GaN-based heterojunction bipolar transistors (HBTs) and UV light-emitting diodes (LEDs).

Photocatalytic, antioxidant, antibacterial and anti-inflammatory activity of silver nanoparticles synthesised using forest and edible mushroom

NASA Astrophysics Data System (ADS)

Sriramulu, Mohana; Sumathi, Shanmugam

2017-12-01

Mushroom has been part of the human diet for thousands of years, and in recent times, the amounts consumed have risen greatly, involving a large number of species. Mushrooms used for nutritional and therapeutic purposes. In this study silver nanoparticles were synthesised using an edible mushroom (Agaricus bisporus) and forest mushroom (Ganoderma lucidum) extract. The synthesised nanoparticles were characterised by UV-vis spectroscopy, FTIR, powder XRD and SEM. Silver nanoparticles were synthesised at room temperature and at 60 °C. FTIR results recognised the presence of bioactive functional groups responsible for the reduction of silver nitrate to silver nanoparticles. From the XRD, it was observed that the nanoparticles are silver with an average size of 10-80 nm. The silver nanoparticles are explored for photocatalytic activity and biological activities such as in vitro antioxidant activity, anti-inflammatory activity and antimicrobial activity against Escherichia coli and Staphylococcus aureus organisms. 98% of textile dye (direct blue 71) degradation was noticed under UV light within 150 min for forest mushroom synthesised silver nanoparticles at room temperature.

One-step synthesis and characterizations of cerium oxide nanoparticles in an ambient temperature via Co-precipitation method

NASA Astrophysics Data System (ADS)

Pujar, Malatesh S.; Hunagund, Shirajahammad M.; Desai, Vani R.; Patil, Shivaprasadgouda; Sidarai, Ashok H.

2018-04-01

We report the simple Co-precipitation method for the synthesis of Cerium oxide (CeO2) nanoparticles (NPs) in an ambient temperature. We have taken the Cerium (III) nitrate hexahydrate (Ce(NO3)3.6H2O) and Sodium hydroxide (NaOH) as the precursors. The obtained NPs were analyzed using the UV-Vis spectrophotometer, Fourier transform infrared spectroscopy (FT-IR) and X-ray diffraction (XRD). The obtained results signify that UV-Vis spectrum exhibited a well-defined absorption peak at 274 nm and the estimated energy gap (Eg) is 4.05 eV. The FT-IR analysis provides the supporting evidence for the presence of bonding of O-H, nitrates, alcohols and O-Ce-O vibrations. The XRD result reveals that the synthesized CeO2 NPs was crystallite with cubic phase structure and the estimated average crystallite size of CeO2 NPs using Scherer's and W-H method was significantly different due to their assumptions. Further, it is purposed to study their photocatalytic biological activities.

Impedance analysis and dielectric response of anatase TiO2 nanoparticles codoped with Mn and Co ions

NASA Astrophysics Data System (ADS)

Kumar, Anand; Kashyap, Manish K.; Sabharwal, Namita; Kumar, Sarvesh; Kumar, Ashok; Kumar, Parmod; Asokan, K.

2017-11-01

In order to elucidate the effect of transition metal (TM) doping, the impedance and dielectric responses of Co and/or Mn-doped TiO2 nanocrystalline powder samples with 3% doping concentration synthesized via sol gel technique, have been analyzed. X-ray diffraction (XRD) analysis confirms the formation of tetragonal TiO2 anatase phase for all studied samples without any extra impurity phase peaks. The variation in the grain size measured from field emission scanning electron microscope (FESEM) measurements for all the samples are in accordance with the change in crystallite size as obtained from XRD. The DC resistivity for pure TiO2 nanoparticles is the highest while codoped samples exhibit low resistivity. The temperature dependent dielectric constant and dielectric loss possess step like enhancement and show the relaxation behavior. At room temperature, the dielectric function and dielectric loss decrease rapidly with increase in frequency and become almost constant at the higher frequencies. Such a decrease in dielectric loss is suitable for energy storage devices.

Milestone Report - M3FT-15OR03120215 - Recommend HIP Conditions for AgZ

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bruffey, Stephanie H.; Jubin, Robert Thomas

2015-09-18

The purpose of this study was to continue research to determine if HIPing could directly convert I-Ag 0Z into a suitable waste form. Fiscal year (FY) 2015 work completed studies of Phase IIA, IIB, and IIC samples. Product consistency testing (PCT) of Phase IIA samples resulted in iodine release below detection limit for six of twelve samples. This is promising and indicates that a durable waste form may be produced through HIPing even if transformation of the zeolite to a distinct mineral phase does not occur. From PCT results of Phase IIA samples, it was determined that future pressing shouldmore » be conducted at a temperature of 900°C. Phase IIC testing continued production of samples to examine the effects of multiple source materials, compositional variations, and an expanded temperature range. The density of each sample was determined and x-ray diffraction (XRD) patterns were obtained. In all cases, there was nothing in the XRD analyses to indicate the creation of any AgI-containing silicon phase; the samples were found to be largely amorphous.« less

One pot synthesis of pure micro/nano photoactive α-PbO crystals

NASA Astrophysics Data System (ADS)

Bhagat, Dharini; Waldiya, Manmohansingh; Vanpariya, Anjali; Mukhopadhyay, Indrajit

2018-05-01

The present study reports a simple, fast and cost effective precipitation technique for synthesis of pure α-PbO powder. Lead monoxide powder with tetragonal structure was synthesized chemically at an elevated temperature using lead acetate and sodium hydroxide solution bath. XRD powder diffraction was used to find the structural properties as well as phase transition from alpha to beta. Study revealed that synthesized PbO powder was crystalline with tetragonal symmetry, having an average crystallite size of 70 nm and lattice constants; a=3.97Å, b=3.97Å, and c=5.02Å. Phase transition from tetragonal to orthorhombic structure was studied by comparing the XRD data of the annealed samples in the temperature range from 200 °C to 600 °C. UV-Visible spectroscopy was used to find out the optical properties of prepared PbO powder. Diffuse reflectance and absorbance spectra confirmed the formation of α-PbO with obtained direct band gap of 1.9 eV. Synthesized lead monoxide (α-PbO) powder has promising application in energy conversion as well as energy storage applications.

Microstructural and thermal properties of pure BaFe{sub 12}O{sub 19} and Sr doped barium ferrite (Ba{sub 0.9}Sr{sub 0.1}Fe{sub 12}O{sub 19}) synthesized by auto combustion method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Taufeeq, Saba, E-mail: sabataufeeq23@gmail.com; Parveen, Azra; Agrawal, Shraddha

2016-05-23

Nanoparticles (NPs) of Pure BaFe{sub 12}O{sub 19} and Strontium doped Barium Ferrite (Ba{sub 0.9}Sr{sub 0.1}Fe{sub 12}O{sub 19}) have been successfully synthesized by Auto combustion method using citric acid as a chelating agent and calcined at 450°C for 3 hrs and 850°C for 4 hrs. Microstructural studies were carried by XRD and SEM techniques. Structural studies suggest that the crystal system remains hexagonal even with the doping of Strontium. The XRD analysis confirms the formation of the structures in the nanometer regime and the peaks are the evidence of the crystalline phase. The SEM images shows the morphology of surface ofmore » the samples. The thermal property studied by TGA shows the weight loss which is with varying the temperature and weight loss also varies with Sr doping. The TGA analysis exhibits the loss of weight at different temperatures.« less

Bricks in historical buildings of Toledo City: characterisation and restoration

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lopez-Arce, Paula; Garcia-Guinea, Javier; Gracia, Mercedes

2003-01-15

Two different types of ancient bricks (12th to 14th centuries) collected from historical buildings of Toledo (Spain) were characterised by optical microscopy, scanning electron microscopy/energy-dispersive X-ray spectrometers (SEM/EDS), electron probe microanalysis (EM), X-ray diffraction (XRD), differential thermal analysis (DTA) and {sup 57}Fe-Moessbauer spectroscopy. Physical properties such as water absorption and suction, porosity, density and compression strength were also determined. Several minerals found in the brick matrix, such as garnet, let us infer raw material sources; calcite, dolomite, illite and neoformed gehlenite and diopside phases, on temperature reached in firing; secondary calcite, on first cooling scenarios; and manganese micronodules, on latemore » pollution environments. XRD and DTA of original and refired samples supply information about firing temperatures. Additional data on firing conditions and type of the original clay are provided by the Moessbauer study. Physical properties of both types of bricks were compared and correlated with raw materials and fabric and firing technology employed. The physicochemical characterisation of these bricks provides valuable data for restoration purposes to formulate new specific bricks using neighbouring raw materials.« less

Synthesis and electrical behavior of Ni-Ti substituted Y-type hexaferrites for high frequency application

NASA Astrophysics Data System (ADS)

Ahmad, Bashir; Ashiq, Muhammad Naeem; Mumtaz, Saleem; Ali, Irshad; Najam-Ul-Haq, Muhmmad; Sadiq, Imran

2018-04-01

This article reports the fabrication of Ni-Ti doped derivatives of Sr2Co2Fe12-2xO22 by economical Sol-gel method. At room temperature X-ray diffraction (XRD) pattern of powder was obtained after sintering at 1050 °C. The XRD analysis revealed the formation of pure Sr-Y hexaferrite phase. It was found that the observed values of dielectric parameters decreased with increasing Ni-Ti substitution. The higher values of dielectric constants and dielectric loss factor at lower frequency were owing to surface charge polarization. In all the samples the resonance peaks were also observed. The observed room temperature DC electrical resistivity found to increase from 1.8x106 to 4.9x109 ohm cm. The observed activation energies values of the fabricated materials are found in 0.52-0.82 eV range. The decrease in dielectric parameters and increase in resistivity of the fabricated samples with substituents suggest these materials have worth application in micro-wave devices as such devices required highly resistive materials.

High thermal behavior of a new glass ceramic developed from silica xerogel/SnO{sub 2} composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aripin, H., E-mail: aripin@unsil.ac.id; Mitsudo, Seitaro, E-mail: mitsudo@fir.u-fukui.ac.jp; Sudiana, I. Nyoman, E-mail: sudiana75@yahoo.com

2016-02-08

In this investigation, a new glass ceramics have been produced by mixing SnO{sub 2} and amorphous silica xerogel (ASX) extracted from sago waste ash. The composition has been prepared by adding 10 mol% of SnO{sub 2} into SX. The samples have been dry pressed and sintered in the temperature range between 800 °C and 1500 °C. The effects of temperature on the crystallization of silica xerogel after adding SnO{sub 2} and their relationship to bulk density have been studied. The crystallization process of the silica xerogel/SnO{sub 2} composite has been examined by an X-ray diffraction (XRD) and the bulk density hasmore » been characterized on the basis of the experimental data obtained using Archimedes′ principle. It has been found that an addition of SnO{sub 2} confers an appreciable effect on the grain and from the interpretation of XRD patterns allow one to explain the increase in the density by an increased crystallite size of SnO{sub 2} in the composite.« less

High thermal behavior of a new glass ceramic developed from silica xerogel/SnO2 composite

NASA Astrophysics Data System (ADS)

Aripin, H.; Mitsudo, Seitaro; Sudiana, I. Nyoman; Priatna, Edvin; Sabchevski, Svilen

2016-02-01

In this investigation, a new glass ceramics have been produced by mixing SnO2 and amorphous silica xerogel (ASX) extracted from sago waste ash. The composition has been prepared by adding 10 mol% of SnO2 into SX. The samples have been dry pressed and sintered in the temperature range between 800 °C and 1500 °C. The effects of temperature on the crystallization of silica xerogel after adding SnO2 and their relationship to bulk density have been studied. The crystallization process of the silica xerogel/SnO2 composite has been examined by an X-ray diffraction (XRD) and the bulk density has been characterized on the basis of the experimental data obtained using Archimedes' principle. It has been found that an addition of SnO2 confers an appreciable effect on the grain and from the interpretation of XRD patterns allow one to explain the increase in the density by an increased crystallite size of SnO2 in the composite.

Magnetic transition in Y-site doped multiferroic YMnO3

NASA Astrophysics Data System (ADS)

Thakur, Rajesh K.; Thakur, Rasna; Gaur, N. K.

2016-05-01

We have synthesized polycrystalline hexagonal Y1-xSrxMnO3 (x=0.02, 0.1) compounds by using conventional solid state reaction method. The detailed structural investigations are carried out by using XRD studies which reveals the single phase formation of the reported compounds with hexagonal structure and space group P63cm (JCPDS: 25-1079). Further the XRD data of reported compounds were analyzed by RIETVELD (FULLPROFF) method which shows the decrease in the lattice parameter with increasing concentration of divalent strontium to Y-site. The observed pointed kinks in the specific heat study are indicative of the probable coupling in between the electric and magnetic orders in this class of materials. The reported systematic specific heat studies shows that the antiferromagnetic (AFM) transition temperature (TN) shifts to higher value with increasing concentration of Sr2+ ion in the YMnO3 compound which is attributed to the enhanced lattice contribution to the specific heat in the this compound. The present compound shows the independence of specific heat and magnetic transition temperature with applied magnetic field of 8T and 12T.

Molten salt synthesis and luminescent properties of YVO4:Ln (Ln = Eu3+, Dy3+) nanophosphors.

PubMed

Liu, Chenglu; Wang, Fang; Jia, Peiyun; Lin, Jun; Zhou, Zhiqiang

2012-01-01

Eu3+ and Dy(3+)-doped YVO4 nanocrystallites were successfully prepared at 400 degrees C in equal moles of NaNO3 and KNO3 molten salts. X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, transmission electronic microscopy (TEM), photoluminescence (PL) spectrum and lifetime were used to characterize the nanocrystallites. XRD results demonstrate that NaOH concentration and annealing temperature play important roles in phase purity and crystallinity of the nanocrystallites, the optimum NaOH concentration and annealing temperature being 6:40 and 400 degrees C respectively. TEM micrographs show the nanocrystallites are well crystallized with a cubic morphology in an average grain size of about 18 nm. Upon excitation of the vanadate group at 314 nm, YVO4:Eu3+ and YVO4:Dy3+ nanocrystallites exhibit the characteristic emission of Eu3+ and Dy3+, which indicates that there is an energy transfer from the vanadate group to the rare earth ions. Moreover, the structure and luminescent properties of the nanocrystallites were compared with their bulk counterparts with same composition in detail.

Microstructure Characterization and Wear-Resistant Properties Evaluation of an Intermetallic Composite in Ni-Mo-Si System.

PubMed

Huang, Boyuan; Song, Chunyan; Liu, Yang; Gui, Yongliang

2017-02-04

Intermetallic compounds have been studied for their potential application as structural wear materials or coatings on engineering steels. In the present work, a newly designed intermetallic composite in a Ni-Mo-Si system was fabricated by arc-melting process with commercially pure metal powders as starting materials. The chemical composition of this intermetallic composite is 45Ni-40Mo-15Si (at %), selected according to the ternary alloy diagram. The microstructure was characterized using optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), and energy dispersive spectroscopy (EDS), and the wear-resistant properties at room temperature were evaluated under different wear test conditions. Microstructure characterization showed that the composite has a dense and uniform microstructure. XRD results showed that the intermetallic composite is constituted by a binary intermetallic compound NiMo and a ternary Mo₂Ni₃Si metal silicide phase. Wear test results indicated that the intermetallic composite has an excellent wear-resistance at room-temperature, which is attributed to the high hardness and strong atomic bonding of constituent phases NiMo and Mo₂Ni₃Si.

One Step Synthesis of NiO Nanoparticles via Solid-State Thermal Decomposition at Low-Temperature of Novel Aqua(2,9-dimethyl-1,10-phenanthroline)NiCl2 Complex

PubMed Central

Barakat, Assem; Al-Noaimi, Mousa; Suleiman, Mohammed; Aldwayyan, Abdullah S.; Hammouti, Belkheir; Ben Hadda, Taibi; Haddad, Salim F.; Boshaala, Ahmed; Warad, Ismail

2013-01-01

[NiCl2(C14H12N2)(H2O)] complex has been synthesized from nickel chloride hexahydrate (NiCl2·6H2O) and 2,9-dimethyl-1,10-phenanthroline (dmphen) as N,N-bidentate ligand. The synthesized complex was characterized by elemental analysis, infrared (IR) spectroscopy, ultraviolet-visible (UV-vis) spectroscopy and differential thermal/thermogravimetric analysis (TG/DTA). The complex was further confirmed by single crystal X-ray diffraction (XRD) as triclinic with space group P-1. The desired complex, subjected to thermal decomposition at low temperature of 400 ºC in an open atmosphere, revealed a novel and facile synthesis of pure NiO nanoparticles with uniform spherical particle; the structure of the NiO nanoparticles product was elucidated on the basis of Fourier transform infrared (FT-IR), UV-vis spectroscopy, TG/DTA, XRD, scanning electron microscopy (SEM), energy-dispersive X-ray spectrometry (EDXS) and transmission electron microscopy (TEM). PMID:24351867

Cyanidation Study of Slag Rich in Silver

NASA Astrophysics Data System (ADS)

Pérez-Labra, Miguel; Romero-Serrano, J. Antonio; Ávila-Davila, E. O.; Reyes-Pérez, M.; Barrientos-Hernández, F. R.; Hernández, I. A. Lira

Slag from smelting reduction processes were characterized by chemical analysis, XRD, SEM-EDS and XRF. The results revealed Ag concentrations of 362 g/t of slag, the slag mineralogical characterization by XRD and SEM-EDS showed mineralogical species oxidized complex containing Pb, Zn, Ca, Si, Fe, As, S in its structure, silver was found in globules associated lead in the slag and the furutobeite specie. The leaching study was conducted to evaluate process variables such as NaCN concentration: from 7.8×10-3M - 1.26×10-1M, temperature: 25-50°C, particle size: +140 mesh to -400 mesh, stirring speed of 750 rpm - 900 rpm. All studies were performed with a NaOH concentration of 0.2 M. The optimal values of silver recovery encountered in conditions of 7.8×10-3M NaCN, agitation rate of 750 rpm, temperature of 35°C and with a treatment time of 240 min. We also observed that a particle size -400 mesh will have optimum recoveries compared to +140 mesh, +200, +270 and +325.

Enhanced electrochemical performance of a ZnO-MnO composite as an anode material for lithium ion batteries.

PubMed

Song, Min Seob; Nahm, Sahn; Cho, Won Il; Lee, Chongmok

2015-09-28

A ZnO-MnO composite was synthesized using a simple solvothermal method combined with a high-temperature treatment. To observe the phase change during the heating process, in situ high-temperature XRD analysis was performed under vacuum conditions. The results indicated that ZnMn2O4 transformed into the ZnO-MnO composite phase starting from 500 °C and that this composite structure was retained until 700 °C. The electrochemical performances of the ZnO-MnO composite electrode were evaluated through galvanostatic discharge-charge tests and cyclic voltammetry analysis. Its initial coulombic efficiency was significantly improved to 68.3% compared to that of ZnMn2O4 at 54.7%. Furthermore, the ZnO-MnO composite exhibited improved cycling performance and enhanced rate capability compared with untreated ZnMn2O4. To clarify the discharge-charge mechanism of the ZnO-MnO composite electrode, the structural changes during the charge and discharge processes were also investigated using ex situ XRD and TEM.

Improvement of magnetic and ferroelectric properties of BiFeO{sub 3} nanoparticles on Tb and Co substitution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Das, A.; De, S.; Chatterjee, S.

2016-05-06

Tb and Co substituted bismuth ferrite nanoparticles (NPs) with chemical composition Bi{sub 1-x}Tb{sub x}Fe{sub 1-y}Co{sub y}O{sub 3} (x = 0, 0.05; y = 0, 0.05) have been synthesized by a sol-gel method and characterized by x-ray diffraction (XRD), Mossbauer spectroscopy, dc magnetization and electric polarization measurements. The aim of the present work is to improve ferroelectric properties of BiFeO{sub 3} by substitution of Tb{sup 3+} ions in Bi{sup 3+} site and magnetic properties by substitution of Co{sup 2+} in Fe{sup 3+} site. The XRD patterns of all prepared samples show formation of the desired phase along with a small amountmore » of impurity. Room temperature Mossbauer spectroscopic studies reveal that all samples are in magnetically ordered state. Magnetic hysteresis loops of all samples indicate a significant enhancement of magnetic moment and coercivity whereas electric polarization measurements at room temperature reveal an improvement of ferroelectric properties in the co-substituted sample.« less

Generalized green synthesis and formation mechanism of sponge-like ferrite micro-polyhedra with tunable structure and composition

NASA Astrophysics Data System (ADS)

Tong, Guoxiu; Du, Fangfang; Xiang, Lingjing; Liu, Fangting; Mao, Lulu; Guan, Jianguo

2013-12-01

This paper describes a green versatile glucose-engineered precipitation-sintering process that allows for the selective and mass preparation of spongy porous ferrite (M = Fe, Zn, Co, Ni, Mn, etc.) micro-polyhedra with tunable morphology, texture, and composition. Some kinetic factors, such as the molar ratio of glucose to metal nitrates, reaction temperature, sintering temperature and time, and type of metal nitrates, can be expediently employed to modulate their aspect ratio, shape, size, composition, and textural properties. In this protocol, glucose functions as a reductant, protecting agent, structure-directing agent, and a sacrificial template to guide the assembly of sheet-like nuclei into polyhedral precursors and the formation of spongy porous structures. Owing to larger EM parameters, multiresonant behavior, and dissipative current, spongy porous Fe3O4 polyhedra exhibited enhanced microwave-absorbing properties. This endows them with important potential applications in magnetic devices, catalysis, sorption, photoluminescence, electromagnetic wave absorbing materials, anode materials, and so on. Meanwhile, this general approach can be extended to synthesize other porous sponges with regular geometric configuration because it is simple, inexpensive, environmentally benign, and suitable for extensive production.This paper describes a green versatile glucose-engineered precipitation-sintering process that allows for the selective and mass preparation of spongy porous ferrite (M = Fe, Zn, Co, Ni, Mn, etc.) micro-polyhedra with tunable morphology, texture, and composition. Some kinetic factors, such as the molar ratio of glucose to metal nitrates, reaction temperature, sintering temperature and time, and type of metal nitrates, can be expediently employed to modulate their aspect ratio, shape, size, composition, and textural properties. In this protocol, glucose functions as a reductant, protecting agent, structure-directing agent, and a sacrificial template to guide the assembly of sheet-like nuclei into polyhedral precursors and the formation of spongy porous structures. Owing to larger EM parameters, multiresonant behavior, and dissipative current, spongy porous Fe3O4 polyhedra exhibited enhanced microwave-absorbing properties. This endows them with important potential applications in magnetic devices, catalysis, sorption, photoluminescence, electromagnetic wave absorbing materials, anode materials, and so on. Meanwhile, this general approach can be extended to synthesize other porous sponges with regular geometric configuration because it is simple, inexpensive, environmentally benign, and suitable for extensive production. Electronic supplementary information (ESI) available: Nitrogen adsorption-desorption isotherms, the corresponding pore size distribution curves, TG-DSC curves, XRD pattern, and IR spectra for the precursors; XRD patterns of the samples obtained at various temperatures under N2; XRD pattern, reduction rate, and reactive oxygen species production of ZnO-ZnFe2O4 XRD patterns, SEM images, EDX patterns, nitrogen adsorption-desorption isotherms, and the corresponding pore size distribution curves of CoFe2O4-NiFe2O4-Co1.29Ni1.71O4 polyhedra and NiO-ZnFe2O4. See DOI: 10.1039/c3nr03745b

Quantitative XRD analysis of {110} twin density in biotic aragonites.

PubMed

Suzuki, Michio; Kim, Hyejin; Mukai, Hiroki; Nagasawa, Hiromichi; Kogure, Toshihiro

2012-12-01

{110} Twin densities in biotic aragonite have been estimated quantitatively from the peak widths of specific reflections in powder X-ray diffraction (XRD) patterns, as well as direct confirmation of the twins using transmission electron microscopy (TEM). Influence of the twin density on the peak widths in the XRD pattern was simulated using DIFFaX program, regarding (110) twin as interstratification of two types of aragonite unit layers with mirrored relationship. The simulation suggested that the twin density can be estimated from the difference of the peak widths between 111 and 021, or between 221 and 211 reflections. Biotic aragonite in the crossed-lamellar microstructure (three species) and nacreous microstructure (four species) of molluscan shells, fish otoliths (two species), and a coral were investigated. The XRD analyses indicated that aragonite crystals in the crossed-lamellar microstructure of the three species contain high density of the twins, which is consistent with the TEM examination. On the other hand, aragonite in the nacre of the four species showed almost no difference of the peak widths between the paired reflections, indicating low twin densities. The results for the fish otoliths were varied between the species. Such variation of the twin density in biotic aragonites may reflect different schemes of crystal growth in biomineralization. Copyright © 2012 Elsevier Inc. All rights reserved.

Simulation and measurement of nanometer-scale resistivity of copper films for interconnect applications

NASA Astrophysics Data System (ADS)

Yarimbiyik, Arif Emre

2007-12-01

A highly versatile simulation program is developed and used to examine how the resistivity of thin metal films and lines increases as their dimensions approach and become smaller than the mean fee path of electrons in metals such as copper (size effect). The simulation program: (1) provides a more accurate calculation of surface scattering effects than that obtained from the usual formulation of Fuchs' theory, (2) calculates grain-boundary effects that are consistent with the theory of Mayadas and Shatzkes, (3) includes the effects of surface and grain-boundary scattering either separately or together, and (4) simulates the effect on resistivity if a surface of a film or line has a different value for the scattering parameter. The increase in resistivity with decreasing thickness of thin, evaporated copper films (approximately 10 nm to 150 nm thick) was determined from sheet resistance and film thickness measurements. Good agreement between the experimental results with those of the simulation program was obtained when the measured mean grain sizes were used by the simulation program. The mean of the grain sizes tend to decrease with decreasing film thickness and thereby increase the impact of grain-boundary scattering on the effective resistivity of the film. Estimates of the mean grain size for each film were determined from using, in combination, the electron backscatter diffraction (EBSD) and the X-ray diffraction (XRD) methods. With values for the measured change in sheet resistance with temperature of these films, it is shown that measurements of the electrical film thickness, using Matthiessen's rule, agreed to within 3 nm of the physical measurements (profilometer) of these films. Hence, Matthiessen's rule can continue to be used to measure the thickness of a copper film and, by inference, the cross-sectional area of a copper line for dimensions well below the mean free path of electrons in copper at room temperature (39 nm).

Uncovering the local inelastic interactions during manufacture of ductile cast iron: How the substructure of the graphite particles can induce residual stress concentrations in the matrix

NASA Astrophysics Data System (ADS)

Andriollo, Tito; Hellström, Kristina; Sonne, Mads Rostgaard; Thorborg, Jesper; Tiedje, Niels; Hattel, Jesper

2018-02-01

Recent X-ray diffraction (XRD) measurements have revealed that plastic deformation and a residual elastic strain field can be present around the graphite particles in ductile cast iron after manufacturing, probably due to some local mismatch in thermal contraction. However, as only one component of the elastic strain tensor could be obtained from the XRD data, the shape and magnitude of the associated residual stress field have remained unknown. To compensate for this and to provide theoretical insight into this unexplored topic, a combined experimental-numerical approach is presented in this paper. First, a material equivalent to the ductile cast iron matrix is manufactured and subjected to dilatometric and high-temperature tensile tests. Subsequently, a two-scale hierarchical top-down model is devised, calibrated on the basis of the collected data and used to simulate the interaction between the graphite particles and the matrix during manufacturing of the industrial part considered in the XRD study. The model indicates that, besides the viscoplastic deformation of the matrix, the effect of the inelastic deformation of the graphite has to be considered to explain the magnitude of the XRD strain. Moreover, the model shows that the large elastic strain perturbations recorded with XRD close to the graphite-matrix interface are not artifacts due to e.g. sharp gradients in chemical composition, but correspond to residual stress concentrations induced by the conical sectors forming the internal structure of the graphite particles. In contrast to common belief, these results thus suggest that ductile cast iron parts cannot be considered, in general, as stress-free at the microstructural scale.

Nanostructural Characters of β-SiC Nanoparticles Prepared from Indonesian Natural Resource using Sonochemical Method

NASA Astrophysics Data System (ADS)

Fuad, A.; Kultsum, U.; Taufiq, A.; Hartatiek; Latifah, E.

2018-04-01

Silicon carbide (SiC) nanoparticles become one of the interesting non-oxide ceramics due to their physical and chemical properties. For an extended period, SiC nanoparticles have been prepared by several methods that usually performed at high temperatures ranging from 1200 - 2000 °C from inexpensive commercial precursors. In this work, we prepared SiC nanoparticles from the low priced precursor of Indonesia natural resource using the sonochemical method at a temperature that is lower than 1000 °C. To produce samples with particular characters, we varied the sintering holding time (1, 10, and 20 hours) and the sintering temperatures (850, 950, and 1050 °C) during the synthesis. The samples were then characterized using XRD, SEM-EDX, TEM, and FTIR. The XRD data analysis showed that the samples have a dominant phase of SiC in the form of β-SiC with a 3C-SiC structure and SiO2 phase in a low composition within a good agreement with the EDX characterization. Interestingly, the sample prepared at the sintering temperature of 850 °C for 1 hour showed a non-crystallite phase. Using a Scherer’s equation, the particles of the samples sized from 13 to 18 nm, which were validated by SEM and TEM images. Furthermore, the FT-IR spectra presented several peaks, i.e., at wavenumbers of 482.2 and 1150 cm-1 representing Si-O-Si bonding and also at 798.5 cm-1 regarding with Si-C bonding.

Investigation of Pb doping on electrical, structural and superconducting properties of YBa2-xPbxCu3O7-δ superconductors

NASA Astrophysics Data System (ADS)

Ezzatpour, S.; Sharifzadegan, L.; Sarvari, F.; Sedghi, H.

2018-06-01

In this study the high temperature superconductor YBa2-xPbxCu3O7-δ with doping x = ,0.05,0.1,0.15 were prepared by the standard solid-state reaction method. The effect of Pb substitution on Ba site of YBCO superconducting system, structural, electrical and superconducting properties of Y-based superconductor has been investigated. The measurements of dc resisitivity were performed on all samples with four-probe method using low frequency/lowAC current (4 mA) . The superconducting temperature, Tc, were determined from the resistivity versus temperature (R-T) curves. Results show that Pb doping reduced the cirtical temperature(Tc) and superconductivity properties of our samples. The maximum and the minimum Tc were observed for the samples with x = 0.15 and x = 0.1 respectively. The structure and phase purity of samples were examined by the X-ray powder diffraction technique (XRD) performed by means of D8 Advance Bruker diffractometer with Cu kα radiation. The grain morphology of surface of the samples was analyzed by sacanning electron microscopy (SEM). XRD patterns of polycrystalline materials of composition YBa2-xPbxCu3O7-δ revealed that all prepared samples are orthorhombic. All of the peaks of YBCO and YBa2-xPbxCu3O7-δ have been used for the estimation of volume fractions of the phases and ignored the void peaks.

The formation of illite from nontronite by mesophilic and thermophilic bacterial reaction

USGS Publications Warehouse

Jaisi, Deb P.; Eberl, Dennis D.; Dong, Hailiang; Kim, Jinwook

2011-01-01

The formation of illite through the smectite-to-illite (S-I) reaction is considered to be one of the most important mineral reactions occurring during diagenesis. In biologically catalyzed systems, however, this transformation has been suggested to be rapid and to bypass the high temperature and long time requirements. To understand the factors that promote the S-I reaction, the present study focused on the effects of pH, temperature, solution chemistry, and aging on the S-I reaction in microbially mediated systems. Fe(III)-reduction experiments were performed in both growth and non-growth media with two types of bacteria: mesophilic (Shewanella putrefaciens CN32) and thermophilic (Thermus scotoductus SA-01). Reductive dissolution of NAu-2 was observed and the formation of illite in treatment with thermophilic SA-01 was indicated by X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM). A basic pH (8.4) and high temperature (65°C) were the most favorable conditions for the formation of illite. A long incubation time was also found to enhance the formation of illite. K-nontronite (non-permanent fixation of K) was also detected and differentiated from the discrete illite in the XRD profiles. These results collectively suggested that the formation of illite associated with the biologically catalyzed smectite-to-illite reaction pathway may bypass the prolonged time and high temperature required for the S-I reaction in the absence of microbial activity.

Low-temperature hydrothermal synthesis of ZnO nanorods: Effects of zinc salt concentration, various solvents and alkaline mineralizers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Edalati, Khatereh, E-mail: kh_ed834@stu.um.ac.ir; Shakiba, Atefeh; Vahdati-Khaki, Jalil

2016-02-15

Highlights: • We synthesized ZnO nanorods by a simple hydrothermal process at 60 °C. • Effects of zinc salt concentration, solvent and alkaline mineralizer was studied. • Increasing concentration of zinc salt changed ZnO nucleation system. • NaOH yielded better results in the production of nanorods in both solvents. • Methanol performed better in the formation of nanorods using the two mineralizers. - Abstract: ZnO has been produced using various methods in the solid, gaseous, and liquid states, and the hydrothermal synthesis at low temperatures has been shown to be an environmentally-friendly one. The current work utilizes a low reactionmore » temperature (60 °C) for the simple hydrothermal synthesis of ZnO nanorod morphologies. Furthermore, the effects of zinc salt concentration, solvent type and alkaline mineralizer type on ZnO nanorods synthesis at a low reaction temperature by hydrothermal processing was studied. Obtained samples were analyzed using X-ray powder diffraction (XRD) and scanning electron microscopy (SEM). Increasing the concentration of the starting zinc salt from 0.02 to 0.2 M changed ZnO nucleation system from the homogeneous to the heterogeneous state. The XRD results confirmed the production hexagonal ZnO nanostructures of with a crystallite size of 40.4 nm. Varying the experimental parameters (mineralizer and solvent) yielded ZnO nanorods with diameters ranging from 90–250 nm and lengths of 1–2 μm.« less

Influence of deposition substrate temperature on the morphology and molecular orientation of chloroaluminum phthalocyanine films as well the performance of organic photovoltaic cells.

PubMed

Zheng, Yan-Qiong; Zhang, Jing; Yang, Fang; Komino, Takeshi; Wei, Bin; Zhang, Jianhua; Wang, Zixing; Pu, Wenhong; Yang, Changzhu; Adachi, Chihaya

2015-10-09

The dependence of the morphology of neat chloroaluminum phthalocyanine (ClAlPc) films on substrate temperature (Tsub) during deposition is investigated by variable angle spectroscopic ellipsometry (VASE), x-ray diffraction (XRD), and atomic force microscopy (AFM) to obtain detailed information about the molecular orientation, phase separation, and crystallinity. AFM images indicate that both grain size and root mean square (RMS) roughness noticeably increase with Tsub both in neat and blend films. Increasing Tsub from room temperature to 420 K increases the horizontal orientation of the ClAlPc molecules with an increase of the mean molecular tilt angle from 60.13° (300 K) to 65.86° (420 K). The UV-vis absorption band of the corresponding films increases and the peak wavelength slightly red shifts with the Tsub increase. XRD patterns show a clear diffraction peak at Tsub over 390 K, implying the π-stacking of interconnected ClAlPc molecules at high Tsub. Planar and bulk heterojunction (BHJ) photovoltaic cells containing pristine ClAlPc films and ClAlPc:C60 blend films fabricated at Tsub of 390 K show increases in the power conversion efficiency (ηPCE) of 28% (ηPCE = 3.12%) and 36% (ηPCE = 3.58%), respectively, relative to devices as-deposited at room temperature. The maximum short circuit current in BHJs is obtained at 390 K in the Tsub range from 300 K to 450 K.

Single crystal growth, crystalline structure investigation and high-pressure behavior of impurity-free siderite (FeCO3)

NASA Astrophysics Data System (ADS)

Liang, Wen; Yin, Yuan; Li, Zeming; Li, Rui; Li, Lin; He, Yu; Dong, Haini; Li, Zengsheng; Yan, Shuai; Zhai, Shuangmeng; Li, Heping

2018-03-01

Single crystals of impurity-free siderite were grown successfully using high-temperature-pressure annealing. The size of crystals ranged up to 100 µm, and they exhibited a rhomboid shape upon cleavage along the (101) plane. The composition of Fe0.9988±0.0011CO3 was quantified using electron probe analysis. Accurate crystalline structural data were investigated by means of single crystal X-ray diffraction (XRD) and the unit cell dimensions obtained in the rhombohedral symmetry of the R\\bar {3}c space group were a = 4.6861(3) and c = 15.362(2), and the final R = 0.0499. Using in situ synchrotron XRD, the high-pressure behavior of impurity-free siderite was investigated up to 20 GPa at ambient temperature. The pressure-volume (P-V) EoS was fitted by a third-order Birch-Murnaghan equation, and the isothermal bulk modulus was K 0 = 97.5(11) GPa for K 0' = 4. High-pressure Raman spectroscopy was performed at up to 30 GPa at ambient temperature, and the Raman bands shifted as the increase of pressure ({{d/ν _i}}{{{d}P}} ) was determined. In combination with the high-pressure Raman results and the bulk modulus K 0, the mode Grüneisen parameters of each vibration were calculated. Meanwhile, high-temperature Raman spectroscopy was carried out at up to 300 °C and the Raman band shift ({{d/ν _i}}{{{d}t}} ) was also quantified.

Characterization of ZnAl cast alloys with Na addition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gancarz, Tomasz, E-mail: t.gancarz@imim.pl; Cempura, Grzegorz; Skuza, Wojciech

2016-01-15

This study was aimed at evaluating the microstructural change and thermal, electrical and mechanical properties with the addition of Na to eutectic ZnAl alloys. Solders based on eutectic ZnAl containing 0.2 to 3.0 (wt.%) of Na were developed for high temperature solder. Differential scanning calorimetry (DSC) measurements were performed to determine the melting temperatures of the alloys. Thermal linear expansion and electrical resistivity measurements were performed over − 50 °C to 300 °C and 30 °C to 300 °C temperature ranges, respectively. The microstructure of the specimens was analyzed using scanning (SEM) and transmission electron microscopy (TEM) techniques. Chemical microanalysismore » was performed by energy-dispersive X-ray spectroscopy (EDS) on SEM and TEM. The precipitates of NaZn{sub 13} were confirmed by X-ray diffraction (XRD) measurements and selected area electron diffraction (SAED) techniques. The addition of Na to eutectic ZnAl alloy increased the electrical resistivity and reduced the coefficient of thermal expansion; however, the melting point did not change. The mechanical properties, strain and microhardness increased with Na content in alloys. - Highlights: • High temperature soldering materials of ZnAl with Na were designed and characterized. • Precipitates of NaZn{sub 13}were observed and confirmed using TEM and XRD. • Addition of Na to eutectic ZnAl cussed increased mechanical properties. • NaZn{sub 13} caused increased electrical resistivity and microhardness, and reduced the CTE.« less

Point defects in Cu 2 ZnSnSe 4 (CZTSe): Resonant X-ray diffraction study of the low-temperature order/disorder transition: Point defects in Cu 2 ZnSnSe 4 (CZTSe)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schelhas, L. T.; Stone, K. H.; Harvey, S. P.

The interest in Cu2ZnSn(S,Se)4 (CZTS) for photovoltaic applications is motivated by similarities to Cu(In,Ga)Se2 while being comprised of non-toxic and earth abundant elements. However, CZTS suffers from a Voc deficit, where the Voc is much lower than expected based on the band gap, which may be the result of a high concentration of point-defects in the CZTS lattice. Recently, reports have observed a low-temperature order/disorder transition by Raman and optical spectroscopies in CZTS films and is reported to describe the ordering of Cu and Zn atoms in the CZTS crystal structure. To directly determine the level of Cu/Zn ordering, wemore » have used resonant-XRD, a site, and element specific probe of long range order. We used CZTSe films annealed just below and quenched from just above the transition temperature; based on previous work, the Cu and Zn should be ordered and highly disordered, respectively. Our data show that there is some Cu/Zn ordering near the low temperature transition but significantly less than high chemical order expected from Raman. To understand both our resonant-XRD results and the Raman results, we present a structural model that involves antiphase domain boundaries and accommodates the excess Zn within the CZTS lattice.« less

Fabrication of solar light induced Fe-TiO{sub 2} immobilized on glass-fiber and application for phenol photocatalytic degradation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lin, Shaohua, E-mail: linsh75@163.com; Zhang, Xiwang; Sun, Qinju

2013-11-15

Graphical abstract: - Highlights: • Fe-doped TiO{sub 2} immobilized on glass-fiber net were prepared by sol–gel method. • Fe inhibited the phase transition of TiO{sub 2} from anatase to rutile. • The optimal Fe doping dose was around 0.005 wt%. • The optimal calcination temperature was around 600 °C. - Abstract: Iron-doped anatase titanium dioxide catalysts coated on glass-fiber were successfully synthesized by a dip-coating sol–gel method. The prepared catalysts were characterized by scanning electron microscopy (SEM) with energy dispersive X-ray (EDX) analysis, X-ray diffraction (XRD), UV-Vis diffuse reflectance spectroscopy to understand the synthesis mechanism, and their photocatalytic activities weremore » evaluated by photodegradation of phenol under simulated solar irradiation. EDX analysis confirmed the existence of iron in the immobilized catalysts. XRD suggested that the phase transition of the catalysts from anatase to rutile were restrained, and almost pure anatase TiO{sub 2} could retain even the calcination temperature reached 800 °C. The UV-Vis diffuse reflectance spectroscopy of the catalysts showed a red shift and increased photoabsorbance in the visible range for all the doped samples. Iron loading and calcination temperature have obvious influences on photocatalytic activity. In this study, the optimal doping dose and calcination temperature were around 0.005 wt% and 600 °C, respectively.« less

Spectroscopy analysis of graphene like deposition using DC unbalanced magnetron sputtering on γ‐Al{sub 2}O{sub 3} buffer layer

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aji, A. S., E-mail: yudi@fi.itb.ac.id; Darma, Y., E-mail: yudi@fi.itb.ac.id

In this work, graphene-like deposition using DC unbalanced magnetron-sputtering technique on γ‐Al{sub 2}O{sub 3} layer at low temperature has been systematically studied. The γ‐Al{sub 2}O{sub 3} was growth on silicon substrate using thermal evaporation of Al wire and continuing with dry oxidation of Al at 550 °C. Sputtering process were carried out using Fe-doped carbon pellet as a target by maintain the chamber pressure of 4.6×10{sup −2} Torr at substrate temperature of 300 °C for time deposition range of 1 to 4 hours. The quality of Al{sub 2}O{sub 3} on Si(100) and the characteristic of carbon thin film on γ‐Al{submore » 2}O{sub 3} were analized by mean XRD, opctical microscopy, EDAX, FTIR, and Raman spectra. XRD and optical microscopy analysis shows that Al{sub 2}O{sub 3} film is growth uniformly on Si substrate and forming the γ phase of Al{sub 2}O{sub 3}. Raman and FTIR spectra confirm the formation of graphene like carbon layer on Al{sub 2}O{sub 3}. Additionally, thermal annealing for some sample series have been performed to study their structural stability. The change of atomic structure due to thermal annealing were analized by XRD spectra. The quality and the number of graphene layers are investigated by using Raman spectra peaks analysis.« less

Magnetic response of hybrid ferromagnetic and antiferromagnetic core-shell nanostructures

NASA Astrophysics Data System (ADS)

Khan, U.; Li, W. J.; Adeela, N.; Irfan, M.; Javed, K.; Wan, C. H.; Riaz, S.; Han, X. F.

2016-03-01

The synthesis of FeTiO3-Ni(Ni80Fe20) core-shell nanostructures by a two-step method (sol-gel and DC electrodeposition) has been demonstrated. XRD analysis confirms the rhombohedral crystal structure of FeTiO3(FTO) with space group R3&cmb.macr;. Transmission electron microscopy clearly depicts better morphology of nanostructures with shell thicknesses of ~25 nm. Room temperature magnetic measurements showed significant enhancement of magnetic anisotropy for the permalloy (Ni80Fe20)-FTO over Ni-FTO core-shell nanostructures. Low temperature magnetic measurements of permalloy-FeTiO3 core-shell structure indicated a strong exchange bias mechanism with magnetic coercivity below the antiferromagnetic Neel temperature (TN = 59 K). The exchange bias is attributed to the alignment of magnetic moments in the antiferromagnetic material at low temperature. Our scheme opens a path towards optimum automotive systems and wireless communications wherein broader bandwidths and smaller sizes are required.The synthesis of FeTiO3-Ni(Ni80Fe20) core-shell nanostructures by a two-step method (sol-gel and DC electrodeposition) has been demonstrated. XRD analysis confirms the rhombohedral crystal structure of FeTiO3(FTO) with space group R3&cmb.macr;. Transmission electron microscopy clearly depicts better morphology of nanostructures with shell thicknesses of ~25 nm. Room temperature magnetic measurements showed significant enhancement of magnetic anisotropy for the permalloy (Ni80Fe20)-FTO over Ni-FTO core-shell nanostructures. Low temperature magnetic measurements of permalloy-FeTiO3 core-shell structure indicated a strong exchange bias mechanism with magnetic coercivity below the antiferromagnetic Neel temperature (TN = 59 K). The exchange bias is attributed to the alignment of magnetic moments in the antiferromagnetic material at low temperature. Our scheme opens a path towards optimum automotive systems and wireless communications wherein broader bandwidths and smaller sizes are required. Electronic supplementary information (ESI) available. See DOI: 10.1039/c5nr07946b

[Based on Curing Age of Calcined Coal Gangue Fine Aggregate Mortar of X-Ray Diffraction and Scanning Electron Microscopy Analysis].

PubMed

Dong, Zuo-chao; Xia, Jun-wu; Duan, Xiao-mu; Cao, Ji-chang

2016-03-01

By using X-ray diffraction (XRD) and environmental scanning electron microscope (SEM) analysis method, we stud- ied the activity of coal gangue fine aggregate under different calcination temperature. In view of the activity of the highest-700 degrees C high temperature calcined coal gangue fine aggregate mortar of hydration products, microstructure and strength were discussed in this paper, and the change laws of mortar strength with curing age (3, 7, 14, 28, 60 and 90 d) growth were analyzed. Test results showed that coal gangue fine aggregate with the increase of calcination temperature, the active gradually increases. When the calcination temperature reaches 700 degrees C, the activity of coal gangue fine aggregate is the highest. When calcining temperature continues to rise, activity falls. After 700 degrees C high temperature calcined coal gangue fine aggregate has obvious ash activity, the active components of SiO2 and Al2 O3 can be with cement hydration products in a certain degree of secondary hydration reaction. Through on the top of the activity of different curing age 700 degrees C high temperature calcined coal gangue fine aggregate mortar, XRD and SEM analysis showed that with the increase of curing age, secondary hydration reaction will be more fully, and the amount of hydration products also gradually increases. Compared with the early ages of the cement mortar, the products are more stable hydration products filling in mortar microscopic pore, which can further improve the microstructure of mortar, strengthen the interface performance of the mortar. The mortar internal structure is more uniform, calcined coal gangue fine aggregate and cement mortar are more of a strong continuous whole, which increase the later strength of hardened cement mortar, 700 degrees C high temperature calcined coal gangue fine aggregate pozzolanic effect is obvious.

Microstructure and Electrical Conductivity of ZnO Addition on the Properties of (Bi0.92Ho0.03Er0.05)2O3

NASA Astrophysics Data System (ADS)

Ermiş, İ.; Çorumlu, V.; Sertkol, M.; Öztürk, M.; Kaleli, M.; Çetin, A.; Turemiş, M.; Arı, M.

2016-11-01

The solid electrolyte is one of the most important components for a solid oxide fuel cell (SOFC). The various divalent or trivalent metal ion-doped bismuth-based materials exhibit good ionic conductivity. Therefore, these materials are used as electrolytes in the SOFC. In this paper, the samples of (Bi0.92- x Ho0.03Er0.05)2O3 + (ZnO) x solutions with a 0 ≤ x ≤ 0.2 molar ratio are synthesized by the solid state reaction method. The detailed structural and electrical characterizations are investigated by using x-ray diffraction (XRD), alternating current electrochemical impedance spectroscopy, and scanning electron microscopy (SEM). The XRD patterns of all samples are indexed on a monoclinic symmetry with a P21/c space group. In addition, the rietveld parameters are determined by using the FullProf software program. The impedance measurements of the samples are obtained at the 1 Hz to 20 MHz frequency range. The impedance value of the pellets increases with temperature. Based on the impedance results, it is found that the contribution of grain (bulk) is more than a grain boundary in terms of conductivity, which permits the attribution of a grain boundary. The ionic conductivity decreases with an increasing amount of Zn contribution. The value of highest electrical conductivity among all samples is calculated as 0.358 S cm-1 at 800°C for undoped (Bi0.92Ho0.03Er0.05)2O3.

Structural and optical properties of electron beam evaporated yttria stabilized zirconia thin films

NASA Astrophysics Data System (ADS)

Kirubaharan, A. Kamalan; Kuppusami, P.; Singh, Akash; Dharini, T.; Ramachandran, D.; Mohandas, E.

2015-06-01

Yttria stabilized zirconia (10 mole % Y2O3) thin films were deposited on quartz substrates using electron beam physical vapor deposition at the substrate temperatures in the range 300 - 973 K. XRD analysis showed cubic crystalline phase of YSZ films with preferred orientation along (111). The surface roughness was found to increase with the increase of deposition temperatures. The optical band gap of ˜5.7 eV was calculated from transmittance curves. The variation in the optical properties is correlated with the changes in the microstructural features of the films prepared as a function of substrate temperature.

Properties of cellulase as template molecule on chitosan—methyl methacrylate membrane

NASA Astrophysics Data System (ADS)

Lian, Qi; Zheng, Xuefang; Wu, Haixia; Song, Shitao; Wang, Dongjun

2015-12-01

In this study, a novel molecular imprinting membrane made of chitosan and methyl methacrylate (MMA) was fabricated with cellulase as template molecule and the thermal response to cellulase was characterized. The film was characterized by infrared spectroscopy (IR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and the permeation experiment. The results showed that the space structure of the film was as similar as the cellulase. Moreover, the membrane had advanced molecular imprinting capability to cellulase comparing to pepsin and pectinase at any temperature and the film had excellent ability to identify specific template molecule (cellulase) at the synthesis temperature compared to other temperatures.

Effect of Sn addition on glassy Si-Te bulk sample

NASA Astrophysics Data System (ADS)

Babanna, Jagannatha K.; Roy, Diptoshi; Varma, Sreevidya G.; Asokan, Sundarrajan; Das, Chandasree

2018-05-01

Bulk Si20Te79Sn1 glass is prepared by melt-quenching method, amorphous nature of the as-quenched glass is confirmed by XRD. I-V characteristics reveals that Si20Te79Sn1 bulk sample exhibits threshold type electrical switching behavior. The thermal parameters such as crystallization temperature, glass transition temperature are obtained using differential scanning calorimetry. The crystalline peak study of the sample annealed at crystallization temperature for 2 hr shows that the Sn atom interact with Si or Te but do not interact with the Si-Te matrix in a greater extent and it forms a separate phase network individually.

Role of CeO2 promoter in NiO/α-Al2O3 catalyst for dry reforming of methane

NASA Astrophysics Data System (ADS)

Loc, Luu Cam; Phuong, Phan Hong; Tri, Nguyen

2017-09-01

A series of Ni/α-Al2O3 (NiAl) catalysts promoted by CeO2 was prepared by co-impregnation methods with content of (NiO+CeO2) being in the range of 10-30 wt%. The NiO:CeO2 weight ratio was fluctuated at 1:1, 1:2 and 1:3. Several techniques, including X-ray powder diffraction (XRD), Hydrogen temperature-programmed reduction (H2-TPR), and transmission electron microscopy (TEM) were used to investigate catalysts' physico-chemical properties. The activity of these catalysts in dry reforming of CH4 was investigated at temperature range of 550-800 °C. The results revealed that the most suitable CeO2 promoted Ni catalyst contained 20 wt% of (NiO+CeO2) and NiO:CeO2 weight ratio of 1:2. The best catalytic performance of catalyst [20(1Ni2Ce)Al] due to a better reducibility resulted in a higher amount of free small particle NiO. At 700 °C and CH4:CO2 molar ratio of 1:1, the conversion of CH4 and CO2 on the most suitable CeO2 promoted Ni catalyst reached 86% and 67%, respectively; H2 and CO selectivity of 90% and H2:CO molar ratio of 1.15 were obtained. Being similar to MgO [1], promoter CeO2 could improve catalytic activity of Ni/α-Al2O3 catalyst at a lower range of temperature. Besides, both MgO and CeO2 had a great impact on improving coke resistance of Ni catalysts. At higher temperature, the role of CeO2 as well as MgO in preventing coke formation on catalyst was clarified by temperature-programmed oxidation (TPO) technique. Coke amount formed after 30-h TOS on 20(1Ni2Ce) catalyst was found to be 22.18 mgC/gcat, being less than on non-promoted catalyst (36.75 mgC/gcat), but more than on 20(1Ni2Mg)Al one (5.25 mgC/gcat).

Influence of Synthesis Temperature on the Growth and Surface Morphology of Co3O4 Nanocubes for Supercapacitor Applications

PubMed Central

Samal, Rashmirekha; Dash, Barsha; Sarangi, Chinmaya Kumar; Subbaiah, Tondepu; Senanayake, Gamini; Minakshi, Manickam

2017-01-01

A facile hydrothermal route to control the crystal growth on the synthesis of Co3O4 nanostructures with cube-like morphologies has been reported and tested its suitability for supercapacitor applications. The chemical composition and morphologies of the as-prepared Co3O4 nanoparticles were extensively characterized using X-ray diffraction (XRD) and transmission electron microscopy (TEM). Varying the temperature caused considerable changes in the morphology, the electrochemical performance increased with rising temperature, and the redox reactions become more reversible. The results showed that the Co3O4 synthesized at a higher temperature (180 °C) demonstrated a high specific capacitance of 833 F/g. This is attributed to the optimal temperature and the controlled growth of nanocubes. PMID:29088061

Magnetic study of Co-doped CdSe nanoparticles

NASA Astrophysics Data System (ADS)

Das, Sayantani; Banerjee, Sourish; Sinha, T. P.

2018-04-01

Cobalt (2 %, 5 % and 10 %) doped cadmium selenide (CdSe) nanoparticles have been synthesized by soft chemical route. The XRD pattern shows the cubic structure of the sample. Crystallization temperature of the samples is calculated using differential scanning calorimeter. The average particle size of all the samples is found to be ˜ 25 nm. Field dependent (M-H) and temperature dependent (M-T) magnetization explains the presence of ferromagnetic components in the samples at room temperature and low temperature. In order to estimate the antiferromagnetic coupling among the doped TM atoms, an M-T measurement at 500 Oe has been carried out under zero field cooled (ZFC) and field cooled (FC) conditions and Curie-Weiss temperature θ of the samples has been estimated from 1/χ vs T plots.

To study the effect of doping concentration of silver on structural and optical properties of cadmium oxide (CdO) nanostructure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Rajesh, E-mail: rkkaushik06@gmail.com; Dept. of Physics, Vaish College of Engineering, Rohtak-124001, Haryana; Sharma, Ashwani

The present work deals with study of structural and optical properties of Silver (Ag) doped Cadmium oxide (CdO) nanostructured synthesized by Chemical Co-precipitation Techniques followed by calcinations at small temperature. The doping concentrations were changing from 0.1 to 10 at% respectively. Structural analysis study of these calcined materials is carried out by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The optical properties of calcined samples were investigating by Fourier transformation infrared (FTIR)spectroscopy, UV-Visible Spectroscopy (UV-Vis). The structural properties analysis results revels that crystallite size are in the range of nano region and TEM results aremore » quite in accordance with XRD results.« less

Growth of bulk ZnO crystals by self-selecting CVT method

NASA Astrophysics Data System (ADS)

Fan, Long; Jiang, Tao; Xiao, TingTing; Chen, Jie; Peng, Liping; Wang, Xuemin; Yan, Dawei; Wu, Weidong

2018-05-01

Bulk ZnO crystals were grown by self-selecting CVT method using carbon as the transport agent. The crystal growth process took place on the top of the polycrystalline source material, and deep-red colored ZnO crystals of several millimeters were obtained. The as-grown crystals were characterized by X-ray diffraction (XRD), Energy Dispersive Spectrometer (EDS), Raman scattering (RS) spectroscopy, visible-near infrared (VIS-NIR) spectrophotometer and room temperature photoluminescence (PL) spectroscopy. XRD results indicate good crystallinity of the ZnO crystal. The EDS analysis shows that the crystal has a stoichiometry ratio Zn: O = 52: 48. The results suggest the existence of native defects of oxygen vacancies (OV) in the as-grown ZnO samples, which is caused by the stoichiometry shift to Zn-rich.

Dendritic Ag-Fe nanocrystalline alloy synthesized by pulsed electrodeposition and its characterization

NASA Astrophysics Data System (ADS)

Santhi, Kalavathy; Revathy, T. A.; Narayanan, V.; Stephen, A.

2014-10-01

Synthesis of dendrite shaped Ag-Fe alloy nanomaterial by pulsed electrodeposition route was investigated. The alloy samples were deposited at different current densities from electrolytes of different compositions to study the influence of current density and bath composition on metal contents in the alloy, which was determined by ICP-OES analysis. The XRD studies were carried out to determine the structure of these samples. Magnetic characterization at room temperature and during heating was carried out to understand their magnetic behaviour and to confirm the inferences drawn from the XRD results. The XPS spectra proved the presence of Fe and Ag in the metallic form in the alloy samples. The FESEM and TEM micrographs were taken to view the surface morphology of the nanosized particles.

Manganese oxide arrays on carbon fiber paper and its application for PEMFC

NASA Astrophysics Data System (ADS)

Lu, Lu; Zhao, Yu; Deng, Han; Xu, Bing

2018-02-01

C-MnO2 was synthesized by direct hydrothermal decomposition of KMnO4. The structure and morphology of C-MnO2 was characterized by XRD and SEM, electrochemical performances were investigated by cyclic voltammetry. The effects of hydrothermal temperatures, and time were systemat ically investigated. The XRD pattern can be identified as a α-types space group, and it matches well with Bragg reflection of the standard α-MnO2, suggesting that a targeted α-MnO2 has been successfully synthesized. The results show that pure phase MnO2 nanorods can be obtained in 160 °C. C-MnO2 composites show a larger current response and C-MnO2 composite material has improved the efficiency of the large current charge and discharge.

Phase study and surface morphology of beta-alumina

NASA Astrophysics Data System (ADS)

Tak, S. K.

2018-05-01

Beta alumina ceramic is well known as a polycrystalline ceramic material. The characteristic crystal structure of beta-alumina makes it useful as a separator in sodium sulphur batteries and other electrochemical devices requiring the passage of sodium ions. β"-alumina powders for this study were prepared by zeta process. The pellets were sintered at different microwave power levels and power schedule to optimize the sintering conditions to obtain preferred β" phase with improved microstructure. Phase identification was studied by X-ray diffraction (XRD). XRD analysis shows increase in β'' phase as the sintering temperature was increased from 1400°C to 1600°C. Surface morphology of the pellets was carried out by Scanning Electron microscopy (SEM). SEM studies revealed the formation and growth of platelet grains with interconnected porosity.

Influence of rare earth ions on microstructural and optical properties of ZnO nanostructures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Riyajuddin, Sk., E-mail: riyaj5303@gmail.com; Ahmad, Shabbir; Faizan, M.

2016-05-23

Pure and 3% rare earth ions (Nd{sup 3+} & Gd{sup 3+}) doped ZnO samples were synthesized by sol-gel method, followed by annealing at temperature 450°C for 2hr. The samples were characterized by XRD, FTIR and UV-visible spectroscopy. XRD result confirmed single phase nature of all samples with crystalline structure. The average crystallite size of the doped samples found to be decreases as caculated using Debye-Scherrer’s formula. FTIR spectra indicate absorption band centered at 464 cm{sup −1} which is attributed to Zn-O lattice vibration. It confirms the formaton of compounds. UV-visible spectroscopy was used to study the optical properties and band gapmore » of the synthesised materials using Tauc’s relation.« less

Synthesis and properties of the compound: LiNi 3/5Cu 2/5VO 4

NASA Astrophysics Data System (ADS)

Ram, Moti

2009-12-01

The LiNi 3/5Cu 2/5VO 4 is synthesized by solution-based chemical method and its formation has been checked by X-ray diffraction (XRD) study. XRD study shows a tetragonal unit cell structure with lattice parameters of a = 11.6475 (18) Å, c = 2.4855 (18) Å and c/ a = 0.2134 Å. Electrical properties are verified using complex impedance spectroscopy (CIS) technique. Complex impedance analysis reveals following points: (i) the bulk contribution to electrical properties up to 200 °C, (ii) the bulk and grain boundary contribution at T ≥ 225 °C, (iii) the presence of temperature dependent electrical relaxation phenomena in the material. D.c. conductivity study indicates that electrical conduction in the material is a thermally activated process.

Synthesis and characterization of high-quality cobalt vanadate crystals and their applications in lithium-ion batteries

NASA Astrophysics Data System (ADS)

Bhuiyan, Md. Tofajjol Hossen; Rahman, Md. Afjalur; Rahman, Md. Atikur; Sultana, Rajia; Mostafa, Md. Rakib; Tania, Asmaul Husna; Sarker, Md. Abdur Razzaque

2016-12-01

High-quality cobalt vanadate crystals have been synthesized by solid-state reaction route. Structure and morphology of the synthesized powders were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), and Fourier transform infrared (FT-IR) spectroscopy. The XRD patterns revealed that the as prepared materials are of high crystallinity and high quality. The SEM images showed that the crystalline CoV2O6 material is very uniform and well separated, with particle (of) area 252 μm. The electronic and optical properties were investigated by impedance analyzer and UV-visible spectrophotometer. Temperature-dependent electrical resistivity was measured using four-probe technique. The crystalline CoV2O6 material is a semiconductor and its activation energy is 0.05 eV.

Preparation and optical characteristics of ZnSe nanocrystals doped glass by sol gel in situ crystallization method

NASA Astrophysics Data System (ADS)

Hao, Haiyan; Yao, Xi; Wang, Minqiang

2007-01-01

Homogeneous ZnSe nanocrystals doped SiO 2 glass was successfully prepared by sol-gel in situ crystallization method. The structure of the doped ZnSe nanocrystals was studied by X-ray diffraction (XRD). ZnSe nanocrystals in silica were about 4-10 nm analysed by transmission electron microscopy (TEM), which was consistent with the results of XRD estimated using Scherrer's formular. The quantum size effect in ZnSe nanocrystals was evidenced from the blue-shifts of the optical absorption edge, and the average size of ZnSe nanocrystals was estimated by the magnitude of blue shift according to the L.E. Brus' effective mass model. The size of ZnSe nanocrystals depending on annealing time and temperature was further discussed using XRF.

Hydrocracking of Jatropha Oil over non-sulfided PTA-NiMo/ZSM-5 Catalyst

PubMed Central

Yang, Xiaosong; Liu, Jing; Fan, Kai; Rong, Long

2017-01-01

The PTA-NiMo/ZSM-5 catalyst impregnated with phosphotungstic acid (PTA) was designed for the transformation of Jatropha oil into benzene, toluene, and xylenes (BTX) aromatics. The produced catalyst was characterized by N2 adsorption-desorption, powder X-ray diffraction (XRD), Fourier transform infrared (FT-IR), X-ray photoelectron spectroscopy (XPS), and the temperature-programmed desorption of ammonia (NH3-TPD). The catalytic performance was evaluated by gas chromatography (GC). The liquid products were 70 wt% of the feed oil, and the majority of the liquid products were BTX. The aromatization activity of the catalyst was improved by the addition of PTA and the hierarchical process. The favorable PTA amount was 20 wt% and the yield of BTX was 59 wt% at 380 °C, 3 MPa, H2/oil (v/v) = 1000 and LHSV = 1 h−1 over the PTA20-NiMo/HZ0.5 catalyst (PTA 20 wt%) without sulfurization. PMID:28134313

Synthesis and characterization of iron based superconductor Nd-1111

NASA Astrophysics Data System (ADS)

Alborzi, Z.; Daadmehr, V.

2018-06-01

Polycrystalline sample of NdFeAsO0.8F0.2 was prepared by one-step solid-state reaction method. The structural and electrical properties of sample were characterized through XRD pattern and the 4-probe method. The critical temperature was obtained at 56 K. The crystal structure was tetragonal with P4/nmm:2 symmetry group.

Low-temperature growth and photoluminescence property of ZnS nanoribbons.

PubMed

Zhang, Zengxing; Wang, Jianxiong; Yuan, Huajun; Gao, Yan; Liu, Dongfang; Song, Li; Xiang, Yanjuan; Zhao, Xiaowei; Liu, Lifeng; Luo, Shudong; Dou, Xinyuan; Mou, Shicheng; Zhou, Weiya; Xie, Sishen

2005-10-06

At a low temperature of 450 degrees C, ZnS nanoribbons have been synthesized on Si and KCl substrates by a simple chemical vapor deposition (CVD) method with a two-temperature-zone furnace. Zinc and sulfur powders are used as sources in the different temperature zones. X-ray diffraction (XRD), selected area electron diffraction (SEAD), and transmission electron microscopy (TEM) analysis show that the ZnS nanoribbons are the wurtzite structure, and there are two types-single-crystal and bicrystal nanoribbons. Photoluminescence (PL) spectrum shows that the spectrum mainly includes two parts: a purple emission band centering at about 390 nm and a blue emission band centering at about 445 nm with a weak green shoulder around 510 nm.

Effect of microwave irradiation on TATB explosive (II): temperature response and other risk.

PubMed

Yu, Weifei; Zhang, Tonglai; Zuo, Jun; Huang, Yigang; Li, Gang; Han, Chao; Li, Jinshan; Huang, Hui

2010-01-15

TATB (1,3,5-triamino-2,4,6-trinitrobenzene) explosives were safely irradiated with microwave and showed no visible change according to XPS and XRD spectra. Temperature of TATB sample increased quickly at the beginning and gently during sequent continuous irradiation with temperature less than 140 degrees C after 60 min, 480 W irradiation, and increased more quickly in 300 g at 480 W than in 150 g at 480 W, both implied that heat dissipation was in the majority of microwave energy. Two major risk factors in microwave irradiation were concerned including overheating which should be avoidable with temperature monitor and microwave discharge which should be controllable experimentally though dielectric breakdown mechanism was not elucidated theoretically yet.

[A new method for the preparation of potassium ferrate and spectroscopic characterization].

PubMed

Zheng, Huai-li; Deng, Lin-li; Ji, Fang-ying; Jiang, Shao-jie; Zhang, Peng

2010-10-01

Calcium hypochlorite was used as the raw material for preparation of the high purity potassium ferrate. The study includes the effects of reaction temperature, recrystallization temperature, reaction time, Ca(ClO)2 dosage, and the amount of calcium hypochlorite on the yield. It was determined that when the reaction temperature was 25 degrees C, recrystallization temperature 0 degree C and reaction time 40 min, the yield was more than 75%. The purity was detected by direct spectrophotometric method to be more than 92%. The product was characterized by infrated spectrum(IR), X-ray diffraction (XRD) and ultraviolet spectrum (UV) methods and proved to be potassium ferrate that was prepared by calcium hypochlorite as the raw material.

Photoactive lead oxide thin films by spray pyrolysis

NASA Astrophysics Data System (ADS)

Bhagat, Dharini; Waldiya, Manmohansingh; Mukhopadhyay, Indrajit

2018-05-01

We report the synthesis of photoactive lead monoxide thin films on fluorine doped tin oxide substrate by cost effective spray pyrolysis technique using aqueous solution of lead acetate trihydrate. Influence of substrate temperature on the structural and optical properties of thin films was studied. Polymorph of lead monoxide, litharge (α-PbO), was obtained when the substrate temperature was kept constant at 360 °C. XRD analysis revealed that the deposits were tetragonal structured with preferred orientation along 002 plane. Band gap value was found to be 1.93ev from diffuse reflectance spectra.

User's Guide to Handlens - A Computer Program that Calculates the Chemistry of Minerals in Mixtures

USGS Publications Warehouse

Eberl, D.D.

2008-01-01

HandLens is a computer program, written in Excel macro language, that calculates the chemistry of minerals in mineral mixtures (for example, in rocks, soils and sediments) for related samples from inputs of quantitative mineralogy and chemistry. For best results, the related samples should contain minerals having the same chemical compositions; that is, the samples should differ only in the proportions of minerals present. This manual describes how to use the program, discusses the theory behind its operation, and presents test results of the program's accuracy. Required input for HandLens includes quantitative mineralogical data, obtained, for example, by RockJock analysis of X-ray diffraction (XRD) patterns, and quantitative chemical data, obtained, for example, by X-ray florescence (XRF) analysis of the same samples. Other quantitative data, such as sample depth, temperature, surface area, also can be entered. The minerals present in the samples are selected from a list, and the program is started. The results of the calculation include: (1) a table of linear coefficients of determination (r2's) which relate pairs of input data (for example, Si versus quartz weight percents); (2) a utility for plotting all input data, either as pairs of variables, or as sums of up to eight variables; (3) a table that presents the calculated chemical formulae for minerals in the samples; (4) a table that lists the calculated concentrations of major, minor, and trace elements in the various minerals; and (5) a table that presents chemical formulae for the minerals that have been corrected for possible systematic errors in the mineralogical and/or chemical analyses. In addition, the program contains a method for testing the assumption of constant chemistry of the minerals within a sample set.

(18)O(2) label mechanism of sulfur generation and characterization in properties over mesoporous Sm-based sorbents for hot coal gas desulfurization.

PubMed

Liu, B S; Wan, Z Y; Wang, F; Zhan, Y P; Tian, M; Cheung, A S C

2014-02-28

Using a sol-gel method, SmMeOx/MCM-41 or SBA-15 (Me=Fe, Co and Zn) and corresponding unsupported sorbents were prepared. The desulfurization performance of these sorbents was evaluated over a fixed-bed reactor and the effects of reaction temperature, feed and sorbent composition on desulfurization performance were studied. Samarium-based sorbents used to remove H2S from hot coal gas were reported for the first time. The results of successive sulfidation/regeneration cycles revealed that SmFeO3/SBA-15 sorbent was suitable for desulfurization of hot coal gas in the chemical industry. The formation of elemental sulfur during both sulfidation and regeneration processes depended strongly on the catalytic action of Sm2O2S species, which was confirmed for the first time via high sensitive time of flight mass spectrometer (TOF-MS) using 6%vol(18)O2/Ar regeneration gas and can reduce markedly procedural complexity. The sorbents were characterized using N2-adsorption, high-resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), temperature-programmed reduction of H2 (H2-TPR), thermogravimetry (TG) and time-of-flight mass spectrometry (TOF-MS) techniques. Copyright © 2014 Elsevier B.V. All rights reserved.

Promising SiC support for Pd catalyst in selective hydrogenation of acetylene to ethylene

NASA Astrophysics Data System (ADS)

Guo, Zhanglong; Liu, Yuefeng; Liu, Yan; Chu, Wei

2018-06-01

In this study, SiC supported Pd nanoparticles were found to be an efficient catalyst in acetylene selective hydrogenation reaction. The ethylene selectivity can be about 20% higher than that on Pd/TiO2 catalyst at the same acetylene conversion at 90%. Moreover, Pd/SiC catalyst showed a stable catalytic life at 65 °C with 80% ethylene selectivity. With the detailed characterization using temperature-programmed reduction (H2-TPR), powder X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), N2 adsorption/desorption analysis, CO-chemisorption and thermo-gravimetric analysis (TGA), it was found that SiC owns a lower surface area (22.9 m2/g) and a broad distribution of meso-/macro-porosity (from 5 to 65 nm), which enhanced the mass transfer during the chemical process at high reaction rate and decreased the residence time of ethylene on catalyst surface. Importantly, SiC support has the high thermal conductivity, which favored the rapid temperature homogenization through the catalyst bed and inhabited the over-hydrogenation of acetylene. The surface electronic density of Pd on Pd/SiC catalyst was higher than that on Pd/TiO2, which could promote desorption of ethylene from surface of the catalyst. TGA results confirmed a much less coke deposition on Pd/SiC catalyst.

Analysis of Chemical and Physical Properties of Biochar from Rice Husk Biomass

NASA Astrophysics Data System (ADS)

Armynah, Bidayatul; Atika; Djafar, Zuryati; Piarah, Wahyu H.; Tahir, Dahlang

2018-03-01

Chemical and physical properties of Rice Husk as a potential energy resource were analyzed by means Fourier transform infrared (FTIR), x-ray diffraction (XRD), scanning electron microscope (SEM), and energy disperse spectroscopy (EDS). Rice husk is heated with varied temperature of 250°C, 350°C, 450°C and 30, 60, 90 minutes respectively combine with time variation. The results show that the calorific value decreases whenever the temperature and time increase. The heating time of 30 minutes at 250 °C of temperature gives calorific value of 10.4 MJ/Kg. While at the 450°C of temperature, the calorific value decrease to 4.7 MJ/Kg. The EDS shows that the time of heating is an important parameter where carbon and nitrogen were decreasing with the increment of the heating time while the oxygen increase when the heating time increase. The XRD shows that the broad (002) reflections between 20° and 30° indicate carbon disordered with small domains of coherent and parallel stacking of the graphene sheets, which consists of surface morphology from SEM. FTIR shows that the O-H stretching pronounced at around 3452 cm-1 and 3412 cm-1 and pronounced clearly at the highest temperature. The aromatic group from lignin gives rise to C=C asymmetric stretching at cm-1 as a G band corresponds to the sp2-hybradization bonding of carbon atoms and C-H bending modes at 2927 at 796 cm-1. This results of the characteristic of chemical and physical properties of the rice husk examination provide the prominent source of useful energy that can eventually replace the fossil fuel.

Gallium Oxide Nanostructures for High Temperature Sensors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chintalapalle, Ramana V.

Gallium oxide (Ga 2O 3) thin films were produced by sputter deposition by varying the substrate temperature (T s) in a wide range (T s=25-800 °C). The structural characteristics and electronic properties of Ga 2O 3 films were evaluated using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectrometry (EDS), Rutherford backscattering spectrometry (RBS) and spectrophotometric measurements. The effect of growth temperature is significant on the chemistry, crystal structure and morphology of Ga 2O 3 films. XRD and SEM analyses indicate that the Ga 2O 3 films grown at lower temperatures were amorphous while those grown at T s≥500more » oC were nanocrystalline. RBS measurements indicate the well-maintained stoichiometry of Ga 2O 3 films at T s=300-800 °C. The electronic structure determination indicated that the nanocrystalline Ga 2O 3films exhibit a band gap of ~5 eV. Tungsten (W) incorporated Ga 2O 3 films were produced by co-sputter deposition. W-concentration was varied by the applied sputtering-power. No secondary phase formation was observed in W-incorporated Ga 2O 3 films. W-induced effects were significant on the structure and electronic properties of Ga2O3 films. The band gap of Ga 2O 3 films without W-incorporation was ~5 eV. Oxygen sensor characteristics evaluated using optical and electrical methods indicate a faster response in W-doped Ga 2O 3 films compared to intrinsic Ga 2O 3 films. The results demonstrate the applicability of both intrinsic and W-doped Ga-oxide films for oxygen sensor application at temperatures ≥700 °C.« less

Magnetic and dielectric properties of Ca-substituted BiFeO3 nanoferrites by the sol-gel method.

PubMed

Lin, Jinpei; Guo, Zeping; Li, Mei; Lin, Qing; Huang, Kangling; He, Yun

2018-01-01

A multiferroic material can simultaneously show two or more basic magnetic properties, including ferromagnetism, antiferromagnetism, and ferroelectricity. BiFeO 3 is a multiferroic material with a rhombohedral distorted perovskite structure. Doping can reduce the volatility of Bi and greatly improve the magnetoelectric properties of BiFeO 3 . To investigate the influence of the doping content we used the following analytical methods: X-ray powder diffraction (XRD), scanning electron microscopy (SEM), microwave network analysis (PNA-N5244A), and the Superconducting Quantum Interference Device (Quantum Design MPMS) test. With the increase of Ca 2+ concentration in the solution, the grain size of Bi 1- x Ca x FeO 3 becomes smaller, showing the role of Ca 2+ ions as the dopant for fine grains. The calcination temperatures are the major causes for the saturated magnetization. The residual magnetization ( M r ) and the coercive force ( H c ) decrease linearly with the increase of x value, and due to the effect of Ca 2+ substitution at Bi 3+ sites, which causes the valence change of Fe and/or the oxygen vacancies. The XRD result indicates that the diffraction peak emerges with the increase of Ca 2+ and the main diffraction peak achieves a high angle. The best calcining temperature is 600 °C, and the morphology is very dependent on the calcining temperature.

Controlled precipitation of nesquehonite (MgCO 3·3H 2O) by the reaction of MgCl 2 with (NH 4) 2CO 3

NASA Astrophysics Data System (ADS)

Wang, Yong; Li, Zhibao; Demopoulos, George P.

2008-03-01

In this study, homogeneous (unseeded) precipitation of nesquehonite (MgCO 3·3H 2O) by the reaction of MgCl 2 with (NH 4) 2CO 3 in supersaturated solutions was investigated. Factors that influence the precipitation of MgCO 3·3H 2O, such as reaction temperature, initial concentration, stirring speed, titration speed, equilibration time, have been studied. SEM images and particle size distribution show that the temperature, initial concentration and titration speed have significant effect on nesquehonite's crystal morphology and particle size. In addition, stirring speed and equilibration time also have some influence on its properties. X-ray powder diffraction (XRD) results show that the obtained crystals compositions are greatly affected by the reaction temperature. With the morphological transformation, their corresponding composition also change from MgCO 3· xH 2O to Mg 5(CO 3) 4(OH) 2·4H 2O in the interval of 288-333 K. With the optimization of operating conditions, the crystals can grow up to a length of about 40 μm and a width of 5 μm, indicating good filtration properties. High-purity nesquehonite obtained in this study was calcined to produce highly pure MgO at 1073 K as shown by XRD results.

Structural, electrical, and optical properties of antimony-doped tin oxide films prepared at room temperature by radio frequency magnetron sputtering for transparent electrodes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lee, Sung Uk; Hong, Byungyou; Choi, Won Seok

2009-07-15

Antimony-doped tin oxide (ATO) films were prepared on 7059 Corning glass substrate by the radio frequency (rf) magnetron sputtering method using SnO{sub 2} target mixed with Sb of 6 wt % at room temperature. The working pressure was varied from 0.67 to 2 Pa in steps of 0.67 Pa, and the rf power was varied from 100 to 175 W in steps of 25 W at room temperature. The thickness of the deposited ATO films was about 150 nm. X-ray diffraction (XRD) measurements showed the ATO films to be crystallized with a strong (101) preferred orientation as the rf powermore » is increased. The spectra revealed that the deposited films were polycrystalline, retaining the tetragonal structure. The grain size was estimated from the XRD spectra using the Scherrer equation and found to decrease with a decrease in the working pressure and an increase in the rf power, while the surface roughness was observed to be smoothened. The ATO film that was deposited at a working pressure of 0.67 Pa with rf power of 175 W showed the lowest resistivity of 8.6x10{sup -3} {Omega} cm, and the optical transmittance was 86.5% in the visible wavelength range from 400 to 800 nm.« less

Electrical conductivity, differential scanning calorimetry, X-ray diffraction, and 7Li nuclear magnetic resonance studies of n-C x H(2 x+1)OSO3Li ( x = 12, 14, 16, 18, and 20)

NASA Astrophysics Data System (ADS)

Hirakawa, Satoru; Morimoto, Yoshiaki; Honda, Hisashi

2015-04-01

Electrical conductivity ( σ), differential scanning calorimetry (DSC), and X-ray diffraction (XRD) measurements of n-C x H (2 x+1) OSO 3Li ( x= 12, 14, 16, 18, and 20) crystals were performed as a function of temperature. In addition, σ, DSC, and XRD observations of n-C x H (2 x+1) OSO 3Na and n-C x H (2 x+1) OSO 3K ( x= 12, 14, 16, 18, and 20) crystals were carried out for comparison. DSC results of the salts revealed several solid-solid phase transitions with large entropy changes (Δ S). For n-C 18 H 37 OSO 3Li and n-C 20 H 41 OSO 3Li salts, each melting point produced a small Δ S mp value compared with the total entropy change in the solid phases (Δ S tr1+Δ S tr2). Additionally, Li + ion diffusion was detected in the highest temperature solid phases. For K salts, larger σ values were detected for potassium alkylsulfates compared with those reported for alkyl carboxylate. 7Li NMR spectra of n-C 18 H 37 OSO 3Li crystals recorded in the low-temperature phase showed large asymmetry parameters, suggesting the Li + ions are localized at asymmetric sites in the crystals.

Growth of CH3NH3PbI3 Perovskite on Stainless Steel Substrate Layered by ZnO Nanoparticles Using One-Step Spin Coating Route

NASA Astrophysics Data System (ADS)

Fuad, A.; Fibriyanti, A. A.; Mufti, N.; Taufiq, A.; Maryam, S.; Hidayat, N.

2018-04-01

In this work, we report the preparation of CH3NH3PbI3 perovskite using one-step spin coating route for solar cell application. CH3NH3I• PbI2•DMF•DMSO complexes were coated on stainless steel as a subtrate layered by ZnO nanoparticles as an electron transport layer. To obtain samples with a special performance, we annealed the samples at a temperature of 100, 120, and 140°C for 10 minutes. The samples were then characterized by means of XRD, SEM/EDX, and Spectroscopic Ellipsometry. The analysis of XRD data presented that the CH3NH3PbI3 perovskites were successfully prepared and crystallized in tetragonal structure confirming from crystalline planes (110) and (220). Meanwhile, the particle size of the samples prepared at a temperature of 100, 120, and 140°C presented 42.96, 54.73, and 55.19 nm, respectively with coincide with the SEM images. The results indicated that the increase in temperature during synthesis influenced the particle growth. Furthermore, the characterization using Spectroscopic Ellipsometry exhibited that the CH3NH3PbI3 successfully layered on the substrate sizing nano metric scale that open high opportunity to be applied to solar cells with high performance.

Hierarchical Self-Organization of Perylene Bisimides into Supramolecular Spheres and Periodic Arrays Thereof.

PubMed

Sahoo, Dipankar; Peterca, Mihai; Aqad, Emad; Partridge, Benjamin E; Heiney, Paul A; Graf, Robert; Spiess, Hans W; Zeng, Xiangbing; Percec, Virgil

2016-11-09

Perylene bisimide derivatives (PBIs) are known to form only columnar or lamellar assemblies. There is no known example of a PBI self-assembling into a supramolecular sphere. Therefore, periodic and quasiperiodic arrays generated from spherical assemblies produced from PBIs are also not known. Here, a PBI functionalized at its imide groups with a second generation self-assembling dendron is reported to self-assemble into supramolecular spheres. These spheres self-organize in a body-centered cubic (BCC) periodic array, rarely encountered for self-assembling dendrons but often encountered in block copolymers. These supramolecular spheres also assemble into a columnar hexagonal array in which the supramolecular columns are unexpectedly and unprecedentedly made from spheres. At lower temperature, two additional columnar hexagonal phases consisting of symmetric and asymmetric tetrameric crowns of PBI are observed. Structural and retrostructural analysis via X-ray diffraction (XRD), molecular modeling, molecular simulation, and solid state NMR suggests that inversion of the symmetric tetrameric crowns at high temperature mediates their transformation into supramolecular spheres. The tetrameric crowns of PBIs are able to form an isotropic sphere in the cubic phase due to rapid molecular motion at high temperature, unobservable by XRD but demonstrated by solid state NMR studies. This mechanism of hierarchical self-organization of PBI into supramolecular spheres is most probably general and can be applied to other related planar molecules to generate new functions.

Characterisation of silica derived from rice husk (Muar, Johor, Malaysia) decomposition at different temperatures

NASA Astrophysics Data System (ADS)

Azmi, M. A.; Ismail, N. A. A.; Rizamarhaiza, M.; W. M. Hasif. A. A., K.; Taib, H.

2016-07-01

Rice husk was thermally decomposed to yield powder composed of silica (SiO2). Temperatures of 700°C and 1000°C were chosen as the decomposition temperatures. X-Ray Diffraction (XRD), X-Ray Florescence (XRF), Fourier Transform Infrared (FTIR), and Field Emission Scanning Electron Microscope (FESEM) analyses were conducted on a synthetic silica powder (SS-SiO2) and the rice husk ash as for the comparative characterisation study. XRD analyses clearly indicated that the decomposed rice husk yielded silica of different nature which are Crystalline Rice Husk Silica (C-RHSiO2) and Amorphous Rice Husk Silica (A-RHSiO2). Moreover, it was found that SS-SiO2 was of Quartz phase, C-RHSiO2 was of Trydimite and Cristobalite. Through XRF detection, the highest SiO2 purity was detected in SS-SiO2 followed by C-RHSiO2 and A-RHSiO2 with purity percentages of 99.60%, 82.30% and 86.30% respectively. FTIR results clearly indicated silica (SiO2) bonding 1056, 1064, 1047, 777, 790 and 798 cm-1) increased as the crystallinity silica increased. The Cristobalite phase was detected in C-RH SiO2 at the wavelength of 620 cm-1. Morphological features as observed by FESEM analyses confirmed that, SS-SiO2 and C-RH SiO2 showed prominent coarse granular morphology.

Water Structure and Dynamics in Smectites: X-ray Diffraction and 2 H NMR Spectroscopy of Mg–, Ca–, Sr–, Na–, Cs–, and Pb–Hectorite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reddy, U. Venkateswara; Bowers, Geoffrey M.; Loganathan, Narasimhan

2016-04-06

Variable-temperature X-ray diffraction and 2H NMR spectroscopy of the smectite mineral, hectorite, containing interlayer Na +, K +, Cs +, Mg 2+, Ca 2+, Sr 2+, and Pb 2+ equilibrated at 43% relative humidity (RH) and mixed with 2H 2O to form a paste provide a comprehensive picture of the structural environments and dynamics of interlayer 2H 2O and the relationships of these properties to interlayer hydration state, the hydration energy and polarizability of the cation, temperature, and the formation of ice-1h in the interparticle pores. The variation in basal spacing shown by the XRD data correlates well with themore » 2H NMR behavior, and the XRD data show for the first time in hectorites that crystallization of interparticle ice-1h causes a decrease in the interlayer spacing, likely due to removal of interlayer 2H 2O. The variation of the 2H NMR behavior of all the samples with decreasing temperature reflects decreasing frequencies of motion for the rotation of the 2H 2O molecules around their dipoles, reorientation of the 2H 2O molecules, and exchange of the 2H 2O molecules between interlayer sites coordinated to and not coordinated to the cations.« less

Local configurations and atomic intermixing in as-quenched and annealed Fe1-xCrx and Fe1-xMox ribbons

NASA Astrophysics Data System (ADS)

Stanciu, A. E.; Greculeasa, S. G.; Bartha, C.; Schinteie, G.; Palade, P.; Kuncser, A.; Leca, A.; Filoti, G.; Birsan, A.; Crisan, O.; Kuncser, V.

2018-04-01

Local atomic configuration, phase composition and atomic intermixing in Fe-rich Fe1-xCrx and Fe1-xMox ribbons (x = 0.05, 0.10, 0.15), of potential interest for high-temperature applications and nuclear devices, are investigated in this study in relation to specific processing and annealing routes. The Fe-based thin ribbons have been prepared by induction melting, followed by melt spinning and further annealed in He at temperatures up to 1250 °C. The complex structural, compositional and atomic configuration characterisation has been performed by means of X-ray diffraction (XRD), transmission Mössbauer spectroscopy and differential scanning calorimetry (TG-DSC). The XRD analysis indicates the formation of the desired solid solutions with body-centred cubic (bcc) structure in the as-quenched state. The Mössbauer spectroscopy results have been analysed in terms of the two-shell model. The distribution of Cr/Mo atoms in the first two coordination spheres is not homogeneous, especially after annealing, as supported by the short-range order parameters. In addition, high-temperature annealing treatments give rise to oxidation of Fe (to haematite, maghemite and magnetite) at the surface of the ribbons. Fe1-xCrx alloys are structurally more stable than the Mo counterpart under annealing at 700 °C. Annealing at 1250 °C in He enhances drastically the Cr clustering around Fe nuclei.

Enhanced room temperature ferromagnetism in Cr-doped ZnO nanoparticles prepared by auto-combustion method

NASA Astrophysics Data System (ADS)

Haq, Khizar-ul; Irfan, M.; Masood, Muhammad; Saleem, Murtaza; Iqbal, Tahir; Ahmad, Ishaq; Khan, M. A.; Zaffar, M.; Irfan, Muhammad

2018-04-01

Zn1‑x Cr x O (x = 0.00, 0.01, 0.03, 0.05, 0.07, and 0.09) nanoparticles were synthesized, by an auto-combustion method. Structural, optical, and magnetic characteristics of Cr-doped ZnO samples calcined at 600 °C have been analyzed by using X-ray diffraction (XRD), field emission scanning electron microscope (FESEM), UV–Vis spectroscopy and vibrating sample magnetometer (VSM). The XRD data confirmed the hexagonal wurtzite structure of pure and Cr-doped ZnO nanoparticles. The calculated values of grain size using Scherrer's formula are in the range of 30.7–9.2 nm. The morphology of nanopowders has been observed by FESEM, and EDS results confirmed a systematic increase of Cr content in the samples and clearly indicate with no impurity element. The band gaps, computed by UV–Vis spectroscopy, are in the range of 2.83–2.35 eV for different doping concentrations. By analyzing VSM data, significantly enhanced room temperature ferromagnetism is identified in Cr-doped ZnO samples. The value of magnetization is a 12 times increased of the value reported by Daunet al. (2010). Room temperature ferromagnetism of the nanoparticles is of vital prominence for spintronics applications. Project supported by the Office of Research, Innovation, and Commercialization (ORIC), MUST Mirpur (AJK).

Experiment Investigation of the Influencing Factors on Bed Agglomeration During Fluidized-Bed Gasification of Biomass Fuels

NASA Astrophysics Data System (ADS)

Chen, Y. Q.; Chen, H. P.; Yang, H. P.; Wang, X. H.; Zhang, S. H.

With the depleting of fossil fuel and environmental polluting increasing, the utilization of biomass resources caught increasing concern. Biomass gasification in fluidized bed, as one promising technology, developed quickly. However, serious agglomeration was displayed as biomass ash reacted with bed material (silica sand) at higher temperature. It hindered the wide utilization of CFB gasifier. The objective ofthis work is to investigate the agglomeration behavior between biomass ash and silica sand, and catch the inherent mechanism. Firstly, the influence of ash compounds on the agglomeration behavior was analyzed with biomass ash and synthesis ash compounds addition in fixed bed as ash sample mixed with bed material evenly before every trial. The reaction temperature was set 850°C that is the operated temperature for many fluidized bed gasificated biomass fuels. Then the influence of reaction time was analyzed. The characteristics of the agglomerated silica sand particles were analyzed by the XRD. Finally, it was simulated with HSC computer mode based on thermodynamic equilibrium. It was observed that when the ratio of the biomass ash to the silica sand was above 0.2, the agglomeration was observed. With the increase of the reaction time, more silica sand particles agglomerated with the biomass ash. There are two kinds of silicate eutecticum investigated by the XRD. It is of great significance for the running ofCFB biomass gasifier and the development ofbiomass utilization technology.

Structure refinement of Ba{sub 0.5}Sr{sub 0.5}Co{sub 0.8}Fe{sub 0.2}O{sub 3-d} as cathode materials for intermediate temperature solid oxide fuel cells (IT-SOFC)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zakaria, Nurhamidah, E-mail: nurhamidahzakaria@yahoo.com; Idris, Mohd Sobri, E-mail: sobri@unimap.edu.my; Osman, Rozana A. M., E-mail: rozana@unimap.edu.my

2016-07-19

Ba{sub 0.5}Sr{sub 0.5}Co{sub 0.8}Fe{sub 0.2}O{sub 3-δ} was successfully prepared using modified solid-state synthesis routes. The lowest temperature to obtained single phase of Ba{sub 0.5}Sr{sub 0.5}Co{sub 0.8}Fe{sub 0.2}O{sub 3-δ} is about 900°C for 15 hours. Longer period of time are required compared to only 5 hours at 950°C as established in literatures. The X-ray Diffraction (XRD) data confirmed that Ba{sub 0.5}Sr{sub 0.5}Co{sub 0.8}Fe{sub 0.2}O{sub 3-δ} is formed a cubic perovskite with the space group of Pm-3m. The lattice parameters of Ba{sub 0.5}Sr{sub 0.5}Co{sub 0.8}Fe{sub 0.2}O{sub 3-δ} are a = 3.990 (1) Å and unit cell volume is V = 63.5 (1)more » Å{sup 3}. The Rietveld refinement of XRD data revealed that the crystal structure of Ba{sub 0.5}Sr{sub 0.5}Co{sub 0.8}Fe{sub 0.2}O{sub 3-δ} slightly changes as a function of temperature.« less

Effect of Synthesis Parameter on Crystal Structures and Magnetic Properties of Magnesium Nickel Ferrite (Mg0.5Ni0.5Fe2O4) Nanoparticles

NASA Astrophysics Data System (ADS)

Maulia, R.; Putra, R. A.; Suharyadi, E.

2017-05-01

Mg0.5Ni0.5Fe2O4 nanoparticles have been successfully synthesized by using co-precipitation method and varying the synthesis parameter, i.e. synthesis temperature and NaOH concentration. X-ray Diffraction (XRD) pattern showed that nanoparticles have cubic spinel structures with an additional phase of γ-Fe2O3 and particle size varies within the range of 4.3 - 6.7 nm. This variation is due to the effect of various synthesis parameters. Transmission Electron Microscopy (TEM) image showed that the nanoparticles exhibited agglomeration. The observed diffraction ring from selected area electron diffraction showed that the sample was polycrystalline and confirmed the peak appearing in XRD. The coercivities showed an increasing trend with an increase in particle size from 44.7 Oe to 49.6 Oe for variation of NaOH concentration, and a decreasing trend with an increase in particle size from 46.8 to 45.1 Oe for variation of synthesis temperature. The maximum magnetization showed an increasing trend with an increase in the ferrite phase from 3.7 emu/g to 5.4 emu/g possessed in the sample with variations on NaOH concentration. The maximum magnetization for the sample with variations on synthesis temperature varied from 4.4 emu/g to 5.7 emu/g due to its crystal structures.

Performance of RF sputtered p-Si/n-ZnO nanoparticle thin film heterojunction diodes in high temperature environment

NASA Astrophysics Data System (ADS)

Singh, Satyendra Kumar; Hazra, Purnima

2017-04-01

In this article, temperature-dependent current-voltage characteristics of n-ZnO/p-Si nanoparticle thin film heterojunction diode grown by RF sputtering technique are analyzed in the temperature range of 300-433 k to investigate the performance of the device in high temperature environment. The microstructural, morphological, optical and temptrature dependent electrical properties of as-grown nanoparticle thin film were characterized by X-ray diffractometer (XRD), atomic force microscopy (AFM), field emmision scanning electron microscopy (FESEM), energy-dispersive X-ray spectroscopy (EDX), variable angle ellipsometer and semiconductor device analyzer. XRD spectra of as-grown ZnO films are exhibited that highly c-axis oriented ZnO nanostructures are grown on p- Si〈100〉 substrate whereas AFM and FESEM images confirm the homogeneous deposition of ZnO nanoparticles on surface of Si substratewith minimum roughness.The optical propertiesof as-grown ZnO nanoparticles have been measured in the spectral range of 300-800 nm using variable angle ellipsometer.To measure electrical parameters of the device prototype in the temperature range of room temperature (300 K) to 433 K, large area ohmic contacts were fabricated on both side of the ZnO/Si heterostructure. From the current-voltage charcteristics of ZnO/Si heterojunction device, it is observed that the device exhibits rectifing nature at room temperature. However, with increase in temperature, reverse saturation current and barrier height are found to increase, whereas ideality factor is started decreasing. This phenomenon confirms that barrier inhomogeneities are present at the interface of ZnO/Si heterojunction, as a result of lattice constant and thermal coefficient mismatch between Si and ZnO. Therefore, a modified value of Richardson constant [33.06 Acm-2K-2] has been extracted from the temperature-dependent electrical characteristics after assuming the Gaussian distribution of special barrier height inhomogeneities across the Si/ZnO interface which is close to its theoretical value [32 Acm-2K-2]. This result indicates that regardless of presence of barrier height inmogeneities, ZnO/Si heterojunction diode still hasability to perform well in high temperature environment.

Synthesis and characterization of nanocrystalline mordenite, high silica zeolite RHO, and copper faujasite

NASA Astrophysics Data System (ADS)

Hincapie Palacio, Beatriz Omaira

Mordenite is a zeolite that has been used as a selective adsorbent and as a catalyst. In reactions where the diffusion of reagents into the pore system is the rate-determining step, nanoparticles of the catalyst improve the reaction rate. Mordenite with a crystal diameter smaller than 100 nm has been prepared by the modification of different synthetic parameters such as the source of aluminum, the presence of seeds, the use of low temperatures (150°C vs. 170°C), longer crystallization times (24 h vs. 96 h), and different silica to alumina ratios (10--30). The decrease in the crystal diameter of the prepared mordenite was monitored by the application of the Scherrer equation that relates the broadness of the X-ray diffraction peaks to crystal sizes. Zeolite RHO with an initial silica to alumina ratio (SAR) higher than 20 has been prepared. EDTA, citric acid, and tartaric acid have been used as complexing agents in the synthesis of zeolite RHO. Crystallization time increases (from 48 h to 900 h) with increasing the silica to alumina ratios (SAR) of the initial gel (SAR: 10.8 to 30) and by adding complexing agents. Complexing agents favor the formation of small crystals (0.8 mum) with increased silica to alumina ratio (final SAR: 4.5 vs. 4.0 without complexing agents). The products were characterized by XRD, FESEM, EDX, FTIR, and in-situ XRD. Copper containing faujasite has been successfully prepared for the first time using a direct synthesis method. Ammonium hydroxide was used to form a copper complex that was later mixed with the reacting gel. Crystallization took place at 85°C for 11 days. The copper containing faujasite obtained was characterized by XRD, FESEM, EDX, EPR, FTIR, TPR, and BET. According to the XRD pattern only FAU type zeolite was obtained. According to TPR experiments, the reduction temperature for Cu2+ ions present in Cu-FAU prepared by direct synthesis was 70 K higher than for Cu-FAU prepared by ion-exchange. This difference can be due to the different location of the copper ions in the supercages or in the sodalite cages of the faujasite.

Development of Ternary and Quaternary Catalysts for the Electrooxidation of Glycerol

PubMed Central

Artem, L. M.; Santos, D. M.; De Andrade, A. R.; Kokoh, K. B.; Ribeiro, J.

2012-01-01

This work consisted in the preparation of platinum-based catalysts supported on carbon (Vulcan XC-72) and investigation of their physicochemical and electrochemical properties. Catalysts of the C/Pt-Ni-Sn-Me (Me = Ru or Ir) type were prepared by the Pechini method at temperature of 350°C. Four different compositions were homemade: C/Pt60Sn10Ni30, C/Pt60Sn10Ni20Ru10, C/Pt60Sn10Ni10Ru20, and C/Pt60Sn10Ni10Ir20. These catalysts were electrochemically and physically characterized by cyclic voltammetry (CV), chronoamperometry (CA) in the presence of glycerol 1.0 mol dm−3, X-ray diffraction (XRD), and high-resolution transmission electron microscopy (HRTEM). XRD results showed the main peaks of face-centered cubic Pt. The particle sizes obtained from XRD and HRTEM experiments were close to values ranging from 3 to 8.5 nm. The CV results indicate behavior typical of Pt-based catalysts in acid medium. The CV and CA data reveal that quaternary catalysts present the highest current density for the electrooxidation of glycerol. PMID:22623905

CoO doping effects on the ZnO films through EBPDV technique

NASA Astrophysics Data System (ADS)

Inês Basso Bernardi, Maria; Queiroz Maia, Lauro June; Antonelli, Eduardo; Mesquita, Alexandre; Li, Maximo Siu; Gama, Lucianna

2014-03-01

Nanometric Zn1-xCo xO (x = 0.020, 0.025 and 0.030 in mol.%) nanopowders were obtained from low temperature calcination of a resin prepared using the Pechini's method. Firing the Zn1-xCoxO resin at 400 °C/2 h a powder with hexagonal structure was obtained as measured by X-ray diffraction (XRD). The powder presented average particle size of 40 nm observed by field emission scanning electronic microscopy (FE-SEM) micrographs and average crystallite size of 10 nm calculated from the XRD using Scherrer's equation. Nanocrystalline Zn1-xCo xO films with good homogeneity and optical quality were obtained with 280-980 nm thicknesses by electron beam physical vapour deposition (EBPVD) under vacuum onto silica substrate at 25 °C. Scanning electron microscopy with field emission gun showed that the film microstructure is composed by spherical grains and some needles. In these conditions of deposition the films presented only hexagonal phase observed by XRD. The UV-visible-NIR and diffuse reflectance properties of the films were measured and the electric properties were calculated using the reflectance and transmittance spectra.

Preparation and physical properties of polycrystalline (Bi1-xPbx)2Sr2Ca2Cu3Oy high T c superconductors

NASA Astrophysics Data System (ADS)

Awan, M. S.; Maqsood, M.; Mirza, S. A.; Yousaf, M.; Maqsood, A.

1995-02-01

(Bi1-xPbx:)2Sr2Ca2Cu3Oy ( x = 0.3) high critical transition temperature ( T c) superconductors are synthesized by the solid-state reaction method in polycrystalline form. X-ray diffraction (XRD) studies, direct current (dc) electrical resistivity measurements, scanning electron microscopic (SEM) studies, critical current density measurements, and zero-field alternating current (ac) susceptibility measurements are performed to investigate the physical changes, structural changes, and magnetic behavior of the superconducting samples. X-ray diffraction studies show that a high T c phase exists with orthorhombic symmetry in the specimen. According to the XRD data, the lattice parameters of the high T c phase were determined as a = 0.537(1) nm, b = 0.539(1) nm, and c = 3.70(1) nm. The compound exhibits a superconducting transition at 106 ±1 K for zero resistance. The ac susceptibility measurements in zero field confirm the dc electrical resistivity results; hence both support the XRD results. The particle size and structural changes as a function of the cold-pressing and aging effect are also reported.

Synthesis Structural and Optical Properties Of (Co, Al) co-doped ZnO Nano Particles

NASA Astrophysics Data System (ADS)

Swapna, P.; Venkatramana Reddy, S.

2018-02-01

We prepared (Co, Al) co-doped ZnO nanostructures using the method chemical co-precipitation successfully, at room temperature using PEG (Poly ethylene glycol) as stabilizing agent. Samples are prepared with different concentrations by keeping aluminium at 5 mol percent constant and varying the concentration of cobalt from 1 to 5 mol percent. After the preparation all the samples are carefully subjected to characterizations such as XRD, SEM with EDS, TEM, PL and UV-VIS-NIR. XRD pattern shows that all the samples possess hexagonal wurtzite crystal structure having no secondary phases pertaining to Al or cobalt, which shows successful dissolution of the dopents. TEM results shows the accurate size of particles and is confirmed the XRD data. SEM images of all the samples shows that particles are in nearly spherical shape, EDS spectrum reveals that incorporation of cobalt and aluminum in host lattice. PL spectrum shows that all the samples containing two prominent peaks centered at 420 nm and 446 nm. UV-VIS-NIR spectra has shown three absorptions peaks in the range of wavelength 550 nm to 700 nm, which are ascribed as typical d-d transitions of cobalt ions.