CO Oxidation and Subsequent CO 2 Chemisorption on Alkaline Zirconates: Li 2 ZrO 3 and Na 2 ZrO 3

DOE PAGES

Alcántar-Vázquez, Brenda; Duan, Yuhua; Pfeiffer, Heriberto

2016-08-26

Here, two different alkaline zirconates (Li 2ZrO 3 and Na 2ZrO 3) were studied as possible bifunctional catalytic-captor materials for CO oxidation and the subsequent CO 2 chemisorption process. Initially, CO oxidation reactions were analyzed in a catalytic reactor coupled to a gas chromatograph, using Li 2ZrO 3 and Na 2ZrO 3, under different O 2 partial flows. We found results clearly showed that Na 2ZrO 3 possesses much better catalytic properties than Li 2ZrO 3. After the CO-O 2 oxidation catalytic analysis, CO2 chemisorption process was analyzed by thermogravimetric analysis, only for the Na 2ZrO 3 ceramic. The resultsmore » confirmed that Na 2ZrO 3 is able to work as a bifunctional material (CO oxidation and subsequent CO 2 chemisorption), although the kinetic CO 2 capture process was not the best one under the physicochemical condition used in this case. For Na 2ZrO 3, the best CO conversions were found between 445 and 580 °C (100%), while Li 2ZrO 3 only showed a 35% of efficiency between 460 and 503 °C. However, in the Na 2ZrO 3 case, at temperatures higher than 580 °C its catalytic activity gradually decreases as a result of CO 2 capture process. Finally, all these experiments were compared and supported with theoretical thermodynamic data.« less

Miscibility of amorphous ZrO2-Al2O3 binary alloy

NASA Astrophysics Data System (ADS)

Zhao, C.; Richard, O.; Bender, H.; Caymax, M.; De Gendt, S.; Heyns, M.; Young, E.; Roebben, G.; Van Der Biest, O.; Haukka, S.

2002-04-01

Miscibility is a key factor for maintaining the homogeneity of the amorphous structure in a ZrO2-Al2O3 binary alloy high-k dielectric layer. In the present work, a ZrO2/Al2O3 laminate thin layer has been prepared by atomic layer chemical vapor deposition on a Si (100) wafer. This layer, with artificially induced inhomogeneity (lamination), enables one to study the change in homogeneity of the amorphous phase in the ZrO2/Al2O3 system during annealing. High temperature grazing incidence x-ray diffraction (HT-XRD) was used to investigate the change in intensity of the constructive interference peak of the x-ray beams which are reflected from the interfaces of ZrO2/Al2O3 laminae. The HT-XRD spectra show that the intensity of the peak decreases with an increase in the anneal temperature, and at 800 °C, the peak disappears. The same samples were annealed by a rapid thermal process (RTP) at temperatures between 700 and 1000 °C for 60 s. Room temperature XRD of the RTP annealed samples shows a similar decrease in peak intensity. Transmission electronic microscope images confirm that the laminate structure is destroyed by RTP anneals and, just below the crystallization onset temperature, a homogeneous amorphous ZrAlxOy phase forms. The results demonstrate that the two artificially separated phases, ZrO2 and Al2O3 laminae, tend to mix into a homogeneous amorphous phase before crystallization. This observation indicates that the thermal stability of ZrO2-Al2O3 amorphous phase is suitable for high-k applications.

Methane Decomposition and Carbon Growth on Y2O3, Yttria-Stabilized Zirconia, and ZrO2

PubMed Central

2014-01-01

Carbon deposition following thermal methane decomposition under dry and steam reforming conditions has been studied on yttria-stabilized zirconia (YSZ), Y2O3, and ZrO2 by a range of different chemical, structural, and spectroscopic characterization techniques, including aberration-corrected electron microscopy, Raman spectroscopy, electric impedance spectroscopy, and volumetric adsorption techniques. Concordantly, all experimental techniques reveal the formation of a conducting layer of disordered nanocrystalline graphite covering the individual grains of the respective pure oxides after treatment in dry methane at temperatures T ≥ 1000 K. In addition, treatment under moist methane conditions causes additional formation of carbon-nanotube-like architectures by partial detachment of the graphite layers. All experiments show that during carbon growth, no substantial reduction of any of the oxides takes place. Our results, therefore, indicate that these pure oxides can act as efficient nonmetallic substrates for methane-induced growth of different carbon species with potentially important implications regarding their use in solid oxide fuel cells. Moreover, by comparing the three oxides, we could elucidate differences in the methane reactivities of the respective SOFC-relevant purely oxidic surfaces under typical SOFC operation conditions without the presence of metallic constituents. PMID:24587591

Characterization of ZrO2 buffer layers for sequentially evaporated Y-Ba-CuO on Si and Al2O3 substrates

NASA Technical Reports Server (NTRS)

Valco, George J.; Rohrer, Norman J.; Pouch, John J.; Warner, Joseph D.; Bhasin, Kul B.

1988-01-01

Thin film high temperature superconductors have the potential to change the microwave technology for space communications systems. For such applications it is desirable that the films be formed on substrates such as Al2O3 which have good microwave properties. The use of ZrO2 buffer layers between Y-Ba-Cu-O and the substrate has been investigated. These superconducting films have been formed by multilayer sequential electron beam evaporation of Cu, BaF2 and Y with subsequent annealing. The three layer sequence of Y/BaF2/Cu is repeated four times for a total of twelve layers. Such a multilayer film, approximately 1 micron thick, deposited directly on SrTiO3 and annealed at 900 C for 45 min produces a film with a superconducting onset of 93 K and critical temperature of 85 K. Auger electron spectroscopy in conjunction with argon ion sputtering was used to obtain the distribution of each element as a function of depth for an unannealed film, the annealed film on SrTiO3 and annealed films on ZrO2 buffer layers. The individual layers were apparent. After annealing, the bulk of the film on SrTiO3 is observed to be fairly uniform while films on the substrates with buffer layers are less uniform. The Y-Ba-Cu-O/ZrO2 interface is broad with a long Ba tail into the ZrO2, suggesting interaction between the film and the buffer layer. The underlying ZrO2/Si interface is sharper. The detailed Auger results are presented and compared with samples annealed at different temperatures and durations.

Hydrothermal-precipitation preparation of CdS@(Er3+:Y3Al5O12/ZrO2) coated composite and sonocatalytic degradation of caffeine.

PubMed

Huang, Yingying; Wang, Guowei; Zhang, Hongbo; Li, Guanshu; Fang, Dawei; Wang, Jun; Song, Youtao

2017-07-01

Here, we reported a novel method to dispose caffeine by means of ultrasound irradiation combinated with CdS@(Er 3+ :Y 3 Al 5 O 12 /ZrO 2 ) coated composite as sonocatalyst. The CdS@(Er 3+ :Y 3 Al 5 O 12 /ZrO 2 ) was synthesized via hydrothermal-precipitation method and then characterized by X-ray diffractometer (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray analysis (EDX) and UV-vis diffuse reflectance spectra (DRS). After that, the sonocatalytic degradation of caffeine in aqueous solution was conducted adopting CdS@(Er 3+ :Y 3 Al 5 O 12 /ZrO 2 ) and CdS@ZrO 2 coated composites as sonocatalysts. In addition, some influencing factors such as CdS and ZrO 2 molar proportion, caffeine concentration, ultrasonic irradiation time, sonocatalyst dosage and addition of several inorganic oxidants on sonocatalytic degradation of caffeine were investigated by using UV-vis spectra and gas chromatograph. The experimental results showed that the presence of Er 3+ :Y 3 Al 5 O 12 could effectively improve the sonocatalytic degradation activity of CdS@ZrO 2 . To a certain extent some inorganic oxidants can also enhance sonocatalytic degradation of caffeine in the presence of CdS@(Er 3+ :Y 3 Al 5 O 12 /ZrO 2 ). The best sonocatalytic degradation ratio (94.00%) of caffeine could be obtained when the conditions of 5.00mg/L caffeine, 1.00g/L prepared CdS@(Er 3+ :Y 3 Al 5 O 12 /ZrO 2 ), 10.00mmol/LK 2 S 2 O 8 , 180min ultrasonic irradiation (40kHz frequency and 50W output power), 100mL total volume and 25-28°C temperature were adopted. It seems that the method of sonocatalytic degradation caused by CdS@(Er 3+ :Y 3 Al 5 O 12 /ZrO 2 ) displayspotentialadvantages in disposing caffeine. Copyright © 2017 Elsevier B.V. All rights reserved.

Tensile Strength and Microstructure of Al2O3-ZrO2 Hypo-Eutectic Fibers Studied

NASA Technical Reports Server (NTRS)

Farmer, Serene C.; Sayir, Ali

2001-01-01

Oxide eutectics offer high-temperature strength retention and creep resistance in oxidizing environments. Al2O3-ZrO2 eutectic strengths have been studied since the 1970's. Directionally solidified oxide eutectics exhibit improved resistance to slow crack growth and excellent strength retention at high temperatures up to 1400 C. Materials studied typically contain Y2O3 to metastably retain the high-temperature cubic and tetragonal polymorphs at room temperature. Al2O3-ZrO2 is of fundamental interest for creep studies because it combines a creep-resistant material, Al2O3, with a very low creep resistance material, ZrO2. Results on mechanical properties and microstructures of these materials will be used to define compositions for creep testing in future work. Substantial variations from the eutectic alumina to zirconia ratio can be tolerated without a loss in room-temperature strength. The effect of increasing Y2O3 addition on the room-temperature tensile strength of an Al2O3-ZrO2 material containing excess Al2O3 was examined at the NASA Glenn Research Center, where the materials were grown using Glenn's world-class laser growth facilities.

Raman Spectrum of Er-Y-codoped ZrO2 and Fluorescence Properties of Er3+

NASA Astrophysics Data System (ADS)

He, Jun; Luo, Meng-fei; Jin, Ling-yun; He, Mai; Fang, Ping; Xie, Yun-long

2007-02-01

Er-Y-codoped ZrO2 mixed oxides with monoclinic, tetragonal and cubic structures were prepared by a sol-gel method. The crystal structure of ZrO2 matrix and the effect of the ZrO2 phases on the fluorescence properties of Er3+ were studied using Raman spectroscopy. The results indicated that the fluorescence properties of Er3+ depend on its local ZrO2 crystal structures. As ZrO2 matrix transferred from monoclinic to tetragonal and cubic phase, the Raman and fluorescence bands of Er3+ decreased in intensities and tended to form a single peak. With 632.8 nm excitation, the bands between 640 and 680 nm were attributed to the fluorescence of Er3+ in the ZrO2 environment. However, only the fluorescence was observed and no Raman spectra were seen under 514.5 nm excitation, while only Raman spectra were observed under 325 nm excitation. UV Raman spectroscopy was found to be more sensitive in the surface region while the information provided by XRD mainly came from the bulk. The phase with lower symmetry forms more easily on the surface than in the bulk.

Sintering, thermal stability and mechanical properties of ZrO2-WC composites obtained by pulsed electric current sintering

NASA Astrophysics Data System (ADS)

Huang, Shuigen; Vanmeensel, Kim; van der Biest, Omer; Vleugels, Jozef

2011-03-01

ZrO2-WC composites exhibit comparable mechanical properties as traditional WC-Co materials, which provides an opportunity to partially replace WC-Co for some applications. In this study, 2 mol.% Y2O3 stabilized ZrO2 composites with 40 vol.% WC were consolidated in the 1150°C-1850°C range under a pressure of 60 MPa by pulsed electric current sintering (PECS). The densification behavior, microstructure and phase constitution of the composites were investigated to clarify the role of the sintering temperature on the grain growth, mechanical properties and thermal stability of ZrO2 and WC components. Analysis results indicated that the composites sintered at 1350°C and 1450°C exhibited the highest tetragonal ZrO2 phase transformability, maximum toughness, and hardness and an optimal flexural strength. Chemical reaction of ZrO2 and C, originating from the graphite die, was detected in the composite PECS for 20 min at 1850°C in vacuum.

Atomic layer deposition and properties of ZrO2/Fe2O3 thin films

PubMed Central

Seemen, Helina; Ritslaid, Peeter; Rähn, Mihkel; Tamm, Aile; Kukli, Kaupo; Kasikov, Aarne; Link, Joosep; Stern, Raivo; Dueñas, Salvador; Castán, Helena; García, Héctor

2018-01-01

Thin solid films consisting of ZrO2 and Fe2O3 were grown by atomic layer deposition (ALD) at 400 °C. Metastable phases of ZrO2 were stabilized by Fe2O3 doping. The number of alternating ZrO2 and Fe2O3 deposition cycles were varied in order to achieve films with different cation ratios. The influence of annealing on the composition and structure of the thin films was investigated. Additionally, the influence of composition and structure on electrical and magnetic properties was studied. Several samples exhibited a measurable saturation magnetization and most of the samples exhibited a charge polarization. Both phenomena were observed in the sample with a Zr/Fe atomic ratio of 2.0. PMID:29441257

Dip-coated ZrO2-Y2O3 coatings tested in molten salts for CSP applications

NASA Astrophysics Data System (ADS)

Pérez, Francisco Javier; Encinas-Sánchez, Víctor; Lasanta, María Isabel; de Miguel, María Teresa; García-Martín, Gustavo

2017-06-01

In the present work, the behaviour of ZrO2 - Y2O3 coatings in contact with molten salts at 500 °C has been studied. The coatings were prepared by sol-gel and deposited by dip-coating on AISI 304 specimens previously prepared by sanding and polishing. The behaviour in contact with molten salt was studied through static corrosion tests by the immersion of the coated samples in an alkali-nitrate mixture with a composition of 60 wt.% NaNO3/40 wt.% KNO3 (commonly known as Solar Salt). Prior to test, the deposited coatings were characterized using Scanning Electron Microscopy and X-Ray Diffraction, showing a compacted, homogeneous and uniform aspect and t-YSZ as main component. After corrosion tests, the samples were characterized via gravimetric, Scanning Electron Microscopy and X-Ray Diffraction. The results show a good behaviour of the coated samples compared with the bare coupon samples. However after 1000 h of testing m-ZrO2 appears in the composition,. At this preliminary study, results confirm the suitability of ZrO2 - Y2O3 coatings in solar applications after those working hours, although it is necessary to optimize the coating and study its behaviour at longer times.

Mechanical Properties of Plasma-Sprayed ZrO2-8 wt% Y2O3 Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Zhu, Dongming; Miller, Robert A.

2004-01-01

Mechanical behavior of free standing, plasma-sprayed ZrO2-8 wt% Y2O3 thermal barrier coatings, including strength, fracture toughness, fatigue, constitutive relation, elastic modulus, and directionality, has been determined under various loading-specimen configurations. This report presents and describes a summary of mechanical properties of the plasma-sprayed coating material to provide them as a design database.

Mechanical Properties and Plasma Erosion Resistance of ZrO2p(3Y)/BN-SiO2 Ceramic Composites under Different Sintering Temperature

NASA Astrophysics Data System (ADS)

Zhou, Yu; Duan1, Xiaoming; Jia, Dechang; Yang, Zhihua; Meng, Qingchang; Yu, Yang; Yu, Daren; Ding, Yongjie

2011-10-01

ZrO2p(3Y)/BN-SiO2 ceramic composites were hot pressed under different sintering temperature. The ceramic composites were composed by BN, m-ZrO2, t-ZrO2 and SiO2. The relative density, bending strength, elastic modulus and fracture toughness increase with the sintering temperature increasing, the maximum value of which at the sintering temperature of 1800°C are 97.5%, 229.9MPa, 60.8GPa and 3.55MPam1/2, respectively. The erosion resistance ability of ZrO2p(3Y)/BN-SiO2 ceramic composites rise gradually with the sintering temperature increasing, and the erosion rate of the ceramic composite sintered at 1800°C is 8.03×10-3mm/h.

Interaction of Au with thin ZrO2 films: influence of ZrO2 morphology on the adsorption and thermal stability of Au nanoparticles.

PubMed

Pan, Yonghe; Gao, Yan; Kong, Dandan; Wang, Guodong; Hou, Jianbo; Hu, Shanwei; Pan, Haibin; Zhu, Junfa

2012-04-10

The model catalysts of ZrO(2)-supported Au nanoparticles have been prepared by deposition of Au atoms onto the surfaces of thin ZrO(2) films with different morphologies. The adsorption and thermal stability of Au nanoparticles on thin ZrO(2) films have been investigated using synchrotron radiation photoemission spectroscopy (SRPES) and X-ray photoelectron spectroscopy (XPS). The thin ZrO(2) films were prepared by two different methods, giving rise to different morphologies. The first method utilized wet chemical impregnation to synthesize the thin ZrO(2) film through the procedure of first spin-coating a zirconium ethoxide (Zr(OC(2)H(5))(4)) precursor onto a SiO(2)/Si(100) substrate at room temperature followed by calcination at 773 K for 12 h. Scanning electron microscopy (SEM) investigations indicate that highly porous "sponge-like nanostructures" were obtained in this case. The second method was epitaxial growth of a ZrO(2)(111) film through vacuum evaporation of Zr metal onto Pt(111) in 1 × 10(-6) Torr of oxygen at 550 K followed by annealing at 1000 K. The structural analysis with low energy electron diffraction (LEED) of this film exhibits good long-range ordering. It has been found that Au forms smaller particles on the porous ZrO(2) film as compared to those on the ordered ZrO(2)(111) film at a given coverage. Thermal annealing experiments demonstrate that Au particles are more thermally stable on the porous ZrO(2) surface than on the ZrO(2)(111) surface, although on both surfaces, Au particles experience significant sintering at elevated temperatures. In addition, by annealing the surfaces to 1100 K, Au particles desorb completely from ZrO(2)(111) but not from porous ZrO(2). The enhanced thermal stability for Au on porous ZrO(2) can be attributed to the stronger interaction of the adsorbed Au with the defects and the hindered migration or coalescence resulting from the porous structures. © 2012 American Chemical Society

Doped ZrO2 for future lead free piezoelectric devices

NASA Astrophysics Data System (ADS)

Starschich, S.; Böttger, U.

2018-01-01

The ferroelectric and piezoelectric properties of doped ZrO2 prepared by chemical solution deposition (CSD) are investigated. Doping with different elements such as Mg, In, La, and Y leads to a stabilization of the constricted hysteresis. As shown in a previous work, for the constricted hysteresis of ZrO2, the piezoelectric response is significantly larger compared to ZrO2 with a normal hysteresis. The Mg doped ZrO2 shows a strong temperature and cycle stability. For the piezoelectric properties, a magnesium concentration of 7% shows the largest piezoelectric response with a piezoelectric coefficient of >10 pm/V, as well as the best cycle stability. Due to thicker films, which can be realized by the CSD technique, the shown doped ZrO2 films are a promising candidate for energy related applications such as piezoelectric energy harvesting as well as for microelectromechanical systems.

Characterization of ZrO2 and (ZrO2)x(Al2O3)1-X thin films on Si substrates: effect of the Al2O3 component

NASA Astrophysics Data System (ADS)

Vitanov, P.; Harizanova, A.; Ivanova, T.

2014-05-01

ZrO2 and (ZrO2)x(Al2O3)1-x films were deposited by the sol-gel technique on Si substrates. The effect of the Al2O3 additive on the film surface morphology was studied by atomic force microscopy (AFM). The mixed oxide films showed a smoother morphology and lower values of the root-mean-square (RMS) roughness compared to ZrO2. Further, FTIR spectra indicated that ZrO2 underwent crystallization. The electrical measurements of the MIS structure revealed that the presence of Al2O3 and the amorphization affects its dielectric properties. The MIS structure with (ZrO2)x(Al2O3)1-x showed a lower fixed charge (~ 6×1010 cm-2) and an interface state density in the middle of the band gap of 6×1011 eV-1 cm-2). The dielectric constant measured was 22, with the leakage current density decreasing to 2×10-8 A cm-2 at 1×106 V cm-1.

Microstructural and mechanical properties of Al2O3/ZrO2 nanomultilayer thin films prepared by pulsed laser deposition

NASA Astrophysics Data System (ADS)

Balakrishnan, G.; Sastikumar, D.; Kuppusami, P.; Babu, R. Venkatesh; Song, Jung Il

2018-02-01

Single layer aluminium oxide (Al2O3), zirconium oxide (ZrO2) and Al2O3/ZrO2 nano multilayer films were deposited on Si (100) substrates at room temperature by pulsed laser deposition. The development of Al2O3/ZrO2 nanolayered structure is an important method used to stabilize the high temperature phase (tetragonal and cubic) of ZrO2 at room temperature. In the Al2O3/ZrO2 multilayer structure, the Al2O3 layer was kept constant at 5 nm, while the ZrO2 layer thickness varied from 5 to 20 nm (5/5, 5/10, 5/15 and 5/20 nm) with a total of 40 bilayers. The X-ray diffraction studies of single layer Al2O3 indicated the γ-Al2O3 of cubic structure, while the single layer ZrO2 indicated both monoclinic and tetragonal phases. The 5/5 and 5/10 nm multilayer films showed the nanocrystalline nature of ZrO2 with tetragonal phase. The high resolution transmission electron microscopy studies indicated the formation of well-defined Al2O3 and ZrO2 layers and that they are of uniform thickness. The atomic force microscopy studies revealed the uniform and dense distribution of nanocrystallites. The nanoindentation studies indicated the hardness of 20.8 ± 1.10 and 10 ± 0.60 GPa, for single layer Al2O3 and ZrO2, respectively, and the hardness of multilayer films varied with bilayer thickness.

Effect of thermal cycling on ZrO2-Y2O3 thermal barrier coatings

NASA Technical Reports Server (NTRS)

Mcdonald, G.; Hendricks, R. C.

1980-01-01

A study was made of the comparative life of plasma sprayed ZrO2-Y2O3 thermal barrier coatings on NiCrAlY bond coats on Rene 41 in short (4 min) and long (57 min) thermal cycles to 1040 C in a 0.3 Mach flame. Short cycles greatly reduced the life of the ceramic coating in terms of time at temperature as compared to longer cycles. Appearance of the failed coating indicated compressive failure. Failure occurred at the bond coat-ceramic coat junction. At heating rates greater than 550 kw/sq m, the calculated coating detachment stress was in the range of literature values of coating adhesive/cohesive strength. Methods are discussed for decreasing the effect of high heating rate by avoiding compressive stress.

Promotional effect of Al2O3 on WO3/CeO2-ZrO2 monolithic catalyst for selective catalytic reduction of nitrogen oxides with ammonia after hydrothermal aging treatment

NASA Astrophysics Data System (ADS)

Xu, Haidi; Liu, Shuang; Wang, Yun; Lin, Qingjin; Lin, Chenlu; Lan, Li; Wang, Qin; Chen, Yaoqiang

2018-01-01

Hydrothermal stability of catalysts for selective catalytic reduction of NOx with NH3 (NH3-SCR) has always been recognized as a challenge in development of candidate catalysts for applications in diesel engine emissions. In this study, Al2O3 was introduced into CeO2-ZrO2 to improve the NH3-SCR activity of WO3/CeO2-ZrO2 after hydrothermal aging (HA) treatment at 800 °C for 12 h. The activity results indicated that the NH3-SCR activity of WO3/CeO2-ZrO2-HA was obviously improved in the whole reaction temperature range after doping Al2O3 into CeO2-ZrO2, for example, the average and maximum NOx conversion were separately increased by ca. 20% and 25% after HA treatment. XRD, Raman, TEM and EDX results revealed that the introduction of Al2O3 inhibited the sintering and agglomeration of CeO2-ZrO2 and WO3 and the formation of Ce2(WO4)3 after HA treatment. Accordingly, WO3/CeO2-ZrO2-Al2O3-HA showed remarkably improved structural stability and reducibility, increased surface acidity, and facilitated the reactivity between adsorbed NH3 and nitrate species, which together contributed to its better catalytic performance after hydrothermal aging treatment.

Mechanochemical stabilization and sintering of nanocrystalline the (ZrO2)0.97 (Y2O3)0.03 solid solution from pure oxides

NASA Astrophysics Data System (ADS)

Rendtorff, N. M.; Suárez, G.; Sakka, Y.; Aglietti, E. F.

2011-10-01

The mechanochemical activation processing has proved to be an effective technique to enhance a solid-state reaction at relatively low temperatures. In such a process, the mechanical effects of milling, such as reduction of particle size and mixture homogenization, are accompanied by chemical effects, such as partial decomposition of salts or hydroxides resulting in very active reactants. The objective of the present work is to obtain (ZrO2)0.97(Y2O3)0.03 nanocrystalline tetragonal solid solution powders directly using a high energy milling on a mixture of the pure oxides. A second objective is to evaluate the efficiency of the processing proposed and to characterize both textural and structural evolution of the mixtures during the milling processes and throughout posterior low temperature treatments. The Textural and structural evolution were studied by XRD analysis, specific area measurements (BET) and SEM. Firstly a decrease of the crystallinity of the reactants was observed, followed by the disappearance of Y2O3 diffraction peaks and the partial appearance of the tetragonal phase at room temperature. The solid solution proportion was increased with the high energy milling time, obtaining complete stabilization of the tetragonal solid solution with long milling treatments (60 min).The obtained powders were uniaxially pressed and sintered at different temperatures (600-1400°C) the influence of the milling time was correlated with the sinterization degree and final crystalline composition of the materials. Finally, fully stabilized nanocrystalline zirconia materials were obtained satisfactorily by the proposed method.

Characterizing the residual glass in a MgO/Al2O3/SiO2/ZrO2/Y2O3 glass-ceramic

PubMed Central

Seidel, Sabrina; Patzig, Christian; Wisniewski, Wolfgang; Gawronski, Antje; Hu, Yongfeng; Höche, Thomas; Rüssel, Christian

2016-01-01

The non-isochemical crystallization of glasses leads to glass-ceramics in which the chemical composition of the amorphous matrix differs from that of the parent glass. It is challenging to solely analyse the properties of these residual glassy phases because they frequently contain finely dispersed crystals. In this study, the composition of the residual glass matrix after the crystallization of a glass with the mol% composition 50.6 SiO2 · 20.7 MgO · 20.7 Al2O3 · 5.6 ZrO2 · 2.4 Y2O3 is analysed by scanning transmission electron microscopy (STEM) including energy dispersive X-ray analysis (EDXS). A batch of the residual glass with the determined composition is subsequently melted and selected properties are analysed. Furthermore, the crystallization behaviour of this residual glass is studied by X-ray diffraction, scanning electron microscopy including electron backscatter diffraction and STEM-EDXS analyses. The residual glass shows sole surface crystallization of indialite and multiple yttrium silicates while bulk nucleation does not occur. This is in contrast to the crystallization behaviour of the parent glass, in which a predominant bulk nucleation of spinel and ZrO2 is observed. The crystallization of the residual glass probably leads to different crystalline phases when it is in contact to air, rather than when it is enclosed within the microstructure of the parent glass-ceramics. PMID:27734918

Fabrication of dense and porous Li2ZrO3 nanofibers with electrospinning method

NASA Astrophysics Data System (ADS)

Yuan, Kangkang; Jin, Xiaotong; Xu, Chonghe; Wang, Xinqiang; Zhang, Guanghui; Zhu, Luyi; Xu, Dong

2018-06-01

Lithium zirconate (Li2ZrO3) has been extensively studied as CO2 capture material, electrolyte material and coating material. Most of the previous studies were focused on the powder structure, while seldom taking a consideration of fiber structure. In the present work, dense and porous Li2ZrO3 nanofibers with surface area of 16 m2 g-1 were prepared by electrospinning method. IR spectral results showed that lithium carbonate was the intermediate for the formation of Li2ZrO3. The phase transformation of Li2ZrO3 underwent the pathway of amorphous precursor fibers, tetragonal zirconia and Li2CO3, tetragonal Li2ZrO3, and monoclinic Li2ZrO3. XRD and XPS results further suggested that Li2O diffusion from the fiber body to surface occurred for Li2ZrO3 nanofibers when heat-treated above 900 °C, and the tetragonal Li2ZrO3 with high surface area could be obtained at 800 °C. Bamboo structure appeared both for the dense and porous nanofibers heat-treated at 1000 °C. The high surface area and high thermal stability of tetragonal phase of Li2ZrO3 make it a promising candidate in CO2 absorption, electrolyte and coating material.

Density functional theory calculations of the water interactions with ZrO2 nanoparticles Y2O3 doped

NASA Astrophysics Data System (ADS)

Subhoni, Mekhrdod; Kholmurodov, Kholmirzo; Doroshkevich, Aleksandr; Asgerov, Elmar; Yamamoto, Tomoyuki; Lyubchyk, Andrei; Almasan, Valer; Madadzada, Afag

2018-03-01

Development of a new electricity generation techniques is one of the most relevant tasks, especially nowadays under conditions of extreme growth in energy consumption. The exothermic heterogeneous electrochemical energy conversion to the electric energy through interaction of the ZrO2 based nanopowder system with atmospheric moisture is one of the ways of electric energy obtaining. The questions of conversion into the electric form of the energy of water molecules adsorption in 3 mol% Y2O3 doped ZrO2 nanopowder systems were investigated using the density functional theory calculations. The density functional theory calculations has been realized as in the Kohn-Sham formulation, where the exchange-correlation potential is approximated by a functional of the electronic density. The electronic density, total energy and band structure calculations are carried out using the all-electron, full potential, linear augmented plane wave method of the electronic density and related approximations, i.e. the local density, the generalized gradient and their hybrid approximations.

Study of fracture toughness of ZrO2 ceramics

NASA Astrophysics Data System (ADS)

Deryugin, Yevgeny; Narkevich, Natalya; Vlasov, Ilya; Panin, Victor; Danilenko, Igor; Schmauder, Siegfried

2017-12-01

The fracture toughness characteristics of ZrO2ceramics were determined experimentally using an original technique of wedging small-sized chevron notch specimens developed at the Institute of Strength Physics and Materials Science SB RAS (Russia) in the laboratory of physical mesomechanics of materials and non-destructive testing. Measurements have shown that inelastic displacements can be more than 22% of the total displacement of the consoles by the time of the specimen failure. The effect of the Y2O3 stabilizer on the critical stress intensity factor KIc was verified. It was shown that an increase in the Y2O3 stabilizer content from 3 to 8% significantly decreases the fracture toughness. The stress intensity factor KIc falls within the range from 5.7 to 2.35 MPa m1/2.

Structural and chemical degradation mechanisms of pure YSZ and its components ZrO2 and Y2O3 in carbon-rich fuel gases.

PubMed

Köck, Eva-Maria; Kogler, Michaela; Götsch, Thomas; Klötzer, Bernhard; Penner, Simon

2016-05-25

Structural and chemical degradation mechanisms of metal-free yttria stabilized zirconia (YSZ-8, 8 mol% Y2O3 in ZrO2) in comparison to its pure oxidic components ZrO2 and Y2O3 have been studied in carbon-rich fuel gases with respect to coking/graphitization and (oxy)carbide formation. By combining operando electrochemical impedance spectroscopy (EIS), operando Fourier-transform infrared (FT-IR) spectroscopy and X-ray photoelectron spectroscopy (XPS), the removal and suppression of CH4- and CO-induced carbon deposits and of those generated in more realistic fuel gas mixtures (syngas, mixtures of CH4 or CO with CO2 and H2O) was examined under SOFC-relevant conditions up to 1273 K and ambient pressures. Surface-near carbidization is a major problem already on the "isolated" (i.e. Nickel-free) cermet components, leading to irreversible changes of the conduction properties. Graphitic carbon deposition takes place already on the "isolated" oxides under sufficiently fuel-rich conditions, most pronounced in the pure gases CH4 and CO, but also significantly in fuel gas mixtures containing H2O and CO2. For YSZ, a comparative quantification of the total amount of deposited carbon in all gases and mixtures is provided and thus yields favorable and detrimental experimental approaches to suppress the carbon formation. In addition, the effectivity and reversibility of removal of the coke/graphite layers was comparably studied in the pure oxidants O2, CO2 and H2O and their effective contribution upon addition to the pure fuel gases CO and CH4 verified.

Effect of milling methods on performance of Ni-Y 2O 3-stabilized ZrO 2 anode for solid oxide fuel cell

NASA Astrophysics Data System (ADS)

Cho, Hyoup Je; Choi, Gyeong Man

A Ni-YSZ (Y 2O 3-stabilized ZrO 2) composite is commonly used as a solid oxide fuel cell anode. The composite powders are usually synthesized by mixing NiO and YSZ powders. The particle size and distribution of the two phases generally determine the performance of the anode. Two different milling methods are used to prepare the composite anode powders, namely, high-energy milling and ball-milling that reduce the particle size. The particle size and the Ni distribution of the two composite powders are examined. The effects of milling on the performance are evaluated by using both an electrolyte-supported, symmetric Ni-YSZ/YSZ/Ni-YSZ cell and an anode-supported, asymmetric cell. The performance is examined at 800 °C by impedance analysis and current-voltage measurements. Pellets made by using high-energy milled NiO-YSZ powders have much smaller particle sizes and a more uniform distribution of Ni particles than pellets made from ball-milled powder, and thus the polarization resistance of the electrode is also smaller. The maximum power density of the anode-supported cell prepared by using the high-energy milled powder is ∼850 mW cm -2 at 800 °C compared with ∼500 mW cm -2 for the cell with ball-milled powder. Thus, high-energy milling is found to be more effective in reducing particle size and obtaining a uniform distribution of Ni particles.

CONDENSED MATTER: ELECTRONIC STRUCTURE, ELECTRICAL, MAGNETIC, AND OPTICAL PROPERTIES: Influence of Ytterbia Content on Residual Stress and Microstructure of Y2O3-ZrO2 Thin Films Prepared by EB-PVD*

NASA Astrophysics Data System (ADS)

Xiao, Qi-Ling; Shao, Sriu-Ying; He, Hong-Bo; Shao, Jian-Da; Fan, Zheng-Xiu

2008-09-01

Y2O3 stabilized ZrO2 (YSZ) thin films with different Y2O3 molar contents (0, 3, 7, and 12mol%) are deposited on BK7 substrates by electron-beam evaporation technique. The effects of different Y2O3 contents on residual stresses and structures of YSZ thin films are studied. Residual stresses are investigated by means of two different techniques: the curvature measurement and x-ray diffraction method. It is found that the evolution of residual stresses of YSZ thin films by the two different methods is consistent. Residual stresses of films transform from compressive stress into tensile stress and the tensile stress incre ases monotonically with the increase of Y2O3 content. At the same time, the structures of these films change from the mixture of amorphous and monoclinic phases into high temperature cubic phase. The variations of residual stress correspond to the evolution of structures induced by adding of Y2O3 content.

Fabrication and Properties of Plasma-Sprayed Al2O3/ZrO2 Composite Coatings

NASA Astrophysics Data System (ADS)

Dejang, N.; Limpichaipanit, A.; Watcharapasorn, A.; Wirojanupatump, S.; Niranatlumpong, P.; Jiansirisomboon, S.

2011-12-01

Al2O3 /xZrO2 (where x = 0, 3, 13, and 20 wt.%) composite coatings were deposited onto mild steel substrates by atmospheric plasma spraying of mixed α-Al2O3 and nano-sized monoclinic-ZrO2 powders. Microstructural investigation showed that the coatings comprised well-separated Al2O3 and ZrO2 lamellae, pores, and partially molten particles. The coating comprised mainly of metastable γ-Al2O3 and tetragonal-ZrO2 with trace of original α-Al2O3 and monoclinic-ZrO2 phases. The effect of ZrO2 addition on the properties of coatings were investigated in terms of microhardness, fracture toughness, and wear behavior. It was found that ZrO2 improved the fracture toughness, reduced friction coefficient, and wear rate of the coatings.

Effects of firing schedule on solubility limits and transport properties of ZrO 2-TiO 2-Y 2O 3 fluorites

NASA Astrophysics Data System (ADS)

Fagg, D. P.; Frade, J. R.; Mogensen, M.; Irvine, J. T. S.

2007-08-01

The low Y/high Zr edge of the cubic defect fluorite solid solution in the system ZrO 2-TiO 2-Y 2O 3 in air is reassessed, as it is these compositions which have been suggested to offer the highest levels of mixed conductivity. Vegard's law is obeyed for values of x which lie within the cubic defect fluorite phase in Zr 1-x-yY yTi xO 2-δ for values of y=0.2 and 0.25. Measured lattice parameters show good agreement with those calculated from the Kim relation. Deviation from Vegard's law places the limit of the solid solution at x=0.18 and 0.20 for values of y=0.2 and 0.25, respectively, at 1500 °C. Discrepancies in current literature data can be shown to be due to differences in firing schedule such as slight temperature fluctuations and/or different cooling rates. A high level of care of sintering temperature and cooling profile is essential to form the most promising single-phase materials which contain maximum Ti-contents with low Y-contents. Contraction of the phase limit as a result of poor synthesis control leads to erroneously high values of bulk ionic conductivity while values of electronic conductivity are shown to be less affected.

The effect of preliminary hydrolysis on the properties of ZrO2-7% Y2O3 powders prepared by hydroxide precipitation

NASA Astrophysics Data System (ADS)

Zhirenkina, Nina V.; Mashkovtsev, Maxim A.; Bereskina, Polina A.; Zakirov, Ilsur F.; Baksheev, Evgenie O.; Bujnachev, Sergey V.; Vereshchagin, Artem O.

2017-09-01

In this study, the effect of preliminary hydrolysis of zirconyl oxysulfate on the properties of ZrO2-7 % Y2O3 powders prepared by hydroxides precipitation at a constant pH of 5 was studied. X-ray diffraction analysis showed the monophasic nature of the samples and the insignificant difference between CSR (coherent scattering regions). Samples differed in particle size distribution, porosity and morphology.

Assessment of solid/liquid equilibria in the (U, Zr)O2+y system

NASA Astrophysics Data System (ADS)

Mastromarino, S.; Seibert, A.; Hashem, E.; Ciccioli, A.; Prieur, D.; Scheinost, A.; Stohr, S.; Lajarge, P.; Boshoven, J.; Robba, D.; Ernstberger, M.; Bottomley, D.; Manara, D.

2017-10-01

Solid/liquid equilibria in the system UO2sbnd ZrO2 are revisited in this work by laser heating coupled with fast optical thermometry. Phase transition points newly measured under inert gas are in fair agreement with the early measurements performed by Wisnyi et al., in 1957, the only study available in the literature on the whole pseudo-binary system. In addition, a minimum melting point is identified here for compositions near (U0.6Zr0.4)O2+y, around 2800 K. The solidus line is rather flat on a broad range of compositions around the minimum. It increases for compositions closer to the pure end members, up to the melting point of pure UO2 (3130 K) on one side and pure ZrO2 (2970 K) on the other. Solid state phase transitions (cubic-tetragonal-monoclinic) have also been observed in the ZrO2-rich compositions X-ray diffraction. Investigations under 0.3 MPa air (0.063 MPa O2) revealed a significant decrease in the melting points down to 2500 K-2600 K for increasing uranium content (x(UO2)> 0.2). This was found to be related to further oxidation of uranium dioxide, confirmed by X-ray absorption spectroscopy. For example, a typical oxidised corium composition U0.6Zr0.4O2.13 was observed to solidify at a temperature as low as 2493 K. The current results are important for assessing the thermal stability of the system fuel - cladding in an oxide based nuclear reactor, and for simulating the system behaviour during a hypothetical severe accident.

Extremely fine structured cathode for solid oxide fuel cells using Sr-doped LaMnO3 and Y2O3-stabilized ZrO2 nano-composite powder synthesized by spray pyrolysis

NASA Astrophysics Data System (ADS)

Shimada, Hiroyuki; Yamaguchi, Toshiaki; Sumi, Hirofumi; Nomura, Katsuhiro; Yamaguchi, Yuki; Fujishiro, Yoshinobu

2017-02-01

A solid oxide fuel cell (SOFC) for high power density operation was developed with a microstructure-controlled cathode using a nano-composite powder of Sr-doped LaMnO3 (LSM) and Y2O3-stabilized ZrO2 (YSZ) synthesized by spray pyrolysis. The individual LSM-YSZ nano-composite particles, formed by crystalline and amorphous nano-size LSM and YSZ particles, showed spherical morphology with uniform particle size. The use of this powder for cathode material led to an extremely fine microstructure, in which all the LSM and YSZ grains (approximately 100-200 nm) were highly dispersed and formed their own network structures. This microstructure was due to the two phase electrode structure control using the powder, namely, nano-order level in each particle and micro-order level between particles. An anode-supported SOFC with the LSM-YSZ cathode using humidified H2 as fuel and ambient air as oxidant exhibited high power densities, such as 1.29 W cm-2 under a voltage of 0.75 V and a maximum power density of 2.65 W cm-2 at 800 °C. Also, the SOFC could be stably operated for 250 h with no degradation, even at a high temperature of 800 °C.

Dielectric Properties of BST/(Y 2O 3) x(ZrO 2) 1-x/BST Trilayer Films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sahoo, Santosh K.; Misra, D.

2011-01-31

Thin films of Ba1-xSrxTiO3 (BST) are being actively investigated for applications in dynamic random access memories (DRAM) because of their properties such as high dielectric constant, low leakage current, and high dielectric breakdown strength. Various approaches have been used to improve the dielectric properties of BST thin films such as doping, graded compositions, and multilayer structures. We have found that inserting a ZrO2 layer in between two BST layers results in a significant reduction in dielectric constant as well as dielectric loss. In this work the effect of Y2O3 doped ZrO2 on the dielectric properties of BST/ZrO2/BST trilayer structure ismore » studied. The structure Ba0.8Sr0.2TiO3/(Y2O3)x(ZrO2)1-x/Ba0.8Sr0.2TiO3 is deposited by a sol-gel process on platinized Si substrate. The composition (x) of the middle layer is varied while keeping the total thickness of the trilayer film constant. The dielectric constant of the multilayer film decreases with the increase of Y2O3 amount in the film whereas there is a slight variation in dielectric loss. In Y2O3 doped multilayer thin films, the dielectric loss is lower in comparison to other films and also there is good frequency stability in the loss in the measured frequency range and hence very suitable for microwave device applications.« less

Hydrodeoxygenation of p -Cresol over Pt/Al 2 O 3 Catalyst Promoted by ZrO 2 , CeO 2 , and CeO 2 –ZrO 2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Weiyan; Wu, Kui; Liu, Pengli

2016-07-20

ZrO 2-Al 2O 3 and CeO 2-Al 2O 3 were prepared by a co-precipitation method and selected as supports for Pt catalysts. The effects of CeO 2 and ZrO 2 on the surface area and Brønsted acidity of Pt/Al 2O 3 were studied. In the hydrodeoxygenation (HDO) of p-cresol, the addition of ZrO 2 promoted the direct deoxygenation activity on Pt/ZrOO 2-Al 2O 3 via Caromatic-O bond scission without benzene ring saturation. Pt/CeOO 2-Al 2O 3 exhibited higher deoxygenation extent than Pt/Al 2O 3 due to the fact that Brønsted acid sites on the catalyst surface favored the adsorption ofmore » p-cresol. With the advantages of CeO 2 and ZrO 2 taken into consideration, CeO 2-ZrOO 2-Al 2O 3 was prepared, leading to the highest HDO activity of Pt/CeO 2-ZrOO 2-Al 2O 3. The deoxygenation extent for Pt/CeO 2-ZrOO 2-Al 2O 3 was 48.4% and 14.5% higher than that for Pt/ZrO2O 2-Al 2O 3 and Pt/CeOO 2-Al 2O 3, respectively.« less

Theoretical study of the promotional effect of ZrO2 on In2O3 catalyzed methanol synthesis from CO2 hydrogenation

NASA Astrophysics Data System (ADS)

Zhang, Minhua; Dou, Maobin; Yu, Yingzhe

2018-03-01

Methanol synthesis from CO2 hydrogenation on the ZrO2 doped In2O3(110) surface (Zr-In2O3(110)) with oxygen vacancy has been studied using the density functional theory calculations. The calculated results show that the doped ZrO2 species prohibits the excessive formation of oxygen vacancies and dissociation of H2 on In2O3 surface slightly, but enhances the adsorption of CO2 on both perfect and defective Zr-In2O3(110) surface. Methanol is formed via the HCOO route. The hydrogenation of CO2 to HCOO is both energetically and kinetically facile. The HCOO hydrogenates to polydentate H2CO (p-H2CO) species with an activation barrier of 0.75 eV. H3CO is produced from the hydrogenation of monodentate H2CO (mono-H2CO), transformation from p-H2CO with 0.82 eV reaction energy, with no barrier whether there is hydroxyl group between the mono-H2CO and the neighboring hydride or not. Methanol is the product of H3CO protonation with 0.75 eV barrier. The dissociation and protonation of CO2 are both energetically and kinetically prohibited on Zr-In2O3(110) surface. The doped ZrO2 species can further enhance the adsorption of all the intermediates involved in CO2 hydrogenation to methanol, activate the adsorbed CO2 and H2CO, and stabilize the HCOO, H2CO and H3CO, especially prohibit the dissociation of H2CO or the reaction of H2CO with neighboring hydride to form HCOO and gas phase H2. All these effects make the ZrO2 supported In2O3 catalyst exhibit higher activity and selectivity on methanol synthesis from CO2 hydrogenation.

A composite material with CeO2-ZrO2 nanocrystallines embedded in SiO2 matrices and its enhanced thermal stability and oxygen storage capacity

NASA Astrophysics Data System (ADS)

Yang, Runnong; Liu, Yumei; Yu, Lin; Zhao, Xiangyun; Yang, Xiaobo; Sun, Ming; Luo, Junyin; Fan, Qun; Xiao, Jianming; Zhao, Yuzhong

2018-06-01

A simple hydrothermal procedure is introduced, which leads to the successful synthesis of a new composite material with fine CeO2-ZrO2 nanocrystallites embedded in amorphous and porous SiO2 matrices. The composite material possesses an extraordinary high thermal stability. After being calcined at 1000 °C, it retains CeO2-ZrO2 nanocrystallites of the size around 5 nm, a BET-specific surface area of 165 m2/g, and an oxygen storage capacity of 468 μmol/g. No phase segregation for CeO2-ZrO2 nanocrystallites is detected and the SiO2 matrices remain not crystallized. The composite material shows a great potential as a support of three-way catalyst, as evidenced in catalytic tests with supported Pt.

The glass-like thermal conductivity in ZrO2-Dy3TaO7 ceramic for promising thermal barrier coating application

NASA Astrophysics Data System (ADS)

Wu, Peng; Hu, Ming Yu; Chong, Xiao Yu; Feng, Jing

2018-03-01

Using the solid-state reaction method, the (ZrO2)x-(Dy3TaO7)1-x (x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1) ceramics are synthesized in this work. The identification of the crystal structures indicates that the (ZrO2)x-(Dy3TaO7)1-x ceramics belong to the orthorhombic system, and the space group is C2221 in spite of the value of x increasing to 0.1. The thermal conductivities of the (ZrO2)x-(Dy3TaO7)1-x ceramics range from 1.3 W/(m K) to 1.8 W/(m K), and this value is much lower than that of 7-8 YSZ (yttria-stabilized zirconia). Besides, the (ZrO2)x-(Dy3TaO7)1-x ceramics possess the glass-like thermal conductivity caused by intrinsic oxygen vacancies existing in the lattice of Dy3TaO7. Moreover, the results of thermal expansion rates demonstrate that the (ZrO2)x-(Dy3TaO7)1-x ceramics possess excellent high temperature phase stability, and the thermal expansion coefficients [(9.7-11) × 10-6 K-1] are comparable to that of 7-8 YSZ.

Annealing Behavior of 57Fe Implanted in ZrO2(Y)

NASA Astrophysics Data System (ADS)

Zhang, G. L.; Yu, F. H.; Weng, H. M.; Zhang, H. H.

1998-12-01

Using conversion electron Mossbauer spectroscopy(CEMS) and slow positron beam, the chemical states of the implanted 57Fe (100KeV,3 × 10 16 ions/cm 2) in ZrO2 containing 3 mol% Y 2O 3( ZY 3) and its thermodynamic behavior during annealing process with the temperature from 200 to 500°C were studied. After annealing at 400°C the complex of Fe3+-V has been mostly dissolved, and the prior phase to α-Fe and α-Fe nano-crystalline cluster were present in the sample. Meanwhile the mixed conducting of oxygen-ions and electrons in the ZY3 containing Fe sample appeared.

Effect of Er3+ concentration on the luminescence properties of Al2O3-ZrO2 powder

NASA Astrophysics Data System (ADS)

Clabel H., J. L.; Rivera, V. A. G.; Nogueira, I. C.; Leite, E. R.; Siu Li, M.; Marega, E.

2016-12-01

This manuscript reports on the effects of the luminescence properties of Er3+ on Al2O3-ZrO2 powder synthesized by the conventional solid-state method. The best conditions found for the calcinations were 1500 °C and 4 h. The structural dependence of the luminescence on Er3+:Al2O3-ZrO2 is associated with phase transformations of the Al2O3-ZrO2 host and presence of the OH group. Green and red emissions at room temperature from the 2H11/2, 4S3/2 → 4I15/2 and 4F9/2 → 4I15/2 levels of Er3+ ions were observed under 482 nm pumping. The green-to-red emission intensity ratios and CIE chromaticity coordinates were determined from emission spectra for the evaluation of light emitted as a function of the Er3+ concentration. The Er3+ luminescence quenching due to group OH and variation in the Er3+ concentration plays an important role in the definition of the luminescent response.

One-pot synthesis and optical properties of Eu3+-doped nanocrystalline TiO2 and ZrO2

NASA Astrophysics Data System (ADS)

Julián, Beatriz; Corberán, Rosa; Cordoncillo, Eloisa; Escribano, Purificación; Viana, Bruno; Sanchez, Clément

2005-11-01

A simple and versatile one-pot sol-gel synthesis of Eu3+-doped nanocrystalline TiO2 and ZrO2 nanomaterials is reported in this paper. It consists of the controlled crystallization of Eu3+-doped TiO2 or ZrO2 nanoparticles from an initial solution containing the metal alkoxide, the lanthanide precursor, a complexing agent and a non-complexing acid. The main interest is that it could be extended to different lanthanide ions and inorganic metal oxides to prepare other multifunctional nanomaterials. The characterization by XRD, HRTEM and SAED techniques showed that the TiO2 and ZrO2 crystallization takes place at very low temperatures (60 °C) and that the crystallite size can be tailored by modifying the synthetic conditions. The optical properties of the resulting materials were studied by emission spectra and decay measurements. Both Eu3+:TiO2 and Eu3+:ZrO2 samples exhibited long lifetime values after removing organic components (τ = 0.7 and 1.3 ms, respectively), but the Eu3+:ZrO2 system is specially promising for photonic applications since its τ value is longer than some reported for other inorganic or hybrid matrices in which Eu3+ ions are complexed. This behaviour has been explained through an effective dispersion of the lanthanide ions within the ZrO2 nanocrystals.

Influence of miscut Y2O3-stabilized ZrO2 substrates on the azimuthal domain structure and ferroelectric properties of epitaxial La-substituted Bi4Ti3O12 films

NASA Astrophysics Data System (ADS)

Lee, Sung Kyun; Hesse, Dietrich; Gösele, Ulrich; Lee, Ho Nyung

2006-09-01

We have investigated the influence of both miscut angle and miscut direction of Y2O3-stabilized ZrO2 (YSZ) (100) single crystal substrates on the azimuthal domain structure of SrRuO3 electrode layers as well as of La-substituted Bi4Ti3O12 (BLT) ferroelectric thin films, both grown on these substrates by pulsed laser deposition. X-ray diffraction ϕ scan and pole figure characterizations revealed that the YSZ[011] miscut direction is more effective to uniformly reduce the number of azimuthal domain variants in the films than the YSZ[001] miscut direction. The BLT films on YSZ(100) substrates with miscut angle of 5° and [011] miscut direction involve only half the number of azimuthal domains, compared to the BLT films on exactly cut YSZ(100) substrates. Atomic force microscopy and plan-view transmission electron microscopy also confirmed that almost all BLT grains on these miscut YSZ(100) substrates are arranged along only two (out of four) specific azimuthal directions. The BLT films on YSZ(100) substrates with 5° miscut towards YSZ[011] showed an about 1.3 times higher remanent polarization (Pr=12.5μC /cm2) than the BLT films on exactly cut YSZ(100) substrates (Pr=9.5μC/cm2), due most probably to a lower areal density of azimuthal domain boundaries. It thus appears that reducing the structural domains can be an effective way to further enhance the ferroelectric properties of multiply twinned, epitaxial ferroelectric films.

Chitosan /Zeolite Y/Nano ZrO2 nanocomposite as an adsorbent for the removal of nitrate from the aqueous solution.

PubMed

Teimouri, Abbas; Nasab, Shima Ghanavati; Vahdatpoor, Niaz; Habibollahi, Saeed; Salavati, Hossein; Chermahini, Alireza Najafi

2016-12-01

In the present study, a series of chitosan/Zeolite Y/Nano Zirconium oxide (CTS/ZY/Nano ZrO 2 ) nanocomposites were made by controlling the molar ratio of chitosan (CTS) to Zeolite Y/Nano Zirconium oxide in order to remove nitrate (NO 3 - ) ions in the aqueous solution. The nanocomposite adsorbents were characterized by XRD, FTIR, BET, SEM and TEM. The influence of different molar ratios of CTS to ZY/Nano ZrO 2 , the initial pH value of the nitrate solution, contact time, temperature, the initial concentration of nitrate and adsorbent dose was studied. The adsorption isotherms and kinetics were also analyzed. It was attempted to describe the sorption processes by the Langmuir equation and the theoretical adsorption capacity (Q 0 ) was found to be 23.58mg nitrate per g of the adsorbent. The optimal conditions for nitrate removal were found to be: molar ratio of CTS/ZY/Nano ZrO 2 : 5:1; pH: 3; 0.02g of adsorbent and temperature: 35°C, for 60min. The adsorption capacities of CTS, ZY, Nano ZrO 2 , CTS/Nano ZrO 2 , CTS/ZY and CTS/ZY/Nano ZrO 2 nanocomposites for nitrate removal were compared, showing that the adsorption ability of CTS/ZY/Nano ZrO 2 nanocomposite was higher than the average values of those of CTS (1.95mg/g for nitrate removal), ZY, Nano ZrO 2 , CTS/Nano ZrO 2, and CTS/ZY. Copyright © 2016. Published by Elsevier B.V.

Radiation damage in cubic ZrO 2 and yttria-stabilized zirconia from molecular dynamics simulations

DOE PAGES

Aidhy, Dilpuneet S.; Zhang, Yanwen; Weber, William J.

2014-11-20

Here, we perform molecular dynamics simulation on cubic ZrO 2 and yttria-stabilized zirconia (YSZ) to elucidate defect cluster formation resulting from radiation damage, and evaluate the impact of Y-dopants. Interstitial clusters composed of split-interstitial building blocks, i.e., Zr-Zr or Y-Zr are formed. Moreover, oxygen vacancies control cation defect migration; in their presence, Zr interstitials aggregate to form split-interstitials whereas in their absence Zr interstitials remain immobile, as isolated single-interstitials. Y-doping prevents interstitial cluster formation due to sequestration of oxygen vacancies.

ZrO2-Nanoparticle-Modified Graphite Felt: Bifunctional Effects on Vanadium Flow Batteries.

PubMed

Zhou, Haipeng; Shen, Yi; Xi, Jingyu; Qiu, Xinping; Chen, Liquan

2016-06-22

To improve the electrochemical performance of graphite felt (GF) electrodes in vanadium flow batteries (VFBs), we synthesize a series of ZrO2-modified GF (ZrO2/GF) electrodes with varying ZrO2 contents via a facile immersion-precipitation approach. It is found that the uniform immobilization of ZrO2 nanoparticles on the GF not only significantly promotes the accessibility of vanadium electrolyte, but also provides more active sites for the redox reactions, thereby resulting in better electrochemical activity and reversibility toward the VO(2+)/VO2(+) and V(2+)/V(3+) redox reactions as compared with those of GF. In particular, The ZrO2/GF composite with 0.3 wt % ZrO2 displays the best electrochemical performance with voltage and energy efficiencies of 71.9% and 67.4%, respectively, which are much higher than those of 57.3% and 53.8% as obtained from the GF electrode at 200 mA cm(-2). The cycle life tests demonstrate that the ZrO2/GF electrodes exhibit outstanding stability. The ZrO2/GF-based VFB battery shows negligible activity decay after 200 cycles.

Theoretical study of methanol synthesis from CO2 and CO hydrogenation on the surface of ZrO2 supported In2O3 catalyst

NASA Astrophysics Data System (ADS)

Dou, Maobin; Zhang, Minhua; Chen, Yifei; Yu, Yingzhe

2018-06-01

The interactions between ZrO2 support and In2O3 catalyst play pivotal role in the catalytic conversion of CO2 to methanol. Herein, a density functional theory study has been conducted to research the mechanism of methanol synthesis from CO2 and CO hydrogenation on the defective ZrO2 supported In2O3(110) surface (D surface). The calculations reveal that methanol is produced mainly via the HCOO reaction pathway from CO2 hydrogenation on D surface, and the hydrogenation of HCOO to form H2COO species with an activation barrier of 1.21 eV plays the rate determining step for the HCOO reaction pathway. The direct dissociation of CO2 to CO on D surface is kinetically and energetically prohibited. Methanol synthesis from CO hydrogenation on D surface is much facile comparing with the elementary steps involved in CO2 hydrogenation. The rate determining step of CO hydrogenation to methanol is the formation of H3CO species on the vacancy site with a barrier of 0.51 eV. ZrO2 support has significant effect on the suppressing of the dissociation of CO2 and stabilization of H2COO species on the surface of In2O3 catalyst.

Irradiation behavior of LiAlO 2 and Li 2ZrO 3 ceramics in the ALICE 3 experiment

NASA Astrophysics Data System (ADS)

Rasneur, B.; Thevenot, G.; Bouilloux, Y.

1992-09-01

Within the framework of the investigation of ceramic breeders for the DEMO relevant solid blankets developed in Europe, the ALICE 3 experiment was foreseen to study the irradiation behavior of the ceramics. The irradiation was performed in the core of the OSIRIS reactor for 46 FPD (full power days) at 400°C and 600°C. The three ceramics in the configuration contemplated in the BIT and BOT concepts were tested, i.e. LiAlO 2 and Li 2ZrO 3 pellets, Li 4SiO 4 and Li 2ZrO 3 pebbles, respectively. In this paper are reported the results of the post-irradiation examination carried out at CEA on CEA Li 2ZrO 3 and LiAlO 2 specimens: dimensions, X-ray diffraction, ultimate bending strength, diametral compressive strength and residual tritium.

The effect of B 2O 3 addition on the crystallization of amorphous TiO 2-ZrO 2 mixed oxide

NASA Astrophysics Data System (ADS)

Mao, Dongsen; Lu, Guanzhong

2007-02-01

The effect of B 2O 3 addition on the crystallization of amorphous TiO 2-ZrO 2 mixed oxide was investigated by X-ray diffraction (XRD), thermogravimetric and differential thermal analysis (TG/DTA). TiO 2-ZrO 2 mixed oxide was prepared by co-precipitation method with aqueous ammonia as the precipitation reagent. Boric acid was used as a source of boria, and boria contents varied from 2 to 20 wt%. The results indicate that the addition of small amount of boria (<8 wt%) hinders the crystallization of amorphous TiO 2-ZrO 2 into a crystalline ZrTiO 4 compound, while a larger amount of boria (⩾8 wt%) promotes the crystallization process. FT-IR spectroscopy and 11B MAS NMR results show that tetrahedral borate species predominate at low boria loading, and trigonal borate species increase with increasing boria loading. Thus it is concluded that highly dispersed tetrahedral BO 4 units delay, while a build-up of trigonal BO 3 promote, the crystallization of amorphous TiO 2-ZrO 2 to form ZrTiO 4 crystals.

Synthesis of Zr2WP2O12/ZrO2 Composites with Adjustable Thermal Expansion.

PubMed

Zhang, Zhiping; Sun, Weikang; Liu, Hongfei; Xie, Guanhua; Chen, Xiaobing; Zeng, Xianghua

2017-01-01

Zr 2 WP 2 O 12 /ZrO 2 composites were fabricated by solid state reaction with the goal of tailoring the thermal expansion coefficient. XRD, SEM and TMA were used to investigate the composition, microstructure, and thermal expansion behavior of Zr 2 WP 2 O 12 /ZrO 2 composites with different mass ratio. Relative densities of all the resulting Zr 2 WP 2 O 12 /ZrO 2 samples were also tested by Archimedes' methods. The obtained Zr 2 WP 2 O 12 /ZrO 2 composites were comprised of orthorhombic Zr 2 WP 2 O 12 and monoclinic ZrO 2 . As the increase of the Zr 2 WP 2 O 12 , the relative densities of Zr 2 WP 2 O 12 /ZrO 2 ceramic composites increased gradually. The coefficient of thermal expansion of the Zr 2 WP 2 O 12 /ZrO 2 composites can be tailored from 4.1 × 10 -6 K -1 to -3.3 × 10 -6 K -1 by changing the content of Zr 2 WP 2 O 12 . The 2:1 Zr 2 WP 2 O 12 /ZrO 2 specimen shows close to zero thermal expansion from 25 to 700°C with an average linear thermal expansion coefficient of -0.09 × 10 -6 K -1 . These adjustable and near zero expansion ceramic composites will have great potential application in many fields.

Structural, electronic, elastic and thermodynamic properties of Li2ZrO3: A comprehensive study using DFT formalism

NASA Astrophysics Data System (ADS)

Chattaraj, D.

2017-12-01

Lithium zirconate is considered to be potential tritium breeder material for fusion reactors. Here I report a comprehensive study on structural, electronic, elastic, and thermodynamic properties of Li2ZrO3 using plane wave based density functional theory. While the electron-ion interaction term has been described by projected-augmented wave method, the exchange-correlation energy was taken care of through generalized gradient approximation scheme. The optimized lattice and internal parameters of Li2ZrO3 unit cell agree well within ±1-2% from the experimental values. From the electronic structure analysis it is seen that the Fermi energy has significant contribution from the 2s, 2p and 4d orbitals of Li, O and Zr atoms, respectively. Elastic property calculation of Li2ZrO3 showed mechanical stability and anisotropy at ambient pressure. The formation energy (ΔfH) of Li2ZrO3 at 0 K, after zero point energy correction, has been estimated to be -1550 kJ/mol. The temperature dependent thermodynamic functions of Li2ZrO3 have also been calculated from the Debye-Grüneisen quasi-harmonic approximation and reported here.

Temperature-dependent local structural properties of redox Pt nanoparticles on TiO 2 and ZrO 2 supports

DOE PAGES

Jeong, Eun -Suk; Park, Chang -In; Jin, Zhenlan; ...

2015-01-21

This paper examined the local structural properties of Pt nanoparticles on SiO 2, TiO 2–SiO 2, and ZrO 2–SiO 2 supports to better understand the impact of oxide-support type on the performance of Pt-based catalysts. In situ X-ray absorption fine structure (XAFS) measurements were taken for the Pt L3-edge in a temperature range from 300 to 700 K in He, H 2, and O 2 gas environments. The XAFS measurements demonstrated that Pt atoms were highly dispersed on TiO 2–SiO 2 and ZrO 2–SiO 2 forming pancake-shaped nanoparticles, whereas Pt atoms formed larger particles of hemispherical shapes on SiO 2more » supports. Contrary to the SiO 2 case, the coordination numbers for Pt, Ti, and Zr around Pt atoms on the TiO 2–SiO 2 and ZrO 2–SiO 2 supports were nearly constant from 300 to 700 K under the different gas environments. These results are consistent with the improvements in thermal stability of Pt nanoparticles achieved by incorporating TiO 2 or ZrO 2 on the surface of SiO 2 supports. XAFS analysis further indicated that the enhanced dispersion and stability of Pt were a consequence of the strong metal support interaction via Pt–Ti and Pt–Zr bonds.« less

High-yield sol-gel synthesis of well-dispersed, colorless ZrO(2) nanocrystals.

PubMed

Mizuno, Mikihisa; Sasaki, Yuichi; Lee, Sungkil; Katakura, Hitoshi

2006-08-15

A 93% high-yield synthesis of well-dispersed, colorless zirconium dioxide (ZrO(2)) nanocrystals is reported. In this synthesis, hydrolysis and condensation reactions of zirconium(IV) tert-butoxide in the presence of oleic acid (100 degrees C) formed ZrO(2) precursors. The ZrO(2) precursors were made of -Zr-O-Zr- networks surrounded by oleic acid molecules. Annealing (280 degrees C) the precursors dispersed in dioctyl ether caused crystallization of the -Zr-O-Zr- networks, thereby generating 4 nm ZrO(2) nanocrystals stabilized with oleic acid. The particles were highly crystalline and tetragonal phase. A dense ZrO(2) nanocrystal dispersion in toluene (280 mg/mL) showed a transmittance of about 90% (3 mm optical path length) in the whole visible region.

Kinetics of nitric oxide and oxygen gases on porous Y-stabilized ZrO2-based sensors.

PubMed

Killa, Sajin; Cui, Ling; Murray, Erica P; Mainardi, Daniela S

2013-08-16

Using impedance spectroscopy the electrical response of sensors with various porous Y-stabilized ZrO2 (YSZ) microstructures was measured for gas concentrations containing 0-100 ppm NO with 10.5%O2 at temperatures ranging from 600-700 °C. The impedance response increased substantially as the sensor porosity increased from 46%-50%. Activation energies calculated based on data from the impedance measurements increased in magnitude (97.4-104.9 kJ/mol for 100 ppm NO) with respect to increasing YSZ porosity. Analysis of the oxygen partial pressure dependence of the sensors suggested that dissociative adsorption was the dominant rate limiting. The PWC/DNP theory level was used to investigate the gas-phase energy barrier of the 2NO+O2 → 2NO2 reaction on a 56-atom YSZ/Au model cluster using Density Functional Theory and Linear Synchronous Transit/Quadratic Synchronous Transit calculations. The reaction path shows oxygen surface reactions that begin with NO association with adsorbed O2 on a Zr surface site, followed by O2 dissociative adsorption, atomic oxygen diffusion, and further NO2 formation. The free energy barrier was calculated to be 181.7 kJ/mol at PWC/DNP. A qualitative comparison with the extrapolated data at 62% ± 2% porosity representing the YSZ model cluster indicates that the calculated barriers are in reasonable agreement with experiments, especially when the RPBE functional is used.

Chemical Stability and Biological Properties of Plasma-Sprayed CaO-SiO2-ZrO2 Coatings

NASA Astrophysics Data System (ADS)

Liang, Ying; Xie, Youtao; Ji, Heng; Huang, Liping; Zheng, Xuebin

2010-12-01

In this work, calcia-stabilized zirconia powders were coated by silica derived from tetraethoxysilane (TEOS) hydrolysis. After calcining at 1400 °C, decalcification of calcia-stabilized zirconia by silica occurred and powders composed of Ca2SiO4, ZrO2, and CaZrO3 were prepared. We produced three kinds of powders with different Ca2SiO4 contents [20 wt.% (denoted as CZS2), 40 wt.% (denoted as CZS4), and 60 wt.% (denoted as CZS6)]. The obtained powders were sprayed onto Ti-6Al-4V substrates using atmospheric plasma spraying. The microstructure of the powders and coatings were analyzed. The dissolution rates of the coatings were assessed by monitoring the ions release and mass losses after immersion in Tris-HCl buffer solution. Results showed that the chemical stability of the coatings were significantly improved compared with pure calcium silicate coatings, and increased with the increase of Zr contents. The CZS4 coating showed not only good apatite-formation ability in simulated body fluid, but also well attachment and proliferation capability for the canine bone marrow stem cells. Results presented here indicate that plasma-sprayed CZS4 coating has medium dissolution rate and good biological properties, suggesting its potential use as bone implants.

Application of the method of images on electrostatic phenomena in aqueous Al2O3 and ZrO2 suspensions.

PubMed

Cordelair, Jens; Greil, Peter

2003-09-15

A new solution for the Poisson equation for the diffuse part of the double layer around spherical particles will be presented. The numerical results are compared with the solution of the well-known DLVO theory. The range of the diffuse layer differs considerably in the two theories. Also, the inconsistent representation of the surface and diffuse layer charge in the DLVO theory do not occur in the new theory. Experimental zeta potential measurements were used to determine the charge of colloidal Al2O3 and ZrO2 particles. It is shown that the calculated charge can be interpreted as a superposition of independent H+ and OH- adsorption isotherms. The corresponding Langmuir adsorption isotherms are taken to model the zeta potential dependence on pH. In the vicinity of the isoelectric point the model fits well with the experimental data, but at higher ion concentrations considerable deviations occur. The deviations are discussed. Furthermore, the numerical results for the run of the potential in the diffuse part of the double layer were used to determine the electrostatic interaction potential between the particles in correlation with the zeta potential measurements. The corresponding total interaction potentials, including the van der Waals attraction, were taken to calculate the coagulation half-life for a suspension with a particle loading of 2 vol%. It is shown that stability against coagulation is maintained for Al2O3 particles in the pH region between 3.3 and 7 and for ZrO2 only around pH 5. Stability against flocculation can be achieved in the pH regime between 4.5 and 7 for Al2O3, while the examined ZrO2 particles are not stable against flocculation in aqueous suspensions.

The affects of doping Eu 3+ on structures and morphology of ZrO 2 nanocrystals

NASA Astrophysics Data System (ADS)

Yu, Lixin; Liu, Hai; Nogami, Masayuki

2010-07-01

The ZrO 2 and ZrO 2:Eu 3+ nanocrystals (NCs) were prepared by a hydrothermal method. The samples were sintered at different temperatures (500, 800 and 1100 °C). The results indicate that the Eu 3+ ions affect not only the structures of hosts (ZrO 2), but also the morphology of hosts. The shape of ZrO 2:Eu 3+ NCs heated at 1100 °C is the one-dimensional nanorod, while is the zero-dimensional nanoparticle for pure ZrO 2 samples sintered at the same temperature. The excitation and emission spectra of ZrO 2:Eu 3+ NCs were studied. In excitation spectra, the charge transfer band of Eu 3+ in ZrO 2 NCs heated at 1100 °C evidently blue-shifts in comparison with the NCs calcined at 500 and 800 °C. The relative intensity of 5D-7F transitions of Eu 3+ ions and color chromaticity for nanorods are increased in comparison with the nanoparticles.

Thermodynamic Database for the NdO(1.5)-YO(1.5)-YbO(1.5)-ScO(1.5)-ZrO2 System

NASA Technical Reports Server (NTRS)

Jacobson, Nathan S.; Copland, Evan H.; Kaufman, Larry

2001-01-01

A database for YO(1.5)-NdO(1.5)-YbO(1.5)-ScO(1.5)-ZrO2 for ThermoCalc (ThermoCalc AB, Stockholm, Sweden) has been developed. The basis of this work is the YO(1.5)-ZrO2 assessment by Y. Du, Z. Jin, and P. Huang, 'Thermodynamic Assessment of the ZrO2-YO(1.5) System'. Experimentally only the YO(1.5)-ZrO2 system has been well-studied. All other systems are only approximately known. The major simplification in this work is the treatment of each single cation unit as a component. The pure liquid oxides are taken as reference states and two term lattice stability descriptions are used for each of the components. The limited experimental phase diagrams are reproduced.

Effect of TiO2, ZrO2, and TiO2-ZrO2 on the performance of CuO-ZnO catalyst for CO2 hydrogenation to methanol

NASA Astrophysics Data System (ADS)

Xiao, Jie; Mao, Dongsen; Guo, Xiaoming; Yu, Jun

2015-05-01

The influence of TiO2, ZrO2, and TiO2-ZrO2 mixed oxide on the catalytic performance of CuO-ZnO catalyst in the methanol synthesis from CO2 hydrogenation was studied. The catalysts were prepared by oxalate co-precipitation method and characterized by TGA, N2 adsorption, XRD, reactive N2O adsorption, XPS, H2-TPR, H2-TPD, and CO2-TPD techniques. Characterization results reveal that all the additives improve the CuO dispersion in the catalyst body and increase the Cu surface area and adsorption capacities of CO2 and H2. The results of catalytic test reveal that the additives increase both the CO2 conversion and methanol selectivity, and TiO2-ZrO2 mixed oxide is more effective than single components of TiO2 or ZrO2. Moreover, the activity of methanol synthesis is correlated directly with CO2 adsorption capacity over the catalysts.

The new insight into the structure-activity relation of Pd/CeO2-ZrO2-Nd2O3 catalysts by Raman, in situ DRIFTS and XRD Rietveld analysis.

PubMed

Yang, X; Yang, L; Lin, J; Zhou, R

2016-01-28

Pd/CeO2-ZrO2-Nd2O3 (CZN) catalysts with different CeO2/ZrO2 molar ratios were synthesized and have been characterized by multiple techniques, e.g. XRD in combination with Rietveld refinement, UV-Raman, XPS and in situ DRIFTS. The XRD pattern of CZN with CeO2/ZrO2 molar ratios ≥1/2 can be indexed satisfactorily to the fluorite structure with a space group Fm3̄m, while the XRD patterns of CZ12 only display diffraction peaks of the tetragonal phase (S.G. P42/nmc). Nd addition can effectively stabilize the cubic structure of the CZN support and increase the enrichment of defect sites on the surface, which may be related to the better catalytic activity of Pd/CZN12 catalysts compared with Pd/CZ12. The presence of moderate ZrO2 can increase the concentration of O* active species, leading to accelerate the formation of nitrate species and thus enhance the catalytic activity of NOx and HC elimination. The Pd-dispersion decreases with the increasing Zr content, leading to the decreased CO catalytic activity, especially for the aged catalysts. The change regularity of the OSC value is almost the same with the in situ dynamic operational window, demonstrating that the in situ dynamic operational window is basically affected by the OSC value.

(Zr,Ti)O2 interface structure in ZrO2-TiO2 nanolaminates with ultrathin periodicity

NASA Astrophysics Data System (ADS)

Aita, C. R.; DeLoach, J. D.; Yakovlev, V. V.

2002-07-01

A mixed cation interfacial structure in ZrO2-TiO2 nanolaminate films with ultrathin bilayer periodicity grown by sputter deposition at 297 K was identified by x-ray diffraction and nonresonant Raman spectroscopy. This structure consists of an amorphous phase at a ZrO2-on-TiO2 bilayer interface, followed by an extensive crystalline monoclinic (Zr,Ti)O2 solid solution predicted by Vegard's law. Monoclinic (Zr,Ti)O2 has previously been reported only once, in bulk powder of a single composition (ZrTiO4) at high pressure. Its stabilization in the nanolaminates is explained by the Gibbs-Thomson effect. This complex interfacial structure is shown to be a means of accommodating chemical mixing in the absence of a driving force for heteroepitaxy.

Corrosion Protection of Copper Using Al2O3, TiO2, ZnO, HfO2, and ZrO2 Atomic Layer Deposition.

PubMed

Daubert, James S; Hill, Grant T; Gotsch, Hannah N; Gremaud, Antoine P; Ovental, Jennifer S; Williams, Philip S; Oldham, Christopher J; Parsons, Gregory N

2017-02-01

Atomic layer deposition (ALD) is a viable means to add corrosion protection to copper metal. Ultrathin films of Al 2 O 3 , TiO 2 , ZnO, HfO 2 , and ZrO 2 were deposited on copper metal using ALD, and their corrosion protection properties were measured using electrochemical impedance spectroscopy (EIS) and linear sweep voltammetry (LSV). Analysis of ∼50 nm thick films of each metal oxide demonstrated low electrochemical porosity and provided enhanced corrosion protection from aqueous NaCl solution. The surface pretreatment and roughness was found to affect the extent of the corrosion protection. Films of Al 2 O 3 or HfO 2 provided the highest level of initial corrosion protection, but films of HfO 2 exhibited the best coating quality after extended exposure. This is the first reported instance of using ultrathin films of HfO 2 or ZrO 2 produced with ALD for corrosion protection, and both are promising materials for corrosion protection.

ZrO2/MoS2 heterojunction photocatalysts for efficient photocatalytic degradation of methyl orange

NASA Astrophysics Data System (ADS)

Prabhakar Vattikuti, Surya Veerendra; Byon, Chan; Reddy, Chandragiri Venkata

2016-10-01

We report a simple solution-chemistry approach for the synthesis of ZrO2/MoS2 hybrid photocatalysts, which contain MoS2 as a cocatalyst. The material is usually obtained by a wet chemical method using ZrO(NO3)2 or (NH4)6Mo7O24·4H2O and C8H6S as precursors. The structural features of obtained materials were characterized by X-ray diffraction (XRD), highresolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), thermal analysis (TG-DTA), N2 adsorption-desorption, and photoluminescence (PL). The influence on the photocatalytic activity of the MoS2 cocatalyst concentration with ZrO2 nanoparticles was studied. The MZr-2 hybrid sample had the highest photocatalytic activity for the degradation of methyl orange (MO), which was 8.45 times higher than that of pristine ZrO2 ascribed to high specific surface area and absorbance efficiency. Recycling experiments revealed that the reusability of the MZr-2 hybrid was due to the low photocorrosive effect and good catalytic stability. PL spectra confirmed the electronic interaction between ZrO2 and MoS2. The photoinduced electrons could be easily transferred from CB of ZrO2 to the MoS2 cocatalyst, which facilitate effective charge separation and enhanced the photocatalytic degradation in the UV region. A photocatalytic mechanism is proposed. It is believed that the ZrO2/MoS2 hybrid structure has promise as a photocatalyst with low cost and high efficiency for photoreactions.

Thermodynamic Modeling of the YO(l.5)-ZrO2 System

NASA Technical Reports Server (NTRS)

Jacobson, Nathan S.; Liu, Zi-Kui; Kaufman, Larry; Zhang, Fan

2003-01-01

The YO1.5-ZrO2 system consists of five solid solutions, one liquid solution, and one intermediate compound. A thermodynamic description of this system is developed, which allows calculation of the phase diagram and thermodynamic properties. Two different solution models are used-a neutral species model with YO1.5 and ZrO2 as the components and a charged species model with Y(+3), Zr(+4), O(-2), and vacancies as components. For each model, regular and sub-regular solution parameters are derived fiom selected equilibrium phase and thermodynamic data.

ZrO2-modified mesoporous nanocrystalline TiO2-xNx as efficient visible light photocatalysts.

PubMed

Wang, Xinchen; Yu, Jimmy C; Chen, Yilin; Wu, Ling; Fu, Xianzhi

2006-04-01

Mesoporous nanocrystalline TiO2-xNx and TiO2-xNx/ZrO2 visible-light photocatalysts have been prepared by a sol-gel method. The photocatalysts were characterized by XRD, N2 adsorption-desorption, TEM, XPS, UV/Vis, and IR spectroscopy. The photocatalytic activity of the samples was evaluated by the decomposition of ethylene in air under visible light (lambda > 450 nm) illumination. Results revealed that nitrogen was doped into the lattice of TiO2 by the thermal treatment of NH3-adsorbed TiO2 hydrous gels, converting the TiO2 into a visible-light responsive catalyst. The introduction of ZrO2 into TiO2-xNx considerably inhibits the undesirable crystal growth during calcination. Consequently, the ZrO2-modified TiO2-xNx displays higher porosity, higher specific surface area, and an improved thermal stability over the corresponding unmodified TiO2-xNx samples.

Unctuous ZrO2 nanoparticles with improved functional attributes as lubricant additives

NASA Astrophysics Data System (ADS)

Espina Casado, Jorge; Fernández González, Alfonso; José del Reguero Huerga, Ángel; Rodríguez-Solla, Humberto; Díaz-García, Marta Elena; Badía-Laíño, Rosana

2017-12-01

One of the main drawbacks in the application of metal-oxide nanoparticles as lubricant additives is their poor stability in organic media, despite the good anti-wear, friction-reducing and high-load capacity properties described for these materials. In this work, we present a novel procedure to chemically cap the surface of ZrO2 nanoparticles (ZrO2NPs) with long hydrocarbon chains in order to obtain stable dispersions of ZrO2NPs in non-aqueous media without disrupting their attributes as lubricant additives. C-8, C-10 and C-16 saturated flexible chains were attached to the ZrO2NP surface and their physical and chemical characterization was performed by transmission electron microscopy, thermogravimetric analysis, attenuated total reflectance Fourier transform infrared spectroscopy, x-ray photoelectron spectroscopy and solid-state nuclear magnetic resonance. The dispersion stability of the modified ZrO2NPs in non-aqueous media was studied using static multiple light scattering. Tribological tests demonstrated that dispersions of the long-chain capped ZrO2NPs in base lubricating oils exhibited low friction coefficients and improved the anti-wear properties of the base oil when compared with the raw lubricating oil.

Comparing the Thermodynamic Behaviour of Al(1)+ZrO2(s) to Al(1)+Al2O3(s)

NASA Technical Reports Server (NTRS)

Copland, Evan

2004-01-01

In an effort to better determine the thermodynamic properties of Al(g) and Al2O(g). the vapor in equilibrium with Al(l)+ZrO2(s) was compared to the vapor in equilibrium with Al(l)+Al2O3(s) over temperature range 1197-to-1509K. The comparison was made directly by Knudsen effusion-cell mass spectrometry with an instrument configured for a multiple effusion-cell vapor source (multi-cell KEMS). Second law enthalpies of vaporization of Al(g) and Al2O(g) together with activity measurements show that Al(l)+ZrO2(s) is thermodynamically equivalent to Al(l)+Al2O3(s), indicating Al(l) remained pure and Al2O3(s) was present in the ZrO2-cell. Subsequent observation of the Al(l)/ZrO2 and vapor/ZrO2 interfaces revealed a thin Al2O3-layer had formed, separating the ZrO2-cell from Al(l) and Al(g)+Al2O(g), effectively transforming it into an Al2O3 effusion-cell. This behavior agrees with recent observations made for Beta-NiAl(Pt) alloys measured in ZrO2 effusion-cell.

The behavior of ZrO2/20%Y2O3 and Al2O3 coatings deposited on aluminum alloys at high temperature regime

NASA Astrophysics Data System (ADS)

Pintilei, G. L.; Crismaru, V. I.; Abrudeanu, M.; Munteanu, C.; Baciu, E. R.; Istrate, B.; Basescu, N.

2015-10-01

Aluminum alloy present numerous advantages like lightness, high specific strength and diversity which recommend them to a high number of applications from different fields. In extreme environments the protection of aluminum alloys is difficult and requires a high number of requirements like high temperature resistance, thermal fatigue resistance, corrosion fatigue resistance and galvanic corrosion resistance. To obtain these characteristics coatings can be applied to the surfaces so they can enhance the mechanical and chemical properties of the parts. In this paper two coatings were considered for deposition on an AA2024 aluminum alloy, ZrO2/20%Y2O3 and Al2O3. To obtain a better adherence of the coating to the base material an additional bond layer of NiCr is used. Both the coatings and bond layer were deposited by atmospheric plasma spraying on the samples. The samples were subjected to a temperature of 500 °C and after that slowly cooled to room temperature. The samples were analyzed by electron microscopy and X-ray diffraction to determine the morphological and phase changes that occurred during the temperature exposure. To determine the stress level in the parts due to thermal expansion a finite element analysis was performed in the same conditions as the tests.

The synthesis of ZrO2-Y2O3 ceramic fibers by the method of impregnation of viscous threads

NASA Astrophysics Data System (ADS)

Titova, S. M.; Obabkov, N. V.; Zakirova, A. F.; Zakirov, I. F.; Dokuchaev, V. S.; Shak, A. V.

2017-09-01

The possibility of synthesis of ZrO2-Y2O3 oxide fibers and their applicatiuon for reinforcing porous ceramics of the same composition was investigated. Ceramic fibers were obtained by impregnating viscose strings with solutions of zirconyl and yttrium nitrates. The method allows synthesis of the fibers with a diameter of 400 µm and length of 5 to 20 mm. The strength of the synthesized fibers was determined. The maximum tensile strength (132.45 MPa) was demonstrated by fibers obtained with a working solution concentration of 500 g oxides/L. Repeated impregnation of the viscose yarn led to an increase in the strength of the fibers to 205 MPa. Ceramic fibers can be used as reinforcing elements of oxide ceramics. The bending strength of the reinforced ceramics was 3 MPa. After 10 cycles of thermal cycling (heating to 1100 °C and cooling in water) the bending strength was reduced to 1 MPa.

The photoelectronic behaviors of MoO3-loaded ZrO2/carbon cluster nanocomposite materials

NASA Astrophysics Data System (ADS)

Matsui, H.; Ishiko, A.; Karuppuchamy, S.; Hassan, M. A.; Yoshihara, M.

2012-03-01

A novel nano-sized ZrO2/carbon cluster composite materials (Ic's) were successfully obtained by the calcination of ZrCl4/starch complexes I's under an argon atmosphere. Pt- and/or MoO3-loaded ZrO2/carbon clusters composite materials were also prepared by doping Pt and/or MoO3 particles on the surface of Ic's. The surface characterization of the composite materials was carried out using transmission electron microscopy (TEM). The TEM observation of the materials showed the presence of particles with the diameters of a few nanometers, possibly Pt particles, and of 50-100 nm, possibly MoO3 particles, in the matrix. Pt- and/or MoO3-loaded ZrO2/carbon cluster composite materials show the efficient photocatalytic activity under visible light irradiation.

A study of Pd/SO4/ZrO2/Al2O3 catalysts in n-hexane isomerization

NASA Astrophysics Data System (ADS)

Dzhikiya, O. V.; Smolikov, M. D.; Kazantsev, K. V.; Yablokova, S. S.; Kireeva, T. V.; Paukshtis, E. A.; Gulyaeva, T. I.; Belyi, A. S.

2017-08-01

The effect of palladium concentration in a range from 0.02 to 1.6 wt.% on characteristics of n-hexane isomerization was studied. The (O2-Hchem) titration and O2 chemisorption study revealed that palladium in Pd/SO4/ZrO2/Al2O3 systems adsorbs hydrogen in a ratio H/Pds = 1.13-1.65 at./at. Investigation of the charge state of the metal by IR spectroscopy of adsorbed CO showed the presence of both the metallic (Pd0) and charged palladium species. Pd/SO4/ZrO2/Al2O3 catalysts with charged palladium atoms exhibit high activity and selectivity in n-hexane isomerization.

The influence of ZrO2/20%Y2O3 and Al2O3 deposited coatings to the behavior of an aluminum alloy subjected to mechanical shock

NASA Astrophysics Data System (ADS)

Pintilei, G. L.; Crismaru, V. I.; Abrudeanu, M.; Munteanu, C.; Luca, D.; Istrate, B.

2015-10-01

Aluminum alloys are used in the aerospace industry due to their good mechanical properties and their low density compared with the density of steels. Usually the parts made of aluminum alloys contribute to the structural frame of aircrafts and they must withstand static and variable mechanical loads and also mechanical loads applied in a very short time which determine different phenomenon's in the material behavior then static or fatigue loads. This paper analysis the resilience of a 2024 aluminum alloy subjected to shock loads and the way how a coating can improve its behavior. For improving the behavior two coatings were considered: Al2O3 with 99.5% purity and ZrO2/20%Y2O3. The coatings were deposited on the base material by plasma spraying. The samples with and without coating were subject to mechanical shock to determine the resilience of the materials and the cracks propagation was investigated using SEM analysis. To highlight the physical phenomenon's that appear in the samples during the mechanical shock, explicit finite element analysis were done using Ansys 14.5 software.

Ethanol dehydrogenation on copper catalysts with ytterbium stabilized tetragonal ZrO2 support

NASA Astrophysics Data System (ADS)

Chuklina, S. G.; Pylinina, A. I.; Podzorova, L. I.; Mikhailina, N. A.; Mikhalenko, I. I.

2016-12-01

The physicochemical and catalytic properties of Cu-containing crystalline zirconia, obtained via sol-gel synthesis in the presence of Yb3+ ions and polyvinylpyrrolidone, are studied. DTG/DSC, TEM, XRD and BET methods are used to analyze the crystallization, texture, phase uniformity, surface and porosity of ZrO2 nanopowders. It is shown that increasing the copper content (1, 3, and 5 wt % from ZrO2) raises the dehydrogenation activity in the temperature range of 100-400°C and lowers the activation energy of acetaldehyde formation. It is found that the activity of all Cu/ t-ZrO2 catalysts grows under the effects of the reaction medium, due to the migration and redispersion of copper.

Effect of SiO 2-ZrO 2 supports prepared by a grafting method on hydrogen production by steam reforming of liquefied natural gas over Ni/SiO 2-ZrO 2 catalysts

NASA Astrophysics Data System (ADS)

Seo, Jeong Gil; Youn, Min Hye; Song, In Kyu

SiO 2-ZrO 2 supports with various zirconium contents are prepared by grafting a zirconium precursor onto the surface of commercial Carbosil silica. Ni(20 wt.%)/SiO 2-ZrO 2 catalysts are then prepared by an impregnation method, and are applied to hydrogen production by steam reforming of liquefied natural gas (LNG). The effect of SiO 2-ZrO 2 supports on the performance of the Ni(20 wt.%)/SiO 2-ZrO 2 catalysts is investigated. SiO 2-ZrO 2 prepared by a grafting method serves as an efficient support for the nickel catalyst in the steam reforming of LNG. Zirconia enhances the resistance of silica to steam significantly and increases the interaction between nickel and the support, and furthermore, prevents the growth of nickel oxide species during the calcination process through the formation of a ZrO 2-SiO 2 composite structure. The crystalline structures and catalytic activities of the Ni(20 wt.%)/SiO 2-ZrO 2 catalysts are strongly influenced by the amount of zirconium grafted. The conversion of LNG and the yield of hydrogen show volcano-shaped curves with respect to zirconium content. Among the catalysts tested, the Ni(20 wt.%)/SiO 2-ZrO 2 (Zr/Si = 0.54) sample shows the best catalytic performance in terms of both LNG conversion and hydrogen yield. The well-developed and pure tetragonal phase of ZrO 2-SiO 2 (Zr/Si = 0.54) appears to play an important role in the adsorption of steam and subsequent spillover of steam from the support to the active nickel. The small particle size of the metallic nickel in the Ni(20 wt.%)/SiO 2-ZrO 2 (Zr/Si = 0.54) catalyst is also responsible for its high performance.

Oxidant effect of La(NO3)3·6H2O solution on the crystalline characteristics of nanocrystalline ZrO2 films grown by atomic layer deposition

NASA Astrophysics Data System (ADS)

Oh, Nam Khen; Kim, Jin-Tae; Kang, Goru; An, Jong-Ki; Nam, Minwoo; Kim, So Yeon; Park, In-Sung; Yun, Ju-Young

2017-02-01

Nanocrystalline ZrO2 films were synthesized by atomic layer deposition method using CpZr[N(CH3)2]3 (Cp = C5H5) as the metal precursor and La(NO3)3·6H2O solution as the oxygen source. La element in the deposited ZrO2 films could not be detected as its content was below the resolution limit of the X-ray photoelectron spectroscopy. The alternative introduction of La(NO3)3·6H2O solution to conventionally used H2O as the oxidant effectively altered the crystalline structure, grain size, and surface roughness of the grown ZrO2 films. Specifically, the crystalline structure of the ZrO2 film changed from a mixture of tetragonal and monoclinic phases to monoclinic phase. The average grain size also increased, and the resulting film surface became rougher. The average grain sizes of the ZrO2 films prepared from La(NO3)3·6H2O solution at concentrations of 10, 20, 30, and 40% were 280, 256, 208, and 200 nm, respectively, whereas that prepared using H2O oxidant was 142 nm. However, the concentration of La(NO3)3·6H2O solution minimally influenced the crystalline characteristics of the nanocrystalline ZrO2 films i.e., the crystalline structure, grain size, and surface roughness except for crystallite size.

Efficient removal of arsenite through photocatalytic oxidation and adsorption by ZrO2-Fe3O4 magnetic nanoparticles

NASA Astrophysics Data System (ADS)

Sun, Tianyi; Zhao, Zhiwei; Liang, Zhijie; Liu, Jie; Shi, Wenxin; Cui, Fuyi

2017-09-01

Bifunctional ZrO2-Fe3O4 magnetic nanoparticles were synthesized and characterized, to remove As(III) through photocatalyic oxidation and adsorption. With a saturation magnetization of 27.39 emu/g, ZrO2-Fe3O4 nanoparticles with size of 10-30 nm could be easily separated from solutions with a simple magnetic process. Under UV light, As(III) could be completely oxidized to less toxic As(V) by ZrO2-Fe3O4 nanoparticles within 40 min in the photocatalytic reaction. Simultaneously, As(V) could be adsorbed onto the surface of nanoparticles with high efficiency. The adsorption of As(V) was well fitted by the pseudo-second-order model and the Freundlich isotherm model, respectively, and the maximum adsorption capacities of the nanoparticles was 133.48 mg/g at pH 7.0. As(III) could be effectively removed by ZrO2-Fe3O4 nanoparticles at initial pH range from 4 to 8. Among all the common coexisting ions investigated, except for chloride and sulfate, carbonate, silicate and phosphate decreased the As(III) removal by competing with arsenic species for adsorption sites. The synthesized magnetic ZrO2-Fe3O4 combined the photocatalytic oxidation property of ZrO2 and the high adsorption capacity of both ZrO2 and Fe3O4, which make it have significant potential applications in the As(III)-contaminated water treatment.

Substitutional Cd and Cd-Oxygen Vacancy Complexes in ZrO2 and Ce-doped ZrO_2

NASA Astrophysics Data System (ADS)

Zacate, Matthew O.; Karapetrova, E.; Platzer, R.; Gardner, J. A.; Evenson, W. E.; Sommers, J. A.

1996-03-01

We are using Perturbed Angular Correlation Spectroscopy (PAC) to study oxygen vacancy (V_O) dynamics in tetragonal ZrO2 and Ce-doped ZrO_2. PAC requires a radioactive probe atom, Cd in this study, which sits substitutionally for a Zr ion. Cd is doubly-negatively charged relative to the lattice and attracts doubly-positively charged V_Os. Pure tetragonal zirconia exists only above 950 ^circC and in this temperature range, the V_Os are very mobile. Above 950 ^circC we observe V_Os rapidly hopping about the Cd allowing us to determine the VO concentration and the trapping energy. We have been Ce-doping to stabilize the tetragonal phase to lower temperature to determine the electric field gradient the Cd experiences due to a stationary V_O. As a consequence of the Ce-doping, we observe a local lattice distortion about the Cd which increases with Ce-doping.

CeO2-Y2O3-ZrO2 Membrane with Enhanced Molten Salt Corrosion Resistance for Solid Oxide Membrane (SOM) Electrolysis Process

NASA Astrophysics Data System (ADS)

Zou, Xingli; Li, Xin; Shen, Bin; Lu, Xionggang; Xu, Qian; Zhou, Zhongfu; Ding, Weizhong

2017-02-01

Innovative CeO2-Y2O3-ZrO2 membrane has been successfully developed and used in the solid oxide membrane (SOM) electrolysis process for green metallic materials production. The x mol pct ceria/(8- x) mol pct yttria-costabilized zirconia ( xCe(8- x)YSZ, x = 0, 1, 4, or 7) membranes have been fabricated and investigated as the membrane-based inert anodes to control the SOM electroreduction process in molten salt. The characteristics of these fabricated xCe(8- x)YSZ membranes including their corrosion resistances in molten salt and their degradation mechanisms have been systematically investigated and compared. The results show that the addition of ceria in the YSZ-based membrane can inhibit the depletion of yttrium during the SOM electrolysis, which thus makes the ceria-reinforced YSZ-based membranes possess enhanced corrosion resistances to molten salt. The ceria/yttria-costabilized zirconia membranes can also provide reasonable oxygen ion conductivity during electrolysis. Further investigation shows that the newly modified 4Ce4YSZ ceramic membrane has the potential to be used as novel inert SOM anode for the facile and sustainable production of metals/alloys/composites materials such as Si, Ti5Si3, TiC, and Ti5Si3/TiC from their metal oxides precursors in molten CaCl2.

Highly Stable Sr-Free Cobaltite-Based Perovskite Cathodes Directly Assembled on a Barrier-Layer-Free Y2 O3 -ZrO2 Electrolyte of Solid Oxide Fuel Cells.

PubMed

Ai, Na; Li, Na; Rickard, William D A; Cheng, Yi; Chen, Kongfa; Jiang, San Ping

2017-03-09

Direct assembly is a newly developed technique in which a cobaltite-based perovskite (CBP) cathode can be directly applied to a barrier-layer-free Y 2 O 3 -ZrO 2 (YSZ) electrolyte with no high-temperature pre-sintering steps. Solid oxide fuel cells (SOFCs) based on directly assembled CBPs such as La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3-δ show high performance initially but degrade rapidly under SOFC operation conditions at 750 °C owing to Sr segregation and accumulation at the electrode/electrolyte interface. Herein, the performance and interface of Sr-free CBPs such as LaCoO 3-δ (LC) and Sm 0.95 CoO 3-δ (SmC) and their composite cathodes directly assembled on YSZ electrolyte was studied systematically. The LC electrode underwent performance degradation, most likely owing to cation demixing and accumulation of La on the YSZ electrolyte under polarization at 500 mA cm -2 and 750 °C. However, the performance and stability of LC electrodes could be substantially enhanced by the formation of LC-gadolinium-doped ceria (GDC) composite cathodes. Replacement of La by Sm increased the cell stability, and doping of 5 % Pd to form Sm 0.95 Co 0.95 Pd 0.05 O 3-δ (SmCPd) significantly improved the electrode activity. An anode-supported YSZ-electrolyte cell with a directly assembled SmCPd-GDC composite electrode exhibited a peak power density of 1.4 W cm -2 at 750 °C, and an excellent stability at 750 °C for over 240 h. The higher stability of SmC as compared to that of LC is most likely a result of the lower reactivity of SmC with YSZ. This study demonstrates the new opportunities in the design and development of intermediate-temperature SOFCs based on the directly assembled high-performance and durable Sr-free CBP cathodes. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Selection by current compliance of negative and positive bipolar resistive switching behaviour in ZrO2-x /ZrO2 bilayer memory

NASA Astrophysics Data System (ADS)

Huang, Ruomeng; Yan, Xingzhao; Morgan, Katrina A.; Charlton, Martin D. B.; (Kees de Groot, C. H.

2017-05-01

We report here a ZrO2-x /ZrO2-based bilayer resistive switching memory with unique properties that enables the selection of the switching mode by applying different electroforming current compliances. Two opposite polarity modes, positive bipolar and negative bipolar, correspond to the switching in the ZrO2 and ZrO2-x layer, respectively. The ZrO2 layer is proved to be responsible for the negative bipolar mode which is also observed in a ZrO2 single layer device. The oxygen deficient ZrO2-x layer plays the dominant role in the positive bipolar mode, which is exclusive to the bilayer memory. A systematic investigation of the ZrO2-x composition in the bilayer memory suggests that ZrO1.8 layer demonstrates optimum switching performance with low switching voltage, narrow switching voltage distribution and good cycling endurance. An excess of oxygen vacancies, beyond this composition, leads to a deterioration of switching properties. The formation and dissolution of the oxygen vacancy filament model has been proposed to explain both polarity switching behaviours and the improved properties in the bilayer positive bipolar mode are attributed to the confined oxygen vacancy filament size within the ZrO2-x layer.

Conductive atomic force microscopy study of the photoexcitation effect on resistive switching in ZrO2(Y) films with Au nanoparticles

NASA Astrophysics Data System (ADS)

Novikov, A. S.; Filatov, D. O.; Antonov, D. A.; Antonov, I. N.; Shenina, M. E.; Gorshkov, O. N.

2018-03-01

We report on the experimental observation of the effect of optical excitation on resistive switching in ultrathin ZrO2(Y) films with single-layered arrays of Au nanoparticles. The samples were prepared by depositing nanometer-thick Au films sandwiched between two ZrO2(Y) layers by magnetron sputtering followed by annealing. Resistive switching was studied by conductive atomic force microscopy by measuring cyclic current-voltage curves of a probe-to-sample contact. The contact area was illuminated by radiation of a semiconductor laser diode with the wavelength corresponding to the plasmon resonance in an Au nanoparticle array. The enhancement of the hysteresis in cyclic current-voltage curves due to bipolar resistive switching under illumination was observed. The effect was attributed to heating of Au nanoparticles due to plasmonic optical absorption and a plasmon resonance, which enhances internal photoemission of electrons from the Fermi level in Au nanoparticles into the conduction band of ZrO2(Y). Both factors promote resistive switching in a ZrO2(Y) matrix.

Improved WO3 photocatalytic efficiency using ZrO2 and Ru for the degradation of carbofuran and ampicillin.

PubMed

Gar Alalm, Mohamed; Ookawara, Shinichi; Fukushi, Daisuke; Sato, Akira; Tawfik, Ahmed

2016-01-25

The photocatalytic degradation of carbofuran (pesticide) and ampicillin (pharmaceutical) using synthesized WO3/ZrO2 nanoparticles under simulated solar light was investigated. Transmission electron microscopy (TEM), X-ray diffraction (XRD), and Raman spectra analyses were used to characterize the prepared catalysts. The optimum ratio of WO3 to ZrO2 was determined to be 1:1 for the degradation of both contaminants. The degradation of carbofuran and ampicillin by WO3/ZrO2 after 240 min of irradiation was 100% and 96%, respectively. Ruthenium (Ru) was employed as an additive to WO3/ZrO2 to enhance the photocatalytic degradation rate. Ru/WO3/ZrO2 exhibited faster degradation rates than WO3/ZrO2. Furthermore, 100% and 97% degradation of carbofuran and ampicillin, respectively, was achieved using Ru/WO3/ZrO2 after 180 min of irradiation. The durability of the catalyst was investigated by reusing the same suspended catalyst, which achieved 92% of its initial efficiency. The photocatalytic degradation of ampicillin and carbofuran followed pseudo-first order kinetics according to the Langmuir-Hinshelwood model. Copyright © 2015 Elsevier B.V. All rights reserved.

Enhancing low-temperature activity and durability of Pd-based diesel oxidation catalysts using ZrO 2 supports

DOE PAGES

Kim, Mi -Young; Kyriakidou, Eleni A.; Choi, Jae -Soon; ...

2016-01-18

In this study, we investigated the impact of ZrO 2 on the performance of palladium-based oxidation catalysts with respect to low-temperature activity, hydrothermal stability, and sulfur tolerance. Pd supported on ZrO 2 and SiO 2 were synthesized for a comparative study. Additionally, in an attempt to maximize the ZrO 2 surface area and improve sulfur tolerance, a Pd support with ZrO 2-dispersed onto SiO 2 was studied. The physicochemical properties of the catalysts were examined using ICP, N 2 sorption, XRD, SEM, TEM, and NH 3-, CO 2-, and NO x-TPD. The activity of the Pd catalysts were measured frommore » 60 to 600 °C in a flow of 4000 ppm CO, 500 ppm NO, 1000 ppm C 3H 6, 4% O 2, 5% H 2O, and Ar balance. The Pd catalysts were evaluated in fresh, sulfated, and hydrothermally aged states. Overall, the ZrO 2-containing catalysts showed considerably higher CO and C 3H 6 oxidation activity than Pd/SiO 2 under the reaction conditions studied.« less

Effects of SnO2, WO3, and ZrO2 addition on the magnetic and mechanical properties of NiCuZn ferrites

NASA Astrophysics Data System (ADS)

Wang, Sea-Fue; Yang, Hsiao-Ching; Hsu, Yung-Fu; Hsieh, Chung-Kai

2015-01-01

In this study, the effects of SnO2, WO3 and ZrO2 addition at levels up to 5 wt% on the magnetic and mechanical properties of Ni0.5Cu0.3Zn0.2Fe2O4 ceramics were investigated. Only Ni0.5Cu0.3Zn0.2Fe2O4 ceramic with a SnO2 addition of ≥3.5 wt% required a densification temperature of 1150 °C, while the others reached maximum densification at 1075 °C. All samples revealed a pure spinel phase and a uniform microstructure, except for the Ni0.5Cu0.3Zn0.2Fe2O4 ceramic with the WO3 addition, which showed an exaggerated grain growth accompanied with a small amount of needle-shaped Cu0.85Zn0.15WO4 second phase. The fracture mode in the pure Ni0.5Cu0.3Zn0.2Fe2O4 ceramic revealed a transgranular phase, as the CuO second phase increased the grain boundary strength; the Ni0.5Cu0.3Zn0.2Fe2O4 ceramics sintered with 5 wt% additives showed an intergranular phase. The Vickers hardness and the bending strength of the Ni0.5Cu0.3Zn0.2Fe2O4 ceramic were 733.6 and 62.0 MPa, respectively. The Vickers hardness of the ferrite with added SnO2 or ZrO2 showed only a slight improvement, while an apparent change (832.7) was observed with the addition of 5.0 wt% WO3. The bending strength of the ferrite was optimized at 75.7 MPa with 2.0 wt% SnO2 and at 90.5 MPa with 3.5 wt% ZrO2, while that of the ferrite sintered with WO3 added dropped gradually from 62.0 to 47.7 MPa as the amount of WO3 was increased from 0 to 5.0 wt% due to the non-uniform microstructure. The pure Ni0.5Cu0.3Zn0.2Fe2O4 ceramic sintered at 1075 °C had an initial permeability of 356.9 and a quality factor of 71.2. The addition of ZrO2 led to a significant increase in the initial permeability (588.4 at 5.0 wt% ZrO2), but a slight decline in the quality factor (56.6 at 5.0 wt% ZrO2).

Influence of ZrO2, SiO2, Al2O3 and TiO2 nanoparticles on maize seed germination under different growth conditions.

PubMed

Karunakaran, Gopalu; Suriyaprabha, Rangaraj; Rajendran, Venkatachalam; Kannan, Narayanasamy

2016-08-01

The focus of this investigation is to evaluate the phytotoxicity of selected metal oxide nanoparticles and microparticles as a function of maize seed germination and root elongation under different growth conditions (Petri plate, cotton and soil). The results of seed germination and root elongation experiments reveal that all the growth conditions show almost similar results. Alumina (Al2O3) and titania (TiO2) nanoparticles significantly reduce the germination percentage, whereas silica (SiO2) nanoparticles and microparticles enhance the same. The results of nanoparticles and microparticles of zirconia (ZrO2) are found to be same as those of controls. Root elongation is enhanced by SiO2 nanoparticles and microparticles treatment, whereas inhibition is observed with Al2O3 and TiO2 nanoparticles and microparticles. The X-ray fluorescence spectrometry data of the treated and control seed samples show that seeds uptake SiO2 particles to a greater extent followed by TiO2, Al2O3 and ZrO2. In addition, the uptake of nanoparticles is found to be greater than that of microparticles. Thus, the tested metal oxides penetrated seeds at the nanoscale as compared with the microscale. This study clarifies phytotoxicity of nanoparticles treated in different growth substrates and highlights the impact of nanoparticles on environment and agricultural systems.

A stable solid acid material: Sulfated ZrO2 dispersed on alumina nanotubes

NASA Astrophysics Data System (ADS)

Feng, Yu; Jiaqi, Chen; Xu, Wang; Rui-Feng, Li

2017-02-01

A tubular solid acid catalyst was designed by loading sulfated zirconia into γ-Al2O3 nanotubes using the method of stepwise deposition. The XRD, N2 adsorption-desorption characterization demonstrated that introducing alumina nanotube and SO4 2- anions have played an important role in stabilizing the metastable tetragonal ZrO2 phase, and the sulfated zirconia on the surface of the γ-Al2O3 nanotube has high dispersion and stability. The catalyst reused repeatedly possesses large amounts of acid sites and good acidity, exhibiting high catalytic activity and stability for isopropylbenzene cracking.

Phenol-photodegradation on ZrO2. Enhancement by semiconductors.

PubMed

Karunakaran, C; Dhanalakshmi, R; Gomathisankar, P

2012-06-15

On illumination with light of wavelength 365 nm phenol undergoes degradation on the surface of ZrO(2). The rate of degradation enhances linearly with the concentration of phenol and also the light intensity but decreases with increase of pH. The photonic efficiency of degradation is higher with illumination at 254 nm than with 365 nm. The diffuse reflectance spectral study suggests phenol-sensitized activation of ZrO(2) with 365 nm light. TiO(2), Fe(2)O(3), CuO, ZnO, ZnS, Nb(2)O(5) and CdO particles enhance the photodegradation on ZrO(2), indicating inter-particle charge-transfer. Determination of size of the particles under suspension, by light scattering technique, shows agglomeration of particles supporting the proposition of charge-transfer between particles. Copyright © 2012 Elsevier B.V. All rights reserved.

Improved conversion efficiency of dye sensitized solar cell using Zn doped TiO2-ZrO2 nanocomposite

NASA Astrophysics Data System (ADS)

Tomar, Laxmi J.; Bhatt, Piyush J.; Desai, Rahul K.; Chakrabarty, B. S.; Panchal, C. J.

2016-05-01

TiO2-ZrO2 and Zn doped TiO2-ZrO2 nanocomposites were prepared by hydrothermal method for dye sensitized solar cell (DSSC) application. The structural and optical properties were investigated by X -ray diffraction (XRD) and UV-Visible spectroscopy respectively. XRD results revealed the formation of material in nano size. The average crystallite size is 22.32 nm, 17.41 nm and 6.31 nm for TiO2, TiO2-ZrO2 and Zn doped TiO2-ZrO2 nanocomposites respectively. The optical bandgap varies from 2.04 eV to 3.75 eV. Dye sensitized solar cells were fabricated using the prepared material. Pomegranate juice was used as a sensitizer and graphite coated conducting glass plate was used as counter electrode. The I - V characteristics were recorded to measure photo response of DSSC. Photovoltaic parameter like open circuit voltage, power conversion efficiency, and fill factor were evaluated for fabricated solar cell. The power conversion efficiency of DSSC fabricated with TiO2, TiO2-ZrO2 and Zn doped TiO2-ZrO2 nanocomposites were found 0.71%, 1.97% and 4.58% respectively.

ZrO2:Sm3+ nanophosphor: synthesis, Rietveld refinement, optical and thermoluminescent properties

NASA Astrophysics Data System (ADS)

Ponkumar, S.; Janaki, K.; Prakashbabu, D.; Ramalingam, H. B.; Munirathnam, K.; Sreekanth, T. V. M.; Dhoble, S. J.

2018-02-01

We have synthesized undoped and Sm3+ ions doped ZrO2 nanophosphors by solution combustion method. These nanophosphors crystallized in cubic structure. Rietveld refinement of the samples was performed to estimate lattice parameters. Spherical particles with the sizes of 10-25 nm were observed by transmission electron microscopy. Photoluminescence and thermoluminescence (TL) properties of samples were investigated. Under 400 nm excitation, the nanophosphors have intense red emission at 600 nm. The color coordinates (0.67, 0.33) were located in the red region of CIE diagram. TL properties of nanophosphors were studied by exposing the samples to γ-rays. 5 mol% Sm3+ doped ZrO2 nanophosphor has shown maximum TL intensity after γ-irradiation. To test suitability of the nanophosphors for practical application in dosimetry, the 5 mol% Sm3+ doped ZrO2 sample was irradiated by 14 MeV electron beam in various electron fluence ranging from 100 to 900 Gy and their TL response was recorded.

Electrical characteristics of SiO2/ZrO2 hybrid tunnel barrier for charge trap flash memory

NASA Astrophysics Data System (ADS)

Choi, Jaeho; Bae, Juhyun; Ahn, Jaeyoung; Hwang, Kihyun; Chung, Ilsub

2017-08-01

In this paper, we investigate the electrical characteristics of SiO2/ZrO2 hybrid tunnel oxide in metal-Al2O3-SiO2-Si3N4-SiO2-silicon (MAONOS) structure in an effort to improve program and erase speed as well as retention characteristics. Inserting ZrO2 into the conventional MAONOS structure increased the programmed V th variation to 6.8 V, and increased the erased V th variation to -3.7 V at 17 MV/cm. The results can be understood in terms of reducing the Fowler-Nordheim (F/N) tunneling barrier due to high-k ZrO2 in the tunneling oxide. In addition, Zr diffusion in SiO2 caused the formation of Zr x Si1- x O2 at the interface region, which reduced the energy band gap of SiO2. The retention property of the hybrid tunnel oxide varied depending on the thickness of SiO2. For thin SiO2 less than 30 Å, the retention properties of the tunneling oxides were poor compared with those of the SiO2 only tunneling oxides. However, the hybrid tunneling oxides with SiO2 thickness thicker than 40 Å yielded improved retention behavior compared with those of the SiO2-only tunneling oxides. The detailed analysis in charge density of ZrO2 was carried out by ISPP test. The obtained charge density was quite small compared to that of the total charge density, which indicates that the inserted ZrO2 layer serves as a tunneling material rather than charge storage dielectric.

New ZrO2/Al2O3 Nanocomposite Fabricated from Hybrid Nanoparticles Prepared by CO2 Laser Co-Vaporization

PubMed Central

Bartolomé, José F.; Smirnov, Anton; Kurland, Heinz-Dieter; Grabow, Janet; Müller, Frank A.

2016-01-01

Alumina toughened zirconia (ATZ) and zirconia toughened alumina (ZTA) are currently the materials of choice to meet the need for tough, strong, and bioinert ceramics for medical devices. However, the mechanical properties of ZrO2/Al2O3 dispersion ceramics could be considerably increased by reducing the corresponding grain sizes and by improving the homogeneity of the phase dispersion. Here, we prepare nanoparticles with an intraparticular phase distribution of Zr(1−x)AlxO(2−x/2) and (γ-, δ-)Al2O3 by the simultaneous gas phase condensation of laser co-vaporized zirconia and alumina raw powders. During subsequent spark plasma sintering the zirconia defect structures and transition alumina phases transform to a homogeneously distributed dispersion of tetragonal ZrO2 (52.4 vol%) and α-Al2O3 (47.6 vol%). Ceramics sintered by spark plasma sintering are completely dense with average grain sizes in the range around 250 nm. Outstanding mechanical properties (flexural strength σf = 1500 MPa, fracture toughness KIc = 6.8 MPa m1/2) together with a high resistance against low temperature degradation make these materials promising candidates for next generation bioceramics in total hip replacements and for dental implants. PMID:26846310

New ZrO2/Al2O3 Nanocomposite Fabricated from Hybrid Nanoparticles Prepared by CO2 Laser Co-Vaporization

NASA Astrophysics Data System (ADS)

Bartolomé, José F.; Smirnov, Anton; Kurland, Heinz-Dieter; Grabow, Janet; Müller, Frank A.

2016-02-01

Alumina toughened zirconia (ATZ) and zirconia toughened alumina (ZTA) are currently the materials of choice to meet the need for tough, strong, and bioinert ceramics for medical devices. However, the mechanical properties of ZrO2/Al2O3 dispersion ceramics could be considerably increased by reducing the corresponding grain sizes and by improving the homogeneity of the phase dispersion. Here, we prepare nanoparticles with an intraparticular phase distribution of Zr(1-x)AlxO(2-x/2) and (γ-, δ-)Al2O3 by the simultaneous gas phase condensation of laser co-vaporized zirconia and alumina raw powders. During subsequent spark plasma sintering the zirconia defect structures and transition alumina phases transform to a homogeneously distributed dispersion of tetragonal ZrO2 (52.4 vol%) and α-Al2O3 (47.6 vol%). Ceramics sintered by spark plasma sintering are completely dense with average grain sizes in the range around 250 nm. Outstanding mechanical properties (flexural strength σf = 1500 MPa, fracture toughness KIc = 6.8 MPa m1/2) together with a high resistance against low temperature degradation make these materials promising candidates for next generation bioceramics in total hip replacements and for dental implants.

Improved Tribological Performance of Amorphous Carbon (a-C) Coating by ZrO2 Nanoparticles

PubMed Central

Tang, Jinzhu; Ding, Qi; Zhang, Songwei; Wu, Guizhi; Hu, Litian

2016-01-01

Nanomaterials, such as Graphene, h-BN nanoparticles and MoS2 nanotubes, have shown their ability in improving the tribological performance of amorphous carbon (a-C) coatings. In the current study, the effectiveness of ZrO2 nanoparticles (ZrO2-NPs) in lubricating the self-mated nonhydrogenated a-C contacts was investigated in boundary lubrication regime. The results showed that 13% less friction and 50% less wear compared to the base oil were achieved by employing ZrO2-NPs in the base oil in self-mated a-C contacts. Via analyzing the ZrO2-NPs and the worn a-C surface after tests, it was found that the improved lubrication by ZrO2-NPs was based on “polishing effects”, which is a new phenomenon observed between a-C and nanoparticles. Under the “polishing effect”, micro-plateaus with extremely smooth surface and uniform height were produced on the analyzed a-C surface. The resulting topography of the a-C coating is suitable for ZrO2-NPs to act as nano-bearings between rubbing surfaces. Especially, the ZrO2-NPs exhibited excellent mechanical and chemical stability, even under the severe service condition, suggesting that the combination of nonhydrogenated a-C coating with ZrO2-NPs is an effective, long lasting and environment-friendly lubrication solution. PMID:28773916

Labeling of HeLa cells using ZrO2:Yb3+-Er3+ nanoparticles with upconversion emission

NASA Astrophysics Data System (ADS)

Ceja-Fdez, Andrea; López-Luke, Tzarara; Oliva, Jorge; Vivero-Escoto, Juan; Gonzalez-Yebra, Ana Lilia; Rojas, Ruben A. Rodriguez; Martínez-Pérez, Andrea; de la Rosa, Elder

2015-04-01

This work reports the synthesis, structural characterization, and optical properties of ZrO2:Yb3+-Er3+ (2-1 mol%) nanocrystals. The nanoparticles were coated with 3-aminopropyl triethoxysilane (APTES) and further modified with biomolecules, such as Biotin-Anti-rabbit (mouse IgG) and rabbit antibody-AntiKi-67, through a conjugation method. The conjugation was successfully confirmed by Fourier transform infrared, zeta potential, and dynamic light scattering. The internalization of the conjugated nanoparticles in human cervical cancer (HeLa) cells was followed by two-photon confocal microscopy. The ZrO2:Yb3+-Er3+ nanocrystals exhibited strong red emission under 970-nm excitation. Moreover, the luminescence change due to the addition of APTES molecules and biomolecules on the nanocrystals was also studied. These results demonstrate that ZrO2:Yb3+-Er3+ nanocrystals can be successfully functionalized with biomolecules to develop platforms for biolabeling and bioimaging.

Photoluminescence and cathodoluminescence of Tb-doped Al 2O 3-ZrO 2 nanostructures obtained by sol-gel method

NASA Astrophysics Data System (ADS)

Zawadzki, M.; Hreniak, D.; Wrzyszcz, J.; Miśta, W.; Grabowska, H.; Malta, O. L.; Stręk, W.

2003-07-01

Terbium-doped Al 2O 3-ZrO 2 mixed oxides of 10 wt% zirconia content were prepared by the alkoxide sol-gel method. The obtained samples were characterized by XRD, SEM, thermal analysis, textural and TPR studies. The effect of thermal treatment of Tb-doped Al 2O 3-ZrO 2 samples on photo- and cathodoluminescence spectra was investigated. It was found that the photoluminescence spectrum induced by UV excitation was characterized by a green luminescence pattern arising from the 5D 4 → 7F J ( J=6-0) transitions of the Tb 3+ ion. This photoluminescence became almost completely damped for the samples sintered at 1200 °C. However, these samples have demonstrated an intense cathodoluminescence under high electron accelerating potential (60 kV). Moreover, it was observed that apart of the green luminescence, the blue emission lines arising from 5D 3 → 7F J transitions of Tb 3+ were observed. The nature of such behavior is discussed.

Thermal Conductivity and Stability of HfO2-Y2O3 and La2Zr2O7 Evaluated for 1650 Deg C Thermal/Environmental Barrier Coating Applications

NASA Technical Reports Server (NTRS)

Zhu, Dong-Ming; Bansal, Narottam P.; Miller, Robert A.

2003-01-01

HfO2-Y2O3 and La2Zr2O7 are candidate thermal and environmental barrier coating (T/EBC) materials for gas turbine ceramic matrix composite (CMC) combustor applications because of their relatively low thermal conductivity and high temperature capability. In this paper, thermal conductivity and high temperature stability of hot-pressed and plasma sprayed specimens with representative partially-stabilized and fully-cubic HfO2-Y2O3 compositions and La2Zr2O7 were evaluated at temperatures up to 1700 C using a steady-state laser heat-flux technique. Sintering behavior of the plasmasprayed coatings was determined by monitoring the thermal conductivity increases during a 20-hour test period at various temperatures. Durability and failure mechanisms of the HfO2-Y2O3 and La2Zr2O7 coatings on mullite/SiC hexoloy or SiC/SiC CMC substrates were investigated at 1650 C under thermal gradient cyclic conditions. Coating design and testing issues for the 1650 C thermal/environmental barrier coating applications are also discussed.

New nano-sized Al2O3-BN coating 3Y-TZP ceramic composites for CAD/CAM-produced all-ceramic dental restorations. Part I. Fabrication of powders.

PubMed

Yang, Se Fei; Yang, Li Qiang; Jin, Zhi Hao; Guo, Tian Wen; Wang, Lei; Liu, Hong Chen

2009-06-01

Partially sintered 3 mol % yttria-stabilized tetragonal zirconium dioxide (ZrO(2), zirconia) polycrystal (3Y-TZP) ceramics are used in dental posterior restorations with computer-aided design-computer-aided manufacturing (CAD/CAM) techniques. High strength is acquired after sintering, but shape distortion of preshaped compacts during their sintering is inevitable. The aim of this study is to fabricate new machinable ceramic composites with strong mechanical properties that are fit for all-ceramic dental restorations. Aluminum oxide (Al(2)O(3))-coated 3Y-TZP powders were first prepared by the heterogeneous precipitation method starting with 3Y-TZP, Al(NO(3))(3) . 9H(2)O, and ammonia, then amorphous boron nitride (BN) was produced and the as-received composite powders were coated via in situ reaction with boric acid and urea. Transmission electron microscopy (TEM) and X-ray diffraction (XRD) were used to analyze the status of Al(2)O(3)-BN on the surface of the 3Y-TZP particles. TEM micrographs show an abundance of Al(2)O(3) particles and amorphous BN appearing uniformly on the surface of the 3Y-TZP particles after the coating process. The size of the Al(2)O(3) particles is about 20 nm. The XRD pattern shows clearly the peak of amorphous BN among the peaks of ZrO(2).

Electronic structural studies on the improved thermal stability of Li(Ni0.8Co0.15Al0.05)O2 by ZrO2 coating for lithium ion batteries

DOE PAGES

Kim, Ji-Young; Kim, Sang Hoon; Kim, Dong Hyun; ...

2017-03-21

The electronic structures of bare and ZrO 2-coated Li(Ni 0.8Co 0.15Al 0.05)O 2 electrode systems were investigated using a combination of time-resolved X-ray diffraction and soft X-ray absorption spectroscopy (XAS) techniques. The ZrO 2 coating on the surface of Li(Ni 0.8Co 0.15Al 0.05)O 2 was effective in elevating the onset temperature of the dissociation of charged Li 0.33(Ni 0.8Co 0.15Al 0.05)O 2, which will enhance the safety of Li-ion cells. Lastly, soft XAS spectra of the Ni LII,III-edge in the partial electron yield mode were obtained, which showed that the enhanced electrochemical properties and thermal stability of the cathode materialsmore » by ZrO 2 coating can be attributed to the suppression of unwanted Ni oxidation state changes at the surface.« less

Single-walled carbon nanotube-facilitated dispersion of particulate TiO2 on ZrO2 ceramic membrane filters.

PubMed

Yao, Yuan; Li, Gonghu; Gray, Kimberly A; Lueptow, Richard M

2008-07-15

We report that SWCNTs substantially improve the uniformity and coverage of TiO2 coatings on porous ZrO2 ceramic membrane filters. The ZrO2 filters were dip coated with 100 nm anatase TiO2, TiO2/SWCNT composites, a TiO2+SWCNT mixture, and a TiO2/MWCNT composite at pH 3, 5, and 8. Whereas the TiO2+SWCNT mixture and the TiO2/MWCNT composite promote better coverage and less clumping than TiO2 alone, the TiO2/SWCNT composite forms a complete uniform coating without cracking at pH 5 ( approximately 100% coverage). A combination of chemical and electrostatic effects between TiO2 and SWCNTs forming the composite as well as between the composite and the ZrO2 surface explains these observations.

Thermoluminescence (TL) of europium-doped ZrO2 obtained by sol-gel method

NASA Astrophysics Data System (ADS)

Rivera, T.; Furetta, C.; Azorín, J.; Barrera, M.; Soto, A. M.

This article reports the preparation and characterization of europium-doped zirconium oxide (ZrO2:Eu3+) formed by homogeneous precipitation from propoxyde of zirconium [Zr(OC3H7)4]. The alkoxide sol gel process is an efficient method to prepare the zirconium oxide matrix by the hydrolysis of alkoxide precursors followed by condensation to yield a polymeric oxo-bridged ZrO2 network. All compounds were characterized by thermal analysis and the X-ray diffractometry method. The thermoluminescence (TL) emission properties of ZrO2:Eu3+ under beta radiation effects are studied. The europium-doped sintered zirconia powder presents a TL glow curve with two peaks (Tmax) centered at around 204 and around 292 °C, respectively. TL response of ZrO2:Eu3+ as a function of beta-absorbed dose was linear from 2 Gy up to 90 Gy. The europium ion (Eu3+)-doped ZrO2 was found to be more sensitive to beta radiation than undoped ZrO2 obtained by the same method and presented a little fading of the TL signal compared with undoped zirconium oxide.

A thermal study on the structural changes of bimetallic ZrO2-modified TiO2 nanotubes synthesized using supercritical CO2.

PubMed

Lucky, R A; Charpentier, P A

2009-05-13

In this study the thermal behavior of bimetallic ZrO(2)-TiO(2) (10/90 mol/mol) nanotubes are discussed which were synthesized via a sol-gel process in supercritical carbon dioxide (scCO(2)). The effects of calcination temperature on the morphology, phase structure, mean crystallite size, specific surface area and pore volume of the nanotubes were investigated by using a variety of physiochemical techniques. We report that SEM and TEM images showed that the nanotubular structure was preserved at up to 800 degrees C calcination temperature. When exposed to higher temperatures (900-1000 degrees C) the ZrO(2)-TiO(2) tubes deformed and the crystallites fused together, forming larger crystallites, and a bimetallic ZrTiO(4) species was detected. These results were further examined using TGA, FTIR, XRD and HRTEM analysis. The BET textural properties demonstrated that the presence of a small amount of Zr in the TiO(2) matrix inhibited the grain growth, stabilized the anatase phase and increased the thermal stability.

[Preliminary study on DNA damage of ZrO(2)/LaPO(4) diphase ceramics on human peripheral blood lymphocytes in vitro].

PubMed

Zhu, Hui-fang; Chen, Li-ping; Zhang, Xiu-li; Zhang, Bao-wei

2009-06-01

To detect the genotoxicity of dental machinable ZrO(2)/LaPO(4) diphase ceramics on human peripheral blood lymphocytes in vitro. The evaluation of DNA damage on human lymphocytes was performed by comet assay for three groups of ZrO(2)/LaPO(4) diphase ceramics with 30wt% of LaPO(4) (with 3wt% and 5wt% of Y(2)O(3)) and 40wt% of LaPO(4) (with 5wt% of Y(2)O(3)). The results were analyzed with SPSS16.0 software package for one-factor ANOVA and LSD. Three experimental groups with different concentration of LaPO(4) of ZrO(2)/LaPO(4) diphase ceramics, the negative control of IPS Empress II ceramics and the blank behaved little migration of the DNA strands respectively after six-day test, and there was no significant difference in all the groups except the positive control (P>0.05). The study indicates little effect of DNA damage of ZrO(2)/LaPO(4) diphase ceramics.

Ceramic composite separators coated with moisturized ZrO(2) nanoparticles for improving the electrochemical performance and thermal stability of lithium ion batteries.

PubMed

Kim, Ki Jae; Kwon, Hyuk Kwon; Park, Min-Sik; Yim, Taeeun; Yu, Ji-Sang; Kim, Young-Jun

2014-05-28

We introduce a ceramic composite separator prepared by coating moisturized ZrO2 nanoparticles with a poly(vinylidene fluoride-co-hexafluoropropylene) (PVdF-12wt%HFP) copolymer on a polyethylene separator. The effect of moisturized ZrO2 nanoparticles on the morphology and the microstructure of the polymeric coating layer is investigated. A large number of micropores formed around the embedded ZrO2 nanoparticles in the coating layer as a result of the phase inversion caused by the adsorbed moisture. The formation of micropores highly affects the ionic conductivity and electrolyte uptake of the ceramic composite separator and, by extension, the rate discharge properties of lithium ion batteries. In particular, thermal stability of the ceramic composite separators coated with the highly moisturized ZrO2 nanoparticles (a moisture content of 16 000 ppm) is dramatically improved without any degradation in electrochemical performance compared to the performance of pristine polyethylene separators.

Fabrication and magnetic properties of Fe and Co co-doped ZrO2

NASA Astrophysics Data System (ADS)

Okabayashi, J.; Kono, S.; Yamada, Y.; Nomura, K.

2011-12-01

We investigate the effects of Fe and Co co-doping on the magnetic and electronic properties of ZrO2 ceramics prepared by a sol-gel method, and study their dependence on the annealing temperature. Dilute Fe and Co co-doping into ZrO2 exhibits ferromagnetic behavior at room temperature for annealing temperatures above 900 °C, accompanying the phase transition from tetragonal to monoclinic structure in ZrO2. The electronic structures are studied by x-ray absorption spectroscopy and Mössbauer spectroscopy, which suggest that the Fe3+ and Co2+/Co3+ mixing states are dominant in Fe and Co co-doped ZrO2.

Ceramic oxide reactions with V2O5 and SO3

NASA Technical Reports Server (NTRS)

Jones, R. L.; Williams, C. E.

1985-01-01

Ceramic oxides are not inert in combustion environments, but can react with, inter alia, SO3, and Na2SO4 to yield low melting mixed sulfate eutectics, and with vanadium compounds to produce vanadates. Assuming ceramic degradation to become severe only when molten phases are generated in the surface salt (as found for metallic hot corrosion), the reactivity of ceramic oxides can be quantified by determining the SO3 partial pressure necessary for molten mixed sulfate formation with Na2SO3. Vanadium pentoxide is an acidic oxide that reacts with Na2O, SO3, and the different ceramic oxides in a series of Lux-Flood type of acid-base displacement reactions. To elucidate the various possible vanadium compound-ceramic oxide interactions, a study was made of the reactions of a matrix involving, on the one axis, ceramix oxides of increasing acidity, and on the other axis, vanadium compounds of increasing acidity. Resistance to vanadium compound reaction increased as the oxide acidity increased. Oxides more acidic than ZrO2 displaced V2O5. Examination of Y2O3- and CeO2-stabilized ZrO2 sintered ceramics which were degraded in 700 C NaVO3 has shown good agreement with the reactions predicted above, except that the CeO2-ZrO2 ceramic appears to be inexplicably degraded by NaVO3.

Yb:Y2O3 transparent ceramics processed with hot isostatic pressing

NASA Astrophysics Data System (ADS)

Wang, Jun; Ma, Jie; Zhang, Jian; Liu, Peng; Luo, Dewei; Yin, Danlei; Tang, Dingyuan; Kong, Ling Bing

2017-09-01

Highly transparent 5 at.% Yb:Y2O3 ceramics were fabricated by using a combination method of vacuum sintering and hot isostatic pressing (HIP). Co-precipitated Yb:Y2O3 powders, with 1 at.% ZrO2 as the sintering aid, were used as the starting material. The Yb:Y2O3 ceramics, vacuum sintered at 1700 °C for 2 h and HIPed at 1775 °C for 4 h, exhibited small grain size of 1.9 μm and highly dense microstructure. In-line optical transmittance of the ceramics reached 83.4% and 78.9% at 2000 and 600 nm, respectively. As the ceramic slab was pumped by a fiber-coupled laser diode at about 940 nm, a maximum output power of 0.77 W at 1076 nm was achieved, with a corresponding slope efficiency of 10.6%.

Effects of Post-Deposition Annealing on ZrO2/n-GaN MOS Capacitors with H2O and O3 as the Oxidizers

NASA Astrophysics Data System (ADS)

Zheng, Meijuan; Zhang, Guozhen; Wang, Xiao; Wan, Jiaxian; Wu, Hao; Liu, Chang

2017-04-01

GaN-based metal-oxide-semiconductor capacitors with ZrO2 as the dielectric layer have been prepared by atomic layer deposition. The accumulation and depletion regions can be clearly distinguished when the voltage was swept from -4 to 4 V. Post-annealing results suggested that the capacitance in accumulation region went up gradually as the annealing temperature increased from 300 to 500 °C. A minimum leakage current density of 3 × 10-9 A/cm2 at 1 V was obtained when O3 was used for the growth of ZrO2. Leakage analysis revealed that Schottky emission and Fowler-Nordheim tunneling were the main leakage mechanisms.

Insights on the High-Temperature Operational Limits of ZrO2-Y2O3 TBCs Manufactured via Air Plasma Spray

NASA Astrophysics Data System (ADS)

Lima, Rogerio S.; Marple, Basil R.

2017-03-01

The effective high-temperature operation limit of a ZrO2-7-8 wt.%Y2O3 (YSZ) thermal barrier coating (TBC) manufactured via air plasma spray (APS) is considered to be 1300 °C. This is related to the metastable tetragonal t'-phase formed during the rapid quenching of the YSZ particles during spraying. The t'-phase transforms into the equilibrium tetragonal and cubic phases at temperatures ≥ 1300 °C, which can lead to the formation of the monoclinic phase of YSZ upon cooling to room temperature. This formation of the monoclinic phase is accompanied by a volume expansion that leads to TBC failure due to extensive micro-cracking. To further investigate this limitation, an APS YSZ TBC was sprayed on a CMSX-4 substrate. By using a thermal (laser) gradient cyclic testing, a temperature gradient was generated across the TBC/substrate system. The YSZ T- front and substrate backside T- back temperature levels were 1500 and 1000 °C, respectively. In cycle conditions (5-min or 1-h hot and 2-min cool), no TBC failure has been observed. This behavior was partially attributed to the unexpected absence of the monoclinic phase of the YSZ in the cycled coatings. Although preliminary, these results are promising regarding increasing the effective high-temperature operational limits of APS YSZ TBCs.

Effects of Post-Deposition Annealing on ZrO2/n-GaN MOS Capacitors with H2O and O3 as the Oxidizers.

PubMed

Zheng, Meijuan; Zhang, Guozhen; Wang, Xiao; Wan, Jiaxian; Wu, Hao; Liu, Chang

2017-12-01

GaN-based metal-oxide-semiconductor capacitors with ZrO 2 as the dielectric layer have been prepared by atomic layer deposition. The accumulation and depletion regions can be clearly distinguished when the voltage was swept from -4 to 4 V. Post-annealing results suggested that the capacitance in accumulation region went up gradually as the annealing temperature increased from 300 to 500 °C. A minimum leakage current density of 3 × 10 -9  A/cm 2 at 1 V was obtained when O 3 was used for the growth of ZrO 2 . Leakage analysis revealed that Schottky emission and Fowler-Nordheim tunneling were the main leakage mechanisms.

Popcorn balls-like ZnFe2O4-ZrO2 microsphere for photocatalytic degradation of 2,4-dinitrophenol

NASA Astrophysics Data System (ADS)

Chen, Xi; Liu, Yutang; Xia, Xinnian; Wang, Longlu

2017-06-01

In this paper, novel popcorn balls-like ZnFe2O4-ZrO2 composite microspheres were successfully fabricated by a simple hydrothermal method. The morphology, structure and optical property of the microspheres were characterized. The microspheres were used as the photocatalysts to degrade 2,4-dinitrophenol, and exhibited superior photocatalytic performance. Under simulated solar visible light irradiation, the degradation rate of ZnFe2O4-ZrO2 photocatalyst (mass ratio of ZnFe2O4/ZrO2 = 2:1) was almost 7.4 and 2.4 times higher than those of pure ZnFe2O4 and ZrO2. The enhancement could attribute to stronger light absorption, lower carrier recombination and multi-porous structure of the microspheres. Moreover, the popcorn balls-like photocatalysts can be easily separated, because of the magnetism of the samples. After five times runs, the photocatalyst still showed 90% of its photocatalytic degradation efficiency. This work demonstrated a good prospect for removing organic pollutants in water.

ZrO2 film interfaces with Si and SiO2

NASA Astrophysics Data System (ADS)

Lopez, C. M.; Suvorova, N. A.; Irene, E. A.; Suvorova, A. A.; Saunders, M.

2005-08-01

The interface formed by the thermal oxidation of sputter-deposited Zr metal onto Si(100)- and SiO2-coated Si(100) wafers was studied in situ and in real time using spectroscopic ellipsometry (SE) in the 1.5-4.5 photon energy range and mass spectrometry of recoiled ions (MSRI). SE yielded optical properties for the film and interface and MSRI yielded film and interface composition. An optical model was developed and verified using transmission electron microscopy. Interfacial reaction of the ZrO2 was observed for both substrates, with more interaction for Si substrates. Equivalent oxide thicknesses and interface trap levels were determined on capacitors with lower trap levels found on samples with a thicker SiO2 underlayer. In addition to the optical properties for the intermixed interface layer, the optical properties for Zr metal and unreacted ZrO2 are also reported.

Combinatorial Investigation of ZrO2-Based Dielectric Materials for Dynamic Random-Access Memory Capacitors

NASA Astrophysics Data System (ADS)

Kiyota, Yuji; Itaka, Kenji; Iwashita, Yuta; Adachi, Tetsuya; Chikyow, Toyohiro; Ogura, Atsushi

2011-06-01

We investigated zirconia (ZrO2)-based material libraries in search of new dielectric materials for dynamic random-access memory (DRAM) by combinatorial-pulsed laser deposition (combi-PLD). We found that the substitution of yttrium (Y) to Zr sites in the ZrO2 system suppressed the leakage current effectively. The metal-insulator-metal (MIM) capacitor property of this system showed a leakage current density of less than 5×10-7 A/cm2 and the dielectric constant was 20. Moreover, the addition of titanium (Ti) or tantalum (Ta) to this system caused the dielectric constant to increase to ˜25 within the allowed leakage level of 5×10-7 A/cm2. Therefore, Zr-Y-Ti-O and Zr-Y-Ta-O systems have good potentials for use as new materials with high dielectric constants of DRAM capacitors instead of silicon dioxides (SiO2).

Physicochemical properties of precursors of Al2O3-ZrO2 oxide ceramics prepared by electrochemical method

NASA Astrophysics Data System (ADS)

Petrova, E. V.; Dresvyannikov, A. F.; Ahmadi Daryakenari, M.; Khairullina, A. I.

2016-05-01

Scanning electron microscopy, X-ray, and thermal analysis are used to examine the structure and properties of dispersive systems based on aluminum and zirconium oxides prepared electrochemically. The effect the conditions of synthesis have on the structure and morphology of Al2O3-ZrO2 particles is studied. It is shown that the effect of an electric field on the reaction medium allows us to adjust the physicochemical properties and morphology.

Spectroscopic properties of Sm3+ and V4+ ions in Na2O-SiO2-ZrO2 glasses

NASA Astrophysics Data System (ADS)

Neeraja, K.; Rao, T. G. V. M.; Kumar, A. Rupesh; Uma Lakshmi, V.; Veeraiah, N.; Rami Reddy, M.

2013-12-01

Na2O-SiO2-ZrO2 glasses of Sm3+ ions with and without V2O5 are characterized by spectroscopic and optical properties. The XRD and EDS spectra of the glass samples reveal an amorphous nature with different compositions within the glass matrix. The Infrared and Raman spectral studies are carried out and the existence of conventional structural units are analyzed in the glass network. The ESR spectra of the glass samples have indicating that a considerable proportion of vanadium ion exists in V4+ state. The optical absorption spectra of these glasses are recorded at room temperature, from the measured intensities of various absorption bands the Judd-Ofelt parameters Ω2, Ω4 and Ω6 are calculated. The photo-luminescence spectra recorded with excited wavelength 400 nm, five emission bands are observed; in this the energy transfer probability takes place between Sm3+ and V4+ ions.

MgO-Al2O3-ZrO2 Amorphous Ternary Composite: A Dense and Stable Optical Coating

NASA Technical Reports Server (NTRS)

Shaoo, Naba K.; Shapiro, Alan P.

1998-01-01

The process-parameter-dependent optical and structural properties of MgO-Al2O3-ZrO2 ternary mixed-composite material were investigated. Optical properties were derived from spectrophotometric measurements. The surface morphology, grain size distributions, crystallographic phases, and process- dependent material composition of films were investigated through the use of atomic force microscopy, x-ray diffraction analysis, and energy-dispersive x-ray analysis. Energy-dispersive x-ray analysis made evident the correlation between the optical constants and the process-dependent compositions in the films. It is possible to achieve environmentally stable amorphous films with high packing density under certain optimized process conditions.

Low-temperature CO oxidation over Cu/Pt co-doped ZrO2 nanoparticles synthesized by solution combustion.

PubMed

Singhania, Amit; Gupta, Shipra Mital

2017-01-01

Zirconia (ZrO 2 ) nanoparticles co-doped with Cu and Pt were applied as catalysts for carbon monoxide (CO) oxidation. These materials were prepared through solution combustion in order to obtain highly active and stable catalytic nanomaterials. This method allows Pt 2+ and Cu 2+ ions to dissolve into the ZrO 2 lattice and thus creates oxygen vacancies due to lattice distortion and charge imbalance. High-resolution transmission electron microscopy (HRTEM) results showed Cu/Pt co-doped ZrO 2 nanoparticles with a size of ca. 10 nm. X-ray diffraction (XRD) and Raman spectra confirmed cubic structure and larger oxygen vacancies. The nanoparticles showed excellent activity for CO oxidation. The temperature T 50 (the temperature at which 50% of CO are converted) was lowered by 175 °C in comparison to bare ZrO 2 . Further, they exhibited very high stability for CO reaction (time-on-stream ≈ 70 h). This is due to combined effect of smaller particle size, large oxygen vacancies, high specific surface area and better thermal stability of the Cu/Pt co-doped ZrO 2 nanoparticles. The apparent activation energy for CO oxidation is found to be 45.6 kJ·mol -1 . The CO conversion decreases with increase in gas hourly space velocity (GHSV) and initial CO concentration.

X ray photoelectron spectroscopy (XPS) analysis of Photosensitive ZrO2 array

NASA Astrophysics Data System (ADS)

Li, Y.; Zhao, G.; Zhu, R.; Kou, Z.

2018-03-01

Based on organic zirconium source as the starting material, by adding chemical modifiers which are made up with photosensitive ZrO2 sol. A uniformed ZrO2 array dot was fabricated with a mean diameter of around 800 nm. By using UV-vis spectra and X-ray photoelectron spectroscopy analysis method, studies the photosensitive ZrO2 gel film of photochemical reaction process and the photosensitive mechanism, to determine the zirconium atom centered chelate structure, reaction formed by metal chelate Zr atom for the center, and to establish the molecular model of the chelate. And studied the ultraviolet light in the process of the variation of the XPS spectra, Zr3d5/2 to 184.9 eV corresponding to the binding energy of the as the combination of state peak gradually reduce; By combining with the status of Zr-O peak gradually increase; The strength of the peak is gradually decline. This suggests that in the process of ultraviolet light photo chemical reaction happened. This study is of great significance to the micro fabrication of ZrO2 array not only to the memory devices but also to the optical devices.

Lu2O3-SiO2-ZrO2 Coatings for Environmental Barrier Application by Solution Precursor Plasma Spraying and Influence of Precursor Chemistry

NASA Astrophysics Data System (ADS)

Darthout, Émilien; Quet, Aurélie; Braidy, Nadi; Gitzhofer, François

2014-02-01

As environmental barrier coatings are subjected to thermal stress in gas turbine engines, the introduction of a secondary phase as zircon (ZrSiO4) is likely to increase the stress resistance of Lu2Si2O7 coatings generated by induction plasma spraying using liquid precursors. In a first step, precursor chemistry effect is investigated by the synthesis of ZrO2-SiO2 nanopowders by induction plasma nanopowder synthesis technique. Tetraethyl orthosilicate (TEOS) as silicon precursor and zirconium oxynitrate and zirconium ethoxide as zirconium precursors are mixed in ethanol and produce a mixture of tetragonal zirconia and amorphous silica nanoparticles. The use of zirconium ethoxide precursor results in zirconia particles with diameter below 50 nm because of exothermic thermal decomposition of the ethoxide and its high boiling point with respect to solvent, while larger particles are formed when zirconium oxynitrate is employed. The formation temperature of zircon from zirconia and silica oxides is found at 1425 °C. Second, coatings are synthesized in Lu2O3-ZrO2-SiO2 system. After heat treatment, the doping effect of lutetium on zirconia grains totally inhibits the zircon formation. Dense coatings are obtained with the use of zirconium ethoxide because denser particles with a homogeneous diameter distribution constitute the coating.

Chlorine mobility during annealing in N2 in ZrO2 and HfO2 films grown by atomic layer deposition

NASA Astrophysics Data System (ADS)

Ferrari, S.; Scarel, G.; Wiemer, C.; Fanciulli, M.

2002-12-01

Atomic layer deposition (ALD) growth of high-κ dielectric films (ZrO2 and HfO2) was performed using ZrCl4, HfCl4, and H2O as precursors. In this work, we use time of flight secondary ion mass spectrometry to investigate the chlorine distribution in ALD grown ZrO2 and HfO2 films, and its evolution during rapid thermal processes in nitrogen atmosphere. Chlorine outdiffusion is found to depend strongly upon annealing temperature and weakly upon the annealing time. While in ZrO2 chlorine concentration is significantly decreased already at 900 °C, in HfO2 it is extremely stable, even at temperatures as high as 1050 °C.

Defect-related electroluminescence from metal-oxide-semiconductor devices with ZrO2 films on silicon

NASA Astrophysics Data System (ADS)

Lv, Chunyan; Zhu, Chen; Wang, Canxing; Li, Dongsheng; Ma, Xiangyang; Yang, Deren

2016-11-01

Defect-related electroluminescence (EL) from ZrO2 films annealed under different atmosphere has been realized by means of electrical pumping scheme of metal-oxide-semiconductor (MOS) devices. At the same injection current, the acquired EL from the MOS device with the vacuum-annealed ZrO2 film is much stronger than that from the counterpart with the oxygen-annealed ZrO2 film. This is because the vacuum-annealed ZrO2 film contains more oxygen vacancies and Zr3+ ions. Analysis on the current-voltage characteristic of the ZrO2-based MOS devices indicates the P-F conduction mechanism dominates the electron transportation at the EL-enabling voltages under forward bias. It is tentatively proposed that the recombination of the electrons trapped in multiple oxygen-vacancy-related states with the holes in the defect level pertaining to Zr3+ ions brings about the EL emissions.

Enhanced electrical properties of SrBi4Ti4O15 ceramic with addition of ZrO2

NASA Astrophysics Data System (ADS)

Mamatha, B.; Rani, G. Neeraja; Shankar, J.

2018-04-01

Polycrystalline SrBi4Ti3.95Zr0.05O15 (SBZT) ceramic was prepared by solid-state double sintering method. It was characterized by X-Ray Diffraction (XRD) and Scanning Electron Micrograph (SEM). With the increased addition of ZrO2, the electrical properties as dielectric, ferroelectric and piezoelectric were studied. From XRD, single-phase formation with orthorhombic structure was identified by the increase of ZrO2. The remnant polarization (Pr) and dielectric constant was found to be increased with the increase of ZrO2. With the increase of ZrO2, Curie temperature (Tc) was found to be decreased. The planar electromechanical coupling coefficient (Kp = 0.57) and Piezoelectric coefficient (d33 = 18 pC/N) was found to be increased with the increase of ZrO2.

A Synergistic Effect of Surfactant and ZrO2 Underlayer on Photocurrent Enhancement and Cathodic Shift of Nanoporous Fe2O3 Photoanode

PubMed Central

Shinde, Pravin S.; Lee, Su Yong; Choi, Sun Hee; Lee, Hyun Hwi; Ryu, Jungho; Jang, Jum Suk

2016-01-01

Augmenting the donor density and nanostructure engineering are the crucial points to improve solar water oxidation performance of hematite (α-Fe2O3). This work addresses the sluggish water oxidation reaction associated with hematite photoanode by tweaking its internal porosity. The porous hematite photoanodes are fabricated by a novel synthetic strategy via pulse reverse electrodeposition (PRED) method that involves incorporation of a cationic CTAB surfactant in a sulfate electrolyte and spin-coated ZrO2 underlayer (UL) on FTO. CTAB is found to be beneficial in promoting the film growth rate during PRED. Incorporation of Zr4+ ions from ZrO2 UL and Sn4+ ions from FTO into the Fe2O3 lattice via solid-state diffusion reaction during pertinent annihilation of surfactant molecules at 800 °C produced internally porous hematite films with improved carrier concentration. The porous hematite demonstrated a sustained photocurrent enhancement and a significant cathodic shift of 130 mV relative to the planar hematite under standard illumination conditions (AM 1.5G) in 1 M NaOH electrolyte. The absorption, electrochemical impedance spectroscopy and Mott-Schottky analyses revealed that the ZrO2 UL and CTAB not only increased the carrier density and light harvesting but also accelerated the surface oxidation reaction kinetics, synergistically boosting the performance of internally porous hematite photoanodes. PMID:27577967

A Synergistic Effect of Surfactant and ZrO2 Underlayer on Photocurrent Enhancement and Cathodic Shift of Nanoporous Fe2O3 Photoanode.

PubMed

Shinde, Pravin S; Lee, Su Yong; Choi, Sun Hee; Lee, Hyun Hwi; Ryu, Jungho; Jang, Jum Suk

2016-08-31

Augmenting the donor density and nanostructure engineering are the crucial points to improve solar water oxidation performance of hematite (α-Fe2O3). This work addresses the sluggish water oxidation reaction associated with hematite photoanode by tweaking its internal porosity. The porous hematite photoanodes are fabricated by a novel synthetic strategy via pulse reverse electrodeposition (PRED) method that involves incorporation of a cationic CTAB surfactant in a sulfate electrolyte and spin-coated ZrO2 underlayer (UL) on FTO. CTAB is found to be beneficial in promoting the film growth rate during PRED. Incorporation of Zr(4+) ions from ZrO2 UL and Sn(4+) ions from FTO into the Fe2O3 lattice via solid-state diffusion reaction during pertinent annihilation of surfactant molecules at 800 °C produced internally porous hematite films with improved carrier concentration. The porous hematite demonstrated a sustained photocurrent enhancement and a significant cathodic shift of 130 mV relative to the planar hematite under standard illumination conditions (AM 1.5G) in 1 M NaOH electrolyte. The absorption, electrochemical impedance spectroscopy and Mott-Schottky analyses revealed that the ZrO2 UL and CTAB not only increased the carrier density and light harvesting but also accelerated the surface oxidation reaction kinetics, synergistically boosting the performance of internally porous hematite photoanodes.

A Synergistic Effect of Surfactant and ZrO2 Underlayer on Photocurrent Enhancement and Cathodic Shift of Nanoporous Fe2O3 Photoanode

NASA Astrophysics Data System (ADS)

Shinde, Pravin S.; Lee, Su Yong; Choi, Sun Hee; Lee, Hyun Hwi; Ryu, Jungho; Jang, Jum Suk

2016-08-01

Augmenting the donor density and nanostructure engineering are the crucial points to improve solar water oxidation performance of hematite (α-Fe2O3). This work addresses the sluggish water oxidation reaction associated with hematite photoanode by tweaking its internal porosity. The porous hematite photoanodes are fabricated by a novel synthetic strategy via pulse reverse electrodeposition (PRED) method that involves incorporation of a cationic CTAB surfactant in a sulfate electrolyte and spin-coated ZrO2 underlayer (UL) on FTO. CTAB is found to be beneficial in promoting the film growth rate during PRED. Incorporation of Zr4+ ions from ZrO2 UL and Sn4+ ions from FTO into the Fe2O3 lattice via solid-state diffusion reaction during pertinent annihilation of surfactant molecules at 800 °C produced internally porous hematite films with improved carrier concentration. The porous hematite demonstrated a sustained photocurrent enhancement and a significant cathodic shift of 130 mV relative to the planar hematite under standard illumination conditions (AM 1.5G) in 1 M NaOH electrolyte. The absorption, electrochemical impedance spectroscopy and Mott-Schottky analyses revealed that the ZrO2 UL and CTAB not only increased the carrier density and light harvesting but also accelerated the surface oxidation reaction kinetics, synergistically boosting the performance of internally porous hematite photoanodes.

Impact of nano and bulk ZrO2, TiO2 particles on soil nutrient contents and PGPR.

PubMed

Karunakaran, Gopalu; Suriyaprabha, Rangaraj; Manivasakan, Palanisamy; Yuvakkumar, Rathinam; Rajendran, Venkatachalam; Kannan, Narayanasamy

2013-01-01

Currently, nanometal oxides are used extensively in different industries such as medicine, cosmetics and food. The increased consumption of nanoparticles (NPs) leads the necessity to understand the fate of the nanoparticles in the environment. The present study focused on the ecotoxicological behaviour of bulk and nano ZrO2 (Zirconia) and TiO2 (Titania) particles on PGPR (plant growth promoting rhizobacteria), soil and its nutrient contents. The microbial susceptibility study showed that nano TiO2 had 13 +/- 0.9 mm (B. megaterium), 15 +/- 0.2 mm (P. fluorescens), 16 +/- 0.2 mm (A. vinelandii) and 12 +/- 0.3 mm (B. brevis) zones of inhibition. However, nano and bulk ZrO2 particles were non-toxic to PGPR. In addition, it was found that toxicity varied depends on the medium of reaction. The soil study showed that nano TiO2 was found to be highly toxic, whereas bulk TiO2 was less toxic towards soil bacterial populations at 1000 mg L(-1). In contrast, nano and bulk ZrO2 were found to be inert at 1000 mg L(-1). The observed zeta potential and hydrophobicity of TiO2 particles causes more toxic than ZrO2 in parallel with particle size. However, nano TiO2 decreases the microbial population as well as nutrient level of the soil but not zirconia. Our finding shows that the mechanism of toxicity depends on size, hydrophobic potential and zeta potential of the metal oxide particles. Thus, it is necessary to take safety measures during the disposal and use of such toxic nanoparticles in the soil to prevent their hazardous effects.

Schottky barrier SOI-MOSFETs with high-k La2O3/ZrO2 gate dielectrics

PubMed Central

Henkel, C.; Abermann, S.; Bethge, O.; Pozzovivo, G.; Klang, P.; Stöger-Pollach, M.; Bertagnolli, E.

2011-01-01

Schottky barrier SOI-MOSFETs incorporating a La2O3/ZrO2 high-k dielectric stack deposited by atomic layer deposition are investigated. As the La precursor tris(N,N′-diisopropylformamidinato) lanthanum is used. As a mid-gap metal gate electrode TiN capped with W is applied. Processing parameters are optimized to issue a minimal overall thermal budget and an improved device performance. As a result, the overall thermal load was kept as low as 350, 400 or 500 °C. Excellent drive current properties, low interface trap densities of 1.9 × 1011 eV−1 cm−2, a low subthreshold slope of 70-80 mV/decade, and an ION/IOFF current ratio greater than 2 × 106 are obtained. PMID:21461054

Na2O-Al2O3 system: Activity of Na2O in (α + β)- and (β + β)-alumina

NASA Astrophysics Data System (ADS)

Kale, G. M.

1992-12-01

The activity of Na2O in a biphasic mixture of (α + β)-alumina has been measured in the temperature range of 700 to 1100 K using the solid-state galvanic cell: 11663_2007_Article_BF02656462_TeX2GIFE1.gif _{(1:1)}^{Pt,CO_2 + O_2 /Na_2 CO_3 /(α + β ) - alumin a//(Y_2 O_3 )ZrO_2 //In + In_2 O_3 ,Ta,Pt} Similarly, the activity of Na2O in a (β + β’’)-alumina two-phase mixture has been measured between 700 and 1100 K employing the galvanic cell: 11663_2007_Article_BF02656462_TeX2GIFE2.gif _{(1:1)}^{Pt,CO_2 + O_2 /Na_2 CO_3 /(β + β ) - alumin a//(Y_2 O_3 )ZrO_2 //In + In_2 O_3 ,Ta,Pt} The reversible electromotive force (emf ) of both the cells was found to vary linearly with temperature over the entire temperature range of measurement. From the measured reversible emf and auxiliary thermodynamic data for In2O2, Na2O, CO2 and Na2CO3 reported in the literature, the temperature dependence of the logarithm of activity of Na2O in (α + β)-alumina is obtained: 11663_2007_Article_BF02656462_TeX2GIFE3.gif log α _{Na_2 O} (α + β ) = 1.85 - 14,750/T(K)( ± 0.015)(700 ≤slant T ≤slant 1100) For (β + β'’)-alumina, 11663_2007_Article_BF02656462_TeX2GIFE4.gif log α _{Na_2 O} (β + β ) = 3.9 - 13,000/T(K)( ± 0.015)(700 ≤slant T ≤slant 1100)

Doping Li and K into Na2ZrO3 Sorbent to Improve Its CO2 Capture Capability

NASA Astrophysics Data System (ADS)

Duan, Yuhua

Carbon dioxide is one of the major combustion products which once released into the air can contribute to global climate change. Solid sorbents have been reported in several previous studies to be promising candidates for CO2 sorbent applications due to their high CO2 absorption capacities at moderate working temperatures. However, at a given CO2 pressure, the turnover temperature (Tt) of an individual solid capture CO2 reaction is fixed and may be outside the operating temperature range (ΔTo) for a particularly capture technology. In order to shift such Tt for a solid into the range of ΔTo, its corresponding thermodynamic property must be changed by changing its structure by reacting (mixing) with other materials or doping with other elements. As an example, by combining thermodynamic database searching with ab initio thermodynamics calculations, in this work, we explored the Li- and K-doping effects on the Tt shifts of Na2ZrO3 at different doping levels. The obtained results showed that compared to pure Na2ZrO3, the Li- and K-doped mixtures Na2-αMαZrO3 (M =Li, K) have lower Tt and higher CO2 capture capacities.

Potential of SiO2/ZrO2 matrix doped with CoFe2O4 magnetic nanoparticles in achieving integrated magneto-optical isolators

NASA Astrophysics Data System (ADS)

Zamani, Mehdi; Hocini, Abdesselam

2017-05-01

We have investigated the potential of the SiO2/ZrO2 matrix doped with CoFe2O4 magnetic nanoparticles in order to overcome the problem of integration of the magneto-optical isolators (MOIs). In this way, we have performed a theoretical study for the case of designing perfect and adjustable MOIs based on magnetophotonic crystals (MPCs) containing SiO2/ZrO2 matrix doped with CoFe2O4 magnetic nanoparticles as a magnetic medium. Despite the existence the attenuation coefficient for SiO2/ZrO2 matrix at wavelength 1550 nm that leads to a non-perfect transmittance, we could introduce an MPC structure having no reflectance; therefore, an ideal MOI for eliminating unwanted back-reflection could be achieved.

Fischer-Tropsch Cobalt Catalyst Improvements with the Presence of TiO2, La2O3, and ZrO2 on an Alumina Support

NASA Technical Reports Server (NTRS)

Klettlinger, Jennifer Lindsey Suder

2012-01-01

The objective of this study was to evaluate the effect of titanium oxide, lanthanum oxide, and zirconium oxide on alumina supported cobalt catalysts. The hypothesis was that the presence of lanthanum oxide, titanium oxide, and zirconium oxide would reduce the interaction between cobalt and the alumina support. This was of interest because an optimized weakened interaction could lead to the most advantageous cobalt dispersion, particle size, and reducibility. The presence of these oxides on the support were investigated using a wide range of characterization techniques such as SEM, nitrogen adsorption, x-ray diffraction (XRD), temperature programmed reduction (TPR), temperature programmed reduction after reduction (TPR-AR), and hydrogen chemisorptions/pulse reoxidation. Results indicated that both La2O3 and TiO2 doped supports facilitated the reduction of cobalt oxide species in reference to pure alumina supported cobalt catalysts, however further investigation is needed to determine the effect of ZrO2 on the reduction profile. Results showed an increased corrected cluster size for all three doped supported catalysts in comparison to their reference catalysts. The increase in reduction and an increase in the cluster size led to the conclusion that the support-metal interaction weakened by the addition of TiO2 and La2O3. It is also likely that the interaction decreased upon presence of ZrO2 on the alumina, but further research is necessary. Preliminary results have indicated that the alumina-supported catalysts with titanium oxide and lanthanum oxide present are of interest because of the weakened cobalt support interaction. These catalysts showed an increased extent of reduction, therefore more metallic cobalt is present on the support. However, whether or not there is more cobalt available to participate in the Fischer-Tropsch synthesis reaction (cobalt surface atoms) depends also on the cluster size. On one hand, increasing cluster size alone tends to decrease the

Oxygen potentials in Ni + NiO and Ni + Cr2O3 + NiCr2O4 systems

NASA Astrophysics Data System (ADS)

Kale, G. M.; Fray, D. J.

1994-06-01

The chemical potential of O for the coexistence of Ni + NiO and Ni + Cr2O3 + NiCr2O4 equilibria has been measured employing solid-state galvanic cells, (+) Pt, Cu + Cu2O // (Y2O3)ZrO2 // Ni + NiO, Pt (-) and (+) Pt, Ni + NiO // (Y2O3)ZrO2 // Ni + Cr2O3 + NiCr2O4, Pt (-) in the temperature range of 800 to 1300 K and 1100 to 1460 K, respectively. The electromotive force (emf) of both the cells was reversible, reproducible on thermal cycling, and varied linearly with temperature. For the coexistence of the two-phase mixture of Ni + NiO, δΜO 2(Ni + NiO) = -470,768 + 171.77T (±20) J mol-1 (800 ≤ T ≤ 1300 K) and for the coexistence of Ni + Cr2O3 + NiCr2O4, δΜO 2(Ni + Cr2O3 + NiCr2O4) = -523,190 + 191.07T (±100) J mol-1 (1100≤ T≤ 1460 K) The “third-law” analysis of the present results for Ni + NiO gives the value of ‡H{298/o} = -239.8 (±0.05) kJ mol-1, which is independent of temperature, for the formation of one mole of NiO from its elements. This is in excellent agreement with the calorimetric enthalpy of formation of NiO reported in the literature.

Preparation, chromatographic evaluation and application of adenosine 5'-monophosphate modified ZrO2/SiO2 stationary phase in hydrophilic interaction chromatography.

PubMed

Wang, Qing; Luo, Zhi-Yuan; Ye, Mao; Wang, Yu-Zhuo; Xu, Li; Shi, Zhi-Guo; Xu, Lanying

2015-02-27

The zirconia-coated silica (ZrO2/SiO2) material was obtained by coupling layer-by-layer (LbL) self-assembly method and sol-gel technology, to take dual advantages of the suitable porous structure of SiO2 and basic resistance of ZrO2. Adenosine 5'-monophosphate (5'-AMP) was then self-assembled onto ZrO2/SiO2 via Lewis acid-base interaction, generating 5'-AMP-ZrO2/SiO2. The chromatographic properties of 5'-AMP-ZrO2/SiO2 were systemically studied by evaluating the effect of acetonitrile content, pH and buffer concentration in the mobile phase. The results demonstrated that the 5'-AMP-ZrO2/SiO2 possessed hydrophilic interaction chromatographic (HILIC) property comprising hydrophilic, hydrogen-bonding, electrostatic and ion-exchange interactions. For basic analytes, the column efficiency of ZrO2/SiO2 and 5'-AMP-ZrO2/SiO2 was superior to the bare ZrO2, and different selectivity was obtained after the introduction of 5'-AMP. For acidic analytes, good resolution was obtained on 5'-AMP-ZrO2/SiO2 while the analysis failed on the bare ZrO2 column owing to strong adsorption. Hence, the proposed 5'-AMP-ZrO2/SiO2 had great potential in analyzing acidic compounds in HILIC mode. It was an extended application of ZrO2 based SP. Copyright © 2015 Elsevier B.V. All rights reserved.

Enhanced Light Stability of InGaZnO Thin-Film Transistors by Atomic-Layer-Deposited Y2O3 with Ozone.

PubMed

Jung, Hanearl; Kim, Woo-Hee; Park, Bo-Eun; Woo, Whang Je; Oh, Il-Kwon; Lee, Su Jeong; Kim, Yun Cheol; Myoung, Jae-Min; Gatineau, Satoko; Dussarrat, Christian; Kim, Hyungjun

2018-01-17

We report the effect of Y 2 O 3 passivation by atomic layer deposition (ALD) using various oxidants, such as H 2 O, O 2 plasma, and O 3 , on In-Ga-Zn-O thin-film transistors (IGZO TFTs). A large negative shift in the threshold voltage (V th ) was observed in the case of the TFT subjected to the H 2 O-ALD Y 2 O 3 process; this shift was caused by a donor effect of negatively charged chemisorbed H 2 O molecules. In addition, degradation of the IGZO TFT device performance after the O 2 plasma-ALD Y 2 O 3 process (field-effect mobility (μ) = 8.7 cm 2 /(V·s), subthreshold swing (SS) = 0.77 V/dec, and V th = 3.7 V) was observed, which was attributed to plasma damage on the IGZO surface adversely affecting the stability of the TFT under light illumination. In contrast, the O 3 -ALD Y 2 O 3 process led to enhanced device stability under light illumination (ΔV th = -1 V after 3 h of illumination) by passivating the subgap defect states in the IGZO surface region. In addition, TFTs with a thicker IGZO film (55 nm, which was the optimum thickness under the current investigation) showed more stable device performance than TFTs with a thinner IGZO film (30 nm) (ΔV th = -0.4 V after 3 h of light illumination) by triggering the recombination of holes diffusing from the IGZO surface to the insulator-channel interface. Therefore, we envisioned that the O 3 -ALD Y 2 O 3 passivation layer suggested in this paper can improve the photostability of TFTs under light illumination.

Synthesis, characterization and biological study on Cr(3+), ZrO(2+), HfO(2+) and UO(2)(2+) complexes of oxalohydrazide and bis(3-hydroxyimino)butan-2-ylidene)-oxalohydrazide.

PubMed

El-Asmy, A A; El-Gammal, O A; Radwan, H A

2010-09-01

Cr(3+), ZrO(2+), HfO(2+) and UO(2)(2+) complexes of oxalohydrazide (H(2)L(1)) and oxalyl bis(diacetylmonoxime hydrazone) [its IUPAC name is oxalyl bis(3-hydroxyimino)butan-2-ylidene)oxalohydrazide] (H(4)L(2)) have been synthesized and characterized by partial elemental analysis, spectral (IR; electronic), thermal and magnetic measurements. [Cr(L(1))(H(2)O)(3)(Cl)].H(2)O, [ZrO(HL(1))(2)].C(2)H(5)OH, [UO(2)(L(1))(H(2)O)(2)] [ZrO(H(3)L(2))(Cl)](2).2H(2)O, [HfO(H(3)L(2))(Cl)](2).2H(2)O and [UO(2)(H(2)L(2))].2H(2)O have been suggested. H(2)L(1) behaves as a monobasic or dibasic bidentate ligand while H(4)L(2) acts as a tetrabasic octadentate with the two metal centers. The molecular modeling of the two ligands have been drawn and their molecular parameters were calculated. Examination of the DNA degradation of H(2)L(1) and H(4)L(2) as well as their complexes revealed that direct contact of [ZrO(H(3)L(2))(Cl)](2).2H(2)O or [HfO(H(3)L(2))(Cl)](2).2H(2)O degrading the DNA of Eukaryotic subject. The ligands and their metal complexes were tested against Gram's positive Bacillus thuringiensis (BT) and Gram's negative (Escherichia coli) bacteria. All compounds have small inhibitory effects. Copyright 2010 Elsevier B.V. All rights reserved.

Laser-synthesized Y2O3:Eu3+ nanophosphors and their stabilization in water suspensions

NASA Astrophysics Data System (ADS)

Ivanov, M. G.; Krutikova, I. V.; Kynast, U.; Lezhnina, M.; Puzyrev, I. S.

2017-12-01

Europium doped yttrium oxide nanophosphors (Y2O3 doped with 5% Eu3+), which consists of spherical single-phase monoclinic particles with an average size of 17 nm, was prepared by laser synthesis. While the monoclinic material has a low efficiency of only 19% of a μm-sized commercial Y2O3:Eu product, the cubic phase after calcination at 900 °C achieves 68% despite the remaining hydroxo-groups at the surface and still small crystallite size (56 nm). An ethanolammonium salt of citric acid (Dolapix CE64) was used as a dispersant in water suspension. To estimate the stability of the dispersed phase, the electrokinetic potential and agglomerate sizes were measured as a function of pH. With this dispersant, a 30 wt% nanopowder water suspension, showing a Newtonian viscosity of about 6 mPa × s, was obtained. Maximum content of the nanopowder of about 60 wt% can be accomplished in the slurry, still fluid enough to be used to cast a highly uniform and dense ceramic green body to sinter nanostructured Y2O3:Eu3+ phosphors ceramics.

Interfacial Energy Transfer during Gamma Radiolysis of Water on the Surface of ZrO2 and Some Other Oxides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Petrik, Nikolay G.; Alexandrov, Alexandr B.; Vall, Andrey I.

Effect of oxide interface on 60Co gamma radiolysis of water molecules was studied. Based on the molecular hydrogen yield when compared with that from the radiolysis of pure gas-phase water, all tested oxides can be classified into three groups: (i) inhibitors - MnO2, Co3O4, CuO and Fe2O3; (ii) oxides with H2 yields, which are similar to or slightly greater than radiolysis of pure gas-phase water - MgO, CaO, SrO, BaO, ZnO, CdO, Cu2O, NiO, Cr2O3, Al2O3, CeO2, SiO2, TiO2, Nb2O5 and WO3; (iii) promoters - Ga2O3, Y2O3, La2O3, Nd2O3, Sm2O3, Eu2O3, Gd2O3, Yb2O3, Er2O3, HfO2, and ZrO2. H2O radiolysis enhancementmore » for ZrO2 and other promoters is result of effective energy transfer at the oxide/water interface, presumably due to migration of excitons to the surface and their resonant coupling with the H2O adsorption complex. Plot''effective H2 yield vs. band-gap (Eg) energy'' shows a maximum near 5 eV.« less

TiO2, SiO2 and ZrO2 Nanoparticles Synergistically Provoke Cellular Oxidative Damage in Freshwater Microalgae

PubMed Central

Liu, Yinghan; Ye, Nan; Fang, Hao; Wang, Degao

2018-01-01

Metal-based nanoparticles (NPs) are the most widely used engineered nanomaterials. The individual toxicities of metal-based NPs have been plentifully studied. However, the mixture toxicity of multiple NP systems (n ≥ 3) remains much less understood. Herein, the toxicity of titanium dioxide (TiO2) nanoparticles (NPs), silicon dioxide (SiO2) NPs and zirconium dioxide (ZrO2) NPs to unicellular freshwater algae Scenedesmus obliquus was investigated individually and in binary and ternary combination. Results show that the ternary combination systems of TiO2, SiO2 and ZrO2 NPs at a mixture concentration of 1 mg/L significantly enhanced mitochondrial membrane potential and intracellular reactive oxygen species level in the algae. Moreover, the ternary NP systems remarkably increased the activity of the antioxidant defense enzymes superoxide dismutase and catalase, together with an increase in lipid peroxidation products and small molecule metabolites. Furthermore, the observation of superficial structures of S. obliquus revealed obvious oxidative damage induced by the ternary mixtures. Taken together, the ternary NP systems exerted more severe oxidative stress in the algae than the individual and the binary NP systems. Thus, our findings highlight the importance of the assessment of the synergistic toxicity of multi-nanomaterial systems. PMID:29419775

Influence of Solvent on Liquid Phase Hydrodeoxygenation of Furfural-Acetone Condensation Adduct using Ni/Al2O3-ZrO2 Catalysts

NASA Astrophysics Data System (ADS)

Ulfa, S. M.; Mahfud, A.; Nabilah, S.; Rahman, M. F.

2017-02-01

Influence of water and acidic protic solvent on hydrodeoxygenation (HDO) of the furfural-acetone adduct (FAA) over Ni/Al2O3-ZrO2 (NiAZ) catalysts were investigated. The HDO of FAA was carried out in a batch reactor at 150°C for 8 hours. The NiAZ catalysts were home-made catalysts which were prepared by wet impregnation method with 10 and 20% nickel loading. The HDO reaction of FAA using 10NiAZ in water at 150°C gave alkane and oxygenated hydrocarbons at 31.41% with selectivity over tridecane (C13) in 6.67%. On the other hand, a reaction using acetic acid:water (1:19 v/v) in similar reaction condition gave only oxygenated compounds and hydrocracking product (C8-C10). The formation of tridecane (C13) was proposed by hydrogenation of C=O and C=C followed by decarboxylation without hydrocracking process. The presence of water facilitated decarboxylation mechanism by stabilized dehydrogenated derivatives of FAA.

Modeling of methanol decomposition on Pt/CeO2/ZrO2 catalyst in a packed bed microreactor

NASA Astrophysics Data System (ADS)

Pohar, Andrej; Belavič, Darko; Dolanc, Gregor; Hočevar, Stanko

2014-06-01

Methanol decomposition on Pt/CeO2/ZrO2 catalyst is studied inside a packed bed microreactor in the temperature range of 300-380 °C. The microreactor is fabricated using low-temperature co-fired ceramic (LTCC) technology, which is well suited for the production of relatively complex three-dimensional structures. It is packed with 2 wt% Pt-CeO2 catalyst, which is deposited onto ZrO2 spherical particles. A 1D mathematical model, which incorporates diffusion, convection and mass transfer through the boundary layer to the catalyst particles, as well as a 3D computational fluid dynamics model, are developed to describe the methanol decomposition process inside the packed bed. The microreactor exhibits reliable operation and no catalyst deactivation was observed during three months of experimentation. A comparison between the 1D mathematical model and the 3D model, considering the full 3D geometry of the microreactor is made and the differences between the models are identified and evaluated.

Aqueous Isolation of 17-Nuclear Zr-/Hf- Oxide Clusters during the Hydrothermal Synthesis of ZrO2/HfO2.

PubMed

Sung, Qing; Liu, Caiyun; Zhang, Guanyun; Zhang, Jian; Tung, Chen-Ho; Wang, Yifeng

2018-06-21

Novel 17-nuclear Zr-/Hf- oxide clusters ({Zr17} and {Hf17}) are isolated from aqueous systems. In the clusters, Zr/Hf ions are connected via μ3-O, μ3-OH and μ2-OH linkages into a pinwheel core which is wrapped with SO42-, HCOO- and aqua ligands. Octahedral hexanuclear Zr-/Hf- oxide clusters ({Zr6}oct and {Hf6}oct) are also isolated from the same hydrothermal system by decreasing the synthesis temperature. Structural analysis, synthetic conditions, vibrational spectra and ionic conductivity of the clusters are studied. Structural studies and synthesis inspection suggest that formation of {Zr6}oct and {Zr17} involves assembly of the same transferable building blocks, but the condensation degree and thermodynamic stability of the products increase with hydrothermal temperature. The role of {Zr6}oct and {Zr17} in the formation of ZrO2 nanocrystals are then discussed in the scenario of nonclassical nucleation theory. Besides, the Zr-oxide clusters exhibit ionic conductivity due to the mobility of protons. This study not only adds new members to the Zr-/Hf- oxide cluster family, but also establishes a connection from Zr4+ ions to ZrO2 in the hydrothermal preparation of zirconium oxide nanomaterials. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Hierarchical Na-doped cubic ZrO2 synthesis by a simple hydrothermal route and its application in biodiesel production

NASA Astrophysics Data System (ADS)

Lara-García, Hugo A.; Romero-Ibarra, Issis C.; Pfeiffer, Heriberto

2014-10-01

Hierarchical growth of cubic ZrO2 phase was successfully synthesized via a simple hydrothermal process in the presence of different surfactants (cationic, non-ionic and anionic) and sodium hydroxide. The structural and microstructural characterizations of different ZrO2 powders were performed using various techniques, such as X-ray diffraction, transmission electron microscopy, N2 adsorption-desorption, scanning electron microscopy and infrared. Results indicated that sodium addition stabilized the cubic ZrO2 phase by a Na-doping process, independently of the surfactant used. In contrast, microstructural characteristics varied as a function of the surfactant and sodium presence. In addition, water vapor (H2O) and carbon dioxide (CO2) sorption properties were evaluated on ZrO2 samples. Results evidenced that sample surface reactivity changed as a function of the sodium content. Finally, this surface reactivity was evaluated on the biodiesel transesterification reaction using the different synthesized samples, obtaining yields of 93%.

Indentation studies on Y[sub 2]O[sub 3]-stabilized ZrO[sub 2]; 1: Development of indentation-induced cracks

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kaliszewski, M.S.; Behrens, G.; Heuer, A.H.

1994-05-01

The development of Vickers indent-induced cracks with increasing indent load has been studied in two Y[sub 2]O[sub 3]-stabilized ZrO[sub 2] ceramics. Such cracks form as radial or Palmqvist cracks at low loads, assume kidney'' shapes at intermediate loads, and finally form median (half-penny) cracks at high loads. The plastic zone directly beneath the indent is uncracked; a significant portion of the plasticity induced by indentation occurs by martensitic transformation.

Preparation of magnetron sputtered ZrO2 films on Si for gate dielectric application

NASA Astrophysics Data System (ADS)

Kondaiah, P.; Mohan Rao, G.; Uthanna, S.

2012-11-01

Zirconium oxide (ZrO2) thin films were deposited on to p - Si and quartz substrates by sputtering of zirconium target at an oxygen partial pressure of 4x10-2 Pa and sputter pressure of 0.4 Pa by using DC reactive magnetron sputtering technique. The effect of annealing temperature on structural, optical, electrical and dielectric properties of the ZrO2 films was systematically studied. The as-deposited films were mixed phases of monoclinic and orthorhombic ZrO2. As the annealing temperature increased to 1073 K, the films were transformed in to single phase orthorhombic ZrO2. Fourier transform infrared studies conform the presence of interfacial layer between Si and ZrO2. The optical band gap and refractive index of the as-deposited films were 5.82 eV and 1.81. As the annealing temperature increased to 1073 K the optical band gap and refractive index increased to 5.92 eV and 2.10 respectively. The structural changes were influenced the capacitance-voltage and current-voltage characteristics of Al/ZrO2/p-Si capacitors. The dielectric constant was increased from 11.6 to 24.5 and the leakage current was decreased from 1.65×10-7 to 3.30×10-9 A/ cm2 for the as-deposited and annealed at 1073 K respectively.

Relationship between fabrication method and chemical stability of Ni-BaZr0.8Y0.2O3-δ membrane

NASA Astrophysics Data System (ADS)

Fang, Shumin; Wang, Siwei; Brinkman, Kyle S.; Su, Qing; Wang, Haiyan; Chen, Fanglin

2015-03-01

NiO effectively promotes the sintering of highly refractory Y-doped BaZrO3 (BZY) through the formation of BaY2NiO5, providing a simple and cost-effective method for the fabrication of dense BZY electrolyte and Ni-BZY hydrogen separation membrane at ∼1400 °C. Unfortunately, insulating BaCO3 and Y2O3 phases formed on the surface of BZY and Ni-BZY prepared by solid state reaction method with NiO after annealing in wet CO2. Ni-BZY membranes prepared from different methods suffered different degree of performance loss in wet H2 at 900 °C. The chemical instability of Ni-BZY is attributed to the formation of a secondary phase (BaY2O4) generated from the reduction of BaY2NiO5 in H2 during the sintering process. Both BaY2O4 and BaY2NiO5 react with H2O, and CO2 at elevated temperatures, generating insulating Ba(OH)2 and BaCO3 phases, respectively. The less BaY2O4 is formed in the fabrication process, the better chemical stability the Ni-BZY membranes possess. Therefore, a new Ni-BZY membrane is prepared through a judicial combination of BZY powders prepared from combined EDTA-citric and solid state reaction methods, and demonstrates exceptional chemical stability in H2O and CO2, enabling stable and even improved hydrogen flux in wet 50% CO2 at 900 °C.

Optical and structural characterization of Ge clusters embedded in ZrO2

NASA Astrophysics Data System (ADS)

Agocs, E.; Zolnai, Z.; Rossall, A. K.; van den Berg, J. A.; Fodor, B.; Lehninger, D.; Khomenkova, L.; Ponomaryov, S.; Gudymenko, O.; Yukhymchuk, V.; Kalas, B.; Heitmann, J.; Petrik, P.

2017-11-01

The change of optical and structural properties of Ge nanoclusters in ZrO2 matrix have been investigated by spectroscopic ellipsometry versus annealing temperatures. Radio-frequency top-down magnetron sputtering approach was used to produce the samples of different types, i.e. single-layers of pure Ge, pure ZrO2 and Ge-rich-ZrO2 as well as multi-layers stacked of 40 periods of 5-nm-Ge-rich-ZrO2 layers alternated by 5-nm-ZrO2 ones. Germanium nanoclusters in ZrO2 host were formed by rapid-thermal annealing at 600-800 °C during 30 s in nitrogen atmosphere. Reference optical properties for pure ZrO2 and pure Ge have been extracted using single-layer samples. As-deposited multi-layer structures can be perfectly modeled using the effective medium theory. However, annealed multi-layers demonstrated a significant diffusion of elements that was confirmed by medium energy ion scattering measurements. This fact prevents fitting of such annealed structure either by homogeneous or by periodic multi-layer models.

Chemical vapor deposited monolayer MoS2 top-gate MOSFET with atomic-layer-deposited ZrO2 as gate dielectric

NASA Astrophysics Data System (ADS)

Hu, Yaoqiao; Jiang, Huaxing; Lau, Kei May; Li, Qiang

2018-04-01

For the first time, ZrO2 dielectric deposition on pristine monolayer MoS2 by atomic layer deposition (ALD) is demonstrated and ZrO2/MoS2 top-gate MOSFETs have been fabricated. ALD ZrO2 overcoat, like other high-k oxides such as HfO2 and Al2O3, was shown to enhance the MoS2 channel mobility. As a result, an on/off current ratio of over 107, a subthreshold slope of 276 mV dec-1, and a field-effect electron mobility of 12.1 cm2 V-1 s-1 have been achieved. The maximum drain current of the MOSFET with a top-gate length of 4 μm and a source/drain spacing of 9 μm is measured to be 1.4 μA μm-1 at V DS = 5 V. The gate leakage current is below 10-2 A cm-2 under a gate bias of 10 V. A high dielectric breakdown field of 4.9 MV cm-1 is obtained. Gate hysteresis and frequency-dependent capacitance-voltage measurements were also performed to characterize the ZrO2/MoS2 interface quality, which yielded an interface state density of ˜3 × 1012 cm-2 eV-1.

Photo-, sono- and sonophotocatalytic degradation of methylene blue using Fe3O4/ZrO2 composites catalysts

NASA Astrophysics Data System (ADS)

Kristianto, Y.; Taufik, A.; Saleh, R.

2017-07-01

In the present work, magnetite material Fe3O4/ZrO2 with various molar ratios was prepared by the two-step method (sol-gel followed by the ultrasonic-assisted method). The as-prepared samples were fairly characterized by various characterization methods, such as X-ray Diffraction (XRD), Vibrating Sample Magnetometer (VSM), Fourier Transform Infrared (FT-IR) and Thermal Gravimetric Analysis (TGA). The catalytic performance of the as-prepared samples was evaluated based on the degradation of methylene blue under UV light, ultrasound and combination of UV and ultrasound irradiation. The results revealed that the sample with Fe3O4:ZrO2 molar ratio of 0.5:1 showed the best catalytic performance under UV, ultrasound and UV + ultrasound irradiation. The degradation of methylene blue follows the order: sonophotocatalytic > sonocatalytic > photocatalytic. In addition, the effect of various scavengers has also been studied. Furthermore, all prepared samples could be used as a convenient recyclable catalyst.

Intense visible light emission from stress-activated ZrO2:Ti

NASA Astrophysics Data System (ADS)

Akiyama, Morito; Xu, Chao-Nan; Nonaka, Kazuhiro

2002-07-01

We have investigated the luminescence phenomena from stress-activated ZrO2:Ti. The luminescence is clearly visible to the naked eye in the atmosphere. The luminescence center has been identified as the Ti4+ ion from spectra of the mechanoluminescence and also from photoluminescence studies of ZrO2:Ti. The mechanoluminescence intensity decreases on repetitive application of stress but recovers completely on irradiation with ultraviolet light. ZrO2 is an n-type semiconductor and has electron traps. It is suggested that the mechanoluminescence mechanism arises from the movement of dislocations and recombination between electrons and holes released from these traps which are associated with the Ti4+ centers.

The effect of micro-structure on upconversion luminescence of Nd3+/Yb3+ co-doped La2O3-TiO2-ZrO2 glass-ceramics

NASA Astrophysics Data System (ADS)

Zhang, Minghui; Wen, Haiqin; Pan, Xiuhong; Yu, Jianding; Jiang, Meng; Yu, Huimei; Tang, Meibo; Gai, Lijun; Ai, Fei

2018-03-01

Nd3+/Yb3+ co-doped La2O3-TiO2-ZrO2 glasses have been prepared by aerodynamic levitation method. The glasses show high refractive index of 2.28 and Abbe number of 18.3. Glass-ceramics heated at 880 °C for 50 min perform the strongest upconversion luminescence. X-ray diffraction patterns of glass-ceramics with different depths indicate that rare earth ions restrain crystallization. Body crystallization mechanism mixed with surface crystallization is confirmed in the heat treatment. Surface crystals achieve priority to grow, resulting in important effects on upconversion luminescence. The results of atomic force microscope and scanning electron microscope indicate that crystal particles with uniform size distribute densely and homogenously on the surface and large amount of glass matrix exists in the glass ceramics heated at 880 °C for 50 min. Crystals in the glass-ceramics present dense structure and strong boundaries, which can reduce the mutual nonradiative relaxation rate among rare earth ions and then improve upconversion luminescence effectively. Based on micro-structural study, the mechanism that upconversion luminescence can be improved by heat treatment has been revealed. The results of micro-structural analysis agree well with the spectra.

Influence of in situ and ex situ ZrO2 addition on the properties of MgB2

NASA Astrophysics Data System (ADS)

Chen, S. K.; Glowacki, B. A.; MacManus-Driscoll, J. L.; Vickers, M. E.; Majoros, M.

2004-02-01

The effect of ZrO2 addition on the properties of MgB2 has been studied using in situ and ex situ processes. The in situ process was performed by introducing ZrO2 from the milling tools into MgB2 throughout the planetary ball milling, whereas the ex situ process was accomplished by mixing ZrO2 from the milling tools with MgB2 by hand grinding in a mortar. A detectable amount of ZrO2 was present in MgB2 after 4 h of milling during the in situ process and its content increased with milling time as expected. The 400 h milled powder was partially amorphized and showed the formation of a minority ZrB2 phase. For milling up to 100 h, diamagnetism of MgB2 was significantly reduced while Tc remained unchanged. Superconductivity was totally destroyed after 148 h of milling. The loss of superconductivity is attributed to the effect of disordering induced by mechanical milling. As a result of in situ ZrO2 addition, the initial Tc and crystal structure of MgB2 could not be restored upon annealing. With increasing milling time, the expansion of lattice parameters in both the a-axis and c-axis may be due to possible substitution of Mg or B by Zr. The result from the magnetic measurement shows that Jc of MgB2 is deteriorated by in situ ZrO2 addition. On the other hand, ex situ ZrO2 addition with annealing did not degrade the Tc of MgB2.

Ultrasound-assisted sol-gel synthesis of ZrO2.

PubMed

Guel, Marlene Lariza Andrade; Jiménez, Lourdes Díaz; Hernández, Dora Alicia Cortés

2017-03-01

Synthesis of tetragonal ZrO 2 by both conventional sol-gel and ultrasound-assisted sol-gel methods and using a non-ionic surfactant Tween-20, was performed. A porous microstructure composed of nanometric particles was observed. Tetragonal ZrO 2 was obtained using a low heat treatment temperature of powders, 500°C by both methods. A higher crystallinity and a shorter reaction time were observed when ultrasound was used in the sol-gel method due to the cavitation phenomenon. Copyright © 2016 Elsevier B.V. All rights reserved.

Thermochemistry of CaO-MgO-Al2O3-SiO2 (CMAS) and Advanced Thermal and Environmental Barrier Coating Systems

NASA Technical Reports Server (NTRS)

Costa, Gustavo; Zhu, Dongming

2017-01-01

CaO-MgO-Al2O3-SiO2 (CMAS) oxides are constituents in a broad number of materials and minerals which have recently inferred to discussions in materials science, planetary science, geochemistry and cosmochemistry communities. In materials science, there is increasing interest in the degradation studies of thermal (TBC) and environmental (EBC) barrier coatings of gas turbines by molten CMAS. CMAS minerals usually are carried by the intake air into gas turbines, e.g. in aircraft engines, and their deposits react at high temperatures (1000C) with the coating materials. This causes degradation and accelerated failure of the static and rotating components of the turbine engines. We discuss some preliminary results of the reactions between CMAS and Rare-Earth (RE Y, Yb, Dy, Gd, Nd and Sm) oxide stabilized ZrO2 or HfO2 systems, and the stability of the resulting oxides and silicates. Plasma sprayed hollow tube samples ( 2.2 mm and 26 mm height) were half filled with CMAS powder, wrapped and sealed with platinum foil, and heat treated at 1310 C for 5h. Samples were characterized by differential scanning calorimetry, X-ray diffraction and cross section electron microscopy analysis.

[Preparing of Al2O3/ZrO2 composite dental ceramics through isostatic pressing technology].

PubMed

Liang, Xiao-Feng; Yin, Guang-Fu; Yang, Shi-Yuan; Wang, Jun-Xia

2006-08-01

To find out how to prepare high-density dental ceramics through isostatic pressing so that sintering shrinkage will be reduced. To prepare Al2O3/ZrO2 composite powder first, then to mold through dry-pressing, and to shape the green-body through isostatic pressing. The green-bodies were sintered at the temperature of 1 400 degrees C and kept at the temperature for different period of time (2 h, 3 h, 4 h). After that, the density and fracture strength were measured and the microstructure observed by scanning electron microscope (SEM). The sample product's density, line-shrinkage, and fracture strength of ceramics was rising with the sintering time lengthened. The sample product kept under the temperature of 1 400 degrees C for 4 hours, the fracture strength was (497.27 +/- 78.45) MPa and glass phase distributed evenly in the ceramics and the grains were integrated owing to the glass phase. The longer the sintering time, the more even the microstructure was. The sintering quality and the efficiency were improved through isostatic pressing.

Synthesis of Copper-Based Nanostructured Catalysts on SiO2-Al2O3, SiO2-TiO2, and SiO2-ZrO2 Supports for NO Reduction.

PubMed

Namkhang, Pornpan; Kongkachuichay, Paisan

2015-07-01

The selective catalytic reduction of NO over a series of Cu-based catalysts supported on modified silica including SiO2-Al2O3, SiO2-TiO2, and SiO2-ZrO2 prepared via a sol-gel process and a flame spray pyrolysis (FSP) was studied. The prepared catalysts were characterized by means of TEM, XRD, XRF, TPR, and nitrogen physisorption measurement techniques, to determine particle diameter, morphology, crystallinity, phase composition, copper reducibility, surface area, and pore size of catalysts. The particles obtained from sol-gel method were almost spherical while the particles obtained from the FSP were clearly spherical and non-porous nanosized particles. The effects of Si:Al, Si:Ti, and Si:Zr molar ratio of precursor were identified as the domain for different crystalline phase of materials. It was clearly seen that a high SiO2 content inhibited the crystallization of materials. The BET surface area of catalysts obtained from sol-gel method was higher than that from the FSP and it shows that surface area increased with increasing SiO2 molar ratio due to high surface area from SiO2. The catalyst performances were tested for the selective catalytic reduction of NO with H2. It was found that the catalyst prepared over 7 wt% Cu on Si02-Al2O3 support was the most active compared with the others which converted NO as more than 70%. Moreover, the excess copper decreased the performance of NO reduction, due to the formation of CuO agglomeration covered on the porous silica as well as the alumina surface, preventing the direct contact of CO2 and AL2O3.

Thermochemistry of CaO-MgO-Al2O3-SiO2 (CMAS) and Advanced Thermal and Environmental Barrier Coating Systems

NASA Technical Reports Server (NTRS)

Costa, Gustavo C. C.; Zhu, Dongming

2016-01-01

CaO-MgO-Al2O3-SiO2 (CMAS) oxides are constituents in a broad number of materials and minerals which have recently inferred to discussions in materials science, planetary science, geochemistry and cosmochemistry communities. In materials science, there is increasing interest in the degradation studies of thermal (TBC) and environmental (EBC) barrier coatings of gas turbines by molten CMAS. These coatings have been explored to be applied on silicon-based ceramics and composites which are lighter and more temperature capable hot-section materials of gas turbines than the current Ni-based superalloys. The degradation of the coatings occurs when CMAS minerals carried by the intake air into gas turbines, e.g. in aircraft engines, reacts at high temperatures (1000C) with the coating materials. This causes premature failure of the static and rotating components of the turbine engines. We discuss some preliminary results of the reactions between CMAS and Rare-Earth (RE Y, Yb and Gd) oxide stabilized ZrO2 systems, and stability of the resulting oxides and silicates.

Bioactivity and cell proliferation in radiopaque gel-derived CaO-P2O5-SiO2-ZrO2 glass and glass-ceramic powders.

PubMed

Montazerian, Maziar; Yekta, Bijan Eftekhari; Marghussian, Vahak Kaspari; Bellani, Caroline Faria; Siqueira, Renato Luiz; Zanotto, Edgar Dutra

2015-10-01

In this study, 10 mol% ZrO2 was added to a 27CaO-5P2O5-68SiO2 (mol%) base composition synthesized via a simple sol-gel method. This composition is similar to that of a frequently investigated bioactive gel-glass. The effects of ZrO2 on the in vitro bioactivity and MG-63 cell proliferation of the glass and its derivative polycrystalline (glass-ceramic) powder were investigated. The samples were characterized using thermo-gravimetric and differential thermal analysis (TG/DTA), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM) coupled to energy dispersive X-ray spectroscopy (EDS). Release of Si, Ca, P and Zr into simulated body fluid (SBF) was determined by inductively coupled plasma (ICP). Upon heat treatment at 1000 °C, the glass powder crystallized into an apatite-wollastonite-zirconia glass-ceramic powder. Hydroxycarbonate apatite (HCA) formation on the surface of the glass and glass-ceramic particles containing ZrO2 was confirmed by FTIR and SEM. Addition of ZrO2 to the base glass composition decreased the rate of HCA formation in vitro from one day to three days, and hence, ZrO2 could be employed to control the rate of apatite formation. However, the rate of HCA formation on the glass-ceramic powder containing ZrO2 crystal was equal to that in the base glassy powder. Tests with a cultured human osteoblast-like MG-63 cells revealed that the glass and glass-ceramic materials stimulated cell proliferation, indicating that they are biocompatible and are not cytotoxic in vitro. Moreover, zirconia clearly increased osteoblast proliferation over that of the Zr-free samples. This increase is likely associated with the lower solubility of these samples and, consequently, a smaller variation in the media pH. Despite the low solubility of these materials, bioactivity was maintained, indicating that these glassy and polycrystalline powders are potential candidates for bone graft substitutes and bone cements with

Density functional analysis of fluorite-structured (Ce, Zr)O 2/CeO 2 interfaces [Density functional analysis of fluorite-structured (Ce, Zr)O 2/CeO 2 interfaces: Implications for catalysis and energy applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weck, Philippe F.; Juan, Pierre -Alexandre; Dingreville, Remi

The structures and properties of Ce 1–xZr xO 2 (x = 0–1) solid solutions, selected Ce 1–xZr xO 2 surfaces, and Ce 1–xZr xO 2/CeO 2 interfaces were computed within the framework of density functional theory corrected for strong electron correlation (DFT+ U). The calculated Debye temperature increases steadily with Zr content in (Ce, Zr)O 2 phases, indicating a significant rise in microhardness from CeO 2 to ZrO 2, without appreciable loss in ductility as the interfacial stoichiometry changes. Surface energy calculations for the low-index CeO 2(111) and (110) surfaces show limited sensitivity to strong 4f-electron correlation. The fracture energymore » of Ce 1–xZr xO 2(111)/CeO 2(111) increases markedly with Zr content, with a significant decrease in energy for thicker Ce 1–xZr xO 2 films. These findings suggest the crucial role of Zr acting as a binder at the Ce 1–xZr xO 2/CeO 2 interfaces, due to the more covalent character of Zr–O bonds compared to Ce–O. Finally, the impact of surface relaxation upon interface cracking was assessed and found to reach a maximum for Ce 0.25Zr 0.75O 2/CeO 2 interfaces.« less

Density functional analysis of fluorite-structured (Ce, Zr)O 2/CeO 2 interfaces [Density functional analysis of fluorite-structured (Ce, Zr)O 2/CeO 2 interfaces: Implications for catalysis and energy applications

DOE PAGES

Weck, Philippe F.; Juan, Pierre -Alexandre; Dingreville, Remi; ...

2017-06-21

The structures and properties of Ce 1–xZr xO 2 (x = 0–1) solid solutions, selected Ce 1–xZr xO 2 surfaces, and Ce 1–xZr xO 2/CeO 2 interfaces were computed within the framework of density functional theory corrected for strong electron correlation (DFT+ U). The calculated Debye temperature increases steadily with Zr content in (Ce, Zr)O 2 phases, indicating a significant rise in microhardness from CeO 2 to ZrO 2, without appreciable loss in ductility as the interfacial stoichiometry changes. Surface energy calculations for the low-index CeO 2(111) and (110) surfaces show limited sensitivity to strong 4f-electron correlation. The fracture energymore » of Ce 1–xZr xO 2(111)/CeO 2(111) increases markedly with Zr content, with a significant decrease in energy for thicker Ce 1–xZr xO 2 films. These findings suggest the crucial role of Zr acting as a binder at the Ce 1–xZr xO 2/CeO 2 interfaces, due to the more covalent character of Zr–O bonds compared to Ce–O. Finally, the impact of surface relaxation upon interface cracking was assessed and found to reach a maximum for Ce 0.25Zr 0.75O 2/CeO 2 interfaces.« less

Effect of annealing temperature on optical and electrical properties of ZrO2-SnO2 based nanocomposite thin films

NASA Astrophysics Data System (ADS)

Anitha, V. S.; Lekshmy, S. Sujatha; Berlin, I. John; Joy, K.

2014-01-01

Transparent nanocomposite ZrO2-SnO2 thin films were prepared by sol-gel dip-coating technique. Films were annealed at 500°C, 800°C and 1200°C respectively. X-ray diffraction(XRD) spectra showed a mixture of three phases: tetragonal ZrO2 and SnO2 and orthorhombic ZrSnO4. The grain size of all the three phases' increased with annealing temperature. An average transmittance greater than 85%(in UV-Visible region) is observed for all the films. The band gap for the films decreased from 4.79 eV to 4.62 eV with increase in annealing temperature from 500 to 1200 °C. The electrical resistivity increased with increase in annealing temperature. Such composite ZrO2-SnO2 films can be used in many applications and in optoelectronic devices.

Intermixing and thermal oxidation of ZrO2 thin films grown on a-Si, SiN, and SiO2 by metallic and oxidic mode magnetron sputtering

NASA Astrophysics Data System (ADS)

Coloma Ribera, R.; van de Kruijs, R. W. E.; Sturm, J. M.; Yakshin, A. E.; Bijkerk, F.

2017-03-01

The initial growth of DC sputtered ZrO2 on top of a-Si, SiN, and SiO2 layers has been studied by in vacuo high-sensitivity low energy ion scattering for two gas deposition conditions with different oxygen contents (high-O and low-O conditions). This unique surface sensitive technique allowed the determination of surface composition and thicknesses required to close the ZrO2 layer on all three substrates for both conditions. The ZrO2 layer closes similarly on all substrates due to more favorable enthalpies of formation for ZrO2 and ZrSiO4, resulting in passivation of the Si from the substrate. However, this layer closes at about half of the thickness (˜1.7 nm) for low-O conditions due to less oxidative conditions and less energetic particles arriving at the sample, which leads to less intermixing via silicate formation. In contrast, for high-O conditions, there is more ZrSiO4 and/or SiOx formation, giving more intermixing (˜3.4 nm). In vacuo X-ray photoelectron spectroscopy (XPS) measurements revealed similar stoichiometric ZrO2 layers deposited by both conditions and a higher interaction of the ZrO2 layer with the underlying a-Si for high-O conditions. In addition, oxygen diffusion through low-O ZrO2 films on a-Si has been investigated by ex situ angular-resolved XPS of samples annealed in atmospheric oxygen. For temperatures below 400 °C, no additional oxidation of the underlying a-Si was observed. This, together with the amorphous nature and smoothness of these samples, makes ZrO2 a good candidate as an oxidation protective layer on top of a-Si.

High temperature investigation of the solid/liquid transition in the PuO2-UO2-ZrO2 system

NASA Astrophysics Data System (ADS)

Quaini, A.; Guéneau, C.; Gossé, S.; Sundman, B.; Manara, D.; Smith, A. L.; Bottomley, D.; Lajarge, P.; Ernstberger, M.; Hodaj, F.

2015-12-01

The solid/liquid transitions in the quaternary U-Pu-Zr-O system are of great interest for the analysis of core meltdown accidents in Pressurised Water Reactors (PWR) fuelled with uranium-dioxide and MOX. During a severe accident the Zr-based cladding can become completely oxidised due to the interaction with the oxide fuel and the water coolant. In this framework, the present analysis is focused on the pseudo-ternary system UO2-PuO2-ZrO2. The melting/solidification behaviour of five pseudo-ternary and one pseudo-binary ((PuO2)0.50(ZrO2)0.50) compositions have been investigated experimentally by a laser heating method under pre-set atmospheres. The effects of an oxidising or reducing atmosphere on the observed melting/freezing temperatures, as well as the amount of UO2 in the sample, have been clearly identified for the different compositions. The oxygen-to-metal ratio is a key parameter affecting the melting/freezing temperature because of incongruent vaporisation effects. In parallel, a detailed thermodynamic model for the UO2-PuO2-ZrO2 system has been developed using the CALPHAD method, and thermodynamic calculations have been performed to interpret the present laser heating results, as well as the high temperature behaviour of the cubic (Pu,U,Zr)O2±x-c mixed oxide phase. A good agreement was obtained between the calculated and experimental data points. This work enables an improved understanding of the major factors relevant to severe accident in nuclear reactors.

Dimensional stability and electrochemical behaviour of ZrO2 incorporated electrospun PVdF-HFP based nanocomposite polymer membrane electrolyte for Li-ion capacitors.

PubMed

Solarajan, Arun Kumar; Murugadoss, Vignesh; Angaiah, Subramania

2017-04-11

Different weight percentages of ZrO 2 (0, 3, 5, 7 and 10 wt%) incorporated electrospun PVDF-HFP nanocomposite polymer membranes (esCPMs) were prepared by electrospinning technique. They were activated by soaking in 1 M LiPF 6 containing 1:1 volume ratio of EC : DMC (ethylene carbonate:dimethyl carbonate) to get electrospun nanocomposite polymer membrane electrolytes (esCPMEs). The influence of ZrO 2 on the physical, mechanical and electrochemical properties of esCPM was studied in detail. Finally, coin type Li-ion capacitor cell was assembled using LiCo 0.2 Mn 1.8 O 4 as the cathode, Activated carbon as the anode and the esCPME containing 7 wt% of ZrO 2 as the separator, which delivered a discharge capacitance of 182.5 Fg -1 at the current density of 1Ag -1 and retained 92% of its initial discharge capacitance even after 2,000 cycles. It revealed that the electrospun PVdF-HFP/ZrO 2 based nanocomposite membrane electrolyte could be used as a good candidate for high performance Li-ion capacitors.

Synthesis of nano-sized crystalline oxide ion conducting fluorite-type Y 2O 3-doped CeO 2 using perovskite-like BaCe 0.9Y 0.1O 2.95 (BCY) and study of CO 2 capture properties of BCY

NASA Astrophysics Data System (ADS)

Sneha, B. R.; Thangadurai, V.

2007-10-01

Formation of nano-sized Y 2O 3-doped CeO 2 (YCO) was observed in the chemical reaction between proton conducting Y 2O 3-doped BaCeO 3 (BCY) and CO 2 in the temperature range 700-1000 °C, which is generally prepared by wet-chemical methods that include sol-gel, hydrothermal, polymerization, combustion, and precipitation reactions. BCY can capture CO 2 of 0.13 g per ceramic gram at 700 °C, which is comparable to that of the well-known Li 2ZrO 3 (0.15 g per ceramic gram at 600 °C). Powder X-ray diffraction (PXRD), energy dispersive X-ray analysis (EDX), laser particle size analysis (LPSA), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and ac impedance spectroscopy were employed to characterize the reaction product obtained from reaction between BCY and CO 2 and subsequent acid washing. PXRD study reveals presence of fluorite-like CeO 2 ( a=5.410 (1) Å) structure and BaCO 3 in reaction products. TEM investigation of the acid washed product showed the formation of nano-sized material with particle sizes of about 50 nm. The electrical conductivity of acid washed product (YCO) in air was found to be about an order higher than the undoped CeO 2 reported in the literature.

Ionic Conductivity Increased by Two Orders of Magnitude in Micrometer-Thick Vertical Yttria-Stabilized ZrO 2 Nanocomposite Films

DOE PAGES

Lee, Shinbuhm; Zhang, Wenrui; Khatkhatay, Fauzia; ...

2015-09-03

We design and create a unique cell geometry of templated micrometer-thick epitaxial nanocomposite films which contain ~20 nm diameter yttria-stabilized ZrO 2 (YSZ) nanocolumns, strain coupled to a SrTiO 3 matrix. We also enhanced the ionic conductivity of these nanocolumnsby over 2 orders of magnitude compared to plain YSZ films. Concomitant with the higher ionic conduction is the finding that the YSZ nanocolumns in the films have much higher crystallinity and orientation, compared to plain YSZ films. Hence, “oxygen migration highways” are formed in the desired out-of-plane direction. This improved structure is shown to originate from the epitaxial coupling ofmore » the YSZ nanocolumns to the SrTiO 3 film matrix and from nucleation of the YSZ nanocolumns on an intermediate nanocomposite base layer of highly aligned Sm-doped CeO 2 nanocolumns within the SrTiO 3 matrix. Furthermore, this intermediate layer reduces the lattice mismatch between the YSZ nanocolumns and the substrate. Vertical ionic conduction values as high as 10 –2 Ω –1 cm –1 were demonstrated at 360 °C (300 °C lower than plain YSZ films), showing the strong practical potential of these nanostructured films for use in much lower operation temperature ionic devices.« less

Surface Modification of Solution-Processed ZrO2 Films through Double Coating for Pentacene Thin-Film Transistors

NASA Astrophysics Data System (ADS)

Kwon, Jin-Hyuk; Bae, Jin-Hyuk; Lee, Hyeonju; Park, Jaehoon

2018-03-01

We report the modification of surface properties of solution-processed zirconium oxide (ZrO2) dielectric films achieved by using double-coating process. It is proven that the surface properties of the ZrO2 film are modified through the double-coating process; the surface roughness decreases and the surface energy increases. The present surface modification of the ZrO2 film contributes to an increase in grain size of the pentacene film, thereby increasing the field-effect mobility and decreasing the threshold voltage of the pentacene thin-film transistors (TFTs) having the ZrO2 gate dielectric. Herein, the molecular orientation of pentacene film is also studied based on the results of contact angle and X-ray diffraction measurements. Pentacene molecules on the double-coated ZrO2 film are found to be more tilted than those on the single-coated ZrO2 film, which is attributed to the surface modification of the ZrO2 film. However, no significant differences are observed in insulating properties between the single-and the double-coated ZrO2 dielectric films. Consequently, the characteristic improvements of the pentacene TFTs with the double-coated ZrO2 gate dielectric film can be understood through the increase in pentacene grain size and the reduction in grain boundary density.

Improved photocatalytic degradation rates of phenol achieved using novel porous ZrO2-doped TiO2 nanoparticulate powders.

PubMed

McManamon, Colm; Holmes, Justin D; Morris, Michael A

2011-10-15

This paper studies the photocatalytic degradation of phenol using zirconia-doped TiO(2) nanoparticles. ZrO(2) was chosen due to its promising results during preliminary studies. Particles smaller than 10nm were synthesised and doped with quantities of ZrO(2) ranging from 0.5 to 4% (molar metal content). Particles were calcined at different temperatures to alter the TiO(2) structure, from anatase to rutile, in order to provide an ideal ratio of the two phases. Powder X-ray diffraction (PXRD) analysis was used to examine the transformation between anatase and rutile. Degradation of phenol was carried out using a 40 W UV bulb at 365 nm and results were measured by UV-vis spectrometry. TEM images were obtained and show the particles exhibit a highly ordered structure. TiO(2) doped with 1% ZrO(2) (molar metal content) calcined at 700 °C proved to be the most efficient catalyst. This is due to an ideal anatase:rutlie ratio of 80:20, a large surface area and the existence of stable electron-hole pairs. ZrO(2) doping above the optimum loading acted as an electron-hole recombination centre for electron-hole pairs and reduced photocatalytic degradation. Synthesised photocatalysts compared favourably to the commercially available photocatalyst P25. The materials also demonstrated the ability to be recycled with similar results to those achieved on fresh material after 5 uses. Copyright © 2011 Elsevier B.V. All rights reserved.

Afterglow based detection and dosimetry of beta particle irradiated ZrO2.

PubMed

Salas-Juárez, Ch J; Cruz-Vázquez, C; Avilés-Monreal, R; Bernal, R

2018-08-01

In this work, we report on the afterglow (AG) response characterization of commercially available ZrO 2 . Pellet shaped samples previously annealed in air at 1000°C during 24h were exposed to beta particle irradiation in the dose range from 0.5 up to 128Gy and their AG decay curves recorded during 600s after irradiation exposure. The characteristic glow curves of beta particle irradiated ZrO 2 show two maxima located around 80°C and 150°C. The first one rapidly vanishes at room temperature, giving rise to AG. The integrated AG signal increases as dose increases from 0.5 to 128Gy, with a linear dependence from 0.5 up to ca. 32Gy. Excellent reproducibility of the AG response was observed in 10 irradiation - AG readout cycles, showing that the studied ZrO 2 samples are reusable. The results here presented show that ZrO 2 is a promising material for use as a radiation dosimeter based on the AG phenomenon. Copyright © 2017 Elsevier Ltd. All rights reserved.

Local epitaxial growth of ZrO2 on Ge (100) substrates by atomic layer epitaxy

NASA Astrophysics Data System (ADS)

Kim, Hyoungsub; Chui, Chi On; Saraswat, Krishna C.; McIntyre, Paul C.

2003-09-01

High-k dielectric deposition processes for gate dielectric preparation on Si surfaces usually result in the unavoidable and uncontrolled formation of a thin interfacial oxide layer. Atomic layer deposition of ˜55-Å ZrO2 film on a Ge (100) substrate using ZrCl4 and H2O at 300 °C was found to produce local epitaxial growth [(001) Ge//(001) ZrO2 and [100] Ge//[100] ZrO2] without a distinct interfacial layer, unlike the situation observed when ZrO2 is deposited using the same method on Si. Relatively large lattice mismatch (˜10%) between ZrO2 and Ge produced a high areal density of interfacial misfit dislocations. Large hysteresis (>200 mV) and high frequency dispersion were observed in capacitance-voltage measurements due to the high density of interface states. However, a low leakage current density, comparable to values obtained on Si substrates, was observed with the same capacitance density regardless of the high defect density.

Ultrasonic-assisted synthesis of ZrO2 nanoparticles and their application to improve the chemical stability of Nafion membrane in proton exchange membrane (PEM) fuel cells.

PubMed

Taghizadeh, Mohammad Taghi; Vatanparast, Morteza

2016-12-01

Zirconium dioxide (ZrO2) nanoparticles were fabricated successfully via ultrasonic-assisted method using ZrO(NO3)2·H2O, ethylenediamine and hydrazine as precursors in aqueous solution. Morphology, structure and composition of the obtained products were characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), dynamic light scattering (DLS), Fourier transform infrared spectroscopy (FT-IR) and diffuse reflectance spectroscopy (DRS). Then, the synthesized nanoparticles were used to prepare Nafion/ZrO2 nanocomposite membranes. The properties of the membranes were studied by ion exchange capacity (IEC) proton conductivity (σ), thermal stability and water uptake measurements. The ex-situ Fenton's test was used to investigate the chemical stability of the membranes. From our results, compared with Nafion membrane, the nanocomposite membrane exhibited lower fluoride release and weight loss. Therefore, it can concluded that Nafion/ZrO2 nanocomposite exhibit more chemical stability than the pure Nafion membrane. ATR-FTIR spectra and SEM surface images of membranes also confirm these results. Copyright © 2016 Elsevier Inc. All rights reserved.

Facile synthesis of highly stable and well-dispersed mesoporous ZrO(2)/carbon composites with high performance in oxidative dehydrogenation of ethylbenzene.

PubMed

Li, Qiang; Xu, Jie; Wu, Zhangxiong; Feng, Dan; Yang, Jianping; Wei, Jing; Wu, Qingling; Tu, Bo; Cao, Yong; Zhao, Dongyuan

2010-09-28

Highly ordered mesoporous ZrO(2)/carbon (FDU-15) composites have been synthesized via a facile evaporation induced triconstituent co-assembly (EISA) approach by using Pluronic F127 as a template and zirconium oxychloride octahydrate and resol as Zr and carbon sources. The synthesized mesoporous composites exhibit a highly ordered two-dimensional (2-D) hexagonal mesostructure with relatively high specific surface areas (up to 947 m(2) g(-1)), pore sizes around 3.8 nm and high pore volumes (up to 0.71 cm(3) g(-1)). The results clearly show that the crystalline zirconia nanoparticles (ca. 1.9-3.9 nm) are well-dispersed in amorphous matrices of the ordered mesoporous carbon FDU-15 materials, which construct the nanocomposites. The ordered mesostructures of the obtained ZrO(2)/FDU-15 composites can be well-retained even at the high pyrolysis temperature (up to 900 degrees C), suggesting a high thermal stability. The zirconia content of the ZrO(2)/FDU-15 composites can be tunable in a wide range (up to 47%). Moreover, the resultant mesoporous ZrO(2)/FDU-15 composites exhibit high catalytic activity in oxidative dehydrogenation (ODH) of ethylbenzene (EB) to styrene (ST), with high ethylbenzene conversion (59.6%) and styrene selectivity (90.4%), which is mainly attributed to the synergistic catalytic effect between the oxygen-containing groups located on the carbon pore walls and weakly basic sites of the nanocrystalline ZrO(2). Furthermore, the high specific surface areas and opening pore channels are also responsible for their high catalytic activity. Therefore, it is a very promising catalyst material in styrene production on an industrial scale.

Pulsed laser deposition of thick BaHfO3-doped YBa2Cu307-δ films on highly alloyed textured Ni-W tapes

NASA Astrophysics Data System (ADS)

Sieger, M.; Hänisch, J.; Iida, K.; Gaitzsch, U.; Rodig, C.; Schultz, L.; Holzapfel, B.; Hühne, R.

2014-05-01

YBa2Cu3O7-δ (YBCO) films with a thickness of up to 3 μm containing nano-sized BaHfO3 (BHO) have been grown on Y2O3/Y-stabilized ZrO2/CeO2 buffered Ni-9at% W tapes by pulsed laser deposition (PLD). Structural characterization by means of X-ray diffraction confirmed that the YBCO layer grew epitaxial. A superconducting transition temperature Tc of about 89 K with a transition width of 1 K was determined, decreasing with increasing BHO content. Critical current density in self-field and at 0.3 T increased with increasing dopant level.

An Atomistic-Scale Study for Thermal Conductivity and Thermochemical Compatibility in (DyY)Zr2O7 Combining an Experimental Approach with Theoretical Calculation.

PubMed

Qu, Liu; Choy, Kwang-Leong; Wheatley, Richard

2016-02-18

Ceramic oxides that have high-temperature capabilities can be deposited on the superalloy components in aero engines and diesel engines to advance engine efficiency and reduce fuel consumption. This paper aims to study doping effects of Dy(3+) and Y(3+)on the thermodynamic properties of ZrO2 synthesized via a sol-gel route for a better control of the stoichiometry, combined with molecular dynamics (MD) simulation for the calculation of theoretical properties. The thermal conductivity is investigated by the MD simulation and Clarke's model. This can improve the understanding of the microstructure and thermodynamic properties of (DyY)Zr2O7 (DYZ) at the atomistic level. The phonon-defect scattering and phonon-phonon scattering processes are investigated via the theoretical calculation, which provides an effective way to study thermal transport properties of ionic oxides. The measured and predicted thermal conductivity of DYZ is lower than that of 4 mol % Y2O3 stabilized ZrO2 (4YSZ). It is discovered that DYZ is thermochemically compatible with Al2O3 at 1300 °C, whereas at 1350 °C DYZ reacts with Al2O3 forming a small amount of new phases.

An Atomistic-Scale Study for Thermal Conductivity and Thermochemical Compatibility in (DyY)Zr2O7 Combining an Experimental Approach with Theoretical Calculation

PubMed Central

Qu, Liu; Choy, Kwang-Leong; Wheatley, Richard

2016-01-01

Ceramic oxides that have high-temperature capabilities can be deposited on the superalloy components in aero engines and diesel engines to advance engine efficiency and reduce fuel consumption. This paper aims to study doping effects of Dy3+ and Y3+on the thermodynamic properties of ZrO2 synthesized via a sol-gel route for a better control of the stoichiometry, combined with molecular dynamics (MD) simulation for the calculation of theoretical properties. The thermal conductivity is investigated by the MD simulation and Clarke’s model. This can improve the understanding of the microstructure and thermodynamic properties of (DyY)Zr2O7 (DYZ) at the atomistic level. The phonon-defect scattering and phonon-phonon scattering processes are investigated via the theoretical calculation, which provides an effective way to study thermal transport properties of ionic oxides. The measured and predicted thermal conductivity of DYZ is lower than that of 4 mol % Y2O3 stabilized ZrO2 (4YSZ). It is discovered that DYZ is thermochemically compatible with Al2O3 at 1300 °C, whereas at 1350 °C DYZ reacts with Al2O3 forming a small amount of new phases. PMID:26888438

Stress analysis of ZrO2/SiO2 multilayers deposited on different substrates with different thickness periods

NASA Astrophysics Data System (ADS)

Shao, Shuying; Shao, Jianda; He, Hongbo; Fan, Zhengxiu

2005-08-01

The effects of repeating thickness periods on stress are studied in ZrO2/SiO2 multilayers deposited by electron-beam evaporation on BK7 glass and fused-silica substrates. The results show that the residual stress is compressive and decreases with an increase of the periods of repeating thickness in the ZrO2/SiO2 multilayers. At the same time, the residual stress in multilayers deposited on BK7 glass is less than that of samples deposited on fused silica. The variation of the microstructure examined by x-ray diffraction shows that microscopic deformation does not correspond to macroscopic stress, which may be due to variation of the interface stress.

Atomic layer deposition of ZrO2 on W for metal-insulator-metal capacitor application

NASA Astrophysics Data System (ADS)

Lee, Sang-Yun; Kim, Hyoungsub; McIntyre, Paul C.; Saraswat, Krishna C.; Byun, Jeong-Soo

2003-04-01

A metal-insulator-metal (MIM) capacitor using ZrO2 on tungsten (W) metal bottom electrode was demonstrated and characterized in this letter. Both ZrO2 and W metal were synthesized by an atomic layer deposition (ALD) method. High-quality 110˜115 Å ZrO2 films were grown uniformly on ALD W using ZrCl4 and H2O precursors at 300 °C, and polycrystalline ZrO2 in the ALD regime could be obtained. A 13˜14-Å-thick interfacial layer between ZrO2 and W was observed after fabrication, and it was identified as WOx through angle-resolved x-ray photoelectron spectroscopy analysis with wet chemical etching. The apparent equivalent oxide thickness was 20˜21 Å. An effective dielectric constant of 22˜25 including an interfacial WOx layer was obtained by measuring capacitance and thickness of MIM capacitors with Pt top electrodes. High capacitance per area (16˜17 fF/μm2) and low leakage current (10-7 A/cm2 at ±1 V) were achieved.

High Temperature Degradation of Advanced Thermal and Environmental Barrier Coatings (TEBCs) by CaO-MgO-Al2O3-SiO2 (CMAS)

NASA Technical Reports Server (NTRS)

Costa, Gustavo; Zhu, Dongming

2017-01-01

There is increasing interest in the degradation studies of thermal and environmental barrier coatings (TEBCs) of gas turbines by molten CaO-MgO-Al2O3-SiO2 (CMAS). CMAS minerals are usually referred as silica-containing sand dust and volcano ash materials that are carried by the intake air into gas turbines, e.g. aircraft engines. The low-melting deposits react at high temperatures (1000C) with the coating materials. This causes degradation and accelerated coating failure of the static and rotating components of the turbine engines. We discuss some preliminary results of the reactions between CMAS and Rare-Earth (RE Y, Yb, Dy, Gd, Nd and Sm) oxide stabilized ZrO2 or HfO2 systems, and the stability of the resulting oxides and silicates. Plasma sprayed hollow tube samples (outer diameter 4.7 mm, wall thickness 0.76 mm and 26 mm height) were half filled with CMAS powder, wrapped and sealed with platinum foil, and heat- treated at 1310 C for 5h. Samples were characterized by differential scanning calorimetry, X-ray diffraction and cross section electron microscopy analysis.

High-Temperature Particulate Matter Filtration with Resilient Yttria-Stabilized ZrO2 Nanofiber Sponge.

PubMed

Wang, Haolun; Lin, Sen; Yang, Shen; Yang, Xudong; Song, Jianan; Wang, Dong; Wang, Haiyang; Liu, Zhenglian; Li, Bo; Fang, Minghao; Wang, Ning; Wu, Hui

2018-05-01

Particulate matter (PM) is a major air pollutant in many regions, jeopardizing ecosystems and public health. Filtration at pollutant source is one of the most important ways to protect the environment, however, considering the high-temperature exhaust gas emissions, effective removal of PM and related pollutants from their sources remains a major challenge. In this study, a resilient, heat-resisting, and high-efficiency PM filter based on yttria-stabilized ZrO 2 (YSZ) nanofiber sponge produced with a scalable solution blow spinning process is reported. The porous 3D sponge composed of YSZ nanofibers is lightweight (density of 20 mg cm -3 ) and resilient at both room temperature and high temperatures. At room-temperature conditions, the YSZ nanofiber sponge exhibits 99.4% filtration efficiency for aerosol particles with size in the range of 20-600 nm, associated with a low pressure drop of only 57 Pa under an airflow velocity of 4.8 cm s -1 . At a high temperature of 750 °C, the ceramic sponge maintains a high filtration efficiency of 99.97% for PM 0.3-2.5 under a high airflow velocity of 10 cm s -1 . A practical vehicle exhaust filter to capture particles with filtration efficiency of >98.3% is also assembled. Hence, the YSZ nanofiber sponge has enormous potential to be applied in industry. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Hydrothermal synthesis of Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} nanotubes for enhanced photoluminescence properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gao, Linhui, E-mail: gaolhui@zstu.edu.cn; Wang, Guangfa; Zhu, Hongliang

Highlights: • Eu{sup 3+} doped Y{sub 2}O{sub 3} nanotubes. • Hydrothermal synthesis of Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} nanostructures assissted with a further heat treatment. • Tunable coating ratios of Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} nanophosphor. • Enhanced photoluminescence intensity of Y{sub 2}O{sub 3}:Eu{sup 3+} more than 60% by Y{sub 2}O{sub 3} surface coating. - Abstract: Novel Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} nanotubes with different coating ratios were synthesized successfully by a facile two-step process, including hydrothermal synthesis of Y(OH){sub 3} coated Y(OH){sub 3}:Eu{sup 3+} as precursors and then calcination ofmore » them at 1000 °C for 2 h. X-ray diffraction patterns and field emission scanning electron microscope images indicated these Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} phosphors possess tubular nanostructures. The photoluminescence properties of Y{sub 2}O{sub 3} coated Y{sub 2}O{sub 3}:Eu{sup 3+} were systematically investigated by photoluminescence spectra, and photoluminescence enhancement was observed after proper coating. In other words, the coating ratio played a crucial role in photoluminescence efficiency. When it was 1/9, the photoluminescence intensity of {sup 5}D{sub 0} → {sup 7}F{sub 2} emission (about 613 nm) was 60% higher than that of Y{sub 2}O{sub 3}: Eu{sup 3+} phosphors under 255 nm excitation. Therefore, surface coating may be an alternative route for enhanced photoluminescence properties of the Y{sub 2}O{sub 3}:Eu{sup 3+} red-emitting phosphor.« less

Electrical characteristics and thermal stability of n+ polycrystalline- Si/ZrO2/SiO2/Si metal-oxide-semiconductor capacitors

NASA Astrophysics Data System (ADS)

Lim, Kwan-Yong; Park, Dae-Gyu; Cho, Heung-Jae; Kim, Joong-Jung; Yang, Jun-Mo; Ii, Choi-Sang; Yeo, In-Seok; Park, Jin Won

2002-01-01

We have investigated the thermal stability of n+ polycrystalline-Si(poly-Si)/ZrO2(50-140 Å)/SiO2(7 Å)/p-Si metal-oxide-semiconductor (MOS) capacitors via electrical and material characterization. The ZrO2 gate dielectric was prepared by atomic layer chemical vapor deposition using ZrCl4 and H2O vapor. Capacitance-voltage hysteresis as small as ˜12 mV with the flatband voltage of -0.5 V and the interface trap density of ˜5×1010cm-2 eV-1 were attained with activation anneal at 750 °C. A high level of gate leakage current was observed at the activation temperatures over 750 °C and attributed to the interfacial reaction of poly-Si and ZrO2 during the poly-Si deposition and the following high temperature anneal. Because of this, the ZrO2 gate dielectric is incompatible with the conventional poly-Si gate process. In the MOS capacitors having a smaller active area (<50×50 μm2), fortunately, the electrical degradation by further severe silicidation does not occur up to an 800 °C anneal in N2 for 30 min.

Dimensional stability and electrochemical behaviour of ZrO2 incorporated electrospun PVdF-HFP based nanocomposite polymer membrane electrolyte for Li-ion capacitors

PubMed Central

Solarajan, Arun Kumar; Murugadoss, Vignesh; Angaiah, Subramania

2017-01-01

Different weight percentages of ZrO2 (0, 3, 5, 7 and 10 wt%) incorporated electrospun PVDF-HFP nanocomposite polymer membranes (esCPMs) were prepared by electrospinning technique. They were activated by soaking in 1 M LiPF6 containing 1:1 volume ratio of EC : DMC (ethylene carbonate:dimethyl carbonate) to get electrospun nanocomposite polymer membrane electrolytes (esCPMEs). The influence of ZrO2 on the physical, mechanical and electrochemical properties of esCPM was studied in detail. Finally, coin type Li-ion capacitor cell was assembled using LiCo0.2Mn1.8O4 as the cathode, Activated carbon as the anode and the esCPME containing 7 wt% of ZrO2 as the separator, which delivered a discharge capacitance of 182.5 Fg−1 at the current density of 1Ag−1 and retained 92% of its initial discharge capacitance even after 2,000 cycles. It revealed that the electrospun PVdF-HFP/ZrO2 based nanocomposite membrane electrolyte could be used as a good candidate for high performance Li-ion capacitors. PMID:28397783

Electronic structure of a laterally graded ZrO2-TiO2 film on Si(100) prepared by metal-organic chemical vapor deposition in ultrahigh vacuum

NASA Astrophysics Data System (ADS)

Richter, J. H.; Karlsson, P. G.; Sandell, A.

2008-05-01

A TiO2-ZrO2 film with laterally graded stoichiometry has been prepared by metal-organic chemical vapor deposition in ultrahigh vacuum. The film was characterized in situ using synchrotron radiation photoelectron spectroscopy (PES) and x-ray absorption spectroscopy. PES depth profiling clearly shows that Ti ions segregate toward the surface region when mixed with ZrO2. The binding energy of the ZrO2 electronic levels is constant with respect to the local vacuum level. The binding energy of the TiO2 electronic levels is aligned to the Fermi level down to a Ti /Zr ratio of about 0.5. At a Ti /Zr ratio between 0.1 and 0.5, the TiO2 related electronic levels become aligned to the local vacuum level. The addition of small amounts of TiO2 to ZrO2 results in a ZrO2 band alignment relative to the Fermi level that is less asymmetric than for pure ZrO2. The band edge positions shift by -0.6eV for a Ti /Zr ratio of 0.03. This is explained in terms of an increase in the work function when adding TiO2, an effect that becomes emphasized by Ti surface segregation.

Structural and dielectric properties of thin ZrO2 films on silicon grown by atomic layer deposition from cyclopentadienyl precursor

NASA Astrophysics Data System (ADS)

Niinistö, J.; Putkonen, M.; Niinistö, L.; Kukli, K.; Ritala, M.; Leskelä, M.

2004-01-01

ZrO2 thin films with thicknesses below 20 nm were deposited by the atomic layer deposition process on Si(100) substrates at 350 °C. An organometallic precursor, Cp2Zr(CH3)2 (Cp=cyclopentadienyl, C5H5) was used as the zirconium source and water or ozone as oxygen source. The influence of oxygen source and substrate pretreatment on the dielectric properties of ZrO2 films was investigated. Structural characterization with high-resolution transmission electron microscopy was performed to films grown onto HF-etched or native oxide covered silicon. Strong inhibition of ZrO2 film growth was observed with the water process on HF-etched Si. Ozone process on HF-etched Si resulted in interfacial SiO2 formation between the dense and uniform film and the substrate while water process produced interfacial layer with intermixing of SiO2 and ZrO2. The effective permittivity of ZrO2 in Al/ZrO2/Si/Al capacitor structures was dependent on the ZrO2 layer thickness and oxygen source used. The interfacial layer formation increased the capacitance equivalent oxide thickness (CET). CET of 2.0 nm was achieved with 5.9 nm ZrO2 film deposited with the H2O process on HF-stripped Si. The ozone-processed films showed good dielectric properties such as low hysteresis and nearly ideal flatband voltage. The leakage current density was lower and breakdown field higher for the ozone-processed ZrO2 films.

Low-temperature, solution-processed ZrO2:B thin film: a bifunctional inorganic/organic interfacial glue for flexible thin-film transistors.

PubMed

Park, Jee Ho; Oh, Jin Young; Han, Sun Woong; Lee, Tae Il; Baik, Hong Koo

2015-03-04

A solution-processed boron-doped peroxo-zirconium oxide (ZrO2:B) thin film has been found to have multifunctional characteristics, providing both hydrophobic surface modification and a chemical glue layer. Specifically, a ZrO2:B thin film deposited on a hydrophobic layer becomes superhydrophilic following ultraviolet-ozone (UVO) treatment, whereas the same treatment has no effect on the hydrophobicity of the hydrophobic layer alone. Investigation of the ZrO2:B/hydrophobic interface layer using angle-resolved X-ray photoelectron spectroscopy (AR XPS) confirmed it to be chemically bonded like glue. Using the multifunctional nature of the ZrO2:B thin film, flexible amorphous indium oxide (In2O3) thin-film transistors (TFTs) were subsequently fabricated on a polyimide substrate along with a ZrO2:B/poly-4-vinylphenol (PVP) dielectric. An aqueous In2O3 solution was successfully coated onto the ZrO2:B/PVP dielectric, and the surface and chemical properties of the PVP and ZrO2:B thin films were analyzed by contact angle measurement, atomic force microscopy (AFM), Fourier transform infrared (FT-IR) spectroscopy, and X-ray photoelectron spectroscopy (XPS). The surface-engineered PVP dielectric was found to have a lower leakage current density (Jleak) of 4.38 × 10(-8) A/cm(2) at 1 MV/cm, with no breakdown behavior observed up to a bending radius of 5 mm. In contrast, the electrical characteristics of the flexible amorphous In2O3 TFT such as on/off current ratio (Ion/off) and electron mobility remained similar up to 10 mm of bending without degradation, with the device being nonactivated at a bending radius of 5 mm. These results suggest that ZrO2:B thin films could be used for low-temperature, solution-processed surface-modified flexible devices.

ZrO2 nanoparticles labeled via a native protein corona: detection by fluorescence microscopy and Raman microspectroscopy in rat lungs.

PubMed

Silge, Anja; Bräutigam, Katharina; Bocklitz, Thomas; Rösch, Petra; Vennemann, Antje; Schmitz, Inge; Popp, Jürgen; Wiemann, Martin

2015-08-07

ZrO2 nanoparticles are frequently used in composite materials such as dental fillers from where they may be released and inhaled upon polishing and grinding. Since the overall distribution of ZrO2 NP inside the lung parenchyma can hardly be observed by routine histology, here a labeling with a fluorphore was used secondary to the adsorption of serum proteins. Particles were then intratracheally instilled into rat lungs. After 3 h fluorescent structures consisted of agglomerates scattered throughout the lung parenchyma, which were mainly concentrated in alveolar macrophages after 3 d. A detection method based on Raman microspectroscopy was established to investigate the chemical composition of those fluorescent structures in detail. Raman measurements were arranged such that no spectral interference with the protein-bound fluorescence label was evident. Applying chemometrical methods, Raman signals of the ZrO2 nanomaterial were co-localized with the fluorescence label, indicating the stability of the nanomaterial-protein-dye complex inside the rat lung. The combination of Raman microspectroscopy and adsorptive fluorescence labeling may, therefore, become a useful tool for studying the localization of protein-coated nanomaterials in cells and tissues.

Effect of zirconia morphology on sulfur-resistant methanation performance of MoO3/ZrO2 catalyst

NASA Astrophysics Data System (ADS)

Liu, Chen; Wang, Weihan; Xu, Yan; Li, Zhenhua; Wang, Baowei; Ma, Xinbin

2018-05-01

Two kinds of ZrO2 support with different morphologies were prepared by facile solvothermal method in different solvents. The obtained two supports showed monoclinic zirconia (m-ZrO2) and tetragonal zirconia (t-ZrO2) phase with similar crystalline size. Their supported Mo-based catalysts were prepared by impregnation method and the effect of zirconia morphology on the performance of sulfur-resistant methanation was examined. The results indicated that the MoO3/m-ZrO2 has higher CO conversion than the MoO3/t-ZrO2 catalyst. Characterizations by XRD, Raman, H2-TPR and IR confirmed that the m-ZrO2 is superior to t-ZrO2 for dispersing molybdenum species. In addition, the MoO3/m-ZrO2 catalyst has weaker interaction between support and active Mo speices than the MoO3/t-ZrO2 catalyst, which facilitates to forming active species of nanocrystalline MoS2 layers for sulfur-resistant methanation. The weaker interaction of molybdenum species with m-ZrO2 is related with the more covalent character of the Zrsbnd O bond and more oxygen defective structure of m-ZrO2. A larger number of Lewis acid centers appear on the surface of m-ZrO2, which verified the substantial vacancies on m-ZrO2 exposing coordinately unsaturated Zr3+ and Zr4+ cations. Meanwhile, the less Lewis acid of t-ZrO2 result in stronger interaction between support and molybdenum species and trigger crystalline phase MoO3 and Mosbnd Osbnd Zr linkages.

About properties of ZrO2 thermal protective coatings obtained from spherical powder mixtures

NASA Astrophysics Data System (ADS)

Berdnik, O. B.; Tsareva, I. N.; Tarasenko, Yu P.

2017-05-01

It is developed the technology of high-energy plasma spraying of the zirconium dioxide (ZrO2) thermal protective coating on the basis of ZrO2 tetragonal and cubic phases with the spheroidal grain shape and the columnar substructure, with the total porosity P = 4 %, the hardness HV = 12 GPa, the roughness parameter R a ˜ 6 μm, the thickness 0.3-3 mm. As a sublayer it is used the heat-resistant coating of “Ni-Co-Cr-Al-Y” system with an intermetallic phase composition and the layered microstructure of the grains.

Phase study of SiO2-ZrO2 composites prepared from polymorphic combination of starting powders via a ball-milling followed by calcination

NASA Astrophysics Data System (ADS)

Musyarofah; Nurlaila, R.; Muwwaqor, N. F.; Saukani, M.; Kuswoyo, A.; Triwikantoro; Pratapa, S.

2017-04-01

The effects of SiO2-ZrO2 polymorphic combinations as starting powders and calcination temperature on phase composition of the SiO2-ZrO2 composites were studied. Stoichiometric (1:1 mol%) mixtures of the SiO2-ZrO2 composites were mechanically activated using a ball-milling for 5 h followed by calcinations at 1000, 1100 and 1200 °C for 3 h. The composites used in the present study were a-SiO2+ a-ZrO2, a-SiO2+ t-ZrO2, c-SiO2+ a-ZrO2 and c-SiO2+ t-ZrO2 which were symbolized by AA, AT, CA and CT, respectively. Prefixes a, t and c denote amorphous, tetragonal and cristobalite, respectively. The phase composition was determined by Rietveld analysis of X-ray diffraction (XRD) data using Rietica software. The identified phases for all calcined samples were a combination among t-ZrO2, c-SiO2, m-ZrO2 and zircon (ZrSiO4). Amorphous zirconia formed a transient tetragonal zirconia phase during heating, which reacted with silica to form zircon. The zircon phase was not found to form even at 1200 °C in the AT and CT mixtures and at 1100 °C in the CA mixture. The AA mixture in particular crystallized to form zircon at a lower temperature with more composition fraction than the others, ca 82.9 (14) mol%.

Facile biological synthetic strategy to morphologically aligned CeO2/ZrO2 core nanoparticles using Justicia adhatoda extract and ionic liquid: Enhancement of its bio-medical properties.

PubMed

Pandiyan, Nithya; Murugesan, Balaji; Sonamuthu, Jegatheeswaran; Samayanan, Selvam; Mahalingam, Sundrarajan

2018-01-01

In this study, a typical green synthesis route has approached for CeO 2 /ZrO 2 core metal oxide nanoparticles using ionic liquid mediated Justicia adhatoda extract. This synthesis method is carried out at simple room temperature condition to obtain the core metal oxide nanoparticles. XRD, SEM and TEM studies employed to study the crystalline and surface morphological properties under nucleation, growth, and aggregation processes. CeO 2 /ZrO 2 core metal oxides display agglomerated nano stick-like structure with 20-45nm size. GC-MS spectroscopy confirms the presence of vasicinone and N,N-Dimethylglycine present in the plant extract, which are capable of converting the corresponding metal ion precursor to CeO 2 /ZrO 2 core metal oxide nanoparticles. In FTIR, the corresponding stretching for Ce-O and Zr-O bands indicated at 498 and 416cm -1 and Raman spectroscopy also supports typical stretching frequencies at 463 and 160cm -1 . Band gap energy of the CeO 2 /ZrO 2 core metal oxide is 3.37eV calculated from UV- DRS spectroscopy. The anti-bacterial studies performed against a set of bacterial strains the result showed that core metal oxide nanoparticles more susceptible to gram-positive (G+) bacteria than gram-negative (G-) bacteria. A unique feature of the antioxidant behaviors core metal oxides reduces the concentration of DPPH radical up to 89%. The CeO 2 /ZrO 2 core metal oxide nanoparticles control the S. marcescent bio-film formation and restrict the quorum sensing. The toxicology behavior of CeO 2 /ZrO 2 core metal oxide NPs is found due to the high oxygen site vacancies, ROS formation, smallest particle size and higher surface area. This type of green synthesis route may efficient and the core metal oxide nanoparticles will possess a good bio-medical agent in future. Copyright © 2017 Elsevier B.V. All rights reserved.

Effect of the ZrCl4 concentration in the (NaCl-KCl)eqiv-UO2Cl2-ZrCl4 melt and the electrolysis current density on the quantitative composition of UO2-ZrO2 cathode deposits. Calculation and experiment

NASA Astrophysics Data System (ADS)

Krotov, V. E.; Filatov, E. C.

2014-08-01

A method is proposed for calculating the ZrO2 content in the (NaCl-KCl)eqiv-UO2Cl2-ZrCl4 melt. Based on the known composition of a UO2-ZrO2 cathode deposit, the content is calculated at current densities of 0.08-0.63 A/cm2 and ZrCl4 concentrations of 0-12.3 wt %. The calculated and experimental ZrO2 contents in UO2-ZrO2 cathode deposits are in qualitative and adequate quantitative agreement.

Ion-enhanced chemical etching of ZrO2 in a chlorine discharge

NASA Astrophysics Data System (ADS)

Sha, Lin; Cho, Byeong-Ok; Chang, Jane P.

2002-09-01

Chlorine plasma is found to chemically etch ZrO2 thin films in an electron cyclotron resonance reactor, and the etch rate scaled linearly with the square root of ion energy at high ion energies with a threshold energy between 12-20 eV. The etching rate decreased monotonically with increasing chamber pressures, which corresponds to reduced electron temperatures. Optical emission spectroscopy and quadrupole mass spectrometry were used to identify the reaction etching products. No Zr, O, or ZrCl were detected as etching products, but highly chlorinated zirconium compounds (ZrCl2, ZrCl3, and ZrCl4) and ClO were found to be the dominant etching products. ZrCl3 was the dominant etching products at low ion energies, while ZrCl4 became dominant at higher ion energies. This is consistent with greater momentum transfer and enhanced surface chlorination, as determined by x-ray photoelectron spectroscopy, at increased ion energies. Several ion-enhanced chemical reactions are proposed to contribute to the ZrO2 etching. copyright 2002 American Vacuum Society.

The improvement of retention time of metal-ferroelectric (PbZr0.53Ti0.47O3)-insulator (ZrO2)-semiconductor transistors and capacitors by leakage current reduction using surface treatment

NASA Astrophysics Data System (ADS)

Shih, Wen-Chieh; Kang, Kun-Yung; Lee, Joseph Ya-Min

2007-11-01

Metal-ferroelectric-insulator-semiconductor transistors (MFISFETs) and capacitors with the structure of Al /Pb (Zr0.53,Ti0.47) O3/ZrO2/Si were fabricated. The wafers were pretreated with H2O2 before ZrO2 deposition and/or post-treated with HCl after ZrO2 deposition. The leakage current density at 5V is reduced from 10-1to5×10-6A /cm2. The subthreshold slope was improved to 91mV/decade. The MFISFETs maintain a threshold voltage window of about 1.1V after an elapsed time of 3000s. The mobility is 267cm2/Vs. The improvements are most likely due to the reduction of interfacial layer thickness and the interface states at the ZrO2/Si interface.

Polymorphism in the Sc 2Si 2O 7-Y 2Si 2O 7 system

NASA Astrophysics Data System (ADS)

Escudero, Alberto; Alba, María D.; Becerro, Ana. I.

2007-04-01

This paper examines the structural changes with temperature and composition in the Sc 2Si 2O 7-Y 2Si 2O 7 system; members of this system are expected to form in the intergranular region of Si 3N 4 and SiC structural ceramics when sintered with the aid of Y 2O 3 and Sc 2O 3 mixtures. A set of different compositions have been synthesized using the sol-gel method to obtain a xerogel, which has been calcined at temperatures between 1300 and 1750 °C during different times. The temperature-composition diagram of the system, obtained from powder XRD data, is dominated by the β- RE2Si 2O 7 polymorph, with γ- RE2Si 2O 7 and δ- RE2Si 2O 7 showing very reduced stability fields. Isotherms at 1300 and 1600 °C have been analysed in detail to evaluate the solid solubility of the components. Although, the XRD data show a complete solid solubility of β-Sc 2Si 2O 7 in β-Y 2Si 2O 7 at 1300 °C, the 29Si MAS-NMR spectra indicate a local structural change at x ca. 1.15 (Sc 2-xY xSi 2O 7) related to the configuration of the Si tetrahedron, which does not affect the long-range order of the β- RE2Si 2O 7 structure. Finally, it is interesting to note that, although Sc 2Si 2O 7 shows a unique stable polymorph ( β), Sc 3+ is able to replace Y 3+ in γ-Y 2Si 2O 7 in the compositional range 1.86⩽ x⩽2 (where x is Sc 2-xY xSi 2O 7) as well as in δ-Y 2Si 2O 7 for compositions much closer to the pure Y 2Si 2O 7.

Structural and dielectric properties of CTAB modified ZrO2 nanoparticles

NASA Astrophysics Data System (ADS)

Sidhu, Gaganpreet Kaur; Tripathi, S. K.; Kumar, Rajesh

2016-05-01

Zirconia (ZrO2) has been considered as one of the most investigated materials among various metal oxides due its outstanding dielectric properties and ionic conduction properties, which is mainly due to its high oxygen ion conduction. ZrO2 nanoparticles were synthesized using surfactant (CTAB) to study the variation of its dielectric behavior at room temperature. Surfactants form a unique class of chemical compounds, because of their remarkable ability to influence the properties of surfaces and interfaces of nanostructures. The dielectric properties of prepared nanoparticles were studied using LCR meter.

Photoelectron spectroscopy and density functional theory study of TiAlO(y) (-) (y=1-3) and TiAl(2)O(y) (-) (y=2-3) clusters.

PubMed

Zhang, Zeng-Guang; Xu, Hong-Guang; Zhao, Yuchao; Zheng, Weijun

2010-10-21

Small titanium-aluminum oxide clusters, TiAlO(y) (-) (y=1-3) and TiAl(2)O(y) (-) (y=2-3), were studied by using anion photoelectron spectroscopy. The adiabatic detachment energies of TiAlO(y) (-) (y=1-3) were estimated to be 1.11±0.05, 1.70±0.08, and 2.47±0.08eV based on their photoelectron spectra; those of TiAl(2)O(2) (-) and TiAl(2)O(3) (-) were estimated to be 1.17±0.08 and 2.2±0.1eV, respectively. The structures of these clusters were determined by comparison of density functional calculations with the experimental results. The structure of TiAlO(-) is nearly linear with the O atom in the middle. That of TiAlO(2) (-) is a kite-shaped structure. TiAlO(3) (-) has a kite-shaped TiAlO(2) unit with the third O atom attaching to the Ti atom. TiAl(2)O(2) (-) has two nearly degenerate Al-O-Ti-O-Al chain structures that can be considered as cis and trans forms. TiAl(2)O(3) (-) has two low-lying isomers, kite structure and book structure. The structures of these clusters indicate that the Ti atom tends to bind to more O atoms.

Amorphization of nanocrystalline monoclinic ZrO2 by swift heavy ion irradiation.

PubMed

Lu, Fengyuan; Wang, Jianwei; Lang, Maik; Toulemonde, Marcel; Namavar, Fereydoon; Trautmann, Christina; Zhang, Jiaming; Ewing, Rodney C; Lian, Jie

2012-09-21

Bulk ZrO(2) polymorphs generally have an extremely high amorphization tolerance upon low energy ion and swift heavy ion irradiation in which ballistic interaction and ionization radiation dominate the ion-solid interaction, respectively. However, under very high-energy irradiation by 1.33 GeV U-238, nanocrystalline (40-50 nm) monoclinic ZrO(2) can be amorphized. A computational simulation based on a thermal spike model reveals that the strong ionizing radiation from swift heavy ions with a very high electronic energy loss of 52.2 keV nm(-1) can induce transient zones with temperatures well above the ZrO(2) melting point. The extreme electronic energy loss, coupled with the high energy state of the nanostructured materials and a high thermal confinement due to the less effective heat transport within the transient hot zone, may eventually be responsible for the ionizing radiation-induced amorphization without transforming to the tetragonal polymorph. The amorphization of nanocrystalline zirconia was also confirmed by 1.69 GeV Au ion irradiation with the electronic energy loss of 40 keV nm(-1). These results suggest that highly radiation tolerant materials in bulk forms, such as ZrO(2), may be radiation sensitive with the reduced length scale down to the nano-metered regime upon irradiation above a threshold value of electronic energy loss.

Electrochemical corrosion, wear and cell behavior of ZrO2/TiO2 alloyed layer on Ti-6Al-4V.

PubMed

Li, Jianfang; He, Xiaojing; Zhang, Guannan; Hang, Ruiqiang; Huang, Xiaobo; Tang, Bin; Zhang, Xiangyu

2018-06-01

Ti-6Al-4V (TC4) has received increasing attention as biomaterial but also raised concerns about the long-term safety of releasing of metal ions and poor wear resistance. In this work, an ZrO 2 /TiO 2 alloyed layer was prepared on TC4 by plasma surface alloying with Zr and subsequently annealed in the air for improved corrosion and wear resistant. To assess the corrosion performance of the alloyed layer, the specimens were measured by open circuit potential, electrochemical impedance spectroscopy and potentiodynamic polarization in simulated body fluid solution. The result shows that the ZrO 2 /TiO 2 alloyed layer exhibits strikingly high polarization resistance, wide passive region and very low current density, indicating the excellent corrosion resistance. The layer also displays significant improvement of wear resistance. Furthermore, the alloyed layer restricts cell adhesion and spreading. We infer that the ZrO 2 /TiO 2 alloyed layer might be potentially useful implanted devices such as biosensors, bioelectronics or drug delivery devices. Copyright © 2018 Elsevier B.V. All rights reserved.

Synthesis of Transparent Aqueous ZrO2 Nanodispersion with a Controllable Crystalline Phase without Modification for a High-Refractive-Index Nanocomposite Film.

PubMed

Xia, Yi; Zhang, Cong; Wang, Jie-Xin; Wang, Dan; Zeng, Xiao-Fei; Chen, Jian-Feng

2018-05-30

The controllable synthesis of metal oxide nanoparticles is of fundamental and technological interest. In this article, highly transparent aqueous nanodispersion of ZrO 2 with controllable crystalline phase, high concentration, and long-term stability was facilely prepared without any modification via the reaction of inexpensive inorganic zirconium salt and sodium hydroxide in water under an acid surrounding, combined with hydrothermal treatment. The as-prepared transparent nanodispersion had an average particle size of 7 nm, a high stability of 18 months, and a high solid content of 35 wt %. ZrO 2 nanocrystals could be readily dispersed in many solvents with high polarity including ethanol, dimethyl sulfoxide, acetic acid, ethylene glycol, and N, N-dimethylformamide, forming stable transparent nanodispersions. Furthermore, highly transparent polyvinyl alcohol/ZrO 2 nanocomposite films with high refractive index were successfully prepared with a simple solution mixing route. The refractive index could be tuned from 1.528 to 1.754 (@ 589 nm) by changing the mass fraction (0-80 wt %) of ZrO 2 in transparent nanocomposite films.

Catalytic ethanolysis and gasification of kraft lignin into aromatic alcohols and H2-rich gas over Rh supported on La2O3/CeO2-ZrO2.

PubMed

Yang, Jing; Zhao, Liang; Liu, Chunze; Wang, Yuanyuan; Dai, Liyi

2016-10-01

Efficient catalytic ethanolysis and gasification of kraft lignin were conducted over a versatile supported catalyst Rh/La2O3/CeO2-ZrO2 to give high-value aromatic alcohols and H2-rich gas. The removal of phenolic hydroxyl group was the most prevalent reaction, and importantly, almost no phenols, undesired char and saturating the aromatic ring were detected. Meanwhile, the feedstock and solvent both played key roles in H2 generation that contributed to the hydrodeoxygenation of liquid components and made the whole catalytic process out of H2 supply. Reusability tests of catalyst indicated that the crystalline phase transition and agglomeration of support, the loss of noble metal Rh and carbon deposition were the possible reasons for its deactivation in supercritical ethanol. Comparing with water, methanol and isopropanol system, ethanol was the only effective solvent for the depolymerization process. Copyright © 2016 Elsevier Ltd. All rights reserved.

Thermodynamic approach to the stability of multi-phase systems. Application to the Y 2O 3–Fe system

DOE PAGES

Samolyuk, German D.; Osetskiy, Yury N.

2015-07-07

Oxide-metal systems (OMSs) are important in many practical applications, and therefore, are under extensive studies using a wide range of techniques. The most accurate theoretical approaches are based on density functional theory (DFT), which are limited to ~10 2 atoms. Multi-scale approaches, e.g., DFT+Monte Carlo, are often used to model OMSs at the atomic level. These approaches can describe qualitatively the kinetics of some processes but not the overall stability of OMSs. In this paper, we propose a thermodynamic approach to study equilibrium in multiphase systems, which can be sequentially enhanced by considering different defects and microstructures. We estimate themore » thermodynamic equilibrium by minimization the free energy of the whole multiphase system using a limited set of defects and microstructural objects for which the properties are calculated by DFT. As an example, we consider Y 2O 3+bcc Fe with vacancies in both the Y 2O 3 and bcc Fe phases, Y substitutions and O interstitials in Fe, Fe impurities and antisite defects in Y 2O 3. The output of these calculations is the thermal equilibrium concentration of all the defects for a particular temperature and composition. The results obtained confirmed the high temperature stability of yttria in iron. As a result, model development towards more accurate calculations is discussed.« less