Study of deposition of YBa2Cu3O7-x on cubic zirconia

NASA Technical Reports Server (NTRS)

Warner, Joseph D.; Meola, Joseph E.; Jenkins, Kimberly A.

1989-01-01

Films of YBa2Cu3O7-x were grown on (100) cubic zirconia with 8 percent yttria by laser ablation from sintered targets of YBa2Cu3O7-x. The temperature of the zirconia substrate during growth was varied between 700 and 780 C. The atmosphere during growth was 170 mtorr of O2. The films were subsequently slowly cooled in-situ in 1 atm of O2. The best films were c-axis aligned and had a transition temperature of 87.7 K. The superconducting transition temperature and the X-ray diffraction analysis is reported as a function of the substrate temperature and of the angle between the laser beam and the target's normal.

Desorption of oxygen from YBa2Cu3O6+x films studied by Raman spectroscopy

NASA Astrophysics Data System (ADS)

Bock, A.; Kürsten, R.; Brühl, M.; Dieckmann, N.; Merkt, U.

1996-08-01

Phonons of laser-deposited YBa2Cu3O6+x films on MgO(100) substrates are investigated in a Raman setup as a function of laser power density. Investigations of YBa2Cu3O7 films allow us to study oxygen out-diffusion, where the onset of out-diffusion is indicated by the appearance of disorder-induced modes in the Raman spectra. At a pressure of 5×10-6 mbar the temperature threshold of the out-diffusion is (490+/-15) K. With increasing oxygen pressure the observed temperature thresholds rise only moderately in contrast to the behavior expected from the pox-T phase diagram of YBa2Cu3O6+x. Even at 1 bar oxygen partial pressure out-diffusion is observed and tetragonal sites with x=0 develop. These observations can be explained by photon-stimulated desorption of oxygen. Investigations of YBa2Cu3O6 films allow us to study oxygen in-diffusion. In 1 bar oxygen we observe competing oxygen fluxes due to thermally activated diffusion and photon-stimulated desorption. From these measurements we determine an upper bound of the thermal activation energy of the oxygen in-diffusion into YBa2Cu3O6 films of (0.19+/-0.01) eV.

Superconducting YBa2Cu3O7- δ Thin Film Detectors for Picosecond THz Pulses

NASA Astrophysics Data System (ADS)

Probst, P.; Scheuring, A.; Hofherr, M.; Wünsch, S.; Il'in, K.; Semenov, A.; Hübers, H.-W.; Judin, V.; Müller, A.-S.; Hänisch, J.; Holzapfel, B.; Siegel, M.

2012-06-01

Ultra-fast THz detectors from superconducting YBa2Cu3O7- δ (YBCO) thin films were developed to monitor picosecond THz pulses. YBCO thin films were optimized by the introduction of CeO2 and PrBaCuO buffer layers. The transition temperature of 10 nm thick films reaches 79 K. A 15 nm thick YBCO microbridge (transition temperature—83 K, critical current density at 77 K—2.4 MA/cm2) embedded in a planar log-spiral antenna was used to detect pulsed THz radiation of the ANKA storage ring. First time resolved measurements of the multi-bunch filling pattern are presented.

Critical current density in (YBa2Cu3O7-δ)1-x-(PrBa2Cu3O7-δ)x melt-textured composites

NASA Astrophysics Data System (ADS)

Opata, Yuri Aparecido; Monteiro, João Frederico Haas Leandro; Jurelo, Alcione Roberto; Siqueira, Ezequiel Costa

2018-06-01

Melt textured (YBa2Cu3O7-δ)1-x-(PrBa2Cu3O7-δ)x composites (x = 0.00 and x = 0.05) were grown using the top seeding method. The effect of the PrBa2Cu3O7-δ phase on the growth process and the modification of the microstructure as well as on the physical properties was analyzed. X-ray analyses indicated that both pure and Pr-doped samples present an orthorhombic superconducting phase. From resistivity measurements for YBa2Cu3O7-δ and (YBa2Cu3O7-δ)0.95-(PrBa2Cu3O7-δ)0.05 samples, the Tcab did not change and was around 90.5 K. However, from magnetic measurements, the superconductivity was observed in critical temperatures TC = 92.9 K and 92.4 K for YBa2Cu3O7-δ and (YBa2Cu3O7-δ)0.95-(PrBa2Cu3O7-δ)0.05 samples, respectively. The YBa2Cu3O7-δ sample showed higher critical current densities than those shown by the (YBa2Cu3O7-δ)0.95-(PrBa2Cu3O7-δ)0.05 sample, with values of JC = 5.85 × 105 A/cm2 and 4.72 × 105 A/cm2, respectively. This paper also discusses the importance of Pr substitution on nano- and micro-meter scales to enhance JC(H).

Fabrication and characterization of La2Zr2O7 films on different buffer architectures for YBa2Cu3O7-δ coated conductors by RF magnetron sputtering.

PubMed

Xu, Da; Liu, Linfei; Xiao, Guina; Li, Yijie

2013-02-27

La2Zr2O7 (LZO) films were grown on different buffer architectures by radio frequency magnetron sputtering for the large-scale application of YBa2Cu3O7-x (YBCO)-coated conductors. The three different buffer architectures were cerium oxide (CeO2), yttria-stabilized zirconia (YSZ)/CeO2, and CeO2/YSZ/CeO2. The microstructure and surface morphology of the LZO film were studied by X-ray diffraction, optical microscopy, field emission scanning electron microscopy, and atomic force microscopy. The LZO films prepared on the CeO2, YSZ/CeO2, and CeO2/YSZ/CeO2 buffer architectures were preferentially c-axis-oriented and highly textured. The in-plane texture of LZO film on CeO2 single-buffer architecture was ∆ φ = 5.5° and the out-of-plane texture was ∆ ω = 3.4°. All the LZO films had very smooth surfaces, but LZO films grown on YSZ/CeO2 and CeO2/YSZ/CeO2 buffer architectures had cracks. The highly textured LZO film grown on CeO2-seed buffered NiW tape was suitable for the epitaxial growth of YBCO film with high currents.

Preparation of YBa2Cu3O7 High Tc Superconducting Coatings by Plasma Spraying

NASA Astrophysics Data System (ADS)

Danroc, J.; Lacombe, J.

The following sections are included: * INTRODUCTION * THE COMPOUND YBa2Cu3O7-δ * Structure * Critical temperature * Critical current density * Phase equilibria in the YBaCuO system * PREPARATION OF YBa2Cu3O7 COATINGS * General organisation of the preparation process * The powder * Hot plasma spraying of YBa2Cu3O7 * The post-spraying thermal treatment * CHARACTERISTICS OF THE YBa2Cu3O7-δ COATINGS * Chemical composition * Crystalline structure * Morphology of the coatings * Electrical and magnetic characteristics * Conclusion * REFERENCES

YBa2Cu3O7 thin films on nanocrystalline diamond films for HTSC bolometer

NASA Technical Reports Server (NTRS)

Cui, G.; Beetz, C. P., Jr.; Boerstler, R.; Steinbeck, J.

1993-01-01

Superconducting YBa2Cu3O(7-x) films on nanocrystalline diamond thin films have been fabricated. A composite buffer layer system consisting of diamond/Si3N4/YSZ/YBCO was explored for this purpose. The as-deposited YBCO films were superconducting with Tc of about 84 K and a relatively narrow transition width of about 8 K. SEM cross sections of the films showed very sharp interfaces between diamond/Si3N4 and between Si3N4/YSZ. The deposited YBCO film had a surface roughness of about 1000 A, which is suitable for high-temperature superconductive (HTSC) bolometer fabrication. It was also found that preannealing of the nanocrystalline diamond thin films at high temperature was very important for obtaining high-quality YBCO films.

Cation disorder and gas phase equilibrium in an YBa 2Cu 3O 7- x superconducting thin film

NASA Astrophysics Data System (ADS)

Shin, Dong Chan; Ki Park, Yong; Park, Jong-Chul; Kang, Suk-Joong L.; Yong Yoon, Duk

1997-02-01

YBa 2Cu 3O 7- x superconducting thin films have been grown by in situ off-axis rf sputtering with varying oxygen pressure, Ba/Y ratio in a target, and deposition temperature. With decreasing oxygen pressure, increasing Ba/Y ratio, increasing deposition temperature, the critical temperature of the thin films decreased and the c-axis length increased. The property change of films with the variation of deposition variables has been explained by a gas phase equilibrium of the oxidation reaction of Ba and Y. Applying Le Chatelier's principle to the oxidation reaction, we were able to predict the relation of deposition variables and the resultant properties of thin films; the prediction was in good agreement with the experimental results. From the relation between the three deposition variables and gas phase equilibrium, a 3-dimensional processing diagram was introduced. This diagram has shown that the optimum deposition condition of YBa 2Cu 3O 7- x thin films is not a fixed point but can be varied. The gas phase equilibrium can also be applied to the explanation of previous results that good quality films were obtained at low deposition temperature using active species, such as O, O 3, and O 2+.

Epitaxial YBa2Cu3O7-x nanocomposite films and coated conductors from BaMO3 (M = Zr, Hf) colloidal solutions

NASA Astrophysics Data System (ADS)

Obradors, X.; Puig, T.; Li, Z.; Pop, C.; Mundet, B.; Chamorro, N.; Vallés, F.; Coll, M.; Ricart, S.; Vallejo, B.; Pino, F.; Palau, A.; Gázquez, J.; Ros, J.; Usoskin, A.

2018-04-01

Superconducting nanocomposites are the best material choice to address the performance required in power applications and magnets working under high magnetic fields. However, it is still challenging to sort out how to achieve the highest superconducting performance using attractive and competitive manufacturing processes. Colloidal solutions have been recently developed as a novel and very promising low cost route to manufacture nanocomposite coated conductors. Well dispersed and stabilized preformance nanoparticle solutions are first prepared with high concentrations and then mixed with the YBa2Cu3O7 metalorganic precursor solutions to generate colloidal solutions to grow the nanocomposite films. Here we demonstrate, for the first time, that non-reactive BaZrO3 and BaHfO3 perovskite preformed nanoparticles are suitable for growing high quality thin and thick films, and coated conductors with a homogeneous distribution and controlled particle size using this fabrication method. Additionally, we extend the nanoparticle content of the nanocomposites up to 20%-25% mol without any degradation of the superconducting properties. Thick nanocomposite films, up to 0.8 μm, have been prepared with a single deposition of low-fluorine solutions using an ink jet printing dispenser and we demonstrate that the preformed nanoparticles display only a very limited coarsening during the growth process and so high critical current densities J c (B) under high magnetic fields. These films show the highest critical currents achieved so far based on the colloidal solution approach, I c = 220 A/cm-w at 77 K and self-field, and they still have a high potential for further increase in the film thickness. Finally, we also show that nanocomposite YBa2Cu3O7-BaZrO3 coated conductors based on an alternating beam assisted deposited YSZ buffer layer on stainless steel metallic substrates can be developed based on these novel colloidal solutions. Non-reactive preformed oxide perovskite

Millimeter-wave surface resistance of laser-ablated YBa2Cu3O(7-delta) superconducting films

NASA Technical Reports Server (NTRS)

Miranda, F. A.; Gordon, W. L.; Bhasin, K. B.; Warner, J. D.

1990-01-01

The millimeter-wave surface resistance of YBa2Cu3O(7-delta) superconducting films was measured in a gold-plated copper host cavity at 58.6 GHz between 25 and 300 K. High-quality laser-ablated films of 1.2-micron thickness were deposited on SrTiO3 and LaGaO3 substrates. Their transition temperatures were 90.0 and 88.9 K, with a surface resistance at 70 K of 82 and 116 milliohms, respectively. These values are better than the values for the gold-plated cavity at the same temperature and frequency.

Flux Pinning Enhancement in YBa2Cu3O7-x Films with BaSnO3 Nanoparticles

DTIC Science & Technology

2008-10-01

SUPERCONDUCTOR SCIENCE AND TECHNOLOGY Supercond. Sci. Technol. 19 (2006) L37 –L41 doi:10.1088/0953-2048/19/10/L01 RAPID COMMUNICATION Flux pinning enhancement in...2006 Online at stacks.iop.org/SUST/19/ L37 Abstract Nanoparticles of BaSnO3 were incorporated into YBa2Cu3O7−x (YBCO) films on LaAlO3 substrates for...0953-2048/06/100037+05$30.00 © 2006 IOP Publishing Ltd Printed in the UK L37 1 Rapid Communication materials and sintered together to form a composite

Transformational dynamics of BZO and BHO nanorods imposed by Y2O3 nanoparticles for improved isotropic pinning in YBa2Cu3O7 -δ thin films

NASA Astrophysics Data System (ADS)

Gautam, Bibek; Sebastian, Mary Ann; Chen, Shihong; Shi, Jack; Haugan, Timothy; Xing, Zhongwen; Zhang, Wenrui; Huang, Jijie; Wang, Haiyan; Osofsky, Mike; Prestigiacomo, Joseph; Wu, Judy Z.

2017-07-01

An elastic strain model was applied to evaluate the rigidity of the c-axis aligned one-dimensional artificial pinning centers (1D-APCs) in YBa2Cu3O7-δ matrix films. Higher rigidity was predicted for BaZrO3 1D-APCs than that of the BaHfO3 1D-APCs. This suggests a secondary APC doping of Y2O3 in the 1D-APC/YBa2Cu3O7-δ nanocomposite films would generate a stronger perturbation to the c-axis alignment of the BaHfO3 1D-APCs and therefore a more isotropic magnetic vortex pinning landscape. In order to experimentally confirm this, we have made a comparative study of the critical current density Jc (H, θ, T) of 2 vol.% BaZrO3 + 3 vol.%Y2O3 and 2 vol.%BaHfO3 + 3 vol.%Y2O3 double-doped (DD) YBa2Cu3O7-δ films deposited at their optimal growth conditions. A much enhanced isotropic pinning was observed in the BaHfO3 DD samples. For example, at 65 K and 9.0 T, the variation of the Jc across the entire θ range from θ=0 (H//c) to θ=90 degree (H//ab) is less than 18% for BaHfO3 DD films, in contrast to about 100% for the BaZrO3 DD counterpart. In addition, lower α values from the Jc(H) ˜ H-α fitting were observed in the BaHfO3 DD films in a large θ range away from the H//c-axis. Since the two samples have comparable Jc values at H//c-axis, the improved isotropic pinning in BaHfO3 DD films confirms the theoretically predicted higher tunability of the BaHfO3 1D-APCs in APC/YBa2Cu3O7-δ nanocomposite films.

Wet chemical techniques for passivation of YBa2Cu3O7(7-x)

NASA Technical Reports Server (NTRS)

Vasquez, R. P.; Foote, M. C.; Hunt, B. D.

1989-01-01

Wet chemical techniques are described for treatment of YBa2Cu3O(7-x) surfaces, resulting in the formation of native compounds with little or no reactivity to water. Promising native compounds include CuI, BaSO4, CuS, Cu2S, and the oxalates, all of which are either insoluble or have very low solubility in water. Treatment with dilute HI results in the formation of a native iodide film which is 80-90 percent CuI with small amounts of YI3 and BaI2. Treatment with dilute H2SO4 results in the formation of a film which is 95 percent BaSO4 and 5 percent Y2(SO4)3. Cu2S is formed on the surface with a dilute Na2S solution. An oxalate film with equal amounts of Y2(C2O4)3 and BaC2O4 results from treatment with dilute oxalic acid. X-ray photoelectron spectra show no significant changes when the sulfide, sulfate, or oxalate films are dipped in water, while the iodide film shows evidence of Cu(OH)2 formation.

Single liquid source plasma-enhanced metalorganic chemical vapor deposition of high-quality YBa2Cu3O(7-x) thin films

NASA Technical Reports Server (NTRS)

Zhang, Jiming; Gardiner, Robin A.; Kirlin, Peter S.; Boerstler, Robert W.; Steinbeck, John

1992-01-01

High quality YBa2Cu3O(7-x) films were grown in-situ on LaAlO3 (100) by a novel single liquid source plasma-enhanced metalorganic chemical vapor deposition process. The metalorganic complexes M(thd) (sub n), (thd = 2,2,6,6-tetramethyl-3,5-heptanedionate; M = Y, Ba, Cu) were dissolved in an organic solution and injected into a vaporizer immediately upstream of the reactor inlet. The single liquid source technique dramatically simplifies current CVD processing and can significantly improve the process reproducibility. X-ray diffraction measurements indicated that single phase, highly c-axis oriented YBa2Cu3O(7-x) was formed in-situ at substrate temperature 680 C. The as-deposited films exhibited a mirror-like surface, had transition temperature T(sub cO) approximately equal to 89 K, Delta T(sub c) less than 1 K, and Jc (77 K) = 10(exp 6) A/sq cm.

Growth, patterning, and weak-link fabrication of superconducting YBa2Cu3O(7-x) thin films

NASA Astrophysics Data System (ADS)

Hilton, G. C.; Harris, E. B.; van Harlingen, D. J.

1988-09-01

Thin films of the high-temperature superconducting ceramic oxides have been grown, and techniques for fabricating weak-link structures have been investigated. Films of YBa2Cu3O(7-x) grown on SrTiO3 by a combination of dc magnetron sputtering and thermal evaporation from the three sources have been patterned into microbridges with widths down to 2 microns. Evidence is found that the bridges behave as arrays of Josephson-coupled superconducting islands. Further weak-link behavior is induced by in situ modification of the coupling by ion milling through the bridge.

Flux Pinning Enhancement in YBa2Cu3O7-x Films for Coated Conductor Applications (Postprint)

DTIC Science & Technology

2010-01-01

YBa2Cu3O7–x Films for Coated Conductor Applications Maiorov , B. , Civale , L. , Lin , Y. , Hawley , M.E. , Maley , M.P. , and Peterson , D.E...L. , Maiorov , B. , Hawley , M.E. , Maley , M.P. , and Peterson , D.E. ( 2004 ) Nat. Mater. , 3 , 439 . 30 Kang , S. , Goyal...1864 . 47 Civale , L. , Maiorov , B. , Serquis , A. , Willis , J.O. , Coulter , J.Y. , Wang , H. , Jia , Q.X. , Arendt , P.N

Ellipsometric study of YBa2Cu3O(7-x) laser ablated and co-evaporated films

NASA Technical Reports Server (NTRS)

Alterovitz, S. A.; Sieg, R. E.; Warner, J. D.; Stan, M. A.; Vitta, S.

1990-01-01

High temperature superconducting films of YBa2Cu3O(7-x) (YBCO were grown on SrTiO3, LaA1O3, and YSZ substrates using two techniques: excimer laser ablation with in situ annealing and co-evaporation of Y, Cu, and BaF2 with ex-situ annealing. Film thicknesses were typically 5000 A, with predominant c-axis alignment perpendicular to the substrate. Critical temperatures up to Tc(R=O)=90 K were achieved by both techniques. Ellipsometric measurements were taken in the range 1.6 to 4.3 eV using a variable angle spectroscopic ellipsometer. The complex dielectric function of the laser ablated films was reproducible from run to run, and was found to be within 10 percent of that previously reported for (001) oriented single crystals. A dielectric overlayer was observed in these films, with an index of refraction of approximately 1.55 and nearly zero absorption. For the laser ablated films the optical properties were essentially independent of substrate material. The magnitude of the dielectric function obtained for the co-evaported films was much lower than the value reported for single crystals, and was sample dependent.

Coaxial line configuration for microwave power transmission study of YBa2Cu3O(7-delta) thin films

NASA Technical Reports Server (NTRS)

Chorey, C. M.; Miranda, F. A.; Bhasin, K. B.

1991-01-01

Microwave transmission measurements through YBa2Cu3O(7-delta) (YBCO) high-transition-temperature superconducting thin films on lanthanum aluminate (LaAlO3) have been performed in a coaxial line at 10 GHz. LaAlO3 substrates were ultrasonically machined into washer-shaped discs, polished, and coated with laser-ablated YBCO. These samples were mounted in a 50-ohm coaxial air line to form a short circuit. The power transmitted through the films as a function of temperature was used to calculate the normal state conductivity and the magnetic penetration depth for the films.

Atomic-scale identification of novel planar defect phases in heteroepitaxial YBa2Cu3O7-δ thin films

NASA Astrophysics Data System (ADS)

Gauquelin, Nicolas; Zhang, Hao; Zhu, Guozhen; Wei, John Y. T.; Botton, Gianluigi A.

2018-05-01

We have discovered two novel types of planar defects that appear in heteroepitaxial YBa2Cu3O7-δ (YBCO123) thin films, grown by pulsed-laser deposition (PLD) either with or without a La2/3Ca1/3MnO3 (LCMO) overlayer, using the combination of high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) imaging and electron energy loss spectroscopy (EELS) mapping for unambiguous identification. These planar lattice defects are based on the intergrowth of either a BaO plane between two CuO chains or multiple Y-O layers between two CuO2 planes, resulting in non-stoichiometric layer sequences that could directly impact the high-Tc superconductivity.

Laser ablated YBa2Cu3O(7-x) high temperature superconductor coplanar waveguide resonator

NASA Technical Reports Server (NTRS)

Valco, G. J.; Blemker, A. R.; Bhasin, K. B.

1992-01-01

Several 8.8-GHz coplanar waveguide resonators are fabricated and tested that are made from laser ablated YBa2Cu3O(7-x) thin films on LaAlO3 substrates. A quality factor of 1250 at 77 K was measured. A correlation between the microwave performance of the resonators and the critical temperature and morphology of the films was observed.

Low-pressure large-area magnetron sputter deposition of YBa2Cu3O7-δ films for industrial applications

NASA Astrophysics Data System (ADS)

Wördenweber, Roger; Hollmann, Eugen; Poltiasev, Michael; Neumüller, Heinz-Werner

2003-05-01

This paper addresses the development of a technically relevant sputter-deposition process for YBa2Cu3O7-delta films. First, the simulation of the particle transport from target to substrate indicates that only at a reduced pressure of p approx 1-10 Pa can a sufficiently large deposition rate and homogeneous stoichiometric distribution of the particles during large-area deposition be expected. The results of the simulations are generally confirmed by deposition experiments on CeO2 buffered sapphire and LaAlO3 substrates using a magnetron sputtering system suitable for large-area deposition. However, it is shown that in addition to the effect of scattering during particle transport, the conditions at the substrate lead to a selective growth of Y-Ba-Cu-O phases that, among others, strongly affect the growth rate. For example, the growth rate is more than three times larger for optimized parameters compared to the same set of parameters but at 100 K lower substrate temperature. Stoichiometrical and structural perfect films can be grown at low pressure (p < 10 Pa). However, the superconducting transition temperature of these films is reduced. The Tc reduction seems to be correlated with the c-axis length of YBa2Cu3O7-delta. Two possible explanations for the increased c-axis length and the correlated reduced transition temperature are discussed, i.e. reduced oxygen content and strong cation site disorder due to the heavy particle bombardment.

Pulsed laser deposition of thick BaHfO3-doped YBa2Cu307-δ films on highly alloyed textured Ni-W tapes

NASA Astrophysics Data System (ADS)

Sieger, M.; Hänisch, J.; Iida, K.; Gaitzsch, U.; Rodig, C.; Schultz, L.; Holzapfel, B.; Hühne, R.

2014-05-01

YBa2Cu3O7-δ (YBCO) films with a thickness of up to 3 μm containing nano-sized BaHfO3 (BHO) have been grown on Y2O3/Y-stabilized ZrO2/CeO2 buffered Ni-9at% W tapes by pulsed laser deposition (PLD). Structural characterization by means of X-ray diffraction confirmed that the YBCO layer grew epitaxial. A superconducting transition temperature Tc of about 89 K with a transition width of 1 K was determined, decreasing with increasing BHO content. Critical current density in self-field and at 0.3 T increased with increasing dopant level.

Secondary ion mass spectroscopy study of Au trapping and migration in the Au-irradiated YBa2Cu3O7 - delta film

NASA Astrophysics Data System (ADS)

Li, Yupu; Kilner, J. A.; Liu, J. R.; Chu, W. K.; Wagner, G. A.; Somekh, R. E.

1996-05-01

The range data and migration of Au in YBa2Cu3O7-δ film were studied with implanted 197Au (1.5 MeV 5×1015 Au+/cm2) as a tracer. The film was a c-axis oriented film, ˜750 nm thick, deposited by high-pressure planar dc sputtering on <100> LaAlO3. Analysis by secondary ion mass spectroscopy shows that the as-implanted Au concentration distribution is essentially Gaussian-like and the depth (R̂p) of maximum Au concentration (˜1.2 wt %) is 201 nm. The projected range (R¯p) and (R̂p) are found to be in very good agreement with the simulated data by TRIM-95, whereas the measured ``straggle'' (ΔRp*) is about 20% larger than that by TRIM-95 simulation. It has also been found that the implanted 197Au starts to migrate within the film at a temperature between 650 and 700 °C, which is much higher than that for the implanted 2H (˜175 °C) and the implanted 18O (between 250 and 300 °C) in c-oriented YBa2Cu3O7-δ films.

Observation of a three-dimensional quasi-long-range electronic supermodulation in YBa 2Cu 3O 7-x/La 0.7Ca 0.3MnO 3 heterostructures

DOE Office of Scientific and Technical Information (OSTI.GOV)

He, Junfeng; Shafer, Padraic; Mion, Thomas R.

Recent developments in high-temperature superconductivity highlight a generic tendency of the cuprates to develop competing electronic (charge) supermodulations. While coupled with the lattice and showing different characteristics in different materials, these supermodulations themselves are generally conceived to be quasi-two-dimensional, residing mainly in individual CuO 2 planes, and poorly correlated along the c axis. Here we observed with resonant elastic X-ray scattering a distinct type of electronic supermodulation in YBa 2Cu 3O 7–x (YBCO) thin films grown epitaxially on La 0.7Ca 0.3MnO 3 (LCMO). This supermodulation has a periodicity nearly commensurate with four lattice constants in-plane, eight out of plane, withmore » long correlation lengths in three dimensions. It sets in far above the superconducting transition temperature and competes with superconductivity below this temperature for electronic states predominantly in the CuO 2 plane. Our finding sheds light on the nature of charge ordering in cuprates as well as a reported long-range proximity effect between superconductivity and ferromagnetism in YBCO/LCMO heterostructures.« less

Observation of a three-dimensional quasi-long-range electronic supermodulation in YBa 2Cu 3O 7-x/La 0.7Ca 0.3MnO 3 heterostructures

DOE PAGES

He, Junfeng; Shafer, Padraic; Mion, Thomas R.; ...

2016-03-01

Recent developments in high-temperature superconductivity highlight a generic tendency of the cuprates to develop competing electronic (charge) supermodulations. While coupled with the lattice and showing different characteristics in different materials, these supermodulations themselves are generally conceived to be quasi-two-dimensional, residing mainly in individual CuO 2 planes, and poorly correlated along the c axis. Here we observed with resonant elastic X-ray scattering a distinct type of electronic supermodulation in YBa 2Cu 3O 7–x (YBCO) thin films grown epitaxially on La 0.7Ca 0.3MnO 3 (LCMO). This supermodulation has a periodicity nearly commensurate with four lattice constants in-plane, eight out of plane, withmore » long correlation lengths in three dimensions. It sets in far above the superconducting transition temperature and competes with superconductivity below this temperature for electronic states predominantly in the CuO 2 plane. Our finding sheds light on the nature of charge ordering in cuprates as well as a reported long-range proximity effect between superconductivity and ferromagnetism in YBCO/LCMO heterostructures.« less

Critical current density enhancement by phase decomposition of YBa 2Cu 4O 8 into YBa 2Cu 3O 7-σ and CuO

NASA Astrophysics Data System (ADS)

Krelaus, J.; Heinemann, K.; Ullmann, B.; Freyhardt, H. C.

1995-02-01

Bulk YBa 2Cu 4O 8 (Y-124) is prepared from YBa 2Cu 3O 7-σ (Y-123) and CuO by a powder-metallurgical method. The superconducting features of the Y-124, in particular critical current densities and activation energies, are measured resistively using a four-probe technique and magnetically using a Faraday magnetometer. In a second step the Y-124 is decomposed at high temperatures. The intragranular critical current density is measured at different annealing times, tA, in order to determine and discuss the characteristics of the jc( tA) curves.

Geometric and compositional factors on critical current density in YBa2Cu3O7‑δ films containing nanorods

NASA Astrophysics Data System (ADS)

Horide, Tomoya; Nagao, Sho; Izutsu, Ryosuke; Ishimaru, Manabu; Kita, Ryusuke; Matsumoto, Kaname

2018-06-01

Critical current density (J c) was investigated in YBa2Cu3O7‑δ films containing nanorods prepared with various nanorod materials, with variation of nanorod content, substrate temperature, and oxidization condition. Three types of compositional situation were realized: films containing strain induced oxygen vacancies; fully oxidized films containing cation compositional deviation; and oxygen deficient films. Normalized J c‑B behavior was determined via the matching field, which is a geometric factor, regardless of the compositional details. A J c‑critical temperature (T c) relation depending on distribution and fraction of compositional deviation (cation compositional deviation and strain induced oxygen vacancies) was found: the J c values decreased with decreasing T c due to the effect of T c on nanorod pinning strength in the fully oxidized films; J c decreased with decreasing oxygen pressure in the film cooling process after film deposition in spite of T c remaining almost the same, due to reduction of the effective area for current flow in the oxygen deficient films. Thus, a J c landscape based on geometric and compositional factors was obtained. The study highlights the importance of the J c‑T c analysis in the understanding of J c in YBa2Cu3O7‑δ films containing nanorods.

Near-edge study of gold-substituted YBa2Cu3O(7-delta)

NASA Technical Reports Server (NTRS)

Ruckman, Mark W.; Hepp, Aloysius F.

1991-01-01

The valence of Cu and Au in YBa2Au0.3Cu2.7O7-delta was investigated using X-ray absorption near edge structure (XANES). X-ray and neutron diffraction studies indicate that Au goes on the Cu(1) site and Cu K-edge XANES shows that this has little effect on the oxidation state of the remaining copper. The Au L3 edge develops a white line feature whose position lies between that of trivalent gold oxide and monovalent potassium gold cyanide, and whose height relative to the edge step is smaller than in the two reference compounds. The appearance of the Au L3 edge suggests that fewer Au 3d states are involved in forming the Au-O bond in YBa2Au0.3Cu2.7O7-delta than in trivalent gold oxide.

Near-edge study of gold-substituted YBa2Cu3O(7-delta)

NASA Technical Reports Server (NTRS)

Ruckman, Mark W.; Hepp, Aloysius F.

1991-01-01

The valence of Cu and Au in YBa2Au0.3Cu2.7O7-delta was investigated using x-ray absorption near edge structure (XANES). X-ray and neutron diffraction studies indicate that Au goes on the Cu(1) site and Cu K-edge XANES shows that this has little effect on the oxidation state of the remaining copper. The Au L3 edge develops a white line feature whose position lies between that of trivalent gold oxide and monovalent potassium gold cyanide, and whose height relative to the edge step is smaller than in the two reference compounds. The appearance of the Au L3 edge suggests that fewer Au 3d states are involved in forming the Au-O bond in YBa2Au0.3Cu2.7O7-delta than in trivalent gold oxide.

Physical properties of YBa 2Cu 3O 7- δ thin films using microstrip ring resonators technique

NASA Astrophysics Data System (ADS)

Lai, L. S.; Zeng, H. K.; Juang, J. Y.; Wu, K. H.; Uen, T. M.; Lin, J. Y.; Gou, Y. S.

2006-09-01

Microstrip ring resonators with quality factor ( Q) over 10 4 at temperature 5 K, were fabricated using the double-side YBa 2Cu 3O 7- δ (YBCO) epitaxial films deposited on LaAlO 3 (LAO) substrates. By placing a narrow gap in the ring resonator, we observed that the original fundamental resonating mode (resonance frequency f = 3.61 GHz) splits into a dual-mode with different resonating frequencies ( f = 1.80 GHz and f = 5.33 GHz). These two kinds of the resonator allow us to determine the temperature and frequency dependences of the magnetic penetration depth λ( T, f) and the surface loss. Several salient features of the above findings related to the nature of low-lying excitations for high- Tc superconductivity as a function of oxygen content will be elucidated. In particular, the current models, suggested by Wen and Lee, will be examined in a quantitative manner. It allows us to give a justification of quasiparticle as Fermi-liquid in the superconducting state. In addition, an equivalent inductance circuit model is suggested to account for the occurrence of the dual-mode resonance.

Synthesis of high-oxidation Y-Ba-Cu-O phases in superoxygenated thin films

NASA Astrophysics Data System (ADS)

Zhang, H.; Gauquelin, N.; McMahon, C.; Hawthorn, D. G.; Botton, G. A.; Wei, J. Y. T.

2018-03-01

It is known that solid-state reaction in high-pressure oxygen can stabilize high-oxidation phases of Y-Ba-Cu-O superconductors in powder form. We extend this superoxygenation concept of synthesis to thin films which, due to their large surface-to-volume ratio, are more reactive thermodynamically. Epitaxial thin films of YBa2Cu3O7 -δ grown by pulsed laser deposition are annealed at up to 700 atm O2 and 900 ∘C , in conjunction with Cu enrichment by solid-state diffusion. The films show the clear formation of Y2Ba4Cu7O15 -δ and Y2Ba4Cu8O16 as well as regions of YBa2Cu5O9 -δ and YBa2Cu6O10 -δ phases, according to scanning transmission electron microscopy, x-ray diffraction, and x-ray absorption spectroscopy. Similarly annealed YBa2Cu3O7 -δ powders show no phase conversion. Our results demonstrate a route of synthesis towards discovering more complex phases of cuprates and other superconducting oxides.

Reduced reactivity to air on HF-treated YBa2Cu3O(7-x)surfaces

NASA Technical Reports Server (NTRS)

Vasquez, R. P.; Hunt, B. D.; Foote, M. C.

1989-01-01

Treatment of YBa2Cu3O(7-x) films with a nonaqueous solution of HF in absolute ethanol results in the formation of an oxyfluoride with relative Y:Ba:Cu concentrations of 1:4:3 on the surface, as determined by X-ray photoelectron spectroscopy. The passivation properties of chemically treated films were tested by monitoring the growth of the high binding energy O 1s peak, associated with nonsuperconducting surface species, as a function of air exposure time, for both HF-treated and untreated films. The native oxyfluoride is shown to reduce the reactivity of the superconductor to air.

Growth and patterning of laser ablated superconducting YBa2Cu3O7 films on LaAlO3 substrates

NASA Technical Reports Server (NTRS)

Warner, J. D.; Bhasin, K. B.; Varaljay, N. C.; Bohman, D. Y.; Chorey, C. M.

1989-01-01

A high quality superconducting film on a substrate with a low dielectric constant is desired for passive microwave circuit applications. In addition, it is essential that the patterning process does not effect the superconducting properties of the thin films to achieve the highest circuit operating temperatures. YBa2Cu3O7 superconducting films were grown on lanthanum aluminate substrates using laser ablation with resulting maximum transition temperature (T sub c) of 90 K. The films were grown on a LaAlO3 which was at 775 C and in 170 mtorr of oxygen and slowly cooled to room temperature in 1 atm of oxygen. These films were then processed using photolithography and a negative photoresist with an etch solution of bromine and ethanol. Results are presented on the effect of the processing on T(sub c) of the film and the microwave properties of the patterned films.

Positron trapping in Y1-xPrxBa2Cu3O7-δ and the Fermi surface of YBa2Cu3O7-δ

NASA Astrophysics Data System (ADS)

Shukla, A.; Hoffmann, L.; Manuel, A. A.; Walker, E.; Barbiellini, B.; Peter, M.

1995-03-01

Temperature-dependent positron lifetime measurements in ceramic Y1-xPrxBa2Cu3O7-δ samples reveal positron trapping, in particular at low temperature and for small x. Positrons appear to be completely delocalized for T~400 K and higher. At high temperatures the lifetime for YBa2Cu3O7-δ and PrBa2Cu3O7-δ is identical (~165 ps) and close to the theoretical value. For these reasons a two-dimensional angular correlation of annihilation radiation (2D-ACAR) spectrum was measured in YBa2Cu3O7 at T=400 K. The spectrum width confirms the delocalization of the positron and the 2D-ACAR shows, apart from the one-dimensional Fermi surface due to CuO chains, a smaller Fermi surface sheet centered around the S point, in the first Brillouin zone.

Low resistivity contacts to YBa2Cu3O(7-x) superconductors

NASA Technical Reports Server (NTRS)

Hsi, Chi-Shiung; Haertling, Gene H.

1991-01-01

Silver, gold, platinum, and palladium metals were investigated as electroding materials for the YBa2Cu3O(7-x) superconductors. Painting, embedding, and melting techniques were used to apply the electrodes. Contact resistivities were determined by: (1) type of electrode; (2) firing conditions; and (3) application method. Electrodes fired for long times exhibited lower contact resistivities than those fired for short times. Low-resistivity contacts were found for silver and gold electrodes. Silver, which made good ohmic contact to the YBa2Cu3O(7-x) superconductor with low contact resistivities was found to be the best electroding material among the materials evaluated in this investigation.

Laser ablated high T(sub c) superconducting thin YBa2Cu3O(7-x) films on substrates suitable for microwave applications

NASA Astrophysics Data System (ADS)

Warner, J. D.; Meola, J. E.; Jenkins, K. A.; Bhasin, K. B.

1990-04-01

The development of high temperature superconducting YBa2Cu3O(7-x) thin films on substrates suitable for microwave applications is of great interest for evaluating their applications for space radar, communication, and sensor systems. Thin films of YBa2Cu3O(7-x) were formed on SrTiO3, ZrO2, MgO, and LaAlO3 substrates by laser ablation. The wavelength used was 248 nm from a KrF excimer laser. During deposition the films were heated to 600 C in a flowing oxygen environment, and required no post annealing. The low substrate temperature during deposition with no post annealing gave films which were smooth, which had their c-axis aligned to the substrates, and which had grains ranging from 0.2 to 0.5 microns in size. The films being c-axis aligned gave excellent surface resistance at 35 GHz which was lower than that of copper at 77 K. At present, LaAlO3 substrates with a dielectric constant of 22, appears suitable as a substrate for microwave and electronic applications. The films were characterized by resistance-temperature measurements, scanning electron microscopy, and x ray diffraction. The highest critical transition temperatures (T sub c) are above 89 K for films on SrTiO3 and LaAlO3, above 88 K for ZrO2, and above 86 K for MgO. The critical current density (J sub c) of the films on SrTiO3 is above 2 x 10(exp 6) amperes/sq cm at 77 K. The T(sub c) and J(sub c) are reported as a function of laser power, composition of the substrate, and temperature of the substrate during deposition.

Microscopic adaptation of BaHfO3 and Y2O3 artificial pinning centers for strong and isotropic pinning landscape in YBa2Cu3O7-x thin films

NASA Astrophysics Data System (ADS)

Gautam, Bibek; Sebastian, Mary Ann; Chen, Shihong; Haugan, Timothy; Zhang, Wenrui; Huang, Jijie; Wang, Haiyan; Wu, Judy Z.

2018-07-01

A study of 3 vol% Y2O3 + 2-6 vol% BaHfO3 double-doped YBa2Cu3O7-x (BHO DD) epitaxial thin films was carried out to explore the morphology adaption of c-axis aligned one-dimensional BHO artificial pinning centers (1D APCs) to secondary Y2O3 nanoparticles (3D APCs). BHO 1D APCs have been predicted to have the least rigidity in an elastic strain energy model in APC/YBa2Cu3O7-x nanocomposite films. Consequently, they could be best ‘tuned’ away from the c-axis alignment by local strains generated by the Y2O3 3D APCs. This provides an opportunity to generate mixed-morphology APCs, especially at high BHO concentrations. Motivated by this, we have carried out a systematic study of the transport critical current density J c(H, T, θ) on the BHO DD samples in magnetic fields (H) up to 90 kOe at different H orientations from H//c-axis (θ = 0), to θ = 45°, and to H//ab-plane (θ = 90°). Enhanced pinning at all three orientations was observed as illustrated in the comparable low alpha (α) values in the range of 0.13-0.25 at 65 K, which is consistent with the mixed 1D (in c-axis) + 2D (in ab-plane) + 3D APCs observed in transmission electron microscopy (TEM). Upon increasing BHO concentration from 2 to 4 vol%, a monotonic increase of the accommodation field H* at θ = 0°, 45° and 90° was observed, indicative of the APC concentration increase of the mixed morphologies. At 6 vol% BHO, the H* continues the increase to 85 kOe at H//c-axis (θ = 0), and >90 kOe H//ab-plane (θ = 90°), while it decreases from 80 to 85 kOe at 2-4 vol% to 60 kOe at 6 vol% at θ = 45°, which is consistent with the TEM observation of the connection of 3D APCs, appeared at lower BHO concentration into 2D ones in ab-plane at the higher BHO concentrations. These results shed light on the quantitative adaptation of APCs of mixed morphologies with increasing BHO doping in the BHO DD thin films and are important for controlling the APC pinning landscape towards minimal angular dependence.

Nonaqueous slip casting of YBa2Cu3O(7-x) superconductive ceramics. Ph.D. Thesis - 1993

NASA Technical Reports Server (NTRS)

Hooker, Matthew W.; Taylor, Theodore D.

1994-01-01

This study investigates the slip casting of YBa2Cu3O(7-x) powders using nonaqueous carrier liquids and fired ceramic molds. The parameters of the process examined here include the rheological properties of YBa2Cu3O(7-x) powder dispersed in various solvent/dispersant systems, the combination of nonaqueous slips with fired ceramic molds to form the superconductive ceramics, the process-property relationships using a four-factor factorial experiment, and the applicability of magnetic fields to align the YBa2Cu3O(7-x) grains during the casting process.

Lanthanum gallate substrates for epitaxial high-temperature superconducting thin films

NASA Astrophysics Data System (ADS)

Sandstrom, R. L.; Giess, E. A.; Gallagher, W. J.; Segmuller, A.; Cooper, E. I.

1988-11-01

It is demonstrated that lanthanum gallate (LaGaO3) has considerable potential as an electronic substrate material for high-temperature superconducting films. It provides a good lattice and thermal expansion match to YBa2Cu3O(7-x), can be grown in large crystal sizes, is compatible with high-temperature film processing, and has a reasonably low dielectric constant and low dielectric losses. Epitaxial YBa2Cu3O(7-x) films grown on LaGaO3 single-crystal substrates by three techniques have zero resistance between 87 and 91 K.

Magnetic penetration depth of YBa2Cu3O(7-delta) thin films determined by the power transmission method

NASA Technical Reports Server (NTRS)

Heinen, Vernon O.; Miranda, Felix A.; Bhasin, Kul B.

1992-01-01

A power transmission measurement technique was used to determine the magnetic penetration depth (lambda) of YBa2Cu3O(7-delta) superconducting thin films on LaAlO3 within the 26.5 to 40.0 GHz frequency range, and at temperatures from 20 to 300 K. Values of lambda ranging from 1100 to 2500 A were obtained at low temperatures. The anisotropy of lambda was determined from measurements of c-axis and a-axis oriented films. An estimate of the intrinsic value of lambda of 90 +/- 30 nm was obtained from the dependence of lambda on film thickness. The advantage of this technique is that it allows lambda to be determined nondestructively.

Ten Ghz YBa2Cu3O(7-Delta) Superconducting Ring Resonators on NdGaO3 Substrates

NASA Technical Reports Server (NTRS)

To, H. Y.; Valco, G. J.; Bhasin, K. B.

1993-01-01

YBa2Cu3O(7-delta) thin films were formed on NdGaO3 substrates by laser ablation. Critical temperatures greater than 89 K and critical current densities exceeding 2 x 10(exp 8) Acm(sub -2) at 77 K were obtained. The microwave performance of films patterned into microstrip ring resonators with gold ground planes was measured. An unloaded quality factor six times larger than that of a gold resonator of identical geometry was achieved. The unloaded quality factor decreased below 70 K for both the superconducting and gold resonators due to increasing dielectric losses in the substrate. The temperature dependence of the loss tangent of NdGaO3 was extracted from the measurements.

Artificial in-plane ordering of textured YBa2Cu3O(7-x) films deposited on polycrystalline yttria-stabilized zirconia substrates

NASA Astrophysics Data System (ADS)

Harshavardhan, K. S.; Rajeswari, M.; Hwang, D. M.; Chen, C. Y.; Sands, T. D.; Venkatesan, T.; Tkaczyk, J. E.; Lay, K. W.; Safari, A.; Johnson, L.

1992-12-01

Anisotropic surface texturing of the polycrystalline yttria-stabilized zirconia substrates, prior to YBa2Cu3O(7-x) film deposition, is shown to promote in-plane (basal plane) ordering of the film growth in addition to the c-axis texturing. The Jc's of the films in the weak-link-dominated low-field regime are enhanced considerably, and this result is attributed to the reduction of weak links resulting from a reduction in the number of in-plane large-angle grain boundaries.

Vibrational spectra and lattice instabilities in the high-Tc superconductors YBa2Cu3O7 and GdBa2Cu3O7

NASA Astrophysics Data System (ADS)

Bozović, I.; Mitzi, D.; Beasley, M.; Kapitulnik, A.; Geballe, T.; Perkowitz, S.; Carr, G. L.; Lou, B.; Sudharsanan, R.; Yom, S. S.

1987-09-01

The exceptionally high Tc of layered cuprates was proposed recently as originating from electronically driven structural instabilities. We have studied the infrared and Raman spectra of YBa2Cu3O7-δ and GdBa2Cu3O7-δ over a broad range of temperatures, from 10 to 300 K. We observed neither mode softening nor any other spectroscopic signature of lattice instabilities.

Magnetic flux relaxation in YBa2Cu3O(7-x) thin film: Thermal or athermal

NASA Technical Reports Server (NTRS)

Vitta, Satish; Stan, M. A.; Warner, Joseph D.; Alterovitz, Samuel A.

1992-01-01

The magnetic flux relaxation behavior of YBa2Cu3O(7-x) thin film on LaAlO3 for H parallel c was studied in the range of 4.2-40 k and 0.2-1.0 T. Both the normalized flux relaxation rate (S) and the net flux pinning energy (U) increase continuously from 1.3 x 10 exp -2 to 3.0 x 10 exp -2 and from 70-240 meV respectively, as the temperature (T) increases from 10 to 40 K. This behavior is consistent with the thermally activated flux motion model. At low temperatures, however, S is found to decrease much more slowly as compared with kT, in contradiction to the thermal activation model. This behavior is discussed in terms of the athermal quantum tunneling of flux lines. The magnetic field dependence of U, however, is not completely understood.

Theoretical calculation of electron-positron momentum density in YBa 2Cu 3O 7-δ

NASA Astrophysics Data System (ADS)

Massidda, S.

1990-07-01

We present calculations of the electron-positron momentum density for the high- Tc superconductor YBa 2Cu 3O 7-δ for δ=0 and for the insulating parent compound YBa 2Cu 3O 6, based on first-principle electronic structure calculations performed within the local density approximation (LDA) using the full potential linearized augmented plane wave (FLAPW) method. Our results indicate a small overlap of the positron wave function with the CuO 2 plane electrons and, as a consequence, relatively small signals due to the related Fermi surfaces. By contrast, the present calculations show, after the folding of Umklapp terms according to Lock, Crisp and West, clear Fermi surface breaks arising from the Cu-O chain bands. No general agreement with existing experiments allows a clear definition of Fermi surface structures in the latter. A comparison of the calculated momentum with the experimental two-dimensional angular correlation of annihilation radiation (2D-ACAR) recently measured in Geneva shows an overall agreement for the insulating compound, despite the spurious LDA metallic state, and possibly suggests the importance of O vacancies in experiments performed on non-stoichiometric YBa 2Cu 3O 7-δ samples.

Method for making high-critical-current-density YBa.sub.2 Cu.sub.3 O.sub.7 superconducting layers on metallic substrates

DOEpatents

Feenstra, Roeland; Christen, David; Paranthaman, Mariappan

1999-01-01

A method is disclosed for fabricating YBa.sub.2 Cu.sub.3 O.sub.7 superconductor layers with the capability of carrying large superconducting currents on a metallic tape (substrate) supplied with a biaxially textured oxide buffer layer. The method represents a simplification of previously established techniques and provides processing requirements compatible with scale-up to long wire (tape) lengths and high processing speeds. This simplification has been realized by employing the BaF.sub.2 method to grow a YBa.sub.2 Cu.sub.3 O.sub.7 film on a metallic substrate having a biaxially textured oxide buffer layer.

Temperature and depth dependence of positron annihilation parameters in YBa2Cu3O7-x and La1.85Sr0.15CuO4

NASA Astrophysics Data System (ADS)

Lynn, K. G.; Usmar, S. G.; Nielsen, B.; van der Kolk, G. J.; Kanazawa, I.; Sferlazzo, P.; Moodenbaugh, A. R.

1988-02-01

The temperature dependence of the positron annihilation parameters for YBa2Cu3O7-x x=0.7, 0.4 and 0.0 and La1.85Sr0.15CuO4 were measured. The depth dependence of the YBa2Cu3O7 was studied using a variable-energy positron beam showing a strong depth dependence in the Doppler line-shape extending up to an average depth of ˜5.0 μm. It was found that a transition in the Doppler line-shape parameter, ``S'', was associated with the superconducting transition temperature (Tc) in YBa2Cu3O7-x x=0.4 and 0.0 while no transition was observed in the nonsuperconducting YBa2Cu3O6.3. Positron lifetime parameters in YBa2Cu3O7 were found to be consistent with positrons localized at open volume regions (probably unoccupied crystallographic sites) in this material with a lifetime of 210 psec at 300 K. These results indicate that the electron density at these unoccupied sites increases, using a free electron model, approximately 9% between 100 and 12 K.

Ultrafast relaxation dynamics in BiFeO 3/YBa 2Cu 3O 7 bilayers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Springer, D.; Nair, Saritha K.; He, Mi

The temperature dependence of the relaxation dynamics in the bilayer thin film heterostructure composed of multiferroic BiFeO 3 (BFO) and superconducting YBa 2Cu 3O 7 (YBCO) grown on (001) SrTiO 3 substrate is studied by time-resolved pump-probe technique, and compared with that of pure YBCO thin film grown under the same growth conditions. The superconductivity of YBCO is found to be retained in the heterostructure. We observe a speeding up of the YBCO recombination dynamics in the superconducting state of the heterostructure, and attribute it to the presence of weak ferromagnetism at the BFO/YBCOinterface as observed inmagnetization data. An extensionmore » of the Rothwarf-Taylor model is used to fit the ultrafast dynamics of BFO/YBCO, that models an increased quasiparticle occupation of the ferromagnetic interfacial layer in the superconducting state of YBCO.« less

Ultrafast relaxation dynamics in BiFeO 3/YBa 2Cu 3O 7 bilayers

DOE PAGES

Springer, D.; Nair, Saritha K.; He, Mi; ...

2016-02-12

The temperature dependence of the relaxation dynamics in the bilayer thin film heterostructure composed of multiferroic BiFeO 3 (BFO) and superconducting YBa 2Cu 3O 7 (YBCO) grown on (001) SrTiO 3 substrate is studied by time-resolved pump-probe technique, and compared with that of pure YBCO thin film grown under the same growth conditions. The superconductivity of YBCO is found to be retained in the heterostructure. We observe a speeding up of the YBCO recombination dynamics in the superconducting state of the heterostructure, and attribute it to the presence of weak ferromagnetism at the BFO/YBCOinterface as observed inmagnetization data. An extensionmore » of the Rothwarf-Taylor model is used to fit the ultrafast dynamics of BFO/YBCO, that models an increased quasiparticle occupation of the ferromagnetic interfacial layer in the superconducting state of YBCO.« less

The early growth and interface of YBa 2Cu 3O y thin films deposited on YSZ substrates

NASA Astrophysics Data System (ADS)

Gao, J.; Tang, W. H.; Yau, C. Y.

2001-11-01

Epitaxial thin films of YBa 2Cu 3O y (YBCO) have been prepared on yttrium-stabilized zirconia substrates with and without a buffer layer. The early growth, crystallinity and surface morphology of these thin films have been characterized by X-ray diffraction, rocking curves, scanning electron microscope, in situ conductance measurements, and surface step profiler. The full width at half maximum of the ( 0 0 5 ) peak of rocking curve was found to be less than 0.1°. Over a wide scanning range of 2000 μm the average surface roughness is just 5 nm, indicating very smooth films. Grazing incident X-ray reflection and positron annihilation spectroscopy shows well-defined interfaces between layers and substrate. By applying a new Eu 2CuO 4 (ECO) buffer layer the initial formation of YBCO appears to grow layer-by-layer rather than the typical island growth mode. The obtained results reveal significant improvements at the early formation and crystallinity of YBCO by using the 214-T ‧ ECO as a buffer layer.

La0.7Sr0.3MnO3: A single, conductive-oxide buffer layer for the development of YBa2Cu3O7-δ coated conductors

NASA Astrophysics Data System (ADS)

Aytug, T.; Paranthaman, M.; Kang, B. W.; Sathyamurthy, S.; Goyal, A.; Christen, D. K.

2001-10-01

Coated conductor applications in power technologies require stabilization of the high-temperature superconducting (HTS) layers against thermal runaway. Conductive La0.7Sr0.3MnO3 (LSMO) has been epitaxially grown on biaxially textured Ni substrates as a single buffer layer. The subsequent epitaxial growth of YBa2Cu3O7-δ (YBCO) coatings by pulsed laser deposition yielded self-field critical current densities (Jc) of 0.5×106A/cm2 at 77 K, and provided good electrical connectivity over the entire structure (HTS+conductive-buffer+metal substrate). Property characterizations of YBCO/LSMO/Ni architecture revealed excellent crystallographic and morphological properties. These results have demonstrated that LSMO, used as a single, conductive buffer layer, may offer potential for use in fully stabilized YBCO coated conductors.

Controlling particle properties in {{YBa}}_{2}{{Cu}}_{3}{{\\rm{O}}}_{7-\\delta } nanocomposites by combining PLD with an inert gas condensation system

NASA Astrophysics Data System (ADS)

Sparing, M.; Reich, E.; Hänisch, J.; Gottschall, T.; Hühne, R.; Fähler, S.; Rellinghaus, B.; Schultz, L.; Holzapfel, B.

2017-10-01

The critical current density {J}{{c}} in {{YBa}}2{{Cu}}3{{{O}}}7-δ thin films, which limits their application in external magnetic fields, can be enhanced by the introduction of artificial pinning centers such as non-superconducting nanoparticles inducing additional defects and local strain in the superconducting matrix. To understand the correlation between superconductivity, defect structures and particles, a controlled integration of particles with adjustable properties is essential. A powerful technique for the growth of isolated nanoparticles in the range of 10 nm is dc-magnetron sputtering in an inert gas flow. The inert gas condensation (IGC) of particles allows for an independent control of both the particle diameter distribution and the areal density. We report on the integration of such gas-phase-condensed {{HfO}}2 nanoparticles into pulsed laser deposited (PLD) {{YBa}}2{{Cu}}3{{{O}}}7-δ thin film multilayers with a combined PLD-IGC system. The particles and the structure of the multilayers are analyzed by transmission electron microscopy on cross-sectional FIB lamellae. As a result of the IGC particle implementation, randomly as well as biaxially oriented {{BaHfO}}3 precipitates are formed in the {{YBa}}2{{Cu}}3{{{O}}}7-δ thin films. With as few as three interlayers of nanoparticles, the pinning force density is enhanced in the low-field region.

Chemical nature of the barrier in Pb/YBa2Cu3O(7-x) tunneling structures

NASA Technical Reports Server (NTRS)

Vasquez, R. P.; Foote, M. C.; Hunt, B. D.; Bajuk, L.

1991-01-01

Several reports of reproducible tunneling measurements on YBa2Cu3O(7-x) thin films or single crystals with a Pb counterelectrode have recently appeared. The nature of the tunnel barrier, formed by air exposure, in these structures has been unknown. In the present work, the chemical nature of the tunnel barrier is studied with X-ray photoelectron spectroscopy (XPS). Laser-ablated films grown on LaAlO3 which have been chemically etched and heated in air are found to form nonsuperconducting surface Ba species, evident in an increase of the high binding energy Ba 3d and O 1s signals. A deposited Pb film about 10 A thick is found to be oxidized, and Cu(+2) is partially reduced to Cu(+1). The tunneling barrier thus appears to consist of species resulting from a combination of the air exposure and a reaction between the superconductor and the deposited Pb counterelectrode.

Environment-resistive coating for the thin-film-based superconducting fault-current limiter Ag/Au-Ag/YBa 2Cu 3O 7/CeO 2/Al 2O 3

NASA Astrophysics Data System (ADS)

Matsui, H.; Kondo, W.; Tsukada, K.; Sohma, M.; Yamaguchi, I.; Kumagai, T.; Manabe, T.; Arai, K.; Yamasaki, H.

2010-02-01

We have studied environment-resistive coatings (ERC) for the thin-film-based superconducting fault-current limiter (SFCL) Ag/Au-Ag/YBa 2Cu 3O 7/CeO 2/Al 2O 3. We evaluated nine candidate ERC materials by two accelerating-environment tests, and revealed that the shellac- and the fluorine-resin have a high environmental resistance. Especially, the shellac resin almost completely protected Jc of an element exposed to 60 °C saturated water vapor for 2 h (3.4->3.2 MA/cm 2). We also performed a practical operation test of SFCL using an element half covered by shellac, and found that the ERC does not diminish the current limiting properties similarly to the previous results of the Teflon-coated SFCL [1].

RAPID COMMUNICATION: Large-area uniform ultrahigh-Jc YBa2Cu3O7-x film fabricated by the metalorganic deposition method using trifluoroacetates

NASA Astrophysics Data System (ADS)

Araki, Takeshi; Yamagiwa, Katsuya; Hirabayashi, Izumi; Suzuki, Katsumi; Tanaka, Shoji

2001-07-01

Ultrahigh-Jc YBa2Cu3O7-x (YBCO) films have been successfully fabricated by the metalorganic deposition method using a trifluoroacetate coating solution which is prepared by a newly developed purification technique, the solvent-into-gel (SIG) method. The prepared pure coating solution has less than 0.25% impurities and has a wide flexibility in process conditions to obtain high-Jc YBCO film. Using this feature, we have successfully formed 50 mm diameter YBCO films, which have a critical current density over 10 MA cm-2 (77 K, 0 T) on LaAlO3 single crystalline substrates.

Modification of structural and transport properties in epitaxial YBa2CU3Ox films by pulsed laser irradiation

NASA Astrophysics Data System (ADS)

Chechenin, N. G.; Chernysh, A. V.; Korneev, V. V.; Monakhov, E. V.; Seleznev, B. V.

1993-12-01

Pulsed (~20 ns) laser effects in epitaxial YBa2CU3Ox/SrTiO3 thin films were investigated, using RBS/channeling for compositional and structural characterization and 4-point technique for electrical measurements. It was found that laser pulse melting and following quenching lead to a transition from a single-crystalline to a polycrystalline state in films. The formation of grain boundaries causes a room temperature electrical resistivity increase by a factor 10-40, depending on the initial film properties and on the irradiation conditions. Unlike corpuscular (ions, neutrons) irradiation, the laser pulse induced structural damage did not lead to the disappearance of HTS, which persisted up to the highest laser fluences used. It was found, that a thermal model can consistently describe the fluence dependence of disorder, depth of surface relief and helps, with a simple two-layer model, in understanding of fluence dependence of room temperature resistivity in a relatively thick film. Les effects de pulses laser (~20 ns) sur des films minces épitaxiés d'YBa2Cu3Ox/SrTiO3 ont été étudiés par rétrodiffusion Rutherford et canalisation afin de caractériser leur composition et leur structure et à l'aide de la technique des 4 points pour les mesures électriques. On a trouvé que la fusion par pulse laser suivie par une trempe entraîne une transition d'un film monocristallin vers un film polycristallin. La formation de joints de grains s'accompagne d'une augmentation d'un facteur 10-40, de la résistivité électrique à température ambiante, dépendante des propriétés initiales du film et des conditions d'irradiation. Contrairement à l'irradiation corpusculaire (ions, neutrons) l'endommagement produit par la pulse laser n'entraîne pas la disparition de la superconductivité à haute température (HTS), qui persiste jusqu'aux plus hautes doses utilisées. On a trouvé qu'un modèle thermique peut décrire de façon consistante, la profondeur de la rugosité de

High Tc screen-printed YBa2Cu3O(7-x) films - Effect of the substrate material

NASA Astrophysics Data System (ADS)

Bansal, Narottam P.; Simons, Rainee N.; Farrell, D. E.

1988-08-01

Thick films of YBa2Cu3O(7-x) have been deposited on highly polished alumina, magnesia spinel, nickel aluminum titanate (Ni-Al-Ti), and barium tetratitanate (Ba-Ti) substrates by the screen printing technique. Properties of the films were found to be highly sensitive to the choice of the substrate material. The film on Ba-Ti turned green after firing, due to a reaction with the substrate and were insulating. A film on Ni-Al-Ti had a Tc (onset) of about 95 K and lost 90 percent of its resistance by about 75 K. However, even at 4 K it was not fully superconducting, possibly due to a reaction between the film and the substrate and interdiffusion of the reaction products. The film on alumina had Tc (onset) of about 96 K, Tc (zero) of about 66 K, and Delta Tc of about 10 K. The best film was obtained on spinel and had Tc (onset) of about 94 K, zero resistance at 81 K, and a transition width of about 7 K.

High Tc screen-printed YBa2Cu3O(7-x) films - Effect of the substrate material

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.; Simons, Rainee N.; Farrell, D. E.

1988-01-01

Thick films of YBa2Cu3O(7-x) have been deposited on highly polished alumina, magnesia spinel, nickel aluminum titanate (Ni-Al-Ti), and barium tetratitanate (Ba-Ti) substrates by the screen printing technique. Properties of the films were found to be highly sensitive to the choice of the substrate material. The film on Ba-Ti turned green after firing, due to a reaction with the substrate and were insulating. A film on Ni-Al-Ti had a Tc (onset) of about 95 K and lost 90 percent of its resistance by about 75 K. However, even at 4 K it was not fully superconducting, possibly due to a reaction between the film and the substrate and interdiffusion of the reaction products. The film on alumina had Tc (onset) of about 96 K, Tc (zero) of about 66 K, and Delta Tc of about 10 K. The best film was obtained on spinel and had Tc (onset) of about 94 K, zero resistance at 81 K, and a transition width of about 7 K.

Synthesis and characterization of YBaCu2O5-δ compound

NASA Astrophysics Data System (ADS)

Ehsandoust, A.; Sandoghchi, M.; Mokhtari, P.; Akhavan, M.

2018-05-01

YBaCu2O5 compound as one of the possible microstructures of Y3Ba5Cu8O19 has been synthesized. The X-ray diffraction analysis of this compound indicates that its formation is accompanied with the formation of YBa2Cu3O7-δ. The observed superconductivity around ∼92 K supports this. So, it seems that YBa2Cu3O7-δ is responsible for the observed superconductivity in YBaCu2O5, and this phase is not an independent superconducting phase. Consequently, the overall effect of the YBaCu2O5 formation during the Y3Ba5Cu8O19 fabrication process could be a reduction in Tc.

Dependence of the critical temperature of laser-ablated YBa2Cu3O(7-delta) thin films on LaAlO3 substrate growth technique

NASA Technical Reports Server (NTRS)

Warner, Joseph D.; Bhasin, Kul B.; Miranda, Felix A.

1991-01-01

Samples of LaAlO3 made by flame fusion and Czochralski method were subjected to the same temperature conditions that they have to undergo during the laser ablation deposition of YBa2Cu3O(7 - delta) thin films. After oxygen annealing at 750 C, the LaAlO3 substrate made by two methods experienced surface roughening. The degree of roughening on the substrate made by Czochralski method was three times greater than that on the substrate made by flame fusion. This excessive surface roughening may be the origin of the experimentally observed lowering of the critical temperature of a film deposited by laser ablation on a LaAlO3 substrate made by Czochralski method with respect to its counterpart deposited on LaAlO3 substrates made by flame fusion.

Direct observation of twin deformation in YBa2Cu3O7-x thin films by in situ nanoindentation in TEM

NASA Astrophysics Data System (ADS)

Lee, Joon Hwan; Zhang, Xinghang; Wang, Haiyan

2011-04-01

The deformation behaviors of YBa2Cu3O7-x (YBCO) thin films with twinning structures were studied via in situ nanoindentation experiments in a transmission electron microscope. The YBCO films were grown on SrTiO3 (001) substrates by pulsed laser deposition. Both ex situ (conventional) and in situ nanoindentation were conducted to reveal the deformation of the YBCO films from the directions perpendicular and parallel to the twin interfaces. The hardness measured perpendicular to the twin interfaces is ˜50% and 40% higher than that measured parallel to the twin interfaces ex situ and in situ, respectively. Detailed in situ movie analysis reveals that the twin structures play an important role in deformation and strengthening mechanisms in YBCO thin films.

Preparation of epitaxial TlBa2Ca2Cu3O9 high Tc thin films on LaAlO3 (100) substrates

NASA Astrophysics Data System (ADS)

Piehler, A.; Reschauer, N.; Spreitzer, U.; Ströbel, J. P.; Schönberger, R.; Renk, K. F.; Saemann-Ischenko, G.

1994-09-01

Epitaxial TlBa2Ca2Cu3O9 high Tc thin films were prepared on LaAlO3 (100) substrates by a combination of laser ablation and thermal evaporation of thallium oxide. X-ray diffraction patterns of θ-2θ scans showed that the films consisted of highly c axis oriented TlBa2Ca2Cu3O9. φ scan measurements revealed an epitaxial growth of the TlBa2Ca2Cu3O9 thin films on the LaAlO3 (100) substrates. Ac inductive measurements indicated the onset of superconductivity at 110 K. At 6 K, the critical current density was 4×106 A/cm2 in zero magnetic field and 6×105 A/cm2 at a magnetic field of 3 T parallel to the c axis.

Disorder-controlled superconductivity at YBa2Cu3O7/SrTiO3 interfaces

NASA Astrophysics Data System (ADS)

Garcia-Barriocanal, J.; Perez-Muñoz, A. M.; Sefrioui, Z.; Arias, D.; Varela, M.; Leon, C.; Pennycook, S. J.; Santamaria, J.

2013-06-01

We examine the effect of interface disorder in suppressing superconductivity in coherently grown ultrathin YBa2Cu3O7 (YBCO) layers on SrTiO3 (STO) in YBCO/STO superlattices. The termination plane of the STO is TiO2 and the CuO chains are missing at the interface. Disorder (steps) at the STO interface cause alterations of the stacking sequence of the intracell YBCO atomic layers. Stacking faults give rise to antiphase boundaries which break the continuity of the CuO2 planes and depress superconductivity. We show that superconductivity is directly controlled by interface disorder outlining the importance of pair breaking and localization by disorder in ultrathin layers.

Uncovering a new quasi-2D CuO2 plane between the YBa2Cu3O7 and CeO2 buffer layer of coated conductors

NASA Astrophysics Data System (ADS)

Li, Zhi-Xin; Cao, Jin-Jin; Gou, Xiao-Fan; Wang, Tian-Ge; Xue, Feng

2018-01-01

We report a discovery of the quasi-two-dimensional (quasi-2D) CuO2 plane between the superconductor YBa2Cu3O7 (YBCO) and CeO2 buffer layer (mostly used in the fabrication) of coated conductors through the atomistic computer simulations with the molecular dynamics (MD) and first-principle calculations. For an YBCO coated conductor with multilayer structures, the buffer layers deposited onto a substrate are mainly considered to transfer a strong biaxial texture from the substrate to the YBCO layer. To deeply understand the tuning mechanism of the texture transfer, exploring the complete atomic-level picture of the structure between the YBa2Cu3O7/CeO2 interfaces is firstly required. However, the related observation data have not been available due to some big challenges of experimental techniques. With the MD simulations, having tested the accuracy of the potential functions for the YBa2Cu3O7/CeO2 interface, we constructed a total of 54 possible atom stacking models of the interface and identified its most appropriate and stable structure according to the criterion of the interface adhesion energy and the coherent characterization. To further verify the stability of the identified structure, we performed the first-principle calculations to obtain the adhesion energy and developed the general knowledge of the interface structure. Finally, a coherent interface formed with a new built quasi-2D CuO2 plane that is structurally similar to the CuO2 plane inside bulk YBCO was determined.

Controlling BaZrO3 nanostructure orientation in YBa2Cu3O{}_{7-\\delta } films for a three-dimensional pinning landscape

NASA Astrophysics Data System (ADS)

Wu, J. Z.; Shi, J. J.; Baca, F. J.; Emergo, R.; Wilt, J.; Haugan, T. J.

2015-12-01

The orientation phase diagram of self-assembled BaZrO3 (BZO) nanostructures in c-oriented YBa2Cu3O{}7-δ (YBCO) films on flat and vicinal SrTiO3 substrates was studied experimentally with different dopant concentrations and vicinal angles and theoretically using a micromechanical model based on the theory of elasticity. The organized BZO nanostructure configuration was found to be tunable, between c-axis to ab-plane alignment, by the dopant concentration in the YBCO film matrix strained via lattice mismatched substrates. The correlation between the local strain caused by the BZO doping and the global strain on the matrix provides a unique approach for controllable growth of dopant nanostructure landscapes. In particular, a mixed phase of the c-axis-aligned nanorods and the ab-plane-aligned planar nanostructures can be obtained, leading to a three-dimensional pinning landscape with single impurity doping and much improved J c in almost all directions of applied magnetic field.

Dominant pinning mechanisms in YBa2Cu3O7-x films on single and polycrystalline yttria stabilized zirconia substrates

NASA Astrophysics Data System (ADS)

Harshavardhan, K. S.; Rajeswari, M.; Hwang, D. M.; Chen, C. Y.; Sands, T.; Venkatesan, T.; Tkaczyk, J. E.; Lay, K. W.; Safari, A.

1992-04-01

Critical-current densities have been measured in YBa2Cu3O7-x films deposited on (100) yttria stabilized zirconia (YSZ) and polycrystalline YSZ substrates as a function of temperature (4.5-88 K), magnetic field (0-1 T) and orientation relative to the applied field. The results indicate that in films on polycrystalline substrates, surface and interface pinning play a dominant role at high temperatures. In films on (100) YSZ, pinning is mainly due to intrinsic layer pinning as well as extrinsic pinning associated with the interaction of the fluxoids with point defects and low energy planar (2D) boundaries. The differences are attributed to the intrinsic rigidity of single fluxoids which is reduced in films on polycrystalline substrates thereby weakening the intrinsic layer pinning.

Scanning micro-Hall probe mapping of magnetic flux distributions and current densities in YBa2Cu3O7 thin films

NASA Technical Reports Server (NTRS)

Xing, W.; Heinrich, B.; Zhou, HU; Fife, A. A.; Cragg, A. R.; Grant, P. D.

1995-01-01

Mapping of the magnetic flux density B(sub z) (perpendicular to the film plane) for a YBa2Cu3O7 thin-film sample was carried out using a scanning micro-Hall probe. The sheet magnetization and sheet current densities were calculated from the B(sub z) distributions. From the known sheet magnetization, the tangential (B(sub x,y)) and normal components of the flux density B were calculated in the vicinity of the film. It was found that the sheet current density was mostly determined by 2B(sub x,y)/d, where d is the film thickness. The evolution of flux penetration as a function of applied field will be shown.

Crystal growth of YBa2Cu3O(7-x) and reaction of gold crucible with Ba-Cu-rich flux

NASA Technical Reports Server (NTRS)

Tao, Y. K.; Chen, H. C.; Martini, L.; Bechtold, J.; Huang, Z. J.; Hor, P. H.

1991-01-01

YBa2Cu3O(7-x) crystals are grown in a gold crucible by a self-flux method. The flux moves along the gold surface due to surface wetting and leaves Y123 crystals behind. The obtained crystals are clean and have a size up to two millimeters and a Tc is greater than 90 K. In an effort to recycle the used crucibles, it is found that the used gold is contaminated by copper. A CuO thin film is easily formed on the surface of the crucible that is made of the used gold. This film provides good surface wetting and a buffer layer, which reduces the reaction between gold and the Y-Ba-Cu-oxide melt.

Fluctuation-induced conductivity in melt-textured Pr-doped YBa2Cu3O7-δ composite superconductor

NASA Astrophysics Data System (ADS)

Opata, Yuri Aparecido; Monteiro, João Frederico Haas Leandro; Siqueira, Ezequiel Costa; Rodrigues, Pedro Júnior; Jurelo, Alcione Roberto

2018-04-01

In this study, the effects of thermal fluctuations on the electrical conductivity in melt-textured YBa2Cu3O7-δ, Y0.95Pr0.05Ba2Cu3O7-δ and (YBa2Cu3O7-δ)0.95-(PrBa2Cu3O7-δ)0.05 composite superconductor were considered. The composite superconductor samples were prepared through the top seeding method using melt-textured NdBa2Cu3O7-d seeds. The resistivity measurements were performed with a low-frequency, low-current AC technique in order to extract the temperature derivative and analyze the influence of the praseodymium ion on the normal superconductor transition and consequently on the fluctuation regimes. The results show that the resistive transition is a two-step process. In the normal phase, above the critical temperature, Gaussian and critical fluctuation regimes were identified, while below the critical temperature, in the regime near the approach to the zero-resistance state, the fluctuation conductivity diverges as expected in a paracoherent-coherent transition.

Phase Evolution of YBa2Cu3O7-x films by all-chemical solution deposition route for coated conductors

NASA Astrophysics Data System (ADS)

Zhao, Yue; Tang, Xiao; Wu, Wei; Grivel, Jean-Claude

2014-05-01

In order to understand the all-chemical-solution-deposition (CSD) processes for manufacturing coated conductors, we investigated the phase evolution of YBa2Cu3O7 (YBCO) films deposited by a low-fluorine metal-organic solution deposition (LF-MOD) method on CSD derived Ce0.9La0.1O2/Gd2Zr2O7/NiW. It is shown that the phase transition from the pyrolyzed film to fully converted YBCO film in the LF-MOD process is similar to that in typical trifluoroacetates-metal organic deposition (TFA-MOD) processes even though the amount of TFA in the solution is reduced by almost one half compared with typical TFA-MOD cases. Moreover, we found that the formation of impurities (mainly BaCeO3, NiWO4 and NiO) is strongly related to the annealing temperature, i.e., the diffusion controlled reactions become intensive from 760 oC, which might be connected with the poor structural and superconducting properties of the films deposited at high sintering temperatures. Based on these results, the optimized growth conditions of YBCO films were established, and a high critical current density (Jc) of about 2 MA/cm2 (77 K, self field) is achieved in a 200 nm thick YBCO film in the architecture made by our all CSD route.

Epitaxial growth and characterization of CuGa2O4 films by laser molecular beam epitaxy

NASA Astrophysics Data System (ADS)

Wei, Hongling; Chen, Zhengwei; Wu, Zhenping; Cui, Wei; Huang, Yuanqi; Tang, Weihua

2017-11-01

Ga2O3 with a wide bandgap of ˜ 4.9 eV can crystalize in five crystalline phases. Among those phases, the most stable monoclinic β-Ga2O3 has been studied most, however, it is hard to find materials lattice matching with β-Ga2O3 to grown epitaxial thin films for optoelectronic applications. In this work, CuGa2O4 bulk were prepared by solid state reaction as target, and the films were deposited on sapphire substrates by laser molecular beam epitaxy (L-MBE) at different substrate temperatures. The influences of substrate temperature on structural and optical properties have been systematically investigated by means of X-ray diffraction, Transmission electron microscope and UV-vis absorption spectra. High quality cubic structure and [111] oriented CuGa2O4 film can be obtained at substrate temperature of 750 °C. It's also demonstrated that the CuGa2O4 film has a bandgap of ˜ 4.4 eV and a best crystal quality at 750 °C, suggesting that CuGa2O4 film is a promising candidate for applications in ultraviolet optoelectronic devices.

Structural morphology of YBa 2Cu 3O 7- x

NASA Astrophysics Data System (ADS)

Sun, B. N.; Hartman, P.; Woensdregt, C. F.; Schmid, H.

1990-03-01

The structural morphology of YBa 2Cu 3O 7- x (YBCO) has been investigated by application of the periodic bond chain (PBC) theory. For x=1, the F forms were found to be {001}, {011}, {013}, {112} and {114}. Attachment energies have been calculated in broken bond model and in an electrostatic point charge model. For x=1 the theoretical growth habit is tabular to platy {001} with {011} as side faces. For x=0 {010} also becomes an F form. The habit is isometric with large {001} and {011} and small {010} faces. The outermost layer of {001} contains half of the Cu + ( x=1) or Cu 3+ and O 2- ( x=0) ions in an ordered arrangement based on a c(2x2) quadratic lattice. For the outermost layer of (010) ( x=0) an ordering scheme of the copper and oxygen ions is proposed. The occurrence of {010} rather than {011} on grown crystals has to be ascribed to external factors.

Thickness effect of Gd2Zr2O7 buffer layer on performance of YBa2Cu3O7-δ coated conductors

NASA Astrophysics Data System (ADS)

Qiu, Wenbin; Fan, Feng; Lu, Yuming; Liu, Zhiyong; Bai, Chuanyi; Guo, Yanqun; Cai, Chuanbing

2014-12-01

Bilayer buffer architecture of Gd2Zr2O7 (GZO)/Y2O3 was prepared on the biaxially textured tape of Ni-5 at% W (NiW) by reactive sputtering deposition technique. The buffer layer of GZO films were deposited with different thicknesses on Y2O3 seeding layer with a given thickness of 20 nm. According to the results of φ-scan, the in-plane FWHMs of GZO films decreased and then reversed with increasing thickness of GZO, which corresponded with the in-plane FWHMs and superconducting properties of YBa2Cu3O7-δ (YBCO) films. Reflection High-Energy Electron Diffraction (RHEED) was carried out to examine the surface texture of GZO films and the deteriorated surface alignment was found for thicker films. The thickness effect of GZO on performance of YBCO is the coupling result of surface texture and blocking effect caused by thickness. With the balance of these two factors, the YBCO/GZO(120 nm)/Y2O3/NiW architecture exhibit relatively high performance with the transition temperature Tc of 92 K, a transition width ΔTc below 1 K, and a critical current density Jc of 0.65 MA/cm2.

Influence of γ-Irradiation on the Optical Properties of the Polyimide-YBa2Cu3O6.7 System

NASA Astrophysics Data System (ADS)

Muradov, A. D.; Korobova, N. E.; Kyrykbaeva, A. A.; Yar-Mukhamedova, G. Sh.; Mukashev, K. M.

2018-05-01

Influence of γ-irradiation on the optical properties of a polyimide film and its polymer compositions with fillers of a dispersed powder of a high-temperature superconductor ҮBa2Cu3O6.7 (YBaCuO) with concentrations of 0.05, 0.10, and 0.50 wt.% was studied. It was established that γ-irradiation with a dose up to 600 kGy does not affect the transparency of polyimide films in the visible region of the spectrum. However, at irradiation doses of 250 and 600 kGy, a weakly expressed fine structure appears in the spectra of polyimide films in the range of 220-300 nm due to the contribution of the resulting diene structures to the optical transmission and the increased content of oxygen atoms. The YBaCuO filler and γ-irradiation cause the polyimide transition from the amorphous state to the crystalline state, which is manifested in a sharp change in the spectrum in the range of 2.3-3.9 eV. A significant increase in the extinction coefficient was found in the composite containing 0.50 wt.% of the filler that is associated with an increase in the radius of action of structurally active fillers on the macromolecules of the matrix.

Peak effect in untwinned YBa 2Cu 3O 7-δ single crystals

NASA Astrophysics Data System (ADS)

D'Anna, G.; André, M.-O.; Indenbom, M. V.; Benoit, W.

1994-12-01

We report on the observation of a weak effect of the critical current density in untwinned YBa 2Cu 3O 7-δ single crystals of different purity, using a low frequency torsion pendulum. We construct the peak effect line and the irreversibility line.

Fabrication of YBa2Cu3O7 twin-boundary-junction dc SQUID by using a focused-ion-beam pattern technique

NASA Astrophysics Data System (ADS)

Lee, Sung Hoon; Lee, Soon-Gul

2017-09-01

We have fabricated YBa2Cu3O7 (YBCO) dc SQUIDs containing nanobridges across twin boundaries of LaAlO3 (LAO) substrates as Josephson elements by using a focused ion beam (FIB) etching method and measured their transport properties. The beam energy was 30 keV and the current was 1.5 pA for the nanobridge pattern. Each bridge with a nominal width of 200 nm crossed a twin boundary in the (100) direction. The SQUID loop had a 10 μm × 10 μm hole with a 5.7 μm average linewidth. The SQUID voltage showed modulations in response to the external flux with a maximum modulation depth of 350 μV at 77.0 K. HR-XRD spectra showed that the epitaxially grown YBCO film was twinned in commensurate with the twinning of the LAO substrate. Tilting of the c-axis of YBCO across the twin boundary is believed to play a role as a tunnel barrier.

YBa_2Cu_3O_{7-δ} : in pursuit of the ideal microstructure

NASA Astrophysics Data System (ADS)

Smith, D. S.; Suasmoro, S.; Lejeune, M.; Rabier, J.; Denanot, M. F.; Heintz, J. M.; Magro, C.; Bonnet, J. P.

1992-02-01

This paper examines the role of different factors in the microstructure of ceramic YBa2Cu3O{7-δ} with emphasis on its electrical response. In particular we discuss : 1. the effect of microstructural variations on j_c and ρ_{300}, 2. measurement of j_c, 3. the presence of minor phases and carbonates, 4. oxygen uptake and microcracks, 5. plastic deformation and related structural defects. Dans cet article, nous examinons d'une part la réponse électrique de céramiques supraconductrices massives de type YBa2Cu3O{7-δ} et d'autre part sa relation avec la microstructure. Nous présenterons successivement : 1. L'incidence de modifications microstructurales sur les valeurs de j_c et ρ_{300}, 2. les mesures expérimentales de j_c, 3. la présence de phases minoritaires et de carbonates, 4. la reprise d'oxygène et la microfissuration, 5. la déformation plastique et les défauts structuraux associés.

TOPICAL REVIEW: Importance of low-angle grain boundaries in YBa2Cu3O7-δ coated conductors

NASA Astrophysics Data System (ADS)

Durrell, J. H.; Rutter, N. A.

2009-01-01

Over the past ten years the perception of grain boundaries in YBa2Cu3O7-δ conductors has changed greatly. They are now not a problem to be eliminated, but an inevitable and potentially favourable part of the material. This change has arisen as a consequence of new manufacturing techniques which result in excellent grain alignment, reducing the spread of grain boundary misorientation angles. At the same time there is considerable recent evidence which indicates that the variation of properties of grain boundaries with mismatch angle is more complex than a simple exponential decrease in critical current. This is due to the fact that low-angle grain boundaries represent a qualitatively different system to high-angle boundaries. The time is therefore right for a targeted review of research into low-angle YBa2Cu3O7-δ grain boundaries. This article does not purport to be a comprehensive review of the physics of grain boundaries as found in YBa2Cu3O7-δ in general; for a broader overview we would recommend that the reader consult the comprehensive review of Hilgenkamp and Mannhart (2002 Rev. Mod. Phys. 74 485). The purpose of this article is to review the origin and properties of the low-angle grain boundaries found in YBa2Cu3O7-δ coated conductors both individually and as a collective system.

Improved Epitaxy and Surface Morphology in YBa2Cu3Oy Thin Films Grown on Double Buffered Si Wafers

NASA Astrophysics Data System (ADS)

Gao, J.; Kang, L.; Wong, H. Y.; Cheung, Y. L.; Yang, J.

Highly epitaxial thin films of YBCO have been obtained on silicon wafers using a Eu2CuO4/YSZ (yttrium-stabilized ZrO2) double buffer. Our results showed that application of such a double buffer can significantly enhance the epitaxy of grown YBCO. It also leads to an excellent surface morphology. The average surface roughness was found less than 5 nm in a large range. The results of X-ray small angle reflection and positron spectroscpy demonstrate a very clear and flat interface between YBCO and buffer layers. The Eu2CuO4/YSZ double buffer could be promising for coating high-TC superconducting films on various reactive substrates.

Defect ordering in YBa 2Cu 3O 6.5 and YBa 2Cu 3O 6.6: Synthesis and characterization by neutron and electron diffraction

NASA Astrophysics Data System (ADS)

Lin, Y. P.; Greedan, J. E.; O'Reilly, A. H.; Reimers, J. N.; Stager, C. V.; Post, M. L.

1990-02-01

Polycrystalline samples of YBa 2Cu 3O 6.5 and YBa 2Cu 3O 6.6 were prepared by oxygen titration of YBa 2 Cu 3O 6.0 at 450°C followed by slow cooling to room temperature. Both samples showed evidence for the a' = 2a supercell in individual grains by electron diffraction as reported previously. In addition the superlattice was observed in neutron powder diffraction indicating that the bulk material is also well ordered. In this study the YBa 2Cu 3O 6.6 phase showed longer correlation lengths for ordering along both a* and b* than YBa 2Cu 3O 6.5. For the former compound the powder-averaged, sample-averaged a* correlation distance is 26A˚from neutron diffraction. Analysis of electron diffraction profiles on selected single crystals give correlation lengths along a*, b*, and c* of 100, 200, and 50A˚, respectively. Dark field imaging discloses the presence of striped, ordered domains elongated along b* with a distribution of sizes. Both neutron diffraction and dark field imaging indicate that the volume fraction of the ordered domains is about 50%. A correlation is noted between the Meissner Effect and the extent of defect ordering in the bulk samples of the two phases.

Impact of oxygen diffusion on superconductivity in YBa2Cu3O7 -δ thin films studied by positron annihilation spectroscopy

NASA Astrophysics Data System (ADS)

Reiner, M.; Gigl, T.; Jany, R.; Hammerl, G.; Hugenschmidt, C.

2018-04-01

The oxygen deficiency δ in YBa2Cu3O7 -δ (YBCO) plays a crucial role for affecting high-temperature superconductivity. We apply (coincident) Doppler broadening spectroscopy of the electron-positron annihilation line to study in situ the temperature dependence of the oxygen concentration and its depth profile in single crystalline YBCO film grown on SrTiO3 (STO) substrates. The oxygen diffusion during tempering is found to lead to a distinct depth dependence of δ , which is not accessible using x-ray diffraction. A steady state reached within a few minutes is defined by both, the oxygen exchange at the surface and at the interface to the STO substrate. Moreover, we reveal the depth-dependent critical temperature Tc in the as prepared and tempered YBCO film.

Magnetic flux relaxation in YBa2Cu3)(7-x) thin film: Thermal or athermal

NASA Technical Reports Server (NTRS)

Vitta, Satish; Stan, M. A.; Warner, J. D.; Alterovitz, S. A.

1991-01-01

The magnetic flux relaxation behavior of YBa2Cu3O(7-x) thin film on LaAlO3 for H is parallel to c was studied in the range 4.2 - 40 K and 0.2 - 1.0 T. Both the normalized flux relaxation rate S and the net flux pinning energy U increase continuously from 1.3 x 10(exp -2) to 3.0 x 10(exp -2) and from 70 to 240 meV respectively, as the temperature T increases from 10 to 40 K. This behavior is consistent with the thermally activated flux motion model. At low temperatures, however, S is found to decrease much more slowly as compared with kT, in contradiction to the thermal activation model. This behavior is discussed in terms of the athermal quantum tunneling of flux lines. The magnetic field dependence of U, however, is not completely understood.

Forming YBa2Cu3O7-x Superconductors On Copper Substrates

NASA Technical Reports Server (NTRS)

Mackenzie, J. Devin; Young, Stanley G.

1991-01-01

Experimental process forms layer of high-critical-temperature ceramic superconductor YBa2Cu3O7-x on surface of copper substrate. Offers possible solution to problem of finishing ceramic superconductors to required final sizes and shapes (difficult problem because these materials brittle and cannot be machined or bent). Further research necessary to evaluate superconducting qualities of surface layers and optimize process.

Nonthermal response of YBa2Cu3O7-δ thin films to picosecond THz pulses

NASA Astrophysics Data System (ADS)

Probst, P.; Semenov, A.; Ries, M.; Hoehl, A.; Rieger, P.; Scheuring, A.; Judin, V.; Wünsch, S.; Il'in, K.; Smale, N.; Mathis, Y.-L.; Müller, R.; Ulm, G.; Wüstefeld, G.; Hübers, H.-W.; Hänisch, J.; Holzapfel, B.; Siegel, M.; Müller, A.-S.

2012-05-01

The photoresponse of YBa2Cu3O7-δ thin film microbridges with thicknesses between 15 and 50 nm was studied in the optical and terahertz frequency range. The voltage transients in response to short radiation pulses were recorded in real time with a resolution of a few tens of picoseconds. The bridges were excited by either femtosecond pulses at a wavelength of 0.8 μm or broadband (0.1-1.5 THz) picosecond pulses of coherent synchrotron radiation. The transients in response to optical radiation are qualitatively well explained in the framework of the two-temperature model with a fast component in the picosecond range and a bolometric nanosecond component whose decay time depends on the film thickness. The transients in the THz regime showed no bolometric component and had amplitudes up to three orders of magnitude larger than the two-temperature model predicts. Additionally THz field-dependent transients in the absence of DC bias were observed. We attribute the response in the THz regime to a rearrangement of vortices caused by high-frequency currents.

Studies of anisotropic in-plane aligned a-axis oriented YBa(2)Cu(3)O(7-x) thin films

NASA Astrophysics Data System (ADS)

Trajanovic, Zoran

1997-12-01

Due to their layered planar structure, cuprate oxide superconductors possess remarkable anisotropic properties which may be related to their high transition temperatures. In-plane aligned a-axis YBa2Cu3O7 (YBCO) films are good candidates for such anisotropic studies. Furthermore, the full advantage of favorable material characteristics can be then utilized in applications such as vertical SNS junctions with the leads along the b-direction of YBCO and other novel junction configurations. High quality, smooth, in-plane aligned films are obtained on (100) LaSrGaO4. Form x-ray data, the films show complete b- and c-axes separation for the measured a-axis orientation. The anisotropic resistivity ratio (ρ c/ρ b), measured along the two crystallographic axes of single films gives ρ c/ρ b of ≈20 near the transition, with T cs near 90 K. In such films the grain boundary effects can be decoupled from the intrinsic anisotropic properties of YBCO. From oxygen annealing studies it was estimated that the CuO chains supply about 60% of the carriers. From J c measurements it is determined that the orientation of magnetic field with respect to the crystallographic film axes is the primary factor governing the J c values. The angular dependence of J c on the applied magnetic field is compared against various theoretical models showing the best agreement with the modified Ginzburg-Landau's anisotropic mass model (at T ≈ T c) and Tinkham's thin film model (at T < T c). By utilizing the Co-dopant, the coupling between CuO2 planes and the resulting enhancement of the intrinsic anisotropy of YBCO can be studied. Deposition and cooling conditions are shown to be the primary factor that influence the quality of dopant incorporation and the resulting oxygen ordering within the YBCO lattice. Various complex structures and devices utilizing in-plane aligned, a-axis films are presented. Other materials exhibiting in-plane alignment and a-axis growth are described. Optional substrates

Momentum Dependence of Charge Excitations in YBa2Cu3O7-δ and Nd2-xCexCuO4

NASA Astrophysics Data System (ADS)

Ishii, Kenji

2006-03-01

Resonant inelastic x-ray scattering (RIXS) studies at Cu K-edge on high-Tc superconducting cuprates, YBa2Cu3O7-δ and Nd2-xCexCuO4 are presented. The superconductivity occurs in the vicinity of the Mott insulating state and it is important to clarify the nature of the Mott gap and its doping dependence. Because RIXS has an advantage that we can measure charge excitation in a wide energy-momentum space, it gives a unique opportunity to study the electronic structure of materials. We apply this technique to high-Tc superconducting cuprates. In particular the electronic structure of strongly correlated metals is in the focus of our RIXS study. The experiments were performed at BL11XU of SPring-8, Japan, where a specially designed spectrometer for inelastic x-ray scattering is installed. In optimally doped YBa2Cu3O7-δ, anisotropic spectra are observed in the ab plane of a twin-free crystal. The Mott gap excitation from the one-dimensional CuO chain is enhanced at 2 eV near the zone boundary of the chain direction, while the excitation from the CuO2 plane is broad at 1.5-4 eV and almost independent of momentum. Theoretical calculation based on the one-dimensional and two-dimensional Hubbard model reproduces the observed features in the RIXS spectra when smaller values of the on-site Coulomb energy of the chain than that of the plane are assumed. This means that the charge transfer gap of the chain is smaller than that of the plane. On the other hand, both interband excitation across the Mott gap and intraband excitation in the upper Hubbard band are observed in the electron-doped Nd2-xCexCuO4. The intensity of the interband excitation is concentrated at ˜ 2 eV near the zone boundary while a dispersion relation with a momentum-dependent width emerges in the intraband excitation. The author would like to acknowledge to his collaborators, K. Tsutsui, Y. Endoh, T. Tohyama, K. Kuzushita, T. Inami, K. Ohwada, M. Hoesch, M. Tsubota, Y. Murakami, J. Mizuki, S. Maekawa, T

Fermi surface measurements in YBa2Cu3O(7-x) and La(1.874)Sr(126)CuO4

NASA Astrophysics Data System (ADS)

Howell, R. H.; Sterne, P. A.; Solal, F.; Fluss, M. J.; Haghighi, H.; Kaiser, J. H.; Rayner, S. L.; West, R. N.; Liu, J. Z.; Shelton, R.

1991-06-01

We report new, ultra high precision measurements of the electron-positron momentum spectra of YBa2Cu3O(7-x) and La(1.874)Sr(126)CuO4. The YBCO experiments were performed on twin free, single crystals and show discontinuities with the symmetry of the Fermi surface of the CuO chain bands. Conduction band and underlying features in LSCO share the same symmetry and can only be separated with the aid of LDA calculations.

Fermi surface measurements in YBa 2Cu 3O 7- x and La 1.874Sr .126CuO 4

NASA Astrophysics Data System (ADS)

Howell, R. H.; Sterne, P. A.; Solal, F.; Fluss, M. J.; Haghight, H.; Kaiser, J. H.; Rayner, S. L.; West, R. N.; Liu, J. Z.; Shelton, R.; Kojima, H.; Kitazawa, K.

1991-12-01

We report new, ultra high precision measurements of the electron-positron momentum spectra of YBa 2Cu 3O 7- x and La 1.874Sr .126CuO 4. The YBCO experiments were performed on twin free, single crystals and show discontinuities with the symmetry of the Fermi surface of the CuO chain bands. Conduction band and underlying features in LSCO share the same symmetry and can only be separated with the aid of LDA calculations.

YBa2Cu3O x superconducting nanorods

NASA Astrophysics Data System (ADS)

Rieken, William; Bhargava, Atit; Horie, Rie; Akimitsu, Jun; Daimon, Hiroshi

2018-02-01

Herein, we report the synthesis of YBa2Cu3O x superconducting nanorods performed by solution chemistry. Initially, a mixture of fine-grained coprecipitated powder was obtained and subsequently converted to YBa2Cu3O x nanorods by heating to 1223 K in oxygen for 12 h. The nanorods are superconducting without the need for any further sintering or oxygenation, thereby providing an avenue for direct application to substrates at room temperature or direct use as formed nanorods. A critical superconducting transition temperature T c of about 92 K was achieved at a critical magnetic field of 10 Oe.

Flux pinning properties of YBa2Cu3O7-δ thin films containing a high density of nanoprecipitates: A comparative study to reveal size effects

NASA Astrophysics Data System (ADS)

Yamasaki, Hirofumi; Yamada, Hiroshi

2017-11-01

Temperature dependence of critical current density Jc(H, T) was measured in moderate magnetic fields (H ⊥ film) in two thermally co-evaporated YBa2Cu3O7-δ (YBCO) thin films (A, B) and two YBCO films (C, D) deposited using a pulsed-laser deposition method. All sample films were grown epitaxially with the c-axis perpendicular to the surface of a single-crystalline substrate. Transmission electron microscopy observation revealed that these four films contained a high density of nanoprecipitates with typical sizes of 3.6 - 5.0 nm (A), 5.0 - 7.1 nm (B), 7.0 - 10.1 nm (C) and 8.7 - 14.3 nm (D). Films A and B contained very fine nanoprecipitates, whose typical diameters Dtyp are smaller than double the estimated Ginzburg-Landau coherence length 2ξab at T = 77 K, and exhibited a steep increase of Jc with decreasing temperature. Whereas, film D, which contained relatively large nanoprecipitates (Dtyp > 2ξab at T ≤ 70 K), exhibited a gradual increase in Jc. This led to a remarkable crossing of the Jc(T) curves. The temperature dependence of Jc(H//c) under a fixed magnetic field is approximated by Jc ∼ (1 - T/Tc)m(1 + T/Tc)2 where the index m is larger for films containing finer precipitates; that is, m(A) > m(B) > m(C) > m(D). This means that finer nanoprecipitates generally cause steeper Jc increase at low temperatures, which is the origin of the observed crossing phenomenon. The experimental results are reasonably explained by several theoretical models based on the direct summation of elementary pinning forces fp calculated by core pinning interactions.

Millimeter wave transmission studies of YBa2Cu3O7-delta thin films in the 26.5 to 40.0 GHz frequency range

NASA Technical Reports Server (NTRS)

Miranda, F. A.; Gordon, W. L.; Bhasin, K. B.; Heinen, V. O.; Warner, J. D.; Valco, G. J.

1989-01-01

Millimeter wave transmission measurements through YBa2Cu3O(7-delta) thin films on MgO, ZrO2 and LaAlO3 substrates, are reported. The films (approx. 1 micron) were deposited by sequential evaporation and laser ablation techniques. Transition temperatures T sub c, ranging from 89.7 K for the Laser Ablated film on LaAlO3 to approximately 72 K for the sequentially evaporated film on MgO, were obtained. The values of the real and imaginary parts of the complex conductivity, sigma 1 and sigma 2, are obtained from the transmission data, assuming a two fluid model. The BCS approach is used to calculate values for an effective energy gap from the obtained values of sigma sub 1. A range of gap values from 2 DELTA o/K sub B T sub c = 4.19 to 4.35 was obtained. The magnetic penetration depth is evaluated from the deduced values of sigma 2. These results are discussed together with the frequency dependence of the normalized transmission amplitude, P/P sub c, below and above T sub c.

Microstructure of epitaxial ferroelectric/metal oxide electrode thin film heterostructures on LaAlO{sub 3} and silicon

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ghonge, S.G.; Goo, E.; Ramesh, R.

1994-12-31

TEM and X-ray diffraction studies of PZT, PLZT, lead titanate and bismuth titanate ferroelectric thin films and YBa{sub 2}Cu{sub 3}O{sub 7{minus}x}(YBCO), Bi{sub 2}Sr{sub 2}CaCu{sub 2}O{sub 8}(BSCCO) and La{sub 0.5}Sr{sub 0.5}CoO{sub 3}(LSCO) electrically conductive oxide thin films, that are sequentially deposited by pulsed laser ablation, show that these films may be deposited epitaxially onto LaAlO{sub 3}(LAO) or Si substrates. The conductive oxides are promising candidates for use is electrodes in place of metal electrodes in integrated ferroelectric device applications. The oxide electrodes are more chemically compatible with the ferroelectric films. High resolution electron microscopy his been used to investigate the interfacemore » between the ferroelectric and metal oxide thin films and no reaction was detected. Epitaxial growth is possible due to the similar crystal structures and the small lattice mismatch. The lattice mismatch that is present causes the domains in the ferroelectric films to be preferentially oriented and in the case of lead titanate, the film is single domain. These films may also have potential applications in integrated optical devices.« less

XANES and EXAFS study of Au-substituted YBa2Cu3O(7-delta)

NASA Technical Reports Server (NTRS)

Ruckman, Mark W.; Hepp, Aloysius F.

1990-01-01

The near-edge structure (XANES) of the Au L3 and Cu K edges of YBa2Au(0.3)Cu(2.7)O(7-delta) was studied. X ray diffraction suggests that Au goes on the Cu(1) site and XANES shows that this has little effect on the oxidation state of the remaining copper. The gold L3 edge develops a white line feature whose position lies between that of trivalent gold oxide (Au2O3) and monovalent potassium gold cyanide (KAu(CN)2) and whose intensity relative to the edge step is smaller than in the two reference compounds. The L3 EXAFS for Au in the superconductor resembles that of Au2O3. However, differences in the envelope of the Fourier filtered component for the first shell suggest that the local structure of the Au in the superconductor is not equivalent to Au2O3.

Study of Substitution of Zn FOR Cu in YBa2Cu3O7 System

NASA Astrophysics Data System (ADS)

Sharma, P. K.; Samariya, A.; Dhawan, M. S.; Singhal, R. K.

The polycrystalline YBa2(Cu1-XZnX)3O7-δ samples (x=0.0 to 0.06) were synthesized and studied using X Ray diffraction, titration, resistivity, magnetization and X ray photoelectron spectroscopy (XPS). Results show that O2 stoichiometry (δ) changes on Zn substitution which affects their normal state resistivity as well as the TC. Zn also induces local magnetic moment as evidenced from magnetization results. A combination of change in O2 stoichiometry and magnetic pair breaking is found to be responsible for a rapid suppression of superconductivity.

Elliptical flux vortices in YBa2Cu3O7

NASA Technical Reports Server (NTRS)

Hickman, H.; Dekker, A. J.; Chen, T. M.

1991-01-01

The most energetically favorable vortex in YBa2Cu3O7 forms perpendicular to an anisotropic plane. This vortex is elliptical in shape and is distinguished by an effective interchange of London penetration depths from one axis of the ellipse to another. By generalizing qualitatively from the isotropic to the anisotropic case, we suggest that the flux flow resistivity for the vortex that forms perpendicular to an anistropic plane should have a preferred direction. Similar reasoning indicates that the Kosterlitz-Thouless transition temperature for a vortex mediated transition should be lower if the vortex is elliptical in shape.

Quasiparticle properties at microwave frequencies in the underdoped YBa2Cu3O7-δ thin films

NASA Astrophysics Data System (ADS)

Hsing, Lai

2004-03-01

Microstrip ring resonators with quality factor (Q) over 10^4 at temperature 5 K were fabricated using the double-side YBa_2Cu_3O_7-δ (YBCO) films deposited on LaAlO3 (LAO) substrates. By placing a narrow gap in the ring resonator, the original fundamental resonating mode (3.61 GHz) splits into two modes (1.80 GHz and 5.33 GHz) with distinct resonating frequencies. The samples allow us to determine the temperature and the frequency dependences of penetration depth and microwave conductivity for various underdoped-cuprates by using Drude formula and the modified two-fluid model. The natures of the order parameter of high-Tc superconductivity in the underdoped cases are shown to be of d-wave type in an exact manner. In particular, the Fermi-liquid correction factor α ^2 and the vertex correction factor β from the model, proposed by Wen and Lee, can be estimated that α ^2 is doping independent in the underdoped regime and β decreases as oxygen content is decreasing in our experiment data. All these results are independent of frequencies as well. The results reveal that the interaction between quasiparticles is insensitive dependence of the impurity concentrations due to oxygen deficiency on the CuO chain and the impurity potential for forward scattering approaches the same as back scattering with more oxygen deficiency.

Nucléation et croissance de films YBa_{2Cu3O_{7 - δ}} déposés par ablation laser sur substrat de MgO(001)

NASA Astrophysics Data System (ADS)

Keller, D.; Gervais, A.; Chambonnet, D.; Belouet, C.; Audry, C.

1995-02-01

In the field of superconducting devices devoted to microwave applications, the crystalline texture of high quality thin films based on YBa{2}Cu{3}O{7 - δ} is of primary importance. This study presents the formation of this texture on MgO substrates with the nucleation and growth steps up to a film thickness of 300 nm as observed by means of AFM, HRTEM and XRD. The influence of deposition temperature on the growth mode is shown and a nucleation/growth model is discussed. The minimum roughness of c_{bot 0}{(^1)} textured films, 300 nm thick and 20 × 20 mm2 in size is as slow as 2 nm. Dans le cadre de la réalisation de composants supraconducteurs de haute qualité à base du composé YBa{2}Cu{3}O{7 - δ} destinés aux applications en hyperfréquences, le contrôle de la texture cristalline des films est de première importance. La formation de celle-ci sur substrat MgO est étudiée depuis la nucléation jusqu'à une épaisseur de 300 nm au moyen de la microscopie à force atomique, de la microscopie électronique en transmission à haute résolution et de la diffraction des rayons X. L'influence de la température de dépôt sur le mode de croissance est abordée et un modèle de nucléation/croissance est discuté. La rugosité minimale des films d'épaisseur 300 nm et de dimensions 20 × 20 mm2 de texture c_{bot 0}{(^1)} est voisine de 2 nm.

Single domain YBa2Cu3Oy thick films on metallic substrates

NASA Astrophysics Data System (ADS)

Reddy, E. S.; Noudem, J. G.; Goodilin, E. A.; Tarka, M.; Schmitz, G. J.

2003-03-01

The fabrication of single domain YBa2Cu3Oy (123) thick films (10-100 mum) on metallic substrates is reported. The process involves the formation of the 123 phase by a peritectic reaction between an air-brushed dense Y2BaCuO5 (211) layer on a Ag12Pd substrate and infiltrated liquid phases containing barium cuprates and copper oxides. Single domain growth is achieved by seeding the green films with a c-axis oriented NdBa2Cu3Oy crystal prior to processing. The maximum processing temperatures are lowered to 970 °C by modifying the characteristics of the liquid phases meant for infiltration by addition of Ag powder. The fabrication technique, processing conditions for single domain growth and the resulting microstructures are discussed.

Electronic correlations in YBa/sub 2/Cu/sub 3/O/sub 7-//sub delta/ from Auger spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Balzarotti, A.; De Crescenzi, M.; Giovannella, C.

1987-12-01

Cu L/sub 3/VV Auger spectra of the superconducting compound YBa/sub 2/Cu/sub 3/O/sub 7-//sub delta/ have been measured above and below the critical temperature T/sub c/ = 90 K and compared with those of CuO. In the superconductor a localized peak whose intensity increases with temperature is found. Such a structure, lacking in copper oxide, is attributed to electronic correlations in the Cu 3d/sup 8/ configuration.

Atomic scale real-space mapping of holes in YBa2Cu3O(6+δ).

PubMed

Gauquelin, N; Hawthorn, D G; Sawatzky, G A; Liang, R X; Bonn, D A; Hardy, W N; Botton, G A

2014-07-15

The high-temperature superconductor YBa2Cu3O(6+δ) consists of two main structural units--a bilayer of CuO2 planes that are central to superconductivity and a CuO(2+δ) chain layer. Although the functional role of the planes and chains has long been established, most probes integrate over both, which makes it difficult to distinguish the contribution of each. Here we use electron energy loss spectroscopy to directly resolve the plane and chain contributions to the electronic structure in YBa2Cu3O6 and YBa2Cu3O7. We directly probe the charge transfer of holes from the chains to the planes as a function of oxygen content, and show that the change in orbital occupation of Cu is large in the chain layer but modest in CuO2 planes, with holes in the planes doped primarily into the O 2p states. These results provide direct insight into the local electronic structure and charge transfers in this important high-temperature superconductor.

A new method for measuring low resistivity contacts between silver and YBa2Cu3O(7-x) superconductor

NASA Technical Reports Server (NTRS)

Hsi, Chi-Shiung; Haertling, Gene H.; Sherrill, Max D.

1991-01-01

Several methods of measuring contact resistivity between silver electrodes and YBa2Cu3O(7-x) superconductors were investigated; including the two-point, the three point, and the lap-joint methods. The lap-joint method was found to yield the most consistent and reliable results and is proposed as a new technique for this measurement. Painting, embedding, and melting methods were used to apply the electrodes to the superconductor. Silver electrodes produced good ohmic contacts to YBa2Cu3O(7-x) superconductors with contact resistivities as low as 1.9 x 10 to the -9th ohm sq cm.

Direct observation of vortex structure in a high-{Tc} YBa{sub 2}Cu{sub 3}O{sub 7{minus}y} thin film by Bitter decoration method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sugimoto, Akira; Yamaguchi, Tetsuji; Iguchi, Ienari

1999-12-01

The Bitter decoration technique is one of the most powerful techniques to study the vortex structure of superconductor. The authors report the observation of vortex structure in a high {Tc} YBa{sub 2}Cu{sub 3}O{sub 7{minus}y} (YBCO) thin film by Bitter decoration method. The image of vortex structure was monitored by SEM, AFM and high resolution optical microscope. For magnetic field about 4--6mT, a vortex structure is seen. The vortex image varied with changing magnetic field. As compared with the vortex image of a Bi{sub 2}Sr{sub 2}CaCu{sub 2}O{sub 8+y} single crystal, the observed image appeared to be more randomly distributed.

Microwave Conductivity of Laser Ablated YBa2Cu3O7-delta Superconducting Films and Its Relation to Microstrip Transmission Line Performance

NASA Technical Reports Server (NTRS)

Bhasin, K. B.; Warner, J. D.; Chorey, C. M.; Ebihara, B. T.; Romanofsky, R. R.; Heinen, V. O.

1990-01-01

We report on the values of the microwave conductivity in the normal (sigma(subN)) and superconducting (sigma*=sigma(sub1)-j sigma(sub2)) states of two laser ablated YBa2CU3O7(sigma) thin films at 35 GHz, in the temperature range from 20 to 300 K. The films 0.7 and 0.4 micrometers) were deposited on LaA10(sub3) by laser ablation. The conductivity was obtained from the microwave power transmitted through the films and assuming a two-fluid model. Values of sigma(subN) approximately 2.3 X 10(exp5) S/m at room temperature for both films, and of sigma(sub1) approximately 6.3 X 10(exp5) and 4.6 X 10(exp5) S/m at temperatures around 80 K were obtained for the 0.7 and 0.4 micrometer films respectively. For sigma(sub2) values of 4.9 X 10(exp6) and 5.4 X 10(exp6) S/m were obtained for the 0.7 and 0.4 micrometer films at 80 K. The expected conductor losses and Q-factor of a superconducting ring resonator were calculated using these conductivity values. The theoretical values were then compared with the experimental results obtained for a resonator fabricated from one of these films.

Effectiveness of BaTiO 3 dielectric patches on YBa 2Cu 3O 7 thin films for MEM switches

DOE PAGES

Vargas, J.; Hijazi, Y.; Noel, J.; ...

2014-05-12

A micro-electro-mechanical (MEM) switch built on a superconducting microstrip filter will be utilized to investigate BaTiO 3 dielectric patches for functional switching points of contact. Actuation voltage resulting from the MEM switch provokes static friction between the bridge membrane and BaTiO 3 insulation layer. Furthermore, the dielectric patch crystal structure and roughness affect the ability of repetitively switching cycles and lifetime. We performed a series of experiments using different deposition methods and RF magnetron sputtering was found to be the best deposition process for the BaTiO 3 layer. The effect examination of surface morphology will be presented using characterization techniquesmore » as x-ray diffraction, SEM and AFM for an optimum switching device. The thin film is made of YBa 2Cu 3O 7 deposited on LaAlO 3 substrate by pulsed laser deposition. In our work, the dielectric material sputtering pressure is set at 9.5x10 -6 Torr. The argon gas is released through a mass-flow controller to purge the system prior to deposition. RF power is 85 W at a distance of 9 cm. The behavior of Au membranes built on ultimate BaTiO 3 patches will be shown as part of the results. These novel surface patterns will in turn be used in modelling other RF MEM switch devices such as distributed-satellite communication system operating at cryogenic temperatures.« less

Investigation of flux penetration in YBa 2Cu 3O 7-δ filaments

NASA Astrophysics Data System (ADS)

Devos, P.; Buekenhoudt, A.; D'Anna, G.; André, M.-O.; Indenbom, M. V.; Benoit, W.; De Batist, R.; Cornelis, J.

1994-12-01

ac Susceptibility measurements using a low frequency torsion pendulum and an ac susceptometer were conducted on YBa 2Cu 3O 7-δ filaments in low magnetic dc fields (≤1T). Different dissipation peaks are observed, dependent on the temperature and the applied amplitude. The peak at low temperatures, which is of intergranular nature is studied in detail. The penetration follows the Bean model and the intergranular creep is observed.

Subtle porosity variation in the YBa2Cu3O(7-x) high-temperature superconductor revealed by ultrasonic imaging

NASA Technical Reports Server (NTRS)

Roth, D. J.; Generazio, E. R.; Stang, D. B.; Hepp, A. F.

1990-01-01

The characterization of global porosity variation within a nominally 93-percent-dense specimen of YBa2Cu3O(7-x) high-temperature superconductor is reported. With a computer-controlled scanning system, precision ultrasonic velocity measurements were obtained at 100 micron increments over an 8- by 8-mm area of the YBa2Cu3O(7-x) specimen. The measurements were used to form a color map of velocity variation across the scanned region of the specimen. Subtle velocity variation on the order of 1 percent was observed. The specimen was shown by experimental methods to be single-phase, untextured, and free of nonuniform residual microstresses. From this knowledge and an established velocity-density relationship, a likely conclusion is that the observed velocity variations are solely due to porosity variations of similar magnitude. Locating these subtle porosity variations is critical since they can result in an order of magnitude variation in J(sub c) for dense YBCO specimens. Thus, mapping the global porosity distribution within YBa2Cu3O(7-x) may reveal regions that have poorer superconducting properties. Ultrasonic velocity results are translated into useful microstructural information for the material scientist.

Investigations of YBa2Cu3O y films sputtered onto a substrate of amorphous quartz with a platinum buffer layer

NASA Astrophysics Data System (ADS)

Blinova, Yu. V.; Snigirev, O. V.; Porokhov, N. V.; Evlashin, S. A.

2017-10-01

Results of investigations using X-ray diffraction and scanning electron microscopy of composite materials made from YBa2Cu3O y films sputtered (using various regimes) onto a substrate of amorphous quartz with a platinum buffer layer, have been given.

Determination of surface resistance and magnetic penetration depth of superconducting YBa2Cu3O(7-delta) thin films by microwave power transmission measurements

NASA Technical Reports Server (NTRS)

Bhasin, K. B.; Warner, J. D.; Miranda, F. A.; Gordon, W. L.; Newman, H. S.

1991-01-01

A novel waveguide power transmission measurement technique was developed to extract the complex conductivity of superconducting thin films at microwave frequencies. The microwave conductivity was taken of two laser ablated YBa2Cu3O(7-delta) thin films on LaAlO3 with transition temperatures of approximately 86.3 and 82 K, respectively, in the temperature range 25 to 300 K. From the conductivity values, the penetration depth was found to be approximately 0.54 and 0.43 micron, and the surface resistance (R sub s) to be approximately 24 and 36 micro-Ohms at 36 GHz and 76 K for the two films under consideration. The R sub s values were compared with those obtained from the change in the Q-factor of a 36 GHz Te sub 011-mode (OFHC) copper cavity by replacing one of its end walls with the superconducting sample. This technique allows noninvasive characterization of high transition superconducting thin films at microwave frequencies.

Determination of surface resistance and magnetic penetration depth of superconducting YBa2Cu3O(7-delta) thin films by microwave power transmission measurements

NASA Technical Reports Server (NTRS)

Bhasin, K. B.; Warner, J. D.; Miranda, F. A.; Gordon, W. L.; Newman, H. S.

1990-01-01

A novel waveguide power transmission measurement technique was developed to extract the complex conductivity of superconducting thin films at microwave frequencies. The microwave conductivity was taken of two laser ablated YBa2Cu3O(7-delta) thin films on LaAlO3 with transition temperatures of approx. 86.3 and 82 K, respectively, in the temperature range 25 to 300 K. From the conductivity values, the penetration depth was found to be approx. 0.54 and 0.43 micron, and the surface resistance (R sub s) to be approx. 24 and 36 micro-Ohms at 36 GHz and 76 K for the two films under consideration. The R sub s values were compared with those obtained from the change in the Q-factor of a 36 GHz Te sub 011-mode (OFHC) copper cavity by replacing one of its end walls with the superconducting sample. This technique allows noninvasive characterization of high transition temperature superconducting thin films at microwave frequencies.

Composition dependence of superconductivity in YBa2(Cu(3-x)Al(x))O(y)

NASA Technical Reports Server (NTRS)

Bansal, N. P.

1993-01-01

Eleven different compositions in the system YBa2(Cu(3-x)Al(x))O(y) (x = 0 to 0.3) have been synthesized and characterized by electrical resistivity measurements, powder X-ray diffraction, and scanning electron microscopy. The superconducting transition temperature T sub c (onset) was almost unaffected by the presence of alumina due to its limited solubility in YBa2Cu3O(7-x). However, T sub c(R = 0) gradually decreased, and the resistive tails became longer with increasing Al2O3 concentration. This was probably due to formation of BaAl2O4 and other impurity phases from chemical decomposition of the superconducting phase by reaction with Al2O3.

Atomic and electronic structures of BaHfO3-doped TFA-MOD-derived YBa2Cu3O7-δ thin films

NASA Astrophysics Data System (ADS)

Molina-Luna, Leopoldo; Duerrschnabel, Michael; Turner, Stuart; Erbe, Manuela; Martinez, Gerardo T.; Van Aert, Sandra; Holzapfel, Bernhard; Van Tendeloo, Gustaaf

2015-11-01

Tailoring the properties of oxide-based nanocomposites is of great importance for a wide range of materials relevant for energy technology. YBa2Cu3O7-δ (YBCO) superconducting thin films containing nanosized BaHfO3 (BHO) particles yield a significant improvement of the magnetic flux pinning properties and a reduced anisotropy of the critical current density. These films were prepared by chemical solution deposition (CSD) on (100) SrTiO3 (STO) substrates yielding critical current densities up to 3.6 MA cm-2 at 77 K and self-field. Transport in-field J c measurements demonstrated a high pinning force maximum of around 6 GN/m3 for a sample annealed at T = 760 °C that has a doping of 12 mol% of BHO. This sample was investigated by scanning transmission electron microscopy (STEM) in combination with electron energy-loss spectroscopy (EELS) yielding strain and spectral maps. Spherical BHO nanoparticles of 15 nm in size were found in the matrix, whereas the particles at the interface were flat. A 2 nm diffusion layer containing Ti was found at the YBCO (BHO)/STO interface. Local lattice deformation mapping at the atomic scale revealed crystal defects induced by the presence of both sorts of BHO nanoparticles, which can act as pinning centers for magnetic flux lines. Two types of local lattice defects were identified and imaged: (i) misfit edge dislocations and (ii) Ba-Cu-Cu-Ba stacking faults (Y-248 intergrowths). The local electronic structure and charge transfer were probed by high energy resolution monochromated electron energy-loss spectroscopy. This technique made it possible to distinguish superconducting from non-superconducting areas in nanocomposite samples with atomic resolution in real space, allowing the identification of local pinning sites on the order of the coherence length of YBCO (˜1.5 nm) and the determination of 0.25 nm dislocation cores.

Oxygen desorption from YBa2Cu3O(7-x) and Bi2CaSr2Cu2O(8 + delta) superconductors

NASA Technical Reports Server (NTRS)

Mesarwi, A.; Levenson, L. L.; Ignatiev, A.

1991-01-01

Oxygen desorption experiments from YBa2Cu3O(7-x) (YBCO) and Bi2CaSr2Cu2O(8 + delta) (BSCCO) superconductors were carried out using a quadrupole mass spectrometer for monitoring the desorbing species and X-ray photoemission spectroscopy for surface characterization. Molecular oxygen was found to desorb from both superconductors following photoirradiation with ultraviolet/optical radiation and subsequent heating at over 150 C. Both YBCO and BSCCO were found to have similar oxygen desorption rates and similar activation energies. The desorption data as well as the X-ray photoemission data indicate that the oxygen desorption is not intrinsic to the superconductors but rather due to molecular oxygen entrapped in the material.

High sensitivity of positrons to oxygen vacancies and to copper-oxygen chain disorder in YBa2Cu3O(7-x)

NASA Astrophysics Data System (ADS)

von Stetten, E. C.; Berko, S.; Li, X. S.; Lee, R. R.; Brynestad, J.

1988-05-01

Temperature-dependent positron-electron momentum densities have been studied by two-dimensional angular correlation of annihilation radiation from 10 to 320 K in YBa2Cu3O(7-x) samples. The positron ground-state charge density, computed by the linearized augmented-plane-wave method, indicates that in YBa2Cu3O7 delocalized positrons sample preferentially the linear copper-oxygen chains. Positron localization due to disorder in these chains is invoked to explain the striking differences observed between superconducting (x = about 0.02) and nonsuperconducting (x = about 0.70) samples.

Reaction of YBa2Cu3O(7-beta) with Gold, Silver, Bismuth and Lead: Substitution Chemistry and Composite Fabrication

NASA Technical Reports Server (NTRS)

Hepp, Aloysius F.; Gaier, James R.

1993-01-01

The reaction of YBa2Cu3O(7-beta) with Au, Ag, Bi, and Ph ions or metal is described. Three types of materials were produced: a well-defined series of homogeneous superconductors was obtained for Au ion substitution with little effect on T(sub c); attempted Ag and Bi ion substitution resulted in multi-phase samples with slightly enhanced T(sub c); finally, attempts to produce superconducting metal/superconducting ceramic composites with Pb and Bi powders resulted in multi-phase samples with drastically diminished superconducting properties. For Au- substituted superconductors, YBa2(Cu(l-x)Au(x))3O(7-beta), a substitution series (x = 0 - 0.1) has been synthesized. For x = 0.1 there was no change in the a and b lattice parameters (a = 3.826 A and b = 3.889 A) but a 0.06 A c axis expansion to 11.75 A was observed. The valence of Cu and Au in YBa2Au(0.3)Cu(2.7)O(7-beta) was investigated using X-ray Absorption Near-Edge Structure (XANES). X-ray studies indicate that Au goes into the Cu(l) site and Cu K edge XANES shows that this has little effect on the oxidation state of the remaining copper. A small effect on T(sub c) is observed (T(sub c) = 89 K for x = 0.10). Ag and Bi addition results in a rise in T(sub c) and a decrease in (delta)T(sub c) at low levels (x = 0.10 Ag, T(sub c) = 94 K and (delta)T(sub c) = 0.5 K; x = 0.02 Bi, T(sub c) = 94 K and (delta)T(sub c) = 1K) relative to typical values for YBa2Cu3O(7-beta) (T(sub c) = 91 K, (delta)T(sub c) = 2 K). Attempts at fabrication of Pb- and Pb(1-x)Bi(x)-superconductor composites are described. Cold pressing followed by low temperature (200 C) sintering resulted in a composite which excluded flux below 90 K but did not show zero electrical resistance until the metal (alloy) superconducting transition. X-ray diffraction showed the presence of pervoskite and metal. Processing at moderate (450 C) or high (950 C) temperatures resulted in oxygen-depleted pervoskite and/or metal oxides. These materials displayed greatly

Spectrophotometric Determination of the Hole Concentration in the Superconductor YBa2Cu3O(sub 7-x)

ERIC Educational Resources Information Center

Hoppe, Jack I.; Malati, Mounir A.

2005-01-01

An experimental study of ceramic superconductors namely YBa2Cu3O(sub 7-x), which illustrates the use of spectrophotometry, based on the electronic spectra of complexes of Fe(II), Fe(III) and Cu(II) to better understand the stoichiometry of YBCO is described. The results from this experiment are in good agreement with those obtained by the…

Crystalline orientation engineering and charge transport in thin film YBa(2)Cu(3)O(7-x) superconducting surface-coated conductors

NASA Astrophysics Data System (ADS)

Chudzik, Michael Patrick

The weak-link behavior of grain boundaries in polycrystalline high-T c superconductors adversely affects the current density in these materials. The development of wire technology based on polycrystalline high-Tc materials requires understanding and controlling the development of low-angle grain boundaries in these conductors. The research goal is to comprehensively examine the methodology in fabrication and characterization to understand the structure-transport correlation in YBa2Cu3O 7-x (YBCO) surface-coated conductors. High current density YBCO coated conductors were fabricated and characterized as candidates for second generation high-Tc wire technology. Critical current densities (Jc) greater than 1 x 106 A/cm2 at 77 K and zero magnetic field were obtained using thin films epitaxially grown by metalorganic chemical vapor deposition (MOCVD) and pulsed laser deposition (PLD) on oriented buffer layers. The biaxially textured oxide buffer layers were deposited by ion-beam-assisted deposition (IBAD). The transport properties of coated conductors were evaluated in high magnetic fields for intrinsic and extrinsic flux vortex pinning effects for improved high-field properties. Transport Jc's of these coated conductors at 7 tesla (77 K) were measured at values greater than 105 A/cm 2 with the magnetic field perpendicular to the YBCO c-axis (B⊥ c) in both MOCVD and PLD derived conductors. The Jc's in B || c orientation fell an order of magnitude lower at 7 tesla to values near 10 4 A/cm2 due to decreased intrinsic flux pinning. The critical current densities as a function of grain boundary misorientation were found to deviate from the general trend determined for single grain boundary junctions, due to the mosaic structure, which allows meandering current flow. Extensive parametric investigations of relevant thin film growth techniques were utilized to establish growth-property relationships that led to optimized fabrication of high-Tc conductors. The work contained

High-temperature change of the creep rate in YBa2Cu3O7-δ films with different pinning landscapes

NASA Astrophysics Data System (ADS)

Haberkorn, N.; Miura, M.; Baca, J.; Maiorov, B.; Usov, I.; Dowden, P.; Foltyn, S. R.; Holesinger, T. G.; Willis, J. O.; Marken, K. R.; Izumi, T.; Shiohara, Y.; Civale, L.

2012-05-01

Magnetic relaxation measurements in YBa2Cu3O7-δ (YBCO) films at intermediate and high temperatures show that the collective vortex creep based on the elastic motion of the vortex lattice has a crossover to fast creep that significantly reduces the superconducting critical current density (Jc). This crossover occurs at temperatures much lower than the irreversibility field line. We study the influence of different kinds of crystalline defects, such as nanorods, twin boundaries, and nanoparticles, on the high-temperature vortex phase diagram of YBCO films. We found that the magnetization relaxation data is a fundamental tool to understand the pinning at high temperatures. The results indicate that high Jc values are directly associated with small creep rates. Based on the analysis of the depinning temperature in films with columnar defects, our results indicate that the size of the defects is the relevant parameter that determines thermal depinning at high temperatures. Also, the extension of the collective creep regime depends on the density of the pinning centers.

Large pinning forces and matching effects in YBa2Cu3O7-δ thin films with Ba2Y(Nb/Ta)O6 nano-precipitates

PubMed Central

Opherden, Lars; Sieger, Max; Pahlke, Patrick; Hühne, Ruben; Schultz, Ludwig; Meledin, Alexander; Van Tendeloo, Gustaaf; Nast, Rainer; Holzapfel, Bernhard; Bianchetti, Marco; MacManus-Driscoll, Judith L.; Hänisch, Jens

2016-01-01

The addition of mixed double perovskite Ba2Y(Nb/Ta)O6 (BYNTO) to YBa2Cu3O7−δ (YBCO) thin films leads to a large improvement of the in-field current carrying capability. For low deposition rates, BYNTO grows as well-oriented, densely distributed nanocolumns. We achieved a pinning force density of 25 GN/m3 at 77 K at a matching field of 2.3 T, which is among the highest values reported for YBCO. The anisotropy of the critical current density shows a complex behavior whereby additional maxima are developed at field dependent angles. This is caused by a matching effect of the magnetic fields c-axis component. The exponent N of the current-voltage characteristics (inversely proportional to the creep rate S) allows the depinning mechanism to be determined. It changes from a double-kink excitation below the matching field to pinning-potential-determined creep above it. PMID:26887291

Large pinning forces and matching effects in YBa2Cu3O7-δ thin films with Ba2Y(Nb/Ta)O6 nano-precipitates

NASA Astrophysics Data System (ADS)

Opherden, Lars; Sieger, Max; Pahlke, Patrick; Hühne, Ruben; Schultz, Ludwig; Meledin, Alexander; van Tendeloo, Gustaaf; Nast, Rainer; Holzapfel, Bernhard; Bianchetti, Marco; MacManus-Driscoll, Judith L.; Hänisch, Jens

2016-02-01

The addition of mixed double perovskite Ba2Y(Nb/Ta)O6 (BYNTO) to YBa2Cu3O7-δ (YBCO) thin films leads to a large improvement of the in-field current carrying capability. For low deposition rates, BYNTO grows as well-oriented, densely distributed nanocolumns. We achieved a pinning force density of 25 GN/m3 at 77 K at a matching field of 2.3 T, which is among the highest values reported for YBCO. The anisotropy of the critical current density shows a complex behavior whereby additional maxima are developed at field dependent angles. This is caused by a matching effect of the magnetic fields c-axis component. The exponent N of the current-voltage characteristics (inversely proportional to the creep rate S) allows the depinning mechanism to be determined. It changes from a double-kink excitation below the matching field to pinning-potential-determined creep above it.

Shaping and reinforcement of melt textured YBa2Cu3O7-δ superconductors

NASA Astrophysics Data System (ADS)

Meslin, S.; Harnois, C.; Chubilleau, C.; Horvath, D.; Grossin, D.; Suddhakar, E. R.; Noudem, J. G.

2006-07-01

From porous Y2BaCuO5 (Y211) with various grain sizes, single domain ceramic composites YBa2Cu3Oy/Y2BaCuO5 have been prepared by combination of the infiltration and top seed growth (ITSG) process. In addition, perforated Y123 has been prepared from Y211 by the ITSG method in order to magnify the specific surface and then increase oxygen diffusion into the core of the material. Magnetic and electrical properties were determined and correlate well with the microstructure of the composites and were compared to the conventional doped or undoped YBa2Cu3Oy (Y123). From magnetic measurements, high critical current densities, Jc, of 86 000 A cm-2 have been measured. Transport Jc values higher than 10 600 A cm-2 are reached at 77 K and 0 T, corresponding to the nominal critical currents of 325 A injected reproducibly through sections less than 3.082 mm2. This confirms the high quality of single domains obtained with a well controlled ITSG process. On the other hand, the perforated samples were reinforced using resin impregnation and the flux mapping has been investigated.

Room temperature degradation of YBa2Cu3O(7-x) superconductors in varying relative humidity environments

NASA Technical Reports Server (NTRS)

Hooker, M. W.; Wise, S. A.; Carlberg, I. A.; Stephens, R. M.; Simchick, R. T.; Farjami, A.

1993-01-01

An aging study was performed to determine the stability of YBa2Cu3O(7-x) ceramics in humid environments at 20 C. In this study, fired ceramic specimens were exposed to humidity levels ranging from 30.5 to 100 percent for 2-, 4-, and 6-week time intervals. After storage under these conditions, the specimens were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and electrical resistance measurements. At every storage condition evaluated, the fired ceramics were found to interact with H2O present in the surrounding environment, resulting in the decomposition of the YBa2Cu3O(7-x) phase. XRD data showed that BaCO3, CuO, and Y2BaCuO5 were present after aging and that the peak intensities of these impurity phases increased both with increasing humidity level and with increasing time of exposure. Additionally, SEM analyses of the ceramic microstructures after aging revealed the development of needle-like crystallites along the surface of the test specimens after aging. Furthermore, the superconducting transition temperature T(sub c) was found to decrease both with increasing humidity level and with increasing time of exposure. All the specimens aged at 30.5, 66, and 81 percent relative humidity exhibited superconducting transitions above 80 K, although these values were reduced by the exposure to the test conditions. Conversely, the specimens stored in direct contact with water (100 percent relative humidity) exhibited no superconducting transitions.

The effect of fluctuations on the electrical transport behavior in YBa2Cu3O(7-x)

NASA Technical Reports Server (NTRS)

Vitta, Satish; Alterovitz, S. A.; Stan, M. A.

1993-01-01

The excess conductivity behavior of highly oriented YBa2Cu3O(7-x) thin films prepared by both coevaporation and laser ablation was studied in detail in the reduced-temperature range 9 x 10(exp -4) is less than t is less than 1. The excess conductivity in all the films studied was found to diverge sharply near T(sub c), in agreement with the conventional mean-field theory. However, the detailed temperature dependence could not be fitted to either the power-law or the logarithmic functional forms as predicted by the theory. The excess conductivity of all the films was found to be exponentially dependent on the temperature over nearly three decades for 9 x 10(exp -4) is less than t is less than 10(exp -1), in contradiction to the mean-field theory.

Chemical durability of high-temperature superconductor YBa2Cu3O(7-x) in aqueous environments

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.; Sandkuhl, Ann L.

1988-01-01

The stability of YBa2Cu3O(7-x) in water and 100-percent humidity has been investigated at three temperatures, using pH measurements, X-ray diffraction, and scanning electron microscopy. The oxide-ceramic superconductor is highly unstable; it reacts rapidly with water and degrades in moisture. Dissolution of the oxide perovskite in water is highly incongruent. The corrosion products are found to be BaCO3, CuO, O2, etc. Barium hydroxide is first formed and further reacts with atmospheric CO2 to form needle-shaped crystals of BaCO3. For any practical applications, devices made from these materials would have to be protected with an impermeable coating to prevent deterioration from atmosphere.

Induced Ferromagnetism at BiFeO 3/YBa 2Cu 3O 7 Interfaces

DOE PAGES

Zhu, Jian-Xin; Wen, Xiao-Dong; Haraldsen, J. T.; ...

2014-06-20

We report that transition metal oxides (TMOs) exhibit many emergent phenomena ranging from high-temperature superconductivity and giant magnetoresistance to magnetism and ferroelectricity. In addition, when TMOs are interfaced with each other, new functionalities can arise, which are absent in individual components. Here, we report results from first-principles calculations on the magnetism at the BiFeO 3/YBa 2Cu 3O 7 interfaces. By comparing the total energy for various magnetic spin configurations inside BiFeO 3, we are able to show that a metallic ferromagnetism is induced near the interface. We further develop an interface exchange-coupling model and place the extracted exchange coupling interactionmore » strengths, from the first-principles calculations, into a resultant generic phase diagram. Our conclusion of interfacial ferromagnetism is confirmed by the presence of a hysteresis loop in field-dependent magnetization data. Lastly, the emergence of interfacial ferromagnetism should have implications to electronic and transport properties.« less

Disentangling vortex pinning landscape in chemical solution deposited superconducting YBa2Cu3O7-x films and nanocomposites

NASA Astrophysics Data System (ADS)

Palau, A.; Vallès, F.; Rouco, V.; Coll, M.; Li, Z.; Pop, C.; Mundet, B.; Gàzquez, J.; Guzman, R.; Gutierrez, J.; Obradors, X.; Puig, T.

2018-07-01

In-field angular pinning performances at different temperatures have been analysed on chemical solution deposited (CSD) YBa2Cu3O7-x (YBCO) pristine films and nanocomposites. We show that with this analysis we are able to quantify the vortex pinning strength and energies, associated with different kinds of natural and artificial pinning defects, acting as efficient pinning centres at different regions of the H-T phase diagram. A good quantification of the variety of pinning defects active at different temperatures and magnetic fields provides a unique tool to design the best vortex pinning landscape under different operating conditions. We have found that by artificially introducing a unique defect in the YBCO matrix, the stacking faults, we are able to modify three different contributions to vortex pinning (isotropic-strong, anisotropic-strong, and isotropic-weak). The isotropic-strong contribution, widely studied in CSD YBCO nanocomposites, is associated with nanostrained regions induced at the partial dislocations surrounding the stacking faults. Moreover, the stacking fault itself acts as a planar defect which provides a very effective anisotropic-strong pinning at H//ab. Finally, the large presence of Cu-O cluster vacancies found in the stacking faults have been revealed as a source of isotropic-weak pinning sites, very active at low temperatures and high fields.

Selective interlayer ferromagnetic coupling between the Cu spins in YBa2Cu3O7−x grown on top of La0.7Ca0.3MnO3

PubMed Central

Huang, S. W.; Wray, L. Andrew; Jeng, Horng-Tay; Tra, V. T.; Lee, J. M.; Langner, M. C.; Chen, J. M.; Roy, S.; Chu, Y. H.; Schoenlein, R. W.; Chuang, Y.-D.; Lin, J.-Y.

2015-01-01

Studies to date on ferromagnet/d-wave superconductor heterostructures focus mainly on the effects at or near the interfaces while the response of bulk properties to heterostructuring is overlooked. Here we use resonant soft x-ray scattering spectroscopy to reveal a novel c-axis ferromagnetic coupling between the in-plane Cu spins in YBa2Cu3O7−x (YBCO) superconductor when it is grown on top of ferromagnetic La0.7Ca0.3MnO3 (LCMO) manganite layer. This coupling, present in both normal and superconducting states of YBCO, is sensitive to the interfacial termination such that it is only observed in bilayers with MnO2 but not with La0.7Ca0.3O interfacial termination. Such contrasting behaviors, we propose, are due to distinct energetic of CuO chain and CuO2 plane at the La0.7Ca0.3O and MnO2 terminated interfaces respectively, therefore influencing the transfer of spin-polarized electrons from manganite to cuprate differently. Our findings suggest that the superconducting/ferromagnetic bilayers with proper interfacial engineering can be good candidates for searching the theorized Fulde-Ferrel-Larkin-Ovchinnikov (FFLO) state in cuprates and studying the competing quantum orders in highly correlated electron systems. PMID:26573394

Interplay between current driven ferromagnetism in charge ordered antiferromagnetic Pr0.5Ca0.5MnO3 and superconducting YBa2Cu3O7-δ thin film multilayer

NASA Astrophysics Data System (ADS)

Baisnab, Dipak Kumar; Sardar, Manas; Amaladass, E. P.; Vaidhyanathan, L. S.; Baskaran, R.

2018-07-01

Thin film multilayer heterostructure of alternate YBa2Cu3O7-δ (YBCO) and Pr0.5Ca0.5MnO3 (PCMO) with thickness of each layer ∼60 nm has been deposited on (100) oriented SrTiO3 substrate by Pulsed Laser Deposition technique. A half portion of the base YBCO layer was masked in situ using mechanical shadow mask and in the remaining half portion, five alternate layers of PCMO and YBCO thin films were deposited. Magnetoresistance measurements were carried out under externally applied magnetic field and injection current. A noticeable damped oscillation of the superconducting transition temperature (TC) of this multilayer with respect to magnetic field is seen. Curiously, the field at which the first minimum in TC occurs, decreases as an injection current is driven perpendicular/parallel to the multilayers. Both these phenomena indicate that ferromagnetic correlation can be induced in antiferromagnetic PCMO thin films by (1) external magnetic field, or (2) injection current. While (1) is well researched, our study indicates that ferromagnetism can be induced by small amount of current in PCMO thin films. This unusual behavior points towards the strongly correlated nature of electrons in PCMO.

Phonon Dispersion Measurements of YBa 2Cu 3O 6.15 and YBa 2Cu 3O 6.95 by Time-of-Flight Neutron Spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chung, J.-H.; Egami, T.; McQueeny, R. J.

We measured the phonon dispersions of YBa{sub 2}Cu{sub 3}O{sub 6.15} and YBa{sub 2}Cu{sub 3}O{sub 6.95} by time-of-flight inelastic neutron scattering. The in-plane bond-stretching modes in the metallic phase showed a distinct a-b plane anisotropy beyond what is expected for structural origin. Such anisotropy in the longitudinal optical modes, which is absent in the TO, suggests strong in-plane anisotropy in the underlying electronic structure. Apical oxygen bond-stretching modes showed a large frequency change between the insulating and the metallic phases. This large softening also is beyond structural origin, and suggests the effect of local electronic environment.

Theoretical calculations of oxygen relaxation in YBa2Cu3O6+x ceramics

NASA Astrophysics Data System (ADS)

Mi, Y.; Schaller, R.; Sathish, S.; Benoit, W.

1991-12-01

A two-dimensional theoretical model of stress-induced point-defect relaxation in a layered structure is presented, with a detailed discussion of the special case of YBa2Cu3O6+x. The experimental results of oxygen relaxation in YBa2Cu3O6+x can be explained qualitatively by this model.

Crossover between superconductivity and magnetism in SrRuO3 mesocrystal embedded YBa2Cu3O7-x heterostructures.

PubMed

Suresh, Vandrangi; Lin, Jheng-Cyuan; Liu, Heng-Jui; Zhang, Zaoli; Chiang, Ping-Chih; Hsun, Yu-Ching; Chen, Yi-Chun; Lin, Jiunn-Yuan; Chu, Ying-Hao

2016-11-03

The competition between superconductivity and ferromagnetism poses great challenges and has attracted renewed interest for applications in novel spintronic devices. In order to emphasize their interactions, we fabricated a heterostructure composed of superconducting YBa 2 Cu 3 O 7-δ (YBCO) film embedded with itinerant ferromagnetic SrRuO 3 (SRO) mesocrystals. Starting from a doping concentration of 10 vol% of SRO mesocrystal in a YBCO matrix, corresponding to the density of SRO nanocrystals ∼5 × 10 9 cm -2 , which exhibits the typical characteristic of a metal-superconductor transition, and then increasing the magnetic interactions as a function of SRO embedment, the electronic correlation and the interplay between superconductivity and magnetism throughout the temperature regime were investigated. A metal-insulator transition in the normal state of YBCO and a crossover between superconductivity and magnetism at low temperatures were found upon increasing the density of nano-size SRO crystallites in the YBCO matrix as a consequence of competing interactions between these two ordered phases.

Epitaxial growth of iridate pyrochlore Nd 2Ir 2O 7 films

DOE PAGES

Gallagher, J. C.; Esser, B. D.; Morrow, R.; ...

2016-02-29

Epitaxial films of the pyrochlore Nd 2Ir 2O 7 have been grown on (111)-oriented yttria-stabilized zirconia (YSZ) substrates by off-axis sputtering followed by post-growth annealing. X-ray diffraction (XRD) results demonstrate phase-pure epitaxial growth of the pyrochlore films on YSZ. Scanning transmission electron microscopy (STEM) investigation of an Nd 2Ir 2O 7 film with a short post-annealing provides insight into the mechanism for crystallization of Nd 2Ir 2O 7 during the post-annealing process. STEM images reveal clear pyrochlore ordering of Nd and Ir in the films. As a result, the epitaxial relationship between the YSZ and Nd 2Ir 2O 7 ismore » observed clearly while some interfacial regions show a thin region with polycrystalline Ir nanocrystals.« less

Process for forming epitaxial perovskite thin film layers using halide precursors

DOEpatents

Clem, Paul G.; Rodriguez, Mark A.; Voigt, James A.; Ashley, Carol S.

2001-01-01

A process for forming an epitaxial perovskite-phase thin film on a substrate. This thin film can act as a buffer layer between a Ni substrate and a YBa.sub.2 Cu.sub.3 O.sub.7-x superconductor layer. The process utilizes alkali or alkaline metal acetates dissolved in halogenated organic acid along with titanium isopropoxide to dip or spin-coat the substrate which is then heated to about 700.degree. C. in an inert gas atmosphere to form the epitaxial film on the substrate. The YBCO superconductor can then be deposited on the layer formed by this invention.

Distribution of flux-pinning energies in YBa2Cu3O(7-delta) and Bi2Sr2CaCu2O(8+delta) from flux noise

NASA Astrophysics Data System (ADS)

Ferrari, M. J.; Johnson, Mark; Wellstood, Frederick C.; Clarke, John; Mitzi, D.

1990-01-01

The spectral density of the magnetic flux noise measured in high-temperature superconductors in low magnetic fields scales approximately as the inverse of the frequency and increases with temperature. The temperature and frequency dependence of the noise are used to determine the pinning energies of individual flux vortices in thermal equilibrium. The distribution of pinning energies below 0.1 eV in YBa(2)Cu(3)O(7-delta) and near 0.2 eV in Bi(2)Sr(2)CaCu(2)O(8+delta). The noise power is proportional to the ambient magnetic field, indicating that the vortex motion is uncorrelated.

Selective interlayer ferromagnetic coupling between the Cu spins in YBa 2Cu 3O 7–x grown on top of La 0.7Ca 0.3MnO 3

DOE PAGES

Huang, S. W.; Wray, L. Andrew; Jeng, Horng -Tay; ...

2015-11-17

Studies to date on ferromagnet/d-wave superconductor heterostructures focus mainly on the effects at or near the interfaces while the response of bulk properties to heterostructuring is overlooked. Here we use resonant soft x-ray scattering spectroscopy to reveal a novel c-axis ferromagnetic coupling between the in-plane Cu spins in YBa 2Cu 3O 7–x (YBCO) superconductor when it is grown on top of ferromagnetic La 0.7Ca 0.3MnO 3 (LCMO) manganite layer. This coupling, present in both normal and superconducting states of YBCO, is sensitive to the interfacial termination such that it is only observed in bilayers with MnO 2 but not withmore » La 0.7Ca 0.3O interfacial termination. Thus, such contrasting behaviors, we propose, are due to distinct energetic of CuO chain and CuO 2 plane at the La 0.7Ca 0.3O and MnO 2 terminated interfaces respectively, therefore influencing the transfer of spin-polarized electrons from manganite to cuprate differently. Our findings suggest that the superconducting/ferromagnetic bilayers with proper interfacial engineering can be good candidates for searching the theorized Fulde-Ferrel-Larkin-Ovchinnikov (FFLO) state in cuprates and studying the competing quantum orders in highly correlated electron systems.« less

Transport properties of ultrathin YBa2Cu3O7 -δ nanowires: A route to single-photon detection

NASA Astrophysics Data System (ADS)

Arpaia, Riccardo; Golubev, Dmitri; Baghdadi, Reza; Ciancio, Regina; Dražić, Goran; Orgiani, Pasquale; Montemurro, Domenico; Bauch, Thilo; Lombardi, Floriana

2017-08-01

We report on the growth and characterization of ultrathin YBa2Cu3O7 -δ (YBCO) films on MgO (110) substrates, which exhibit superconducting properties at thicknesses down to 3 nm. YBCO nanowires, with thicknesses down to 10 nm and widths down to 65 nm, have also been successfully fabricated. The nanowires protected by a Au capping layer show superconducting properties close to the as-grown films and critical current densities, which are limited by only vortex dynamics. The 10-nm-thick YBCO nanowires without the Au capping present hysteretic current-voltage characteristics, characterized by a voltage switch which drives the nanowires directly from the superconducting to the normal state. We associate such bistability to the presence of localized normal domains within the superconductor. The presence of the voltage switch in ultrathin YBCO nanostructures, characterized by high sheet resistance values and high critical current values, makes our nanowires very attractive devices to engineer single-photon detectors.

Method for preparation of textured YBa.sub.2 Cu.sub.3 O.sub.x superconductor

DOEpatents

Selvamanickam, Venkat; Goyal, Amit; Kroeger, Donald M.

1998-01-01

The present invention relate to textured YBa.sub.2 Cu.sub.3 O.sub.x (Y-123) superconductors and a process of preparing them by directional recrystallization of compacts fabricated from quenched YBCO powders at temperatures about 100.degree. C. below the peritectic temperature to provide a superconductor where more than 75% of the YBa.sub.2 Cu.sub.3 O.sub.x phase is obtained without any Y.sub.2 BaCuO.sub.5 .

Scanning micro-Hall probe mapping of magnetic flux distributions and current densities in YBa{sub 2}Cu{sub 3}O{sub 7}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xing, W.; Heinrich, B.; Zhou, H.

1994-12-31

Mapping of the magnetic flux density B{sub z} (perpendicular to the film plane) for a YBa{sub 2}Cu{sub 3}O{sub 7} thin-film sample was carried out using a scanning micro-Hall probe. The sheet magnetization and sheet current densities were calculated from the B{sub z} distributions. From the known sheet magnetization, the tangential (B{sub x,y}) and normal components of the flux density B were calculated in the vicinity of the film. It was found that the sheet current density was mostly determined by 2B{sub x,y}/d, where d is the film thickness. The evolution of flux penetration as a function of applied field willmore » be shown.« less

Pinning-to-barrier crossover in YBa2Cu3O7-δ single crystals

NASA Astrophysics Data System (ADS)

Indenbom, M. V.; van der Beek, C. J.; Berseth, V.; Konczykowski, M.; Holtzberg, F.; Benoit, W.

1996-03-01

The behaviour of magnetic flux in high purity untwinned YBa2Cu3O7-δ (YBCO) single crystals is visualised by means of the magneto-optical technique. It is observed that after zero field-cooling at high temperatures near T c , flux penetrates directly to the sample center over a flux free edge area, in contrast to the usual Bean-like flux penetration from the edges. This fact clearly shows that volume pinning becomes negligible compared with the edge barrier. The role of the recently rediscovered geometrical barrier in the crystal magnetisation is discussed.

Bulk modulus and its pressure derivative of YBa2Cu3O7-x

NASA Astrophysics Data System (ADS)

Cankurtaran, M.; Saunders, G. A.; Willis, J. R.; Al-Kheffaji, A.; Almond, D. P.

1989-02-01

Pressure dependences of the ultrasonic wave velocities in polycrystalline YBa2Cu3O7-x are reported. Porosity effects are taken into account using wave-scattering theory in a porous medium. The bulk modulus B0 at atmospheric pressure for the nonporous matrix is 65 GPa, much smaller than B(P) obtained at high pressures from lattice-parameter measurements. This discrepancy accrues from the large value of (∂B/∂P). The comparatively small B0 and large (∂B/∂P) are due to vacant anion sites in this defect perovskite.

TOPICAL REVIEW: Review of a chemical approach to YBa2Cu3O7-x-coated superconductors—metalorganic deposition using trifluoroacetates

NASA Astrophysics Data System (ADS)

Araki, Takeshi; Hirabayashi, Izumi

2003-11-01

Large-area, uniform, high critical current density (Jc) YBa2Cu3O7-x (YBCO) superconductor films are now routinely obtained by metalorganic deposition using trifluoroacetates (TFA-MOD). This method does not require any expensive vacuum apparatus at any time during the whole process. Thus, TFA-MOD is regarded as one of the most suitable candidates for fabricating a YBCO tape for many high-power applications. This method originated from an electron beam process using BaF2 developed by Mankiewich et al. Afterwards, Gupta et al reported using TFA-MOD to prepare a similar precursor film. These two ex situ processes used fluorides instead of BaCO3 to avoid the fatal deterioration in Jc, which is caused in the resulting films through metal carboxylic groups. Fluorides not only avoid such deterioration but also lead to perfectly c-axis-oriented epitaxial crystal growth. In conventional metalorganic deposition, nucleation in the precursor film causes random orientation in the resulting film. However, in TFA-MOD, nanocrystallites in the precursor film never cause such disorder. Furthermore, during the firing process of TFA-MOD, water and HF gas diffuse quickly between the film surface and growth front of the YBCO layer. This diffusion never limits the growth rate of YBCO. What distinguishes TFA-MOD from conventional metalorganic deposition? What happens during heat treatment? In this paper, we discuss all the TFA-MOD processes and the peculiar growth scheme of the YBCO layer in TFA-MOD using the model of a quasi-liquid network. In addition, we review the history of TFA-MOD and recent results and discuss the prospects of future applications.

Investigation of Pb doping on electrical, structural and superconducting properties of YBa2-xPbxCu3O7-δ superconductors

NASA Astrophysics Data System (ADS)

Ezzatpour, S.; Sharifzadegan, L.; Sarvari, F.; Sedghi, H.

2018-06-01

In this study the high temperature superconductor YBa2-xPbxCu3O7-δ with doping x = ,0.05,0.1,0.15 were prepared by the standard solid-state reaction method. The effect of Pb substitution on Ba site of YBCO superconducting system, structural, electrical and superconducting properties of Y-based superconductor has been investigated. The measurements of dc resisitivity were performed on all samples with four-probe method using low frequency/lowAC current (4 mA) . The superconducting temperature, Tc, were determined from the resistivity versus temperature (R-T) curves. Results show that Pb doping reduced the cirtical temperature(Tc) and superconductivity properties of our samples. The maximum and the minimum Tc were observed for the samples with x = 0.15 and x = 0.1 respectively. The structure and phase purity of samples were examined by the X-ray powder diffraction technique (XRD) performed by means of D8 Advance Bruker diffractometer with Cu kα radiation. The grain morphology of surface of the samples was analyzed by sacanning electron microscopy (SEM). XRD patterns of polycrystalline materials of composition YBa2-xPbxCu3O7-δ revealed that all prepared samples are orthorhombic. All of the peaks of YBCO and YBa2-xPbxCu3O7-δ have been used for the estimation of volume fractions of the phases and ignored the void peaks.

Heteroepitaxial Cu2O thin film solar cell on metallic substrates

PubMed Central

Wee, Sung Hun; Huang, Po-Shun; Lee, Jung-Kun; Goyal, Amit

2015-01-01

Heteroepitaxial, single-crystal-like Cu2O films on inexpensive, flexible, metallic substrates can potentially be used as absorber layers for fabrication of low-cost, high-performance, non-toxic, earth-abundant solar cells. Here, we report epitaxial growth of Cu2O films on low cost, flexible, textured metallic substrates. Cu2O films were deposited on the metallic templates via pulsed laser deposition under various processing conditions to study the influence of processing parameters on the structural and electronic properties of the films. It is found that pure, epitaxial Cu2O phase without any trace of CuO phase is only formed in a limited deposition window of P(O2) - temperature. The (00l) single-oriented, highly textured, Cu2O films deposited under optimum P(O2) - temperature conditions exhibit excellent electronic properties with carrier mobility in the range of 40–60 cm2 V−1 s−1 and carrier concentration over 1016 cm−3. The power conversion efficiency of 1.65% is demonstrated from a proof-of-concept Cu2O solar cell based on epitaxial Cu2O film prepared on the textured metal substrate. PMID:26541499

Heteroepitaxial Cu 2O thin film solar cell on metallic substrates

DOE PAGES

Wee, Sung Hun; Huang, Po-Shun; Lee, Jung-Kun; ...

2015-11-06

Heteroepitaxial, single-crystal-like Cu 2O films on inexpensive, flexible, metallic substrates can potentially be used as absorber layers for fabrication of low-cost, high-performance, non-toxic, earth-abundant solar cells. Here, we report epitaxial growth of Cu 2O films on low cost, flexible, textured metallic substrates. Cu 2O films were deposited on the metallic templates via pulsed laser deposition under various processing conditions to study the influence of processing parameters on the structural and electronic properties of the films. It is found that pure, epitaxial Cu 2O phase without any trace of CuO phase is only formed in a limited deposition window of P(Omore » 2) - temperature. The (00l) single-oriented, highly textured, Cu 2O films deposited under optimum P(O 2) - temperature conditions exhibit excellent electronic properties with carrier mobility in the range of 40-60 cm 2 V -1 s -1 and carrier concentration over 10 16 cm -3. The power conversion efficiency of 1.65% is demonstrated from a proof-of-concept Cu 2O solar cell based on epitaxial Cu 2O film prepared on the textured metal substrate.« less

Evidence for three-dimensional XY critical properties in underdoped YBa2Cu3O7-δ

NASA Astrophysics Data System (ADS)

Schneider, T.

2007-05-01

We perform a detailed analysis of the reversible magnetization data of Salem-Sugui and Babíc of underdoped and optimally doped YBa2Cu3O7-δ single crystals. Near the zero field transition temperature we observe extended consistency with the properties of the three-dimensional XY universality class, even though the attained critical regime is limited by an inhomogeneity induced finite size effect. Nevertheless, as Tc falls from 93.5to41.5K , the critical amplitude of the in-plane correlation length ξab0 , the anisotropy γ=ξab0/ξc0 and the critical amplitude of the in-plane penetration depth λab0 increase substantially, while the critical amplitude of the c -axis correlation length ξc0 does not change much. As a consequence, the correlation volume Vcorr- increases and the critical amplitude of the specific heat singularity A- decreases dramatically, while the rise of λab0 reflects the behavior of the zero temperature counterpart. Conversely, although ξab0 and λab0 increase with reduced Tc , the ratio λab0/ξab0- , corresponding to the Ginzburg-Landau parameter κab , decreases substantially and YBa2Cu3O7-δ crosses over from an extreme to a weak type-II superconductor.

Fermi surface ridge at second and third UMKLAPP positron annihilations in YBa 2Cu 3O 7- δ

NASA Astrophysics Data System (ADS)

Adam, Gh.; Adam, S.; Barbiellini, B.; Hoffmann, L.; Manuel, A. A.; Peter, M.; Massida, S.

1993-12-01

Results of statistical noise smoothing of the electron momentum distribution got by two-dimensional angular correlation of the electron-positron annihilation radiation technique on untwinned YBa 2Cu 3O 7- δ single crystals are reported. Two distinct signatures of the sheet of Fermi surface related to the CuO chains (the ridge) are resolved. The first occurs at second Umklapp processes, in agreement with previous evidence. The second one, identified for the first time, occurs at third Umklapp processes. Comparison with FLAPW calculations confirms this result.

Thermodynamic evidence for the Bose glass transition in twinned YBa 2 Cu 3 O 7 - δ crystals

DOE PAGES

Pérez-Morelo, D. J.; Osquiguil, E.; Kolton, A. B.; ...

2015-07-21

We used a micromechanical torsional o scillator to measure the magnetic response of a twinned YBaBa2Cu3O7-δ single crystal disk near the Bose glass transition. We observe an anomaly in the temperature dependence of the magnetization consistent with the appearance of a magnetic shielding perpendicular to the correlated pinning of the twin boundaries. This effect is related to the thermodynamic transition from the vortex liquid phase to a Bose glass state.

Dependence of millimeter wave surface resistance on the deposition parameters of laser ablated YBa2Cu3O(x) thin films

NASA Technical Reports Server (NTRS)

Wosik, J.; Robin, T.; Davis, M.; Wolfe, J. C.; Forster, K.; Deshmukh, S.; Bensaoula, A.; Sega, R.; Economou, D.; Ignatiev, A.

1990-01-01

Measurements of millimeter-wave surface resistance versus temperature have been performed for YBa2Cu3O(x) thin films on 100 line-type SrTiO(3) substrates using a TE(011) cylindrical copper cavity at 80 GHz. The 0.6-micron thick films were grown at several deposition temperatures in the range 690 C to 810 C by means of a pulsed excimer laser ablation technique. A surface resistance minimum (60 milliohm at 77 K) near 770 C is shown to correlate with a minimum in c-axis lattice parameter (11.72 A). The highest value of Tc also occurs near this temperature. The surface resistance of films deposited at 790 C on 110 line-type LaAlO3 subtrates is lower, reaching 8 milliohm at 98 GHz and 80 K, demonstrating the influence of substate material on film quality.

The effect of temperature cycling typical of low earth orbit satellites on thin films of YBa2Cu3O(7-x)

NASA Technical Reports Server (NTRS)

Mogro-Campero, A.; Turner, L. G.; Bogorad, A.; Herschitz, R.

1990-01-01

The refrigeration of superconductors in space poses a challenging problem. The problem could be less severe if superconducting materials would not have to be cooled when not in use. Thin films of the YBa2Cu3O(7-x) (YBCO) superconductor were subjected to thermal cycling, which was carried out to simulate a large number of eclipses of a low earth orbit satellite. Electrical measurements were performed to find the effect of the temperature cycling. Thin films of YBCO were formed by coevaporation of Y, BaF2, and Cu and postannealing in wet oxygen at 850 C for 3.5 h. The substrates used were (100) SrTiO3, polycrystalline alumina, and oxidized silicon; the last two have an evaporated zirconia layer. Processing and microstructure studies of these types of films have been published. THe zero resistance transition temperatures of the samples used in this study were 91, 82, and 86 K, respectively. The samples were characterized by four point probe electrical measurements as a function of temperature. The parameters measured were: the zero resistance transition temperature, the 10 to 90 percent transition width, and the room temperature resistance, normalized to that measured before temperature cycling. The results for two samples are presented. Each sample had a cumulative exposure. Cycling in atmospheric pressure nitrogen was performed at a rate of about 60 cycles per day, whereas in vacuum the rate was only about 10 cycles per day. The results indicate only little or no changes in the parameters measured. Degradation of superconducting thin films of YBCO has been reported due to storage in nitrogen. It is believed that the relatively good performance of films after temperature cycling is related to the fact that BaF2 was used as an evaporation source. The latest result on extended temperature cycling indicates significant degradation. Further tests of extended cycling will be carried out to provide additional data and to clarify this preliminary finding.

Analysis of low-field isotropic vortex glass containing vortex groups in YBa2Cu3O7−x thin films visualized by scanning SQUID microscopy

PubMed Central

Wells, Frederick S.; Pan, Alexey V.; Wang, X. Renshaw; Fedoseev, Sergey A.; Hilgenkamp, Hans

2015-01-01

The glass-like vortex distribution in pulsed laser deposited YBa2Cu3O7 − x thin films is observed by scanning superconducting quantum interference device microscopy and analysed for ordering after cooling in magnetic fields significantly smaller than the Earth's field. Autocorrelation calculations on this distribution show a weak short-range positional order, while Delaunay triangulation shows a near-complete lack of orientational order. The distribution of these vortices is finally characterised as an isotropic vortex glass. Abnormally closely spaced groups of vortices, which are statistically unlikely to occur, are observed above a threshold magnetic field. The origin of these groups is discussed, but will require further investigation. PMID:25728772

Shear at Twin Domain Boundaries in YBa2Cu3O7-x

NASA Astrophysics Data System (ADS)

Caldwell, W. A.; Tamura, N.; Celestre, R. S.; MacDowell, A. A.; Padmore, H. A.; Geballe, T. H.; Koster, G.; Batterman, B. W.; Patel, J. R.

2004-05-01

The microstructure and strain state of twin domains in YBa2Cu3O7-x are discussed based upon synchrotron white-beam x-ray microdiffraction measurements. Intensity variations of the fourfold twin splitting of Laue diffraction peaks are used to determine the twin domain structure. Strain analysis shows that interfaces between neighboring twin domains are strained in shear, whereas the interior of these domains are regions of low strain. These measurements are consistent with the orientation relationships of twin boundaries within and across domains and show that basal plane shear stresses can exceed 100MPa where twin domains meet. Our results support stress field pinning of magnetic flux vortices by twin domain boundaries.

Characteristics of YBa2Cu3O7 high-Tc superconductor with KCl

NASA Astrophysics Data System (ADS)

Yoon, Ki Hyun; Chang, Sung Sik

1990-03-01

The lattice parameters, microstructural change, transition temperature, and electrical properties of the YBa2-xKxCu3O7 high-Tc superconductor in the range from x=0 to x=0.25 have been investigated. The high-Tc orthorhombic phase increases with increasing KCl up to x=0.20, above which it decreases. The lattice parameters decrease with increasing KCl up to x=0.10, and then become nearly uniform. The grain size increases with increasing KCl up to x=0.20 due to its role as sintering agent. The specimens with x=0.2 have transition temperatures of 96 K and high magnetic susceptibility due to the contraction of lattice parameters a and b and the increase of orthorhombic distortion.

A two-dimensional ACAR study of untwinned YBa2Cu3O(7-x)

NASA Astrophysics Data System (ADS)

Smedskjaer, L. C.; Bansil, A.

1991-12-01

We have carried out 2D-ACAR measurements on an untwinned single crystal of YBa2Cu3O(sub 7-x) as a function of temperature, for five temperatures ranging from 30K to 300K. We show that these temperature-dependent 2D-ACAR spectra can be described to a good approximation as a superposition of two temperature independent spectra with temperature-dependent weighting factors. We show further how the data can be used to correct for the 'background' in the experimental spectrum. Such a 'background corrected' spectrum is in remarkable accord with the corresponding band theory predictions, and displays, in particular, clear signatures of the electron ridge Fermi surface.

Optical characterization of sputtered YBaCo 4O 7+ δ thin films

NASA Astrophysics Data System (ADS)

Montoya, J. F.; Izquierdo, J. L.; Causado, J. D.; Bastidas, A.; Nisperuza, D.; Gómez, A.; Arnache, O.; Osorio, J.; Marín, J.; Paucar, C.; Morán, O.

2011-02-01

Thin films of YBaCo 4O 7+ δ were deposited on r (1012)-oriented Al 2O 3 substrates by dc magnetron sputtering. The as-grown films were characterized after their structural, morphological and optical properties. Special attention is devoted to the analysis of the optical response of these films as reports on optical properties of YBaCo 4O 7+ δ, especially in thin film form, are not frequently reported in the literature. Transmittance/absorbance measurements allow for determining two well defined energy gaps at 3.7 and 2.2 eV. In turn, infrared (IR) measurements show infrared transparency in the wave length range 4000-2500 nm with a sharp absorption edge at wave lengths less than 2500 nm. Complementary Raman spectra measurements on the thin films allowed for identifying bands associated with vibrating modes of CoO 4 and YO 6 in tetrahedral and octahedral oxygen coordination, respectively. Additional bands which seemed to stem from Co ions in octahedral oxygen coordination were also clearly identified.

The Formation, Transport Properties and Microstructure of 45 Degrees (001) Tilt Grain Boundaries in Yttrium BARIUM(2) COPPER(3) OXYGEN(7-X) Thin Films

NASA Astrophysics Data System (ADS)

Vuchic, Boris Vukan

1995-01-01

Most high angle grain boundaries in high-T _{c} superconductors exhibit weak link behavior. The Josephson-like properties of these grain boundaries can be used for many device applications such as superconducting quantum interference devices (SQUIDs). The structure-property relationship of different types of 45 ^circ (001) YBa_2 Cu_3O_{7-x} thin film grain boundary junctions are examined to study their weak link nature. A technique, termed sputter-induced epitaxy, is developed to form 45^circ (001) tilt grain boundaries in YBa_2Cu _3O_{7-x} thin films on (100) MgO substrates. A low voltage ion bombardment pre-growth substrate treatment is used to modify the epitaxial orientation relationship between the thin film and the substrate in selected regions. By modifying the orientation of the thin film, grain boundary junctions can be placed in any configuration on the substrate. A variety of pre-growth sputtering conditions in conjunction with atomic force microscopy and Rutherford backscatter spectrometry are used to determine the role of the ions in modifying the substrate surface. Sputter-induced epitaxy is extended to a multilayer MgO/LaAlO_3 substrate, allowing integration of the sputter -induced epitaxy junctions into multilayer structures. The low temperature transport properties of the sputter-induced epitaxy junctions and a set of bi-epitaxial grain boundaries are studied. Individual grain boundaries are isolated and characterized for resistance vs. temperature, current vs. voltage as a function of temperature and magnetic field behavior. Resistive and superconducting grain boundaries are compared. Microstructural analysis is performed using scanning electron microscopy, transmission electron microscopy and high resolution electron microscopy (HREM). Marked differences are observed in the microstructure of resistive and superconducting grain boundaries. HREM studies suggest the importance of the local atomic scale structure of the grain boundary in transport

Strongly suppressed proximity effect and ferromagnetism in topological insulator/ferromagnet/superconductor thin film trilayers of Bi2Se3/SrRuO3/underdoped YBa2Cu3O x : a possible new platform for Majorana nano-electronics

NASA Astrophysics Data System (ADS)

Koren, Gad

2018-07-01

We report properties of a topological insulator–ferromagnet–superconductor trilayers comprised of thin films of 20 nm thick {Bi}}2{Se}}3 on 10 nm SrRuO3 on 30 nm {YBa}}2{Cu}}3{{{O}}}x. As deposited trilayers are underdoped and have a superconductive transition with {{T}}{{c}} onset at 75 K, zero resistance at 65 K, {{T}}Cueri} at 150 K and {{T}}* of about 200 K. Further reannealing under vacuum yields the 60 K phase of {YBa}}2{Cu}}3{{{O}}}x which still has zero resistance below about 40 K. Only when 10 × 100 microbridges were patterned in the trilayer, some of the bridges showed resistive behavior all the way down to low temperatures. Magnetoresistance versus temperature of the superconductive ones showed the typical peak due to flux flow against pinning below {{T}}{{c}}, while the resistive ones showed only the broad leading edge of such a peak. All this indicates clearly weak-link superconductivity in the resistive bridges between superconductive {YBa}}2{Cu}}3{{{O}}}x grains via the topological and ferromagnetic cap layers. Comparing our results to those of a reference trilayer (RTL) with the topological {Bi}}2{Se}}3 layer substituted by a non-superconducting highly overdoped {La}}1.65{Sr}}0.35{CuO}}4, indicates that the superconductive proximity effect as well as ferromagnetism in the topological trilayer are actually strongly suppressed compared to the non-topological RTL. This strong suppression could originate in lattice and Fermi levels mismatch as well as in short coherence length and unfavorable effects of strong spin–orbit coupling in {Bi}}2{Se}}3 on the d-wave pairing of {YBa}}2{Cu}}3{{{O}}}x. Proximity induced edge currents in the SRO/YBCO layer could lead to Majorana bound states, a possible signature of which is observed in the present study as zero bias conductance peaks.

Electronic state and superconductivity of YBa2Cu3-xO7-y (M=Al,Zn and Sn) systems

NASA Technical Reports Server (NTRS)

Zhao, Y.; Zhang, Q. R.; Zhang, H.

1990-01-01

A series of YBa2Cu(3-x)MxO(7-y) (M=Al,Zn and Sn) single phase samples were prepared, and the measurements of the crystal structure, oxygen content, electric resistivity, thermoelectric power, Mossbauer spectrum, XPS and superconductivity were performed. The experimental results of X ray powder diffraction, Mossbauer spectrum and oxygen content show that the Zn(2+) and the Al(3+) occupy the Cu(2) site in Cu-O planes and the Cu(1) site in Cu-O chains respectively, but the Sn(4+) occupies both the Cu(1) sites. As regards the properties in superconducting state, both the Zn(2+) and the Al(3+) depress T(sub c) strongly, but the Sn(4+) does not. As for the electronic transport properties in normal state, the system doped by Al(3+) displays a rapid increase of resistivity and some electron localization-like effects, and the thermoelectric power enhances obviously; the series contained Zn(2+) almost shows no changes of electric resistivity but the sign of the thermoelectric power is reversed. Other results are given and briefly discussed.

Electronic Structure of Tl2Ba2CuO(6+Delta) Epitaxial Films Measured by X-Ray Photoemission

NASA Technical Reports Server (NTRS)

Vasquez, R. P.; Ren, Z. F.; Wang, J. H.

1996-01-01

The valence electronic structure and core levels of Tl2Ba2CuO(6 + delta) (Tl-2201) epitaxial films have been measured with X-ray photoelectron spectroscopy and are compared to those of Tl2Ba2CaCu2O(8 + delta) (Tl-2212). Changes in the Tl-2201 core-level binding energies with oxygen doping are consistent with a change in the chemical potential. Differences between the Tl-2201 and Tl-2212 measured densities of states are consistent with the calculated Cu 3d and Tl 6s partial densities of states.

Detection and imaging of the oxygen deficiency in single crystalline YBa{sub 2}Cu{sub 3}O{sub 7−δ} thin films using a scanning positron beam

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reiner, M.; Gigl, T.; Hugenschmidt, C.

2015-03-16

Single crystalline YBa{sub 2}Cu{sub 3}O{sub 7−δ} (YBCO) thin films were grown by pulsed laser deposition in order to probe the oxygen deficiency δ using a mono-energetic positron beam. The sample set covered a large range of δ (0.191 < δ < 0.791) yielding a variation of the critical temperature T{sub c} between 25 and 90 K. We found a linear correlation between the Doppler broadening of the positron electron annihilation line and δ determined by X-ray diffraction. Ab-initio calculations have been performed in order to exclude the presence of Y vacancies and to ensure the negligible influence of potentially present Ba or Cu vacancies tomore » the found correlation. Moreover, scanning with the positron beam allowed us to analyze the spatial variation of δ, which was found to fluctuate with a standard deviation of up to 0.079(5) within a single YBCO film.« less

Influence of calcium on transport properties, band spectrum and superconductivity of YBa2Cu3O(y) and YBa(1.5)La(0.5)Cu3O(y)

NASA Technical Reports Server (NTRS)

Gasumyants, V. E.; Vladimirskaya, E. V.; Patrina, I. B.

1995-01-01

The comparative investigation of transport phenomena in Y(1-x)Ca(x)Ba2Cu3O(y) (0 is less than x is less than 0.25; 6.96 is greater than y is greater than 6.87 and 6.73 is less than x is less than 6.53); Y(1-x)Ca(x)Ba(1.5)La(0.5)Cu3O(y) (0 is less than x is less than 0.5; 7.12 is greater than y is greater than 6.96) and YBa(2-x)La(x)Cu3O(y) (0 is less than x is less than 0.5; 6.95 is less than y is less than 7.21) systems have been carried out. The temperature dependencies of resistivity and thermopower have been measured. It was found that the S(T) dependencies take some additional features with Ca content increase. The results obtained have been analyzed on the basis of the phenomenological theory of electron transport in the case of the narrow conductive band. The main parameters of the band spectrum (the band filling with electrons degree and the total effective band width) have been determined. The dependencies of these from contents of substituting elements are discussed. Analyzing the results obtained simultaneously with the tendencies in oxygen content and critical temperature change we have confirmed the conclusion that the oxygen sublattice disordering has a determinant effect on band structure parameters and superconductive properties of YBa2Cu3O(y). The results obtained suggest that Ca gives rise to some peculiarities in band spectrum of this compound.

Pulsed laser deposition of {CeO_2} and {Ce_{1-x}M_xO_2} (M = La, Zr): Application to insulating barrier in cuprate heterostructures

NASA Astrophysics Data System (ADS)

Berger, S.; Contour, J.-P.; Drouet, M.; Durand, O.; Khodan, A.; Michel, D.; Régi, F.-X.

1998-03-01

SrTiO_3 had been often tentatively used as an insulating barrier for HT superconductor/insulator heterostructures. Unfortunately, the deposition of SrTiO_3 on the YBa_2Cu_3O_7 inverse interface results in a poor epitaxial regrowth producing a high roughness dislocated titanate layer. Taking into account the good matching with YBa_2Cu_3O_7 and LaAlO_3, CeO_2 and Ce_{1-x}M_xO_2 (M = La, Zr), epitaxial layers were grown by pulsed laser deposition on LaAlO_3 substrates and introduced into YBa_2Cu_3O_7 based heterostructures as insulating barrier. After adjusting the growth parameters from RHEED oscillations, epitaxial growth is achieved, the oxide crystal axes being rotated by 45^circ from those of the substrate. The surface roughness of 250 nm thick films is very low with a rms value lower than 0.5 nm over 1;μ m^2. The YBa_2Cu_3O_7 layers of a YBa_2Cu_3O_7/CeO_2 /YBa_2Cu_3O_7 heterostructures grown using these optimized parameters show an independent resistive transition, when the thickness is larger than 25 nm, respectively at T_c_1 = 89.6;K and T_c_2 = 91.4;{K}. SrTiO3 est souvent utilisé comme barrière isolante dans des hétérostructures SIS de cuprates supraconducteurs, cependant les défauts générés lors de la croissance de ce titanate sur l'interface inverse de YBa2Cu3O7 conduisent à un matériau dont la qualité cristalline et les propriétés physiques sont médiocres. L'oxyde de cérium CeO2 est également une barrière isolante potentielle intéressante pour ces structures SIS basées sur YBa2Cu3O7 car cet oxyde cubique (a = 0,5411 nm, asqrt{2}/2 = 0,3825 nm) qui est peu désaccordé par rapport au plan ab du cuprate (Δ a/a = - 0,18 %, Δ b/a = 1,6 %) présente de plus un coefficient de dilatation thermique (10,6 × 10^{-6 circ}C^{-1}) très voisin de celui de YBa2Cu3O7 (13 × 10^{-6 circ}C^{-1}). Nous avons donc étudié l'épitaxie de CeO2 et des oxydes de type Ce{1-x}MxO2 (M = La, Zr) en ablation laser pulsée afin de définir des conditions de

Method of producing superconducting fibers of YBa[sub 2]Cu[sub 3]O[sub x

DOEpatents

Schwartzkopf, L.A.; Ostenson, J.E.; Finnemore, D.K.

1990-11-13

Fibers of YBa[sub 2]Cu[sub 3]O[sub x] have been produce by pendant drop melt extraction. This technique involves the end of a rod of YBa[sub 2]Cu[sub 3]O[sub x] melted with a hydrogen-oxygen torch, followed by lowering onto the edge of a spinning wheel. The fibers are up to 10 cm in length with the usual lateral dimensions, ranging from 20 [mu]m to 125 [mu]m. The fibers require a heat treatment to make them superconducting.

Modification of structural disorder by hydrostatic pressure in the superconducting cuprate YBa2Cu3O6.73

NASA Astrophysics Data System (ADS)

Huang, H.; Jang, H.; Fujita, M.; Nishizaki, T.; Lin, Y.; Wang, J.; Ying, J.; Smith, J. S.; Kenney-Benson, C.; Shen, G.; Mao, W. L.; Kao, C.-C.; Liu, Y.-J.; Lee, J.-S.

2018-05-01

Compelling efforts to improve the critical temperature (Tc) of superconductors have been made through high-pressure application. Understanding the underlying mechanism behind such improvements is critically important; however, much remains unclear. Here we studied ortho-III YBa2Cu3O6.73 (YBCO) using x-ray scattering under hydrostatic pressure (HP) up to ˜6.0 GPa . We found the reinforced oxygen order of YBCO under HP, revealing an oxygen rearrangement in the Cu-O layer, which evidently shows the charge-transfer phenomenon between the Cu O2 plane and Cu-O layer. Concurrently, we also observed no disorder-pinned charge-density-wave signature in Cu O2 plane under HP. This indicates that the oxygen rearrangement modifies the quenched disorder state in the Cu O2 plane. Using these results, we appropriately explain why pressure condition can achieve higher Tc compared with the optimal Tc under ambient pressure in YBa2Cu3O6 +x . As an implication of these results, finally we have discussed that the change in disorder could make it easier for YBa2Cu3O6 +x to undergo a transition to the nematic order under an external magnetic field.

Depletion-mode vertical Ga2O3 trench MOSFETs fabricated using Ga2O3 homoepitaxial films grown by halide vapor phase epitaxy

NASA Astrophysics Data System (ADS)

Sasaki, Kohei; Thieu, Quang Tu; Wakimoto, Daiki; Koishikawa, Yuki; Kuramata, Akito; Yamakoshi, Shigenobu

2017-12-01

We developed depletion-mode vertical Ga2O3 trench metal-oxide-semiconductor field-effect transistors by using n+ contact and n- drift layers. These epilayers were grown on an n+ (001) Ga2O3 single-crystal substrate by halide vapor phase epitaxy. Cu and HfO2 were used for the gate metal and dielectric film, respectively. The mesa width and gate length were approximately 2 and 1 µm, respectively. The devices showed good DC characteristics, with a specific on-resistance of 3.7 mΩ cm2 and clear current modulation. An on-off ratio of approximately 103 was obtained.

Influence of planar macrodefects on the anisotropy of magnetic-flux penetration in YBa 2Cu 3O 7-δ

NASA Astrophysics Data System (ADS)

Cuche, E.; Indenbom, M. V.; André, M.-O.; Richard, P.; Benoit, W.; Wolf, Th.

1996-02-01

The magnetic flux penetration in a high-quality YBa 2Cu 3O 7-δ single crystal with an external field applied perpendicular to the crystalline c axis is directly visualized by means of the magneto-optical technique. The observations show that the field penetrates preferentially along the ab planes. Scanning acoustic microscopy reveals macrodefects along ab planes which strongly affect this anisotropy of the field penetration.

Valence charge fluctuations in YBa/sub 2/Cu/sub 3/O/sub 7-//sub delta/ from core-level spectroscopies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Balzarotti, A.; De Crescenzi, M.; Motta, N.

1988-10-01

From x-ray photoemission and Auger measurements of the Cu 2p and O 1s core levels of YBa/sub 2/Cu/sub 3/O/sub 7-//sub delta/ as a function of the oxygen concentration delta, the average copper charge is determined. Evidence is found of dynamic charge fluctuations on the oxygen sublattice giving rise to a greater concentration of trivalent copper at the Cu(1) sites with respect to that determined by the analysis of neutron-diffraction data. On the basis of our experimental results, we introduce a molecular cluster description for the Cu states. The lowest final-states configurations of Cu/sup 2+/ and Cu/sup 3+/ are c3d/sup 10/Lmore » and c3d/sup 10/L/sup 2/, respectively, where c and L denote core holes on copper and oxygen atoms. Oxygen holes have high mobility and a Hubbard correlation energy less than 2 eV, a signature of their delocalization. The effect of temperature on the spectra is minor. Surface degradation modifies the relative intensity of the structures, particularly those of the O spectrum.« less

Phase compatibilities of YBa2Cu3O(9-delta) type structure in quintenary systems Y-Ba-Cu-O-X (impurity)

NASA Technical Reports Server (NTRS)

Karen, P.; Fjellvag, H.; Kjekshus, A.

1990-01-01

Electrical transport properties of the oxidic high T(sub c) superconductors are significantly affected by the presence of minor amounts of various elements adventing as impurities, e.g., from the chemical environment during manufacturing. YBa2Cu3O(9-delta) is prone to an extinction of the superconductivity on (partial) substitution of all four elemental components. E.g., Pr (for Y), La (for Ba), Zn (for Cu) or peroxygroup (for O) substituents will alter some of the superconductivity preconditions, like mixed valence state in Cu3O7/O(9-delta) network or structural distortion of the network. Although various pseudoternary chemical equilibrium phase diagrams of the Y(O)-Ba(O)-Cu(O) system now are available, no consensus is generally shown, however, this is partly due to lack of compatible definitions of the equilibrium conditions. Less information is available about the phase compatibilities in the appropriate quaternary phase diagram (including oxygen) and virtually no information exists about any pentenary phase diagrams (including one impurity). Unfortunately, complexity of such systems, stemming both from number of quaternary or pentenary compounds and from visualizing the five-component phase system, limits this presentation to more or less close surroundings of the YBa2Cu3O(9-delta) type phase in appropriate pseudoquaternary or pseudopseudoternary diagrams, involving Y-Ba-Cu and O, O-CO2, alkaline metals, Mg and alkaline earths, and Sc and most of the 3-d and 4-f elements. The systems were investigated by means of x ray diffraction, neutron diffraction and chemical analytical methods on samples prepared by sol-gel technique from citrates. The superconductivity was characterized by measuring the diamagnetic susceptibility by SQUID.

Defects and anharmonicity induced electron spectra of YBa2Cu3O7-δ superconductors

NASA Astrophysics Data System (ADS)

Singh, Anu; Indu, B. D.

2018-05-01

The effects of defects and anharmonicities on the electron density of states (EDOS) have been studied in high-temperature superconductors (HTS) adopting the many body quantum dynamical theory of electron Green's functions via a generalized Hamiltonian that includes the effects of electron-phonon interactions, anharmonicities and point impurities. The automatic emergence of pairons and temperature dependence of EDOS are appear as special feature of the theory. The results thus obtained and their numerical analysis for YBa2Cu3O7-δ superconductors clearly demonstrate that the presence of defects, anharmonicities and electron-phonon interactions modifies the behavior of EDOS over a wide range of temperature.

Epitaxial cuprate superconductor/ferroelectric heterostructures.

PubMed

Ramesh, R; Inam, A; Chan, W K; Wilkens, B; Myers, K; Remschnig, K; Hart, D L; Tarascon, J M

1991-05-17

Thin-film heterostructures of Bi(4)Ti(3)O(12)Bi(2)Sr(2)CuO(6+x), have been grown on single crystals of SrTiO(3), LaAlO(3), and MgAl(2)O(4) by pulsed laser deposition. X-ray diffraction studies show the presence of c-axis orientation only; Rutherford backscattering experiments show the composition to be close to the nominal stoichiometry. The films are ferroelectric and exhibit a symmetric hysteresis loop. The remanent polarization was 1.0 microcoulomb per square centimeter, and the coercive field was 2.0 x 10(5) volts per centimeter. Similar results were obtained with YBa(2)Cu(3)O(7-x) and Bi(2)Sr(2)CaCu(2)O(8+x), and single-crystal Bi(2)Sr(2)CuO(6+x)as the bottom electrodes. These films look promising for use as novel, lattice-matched, epitaxial ferroelectric film/electrode heterostructures in nonvolatile memory applications.

Modification of structural disorder by hydrostatic pressure in the superconducting cuprate YBa 2 Cu 3 O 6.73

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, H.; Jang, H.; Fujita, M.

Here, compelling efforts to improve the critical temperature (T c) of superconductors have been made through high-pressure application. Understanding the underlying mechanism behind such improvements is critically important; however, much remains unclear. Here we studied ortho-III YBa 2Cu 3O 6.73 (YBCO) using x-ray scattering under hydrostatic pressure (HP) up to ~6.0GPa. We found the reinforced oxygen order of YBCO under HP, revealing an oxygen rearrangement in the Cu-O layer, which evidently shows the charge-transfer phenomenon between the CuO 2 plane and Cu-O layer. Concurrently, we also observed no disorder-pinned charge-density-wave signature in CuO 2 plane under HP. This indicates thatmore » the oxygen rearrangement modifies the quenched disorder state in the CuO 2 plane. Using these results, we appropriately explain why pressure condition can achieve higher T c compared with the optimal T c under ambient pressure in YBa 2Cu 3O 6+x. As an implication of these results, finally we have discussed that the change in disorder could make it easier for YBa 2Cu 3O 6+x to undergo a transition to the nematic order under an external magnetic field.« less

Modification of structural disorder by hydrostatic pressure in the superconducting cuprate YBa 2 Cu 3 O 6.73

DOE PAGES

Huang, H.; Jang, H.; Fujita, M.; ...

2018-05-09

Here, compelling efforts to improve the critical temperature (T c) of superconductors have been made through high-pressure application. Understanding the underlying mechanism behind such improvements is critically important; however, much remains unclear. Here we studied ortho-III YBa 2Cu 3O 6.73 (YBCO) using x-ray scattering under hydrostatic pressure (HP) up to ~6.0GPa. We found the reinforced oxygen order of YBCO under HP, revealing an oxygen rearrangement in the Cu-O layer, which evidently shows the charge-transfer phenomenon between the CuO 2 plane and Cu-O layer. Concurrently, we also observed no disorder-pinned charge-density-wave signature in CuO 2 plane under HP. This indicates thatmore » the oxygen rearrangement modifies the quenched disorder state in the CuO 2 plane. Using these results, we appropriately explain why pressure condition can achieve higher T c compared with the optimal T c under ambient pressure in YBa 2Cu 3O 6+x. As an implication of these results, finally we have discussed that the change in disorder could make it easier for YBa 2Cu 3O 6+x to undergo a transition to the nematic order under an external magnetic field.« less

Effects of oxygen stoichiometry on the scaling behaviors of YBa2Cu3O(x) grain boundary weak-links

NASA Technical Reports Server (NTRS)

Wu, K. H.; Fu, C. M.; Jeng, W. J.; Juang, J. Y.; Uen, T. M.; Gou, Y. S.

1995-01-01

The effects of oxygen stoichiometry on the transport properties of the pulsed laser deposited YBa2Cu3O(x) bicrystalline grain boundary weak-link junctions were studied. It is found that not only the cross boundary resistive transition foot structure can be manipulated repeatedly with oxygen annealing processes but the junction behaviors are also altered in accordance. In the fully oxygenated state i.e with x = 7.0 in YBa2Cu3O(x) stoichiometry, the junction critical current exhibits a power of 2 scaling behavior with temperature. In contrast, when annealed in the conditions of oxygen-deficient state (e.g with x = 6.9 in YBa2Cu3O(x) stoichiometry) the junction critical current switches to a linear temperature dependence behavior. The results are tentatively attributed to the modification of the structure in the boundary area upon oxygen annealing, which, in turn, will affect the effective dimension of the geometrically constrained weak-link bridges. The detailed discussion on the responsible physical mechanisms as well as the implications of the present results on device applications will be given.

Q factor of megahertz LC circuits based on thin films of YBaCuO high-temperature superconductor

NASA Astrophysics Data System (ADS)

Masterov, D. V.; Pavlov, S. A.; Parafin, A. E.

2008-05-01

High-frequency properties of resonant structures based on thin films of YBa2Cu3O7 δ high-temperature superconductor are studied experimentally in the frequency range 30 100 MHz. The structures planar induction coils with a self-capacitance fabricated on neodymium gallate and lanthanum aluminate substrates. The unloaded Q factor of the circuits exceeds 2 × 105 at 77 K and 40 MHz. Possible loss mechanisms that determine the Q factor of the superconducting resonant structures in the megahertz range are considered.

Micro-Raman study of isotope substitution in YBa2Cu183O6.2 during local laser annealing

NASA Astrophysics Data System (ADS)

Ivanov, V. G.; Iliev, M. N.; Thomsen, C.

1995-11-01

The local laser heating of YBa2Cu183O6.2 in air was used to study the oxygen diffusion and oxygen ordering in sample volumes of the order of a few μm3. Raman microprobe at points corresponding to different annealing temperatures was applied to monitor both the stages of substitution of 16O for 18O at different oxygen sites and the structural changes in the basal [Cu(1)-O(1)] planes occurring during the oxygen in-diffusion. The population of the O(1) sites initially results in the formation of short Cu(1)-O(1) fragments which later conjunct into long chains. The results can be applied for a better understanding of oxygen reordering processes in YBa2Cu3O7-δ during thermal treatment.

Electronic and optical properties of La-doped S r3I r2O7 epitaxial thin films

NASA Astrophysics Data System (ADS)

Souri, M.; Terzic, J.; Johnson, J. M.; Connell, J. G.; Gruenewald, J. H.; Thompson, J.; Brill, J. W.; Hwang, J.; Cao, G.; Seo, A.

2018-02-01

We have investigated structural, transport, and optical properties of tensile strained (Sr1-xL ax ) 3I r2O7 (x =0 , 0.025, 0.05) epitaxial thin films. While high-Tc superconductivity is predicted theoretically in the system, we have observed that all of the samples remain insulating with finite optical gap energies and Mott variable-range hopping characteristics in transport. Cross-sectional scanning transmission electron microscopy indicates that structural defects such as stacking faults appear in this system. The insulating behavior of the La-doped S r3I r2O7 thin films is presumably due to disorder-induced localization and ineffective electron doping of La, which brings to light the intriguing difference between epitaxial thin films and bulk single crystals of the iridates.

Broadening of resistive transition and irreversibility line for epitaxial YBa2Cu3O7-δ thin film

NASA Astrophysics Data System (ADS)

Xiao-jun, Xu; Ke-bin, Li; Jun, Fang; Zhi-he, Wang; Xiao-wen, Cao

1996-04-01

The broadening of resistive transition of c axis oriented epitaxial YBCO thin film has been measured for three configurations: (1) Hparc and H ⊥ I; (2) Hparab plane and H ⊥ I; (3) Hparab plane and HparI in magnetic field up to 8 Tesla(T), and for different angle θ of magnetic field relative to the ab plane with H = 4T. The results obtained indicate that the broadening of resistive transition is mainly determined by the angle θ, but is hardly related to the angle α made between magnetic field and tran sport current in ab plane. This means that the broadening of resistive transition is not determined by flux motion drived by apparent Lorentz force. An expression of angular dependence of irreversibility line has been given.

Correlation between superfluid density and T(C) of underdoped YBa2Cu3O6+x near the superconductor-insulator transition.

PubMed

Zuev, Yuri; Kim, Mun Seog; Lemberger, Thomas R

2005-09-23

We report measurements of the ab-plane superfluid density n(s) (magnetic penetration depth lambda) of heavily underdoped films of YBa2Cu3O6+x, with T(C)'s from 6 to 50 K. We find the characteristic length for vortex unbinding transition equal to the film thickness, suggesting strongly coupled CuO2 layers. At the lowest dopings, T(C) is as much as 5 times larger than the upper limit set by the 2D Kosterlitz-Thouless-Berezinskii transition temperature calculated for individual CuO2 bilayers. Our main finding is that T(C) is not proportional to n(s)(0); instead, we find T(C) proportional to ns(1/2.3+/-0.4). This conflicts with a popular point of view that quasi-2D thermal phase fluctuations determine the transition temperature.

YBa2Cu307 superconducting microbolometer linear arrays

NASA Astrophysics Data System (ADS)

Johnson, Burgess R.; Ohnstein, Thomas R.; Marsh, Holly A.; Dunham, Scott B.; Kruse, Paul W.

1992-09-01

Single pixels and linear arrays of microbolometers employing the high-T(subscript c) superconductor YBa(subscript 2)Cu(subscript 3)O(subscript 7) have been fabricated by silicon micromachining techniques. The substrates are 3 in. diameter silicon wafers upon which buffer layers of Si(subscript 3)N(subscript 4) and yttria-stabilized zirconia (YSZ) have been deposited. The YBa(subscript 2)Cu(subscript 3)O(subscript 7) was deposited by ion beam sputtering upon the yttria-stabilized zirconia (YSZ), then photolithographically patterned into serpentines 4 micrometers wide. Anisotropic etching in KOH removed the silicon underlying each pixel, thereby providing the necessary thermal isolation. When operated at 70 degree(s)K with 1 (mu) A dc bias, the D(superscript *) is 7.5 X 10(superscript 8) cm Hz(superscript 1/2)/Watt with a thermal response time of 24 msec.

Tuning piezoelectric properties through epitaxy of La2Ti2O7 and related thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kaspar, Tiffany C.; Hong, Seungbum; Bowden, Mark E.

2018-02-14

Current piezoelectric sensors and actuators are limited to operating temperatures less than ~200°C due to the low Curie temperature of the piezoelectric material. High temperature piezoelectric materials such as La2Ti2O7 (LTO) would facilitate the development of high-temperature sensors if the piezoelectric coupling coefficient could be maximized. We have deposited epitaxial LTO films on SrTiO3(001), SrTiO3(110), and rutile TiO2(110) substrates by pulsed laser deposition, and show that the crystalline orientation of the LTO film, and thus its piezoelectric coupling direction, can be controlled by epitaxial matching to the substrate. The structure and phase purity of the films were investigated by x-raymore » diffraction and scanning transmission electron microscopy. To characterize the piezoelectric properties, piezoresponse force microscopy was used to measure the in-plane and out-of-plane piezoelectric coupling in the films. We find that the strength of the out-of-plane piezoelectric coupling can be increased when the piezoelectric crystalline direction is rotated partially out-of-plane via epitaxy. The strongest out-of-plane coupling is observed for LTO/STO(001). Deposition on TiO2(110) results in epitaxial La2/3TiO3, an orthorhombic perovskite of interest as a microwave dielectric material. La2/3TiO3 can be difficult to stabilize in bulk form, and epitaxial deposition has not been previously reported. These results confirm that control of the crystalline orientation of LTO-based materials can increase the out-of-plane strength of its piezoelectric coupling, which can be exploited in piezoelectric devices.« less

Lower critical field measurements in YBa2Cu3O(6+x) single crystals

NASA Technical Reports Server (NTRS)

Kaiser, D. L.; Swartzendruber, L. J.; Gayle, F. W.; Bennett, L. H.

1991-01-01

The temperature dependence of the lower critical field in YBa2Cu3O(6+x) single crystals was determined by magnetization measurements with the applied field parallel and perpendicular to the c-axis. Results are compared with data from the literature and fitted to Ginzberg-Landau equations by assuming a linear dependence of the parameter kappa on temperature. A value of 7 plus or minus 2 kOe was estimated for the thermodynamic critical field at T = O by comparison of calculated H (sub c2) values with experimental data from the literature.

Evaluation of Characteristic Energy Scales of Pressure Stabilized Oxygen Chain States in YBa2Cu3Ox Films

DTIC Science & Technology

2017-03-14

2], and [4]. In the case of YBa2Cu3O∇x, the application of sufficient uniaxial pressure results in the film having discrete regions of uniform...that discrete regions of uniform oxygen content are stabilized where x ≈ [6, 6.5, 6.72, 6.81, 7]. The latter four oxygen content levels correspond to...associated energy levels of the stabilized lattice states ᝺>, �>, >, and ə>, and find evidence for discrete energy levels of the pressure

Compatibilities of YBa2Cu3O(9-delta) type phase in quintenary systems Y-Ba-Cu-O-X (impurity)

NASA Technical Reports Server (NTRS)

Karen, P.; Braaten, O.; Fjellvag, H.; Kjekshus, A.

1991-01-01

Isothermal phase diagrams at various oxygen pressures were studied by powder diffraction and chemical analytical methods. The components, Y, Ba, Cu, and O (specifically O2, O2-, and O2 sup 2-) are treated, together with C (specifically CO2 and CO2 sup 2-), alkaline metals, Mg, alkaline earths, Sc, 3-d and 4-f elements. Effects of the substitutions at the structural sites of YBa2Cu3O(9-delta) on T sub c are discussed with respect to changes in crystallochemical characteristics of the substituted phase and to the nature of the substituents.

Positron annihilation study of Y 1- xPr xBa 2Cu 3O 7

NASA Astrophysics Data System (ADS)

Zhao, Y. G.; Cao, B. S.; Yu, W. Z.; Du, Z. H.; Wang, Y. J.; Luo, C. Y.; Hu, H.; Wang, S.; Yang, J. H.; He, A. S.; Gu, B. L.

1995-02-01

A positron annihilation study of Y 1- xPr xBa 2Cu 3O 7 was performed. The results showed that charge transfer between the CuO 2 planes and 1D CuO chains upon Pr doping, as proposed in the literature, did not occur. Pr doping suppressed the anomaly of positron annihilation lifetime near and below Tc which has been observed in YBa 2Cu 3O 7. The perfection of the 1D CuO chains was reduced by Pr doping and this may be partly responsible for the increase of resistivity with Pr doping, and finally the semiconducting behaviour of DC resistivity in Y 1- xPr xBa 2Cu 3O 7 with x > 0.6.

Study of photoirradiation for YBa 2Cu 3O 6+ x compounds and the electron structure by positron experiment

NASA Astrophysics Data System (ADS)

Guosheng, Cheng; Jiaxiang, Shang; Xigui, Li; xianqi, Dai; Xizhong, Wang; Jincang, Zhang

1997-08-01

We present positron lifetime data of YBa 2Cu 3O 6+ x (x=0.92, 0.43) compounds for different photo-irradiation time. It is given that change of the local electron density and vacancy concentration with photoirradiation time. It is found that there is transform at the electronic structure of CuO chains. We also have discussed the effect of photoirradiations time on the electronic structure of YBa 2Cu 3O 6+ x systems and their charge reservoir layer and CuO 2 plane conduction.layer. The positron experimental results support the model of photoinduced oxygen-diffusion mechanism.

Epitaxial growth and dielectric properties of Pb0.4Sr0.6TiO3 thin films on (00l)-oriented metallic Li0.3Ni0.7O2 coated MgO substrates

NASA Astrophysics Data System (ADS)

Li, X. T.; Du, P. Y.; Mak, C. L.; Wong, K. H.

2007-06-01

Highly (00l)-oriented Li0.3Ni0.7O2 thin films have been fabricated on (001) MgO substrates by pulsed laser deposition. The Pb0.4Sr0.6TiO3 (PST40) thin film deposited subsequently also shows a significant (00l)-oriented texture. Both the PST40 and Li0.3Ni0.7O2 have good epitaxial behavior. The epitaxial growth of the PST40 thin film is more perfect with the Li0.3Ni0.7O2 buffer layer due to the less distortion in the film. The dielectric tunability of the PST40 thin film with Li0.3Ni0.7O2 buffer layer therefore reaches 70%, which is 75% higher than that without Li0.3Ni0.7O2 buffer layer, and the dielectric loss of the PST40 thin film is 0.06.

Epitaxial thin films of Dirac semimetal antiperovskite Cu3PdN

NASA Astrophysics Data System (ADS)

Quintela, C. X.; Campbell, N.; Shao, D. F.; Irwin, J.; Harris, D. T.; Xie, L.; Anderson, T. J.; Reiser, N.; Pan, X. Q.; Tsymbal, E. Y.; Rzchowski, M. S.; Eom, C. B.

2017-09-01

The growth and study of materials showing novel topological states of matter is one of the frontiers in condensed matter physics. Among this class of materials, the nitride antiperovskite Cu3PdN has been proposed as a new three-dimensional Dirac semimetal. However, the experimental realization of Cu3PdN and the consequent study of its electronic properties have been hindered due to the difficulty of synthesizing this material. In this study, we report fabrication and both structural and transport characterization of epitaxial Cu3PdN thin films grown on (001)-oriented SrTiO3 substrates by reactive magnetron sputtering and post-annealed in NH3 atmosphere. The structural properties of the films, investigated by x-ray diffraction and scanning transmission electron microscopy, establish single phase Cu3PdN exhibiting cube-on-cube epitaxy (001)[100]Cu3PdN||(001)[100]SrTiO3. Electrical transport measurements of as-grown samples show metallic conduction with a small temperature coefficient of the resistivity of 1.5 × 10-4 K-1 and a positive Hall coefficient. Post-annealing in NH3 results in the reduction of the electrical resistivity accompanied by the Hall coefficient sign reversal. Using a combination of chemical composition analyses and ab initio band structure calculations, we discuss the interplay between nitrogen stoichiometry and magneto-transport results in the framework of the electronic band structure of Cu3PdN. Our successful growth of thin films of antiperovskite Cu3PdN opens the path to further investigate its physical properties and their dependence on dimensionality, strain engineering, and doping.

Processing-property relations in YBa2Cu3O(6+x) superconductors

NASA Astrophysics Data System (ADS)

Safari, A.; Wachtman, J. B., Jr.; Parkhe, V.; Caracciolo, R.; Jeter, D.

Processing of YBa2Cu3O(6+x) superconducting samples by employing different precursor powder preparation techniques such as ball milling, attrition milling, and narrow particle size distribution powder preparation through coprecipitation by spraying will be discussed. CuO coated with oxalates shows the lowest resistance above Tc up to room temperature. The extent of corrosion by water has been studied by employing magnetic susceptibility, XPS, and X-ray diffraction. Superconducting samples are affected to a considerable extent when treated in water at 60 C and the severity of the attack increases with time.

Ferromagnetic order in epitaxially strained LaCoO3 thin films

NASA Astrophysics Data System (ADS)

Fuchs, D.; Pinta, C.; Schwarz, T.; Schweiss, P.; Nagel, P.; Schuppler, S.; Schneider, R.; Merz, M.; Roth, G.; v. Löhneysen, H.

2007-04-01

LaCoO3 films grown epitaxially on ⟨001⟩ oriented (LaAlO3)0.3(Sr2AlTaO6)0.7 substrates by pulsed laser deposition exhibit ferromagnetic ordering below a critical temperature, Tc , of 85K . Polycrystalline films of LaCoO3 prepared in the same way did not show ferromagnetic order down to T≈5K , and their temperature dependent susceptibility was identical to that of bulk LaCoO3 . The ferromagnetism in epitaxial films is not simply a property of the surface region, rather it extends over the complete film thickness, as shown by the linear increase of the saturated magnetic moment with increasing film thickness. We discuss this surprising result in terms of epitaxial tensile strain via the properly chosen substrate inducing ferromagnetic order.

Optimisation of growth of epitaxial Tl 2Ba 2Ca 1Cu 2O 8 superconducting thin films for electronic device applications

NASA Astrophysics Data System (ADS)

Michael, Peter C.; Johansson, L.-G.; Bengtsson, L.; Claeson, T.; Ivanov, Z. G.; Olsson, E.; Berastegui, P.; Stepantsov, E.

1994-12-01

Epitaxial thin films of Tl 2Ba 2Ca 1Cu 2O 8 (Tl-2212) superconductor have been grown on single crystal (100) lanthanum aluminate (LaAlO 3) substrates by a two stage process: laser ablation of a BaCaCuO (0212) sintered target and post-deposition anneal ex-situ in a thallium environment. The films are c-axis oriented with in-plane epitaxy as determined by x-ray diffraction (XRD θ-2θ and φ-scans). Superconducting transition temperatures as high as 105.5K have been obtained both from four-probe resistance and a.c. magnetic susceptibility measurements. Film morphology and chemical composition have been assessed by scanning electron microscopy (SEM) and energy dispersive x-ray analysis (EDX). Sensitivity of the precursor film to environmental exposure has proven to be a determining factor in the reproducibility of film growth characteristics. The effect of oxygen partial pressure and substrate temperature used in the precursor film synthesis, as well as the thallium annealing temperature and duration, on the growth of Tl-2212 thin films is reported.

Comparative study of flux pinning, creep and critical currents between YBaCuO crystals with and without Y2BaCuO5 inclusions

NASA Technical Reports Server (NTRS)

Murakami, Masato; Gotoh, Satoshi; Fujimoto, Hiroyuki; Koshizuka, Naoki; Tanaka, Shoji

1991-01-01

In the Y-Ba-Cu-O system, YBa2Cu3O(x) phase is produced by the following peritectic reaction: Y2BaCuO5 + liquid yields 2YBa2Cu3O(x). Through the control of processing conditions and starting compositions, it becomes possible to fabricate large crystals containing fine Y2BaCuO5(211) inclusions. Such crystals exhibit Jc values exceeding 10000 A/sq cm at 77 K and 1T. Recently, researchers developed a novel process which can control the volume fraction of 211 inclusions. Elimination of 211 inclusions is also possible. In this study, researchers prepared YBaCuO crystals with and without 211 inclusions using the novel process, and compared flux pinning, flux creep and critical currents. Magnetic field dependence of Jc for YBaCuO crystals with and with 211 inclusions is shown. It is clear that fine 211 inclusions can contribute to flux pinning. It was also found that flux creep rate could be reduced by increasing flux pinning force. Critical current density estimates based on the conventional flux pinning theory were in good agreement with experimental results.

Comparative study of electrical transport and magnetic measurements of Y3Ba5Cu8O18±δ and YBa2Cu3O7-δ compounds: intragranular and intergranular superconducting properties

NASA Astrophysics Data System (ADS)

Slimani, Y.; Hannachi, E.; Ben Salem, M. K.; Ben Azzouz, F.; Ben Salem, M.

2018-02-01

We compare the superconducting properties and flux pinning characteristics between YBa2Cu3O7-δ (called Y-123) and Y3Ba5Cu8O18±δ (called Y-358) compounds. Both samples were synthesized through the solid-state reaction. The samples were examined by X-ray diffraction, and scanning electron microscope coupled with energy dispersive spectrometry. The critical current densities of the prepared samples were investigated using current-voltage, magnetization measurements and ac-susceptibility. It is demonstrated that the Y-358 exhibits better superconducting and pinning properties than the Y-123 one. This may be ascribed to the layered structure and the occurrence of a greater number of insulating layers between the CuO2 planes that act as effective pinning sites and consequently conduce to a better fundamental pinning capacity in Y-358.

Electronic Structure of HgBa2CaCu2O(6+delta) Epitaxial films measured by x-ray Photoemission

NASA Technical Reports Server (NTRS)

Vasquez, R. P.; Rupp, M.; Gupta, A.; Tsuei, C. C.

1995-01-01

The electronic structure and chemical states of HgBa2CaCu20(sub 6 + delta), epitaxial films have been studied with x-ray photelectron spectroscopy. Signals from the superconducting phase dominate all the core-level spectra, and a clear Fermi edge is observed in the valence-band region. The Ba, Ca, Cu, and O core levels are similar to those of Tl2Ba2CaCu208(+)O(sub 6 + delta), but distinct differences are observed in the valence bands which are consistent with differences in the calculated densities of states.

Transport properties of YBa2Cu3Ox /La0.67Sr0.33MnO3 nanostrips and YBa2Cu3Ox/La0.67Sr0.33MnO3/YBa2Cu3Ox nanojunctions

NASA Astrophysics Data System (ADS)

Štrbík, V.; Beňačka, Š.; Gaži, Š.; Španková, M.; Šmatko, V.; Chromik, Š.; Gál, N.; Knoška, J.; Sojková, M.; Pisarčík, M.

2016-03-01

A metallic ferromagnet (F) in proximity with a superconductor (S) can transport supercurrent on a long distance through conversion of opposite-spin singlet Cooper pairs (CP) into equal-spin triplet CP (long range triplet component, LRTC), which are not broken by the exchange energy of F. The optimal conditions for the conversion are yet to be clarified; however, it is accepted that the key point to this process include high interface transparency and magnetic inhomogeneity at the SF interface. The aim of our paper is to study SF nanostrips (length of about 1500 nm and width down to 300 nm) and lateral SFS nanojunctions based on high critical temperature YBa2Cu3Ox (YBCO) and half-metallic La0.67Sr0.33MnO3 (LSMO) thin films. We applied a focused Ga+ ion beam (FIB) for patterning the SF nanostrips, as well as lateral SFS nanojunctions, by creating a slot in the nanostrip after removing the YBCO film in the slot along a length of about 200 nm. The temperature dependences of the samples resistance R(T) show critical temperature TCn ≈ 89 K of the SF nanostrips; however, the SFS nanojunctions at T < TCn show a residual resistance R < 100 Ω corresponding to a dirty LSMO (ρ≈ 10 mΩ cm) in the slot. The LRTC was not observed in our lateral SFS nanojunctions until now.

Room-temperature annealing effects on the basal-plane resistivity of optimally doped YBa2Cu3O7-δ single crystals

NASA Astrophysics Data System (ADS)

Khadzhai, G. Ya.; Vovk, R. V.; Vovk, N. R.; Kamchatnaya, S. N.; Dobrovolskiy, O. V.

2018-02-01

We reveal that the temperature dependence of the basal-plane normal-state electrical resistance of optimally doped YBa2Cu3O7-δ single crystals can be with great accuracy approximated within the framework of the model of s-d electron-phonon scattering. This requires taking into account the fluctuation conductivity whose contribution exponentially increases with decreasing temperature and decreases with an increase of oxygen deficiency. Room-temperature annealing improves the sample and, thus, increases the superconducting transition temperature. The temperature of the 2D-3D crossover decreases during annealing.

Preparation of thin-film (Ba(0.5),Sr(0.5))TiO3 by the laser ablation technique and electrical properties

NASA Astrophysics Data System (ADS)

Yoon, Soon-Gil; Lee, Jai-Chan; Safari, A.

1994-09-01

The chemical composition and electrical properties were investigated for epitaxially crystallized (Ba(0.5),Sr(0.5))TiO3 (BST) films deposited on Pt/MgO and YBa2Cu3O(7-x) (YBCO)/MgO substrates by the laser ablation technique. Rutherford backscattering spectroscopy analysis shows that thin films on Pt/MgO have almost the same stoichiometric composition as the target material. Films deposited at 600 C exhibited an excellent epitaxial growth, a dielectric constant of 430, and a dissipation factor of 0.02 at 10 kHz frequency. They have a charge storage density of 40 fC/sq micron at an applied electric field of 0.15 MV/cm. Leakage current density of BST thin films on Pt/MgO was smaller than on YBCO/MgO. Their leakage current density is about 0.8 microA/sq cm at an applied electric field of 0.15 MV/cm.

Unconventional critical state in YBa2Cu3O7-δ thin films with a vortex-pin lattice fabricated by masked He+ ion beam irradiation

NASA Astrophysics Data System (ADS)

Zechner, G.; Mletschnig, K. L.; Lang, W.; Dosmailov, M.; Bodea, M. A.; Pedarnig, J. D.

2018-04-01

Thin superconducting YBa2Cu3O7-δ films are patterned with a vortex-pin lattice consisting of columnar defect regions (CDs) with 180 nm diameter and 300 nm spacing. They are fabricated by irradiation with 75 keV He+ ions through a stencil mask. Peaks of the critical current reveal the commensurate trapping of vortices in domains near the edges of the sample. Upon ramping an external magnetic field, the positions of the critical current peaks are shifted from their equilibrium values to lower magnetic fields in virgin and to higher fields in field-saturated down-sweep curves, respectively. Based on previous theoretical predictions, this irreversibility is interpreted as a nonuniform, terrace-like critical state, in which individual domains are occupied by a constant number of vortices per pinning site. The magnetoresistance, probed at low current densities, is hysteretic and angle dependent and exhibits minima that correspond to the peaks of the critical current. The minima’s positions scale with the component of the magnetic field parallel to the axes of the CDs, as long as the tilted vortices can be accommodated within the CDs. This behavior, different from unirradiated films, confirms that the CDs dominate the pinning.

Effects of oxygen stoichiometry on the scaling behaviors of YBa{sub 2}Cu{sub 3}O{sub x} grain boundary weak-links

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, K.H.; Fu, C.M.; Jeng, W.J.

1994-12-31

The effects of oxygen stoichiometry on the transport properties of the pulsed laser deposited YBa{sub 2}Cu{sub 3}O{sub x} bicrystalline grain boundary weak-link junctions were studied. It is found that not only the cross boundary resistive transition foot structure can be manipulated repeatedly with oxygen annealling processes but the junction behaviors are also altered in accordance. In the fully oxygenated state i.e. with x=7.0 in YBa{sub 2}Cu{sub 3}O{sub x} stoichiometry, the junction critical current exhibits a power of 2 scaling behavior with temperature. In contrast, when annealed in the conditions of oxygen-deficient state (e.g. with x=6.9 in YBa{sub 2}Cu{sub 3}O{sub x}more » stoichiometry) the junction critical current switches to a linear temperature dependence behavior. The results are tentatively attributed to the modification of the structure in the boundary area upon oxygen annealing, which, in turn, will affect the effective dimension of the geometrically constrained weak-link bridges. The detailed discussion on the responsible physical mechanisms as well as the implications of the present results on device applications will be given.« less

Observation of Caroli-de Gennes-Matricon Vortex States in YBa2Cu3O7 -δ

NASA Astrophysics Data System (ADS)

Berthod, Christophe; Maggio-Aprile, Ivan; Bruér, Jens; Erb, Andreas; Renner, Christoph

2017-12-01

The copper oxides present the highest superconducting temperature and properties at odds with other compounds, suggestive of a fundamentally different superconductivity. In particular, the Abrikosov vortices fail to exhibit localized states expected and observed in all clean superconductors. We have explored the possibility that the elusive vortex-core signatures are actually present but weak. Combining local tunneling measurements with large-scale theoretical modeling, we positively identify the vortex states in YBa2Cu3O7 -δ . We explain their spectrum and the observed variations thereof from one vortex to the next by considering the effects of nearby vortices and disorder in the vortex lattice. We argue that the superconductivity of copper oxides is conventional, but the spectroscopic signature does not look so because the superconducting carriers are a minority.

Optical Studies of Thin Film and Bulk Superconductor Yttrium BARIUM(2) COPPER(3) OXYGEN(7-DELTA)

NASA Astrophysics Data System (ADS)

Sengupta, Louise Clare

This dissertation summarizes a systematic study of the optical properties of YBa_2Cu _3O_{7-delta } using the nondestructive techniques of spectroscopic ellipsometry, Raman scattering, and infrared absorption spectroscopy. In order to complete this research, a spectroscopic ellipsometric system has been designed and the fully automated system has been developed in this laboratory. Using the ellipsometric study, we have determined the effect of metallic replacement for Cu by Co, Fe, Ni, and Zn in YBa _2Cu_3O_ {7-delta} on the 1.7 eV electronic transition. The transition is observed in the case of doping by trivalent Co and Fe and in the case of oxygen deficiency. In all cases, it was established as result of a decrease in the hole concentration. The Raman spectra show a decrease in the frequency of the 500 cm ^{-1} mode with increase in Co and Fe concentration and an upward shift in frequency of the 435 cm^{-1} mode. These results, along with those for Ni and Zn doping are discussed in terms of the normal mode calculations for the material. The infrared phonon spectra also indicate a reduction in the electronic screening for trivalent dopants Co and Fe. All the optical experiments support evidence of the occurrence of a charge transfer mechanism in the high T_ {rm c} material YBa_2 Cu_3O in which the more insulating chains act as reservoirs of charge for the conducting copper -oxygen planes. As part of investigating the effects of orientation of the films on the optical constants of the material, studies on YBa_2Cu_3 O_{7-delta} deposited at various thicknesses on SrTiO_3 substrates have been completed using spectroscopic ellipsometry. The results indicate that the metallic behavior associated with the ab planes decreases with increasing film thickness. This behavior is well characterized by an exponential relationship between the relaxation time and the critical energy position at which the real part of the dielectric function becomes zero. The anisotropy of the

Influence of water vapor on the formation of pinning centers in YBa2Cu3O y upon low-temperature annealing

NASA Astrophysics Data System (ADS)

Bobylev, I. B.; Gerasimov, E. G.; Zyuzeva, N. A.

2017-08-01

The influence of the double heat treatment ( T = 300 and 930°C) on the critical parameters of highly textured YBa2Cu3O6.96 and YBa2Cu3O6.8 ceramics has been investigated. It has been shown that, upon low-temperature annealing in humid air, planar stacking faults are formed in these ceramics. These defects are partly retained after reduction annealing (at T = 930°C) and are efficient pinning centers in magnetic fields applied parallel and perpendicular to the c axis. Due to the absorption of water, the oxygen content is increased in the ceramics, which is accompanied by an increase in the critical temperature of superconducting transition up to 94 K for YBa2Cu3O6.96 and up to 90 K for YBa2Cu3O6.8. Optimal conditions of the double annealing have been established, after which the critical-current density increased to j c ≥ 104 A/cm2 in an external magnetic field of up to 6 T. The low-temperature treatment in the neutral atmosphere saturated by water vapors deteriorates the current-carrying capacity of the highly textured ceramics, which is connected with the disappearance of texture due to the copper reduction and the precipitation of impurity phases.

High T c superconductivity in YBa2Cu3O7- x studied by PAC and PAS

NASA Astrophysics Data System (ADS)

Zhu, Shengyun; Li, Anli; Zheng, Shengnan; Huang, Hanchen; Li, Donghong; Din, Honglin; Du, Hongshan; Sun, Hancheng

1993-03-01

High T c superconductivity has been investigated in YBaCuO by both perturbed angular correlation and positron annihilation spectroscopy techniques as a function of temperature from 77 to 300 K. An abrupt change has been observed in the positron lifetime and Doppler broadening and the electric field gradient and its asymmetry parameter across T c, indicating a transition of two- to one-dimensional Cu-O-Cu chain structure and a charge transfer from CuO layers to CuO chains. An anomaly of the normal state has been demonstrated around 125 K, which is attributed to the structural instability.

Superconducting YBa2Cu3O7 Powder: Reduction of Carbon, Moisture, and Impurity Phase Concentrations in Commercial Powders and the Reactivity with Moisture and Carbon Dioxide

NASA Technical Reports Server (NTRS)

Stecura, Stephan

1994-01-01

The purpose of this study was to determine the experimental parameters under which commercially pure YBa2Cu3O7 (1237) powders would be converted into a single phase (1237) powder only. Carbon (present as carbonate) and impurity phase concentrations in the (1237) powder are very dependent upon the firing temperatures, heat-treating temperatures and times, and atmosphere, while the moisture concentration is not. YBa2Cu3O7 powder with about 0.03 wt/%, carbon, 0.03 wt% moisture, and low impurity phase concentrations was obtained. Moisture and carbon concentrations in heat-treated powders did not increase significantly after 48 and 72 h of exposure to air, respectively, and after 144 h of exposure they were less than 0.26 and 0.08 wt/%, respectively. The (1237) powder first reacts with moisture and then hydroxide reacts with CO2. Firing the as received powders in air led to the decomposition of the superconducting (1237) phase.

Direct, experimental evidence of the Fermi surface in YBa2Cu3O(7-x)

NASA Astrophysics Data System (ADS)

Haghighi, H.; Kaiser, J. H.; Rayner, S. L.; West, R. N.; Liu, J. Z.; Shelton, R.; Howell, R. H.; Sterne, P. A.; Solal, F. R.; Fluss, M. J.

1991-04-01

We report new measurements of the electron positron momentum spectra of YBa2Cu3O(7-x) performed with ultra-high statistical precision. These data differ from previous results in two significant respects: They show the D(sub 2) symmetry appropriate for untwinned crystals and, more importantly, they show unmistakable, statistically significant, discontinuities that are evidence of a major Fermi surface section. These results provide a partial answer to a question of special significance to the study of high temperature superconductors i.e., the distribution of the electrons in the material, the electronic structure. Special consideration has been given both experimentally and theoretically to the existence and shape of a Fermi surface in the materials and to the superconducting gap. There are only three experimental techniques that can provide details of the electronic structure at useful resolutions. They are angular correlation of positron annihilation radiation, ACAR, angle resolved photo emission, PE, and de Haas van Alphen measurements.

Charge Order and Superconductivity in Underdoped YBa2 Cu3 O7 -δ under Pressure

NASA Astrophysics Data System (ADS)

Putzke, Carsten; Ayres, Jake; Buhot, Jonathan; Licciardello, Salvatore; Hussey, Nigel E.; Friedemann, Sven; Carrington, Antony

2018-03-01

In underdoped cuprates, an incommensurate charge density wave (CDW) order is known to coexist with superconductivity. A dip in Tc at the hole doping level where the CDW is strongest (np≃0.12 ) suggests that CDW order may suppress superconductivity. We investigate the interplay of charge order with superconductivity in underdoped YBa2 Cu3 O7 -δ by measuring the temperature dependence of the Hall coefficient RH(T ) at high magnetic field and at high hydrostatic pressure. We find that, although pressure increases Tc by up to 10 K at 2.6 GPa, it has very little effect on RH(T ). This suggests that pressure, at these levels, only weakly affects the CDW and that the increase in Tc with pressure cannot be attributed to a suppression of the CDW. We argue, therefore, that the dip in Tc at np≃0.12 at ambient pressure is probably not caused by the CDW formation.

Mechanical response of the flux lines in ceramic YBa2Cu3O7-δ

NASA Astrophysics Data System (ADS)

Luzuriaga, J.; André, M.-O.; Benoit, W.

1992-06-01

We have studied the mechanical response of the flux-line lattice (FLL) in ceramic samples of YBa2Cu3O7 by means of a low-frequency forced pendulum. The internal friction and elastic modulus variation of the FLL have been measured as a function of temperature for different values of the applied stress. A somewhat different behavior was observed whether a zero-field-cooling or field-cooling procedure was followed. Measurements of the internal friction and elastic modulus as a function of the applied stress at constant temperature show amplitude-dependent dissipation, with a maximum dissipation at intermediate values of the stress. This dependence is well fitted by a rheological model of extended dry friction, if we restrict ourselves to the dissipation and modulus at fixed temperature. The agreement is not so good when attempting to extend the model to fit the temperature dependence.