Electro-Caloric Properties of BT/PZT Multilayer Thin Films Prepared by Sol-Gel Method.

PubMed

Kwon, Min-Su; Lee, Sung-Gap; Kim, Kyeong-Min

2018-09-01

In this study, Barium Titanate (BT)/Lead Zirconate Titanate (PZT) multilayer thin films were fabricated by the spin-coating method on Pt (200 nm)/Ti (10 nm) SiO2 (100 nm)/P-Si (100) substrates using BaTiO3 and Pb(Zr0.90Ti0.10)O3 metal alkoxide solutions. The coating and heating procedure was repeated several times to form the multilayer thin films. All of BT/PZT multilayer thin films show X-ray diffraction patterns typical to a polycrystalline perovskite structure and a uniform and void free grain microstructure. The thickness of the BT and PZT film by one-cycle of drying/sintering was approximately 50 nm and all of the films consisted of fine grains with a flat surface morphology. The electrocaloric properties of BT/PZT thin films were investigated by indirect estimation. The results showed that the temperature change ΔT can be calculated as a function of temperature using Maxwell's relation; the temperature change reaches a maximum value of ~1.85 °C at 135 °C under an applied electric field of 260 kV/cm.

Transverse piezoelectric coefficient measurement of flexible lead zirconate titanate thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dufay, T.; Guiffard, B.; Seveno, R.

Highly flexible lead zirconate titanate, Pb(Zr,Ti)O{sub 3} (PZT), thin films have been realized by modified sol-gel process. The transverse piezoelectric coefficient d{sub 31} was determined from the tip displacement of bending-mode actuators made of PZT cantilever deposited onto bare or RuO{sub 2} coated aluminium substrate (16 μm thick). The influence of the thickness of ruthenium dioxide RuO{sub 2} and PZT layers was investigated for Pb(Zr{sub 0.57}Ti{sub 0.43})O{sub 3}. The modification of Zr/Ti ratio from 40/60 to 60/40 was done for 3 μm thick PZT thin films onto aluminium (Al) and Al/RuO{sub 2} substrates. A laser vibrometer was used to measure the beammore » displacement under controlled electric field. The experimental results were fitted in order to find the piezoelectric coefficient. Very large tip deflections of about 1 mm under low voltage (∼8 V) were measured for every cantilevers at the resonance frequency (∼180 Hz). For a given Zr/Ti ratio of 58/42, it was found that the addition of a 40 nm thick RuO{sub 2} interfacial layer between the aluminium substrate and the PZT layer induces a remarkable increase of the d{sub 31} coefficient by a factor of 2.7, thus corresponding to a maximal d{sub 31} value of 33 pC/N. These results make the recently developed PZT/Al thin films very attractive for both low frequency bending mode actuating applications and vibrating energy harvesting.« less

Optimization of PbTiO3 Seed Layers for PZT MEMS Actuators

DTIC Science & Technology

2008-12-01

14. ABSTRACT The material properties of sol-gel lead zirconate titanate ( PZT ) are inherently linked with its crystallinity and texture . The use...will lead to a greater degree of texturing within the PZT thin film. Figure 6. X-ray diffraction data for PT seed solution. (001) oriented...previous studies PZT 45/55 has shown a higher piezoelectric coefficient compared to PZT 52/48 due to the random crystalline texture of the existing

Nano-embossing technology on ferroelectric thin film Pb(Zr0.3,Ti0.7)O3 for multi-bit storage application

PubMed Central

2011-01-01

In this work, we apply nano-embossing technique to form a stagger structure in ferroelectric lead zirconate titanate [Pb(Zr0.3, Ti0.7)O3 (PZT)] films and investigate the ferroelectric and electrical characterizations of the embossed and un-embossed regions, respectively, of the same films by using piezoresponse force microscopy (PFM) and Radiant Technologies Precision Material Analyzer. Attributed to the different layer thickness of the patterned ferroelectric thin film, two distinctive coercive voltages have been obtained, thereby, allowing for a single ferroelectric memory cell to contain more than one bit of data. PMID:21794156

Effect of ultraviolet light on fatigue of lead zirconate titanate thin-film capacitors

NASA Astrophysics Data System (ADS)

Lee, J.; Esayan, S.; Safari, A.; Ramesh, R.

1994-07-01

Fatigue of Pb(Zr0.52Ti0.48)O3 (PZT) thin-film capacitors was studied under UV light (He-Cd laser, λ=325 nm). The remanent polarization of the PZT film capacitors increased upon light illumination. Fatigue resistance was also improved under UV light. During fatigue test, the change in polarization of PZT films upon UV light illumination increased gradually with cycling. These results were examined within the framework of the polarization screening model, which is suggested as an essential process for fatigue. This leads to a conclusion that more charged defects are involved in the fatigue process through internal screening of polarization.

Effect of La and W dopants on dielectric and ferroelectric properties of PZT thin films prepared by sol-gel process

NASA Astrophysics Data System (ADS)

Xiao, Mi; Zhang, Zebin; Zhang, Weikang; Zhang, Ping

2018-01-01

La or W-doped lead zirconate titanate thin films (PLZT or PZTW) were prepared on platinized silicon substrates by sol-gel process. The effects of La or W dopant on the phase development, microstructure, dielectric and ferroelectric characteristics of films were studied. For PLZT films, the optimum doping concentration was found to be 2 mol%. While for PZTW films, the dielectric and ferroelectric properties were found to be improved as the doping concentration increased. The fatigue properties of PLZT and PZTW thin films were also investigated, the results showed that A- or B-site donor doping could improve the fatigue properties of PZT thin films. The theory of oxygen vacancy was used to explain the performance improvement caused by donor doping.

High-piezoelectric behavior of c-axis-oriented lead zirconate titanate thin films with composition near the morphotropic phase boundary

NASA Astrophysics Data System (ADS)

Fu, Desheng; Suzuki, Hisao; Ogawa, Takeshi; Ishikawa, Kenji

2002-05-01

The piezoelectric responses of c-axis-oriented Pb(Zr0.53Ti0.47)O3 (PZT) thin films have been studied by measuring the stress-induced charge with an accurate charge integrator. These measurements reveal that the c-axis-oriented PZT films have high values of d33, which are several times those of ceramic materials. The intrinsic d33 values of poled films are about 680 and 800 pC/N for the c-axis-oriented films on Si and MgO single-crystal substrates, respectively. It shows that the thin-film deposition technique opens an approach for exploring the potential superior properties of PZT near the morphotropic phase boundary.

Development of lead zirconate titanate cantilevers on the micrometer length scale

NASA Astrophysics Data System (ADS)

Martin, Christopher Robert

The objective of this research project was to fabricate a functional ferroelectric microcantilever from patterned lead zirconate titanate (PZT) thin films. Cantilevers fabricated from ferroelectric materials have tremendous potential in sensing applications, particularly due to the increased sensitivity that miniaturized devices offer. This thesis highlights and explores a number of the processing issues that hindered the production of a working prototype. PZT is patterned using soft lithography-inspired techniques from a PZT chemical precursor solution derived by the chelation synthesis route. As the ability to pattern ceramic materials derived from sol-gels on the micrometer scale is a relatively new technology, this thesis aims to expand the scientific understanding of new issues that arise when working with these patterned films. For example, the use of Micromolding in Capillaries (MIMIC) to pattern the PZT thin films results in the evolution of topographical distortions from the shape of the original mold during the shrinkage of patterned thin film during drying and sintering. The factors that contribute to this effect have been explained and a new processing technique called MicroChannel Molding (muCM) was developed. This new process combines the advantages of soft lithography with traditional silicon microfabrication techniques to ensure compatibility with current industrial practices. This work lays the foundation for the future production of working ferroelectric microcantilevers. The proposed microfabrication process is described along with descriptions of each processing difficulty that was encountered. Modifications to the process are proposed along with the descriptions of alternative processing techniques that were attempted for the benefit of future researchers. This dissertation concludes with the electronic characterization of micropattemed PZT thin films. To our knowledge, the ferroelectric properties of patterned PZT thin films have never been directly characterized before. The properties are measured with a commercial ferroelectric test system connected through a conductive Atomic Force Microscope tip. The films patterned by MIMIC and muCM are compared to large-area spin cast films to identify the role that the processing method has on the resulting properties.

Energy Harvesting with Coupled Magnetorestrictive Resonators

DTIC Science & Technology

2013-09-01

matching, small hysteresis, and low coercivity2. Ceramic material like PZT tends to develop fatigue during its cycles whereas Galfenol does not have...Magnetostrictive Material PZT Pb [ZrxTi1-x] O3, 0<xə, Lead Zirconate Titanate RX Receiver SHM Structural Health Monitoring...zirconate titanate [ PZT ]) have lead in their fabrication process, which is an environmental risk. Another major issue with standard energy

Misfit strain phase diagrams of epitaxial PMN–PT films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Khakpash, N.; Khassaf, H.; Rossetti, G. A.

Misfit strain–temperature phase diagrams of three compositions of (001) pseudocubic (1 − x)·Pb (Mg{sub l/3}Nb{sub 2/3})O{sub 3} − x·PbTiO{sub 3} (PMN–PT) thin films are computed using a phenomenological model. Two (x = 0.30, 0.42) are located near the morphotropic phase boundary (MPB) of bulk PMN–PT at room temperature (RT) and one (x = 0.70) is located far from the MPB. The results show that it is possible to stabilize an adaptive monoclinic phase over a wide range of misfit strains. At RT, the stability region of this phase is much larger for PMN–PT compared to barium strontium titanate and lead zirconate titanate films.

Wafer-scale growth of highly textured piezoelectric thin films by pulsed laser deposition for micro-scale sensors and actuators

NASA Astrophysics Data System (ADS)

Nguyen, M. D.; Tiggelaar, R.; Aukes, T.; Rijnders, G.; Roelof, G.

2017-11-01

Piezoelectric lead-zirconate-titanate (PZT) thin films were deposited on 4-inch (111)Pt/Ti/SiO2/Si(001) wafers using large-area pulsed laser deposition (PLD). This study was focused on the homogeneity in film thickness, microstructure, ferroelectric and piezoelectric properties of PZT thin films. The results indicated that the highly textured (001)-oriented PZT thin films with wafer-scale thickness homogeneity (990 nm ± 0.8%) were obtained. The films were fabricated into piezoelectric cantilevers through a MEMS microfabrication process. The measured longitudinal piezoelectric coefficient (d 33f = 210 pm/V ± 1.6%) and piezoelectric transverse coefficient (e 31f = -18.8 C/m2 ± 2.8%) were high and homogeneity across wafers. The high piezoelectric properties on Si wafers will extend industrial application of PZT thin films and further development of piezoMEMS.

A Bayesian approach to modeling diffraction profiles and application to ferroelectric materials

DOE PAGES

Iamsasri, Thanakorn; Guerrier, Jonathon; Esteves, Giovanni; ...

2017-02-01

A new statistical approach for modeling diffraction profiles is introduced, using Bayesian inference and a Markov chain Monte Carlo (MCMC) algorithm. This method is demonstrated by modeling the degenerate reflections during application of an electric field to two different ferroelectric materials: thin-film lead zirconate titanate (PZT) of composition PbZr 0.3Ti 0.7O 3and a bulk commercial PZT polycrystalline ferroelectric. Here, the new method offers a unique uncertainty quantification of the model parameters that can be readily propagated into new calculated parameters.

Piezoelectric ultrasonic micromotor with 1.5 mm diameter.

PubMed

Dong, Shuxiang; Lim, Siak P; Lee, Kwork H; Zhang, Jingdong; Lim, Leong C; Uchino, Kenji

2003-04-01

A piezoelectric ultrasonic micromotor has been developed using a lead zirconate titanate (PZT) ceramic/metal composite tube stator that was 1.5 mm in diameter and 7 mm in length. The micromotor was operated in its first bending vibration mode (approximately 70 kHz), producing speeds from hundreds to over 2000 rpm in both rotational directions. The maximum torque-output was 45 microN-m, which is far superior to previous PZT thin film-based micromotors. This micromotor showed good reliability and stability for more than 300 hours of continued operation.

Lead zirconate titanate (PZT)-based thin film capacitors for embedded passive applications

NASA Astrophysics Data System (ADS)

Kim, Taeyun

Investigations on the key processing parameters and properties relationship for lead zirconate titanate (PZT, 52/48) based thin film capacitors for embedded passive capacitor application were performed using electroless Ni coated Cu foils as substrates. Undoped and Ca-doped PZT (52/48) thin film capacitors were prepared on electroless Ni coated Cu foil by chemical solution deposition. For PZT (52/48) thin film capacitors on electroless Ni coated Cu foil, voltage independent (zero tunability) capacitance behavior was observed. Dielectric constant reduced to more than half of the identical capacitor processed on Pt/SiO2/Si. Dielectric properties of the capacitors were mostly dependent on the crystallization temperature. Capacitance densities of almost 350 nF/cm2 and 0.02˜0.03 of loss tangent were routinely measured for capacitors crystallized at 575˜600°C. Leakage current showed dependence on film thickness and crystallization temperature. From a two-capacitor model, the existence of a low permittivity interface layer (permittivity ˜30) was suggested. For Ca-doped PZT (52/48) thin film capacitors prepared on Pt, typical ferroelectric and dielectric properties were measured up to 5 mol% Ca doping. When Ca-doped PZT (52/48) thin film capacitors were prepared on electroless Ni coated Cu foil, phase stability was influenced by Ca doping and phosphorous content. Dielectric properties showed dependence on the crystallization temperature and phosphorous content. Capacitance density of ˜400 nF/cm2 was achieved, which is an improvement by more than 30% compared to undoped composition. Ca doping also reduced the temperature coefficient of capacitance (TCC) less than 10%, all of them were consistent in satisfying the requirements of embedded passive capacitor. Leakage current density was not affected significantly by doping. To tailor the dielectric and reliability properties, ZrO2 was selected as buffer layer between PZT and electroless Ni. Only RF magnetron sputtering process could yield stable ZrO2 layers on electroless Ni coated Cu foil. Other processes resulted in secondary phase formation, which supports the reaction between PZT capacitor and electroless Ni might be dominated by phosphorous component. (Abstract shortened by UMI.)

Lead zirconate titanate nanowire textile nanogenerator for wearable energy-harvesting and self-powered devices.

PubMed

Wu, Weiwei; Bai, Suo; Yuan, Miaomiao; Qin, Yong; Wang, Zhong Lin; Jing, Tao

2012-07-24

Wearable nanogenerators are of vital importance to portable energy-harvesting and personal electronics. Here we report a method to synthesize a lead zirconate titanate textile in which nanowires are parallel with each other and a procedure to make it into flexible and wearable nanogenerators. The nanogenerator can generate 6 V output voltage and 45 nA output current, which are large enough to power a liquid crystal display and a UV sensor.

MEMS-Based Waste Vibrational Energy Harvesters

DTIC Science & Technology

2013-06-01

7 1. Lead Zirconium Titanate ( PZT ) .........................................................7 2. Aluminum...Laboratory PiezoMUMPS Piezoelectric Multi-User MEMS Processes PZT Lead Zirconate Titanate SEM Scanning Electron Microscopy SiO2 Silicon...titanate ( PZT ) possess high 4 coupling between the electrical and mechanical domains [11]. The output voltage, V, is related to the z-component

Growth and properties of gradient free sol-gel lead zirconate titanate thin films

NASA Astrophysics Data System (ADS)

Calame, F.; Muralt, P.

2007-02-01

Pb(Zrx,Ti1-x)O3 thin films of homogeneous composition were synthesized by means of a modified sol-gel route on Pt(111)/TiOx/SiO2/Si substrates. The gradient in B-site composition as obtained by standard routes could be lowered, reducing Zr concentration fluctuations form ±12to±2.5at.%. The 2μm thick, dense and crack-free films exhibited a {100}-texture index of 98.4%. Grain diameters increased by 50%. Dielectric and piezoelectric properties were remarkably improved. The relative dielectric constant ɛ33,f was obtained as 1620, and the remanent transverse piezoelectric coefficient e31,f was measured as -17.7Cm2.

Effect of the Sintering Temperature on the Formation of Ferroelectric Properties of a Lead Zirconate-Titanate Ceramic

NASA Astrophysics Data System (ADS)

Barabanova, E. V.; Topchiev, A. A.; Malyshkina, O. V.

2018-04-01

Effect of the sintering temperature on the formation of the microstructure, the domain structure, and the ferroelectric properties of a lead zirconate-titanate Pb(Ti x Zr1 - x )O3 piezoelectric ceramics has been studied. It is shown that the ferroelectric phase forms at a sintering temperature of 860°C. At higher sintering temperatures, the main effect on the properties is due to a unit cell deformation and free charge carriers.

Effects of Thickness, Pulse Duration, and Size of Strip Electrode on Ferroelectric Electron Emission of Lead Zirconate Titanate Films

NASA Astrophysics Data System (ADS)

Yaseen, Muhammad; Ren, Wei; Chen, Xiaofeng; Feng, Yujun; Shi, Peng; Wu, Xiaoqing

2018-02-01

Sol-gel-derived lead zirconate titanate (PZT) thin-film emitters with thickness up to 9.8 μm have been prepared on Pt/TiO2/SiO2/Si wafer via chemical solution deposition with/without polyvinylpyrrolidone (PVP) modification, and the relationship between the film thickness and electron emission investigated. Notable electron emission was observed on application of a trigger voltage of 120 V for PZT film with thickness of 1.1 μm. Increasing the film thickness decreased the threshold field to initiate electron emission for non-PVP-modified films. In contrast, the electron emission behavior of PVP-modified films did not show significant dependence on film thickness, probably due to their porous structure. The emission current increased with decreasing strip width and space between strips. Furthermore, it was observed that increasing the duration of the applied pulse increased the magnitude of the emission current. The stray field on the PZT film thickness was also calculated and found to increase with increasing ferroelectric sample thickness. The PZT emitters were found to be fatigue free up to 105 emission cycles. Saturated emission current of around 25 mA to 30 mA was achieved for the electrode pattern used in this work.

Lanthanide stannate pyrochlores (Ln2Sn2O7; Ln  =  Nd, Gd, Er) at high pressure

NASA Astrophysics Data System (ADS)

Turner, Katlyn M.; Tracy, Cameron L.; Mao, Wendy L.; Ewing, Rodney C.

2017-12-01

Lanthanide stannate pyrochlores (Ln2Sn2O7; Ln  =  Nd, Gd, and Er) were investigated in situ to 50 GPa in order to determine their structural response to compression and compare their response to that of lanthanide titanate, zirconate, and hafnate pyrochlores. The cation radius ratio of A3+/B4+ in pyrochlore oxides (A2B2O7) is thought to be the dominant feature that influences their response on compression. The ionic radius of Sn4+ is intermediate to that of Ti4+, Zr4+, and Hf4+, but the 〈Sn-O〉 bond in stannate pyrochlore is more covalent than the 〈B-O〉 bonds in titanates, zirconate, and hafnates. In stannates, based on in situ Raman spectroscopy, pyrochlore cation and anion sublattices begin to disorder with the onset of compression, first measured at 0.3 GPa. The extent of sublattice disorder versus pressure is greater in stannates with a smaller Ln3+ cation. Stannate pyrochlores (Fd-3m) begin a sluggish transformation to an orthorhombic, cotunnite-like structure at ~28 GPa similar transitions have been observed in titanate, zirconate, and hafnate pyrochlores at varying pressures (18-40 GPa) with cation radius ratio. The extent of the phase transition versus pressure varies directly with the size of the Ln3+ cation. Post-decompression from ~50 GPa, Er2Sn2O7 and Gd2Sn2O7 adopt a pyrochlore structure, rather than the multi-scale defect-fluorite  +  weberite-type structure adopted by Nd2Sn2O7 that is characteristic of titanate, zirconate, and hafnate pyrochlores under similar conditions. Like pyrochlore titanates, zirconates, and hafnates, the bulk modulus, B 0, of stannates varies linearly and inversely with cation radius ratio from 1 1 1 GPa (Nd2Sn2O7) to 251 GPa (Er2Sn2O7). The trends of bulk moduli in stannates in this study are in excellent agreement with previous experimental studies on stannates and suggest that the size of the Ln3+ cation is the primary determining factor of B 0. Additionally, when normalized to r A/r B, the bulk moduli of stannates are comparable to those of zirconates and hafnates, which vary from titanates. Our results suggest that the cation radius ratio strongly influences the bulk moduli of stannates, as well as their overall compression response.

Integration of PLZT and BST family oxides with GaN[Lead Lanthanum Zirconate Titanate, Barium Strontium Titanate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Osinsky, A.V.; Fuflyigin, V.N.; Wang, F.

2000-07-01

Recent advances in the processing of complex-oxide materials has allowed the authors to monolithically grow ferroelectrics of lead lanthanum zirconate titanate (PLZT) and barium strontium titanate (BST) systems on a GaN/sapphire structure. High quality films of PLZT and BST were grown on GaN/c-Al{sub 2}O{sub 3} in a thickness range of 0.3--5 {micro}m by a sol-gel technique. Field-induced birefringence, as large as 0.02, was measured from a PLZT layer grown on a buffered GaN/sapphire structure. UV illumination was found to result in more symmetrical electrooptic hysteresis loop. BST films on GaN demonstrated a low frequency dielectric constant of up to 800more » with leakage current density as low as 5.5 {center_dot} 10{sup {minus}8} A/cm{sup 2}.« less

Hydrogen species motion in piezoelectrics: A quasi-elastic neutron scattering study

NASA Astrophysics Data System (ADS)

Alvine, K. J.; Tyagi, M.; Brown, C. M.; Udovic, T. J.; Jenkins, T.; Pitman, S. G.

2012-03-01

Hydrogen is known to damage or degrade piezoelectric materials, at low pressure for ferroelectric random access memory applications, and at high pressure for hydrogen-powered vehicle applications. The piezoelectric degradation is in part governed by the motion of hydrogen species within the piezoelectric materials. We present here quasi-elastic neutron scattering (QENS) measurements of the local hydrogen species motion within lead zirconate titanate (PZT) and barium titanate (BTO) on samples charged by exposure to high-pressure gaseous hydrogen (≈17 MPa). Neutron vibrational spectroscopy (NVS) studies of the hydrogen-enhanced vibrational modes are presented as well. Results are discussed in the context of theoretically predicted interstitial hydrogen lattice sites and compared to comparable bulk diffusion studies of hydrogen diffusion in lead zirconate titanate.

Large displacement vertical translational actuator based on piezoelectric thin films.

PubMed

Qiu, Zhen; Pulskamp, Jeffrey S; Lin, Xianke; Rhee, Choong-Ho; Wang, Thomas; Polcawich, Ronald G; Oldham, Kenn

2010-07-01

A novel vertical translational microactuator based on thin-film piezoelectric actuation is presented, using a set of four compound bend-up/bend-down unimorphs to produce translational motion of a moving platform or stage. The actuation material is a chemical-solution deposited lead-zirconate-titanate (PZT) thin film. Prototype designs have shown as much as 120 μ m of static displacement, with 80-90 μ m displacements being typical, using four 920 μ m long by 70 μ m legs. Analytical models are presented that accurately describe nonlinear behavior in both static and dynamic operation of prototype stages when the dependence of piezoelectric coefficients on voltage is known. Resonance of the system is observed at a frequency of 200 Hz. The large displacement and high bandwidth of the actuators at low-voltage and low-power levels should make them useful to a variety of optical applications, including endoscopic microscopy.

A fatigue test method for Pb(Zr,Ti)O3 thin films by using MEMS-based self-sensitive piezoelectric microcantilevers

NASA Astrophysics Data System (ADS)

Kobayashi, T.; Maeda, R.; Itoh, T.

2008-11-01

In the present study, we propose a new method for the fatigue test of lead zirconate titanate (PZT) thin films for MEMS devices by using self-sensitive piezoelectric microcantilevers developed in our previous study. We have deposited PZT thin films on SOI wafers and fabricated the microcantilevers through the MEMS microfabrication process. In the self-sensitive piezoelectric microcantilevers, the PZT thin films are separated in order to act as an actuator and a sensor. The fatigue characteristic of the PZT thin films can be evaluated by measuring the output voltage of the sensor as a function of time. When a sine wave of 20 Vpp and a dc bias of 10 V were applied to the PZT thin films for an actuator, the output voltage of the sensor fell down after 107 fatigue cycles. We have also investigated the influence of amplitude of the actuation sine wave and dc bias on the fatigue of the PZT thin films by using the proposed fatigue test method.

Single crystal functional oxides on silicon

PubMed Central

Bakaul, Saidur Rahman; Serrao, Claudy Rayan; Lee, Michelle; Yeung, Chun Wing; Sarker, Asis; Hsu, Shang-Lin; Yadav, Ajay Kumar; Dedon, Liv; You, Long; Khan, Asif Islam; Clarkson, James David; Hu, Chenming; Ramesh, Ramamoorthy; Salahuddin, Sayeef

2016-01-01

Single-crystalline thin films of complex oxides show a rich variety of functional properties such as ferroelectricity, piezoelectricity, ferro and antiferromagnetism and so on that have the potential for completely new electronic applications. Direct synthesis of such oxides on silicon remains challenging because of the fundamental crystal chemistry and mechanical incompatibility of dissimilar interfaces. Here we report integration of thin (down to one unit cell) single crystalline, complex oxide films onto silicon substrates, by epitaxial transfer at room temperature. In a field-effect transistor using a transferred lead zirconate titanate layer as the gate insulator, we demonstrate direct reversible control of the semiconductor channel charge with polarization state. These results represent the realization of long pursued but yet to be demonstrated single-crystal functional oxides on-demand on silicon. PMID:26853112

Development, Characterization and Piezoelectric Fatigue Behavior of Lead-Free Perovskite Piezoelectric Ceramics

NASA Astrophysics Data System (ADS)

Patterson, Eric Andrew

Much recent research has focused on the development lead-free perovskite piezoelectrics as environmentally compatible alternatives to lead zirconate titanate (PZT). Two main categories of lead free perovskite piezoelectric ceramic systems were investigated as potential replacements to lead zirconate titanate (PZT) for actuator devices. First, solid solutions based on Li, Ta, and Sb modified (K0.5Na0.5)NbO3 (KNN) lead-free perovskite systems were created using standard solid state methods. Secondly, Bi-based materials a variety of compositions were explored for (1-x)(Bi 0.5Na0.5)TiO3-xBi(Zn0.5Ti0.5)O 3 (BNT-BZT) and Bi(Zn0.5Ti0.5)O3-(Bi 0.5K0.5)TiO3-(Bi0.5Na0.5)TiO 3 (BZT-BKT-BNT). It was shown that when BNT-BKT is combined with increasing concentrations of Bi(Zn1/2i1/2)O3 (BZT), a transition from normal ferroelectric behavior to a material with large electric field induced strains was observed. The higher BZT containing compositions are characterized by large hysteretic strains(> 0.3%) with no negative strains that might indicate domain switching. This work summarizes and analyzes the fatigue behavior of the new generation of Pb-free piezoelectric materials. In piezoelectric materials, fatigue is observed as a degradation in the electromechanical properties under the application of a bipolar or unipolar cyclic electrical load. In Pb-based materials such as lead zirconate titanate (PZT), fatigue has been studied in great depth for both bulk and thin film applications. In PZT, fatigue can result from microcracking or electrode effects (especially in thin films). Ultimately, however, it is electronic and ionic point defects that are the most influential mechanism. Therefore, this work also analyzes the fatigue characteristics of bulk polycrystalline ceramics of the modified-KNN and BNT-BKT-BZT compositions developed. The defect chemistry that underpins the fatigue behavior will be examined and the results will be compared to the existing body of work on PZT. It will be demonstrated that while some Pb-free materials show severe property degradation under cyclic loading, other materials such as BNT-BKT-BZT essentially exhibit fatigue- free piezoelectric properties with chemical doping or other modifications. Based on these results, these new Pb-free materials have great potential for use in piezoelectric applications requiring a large number of drive cycles such as MEMS devices or high frequency actuators.

Effect of dead layer and strain on diffuse phase transition of PLZT relaxor thin films.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tong, S.; Narayanan, M.; Ma, B.

2011-02-01

Bulk relaxor ferroelectrics exhibit excellent permittivity compared to their thin film counterpart, although both show diffuse phase transition (DPT) behavior unlike normal ferroelectrics. To better understand the effect of dead layer and strain on the observed anomaly in the dielectric properties, we have developed relaxor PLZT (lead lanthanum zirconate titanate) thin films with different thicknesses and measured their dielectric properties as a function of temperature and frequency. The effect of dead layer on thin film permittivity has been found to be independent of temperature and frequency, and is governed by the Schottky barrier between the platinum electrode and PLZT. Themore » total strain (thermal and intrinsic) in the film majorly determines the broadening, dielectric peak and temperature shift in the relaxor ferroelectric. The Curie-Weiss type law for relaxors has been further modified to incorporate these two effects to accurately predict the DPT behavior of thin film and bulk relaxor ferroelectrics. The dielectric behavior of thin film is predicted by using the bulk dielectric data from literature in the proposed equation, which agree well with the measured dielectric behavior.« less

Dielectric properties of rare earth (Sm and La) substituted lead zirconate titanate (PZT) ceramics

NASA Astrophysics Data System (ADS)

Dipti, Singh, Sangeeta; Juneja, J. K.; Raina, K. K.; Prakash, Chandra

2013-06-01

In the present paper, we are reporting the studies on dielectric properties of Lanthanum (La) and Samarium (Sm) substituted Lead Zirconate Titanate with compositional formula Pb(1.02-x)SmxZr0.55Ti0.45O3 and Pb(1.02-x)LaxZr0.55Ti0.45O3 with x = 0.00, 0.01, 0.02, 0.03. The materials were synthesized by solid state reaction route. XRD analysis shows that all the samples be in single phase with tetragonal structure. Dielectric properties were studied as a function of temperature.

Investigation of the effect of temperature on aging behavior of Fe-doped lead zirconate titanate

NASA Astrophysics Data System (ADS)

Promsawat, Napatporn; Promsawat, Methee; Janphuang, Pattanaphong; Marungsri, Boonruang; Luo, Zhenhua; Pojprapai, Soodkhet

The aging degradation behavior of Fe-doped Lead zirconate titanate (PZT) subjected to different heat-treated temperatures was investigated over 1000h. The aging degradation in the piezoelectric properties of PZT was indicated by the decrease in piezoelectric charge coefficient, electric field-induced strain and remanent polarization. It was found that the aging degradation became more pronounced at temperature above 50% of the PZT’s Curie temperature. A mathematical model based on the linear logarithmic stretched exponential function was applied to explain the aging behavior. A qualitative aging model based on polar macrodomain switchability was proposed.

Chemical Synthesis of Porous Barium Titanate Thin Film and Thermal Stabilization of Ferroelectric Phase by Porosity-Induced Strain.

PubMed

Suzuki, Norihiro; Osada, Minoru; Billah, Motasim; Bando, Yoshio; Yamauchi, Yusuke; Hossain, Shahriar A

2018-03-27

Barium titanate (BaTiO3, hereafter BT) is an established ferroelectric material first discovered in the 1940s and still widely used because of its well-balanced ferroelectricity, piezoelectricity, and dielectric constant. In addition, BT does not contain any toxic elements. Therefore, it is considered to be an eco-friendly material, which has attracted considerable interest as a replacement for lead zirconate titanate (PZT). However, bulk BT loses its ferroelectricity at approximately 130 °C, thus, it cannot be used at high temperatures. Because of the growing demand for high-temperature ferroelectric materials, it is important to enhance the thermal stability of ferroelectricity in BT. In previous studies, strain originating from the lattice mismatch at hetero-interfaces has been used. However, the sample preparation in this approach requires complicated and expensive physical processes, which are undesirable for practical applications. In this study, we propose a chemical synthesis of a porous material as an alternative means of introducing strain. We synthesized a porous BT thin film using a surfactant-assisted sol-gel method, in which self-assembled amphipathic surfactant micelles were used as an organic template. Through a series of studies, we clarified that the introduction of pores had a similar effect on distorting the BT crystal lattice, to that of a hetero-interface, leading to the enhancement and stabilization of ferroelectricity. Owing to its simplicity and cost effectiveness, this fabrication process has considerable advantages over conventional methods.

Chemical Synthesis of Porous Barium Titanate Thin Film and Thermal Stabilization of Ferroelectric Phase by Porosity-Induced Strain

PubMed Central

Suzuki, Norihiro; Osada, Minoru; Billah, Motasim; Bando, Yoshio; Yamauchi, Yusuke; Hossain, Shahriar A.

2018-01-01

Barium titanate (BaTiO3, hereafter BT) is an established ferroelectric material first discovered in the 1940s and still widely used because of its well-balanced ferroelectricity, piezoelectricity, and dielectric constant. In addition, BT does not contain any toxic elements. Therefore, it is considered to be an eco-friendly material, which has attracted considerable interest as a replacement for lead zirconate titanate (PZT). However, bulk BT loses its ferroelectricity at approximately 130 °C, thus, it cannot be used at high temperatures. Because of the growing demand for high-temperature ferroelectric materials, it is important to enhance the thermal stability of ferroelectricity in BT. In previous studies, strain originating from the lattice mismatch at hetero-interfaces has been used. However, the sample preparation in this approach requires complicated and expensive physical processes, which are undesirable for practical applications. In this study, we propose a chemical synthesis of a porous material as an alternative means of introducing strain. We synthesized a porous BT thin film using a surfactant-assisted sol-gel method, in which self-assembled amphipathic surfactant micelles were used as an organic template. Through a series of studies, we clarified that the introduction of pores had a similar effect on distorting the BT crystal lattice, to that of a hetero-interface, leading to the enhancement and stabilization of ferroelectricity. Owing to its simplicity and cost effectiveness, this fabrication process has considerable advantages over conventional methods. PMID:29658917

Compact piezoelectric micromotor with a single bulk lead zirconate titanate stator

NASA Astrophysics Data System (ADS)

Yan, Liang; Lan, Hua; Jiao, Zongxia; Chen, Chin-Yin; Chen, I.-Ming

2013-04-01

The advance of micro/nanotechnology promotes the development of micromotors in recent years. In this article, a compact piezoelectric ultrasonic micromotor with a single bulk lead zirconate titanate stator is proposed. A traveling wave is generated by superposition of bending modes with 90° phase difference excited by d15 inverse piezoelectric effects. The operating principle simplifies the system structure significantly, and provides a miniaturization solution. A research prototype with the size of 0.75× 0.75×1.55 mm is developed. It can produce start-up torque of 0.27μNmand maximum speed of 2760 r/min at 14RMS.

PZT Thin Film Piezoelectric Traveling Wave Motor

NASA Technical Reports Server (NTRS)

Shen, Dexin; Zhang, Baoan; Yang, Genqing; Jiao, Jiwei; Lu, Jianguo; Wang, Weiyuan

1995-01-01

With the development of micro-electro-mechanical systems (MEMS), its various applications are attracting more and more attention. Among MEMS, micro motors, electrostatic and electromagnetic, are the typical and important ones. As an alternative approach, the piezoelectric traveling wave micro motor, based on thin film material and integrated circuit technologies, circumvents many of the drawbacks of the above mentioned two types of motors and displays distinct advantages. In this paper we report on a lead-zirconate-titanate (PZT) piezoelectric thin film traveling wave motor. The PZT film with a thickness of 150 micrometers and a diameter of 8 mm was first deposited onto a metal substrate as the stator material. Then, eight sections were patterned to form the stator electrodes. The rotor had an 8 kHz frequency power supply. The rotation speed of the motor is 100 rpm. The relationship of the friction between the stator and the rotor and the structure of the rotor on rotation were also studied.

A battery-less photo-detector enabled with simultaneous ferroelectric sensing and energy harnessing mechanism

NASA Astrophysics Data System (ADS)

Lai, Szu Cheng; Yao, Kui; Chen, Yi Fan

2013-08-01

A self-sustainable mechanism for simultaneously sensing and harnessing photon energy was proposed and implemented to create a battery-less and wire-less ultraviolet sensor made of ferroelectric lead lanthanum zirconate titanate thin film with in-plane polarization configuration. The mechanism involved accumulating and storing the photovoltaic charge, and transferring the stored charge via a piezoelectric switch to a radio frequency transmitter. The time-interval between the radio frequency pulses generated by the transmitter was inversely proportional to the photo-intensity. The sustainability of the operation was ascribed to the low leakage, high photovoltage, and linear current-voltage characteristics of ferroelectric sensing material instead of semiconductors.

Subtractive fabrication of ferroelectric thin films with precisely controlled thickness

NASA Astrophysics Data System (ADS)

Ievlev, Anton V.; Chyasnavichyus, Marius; Leonard, Donovan N.; Agar, Joshua C.; Velarde, Gabriel A.; Martin, Lane W.; Kalinin, Sergei V.; Maksymovych, Petro; Ovchinnikova, Olga S.

2018-04-01

The ability to control thin-film growth has led to advances in our understanding of fundamental physics as well as to the emergence of novel technologies. However, common thin-film growth techniques introduce a number of limitations related to the concentration of defects on film interfaces and surfaces that limit the scope of systems that can be produced and studied experimentally. Here, we developed an ion-beam based subtractive fabrication process that enables creation and modification of thin films with pre-defined thicknesses. To accomplish this we transformed a multimodal imaging platform that combines time-of-flight secondary ion mass spectrometry with atomic force microscopy to a unique fabrication tool that allows for precise sputtering of the nanometer-thin layers of material. To demonstrate fabrication of thin-films with in situ feedback and control on film thickness and functionality we systematically studied thickness dependence of ferroelectric switching of lead-zirconate-titanate, within a single epitaxial film. Our results demonstrate that through a subtractive film fabrication process we can control the piezoelectric response as a function of film thickness as well as improve on the overall piezoelectric response versus an untreated film.

Subtractive fabrication of ferroelectric thin films with precisely controlled thickness.

PubMed

Ievlev, Anton V; Chyasnavichyus, Marius; Leonard, Donovan N; Agar, Joshua C; Velarde, Gabriel A; Martin, Lane W; Kalinin, Sergei V; Maksymovych, Petro; Ovchinnikova, Olga S

2018-04-02

The ability to control thin-film growth has led to advances in our understanding of fundamental physics as well as to the emergence of novel technologies. However, common thin-film growth techniques introduce a number of limitations related to the concentration of defects on film interfaces and surfaces that limit the scope of systems that can be produced and studied experimentally. Here, we developed an ion-beam based subtractive fabrication process that enables creation and modification of thin films with pre-defined thicknesses. To accomplish this we transformed a multimodal imaging platform that combines time-of-flight secondary ion mass spectrometry with atomic force microscopy to a unique fabrication tool that allows for precise sputtering of the nanometer-thin layers of material. To demonstrate fabrication of thin-films with in situ feedback and control on film thickness and functionality we systematically studied thickness dependence of ferroelectric switching of lead-zirconate-titanate, within a single epitaxial film. Our results demonstrate that through a subtractive film fabrication process we can control the piezoelectric response as a function of film thickness as well as improve on the overall piezoelectric response versus an untreated film.

Subtractive fabrication of ferroelectric thin films with precisely controlled thickness

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ievlev, Anton; Chyasnavichyus, Marius; Leonard, Donovan N.

The ability to control thin-film growth has led to advances in our understanding of fundamental physics as well as to the emergence of novel technologies. However, common thin-film growth techniques introduce a number of limitations related to the concentration of defects on film interfaces and surfaces that limit the scope of systems that can be produced and studied experimentally. Here, we developed an ion-beam based subtractive fabrication process that enables creation and modification of thin films with pre-defined thicknesses. To accomplish this we transformed a multimodal imaging platform that combines time-of-flight secondary ion mass spectrometry with atomic force microscopy tomore » a unique fabrication tool that allows for precise sputtering of the nanometer-thin layers of material. To demonstrate fabrication of thin-films with in situ feedback and control on film thickness and functionality we systematically studied thickness dependence of ferroelectric switching of lead-zirconate-titanate, within a single epitaxial film. Lastly, our results demonstrate that through a subtractive film fabrication process we can control the piezoelectric response as a function of film thickness as well as improve on the overall piezoelectric response versus an untreated film.« less

Subtractive fabrication of ferroelectric thin films with precisely controlled thickness

DOE PAGES

Ievlev, Anton; Chyasnavichyus, Marius; Leonard, Donovan N.; ...

2018-02-22

The ability to control thin-film growth has led to advances in our understanding of fundamental physics as well as to the emergence of novel technologies. However, common thin-film growth techniques introduce a number of limitations related to the concentration of defects on film interfaces and surfaces that limit the scope of systems that can be produced and studied experimentally. Here, we developed an ion-beam based subtractive fabrication process that enables creation and modification of thin films with pre-defined thicknesses. To accomplish this we transformed a multimodal imaging platform that combines time-of-flight secondary ion mass spectrometry with atomic force microscopy tomore » a unique fabrication tool that allows for precise sputtering of the nanometer-thin layers of material. To demonstrate fabrication of thin-films with in situ feedback and control on film thickness and functionality we systematically studied thickness dependence of ferroelectric switching of lead-zirconate-titanate, within a single epitaxial film. Lastly, our results demonstrate that through a subtractive film fabrication process we can control the piezoelectric response as a function of film thickness as well as improve on the overall piezoelectric response versus an untreated film.« less

Measurement and modeling of dielectric properties of Pb(Zr,Ti)O3 ferroelectric thin films.

PubMed

Renoud, Raphaël; Borderon, Caroline; Gundel, Hartmut W

2011-09-01

In this study, the real and imaginary parts of the complex permittivity of lead zirconate titanate ferroelectric thin films are studied in the frequency range of 100 Hz to 100 MHz. The permittivity is well fitted by the Cole-Cole model. The variation of the relaxation time with the temperature is described by the Arrhenius law and an activation energy of 0.38 eV is found. Because of its nonlinear character, the dielectric response of the ferroelectric sample depends on the amplitude of the applied ac electric field. The permittivity is composed of three different contributions: the first is due to intrinsic lattice, the second is due to domain wall vibrations, and the third is due to domain wall jumps between pinning centers. This last contribution depends on the electric field, so it is important to control the field amplitude to obtain the desired values of permittivity and tunability.

Novel Electrically Tunable Microwave Solenoid Inductor and Compact Phase Shifter Utilizing Permaloy and PZT Thin Films

DOE PAGES

Wang, Tengxing; Jiang, Wei; Divan, Ralu; ...

2017-08-03

A Permalloy (Py) thin film enabled tunable 3-D solenoid inductor is designed and fabricated. The special configuration of magnetic core is discussed and by selectively patterning Py thin film, the proposed tunable inductor can work at frequency up to several GHz range. The inductance of the solenoid inductor can be electrically tuned by dc current and the tunability is above 10%. Utilizing the implemented Py enabled tunable solenoid inductor and Lead Zirconate Titanate (PZT) thin film enabled metal-insulator-metal (MIM) capacitor, a compact fully electrically tunable lumped elements phase shifter is achieved. The tunable phase shifter has both inductive and capacitivemore » tunability and the dual tunability significantly improves the tuning range and design flexibility. Moreover, the dual tunability is able to retain the equivalent characteristic impedance of the device in the process of the phase being tuned. Here, the phase of the device can be tuned by fully electrical methods and when dc current and dc voltage are provided, the length normalized phase tunability is up to 210°/cm« less

Thin-film decoupling capacitors for multi-chip modules

NASA Astrophysics Data System (ADS)

Dimos, D.; Lockwood, S. J.; Schwartz, R. W.; Rogers, M. S.

Thin-film decoupling capacitors based on ferroelectric lead lanthanum zirconate titanate (PLZT) films are being developed for use in advanced packages, such as multi-chip modules. These thin-film decoupling capacitors are intended to replace multi-layer ceramic capacitors for certain applications, since they can be more fully integrated into the packaging architecture. The increased integration that can be achieved should lead to decreased package volume and improved high-speed performance, due to a decrease in interconnect inductance. PLZT films are fabricated by spin coating using metal carboxylate/alkoxide solutions. These films exhibit very high dielectric constants ((var epsilon) greater than or equal to 900), low dielectric losses (tan(delta) = 0.01), excellent insulation resistances (rho greater than 10(exp 13) (Omega)-cm at 125 C), and good breakdown field strengths (E(sub B) = 900 kV/cm). For integrated circuit applications, the PLZT dielectric is less than 1 micron thick, which results in a large capacitance/area (8-9 nF/sq mm). The thin-film geometry and processing conditions also make these capacitors suitable for direct incorporation onto integrated circuits and for packages that require embedded components.

Anisotropy of domain switching in prepoled lead titanate zirconate ceramics under multiaxial electrical loading

NASA Astrophysics Data System (ADS)

Liu, Yuan-Ming; Li, Fa-Xin; Fang, Dai-Ning

2007-01-01

The authors report an observation of anisotropic domain switching process in prepoled lead titanate zirconate (PZT) ceramics under multiaxial electrical loading. Prepoled PZT blocks were obliquely cut to apply an electric field at discrete angles θ (0°-180°) to the initial poling direction. Both the coercive field and switchable polarization are found to decrease significantly when sinθ increases from zero to unity. The measured strain curves show that most domains that accomplished 180° domain switching actually experienced two successive 90° switching. The oriented domain texture after poling plus the induced nonuniform stress are used to explain the observed domain switching anisotropy.

Structural contribution to the ferroelectric fatigue in lead zirconate titanate ceramics

NASA Astrophysics Data System (ADS)

Hinterstein, M.; Rouquette, J.; Haines, J.; Papet, Ph.; Glaum, J.; Knapp, M.; Eckert, J.; Hoffman, M.

2014-09-01

Many ferroelectric devices are based on doped lead zirconate titanate (PZT) ceramics with compositions near the morphotropic phase boundary (MPB), at which the relevant material's properties approach their maximum. Based on a synchrotron x-ray diffraction study of MPB PZT, bulk fatigue is unambiguously found to arise from a less effective field induced tetragonal-to-monoclinic transformation, at which the degradation of the polarization flipping is detected by a less intense and more diffuse anomaly in the atomic displacement parameter of lead. The time dependence of the ferroelectric response on a structural level down to 250 μs confirms this interpretation in the time scale of the piezolectric strain response.

Degradation of lead-zirconate-titanate ceramics under different dc loads

NASA Astrophysics Data System (ADS)

Balke, Nina; Granzow, Torsten; Rödel, Jürgen

2009-05-01

During poling and application in actuators, piezoelectric ceramics like lead-zirconate-titanate are exposed to static or cyclically varying electric fields, often leading to pronounced changes in the electromechanical properties. These fatigue phenomena depend on time, peak electric load, and temperature. Although this process impacts the performance of many actuator materials, its physical understanding remains elusive. This paper proposes a set of key experiments to systematically investigate the changes in the ferroelectric hysteresis, field-dependent relative permittivity, and piezoelectric coefficient after submitting the material to dc loads of varying amplitude and duration. The observed effects are explained based on a model of domain stabilization due to charge accumulation at domain boundaries.

An optimized one-step wet etching process of Pb(Zr0.52Ti0.48)O3 thin films for microelectromechanical system applications

NASA Astrophysics Data System (ADS)

Che, L.; Halvorsen, E.; Chen, X.

2011-10-01

The existence of insoluble residues as intermediate products produced during the wet etching process is the main quality-reducing and structure-patterning issue for lead zirconate titanate (PZT) thin films. A one-step wet etching process using the solutions of buffered HF (BHF) and HNO3 acid was developed for patterning PZT thin films for microelectomechanical system (MEMS) applications. PZT thin films with 1 µm thickness were prepared on the Pt/Ti/SiO2/Si substrate by the sol-gel process for compatibility with Si micromachining. Various compositions of the etchant were investigated and the patterns were examined to optimize the etching process. The optimal result is demonstrated by a high etch rate (3.3 µm min-1) and low undercutting (1.1: 1). The patterned PZT thin film exhibits a remnant polarization of 24 µC cm-2, a coercive field of 53 kV cm-1, a leakage current density of 4.7 × 10-8 A cm-2 at 320 kV cm-1 and a dielectric constant of 1100 at 1 KHz.

Fabrication of ultrathin film capacitors by chemical solution deposition

DOE PAGES

Brennecka, Geoff L.; Tuttle, Bruce A.

2007-10-01

We present that a facile solution-based processing route using standard spin-coating deposition techniques has been developed for the production of reliable capacitors based on lead lanthanum zirconate titanate (PLZT) with active areas of ≥1 mm 2 and dielectric layer thicknesses down to 50 nm. With careful control of the dielectric phase development through improved processing, ultrathin capacitors exhibited slim ferroelectric hysteresis loops and dielectric constants of >1000, similar to those of much thicker films. Furthermore, it has been demonstrated that chemical solution deposition is a viable route to the production of capacitor films which are as thin as 50 nmmore » but are still macroscopically addressable with specific capacitance values >160 nF/mm 2.« less

High-frequency, transient magnetic susceptibility of ferroelectrics

NASA Astrophysics Data System (ADS)

Grimes, Craig A.

1996-10-01

A significant high-frequency magnetic susceptibility was measured both in weakly polarized and nonpolarized samples of barium titanate, lead zirconate titanate, and carnauba wax. Magnetic susceptibility measurements were made from 10 to 500 MHz using a thin film permeameter at room temperature; initial susceptibilities ranged from 0.1 to 2.5. These values are larger than expected for paramagnets and smaller than expected for ferromagnets. It was found that the magnetic susceptibility decreases rapidly with exposure to the exciting field. The origin of the magnetic susceptibility is thought to originate with the applied time varying electric field associated with the susceptibility measurements. An electric field acts to rotate an electric dipole, creating a magnetic quadrupole if the two moments are balanced, and a net magnetic dipole moment if imbalanced. It is thought that local electrostatic fields created at ferroelectric domain discontinuities associated with grain boundaries create an imbalance in the anion rotation that results in a net, measurable, magnetic moment. The origin of the magnetic aftereffect may be due to the local heating of the material through the moving charges associated with the magnetic moment.

Comparison of the Thermal Degradation of Heavily Nb-Doped and Normal PZT Thin Films.

PubMed

Yang, Jeong-Suong; Kang, YunSung; Kang, Inyoung; Lim, SeungMo; Shin, Seung-Joo; Lee, JungWon; Hur, Kang Heon

2017-03-01

The degradation of niobium-doped lead zirconate titanate (PZT) and two types of PZT thin films were investigated. Undoped PZT, two-step PZT, and heavily Nb-doped PZT (PNZT) around the morphotropic phase boundary were in situ deposited under optimum condition by RF-magnetron sputtering. All 2- [Formula: see text]-thick films had dense perovskite columnar grain structure and self-polarized (100) dominant orientation. PZT thin films were deposited on Pt/TiO x bottom electrode on Si wafer, and PNZT thin film was on Ir/TiW electrode with the help of orientation control. Sputtered PZT films formed on microelectromechanical system (MEMS) gyroscope and the degradation rates were compared at different temperatures. PNZT showed the best resistance to the thermal degradation, followed by two-step PZT. To clarify the effect of oxygen vacancies on the degradation of the film at high temperature, photoluminescence measurement was conducted, which confirmed that oxygen vacancy rate was the lowest in heavy PNZT. Nb-doping PZT thin films suppressed the oxygen deficit and made high imprint with self-polarization. This defect distribution and high internal field allowed PNZT thin film to make the piezoelectric sensors more stable and reliable at high temperature, such as reflow process of MEMS packaging.

Multi-photon vertical cross-sectional imaging with a dynamically-balanced thin-film PZT z-axis microactuator.

PubMed

Choi, Jongsoo; Duan, Xiyu; Li, Haijun; Wang, Thomas D; Oldham, Kenn R

2017-10-01

Use of a thin-film piezoelectric microactuator for axial scanning during multi-photon vertical cross-sectional imaging is described. The actuator uses thin-film lead-zirconate-titanate (PZT) to generate upward displacement of a central mirror platform, micro-machined from a silicon-on-insulator (SOI) wafer to dimensions compatible with endoscopic imaging instruments. Device modeling in this paper focuses on existence of frequencies near device resonance producing vertical motion with minimal off-axis tilt even in the presence of multiple vibration modes and non-uniformity in fabrication outcomes. Operation near rear resonance permits large stroke lengths at low voltages relative to other vertical microactuators. Highly uniform vertical motion of the mirror platform is a key requirement for vertical cross-sectional imaging in the remote scan architecture being used for multi-photon instrument prototyping. The stage is installed in a benchtop testbed in combination with an electrostatic mirror that performs in-plane scanning. Vertical sectional images are acquired from 15 μm diameter beads and excised mouse colon tissue.

Active micromixer for microfluidic systems using lead-zirconate-titanate (PZT)-generated ultrasonic vibration.

PubMed

Yang, Z; Goto, H; Matsumoto, M; Maeda, R

2000-01-01

A micromixer using direct ultrasonic vibration is first reported in this paper. The ultrasonic vibration was induced by a bulk lead-zirconate-titanate (PZT; 5 x 4 x 0.2 mm), which was excited by a 48 kHz square wave at 150 V (peak-to-peak). Liquids were mixed in a chamber (6 x 6 x 0.06 mm) with an oscillating diaphragm driven by the PZT. The oscillating diaphragm was in the size of 6 x 6 x 0.15 mm. Ethanol and water were used to test the mixing effectiveness. The laminar flows of ethanol (115 microL/min) and water (100 microL/min) were mixed effectively when the PZT was excited. The entire process was recorded using a video camera.

Lead zirconate titanate-nickel zink ferrite thick-film composites: obtaining by the screen printing technique and magnetoelectric properties

NASA Astrophysics Data System (ADS)

Bush, A. A.; Shkuratov, V. Ya.; Chernykh, I. A.; Fetisov, Y. K.

2010-03-01

Layered thick-film composites containing one lead zirconate titanate (PZT) layer, one nickel zinc ferrite (NZF) layer, two PZT-NZF layers, or three PZT-NZF-PZT layers each 40-50 μm thick are prepared. The layers are applied by screen printing on a ceramic aluminum oxide substrate with a preformed contact (conducting) layer. The dielectric properties of the composites are studied in the temperature interval 80-900 K and the frequency interval 25 Hz-1 MHz. Polarized samples exhibit piezoelectric, pyroelectric, and magnetoelectric effects. In tangentially magnetized two- and three-layer composites, the magnetoelectric conversion factor equals 57 kV/(m T) at low frequencies and reaches 2000 kV/(m T) at the mechanical resonance frequency.

Investigation of fatigue behavior of Pb(Zr0.45Ti0.55)O3 thin films under asymmetric polarization switching

NASA Astrophysics Data System (ADS)

Zhu, Hui; Chen, Yueyuan; Chu, Daping; Feng, Shiwei; Zhang, Yingqiao; Wang, Pengfei

2016-09-01

The fatigue of lead zirconate titanate (PZT) thin films was measured under repetitive switching using asymmetric square waves. The remnant polarization and coercive voltage were found to present regular changes in the initial 10 s, independent of the asymmetry or frequency of switching waves. We attributed the change to the relaxation of stress in the film and identified a coercive voltage V 0 of 0.6 V for the stress-free film. By comparing the coercive voltage and V 0, we found that a built-in electric field was induced by asymmetric switching, where the direction and magnitude were dependent on the degree of waveform asymmetry. Furthermore, the fatigue speed was suggested to be closely related to the generation rate of oxygen vacancies. It was confirmed by our result that a faster decay of remnant polarization can be obtained by applying square waves with a higher degree of asymmetry or symmetry of square waves with a lower frequency.

Integrating Nano-patterned Ferromagnetic and Ferroelectric Thin Films for Electrically Tunable RF Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Tengxing; Peng, Yujia; Jiang, Wei

Tunable radio frequency (RF) components are pivotal elements in frequency-agile and multifunctional systems. However, there is a technical barrier to achieve miniaturized fully electrically tunable RF components. This paper provides and demonstrates the efficacy of a first unique design methodology in developing fully electrically tunable RF components by integrating ferromagnetic (e.g., Permalloy) and ferroelectric (e.g., Lead Zirconate Titanate: PZT) thin films patterns. Permalloy thin film has been patterned in nanometer scale to improve its ferromagnetic resonance frequency (FMR) for RF applications. Tunable inductors are developed with the utilization of different thickness of Permalloy thin film, which show over 50% incrementmore » in inductance and over 4% in tunability with DC current. More tunability can be achieved with multiple layers of Permalloy thin film and optimized thickness. A fully electrically tunable slow wave RF transmission line with simultaneously variable inductance and capacitance density has been implemented and thoroughly investigated for the first time. Measured results show that a fixed phase shift of 90° can be achieved from 1.5 GHz to 1.85 GHz continuously by applying external DC current from 0 to 200 mA and external DC voltage from 0 to 15 Volts, respectively.« less

Integrating Nano-patterned Ferromagnetic and Ferroelectric Thin Films for Electrically Tunable RF Applications

DOE PAGES

Wang, Tengxing; Peng, Yujia; Jiang, Wei; ...

2016-10-31

Tunable radio frequency (RF) components are pivotal elements in frequency-agile and multifunctional systems. However, there is a technical barrier to achieve miniaturized fully electrically tunable RF components. This paper provides and demonstrates the efficacy of a first unique design methodology in developing fully electrically tunable RF components by integrating ferromagnetic (e.g., Permalloy) and ferroelectric (e.g., Lead Zirconate Titanate: PZT) thin films patterns. Permalloy thin film has been patterned in nanometer scale to improve its ferromagnetic resonance frequency (FMR) for RF applications. Tunable inductors are developed with the utilization of different thickness of Permalloy thin film, which show over 50% incrementmore » in inductance and over 4% in tunability with DC current. More tunability can be achieved with multiple layers of Permalloy thin film and optimized thickness. A fully electrically tunable slow wave RF transmission line with simultaneously variable inductance and capacitance density has been implemented and thoroughly investigated for the first time. Measured results show that a fixed phase shift of 90° can be achieved from 1.5 GHz to 1.85 GHz continuously by applying external DC current from 0 to 200 mA and external DC voltage from 0 to 15 Volts, respectively.« less

Ferroelectric devices using lead zirconate titanate (PZT) nanoparticles.

PubMed

Paik, Young Hun; Kojori, Hossein Shokri; Kim, Sung Jin

2016-02-19

We successfully demonstrate the synthesis of lead zirconate titanate nanoparticles (PZT NPs) and a ferroelectric device using the synthesized PZT NPs. The crystalline structure and the size of the nanocrystals are studied using x-ray diffraction and transmission electron microscopy, respectively. We observe <100 nm of PZT NPs and this result matches dynamic light scattering measurements. A solution-based low-temperature process is used to fabricate PZT NP-based devices on an indium tin oxide substrate. The fabricated ferroelectric devices are characterized using various optical and electrical measurements and we verify ferroelectric properties including ferroelectric hysteresis and the ferroelectric photovoltaic effect. Our approach enables low-temperature solution-based processes that could be used for various applications. To the best of our knowledge, this low-temperature solution processed ferroelectric device using PZT NPs is the first successful demonstration of its kind.

Ferroelectric devices using lead zirconate titanate (PZT) nanoparticles

NASA Astrophysics Data System (ADS)

Paik, Young Hun; Shokri Kojori, Hossein; Kim, Sung Jin

2016-02-01

We successfully demonstrate the synthesis of lead zirconate titanate nanoparticles (PZT NPs) and a ferroelectric device using the synthesized PZT NPs. The crystalline structure and the size of the nanocrystals are studied using x-ray diffraction and transmission electron microscopy, respectively. We observe <100 nm of PZT NPs and this result matches dynamic light scattering measurements. A solution-based low-temperature process is used to fabricate PZT NP-based devices on an indium tin oxide substrate. The fabricated ferroelectric devices are characterized using various optical and electrical measurements and we verify ferroelectric properties including ferroelectric hysteresis and the ferroelectric photovoltaic effect. Our approach enables low-temperature solution-based processes that could be used for various applications. To the best of our knowledge, this low-temperature solution processed ferroelectric device using PZT NPs is the first successful demonstration of its kind.

Piezoelectric and dielectric performance of poled lead zirconate titanate subjected to electric cyclic fatigue

NASA Astrophysics Data System (ADS)

Wang, Hong; Matsunaga, Tadashi; Lin, Hua-Tay; Mottern, Alexander M.

2012-02-01

Poled lead zirconate titanate (PZT) material as a single-layer plate was tested using a piezodilatometer under electric cyclic loading in both unipolar and bipolar modes. Its responses were evaluated using unipolar and bipolar measurements on the same setup. The mechanical strain and charge density loops exhibited various variations when the material was cycled for more than 108 cycles. The various quantities including loop amplitude, hysteresis, switchable polarization, and coercive field were characterized accordingly under the corresponding measurement conditions. At the same time, the offset polarization and bias electric field of the material were observed to be changed and the trend was found to be related to the measurement conditions also. Finally, the piezoelectric and dielectric coefficients were analyzed and their implications for the application of interest have been discussed.

Energy harvesting on highway bridges.

DOT National Transportation Integrated Search

2011-01-01

A concept for harvesting energy from the traffic-induced loadings on a highway bridge using piezoelectric : materials to generate electricity was explored through the prototype stage. A total of sixteen lead-zirconate : titanate (PZT) Type 5A piezoel...

Barium strontium titanate thin film growth with variation of lanthanum dopant compatibility as sensor prototype in the satellite technology

NASA Astrophysics Data System (ADS)

Mulyadi; Wahyuni, Rika; Hardhienata, Hendradi; Irzaman

2018-05-01

Electrical properties of barium strontium titanate thin films were investigated. Three layers of barium strontium titanate thin films have been prepared by chemical solution deposition method and spin coating technique at 8000 rpm rotational speed for 30 seconds and temperature of annealing at 850°C for eight hours with temperature increment of 1.67°C/minute. Materials produced by the process of lanthanum dopant with doping variations of 2%, 4% and 6% above type-p silicon (100) substrates. Film obtained was then carried out the characterization using USB 2000 VIS-NIR and tauc plot method. As a result, the barium strontium titanate thin film has the value of band gap energy of 1.58 eV, 1.92 eV and 2.24 eV respectively. The characterization of electrical properties shows that the band gap value of barium strontium titanate thin film with lanthanum dopant was in the range of semiconductor value. Barium strontium titanate thin films with lanthanum dopant are sensitive to temperature changes, so it potentially to be applied to temperature monitoring on satellite technology.

U-Pb Dating of Unabraded Detrital Zircon Metamorphic Rims in the Nanaimo Basin, British Columbia

NASA Astrophysics Data System (ADS)

Boivin, M. P.; Guest, B.; Matthews, W.

2016-12-01

Thin metamorphic rims on detrital zircons from the Nanaimo Basin in SW British Columbia offer a unique opportunity to further constrain the source of these zircons, helping to resolve the long standing Baja BC controversy. Here we present an analytical approach for dating thin zircon rims and use it to show that zircons from the Nanaimo Basin are most likely derived from metamorphic rocks in southern California. Conventional in-situ laser ablation sample preparation typically requires mounting and polishing zircon grains to expose their core. However, in order to date these thin metamorphic zircon rims a depth-profiling approach on unabraded grains was employed. Zircon grains from the Upper Cretaceous Geoffrey, Spray, and Gabriola formations of the Nanaimo Group exposed on Denman and Hornby Islands (British Columbia) were sorted into five groups based on morphology. The zircons were then mounted on tape along with several grains of a well-characterised zircon reference material to validate the uncertainty of the method. The zircons were then imaged using a Zygo Zescope optical profilometer in order to correct for grain-to-grain variations in elevation relative to mounting medium and ensure consistent laser focus. Backscatter electron images (BSE) were used to further characterised the grains and optimize the location of laser ablation targets. Zircons were ablated using a Resonetics 193 nm excimer laser and uranium and lead isotopic ratios were measured using an Agilent 7700 quadrupole mass spectrometer. A low frequency laser repetition rate extended the data collection period on relatively thin zircon rims. Our results show that metamorphic zircon growth occurred in two main phases at 100 Ma and 77 Ma suggesting two sources of detrital zircons with differing metamorphic histories were present in the catchment area. The timing of metamorphism of the source area for the Nanaimo basin is inconsistent with derivation from sources in the Rocky Mountains (Lemhi sub-basin of the Belt-Purcell basin) and consistent with derivation from Mojave-Sonoran region of southern California and northern Mexico. We speculate that some parts of the detrital zircon population of the Nanaimo basin sediments were likely derived from exhumed bodies of the Pelona, Orocopia and Rand schists.

Effects of crystallization interfaces on irradiated ferroelectric thin films

NASA Astrophysics Data System (ADS)

Brewer, S. J.; Williams, S. C.; Cress, C. D.; Bassiri-Gharb, N.

2017-11-01

This work investigates the role of crystallization interfaces and chemical heterogeneity in the radiation tolerance of chemical solution-deposited lead zirconate titanate (PZT) thin films. Two sets of PZT thin films were fabricated with crystallization performed at (i) every deposited layer or (ii) every three layers. The films were exposed to a range of 60Co gamma radiation doses, between 0.2 and 20 Mrad, and their functional response was compared before and after irradiation. The observed trends indicate enhancements of dielectric, ferroelectric, and piezoelectric responses at low radiation doses and degradation of the same at higher doses. Response enhancements are expected to result from low-dose (≤2 Mrad), ionizing radiation-induced charging of internal interfaces—an effect that results in neutralization of pre-existing internal bias in the samples. At higher radiation doses (>2 Mrad), accumulation and self-ordering of radiation-modified, mobile, oxygen vacancy-related defects contribute to degradation of dielectric, ferroelectric, and piezoelectric properties, exacerbated in the samples with more crystallization layers, potentially due to increased defect accumulation at these internal interfaces. These results suggest that the interaction between radiation and crystallization interfaces is multifaceted—the effects of ionization, domain wall motion, point defect mobility, and microstructure are considered.

Enhanced fatigue and retention in ferroelectric thin film memory capacitors by post-top electrode anneal treatment

NASA Technical Reports Server (NTRS)

Thakoor, Sarita (Inventor)

1992-01-01

Thin film ferroelectric capacitors comprising a ferroelectric film sandwiched between electrodes for nonvolatile memory operations are rendered more stable by subjecting the capacitors to an anneal following deposition of the top electrode. The anneal is done so as to form the interface between the ferroelectric film and the top electrode. Heating in an air oven, laser annealing, or electron bombardment may be used to form the interface. Heating in an air oven is done at a temperature at least equal to the crystallization temperature of the ferroelectric film. Where the ferroelectric film comprises lead zirconate titanate, annealing is done at about 550 to 600 C for about 10 to 15 minutes. The formation treatment reduces the magnitude of charge associated with the nonswitching pulse in the thin film ferroelectric capacitors. Reduction of this charge leads to significantly more stable nonvolatile memory operations in both digital and analog memory devices. The formation treatment also reduces the ratio of change of the charge associated with the nonswitching pulse as a function of retention time. These improved memory devices exhibit greater performance in retention and reduced fatigue in memory arrays.

Enhanced fatigue and retention in ferroelectric thin film memory capacitors by post-top electrode anneal treatment

NASA Technical Reports Server (NTRS)

Thakoor, Sarita (Inventor)

1994-01-01

Thin film ferroelectric capacitors (10) comprising a ferroelectric film (18) sandwiched between electrodes (16 and 20) for nonvolatile memory operations are rendered more stable by subjecting the capacitors to an anneal following deposition of the top electrode (20). The anneal is done so as to form the interface (22) between the ferroelectric film and the top electrode. Heating in an air oven, laser annealing, or electron bombardment may be used to form the interface. Heating in an air oven is done at a temperature at least equal to the crystallization temperature of the ferroelectric film. Where the ferroelectric film comprises lead zirconate titanate, annealing is done at about 550.degree. to 600.degree. C. for about 10 to 15 minutes. The formation treatment reduces the magnitude of charge associated with the non-switching pulse in the thin film ferroelectric capacitors. Reduction of this charge leads to significantly more stable nonvolatile memory operations in both digital and analog memory devices. The formation treatment also reduces the ratio of change of the charge associated with the non-switching pulse as a function of retention time. These improved memory devices exhibit greater performance in retention and reduced fatigue in memory arrays.

Optimizing a spectral element for modeling PZT-induced Lamb wave propagation in thin plates

NASA Astrophysics Data System (ADS)

Ha, Sungwon; Chang, Fu-Kuo

2010-01-01

Use of surface-mounted piezoelectric actuators to generate acoustic ultrasound has been demonstrated to be a key component of built-in nondestructive detection evaluation (NDE) techniques, which can automatically inspect and interrogate damage in hard-to-access areas in real time without disassembly of the structural parts. However, piezoelectric actuators create complex waves, which propagate through the structure. Having the capability to model piezoelectric actuator-induced wave propagation and understanding its physics are essential to developing advanced algorithms for the built-in NDE techniques. Therefore, the objective of this investigation was to develop an efficient hybrid spectral element for modeling piezoelectric actuator-induced high-frequency wave propagation in thin plates. With the hybrid element we take advantage of both a high-order spectral element in the in-plane direction and a linear finite element in the thickness direction in order to efficiently analyze Lamb wave propagation in thin plates. The hybrid spectral element out-performs other elements in terms of leading to significantly faster computation and smaller memory requirements. Use of the hybrid spectral element is proven to be an efficient technique for modeling PZT-induced (PZT: lead zirconate titanate) wave propagation in thin plates. The element enables fundamental understanding of PZT-induced wave propagation.

Lead zirconate titanate nanoscale patterning by ultraviolet-based lithography lift-off technique for nano-electromechanical system applications.

PubMed

Guillon, Samuel; Saya, Daisuke; Mazenq, Laurent; Costecalde, Jean; Rèmiens, Denis; Soyer, Caroline; Nicu, Liviu

2012-09-01

The advantage of using lead zirconate titanate (PbZr(0.54)Ti(0.46)O(3)) ceramics as an active material in nanoelectromechanical systems (NEMS) comes from its relatively high piezoelectric coefficients. However, its integration within a technological process is limited by the difficulty of structuring this material with submicrometer resolution at the wafer scale. In this work, we develop a specific patterning method based on optical lithography coupled with a dual-layer resist process. The main objective is to obtain sub-micrometer features by lifting off a 100-nm-thick PZT layer while preserving the material's piezoelectric properties. A subsequent result of the developed method is the ability to stack several layers with a lateral resolution of few tens of nanometers, which is mandatory for the fabrication of NEMS with integrated actuation and read-out capabilities.

Electromechanical properties of lead zirconate titanate piezoceramics under the influence of mechanical stresses.

PubMed

Zhang, Q M; Zhao, J

1999-01-01

In lead zirconate titanate piezoceramics, external stresses can cause substantial changes in the piezoelectric coefficients, dielectric constant, and elastic compliance due to nonlinear effects and stress depoling effects. In both soft and hard PZT piezoceramics, the aging can produce a memory effect that will facilitate the recovery of the poled state in the ceramics from momentary electric or stress depoling. In hard PZT ceramics, the local defect fields built up during the aging process can stabilize the ceramic against external stress depoling that results in a marked increase in the piezoelectric coefficient and electromechanical coupling factor in the ceramic under the stress. Although soft PZT ceramics can be easily stress depoled (losing piezoelectricity), a DC bias electric field, parallel to the original poling direction, can be employed to maintain the ceramic poling state so that the ceramic can be used at high stresses without depoling.

Reconstruction of the domain orientation distribution function of polycrystalline PZT ceramics using vector piezoresponse force microscopy.

PubMed

Kratzer, Markus; Lasnik, Michael; Röhrig, Sören; Teichert, Christian; Deluca, Marco

2018-01-11

Lead zirconate titanate (PZT) is one of the prominent materials used in polycrystalline piezoelectric devices. Since the ferroelectric domain orientation is the most important parameter affecting the electromechanical performance, analyzing the domain orientation distribution is of great importance for the development and understanding of improved piezoceramic devices. Here, vector piezoresponse force microscopy (vector-PFM) has been applied in order to reconstruct the ferroelectric domain orientation distribution function of polished sections of device-ready polycrystalline lead zirconate titanate (PZT) material. A measurement procedure and a computer program based on the software Mathematica have been developed to automatically evaluate the vector-PFM data for reconstructing the domain orientation function. The method is tested on differently in-plane and out-of-plane poled PZT samples, and the results reveal the expected domain patterns and allow determination of the polarization orientation distribution function at high accuracy.

Electrical fatigue behaviour in lead zirconate titanate: an experimental and theoretical study

NASA Astrophysics Data System (ADS)

Bhattacharyya, Mainak; Arockiarajan, A.

2013-08-01

A systematic investigation on electrical fatigue in lead zirconate titanate (PZT) is carried out for different loading frequencies. Experiments are conducted up to 106 cycles to measure the electrical displacement and longitudinal strain on bulk ceramics in the bipolar mode with large electrical loading conditions. A simplified macroscopic model based on physical mechanisms of domain switching is developed to predict the non-linear behaviour. In this model, the volume fraction of a domain is used as the internal variable by considering the mechanisms of domain nucleation and propagation (domain wall movement). The measured material properties at different fatigue cycles are incorporated into the switching model as damage parameters and the classical strain versus electric field and electric displacement versus electric field curves are simulated. Comparison between the experiments and simulations shows that the proposed model can reproduce the characteristics of non-linear as well as fatigue responses.

Observation of Failure and Domain Switching in Lead Zirconate Titanate Ceramics

NASA Astrophysics Data System (ADS)

Okayasu, Mitsuhiro; Sugiyama, Eriko; Sato, Kazuto; Mizuno, Mamoru

The mechanical and electrical properties (electromechanical coupling coefficient, piezoelectric constant and dielectric constant) of lead zirconate titanate (PZT) ceramics are investigated during mechanical static and cyclic loading. There are several failure characteristics which can alter the material properties of PZT ceramics. The elastic constant increases and electrical properties decrease with increasing the applied load. This is due to the internal strain arising from the domain switching. In this case, 90° domain switching occurs anywhere in the samples as the sample is loaded. It is also apparent that electrogenesis occurs several times during cyclic loading to the final fracture. This occurrence is related to the domain switching. The elastic constant and electrical properties can decrease because of crack generation in the PZT ceramics. Moreover, the elastic constant increases with increase of the mechanical load and decreases with decrease of the load. On the contrary, the opposite sense of change of the electrical properties is observed.

Improvement of fatigue resistance for multilayer lead zirconate titanate (PZT)-based ceramic actuators by external mechanical loads

NASA Astrophysics Data System (ADS)

Yang, Gang; Yue, Zhenxing; Ji, Ye; Chu, Xiangcheng; Li, Longtu

2008-12-01

The influence of external compressive loads, applied along a direction perpendicular to polarization, on fatigue behaviors of multilayer lead zirconate titanate (PZT)-based ceramic actuators was investigated. Under no external mechanical load, a normal fatigue behavior was observed, demonstrating that both switching polarization (Pswitching) and remnant polarization (Pr) progressively decreased with increasing switching cycles due to domain pinning by charge point defects. However, an anomalous enhancement in both switching and remnant polarizations was observed upon application of the external compressive loads. After 5×106 cycles of polarization switching, Pswitching and Pr increase by about 13% and 6% at 40 MPa, respectively, while Pswitching and Pr increase by about 11% and 21% at 60 MPa, respectively. The improvement of fatigue resistance can be attributed to non-180° domain switching and suppression of microcracking, triggered by external mechanical loads.

A smart, intermittent driven particle sensor with an airflow change trigger using a lead zirconate titanate (PZT) cantilever

NASA Astrophysics Data System (ADS)

Takahashi, Hidetoshi; Tomimatsu, Yutaka; Kobayashi, Takeshi; Isozaki, Akihiro; Itoh, Toshihiro; Maeda, Ryutaro; Matsumoto, Kiyoshi; Shimoyama, Isao

2014-02-01

This paper reports on a smart, intermittent driven particle sensor with an airflow trigger. A lead zirconate titanate cantilever functions as the trigger, which detects an airflow change without requiring a power supply to drive the sensing element. Because an airflow change indicates that the particle concentration has changed, the trigger switches the optical particle counter from sleep mode to active mode only when the particle concentration surrounding the sensor changes. The sensor power consumption in sleep mode is 100 times less than that in the active mode. Thus, this intermittent driven method significantly reduces the total power consumption of the particle sensor. In this paper, we fabricate a prototype of the particle sensor and demonstrate that the optical particle counter can be switched on by the fabricated trigger and thus that the particle concentration can be measured.

Effect of the Crystal Structure on the Electrical Properties of Thin-Film PZT Structures

NASA Astrophysics Data System (ADS)

Delimova, L. A.; Gushchina, E. V.; Zaitseva, N. V.; Seregin, D. S.; Vorotilov, K. A.; Sigov, A. S.

2018-03-01

A new method of two-stage crystallization of lead zirconate-titanate (PZT) films using a seed sublayer with a low excess lead content has been proposed and realized. A seed layer with a strong texture of perovskite Pe(111) grains is formed from a solution with a lead excess of 0-5 wt %; the fast growth of the grains is provided by the deposition of the main film from a solution with high lead content. As a result, a strong Pe(111) texture with complete suppression of the Pe(100) orientation forms. An analysis of current-voltage dependences of the transient currents and the distributions of the local conductivity measured by the contact AFM method reveals two various mechanisms of current percolation that are determined by traps in the bulk and at the perovskite grain interfaces.

Correlation of electron backscatter diffraction and piezoresponse force microscopy for the nanoscale characterization of ferroelectric domains in polycrystalline lead zirconate titanate

NASA Astrophysics Data System (ADS)

Burnett, T. L.; Weaver, P. M.; Blackburn, J. F.; Stewart, M.; Cain, M. G.

2010-08-01

The functional properties of ferroelectric ceramic bulk or thin film materials are strongly influenced by their nanostructure, crystallographic orientation, and structural geometry. In this paper, we show how, by combining textural analysis, through electron backscattered diffraction, with piezoresponse force microscopy, quantitative measurements of the piezoelectric properties can be made at a scale of 25 nm, smaller than the domain size. The combined technique is used to obtain data on the domain-resolved effective single crystal piezoelectric response of individual crystallites in Pb(Zr0.4Ti0.6)O3 ceramics. The results offer insight into the science of domain engineering and provide a tool for the future development of new nanostructured ferroelectric materials for memory, nanoactuators, and sensors based on magnetoelectric multiferroics.

Growth and optical property characterization of textured barium titanate thin films for photonic applications

NASA Astrophysics Data System (ADS)

Dicken, Matthew J.; Diest, Kenneth; Park, Young-Bae; Atwater, Harry A.

2007-03-01

We have investigated the growth of barium titanate thin films on bulk crystalline and amorphous substrates utilizing biaxially oriented template layers. Ion beam-assisted deposition was used to grow thin, biaxially textured, magnesium oxide template layers on amorphous and silicon substrates. Growth of highly oriented barium titanate films on these template layers was achieved by molecular beam epitaxy using a layer-by-layer growth process. Barium titanate thin films were grown in molecular oxygen and in the presence of oxygen radicals produced by a 300 W radio frequency plasma. We used X-ray and in situ reflection high-energy electron diffraction (RHEED) to analyze the structural properties and show the predominantly c-oriented grains in the films. Variable angle spectroscopic ellipsometry was used to analyze and compare the optical properties of the thin films grown with and without oxygen plasma. We have shown that optical quality barium titanate thin films, which show bulk crystal-like properties, can be grown on any substrate through the use of biaxially oriented magnesium oxide template layers.

Modified lead titanate thin films for pyroelectric infrared detectors on gold electrodes

NASA Astrophysics Data System (ADS)

Ahmed, Moinuddin; Butler, Donald P.

2015-07-01

Pyroelectric infrared detectors provide the advantage of both a wide spectral response and dynamic range, which also has enabled systems to be developed with reduced size, weight and power consumption. This paper demonstrates the deposition of lead zirconium titanate (PZT) and lead calcium titanate (PCT) thin films for uncooled pyroelectric detectors with the utilization of gold electrodes. The modified lead titanate thin films were deposited by pulsed laser deposition on gold electrodes. The PZT and PCT thins films deposited and annealed at temperatures of 650 °C and 550 °C respectively demonstrated the best pyroelectric performance in this work. The thin films displayed a pyroelectric effect that increased with temperature. Poling of the thin films was carried out for a fixed time periods and fixed dc bias voltages at elevated temperature in order to increase the pyroelectric coefficient by establishing a spontaneous polarization of the thin films. Poling caused the pyroelectric current to increase one order of magnitude.

Potassium Sodium Niobate-Based Lead-Free Piezoelectric Multilayer Ceramics Co-Fired with Nickel Electrodes.

PubMed

Kawada, Shinichiro; Hayashi, Hiroyuki; Ishii, Hideki; Kimura, Masahiko; Ando, Akira; Omiya, Suetake; Kubodera, Noriyuki

2015-11-03

Although lead-free piezoelectric ceramics have been extensively studied, many problems must still be overcome before they are suitable for practical use. One of the main problems is fabricating a multilayer structure, and one solution attracting growing interest is the use of lead-free multilayer piezoelectric ceramics. The paper reviews work that has been done by the authors on lead-free alkali niobate-based multilayer piezoelectric ceramics co-fired with nickel inner electrodes. Nickel inner electrodes have many advantages, such as high electromigration resistance, high interfacial strength with ceramics, and greater cost effectiveness than silver palladium inner electrodes. However, widely used lead zirconate titanate-based ceramics cannot be co-fired with nickel inner electrodes, and silver palladium inner electrodes are usually used for lead zirconate titanate-based piezoelectric ceramics. A possible alternative is lead-free ceramics co-fired with nickel inner electrodes. We have thus been developing lead-free alkali niobate-based multilayer ceramics co-fired with nickel inner electrodes. The normalized electric-field-induced thickness strain ( S max / E max ) of a representative alkali niobate-based multilayer ceramic structure with nickel inner electrodes was 360 pm/V, where S max denotes the maximum strain and E max denotes the maximum electric field. This value is about half that for the lead zirconate titanate-based ceramics that are widely used. However, a comparable value can be obtained by stacking more ceramic layers with smaller thicknesses. In the paper, the compositional design and process used to co-fire lead-free ceramics with nickel inner electrodes are introduced, and their piezoelectric properties and reliabilities are shown. Recent advances are introduced, and future development is discussed.

Potassium Sodium Niobate-Based Lead-Free Piezoelectric Multilayer Ceramics Co-Fired with Nickel Electrodes

PubMed Central

Kawada, Shinichiro; Hayashi, Hiroyuki; Ishii, Hideki; Kimura, Masahiko; Ando, Akira; Omiya, Suetake; Kubodera, Noriyuki

2015-01-01

Although lead-free piezoelectric ceramics have been extensively studied, many problems must still be overcome before they are suitable for practical use. One of the main problems is fabricating a multilayer structure, and one solution attracting growing interest is the use of lead-free multilayer piezoelectric ceramics. The paper reviews work that has been done by the authors on lead-free alkali niobate-based multilayer piezoelectric ceramics co-fired with nickel inner electrodes. Nickel inner electrodes have many advantages, such as high electromigration resistance, high interfacial strength with ceramics, and greater cost effectiveness than silver palladium inner electrodes. However, widely used lead zirconate titanate-based ceramics cannot be co-fired with nickel inner electrodes, and silver palladium inner electrodes are usually used for lead zirconate titanate-based piezoelectric ceramics. A possible alternative is lead-free ceramics co-fired with nickel inner electrodes. We have thus been developing lead-free alkali niobate-based multilayer ceramics co-fired with nickel inner electrodes. The normalized electric-field-induced thickness strain (Smax/Emax) of a representative alkali niobate-based multilayer ceramic structure with nickel inner electrodes was 360 pm/V, where Smax denotes the maximum strain and Emax denotes the maximum electric field. This value is about half that for the lead zirconate titanate-based ceramics that are widely used. However, a comparable value can be obtained by stacking more ceramic layers with smaller thicknesses. In the paper, the compositional design and process used to co-fire lead-free ceramics with nickel inner electrodes are introduced, and their piezoelectric properties and reliabilities are shown. Recent advances are introduced, and future development is discussed. PMID:28793646

A-site stoichiometry and piezoelectric response in thin film PbZr 1-xTi xO 3

DOE PAGES

Marincel, Dan; Jesse, Stephen; Belianinov, Alex; ...

2015-05-29

Lead zirconate titanate (PZT) films with Zr/Ti ratios of 52/48 and 30/70 annealed at varying partial pressures of PbO within the perovskite phase field exhibited permittivities of 1150 and 600, respectively, with loss tangents of 0.02. Many of the functional properties, including the permittivity, piezoelectricity as indicated via the Rayleigh coefficients, and the aging rates were found to be weakly dependent of the lead content in the single phase field. Minor polarization electric field hysteresis loops and piezoelectric coefficient e 31,f values after a hot poling process suggest that the point defect helps stabilize the aligned domain states. Measurements ofmore » the local nonlinear response show an increased low response cluster size with decreasing PbO content, indicating that PbO deficiency acts to reduce domain wall motion where it is already low« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Melo, M.; Araújo, E. B., E-mail: eudes@dfq.feis.unesp.br; Shvartsman, V. V.

Polycrystalline lanthanum lead zirconate titanate (PLZT) thin films were deposited on Pt/TiO{sub 2}/SiO{sub 2}/Si substrates to study the effects of the thickness and grain size on their structural and piezoresponse properties at nanoscale. Thinner PLZT films show a slight (100)-orientation tendency that tends to random orientation for the thicker film, while microstrain and crystallite size increases almost linearly with increasing thickness. Piezoresponse force microscopy and autocorrelation function technique were used to demonstrate the existence of local self-polarization effect and to study the thickness dependence of correlation length. The obtained results ruled out the bulk mechanisms and suggest that Schottky barriersmore » near the film-substrate are likely responsible for a build-in electric field in the films. Larger correlation length evidence that this build-in field increases the number of coexisting polarization directions in larger grains leading to an alignment of macrodomains in thinner films.« less

Growth of epitaxial Pb(Zr,Ti)O3 films by pulsed laser deposition

NASA Astrophysics Data System (ADS)

Lee, J.; Safari, A.; Pfeffer, R. L.

1992-10-01

Lead zirconate titanate (PZT) thin films with a composition near the morphotropic phase boundary have been grown on MgO (100) and Y1Ba2Cu3Ox (YBCO) coated MgO substrates. Substrate temperature and oxygen pressure were varied to achieve ferroelectric films with a perovskite structure. Films grown on MgO had the perovskite structure with an epitaxial relationship with the MgO substrate. On the other hand, films grown on the YBCO/MgO substrate had an oriented structure to the surface normal with a misorientation in the plane parallel to the surface. The measured dielectric constant and loss tangent at 1 kHz were 670 and 0.05, respectively. The remnant polarization and coercive field were 42 μC/cm2 and 53 kV/cm. A large internal bias field (12 kV/cm) was observed in the as-deposited state of the undoped PZT films.

Mapping piezoelectric response in nanomaterials using a dedicated non-destructive scanning probe technique.

PubMed

Calahorra, Yonatan; Smith, Michael; Datta, Anuja; Benisty, Hadas; Kar-Narayan, Sohini

2017-12-14

There has been tremendous interest in piezoelectricity at the nanoscale, for example in nanowires and nanofibers where piezoelectric properties may be enhanced or controllably tuned, thus necessitating robust characterization techniques of piezoelectric response in nanomaterials. Piezo-response force microscopy (PFM) is a well-established scanning probe technique routinely used to image piezoelectric/ferroelectric domains in thin films, however, its applicability to nanoscale objects is limited due to the requirement for physical contact with an atomic force microscope (AFM) tip that may cause dislocation or damage, particularly to soft materials, during scanning. Here we report a non-destructive PFM (ND-PFM) technique wherein the tip is oscillated into "discontinuous" contact during scanning, while applying an AC bias between tip and sample and extracting the piezoelectric response for each contact point by monitoring the resulting localized deformation at the AC frequency. ND-PFM is successfully applied to soft polymeric (poly-l-lactic acid) nanowires, as well as hard ceramic (barium zirconate titanate-barium calcium titanate) nanowires, both previously inaccessible by conventional PFM. Our ND-PFM technique is versatile and compatible with commercial AFMs, and can be used to correlate piezoelectric properties of nanomaterials with their microstructural features thus overcoming key characterisation challenges in the field.

Study of samarium modified lead zirconate titanate and nickel zinc ferrite composite system

NASA Astrophysics Data System (ADS)

Rani, Rekha; Juneja, J. K.; Singh, Sangeeta; Raina, K. K.; Prakash, Chandra

2015-03-01

In the present work, composites of samarium substituted lead zirconate titanate and nickel zinc ferrite with compositional formula 0.95Pb1-3x/2 SmxZr0.65Ti0.35O3-0.05Ni0.8Zn0.2Fe2O4 (x=0, 0.01, 0.02 and 0.03) were prepared by the conventional solid state route. X-ray diffraction analysis was carried out to confirm the coexistence of individual phases. Microstructural study was done by using scanning electron microscope. Dielectric constant and loss were studied as a function of temperature and frequency. To study ferroelectric and magnetic properties of the composite samples, corresponding P-E and M-H hysteresis loops were recorded. Change in magnetic properties of electrically poled composite sample (x=0.02) was studied to confirm the magnetoelectric (ME) coupling. ME coefficient (dE/dH) of the samples (x=0 and 0.02) was measured as a function of DC magnetic field.

Fatigue responses of lead zirconate titanate stacks under semibipolar electric cycling with mechanical preload

NASA Astrophysics Data System (ADS)

Wang, Hong; Cooper, Thomas A.; Lin, Hua-Tay; Wereszczak, Andrew A.

2010-10-01

Lead zirconate titanate (PZT) stacks that had an interdigital internal electrode configuration were tested to more than 108 cycles. A 100 Hz semibipolar sine wave with a field range of +4.5/-0.9 kV/mm was used in cycling with a concurrently-applied 20 MPa preload. Significant reductions in piezoelectric and dielectric responses were observed during the cycling depending on the measuring condition. Extensive partial discharges were also observed. These surface events resulted in the erosion of external electrode and the exposure of internal electrodes. Sections prepared by sequential polishing technique revealed a variety of damage mechanisms including delaminations, pores, and etch grooves. The scale of damage was correlated with the degree of fatigue-induced reduction in piezoelectric and dielectric responses. The results from this study demonstrate the feasibility of using a semibipolar mode to drive a PZT stack under a mechanical preload and illustrate the potential fatigue and damages of the stack in service.

Conformable amplified lead zirconate titanate sensors with enhanced piezoelectric response for cutaneous pressure monitoring.

PubMed

Dagdeviren, Canan; Su, Yewang; Joe, Pauline; Yona, Raissa; Liu, Yuhao; Kim, Yun-Soung; Huang, YongAn; Damadoran, Anoop R; Xia, Jing; Martin, Lane W; Huang, Yonggang; Rogers, John A

2014-08-05

The ability to measure subtle changes in arterial pressure using devices mounted on the skin can be valuable for monitoring vital signs in emergency care, detecting the early onset of cardiovascular disease and continuously assessing health status. Conventional technologies are well suited for use in traditional clinical settings, but cannot be easily adapted for sustained use during daily activities. Here we introduce a conformal device that avoids these limitations. Ultrathin inorganic piezoelectric and semiconductor materials on elastomer substrates enable amplified, low hysteresis measurements of pressure on the skin, with high levels of sensitivity (~0.005 Pa) and fast response times (~0.1 ms). Experimental and theoretical studies reveal enhanced piezoelectric responses in lead zirconate titanate that follow from integration on soft supports as well as engineering behaviours of the associated devices. Calibrated measurements of pressure variations of blood flow in near-surface arteries demonstrate capabilities for measuring radial artery augmentation index and pulse pressure velocity.

Giant actuation strain nearly 0.6% in a periodically orthogonal poled lead titanate zirconate ceramic via reversible domain switching

NASA Astrophysics Data System (ADS)

Li, Faxin; Wang, Qiangzhong; Miao, Hongchen

2017-08-01

The widely used ferroelectric ceramics based actuators always suffer from small output strains (typically ˜0.1%-0.15%). Non-180° domain switching can generate a large strain in ferroelectrics but it is usually irreversible. In this work, we tailored the domain structures in a soft lead titanate zirconate (PZT) ceramic by periodical orthogonal poling. The non-180° switching in this domain-engineered PZT ceramics turns to be reversible, resulting in a local giant actuation strain of nearly 0.6% under a field of 2 kV/mm at 0.1 Hz. The large interfacial stresses between regions with different poling directions during electric loading/unloading were thought to be responsible for the reversible non-180° domain switching. The switching strain drops quickly with the increasing frequency, and stabilized at about 0.2% at or above 1.0 Hz. The large actuation strain remains quite stable after 104 cycles of loading, which is very promising for low-frequency, large-strain actuators.

Lanthanide-Assisted Deposition of Strongly Electro-optic PZT Thin Films on Silicon: Toward Integrated Active Nanophotonic Devices.

PubMed

George, J P; Smet, P F; Botterman, J; Bliznuk, V; Woestenborghs, W; Van Thourhout, D; Neyts, K; Beeckman, J

2015-06-24

The electro-optical properties of lead zirconate titanate (PZT) thin films depend strongly on the quality and crystallographic orientation of the thin films. We demonstrate a novel method to grow highly textured PZT thin films on silicon using the chemical solution deposition (CSD) process. We report the use of ultrathin (5-15 nm) lanthanide (La, Pr, Nd, Sm) based intermediate layers for obtaining preferentially (100) oriented PZT thin films. X-ray diffraction measurements indicate preferentially oriented intermediate Ln2O2CO3 layers providing an excellent lattice match with the PZT thin films grown on top. The XRD and scanning electron microscopy measurements reveal that the annealed layers are dense, uniform, crack-free and highly oriented (>99.8%) without apparent defects or secondary phases. The EDX and HRTEM characterization confirm that the template layers act as an efficient diffusion barrier and form a sharp interface between the substrate and the PZT. The electrical measurements indicate a dielectric constant of ∼650, low dielectric loss of ∼0.02, coercive field of 70 kV/cm, remnant polarization of 25 μC/cm(2), and large breakdown electric field of 1000 kV/cm. Finally, the effective electro-optic coefficients of the films are estimated with a spectroscopic ellipsometer measurement, considering the electric field induced variations in the phase reflectance ratio. The electro-optic measurements reveal excellent linear effective pockels coefficients of 110 to 240 pm/V, which makes the CSD deposited PZT thin film an ideal candidate for Si-based active integrated nanophotonic devices.

A Further Investigation of the Exceptional Zircon Aggregate in Lunar Thin Section 73235,82

NASA Technical Reports Server (NTRS)

Pidgeon, R. T.; Nemchin, a. A.; Meyer, C.

2005-01-01

Introduction: Smith et al. described an exceptional zircon assemblage in thin section 82 from lunar breccia 73235 which, in transmitted light, resembles a cluster of pomegranate seeds, situated in a clast dominated by bytownite (Fig.1). They reported that high-contrast back-scattered electron (BSE) images of the zircon assemblage clearly show an overgrowth around most of the crystals. Most significantly these authors reported that the age of the rims of ca 4.18Ga is 120 million years younger than age of the interiors, dated at ca 4.31Ga. Smith et al. concluded that ca 4.31 billion years ago a relatively large (500+micron) zircon crystallized within a clast of Ca rich plagioclase. The zircon was fractured into numerous smaller crystals and was subsequently overgrown by a second generation of zircon at approximately 4.18Ga.

Guided-Wave Testing of Trunnion Rods at Greenup Lock and Dam, Kentucky

DTIC Science & Technology

2014-04-01

fatigue cracks which go through opening and closing periods during their progression, microcracks in post-tension trunnion anchor rods are believed to be...produce undesired interference effects. A new 1.5 in. diameter, medium-damped lead zirconate titanate ( PZT ), ceramic-based crystal (i.e., an Accuscan

Bi-axial Vibration Energy Harvesting

DTIC Science & Technology

2012-07-01

included early dedicated portable signal averaging equipment, Nomad, CT4 and F18 fatigue test control systems and some field trials. Currently he is...and repairs to acoustically- fatigued structures. ____________________ ________________________________________________ UNCLASSIFIED...Physicists at the Tokyo Institute of Technology investigated various piezoceramic materials [20], developing lead zirconate titanate ( PZT ) in around 1952

Accounting for the various contributions to pyroelectricity in lead zirconate titanate thin films

NASA Astrophysics Data System (ADS)

Hanrahan, B.; Espinal, Y.; Neville, C.; Rudy, R.; Rivas, M.; Smith, A.; Kesim, M. T.; Alpay, S. P.

2018-03-01

An understanding of the pyroelectric coefficient and particularly its relationship with the applied electric field is critical to predicting the device performance for infrared imaging, energy harvesting, and solid-state cooling devices. In this work, we compare direct measurements of the pyroelectric effect under pulsed heating to the indirect extraction of the pyroelectric coefficient from adiabatic hysteresis loops and predictions from Landau-Devonshire theory for PbZr0.52Ti0.48O3 (PZT 52/48) on platinized silicon substrates. The differences between these measurements are explained through a series of careful measurements that quantify the magnitude and direction of the secondary and field-induced pyroelectric effects. The indirect measurement is shown to be up to 25% of the direct measurement at high fields, while the direct measurements and theoretical predictions converge at high fields as the film approaches a mono-domain state. These measurements highlight the importance of directly measuring the pyroelectric response in thin films, where non-intrinsic effects can be a significant proportion of the total observed pyroelectricity. Material and operating conditions are also discussed which could simultaneously maximize all contributions to pyroelectricity.

Photopyroelectric response of PTCa∕PEEK composite.

PubMed

Estevam, Giuliano Pierre; de Melo, Washington Luiz Barros; Sakamoto, Walter Katsumi

2011-02-01

A pyroelectric composite made of calcium modified lead titanate ceramic and polyether-ether-ketone high performance polymer was obtained in the film form by hot pressing the ceramic/polymer mixture into the desired composition. After polarization with a suitable electric field, a ceramic composite film (60% vol.) exhibited a pyroelectric figure of merit three times higher than that of a lead zirconate titanate ceramic. The material was used as infrared radiation sensor. The voltage responsivity decreases with the inverse of the frequency showing the same behavior of the thermally thick sensor. The reproducibility of the sensor responses was observed.

Preparation of catalysts via ion-exchangeable coatings on supports

DOEpatents

Dosch, R.G.; Stephens, H.P.

1986-04-09

Disclosed are: new catalytic compositions which comprise an inert support coated with a hydrous alkali metal, alkaline earth metal, or quaternary ammonium titanate, niobate, zirconate, or tantalate, in which the alkali or alkaline earth metal or quaternary ammonium cations have been exchanged for a catalytically effective quantity of a catalytically effective metal.

Hydrous oxide ion-exchange compound catalysts

DOEpatents

Dosch, Robert G.; Stephens, Howard P.

1990-01-01

A catalytic material of improved activity which comprises a hydrous, alkali metal or alkaline earth metal or quaternary ammonium titanate, zirconate, niobate, or tantalate, in which the metal or ammonium cations have been exchange with a catalytically effective quantity of a catalyst metal, and which has been subsequently treated with a solution of a Bronsted acid.

Fabrication and energy harvesting characteristics of unimorph piezoelectric cantilever generators with interdigitated electrode lead zirconate titanate laminates

NASA Astrophysics Data System (ADS)

Lee, Min-seon; Yun, Ji-sun; Park, Woon-ik; Hong, Youn-woo; Cho, Jeong-ho; Paik, Jong-hoo; Park, Yong Ho; Son, Chun-myung; Jeong, Young Hun

2017-12-01

Interdigitated electrode (IDE) unimorph piezoelectric cantilever generators (UPCGs) were fabricated and their energy harvesting characteristics were investigated. A hard lead zirconate titanate (PZT) material with a high mechanical quality factor (Q m) of 1280 was used for the active piezoelectric film of the IDE UPCGs. Two different laminated IDE UPCGs were prepared; one has Ag/Pd interdigitated electrode (IDE) formed only on the top and bottom PZT sheets (D-IDE), while the other has Ag/Pd IDE on all of the PZT sheets (M-IDE). Cofiring was conducted at 1050 °C for 2 h for PZT laminates with IDEs. The fabricated IDE UPCGs exhibited power densities of 50.4 µW/cm3 for the D-IDE and 820 µW/cm3 for the M-IDE. The UPCG with the M-IDE exhibited a higher performance than that with the D-IDE. Specifically, a significantly enhanced normalized power factor of 670 µW/(g2·cm3) was found at 118 Hz across 100 kΩ.

Non-aqueous electrochemical deposition of lead zirconate titanate films for flexible sensor applications

NASA Astrophysics Data System (ADS)

Joseph, Sherin; Kumar, A. V. Ramesh; John, Reji

2017-11-01

Lead zirconate titanate (PZT) is one of the most important piezoelectric materials widely used for underwater sensors. However, PZTs are hard and non-compliant and hence there is an overwhelming attention devoted toward making it flexible by preparing films on flexible substrates by different routes. In this work, the electrochemical deposition of composition controlled PZT films over flexible stainless steel (SS) foil substrates using non-aqueous electrolyte dimethyl sulphoxide (DMSO) was carried out. Effects of various key parameters involved in electrochemical deposition process such as current density and time of deposition were studied. It was found that a current density of 25 mA/cm2 for 5 min gave a good film. The morphology and topography evaluation of the films was carried out by scanning electron microscopy (SEM) and atomic force microscopy (AFM), respectively, which showed a uniform morphology with a surface roughness of 2 nm. The PZT phase formation was studied using X-ray diffraction (XRD) and corroborated with Raman spectroscopic studies. The dielectric constant, dielectric loss, hysteresis and I-V characteristics of the film was evaluated.

Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

NASA Astrophysics Data System (ADS)

Wang, Hong; Lee, Sung-Min; Wang, James L.; Lin, Hua-Tay

2014-12-01

Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 108 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and the fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications, such as piezoelectric fuel injectors in heavy-duty diesel engines.

Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hong; Lee, Sung Min; Wang, James L.

Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10^8 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and themore » fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications such as piezoelectric fuel injectors in heavy-duty diesel engines.« less

Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hong, E-mail: wangh@ornl.gov; Lee, Sung-Min; Wang, James L.

Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10{sup 8} cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and the fatiguemore » index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications, such as piezoelectric fuel injectors in heavy-duty diesel engines.« less

Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

DOE PAGES

Wang, Hong; Lee, Sung Min; Wang, James L.; ...

2014-12-19

Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10^8 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and themore » fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications such as piezoelectric fuel injectors in heavy-duty diesel engines.« less

Comparative analysis of barium titanate thin films dry etching using inductively coupled plasmas by different fluorine-based mixture gas

PubMed Central

2014-01-01

In this work, the inductively coupled plasma etching technique was applied to etch the barium titanate thin film. A comparative study of etch characteristics of the barium titanate thin film has been investigated in fluorine-based (CF4/O2, C4F8/O2 and SF6/O2) plasmas. The etch rates were measured using focused ion beam in order to ensure the accuracy of measurement. The surface morphology of etched barium titanate thin film was characterized by atomic force microscope. The chemical state of the etched surfaces was investigated by X-ray photoelectron spectroscopy. According to the experimental result, we monitored that a higher barium titanate thin film etch rate was achieved with SF6/O2 due to minimum amount of necessary ion energy and its higher volatility of etching byproducts as compared with CF4/O2 and C4F8/O2. Low-volatile C-F compound etching byproducts from C4F8/O2 were observed on the etched surface and resulted in the reduction of etch rate. As a result, the barium titanate films can be effectively etched by the plasma with the composition of SF6/O2, which has an etch rate of over than 46.7 nm/min at RF power/inductively coupled plasma (ICP) power of 150/1,000 W under gas pressure of 7.5 mTorr with a better surface morphology. PMID:25278821

In situ 2D diffraction as a tool to characterize ferroelectric and piezoelectric thin films

NASA Astrophysics Data System (ADS)

Khamidy, N. I.; Kovacova, V.; Bernasconi, A.; Le Rhun, G.; Vaxelaire, N.

2017-08-01

In this paper the application of 2D x-ray diffraction (XRD2) as a technique to characterize in situ during electrical cycling the properties of a ferroelectric and piezoelectric thin film is discussed. XRD2 is one type of XRD on which a 2D detector is used instead of a point detector. This technique enables simultaneous recording of many sample information in a much shorter time compared to conventional XRD. The discussion is focused especially on the data processing technique of the huge data acquired. The methodology to calculate an effective piezoelectric coefficient, analyze the phase and texture, and estimate the domain size and shape is described in this paper. This methodology is then applied to a lead zirconate titanate (PZT) thin film at the morphotropic phase boundary (MPB) composition (i.e. Pb[Zr0.52Ti0.48]O3) with a preferred orientation of (1 0 0). The in situ XRD2 characterization was conducted in the European synchrotron radiation facility (ESRF) in Grenoble, France. Since a high-energy beam with vertical resolution as small as 100 nm was used, a cross-sectional scan of the sample was performed over the entire thickness of the film. From these experimental results, a better understanding on the piezoelectricity phenomena in PZT thin film at MPB composition were achieved, providing original feedback between the elaboration processes and functional properties of the film.

Comparison of Piezo-material based Energy Transduction Systems for Artificial Nanoswimmer

NASA Astrophysics Data System (ADS)

Nain, S.; Rathore, J. S.; Sharma, N. N.

2018-04-01

The energy harnessing is a process of obtaining energy from the surrounding environment and converting into electrical energy. In the last two decades, there has been a plenteous study in energy harnessing. Now a day, energy harnessing using piezoelectric materials has drawn attention of researchers due to low cost, flexibility and light weight. The benefits of piezoelectric material can be utilized by designing a self-powered device for artificial nanoswimmer. Some of the ceramics which displays the piezoelectric effect are lead-zirconate-titanate (PZT), lead-titanate (PbTiO2), lead-zirconate (PbZrO3) and Barium Titanate (BaTiO3). PZT is most extensively used piezoelectric material in the field of energy harnessing but it is brittle in nature. Lead based piezoelectric materials are toxic in nature and may not suitable for in-vivo biomedical applications. To eradicate this problem, researchers are interested in synthesizing lead free piezoelectric material such as Aluminium Nitride (AIN), Barium Titanate (BaTiO3) and Polyvinylidenefluoride (PVDF). The biocompatibility of PVDF makes it appropriate to be used for energy harnessing in human body for applications like on board powering of nanoswimmer for various disease detection and drug delivery. In this paper, a cantilever beam is being simulated in COMSOL to study electric potential generated on the surface of beam made of different piezoelectric materials such as AIN, PVDF and PZT due to fluidic pressure, which will be utilized as energy for actuation of artificial nanoswimmer. Piezo-based cantilever beams have been compared and maximum electric potential is being observed in PVDF based beam. PVDF seems most promising piezoelectric material for in-vivo biomedical application and it is readily available.

Study of entry and landing probes for exploration of Titan

NASA Technical Reports Server (NTRS)

1979-01-01

Saturn's largest moon, Titan, is a totally unique planetary body which is certain to yield exciting new phenomena. Current information is lacking in detail to distinguish between a thin methane rich atmosphere and a thick nitrogen rich atmosphere. Therefore, both the thin and thick atmospheric models were used for the study of various Titan probe classes described in this report. The technical requirements, conceptual design, science return, schedule, cost and mission implications of three probe classes that could be used for exploration of Titan are defined. The three probe classes were based on a wide range of exploration mission possibilities.

Bismuth Sodium Titanate Based Materials for Piezoelectric Actuators

PubMed Central

Reichmann, Klaus; Feteira, Antonio; Li, Ming

2015-01-01

The ban of lead in many electronic products and the expectation that, sooner or later, this ban will include the currently exempt piezoelectric ceramics based on Lead-Zirconate-Titanate has motivated many research groups to look for lead-free substitutes. After a short overview on different classes of lead-free piezoelectric ceramics with large strain, this review will focus on Bismuth-Sodium-Titanate and its solid solutions. These compounds exhibit extraordinarily high strain, due to a field induced phase transition, which makes them attractive for actuator applications. The structural features of these materials and the origin of the field-induced strain will be revised. Technologies for texturing, which increases the useable strain, will be introduced. Finally, the features that are relevant for the application of these materials in a multilayer design will be summarized. PMID:28793724

High temperature ultrasonic transducers for the generation of guided waves for non-destructive evaluation of pipes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sinding, K.; Searfass, C.; Malarich, N.

2014-02-18

Applications for non-destructive evaluation and structural health monitoring of steam generators require ultrasonic transducers capable of withstanding the high temperatures of the pipes and heat exchangers. These applications require a strong coupling of the transducer to the heat exchanger’s complex geometry at the elevated temperatures. Our objective is to use spray-on piezo-electrics for depositing comb transducers onto the curved surfaces. This paper shows results for composite transducers such as lead zirconate titanate/ bismuth titanate and bismuth titanate/ lithium niobate. The comb transducers were prepared by precision laser ablation. The feasibility of producing second harmonic waves in rods with these spay-onmore » comb transducers was demonstrated and paves the way toward measuring material degradation early-on before crack initiation occurs.« less

Local probing of ferroelectric and ferroelastic switching through stress-mediated piezoelectric spectroscopy

DOE PAGES

Edwards, David; Bastani, Yaser; Cao, Ye; ...

2016-01-19

The role of local strains is fundamental to the large effective piezoelectric and ferroelectric response of thin films. Therefore a method to investigate local strain-induced phenomena is imperative. Here, pressure induced domain reorganization is reported in lead zirconate titanate films with composition near the morphotropic phase boundary. An approach is thus demonstrated to simultaneously study the role of applied mechanical pressure on multiple local properties of the film. In particular, the modification of hysteresis loops collected at different tip pressures is consistent with first mostly ferroelastic and then ferroelectric dominated reorientation of domains under increasing applied pressure. The pressure inducedmore » domain writing is also investigated through phase field simulations where the applied pressure is generally found to increase the in-plane polarization of the domains with respect to the out-of-plane component, corroborating the experimental observations. The approach developed here has the potential to explore other hysteretic phenomena and phase transitions in a spatially resolved manner with varying local pressure.« less

Piezo-generated charge mapping revealed through direct piezoelectric force microscopy.

PubMed

Gomez, A; Gich, M; Carretero-Genevrier, A; Puig, T; Obradors, X

2017-10-24

While piezoelectric and ferroelectric materials play a key role in many everyday applications, there are still a number of open questions related to their physics. To enhance our understanding of piezoelectrics and ferroelectrics, nanoscale characterization is essential. Here, we develop an atomic force microscopy based mode that obtains a direct quantitative analysis of the piezoelectric coefficient d 33 . We report nanoscale images of piezogenerated charge in a thick single crystal of periodically poled lithium niobate (PPLN), a bismuth ferrite (BiFO 3 ) thin film, and lead zirconate titanate (PZT) by applying a force and recording the current produced by these materials. The quantification of d 33 coefficients for PPLN (14 ± 3 pC per N) and BFO (43 ± 6 pC per N) is in agreement with the values reported in the literature. Even stronger evidence of the reliability of the method is provided by an equally accurate measurement of the significantly larger d 33 of PZT.

Study on optimizing ultrasonic irradiation period for thick polycrystalline PZT film by hydrothermal method.

PubMed

Ohta, Kanako; Isobe, Gaku; Bornmann, Peter; Hemsel, Tobias; Morita, Takeshi

2013-04-01

The hydrothermal method utilizes a solution-based chemical reaction to synthesize piezoelectric thin films and powders. This method has a number of advantages, such as low-temperature synthesis, and high purity and high quality of the product. In order to promote hydrothermal reactions, we developed an ultrasonic assisted hydrothermal method and confirmed that it produces dense and thick lead-zirconate-titanate (PZT) films. In the hydrothermal method, a crystal growth process follows the nucleation process. In this study, we verified that ultrasonic irradiation is effective for the nucleation process, and there is an optimum irradiation period to obtain thicker PZT films. With this optimization, a 9.2-μm-thick PZT polycrystalline film was obtained in a single deposition process. For this film, ultrasonic irradiation was carried out from the beginning of the reaction for 18 h, followed by a 6 h deposition without ultrasonic irradiation. These results indicate that the ultrasonic irradiation mainly promotes the nucleation process. Copyright © 2012 Elsevier B.V. All rights reserved.

Strain and in-plane orientation effects on the ferroelectricity of (111)-oriented tetragonal Pb(Zr0.35Ti0.65)O3 thin films prepared by metal organic chemical vapor deposition

NASA Astrophysics Data System (ADS)

Kuwabara, Hiroki; Menou, Nicolas; Funakubo, Hiroshi

2007-05-01

The growth and characterization of epitaxial (111)-oriented Pb(Zr0.35Ti0.65)O3 films deposited by metal organic chemical vapor deposition on (100)-oriented silicon substrates [(111)SrRuO3‖(111)Pt ‖(100)yttria-stabilizedzirconia‖(100)Si] are reported. The orientation, microstructure, and electric properties of these films are compared to those of fiber-textured highly (111)-oriented lead zirconate titanate (PZT) films deposited on (111)SrRuO3/(111)Pt/TiOx/SiO2/(100)Si substrates and epitaxial (111)-oriented PZT films deposited on (111)SrRuO3‖(111)SrTiO3 substrates. The ferroelectric properties of these films are not drastically influenced by the in-plane orientation of the film and by the strain state imposed by the underlying substrate. These results support the use of fiber-textured highly (111)-oriented films in highly stable ferroelectric capacitors.

Electric field cycling behavior of ferroelectric hafnium oxide.

PubMed

Schenk, Tony; Schroeder, Uwe; Pešić, Milan; Popovici, Mihaela; Pershin, Yuriy V; Mikolajick, Thomas

2014-11-26

HfO2 based ferroelectrics are lead-free, simple binary oxides with nonperovskite structure and low permittivity. They just recently started attracting attention of theoretical groups in the fields of ferroelectric memories and electrostatic supercapacitors. A modified approach of harmonic analysis is introduced for temperature-dependent studies of the field cycling behavior and the underlying defect mechanisms. Activation energies for wake-up and fatigue are extracted. Notably, all values are about 100 meV, which is 1 order of magnitude lower than for conventional ferroelectrics like lead zirconate titanate (PZT). This difference is mainly atttributed to the one to two orders of magnitude higher electric fields used for cycling and to the different surface to volume ratios between the 10 nm thin films in this study and the bulk samples of former measurements or simulations. Moreover, a new, analog-like split-up effect of switching peaks by field cycling is discovered and is explained by a network model based on memcapacitive behavior as a result of defect redistribution.

Imaging nanoscale lattice variations by machine learning of x-ray diffraction microscopy data

DOE PAGES

Laanait, Nouamane; Zhang, Zhan; Schlepütz, Christian M.

2016-08-09

In this paper, we present a novel methodology based on machine learning to extract lattice variations in crystalline materials, at the nanoscale, from an x-ray Bragg diffraction-based imaging technique. By employing a full-field microscopy setup, we capture real space images of materials, with imaging contrast determined solely by the x-ray diffracted signal. The data sets that emanate from this imaging technique are a hybrid of real space information (image spatial support) and reciprocal lattice space information (image contrast), and are intrinsically multidimensional (5D). By a judicious application of established unsupervised machine learning techniques and multivariate analysis to this multidimensional datamore » cube, we show how to extract features that can be ascribed physical interpretations in terms of common structural distortions, such as lattice tilts and dislocation arrays. Finally, we demonstrate this 'big data' approach to x-ray diffraction microscopy by identifying structural defects present in an epitaxial ferroelectric thin-film of lead zirconate titanate.« less

Imaging nanoscale lattice variations by machine learning of x-ray diffraction microscopy data

DOE Office of Scientific and Technical Information (OSTI.GOV)

Laanait, Nouamane; Zhang, Zhan; Schlepütz, Christian M.

In this paper, we present a novel methodology based on machine learning to extract lattice variations in crystalline materials, at the nanoscale, from an x-ray Bragg diffraction-based imaging technique. By employing a full-field microscopy setup, we capture real space images of materials, with imaging contrast determined solely by the x-ray diffracted signal. The data sets that emanate from this imaging technique are a hybrid of real space information (image spatial support) and reciprocal lattice space information (image contrast), and are intrinsically multidimensional (5D). By a judicious application of established unsupervised machine learning techniques and multivariate analysis to this multidimensional datamore » cube, we show how to extract features that can be ascribed physical interpretations in terms of common structural distortions, such as lattice tilts and dislocation arrays. Finally, we demonstrate this 'big data' approach to x-ray diffraction microscopy by identifying structural defects present in an epitaxial ferroelectric thin-film of lead zirconate titanate.« less

Thermal effects on domain orientation of tetragonal piezoelectrics studied by in situ x-ray diffraction

NASA Astrophysics Data System (ADS)

Chang, Wonyoung; King, Alexander H.; Bowman, Keith J.

2006-06-01

Thermal effects on domain orientation in tetragonal lead zirconate titanate (PZT) and lead titanate (PT) have been investigated by using in situ x-ray diffraction with an area detector. In the case of a soft PZT, it is found that the texture parameter called multiples of a random distribution (MRD) initially increases with temperature up to approximately 100°C and then falls to unity at temperatures approaching the Curie temperature, whereas the MRD of hard PZT and PT initially undergoes a smaller increase or no change. The relationship between the mechanical strain energy and domain wall mobility with temperature is discussed.

Processing of Fine-Scale Piezoelectric Ceramic/Polymer Composites for Sensors and Actuators

NASA Technical Reports Server (NTRS)

Janas, V. F.; Safari, A.

1996-01-01

The objective of the research effort at Rutgers is the development of lead zirconate titanate (PZT) ceramic/polymer composites with different designs for transducer applications including hydrophones, biomedical imaging, non-destructive testing, and air imaging. In this review, methods for processing both large area and multifunctional ceramic/polymer composites for acoustic transducers were discussed.

Improved hydrous oxide ion-exchange compound catalysts

DOEpatents

Dosch, R.G.; Stephens, H.P.

1986-04-09

Disclosed is a catalytic material of improved activity which comprises a hydrous, alkali metal or alkaline earth metal or quaternary ammonium titanate, zirconate, niobate, or tantalate, in which the metal or ammonium cations have been exchanged with a catalytically effective quantity of a catalyst metal, and which has been subsequently treated with a solution of a Bronsted acid.

STIR: Novel Electronic States by Gating Strongly Correlated Materials

DTIC Science & Technology

2016-03-01

plan built on my group’s recent demonstration of electrolyte gating in Strontium Titanate, using an atomically thin hexagonal Boron Nitride barrier to...demonstration of electrolyte gating in Strontium Titanate, using an atomically thin hexagonal Boron Nitride barrier to prevent disorder and chemical...techniques and learned to apply thin hexagonal Boron Nitride to single crystals of materials expected to show some of the most exciting correlated

Comparative measurements of piezoelectric coefficient of PZT films by Berlincourt, interferometer, and vibrometer methods.

PubMed

Huang, Zhaorong; Zhang, Qi; Corkovic, Silvana; Dorey, Robert; Whatmore, Roger W

2006-12-01

Chemical solution deposition (CSD) techniques were used to prepare lead zirconate (Zr) titanate (Ti) (PZT) thin films with Zr/Ti ratios of 30/70 and 52/48. Usually CSD processing is restricted to making crack-free, single-layer films of 70-nm thick, but modifications to the sol-gel process have permitted the fabrication of dense, crack-free, single layers up to 200 to 300 nm thick, which can be built-up into layers up to 3-microm thick. Thicker PZT films (> 2-microm single layer) can be produced by using a composite sol-gel/ceramic process. Knowledge of the electroactive properties of these materials is essential for modeling and design of novel micro-electromechanical systems (MEMS) devices, but accurate measurement of these properties is by no means straightforward. A novel, double-beam, common-path laser interferometer has been developed to measure the longitudinal (d33) piezoelectric coefficient in films; the results were compared with the values obtained by Berlin-court and laser scanning vibrometer methods. It was found that, for thin-film samples, the d(33,f) values obtained from the Berlincourt method are usually larger: than those obtained from the interferometer and the vibrometer methods; the reasons for this are discussed.

Multiscale Modeling of Advanced Materials for Damage Prediction and Structural Health Monitoring

DTIC Science & Technology

2015-05-01

Viscoplasticity Model ................................................. 71 4.1. PZT (APC 850) Orthotropic Properties...surface-mounted lead zirconate titanate ( PZT ) transducer using a coupled FEM-normal mode expansion method. Other researchers have also utilized the...orthotropic material properties of the PZT piezoelectric actuators and sensors are presented in Table 4.1. A 5 cycle cosine tone burst signal, seen in

Photosensitivity enhancement of PLZT ceramics by positive ion implantation

DOEpatents

Land, Cecil E.; Peercy, Paul S.

1983-01-01

The photosensitivity of lead lanthanum zirconate titanate (PLZT) ceramic material used in high resolution, high contrast, and non-volatile photoferroelectric image storage and display devices is enhanced significantly by positive ion implantation of the PLZT near its surface. Implanted ions include H.sup.+, He.sup.+, Ne.sup.+, Ar.sup.+, as well as chemically reactive ions from Fe, Cr, and Al. The positive ion implantation advantageously serves to shift the absorption characteristics of the PLZT material from near-UV light to visible light. As a result, photosensitivity enhancement is such that the positive ion implanted PLZT plate is sensitive even to sunlight and conventional room lighting, such as fluorescent and incandescent light sources. The method disclosed includes exposing the PLZT plate to the positive ions at sufficient density, from 1.times.10.sup.12 to 1.times.10.sup.17, and with sufficient energy, from 100 to 500 KeV, to provide photosensitivity enhancement. The PLZT material may have a lanthanum content ranging from 5 to 10%, a lead zirconate content of 62 to 70 mole %, and a lead titanate content of 38 to 30%. The ions are implanted at a depth of 0.1 to 2 microns below the surface of the PLZT plate.

Using the methods of radiospectroscopy (EPR, NMR) to study the nature of the defect structure of solid solutions based on lead zirconate titanate (PZT).

PubMed

Bykov, Igor; Zagorodniy, Yuriy; Yurchenko, Lesya; Korduban, Alexander; Nejezchleb, Karel; Trachevsky, Vladimir; Dimza, Vilnis; Jastrabik, Lubomir; Dejneka, Alexander

2014-08-01

The nature of intrinsic and impurity point defects in lead zirconate titanate (PZT) ceramics has been explored. Using electron paramagnetic resonance (EPR), nuclear magnetic resonance (NMR), and X-ray photoelectron spectroscopy (XPS) methods, several impurity sites have been identified in the materials, including the Fe(3+)-oxygen vacancy (VO) complex and Pb ions. Both of these centers are incorporated into the PZT lattice. The Fe(3+) –VО paramagnetic complex serves as a sensitive probe of the local crystal field in the ceramic; the symmetry of this defect roughly correlates with PZT phase diagram as the composition is varied from PbTiO3 to PbZrO3. NMR spectra (207)Pb in PbTiO3, PbZrO3, and PZT with iron content from 0 to 0.4 wt% showed that increasing the iron concentration leads to a distortion of the crystal structure and to improvement of the electrophysical parameters of the piezoceramics. This is due to the formation of a phase which has a higher symmetry, but at high concentrations of iron (>0.4 wt%), it leads to sharp degradation of electrophysical parameters.

The Effect of Acceptor and Donor Doping on Oxygen Vacancy Concentrations in Lead Zirconate Titanate (PZT).

PubMed

Slouka, Christoph; Kainz, Theresa; Navickas, Edvinas; Walch, Gregor; Hutter, Herbert; Reichmann, Klaus; Fleig, Jürgen

2016-11-22

The different properties of acceptor-doped (hard) and donor-doped (soft) lead zirconate titanate (PZT) ceramics are often attributed to different amounts of oxygen vacancies introduced by the dopant. Acceptor doping is believed to cause high oxygen vacancy concentrations, while donors are expected to strongly suppress their amount. In this study, La 3+ donor-doped, Fe 3+ acceptor-doped and La 3+ /Fe 3+ -co-doped PZT samples were investigated by oxygen tracer exchange and electrochemical impedance spectroscopy in order to analyse the effect of doping on oxygen vacancy concentrations. Relative changes in the tracer diffusion coefficients for different doping and quantitative relations between defect concentrations allowed estimates of oxygen vacancy concentrations. Donor doping does not completely suppress the formation of oxygen vacancies; rather, it concentrates them in the grain boundary region. Acceptor doping enhances the amount of oxygen vacancies but estimates suggest that bulk concentrations are still in the ppm range, even for 1% acceptor doping. Trapped holes might thus considerably contribute to the charge balancing of the acceptor dopants. This could also be of relevance in understanding the properties of hard and soft PZT.

Oxalate co-precipitation synthesis of calcium zirconate and calcium titanate powders.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hernandez-Sanchez, Bernadette A.; Tuttle, Bruce Andrew

2009-06-01

Fine powders of calcium zirconate (CaZrO{sub 3}, CZ) and calcium titanate (CaTiO{sub 3}, CT) were synthesized using a nonaqueous oxalate co-precipitation route from Ca(NO{sub 3}){sub 2}{center_dot}4 H{sub 2}O and group(IV) n-butoxides (Ti(OBu{sup n}){sub 4} or Zr(OBu{sup n}){sub 4}). Several reaction conditions and batch sizes (2-35 g) were explored to determine their influence on final particle size, morphology, and phase. Characterization of the as-prepared oxalate precursors, oven dried oxalate precursors (60-90 C), and calcined powders (635-900 C) were analyzed with TGA/DTA, XRD, TEM, and SEM. Densification and sintering studies on pressed CZ pellets at 1375 and 1400 C were also performed.more » Through the developed oxalate co-precipitation route, densification temperatures for CZ were lowered by 125 C from the 1500 C firing temperature required for conventional mixed oxide powders. Low field electrical tests of the CZ pellets indicated excellent dielectric properties with dielectric constants of {approx}30 and a dissipation factor of 0.0004 were measured at 1 kHz.« less

The Effect of Acceptor and Donor Doping on Oxygen Vacancy Concentrations in Lead Zirconate Titanate (PZT)

PubMed Central

Slouka, Christoph; Kainz, Theresa; Navickas, Edvinas; Walch, Gregor; Hutter, Herbert; Reichmann, Klaus; Fleig, Jürgen

2016-01-01

The different properties of acceptor-doped (hard) and donor-doped (soft) lead zirconate titanate (PZT) ceramics are often attributed to different amounts of oxygen vacancies introduced by the dopant. Acceptor doping is believed to cause high oxygen vacancy concentrations, while donors are expected to strongly suppress their amount. In this study, La3+ donor-doped, Fe3+ acceptor-doped and La3+/Fe3+-co-doped PZT samples were investigated by oxygen tracer exchange and electrochemical impedance spectroscopy in order to analyse the effect of doping on oxygen vacancy concentrations. Relative changes in the tracer diffusion coefficients for different doping and quantitative relations between defect concentrations allowed estimates of oxygen vacancy concentrations. Donor doping does not completely suppress the formation of oxygen vacancies; rather, it concentrates them in the grain boundary region. Acceptor doping enhances the amount of oxygen vacancies but estimates suggest that bulk concentrations are still in the ppm range, even for 1% acceptor doping. Trapped holes might thus considerably contribute to the charge balancing of the acceptor dopants. This could also be of relevance in understanding the properties of hard and soft PZT. PMID:28774067

Design and Fabrication of 1D and 2D Micro Scanners Actuated by Double Layered Lead Zirconate Titanate (PZT) Bimorph Beams

NASA Astrophysics Data System (ADS)

Tsaur, Jiunnjye; Zhang, Lulu; Maeda, Ryutaro; Matsumoto, Sohei; Khumpuang, Sommawan

2002-06-01

Micro scanners including 1D scanner beams and 2D scanning micromirrors are designed and fabricated. In order to yield large bending force, the sol-gel derived double layered lead zirconate titanate (PZT) structures are developed to be the actuator components. In our developed fabrication process, the use of thermal treatment and the addition of one platinium/titanium film played an important role to yield the well-crystallized perovskite phase and decrease the residual strss of total cantilever structures successfully. In the case of 1D scanner beams with the size of 750× 230 μm2, the optical scanning angle was 41.2 deg with respect to actuation with AC 5 V at 2706 Hz. Under the applied bias of 10 V, the bimorph beam bended upward and the deflection angle of 34.3 deg was measured. A 2D scanning micromirror supported by four suspended double layered PZT actuators was designed to rotate around two orthogonal axes by the operation at different resonant frequencies. While resonating with AC 7.5 V at 3750 Hz and 5350 Hz, the maximum scanning area of 24\\circ× 26\\circ was obtained.

High Discharge Energy Density at Low Electric Field Using an Aligned Titanium Dioxide/Lead Zirconate Titanate Nanowire Array.

PubMed

Zhang, Dou; Liu, Weiwei; Guo, Ru; Zhou, Kechao; Luo, Hang

2018-02-01

Polymer-based capacitors with high energy density have attracted significant attention in recent years due to their wide range of potential applications in electronic devices. However, the obtained high energy density is predominantly dependent on high applied electric field, e.g., 400-600 kV mm -1 , which may bring more challenges relating to the failure probability. Here, a simple two-step method for synthesizing titanium dioxide/lead zirconate titanate nanowire arrays is exploited and a demonstration of their ability to achieve high discharge energy density capacitors for low operating voltage applications is provided. A high discharge energy density of 6.9 J cm -3 is achieved at low electric fields, i.e., 143 kV mm -1 , which is attributed to the high relative permittivity of 218.9 at 1 kHz and high polarization of 23.35 µC cm -2 at this electric field. The discharge energy density obtained in this work is the highest known for a ceramic/polymer nanocomposite at such a low electric field. The novel nanowire arrays used in this work are applicable to a wide range of fields, such as energy harvesting, energy storage, and photocatalysis.

Miniature Cryogenic Valves for a Titan Lake Sampling System

NASA Technical Reports Server (NTRS)

Sherrit, Stewart; Zimmerman, Wayne; Takano, Nobuyuki; Avellar, Louisa

2014-01-01

The Cassini mission has revealed Titan to be one of the most Earthlike worlds in the Solar System complete with many of the same surface features including lakes, river channels, basins, and dunes. But unlike Earth, the materials and fluids on Titan are composed of cryogenic organic compounds with lakes of liquid methane and ethane. One of the potential mission concepts to explore Titan is to land a floating platform on one of the Titan Lakes and determine the local lake chemistry. In order to accomplish this within the expected mass volume and power budgets there is a need to pursue the development for a low power lightweight cryogenic valves which can be used along with vacuum lines to sample lake liquid and to distribute to various instruments aboard the Lander. To meet this need we have initiated the development of low power cryogenic valves and actuators based on a single crystal piezoelectric flextensional stacks produced by TRS Ceramics Inc. Since the origin of such high electromechanical properties of Relaxor-PT single crystals is due to the polarization rotation effect, (i.e., intrinsic contributions), the strain per volt decrease at cryogenic temperatures is much lower than in standard Lead Zirconate Titanate (PZT) ceramics. This makes them promising candidates for cryogenic actuators with regards to the stroke for a given voltage. This paper will present our Titan Lake Sampling and Sample Handling system design and the development of small cryogenic piezoelectric valves developed to meet the system specifications.

Volume II: Compendium Abstracts

DTIC Science & Technology

2008-08-01

project developed a fast and simple method of characterization for ceramic , polymer composite, and ceramic -composite materials systems. Current methods...incrementally at 1-inch intervals and displayed as a false-color image map of the sample. This experimental setup can be easily scaled from single ceramic ...low-power, high-force characteristics of lead zirconate titanate ( PZT ) and an offset-beam design to achieve rotational or near-linear translational

Catalysis using hydrous metal oxide ion exchanges

DOEpatents

Dosch, Robert G.; Stephens, Howard P.; Stohl, Frances V.

1985-01-01

In a process which is catalyzed by a catalyst comprising an active metal on a carrier, said metal being active as a catalyst for the process, an improvement is provided wherein the catalyst is a hydrous, alkali metal or alkaline earth metal titanate, zirconate, niobate or tantalate wherein alkali or alkaline earth metal cations have been exchanged with a catalytically effective amount of cations of said metal.

Catalysis using hydrous metal oxide ion exchangers

DOEpatents

Dosch, R.G.; Stephens, H.P.; Stohl, F.V.

1983-07-21

In a process which is catalyzed by a catalyst comprising an active metal on a carrier, said metal being active as a catalyst for the process, an improvement is provided wherein the catalyst is a hydrous, alkali metal or alkaline earth metal titanate, zirconate, niobate or tantalate wherein alkali or alkaline earth metal cations have been exchanged with a catalytically effective amount of cations of said metal.

Demonstrating the potential of yttrium-doped barium zirconate electrolyte for high-performance fuel cells.

PubMed

Bae, Kiho; Jang, Dong Young; Choi, Hyung Jong; Kim, Donghwan; Hong, Jongsup; Kim, Byung-Kook; Lee, Jong-Ho; Son, Ji-Won; Shim, Joon Hyung

2017-02-23

In reducing the high operating temperatures (≥800 °C) of solid-oxide fuel cells, use of protonic ceramics as an alternative electrolyte material is attractive due to their high conductivity and low activation energy in a low-temperature regime (≤600 °C). Among many protonic ceramics, yttrium-doped barium zirconate has attracted attention due to its excellent chemical stability, which is the main issue in protonic-ceramic fuel cells. However, poor sinterability of yttrium-doped barium zirconate discourages its fabrication as a thin-film electrolyte and integration on porous anode supports, both of which are essential to achieve high performance. Here we fabricate a protonic-ceramic fuel cell using a thin-film-deposited yttrium-doped barium zirconate electrolyte with no impeding grain boundaries owing to the columnar structure tightly integrated with nanogranular cathode and nanoporous anode supports, which to the best of our knowledge exhibits a record high-power output of up to an order of magnitude higher than those of other reported barium zirconate-based fuel cells.

Characteristic analysis of diaphragm-type transducer that is thick relative to its size

NASA Astrophysics Data System (ADS)

Ishiguro, Yuya; Zhu, Jing; Tagawa, Norio; Okubo, Tsuyoshi; Okubo, Kan

2017-07-01

In recent years, high-performance piezoelectric micromachined ultrasonic transducers (PMUTs) have been fabricated by micro electro mechanical systems (MEMS) technology. For high-resolution imaging, it is important to broaden the frequency bandwidth. By reducing the diaphragm size to increase the resonance frequency, the film thickness becomes relatively larger and hence the transmitting and receiving characteristics may different from those of a usual thin diaphragm. In this study, we examine the performance of a square-diaphragm-type lead zirconate titanate (PZT) transducer through simulations. To realize the desired resonance frequency of 20 MHz, firstly, the diaphragm size and the thickness of the layers of PZT and Si constituting a PMUT are examined, and then, three PZT/Si models with different thicknesses are selected. Subsequently, using the models, we analyze the transmitting efficiency, transmitting bandwidth, receiving sensitivity (piezoelectric voltage/electric charge), and receiving bandwidth using an FEM simulator. It is found that the proposed models can transmit ultrasound independently of the diaphragm vibration and have wide bandwidth of the receiving frequency as compared with that of a typical PMUT.

A New Paradigm for NDE (Non Destructive Evaluation)

DTIC Science & Technology

2013-12-06

determining specific physical properties of the armor which are correlated with armor structural health. A pair of Lead Zirconate Titanate ( PZT ...this is commonly called the “pitch and catch” method. The armor plate vibrates when it is excited by a mechanical vibration from the PZT actuator...transducer, and this vibration is transmitted through the plate and induces an electrical signal in the PZT receiver transducer by virtue of the

Spatial Light Modulator Would Serve As Electronic Iris

NASA Technical Reports Server (NTRS)

Gutow, David A.

1991-01-01

In proposed technique for controlling brightness of image formed by lens, spatial light modulator serves as segmented, electronically variable aperture. Offers several advantages: spatial light modulator controlled remotely and responds faster than motorized iris or other remotely controlled mechanical iris. Unlike iris, modulator also configured so as not to vary depth of field appreciably. Unlike lead lanthanum zirconate titanate crystal, spatial light modulator does not require high voltage.

Symmetries and multiferroic properties of novel room-temperature magnetoelectrics: Lead iron tantalate – lead zirconate titanate (PFT/PZT)

DOE PAGES

Sanchez, Dilsom A.; Ortega, N.; Kumar, Ashok; ...

2011-12-05

Mixing 60-70% lead zirconate titanate with 40-30% lead iron tantalate produces a single-phase, low-loss, room-temperature multiferroic with magnetoelectric coupling: (PbZr 0.53Ti 0.47O 3) (1-x)- (PbFe 0.5Ta 0.5O 3) x. Our study combines x-ray scattering, magnetic and polarization hysteresis in both phases, plus a second-order dielectric divergence (to epsilon = 6000 at 475 K for 0.4 PFT; to 4000 at 520 K for 0.3 PFT) for an unambiguous assignment as a C 2v-C 4v (Pmm2-P4mm) transition. Furthermore, the material exhibits square saturated magnetic hysteresis loops with 0.1 emu/g at 295 K and saturation polarization P r = 25 μC/cm 2, whichmore » actually increases (to 40 μC/cm 2) in the high-T tetragonal phase, representing an exciting new room temperature oxide multiferroic to compete with BiFeO 3. Additional transitions at high temperatures (cubic at T>1300 K) and low temperatures (rhombohedral or monoclinic at T<250 K) are found. Finally, these are the lowest-loss room-temperature multiferroics known, which is a great advantage for magnetoelectric devices.« less

Unexpectedly high piezoelectricity of Sm-doped lead zirconate titanate in the Curie point region.

PubMed

Seshadri, Shruti B; Nolan, Michelle M; Tutuncu, Goknur; Forrester, Jennifer S; Sapper, Eva; Esteves, Giovanni; Granzow, Torsten; Thomas, Pam A; Nino, Juan C; Rojac, Tadej; Jones, Jacob L

2018-03-07

Large piezoelectric coefficients in polycrystalline lead zirconate titanate (PZT) are traditionally achieved through compositional design using a combination of chemical substitution with a donor dopant and adjustment of the zirconium to titanium compositional ratio to meet the morphotropic phase boundary (MPB). In this work, a different route to large piezoelectricity is demonstrated. Results reveal unexpectedly high piezoelectric coefficients at elevated temperatures and compositions far from the MPB. At temperatures near the Curie point, doping with 2 at% Sm results in exceptionally large piezoelectric coefficients of up to 915 pm/V. This value is approximately twice those of other donor dopants (e.g., 477 pm/V for Nb and 435 pm/V for La). Structural changes during the phase transitions of Sm-doped PZT show a pseudo-cubic phase forming ≈50 °C below the Curie temperature. Possible origins of these effects are discussed and the high piezoelectricity is posited to be due to extrinsic effects. The enhancement of the mechanism at elevated temperatures is attributed to the coexistence of tetragonal and pseudo-cubic phases, which enables strain accommodation during electromechanical deformation and interphase boundary motion. This work provides insight into possible routes for designing high performance piezoelectrics which are alternatives to traditional methods relying on MPB compositions.

Piezoelectric Lead Zirconate Titanate (PZT) Ring Shaped Contour-Mode MEMS Resonators

NASA Astrophysics Data System (ADS)

Kasambe, P. V.; Asgaonkar, V. V.; Bangera, A. D.; Lokre, A. S.; Rathod, S. S.; Bhoir, D. V.

2018-02-01

Flexibility in setting fundamental frequency of resonator independent of its motional resistance is one of the desired criteria in micro-electromechanical (MEMS) resonator design. It is observed that ring-shaped piezoelectric contour-mode MEMS resonators satisfy this design criterion than in case of rectangular plate MEMS resonators. Also ring-shaped contour-mode piezoelectric MEMS resonator has an advantage that its fundamental frequency is defined by in-plane dimensions, but they show variation of fundamental frequency with different Platinum (Pt) thickness referred as change in ratio of fNEW /fO . This paper presents the effects of variation in geometrical parameters and change in piezoelectric material on the resonant frequencies of Platinum piezoelectric-Aluminium ring-shaped contour-mode MEMS resonators and its electrical parameters. The proposed structure with Lead Zirconate Titanate (PZT) as the piezoelectric material was observed to be a piezoelectric material with minimal change in fundamental resonant frequency due to Platinum thickness variation. This structure was also found to exhibit extremely low motional resistance of 0.03 Ω as compared to the 31-35 Ω range obtained when using AlN as the piezoelectric material. CoventorWare 10 is used for the design, simulation and corresponding analysis of resonators which is Finite Element Method (FEM) analysis and design tool for MEMS devices.

High Discharge Energy Density at Low Electric Field Using an Aligned Titanium Dioxide/Lead Zirconate Titanate Nanowire Array

PubMed Central

Zhang, Dou; Liu, Weiwei; Guo, Ru; Zhou, Kechao

2017-01-01

Abstract Polymer‐based capacitors with high energy density have attracted significant attention in recent years due to their wide range of potential applications in electronic devices. However, the obtained high energy density is predominantly dependent on high applied electric field, e.g., 400–600 kV mm−1, which may bring more challenges relating to the failure probability. Here, a simple two‐step method for synthesizing titanium dioxide/lead zirconate titanate nanowire arrays is exploited and a demonstration of their ability to achieve high discharge energy density capacitors for low operating voltage applications is provided. A high discharge energy density of 6.9 J cm−3 is achieved at low electric fields, i.e., 143 kV mm−1, which is attributed to the high relative permittivity of 218.9 at 1 kHz and high polarization of 23.35 µC cm−2 at this electric field. The discharge energy density obtained in this work is the highest known for a ceramic/polymer nanocomposite at such a low electric field. The novel nanowire arrays used in this work are applicable to a wide range of fields, such as energy harvesting, energy storage, and photocatalysis. PMID:29610724

Cold sintering and electrical characterization of lead zirconate titanate piezoelectric ceramics

NASA Astrophysics Data System (ADS)

Wang, Dixiong; Guo, Hanzheng; Morandi, Carl S.; Randall, Clive A.; Trolier-McKinstry, Susan

2018-01-01

This paper describes a cold sintering process for Pb(Zr,Ti)O3 ceramics and the associated processing-property relations. Pb(Zr,Ti)O3 has a very small, incongruent solubility that is a challenge during cold sintering. To circumvent this, a Pb(NO3)2 solution was used as the transient liquid phase. A bimodal lead zirconate titanate powder was densified to a relative density of 89% by cold sintering at 300 °C and 500 MPa. After the cold sintering step, the permittivity was 200, and the dielectric loss was 2.0%. A second heat-treatment involving a 3 h anneal at 900 °C increased the relative density to 99%; the resulting relative dielectric permittivity was 1300 at room temperature and 100 kHz. The samples showed well-defined ferroelectric hysteresis loops, having a remanent polarization of 28 μC/cm2. On poling, the piezoelectric coefficient d33 was ˜200 pC/N. With a 700 °C 3 h post-annealing, samples show a lower room temperature relative permittivity (950 at 100 kHz), but a 24 h hold time at 700 °C produces ceramics where there is an improved relative dielectric constant (1050 at 100 kHz).

MECHANICAL STRENGTH RESPONSES OF POLED LEAD ZIRCONATE TITANATE UNDER EXTREME ELECTRIC FIELD AND VARIOUS TEMPERATURE CONDITIONS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hong; Matsunaga, Tadashi; Zhang, Kewei

PZT (lead zirconate titanate), particularly PZT-5A, is used in a variety of critical actuation and sensing systems because of its high Curie temperature and large piezoelectric coefficients. However, PZT is susceptible to mechanical failure. The evaluation of the mechanical strength of the material under the target working conditions is very important. This study presents part of the recent experimental developments in mechanical testing and evaluation of PZT materials at Oak Ridge National Laboratory. Ball-on-ring and four-point bending testing setups were used, with modifications made to account for testing requirements from high-level electric field and elevated temperature. The poled PZT-5A ormore » equivalent material was tested under various specimen and testing conditions. The parameters of the distribution of strengths (characteristic strength and Weibull modulus) are discussed in relation to the testing conditions. Fractographic results based on scanning electron microscopy are also presented and discussed. The related data can serve as input for the design of piezoceramic devices, not only those used in energy systems like fuel injectors in heavy-duty diesel engines, but also those used in structural health monitoring, energy harvesting, and other critical systems in aerospace and civil engineering.« less

Thermochronology of the Sulu ultrahigh-pressure metamorphic terrane: Implications for continental collision and lithospheric thinning

NASA Astrophysics Data System (ADS)

Liu, Li-Ping; Li, Zheng-Xiang; Danišík, Martin; Li, Sanzhong; Evans, Noreen; Jourdan, Fred; Tao, Ni

2017-08-01

The thermal history of the Dabie-Sulu orogenic belt provides important constraints on the collision process between the South China and North China blocks during the Mesozoic, and possible lithospheric thinning event(s) in the eastern North China Block. This study reports on the thermal evolution of the Sulu ultrahigh-pressure metamorphic (UHP) terrane using zircon U-Pb geochronology and multiple thermochronology methods such as mica and hornblende 40Ar/39Ar, zircon and apatite fission track, and zircon and apatite (U-Th)/He dating. 40Ar/39Ar and zircon (U-Th)/He data show that the UHP terrane experienced accelerated cooling during 180-160 Ma. This cooling event could be interpreted to have resulted from extensional unroofing of an earlier southward thrusting nappe, or, more likely, an episode of northward thrusting of the UHP rocks as a hanging wall. A subsequent episode of exhumation took place between ca. 125 Ma and 90 Ma as recorded by zircon (U-Th)/He data. This event was more pronounced in the northwest section of the UHP terrane, whereas in the southeast section, the zircon (U-Th)/He system retained Jurassic cooling ages of ca. 180-160 Ma. The mid-Cretaceous episode of exhumation is interpreted to have resulted from crustal extension due to the removal of thickened, enriched mantle. A younger episode of exhumation was recorded by apatite fission track and apatite (U-Th)/He ages at ca. 65-40 Ma. Both latter events were linked to episodic thinning of lithosphere along the Sulu UHP terrane in an extensional environment, likely caused by the roll-back of the Western Pacific subduction system.

Coupling of PZT Thin Films with Bimetallic Strip Heat Engines for Thermal Energy Harvesting.

PubMed

Boughaleb, Jihane; Arnaud, Arthur; Guiffard, Benoit; Guyomar, Daniel; Seveno, Raynald; Monfray, Stéphane; Skotnicki, Thomas; Cottinet, Pierre-Jean

2018-06-06

A thermal energy harvester based on a double transduction mechanism and which converts thermal energy into electrical energy by means of piezoelectric membranes and bimetals, has previously been developed and widely presented in the literature In such a device, the thermo-mechanical conversion is ensured by a bimetal whereas the electro-mechanical conversion is generated by a piezoelectric ceramic. However, it has been shown that only 19% of the mechanical energy delivered by the bimetal during its snap is converted into electrical energy. To extract more energy from the bimetallic strip and to increase the transduction efficiency, a new way to couple piezoelectric materials with bimetals has thus been explored through direct deposition of piezoelectric layers on bimetals. This paper consequently presents an alternative way to harvest heat, based on piezoelectric bimetallic strip heat engines and presents a proof of concept of such a system. In this light, different PZT (Lead zirconate titanate) thin films were synthesized directly on aluminium foils and were attached to the bimetals using conductive epoxy. The fabrication process of each sample is presented herein as well as the experimental tests carried out on the devices. Throughout this study, different thicknesses of the piezoelectric layers and substrates were tested to determine the most powerful configuration. Finally, the study also gives some guidelines for future improvements of piezoelectric bimetals.

A large-scan-angle piezoelectric MEMS optical scanner actuated by a Nb-doped PZT thin film

NASA Astrophysics Data System (ADS)

Naono, Takayuki; Fujii, Takamichi; Esashi, Masayoshi; Tanaka, Shuji

2014-01-01

Resonant 1D microelectromechanical systems (MEMS) optical scanners actuated by piezoelectric unimorph actuators with a Nb-doped lead zirconate titanate (PNZT) thin film were developed for endoscopic optical coherence tomography (OCT) application. The MEMS scanners were designed as the resonance frequency was less than 125 Hz to obtain enough pixels per frame in OCT images. The device size was within 3.4 mm × 2.5 mm, which is compact enough to be installed in a side-imaging probe with 4 mm inner diameter. The fabrication process started with a silicon-on-insulator wafer, followed by PNZT deposition by the Rf sputtering and Si bulk micromachining process. The fabricated MEMS scanners showed maximum optical scan angles of 146° at 90 Hz, 148° at 124 Hz, 162° at 180 Hz, and 152° at 394 Hz at resonance in atmospheric pressure. Such wide scan angles were obtained by a drive voltage below 1.3 Vpp, ensuring intrinsic safety in in vivo uses. The scanner with the unpoled PNZT film showed three times as large a scan angle as that with a poled PZT films. A swept-source OCT system was constructed using the fabricated MEMS scanner, and cross-sectional images of a fingertip with image widths of 4.6 and 2.3 mm were acquired. In addition, a PNZT-based angle sensor was studied for feedback operation.

Static/dynamic trade-off performance of PZT thick film micro-actuators

NASA Astrophysics Data System (ADS)

Bienaimé, Alex; Chalvet, Vincent; Clévy, Cédric; Gauthier-Manuel, Ludovic; Baron, Thomas; Rakotondrabe, Micky

2015-07-01

Piezoelectric actuators are widespread in the design of micro/nanorobotic tools and microsystems. Studies toward the integration of such actuators in complex micromechatronic systems require the size reduction of these actuators while retaining a wide range of performance. Two main fabrication processes are currently used for the fabrication of piezoelectric actuators, providing very different behaviors: (i) the use of a bulk lead zirconate titanate (PZT) layer and (ii) the use of thin film growth. In this paper, we propose a trade-off between these two extreme processes and technologies in order to explore the performance of new actuators. This resulted in the design and fabrication of thick film PZT unimorph cantilevers. They allowed a high level of performance, both in the static (displacement) and dynamic (first resonance frequency) regimes, in addition to being small in size. Such cantilever sizes are obtained through the wafer scale bonding and thinning of a PZT plate onto a silicon on insulator wafer. The piezoelectric cantilevers have a 26 μm thick PZT layer with a 5 μm thick silicon layer, over a length of 4 mm and a width of 150 μm. Experimental characterization has shown that the static displacements obtained are in excess of 4.8 μm V-1 and the resonance frequencies are up to 1103 Hz, which are useful for large displacements and low voltage actuators.

Structures and Techniques For Implementing and Packaging Complex, Large Scale Microelectromechanical Systems Using Foundry Fabrication Processes.

DTIC Science & Technology

1996-06-01

switches 5-43 Figure 5-27. Mechanical interference between ’Pull Spring’ devices 5-45 Figure 5-28. Array of LIGA mechanical relay switches 5-49...like coating DM Direct metal interconnect technique DMD ™ Digital Micromirror Device EDP Ethylene, diamine, pyrocatechol and water; silicon anisotropic...mechanical systems MOSIS MOS Implementation Service PGA Pin grid array, an electronic die package PZT Lead-zirconate-titanate LIGA Lithographie

A Study of Ultrasonic Wavefront Distortion Compensation.

DTIC Science & Technology

1998-08-01

arrays. The array is made of piezoelectric composite consisting of PZT (lead zirconate titanate) ceramic rods in a polymer matrix. The transducer...We have developed the procedures for making the final transducer array package by a series of steps. The arrays utilize PZT piezoelectric ceramic ...the low contrast cyst at coordinates (250,425) in Figure 6a. Seen below the cyst is a region with an altered texture and poorer angular resolution, a

Study of the photovoltaic effect in thin film barium titanate

NASA Technical Reports Server (NTRS)

Grannemann, W. W.; Dharmadhikari, V. S.

1983-01-01

The feasibility of making non-volatile digital memory devices of barium titanate, BaTiO3, that are integrated onto a silicon substrate with the required ferroelectric film produced by processing, compatible with silicon technology was examined.

Buffer layer for thin film structures

DOEpatents

Foltyn, Stephen R.; Jia, Quanxi; Arendt, Paul N.; Wang, Haiyan

2006-10-31

A composite structure including a base substrate and a layer of a mixture of strontium titanate and strontium ruthenate is provided. A superconducting article can include a composite structure including an outermost layer of magnesium oxide, a buffer layer of strontium titanate or a mixture of strontium titanate and strontium ruthenate and a top-layer of a superconducting material such as YBCO upon the buffer layer.

Buffer layer for thin film structures

DOEpatents

Foltyn, Stephen R.; Jia, Quanxi; Arendt, Paul N.; Wang, Haiyan

2010-06-15

A composite structure including a base substrate and a layer of a mixture of strontium titanate and strontium ruthenate is provided. A superconducting article can include a composite structure including an outermost layer of magnesium oxide, a buffer layer of strontium titanate or a mixture of strontium titanate and strontium ruthenate and a top-layer of a superconducting material such as YBCO upon the buffer layer.

Enhanced Sensitivity of Magnetoelectric Sensors by Tuning the Resonant Frequency

DTIC Science & Technology

2011-01-01

charge without requiring any operating power. ME sensors consist of layers or plates of at least two components, a magneto- strictive layer, such as...Metglas, and a piezoelectric layer, such as lead zirconate titanate (PZT). These plates or lami- nates are mechanically coupled by nonconductive epoxy. The...applications and the growing energy har- vesting field, it is desirable to tune the resonant frequency to match an input frequency that may vary in time.8

Bio-Inspired Stretchable Network-Based Intelligent Composites

DTIC Science & Technology

2012-05-03

on par with that of lead zirconate titanate ( PZT ). This shows that the BSPT piezo-transducer has the potential to function in ultrasonic situations as...well as the PZTs typically used As a final test, the full network was used, with the same data acquisition computer, designed for PZT - based networks...ality of BSPT in SHM systems. These experiments indicate that BSPT has function- ality on par with PZT -5A and can simply replace the PZT in existing

Signal Processing and Imaging with Ultrasonic Guided Waves: Goals, Challenges and Recent Progress (Preprint)

DTIC Science & Technology

2012-07-01

SHM). 3 Approved for public release; distribution unlimited. The transducers, which are Lead Zirconate Titanate ( PZT ) discs, are permanently... fatigued . Data were recorded as a function of load before the hole was drilled, after the hole was drilled, and at intervals thereafter as a function...of fatigue life. Figure 7 illustrates the effects of matched loads on a fatigue crack about 5 mm in length. Figures 7(a), (b) and (c) correspond

Active layers of high-performance lead zirconate titanate at temperatures compatible with silicon nano- and microelecronic devices

PubMed Central

Bretos, Iñigo; Jiménez, Ricardo; Tomczyk, Monika; Rodríguez-Castellón, Enrique; Vilarinho, Paula M.; Calzada, M. Lourdes

2016-01-01

Applications of ferroelectric materials in modern microelectronics will be greatly encouraged if the thermal incompatibility between inorganic ferroelectrics and semiconductor devices is overcome. Here, solution-processable layers of the most commercial ferroelectric compound ─ morphotrophic phase boundary lead zirconate titanate, namely Pb(Zr0.52Ti0.48)O3 (PZT) ─ are grown on silicon substrates at temperatures well below the standard CMOS process of semiconductor technology. The method, potentially transferable to a broader range of Zr:Ti ratios, is based on the addition of crystalline nanoseeds to photosensitive solutions of PZT resulting in perovskite crystallization from only 350 °C after the enhanced decomposition of metal precursors in the films by UV irradiation. A remanent polarization of 10.0 μC cm−2 is obtained for these films that is in the order of the switching charge densities demanded for FeRAM devices. Also, a dielectric constant of ~90 is measured at zero voltage which exceeds that of current single-oxide candidates for capacitance applications. The multifunctionality of the films is additionally demonstrated by their pyroelectric and piezoelectric performance. The potential integration of PZT layers at such low fabrication temperatures may redefine the concept design of classical microelectronic devices, besides allowing inorganic ferroelectrics to enter the scene of the emerging large-area, flexible electronics. PMID:26837240

Photosensitivity enhancement of PLZT ceramics by positive ion implantation

DOEpatents

Peercy, P.S.; Land, C.E.

1980-06-13

The photosensitivity of lead lanthanum zirconate titanate (PLZT) ceramic material used in high resolution, high contrast, and non-volatile photoferroelectric image storage and display devices is enhanced significantly by positive ion implantation of the PLZT near its surface. Ions that are implanted include H/sup +/, He/sup +/, Ar/sup +/, and a preferred co-implant of Ar/sup +/ and Ne/sup +/. The positive ion implantation advantageously serves to shift the band gap energy threshold of the PLZT material from near-uv light to visible blue light. As a result, photosensitivity enhancement is such that the positive ion implanted PLZT plate is sensitive even to sunlight and conventional room lighting, such as fluorescent and incandescent light sources. The method disclosed includes exposing the PLZT plate to these positive ions of sufficient density and with sufficient energy to provide an image. The PLZT material may have a lanthanum content ranging from 5 to 10%; a lead zirconate content ranging from 62 to 70 mole %; and a lead titanate content ranging from 38 to 30%. The region of ion implantation is in a range from 0.1 to 2 microns below the surface of the PLZT plate. Density of ions is in the range from 1 x 10/sup 12/ to 1 x 10/sup 17/ ions/cm/sup 2/ and having an energy in the range from 100 to 500 keV.

Active layers of high-performance lead zirconate titanate at temperatures compatible with silicon nano- and microeletronic [corrected] devices.

PubMed

Bretos, Iñigo; Jiménez, Ricardo; Tomczyk, Monika; Rodríguez-Castellón, Enrique; Vilarinho, Paula M; Calzada, M Lourdes

2016-02-03

Applications of ferroelectric materials in modern microelectronics will be greatly encouraged if the thermal incompatibility between inorganic ferroelectrics and semiconductor devices is overcome. Here, solution-processable layers of the most commercial ferroelectric compound--morphotrophic phase boundary lead zirconate titanate, namely Pb(Zr0.52Ti0.48)O3 (PZT)--are grown on silicon substrates at temperatures well below the standard CMOS process of semiconductor technology. The method, potentially transferable to a broader range of Zr:Ti ratios, is based on the addition of crystalline nanoseeds to photosensitive solutions of PZT resulting in perovskite crystallization from only 350 °C after the enhanced decomposition of metal precursors in the films by UV irradiation. A remanent polarization of 10.0 μC cm(-2) is obtained for these films that is in the order of the switching charge densities demanded for FeRAM devices. Also, a dielectric constant of ~90 is measured at zero voltage which exceeds that of current single-oxide candidates for capacitance applications. The multifunctionality of the films is additionally demonstrated by their pyroelectric and piezoelectric performance. The potential integration of PZT layers at such low fabrication temperatures may redefine the concept design of classical microelectronic devices, besides allowing inorganic ferroelectrics to enter the scene of the emerging large-area, flexible electronics.

Pressure, temperature, and electric field dependence of phase transformations in niobium modified 95/5 lead zirconate titanate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dong, Wen D.; Carlos Valadez, J.; Gallagher, John A.

2015-06-28

Ceramic niobium modified 95/5 lead zirconate-lead titanate (PZT) undergoes a pressure induced ferroelectric to antiferroelectric phase transformation accompanied by an elimination of polarization and a volume reduction. Electric field and temperature drive the reverse transformation from the antiferroelectric to ferroelectric phase. The phase transformation was monitored under pressure, temperature, and electric field loading. Pressures and temperatures were varied in discrete steps from 0 MPa to 500 MPa and 25 °C to 125 °C, respectively. Cyclic bipolar electric fields were applied with peak amplitudes of up to 6 MV m{sup −1} at each pressure and temperature combination. The resulting electric displacement–electric field hysteresis loops weremore » open “D” shaped at low pressure, characteristic of soft ferroelectric PZT. Just below the phase transformation pressure, the hysteresis loops took on an “S” shape, which split into a double hysteresis loop just above the phase transformation pressure. Far above the phase transformation pressure, when the applied electric field is insufficient to drive an antiferroelectric to ferroelectric phase transformation, the hysteresis loops collapse to linear dielectric behavior. Phase stability maps were generated from the experimental data at each of the temperature steps and used to form a three dimensional pressure–temperature–electric field phase diagram.« less

Electric field tuning of magnetism in heterostructure of yttrium iron garnet film/lead magnesium niobate-lead zirconate titanate ceramic

NASA Astrophysics Data System (ADS)

Lian, Jianyun; Ponchel, Freddy; Tiercelin, Nicolas; Chen, Ying; Rémiens, Denis; Lasri, Tuami; Wang, Genshui; Pernod, Philippe; Zhang, Wenbin; Dong, Xianlin

2018-04-01

In this paper, the converse magnetoelectric (CME) effect by electric field tuning of magnetization in an original heterostructure composed of a polycrystalline yttrium iron garnet (YIG) film and a lead magnesium niobate-lead zirconate titanate (PMN-PZT) ceramic is presented. The magnetic performances of the YIG films with different thicknesses under a DC electric field applied to the PMN-PZT ceramics and a bias magnetic field are investigated. All the magnetization-electric field curves are found to be in good agreement with the butterfly like strain curve of the PMN-PZT ceramic. Both the sharp deformation of about 2.5‰ of PMN-PZT and the easy magnetization switching of YIG are proposed to be the reasons for the strongest CME interaction in the composite at the small electric coercive field of PMN-PZT (4.1 kV/cm) and the small magnetic coercive field of YIG (20 Oe) where the magnetic susceptibility reaches its maximum value. A remarkable CME coefficient of 3.1 × 10-7 s/m is obtained in the system with a 600 nm-thick YIG film. This heterostructure combining multiferroics and partially magnetized ferrite concepts is able to operate under a small or even in the absence of an external bias magnetic field and is more compact and power efficient than the traditional magnetoelectric devices.

Fatigue and failure responses of lead zirconate titanate multilayer actuator under unipolar high-field electric cycling

NASA Astrophysics Data System (ADS)

Zeng, Fan Wen; Wang, Hong; Lin, Hua-Tay

2013-07-01

Lead zirconate titanate (PZT) multilayer actuators with an interdigital electrode design were studied under high electric fields (3 and 6 kV/mm) in a unipolar cycling mode. A 100 Hz sine wave was used in cycling. Five specimens tested under 6 kV/mm failed from 3.8 × 105 to 7 × 105 cycles, whereas three other specimens tested under 3 kV/mm were found to be still functional after 108 cycles. Variations in piezoelectric and dielectric responses of the tested specimens were observed during the fatigue test, depending on the measuring and cycling conditions. Selected fatigued and damaged actuators were characterized using an impedance analyzer or small signal measurement. Furthermore, involved fatigue and failure mechanisms were investigated using scanning acoustic microscope and scanning electron microscope. The extensive cracks and porous regions were revealed across the PZT layers on the cross sections of a failed actuator. The results from this study have demonstrated that the high-field cycling can accelerate the fatigue of PZT stacks as long as the partial discharge is controlled. The small signal measurement can also be integrated into the large signal measurement to characterize the fatigue response of PZT stacks in a more comprehensive basis. The former can further serve as an experimental method to test and monitor the behavior of PZT stacks.

Effect of bipolar electric fatigue on polarization switching in lead-zirconate-titanate ceramics

NASA Astrophysics Data System (ADS)

Zhukov, Sergey; Fedosov, Sergey; Glaum, Julia; Granzow, Torsten; Genenko, Yuri A.; von Seggern, Heinz

2010-07-01

From comparison of experimental results on polarization switching in fresh and electrically fatigued lead-zirconate-titanate (PZT) over a wide range of applied fields and switching times it is concluded that fatigue alters the local field distribution inside the sample due to the generation of discrete defects, such as voids and cracks. Such defects have a strong influence on the overall electric field distribution by their shape and dielectric permittivity. On this hypothesis, a new phenomenological model of polarization switching in fatigued PZT is proposed. The model assumes that the fatigued sample can be composed of different local regions which exhibit different field strengths but otherwise can be considered as unfatigued. Consequently the temporal response of a fatigued sample is assumed to be the superposition of the field-dependent temporal responses of unfatigued samples weighted by their respective volume fraction. A certain part of the volume is excluded from the overall switching process due to the domain pinning even at earlier stages of fatigue, which can be recovered by annealing. Suitability of the proposed model is demonstrated by a good correlation between experimental and calculated data for differently fatigued samples. Plausible cause of the formation of such regions is the generation of defects such as microcracks and the change in electrical properties at imperfections such as pores or voids.

Elution of lead from lead zirconate titanate ceramics to acid rain

NASA Astrophysics Data System (ADS)

Tsurumi, Takaaki; Takezawa, Shuhei; Hoshina, Takuya; Takeda, Hiroaki

2017-10-01

The amount of lead that eluted from lead zirconate titanate (PZT) ceramics to artificial acid rain was evaluated. Four kinds of PZT ceramics, namely, pure PZT at MPB composition, CuO-added PZT, PZT with 10 mol % substitution of Ba for Pb, and CuO-added PZT with 10 mol % substitution of Ba for Pb, were used as samples of the elution test. These PZT ceramics of 8 mm2 and 1.1-1.2 mm thickness were suspended in 300 ml of H2SO4 solution of pH 4.0. The concentration of lead eluted from PZT was in the range from 0.2 to 0.8 ppm. It was found that both liquid phase formation by the addition of CuO and the substitution of Ba for Pb were effective to reduce the amount of lead that eluted. By fitting the leaching out curve with a classical equation, a master curve assuming no sampling effect was obtained. The lead concentration evaluated from the amount of lead that eluted from a commercial PZT plate to H2SO4 solution of pH 5.3 was almost the same as the limit in city water. It is concluded that PZT is not harmful to health and the environment and the amount of lead that eluted from PZT can be controlled by modifying PZT composition.

PZT/PLZT - elastomer composites with improved piezoelectric voltage coefficient

NASA Astrophysics Data System (ADS)

Harikrishnan, K.; Bavbande, D. V.; Mohan, Dhirendra; Manoharan, B.; Prasad, M. R. S.; Kalyanakrishnan, G.

2018-02-01

Lead Zirconate Titanate (PZT) and Lanthanum-modified Lead Zirconate Titanate (PLZT) ceramic sensor materials are widely used because of their excellent piezoelectric coefficients. These materials are brittle, high density and have low achievable piezoelectric voltage coefficients. The density of the sintered ceramics shall be reduced by burnable polymeric sponge method. The achievable porosity level in this case is nearly 60 - 90%. However, the porous ceramic structure with 3-3 connectivity produced by this method is very fragile in nature. The strength of the porous structure is improved with Sylgard®-184 (silicone elastomer) by vacuum impregnation method maintaining the dynamic vacuum level in the range of -650 mm Hg. The elastomer Sylgard®-184 is having low density, low dielectric constant and high compliance (as a resultant stiffness of the composites is increased). To obtain a net dipole moment, the impregnated ceramic composites were subjected to poling treatment with varying conditions of D.C. field and temperature. The properties of the poled PZT/PLZT - elastomer composites were characterized with LCR meter for measuring the dielectric constant values (k), d33 meter used for measuring piezo-electric charge coefficient values (d33) and piezo-electric voltage coefficient (g33) values which were derived from d33 values. The voltage coefficient (g33) values of these composites are increased by 10 fold as compared to the conventional solid ceramics demonstrates that it is possible to fabricate a conformable detector.

Phonon scattering mechanisms dictating the thermal conductivity of lead zirconate titanate (PbZr 1- xTi xO 3) thin films across the compositional phase diagram

DOE PAGES

Foley, Brian M.; Paisley, Elizabeth A.; DiAntonio, Christopher; ...

2017-05-23

This paper represents a thorough investigation of the thermal conductivity (κ) in both thin film and bulk PbZr 1–xTi xO 3 (PZT) across the compositional phase diagram. Given the technological importance of PZT as a superb piezoelectric and ferroelectric material in devices and systems impacting a wide array of industries, this research serves to fill the gap in knowledge regarding the thermal properties. The thermal conductivities of both thin film and bulk PZT are found to vary by a considerable margin as a function of composition x. Additionally, we observe a discontinuity in κ in the vicinity of the morphotropicmore » phase boundary (MPB, x = 0.48) where there is a 20%–25% decrease in κ in our thin film data, similar to that found in literature data for bulk PZT. The comparison between bulk and thin film materials highlights the sensitivity of κ to size effects such as film thickness and grain size even in disordered alloy/solid-solution materials. A model for the thermal conductivity of PZT as a function of composition (κ(x)) is presented, which enables the application of the virtual crystal approximation for alloy-type material systems with very different crystals structures, resulting in differing temperature trends for κ. We show that in the case of crystalline solid-solutions where the thermal conductivity of one of the parent materials exhibits glass-like temperature trends the compositional dependence of thermal conductivity is relatively constant for most values of x. Finally, this is in stark contrast with the typical trends of thermal conductivity with x in alloys, where the thermal conductivity increases dramatically as the composition of the alloy or solid-solution approaches that of a pure parent materials (i.e., as x = 0 or 1).« less

Phonon scattering mechanisms dictating the thermal conductivity of lead zirconate titanate (PbZr 1- xTi xO 3) thin films across the compositional phase diagram

DOE Office of Scientific and Technical Information (OSTI.GOV)

Foley, Brian M.; Paisley, Elizabeth A.; DiAntonio, Christopher

This paper represents a thorough investigation of the thermal conductivity (κ) in both thin film and bulk PbZr 1–xTi xO 3 (PZT) across the compositional phase diagram. Given the technological importance of PZT as a superb piezoelectric and ferroelectric material in devices and systems impacting a wide array of industries, this research serves to fill the gap in knowledge regarding the thermal properties. The thermal conductivities of both thin film and bulk PZT are found to vary by a considerable margin as a function of composition x. Additionally, we observe a discontinuity in κ in the vicinity of the morphotropicmore » phase boundary (MPB, x = 0.48) where there is a 20%–25% decrease in κ in our thin film data, similar to that found in literature data for bulk PZT. The comparison between bulk and thin film materials highlights the sensitivity of κ to size effects such as film thickness and grain size even in disordered alloy/solid-solution materials. A model for the thermal conductivity of PZT as a function of composition (κ(x)) is presented, which enables the application of the virtual crystal approximation for alloy-type material systems with very different crystals structures, resulting in differing temperature trends for κ. We show that in the case of crystalline solid-solutions where the thermal conductivity of one of the parent materials exhibits glass-like temperature trends the compositional dependence of thermal conductivity is relatively constant for most values of x. Finally, this is in stark contrast with the typical trends of thermal conductivity with x in alloys, where the thermal conductivity increases dramatically as the composition of the alloy or solid-solution approaches that of a pure parent materials (i.e., as x = 0 or 1).« less

A novel ultra-planar, long-stroke and low-voltage piezoelectric micromirror

NASA Astrophysics Data System (ADS)

Bakke, Thor; Vogl, Andreas; Żero, Oleg; Tyholdt, Frode; Johansen, Ib-Rune; Wang, Dag

2010-06-01

A novel piston-type micromirror with a stroke of up to 20 µm at 20 V formed out of a silicon-on-insulator wafer with integrated piezoelectric actuators was designed, fabricated and characterized. The peak-to-valley planarity of a 2 mm diameter mirror was better than 15 nm, and tip-to-tip tilt upon actuation less than 30 nm. A resonance frequency of 9.8 kHz was measured. Analytical and finite element models were developed and compared to measurements. The design is based on a silicon-on-insulator wafer where the circular mirror is formed out of the handle silicon, thus forming a thick, highly rigid and ultra-planar mirror surface. The mirror plate is connected to a supporting frame through a membrane formed out of the device silicon layer. A piezoelectric actuator made of lead-zirconate-titanate (PZT) thin film is structured on top of the membrane, providing mirror deflection by deformation of the membrane. Two actuator designs were tested: one with a single ring and the other with a double ring providing bidirectional movement of the mirror. The fabricated mirrors were characterized by white light interferometry to determine the static and temporal response as well as mirror planarity.

Electrode-shaping for the excitation and detection of permitted arbitrary modes in arbitrary geometries in piezoelectric resonators.

PubMed

Pulskamp, Jeffrey S; Bedair, Sarah S; Polcawich, Ronald G; Smith, Gabriel L; Martin, Joel; Power, Brian; Bhave, Sunil A

2012-05-01

This paper reports theoretical analysis and experimental results on a numerical electrode shaping design technique that permits the excitation of arbitrary modes in arbitrary geometries for piezoelectric resonators, for those modes permitted to exist by the nonzero piezoelectric coefficients and electrode configuration. The technique directly determines optimal electrode shapes by assessing the local suitability of excitation and detection electrode placement on two-port resonators without the need for iterative numerical techniques. The technique is demonstrated in 61 different electrode designs in lead zirconate titanate (PZT) thin film on silicon RF micro electro-mechanical system (MEMS) plate, beam, ring, and disc resonators for out-of-plane flexural and various contour modes up to 200 MHz. The average squared effective electromechanical coupling factor for the designs was 0.54%, approximately equivalent to the theoretical maximum value of 0.53% for a fully electroded length-extensional mode beam resonator comprised of the same composite. The average improvement in S(21) for the electrode-shaped designs was 14.6 dB with a maximum improvement of 44.3 dB. Through this piezoelectric electrodeshaping technique, 95% of the designs showed a reduction in insertion loss.

Polarization recovery in lead zirconate titanate thin films deposited on nanosheets-buffered Si (001)

NASA Astrophysics Data System (ADS)

Chopra, Anuj; Bayraktar, Muharrem; Nijland, Maarten; ten Elshof, Johan E.; Bijkerk, Fred; Rijnders, Guus

2016-12-01

Fatigue behavior of Pb(Zr,Ti)O3 (PZT) films is one of the deterrent factors that limits the use of these films in technological applications. Thus, understanding and minimization of the fatigue behavior is highly beneficial for fabricating reliable devices using PZT films. We have investigated the fatigue behavior of preferentially oriented PZT films deposited on nanosheets-buffered Si substrates using LaNiO3 bottom and top electrodes. The films show fatigue of up to 10% at 100 kHz, whereas no fatigue has been observed at 1 MHz. This frequency dependence of the fatigue behavior is found to be in accordance with Dawber-Scott fatigue model that explains the origin of the fatigue as migration of oxygen vacancies. Interestingly, a partial recovery of remnant polarization up to ˜97% of the maximum value is observed after 4×109 cycles which can be further extended to full recovery by increasing the applied electric field. This full recovery is qualitatively explained using kinetic approach as a manifestation of depinning of domains walls. The understanding of the fatigue behavior and polarization recovery that is explained in this paper can be highly useful in developing more reliable PZT devices.

Giant Electric Field Control of Magnetism and Narrow Ferromagnetic Resonance Linewidth in FeCoSiB/Si/SiO2/PMN PT Multiferroic Heterostructures (Open Access Author’s Manuscript)

DTIC Science & Technology

2016-06-06

the widely used lead zirconate titanate ceramics which have a typical piezoelectric coefficient d31 of ~- 200pC/N, PMN-PT single crystals used in...substrate clamping effect, therefore, a relatively giant tunability can be obtained. However, the normally large roughness of piezoelectric layer...is the saturation magnetostriction constant, Y the Young’s modulus of the magnetic film, deff the effective piezoelectric coefficient, E

Nonaqueous solution synthesis process for preparing oxide powders of lead zirconate titanate and related materials

DOEpatents

Voigt, J.A.; Sipola, D.L.; Tuttle, B.A.; Anderson, M.T.

1999-06-01

A process is disclosed for producing powders of perovskite-type compounds which comprises mixing a metal alkoxide solution with a lead acetate solution to form a homogeneous, clear metal solution, adding an oxalic acid/n-propanol solution to this metal solution to form an easily filterable, free-flowing precursor powder and then calcining this powder. This process provides fine perovskite-phase powders with ferroelectric properties which are particularly useful in a variety of electronic applications. 4 figs.

Determination of the Steady State Leakage Current in Structures with Ferroelectric Ceramic Films

NASA Astrophysics Data System (ADS)

Podgornyi, Yu. V.; Vorotilov, K. A.; Sigov, A. S.

2018-03-01

Steady state leakage currents have been investigated in capacitor structures with ferroelectric solgel films of lead zirconate titanate (PZT) formed on silicon substrates with a lower Pt electrode. It is established that Pt/PZT/Hg structures, regardless of the PZT film thickness, are characterized by the presence of a rectifying contact similar to p-n junction. The steady state leakage current in the forward direction increases with a decrease in the film thickness and is determined by the ferroelectric bulk conductivity.

Method of bistable optical information storage using antiferroelectric phase PLZT ceramics

DOEpatents

Land, Cecil E.

1990-01-01

A method for bistable storage of binary optical information includes an antiferroelectric (AFE) lead lanthanum zirconate titanate (PLZT) layer having a stable antiferroelectric first phase and a ferroelectric (FE) second phase obtained by applying a switching electric field across the surface of the device. Optical information is stored by illuminating selected portions of the layer to photoactivate an FE to AFE transition in those portions. Erasure of the stored information is obtained by reapplying the switching field.

Method of bistable optical information storage using antiferroelectric phase PLZT ceramics

DOEpatents

Land, C.E.

1990-07-31

A method for bistable storage of binary optical information includes an antiferroelectric (AFE) lead lanthanum zirconate titanate (PLZT) layer having a stable antiferroelectric first phase and a ferroelectric (FE) second phase obtained by applying a switching electric field across the surface of the device. Optical information is stored by illuminating selected portions of the layer to photoactivate an FE to AFE transition in those portions. Erasure of the stored information is obtained by reapplying the switching field. 8 figs.

Nonaqueous solution synthesis process for preparing oxide powders of lead zirconate titanate and related materials

DOEpatents

Voigt, James A.; Sipola, Diana L.; Tuttle, Bruce A.; Anderson, Mark T.

1999-01-01

A process for producing powders of perovskite-type compounds which comprises mixing a metal alkoxide solution with a lead acetate solution to form a homogeneous, clear metal solution, adding an oxalic acid/n-propanol solution to this metal solution to form an easily filterable, free-flowing precursor powder and then calcining this powder. This process provides fine perovskite-phase powders with ferroelectric properties which are particularly useful in a variety of electronic applications.

Enhanced Dielectric Nonlinearity in Epitaxial Pb(0.92)La(0.08)Zr(0.52)Ti(0.48)O(3)

DTIC Science & Technology

2014-04-23

storage capacitors, electro-mechanical, or photo- mechanical transducers, etc.1–3 Among them, Lead zirconate titanate system ( PZT ), which exhibits...and at the interfaces between PZT and electro- des. Recently, lanthanum doped PZT with different Zr/Ti ra- tio, such as 65/35, 53/47, or 20/80, has...been investigated, since it can effectively reduce oxygen vacancy, decrease leakage current, and lower the fatigue and domain pinning.8–10 In general

Control of mechanical response of freestanding PbZr0.52Ti0.48O3 films through texture

NASA Astrophysics Data System (ADS)

Das, Debashish; Sanchez, Luz; Martin, Joel; Power, Brian; Isaacson, Steven; Polcawich, Ronald G.; Chasiotis, Ioannis

2016-09-01

The texture of piezoelectric lead zirconate titanate (PZT) thin films plays a key role in their mechanical response and linearity in the stress vs. strain behavior. The open circuit mechanical properties of PZT films with controlled texture varying from 100% (001) to 100% (111) were quantified with the aid of direct strain measurements from freestanding thin film specimens. The texture was tuned using a highly {111}-textured Pt substrate and excess-Pb in the PbTiO3 seed layer. The mechanical and ferroelastic properties of 500 nm thick PZT (52/48) films were found to be strongly dependent on grain orientation: the lowest elastic modulus of 90 ± 2 GPa corresponded to pure (001) texture, and its value increased linearly with the percentage of (111) texture reaching 122 ± 3 GPa for pure (111) texture. These elastic modulus values were between those computed for transversely isotropic textured PZT films by using the soft and hard bulk PZT compliance coefficients. Pure (001) texture exhibited maximum non-linearity and ferroelastic domain switching, contrary to pure (111) texture that exhibited more linearity and the least amount of switching. A micromechanics model was employed to calculate the strain due to domain switching. The model fitted well the non-linearities in the experimental stress-strain curves of (001) and (111) textured PZT films, predicting 17% and 10% of switched 90° domains that initially were favorably aligned with the applied stress in (001) and (111) textured PZT films, respectively.

A self-running standing wave-type bidirectional slider for the ultrasonically levitated thin linear stage.

PubMed

Koyama, Daisuke; Takei, Hiroyuki; Nakamura, Kentaro; Ueha, Sadayuki

2008-08-01

A slider for a self-running standing wave-type, ultrasonically levitated, thin linear stage is discussed. The slider can be levitated and moved using acoustic radiation force and acoustic streaming. The slider has a simple configuration and consists of an aluminum vibrating plate and a piezoelectric zirconate titanate (PZT) element. The large asymmetric vibration distribution for the high thrust and levitation performance was obtained by adjusting the configuration determined by finite elemental analysis (FEA). As a preliminary step, the computed results of the sound pressure distribution in the 1-mm air gap by FEA was com pared with experimental results obtained using a fiber optic probe. The direction of the total driving force for the acoustic streaming in the small air gap was estimated by the sound pressure distribution calculated by FEA, and it was found that the direction of the acoustic streaming could be altered by controlling the vibration mode of the slider. The flexural standing wave could be generated along the vibrating plate near the frequencies predicted based on the FEA results. The slider could be levitated by the acoustic radiation force radiated from its own vibrating plate at several frequencies. The slider could be moved in the negative and positive directions at 68 kHz and 69 kHz, which correspond to the results computed by FEA, with the asymmetric vibration distribution of the slider's vibrating plate. Larger thrust could be obtained with the smaller levitation distance, and the maximum thrust was 19 mN.

Dating sub-20 micron zircons in granulite-facies mafic dikes from SW Montana: a new approach using automated mineralogy and SIMS U-Pb geochronology

NASA Astrophysics Data System (ADS)

Ault, A. K.; Mahan, K. H.; Flowers, R. M.; Chamberlain, K.; Appleby, S. K.; Schmitt, A. K.

2010-12-01

Geochronological data is fundamental to all tectonic studies, but a major limitation for many lithologies is a paucity of sizeable zircons suitable for conventional U-Pb techniques. In particular, mafic dike swarms provide important time markers for tectonometamorphic activity in Precambrian terranes, but commonly yield little or no zircon or baddeleyite sufficient for TIMS or standard ion-probe analysis of crystal separates. We apply a new approach involving in-situ automated mineralogy and high spatial resolution Secondary Ion Mass Spectrometry (SIMS) geochronology to a mafic dike swarm exposed in the Northern Madison Range of SW Montana. The dikes cross-cut early fabrics but are also variably deformed and metamorphosed to P-T conditions as high as 1.2 GPa and 850 C. The swarm emplacement age is inferred to be ca. 2.1 Ga based on similarities to dated dikes in the adjacent Tobacco Root Mountains. Resolving the timing of dike emplacement and high-grade metamorphism in the study area is important for understanding the extent of post-Archean modification to the northwest margin of the Wyoming craton. Identification and textural characterization of zircons were facilitated by in-situ automated mineralogical analysis, in contrast to a standard elemental X-ray mapping approach. Our technique uses an SEM-based platform coupling calibrated BSE data with X-ray data collected by multiple energy dispersive spectrometers to rapidly identify target accessory phases at high spatial resolution. Whole thin section search maps were generated in ~30 minutes at 4 µm pixel resolution. Our dike thin sections commonly contained >300 zircons in a variety of textural settings, with 80% having a short dimension <10 µm. Zircons were dated in-situ by adjusting the field aperture of the CAMECA ims1270 to preferentially collect secondary ions emitted from within the inner few microns of the ~15 µm diameter analysis pit. This allows us to analyze zircon grains with a minimum dimension as small as 8 μm at radiogenic yields typically >95% for 206Pb. SIMS data for 22 zircons from a granulite-facies mafic dike thin section define a chord with upper and lower intercepts of 1753.1 ± 9.5 Ma and 63.2 ± 7.9 Ma, respectively (2 sigma error, MSWD = 1.6). A positive correlation between U concentration and degree of discordance indicates that the more radiation-damaged zircons underwent greater Pb loss. We infer Pb loss to reflect re-heating linked to emplacement of the nearby Tobacco Roots Batholith (ca. 74-71 Ma). Metamorphic zircon growth ca. 1750 Ma indicates that the high-grade metamorphic core of the Big Sky orogeny extends into the Northern Madison Range, farther inboard into the Wyoming craton than previously recognized. Coupling automated mineralogy searching with refined SIMS methods enables acquisition and interpretation of in-situ U-Pb data from zircons of a size that would not be feasible with most other techniques.

Pulsed-Laser Crystallization of Ferroelectric/Piezoelectric Oxide Thin Films

NASA Astrophysics Data System (ADS)

Rajashekhar, Adarsh

Integration of ferroelectric/piezoelectric thin films, such as those of lead zirconate titanate (PZT), with temperature sensitive substrates (complementary metal oxide semiconductors (CMOS), or polymers) would benefit from growth at substrate temperatures below 400°C. However, high temperatures are usually required for obtaining good quality PZT films via conventional routes like rapid thermal processing (>550°C). Those conditions are not compatible either with polymer substrates or completed CMOS circuits and dictate exploration of alternative methods to realize integration with such substrates. In part of this work, factors influencing KrF excimer laser induced crystallization of amorphous sputtered Pb(Zr0.30Ti0.70)O3 thin films at substrate temperatures < 215°C were investigated. (111) Pt/Si substrates were utilized to understand the process window. Laser energy densities studied were in the range 35 - 85 mJ/cm2. The Pb content in the films was varied via the Ar gas pressure (in the range 5 mTorr - 9 mTorr) during sputtering of amorphous films. It was seen that a higher Pb content in the asdeposited films aided nucleation of the perovskite phase. Ozone-containing ambients (10% O3/90% O2) during the annealing promoted the formation of the metastable Pb-rich pyrochlore/fluorite phase, while annealing in pure oxygen produced the perovskite phase at relatively lower annealing laser energy densities. Heterogeneous nucleation from the substrate is favored on utilizing a layer-by-layer growth and crystallization process. Films were also grown on polymers using this method. Ferroelectric switching was demonstrated, but extensive process optimization would be needed to reduce leakage and porosity. Real time laser annealing during growth allows for scaling of the layer-by-layer growth process. A pulsed laser deposition system with in situ laser annealing was thus designed, built, and utilized to grow Pb(Zr 0.52Ti0.48)O3 thin films on a laser crystallized Pb(Zr0.20Ti0.80)O3 seed layer, at a temperature of 370°C. Polycrystalline 1.1 microm thick films exhibited columnar grains with small grain sizes ( 30 nm). The films showed well-saturated hysteresis loops (with a remanent polarization of 25 microC/cm2, and a coercive field of 50 kV/cm) and exhibited loss tangents <2.5% with a permittivity of 730. Film orientation could be controlled via the substrate choice; {111} Pb(Zr0.52Ti0.48)O3 films were grown on oriented (111) Pb(Zr0.30Ti0.70)O3 sol-gel seed layers, while epitaxial {001} films were prepared on (100) SrTiO 3 single crystals. In order to study the microstructure evolution in these films, in situ pulsed-laser annealing was used to grow crystalline lead zirconate titanate (PbZr0.52Ti0.48O3) thin films at a substrate temperature of 370°C on PbZr0.30Ti 0.70O3-buffered platinized silicon substrates. Transmission electron microscopy (TEM) analysis indicated that the films were well crystallized into columnar grains, but with pores segregated at the grain boundaries. Lateral densification of the grain columns was significantly improved by reducing the partial pressure of oxygen from 120 mTorr to 50 mTorr, presumably due to enhanced adatom mobility at the surface accompanying increased bombardment. It was found that varying the fractional annealing duration with respect to the deposition duration produced little effect on lateral grain growth. However, increasing the fractional annealing duration led to shift of 111 PZT X-ray diffraction peaks to higher 2theta values, suggesting residual in-plane tensile stresses in the films. Thermal simulations were used to understand the annealing process. Evolution of the film microstructure is described in terms of transient heating from the pulsed laser determining the nucleation events, while the energy of the arriving species dictates grain growth/coarsening.

Gold in Accessory Zircon (the Kozhim Massif, Subpolar Urals)

NASA Astrophysics Data System (ADS)

Denisova, Yuliya; Pystin, Aleksandr

2017-12-01

The crystals of zircon due to their resistance to external impact of various processes can reveal information about the environment of their formation and the inclusions observed of them. Zircon contains different mineral inclusions: biotite, plagioclase, quartz, apatite, etc. However, there is no information about gold inclusions in the zircons from granites of the Sudpolar Urals. The study results of the inclusions of gold in accessory zircon of the Kozhim granitic massif are presented in this paper. The studied mineral is a dark-brown translucent short-prismatic crystal containing the inclusion of gold and the allocations of quartz. According to studies, the inclusion of gold formed during the growth of zircon and it is the gold covered with a thin film of oxide gold. It was confirmed that the crystallization of the studied zircon occurred at a temperature of 800°C and above on the stage of formation of granites of Kozhim massif. The assumption is made about the additional temperature in the course of which was caused by decreasing of temperature up to 700° C and below during postmagmatic stage.

Titanate nanotube thin films with enhanced thermal stability and high-transparency prepared from additive-free sols

DOE Office of Scientific and Technical Information (OSTI.GOV)

Koroesi, Laszlo, E-mail: korosi@enviroinvest.hu; Department of Biotechnology, Nanophage Therapy Center, Enviroinvest Corporation, Kertvaros utca 2, H-7632 Pecs; Papp, Szilvia

2012-08-15

Titanate nanotubes were synthesized from TiO{sub 2} in alkaline medium by a conventional hydrothermal method (150 Degree-Sign C, 4.7 bar). To obtain hydrogen titanates, the as-prepared sodium titanates were treated with either HCl or H{sub 3}PO{sub 4} aqueous solutions. A simple synthesis procedure was devised for stable titanate nanotube sols without using any additives. These highly stable ethanolic sols can readily be used to prepare transparent titanate nanotube thin films of high quality. The resulting samples were studied by X-ray diffraction, N{sub 2}-sorption measurements, Raman spectroscopy, transmission and scanning electron microscopy, X-ray photoelectron spectroscopy and spectroscopic ellipsometry. The comparative resultsmore » of using two kinds of acids shed light on the superior thermal stability of the H{sub 3}PO{sub 4}-treated titanate nanotubes (P-TNTs). X-ray photoelectron spectroscopy revealed that P-TNTs contains P in the near-surface region and the thermal stability was enhanced even at a low ({approx}0.5 at%) concentration of P. After calcination at 500 Degree-Sign C, the specific surface areas of the HCl- and H{sub 3}PO{sub 4}-treated samples were 153 and 244 m{sup 2} g{sup -1}, respectively. The effects of H{sub 3}PO{sub 4} treatment on the structure, morphology and porosity of titanate nanotubes are discussed. - Graphical Abstract: TEM picture (left) shows P-TNTs with diameters about 5-6 nm. Inset shows a stable titanate nanotube sol illuminated by a 532 nm laser beam. Due to the presence of the nanoparticles the way of the light is visible in the sol. Cross sectional SEM picture (right) as well as ellipsometry revealed the formation of optical quality P-TNT films with thicknesses below 50 nm. Highlights: Black-Right-Pointing-Pointer H{sub 3}PO{sub 4} treatment led to TNTs with high surface area even after calcination at 500 Degree-Sign C. Black-Right-Pointing-Pointer H{sub 3}PO{sub 4}-treated TNTs preserved their nanotube morphology up to 500 Degree-Sign C. Black-Right-Pointing-Pointer Stable TNT sols can be prepared by the peptization of TNT gels. Black-Right-Pointing-Pointer High-transparency TNT thin films of high quality were fabricated.« less

Interpretation of zircon coronae textures from metapelitic granulites of the Ivrea-Verbano Zone, northern Italy: two-stage decomposition of Fe-Ti oxides

NASA Astrophysics Data System (ADS)

Kovaleva, Elizaveta; Austrheim, Håkon O.; Klötzli, Urs S.

2017-07-01

In this study, we report the occurrence of zircon coronae textures in metapelitic granulites of the Ivrea-Verbano Zone. Unusual zircon textures are spatially associated with Fe-Ti oxides and occur as (1) vermicular-shaped aggregates 50-200 µm long and 5-20 µm thick and as (2) zircon coronae and fine-grained chains, hundreds of micrometers long and ≤ 1 µm thick, spatially associated with the larger zircon grains. Formation of such textures is a result of zircon precipitation during cooling after peak metamorphic conditions, which involved: (1) decomposition of Zr-rich ilmenite to Zr-bearing rutile, and formation of the vermicular-shaped zircon during retrograde metamorphism and hydration; and (2) recrystallization of Zr-bearing rutile to Zr-depleted rutile intergrown with quartz, and precipitation of the submicron-thick zircon coronae during further exhumation and cooling. We also observed hat-shaped grains that are composed of preexisting zircon overgrown by zircon coronae during stage (2). Formation of vermicular zircon (1) preceded ductile and brittle deformation of the host rock, as vermicular zircon is found both plastically and cataclastically deformed. Formation of thin zircon coronae (2) was coeval with, or immediately after, brittle deformation as coronae are found to fill fractures in the host rock. The latter is evidence of local, fluid-aided mobility of Zr. This study demonstrates that metamorphic zircon can nucleate and grow as a result of hydration reactions and mineral breakdown during cooling after granulite-facies metamorphism. Zircon coronae textures indicate metamorphic reactions in the host rock and establish the direction of the reaction front.

Recent Progress in Understanding the Shock Response of Ferroelectric Ceramics*

NASA Astrophysics Data System (ADS)

Setchell, Robert E.

2001-06-01

Ferroelectric ceramics exhibit a permanent remanent polarization, and the use of shock depoling of these materials to achieve pulsed sources of electrical power was proposed in the late 1950s. During the following twenty years, extensive studies were conducted to examine the shock response of ferroelectric ceramics primarily based on lead zirconate titanate (PZT). Under limited conditions, relatively simple analytical models were found to adequately describe the observed electrical behavior. In general, however, the studies indicated a complex behavior involving finite-rate depoling kinetics with stress and field dependencies. Dielectric relaxation and shock-induced conductivity were also suggested. Unfortunately, few experimental studies were undertaken over the next twenty years, and the development of more comprehensive models was inhibited. In recent years, a strong interest in advancing numerical simulation capabilities has motivated new experimental studies and corresponding model development. More than seventy gas gun experiments have examined several ferroelectric ceramics, with most experiments on lead zirconate titanate having a Zr:Ti ratio of 95:5 and modified with 2ferroelectric but is near an antiferroelectric phase boundary, and depoling results from a shock-driven phase transition. Experiments have examined unpoled, normally poled, and axially poled PZT 95/5 over broad ranges of shock pressure and peak electric field. The extensive base of new data provides quantitative insights into the stress and field dependencies of depoling kinetics and dielectric properties, and is being actively utilized to develop and refine material response models used in numerical simulations of pulsed power devices.

Lead-free piezoelectric (K,Na)NbO3-based ceramic with planar-mode coupling coefficient comparable to that of conventional lead zirconate titanate

NASA Astrophysics Data System (ADS)

Ohbayashi, Kazushige; Matsuoka, Takayuki; Kitamura, Kazuaki; Yamada, Hideto; Hishida, Tomoko; Yamazaki, Masato

2017-06-01

We developed a (K,Na)NbO3-based lead-free piezoelectric ceramic with a KTiNbO5 system, (K1- x Na x )0.86Ca0.04Li0.02Nb0.85O3-δ-K0.85Ti0.85Nb1.15O5-BaZrO3-Fe2O3-MgO (K1- x N x N-NTK-FM). K1- x N x N-NTK-FM ceramic exhibits a very dense microstructure and a coupling coefficient of k p = 0.59, which is almost comparable to that of conventional lead zirconate titanate (PZT). The (K,Na)NbO3-based ceramic has the Γ15 mode for a wide x range. The nanodomains of orthorhombic (K,Na)NbO3 with the M3 mode coexist within the tetragonal Γ15 mode (K,Na)NbO3 matrix. Successive phase transition cannot occur with increasing x. The maximum k p is observed at approximately the minimum x required to generate the M3 mode phase. Unlike the behavior at the morphotropic phase boundary (MPB) in PZT, the characteristics of K1- x N x N-NTK-FM ceramic in this region changed moderately. This gentle phase transition seems to be a relaxor, although the diffuseness degree is not in line with this hypothesis. Furthermore, piezoelectric properties change from “soft” to “hard” upon the M3 mode phase aggregation.

Experimental shock deformation in zircon: a transmission electron microscopic study

NASA Astrophysics Data System (ADS)

Leroux, H.; Reimold, W. U.; Koeberl, C.; Hornemann, U.; Doukhan, J.-C.

1999-06-01

In recent years, apparently shock-induced and, thus, impact-characteristic microdeformations, in the form of planar microdeformation features and so-called strawberry (granular) texture, have been observed in zircons in rocks from confirmed impact structures and from the K/ T boundary. The nature of the planar microdeformations in this mineral is, however, still unknown, and critical information is needed regarding the shock pressure range in which these deformation effects are produced. We experimentally shock deformed two series of thin zircon (ZrSiO 4) target plates, cut perpendicular to the c-axis, at shock pressures of 20, 40, and 60 GPa. The recovered samples were characterized by optical and scanning electron microscopy. In addition, one sample series was studied by transmission electron microscopy (TEM). Microdeformation effects observed at 20 GPa include pervasive micro-cleavage and dislocation patterns. Plastic deformation is indicated by a high density of straight dislocations in glide configuration. The dominant glide systems are <100>{010}. Micro-cleavages, induced by shear stresses during the compression stage, occur mostly in the {100} planes. The large density of dislocations at crack tips shows that plastic deformation was initiated by the micro-cracking processs. At 40 GPa, the sample was partly transformed from the zircon (z) to a scheelite (CaWO 4)-type (s) structure. Planar deformation features (PDFs) containing an amorphous phase of zircon composition are present in the not yet transformed zircon relics. The phase with scheelite structure, initiated in the {100} planes of zircon, consists of thin (0.1 to several μm) bands that crosscut the zircon matrix. The phase transformation is displacive (martensitic) and can be related by {100} z // {112} s and [001] z // <110> s. The scheelite structure phase is densely twinned, with twins in the (112) plane. The 60-GPa sample consists completely of the scheelite structure phase. Crosscutting and displacing relationships between twins and PDFs demonstrate that PDFs are formed in the zircon structure, i.e., before the phase transformation to the scheelite structure occurred, most likely at the shock front. Crystallographic orientations of optically visible planar features in zircon, in comparison with orientations of planar defects at the TEM scale, suggest that the optically visible features are more likely planar microfractures than PDFs.

Fabrication of Crack-Free Barium Titanate Thin Film with High Dielectric Constant Using Sub-Micrometric Scale Layer-by-Layer E-Jet Deposition.

PubMed

Liang, Junsheng; Li, Pengfei; Wang, Dazhi; Fang, Xu; Ding, Jiahong; Wu, Junxiong; Tang, Chang

2016-01-19

Dense and crack-free barium titanate (BaTiO₃, BTO) thin films with a thickness of less than 4 μm were prepared by using sub-micrometric scale, layer-by-layer electrohydrodynamic jet (E-jet) deposition of the suspension ink which is composed of BTO nanopowder and BTO sol. Impacts of the jet height and line-to-line pitch of the deposition on the micro-structure of BTO thin films were investigated. Results show that crack-free BTO thin films can be prepared with 4 mm jet height and 300 μm line-to-line pitch in this work. Dielectric constant of the prepared BTO thin film was recorded as high as 2940 at 1 kHz at room temperature. Meanwhile, low dissipation factor of the BTO thin film of about 8.6% at 1 kHz was also obtained. The layer-by-layer E-jet deposition technique developed in this work has been proved to be a cost-effective, flexible and easy to control approach for the preparation of high-quality solid thin film.

In-situ deposition of sodium titanate thin film as anode for sodium-ion micro-batteries developed by pulsed laser deposition.

PubMed

Rambabu, A; Senthilkumar, B; Sada, K; Krupanidhi, S B; Barpanda, P

2018-03-15

Sodium-ion thin-film micro-batteries form a niche sector of energy storage devices. Sodium titanate, Na 2 Ti 6 O 13 (NTO) thin films were deposited by pulsed laser deposition (PLD) using solid-state synthesized polycrystalline Na 2 Ti 6 O 13 compound. The phase-purity and crystallinity of NTO in bulk and thin-film forms were confirmed by Rietveld refinement. Electron microscopy and atomic force microscopy revealed the formation of uniform ∼100 nm thin film with roughness of ∼4 nm consisting of homogeneous nanoscale grains. These PLD-deposited NTO thin-films, when tested in Na-half cell architecture, delivered a near theoretical reversible capacity close to 42 mA h g -1 involving Ti 4+ /Ti 3+ redox activity along with good cycling stability and rate kinetics. Na 2 Ti 6 O 13 can work as an efficient and safe anode in designing sodium-ion thin-film micro-batteries. Copyright © 2017 Elsevier Inc. All rights reserved.

Laboratory analogues simulating Titan's atmospheric aerosols: Compared chemical compositions of grains and thin films

NASA Astrophysics Data System (ADS)

Carrasco, Nathalie; Jomard, François; Vigneron, Jackie; Etcheberry, Arnaud; Cernogora, Guy

2016-09-01

Two sorts of solid organic samples can be produced in laboratory experiments simulating Titan's atmospheric reactivity: grains in the volume and thin films on the reactor walls. We expect that grains are more representative of Titan's atmospheric aerosols, but films are used to provide optical indices for radiative models of Titan's atmosphere. The aim of the present study is to address if these two sorts of analogues are chemically equivalent or not, when produced in the same N2-CH4 plasma discharge. The chemical compositions of both these materials are measured by using elemental analysis, XPS analysis and Secondary Ion Mass Spectrometry. The main parameter probed is the CH4/N2 ratio to explore various possible chemical regimes. We find that films are homogeneous but significantly less rich in nitrogen and hydrogen than grains produced in the same experimental conditions. This surprising difference in their chemical compositions could be explained by the efficient etching occurring on the films, which stay in the discharge during the whole plasma duration, whereas the grains are ejected after a few minutes. The higher nitrogen content in the grains possibly involves a higher optical absorption than the one measured on the films, with a possible impact on Titan's radiative models.

Microstructure of epitaxial ferroelectric/metal oxide electrode thin film heterostructures on LaAlO{sub 3} and silicon

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ghonge, S.G.; Goo, E.; Ramesh, R.

1994-12-31

TEM and X-ray diffraction studies of PZT, PLZT, lead titanate and bismuth titanate ferroelectric thin films and YBa{sub 2}Cu{sub 3}O{sub 7{minus}x}(YBCO), Bi{sub 2}Sr{sub 2}CaCu{sub 2}O{sub 8}(BSCCO) and La{sub 0.5}Sr{sub 0.5}CoO{sub 3}(LSCO) electrically conductive oxide thin films, that are sequentially deposited by pulsed laser ablation, show that these films may be deposited epitaxially onto LaAlO{sub 3}(LAO) or Si substrates. The conductive oxides are promising candidates for use is electrodes in place of metal electrodes in integrated ferroelectric device applications. The oxide electrodes are more chemically compatible with the ferroelectric films. High resolution electron microscopy his been used to investigate the interfacemore » between the ferroelectric and metal oxide thin films and no reaction was detected. Epitaxial growth is possible due to the similar crystal structures and the small lattice mismatch. The lattice mismatch that is present causes the domains in the ferroelectric films to be preferentially oriented and in the case of lead titanate, the film is single domain. These films may also have potential applications in integrated optical devices.« less

The Comparison of Detrital Zircon Ages to Point Count Provenance Analysis for the Pottsville Sandstone in the Northern Appalachian Foreland Basin Venango County, Pennsylvania

NASA Astrophysics Data System (ADS)

Loveday, S.; Harris, D. B.; Schiappa, T.; Pecha, M.

2017-12-01

The specific sources of sediments deposited in the Appalachian basin prior to and immediately following the Alleghenian orogeny has long been a topic of debate. Recent advances in U-Pb dating of detrital zircons have greatly helped to determine some of the sources of these sediments. For this study, sandstone samples were collected from the Pottsville Formation in the northern Appalachian Foreland Basin, Venango County, Pennsylvania to provide supplementary data for previous work that sought to describe the provenance of the same sediments by point counts of thin sections of the same units. Results of this previous work established that the provenance for these units was transitional recycled orogenic, including multiple recycled sediments, and that a cratonic contribution was not able to be determined clearly. The previous results suggested that the paleoenvironment was a fluvial dominated delta prograding in the northern direction. However, no geochronologic data was found during this study to confirm this interpretation. We sought to verify these results by U-Pb analysis of detrital zircons. Samples were collected from the areas where the previous research took place. U-Pb ages were found from sample at the highest elevation and lowest elevation. In the first sample, sample 17SL01 (younger sample stratigraphically), the zircons yield U-Pb age range peaks at 442-468 ma and 1037-1081 ma. The probability density plot for this specific sample displays a complete age gap from 500 ma to 811 ma. In the second sample, sample 17SL03 (older rock stratigraphically), the zircons yield U-Pb ages range peaks of 424-616 ma and 975-1057 ma. This sample doesn't show any ages younger than 424 ma and it doesn't display the sample age gap as sample 17SL01 does. The ages of zircons are consistent with thin section point counting provenance results from previous research suggesting zircon transport from the northern direction.

Magnetic phase composition of strontium titanate implanted with iron ions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dulov, E.N., E-mail: evgeny.dulov@ksu.ru; Ivoilov, N.G.; Strebkov, O.A.

2011-12-15

Highlights: Black-Right-Pointing-Pointer The origin of RT-ferromagnetism in iron implanted strontium titanate. Black-Right-Pointing-Pointer Metallic iron nanoclusters form during implantation and define magnetic behaviour. Black-Right-Pointing-Pointer Paramagnetic at room temperature iron-substituted strontium titanate identified. -- Abstract: Thin magnetic films were synthesized by means of implantation of iron ions into single-crystalline (1 0 0) substrates of strontium titanate. Depth-selective conversion electron Moessbauer spectroscopy (DCEMS) indicates that origin of the samples magnetism is {alpha}-Fe nanoparticles. Iron-substituted strontium titanate was also identified but with paramagnetic behaviour at room temperature. Surface magneto-optical Kerr effect (SMOKE) confirms that the films reveal superparamagnetism (the low-fluence sample) or ferromagnetism (themore » high-fluence sample), and demonstrate absence of magnetic in-plane anisotropy. These findings highlight iron implanted strontium titanate as a promising candidate for composite multiferroic material and also for gas sensing applications.« less

NASA Prototype All Composite Tank Cryogenic Pressure Tests to Failure with Structural Health Monitoring

NASA Technical Reports Server (NTRS)

Werlink, Rudolph J.; Pena, Francisco

2015-01-01

This Paper will describe the results of pressurization to failure of 100 gallon composite tanks using liquid nitrogen. Advanced methods of health monitoring will be compared as will the experimental data to a finite element model. The testing is wholly under NASA including unique PZT (Lead Zirconate Titanate) based active vibration technology. Other technologies include fiber optics strain based systems including NASA AFRC technology, Acoustic Emission, Acellent smart sensor, this work is expected to lead to a practical in-Sutu system for composite tanks.

Polyvinyl alcohol battery separator containing inert filler. [alkaline batteries

NASA Technical Reports Server (NTRS)

Sheibley, D. W.; Hsu, L. C.; Manzo, M. A. (Inventor)

1981-01-01

A cross-linked polyvinyl alcohol battery separator is disclosed. A particulate filler, inert to alkaline electrolyte of an alkaline battery, is incorporated in the separator in an amount of 1-20% by weight, based on the weight of the polyvinyl alcohol, and is dispersed throughout the product. Incorporation of the filler enhances performance and increases cycle life of alkaline batteries when compared with batteries containing a similar separator not containing filler. Suitable fillers include titanates, silicates, zirconates, aluminates, wood floor, lignin, and titania. Particle size is not greater than about 50 microns.

Two-range magnetoelectric sensor

NASA Astrophysics Data System (ADS)

Bichurin, M.; Petrov, V.; Leontyev, V.; Saplev, A.

2017-01-01

In this study, we present a two-range magnetoelectric ME sensor design comprising of permendur (alloy of Fe-Co-V), nickel, and lead zirconate titanate (PZT) laminate composite. A systematic study was conducted to clarify the contribution of magnetostrictive layers variables to the ME response over the applied range of magnetic bias field. The two-range behavior was characterized by opposite sign of the ME response when magnetic dc bias is in different sub-ranges. The ME coefficient as a function of magnetic bias field was found to be dependent on the laminate composite structure.

Mantle metasomatism in the Kaapvaal Craton lithosphere: constraints on the composition of the metasomatic agent from fluid inclusions in MARID-type xenoliths

NASA Astrophysics Data System (ADS)

Konzett, J.; Krenn, K.; Hauzenberger, Ch.

2012-04-01

The emplacement of both group I and group II kimberlites in the Kaapvaal Craton of the Kimberley region in South Africa is associated with an intense metasomatic alteration of the country rocks as evidenced by a diverse suite of xenoliths sampled by the kimberlites mainly comprising metasomatized peridotites and minor MARID-type xenoliths. These are characterized by hydrous potassic silicates and LILE-HFSE-rich titanates. Because the metasomatic agent is not preserved in these rocks its composition has to be inferred from that of the metasomatic assemblages. Here we present for the first time data on fluid inclusions from two MARID-xenoliths sampled by group-I kimberlites of the Kimberley cluster. They provide direct evidence for the nature of the metasomatic fluids involved in kimberlite-related metsomatism. The xenoliths contain phlogopite+K-richterite+diopside+ilmenite±rutile±apatite±zircon. Fluid inclusions with 4-10 µm in size were found in diopside, K-richterite and zircon and contain L+V+one-to-several daughter phases. Investigations with the freezing and heating stage indicate two different chemical systems for the fluids: (1) H2O-NaCl dominant fluids found as L+V+S inclusions in zircon together with abundant needle-like apatite, rutile and phlogopite solid inclusions. The fluid inclusions in part occur along zircon host-rutile/apatite inclusion grain boundaries which indicates that the fluids were trapped during zircon growth. They contain 30-32 mass% NaCl and show a density of 0.87-0.94 g/cm3. Halos of tiny fluid inclusions, however, indicate that most if not all zircon inclusions are decrepitated during ascent from depth and/or superheating during entrainment of the xenoliths into the kimberlite. Using EMPA, enstatite and a SiO2 polymorph were identified in opened fluid inclusions exposed at the surface of polished thin sections. Because these phases were exclusively found in the fluid inclusions, they are considered daughter crystals. The enstatite composition is identical to that found in the matrix of other MARID xenoliths. Projection on a 40 mW/m2 geotherm of Ca-in-opx temperatures yields ˜950°C/˜4 GPa which are thought to be P and T of MARID-crystallization and fluid entrapment; (2) H2O-CaCl2 dominant fluids trapped in diopside and K-richterite as tubular to rounded L+V inclusions. These inclusions have 35-45 mass% CaCl2 and densities of 0.51-0.98 g/cm3 without any evidence for significant NaCl. During heating all inclusions of this type show a solid with Tm in the range 0-30°C which is consistent with the solid being CaCl2 x 6 H2O. This study provides physical evidence for the presence of saline brines during metasomatism associated with kimberlite emplacement on the Kaapvaal Craton and contributes to the growing body of evidence for the important role of Cl in kimberlite evolution and diamond genesis.

At what conditions does zircon grow/dissolve during high-T metamorphism? Relating zircon textures to PT-conditions

NASA Astrophysics Data System (ADS)

Kunz, Barbara E.; Regis, Daniele; Manzotti, Paola; Engi, Martin

2015-04-01

A key question in ziconology is when and how zircon grows during metamorphism. To shed light on zircon forming processes and the corresponding PT-conditions during high-T metamorphism a case study was undertaken. The Ivrea Zone (N-Italy) exposes a lower continental crustal section in which a continuous metamorphic field gradient from amphibolite to granulite facies is documented. This field gradient is thought to reflect protracted heating during late Paleozoic times, with a probable high-T peak in the Permian. We present first results from a primarily textural study supported by U-Pb ages, Th/U ratios and Ti-in-Zrn thermometry. Four types of zircon were identified based on their overgrowth proportions and the preservation of detrital cores. Zircon grains were thus classified as Type1 - detrital grains with no overgrowth or very narrow rims (300 Ma) and appears to reflect an early dehydration phase. Rim2b has Permian ages (median 275 Ma), is by far the most common overgrowth type, found in a wide PT-range. Its development appears related to biotite breakdown. Rim3 is texturally indicative of magmatic zircon, occurs only in diatexites. Rim4 is the latest overgrowth and is locally found at all metamorphic grades. Textural features suggest late fluid-related recrystallization of existing zircon. At lowest grade (675±35°C, 6±2 kbar) zircons show type1 only, overgrowths are too thin to clearly identify the rim type. Further upgrade (~700°C, 7 kbar) type1 and type2 dominate. Type2 zircons show rim1, rim2a and occasionally rim4. At the Mu-out isograd (750±50°C, 8.2±1.4 kbar) most zircons are of type2, now with rim2b instead of 2a, in addition to rim1 and rim4. Near and in granulite facies (to 800°C, 8±2 kbar) mostly zircon type2 and type4 are present. While rim1 gets more narrow with increasing metamorphic grade, rim2b grows significantly thicker. Occasionally rim2a and rim4 occur. Close to the Bt-out isograd (~860°C, 9.2±1.7 kbar), mostly type3 and type4 are found. Rim1 is absent, and rim2b is commonly overgrown by rim3. Above the Bt-out isograd (>870°C, 9.5 kbar) zircon types3 and type4 dominate. Rim1 is missing, while Rim2b is the most common type, often with a thin rim4. Detailed textural features alone often are not sufficient to relate zircon growth zones to PT-conditions. In combination with U-Pb ages, Th/U ratios and Ti-in-Zrn thermometry, however it is possible to link spot ages to PT-conditions.

Assessing the isotopic evolution of S-type granites of the Carlos Chagas Batholith, SE Brazil: Clues from U-Pb, Hf isotopes, Ti geothermometry and trace element composition of zircon

NASA Astrophysics Data System (ADS)

Melo, Marilane G.; Lana, Cristiano; Stevens, Gary; Pedrosa-Soares, Antônio C.; Gerdes, Axel; Alkmin, Leonardo A.; Nalini, Hermínio A.; Alkmim, Fernando F.

2017-07-01

The Carlos Chagas batholith (CCB) is a very large ( 14,000 km2) S-type granitic body formed during the syn-collisional stage of the Araçuaí orogen (southeastern Brazil). Zircons extracted from the CCB record a wide range of U-Pb ages (from 825 to 490 Ma), indicating a complex history of inheritance, magmatic crystallization and partial melting during the evolution of the orogeny. Magmatic zircons (ca. 578-588 Ma) are marked by similar Hf isotope compositions and REE patterns to those of inherited cores (ca. 825-600 Ma), indicating that these aspects of the chemical signature of the magmatic zircons have likely been inherited from the source. The U-Pb ages and initial 176Hf/177Hf ratios from anatectic and metamorphic zircon domains are consistent with a two-stage metamorphic evolution marked by contrasting mechanisms of zircon growth and recrystallization during the orogeny. Ti-in-zircon thermometry is consistent with the findings of previous metamorphic work and indicates that the two metamorphic events in the batholith reached granulite facies conditions (> 800 °C) producing two generations of garnet via fluid-absent partial melting reactions. The oldest metamorphic episode (ca. 570-550 Ma) is recorded by development of thin anatectic overgrowths on older cores and by growth of new anatectic zircon crystals. Both domains have higher initial 176Hf/177Hf values compared to relict cores and display REE patterns typical of zircon that grew contemporaneously with peritectic garnet through biotite-absent fluid partial melting reactions. Hf isotopic and chemical evidences indicate that a second anatectic episode (ca. 535-500 Ma) is only recorded in parts from the CCB. In these rocks, the growth of new anatectic zircon and/or overgrowths is marked by high initial 176Hf/177Hf values and also by formation of second generation of garnet, as indicated by petrographic observations and REE patterns. In addition, some rocks contain zircon crystals formed by solid-state recrystallization of pre-existing zircon, which exhibit similar Hf isotope composition to those of inherited/magmatic core domains. The first anatectic event is interpreted as result of crustal thickening after the intrusion of the batholith. This introduced the batholith to a depth in excess of 30 km and produced widespread anatexis throughout the batholith. The second event was associated with asthenospheric upwelling during extensional thinning and gravitational collapse of the orogen, this produced anatexis in parts from the CCB that had been re-fertilized for anatexis by retrogression along shear zones following the first granulite facies event.

Control of crystallographic texture and surface morphology of Pt/Tio2 templates for enhanced PZT thin film texture.

PubMed

Fox, Austin J; Drawl, Bill; Fox, Glen R; Gibbons, Brady J; Trolier-McKinstry, Susan

2015-01-01

Optimized processing conditions for Pt/TiO2/SiO2/Si templating electrodes were investigated. These electrodes are used to obtain [111] textured thin film lead zirconate titanate (Pb[ZrxTi1-x ]O3 0 ≤ x ≤ 1) (PZT). Titanium deposited by dc magnetron sputtering yields [0001] texture on a thermally oxidized Si wafer. It was found that by optimizing deposition time, pressure, power, and the chamber pre-conditioning, the Ti texture could be maximized while maintaining low surface roughness. When oxidized, titanium yields [100]-oriented rutile. This seed layer has as low as a 4.6% lattice mismatch with [111] Pt; thus, it is possible to achieve strongly oriented [111] Pt. The quality of the orientation and surface roughness of the TiO2 and the Ti directly affect the achievable Pt texture and surface morphology. A transition between optimal crystallographic texture and the smoothest templating surface occurs at approximately 30 nm of original Ti thickness (45 nm TiO2). This corresponds to 0.5 nm (2 nm for TiO2) rms roughness as determined by atomic force microscopy and a full-width at half-maximum (FWHM) of the rocking curve 0002 (200) peak of 5.5/spl degrees/ (3.1/spl degrees/ for TiO2). A Pb[Zr0.52Ti 0.48]O3 layer was deposited and shown to template from the textured Pt electrode, with a maximum [111] Lotgering factor of 87% and a minimum 111 FWHM of 2.4/spl degrees/ at approximately 30 nm of original Ti.

Flexible ultrasonic transducers for structural health monitoring of metals and composites

NASA Astrophysics Data System (ADS)

Kobayashi, M.; Wu, K.-T.; Shih, J.-L.; Jen, C.-K.; Kruger, S. E.

2010-03-01

Flexible ultrasonic transducers (FUTs) which have the on-site installation capability are presented for the non-destructive evaluation (NDE) and structural health monitoring (SHM) purposes. These FUTs consist of 75 μm thick titanium membrane, thick (> 70 μm) thick piezoelectric lead-zirconate-titanate (PZT) composite (PZT-c) films and thin (< 5 μm) thick top electrodes. The PZT-c films are made by a sol-gel spray technique. Such FUT has been glued onto a steel pipe of 101 mm in diameter and 4.5 mm in wall thickness and operated up to 200°C. The glue served as high temperature ultrasonic couplant between the FUT and the external surface of the pipe. The estimated pipe thickness measurement accuracy at 200°C is 34 μm. FUTs also were glued onto the end edge of 2 mm thick aluminum (Al) plates to generate and receive predominantly symmetrical and shear-horizontal (SH) plate acoustic waves (PAWs) to detect simulated line defects at temperature up to 100°C. FUTs glued onto a graphite/epoxy (Gr/Ep) composite are also used for the detection of artificial disbonds. An induction type non-contact method for the evaluation of Al plates and Gr/Ep composites using FUTs is also demonstrated.

Travelling wave ultrasonic motor using the B08 flexural mode of a circular membrane.

PubMed

Rayner, P J; Whatmore, R W

2001-05-01

This paper describes the design, construction, and performance of a piezoelectric motor that uses the travelling B08 mode of an 80-mm diameter circular membrane to drive a rotor by frictional contact. The motor is of a thin planar design, giving high torque of up to 0.33 Nm at low speed and has been developed as a design that can be made with lithographic techniques for miniaturization. Investigations of the free stator with a vibration pattern imager and impedance analyzer gave the resonance frequency, mode, and electromechanical coupling of the stator. Motor speed as a function of frequency for a constant voltage and performance charts of speed, output power, and efficiency against torque are presented for a particular input voltage and rotor pre-load. The effects of two different lead zirconate titanate (PZT) ring dimensions have been investigated. Excitation of the B09 mode has been observed, incommensurate with the piezoelectric excitation of the stator. This is discussed with relation to edge-clamping of the stator. Single standing wave motoring was observed, believed to arise from asymmetry of the stator and its perturbation of the B08 resonance mode. Sources of power loss, including frame vibration and friction interface slip, are considered and discussed.

Optimizing Pt/TiO2 templates for textured PZT growth and MEMS devices

NASA Astrophysics Data System (ADS)

Potrepka, Daniel; Fox, Glenn; Sanchez, Luz; Polcawich, Ronald

2013-03-01

Crystallographic texture of lead zirconate titanate (PZT) thin films strongly influences piezoelectric properties used in MEMS applications. Textured growth can be achieved by relying on crystal growth habit and can also be initiated by the use of a seed-layer heteroepitaxial template. Template choice and the process used to form it determine structural quality, ultimately influencing performance and reliability of MEMS PZT devices such as switches, filters, and actuators. This study focuses on how 111-textured PZT is generated by a combination of crystal habit and templating mechanisms that occur in the PZT/bottom-electrode stack. The sequence begins with 0001-textured Ti deposited on thermally grown SiO2 on a Si wafer. The Ti is converted to 100-textured TiO2 (rutile) through thermal oxidation. Then 111-textured Pt can be grown to act as a template for 111-textured PZT. Ti and Pt are deposited by DC magnetron sputtering. TiO2 and Pt film textures and structure were optimized by variation of sputtering deposition times, temperatures and power levels, and post-deposition anneal conditions. The relationship between Ti, TiO2, and Pt texture and their impact on PZT growth will be presented. Also affiliated with U.S. Army Research Lab, Adelphi, MD 20783, USA

An analysis of lead-free (Bi{sub 0.5}Na{sub 0.5}){sub 0.915}-(Bi{sub 0.5}K{sub 0.5}){sub 0.05}Ba{sub 0.02}Sr{sub 0.015}TiO{sub 3} ceramic for efficient refrigeration and thermal energy harvesting

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vats, Gaurav; Vaish, Rahul, E-mail: rahul@iitmandi.ac.in; Bowen, Chris R.

This article demonstrates the colossal energy harvesting capability of a lead-free (Bi{sub 0.5}Na{sub 0.5}){sub 0.915}-(Bi{sub 0.5}K{sub 0.5}){sub 0.05}Ba{sub 0.02}Sr{sub 0.015}TiO{sub 3} ceramic using the Olsen cycle. The maximum harvestable energy density estimated for this system is found to be 1523 J/L (1523 kJ/m{sup 3}) where the results are presented for extreme ambient conditions of 20–160 °C and electric fields of 0.1–4 MV/m. This estimated energy density is 1.7 times higher than the maximum reported to date for the lanthanum-doped lead zirconate titanate (thin film) system. Moreover, this study introduces a generalized and effective solid state refrigeration cycle in contrast to the ferroelectric Ericsonmore » refrigeration cycle. The cycle is based on a temperature induced polarization change on application of an unipolar electric field to ferroelectric ceramics.« less

Fabrication and investigation of three-dimensional ferroelectric capacitors for the application of FeRAM

NASA Astrophysics Data System (ADS)

Yeh, Chia-Pin; Lisker, Marco; Kalkofen, Bodo; Burte, Edmund P.

2016-03-01

Ferroelectric capacitors made by lead zirconate titanate (PZT) thin films and iridium electrodes are fabricated on three-dimensional structures and their properties are investigated. The iridium films are grown by Plasma Enhanced MOCVD at 300°C, while the PZT films are deposited by thermal MOCVD at different process temperatures between 450°C and 550°C. The step coverage and composition uniformity of the PZT films on trench holes and lines are investigated. Phase separation of PZT films has been observed on both 3D and planar structures. No clear dependences of the crystallization and composition of PZT on 3D structure topography have been found. STEM EDX line scans show a uniform Zr/(Zr+Ti) concentration ratio along the 3D profile but the variation of the Pb/(Zr+Ti) concentration ratio is large because of the phase separation. 3D ferroelectric capacitors show good ferroelectric properties but have much higher leakage currents than 2D ferroelectric capacitors. Nevertheless, during cycling tests the degradation of the remnant polarization between 2D and 3D capacitors is similar after 109 switching cycles. In addition, the sidewalls and bottoms of the 3D structures seem to have comparable remnant polarizations with the horizontal top surfaces.

Fabrication and Evaluation of One-Axis Oriented Lead Zirconate Titanate Films Using Metal-Oxide Nanosheet Interface Layer

NASA Astrophysics Data System (ADS)

Minemura, Yoshiki; Nagasaka, Kohei; Kiguchi, Takanori; Konno, Toyohiko J.; Funakubo, Hiroshi; Uchida, Hiroshi

2013-09-01

Nanosheet Ca2Nb3O20 (ns-CN) layers with pseudo-perovskite-type crystal configuration were applied on the surface of polycrystalline metal substrates to achieve preferential crystal orientation of Pb(Zr,Ti)O3 (PZT) films for the purpose of enhanced ferroelectricity comparable to that of epitaxial thin films. PZT films with tetragonal symmetry (Zr/Ti=0.40:0.60) were fabricated by chemical solution deposition (CSD) on ns-CN-buffered Inconel 625 and SUS 316L substrates, while ns-CN was applied on the the substrates by dip-coating. The preferential crystal growth on the ns-CN layer can be achieved by favorable lattice matching between (001)/(100)PZT and (001)ns-CN planes. The degree of (001) orientation was increased for PZT films on ns-CN/Inconel 625 and ns-CN/SUS 316L substrates, whereas randomly-oriented PZT films with a lower degree of (001) orientation were grown on bare and Inconel 625 films. Enhanced remanent polarization of 60 µC/cm2 was confirmed for the PZT films on ns-CN/metal substrates, ascribed to the preferential alignment of the polar [001] axis normal to the substrate surface, although it also suffered from higher coercive field above 500 kV/cm caused by PZT/metal interfacial reaction.

Recent Progress in Understanding the Shock Response of Ferroelectric Ceramics

NASA Astrophysics Data System (ADS)

Setchell, R. E.

2002-07-01

Ferroelectric ceramics exhibit a permanent remanent polarization, and shock depoling of these materials to achieve pulsed sources of electrical power was proposed in the late 1950s. During the following twenty years, extensive studies were conducted to examine the shock response of ferroelectric ceramics primarily based on lead zirconate titanate (PZT). Under limited conditions, relatively simple analytical models were found to adequately describe the observed electrical behavior. A more complex behavior was indicated over broader conditions, however, resulting in the incorporation of shock-induced conductivity and dielectric relaxation into analytical models. Unfortunately, few experimental studies were undertaken over the next twenty years, and the development of more comprehensive models was inhibited. In recent years, a strong interest in advancing numerical simulation capabilities has motivated new experimental studies and corresponding model development. More than seventy gas gun experiments have examined several ferroelectric ceramics, with most experiments on lead zirconate titanate having a Zr:Ti ratio of 95:5 and modified with 2% niobium (PZT 95/5). This material is nominally ferroelectric but is near an antiferroelectric phase boundary, and depoling results from a shock-driven phase transition. Experiments have examined unpoled, normally poled, and axially poled PZT 95/5 over broad ranges of shock pressure and peak electric field. The extensive base of new data provides quantitative insights into both the stress and field dependencies of depoling kinetics, and the significance of pore collapse at higher stresses. The results are being actively utilized to develop and refine material response models used in numerical simulations of pulsed power devices.

Effect of off-center ion substitution in morphotropic lead zirconate titanate composition

NASA Astrophysics Data System (ADS)

Bhattarai, Mohan K.; Pavunny, Shojan P.; Instan, Alvaro A.; Scott, James F.; Katiyar, Ram S.

2017-05-01

A detailed study of the effect of off-center donor ion (Sc3+) substitution on structural, microstructural, optical, dielectric, electrical, and ferroelectric properties of morphotropic composition of lead zirconate titanate electroceramics with the stoichiometric formula Pb0.85Sc0.10Zr0.53Ti0.47O3 (PSZT) and synthesized using a high energy solid-state reaction technique was carried out. Powder x-ray diffractometry was used to identify the stabilized tetragonal phase (space group P 4 m m ) with considerably reduced tetragonal strain, c /a = 1.005. An analysis of the thermal dependence of the Raman results indicated a smooth displacive (ferroelectric-paraelectric) phase transition as revealed by the observed disappearance of the soft modes A1 (1TO) and A1 (2TO) above 460 K. The dielectric response of Pt/PSZT/Pt metal-ferroelectric-metal capacitors was probed over a wide range of thermal excursions (85-600 K) and ac signal frequencies (102-106 Hz). Thermally activated dynamic and static conduction processes indicate hopping conduction mechanism ( Ea c t ≤ 0.015 eV) and the formation of small polarons caused by the electron and/or hole-lattice (phonon) interaction ( Ea c t ≥ 0.1 eV) at low (100-300 K) and high temperatures (300-600 K), respectively. The reduction in remnant polarization obtained is in good agreement with the largely reduced tetragonal strain observed in this sample, ( Pr ∝ √{c /a -1 } ). DC conduction is dominated by Poole-Frenkel mechanism that assumes a Coulombic attraction between detrapped electrons and positively charged stationary defect species in the polycrystalline matrix.

Evaluation of antibacterial properties of Barium Zirconate Titanate (BZT) nanoparticle

PubMed Central

Mohseni, Simin; Aghayan, Mahdi; Ghorani-Azam, Adel; Behdani, Mohammad; Asoodeh, Ahmad

2014-01-01

So far, the antibacterial activity of some organic and inorganic compounds has been studied. Barium zirconate titanate [Ba(ZrxTi1-x)O3] (x = 0.05) nanoparticle is an example of inorganic materials. In vitro studies have provided evidence for the antibacterial activity of this nanoparticle. In the current study, the nano-powder was synthesized by sol-gel method. X-ray diffraction showed that the powder was single-phase and had a perovskite structure at the calcination temperature of 1000 °C. Antibacterial activity of the desired nanoparticle was assessed on two gram-positive (Staphylococcus aureus PTCC1431 and Micrococcus luteus PTCC1625) and two gram-negative (Escherichia coli HP101BA 7601c and clinically isolated Klebsiella pneumoniae) bacteria according to Radial Diffusion Assay (RDA). The results showed that the antibacterial activity of BZT nano-powder on both gram-positive and gram-negative bacteria was acceptable. The minimum inhibitory concentration of this nano-powder was determined. The results showed that MIC values for E. coli, K. pneumoniae, M. luteus and S. aureus were about 2.3 μg/mL, 7.3 μg/mL, 3 μg/mL and 12 μg/mL, respectively. Minimum bactericidal concentration (MBC) was also evaluated and showed that the growth of E. coli, K. pneumoniae, M. luteus and S. aureus could be decreased at 2.3, 14, 3 and 18 μg/mL of BZT. Average log reduction in viable bacteria count in time-kill assay ranged between 6 Log10 cfu/mL to zero after 24 h of incubation with BZT nanoparticle. PMID:25763046

Microwave emission from lead zirconate titanate induced by impulsive mechanical load

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aman, A., E-mail: alexander.aman@ovgu.de; Packaging Group, Institute of Micro- and Sensorsytems, Otto-von-Guericke University, Universitätsplatz 2, 39106 Magdeburg; Majcherek, S.

2015-10-28

This paper focuses on microwave emission from Lead zirconate titanate Pb [Zr{sub x}Ti{sub 1−x}] O{sub 3} (PZT) induced by mechanical stressing. The mechanical stress was initiated by impact of a sharp tungsten indenter on the upper surface of PZT ceramic. The sequences of microwave and current impulses, which flew from indenter to electric ground, were detected simultaneously. The voltage between the upper and lower surface of ceramic was measured to obtain the behavior of mechanical force acting on ceramic during the impact. It was found that the amplitude, form, and frequency of measured microwave impulses were different by compression andmore » restitution phase of impact. Two different mechanisms of electron emission, responsible for microwave impulse generation, were proposed based on the dissimilar impulse behavior. The field emission from tungsten indenter is dominant during compression, whereas ferroemission dominates during restitution phase. Indeed, it was observed that the direction of the current flow, i.e., sign of current impulses is changed by transitions from compression to restitution phase of impact. The observed dissimilar behavior of microwave impulses, caused by increasing and decreasing applied force, can be used to calculate the contact time and behavior of mechanical force during mechanical impact on ceramic surface. It is shown that the generation of microwave impulses exhibits high reproducibility, impulse intensity, a low damping factor, and high mechanical failure resistance. Based on these microwave emission properties of PZT, the development of new type of stress sensor with spatial resolution of few microns becomes possible.« less

Fabrication of Crack-Free Barium Titanate Thin Film with High Dielectric Constant Using Sub-Micrometric Scale Layer-by-Layer E-Jet Deposition

PubMed Central

Liang, Junsheng; Li, Pengfei; Wang, Dazhi; Fang, Xu; Ding, Jiahong; Wu, Junxiong; Tang, Chang

2016-01-01

Dense and crack-free barium titanate (BaTiO3, BTO) thin films with a thickness of less than 4 μm were prepared by using sub-micrometric scale, layer-by-layer electrohydrodynamic jet (E-jet) deposition of the suspension ink which is composed of BTO nanopowder and BTO sol. Impacts of the jet height and line-to-line pitch of the deposition on the micro-structure of BTO thin films were investigated. Results show that crack-free BTO thin films can be prepared with 4 mm jet height and 300 μm line-to-line pitch in this work. Dielectric constant of the prepared BTO thin film was recorded as high as 2940 at 1 kHz at room temperature. Meanwhile, low dissipation factor of the BTO thin film of about 8.6% at 1 kHz was also obtained. The layer-by-layer E-jet deposition technique developed in this work has been proved to be a cost-effective, flexible and easy to control approach for the preparation of high-quality solid thin film. PMID:28787860

Separating Multiple Episodes of Partial Melting in Polyorogenic Crust: AN Example from the Haiyangsuo Complex, Northern Sulu Belt, Eastern China

NASA Astrophysics Data System (ADS)

Feng, P.; Wang, L.; Brown, M.; Wang, S.

2017-12-01

Determining the timing, mechanism and source of partial melts in polyorogenic crust is challenging. In the Sulu belt, the tectonic affinity of the Haiyangsuo (HYS) complex is controversial due to its polyphase metamorphic history. Here we use detailed field mapping, petrology, microstructural analysis and zircon geochronology to study thin stromatic leucosomes in host granite gneiss, and crosscutting leucogranite dykes to decipher the melting history. Zircon grains from both granite gneiss and thin leucosomes exhibit core-mantle-rim structures. Zircon cores yield protolith ages of 2.86-2.81 Ga, whereas the mantles and rims yield younger metamorphic/melt crystallization ages of ca. 1.82-1.80 Ga. The mantles are characterized by gray luminescence, flat HREE distribution patterns and relatively low Th/U ratios, indicating crystallization during granulite-facies metamorphism. Whereas rims show bright luminescence, steep HREE distribution patterns and higher Th/U ratios, suggesting they crystallized from melt. The mantles and rims have ɛHf (t) of -18.2 to -11.0. Using 176Lu/177Hf = 0.001, these data project back to the array of ɛHf (t) values for the zircon cores. This demonstrates that the thin leucosomes were derived from the gneiss without any mass input from a mantle source. These features are consistent with an origin of the HYS as part of the eastern margin of the NCC prior to juxtaposition with the Sulu belt. Zircons from the leucogranite dykes also show core-mantle-rim structure. Inherited cores yield concordant 206Pb/238U ages of 776-701 Ma consistent with the dominant age range for protoliths of the UHP metamorphic rocks in the Sulu belt. Zircon mantle and rim domains, which both contain multiphase solid inclusions (Kfs + Pl + Qz and Hem + Pl + Qz in mantles and Kfs + Pl + Qz + Bt in rims), yield melt crystallization ages of 226-217 and 169-156 Ma, respectively. High Sr, low Y and Yb contents, high Sr/Y ratios, and the range of ɛNd (t) values (-18.2- -15.0) and initial 87Sr/86Sr ratios (0.7106 - 0.7146) for the leucogranites are consistent with melting of thickened lower continental crust of the Sulu belt. We interpret the dykes to have been emplaced during post-collisional collapse of the orogenic root of this belt in the Middle-Upper Jurassic.

Control of piezoelectricity in amino acids by supramolecular packing

NASA Astrophysics Data System (ADS)

Guerin, Sarah; Stapleton, Aimee; Chovan, Drahomir; Mouras, Rabah; Gleeson, Matthew; McKeown, Cian; Noor, Mohamed Radzi; Silien, Christophe; Rhen, Fernando M. F.; Kholkin, Andrei L.; Liu, Ning; Soulimane, Tewfik; Tofail, Syed A. M.; Thompson, Damien

2018-02-01

Piezoelectricity, the linear relationship between stress and induced electrical charge, has attracted recent interest due to its manifestation in biological molecules such as synthetic polypeptides or amino acid crystals, including gamma (γ) glycine. It has also been demonstrated in bone, collagen, elastin and the synthetic bone mineral hydroxyapatite. Piezoelectric coefficients exhibited by these biological materials are generally low, typically in the range of 0.1-10 pm V-1, limiting technological applications. Guided by quantum mechanical calculations we have measured a high shear piezoelectricity (178 pm V-1) in the amino acid crystal beta (β) glycine, which is of similar magnitude to barium titanate or lead zirconate titanate. Our calculations show that the high piezoelectric coefficients originate from an efficient packing of the molecules along certain crystallographic planes and directions. The highest predicted piezoelectric voltage constant for β-glycine crystals is 8 V mN-1, which is an order of magnitude larger than the voltage generated by any currently used ceramic or polymer.

The anhysteretic polarisation of ferroelectrics

NASA Astrophysics Data System (ADS)

Kaeswurm, B.; Segouin, V.; Daniel, L.; Webber, K. G.

2018-02-01

Measurement and calculation of anhysteretic curves is a well-established method in the field of magnetic materials and is applied to ferroelectric materials here. The anhysteretic curve is linked to a stable equilibrium state in the domain structure, and ignores dissipative effects related to mechanisms such as domain wall pinning. In this study, an experimental method for characterising the anhysteretic behaviour of ferroelectrics is presented, which is subsequently used to determine the anhysteretic polarisation response of polycrystalline barium titanate and a doped lead zirconate titanate composition at room temperature. Various external parameters, such as electric field, stress, and temperature, can significantly affect ferroelectric behaviour. Ferroelectric hysteresis curves can assess the importance of such effects but cannot distinguish their contribution on the different intrinsic and extrinsic mechanisms involved in ferroelectric behaviour. In this work, the influence of compressive stress on the anhysteretic polarisation is measured and discussed. The comparison of the polarization loop to the anhysteretic curve under compressive stress elucidates the effects on the stable equilibrium domain configuration and dynamic effects associated to dissipation.

Control of piezoelectricity in amino acids by supramolecular packing.

PubMed

Guerin, Sarah; Stapleton, Aimee; Chovan, Drahomir; Mouras, Rabah; Gleeson, Matthew; McKeown, Cian; Noor, Mohamed Radzi; Silien, Christophe; Rhen, Fernando M F; Kholkin, Andrei L; Liu, Ning; Soulimane, Tewfik; Tofail, Syed A M; Thompson, Damien

2018-02-01

Piezoelectricity, the linear relationship between stress and induced electrical charge, has attracted recent interest due to its manifestation in biological molecules such as synthetic polypeptides or amino acid crystals, including gamma (γ) glycine. It has also been demonstrated in bone, collagen, elastin and the synthetic bone mineral hydroxyapatite. Piezoelectric coefficients exhibited by these biological materials are generally low, typically in the range of 0.1-10 pm V -1 , limiting technological applications. Guided by quantum mechanical calculations we have measured a high shear piezoelectricity (178 pm V -1 ) in the amino acid crystal beta (β) glycine, which is of similar magnitude to barium titanate or lead zirconate titanate. Our calculations show that the high piezoelectric coefficients originate from an efficient packing of the molecules along certain crystallographic planes and directions. The highest predicted piezoelectric voltage constant for β-glycine crystals is 8 V mN -1 , which is an order of magnitude larger than the voltage generated by any currently used ceramic or polymer.

Characterization of barium strontium titanate thin films on sapphire substrate prepared via RF magnetron sputtering system

NASA Astrophysics Data System (ADS)

Jamaluddin, F. W.; Khalid, M. F. Abdul; Mamat, M. H.; Zoolfakar, A. S.; Zulkefle, M. A.; Rusop, M.; Awang, Z.

2018-05-01

Barium Strontium Titanate (Ba0.5Sr0.5TiO3) is known to have a high dielectric constant and low loss at microwave frequencies. These unique features are useful for many electronic applications. This paper focuses on material characterization of BST thin films deposited on sapphire substrate by RF magnetron sputtering system. The sample was then annealed at 900 °C for two hours. Several methods were used to characterize the structural properties of the material such as X-ray diffraction (XRD) and atomic force microscopy (AFM). Field emission scanning electron microscopy (FESEM) was used to analyze the surface morphology of the thin film. From the results obtained, it can be shown that the annealed sample had a rougher surface and better crystallinity as compared to as-deposited sample.

Multilayer bioactive glass/zirconium titanate thin films in bone tissue engineering and regenerative dentistry

PubMed Central

Mozafari, Masoud; Salahinejad, Erfan; Shabafrooz, Vahid; Yazdimamaghani, Mostafa; Vashaee, Daryoosh; Tayebi, Lobat

2013-01-01

Surface modification, particularly coatings deposition, is beneficial to tissue-engineering applications. In this work, bioactive glass/zirconium titanate composite thin films were prepared by a sol-gel spin-coating method. The surface features of the coatings were studied by scanning electron microscopy, atomic force microscopy, and spectroscopic reflection analyses. The results show that uniform and sound multilayer thin films were successfully prepared through the optimization of the process variables and the application of carboxymethyl cellulose as a dispersing agent. Also, it was found that the thickness and roughness of the multilayer coatings increase nonlinearly with increasing the number of the layers. This new class of nanocomposite coatings, comprising the bioactive and inert components, is expected not only to enhance bioactivity and biocompatibility, but also to protect the surface of metallic implants against wear and corrosion. PMID:23641155

Electrical characteristics of paraelectric lead lanthanum zirconium titanate thin films for dynamic random access memory applications

NASA Astrophysics Data System (ADS)

Jones, R. E., Jr.; Maniar, P. D.; Olowolafe, J. O.; Campbell, A. C.; Mogab, C. J.

1992-02-01

Paraelectric lead lanthanum zirconium titanate (PLZT) films, 150 nm thick, were deposited using a spin-coat, sol-gel process followed by a 650 °C oxygen anneal. X-ray diffraction indicated complete conversion to the perovskite phase. Sputter-deposited platinum electrodes were employed with the PLZT films to form thin-film capacitors with the best combination of high charge storage density (26.1 μC/cm2 at 3 V and 36.4 μC/cm2 at 5 V) and leakage current density (0.2 μA/cm2 at 3 V and 0.5 μA/cm2 at 5 V ) reported to date. The electrical characteristics of these thin-film capacitors meet the requirements for a planar bit cell capacitor for 64-Mbit dynamic random access memories.

Thick-film acoustic emission sensors for use in structurally integrated condition-monitoring applications.

PubMed

Pickwell, Andrew J; Dorey, Robert A; Mba, David

2011-09-01

Monitoring the condition of complex engineering structures is an important aspect of modern engineering, eliminating unnecessary work and enabling planned maintenance, preventing failure. Acoustic emissions (AE) testing is one method of implementing continuous nondestructive structural health monitoring. A novel thick-film (17.6 μm) AE sensor is presented. Lead zirconate titanate thick films were fabricated using a powder/sol composite ink deposition technique and mechanically patterned to form a discrete thick-film piezoelectric AE sensor. The thick-film sensor was benchmarked against a commercial AE device and was found to exhibit comparable responses to simulated acoustic emissions.

Optoenergy storage and random walks assisted broadband amplification in Er3+-doped (Pb,La)(Zr,Ti)O3 disordered ceramics.

PubMed

Xu, Long; Zhao, Hua; Xu, Caixia; Zhang, Siqi; Zou, Yingyin K; Zhang, Jingwen

2014-02-01

A broadband optical amplification was observed and investigated in Er3+-doped electrostrictive ceramics of lanthanum-modified lead zirconate titanate under a corona atmosphere. The ceramic structure change caused by UV light, electric field, and random walks originated from the diffusive process in intrinsically disordered materials may all contribute to the optical amplification and the associated energy storage. Discussion based on optical energy storage and diffusive equations was given to explain the findings. Those experiments performed made it possible to study random walks and optical amplification in transparent ceramics materials.

New fabrication of high-frequency (100-MHz) ultrasound PZT film kerfless linear array.

PubMed

Zhu, Benpeng; Chan, Ngai Yui; Dai, Jiyan; Shung, K Kirk; Takeuchi, Shinichi; Zhou, Qifa

2013-04-01

The paper describes the design, fabrication, and measurements of a high-frequency ultrasound kerfless linear array prepared from hydrothermal lead zirconate titanate (PZT) thick film. The 15-μm hydrothermal PZT thick film with an area of 1 × 1 cm, obtained through a self-separation process from Ti substrate, was used to fabricate a 32-element 100-MHz kerfless linear array with photolithography. The bandwidth at -6 dB without matching layer, insertion loss around center frequency, and crosstalk between adjacent elements were measured to be 39%, -30 dB, and -15 dB, respectively.

Regenerable sorbents for CO.sub.2 capture from moderate and high temperature gas streams

DOEpatents

Siriwardane, Ranjani V [Morgantown, WV

2008-01-01

A process for making a granular sorbent to capture carbon dioxide from gas streams comprising homogeneously mixing an alkali metal oxide, alkali metal hydroxide, alkaline earth metal oxide, alkaline earth metal hydroxide, alkali titanate, alkali zirconate, alkali silicate and combinations thereof with a binder selected from the group consisting of sodium ortho silicate, calcium sulfate dihydrate (CaSO.sub.4.2H.sub.2O), alkali silicates, calcium aluminate, bentonite, inorganic clays and organic clays and combinations thereof and water; drying the mixture and placing the sorbent in a container permeable to a gas stream.

Effects of Polarization on Mechanical Properties of Lead Zirconate Titanate Ceramics Evaluated by Modified Small Punch Tests

NASA Astrophysics Data System (ADS)

Deng, Qihuang; Fan, Yuchi; Wang, Lianjun; Xiong, Zhi; Wang, Hongzhi; Li, Yaogang; Zhang, Qinghong; Kawasaki, Akira; Jiang, Wan

2012-01-01

Pb(Zr,Ti)O3 (PZT) ceramics were prepared by the conventional mixed oxide method, and the strength of the resultant PZT ceramics was evaluated using modified small punch (MSP) tests. Load-displacement curve test results showed that the crack-initiation and fracture strengths of PZT ceramics decreased after polarization. The effect of the polarization accelerated the fatigue properties of PZT ceramics. Scanning electron microscopy (SEM) results showed that microcracks were formed before the maximum load in the MSP test, and the first load drop corresponded to crack initiation.

Voltage generation of piezoelectric cantilevers by laser heating

PubMed Central

Hsieh, Chun-Yi; Liu, Wei-Hung; Chen, Yang-Fang; Shih, Wan Y.; Gao, Xiaotong; Shih, Wei-Heng

2012-01-01

Converting ambient thermal energy into electricity is of great interest in harvesting energy from the environment. Piezoelectric cantilevers have previously been shown to be an effective biosensor and a tool for elasticity mapping. Here we show that a single piezoelectric (lead-zirconate titanate (PZT)) layer cantilever can be used to convert heat to electricity through pyroelectric effect. Furthermore, piezoelectric-metal (PZT-Ti) bi-layer cantilever showed an enhanced induced voltage over the single PZT layer alone due to the additional piezoelectric effect. This type of device can be a way for converting heat energy into electricity. PMID:23258941

Toward self-assembled ferroelectric random access memories: hard-wired switching capacitor arrays with almost Tb/in.(2) densities.

PubMed

Evans, Paul R; Zhu, Xinhau; Baxter, Paul; McMillen, Mark; McPhillips, John; Morrison, Finlay D; Scott, James F; Pollard, Robert J; Bowman, Robert M; Gregg, J Marty

2007-05-01

We report on the successful fabrication of arrays of switchable nanocapacitors made by harnessing the self-assembly of materials. The structures are composed of arrays of 20-40 nm diameter Pt nanowires, spaced 50-100 nm apart, electrodeposited through nanoporous alumina onto a thin film lower electrode on a silicon wafer. A thin film ferroelectric (both barium titanate (BTO) and lead zirconium titanate (PZT)) has been deposited on top of the nanowire array, followed by the deposition of thin film upper electrodes. The PZT nanocapacitors exhibit hysteresis loops with substantial remnant polarizations, while although the switching performance was inferior, the low-field characteristics of the BTO nanocapacitors show dielectric behavior comparable to conventional thin film heterostructures. While registration is not sufficient for commercial RAM production, this is nevertheless an embryonic form of the highest density hard-wired FRAM capacitor array reported to date and compares favorably with atomic force microscopy read-write densities.

Thermal properties and dynamic mechanical properties of ceramic fillers filled epoxy composites

NASA Astrophysics Data System (ADS)

Saidina, D. S.; Mariatti, M.; Juliewatty, J.

2015-07-01

This present study is aimed to enhance the thermal and dynamic mechanical properties of ceramic fillers such as Calcium Copper Titanate, CaCu3Ti4O12 (CCTO) and Barium Titanate (BaTiO3) filled epoxy thin film composites. As can be seen from the results, 20 vol% BaTiO3/epoxy thin film composite showed the lowest coefficient of thermal expansion (CTE) value, the highest decomposition temperature (T5 and Tonset) and weight of residue among the composites as the filler has low CTE value, distributed homogeneously throughout the composite and less voids can be seen between epoxy resin and BaTiO3 filler.

Provenance and metamorphic PT conditions of Cryogenian-Ediacaran metasediments from the Kid metamorphic complex, Sinai, NE Arabian-Nubian Shield: Insights from detrital zircon geochemistry and mineral chemistry

NASA Astrophysics Data System (ADS)

El-Bialy, Mohammed Z.; Ali, Kamal A.; Abu El-Enen, Mahrous M.; Ahmed, Ahmed H.

2015-12-01

The Malhaq and Um Zariq formations occupy the northern part of the Neoproterozoic Kid metamorphic complex of SE Sinai, NE Arabian-Nubian Shield. This study presents new mineral chemistry data and LA-ICP-MS analyses of the trace element concentrations on zircons separated from metapelites from these formations. The detrital zircons of Um Zariq Formation are more enriched in ΣREE, whereas Malhaq Formation zircons are markedly HREE-enriched with strongly fractionated HREE patterns. The quite differences in the overall slope and size of the Eu and Ce anomalies between REE patterns of the two zircon suites provide a robust indication of different sources. The Ti-in-zircon thermometer has revealed that the zircons separated from Malhaq Formation were crystallized within the 916-1018 °C range, while those from Um Zariq Formation exhibit higher range of crystallization temperatures (1084-1154 °C). The detrital zircons of Malhaq Formation were derived mainly from mafic source rocks (basalt and dolerite), whereas Um Zariq Formation zircons have varied and more evolved parent rocks. Most of the investigated zircons from both formations are concluded to be unaltered magmatic that were lately crystallized from a high LREE/HREE melt. All the studied detrital zircon grains show typical trace elements features of crustal-derived zircons. All of the Um Zariq Formation and most of Malhaq Formation detrital zircons are geochemically discriminated as continental zircons. Both formation metapelites record similar, overlapping peak metamorphic temperatures (537-602 °C and 550-579 °C, respectively), and pressures (3.83-4.93 kbar and 3.69-4.07 kbar, respectively). The geothermal gradient, at the peak metamorphic conditions, was quite high (37-41 °C/km) corresponding to metamorphism at burial depth of 14-16 km. The peak regional metamorphism of Um Zariq and Malhaq formations is concluded to be generated during extensional regime and thinning of the lithosphere in an island arc setting with heat flow from the underlying arc granitoids.

Widespread morning drizzle on Titan.

PubMed

Adámkovics, Máté; Wong, Michael H; Laver, Conor; de Pater, Imke

2007-11-09

Precipitation is expected in Titan's atmosphere, yet it has not been directly observed, and the geographical regions where rain occurs are unknown. Here we present near-infrared spectra from the Very Large Telescope and W. M. Keck Observatories that reveal an enhancement of opacity in Titan's troposphere on the morning side of the leading hemisphere. Retrieved extinction profiles are consistent with condensed methane in clouds at an altitude near 30 kilometers and concomitant methane drizzle below. The moisture encompasses the equatorial region over Titan's brightest continent, Xanadu. Diurnal temperature gradients that cause variations in methane relative humidity, winds, and topography may each be a contributing factor to the condensation mechanism. The clouds and precipitation are optically thin at 2.0 micrometers, and models of "subvisible" clouds suggest that the droplets are 0.1 millimeter or larger.

Barium Strontium Titanate Thin Film Growth with rotational speed variation as a satellite temperature sensor prototype

NASA Astrophysics Data System (ADS)

Mulyadi; Rika, W.; Sulidah; Irzaman; Hardhienata, Hendradi

2017-01-01

Barium Strontium Titanate(BST) is a promising material for sensor devices such as temperature and infrared sensor. BaxSr1-xTiO3 thin films with affordable Si substrate were prepared by chemical solution deposition method and spin coating technique for 30 seconds with variation in rotation speed (3000 rpm, 5500 rpm and 8000 rpm). A high baking temperature at 8500C has been used for 15 hours during the annealing process. The thickness of BST film was calculated via gravimetric calculation. USB 2000 VIS-NIR was used to characterize the optical properties of BST thin film. The obtained reflectance curve showed that the most reflected wavelengths were in the range of 408-452 nm respectively. The result of the optical film characterization is very important for further development as a sensor in satellite technology.

Epitaxial growth of lead zirconium titanate thin films on Ag buffered Si substrates using rf sputtering

NASA Astrophysics Data System (ADS)

Wang, Chun; Laughlin, David E.; Kryder, Mark H.

2007-04-01

Epitaxial lead zirconium titanate (PZT) (001) thin films with a Pt bottom electrode were deposited by rf sputtering onto Si(001) single crystal substrates with a Ag buffer layer. Both PZT(20/80) and PZT(53/47) samples were shown to consist of a single perovskite phase and to have the (001) orientation. The orientation relationship was determined to be PZT(001)[110]‖Pt(001)[110]‖Ag(001)[110]‖Si(001)[110]. The microstructure of the multilayer was studied using transmission electron microscopy (TEM). The electron diffraction pattern confirmed the epitaxial relationship between each layer. The measured remanent polarization Pr and coercive field Ec of the PZT(20/80) thin film were 26μC /cm2 and 110kV/cm, respectively. For PZT(53/47), Pr was 10μC /cm2 and Ec was 80kV/cm.

Fabrication and characterization of thick-film piezoelectric lead zirconate titanate ceramic resonators by tape-casting.

PubMed

Qin, Lifeng; Sun, Yingying; Wang, Qing-Ming; Zhong, Youliang; Ou, Ming; Jiang, Zhishui; Tian, Wei

2012-12-01

In this paper, thick-film piezoelectric lead zirconate titanate (PZT) ceramic resonators with thicknesses down to tens of micrometers have been fabricated by tape-casting processing. PZT ceramic resonators with composition near the morphotropic phase boundary and with different dopants added were prepared for piezoelectric transducer applications. Material property characterization for these thick-film PZT resonators is essential for device design and applications. For the property characterization, a recently developed normalized electrical impedance spectrum method was used to determine the electromechanical coefficient and the complex piezoelectric, elastic, and dielectric coefficients from the electrical measurement of resonators using thick films. In this work, nine PZT thick-film resonators have been fabricated and characterized, and two different types of resonators, namely thickness longitudinal and transverse modes, were used for material property characterization. The results were compared with those determined by the IEEE standard method, and they agreed well. It was found that depending on the PZT formulation and dopants, the relative permittivities ε(T)(33)/ε(0) measured at 2 kHz for these thick-films are in the range of 1527 to 4829, piezoelectric stress constants (e(33) in the range of 15 to 26 C/m(2), piezoelectric strain constants (d(31)) in the range of -169 × 10(-12) C/N to -314 × 10(-12) C/N, electromechanical coupling coefficients (k(t)) in the range of 0.48 to 0.53, and k(31) in the range of 0.35 to 0.38. The characterization results shows tape-casting processing can be used to fabricate high-quality PZT thick-film resonators, and the extracted material constants can be used to for device design and application.

Nuclear waste disposal—pyrochlore (A2B2O7): Nuclear waste form for the immobilization of plutonium and "minor" actinides

NASA Astrophysics Data System (ADS)

Ewing, Rodney C.; Weber, William J.; Lian, Jie

2004-06-01

During the past half-century, the nuclear fuel cycle has generated approximately 1400 metric tons of plutonium and substantial quantities of the "minor" actinides, such as Np, Am, and Cm. The successful disposition of these actinides has an important impact on the strategy for developing advanced nuclear fuel cycles, weapons proliferation, and the geologic disposal of high-level radioactive waste. During the last decade, there has been substantial interest in the use of the isometric pyrochlore structure-type, A2B2O7, for the immobilization of actinides. Most of the interest has focused on titanate-pyrochlore because of its chemical durability; however, these compositions experience a radiation-induced transition from the crystalline-to-aperiodic state due to radiation damage from the alpha-decay of actinides. Depending on the actinide concentration, the titanate pyrochlore will become amorphous in less than 1000 years of storage. Recently, systematic ion beam irradiations of a variety of pyrochlore compositions has revealed that many zirconate pyrochlores do not become amorphous, but remain crystalline as a defect fluorite structure-type due to disordering of the A- and B-site cations. The zirconate pyrochlores will remain crystalline even to very high doses, greater than 100 displacements per atom. Systematic experimental studies of actinide-doped and ion beam-irradiated pyrochlore, analyses of natural U- and Th-bearing pyrochlore, and simulations of the energetics of the disordering process now provide a rather detailed understanding of the structural and chemical controls on the response of pyrochlore to radiation. These results provide a solid basis for predicting the behavior and durability of pyrochlore used to immobilize plutonium.

Corrosion Testing of Zirconia, Beryllia and Magnesia Ceramics in Molten Alkali Metal Carbonates at 900°C

NASA Astrophysics Data System (ADS)

Kaplan, Valery; Lubomirsky, Igor

An electrochemical cell containing molten Li2CO3-Li2O has been proposed for the conversion of the greenhouse gas CO2 to CO, which can then either be used to power gas turbines or converted to methanol. Since efficient electrolysis takes place at 900°C, the materials which can be used in such a cell must satisfy stringent requirements. In the current work, we have examined the static corrosion resistance of zirconia, beryllia and magnesia ceramics at 900°C in the Li2CO3-Li2O mixture and in a Li-Na-K carbonate eutectic mixture with the ultimate objective of identifying suitable electrically insulating materials. Conclusions regarding material stability were based on elemental analysis of the melt, primarily via X-ray photoelectron spectroscopy, a particularly sensitive technique. It was found that magnesia is completely stable for at least 33 hrs in a Li2CO3-Li2O melt, while a combined lithium titanate/lithium zirconate layer forms on the zirconia ceramic as detected by XRD. Under the same melt conditions, beryllia shows considerable leaching into solution. In a Li-Na-K carbonate eutectic mixture containing 10.2 mol% oxide at 900°C under standard atmospheric conditions, magnesia showed no signs of degradation. Stabilization of the zirconia content of the eutectic mixture at 0.01-0.02 at% after 2 hrs is again explained by the formation of a lithium titanate/ lithium zirconate coating. On the basis of these results, we conclude that only magnesia can be satisfactorily used as an insulating material in electrolysis cells containing Li2CO3-Li2O melts.

Microelectromechanical systems (MEMS) sensors based on lead zirconate titanate (PZT) films

NASA Astrophysics Data System (ADS)

Wang, Li-Peng

2001-12-01

In this thesis, modeling, fabrication and testing of microelectromechanical systems (MEMS) accelerometers based on piezoelectric lead zirconate titanate (PZT) films are investigated. Three different types of structures, cantilever beam, trampoline, and annular diaphragm, are studied. It demonstrates the high-performance, miniaturate, mass-production-compatible, and potentially circuitry-integratable piezoelectric-type PZT MEMS devices. Theoretical models of the cantilever-beam and trampoline accelerometers are derived via structural dynamics and the constitutive equations of piezoelectricity. The time-dependent transverse vibration equations, mode shapes, resonant frequencies, and sensitivities of the accelerometers are calculated through the models. Optimization of the silicon and PZT thickness is achieved with considering the effects of the structural dynamics, the material properties, and manufacturability for different accelerometer specifications. This work is the first demonstration of the fabrication of bulk-micromachined accelerometers combining a deep-trench reactive ion etching (DRIE) release strategy and thick piezoelectric PZT films deposited using a sol-gel method. Processing challenges which are overcome included materials compatibility, metallization, processing of thick layers, double-side processing, deep-trench silicon etching, post-etch cleaning and process integration. In addition, the processed PZT films are characterized by dielectric, ferroelectric (polarization electric-field hysteresis), and piezoelectric measurements and no adverse effects are found. Dynamic frequency response and impedance resonance measurements are performed to ascertain the performance of the MEMS accelerometers. The results show high sensitivities and broad frequency ranges of the piezoelectric-type PZT MEMS accelerometers; the sensitivities range from 0.1 to 7.6 pC/g for resonant frequencies ranging from 44.3 kHz to 3.7 kHz. The sensitivities were compared to theoretical values and a reasonable agreement (˜36% difference) is obtained.

A three-degree-of-freedom thin-film PZT-actuated microactuator with large out-of-plane displacement.

PubMed

Choi, Jongsoo; Qiu, Zhen; Rhee, Choong-Ho; Wang, Thomas; Oldham, Kenn

2014-07-01

A novel three degree-of-freedom microactuator based on thin-film lead-zirconate-titanate (PZT) is described with its detailed structural model. Its central rectangular-shaped mirror platform, also referred to as the stage, is actuated by four symmetric PZT bending legs such that each leg provides vertical translation for one corner of the stage. It has been developed to support real-time in vivo vertical cross-sectional imaging with a dual axes confocal endomicroscope for early cancer detection, having large displacements in three axes (z, θ x , θ y ) and a relatively high bandwidth in the z-axis direction. Prototype microactuators closely meet the performance requirements for this application; in the out-of-plane (z-axis) direction, it has shown more than 177 μ m of displacement and about 84 Hz of structural natural frequency, when two diagonal legs are actuated at 14V. With all four legs, another prototype of the same design with lighter stage mass has achieved more than 430 μ m of out-of-plane displacement at 15V and about 200 Hz of bandwidth. The former design has shown approximately 6.4° and 2.9° of stage tilting about the x-axis and y-axis, respectively, at 14V. This paper also presents a modeling technique that uses experimental data to account for the effects of fabrication uncertainties in residual stress and structural dimensions. The presented model predicts the static motion of the stage within an average absolute error of 14.6 μ m, which approaches the desired imaging resolution, 5 μ m, and also reasonably anticipates the structural dynamic behavior of the stage. The refined model will support development of a future trajectory tracking controller for the system.

A three-degree-of-freedom thin-film PZT-actuated microactuator with large out-of-plane displacement

PubMed Central

Choi, Jongsoo; Qiu, Zhen; Rhee, Choong-Ho; Wang, Thomas; Oldham, Kenn

2014-01-01

A novel three degree-of-freedom microactuator based on thin-film lead-zirconate-titanate (PZT) is described with its detailed structural model. Its central rectangular-shaped mirror platform, also referred to as the stage, is actuated by four symmetric PZT bending legs such that each leg provides vertical translation for one corner of the stage. It has been developed to support real-time in vivo vertical cross-sectional imaging with a dual axes confocal endomicroscope for early cancer detection, having large displacements in three axes (z, θx, θy) and a relatively high bandwidth in the z-axis direction. Prototype microactuators closely meet the performance requirements for this application; in the out-of-plane (z-axis) direction, it has shown more than 177 μm of displacement and about 84 Hz of structural natural frequency, when two diagonal legs are actuated at 14V. With all four legs, another prototype of the same design with lighter stage mass has achieved more than 430 μm of out-of-plane displacement at 15V and about 200 Hz of bandwidth. The former design has shown approximately 6.4° and 2.9° of stage tilting about the x-axis and y-axis, respectively, at 14V. This paper also presents a modeling technique that uses experimental data to account for the effects of fabrication uncertainties in residual stress and structural dimensions. The presented model predicts the static motion of the stage within an average absolute error of 14.6 μm, which approaches the desired imaging resolution, 5 μm, and also reasonably anticipates the structural dynamic behavior of the stage. The refined model will support development of a future trajectory tracking controller for the system. PMID:25506131

Fitful and protracted magma assembly leading to a giant eruption, Youngest Toba Tuff, Indonesia

USGS Publications Warehouse

Reid, Mary R; Vazquez, Jorge A.

2017-01-01

The paroxysmal eruption of the 74 ka Youngest Toba Tuff (YTT) of northern Sumatra produced an extraordinary 2800 km3 of non-welded to densely welded ignimbrite and co-ignimbrite ash-fall. We report insights into the duration of YTT magma assembly obtained from ion microprobe U-Th and U-Pb dates, including continuous age spectra over >50% of final zircon growth, for pumices and a welded tuff spanning the compositional range of the YTT. A relatively large subpopulation of zircon crystals nucleated before the penultimate caldera-related eruption at 501 ka, but most zircons yielded interior dates 100-300 ka thereafter. Zircon nucleation and growth was likely episodic and from diverse conditions over protracted time intervals of >100 to >500 ka. Final zircon growth is evident as thin rim plateaus that are in Th/U chemical equilibrium with hosts, and that give crystallization ages within tens of ka of eruption. The longevity and chemical characteristics of the YTT zircons, as well as evidence for intermittent zircon isolation and remobilization associated with magma recharge, is especially favored at the cool and wet eutectoid conditions that characterize at least half of the YTT, wherein heat fluxes could dissolve major phases but have only a minor effect on larger zircon crystals. Repeated magma recharge may have contributed to the development of compositional zoning in the YTT but, considered together with limited allanite, quartz, and other mineral dating and geospeedometry, regular perturbations to the magma reservoir over >400 ka did not lead to eruption until 74 ka ago.

Off Axis Growth of Strontium Titanate Films with High Dielectric Constant Tuning and Low Loss

DTIC Science & Technology

2003-04-03

80309, U.S.A. ABSTRACT We have measured the nonlinear dielectric properties of strontium titanate (STO) thin films grown on neodymium gallate (NGO...and lanthanum aluminate (LAO) substrates. The films prepared by off-axis pulsed laser deposition were characterized by their dielectric constant and...performed on the films prepared with the off axis growth. EXPERIMENTAL Pulsed laser deposition (PLD) was used to deposit STO films on lanthanum

Temperature Compensation of Aluminum Nitride Lamb Wave Resonators Utilizing the Lowest-Order Symmetric Mode

DTIC Science & Technology

2012-12-14

PZT ceramic plate [40]. Since then Lamb wave devices utilizing the lowest-order antisymmetric (A0) mode propagation in ZnO thin plate were widely...Million Pt Platinum PVDF Polyvinylidene Flouride PZT Lead Zirconium Titanate Q Quality Factor R Resistor RIE Reactive Ion Etching Rm Motional...GaAs), silicon carbide (SiC), langasite (LGS), lead zirconium titanate ( PZT ), and polyvinylidene flouride (PVDF). Each piezoelectric material has

The seasonal cycle of Titan's detached haze

NASA Astrophysics Data System (ADS)

West, Robert A.; Seignovert, Benoît.; Rannou, Pascal; Dumont, Philip; Turtle, Elizabeth P.; Perry, Jason; Roy, Mou; Ovanessian, Aida

2018-06-01

Titan's `detached' haze, seen in Voyager images in 1980 and 1981 and monitored by the Cassini Imaging Science Subsystem (ISS) during the period 2004-2017, provides a measure of seasonal activity in Titan's mesosphere with observations over almost half of Saturn's seasonal cycle. Here we report on retrieved haze extinction profiles that reveal a depleted layer (having a diminished aerosol content), visually manifested as a gap between the main haze and a thin, detached upper layer. Our measurements show the disappearance of the feature in 2012 and its reappearance in 2016, as well as details after the reappearance. These observations highlight the dynamical nature of the detached haze. The reappearance seems congruent with earlier descriptions by climate models but more complex than previously described. It occurs in two steps, first as haze reappearing at 450 ± 20 km and one year later at 510 ± 20 km. These observations provide additional tight and valuable constraints about the underlying mechanisms, especially for Titan's mesosphere, that control Titan's haze cycle.

The seasonal cycle of Titan's detached haze

NASA Astrophysics Data System (ADS)

West, Robert A.; Seignovert, Benoît; Rannou, Pascal; Dumont, Philip; Turtle, Elizabeth P.; Perry, Jason; Roy, Mou; Ovanessian, Aida

2018-04-01

Titan's `detached' haze, seen in Voyager images in 1980 and 1981 and monitored by the Cassini Imaging Science Subsystem (ISS) during the period 2004-2017, provides a measure of seasonal activity in Titan's mesosphere with observations over almost half of Saturn's seasonal cycle. Here we report on retrieved haze extinction profiles that reveal a depleted layer (having a diminished aerosol content), visually manifested as a gap between the main haze and a thin, detached upper layer. Our measurements show the disappearance of the feature in 2012 and its reappearance in 2016, as well as details after the reappearance. These observations highlight the dynamical nature of the detached haze. The reappearance seems congruent with earlier descriptions by climate models but more complex than previously described. It occurs in two steps, first as haze reappearing at 450 ± 20 km and one year later at 510 ± 20 km. These observations provide additional tight and valuable constraints about the underlying mechanisms, especially for Titan's mesosphere, that control Titan's haze cycle.

Electric properties and phase transition behavior in lead lanthanum zirconate stannate titanate ceramics with low zirconate content

NASA Astrophysics Data System (ADS)

Zeng, Tao; Lou, Qi-Wei; Chen, Xue-Feng; Zhang, Hong-Ling; Dong, Xian-Lin; Wang, Gen-Shui

2015-11-01

The phase transitions, dielectric properties, and polarization versus electric field (P-E) hysteresis loops of Pb0.97La0.02(Zr0.42Sn0.58-xTix)O3 (0.13≤ x ≤0.18) (PLZST) bulk ceramics were systematically investigated. This study exhibited a sequence of phase transitions by analyzing the change of the P-E hysteresis loops with increasing temperature. The antiferroelectric (AFE) to ferroelectric (FE) phase boundary of PLZST with the Zr content of 0.42 was found to locate at the Ti content between 0.14 and 0.15. This work is aimed to improve the ternary phase diagram of lanthanum-doped PZST with the Zr content of 0.42 and will be a good reference for seeking high energy storage density in the PLZST system with low-Zr content. Project supported by the National Natural Science Foundation of China (Grant Nos. 51202273, 11204304, and 11304334) and the Science and Technology Commission of Shanghai Municipality, China (Grant No. 14DZ2261000).

Three-dimensional micro electromechanical system piezoelectric ultrasound transducer

NASA Astrophysics Data System (ADS)

Hajati, Arman; Latev, Dimitre; Gardner, Deane; Hajati, Azadeh; Imai, Darren; Torrey, Marc; Schoeppler, Martin

2012-12-01

Here we present the design and experimental acoustic test data for an ultrasound transducer technology based on a combination of micromachined dome-shaped piezoelectric resonators arranged in a flexible architecture. Our high performance niobium-doped lead zirconate titanate film is implemented in three-dimensional dome-shaped structures, which form the basic resonating cells. Adjustable frequency response is realized by mixing these basic cells and modifying their dimensions by lithography. Improved characteristics such as high sensitivity, adjustable wide-bandwidth frequency response, low transmit voltage compatible with ordinary integrated circuitry, low electrical impedance well matched to coaxial cabling, and intrinsic acoustic impedance match to water are demonstrated.

Study of x CNFO + (1-x) PLZT magnetoelectric composites

NASA Astrophysics Data System (ADS)

Dipti, Singh, Sangeeta; Juneja, J. K.; Pant, R. P.; Raina, K. K.; Prakash, Chandra

2014-04-01

In the present paper, we are reporting the studies on structural, dielectric, ferroelectric and magnetic properties of Lanthanum (La) substituted Lead Zirconate Titanate (PZT) and Cobalt Nickel ferrite (CNFO) composites with compositional formula x(Co0.80Ni0.20Fe2O4)+(1-x)(Pb1.01625La0.0025Zr0.55Ti0.45O3) (x = 0.00,0.10). The materials were synthesized by solid state reaction route. XRD analysis confirms the presence of both ferrite and ferroelectric phases. Dielectric properties were studied as a function of frequency and temperature. Ferroelectric P-E and Magnetic M-H hysteresis loops were measured at room temperature.

Determination of the reduced matrix of the piezoelectric, dielectric, and elastic material constants for a piezoelectric material with C∞ symmetry.

PubMed

Sherrit, Stewart; Masys, Tony J; Wiederick, Harvey D; Mukherjee, Binu K

2011-09-01

We present a procedure for determining the reduced piezoelectric, dielectric, and elastic coefficients for a C(∞) material, including losses, from a single disk sample. Measurements have been made on a Navy III lead zirconate titanate (PZT) ceramic sample and the reduced matrix of coefficients for this material is presented. In addition, we present the transform equations, in reduced matrix form, to other consistent material constant sets. We discuss the propagation of errors in going from one material data set to another and look at the limitations inherent in direct calculations of other useful coefficients from the data.

Analyzing the defect structure of CuO-doped PZT and KNN piezoelectrics from electron paramagnetic resonance.

PubMed

Jakes, Peter; Kungl, Hans; Schierholz, Roland; Eichel, Rüdiger-A

2014-09-01

The defect structure for copper-doped sodium potassium niobate (KNN) ferroelectrics has been analyzed with respect to its defect structure. In particular, the interplay between the mutually compensating dimeric (Cu(Nb)'''-V(O)··) and trimeric (V(O)··-Cu(Nb)'''-V(O)··)· defect complexes with 180° and non-180° domain walls has been analyzed and compared to the effects from (Cu'' - V(O)··)(x)× dipoles in CuO-doped lead zirconate titanate (PZT). Attempts are made to relate the rearrangement of defect complexes to macroscopic electromechanical properties.

Method and apparatus for bistable optical information storage for erasable optical disks

DOEpatents

Land, Cecil E.; McKinney, Ira D.

1990-01-01

A method and an optical device for bistable storage of optical information, together with reading and erasure of the optical information, using a photoactivated shift in a field dependent phase transition between a metastable or a bias-stabilized ferroelectric (FE) phase and a stable antiferroelectric (AFE) phase in an lead lanthanum zirconate titanate (PLZT). An optical disk contains the PLZT. Writing and erasing of optical information can be accomplished by a light beam normal to the disk. Reading of optical information can be accomplished by a light beam at an incidence angle of 15 to 60 degrees to the normal of the disk.

Method and apparatus for bistable optical information storage for erasable optical disks

DOEpatents

Land, C.E.; McKinney, I.D.

1988-05-31

A method and an optical device for bistable storage of optical information, together with reading and erasure of the optical information, using a photoactivated shift in a field dependent phase transition between a metastable or a bias-stabilized ferroelectric (FE) phase and a stable antiferroelectric (AFE) phase in a lead lanthanum zirconate titanate (PLZT). An optical disk contains the PLZT. Writing and erasing of optical information can be accomplished by a light beam normal to the disk. Reading of optical information can be accomplished by a light beam at an incidence angle of 15 to 60 degrees to the normal of the disk. 10 figs.

An Experimental Investigation of the Structural Dynamics of a Torsionally Soft Rotor in Vacuum.

DTIC Science & Technology

1986-07-01

attached to the blades for the present test program were of G1356 material supplied by Piezo Electric Products. They were made of lead zirconate...titanate ceramic material with nickel surface electrodes. The elements, nominally measuring 1.0 x 0.5 x 0.010 inch, were epoxied directly to the upper...DAMPING- 0.53 Z RECURO Me. 221 :&CORD ND. 2Z2 RECORD NO. 23) O23 MUg 1 (MLI 6) Ku 2 I.D Si MuM 3 (1A 80 R"T 26 1U SG AP $S SCM AP VMS SGS AMP P94 SGC

Cellular structures with interconnected microchannels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shaefer, Robert Shahram; Ghoniem, Nasr M.; Williams, Brian

A method for fabricating a cellular tritium breeder component includes obtaining a reticulated carbon foam skeleton comprising a network of interconnected ligaments. The foam skeleton is then melt-infiltrated with a tritium breeder material, for example, lithium zirconate or lithium titanate. The foam skeleton is then removed to define a cellular breeder component having a network of interconnected tritium purge channels. In an embodiment the ligaments of the foam skeleton are enlarged by adding carbon using chemical vapor infiltration (CVI) prior to melt-infiltration. In an embodiment the foam skeleton is coated with a refractory material, for example, tungsten, prior to meltmore » infiltration.« less

Temperature Dependent Electrical Properties of PZT Wafer

NASA Astrophysics Data System (ADS)

Basu, T.; Sen, S.; Seal, A.; Sen, A.

2016-04-01

The electrical and electromechanical properties of lead zirconate titanate (PZT) wafers were investigated and compared with PZT bulk. PZT wafers were prepared by tape casting technique. The transition temperature of both the PZT forms remained the same. The transition from an asymmetric to a symmetric shape was observed for PZT wafers at higher temperature. The piezoelectric coefficient (d 33) values obtained were 560 pc/N and 234 pc/N, and the electromechanical coupling coefficient (k p) values were 0.68 and 0.49 for bulk and wafer, respectively. The reduction in polarization after fatigue was only ~3% in case of PZT bulk and ~7% for PZT wafer.

Multi-layer micro/nanofluid devices with bio-nanovalves

DOEpatents

Li, Hao; Ocola, Leonidas E.; Auciello, Orlando H.; Firestone, Millicent A.

2013-01-01

A user-friendly multi-layer micro/nanofluidic flow device and micro/nano fabrication process are provided for numerous uses. The multi-layer micro/nanofluidic flow device can comprise: a substrate, such as indium tin oxide coated glass (ITO glass); a conductive layer of ferroelectric material, preferably comprising a PZT layer of lead zirconate titanate (PZT) positioned on the substrate; electrodes connected to the conductive layer; a nanofluidics layer positioned on the conductive layer and defining nanochannels; a microfluidics layer positioned upon the nanofluidics layer and defining microchannels; and biomolecular nanovalves providing bio-nanovalves which are moveable from a closed position to an open position to control fluid flow at a nanoscale.

Fundamental understanding of wave generation and reception using d(36) type piezoelectric transducers.

PubMed

Zhou, Wensong; Li, Hui; Yuan, Fuh-Gwo

2015-03-01

A new piezoelectric wafer made from a PMN-PT single crystal with dominant piezoelectric coefficient d36 is proposed to generate and detect guided waves on isotropic plates. The in-plane shear coupled with electric field arising from the piezoelectric coefficient is not usually present for conventional piezoelectric wafers, such as lead zirconate titanate (PZT). The direct piezoelectric effect of coefficient d36 indicates that under external in-plane shear stress the charge is induced on a face perpendicular to the poled z-direction. On thin plates, this type of piezoelectric wafer will generate shear horizontal (SH) waves in two orthogonal wave propagation directions as well as two Lamb wave modes in other wave propagation directions. Finite element analyses are employed to explore the wave disturbance in terms of time-varying displacements excited by the d36 wafer in different directions of wave propagation to understand all the guided wave modes accurately. Experiments are conducted to examine the voltage responses received by this type of wafer, and also investigate results of tuning frequency and effects of d31 piezoelectric coefficient, which is intentionally ignored in the finite element analysis. All results demonstrate the main features and utility of proposed d36 piezoelectric wafer for guided wave generation and detection in structural health monitoring. Copyright © 2014 Elsevier B.V. All rights reserved.

Provenance of sediments from Sumatra, Indonesia - Insights from detrital U-Pb zircon geochronology, heavy mineral analyses and Raman spectroscopy

NASA Astrophysics Data System (ADS)

Liebermann, C.; Hall, R.; Gough, A.

2017-12-01

The island of Sumatra is situated at the southwestern margin of the Indonesian archipelago. Although it is the sixth largest island in the world, the geology of the Sumatra sedimentary basins and their underlying basement is relatively poorly understood in terms of their provenance. This work is a multi-proxy provenance study utilizing U-Pb detrital zircon dating by LA-ICP-MS combined with optical and Raman spectroscopy-based heavy mineral analysis. It will help to unravel the stratigraphy of Sumatra, contribute to paleogeographic reconstruction of western SE Asia, and aid a wider understanding of Sumatran petroleum plays. Thin section analyses, heavy mineral assemblages, and >3500 concordant U-Pb zircon ages, from samples acquired during two fieldwork seasons indicate a mixed provenance for Cenozoic sedimentary formations, including both local igneous sources and mature basement rocks. Characteristic Precambrian zircon age spectra are found in all analysed Cenozoic sedimentary strata. These can be correlated with zircon age populations found in Sumatran basement rocks; Neoproterozoic and Mesoproterozoic age groups are dominant (c. 500-600 Ma, c. 850-1000 Ma, c. 1050-1200 Ma). Paleoproterozoic to Archaean zircons occur as minor populations. The Phanerozoic age spectra of the Cenozoic formations are characterised by distinct Carboniferous, Permo-Triassic, and Jurassic-Cretaceous zircon populations. Permo-Triassic zircons are interpreted to come from granitoids in the Malay peninsula or Sumatra itself. Eocene to Lower Miocene strata are characterised by ultrastable heavy minerals such as zircon, tourmaline, and rutile, which together with garnet, suggest the principal sources were igneous and metamorphic basement rocks. Cenozoic zircons appear only from the Middle Miocene onwards. This change is interpreted to indicate a new contribution from a local volcanic arc, and is supported by the occurrence of unstable heavy minerals such as apatite and clinopyroxene, and the presence of volcanic quartz. The absence of an earlier volcanic contribution is surprising since subduction is widely considered to have been active from the Eocene.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jégou, C.; Maroutian, T.; Pillard, V.

We describe a vector network analyzer-based method to study the electromagnetic properties of nanoscale dielectrics at microwave frequencies (1 MHz–40 GHz). The complex permittivity spectrum of a given dielectric can be determined by placing it in a capacitor accessed on its both electrodes by coplanar waveguides. However, inherent propagation delays along the signal paths together with frequency-dependent effective surface of the capacitor at microwave frequencies can lead to significant distortion in the measured permittivity, which in turn can give rise to artificial frequency variations of the complex permittivity. We detail a fully analytical rigorous correction sequence with neither recourse tomore » extrinsic loss mechanisms nor to arbitrary parasitic signal paths. We illustrate our method on 3 emblematic dielectrics: ferroelectric morphotropic lead zirconate titanate, its paraelectric pyrochlore counterpart, and strontium titanate. Permittivity spectra taken at various points along the hysteresis loop help shedding light onto the nature of the different dielectric energy loss mechanisms. Thanks to the analytical character of our method, we can discuss routes to extend it to higher frequencies and we can identify unambiguously the sources of potential artifacts.« less

Titan's Exotic Weather

NASA Astrophysics Data System (ADS)

Griffith, Caitlin A.

2006-09-01

Images of Titan, taken during the joint NASA and European Space Agency Cassini-Huygens mission, invoke a feeling of familiarity: washes wind downhill to damp lakebeds; massive cumuli form and quickly dissipate, suggestive of rain; and dark oval regions resemble lakes. These features arise from Titan's unique similarity with Earth: both cycle liquid between their surfaces and atmospheres, but in Titan's cool atmosphere it is methane that exists as a gas, liquid, and ice. While Titan enticingly resembles Earth, its atmosphere is 10 times thicker, so that its radiative time constant near the surface exceeds a Titan year, and prohibits large thermal gradients and seasonal surface temperature variations exceeding 3K. Titan also lacks oceans - central to Earth's climate - and instead stores much of its condensible in its atmosphere. As a result, Titan's weather differs remarkably from Earth's. Evidence for this difference appears in the location of Titan's large clouds, which frequent a narrow band at 40S latitude and a region within 30 latitude of the S. Pole. Ground-based and Cassini observations, combined with thermodynamic considerations, indicate that we are seeing large convective cloud systems. Detailed cloud models and general circulation models further suggest that these are severe rain storms, which will migrate with the change in season. Outside these migrating "gypsy" cloud bands, the atmosphere appears to be calm, humid and thus frequented by thin stratiform clouds. An intriguingly alien environment is predicted. Yet, the combined effects of Titan's patchy wet surface, atmospheric tides, possible ice volcanoes, and detailed seasonal variations remain unclear as we have witnessed only one season so far. This talk will review observations of Titan's lower atmosphere and modeling efforts to explain the observations, and explore the questions that still elude us.

Fabrication of patterned single-crystal SrTiO3 thin films by ion slicing and anodic bonding

NASA Astrophysics Data System (ADS)

Lee, Yoo Seung; Djukic, Djordje; Roth, Ryan M.; Laibowitz, Robert; Izuhara, Tomoyuki; Osgood, Richard M.; Bakhru, Sasha; Bakhru, Hassaram; Si, Weidong; Welch, David

2006-09-01

A new technique for directly fabricating patterned thin films (<1μm thick) of fully single-crystal strontium titanate uses deep H+ implantation into the oxide sample, followed by anodic bonding of the sample to a Pyrex or Pyrex-on-Si substrate. The dielectric properties and crystal structure of such thin films are characterized and are found to be essentially those of the bulk single crystal.

A novel transparent charged particle detector for the CPET upgrade at TITAN

NASA Astrophysics Data System (ADS)

Lascar, D.; Kootte, B.; Barquest, B. R.; Chowdhury, U.; Gallant, A. T.; Good, M.; Klawitter, R.; Leistenschneider, E.; Andreoiu, C.; Dilling, J.; Even, J.; Gwinner, G.; Kwiatkowski, A. A.; Leach, K. G.

2017-10-01

The detection of an electron bunch exiting a strong magnetic field can prove challenging due to the small mass of the electron. If placed too far from a solenoid's entrance, a detector outside the magnetic field will be too small to reliably intersect with the exiting electron beam because the light electrons will follow the diverging magnetic field outside the solenoid. The TITAN group at TRIUMF in Vancouver, Canada, has made use of advances in the practice and precision of photochemical machining (PCM) to create a new kind of charge collecting detector called the "mesh detector." The TITAN mesh detector was used to solve the problem of trapped electron detection in the new Cooler PEnning Trap (CPET) currently under development at TITAN. This thin array of wires etched out of a copper plate is a novel, low profile, charge agnostic detector that can be made effectively transparent or opaque at the user's discretion.

Pluto's Implications for a Snowball Titan

NASA Astrophysics Data System (ADS)

Wong, M.; Yung, Y. L.; Gladstone, R.

2013-12-01

The recent Cassini-Huygens Mission to the Saturnian system provides compelling evidence that the present state of Titan's dense atmosphere is unsustainable over the age of the Solar System. Instead, for most of the time Titan's atmosphere must have existed in a collapsed snowball state, characterized by a cold surface and a thin atmosphere, much like those of present-day Pluto and Triton. We will briefly review how the present Titan atmosphere exists due to a sensitive coupling between photochemistry, radiation, and dynamics. This delicate 'house of cards' must have collapsed in the past when it ran out of CH4 or when the sun was dimmer. We will investigate how the rate of organic synthesis on Snowball Titan differs from that of contemporary Titan. The forthcoming New Horizons Mission to Pluto and the Kuiper Belt may allow us to gain insights into the fine balance and the evolutionary history of certain planetary atmospheres. In particular, the high SNR solar occultations planned for observation with the Alice UV spectrograph on New Horizons are expected to yield abundance profiles of important hydrocarbons and nitriles in Pluto's atmosphere, providing detailed constraints for photochemical models such as those considered here.

Age and evolution of thin-skinned deformation in Zacatecas, Mexico: Sevier orogeny evidence in the Mexican Fold-Thrust Belt

NASA Astrophysics Data System (ADS)

Ramírez-Peña, César Francisco; Chávez-Cabello, Gabriel

2017-07-01

Integrating U-Pb ages from zircons of syn- and postectonic intrusives emplaced in folded pre- and synorogenic marine sedimentary rocks, it is proposed that thin-skinned deformation in the Concepción del Oro salient of the Mexican Fold Thrust Belt in northern Zacatecas, Mexico, was active between 92 and 71.6 Ma. The intrusives Pico de Teyra and El Peñuelo (U-Pb zircon ages: 76.9 and 72.5 Ma) show internal tectonic foliations and horizontal shear zones that cut off aplitic veins, which apparently developed syntectonically to thin-skinned deformation. Other intrusives like Saltillito (71.6 Ma) and Concepción del Oro are clearly postectonic because they are undeformed internally, cut regional structures and are younger than syntectonic plutons. Biostratigraphic ages reported for synorogenic sediments (Concepción del Oro and Parras formations) indicate that regional thin-skinned deformation was active between Early Turonian and Late Campanian, which is in agreement with syn and postectonic intrusive emplacement ages in the area. Nevertheless, the thin-skinned structures are disrupted by a younger NNW-SSE high angle reverse and normal faults that uplifts the San Julián Block in the west and truncate the Concepción del Oro salient, suggesting a post-Paleocene thick-skinned stage of deformation. In this work, we propose that style and age of thin-skinned deformation is similar to the Sevier orogeny in the Rocky Mountains.

Triton, Pluto, and Titan: A Comparison of Haze Photometry

NASA Astrophysics Data System (ADS)

Buratti, Bonnie J.; Hillier, John K.; Abgarian, Mary; Kutsop, Nicholas; Devins, Spencer; Mosher, Joel A.; Stern, S. Alan; Weaver, Harold A.; Olkin, Catherine; Young, Leslie; Ennico, Kimberly; New Horizons Science Team

2017-10-01

As Kuiper Belt Objects of similar size and albedo, Triton and Pluto were thought to be kindred bodies exhibiting like geologic histories and features, with possible seasonal volatile transport in their polar regions. During the flyby of Pluto in July 2015, active geological processes were observed on the planet (Stern et al., 2015), and a substantial haze layer that was more akin to Titan’s was observed (Gladstone et. al., 2016). Multiple haze layers were discovered surrounding the dwarf planet (Cheng et al. 2017).Using a radiative transfer model based on Chandrasekhar’s “Planetary Problem” of an optically thin atmosphere and a surface of arbitrary single scattering albedo and single particle phase function (Chandrasekhar, 1960; Hillier et al., 1990, 1991; Buratti et al., 2011), we have characterized the optical depth and surface properties of Pluto, Triton, and Titan. The forward-scattering properties of the haze can also be quantified by this model. Optical imaging data was analyzed for Triton and Pluto. For Titan we made use of published data on Titan (Tomasko and West, 2009) plus new Cassini Visual Infrared Mapping Spectrometer (VIMS) data, which spans the wavelength range between 0.35 and 5.2 microns, and which has several channels in the mid-infrared where both the haze opacity is relatively low and the atmosphere is optically thin. Pluto’s atmosphere is more optically thick than Triton’s but both are far thinner than Titan’s. The composition of Triton’s haze layer differs markedly from Titan’s. Observations of Pluto’s haze reveal a bluish color (Gladstone et al., 2016), but the reddish tint of possible haze deposits on the surface (Stern et al., 2015; Buratti et al., 2015) suggest Pluto’s haze composition is Titan-like. Institute of Technology. Government sponsorship acknowledged.

Direct Measurement of Interparticle Forces of Titan Aerosol Analogs ("Tholin") Using Atomic Force Microscopy

NASA Astrophysics Data System (ADS)

Yu, Xinting; Hörst, Sarah M.; He, Chao; McGuiggan, Patricia; Bridges, Nathan T.

2017-12-01

To understand the origin of the dunes on Titan, it is important to investigate the material properties of Titan's organic sand particles on Titan. The organic sand may behave distinctively compared to the quartz/basaltic sand on terrestrial planets (Earth, Venus, and Mars) due to differences in interparticle forces. We measured the surface energy (through contact angle measurements) and elastic modulus (through Atomic Force Microscopy) of the Titan aerosol analog (tholin). We find that the surface energy of a tholin thin film is about 70.9 mN/m, and its elastic modulus is about 3.0 GPa (similar to hard polymers like PMMA and polystyrene). For two 20 μm diameter particles, the theoretical cohesion force is therefore 3.3 μN. We directly measured interparticle forces for relevant materials: tholin particles are 0.8 ± 0.6 μN, while the interparticle cohesion between walnut shell particles (a typical model materials for the Titan Wind Tunnel, TWT) is only 0.4 ± 0.1 μN. The interparticle cohesion forces are much larger for tholins and presumably Titan sand particles than materials used in the TWT. This suggests that we should increase the interparticle force in both analog experiments (TWT) and threshold models to correctly translate the results to real Titan conditions. The strong cohesion of tholins may also inform us how the small aerosol particles (˜1 μm) in Titan's atmosphere are transformed into large sand particles (˜200 μm). It may also support the cohesive sand formation mechanism suggested by Rubin and Hesp (2009), where only unidirectional wind is needed to form linear dunes on Titan.

Study of the photovoltaic effect in thin film barium titanate

NASA Technical Reports Server (NTRS)

Grannemann, W. W.; Dharmadhikari, V. S.

1982-01-01

Ferroelectric films of barium titanate were synthesized on silicon and quartz substrates, and the photoelectric effect in the structure consisting of metal deposited ferroelectric barium titanate film silicon was studied. A photovoltage with polarity that depends on the direction of the remanent polarization was observed. The deposition of BaTiO3 on silicon and fused quartz substrates was accomplished by an rf sputtering technique. A series of experiments to study the growth of ferroelectric BaTiO3 films on single crystal silicon and fused quartz substrates were conducted. The ferroelectric character in these films was found on the basis of evidence from the polarization electric field hysteresis loops, capacitance voltage and capacitance temperature techniques and from X-ray diffraction studies.

Hydrothermal Barium Titanate Thin-Film Characteristics and their Suitability as Decoupling Capacitors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Raj, P. Markondeya; Lee, Baik-Woo; Kang, Nam-Kee

System integration and miniaturization demands are driving integrated thin film capacitor technologies towards ultrahigh capacitance densities for noise-free power supply, power conversion and efficient power management. Hydrothermal route can deposit crystalline ferroelectric films at low temperatures of less than 150 C. It is hence an attractive route for integrating high permittivity thin film capacitors on organic, silicon or flex substrates. However, hydrothermal films are not commercialized so far because of their inferior insulation characteristics. Embedded hydroxyl groups are attributed to be the cause for high leakage currents, temperature dependent properties and lower Breakdown Voltages (BDVs). This paper discusses the dielectricmore » characteristics such as capacitance density, leakage currents and Temperature Coefficient of Capacitance (TCC) of hydrothermal barium titanate films and correlates them to the embedded water and OH groups, film morphology, stoichiometry and crystallinity. With thermal treatment, majority of the OH groups can be removed leading to improved insulation characteristics. The room temperature I-V characteristics agreed with ionic conduction models for films baked at 160 C while higher baking temperatures of above 300 C resulted in Poole-Frenkel type conduction. A brief perspective is provided on the suitability of hydrothermal thin film capacitors for power supply applications.« less

Synthesis and ferroelectric properties of La-substituted PZFNT

NASA Astrophysics Data System (ADS)

Singh, Pratibha; Singh, Sangeeta; Juneja, J. K.; Prakash, Chandra; Raina, K. K.; Kumar, Vinod; Pant, R. P.

2010-01-01

In this paper we are reporting a systematic study on ferroelectric properties of lanthanum (La) substituted modified lead zirconate titanate (PLZFNT) ceramics which were fabricated by mixed oxide process. La contents were varied in between 0 and 0.01 in steps of 0.0025. The X-ray diffraction study shows single phase for all samples. Silver electrode was deposited on flat surfaces of sintered discs for P-E (polarization vs. electric field) measurements. All compositions exhibited well-defined ferroelectric behavior at room temperature. Hysteresis loops were also recorded at different temperatures for all the compositions which showed typical variation of ferroelectric nature. The PLZFNT composition with 1 mol% of La showed the best retention behavior. The results are discussed.

Analysis on ultrashort-pulse laser ablation for nanoscale film of ceramics

NASA Astrophysics Data System (ADS)

Ho, C. Y.; Tsai, Y. H.; Chiou, Y. J.

2017-06-01

This paper uses the dual-phase-lag model to study the ablation characteristics of femtosecond laser processing for nanometer-sized ceramic films. In ultrafast process and ultrasmall size where the two lags occur, a dual-phase-lag can be applied to analyse the ablation characteristics of femtosecond laser processing for materials. In this work, the ablation rates of nanometer-sized lead zirconate titanate (PZT) ceramics are investigated using a dual-phase-lag and the model is solved by Laplace transform method. The results obtained from this work are validated by the available experimental data. The effects of material thermal properties on the ablation characteristics of femtosecond laser processing for ceramics are also discussed.

Single ZnO nanowire-PZT optothermal field effect transistors.

PubMed

Hsieh, Chun-Yi; Lu, Meng-Lin; Chen, Ju-Ying; Chen, Yung-Ting; Chen, Yang-Fang; Shih, Wan Y; Shih, Wei-Heng

2012-09-07

A new type of pyroelectric field effect transistor based on a composite consisting of single zinc oxide nanowire and lead zirconate titanate (ZnO NW-PZT) has been developed. Under infrared (IR) laser illumination, the transconductance of the ZnO NW can be modulated by optothermal gating. The drain current can be increased or decreased by IR illumination depending on the polarization orientation of the Pb(Zr(0.3)Ti(0.7))O(3) (PZT) substrate. Furthermore, by combining the photocurrent behavior in the UV range and the optothermal gating effect in the IR range, the wide spectrum of response of current by light offers a variety of opportunities for nanoscale optoelectronic devices.

Longitudinal-bending mode micromotor using multilayer piezoelectric actuator.

PubMed

Yao, K; Koc, B; Uchino, K

2001-07-01

Longitudinal-bending mode ultrasonic motors with a diameter of 3 mm were fabricated using stacked multilayer piezoelectric actuators, which were self-developed from hard lead zirconate titanate (PZT) ceramic. A bending vibration was converted from a longitudinal vibration with a longitudinal-bending coupler. The motors could be bidirectionally operated by changing driving frequency. Their starting and braking torque were analyzed based on the transient velocity response. With a load of moment of inertia 2.5 x 10(-7) kgm2, the motor showed a maximum starting torque of 127.5 microNm. The braking torque proved to be a constant independent on the motor's driving conditions and was roughly equivalent to the maximum starting torque achievable with our micromotors.

Note: Comparative experimental studies on the performance of 2-2 piezocomposite for medical ultrasound transducers

NASA Astrophysics Data System (ADS)

Marinozzi, F.; Bini, F.; Biagioni, A.; Grandoni, A.; Spicci, L.

2013-09-01

The paper reports the experimental investigation of the behavior of 2-2 Lead Zirconate Titanate (PZT)-polymer composite transducers array for clinical ultrasound equipments. Several 2-2 plate composites having the same dicing pitch of 0.11 mm and different volume fractions were manufactured and investigated. Measurements were performed through different techniques such as electrical impedance, pulse-echo, and Laser Doppler Vibrometer. With the last one, maps of the surface displacement were presented relative to thickness mode and first lateral mode resonance frequencies. The transducers with volume fractions of the 40% resulted markedly inefficient, whereas the largest bandwidth and best band shape were achieved by the 50%.

A hybrid phenomenological model for ferroelectroelastic ceramics. Part II: Morphotropic PZT ceramics

NASA Astrophysics Data System (ADS)

Stark, S.; Neumeister, P.; Balke, H.

2016-10-01

In this part II of a two part series, the rate-independent hybrid phenomenological constitutive model introduced in part I is modified to account for the material behavior of morphotropic lead zirconate titanate ceramics (PZT ceramics). The modifications are based on a discussion of the available literature results regarding the micro-structure of these materials. In particular, a monoclinic phase and a highly simplified representation of the hierarchical structure of micro-domains and nano-domains observed experimentally are incorporated into the model. It is shown that experimental data for the commercially available morphotropic PZT material PIC151 (PI Ceramic GmbH, Lederhose, Germany) can be reproduced and predicted based on the modified hybrid model.

Energy Harvesting Devices Utilizing Resonance Vibration of Piezoelectric Buzzer

NASA Astrophysics Data System (ADS)

Ogawa, Toshio; Sugisawa, Ryosuke; Sakurada, Yuta; Aoshima, Hiroshi; Hikida, Masahito; Akaishi, Hiroshi

2013-09-01

A piezoelectric buzzer for energy harvesting was investigated. Although an external force was added to a buzzer, a lead zirconate titanate (PZT) unimorph in the buzzer, the ceramic disc diameter, thickness, and capacitance of which were respectively 14 mm, 0.2 mm, and 10 nF, generated resonance vibration. As a result, alternating voltages of around 30 V and a frequency of 5 kHz were observed. When the generated voltages were applied to a LED lamp, new devices such as a “night-view footwear” and a “piezo-walker” were developed. It was confirmed that the piezo-buzzer for energy harvesting utilizing resonance vibration is an effective tool for obtaining clean energy.

Green piezoelectric for autonomous smart textile

NASA Astrophysics Data System (ADS)

Lemaire, E.; Borsa, C. J.; Briand, D.

2015-12-01

In this work, the fabrication of Rochelle salt based piezoelectric textiles are shown. Structures composed of fibers and Rochelle salt are easily produced using green processes. Both manufacturing and the material itself are really efficient in terms of environmental impact, considering the fabrication processes and the material resources involved. Additionally Rochelle salt is biocompatible. In this green paradigm, active sensing or actuating textiles are developed. Thus processing method and piezoelectric properties have been studied: (1) pure crystals are used as acoustic actuator, (2) fabrication of the textile-based composite is detailed, (3) converse effective d33 is evaluated and compared to lead zirconate titanate ceramic. The utility of textile-based piezoelectric merits its use in a wide array of applications.

Gas pipeline leakage detection based on PZT sensors

NASA Astrophysics Data System (ADS)

Zhu, Junxiao; Ren, Liang; Ho, Siu-Chun; Jia, Ziguang; Song, Gangbing

2017-02-01

In this paper, an innovative method for rapid detection and location determination of pipeline leakage utilizing lead zirconate titanate (PZT) sensors is proposed. The negative pressure wave (NPW) is a stress wave generated by leakage in the pipeline, and propagates along the pipeline from the leakage point to both ends. Thus the NPW is associated with hoop strain variation along the pipe wall. PZT sensors mounted on the pipeline were used to measure the strain variation and allowed accurate (within 2% error) and repeatable location (within 4% variance) of five manually controlled leakage points. Experimental results have verified the effectiveness and the location accuracy for leakage in a 55 meter long model pipeline.

Modelling of Piezothermoelastic Beam with Fractional Order Derivative

NASA Astrophysics Data System (ADS)

Kumar, Rajneesh; Sharma, Poonam

2016-04-01

This paper deals with the study of transverse vibrations in piezothermoelastic beam resonators with fractional order derivative. The fractional order theory of thermoelasticity developed by Sherief et al. [1] has been used to study the problem. The expressions for frequency shift and damping factor are derived for a thermo micro-electromechanical (MEM) and thermo nano-electromechanical (NEM) beam resonators clamped on one side and free on another. The effect of fractional order derivative on the derived expressions is observed analytically and shown graphically in the case of Lead Zirconate Titanate (PZT)-5A material. For α = 1, our results agree with those that are obtained by Grover and Sharma [20] and other particular cases of interest are also discussed.

Uranium-Bearing Srilankite from High-Pressure Garnetites of the Southern Urals: First Data

NASA Astrophysics Data System (ADS)

Gottman, I. A.; Pushkarev, E. V.; Khiller, V. V.

2018-04-01

This work presents the results of studying srilankite, a rare zirconium titanate (ZrTi2O6), associated with ilmenite, rutile, zircon, uraninite, and other minerals discovered in high-pressure garnetites of the lherzolite Mindyak massif (Southern Urals). Srilankite occurs as inclusions in ilmenite and rutile of up to several tens of microns in size. It was established for the first time that srilankite contains a significant UO2 admixture (up to 20%). The negative correlation between Zr and U is evidence of isomorphism in the srilankite-brannerite system. The association of srilankite with high-Zr rutile indicates that formation of these minerals occurred at T > 850°C.

Catalyst for producing lower alcohols

DOEpatents

Rathke, Jerome W.; Klingler, Robert J.; Heiberger, John J.

1987-01-01

A process and system for the production of the lower alcohols such as methanol, ethanol and propanol involves the reaction of carbon monoxide and water in the presence of a lead salt and an alkali metal formate catalyst combination. The lead salt is present as solid particles such as lead titanate, lead molybdate, lead vanadate, lead zirconate, lead tantalate and lead silicates coated or in slurry within molten alkali metal formate. The reactants, carbon monoxide and steam are provided in gas form at relatively low pressures below 100 atmospheres and at temperatures of 200-400.degree. C. The resulted lower alcohols can be separated into boiling point fractions and recovered from the excess reactants by distillation.

Relaxorlike dielectric behavior in Ba0.7Sr0.3TiO3 thin films

NASA Astrophysics Data System (ADS)

Zednik, Ricardo J.; McIntyre, Paul C.; Baniecki, John D.; Ishii, Masatoshi; Shioga, Takeshi; Kurihara, Kazuaki

2007-03-01

We present the results of a systematic dielectric study for sputter deposited barium strontium titanate thin film planar capacitors measured over a wide temperature range of 20-575K for frequencies between 1kHz and 1MHz. Our observations of dielectric loss peaks in the temperature and frequency domains cannot be understood in the typical framework of intrinsic phonon losses. We find that the accepted phenomenological Curie-von Schweidler dielectric behavior (universal relaxation law) in our barium strontium titanate films is only applicable over a narrow temperature range. An excellent fit to the Vogel-Fulcher expression suggests relaxorlike behavior in these films. The activation energy of the observed phenomenon suggests that oxygen ion motion play a role in the apparent relaxor behavior, although further experimental work is required to test this hypothesis.

Damage-free patterning of ferroelectric lead zirconate titanate thin films for microelectromechanical systems via contact printing

NASA Astrophysics Data System (ADS)

Welsh, Aaron

This thesis describes the utilization and optimization of the soft lithographic technique, microcontact printing, to additively pattern ferroelectric lead zirconate titanate (PZT) thin films for application in microelectromechanical systems (MEMS). For this purpose, the solution wetting, pattern transfer, printing dynamics, stamp/substrate configurations, and processing damages were optimized for incorporation of PZT thin films into a bio-mass sensor application. This patterning technique transfers liquid ceramic precursors onto a device stack in a desired configuration either through pattern definition in the stamp, substrate or both surfaces. It was determined that for ideal transfer of the pattern from the stamp to the substrate surface, wetting between the solution and the printing surface is paramount. To this end, polyurethane-based stamp surfaces were shown to be wet uniformly by polar solutions. Patterned stamp surfaces revealed that printing from raised features onto flat substrates could be accomplished with a minimum feature size of 5 mum. Films patterned by printing as a function of thickness (0.1 to 1 mum) showed analogous functional properties to continuous films that were not patterned. Specifically, 1 mum thick PZT printed features had a relative permittivity of 1050 +/- 10 and a loss tangent of 2.0 +/- 0.4 % at 10 kHz; remanent polarization was 30 +/- 0.4 muC/cm 2 and the coercive field was 45 +/- 1 kV/cm; and a piezoelectric coefficient e31,f of -7 +/- 0.4 C/m2. No pinching in the minor hysteresis loops or splitting of the first order reversal curve (FORC) distributions was observed. Non-uniform distribution of the solution over the printed area becomes more problematic as feature size is decreased. This resulted in solutions printed from 5 mum wide raised features exhibiting a parabolic shape with sidewall angles of ˜ 1 degree. As an alternative, printing solutions from recesses in the stamp surface resulted in more uniform solution thickness transfer across the entire feature widths, with increased sidewall angles of ˜ 35 degrees. This was at the cost of degrading line edge definition from ˜ 200 nm to ˜ 500 nm. The loss of line edge definition was mitigated through the combined use of printing from stamp recesses onto raised substrate features. This allowed for printing of PZT features down to 1 mum wide. Solutions could also be transferred onto both fixed and free standing cantilever structures patterned into a substrate surface. Optimization of the stamp removal from the substrate was crucial in increasing sidewall angles of printed PZT films. It was determined that solutions gel once deposited onto the stamp before printing. As a result, printed films could not redistribute easily after transfer had occurred. Through a combination of varying peeling directions and peeling rates, it was possible to deposit thin film PZT on a pre patterned feature ˜ 1 mum wide with sidewall angles > 80 degrees. These printing techniques were utilized in printing a 250 nm thick 30/70 PZT onto prepatterned cantilever structures for use in a bio-functionalized, mass sensing resonating structure in collaboration with a bio-nanoelectromechincal sensing research group from the University of Toulouse, France. The features ranged in lateral size from 30 down to 1 mum. The printed devices exhibited a relative permittivity of 500 +/- 10 and a loss tangent of 0.9 +/- 0.1 %. The hysteresis loops were well formed, without pinching of the loops, and exhibited remanent polarizations of 24 +/- 0.5 muC/cm2, and coercive fields of 110 +/- 1 kV/cm. Dry etched features of the same size and thickness displayed a relative permittivity of 445 +/- 8 and a loss tangent of 0.9 +/- 0.1 %. The hysteresis loops exhibited pinched loops with remanent polarizations of 24 +/- 0.7 muC/cm2, and coercive fields of 112 +/- 2 kV/cm. Upon cycling, the dry etched films developed a 20 kV/cm imprint with reduced remanent polarizations to 20.5 +/- 0.5 muC/cm2 .

Interaction of the Siberian craton and Central Asian Orogenic Belt (CAOB) recorded by detrital zircons from Transbaikalia

NASA Astrophysics Data System (ADS)

Powerman, V.; Shatsillo, A.; Chumakov, N.; Kapitonov, I.; Hourigan, J. K.

2015-12-01

The goal of this study is to pinpoint the beginning of interaction of two gigantic crustal structures: the Siberian Craton and the Central Asian Orogenic Belt (CAOB). We hypothesize that the beginning of convergence should be recorded in the Neoproterozoic passive margin strata of Siberian Craton by the first appearance of extraregional Neoproterozoic zircons. In order to test this hypothesis, we have acquired U-Pb zircon age distributions from twelve Neoproterozoic clastic rocks from the Baikal-Patom margin of Siberia and one sample from the volcaniclastic Padrinsky Group that was deposited atop accreted CAOB crust. Stratigraphically lower strata from the Siberian margin yield Archean - Paleoproterozoic detrital zircon ages, which are similar to, and probably derived from the Siberian Precambrian craton. A few extra-regional Mesoproterozoic grains are also present. The provenance shift happens in the upper portion of the section and is marked by a strong influx of extra-regional Neoproterozoic sediments. The youngest grains of 610 Ma constrain the sedimentation age and confine the timing of interaction between CAOB and Siberia in this region. Neoproterozoic zircons also dominate the overlying sedimentary unit, suggesting the continuance of the convergence. The coeval volcanoclastic unit on the CAOB side has a similar U-Pb detrital age distribution, strengthening the provenance link. Analysis of the local tectonics suggests that the beginning of accretion might have started even before the first appearance of Neoproterozoic zircon: during the development of a regional unconformity, capped by 635 Ma (?) "Snowball Earth" tillites of Dzhemkukan Fm. The absence of Neoproterozoic zircons in Dzhemkukan Fm. is probably explained by a thin-skinned tectonics that did not result in massive orogenesis . Our data are in good correlation with other Neoproterozoic sedimentary basins of southern Siberian Craton, including Cisbaikalia and Bodaibo Synclinorium.

Provenance of north Gondwana Cambrian-Ordovician sandstone: U-Pb SHRIMP dating of detrital zircons from Israel and Jordan

USGS Publications Warehouse

Kolodner, K.; Avigad, D.; McWilliams, M.; Wooden, J.L.; Weissbrod, T.; Feinstein, S.

2006-01-01

A vast sequence of quartz-rich sandstone was deposited over North Africa and Arabia during Early Palaeozoic times, in the aftermath of Neoproterozoic Pan-African orogeny and the amalgamation of Gondwana. This rock sequence forms a relatively thin sheet (1-3 km thick) that was transported over a very gentle slope and deposited over a huge area. The sense of transport indicates unroofing of Gondwana terranes but the exact provenance of the siliciclastic deposit remains unclear. Detrital zircons from Cambrian arkoses that immediately overlie the Neoproterozoic Arabian-Nubian Shield in Israel and Jordan yielded Neoproterozoic U-Pb ages (900-530 Ma), suggesting derivation from a proximal source such as the Arabian-Nubian Shield. A minor fraction of earliest Neoproterozoic and older age zircons was also detected. Upward in the section, the proportion of old zircons increases and reaches a maximum (40%) in the Ordovician strata of Jordan. The major earliest Neoproterozoic and older age groups detected are 0.95-1.1, 1.8-1.9 and 2.65-2.7 Ga, among which the 0.95-1.1 Ga group is ubiquitous and makes up as much as 27% in the Ordovician of Jordan, indicating it is a prominent component of the detrital zircon age spectra of northeast Gondwana. The pattern of zircon ages obtained in the present work reflects progressive blanketing of the northern Arabian-Nubian Shield by Cambrian-Ordovician sediments and an increasing contribution from a more distal source, possibly south of the Arabian-Nubian Shield. The significant changes in the zircon age signal reflect many hundreds of kilometres of southward migration of the provenance. ?? 2006 Cambridge University Press.

Stability of Zircon and its Isotopic Ratios in High-Temperature Fluids: Long-Term (4 months) Isotope Exchange Experiment at 850 °C and 50 MPa

NASA Astrophysics Data System (ADS)

Bindeman, Ilya N.; Schmitt, Axel K.; Lundstrom, Craig C.; Hervig, Richard L.

2018-05-01

Stability of zircon in hydrothermal fluids and vanishingly slow rates of diffusion identify zircon as a reliable recorder of its formation conditions in recent and ancient rocks. Debate, however, persists on how rapidly oxygen and key trace elements (e.g., Li, B, Pb) diffuse when zircon is exposed to hot aqueous fluids. Here, we report results of a nano- to micrometer-scale investigation of isotopic exchange using natural zircon from Mesa Falls Tuff (Yellowstone) treated with quartz-saturated, isotopically (18O, D, 7Li, and 11B) labeled water with a nominal δ18O value of +450‰ over 4 months at 850°C and 50 MPa. Frontside (crystal rim inwards) δ18O depth profiling of zircon by magnetic sector SIMS shows initially high but decreasing 18O/16O over a 130 nm non-Fickian profile, with a decay length comparable to the signal from surficial Au coating deposited onto zircon. In contrast, backside (crystal interior outwards) depth profiling on a 2-3 µm thick wafer cut and thinned from treated zircon by focused ion beam (FIB) milling lacks any significant increase in 18O/16O during penetration of the original surface layer. Near-surface time-of-flight (TOF-SIMS) frontside profiles of uncoated zircon from 4-month and 1-day-long experiments as well as untreated zircons display similar enrichments of 18O over a distance of 20 nm. All frontside 18O profiles are here interpreted as transient surface signals from nm-thick surface enrichment or contamination unrelated to diffusion. Likewise, frontside depth profiling of H, Li, and B isotopes are similar for long- and short-duration experiments. Additionally, surface U-Pb dating of zircon from the 4-month experiment returned U-Pb ages by depth profiling with 1 µm penetration that were identical to untreated samples. Frontside and backside depth-profiling thus demonstrate that diffusive 18O enrichment in the presence of H2O is much slower than predicted from experiments in Watson and Cherniak (1997). Instead, intracrystalline exchange of oxygen between fluid and zircon in wet experimental conditions with excess silica occurred over length-scales equivalent to those predicted for dry diffusion. Oxygen diffusion coefficients even under wet conditions and elevated temperatures (850 °C) are <1-3×10-23 m2/sec, underscoring a virtual lack of oxygen diffusion and an outstanding survivability of zircons

Study of the photovoltaic effect in thin film barium titanate

NASA Technical Reports Server (NTRS)

Grannemann, W. W.; Dharmadhikari, V. S.

1981-01-01

The photoelectric effect in structures consisting of metal deposited barium titanate film silicon is described. A radio frequency sputtering technique is used to deposit ferroelectric barium titantate films on silicon and quartz. Film properties are measured and correlated with the photoelectric effect characteristics of the films. It was found that to obtain good quality pin hole free films, it is necessary to reduce the substrate temperature during the last part of the deposition. The switching ability of the device with internal applied voltage is improved when applied with a ferroelectric memory device.

Possible formation of amino acid precursors in the lower atmosphere of Titan

NASA Astrophysics Data System (ADS)

Kobayashi, K.; Taniuchi, T.; Kaneko, T.; Al-Hanbali, H.; Yamori, A.; Miyakawa, S.; Takano, Y.

Titan is a quite interesting satellite of Saturn from the point of view of astrobiology and origins of life It has ca 0 15 MPa atmosphere mainly composed of nitrogen and methane which can give us the possible implication of primitive Earth environments There have been a great number of experiments simulating chemical reactions in Titan atmosphere In most experiments electric discharges and ultraviolet light were used as energy sources The former is simulation of charged particles trapped in Saturn s magnetosphere and the latter is simulation of solar light Thus it can be said that these experiments simulate chemical reaction in the upper thin atmosphere Cosmic rays are another possible energy source available in Titan atmosphere Their energy is so high that they can penetrate into the lower atmosphere of Titan The energy flux of cosmic rays in the lower Titan atmosphere was estimated as to 9 0 x 10 -3 erg cm -2 s -1 Sagan and Thompson 1984 In order to simulate the action of cosmic rays in Titan atmosphere we irradiated simulated Titan atmosphere with high-energy protons A gas mixture of methane 1-10 and nitrogen balance total pressure was 700 Torr was sealed in a Pyrex tube with a window of Havar foil 0 01 mm thick It was irradiated with 3 MeV protons from a van de Graaff accelerator Tokyo Institute of Technology The products were dissolved in water dichloromethane tetrahydrofuran or benzene They were evaporated to dryness and then acid-hydrolyzed Amino acids were analyzed by cation exchange HPLC

First principles study of carbon nanostructures, transition metal dichalcogenides, and magnetoelectric interfaces

NASA Astrophysics Data System (ADS)

Hammouri, Mahmoud

Perovskite oxides such as lead zirconate titanate, lanthanum manganite and two dimensional, atomically thick materials such as graphene, carbon nanotubes, graphene nanoribbon, and transition-metal dichalcogenides (TMDs) received intensive attention due to their electronic, magnetic, and transport properties. Understanding the properties and structure of these materials in solid state is a longstanding scientific challenge, especially for experimentalists. Using state-of-the-art density functional theory, different properties can be explained with an excellent match with experiments. This thesis presents an Ab initio density functional theory study of the electronic, magnetic, and transport properties of nanostructure systems. Nanostructures studied in this thesis include graphene, carbon nanotubes, graphene nanoribbons, zirconium disulfide, and La0.67Sr0.33MnO3/PbZr 02 Ti0.8O3 (LSMO/PZT) (100) interface. I investigated the mechanism of chemical functionalization of the side walls of carbon nanotubes by benzyne molecules. Binding energies, geometries, and electronic structure changes due to this functionalization are examined in detail. The binding energies between benzyne molecules and carbon nanotubes are found to be inversely proportional to nanotube diameter. We also studied the properties of graphene nanoribbons under compressions. Our study showed that the band gaps of graphene nanoribbons were strongly affected by applied compression. In addition, we found that the effect of compression has a strong influence on the IV-characteristic. We also investigated the effect of uniaxial strain on the electronic and magnetic properties of zirconium disulfide nanoribbons. Our calculation showed that the magnetization of zirconium disulfide nanoribbons can be switched on and off by the applied strain. In the last part, we studied the properties of the interface between two perovskite oxides, lead zirconate titanate and lanthanum strontium manganite. Our study demonstrated that the magnetoelectric coupling observed at this interface can be explained by the magnetic reconstruction of lanthanum strontium manganite.

Thickness dependence of the poling and current-voltage characteristics of paint films made up of lead zirconate titanate ceramic powder and epoxy resin

NASA Astrophysics Data System (ADS)

Egusa, Shigenori; Iwasawa, Naozumi

1995-11-01

A specially prepared paint made up of lead zirconate titanate (PZT) ceramic powder and epoxy resin was coated on an aluminum plate and was cured at room temperature, thus forming the paint film of 25-300 μm thickness with a PZT volume fraction of 53%. The paint film was then poled at room temperature, and the poling behavior was determined by measuring the piezoelectric activity as a function of poling field. The poling behavior shows that the piezoelectric activity obtained at a given poling field increases with an increase in the film thickness from 25 to 300 μm. The current-voltage characteristic of the paint film, on the other hand, shows that the increase in the film thickness leads not only to an increase in the magnitude of the current density at a given electric field but also to an increase in the critical electric field at which the transition from the ohmic to space-charge-limited conduction takes place. This fact indicates that the amount of the space charge of electrons injected into the paint film decreases as the film thickness increases. Furthermore, comparison of the current-voltage characteristic of the paint film with that of a pure epoxy film reveals that the space charge is accumulated largely at the interface between the PZT and epoxy phases in the paint film. On the basis of this finding, a model is developed for the poling behavior of the paint film by taking into account a possible effect of the space-charge accumulation and a broad distribution of the electric field in the PZT phase. This model is shown to give an excellent fit to the experimental data of the piezoelectric activity obtained here as a function of poling field and film thickness.

Crystallization dynamics and interface stability of strontium titanate thin films on silicon.

PubMed

Hanzig, Florian; Hanzig, Juliane; Mehner, Erik; Richter, Carsten; Veselý, Jozef; Stöcker, Hartmut; Abendroth, Barbara; Motylenko, Mykhaylo; Klemm, Volker; Novikov, Dmitri; Meyer, Dirk C

2015-04-01

Different physical vapor deposition methods have been used to fabricate strontium titanate thin films. Within the binary phase diagram of SrO and TiO 2 the stoichiometry ranges from Ti rich to Sr rich, respectively. The crystallization of these amorphous SrTiO 3 layers is investigated by in situ grazing-incidence X-ray diffraction using synchrotron radiation. The crystallization dynamics and evolution of the lattice constants as well as crystallite sizes of the SrTiO 3 layers were determined for temperatures up to 1223 K under atmospheric conditions applying different heating rates. At approximately 473 K, crystallization of perovskite-type SrTiO 3 is initiated for Sr-rich electron beam evaporated layers, whereas Sr-depleted sputter-deposited thin films crystallize at 739 K. During annealing, a significant diffusion of Si from the substrate into the SrTiO 3 layers occurs in the case of Sr-rich composition. This leads to the formation of secondary silicate phases which are observed by X-ray diffraction, transmission electron microscopy and X-ray photoelectron spectroscopy.

Amorphous lithium lanthanum titanate for solid-state microbatteries

DOE PAGES

Lee, Jungwoo Z.; Wang, Ziying; Xin, Huolin L.; ...

2016-12-16

Lithium lanthanum titanate (LLTO) is a promising solid state electrolyte for solid state batteries due to its demonstrated high bulk ionic conductivity. However, crystalline LLTO has a relatively low grain boundary conductivity, limiting the overall material conductivity. In this work, we investigate amorphous LLTO (a-LLTO) thin films grown by pulsed laser deposition (PLD). By controlling the background pressure and temperature we are able to optimize the ionic conductivity to 3 × 10 –4 S/cm and electronic conductivity to 5 × 10 –11 S/cm. XRD, TEM, and STEM/EELS analysis confirm that the films are amorphous and indicate that oxygen background gasmore » is necessary during the PLD process to decrease the oxygen vacancy concentration, decreasing the electrical conductivity. Amorphous LLTO is deposited onto high voltage LiNi 0.5Mn 1.5O 4 (LNMO) spinel cathode thin films and cycled up to 4.8 V vs. Li showing excellent capacity retention. Finally, these results demonstrate that a-LLTO has the potential to be integrated into high voltage thin film batteries.« less

Effect of structural in-depth heterogeneities on electrical properties of Pb(Zr0.52Ti0.48) O3 thin films as revealed by nano-beam X-ray diffraction

NASA Astrophysics Data System (ADS)

Vaxelaire, N.; Kovacova, V.; Bernasconi, A.; Le Rhun, G.; Alvarez-Murga, M.; Vaughan, G. B. M.; Defay, E.; Gergaud, P.

2016-09-01

A direct quantification of a structural in-depth composition in the lead zirconate titanate Pb(Zr,Ti)O3 thin films of morphotropic composition has been conducted using the newly available X-ray nano-pencil beam (i.e., beam size of 100 nm × 1 μm) diffraction approach. We tested two samples with different Zr/Ti chemical gradients. Here, we demonstrate the presence of a significant microstructural gradient between the rhombohedral and tetragonal phases through PbZrxTi1-xO3 (PZT) films with a 100 nm in-depth resolution. The phase gradient extends over around 350 nm, and it is repeated through the PZT film three times, which corresponds to the number of thermal annealings. Moreover, this microstructural gradient is in agreement with the Zr/Ti chemical gradient observed by the secondary ion mass spectroscopy (SIMS). Indeed, the quantity of tetragonal phases rises in the Ti-rich zones as revealed by SIMS, and the quantity of rhombohedral phases rises in the Zr-rich zones. We also demonstrated a huge difference in the in-depth phase variation between the two tested samples. The gradient free sample still contains 4.7% of phase variation through the film and the amplified gradient contains 9.6% of phase variation through the film. Knowing that the gradient free sample shows better electric and piezoelectric coefficients, one can draw a correlation between the chemical composition, crystallographic homogeneity, and electro-mechanical properties of the film. The more close the film is to the morphotropic composition and the more it is crystallographically homogeneous, the higher the piezoelectric coefficients of the PZT are. Finally, the adequate knowledge of phase variation and its relation to the fabrication technique are crucial for the enhancement of the PZT electro-mechanical properties. Our methodology and findings open up new perspectives in establishing a relevant quantitative feedback to reach an ultimate electro-mechanical coupling in the sol-gel PZT thin films.

Electric tunable behavior of sputtered lead barium zirconate thin films

NASA Astrophysics Data System (ADS)

Wu, Lin-Jung; Wu, Jenn-Ming; Huang, Hsin-Erh; Bor, Hui-Yun

2007-02-01

Lead barium zirconate (PBZ) films were grown on Pt /Ti/SiO2/Si substrates by rf-magnetron sputtering. The sputtered PBZ films possess pure perovskite phase, uniform microstructure, and excellent tunable behaviors. The tunability and loss tangent of sputtered PBZ films depend greatly on the oxygen mixing ratio (OMR). The optimal dielectric tunable behavior occurs in the PBZ films sputtered at 10% OMR. The sputtered PBZ film (10% OMR) possesses a value of figure of merit of 60, promising for frequency-agile applications. Bulk acoustic waves induced by electromechanical coupling occur at 2.72GHz, which is useful in fabricating filters and related devices in the microwave range.

Long-life high performance fuel cell program

NASA Technical Reports Server (NTRS)

Martin, R. E.

1985-01-01

A multihundred kilowatt Regenerative Fuel Cell for use in a space station is envisioned. Three 0.508 sq ft (471.9 cm) active area multicell stacks were assembled and endurance tested. The long term performance stability of the platinum on carbon catalyst configuration suitability of the lightweight graphite electrolyte reservoir plate, the stability of the free standing butyl bonded potassium titanate matrix structure, and the long life potential of a hybrid polysulfone cell edge frame construction were demonstrated. A 18,000 hour demonstration test of multicell stack to a continuous cyclical load profile was conducted. A total of 12,000 cycles was completed, confirming the ability of the alkaline fuel cell to operate to a load profile simulating Regenerative Fuel Cell operation. An orbiter production hydrogen recirculation pump employed in support of the cyclical load profile test completed 13,000 hours of maintenance free operation. Laboratory endurance tests demonstrated the suitability of the butyl bonded potassium matrix, perforated nickel foil electrode substrates, and carbon ribbed substrate anode for use in the alkaline fuel cell. Corrosion testing of materials at 250 F (121.1 C) in 42% wgt. potassium identified ceria, zirconia, strontium titanate, strontium zirconate and lithium cobaltate as candidate matrix materials.

Electric and ferroelectric properties of PZT/BLT multilayer films prepared by photochemical metal-organic deposition

NASA Astrophysics Data System (ADS)

Park, Hyeong-Ho; Lee, Hong-Sub; Park, Hyung-Ho; Hill, Ross H.; Hwang, Yun Taek

2009-01-01

The electric and ferroelectric properties of lead zirconate titanate (PZT) and lanthanum-substituted bismuth titanate (BLT) multilayer films prepared using photosensitive precursors were characterized. The electric and ferroelectric properties were investigated by studying the effect of the stacking order of four ferroelectric layers of PZT or BLT in 4-PZT, PZT/2-BLT/PZT, BLT/2-PZT/BLT, and 4-BLT multilayer films. The remnant polarization values of the 4-BLT and BLT/2-PZT/BLT multilayer films were 12 and 17 μC/cm 2, respectively. Improved ferroelectric properties of the PZT/BLT multilayer films were obtained by using a PZT intermediate layer. The films which contained a BLT layer on the Pt substrate had improved leakage currents of approximately two orders of magnitude and enhanced fatigue resistances compared to the films with a PZT layer on the Pt substrate. These improvements are due to the reduced number of defects and space charges near the Pt electrodes. The PZT/BLT multilayer films prepared by photochemical metal-organic deposition (PMOD) possessed enhanced electric and ferroelectric properties, and allow direct patterning to fabricate micro-patterned systems without dry etching.

Phase and Texture Evolution in Chemically Derived PZT Thin Films on Pt Substrates

DTIC Science & Technology

2014-09-01

function of heating rate. The FWHM of the Ill PZT texture components is sim 2978 Journal of the American Ceramic Society Mhin et al. Vol. 97, No. 9...Z39.18 ABSTRACT Phase and Texture Evolution in Chemically Derived PZT Thin Films on Pt Substrates Report Title The crystallization of lead zirconate...phase influencing texture evolution. The results suggest that PZT nucleates directly on Pt, which explains the observation of a more highly oriented

Thickness Dependent Structural and Dielectric Properties of Calcium Copper Titanate Thin Films Produced by Spin-Coating Method for Microelectronic Devices

NASA Astrophysics Data System (ADS)

Thiruramanathan, P.; Sankar, S.; Marikani, A.; Madhavan, D.; Sharma, Sanjeev K.

2017-07-01

Calcium copper titanate (CaCu3Ti4O12, CCTO) thin films have been deposited on platinized silicon [(111)Pt/Ti/SiO2/Si] substrate through a sol-gel spin coating technique and annealed at 600-900°C with a variation of 100°C per sample for 3 h. The activation energy for crystalline growth, as well as optimal annealing temperature (900°C) of the CCTO crystallites was studied by x-ray diffraction analysis (XRD). Thickness dependent structural, morphological, and optical properties of CCTO thin films were observed. The field emission scanning electron microscopy (FE-SEM) verified that the CCTO thin films are uniform, fully covered, densely packed, and the particle size was found to be increased with film thickness. Meanwhile, quantitative analysis of dielectric properties (interfacial capacitance, dead layers, and bulk dielectric constant) of CCTO thin film with metal-insulator-metal (M-I-M) structures has been investigated systematically using a series capacitor model. Room temperature dielectric properties of all the samples exhibit dispersion at low frequencies, which can be explained based on Maxwell-Wagner two-layer models and Koop's theory. It was found that the 483 nm thick CCTO film represents a high dielectric constant ( ɛ r = 3334), low loss (tan δ = 3.54), capacitance ( C = 4951 nF), which might satisfy the requirements of embedded capacitor.

Orientation dependent ferroelectric properties in samarium doped bismuth titanate thin films grown by the pulsed-laser-ablation method

NASA Astrophysics Data System (ADS)

Cheng, Zhenxiang; Kannan, Chinna Venkatasamy; Ozawa, Kiyoshi; Kimura, Hideo; Wang, Xiaolin

2006-07-01

Samarium doped bismuth titanate thin films with the composition of Bi3.25Sm0.75Ti3O12 and with strong preferred orientations along the c axis and the (117) direction were fabricated on Pt /TiO2/SiO2/Si substrate by pulsed laser ablation. Measurements on Pt /BSmT/Pt capacitors showed that the c-axis oriented film had a small remanent polarization (2Pr) of 5μC/cm2, while the highly (117) oriented film showed a 2Pr value of 54μC/cm2 at an electrical field of 268kV/cm and a coercive field Ec of 89kV/cm. This is different from the sol-gel derived c-axis oriented Bi3.15Sm0.85Ti3O12 film showing a 2Pr value of 49μC/cm2.

Development and characterization of ultrathin hafnium titanates as high permittivity gate insulators

NASA Astrophysics Data System (ADS)

Li, Min

High permittivity or high-kappa materials are being developed for use as gate insulators for future ultrascaled metal oxide semiconductor field effect transistors (MOSFETs). Hafnium containing compounds are the leading candidates. Due to its moderate permittivity, however, it is difficult to achieve HfO2 gate structures with an EOT well below 1.0 nm. One approach to increase HfO2 permittivity is combining it with a very high-kappa material, such as TiO2. In this thesis, we systematically studied the electrical and physical characteristics of high-kappa hafnium titanates films as gate insulators. A series of HfxTi1-xO2 films with well-controlled composition were deposited using an MOCVD system. The physical properties of the films were analyzed using a variety of characterization techniques. X-ray micro diffraction indicates that the Ti-rich thin film is more immune to crystallization. TEM analysis showed that the thick stoichiometric HfTiO 4 film has an orthorhombic structure and large anisotropic grains. The C-V curves from the devices with the hafnium titanates films displayed relatively low hysteresis. In a certain composition range, the interfacial layer (IL) EOT and permittivity of HfxTi1-x O2 increases linearly with increasing Ti. The charge is negative for HfxTi1-xO2/IL and positive for Si/IL interface, and the magnitude increases as Hf increases. For ultra-thin films (less than 2 nm EOT), the leakage current increases with increasing HE Moreover, the Hf-rich sample has weaker temperature dependence of the current. In the MOSFET devices with the hafnium titanates films, normal transistor characteristics were observed, also electron mobility degradation. Next, we investigated the effects that different pre-deposition surface treatments, including HF dipping, NH3 surface nitridation, and HfO2 deposition, have on the electrical properties of hafnium titanates. Surface nitridation shows stronger effect than the thin HfO2 layer. The nitrided samples displayed a negative flat band voltage shift and larger hysteresis relative to the HF-dipped samples. The IL EOT reduction by mtridation increases with increasing HE Surface nitridation also induces extra charge, more considerable at the Si/IL interface. The leakage current is reduced in the Hf-rich samples with a nitride layer. Electron mobility degradation by surface nitridation was also observed.

Guided wave technique for non-destructive testing of StifPipe

NASA Astrophysics Data System (ADS)

Amjad, Umar; Yadav, Susheel K.; Nguyen, Chi H.; Ehsani, Mohammad; Kundu, Tribikram

2015-03-01

The newly-developed StifPipe® is an effective technology for repair and strengthening of existing pipes and culverts. The wall of this pipe consists of a lightweight honeycomb core with carbon or glass fiber reinforced polymer (FRP) applied to the skin. The presence of the hollow honeycomb introduces challenges in the nondestructive testing (NDT) of this pipe. In this study, it is investigated if guided waves, excited by PZT (Lead ZirconateTitanate) transducer can detect damages in the honeycomb layer of the StifPipe®. Multiple signal processing techniques are used for in-depth study and understanding of the recorded signals. The experimental technique for damage detection in StifPipe® material is described and the obtained results are presented in this paper.

KSC-2014-3645

NASA Image and Video Library

2014-08-25

CAPE CANAVERAL, Fla. – Several Lead Zirconate Titanate, or PZT, mass gaging sensors have been attached to a composite tank during a test inside a laboratory at the Cryogenics Testbed Facility at NASA's Kennedy Space Center in Florida. The PZT-based system was developed at Kennedy as a way to measure the mass of a fluid and the structural health of a tank using vibration signatures on Earth or in reduced/zero g gravity. The mass gaging technology has received approval to be on the first sub-orbital flight on the Virgin Galactic Space Plane in 2015. NASA experiments using the PZT technology will be used by Embry-Riddle Aeronautical University in conjunction with Carthage College on a fluid transfer experiment. Photo credit: NASA/Daniel Casper

KSC-2014-3646

NASA Image and Video Library

2014-08-25

CAPE CANAVERAL, Fla. – Several Lead Zirconate Titanate, or PZT, mass gaging sensors have been attached to a composite tank during a test inside a laboratory at the Cryogenics Testbed Facility at NASA's Kennedy Space Center in Florida. The PZT-based system was developed at Kennedy as a way to measure the mass of a fluid and the structural health of a tank using vibration signatures on Earth or in reduced/zero g gravity. The mass gaging technology has received approval to be on the first sub-orbital flight on the Virgin Galactic Space Plane in 2015. NASA experiments using the PZT technology will be used by Embry-Riddle Aeronautical University in conjunction with Carthage College on a fluid transfer experiment. Photo credit: NASA/Daniel Casper

Study on structural, dielectric, ferroelectric and piezoelectric properties of Ba doped Lead Zirconate Titanate Ceramics

NASA Astrophysics Data System (ADS)

Dipti; Juneja, J. K.; Singh, Sangeeta; Raina, K. K.; Prakash, Chandra

2013-12-01

The perovskite Pb(1-x)BaxZr0.55Ti0.45O3 material (x=0.00, 0.01, 0.02, 0.03, 0.05, and 0.07) was synthesized by solid state reaction route. Green bodies were sintered at 1250 °C. All samples were subjected to X-ray diffraction analysis and they were found to be in single phase. Dielectric properties were studied as a function of temperature and frequency. Ferroelectric properties were studied as a function of temperature. Remnant polarization, saturation polarization and coercive field were determined for all the samples using ferroelectric loops. Piezoelectric properties such as d33 and electromechanical coupling factor (kp) were also measured at room temperature for all samples.

Composition and temperature dependence of the dielectric, piezoelectric and elastic properties of pure PZT ceramics.

PubMed

Zhuang, Z Q; Haun, M J; Jang, S J; Cross, L E

1989-01-01

Pure (undoped) piezoelectric lead zirconate titanate (PZT) ceramic samples at compositions across the ferroelectric region of the phase diagram were prepared from sol-gel-derived fine powders. Excess lead oxide was included in the PZT powders to obtain dense (95-96% of theoretical density) ceramics with large grain size (>7 mum) and to control the lead stoichiometry. The dielectric, piezoelectric, and elastic properties were measured from 4.2 to 300 K. At very low temperatures, the extrinsic domain wall and thermal defect motions freeze out. The low-temperature dielectric data can be used to determine coefficients in a phenomenological theory. The extrinsic contribution to the properties can then be separated from the single-domain properties derived from the theory.

Crystallographic changes in lead zirconate titanate due to neutron irradiation

DOE PAGES

Henriques, Alexandra; Graham, Joseph T.; Landsberger, Sheldon; ...

2014-11-17

Piezoelectric and ferroelectric materials are useful as the active element in non-destructive monitoring devices for high-radiation areas. Here, crystallographic structural refinement (i.e., the Rietveld method) is used to quantify the type and extent of structural changes in PbZr 0 .5Ti 0 .5O 3 after exposure to a 1 MeV equivalent neutron fluence of 1.7 × 10 15 neutrons/cm 2. The results show a measurable decrease in the occupancy of Pb and O due to irradiation, with O vacancies in the tetragonal phase being created preferentially on one of the two O sites. The results demonstrate a method by which themore » effects of radiation on crystallographic structure may be investigated.« less

Active Interior Noise Control Studies

NASA Technical Reports Server (NTRS)

Park, J.; Veeramani, S.; Sampath, A.; Balachandran, B.; Wereley, N.

1996-01-01

Analytical and experimental investigations into the control of noise in the interior of a three-dimensional enclosure with a flexible boundary are presented. The rigid boundaries are constructed from acrylic material, and in the different cases considered the flexible boundary is constructed from either aluminum or composite material. Noise generated by an external speaker is transmitted into the enclosure through the flexible boundary and active control is realized by using Lead Zirconate Titanate (PZT) piezoelectric actuators bonded to the flexible boundary. Condenser microphones are used for noise measurements inside and outside the enclosure. Minimization schemes for global and local noise control in the presence of a harmonic disturbance are developed and discussed. In the experiments, analog feedforward control is implemented by using the harmonic disturbance as a reference signal.

Three-degree-of-freedom ultrasonic motor using a 5-mm-diameter piezoelectric ceramic tube.

PubMed

Mingsen Guo; Junhui Hu; Hua Zhu; Chunsheng Zhao; Shuxiang Dong

2013-07-01

A small three-degree-of-freedom ultrasonic motor has been developed using a simple piezoelectric lead zirconate titanate (PZT)-tube stator (OD 5 mm, ID 3 mm, length 15 mm). The stator drives a ball-rotor into rotational motion around one of three orthogonal (x-, y-, and z-) axes by combing the first longitudinal and second bending vibration modes. A motor prototype was fabricated and characterized; its performance was superior to those of previous motors made with a PZT ceramic/metal composite stator of comparable size. The method for further improving the performance was discussed. The motor can be further miniaturized and it has potential to be applied to medical microrobots, endoscopes or micro laparoscopic devices, and cell manipulation devices.

Measurements of Generated Energy/Electrical Quantities from Locomotion Activities Using Piezoelectric Wearable Sensors for Body Motion Energy Harvesting

PubMed Central

Proto, Antonino; Penhaker, Marek; Bibbo, Daniele; Vala, David; Conforto, Silvia; Schmid, Maurizio

2016-01-01

In this paper, two different piezoelectric transducers—a ceramic piezoelectric, lead zirconate titanate (PZT), and a polymeric piezoelectric, polyvinylidene fluoride (PVDF)—were compared in terms of energy that could be harvested during locomotion activities. The transducers were placed into a tight suit in proximity of the main body joints. Initial testing was performed by placing the transducers on the neck, shoulder, elbow, wrist, hip, knee and ankle; then, five locomotion activities—walking, walking up and down stairs, jogging and running—were chosen for the tests. The values of the power output measured during the five activities were in the range 6 µW–74 µW using both transducers for each joint. PMID:27077867

Electronic structure of barium strontium titanate by soft-x-ray absorption spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Uehara, Y.; Underwood, J.H.; Gullikson, E.M.

1997-04-01

Perovskite-type titanates, such as Strontium Titanate (STO), Barium Titanate (BTO), and Lead Titanate (PTO) have been widely studied because they show good electric and optical properties. In recent years, thin films of Barium Strontium Titanate (BST) have been paid much attention as dielectrics of dynamic random access memory (DRAM) capacitors. BST is a better insulator with a higher dielectric constant than STO and can be controlled in a paraelectric phase with an appropriate ratio of Ba/Sr composition, however, few studies have been done on the electronic structure of the material. Studies of the electronic structure of such materials can bemore » beneficial, both for fundamental physics research and for improving technological applications. BTO is a famous ferroelectric material with a tetragonal structure, in which Ti and Ba atoms are slightly displaced from the lattice points. On the other hand, BST keeps a paraelectric phase, which means that the atoms are still at the cubic lattice points. It should be of great interest to see how this difference of the local structure around Ti atoms between BTO and BST effects the electronic structure of these two materials. In this report, the authors present the Ti L{sub 2,3} absorption spectra of STO, BTO, and BST measured with very high accuracy in energy of the absorption features.« less

Development of Functional Inorganic Materials by Soft Chemical Process Using Ion-Exchange Reactions

NASA Astrophysics Data System (ADS)

Feng, Qi

Our study on soft chemical process using the metal oxide and metal hydroxide nanosheets obtained by exfoliation their layered compounds were reviewed. Ni(OH)2⁄MnO2 sandwich layered nanostructure can be prepared by layer by-layer stacking of exfoliated manganese oxide nanosheets and nickel hydroxide layers. Manganese oxide nanotubes can be obtained by curling the manganese oxide nanosheets using the cationic surfactants as the template. The layered titanate oriented thin film can be prepared by restacking the titanate nanosheets on a polycrystalline substrate, and transformed to the oriented BaTiO3 and TiO2 thin films by the topotactic structural transformation reactions, respectively. The titanate nanosheets can be transformed anatase-type TiO2 nanocrystals under hydrothermal conditions. The TiO2 nanocrystals are formed by a topotactic structural transformation reaction. The TiO2 nanocrystals prepared by this method expose specific crystal plane on their surfaces, and show high photocatalytic activity and high dye adsorption capacity for high performance dye-sensitized solar cell. A series of layered basic metal salt (LBMS) compounds were prepared by hydrothermal reactions of transition metal hydroxides and organic acids. We succeeded in the exfoliation of these LBMS compounds in alcohol solvents, and obtained the transition metal hydroxide nanosheets for the first time.

Origin and Evolution of Nitrogen on Titan, Enceladus, Triton, and Pluto

NASA Technical Reports Server (NTRS)

Atreya, S. K.; Niemann, H. B.; Mahaffy, P. R.; Owen, T. C.

2007-01-01

Nitrogen, together with carbon, hydrogen, oxygen, phosphorus and sulfur (CHNOPS), plays a central role in life as we know it. Indeed, molecular nitrogen is the most abundant component of the terrestrial atmosphere, and second only to carbon dioxide on Mars and Venus. The Voyager and Cassini-Huygens observations show that copious nitrogen is present on Titan also, comprising some 95% by volume of this moon's 1500 millibar atmosphere. After water vapor, it may be the most abundant (4%) of the gases around tiny Enceladus, as revealed by the recent Cassini observations. A thin nitrogen atmosphere is found even on the coldest of the solar system bodies, Triton and Pluto. The available evidence on nitrogen isotopes and the heavy noble gases suggests that Titan acquired its nitrogen largely in the form of ammonia. Subsequent chemical evolution, beginning with the photolysis of NH3 on primordial Titan, led to the nitrogen atmosphere we see on Titan today. This is also the scenario for the origin of nitrogen on the terrestrial planets. Contrary to Titan, the colder outer solar system objects, Triton and Pluto, neither had the luxury of receiving much arnmonia in the first place, nor of photolyzing whatever little ammonia they did receive in the planetesimals that formed them. On the other hand, it is plausible the planetesimals were capable of trapping and delivering molecular nitrogen directly to Triton and Pluto, unlike Titan. The origin of nitrogen on Enceladus is somewhat enigmatic. A scenario similar to Titan's, but with a role for the interior processes, may be at work. In this paper, we will discuss the source and loss of nitrogen for the above objects, and why Ganymede, the largest moon in the solar system, is nitrogen starved.

Liquid-Phase Processing of Barium Titanate Thin Films

NASA Astrophysics Data System (ADS)

Harris, David Thomas

Processing of thin films introduces strict limits on the thermal budget due to substrate stability and thermal expansion mismatch stresses. Barium titanate serves as a model system for the difficulty in producing high quality thin films because of sensitivity to stress, scale, and crystal quality. Thermal budget restriction leads to reduced crystal quality, density, and grain growth, depressing ferroelectric and nonlinear dielectric properties. Processing of barium titanate is typically performed at temperatures hundreds of degrees above compatibility with metalized substrates. In particular integration with silicon and other low thermal expansion substrates is desirable for reductions in costs and wider availability of technologies. In bulk metal and ceramic systems, sintering behavior has been encouraged by the addition of a liquid forming second phase, improving kinetics and promoting densification and grain growth at lower temperatures. This approach is also widespread in the multilayer ceramic capacitor industry. However only limited exploration of flux processing with refractory thin films has been performed despite offering improved dielectric properties for barium titanate films at lower temperatures. This dissertation explores physical vapor deposition of barium titanate thin films with addition of liquid forming fluxes. Flux systems studied include BaO-B2O3, Bi2O3-BaB2O 4, BaO-V2O5, CuO-BaO-B2O3, and BaO-B2O3 modified by Al, Si, V, and Li. Additions of BaO-B2O3 leads to densification and an increase in average grain size from 50 nm to over 300 nm after annealing at 900 °C. The ability to tune permittivity of the material improved from 20% to 70%. Development of high quality films enables engineering of ferroelectric phase stability using residual thermal expansion mismatch in polycrystalline films. The observed shifts to TC match thermodynamic calculations, expected strain from the thermal expansion coefficients, as well as x-ray diffract measurements . Our system exhibits flux-film-substrate interactions that can lead to dramatic changes to the microstructure. This effect is especially pronounced onc -sapphire, with Al diffusion from the substrate leading to formation of an epitaxial BaAl2O4 second phase at the substrate-film interface. The formation of this second phase in the presence of a liquid phase seeds {111} twins that drive abnormal grain growth. The orientation of the sapphire substrate determines the BaAl2O 4 morphology, enabling control the abnormal grain growth behavior. CuO additions leads to significant grain growth at 900 °C, with average grain size approaching 500 nm. The orthorhombic-tetragonal phase transition is clearly observable in temperature dependent measurements and both linear and nonlinear dielectric properties are improved. All films containing CuO are susceptible to aging. A number of other systems were investigated for efficacy at temperatures below 900 °C. Pulsed laser deposition was used to study flux + BaTiO 3 targets, layered flux films, and in situ liquids. RF-magnetron sputtering using a dual-gun approach was used to explore integration on flexible foils with Ba1-xSrxTiO3. Many of these systems were based on the BaO-B2O3 system, which has proven effective in thin films, multilayer ceramic capacitors, and bulk ceramics. Modifiers allow tailoring of the microstructure at 900 °C, however no compositions were found, and no reports exist in the open literature, that provide significant grain growth or densification below 900 °C. Liquid phase fluxes offer a promising path forward for low temperature processing of barium titanate, with the ultimate goal of integration with metalized silicon substrates. This work demonstrates significant improvements to dielectric properties and the necessity of understanding interactions in the film-flux-substrate system.

Titan Mystery Clouds

NASA Image and Video Library

2016-12-21

This comparison of two views from NASA's Cassini spacecraft, taken fairly close together in time, illustrates a peculiar mystery: Why would clouds on Saturn's moon Titan be visible in some images, but not in others? In the top view, a near-infrared image from Cassini's imaging cameras, the skies above Saturn's moon Titan look relatively cloud free. But in the bottom view, at longer infrared wavelengths, Cassini sees a large field of bright clouds. Even though these views were taken at different wavelengths, researchers would expect at least a hint of the clouds to show up in the upper image. Thus they have been trying to understand what's behind the difference. As northern summer approaches on Titan, atmospheric models have predicted that clouds will become more common at high northern latitudes, similar to what was observed at high southern latitudes during Titan's late southern summer in 2004. Cassini's Imaging Science Subsystem (ISS) and Visual and Infrared Mapping Spectrometer (VIMS) teams have been observing Titan to document changes in weather patterns as the seasons change, and there is particular interest in following the onset of clouds in the north polar region where Titan's lakes and seas are concentrated. Cassini's "T120" and "T121" flybys of Titan, on June 7 and July 25, 2016, respectively, provided views of high northern latitudes over extended time periods -- more than 24 hours during both flybys. Intriguingly, the ISS and VIMS observations appear strikingly different from each other. In the ISS observations (monochrome image at top), surface features are easily identifiable and only a few small, isolated clouds were detected. In contrast, the VIMS observations (color image at bottom) suggest widespread cloud cover during both flybys. The observations were made over the same time period, so differences in illumination geometry or changes in the clouds themselves are unlikely to be the cause for the apparent discrepancy: VIMS shows persistent atmospheric features over the entire observation period and ISS consistently detects surface features with just a few localized clouds. The answer to what could be causing the discrepancy appears to lie with Titan's hazy atmosphere, which is much easier to see through at the longer infrared wavelengths that VIMS is sensitive to (up to 5 microns) than at the shorter, near-infrared wavelength used by ISS to image Titan's surface and lower atmosphere (0.94 microns). High, thin cirrus clouds that are optically thicker than the atmospheric haze at longer wavelengths, but optically thinner than the haze at the shorter wavelength of the ISS observations, could be detected by VIMS and simultaneously lost in the haze to ISS -- similar to trying to see a thin cloud layer on a hazy day on Earth. This phenomenon has not been seen again since July 2016, but Cassini has several more opportunities to observe Titan over the last months of the mission in 2017, and scientists will be watching to see if and how the weather changes. These two images were taken as part of the T120 flyby on June 7 (VIMS) and 8 (ISS), 2016. The distance to Titan was about 28,000 miles (45,000 kilometers) for the VIMS image and about 398,000 miles (640,000 kilometers) for the ISS image. The VIMS image has been processed to enhance the visibility of the clouds; in this false-color view, clouds appear nearly white, atmospheric haze is pink, and surface areas would appear green. http://photojournal.jpl.nasa.gov/catalog/PIA21054

Titan's Stratospheric Condensibles at High Northern Latitudes During Northern Winter

NASA Technical Reports Server (NTRS)

Anderson, Carrie; Samuelson, R.; Achterberg, R.

2012-01-01

The Infrared Interferometer Spectrometer (IRIS) instrument on board Voyager 1 caught the first glimpse of an unidentified particulate feature in Titan's stratosphere that spectrally peaks at 221 per centimeter. Until recently, this feature that we have termed 'the haystack,' has been seen persistently at high northern latitudes with the Composite Infrared Spectrometer (CIRS) instrument onboard Cassini, The strength of the haystack emission feature diminishes rapidly with season, becoming drastically reduced at high northern latitudes, as Titan transitions from northern winter into spring, In contrast to IRIS whose shortest wavenumber was 200 per centimeter, CIRS extends down to 10 per centimeter, thus revealing an entirely unexplored spectral region in which nitrile ices have numerous broad lattice vibration features, Unlike the haystack, which is only found at high northern latitudes during northern winter/early northern spring, this geometrically thin nitrile cloud pervades Titan's lower stratosphere, spectrally peaking at 160 per centimeter, and is almost global in extent spanning latitudes 85 N to 600 S, The inference of nitrile ices are consistent with the highly restricted altitude ranges over which these features are observed, and appear to be dominated by a mixture of HCN and HC3N, The narrow range in altitude over which the nitrile ices extend is unlike the haystack, whose vertical distribution is significantly broader, spanning roughly 70 kilometers in altitude in Titan's lower stratosphere, The nitrile clouds that CIRS observes are located in a dynamically stable region of Titan's atmosphere, whereas CH4 clouds, which ordinarily form in the troposphere, form in a more dynamically unstable region, where convective cloud systems tend to occur. In the unusual situation where Titan's tropopause cools significantly from the HASI 70.5K temperature minimum, CH4 should condense in Titan's lower stratosphere, just like the aforementioned nitrile clouds, although in significantly larger abundances. We will present the spectral and vertical distribution of Titan's stratospheric particulates during northern winter on Titan. The drastically changing abundance of the haystack over a small latitude range will be highlighted, specifically comparing the IRIS and CIRS epochs, Finally, we will discuss the situation in which CH4 condenses in Titan's lower stratosphere, forming an unexpected quasi steady-state stratospheric Ice cloud.

The Effects of Postprocessing on Physical and Solution Deposition of Complex Oxide Thin Films for Tunable Applications

DTIC Science & Technology

2016-02-01

BST barium strontium titanate εr dielectric constant MIM metal /insulator/ metal MOSD metal organic spin deposition PtSi platinum silicide RF...improvement. In addition, BST films processed via solution metal organic spin deposition, which yield a lower dielectric range of 150–335, also...layers. This report details how we used solution and physical deposition to fabricate thin films via radio frequency (RF) sputtering and metal

Magnetoelectric coupling of multiferroic chromium doped barium titanate thin film probed by magneto-impedance spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shah, Jyoti, E-mail: shah.jyoti1@gmail.com; Kotnala, Ravinder K., E-mail: rkkotnala@nplindia.org, E-mail: rkkotnala@gmail.com

2014-04-07

Thin film of BaTiO{sub 3} doped with 0.1 at. % Cr (Cr:BTO) has been prepared by pulsed laser deposition technique. Film was deposited on Pt/SrTiO{sub 3} substrate at 500 °C in 50 mTorr Oxygen gas pressure using KrF (298 nm) laser. Polycrystalline growth of single phase Cr:BTO thin film has been confirmed by grazing angle X-ray diffraction. Cr:BTO film exhibited remnant polarization 6.4 μC/cm{sup 2} and 0.79 MV/cm coercivity. Magnetization measurement of Cr:BTO film showed magnetic moment 12 emu/cc. Formation of weakly magnetic domains has been captured by magnetic force microscopy. Theoretical impedance equation fitted to experimental data in Cole-Cole plot for thin film inmore » presence of transverse magnetic field resolved the increase in grain capacitance from 4.58 × 10{sup −12} to 5.4 × 10{sup −11} F. Film exhibited high value 137 mV/cm-Oe magneto-electric (ME) coupling coefficient at room temperature. The high value of ME coupling obtained can reduce the typical processing steps involved in multilayer deposition to obtain multiferrocity in thin film. Barium titanate being best ferroelectric material has been tailored to be multiferroic by non ferromagnetic element, Cr, doping in thin film form opens an avenue for more stable and reliable spintronic material for low power magnetoelectric random excess memory applications.« less

PZT Thin-Film Micro Probe Device with Dual Top Electrodes

NASA Astrophysics Data System (ADS)

Luo, Chuan

Lead zirconate titanate (PZT) thin-film actuators have been studied intensively for years because of their potential applications in many fields. In this dissertation, a PZT thin-film micro probe device is designed, fabricated, studied, and proven to be acceptable as an intracochlear acoustic actuator. The micro probe device takes the form of a cantilever with a PZT thin-film diaphragm at the tip of the probe. The tip portion of the probe will be implanted in cochlea later in animal tests to prove its feasibility in hearing rehabilitation. The contribution of the dissertation is three-fold. First, a dual top electrodes design, consisting of a center electrode and an outer electrode, is developed to improve actuation displacement of the PZT thin-film diaphragm. The improvement by the dual top electrodes design is studied via a finite element model. When the dimensions of the dual electrodes are optimized, the displacement of the PZT thin-film diaphragm increases about 30%. A PZT thin-film diaphragm with dual top electrodes is fabricated to prove the concept, and experimental results confirm the predictions from the finite element analyses. Moreover, the dual electrode design can accommodate presence of significant residual stresses in the PZT thin-film diaphragm by changing the phase difference between the two electrodes. Second, a PZT thin-film micro probe device is fabricated and tested. The fabrication process consists of PZT thin-film deposition and deep reactive ion etching (DRIE). The uniqueness of the fabrication process is an automatic dicing mechanism that allows a large number of probes to be released easily from the wafer. Moreover, the fabrication is very efficient, because the DRIE process will form the PZT thin-film diaphragm and the special dicing mechanism simultaneously. After the probes are fabricated, they are tested with various possible implantation depths (i.e., boundary conditions). Experimental results show that future implantation depths should be less than 3 mm in order to guarantee the first resonant frequency above 60 kHz. Finally, a package for the PZT thin-film micro probe device is developed to ensure its proper function in an aqueous environment, such as inside of cochlea. The package is an insulation layer of parylene coating on the probe. A finite element analysis indicates that a coating thickness of less than 1 mum will reduce the PZT diaphragm displacement by less than 10%. A special fixture is designed to hold a large number of probes for parylene deposition of a thickness of 250 nm. A packaged probe is then submerged in deionized water and functions properly for at least 55 hours. Displacement and impedance of the probe are measured via a laser Doppler vibrometer and an impedance analyzer, respectively. Experimental results show that displacement of the PZT diaphragm increases about 30% in two hours, after the probe is submerged in the deionized water. The impedance measurement shows consistent trends. A hypothesis to explain this unusual phenomenon is diffusion of water molecules into the PZT thin film. High-resolution SEM images of the probe indicate presence of numerous nano-pores in the surface of the PZT thin film, indirectly confirming the hypothesis. Keywords: PZT, Thin-Film, Dual Electrodes, Parylene Coating, Aqueous Environment, Cochlear Implant

Barium titanate nanocrystals and nanocrystal thin films: Synthesis, ferroelectricity, and dielectric properties

NASA Astrophysics Data System (ADS)

Huang, Limin; Chen, Zhuoying; Wilson, James D.; Banerjee, Sarbajit; Robinson, Richard D.; Herman, Irving P.; Laibowitz, Robert; O'Brien, Stephen

2006-08-01

Advanced applications for high k dielectric and ferroelectric materials in the electronics industry continues to demand an understanding of the underlying physics in decreasing dimensions into the nanoscale. We report the synthesis, processing, and electrical characterization of thin (<100nm thick) nanostructured thin films of barium titanate (BaTiO3) built from uniform nanoparticles (<20nm in diameter). We introduce a form of processing as a step toward the ability to prepare textured films based on assembly of nanoparticles. Essential to this approach is an understanding of the nanoparticle as a building block, combined with an ability to integrate them into thin films that have uniform and characteristic electrical properties. Our method offers a versatile means of preparing BaTiO3 nanocrystals, which can be used as a basis for micropatterned or continuous BaTiO3 nanocrystal thin films. We observe the BaTiO3 nanocrystals crystallize with evidence of tetragonality. We investigated the preparation of well-isolated BaTiO3 nanocrystals smaller than 10nm with control over aggregation and crystal densities on various substrates such as Si, Si /SiO2, Si3N4/Si, and Pt-coated Si substrates. BaTiO3 nanocrystal thin films were then prepared, resulting in films with a uniform nanocrystalline grain texture. Electric field dependent polarization measurements show spontaneous polarization and hysteresis, indicating ferroelectric behavior for the BaTiO3 nanocrystalline films with grain sizes in the range of 10-30nm. Dielectric measurements of the films show dielectic constants in the range of 85-90 over the 1KHz -100KHz, with low loss. We present nanocrystals as initial building blocks for the preparation of thin films which exhibit highly uniform nanostructured texture and grain sizes.

Textural and U-Pb systematics (CA-TIMS) of stepwise leaching in zircon from granophyres in the Archean Stillwater Complex

NASA Astrophysics Data System (ADS)

Wall, C. J.; Scoates, J. S.; Friedman, R. M.; Meurer, W. P.

2011-12-01

The chemical abrasion-TIMS method or CA-TIMS uses a high-temperature annealing treatment to remove the effects of Pb-loss from radiation damaged parts of the zircon lattice and allows for highly precise and accurate U-Pb dating [1]. Zircon with high U-Th concentrations can be strongly metamict and it is not yet clear how effective the chemical abrasion treatment is when applied to these types of grains. In this study, we evaluate the link between the textural response and U-Pb systematics of zircon during chemical leaching for a granophyric rock from the Archean Stillwater Complex in Montana. The sample was selected based on the high abundance of zircon and the high degree of metamictization of the grains. Untreated and leached zircon grains were analyzed by scanning electron microscopy (SEM) and isotope dilution thermal ionization mass spectrometry (ID-TIMS). In thin section, zircon grains are euhedral in morphology and tend to be associated with amphibole-rich zones. Under the SEM, zircon grains typically have two distinct zones, a Ca-rich amorphous zone in the core and a more intact outer shell. Five acid-leaching steps were carried out on grains with each step increasing in temperature and acid strength until the zircon residue completely dissolved (starting at a 50% strength HF/HNO3 mixture at 100°C for 4 hours and finishing at full strength acid at 170°C for 4 hours). SEM imaging was conducted on grains after each step with a noticeable change in the morphology of the grains. As the leaching progressed, the acid leach created large pathways through the crystal lattice until only grain fragments remained, in some cases even boring large holes into the centre of the zircon grain. The acid preferentially dissolved the more soluble Ca-rich zones leaving behind fragile zircon "shells". U-Pb results of untreated grains are highly discordant (37-80%) and yield a chord with an upper intercept age of 1981 ± 140 Ma, whereas leached grains are slightly less discordant (12-69%) and define a much different chord with an upper intercept age of 2618 ± 4 Ma. Both ages are too young in comparison to the crystallization age of the Stillwater Complex (ca. 2709 Ma) and are considered to represent two discrete Pb-loss events that have reset the U-Pb systematics of these zircon grains. These Pb-loss events may be due to hydrothermal events associated with the emplacement of mafic dikes or the crystallization of regionally extensive monzonite plutons that intruded the Stillwater Complex. Dating different geological events using the U-Pb isotopic compositions of untreated metamict zircon and leached zircon by systematic acid leaching could prove to be a useful application of CA-TIMS. [1] Mattinson (2005) Chemical Geology 220, 47-66.

Trace Element Zoning and Incipient Metamictization in a Lunar Zircon: Application of Three Microprobe Techniques

NASA Technical Reports Server (NTRS)

Wopenka, Brigitte; Jollife, Bradley L.; Zinner, Ernst; Kremser, Daniel T.

1996-01-01

We have determined major (Si, Zr, Hf), minor (Al, Y, Fe, P), and trace element (Ca, Sc, Ti, Ba, REE, Th, U) concentrations and Raman spectra of a zoned, 200 microns zircon grain in lunar sample 14161,7069, a quartz monzodiorite breccia collected at the Apollo 14 site. Analyses were obtained on a thin section in situ with an ion microprobe, an electron microprobe, and a laser Raman microprobe. The zircon grain is optically zoned in birefringence, a reflection of variable (incomplete) metamictization resulting from zo- nation in U and Th concentrations. Variations in the concentrations of U and Th correlate strongly with those of other high-field-strength trace elements and with changes in Raman spectral parameters. Concentrations of U and Th range from 21 to 55 ppm and 6 to 31 ppm, respectively, and correlate with lower Raman peak intensities, wider Raman peaks, and shifted Si-O peak positions. Concentrations of heavy rare earth elements range over a factor of three to four and correlate with intensities of fluorescence peaks. Correlated variations in trace element concentrations reflect the original magmatic differentiation of the parental melt approx. 4 b.y. ago. Degradation of the zircon structure, as reflected by the observed Raman spectral parameters, has occurred in this sample over a range of alpha-decay event dose from approx. 5.2 x 10(exp 14) to 1.4 x 10(exp 15) decay events per milligram of zircon, as calculated from the U and Th concentrations. This dose is well below the approx. 10(exp 16) events per milligram cumulative dose that causes complete metamictization and indicates that laser Raman microprobe spectroscopy is an analytical technique that is very sensitive to the radiation-induced damage in zircon.

Aerosol chemistry in Titan's ionosphere: simultaneous growth and etching processes

NASA Astrophysics Data System (ADS)

Carrasco, Nathalie; Cernogora, Guy; Jomard, François; Etcheberry, Arnaud; Vigneron, Jackie

2016-10-01

Since the Cassini-CAPS measurements, organic aerosols are known to be present and formed at high altitudes in the diluted and partially ionized medium that is Titan's ionosphere [1]. This unexpected chemistry can be further investigated in the laboratory with plasma experiments simulating the complex ion-neutral chemistry starting from N2-CH4 [2]. Two sorts of solid organic samples can be produced in laboratory experiments simulating Titan's atmospheric reactivity: grains in the volume and thin films on the reactor walls. We expect that grains are more representative of Titan's atmospheric aerosols, but films are used to provide optical indices for radiative models of Titan's atmosphere.The aim of the present study is to address if these two sorts of analogues are chemically equivalent or not, when produced in the same N2-CH4 plasma discharge. The chemical compositions of both these materials are measured by using elemental analysis, XPS analysis and Secondary Ion Mass Spectrometry. We find that films are homogeneous but significantly less rich in nitrogen and hydrogen than grains produced in the same experimental conditions. This surprising difference in their chemical compositions is explained by the efficient etching occurring on the films, which stay in the discharge during the whole plasma duration, whereas the grains are ejected after a few minutes [3]. The impact for our understanding of Titan's aerosols chemical composition is important. Our study shows that chemical growth and etching process are simultaneously at stake in Titan's ionosphere. The more the aerosols stay in the ionosphere, the more graphitized they get through etching process. In order to infer Titan's aerosols composition, our work highlights a need for constraints on the residence time of aerosols in Titan's ionosphere. [1] Waite et al. (2009) Science , 316, p. 870[2] Szopa et al. (2006) PSS, 54, p. 394[3] Carrasco et al. (2016) PSS, 128, p. 52

Development of Si3N4 and SiC of improved toughness. [for gas turbine engines

NASA Technical Reports Server (NTRS)

Brennan, J. J.; Hulse, C. O.

1977-01-01

The application of energy absorbing surface layers to Si3N4 and SiC was investigated. Among the layers studied were microcracked materials such as iron titanate and a silica-zircon mixture and porous materials such as reaction sintered Si3N4. Energy absorption due to microcrack extension upon impact was found not to be an important mechanism. Instead, the fivefold improvement in Charpy and ballistic impact at elevated temperature (1250 C and 1370 C) found for Fe2TiO5 was due to plastic deformation while similar improvement found for silica-zircon mixtures at RT was due to crushing of the porous material. Due to thermal expansion mismatch, these two materials could not withstand thermal cycling when used as energy absorbing surface layers on Si3N4. Reaction sintered Si3N4 layers on dense Si3N4 were found to give up to a sevenfold increase in ballistic impact resistance due to crushing of the layer upon impact. High porosity (45%), large particle size R.S. Si3N4 layers fabricated from -100, +200 mesh Si powder gave better impact improvement than less porous (30%), small particle size layers fabricated from -325 mesh Si powder.

CL-imaging and ion microprobe dating of single zircons from a high-grade rock from the Central Zone, Limpopo Belt, South Africa: Evidence for a single metamorphic event at ˜2.0 Ga

NASA Astrophysics Data System (ADS)

Mouri, H.; Brandl, G.; Whitehouse, M.; de Waal, S.; Guiraud, M.

2008-02-01

The combination of ion microprobe dating and cathodoluminescence (CL) imaging of zircons from a high-grade rock from the Central Zone of the Limpopo Belt were used to constrain the age of metamorphic events in the area. Zircon grains extracted from an orthopyroxene-gedrite-bearing granulite were prepared for single crystal CL-imaging and ion microprobe dating. The grains display complex zoning when using SEM-based CL-imaging. A common feature in most grains is the presence of a distinct core with a broken oscillatory zoned structure, which clearly appears to be the remnant of an original grain of igneous origin. This core is overgrown by an unzoned thin rim measuring about 10-30 μm in diameter, which is considered as new zircon growth during a single metamorphic event. Selected domains of the zircon grains were analysed for U, Pb and Th isotopic composition using a CAMECA IMS 1270 ion microprobe (Nordsim facility). Most of the grains define a near-concordant cluster with some evidence of Pb loss. The most concordant ages of the cores yielded a weighted mean 207Pb/ 206Pb age of 2689 ± 15 (2 σ) Ma, interpreted as the age of the protolith of an igneous origin. The unzoned overgrowths of the zircon grains yielded a considerably younger weighted mean 207Pb/ 206Pb age of ˜2006.5 ± 8.0 Ma (2 σ), and these data are interpreted to reflect closely the age of the ubiquitous high-grade metamorphic event in the Central Zone. This study shows clearly, based on both the internal structure of the zircons and the data obtained by ion microprobe dating, that only a single metamorphic event is recorded by the studied 2.69 Ga old rocks, and we found no evidence of an earlier metamorphic event at ˜2.5 Ga as postulated earlier by some workers.

Geochronology of Zircon in Eclogite Reveals Imbrication of the Ultrahigh-Pressure Western Gneiss Region of Norway.

NASA Astrophysics Data System (ADS)

Young, D. J.; Kylander-Clark, A. R.; Root, D. B.

2014-12-01

Eclogite provides the only record of kinematic events at the deepest levels of orogens. Integrating the U-Pb geochronology and trace element chemistry of zircon in eclogite reveals the most complete view of the PTt history, yet low concentrations of uranium and zirconium and drier compositions that hinder zircon growth at peak conditions render it a challenging rocktype for this approach. The iconic Western Gneiss Region (WGR) in Norway is one of the largest terranes of deeply subducted continental rocks in the world, and contains many indicators of ultrahigh-pressure metamorphic conditions (P>2.8 GPa) that developed during the Siluro-Devonian Caledonian Orogeny. A metamorphic transition from amphibolite-facies to ultrahigh-pressure eclogite facies broadly coincides with a km-scale shear zone that underlies the majority of the WGR. A critical unknown is the timing of movement on this feature, which emplaced allochthonous units above the Baltica basement, but might also have accommodated late-orogenic exhumation of the WGR from mantle depths. We carried out laser ablation split-stream ICPMS (LASS) and selected multigrain TIMS analyses of zircons from eleven eclogites across the southern WGR, of which eight are located within or above the shear zone. LASS spots on polished grains mostly yield weakly discordant Proterozoic intrusive ages, and often minimal indication of a Caledonian (U)HP metamorphic overprint. Direct ablation into unpolished zircon reveals thin rims of Caledonian age in some cases. Overall, the dataset shows that all samples began zircon growth at approximately the same time (ca. 430-420 Ma). Eclogite from lower levels of the shear zone does not contain any dates younger than ca. 410 Ma, however, while eclogite from higher levels continued growth until ca. 400 Ma. We interpret this to result from thrusting of the WGR above cooler basement after 410 Ma, terminating new zircon crystallization within the shear zone but allowing limited further growth in rocks above.

Provenance analysis and detrital zircon geochronology on the onshore Makran accretionary wedge, SE Iran: implication for the geodynamic setting

NASA Astrophysics Data System (ADS)

Mohammadi, Ali; Burg, Jean-Pierre; Winkler, Wilfried; Ruh, Jonas

2014-05-01

The Makran, located in Southeast Iran and South Pakistan, is one of the largest accretionary wedges on Earth. In Iran it comprises turbiditic sediments ranging in age from Late Cretaceous to Holocene. We present a provenance analysis on sandstones, which is aimed at reconstructing the assemblages of source rocks and the tectonic setting from which the clastic material was derived. Sandstone samples collected from different units span the regional stratigraphy from Late Cretaceous to Miocene. Laser ablation ICP-MS resulted in ca 2800 new U-Pb ages of individual detrital zircons from 18 samples collected in onshore Makran. 101 detrital zircons from a Late Cretaceous fine grained sandstone range from 180 to 160 Ma (Middle Jurassic). 478 detrital zircons from mid- to late Eocene sandstones allow differentiating a NE and NW sector of the Makran Basin. Zircon grains in the NE basin belong to two populations peaking at 180 to 160 Ma (late Early to Middle Jurassic) and 50 to 40 Ma (Mid-Eocene), with the noticeable absence of Cretaceous grains. In the NW basin, detrital zircons are 120 to 40 Ma (late Early Cretaceous to Lutetian, Eocene). 587 detrital zircon grains from fine to medium grained Oligocene sandstones collected over the whole area also range from 120 to 40 Ma (late Early Cretaceous to Eocene, Lutetian). 1611 detrital zircons from early Miocene sandstones show again distinctly different ages in the eastern and western parts of the basin. They range from 120 to 40 Ma (late Early Cretaceous to Eocene) in the eastern and from 80 to 40 Ma (Late Cretaceous to Eocene) in the western basin. Hf isotopes analyses were performed on 120 zircon grains from 6 samples. Negative values (-2 to -15) in Middle Jurassic and late Early Cretaceous zircons indicate minor or no influence of mantle reservoirs which implies a rifting setting during crystallization of the zircons. Low negative to positive (-5 to +10) values in Late Cretaceous and Eocene zircons indicate mixed crustal and juvenile magma sources, which are common in continental arc environments. Point counts of 32 sandstone thin sections were performed following the Gazzi-Dikinson method. 300-400 points were counted in each thin section. The sandstones are feldspathic litharenites and litharenites. Feldspar is dominantly plagioclase (> 90%) with minor amounts of K-feldspar. Most of the quartz grains (75%) are mono-crystalline but poly-crystalline ones (maximum 25%) also occur. Rock fragments are represented by sedimentary, volcanic and metamorphic grains. Volcanic rock-fragments mostly are andesites and volcanic chert. Sedimentary lithic grains comprise mostly sandstone, siltstone, limestone and dolomite. Metamorphic lithic grains generally are low-grade schists and phyllites. In various compositional ternary diagrams, the sources of the sandstones plot in the transitional to dissected arc and recycled orogenic fields. We selected 26 samples for heavy mineral study. 200-300 grain were identified and counted in each sample. Heavy mineral suites show a highly variable composition including (1) a group of ultra-stable minerals (zircon, monazite, tourmaline, rutile, brookite, anatase and sphene) derived from a granitic continental crust sources, (2) metastable minerals delivered from variable metamorphic-grade source rocks (epidote group, garnet, staurolite, chloritoid, kyanite, andalusite, glaucophane), (3) chromian spinel from ultrabasic rocks, (4) common hornblende either supplied from metamorphic or basic igneous series, and (5) a local pyroxene-rich source in the pyroclastic sandstone formation overlying pillow lavas. Glaucophane (5-20%) occurs in several samples, which indicates high-pressure/low-temperature metamorphic rocks in the detrital source areas for Eocene and Miocene sandstones. Earlier work in the Pakistani Makran suggested that pre-Miocene sediments were supplied from the Himalaya, whereas Miocene to Recent deposits were reworked older sediments of the accretionary wedge. Our data do not support this conclusion. Instead, we identified rifting-related detrital sources from Middle Jurassic to late Early Cretaceous (175 - 100 Ma) and the establishment of a continental volcanic arc from Late Cretaceous to Eocene (80 to 40 Ma). In addition, paleocurrent directions in Makran sandstone show general sediment transport from North to South; Cr-spinel as well as high-P/low-T heavy minerals most likely have been derived from the blueschist-bearing Makran ophiolitic and igneous belt to the North.

Hydrogen diffusion in Zircon

NASA Astrophysics Data System (ADS)

Ingrin, Jannick; Zhang, Peipei

2016-04-01

Hydrogen mobility in gem quality zircon single crystals from Madagascar was investigated through H-D exchange experiments. Thin slices were annealed in a horizontal furnace flushed with a gas mixture of Ar/D2(10%) under ambient pressure between 900 ° C to 1150 ° C. FTIR analyses were performed on oriented slices before and after each annealing run. H diffusion along [100] and [010] follow the same diffusion law D = D0exp[-E /RT], with log D0 = 2.24 ± 1.57 (in m2/s) and E = 374 ± 39 kJ/mol. H diffusion along [001] follows a slightly more rapid diffusion law, with log D0 = 1.11 ± 0.22 (in m2/s) and E = 334 ± 49 kJ/mol. H diffusion in zircon has much higher activation energy and slower diffusivity than other NAMs below 1150 ° C even iron-poor garnets which are known to be among the slowest (Blanchard and Ingrin, 2004; Kurka et al. 2005). During H-D exchange zircon incorporates also deuterium. This hydration reaction involves uranium reduction as it is shown from the exchange of U5+ and U4+ characteristic bands in the near infrared region during annealing. It is the first time that a hydration reaction U5+ + OH- = U4+ + O2- + 1/2H2, is experimentally reported. The kinetics of deuterium incorporation is slightly slower than hydrogen diffusion, suggesting that the reaction is limited by hydrogen mobility. Hydrogen isotopic memory of zircon is higher than other NAMs. Zircons will be moderately retentive of H signatures at mid-crustal metamorphic temperatures. At 500 ° C, a zircon with a radius of 300 μm would retain its H isotopic signature over more than a million years. However, a zircon is unable to retain this information for geologically significant times under high-grade metamorphism unless the grain size is large enough. Refrences Blanchard, M. and Ingrin, J. (2004) Hydrogen diffusion in Dora Maira pyrope. Physics and Chemistry of Minerals, 31, 593-605. Kurka, A., Blanchard, M. and Ingrin, J. (2005) Kinetics of hydrogen extraction and deuteration in grossular. Mineralogical Magazine, 69, 359-371.

The role of trace element partitioning between garnet, zircon and orthopyroxene on the interpretation of zircon U-Pb ages: an example from high-grade basement in Calabria (Southern Italy)

NASA Astrophysics Data System (ADS)

Fornelli, A.; Langone, A.; Micheletti, F.; Pascazio, A.; Piccarreta, G.

2014-03-01

The recognition of the coeval growth of zircon, orthopyroxene and garnet domains formed during the same metamorphic cycle has been attempted with detailed microanalyses coupled with textural analyses. A coronitic garnet-bearing granulite from the lower crust of Calabria has been considered. U-Pb zircon data and zircon, garnet and orthopyroxene chemistries, at different textural sites, on a thin section of the considered granulite have been used to test possible equilibrium and better constrain the geological significance of the U-Pb ages related to zircon separates from other rocks of the same structural level. The garnet is very rich in REE and is characterised by a decrease in HREE from core to outer core and an increase in the margin. Zircons show core-overgrowth structures showing different chemistries, likely reflecting episodic metamorphic new growth. Zircon grains in matrix, corona around garnet and within the inner rim of garnet, are decidedly poorer in HREE up to Ho than garnet interior. Orthopyroxene in matrix and corona is homogeneously poor in REE. Thus, the outer core of garnet and the analysed zircon grains grew or equilibrated in a REE depleted system due to the former growth of garnet core. Zircon ages ranging from 357 to 333 Ma have been determined in the matrix, whereas ages 327-320 Ma and around 300 Ma have been determined, respectively, on cores and overgrowths of zircons from matrix, corona and inner rim of garnet. The calculated DREEzrn/grt and DREEopx/grt are largely different from the equilibrium values of literature due to strong depletion up to Ho in zircon and orthopyroxene with respect to garnet. On the other hand, the literature data show large variability. In the case study, (1) the D zrn/grt values define positive and linear trends from Gd to Lu as many examples from literature do and the values from Er to Lu approach the experimental results at about 900 °C in the combination zircon dated from 339 to 305 Ma with garnet outer core, and (2) D opx/grt values define positive trends reaching values considered as suggestive of equilibrium from Er to Lu only with respect to the outer core of garnet. The presence of a zircon core dated 320 Ma in the inner rim of garnet suggests that it, as well as those dated at 325-320 Ma in the other textural sites and, probably, those dated at 339-336 Ma showing depletion of HREE, grew after the garnet core, which sequestered a lot of HREE and earlier than the HREE rich margin of garnet. The quite uniform REE contents in orthopyroxene from matrix and corona and the low and uniform contents of HREE in the zircon overgrowths dated at about 300 Ma allow to think that homogenisation occurred during or after the corona formation around this age. The domains dated around 325-320 Ma would approximate the stages of decompression, whereas the metamorphic peak probably occurred earlier than 339 Ma.

Possibilities of surface coating for thermal insulation. [zirconium dioxide, titanium dioxide, and zircon coatings

NASA Technical Reports Server (NTRS)

Poeschel, E.; Weisser, G.

1979-01-01

Calculations performed for pulsating heat sources indicate a relatively thin (200-1000 micron) coating can lower temperature both inside and on the surface of a construction material. Various coating materials (including zirconium dioxide) are discussed, together with possible thermic stresses and ways to deal with the latter.

Experiment-scale molecular simulation study of liquid crystal thin films

NASA Astrophysics Data System (ADS)

Nguyen, Trung Dac; Carrillo, Jan-Michael Y.; Matheson, Michael A.; Brown, W. Michael

2014-03-01

Supercomputers have now reached a performance level adequate for studying thin films with molecular detail at the relevant scales. By exploiting the power of GPU accelerators on Titan, we have been able to perform simulations of characteristic liquid crystal films that provide remarkable qualitative agreement with experimental images. We have demonstrated that key features of spinodal instability can only be observed with sufficiently large system sizes, which were not accessible with previous simulation studies. Our study emphasizes the capability and significance of petascale simulations in providing molecular-level insights in thin film systems as well as other interfacial phenomena.

A strong electro-optically active lead-free ferroelectric integrated on silicon

NASA Astrophysics Data System (ADS)

Abel, Stefan; Stöferle, Thilo; Marchiori, Chiara; Rossel, Christophe; Rossell, Marta D.; Erni, Rolf; Caimi, Daniele; Sousa, Marilyne; Chelnokov, Alexei; Offrein, Bert J.; Fompeyrine, Jean

2013-04-01

The development of silicon photonics could greatly benefit from the linear electro-optical properties, absent in bulk silicon, of ferroelectric oxides, as a novel way to seamlessly connect the electrical and optical domain. Of all oxides, barium titanate exhibits one of the largest linear electro-optical coefficients, which has however not yet been explored for thin films on silicon. Here we report on the electro-optical properties of thin barium titanate films epitaxially grown on silicon substrates. We extract a large effective Pockels coefficient of reff=148 pm V-1, which is five times larger than in the current standard material for electro-optical devices, lithium niobate. We also reveal the tensor nature of the electro-optical properties, as necessary for properly designing future devices, and furthermore unambiguously demonstrate the presence of ferroelectricity. The integration of electro-optical active films on silicon could pave the way towards power-efficient, ultra-compact integrated devices, such as modulators, tuning elements and bistable switches.

Stoichiometry determination of (Pb,La)(Zr,Ti)O3-type nano-crystalline ferroelectric ceramics by wavelength-dispersive X-ray fluorescence spectrometry.

PubMed

Sitko, Rafał; Zawisza, Beata; Kita, Andrzej; Płońska, Małgorzata

2006-07-01

Analysis of small samples of lanthanum-doped lead zirconate titanate (PLZT) by wavelength-dispersive X-ray fluorescence spectrometry (WDXRF) is presented. The powdered material in ca. 30 mg was suspended in water and collected on the membrane filter. The pure oxide standards (PbO, La2O3, ZrO2 and TiO2) were used for calibration. The matrix effects were corrected using a theoretical influence coefficients algorithm for intermediate-thickness specimens. The results from XRF method were compared with the results from the inductively coupled plasma optical emission spectrometry (ICP-OES). Agreement between XRF and ICP-OES analysis was satisfactory and indicates the usefulness of XRF method for stoichiometry determination of PLZT.

An experimental study on the effect of temperature on piezoelectric sensors for impedance-based structural health monitoring.

PubMed

Baptista, Fabricio G; Budoya, Danilo E; de Almeida, Vinicius A D; Ulson, Jose Alfredo C

2014-01-10

The electromechanical impedance (EMI) technique is considered to be one of the most promising methods for developing structural health monitoring (SHM) systems. This technique is simple to implement and uses small and inexpensive piezoelectric sensors. However, practical problems have hindered its application to real-world structures, and temperature effects have been cited in the literature as critical problems. In this paper, we present an experimental study of the effect of temperature on the electrical impedance of the piezoelectric sensors used in the EMI technique. We used 5H PZT (lead zirconate titanate) ceramic sensors, which are commonly used in the EMI technique. The experimental results showed that the temperature effects were strongly frequency-dependent, which may motivate future research in the SHM field.

Analysis of signals propagating in a phononic crystal PZT layer deposited on a silicon substrate.

PubMed

Hladky-Hennion, Anne-Christine; Vasseur, Jérôme; Dubus, Bertrand; Morvan, Bruno; Wilkie-Chancellier, Nicolas; Martinez, Loïc

2013-12-01

The design of a stop-band filter constituted by a periodically patterned lead zirconate titanate (PZT) layer, polarized along its thickness, deposited on a silicon substrate and sandwiched between interdigitated electrodes for emission/reception of guided elastic waves, is investigated. The filter characteristics are theoretically evaluated by using finite element simulations: dispersion curves of a patterned PZT layer with a specific pattern geometry deposited on a silicon substrate present an absolute stop band. The whole structure is modeled with realistic conditions, including appropriate interdigitated electrodes to propagate a guided mode in the piezoelectric layer. A robust method for signal analysis based on the Gabor transform is applied to treat transmitted signals; extract attenuation, group delays, and wave number variations versus frequency; and identify stop-band filter characteristics.

A modified thickness extensional disk transducer.

PubMed

Trolier, S E; Xu, Q C; Newnham, R E

1988-01-01

Photolithography and chemical etching were investigated as a means of patterning miniature piezoelectric devices. Using a processing procedure analogous to that utilized in the production of integrated circuitry, concentrated hydrochloric acid and a commercially available photoresist were used to fabricate a number of complex structures from soft lead zirconate titanate (PZT) substrates. Among the devices produced in this manner was a modified thickness-mode resonator etched to destroy the simple geometry responsible for radial vibrations. The resultant transducer demonstrated significantly smaller amplitudes for lateral resonances and a marked reduction in the effective planar coupling coefficient over the unaltered disk. The results indicate that photolithographic patterning is useful both for eliminating spurious resonances from transducers for medical imaging or nondestructive evaluation and for engineering low planar coupling coefficients into a variety of substrate materials.

Damage Evaluation Based on a Wave Energy Flow Map Using Multiple PZT Sensors

PubMed Central

Liu, Yaolu; Hu, Ning; Xu, Hong; Yuan, Weifeng; Yan, Cheng; Li, Yuan; Goda, Riu; Alamusi; Qiu, Jinhao; Ning, Huiming; Wu, Liangke

2014-01-01

A new wave energy flow (WEF) map concept was proposed in this work. Based on it, an improved technique incorporating the laser scanning method and Betti's reciprocal theorem was developed to evaluate the shape and size of damage as well as to realize visualization of wave propagation. In this technique, a simple signal processing algorithm was proposed to construct the WEF map when waves propagate through an inspection region, and multiple lead zirconate titanate (PZT) sensors were employed to improve inspection reliability. Various damages in aluminum and carbon fiber reinforced plastic laminated plates were experimentally and numerically evaluated to validate this technique. The results show that it can effectively evaluate the shape and size of damage from wave field variations around the damage in the WEF map. PMID:24463430

Residual stress relief due to fatigue in tetragonal lead zirconate titanate ceramics

NASA Astrophysics Data System (ADS)

Hall, D. A.; Mori, T.; Comyn, T. P.; Ringgaard, E.; Wright, J. P.

2013-07-01

High energy synchrotron XRD was employed to determine the lattice strain ɛ{111} and diffraction peak intensity ratio R{200} in tetragonal PZT ceramics, both in the virgin poled state and after a bipolar fatigue experiment. It was shown that the occurrence of microstructural damage during fatigue was accompanied by a reduction in the gradient of the ɛ{111}-cos2 ψ plot, indicating a reduction in the level of residual stress due to poling. In contrast, the fraction of oriented 90° ferroelectric domains, quantified in terms of R{200}, was not affected significantly by fatigue. The change in residual stress due to fatigue is interpreted in terms of a change in the average elastic stiffness of the polycrystalline matrix due to the presence of inter-granular microcracks.

Large Displacement in Relaxor Ferroelectric Terpolymer Blend Derived Actuators Using Al Electrode for Braille Displays

NASA Astrophysics Data System (ADS)

Lu, S. G.; Chen, X.; Levard, T.; Diglio, P. J.; Gorny, L. J.; Rahn, C. D.; Zhang, Q. M.

2015-06-01

Poly(vinylidene fluoride) (PVDF) based polymers are attractive for applications for artificial muscles, high energy density storage devices etc. Recently these polymers have been found great potential for being used as actuators for refreshable full-page Braille displays for visually impaired people in terms of light weight, miniaturized size, and larger displacement, compared with currently used lead zirconate titanate ceramic actuators. The applied voltages of published polymer actuators, however, cannot be reduced to meet the requirements of using city power. Here, we report the polymer actuator generating quite large displacement and blocking force at a voltage close to the city power. Our embodiments also show good self-healing performance and disuse of lead-containing material, which makes the Braille device safer, more reliable and more environment-friendly.

Large Displacement in Relaxor Ferroelectric Terpolymer Blend Derived Actuators Using Al Electrode for Braille Displays.

PubMed

Lu, S G; Chen, X; Levard, T; Diglio, P J; Gorny, L J; Rahn, C D; Zhang, Q M

2015-06-16

Poly(vinylidene fluoride) (PVDF) based polymers are attractive for applications for artificial muscles, high energy density storage devices etc. Recently these polymers have been found great potential for being used as actuators for refreshable full-page Braille displays for visually impaired people in terms of light weight, miniaturized size, and larger displacement, compared with currently used lead zirconate titanate ceramic actuators. The applied voltages of published polymer actuators, however, cannot be reduced to meet the requirements of using city power. Here, we report the polymer actuator generating quite large displacement and blocking force at a voltage close to the city power. Our embodiments also show good self-healing performance and disuse of lead-containing material, which makes the Braille device safer, more reliable and more environment-friendly.

Wave velocity characteristic for Kenaf natural fibre under impact damage

NASA Astrophysics Data System (ADS)

Zaleha, M.; Mahzan, S.; Fitri, Muhamad; Kamarudin, K. A.; Eliza, Y.; Tobi, A. L. Mohd

2017-01-01

This paper aims to determining the wave velocity characteristics for kenaf fibre reinforced composite (KFC) and it includes both experimental and simulation results. Lead zirconate titanate (PZT) sensor were proposed to be positioned to corresponding locations on the panel. In order to demonstrate the wave velocity, an impacts was introduced onto the panel. It is based on a classical sensor triangulation methodology, combines with experimental strain wave velocity analysis. Then the simulation was designed to replicate panel used in the experimental impacts test. This simulation was carried out using ABAQUS. It was shown that the wave velocity propagates faster in the finite element simulation. Although the experimental strain wave velocity and finite element simulation results do not match exactly, the shape of both waves is similar.

Power harvesting using PZT ceramics embedded in orthopedic implants.

PubMed

Chen, Hong; Liu, Ming; Jia, Chen; Wang, Zihua

2009-09-01

Battery lifetime has been the stumbling block for many power-critical or maintenance-free real-time embedded applications, such as wireless sensors and orthopedic implants. Thus a piezoelectric material that could convert human motion into electrical energy provides a very attractive solution for clinical implants. In this work, we analyze the power generation characteristics of stiff lead zirconate titanate (PZT) ceramics and the equivalent circuit through extensive experiments. Our experimental framework allows us to explore many important design considerations of such a PZT-based power generator. Overall we can achieve a PZT element volume of 0.5 x 0.5 x 1.8 cm, which is considerably smaller than the results reported so far. Finally, we outline the application of our PZT elements in a total knee replacement (TKR) implant.

Voltage-impulse-induced dual-range nonvolatile magnetization modulation in metglas/PZT heterostructure

NASA Astrophysics Data System (ADS)

Tang, Xiaoli; Su, Hua; Zhang, Huaiwu; Sun, Nian X.

2016-11-01

Dual-range, nonvolatile magnetization modulation induced by voltage impulses was investigated in the metglas/lead zirconate titanate (PZT) heterostructure at room temperature. The heterostructure was obtained by bonding a square metglas ribbon on the top electrode of the PZT substrate, which contained defect dipoles resulting from acceptor doping. The PZT substrate achieved two strain hysteretic loops with the application of specific voltage impulse excitation modes. Through strain-mediated magnetoelectric coupling between the metglas ribbon and the PZT substrate, two strain hysteretic loops led to a dual-range nonvolatile magnetization modulation in the heterostructure. Reversible and stable voltage-impulse-induced nonvolatile modulation in the ferromagnetic resonance field and magnetic hysteresis characteristics were also realized. This method provides a promising approach in reducing energy consumption in magnetization modulation and other related devices.

A micromachined carbon nanotube film cantilever-based energy cell

NASA Astrophysics Data System (ADS)

Gong, Zhongcheng; He, Yuan; Tseng, Yi-Hsuan; O'Neal, Chad; Que, Long

2012-08-01

This paper reports a new type of energy cell based on micromachined carbon nanotube film (CNF)-lead zirconate titanate cantilevers that is fabricated on silicon substrates. Measurements found that this type of micro-energy cell generates both AC voltages due to the self-reciprocation of the microcantilevers and DC voltages due to the thermoelectric effect upon exposure to light and thermal radiation, resulting from the unique optical and thermal properties of the CNF. Typically the measured power density of the micro-energy cell can be from 4 to 300 μW cm-2 when it is exposed to sunlight under different operational conditions. It is anticipated that hundreds of integrated micro-energy cells can generate power in the range of milliwatts, paving the way for the construction of self-powered micro- or nanosystems.

Long-Term (4 mo) Oxygen Isotope Exchange Experiment between Zircon and Hydrothermal Fluid

NASA Astrophysics Data System (ADS)

Bindeman, I. N.; Schmitt, A. K.; Lundstrom, C.; Golledge, S.

2013-12-01

Knowing oxygen diffusivity in zircon has several critical applications: 1) establishing zircon stability and solubility in hot silica-saturated hydrothermal solutions; 2) deriving metamorphic and magmatic heating timescales from intra-crystal oxygen isotopic gradients; 3) assessing the survivability of oxygen isotopic signatures in Hadean zircons. We report results of a microanalytical investigation of an isotope exchange experiment using a cold-seal pressure apparatus at 850°C and 500 MPa over 4 months duration. Natural zircon, quartz and rutile were sealed with a silica-rich solution doped with 18-O, D, 7-Li and 10-B in a gold capsule. The diffusion length-scales were examined by depth profiling using time-of-flight (TOF) and high-sensitivity dynamic secondary ionization mass spectrometry (SIMS). Starting materials had distinct and homogeneous δ18O: zircon from Mesa Falls tuff of Yellowstone (+3.6‰), rutile from Karelia (-29‰), Bishop Tuff Quartz (+8.4‰), and δ18O doped water (+400‰). Starting material zircon showed invariant 18O/16O during depth profiling. After the 4 month experiment, rutile crystal surfaces displayed etching (100's of nm), while zircon exteriors lacked visible change. Quartz was completely dissolved and reprecipitated in a minor residue. Rutile developed ~2 μm long Fickian diffusion profiles largely consistent with the wet diffusion coefficients for rutile previously reported [1]. Surface U-Pb dating of zircon detected no significant Pb loss from the outermost ~300 nm of the crystal face and returned identical core-face ages. We performed δ18O depth profiling of zircon in two directions. First, forward profiles (crystal rim inwards) by dynamic SIMS (no surface treatment besides Au-coating; Cs+ beam of 20 kV impact energy) showed initially high and decreasing 18O/16O over ~130 nm; TOF-SIMS forward profiles using a 2 kV Cs+ sputter beam and 25 kV Bi3+ primary ions on uncoated zircon surfaces (cleaned for 2 min with HF) yielded decreasing 18O/16O over a similar length scale. These profile lengths are largely consistent with wet diffusion coefficient for zircon reported by [2]. In contrast, back-side depth profiling was conducted by dynamic SIMS on a 1 μm thick wafer cut from the zircon by FIB. No significant elevation in 18O/16O was detected when the surface layer was penetrated, consistent with dry diffusion coefficients of [2]. The results suggest that nm-scale SIMS surface analysis of isotope ratios is challenging. We are investigating if they can be critically affected by knock-on effects and/or continuous mixing of a very thin enriched surface layer during depth profiling in our and previous experiments. [1] Moore et al., 1998, Am. Min. 83, 700-711 [2] Watson and Cherniak, 1997, EPSL 148, 537-544

Preliminary investigation of an active PLZT lens

NASA Astrophysics Data System (ADS)

Peters, Bruce R.; Reardon, Patrick J.; Wong, K. J.

2001-05-01

The design analysis and preliminary testing of a prototype AFOCL is described. The AFOCL is an active optical component composed of solid state lead lanthanum-modified zirconate titanate (PLZT) ferroelectric ceramic with patterned indium tin oxide (ITO) transparent surface electrodes that modulate the refractive index of the PLZT to function as an electro- optic lens. The AFOCL was developed to perform optical re- alignment and wavefront correction to enhance the performance of Ultra-Lightweight Structures and Space Observatories. The AFOCL would be an active optical component within a larger optical system. Information from a wavefront sensor would be processed to provide input to the AFOCL to drive the sense4d wavefront tot he desired shape and location. While offering variable and rapid focusing capability similar to liquid crystal based spatial light modulators, the AFOCL offers some potential advantages because it is a solid-stat, stationary, low-mass, rugged, and thin optical element that can produce wavefront quality comparable to the solid refractive lens it replaces. The AFOCL acts as a positive or negative lens by producing a parabolic phase-shift in the PLZT material through the application of a controlled voltage potential across the ITO electrodes. To demonstrate the technology, a 4 mm diameter lens was fabricated to produce 5-waves of optical power operating at 2.051 micrometers wavelength. Optical metrology was performed on the device to measure focal length, optical quality, and efficiency for a variety of test configurations. Preliminary data was analyzed and compared to idealized performance available from computer-based models of the AFOCL.

Preliminary Investigation of an Active PLZT Lens

NASA Technical Reports Server (NTRS)

Lightsey, W. D.; Peters, B. R.; Reardon, P. J.; Wong, J. K.

2001-01-01

The design, analysis and preliminary testing of a prototype Adjustable Focus Optical Correction Lens (AFOCL) is described. The AFOCL is an active optical component composed of solid state lead lanthanum-modified zirconate titanate (PLZT) ferroelectric ceramic with patterned indium tin oxide (ITO) transparent surface electrodes that modulate the refractive index of the PLZT to function as an electro-optic lens. The AFOCL was developed to perform optical re-alignment and wavefront correction to enhance the performance of Ultra-Lightweight Structures and Space Observatories (ULSSO). The AFOCL has potential application as an active optical component within a larger optical system. As such, information from a wavefront sensor would be processed to provide input to the AFOCL to drive the sensed wavefront to the desired shape and location. While offering variable and rapid focussing capability (controlled wavefront manipulation) similar to liquid crystal based spatial light modulators (SLM), the AFOCL offers some potential advantages because it is a solid-state, stationary, low-mass, rugged, and thin optical element that can produce wavefront quality comparable to the solid refractive lens it replaces. The AFOCL acts as a positive or negative lens by producing a parabolic phase-shift in the PLZT material through the application of a controlled voltage potential across the ITO electrodes. To demonstrate the technology, a 4 mm diameter lens was fabricated to produce 5-waves of optical power operating at 2.051 micrometer wavelength. Optical metrology was performed on the device to measure focal length, optical quality, and efficiency for a variety of test configurations. The data was analyzed and compared to theoretical data available from computer-based models of the AFOCL.

Development of dual PZT transducers for reference-free crack detection in thin plate structures.

PubMed

Sohn, Hoon; Kim, Seuno Bum

2010-01-01

A new Lamb-wave-based nondestructive testing (NDT) technique, which does not rely on previously stored baseline data, is developed for crack monitoring in plate structures. Commonly, the presence of damage is identified by comparing "current data" measured from a potentially damaged stage of a structure with "baseline data" previously obtained at the intact condition of the structure. In practice, structural defects typically take place long after collection of the baseline data, and the baseline data can be also affected by external loading, temperature variations, and changing boundary conditions. To eliminate the dependence on the baseline data comparison, the authors previously developed a reference-free NDT technique using 2 pairs of collocated lead zirconate titanate (PZT) transducers placed on both sides of a plate. This reference-free technique is further advanced in the present study by the necessity of attaching transducers only on a single surface of a structure for certain applications such as aircraft. To achieve this goal, a new design of PZT transducers called dual PZT transducers is proposed. Crack formation creates Lamb wave mode conversion due to a sudden thickness change of the structure. This crack appearance is instantly detected from the measured Lamb wave signals using the dual PZT transducers. This study also suggests a reference-free statistical approach that enables damage classification using only the currently measured data set. Numerical simulations and experiments were conducted using an aluminum plate with uniform thickness and fundamental Lamb waves modes to demonstrate the applicability of the proposed technique to reference-free crack detection.

Multiferroic Applications of Nanoarchitectured, Solution-Processed Materials

NASA Astrophysics Data System (ADS)

Buditama, Abraham Nataniel

This dissertation compiles work on sol-gel syntheses of multiferroic materials and applications thereof. Multiferroics, or materials that simultaneously exhibit multiple order parameters such as ferromagnetism, ferroelectricity, or ferroelasticity, may be fabricated by solution processing techniques. Specifically, these techniques may be used to control both the atomic and the nanoscale structures of piezoelectric lead zirconate titanate (PbZrxTi 1-xO3 or PZT) and magnetostrictive cobalt ferrite (CoFe 2O4 or CFO). The first part of this work focuses on strain-coupling PZT and CFO into a magnetoelectric composite. A mesoporous CFO framework was synthesized using block copolymer templating, which was subsequently conformally filled by PZT by atomic layer deposition (ALD). The final porosity of the film is controlled by the ALD PZT layer, and we show that this porosity influences the magnetoelectric coupling of the composite. An ex situ external electric field is applied to the composite, and samples with the greatest porosity, and thus greatest mechanical flexibility, were able to accommodate strain transfer to the CFO, resulting in a greater reduction of the sample saturation magnetization. The second part of this work focuses on using solution processing to control domain-level contributions to the material's ferroic properties. An iterative spin coating process can be used to create PZT films of arbitrary thickness. Electric domains are generally pinned in nanoscale PZT thin films, but models of PZT films on the mesoscale must consider domain reorientation. As for CFO, solution processing may be used to control the CFO grain size, which in turn limits the size of its magnetic domains, and subsequently its static magnetic properties.

An X-ray photoelectron spectroscopy study of BF3 adsorption on positively and negatively poled LiNbO3 (0001)

NASA Astrophysics Data System (ADS)

Herdiech, M. W.; Mönig, H.; Altman, E. I.

2014-08-01

Adsorption of the strong Lewis acid BF3 was investigated to probe the sensitivity of the Lewis basicity of surface oxygens on LiNbO3 (0001) to the ferroelectric polarization direction. Adsorption and desorption were characterized by using X-ray photoelectron spectroscopy (XPS) to monitor the intensity and binding energy of the F 1s core level as a function of BF3 exposure and temperature. The results indicate that both BF3 uptake and desorption are very similar on the positively and negatively poled surfaces. In particular, BF3 only weakly adsorbs with the majority of the adsorbed BF3 desorbing below 200 K. Despite the similarities in the uptake and desorption behavior, the binding energy of the F 1s peak relative to the substrate Nb 3d5/2 peak was sensitive to the polarization direction, with the F 1s peak occurring at a binding energy up to 0.3 eV lower on positively poled than negatively poled LiNbO3 for equivalent BF3 exposures. Rather than reflecting a difference in bonding to the surface, however, this shift could be associated with oppositely oriented dipoles at the positively and negatively poled surfaces creating opposite band offsets between the adsorbate and the substrate. A similar effect was observed with lead zirconate titanate thin films where the Pb 4f XPS peak position changes as a function of temperature as a result of the pyroelectric effect which changes the magnitude of the surface and interface dipoles.

Strain engineered barium strontium titanate for tunable thin film resonators

DOE Office of Scientific and Technical Information (OSTI.GOV)

Khassaf, H.; Khakpash, N.; Sun, F.

2014-05-19

Piezoelectric properties of epitaxial (001) barium strontium titanate (BST) films are computed as functions of composition, misfit strain, and temperature using a non-linear thermodynamic model. Results show that through adjusting in-plane strains, a highly adaptive rhombohedral ferroelectric phase can be stabilized at room temperature with outstanding piezoelectric response exceeding those of lead based piezoceramics. Furthermore, by adjusting the composition and the in-plane misfit, an electrically tunable piezoelectric response can be obtained in the paraelectric state. These findings indicate that strain engineered BST films can be utilized in the development of electrically tunable and switchable surface and bulk acoustic wave resonators.

Brittle-ductile deformation effects on zircon crystal-chemistry and U-Pb ages: an example from the Finero Mafic Complex (Ivrea-Verbano Zone, western Alps)

NASA Astrophysics Data System (ADS)

Langone, Antonio; José Alberto, Padrón-Navarta; Zanetti, Alberto; Mazzucchelli, Maurizio; Tiepolo, Massimo; Giovanardi, Tommaso; Bonazzi, Mattia

2016-04-01

A detailed structural, geochemical and geochronological survey was performed on zircon grains from a leucocratic dioritic dyke discordantly intruded within meta-diorites/gabbros forming the External Gabbro unit of the Finero Mafic Complex. This latter is nowadays exposed as part of a near complete crustal section spanning from mantle rocks to upper crustal metasediments (Val Cannobina, Ivrea-Verbano Zone, Italy). The leucocratic dyke consists mainly of plagioclase (An18-24Ab79-82Or0.3-0.7) with subordinate amounts of biotite, spinel, zircon and corundum. Both the leucocratic dyke and the surrounding meta-diorites show evidence of ductile deformation occurred under amphibolite-facies conditions. Zircon grains (up to 2 mm in length) occur mainly as euhedral grains surrounded by fine grained plagioclase-dominated matrix and pressure shadows, typically filled by oxides. Fractures and cracks within zircon are common and can be associated with grain displacement or they can be filled by secondary minerals (oxides and chlorite). Cathodoluminescence (CL) images show that zircon grains have internal features typical of magmatic growth, but with local disturbances. However EBSD maps on two selected zircon grains revealed a profuse mosaic texture resulting in an internal misorientation of ca. 10o. The majority of the domains of the mosaic texture are related to parting and fractures, but some domains show no clear relation with brittle features. Rotation angles related to the mosaic texture are not crystallographically controlled. In addition, one of the analysed zircons shows clear evidence of plastic deformation at one of its corners due to indentation. Plastic deformation results in gradual misorientations of up to 12o, which are crystallographically controlled. Trace elements and U-Pb analyses were carried out by LA-ICP-MS directly on petrographic thin sections and designed to cover the entire exposed surface of selected grains. Such investigations revealed a strong correlation between internal zircon structures, chemistry, U-Pb isotope ratios and mylonitic fabric. U-Pb data return highly discordant and variable ages: in particular, the 206Pb/238U ages range from Carboniferous to Triassic within the same zircon grain. The youngest 206Pb/238U data derive from narrow axial stripes oriented parallel or at low angle with respect to the foliation planes. These stripes are characterized by an overall HREE, Y, U and Th enrichment possibly reflecting deformation of the grain in presence of interstitial fluid phases, likely related to a concomitant magmatic activity. Deformation related structures (cracks and fractures) within zircon grains acted as fast-diffusion pathways allowing fluids to modify the geochemistry and isotopic systems of zircon. Our results suggest that fluid-assisted brittle-ductile deformation can severely modify the trace elements and isotopic composition of zircon with unexpected patterns constrained by stress regime. In similar cases, our observations suggest that, for a more appropriate interpretation of the petrologic evolution and age variability, a direct characterization of the internal structures of zircons still placed in their microtextural site is highly recommended.

Optimization of Strontium Titanate (SrTiO3) Thin Films Fabricated by Metal Organic Chemical Vapor Deposition (MOCVD) for Microwave-Tunable Devices

DTIC Science & Technology

2015-12-01

induced (non)stoichiometry on the structure, dielectric response, and thermal conductivity of SrTiO3 thin films. Chemistry of Materials. 2012;24:331...must be below a few percent. The external sources of loss, such as conductor interface losses and various losses that inevitably arise from device...epitaxy • Excellent control of film stoichiometry and thickness • Large area uniformity and potential for complex structure coating • Optimized

The organic aerosols of Titan

NASA Technical Reports Server (NTRS)

Khare, B. N.; Sagan, C.; Thompson, W. R.; Arakawa, E. T.; Suits, F.; Calcott, T. A.; Williams, M. W.; Shrader, S.; Ogino, H.; Willingham, T. O.

1986-01-01

A dark reddish organic solid, called tholin, is synthesized from simulated Titanian atmospheres by irradiation with high energy electrons in a plasma discharge. The visible reflection spectrum of this tholin is found to be similar to that of high altitude aerosols responsible for the albedo and reddish color of Titan. The real (n) and imaginary (k) parts of the complex refractive index of thin films of Titan prepared by continuous dc discharge through a 0.9 N2/0.1 CH4 gas mixture at 0.2 mb is determined from X-ray to microwave frequencies. Values of n (approx. 1.65) and k (approx. 0.004 to 0.08) in the visible are consistent with deductions made by groundbased and spaceborne observations of Titan. Many infrared absorption features are present in k(lambda), including the 4.6 micrometer nitrile band. Molecular analysis of the volatile components of this tholin was performed by sequential and nonsequential pyrolytic gas chromatography/mass spectrometry. More than one hundred organic compounds are released; tentative identifications include saturated and unsaturated aliphatic hydrocarbons, substituted polycylic aromatics, nitriles, amines, pyrroles, pyrazines, pyridines, pyrimidines, and the purine, adenine. In addition,acid hydrolysis produces a racemic mixture of biological and nonbiological amino acids. Many of these molecules are implicated in the origin of life on Earth, suggesting Titan as a contemporary laboratory environment for prebiological organic chemistry on a planetary scale.

Effect of Selectively Etched Ferroelectric Thin-Film Layer on the Performance of a Tunable Bandpass Filter

NASA Technical Reports Server (NTRS)

Subramanyam, Guru; Vignesparamoorthy, Sivaruban; Mueller, Carl; VanKeuls, Fred; Warner, Joseph; Miranda, Felix A.

2001-01-01

The main purpose of this work is to study the effect of a selectively etched ferroelectric thin film layer on the performance of an electrically tunable filter. An X-band tunable filter was designed, fabricated and tested on a selectively etched Barium Strontium Titanate (BSTO) ferroelectric thin film layer. Tunable filters with varying lengths of BSTO thin-film in the input and output coupling gaps were modeled, as well as experimentally tested. Experimental results showed that filters with coupling gaps partially filled with BSTO maintained frequency tunability and improved the insertion loss by approx. 2dB. To the best of our knowledge, these results represent the first experimental demonstration of the advantages of selective etching in the performance of thin film ferroelectric-based tunable microwave components.

Landscape Evolution of Titan

NASA Technical Reports Server (NTRS)

Moore, Jeffrey

2012-01-01

Titan may have acquired its massive atmosphere relatively recently in solar system history. The warming sun may have been key to generating Titan's atmosphere over time, starting from a thin atmosphere with condensed surface volatiles like Triton, with increased luminosity releasing methane, and then large amounts of nitrogen (perhaps suddenly), into the atmosphere. This thick atmosphere, initially with much more methane than at present, resulted in global fluvial erosion that has over time retreated towards the poles with the removal of methane from the atmosphere. Basement rock, as manifested by bright, rough, ridges, scarps, crenulated blocks, or aligned massifs, mostly appears within 30 degrees of the equator. This landscape was intensely eroded by fluvial processes as evidenced by numerous valley systems, fan-like depositional features and regularly-spaced ridges (crenulated terrain). Much of this bedrock landscape, however, is mantled by dunes, suggesting that fluvial erosion no longer dominates in equatorial regions. High midlatitude regions on Titan exhibit dissected sedimentary plains at a number of localities, suggesting deposition (perhaps by sediment eroded from equatorial regions) followed by erosion. The polar regions are mainly dominated by deposits of fluvial and lacustrine sediment. Fluvial processes are active in polar areas as evidenced by alkane lakes and occasional cloud cover.

A rigid and weathered ice shell on Titan.

PubMed

Hemingway, D; Nimmo, F; Zebker, H; Iess, L

2013-08-29

Several lines of evidence suggest that Saturn's largest moon, Titan, has a global subsurface ocean beneath an outer ice shell 50 to 200 kilometres thick. If convection is occurring, the rigid portion of the shell is expected to be thin; similarly, a weak, isostatically compensated shell has been proposed to explain the observed topography. Here we report a strong inverse correlation between gravity and topography at long wavelengths that are not dominated by tides and rotation. We argue that negative gravity anomalies (mass deficits) produced by crustal thickening at the base of the ice shell overwhelm positive gravity anomalies (mass excesses) produced by the small surface topography, giving rise to this inverse correlation. We show that this situation requires a substantially rigid ice shell with an elastic thickness exceeding 40 kilometres, and hundreds of metres of surface erosion and deposition, consistent with recent estimates from local features. Our results are therefore not compatible with a geologically active, low-rigidity ice shell. After extrapolating to wavelengths that are controlled by tides and rotation, we suggest that Titan's moment of inertia may be even higher (that is, Titan may be even less centrally condensed) than is currently thought.

Multiple age components in individual molybdenite grains

USGS Publications Warehouse

Aleinikoff, John N.; Creaser, Robert A.; Lowers, Heather; Magee, Charles W.; Grauch, Richard I.

2012-01-01

Re–Os geochronology of fractions composed of unsized, coarse, and fine molybdenite from a pod of unusual monazite–xenotime gneiss within a granulite facies paragneiss, Hudson Highlands, NY, yielded dates of 950.5 ± 2.5, 953.8 ± 2.6, and 941.2 ± 2.6 Ma, respectively. These dates are not recorded by co-existing zircon, monazite, or xenotime. SEM–BSE imagery of thin sections and separated grains reveals that most molybdenite grains are composed of core and rim plates that are approximately perpendicular. Rim material invaded cores, forming irregular contacts, probably reflecting dissolution/reprecipitation. EPMA and LA-ICP-MS analyses show that cores and rims have different trace element concentrations (for example, cores are relatively enriched in W). On the basis of inclusions of zircon with metamorphic overgrowths, we conclude that molybdenite cores and rims formed after high-grade regional metamorphism. The discovery of cores and rims in individual molybdenite grains is analogous to multi-component U-Pb geochronometers such as zircon, monazite, and titanite; thus, molybdenite should be carefully examined before dating to ensure that the requirement of age homogeneity is fulfilled.

Experimental simulation of the alkali-carbonate metasomatism

NASA Astrophysics Data System (ADS)

Gorbachev, Nikolay; Kostyuk, Anastasia

2010-05-01

Close association of alkaline and ultrabasic rocks, carbonatites, apatitic and sulfidic mineralization, features of structure testify about mantle a source and the important role alcalic-carbonaceous fluids in genesis of these rocks. Formation alkaline silicate, carbonaceous and sulfidic melts, phase relationship, behaviour of the ti-tan, phosphorus, sulphur and zircon has been experimentally studied at pressure 3.9 GPa, temperature 1250°С in system peridotit-basalt (eclogite)-alcalic-carbonaceous fluid with additives in quality acces-sory minerals, apatite, nickel-containing pyrrhotite, ilmenite, zircon. Experiments were carried out using of apparatus high pressure (piston cilinder and anvil with hole) by a quenching technique. It was used two ampoules (platinum and peridotite, content basalt powder) method. Duration of experiments was 6-8 hours. Products of experiments were studied on electronic scanning microscope Tescan VEGA TS 5130MM with YAG detector of secondary and reflected elec-tron and energy-dispersive the x-ray microanalyzer with semi-conductor Si (Li) detector INCA Energy 350. The morphology, structure and relationship of glass, inclusions of carbonatic and sulfidic globules specify in existence in the conditions of experiment immiscibility silicate, carbonate and sulfidic melts. The composition of silicate melt answered phonolite, carbonaceous melts it is essential calciferous composition with an impurity of alkaline metals and silicate components. Solubility of zircon in silicate melts reached 0.8 wt.% ZrO2, in co-existing carbonaceous melt - 1.5 wt.%. Concentration TiO2 and Р2О5 in silicate melt reached 2 wt.%, in carbonaceous melt - 1.7 wt.% TiO2 and up to 14 wt.% Р2О5. Concentration of sulphur in these melts did not exceed 0.2 мас. %. From minerals of liqudus the main concentrators of the titan and phosphorus were the X-phase and phlogopite - up to 8 wt.% TiO2 and up to 3 wt.% Р2О5 in the X-phase, up to 6 wt. % TiO2 and to 2.5 wt. % Р2О5 in phlogopite. Absence ilmenite and apatite in experimental samples under the studied conditions is obviously caused by their high solubility in co-existing phases. The composition of X-phase is similar to composition of Cpx, but X-phase enrich in TiO2 and de-plete in SiO2 . The partition coefficient of oxides some elements between silicate and carbonaceous melts Dka/si increasing from SiO2 (D<1) to CaO (D>10). Reduction of solubility of apatite in alkaline silicate melt at pressure decline promotes silicate-phosphate stratification and formation of apatite mineralization at introduction of mantle magmas into the earth crust. Supported by grant RFBR № 09-05-01131, ONZ th. 2

Study on Resistive Switching Property of Ti Doped Novel NiO Thin Films

NASA Astrophysics Data System (ADS)

Li, Y.; Zhao, G. Y.; Kou, Z. B.; Liu, J. C.; Zhu, R.

2018-01-01

Ti doped nickel oxide thin films have been fabricated by sol-gel dip-coating process using nickel acetate and tetrabutyl titanate as source materials. The effect of the amount of Ti dopant on the surface roughness, optical, chemical state and electrical properties of NiO: Ti thin films was observed by atomic force microscopy (AFM), Uv-vis spectroscopy, X-ray photoelectron spectroscopy(XPS) and I-V measurement, respectively. Results show that the Ti doping is an effective ways to improve the resistive switching behaviors and it is a convenient way to understand the mechanism of the resistive switching behaviors.

Surface modification of thin film composite membrane by nanoporous titanate nanoparticles for improving combined organic and inorganic antifouling properties.

PubMed

Emadzadeh, D; Ghanbari, M; Lau, W J; Rahbari-Sisakht, M; Rana, D; Matsuura, T; Kruczek, B; Ismail, A F

2017-06-01

In this study, nanoporous titanate (NT) nanoparticle synthesized by the solvothermal method was used to modify polyamide layer of thin film composite membranes with the aim of improving membrane resistances against organic and inorganic fouling. Thin film nanocomposite membranes (NMs) were synthesized by adding mNTs (modified nanoparticles) into polyamide selective layer followed by characterization using different analytical instruments. The results of XPS and XRD confirmed the presence of mNTs in the polyamide layer of NMs, while FESEM, AFM, zeta potential and contact angle measurement further supported the changes in physical and chemical properties of the membrane surface upon mNTs incorporation. Results of fouling showed that NM1 (the membrane incorporated with 0.01w/v% mNTs) always demonstrated lower degree of flux decline compared to the control membrane when membranes were tested with organic, inorganic and multicomponent synthesized water, brackish water or seawater. Besides showing greater antifouling resistance, the NM also displayed significantly higher water flux compared to the control M membrane. The findings of this work confirmed the positive impact of mNTs in improving the properties of NM with respect to fouling mitigation and flux improvement. Copyright © 2017. Published by Elsevier B.V.

Active x-ray optics for high resolution space telescopes

NASA Astrophysics Data System (ADS)

Doel, Peter; Atkins, Carolyn; Brooks, D.; Feldman, Charlotte; Willingale, Richard; Button, Tim; Rodriguez Sanmartin, Daniel; Meggs, Carl; James, Ady; Willis, Graham; Smith, Andy

2017-11-01

The Smart X-ray Optics (SXO) Basic Technology project started in April 2006 and will end in October 2010. The aim is to develop new technologies in the field of X-ray focusing, in particular the application of active and adaptive optics. While very major advances have been made in active/adaptive astronomical optics for visible light, little was previously achieved for X-ray optics where the technological challenges differ because of the much shorter wavelengths involved. The field of X-ray astronomy has been characterized by the development and launch of ever larger observatories with the culmination in the European Space Agency's XMM-Newton and NASA's Chandra missions which are currently operational. XMM-Newton uses a multi-nested structure to provide modest angular resolution ( 10 arcsec) but large effective area, while Chandra sacrifices effective area to achieve the optical stability necessary to provide sub-arc second resolution. Currently the European Space Agency (ESA) is engaged in studies of the next generation of X-ray space observatories, with the aim of producing telescopes with increased sensitivity and resolution. To achieve these aims several telescopes have been proposed, for example ESA and NASA's combined International X-ray Observatory (IXO), aimed at spectroscopy, and NASA's Generation-X. In the field of X-ray astronomy sub 0.2 arcsecond resolution with high efficiency would be very exciting. Such resolution is unlikely to be achieved by anything other than an active system. The benefits of a such a high resolution would be important for a range of astrophysics subjects, for example the potential angular resolution offered by active X-ray optics could provide unprecedented structural imaging detail of the Solar Wind bowshock interaction of comets, planets and similar objects and auroral phenomena throughout the Solar system using an observing platform in low Earth orbit. A major aim of the SXO project was to investigate the production of thin actively controlled grazing incident optics for the next generation of X-ray space telescopes. Currently telescope systems are limited in the resolution and sensitivity by the optical quality of the thin shell optics used. As part of its research programme an actively controlled prototype X-ray thin shell telescope optic of dimensions 30x10cm has been developed to bench test the technology. The design is based on thin nickel shells bonded to shaped piezo-electric unimorph actuators made from lead zirconate titanate (PZT).

Efficiency of thermoelectric conversion in ferroelectric film capacitive structures

NASA Astrophysics Data System (ADS)

Volpyas, V. A.; Kozyrev, A. B.; Soldatenkov, O. I.; Tepina, E. R.

2012-06-01

Thermal heating/cooling conditions for metal-insulator-metal structures based on barium strontium titanate ferroelectric films are studied by numerical methods with the aim of their application in capacitive thermoelectric converters. A correlation between the thermal and capacitive properties of thin-film ferroelectric capacitors is considered. The time of the temperature response and the rate of variation of the capacitive properties of the metal-insulator-metal structures are determined by analyzing the dynamics of thermal processes. Thermophysical calculations are carried out that take into consideration the real electrical properties of barium strontium titanate ferroelectric films and allow estimation of thermal modulation parameters and the efficiency of capacitive thermoelectric converters on their basis.

U-Pb Detrital Zircon Geochronologic Constraints on Depositional Age and Sediment Source Terrains of the Late Paleozoic Tepuel-Genoa Basin

NASA Astrophysics Data System (ADS)

Griffis, N. P.; Montanez, I. P.; Isbell, J.; Gulbranson, E. L.; Wimpenny, J.; Yin, Q. Z.; Cúneo, N. R.; Pagani, M. A.; Taboada, A. C.

2014-12-01

The late Paleozoic Ice Age (LPIA) is the longest-lived icehouse of the Phanerozoic and the only time a metazoan dominated and vegetated world transitioned from an icehouse climate into a greenhouse. Despite several decades of research, the timing, extent of glaciation and the location of ice centers remain unresolved, which prohibits reconstruction of ice volume. The Permo-Carboniferous sediments in the Tepuel-Genoa Basin, Patagonia contains a near complete record of sedimentation from the lower Carboniferous through lower Permian. Outsized clasts, thin pebble-rich diamictites and slumps represent the last of the late Paleozoic glacially influenced deep-water marine sediments in the Mojón de Hierro Fm. and the Paleozoic of Patagonia. U-Pb analysis of detrital zircons separated from slope sediments reveal groupings (20 myr bins, n≥5 zircons) with peak depositional ages of 420, 540 to 660 and 1040 Ma. Zircon age populations recovered from the Mojón de Hierro Fm. compare well with bedrock ages of the Deseado Massif of SE Patagonia, suggesting this may be a potential source of sediments. The maximum depositional age of the sediments is 306.05 ± 3.7 Ma (2σ) as determined by the median age of the two youngest concordant zircons that overlap in error. The youngest zircon from the analysis yields a 238U/206Pb age of 301.3 ± 4.5 Ma (2σ; MSWD = 2.3). Younger zircons from the analysis compare well with the age of granite bedrock exposed along the basin margin to the E-NE suggesting they may reflect a more proximal source. These data, which indicate a maximum age of late Carboniferous for the Mojón de Hierro Fm, provide the first geochemical constraints for the timing of final deposition of glaciomarine sediments in the Tepuel-Genoa Basin, and contributes to the biostratigraphic correlation of the late Paleozoic succession in Patagonia with other key LPIA basins that has thus far been hindered by faunal provincialism.

Anatase TiO2 ultrathin nanobelts derived from room-temperature-synthesized titanates for fast and safe lithium storage

PubMed Central

Wen, Wei; Wu, Jin-ming; Jiang, Yin-zhu; Yu, Sheng-lan; Bai, Jun-qiang; Cao, Min-hua; Cui, Jie

2015-01-01

Lithium-ion batteries (LIBs) are promising energy storage devices for portable electronics, electric vehicles, and power-grid applications. It is highly desirable yet challenging to develop a simple and scalable method for constructions of sustainable materials for fast and safe LIBs. Herein, we exploit a novel and scalable route to synthesize ultrathin nanobelts of anatase TiO2, which is resource abundant and is eligible for safe anodes in LIBs. The achieved ultrathin nanobelts demonstrate outstanding performances for lithium storage because of the unique nanoarchitecture and appropriate composition. Unlike conventional alkali-hydrothermal approaches to hydrogen titanates, the present room temperature alkaline-free wet chemistry strategy guarantees the ultrathin thickness for the resultant titanate nanobelts. The anatase TiO2 ultrathin nanobelts were achieved simply by a subsequent calcination in air. The synthesis route is convenient for metal decoration and also for fabricating thin films of one/three dimensional arrays on various substrates at low temperatures, in absence of any seed layers. PMID:26133276

Two-dimensional electron gas in tricolor oxide interfaces

NASA Astrophysics Data System (ADS)

Cao, Yanwei; Kareev, Michael; Liu, Xiaoran; Middey, Srimanta; Meyers, Derek; Tchakhalian, Jak

2014-03-01

Understanding and manipulating spin of electrons in nanometer scale is the main challenge of current spintronics, recent emergent two-dimensional electron gas in oxide interface provides a good platform to investigate the spin behavior by covering an insulating magnetic oxide layer. In this work, take titanates as an example, ultra-thin tricolor (tri-compound) titanate superlattices ([LaTiO3/SrTiO3/YTiO3]) were grown in a layer-by-layer way by pulsed laser deposition. High sample quality and their electronic structures were characterized by the combination of in-situ photoelectron and ex-situ structure and surface morphology probes. Temperature-dependent sheet resistance indicates the presence of metallic interfaces in both [LaTiO3 /SrTiO3 ] and all the tricolor structures, whereas a [YTiO3 /SrTiO3] bi-layer shows insulating behavior. The tricolor titanate superlattices provide an opportunity to induce tunable spin-polarization into the two-dimensional electron gas (2DEG) with Mott carriers.

Metallic conductance at the interface of tri-color titanate superlattices

NASA Astrophysics Data System (ADS)

Kareev, M.; Cao, Yanwei; Liu, Xiaoran; Middey, S.; Meyers, D.; Chakhalian, J.

2013-12-01

Ultra-thin tri-color (tri-layer) titanate superlattices ([3 u.c. LaTiO3/2 u.c. SrTiO3/3 u.c. YTiO3], u.c. = unit cells) were grown in a layer-by-layer way on single crystal TbScO3 (110) substrates by pulsed laser deposition. High sample quality and electronic structure were characterized by the combination of in-situ photoelectron and ex-situ structure and surface morphology probes. Temperature-dependent sheet resistance indicates the presence of metallic interfaces in both [3 u.c. LaTiO3/2 u.c. SrTiO3] bi-layers and all the tri-color structures, whereas a [3 u.c. YTiO3/2 u.c. SrTiO3] bi-layer shows insulating behavior. Considering that in the bulk YTiO3 is ferromagnetic below 30 K, the tri-color titanate superlattices provide an opportunity to induce tunable spin-polarization into the two-dimensional electron gas with Mott carriers.

Jurassic to Miocene magmatism and metamorphism in the Mogok metamorphic belt and the India-Eurasia collision in Myanmar

NASA Astrophysics Data System (ADS)

Barley, M. E.; Pickard, A. L.; Zaw, Khin; Rak, P.; Doyle, M. G.

2003-06-01

Situated south of the eastern Himalayan syntaxis at the western margin of the Shan-Thai terrane the high-grade Mogok metamorphic belt (MMB) in Myanmar occupies a key position in the tectonic evolution of Southeast Asia. The first sensitive high-resolution ion microprobe U-Pb in zircon geochronology for the MMB shows that strongly deformed granitic orthogneisses near Mandalay contain Jurassic (˜170 Ma) zircons that have partly recrystallized during ˜43 Ma high-grade metamorphism. A hornblende syenite from Mandalay Hill also contains Jurassic zircons with evidence of Eocene metamorphic recrystallization rimmed by thin zones of 30.9 ± 0.7 Ma magmatic zircon. The relative abundance of Jurassic zircons in these rocks is consistent with suggestions that southern Eurasia had an Andean-type margin at that time. Mid-Cretaceous to earliest Eocene (120 to 50 Ma) I-type granitoids in the MMB, Myeik Archipelago, and Western Myanmar confirm that prior to the collision of India, an up to 200 km wide magmatic belt extended along the Eurasian margin from Pakistan to Sumatra. Metamorphic overgrowths to zircons in the orthogneiss near Mandalay date a period of Eocene (˜43 Ma) high-grade metamorphism possibly during crustal thickening related to the initial collision between India and Eurasia (at 65 to 55 Ma). This was followed by emplacement of syntectonic hornblende syenites and leucogranites between 35 and 23 Ma. Similar syntectonic syenites and leucogranites intruded the Ailao Shan-Red River shear belt in southern China and Vietnam during the Eocene-Oligocene to Miocene, and the Wang Chao and Three Pagodas faults in northern Thailand (that most likely link with the MMB) were also active at this time. The complex history of Eocene to early Miocene metamorphism, deformation, and magmatism in the MMB provides evidence that it may have played a key role in the network of deformation zones that accommodated strain during the northwards movement of India and resulting extrusion or rotation of Indochina.

Detrital Zircon Geochronology of Sedimentary Rocks of the 3.6 - 3.2 Ga Barberton Greenstone Belt: No Evidence for Older Continental Crust

NASA Astrophysics Data System (ADS)

Drabon, N.; Lowe, D. R.; Byerly, G. R.; Harrington, J.

2017-12-01

The crustal setting of early Archean greenstone belts and whether they formed on or associated with blocks of older continental crust or in more oceanic settings remains a major issue in Archean geology. We report detrital zircon U-Pb age data from sandstones of the 3.26-3.20 Ga Fig Tree and Moodies Groups and from 3.47 to 3.23 Ga meteorite impact-related deposits in the 3.55-3.20 Ga Barberton greenstone belt (BGB), South Africa. The provenance signatures of these sediments are characterized by zircon age peaks at 3.54, 3.46, 3.40, 3.30, and 3.25 Ga. These clusters are coincident either with the ages of major episodes of felsic to intermediate igneous activity within and around the belt or with the ages of thin felsic tuffs reflecting distant volcanic activity. Only 15 of the reported 3410 grains (<0.5%) pre-date the age of the oldest rocks in the BGB. The extreme rarity of zircons older than the felsic components of the BGB itself, even after widespread deformation, uplift, and deep erosion of the BGB, implies that an older continental substrate is unlikely to have existed beneath or adjacent to the BGB. Ten of the 15 pre -BGB zircons were recovered from a single meteorite impact-related layer and may have been derived from far beyond the BGB by impact-related processes. The remaining old zircons could represent felsic rocks in older, unexposed parts of the BGB sequence, but are too few to provide evidence for a continental source. This finding offers further evidence that the large, thick, high-standing, highly evolved blocks of continental crust with an andesitic bulk composition that characterize the Earth during younger geologic times were scarce in the early Archean.

Control of liquid crystal molecular orientation using ultrasound vibration

DOE Office of Scientific and Technical Information (OSTI.GOV)

Taniguchi, Satoki; Wave Electronics Research Center, Doshisha University, 1-3 Tataramiyakodani, Kyotanabe, Kyoto 610-0321; Koyama, Daisuke

2016-03-07

We propose a technique to control the orientation of nematic liquid crystals using ultrasound and investigate the optical characteristics of the oriented samples. An ultrasonic liquid crystal cell with a thickness of 5–25 μm and two ultrasonic lead zirconate titanate transducers was fabricated. By exciting the ultrasonic transducers, the flexural vibration modes were generated on the cell. An acoustic radiation force to the liquid crystal layer was generated, changing the molecular orientation and thus the light transmission. By modulating the ultrasonic driving frequency and voltage, the spatial distribution of the molecular orientation of the liquid crystals could be controlled. The distributionmore » of the transmitted light intensity depends on the thickness of the liquid crystal layer because the acoustic field in the liquid crystal layer is changed by the orientational film.« less

Fatigue in artificially layered Pb(Zr,Ti)O3 ferroelectric films

NASA Astrophysics Data System (ADS)

Jiang, A. Q.; Scott, J. F.; Dawber, M.; Wang, C.

2002-12-01

We have performed fatigue tests on lead zirconate titanate (PZT) multilayers having stacks of Pb(Zr0.8Ti0.2)O3/Pb(Zr0.2Ti0.8)O3 with repeated distances of 12 formula groups. The results are compared with single-layer n-type (0.5 at. % Ta-doped) PZT films. We conclude that fatigue is dominated by space-charge layers in each case, but that in the multilayer such space charge accumulates at the layer interfaces, rather than at the electrode-dielectric interface. The model, which includes both drift and diffusion, is quantitative and yields a rate-limiting mobility of 6.9±0.9×10-12 cm2/V s, in excellent agreement with the oxygen vacancy mobility for perovskite oxides obtained from Zafar et al.

A Micro Ultrasonic Scalpel with Modified Stepped Horn

NASA Astrophysics Data System (ADS)

Kurosawa, Minoru; Umehara, Yuji

A transducer for a micro ultrasonic scalpel has been fabricated. The micro ultrasonic scalpel can be used with an endoscope for a non-abdominal operation or micro surgery, for example, through a microscope. The ultrasonic transducer was 9.8 mm long and 2.7 mm wide and has stepped horn to amplify vibration velocity; tip of the horn is 0.6 mm wide. The scalpel operated at the resonance frequency in longitudinal mode of 278 kHz. The piezoelectric material was lead zirconate titanate (PZT) that was deposited by the hydrothermal method. The vibration velocity at the tip of the horn in longitudinal direction was 4.0 m/s with 40Vp-p driving voltage in both side electrodes. To demonstrate a beneficial effect of the scalpel, a cutting test that the transducer was stuck into pork fat was carried out.

Invariants of electromechanical coupling coefficients in piezoceramics.

PubMed

Mezheritsky, Alex V

2003-12-01

The relationships between coefficients of electromechanical coupling (CEMC) of various types of piezoceramic resonator (PR) vibrations are considered. Being constant for a given piezoceramic state, the range of variation of piezoceramics dielectric permittivity from a mechanically "free" condition at relatively low frequencies up to an "overall clamped" condition at high frequencies is determined by a consecutive "clamping", caused by a complex of CEMCs of various particular vibrational modes peculiar to the resonator. As the difference between "free" and "overall clamped" permittivities is always determined by the maximal piezomaterial ki3 coupling coefficient, the difference does not depend on the path that was gone through the low-high frequency range, which includes all the vibrational modes possible for a particular PR. The influence of the piezoelectric and elastic anisotropy of lead-zirconate-titanate (PZT) piezoceramic materials on relative CEMC variations was experimentally investigated.

Piezoelectric characterization of ejecta from shocked tin surfaces

NASA Astrophysics Data System (ADS)

Vogan, W. S.; Anderson, W. W.; Grover, M.; Hammerberg, J. E.; King, N. S. P.; Lamoreaux, S. K.; Macrum, G.; Morley, K. B.; Rigg, P. A.; Stevens, G. D.; Turley, W. D.; Veeser, L. R.; Buttler, W. T.

2005-12-01

Using piezoelectric diagnostics, we have measured densities and velocities of ejected particulate as well as "free-surface velocities" of bulk tin targets shock loaded with high explosive. The targets had finely grooved, machined finishes ranging from 10 to 250μin. Two types of piezoelectric sensor ("piezopins"), lithium niobate and lead zirconate titanate, were compared for durability and repeatability; in addition, some piezopins were "shielded" with foam and metal foil in order to mitigate premature failure of the pins in high ejecta regimes. These experiments address questions about ejecta production at a given shock pressure as a function of surface finish; piezopin results are compared with those from complementary diagnostics such as x-ray radiography and time-resolved optical transmission techniques. The mass ejection shows a marked dependence on groove characteristics and cannot be described by a groove defect theory alone.

Transient Characteristics of a Fluidic Device for Circulatory Jet Flow.

PubMed

Phan, Hoa Thanh; Dinh, Thien Xuan; Bui, Phong Nhu; Dau, Van Thanh

2018-03-13

In this paper, we report on the design, simulation, and experimental analysis of a miniaturized device that can generate multiple circulated jet flows. The device is actuated by a lead zirconate titanate (PZT) diaphragm. The flows in the device were studied using three-dimensional transient numerical simulation with the programmable open source OpenFOAM and was comparable to the experimental result. Each flow is verified by two hotwires mounted at two positions inside each consisting chamber. The experiment confirmed that the flow was successfully created, and it demonstrated good agreement with the simulation. In addition, a prospective application of the device as an angular rate sensor is also demonstrated. The device is robust, is minimal in size, and can contribute to the development of multi-axis fluidic inertial sensors, fluidic amplifiers, gas mixing, coupling, and analysis.

Transient Characteristics of a Fluidic Device for Circulatory Jet Flow

PubMed Central

Phan, Hoa Thanh; Dinh, Thien Xuan; Bui, Phong Nhu

2018-01-01

In this paper, we report on the design, simulation, and experimental analysis of a miniaturized device that can generate multiple circulated jet flows. The device is actuated by a lead zirconate titanate (PZT) diaphragm. The flows in the device were studied using three-dimensional transient numerical simulation with the programmable open source OpenFOAM and was comparable to the experimental result. Each flow is verified by two hotwires mounted at two positions inside each consisting chamber. The experiment confirmed that the flow was successfully created, and it demonstrated good agreement with the simulation. In addition, a prospective application of the device as an angular rate sensor is also demonstrated. The device is robust, is minimal in size, and can contribute to the development of multi-axis fluidic inertial sensors, fluidic amplifiers, gas mixing, coupling, and analysis. PMID:29534014

Effect of electrical and mechanical poling history on domain orientation and piezoelectric properties of soft and hard PZT ceramics

NASA Astrophysics Data System (ADS)

Marsilius, Mie; Granzow, Torsten; Jones, Jacob L.

2011-02-01

The superior piezoelectric properties of all polycrystalline ferroelectrics are based on the extent of non-180° domain wall motion under electrical and mechanical poling loads. To distinguish between 180° and non-180° domain wall motion in a soft-doped and a hard-doped lead zirconate titanate (PZT) ceramic, domain texture measurements were performed using x-ray and neutron diffraction after different loading procedures. Comparing the results to measurements of the remanent strain and piezoelectric coefficient allowed the differentiation between different microstructural contributions to the macroscopic parameters. Both types of ceramic showed similar behavior under electric field, but the hard-doped material was more susceptible to mechanical load. A considerable fraction of the piezoelectric coefficient originated from poling by the preferred orientation of 180° domains.

Lamb wave-based damage quantification and probability of detection modeling for fatigue life assessment of riveted lap joint

NASA Astrophysics Data System (ADS)

He, Jingjing; Wang, Dengjiang; Zhang, Weifang

2015-03-01

This study presents an experimental and modeling study for damage detection and quantification in riveted lap joints. Embedded lead zirconate titanate piezoelectric (PZT) ceramic wafer-type sensors are employed to perform in-situ non-destructive testing during fatigue cyclical loading. A multi-feature integration method is developed to quantify the crack size using signal features of correlation coefficient, amplitude change, and phase change. In addition, probability of detection (POD) model is constructed to quantify the reliability of the developed sizing method. Using the developed crack size quantification method and the resulting POD curve, probabilistic fatigue life prediction can be performed to provide comprehensive information for decision-making. The effectiveness of the overall methodology is demonstrated and validated using several aircraft lap joint specimens from different manufactures and under different loading conditions.

Large Displacement in Relaxor Ferroelectric Terpolymer Blend Derived Actuators Using Al Electrode for Braille Displays

PubMed Central

Lu, S. G.; Chen, X.; Levard, T.; Diglio, P. J.; Gorny, L. J.; Rahn, C. D.; Zhang, Q. M.

2015-01-01

Poly(vinylidene fluoride) (PVDF) based polymers are attractive for applications for artificial muscles, high energy density storage devices etc. Recently these polymers have been found great potential for being used as actuators for refreshable full-page Braille displays for visually impaired people in terms of light weight, miniaturized size, and larger displacement, compared with currently used lead zirconate titanate ceramic actuators. The applied voltages of published polymer actuators, however, cannot be reduced to meet the requirements of using city power. Here, we report the polymer actuator generating quite large displacement and blocking force at a voltage close to the city power. Our embodiments also show good self-healing performance and disuse of lead-containing material, which makes the Braille device safer, more reliable and more environment-friendly. PMID:26079628

Candle Soot-Driven Performance Enhancement in Pyroelectric Energy Conversion

NASA Astrophysics Data System (ADS)

Azad, Puneet; Singh, V. P.; Vaish, Rahul

2018-05-01

We observed substantial enhancement in pyroelectric output with the help of candle soot coating on the surface of lead zirconate titanate (PZT). Candle soot of varying thicknesses was coated by directly exposing pyroelectric material to the candle flame. The open-circuit pyroelectric voltage and closed-circuit pyroelectric current were recorded while applying infrared heating across the uncoated and candle soot-coated samples for different heating and cooling cycles. In comparison to the uncoated sample, the maximum open-circuit voltage improves seven times for the candle soot-coated sample and electric current increases by eight times across a resistance of 10Å. Moreover, the harvested energy is enhanced by 50 times for candle soot-coated sample. Results indicate that candle soot coating is an effective and economic method to improve infrared sensing performance of pyroelectric materials.

The role of detrital zircons in Hadean crustal research

NASA Astrophysics Data System (ADS)

Nebel, Oliver; Rapp, Robert P.; Yaxley, Gregory M.

2014-03-01

Meso-Archean sedimentary sequences at Mt. Narryer and the Jack Hills of the Narryer Terrane in Western Australia's Yilgarn Craton contain detrital zircon grains with ages as old as 4.37 Ga, the oldest preserved terrestrial matter. These grains are rare remnants of Hadean (4.5-4.0 Ga) terrestrial crust and their survival stems from the crystallographic properties of zircon during crustal reworking: they are resistant to physical and chemical weathering. Zircons are further suitable for single grain, precise age determinations making them a unique archive of the crustal past. Only a small proportion of all detrital zircons from the Narryer Terrane show Hadean age spectra and younger overgrowth rims on all 'Hadean' grains indicate multiple recycling events. Numerous studies that applied a spectacular range of analytical tools and proxies have been undertaken to decipher the geochemical nature of these zircons' host rocks, in order to place constraints on Hadean geodynamics and the processes responsible for creating the earliest terrestrial crust. Their elemental and isotope budget and mineral inclusions have helped to develop an emerging picture of a water-rich, evolved Hadean crust. However, subsequent studies have challenged this view and it seems that each piece of new evidence indicative of an early, evolved continental crust has non-unique interpretations also permissive of mafic to ultra-mafic crust. In this review we examine these disparate interpretations and their possible implications and conclude that at least parts of the earliest terrestrial crust were hydrated. However, to date there is no conclusive evidence for preserved granitic, continental crust. The protoliths of the Hadean detrital zircons were likely acidic in nature, yet the composition of the greater terrane from which these melts were derived was probably mafic. It remains unclear if the zircons formed in a geodynamic environment that includes Hadean subduction. We suspect that the Hadean crust was an initially homogeneous, thin, mafic layer. It was spiked with minor, low-degree, anatectic melts of granitoid composition formed from material that formerly resided at the surface and was subsequently buried. The process responsible for this was likely sag-subduction triggered by repeated volcanic resurfacing, possibly fed by early mantle plumes. Regional scale granitoid plutonism of the tonalite-trondhjemite-granodiorite suite (TTG) predominates granitoid-generating processes in the Eo-Archean, along with the first appearance of low-Ca (s-type) granites at around 3.9 Ga, evidenced by the first occurrence of detrital monazite in the Narryer Terrane. This coincides with the first addition of juvenile crust as documented by the global detrital zircon record and temperature signatures of the late heavy bombardment in Narryer Terrane zircons. This age probably marks the onset of Archean-style tectonics, likely associated with subduction activity, which lasted until ~ 3 Ga, when modern style plate tectonics emerged.

Carboniferous - Early Permian magmatic evolution of the Bogda Range (Xinjiang, NW China): Implications for the Late Paleozoic accretionary tectonics of the SW Central Asian Orogenic Belt

NASA Astrophysics Data System (ADS)

Wali, Guzalnur; Wang, Bo; Cluzel, Dominique; Zhong, Linglin

2018-03-01

The Late Paleozoic magmatic evolution of the Bogda Range (Chinese North Tianshan) is important for understanding the accretionary history of the Central Asian Orogenic Belt. We investigated the Carboniferous and Lower Permian volcanic and sedimentary sequences of the Daheyan section, southern Bogda Range, and present new zircon U-Pb ages and whole-rock geochemical data for the volcanic rocks. One Carboniferous rhyolite is dated at 298 ± 8 Ma; a Permian basalt yielded many Proterozoic zircon xenocrysts, and its maximum age (∼297 Ma) is constrained by the detrital zircon ages of the sandstone that stratigraphically underlies it. These volcanic rocks belong to calc-alkaline series. We further synthesize previous geochronological, geochemical and isotopic data of magmatic and sedimentary rocks in the Bogda Range. The available data indicate that the magmatism occurred continuously from 350 Ma to 280 Ma. A comprehensive analysis allows us to propose that: (1) the Carboniferous to Early Permian magmatic rocks of the Bogda Range generally show consistent arc-type features; (2) increasing mantle input through time suggests intra-arc extension in a supra-subduction zone; (3) the localized occurrence of Early Permian alkaline pillow basalts and deep water sediments close to the major shear zone advocate a transtensional crustal thinning during the transition from Carboniferous convergence to Early Permian transcurrent tectonics; (4) occurrence of a large number of Proterozoic zircon xenocrysts in the Late Paleozoic magmatic rocks, and Proterozoic detrital zircons in the coeval clastic sediments suggest a continental or transitional basement of the Bogda Arc; (5) subduction in the Bogda area terminated prior to the deposition of Middle Permian terrestrial sediments.

The timing of tertiary metamorphism and deformation in the Albion-Raft River-Grouse Creek metamorphic core complex, Utah and Idaho

USGS Publications Warehouse

Strickland, A.; Miller, E.L.; Wooden, J.L.

2011-01-01

The Albion-Raft River-Grouse Creek metamorphic core complex of southern Idaho and northern Utah exposes 2.56-Ga orthogneisses and Neoproterozoic metasedimentary rocks that were intruded by 32-25-Ma granitic plutons. Pluton emplacement was contemporaneous with peak metamorphism, ductile thinning of the country rocks, and top-to-thewest, normal-sense shear along the Middle Mountain shear zone. Monazite and zircon from an attenuated stratigraphic section in the Middle Mountain were dated with U-Pb, using a SHRIMP-RG (reverse geometry) ion microprobe. Zircons from the deformed Archean gneiss preserve a crystallization age of 2532 ?? 33 Ma, while monazites range from 32.6 ?? 0.6 to 27.1 ?? 0.6 Ma. In the schist of the Upper Narrows, detrital zircons lack metamorphic overgrowths, and monazites produced discordant U-Pb ages that range from 52.8 ?? 0.6 to 37.5 ?? 0.3 Ma. From the structurally and stratigraphically highest unit sampled, the schist of Stevens Spring, narrow metamorphic rims on detrital zircons yield ages from 140-110 Ma, and monazite grains contained cores that yield an age of 141 ??2 Ma, whereas rims and some whole grains ranged from 35.5 ?? 0.5 to 30.0 ?? 0.4 Ma. A boudinaged pegmatite exposed in Basin Creek is deformed by the Middle Mountains shear zone and yields a monazite age of 27.6 ?? 0.2 Ma. We interpret these data to indicate two periods of monazite and metamorphic zircon growth: a poorly preserved Early Cretaceous period (???140 Ma) that is strongly overprinted by Oligocene metamorphism (???32-27 Ma) related to regional plutonism and extension. ?? 2011 by The University of Chicago.

Nd and Ru co-doped bismuth titanate polycrystalline thin films with improved ferroelectric properties

NASA Astrophysics Data System (ADS)

Sahoo, Kishor Kumar; Singh Rajput, Shailendra; Gupta, Rajeev; Roy, Amritendu; Garg, Ashish

2018-02-01

We report the ferroelectric properties of pulsed laser deposited thin films of Nd and Ru co-doped bismuth titanate (Bi4-x Nd x Ti3-y Ru y O12). Structural analysis of the as-grown films, using x-ray diffraction, showed a single-phase formation with a polycrystalline structure. In comparison to un-doped and Nd-doped films, ferroelectric measurements on co-doped films demonstrated improved properties with remnant polarization (P r) ~ 12.5 µC cm-2 and an enhanced electrical fatigue life for Bi3.25Nd0.75Ti2.8Ru0.20O12 films. The enhancement in remanent polarization is attributed to microscopic changes, such as local structural distortion and the modification of the dynamical/effective charges on constituent ions due to chemical strain upon simultaneous Bi- (A) and Ti- (B) site doping with Nd and Ru, which has a far stronger effect than only A-site doping with Nd. Piezoresponse force microscopy further confirmed the polar structure and domain switching at nanoscale. The films exhibit small yet finite magnetization at 10 K resulting from strain.

Electrical characterization of doped strontium titanate thin films for semiconductor memories

NASA Astrophysics Data System (ADS)

Han, Jeong Hee

2002-08-01

Doped strontium titanate (ST) thin films were investigated for high-density memory applications. ST has become a promising candidate to replace conventional silicon oxide due to its high inherent dielectric constant, superior leakage characteristics, and good chemical stability. However, oxygen vacancies and the problems that arise as a result are one of the main drawbacks against this material. Resistance degradation is a serious reliability issue in perovskite titanate films and may be a result of oxygen vacancies. In this dissertation, an attempt to reduce the resistance degradation was made by doping the ST films with both niobium and lanthanum. Niobium is a B-site donor in the perovskite, whereas lanthanum is an A-site donor. Both have an extra valence charge than the atom which it replaces in the crystal structure. With a higher valence charge, the number of oxygen vacancies is hoped to be reduced and result in better electrical performance. Experimental results showed that the degradation rate is reduced by doping with either niobium or lanthanum. A bi-layer study was also performed to optimize the dielectric with the strengths of both doped and undoped strontium titanate and to distinguish the source of the oxygen vacancies. A study on the conduction mechanisms and dielectric dispersion was also performed. An additional study was made on the effect of iridium as a possible gate electrode for a MOS capacitor. Hafnium oxide was used as the high-permittivity oxide. The results observed showed that the capacitance was higher for iridium electrodes than those for platinum electrodes. However, both electrodes showed unacceptable frequency dispersion which may be caused by crude patterning techniques. A hysteresis review was also done for hafnium and zirconium oxides. It was observed that the hysteresis measured in the high-permittivity oxides are dependent on the accumulation sweep voltage due to the trapping and de-trapping of charge at the dielectric-silicon interface.

Cyclic formation and stabilization of Archean lithosphere by accretionary orogenesis: Constraints from TTG and potassic granitoids, North China Craton

NASA Astrophysics Data System (ADS)

Wang, Wei; Cawood, Peter A.; Liu, Shuwen; Guo, Rongrong; Bai, Xiang; Wang, Kang

2017-09-01

Accretionary orogens are major sites of modern continental growth, yet their role in the development of Archean continental crust remains enigmatic. Diverse granitoid suites from tonalite-trondhjemite-granodiorite (TTG) to potassic granitoids appeared during late Archean, representing a period of major continental formation and stabilization. In this study, whole-rock geochemical and zircon U-Pb and Lu-Hf isotopic data are reported for Neoarchean granitoid gneisses from the Northern Liaoning Terrane, northeastern North China Craton (NCC). Older granitoid gneisses ( 2592-2537 Ma) define three magmatic zones migrating from southeast to northwest, each showing a common magmatic evolution from high-pressure TTGs to medium-/low-pressure TTGs and potassic granitoids. They have depleted zircon ƐHf(t) of +0.5 to +8.7. Younger 2529-2503 Ma potassic granitoids and TTGs occur throughout the terrane, which are marked by variable zircon ƐHf(t) of -4.7 to +8.1, and are coeval with regional high-grade metamorphism. Petrogenetic modeling and changing Sr/Y and (La/Yb)N of the granitoids suggest that the crust experienced episodic thickening and thinning and became progressively evolved through development of potassic granitoids and sedimentary successions. The metavolcanic basement to the granitoids display tholeiitic to calc-alkaline affinities, together with the top-to-the-northwest thrusting and associated volcanogenic massive sulfide-type Cu-Zn deposits, suggesting cyclic crustal formation of Northern Liaoning within an accretionary orogen with a SE-dipping subduction polarity. Cyclic crustal thickening and thinning is related to tectonic switching from advancing to retreating relations between the downgoing and overriding plate. After 2530 Ma, this accretionary system accreted to the ancient continental nucleus of NCC (Anshan-Benxi Terrane), signifying final lithosphere stabilization.

Ferroelectric relaxor behaviour and impedance spectroscopy of Bi2O3-doped barium zirconium titanate ceramics

NASA Astrophysics Data System (ADS)

Mahajan, Sandeep; Thakur, O P; Bhattacharya, D K; Sreenivas, K

2009-03-01

Bi2O3-doped barium zirconate titanate ceramics, Ba1-xBix(Zr0.05Ti0.95)O3, have been prepared by the conventional solid-state reaction method. The ferroelectric relaxor behaviour and dielectric properties have been investigated in detail. By XRD analysis, it is suggested that up to x = 0.04, Bi3+ substitutes A-site ion, and thereafter with higher Bi3+ content, it enters the B-site sub lattice. Substitution of Bi3+ ions induces ferroelectric relaxor behaviour and the degree of relaxation behaviour increases with bismuth concentration. The remanent polarization and strain behaviour show a slight increase with the substitution level. The degree of hysteresis (strain versus electric field) also reduces from 21.4% to 4.6% with bismuth substitution. Impedance measurements were made on the prepared sample over a wide range of temperatures (300-723 K) and frequencies (40 Hz-1 MHz), which show the presence of both bulk and grain boundary effects in the material. The bulk and grain boundary conductivities determined from impedance study indicate the Arrhenius-type thermally activated process. Impedance spectroscopy is shown to be an efficient method capable of detecting the contributions of the resistances of grains and grain boundaries to the complex impedance of a ceramic system, accurately estimating its electrical conductivity as well as its corresponding activation energies and drawing conclusions on its structural properties.

Effect of vanadium content on remanent polarization in bismuth titanate thin films prepared by liquid source misted chemical deposition

NASA Astrophysics Data System (ADS)

Kim, Tai Suk; Kim, Ki Woong; Jeon, Min Ku; Jung, Chang Hwa; Woo, Seong Ihl

2007-01-01

Bi4-x/3Ti3-xVxO12 (BTV) ferroelectric thin films were fabricated by liquid source misted chemical deposition. The substitution of vanadium for titanium site changed the crystalline orientation and surface morphology of the thin film, which in turn influenced the remanent polarization (Pr). 2Pr of BTV thin film increased with increase of vanadium content and reached a maximum value (21.5μC/cm2) at x =0.03, as this corresponded with the largest degree of a-axis orientation. However, at 0.05⩽x⩽0.09, 2Pr reduced with decrease in the degree of a-axis orientation. These results indicate that the Pr of the films is dependent on the degree of a-axis orientation.

Optical and microwave dielectric properties of pulsed laser deposited Na{sub 0.5}Bi{sub 0.5}TiO{sub 3} thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Joseph, Andrews; Goud, J. Pundareekam; Raju, K. C. James

2016-05-23

Optical properties of pulsed laser deposited (PLD) sodium bismuth titanate thin films (NBT), are investigated at wavelengths of 190-2500 nm. Microwave dielectric properties were investigated using the Split Post Dielectric Resonator (SPDR) technique. At 10 GHz, the NBT films have a dielectric constant of 205 and loss tangent of 0.0373 at room temperature. The optical spectra analysis reveals that NBT thin films have an optical band gap E{sub g}=3.55 eV and it has a dielectric constant of 3.37 at 1000 nm with dielectric loss of 0.299. Hence, NBT is a promising candidate for photonic device applications.

Regional geomorphology and history of Titan's Xanadu province

USGS Publications Warehouse

Radebaugh, J.; Lorenz, R.D.; Wall, S.D.; Kirk, R.L.; Wood, C.A.; Lunine, J.I.; Stofan, E.R.; Lopes, R M.C.; Valora, P.; Farr, T.G.; Hayes, A.; Stiles, B.; Mitri, Giuseppe; Zebker, H.; Janssen, M.; Wye, L.; LeGall, A.; Mitchell, K.L.; Paganelli, F.; West, R.D.; Schaller, E.L.; ,

2011-01-01

Titan's enigmatic Xanadu province has been seen in some detail with instruments from the Cassini spacecraft. The region contains some of the most rugged, mountainous terrain on Titan, with relief over 2000 m. Xanadu contains evolved and integrated river channels, impact craters, and dry basins filled with smooth, radar-dark material, perhaps sediments from past lake beds. Arcuate and aligned mountain chains give evidence of compressional tectonism, yet the overall elevation of Xanadu is puzzlingly low compared to surrounding sand seas. Lineations associated with mountain fronts and valley floors give evidence of extension that probably contributed to this regional lowering. Several locations on Xanadu's western and southern margins contain flow-like features that may be cryovolcanic in origin, perhaps ascended from lithospheric faults related to regional downdropping late in its history. Radiometry and scatterometry observations are consistent with a water–ice or water–ammonia–ice composition to its exposed, eroded, fractured bedrock; both microwave and visible to near-infrared (v-nIR) data indicate a thin overcoating of organics, likely derived from the atmosphere. We suggest Xanadu is one of the oldest terrains on Titan and that its origin and evolution have been controlled and shaped by compressional and then extensional tectonism in the icy crust and ongoing erosion by methane rainfall.

Effect of feature size on dielectric nonlinearity of patterned PbZr{sub 0.52}Ti{sub 0.48}O{sub 3} films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, J. I., E-mail: jxy194@psu.edu; Trolier-McKinstry, S.; Polcawich, R. G.

2015-01-07

Lead zirconate titanate, PZT (52/48), thin films with a PbTiO{sub 3} seed layer were patterned into features of different widths, including various sizes of squares and 100 μm, 50 μm, and 10 μm serpentine designs, using argon ion beam milling. Patterns with different surface area/perimeter ratios were used to study the relative importance of damage produced by the patterning. It was found that as the pattern dimensions decreased, the remanent polarization increased, presumably due to the fact that the dipoles near the feature perimeter are not as severely clamped to the substrate. This investigation is in agreement with a model in which clampingmore » produces deep wells, which do not allow some fraction of the spontaneous polarization to switch at high field. The domain wall mobility at modest electric fields was investigated using the Rayleigh law. Both the reversible, ε{sub init}, and irreversible, α, Rayleigh coefficients increased with decreasing serpentine line width for de-aged samples. For measurements made immediately after annealing, ε{sub init} of 500 μm square patterns was 1510 ± 13; with decreasing serpentine line width, ε{sub init} rose from 1520 ± 10 for the 100 μm serpentine to 1568 ± 23 for the 10 μm serpentine. The irreversible parameter, α, for the square patterns was 39.4 ± 3.2 cm/kV and it increased to 44.1 ± 3.2 cm/kV as the lateral dimension is reduced. However, it was found that as the width of the serpentine features decreased, the aging rate rose. These observations are consistent with a model in which sidewall damage produces shallow wells that lower the Rayleigh constants of aged samples at small fields. These shallow wells can be overcome by the large fields used to measure the remanent polarization and the large unipolar electric fields typically used to drive thin film piezoelectric actuators.« less

Measurement of effective piezoelectric coefficients of PZT thin films for energy harvesting application with interdigitated electrodes.

PubMed

Chidambaram, Nachiappan; Mazzalai, Andrea; Muralt, Paul

2012-08-01

Interdigitated electrode (IDE) systems with lead zirconate titanate (PZT) thin films play an increasingly important role for two reasons: first, such a configuration generates higher voltages than parallel plate capacitor-type electrode (PPE) structures, and second, the application of an electric field leads to a compressive stress component in addition to the overall stress state, unlike a PPE structure, which results in tensile stress component. Because ceramics tend to crack at relatively moderate tensile stresses, this means that IDEs have a lower risk of cracking than PPEs. For these reasons, IDE systems are ideal for energy harvesting of vibration energy, and for actuators. Systematic investigations of PZT films with IDE systems have not yet been undertaken. In this work, we present results on the evaluation of the in-plane piezoelectric coefficients with IDE systems. Additionally, we also propose a simple and measurable figure of merit (FOM) to analyze and evaluate the relevant piezoelectric parameter for harvesting efficiency without the need to fabricate the energy harvesting device. Idealized effective coefficients e(IDE) and h(IDE) are derived, showing its composite nature with about one-third contribution of the transverse effect, and about two-thirds contribution of the longitudinal effect in the case of a PZT film deposited on a (100)-oriented silicon wafer with the in-plane electric field along one of the <011> Si directions. Randomly oriented 1-μm-thick PZT 53/47 film deposited by a sol-gel technique, was evaluated and yielded an effective coefficient e(IDE) of 15 C·m(-2). Our FOM is the product between effective e and h coefficient representing twice the electrical energy density stored in the piezoelectric film per unit strain deformation (both for IDE and PPE systems). Assuming homogeneous fields between the fingers, and neglecting the contribution from below the electrode fingers, the FOM for IDE structures with larger electrode gap is derived to be twice as large as for PPE structures, for PZT-5H properties. The experiments yielded an FOM of the IDE structures of 1.25 × 10(10) J/m(3) and 14 mV/μ strain.

Strongly Enhanced Piezoelectric Response in Lead Zirconate Titanate Films with Vertically Aligned Columnar Grains.

PubMed

Nguyen, Minh D; Houwman, Evert P; Dekkers, Matthijn; Rijnders, Guus

2017-03-22

Pb(Zr 0.52 Ti 0.48 )O 3 (PZT) films with (001) orientation were deposited on Pt(111)/Ti/SiO 2 /Si(100) substrates using pulsed laser deposition. Variation of the laser pulse rate during the deposition of the PZT films was found to play a key role in the control of the microstructure and to change strongly the piezoelectric response of the thin film. The film deposited at low pulse rate has a denser columnar microstructure, which improves the transverse piezoelectric coefficient (d 31f ) and ferroelectric remanent polarization (P r ), whereas the less densely packed columnar grains in the film deposited at high pulse rates give rise to a significantly higher longitudinal piezoelectric coefficient (d 33f ) value. The effect of film thickness on the ferroelectric and piezoelectric properties of the PZT films was also investigated. With increasing film thickness, the grain column diameter gradually increases, and also the average P r and d 33f values become larger. The largest piezoelectric coefficient of d 33f = 408 pm V -1 was found for a 4-μm film thickness. From a series of films in the thickness range 0.5-5 μm, the z-position dependence of the piezoelectric coefficient could be deduced. A local maximum value of 600 pm V -1 was deduced in the 3.5-4.5 μm section of the thickest films. The dependence of the film properties on film thickness is attributed to the decreasing effect of the clamping constraint imposed by the substrate and the increasing spatial separation between the grains with increasing film thickness.

Strongly Enhanced Piezoelectric Response in Lead Zirconate Titanate Films with Vertically Aligned Columnar Grains

PubMed Central

2017-01-01

Pb(Zr0.52Ti0.48)O3 (PZT) films with (001) orientation were deposited on Pt(111)/Ti/SiO2/Si(100) substrates using pulsed laser deposition. Variation of the laser pulse rate during the deposition of the PZT films was found to play a key role in the control of the microstructure and to change strongly the piezoelectric response of the thin film. The film deposited at low pulse rate has a denser columnar microstructure, which improves the transverse piezoelectric coefficient (d31f) and ferroelectric remanent polarization (Pr), whereas the less densely packed columnar grains in the film deposited at high pulse rates give rise to a significantly higher longitudinal piezoelectric coefficient (d33f) value. The effect of film thickness on the ferroelectric and piezoelectric properties of the PZT films was also investigated. With increasing film thickness, the grain column diameter gradually increases, and also the average Pr and d33f values become larger. The largest piezoelectric coefficient of d33f = 408 pm V–1 was found for a 4-μm film thickness. From a series of films in the thickness range 0.5–5 μm, the z-position dependence of the piezoelectric coefficient could be deduced. A local maximum value of 600 pm V–1 was deduced in the 3.5–4.5 μm section of the thickest films. The dependence of the film properties on film thickness is attributed to the decreasing effect of the clamping constraint imposed by the substrate and the increasing spatial separation between the grains with increasing film thickness. PMID:28247756

Fabrication of a two-dimensional piezoelectric micromachined ultrasonic transducer array using a top-crossover-to-bottom structure and metal bridge connections

NASA Astrophysics Data System (ADS)

Jung, Joontaek; Kim, Sangwon; Lee, Wonjun; Choi, Hongsoo

2013-12-01

A new design methodology and fabrication process for two-dimensional (2D) piezoelectric micromachined ultrasonic transducer (pMUT) arrays using a top-crossover-to-bottom (TCTB) structure was developed. Individual sensing and actuation of pMUT elements from a small number of connection lines was enabled by the TCTB structure, and the parasitic coupling capacitance of the array was significantly reduced as a result. A 32 × 32 pMUT array with a TCTB structure was fabricated, resulting in 64 connection lines over an area of 4.8 × 4.8 mm2. The top electrodes for each pMUT element were re-connected by metal bridging after bottom-electrode etching caused them to become disconnected. A deep reactive ion etching process was used to compactify the array. Each pMUT element was a circular-shaped K31-type ultrasonic transducer using a 1 µm thick sol-gel lead zirconate titanate (PZT: Pb1.10 Zr0.52 Ti0.48) thin film. To characterize a single element in the 2D pMUT array, the resonant frequency and coupling coefficient of 20 pMUT elements were averaged to 3.85 MHz and 0.0112, respectively. The maximum measured ultrasound intensity in water, measured at a distance of 4 mm, was 4.6 µW cm-2 from a single pMUT element driven by a 5 Vpp sine wave at 2.22 MHz. Potential applications for development of a TCTB-arranged 2D pMUT array include ultrasonic medical imaging, ultrasonic communication, ultrasonic range-finding and handwriting input systems.

Accessory Mineral Depth-Profiling Applied to the Corsican Lower Crust: A Continuous Thermal History of Mesozoic Continental Rifting

NASA Astrophysics Data System (ADS)

Seymour, N. M.; Stockli, D. F.; Beltrando, M.; Smye, A.

2015-12-01

Despite advances in understanding the structural development of hyperextended magma-poor rift margins, the temporal and thermal evolution of lithospheric hyperextension during rifting remains only poorly understood. In contrast to classic pure-shear models, multi-stage rift models that include depth-dependent thinning predict significant lower-crustal reheating during the necking phase due to buoyant rise of the asthenosphere. The Santa Lucia nappe of NE Corsica is an ideal laboratory to test for lower-crustal reheating as it preserves Permian lower crust exhumed from granulitic conditions during Mesozoic Tethyan rifting. This study presents the first use of apatite U-Pb depth-profile thermochronology in conjunction with novel rutile U-Pb and zircon U-Pb thermo- and geochronology to reconstruct a continuous t-T path to constrain the syn-rift thermal evolution of this exposed lower-crustal section. LASS-ICP-MS depth-profile analyses of zircon reveal thin (<10 μm) ~210-180 Ma overgrowths on 300-270 Ma cores in lower-crustal lithologies, indicative of renewed thermal activity during Mesozoic rifting. Cooling due to rapid rift margin exhumation is recorded by the topology of rutile and apatite depth profiles caused by thermally-activated volume diffusion at T >400°C. Lower-crustal rutile reveal a rounded progression from core plateaus at ~170 Ma to 150-145 Ma at the outer 8-10 μm of grains while middle-crustal apatite records 170 Ma cores grading to 140-135 Ma rims. Inverse modeling of rutile profiles suggests the lower crust cooled from 700°C at 200 Ma to 425°C at 140 Ma. Middle-crustal apatite yield a two-stage history, with rapid cooling from 500°C at 200 Ma to 420°C at ~180 Ma followed by slow cooling to 400°C by 160 Ma. Combined with zircon overgrowth ages, these data indicate the Santa Lucia nappe underwent a thermal pulse in the late Triassic-early Jurassic associated with depth-dependent thinning and hyperextension of the Corsican margin.

High-Performance Protonic Ceramic Fuel Cells with Thin-Film Yttrium-Doped Barium Cerate-Zirconate Electrolytes on Compositionally Gradient Anodes.

PubMed

Bae, Kiho; Lee, Sewook; Jang, Dong Young; Kim, Hyun Joong; Lee, Hunhyeong; Shin, Dongwook; Son, Ji-Won; Shim, Joon Hyung

2016-04-13

In this study, we used a compositionally gradient anode functional layer (AFL) consisting of Ni-BaCe(0.5)Zr(0.35)Y(0.15)O(3-δ) (BCZY) with increasing BCZY contents toward the electrolyte-anode interface for high-performance protonic ceramic fuel cells. It is identified that conventional homogeneous AFLs fail to stably accommodate a thin film of BCZY electrolyte. In contrast, a dense 2 μm thick BCZY electrolyte was successfully deposited onto the proposed gradient AFL with improved adhesion. A fuel cell containing this thin electrolyte showed a promising maximum peak power density of 635 mW cm(-2) at 600 °C, with an open-circuit voltage of over 1 V. Impedance analysis confirmed that minimizing the electrolyte thickness is essential for achieving a high power output, suggesting that the anode structure is important in stably accommodating thin electrolytes.

Processing effects on the microstructure and dielectric properties of hydrothermal barium titanate and (barium,strontium)titanate thin films

NASA Astrophysics Data System (ADS)

McCormick, Mark Alan

The goal of this work was to produce BaTiO3 and BaxSr (1-x)TiO3 (BST) thin films with high dielectric constants, using a low-temperature (<100°C) hydrothermal synthesis route. To accomplish this, titanium metal-organic precursor films were spin-cast onto metal-coated glass substrates and converted to polycrystalline BaTiO3 or BST upon reacting in aqueous solutions of Ba(OH)2 or Ba(OH)2 and Sr(OH)2. The influences of solution molarity, processing temperature, and reaction time on thin film reaction kinetics, microstructure, and dielectric properties were examined for BaTiO3 films. Post-deposition annealing at temperatures as low as 200°C substantially affected the lattice parameter, dielectric constant, and dielectric loss. This behavior is explained in terms of hydroxyl defect incorporation during film formation. Current-voltage (I-V) measurements were performed to determine the dominant conduction mechanism(s) during application of a do field, and to extract the metal/ceramic barrier height. In particular, Schottky barrier-limited conduction and Poole-Frenkel conduction were investigated as potential leakage mechanisms. For BST thin films, film stoichiometry deviated from the initial solution composition, with a preferred incorporation of Sr2+ into the perovskite lattice. The dielectric constant of the BST films was measured as a function of composition (Ba:Sr ratio) and temperature over the range 25--150°C. Finally, capacitance-voltage (C-V) measurements were made for BST films to determine the influence of film composition on dielectric tunability.

Electrical Properties of Thin-Film Capacitors Fabricated Using High Temperature Sputtered Modified Barium Titanate.

PubMed

Reynolds, Glyn J; Kratzer, Martin; Dubs, Martin; Felzer, Heinz; Mamazza, Robert

2012-04-13

Simple thin-film capacitor stacks were fabricated from sputter-deposited doped barium titanate dielectric films with sputtered Pt and/or Ni electrodes and characterized electrically. Here, we report small signal, low frequency capacitance and parallel resistance data measured as a function of applied DC bias, polarization versus applied electric field strength and DC load/unload experiments. These capacitors exhibited significant leakage (in the range 8-210 μA/cm²) and dielectric loss. Measured breakdown strength for the sputtered doped barium titanate films was in the range 200 kV/cm -2 MV/cm. For all devices tested, we observed clear evidence for dielectric saturation at applied electric field strengths above 100 kV/cm: saturated polarization was in the range 8-15 μC/cm². When cycled under DC conditions, the maximum energy density measured for any of the capacitors tested here was ~4.7 × 10 -2 W-h/liter based on the volume of the dielectric material only. This corresponds to a specific energy of ~8 × 10 -3 W-h/kg, again calculated on a dielectric-only basis. These results are compared to those reported by other authors and a simple theoretical treatment provided that quantifies the maximum energy that can be stored in these and similar devices as a function of dielectric strength and saturation polarization. Finally, a predictive model is developed to provide guidance on how to tailor the relative permittivities of high-k dielectrics in order to optimize their energy storage capacities.

Electrical Properties of Thin-Film Capacitors Fabricated Using High Temperature Sputtered Modified Barium Titanate

PubMed Central

Reynolds, Glyn J.; Kratzer, Martin; Dubs, Martin; Felzer, Heinz; Mamazza, Robert

2012-01-01

Simple thin-film capacitor stacks were fabricated from sputter-deposited doped barium titanate dielectric films with sputtered Pt and/or Ni electrodes and characterized electrically. Here, we report small signal, low frequency capacitance and parallel resistance data measured as a function of applied DC bias, polarization versus applied electric field strength and DC load/unload experiments. These capacitors exhibited significant leakage (in the range 8–210 μA/cm2) and dielectric loss. Measured breakdown strength for the sputtered doped barium titanate films was in the range 200 kV/cm −2 MV/cm. For all devices tested, we observed clear evidence for dielectric saturation at applied electric field strengths above 100 kV/cm: saturated polarization was in the range 8–15 μC/cm2. When cycled under DC conditions, the maximum energy density measured for any of the capacitors tested here was ~4.7 × 10−2 W-h/liter based on the volume of the dielectric material only. This corresponds to a specific energy of ~8 × 10−3 W-h/kg, again calculated on a dielectric-only basis. These results are compared to those reported by other authors and a simple theoretical treatment provided that quantifies the maximum energy that can be stored in these and similar devices as a function of dielectric strength and saturation polarization. Finally, a predictive model is developed to provide guidance on how to tailor the relative permittivities of high-k dielectrics in order to optimize their energy storage capacities. PMID:28817001

Reliable bonding using indium-based solders

NASA Astrophysics Data System (ADS)

Cheong, Jongpil; Goyal, Abhijat; Tadigadapa, Srinivas; Rahn, Christopher

2004-01-01

Low temperature bonding techniques with high bond strengths and reliability are required for the fabrication and packaging of MEMS devices. Indium and indium-tin based bonding processes are explored for the fabrication of a flextensional MEMS actuator, which requires the integration of lead zirconate titanate (PZT) substrate with a silicon micromachined structure at low temperatures. The developed technique can be used either for wafer or chip level bonding. The lithographic steps used for the patterning and delineation of the seed layer limit the resolution of this technique. Using this technique, reliable bonds were achieved at a temperature of 200°C. The bonds yielded an average tensile strength of 5.41 MPa and 7.38 MPa for samples using indium and indium-tin alloy solders as the intermediate bonding layers respectively. The bonds (with line width of 100 microns) showed hermetic sealing capability of better than 10-11 mbar-l/s when tested using a commercial helium leak tester.

Reliable bonding using indium-based solders

NASA Astrophysics Data System (ADS)

Cheong, Jongpil; Goyal, Abhijat; Tadigadapa, Srinivas; Rahn, Christopher

2003-12-01

Low temperature bonding techniques with high bond strengths and reliability are required for the fabrication and packaging of MEMS devices. Indium and indium-tin based bonding processes are explored for the fabrication of a flextensional MEMS actuator, which requires the integration of lead zirconate titanate (PZT) substrate with a silicon micromachined structure at low temperatures. The developed technique can be used either for wafer or chip level bonding. The lithographic steps used for the patterning and delineation of the seed layer limit the resolution of this technique. Using this technique, reliable bonds were achieved at a temperature of 200°C. The bonds yielded an average tensile strength of 5.41 MPa and 7.38 MPa for samples using indium and indium-tin alloy solders as the intermediate bonding layers respectively. The bonds (with line width of 100 microns) showed hermetic sealing capability of better than 10-11 mbar-l/s when tested using a commercial helium leak tester.

Optimizing piezoelectric receivers for acoustic power transfer applications

NASA Astrophysics Data System (ADS)

Gorostiaga, M.; Wapler, M. C.; Wallrabe, U.

2018-07-01

In this paper, we aim to optimize piezoelectric plate receivers for acoustic power transfer applications by analyzing the influence of the losses and of the acoustic boundary conditions. We derive the analytic expressions of the efficiency of the receiver with the optimal electric loads attached, and analyze the maximum efficiency value and its frequency with different loss and acoustic boundary conditions. To validate the analytical expressions that we have derived, we perform experiments in water with composite transducers of different filling fractions, and see that a lower acoustic impedance mismatch can compensate the influence of large dielectric and acoustic losses to achieve a good performance. Finally, we briefly compare the advantages and drawbacks of composite transducers and pure PZT (lead zirconate titanate) plates as acoustic power receivers, and conclude that 1–3 composites can achieve similar efficiency values in low power applications due to their adjustable acoustic impedance.

Recent trends in reinforcement corrosion assessment using piezo sensors via electro mechanical impedance technique

NASA Astrophysics Data System (ADS)

Visalakshi, Talakokula; Bhalla, Suresh; Gupta, Ashok; Bhattacharjee, Bishwajit

2014-03-01

Reinforced concrete (RC) is an economical, versatile and successful construction material as it can be moulded into a variety of shapes and finishes. In most cases, it is durable and strong, performing well throughout its service life. However, in some cases, it does not perform adequately due to various reasons, one of which is the corrosion of the embedded steel bars used as reinforcement. . Although the electro-mechanical impedance (EMI) technique is well established for damage detection and quantification of civil, mechanical and aerospace structures, only limited studies have been reported of its application for rebar corrosion detection in RC structures. This paper presents the recent trends in corrosion assessment based on the model derived from the equivalent structural parameters extracted from the impedance spectrum of concrete-rebar system using the lead zirconate titanate (PZT) sensors via EMI technique.

Low temperature dielectric relaxation in ordinary perovskite ferroelectrics: enlightenment from high-energy x-ray diffraction

NASA Astrophysics Data System (ADS)

Ochoa, D. A.; Levit, R.; Fancher, C. M.; Esteves, G.; Jones, J. L.; E García, J.

2017-05-01

Ordinary ferroelectrics exhibit a second order phase transition that is characterized by a sharp peak in the dielectric permittivity at a frequency-independent temperature. Furthermore, these materials show a low temperature dielectric relaxation that appears to be a common behavior of perovskite systems. Tetragonal lead zirconate titanate is used here as a model system in order to explore the origin of such an anomaly, since there is no consensus about the physical phenomenon involved in it. Crystallographic and domain structure studies are performed from temperature dependent synchrotron x-ray diffraction measurement. Results indicate that the dielectric relaxation cannot be associated with crystallographic or domain configuration changes. The relaxation process is then parameterized by using the Vogel-Fulcher-Tammann phenomenological equation. Results allow us to hypothesize that the observed phenomenon is due to changes in the dynamic behavior of the ferroelectric domains related to the fluctuation of the local polarization.

Effect of material constants on power output in piezoelectric vibration-based generators.

PubMed

Takeda, Hiroaki; Mihara, Kensuke; Yoshimura, Tomohiro; Hoshina, Takuya; Tsurumi, Takaaki

2011-09-01

A possible power output estimation based on material constants in piezoelectric vibration-based generators is proposed. A modified equivalent circuit model of the generator was built and was validated by the measurement results in the generator fabricated using potassium sodium niobate-based and lead zirconate titanate (PZT) ceramics. Subsequently, generators with the same structure using other PZT-based and bismuth-layered structure ferroelectrics ceramics were fabricated and tested. The power outputs of these generators were expressed as a linear functions of the term composed of electromechanical coupling coefficients k(sys)(2) and mechanical quality factors Q*(m) of the generator. The relationship between device constants (k(sys)(2) and Q*(m)) and material constants (k(31)(2) and Q(m)) was clarified. Estimation of the power output using material constants is demonstrated and the appropriate piezoelectric material for the generator is suggested.

Accurate determination of complex materials coefficients of piezoelectric resonators.

PubMed

Du, Xiao-Hong; Wang, Qing-Ming; Uchino, Kenji

2003-03-01

This paper presents a method of accurately determining the complex piezoelectric and elastic coefficients of piezoelectric ceramic resonators from the measurement of the normalized electric admittance, Y, which is electric admittance Y of piezoelectric resonator normalized by the angular frequency omega. The coefficients are derived from the measurements near three special frequency points that correspond to the maximum and the minimum normalized susceptance (B) and the maximum normalized conductance (G). The complex elastic coefficient is determined from the frequencies at these points, and the real and imaginary parts of the piezoelectric coefficient are related to the derivative of the susceptance with respect to the frequency and the asymmetry of the conductance, respectively, near the maximum conductance point. The measurements for some lead zirconate titanate (PZT) based ceramics are used as examples to demonstrate the calculation and experimental procedures and the comparisons with the standard methods.

Piezoelectric and pyroelectric properties of PZT/P(VDF-TrFE) composites with constituent phases poled in parallel or antiparallel directions.

PubMed

Ng, K L; Chan, H L; Choy, C L

2000-01-01

Composites of lead zirconate titanate (PZT) powder dispersed in a vinylidene fluoride-trifluoroethylene copolymer [P(VDF-TrFE)] matrix have been prepared by compression molding. Three groups of polarized samples have been prepared by poling: only the ceramic phase, the ceramic and polymer phases in parallel directions, and the two phases in antiparallel directions. The measured permittivities of the unpoled composites are consistent with the predictions of the Bruggeman model. The changes in the pyroelectric and piezoelectric coefficients of the poled composites with increasing ceramic volume fraction can be described by modified linear mixture rules. When the ceramic and copolymer phases are poled in the same direction, their pyroelectric activities reinforce while their piezoelectric activities partially cancel. However, when the ceramic and copolymer phases are poled in opposite directions, their piezoelectric activities reinforce while their pyroelectric activities partially cancel.

Temperature dependent mechanical property of PZT film: an investigation by nanoindentation.

PubMed

Li, Yingwei; Feng, Shangming; Wu, Wenping; Li, Faxin

2015-01-01

Load-depth curves of an unpoled Lead Zirconate Titanate (PZT) film composite as a function of temperature were measured by nanoindentation technique. Its reduce modulus and hardness were calculated by the typical Oliver-Pharr method. Then the true modulus and hardness of the PZT film were assessed by decoupling the influence of substrate using methods proposed by Zhou et al. and Korsunsky et al., respectively. Results show that the indentation depth and modulus increase, but the hardness decreases at elevated temperature. The increasing of indentation depth and the decreasing of hardness are thought to be caused by the decreasing of the critical stress needed to excite dislocation initiation at high temperature. The increasing of true modulus is attributed to the reducing of recoverable indentation depth induced by back-switched domains. The influence of residual stress on the indentation behavior of PZT film composite was also investigated by measuring its load-depth curves with pre-load strains.

1.6 V nanogenerator for mechanical energy harvesting using PZT nanofibers.

PubMed

Chen, Xi; Xu, Shiyou; Yao, Nan; Shi, Yong

2010-06-09

Energy harvesting technologies that are engineered to miniature sizes, while still increasing the power delivered to wireless electronics, (1, 2) portable devices, stretchable electronics, (3) and implantable biosensors, (4, 5) are strongly desired. Piezoelectric nanowire- and nanofiber-based generators have potential uses for powering such devices through a conversion of mechanical energy into electrical energy. (6) However, the piezoelectric voltage constant of the semiconductor piezoelectric nanowires in the recently reported piezoelectric nanogenerators (7-12) is lower than that of lead zirconate titanate (PZT) nanomaterials. Here we report a piezoelectric nanogenerator based on PZT nanofibers. The PZT nanofibers, with a diameter and length of approximately 60 nm and 500 microm, were aligned on interdigitated electrodes of platinum fine wires and packaged using a soft polymer on a silicon substrate. The measured output voltage and power under periodic stress application to the soft polymer was 1.63 V and 0.03 microW, respectively.

Damage Detection Based on Power Dissipation Measured with PZT Sensors through the Combination of Electro-Mechanical Impedances and Guided Waves.

PubMed

Sevillano, Enrique; Sun, Rui; Perera, Ricardo

2016-05-05

The use of piezoelectric ceramic transducers (such as Lead-Zirconate-Titanate-PZT) has become more and more widespread for Structural Health Monitoring (SHM) applications. Among all the techniques that are based on this smart sensing solution, guided waves and electro-mechanical impedance techniques have found wider acceptance, and so more studies and experimental works can be found containing these applications. However, even though these two techniques can be considered as complementary to each other, little work can be found focused on the combination of them in order to define a new and integrated damage detection procedure. In this work, this combination of techniques has been studied by proposing a new integrated damage indicator based on Electro-Mechanical Power Dissipation (EMPD). The applicability of this proposed technique has been tested through different experimental tests, with both lab-scale and real-scale structures.

PVDF-PZT nanocomposite film based self-charging power cell.

PubMed

Zhang, Yan; Zhang, Yujing; Xue, Xinyu; Cui, Chunxiao; He, Bin; Nie, Yuxin; Deng, Ping; Lin Wang, Zhong

2014-03-14

A novel PVDF-PZT nanocomposite film has been proposed and used as a piezoseparator in self-charging power cells (SCPCs). The structure, composed of poly(vinylidene fluoride) (PVDF) and lead zirconate titanate (PZT), provides a high piezoelectric output, because PZT in this nanocomposite film can improve the piezopotential compared to the pure PVDF film. The SCPC based on this nanocomposite film can be efficiently charged up by the mechanical deformation in the absence of an external power source. The charge capacity of the PVDF-PZT nanocomposite film based SCPC in 240 s is ∼0.010 μA h, higher than that of a pure PVDF film based SCPC (∼0.004 μA h). This is the first demonstration of using PVDF-PZT nanocomposite film as a piezoseparator for SCPC, and is an important step for the practical applications of SCPC for harvesting and storing mechanical energy.

Enhanced ferroelectric and piezoelectric properties in La-modified PZT ceramics

NASA Astrophysics Data System (ADS)

Kour, P.; Pradhan, S. K.; Kumar, Pawan; Sinha, S. K.; Kar, Manoranjan

2016-06-01

The effect of lanthanum (La) doping on ferroelectric and piezoelectric properties of lead zirconate titanate (PZT) sample has been investigated. Pb1- x La x Zr0.52Ti0.48O3 ceramics with x = 0.00, 0.02, 0.04, 0.06 and 0.10 were prepared by the sol-gel technique. Raman and Fourier transforms infrared spectroscopy have been employed to understand the structural modification due to ionic size mismatch. Raman spectra show the existence of both rhombohedral and tetragonal crystal symmetries. It also shows the dielectric relaxation with increase in La concentration in the sample. The increase in lattice strain due to La doping increases the remnant polarization and coercive field. The linear piezoelectric coefficient increases with the increase in La concentration. It reveals that La-substituted PZT is a better candidate for piezoelectric sensor applications as compared to that of PZT.

Surface acoustic wave micromotor with arbitrary axis rotational capability

NASA Astrophysics Data System (ADS)

Tjeung, Ricky T.; Hughes, Mark S.; Yeo, Leslie Y.; Friend, James R.

2011-11-01

A surface acoustic wave (SAW) actuated rotary motor is reported here, consisting of a millimeter-sized spherical metal rotor placed on the surface of a lead zirconate titanate piezoelectric substrate upon which the SAW is made to propagate. At the design frequency of 3.2 MHz and with a fixed preload of 41.1 μN, the maximum rotational speed and torque achieved were approximately 1900 rpm and 5.37 μN-mm, respectively, producing a maximum output power of 1.19 μW. The surface vibrations were visualized using laser Doppler vibrometry and indicate that the rotational motion arises due to retrograde elliptical motions of the piezoelectric surface elements. Rotation about orthogonal axes in the plane of the substrate has been obtained by using orthogonally placed interdigital electrodes on the substrate to generate SAW impinging on the rotor, offering a means to generate rotation about an arbitrary axis in the plane of the substrate.

Triple degree-of-freedom piezoelectric ultrasonic micromotor via flexural-axial coupled vibration.

PubMed

Khoo, Ter Fong; Dang, Dinh Huy; Friend, James; Oetomo, Denny; Yeo, Leslie

2009-08-01

Actuators remain a limiting factor in robotics, especially in microrobotics where the power density of actuators is a problem. A 3 x 3 x 8.7 mm 3-axis piezoelectric ultrasonic micromotor system is described here in an effort to help solve this problem. Formed from 4 bulk lead zirconate titanate (PZT) thickness-polarized elements placed around the periphery of a rectangular rod, the stator is designed to combine axial and flexural vibrations in a way that permits rotation of a hardened steel ball as a rotor about an arbitrary axis. A simple prototype of the micromotor was found to produce at least a rotation speed of 10.4 rad/s with 4 microN-m torque about all 3 orthogonal directions at an excitation frequency of about 221 kHz, demonstrating the feasibility of a 3 degree-of-freedom millimeter-scale piezoelectric motor.

Ultra-flexible Piezoelectric Devices Integrated with Heart to Harvest the Biomechanical Energy

PubMed Central

Lu, Bingwei; Chen, Ying; Ou, Dapeng; Chen, Hang; Diao, Liwei; Zhang, Wei; Zheng, Jun; Ma, Weiguo; Sun, Lizhong; Feng, Xue

2015-01-01

Power supply for medical implantable devices (i.e. pacemaker) always challenges not only the surgery but also the battery technology. Here, we report a strategy for energy harvesting from the heart motion by using ultra-flexible piezoelectric device based on lead zirconate titanate (PZT) ceramics that has most excellent piezoelectricity in commercial materials, without any burden or damage to hearts. Experimental swine are selected for in vivo test with different settings, i.e. opened chest, close chest and awake from anesthesia, to simulate the scenario of application in body due to their hearts similar to human. The results show the peak-to-peak voltage can reach as high as 3 V when the ultra-flexible piezoelectric device is fixed from left ventricular apex to right ventricle. This demonstrates the possibility and feasibility of fully using the biomechanical energy from heart motion in human body for sustainably driving implantable devices. PMID:26538375

Plate-shaped non-contact ultrasonic transporter using flexural vibration.

PubMed

Ishii, Takahiko; Mizuno, Yosuke; Koyama, Daisuke; Nakamura, Kentaro; Harada, Kana; Uchida, Yukiyoshi

2014-02-01

We developed a plate-shaped non-contact transporter based on ultrasonic vibration, exploiting a phenomenon that a plate can be statically levitated at the place where its gravity and the acoustic radiation force are balanced. In the experiment, four piezoelectric zirconate titanate elements were attached to aluminum plates, on which lattice flexural vibration was excited at 22.3 kHz. The vibrating plates were connected to a loading plate via flexible posts that can minimize the influence of the flexure induced by heavy loads. The distribution of the vibration displacement on the plate was predicted through finite-element analysis to find the appropriate positions of the posts. The maximum levitation height of this transporter was 256 μm with no load. When two vibrating plates were connected to a loading plate, the maximum transportable load was 4.0 kgf. Copyright © 2013. Published by Elsevier B.V.

Design of Fresnel Lens-Type Multi-Trapping Acoustic Tweezers

PubMed Central

Tu, You-Lin; Chen, Shih-Jui; Hwang, Yean-Ren

2016-01-01

In this paper, acoustic tweezers which use beam forming performed by a Fresnel zone plate are proposed. The performance has been demonstrated by finite element analysis, including the acoustic intensity, acoustic pressure, acoustic potential energy, gradient force, and particle distribution. The acoustic tweezers use an ultrasound beam produced by a lead zirconate titanate (PZT) transducer operating at 2.4 MHz and 100 Vpeak-to-peak in a water medium. The design of the Fresnel lens (zone plate) is based on air reflection, acoustic impedance matching, and the Fresnel half-wave band (FHWB) theory. This acoustic Fresnel lens can produce gradient force and acoustic potential wells that allow the capture and manipulation of single particles or clusters of particles. Simulation results strongly indicate a good trapping ability, for particles under 150 µm in diameter, in the minimum energy location. This can be useful for cell or microorganism manipulation. PMID:27886050

Solid state electro-optic color filter and iris

NASA Technical Reports Server (NTRS)

1974-01-01

The electro-optic properties of lanthanum-modified lead zirconate titanate (PLZT) ferroelectric ceramic material are evaluated when utilized as a variable density and/or spectral filter in conjunction with a television scanning system. Emphasis was placed on the development of techniques and procedures for processing the PLZT disks and for applying efficient electrode structures. A number of samples were processed using different combinations of cleaning, electrode material, and deposition process. Best overall performance resulted from the direct evaporation of gold over chrome electrodes. A ruggedized mounting holder assembly was designed, fabricated, and tested. The assembly provides electrical contacts, high voltage protection, and support for the fragile PLZT disk, and permits mounting and optical alignment of the associated polarizers. Operational measurements of a PLZT sample mounted in the holder assembly were performed in conjunction with a television camera and the associated drive circuits. The data verified achievement of the elimination of the observed white-line effect.

Reference-free fatigue crack detection using nonlinear ultrasonic modulation under various temperature and loading conditions

NASA Astrophysics Data System (ADS)

Lim, Hyung Jin; Sohn, Hoon; DeSimio, Martin P.; Brown, Kevin

2014-04-01

This study presents a reference-free fatigue crack detection technique using nonlinear ultrasonic modulation. When low frequency (LF) and high frequency (HF) inputs generated by two surface-mounted lead zirconate titanate (PZT) transducers are applied to a structure, the presence of a fatigue crack can provide a mechanism for nonlinear ultrasonic modulation and create spectral sidebands around the frequency of the HF signal. The crack-induced spectral sidebands are isolated using a combination of linear response subtraction (LRS), synchronous demodulation (SD) and continuous wavelet transform (CWT) filtering. Then, a sequential outlier analysis is performed on the extracted sidebands to identify the crack presence without referring any baseline data obtained from the intact condition of the structure. Finally, the robustness of the proposed technique is demonstrated using actual test data obtained from simple aluminum plate and complex aircraft fitting-lug specimens under varying temperature and loading variations.

Piezoelectric ribbons printed onto rubber for flexible energy conversion.

PubMed

Qi, Yi; Jafferis, Noah T; Lyons, Kenneth; Lee, Christine M; Ahmad, Habib; McAlpine, Michael C

2010-02-10

The development of a method for integrating highly efficient energy conversion materials onto stretchable, biocompatible rubbers could yield breakthroughs in implantable or wearable energy harvesting systems. Being electromechanically coupled, piezoelectric crystals represent a particularly interesting subset of smart materials that function as sensors/actuators, bioMEMS devices, and energy converters. Yet, the crystallization of these materials generally requires high temperatures for maximally efficient performance, rendering them incompatible with temperature-sensitive plastics and rubbers. Here, we overcome these limitations by presenting a scalable and parallel process for transferring crystalline piezoelectric nanothick ribbons of lead zirconate titanate from host substrates onto flexible rubbers over macroscopic areas. Fundamental characterization of the ribbons by piezo-force microscopy indicates that their electromechanical energy conversion metrics are among the highest reported on a flexible medium. The excellent performance of the piezo-ribbon assemblies coupled with stretchable, biocompatible rubber may enable a host of exciting avenues in fundamental research and novel applications.

Ultra-flexible Piezoelectric Devices Integrated with Heart to Harvest the Biomechanical Energy

NASA Astrophysics Data System (ADS)

Lu, Bingwei; Chen, Ying; Ou, Dapeng; Chen, Hang; Diao, Liwei; Zhang, Wei; Zheng, Jun; Ma, Weiguo; Sun, Lizhong; Feng, Xue

2015-11-01

Power supply for medical implantable devices (i.e. pacemaker) always challenges not only the surgery but also the battery technology. Here, we report a strategy for energy harvesting from the heart motion by using ultra-flexible piezoelectric device based on lead zirconate titanate (PZT) ceramics that has most excellent piezoelectricity in commercial materials, without any burden or damage to hearts. Experimental swine are selected for in vivo test with different settings, i.e. opened chest, close chest and awake from anesthesia, to simulate the scenario of application in body due to their hearts similar to human. The results show the peak-to-peak voltage can reach as high as 3 V when the ultra-flexible piezoelectric device is fixed from left ventricular apex to right ventricle. This demonstrates the possibility and feasibility of fully using the biomechanical energy from heart motion in human body for sustainably driving implantable devices.

Enlarging photovoltaic effect: combination of classic photoelectric and ferroelectric photovoltaic effects.

PubMed

Zhang, Jingjiao; Su, Xiaodong; Shen, Mingrong; Dai, Zhihua; Zhang, Lingjun; He, Xiyun; Cheng, Wenxiu; Cao, Mengyu; Zou, Guifu

2013-01-01

Converting light energy to electrical energy in photovoltaic devices relies on the photogenerated electrons and holes separated by the built-in potential in semiconductors. Photo-excited electrons in metal electrodes are usually not considered in this process. Here, we report an enhanced photovoltaic effect in the ferroelectric lanthanum-modified lead zirconate titanate (PLZT) by using low work function metals as the electrodes. We believe that electrons in the metal with low work function could be photo-emitted into PLZT and form the dominant photocurrent in our devices. Under AM1.5 (100 mW/cm²) illumination, the short-circuit current and open-circuit voltage of Mg/PLZT/ITO are about 150 and 2 times of those of Pt/PLZT/ITO, respectively. The photovoltaic response of PLZT capacitor was expanded from ultraviolet to visible spectra, and it may have important impact on design and fabrication of high performance photovoltaic devices based on ferroelectric materials.

A standing wave linear ultrasonic motor operating in in-plane expanding and bending modes.

PubMed

Chen, Zhijiang; Li, Xiaotian; Ci, Penghong; Liu, Guoxi; Dong, Shuxiang

2015-03-01

A novel standing wave linear ultrasonic motor operating in in-plane expanding and bending modes was proposed in this study. The stator (or actuator) of the linear motor was made of a simple single Lead Zirconate Titanate (PZT) ceramic square plate (15 × 15 × 2 mm(3)) with a circular hole (D = 6.7 mm) in the center. The geometric parameters of the stator were computed with the finite element analysis to produce in-plane bi-mode standing wave vibration. The calculated results predicted that a driving tip attached at midpoint of one edge of the stator can produce two orthogonal, approximate straight-line trajectories, which can be used to move a slider in linear motion via frictional forces in forward or reverse direction. The investigations showed that the proposed linear motor can produce a six times higher power density than that of a previously reported square plate motor.

A study on (K, Na) NbO3 based multilayer piezoelectric ceramics micro speaker

NASA Astrophysics Data System (ADS)

Gao, Renlong; Chu, Xiangcheng; Huan, Yu; Sun, Yiming; Liu, Jiayi; Wang, Xiaohui; Li, Longtu

2014-10-01

A flat panel micro speaker was fabricated from (K, Na) NbO3 (KNN)-based multilayer piezoelectric ceramics by a tape casting and cofiring process using Ag-Pd alloys as an inner electrode. The interface between ceramic and electrode was investigated by scanning electron microscope (SEM) and transmission electron microscope (TEM). The acoustic response was characterized by a standard audio test system. We found that the micro speaker with dimensions of 23 × 27 × 0.6 mm3, using three layers of 30 μm thickness KNN-based ceramic, has a high average sound pressure level (SPL) of 87 dB, between 100 Hz-20 kHz under five voltage. This result was even better than that of lead zirconate titanate (PZT)-based ceramics under the same conditions. The experimental results show that the KNN-based multilayer ceramics could be used as lead free piezoelectric micro speakers.

Titan's interior from its rotation axis orientation and its Love number

NASA Astrophysics Data System (ADS)

Baland, Rose-Marie; Gabriel, Tobie; Axel, Lefèvre

2013-04-01

The tidal Love number k2 of Titan has been recently estimated from Cassini flybys radio-tracking and is consistent with the presence of a global ocean in Titan's interior, located between two ice layers (Iess et al. 2012), in accordance with prediction from interior and evolutionary models for Titan. Previously, the orientation of the rotation axis of Titan has been measured on the basis of radar images from Cassini (Stiles et al. 2008). Titan's obliquity, is about 0.3. The measured orientation is more consistent with the presence of a global internal liquid ocean than with an entirely solid Titan (Baland et al. 2011). The global topography data of Titan seem to indicate some departure from the hydrostatic shape expected for a synchronous satellite under the influence of its rotation and the static tides raised by the central planet (Zebker et al. 2009). This may be explained by a differential tidal heating in the ice shell which flattens the poles (Nimmo and Bills 2010). A surface more flattened than expected implies compensation in depth to explain the measured gravity coefficients C20 and C22 of Iess et al. (2012). Here, all layers are assumed to have a tri-axial ellipsoid shape, but with polar and equatorial flattenings that differ from the hydrostatic expected ones. We assess the influence of this non-hydrostatic shape on the conclusions of Baland et al. (2011), which developped a Cassini state model for the orientation of the rotation axis of a synchronous satellite having an internal liquid layer. We assess the possibility to constrain Titan's interior (and particularly the structure of the water/ice layer) from both the rotation axis orientation and the Love number. We consider a range of internal structure models consistent with the mean density and the mean radius of Titan, and made of a shell, an ocean, a mantle, and a core, from the surface to the center, with various possible compositions (e.g. ammonia mixed with water for the ocean). The internal structure models consistent with the measured orientation of the rotation axis and Love number still have to be examined with respect to other constrains, such as the shell thickness estimation derived from electric-field measurement of the Huyges probe (Béghin et al. 2012) and the expected temperature profile of the water/ice layer. For instance, a thin shell would imply a rather thick ocean, based on water (or water/ammonia) phase diagram.

Novel Photovoltaic Devices Using Ferroelectric Material and Colloidal Quantum Dots

NASA Astrophysics Data System (ADS)

Paik, Young Hun

As the global concern for the financial and environmental costs of traditional energy resources increases, research on renewable energy, most notably solar energy, has taken center stage. Many alternative photovoltaic (PV) technologies for 'the next generation solar cell' have been extensively studied to overcome the Shockley-Queisser 31% efficiency limit as well as tackle the efficiency vs. cost issues. This dissertation focuses on the novel photovoltaic mechanism for the next generation solar cells using two inorganic nanomaterials, nanocrystal quantum dots and ferroelectric nanoparticles. Lead zirconate titanate (PZT) materials are widely studied and easy to synthesize using solution based chemistry. One of the fascinating properties of the PZT material is a Bulk Photovoltaic effect (BPVE). This property has been spotlighted because it can produce very high open circuit voltage regardless of the electrical bandgap of the materials. However, the poor optical absorption of the PZT materials and the required high temperature to form the ferroelectric crystalline structure have been obstacles to fabricate efficient photovoltaic devices. Colloidal quantum dots also have fascinating optical and electrical properties such as tailored absorption spectrum, capability of the bandgap engineering due to the wide range of material selection and quantum confinement, and very efficient carrier dynamics called multiple exciton generations. In order to utilize these properties, many researchers have put numerous efforts in colloidal quantum dot photovoltaic research and there has been remarkable progress in the past decade. However, several drawbacks are still remaining to achieve highly efficient photovoltaic device. Traps created on the large surface area, low carrier mobility, and lower open circuit voltage while increasing the absorption of the solar spectrum is main issues of the nanocrystal based photovoltaic effect. To address these issues and to take the advantages of the two materials, this dissertation focused on material synthesis for low cost solution process for both materials, fabrication of various device structures and electrical/optical characterization to understand the underlying physics. We successfully demonstrated lead sulfide quantum dots (PbS QDs) and lead zirconate titanate nanoparticles (PZT NPs) in an aqueous solution and fabricated a photosensitive device. Solution based low-temperature process was used to fabricate a PbS QD and a PZT NP device. We exhibited a superior photoresponse and ferroelectric photovoltaic properties with the novel PZT NP device and studied the physics on domain wall effect and internal polarity effect. PZT NP was mainly investigated because PZT NP device is the first report as a photosensitive device with a successful property demonstration, as we know of. PZT's crystalline structure and the size of the nanocrystals were studied using X-ray diffraction and TEM (Transmission electron microscopy) respectively. We observed < 100 nm of PZT NPs and this result matched with DLS (dynamic light scattering) measurement. We fabricated ferroelectric devices using the PZT NPs for the various optical and electrical characterizations and verified ferroelectric properties including ferroelectric hysteresis loop. We also observed a typical ferroelectric photovoltaic effect from a PZT NP based device which was fabricated on an ITO substrate. We synthesized colloidal quantum dots (CQD) with the inexpensive soluble process. Fabricated PbS QD was used for the hybrid device with PZT thin films. J-V measured and the result shows superior open circuit voltage characteristics compared to conventional PbS QD PV devices, and resulting the improvement of the solar cell efficiency. This Ferroelectrics and Quantum Dots (FE-QDs) device also the first trial and the success as we know of.

ZnO Thin Film Electronics for More than Displays

NASA Astrophysics Data System (ADS)

Ramirez, Jose Israel

Zinc oxide thin film transistors (TFTs) are investigated in this work for large-area electronic applications outside of display technology. A constant pressure, constant flow, showerhead, plasma-enhanced atomic layer deposition (PEALD) process has been developed to fabricate high mobility TFTs and circuits on rigid and flexible substrates at 200 °C. ZnO films and resulting devices prepared by PEALD and pulsed laser deposition (PLD) have been compared. Both PEALD and PLD ZnO films result in densely packed, polycrystalline ZnO thin films that were used to make high performance devices. PEALD ZnO TFTs deposited at 300 °C have a field-effect mobility of ˜ 40 cm2/V-s (and > 20 cm2/V-S deposited at 200 °C). PLD ZnO TFTs, annealed at 400 °C, have a field-effect mobility of > 60 cm2/V-s (and up to 100 cm2/V-s). Devices, prepared by either technique, show high gamma-ray radiation tolerance of up to 100 Mrad(SiO2) with only a small radiation-induced threshold voltage shift (VT ˜ -1.5 V). Electrical biasing during irradiation showed no enhanced radiation-induced effects. The study of the radiation effects as a function of material stack thicknesses revealed the majority of the radiation-induced charge collection happens at the semiconductor-passivation interface. A simple sheet-charge model at that interface can describe the radiation-induced charge in ZnO TFTs. By taking advantage of the substrate-agnostic process provided by PEALD, due to its low-temperature and excellent conformal coatings, ZnO electronics were monolithically integrated with thin-film complex oxides. Application-based examples where ZnO electronics provide added functionality to complex oxide-based devices are presented. In particular, the integration of arrayed lead zirconate titanate (Pb(Zr, Ti)O3 or PZT) thin films with ZnO electronics for microelectromechanical systems (MEMs) and deformable mirrors is demonstrated. ZnO switches can provide voltage to PZT capacitors with fast charging and slow discharging time constants. Finally, to circumvent fabrication challenges on predetermined complex shapes, like curved mirror optics, a technique to transfer electronics from a rigid substrate to a flexible substrate is used. This technique allows various thin films, regardless of their deposition temperature, to be transferred to flexible substrates. Finally, ultra-low power operation of ZnO TFT gas sensors was demonstrated. The ZnO ozone sensors were optimized to operate with excellent electrical stability in ambient conditions, without using elevated temperatures, while still providing good gas sensitivity. This was achieved by using a post-deposition anneal and by partially passivating the contact regions while leaving the semiconductor sensing area open to the ambient. A novel technique to reset the gas sensor using periodic pulsing of a UV light over the sensor results in less than 25 milliseconds recovery time. A pathway to achieve gas selectivity by using organic thin-film layers as filters deposited over the gas sensors tis demonstrated. The ZnO ozone sensor TFTs and the UV light operate at room temperature with an average power below 1 muW.

Electrical Properties of Tholins and Derived Constraints on the Huygens Landing Site Composition at the Surface of Titan

NASA Astrophysics Data System (ADS)

Lethuillier, A.; Le Gall, A.; Hamelin, M.; Caujolle-Bert, S.; Schreiber, F.; Carrasco, N.; Cernogora, G.; Szopa, C.; Brouet, Y.; Simões, F.; Correia, J. J.; Ruffié, G.

2018-04-01

In 2005, the complex permittivity of the surface of Saturn's moon Titan was measured by the PWA-MIP/HASI (Permittivity Wave Altimetry-Mutual Impedance Probe/Huygens Atmospheric Structure Instrument) experiment on board the Huygens probe. The analysis of these measurements was recently refined but could not be interpreted in terms of composition due to the lack of knowledge on the low-frequency/low-temperature electrical properties of Titan's organic material, a likely key ingredient of the surface composition. In order to fill that gap, we developed a dedicated measurement bench and investigated the complex permittivity of analogs of Titan's organic aerosols called "tholins." These laboratory measurements, together with those performed in the microwave domain, are then used to derive constraints on the composition of Titan's first meter below the surface based on both the PWA-MIP/HASI and the Cassini Radar observations. Assuming a ternary mixture of water ice, tholin-like dust and pores (filled or not with liquid methane), we find that at least 10% of water ice and 15% of porosity are required to explain observations. On the other hand, there should be at most 50-60% of organic dust. PWA-MIP/HASI measurements also suggest the presence of a thin conductive superficial layer at the Huygens landing site. Using accurate numerical simulations, we put constraints on the electrical conductivity of this layer as a function of its thickness (e.g., in the range 7-40 nS/m for a 7-mm thick layer). Potential candidates for the composition of this layer are discussed.

Ferroelectric thin-film capacitors and piezoelectric switches for mobile communication applications.

PubMed

Klee, Mareike; van Esch, Harry; Keur, Wilco; Kumar, Biju; van Leuken-Peters, Linda; Liu, Jin; Mauczok, Rüdiger; Neumann, Kai; Reimann, Klaus; Renders, Christel; Roest, Aarnoud L; Tiggelman, Mark P J; de Wild, Marco; Wunnicke, Olaf; Zhao, Jing

2009-08-01

Thin-film ferroelectric capacitors have been integrated with resistors and active functions such as ESD protection into small, miniaturized modules, which enable a board space saving of up to 80%. With the optimum materials and processes, integrated capacitors with capacitance densities of up to 100 nF/mm2 for stacked capacitors combined with breakdown voltages of 90 V have been achieved. The integration of these high-density capacitors with extremely high breakdown voltage is a major accomplishment in the world of passive components and has not yet been reported for any other passive integration technology. Furthermore, thin-film tunable capacitors based on barium strontium titanate with high tuning range and high quality factor at 1 GHz have been demonstrated. Finally, piezoelectric thin films for piezoelectric switches with high switching speed have been realized.

Tungsten-doped thin film materials

DOEpatents

Xiang, Xiao-Dong; Chang, Hauyee; Gao, Chen; Takeuchi, Ichiro; Schultz, Peter G.

2003-12-09

A dielectric thin film material for high frequency use, including use as a capacitor, and having a low dielectric loss factor is provided, the film comprising a composition of tungsten-doped barium strontium titanate of the general formula (Ba.sub.x Sr.sub.1-x)TiO.sub.3, where X is between about 0.5 and about 1.0. Also provided is a method for making a dielectric thin film of the general formula (Ba.sub.x Sr.sub.1-x)TiO.sub.3 and doped with W, where X is between about 0.5 and about 1.0, a substrate is provided, TiO.sub.2, the W dopant, Ba, and optionally Sr are deposited on the substrate, and the substrate containing TiO.sub.2, the W dopant, Ba, and optionally Sr is heated to form a low loss dielectric thin film.

Examining the Magnetic Properties of LaCoO3 Thin Films Using Magnetic Force Microscopy

NASA Astrophysics Data System (ADS)

Berg, Morgann; Posadas, Agham; de Lozanne, Alex; Demkov, Alexander

2011-03-01

In contrast to the non-magnetic ground state of bulk LaCo O3 (LCO) at low temperatures, ferromagnetism has been observed in elastically strained thin film specimens. The origins of ferromagnetism in strained LCO thin films have been obscured by conflicting experimental results. Pulsed laser deposition (PLD) is the current standard of preparation techniques used to grow thin films of LCO, but results from thin film LCO samples prepared by PLD have been questioned on the basis of chemical inhomogeneity and film defects. Using magnetic force microscopy, we investigate the microscale magnetic properties of strained thin films of LCO prepared by molecular beam epitaxy and deposited on lanthanum aluminate and strontium titanate substrates. We observe these properties across a temperature range surrounding the Curie temperature (Tc ~ 80 K) and compare our results to global magnetic characteristics of these films as measured by a SQUID magnetometer. Supported by NSF-DMR and NSF-IGERT.

Effect of crystal structure on strontium titanate thin films and their dielectric properties

NASA Astrophysics Data System (ADS)

Kampangkeaw, Satreerat

Strontium titanate (SrTiO3 or STO) has application in radio and microwave-frequency tunable capacitor devices particularly at low temperatures due to its high dielectric constant, low loss and the electric field tunability of its dielectric constant. The main goal of improving the performance in these devices is to increase the tunability and decrease the dielectric loss at the same time, especially at microwave frequencies. Thin films of STO however, show dramatic differences compared to the bulk. The dielectric constant of bulk STO increases nonlinearly from 300 at room temperature to 30000 at 4 K and the loss range is 10-3--10 -4. On the other hand. STO thin films, while showing a dielectric constant close to 300 at room temperature, typically reach a maximum between 1000 and 10000 in the 30 K to 100 K range before decreasing, and the high-loss range is 10-2--10-3. We have grown strontium titanate thin films using a pulsed laser deposition technique on substrates selected to have a small lattice mismatch between the film and substrate. Neodymium gallate (NdGaO3 or NGO) and lanthanum aluminate (LaAlO3 or LAO) substrates were good candidates due to only 1--2% mismatching. Film capacitor devices were fabricated with 25 micron gap separation. 1.5 mm total gap length and an overall 1 x 2 mm dimension using standard lithography and gold metal evaporative techniques. Their nonlinear dielectric constant and loss tangent were measured at low frequencies and also at 2 GHz, and from room temperature down to 4 K. The resulting films show significant variations of dielectric properties with position on the substrates with respect to the deposition plume axis. In the presence of DC electric fields up to +/-4 V/mum, STO films show improved dielectric tunability and low loss in regions far from the plume axis. We found that the films grown on NCO have lower dielectric loss than those on LAO due to a closer match of the NCO lattice to that of STO. We investigated the possible causes that make dielectric behavior in STO thin films different from the bulk. We characterized such film structures as lattice parameters, out-of-plane grain size, in-plane grain size, thickness, roughness, strains, and defects using ellipsometry, atomic force microscopy, and a high-resolution X-ray diffractometry. In plane grain size and percentage of defects were found to play a major role on the dielectric performance of the films.

Characterization of a Planet: Dependence on Coverage Fraction

NASA Astrophysics Data System (ADS)

Lorenz, R. D.

1996-03-01

I investigate, by means of numerical experiments and a real-time quiz of colleagues (to be repeated at the poster presentation associated with this abstract), how well-characterized a planet may be considered, as a function of how much of its surface has been studied. Most measures seem to indicate that characterization quality increases steeply up to about 30% coverage. Beyond 30%, additional coverage has a lower marginal value as a 'complete' knowledge of the surface is asymptotically reached. These studies are pertinent where tradeoffs of coverage against other scientific objectives exist, for example the orbital tour design of the Cassini mission. The tour design affects how much of Titan's surface (after the Galileo mission, Titan's surface becomes the largest mappable, but unmapped, area in the solar system) may be covered by the Cassini radar. The mission has too few flybys to cover all of Titan's surface: the Radar team aims to have 30% coverage at 1km resolution or better. I also find that long, thin swaths sample a planet better than square blocks of equivalent area.

Interesting Inclusions From Podiform Chromitites in Luobusa Ophiolite, Tibet

NASA Astrophysics Data System (ADS)

Yamamoto, S.; Komiya, T.; Hirose, K.; Maruyama, S.

2003-12-01

For the past decade, diamonds and unusual mineral asemblages were reported in podiform chromitites of the Luobusa ophiolite, southern Tibet, China (Bai 1993, Bai 2000, Yan 2001). These minerals were found from heavy mineral separation of chromitites. These minerals include (1) native elements, (2) alloys, (3) carbide (SiC, CrC), (4) platinium group elements (PGE) and arsenides, (5) silicates (Ol, Opx, Cpx, Amp, Srp, Chl, Uv, Prp, Alm, Wo, Zrn, Ap, Bt, Spn, Rt, Pl, Kfs, Phl, Sil, Qz and octahedral serpentine (possible pseduomorph after ringwoodite?), (5) oxide (corundum and chromite), (6) carbonates. Despite many questions as to these minerals above still remain open, these mineral inclusions would provide us the important infomation on the formation of the podiform chromitites. In this study, octahedral serpentine was discovered both on a thin section and from the heavy mineral separation. These octahedral inclusions exist within chromites, forming a line. These minerals are approximately 5-15μ m in diameter and have well octahedral morphology. EPMA, laser raman spectrometer and transmission electron microscopy (TEM) were used to determine the structure and chemical composition of this crystal. For the present, there are several interpretations of this octahedral silicate. One possibility is that if the octahedral structuer is euhedral so this octahedral serpentine may be pseudomorph after ringwoodite because of its chemical composition and octahedral crystal shape. Another is that ocahedral minerals are melt inclusions. Linear occurrence of octahedral minerals is similar to that of fuluid inclusions. If the octahedral structuer is negative crystal shape reflecting octahedral crystal of cromian spinel, then octahedral inclusions may be melt inclusions judging from linear occurrence. At the same time, zircons were obtained from the mineral separation from chromitites. U-Pb dating of these zircons by LA-ICP-MS yielded two different ages. One group has relatively younger age 107-534 Ma, which nearly plots on a concordia line. Another group has older age 1460-1822 Ma, which plots off the concordia line. Cathode luminescence images of these zircons indicate that some zircons have clear oscillatory zoning whereas other zircons show apparent homogeneous overgrowth. But any correlation between CL image and the U-Pb age was not identified in particular. Luobusa ophiolite has been recognized as fragment of Tethys oceanic crust formed in Cretaceous at 100-120 Ma (Allegre et al. 1984). The minimum age 107 Ma corresponds to the age of the formation of Luobusa ophiolite and all other age of zircons in chromitites is much older than that of ophiolite. In addition, the inclusions in the zircons were analyzed by EPMA and laser raman spectrometer. Several zircons contain some inclusions, which are quartz, feldsper, mica, apatite, titanite and others. These inclusions are the minerals composed of crustal material, which means that these zircons were crystalized in the low pressuer crustal condition. On the other hand, Yu et al. (2001) reported that zircons from chromitites in Luobusa ophiolite have shorter inter-atomic distances for Zr-O and Si-O bonds. They concluded that Tibetan-zircons were derived from the high-pressure mantle environment. Judging from the line of evidence mentioned avobe, it is highly possible that these zircons captured by chromitites were originated from recycled crustal materials convecting through upper mantle.

1T1R Nonvolatile Memory with Al/TiO₂/Au and Sol-Gel-Processed Insulator for Barium Zirconate Nickelate Gate in Pentacene Thin Film Transistor.

PubMed

Lee, Ke-Jing; Chang, Yu-Chi; Lee, Cheng-Jung; Wang, Li-Wen; Wang, Yeong-Her

2017-12-09

A one-transistor and one-resistor (1T1R) architecture with a resistive random access memory (RRAM) cell connected to an organic thin-film transistor (OTFT) device is successfully demonstrated to avoid the cross-talk issues of only one RRAM cell. The OTFT device, which uses barium zirconate nickelate (BZN) as a dielectric layer, exhibits favorable electrical properties, such as a high field-effect mobility of 5 cm²/Vs, low threshold voltage of -1.1 V, and low leakage current of 10 -12 A, for a driver in the 1T1R operation scheme. The 1T1R architecture with a TiO₂-based RRAM cell connected with a BZN OTFT device indicates a low operation current (10 μA) and reliable data retention (over ten years). This favorable performance of the 1T1R device can be attributed to the additional barrier heights introduced by using Ni (II) acetylacetone as a substitute for acetylacetone, and the relatively low leakage current of a BZN dielectric layer. The proposed 1T1R device with low leakage current OTFT and excellent uniform resistance distribution of RRAM exhibits a good potential for use in practical low-power electronic applications.

Corrosion testing of zirconia, beryllia and magnesia ceramics in molten alkali metal carbonates at 900 °C

NASA Astrophysics Data System (ADS)

Kaplan, Valery; Bendikov, Tatyana; Feldman, Yishay; Gartsman, Konstantin; Wachtel, Ellen; Lubomirsky, Igor

2016-01-01

An electrochemical cell containing molten Li2CO3-Li2O at 900 °C has been proposed for the conversion of the greenhouse gas CO2 to CO for chemical energy storage. In the current work, we have examined the corrosion resistance of zirconia, beryllia and magnesia ceramics at 900 °C in the Li2CO3-Li2O and Li-Na-K carbonate eutectic mixtures to identify suitable electrically insulating materials. Conclusions regarding material stability were based on elemental analysis of the melt, primarily via X-ray photoelectron spectroscopy, a particularly sensitive technique. It was found that magnesia is completely stable for at least 33 h in a Li2CO3-Li2O melt, while a combined lithium titanate/lithium zirconate layer forms on the zirconia ceramic as detected by XRD. Under the same melt conditions, beryllia shows considerable leaching into solution. In a Li-Na-K carbonate eutectic mixture containing 10.2 mol% oxide at 900 °C under standard atmospheric conditions, magnesia showed no signs of degradation. Stabilization of the zirconia content of the eutectic mixture at 0.01-0.02 at% after 2 h is explained by the formation of a lithium zirconate coating on the ceramic. On the basis of these results, we conclude that only magnesia can be satisfactorily used as an insulating material in electrolysis cells containing Li2CO3-Li2O melts.

Cassini-Huygens makes first close approach to Titan

NASA Astrophysics Data System (ADS)

2004-10-01

Purple zaze hi-res Size hi-res: 88 kb Credits: NASA/JPL/Space Science Institute Purple haze around Titan This NASA/ESA/ASI Cassini-Huygens image of Titan was taken with the narrow-angle camera on 3 July 2004, from a distance of about 789 000 kilometres from Titan. The image scale is 4.7 kilometres per pixel. This image shows two thin haze layers. The outer haze layer is detached and appears to float high in the atmosphere. Because of its thinness, the high haze layer is best seen at the moon's limb. The image was taken using a spectral filter sensitive to wavelengths of ultraviolet light centred at 338 nanometres. The image has been falsely coloured, the globe of Titan retains the pale orange hue our eyes would usually see, but both the main atmospheric haze and the thin detached layer have been brightened and given a purple colour to enhance their visibility. At the time of the closest approach, which is scheduled for 18:44 CEST, the spacecraft will be travelling only 1200 kilometres above the surface of the moon, almost grazing the outer atmosphere, at a speed of six kilometres per second (21 800 kilometres per hour)! Confirmation that the fly-by was successful and that all the data were received will not take place until 03:30 CEST on 27 October. This fly-by not only allows important surface science to be performed, such as radar analysis at close quarters, but also it significantly changes the orbit of the spacecraft around Saturn. Currently Cassini-Huygens has an orbital period of four months, which will change to 48 days, thus setting the course for the next close Titan fly-by on 13 December 2004 and the Huygens probe release on 25 December. Several of the observations performed during this fly-by will provide important information for ESA’s Huygens team, who will be using the data gathered to double-check atmospheric models for entry and descent on 14 January 2005. The Huygens probe will need to perform reliably in some of the most challenging and remote environments ever attempted by a man-made object. On this pass, the Huygens touchdown site will be visible at around 167 degrees East and 10.7 degrees South on the sunlit face of Titan before reaching the point of closest approach. Data from the imaging and radar instrumentation on board Cassini-Huygens should provide a tantalising idea of what the surface of Titan could be like. A second view of the Huygens touchdown site will be possible on the second close fly-by in December. Jean-Pierre Lebreton, ESA’s Huygens Mission Manager and Project Scientist, said: “This first close-up look at Titan should enable us to find out just how precisely our atmospheric models fit with the real situation and of course we are excited about the prospect of discovering just what type of surface the Huygens probe could impact on early next year.” Today’s fly-by will also be looking at other aspects of Titan which, although it is the second largest moon in the Solar System after Jupiter’s Ganymede, we know relatively little about. The instruments on board the Cassini orbiter will be looking at the surface characteristics, atmospheric properties and interactions with Saturn’s magnetosphere. Huygens is dormant during the fly-by. The first images are expected at 03:30 CEST on 28 October. However, at the point of closest approach, Titan will have an apparent size far exceeding the field of view of the Cassini orbiter’s narrow-angle camera. Details below a 100-metre resolution may be seen if the camera can pierce the haze and fog. Spectacular multicolour images at 1-2 kilometre resolution are also anticipated from the Visual Infrared and Mapping Spectrometer and may reveal details about Titan surface structure and composition. However, the excitement does not stop after 26 October. On 28 October, at about 12:30 CEST, there is a close encounter with Tethys, another of the significant moons of Saturn. Tethys is a ball of solid ice about 1060 kilometres in diameter which orbits Saturn at a distance of 295 000 kilometres. The Cassini-Huygens spacecraft will pass within 246 000 kilometres of this moon at a speed of 13.8 kilometres per second. At this distance the narrow-angle camera should be able to resolve features down to about 1.4 kilometres in size. Note to Editors The Cassini-Huygens mission to Saturn is the most ambitious effort in planetary space exploration ever mounted. A cooperative endeavour of the European Space Agency (ESA), NASA and the Italian space agency, Agenzia Spaziale Italiana (ASI), Cassini-Huygens is sending a sophisticated robotic spacecraft to orbit the ringed planet and study the Saturnian system in detail over a four-year period. On board Cassini is a scientific probe called Huygens, provided by ESA, which will be released from the main spacecraft to parachute through the atmosphere to the surface of Saturn’s largest and most interesting moon, Titan. For more information about the Cassini-Huygens mission please see: http://saturn.esa.int

SHRIMP U-Pb evidence for a Late Silurian age of metasedimentary rocks in the Merrimack and Putnam-Nashoba terranes, eastern New England

USGS Publications Warehouse

Wintsch, R.P.; Aleinikoff, J.N.; Walsh, G.J.; Bothner, Wallace A.; Hussey, A.M.; Fanning, C.M.

2007-01-01

U-Pb ages of detrital, metamorphic, and magmatic zircon and metamorphic monazite and titanite provide evidence for the ages of deposition and metamorphism of metasedimentary rocks from the Merrimack and Putnam-Nashoba terranes of eastern New England. Rocks from these terranes are interpreted here as having been deposited in the middle Paleozoic above Neoproterozoic basement of the Gander terrane and juxtaposed by Late Paleozoic thrusting in thin, fault-bounded slices. The correlative Hebron and Berwick formations (Merrimack terrane) and Tatnic Hill Formation (Putnam-Nashoba terrane), contain detrital zircons with Mesoproterozoic, Ordovician, and Silurian age populations. On the basis of the age of the youngest detrital zircon population (???425 Ma), the Hebron, Berwick and Tatnic Hill formations are no older than Late Silurian (Wenlockian). The minimum deposition ages of the Hebron and Berwick are constrained by ages of cross-cutting plutons (414 ?? 3 and 418 ?? 2 Ma, respectively). The Tatnic Hill Formation must be older than the oldest metamorphic monazite and zircon (???407 Ma). Thus, all three of these units were deposited between ???425 and 418 Ma, probably in the Ludlovian. Age populations of detrital zircons suggest Laurentian and Ordovician arc provenance to the west. High grade metamorphism of the Tatnic Hill Formation soon after deposition probably requires that sedimentation and burial occurred in a fore-arc environment, whereas time-equivalent calcareous sediments of the Hebron and Berwick formations probably originated in a back-arc setting. In contrast to age data from the Berwick Formation, the Kittery Formation contains primarily Mesoproterozoic detrital zircons; only 2 younger grains were identified. The absence of a significant Ordovician population, in addition to paleocurrent directions from the east and structural data indicating thrusting, suggest that the Kittery was derived from peri-Gondwanan sources and deposited in the Fredericton Sea. Thus, the Kittery should not be considered part of the Laurentian-derived Merrimack terrane; it more likely correlates with the early Silurian Fredericton terrane of northeastern New England and Maritime Canada.

Xenotime-(Y) formation from zircon dissolution-precipitation and HREE fractionation: an example from a metamorphosed phosphatic sandstone, Espinhaço fold belt (Brazil)

NASA Astrophysics Data System (ADS)

Franz, Gerhard; Morteani, Giulio; Rhede, Dieter

2015-10-01

We present an example where xenotime-(Y) together with metamorphic zircon replaces detrital zircon in a phosphatic sandstone from the Mesoproterozoic Espinhaço fold belt, Brazil, in a dissolution-precipitation reaction: {{zircon}}1 ( {{relict}} ) + {{P-}}{{bearing fluid}} = {{zircon}}2 ( {{metamorphic}} ) + {{xenotime}}. During the Brasiliano orogeny at 634 ± 19 Ma, the rocks experienced amphibolite facies metamorphism at ≥0.6 GPa/ 550 ± 37 °C (Southern Espinhaço) and ≥0.6 GPa/ 570 ± 35 °C (Northern Espinhaço), constrained by Zr-in-rutile and Ti-in-quartz thermometry and the presence of kyanite + muscovite + quartz. Many of the rocks show unusual rare earth element (REE) patterns with a hump at Gd-Tb-Dy and depletion in light REE. Detrital zircons (with relict ages between 1.5 and 3.3 Ga) show varying degrees of replacement as indicated by the presence of xenotime and associated porosity, from almost pristine to complete alteration. Textural evidence indicates local mobility of Zr and REE at the scale of the thin section. Xenotime-(Y) occurs together with other phosphates, mainly augelite, lazulite, and minerals of the svanbergite-crandallite-goyacite-florencite group. Xenotime-(Y) is very heterogeneous and reaches unusually high contents of up to 14 wt% Gd2O3, 13 wt% Dy2O3, and 3 wt% Tb2O3, corresponding to ≤0.36 REE atoms per formula unit due to the exchange Y = REE. The heavy REE patterns of xenotime-(Y) therefore show variable enrichment in individual elements, which explains the characteristic hump at Gd-Tb-Dy in the REE patterns of the whole rock. Although the rocks reached amphibolite facies conditions, textures indicate that formation of xenotime likely occurred during the early stages of diagenesis—metamorphism. Comparison with REE concentrations in xenotime-(Y) from the literature shows that selective REE incorporation into xenotime-(Y) is controlled by interaction with P-bearing hydrous fluids.

Development of advanced polymer nanocomposite capacitors

NASA Astrophysics Data System (ADS)

Mendoza, Miguel

The current development of modern electronics has driven the need for new series of energy storage devices with higher energy density and faster charge/discharge rate. Batteries and capacitors are two of the most widely used energy storage devices. Compared with batteries, capacitors have higher power density and significant higher charge/discharge rate. Therefore, high energy density capacitors play a significant role in modern electronic devices, power applications, space flight technologies, hybrid electric vehicles, portable defibrillators, and pulse power applications. Dielectric film capacitors represent an exceptional alternative for developing high energy density capacitors due to their high dielectric constants, outstanding breakdown voltages, and flexibility. The implementation of high aspect ratio dielectric inclusions such as nanowires into polymer capacitors could lead to further enhancement of its energy density. Therefore, this research effort is focused on the development of a new series of dielectric capacitors composed of nanowire reinforced polymer matrix composites. This concept of nanocomposite capacitors combines the extraordinary physical and chemical properties of the one-dimension (1D) nanoceramics and high dielectric strength of polymer matrices, leading to a capacitor with improved dielectric properties and energy density. Lead-free sodium niobate (NaNbO3) and lead-containing lead magnesium niobate-lead titanate (0.65PMN-0.35PT) nanowires were synthesized following hydrothermal and sol-gel approaches, respectively. The as-prepared nanowires were mixed with a polyvinylidene fluoride (PVDF) matrix using solution-casting method for nanocomposites fabrication. The dielectric constants and breakdown voltages of the NaNbO3/PVDF and 0.65PMN-0.35PT/PVDF nanocomposites were measured under different frequency ranges and temperatures in order to determine their maximum energy (J/cm3) and specific (J/g) densities. The electrical properties of the synthesized nanoceramics were compared with commercially available barium titanate (BaTiO3) and lead zirconate titanate Pb(ZrxTi1-x)O3 powders embedded into a PVDF matrix. The resulting dielectric film capacitors represent an excellent alternative energy storage device for future high energy density applications.

Physics and chemistry of complex oxide etching and redeposition control

NASA Astrophysics Data System (ADS)

Margot, Joëlle

2012-10-01

Since its introduction in the 1970s, plasma etching has become the universal method for fine-line pattern transfer onto thin films and is anticipated to remain so in foreseeable future. Despite many success stories, plasma etching processes fail to meet the needs for several of the newest materials involved in advanced devices for photonic, electronic and RF applications like ferroelectrics, electro-optic materials, high-k dielectrics, giant magnetoresistance materials and unconventional conductors. In this context, the work achieved over the last decade on the etching of multicomponent oxides thin films such as barium strontium titanate (BST), strontium titanate (STO) and niobate of calcium and barium (CBN) will be reviewed. These materials present a low reactivity with usual etching gases such as fluorinated and chlorinated gases, their etching is mainly governed by ion sputtering and reactive gases sometimes interact with surface materials to form compounds that inhibit etching. The etching of platinum will also be presented as an example of unconventional conductor materials for which severe redeposition limits the achievable etching quality. Finally, it will be shown how simulation can help to understand the etching mechanisms and to define avenues for higher quality patterning.

Nanostructured ultra-thin patches for ultrasound-modulated delivery of anti-restenotic drug

PubMed Central

Vannozzi, Lorenzo; Ricotti, Leonardo; Filippeschi, Carlo; Sartini, Stefania; Coviello, Vito; Piazza, Vincenzo; Pingue, Pasqualantonio; La Motta, Concettina; Dario, Paolo; Menciassi, Arianna

2016-01-01

This work aims to demonstrate the possibility to fabricate ultra-thin polymeric films loaded with an anti-restenotic drug and capable of tunable drug release kinetics for the local treatment of restenosis. Vascular nanopatches are composed of a poly(lactic acid) supporting membrane (thickness: ~250 nm) on which 20 polyelectrolyte bilayers (overall thickness: ~70 nm) are alternatively deposited. The anti-restenotic drug is embedded in the middle of the polyelectrolyte structure, and released by diffusion mechanisms. Nanofilm fabrication procedure and detailed morphological characterization are reported here. Barium titanate nanoparticles (showing piezoelectric properties) are included in the polymeric support and their role is investigated in terms of influence on nanofilm morphology, drug release kinetics, and cell response. Results show an efficient drug release from the polyelectrolyte structure in phosphate-buffered saline, and a clear antiproliferative effect on human smooth muscle cells, which are responsible for restenosis. In addition, preliminary evidences of ultrasound-mediated modulation of drug release kinetics are reported, thus evaluating the influence of barium titanate nanoparticles on the release mechanism. Such data were integrated with quantitative piezoelectric and thermal measurements. These results open new avenues for a fine control of local therapies based on smart responsive materials. PMID:26730191

Effect of structure and thermodynamic stability on the response of lanthanide stannate pyrochlores to ion beam irradiation.

PubMed

Lian, J; Helean, K B; Kennedy, B J; Wang, L M; Navrotsky, A; Ewing, R C

2006-02-09

The lanthanide stannates, Ln2Sn2O7, Ln=La-Lu and Y, have the isometric pyrochlore structure, A2B2O7, and their structural properties have been refined by Rietveld analysis of powder neutron and synchrotron X-ray diffraction data. In this study, the enthalpies of formation of selected stannate pyrochlores, Ln=La, Nd, Sm, Eu, Dy, and Yb, were measured by high-temperature oxide melt solution calorimetry. Their radiation response was determined by 1 MeV Kr2+ ion irradiation combined with in situ TEM observation over the temperature range of 25 to 1000 K. The enthalpy of formation from binary oxides of stannate pyrochlores became more endothermic (from -145 to -40 kJ/mol) as the size of the lanthanide in the A-site decreases. A more exothermic trend of the enthalpy of formation was observed in stannate pyrochlores with larger lanthanide ions, particularly La, possibly as a result of increased covalency in the Sn-O bond. In contrast to lanthanide titanate pyrochlores, Ln2Ti2O7, that are generally susceptible to radiation-induced amorphization and zirconate pyrochlores, Ln2Zr2O7, that are generally resistant to radiation-induced amorphization, the lanthanide stannate pyrochlores show a much greater variation in their response to ion irradiation. La, Nd, and Gd stannates experience the radiation-induced transformation to the aperiodic state, and the critical amorphization temperatures are approximately 960, 700, and 350 K, respectively. Y and Er stannate pyrochlores cannot be amorphized by ion beam irradiation, even at 25 K, and instead disorder to a defect fluorite structure. Comparison of the calorimetric and ion irradiation data for titanate, zirconate, and stannate pyrochlores reveals a strong correlation among subtle changes in crystal structure with changing composition, the energetics of the disordering process, and the temperature above which the material can no longer be amorphized. In summary, as the structure approaches the ideal, ordered pyrochlore structure, radiation-induced amorphization is more easily attained. This is consistent with an increasingly exothermic trend in the enthalpies of formation of pyrochlores from the oxides, that is, the greater the thermochemical stability of the pyrochlore structure, the more likely it will be amorphized upon radiation damage rather than recover to a disordered fluorite structure.

Electron emission and beam generation using ferroelectric cathodes

NASA Astrophysics Data System (ADS)

Flechtner, Donald D.

1999-06-01

In 1989, researchers at CERN published the discovery of significant electron emission (1-100 A/cm2) from Lead-Lanthanum-Zirconate- Titanate (PLZT). The publication of these results led to international interest in ferroelectric cathodes studies for use in pulsed power devices. At Cornell University in 1991, experiments with Lead-Zirconate-Titanate (PZT) compositions were begun to study the feasibility of using this ferroelectric material as a cathode in the electron gun section of High Power Traveling Wave Tube Amplifier Experiments. Current-voltage characteristics were documented for diode voltages ranging from 50-500,000 V with anode cathode gaps of.5-6 cm. A linear current-voltage relation was found for voltages less than 50 kV. For diode voltages >=200 kV, a typical Child-Langmuir V3/2 dependence was observed. Additional experiments have demonstrated repetition rates of up to 50 Hz with current densities of >=20 A/cm2. These results have been used in the ongoing design and construction of the electron gun for a 500 kV pulse modulator capable of repetitive operation at 1 Hz. The electron gun uses a PZT 55/45 (Pb(Zr.55,Ti.45 )O3) cathode to produce a <=400 A electron beam focused by a converging magnetic field. Studies of the emission process itself indicate the initial electrons are produced by field emission from the metallic grid applied to the front surface of the cathode. The field emission is induced by the application of a fast rising 1-3 kV, 150 ns pulse to the rear electrode of the 1 mm thick ferroelectric. Field emission can lead to explosive emission from microprotrusions and metal-ferroelectric-vacuum triple points forming a diffuse plasma on the surface of the sample. Under long pulse experiments (1-5 μs), plasma velocities of ~2 cm/μs were measured from gap closure rates. Results from an ion Faraday cup experiment showed ion velocities of 1-2 cm/μs. Experimental evidence indicates the electron emission is dependent on the field emission initiated by the voltage applied to rear surface of the ferroelectric; however, for current pulse durations on the order of microseconds, the surface plasma expansion into the gap can dominate current flow.

Titan's Topside Ionospheric Composition: Cassini Plasma Spectrometer Ion Mass Spectrometer Measurements

NASA Astrophysics Data System (ADS)

Sittler, Edward; Hartle, Richard; Ali, Ashraf; Cooper, John; Lipatov, Alexander; Simpson, David; Sarantos, Menelaos; Chornay, Dennis; Smith, Todd

2017-01-01

We present ion composition measurements of Titan's topside ionosphere using both T9 and T15 Cassini Plasma Spectrometer (CAPS) Ion Mass Spectrometer (IMS) measurements. The IMS is able to make measurements of Titan's ionosphere due to ionospheric outflows as originally reported for the T9 flyby. This allows one to take advantage of the unique capabilities of the CAPS IMS which measures both the mass-per-charge (M/Q) of the ions and the fragments of the ions produced inside the sensor such as carbon, nitrogen and oxygen fragments. Specific attention will be given to such ions as NH4 +, N +, O +, CH4 +, CxHy +, and HCNH + ions as examples. The CAPS IMS uses a time-of-flight (TOF) technique which accelerates ions up to 14.6 kV, so they can pass through ultra-thin carbon foils. Neutral fragments are used to measure the ion M/Q and positive fragments to measure the atomic components. We preliminarily find, by using IMS measurements of T9 and T15 ionospheric outflows, evidence for methane group ions, nitrogen ions, ammonium ions, water group ions and CnHm + ions with n = 2, 3, and 4 within Titan's topside ionosphere. E.C. Sittler acknowledges support at Goddard Space Flight Center by the CAPS Cassini Project from JPL funds under contract # NAS703001TONMO711123/1405851.

Zircon crytallization and recycling in the magma chamber of the rhyolitic Kos Plateau Tuff (Aegean arc)

USGS Publications Warehouse

Bachman, O.; Charlier, B.L.A.; Lowenstern, J. B.

2007-01-01

In contrast to most large-volume silicic magmas in continental arcs, which are thought to evolve as open systems with significant assimilation of preexisting crust, the Kos Plateau Miff magma formed dominantly by crystal fractionation of mafic parents. Deposits from this ??? 60 km3 pyroclastic eruption (the largest known in the Aegean arc) lack xenocrystic zircons [secondary ion mass spectrometry (SIMS) U-Pb ages on zircon cores never older than 500 ka] and display Sr-Nd whole-rock isotopic ratios within the range of European mantle in an area with exposed Paleozoic and Tertiary continental crust; this evidence implies a nearly closed-system chemical differentiation. Consequently, the age range provided by zircon SIMS U-Th-Pb dating is a reliable indicator of the duration of assembly and longevity of the silicic magma body above its solidus. The age distribution from 160 ka (age of eruption by sanidine 40Ar/39Ar dating; Smith et al., 1996) to ca. 500 ka combined with textural characteristics (high crystal content, corrosion of most anhydrous phenocrysts, but stability of hydrous phases) suggest (1) a protracted residence in the crust as a crystal mush and (2) rejuvenation (reduced crystallization and even partial resorption of minerals) prior to eruption probably induced by new influx of heat (and volatiles). This extended evolution chemically isolated from the surrounding crust is a likely consequence of the regional geodynamics because the thinned Aegean microplate acts as a refractory container for magmas in the dying Aegean subduction zone (continent-continent subduction). ?? 2007 Geological Society of America.

Zircon crystallization and recycling in the magma chamber of the rhyolitic Kos Plateau Tuff (Aegean arc)

USGS Publications Warehouse

Bachman, O.; Charlier, B.L.A.; Lowenstern, J. B.

2007-01-01

In contrast to most large-volume silicic magmas in continental arcs, which are thought to evolve as open systems with significant assimilation of preexisting crust, the Kos Plateau Tuff magma formed dominantly by crystal fractionation of mafic parents. Deposits from this ~60 km3 pyroclastic eruption (the largest known in the Aegean arc) lack xenocrystic zircons [secondary ion mass spectrometry (SIMS) U-Pb ages on zircon cores never older than 500 ka] and display Sr-Nd whole-rock isotopic ratios within the range of European mantle in an area with exposed Paleozoic and Tertiary continental crust; this evidence implies a nearly closed-system chemical differentiation. Consequently, the age range provided by zircon SIMS U-Th-Pb dating is a reliable indicator of the duration of assembly and longevity of the silicic magma body above its solidus. The age distribution from 160 ka (age of eruption by sanidine 40Ar/39Ar dating; Smith et al., 1996) to ca. 500 ka combined with textural characteristics (high crystal content, corrosion of most anhydrous phenocrysts, but stability of hydrous phases) suggest (1) a protracted residence in the crust as a crystal mush and (2) rejuvenation (reduced crystallization and even partial resorption of minerals) prior to eruption probably induced by new influx of heat (and volatiles). This extended evolution chemically isolated from the surrounding crust is a likely consequence of the regional geodynamics because the thinned Aegean microplate acts as a refractory container for magmas in the dying Aegean subduction zone (continent-continent subduction).

Long-lived melting of ancient lower crust of the North China Craton in response to paleo-Pacific plate subduction, recorded by adakitic rhyolite

NASA Astrophysics Data System (ADS)

Wang, Chao; Song, Shuguang; Niu, Yaoling; Allen, Mark B.; Su, Li; Wei, Chunjing; Zhang, Guibin; Fu, Bin

2017-11-01

Magmatism in eastern China in response to paleo-Pacific plate subduction during the Mesozoic was complex, and it is unclear how and when exactly the magmas formed via thinning and partial destruction of the continental lithosphere. To better understand this magmatism, we report the results of a geochronological and geochemical study of Early Cretaceous adakitic rhyolite (erupted at 125.4 ± 2.2 Ma) in the Xintaimen area within the eastern North China Craton (NCC). In situ zircon U-Pb dating shows that this adakitic rhyolite records a long ( 70 Myrs) and complicated period of magmatism with concordant 206Pb/238U ages from 193 Ma to 117 Ma. The enriched bulk rock Sr-Nd isotopic compositions of the Xintaimen adakitic rhyolite, as well as the enriched zircon Hf and O isotopic compositions, indicate that the magmas parental to the adakitic rhyolite were derived from partial melting of the Paleoproterozoic mafic lower crust, heated by mafic melts derived from the mantle during the paleo-Pacific plate subduction. A minor older basement component is indicated by the presence of captured Neoarchean to Early Paleoproterozoic zircons. The Mesozoic zircons have restricted Hf and O isotopic compositions irrespective of their ages, suggesting that they formed from similar sources at similar melting conditions. The Xintaimen adakitic rhyolite offers an independent line of evidence that the ancient lower crust of eastern China underwent a long period ( 70 Myrs) of destruction, melting or remelting, from 193 to 120 Ma, related to the subduction of the paleo-Pacific plate beneath eastern China.

Fundamentals of diagnostic ultrasonography.

PubMed

Noce, J P

1990-01-01

Diagnostic ultrasonography uses acoustical waves in the frequency range of 1 to 20 MHz. These waves obey Snell's law of reflection and refraction, which are rules ordinary to wave behavior. In ultrasound, the analogy to momentum is acoustic impedance. The acoustic impedance, Z, is equal to the density, p, times velocity, v. The ultrasound transducer converts electrical energy into ultrasound energy and vice versa. The transducer usually consists of a piezoelectric crystal composed of such ceramic materials as barium titanate, lead titanate, zirconate, or lead metaniobate. Five basic ultrasonic scanning modes play the major roles in clinical applications. A-mode, or amplitude-mode, scanning measures the tissue discontinuity along the scan axis. B-mode scanning produces a two-dimensional image of the tissue under study by combining A-mode signals from various directions through mechanical transducer scanning. M-mode, or time motion scanning, is an extension of the A-mode approach in which a single stationary transducer is used. The depth of the echo is displayed on the vertical axis; the brightness of the oscilloscope display is modulated by the echo amplitude. Real-time scanning, or rapid B-scanning, techniques provide continuous data acquisition at a rate sufficient to give the impression of the instantaneous motion of moving structures. Doppler scanning relies on the presence of motion. The Doppler effect occurs when there is relative motion between the source of sound and the receiver of the sound, causing a change in the detected frequency of the sound source.

Co-doping of (Bi(0.5)Na(0.5))TiO(3): secondary phase formation and lattice site preference of Co.

PubMed

Schmitt, V; Staab, T E M

2012-11-14

Bismuth sodium titanate (Bi(0.5)Na(0.5))TiO(3) (BNT) is considered to be one of the most promising lead-free alternatives to piezoelectric lead zirconate titanate (PZT). However, the effect of dopants on the material has so far received little attention from an atomic point of view. In this study we investigated the effects of cobalt-doping on the formation of additional phases and determined the preferred lattice site of cobalt in BNT. The latter was achieved by comparing the measured x-ray absorption near-edge structure (XANES) spectra to numerically calculated spectra of cobalt on various lattice sites in BNT. (Bi(0.5)Na(0.5))TiO(3) + x mol% Co (x = 0.0, 0.5, 1.0, 2.6) was synthesized via solid state reaction. As revealed by SEM backscattering images, a secondary phase formed in all doped specimens. Using both XRD and SEM-EDX, it was identified as Co(2)TiO(4) for dopant levels >0.5 mol%. In addition, a certain amount of cobalt was incorporated into BNT, as shown by electron probe microanalysis. This amount increased with increasing dopant levels, suggesting that an equilibrium forms together with the secondary phase. The XANES experiments revealed that cobalt occupies the octahedral B-site in the BNT perovskite lattice, substituting Ti and promoting the formation of oxygen vacancies in the material.

Analytic Theory of Titans Schumann Resonance: Constraints on Ionospheric Conductivity and Buried Water Ocean

NASA Technical Reports Server (NTRS)

Beghin, Christian; Randriamboarison, Orelien; Hamelin, Michel; Karkoschka, Erich; Sotin, Christophe; Whitten, Robert C.; Berthelier, Jean-Jacques; Grard, Rejean; Simoes, Fernando

2013-01-01

This study presents an approximate model for the atypical Schumann resonance in Titan's atmosphere that accounts for the observations of electromagnetic waves and the measurements of atmospheric conductivity performed with the Huygens Atmospheric Structure and Permittivity, Wave and Altimetry (HASI-PWA) instrumentation during the descent of the Huygens Probe through Titan's atmosphere in January 2005. After many years of thorough analyses of the collected data, several arguments enable us to claim that the Extremely Low Frequency (ELF) wave observed at around 36 Hz displays all the characteristics of the second harmonic of a Schumann resonance. On Earth, this phenomenon is well known to be triggered by lightning activity. Given the lack of evidence of any thunderstorm activity on Titan, we proposed in early works a model based on an alternative powering mechanism involving the electric current sheets induced in Titan's ionosphere by the Saturn's magnetospheric plasma flow. The present study is a further step in improving the initial model and corroborating our preliminary assessments. We first develop an analytic theory of the guided modes that appear to be the most suitable for sustaining Schumann resonances in Titan's atmosphere. We then introduce the characteristics of the Huygens electric field measurements in the equations, in order to constrain the physical parameters of the resonating cavity. The latter is assumed to be made of different structures distributed between an upper boundary, presumably made of a succession of thin ionized layers of stratospheric aerosols spread up to 150 km and a lower quasi-perfect conductive surface hidden beneath the non-conductive ground. The inner reflecting boundary is proposed to be a buried water-ammonia ocean lying at a likely depth of 55-80 km below a dielectric icy crust. Such estimate is found to comply with models suggesting that the internal heat could be transferred upwards by thermal conduction of the crust, while convective processes cannot be ruled out.

Losses in Ferroelectric Materials

PubMed Central

Liu, Gang; Zhang, Shujun; Jiang, Wenhua; Cao, Wenwu

2015-01-01

Ferroelectric materials are the best dielectric and piezoelectric materials known today. Since the discovery of barium titanate in the 1940s, lead zirconate titanate ceramics in the 1950s and relaxor-PT single crystals (such as lead magnesium niobate-lead titanate and lead zinc niobate-lead titanate) in the 1980s and 1990s, perovskite ferroelectric materials have been the dominating piezoelectric materials for electromechanical devices, and are widely used in sensors, actuators and ultrasonic transducers. Energy losses (or energy dissipation) in ferroelectrics are one of the most critical issues for high power devices, such as therapeutic ultrasonic transducers, large displacement actuators, SONAR projectors, and high frequency medical imaging transducers. The losses of ferroelectric materials have three distinct types, i.e., elastic, piezoelectric and dielectric losses. People have been investigating the mechanisms of these losses and are trying hard to control and minimize them so as to reduce performance degradation in electromechanical devices. There are impressive progresses made in the past several decades on this topic, but some confusions still exist. Therefore, a systematic review to define related concepts and clear up confusions is urgently in need. With this objective in mind, we provide here a comprehensive review on the energy losses in ferroelectrics, including related mechanisms, characterization techniques and collections of published data on many ferroelectric materials to provide a useful resource for interested scientists and engineers to design electromechanical devices and to gain a global perspective on the complex physical phenomena involved. More importantly, based on the analysis of available information, we proposed a general theoretical model to describe the inherent relationships among elastic, dielectric, piezoelectric and mechanical losses. For multi-domain ferroelectric single crystals and ceramics, intrinsic and extrinsic energy loss mechanisms are discussed in terms of compositions, crystal structures, temperature, domain configurations, domain sizes and grain boundaries. The intrinsic and extrinsic contributions to the total energy dissipation are quantified. In domain engineered ferroelectric single crystals and ceramics, polarization rotations, domain wall motions and mechanical wave scatterings at grain boundaries are believed to control the mechanical quality factors of piezoelectric resonators. We show that a thorough understanding on the kinetic processes is critical in analyzing energy loss behavior and other time-dependent properties in ferroelectric materials. At the end of the review, existing challenges in the study and control of losses in ferroelectric materials are analyzed, and future perspective in resolving these issues is discussed. PMID:25814784

Losses in Ferroelectric Materials.

PubMed

Liu, Gang; Zhang, Shujun; Jiang, Wenhua; Cao, Wenwu

2015-03-01

Ferroelectric materials are the best dielectric and piezoelectric materials known today. Since the discovery of barium titanate in the 1940s, lead zirconate titanate ceramics in the 1950s and relaxor-PT single crystals (such as lead magnesium niobate-lead titanate and lead zinc niobate-lead titanate) in the 1980s and 1990s, perovskite ferroelectric materials have been the dominating piezoelectric materials for electromechanical devices, and are widely used in sensors, actuators and ultrasonic transducers. Energy losses (or energy dissipation) in ferroelectrics are one of the most critical issues for high power devices, such as therapeutic ultrasonic transducers, large displacement actuators, SONAR projectors, and high frequency medical imaging transducers. The losses of ferroelectric materials have three distinct types, i.e., elastic, piezoelectric and dielectric losses. People have been investigating the mechanisms of these losses and are trying hard to control and minimize them so as to reduce performance degradation in electromechanical devices. There are impressive progresses made in the past several decades on this topic, but some confusions still exist. Therefore, a systematic review to define related concepts and clear up confusions is urgently in need. With this objective in mind, we provide here a comprehensive review on the energy losses in ferroelectrics, including related mechanisms, characterization techniques and collections of published data on many ferroelectric materials to provide a useful resource for interested scientists and engineers to design electromechanical devices and to gain a global perspective on the complex physical phenomena involved. More importantly, based on the analysis of available information, we proposed a general theoretical model to describe the inherent relationships among elastic, dielectric, piezoelectric and mechanical losses. For multi-domain ferroelectric single crystals and ceramics, intrinsic and extrinsic energy loss mechanisms are discussed in terms of compositions, crystal structures, temperature, domain configurations, domain sizes and grain boundaries. The intrinsic and extrinsic contributions to the total energy dissipation are quantified. In domain engineered ferroelectric single crystals and ceramics, polarization rotations, domain wall motions and mechanical wave scatterings at grain boundaries are believed to control the mechanical quality factors of piezoelectric resonators. We show that a thorough understanding on the kinetic processes is critical in analyzing energy loss behavior and other time-dependent properties in ferroelectric materials. At the end of the review, existing challenges in the study and control of losses in ferroelectric materials are analyzed, and future perspective in resolving these issues is discussed.

U-Pb Geochronology of Devonian Granites in the Meguma Terrane of Nova Scotia, Canada: Evidence for Hotspot Melting of a Neoproterozoic Source.

PubMed

Keppie; Krogh

1999-09-01

U-Pb isotopic analyses of monazite and zircon from six granitic plutons in the Meguma Terrane yield nearly concordant ages of 373+/-3 Ma, interpreted as the time of intrusion. U-Pb analyses of euhedral zircons with thick rims overgrowing cores, which were abraded to remove all or most of the rim, plot on chords between 370+/-3 and 628+/-33 Ma (Larrys River and Halfway Cove plutons), 372+/-3 and approximately 660 Ma (Shelburne pluton), and 373+/-2 and approximately 732 Ma (Barrington Passage pluton). The upper intercepts are interpreted as the age of magma source, correlatives of which are present in the Avalon Composite Terrane to the north. This basement may be either in depositional or tectonic contact with the overlying Cambro-Ordovician Meguma Group. Other zircons in the granites are generally irregular-euhedral with thin rims, and most U-Pb isotopic analyses fall between two chords from 373-2040 and 373-2300 Ma, with a few lying outside this field. These zircons are probably derived from the country rock (Goldenville Formation), which a previous study has shown contains detrital zircons with concordant U-Pb ages of 3000, 2000, and 600 Ma, and numerous intermediate discordant ages. These new ages, along with published data, document a relatively short (5-10 m.yr.) but voluminous period of magmatism. This age is approximately synchronous with intrusion of mafic rocks and lamprophyre dikes and regional low-pressure metamorphism and was followed by rapid denudation of 5-12 km. These observations may be interpreted in terms of shallowly dipping subduction and overriding of a mantle plume that eventually penetrates through the subducting plate to melt the overriding continental plate. Subsequent northward migration of the plume could explain both the approximately 360 Ma magmatism in the Cobequid Highlands (Avalon Composite Terrane) and the mid-Carboniferous plume-related intrusions around the Magdalen Basin.

Direct Measurements of Surface Energy, Elastic Modulus and Interparticle Forces of Titan Aerosol Analog (`Tholin') Using Atomic Force Microscopy

NASA Astrophysics Data System (ADS)

Yu, X.; Horst, S. M.; He, C.; McGuiggan, P.; Bridges, N. T.

2017-12-01

To understand the origin of the dunes on Titan, it is important to investigate the material properties of the sand particles on Titan, which are mainly made of organics deposited from the atmosphere [1]. The organic sand may behave differently compared to the quartz/basaltic sand on terrestrial planets (Earth, Venus, Mars) in terms of interparticle forces. We measured the surface energy (through contact angle measurements) and elastic modulus (through Atomic Force Microscopy, AFM) of Titan aerosol analog (tholins) produced in our lab. Tholins may be compositionally similar to sand on Titan. We directly measured the interparticle forces between a tholin particle adhered to an AFM cantilver and tholin particles on a substrate. We also measured the properties of walnut shells, a typical material used in the Titan Wind Tunnel (TWT, [2, 3]). We find the surface energy of a tholin thin film is about 70.9 mN/m and its elastic modulus is about 3.5 GPa (similar to hard polymers like PMMA and polystyrene). We used the two measured material properties of tholin to calculate its interparticle cohesion assuming simple sphere-sphere geometry [4]. For two 20 µm particles, the theoretical cohesion force is about 6682 nN. Under dry nitrogen (RH<1%), the directly measured interparticle forces using AFM was approximately 4000 nN, which is smaller than theoretical predictions but still relatively strong under dry conditions. The interparticle cohesion between walnut shell particles is only 200 nN, which is much lower than between tholin particles. The key finding of this study is that the interparticle cohesion forces are much larger for tholins and presumably Titan sand particles than for terrestrial sand and materials used in the wind tunnel. This suggests we should increase the interparticle force in both analog experiments (TWT) and threshold models (e.g. [5]) to correctly translate the results to real Titan conditions. The strong cohesion of tholins may also inform us how the small aerosol particles ( 1 µm) in Titan's atmosphere are transformed into large sand particles ( 200 µm). References: [1] J. W. Barnes et al. Icarus, 195, 400, 2008. [2] D. M. Burr, et al. Nat., 517, 60, 2015. [3] X. Yu et al., Icarus, 297, 97, 2017. [4] K. L. Johnson et al., Proc. R. Soc. Lond., A 324, 301, 1971. [5] Y. Shao & H. Lu, J. Geophys. Res., 105, 22437, 2000.

Titan-Like Exoplanets: Variations in Geometric Albedo and Effective Transit Height with Haze Production Rate

NASA Technical Reports Server (NTRS)

Checlair, Jade; McKay, Christopher P.; Imanaka, Hiroshi

2016-01-01

Extensive studies characterizing Titan present an opportunity to study the atmospheric properties of Titan-like exoplanets. Using an existing model of Titan's atmospheric haze, we computed geometric albedo spectra and effective transit height spectra for six values of the haze production rate (zero haze to twice present) over a wide range of wavelengths (0.2-2 microns). In the geometric albedo spectra, the slope in the UV-visible changes from blue to red when varying the haze production rate values from zero to twice the current Titan value. This spectral feature is the most effective way to characterize the haze production rates. Methane absorption bands in the visible-NIR compete with the absorbing haze, being more prominent for smaller haze production rates. The effective transit heights probe a region of the atmosphere where the haze and gas are optically thin and that is thus not effectively probed by the geometric albedo. The effective transit height decreases smoothly with increasing wavelength, from 376 km to 123 km at 0.2 and 2 microns, respectively. When decreasing the haze production rate, the methane absorption bands become more prominent, and the effective transit height decreases with a steeper slope with increasing wavelength. The slope of the geometric albedo in the UV-visible increases smoothly with increasing haze production rate, while the slope of the effective transit height spectra is not sensitive to the haze production rate other than showing a sharp rise when the haze production rate increases from zero. We conclude that geometric albedo spectra provide the most sensitive indicator of the haze production rate and the background Rayleigh gas. Our results suggest that important and complementary information can be obtained from the geometric albedo and motivates improvements in the technology for direct imaging of nearby exoplanets.

Processing/structure/property Relationships of Barium Strontium Titanate Thin Films for Dynamic Random Access Memory Application.

NASA Astrophysics Data System (ADS)

Peng, Cheng-Jien

The purpose of this study is to see the application feasibility of barium strontium titanate (BST) thin films on ultra large scale integration (ULSI) dynamic random access memory (DRAM) capacitors through the understanding of the relationships among processing, structure and electrical properties. Thin films of BST were deposited by multi-ion -beam reactive sputtering (MIBERS) technique and metallo -organic decomposition (MOD) method. The processing parameters such as Ba/Sr ratio, substrate temperature, annealing temperature and time, film thickness and doping concentration were correlated with the structure and electric properties of the films. Some effects of secondary low-energy oxygen ion bombardment were also examined. Microstructures of BST thin films could be classified into two types: (a) Type I structures, with multi-grains through the film thickness, for amorphous as-grown films after high temperature annealing, and (b) columnar structure (Type II) which remained even after high temperature annealing, for well-crystallized films deposited at high substrate temperatures. Type I films showed Curie-von Schweidler response, while Type II films showed Debted type behavior. Type I behavior may be attributed to the presence of a high density of disordered grain boundaries. Two types of current -voltage characteristics could be seen in non-bombarded films depending on the chemistry of the films (doped or undoped) and substrate temperature during deposition. Only the MIBERS films doped with high donor concentration and deposited at high substrate temperature showed space-charge -limited conduction (SCLC) with discrete shallow traps embedded in trap-distributed background at high electric field. All other non-bombarded films, including MOD films, showed trap-distributed SCLC behavior with a slope of {~}7.5-10 due to the presence of grain boundaries through film thickness or traps induced by unavoidable acceptor impurities in the films. Donor-doping could significantly improve the time -dependent dielectric breakdown (TDDB) behavior of BST thin films, mostly likely due to the lower oxygen vacancy concentration resulted from donor-doping.

Flexoelectricity in barium strontium titanate thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kwon, Seol Ryung; Huang, Wenbin; Yuan, Fuh-Gwo

2014-10-06

Flexoelectricity, the linear coupling between the strain gradient and the induced electric polarization, has been intensively studied as an alternative to piezoelectricity. Especially, it is of interest to develop flexoelectric devices on micro/nano scales due to the inherent scaling effect of flexoelectric effect. Ba{sub 0.7}Sr{sub 0.3}TiO{sub 3} thin film with a thickness of 130 nm was fabricated on a silicon wafer using a RF magnetron sputtering process. The flexoelectric coefficients of the prepared thin films were determined experimentally. It was revealed that the thin films possessed a transverse flexoelectric coefficient of 24.5 μC/m at Curie temperature (∼28 °C) and 17.44 μC/m at 41 °C. Themore » measured flexoelectric coefficients are comparable to that of bulk BST ceramics, which are reported to be 10–100 μC/m. This result suggests that the flexoelectric thin film structures can be effectively used for micro/nano-sensing devices.« less

Formation and photopatterning of nanoporous titania thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, Oun-Ho; Cheng, Joy Y.; Kim, Hyun Suk

2007-06-04

Photopatternable nanoporous titania thin films were generated from mixtures of an organic diblock copolymer, poly(styrene-b-ethylene oxide) (PS-b-PEO), and an oligomeric titanate (OT) prepared from a chelated titanium isopropoxide. The PS-b-PEO templates well-defined microdomains in thin films of the mixtures, which upon thermal treatment at 450 deg. C, become nanopores in titania. Average pore size and porosity are controlled by the molecular weight and loading level of the PS-b-PEO, respectively. Patterns of nanoporous titania were created by selectively exposing UV light on the mixture films. The UV irradiation destroys the chelating bond and induces the cross-linking reaction of the OT. Subsequentmore » wet development followed by thermal treatment gives patterned nanoporous films of anatase phase titania.« less

Provenance of sediments from Sumatra, Indonesia

NASA Astrophysics Data System (ADS)

Liebermann, Christof; Hall, Robert; Gough, Amy

2017-04-01

The island of Sumatra is situated at the south-western margin of the Indonesian archipelago. Sumatra is affected by active continental margin volcanism along the Sunda Trench, west of Sumatra as a result of active northeast subduction of the Indian plate under the Eurasian plate. Exposures of the Palaeozoic meta-sedimentary basement are mainly limited in extent to the northeast-southwest trending Barisan Mountain chain. The younger Cenozoic rocks are widespread across Sumatra, but can be grouped into structurally subdivided 'fore-arc', 'intramontane', and 'back-arc' basins. However, the formation of the basins pre-dates the current magmatic arc, thus a classical arc-related generation model can not be applied. The Cenozoic formations are well studied due to hydrocarbon enrichment, but little is known about their provenance history. A comprehensive sedimentary provenance study of the Cenozoic formations can aid in the wider understanding of Sumatran petroleum plays, can contribute to palaeographic reconstruction of western SE Asia, and might help to simplify the overall stratigraphy of Sumatra. This work represents a multi-proxy provenance study of sedimentary rocks from the main Cenozoic basins of Sumatra, alongside sediment from present-day river systems. The project refines the provenance in two ways: first, by studying the heavy mineral assemblages of the targeted formations, and secondly, by U-Pb detrital zircon dating using LA-ICP-MS to identify the age-range of the potential sediment sources. Preliminary U-Pb zircon age-data of >1500 concordant grains (10% discordant cut-off), heavy mineral compositions, and thin section analysis from two fieldwork seasons indicate a mixed provenance model, with a proximal igneous source, and mature basement rocks. An increase of the proximal signature in Lower-Miocene strata indicated by the occurrence of unstable heavy mineral phases such as apatite, and clinopyroxene suggests a major change of the source at the Oligocene-Miocene boundary. This can be interpreted as a pulse in the uplift of the Barisan Mountains. The presence of volcanic quartz in thin section supports this hypothesis. On the contrary, older sedimentary strata are characterised by ultra-stable heavy minerals such as zircon, tourmaline, and rutile; the presence of garnet in both pre-, and post-uplift affected strata indicates a contribution from metamorphic basement rocks, either from the local Sumatran basement or the Malay-Peninsula. Detrital zircon ages as old as Archean are present in all sedimentary formations; a prominent Triassic age group can be correlated with the Main Range Province granitoids reported from the Malay-Peninsula. It is noteworthy that zircon age spectra from Sumatra lack some diagnostic age groups commonly found in central- and western SE Asia, such as Cretaceous ages, correlated with igneous rock in the Schwaner Mountains, SW Borneo. The analysis of modern river sands suggests that the current sedimentary fluvial systems are mainly sourced from the recent Barisan-related volcanic arc. Zircon age patterns of the modern river sands resemble the populations found in the sedimentary strata, whereas, the heavy mineral composition is highly diluted by the recent igneous sources.

Extensive crustal melting during craton destruction: Evidence from the Mesozoic magmatic suite of Junan, eastern North China Craton

NASA Astrophysics Data System (ADS)

Yang, Fan; Santosh, M.; Tang, Li

2018-05-01

The cratonic destruction associated with the Pacific plate subduction beneath the eastern North China Craton (NCC) shows a close relationship with the widespread magmatism during the Late Mesozoic. Here we investigate a suite of intrusive and extrusive magmatic rocks from the Junan region of the eastern NCC in order to evaluate the role of extensive crustal melting related to decratonization. We present petrological, geochemical, zircon U-Pb geochronological and Lu-Hf isotopic data to evaluate the petrogenesis, timing and tectonic significance of the Early Cretaceous magmatism. Zircon grains in the basalt from the extrusive suite of Junan show multiple populations with Neoproterozoic and Early Paleozoic xenocrystic grains ranging in age from 764 Ma to 495 Ma as well as Jurassic grains with an age range of 189-165 Ma. The dominant population of magmatic zircon grains in the syenite defines three major age peaks of 772 Ma, 132 Ma and 126 Ma. Zircons in the granitoids including alkali syenite, monzonite and granodiorite yield a tightly restricted age range of 124-130 Ma representing their emplacement ages. The Neoproterozoic (841-547 Ma) zircon grains from the basalt and the syenite possess εHf(t) values of -22.9 to -8.4 and from -18.8 to -17.3, respectively. The Early Paleozoic (523-494 Ma) zircons from the basalt and the syenite also show markedly negative εHf(t) values of -22.7 to -18.0. The dominant population of Early Cretaceous (134-121 Ma) zircon grains presented in all the samples also displays negative εHf(t) values range from -31.7 to -21.1, with TDM of 1653-2017 Ma and TDMC in the range of 2193-3187 Ma. Accordingly, the Lu-Hf data suggest that the parent magma was sourced through melting of Mesoarchean to Paleoproterozoic basement rocks. Geochemical data on the Junan magmatic suite display features similar to those associated with the arc magmatic rocks involving subduction-related components, with interaction of fluids and melts in the suprasubduction mantle wedge. From the data presented, we propose that the Late Mesozoic intrusive and extrusive suites of Junan represent extensive lower and middle crustal melting, possibly triggered by mantle upwelling during the back-arc spreading associated with the Pacific plate subduction beneath the NCC. Intense asthenospheric upwelling resulted in lithospheric thinning and partial delamination during the Early Cretaceous, marking one of the peak decratonization stages of the NCC.

Petrological and zircon evidence for the Early Cretaceous granulite-facies metamorphism in the Dabie orogen, China

NASA Astrophysics Data System (ADS)

Gao, Xiao-Ying; Zhang, Qiang-Qiang; Zheng, Yong-Fei; Chen, Yi-Xiang

2017-07-01

An integrated study of petrology, mineralogy, geochemistry, and geochronology was carried out for contemporaneous mafic granulite and diorite from the Dabie orogen. The results provide evidence for granulite-facies reworking of the ultrahigh-pressure (UHP) metamorphic rock in the collisional orogen. Most zircons from the granulite are new growth, and their U-Pb ages are clearly categorized into two groups at 122-127 Ma and 188 ± 2 Ma. Although these two groups of zircons show similarly steep HREE patterns and variably negative Eu anomalies, the younger group has much higher U, Th and REE contents and Th/U ratios, much lower εHf(t) values than the older group. This suggests their growth is associated with different types of dehydration reactions. The older zircon domains contain mineral inclusions of garnet + clinopyroxene ± quartz, indicating their growth through metamorphic reactions at high pressures. In contrast, the young zircon domains only contain a few quartz inclusions and the garnet-clinopyroxene-plagioclase-quartz barometry yields pressures of 4.9 to 12.5 kb. In addition, the clinopyroxene-garnet Fe-Mg exchange thermometry gives temperatures of 738-951 °C. Therefore, the young zircon domains would have grown through peritectic reaction at low to medium pressures. The younger granulite-facies metamorphic age is in agreement not only with the adjacent diorite at 125 ± 1 Ma in this study but also the voluminous emplacement of coeval mafic and felsic magmas in the Dabie orogen. Mineral separates from both mafic granulite and its adjacent diorite show uniformly lower δ18O values than normal mantle, similar to those for UHP eclogite-facies metaigneous rocks in the Dabie orogen. In combination with major-trace elements and zircon Lu-Hf isotope compositions, it is inferred that the protolith of mafic granulites shares with the source rock of diorites, both being a kind of mafic metasomatites at the slab-mantle interface in the continental subduction channel. The spatial and temporal distribution of Early Cretaceous granulite-facies metamorphic rocks in this region is associated with the bimodal magmatism within a short period of 120-130 Ma in the postcollisional stage. This provides a direct link in petrogenesis between the granulitic, migmatic and magmatic rocks in the collisional orogen to active continental rifting, whereby high heat flow was transferred from the asthenospheric mantle into the thinned orogenic lithosphere for partial melting.

1T1R Nonvolatile Memory with Al/TiO2/Au and Sol-Gel-Processed Insulator for Barium Zirconate Nickelate Gate in Pentacene Thin Film Transistor

PubMed Central

Lee, Ke-Jing; Chang, Yu-Chi; Lee, Cheng-Jung; Wang, Li-Wen; Wang, Yeong-Her

2017-01-01

A one-transistor and one-resistor (1T1R) architecture with a resistive random access memory (RRAM) cell connected to an organic thin-film transistor (OTFT) device is successfully demonstrated to avoid the cross-talk issues of only one RRAM cell. The OTFT device, which uses barium zirconate nickelate (BZN) as a dielectric layer, exhibits favorable electrical properties, such as a high field-effect mobility of 2.5 cm2/Vs, low threshold voltage of −2.8 V, and low leakage current of 10−12 A, for a driver in the 1T1R operation scheme. The 1T1R architecture with a TiO2-based RRAM cell connected with a BZN OTFT device indicates a low operation current (10 μA) and reliable data retention (over ten years). This favorable performance of the 1T1R device can be attributed to the additional barrier heights introduced by using Ni (II) acetylacetone as a substitute for acetylacetone, and the relatively low leakage current of a BZN dielectric layer. The proposed 1T1R device with low leakage current OTFT and excellent uniform resistance distribution of RRAM exhibits a good potential for use in practical low-power electronic applications. PMID:29232828

Infrared Spectra, Index of Refraction, and Optical Constants of Nitrile Ices Relevant to Titan's Atmosphere

NASA Technical Reports Server (NTRS)

Moore, Marla; Ferrante, Robert; Moore, William; Hudson, Reggie

2010-01-01

Spectra and optical constants of nitrite ices known or suspected to be in Titan's atmosphere are presented from 2.5 to 200 microns (4000 to 50 per cm ). These results are relevant to the ongoing modeling of Cassini CIRS observations of Titan's winter pole. Ices studied include: HCN, hydrogen cyanide; C2N2, cyanogen; CH3CN, acetonitrile; C 2H5CN, propionitrile; and HC3N, cyanoacetylene. For each of these molecules we report new measurements of the index of refraction, n, determined in both the amorphous- and crystallinephase at 670 nm. Spectra were measured and optical constants were calculated for each nitrite at a variety of temperatures including 20, 35, 50, 75, 95, and 110 K, in the amorphous- and crystalline-phase. This laboratory effort uses a dedicated FTIR spectrometer to record transmission spectra of thin-film ice samples. Laser interference is used to measure film thickness during condensation onto a transparent cold window attached to the tail section of a closed-cycle helium cryostat. Optical constants, real (n) and imaginary (k) refractive indices, are determined using Kramers-Kronig (K-K) analysis. Our calculation reproduces the complete spectrum, including all interference effects. Index of refraction measurements are made in a separate dedicated FTIR spectrometer where interference deposit fringes are measured using two 670 nm lasers at different angles to the ice substrate. A survey of these new measurements will be presented along with a discussion of their validation, errors, and application to Titan data.

Ore genesis and geodynamic setting of the Lianhuashan porphyry tungsten deposit, eastern Guangdong Province, SE China: constraints from muscovite 40Ar-39Ar and zircon U-Pb dating and Hf isotopes

NASA Astrophysics Data System (ADS)

Liu, Peng; Mao, Jingwen; Pirajno, Franco; Jia, Lihui; Zhang, Feng; Li, Yang

2017-12-01

The Lianhuashan deposit has long been regarded as a typical tungsten porphyry deposit, located in the eastern Guangdong Province, in the Southeastern Coastal Metallogenic Belt (SCMB). LA-MC-ICP-MS zircon U-Pb dating of the quartz porphyry yielded a weighted mean 206Pb/238U age of 137.3 ± 2.0 Ma, which is interpreted as the emplacement age of the quartz porphyry. Hydrothermal muscovite yielded a plateau 40Ar/39Ar age of 133.2 ± 0.9 Ma, which is consistent with the zircon U-Pb age, suggesting that the tungsten mineralization is genetically related to the quartz porphyry. Combined with previous studies, we suggest that there is a 145-135 Ma episode linking the granitic magmas with W-Sn ore systems in the SCMB. Zircon ɛHf (t) values of the quartz porphyry are in range of - 3.8 to 0.9, and the two-stage Hf model ages (TDM2) are 1.1-1.4 Ga, which is younger than the basement rocks in the Cathaysia Block (1.8-2.2 Ga), signifying that the quartz porphyry was predominantly derived from melting of Mesoproterozoic crust containing variable amounts of mantle components. In combination with the newly recognized coeval alkaline/bimodal magmatism and A-type granites in eastern Guangdong, we suggest that the 145-135 Ma W-Sn metallogenic event of the SCMB is related to a geodynamic setting of large-scale lithospheric extension and thinning, which can be ascribed to melting of the crust caused by mantle upwelling, triggered by the oblique subduction of the Izanagi plate.

Integration and High-Temperature Characterization of Ferroelectric Vanadium-Doped Bismuth Titanate Thin Films on Silicon Carbide

NASA Astrophysics Data System (ADS)

Ekström, Mattias; Khartsev, Sergiy; Östling, Mikael; Zetterling, Carl-Mikael

2017-07-01

4H-SiC electronics can operate at high temperature (HT), e.g., 300°C to 500°C, for extended times. Systems using sensors and amplifiers that operate at HT would benefit from microcontrollers which can also operate at HT. Microcontrollers require nonvolatile memory (NVM) for computer programs. In this work, we demonstrate the possibility of integrating ferroelectric vanadium-doped bismuth titanate (BiTV) thin films on 4H-SiC for HT memory applications, with BiTV ferroelectric capacitors providing memory functionality. Film deposition was achieved by laser ablation on Pt (111)/TiO2/4H-SiC substrates, with magnetron-sputtered Pt used as bottom electrode and thermally evaporated Au as upper contacts. Film characterization by x-ray diffraction analysis revealed predominately (117) orientation. P- E hysteresis loops measured at room temperature showed maximum 2 P r of 48 μC/cm2, large enough for wide read margins. P- E loops were measurable up to 450°C, with losses limiting measurements above 450°C. The phase-transition temperature was determined to be about 660°C from the discontinuity in dielectric permittivity, close to what is achieved for ceramics. These BiTV ferroelectric capacitors demonstrate potential for use in HT NVM applications for SiC digital electronics.

Electrodeposition of titania and barium titanate thin films for high dielectric applications

NASA Astrophysics Data System (ADS)

Roy, Biplab Kumar

In order to address the requirement of a low-temperature low-cost cost processing for depositing high dielectric constant ceramic films for applications in embedded capacitor and flexible electronics technology, two different chemical bath processes, namely, thermohydrolytic deposition (TD) and cathodic electrodeposition (ED) have been exploited to generate titania thin films. In thermohydrolytic deposition technique, titania films were generated from acidic aqueous solution of titanium chloride on F: SnO2 coated glass and Si substrates by temperature assisted hydrolysis mechanism. On the other hand, in cathodic electrodeposition, in-situ electro-generation of hydroxyl ions triggered a fast deposition of titania on conductive substrates such as copper and F: SnO2 coated glass from peroxotitanium solution at low temperatures (˜0°C). In both techniques, solution compositions affected the morphology and crystallinity of the films. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) techniques have been employed to perform such characterization. As both processes utilized water as solvent, the as-deposited films contained hydroxyl ligand or physically adsorbed water molecules in the titania layer. Besides that, electrodeposited films contained peroxotitanium bonds which were characterized by FTIR studies. Although as-electrodeposited titania films were X-ray amorphous, considerable crystallinity could be generated by heat treatment. The films obtained from both the processes showed v moderately high dielectric constant (ranging from 9-30 at 100 kHz) and high breakdown voltage (0.09-0.15 MV/cm) in electrical measurements. To further improve the dielectric constant, electrodeposited titania films were converted to barium titanate films in high pH barium ion containing solution at 80-90°C. The resultant film contained cubic crystalline barium titanate verified by XRD analysis. Simple low-temperature hydrothermal technique of conversion worked perfect for F:SnO2 coated glass substrates, but in this process, high pH precursor caused corrosion in copper substrates and deposition of copper oxide in the final films. To overcome this, an innovative technique, which incorporates an electrochemical protection of substrates by application of cathodic potential in addition to common hydrothermal conversion, has been adopted. Films generated by common hydrothermal technique on F:SnO 2/glass substrates and via electrochemical-hydrothermal technique on Cu substrates showed promising dielectric behavior. Apart from the experimental studies, this report also includes various thermodynamic studies related to hydrolysis and precipitation of titanium ion, protection of copper during titania deposition and barium titanate conversion. Gibbs free energy based model and speciation studies were used to understand supersaturation which is a controlling factor in thermohydrolytic deposition. Similar approaches were utilized to understand the possibilities of barium titanate formation at different Ba2+ concentrations with different pH conditions. Possibilities of atmospheric carbon dioxide incorporation to generate barium carbonate instead of barium titanate formation were also determined by mathematical calculations. Whenever relevant, results of such theoretical analysis were utilized to design the experiment or to explain the experimental observations.

Timing of metasomatism in a subcontinental mantle: evidence from zircon at Finero (Italy)

NASA Astrophysics Data System (ADS)

Badanina, I. Yu.; Malitch, K. N.

2012-04-01

The Finero phlogopite-peridotite represents a metasomatized residual mantle harzburgite, exposed at the base of the lower-crust section in the Ivrea Zone, Western Alps (Hartmann and Wedepohl 1993). It forms the core of a concentrically zoned sequence of internal layered gabbro, amphibole-rich peridotite and external gabbro. The phlogopite peridotite contains small-size chromitite bodies, with a suite of accessory minerals such as phlogopite, apatite, Ca-Mg carbonates, zirconolite, zircon, thorianite and uraninite, proposed to form during alkaline-carbonatitic metasomatism process within the mantle (Zaccarini et al. 2004). In this study, the combined application of a non-destructive technique to separate zircon from their host rocks (see details at http://www.natires.com) and in-situ analytical technique for compositional and isotopic analysis (SHRIMP-II at Russian Geological Research Institute, St. Petersburg) has provided new more detailed age constraints on the formation of chromitite and related metasomatic events within a mantle tectonite at Finero. Chromitite samples derived from the dump in the prospecting trenches of Rio Creves. In thin sections, zircon occurs as relatively large (up to 200 μm) grains characterized by subhedral to euhedral shapes. Separated grains of zircon form two distinct populations. Dominant zircon population is pale pink and characterized by different shapes (subhedral, subrounded or elongated). In cathodoluminescense, the main set of population is represented by complex grains, which show development of core-rim relationship (most likely recrystallized rim on a preserved core). Subordinate zircon grains are colourless. They are characterized by a smoky cathodoluminescense, with almost no internal pattern. Three main U-Pb age clusters have been recognized. The youngest age cluster, typical for subordinate colourless zircon population and rims in complex grains of dominant pale pink population, show two concordant 206Pb/238U ages (e.g., 208.6 ± 4.0 Ma, MSWD=2.0; P=0.16, n=8 and 194.9 ± 3.4 Ma, MSWD=0.45; P=0.50, n=3, respectively). Other age clusters are characterized by the cores and rims observed in composite grains. They yielded concordant 206Pb/238U ages of 288.3 ± 7.3 Ma (MSWD=3.3, n=6) and 248.6 ± 3.3 Ma (MSWD=0.13, P=0.72, n=8), respectively. Since the pioneering work of Exley et al. (1982), the complex metasomatic history at Finero has received much attention. New U-Pb results are consistent with the age range obtained for mantle rocks, the phlogopite peridotite (293 ± 13 Ma, Voshage et al. 1987) and chromitite (208 ± 2 Ma, Grieco et al. 2001). The former age estimate, based on a Rb-Sr whole-rock isochron for six phlogopite-bearing peridotites and one phlogopite pyroxenite, has been interpreted as time of K metasomatic enrichment of the harzburgite. This event has been coeval with the intrusion of alkaline ultramafic magmas into the deep crust of the Ivrea Zone during the late Carboniferous (287 ± 3 Ma, Garuti et al. 2001). The U-Pb age of 208±2 Ma for zircon at Alpe Polunia, attributed by Grieco et al. (2001) to one of the major metasomatic episodes, is corroborated by a subordinate subset of zircon grains at Rio Creves. The U-Pb zircon ages identified in this study thus show notable differences. Our U-Pb data do not concur with the assumption of a single metasomatic event during chromitite formation. In contrast, we suggest a prolonged formation and multistage evolution of zircon growth, as mirrored by multiple U-Pb ages. U-Pb results for zircons from two chromitite localities (Alpe Polunia and Rio Creves) place tight constraints on their different temporal evolution. We presume that Hf-isotope data of zircon and Os-isotope data of laurite, to be investigated in the future, will shed new light on the sources of materials involved in a subcontinental mantle at Finero. This investigation was supported by Uralian Branch of Russian Academy of Sciences (grant 12-P-5-1020).

Sputtered Modified Barium Titanate for Thin-Film Capacitor Applications.

PubMed

Reynolds, Glyn J; Kratzer, Martin; Dubs, Martin; Felzer, Heinz; Mamazza, Robert

2012-04-10

New apparatus and a new process for the sputter deposition of modified barium titanate thin-films were developed. Films were deposited at temperatures up to 900 °C from a Ba₀ .96 Ca 0. 04 Ti 0. 82 Zr 0. 18 O₃ (BCZTO) target directly onto Si, Ni and Pt surfaces and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Film texture and crystallinity were found to depend on both deposition temperature and substrate: above 600 °C, the as-deposited films consisted of well-facetted crystallites with the cubic perovskite structure. A strongly textured Pt (111) underlayer enhanced the (001) orientation of BCZTO films deposited at 900 °C, 10 mtorr pressure and 10% oxygen in argon. Similar films deposited onto a Pt (111) textured film at 700 °C and directly onto (100) Si wafers showed relatively larger (011) and diminished intensity (00ℓ) diffraction peaks. Sputter ambients containing oxygen caused the Ni underlayers to oxidize even at 700 °C: Raising the process temperature produced more diffraction peaks of NiO with increased intensities. Thin-film capacitors were fabricated using ~500 nm thick BCZTO dielectrics and both Pt and Ni top and bottom electrodes. Small signal capacitance measurements were carried out to determine capacitance and parallel resistance at low frequencies and from these data, the relative permittivity (e r ) and resistivity (r) of the dielectric films were calculated; values ranged from ~50 to >2,000, and from ~10⁴ to ~10 10 Ω∙cm, respectively.

Performance of magnetoelectric PZT/Ni multiferroic system for energy harvesting application

NASA Astrophysics Data System (ADS)

Gupta, Reema; Tomar, Monika; Kumar, Ashok; Gupta, Vinay

2017-03-01

Magnetoelectric (ME) coefficient of Lead Zirconium Titanate (PZT) thin films has been probed for possible energy harvesting applications. Single phase PZT thin films have been deposited on nickel substrate (PZT/Ni) using pulsed laser deposition (PLD) technique. The effect of PLD process parameters on the ME coupling coefficient in the prepared systems has been investigated. The as grown PZT films on Ni substrate were found to be polycrystalline with improved ferroelectric and ferromagnetic properties. The electrical switching behavior of the PZT thin films were verified using capacitance voltage measurements, where well defined butterfly loops were obtained. The ME coupling coefficient was estimated to be in the range of 94.5 V cm-1 Oe-1-130.5 V cm-1 Oe-1 for PZT/Ni system, which is large enough for harnessing electromagnetic energy for subsequent applications.

Dielectric properties of inorganic fillers filled epoxy thin film

NASA Astrophysics Data System (ADS)

Norshamira, A.; Mariatti, M.

2015-07-01

The demand on the small size and high performance electronics has driven changes in the electronic packaging requirements from discrete capacitor to embedded capacitor. Embedded capacitor can improve electrical performance compared with discrete capacitor. This study aimed to achieve high dielectric of epoxy thin film composite that were targeted for application as embedded capacitor. In this study, inorganic fillers such as Calcium Copper Titanate (CCTO), Iron(III) Oxide (Fe2O3) and Titanium Dioxide (TiO2) were loaded in epoxy system at 5 and 20vol%. Morphology and dielectric properties were investigated to identify the effect of fillers loading and types of fillers on the properties of epoxy thin film composite. Based on the study, CCTO with 20vol% loading was found to have good dielectric properties compared to other type of fillers.

Record of Hybridization Preserved in Zircon, Aztec Wash Pluton, NV

NASA Astrophysics Data System (ADS)

Bromley, S. A.; Miller, C. F.; Claiborne, L. L.; Wooden, J. L.; Mazdab, F. K.

2007-12-01

The mid-Miocene Aztec Wash pluton comprises a smaller granite zone and a larger, highly heterogeneous zone in which evidence for interaction between basaltic and granitic magmas is ubiquitous. Granitic rocks in both zones show textural and compositional evidence for crystal accumulation and melt fractionation. In the heterogeneous zone, basalts have chilled, crenulate margins against granitic rocks, and there is widespread evidence for mechanical contamination of each lithology (coarse resorbed alkali feldspar in fine-grained mafic rock; mafic enclaves in granite). "Grey rocks" of intermediate composition are exposed on dm to 100's of m-scale as enclaves, pods, and initially subhorizontal sheets. They are variable texturally, but most are dominantly fine- grained and equigranular. Textures of grey rocks are consistent with rapid solidification from melt-rich magma, and, in combination with isotopic compositions intermediate between felsic and mafic rocks of the pluton, suggest an origin by near-complete homogenization of a hybrid melt (Bleick et al. 2005; Ericksen 2005). The elemental chemistry of zircon preserves information about the evolving magmatic environment in which it was hosted (Claiborne et al., 2006). Owing to its slow dissolution rate, it has the potential to survive periods of undersaturation with only partial resorption. Thus, it may record drastic shifts in T and melt chemistry that would accompany mafic-felsic hybridization. We are investigating zircon zoning patterns by cathodoluminescence (CL) and elemental compositions by SHRIMP-RG to evaluate the record of processes that they preserve. Temperatures of zircon growth are estimated using Ti-in-zircon thermometry (Watson et al. 2006), assuming a(TiO2) of ca. 0.7 (sphene +/-ilmenite are ubiquitous). Zircons from the granite zone yield estimated T's of 700-860 C, whereas those from grey rocks range from 710- 910 C. While both granite and grey zircon populations show dramatic T variations among and within grains, fluctuation tends to be more common and extreme in grains from the grey rocks, where variations exceed 100°C. Such grains appear to have both survived and recorded a substantial heating event, as would be expected if either mixing or thorough mingling occurred. Zircons from the granitic samples almost invariably have euhedral, concentric, oscillatory zoning; some have truncations in zoning indicating resorption, and many have thin, CL-dark rims. Grey rock zircons typically display thick, concentric zoning or, less commonly, banding, are rarely oscillatory zoned, and many exhibit indistinct or anhedral internal zoning (corresponding to high calculated T). Many have thick CL-bright rims and resorbed surfaces. These rims apparently represent relatively cool (less than 800 C) late stage growth following the heating event recorded in grain interiors. In both granitic and grey samples, Hf (6500-13000 ppm) shows a strong negative correlation with calculated T. In all granite samples, U (100-3000 ppm) & Th (150-3500 ppm) concentrations likewise show a strong negative correlation with calculated T, indicating that both acted as incompatible elements in these magmas. U (50-2000 ppm) & Th (50-2000 ppm) compositions show equally dramatic, but far less systematic, variation in grey samples, with high concentrations at elevated T. Growth of "hot" U, Th-rich zircon at Aztec Wash appears to be limited to the mixing environment.

Room temperature metastable monoclinic phase in BaTiO3 crystals

NASA Astrophysics Data System (ADS)

Lummen, Tom; Wang, Jianjun; Holt, Martin; Kumar, Amit; Vlahos, Eftihia; Denev, Sava; Chen, Long-Qing; Gopalan, Venkatraman

2011-03-01

Low-symmetry monoclinic phases in ferroelectric materials are of considerable interest, due to their associated enhanced electromechanical coupling. Such phases have been found in Pb-based perovskite solid solutions such as lead zirconate titanate (PZT), where they form structural bridges between the rhombohedral and tetragonal ground states in compositional space. In this work, we directly image such a monoclinic phase in BaTi O3 crystals at room-temperature, using optical second harmonic generation, Raman, and X-ray microscopic imaging techniques. Phase-field modeling indicates that ferroelectric domain microstructures in BaTi O3 induce local inhomogeneous stresses in the crystals, which can effectively trap the transient intermediate monoclinic structure that occurs across the thermal orthorhombic-tetragonal phase boundary. The induced metastable monoclinic domains are ferroelectrically soft, being easily moved by electric fields as low as 0.5 kV cm-1 . Stabilizing such intermediate low-symmetry phases could very well lead to Pb-free materials with enhanced piezoelectric properties.

Intraoral conversion of occlusal force to electricity and magnetism by biting of piezoelectric elements.

PubMed

Kameda, Takashi; Ohkuma, Kazuo; Sano, Natsuki; Ogura, Hideo; Terada, Kazuto

2012-01-01

Very weak electrical, magnetic and ultrasound signal stimulations are known to promote the formation, metabolism, restoration and stability of bone and surrounding tissues after treatment and operations. We have therefore investigated the possibility of intraoral generation of electricity and magnetism by occlusal force in an in vitro study. Biting bimorph piezoelectric elements with lead zirconate titanate (PZT) using dental models generated appropriate magnetism for bone formation, i. e. 0.5-0.6 gauss, and lower electric currents and higher voltages, i. e. 2.0-6.0 μA at 10-22 V (appropriate levels are 30 μA and 1.25 V), as observed by a universal testing machine. The electric currents and voltages could be changed using amplifier circuits. These results show that intraoral generation of electricity and magnetism is possible and could provide post-operative stabilization and activation of treated areas of bone and the surrounding tissues directly and/or indirectly by electrical, magnetic and ultrasound stimulation, which could accelerate healing.

Photoinduced charge carriers' accumulation and its impact on random lasing in Nd3+ doped (Pb,La)(Zr,Ti)O3 ceramics

NASA Astrophysics Data System (ADS)

Xu, Caixia; Zhang, Jingwen; Xu, Long; Ma, Xinyan; Zhao, Hua

2017-06-01

To pinpoint the driving forces behind the random lasing in Nd3+ doped lanthanum lead zirconate titanate (Nd:PLZT) ceramic plates, a combinatorial cavity with two gain media (Nd:YVO4 and Nd:PLZT) was used to study the switching feature between conventional lasing and random lasing oscillations. The complex laser output dynamics observed hinted that the photo-induced charge accumulation on the plate surface and the grain boundaries of Nd:PLZT is responsible for the lasing action switching, which was confirmed by a series of experiments, including strong electro-induced scattering, remarkable photoinduced currents, and light transmission reduction, along with measured single-pass-gain over the theoretical limit. It was found that the charge accumulation results in optical energy storage and nonuniform refractive index and hence strong scattering, which give rise to the random walks and weak localization of photons and long lasting lasing action and mode switching.

Enhanced stability of magnetoelectric gyrators under high power conditions

NASA Astrophysics Data System (ADS)

Leung, Chung Ming; Zhuang, Xin; Gao, Min; Tang, Xiao; Xu, Junran; Li, Jiefang; Zhang, Jitao; Srinivasan, G.; Viehland, D.

2017-10-01

In this study, three different coil-based magnetoelectric (ME) gyrators of different geometries, including gyrators with high power output, have been designed and characterized. These included two magnetostrictive/piezoelectric/magnetostrictive (M-P-M) and one piezoelectric/magnetostrictive/piezoelectric (P-M-P) type ME gyrators, which consisted of nickel zinc ferrite (NZFO) and lead zirconate titanate (PZT) ceramic plates. Compared with M-P-M ME gyrators, the P-M-P ones exhibited a higher power efficiency (η) of 85% when operated at resonance under an optimal magnetic bias field (HBias) of 40 Oe at low power conditions. It retained a relatively high efficiency of η = 79% under a high input power density of 2.87 W/cm3. A low reduction in the magnetomechanical coupling and mechanical quality (k33,m and Qm) factors of the NZFO ferrite layer in the ME gyrator explains the resilience of the P-M-P type structure with increasing power drive. The findings open the possibility of using ME gyrators in high power applications.

Effect of trivalent iron substitution on structure and properties of PLZT ceramics

NASA Astrophysics Data System (ADS)

Dutta, S.; Choudhary, R. N. P.

2008-02-01

Polycrystalline samples of Fe-modified PLZT (lead lanthanum zirconate titanate) are prepared by a mixed-oxide reaction technique. The formation of the compound has been confirmed by X-ray powder diffraction studies. The unit cell structure of the material has been found to be rhombohedral. Fourier-transform infrared reflection (FTIR) spectra have been recorded to correspond the structural changes associated with the phase formation. The effects of Fe concentration on the microstructure and dielectric constant of PLZT materials have been investigated. The ferroelectric phase transition of PLFZT materials is studied using dielectric measurements, which shows a shift in the transition temperature towards the higher-temperature side with increased Fe ion concentration. The piezoelectric constants of this system are investigated by the same way of changed contents of Fe ion in the main PLZT compound. The optimum values of Qm, kp, and d33 are 73, 0.32 and 406. The electrical conductivity increases with the increase in Fe ion concentration.

The contribution of 180° domain wall motion to dielectric properties quantified from in situ X-ray diffraction

DOE PAGES

Fancher, C. M.; Brewer, S.; Chung, C. C.; ...

2016-12-27

Here, the contribution of 180° domain wall motion to polarization and dielectric properties of ferroelectric materials has yet to be determined experimentally. In this paper, an approach for estimating the extent of (180°) domain reversal during application of electric fields is presented. We demonstrate this method by determining the contribution of domain reversal to polarization in soft lead zirconate titanate during application of strong electric fields. At the maximum applied field, domain reversal was determined to account for >80% of the measured macroscopic polarization. We also apply the method to quantify the contribution of domain reversal to the weak-field dielectricmore » permittivity of BaTiO 3. The results of this analysis determined that domain reversal accounts for up to ~70% of the macroscopic dielectric permittivity in BaTiO 3. These results demonstrate the predominance of domain reversal to high and low-field dielectric response in ferroelectric polycrystalline materials.« less

Development of a thick film PZT foil sensor for use in structural health monitoring applications.

PubMed

Pickwell, Andrew J; Dorey, Robert A; Mba, David

2013-02-01

Acoustic emission (AE) monitoring is a technique of growing interest in the field of nondestructive testing (NDT). The use of AE devices to monitor the health of structural components is currently limited by the cost of AE equipment, which prohibits the permanent placement of AE devices on structures for the purposes of continuous monitoring and the monitoring of areas with limited access. Micro electromechanical systems (MEMS) can provide solutions to these problems. We present the manufacture of a 4.4-μm-thick lead zirconate titanate (PZT) film on a 110-μm-thick titanium foil substrate for use as an AE sensor. The thick-film sensor is benchmarked against commercially available AE sensors in static and dynamic monitoring applications. The thick-film AE device is found to perform well in the detection of AE in static applications. A low signal-to-noise ratio is found to prohibit the detection of AE in a dynamic application.

Enhanced photoluminescence intensity by modifying the surface nanostructure of Nd3+-doped (Pb, La)(Zr, Ti)O3 ceramics.

PubMed

Xu, Long; Zhang, Jingwen; Zhao, Hua; Sun, Haibin; Xu, Caixia

2017-09-01

Quasi-period cylindrical nanostructures with both diameters and intervals of about 100 nm are manufactured on the surfaces of Nd 3+ -doped lanthanum lead zirconate titanate ceramics by femtosecond laser irradiation under SF 6 atmosphere. A light-emission enhancement of more than 20 times is investigated, accompanied by an extremely long trailing-off time of light emission and lower threshold. A specific polarization state of the light emission is achieved and tuned by changing the incident regions of the pumping source. The increased absorption coefficient of the specimen is discussed based on multiple scattering and weak localization of light. In addition, both the scatterers provided by the laser-machined nanostructure and the recurrent photoinduced trapping and re-excitation process participated in the enhancement of the light emission. This Letter offers new insight to improve the luminescence property of laser materials, as well as to broaden the range of exploring the weak localization of light and random lasers.

Deterministic multi-step rotation of magnetic single-domain state in Nickel nanodisks using multiferroic magnetoelastic coupling

NASA Astrophysics Data System (ADS)

Sohn, Hyunmin; Liang, Cheng-yen; Nowakowski, Mark E.; Hwang, Yongha; Han, Seungoh; Bokor, Jeffrey; Carman, Gregory P.; Candler, Robert N.

2017-10-01

We demonstrate deterministic multi-step rotation of a magnetic single-domain (SD) state in Nickel nanodisks using the multiferroic magnetoelastic effect. Ferromagnetic Nickel nanodisks are fabricated on a piezoelectric Lead Zirconate Titanate (PZT) substrate, surrounded by patterned electrodes. With the application of a voltage between opposing electrode pairs, we generate anisotropic in-plane strains that reshape the magnetic energy landscape of the Nickel disks, reorienting magnetization toward a new easy axis. By applying a series of voltages sequentially to adjacent electrode pairs, circulating in-plane anisotropic strains are applied to the Nickel disks, deterministically rotating a SD state in the Nickel disks by increments of 45°. The rotation of the SD state is numerically predicted by a fully-coupled micromagnetic/elastodynamic finite element analysis (FEA) model, and the predictions are experimentally verified with magnetic force microscopy (MFM). This experimental result will provide a new pathway to develop energy efficient magnetic manipulation techniques at the nanoscale.

Piezoelectric Flexible LCP-PZT Composites for Sensor Applications at Elevated Temperatures

NASA Astrophysics Data System (ADS)

Tolvanen, Jarkko; Hannu, Jari; Juuti, Jari; Jantunen, Heli

2018-03-01

In this paper fabrication of piezoelectric ceramic-polymer composites is demonstrated via filament extrusion enabling cost-efficient large-scale production of highly bendable pressure sensors feasible for elevated temperatures. These composites are fabricated by utilizing environmentally resistant and stable liquid crystal polymer matrix with addition of lead zirconate titanate at loading levels of 30 vol%. These composites, of approximately 0.99 mm thick and length of > 50 cm, achieved excellent bendability with minimum bending radius of 6.6 cm. The maximum piezoelectric coefficients d33 and g33 of the composites were > 14 pC/N and > 108 mVm/N at pressure < 10 kPa. In all cases, the piezoelectric charge coefficient (d33) of the composites decreased as a function of pressure. Also, piezoelectric coefficient (d33) further decreased in the case of increased frequency press-release cycle sand pre-stress levels by approximately 37-50%. However, the obtained results provide tools for fabricating novel piezoelectric sensors in highly efficient way for environments with elevated temperatures.

Study of V-OTDR stability for dynamic strain measurement in piezoelectric vibration

NASA Astrophysics Data System (ADS)

Ren, Meiqi; Lu, Ping; Chen, Liang; Bao, Xiaoyi

2016-09-01

In a phase-sensitive optical-time domain reflectometry (Φ-OTDR) system, the challenge for dynamic strain measurement lies in large intensity fluctuations from trace to trace. The intensity fluctuation caused by stochastic characteristics of Rayleigh backscattering sets detection limit for the minimum strength of vibration measurement and causes the large measurement uncertainty. Thus, a trace-to-trace correlation coefficient is introduced to quantify intensity fluctuation of Φ-OTDR traces and stability of the sensor system theoretically and experimentally. A novel approach of measuring dynamic strain induced by various driving voltages of lead zirconate titanate (PZT) in Φ-OTDR is also demonstrated. Piezoelectric vibration signals are evaluated through analyzing peak values of fast Fourier transform spectra at the fundamental frequency and high-order harmonics based on Bessel functions. High trace-to-trace correlation coefficients varying from 0.824 to 0.967 among 100 measurements are obtained in experimental results, showing the good stability of our sensor system, as well as small uncertainty of measured peak values.

Biotemplated synthesis of PZT nanowires.

PubMed

Cung, Kellye; Han, Booyeon J; Nguyen, Thanh D; Mao, Sheng; Yeh, Yao-Wen; Xu, Shiyou; Naik, Rajesh R; Poirier, Gerald; Yao, Nan; Purohit, Prashant K; McAlpine, Michael C

2013-01-01

Piezoelectric nanowires are an important class of smart materials for next-generation applications including energy harvesting, robotic actuation, and bioMEMS. Lead zirconate titanate (PZT), in particular, has attracted significant attention, owing to its superior electromechanical conversion performance. Yet, the ability to synthesize crystalline PZT nanowires with well-controlled properties remains a challenge. Applications of common nanosynthesis methods to PZT are hampered by issues such as slow kinetics, lack of suitable catalysts, and harsh reaction conditions. Here we report a versatile biomimetic method, in which biotemplates are used to define PZT nanostructures, allowing for rational control over composition and crystallinity. Specifically, stoichiometric PZT nanowires were synthesized using both polysaccharide (alginate) and bacteriophage templates. The wires possessed measured piezoelectric constants of up to 132 pm/V after poling, among the highest reported for PZT nanomaterials. Further, integrated devices can generate up to 0.820 μW/cm(2) of power. These results suggest that biotemplated piezoelectric nanowires are attractive candidates for stimuli-responsive nanosensors, adaptive nanoactuators, and nanoscale energy harvesters.

Temperature Dependent Mechanical Property of PZT Film: An Investigation by Nanoindentation

PubMed Central

Li, Yingwei; Feng, Shangming; Wu, Wenping; Li, Faxin

2015-01-01

Load-depth curves of an unpoled Lead Zirconate Titanate (PZT) film composite as a function of temperature were measured by nanoindentation technique. Its reduce modulus and hardness were calculated by the typical Oliver-Pharr method. Then the true modulus and hardness of the PZT film were assessed by decoupling the influence of substrate using methods proposed by Zhou et al. and Korsunsky et al., respectively. Results show that the indentation depth and modulus increase, but the hardness decreases at elevated temperature. The increasing of indentation depth and the decreasing of hardness are thought to be caused by the decreasing of the critical stress needed to excite dislocation initiation at high temperature. The increasing of true modulus is attributed to the reducing of recoverable indentation depth induced by back-switched domains. The influence of residual stress on the indentation behavior of PZT film composite was also investigated by measuring its load-depth curves with pre-load strains. PMID:25768957

An investigation of vibration-induced protein desorption mechanism using a micromachined membrane and PZT plate.

PubMed

Yeh, Po Ying; Le, Yevgeniya; Kizhakkedathu, Jayachandran N; Chiao, Mu

2008-10-01

A micromachined vibrating membrane is used to remove adsorbed proteins on a surface. A lead zirconate titanate (PZT) composite (3 x 1 x 0.5 mm) is attached to a silicon membrane (2,000 x 500 x 3 microm) and vibrates in a flexural plate wave (FPW) mode with wavelength of 4,000/3 microm at a resonant frequency of 308 kHz. The surface charge on the membrane and fluid shear stress contribute in minimizing the protein adsorption on the SiO(2) surface. In vitro characterization shows that 57 +/- 10% of the adsorbed bovine serum albumin (BSA), 47 +/- 13% of the immunoglobulin G (IgG), and 55.3~59.2 +/- 8% of the proteins from blood plasma are effectively removed from the vibrating surface. A simulation study of the vibration-frequency spectrum and vibrating amplitude distribution matches well with the experimental data. Potentially, a microelectromechanical system (MEMS)-based vibrating membrane could be the tool to minimize biofouling of in vivo MEMS devices.

Enlarging photovoltaic effect: combination of classic photoelectric and ferroelectric photovoltaic effects

PubMed Central

Zhang, Jingjiao; Su, Xiaodong; Shen, Mingrong; Dai, Zhihua; Zhang, Lingjun; He, Xiyun; Cheng, Wenxiu; Cao, Mengyu; Zou, Guifu

2013-01-01

Converting light energy to electrical energy in photovoltaic devices relies on the photogenerated electrons and holes separated by the built-in potential in semiconductors. Photo-excited electrons in metal electrodes are usually not considered in this process. Here, we report an enhanced photovoltaic effect in the ferroelectric lanthanum-modified lead zirconate titanate (PLZT) by using low work function metals as the electrodes. We believe that electrons in the metal with low work function could be photo-emitted into PLZT and form the dominant photocurrent in our devices. Under AM1.5 (100 mW/cm2) illumination, the short-circuit current and open-circuit voltage of Mg/PLZT/ITO are about 150 and 2 times of those of Pt/PLZT/ITO, respectively. The photovoltaic response of PLZT capacitor was expanded from ultraviolet to visible spectra, and it may have important impact on design and fabrication of high performance photovoltaic devices based on ferroelectric materials. PMID:23811832

Electromechanical modelling for piezoelectric flextensional actuators

NASA Astrophysics Data System (ADS)

Liu, Jinghang; O'Connor, William J.; Ahearne, Eamonn; Byrne, Gerald

2014-02-01

The piezoelectric flextensional actuator investigated in this paper comprises three pre-stressed piezoceramic lead zirconate titanate (PZT) stacks and an external, flexure-hinged, mechanical amplifier configuration. An electromechanical model is used to relate the electrical and mechanical domains, comprising the PZT stacks and the flexure mechanism, with the dynamic characteristics of the latter represented by a multiple degree-of-freedom dynamic model. The Maxwell resistive capacitive model is used to describe the nonlinear relationship between charge and voltage within the PZT stacks. The actuator model parameters and the electromechanical couplings of the PZT stacks, which describe the energy transfer between the electrical and mechanical domains, are experimentally identified without disassembling the embedded piezoceramic stacks. To verify the electromechanical model, displacement and frequency experiments are performed. There was good agreement between modelled and experimental results, with less than 1.5% displacement error. This work outlines a general process by which other pre-stressed piezoelectric flextensional actuators can be characterized, modelled and identified in a non-destructive way.

Low temperature dielectric relaxation in ordinary perovskite ferroelectrics: enlightenment from high-energy x-ray diffraction

DOE PAGES

Ochoa, D. A.; Levit, R.; Fancher, C. M.; ...

2017-04-05

We report that ordinary ferroelectrics exhibit a second order phase transition that is characterized by a sharp peak in the dielectric permittivity at a frequency-independent temperature. Furthermore, these materials show a low temperature dielectric relaxation that appears to be a common behavior of perovskite systems. Tetragonal lead zirconate titanate is used here as a model system in order to explore the origin of such an anomaly, since there is no consensus about the physical phenomenon involved in it. Crystallographic and domain structure studies are performed from temperature dependent synchrotron x-ray diffraction measurement. Results indicate that the dielectric relaxation cannot bemore » associated with crystallographic or domain configuration changes. The relaxation process is then parameterized by using the Vogel–Fulcher–Tammann phenomenological equation. Finally, results allow us to hypothesize that the observed phenomenon is due to changes in the dynamic behavior of the ferroelectric domains related to the fluctuation of the local polarization.« less

Fabrication and Performance of Endoscopic Ultrasound Radial Arrays Based on PMN-PT Single Crystal/Epoxy 1-3 Composite

PubMed Central

Zhou, Dan; Cheung, Kwok Fung; Chen, Yan; Lau, Sien Ting; Zhou, Qifa; Shung, K. Kirk; Luo, Hao Su; Dai, Jiyan; Chan, Helen Lai Wa

2011-01-01

In this paper, 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 (PMN-PT) single crystal/epoxy 1–3 composite was used as the active material of the endoscopic ultrasonic radial array transducer, because this composite exhibited ultrahigh electromechanical coupling coefficient (kt = 0.81%), very low mechanical quality factor (Qm = 11) and relatively low acoustic impedance (Zt = 12 MRayls). A 6.91 MHz PMN-PT/epoxy 1–3 composite radial array transducer with 64 elements was tested in a pulse-echo response measurement. The −6-dB bandwidth of the composite array transducer was 102%, which was ~30% larger than that of traditional lead zirconate titanate array transducer. The two-way insertion loss was found to be −32.3 dB. The obtained results show that this broadband array transducer is promising for acquiring high-resolution endoscopic ultrasonic images in many clinical applications. PMID:21342833