Calcium and zirconium as texture modifiers during rolling and annealing of magnesium–zinc alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bohlen, Jan, E-mail: jan.bohlen@hzg.de; Wendt, Joachim; Nienaber, Maria

2015-03-15

Rolling experiments were carried out on a ternary Mg–Zn–Ca alloy and its modification with zirconium. Short time annealing of as-rolled sheets is used to reveal the microstructure and texture development. The texture of the as-rolled sheets can be characterised by basal pole figures with split peak towards the rolling direction (RD) and a broad transverse angular spread of basal planes towards the transverse direction (TD). During annealing the RD split peaks as well as orientations in the sheet plane vanish whereas the distribution of orientations tilted towards the TD remains. It is shown in EBSD measurements that during rolling bandsmore » of twin containing structures form. During subsequent annealing basal orientations close to the sheet plane vanish based on a grain nucleation and growth mechanism of recrystallisation. Orientations with tilt towards the TD remain in grains that do not undergo such a mechanism. The addition of Zr delays texture weakening. - Highlights: • Ca in Mg–Zn-alloys contributes to a significant texture weakening during rolling and annealing. • Grain nucleation and growth in structures consisting of twins explain a texture randomisation during annealing. • Grains with transverse tilt of basal planes preferentially do not undergo a grain nucleation and growth mechanism. • Zr delays the microstructure and texture development.« less

Characterization of deformation mechanisms in zirconium alloys: effect of temperature and irradiation

NASA Astrophysics Data System (ADS)

Long, Fei

Zirconium alloys have been widely used in the CANDU (CANada Deuterium Uranium) reactor as core structural materials. Alloy such as Zircaloy-2 has been used for calandria tubes; fuel cladding; the pressure tube is manufactured from alloy Zr-2.5Nb. During in-reactor service, these alloys are exposed to a high flux of fast neutron at elevated temperatures. It is important to understand the effect of temperature and irradiation on the deformation mechanism of zirconium alloys. Aiming to provide experimental guidance for future modeling predictions on the properties of zirconium alloys this thesis describes the result of an investigation of the change of slip and twinning modes in Zircaloy-2 and Zr-2.5Nb as a function of temperature and irradiation. The aim is to provide scientific fundamentals and experimental evidences for future industry modeling in processing technique design, and in-reactor property change prediction of zirconium components. In situ neutron diffraction mechanical tests carried out on alloy Zircaloy-2 at three temperatures: 100¢ªC, 300¢ªC, and 500¢ªC, and described in Chapter 3. The evolution of the lattice strain of individual grain families in the loading and Poisson's directions during deformation, which probes the operation of slip and twinning modes at different stress levels, are described. By using the same type of in situ neutron diffraction technique, tests on Zr-2.5Nb pressure tube material samples, in either the fast-neutron irradiated or un-irradiated condition, are reported in Chapter 4. In Chapter 5, the measurement of dislocation density by means of line profile analysis of neutron diffraction patterns, as well as TEM observations of the dislocation microstructural evolution, is described. In Chapter 6 a hot-rolled Zr-2.5Nb with a larger grain size compared with the pressure tubing was used to study the development of dislocation microstructures with increasing plastic strain. In Chapter 7, in situ loading of heavy ion irradiated hot-rolled Zr-2.5Nb alloy is described, providing evidence for the interaction between moving dislocations and irradiation induced loops. Chapter 8 gives the effect on the dislocation structure of different levels of compressive strains along two directions in the hot-rolled Zr-2.5Nb alloy. By using high resolution neutron diffraction and TEM observations, the evolution of type and dislocation densities, as well as changes of dislocation microstructure with plastic strain were characterized.

Study of twin-roll cast Aluminium alloys subjected to severe plastic deformation by equal channel angular pressing

NASA Astrophysics Data System (ADS)

Poková, M.; Cieslar, M.

2014-08-01

Aluminium alloys prepared by twin-roll casting method become widely used in industry applications. Their high solid solution supersaturation and finer grains ensure better mechanical properties when compared with the direct-chill cast ones. One of the possibilities how to enhance their thermal stability is the addition of zirconium. After heat treatment Al3Zr precipitates form and these pin moving grain boundaries when the material is exposed to higher temperatures. In the present work twin-roll cast aluminium alloys based on AA3003 with and without Zr addition were annealed for 8 hours at 450 °C to enable precipitation of Al3Zr phase. Afterwards they were subjected to severe plastic deformation by equal channel angular pressing, which led to the reduction of average grain size under 1 μm. During subsequent isochronal annealing recovery and recrystallization took place. These processes were monitored by microhardness measurements, light optical microscopy and in-situ transmission electron microscopy. The addition of Zr stabilizes the grain size and increases the recrystallization temperature by 100 °C.

Thermodynamic Analysis and Growth of Zirconium Carbide by Chemical Vapor Deposition

NASA Astrophysics Data System (ADS)

Wei, Sun; Hua, Hao Zheng; Xiang, Xiong

Equilibrium calculations were used to optimize conditions for the chemical vapor deposition of zirconium carbide from zirconium halide + CxHy+H2+Ar system. The results show the CVD-ZrC phase diagram is divided into ZrC+C, ZrC and ZrC+Zr zones by C, Zr generating lines. For the same mole of ZrCl4 reactant, it needs higher concentration of CH4 to generate single ZrC phase than that of C3H6. Using these calculations as a guide, single-phase cubic zirconium carbide coatings were deposited onto graphite substrate.

Effects of heat treatment on U-Mo fuel foils with a zirconium diffusion barrier

NASA Astrophysics Data System (ADS)

Jue, Jan-Fong; Trowbridge, Tammy L.; Breckenridge, Cynthia R.; Moore, Glenn A.; Meyer, Mitchell K.; Keiser, Dennis D.

2015-05-01

A monolith fuel design based on U-Mo alloy has been selected as the fuel type for conversion of the United States' high performance research reactors (HPRRs) from highly enriched uranium (HEU) to low-enriched uranium (LEU). In this fuel design, a thin layer of zirconium is used to eliminate the direct interaction between the U-Mo fuel meat and the aluminum-alloy cladding during irradiation. The co-rolling process used to bond the Zr barrier layer to the U-Mo foil during fabrication alters the microstructure of both the U-10Mo fuel meat and the U-Mo/Zr interface. This work studied the effects of post-rolling annealing treatment on the microstructure of the co-rolled U-Mo fuel meat and the U-Mo/Zr interaction layer. Microscopic characterization shows that the grain size of U-Mo fuel meat increases with the annealing temperature, as expected. The grain sizes were ∼9, ∼13, and ∼20 μm for annealing temperature of 650, 750, and 850 °C, respectively. No abnormal grain growth was observed. The U-Mo/Zr interaction-layer thickness increased with the annealing temperature with an Arrhenius constant for growth of 184 kJ/mole, consistent with a previous diffusion-couple study. The interaction layer thickness was 3.2 ± 0.5 μm, 11.1 ± 2.1 μm, 27.1 ± 0.9 μm for annealing temperature of 650, 750, to 850 °C, respectively. The homogeneity of Mo improves with post rolling annealing temperature and with U-Mo coupon homogenization. The phases in the Zr/U-Mo interaction layer produced by co-rolling, however, differ from those reported in the previous diffusion couple studies.

Effects of heat treatment on U–Mo fuel foils with a zirconium diffusion barrier

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jue, Jan-Fong; Trowbridge, Tammy L.; Breckenridge, Cynthia R.

A monolith fuel design based on U–Mo alloy has been selected as the fuel type for conversion of the United States’ high performance research reactors (HPRRs) from highly enriched uranium (HEU) to low-enriched uranium (LEU). In this fuel design, a thin layer of zirconium is used to eliminate the direct interaction between the U–Mo fuel meat and the aluminum-alloy cladding during irradiation. The co-rolling process used to bond the Zr barrier layer to the U–Mo foil during fabrication alters the microstructure of both the U–10Mo fuel meat and the U–Mo/Zr interface. This work studied the effects of post-rolling annealing treatmentmore » on the microstructure of the co-rolled U–Mo fuel meat and the U–Mo/Zr interaction layer. Microscopic characterization shows that the grain size of U–Mo fuel meat increases with the annealing temperature, as expected. The grain sizes were ~9, ~13, and ~20 μm for annealing temperature of 650, 750, and 850 °C, respectively. No abnormal grain growth was observed. The U–Mo/Zr interaction-layer thickness increased with the annealing temperature with an Arrhenius constant for growth of 184 kJ/mole, consistent with a previous diffusion-couple study. The interaction layer thickness was 3.2 ± 0.5 μm, 11.1 ± 2.1 μm, 27.1 ± 0.9 μm for annealing temperature of 650, 750, to 850 °C, respectively. The homogeneity of Mo improves with post rolling annealing temperature and with U–Mo coupon homogenization. The phases in the Zr/U–Mo interaction layer produced by co-rolling, however, differ from those reported in the previous diffusion couple studies.« less

Development in corrosion resistance by microstructural refinement in Zr-16 SS 304 alloy using suction casting technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Das, N., E-mail: nirupamd@barc.gov.in; Sengupta, P.; Abraham, G.

Highlights: • Grain refinement was made in Zr–16 wt.% SS alloy while prepared by suction casting process. • Distribution of Laves phase, e.g., Zr{sub 2}(Fe, Cr) was raised in suction cast (SC) Zr–16 wt.% SS. • Corrosion resistance was improved in SC alloy compared to that of arc-melt-cast alloy. • Grain refinement in SC alloy assisted for an increase in its corrosion resistance. - Abstract: Zirconium (Zr)-stainless steel (SS) hybrid alloys are being considered as baseline alloys for developing metallic-waste-form (MWF) with the motivation of disposing of Zr and SS base nuclear metallic wastes. Zr–16 wt.% SS, a MWF alloymore » optimized from previous studies, exhibit significant grain refinement and changes in phase assemblages (soft phase: Zr{sub 2}(Fe, Cr)/α-Zr vs. hard phase: Zr{sub 3}(Fe, Ni)) when prepared by suction casting (SC) technique in comparison to arc-cast-melt (AMC) route. Variation in Cr-distribution among different phases are found to be low in suction cast alloy, which along with grain refinement restricted Cr-depletion at the Zr{sub 2}(Fe, Cr)/Zr interfaces, prone to localized attack. Hence, SC alloy, compared to AMC alloy, showed lower current density, higher potential at the breakdown of passivity and higher corrosion potential during polarization experiments (carried out under possible geological repository environments, viz., pH 8, 5 and 1) indicating its superior corrosion resistance.« less

Microstructural analysis of biodegradable Mg-0.9Ca-1.2Zr alloy

NASA Astrophysics Data System (ADS)

Istrate, B.; Munteanu, C.; Geanta, V.; Baltatu, S.; Focsaneanu, S.; Earar, K.

2016-08-01

Magnesium alloys have applications in aerospace and medical applications as biodegradable orthopedic implants. Alloying with biocompatible elements, such as calcium or zirconium contribute to refining the the microstructure and improves corrosion resistance with the formation of an eutectic compound - Mg2Ca at boundary alpha-Mg grains. The purpose of this paper is to present the microstructure throw optical and scanning electron methods and phase and constituents identification with X-ray analysis. The results showed the presence of alpha-Mg grains with formation of a mechanical compound - Mg2Ca and appearance of alpha- Zr phase relatively uniformly distributed in nests.

Surface Modification of Solution-Processed ZrO2 Films through Double Coating for Pentacene Thin-Film Transistors

NASA Astrophysics Data System (ADS)

Kwon, Jin-Hyuk; Bae, Jin-Hyuk; Lee, Hyeonju; Park, Jaehoon

2018-03-01

We report the modification of surface properties of solution-processed zirconium oxide (ZrO2) dielectric films achieved by using double-coating process. It is proven that the surface properties of the ZrO2 film are modified through the double-coating process; the surface roughness decreases and the surface energy increases. The present surface modification of the ZrO2 film contributes to an increase in grain size of the pentacene film, thereby increasing the field-effect mobility and decreasing the threshold voltage of the pentacene thin-film transistors (TFTs) having the ZrO2 gate dielectric. Herein, the molecular orientation of pentacene film is also studied based on the results of contact angle and X-ray diffraction measurements. Pentacene molecules on the double-coated ZrO2 film are found to be more tilted than those on the single-coated ZrO2 film, which is attributed to the surface modification of the ZrO2 film. However, no significant differences are observed in insulating properties between the single-and the double-coated ZrO2 dielectric films. Consequently, the characteristic improvements of the pentacene TFTs with the double-coated ZrO2 gate dielectric film can be understood through the increase in pentacene grain size and the reduction in grain boundary density.

Effects of cobalt, boron, and zirconium on the microstructure of Udimet 738. M.S. Thesis. Final Report

NASA Technical Reports Server (NTRS)

Nakanishi, T. G.

1984-01-01

A structural study was carried out on Co modified Udimet 738 alloys containing 0.04, 0.10, and 0.20 wt % Zr at 0.01 and 0.03 wt % B levels. Samples in the as-cast and solution-treated conditions were exposed at 843 C to study structural stability. The structures produced by the interactions of Co, Zr, and B were studied by SEM, X-ray diffraction, and dispersive analysis techniques. The additions of large amounts of Zr and B were found to increase the solidification range of the U-738. Structural changes involved eutectic gamma prime islands, formation of low melting point compounds, and precipitation of borides and Zr rich phases. Boron and zirconium additions did not show substantial changes in mechanical properties. Removal of Co from the alloys resulted in reduction of the matrix solubility for carbon and increase in the gamma prime solvus. Structural instabilities found were continuous grain boundary M23C6 films, MC breakdown, and plate-like phases. Removal of cobalt resulted in a slight decrease in tensile and stress rupture properties. Detailed structural results presented.

Characterization of zirconium carbides using electron microscopy, optical anisotropy, Auger depth profiles, X-ray diffraction, and electron density calculated by charge flipping method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chinthaka Silva, G.W., E-mail: chinthaka.silva@gmail.com; Kercher, Andrew A., E-mail: rokparent@comcast.net; Hunn, John D., E-mail: hunnjd@ornl.gov

2012-10-15

Samples with five different zirconium carbide compositions (C/Zr molar ratio=0.84, 0.89, 0.95, 1.05, and 1.17) have been fabricated and studied using a variety of experimental techniques. Each sample was zone refined to ensure that the end product was polycrystalline with a grain size of 10-100 {mu}m. It was found that the lattice parameter was largest for the x=0.89 composition and smallest for the x=1.17 total C/Zr composition, but was not linear; this nonlinearity is possibly explained using electron densities calculated using charge flipping technique. Among the five samples, the unit cell of the ZrC{sub 0.89} sample showed the highest electronmore » density, corresponding to the highest carbon incorporation and the largest lattice parameter. The ZrC{sub 0.84} sample showed the lowest carbon incorporation, resulting in a larger number of carbon vacancies and resultant strain. Samples with larger carbon ratios (x=0.95, 1.05, and 1.17) showed a slight decrease in lattice parameter, due to a decrease in electron density. Optical anisotropy measurements suggest that these three samples contained significant amounts of a graphitic carbon phase, not bonded to the Zr atoms. - Graphical abstract: Characterization of zirconium carbides using electron microscopy, optical anisotropy, Auger depth profiles, X-ray diffraction, and electron density calculated by the charge flipping method. Highlights: Black-Right-Pointing-Pointer The lattice parameter variation: ZrC{sub 0.89}>ZrC{sub 0.84}>ZrC{sub 0.95}>ZrC{sub 1.05}>ZrC{sub 1.17}. Black-Right-Pointing-Pointer Surface oxygen with no correlation to the lattice parameter variation. Black-Right-Pointing-Pointer ZrC{sub 0.89} had highest electron densities correspond to highest carbon incorporation. Black-Right-Pointing-Pointer Second highest lattice parameter in ZrC{sub 0.84} due to strain. Black-Right-Pointing-Pointer Unit cell electron density order: ZrC{sub 0.95}>ZrC{sub 1.05}>ZrC{sub 1.17}.« less

Thermomechanical processing of aluminum micro-alloyed with Sc, Zr, Ti, B, and C

NASA Astrophysics Data System (ADS)

McNamara, Cameron T.

Critical exploration of the minimalistic high strength low alloy aluminum (HSLA-Al) paradigm is necessary for the continued development of advanced aluminum alloys. In this study, scandium (Sc) and zirconium (Zr) are examined as the main precipitation strengthening additions, while magnesium (Mg) is added to probe the synergistic effects of solution and precipitation hardening, as well as the grain refinement during solidification afforded by a moderate growth restriction factor. Further, pathways of recrystallization are explored in several potential HSLA-Al syste =ms sans Sc. Aluminum-titanium-boron (Al-Ti-B) and aluminum-titanium-carbon (Al-Ti-C) grain refining master alloys are added to a series of Al-Zr alloys to examine both the reported Zr poisoning effect on grain size reduction and the impact on recrystallization resistance through the use of electron backscattered diffraction (EBSD) imaging. Results include an analysis of active strengthening mechanisms and advisement for both constitution and thermomechanical processing of HSLA-Al alloys for wrought or near-net shape cast components. The mechanisms of recrystallization are discussed for alloys which contain a bimodal distribution of particles, some of which act as nucleation sites for grain formation during annealing and others which restrict the growth of the newly formed grains.

Calcification of MC3T3-E1 cells on titanium and zirconium.

PubMed

Umezawa, Takayuki; Chen, Peng; Tsutsumi, Yusuke; Doi, Hisashi; Ashida, Maki; Suzuki, Shoichi; Moriyama, Keiji; Hanawa, Takao

2015-01-01

To confirm similarity of hard tissue compatibility between titanium and zirconium, calcification of MC3T3-E1 cells on titanium and zirconium was evaluated in this study. Mirror-polished titanium (Ti) and zirconium (Zr) disks and zirconium-sputter deposited titanium (Zr/Ti) were employed in this study. The surface of specimens were characterized using scanning electron microscopy and X-ray diffraction. Then, the cellular proliferation, differentiation and calcification of MC3T3-E1 cells on specimens were investigated. The surface of Zr/Ti was much smoother and cleaner than those of Ti and Zr. The proliferation of the cell was the same among three specimens, while the differentiation and calcification on Zr/Ti were faster than those on Ti and Zr. Therefore, Ti and Zr showed the identical hard tissue compatibility according to the evaluation with MC3T3-E1 cells. Sputter deposition may improve cytocompatibility.

Zirconium doped TiO2 thin films deposited by chemical spray pyrolysis

NASA Astrophysics Data System (ADS)

Juma, A.; Oja Acik, I.; Oluwabi, A. T.; Mere, A.; Mikli, V.; Danilson, M.; Krunks, M.

2016-11-01

Chemical spray pyrolysis (CSP) is a flexible deposition technique that allows for mixing of the precursor solutions in different proportions suitable for doping thin films. The CSP method was used to dope TiO2 thin films with Zr by adding zirconium(IV) acetylacetonate into a solution of titanium(IV) isopropoxide in ethanol stabilized by acetylacetone at [Zr]/[Ti] of 0, 5, 10 and 20 at%. The Zr-doped TiO2 thin films were uniform and homogeneous showing much smaller grains than the undoped TiO2 films. Zr stabilized the anatase phase to temperatures above 800 °C depending on Zr concentration in the spray solution. The concentration of Zr determined by XPS was 6.4 at% for the thin film deposited from the 20 at% solution. According to AFM studies, Zr doping decreased the root mean square roughness of TiO2 film from 5.9 to 1.1 nm. An XRD study of samples with the highest Zr amount showed the ZrTiO4 phase started forming after annealing at 800 °C. The optical band gap for TiO2 decreased from 3.3 eV to 3.0 eV after annealing at 800 °C but for the TiO2:Zr(20) film it remained at 3.4 eV. The dielectric constant increased by more than four times with Zr-doping and this was associated with the change in the bond formations caused by substitution of Ti by Zr in the lattice.

Thermal Stabilization and Mechanical Properties of Nanocrystalline Iron-Nickel-Zirconium Alloys

NASA Astrophysics Data System (ADS)

Kotan, Hasan

Ultrafine grained and nanostructured materials are promising for structural applications because of the high strength compared to coarse grained counterparts. However, their widespread application is limited by an inherently high driving force for thermally induced grain growth, even at low temperatures. Accordingly, the understanding of and control over grain growth in nanoscale materials is of great technological and scientific importance as many physical properties (i.e. mechanical properties) are functions of the average grain size and the grain size distribution within the microstructure. Here, we investigate the microstructural evolution and grain growth in Fe-Ni alloys with Zr addition and differentiate the stabilization mechanisms acting on grain boundaries. Fe-Ni alloys are chosen for stability investigations since they are important for understanding the behavior of many steels and other ferrous alloys. Zirconium is proven to be an effective grain size stabilizer in pure Fe and Fe-base systems. In this study, nanocrystalline alloys were prepared by high energy ball milling. In situ and ex situ experiments were utilized to directly follow grain growth and microstructural evolution as a function of temperature and composition. The information obtained from these experiments enables the real time observation of microstructural evolution and phase transformation and provides a unique view of dynamic reactions as they occur. The knowledge of the thermal stability will exploit the potential high temperature applications and the consolidation conditions (i.e. temperature and pressure) to obtain high dense materials for advanced mechanical tests. Our investigations reveal that the grain growth of Fe-Ni alloys is not affected by Ni content but strongly inhibited by the addition of 1 at% Zr up to about 700 °C. The microstructural stability is lost due to the bcc-to-fcc transformation (occurring at 700°C) by the sudden appearance of abnormally grown fcc grains. However it was determined grain growth can be suppressed kinetically at higher temperatures for high Zr containing alloys by precipitation of intermetallic compounds. Eventually at high enough temperatures the retention of nanocrystallinity was lost, leaving behind fine micron grains filled with nanoscale intermetallic precipitates. Despite the loss of stability the in-situ formed precipitates were found to induce an Orowan hardening affect. The results from the mechanical tests show that Orowan particle strengthening can be as significant as Hall Petch hardening is at the smallest grain sizes.

Sintering behavior of U 80 at.%Zr powder compacts in a vacuum environment

NASA Astrophysics Data System (ADS)

Kim, Tae-Kyu; Lee, Chong-Tak; Sohn, Dong-Seong

2008-01-01

Sintering behavior of U-80 at.%Zr powder compacts in a temperature range from 1100 to 1500 °C in a vacuum of 1 × 10 -4 Pa was evaluated. The sintered density depended more on the sintering temperature than on the sintering time. The sintered specimens consisted of the δ-UZr 2 matrix with acicular α-Zr precipitates, but it still had un-reacted zirconium when the sintering temperature was 1100 °C. The uranium depletion near the surface of the specimens sintered at temperatures above 1300 °C was detected. Massive Zr(O) grains in the sintered specimen were found, and their formation was restrained when the cooling rate from the sintering temperature was increased.

Mesoporous Silica-Supported Amidozirconium-Catalyzed Carbonyl Hydroboration

DOE PAGES

Eedugurala, Naresh; Wang, Zhuoran; Chaudhary, Umesh; ...

2015-11-04

The hydroboration of aldehydes and ketones using a silica-supported zirconium catalyst is reported. Reaction of Zr(NMe 2) 4 and mesoporous silica nanoparticles (MSN) provides the catalytic material Zr(NMe 2) n@MSN. Exhaustive characterization of Zr(NMe 2) n@MSN with solid-state (SS)NMR and infrared spectroscopy, as well as through reactivity studies, suggests its surface structure is primarily ≡SiOZr(NMe 2) 3. The presence of these nitrogen-containing zirconium sites is supported by 15N NMR spectroscopy, including natural abundance 15N NMR measurements using dynamic nuclear polarization (DNP) SSNMR. The Zr(NMe 2) n@MSN material reacts with pinacolborane (HBpin) to provide Me 2NBpin and the material ZrH/Bpin@MSN thatmore » is composed of interacting surface-bonded zirconium hydride and surface-bonded borane ≡SiOBpin moieties in an approximately 1:1 ratio, as well as zirconium sites coordinated by dimethylamine. The ZrH/Bpin@MSN is characterized by 1H/ 2H and 11B SSNMR and infrared spectroscopy and through its reactivity with D 2. The zirconium hydride material or the zirconium amide precursor Zr(NMe 2) n@MSN catalyzes the selective hydroboration of aldehydes and ketones with HBpin in the presence of functional groups that are often reduced under hydroboration conditions or are sensitive to metal hydrides, including olefins, alkynes, nitro groups, halides, and ethers. Remarkably, this catalytic material may be recycled without loss of activity at least eight times, and air-exposed materials are catalytically active. These supported zirconium centers are robust catalytic sites for carbonyl reduction and that surface-supported, catalytically reactive zirconium hydride may be generated from zirconium-amide or zirconium alkoxide sites.« less

Mesoporous Silica-Supported Amidozirconium-Catalyzed Carbonyl Hydroboration

DOE Office of Scientific and Technical Information (OSTI.GOV)

Eedugurala, Naresh; Wang, Zhuoran; Chaudhary, Umesh

The hydroboration of aldehydes and ketones using a silica-supported zirconium catalyst is reported. Reaction of Zr(NMe 2) 4 and mesoporous silica nanoparticles (MSN) provides the catalytic material Zr(NMe 2) n@MSN. Exhaustive characterization of Zr(NMe 2) n@MSN with solid-state (SS)NMR and infrared spectroscopy, as well as through reactivity studies, suggests its surface structure is primarily ≡SiOZr(NMe 2) 3. The presence of these nitrogen-containing zirconium sites is supported by 15N NMR spectroscopy, including natural abundance 15N NMR measurements using dynamic nuclear polarization (DNP) SSNMR. The Zr(NMe 2) n@MSN material reacts with pinacolborane (HBpin) to provide Me 2NBpin and the material ZrH/Bpin@MSN thatmore » is composed of interacting surface-bonded zirconium hydride and surface-bonded borane ≡SiOBpin moieties in an approximately 1:1 ratio, as well as zirconium sites coordinated by dimethylamine. The ZrH/Bpin@MSN is characterized by 1H/ 2H and 11B SSNMR and infrared spectroscopy and through its reactivity with D 2. The zirconium hydride material or the zirconium amide precursor Zr(NMe 2) n@MSN catalyzes the selective hydroboration of aldehydes and ketones with HBpin in the presence of functional groups that are often reduced under hydroboration conditions or are sensitive to metal hydrides, including olefins, alkynes, nitro groups, halides, and ethers. Remarkably, this catalytic material may be recycled without loss of activity at least eight times, and air-exposed materials are catalytically active. These supported zirconium centers are robust catalytic sites for carbonyl reduction and that surface-supported, catalytically reactive zirconium hydride may be generated from zirconium-amide or zirconium alkoxide sites.« less

Scaling effects in sodium zirconium silicate phosphate (Na 1+ xZr 2Si xP 3- xO 12) ion-conducting thin films

DOE PAGES

Ihlefeld, Jon F.; Gurniak, Emily; Jones, Brad H.; ...

2016-05-04

Preparation of sodium zirconium silicate phosphate (NaSICon), Na 1+xZr 2Si xP 3–xO 12 (0.25 ≤ x ≤ 1.0), thin films has been investigated via a chemical solution approach on platinized silicon substrates. Increasing the silicon content resulted in a reduction in the crystallite size and a reduction in the measured ionic conductivity. Processing temperature was also found to affect microstructure and ionic conductivity with higher processing temperatures resulting in larger crystallite sizes and higher ionic conductivities. The highest room temperature sodium ion conductivity was measured for an x = 0.25 composition at 2.3 × 10 –5 S/cm. In conclusion, themore » decreasing ionic conductivity trends with increasing silicon content and decreasing processing temperature are consistent with grain boundary and defect scattering of conducting ions.« less

Microstructure evolution in the fusion zone of laser-welded Mg–Gd–Y–Zr alloy during solution and aging treatment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Lyuyuan

The microstructure evolution in the fusion zone of laser-welded Mg-Gd-Y-Zr alloy during solution and aging treatment is investigated. The morphology of the Mg{sub 24}(Gd,Y){sub 5} in the divorced eutectic at the grain boundary transforms from a continuous network to disconnected and fragmentized islands and then to spheroidal particles before complete dissolution during the solution treatment at 430 °C. During the subsequent aging treatment at 225 °C, the precipitation sequence in the fusion zone follows the order of supersaturated solid solution (SSSS) → βʺ(D0{sub 19}) → βʹ(cbco) → β{sub 1}(fcc) → β(fcc). High-density precipitates are present at the original grain boundariesmore » of the fusion zone from the welded structure but there are less precipitates in the interior of the original grains. The grain growth during the solution treatment at 430 °C comprises the slowly increasing stage, rapidly increasing stage, and stable stage. The network-distributed Mg{sub 24}(Gd,Y){sub 5} impedes migration of the grain boundaries, restricts grain growth in the first slowly increasing stage, and segregation of zirconium near the grain boundaries also affects migration of the grain boundaries. - Highlights: •Different quantities of precipitates are present at different location of grain. •The network-distributed Mg{sub 24}(Gd,Y){sub 5} restricts grain growth. •Segregation of Zr affects migration of grain boundaries.« less

Mechanical properties of zirconium alloys and zirconium hydrides predicted from density functional perturbation theory

DOE PAGES

Weck, Philippe F.; Kim, Eunja; Tikare, Veena; ...

2015-10-13

Here, the elastic properties and mechanical stability of zirconium alloys and zirconium hydrides have been investigated within the framework of density functional perturbation theory. Results show that the lowest-energy cubic Pn-3m with combining macron]m polymorph of δ-ZrH 1.5 does not satisfy all the Born requirements for mechanical stability, unlike its nearly degenerate tetragonal P4 2/ mcm polymorph. Elastic moduli predicted with the Voigt–Reuss–Hill approximations suggest that mechanical stability of α-Zr, Zr-alloy and Zr-hydride polycrystalline aggregates is limited by the shear modulus. According to both Pugh's and Poisson's ratios, α-Zr, Zr-alloy and Zr-hydride polycrystalline aggregates can be considered ductile. The Debyemore » temperatures predicted for γ-ZrH, δ-ZrH 1.5 and ε-ZrH 2 are θ D = 299.7, 415.6 and 356.9 K, respectively, while θ D = 273.6, 284.2, 264.1 and 257.1 K for the α-Zr, Zry-4, ZIRLO and M5 matrices, i.e. suggesting that Zry-4 possesses the highest micro-hardness among Zr matrices.« less

Atomic layer deposition of zirconium silicate films using zirconium tetra-tert-butoxide and silicon tetrachloride

NASA Astrophysics Data System (ADS)

Kim, Won-Kyu; Kang, Sang-Woo; Rhee, Shi-Woo

2003-09-01

A new precursor combination (SiCl4 and Zr(OtC4H9)4) was used to deposit Zr silicate with Zr(OtC4H9)4 as a zirconium source and oxygen source at the same time. SiCl4 and Zr(OtC4H9)4 have higher vapor pressures than their counterpart, ZrCl4 and tetra-n-butyl orthosilicate (TBOS), and it was expected that the cycle time would be shorter. The deposition temperature of the new combination was about 150 °C lower than that of ZrCl4 and TBOS. The film was zirconium rich while it was silicon rich with ZrCl4 and TBOS. Growth rate (nm/cycle), composition ratio [Zr/(Zr+Si)], and chlorine impurity were decreased with increasing deposition temperature from 125 to 225 °C. The composition ratio of the film deposited at 225 °C was 0.53 and the chlorine content was about 0.4 at. %. No carbon was detected by x-ray photoelectron spectroscopy.

Novel one-pot synthesis of dicarboxylic acids mediated alginate-zirconium biopolymeric complex for defluoridation of water.

PubMed

Prabhu, Subbaiah Muthu; Meenakshi, Sankaran

2015-04-20

The present investigation explains the fluoride removal from aqueous solution using alginate-zirconium complex prepared with respective dicarboxylic acids like oxalic acid (Ox), malonic acid (MA) and succinic acid (SA) as a medium. The complexes viz., alginate-oxalic acid-zirconium (Alg-Ox-Zr), alginate-malonic acid-zirconium (Alg-MA-Zr) and alginate-succinic acid-zirconium (Alg-SA-Zr) were synthesized and studied for fluoride removal. The synthesized complexes were characterized by FTIR, XRD, SEM with EDAX and mapping images. The effects of various operating parameters were optimized. The result showed that the maximum removal of fluoride 9653mgF(-)/kg was achieved by Alg-Ox-Zr complex at acidic pH in an ambient atmospheric condition. Equilibrium data of Alg-Ox-Zr complex was fitted well with Freundlich isotherm. The calculated values of thermodynamic parameters indicated that the fluoride adsorption is spontaneous and endothermic in nature. The mechanism of fluoride removal behind Alg-Ox-Zr complex has been proposed in detail. The suitability of the Alg-Ox-Zr complex has been tested with the field sample collected in a nearby fluoride endemic area. Copyright © 2014 Elsevier Ltd. All rights reserved.

Thermoluminescence (TL) of europium-doped ZrO2 obtained by sol-gel method

NASA Astrophysics Data System (ADS)

Rivera, T.; Furetta, C.; Azorín, J.; Barrera, M.; Soto, A. M.

This article reports the preparation and characterization of europium-doped zirconium oxide (ZrO2:Eu3+) formed by homogeneous precipitation from propoxyde of zirconium [Zr(OC3H7)4]. The alkoxide sol gel process is an efficient method to prepare the zirconium oxide matrix by the hydrolysis of alkoxide precursors followed by condensation to yield a polymeric oxo-bridged ZrO2 network. All compounds were characterized by thermal analysis and the X-ray diffractometry method. The thermoluminescence (TL) emission properties of ZrO2:Eu3+ under beta radiation effects are studied. The europium-doped sintered zirconia powder presents a TL glow curve with two peaks (Tmax) centered at around 204 and around 292 °C, respectively. TL response of ZrO2:Eu3+ as a function of beta-absorbed dose was linear from 2 Gy up to 90 Gy. The europium ion (Eu3+)-doped ZrO2 was found to be more sensitive to beta radiation than undoped ZrO2 obtained by the same method and presented a little fading of the TL signal compared with undoped zirconium oxide.

Optimization of stress relief heat treatment of PHWR pressure tubes (Zr 2.5Nb alloy)

NASA Astrophysics Data System (ADS)

Choudhuri, Gargi; Srivastava, D.; Gurumurthy, K. R.; Shah, B. K.

2008-12-01

The micro-structure of cold worked Zr-2.5%Nb pressure tube material consists of elongated grains of α-zirconium enclosed by a thin film of β-zirconium phase. This β-Zr phase is unstable and on heating, progressively decomposes to α-Zr phase and β-phase enriched with Nb and ultimately form β Nb. Meta-stable ω-phase precipitates as an intermediate step during decomposition depending on the heat treatment schedule, β→α+β→α+ω+β→α+β→α+β Morphological changes occur in the β-zirconium phase during the decomposition. The continuous ligaments of β Zr phase turn into a discontinuous array of particles followed by globulization of the β-phase. The morphological changes impose a significant effect on the creep rate and on the delayed hydride cracking velocity due to reduction in the hydrogen diffusion coefficient in α Zr. If the continuity of β-phase is disrupted by heat treatment, the effective diffusion coefficient decreases with a concomitant reduction in DHC velocity. The pressure tubes for the Indian PHWRs are made by a process of hot extrusion followed by cold pilgering in two stages and an intermediate annealing. Autoclaving at 400 °C for 36 h ensures stress relieving of the finished tubes. In the present studies, autoclaving duration at 400 °C was varied from 24 h to 96 h at 12 h-steps and the micro-structural changes in the β-phase were observed by TEM. Dislocation density, hardness and the micro-structural features such as thickness of β-phase, inter-particle spacing and volume fraction of the phases were measured at each stage. Autoclaving for a longer duration was found to change the morphology of β-phase and increase the inter-particle spacing. Progressive changes in the aspect ratio of the β-phase and their size and distribution are documented and reported. These micro-structural modifications are expected to decrease DHC velocity during reactor operation.

Influence of Deformation Mechanisms on the Mechanical Behavior of Metals and Alloys: Experiments, Constitutive Modeling, and Validation

NASA Astrophysics Data System (ADS)

Gray, G. T.; Cerreta, E.; Chen, Shuh Rong; Maudlin, P. J.

2004-06-01

Jim Williams has made seminal contributions to the field of structure / property relations and its controlling effects on the mechanical behavior of metals and alloys. This talk will discuss experimental results illustrating the role of interstitial content, grain size, texture, temperature, and strain rate on the operative deformation mechanisms, mechanical behavior, and substructure evolution in titanium, zirconium, hafnium, and rhenium. Increasing grain size is shown to significantly decrease the dynamic flow strength of Ti and Zr while increasing work-hardening rates due to an increased incidence of deformation twinning. Increasing oxygen interstitial content is shown to significantly alter both the constitutive response and α-ω shock-induced phase transition in Zr. The influence of crystallographic texture on the mechanical behavior in Ti, Zr, and Hf is discussed in terms of slip system and deformation twinning activity. An example of the utility of incorporation of operative deformation mechanisms into a polycrystalline plasticity constitutive model and validation using Taylor cylinder impact testing is presented.

Phase stability and photocatalytic activity of Zr-doped anatase synthesized in miniemulsion

NASA Astrophysics Data System (ADS)

Schiller, Renate; Weiss, Clemens K.; Landfester, Katharina

2010-10-01

A series of mesoporous anatase-type TiO2 doped with zirconium (0-50 mol% Zr) was synthesized by combining the sol-gel process with the inverse miniemulsion technique. Nanoparticles between 100 and 300 nm were directly prepared from acidic precursor solutions of titanium glycolate (EGMT) and zirconium isopropoxide. The miniemulsion technique is a simple and convenient method to synthesize nanoparticles of homogeneous size because the reactions (here hydrolysis and condensation) take place in the confined space of nanodroplets (several hundreds of nanometres) and therefore in a highly controlled manner. For low doping levels (0-7.1 mol% Zr), ZrxTi1 - xO2 solid solutions were formed where Zr was uniformly dispersed into the anatase framework. For higher amounts of zirconium (Zr >= 7.1 mol%), the crystallization of zirconium titanate (ZrTiO4) occurred at a low temperature of 650 °C and it was obtained as a pure material for 47.4 mol% <= Zr <= 50 mol%. The influence of the amount of zirconium on the crystallinity, crystallite size, phase composition and stability, morphology and specific surface area was investigated. For the characterization transmission electron microscopy (TEM), x-ray diffraction (XRD), nitrogen sorption (BET) and inductively coupled plasma-optical emission spectrometry (ICP-OES) were used. The photocatalytic activity of the crystalline mixed oxides (0-9.4 mol% Zr) was examined for the degradation of methylene blue under UV irradiation.

Effects of different titanium zirconium implant surfaces on initial supragingival plaque formation.

PubMed

John, Gordon; Becker, Jürgen; Schwarz, Frank

2017-07-01

The aim of the current study was the evaluation of biofilm development on different implant surfaces. Initial biofilm formation was investigated on five different implant surfaces, machined titanium (MTi), modified machined acid-etched titanium (modMATi), machined titanium zirconium (MTiZr), modified machined and acid-etched titanium zirconium (modMATiZr) and sandblasted large grid and acid-etched titanium zirconium surface (SLATiZr) for 24 and 48 h. Biocompatibility was tested after tooth brushing of the samples via cell viability testing with human gingival fibroblasts. After 24 h of biofilm collection, mean plaque surface was detected in the following descending order: After 24 h: MTiZr > MTi > SLATiZr > modMATiZr > modMATi. Both M surfaces showed significant higher biofilm formation than the other groups. After 48 h: MTiZr > MTi > SLATiZr > modMATiZr > modMATi. After tooth brushing: SLATiZr > modMATi > modMATiZr > MTi > MTiZr. All native samples depicted significant higher cell viability than their corresponding surfaces after biofilm removal procedure. The TiZr groups especially the modMATiZr group showed slower and less biofilm formation. In combination with the good biocompatibility, both modMA surfaces seem to be interesting candidates for surfaces in transgingival implant design. © 2016 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Production of nuclear grade zirconium: A review

NASA Astrophysics Data System (ADS)

Xu, L.; Xiao, Y.; van Sandwijk, A.; Xu, Q.; Yang, Y.

2015-11-01

Zirconium is an ideal material for nuclear reactors due to its low absorption cross-section for thermal neutrons, whereas the typically contained hafnium with strong neutron-absorption is very harmful for zirconium as a fuel cladding material. This paper provides an overview of the processes for nuclear grade zirconium production with emphasis on the methods of Zr-Hf separation. The separation processes are roughly classified into hydro- and pyrometallurgical routes. The known pyrometallurgical Zr-Hf separation methods are discussed based on the following reaction features: redox characteristics, volatility, electrochemical properties and molten salt-metal equilibrium. In the present paper, the available Zr-Hf separation technologies are compared. The advantages and disadvantages as well as future directions of research and development for nuclear grade zirconium production are discussed.

Effect of annealing temperature on the structural, morphological, and mechanical properties of polycrystalline zirconium oxynitride composite films deposited by plasma focus device

NASA Astrophysics Data System (ADS)

Khan, Ijaz A.; Kashif, Muhammad; Farid, Amjad; Rawat, Rajdeep S.; Ahmad, Riaz

2017-12-01

In this article, we reveal the post deposition annealing effect on the structural, morphological, and mechanical properties of polycrystalline zirconium oxynitride (P-ZrON) composite films deposited for 40 focus shots using a plasma focus device. The development of Zr(101), ZrN(111), ZrN(200), Zr3N4(320), ZrN0.28(002), and m-ZrO2(200) diffraction peaks confirms the deposition of P-ZrON composite films. The peak intensity, crystallite size, dislocation density, compressive stress, and texture coefficient of the Zr3N4(320) plane and the microstructural features such as the shape, size and distribution of nanoparticles as well as the film compactness are influenced by the annealing temperature. Elemental analysis confirms the presence of Zr, N, and O in the deposited films. The microhardness of the P-ZrON composite film annealed at 500 °C is found to be 11.87 GPa which is 7.8 times that of virgin zirconium.

Microstructure and Mechanical Properties of Nano-Size Zirconium Carbide Dispersion Strengthened Tungsten Alloys Fabricated by Spark Plasma Sintering Method

NASA Astrophysics Data System (ADS)

Xie, Zhuoming; Liu, Rui; Fang, Qianfeng; Zhang, Tao; Jiang, Yan; Wang, Xianping; Liu, Changsong

2015-12-01

W-(0.2, 0.5, 1.0)wt% ZrC alloys with a relative density above 97.5% were fabricated through the spark plasma sintering (SPS) method. The grain size of W-1.0wt% ZrC is about 2.7 μm, smaller than that of pure W and W-(0.2, 0.5)wt% ZrC. The results indicated that the W-ZrC alloys exhibit higher hardness at room temperature, higher tensile strength at high temperature, and a lower ductile to brittle transition temperature (DBTT) than pure W. The tensile strength and total elongation of W-0.5wt% ZrC alloy at 700 °C is 535 MPa and 24.8%, which are respectively 59% and 114% higher than those of pure W (337 MPa, 11.6%). The DBTT of W-(0.2, 0.5, 1.0)wt% ZrC materials is in the range of 500°C-600°C, which is about 100 °C lower than that of pure W. Based on microstructure analysis, the improved mechanical properties of the W-ZrC alloys were suggested to originate from the enhanced grain boundary cohesion by ZrC capturing the impurity oxygen in tungsten and nano-size ZrC dispersion strengthening. supported by the Innovation Program of Chinese Academy of Sciences (No. KJCX2-YW-N35), the National Magnetic Confinement Fusion Science Program of China (No. 2011GB108004), National Natural Science Foundation of China (Nos. 51301164, 11075177, 11274305), and Anhui Provincial Natural Science Foundation of China (No. 1408085QE77)

Evaluation of macrocyclic hydroxyisophthalamide ligands as chelators for zirconium-89

PubMed Central

Xu, Jide; Tatum, David; Magda, Darren

2017-01-01

The development of bifunctional chelators (BFCs) for zirconium-89 immuno-PET applications is an area of active research. Herein we report the synthesis and evaluation of octadentate hydroxyisophthalamide ligands (1 and 2) as zirconium-89 chelators. While both radiometal complexes could be prepared quantitatively and with excellent specific activity, preparation of 89Zr-1 required elevated temperature and an increased reaction time. 89Zr-1 was more stable than 89Zr-2 when challenged in vitro by excess DTPA or serum proteins and in vivo during acute biodistribution studies. Differences in radiometal complex stability arise from structural changes between the two ligand systems, and suggest further ligand optimization is necessary to enhance 89Zr chelation. PMID:28575044

Evaluation of macrocyclic hydroxyisophthalamide ligands as chelators for zirconium-89.

PubMed

Bhatt, Nikunj B; Pandya, Darpan N; Xu, Jide; Tatum, David; Magda, Darren; Wadas, Thaddeus J

2017-01-01

The development of bifunctional chelators (BFCs) for zirconium-89 immuno-PET applications is an area of active research. Herein we report the synthesis and evaluation of octadentate hydroxyisophthalamide ligands (1 and 2) as zirconium-89 chelators. While both radiometal complexes could be prepared quantitatively and with excellent specific activity, preparation of 89Zr-1 required elevated temperature and an increased reaction time. 89Zr-1 was more stable than 89Zr-2 when challenged in vitro by excess DTPA or serum proteins and in vivo during acute biodistribution studies. Differences in radiometal complex stability arise from structural changes between the two ligand systems, and suggest further ligand optimization is necessary to enhance 89Zr chelation.

Synthesis of zirconium carbide whiskers by a combination of microwave hydrothermal and carbothermal reduction

NASA Astrophysics Data System (ADS)

Li, Kezhi; Zhou, Xuan; Zhao, Zhigang; Chen, Chunyu; Wang, Changcong; Ren, Biyun; Zhang, Leilei

2018-02-01

Zirconium carbide (ZrC) whiskers were successfully synthesized by a combination of microwave hydrothermal (MH) and carbothermal reduction. The precursors of ZrC whiskers were produced by MH, subsequently carbothermally reduced to ZrC whiskers at 1100-1600 °C in an Ar atmosphere. Effects of the reduction temperature and precursors with various carbon/zirconium (C/Zr) molar ratios on the synthesis of ZrC whiskers were investigated. The results showed that the carbothermal reduction occurred at 1100 °C, and terminated at a relatively low temperature (1400 °C). When the reduction temperature was 1500 °C and the C/Zr molar ratio was 5:1, the ZrC whiskers with the largest aspect ratio and the most uniform distribution were produced. The whiskers exhibited the diameters of 0.1-2 μm and the lengths of 5-30 μm. The synthesized ZrC whiskers with a single crystalline phase displayed cylindrical and pagoda-like morphologies. The growth of ZrC whiskers was considered to be governed by the Ostwald ripening and S-L-S mechanism.

Efficient UV-emitting X-ray phosphors: octahedral Zr(PO 4) 6 luminescence centers in potassium hafnium-zirconium phosphates K 2Hf 1- xZr x(PO 4) 2 and KHf 2(1- x) Zr 2 x(PO 4) 3

NASA Astrophysics Data System (ADS)

Torardi, C. C.; Miao, C. R.; Li, J.

2003-02-01

Potassium hafnium-zirconium phosphates, K 2Hf 1- xZr x(PO 4) 2 and KHf 2(1- x) Zr 2 x(PO 4) 3, are broad-band UV-emitting phosphors. At room temperature, they have emission peak maxima at approximately 322 and 305 nm, respectively, under 30 kV peak molybdenum X-ray excitation. Both phosphors demonstrate luminescence efficiencies that make them up to ˜60% as bright as commercially available CaWO 4 Hi-Plus. The solid-state and flux synthesis conditions, and X-ray excited UV luminescence of these two phosphors are discussed. Even though the two compounds have different atomic structures, they contain zirconium in the same active luminescence environment as that found in highly efficient UV-emitting BaHf 1- xZr x(PO 4) 2. All the three materials have hafnium and zirconium in octahedral coordination via oxygen-atom corner sharing with six separate PO 4 tetrahedra. This octahedral Zr(PO 4) 6 moiety appears to be an important structural element for efficient X-ray excited luminescence, as are the edge-sharing octahedral TaO 6 chains for tantalate emission.

High pressure low temperature hot pressing method for producing a zirconium carbide ceramic

DOEpatents

Cockeram, Brian V.

2017-01-10

A method for producing monolithic Zirconium Carbide (ZrC) is described. The method includes raising a pressure applied to a ZrC powder until a final pressure of greater than 40 MPa is reached; and raising a temperature of the ZrC powder until a final temperature of less than 2200.degree. C. is reached.

Evaluation of macrocyclic hydroxyisophthalamide ligands as chelators for zirconium-89

DOE PAGES

Bhatt, Nikunj B.; Pandya, Darpan N.; Xu, Jide; ...

2017-06-02

The development of bifunctional chelators (BFCs) for zirconium-89 immuno-PET applications is an area of active research. We report the synthesis and evaluation of octadentate hydroxyisophthalamide ligands (1 and 2) as zirconium-89 chelators. And while both radiometal complexes could be prepared quantitatively and with excellent specific activity, preparation of 89Zr-1 required elevated temperature and an increased reaction time. 89Zr-1 was more stable than 89Zr-2 when challenged in vitro by excess DTPA or serum proteins and in vivo during acute biodistribution studies. The differences in radiometal complex stability arise from structural changes between the two ligand systems, and suggest further ligand optimizationmore » is necessary to enhance 89Zr chelation.« less

Evaluation of macrocyclic hydroxyisophthalamide ligands as chelators for zirconium-89

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bhatt, Nikunj B.; Pandya, Darpan N.; Xu, Jide

The development of bifunctional chelators (BFCs) for zirconium-89 immuno-PET applications is an area of active research. We report the synthesis and evaluation of octadentate hydroxyisophthalamide ligands (1 and 2) as zirconium-89 chelators. And while both radiometal complexes could be prepared quantitatively and with excellent specific activity, preparation of 89Zr-1 required elevated temperature and an increased reaction time. 89Zr-1 was more stable than 89Zr-2 when challenged in vitro by excess DTPA or serum proteins and in vivo during acute biodistribution studies. The differences in radiometal complex stability arise from structural changes between the two ligand systems, and suggest further ligand optimizationmore » is necessary to enhance 89Zr chelation.« less

Modification of Different Zirconium Propoxide Precursors by Diethanolamine. Is There a Shelf Stability Issue for Sol-Gel Applications?

PubMed Central

Spijksma, Gerald I.; Blank, Dave H. A.; Bouwmeester, Henny J. M.; Kessler, Vadim G.

2009-01-01

Modification of different zirconium propoxide precursors with H2dea was investigated by characterization of the isolated modified species. Upon modification of zirconium n-propoxide and [Zr(OnPr)(OiPr)3(iPrOH)]2 with ½ a mol equivalent of H2dea the complexes [Zr2(OnPr)6(OCH2CH2)2NH]2 (1) and [Zr2(OnPr)2(OiPr)4(OCH2CH2)2NH]2 (2) were obtained. However, 1H-NMR studies of these tetranuclear compounds showed that these are not time-stable either in solution or solid form. The effect of this time instability on material properties is demonstrated by light scattering and TEM experiments. Modification of zirconium isopropoxide with either ½ or 1 equivalent mol of H2dea results in formation of the trinuclear complex, Zr{η3μ2-NH(C2H4O)2}3[Zr(OiPr)3]2(iPrOH)2 (3) countering a unique nona-coordinated central zirconium atom. This complex 3 is one of the first modified zirconium propoxide precursors shown to be stable in solution for long periods of time. The particle size and morphology of the products of sol-gel synthesis are strongly dependent on the time factor and eventual heat treatment of the precursor solution. Reproducible sol-gel synthesis requires the use of solution stable precursors. PMID:20087472

Nuclear-grade zirconium prepared by combining combustion synthesis with molten-salt electrorefining technique

NASA Astrophysics Data System (ADS)

Li, Hui; Nersisyan, Hayk H.; Park, Kyung-Tae; Park, Sung-Bin; Kim, Jeong-Guk; Lee, Jeong-Min; Lee, Jong-Hyeon

2011-06-01

Zirconium has a low absorption cross-section for neutrons, which makes it an ideal material for use in nuclear reactor applications. However, hafnium typically contained in zirconium causes it to be far less useful for nuclear reactor materials because of its high neutron-absorbing properties. In the present study, a novel effective method has been developed for the production of hafnium-free zirconium. The process includes two main stages: magnesio-thermic reduction of ZrSiO 4 under a combustion mode, to produce zirconium silicide (ZrSi), and recovery of hafnium-free zirconium by molten-salt electrorefining. It was found that, depending on the electrorefining procedure, it is possible to produce zirconium powder with a low hafnium content: 70 ppm, determined by ICP-AES analysis.

Dissolution process for ZrO.sub.2 -UO.sub.2 -CaO fuels

DOEpatents

Paige, Bernice E.

1976-06-22

The present invention provides an improved dissolution process for ZrO.sub.2 -UO.sub.2 -CaO-type pressurized water reactor fuels. The zirconium cladding is dissolved with hydrofluoric acid, immersing the ZrO.sub.2 -UO.sub.2 -CaO fuel wafers in the resulting zirconium-dissolver-product in the dissolver vessel, and nitric acid is added to the dissolver vessel to facilitate dissolution of the uranium from the ZrO.sub.2 -UO.sub.2 -CaO fuel wafers.

High-yield sol-gel synthesis of well-dispersed, colorless ZrO(2) nanocrystals.

PubMed

Mizuno, Mikihisa; Sasaki, Yuichi; Lee, Sungkil; Katakura, Hitoshi

2006-08-15

A 93% high-yield synthesis of well-dispersed, colorless zirconium dioxide (ZrO(2)) nanocrystals is reported. In this synthesis, hydrolysis and condensation reactions of zirconium(IV) tert-butoxide in the presence of oleic acid (100 degrees C) formed ZrO(2) precursors. The ZrO(2) precursors were made of -Zr-O-Zr- networks surrounded by oleic acid molecules. Annealing (280 degrees C) the precursors dispersed in dioctyl ether caused crystallization of the -Zr-O-Zr- networks, thereby generating 4 nm ZrO(2) nanocrystals stabilized with oleic acid. The particles were highly crystalline and tetragonal phase. A dense ZrO(2) nanocrystal dispersion in toluene (280 mg/mL) showed a transmittance of about 90% (3 mm optical path length) in the whole visible region.

Effect of Microstructure on the Mechanical Properties of Extruded Magnesium and a Magnesium Alloy

NASA Astrophysics Data System (ADS)

McGhee, Paul

The main objective of this research was to investigate the relationship between the fatigue behavior and crystallographic texture evolution of magnesium (Mg) alloys with a range of microalloying element content processed under various extrusion conditions. Several Mg alloys were processed under a range of extrusion temperatures, extrusion ratios, and alloying content and tested under monotonic and cyclic fatigue loading conditions: fully-reversed condition tested at strain amplitudes of 0.15% - 1.00% in strain-control mode. After fatigue testing, Mg microstructural analysis was performed using SEM, TEM, optical microscopy, and X-ray diffraction techniques. Microstructural observations revealed significant grain refinement through a combination of zirconium (Zr) addition and hot-extrusion, producing fine equiaxed grain structure with grain sizes ranging between 1-5 microm. Texture analysis and partial compression testing results showed that the initial texture of the extruded alloy gradually evolved upon compressive loading along the c-axes inducing extension twinning creating a strong basal texture along the extrusion direction. Full tensile and compression testing at room temperature showed that the combination of hot extrusion and Zr addition can further refine the grains of the Mg alloys microstructure and enhance the texture while simultaneously enhancing the mechanical properties.

Development of Self-Healing Zirconium-Silicide Coatings for Improved Performance Zirconium-Alloy Fuel Cladding

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sridharan, Kumar; Mariani, Robert; Bai, Xianming

Zirconium-alloy fuel claddings have been used successfully in Light Water Reactors (LWR) for over four decades. However, under high temperature accident conditions, zirconium-alloys fuel claddings exhibit profuse exothermic oxidation accompanied by release of hydrogen gas due to the reaction with water/steam. Additionally, the ZrO 2 layer can undergo monoclinic to tetragonal to cubic phase transformations at high temperatures which can induce stresses and cracking. These events were unfortunately borne out in the Fukushima-Daiichi accident in in Japan in 2011. In reaction to such accident, protective oxidation-resistant coatings for zirconium-alloy fuel claddings has been extensively investigated to enhance safety margins inmore » accidents as well as fuel performance under normal operation conditions. Such surface modification could also beneficially affect fuel rod heat transfer characteristics. Zirconium-silicide, a candidate coating material, is particularly attractive because zirconium-silicide coating is expected to bond strongly to zirconium-alloy substrate. Intermetallic compound phases of zirconium-silicide have high melting points and oxidation of zirconium silicide produces highly corrosion resistant glassy zircon (ZrSiO 4) and silica (SiO 2) which possessing self-healing qualities. Given the long-term goal of developing such coatings for use with nuclear reactor fuel cladding, this work describes results of oxidation and corrosion behavior of bulk zirconium-silicide and fabrication of zirconium-silicide coatings on zirconium-alloy test flats, tube configurations, and SiC test flats. In addition, boiling heat transfer of these modified surfaces (including ZrSi 2 coating) during clad quenching experiments is discussed in detail.« less

Novel approach to Zr powder production by smooth ZrCl4 bubbling through molten salt

NASA Astrophysics Data System (ADS)

Bae, Hyun-Na; Choi, Mi-Seon; Lee, Go-Gi; Kim, Seon-Hyo

2016-01-01

A reduction process using ZrCl4 bubbles as a reactant was investigated to produce zirconium metals. ZrCl4 vapor was bubbled through the lance in the bath, in which Mg melt and MgCl2 salt were separated. Zr powder was formed by a reduction of ZrCl4 bubbles in magnesium layer. However, the lance was clogged by the aggregate of zirconium occurred during ZrCl4 vapor injecting leading to interruption of ZrCl4 supply into the bath. This phenomenon could be caused by the presence of magnesium at the lance tip, which passes through MgCl2 salt during bubbling, and then zirconium was formed in the forms of intermetallic compounds with aluminum. In this study, the effect of molten salt on the troubled phenomena was investigated and it was verified that CaCl2 with relatively low Weber number meaning relatively high surface tension as molten salt is effective in inhibiting the lance clogging phenomena. Then, a few micrometer-sized Zr powder with the high purity of 91.6 wt% was obtained smoothly without the formation of intermetallic compound.

Effect of SiO 2-ZrO 2 supports prepared by a grafting method on hydrogen production by steam reforming of liquefied natural gas over Ni/SiO 2-ZrO 2 catalysts

NASA Astrophysics Data System (ADS)

Seo, Jeong Gil; Youn, Min Hye; Song, In Kyu

SiO 2-ZrO 2 supports with various zirconium contents are prepared by grafting a zirconium precursor onto the surface of commercial Carbosil silica. Ni(20 wt.%)/SiO 2-ZrO 2 catalysts are then prepared by an impregnation method, and are applied to hydrogen production by steam reforming of liquefied natural gas (LNG). The effect of SiO 2-ZrO 2 supports on the performance of the Ni(20 wt.%)/SiO 2-ZrO 2 catalysts is investigated. SiO 2-ZrO 2 prepared by a grafting method serves as an efficient support for the nickel catalyst in the steam reforming of LNG. Zirconia enhances the resistance of silica to steam significantly and increases the interaction between nickel and the support, and furthermore, prevents the growth of nickel oxide species during the calcination process through the formation of a ZrO 2-SiO 2 composite structure. The crystalline structures and catalytic activities of the Ni(20 wt.%)/SiO 2-ZrO 2 catalysts are strongly influenced by the amount of zirconium grafted. The conversion of LNG and the yield of hydrogen show volcano-shaped curves with respect to zirconium content. Among the catalysts tested, the Ni(20 wt.%)/SiO 2-ZrO 2 (Zr/Si = 0.54) sample shows the best catalytic performance in terms of both LNG conversion and hydrogen yield. The well-developed and pure tetragonal phase of ZrO 2-SiO 2 (Zr/Si = 0.54) appears to play an important role in the adsorption of steam and subsequent spillover of steam from the support to the active nickel. The small particle size of the metallic nickel in the Ni(20 wt.%)/SiO 2-ZrO 2 (Zr/Si = 0.54) catalyst is also responsible for its high performance.

Synthesis of 0.1% & 0.2% neodymium doped barium zirconium titanate (BaZr{sub 0.2}Ti{sub 0.8}O{sub 3}) and study of their dielectric behaviour

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Anil, E-mail: anilkantikumar@rediffmail.com; Kumar, Vipin; Gupta, Merry

2015-08-28

Efforts have been made to ease process of producing widely used multilayered ceramics of Barium Zirconium Titanium Oxides and study their dielectric behaviour and structural properties. For this purpose, adequate proportions of Barium Carbonate, Zirconium Oxide and Titanium Oxide were taken and hand milled for 2 hours. Neodymium composition of the order of 0.1% and 0.2% was used for doping to weight percentage of BaZr0.2Ti0.8O3. The samples were authenticated using raw data obtained from Bruker AXS D8 advance Copper KL alpha source XRD equipment. Further, the samples were studied for their phase transition, composition, single phase perovskite structure using XRDmore » technique. The technique has also been applied to know formation of stable homogeneous solid solution from XRD parameters. The other physical parameters like the morphology, micro structural information, crystal arrangements and topography have also been observed through SEM. The SEM has revealed information related to grain size development and composition of sample with fine agglomerates. For complete study of the compounds the atomic and weight composition has also been examined by Electron Dispersive Spectroscopy patterns. The comparison has been made with other works on ceramics at various frequencies and has yielded very interesting results.« less

Fabrication of oxide layer on zirconium by micro-arc oxidation: Structural and antimicrobial characteristics.

PubMed

Fidan, S; Muhaffel, F; Riool, M; Cempura, G; de Boer, L; Zaat, S A J; Filemonowicz, A Czyrska-; Cimenoglu, H

2017-02-01

The aim of this study was to cover the surfaces of zirconium (Zr) with an antimicrobial layer for biomedical applications. For this purpose, the micro-arc oxidation (MAO) process was employed in a sodium silicate and sodium hydroxide containing base electrolyte with and without addition of silver acetate (AgC 2 H 3 O 2 ). In general, synthesized MAO layers were composed of zirconium oxide (ZrO 2 ) and zircon (ZrSiO 4 ). Addition of AgC 2 H 3 O 2 into the base electrolyte caused homogenous precipitation of silver-containing particles in the MAO layer, which exhibited excellent antibacterial efficiency against methicillin-resistant Staphylococcus aureus (MRSA) as compared to the untreated and MAO-treated Zr. Copyright © 2016 Elsevier B.V. All rights reserved.

Di-macrocyclic terephthalamide ligands as chelators for the PET radionuclide zirconium-89

DOE PAGES

Pandya, Darpan N.; Pailloux, Sylvie; Tatum, David; ...

2014-12-18

The development of bifunctional chelators (BFCs) which can stably chelate zirconium-89 ((89)Zr) while being conjugated to targeting molecules is an area of active research. Herein we report the first octadentate terephthalamide ligands, which are easily radiolabeled with (89)Zr and are highly stable in vitro. Lastly, they represent a novel class of chelators, which are worthy of further development as BFCs for (89)Zr.

Zirconium-carbon hybrid sorbent for removal of fluoride from water: oxalic acid mediated Zr(IV) assembly and adsorption mechanism

PubMed Central

Halla, Velazquez-Jimenez Litza; Hurt Robert, H; Juan, Matos; Rene, Rangel-Mendez Jose

2014-01-01

When activated carbon (AC) is modified with zirconium(IV) by impregnation or precipitation, the fluoride adsorption capacity is typically improved. There is significant potential to improve these hybrid sorbent by controlling the impregnation conditions, which determine the assembly and dispersion of the Zr phases on carbon surfaces. Here, commercial activated carbon was modified with Zr(IV) together with oxalic acid (OA) used to maximize the zirconium dispersion and enhance fluoride adsorption. Adsorption experiments were carried out at pH 7 and 25 °C with a fluoride concentration of 40 mg L−1. The OA/Zr ratio was varied to determine the optimal conditions for subsequent fluoride adsorption. The data was analyzed using the Langmuir and Freundlich isotherm models. FTIR, XPS and the surface charge distribution were performed to elucidate the adsorption mechanism. Potentiometric titrations showed that the modified activated carbon (ZrOx-AC) possesses positive charge at pH lower than 7, and FTIR analysis demonstrated that zirconium ions interact mainly with carboxylic groups on the activated carbon surfaces. Moreover, XPS analysis demonstrated that Zr(IV) interacts with oxalate ions, and the fluoride adsorption mechanism is likely to involve –OH− exchange from zirconyl oxalate complexes. PMID:24359079

Superconductivity in zirconium-rhodium alloys

NASA Technical Reports Server (NTRS)

Zegler, S. T.

1969-01-01

Metallographic studies and transition temperature measurements were made with isothermally annealed and water-quenched zirconium-rhodium alloys. The results clarify both the solid-state phase relations at the Zr-rich end of the Zr-Rh alloy system and the influence upon the superconducting transition temperature of structure and composition.

Zr-Containing 4,4'-ODA/PMDA Polyimide Composites. Parts 1 & 2

NASA Technical Reports Server (NTRS)

Illingsworth, M. L.; Betancourt, J. A.; Chen, Y.; Terschak, J. A.; Banks, B. A.; Rutledge, S. K.; Cales, M.; He, L.

2001-01-01

The objective of this research is to improve the atomic oxygen resistance of Kapton(TM), a polyimide (PI) made from pyromellitic acid dianhydride (PMDA) and 4,4'-oxydianiline (ODA), while retaining or enhancing the desirable properties of the pure polymer. Toward this end, zirconium-containing complexes and polymers were used to make composites and blends. Tetra(acetylacetonato)zirconium(IV), Zr(acac)4, which is commercially available, was identified as the best zirconium-containing complex for enhancing the atomic oxygen resistance of polyimide composites of the 10 complexes screened. Films prepared from the commercially available polyamic acid (PAA) of PMDA-ODA (DuPont) have good uniformity, flexibility, and tensile strength. A 24-layer 10% (mol) Zr(acac)4/PI composite film showed significant improvement (ca. 20 fold) of atomic oxygen resistance over the pure polyimide. However, 10% (mol) Zr(acac)4 represents an upper concentration limit, above which films undergo cracking upon thermal imidization. In order to increase the Zr complex concentration in PMDA-ODA PI films, while retaining good film properties, [Zr(adsp)2-PMDA]n coordination polymer [bis(4-amino-N,N'-disalicylidene- 1,2-phenylenediamino)zirconium(IV)-pyromellitic dianhydride] and [Zr(adsp)2-PMDA-ODA-PMDA]n terpolymer were synthesized and blended with commercial PAA, respectively. Several techniques were used to characterize the films made from the polymer containing Zr(acac)4. Plasma studies of films having 2% (mol) incremental concentrations of Zr in the Kapton up to 10% (mol) show that the overall rate of erosion is reduced about 75 percent.

In vitro assessment of artifacts induced by titanium, titanium-zirconium and zirconium dioxide implants in cone-beam computed tomography.

PubMed

Sancho-Puchades, Manuel; Hämmerle, Christoph H F; Benic, Goran I

2015-10-01

The aim of this study was to test whether or not the intensity of artifacts around implants in cone-beam computed tomography (CBCT) differs between titanium, titanium-zirconium and zirconium dioxide implants. Twenty models of a human mandible, each containing one implant in the single-tooth gap position 45, were cast in dental stone. Five test models were produced for each of the following implant types: titanium 4.1 mm diameter (Ti4.1 ), titanium 3.3 mm diameter (Ti3.3 ), titanium-zirconium 3.3 mm diameter (TiZr3.3 ) and zirconium dioxide 3.5-4.5 mm diameter (ZrO3.5-4.5 ) implants. For control purposes, three models without implants were produced. Each model was scanned using a CBCT device. Gray values (GV) were recorded at eight circumferential positions around the implants at 0.5 mm, 1 mm and 2 mm from the implant surface (GVT est ). GV were assessed in the corresponding volumes of interest (VOI) in the control models without implants (GVC ontrol ). Differences of gray values (ΔGV) between GVT est and GVC ontrol were calculated as percentages. One-way ANOVA and post hoc tests were applied to detect differences between implant types. Mean ΔGV for ZrO3.5-4.5 presented the highest absolute values, generally followed by TiZr3.3 , Ti4.1 and Ti3.3 implants. The differences of ΔGV between ZrO3.5-4.5 and the remaining groups were statistically significant in the majority of the VOI (P ≤ 0.0167). ΔGV for TiZr3.3 , Ti4.1 and Ti3.3 implants did not differ significantly in the most VOI. For all implant types, ΔGV showed positive values buccally, mesio-buccally, lingually and disto-lingually, whereas negative values were detected mesially and distally. Zirconium dioxide implants generate significantly more artifacts as compared to titanium and titanium-zirconium implants. The intensity of artifacts around zirconium dioxide implants exhibited in average the threefold in comparison with titanium implants. © 2014 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Atomic layer deposition of zirconium silicate films using zirconium tetrachloride and tetra-n-butyl orthosilicate

NASA Astrophysics Data System (ADS)

Kim, Won-Kyu; Kang, Sang-Woo; Rhee, Shi-Woo; Lee, Nae-In; Lee, Jong-Ho; Kang, Ho-Kyu

2002-11-01

Atomic layer chemical vapor deposition of zirconium silicate films with a precursor combination of ZrCl4 and tetra-n-butyl orthosilicate (TBOS) was studied for high dielectric gate insulators. The effect of deposition conditions, such as deposition temperature, pulse time for purge and precursor injection on the deposition rate per cycle, and composition of the film were studied. At 400 °C, the growth rate saturated to 1.35 Å/cycle above 500 sccm of the argon purge flow rate. The growth rate, composition ratio ((Zr/Zr+Si)), and impurity contents (carbon and chlorine) saturated with the increase of the injection time of ZrCl4 and TBOS and decreased with the increased deposition temperature from 300 to 500 °C. The growth rate, composition ratio, carbon, and chlorine contents of the Zr silicate thin films deposited at 500 °C were 1.05 Å/cycle, 0.23, 1.1 at. %, and 2.1 at. %, respectively. It appeared that by using only zirconium chloride and silicon alkoxide sources, the content of carbon and chlorine impurities could not be lowered below 1%. It was also found that the incorporation rate of metal from halide source was lower than alkoxide source.

Synthesis of Nacre-Like Structures using Novel Fabrication Techniques

DTIC Science & Technology

2010-02-18

vapor deposition methods in order to prepare zirconium nitride (ZrN) and polymethylmethacrylate (PMMA) multilayer Figure 1. (a) Tortuous crack growth...deposition methods in order to prepare zirconium nitride (ZrN) and polymethylmethacrylate (PMMA) multilayer E la st ic m od ul us (G P a) Number

TEM study on the initial oxidation of Zircaloy-4 thin foil specimens heated in a low vacuum air condition at 280-300 °C

NASA Astrophysics Data System (ADS)

Wang, Zhen; Zhou, Bang-xin; Zhu, Wei; Wen, Bang; Yao, Mei-yi; Li, Qiang; Wu, Lu; Zhang, Jin-long; Fang, Zhong-qiang

2017-04-01

As one of the important structural materials in nuclear industry, the corrosion resistance of zirconium alloy limits their in-pile application. Therefore, it is necessary to investigate the corrosion mechanism of zirconium alloys. The zirconium-oxygen reaction at the O/M interface is one of the factors that affect the oxidation process. There are few reports in this regard. Ideally, the reaction process at the O/M interface has certain relevance with the initiation oxidation of zirconium, which provided a new way to investigate the reaction process by observing the initiation oxidation behaviours. To investigate the oxidation behaviours of zirconium alloy at the initial stage, in this paper, zircaloy-4 TEM thin foil specimens in 3 mm diameter were studied by TEM observation after heating in air condition with a vacuum of 3 Pa at 280 °C, 290 °C and 300 °C for 30 min exposures. The results show that, ZrO2 begin to nucleate at a size of 3-5 nm at a high Zr/O ratio of 10.4 and oxide layer formed while Zr/O was 4.6. As a result of stress caused by the P.B ratio of Zr, slip bands formed and a bcc structure sub-oxide b-ZrOx (a = 0.51 nm) grew up along with the slip bands was observed. At both sides of b-ZrOx, two hcp structure sub-oxides having the same a-axis lattice parameter and different c-axis lattice parameter were detected.

Fatigue crack propagation of nickel-base superalloys at 650 deg C

NASA Technical Reports Server (NTRS)

Gayda, J.; Gabb, T. P.; Miner, R. V.

1988-01-01

The 650 C fatigue crack propagation behavior of two nickel-base superalloys, Rene 95 and Waspaloy, is studied with particular emphasis placed on understanding the roles of creep, environment, and two key grain boundary alloying additions, boron and zirconium. Comparison of air and vacuum data shows the air environment to be detrimental over a wide range of frequencies for both alloys. More in-depth analysis on Rene 95 shows at lower frequencies, such as 0.02 Hz, failure in air occurs by intergranular, environmentally-assisted creep crack growth, while at higher frequencies, up to 5.0 Hz, environmental interaction are still evident but creep effects are minimized. The effect of B and Zr in Waspaloy is found to be important where environmental and/or creep interactions are presented. In those instances, removal of B and Zr dramatically increases crack growth and it is therefore plausible that effective dilution of these elements may explain a previously observed trend in which crack growth rates increase with decreasing grain size.

Fatigue crack propagation of nickel-base superalloys at 650 deg C

NASA Technical Reports Server (NTRS)

Gayda, J.; Gabb, T. P.; Miner, R. V.

1985-01-01

The 650 C fatigue crack propagation behavior of two nickel-base superalloys, Rene 95 and Waspaloy, is studied with particular emphasis placed on understanding the roles of creep, environment, and two key grain boundary alloying additions, boron and zirconium. Comparison of air and vacuum data shows the air environment to be detrimental over a wide range of frequencies for both alloys. More in-depth analysis on Rene 95 shows at lower frequencies, such as 0.02 Hz, failure in air occurs by intergranular, environmentally-assisted creep crack growth, while at higher frequencies, up to 5.0 Hz, environmental interactions are still evident but creep effects are minimized. The effect of B and Zr in Waspaloy is found to be important where environmental and/or creep interactions are presented. In those instances, removal of B and Zr dramatically increases crack growth and it is therefore plausible that effective dilution of these elements may explain a previously observed trend in which crack growth rates increase with decreasing grain size.

Computational and Experimental Studies of Microstructure-Scale Porosity in Metallic Fuels for Improved Gas Swelling Behavior

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mllett, Paul; McDeavitt, Sean; Deo, Chaitanya

This proposal will investigate the stability of bimodal pore size distributions in metallic uranium and uranium-zirconium alloys during sintering and re-sintering annealing treatments. The project will utilize both computational and experimental approaches. The computational approach includes both Molecular Dynamics simulations to determine the self-diffusion coefficients in pure U and U-Zr alloys in single crystals, grain boundaries, and free surfaces, as well as calculations of grain boundary and free surface interfacial energies. Phase-field simulations using MOOSE will be conducted to study pore and grain structure evolution in microstructures with bimodal pore size distributions. Experiments will also be performed to validate themore » simulations, and measure the time-dependent densification of bimodal porous compacts.« less

Electrostatic Assembly Preparation of High-Toughness Zirconium Diboride-Based Ceramic Composites with Enhanced Thermal Shock Resistance Performance.

PubMed

Zhang, Baoxi; Zhang, Xinghong; Hong, Changqing; Qiu, Yunfeng; Zhang, Jia; Han, Jiecai; Hu, PingAn

2016-05-11

The central problem of using ceramic as a structural material is its brittleness, which associated with rigid covalent or ionic bonds. Whiskers or fibers of strong ceramics such as silicon carbide (SiC) or silicon nitride (Si3N4) are widely embedded in a ceramic matrix to improve the strength and toughness. The incorporation of these insulating fillers can impede the thermal flow in ceramic matrix, thus decrease its thermal shock resistance that is required in some practical applications. Here we demonstrate that the toughness and thermal shock resistance of zirconium diboride (ZrB2)/SiC composites can be improved simultaneously by introducing graphene into composites via electrostatic assembly and subsequent sintering treatment. The incorporated graphene creates weak interfaces of grain boundaries (GBs) and optimal thermal conductance paths inside composites. In comparison to pristine ZrB2-SiC composites, the toughness of (2.0%) ZrB2-SiC/graphene composites exhibited a 61% increasing (from 4.3 to 6.93 MPa·m(1/2)) after spark plasma sintering (SPS); the retained strength after thermal shock increased as high as 74.8% at 400 °C and 304.4% at 500 °C. Present work presents an important guideline for producing high-toughness ceramic-based composites with enhanced thermal shock properties.

Formation and reduction behaviors of zirconium oxide compounds in LiCl-Li2O melt at 923 K

NASA Astrophysics Data System (ADS)

Sakamura, Yoshiharu; Iizuka, Masatoshi; Kitawaki, Shinichi; Nakayoshi, Akira; Kofuji, Hirohide

2015-11-01

The reduction behaviors of ZrO2, Li2ZrO3 and (U,Pu,Zr)O2 in a LiCl-Li2O salt bath at 923 K were investigated. This study was conducted as part of a feasibility study on the pyrochemical treatment of damaged fuel debris generated by severe accidents at light water reactors. It was demonstrated in electrolytic reduction tests that the uranium in synthetic corium specimens of (U,Pu,Zr)O2 with various ZrO2 contents could be reduced to the metallic form and that part of the zirconium was converted to Li2ZrO3. Zirconium metal and Li2ZrO3 were obtained by the reduction of ZrO2. The reduction of Li2ZrO3 did not proceed even in LiCl containing no Li2O. Moreover, the stable chemical forms of the ZrO2-Li2O complex oxide were investigated as a function of the Li2O concentration in LiCl. ZrO2 was converted to Li2ZrO3 at a Li2O concentration of 0.018 wt%. As the Li2O concentration was increased, Li2ZrO3 was converted to Li6Zr2O7 and then to Li8ZrO6. It is suggested that the removal of Li2ZrO3 from the reduction product is a key point in the pyrochemical treatment of corium.

METHOD OF PRODUCING HAFNIUM-FREE "CRYSTAL-BAR" ZIRCONIUM FROM A CRUDE SOURCE OF ZIRCONIUM

DOE Office of Scientific and Technical Information (OSTI.GOV)

Newnham, I.E.

1959-05-01

Production of Hf-free crystal-bar Zr is described. The crude source of Zr is carbided with carbon in a graphite resistance furnace, then treated with iodide to form ZrI/sub 4/. The ZrI/sub 4/ plus iodide impurities is heated with Zr powder in an evacuated vessel to 500 C. This causes ZrI/sub 3/ to form and be separated from the more volatile HfI/sub 4/ and AlI/sub 3/ which deposit on the condenserlid. The ZrI/sub 3/ is further separated from iodides of Fe, and V by heating to 350 C to re-form ZrI/sub 4/. The morevolatile ZrI/sub 4/ then is collected in puremore » form on another condenser-lid from which it can be removed and reduced to Zr. (T.R.H.)« less

Non-equilibrium oxidation states of zirconium during early stages of metal oxidation

DOE PAGES

Ma, Wen; Senanayake, Sanjaya D.; Herbert, F. William; ...

2015-03-11

The chemical state of Zr during the initial, self-limiting stage of oxidation on single crystal zirconium (0001), with oxide thickness on the order of 1 nm, was probed by synchrotron x-ray photoelectron spectroscopy. Quantitative analysis of the Zr 3d spectrum by the spectrum reconstruction method demonstrated the formation of Zr 1+, Zr 2+, and Zr 3+ as non-equilibrium oxidation states, in addition to Zr 4+ in the stoichiometric ZrO 2. This finding resolves the long-debated question of whether it is possible to form any valence states between Zr 0 and Zr 4+ at the metal-oxide interface. As a result, themore » presence of local strong electric fields and the minimization of interfacial energy are assessed and demonstrated as mechanisms that can drive the formation of these non-equilibrium valence states of Zr.« less

Solid-phase zirconium and fluoride species in alkaline zircaloy cladding waste at Hanford.

PubMed

Reynolds, Jacob G; Huber, Heinz J; Cooke, Gary A; Pestovich, John A

2014-08-15

The United States Department of Energy Hanford Site, near Richland, Washington, USA, processed plutonium between 1944 and 1987. Fifty-six million gallons of waste of various origins remain, including waste from removing zircaloy fuel cladding using the so-called Zirflex process. The speciation of zirconium and fluoride in this waste is important because of the corrosivity and reactivity of fluoride as well as the (potentially) high density of Zr-phases. This study evaluates the solid-phase speciation of zirconium and fluoride using X-ray diffraction (XRD) and scanning electron microscopy with energy dispersive spectroscopy (SEM-EDS). Two waste samples were analyzed: one waste sample that is relatively pure zirconium cladding waste from tank 241-AW-105 and another that is a blend of zirconium cladding wastes and other high-level wastes from tank 241-C-104. Villiaumite (NaF) was found to be the dominant fluoride species in the cladding waste and natrophosphate (Na7F[PO4]2 · 19H2O) was the dominant species in the blended waste. Most zirconium was present as a sub-micron amorphous Na-Zr-O phase in the cladding waste and a Na-Al-Zr-O phase in the blended waste. Some zirconium was present in both tanks as either rounded or elongated crystalline needles of Na-bearing ZrO2 that are up to 200 μm in length. These results provide waste process planners the speciation data needed to develop disposal processes for this waste. Copyright © 2014 Elsevier B.V. All rights reserved.

Separation of Zirconium and Hafnium: A Review

NASA Astrophysics Data System (ADS)

Xu, L.; Xiao, Y.; van Sandwijk, A.; Xu, Q.; Yang, Y.

Zirconium is an ideal material for nuclear reactors due to its low absorption cross-section for thermal neutrons, whereas the typically contained hafnium with strong neutron-absorption is very harmful for zirconium. This paper provides an overview of the processes for separating hafnium from zirconium. The separation processes are roughly classified into hydro- and pyrometallurgical routes. The current dominant zirconium production route involves pyrometallurgical ore cracking, multi-step hydrometallurgical liquid-liquid extraction for hafnium removal and the reduction of zirconium tetrachloride to the pure metal by the Kroll process. The lengthy hydrometallurgical Zr-Hf separation operations leads to high production cost, intensive labour and heavy environmental burden. Using a compact pyrometallurgical separation method can simplify the whole production flowsheet with a higher process efficiency. The known separation methods are discussed based on the following reaction features: redox characteristics, volatility, electrochemical properties and molten salt extraction. The commercially operating extractive distillation process is a significant advance in Zr-Hf separation technology but it suffers from high process maintenance cost. The recently developed new process based on molten salt-metal equilibrium for Zr-Hf separation shows a great potential for industrial application, which is compact for nuclear grade zirconium production starting from crude ore. In the present paper, the available separation technologies are compared. The advantages and disadvantages as well as future directions of research and development for nuclear grade zirconium production are discussed.

Characterisation of well-adhered ZrO2 layers produced on structured reactors using the sonochemical sol-gel method

NASA Astrophysics Data System (ADS)

Jodłowski, Przemysław J.; Chlebda, Damian K.; Jędrzejczyk, Roman J.; Dziedzicka, Anna; Kuterasiński, Łukasz; Sitarz, Maciej

2018-01-01

The aim of this study was to obtain thin zirconium dioxide coatings on structured reactors using the sonochemical sol-gel method. The preparation method of metal oxide layers on metallic structures was based on the synergistic combination of three approaches: the application of ultrasonic irradiation during the synthesis of Zr sol-gel based on a precursor solution containing zirconium(IV) n-propoxide, the addition of stabilszing agents, and the deposition of ZrO2 on the metallic structures using the dip-coating method. As a result, dense, uniform zirconium dioxide films were obtained on the FeCrAlloy supports. The structured reactors were characterised by various physicochemical methods, such as BET, AFM, EDX, XRF, XRD, XPS and in situ Raman spectroscopy. The results of the structural analysis by Raman and XPS spectroscopy confirmed that the metallic surface was covered by a ZrO2 layer without any impurities. SEM/EDX mapping revealed that the deposited ZrO2 covered the metallic support uniformly. The mechanical and high temperature tests showed that the developed ultrasound assisted sol-gel method is an efficient way to obtain thin, well-adhered zirconium dioxide layers on the structured reactors. The prepared metallic supports covered with thin ZrO2 layers may be a good alternative to layered structured reactors in several dynamics flow processes, for example for gas exhaust abatement.

Irradiation-induced effects of proton irradiation on zirconium carbides with different stoichiometries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Y. Huang; B.R. Maier; T.R. Allen

2014-10-01

Zirconium carbide (ZrC) is being considered for utilization in deep burn TRISO fuel particles for hightemperature, gas-cooled reactors. Zirconium carbide has a cubic B1 type crystal structure along with a very high melting point (3420 ?C), exceptional hardness and good thermal and electrical conductivities. Understanding the ZrC irradiation response is crucial for establishing ZrC as an alternative component in TRISO fuel. Until now, very few studies on irradiation effects on ZrC have been released and fundamental aspects of defect evolution and kinetics are not well understood although some atomistic simulations and phenomenological studies have been performed. This work was carriedmore » out to understand the damage evolution in float-zone refined ZrC with different stoichiometries. Proton irradiations at 800 ?C up to doses of 3 dpa were performed on ZrCx (where x ranges from 0.9 to 1.2) to investigate the damage evolution. The irradiation-induced defects, such as density of dislocation loops, at different stoichiometries and doses which were characterized by transmission electron microscopy (TEM) is presented and discussed.« less

Synthesis of ultrafine ZrB2 powders by sol-gel process

NASA Astrophysics Data System (ADS)

Yang, Li-Juan; Zhu, Shi-Zhen; Xu, Qiang; Yan, Zhen-Yu; Liu, Ling

2010-09-01

Ultrafine zirconium diboride (ZrB2) powders have been synthesized by sol-gel process using zirconium oxychloride (ZrOCl2·8H2O), boric acid (H3BO3) and phenolic resin as sources of zirconia, boron oxide and carbon, respectively. The effects of the reaction temperature, B/Zr ratio, holding time, and EtOH/H2O ratio on properties of the synthesized ZrB2 powders were investigated. It was revealed that ultrafine (average crystallite size between 100 and 400 nm) ZrB2 powders can be synthesized with the optimum processing parameters as follows: (i) the ratio of B/Zr is 4; (ii) the solvent is pure ethanol; (iii) the condition of carbothermal reduction heat treatment is at 1550°C for 20 min.

In situ ceramic layer growth on coated fuel particles dispersed in a zirconium metal matrix

DOE Office of Scientific and Technical Information (OSTI.GOV)

Terrani, Kurt A; Silva, G W Chinthaka M; Kiggans, Jim

2013-01-01

The extent and nature of the chemical interaction between the outermost coating layer of coated fuel particles embedded in zirconium metal during fabrication of metal matrix microencapsulated fuels was examined. Various particles with outermost coating layers of pyrocarbon, SiC, and ZrC have been investigated in this study. ZrC-Zr interaction was least substantial while PyC-Zr reaction can be exploited to produce a ZrC layer at the interface in an in situ manner. The thickness of the ZrC layer in the latter case can be controlled by adjusting the time and temperature during processing. The kinetics of ZrC layer growth is significantlymore » faster from what is predicted using literature carbon diffusivity data in ZrC. SiC-Zr interaction is more complex and results in formation of various chemical phases in a layered aggregate morphology at the interface.« less

From Zirconium Nanograins to Zirconia Nanoneedles

PubMed Central

Zalnezhad, E.; Hamouda, A. M. S.; Jaworski, J.; Do Kim, Young

2016-01-01

Combinations of three simple techniques were utilized to gradually form zirconia nanoneedles from zirconium nanograins. First, a physical vapor deposition magnetron sputtering technique was used to deposit pure zirconium nanograins on top of a substrate. Second, an anodic oxidation was applied to fabricate zirconia nanotubular arrays. Finally, heat treatment was used at different annealing temperatures in order to change the structure and morphology from nanotubes to nanowires and subsequently to nanoneedles in the presence of argon gas. The size of the pure zirconium nanograins was estimated to be approximately 200–300 nm. ZrO2 nanotubular arrays with diameters of 70–120 nm were obtained. Both tetragonal and monoclinic ZrO2 were observed after annealing at 450 °C and 650 °C. Only a few tetragonal peaks appeared at 850 °C, while monoclinic ZrO2 was obtained at 900 °C and 950 °C. In assessing the biocompatibility of the ZrO2 surface, the human cell line MDA-MB-231 was found to attach and proliferate well on surfaces annealed at 850 °C and 450 °C; however, the amorphous ZrO2 surface, which was not heat treated, did not permit extensive cell growth, presumably due to remaining fluoride. PMID:27623486

Standardized methods for the production of high specific-activity zirconium-89

PubMed Central

Holland, Jason P.; Sheh, Yiauchung; Lewis, Jason S.

2009-01-01

Zirconium-89 is an attractive metallo-radionuclide for use in immunoPET due to the favorable decay characteristics. Standardized methods for the routine production and isolation of high purity and high specific-activity 89Zr using a small cyclotron are reported. Optimized cyclotron conditions reveal high average yields of 1.52 ± 0.11 mCi/μA·h at a proton beam energy of 15 MeV and current of 15 μA using a solid, commercially available 89Y-foil target (0.1 mm, 100% natural abundance). 89Zr was isolated in high radionuclidic and radiochemical purity (>99.99%) as [89Zr]Zr-oxalate by using a solid-phase hydroxamate resin with >99.5% recovery of the radioactivity. The effective specific-activity of 89Zr was found to be in the range 5.28 – 13.43 mCi/μg (470 – 1195 Ci/mmol) of zirconium. New methods for the facile production of [89Zr]Zr-chloride are reported. Radiolabeling studies using the trihydroxamate ligand desferrioxamine B (DFO) gave 100% radiochemical yields in <15 min. at room temperature and in vitro stability measurements confirmed that [89Zr]Zr-DFO is stable with respect to ligand dissociation in human serum for >7 days. Small-animal PET imaging studies have demonstrated that free 89Zr(IV) ions administered as [89Zr]Zr-chloride accumulate in the liver whilst [89Zr]Zr-DFO is excreted rapidly via the kidneys within <20 min. These results have important implication for the analysis of immunoPET imaging of 89Zr-labeled monoclonal antibodies. The detailed methods described can be easily translated to other radiochemistry facilities and will facilitate the use of 89Zr in both basic science and clinical investigations. PMID:19720285

Microstructure evolution and tensile properties of Zr-2.5 wt.% Nb pressure tubes processed from billets with different microstructures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kapoor, K.; Saratchandran, N.; Muralidharan, K.

1999-02-01

Pressurized heavy water reactors (PHWR) use zirconium-base alloys for their low neutron-absorption cross section, good mechanical strength, low irradiation creep, and high corrosion resistance in reactor atmospheres. Starting with identical ingots, billets having different microstructures were obtained by three different processing methods for fabrication of Zr-2.5 wt%Nb pressure tubes., The billets were further processed by hot extrusion and cold Pilger tube reducing to the finished product. Microstructural characterization was done at each stage of processing. The effects of the initial billet microstructure on the intermediate and final microstructure and mechanical property results were determined. It was found that the structuremore » at each stage and the final mechanical properties depend strongly on the initial billet microstructure. The structure at the final stage consists of elongated alpha zirconium grains with a network of metastable beta zirconium phase. Some of this metastable phase transforms into stable beta niobium during thermomechanical processing. Billets with quenched structure resulted in less beta niobium at the final stage. The air cooled billets resulted in a large amount of beta niobium. The tensile properties, especially the percentage elongation, were found to vary for the different methods. Higher percentage elongation was observed for billets having quenched structure. Extrusion and forging did not produce any characteristic differences in the properties. The results were used to select a process flow sheet which yields the desired mechanical properties with suitable microstructure in the final product.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Campbell, Keri R.; Judge, Elizabeth J.; Barefield, James E.

We show the analysis of light water reactor simulated used nuclear fuel using laser-induced breakdown spectroscopy (LIBS) is explored using a simplified version of the main oxide phase. The main oxide phase consists of the actinides, lanthanides, and zirconium. The purpose of this study is to develop a rapid, quantitative technique for measuring zirconium in a uranium dioxide matrix without the need to dissolve the material. A second set of materials including cerium oxide is also analyzed to determine precision and limit of detection (LOD) using LIBS in a complex matrix. Two types of samples are used in this study:more » binary and ternary oxide pellets. The ternary oxide, (U,Zr,Ce)O 2 pellets used in this study are a simplified version the main oxide phase of used nuclear fuel. The binary oxides, (U,Ce)O 2 and (U,Zr)O 2 are also examined to determine spectral emission lines for Ce and Zr, potential spectral interferences with uranium and baseline LOD values for Ce and Zr in a UO 2 matrix. In the spectral range of 200 to 800 nm, 33 cerium lines and 25 zirconium lines were identified and shown to have linear correlation values (R 2) > 0.97 for both the binary and ternary oxides. The cerium LOD in the (U,Ce)O 2 matrix ranged from 0.34 to 1.08 wt% and 0.94 to 1.22 wt% in (U,Ce,Zr)O 2 for 33 of Ce emission lines. The zirconium limit of detection in the (U,Zr)O 2 matrix ranged from 0.84 to 1.15 wt% and 0.99 to 1.10 wt% in (U,Ce,Zr)O 2 for 25 Zr lines. Finally, the effect of multiple elements in the plasma and the impact on the LOD is discussed.« less

Pre- and post-irradiation characterization and properties measurements of ZrC coated surrogate TRISO particles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vasudevamurthy, Gokul; Katoh, Yutai; Hunn, John D

2010-09-01

Zirconium carbide is a candidate to either replace or supplement silicon carbide as a coating material in TRISO fuel particles for high temperature gas-cooled reactor fuels. Six sets of ZrC coated surrogate microsphere samples, fabricated by the Japan Atomic Energy Agency using the fluidized bed chemical vapor deposition method, were irradiated in the High Flux Isotope Reactor at the Oak Ridge National Laboratory. These developmental samples available for the irradiation experiment were in conditions of either as-fabricated coated particles or particles that had been heat-treated to simulate the fuel compacting process. Five sets of samples were composed of nominally stoichiometricmore » compositions, with the sixth being richer in carbon (C/Zr = 1.4). The samples were irradiated at 800 and 1250 C with fast neutron fluences of 2 and 6 dpa. Post-irradiation, the samples were retrieved from the irradiation capsules followed by microstructural examination performed at the Oak Ridge National Laboratory's Low Activation Materials Development and Analysis Laboratory. This work was supported by the US Department of Energy Office of Nuclear Energy's Advanced Gas Reactor program as part of International Nuclear Energy Research Initiative collaboration with Japan. This report includes progress from that INERI collaboration, as well as results of some follow-up examination of the irradiated specimens. Post-irradiation examination items included microstructural characterization, and nanoindentation hardness/modulus measurements. The examinations revealed grain size enhancement and softening as the primary effects of both heat-treatment and irradiation in stoichiometric ZrC with a non-layered, homogeneous grain structure, raising serious concerns on the mechanical suitability of these particular developmental coatings as a replacement for SiC in TRISO fuel. Samples with either free carbon or carbon-rich layers dispersed in the ZrC coatings experienced negligible grain size enhancement during both heat treatment and irradiation. However, these samples experienced irradiation induced softening similar to stoichiometric ZrC samples.« less

The preparation of Zr-deuteride and phase stability studies of the Zr-D system

NASA Astrophysics Data System (ADS)

Maimaitiyili, T.; Steuwer, A.; Bjerkén, C.; Blomqvist, J.; Hoelzel, M.; Ion, J. C.; Zanellato, O.

2017-03-01

Deuteride phases in the zirconium-deuterium system in the temperature range 25-286 °C have been studied in-situ by high resolution neutron diffraction. The study primarily focused on observations of δ→γ transformation at 180 °C, and the peritectoid reaction α + δ ↔ γ at 255 °C in commercial grade Zr powder that was deuterated to a deuterium/Zr ratio of one to one. A detailed description of the zirconium deuteride preparation route by high temperature gas loading is also described. The lattice parameters of α-Zr, δ-ZrDx and ε-ZrDx were determined by whole pattern crystal structure analysis, using Rietveld and Pawley refinements, and are in good agreement with values reported in the literature. The controversial γ-hydride phase was observed both in-situ and ex-situ in deuterated Zr powder after a heat treatment at 286 °C and slow cooling.

Nanoindentation study of bulk zirconium hydrides at elevated temperatures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cinbiz, Mahmut Nedim; Balooch, Mehdi; Hu, Xunxiang

Here, the mechanical properties of zirconium hydrides was studied using nano-indentation technique at a temperature range of 25 – 400 °C. Temperature dependency of reduced elastic modulus and hardness of δ- and ε-zirconium hydrides were obtained by conducting nanoindentation experiments on the bulk hydride samples with independently heating capability of indenter and heating stage. The reduced elastic modulus of δ-zirconium hydride (H/Zr ratio =1.61) decreased from ~113 GPa to ~109 GPa while temperature increased from room temperature to 400°C. For ε-zirconium hydrides (H/Zr ratio=1.79), the reduced elastic modulus decreased from 61 GPa to 54 GPa as temperature increased from roommore » temperature to 300 °C. Whereas, hardness of δ-zirconium hydride significantly decreased from 4.1 GPa to 2.41 GPa when temperature increased from room temperature to 400 °C. Similarly, hardness of ε-zirconium hydride decreased from 3.06 GPa to 2.19 GPa with temperature increase from room temperature to 300°C.« less

Nanoindentation study of bulk zirconium hydrides at elevated temperatures

DOE PAGES

Cinbiz, Mahmut Nedim; Balooch, Mehdi; Hu, Xunxiang; ...

2017-08-02

Here, the mechanical properties of zirconium hydrides was studied using nano-indentation technique at a temperature range of 25 – 400 °C. Temperature dependency of reduced elastic modulus and hardness of δ- and ε-zirconium hydrides were obtained by conducting nanoindentation experiments on the bulk hydride samples with independently heating capability of indenter and heating stage. The reduced elastic modulus of δ-zirconium hydride (H/Zr ratio =1.61) decreased from ~113 GPa to ~109 GPa while temperature increased from room temperature to 400°C. For ε-zirconium hydrides (H/Zr ratio=1.79), the reduced elastic modulus decreased from 61 GPa to 54 GPa as temperature increased from roommore » temperature to 300 °C. Whereas, hardness of δ-zirconium hydride significantly decreased from 4.1 GPa to 2.41 GPa when temperature increased from room temperature to 400 °C. Similarly, hardness of ε-zirconium hydride decreased from 3.06 GPa to 2.19 GPa with temperature increase from room temperature to 300°C.« less

Synthesis, Structure, and Selective Gas Adsorption of a Single-Crystalline Zirconium Based Microporous Metal–Organic Framework

DOE PAGES

Wang, Hao; Wang, Qining; Teat, Simon J.; ...

2017-02-15

Porous metal-organic framework (MOF) materials with high thermal and water stability are desirable for various adsorption based applications. Early transition metal based MOFs such as those built on zirconium metal have been well recognized for their excellent stability toward heat and/or moisture. However, the difficulty growing large single crystals makes their structural characterization challenging. Herein we report a porous Zr-MOF, [Zr 6O 4(OH) 4(cca) 6] (Zr-cca), which is assembled from zirconium and 4-carboxycinnamic acid (H 2cca) under solvothermal conditions. Single crystal X-ray diffraction analysis reveals that the structure of Zr-cca is isoreticular to the prototype zirconium based MOF, UiO-66. Zr-ccamore » shows permanent porosity upon removal of solvent molecules initially residing inside the pores, with a BET surface area of 1178 m 2/g. As expected, it exhibits good thermal stability (stable up to 400 °C) and high resistance to acidity over a wide pH range. Evaluation of its gas adsorption performance on various hydrocarbons and fluorocarbons indicates that it preferentially adsorbs C 3 and C 4 hydrocarbons over C 2 analogues. At 30°C Zr-cca takes up more than 50 wt % of perfluorohexane and the adsorption-desorption process is fully recyclable. We have compared this material with UiO-66 and studied the underlying reasons for the difference in their adsorption performance toward perfluorohexane.« less

Effects of Rapid Thermal Annealing on the Structural, Electrical, and Optical Properties of Zr-Doped ZnO Thin Films Grown by Atomic Layer Deposition.

PubMed

Wu, Jingjin; Zhao, Yinchao; Zhao, Ce Zhou; Yang, Li; Lu, Qifeng; Zhang, Qian; Smith, Jeremy; Zhao, Yongming

2016-08-13

The 4 at. % zirconium-doped zinc oxide (ZnO:Zr) films grown by atomic layer deposition (ALD) were annealed at various temperatures ranging from 350 to 950 °C. The structural, electrical, and optical properties of rapid thermal annealing (RTA) treated ZnO:Zr films have been evaluated to find out the stability limit. It was found that the grain size increased at 350 °C and decreased between 350 and 850 °C, while creeping up again at 850 °C. UV-vis characterization shows that the optical band gap shifts towards larger wavelengths. The Hall measurement shows that the resistivity almost keeps constant at low annealing temperatures, and increases rapidly after treatment at 750 °C due to the effect of both the carrier concentration and the Hall mobility. The best annealing temperature is found in the range of 350-550 °C. The ZnO:Zr film-coated glass substrates show good optical and electrical performance up to 550 °C during superstrate thin film solar cell deposition.

Effects of Rapid Thermal Annealing on the Structural, Electrical, and Optical Properties of Zr-Doped ZnO Thin Films Grown by Atomic Layer Deposition

PubMed Central

Wu, Jingjin; Zhao, Yinchao; Zhao, Ce Zhou; Yang, Li; Lu, Qifeng; Zhang, Qian; Smith, Jeremy; Zhao, Yongming

2016-01-01

The 4 at. % zirconium-doped zinc oxide (ZnO:Zr) films grown by atomic layer deposition (ALD) were annealed at various temperatures ranging from 350 to 950 °C. The structural, electrical, and optical properties of rapid thermal annealing (RTA) treated ZnO:Zr films have been evaluated to find out the stability limit. It was found that the grain size increased at 350 °C and decreased between 350 and 850 °C, while creeping up again at 850 °C. UV–vis characterization shows that the optical band gap shifts towards larger wavelengths. The Hall measurement shows that the resistivity almost keeps constant at low annealing temperatures, and increases rapidly after treatment at 750 °C due to the effect of both the carrier concentration and the Hall mobility. The best annealing temperature is found in the range of 350–550 °C. The ZnO:Zr film-coated glass substrates show good optical and electrical performance up to 550 °C during superstrate thin film solar cell deposition. PMID:28773816

Zirconium Ions Up-Regulate the BMP/SMAD Signaling Pathway and Promote the Proliferation and Differentiation of Human Osteoblasts

PubMed Central

Chen, Yongjuan; Roohani-Esfahani, Seyed-Iman; Lu, ZuFu; Zreiqat, Hala; Dunstan, Colin R.

2015-01-01

Zirconium (Zr) is an element commonly used in dental and orthopedic implants either as zirconia (ZrO2) or in metal alloys. It can also be incorporated into calcium silicate-based ceramics. However, the effects of in vitro culture of human osteoblasts (HOBs) with soluble ionic forms of Zr have not been determined. In this study, primary culture of human osteoblasts was conducted in the presence of medium containing either ZrCl4 or Zirconium (IV) oxynitrate (ZrO(NO3)2) at concentrations of 0, 5, 50 and 500 µM, and osteoblast proliferation, differentiation and calcium deposition were assessed. Incubation of human osteoblast cultures with Zr ions increased the proliferation of human osteoblasts and also gene expression of genetic markers of osteoblast differentiation. In 21 and 28 day cultures, Zr ions at concentrations of 50 and 500 µM increased the deposition of calcium phosphate. In addition, the gene expression of BMP2 and BMP receptors was increased in response to culture with Zr ions and this was associated with increased phosphorylation of SMAD1/5. Moreover, Noggin suppressed osteogenic gene expression in HOBs co-treated with Zr ions. In conclusion, Zr ions appear able to induce both the proliferation and the differentiation of primary human osteoblasts. This is associated with up-regulation of BMP2 expression and activation of BMP signaling suggesting this action is, at least in part, mediated by BMP signaling. PMID:25602473

On the mechanism of zirconium nitride formation by zirconium, zirconia and yttria burning in air

NASA Astrophysics Data System (ADS)

Malikova, Ekaterina; Pautova, Julia; Gromov, Alexander; Monogarov, Konstantin; Larionov, Kirill; Teipel, Ulrich

2015-10-01

The combustion of Zr and (Zr+ZrO2) powdery mixtures in air was accompanied by major ZrN stabilization. The synthesis of cheap ZrN with the high yield in air was facile and utile. The influence of Y2O3 additive on the content of ZrN the solid combustion products (SCP) was investigated. The reagents and SCP were analyzed by BET, DTA-TGA, XRD, SEM and EDS. Burning temperature was measured by thermal imager. The yield of ZrN in the SCP has been varied by the time regulation of the combustion process. The burning samples were quenched at a certain time to avoid the re-oxidation of the obtained ZrN by oxygen. The quenching of the burned (Zr+ZrO2) samples with the Y2O3 additive was allowed increasing the ZrN yield in SCP up to 66 wt%. The chemical mechanism of ZrN formation in air was discussed and the probable source of ZrN massive formation is suggested.

A mediator-free glucose biosensor based on glucose oxidase/chitosan/α-zirconium phosphate ternary biocomposite.

PubMed

Liu, Li-Min; Wen, Jiwu; Liu, Lijun; He, Deyong; Kuang, Ren-yun; Shi, Taqing

2014-01-15

A novel glucose oxidase/chitosan/α-zirconium phosphate (GOD/chitosan/α-ZrP) ternary biocomposite was prepared by co-intercalating glucose oxidase (GOD) and chitosan into the interlayers of α-zirconium phosphate (α-ZrP) via a delamination-reassembly procedure. The results of X-ray diffraction, infrared spectroscopy, circular dichroism, and ultraviolet spectrum characterizations indicated not only the layered and hybrid structure of the GOD/chitosan/α-ZrP ternary biocomposite but also the recovered activity of the intercalated GOD improved by the co-intercalated chitosan. By depositing the GOD/chitosan/α-ZrP biocomposite film onto a glassy carbon electrode, the direct electrochemistry of the intercalated GOD was achieved with a fast electron transfer rate constant, k(s), of 7.48±3.52 s(-1). Moreover, this GOD/chitosan/α-ZrP biocomposite modified electrode exhibited a sensitive response to glucose in the linear range of 0.25-8.0 mM (R=0.9994, n=14), with a determination limit of 0.076 mM. Copyright © 2013 Elsevier Inc. All rights reserved.

Rational Design of Zirconium-doped Titania Photocatalysts with Synergistic Brønsted Acidity and Photoactivity.

PubMed

Ma, Runyuan; Wang, Liang; Zhang, Bingsen; Yi, Xianfeng; Zheng, Anmin; Deng, Feng; Yan, Xuhua; Pan, Shuxiang; Wei, Xiao; Wang, Kai-Xue; Su, Dang Sheng; Xiao, Feng-Shou

2016-10-06

The preparation of photocatalysts with high activities under visible-light illumination is challenging. We report the rational design and construction of a zirconium-doped anatase catalyst (S-Zr-TiO 2 ) with Brønsted acidity and photoactivity as an efficient catalyst for the degradation of phenol under visible light. Electron microscopy images demonstrate that the zirconium sites are uniformly distributed on the sub-10 nm anatase crystals. UV-visible spectrometry indicates that the S-Zr-TiO 2 is a visible-light-responsive catalyst with narrower band gap than conventional anatase. Pyridine-adsorption infrared and acetone-adsorption 13 C NMR spectra confirm the presence of Brønsted acidic sites on the S-Zr-TiO 2 sample. Interestingly, the S-Zr-TiO 2 catalyst exhibits high catalytic activity in the degradation of phenol under visible-light illumination, owing to a synergistic effect of the Brønsted acidity and photoactivity. Importantly, the S-Zr-TiO 2 shows good recyclability. © 2016 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Zirconium amine tris(phenolate): A more effective initiator for biomedical lactide.

PubMed

Jones, Matthew D; Wu, Xujun; Chaudhuri, Julian; Davidson, Matthew G; Ellis, Marianne J

2017-11-01

Here a zirconium amine tris(phenolate) is used as the initiator for the production of polylactide for biomedical applications, as a replacement for a tin initiator (usually tin octanoate). The ring opening polymerization (ROP) was carried out in the melt at 130°C. The zirconium-catalyzed PLA (PLA-Zr) required 30min, resulting in a polydispersity index (PDI) of 1.17, compared to 1h and PDI=1.77 for tin-catalyzed PLA (PLA-Sn). PLA-Zr and PLA-Sn supported osteosarcoma cell (MG63) culture to the same extent (cell number, morphology, extracellular matrix production and osteogenic function) until day 14 when the PLA-Zr showed increased cell number, overall extracellular matrix production and osteogenic function. To conclude, the reduction in reaction time, controllable microstructure and biologically benign nature of the zirconium amine tris(phenolate) initiator shows that it is a more effective initiator for ROP of polylactide for biomedical applications. Copyright © 2017 Elsevier B.V. All rights reserved.

Phase Transformation Temperatures and Solute Redistribution in a Quaternary Zirconium Alloy

NASA Astrophysics Data System (ADS)

Cochrane, C.; Daymond, M. R.

2018-05-01

This study investigates the phase stability and redistribution of solute during heating and cooling of a quaternary zirconium alloy, Excel (Zr-3.2Sn-0.8Mo-0.8Nb). Time-of-flight neutron diffraction data are analyzed using a novel Vegard's law-based approach to determine the phase fractions and location of substitutional solute atoms in situ during heating from room temperature up to 1050 °C. It is seen that this alloy exhibits direct nucleation of the β Zr phase from martensite during tempering, and stable retention of the β Zr phase to high temperatures, unlike other two-phase zirconium alloys. The transformation strains resulting from the α \\leftrightarrow β transformation are shown to have a direct impact on the development of microstructure and crystallographic texture.

Primary radiation damage of Zr-0.5%Nb binary alloy: atomistic simulation by molecular dynamics method

NASA Astrophysics Data System (ADS)

Tikhonchev, M.; Svetukhin, V.; Kapustin, P.

2017-09-01

Ab initio calculations predict high positive binding energy (˜1 eV) between niobium atoms and self-interstitial configurations in hcp zirconium. It allows the expectation of increased niobium fraction in self-interstitials formed under neutron irradiation in atomic displacement cascades. In this paper, we report the results of molecular dynamics simulation of atomic displacement cascades in Zr-0.5%Nb binary alloy and pure Zr at the temperature of 300 K. Two sets of n-body interatomic potentials have been used for the Zr-Nb system. We consider a cascade energy range of 2-20 keV. Calculations show close estimations of the average number of produced Frenkel pairs in the alloy and pure Zr. A high fraction of Nb is observed in the self-interstitial configurations. Nb is mainly detected in single self-interstitial configurations, where its fraction reaches tens of percent, i.e. more than its tenfold concentration in the matrix. The basic mechanism of this phenomenon is the trapping of mobile self-interstitial configurations by niobium. The diffusion of pure zirconium and mixed zirconium-niobium self-interstitial configurations in the zirconium matrix at 300 K has been simulated. We observe a strong dependence of the estimated diffusion coefficients and fractions of Nb in self-interstitials produced in displacement cascades on the potential.

In-beam studies of sup 96 Zr and sup 98 Zr: Collective excitations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Henry, E.A.; Meyer, R.A.; Aprahamian, A.

1988-04-18

Nearly two decades ago signatures of deformation in the ground state bands of {sup 100}Zr and {sup 102}Zr were identified, and the rapid change in the deformation of heavy zirconium nuclei noted. It is now well accepted that the short-range proton-neutron interaction between the 1g{sub 9/2} and 1g{sub 7/2} spin-orbit partners plays an important role in producing ground state deformation in this region. Nevertheless, recent studies of zirconium nuclei, including those in the transition region, continue to refine our understanding of the interplay between single-particle and collective degrees of freedom. In this report we discuss some aspects of the levelmore » structures of {sup 96}Zr and {sup 98}Zr with emphasis on collective excitations. 18 refs., 2 tabs.« less

Oxygen Migration and Local Structural Changes with Schottky Defects in Pure Zirconium Oxide Crystals

NASA Astrophysics Data System (ADS)

Terada, Yayoi; Mohri, Tetsuo

2018-05-01

By employing the Buckingham potential, we performed classical molecular-dynamics computer simulations at constant pressure and temperature for a pure ZrO2 crystal without any vacancies and for a pure ZrO2 crystal containing zirconium vacancies and oxygen vacancies. We examined the positions of atoms and vacancies in the steady state, and we investigated the migration behavior of atoms and the local structure of vacancies of the pure ZrO2 crystal. We found that Schottky defects (aggregates consisting of one zirconium vacancy with an effective charge of -4 and two oxygen vacancies each with an effective charge of +2 to maintain charge neutrality) are the main defects formed in the steady state in cubic ZrO2, and that oxygen migration occurs through a mechanism involving vacancies on the oxygen sublattice near such defects. We also found that several oxygen atoms near each defect are displaced far from the sublattice site and induce oxygen migration.

Divergent Pathways Involving 1,3-Dipolar Addition and N-N Bond Splitting of an Organic Azide across a Zirconium Methylidene.

PubMed

Kurogi, Takashi; Mane, Manoj V; Zheng, Shuai; Carroll, Patrick J; Baik, Mu-Hyun; Mindiola, Daniel J

2018-02-12

The zirconium methylidene (PNP)Zr=CH 2 (OAr) (1) reacts with N 3 Ad to give two products (PNP)Zr=NAd(OAr) (2) and (PNP)Zr(η 2 -N=NAd)(N=CH 2 )(OAr) (3), both resulting from a common cycloaddition intermediate (PNP)Zr(CH 2 N 3 Ad)(OAr) (A). Using a series of control experiments in combination with DFT calculations, it was found that 2 results from a nitrene by a carbene metathesis reaction in which N 2 acts as a delivery vehicle and forms N 2 CH 2 as a side product. In the case of 3, N-N bond splitting of the azide at the α-position allowed the isolation of a rare example of a parent ketimide complex of zirconium. Isotopic labeling studies and solid-state X-ray analysis are presented for 2 and 3, in addition to an independent synthesis for the former. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Observations on the brittle to ductile transition temperatures of B2 nickel aluminides with and without zirconium

NASA Technical Reports Server (NTRS)

Raj, S. V.; Noebe, R. D.; Bowman, R.

1989-01-01

The effect of a zirconium addition (0.05 at. pct) to a stoichiometric NiAl alloy on the brittle-to-ductile transition temperature (BDTT) of this alloy was investigated. Constant velocity tensile tests were conducted to fracture between 300 and 1100 K under initial strain rate 0.00014/sec, and the true stress and true strain values were determined from plots of load vs time after subtracting the elastic strain. The inelastic strain was measured under a traveling microscope. Microstructural characterization of as-extruded and fractured specimens was carried out by SEM and TEM. It was found that, while the addition of 0.05 at. pct Zr strengthened the NiAl alloy, it increased its BDTT; this shift in the BDTT could not be attributed either to variations in grain size or to impurity contents. Little or no room-temperature ductility was observed for either alloy.

Design and development of novel MRI compatible zirconium- ruthenium alloys with ultralow magnetic susceptibility.

PubMed

Li, H F; Zhou, F Y; Li, L; Zheng, Y F

2016-04-19

In the present study, novel MRI compatible zirconium-ruthenium alloys with ultralow magnetic susceptibility were developed for biomedical and therapeutic devices under MRI diagnostics environments. The results demonstrated that alloying with ruthenium into pure zirconium would significantly increase the strength and hardness properties. The corrosion resistance of zirconium-ruthenium alloys increased significantly. High cell viability could be found and healthy cell morphology observed when culturing MG 63 osteoblast-like cells and L-929 fibroblast cells with zirconium-ruthenium alloys, whereas the hemolysis rates of zirconium-ruthenium alloys are <1%, much lower than 5%, the safe value for biomaterials according to ISO 10993-4 standard. Compared with conventional biomedical 316L stainless steel, Co-Cr alloys and Ti-based alloys, the magnetic susceptibilities of the zirconium-ruthenium alloys (1.25 × 10(-6) cm(3)·g(-1)-1.29 × 10(-6) cm(3)·g(-1) for zirconium-ruthenium alloys) are ultralow, about one-third that of Ti-based alloys (Ti-6Al-4V, ~3.5 × 10(-6) cm(3)·g(-1), CP Ti and Ti-6Al-7Nb, ~3.0 × 10(-6) cm(3)·g(-1)), and one-sixth that of Co-Cr alloys (Co-Cr-Mo, ~7.7 × 10(-6) cm(3)·g(-1)). Among the Zr-Ru alloy series, Zr-1Ru demonstrates enhanced mechanical properties, excellent corrosion resistance and cell viability with lowest magnetic susceptibility, and thus is the optimal Zr-Ru alloy system as therapeutic devices under MRI diagnostics environments.

Nuclear magnetic resonance analysis and activation energy spectrum of the irreversible structural relaxation of amorphous zirconium tungstate

NASA Astrophysics Data System (ADS)

Miotto, F.; Rech, G. L.; Turatti, A. M.; Catafesta, J.; Zorzi, J. E.; Pereira, A. S.; Perottoni, C. A.

2018-03-01

Zirconium tungstate undergoes a sequence of phase transitions from cubic (α -ZrW2O8 ) to orthorhombic (γ -ZrW2O8 ) to amorphous (a -ZrW2O8 ) upon increasing pressure at room temperature. The amorphous phase is known to undergo anomalous endothermic recrystallization into a high-temperature β -ZrW2O8 phase above 600∘C at ambient pressure (and back to α -ZrW2O8 when brought to room temperature). The endothermic recrystallization of a -ZrW2O8 is preceded by an irreversible exothermic structural relaxation. New W-O bonds are formed upon amorphization, continuing a tendency of increasing W coordination number in going from α to γ -ZrW2O8 . In fact, contrarily to α -ZrW2O8 , in which one-quarter of the oxygen atoms are bonded only to one W (terminal oxygens), previous works found no evidence of single-bonded oxygen atoms in a -ZrW2O8 . It thus could be argued that the irreversible character of the structural relaxation of a -ZrW2O8 is due to W-O bond breaking upon annealing of the amorphous phase. To test this hypothesis, x-ray diffraction, 17O magic-angle spinning NMR, Raman, and far-infrared analyses were performed on samples of amorphous zirconium tungstate previously annealed to increasingly higher temperatures, looking for any evidence of features that could be assigned to the presence of terminal oxygen atoms. No evidence of single-bonded oxygen was found before the onset of recrystallization. Furthermore, the kinetics of the structural relaxation of a -ZrW2O8 is consistent with a continuous spectrum of activation energy, spanning all the range from 1 to 2.5 eV . These findings suggest that the structural relaxation of amorphous zirconium tungstate, however irreversible, is not accompanied by W-O bond breaking, but most probably characterized by a succession of (mostly) irreversible local atomic rearrangements.

Fourier Transform IR Spectroscopic Study of Nano-ZrO2 + Nano-SiO2 + Nano-H2O Systems Upon the Action of Gamma Radiation

NASA Astrophysics Data System (ADS)

Agayev, T. N.; Gadzhieva, N. N.; Melikova, S. Z.

2018-05-01

The radiation decomposition of water in a nano-ZrO2 + nano-SiO2 + H2O system at 300 K by the action of gamma radiation has been studied by Fourier transform IR spectroscopy. Water adsorption in the zirconium and silicon nanooxides is attributed to molecular and dissociative mechanisms. Active intermediates in this radiation-induced heterogeneous decomposition of water were detected including zirconium and silicon hydrides and hydroxyl groups. Variation in the ratio of ZrO2 and SiO2 nanopowders was shown to lead to change in their radiation catalytic activity compared to initial ZrO2.

Manufacturing process to reduce large grain growth in zirconium alloys

DOEpatents

Rosecrans, P.M.

1984-08-01

It is an object of the present invention to provide a procedure for desensitizing zirconium-based alloys to large grain growth (LGG) during thermal treatment above the recrystallization temperature of the alloy. It is a further object of the present invention to provide a method for treating zirconium-based alloys which have been cold-worked in the range of 2 to 8% strain to reduce large grain growth. It is another object of the present invention to provide a method for fabricating a zirconium alloy clad nuclear fuel element wherein the zirconium clad is resistant to large grain growth.

Mahlmoodite, FeZr(PO4).4H2O, a new iron zirconium phosphate mineral from Wilson Springs, Arkansas

USGS Publications Warehouse

Milton, C.; McGee, J.J.; Evans, H.T.

1993-01-01

Small (<0.5 mm) cream white spheres observed in V ore have been identified as ferrous zirconium phosphate tetrahedrate, FeZr(PO4)2.4H2O. This new mineral, named mahlmoodite, occurs as spherules of radiating fibers usually perched on crystals of pyroxene in vugs. The optical and crystallographic properties of mahlmoodite are described. -after Authors

Enhancing the performance of single-chambered microbial fuel cell using manganese/palladium and zirconium/palladium composite cathode catalysts.

PubMed

Jadhav, Dipak A; Deshpande, Parag A; Ghangrekar, Makarand M

2017-08-01

Application of ZrO 2 , MnO 2 , palladium, palladium-substituted-zirconium oxide (Zr 0.98 Pd 0.02 O 2 ) and palladium-substituted-manganese oxide (Mn 0.98 Pd 0.02 O 2 ) cathode catalysts in a single-chambered microbial fuel cell (MFC) was explored. The highest power generation (1.28W/m 3 ) was achieved in MFC with Mn 0.98 Pd 0.02 O 2 catalyst, which was higher than that with MnO 2 (0.58W/m 3 ) alone; whereas, MFC having Zr 0.98 Pd 0.02 O 2 catalyzed cathode and non-catalyzed cathode produced powers of 1.02 and 0.23W/m 3 , respectively. Also, low-cost zirconium-palladium-composite showed better catalytic activity and capacitance over ZrO 2 with 20A/m 3 current production and demonstrated its suitability for MFC applications. Cyclic voltammetry analyses showed higher well-defined redox peaks in composite catalysts (Mn/Zr-Pd-C) over other catalyzed MFCs containing MnO 2 or ZrO 2 . Electrochemical behaviour of composite catalysts on cathode showed higher availability of adsorption sites for oxygen reduction and, hence, enhanced the rate of cathodic reactions. Thus, Mn/Zr-Pd-C-based composite catalysts exhibited superior cathodic performance and could be proposed as alternatives to costly Pd-catalyst for field applications. Copyright © 2017 Elsevier Ltd. All rights reserved.

Evaluation of coated metallic bipolar plates for polymer electrolyte membrane fuel cells

NASA Astrophysics Data System (ADS)

Yoon, Wonseok; Huang, Xinyu; Fazzino, Paul; Reifsnider, Kenneth L.; Akkaoui, Michael A.

Metallic bipolar plates for polymer electrolyte membrane (PEM) fuel cells typically require coatings for corrosion protection. Other requirements for the corrosion protective coatings include low electrical contact resistance, good mechanical robustness, low material and fabrication cost. The authors have evaluated a number of protective coatings deposited on stainless steel substrates by electroplating and physical vapor deposition (PVD) methods. The coatings are screened with an electrochemical polarization test for corrosion resistance; then the contact resistance test was performed on selected coatings. The coating investigated include Gold with various thicknesses (2 nm, 10 nm, and 1 μm), Titanium, Zirconium, Zirconium Nitride (ZrN), Zirconium Niobium (ZrNb), and Zirconium Nitride with a Gold top layer (ZrNAu). The substrates include three types of stainless steel: 304, 310, and 316. The results show that Zr-coated samples satisfy the DOE target for corrosion resistance at both anode and cathode sides in typical PEM fuel cell environments in the short-term, but they do not meet the DOE contact resistance goal. Very thin gold coating (2 nm) can significantly decrease the electrical contact resistance, however a relatively thick gold coating (>10 nm) with our deposition method is necessary for adequate corrosion resistance, particularly for the cathode side of the bipolar plate.

Microstructure evolution and tensile properties of Zr-2.5wt%Nb pressure tubes processed from billets with different microstructures

NASA Astrophysics Data System (ADS)

Kapoor, K.; Saratchandran, N.; Muralidharan, K.

1999-02-01

Starting with identical ingots, billets having different microstructures were obtained by three different processing methods for fabrication of Zr-2.5wt%Nb pressure tubes. The billets were further processed by hot extrusion and cold Pilger tube reducing to the finished product. Microstructural characterization was done at each stage of processing. The effects of the initial billet microstructure on the intermediate and final microstructure and mechanical property results were determined. It was found that the structure at each stage and the final mechanical properties depend strongly on the initial billet microstructure. The structure at the final stage consists of elongated alpha zirconium grains with a network of metastable beta zirconium phase. Some of this metastable phase transforms into stable beta niobium during thermomechanical processing. Billets with quenched structure resulted in less beta niobium at the final stage. The air cooled billets resulted in a large amount of beta niobium. The tensile properties, especially the percentage elongation, were found to vary for the different methods. Higher percentage elongation was observed for billets having quenched structure. Extrusion and forging did not produce any characteristic differences in the properties. The results were used to select a process flow sheet which yields the desired mechanical properties with suitable microstructure in the final product.

Atom economy and green elimination of nitric oxide using ZrN powders.

PubMed

Chen, Ning; Wang, Jigang; Yin, Wenyan; Li, Zhen; Li, Peishen; Guo, Ming; Wang, Qiang; Li, Chunlei; Wang, Changzheng; Chen, Shaowei

2018-05-01

Nitric oxide (NO) may cause serious environmental problems, such as acid rain, haze weather, global warming and even death. Herein, a new low-cost, highly efficient and green method for the elimination of NO using zirconium nitride (ZrN) is reported for the first time, which does not produce any waste or any by-product. Relevant experimental parameters, such as reaction temperature and gas concentration, were investigated to explore the reaction mechanism. Interestingly, NO can be easily decomposed into nitrogen (N 2 ) by ZrN powders at 600°C with ZrN simultaneously transformed into zirconium dioxide (ZrO 2 ) gradually. The time for the complete conversion of NO into N 2 was approximately 14 h over 0.5 g of ZrN at a NO concentration of 500 ppm. This green elimination process of NO demonstrated good atom economy and practical significance in mitigating environmental problems.

Accumulation of zirconium phosphate by a Serratia sp.: a benign system for the removal of radionuclides from aqueous flows.

PubMed

Mennan, Claire; Paterson-Beedle, Marion; Macaskie, Lynne E

2010-10-01

Metal phosphate deposited enzymatically on Serratia sp. has been used successfully for the removal of radionuclides from aqueous flows. Previous studies using biogenic hydrogen uranyl phosphate (HUP) on Serratia sp. biofilm showed removal of 100% of (90)Sr, (137)Cs, and (60)Co via their intercalation into biogenic HUP crystals. Zirconium phosphates (ZrP) offer a potential non-toxic and non-radioactive alternative to HUP for water decontamination. A method was developed for biomanufacturing ZrP. Biogenic ZrP removed ca. 100% of Sr(2+) and Co(2+) (0.5 mM) from solutions to a molar ratio at saturation of ca. 1:0.6 for both Zr:Sr and Zr:Co. The potential for drinking water decontamination via bio-ZrP is discussed with respect to bio-HUP and also other commercially available materials.

THE DETERMINATION OF TRACES OF BORON IN ZIRCONIUM METAL AND ZIRCONIUM ALLOYS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hayes, M.R.; Metcalfe, J.

1962-01-01

A general procedure is given for the determination of B, down to 0.2 ppm, in Zr and Zr alloys. Separation of the B is not necessary, the B-curcumin complex being formed directly in an aliquot of the metal sulfate solution. An interference effect has been noted when analyzing Zr alloys containing Sn. The interference is caused by an insoluble compound of curcumin which separates and has similar properties to the B-curcumin complex. This source of interference is, however, readily eliminated during the procedure for the determination of B. The procedure has been applied to the determination of B in puremore » Zr, zr--0.5% Cu-- 0.5% MO, and Zr--1.5% Sn--0.1% Fe--0.1% Cr--0.05% Ni alloys. Results are comparable with those obtained by methods requiring the separation of the B as methyl borate. (auth)« less

Direct intercalation of cisplatin into zirconium phosphate nanoplatelets for potential cancer nanotherapy

PubMed Central

Díaz, Agustín; González, Millie L.; Pérez, Riviam J.; David, Amanda; Mukherjee, Atashi; Báez, Adriana; Clearfield, Abraham

2014-01-01

We report the use of zirconium phosphate nanoplatelets (ZrP) for the encapsulation of the anticancer drug cisplatin and its delivery to tumor cells. Cisplatin was intercalated into ZrP by direct-ion exchange and was tested in-vitro for cytotoxicity in the human breast cancer (MCF-7) cell line. The structural characterization of the intercalated cisplatin in ZrP suggests that during the intercalation process, the chloride ligands of the cisplatin complex were substituted by phosphate groups within the layers. Consequently, a new phosphate phase with the platinum complex directly bound to ZrP (cisPt@ZrP) is produced with an interlayer distance of 9.3 Å. The in-vitro release profile of the intercalated drug by pH stimulus shows that at low pH under lysosomal conditions the platinum complex is released with simultaneous hydrolysis of the zirconium phosphate material, while at higher pH the complex is not released. Experiments with the MCF-7 cell line show that cisPt@ZrP reduced the cell viability up to 40%. The cisPt@ZrP intercalation product is envisioned as a future nanotherapy agent for cancer. Taking advantage of the shape and sizes of the ZrP particles and controlled release of the drug at low pH, it is intended to exploit the enhanced permeability and retention effect of tumors, as well as their intrinsic acidity, for the destruction of malignant cells. PMID:24072038

Physical characterization of a new composition of oxidized zirconium-2.5 wt% niobium produced using a two step process for biomedical applications

NASA Astrophysics Data System (ADS)

Pawar, V.; Weaver, C.; Jani, S.

2011-05-01

Zirconium and particularly Zr-2.5 wt%Nb (Zr2.5Nb) alloy are useful for engineering bearing applications because they can be oxidized in air to form a hard surface ceramic. Oxidized zirconium (OxZr) due to its abrasion resistant ceramic surface and biocompatible substrate alloy has been used as a bearing surface in total joint arthroplasty for several years. OxZr is characterized by hard zirconium oxide (oxide) formed on Zr2.5Nb using one step thermal oxidation carried out in air. Because the oxide is only at the surface, the bulk material behaves like a metal, with high toughness. The oxide, furthermore, exhibits high adhesion to the substrate because of an oxygen-rich diffusion hardened zone (DHZ) interposing between the oxide and the substrate. In this study, we demonstrate a two step process that forms a thicker DHZ and thus increased depth of hardening than that can be obtained using a one step oxidation process. The first step is thermal oxidation in air and the second step is a heat treatment in vacuum. The second step drives oxygen from the oxide formed in the first step deeper into the substrate to form a thicker DHZ. During the process only a portion of the oxide is dissolved. This new composition (DHOxZr) has approximately 4-6 μm oxide similar to that of OxZr. The nano-hardness of the oxide is similar but the DHZ is approximately 10 times thicker. The stoichiometry of the oxide is similar and a secondary phase rich in oxygen is present through the entire thickness. Due to the increased depth of hardening, the critical load required for the onset of oxide cracking is approximately 1.6 times more than that of the oxide of OxZr. This new composition has a potential to be used as a bearing surface in applications where greater depth of hardening is required.

Laser-induced breakdown spectroscopy of light water reactor simulated used nuclear fuel: Main oxide phase

DOE PAGES

Campbell, Keri R.; Judge, Elizabeth J.; Barefield, James E.; ...

2017-04-22

We show the analysis of light water reactor simulated used nuclear fuel using laser-induced breakdown spectroscopy (LIBS) is explored using a simplified version of the main oxide phase. The main oxide phase consists of the actinides, lanthanides, and zirconium. The purpose of this study is to develop a rapid, quantitative technique for measuring zirconium in a uranium dioxide matrix without the need to dissolve the material. A second set of materials including cerium oxide is also analyzed to determine precision and limit of detection (LOD) using LIBS in a complex matrix. Two types of samples are used in this study:more » binary and ternary oxide pellets. The ternary oxide, (U,Zr,Ce)O 2 pellets used in this study are a simplified version the main oxide phase of used nuclear fuel. The binary oxides, (U,Ce)O 2 and (U,Zr)O 2 are also examined to determine spectral emission lines for Ce and Zr, potential spectral interferences with uranium and baseline LOD values for Ce and Zr in a UO 2 matrix. In the spectral range of 200 to 800 nm, 33 cerium lines and 25 zirconium lines were identified and shown to have linear correlation values (R 2) > 0.97 for both the binary and ternary oxides. The cerium LOD in the (U,Ce)O 2 matrix ranged from 0.34 to 1.08 wt% and 0.94 to 1.22 wt% in (U,Ce,Zr)O 2 for 33 of Ce emission lines. The zirconium limit of detection in the (U,Zr)O 2 matrix ranged from 0.84 to 1.15 wt% and 0.99 to 1.10 wt% in (U,Ce,Zr)O 2 for 25 Zr lines. Finally, the effect of multiple elements in the plasma and the impact on the LOD is discussed.« less

Cyclic versus Noncyclic Chelating Scaffold for 89Zr-Labeled ZEGFR:2377 Affibody Bioconjugates Targeting Epidermal Growth Factor Receptor Overexpression

PubMed Central

2017-01-01

Zirconium-89 is an emerging radionuclide for positron emission tomography (PET) especially for biomolecules with slow pharmacokinetics as due to its longer half-life, in comparison to fluorine-18 and gallium-68, imaging at late time points is feasible. Desferrioxamine B (DFO), a linear bifunctional chelator (BFC) is mostly used for this radionuclide so far but shows limitations regarding stability. Our group recently reported on fusarinine C (FSC) with similar zirconium-89 complexing properties but potentially higher stability related to its cyclic structure. This study was designed to compare FSC and DFO head-to-head as bifunctional chelators for 89Zr-radiolabeled EGFR-targeting ZEGFR:2377 affibody bioconjugates. FSC-ZEGFR:2377 and DFO-ZEGFR:2377 were evaluated regarding radiolabeling, in vitro stability, specificity, cell uptake, receptor affinity, biodistribution, and microPET-CT imaging. Both conjugates were efficiently labeled with zirconium-89 at room temperature but radiochemical yields increased substantially at elevated temperature, 85 °C. Both 89Zr-FSC-ZEGFR:2377 and 89Zr-DFO-ZEGFR:2377 revealed remarkable specificity, affinity and slow cell-line dependent internalization. Radiolabeling at 85 °C showed comparable results in A431 tumor xenografted mice with minor differences regarding blood clearance, tumor and liver uptake. In comparison 89Zr-DFO-ZEGFR:2377, radiolabeled at room temperature, showed a significant difference regarding tumor-to-organ ratios. MicroPET-CT imaging studies of 89Zr-FSC-ZEGFR:2377 as well as 89Zr-DFO-ZEGFR:2377 confirmed these findings. In summary we were able to show that FSC is a suitable alternative to DFO for radiolabeling of biomolecules with zirconium-89. Furthermore, our findings indicate that 89Zr-radiolabeling of DFO conjugates at higher temperature reduces off-chelate binding leading to significantly improved tumor-to-organ ratios and therefore enhancing image contrast. PMID:29160082

Microstructure and mechanical properties of Zr-Si-N films prepared by rf-reactive sputtering

NASA Astrophysics Data System (ADS)

Nose, M.; Chiou, W. A.; Zhou, M.; Mae, T.; Meshii, M.

2002-05-01

ZrN and ZrSiN films were prepared in an rf sputtering apparatus that has a pair of targets facing each other (referred to as the facing target-type rf sputtering). Films were deposited on silicon wafers without bias application or substrate heating in order to examine only the effect of silicon addition to the transition metal nitride films. The contents of zirconium, nitrogen, and silicon of the films were determined with an electron probe microanalyzer. The transmission electron microscopy studies were carried out in addition to x-ray diffraction. For the high resolution transmission electron microscopy observation, the field emission type transmission electron microscope was used, which provides a point-to-point resolution of 0.1 nm. The samples were observed both parallel and perpendicular to the film surface, which were plane and cross sectional views, respectively. In order to investigate the relationship between the mechanical properties and microstructure of films, the hardness was measured by a nanoindentation system at room temperature. The load was selected to keep the impression depth below 60 nm (not more than 5% of film thickness) so that the influence from the substrate can be neglected. The hardness of the films increases with small Si additions reaching the maximum value of 35 GPa at around 3 at. % Si. The tendency to grow columnar grains was strongest around this composition, while grains became equiaxial above 5 at. % of Si. The films containing 12.8% Si, which showed the lowest hardness of 18 GPa, consist of nanocrystal grains. The presence of ZrN nanocrystals embedded in Si3N4 was not observed in the present study. The hardening mechanism due to the addition of small amounts of Si in ZrN can not be determined at this time. The grain size and residual stress can make minor contributions to the hardening. A possibility of solid solution hardening due to atomistic strain, such as nitrogen atoms at interstitial sites or other point defects is postulated and should be examined further.

Zirconium: biomedical and nephrological applications.

PubMed

Lee, David B N; Roberts, Martin; Bluchel, Christian G; Odell, Ross A

2010-01-01

Recent years have witnessed a rapid increase in the use of zirconium (Zr)-containing compounds in artificial internal organs. Examples include dental implants and other restorative practices, total knee and hip replacement, and middle-ear ossicular chain reconstruction. In nephrological practice, Zr-containing sorbents have been used in hemofiltration, hemodialysis, peritoneal dialysis, and in the design and construction of wearable artificial kidneys. Zr compounds continue to be widely and extensively used in deodorant and antiperspirant preparations. In the public health arena, Zr compounds have been studied or used in controlling phosphorus pollution and in the reclamation of poison and bacteria-contaminated water. Experimental and clinical studies support the general consensus that Zr compounds are biocompatible and exhibit low toxicity. Reports on possible Zr-associated adverse reactions are rare and, in general, have not rigorously established a cause-and-effect relationship. Although publications on the use of Zr compounds have continued to increase in recent years, reports on Zr toxicity have virtually disappeared from the medical literature. Nevertheless, familiarity with, and continued vigilant monitoring of, the use of these compounds are warranted. This article provides an updated review on the biomedical use of Zr compounds.

The temperature-dependent diffusion coefficient of helium in zirconium carbide studied with first-principles calculations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, Xiao-Yong; Lu, Yong; Zhang, Ping, E-mail: zhang-ping@iapcm.ac.cn

2015-04-28

The temperature-dependent diffusion coefficient of interstitial helium in zirconium carbide (ZrC) matrix is calculated based on the transition state theory. The microscopic parameters in the activation energy and prefactor are obtained from first-principles total energy and phonon frequency calculations including the all atoms. The obtained activation energy is 0.78 eV, consistent with experimental value. Besides, we evaluated the influence of C and Zr vacancies as the perturbation on helium diffusion, and found the C vacancy seems to confine the mobility of helium and the Zr vacancy promotes helium diffusion in some extent. These results provide a good reference to understand themore » behavior of helium in ZrC matrix.« less

Hip Dislocation Increases Roughness of Oxidized Zirconium Femoral Heads in Total Hip Arthroplasty: An Analysis of 59 Retrievals

PubMed Central

Moussa, Mohamed E.; Esposito, Christina I.; Elpers, Marcella E.; Wright, Timothy M.; Padgett, Douglas E.

2014-01-01

The aims of this study were to assess damage on the surface of retrieved oxidized zirconium metal (OxZr) femoral heads, to measure surface roughness of scratches, and to evaluate the extent of surface effacement using scanning electron microscopy (SEM). Ceramic zirconia-toughened alumina (ZTA) heads were analyzed for comparison. OxZr femoral heads explanted for recurrent dislocation had the most severe damage (p<0.001). The median surface roughness of damaged OxZr femoral heads was 1.49μm, compared to 0.084μm for damaged ZTA heads and 0.052μm for undamaged OxZr (p<0.001). This may be of clinical concern because increased surface roughness has the potential to increase the wear of polyethylene liners articulating against these OxZr heads in THA. PMID:25443362

ELECTROLYTIC CLADDING OF ZIRCONIUM ON URANIUM

DOEpatents

Wick, J.J.

1959-09-22

A method is presented for coating uranium with zircoalum by rendering the uranium surface smooth and oxidefree, immersing it in a molten electrolytic bath in NaCI, K/sub 2/ZrF/sub 6/, KF, and ZrO/sub 2/, and before the article reaches temperature equilibrium with the bath, applying an electrolyzing current of 60 amperes per square dectmeter at approximately 3 volts to form a layer of zirconium metal on the uranium.

Effect of anodization on the surface characteristics and electrochemical behaviour of zirconium in artificial saliva.

PubMed

Romonti, Daniela E; Gomez Sanchez, Andrea V; Milošev, Ingrid; Demetrescu, Ioana; Ceré, Silvia

2016-05-01

The paper is focused on elaboration of ZrO2 films on pure zirconium via anodizing in phosphoric acid with and without fluoride at constant potentials of 30 V and 60 V. The structure and composition of the films were investigated using scanning electronic microscopy, Raman spectroscopy and X-ray photoelectron spectroscopy. The composition of the oxides formed at both potentials can be identified as monoclinic ZrO2. In addition to Zr and O, the layers formed in phosphoric acid contain phosphorus originating from the phosphoric acid. When the phosphoric acid solution contains NaF, fluorine is also incorporated into the oxide layer. The oxides formed at a higher voltage have greater roughness than those formed at 30 V. Anodized samples exhibit smaller current densities during anodic polarization compared to the as-received zirconium covered with native oxide. Copyright © 2016 Elsevier B.V. All rights reserved.

Zirconium Phosphate Supported MOF Nanoplatelets.

PubMed

Kan, Yuwei; Clearfield, Abraham

2016-06-06

We report a rare example of the preparation of HKUST-1 metal-organic framework nanoplatelets through a step-by-step seeding procedure. Sodium ion exchanged zirconium phosphate, NaZrP, nanoplatelets were judiciously selected as support for layer-by-layer (LBL) assembly of Cu(II) and benzene-1,3,5-tricarboxylic acid (H3BTC) linkers. The first layer of Cu(II) is attached to the surface of zirconium phosphate through covalent interaction. The successive LBL growth of HKUST-1 film is then realized by soaking the NaZrP nanoplatelets in ethanolic solutions of cupric acetate and H3BTC, respectively. The amount of assembled HKUST-1 can be readily controlled by varying the number of growth cycles, which was characterized by powder X-ray diffraction and gas adsorption analyses. The successful construction of HKUST-1 on NaZrP was also supported by its catalytic performance for the oxidation of cyclohexene.

The Chemical Composition and Structure of Supported Sulfated Zirconia with Regulated Size Nanoparticles

NASA Astrophysics Data System (ADS)

Kanazhevskiy, V. V.; Shmachkova, V. P.; Kotsarenko, N. S.; Kochubey, D. I.; Vedrine, J. C.

2007-02-01

A set of model skeletal isomerization catalysts — sulfated zirconia nanoparticles of controlled thickness anchored on different supports — was prepared using colloidal solutions of Zr salt on titania as support. The nanoparticles of zirconia (1-5 nm) are epitaxially connected to the support surface, with S/Zr ratio equals to 1.3-1.5. It was shown by EXAFS that nanoparticles of non-stoichiometric zirconium sulfate Zr(SO4)1+x, where x<0.5, are formed on the support surface. Its structure looks like half-period shifted counterdirected chains built-up by zirconium atoms linked by triangle pyramids of sulfate groups. Considering catalytic data of skeletal n-butane isomerisation at 150°C, one can suggest that these species behave as the active component of sulfated zirconia. They are formed in subsurface layers as zirconium hydroxide undergoes sulfation followed by thermal treatment.

Ternary cobalt-molybdenum-zirconium coatings for alternative energies

NASA Astrophysics Data System (ADS)

Yar-Mukhamedova, Gulmira; Ved', Maryna; Sakhnenko, Nikolay; Koziar, Maryna

2017-11-01

Consistent patterns for electrodeposition of Co-Mo-Zr coatings from polyligand citrate-pyrophosphate bath were investigated. The effect of both current density amplitude and pulse on/off time on the quality, composition and surface morphology of the galvanic alloys were determined. It was established the coating Co-Mo-Zr enrichment by molybdenum with current density increasing up to 8 A dm-2 as well as the rising of pulse time and pause duration promotes the content of molybdenum because of subsequent chemical reduction of its intermediate oxides by hydrogen ad-atoms. It was found that the content of the alloying metals in the coating Co-Mo-Zr depends on the current density and on/off times extremely and maximum Mo and Zr content corresponds to the current density interval 4-6 A dm-2, on-/off-time 2-10 ms. Chemical resistance of binary and ternary coatings based on cobalt is caused by the increased tendency to passivity and high resistance to pitting corrosion in the presence of molybdenum and zirconium, as well as the acid nature of their oxides. Binary coating with molybdenum content not less than 20 at.% and ternary ones with zirconium content in terms of corrosion deep index are in a group ;very proof;. It was shown that Co-Mo-Zr alloys exhibits the greatest level of catalytic properties as cathode material for hydrogen electrolytic production from acidic media which is not inferior a platinum electrode. The deposits Co-Mo-Zr with zirconium content 2-4 at.% demonstrate high catalytic properties in the carbon(II) oxide conversion. This confirms the efficiency of materials as catalysts for the gaseous wastes purification and gives the reason to recommend them as catalysts for red-ox processes activating by oxygen as well as electrode materials for red-ox batteries.

Effects of temperature, concentration, and uranium chloride mixture on zirconium electrochemical studies in LiClsbnd KCl eutectic salt

NASA Astrophysics Data System (ADS)

Hoover, Robert O.; Yoon, Dalsung; Phongikaroon, Supathorn

2016-08-01

Experimental studies were performed to provide measurement and analysis of zirconium (Zr) electrochemistry in LiClsbnd KCl eutectic salt at different temperatures and concentrations using cyclic voltammetry (CV). An additional experimental set with uranium chloride added into the system forming UCl3sbnd ZrCl4sbnd LiClsbnd KCl was performed to explore the general behavior of these two species together. Results of CV experiments with ZrCl4 show complicated cathodic and anodic peaks, which were identified along with the Zr reactions. The CV results reveal that diffusion coefficients (D) of ZrCl4 and ZrCl2 as the function of temperature can be expressed as DZr(IV) = 0.00046exp(-3716/T) and DZr(II) = 0.027exp(-5617/T), respectively. The standard rate constants and apparent standard potentials of ZrCl4 at different temperatures were calculated. Furthermore, the results from the mixture of UCl3 and ZrCl4 indicate that high concentrations of UCl3 hide the features of the smaller concentration of ZrCl4 while Zr peaks become prominent as the concentration of ZrCl4 increases.

Ca2+-exchange in layered zirconium orthophosphate, α-ZrP: Chemical study and potential application for zinc corrosion inhibition

NASA Astrophysics Data System (ADS)

Bouali, Imane; Rocca, Emmanuel; Veys-Renaux, Delphine; Rhouta, Benaissa; Khalil, Aziza; Aït Aghzzaf, Ahmed

2017-11-01

The control of the corrosion phenomenon occurring at the metal interface requires the development of new non-toxic anticorrosion additives. For this purpose, zirconium orthophosphate compounds (Zr(HPO4)2,H2O noted α-ZrP) were synthesized by both hydrothermal and refluxing methods The Ca2+-cationic exchange in the layered structure is kinetically favoured by low crystallinity of α-ZrP synthesized by refluxing process, and leads to the formation of CaZr(PO4)2,4H2O, noted Ca2+-ZrP. The H+/Ca2+ exchange mechanism is mainly triggered by acid-base considerations, and especially the pKa of α-ZrP/Ca2+-ZrP acid-base couple (evaluated to 2.5). Both compounds are acidic compounds by internal exchangeable H+ for α-ZrP and surface protons for Ca2+-ZrP, and can be used as potential inhibitors of zinc corrosion. Electrochemical measurements show that Ca2+-ZrP compounds dispersed in the NaCl electrolyte buffer the pH value over a long time and therefore allow controlling the corrosion rate of zinc.

Novel Routes for Sintering of Ultra-high Temperature Ceramics and their Properties

DTIC Science & Technology

2014-10-31

UHTCs charge (zirconium and hafnium borides , SiC) with additives (chromium carbide, nickel, chromium, etc.), which activate sintering process, is...temperature phases in a form of carboborides of zirconium and bi borides of zirconium or chromium. Elevation of densification rate of sintered borides is...superplasticity under the slip mechanism of zirconium boride and silica carbide grains on grain boundary interlayers with nanocrystalline grains of carbon

Reactions and products in the Cs-Zr-I-O system relevant to fission product chemistry — a review

NASA Astrophysics Data System (ADS)

Chen, T.-M.; Kauzlarich, S. M.; Corbett, J. D.

1988-02-01

Some results and problems associated with the known chemistry of cesium and iodine in the presence of Zr/ZrO 2 at 400-600°C and under anaerobic conditions are described and discussed. These aspects include (1) the recently synthesized cesium zirconates Cs 2ZrO 3 and Cs 4ZrO 4 and some of their thermal and hydrolytic properties (2) the demonstration that the supposedly stable CsI reacts with ZrO 2 at 400-700°C to form Cs 2ZrO 3 and ZrI 4 (as Cs 2ZrI 6) and its implications regarding cesium and iodine distributions (3) present knowledge of binary zirconium iodides, their contamination reactions, and the limited inhibition of the reduction of ZrI 4 by metal provided by static ZrO 2 films (4) newly discovered ternary and quaternary zirconium iodides that are obtained in the presence of many common impurity atoms and, when prsesent, CsI (e.g., Zr 6I 12C, CsZr 6I 14C, Zr 6I 14Fe), the ease with which some of those form at least as low as 450°C, and the complications these and related new phases provide.

Histomorphometric and histologic evaluation of titanium-zirconium (aTiZr) implants with anodized surfaces.

PubMed

Sharma, Ajay; McQuillan, A James; Shibata, Yo; Sharma, Lavanya A; Waddell, John Neil; Duncan, Warwick John

2016-05-01

The choice of implant surface has a significant influence on osseointegration. Modification of TiZr surface by anodization is reported to have the potential to modulate the osteoblast cell behaviour favouring more rapid bone formation. The aim of this study is to investigate the effect of anodizing the surface of TiZr discs with respect to osseointegration after four weeks implantation in sheep femurs. Titanium (Ti) and TiZr discs were anodized in an electrolyte containing DL-α-glycerophosphate and calcium acetate at 300 V. The surface characteristics were analyzed by scanning electron microscopy, electron dispersive spectroscopy, atomic force microscopy and goniometry. Forty implant discs with thickness of 1.5 and 10 mm diameter (10 of each-titanium, titanium-zirconium, anodized titanium and anodized titanium-zirconium) were placed in the femoral condyles of 10 sheep. Histomorphometric and histologic analysis were performed 4 weeks after implantation. The anodized implants displayed hydrophilic, porous, nano-to-micrometer scale roughened surfaces. Energy dispersive spectroscopy analysis revealed calcium and phosphorous incorporation into the surface of both titanium and titanium-zirconium after anodization. Histologically there was new bone apposition on all implanted discs, slightly more pronounced on anodised discs. The percentage bone-to-implant contact measurements of anodized implants were higher than machined/unmodified implants but there was no significant difference between the two groups with anodized surfaces (P > 0.05, n = 10). The present histomorphometric and histological findings confirm that surface modification of titanium-zirconium by anodization is similar to anodised titanium enhances early osseointegration compared to machined implant surfaces.

Plasma-Sprayed Fine-grained Zirconium Silicate and Its Dielectric Properties

NASA Astrophysics Data System (ADS)

Ctibor, P.; Pala, Z.; Nevrlá, B.; Neufuss, K.

2017-05-01

The article is focused on selected dielectric and electrical properties of ZrSiO4, which was plasma sprayed by a water-stabilized plasma system. A combination of two feeding distances and three spray distances was utilized for spraying and the structure and properties of samples evaluated. The coatings were tested in alternating electric field to determine capacity and loss factor with the frequency from 100 Hz to 100 kHz. Relative permittivity was calculated from the capacity. Volume resistivity and dielectric strength of ZrSiO4 were measured in a direct current regime. The aim was to test electrically this natural silicate material in the form of plasma-sprayed deposits. Microstructure was characterized by relatively large and non-globular pores. Crystallites were very small, about 10-20 nm. Dielectric losses were small, resistivity as well as strength relatively high. This silicate ceramic was recognized to be prospective for electrical engineering.

Fine-grained zirconium-base material

DOEpatents

Van Houten, G.R.

1974-01-01

A method is described for making zirconium with inhibited grain growth characteristics, by the process of vacuum melting the zirconium, adding 0.3 to 0.5% carbon, stirring, homogenizing, and cooling. (Official Gazette)

Reprint of: Effects of cold deformation, electron irradiation and extrusion on deuterium desorption behavior in Zr-1%Nb alloy

NASA Astrophysics Data System (ADS)

Morozov, O.; Mats, O.; Mats, V.; Zhurba, V.; Khaimovich, P.

2018-01-01

The present article introduces the data of analysis of ranges of ion-implanted deuterium desorption from Zr-1% Nb alloy. The samples studied underwent plastic deformation, low temperature extrusion and electron irradiation. Plastic rolling of the samples at temperature ∼300 K resulted in plastic deformation with the degree of ε = 3.9 and the formation of nanostructural state with the average grain size of d = 61 nm. The high degree of defectiveness is shown in thermodesorption spectrum as an additional area of the deuterium desorption in the temperature ranges 650-850 K. The further processing of the sample (that had undergone plastic deformation by plastic rolling) with electron irradiation resulted in the reduction of the average grain size (58 nm) and an increase in borders concentration. As a result the amount of deuterium desorpted increased in the temperature ranges 650-900 K. In case of Zr-1% Nb samples deformed by extrusion the extension of desorption area is observed towards the temperature reduction down to 420 K. The formation of the phase state of deuterium solid solution in zirconium was not observed. The structural state behavior is a control factor in the process of deuterium thermodesorption spectrum structure formation with a fixed implanted deuterium dose (hydrogen diagnostics). It appears as additional temperature ranges of deuterium desorption depending on the type, character and defect content.

Obtaining composite Zr-Al-O coating on the surface of zirconium by microplasma oxidation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gubaidulina, Tatiana A., E-mail: goub2002@mail.ru, E-mail: ostk@mail2000ru; Kuzmin, Oleg S., E-mail: goub2002@mail.ru, E-mail: ostk@mail2000ru; Fedorischva, Marina V., E-mail: fmw@ispms.tsc.ru, E-mail: kmp1980@mail.ru

2014-11-14

The paper describes the application of the microplasma oxidation for production of Zr-Al-O composition on the surface of zirconium. Certification of a new-type power supply for depositing oxide ceramic coatings by microplasma oxidation was also carried out. The growth rate of Zr-Al-O coating amounted around 0.2 nm/s, which around 10 times exceeds that for depositing similar coatings using the similar equipment. We have studied the change of surface morphology and the chemical composition of the formed ceramic coating by means of EVO 50 scanning electron microscope and X-ray spectral analysis.

pH-responsive drug delivery system based on AIE luminogen functionalized layered zirconium phosphate nano-platelets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Dongdong, E-mail: lidongdong@jlu.edu.cn; Zhang, Yuping; Zhou, Bingbing

2015-05-15

Aggregation-induced emission (AIE) luminogen, quaternary tetraphenylethene cation (TPEN), was successfully incorporated into layered α-zirconium phosphate (α-ZrP) by using co-precipitation method to form inorganic–organic hybrid materials. The obtained materials show the characteristic hexagonal platelet shape with the interlayer distance did not reveal significant difference compared with pure α-ZrP. In addition, the obtained hybrid materials emit strong blue emission centered at 476 nm in aqueous media due to the electrostatic interactions of TPEN with the anionic framework of α-ZrP, which largely restrict their intramolecular rotation. More importantly, the materials provide a pH dependent release of doxorubicin (DOX), suggesting that AIE luminogen functionalizedmore » α-ZrP may be used as an imaging guided and pH-responsive delivery system for targeting therapy. - Graphical abstract: AIE luminogen was successfully incorporated into layered α-zirconium phosphate by a co-precipitation method to form inorganic–organic hybrid materials, showing a pH dependent release of DOX. - Highlights: • AIE luminogen cation was incorporated into layered α-ZrP by co-precipitation method. • The obtained material emits strong blue emission upon UV irradiation. • The material exhibits pH dependent release of DOX. • The AIE functionalized α-ZrP has potential applications in imaging guided therapy.« less

Development of a Database of Thermochemical Parameters for Use with the SOLGASMIX Computer Program

DTIC Science & Technology

1988-07-01

TITANIUM CHLORIDE (TICL4) CL4Wl(CR) TUNGSTEN CHLORIDE (WCL4) CL4Wl(G) TUNGSTEN CHLORIDE (WCL4) CL4ZR1(CR) ZIRCONIUM CHLORIDE ( ZRCL4 ) CL4ZR1(G) ZIRCONIUM...CHLORIDE ( ZRCL4 ) % % % CL5MO1(CR) MOLYBDENUM CHLORIDE (MOCL5) CL5MO1(CR,L) MOLYBDENUM CHLORIDE (MOCL5) CL5MO1(G) MOLYBDENUM CHLORIDE (MOCL5) CL5MOI(L

Water/ice phase transition: The role of zirconium acetate, a compound with ice-shaping properties

NASA Astrophysics Data System (ADS)

Marcellini, Moreno; Fernandes, Francisco M.; Dedovets, Dmytro; Deville, Sylvain

2017-04-01

Few compounds feature ice-shaping properties. Zirconium acetate is one of the very few inorganic compounds reported so far to have ice-shaping properties similar to that of ice-shaping proteins, encountered in many organisms living at low temperature. When a zirconium acetate solution is frozen, oriented and perfectly hexagonal ice crystals can be formed and their growth follows the temperature gradient. To shed light on the water/ice phase transition while freezing zirconium acetate solution, we carried out differential scanning calorimetry measurements. From our results, we estimate how many water molecules do not freeze because of their interaction with Zr cations. We estimate the colligative properties of the Zr acetate on the apparent critical temperature. We further show that the phase transition is unaffected by the nature of the base which is used to adjust the pH. Our results provide thus new hints on the ice-shaping mechanism of zirconium acetate.

Water/ice phase transition: The role of zirconium acetate, a compound with ice-shaping properties.

PubMed

Marcellini, Moreno; Fernandes, Francisco M; Dedovets, Dmytro; Deville, Sylvain

2017-04-14

Few compounds feature ice-shaping properties. Zirconium acetate is one of the very few inorganic compounds reported so far to have ice-shaping properties similar to that of ice-shaping proteins, encountered in many organisms living at low temperature. When a zirconium acetate solution is frozen, oriented and perfectly hexagonal ice crystals can be formed and their growth follows the temperature gradient. To shed light on the water/ice phase transition while freezing zirconium acetate solution, we carried out differential scanning calorimetry measurements. From our results, we estimate how many water molecules do not freeze because of their interaction with Zr cations. We estimate the colligative properties of the Zr acetate on the apparent critical temperature. We further show that the phase transition is unaffected by the nature of the base which is used to adjust the pH. Our results provide thus new hints on the ice-shaping mechanism of zirconium acetate.

Enhancement of yield strength in zirconium metal through high-pressure induced structural phase transition

NASA Astrophysics Data System (ADS)

Zhao, Yusheng; Zhang, Jianzhong

2007-11-01

We report here a high-pressure phase-transition induced strengthening in ultrapure zirconium metal. The determined yield strength shows more than sixfold abrupt increase at the transition pressure of Pc=6GPa, from σyα≈180MPa in the low-pressure phase of α-Zr to σyω≈1180MPa in the high-pressure phase of ω-Zr. The observed enhancement provides an alternate route for material strengthening and is the most significant among the known strengthening techniques for metals. Our findings support the theoretical simulations of the substantial covalent bonding and "rougher" corrugation of slip planes for dislocations in the ω-phase of zirconium.

Zirconium and hafnium fractionation in differentiation of alkali carbonatite magmatic systems

NASA Astrophysics Data System (ADS)

Kogarko, L. N.

2016-05-01

Zirconium and hafnium are valuable strategic metals which are in high demand in industry. The Zr and Hf contents are elevated in the final products of magmatic differentiation of alkali carbonatite rocks in the Polar Siberia region (Guli Complex) and Ukraine (Chernigov Massif). Early pyroxene fractionation led to an increase in the Zr/Hf ratio in the evolution of the ultramafic-alkali magmatic system due to a higher distribution coefficient of Hf in pyroxene with respect to Zr. The Rayleigh equation was used to calculate a quantitative model of variation in the Zr/Hf ratio in the development of the Guli magmatic system. Alkali carbonatite rocks originated from rare element-rich mantle reservoirs, in particular, the metasomatized mantle. Carbonated mantle xenoliths are characterized by a high Zr/Hf ratio due to clinopyroxene development during metasomatic replacement of orthopyroxene by carbonate fluid melt.

Defect kinetics and resistance to amorphization in zirconium carbide

NASA Astrophysics Data System (ADS)

Zheng, Ming-Jie; Szlufarska, Izabela; Morgan, Dane

2015-02-01

To better understand the radiation response of zirconium carbide (ZrC), and in particular its excellent resistance to amorphization, we have used density functional theory methods to study the kinetics of point defects in ZrC. The migration barriers and recombination barriers of the simple point defects are calculated using the ab initio molecular dynamics simulation and the nudged elastic band method. These barriers are used to estimate C and Zr interstitial and vacancy diffusion and Frenkel pair recombination rates. A significant barrier for C Frenkel pair recombination is found but it is shown that a large concentration of C vacancies reduces this barrier dramatically, allowing facile healing of radiation damage. The mechanisms underlying high resistance to amorphization of ZrC were analyzed from the perspectives of structural, thermodynamic, chemical and kinetic properties. This study provides insights into the amorphization resistance of ZrC as well as a foundation for understanding general radiation damage in this material.

Tungsten carbide nanorods with zirconium dioxide composite for low cost with high efficiency Pt-free counter electrode in dye sensitized solar cell

NASA Astrophysics Data System (ADS)

Vijayakumar, P.; Senthil Pandian, M.; Ramasamy, P.

2018-04-01

Tungsten carbide nanorods/Zirconium dioxide (WC-NRs/ZrO2) composite material was used as a counter electrode (CE) for efficient dye-sensitized solar cell (DSSC) fabrication. The prepared WC-NRs/ZrO2 (N-Methyl-2-pyrrolidone (NMP)/2-Propanol) gel is drop casted on the FTO substrate for CE. The morphological analysis was confirmed by FESEM and TEM. Nyquist plot clearly indicates that the NMP based WC-NRs/ZrO2 CE possesses high electrocatalytic activity and faster charge-transfer ability for the reduction of I3- due to the lower charge transfer resistance. The fabricated WC-NRs/ZrO2 (NMP) composite CE is demonstrated with high power conversion efficiency (PCE) of 6.63% in comparison to the WC-NRs/ZrO2 (2-propanol) CE of 2.29% under same conditions.

Fabrication and characterization of polyvinyl alcohol/metal (Ca, Mg, Ti) doped zirconium phosphate nanocomposite films for scaffold-guided tissue engineering application.

PubMed

Kalita, Himani; Pal, Pallabi; Dhara, Santanu; Pathak, Amita

2017-02-01

Nanocomposite films of polyvinyl alcohol (PVA) and zirconium phosphate (ZrP)/doped ZrP (doped with Ca, Mg, Ti) nanoparticles have been developed by solvent casting method to assess their potential as matrix material in scaffold-guided tissue engineering application. The prepared ZrP and doped ZrP nanoparticles as well as the nanocomposite films were characterized by various spectroscopic and microscopic techniques. Nanoindentation studies revealed improved nanomechanical properties in the PVA/doped ZrP nanocomposite films (highest for PVA/Ti doped ZrP: hardness=262.4MPa; elastic modulus=5800MPa) as compared to the PVA/ZrP and neat PVA films. In-vitro cell culture experiments carried out to access the cellular viability, attachment, proliferation, and migration on the substrates, using mouse fibroblast (3T3) cell lines, inferred enhanced bioactivity in the PVA/doped ZrP nanocomposite films (highest for PVA/Ca doped ZrP) in contrast to PVA/ZrP and neat PVA films. Controlled biodegradability as well as swelling behavior, superior bioactivity and improved mechanical properties of the PVA/doped ZrP nanocomposite films make them promising matrix materials for scaffold-guided tissue engineering application. Copyright © 2016 Elsevier B.V. All rights reserved.

Selective separation of zirconium from uranium in carbonate solutions by ion flotation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jdid, E.A.; Blazy, P.; Mahamadou, A.

1990-05-01

Separation of zirconium from uranium in carbonate media was undertaken by ion flotation. The collector chosen was octylhydroxamic acid (HOHX). It gave a well-flocculated precipitate with zirconium which floated in less than 5 min. The stoichiometry of the reaction is HOHX/Zr = 3.9/1, and the selectivity in the presence of uranium is very high. In fact, for a ratio {Phi} = (HOHX),M/(Zr),M, which is just stoichiometric and is close to 4, the zirconium removal rate reaches 99%, even in industrial media. The loss of uranium is only 0.5% although its concentration is 37.4 g/L. Mechanisms of separation are not affectedmore » by a variation of pH between 6.7 and 9.8, of temperature up to 60{degree}C, and of carbonate concentration within the 15 to 60 g/L Na{sub 2}CO{sub 3} range.« less

The effects of pulsed electromagnetic field (PEMF) on osteoblast-like cells cultured on titanium and titanium-zirconium surfaces.

PubMed

Atalay, Belir; Aybar, Buket; Ergüven, Mine; Emes, Yusuf; Bultan, Özgür; Akça, Kivanç; Yalçin, Serhat; Baysal, Uğur; Işsever, Halim; Çehreli, Murat Cavit; Bilir, Ayhan

2013-11-01

Commercially pure Ti, together with Ti Ni, Ti-6Al-4V, and Ti-6Al-7Nb alloys, are among the materials currently being used for this purpose. Titanium-zirconium (TiZr) has been developed that allows SLActive surface modification and that has comparable or better mechanical strength and improved biocompatibility compared with existing Ti alloys. Furthermore, approaches have targeted making the implant surface more hydrophilic, as with the Straumann SLActive surface, a modification of the SLA surface. The aim of this study is to evaluate the effects of pulsed electromagnetic field (PEMF) to the behavior of neonatal rat calvarial osteoblast-like cells cultured on commercially pure titanium (cpTi) and titanium-zirconium alloy (TiZr) discs with hydrophilic surface properties. Osteoblast cells were cultured on titanium and TiZr discs, and PEMF was applied. Cell proliferation rates, cell numbers, cell viability rates, alkaline phosphatase, and midkine (MK) levels were measured at 24 and 72 hours. At 24 hours, the number of cells was significantly higher in the TiZr group. At 72 hours, TiZr had a significantly higher number of cells when compared to SLActive, SLActive + PEMF, and machine surface + PEMF groups. At 24 hours, cell proliferation was significantly higher in the TiZr group than SLActive and TiZr + PEMF group. At 72 hours, TiZr group had higher proliferation rate than machine surface and TiZr + PEMF. Cell proliferation in the machine surface group was lower than both SLActive + PEMF and machine surface + PEMF. MK levels of PEMF-treated groups were lower than untreated groups for 72 hours. Our findings conclude that TiZr surfaces are similar to cpTi surfaces in terms of biocompatibility. However, PEMF application has a higher stimulative effect on cells cultured on cpTi surfaces when compared to TiZr.

Facile Synthesis and Characterization of ZrO₂ Nanoparticles via Modified Co-Precipitation Method.

PubMed

Ramachandran, M; Subadevi, R; Liu, Wei-Ren; Sivakumar, M

2018-01-01

The crystalline Zirconium oxide (ZrO2) nano particles were synthesized using optimized content of Zirconium nitrate (Zr(NO3)2·3H2O) with varying KOH concentration (0.5, 1 and 1.5 M) by co-precipitation method. The thermal history of the precursor was carefully analyzed through Thermogravimetric (TG/DTA) measurement. The as prepared samples were characterized to ensure structural, functional, morphological, compositional, chemical composition and band gap by X-ray diffractometer (XRD), Fourier transform infrared spectroscopy (FTIR), Laser Raman, scanning electron microscopy (SEM), High resolution Transverse Electron Microscopy (HR-TEM), X-ray photo electron spectroscopy (XPS), EDX, Photo luminescence spectroscopy (PL). The monoclinic structure with space group P21/c has been confirmed from XRD (JCPDS 89-9066). The Zr-O stretching vibration and Zr-O2-Zr bending vibrations were confirmed through FTIR analysis. The well dispersed particles with spherical morphology were confirmed through SEM and TEM analysis. The oxidation states of Zr, O and C were confirmed through XPS analysis. The oxygen vacancies and band gap of the particles were investigated through PL analysis.

Effect of humic acid preloading on phosphate adsorption onto zirconium-modified zeolite.

PubMed

Lin, Jianwei; Zhang, Zhe; Zhan, Yanhui

2017-05-01

A zirconium-modified zeolite (ZrMZ) was prepared, and then, humic acid (HA) was immobilized on the ZrMZ surface to prepare HA-loaded ZrMZ (HA-ZrMZ). The obtained ZrMZ and HA-ZrMZ were characterized by energy dispersive X-ray spectroscopy, elemental analyzer, N 2 adsorption/desorption isotherms, pH at the point of zero charge, and X-ray photoelectron spectroscopy. The adsorption characteristics of phosphate on ZrMZ and HA-ZrMZ were comparatively investigated in batch mode. The adsorption mechanism of phosphate on ZrMZ and HA-ZrMZ was investigated by ionic strength effect and 31 P nuclear magnetic resonance. The mechanism for phosphate adsorption onto ZrMZ was the formation of inner-sphere phosphate complexes at the solid/solution interface. The preloading of HA on ZrMZ reduced the phosphate adsorption capacity, and the more the HA loading amount, the lower the phosphate adsorption capacity. However, the preloading of HA on ZrMZ did not change the phosphate adsorption mechanism; i.e., the formation of inner-sphere phosphate surface complexes was still responsible for the adsorption of phosphate on HA-ZrMZ. The decreased phosphate adsorption capacity for ZrMZ after HA coating could be attributed to the fact that the coating of HA on ZrMZ reduced the amount of binding active sites available for phosphate adsorption, changed the adsorbent surface charges, and reduced the specific surface areas and pore volumes of ZrMZ.

Effect of zirconium oxide nanofiller and dibutyl phthalate plasticizer on ionic conductivity and optical properties of solid polymer electrolyte.

PubMed

Yasin, Siti Mariah Mohd; Ibrahim, Suriani; Johan, Mohd Rafie

2014-01-01

New solid polymer electrolytes (SPE) based on poly(ethylene oxide) (PEO) doped with lithium trifluoromethanesulfonate (LiCF3SO3), dibutyl phthalate (DBP) plasticizer, and zirconium oxide (ZrO2) nanoparticles were prepared by solution-casting technique. The conductivity was enhanced by addition of dibutyl phthalate (DBP) plasticizer and ZrO2 nanofiller with maximum conductivity (1.38 × 10(-4) Scm(-1)). The absorption edge and band gap values showed decreases upon addition of LiSO3CF3, DBP, and ZrO2 due to the formation of localized states in the SPE and the degree of disorder in the films increased.

Effect of Zirconium Oxide Nanofiller and Dibutyl Phthalate Plasticizer on Ionic Conductivity and Optical Properties of Solid Polymer Electrolyte

PubMed Central

Yasin, Siti Mariah Mohd; Ibrahim, Suriani

2014-01-01

New solid polymer electrolytes (SPE) based on poly(ethylene oxide) (PEO) doped with lithium trifluoromethanesulfonate (LiCF3SO3), dibutyl phthalate (DBP) plasticizer, and zirconium oxide (ZrO2) nanoparticles were prepared by solution-casting technique. The conductivity was enhanced by addition of dibutyl phthalate (DBP) plasticizer and ZrO2 nanofiller with maximum conductivity (1.38 × 10−4 Scm−1). The absorption edge and band gap values showed decreases upon addition of LiSO3CF3, DBP, and ZrO2 due to the formation of localized states in the SPE and the degree of disorder in the films increased. PMID:25133244

Zirconium Phosphate Nanoplatelet Potential for Anticancer Drug Delivery Applications.

PubMed

González, Millie L; Ortiz, Mayra; Hernández, Carmen; Cabán, Jennifer; Rodríguez, Axel; Colón, Jorge L; Báez, Adriana

2016-01-01

Zirconium phosphate (ZrP) nanoplatelets can intercalate anticancer agents via an ion exchange reaction creating an inorganic delivery system with potential for cancer treatment. ZrP delivery of anticancer agents inside tumor cells was explored in vitro. Internalization and cytotoxicity of ZrP nanoplatelets were studied in MCF-7 and MCF-10A cells. DOX-loaded ZrP nanoplatelets (DOX@ZrP) uptake was assessed by confocal (CLSM) and transmission electron microscopy (TEM). Cytotoxicity to MCF-7 and MCF-10A cells was determined by the MTT assay. Reactive Oxy- gen Species (ROS) production was analyzed by fluorometric assay, and cell cycle alterations and induction of apoptosis were analyzed by flow cytometry. ZrP nanoplatelets were localized in the endosomes of MCF-7 cells. DOX and ZrP nanoplatelets were co-internalized into MCF-7 cells as detected by CLSM. While ZrP showed limited toxicity to MCF-7 cells, DOX@ZrP was cytotoxic at an IC₅₀ similar to that of free DOX. Meanwhile, DOX lC₅₀ was significantly lower than the equivalent concentration of DOX@ZrP in MCF-10A cells. ZrP did not induce apoptosis in both cell lines. DOX and DOX@ZrP induced significant oxidative stress in both cell models. Results suggest that ZrP nanoplatelets are promising as carriers of anticancer agents into cancer cells.

6-Peroxo-6-zirconium crown and its hafnium analogue embedded in a triangular polyanion: [M6(O2)6(OH)6(gamma-SiW10O36)3]18- (M = Zr, Hf).

PubMed

Bassil, Bassem S; Mal, Sib Sankar; Dickman, Michael H; Kortz, Ulrich; Oelrich, Holger; Walder, Lorenz

2008-05-28

We have synthesized and structurally characterized the unprecedented peroxo-zirconium(IV) containing [Zr6(O2)6(OH)6(gamma-SiW10O36)3]18- (1). Polyanion 1 comprises a cyclic 6-peroxo-6-zirconium core stabilized by three decatungstosilicate units. We have also prepared the isostructural hafnium(IV) analogue [Hf6(O2)6(OH)6(gamma-SiW10O36)3]18- (2). We investigated the acid/base and redox properties of 1 by UV-vis spectroscopy and electrochemistry studies. Polyanion 1 represents the first structurally characterized Zr-peroxo POM with side-on, bridging peroxo units. The simple, one-pot synthesis of 1 and 2 involving dropwise addition of aqueous hydrogen peroxide could represent a general procedure for incorporating peroxo groups into a large variety of transition metal and lanthanide containing POMs.

Mesoporous zirconium titanium oxides. Part 2: Synthesis, porosity, and adsorption properties of beads.

PubMed

Sizgek, G Devlet; Sizgek, Erden; Griffith, Christopher S; Luca, Vittorio

2008-11-04

Mesoporous zirconium titanium mixed-oxide beads having disordered wormhole textures and mole fractions of Zr (x) ranging from x=0.25 to 0.67 have been prepared. The bead preparation method combined the forced hydrolysis of mixtures of zirconium-titanium alkoxides in the presence of long-chain carboxylates with external gelation. Uniformly sized beads could be produced in the size range 0.5-1.1 mm by varying the droplet size and viscosity of the mixed-oxide sol, thus making them suitable for large-scale column chromatographic applications. The beads exhibited narrow pore size distributions with similar mean pore diameters of around 3.7 nm. The specific surface areas of the beads were linked to the Zr mole fraction in the precursor solution and were generally greater than 350 m2/g for x=0.5. A combination of scanning transmission electron microscopy and X-ray absorption fine structure analysis indicated that the pore walls of the beads were composed of atomically dispersed Zr and Ti to form a continuous network of Zr-O-Ti bonds. Mass transport in the beads was evaluated by monitoring the kinetics of vanadate and vanadyl adsorption at pH 10.5 and 0.87, respectively.

Experimental study of high-temperature properties of zirconium carbide as a protective material for nuclear power and aerospace technologies (from 2000 to 5000 K)

NASA Astrophysics Data System (ADS)

Savvatimskiy, A. I.; Onufriev, S. V.; Muboyadzhyan, S. A.; Seredkin, N. N.

2017-11-01

The temperature dependences of the thermal and electro physical properties of the zirconium carbide ZrC + C and ZrCa0.95 were studied in the temperature range 2000-5000 K. The Zr+C specimens were in the form of thin layers sputtered on quarts substrate and ZrC0.95 specimens were in the form of plates cut off from the sintered block. The properties are measured: temperature and heat of fusion, enthalpy, specific heat and resistivity, referred to the initial dimensions. A steep increase in the specific heat of these substances before melting and a sharp decrease after melting were observed at a heating rate of ∼ 108 K/s, which is possibly due to the formation of Frenkel pair defects in the specimens.

Corrosion resistance of zirconium oxynitride coatings deposited via DC unbalanced magnetron sputtering and spray pyrolysis-nitriding

NASA Astrophysics Data System (ADS)

Cubillos, G. I.; Bethencourt, M.; Olaya, J. J.

2015-02-01

ZrOxNy/ZrO2 thin films were deposited on stainless steel using two different methods: ultrasonic spray pyrolysis-nitriding (SPY-N) and the DC unbalanced magnetron sputtering technique (UBMS). Using the first method, ZrO2 was initially deposited and subsequently nitrided in an anhydrous ammonia atmosphere at 1023 K at atmospheric pressure. For UBMS, the film was deposited in an atmosphere of air/argon with a Φair/ΦAr flow ratio of 3.0. Structural analysis was carried out through X-ray diffraction (XRD), and morphological analysis was done through scanning electron microscopy (SEM) and atomic force microscopy (AFM). Chemical analysis was carried out using X-ray photoelectron spectroscopy (XPS). ZrOxNy rhombohedral polycrystalline film was produced with spray pyrolysis-nitriding, whereas using the UBMS technique, the oxynitride films grew with cubic Zr2ON2 crystalline structures preferentially oriented along the (2 2 2) plane. Upon chemical analysis of the surface, the coatings exhibited spectral lines of Zr3d, O1s, and N1s, characteristic of zirconium oxynitride/zirconia. SEM analysis showed the homogeneity of the films, and AFM showed morphological differences according to the deposition technique of the coatings. Zirconium oxynitride films enhanced the stainless steel's resistance to corrosion using both techniques. The protective efficacy was evaluated using electrochemical techniques based on linear polarization (LP). The results indicated that the layers provide good resistance to corrosion when exposed to chloride-containing media.

Zirconium

USGS Publications Warehouse

Bedinger, G.M.

2013-01-01

Zirconium is the 20th most abundant element in the Earth’s crust. It occurs in a variety of rock types and geologic environments but most often in igneous rocks in the form of zircon (ZrSiO4). Zircon is recovered as a coproduct of the mining and processing of heavy mineral sands for the titanium minerals ilmenite and rutile. The sands are formed by the weathering and erosion of rock containing zircon and titanium heavy minerals and their subsequent concentration in sedimentary systems, particularly in coastal environments. A small quantity of zirconium, less than 10 kt/a (11,000 stpy), compared with total world production of 1.4 Mt (1.5 million st) in 2012, was derived from the mineral baddeleyite (ZrO2), produced from a single source in Kovdor, Russia.

Pyroelectric response in crystalline hafnium zirconium oxide (Hf 1- x Zr x O 2 ) thin films

DOE PAGES

Smith, S. W.; Kitahara, A. R.; Rodriguez, M. A.; ...

2017-02-13

Pyroelectric coefficients were measured for 20 nm thick crystalline hafnium zirconium oxide (Hf 1-xZr xO 2) thin films across a composition range of 0 ≤ x ≤ 1. Pyroelectric currents were collected near room temperature under zero applied bias and a sinusoidal oscillating temperature profile to separate the influence of non-pyroelectric currents. The pyroelectric coefficient was observed to correlate with zirconium content, increased orthorhombic/tetragonal phase content, and maximum polarization response. The largest measured absolute value was 48 μCm -2K -1 for a composition with x = 0.64, while no pyroelectric response was measured for compositions which displayed no remanent polarizationmore » (x = 0, 0.91, 1).« less

High temperature, low-cycle fatigue of copper-base alloys in argon. Part 1: Preliminary results for 12 alloys at 1000 F (538 C)

NASA Technical Reports Server (NTRS)

Conway, J. B.; Stentz, R. H.; Berling, J. T.

1973-01-01

Short-term tensile evaluations at room temperature and 538 C and low-cycle fatigue evaluations at 538 C are presented for the following materials: Zirconium copper-annealed, Zirconium copper-1/4 hard, Zirconium copper-1/2 hard, Tellurium copper-1/2 hard, Chromium copper-SA and aged, OFHC copper-hard, OFHC copper-1/4 hard, OFHC copper-annealed, Silver-as drawn, Zr-Cr-Mg copper-SA, CW and aged, Electroformed copper-30-35 ksi, and Co-Be-Zr- copper-SA, aged. A total of 50 tensile tests and 76 low-cycle fatigue tests were performed using a strain rate of 0.2 percent per second.

Zirconium doped nano-dispersed oxides of Fe, Al and Zn for destruction of warfare agents

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stengl, Vaclav, E-mail: stengl@uach.cz; Houskova, Vendula; Bakardjieva, Snejana

2010-11-15

Zirconium doped nano dispersive oxides of Fe, Al and Zn were prepared by a homogeneous hydrolysis of the respective sulfate salts with urea in aqueous solutions. Synthesized metal oxide hydroxides were characterized using Brunauer-Emmett-Teller (BET) surface area and Barrett-Joiner-Halenda porosity (BJH), X-ray diffraction (XRD), infrared spectroscopy (IR), scanning electron microscopy (SEM) and energy-dispersive X-ray microanalysis (EDX). These oxides were taken for an experimental evaluation of their reactivity with sulfur mustard (HD or bis(2-chloroethyl)sulfide), soman (GD or (3,3'-Dimethylbutan-2-yl)-methylphosphonofluoridate) and VX agent (S-[2-(diisopropylamino)ethyl]-O-ethyl-methylphosphonothionate). The presence of Zr{sup 4+} dopant can increase both the surface area and the surface hydroxylation of the resultingmore » doped oxides, decreases their crystallites' sizes thereby it may contribute in enabling the substrate adsorption at the oxide surface thus it can accelerate the rate of degradation of warfare agents. Addition of Zr{sup 4+} converts the product of the reaction of ferric sulphate with urea from ferrihydrite to goethite. We found out that doped oxo-hydroxides Zr-FeO(OH) - being prepared by a homogeneous hydrolysis of ferric and zirconium oxo-sulfates mixture in aqueous solutions - exhibit a comparatively higher degradation activity towards chemical warfare agents (CWAs). Degradation of soman or VX agent on Zr-doped FeO(OH) containing ca. 8.3 wt.% of zirconium proceeded to completion within 30 min.« less

Photocatalytic performance of freestanding tetragonal zirconia nanotubes formed in H2O2/NH4F/ethylene glycol electrolyte by anodisation of zirconium

NASA Astrophysics Data System (ADS)

Rozana, Monna; Izza Soaid, Nurul; Kian, Tan Wai; Kawamura, Go; Matsuda, Atsunori; Lockman, Zainovia

2017-04-01

ZrO2 nanotubes (ZrNTs) were produced by anodisation of zirconium foil in H2O2/NH4F/ethylene glycol electrolyte. The as-anodised foils were then soaked in the anodising electrolyte for 12 h. Soaking weakens the adherence of the anodic layer from the substrate resulting in freestanding ZrNTs (FS-ZrNTs). Moreover, the presence of H2O2 in the electrolyte also aids in weakening the adhesion of the film from the foil, as foil anodised in electrolyte without H2O2 has good film adherence. The as-anodised FS-ZrNTs film was amorphous and crystallised to predominantly tetragonal phase upon annealing at >300 °C. Annealing must, however, be done at <500 °C to avoid monoclinic ZrO2 formation and nanotubes disintegration. FS-ZrNTs annealed at 450 °C exhibited the highest photocatalytic ability to degrade methyl orange (MO), whereby 82% MO degradation was observed after 5 h, whereas FS-ZrNTs with a mixture of monoclinic and tetragonal degraded 70% of MO after 5 h.

X ray photoelectron spectroscopy (XPS) analysis of Photosensitive ZrO2 array

NASA Astrophysics Data System (ADS)

Li, Y.; Zhao, G.; Zhu, R.; Kou, Z.

2018-03-01

Based on organic zirconium source as the starting material, by adding chemical modifiers which are made up with photosensitive ZrO2 sol. A uniformed ZrO2 array dot was fabricated with a mean diameter of around 800 nm. By using UV-vis spectra and X-ray photoelectron spectroscopy analysis method, studies the photosensitive ZrO2 gel film of photochemical reaction process and the photosensitive mechanism, to determine the zirconium atom centered chelate structure, reaction formed by metal chelate Zr atom for the center, and to establish the molecular model of the chelate. And studied the ultraviolet light in the process of the variation of the XPS spectra, Zr3d5/2 to 184.9 eV corresponding to the binding energy of the as the combination of state peak gradually reduce; By combining with the status of Zr-O peak gradually increase; The strength of the peak is gradually decline. This suggests that in the process of ultraviolet light photo chemical reaction happened. This study is of great significance to the micro fabrication of ZrO2 array not only to the memory devices but also to the optical devices.

Hydrothermal synthesis of copper zirconium phosphate hydrate [Cu(OH)2Zr(HPO4)2·2H2O] and an investigation of its lubrication properties in grease.

PubMed

Zhang, Xiaosheng; Xu, Hong; Zuo, Zhijun; Lin, Zhi; Ferdov, Stanislav; Dong, Jinxiang

2013-08-28

Copper zirconium phosphate hydrate (Cu(OH)2Zr(HPO4)2·2H2O, hereafter referred to as Cu-α-ZrP) with high crystallinity was directly synthesized in a NaF-CuO-ZrO-P2O5-H2O system under hydrothermal conditions. The copper ion was confirmed to be an exchangeable cation in the Cu-α-ZrP through elemental analysis and a proton ion exchange process. The crystal structure of the Cu-α-ZrP was determined ab initio by using X-ray powder diffraction data. In the structure, the CuO6 octahedron would be located in an exchangeable atom position. Moreover, Cu-α-ZrP was evaluated as an additive in grease in a four ball test. The maximum nonseizure load (PB, representing the load-carrying capacity) of the base grease containing Cu-α-ZrP was increased from 353 to 1235 N. The excellent load-carrying capacity may be explained by the easier adherence of the material to the worn surface forming a tight protective film.

The distribution of zirconium and hafnium in terrestrial rocks, meteorites and the moon

NASA Technical Reports Server (NTRS)

Ehmann, W. D.; Chyi, L. L.; Garg, A. N.; Ali, M. Z.

1979-01-01

It is shown that Zr and Hf are not always fractionated in terrestrial igneous differentiation or regional metamorphism. Data do support a Zr-Hf fractionation in the differentiation of the alkali olivine magma at St. Helena Island. A strong Zr-Hf fractionation exists among lunar rocks and minerals. Ilmenite is an excellent concentrator of Zr and Hf and always exhibits high Zr/Hf ratios. Chondritic meteorites exhibit rather uniform Zr abundances and Zr/Hf ratios but a distinct Zr-Hf fractionation is observed among the eucrite and diogenite achondrites.

Synthesis and hydration behavior of calcium zirconium aluminate (Ca{sub 7}ZrAl{sub 6}O{sub 18}) cement

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kang, Eun-Hee; Yoo, Jun-Sang; Kim, Bo-Hye

2014-02-15

Calcium zirconium aluminate (Ca{sub 7}ZrAl{sub 6}O{sub 18}) cements were prepared by solid state reaction and polymeric precursor methods, and their phase evolution, morphology, and hydration behavior were investigated. In polymeric precursor method, a nearly single phase Ca{sub 7}ZrAl{sub 6}O{sub 18} was obtained at relatively lower temperature (1200 °C) whereas in solid state reaction, a small amount of CaZrO{sub 3} coexisted with Ca{sub 7}ZrAl{sub 6}O{sub 18} even at higher temperature (1400 °C). Unexpectedly, Ca{sub 7}ZrAl{sub 6}O{sub 18} synthesized by polymeric precursor process was the large-sized and rough-shaped powder. The planetary ball milling was employed to control the particle size and shape.more » The hydration behavior of Ca{sub 7}ZrAl{sub 6}O{sub 18} was similar to that of Ca{sub 3}Al{sub 2}O{sub 6} (C3A), but the hydration products were Ca{sub 3}Al{sub 2}O{sub 6}·6H{sub 2}O (C3AH6) and several intermediate products. Thus, Zr (or ZrO{sub 2}) stabilized the intermediate hydration products of C3A.« less

η(6) -Arene-Zirconium-PNP-Pincer Complexes: Mechanism of Their Hydrogenolytic Formation and Their Reactivity as Zirconium(II) Synthons.

PubMed

Plundrich, Gudrun T; Wadepohl, Hubert; Clot, Eric; Gade, Lutz H

2016-06-27

The cyclometalated monobenzyl complexes [(Cbzdiphos(R) -CH)ZrBnX] 1 (iPr) Cl and 1 (Ph) I reacted with dihydrogen (10 bar) to yield the η(6) -toluene complexes [(Cbzdiphos(R) )Zr(η(6) -tol)X] 2 (iPr) Cl and 2 (Ph) I (cbzdiphos=1,8-bis(phosphino)-3,6-di-tert-butyl-9H-carbazole). The arene complexes were also found to be directly accessible from the triiodide [(Cbzdiphos(Ph) )ZrI3 ] through an in situ reaction with a dibenzylmagnesium reagent and subsequent hydrogenolysis, as exemplified for the η(6) -mesitylene complex [(Cbzdiphos(Ph) )Zr(η(6) -mes)I] (3 (Ph) I). The tolyl-ring in 2 (iPr) Cl adopts a puckered arrangement (fold angle 23.3°) indicating significant arene-1,4-diido character. Deuterium labeling experiments were consistent with an intramolecular reaction sequence after the initial hydrogenolysis of a Zr-C bond by a σ-bond metathesis. A DFT study of the reaction sequence indicates that hydrogenolysis by σ-bond metathesis first occurs at the cyclometalated ancillary ligand giving a hydrido-benzyl intermediate, which subsequently reductively eliminates toluene that then coordinates to the Zr atom as the reduced arene ligand. Complex 2 (Ph) I was reacted with 2,6-diisopropylphenyl isocyanide giving the deep blue, diamagnetic Zr(II) -diisocyanide complex [(Cbzdiphos(Ph) )Zr(CNDipp)2 I] (4 (Ph) I). DFT modeling of 4 (Ph) I demonstrated that the HOMO of the complex is primarily located as a "lone pair on zirconium", with some degree of back-bonding into the C≡N π* bond, and the complex is thus most appropriately described as a zirconium(II) species. Reaction of 2 (Ph) I with trimethylsilylazide (N3 TMS) and 2 (iPr) Cl with 1-azidoadamantane (N3 Ad) resulted in the formation of the imido complexes [(Cbzdiphos(R) )Zr=NR'(X)] 5 (iPr) Cl-NAd and 5 (Ph) I-NTMS, respectively. Reaction of 2 (iPr) Cl with azobenzene led to N-N bond scission giving 6 (iPr) Cl, in which one of the NPh-fragments is coupled with the carbazole nitrogen to form a central η(2) -bonded hydrazide(-1), whereas the other NPh-fragment binds to zirconium acting as an imido-ligand. Finally, addition of pyridine to 2 (iPr) Cl yielded the dark purple complex [(Cbzdiphos(iPr) )Zr(bpy)Cl] (7 (iPr) Cl) through a combination of CH-activation and C-C-coupling. The structural data and UV/Vis spectroscopic properties of 7 (iPr) Cl indicate that the bpy (bipyridine) may be regarded as a (dianionic) diamido-type ligand. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Mechanical, electronic, and thermodynamic properties of zirconium carbide from first-principles calculations

NASA Astrophysics Data System (ADS)

Yang, Xiao-Yong; Lu, Yong; Zheng, Fa-Wei; Zhang, Ping

2015-11-01

Mechanical, electronic, and thermodynamic properties of zirconium carbide have been systematically studied using the ab initio calculations. The calculated equilibrium lattice parameter, bulk modulus, and elastic constants are all well consistent with the experimental data. The electronic band structure indicates that the mixture of C 2p and Zr 4d and 4p orbitals around the Fermi level makes a large covalent contribution to the chemical bonds between the C and Zr atoms. The Bader charge analysis suggests that there are about 1.71 electrons transferred from each Zr atom to its nearest C atom. Therefore, the Zr-C bond displays a mixed ionic/covalent character. The calculated phonon dispersions of ZrC are stable, coinciding with the experimental measurement. A drastic expansion in the volume of ZrC is seen with increasing temperature, while the bulk modulus decreases linearly. Based on the calculated phonon dispersion curves and within the quasi-harmonic approximation, the temperature dependence of the heat capacities is obtained, which gives a good description compared with the available experimental data. Project supported by the National Natural Science Foundation of China (Grant No. 51071032).

Method For Processing Spent (Trn,Zr)N Fuel

DOEpatents

Miller, William E.; Richmann, Michael K.

2004-07-27

A new process for recycling spent nuclear fuels, in particular, mixed nitrides of transuranic elements and zirconium. The process consists of two electrorefiner cells in series configuration. A transuranic element such as plutonium is reduced at the cathode in the first cell, zirconium at the cathode in the second cell, and nitrogen-15 is released and captured for reuse to make transuranic and zirconium nitrides.

Synthesis of monodisperse spherical nanometer ZrO{sub 2} (Y{sub 2}O{sub 3}) powders via the coupling route of w/o emulsion with urea homogenous precipitation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chang, Ying; Dong, Shijie, E-mail: dongsjsj@163.com; Wang, Huihu

2012-03-15

Graphical abstract: In this paper, the weight loss and reaction evolution of ZrO{sub 2} precursor powders are determined by TG-DTA, and 600 Degree-Sign C is the most reasonable calcination temperature of precursor according to the TG-DTA. At the same time, we study the effect of reaction conditions upon the particle sizes, such as concentration of zirconium nitrate solution, reaction temperature and urea content. TEM micrographs of zirconia powders indicated that ZrO{sub 2} nano-powders prepared via the coupling route of w/o emulsion with homogenous precipitation possess spherical shape and excellent dispersing. Highlights: Black-Right-Pointing-Pointer The monodisperse spherical nanometer ZrO{sub 2} (Y{sub 2}O{submore » 3}) powders have been prepared via the coupling route of w/o emulsion with urea homogenous precipitation. Black-Right-Pointing-Pointer The principle of the coupling route of emulsion with homogenous precipitation has been studied. Black-Right-Pointing-Pointer The concentration of zirconium nitrate, reaction temperature of water bath and the quantity of urea effect regularly on the average particle size of products. -- Abstract: Using xylol as the oil phase, span-80 as the surfactant, and an aqueous solution containing zirconium (3 mol% Y{sub 2}O{sub 3}) and urea as the water phase, tetragonal phase ZrO{sub 2} nano-powders have been prepared via the coupling route of w/o emulsion with urea homogenous precipitation. The effects of the zirconium concentration, the reaction temperature and the urea content on the average size of the products have been examined. The as-prepared ZrO{sub 2} powders and the precursor powders were characterized by TGA-DTA, XRD, TEM and BET. Experimental results indicate that ZrO{sub 2} powders prepared via the coupling route of w/o emulsion with urea homogenous precipitation possess some excellent characteristics, such as well-rounded spherical shape and excellent dispersing.« less

METHOD AND ALLOY FOR BONDING TO ZIRCONIUM

DOEpatents

McCuaig, F.D.; Misch, R.D.

1960-04-19

A brazing alloy can be used for bonding zirconium and its alloys to other metals, ceramics, and cermets, and consists of 6 to 9 wt.% Ni, 6 to 9 wn~.% Cr, Mo, or W, 0 to 7.5 wt.% Fe, and the balance Zr.

In situ Raman spectroscopic investigation of zirconium-niobium alloy corrosion under hydrothermal conditions

NASA Astrophysics Data System (ADS)

Maslar, J. E.; Hurst, W. S.; Bowers, W. J.; Hendricks, J. H.

2001-10-01

In situ Raman spectroscopy was employed to investigate corrosion of a zirconium-niobium alloy in air-saturated water at a pressure of 15.5 MPa and temperatures ranging from 22 to 407 °C in an optically accessible flow cell. Monoclinic ZrO 2 (m-ZrO 2) was identified under all conditions after the coupon was heated to 255 °C for 19 h. Cubic ZrO 2 (c-ZrO 2) was tentatively identified in situ during heating at temperatures between 306 and 407 °C, but was not observed under any other conditions. Species tentatively identified as α-CrOOH and a Cr VI and/or Cr III/Cr VI compound were observed in situ during heating at temperatures between 255 and 407 °C, but were not observed under any other conditions. The chromium compounds were identified as corrosion products released from the optical cell and/or flow system.

High temperature mechanical properties of a zirconium-modified, precipitation- strengthened nickel, 30 percent copper alloy

NASA Technical Reports Server (NTRS)

Whittenberger, J. D.

1974-01-01

A precipitation-strengthened Monel-type alloy has been developed through minor alloying additions of zirconium to a base Ni-30Cu alloy. The results of this exploratory study indicate that thermomechanical processing of a solution-treated Ni-30Cu-0.2Zr alloy produced a dispersion of precipitates. The precipitates have been tentatively identified as a Ni5Zr compound. A comparison of the mechanical properties, as determined by testing in air, of the zirconium-modified alloy to those of a Ni-30Cu alloy reveals that the precipitation-strengthened alloy has improved tensile properties to 1200 K and improved stress-rupture properties to 1100 K. The oxidation characteristics of the modified alloy appeared to be equivalent to those of the base Ni-30Cu alloy.

Solution treatment-delayed zirconium-strengthening behavior in Ti-7.5Mo-xZr alloy system

NASA Astrophysics Data System (ADS)

Chern Lin, Jiin-Huey; Fu, Yen-Han; Chen, Yen-Chun; Peng, Yu-Po; Ju, Chien-Ping

2018-01-01

The present study was devoted to investigate and compare the Zr-strengthening behavior in as-cast (AC) and solution-treated (ST) Ti-7.5Mo-xZr alloys. The experimental results indicated that AC Ti-7.5Mo and AC Ti-7.5Mo-1Zr alloys substantially had an orthorhombic {α }\\prime\\prime phase with a fine, acicular morphology. The content of equi-axed β phase continued to increase with increased Zr content at the expense of {α }\\prime\\prime phase. The threshold Zr content for the formation of β phase in the ST Ti-7.5Mo-xZr alloys was apparently higher than that in the AC Ti-7.5Mo-xZr alloys. The β granular structure was revealed in ST Ti-7.5Mo-5Zr alloy, which increased with increased Zr content. Unlike AC Ti-7.5Mo-9Zr alloy, within each grain of ST Ti-7.5Mo-9Zr alloy were still observed a significant portion of {α }\\prime\\prime morphology. AC Ti-7.5Mo alloy had the lowest YS, lowest tensile modulus and highest elongation among all AC Ti-7.5Mo-xZr alloys. When Zr content increased, both YS and modulus significantly increased while the elongation significantly decreased. Compared to AC Ti-7.5Mo alloy, AC Ti-7.5Mo-9Zr alloy had almost double YS, indicating the effectiveness of Zr-induced strengthening in the AC Ti-7.5Mo-xZr alloys. Compared to AC Ti-7.5Mo, ST Ti-7.5Mo alloys had lower YS, UTS and tensile modulus with almost the same elongation. All the XRD, metallography and tensile test results consistently indicated that the presence of Zr could accelerate the formation of β phase and effectively strengthen the AC Ti-7.5Mo-xZr alloys. A phenomenon of delayed β formation and delayed strengthening was noted in the ST Ti-7.5Mo-xZr alloys, compared to the AC Ti-7.5Mo-xZr alloys.

In situ crystallized zirconium phenylphosphonate films with crystals vertically to the substrate and their hydrophobic, dielectric, and anticorrosion properties.

PubMed

Cui, Zhaohui; Zhang, Fazhi; Wang, Lei; Xu, Sailong; Guo, Xiaoxiao

2010-01-05

The in situ crystallization technique has been utilized to fabricate zirconium phenylphosphonate (ZrPP) films with their hexagonal crystallite perpendicular to the copper substrate. The micro/nano roughness surface structure, as well as the intrinsic hydrophobic characteristic of the surface functional groups, affords ZrPP films excellent hydrophobicity with water contact angle (CA) ranging from 134 degrees to 151 degrees , without any low-surface-energy modification. Particularly, in the corrosive solutions such as acidic or basic solutions over a wide pH from 2 to 12, no obvious fluctuation in CA was observed for all the ZrPP film. The k values of the hydrophobic ZrPP films are in the low-k range (k < 3.0), meeting the development of ultra-large-scale integration (ULSI) circuits. The hydrophobicity feature is proposed to bear ZrPP film a more stable low-k value in an ambient atmosphere. Besides, the polarization current of ZrPP films is reduced by 2 orders of magnitude, compared to that of the untreated copper substrate. Even deposited in a vacuum oven for 30 days at room temperature, ZrPP films also show excellent corrosion resistance, indicating a stable anticorrosion property.

Development of phase analysis methods of impurity elements in alloys based on iron and nickel

NASA Astrophysics Data System (ADS)

Andreeva, N. A.; Anuchkin, S. N.; Volchenkova, V. A.; Kazenas, E. K.; Penkina, T. N.; Fomina, A. A.

2018-04-01

Using the method of AES with ICP, new methods have been developed for quantifying the content of various forms of existence of impurity elements: Al-Al2O3; Zr-ZrO2 in alloys based on iron (Fe-Sn) and nickel (Ni-Sn). Open systems were used to dissolve Al and Zr. To translate difficult-to-open aluminum oxides (corundum) and zirconium oxide (baddeleyite) into the solution, accelerated techniques were developed using the microwave system Mars 5. To confirm the completeness of the dissolution of oxides, a classical scheme of alloy fusion with alkali metal salts was used. Optimal analytical parameters for determining the elements: Al and Zr were chosen. The influence of matrix elements (iron and nickel) and methods of its elimination were studied. This made it possible to determine the elements in a wide concentration range from 1 • 10-3 to n% Al and from 1 • 10-4 to n% Zr without preliminary separation of the matrix with good metrological characteristics. The relative standard deviation (Sr) does not exceed 0,2. The separate determination of the contents of aluminum and aluminium oxide in the model melt of Fe-Sn-Al2O3 and zirconium and zirconium oxide in the Ni-Sn-ZrO2 model melt allowed us to estimate the number of nanoparticles participating in the heterophase interaction with tin and retired to the interface in the form of ensembles and the number of nanoparticles present in the melt and affecting the crystallization process and the structure of the metal.

Environmental Effects on Zirconium Hydroxide Nanoparticles and Chemical Warfare Agent Decomposition: Implications of Atmospheric Water and Carbon Dioxide.

PubMed

Balow, Robert B; Lundin, Jeffrey G; Daniels, Grant C; Gordon, Wesley O; McEntee, Monica; Peterson, Gregory W; Wynne, James H; Pehrsson, Pehr E

2017-11-15

Zirconium hydroxide (Zr(OH) 4 ) has excellent sorption properties and wide-ranging reactivity toward numerous types of chemical warfare agents (CWAs) and toxic industrial chemicals. Under pristine laboratory conditions, the effectiveness of Zr(OH) 4 has been attributed to a combination of diverse surface hydroxyl species and defects; however, atmospheric components (e.g., CO 2 , H 2 O, etc.) and trace contaminants can form adsorbates with potentially detrimental impact to the chemical reactivity of Zr(OH) 4 . Here, we report the hydrolysis of a CWA simulant, dimethyl methylphosphonate (DMMP) on Zr(OH) 4 determined by gas chromatography-mass spectrometry and in situ attenuated total reflectance Fourier transform infrared spectroscopy under ambient conditions. DMMP dosing on Zr(OH) 4 formed methyl methylphosphonate and methoxy degradation products on free bridging and terminal hydroxyl sites of Zr(OH) 4 under all evaluated environmental conditions. CO 2 dosing on Zr(OH) 4 formed adsorbed (bi)carbonates and interfacial carbonate complexes with relative stability dependent on CO 2 and H 2 O partial pressures. High concentrations of CO 2 reduced DMMP decomposition kinetics by occupying Zr(OH) 4 active sites with carbonaceous adsorbates. Elevated humidity promoted hydrolysis of adsorbed DMMP on Zr(OH) 4 to produce methanol and regenerated free hydroxyl species. Hydrolysis of DMMP by Zr(OH) 4 occurred under all conditions evaluated, demonstrating promise for chemical decontamination under diverse, real-world conditions.

Homogeneity of Pb(Zr ,Ti)O3 thin films by chemical solution deposition: Extended x-ray absorption fine structure spectroscopy study of zirconium local environment

NASA Astrophysics Data System (ADS)

Malic, Barbara; Arcon, Iztok; Kodre, Alojz; Kosec, Marija

2006-09-01

Sols for Pb(Zr0.53Ti0.47)O3 (PZT) thin films were prepared by 2-methoxyethanol route from lead acetate, titanium n-propoxide, and zirconium n-propoxide, the latter either unmodified or modified with acetylacetone or acetic acid in a 2/1 molar ratio and deposited on sapphire (0001). By Zr K-edge extended x-ray absorption fine structure (EXAFS) spectroscopy, the structural changes in the Zr local environment, induced by the addition of the two modifiers, were followed from the synthesis of the PZT sol to the transition to the amorphous film. In the unmodified PZT sol segregation of Zr species occurs from the original dimers present in the Zr propoxide solution in 2-methoxyethanol. The immediate neighborhood of Zr atoms changes markedly at the transition from the sol to the amorphous film: the local structure around Zr atoms is similar to the one found in tetragonal zirconia particles. The modification of Zr propoxide with acetylacetone in 2-methoxyethanol results in Zr monomers. In PZT sol, clustering of Zr species is observed continuing into the amorphous film. By modification with acetic acid the original dimeric structure of the Zr precursor is retained in the PZT sol and further in the amorphous film. Selective modification of Zr propoxide with acetic acid therefore results in a more homogeneous distribution of Zr atoms in the PZT sol and amorphous film than in both as-received and acetylacetone-modified Zr propoxide.

Structural environments of incompatible elements in silicate glass/melt systems: I. Zirconium at trace levels

NASA Astrophysics Data System (ADS)

Farges, Franã§Ois; Ponader, Carl W.; Brown, Gordon E., Jr.

1991-06-01

The structural environments of trace levels (2˜000 ppm) of Zr 4+ in several silicate glasses were examined as a function of melt composition and polymerization using Extended X-ray Absorption Fine Structure (EXAFS) spectroscopy. Glass compositions investigated were albite (NaAlSi 3O 8: AB) and a peralkaline composition (Na 3.3AlSi 7O 17: PR)- Zirconium was added to the oxide-carbonate mix prior to melting in the form of ZrO 2 (baddeleyite). A second set of Zr-silicate glasses containing 2000 ppm Zr and 1.0 to 2.4 wt% halogens (F as NaF and Cl as NaCl) was also synthesized. These included the Zr-AB and Zr-PR base-glass compositions as well as Zr-sodium trisilicate composition (Na2Si 3O 7: TS). In all glasses studied, Zr is mainly 6-coordinated by oxygen atoms ( d[Zr-O] ˜2.07 ± 0.01 Å). In the most polymerized glass (AB), a small but significant amount of Zr was also found to occur in 8-coordinated sites ( d[Zr-O] ˜2.22 Å). No clear evidence for F or Cl complexes of Zr was observed in any of the halogen-containing glasses. The regularity of the Zr site increases in the series AB < TS ˜PR. We attribute this change to an increase in the number of non-bridging oxygens in the first-coordination sphere of Zr related to the depolymerizing effects of halogens and/or sodium. Minor but significant interactions of Zr with the tetrahedral network were observed ( d[Zr-{Si, Al}] ˜3.65-3.71 Å ± 0.03 Å), which are consistent with Zr-O-{Si, Al} angles close to 160-170°, as in catapleiite (Na 2ZrSi 3O 9 · 2H 2O). Intermediaterange order, as reflected by the presence and number of second-neighbor {Si, Al} around Zr, increases significantly with increasing melt polymerization. The local environment around Zr is more strongly influenced by bonding requirements than by the network topology of the melt. Stabilization of zirconium in 6-coordinated sites in relatively depolymerized melts should act to decrease the crystal-melt partition coefficients of Zr and may explain the normally incompatible character of Zr during magmatic differentiation. The presence of Zr in sites of higher coordination (ZrO 8) in highly polymerized melts could be a precursor to the crystallization of zircon from such melts and thus may explain why Zr becomes a more compatible element, especially in the latest stages of magmatic differentiation.

Zirconium tetrachloride revisited

DOE PAGES

Borjas Nevarez, Rosendo; Balasekaran, Samundeeswari Mariappan; Kim, Eunja; ...

2018-02-19

We present that zirconium tetrachloride, ZrCl 4, is a strategic material with wide-ranging applications. Until now, only one crystallographic study on ZrCl 4has been reported [Krebs (1970).Z. Anorg. Allg. Chem.378, 263–272] and that was more than 40 years ago. The compound used for the previous determination was prepared from ZrO 2 and Cl 2–CCl 4, and single-crystal X-ray diffraction (SCXRD) studies on ZrCl 4 obtained from Zr metal have not yet been reported. In this context, we prepared ZrCl 4 from the reaction of Zr metal and Cl 2 gas in a sealed tube and investigated its structure at 100,more » 150, 200, 250, and 300 K. At 300 K, the SCXRD analysis indicates that ZrCl 4 crystallizes in the orthorhombic space group Pca2 1 [a= 6.262 (9),b= 7.402 (11),c= 12.039 (17) Å, andV= 558.0 (14) Å 3] and consists of infinite zigzag chains of edge-sharing ZrCl 6 octahedra. This chain motif is similar to that observed previously in ZrCl 4, but the structural parameters and space group differ. Finally, in the temperature range 100–300 K, no phase transformation was identified, while elongation of intra-chain Zr...Zr [3.950 (1) Å at 100 K and 3.968 (5) Å at 300 K] and inter-chain Cl...Cl [3.630 (3) Å at 100 K and 3.687 (9) Å at 300 K] distances occurred.« less

Structure, mechanical properties, and grindability of dental Ti-Zr alloys.

PubMed

Ho, Wen-Fu; Chen, Wei-Kai; Wu, Shih-Ching; Hsu, Hsueh-Chuan

2008-10-01

Structure, mechanical properties and grindability of a series of binary Ti-Zr alloys with zirconium contents ranging from 10 to 40 wt% have been investigated. Commercially pure titanium (c.p. Ti) was used as a control. Experimental results indicated that the diffraction peaks of all the Ti-Zr alloys matched those for alpha Ti. No beta-phase peaks were found. The hardness of the Ti-Zr alloys increased as the Zr contents increased, and ranged from 266 HV (Ti-10Zr) to 350 HV (Ti-40Zr). As the concentration of zirconium in the alloys increased, the strength, elastic recovery angles and hardness increased. Moreover, the elastically recoverable angle of Ti-40Zr was higher than of c.p. Ti by as much as 550%. The grindability of each metal was found to be largely dependent on the grinding conditions. The Ti-40Zr alloy had a higher grinding rate and grinding ratio than c.p. Ti at low speed. The grinding rate of the Ti-40Zr alloy at 500 m/min was about 1.8 times larger than that of c.p. Ti, and the grinding ratio was about 1.6 times larger than that of c.p. Ti. Our research suggested that the Ti-40Zr alloy has better mechanical properties, excellent elastic recovery capability and improved grindability at low grinding speed. The Ti-40Zr alloy has a great potential for use as a dental machining alloy.

Magnesium-Aluminum-Zirconium Oxide Amorphous Ternary Composite: A Dense and Stable Optical Coating

NASA Technical Reports Server (NTRS)

Sahoo, N. K.; Shapiro, A. P.

1998-01-01

In the present work, the process parameter dependent optical and structural properties of MgO-Al(2)O(3)-ZrO(2) ternary mixed-composite material have been investigated. Optical properties were derived from spectrophotometric measurements. The surface morphology, grain size distributions, crystallographic phases and process dependent material composition of films have been investigated through the use of Atomic Force Microscopy (AFM), X-ray diffraction analysis and Energy Dispersive X- ray (EDX) analysis. EDX analysis made evident the correlation between the optical constants and the process dependent compositions in the films. It is possible to achieve environmentally stable amorphous films with high packing density under certain optimized process conditions.

Adsorption of phosphate in water using one-step synthesized zirconium-loaded reduced graphene oxide

NASA Astrophysics Data System (ADS)

Luo, Xin; Wang, Xiurong; Bao, Shaopan; Liu, Xiawei; Zhang, Weicheng; Fang, Tao

2016-12-01

In this account, a one-step green hydrothermal method for zirconium-loaded reduced graphene oxide (RGO-Zr) adsorbent was developed in pure water. It is based on the formation of initially strong-coupling RGO-Zr nanocomposites followed by in situ reduction of GO to RGO during the hydrothermal treatment. The phosphate adsorption performance of the as-prepared nanocomposites was investigated in aqueous environment under various conditions. The characterization results of RGO-Zr nanocomposites showed that ZrO2 was successfully integrated onto the RGO sheets in amorphous. The data from equilibrium phosphate adsorption on RGO-Zr revealed that the adsorption kinetics followed a pseudo-second-order kinetic model, where the adsorption isotherm fitted the Langmuir isotherm model with a maximum adsorption capacity of 27.71 mg P/g at pH 5 and 298 K. The improved phosphate adsorption on RGO-Zr was caused by the dispersion of ZrO2 on the RGO surface. Furthermore, the phosphate adsorption was found insensitive to the increase in pH while it was sensitive to the increase in temperature. The coexisting anions of SO42-, F-, Cl-, NO3- and CO32- affected the phosphate adsorption in a different way. Results suggest that the present RGO-Zr adsorbent has the potential for controlling phosphorus pollution in water.

Structure and Thermodynamical Properties of Zirconium Hydrides from First-Principle

NASA Astrophysics Data System (ADS)

Blomqvist, Jakob; Olofsson, Johan; Alvarez, Anna-Maria; Bjerkén, Christina

Zirconium alloys are used as nuclear fuel cladding material due to their mechanical and corrosion resistant properties together with their favorable cross-section for neutron scattering. At running conditions, however, there will be an increase of hydrogen in the vicinity of the cladding surface at the water side of the fuel. The hydrogen will diffuse into the cladding material and at certain conditions, such as lower temperatures and external load, hydrides will precipitate out in the material and cause well known embrittlement, blistering and other unwanted effects. Using phase-field methods it is now possible to model precipitation buildup in metals, for example as a function of hydrogen concentration, temperature and external load, but the technique relies on input of parameters, such as the formation energy of the hydrides and matrix. To that end, we have computed, using the density functional theory (DFT) code GPAW, the latent heat of fusion as well as solved the crystal structure for three zirconium hydride polymorphs: δ-ZrH1.6, γ-ZrH, and Є-ZrH2.

Pyroprocessing of oxidized sodium-bonded fast reactor fuel - An experimental study of treatment options for degraded EBR-II fuel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hermann, S.D.; Gese, N.J.; Wurth, L.A.

An experimental study was conducted to assess pyrochemical treatment options for degraded EBR-II fuel. As oxidized material, the degraded fuel would need to be converted back to metal to enable electrorefining within an existing electro-metallurgical treatment process. A lithium-based electrolytic reduction process was studied to assess the efficacy of converting oxide materials to metal with a particular focus on the impact of zirconium oxide and sodium oxide on this process. Bench-scale electrolytic reduction experiments were performed in LiCl-Li{sub 2}O at 650 C. degrees with combinations of manganese oxide (used as a surrogate for uranium oxide), zirconium oxide, and sodium oxide.more » In the absence of zirconium or sodium oxide, the electrolytic reduction of MnO showed nearly complete conversion to metal. The electrolytic reduction of a blend of MnO-ZrO{sub 2} in LiCl - 1 wt% Li{sub 2}O showed substantial reduction of manganese, but only 8.5% of the zirconium was found in the metal phase. The electrolytic reduction of the same blend of MnO-ZrO{sub 2} in LiCl - 1 wt% Li{sub 2}O - 6.2 wt% Na{sub 2}O showed substantial reduction of manganese, but zirconium reduction was even less at 2.4%. This study concluded that ZrO{sub 2} cannot be substantially reduced to metal in an electrolytic reduction system with LiCl - 1 wt% Li{sub 2}O at 650 C. degrees due to the perceived preferential formation of lithium zirconate. This study also identified a possible interference that sodium oxide may have on the same system by introducing a parasitic and cyclic reaction of dissolved sodium metal between oxidation at the anode and reduction at the cathode. When applied to oxidized sodium-bonded EBR-II fuel (e.g., U-10Zr), the prescribed electrolytic reduction system would not be expected to substantially reduce zirconium oxide, and the accumulation of sodium in the electrolyte could interfere with the reduction of uranium oxide, or at least render it less efficient.« less

Synthesis of BaTiO3 and Ba(ZrxTi1-X)O3 by using the soft combustion method

NASA Astrophysics Data System (ADS)

Ahmad, Atiqah; Razak, Khairunisak Abdul

2017-07-01

In this work, barium titanate, BaTiO3 (BT) and Zr doped BT, BaZrxTi1-xO3 (BZT) with powders were successfully produced using the soft combustion method. Barium nitrate and titanium (IV) isopropoxide were used as the starting materials while zirconium (IV) oxynitrate hydrate as the doping precursors, and glycine as the combustion agent. The produced powders were pressed into 12 mm diameter pellets by using 150 MPa cold press. The effect of Zr dopant in BT was studied with molar ratio of x = 0.00, 0.03, 0.05, 0.08 and 0.10. The phase presence was identified using X-ray diffractometer. Morphology of powders and sintered pellets was observed using a scanning electron microscope. Density of the sintered pellets was measured by using Archimedes' principle, while dielectric properties were analysed by using an LCR meter. Pure perovskite BT and BZT structure were obtained after sintering at 1400 °C for 5 h. BZT with x = 0.03 has grain size of 3.9 µm and shows the highest dielectric constant of 525, compared to undoped BT that has the average grain size of 4.2 µm with dielectric constant 223. The results is in agreement with microstructure observation and density of the sample.

Diamond-like carbon coatings with zirconium-containing interlayers for orthopedic implants.

PubMed

Choudhury, Dipankar; Lackner, Juergen; Fleming, Robert A; Goss, Josh; Chen, Jingyi; Zou, Min

2017-04-01

Six types of diamond-like carbon (DLC) coatings with zirconium (Zr)-containing interlayers on titanium alloy (Ti-6Al-4V) were investigated for improving the biotribological performance of orthopedic implants. The coatings consist of three layers: above the substrate a layer stack of 32 alternating Zr and ZrN sublayers (Zr:ZrN), followed by a layer comprised of Zr and DLC (Zr:DLC), and finally a N-doped DLC layer. The Zr:ZrN layer is designed for increasing load carrying capacity and corrosion resistance; the Zr:DLC layer is for gradual transition of stress, thus enhancing layer adhesion; and the N-doped DLC layer is for decreasing friction, squeaking noises and wear. Biotribological experiments were performed in simulated body fluid employing a ball-on-disc contact with a Si 3 N 4 ball and a rotational oscillating motion to mimic hip motion in terms of gait angle, dynamic contact pressures, speed and body temperature. The results showed that the Zr:DLC layer has a substantial influence on eliminating delamination of the DLC from the substrates. The DLC/Si 3 N 4 pairs significantly reduced friction coefficient, squeaking noise and wear of both the Si 3 N 4 balls and the discs compared to those of the Ti-6Al-4V/Si 3 N 4 pair after testing for a duration that is equivalent to one year of hip motion in vivo. Copyright © 2017 Elsevier Ltd. All rights reserved.

INTERMEDIATE STAGES OF REACTIONS FORMING CARBIDES OF TITANIUM, ZIRCONIUM, VANADIUM, NIOBIUM, AND TANTALIUM

DTIC Science & Technology

Tensimetric examination was made of the formation of the carbides TiC , ZrC, VC, NbC and TaC in a vacuum. During x-ray and chemical analysis of...for obtaining TiC , and ZrC through the stage of intermediate oxides Ti2O3, Ti3O5, TiO and Zr2O3, ZrO, respectively and also for the reaction of

Solution Treatment Effect on Tensile, Impact and Fracture Behaviour of Trace Zr Added Al-12Si-1Mg-1Cu Piston Alloy

NASA Astrophysics Data System (ADS)

Kaiser, Md. Salim

2018-04-01

The effects of T6 solution treatment on tensile, impact and fracture properties of cast Al-12Si-1Mg-1Cu piston alloys with trace of zirconium were investigated. Cast alloys were given precipitation strengthening treatment having a sequence of homogenizing, solutionizing, quenching and ageing. Both cast and solutionized samples are isochronally aged for 90 min at different temperatures up to 300 °C. Tensile and impact properties of the differently processed alloys have been studied to understand the precipitation strengthening of the alloys. Fractograpy of the alloys were observed to understand the mode of fracture. It is observed that the improvement in tensile properties in the aged alloys through heat treatment is mainly attributed to the formation of the Al2Cu and Mg2Si precipitates within the Al matrix. Solution treatment improves the tensile strength for the reason that during solution treatment some alloying elements are re-dissolved to produce a solute-rich solid solution. Impact energy decreases with ageing temperature due to formation of GP zones, β' and β precipitates. The fractography shows large and small dimple structure and broken or cracked primary Si, particles. Microstructure study of alloys revealed that the solution treatment improved distribution of silicon grains. The addition of Zr produces an improvement in the tensile properties as a result of its grain refining action and grain coarsening resistance in the matrix at a higher temperature.

A comparative study of the mechanical behaviour of thermally oxidised commercially pure titanium and zirconium.

PubMed

Alansari, A; Sun, Y

2017-10-01

The objective of this study is to compare the mechanical behaviour of thermally oxidised commercially pure titanium (CP-Ti) and commercially pure zirconium (CP-Zr). For this purpose, these two bio-metals were thermally oxidised under the same condition (650°C for 6h) and the oxidised specimens were characterised using various analytical and experimental techniques, including oxygen uptake analysis, layer thickness and hardness measurements, scratch tests, dry sliding friction and wear tests and tribocorrosion tests in Ringer's solution. The results show that under the present thermal oxidation condition, 4 times more oxygen is introduced into CP-Zr than into CP-Ti and the oxide layer produced on CP-Zr is nearly 6 times thicker than that on CP-Ti. Thermally oxidised CP-Zr possesses a higher hardness, a deeper hardening depth and better scratch resistance than thermally oxidised CP-Ti. Under dry sliding and tribocorrosion conditions, thermally oxidised CP-Zr also possesses much better resistance to material removal and a higher load bearing capacity than thermally oxidised CP-Ti. Thus, thermally oxidised Zr possesses much better mechanical behaviour than thermally oxidised Ti. Copyright © 2017 Elsevier Ltd. All rights reserved.

Study on the antibacterial mechanism of copper ion- and neodymium ion-modified α-zirconium phosphate with better antibacterial activity and lower cytotoxicity.

PubMed

Cai, Xiang; Zhang, Bin; Liang, Yuanyuan; Zhang, Jinglin; Yan, Yinghui; Chen, Xiaoyin; Wu, Zhimin; Liu, Hongxi; Wen, Shuiping; Tan, Shaozao; Wu, Ting

2015-08-01

To improve the antibacterial activity of Cu(2+), a series of Cu(2+) and/or Nd(3+)-modified layered α-zirconium phosphate (ZrP) was prepared and characterized, and the antibacterial activities of the prepared Cu(2+) and/or Nd(3+)-modified ZrP on Gram-negative Escherichia coli were investigated. The results showed that the basal spacing of ZrP was not obviously affected by the incorporation of Cu(2+), but the basal spacing of the modified ZrP changed into an amorphous state with increasing additions of Nd(3+). An antibacterial mechanism showed that Cu(2+) and Nd(3+) could enter into E. coli cells, leading to changes in ion concentrations and leakage of DNA, RNA and protein. The Cu(2+)- and Nd(3+)-modified ZrP, combining the advantages of Cu(2+) and Nd(3+), displayed excellent additive antibacterial activity and lower cytotoxicity, suggesting the great potential application as an antibacterial powder for microbial control. Crown Copyright © 2015. Published by Elsevier B.V. All rights reserved.

Synthesis and nonstoichiometry of the zirconium trihalides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Daake, R.L.; Corbett, J.D.

1978-05-01

The synthesis of ZrX/sub 3/ (X = Cl, Br, I) by reaction of the corresponding tetrahalides with ZrCl, ZrBr, or ZrI/sub 1.8/ in sealed tantalum tubing gives high-purity, single-phase products, thereby avoiding problems of the relatively low reactivity of and contamination by zirconium powder reductant used previously. Phase limits for the three trihalides established by isopiestic equilibration with the adjoining phases are 2.94 (2) less than or equal to Cl:Zr less than or equal to 3.03 (2) (440/sup 0/C), 2.87 (2) less than or equal to Br:Zr less than or equal to 3.23 (2) (435/sup 0/C), and 2.83 (5) (775/supmore » 0/C) less than or equal to I:Zr less than or equal to 3.43 (5) (475/sup 0/C). The hexagonal lattice constants for the bromide phase (Guinier techniques) decrease linearly with increasing bromide content across the entire range without the development of any additional lines. The variation of the c dimension for ZrI/sub 3/ (and HfI/sub 3/) on oxidation is in the opposite direction, and in this case extra lines from a presumed superlattice structure developed toward the upper limit. The structural implications of these results are considered. The reported structure for ..cap alpha..-ZrCl/sub 3/, an unusual BiI/sub 3/-type variant, was based on a misassigned ZrCl powder pattern and therefore appears to be in error. 25 references.« less

Structure of zirconium-93 and zirconium-91 as shown by the reactions Zr-92(d,p)Zr-93 and Zr-92(d,t)Zr-91

NASA Technical Reports Server (NTRS)

Baron, N.; Leonard, R. F.; Stewart, W. M.; Fink, C. L.; Christensen, P. R.; Nickles, J.; Thorsteinsen, T. F.

1972-01-01

Deuterons of 13-MeV incident energy were scattered from Zr-92(d,p)Zr-93. The Zr-92(d,p)Zr-93 data analysis resulted in the location of 47 levels up to an excitation energy of 4.84 MeV, and the spins of 43 of these levels were identified. Essentially all the strength of the 2d5/2, 3s1/2, 2d3/2, and 1g7/2 shells was observed; and the excitation energy of their centroids was computed to be 0.00, 1.21, 2.23, and 2.37 MeV, respectively. Also, 43 percent of the 1h11/2 strength, 21 percent of the 2f7/2 strength, and 3 percent of the 3p3/2 strength were observed. In addition, the Zr-92(d,t)Zr-91 data analysis resulted in the location of 26 levels up to an excitation energy of 4.01 MeV, and the spins of 21 of these levels were identified. Most of the expected strength of the 2d5/2 and 1g9/2 shells was obtained, and the excitation energy of their centroids was computed to be 0.31 and 3.19 MeV, respectively. In addition, six l=1 states are populated belonging to either the 2p1/2 or 2p3/2 shells.

Evaluation of steam corrosion and water quenching behavior of zirconium-silicide coated LWR fuel claddings

NASA Astrophysics Data System (ADS)

Yeom, Hwasung; Lockhart, Cody; Mariani, Robert; Xu, Peng; Corradini, Michael; Sridharan, Kumar

2018-02-01

This study investigates steam corrosion of bulk ZrSi2, pure Si, and zirconium-silicide coatings as well as water quenching behavior of ZrSi2 coatings to evaluate its feasibility as a potential accident-tolerant fuel cladding coating material in light water nuclear reactor. The ZrSi2 coating and Zr2Si-ZrSi2 coating were deposited on Zircaloy-4 flats, SiC flats, and cylindrical Zircaloy-4 rodlets using magnetron sputter deposition. Bulk ZrSi2 and pure Si samples showed weight loss after the corrosion test in pure steam at 400 °C and 10.3 MPa for 72 h. Silicon depletion on the ZrSi2 surface during the steam test was related to the surface recession observed in the silicon samples. ZrSi2 coating (∼3.9 μm) pre-oxidized in 700 °C air prevented substrate oxidation but thin porous ZrO2 formed on the coating. The only condition which achieved complete silicon immobilization in the oxide scale in aqueous environments was the formation of ZrSiO4 via ZrSi2 coating oxidation in 1400 °C air. In addition, ZrSi2 coatings were beneficial in enhancing quenching heat transfer - the minimum film boiling temperature increased by 6-8% in the three different environmental conditions tested. During repeated thermal cycles (water quenching from 700 °C to 85 °C for 20 s) performed as a part of quench tests, no spallation and cracking was observed and the coating prevented oxidation of the underlying Zircaloy-4 substrate.

Structural, mechanical, electrical and wetting properties of ZrNx films deposited by Ar/N2 vacuum arc discharge: Effect of nitrogen partial pressure

NASA Astrophysics Data System (ADS)

Abdallah, B.; Naddaf, M.; A-Kharroub, M.

2013-03-01

Non-stiochiometric zirconium nitride (ZrNx) thin films have been deposited on silicon substrates by vacuum arc discharge of (N2 + Ar) gas mixtures at different N2 partial pressure ratio. The microstructure, mechanical, electrical and wetting properties of these films are studied by means of X-ray diffraction (XRD), micro-Raman spectroscopy, Rutherford back scattering (RBS) technique, conventional micro-hardness testing, electrical resistivity, atomic force microscopy (AFM) and contact angle (CA) measurements. RBS results and analysis show that the (N/Zr) ratio in the film increases with increasing the N2 partial pressure. A ZrNx film with (Zr/N) ratio in the vicinity of stoichiometric ZrN is obtained at N2 partial pressure of 10%. XRD and Raman results indicate that all deposited films have strained cubic crystal phase of ZrN, regardless of the N2 partial pressure. On increasing the N2 partial pressure, the relative intensity of (1 1 1) orientation with respect to (2 0 0) orientation is seen to decrease. The effect of N2 partial pressure on micro-hardness and the resistivity of the deposited film is revealed and correlated to the alteration of grain size, crystallographic texture, stoichiometry and residual stress developed in the film. In particular, it is found that residual stress and nitrogen incorporation in the film play crucial role in the alteration of micro-hardness and resistivity respectively. In addition, CA and AFM results demonstrate that as N2 partial pressure increases, both the surface hydrophobicity and roughness of the deposited film increase, leading to a significant decrease in the film surface free energy (SFE).

Zirconium oxide surface passivation of crystalline silicon

NASA Astrophysics Data System (ADS)

Wan, Yimao; Bullock, James; Hettick, Mark; Xu, Zhaoran; Yan, Di; Peng, Jun; Javey, Ali; Cuevas, Andres

2018-05-01

This letter reports effective passivation of crystalline silicon (c-Si) surfaces by thermal atomic layer deposited zirconium oxide (ZrOx). The optimum layer thickness and activation annealing conditions are determined to be 20 nm and 300 °C for 20 min. Cross-sectional transmission electron microscopy imaging shows an approximately 1.6 nm thick SiOx interfacial layer underneath an 18 nm ZrOx layer, consistent with ellipsometry measurements (˜20 nm). Capacitance-voltage measurements show that the annealed ZrOx film features a low interface defect density of 1.0 × 1011 cm-2 eV-1 and a low negative film charge density of -6 × 1010 cm-2. Effective lifetimes of 673 μs and 1.1 ms are achieved on p-type and n-type 1 Ω cm undiffused c-Si wafers, respectively, corresponding to an implied open circuit voltage above 720 mV in both cases. The results demonstrate that surface passivation quality provided by ALD ZrOx is consistent with the requirements of high efficiency silicon solar cells.

High pressure phase-transformation induced texture evolution and strengthening in zirconium metal: Experiment and modeling

DOE PAGES

Yu, Xiaohui; Zhang, Ruifeng; Weldon, David; ...

2015-07-28

We studied the phase-transition induced texture changes and strengthening mechanism for zirconium metal under quasi-hydrostatic compression and uni-axial deformation under confined high pressure using the deformation-DIA (D-DIA) apparatus. It is shown that the experimentally obtained texture for ω-phase Zr can be qualitatively described by combining a subset of orientation variants previously proposed in two different models. The determined flow stress for the high-pressure ω-phase is 0.5–1.2 GPa, more than three times higher than that of the α-phase. Using first-principles calculations, we investigated the mechanical and electronic properties of the two Zr polymorphs. We find that the observed strengthening can bemore » attributed to the relatively strong directional bonding in the ω phase, which significantly increases its shear plastic resistance over the α-phase Zr. The present findings provide an alternate route for Zr metal strengthening by high-pressure phase transformation.« less

Synthesis and Characterization of Zirconium Substituted Cobalt Ferrite Nanopowders

DOE PAGES

Rus, S. F.; Vlazan, P.; Herklotz, A.

2016-01-01

Nanocrystalline ferrites; CoFe 2O 4 (CFO) and CoFe 1.9Zr 0.1O 4 (CFZO) have been synthesized through chemical coprecipitation method. Moreover, the role played by the zirconium ions in improving the magnetic and structural properties is analyzed. X-ray diffraction revealed a single-phase cubic spinel structure for both materials, where the crystallite size increases and the lattice parameter decreases with substitution of Zr. The average sizes of the nanoparticles are estimated to be 16-19 nm. These sizes are small enough to achieve the suitable signal to noise ratio in the high density recording media. An increase in the saturation magnetization with themore » substitution of Zr suggests the preferential occupation of Zr 4+ ions in the tetrahedral sites. A decrease in the coercivity values indicates the reduction of magneto-crystalline anisotropy. We investigated spinel ferrites can be used also in recoding media due to the large value of coercivity 1000 Oe which is comparable to those of hard magnetic materials.« less

Porosity and mechanical properties of zirconium ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Buyakova, S., E-mail: sbuyakova@ispms.tsc.ru; Kulkov, S.; Tomsk Polytechnic University

2015-11-17

Has been studied a porous ceramics obtained from ultra-fine powders. Porous ceramic ZrO{sub 2}(MgO), ZrO{sub 2}(Y{sub 2}O{sub 3}) powder was prepared by pressing and subsequent sintering of compacts homologous temperatures ranging from 0.63 to 0.56 during the isothermal holding duration of 1 to 5 hours. The porosity of ceramic samples was from 15 to 80%. The structure of the ceramic materials produced from plasma-sprayed ZrO{sub 2} powder was represented as a system of cell and rod structure elements. Cellular structure formed by stacking hollow powder particles can be easily seen at the images of fracture surfaces of obtained ceramics. Theremore » were three types of pores in ceramics: large cellular hollow spaces, small interparticle pores which are not filled with powder particles and the smallest pores in the shells of cells. The cells generally did not have regular shapes. The size of the interior of the cells many times exceeded the thickness of the walls which was a single-layer packing of ZrO{sub 2} grains. A distinctive feature of all deformation diagrams obtained in the experiment was their nonlinearity at low deformations which was described by the parabolic law. It was shown that the observed nonlinear elasticity for low deformation on deformation diagrams is due to mechanical instability of the cellular elements in the ceramic carcass.« less

Geologic structure of Gofitsky deposit of titanium and zirconium and perspectives of the reserve base of titanium and zirconium in Russia

NASA Astrophysics Data System (ADS)

Kukhmazov, Iskander

2016-04-01

With the fall of the Soviet Union, all the mining deposits of titanium and zirconium appeared outside of Russian Federation. Therefore the studying of deposits of titanium and zirconium in Russia is very important nowadays. There is a paradoxical situation in the country: in spite of possible existence of national mineral resource base of Ti-Zr material, which can cover needs of the country, Russia is the one of the largest buyers of imported Ti-Zr material in the world. Many deposits are not mined, and those which are in the process of mining have poor reserves. Demand for this raw material is very great not only for Russia, but also for the world in general. Today there is a scarcity of zircon around the world and it will only increase through time. Therefore prices of products of titanium and zirconium also increase. Consequently Russian deposits of titanium and zirconium with higher content than foreign may become competitive. Russia is forced to buy raw materials (zirconium and titanium production) from former Soviet Union countries at prices higher than the world's and thus incur huge losses, including customs charges. Russia should create its own mineral resource base of Ti-Zr. Studied titanium-zirconium deposits of Stavropol region may become the basis for the south part of Russia. At first, Beshpagirsky deposit should be pointed out. It has large reserves of ore sands with high content of Ti-Zr. A combination of favorable geographical position of the area with developed industrial infrastructure makes it very beneficial as an object for high priority development. Gofitsky deposit should be pointed out as well. Its sands have a wide areal distribution and a high content of titanium and zirconium. Chokrak, Karagan-Konksk and Sarmatian sediments of the Miocene of Gofitsky deposit are productive for titanium and zirconium placers within Stavropol region of Russia. Gofitsky deposit was evaluated from financial and economic point of view and the following data were received (USGS, 2005): 1. The draft forecasts the highest positive net present value (NPV= 1712879.6 thou.) to a company that uses a discount rate of 15%. 2. The present value factor is quite high (PVR = 9.02), and means that the company will receive 9.02 discounted profit per dollar invested. Profitability index is higher than 1 (PI = 1.3) and indicates that the project is profitable, but it is volatile in term of investment. All these features make the project highly controversial for a company, but with an increase of price of titanium and zirconium raw materials it will improve the attractiveness of Gofitsky deposit for development. As a result: • common patterns of geological structure of Gofitsky deposit field are determined • mineral composition is studied • schlich analysis is held • Gofitsky deposit was evaluated from the financial and economic point of view • profitability was identified and its attractiveness was estimated for potential investors.

Optimized anion exchange column isolation of zirconium-89 ( 89Zr) from yttrium cyclotron target: Method development and implementation on an automated fluidic platform

DOE Office of Scientific and Technical Information (OSTI.GOV)

O’Hara, Matthew J.; Murray, Nathaniel J.; Carter, Jennifer C.

Zirconium-89 ( 89Zr), produced by the (p, n) reaction from naturally monoisotopic yttrium ( natY), is a promising positron emitting isotope for immunoPET imaging. Its long half-life of 78.4 h is sufficient for evaluating slow physiological processes. A prototype automated fluidic system, coupled to on-line and in-line detectors, has been constructed to facilitate development of new 89Zr purification methodologies. The highly reproducible reagent delivery platform and near-real time monitoring of column effluents allows for efficient method optimization. The separation of Zr from dissolved Y metal targets was evaluated using several anion exchange resins. Each resin was evaluated against its abilitymore » to quantitatively capture Zr from a load solution high in dissolved Y. The most appropriate anion exchange resin for this application was identified, and the separation method was optimized. The method is capable of a high Y decontamination factor (>10 5) and has been shown to remove Fe, an abundant contaminant in Y foils, from the 89Zr elution fraction. Finally, the method was evaluated using cyclotron bombarded Y foil targets; the method was shown to achieve >95% recovery of the 89Zr present in the foils. The anion exchange column method described here is intended to be the first 89Zr isolation stage in a dual-column purification process.« less

Optimized anion exchange column isolation of zirconium-89 ( 89Zr) from yttrium cyclotron target: Method development and implementation on an automated fluidic platform

DOE PAGES

O’Hara, Matthew J.; Murray, Nathaniel J.; Carter, Jennifer C.; ...

2018-02-24

Zirconium-89 ( 89Zr), produced by the (p, n) reaction from naturally monoisotopic yttrium ( natY), is a promising positron emitting isotope for immunoPET imaging. Its long half-life of 78.4 h is sufficient for evaluating slow physiological processes. A prototype automated fluidic system, coupled to on-line and in-line detectors, has been constructed to facilitate development of new 89Zr purification methodologies. The highly reproducible reagent delivery platform and near-real time monitoring of column effluents allows for efficient method optimization. The separation of Zr from dissolved Y metal targets was evaluated using several anion exchange resins. Each resin was evaluated against its abilitymore » to quantitatively capture Zr from a load solution high in dissolved Y. The most appropriate anion exchange resin for this application was identified, and the separation method was optimized. The method is capable of a high Y decontamination factor (>10 5) and has been shown to remove Fe, an abundant contaminant in Y foils, from the 89Zr elution fraction. Finally, the method was evaluated using cyclotron bombarded Y foil targets; the method was shown to achieve >95% recovery of the 89Zr present in the foils. The anion exchange column method described here is intended to be the first 89Zr isolation stage in a dual-column purification process.« less

Hydroxyaptite nanorods patterned ZrO2 bilayer coating on zirconium for the application of percutaneous implants.

PubMed

Zhang, Lan; Han, Yong; Tan, Guoxin

2015-03-01

Percutaneous implant requires a tight bond between the underlying dermis of skin and implant surface to prevent epithelial down-growth and infection, while fibroblasts play a key role in the skin-implant integration. In this work, nanorod-shaped hydroxyaptite (HA) with a mean diameter of 70 nm and length of 400 nm was hydrothermally grown on micro-arc oxidized (MAOed) Ca- and P-doped ZrO2 to form a bilayer coating. The hydrothermal formation mechanism of HA nanorods was explored, and the adsorption of total protein on the coating from α-MEM medium containing 10% fetal bovine serum was examined. Employing L-929 cells, the behaviors of fibroblasts on the bilayer coating, including adhesion and proliferation were evaluated together the polished Zr and as-MAOed ZrO2. The obtained results show that the HA nanorods nucleated on ZrO2 and grew at the expense of the doped Ca and P ions during the hydrothermal treatment (HT). The HA nanorods patterned coating enhanced protein absorption, and significantly improved the adhesion and proliferation of fibroblasts compared to the as-MAOed ZrO2 and polished Zr. It suggests that the HA nanorods/ZrO2 coated zirconium has a potential application for percutaneous implants to enhance the attachment of skin. Copyright © 2015 Elsevier B.V. All rights reserved.

Impedance spectroscopy of water soluble resin modified by zirconium sulphate

NASA Astrophysics Data System (ADS)

Joseph, Anandraj; Joshi, Girish M.

2018-04-01

We successfully modified water soluble resin polyvinyl alcohol (PVA) by loading zirconium sulphate (ZrSO4). We demonstrated the measurement of electrical properties by using impedance analyser across frequency range (10 Hz-1 MHz) and the temperature range of (30°C to 150°C). The impedance spectroscopy demonstrates decrease in bulk resistance as a function of temperature loading of zirconia 2.5 wt. %. Increase in AC (10-5 S/cm and DC conductivity (10- 2 S/m) observed due to ionic contribution of zirconia. However, the electrical properties of PVA/ZrSO4 composite useful to develop battery electrolyte applications.

Feasibility of processing the experimental breeder reactor-II driver fuel from the Idaho National Laboratory through Savannah River Site's H-Canyon facility

DOE Office of Scientific and Technical Information (OSTI.GOV)

Magoulas, V. E.

Savannah River National Laboratory (SRNL) was requested to evaluate the potential to receive and process the Idaho National Laboratory (INL) uranium (U) recovered from the Experimental Breeder Reactor II (EBR-II) driver fuel through the Savannah River Site’s (SRS) H-Canyon as a way to disposition the material. INL recovers the uranium from the sodium bonded metallic fuel irradiated in the EBR-II reactor using an electrorefining process. There were two compositions of EBR-II driver fuel. The early generation fuel was U-5Fs, which consisted of 95% U metal alloyed with 5% noble metal elements “fissium” (2.5% molybdenum, 2.0% ruthenium, 0.3% rhodium, 0.1% palladium,more » and 0.1% zirconium), while the later generation was U-10Zr which was 90% U metal alloyed with 10% zirconium. A potential concern during the H-Canyon nitric acid dissolution process of the U metal containing zirconium (Zr) is the explosive behavior that has been reported for alloys of these materials. For this reason, this evaluation was focused on the ability to process the lower Zr content materials, the U-5Fs material.« less

Thermomechanical properties of zirconium tungstate/hydrogenated nitrile butadiene rubber (HNBR) composites for low-temperature applications

NASA Astrophysics Data System (ADS)

Akulichev, Anton G.; Alcock, Ben; Tiwari, Avinash; Echtermeyer, Andreas T.

2016-12-01

Rubber compounds for pressure sealing application typically have inferior dimensional stability with temperature fluctuations compared with their steel counterparts. This effect may result in seal leakage failures when subjected to decreases in temperature. Composites of hydrogenated nitrile butadiene rubber (HNBR) and zirconium tungstate as a negative thermal expansion filler were prepared in order to control the thermal expansivity of the material. The amount of zirconium tungstate (ZrW2O8) was varied in the range of 0 to about 40 vol%. The coefficient of thermal expansion (CTE), bulk modulus, uniaxial extension and compression set properties were measured. The CTE of the ZrW2O8-filled HNBR decreases with the filler content and it is reduced by a factor of 2 at the highest filler concentration used. The filler effect on CTE is found to be stronger when HNBR is below the glass transition temperature. The experimental thermal expansion data of the composites are compared with the theoretical estimates and predictions given by FEA. The effect of ZrW2O8 on the mechanical characteristics and compression set of these materials is also discussed.

Fractionation of Zr and Hf during the differentiation of peralkaline magmatic system (Lovozero rare metal deposit, Kola Peninsula)

NASA Astrophysics Data System (ADS)

Kogarko, Liya

2016-04-01

Zirconium and hafnium are valuable strategic metals. We assessed principal features of the distribution of these elements in peralkaline rocks, ores and rock-forming and accessory minerals of Lovozero complex. The accumulation of these elements during the evolution of alkaline magma of Lovozero deposit up to extremely high concentrations in eudialyte ores (5-8% ZrO2 and 1200-1800 ppm Hf) has been established. These ores represent valuable complex raw material not only for Zr and Hf, but for REE as well. We evaluated partition coefficients of these elements in alkaline pyroxenes (aegirines) from porphyry-like agpaitic lujavrites of Lovozero massif which are 0.40 for zirconium and 0.58 for hafnium. We assessed variations of Zr/Hf ratio for all the rocks of Lovozero alkaline massif. The growth of this ratio in the course of the evolution of alkaline magma has been observed from 38 in the earliest magmatic phase, to 44 in the second phase and to 51-53 in the latest manifestation of alkaline magmatsm. On the basis of the obtained data and equations of equilibrium and fractional crystallization the model of the fractionation of zirconium and hafnium during the evolution of Lovozero intrusion has been constructed. We have demonstrated that the source of strongly enriched magmatic systems similar to Lovozero rare metal deposit is short-lived enriched reservoir - metasomatized and carbonatized mantle substrate. We investigated the fractionation of zirconium and hafnium in carbonatized mantle xenoliths from East Antarctica. The elevated Zr/Hf ratios (up to 125) in metasomatized xenoliths by comparison with the chondritic value have been found. The main reactions of carbonate metasomatism lead to the replacement of primary orthopyroxene by clinopyroxene 2Mg2Si2O6 + CaMg(CO3)2 = 2Mg2SiO4 + CaMgSi2O6 + 2CO2 3CaMg(CO3)2 + CaMgSi2O6 = 4CaCO3 + 2Mg2SiO4 + 2CO2 The substantial expansion of the clinopyroxene crystallization field results in increase of Zr/Hf ratio in equilibrium melt due to the higher value of Hf partition coefficient by comparison with Zr. The migration of active carbonate and carbonate-silicate melts equilibrated with the metasomatic wehrlites leads to the increase in Zr/Hf ratio in carbonatized mantle substrate. This work has been financially supported by the grant 15-17-30019 of the Russian Science Foundation.

Coordination behavior of bis-phenolate saturated and unsaturated N-heterocyclic carbene ligands to zirconium: reactivity and activity in the copolymerization of cyclohexene oxide with CO2.

PubMed

Lalrempuia, Ralte; Breivik, Frida; Törnroos, Karl W; Le Roux, Erwan

2017-06-27

Tetravalent zirconium complexes supported by tridentate bis-phenolate imidazolidin-2-ylidene (L1), imidazol-2-ylidene (L2) and benzimidazol-2-ylidene (L3) NHC ligands were synthesized and evaluated as precursors for the copolymerization of cyclohexene oxide (CHO) with CO 2 . While the reactivity of the imidazolidinium [H 3 L1] chloride salt with Zr(OiPr) 4 (HOiPr), and subsequent ligand exchanges with either (CH 3 ) 3 SiCl or LiOiPr lead to a series of heteroleptic compounds (κ 3 -O,C,O-L1)Zr(X) 2 (THF) (X = Cl, OiPr), both imidazolium [H 3 L2] and benzimidazolium [H 3 L3] chloride salts give a mixture of homoleptic (κ 3 -O,C,O-NHC) 2 Zr and zwitterionic (κ 2 -O,O-HL)ZrCl 2 (OiPr) compounds along with traces or the absence of the heteroleptic intermediate (κ 3 -O,C,O-NHC)Zr(Cl)(OiPr)(THF). Such dissimilar reactivity between the unsaturated and saturated NHC ligands is predominantly ascribed to the increased acidity of azolium salts along with the π-donor strength of the C carbene in L2 and L3-Zr moieties. The reactivity with the more acidic azolium salts (H 3 L2/3) and the destabilized Zr-X trans to NHC carbene bond results in a significant increase in the amount of homoleptic compounds generating HCl. The released HCl reacts preferentially with the heteroleptic intermediates having non-planar NHC ligands (i.e. L2/3) promoting the formation of zwitterionic complexes. The in situ deprotonation of the isolated zwitterionic (κ 2 -O,O-HL3)ZrCl 2 (OiPr) compound by using Ag 2 O gives the homoleptic complex as the major component along with a bimetallic hydroxo-bridged [(κ 3 -O,C,O-L3)Zr(μ-OH)(OiPr)] 2 compound. Of particular interest is that only the heteroleptic NHC-Zr(iv) complexes were identified to be active and highly selective towards the copolymerization of CHO with CO 2 independently of the co-catalysts used (both anionic and neutral) under mild conditions (P CO 2 < 1 bar, T = 60 °C), and gave atactic and completely alternating copolymers in a controlled manner (M w /M n ≈ 1.3-1.8). In contrast, the isolated homoleptic, zwitterionic and bimetallic zirconium species were found to be inactive under similar reaction conditions. Although the activity found for NHC-Zr(iv) complexes is nearly of the same order of magnitude as that of the NHC-Ti(iv) analogues, these results are the first examples of tetravalent zirconium complexes achieving high selectivity (99% in PCHC) in the catalyzed copolymerization of CHO with CO 2 .

Densification and Thermal Properties of Zirconium Diboride Based Ceramics

DTIC Science & Technology

2012-01-01

pulse on the front face and the radiant energy going to an infrared detector on the back face of the specimen...changes going across a row of the periodic table (e.g., Zr, Nb, Mo…) because of the filling of bonding and anti-bonding states in the hybrid orbitals...the relatively small amounts of ZrC (i.e., ə wt%) likely to go into solid solution with the ZrB2, based on the Zr-B-C phase diagram.6 (2

Effects of grain refinement on the biocorrosion and in vitro bioactivity of magnesium.

PubMed

Saha, Partha; Roy, Mangal; Datta, Moni Kanchan; Lee, Boeun; Kumta, Prashant N

2015-12-01

Magnesium is a new class of biodegradable metals potentially suitable for bone fracture fixation due to its suitable mechanical properties, high degradability and biocompatibility. However, rapid corrosion and loss in mechanical strength under physiological conditions render it unsuitable for load-bearing applications. In the present study, grain refinement was implemented to control bio-corrosion demonstrating improved in vitro bioactivity of magnesium. Pure commercial magnesium was grain refined using different amounts of zirconium (0.25 and 1.0 wt.%). Corrosion behavior was studied by potentiodynamic polarization (PDP) and mass loss immersion tests demonstrating corrosion rate decrease with grain size reduction. In vitro biocompatibility tests conducted by MC3T3-E1 pre-osteoblast cells and measured by DNA quantification demonstrate significant increase in cell proliferation for Mg-1 wt.% Zr at day 5. Similarly, alkaline phosphatase (ALP) activity was higher for grain refined Mg. Alloys were also tested for ability to support osteoclast differentiation using RAW264.7 monocytes with receptor activator of nuclear factor kappa-β ligand (RANKL) supplemented cell culture. Osteoclast differentiation process was observed to be severely restricted for smaller grained Mg. Overall, the results indicate grain refinement to be useful not only for improving corrosion resistance of Mg implants for bone fixation devices but also potentially modulate bone regeneration around the implant. Copyright © 2015 Elsevier B.V. All rights reserved.

Chitosan /Zeolite Y/Nano ZrO2 nanocomposite as an adsorbent for the removal of nitrate from the aqueous solution.

PubMed

Teimouri, Abbas; Nasab, Shima Ghanavati; Vahdatpoor, Niaz; Habibollahi, Saeed; Salavati, Hossein; Chermahini, Alireza Najafi

2016-12-01

In the present study, a series of chitosan/Zeolite Y/Nano Zirconium oxide (CTS/ZY/Nano ZrO 2 ) nanocomposites were made by controlling the molar ratio of chitosan (CTS) to Zeolite Y/Nano Zirconium oxide in order to remove nitrate (NO 3 - ) ions in the aqueous solution. The nanocomposite adsorbents were characterized by XRD, FTIR, BET, SEM and TEM. The influence of different molar ratios of CTS to ZY/Nano ZrO 2 , the initial pH value of the nitrate solution, contact time, temperature, the initial concentration of nitrate and adsorbent dose was studied. The adsorption isotherms and kinetics were also analyzed. It was attempted to describe the sorption processes by the Langmuir equation and the theoretical adsorption capacity (Q 0 ) was found to be 23.58mg nitrate per g of the adsorbent. The optimal conditions for nitrate removal were found to be: molar ratio of CTS/ZY/Nano ZrO 2 : 5:1; pH: 3; 0.02g of adsorbent and temperature: 35°C, for 60min. The adsorption capacities of CTS, ZY, Nano ZrO 2 , CTS/Nano ZrO 2 , CTS/ZY and CTS/ZY/Nano ZrO 2 nanocomposites for nitrate removal were compared, showing that the adsorption ability of CTS/ZY/Nano ZrO 2 nanocomposite was higher than the average values of those of CTS (1.95mg/g for nitrate removal), ZY, Nano ZrO 2 , CTS/Nano ZrO 2, and CTS/ZY. Copyright © 2016. Published by Elsevier B.V.

Atomistic modeling of high temperature uranium-zirconium alloy structure and thermodynamics

NASA Astrophysics Data System (ADS)

Moore, A. P.; Beeler, B.; Deo, C.; Baskes, M. I.; Okuniewski, M. A.

2015-12-01

A semi-empirical Modified Embedded Atom Method (MEAM) potential is developed for application to the high temperature body-centered-cubic uranium-zirconium alloy (γ-U-Zr) phase and employed with molecular dynamics (MD) simulations to investigate the high temperature thermo-physical properties of U-Zr alloys. Uranium-rich U-Zr alloys (e.g. U-10Zr) have been tested and qualified for use as metallic nuclear fuel in U.S. fast reactors such as the Integral Fast Reactor and the Experimental Breeder Reactors, and are a common sub-system of ternary metallic alloys like U-Pu-Zr and U-Zr-Nb. The potential was constructed to ensure that basic properties (e.g., elastic constants, bulk modulus, and formation energies) were in agreement with first principles calculations and experimental results. After which, slight adjustments were made to the potential to fit the known thermal properties and thermodynamics of the system. The potentials successfully reproduce the experimental melting point, enthalpy of fusion, volume change upon melting, thermal expansion, and the heat capacity of pure U and Zr. Simulations of the U-Zr system are found to be in good agreement with experimental thermal expansion values, Vegard's law for the lattice constants, and the experimental enthalpy of mixing. This is the first simulation to reproduce the experimental thermodynamics of the high temperature γ-U-Zr metallic alloy system. The MEAM potential is then used to explore thermodynamics properties of the high temperature U-Zr system including the constant volume heat capacity, isothermal compressibility, adiabatic index, and the Grüneisen parameters.

Articulation of Native Cartilage Against Different Femoral Component Materials. Oxidized Zirconium Damages Cartilage Less Than Cobalt-Chrome.

PubMed

Vanlommel, Jan; De Corte, Ronny; Luyckx, Jean Philippe; Anderson, Melissa; Labey, Luc; Bellemans, Johan

2017-01-01

Oxidized zirconium (OxZr) is produced by thermally driven oxidization creating an oxidized surface with the properties of a ceramic at the top of the Zr metal substrate. OxZr is much harder and has a lower coefficient of friction than cobalt-chrome (CoCr), both leading to better wear characteristics. We evaluated and compared damage to the cartilage of porcine patella plugs, articulating against OxZr vs CoCr. Our hypothesis was that, owing to its better wear properties, OxZr would damage cartilage less than CoCr. If this is true, OxZr might be a better material for the femoral component during total knee arthroplasty if the patella is not resurfaced. Twenty-one plugs from porcine patellae were prepared and tested in a reciprocating pin-on-disk machine while lubricated with bovine serum and under a constant load. Three different configurations were tested: cartilage-cartilage as the control group, cartilage-OxZr, and cartilage-CoCr. Macroscopic appearance, cartilage thickness, and the modified Mankin score were evaluated after 400,000 wear cycles. The control group showed statistically significant less damage than plugs articulating against both other materials. Cartilage plugs articulating against OxZr were statistically significantly less damaged than those articulating against CoCr. Although replacing cartilage by an implant always leads to deterioration of the cartilage counterface, OxZr results in less damage than CoCr. The use of OxZr might thus be preferable to CoCr in case of total knee arthroplasty without patella resurfacing. Copyright © 2016 Elsevier Inc. All rights reserved.

Zirconium tungstate/epoxy nanocomposites: effect of nanoparticle morphology and negative thermal expansivity.

PubMed

Wu, Hongchao; Rogalski, Mark; Kessler, Michael R

2013-10-09

The ability to tailor the coefficient of thermal expansion (CTE) of a polymer is essential for mitigating thermal residual stress and reducing microcracks caused by CTE mismatch of different components in electronic applications. This work studies the effect of morphology and thermal expansivity of zirconium tungstate nanoparticles on the rheological, thermo-mechanical, dynamic-mechanical, and dielectric properties of ZrW2O8/epoxy nanocomposites. Three types of ZrW2O8 nanoparticles were synthesized under different hydrothermal conditions and their distinct properties were characterized, including morphology, particle size, aspect ratio, surface area, and CTE. Nanoparticles with a smaller particle size and larger surface area led to a more significant reduction in gel-time and glass transition temperature of the epoxy nanocomposites, while a higher initial viscosity and significant shear thinning behavior was found in prepolymer suspensions containing ZrW2O8 with larger particle sizes and aspect ratios. The thermo- and dynamic-mechanical properties of epoxy-based nanocomposites improved with increasing loadings of the three types of ZrW2O8 nanoparticles. In addition, the introduced ZrW2O8 nanoparticles did not negatively affect the dielectric constant or the breakdown strength of the epoxy resin, suggesting potential applications of ZrW2O8/epoxy nanocomposites in the microelectronic insulation industry.

Production of Ethylene through Ethanol Dehydration on SBA-15 Catalysts Synthesized by Sol-gel and One-step Hydrothermal Methods.

PubMed

Autthanit, Chaowat; Jongsomjit, Bunjerd

2018-02-01

The present work deals with the catalytic performance of SBA-15 supported catalysts in the gas phase catalytic dehydration of ethanol in the temperature range of 200 to 400°C. The SBA-15 support was incorporated on a zirconium (Zr) and bimetal of zirconium and lanthanum (Zr-La) prepared by sol-gel (SG) and hydrothermal (HT) methods. The catalysts were characterized by means of N 2 physisorption, SEM/EDX, and NH 3 -TPD. The experimental results demonstrated that the Zr-La/SBA-15-HT exhibited the highest catalytic activity. Ethanol conversion and ethylene selectivity were found to increase with increased reaction temperature. The best catalytic results were achieved for Zr-La/SBA-15-HT indicating values of ethanol conversion and ethylene yield of ca. 84% and 80%, respectively at 400°C. The most important parameter influencing their catalytic properties appears to be the interaction between metal and support depending on different methods. The metal dispersion inside the siliceous matrix of SBA-15 has a direct influence on their surface acidity. Meanwhile, the performance of these SBA-15 supported catalysts in ethanol dehydration is also related with the alteration of surface acidity caused by the introduction of Zr and Zr-La.

Zirconium oxide nanotube-Nafion composite as high performance membrane for all vanadium redox flow battery

NASA Astrophysics Data System (ADS)

Aziz, Md. Abdul; Shanmugam, Sangaraju

2017-01-01

A high-performance composite membrane for vanadium redox flow battery (VRB) consisting of ZrO2 nanotubes (ZrNT) and perfluorosulfonic acid (Nafion) was fabricated. The VRB operated with a composite (Nafion-ZrNT) membrane showed the improved ion-selectivity (ratio of proton conductivity to permeability), low self-discharge rate, high discharge capacity and high energy efficiency in comparison with a pristine commercial Nafion-117 membrane. The incorporation of zirconium oxide nanotubes in the Nafion matrix exhibits high proton conductivity (95.2 mS cm-1) and high oxidative stability (99.9%). The Nafion-ZrNT composite membrane exhibited low vanadium ion permeability (3.2 × 10-9 cm2 min-1) and superior ion selectivity (2.95 × 107 S min cm-3). The VRB constructed with a Nafion-ZrNT composite membrane has lower self-discharge rate maintaining an open-circuit voltage of 1.3 V for 330 h relative to a pristine Nafion membrane (29 h). The discharge capacity of Nafion-ZrNT membrane (987 mAh) was 3.5-times higher than Nafion-117 membrane (280 mAh) after 100 charge-discharge cycles. These superior properties resulted in higher coulombic and voltage efficiencies with Nafion-ZrNT membranes compared to VRB with Nafion-117 membrane at a 40 mA cm-2 current density.

Preparation of magnetron sputtered ZrO2 films on Si for gate dielectric application

NASA Astrophysics Data System (ADS)

Kondaiah, P.; Mohan Rao, G.; Uthanna, S.

2012-11-01

Zirconium oxide (ZrO2) thin films were deposited on to p - Si and quartz substrates by sputtering of zirconium target at an oxygen partial pressure of 4x10-2 Pa and sputter pressure of 0.4 Pa by using DC reactive magnetron sputtering technique. The effect of annealing temperature on structural, optical, electrical and dielectric properties of the ZrO2 films was systematically studied. The as-deposited films were mixed phases of monoclinic and orthorhombic ZrO2. As the annealing temperature increased to 1073 K, the films were transformed in to single phase orthorhombic ZrO2. Fourier transform infrared studies conform the presence of interfacial layer between Si and ZrO2. The optical band gap and refractive index of the as-deposited films were 5.82 eV and 1.81. As the annealing temperature increased to 1073 K the optical band gap and refractive index increased to 5.92 eV and 2.10 respectively. The structural changes were influenced the capacitance-voltage and current-voltage characteristics of Al/ZrO2/p-Si capacitors. The dielectric constant was increased from 11.6 to 24.5 and the leakage current was decreased from 1.65×10-7 to 3.30×10-9 A/ cm2 for the as-deposited and annealed at 1073 K respectively.

Preliminary investigation of zirconium boride ceramals for gas-turbine blade applications

NASA Technical Reports Server (NTRS)

Hoffman, Charles A

1953-01-01

Zirconium boride ZrB2 ceramals were investigated for possible gas-turbine-blade application. Included in the study were thermal shock evaluations of disks, preliminary turbine-blade operation, and observations of oxidation resistance. Thermal shock disks of the following three compositions were studied: (a) 97.5 percent ZrB2 plus 2.5 percent B by weight; (b) 92.5 percent ZrB2 plus 7.5 percent B by weight; and (c) 100 percent ZrB2. Thermal shock disks were quenched from temperatures of 1800 degrees, 2000 degrees, 2200 degrees, and 2400 degrees F. The life of turbine blades containing 93 percent ZrB2 plus 7 percent B by weight was determined in gas-turbine tests. The blades were run at approximately 1600 degrees F and 15,000 to 26,000 rpm. The thermal shock resistance of the 97.5 percent ZrB2 plus 2.5 percent boron ceramals compares favorably with that of TiC plus Co and TiC plus Ni ceramals. Oxidation of the disks during the thermal shock evaluation was slight for the comparatively short time (8.3 hr) up through 2000 degrees F. Oxidation of a specimen was severe, however, after 100 hours at 2000 degrees F. The turbine blade performance evaluation of the 93 percent ZrB2 plus 7 percent B composition was preliminary in scope ; no conclusions can be drawn.

Dual functions of zirconium modification on improving the electrochemical performance of Ni-rich LiNi0.8Co0.1Mn0.1O2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Xing; Zhang, Kangjia; Wang, Mingshan

2018-02-28

Trace amount of Zirconium (Zr) has been adopted to modify the crystal structure and surface of the Ni-rich LiNi0.8Co0.1Mn0.1O2 (NCM811) cathode material. During cycling at 1.0C, the Zr-modified NCM811 shows an improved capacity retention of 92% after 100 cycles, higher than 75% for pristine NMC811. In addition, the Zr-modified NCM811 is capable of delivering a discharge capacity of 107 mAh g-1 at 10.0C rate, much higher than 28 mAh g-1 delivered by pristine material. These improved electrochemical performances are ascribed to the dual functions of Zr modification. On one hand, part of the Zr enters the crystal lattice, which ismore » beneficial for reducing the Li/Ni cation mixing and enhancing the crystal stability of the cathode. On the other hand, the rest of the Zr forms a 1~2 nm thick coating layer on the surface of the NCM811 cathode, which effectively prevents the direct contact between NCM and the electrolyte, thus suppressing the detrimental interfacial reactions. Therefore, the Zr-modified LiNi0.8Co0.1Mn0.1O2 exhibited significantly enhanced cycling stability and charging/discharging rate capability in comparison with the untreated counterpart.« less

Producing Zirconium Diboride Components with Complex, Near-Net Shape Geometries by Aqueous Room-Temperature Injection Molding

NASA Technical Reports Server (NTRS)

Wiesner, Valerie L.; Youngblood, Jeffrey; Trice, Rodney

2014-01-01

Room-temperature injection molding is proposed as a novel, low-cost and more energy efficient manufacturing process capable of forming complex-shaped zirconium diboride (ZrB2) parts. This innovative processing method utilized aqueous suspensions with high powder loading and a minimal amount (5 vol.) of water-soluble polyvinylpyrrolidone (PVP), which was used as a viscosity modifier. Rheological characterization was performed to evaluate the room-temperature flow properties of ZrB2-PVP suspensions. ZrB2 specimens were fabricated with high green body strength and were machinable prior to binder removal despite their low polymer content. After binder burnout and pressureless sintering, the bulk density and microstructure of specimens were characterized using Archimedes technique and scanning electron microscopy. X-Ray Diffraction was used to determine the phase compositions present in sintered specimens. Ultimate strength of sintered specimens will be determined using ASTM C1323-10 compressive C-ring test.

Corrosion evaluation of zirconium doped oxide coatings on aluminum formed by plasma electrolytic oxidation.

PubMed

Bajat, Jelena; Mišković-Stanković, Vesna; Vasilić, Rastko; Stojadinović, Stevan

2014-01-01

The plasma electrolytic oxidation (PEO) of aluminum in sodium tungstate (Na(2)WO(4) · (2)H(2)O) and Na(2)WO(4) · (2)H(2)O doped with Zr was analyzed in order to obtain oxide coatings with improved corrosion resistance. The influence of current density in PEO process and anodization time was investigated, as well as the influence of Zr, with the aim to find out how they affect the chemical content, morphology, surface roughness, and corrosion stability of oxide coatings. It was shown that the presence of Zr increases the corrosion stability of oxide coatings for all investigated PEO times. Evolution of EIS spectra during the exposure to 3% NaCl, as a strong corrosive agent, indicated the highest corrosion stability for PEO coating formed on aluminum at 70 mA/cm(2) for 2 min in a zirconium containing electrolyte.

In Vivo Wear Performance of Cobalt-Chromium Versus Oxidized Zirconium Femoral Total Knee Replacements.

PubMed

Gascoyne, Trevor C; Teeter, Matthew G; Guenther, Leah E; Burnell, Colin D; Bohm, Eric R; Naudie, Douglas R

2016-01-01

This study examines the damage and wear on the polyethylene (PE) inserts from 52 retrieved Genesis II total knee replacements to identify differences in tribological performance between matched pairs of cobalt-chromium (CoCr) and oxidized zirconium (OxZr) femoral components. Observer damage scoring and microcomputed tomography were used to quantify PE damage and wear, respectively. No significant differences were found between CoCr and OxZr groups in terms of PE insert damage, surface penetration, or wear. No severe damage such as cracking or delamination was noted on any of the 52 PE inserts. Observer damage scoring did not correlate with penetrative or volumetric PE wear. The more costly OxZr femoral component does not demonstrate clear tribological benefit over the standard CoCr component in the short term with this total knee replacement design. Copyright © 2016 Elsevier Inc. All rights reserved.

Constituent Redistribution in U-Zr Metallic Fuel Using the Advanced Fuel Performance Code BISON

DOE Office of Scientific and Technical Information (OSTI.GOV)

Galloway, Jack D.; Unal, Cetin; Matthews, Christopher

2016-09-30

Previous work done by Galloway, et. al. on EBR-II ternary (U-Pu-Zr) fuel constituent redistribution yielded accurate simulation data for the limited data sets of Zr redistribution. The data sets included EPMA scans of two different irradiated rods. First, T179, which was irradiated to 1.9 at% burnup, was analyzed. Second, DP16, which was irradiated to 11 at% burnup, was analyzed. One set of parameters that most accurately represented the zirconium profiles for both experiments was determined. Since the binary fuel (U-Zr) has previously been used as the driver fuel for sodium fast reactors (SFR) as well as being the likely drivermore » fuel if a new SFR is constructed, this same process has been initiated on the binary fuel form. From limited binary EPMA scans as well as other fuel characterization techniques, it has been observed that zirconium redistribution also occurs in the binary fuel, albeit at a reduced rate compared to observation in the ternary fuel, as noted by Kim et. al. While the rate of redistribution has been observed to be slower, numerous metallographs of U-Zr fuel show distinct zone formations.« less

Elaboration of Alumina-Zirconia Composites: Role of the Zirconia Content on the Microstructure and Mechanical Properties

PubMed Central

Naglieri, Valentina; Palmero, Paola; Montanaro, Laura; Chevalier, Jérôme

2013-01-01

Alumina-zirconia (AZ) composites are attractive structural materials, which combine the high hardness and Young’s modulus of the alumina matrix with additional toughening effects, due to the zirconia dispersion. In this study, AZ composites containing different amounts of zirconia (in the range 5–20 vol %) were prepared by a wet chemical method, consisting on the surface coating of alumina powders by mixing them with zirconium salt aqueous solutions. After spray-drying, powders were calcined at 600 °C for 1 h. Green bodies were then prepared by two methods: uniaxial pressing of spray-dried granules and slip casting of slurries, obtained by re-dispersing the spray dried granulates. After pressureless sintering at 1500 °C for 1 h, the slip cast samples gave rise to fully dense materials, characterized by a quite homogeneous distribution of ZrO2 grains in the alumina matrix. The microstructure, phase composition, tetragonal to monoclinic transformation behavior and mechanical properties were investigated and are here discussed as a function of the ZrO2 content. The material containing 10 vol % ZrO2 presented a relevant hardness and exhibited the maximum value of KI0, mainly imputable to the t → m transformation at the crack tip. PMID:28809262

Optimized anion exchange column isolation of zirconium-89 (89Zr) from yttrium cyclotron target: Method development and implementation on an automated fluidic platform.

PubMed

O'Hara, Matthew J; Murray, Nathaniel J; Carter, Jennifer C; Morrison, Samuel S

2018-04-13

Zirconium-89 ( 89 Zr), produced by the (p, n) reaction from naturally monoisotopic yttrium ( nat Y), is a promising positron emitting isotope for immunoPET imaging. Its long half-life of 78.4 h is sufficient for evaluating slow physiological processes. A prototype automated fluidic system, coupled to on-line and in-line detectors, has been constructed to facilitate development of new 89 Zr purification methodologies. The highly reproducible reagent delivery platform and near-real time monitoring of column effluents allows for efficient method optimization. The separation of Zr from dissolved Y metal targets was evaluated using several anion exchange resins. Each resin was evaluated against its ability to quantitatively capture Zr from a load solution high in dissolved Y. The most appropriate anion exchange resin for this application was identified, and the separation method was optimized. The method is capable of a high Y decontamination factor (>10 5 ) and has been shown to remove Fe, an abundant contaminant in Y foils, from the 89 Zr elution fraction. Finally, the method was evaluated using cyclotron bombarded Y foil targets; the method was shown to achieve >95% recovery of the 89 Zr present in the foils. The anion exchange column method described here is intended to be the first 89 Zr isolation stage in a dual-column purification process. Copyright © 2018 Elsevier B.V. All rights reserved.

Synthesis and characterization of insulin/zirconium phosphate@TiO2 hybrid composites for enhanced oral insulin delivery applications.

PubMed

Safari, Mostafa; Kamari, Younes; Ghiaci, Mehran; Sadeghi-Aliabadi, Hojjat; Mirian, Mina

2017-05-01

In this work, a series of composites of insulin (Ins)/zirconium phosphate (ZrP) were synthesized by intercalation method, then, these composites were coated with TiO 2 by sol-gel method to prepare Ins/ZrP@TiO 2 hybrid composites and the drug release of the composites was investigated by using UV-Vis spectroscopy. Ins/ZrP (10, 30, 60 wt%) composites were prepared by intercalation of insulin into the ZrP layers in water. Then Ins/ZrP composites were coated with different amounts of TiO 2 (30, 50, 100 wt %) by using titanium tetra n-butoxide, as precursor. Formation of intercalated Ins/ZrP and Ins/ZrP@TiO 2 hybrid composites was characterized by FT-IR, FE-SEM, BET and XRD analysis. Zeta potential of the optimized Ins/ZrP@TiO 2 hybrid composite was determined -27.2 mV. Cytotoxic effects of the optimized Ins/ZrP@TiO 2 hybrid composite against HeLa and Hek293T cell lines were evaluated using MTT assay and the results showed that designed drug delivery system was not toxic in biological environment. Compared to the Ins/ZrP composites, incorporation of TiO 2 coating enhanced the drug entrapment considerably, and reduced the drug release. The Ins/ZrP composites without TiO 2 coating released the whole drug after 30 min in pH 7.4 (phosphate buffer solution) while the TiO 2 -coated composites released the entrapped drug after 20 h. In addition to increasing the shelf life of hormone, this nanoencapsulation and nanocoating method can convert the insulin utilization from injection to oral and present a painless and more comfortable treatment for diabetics.

Zirconium phosphate nanoplatelets: a biocompatible nanomaterial for drug delivery to cancer

NASA Astrophysics Data System (ADS)

Saxena, Vipin; Diaz, Agustin; Clearfield, Abraham; Batteas, James D.; Hussain, Muhammad Delwar

2013-02-01

The objective of this study was to evaluate the biocompatibility of zirconium phosphate (ZrP) nanoplatelets (NPs), and their use in drug delivery. ZrP and doxorubicin-intercalated ZrP (DOX:ZrP) NPs were characterized by using X-Ray Powder Diffraction (XRPD), Thermogravimetric Analysis (TGA), Transmission Electron Micrography (TEM), Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). Biocompatibility of ZrP NPs was evaluated in human embryonic kidney (HEK-293), breast cancer (MCF-7), metastatic breast cancer (MDA-MB-231), ovarian cancer (OVCAR-3), resistant cancer (NCI-RES/ADR) cells and mouse macrophage (RAW 264.7) cell lines. Hemocompatibility of ZrP NPs was evaluated with human red blood cells. Simulated body fluid (SBF) of pH 7.4 was used to determine the in vitro release of doxorubicin from DOX:ZrP NPs. Cellular uptake and in vitro cytotoxicity studies of DOX:ZrP NPs were determined in MDA-MB-231. The ZrP nanomaterial can be prepared in the 100-200 nm size range with a platelet-like shape. The ZrP NPs themselves are biocompatible, hemocompatible and showed no toxicity to the macrophage cells. ZrP NPs can intercalate high loads (35% w/w) of doxorubicin between their layers. The release of DOX was sustained for about 2 weeks. DOX:ZrP NPs showed higher cellular uptake and increased cytotoxicity than free DOX in MDA-MB-231 cells. ZrP NPs are highly biocompatible, can intercalate large amounts of drugs and sustain the release of drugs. ZrP NPs improved the cellular uptake and cytotoxicity of DOX to MDA-MB-231 cells. ZrP NPs are promising nanocarriers for drug delivery in cancer therapy.The objective of this study was to evaluate the biocompatibility of zirconium phosphate (ZrP) nanoplatelets (NPs), and their use in drug delivery. ZrP and doxorubicin-intercalated ZrP (DOX:ZrP) NPs were characterized by using X-Ray Powder Diffraction (XRPD), Thermogravimetric Analysis (TGA), Transmission Electron Micrography (TEM), Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). Biocompatibility of ZrP NPs was evaluated in human embryonic kidney (HEK-293), breast cancer (MCF-7), metastatic breast cancer (MDA-MB-231), ovarian cancer (OVCAR-3), resistant cancer (NCI-RES/ADR) cells and mouse macrophage (RAW 264.7) cell lines. Hemocompatibility of ZrP NPs was evaluated with human red blood cells. Simulated body fluid (SBF) of pH 7.4 was used to determine the in vitro release of doxorubicin from DOX:ZrP NPs. Cellular uptake and in vitro cytotoxicity studies of DOX:ZrP NPs were determined in MDA-MB-231. The ZrP nanomaterial can be prepared in the 100-200 nm size range with a platelet-like shape. The ZrP NPs themselves are biocompatible, hemocompatible and showed no toxicity to the macrophage cells. ZrP NPs can intercalate high loads (35% w/w) of doxorubicin between their layers. The release of DOX was sustained for about 2 weeks. DOX:ZrP NPs showed higher cellular uptake and increased cytotoxicity than free DOX in MDA-MB-231 cells. ZrP NPs are highly biocompatible, can intercalate large amounts of drugs and sustain the release of drugs. ZrP NPs improved the cellular uptake and cytotoxicity of DOX to MDA-MB-231 cells. ZrP NPs are promising nanocarriers for drug delivery in cancer therapy. Electronic supplementary information (ESI) available. See DOI: 10.1039/c3nr34242e

Optimized anion exchange column isolation of zirconium-89 ( 89 Zr) from yttrium cyclotron target: Method development and implementation on an automated fluidic platform

DOE Office of Scientific and Technical Information (OSTI.GOV)

O’Hara, Matthew J.; Murray, Nathaniel J.; Carter, Jennifer C.

Zirconium-89 (89Zr), produced by the (p,n) reaction from naturally monoisotopic yttrium (natY), is a promising positron emitting isotope for immunoPET imaging. Its long half-life of 78.4 h is sufficient for evaluating slow physiological processes. A prototype automated fluidic system, coupled to on-line and in-line detectors, has been constructed to facilitate development of new 89Zr purification methodologies. The highly reproducible reagent delivery platform and near-real time monitoring of column effluents allows for efficient method optimization. The separation of Zr from dissolved Y metal targets was evaluated using several anion exchange resins. Each resin was evaluated against its ability to quantitatively capturemore » Zr from a load solution that is high in dissolved Y. The most appropriate anion exchange resin for this application was identified, and the separation method was optimized. The method is capable of a high Y decontamination factor (>105) and has been shown to separate Fe, an abundant contaminant in Y foils, from the 89Zr elution fraction. Finally, the performance of the method was evaluated using cyclotron bombarded Y foil targets. The separation method was shown to achieve >95% recovery of the 89Zr present in the foils. The 89Zr eluent, however, was in a chemical matrix not immediately conducive to labeling onto proteins. The main intent of this study was to develop a tandem column 89Zr purification process, wherein the anion exchange column method described here is the first separation in a dual-column purification process.« less

Spectroscopic Study of the Interaction between Horse Heart Myoglobin and Zirconium(IV)-Substituted Polyoxometalates as Artificial Proteases.

PubMed

Ly, Hong Giang T; Parac-Vogt, Tatjana N

2017-09-20

A recent study [Angew. Chem. Int. Ed. 2015, 54, 7391-7394] has shown that horse heart myoglobin (HHM) is selectively hydrolyzed by a range of zirconium(IV)-substituted polyoxometalates (POMs) under mild conditions. In this study, the molecular interactions between the Zr-POM catalysts and HHM are investigated by using a range of complementary techniques, including circular dichroism (CD), UV/Vis spectroscopy, tryptophan fluorescence spectroscopy, and 1 H and 31 P NMR spectroscopy. A tryptophan fluorescence quenching study reveals that, among all examined Zr-POMs, the most reactive POM, 2:2 Zr IV -Keggin, exhibits the strongest interaction with HHM. 31 P NMR spectroscopy studies show that this POM dissociates in solution, resulting in the formation of a monomeric 1:1 Zr IV -Keggin structure, which is likely to be a catalytically active species. In the presence of Zr IV -POMs, HHM does not undergo complete denaturation, as evidenced by CD, UV/Vis, tryptophan fluorescence, and 1 H NMR spectroscopy. CD spectroscopy shows a gradual decrease in the α-helical content of HHM upon addition of Zr IV -POMs. The largest effect is observed in the presence of a large Zr IV -Wells-Dawson structure, whereas small Zr IV -Lindqvist POM has the least influence on the decrease in the α-helical content of HHM. In all cases, the Soret band at λ=409 nm is maintained in the presence of all examined Zr-POMs, which indicates that no conformational changes in the protein occur near the heme group. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Zirconium oxide ceramic foam: a promising supporting biomaterial for massive production of glial cell line-derived neurotrophic factor*

PubMed Central

Liu, Zhong-wei; Li, Wen-qiang; Wang, Jun-kui; Ma, Xian-cang; Liang, Chen; Liu, Peng; Chu, Zheng; Dang, Yong-hui

2014-01-01

This study investigated the potential application of a zirconium oxide (ZrO2) ceramic foam culturing system to the production of glial cell line-derived neurotrophic factor (GDNF). Three sets of ZrO2 ceramic foams with different pore densities of 10, 20, and 30 pores per linear inch (PPI) were prepared to support a 3D culturing system. After primary astrocytes were cultured in these systems, production yields of GDNF were evaluated. The biomaterial biocompatibility, cell proliferation and activation of cellular signaling pathways in GDNF synthesis and secretion in the culturing systems were also assessed and compared with a conventional culturing system. In this study, we found that the ZrO2 ceramic foam culturing system was biocompatible, using which the GDNF yields were elevated and sustained by stimulated cell proliferation and activation of signaling pathways in astrocytes cultured in the system. In conclusion, the ZrO2 ceramic foam is promising for the development of a GDNF mass production device for Parkinson’s disease treatment. PMID:25471830

Atomic-scale study of stacking faults in Zr hydrides and implications on hydride formation.

PubMed

Besson, Remy; Thuinet, L; Louchez, Marc-Antoine

2018-06-25

We performed atomic-scale ab initio calculations to investigate the stacking fault (SF) properties of the metastable zeta-Zr2H zirconium hydride. The effect of H near the SF was found to entail the existence of negative SF energies, showing that the zeta compound is probably unstable with respect to shearing in the basal plane. The effect of temperature on SFs was investigated by means of free energy calculations in the quasiharmonic approximation. This evidenced unexpectedly large temperature effects, confirming the main conclusions drawn at 0 K, in particular the zeta mechanical instability. The complex behaviour of H atoms during the shear process suggested zeta-hcp --> Zr2H[111]-fcc as a plausible shear path leading to an fcc compound with same composition as zeta. Finally, as shown by an analysis based on microelasticity, this Zr2H[111]-fcc intermediate compound may be relevant for better interpreting the currently intricate issue of hydride habit planes in zirconium. © 2018 IOP Publishing Ltd.

Electrophoretic fabrication of chitosan-zirconium-oxide nanobiocomposite platform for nucleic acid detection.

PubMed

Das, Maumita; Dhand, Chetna; Sumana, Gajjala; Srivastava, A K; Nagarajan, R; Nain, Lata; Iwamoto, M; Manaka, Takaaki; Malhotra, B D

2011-03-14

The present work describes electrophoretic fabrication of nanostructured chitosan-zirconium-oxide composite (CHIT-NanoZrO(2)) film (180 nm) onto indium-tin-oxide (ITO)-coated glass plate. This nanobiocomposite film has been explored as immobilization platform for probe DNA specific to M. Tuberculosis as model biomolecule to investigate its sensing characteristics. It is revealed that pH-responsive behavior of CHIT and its cationic skeleton is responsible for the movement of CHIT-NanoZrO(2) colloids toward cathode during electrophoretic deposition. The FT-IR, SEM, TEM, and EDX techniques have been employed for the structural, morphological, and composition analysis of the fabricated electrodes. The morphological studies clearly reveal uniform inter-linking and dispersion of hexagonal nanograins of ZrO(2) (30-50 nm) into the chitosan matrix, resulting in homogeneous nanobiocomposite formation. Electrochemical response measurements of DNA/CHIT-NanoZrO(2)/ITO bioelectrode, carried out using cyclic voltammetry and differential pulse voltammetry, reveal that this bioelectrode can specifically detect complementary target DNA up to 0.00078 μM with sensitivity of 6.38 × 10(-6) AμM(-1).

Evidence for independent motional processes on the two interstitial sublattices of a layer-structured metal hydride: Hydrogen spin-lattice relaxation and motional narrowing in zirconium monohalide hemihydrides, ZrXH0.5

NASA Astrophysics Data System (ADS)

Hwang, T. Y.; Schoenberger, R. J.; Torgeson, D. R.; Barnes, R. G.

1983-01-01

We report the results of a proton-magnetic-resonance investigation of hydrogen location and motion in the hemihydrides ZrXH0.5 of the metallic layer-structured monohalides ZrX of zirconium (X=Br,Cl). Wide-line and pulsed NMR methods were employed to measure the temperature dependence of the linewidth and second moment and of the spin-lattice relaxation time in the laboratory and rotating frames. The results indicate that hydrogen forms an ordered structure on the tetrahedral (T) interstitial sublattice within the Zr metal bilayers, with some (small) random occupancy of octahedral (O) sites. Two stages of motional narrowing observed in the wide-line measurements and double minima found in the relaxation times are consistent with the occurrence of essentially independent hydrogen motional processes on the T and O interstitial sublattices. Hydrogen site occupancy probabilities, jump frequencies, activation energies for hydrogen diffusion, and conduction-electron contributions to the proton spin-lattice relaxation rate are deduced from the measurements.

High performance polymer solar cells with as-prepared zirconium acetylacetonate film as cathode buffer layer

PubMed Central

Tan, Zhan'ao; Li, Shusheng; Wang, Fuzhi; Qian, Deping; Lin, Jun; Hou, Jianhui; Li, Yongfang

2014-01-01

Low-work-function active metals are commonly used as cathode in polymer solar cells (PSCs), but sensitivity of the active metals towards moisture and oxygen results in poor stability of the devices. Therefore, solution-proceessable and stable cathode buffer layer is of great importance for the application of PSCs. Here we demonstrate high performance PSCs by employing as-prepared zirconium acetylacetonate (a-ZrAcac) film spin-cast from its ethanol solution as cathode buffer layer. The PSCs based on a low bandgap polymer PBDTBDD as donor and PC60BM as acceptor with a-ZrAcac/Al cathode demonstrated an average power conversion efficiency (PCE) of 8.75% which is significantly improved than that of the devices with traditional Ca/Al cathode. The improved photovoltaic performance is benefitted from the decreased series resistance and enhanced light harvest of the PSCs with the a-ZrAcac/Al cathode. The results indicate that a-ZrAcac is a promising high performance cathode buffer layer for fabricating large area flexible PSCs. PMID:24732976

Efficient mass-selective three-photon ionization of zirconium atoms

DOEpatents

Page, Ralph H.

1994-01-01

In an AVLIS process, .sup.91 Zr is selectively removed from natural zirconium by a three-step photoionization wherein Zr atoms are irradiated by a laser beam having a wavelength .lambda..sub.1, selectively raising .sup.91 Zr atoms to an odd-parity E.sub.1 energy level in the range of 16000-19000 cm.sup.-1, are irradiated by a laser beam having a wavelength .lambda..sub.2 to raise the atoms from an E.sub.l level to an even-parity E.sub.2 energy level in the range of 35000-37000 cm.sup.-1 and are irradiated by a laser beam having a wavelength .lambda..sub.3 to cause a resonant transition of atoms from an E.sub.2 level to an autoionizing level above 53506 cm.sup.-1. .lambda..sub.3 wavelengths of 5607, 6511 or 5756 .ANG. will excite a zirconium atom from an E.sub.2 energy state of 36344 cm.sup.-1 to an autoionizing level; a .lambda..sub.3 wavelength of 5666 .ANG. will cause an autoionizing transition from an E.sub.2 level of 36068 cm.sup.-1 ; and a .lambda. .sub.3 wavelength of 5662 .ANG. will cause an ionizing resonance of an atom at an E.sub.2 level of 35904 cm.sup.-1.

Surface functionalization of mesoporous silica SBA-15 by liquid-phase grafting of zirconium phosphate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dai, Sheng; Hagaman, Edward; Ma, Zhen

2010-01-01

The introduction of mesoporous silicas in the 1990s has offered new opportunities for the engineering of ordered catalytic nanoreactors, but the acid properties of mesoporous silicas are rather poor. Herein, mesoporous silica (SBA-15) surfaces were functionalized by zirconium phosphate via two methods recently developed in our group. Zr(OPr){sub 4} and POCl{sub 3} were used as appropriate precursors in both methods. The main difference between these methods lies in whether Zr(OPr){sub 4} is grafted onto SBA-15 first and POCl{sub 3} second (method 1) or the grafting process takes place in one pot, with SBA-15, Zr(OPr){sub 4}, and POCl{sub 3} altogether (methodmore » 2). More zirconium phosphate could be grafted by repeating the above procedures. The materials were characterized by ICP-OES, XRD, N{sub 2} adsorption-desorption, TEM, {sup 31}P and {sup 29}Si MAS NMR, and NH{sub 3}-TPD, and their applications in catalytic isopropanol dehydration, cumene cracking, and metal-ion adsorption were demonstrated. Aluminum phosphate-modified SBA-15 samples could be obtained via these two methods as well. This work enriches the family of metal phosphate-functionalized mesoporous silicas as new solid acid catalysts.« less

Comparing XPS on bare and capped ZrN films grown by plasma enhanced ALD: Effect of ambient oxidation

NASA Astrophysics Data System (ADS)

Muneshwar, Triratna; Cadien, Ken

2018-03-01

In this article we compare x-ray photoelectron spectroscopy (XPS) measurements on bare- and capped- zirconium nitride (ZrN) films to investigate the effect of ambient sample oxidation on the detected bound O in the form of oxide ZrO2 and/or oxynitride ZrOxNy. ZrN films in both bare- and Al2O3/AlN capped- XPS samples were grown by plasma-enhanced atomic layer deposition (PEALD) technique using tetrakis dimethylamino zirconium (TDMAZr) precursor, forming gas (5% H2, rest N2) inductively coupled plasma (ICP), and as received research grade process gases under identical process conditions. Capped samples were prepared by depositing 1 nm thick PEALD AlN on ZrN, followed by additional deposition of 1 nm thick ALD Al2O3, without venting of ALD reactor. On bare ZrN sample at room temperature, spectroscopic ellipsometry (SE) measurements with increasing ambient exposure times (texp) showed a self-limiting surface oxidation with the oxide thickness (dox) approaching 3.7 ± 0.02 nm for texp > 120 min. In XPS data measured prior to sample sputtering (tsput = 0), ZrO2 and ZrOxNy were detected in bare- samples, whereas only ZrN and Al2O3/AlN from capping layer were detected in capped- samples. For bare-ZrN samples, appearance of ZrO2 and ZrOxNy up to sputter depth (dsput) of 15 nm in depth-profile XPS data is in contradiction with measured dox = 3.7 nm, but explained from sputtering induced atomic inter-diffusion within analyzed sample. Appearance of artifacts in the XPS spectra from moderately sputtered (dsput = 0.2 nm and 0.4 nm) capped-ZrN sample, provides an evidence to ion-bombardment induced modifications within analyzed sample.

Nanoencapsulation of Insulin into Zirconium Phosphate for Oral Delivery Applications

PubMed Central

Díaz, Agustín; David, Amanda; Pérez, Riviam; González, Millie L.; Báez, Adriana; Wark, Stacey E.; Zhang, Paul; Clearfield, Abraham; Colón, Jorge L.

2010-01-01

The encapsulation of insulin into different kinds of materials for non-invasive delivery is an important field of study because of the many drawbacks of painful needle and syringe delivery such as physiological stress, infection, and local hypertrophy, among others.1 A stable, robust, non-toxic, and viable non-invasive carrier for insulin delivery is needed. We present a new approach for protein nanoencapsulation using layered zirconium phosphate (ZrP) nanoparticles produced without any preintercalator present. The use of ZrP without preintercalators produces a highly pure material, without any kinds of contaminants, such as the preintercalator, which can be noxious. Cytotoxicity cell viability in vitro experiments for the ZrP nanoparticles show that ZrP is not toxic, or harmful, in a biological environment, as previously reported for rats.2 Contrary to previous preintercalator-based methods, we show that insulin can be nanoencapsulated in ZrP if a highly hydrate phase of ZrP with an interlayer distance of 10.3 Å (10.3 Å-ZrP or θ-ZrP) is used as precursor. The intercalation of insulin into ZrP produced a new insulin-intercalated ZrP phase with a ca. 27 Å interlayer distance, as determined by X-ray powder diffraction, demonstrating a successful nanoencapsulation of the hormone. The in vitro release profile of the hormone after the intercalation was determined and circular dichroism was used to study the hormone stability upon intercalation and release. The insulin remains stable in the layered material, at room temperature, for a considerable amount of time, improving the shell life of the peptidic hormone. This type of materials represents a strong candidate to develop a non-invasive insulin carrier for the treatment of diabetes mellitus. PMID:20707305

Effective dose to staff members in a positron emission tomography/CT facility using zirconium-89

PubMed Central

2013-01-01

Objective: Positron emission tomography (PET) using zirconium-89 (89Zr) is complicated by its complex decay scheme. In this study, we quantified the effective dose from 89Zr and compared it with fluorine-18 fludeoxyglucose (18F-FDG). Methods: Effective dose distribution in a PET/CT facility in Riyadh was calculated by Monte Carlo simulations using MCNPX. The positron bremsstrahlung, the annihilation photons, the delayed gammas from 89Zr and those emissions from 18F-FDG were modelled in the simulations but low-energy characteristic X-rays were ignored. Results: On the basis of injected activity, the dose from 89Zr was higher than that of 18F-FDG. However, the dose per scan from 89Zr became less than that from 18F-FDG near the patient, owing to the difference in injected activities. In the corridor and control rooms, the 89Zr dose was much higher than 18F-FDG, owing to the difference in attenuation by the shielding materials. Conclusion: The presence of the high-energy photons from 89Zr-labelled immuno-PET radiopharmaceuticals causes a significantly higher effective dose than 18F-FDG to the staff outside the patient room. Conversely, despite the low administered activity of 89Zr, it gives rise to a comparable or even lower dose than 18F-FDG to the staff near the patient. This interesting result raises apparently contradictory implications in the radiation protection considerations of a PET/CT facility. Advances in knowledge: To the best of our knowledge, radiation exposure to staff and public in the PET/CT unit using 89Zr has not been investigated. The ultimate output of this study will lead to the optimal design of the facility for routine use of 89Zr. PMID:23934963

Investigation of hydrogen interaction with defects in zirconia

NASA Astrophysics Data System (ADS)

Melikhova, O.; Kuriplach, J.; Čížek, J.; Procházka, I.; Brauer, G.; Anwand, W.

2010-04-01

Defect studies of a ZrO2 + 9 mol. % Y2O3 single crystal were performed in this work using a high resolution positron lifetime spectroscopy combined with slow positron implantation spectroscopy. In order to elucidate the nature of positron trapping sites observed experimentally, the structural relaxations of several types of vacancy-like defects in zirconia were performed and positron characteristics for them were calculated. Relaxed atomic configurations of studied defects were obtained by means of ab initio pseudopotential method within the supercell approach. Theoretical calculations indicated that neither oxygen vacancies nor their neutral complexes with substitute yttrium atoms are capable of positron trapping. On the other hand, zirconium vacancies are deep positron traps and are most probably responsible for the saturated positron trapping observed in yttria stabilized zirconia single crystals. However, the calculated positron lifetime for zirconium vacancy is apparently longer than the experimental value corresponding to a single-component spectrum measured for the cubic ZrO2 + 9 mol. % Y2O3 single crystal. It was demonstrated that this effect can be explained by hydrogen trapped in zirconium vacancies. On the basis of structure relaxations, we found that zirconium vacancy - hydrogen complexes represent deep positron traps with the calculated lifetime close to the experimental one. In zirconium vacancy - hydrogen complexes the hydrogen atom forms an O-H bond with one of the nearest neighbour oxygen atoms. The calculated bond length is close to 1 Å.

Studies of anti-fibrillogenic activity of phthalocyanines of zirconium containing out-of-plane ligands.

PubMed

Kovalska, Vladyslava; Losytskyy, Mykhaylo; Chernii, Viktor; Volkova, Kateryna; Tretyakova, Iryna; Cherepanov, Vsevolod; Yarmoluk, Sergiy; Volkov, Sergiy

2012-01-01

Series of phthalocyanines of zirconium containing lysine, citric, nonanoic acid residues and dibenzolylmethane groups as out-of-plane ligands are firstly studied as inhibitors of fibrillogenesis using cyanine-based fluorescent inhibitory assay. It was shown that studied phthalocyanines at concentration of 20μM inhibited aggregation reaction on 38.5-57.6% and inhibitory activity of phthalocyanines depended on the chemical nature of out-of-plane ligand. For the most active compound PcZrLys(2) (zirconium phthalocyanine containing lysine fragment) the efficient inhibitor concentration was estimated to be 37μM. AFM studies have shown that in the presence of PcZrLys(2) the inhibition of fibrils formation and formation of spherical oligomeric aggregates took place. Due to the ability of phthalocyanines to decrease efficiently protein aggregation into the amyloid fibrils, modification of phthalocyanine molecules via out-of-plane substitutions was proposed as approach for design of anti-fibrillogenic agents with required properties. Copyright © 2011. Published by Elsevier Ltd.

Simultaneous spectrophotometric determination of trace amounts of uranium, thorium, and zirconium using the partial least squares method after their preconcentration by alpha-benzoin oxime modified Amberlite XAD-2000 resin.

PubMed

Ghasemi, Jahan B; Zolfonoun, E

2010-01-15

A new solid phase extraction method for separation and preconcentration of trace amounts of uranium, thorium, and zirconium in water samples is proposed. The procedure is based on the adsorption of U(VI), Th(IV) and Zr(IV) ions on a column of Amberlite XAD-2000 resin loaded with alpha-benzoin oxime prior to their simultaneous spectrophotometric determination with Arsenazo III using orthogonal signal correction partial least squares method. The enrichment factor for preconcentration of uranium, thorium, and zirconium was found to be 100. The detection limits for U(VI), Th(IV) and Zr(IV) were 0.50, 0.54, and 0.48microgL(-1), respectively. The precision of the method, evaluated as the relative standard deviation obtained by analyzing a series of 10 replicates, was below 4% for all elements. The practical applicability of the developed sorbent was examined using synthetic seawater, natural waters and ceramic samples.

Thermochemistry of amorphous and crystalline zirconium and hafnium silicates.

NASA Astrophysics Data System (ADS)

Ushakov, S.; Brown, C. E.; Navrotsky, Alexandra; Boatner, L. A.; Demkov, A. A.; Wang, C.; Nguyen, B.-Y.

2003-03-01

Calorimetric investigation of amorphous and crystalline zirconium and hafnium silicates was performed as part of a research program on thermochemistry of alternative gate dielectrics. Amorphous hafnium and zirconium silicates with varying SiO2 content were synthesized by a sol-gel process. Crystalline zirconium and hafnium silicates (zircon and hafnon) were synthesized by solid state reaction at 1450 °C from amorphous gels and grown as single crystals from flux. High temperature oxide melt solution calorimetry in lead borate (2PbO.B2O3) solvent at 800 oC was used to measure drop solution enthalpies for amorphous and crystalline zirconium and hafnium silicates and corresponding oxides. Applying appropriate thermochemical cycles, formation enthalpy of crystalline ZrSiO4 (zircon) from binary oxides (baddeleite and quartz) at 298 K was calculated as -23 +/-2 kJ/mol and enthalpy difference between amorphous and crystalline zirconium silicate (vitrification enthalpy) was found to be 61 +/-3 kJ/mol. Crystallization onset temperatures of amorphous zirconium and hafnium silicates, as measured by differential scanning calorimetry (DSC), increased with silica content. The resulting crystalline phases, as characterized by X-ray diffraction (XRD), were tetragonal HfO2 and ZrO2. Critical crystallite size for tetragonal to monoclinic transformation of HfO2 in the gel was estimated as 6 +/-2 nm from XRD data Crystallization enthalpies per mole of hafnia and zirconia in gels decrease slightly together with crystallite size with increasing silica content, for example from -22 to -15 +/-1 kJ per mol of HfO2 crystallized at 740 and 1006 °C from silicates with 10 and 70 mol Applications of thermal analyses and solution calorimetry techniques together with first-principles density functional calculations to estimate interface and surface energies are discussed.

High Temperature Corrosion and Heat Transfer Studies of Zirconium-Silicide Coatings for Light Water Reactor Cladding Applications

NASA Astrophysics Data System (ADS)

Yeom, Hwasung

Experimental results investigating the feasibility of zirconium-silicide coating for accident tolerance of LWR fuel cladding coating was presented. The oxidation resistance of ZrSi2 appeared to be superior to bare Zircaloy-4 in high temperature air. It was shown that micro- and nanostructures consisting of alternating SiO2 and ZrO2 evolved during transient oxidation of ZrSi2, which was explained by spinodal phase decomposition of Zr-Si-O oxide. Coating optimization regarding oxidation resistance was performed mainly using magnetron sputter deposition method. ZrSi 2 coatings ( 3.9 microm) showed improvement of almost two orders of magnitude when compared to bare Zircaloy-4 after air-oxidation at 700 °C for 20-hours. Pre-oxidation of ZrSi2 coating at 700 °C for 5 h significantly mitigated oxygen diffusion in air-oxidation tests at 1000 °C for 1-hour and 1200 °C for 10-minutes. The ZrSi2 coating with the pre-oxidation was found to be the best condition to prevent oxide formation in Zircaloy-4 substrate in the steam condition even if the top surface of the coating was degraded by formation of zirconium-rich oxide layer. Only the ZrSiO4 phase, formed by exposing the ZrSi2 coating at 1400 °C in air, allowed for immobilization of silicon species in the oxide scale in the aqueous environments. A quench test facility was designed and built to study transient boiling heat transfer of modified Zircaloy-4 surfaces (e.g., roughened surfaces, oxidized surfaces, ZrSi2 coated surfaces) at various system conditions (e.g., elevated pressures and water subcooling). The minimum film boiling temperature increased with increasing system pressure and water subcooling, consistent with past literature. Quenching behavior was affected by the types of surface modification regardless of the environmental conditions. Quenching heat transfer was improved by the ZrSi 2 coating, a degree of surface oxidation (deltaox = 3 to 50 microm), and surface roughening (Ra 20 microm). A plausible hypothesis based on transient heat conduction models for liquid-solid contact in quenching process was proposed to explain the enhanced quenching performance. The theoretical model incorporated localized temperature behavior on superheated surface and elucidated bubble dynamics qualitatively, and predicts minimum film boiling temperature of oxidized Zirc-4 surfaces, which were in good agreement with experimental data.

Thermal conductivity of self-ion irradiated nanocrystalline zirconium thin films

DOE PAGES

Pulavarthy, Raghu; Wang, Baoming; Hattar, Khalid; ...

2017-07-15

Thermomechanical stability and high thermal conductivity are important for nuclear cladding material performance and reliability, which degrade over time under irradiation. The literature suggests nanocrystalline materials as radiation tolerant, but little or no evidence is present from thermal transport perspective. In this study, we irradiated 10 nm grain size zirconium thin films with 800 keV Zr + beam from a 6 MV HVE Tandem accelerator to achieve various doses of 3 × 10 10 to 3.26 × 10 14 ions/cm 2, corresponding to displacement per atom (dpa) of 2.1 × 10 –4 to 2.28. Transmission electron microscopy showed significant grainmore » growth, texture evolution and oxidation in addition to the creation of displacement defects due to the irradiation. The specimens were co-fabricated with micro-heaters to establish thermal gradients that were mapped using infrared thermometry. An energy balance approach was used to estimate the thermal conductivity of the specimens, as function of irradiation dosage. As a result, up to 32% reduction of thermal conductivity was measured for the sample exposed to a dose of 2.1 dpa (3 × 10 14 ions/cm 2).« less

Thermal conductivity of self-ion irradiated nanocrystalline zirconium thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pulavarthy, Raghu; Wang, Baoming; Hattar, Khalid

Thermomechanical stability and high thermal conductivity are important for nuclear cladding material performance and reliability, which degrade over time under irradiation. The literature suggests nanocrystalline materials as radiation tolerant, but little or no evidence is present from thermal transport perspective. In this study, we irradiated 10 nm grain size zirconium thin films with 800 keV Zr + beam from a 6 MV HVE Tandem accelerator to achieve various doses of 3 × 10 10 to 3.26 × 10 14 ions/cm 2, corresponding to displacement per atom (dpa) of 2.1 × 10 –4 to 2.28. Transmission electron microscopy showed significant grainmore » growth, texture evolution and oxidation in addition to the creation of displacement defects due to the irradiation. The specimens were co-fabricated with micro-heaters to establish thermal gradients that were mapped using infrared thermometry. An energy balance approach was used to estimate the thermal conductivity of the specimens, as function of irradiation dosage. As a result, up to 32% reduction of thermal conductivity was measured for the sample exposed to a dose of 2.1 dpa (3 × 10 14 ions/cm 2).« less

Purification of nuclear grade Zr scrap as the high purity dense Zr deposits from Zirlo scrap by electrorefining in LiF-KF-ZrF4 molten fluorides

NASA Astrophysics Data System (ADS)

Park, Kyoung Tae; Lee, Tae Hyuk; Jo, Nam Chan; Nersisyan, Hayk H.; Chun, Byong Sun; Lee, Hyuk Hee; Lee, Jong Hyeon

2013-05-01

Zirconium (Zr) has commonly been used as a cladding material of nuclear fuel. Moreover, it is regarded as the only material that can be used for nuclear fuel cladding because it has the lowest neutron capture cross section of any metal element and because it has high corrosion resistance and size stability. In this study, Hf-free Zr tubes (Zr-1Nb-1Sn-0.1Fe) were used as anode materials and electrorefining was performed in a LiF-KF eutectic 6 wt.% ZrF4 molten fluoride salt system. As a result of electrolysis, Zr scrap metal was recycled into pure Zr with low levels of impurities, and the size and density of the Zr deposit was controlled using applied current density.

Effects of Plasma ZrN Metallurgy and Shot Peening Duplex Treatment on Fretting Wear and Fretting Fatigue Behavior of Ti6Al4V Alloy.

PubMed

Tang, Jingang; Liu, Daoxin; Zhang, Xiaohua; Du, Dongxing; Yu, Shouming

2016-03-23

A metallurgical zirconium nitride (ZrN) layer was fabricated using glow metallurgy using nitriding with zirconiuming prior treatment of the Ti6Al4V alloy. The microstructure, composition and microhardness of the corresponding layer were studied. The influence of this treatment on fretting wear (FW) and fretting fatigue (FF) behavior of the Ti6Al4V alloy was studied. The composite layer consisted of an 8-μm-thick ZrN compound layer and a 50-μm-thick nitrogen-rich Zr-Ti solid solution layer. The surface microhardness of the composite layer is 1775 HK 0.1 . A gradient in cross-sectional microhardness distribution exists in the layer. The plasma ZrN metallurgical layer improves the FW resistance of the Ti6Al4V alloy, but reduces the base FF resistance. This occurs because the improvement in surface hardness results in lowering of the toughness and increasing in the notch sensitivity. Compared with shot peening treatment, plasma ZrN metallurgy and shot peening composite treatment improves the FW resistance and enhances the FF resistance of the Ti6Al4V alloy. This is attributed to the introduction of a compressive stress field. The combination of toughness, strength, FW resistance and fatigue resistance enhance the FF resistance for titanium alloy.

Improved fill factor in inverted planar perovskite solar cells with zirconium acetate as the hole-and-ion-blocking layer.

PubMed

Zhang, Xuewen; Liang, Chunjun; Sun, Mengjie; Zhang, Huimin; Ji, Chao; Guo, Zebang; Xu, Yajun; Sun, Fulin; Song, Qi; He, Zhiqun

2018-03-14

Planar perovskite solar cells (PSCs) have gained great interest due to their low-temperature solution preparation and simple process. In inverted planar PSCs, an additional buffer layer is usually needed on the top of the PCBM electron-transport layer (ETL) to enhance the device performance. In this work, we used a new buffer layer, zirconium acetate (Zr(Ac) 4 ). The inclusion of the Zr(Ac) 4 buffer layer leads to the increase of FF from ∼68% to ∼79% and PCE from ∼14% to ∼17% in the planar PSCs. The UPS measurement indicates that the Zr(Ac) 4 layer has a low HOMO level of -8.2 eV, indicating that the buffer layer can act as a hole-blocking layer. Surface morphology and surface chemistry investigations reveal that the elements I, MA and Pb can diffuse across the PCBM ETL, damaging the device performance. The covering Zr(Ac) 4 molecules fill in the pinholes of the PCBM layer and effectively block the ions/molecules of the perovskite from diffusion across the ETL. The resulting more robust PCBM/Zr(Ac) 4 ETL leads to weaker ionic charge accumulation and lower diode leakage current. The double role of hole-and-ion blocking of the Zr(Ac) 4 layer explains the improved FF and PCE in the PSCs.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ikeuchi, Hirotomo; Yano, Kimihiko; Kaji, Naoya

For the decommissioning of the Fukushima-Daiichi Nuclear Power Station (1F), the characterization of fuel-debris in cores of Units 1-3 is necessary. In this study, typical phases of the in-vessel fuel-debris were estimated using a thermodynamic equilibrium (TDE) calculation. The FactSage program and NUCLEA database were applied to estimate the phase equilibria of debris. It was confirmed that the TDE calculation using the database can reproduce the phase separation behavior of debris observed in the Three Mile Island accident. In the TDE calculation of 1F, the oxygen potential [G(O{sub 2})] was assumed to be a variable. At low G(O{sub 2}) wheremore » metallic zirconium remains, (U,Zr)O{sub 2}, UO{sub 2}, and ZrO{sub 2} were found as oxides, and oxygen-dispersed Zr, Fe{sub 2}(Zr,U), and Fe{sub 3}UZr{sub 2} were found as metals. With an increase in zirconium oxidation, the mass of those metals, especially Fe{sub 3}UZr{sub 2}, decreased, but the other phases of metals hardly changed qualitatively. Consequently, (U,Zr)O{sub 2} is suggested as a typical phase of oxide, and Fe{sub 2}(Zr,U) is suggested as that of metal. However, a more detailed estimation is necessary to consider the distribution of Fe in the reactor pressure vessel through core-melt progression. (authors)« less

Compositional changes at the interface between thorium-doped uranium dioxide and zirconium due to high-temperature annealing

NASA Astrophysics Data System (ADS)

Youn, Young-Sang; Lee, Jeongmook; Kim, Jandee; Kim, Jong-Yun

2018-06-01

Compositional changes at the interface between thorium-doped uranium dioxide (U0.97Th0.03O2) and Zr before and after annealing at 1700 °C for 18 h were studied by X-ray photoelectron spectroscopy, X-ray diffraction, and Raman spectroscopy. At room temperature, the U0.97Th0.03O2 pellet consisted of hyperstoichiometric UO2+x with UO2 and ThO2, and the Zr sample contained Zr with ZrO2. After annealing, the former contained stoichiometric UO2 with ThO2 and the latter consisted of ZrO2 along with ZrO2·2H2O.

Zirconium behaviour during electrorefining of actinide-zirconium alloy in molten LiCl-KCl on aluminium cathodes

NASA Astrophysics Data System (ADS)

Meier, R.; Souček, P.; Malmbeck, R.; Krachler, M.; Rodrigues, A.; Claux, B.; Glatz, J.-P.; Fanghänel, Th.

2016-04-01

A pyrochemical electrorefining process for the recovery of actinides from metallic nuclear fuel based on actinide-zirconium alloys (An-Zr) in a molten salt is being investigated. In this process actinides are group-selectively recovered on solid aluminium cathodes as An-Al alloys using a LiCl-KCl eutectic melt at a temperature of 450 °C. In the present study the electrochemical behaviour of zirconium during electrorefining was investigated. The maximum amount of actinides that can be oxidised without anodic co-dissolution of zirconium was determined at a selected constant cathodic current density. The experiment consisted of three steps to assess the different stages of the electrorefining process, each of which employing a fresh aluminium cathode. The results indicate that almost a complete dissolution of the actinides without co-dissolution of zirconium is possible under the applied experimental conditions.

Minimalistic Liquid-Assisted Route to Highly Crystalline α-Zirconium Phosphate.

PubMed

Cheng, Yu; Wang, Xiaodong Tony; Jaenicke, Stephan; Chuah, Gaik-Khuan

2017-08-24

Zirconium phosphates have potential applications in areas of ion exchange, catalysis, photochemistry, and biotechnology. However, synthesis methodologies to form crystalline α-zirconium phosphate (Zr(HPO 4 ) 2 ⋅H 2 O) typically involve the use of excess phosphoric acid, addition of HF or oxalic acid and long reflux times or hydrothermal conditions. A minimalistic sustainable route to its synthesis has been developed by using only zirconium oxychloride and concentrated phosphoric acid to form highly crystalline α-zirconium phosphate within hours. The morphology can be changed from platelets to rod-shaped particles by fluoride addition. By varying the temperature and time, α-zirconium phosphate with particle sizes from nanometers to microns can be obtained. Key features of this minimal solvent synthesis are the excellent yields obtained with high atom economy under mild conditions and ease of scalability. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Visual and surface plasmon resonance sensor for zirconium based on zirconium-induced aggregation of adenosine triphosphate-stabilized gold nanoparticles.

PubMed

Qi, Wenjing; Zhao, Jianming; Zhang, Wei; Liu, Zhongyuan; Xu, Min; Anjum, Saima; Majeed, Saadat; Xu, Guobao

2013-07-17

Owing to its high affinity with phosphate, Zr(IV) can induce the aggregation of adenosine 5'-triphosphate (ATP)-stabilized AuNPs, leading to the change of surface plasmon resonance (SPR) absorption spectra and color of ATP-stabilized AuNP solutions. Based on these phenomena, visual and SPR sensors for Zr(IV) have been developed for the first time. The A(660 nm)/A(518 nm) values of ATP-stabilized AuNPs in SPR absorption spectra increase linearly with the concentrations of Zr(IV) from 0.5 μM to 100 μM (r=0.9971) with a detection limit of 95 nM. A visual Zr(IV) detection is achieved with a detection limit of 30 μM. The sensor shows excellent selectivity against other metal ions, such as Cu(2+), Fe(3+), Cd(2+), and Pb(2+). The recoveries for the detection of 5 μM, 10 μM, 25 μM and 75 μM Zr(IV) in lake water samples are 96.0%, 97.0%, 95.6% and 102.4%, respectively. The recoveries of the proposed SPR method are comparable with those of ICP-OES method. Copyright © 2013 Elsevier B.V. All rights reserved.

Electrical and dielectric properties of ZnO and CeO{sub 2} doped ZrTi{sub 2}O{sub 6} ceramic

DOE Office of Scientific and Technical Information (OSTI.GOV)

George, Aneesh; Thomas, Jijimon K.; John, Annamma

2014-01-28

Zirconium oxide (ZrO{sub 2}) and titanium dioxide (TiO{sub 2}) are the important catalyst supports, since it has acidic and basic properties. The intermediate phase zirconium titanate ZrTi{sub 2}O{sub 6}, which is a solid solution with Zr:Ti ratio 1:2 has outstanding dielectric properties. The effects of doping of ZnO and CeO{sub 2} on the dielectric and electrical properties of ZrTi{sub 2}O{sub 6} ceramic are investigated. On adding 0.5 wt% ZnO, the dielectric constant is increased but, on adding CeO{sub 2}, the dielectric constant is decreased. The bulk density of pure sample sintered at 1530 °C is 91% of theoretical density whilemore » that of the doped samples sintered at 1450 °C is more than 94% of theoretical density. Scanning electron micrographs reveal that the samples are well sintered with minimum porosity. The semicircle behavior in the Cole-Cole plots at room temperature reveals that the samples are good ionic conductor. The induced impedance is reduced for doped samples and this can be used as a material for electrolyte in Solid Oxide Fuel Cell.« less

Thermally Induced Lateral Motion of α-Zirconium Phosphate Layers Intercalated with Hexadecylamines

NASA Astrophysics Data System (ADS)

Char, Kookheon

2005-03-01

Well-defined intercalated structure, either interdigitated layers or bilayers, of hexadecylamines (HDAs) in a confined space of a highly-functionalized layered material, α- zirconium phosphate (α-ZrP), was prepared and these two distinct intercalated structures can serve as model systems to investigate the interaction of the two monolayers whose amphiphilic tails are adjacent to each other. Acidic functional groups (-POH) on the α-ZrP are in well-ordered array and the number of functional group is quite high (i.e., cationic exchange capacity (CEC) = 664 mmole/100 g, area per one charge site = 0.24 nm^2) enough to realize the bilayers (i.e., discrete two monolayers) of HDAs within the α-ZrP interlayer. We employed the two-step intercalation mechanism for the preparation of well- ordered interdigitated layers as well as the bilayers of alkyl chains attached to both sides of the α-ZrP intergallery. An intriguing lateral motion of the α-ZrP sheets was observed with in-situ SAXS measurements for the interdigitated layer during heating and cooling cycle and verified with TEM. This lateral motion is believed to be due to the transition from the tilted to the untilted conformation of the interdigitated HDA chains and this transition is found to be thermally reversible.

Fabrication of a Biomass-Based Hydrous Zirconium Oxide Nanocomposite for Preferable Phosphate Removal and Recovery.

PubMed

Qiu, Hui; Liang, Chen; Zhang, Xiaolin; Chen, Mindong; Zhao, Yunxia; Tao, Tao; Xu, Zhengwen; Liu, Gang

2015-09-23

Advanced removal of phosphate by low-cost adsorbents from municipal wastewater or industrial effluents is an effective and economic way to prevent the occurrence of eutrophication. Here, we proposed a novel method to immobilize hydrous zirconium oxide nanoparticle within quaternary-aminated wheat straw, and obtained an inexpensive, eco-friendly nanocomposite Ws-N-Zr. The biomass-based Ws-N-Zr exhibited higher preference toward phosphate than commercial anion exchanger IRA-900 when competing sulfate ions coexisted at relatively high levels. Such excellent performance of Ws-N-Zr resulted from its specific hybrid structure, the quaternary ammonium groups bonded on the host favor the preconcentration of phosphate ions inside the wheat straw based on Donnan effect, and the encapsulated HZO nanoparticle exhibits preferable sequestration of phosphate ions through specific interaction, as further demonstrated by FTIR and X-ray photoelectron spectroscopy. Cycle adsorption and regeneration experiments demonstrated that Ws-N-Zr could be employed for repeated use without significant capacity loss, when the binary NaOH-NaCl solution was employed as the regenerant. The influence of solution pH and contact time was also examined. The results suggested that Ws-N-Zr has a great potential in efficient removal of phosphate in contaminated waters.

Lattice dynamics and thermomechanical properties of zirconium(IV) chloride: Evidence for low-temperature negative thermal expansion

NASA Astrophysics Data System (ADS)

Kim, Eunja; Weck, Philippe F.; Borjas, Rosendo; Poineau, Frederic

2018-01-01

The crystal structure, lattice dynamics and themomechanical properties of bulk monoclinic zirconium tetrachloride (ZrCl4) have been investigated using zero-damping dispersion-corrected density functional theory [DFT-D3(zero)]. Phonon analysis reveals that ZrCl4 (cr) undergoes negative thermal expansion (NTE) near T ≈ 10 K, with a coefficient of thermal expansion of α = - 1.2 ppm K-1 and a Grüneisen parameter of γ = - 1.1 . The bulk modulus is predicted to vary from K0 = 8.7 to 7.0 GPa in the temperature range 0-550 K. The isobaric molar heat capacity derived from phonon calculations within the quasi-harmonic approximation is in fair agreement with existing calorimetric data.

Numerical comparison of hydrogen desorption behaviors of metal hydride beds based on uranium and on zirconium-cobalt

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kyoung, S.; Yoo, H.; Ju, H.

2015-03-15

In this paper, the hydrogen delivery capabilities of uranium (U) and zirconium-cobalt (ZrCo) are compared quantitatively in order to find the optimum getter materials for tritium storage. A three-dimensional hydrogen desorption model is applied to two identically designed cylindrical beds with the different materials, and hydrogen desorption simulations are then conducted. The simulation results show superior hydrogen delivery performance and easier thermal management capability for the U bed. This detailed analysis of the hydrogen desorption behaviors of beds with U and ZrCo will help to identify the optimal bed material, bed design, and operating conditions for the storage and deliverymore » system in ITER. (authors)« less

Nanostructure multilayer dielectric materials for capacitors and insulators

DOEpatents

Barbee, Jr., Troy W.; Johnson, Gary W.

1998-04-21

A capacitor is formed of at least two metal conductors having a multilayer dielectric and opposite dielectric-conductor interface layers in between. The multilayer dielectric includes many alternating layers of amorphous zirconium oxide (ZrO.sub.2) and alumina (Al.sub.2 O.sub.3). The dielectric-conductor interface layers are engineered for increased voltage breakdown and extended service life. The local interfacial work function is increased to reduce charge injection and thus increase breakdown voltage. Proper material choices can prevent electrochemical reactions and diffusion between the conductor and dielectric. Physical vapor deposition is used to deposit the zirconium oxide (ZrO.sub.2) and alumina (Al.sub.2 O.sub.3) in alternating layers to form a nano-laminate.

Nanostructure multilayer dielectric materials for capacitors and insulators

DOEpatents

Barbee, T.W. Jr.; Johnson, G.W.

1998-04-21

A capacitor is formed of at least two metal conductors having a multilayer dielectric and opposite dielectric-conductor interface layers in between. The multilayer dielectric includes many alternating layers of amorphous zirconium oxide (ZrO{sub 2}) and alumina (Al{sub 2}O{sub 3}). The dielectric-conductor interface layers are engineered for increased voltage breakdown and extended service life. The local interfacial work function is increased to reduce charge injection and thus increase breakdown voltage. Proper material choices can prevent electrochemical reactions and diffusion between the conductor and dielectric. Physical vapor deposition is used to deposit the zirconium oxide (ZrO{sub 2}) and alumina (Al{sub 2}O{sub 3}) in alternating layers to form a nano-laminate. 1 fig.

Evolution of interphase and intergranular strain in zirconium-niobium alloys during deformation at room temperature

NASA Astrophysics Data System (ADS)

Cai, Song

Zr-2.5Nb is currently used for pressure tubes in the CANDU (CANada Deuterium Uranium) reactor. A complete understanding of the deformation mechanism of Zr-2.5Nb is important if we are to accurately predict the in-reactor performance of pressure tubes and guarantee normal operation of the reactors. This thesis is a first step in gaining such an understanding; the deformation mechanism of ZrNb alloys at room temperature has been evaluated through studying the effect of texture and microstructure on deformation. In-situ neutron diffraction was used to monitor the evolution of the lattice strain of individual grain families along both the loading and Poisson's directions and to track the development of interphase and intergranular strains during deformation. The following experiments were carried out with data interpreted using elasto-plastic modeling techniques: (1) Compression tests of a 100%betaZr material at room temperature. (2) Tension and compression tests of hot rolled Zr-2.5Nb plate material. (3) Compression of annealed Zr-2.5Nb. (4) Cyclic loading of the hot rolled Zr-2.5Nb. (5) Compression tests of ZrNb alloys with different Nb and oxygen contents. The experimental results were interpreted using a combination of finite element (FE) and elasto-plastic self-consistent (EPSC) models. The phase properties and phase interactions well represented by the FE model, the EPSC model successfully captured the evolution of intergranular constraint during deformation and provided reasonable estimates of the critical resolved shear stress and hardening parameters of different slip systems under different conditions. The consistency of the material parameters obtained by the EPSC model allows the deformation mechanism at room temperature and the effect of textures and microstructures of ZrNb alloys to be understood. This work provides useful information towards manufacturing of Zr-2.5Nb components and helps in producing ideal microstructures and material properties for pressure tubes. Also it is helpful in guiding the development of new materials for the next generation of nuclear reactors. Furthermore, the large data set obtained from this study can be used in evaluation and improving current and future polycrystalline deformation models.

Comparison of Zirconium Phosphonate-Modified Surfaces for Immobilizing Phosphopeptides and Phosphate-Tagged Proteins.

PubMed

Forato, Florian; Liu, Hao; Benoit, Roland; Fayon, Franck; Charlier, Cathy; Fateh, Amina; Defontaine, Alain; Tellier, Charles; Talham, Daniel R; Queffélec, Clémence; Bujoli, Bruno

2016-06-07

Different routes for preparing zirconium phosphonate-modified surfaces for immobilizing biomolecular probes are compared. Two chemical-modification approaches were explored to form self-assembled monolayers on commercially available primary amine-functionalized slides, and the resulting surfaces were compared to well-characterized zirconium phosphonate monolayer-modified supports prepared using Langmuir-Blodgett methods. When using POCl3 as the amine phosphorylating agent followed by treatment with zirconyl chloride, the result was not a zirconium-phosphonate monolayer, as commonly assumed in the literature, but rather the process gives adsorbed zirconium oxide/hydroxide species and to a lower extent adsorbed zirconium phosphate and/or phosphonate. Reactions giving rise to these products were modeled in homogeneous-phase studies. Nevertheless, each of the three modified surfaces effectively immobilized phosphopeptides and phosphopeptide tags fused to an affinity protein. Unexpectedly, the zirconium oxide/hydroxide modified surface, formed by treating the amine-coated slides with POCl3/Zr(4+), afforded better immobilization of the peptides and proteins and efficient capture of their targets.

The impact of thermal treatment conditions on the formation of crystalline structure of Ce-Zr-oxide composite obtained by a modified sol-gel technique

NASA Astrophysics Data System (ADS)

Trusova, E. A.; Khrushcheva, A. A.; Shvorneva, L. I.

2012-02-01

We present the results of the modified sol-gel synthesis of ultrafine ceria-doped zirconia powder for medical ceramics (implants) and catalytic purposes (environmental catalysis and petrochemistry). Special attention has been paid to study the influence of thermal treatment on crystallite size and crystal lattice parameters of zirconia doped by ceria. Zirconyl chloride and cerium nitrate were used as metal sources, and tetraethylammonium hydroxide (TEAH) was used as a sol stabilizer at molar ratio TEAH/Σ (Ce + Zr) equal to 0.5. It was proved that zirconium and cerium practically completely were included in the obtained solid solutions, since their phase compositions fully correspond to initial quantities of cerium and zirconium in reaction mixture. It was shown that average crystallite size of the obtained powders did not exceed 75Å, and the powders were resistant to thermal treatment. It was established that stabilization of the crystal lattice of ZrO2 occurs through formation of a cubic ceria sublattice.

Electrical conductivity of KAlCl4-ZrCl4 molten mixtures

NASA Astrophysics Data System (ADS)

Salyulev, A. B.; Khokhlov, V. A.; Moskalenko, N. I.

2017-02-01

The electrical conductivity of commercially challenging KAlCl4-ZrCl4 molten mixtures has been studied as a function of temperature (in the range from 345°C to 500°C) and the ZrCl4 concentration (0‒32.5mol %) using cells of a unique design. It is found to vary in the range from 0.41 to 0.80 S cm-1, increasing with temperature or when the mole concentration of zirconium tetrachloride in molten mixtures decreases.

Biocompatible Zr-Al-Fe bulk metallic glasses with large plasticity

NASA Astrophysics Data System (ADS)

Hua, NengBin; Li, Ran; Wang, JianFeng; Zhang, Tao

2012-09-01

In the present study, high-zirconium ternary Zr-Al-Fe bulk metallic glasses (BMGs) with low Young's modulus and good plasticity were developed. Zr75Al7.5Fe17.5 BMG exhibits a low Young's modulus of 70 GPa and high Poisson's ratio of 0.403. Pronounced plasticity was demonstrated under both compression and bending conditions for the BMGs. Furthermore, the alloys show high corrosion resistance in phosphate buffered solution. The combination of desirable mechanical and chemical properties implies potential for biomedical applications.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abayli, D., E-mail: abayli@itu.edu.tr; Baydogan, N., E-mail: dogannil@itu.edu.tr

In this study, zirconium oxide (ZrO{sub 2}) thin film samples prepared by sol–gel method were irradiated using Co-60 radioisotope as gamma source. Then, it was investigated the ionizing effect on optical properties of ZrO{sub 2} thin film samples with the rise of the absorbed dose. The changes in the optical absorbance of ZrO{sub 2} thin films were determined by using optical transmittance and the reflectance measurements in the range between 190 – 1100 nm obtained from PG Instruments T80 UV-Vis spectrophotometer.

Spark plasma sintering of silicon carbide, multi-walled carbon nanotube and graphene reinforced zirconium diboride ceramic composite

NASA Astrophysics Data System (ADS)

Balaraman Yadhukulakrishnan, Govindaraajan

Scope and Method of Study: Space vehicles re-entering the earth's atmosphere experience very high temperatures due to aerodynamic heating. Ultra-high temperature ceramics (UHTC) with melting point higher than 3200°C are promising materials for thermal protection systems of such space vehicles re-entering the earth's atmosphere. Among several UHTC systems ZrB2 based ceramic composites are particularly important for thermal protection systems due to their better mechanical and thermoelectric properties and high oxidation resistance. In this study spark plasma sintering of SiC, carbon nanotubes (CNT) and graphene nano platelets (GNP) reinforced ZrB2 ultra-high temperature ceramic matrix composites is reported. Findings and Conclusions: Systematic investigations on the effect of reinforcement type (SiC, CNTs and GNP) and content (10-40 vol.% SiC, 2-6 vol.% CNTs and 2-6 vol.% GNP) on densification behavior, microstructure development, and mechanical properties (microhardness, bi-axial flexural strength, and indentation fracture toughness) are reported. With the similar SPS parameters near-full densification (>99% relative density) was achieved with 10-40 vol.% SiC, 4-6 vol.% CNT reinforced composites. Highly dense composites were obtained in 4-6 vol.% GNP reinforced composites. The SiC, CNT and GNP reinforcement improved the indentation fracture toughness of the composites through a range of toughening mechanisms, including particle shearing, crack deflection at the particle-matrix interface, and grain pull-outs for ZrB2-SiC composites, CNT pull-outs and crack deflection in ZrB2-CNT composites and crack deflection, crack bridging and GNP sheet pull-out for ZrB2 -GNP composites.

Manufacturing process to reduce large grain growth in zirconium alloys

DOEpatents

Rosecrans, Peter M.

1987-01-01

A method of treating cold-worked zirconium alloys to reduce large grain gth during thermal treatment at temperatures above the recrystallization temperature of the alloy comprising heating the cold-worked alloy between about 1300.degree.-1350.degree. F. for 1 to 3 hours prior to treatment above its recrystallization temperature.

Resistive switching mechanism of Ag/ZrO2:Cu/Pt memory cell

NASA Astrophysics Data System (ADS)

Long, Shibing; Liu, Qi; Lv, Hangbing; Li, Yingtao; Wang, Yan; Zhang, Sen; Lian, Wentai; Zhang, Kangwei; Wang, Ming; Xie, Hongwei; Liu, Ming

2011-03-01

Resistive switching mechanism of zirconium oxide-based resistive random access memory (RRAM) devices composed of Cu-doped ZrO2 film sandwiched between an oxidizable electrode and an inert electrode was investigated. The Ag/ZrO2:Cu/Pt RRAM devices with crosspoint structure fabricated by e-beam evaporation and e-beam lithography show reproducible bipolar resistive switching. The linear I- V relationship of low resistance state (LRS) and the dependence of LRS resistance ( R ON) and reset current ( I reset) on the set current compliance ( I comp) indicate that the observed resistive switching characteristics of the Ag/ZrO2:Cu/Pt device should be ascribed to the formation and annihilation of localized conductive filaments (CFs). The physical origin of CF was further analyzed by transmission electron microscopy (TEM) and energy dispersive X-ray spectroscopy (EDS). CFs were directly observed by cross-sectional TEM. According to EDS and elemental mapping analysis, the main chemical composition of CF is determined by Ag atoms, coming from the Ag top electrode. On the basis of these experiments, we propose that the set and reset process of the device stem from the electrochemical reactions in the zirconium oxide under different external electrical stimuli.

Influence of growth temperature on properties of zirconium dioxide films grown by atomic layer deposition

NASA Astrophysics Data System (ADS)

Kukli, Kaupo; Ritala, Mikko; Aarik, Jaan; Uustare, Teet; Leskela, Markku

2002-08-01

ZrO2 films were grown by atomic layer deposition from ZrCl4 and H2O or a mixture of H2O and H2O2 on Si(100) substrates in the temperature range of 180-600 degC. The films were evaluated in the as-deposited state, in order to follow the effect of deposition temperature on the film quality. The rate of crystal growth increased and the content of residual impurities decreased with increasing temperature. The zirconium-to-oxygen atomic ratio, determined by ion-beam analysis, corresponded to the stoichiometric dioxide regardless of the growth temperature. The effective permittivity of ZrO2 in Al/ZrO2/Si capacitor structures increased from 13-15 in the films grown at 180 degC to 19 in the films grown at 300-600 degC, measured at 100 kHz. The permittivity was relatively high in the crystallized films, compared to the amorphous ones, but rather insensitive to the crystal structure. The permittivity was higher in the films grown using water. The leakage current density tended to be lower and the breakdown field higher in the films grown using hydrogen peroxide.

Oxygen mobility in CeO{sub 2} and Ce{sub x}Zr({sub 1-x})O{sub 2} compounds: Study by CO transient oxidation and {sup 18}O/{sup 16}O isotopic exchange

DOE Office of Scientific and Technical Information (OSTI.GOV)

Madier, Y.; Descorme, C.; Govic, A.M. Le

Cerium-zirconium mixed oxides (Ce{sub x}Zr{sub 1{minus}x}O{sub 2}), precalcined at 900 C in dry air, were supplied by Rhodia Terres Rares as monophasic solid solutions. Introduction of some zirconium atoms in the ceria lattice by isomorphous substitution clearly influences the final properties of these materials as long as the cubic structure of ceria is maintained. Modifications in oxygen storage capacity (OSC measurements), redox properties (CO TPR), and oxygen exchange processes (TPIE) were studied. Ce{sub 0.63}Zr{sub 0.37}O{sub 2} was shown to have the most promising properties with the largest OSC at 400 C and the highest reactivity in O{sub 2} exchange. Allmore » mixed oxides are able to exchange very large amounts of oxygen compared to ceria, implying the participation of bulk oxygen. Furthermore, on Ce{sub x}Zr{sub (1{minus}x)}O{sub 2} samples, oxygen is predominantly exchanged via a multiple heteroexchange mechanism involving surface dioxygen species as superoxides or peroxides.« less

A novel mesoporous sulfated zirconium solid acid catalyst for Friedel-Crafts benzylation reaction

NASA Astrophysics Data System (ADS)

Miao, Zhichao; Zhou, Jin; Zhao, Jinping; Liu, Dandan; Bi, Xu; Chou, Lingjun; Zhuo, Shuping

2017-07-01

In this paper, a novel mesoporous sulfated zirconium (M-ZrO2/SO42-) has been gotten by one-pot evaporation-induced self-assembly (one-pot EISA) strategy. The SXRD, N2-physisorption and TEM characterization techniques indicated that M-ZrO2/SO42- possessed distinct mesostructure with big specific surface area (133.5 m2 g-1), large pore volume (0.18 cm3 g-1) and narrow pore size distribution (4.90 nm). Moreover, the existing states and the influence in mesostructure of introduced S species were detailedly investigated by the XRD, N2-physisorption, TEM, TG-DSC, FT-IR and XPS techniques and the results showed that the S species, which existed as the type of SO42-, improved the textural properties of prepared materials. In addition, the NH3-TPD and IR spectra of adsorbed pyridine indicated the existence of strong Brønsted and Lewis acid sites in M-ZrO2/SO42- even evacuated at 400 °C. Furthermore, the M-ZrO2/SO42- was used as a promise solid acid catalyst and displayed excellent catalytic performance and reusability in Friedel-Crafts benzylation reaction.

Photocatalytic activity against azo dye and cytotoxicity on MCF-7 cell lines of zirconium oxide nanoparticle mediated using leaves of Lagerstroemia speciosa.

PubMed

Sai Saraswathi, V; Santhakumar, K

2017-04-01

Metal oxide nanoparticles are gaining interest in recent years. The present paper explains about the green synthesis of zirconium oxide nanoparticles (ZrO NPs) mediated from the leaves of Lagerstroemia speciosa. The prepared ZrO NPs were characterized by UV-vis spectroscopy, FT-IR, X-ray diffraction analysis (XRD), Transmission Electron Microscopy (TEM), Scanning Electron Microscopy (SEM), Energy Dispersive X-ray spectroscopy (EDX) and Thermogravimetric Analysis (TGA). The photocatalytic activity of ZrO NPs was studied for azo dye by exposing to sunlight. The azo dye was degraded up to 94.58%. Also the ZrO NPs were studied for in vitro cytotoxicity activity against breast cancer cell lines-MCF-7 and evaluated by MTT assay. The cell morphological changes were recorded by light microscope. The cells viability was seen at 500μg/mL when compared against control. Hence the research highlights, that the method was simple, eco-friendly towards environment by phytoremediation activity of the azo dye and cytotoxicity activity against MCF-7 cell lines. Hence the present paper may help to further explore the metal nanoparticle for its potential applications. Copyright © 2017 Elsevier B.V. All rights reserved.

Effect of chloride incorporation on the crystallization of zirconium-barium-lanthanum-aluminum fluoride glass

NASA Technical Reports Server (NTRS)

Neilson, G. F.; Smith, G. L.; Weinberg, M. C.

1985-01-01

One aspect of the influence of preparation procedure on the crystallization behavior of a zirconium-barium-lanthanum-aluminum fluoride glass was studied. The crystallization pattern of this glass may be affected by the chlorine concentration within it. In particular, when such glasses are heated at low temperatures, the alpha-Ba-Zr-F6 crystalline phase forms only in those glasses which contain chloride.

Bioavailability of Lead in Small Arms Range Soils

DTIC Science & Technology

2009-08-01

titanium TOC total organic carbon USEPA U.S. Environmental Protection Agency XRF X-ray fluorescence Zn zinc Zr zirconium 1 1.0 EXECUTIVE...particles of inert matrix such as rock or slag of variable size, shape, and association; these chemical and physical properties may influence the absorption...zirconium, Pb=lead, Cu=copper, Mn=manganese, Si=silicon, Zn= zinc , As=arsenic, Cd=cadmium, CEC= cation exchange capacity, TOC = total organic carbon, Sb

Spectroscopic, thermal, quantum chemical calculations and in vitro biological studies of titanium/zirconium(IV) complexes of mono-and disubstituted aryldithiocarbonates

NASA Astrophysics Data System (ADS)

Andotra, Savit; Kumar, Sandeep; Kour, Mandeep; Kalgotra, Nidhi; Vikas; Chayawan; Pandey, Sushil K.

2018-03-01

Aryldithiocarbonates of titanium(IV) and zirconium(IV) corresponding to [(ROCS2)2MCl2] (R = o-, m- or p-CH3C6H4 and 4-Cl-3-CH3C6H3; M = Ti or Zr) have been isolated by the reaction of sodium salt of dithiocarbonates with titanium or zirconium tetrachloride in 1:2 M ratio in CHCl3. Donor stabilized addition complexes of titanium/zirconium with aryldithiocarbonates were also successfully isolated in chloroform. These have been characterized by elemental analyses, IR, mass, TGA/DTA, SEM and heteronuclear NMR (1H, 13C and 31P) spectroscopic studies. The antimicrobial test of these complexes has also been conducted against the bacteria Klebsiella pneumonia and Enterococcus faciolus and fungus Fusarium oxysporium, which indicate potential antimicrobial activity. In addition, the antioxidant activities of the complexes were also investigated through their scavenging effect on DPPH radicals. Density Functional Theory (DFT) calculations have been carried out to investigate geometry parameters of the complexes using B3LYP method and LANL2DZ basis set. HOMO (Highest Occupied Molecular Orbital), LUMO (Lowest Unoccupied Molecular Orbital) energies are analyzed. Based on analytical and theoretical results, a hexacoordinate geometry is concluded around the Ti or Zr atom.

Preparation of Aluminum-Zirconium Master Alloy by Aluminothermic Reduction in Cryolite Melt

NASA Astrophysics Data System (ADS)

Liu, Fengguo; Ding, Chenliang; Tao, Wenju; Hu, Xianwei; Gao, Bingliang; Shi, Zhongning; Wang, Zhaowen

2017-12-01

Al-Zr master alloy was prepared by aluminothermic reduction in cryolite melt without alumina impurity. The Al-Zr master alloy was characterized by x-ray diffraction, scanning electron microscopy, and energy-dispersive spectroscopy. The composition of the master alloy was analyzed by inductively coupled plasma optical emission spectrometry. The results indicated that Al-Zr master alloy with high purity could be obtained when byproduct Al2O3 was dissolved in the cryolite melt. The Al-Zr alloy was embedded in the Al matrix in the form of Al3Zr phase with long rod or tetragonal morphology due to temperature variation. Finally, we obtained Al-Zr alloy with 7 wt.% Zr by aluminothermic reduction for 90 min in cryolite melt at 980°C.

DEVELOPMENT OF PLASTICITY MODEL USING NON ASSOCIATED FLOW RULE FOR HCP MATERIALS INCLUDING ZIRCONIUM FOR NUCLEAR APPLICATIONS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Michael V. Glazoff; Jeong-Whan Yoon

2013-08-01

In this report (prepared in collaboration with Prof. Jeong Whan Yoon, Deakin University, Melbourne, Australia) a research effort was made to develop a non associated flow rule for zirconium. Since Zr is a hexagonally close packed (hcp) material, it is impossible to describe its plastic response under arbitrary loading conditions with any associated flow rule (e.g. von Mises). As a result of strong tension compression asymmetry of the yield stress and anisotropy, zirconium displays plastic behavior that requires a more sophisticated approach. Consequently, a new general asymmetric yield function has been developed which accommodates mathematically the four directional anisotropies alongmore » 0 degrees, 45 degrees, 90 degrees, and biaxial, under tension and compression. Stress anisotropy has been completely decoupled from the r value by using non associated flow plasticity, where yield function and plastic potential have been treated separately to take care of stress and r value directionalities, respectively. This theoretical development has been verified using Zr alloys at room temperature as an example as these materials have very strong SD (Strength Differential) effect. The proposed yield function reasonably well models the evolution of yield surfaces for a zirconium clock rolled plate during in plane and through thickness compression. It has been found that this function can predict both tension and compression asymmetry mathematically without any numerical tolerance and shows the significant improvement compared to any reported functions. Finally, in the end of the report, a program of further research is outlined aimed at constructing tensorial relationships for the temperature and fluence dependent creep surfaces for Zr, Zircaloy 2, and Zircaloy 4.« less

Efficient mass-selective three-photon ionization of zirconium atoms

DOEpatents

Page, R.H.

1994-12-27

In an AVLIS process, [sup 91]Zr is selectively removed from natural zirconium by a three-step photoionization wherein Zr atoms are irradiated by a laser beam having a wavelength [lambda][sub 1], selectively raising [sup 91]Zr atoms to an odd-parity E[sub 1] energy level in the range of 16000--19000 cm[sup [minus]1], are irradiated by a laser beam having a wavelength [lambda][sub 2] to raise the atoms from an E[sub l] level to an even-parity E[sub 2] energy level in the range of 35000--37000 cm[sup [minus]1] and are irradiated by a laser beam having a wavelength [lambda][sub 3] to cause a resonant transition of atoms from an E[sub 2] level to an autoionizing level above 53506 cm[sup [minus]1][lambda][sub 3] wavelengths of 5607, 6511 or 5756 [angstrom] will excite a zirconium atom from an E[sub 2] energy state of 36344 cm[sup [minus]1] to an autoionizing level; a [lambda][sub 3] wavelength of 5666 [angstrom] will cause an autoionizing transition from an E[sub 2] level of 36068 cm[sup [minus]1]; and a [lambda][sub 3] wavelength of 5662 [angstrom] will cause an ionizing resonance of an atom at an E[sub 2] level of 35904 cm[sup [minus]1]. 4 figures.

A novel ultrasonication method in the preparation of zirconium impregnated cellulose for effective fluoride adsorption.

PubMed

Barathi, M; Kumar, A Santhana Krishna; Rajesh, N

2014-05-01

In the present work, we propose for the first time a novel ultrasound assisted methodology involving the impregnation of zirconium in a cellulose matrix. Fluoride from aqueous solution interacts with the cellulose hydroxyl groups and the cationic zirconium hydroxide. Ultrasonication ensures a green and quick alternative to the conventional time intensive method of preparation. The effectiveness of this process was confirmed by comprehensive characterization of zirconium impregnated cellulose (ZrIC) adsorbent using Fourier transform infrared spectroscopy (FT-IR), energy dispersive X-ray spectrometry (EDX) and X-ray diffraction (XRD) studies. The study of various adsorption isotherm models, kinetics and thermodynamics of the interaction validated the method. Copyright © 2013 Elsevier B.V. All rights reserved.

Effective dose to immuno-PET patients due to metastable impurities in cyclotron produced zirconium-89

NASA Astrophysics Data System (ADS)

Alfuraih, Abdulrahman; Alzimami, Khalid; Ma, Andy K.; Alghamdi, Ali; Al Jammaz, Ibrahim

2014-11-01

Immuno-PET is a nuclear medicine technique that combines positron emission tommography (PET) with radio-labeled monoclonal antibodies (mAbs) for tumor characterization and therapy. Zirconium-89 (89Zr) is an emerging radionuclide for immuno-PET imaging. Its long half-life (78.4 h) gives ample time for the production, the administering and the patient uptake of the tagged radiopharmaceutical. Furthermore, the nuclides will remain in the tumor cells after the mAbs are catabolized so that time series studies are possible without incurring further administration of radiopharmarceuticals. 89Zr can be produced in medical cyclotrons by bombarding an yttrium-89 (89Y) target with a proton beam through the 89Y(p,n)89Zr reaction. In this study, we estimated the effective dose to the head and neck cancer patients undergoing 89Zr-based immune-PET procedures. The production of 89Zr and the impurities from proton irradiation of the 89Y target in a cyclotron was calculated with the Monte Carlo code MCNPX and the nuclear reaction code TALYS. The cumulated activities of the Zr isotopes were derived from real patient data in literature and the effective doses were estimated using the MIRD specific absorbed fraction formalism. The estimated effective dose from 89Zr is 0.5±0.2 mSv/MBq. The highest organ dose is 1.8±0.2 mSv/MBq in the liver. These values are in agreement with those reported in literature. The effective dose from 89mZr is about 0.2-0.3% of the 89Zr dose in the worst case. Since the ratio of 89mZr to 89Zr depends on the cooling time as well as the irradiation details, contaminant dose estimation is an important aspect in optimizing the cyclotron irradiation geometry, energy and time.

Performance assessment of femoral knee components made from cobalt-chromium alloy and oxidized zirconium.

PubMed

Brandt, J-M; Guenther, L; O'Brien, S; Vecherya, A; Turgeon, T R; Bohm, E R

2013-12-01

The surface characteristics of the femoral component affect polyethylene wear in modular total knee replacements. In the present retrieval study, the surface characteristics of cobalt-chromium (CoCr) alloy and oxidized zirconium (OxZr) femoral components were assessed and compared. Twenty-six retrieved CoCr alloy femoral components were matched with twenty-six retrieved OxZr femoral components for implantation period, body-mass index, patient gender, implant type, and polyethylene insert thickness. The surface damage on the retrieved femoral components was evaluated using a semi-quantitative assessment method, scanning electron microscopy, and contact profilometry. The retrieved CoCr alloy femoral components showed less posterior surface gouging than OxZr femoral components; however, at a higher magnification, the grooving damage features on the retrieved CoCr alloy femoral components confirmed an abrasive wear mechanism. The surface roughness values Rp, Rpm, and Rpk for the retrieved CoCr alloy femoral components were found to be significantly higher than those of the retrieved OxZr femoral components (p≤0.031). The surface roughness values were higher on the medial condyles than on the lateral condyles of the retrieved CoCr alloy femoral components; such a difference was not observed on the retrieved OxZr femoral components. The surface roughness of CoCr alloy femoral components increased while the surface roughness of the OxZr femoral components remained unchanged after in vivo service. Therefore, the OxZr femoral components' resistance to abrasive wear may enable lower polyethylene wear and ensure long-term durability in vivo. Level IV. Crown Copyright © 2013. Published by Elsevier B.V. All rights reserved.

Fluoride glass starting materials - Characterization and effects of thermal treatment

NASA Technical Reports Server (NTRS)

Chen, William; Dunn, Bruce; Shlichta, Paul; Neilson, George F.; Weinberg, Michael C.

1987-01-01

The production of heavy metal fluoride (HMF) glasses, and the effects of thermal treatments on the HMF glasses are investigated. ZrF4, BaF2, AlF3, LaF3, and NaF were utilized in the synthesis of zirconium-barium-lanthanum-aluminum-sodium fluoride glass. The purity of these starting materials, in particular ZrF4, is evaluated using XRD analysis. The data reveal that low temperature heating of ZrF4-H2O is effective in removing the water of hydration, but causes the production of ZrF4 and oxyfluorides; however, dehydration followed by sublimation results in the production of monoclinic ZrFe without water or oxyfluoride contaminants.

Effects of Zr, Ti, and Al Additions on Nonmetallic Inclusions and Impact Toughness of Cast Low-Alloy Steel

NASA Astrophysics Data System (ADS)

Bizyukov, Pavel V.; Giese, Scott R.

2017-04-01

A microalloying of the low-carbon and low-alloy cast steel was conducted with Zr, Ti, and Al that were added to the steel in four combinations. After heat treatment, the samples were tested for impact toughness at room temperature using the Charpy method. The highest values of impact toughness were obtained in the group treated with Zr, while Zr-Ti and Zr-Ti-Al groups showed moderate toughness values; the lowest values were observed in the Zr-Al group. Difference among the treatment groups was observed in the fracture mechanisms, morphology, and area distribution of the inclusions. High toughness values achieved in the trials treated with zirconium corresponded with smooth ductile fracture. The metal treated with a combination of zirconium and titanium had a relatively small area occupied by inclusions, but its toughness was also moderate. Lowest impact toughness values corresponded with the larger area occupied by the inclusions in the trials treated with aluminum. Also, a connection between the solubility product [Al][N] and impact toughness was established. The study also provides a qualitative description and quantitative analysis of the nonmetallic inclusions formation as a result of microalloying treatment. The precipitation sequence of the inclusions was described based on the thermochemical calculations for the nonmetallic compounds discovered in the experimental steel. A description of the size distribution, morphology, and composition was conducted for the oxides, nitrides, sulfides, and multiphase particles.

Metaloxide--ZrO2 catalysts for the esterification and transesterification of free fatty acids and triglycerides to obtain bio-diesel

DOEpatents

Kim, Manhoe; Salley, Steven O.; Ng, K. Y. Simon

2016-09-06

Mixed metal oxide catalysts (ZnO, CeO, La2O3, NiO, Al203, SiO2, TiO2, Nd2O3, Yb2O3, or any combination of these) supported on zirconia (ZrO2) or hydrous zirconia are provided. These mixed metal oxide catalysts can be prepared via coprecipitation, impregnation, or sol-gel methods from metal salt precursors with/without a Zirconium salt precursor. Metal oxides/ZrO2 catalyzes both esterification and transesterification of oil containing free fatty acids in one batch or in single stage. In particular, these mixed metal oxides supported or added on zirconium oxide exhibit good activity and selectivity for esterification and transesterification. The low acid strength of this catalyst can avoid undesirable side reaction such as alcohol dehydration or cracking of fatty acids. Metal oxides/ZrO2 catalysts are not sensitive to any water generated from esterification. Thus, esterification does not require a water free condition or the presence of excess methanol to occur when using the mixed metal oxide catalyst. The FAME yield obtained with metal oxides/ZrO2 is higher than that obtained with homogeneous sulfuric acid catalyst. Metal oxides/ZrO2 catalasts can be prepared as strong pellets and in various shapes for use directly in a flow reactor. Furthermore, the pellet has a strong resistance toward dissolution to aqueous or oil phases.

Zirconium phosphatidylcholine-based nanocapsules as an in vivo degradable drug delivery system of MAP30, a momordica anti-HIV protein.

PubMed

Caizhen, Guo; Yan, Gao; Ronron, Chang; Lirong, Yang; Panpan, Chu; Xuemei, Hu; Yuanbiao, Qiao; Qingshan, Li

2015-04-10

An essential in vivo drug delivery system of a momordica anti-HIV protein, MAP30, was developed through encapsulating in chemically synthesized matrices of zirconium egg- and soy-phosphatidylcholines, abbreviated to Zr/EPC and Zr/SPC, respectively. Matrices were characterized by transmission electron microscopy and powder X-ray diffractometry studies. Zr/EPC granule at an approximate diameter of 69.43±7.78 nm was a less efficient encapsulator than the granule of Zr/SPC. Interlayer spacing of the matrices encapsulating MAP30 increased from 8.8 and 9.7 Å to 7.4 and 7.9 nm, respectively. In vivo kinetics on degradation and protein release was performed by analyzing the serum sampling of intravenously injected SPF chickens. The first order and biphasic variations were obtained for in vivo kinetics using equilibrium dialysis. Antimicrobial and anti-HIV assays yielded greatly decreased MIC50 and EC50 values of nanoformulated MAP30. An acute toxicity of MAP30 encapsulated in Zr/EPC occurred at a single intravenous dose above 14.24 mg/kg bw in NIH/KM/ICR mice. The folding of MAP30 from Zr/EPC sustained in vivo chickens for more than 8 days in high performance liquid chromatography assays. These matrices could protect MAP30 efficiently with strong structure retention, lowered toxicity and prolonged in vivo life. Copyright © 2015 Elsevier B.V. All rights reserved.

Bioactivity and cytocompatibility of zirconia (ZrO(2)) films fabricated by cathodic arc deposition.

PubMed

Liu, Xuanyong; Huang, Anping; Ding, Chuanxian; Chu, Paul K

2006-07-01

Zirconium oxide thin films were fabricated on silicon wafers using a filtered cathodic arc system in concert with oxygen plasma. The structure and phase composition of the zirconium oxide thin films were characterized by atomic force microscopy (AFM), X-ray diffraction (XRD), Rutherford backscattering spectrometry (RBS), and transmission electron microscopy (TEM). The bioactivity was assessed by investigating the formation of apatite on the film surface after soaking in simulated body fluids. Bone marrow mesenchymal stem cells (BMMSC) were used to further evaluate the cytocompatibility of the materials. The results indicate that the films are composed of stoichiometric ZrO(2) and the composition is quite uniform throughout the thickness. Bone-like apatite can be formed on the surface of the ZrO(2) thin film in our SBF immersion experiments, suggesting that the surface is bioactive. The outermost layer of the ZrO(2) thin film comprises nano-sized particles that can be identified by AFM images taken on the thin film surface and TEM micrographs obtained from the interface between the ZrO(2) thin film and apatite layer. The nanostructured surface is believed to be the key factor that apatite is induced to precipitate on the surface. Bone marrow mesenchymal stem cells are observed to grow and proliferate in good states on the film surface. Our results show that ZrO(2) thin films fabricated by cathodic arc deposition exhibit favorable bioactivity and cytocompatibility.

Understanding the Irradiation Behavior of Zirconium Carbide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Motta, Arthur; Sridharan, Kumar; Morgan, Dane

2013-10-11

Zirconium carbide (ZrC) is being considered for utilization in high-temperature gas-cooled reactor fuels in deep-burn TRISO fuel. Zirconium carbide possesses a cubic B1-type crystal structure with a high melting point, exceptional hardness, and good thermal and electrical conductivities. The use of ZrC as part of the TRISO fuel requires a thorough understanding of its irradiation response. However, the radiation effects on ZrC are still poorly understood. The majority of the existing research is focused on the radiation damage phenomena at higher temperatures (>450{degree}C) where many fundamental aspects of defect production and kinetics cannot be easily distinguished. Little is known aboutmore » basic defect formation, clustering, and evolution of ZrC under irradiation, although some atomistic simulation and phenomenological studies have been performed. Such detailed information is needed to construct a model describing the microstructural evolution in fast-neutron irradiated materials that will be of great technological importance for the development of ZrC-based fuel. The goal of the proposed project is to gain fundamental understanding of the radiation-induced defect formation in zirconium carbide and irradiation response by using a combination of state-of-the-art experimental methods and atomistic modeling. This project will combine (1) in situ ion irradiation at a specialized facility at a national laboratory, (2) controlled temperature proton irradiation on bulk samples, and (3) atomistic modeling to gain a fundamental understanding of defect formation in ZrC. The proposed project will cover the irradiation temperatures from cryogenic temperature to as high as 800{degree}C, and dose ranges from 0.1 to 100 dpa. The examination of this wide range of temperatures and doses allows us to obtain an experimental data set that can be effectively used to exercise and benchmark the computer calculations of defect properties. Combining the examination of radiation-induced microstructures mapped spatially and temporally, microstructural evolution during post-irradiation annealing, and atomistic modeling of defect formation and transport energetics will provide new, critical understanding about property changes in ZrC. The behavior of materials under irradiation is determined by the balance between damage production, defect clustering, and lattice response. In order to predict those effects at high temperatures so targeted testing can be expanded and extrapolated beyond the known database, it is necessary to determine the defect energetics and mobilities as these control damage accumulation and annealing. In particular, low-temperature irradiations are invaluable for determining the regions of defect mobility. Computer simulation techniques are particularly useful for identifying basic defect properties, especially if closely coupled with a well-constructed and complete experimental database. The close coupling of calculation and experiment in this project will provide mutual benchmarking and allow us to glean a deeper understanding of the irradiation response of ZrC, which can then be applied to the prediction of its behavior in reactor conditions.« less

Fabrication and characterization of carboxymethyl cellulose novel microparticles for bone tissue engineering.

PubMed

Gaihre, Bipin; Jayasuriya, Ambalangodage C

2016-12-01

In this study we developed carboxymethyl cellulose (CMC) microparticles through ionic crosslinking with the aqueous ion complex of zirconium (Zr) and further complexing with chitosan (CS) and determined the physio-chemical and biological properties of these novel microparticles. In order to assess the role of Zr, microparticles were prepared in 5% and 10% (w/v) zirconium tetrachloride solution. Scanning electron microscopy (SEM) with energy dispersive X-ray spectrometer (EDS) results showed that Zr was uniformly distributed on the surface of the microparticles as a result of which uniform groovy surface was obtained. We found that Zr enhances the surface roughness of the microparticles and stability studies showed that it also increases the stability of microparticles in phosphate buffered saline. The crosslinking of anionic CMC with cationic Zr and CS was confirmed by Fourier transform infrared spectroscopy (FTIR) results. The response of murine pre-osteoblasts (OB-6) when cultured with microparticles was investigated. Live/dead cell assay showed that microparticles did not induce any cytotoxic effects as cells were attaching and proliferating on the well plate as well as along the surface of microparticles. In addition, SEM images showed that microparticles support the attachment of cells and they appeared to be directly interacting with the surface of microparticle. Within 10days of culture most of the top surface of microparticles was covered with a layer of cells indicating that they were proliferating well throughout the surface of microparticles. We observed that Zr enhances the cell attachment and proliferation as more cells were present on microparticles with 10% Zr. These promising results show the potential applications of CMC-Zr microparticles in bone tissue engineering. Copyright © 2016 Elsevier B.V. All rights reserved.

Differences in the calcification of preosteoblast cultured on sputter-deposited titanium, zirconium, and gold.

PubMed

Chen, Peng; Nagai, Akiko; Tsutsumi, Yusuke; Ashida, Maki; Doi, Hisashi; Hanawa, Takao

2016-03-01

In this study, osteogenic differentiation and calcification of preosteoblast (MC3T3-E1) cultured on sputter-deposited titanium (Ti), zirconium (Zr), and gold (Au) on cover glasses were evaluated to understand the differences in bone formation ability among these three metals; these metals show the same high corrosion resistance, but Ti and Zr are covered by surface passive oxide film while Au is not covered by the oxide film. Ti and Zr promoted cellular proliferation without osteogenic differentiation. Cells cultured on Ti and Zr expressed higher levels of Runx2, Col1α1, and Akp2 at an earlier stage, which indicated faster promotion of osteogenic differentiation, as compared to those cultured on Au. Moreover, after 21 days of culture, the Bglap1 and Ifitm5 expression peaks in cells cultured on Ti and Zr were higher than those in cells cultured on Au, which indicated faster promotion of calcification. Cells cultured on Ti showed an advantage in osteogenic differentiation at an early stage, while cells on Zr showed better calcification promotion with a long-term culture. The amount of extracellular calcified deposits was in good agreement with the gene expression results. On the other hand, the intracellular calcium content of cells on Au specimens was higher than that of cells on Ti and Zr specimens. The results indicate that preosteoblasts on Ti and Zr showed faster osteogenic differentiation and calcification than those on Au, whereas Au improved the intracellular calcium content. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 639-651, 2016. © 2015 Wiley Periodicals, Inc.

In situ electrochemical synthesis of highly loaded zirconium nanoparticles decorated reduced graphene oxide for the selective determination of dopamine and paracetamol in presence of ascorbic acid.

PubMed

Ezhil Vilian, A T; Rajkumar, Muniyandi; Chen, Shen-Ming

2014-03-01

Highly loaded zirconium oxide (ZrO2) nanoparticles were supported on graphene oxide (ERGO/ZrO2) via an in situ, simple and clean strategy on the basis of the electrochemical redox reaction between zirconyl chloride and graphene oxide (ZrOCl2 and GO). The electrochemical measurements and surface morphology of the as prepared nanocomposite were studied using cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS) and field emission scanning electron microscopy (FESEM). This ZrO2 decorated reduced graphene oxide nanocomposite modified GCE (ERGO/ZrO2) exhibits a prominent electrocatalytic activity toward the selective detection and determination of dopamine (DA) and paracetamol (PA) in presence of ascorbic acid (AA). The peaks of linear sweep voltammetry (LSV) for DA and PA oxidation at ERGO/ZrO2 modified electrode surface were clearly separated from each other when they co-existed in the physiological pH (pH 7.0) with a potential value of 140 mV (between AA and DA) and 330 mV (between AA and PA). It was, therefore, possible to simultaneously determine DA and PA in the samples at ERGO/ZrO2 nanocomposite modified GCE. Linear calibration curves were obtained for 9-237 μM of PA and DA. The ERGO/ZrO2 nanocomposite electrode has been satisfactorily used for the determination of DA and PA in the presence of AA at pharmaceutical formulations in human urine samples with a linear range of 3-174 μM. The proposed biosensor shows a wide linear range, low detection limit, good reproducibility and acceptable stability, providing a biocompatible platform for bio sensing and bio catalysis. Copyright © 2013 Elsevier B.V. All rights reserved.

Predicting the solid state phase diagram for glass-forming alloys of copper and zirconium

NASA Astrophysics Data System (ADS)

Tang, C.; Harrowell, Peter

2012-06-01

The free energies of six crystal structures associated with Cu-Zr alloys—Cu (face centred cubic), Cu2Zr, Cu10Zr7, CuZr, CuZr2 and Zr (hexagonal close packed)—are calculated using the embedded atom potential of Mendelev et al (2009 Phil. Mag. 89 967). We find that the observed low temperature stability of the Cu10Zr7 and CuZr2 phases is not reproduced. Instead, the model predicts that the CuZr phase remains stable down to T = 0 K. This discrepancy is largely removed when the interaction potentials are cut off at a short distance, such as that used by Duan et al (2005 Phys. Rev. B 71 224208). We present evidence, however, that the cut-off distance necessary to achieve the change in phase stability results in pathological artefacts in the energetics of some crystal phases.

Lattice dynamics and thermomechanical properties of zirconium(IV) chloride: Evidence for low-temperature negative thermal expansion

DOE PAGES

Kim, Eunja; Weck, Philippe F.; Borjas, Rosendo; ...

2017-11-01

For this research, the crystal structure, lattice dynamics and themomechanical properties of bulk monoclinic zirconium tetrachloride (ZrCl 4) have been investigated using zero-damping dispersion-corrected density functional theory [DFT-D3(zero)]. Phonon analysis reveals that ZrCl 4(cr) undergoes negative thermal expansion (NTE) near T≈10 K, with a coefficient of thermal expansion of α=-1.2 ppm K -1 and a Grüneisen parameter of γ=-1.1. The bulk modulus is predicted to vary from K 0=8.7 to 7.0 GPa in the temperature range 0–550 K. Lastly, the isobaric molar heat capacity derived from phonon calculations within the quasi-harmonic approximation is in fair agreement with existing calorimetric data.

Lattice dynamics and thermomechanical properties of zirconium(IV) chloride: Evidence for low-temperature negative thermal expansion

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Eunja; Weck, Philippe F.; Borjas, Rosendo

For this research, the crystal structure, lattice dynamics and themomechanical properties of bulk monoclinic zirconium tetrachloride (ZrCl 4) have been investigated using zero-damping dispersion-corrected density functional theory [DFT-D3(zero)]. Phonon analysis reveals that ZrCl 4(cr) undergoes negative thermal expansion (NTE) near T≈10 K, with a coefficient of thermal expansion of α=-1.2 ppm K -1 and a Grüneisen parameter of γ=-1.1. The bulk modulus is predicted to vary from K 0=8.7 to 7.0 GPa in the temperature range 0–550 K. Lastly, the isobaric molar heat capacity derived from phonon calculations within the quasi-harmonic approximation is in fair agreement with existing calorimetric data.

Highly effective removal of heavy metals by polymer-based zirconium phosphate: a case study of lead ion.

PubMed

Pan, B C; Zhang, Q R; Zhang, W M; Pan, B J; Du, W; Lv, L; Zhang, Q J; Xu, Z W; Zhang, Q X

2007-06-01

Zirconium phosphate (ZrP) has recently been demonstrated as an excellent sorbent for heavy metals due to its high selectivity, high thermal stability, and absolute insolubility in water. However, it cannot be readily adopted in fixed beds or any other flowthrough system due to the excessive pressure drop and poor mechanical strength resulting from its fine submicrometer particle sizes. In the present study a hybrid sorbent, i.e., polymer-supported ZrP, was prepared by dispersing ZrP within a strongly acidic cation exchanger D-001 and used for enhanced lead removal from contaminated waters. D-001 was selected as a host material for sorbent preparation mainly because of the Donnan membrane effect resulting from the nondiffusible negatively charged sulfonic acid group on the exchanger surface, which would enhance permeation of the targeted metal ions. The hybrid sorbent (hereafter denoted ZrP-001) was characterized using a nitrogen adsorption technique, scanning electron microscope (SEM), and X-ray diffraction (XRD). Lead sorption onto ZrP-001 was found to be pH dependent due to the ion-exchange mechanism, and its sorption kinetics onto ZrP-001 followed the pseudo-first-order model. Compared to D-001, ZrP-001 exhibited more favorable lead sorption particularly in terms of high selectivity, as indicated by its substantially larger distribution coefficients when other competing cations Na(+), Ca(2+), and Mg(2+) coexisted at a high level in solution. Fixed-bed column runs showed that lead sorption on ZrP-001 resulted in a conspicuous decrease of this toxic metal from 40 mg/L to below 0.05 mg/L. By comparison with D-001 and ZrP-CP (ZrP dispersion within a neutrally charged polymer CP), enhanced removal efficiency of ZrP-001 resulted from the Donnan membrane effect of the host material D-001. Moreover, its feasible regeneration by diluted acid solution and negligible ZrP loss during operation also helps ZrP-001 to be a potential candidate for lead removal from water. Thus, all the results suggested that ZrP-001 offers excellent potential for lead removal from contaminated water.

Oxygen partial pressure influenced structural and optical properties of DC magnetron sputtered ZrO{sub 2} films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kondaiah, P.; Madhavi, V.; Uthanna, S.

2013-02-05

Thin films of zirconium oxide (ZrO{sub 2}) were deposited on (100) p-silicon and quartz substrates by sputtering of metallic zirconium target under different oxygen partial pressures in the range 8 Multiplication-Sign 10{sup -3}-6 Multiplication-Sign 10{sup -2}Pa. The effect of oxygen partial pressure on the structural and optical properties of the deposited films was systematically investigated. The deposition rate of the films decreased from 3.3 to 1.83 nm/min with the increase of oxygen partial pressure from 8 Multiplication-Sign 10{sup -3}-6 Multiplication-Sign 10{sup -2}Pa respectively. The X-ray diffraction profiles revealed that the films exhibit (111) refection of zirconium oxide in monoclinic phase.more » The optical band gap of the films increased from 5.62 to 5.80 eV and refractive index increased from 2.01 to 2.08 with the increase of oxygen partial pressure from 8 Multiplication-Sign 10{sup -3}-6 Multiplication-Sign 10{sup -2}Pa respectively.« less

Mineral potential tracts for shoreline Ti-Zr placer deposits (phase V, deliverable 85): Chapter P in Second projet de renforcement institutionnel du secteur minier de la République Islamique de Mauritanie (PRISM-II)

USGS Publications Warehouse

Beaudoin, Georges

2015-01-01

Shoreline placer Ti deposits are composed of ilmenite, rutile, zircon, monazite, and magnetite in well-sorted, fine- to medium-grained sand in coastal dunes, beaches and inlets. In addition to titanium, zirconium, in particular, and rare earth elements (REE) have become a major source of value in shoreline placer deposits. Shoreline placer deposits form mostly on tropical beaches around the world (fig. 1), and consist of dark sand layers rich in heavy minerals that are resistant to mechanical abrasion and chemical weathering. According to Hamilton (1995), shoreline placer deposits supply approximately 80 percent of the world’s rutile production, 25 percent of ilmenite, 100 percent of zircon, and 50 percent of both monazite and xenotime.

Effects of growth temperature on the properties of atomic layer deposition grown ZrO2 films

NASA Astrophysics Data System (ADS)

Scarel, G.; Ferrari, S.; Spiga, S.; Wiemer, C.; Tallarida, G.; Fanciulli, M.

2003-07-01

Zirconium dioxide films are grown in 200 atomic layer deposition cycles. Zirconium tetrachloride (ZrCl4) and water (H2O) are used as precursors. A relatively high dielectric constant (κ=22), wide band gap, and conduction band offset (5.8 and 1.4 eV, respectively) indicate that zirconium dioxide is a most promising substitute for silicon dioxide as a dielectric gate in complementary metal-oxide-semiconductor devices. However, crystallization and chlorine ions in the films might affect their electrical properties. These ions are produced during atomic layer deposition in which the ZrCl4 precursor reacts with the growth surface. It is desirable to tune the composition, morphology, and structural properties in order to improve their benefit on the electrical ones. To address this issue it is necessary to properly choose the growth parameters. This work focuses on the effects of the growth temperature Tg. ZrO2 films are grown at different substrate temperatures: 160, 200, 250, and 350 °C. Relevant modification of the film structure with a change in substrate temperature during growth is expected because the density of reactive sites [mainly Si+1-(OH)-1 bonds] decreases with an increase in temperature [Y. B. Kim et al., Electrochem. Solid-State Lett. 3, 346 (2000)]. The amorphous film component, for example, that develops at Si+1-(OH)-1 sites on the starting growth surface, is expected to decrease with an increase in growth temperature. The size and consequences of film property modifications with the growth temperature are investigated in this work using x-ray diffraction and reflectivity, and atomic force microscopy. Time of flight-secondary ion mass spectrometry is used to study contaminant species in the films. From capacitance-voltage (CV) and current-voltage (IV) measurements, respectively, the dielectric constant κZrO2 and the leakage current are studied as a function of the film growth temperature.

Response to antiseptic agents of periodontal pathogens in in vitro biofilms on titanium and zirconium surfaces.

PubMed

Sánchez, M C; Fernández, E; Llama-Palacios, A; Figuero, E; Herrera, D; Sanz, M

2017-04-01

The aim of this study was to develop in vitro biofilms on SLA titanium (Ti-SLA) and zirconium oxide (ZrO 2 ) surfaces and to evaluate the effect of antiseptic agents on the number of putative periodontal pathogenic species. An in vitro biofilm model was developed on sterile discs of Ti-SLA and ZrO 2 . Three antiseptic agents [chlorhexidine and cetyl-pyridinium-chloride (CHX/CPC), essential oils (EEOOs) and cetyl-peridinium-chloride (CPC)] were applied to 72-h biofilms, immersing discs during 1min in the antiseptic solution, either with or without mechanical disruption. Viable bacteria [colony forming units (CFU/mL)] were measured by quantitative polymerase chain reaction (qPCR) combined with propidium monoazide. A generalized lineal model was constructed to determine the effect of the agents on the viable bacterial counts of Aggregatibacter actinomycetemcomitans, Porphyromonas gingivalis and Fusobacterium nucleatum on each surface. The exposure to each antiseptic solution resulted in a statistically significant reductions in the number of viable target species included in the in vitro multi-species biofilm, on both Ti-SLA and ZrO 2 (p<0.001) which was of up to 2 orders for A. actinomycetemcomitans, for P. gingivalis 2 orders on Ti-SLA and up to 3 orders on ZrO 2, and, for F. nucleatum up to 4 orders. No significant differences were found in counts of the tested bacteria between in vitro biofilms formed on both Ti-SLA and ZrO 2 , after topically exposure to the antimicrobial agents whether the application was purely chemical or combined with mechanical disruption. A. actinomycetemcomitans, P. gingivalis and F. nucleatum responded similarly to their exposure to antiseptics when grown in multispecies biofilms on titanium and zirconium surfaces, in spite of the described structural differences between these bacterial communities. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Determination of the five parameter grain boundary character distribution of nanocrystalline alpha-zirconium thin films using transmission electron microscopy

DOE PAGES

Ghamarian, I.; Samani, P.; Rohrer, G. S.; ...

2017-03-24

Grain boundary engineering and other fundamental materials science problems (e.g., phase transformations and physical properties) require an improvement in the understanding of the type and population of grain boundaries in a given system – yet, databases are limited in number and spare in detail, including for hcp crystals such as zirconium. One way to rapidly obtain databases to analyze is to use small-grained materials and high spatial resolution orientation microscopy techniques, such as ASTAR™/precession electron diffraction. To demonstrate this, a study of grain boundary character distributions was conducted for α-zirconium deposited at room temperature on fused silica substrates using physicalmore » vapor deposition. The orientation maps of the nanocrystalline thin films were acquired by the ASTARα/precession electron diffraction technique, a new transmission electron microscope based orientation microscopy method. The reconstructed grain boundaries were classified as pure tilt, pure twist, 180°-twist and 180°-tilt grain boundaries based on the distribution of grain boundary planes with respect to the angle/axis of misorientation associated with grain boundaries. The results of the current study were compared to the results of a similar study on α-titanium and the molecular dynamics results of grain boundary energy for α-titanium.« less

Ab initio calculations for industrial materials engineering: successes and challenges.

PubMed

Wimmer, Erich; Najafabadi, Reza; Young, George A; Ballard, Jake D; Angeliu, Thomas M; Vollmer, James; Chambers, James J; Niimi, Hiroaki; Shaw, Judy B; Freeman, Clive; Christensen, Mikael; Wolf, Walter; Saxe, Paul

2010-09-29

Computational materials science based on ab initio calculations has become an important partner to experiment. This is demonstrated here for the effect of impurities and alloying elements on the strength of a Zr twist grain boundary, the dissociative adsorption and diffusion of iodine on a zirconium surface, the diffusion of oxygen atoms in a Ni twist grain boundary and in bulk Ni, and the dependence of the work function of a TiN-HfO(2) junction on the replacement of N by O atoms. In all of these cases, computations provide atomic-scale understanding as well as quantitative materials property data of value to industrial research and development. There are two key challenges in applying ab initio calculations, namely a higher accuracy in the electronic energy and the efficient exploration of large parts of the configurational space. While progress in these areas is fueled by advances in computer hardware, innovative theoretical concepts combined with systematic large-scale computations will be needed to realize the full potential of ab initio calculations for industrial applications.

Equations of state for crystalline zirconium iodide: The role of dispersion

NASA Astrophysics Data System (ADS)

Rossi, Matthew L.; Taylor, Christopher D.

2013-02-01

We present the first-principle equations of state of several zirconium iodides, ZrI2, ZrI3, and ZrI4, computed using density functional theory methods that apply various methods for introducing the dispersion correction. Iodides formed due to reaction of molecular or atomic iodine with zirconium and zircaloys are of particular interest due to their application to the cladding material used in the fabrication of nuclear fuel rods. Stress corrosion cracking (SCC), associated with fission product chemistry with the clad material, is a major concern in the life cycle of nuclear fuels, as many of the observed rod failures have occurred due to pellet-cladding chemical interactions (PCCI) [A. Atrens, G. Dannhäuser, G. Bäro, Stress-corrosion-cracking of zircaloy-4 cladding tubes, Journal of Nuclear Materials 126 (1984) 91-102; P. Rudling, R. Adamson, B. Cox, F. Garzarolli, A. Strasser, High burn-up fuel issues, Nuclear Engineering and Technology 40 (2008) 1-8]. A proper understanding of the physical properties of the corrosion products is, therefore, required for the development of a comprehensive SCC model. In this particular work, we emphasize that, while existing modeling techniques include methods to compute crystal structures and associated properties, it is important to capture intermolecular forces not traditionally included, such as van der Waals (dispersion) correction. Furthermore, crystal structures with stoichiometries favoring a high I:Zr ratio are found to be particularly sensitive, such that traditional density functional theory approaches that do not incorporate dispersion incorrectly predict significantly larger volumes of the lattice. This latter point is related to the diffuse nature of the iodide electron cloud.

Effects of Plasma ZrN Metallurgy and Shot Peening Duplex Treatment on Fretting Wear and Fretting Fatigue Behavior of Ti6Al4V Alloy

PubMed Central

Tang, Jingang; Liu, Daoxin; Zhang, Xiaohua; Du, Dongxing; Yu, Shouming

2016-01-01

A metallurgical zirconium nitride (ZrN) layer was fabricated using glow metallurgy using nitriding with zirconiuming prior treatment of the Ti6Al4V alloy. The microstructure, composition and microhardness of the corresponding layer were studied. The influence of this treatment on fretting wear (FW) and fretting fatigue (FF) behavior of the Ti6Al4V alloy was studied. The composite layer consisted of an 8-μm-thick ZrN compound layer and a 50-μm-thick nitrogen-rich Zr–Ti solid solution layer. The surface microhardness of the composite layer is 1775 HK0.1. A gradient in cross-sectional microhardness distribution exists in the layer. The plasma ZrN metallurgical layer improves the FW resistance of the Ti6Al4V alloy, but reduces the base FF resistance. This occurs because the improvement in surface hardness results in lowering of the toughness and increasing in the notch sensitivity. Compared with shot peening treatment, plasma ZrN metallurgy and shot peening composite treatment improves the FW resistance and enhances the FF resistance of the Ti6Al4V alloy. This is attributed to the introduction of a compressive stress field. The combination of toughness, strength, FW resistance and fatigue resistance enhance the FF resistance for titanium alloy. PMID:28773345

Effect of Zirconium Oxide and Zinc Oxide Nanoparticles on Physicochemical Properties and Antibiofilm Activity of a Calcium Silicate-Based Material

PubMed Central

Guerreiro-Tanomaru, Juliane Maria; Trindade-Junior, Adinael; Cesar Costa, Bernardo; da Silva, Guilherme Ferreira; Drullis Cifali, Leonardo; Basso Bernardi, Maria Inês

2014-01-01

The aim of the present study was to evaluate the antibiofilm activity against Enterococcus faecalis, compressive strength. and radiopacity of Portland cement (PC) added to zirconium oxide (ZrO2), as radiopacifier, with or without nanoparticulated zinc oxide (ZnO). The following experimental materials were evaluated: PC, PC + ZrO2, PC + ZrO2 + ZnO (5%), and PC + ZrO2 + ZnO (10%). Antibiofilm activity was analyzed by using direct contact test (DCT) on Enterococcus faecalis biofilm, for 5 h or 15 h. The analysis was conducted by using the number of colony-forming units (CFU/mL). The compressive strength was performed in a mechanical testing machine. For the radiopacity tests, the specimens were radiographed together with an aluminium stepwedge. The results were submitted to ANOVA and Tukey tests, with level of significance at 5%. The results showed that all materials presented similar antibiofilm activity (P > 0.05). The addition of nanoparticulated ZnO decreased the compressive strength of PC. All materials presented higher radiopacity than pure PC. It can be concluded that the addition of ZrO2 and ZnO does not interfere with the antibiofilm activity and provides radiopacity to Portland cement. However, the presence of ZnO (5% or 10%) significantly decreased the compressive strength of the materials. PMID:25431798

Formation of heterobimetallic zirconium/cobalt diimido complexes via a four-electron transformation.

PubMed

Wu, Bing; Hernández Sánchez, Raúl; Bezpalko, Mark W; Foxman, Bruce M; Thomas, Christine M

2014-10-06

The reactivity of the reduced heterobimetallic complex Zr((i)PrNP(i)Pr2)3CoN2 (1) toward aryl azides was examined, revealing a four-electron redox transformation to afford unusual heterobimetallic zirconium/cobalt diimido complexes. In the case of p-tolyl azide, the diamagnetic C3-symmetric bis(terminal imido) complex 3 is formed, but mesityl azide instead leads to asymmetric complex 4 featuring a bridging imido fragment.

Investigation of phase transition properties of ZrO2 thin films

NASA Astrophysics Data System (ADS)

Kumar, Davinder; Singh, Avtar; Kaur, Manpreet; Rana, Vikrant Singh; Kaur, Raminder

2018-05-01

This paper presents the synthesis of transparent thin films of zirconium oxide (ZrO2) deposited on glass substrates by sol-gel dip coating technique. Synthesized films were characterized for different annealing time and withdrawal speed. Change in crystallographic properties of thin films was investigated by using X-ray diffraction. Surface morphology of transparent thin films was estimated by using scanning electron microscope.

Hydrogenation behavior of Ti-implanted Zr-1Nb alloy with TiN films deposited using filtered vacuum arc and magnetron sputtering

NASA Astrophysics Data System (ADS)

Kashkarov, E. B.; Nikitenkov, N. N.; Sutygina, A. N.; Bezmaternykh, A. O.; Kudiiarov, V. N.; Syrtanov, M. S.; Pryamushko, T. S.

2018-02-01

More than 60 years of operation of water-cooled reactors have shown that local or general critical hydrogen concentration is one of the basic limiting criteria of zirconium-based fuel element claddings. During the coolant radiolysis, released hydrogen penetrates and accumulates in zirconium alloys. Hydrogenation of zirconium alloys leads to degradation of their mechanical properties, hydride cracking and stress corrosion cracking. In this research the effect of titanium nitride (TiN) deposition on hydrogenation behavior of Ti-implanted Zr-1Nb alloy was described. Ti-implanted interlayer was fabricated by plasma immersion ion implantation (PIII) at the pulsed bias voltage of 1500 V to improve the adhesion of TiN and reduce hydrogen penetration into Zr-1Nb alloy. We conducted the comparative analysis on hydrogenation behavior of the Ti-implanted alloy with sputtered and evaporated TiN films by reactive dc magnetron sputtering (dcMS) and filtered cathodic vacuum arc deposition (FVAD), respectively. The crystalline structure and surface morphology were investigated using X-ray diffraction (XRD) and scanning electron microscopy (SEM). The elemental distribution was analyzed using glow-discharge optical emission spectroscopy (GD-OES). Hydrogenation was performed from gas atmosphere at 350 °C and 2 atm hydrogen pressure. The results revealed that TiN films as well as Ti implantation significantly reduce hydrogen absorption rate of Zr-1Nb alloy. The best performance to reduce the rate of hydrogen absorption is Ti-implanted layer with evaporated TiN film. Morphology of the films impacted hydrogen permeation through TiN films: the denser film the lower hydrogen permeation. The Ti-implanted interface plays an important role of hydrogen accumulation layer for trapping the penetrated hydrogen. No deterioration of adhesive properties of TiN films on Zr-1Nb alloy with Ti-implanted interface occurs under high-temperature hydrogen exposure. Thus, the fabrication of Ti-implanted layer with dense TiN films can be an effective way to protect Zr-1Nb alloy from hydrogen embrittlement.

Investigation of holmium-doped zirconium oxide ceramic phosphor as an ultraviolet wavelength-discriminating laser beam viewer

NASA Astrophysics Data System (ADS)

Yamanoi, Kohei; Hori, Tatsuhiro; Minami, Yuki; Empizo, Melvin John F.; Luong, Mui Viet; Shiro, Atsushi; Watanabe, Jun; Iwano, Keisuke; Iwasa, Yuki; Cadatal-Raduban, Marilou; Gabayno, Jacque Lynn; Shimizu, Toshihiko; Sarukura, Nobuhiko; Norimatsu, Takayoshi

2018-01-01

We report the fluorescence spectra of ZrO2 and trivalent Ho-doped ZrO2 ceramics under ultraviolet (UV) excitation at 213, 266, and 355 nm wavelengths. The Ho3+-doped ZrO2 ceramics exhibited varying fluorescence color tones depending on the excitation wavelength used. The different color tones match the fluorescence spectrum characteristics at each excitation wavelength. Our results demonstrate that Ho3+-doped ZrO2 ceramics can discriminate between UV light, specifically the third, fourth, and fifth harmonics of a Nd:YAG laser. It can potentially be used for developing UV laser beam viewers to aid laser alignment.

Grain Refinement and Mechanical Properties of Cu–Cr–Zr Alloys with Different Nano-Sized TiCp Addition

PubMed Central

Zhang, Dongdong; Bai, Fang; Wang, Yong; Wang, Jinguo; Wang, Wenquan

2017-01-01

The TiCp/Cu master alloy was prepared via thermal explosion reaction. Afterwards, the nano-sized TiCp/Cu master alloy was dispersed by electromagnetic stirring casting into the melting Cu–Cr–Zr alloys to fabricate the nano-sized TiCp-reinforced Cu–Cr–Zr composites. Results show that nano-sized TiCp can effectively refine the grain size of Cu–Cr–Zr alloys. The morphologies of grain in Cu–Cr–Zr composites changed from dendritic grain to equiaxed crystal because of the addition and dispersion of nano-sized TiCp. The grain size decreased from 82 to 28 μm with the nano-sized TiCp content. Compared with Cu–Cr–Zr alloys, the ultimate compressive strength (σUCS) and yield strength (σ0.2) of 4 wt% TiCp-reinforced Cu–Cr–Zr composites increased by 6.7% and 9.4%, respectively. The wear resistance of the nano-sized TiCp-reinforced Cu–Cr–Zr composites increased with the increasing nano-sized TiCp content. The wear loss of the nano-sized TiCp-reinforced Cu–Cr–Zr composites decreased with the increasing TiCp content under abrasive particles. The eletrical conductivity of Cu–Cr–Zr alloys, 2% and 4% nano-sized TiCp-reinforced Cu–Cr–Zr composites are 64.71% IACS, 56.77% IACS and 52.93% IACS, respectively. PMID:28786937

Relevance of single-particle and collective excitations in zirconium isotopes populated by neutron transfer reactions in the {sup 90}Zr+{sup 208}Pb system

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pajtler, M. Varga, E-mail: maja.varga@fizika.unios.hr; Szilner, S.; Malenica, D. Jelavić

2015-10-15

Multineutron transfer reaction {sup 90}Zr+{sup 208}Pb has been studied at the energy close to the Coulomb barrier energy by using the PRISMA + CLARA set-up. In this fragment-γ coincidence measurement, the selective properties of the reaction mechanism in the population of the specific states have been discussed. Based on the observed γ transitions of neutron transfer channels, namely {sup 89–94}Zr isotopes, their level schemes have been constructed and updated.

Enhanced oxygen storage capacity of cation-ordered cerium-zirconium oxide induced by titanium substitution.

PubMed

Goto, Yoshihiro; Morikawa, Akira; Iwasaki, Masaoki; Miura, Masahide; Tanabe, Toshitaka

2018-04-03

Herein, we report on the synthesis of Ce0.5Zr0.5-xTixO2 oxygen storage materials prepared via a solution combustion method. Ce0.5Zr0.4Ti0.1O2 showed an outstanding oxygen storage capacity (1310 μmol-O per g) at 200 °C compared to conventional κ-Ce2Zr2O8 (650 μmol-O per g) due to its cation ordering and the formation of weakly bound oxygen atoms induced by Ti substitution.

Zirconium diselenite microstructures, formation and mechanism

NASA Astrophysics Data System (ADS)

Naik, Chandan C.; Salker, A. V.

2018-04-01

In this work, a series of microstructures of zirconium diselenite (Zr(SeO3)2) has been prepared via a simple precipitation method at room temperature without adding any organic surfactants. Phase purity of the sample has been checked by X-ray Diffraction. From the SEM, FESEM, and TEM images spheroid nanoparticles to the starfish-like structure of zirconium diselenite are detected. The morphological evolution processes were investigated carefully following time-dependent experiments and a growth mechanism has been proposed. Two different crystal growth processes, the oriented attachment process accompanying the Ostwald ripening process were held responsible for the formation of a structure resembling starfish having four arms.

The influence of adding modified zirconium oxide-titanium dioxide nano-particles on mechanical properties of orthodontic adhesive: an in vitro study.

PubMed

Felemban, Nayef H; Ebrahim, Mohamed I

2017-01-13

The purpose of this in-vitro study was to examine the effect of incorporating different concentrations of Zirconium oxide-Titanium dioxide (ZrO2-TiO2) nanoparticles, which can have antibacterial properties, on the mechanical properties of an orthodontic adhesive. ZrO2-TiO2 (Zirconium oxide, HWNANO, Hongwu International Group Ltd, China) -Titanium dioxide, Nanoshell, USA) nanopowder were incorporated into orthodontic adhesive (Transbond XT, 3 M Unitek, Monrovia, USA) with different concentrations (0.5% weight nonofiller and 1% weight nanofiller). The size of nanoparticle was 70-80 nm for ZrO2 and less than 50 nm for TiO2. For measuring the shear bond strength of the three groups of orthodontic adhesives [Transbond (control), Transbond mixed with 0.5% weight ZrO2-TiO2, and Transbond mixed with 1% weight ZrO2-TiO2], 30 freshly extracted human first premolars were used and bonded with stainless steel metal brackets (Dentaurum®, Discovery®, Deutschland), using the 3 orthodontic adhesives and 3 M Unitek; Transbond TM Plus Self-Etching Primer (10 samples in each group). The recorded values of compressive strength and tensile strength (measured separately on 10 samples of orthodontic adhesives (add the 3 D size of sample, light cured for 40 s on both sides) of each orthodontic adhesives), as well as the shear bond strength in Mega Pascal unit (MPa) were collected and exposed to one-way analysis of variance (ANOVA) and Tukey's post-hoc tests. orthodontic adhesive with 1% weight ZrO2-TiO2 showed the highest mean compressive (73.42 ± 1.55 MPa, p: 0.003, F: 12.74), tensile strength (8.65 ± 0.74 MPa, p: 0.001, F: 68.20), and shear bond strength (20.05 ± 0.2 MPa, p: 0.001, F: 0.17). Adding ZrO2-TiO2 nanoparticle to orthodontic adhesive increased compressive strength, tensile strength, and shear bond strength in vitro, but in vivo studies and randomized clinical trials are needed to validate the present findings.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Arul Kumar, M.; Beyerlein, Irene Jane; Tomé, Carlos N.

Here we study the effect of nearest neighboring grains on the propensity for {1012} twin growth in Mg and Zr. Twin lamellae lying within one grain flanked by two neighboring grains with several orientations are considered. The fields of resolved shear stress on the twin system are calculated in the multicrystal using a three-dimensional full-field crystal plasticity Fast Fourier Transform approach. The calculations were carried out for Mg and Zr using slip threshold stresses corresponding to 300K and 76K, respectively, where twin activity is important. We show that the neighboring grain constraint tends to oppose further growth and that themore » critical applied stress needed to overcome this resistance depends on neighboring grain orientation, more strongly in Zr than in Mg. We also present results for a pair of adjacent and parallel twins at various spacings. It is found that their paired interaction increases the resistive forces for twin growth above that for an isolated twin. The critical spacing above which this enhanced resistance is removed is smaller for Zr than Mg. Our analysis reveals that these two disparate responses of Zr and Mg are both a consequence of the fact that Zr is elastically and plastically more anisotropic than Mg. Additional calculations carried out on Ti support this conclusion. Finally, these findings can help explain why, for the same grain size, more twins per grain form in Zr than in Mg, twins in Zr tend to be thinner than those in Mg, and the relationship between the thickness of the twin and its Schmid factor in Zr is not as strong as in Mg.« less

Ferroelectric relaxor behaviour and impedance spectroscopy of Bi2O3-doped barium zirconium titanate ceramics

NASA Astrophysics Data System (ADS)

Mahajan, Sandeep; Thakur, O P; Bhattacharya, D K; Sreenivas, K

2009-03-01

Bi2O3-doped barium zirconate titanate ceramics, Ba1-xBix(Zr0.05Ti0.95)O3, have been prepared by the conventional solid-state reaction method. The ferroelectric relaxor behaviour and dielectric properties have been investigated in detail. By XRD analysis, it is suggested that up to x = 0.04, Bi3+ substitutes A-site ion, and thereafter with higher Bi3+ content, it enters the B-site sub lattice. Substitution of Bi3+ ions induces ferroelectric relaxor behaviour and the degree of relaxation behaviour increases with bismuth concentration. The remanent polarization and strain behaviour show a slight increase with the substitution level. The degree of hysteresis (strain versus electric field) also reduces from 21.4% to 4.6% with bismuth substitution. Impedance measurements were made on the prepared sample over a wide range of temperatures (300-723 K) and frequencies (40 Hz-1 MHz), which show the presence of both bulk and grain boundary effects in the material. The bulk and grain boundary conductivities determined from impedance study indicate the Arrhenius-type thermally activated process. Impedance spectroscopy is shown to be an efficient method capable of detecting the contributions of the resistances of grains and grain boundaries to the complex impedance of a ceramic system, accurately estimating its electrical conductivity as well as its corresponding activation energies and drawing conclusions on its structural properties.

Production of ZrC Matrix for Use in Gas Fast Reactor Composite Fuels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vasudevamurthy, Gokul; Knight, Travis W.; Roberts, Elwyn

2007-07-01

Zirconium carbide is being considered as a candidate for inert matrix material in composite nuclear fuel for Gas fast reactors due to its favorable characteristics. ZrC can be produced by the direct reaction of pure zirconium and graphite powders. Such a reaction is exothermic in nature. The reaction is self sustaining once initial ignition has been achieved. The heat released during the reaction is high enough to complete the reaction and achieve partial sintering without any external pressure applied. External heat source is required to achieve ignition of the reactants and maintain the temperature close to the adiabatic temperature tomore » achieve higher levels of sintering. External pressure is also a driving force for sintering. In the experiments described, cylindrical compacts of ZrC were produced by direct combustion reaction. External induction heating combined with varying amounts of external applied pressure was employed to achieve varying degrees of density/porosity. The effect of reactant particle size on the product characteristics was also studied. The samples were characterized for density/porosity, composition and microstructure. (authors)« less

In Vivo Integrity and Biological Fate of Chelator-Free Zirconium-89-Labeled Mesoporous Silica Nanoparticles

PubMed Central

2015-01-01

Traditional chelator-based radio-labeled nanoparticles and positron emission tomography (PET) imaging are playing vital roles in the field of nano-oncology. However, their long-term in vivo integrity and potential mismatch of the biodistribution patterns between nanoparticles and radio-isotopes are two major concerns for this approach. Here, we present a chelator-free zirconium-89 (89Zr, t1/2 = 78.4 h) labeling of mesoporous silica nanoparticle (MSN) with significantly enhanced in vivo long-term (>20 days) stability. Successful radio-labeling and in vivo stability are demonstrated to be highly dependent on both the concentration and location of deprotonated silanol groups (−Si–O–) from two types of silica nanoparticles investigated. This work reports 89Zr-labeled MSN with a detailed labeling mechanism investigation and long-term stability study. With its attractive radio-stability and the simplicity of chelator-free radio-labeling, 89Zr-MSN offers a novel, simple, and accurate way for studying the in vivo long-term fate and PET image-guided drug delivery of MSN in the near future. PMID:26213260

In Vivo Integrity and Biological Fate of Chelator-Free Zirconium-89-Labeled Mesoporous Silica Nanoparticles.

PubMed

Chen, Feng; Goel, Shreya; Valdovinos, Hector F; Luo, Haiming; Hernandez, Reinier; Barnhart, Todd E; Cai, Weibo

2015-08-25

Traditional chelator-based radio-labeled nanoparticles and positron emission tomography (PET) imaging are playing vital roles in the field of nano-oncology. However, their long-term in vivo integrity and potential mismatch of the biodistribution patterns between nanoparticles and radio-isotopes are two major concerns for this approach. Here, we present a chelator-free zirconium-89 ((89)Zr, t1/2 = 78.4 h) labeling of mesoporous silica nanoparticle (MSN) with significantly enhanced in vivo long-term (>20 days) stability. Successful radio-labeling and in vivo stability are demonstrated to be highly dependent on both the concentration and location of deprotonated silanol groups (-Si-O(-)) from two types of silica nanoparticles investigated. This work reports (89)Zr-labeled MSN with a detailed labeling mechanism investigation and long-term stability study. With its attractive radio-stability and the simplicity of chelator-free radio-labeling, (89)Zr-MSN offers a novel, simple, and accurate way for studying the in vivo long-term fate and PET image-guided drug delivery of MSN in the near future.

Oxidized zirconium versus cobalt-chromium against the native patella in total knee arthroplasty: Patellofemoral outcomes.

PubMed

Matassi, Fabrizio; Paoli, Tommaso; Civinini, Roberto; Carulli, Christian; Innocenti, Massimo

2017-10-01

Oxidized zirconium (OxZr) has demonstrated excellent mechanical properties in vitro when used against articular cartilage; less coefficient of friction and less chondral damage have been found when compared with cobalt-chromium (CoCr) implants. However, controversy exists as to whether implants with a zirconium femoral component articulate safely with a native patella in total knee arthroplasty (TKA). To answer this question, the clinical and radiographic results were analysed from a group of patients who underwent a TKA with patella retention; the OxZr versus CoCr femoral components were compared. The present study prospectively evaluated 83 knees of 74 patients from 2009 to 2010. Each patient was evaluated clinically (visual analogue scale, Knee Society score, patellar score) and radiographically (long leg standing radiograph, anterior-posterior and latero-lateral projections, axial view of the patella) pre-operatively and postoperatively with a mean follow-up of 4.47years. The patellar tilt and shift, and progression of patellofemoral osteoarthritis were calculated with the axial view. There were no patient reported adverse reactions and none of the evaluated prostheses failed. Both the clinical and radiographic evaluations showed no statistically significant between-group differences. No adverse events were observed clinically or radiologically. These results justify pursuing the use of oxidized zirconium as an alternative bearing surface for a femoral component associated with patellar retention in TKA. Published by Elsevier B.V.

The effect of feed rate and recycle rate variable on leaching process of Na2Zro3 with HCl in continuous stirred tank reactor (CSTR) series

NASA Astrophysics Data System (ADS)

Palupi, Bekti; Supranto, Sediawan, Wahyudi Budi; Setyadji, Moch.

2017-05-01

This time, the natural resources of zircon sand is processed into several zirconium products which is utilized for various industries, such as ceramics, glass industry, metal industry and nuclear industry. The process of zircon sand into zirconium products through several stages, one of them is leaching process of Na2ZrO3 with HCl. In this research, several variations of recycle-rate/feed-rate had been done to determine the effect on leaching process. The leaching was processed at temperature of 90°C, ratio of Na2ZrO3:HCl = 1g:30mL, and 142 rotary per minute of stirring speed for 30 minutes with variation of recycle-rate/feed-rate such as 0.478, 0.299, 0.218, 0.171 and 0.141. The diameter size of Na2ZrO3 powder that used are 0.088 to 0.149 mm. This process was carried out in Continuous Stirred Tank Reactor (CSTR) series with recycle. Based on this research, the greater of the recycle-rate/feed-rate variable, the obtained Zr recovery decreased. The correlation between recycle-rate/feed-rate and Zr recovery is shown by the equation y = -146.91x + 103.51, where y is the Zr recovery and x is the recycle-rate/feed-rate. The highest Zr recovery was 90.52% obtained at recycle-rate/feed-rate 0.141. The mathematical modeling involving the probability model P(r) = 2β2r2 exp(-βr2) can be applied to this leaching process with Sum of Squared Errors (SSE) values in the range of 6×10-7 - 7×10-6.

Titanium and Zirconium Levels Are Associated with Changes in MicroRNAs Expression: Results from a Human Cross-Sectional Study on Obese Population

PubMed Central

Dioni, Laura; Angelici, Laura; Vigna, Luisella; Farronato, Giampietro; Pesatori, Angela Cecilia; Bollati, Valentina

2016-01-01

Objectives In this study on 90 individuals we aimed at evaluating the microRNAs (miRNAs) expression profile associated with personal levels of Titanium (Ti) and Zirconium (Zr) traced in hair samples. Ti and Zr materials are broadly used for dental implants but the biological reactions triggered by a long term presence of these materials in the oral cavity still need to be assessed. MiRNAs are mechanisms that need to be investigated as they play a fundamental role in the control of gene expression following external stimuli and contribute to a wide range of pathophysiological processes. Methods Using the TaqMan® Low-Density Array, we assessed the expression levels of 377 human miRNAs in peripheral blood of 90 subjects. Hair samples were analyzed for Ti and Zr content using Inductively Coupled Plasma-Mass Spectrometry. We performed multivariable regression analysis to investigate the effects of Ti and Zr exposure on miRNA expression levels. We used the Ingenuity Pathway Analysis (IPA) software to explore the functional role of the investigated miRNAs and the related target genes. Results Seven miRNAs (miR-99b, miR-142-5p, miR-152, miR-193a-5p, miR-323-3p, miR-335, miR-494) resulted specifically associated with Zr levels. The functional target analysis showed that miRNAs are involved in mechanisms such as inflammation, skeletal and connective tissue disorders. Conclusions Our data suggest that Zr is more bioactive than Ti and show that miRNAs are relevant molecular mechanisms sensitive to Zr exposure. PMID:27611787

Thermal properties of zirconium diboride -- transition metal boride solid solutions

NASA Astrophysics Data System (ADS)

McClane, Devon Lee

This research focuses on the thermal properties of zirconium diboride (ZrB2) based ceramics. The overall goal was to improve the understanding of how different transition metal (TM) additives influence thermal transport in ZrB2. To achieve this, ZrB2 with 0.5 wt% carbon, and 3 mol% of individual transition metal borides, was densified by hot-press sintering. The transition metals that were investigated were: Y, Ti, Hf, V, Nb, Ta, Cr, Mo, W, and Re. The room temperature thermal diffusivities of the compositions ranged from 0.331 cm2/s for nominally pure ZrB2 to 0.105 cm2/s for (Zr,Cr)B2 and converged around 0.155cm2/s at higher temperatures for all compositions. Thermal conductivities were calculated from the diffusivities, using temperature-dependent values for density and heat capacity. The electron contribution to thermal conductivity was calculated from measured electrical resistivity according to the Wiedemann-Franz law. The phonon contribution to thermal conductivity was calculated by subtracting the electron contribution from the total thermal conductivity. Rietveld refinement of x-ray diffraction data was used to determine the lattice parameters of the compositions. The decrease in thermal conductivity for individual additives correlated directly to the metallic radius of the additive. Additional strain appeared to exist for additives when the stable TM boride for that metal had different crystal symmetries than ZrB2. This research provided insight into how additives and impurities affect thermal transport in ZrB2. The research potentially offers a basis for future modeling of thermal conductivity in ultra-high temperature ceramics based on the correlation between metallic radius and the decrease in thermal conductivity.

An Impact of Zirconium Doping of Zn-Al Braze on the Aluminum-Stainless Steel Joints Integrity During Aging

NASA Astrophysics Data System (ADS)

Yang, Jinlong; Xue, Songbai; Sekulic, Dusan P.

2017-01-01

This work offers an analysis of the microstructure and the growth rate of an intermetallic compound within the aged AA 6061 aluminum alloy-304 stainless steel joint brazed with Zn-15Al and Zn-15Al-0.2Zr filler metals. The effect of zirconium addition on mechanical integrity of the brazed joint was studied. The experimental results confirm that the thickness of the Fe-Al intermetallic layer formed at the brazed seam/stainless steel interface increases with the increase of the aging time. Furthermore, it is established that the growth rate of the intermetallic layer for the Zn-15Al-0.2Zr brazed joint was lower than that for Zn-15Al. The results also indicate that the shear strength of both Zn-15Al and Zn-15Al-0.2Zr brazed joints decreases monotonously during aging. The value of the strength after aging lasting for 800 h for Zn-15Al and Zn-15Al-0.2Zr has decreased by 20 and 17%, respectively. The fracture of joints occurred at the interface between the brazed seam and the Fe4Al13 intermetallic layer. The morphology of the surfaces exhibits a cleavage fracture.

Highly selective manganese-doped zinc sulfide quantum dots based label free phosphorescent sensor for phosphopeptides in presence of zirconium (IV).

PubMed

Gong, Yan; Fan, Zhefeng

2015-04-15

We report a room-temperature phosphorescence (RTP) sensor for phosphopeptides based on zirconium (IV)-modulated mercaptopropionic acid (MPA)-capped Mn-doped ZnS quantum dots (QDs). This sensor incorporates the advantages of the well-known Zr(4+)-phosphopeptide affinity pair and the RTP properties of doped QDs. The RTP of Mn-doped ZnS QDs capped with MPA can be effectively quenched by Zr(4+). The high affinity of phosphopeptides to Zr(4+) enables the dissociation of the ion from the surface of MPA-capped ZnS QDs, thereby forming a stable complex with phosphopeptides in the solution, and recovering the RTP of the QDs. The Zr(4+)-induced RTP quenching and subsequent phosphopeptide-induced RTP recovery for MPA-capped ZnS QDs provide a solid basis for the present RTP sensor based on QDs for the detection of phosphopeptides. The detection limit for phosphopeptides is 0.9ngmL(-1), the relative standard deviations is 2.5%, and the recovery of urine and serum samples with phosphopeptides addition rangs from 96% to 105% at optimal conditions. The proposed method was successfully applied to biological fluids and obtained satisfactory results. Copyright © 2014 Elsevier B.V. All rights reserved.

Dielectric, thermal and mechanical properties of zirconium silicate reinforced high density polyethylene composites for antenna applications.

PubMed

Varghese, Jobin; Nair, Dinesh Raghavan; Mohanan, Pezholil; Sebastian, Mailadil Thomas

2015-06-14

A low cost and low dielectric loss zirconium silicate (ZrSiO4) reinforced HDPE (high-density polyethylene) composite has been developed for antenna applications. The 0-3 type composite is prepared by dispersing ZrSiO4 fillers for various volume fractions (0.1 to 0.5) in the HDPE matrix by the melt mixing process. The composite shows good microwave dielectric properties with a relative permittivity of 5.6 and a dielectric loss of 0.003 at 5 GHz at the maximum filler loading of 0.5 volume fraction. The composite exhibits low water absorption, excellent thermal and mechanical properties. It shows a water absorption of 0.03 wt%, a coefficient of thermal expansion of 70 ppm per °C and a room temperature thermal conductivity of 2.4 W mK(-1). The composite shows a tensile strength of 22 MPa and a microhardness of 13.9 kg mm(-2) for the filler loading of 0.5 volume fraction. The HDPE-ZrSiO4 composites show good dielectric, thermal and mechanical properties suitable for microwave soft substrate applications. A microstrip patch antenna is designed and fabricated using the HDPE-0.5 volume fraction ZrSiO4 substrate and the antenna parameters are investigated.

A simple and rapid in situ preconcentration method for the determination of phosphate in environmental waters by use of solid-phase extraction, and its applications to brackish lake waters.

PubMed

Okumura, M; Tong, L; Fujinaga, K; Seike, Y

2001-05-01

A simple and rapid in situ preconcentration method for the determination of phosphate in environmental waters has been developed for field analysis. This method is based on solid-phase extraction on a zirconium-loaded Sep-Pack Accell CM cartridge (Zr-SP) and is applicable to studies in which sampling is performed by use of a graduated syringe to prevent contamination and to ensure easy operation at sampling sites. The Zr-SP cartridge was prepared by passing 0.1 mol L(-1) zirconium solution through a Sep-Pak Accell CM cartridge, packed with cation exchange sorbent based on a silica matrix. The adsorption of phosphate and its desorption depend only on the pH of the solution. A water sample containing phosphate was adjusted to pH 2 and passed through the Zr-SP cartridge to collect it. The retained phosphate was quantitatively eluted with 0.5 mol L(-1) sodium hydroxide solution. The phosphate retained in the Zr-SP cartridge was stable for at least one month. The established preconcentration method was successfully applied to brackish lake waters to investigate seasonal changes in the distribution and behavior of phosphate in a brackish lake.

Zirconium-doped magnetic microspheres for the selective enrichment of cis-diol-containing ribonucleosides.

PubMed

Fan, Hua; Chen, Peihong; Wang, Chaozhan; Wei, Yinmao

2016-05-27

Zirconium-doped magnetic microspheres (Zr-Fe3O4) for the selective enrichment of cis-diol-containing biomolecules were easily synthesized via a one-step hydrothermal method. Characterization of the microspheres revealed that zirconium was successfully doped into the lattice of Fe3O4 at a doping level of 4.0 at%. Zr-Fe3O4 possessed good magnetic properties and high specificity towards cis-diol molecules, as shown using 28 compounds. For ribonucleosides, the adsorbent not only has favorable anti-interferential abilities but also has a high adsorption capacity up to 159.4μmol/g. As an example of a real application, four ribonucleosides in urine were efficiently enriched and detected via magnetic solid-phase extraction coupled with high-performance liquid chromatography. Under the optimized extraction conditions, the detection limits were determined to be between 0.005 and 0.017μg/mL, and the linearities ranged from 0.02 to 5.00μg/mL (R≥0.996) for these analytes. The accuracy of the analytical method was examined by studying the relative recoveries of the analytes in real urine samples, with recoveries varying from 77.8% to 119.6% (RSDs<10.6%, n=6). The results indicate that Zr-Fe3O4 is a suitable adsorbent for the analysis of cis-diol-containing biomolecules in practical applications. Copyright © 2016 Elsevier B.V. All rights reserved.

Surface defects on the Gd{sub 2}Zr{sub 2}O{sub 7} oxide films grown on textured NiW technical substrates by chemical solution method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhao, Y., E-mail: yuezhao@sjtu.edu.cn

2017-02-15

Epitaxial growth of oxide thin films has attracted much interest because of their broad applications in various fields. In this study, we investigated the microstructure of textured Gd{sub 2}Zr{sub 2}O{sub 7} films grown on (001)〈100〉 orientated NiW alloy substrates by a chemical solution deposition (CSD) method. The aging effect of precursor solution on defect formation was thoroughly investigated. A slight difference was observed between the as-obtained and aged precursor solutions with respect to the phase purity and global texture of films prepared using these solutions. However, the surface morphologies are different, i.e., some regular-shaped regions (mainly hexagonal or dodecagonal) weremore » observed on the film prepared using the as-obtained precursor, whereas the film prepared using the aged precursor exhibits a homogeneous structure. Electron backscatter diffraction and scanning electron microscopy analyses showed that the Gd{sub 2}Zr{sub 2}O{sub 7} grains present within the regular-shaped regions are polycrystalline, whereas those present in the surrounding are epitaxial. Some polycrystalline regions ranging from several micrometers to several tens of micrometers grew across the NiW grain boundaries underneath. To understand this phenomenon, the properties of the precursors and corresponding xerogel were studied by Fourier transform infrared spectroscopy and coupled thermogravimetry/differential thermal analysis. The results showed that both the solutions mainly contain small Gd−Zr−O clusters obtained by the reaction of zirconium acetylacetonate with propionic acid during the precursor synthesis. The regular-shaped regions were probably formed by large Gd−Zr−O frameworks with a metastable structure in the solution with limited aging time. This study demonstrates the importance of the precise control of chemical reaction path to enhance the stability and homogeneity of the precursors of the CSD route. - Highlights: •We investigate microstructure of Gd{sub 2}Zr{sub 2}O{sub 7} films grown by a chemical solution route. •The aging effect of precursor solution on formation of surface defect was thoroughly studied. •Gd−Zr−O clusters are present in the precursor solutions.« less

Development of a Modified Embedded Atom Force Field for Zirconium Nitride Using Multi-Objective Evolutionary Optimization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Narayanan, Badri; Sasikumar, Kiran; Mei, Zhi-Gang

2016-07-07

Zirconium nitride (ZrN) exhibits exceptional mechanical, chemical, and electrical properties, which make it attractive for a wide range of technological applications, including wear-resistant coatings, protection from corrosion, cutting/shaping tools, and nuclear breeder reactors. Despite its broad usability, an atomic scale understanding of the superior performance of ZrN, and its response to external stimuli, for example, temperature, applied strain, and so on, is not well understood. This is mainly due to the lack of interatomic potential models that accurately describe the interactions between Zr and N atoms. To address this challenge, we develop a modified embedded atom method (MEAM) interatomic potentialmore » for the Zr–N binary system by training against formation enthalpies, lattice parameters, elastic properties, and surface energies of ZrN (and, in some cases, also Zr3N4) obtained from density functional theory (DFT) calculations. The best set of MEAM parameters are determined by employing a multiobjective global optimization scheme driven by genetic algorithms. Our newly developed MEAM potential accurately reproduces structure, thermodynamics, energetic ordering of polymorphs, as well as elastic and surface properties of Zr–N compounds, in excellent agreement with DFT calculations and experiments. As a representative application, we employed molecular dynamics simulations based on this MEAM potential to investigate the atomic scale mechanisms underlying fracture of bulk and nanopillar ZrN under applied uniaxial strains, as well as the impact of strain rate on their mechanical behavior. These simulations indicate that bulk ZrN undergoes brittle fracture irrespective of the strain rate, while ZrN nanopillars show quasi-plasticity owing to amorphization at the crack front. The MEAM potential for Zr–N developed in this work is an invaluable tool to investigate atomic-scale mechanisms underlying the response of ZrN to external stimuli (e.g, temperature, pressure etc.), as well as other interesting phenomena such as precipitation.« less

Effects of surface treatment of aluminium alloy 1050 on the adhesion and anticorrosion properties of the epoxy coating

NASA Astrophysics Data System (ADS)

Sharifi Golru, S.; Attar, M. M.; Ramezanzadeh, B.

2015-08-01

The objective of this work is to investigate the effects of zirconium-based (Zr) conversion coating on the adhesion properties and corrosion resistance of an epoxy/polyamide coating applied on the aluminium alloy 1050 (AA1050). Field emission scanning electron microscope (FE-SEM), energy dispersive X-ray spectrum (EDS), atomic force microscope (AFM) and contact angle measuring device were employed in order to characterize the surface characteristics of the Zr treated AA1050 samples. The epoxy/polyamide coating was applied on the untreated and Zr treated samples. The epoxy coating adhesion to the aluminium substrate was evaluated by pull-off test before and after 30 days immersion in 3.5% w/w NaCl solution. In addition, the electrochemical impedance spectroscopy (EIS) and salt spray tests were employed to characterize the corrosion protection properties of the epoxy coating applied on the AA1050 samples. Results revealed that the surface treatment of AA1050 by zirconium conversion coating resulted in the increase of surface free energy and surface roughness. The dry and recovery (adhesion strength after 30 days immersion in the 3.5 wt% NaCl solution) adhesion strengths of the coatings applied on the Zr treated aluminium samples were greater than untreated sample. In addition, the adhesion loss of the coating applied on the Zr treated aluminium substrate was lower than other samples. Also, the results obtained from EIS and salt spray test clearly revealed that the Zr conversion coating could enhance the corrosion protective performance of the epoxy coating significantly.

Grain Refinement and Mechanical Properties of Cu-Cr-Zr Alloys with Different Nano-Sized TiCp Addition.

PubMed

Zhang, Dongdong; Bai, Fang; Wang, Yong; Wang, Jinguo; Wang, Wenquan

2017-08-08

The TiC p /Cu master alloy was prepared via thermal explosion reaction. Afterwards, the nano-sized TiC p /Cu master alloy was dispersed by electromagnetic stirring casting into the melting Cu-Cr-Zr alloys to fabricate the nano-sized TiC p -reinforced Cu-Cr-Zr composites. Results show that nano-sized TiC p can effectively refine the grain size of Cu-Cr-Zr alloys. The morphologies of grain in Cu-Cr-Zr composites changed from dendritic grain to equiaxed crystal because of the addition and dispersion of nano-sized TiC p . The grain size decreased from 82 to 28 μm with the nano-sized TiC p content. Compared with Cu-Cr-Zr alloys, the ultimate compressive strength (σ UCS ) and yield strength (σ 0.2 ) of 4 wt% TiC p -reinforced Cu-Cr-Zr composites increased by 6.7% and 9.4%, respectively. The wear resistance of the nano-sized TiCp-reinforced Cu-Cr-Zr composites increased with the increasing nano-sized TiCp content. The wear loss of the nano-sized TiC p -reinforced Cu-Cr-Zr composites decreased with the increasing TiC p content under abrasive particles. The eletrical conductivity of Cu-Cr-Zr alloys, 2% and 4% nano-sized TiCp-reinforced Cu-Cr-Zr composites are 64.71% IACS, 56.77% IACS and 52.93% IACS, respectively.

Zr-based bulk metallic glass as a cylinder material for high pressure apparatuses

DOE PAGES

Komatsu, Kazuki; Munakata, Koji; Matsubayashi, Kazuyuki; ...

2015-05-12

Zirconium-based bulk metallic glass (Zr-based BMG) has outstanding properties as a cylinder mate- rial for piston-cylinder high pressure apparatuses and is especially useful for neutron scattering. The piston-cylinder consisting of a Zr-based BMG cylinder with outer/inner diameters of 8.8/2.5 mm sustains pressures up to 1.81 GPa and ruptured at 2.0 GPa, with pressure values determined by the superconduct- ing temperature of lead. The neutron attenuation of Zr-based BMG is similar to that of TiZr null-scattering alloy and more transparent than that of CuBe alloy. No contamination of sharp Bragg reflections is observed in the neutron diffraction pattern for Zr-based BMG.more » The magnetic susceptibility of Zr-based BMG is similar to that of CuBe alloy; this leads to a potential application for measurements of magnetic properties under pressure.« less

Low-temperature synthesis of nanocrystalline ZrC coatings on flake graphite by molten salts

NASA Astrophysics Data System (ADS)

Ding, Jun; Guo, Ding; Deng, Chengji; Zhu, Hongxi; Yu, Chao

2017-06-01

A novel molten salt synthetic route has been developed to prepare nanocrystalline zirconium carbide (ZrC) coatings on flake graphite at 900 °C, using Zr powder and flake graphite as the source materials in a static argon atmosphere, along with molten salts as the media. The effects of different molten salt media, the sintered temperature, and the heat preservation time on the phase and microstructure of the synthetic materials were investigated. The ZrC coatings formed on the flake graphite were uniform and composed of nanosized particles (30-50 nm). With an increase in the reaction temperature, the ZrC nanosized particles were more denser, and the heat preservation time and thickness of the ZrC coating also increased accordingly. Electron microscopy was used to observe the ZrC coatings on the flake graphite, indicating that a "template mechanism" played an important role during the molten salt synthesis.

Effect of local stress fields on twin characteristics in HCP metals

DOE PAGES

Arul Kumar, M.; Beyerlein, Irene Jane; Tomé, Carlos N.

2016-09-01

Here we study the effect of nearest neighboring grains on the propensity for {1012} twin growth in Mg and Zr. Twin lamellae lying within one grain flanked by two neighboring grains with several orientations are considered. The fields of resolved shear stress on the twin system are calculated in the multicrystal using a three-dimensional full-field crystal plasticity Fast Fourier Transform approach. The calculations were carried out for Mg and Zr using slip threshold stresses corresponding to 300K and 76K, respectively, where twin activity is important. We show that the neighboring grain constraint tends to oppose further growth and that themore » critical applied stress needed to overcome this resistance depends on neighboring grain orientation, more strongly in Zr than in Mg. We also present results for a pair of adjacent and parallel twins at various spacings. It is found that their paired interaction increases the resistive forces for twin growth above that for an isolated twin. The critical spacing above which this enhanced resistance is removed is smaller for Zr than Mg. Our analysis reveals that these two disparate responses of Zr and Mg are both a consequence of the fact that Zr is elastically and plastically more anisotropic than Mg. Additional calculations carried out on Ti support this conclusion. Finally, these findings can help explain why, for the same grain size, more twins per grain form in Zr than in Mg, twins in Zr tend to be thinner than those in Mg, and the relationship between the thickness of the twin and its Schmid factor in Zr is not as strong as in Mg.« less

Concept Feasibility Report for Electroplating Zirconium onto Uranium Foil - Year 2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Coffey, Greg W.; Meinhardt, Kerry D.; Joshi, Vineet V.

2015-03-01

The Fuel Fabrication Capability within the U.S. High Performance Research Reactor Conversion Program is funded through the National Nuclear Security Administration (NNSA) NA-26 (Office of Material Management and Minimization). An investigation was commissioned to determine the feasibility of using electroplating techniques to apply a coating of zirconium onto depleted uranium/molybdenum alloy (U-10Mo). Electroplating would provide an alternative method to the existing process of hot roll-bonding zirconium foil onto the U-10Mo fuel foil during the fabrication of fuel elements for high-performance research reactors. The objective of this research was to develop a reproducible and scalable plating process that will produce amore » uniform, 25 μm thick zirconium metal coating on U-10Mo foil. In previous work, Pacific Northwest National Laboratory (PNNL) established a molten salt electroplating apparatus and protocol to plate zirconium metal onto molybdenum foil (Coffey 2015). During this second year of the research, PNNL furthered this work by moving to the U-10Mo alloy system (90 percent uranium:10 percent molybdenum). The original plating apparatus was disassembled and re-assembled in a laboratory capable of handling low-level radioactive materials. Initially, the work followed the previous year’s approach, and the salt bath composition was targeted at the eutectic composition (LiF:NaF:ZrF4 = 26:37:37 mol%). Early results indicated that the formation of uranium fluoride compounds would be problematic. Other salt bath compositions were investigated in order to eliminate the uranium fluoride production (LiF:NaF = 61:39 mol% and LiF:NaF:KF = 46.5:11.5:42 mol% ). Zirconium metal was used as the crucible for the molten salt. Three plating methods were used—isopotential, galvano static, and pulsed plating. The molten salt method for zirconium metal application provided high-quality plating on molybdenum in PNNL’s previous work. A key advantage of this approach is that plating can be performed under conditions that would greatly reduce the quantity of intermetallics that form at the interface between the zirconium and U-10Mo; unlike roll bonding, the molten salt plating approach would allow for complete coverage of the U-10Mo foil with zirconium. When utilizing the experimental parameters developed for zirconium plating onto molybdenum, a uranium fluoride reaction product was formed at the Zr/U-10Mo interface. By controlling the initial plating potential, the uranium fluoride could be prevented; however, the targeted zirconium thickness (25 ±12.5 μm) could not be achieved while maintaining 100% coverage.« less

The Impact of Updated Zr Neutron-capture Cross Sections and New Asymptotic Giant Branch Models on our Understanding of the s process and the origin of stardust

DOE PAGES

Lugaro, M.; Tagliente, Giuseppe; Karakas, Amanda I.; ...

2013-12-13

We present model predictions for the Zr isotopic ratios produced by slow neutron captures in C-rich asymptotic giant branch (AGB) stars of masses 1.25-4 M-circle dot and metallicities Z = 0.01-0.03, and compare them to data from single meteoritic stardust silicon carbide (SiC) and high-density graphite grains that condensed in the outflows of these stars. We compare predictions produced using the Zr neutron-capture cross sections from Bao et al. and from n_TOF experiments at CERN, and present a new evaluation for the neutron-capture cross section of the unstable isotope Zr-95, the branching point leading to the production of Zr-96. Themore » new cross sections generally present an improved match with the observational data, except for the Zr-92/Zr-94 ratios, which are on average still substantially higher than predicted. The Zr-96/Zr-94 ratios can be explained using our range of initial stellar masses, with the most Zr-96-depleted grains originating from AGB stars of masses 1.8-3 M-circle dot and the others from either lower or higher masses. The Zr-90,Zr-91/Zr-94 variations measured in the grains are well reproduced by the range of stellar metallicities considered here, which is the same needed to cover the Si composition of the grains produced by the chemical evolution of the Galaxy. The Zr-92/Zr-94 versus Si-29/Si-28 positive correlation observed in the available data suggests that stellar metallicity rather than rotation plays the major role in covering the Zr-90,Zr-91,Zr-92/Zr-94 spread« less

Mesoporous silica templated zirconia nanoparticles

NASA Astrophysics Data System (ADS)

Ballem, Mohamed A.; Córdoba, José M.; Odén, Magnus

2011-07-01

Nanoparticles of zirconium oxide (ZrO2) were synthesized by infiltration of a zirconia precursor (ZrOCl2·8H2O) into a SBA-15 mesoporous silica mold using a wet-impregnation technique. X-ray diffractometry and high-resolution transmission electron microscopy show formation of stable ZrO2 nanoparticles inside the silica pores after a thermal treatment at 550 °C. Subsequent leaching out of the silica template by NaOH resulted in well-dispersed ZrO2 nanoparticles with an average diameter of 4 nm. The formed single crystal nanoparticles are faceted with 110 surfaces termination suggesting it to be the preferred growth orientation. A growth model of these nanoparticles is also suggested.

Fabrication of piezoelectric ceramic fibers by extrusion of Pb(Zr, Ti)O3 powder and Pb(Zr, Ti)O3 sol mixture

NASA Astrophysics Data System (ADS)

Qiu, Jinhao; Tani, Junji; Kobayashi, Yoshimasa; Um, Tae Young; Takahashi, Hirofumi

2003-06-01

In this study, Pb(Zr, Ti)O3 (PZT) piezoelectric ceramic fibers were fabricated by extrusion from a mixture of PZT powder and PZT sol. The added PZT sol in this study played the role of a binder; the sol changed into crystalline PZT during sintering, and removal of additives before sintering was not required. To obtain the required PZT fibers, the sol viscosity adjustment condition, the mixture ratio of powder and sol for fiber extrusion, and the sintering condition for obtaining polycrystalline fibers were investigated. The PZT precursor solution was synthesized from lead acetate trihydrate, zirconium n-propoxide, and titanium isopropoxide by reflux at 120 °C for 3 h with 2-methoxyethanol. The appropriate adjustment of the spinnable sol was achieved by the addition of acetic acid to suppress the hydrolysis reaction and by curing the sol at 80 °C to promote the condensation of the sol. Green fibers with diameters of about 300µm were successfully extruded from the mixture of PZT powder and sol (powder:sol = 5- 8:1, molar ratio). The extruded fibers, sintered at 1200 °C, had a microstructure with 2- 6µm grains and had no pores or cracks. From the results of displacement behavior measurements, the PZT fibers fabricated by firing at 1200 °C in this study were considered to have the desired piezoelectric properties.

Clinical evidence on titanium-zirconium dental implants: a systematic review and meta-analysis.

PubMed

Altuna, P; Lucas-Taulé, E; Gargallo-Albiol, J; Figueras-Álvarez, O; Hernández-Alfaro, F; Nart, J

2016-07-01

The use of titanium implants is well documented and they have high survival and success rates. However, when used as reduced-diameter implants, the risk of fracture is increased. Narrow diameter implants (NDIs) of titanium-zirconium (Ti-Zr) alloy have recently been developed (Roxolid; Institut Straumann AG). Ti-Zr alloys (two highly biocompatible materials) demonstrate higher tensile strength than commercially pure titanium. The aim of this systematic review was to summarize the existing clinical evidence on dental NDIs made from Ti-Zr. A systematic literature search was performed using the Medline database to find relevant articles on clinical studies published in the English language up to December 2014. Nine clinical studies using Ti-Zr implants were identified. Overall, 607 patients received 922 implants. The mean marginal bone loss was 0.36±0.06mm after 1 year and 0.41±0.09mm after 2 years. The follow-up period ranged from 3 to 36 months. Mean survival and success rates were 98.4% and 97.8% at 1 year after implant placement and 97.7% and 97.3% at 2 years. Narrow diameter Ti-Zr dental implants show survival and success rates comparable to regular diameter titanium implants (>95%) in the short term. Long-term follow-up clinical data are needed to confirm the excellent clinical performance of these implants. Copyright © 2016 International Association of Oral and Maxillofacial Surgeons. Published by Elsevier Ltd. All rights reserved.

Reduced yield stress for zirconium exposed to iodine: Reactive force field simulation

DOE PAGES

Rossi, Matthew L.; Taylor, Christopher D.; van Duin, Adri C. T.

2014-11-04

Iodine-induced stress-corrosion cracking (ISCC), a known failure mode for nuclear fuel cladding, occurs when iodine generated during the irradiation of a nuclear fuel pellet escapes the pellet through diffusion or thermal cracking and chemically interacts with the inner surface of the clad material, inducing a subsequent effect on the cladding’s resistance to mechanical stress. To complement experimental investigations of ISCC, a reactive force field (ReaxFF) compatible with the Zr-I chemical and materials systems has been developed and applied to simulate the impact of iodine exposure on the mechanical strength of the material. The study shows that the material’s resistance tomore » stress (as captured by the yield stress of a high-energy grain boundary) is related to the surface coverage of iodine, with the implication that ISCC is the result of adsorption-enhanced decohesion.« less

The Crystal Structure of Thorium and Zirconium Dihydrides by X-ray and Neutron Diffraction

DOE R&D Accomplishments Database

Rundle, R.E.; Shull, C.G.; Wollan, E.O.

1951-04-20

Thorium forms a tetragonal lower hydride of composition ThH{sub 2}. The hydrides ThH{sub 2}, ThD{sub 2}, and ZrD{sub 2} have been studied by neutron diffraction in order that hydrogen positions could be determined. The hydrides are isomorphous, and have a deformed fluorite structure. Metal-hydrogen distances in thorium hydride are unusually large, as in UH{sub 3}. Thorium and zirconium scattering amplitudes and a revised scattering amplitude for deuterium are reported.

The origin of 2.7 eV blue luminescence band in zirconium oxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Perevalov, T. V., E-mail: timson@isp.nsc.ru; Zhuravlev, K. S.; Gritsenko, V. A.

2014-12-28

The luminescence spectra of non-stoichiometric zirconium oxide film series with different oxygen vacancies' concentrations show the blue photoluminescence band centered near a 2.7 eV peak. There is a broad band at 5.2 eV in the luminescence excitation spectrum for blue emission. The ab-initio quantum-chemical calculation gives a peak in the optical absorption at 5.1 eV for the oxygen vacancy in cubic ZrO{sub 2}. It was concluded that the 2.7 eV blue luminescence excited near 5.2 eV in a zirconium oxide film is associated with the oxygen vacancy.

An investigation on the preparation of nanocrystalline hydrous zirconia from zirconium tungstate

NASA Astrophysics Data System (ADS)

Antunes, M.; Perottoni, C. A.; Gouvêa, D.; Machado, G.; Zorzi, J. E.

2018-02-01

Hydrous nanocrystalline zirconia was prepared from an unusual precursor—the bimetallic oxide zirconium tungstate (ZrW2O8)—in alkaline medium. Different experimental conditions (NaOH concentration, time and temperature) were used to investigate the effects on crystallographic, morphological, chemical and thermal characteristics of the products. The resulting materials are composed of particles with a crystal structure similar to that of cubic ZrO2 (or a mixture of tetragonal and cubic phases, depending on the synthesis conditions), with particle size around 5 nm and crystallites around 3 nm in diameter. These particles form high surface area agglomerates, exhibiting mesoporosity and capacity for adsorption of water and carbon dioxide. The synthesis mechanism appears to be constituted, first, by a chemical substitution reaction between the WO4 tetrahedra and hydroxyl ions, with subsequent solubilization of the structure. Indeed, excess hydroxyls in the medium form colloidal zirconium ions which polymerize/condense, generating crystalline nuclei in a process facilitated by heterogeneous nucleation and supersaturation. The presence of residual tungsten in all samples appears to be a key element for stabilizing the size and crystalline structure of the materials produced.

Preparation of highly-oxidized starch using hydrogen peroxide and its application as a novel ligand for zirconium tanning of leather.

PubMed

Yu, Yue; Wang, Ya-Nan; Ding, Wei; Zhou, Jianfei; Shi, Bi

2017-10-15

A series of highly-oxidized starch (HOS) were prepared using H 2 O 2 and a copper-iron catalyst as a desired ligand for zirconium tanning of leather. The effects of catalyst and H 2 O 2 dosages, and reaction temperature on the oxidation degree (OD, represented as the amount of carbonyl and carboxyl groups derived) of starch were investigated. The OD reached 76.2% when oxidation was conducted using 60% H 2 O 2 and 0.015% catalyst at 98°C for 2h. 13 C NMR and FT-IR illustrated carbonyl and carboxyl groups were formed in HOS after oxidation. GPC and laser particle size analyses indicated the decrease of HOS molecular size with increasing H 2 O 2 dosage and OD. HOS with moderate OD and molecular weight was able to coordinate with zirconium and remarkably improve tanning process. Leather tanned by Zr complexes using HOS-60 (60% H 2 O 2 , Mn 3516g/mol) as ligand presented considerably better physical and organoleptic properties than those of traditional Zr-tanned leather. Copyright © 2017 Elsevier Ltd. All rights reserved.

Superior removal of arsenic from water with zirconium metal-organic framework UiO-66.

PubMed

Wang, Chenghong; Liu, Xinlei; Chen, J Paul; Li, Kang

2015-11-12

In this study, water stable zirconium metal-organic framework (UiO-66) has been synthesized and for the first time applied as an adsorbent to remove aquatic arsenic contamination. The as-synthesized UiO-66 adsorbent functions excellently across a broad pH range of 1 to 10, and achieves a remarkable arsenate uptake capacity of 303 mg/g at the optimal pH, i.e., pH = 2. To the best of our knowledge, this is the highest arsenate As(V) adsorption capacity ever reported, much higher than that of currently available adsorbents (5-280 mg/g, generally less than 100 mg/g). The superior arsenic uptake performance of UiO-66 adsorbent could be attributed to the highly porous crystalline structure containing zirconium oxide clusters, which provides a large contact area and plenty of active sites in unit space. Two binding sites within the adsorbent framework are proposed for arsenic species, i.e., hydroxyl group and benzenedicarboxylate ligand. At equilibrium, seven equivalent arsenic species can be captured by one Zr6 cluster through the formation of Zr-O-As coordination bonds.

Superior removal of arsenic from water with zirconium metal-organic framework UiO-66

PubMed Central

Wang, Chenghong; Liu, Xinlei; Chen, J. Paul; Li, Kang

2015-01-01

In this study, water stable zirconium metal-organic framework (UiO-66) has been synthesized and for the first time applied as an adsorbent to remove aquatic arsenic contamination. The as-synthesized UiO-66 adsorbent functions excellently across a broad pH range of 1 to 10, and achieves a remarkable arsenate uptake capacity of 303 mg/g at the optimal pH, i.e., pH = 2. To the best of our knowledge, this is the highest arsenate As(V) adsorption capacity ever reported, much higher than that of currently available adsorbents (5–280 mg/g, generally less than 100 mg/g). The superior arsenic uptake performance of UiO-66 adsorbent could be attributed to the highly porous crystalline structure containing zirconium oxide clusters, which provides a large contact area and plenty of active sites in unit space. Two binding sites within the adsorbent framework are proposed for arsenic species, i.e., hydroxyl group and benzenedicarboxylate ligand. At equilibrium, seven equivalent arsenic species can be captured by one Zr6 cluster through the formation of Zr-O-As coordination bonds. PMID:26559001

Adsorption Behavior of Rare Earth Metal Cations in the Interlayer Space of γ-ZrP.

PubMed

Takei, Takahiro; Iidzuka, Kiyoaki; Miura, Akira; Yanagida, Sayaka; Kumada, Nobuhiro; Magome, Eisuke; Moriyoshi, Chikako; Kuroiwa, Yoshihiro

2016-10-04

Adsorption competencies of rare earth metal cations in γ-zirconium phosphate were examined by ICP, synchrotron X-ray diffraction (SXRD), and ab initio simulation. The adsorption amounts are around 0.06-0.10 per zirconium phosphate. From the SXRD patterns of the adsorbed samples, the basal spacing estimated by c sin β increased linearly with an increasing ionic radius of rare earth metal cation, though a and b lattice constants show no change. These SXRD patterns can be classified into four groups that have different super lattices. The four superlattices have multiplicities of x131, x241, and x221 for the xabc axis, and the location of the rare earth metal cation in the original unit cell changes depending on the superlattice cell. In the x131 superlattice, Yb and Er occupied the site near the zirconium phosphate layer, though La and Ce in the x221 superlattice remained in the center position between the phosphate sheet. For the ab initio simulation of γ-ZrP with the typical rare earth metal cations (Tb, Eu, Dy, and La), the results of simulation show a similar tendency of the position estimated by SXRD refinements.

Ab-initio study of high temperature lattice dynamics of BCC zirconium (β-Zr) and uranium (γ-U)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ghosh, Partha S., E-mail: parthasarathi13@gmail.com; Arya, A., E-mail: parthasarathi13@gmail.com; Dey, G. K., E-mail: parthasarathi13@gmail.com

2014-04-24

Using self consistent ab-initio lattice dynamics calculations, we show that bcc structures of Zr and U phases become stable at high temperature by phonon-phonon interactions. The calculated temperature dependent phonon dispersion curve (PDC) of β-Zr match excellently with experimental PDC. But the calculated PDC for γ-U shows negative phonon frequencies even at solid to liquid transition temperature. We show that this discrepancy is due to an overestimation of instability depth of bcc U phase which is removed by incorporation of spin-orbit coupling in the electronic structure calculations.

High-Temperature Stability and Grain Boundary Complexion Formation in a Nanocrystalline Cu-Zr Alloy

NASA Astrophysics Data System (ADS)

Khalajhedayati, Amirhossein; Rupert, Timothy J.

2015-12-01

Nanocrystalline Cu-3 at.% Zr powders with ~20 nm average grain size were created with mechanical alloying and their thermal stability was studied from 550-950°C. Annealing drove Zr segregation to the grain boundaries, which led to the formation of amorphous intergranular complexions at higher temperatures. Grain growth was retarded significantly, with 1 week of annealing at 950°C, or 98% of the solidus temperature, only leading to coarsening of the average grain size to 54 nm. The enhanced thermal stability can be connected to both a reduction in grain boundary energy with doping as well as the precipitation of ZrC particles. High mechanical strength is retained even after these aggressive heat treatments, showing that complexion engineering may be a viable path toward the fabrication of bulk nanostructured materials with excellent properties.

Reduced-Gravity Measurements of the Effect of Oxygen on Properties of Zirconium

NASA Technical Reports Server (NTRS)

Zhao, J.; Lee, J.; Wunderlich, R.; Fecht, H.-J.; Schneider, S.; SanSoucie, M.; Rogers, J.; Hyers, R.

2016-01-01

The influence of oxygen on the thermophysical properties of zirconium is being investigated using MSL-EML (Material Science Laboratory - Electromagnetic Levitator) on ISS (International Space Station) in collaboration with NASA, ESA (European Space Agency), and DLR (German Aerospace Center). Zirconium samples with different oxygen concentrations will be put into multiple melt cycles, during which the density, viscosity, surface tension, heat capacity, and electric conductivity will be measured at various undercooled temperatures. The facility check-up of MSL-EML and the first set of melting experiments have been successfully performed in 2015. The first zirconium sample will be tested near the end of 2015. As part of ground support activities, the thermophysical properties of zirconium and ZrO were measured using a ground-based electrostatic levitator located at the NASA Marshall Space Flight Center. The influence of oxygen on the measured surface tension was evaluated. The results of this research will serve as reference data for those measured in ISS.

Direct synthesis of zirconium powder by magnesium reduction

NASA Astrophysics Data System (ADS)

Lee, Dong-Won; Yun, Jung-Yeul; Yoon, Sung-Won; Wang, Jei-Pil

2013-05-01

The direct synthesis of zirconium powder has been conducted through an analysis of the chemical reaction between evaporated ZrCl4 and molten magnesium over a range of reduction temperatures, concentration of hydrochloric acid, and stirring time. The observed results indicated that the purity of zirconium powder increased with increased stirring time, and Mg and MgCl2 were removed by 10 wt% of hydrochloric acid solution. The pure zirconium powder was obtained by stirring again for 5 h using 5 wt% of hydrochloric acid solution. It was noted that the mean particle size increased when the reaction temperature was increased, and the size of the powder at 1,123 K and 1,173 K was found to be 10 μm and 15 μm, respectively. In addition, the purity of the powder was also improved with temperature, and its purity finally reached up to 99.5% at 1,250 K. Overall, pure zirconium powder was obtained after a stirring stage for 5 hours using 5 wt% of hydrochloric acid solution.

In-situ high-pressure powder X-ray diffraction study of α-zirconium phosphate.

PubMed

Readman, Jennifer E; Lennie, Alistair; Hriljac, Joseph A

2014-06-01

The high-pressure structural chemistry of α-zirconium phosphate, α-Zr(HPO4)2·H2O, was studied using in-situ high-pressure diffraction and synchrotron radiation. The layered phosphate was studied under both hydrostatic and non-hydrostatic conditions and Rietveld refinement carried out on the resulting diffraction patterns. It was found that under hydrostatic conditions no uptake of additional water molecules from the pressure-transmitting medium occurred, contrary to what had previously been observed with some zeolite materials and a layered titanium phosphate. Under hydrostatic conditions the sample remained crystalline up to 10 GPa, but under non-hydrostatic conditions the sample amorphized between 7.3 and 9.5 GPa. The calculated bulk modulus, K0 = 15.2 GPa, showed the material to be very compressible with the weak linkages in the structure of the type Zr-O-P.

Biocompatibility Study of Zirconium-Based Bulk Metallic Glasses for Orthopedic Applications

NASA Astrophysics Data System (ADS)

He, Wei; Chuang, Andrew; Cao, Zheng; Liaw, Peter K.

2010-07-01

Bulk metallic glasses (BMGs) represent an emerging class of materials that offer an attractive combination of properties, such as high strength, low modulus, good fatigue limit, and near-net-shape formability. The BMGs have been explored in mechanical, chemical, and magnetic applications. However, little research has been attracted in the biomedical field. In this work, we study the potential of BMGs for the orthopedic repair and replacement. We report the biocompatibility study of zirconium (Zr)-based solid BMGs using mouse osteoblast cells. Cell attachment, proliferation, and differentiation are compared to Ti-6Al-4V, a well-studied alloy biomaterial. Our in-vitro study has demonstrated that cells cultured on the Zr-based BMG substrate showed higher attachment, alkaline phosphatase activity, and bone matrix deposition compared to those grown on the control Ti alloy substrate. Cytotoxicity staining also revealed the remarkable viability of cells growing on the BMG substrates.

Point defects in crystalline zircon (zirconium silicate), ZrSiO4: electron paramagnetic resonance studies

NASA Astrophysics Data System (ADS)

Tennant, W. C.; Claridge, R. F. C.; Walsby, C. J.; Lees, N. S.

This article outlines the present state of knowledge of paramagnetic defects in crystalline zircon as obtained mainly, but not exclusively, from electron paramagnetic resonance (EPR) studies in crystalline zircon (zirconium silicate, ZrSiO4). The emphasis is on single-crystal studies where, in principle, unambiguous analysis is possible. Firstly, the crystallography of zircon is presented. Secondly, the relationships between available crystal-site symmetries and the symmetries of observed paramagnetic species in zircon, and how these observations lead to unambiguous assignments of point-group symmetries for particular paramagnetic species are detailed. Next, spin-Hamiltonian (SH) analysis is discussed with emphasis on the symmetry relationships that necessarily exist amongst the Laue classes of the crystal sites in zircon, the paramagnetic species occupying those sites and the SH itself. The final sections of the article then survey the results of EPR studies on zircon over the period 1960-2002.

Review of anhydrous zirconium-hafnium separation techniques. Information circular/1984

DOE Office of Scientific and Technical Information (OSTI.GOV)

Skaggs, R.L.; Rogers, D.T.; Hunter, D.B.

1983-12-01

Sixteen nonaqueous techniques conceived to replace the current aqueous scheme for separating hafnium and zirconium tetrachlorides were reviewed and evaluated by the Bureau of Mines. The methods are divided into two classes: separation by fractional volatilization of the tetrachlorides, which takes advantage of the higher volatility of hafnium tetrachloride; and separation by chemical techniques, based on differences in chemical behavior of the two tetrachlorides. The criteria used to evaluate separation methods were temperature, pressure, separation factor per equilibrium stage, complexity, compatibility with existing technology, and potential for continuous operation. Three processes were selected as being most promising: (1) high-pressure distillation,more » (2) extractive distillation from a molten salt, and (3) preferential reduction of gaseous ZrCl4. Any of the proposed nonaqueous Hf-Zr separation schemes must be supplemented with additional purification to remove trace impurities.« less

Synthesis of zirconium dioxide by ultrasound assisted precipitation: effect of calcination temperature.

PubMed

Prasad, Krishnamurthy; Pinjari, D V; Pandit, A B; Mhaske, S T

2011-09-01

Nanostructured zirconium dioxide was synthesized from zirconyl nitrate using both conventional and ultrasound assisted precipitation in alkaline medium. The synthesized samples were calcinated at temperatures ranging from 400°C to 900°C in steps of 100°C. The ZrO(2) specimens were characterized using X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). The thermal characteristics of the samples were studied via Differential Scanning Calorimetry-Thermo-Gravimetry Analysis (DSC-TGA). The influence of the calcination temperature on the phase transformation process from monoclinic to tetragonal to cubic zirconia and its consequent effect on the crystallite size and % crystallinity of the synthesized ZrO(2) was studied and interpreted. It was observed that the ultrasound assisted technique helped to hasten to the phase transformation and also at some point resulted in phase stabilization of the synthesized zirconia. Copyright © 2011 Elsevier B.V. All rights reserved.

Carbon diffusion in bulk hcp zirconium: A multi-scale approach

NASA Astrophysics Data System (ADS)

Xu, Y.; Roques, J.; Domain, C.; Simoni, E.

2016-05-01

In the framework of the geological repository of the used fuel claddings of pressurized water reactor, carbon behavior in bulk zirconium is studied by periodic Density Functional Theory calculations. The C interstitial sites were investigated and it was found that there are two possible carbon interstitial sites: a distorted basal tetragonal site and an octahedral site. There are four types of possible atomic jumps between them. After calculating the migration energies, the attempt frequencies and the jump probabilities for each possible migration path, kinetic Monte Carlo (KMC) simulations were performed to simulate carbon diffusion at the macroscopic scale. The results show that carbon diffusion in pure Zr bulk is extremely limited at the storage temperature (50 °C). Since there are defects in Zr bulk, in a second step, the effect of atomic vacancy was studied and it was proved that vacancies cannot increase carbon diffusion.

A novel method for the synthesis of zirconia powder

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bohe, A.E.; Pasquevich, D.M.

A novel method for the synthesis of zirconia powder is presented in this paper. The formation of fine particles of zirconia takes place when metallic zirconium and hematite are heated in the presence of gaseous chlorine. The overall process, which can be described by the following reaction: 3 Zr(s) + 2 Fe{sub 2}O{sub 3}(s) {r_arrow} 3 ZrO{sub 2}(s) + 4 Fe(s), occurs by a mass-transport mechanism through the vapor phase between 723 and 1223 K. The vapor-mass transport among the solid species takes place by means of zirconium and iron chlorides. The fundamentals of synthesis are discussed on the basismore » of a detailed thermodynamic analysis of reactions involved in the process, as well as by a characterization of the solid phases formed at various temperatures at XRD and SEM examinations.« less

The Performance of a Zirconium-based Root Filling Material with Artifact Reduction Properties in the Detection of Artificially Induced Root Fractures Using Cone-beam Computed Tomographic Imaging.

PubMed

Fox, Aaron; Basrani, Bettina; Lam, Ernest W N

2018-05-01

Limited field of view cone-beam computed tomographic (CBCT) imaging has been used to augment clinical testing of vertical root fractures (VRFs); however, the presence of gutta-percha (GP) in the canal space generates substantial imaging artifacts that make fracture detection difficult. The purpose of this study was to evaluate the influence of a zirconium (Zr)-based root filling material with radiologic properties that reduce beam hardening (BH) artifacts using CBCT imaging in the in vitro diagnosis of VRFs. One hundred seventy-six single-rooted mandibular premolar teeth were obtained, and half of these teeth were filled with GP or Zr (CPoint; EndoTechnologies, LLC, Shrewsbury, MA). VRFs were induced in 44 decoronated teeth in each group using an Instron (Norwood, MA) Universal Testing Machine. Each root was then placed in a dry human mandible and imaged with the Carestream 9000 3D CBCT system (Carestream Dental, Atlanta, GA). The images were evaluated by 6 oral maxillofacial radiologists (OMRs) and residents. The sensitivity was greater for detecting VRFs in the Zr group than the GP group (P = .035). However, the specificity was greater for the GP group than the Zr group (P = .028). Receiver operating characteristic area under the curve values were greater for the Zr group than the GP group, but these differences were not statistically significant. The OMRs outperformed the residents in the detection of VRFs in the Zr group with respect to specificity (P = .006) and positive predictive value (P = .012). The reduced BH of the Zr group improved the sensitivity of the detection of artificially induced VRFs. The ability to detect VRFs in the Zr group was further enhanced by clinical experience. Copyright © 2018 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Effect of structural defects on electronic and magnetic properties of ZrS2 monolayer

NASA Astrophysics Data System (ADS)

Wang, Haiyang; Zhao, Xu; Gao, Yonghui; Wang, Tianxing; Wei, Shuyi

2018-04-01

We aimed at ten configurations of vacancy defects and used the first-principles methods based on density functional theory to research electronic and magnetic properties of ZrS2 monolayer. Results show that the system of two-zirconium vacancy (V2zr) and one Zr atom + one S atom vacancy (V1Zr+1S) can induce to total spin magnetic moment of 0.245μB and 0.196μB, respectively. In addition, three and six S atoms vacancy can induce corresponding system to manifest spin magnetic moment of 0.728μB and 3.311μB, respectively. In S atom vacancy defects, vacancy defects can transform the system from semiconductor to metal, several of the Zr atoms and adjacent S atoms display antiferromagnetism coupling in three apart S atom vacancy defects. Vacancy defects can make the intrisic monolayer ZrS2 transform semiconductor into metal. These results are important for the achievement of spin devices based on ZrS2 semiconductor.

Atomic and electronic structures of an extremely fragile liquid.

PubMed

Kohara, Shinji; Akola, Jaakko; Patrikeev, Leonid; Ropo, Matti; Ohara, Koji; Itou, Masayoshi; Fujiwara, Akihiko; Yahiro, Jumpei; Okada, Junpei T; Ishikawa, Takehiko; Mizuno, Akitoshi; Masuno, Atsunobu; Watanabe, Yasuhiro; Usuki, Takeshi

2014-12-18

The structure of high-temperature liquids is an important topic for understanding the fragility of liquids. Here we report the structure of a high-temperature non-glass-forming oxide liquid, ZrO2, at an atomistic and electronic level. The Bhatia-Thornton number-number structure factor of ZrO2 does not show a first sharp diffraction peak. The atomic structure comprises ZrO5, ZrO6 and ZrO7 polyhedra with a significant contribution of edge sharing of oxygen in addition to corner sharing. The variety of large oxygen coordination and polyhedral connections with short Zr-O bond lifetimes, induced by the relatively large ionic radius of zirconium, disturbs the evolution of intermediate-range ordering, which leads to a reduced electronic band gap and increased delocalization in the ionic Zr-O bonding. The details of the chemical bonding explain the extremely low viscosity of the liquid and the absence of a first sharp diffraction peak, and indicate that liquid ZrO2 is an extremely fragile liquid.

A study of binuclear zirconium hydride catalysts of the hydrogenolysis of alkanes by the density functional theory method

NASA Astrophysics Data System (ADS)

Ustynyuk, L. Yu.; Fast, A. S.; Ustynyuk, Yu. A.; Lunin, V. V.

2012-06-01

Binuclear hydride centers containing two Zr(IV) atoms are suggested as promising catalysts for the hydrogenolysis of alkanes under mild conditions ( T < 450 K, p ˜ 1 atm). Reactions of model compounds L2(H)Zr(X)2Zr(H)L2 (X = H, L = OSi≡ ( 4a), X = L = OMe ( 4d)), L(H)Zr(O)2Zr(H)L (L = OSi≡ ( 4b), Cp( 4c)) and (≡SiO)2(H)Zr-O-Zr(H)(OSi≡)2 ( 4e and 4f) with the propane molecule were studied using the density functional theory method. The results show that centers of the 4a, 4e, and 4f types and especially 4b are promising catalysts of the hydrogenolysis of alkanes due to a high degree of unsaturation of two Zr atoms and their sequential participation in the splitting of the C-C bond and hydrogenation of ethylene formed as a result of splitting.

First-principles study of fission gas incorporation and migration in zirconium nitride

DOE PAGES

Mei, Zhi-Gang; Liang, Linyun; Yacout, Abdellatif M.

2017-03-24

To evaluate the effectiveness of ZrN as a diffusion barrier against fission gases, we investigate in this paper the incorporation and migration of fission gas atoms, with a focus on Xe, in ZrN by first-principles calculations. The formations of point defects in ZrN, including vacancies, interstitials, divacancies, Frenkel pairs, and Schottky defects, are first studied. Among all the defects, the Schottky defect with two vacancies as first nearest neighbor is predicted to be the most favorable incorporation site for fission gas Xe in ZrN. The migration of Xe gas atom in ZrN is investigated through two diffusion mechanisms, i.e., interstitialmore » and vacancy-assisted diffusions. The migration barrier of Xe gas atom through the intrinsic interstitials in ZrN is considerably lower than that through vacancies. Finally, therefore, at low temperatures fission gas Xe atoms diffuse mainly through interstitials in single crystal ZrN, whereas at high temperatures Xe may diffuse in ZrN assisted by vacancies.« less

Cyclotron production for the radiometal Zirconium-89 with an IBA cyclone 18/9 and COSTIS solid target system (STS)

NASA Astrophysics Data System (ADS)

Dabkowski, A. M.; Probst, K.; Marshall, C.

2012-12-01

The development of biological targeting agents such as proteins, peptides, antibodies and nanoparticles with a range of biological half-lives demands the production of new radionuclides with half-lives (physical) complementary to these biological properties. Zirconium-89 (89Zr) is a promising radionuclide for development of new immuno-PET agents due to its convenient half-life of 78.4 h, β+ emission rate of 23%, low maximum energy of 0.9 MeV resulting in good spatial resolution, stable daughter isotope of Yttrium-89 (89Y) and favorable imaging characteristics, with only one significant γ-line of 909 keV emitted during decay alongside the 511 keV positron photons. Our aim was to prove that isotopically pure 89Zr could be produced in an IBA Cyclone 18/9 cyclotron equipped with a COSTIS STS using the 89Y(p,n)89Zr reaction and optimise the yield by reducing the beam degrader thickness without producing either 88Zr or 88Y. The degradation of the beam energy with 400 and 500 μm thick Niobium foils were achieved without overheating problems with 2-3 hours long irradiation times. From repeated measurements of activity, it was clear that there is a bi-exponential decay of radioactivity due to the short lived 89mZr and 89Zr. The measured half-life of the longer lived radionulide was consistent with value for 89Zr. The energy spectrum from 89Zr had energy peaks at 511 keV and 909 keV and was consistent with 89Zr. Production of 89Zr with 500 μm thick Niobium beam degrader (Ep = 9.8MeV) was achieved, without producing either 88Zr or 88Y. It was necessary to wait at least 4 hours before measuring the activity and decay correct in order to calculate the 89gZr activity at the end of cyclotron production. Degrading the proton beam to 10 MeV produces radionuclidically pure 89Zr with yields from 8 to 9 MBq/μAh. Whilst this is enough for pre-clinical use, the yield is not enough for either clinical use or commercial supply. Using thinner beam degraders to increase the proton beam energy increases the radionuclidic yield but it is not yet possible to exclude the presence of radionuclidic impurities.

Toughness of Wear-Resistant Cu-Zr-Based Bulk Metallic Glasses

NASA Astrophysics Data System (ADS)

Andersen, Laura M.

Bulk metallic glasses (BMGs) have the potential to exhibit exceptional wear-resistance due to their high hardness and strength. Combined with their other unique properties, this makes them ideal candidates for a wide range of technological applications (e.g. gears, bearings, biomaterials). In the course of this dissertation, high-glass-forming bulk metallic glasses are prepared and characterized in order to identify wear-resistant compositions and optimize their toughness. First, a comprehensive study identifies a class of Cu-Zr-based BMGs that exhibit more exceptional wear performance than other BMGs. The results demonstrate that when BMGs are designed properly, they exhibit wear properties that compete with, and can surpass, state-of-the-art engineering materials. It is identified that, in order to optimize the wear performance of Cu-Zr-based BMG gears, toughness should be maximized. Second, the notch toughness of wear-resistant Cu43Zr 43Al7Be7 BMGs with in-situ crystallization is investigated. In order to identify in-situ crystallization using X-ray diffraction (XRD) with Cu K? radiation, extremely long dwell times and high X-ray fluxes are required. This demonstrates the importance of reporting operating parameters when trying to evaluate the amorphous nature of BMGs. XRD, energy-dispersive X-ray spectroscopy (EDS) and electron backscatter diffraction (EBSD) are used to identify the metastable crystalline phase. The notch toughness is found to correlate closely with the amount of crystallization and the composition of the remaining amorphous matrix. Finally, the effect of substituting standard-grade zirconium lump (99.8% excluding up to 4% hafnium) for high-purity zirconium crystal bar (99.5%) in Cu43Zr43Al7Be7 is investigated. Introducing low-purity zirconium significantly decreases the glass-forming-ability and reduces the notch toughness of the BMG. Furthermore, Weibull statistics provide an analysis of the variability in toughness for high-purity ingots synthesized both in a small laboratory arc-melter and synthesized commercially. The dissertation concludes with a summary of key findings that have led to our increase in knowledge and a discussion of particularly pressing directions for future research in this field.

[A surface reacted layer study of titanium-zirconium alloy after dental casting].

PubMed

Zhang, Y; Guo, T; Li, Z; Li, C

2000-10-01

To investigate the influence of the mold temperature on the surface reacted layer of Ti-Zr alloy castings. Ti-Zr alloy was casted into a mold which was made of a zircon (ZrO2.SiO2) for inner coating and a phosphate-bonded material for outer investing with a casting machine (China) designed as vacuum, pressure and centrifuge. At three mold temperatures (room temperature, 300 degrees C, 600 degrees C) the Ti-Zr alloy was casted separately. The surface roughness of the castings was calculated by instrument of smooth finish (China). From the surface to the inner part the Knoop hardness and thickness in reacted layer of Ti-Zr alloy casting was measured. The structure of the surface reacted layer was analysed by SEM. Elemental analyses of the interfacial zone of the casting was made by element line scanning observation. The surface roughness of the castings was increased significantly with the mold temperature increasing. At a higher mold temperature the Knoop hardness of the reactive layer was increased. At the three mold temperature the outmost surface was very hard, and microhardness data decreased rapidly where they reached constant values. The thickness was about 85 microns for castings at room temperature and 300 degrees C, 105 microns for castings at 600 degrees C. From the SEM micrograph of the Ti-Zr alloy casting, the surface reacted layer could be divided into three different layers. The first layer was called non-structure layer, which thickness was about 10 microns for room temperature group, 20 microns for 300 degrees C and 25 microns for 600 degrees C. The second layer was characterized by coarse-grained acicular crystal, which thickness was about 50 microns for three mold temperatures. The third layer was Ti-Zr alloy. The element line scanning showed non-structure layer with higher level of element of O, Al, Si and Zr, The higher the mold temperature during casting, the deeper the Si permeating and in the second layer the element Si could also be found. The mold temperature is one of the major factors influencing to casting quality. In order to reduce the surface reacted layer of Ti-Zr alloy castings, the lower mold temperature and the investment without Si should be chosen.

Effects of different radio-opacifying agents on physicochemical and biological properties of a novel root-end filling material

PubMed Central

Lü, Xiao-Ying; Liu, Gen-Di

2018-01-01

Background/Purpose Radio-opacity is an essential attribute of ideal root-end filling materials because it is important for clinicians to observe root canal filling and to facilitate the follow-up instructions. The novel root-end filling material (NRFM) has good cytocompatibility and physicochemical properties but low intrinsic radio-opacity value. To improve its radio-opacity value, three novel radio-opaque root-end filling materials (NRRFMs) were developed by adding barium sulphate (NRFM-Ba), bismuth trioxide (NRFM-Bi) and zirconium dioxide (NRFM-Zr) to NRFM, respectively. The purpose of this study was to identify the suitable radio-opacifier for NRFM through evaluating their physicochemical and biological properties, in comparison with NRFM and glass ionomer cement (GIC). Methods NRRFMs were characterized using X-ray diffraction (XRD) and Fourier transform infrared spectrophotometry (FTIR). Physicochemical properties including setting time, compressive strength, porosity, pH variation, solubility, washout resistance, contact angle and radiopacity were investigated. Cytocompatibility of both freshly mixed and set NRRFMs was investigated by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay. Alkaline phosphatase (ALP) activity assay and alizarin red staining were used to investigate the osteogenic differentiation potential of NRFM-Zr. Data were analyzed using two-way ANOVA (pH variation, solubility and ALP activity) and one-way ANOVA (for the other variables). Results (1) NRRFMs were primarily composed of hydroxyapatite, calcium carboxylate salt and the corresponding radio-opacity agents (barium sulphate, bismuth trioxide or zirconium dioxide). (2) Besides similar physicochemical properties in terms of setting time, pH variation, solubility, washout resistance and contact angle to NRFM, NRFM-Bi and NRFM-Zr exhibited lower porosity and greater compressive strength after being set for 7 days and their radio-opacity were greater than the 3 mm aluminium thickness specified in ISO 6876 (2001). (3) MTT assay revealed that freshly mixed and set NRFM-Zr presented better cell viability than NRFM-Ba and NRFM-Bi at 24 hours and 48 hours (P<0.05). (4) NRFM-Zr significantly enhanced ALP activity and calcium formation of human osteoblast-like Saos-2 cells when compared with negative group and GIC (P<0.05). Conclusion NRFM-Zr presents desirable physicochemical and biological properties, thus zirconium dioxide may be a suitable radio-opacifier for NRFM. PMID:29420559

Effects of different radio-opacifying agents on physicochemical and biological properties of a novel root-end filling material.

PubMed

Chen, Yao-Zhong; Lü, Xiao-Ying; Liu, Gen-Di

2018-01-01

Radio-opacity is an essential attribute of ideal root-end filling materials because it is important for clinicians to observe root canal filling and to facilitate the follow-up instructions. The novel root-end filling material (NRFM) has good cytocompatibility and physicochemical properties but low intrinsic radio-opacity value. To improve its radio-opacity value, three novel radio-opaque root-end filling materials (NRRFMs) were developed by adding barium sulphate (NRFM-Ba), bismuth trioxide (NRFM-Bi) and zirconium dioxide (NRFM-Zr) to NRFM, respectively. The purpose of this study was to identify the suitable radio-opacifier for NRFM through evaluating their physicochemical and biological properties, in comparison with NRFM and glass ionomer cement (GIC). NRRFMs were characterized using X-ray diffraction (XRD) and Fourier transform infrared spectrophotometry (FTIR). Physicochemical properties including setting time, compressive strength, porosity, pH variation, solubility, washout resistance, contact angle and radiopacity were investigated. Cytocompatibility of both freshly mixed and set NRRFMs was investigated by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay. Alkaline phosphatase (ALP) activity assay and alizarin red staining were used to investigate the osteogenic differentiation potential of NRFM-Zr. Data were analyzed using two-way ANOVA (pH variation, solubility and ALP activity) and one-way ANOVA (for the other variables). (1) NRRFMs were primarily composed of hydroxyapatite, calcium carboxylate salt and the corresponding radio-opacity agents (barium sulphate, bismuth trioxide or zirconium dioxide). (2) Besides similar physicochemical properties in terms of setting time, pH variation, solubility, washout resistance and contact angle to NRFM, NRFM-Bi and NRFM-Zr exhibited lower porosity and greater compressive strength after being set for 7 days and their radio-opacity were greater than the 3 mm aluminium thickness specified in ISO 6876 (2001). (3) MTT assay revealed that freshly mixed and set NRFM-Zr presented better cell viability than NRFM-Ba and NRFM-Bi at 24 hours and 48 hours (P<0.05). (4) NRFM-Zr significantly enhanced ALP activity and calcium formation of human osteoblast-like Saos-2 cells when compared with negative group and GIC (P<0.05). NRFM-Zr presents desirable physicochemical and biological properties, thus zirconium dioxide may be a suitable radio-opacifier for NRFM.

Chlorination of zirconium (0001) surface: A first-principles study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, E.; Weck, Philippe F; Poineau, F.

The mechanisms and energetics of Zr(0001) surface chlorination by dissociative adsorption of gaseous Cl 2, and associated speciation and surface degradation processes, have been investigated within the framework of density functional theory. Chlorination of Zr(0001) is predicted to be exothermic by 3 eV/Cl for dissociative adsorption of a single Cl 2 molecule, followed by exothermic chlorination to 1ML and 2 ML under Cl-rich conditions, with respective energy gains of 1.93 and 2.79 eV/Cl. Calculations also show that exfoliation of the top Cl-Zr-Cl sandwich layers is exothermic and most energetically favorable, and can thus be considered as a leading mechanism formore » Zr(0001) surface dissolution. Finally, consistent with experimental findings, formation of ZrCl 4 molecular products is also found to be dominant during Zr(0001) chlorination.« less

Chlorination of zirconium (0001) surface: A first-principles study.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Eunja; Weck, Philippe F; Borjas, Rosendo

Here, the mechanisms and energetics of Zr(0001) surface chlorination by dissociative adsorption of gaseous Cl 2, and associated speciation and surface degradation processes, have been investigated within the framework of density functional theory. Chlorination of Zr(0001) is predicted to be exothermic by ~3 eV/Cl for dissociative adsorption of a single Cl 2 molecule, followed by exothermic chlorination to 1ML and 2 ML under Cl-rich conditions, with respective energy gains of 1.93 and 2.79 eV/Cl. Calculations also show that exfoliation of the top Cl-Zr-Cl sandwich layers is exothermic and most energetically favorable, and can thus be considered as a leading mechanismmore » for Zr(0001) surface dissolution. Consistent with experimental findings, formation of ZrCl 4 molecular products is also found to be dominant during Zr(0001) chlorination.« less

Ion-enhanced chemical etching of ZrO2 in a chlorine discharge

NASA Astrophysics Data System (ADS)

Sha, Lin; Cho, Byeong-Ok; Chang, Jane P.

2002-09-01

Chlorine plasma is found to chemically etch ZrO2 thin films in an electron cyclotron resonance reactor, and the etch rate scaled linearly with the square root of ion energy at high ion energies with a threshold energy between 12-20 eV. The etching rate decreased monotonically with increasing chamber pressures, which corresponds to reduced electron temperatures. Optical emission spectroscopy and quadrupole mass spectrometry were used to identify the reaction etching products. No Zr, O, or ZrCl were detected as etching products, but highly chlorinated zirconium compounds (ZrCl2, ZrCl3, and ZrCl4) and ClO were found to be the dominant etching products. ZrCl3 was the dominant etching products at low ion energies, while ZrCl4 became dominant at higher ion energies. This is consistent with greater momentum transfer and enhanced surface chlorination, as determined by x-ray photoelectron spectroscopy, at increased ion energies. Several ion-enhanced chemical reactions are proposed to contribute to the ZrO2 etching. copyright 2002 American Vacuum Society.

Reliability of a new biokinetic model of zirconium in internal dosimetry: part II, parameter sensitivity analysis.

PubMed

Li, Wei Bo; Greiter, Matthias; Oeh, Uwe; Hoeschen, Christoph

2011-12-01

The reliability of biokinetic models is essential for the assessment of internal doses and a radiation risk analysis for the public and occupational workers exposed to radionuclides. In the present study, a method for assessing the reliability of biokinetic models by means of uncertainty and sensitivity analysis was developed. In the first part of the paper, the parameter uncertainty was analyzed for two biokinetic models of zirconium (Zr); one was reported by the International Commission on Radiological Protection (ICRP), and one was developed at the Helmholtz Zentrum München-German Research Center for Environmental Health (HMGU). In the second part of the paper, the parameter uncertainties and distributions of the Zr biokinetic models evaluated in Part I are used as the model inputs for identifying the most influential parameters in the models. Furthermore, the most influential model parameter on the integral of the radioactivity of Zr over 50 y in source organs after ingestion was identified. The results of the systemic HMGU Zr model showed that over the first 10 d, the parameters of transfer rates between blood and other soft tissues have the largest influence on the content of Zr in the blood and the daily urinary excretion; however, after day 1,000, the transfer rate from bone to blood becomes dominant. For the retention in bone, the transfer rate from blood to bone surfaces has the most influence out to the endpoint of the simulation; the transfer rate from blood to the upper larger intestine contributes a lot in the later days; i.e., after day 300. The alimentary tract absorption factor (fA) influences mostly the integral of radioactivity of Zr in most source organs after ingestion.

Cycloheptatrienyl zirconium sandwich complexes with lewis basic phospholyl ligands (phosphatrozircenes): synthesis, structure, bonding and coordination chemistry.

PubMed

Glöckner, Andreas; Bannenberg, Thomas; Büschel, Susanne; Daniliuc, Constantin G; Jones, Peter G; Tamm, Matthias

2011-05-23

The transmetalation reaction between [(η(7) -C(7) H(7) )ZrCl(tmeda)] (1; tmeda=N,N,N',N'-tetramethylethylenediamine) and various phospholide anions leads to a new class of mixed sandwich complexes: [(η(7)-C(7)H(7))Zr(η(5)-C(4)PMe(4))] (2), [(η(7)-C(7)H(7))Zr(η(5)-C(4)PH(2)Me(2))] (3) and [(η(7)-C(7)H(7))Zr(η(5)-C(4)PPhHMe(2))] (4). The presence of Lewis basic phosphorus atoms and Lewis acidic zirconium atoms allows ambiphilic behaviour to be observed, and X-ray diffraction analysis reveals dimeric arrangements for 2 and 3 with long intermolecular Zr-P bonds, whereas 4 remains monomeric in the solid state. DFT calculations indicate that the metal-phosphorus interaction is weak, and accordingly, complexes 2-4 act as monodentate ligands upon reaction with [W(CO)(5)(thf)]. The resulting complexes [W(CO)(5)(L)] 5-7 (L=2-4) were studied by IR spectroscopy and compared with the [W(CO)(5) ] complex 9, containing the phosphane-functionalised trozircene [(η(7)-C(7)H(7))Zr(η(5)-C(5)H(4)PPh(2))] (8). They all show a close resemblance to simple phosphanes, such as PMe(3) , although molecular orbital analysis of 2 reveals that the free electron pair in the phosphatrozircenes is not the HOMO. Four equivalents of 2 can replace 1,4-cyclooctadiene (COD) in [Ni(cod)(2)] to form the homoleptic, distorted tetrahedral complex [Ni{2}(4)] (10). Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Oxidised zirconium versus cobalt alloy bearing surfaces in total knee arthroplasty: 3D laser scanning of retrieved polyethylene inserts.

PubMed

Anderson, F L; Koch, C N; Elpers, M E; Wright, T M; Haas, S B; Heyse, T J

2017-06-01

We sought to establish whether an oxidised zirconium (OxZr) femoral component causes less loss of polyethylene volume than a cobalt alloy (CoCr) femoral component in total knee arthroplasty. A total of 20 retrieved tibial inserts that had articulated with OxZr components were matched with 20 inserts from CoCr articulations for patient age, body mass index, length of implantation, and revision diagnosis. Changes in dimensions of the articular surfaces were compared with those of pristine inserts using laser scanning. The differences in volume between the retrieved and pristine surfaces of the two groups were calculated and compared. The loss of polyethylene volume was 122 mm 3 (standard deviation (sd) 87) in the OxZr group and 170 mm 3 (sd 96) in the CoCr group (p = 0.033). The volume loss in the OxZr group was also lower in the medial (72 mm 3 (sd 67) versus 92 mm 3 (sd 60); p = 0.096) and lateral (49 mm 3 (sd 36) versus 79 mm 3 (sd 61); p = 0.096) compartments separately, but these differences were not significant. Our results corroborate earlier findings from in vitro testing and visual retrieval analysis which suggest that polyethylene volume loss is lower with OxZr femoral components. Since both OxZr and CoCr are hard surfaces that would be expected to create comparable amounts of polyethylene creep, the differences in volume loss may reflect differences in the in vivo wear of these inserts. Cite this article: Bone Joint J 2017;99-B:793-8. ©2017 The British Editorial Society of Bone & Joint Surgery.

Influence of chemical composition of zirconium alloy E110 on embrittlement under LOCA conditions - Part 1: Oxidation kinetics and macrocharacteristics of structure and fracture

NASA Astrophysics Data System (ADS)

Nikulin, S. A.; Rozhnov, A. B.; Belov, V. A.; Li, E. V.; Glazkina, V. S.

2011-11-01

Exploratory investigations of the influence of alloying and impurity content in the E110 alloy cladding tubes on the behavior under conditions of Loss of Coolant Accidents (LOCA) has been performed. Three alloys of E110 type have been tested: E110 alloy of nominal composition Zr-1%Nb (E110), E110 alloy of modified composition Zr-1%Nb-0.12%Fe-0.13%O (E110M), E110 alloy of nominal composition Zr-1%Nb with reduced impurity content (E110G). Alloys E110 and E110M were manufactured on the electrolytic basis and alloy E110G was manufactured on the basis of zirconium sponge. The high temperature oxidation tests in steam ( T = 1100 °C, 18% of equivalent cladding reacted (ECR)) have been conducted, kinetics of oxidation was investigated. Quantitative research of structure and fracture macrocharacteristics was performed by means of optical and electron microscopy. The results received were compared with the residual ductility of specimens. The results of the investigation showed the existence of "breakaway oxidation" kinetics and white spalling oxide in E110 and E110M alloys while the specimen oxidation kinetics in E110G alloy was characterized by a parabolic law and specimens had a dense black oxide. Oxygen and iron alloying in the E110 alloy positively changed the macrocharacteristics of structure and fracture. However, in general, it did not improve the resistance to embrittlement in LOCA conditions apparently because of a strong impurity influence caused by electrolytic process of zirconium production.

Trichlorido(tetra­hydro­furan){(1,2,3,3a,7a-η)-1-[2-(1-trimethyl­silyl-1H-imidazol-2-yl-κN 3)-1-methyl­prop­yl]inden­yl}zirconium(IV)

PubMed Central

Guan, Shengzhou; Nie, Wanli; Borzov, Maxim V.

2011-01-01

The title compound, [ZrCl3(C19H25N2Si)(C4H8O)], was prepared from bis­(N,N-dimethyl­amido-κN)(2-{2-[(1,2,3,3a,7a-η)-inden­yl]-2-methyl­prop­yl}-1H-imidazolido-κN 1)zirconium(IV) [(C16H16N2)Zr(NMe2)] by reaction with excess Me3SiCl in tetra­hydro­furan (THF) at elevated temperature. The crystal studied contained a minor non-merohedral twin contaminant [6.3 (4)%] which was taken into account during the refinement. The coordination polyhedron of the ZrIV atom is a distorted octa­hedron [assuming that the five-membered ring of the indenyl group (Cp) occupies one coordination site], with the Cp group and a THF O atom at the apical positions and the three Cl and ligating N atoms at the equatorial positions. The Zr, Si and the methyl­ene C atoms deviate noticeably from the imidazole ring plane [by −0.197 (5), −0.207 (5) and 0.119 (6) Å, respectively]. The THF ligand adopts an envelope conformation. PMID:21754279

Joining of Zirconium Diboride-Based Ceramic Composites to Metallic Systems for High-Temperature Applications

NASA Technical Reports Server (NTRS)

Asthana, R.; Singh, M.

2008-01-01

Three types of hot-pressed zirconium diboride (ZrB2)-based ultra-high-temperature ceramic composites (UHTCC), ZrB2-SiC (ZS), ZrB2-SiC-C (ZSC), and ZrB2-SCS9-SiC (ZSS), were joined to Cu-clad-Mo using two Ag-Cu brazes (Cusil-ABA and Ticusil, T(sub L) approx.1073-1173 K) and two Pd-base brazes (Palco and Palni, T(sub L) approx.1493-1513 K). Scanning Electron Microscopy (SEM) coupled with energy-dispersive spectroscopy (EDS) revealed greater chemical interaction in joints made using Pd-base brazes than in joints made using Ag-Cu based active brazes. The degree of densification achieved in hot pressed composites influenced the Knoop hardness of the UHTCC and the hardness distribution across the braze interlayer. The braze region in Pd-base system displayed higher hardness in joints made using fully-dense ZS composites than in joints made using partially-dense ZSS composites and the carbon-containing ZSC composites. Calculations indicate a small negative elastic strain energy and an increase in the UHTCC's fracture stress up to a critical clad layer thickness . Above this critical thickness, strain energy in the UHTCC is positive, and it increases with increasing clad layer thickness. Empirical projections show a reduction in the effective thermal resistance of the joints and highlight the potential benefits of joining the UHTCC to Cu-clad-Mo.

Influence of dosage, pH and contact time in stabilized landfill leachate treatment using ozone/zirconium tetrachloride catalytic oxidation

NASA Astrophysics Data System (ADS)

Zakaria, Siti Nor Farhana; Aziz, Hamidi Abdul

2017-10-01

Leachate is a critical problem of sanitary landfills because it contains high organic matter and hazardous compounds that can generate negative environmental effects. The high chemical oxygen demand (COD) and color of the leachate necessitates its treatment before it can be released to the water body. Thus, an investigation into the performance of advanced oxidation processes (AOPs) was conducted using a combination of ozone (O3) with zirconium tetrachloride (ZrCl4) as catalyst in stabilized landfill leachate treatment. Such leachate was collected from the Alor Pongsu Landfill site (APLS), Perak, Malaysia. COD and color parameter were used as indicators to examine the effect of O3/ZrCl4 dosage, pH, and contact time. The experiment was run under gas flow rate of 1,000 mL/min±10% and temperature below 15 °C. The maximum removal obtained for COD and color were 88% and 100%, respectively. This outcome was achieved at 27 g/m3 ozone dosage, pH 6, 90 min reaction time, and dosage ratio of 1:2 (COD g: ZrCl4 g). The reaction rate constant (k) was 0.2364 min-1 and followed pseudo first order. Thus, given the efficiency of the O3/ZrCl4 mixture for the remediation of stabilized landfill leachate, a new alternative method in leachate industrial treatment was identified.

Crystal structure of the formal 20 electron zirconocene penta-fulvene complex Cp2Zr(η5,η1-adamantyl-idene-penta-fulvene):toluene:n-hexane = 1:0.125:0.125.

PubMed

Fischer, Malte; Schmidtmann, Marc; Beckhaus, Rüdiger

2017-12-01

The crystal structure of a solvated zirconocene penta-fulvene complex with a bulky adamantyl-idene substitution pattern, namely (η 5 ,η 1 -adamantyl-idene-penta-fulvene)bis-(η 5 -cyclo-penta-dien-yl)zirconium(IV)-toluene- n -hexane (8/1/1), [Zr(C 15 H 18 )(C 5 H 5 ) 2 ]·0.125C 7 H 8 ·0.125C 6 H 14 , is reported. Reducing zirconocene dichloride with magnesium results in the formation of a low-valent zirconocene reagent that reacts readily with adamantyl-idene-penta-fulvene to give the aforementioned complex. Single crystal X-ray diffraction proves the dianion-like η 5 :η 1 binding mode of the fulvene ligand to the central Zr IV atom. The asymmetric unit contains four independent mol-ecules of [η 5 :η 1 -adamantyl-idene-penta-fulvene]bis-[(η 5 )-cyclo-penta-dien-yl]zirconium(IV), together with half a mol-ecule of toluene disordered with half a mol-ecule of n -hexane (the solvent mol-ecules have no direct influence on the complex). In each of the four complex mol-ecules, the central Zr IV atom has a distorted tetra-hedral coordination environment. The measured crystal consisted of two domains with a refined ratio of 0.77:0.23.

Structural studies of degradation process of zirconium dioxide tetragonal phase induced by grinding with dental bur

NASA Astrophysics Data System (ADS)

Piosik, A.; Żurowski, K.; Pietralik, Z.; Hędzelek, W.; Kozak, M.

2017-11-01

Zirconium dioxide has been widely used in dental prosthetics. However, the improper mechanical treatment can induce changes in the microstructure of zirconium dioxide. From the viewpoint of mechanical properties and performance, the phase transitions of ZrO2 from the tetragonal to the monoclinic phase induced by mechanical processing, are particularly undesirable. In this study, the phase transitions of yttrium stabilized zirconium dioxide (Y-TZP) induced by mechanical treatment are investigated by the scanning electron microscopy (SEM), atomic force microscopy (AFM) and powder diffraction (XRD). Mechanical stress was induced by different types of drills used presently in dentistry. At the same time the surface temperature was monitored during milling using a thermal imaging camera. Diffraction analysis allowed determination of the effect of temperature and mechanical processing on the scale of induced changes. The observed phase transition to the monoclinic phase was correlated with the methods of mechanical processing.

Amorphization driven by defect-induced mechanical instability.

PubMed

Jiang, Chao; Zheng, Ming-Jie; Morgan, Dane; Szlufarska, Izabela

2013-10-11

Using ab initio molecular dynamics simulations, we perform a comparative study of the defect accumulation process in silicon carbide (SiC) and zirconium carbide (ZrC). Interestingly, we find that the fcc Si sublattice in SiC spontaneously and gradually collapses following the continuous introduction of C Frenkel pairs (FPs). Above a critical amorphization dose of ~0.33 displacements per atom (dpa), the pair correlation function exhibits no long-range order. In contrast, the fcc Zr sublattice in ZrC remains structurally stable against C sublattice displacements up to the highest dose of 1.0 dpa considered. Consequently, ZrC cannot be amorphized by the accumulation of C FPs. We propose defect-induced mechanical instability as the key mechanism driving the amorphization of SiC under electron irradiation.

Super-strong materials for temperatures exceeding 2000 °C.

PubMed

Silvestroni, Laura; Kleebe, Hans-Joachim; Fahrenholtz, William G; Watts, Jeremy

2017-01-19

Ceramics based on group IV-V transition metal borides and carbides possess melting points above 3000 °C, are ablation resistant and are, therefore, candidates for the design of components of next generation space vehicles, rocket nozzle inserts, and nose cones or leading edges for hypersonic aerospace vehicles. As such, they will have to bear high thermo-mechanical loads, which makes strength at high temperature of great importance. While testing of these materials above 2000 °C is necessary to prove their capabilities at anticipated operating temperatures, literature reports are quite limited. Reported strength values for zirconium diboride (ZrB 2 ) ceramics can exceed 1 GPa at room temperature, but these values rapidly decrease, with all previously reported strengths being less than 340 MPa at 1500 °C or above. Here, we show how the strength of ZrB 2 ceramics can be increased to more than 800 MPa at temperatures in the range of 1500-2100 °C. These exceptional strengths are due to a core-shell microstructure, which leads to in-situ toughening and sub-grain refinement at elevated temperatures. Our findings promise to open a new avenue to designing materials that are super-strong at ultra-high temperatures.

Super-strong materials for temperatures exceeding 2000 °C

NASA Astrophysics Data System (ADS)

Silvestroni, Laura; Kleebe, Hans-Joachim; Fahrenholtz, William G.; Watts, Jeremy

2017-01-01

Ceramics based on group IV-V transition metal borides and carbides possess melting points above 3000 °C, are ablation resistant and are, therefore, candidates for the design of components of next generation space vehicles, rocket nozzle inserts, and nose cones or leading edges for hypersonic aerospace vehicles. As such, they will have to bear high thermo-mechanical loads, which makes strength at high temperature of great importance. While testing of these materials above 2000 °C is necessary to prove their capabilities at anticipated operating temperatures, literature reports are quite limited. Reported strength values for zirconium diboride (ZrB2) ceramics can exceed 1 GPa at room temperature, but these values rapidly decrease, with all previously reported strengths being less than 340 MPa at 1500 °C or above. Here, we show how the strength of ZrB2 ceramics can be increased to more than 800 MPa at temperatures in the range of 1500-2100 °C. These exceptional strengths are due to a core-shell microstructure, which leads to in-situ toughening and sub-grain refinement at elevated temperatures. Our findings promise to open a new avenue to designing materials that are super-strong at ultra-high temperatures.

Super-strong materials for temperatures exceeding 2000 °C

PubMed Central

Silvestroni, Laura; Kleebe, Hans-Joachim; Fahrenholtz, William G.; Watts, Jeremy

2017-01-01

Ceramics based on group IV-V transition metal borides and carbides possess melting points above 3000 °C, are ablation resistant and are, therefore, candidates for the design of components of next generation space vehicles, rocket nozzle inserts, and nose cones or leading edges for hypersonic aerospace vehicles. As such, they will have to bear high thermo-mechanical loads, which makes strength at high temperature of great importance. While testing of these materials above 2000 °C is necessary to prove their capabilities at anticipated operating temperatures, literature reports are quite limited. Reported strength values for zirconium diboride (ZrB2) ceramics can exceed 1 GPa at room temperature, but these values rapidly decrease, with all previously reported strengths being less than 340 MPa at 1500 °C or above. Here, we show how the strength of ZrB2 ceramics can be increased to more than 800 MPa at temperatures in the range of 1500–2100 °C. These exceptional strengths are due to a core-shell microstructure, which leads to in-situ toughening and sub-grain refinement at elevated temperatures. Our findings promise to open a new avenue to designing materials that are super-strong at ultra-high temperatures. PMID:28102327

Extending FEAST-METAL for analysis of low content minor actinide bearing and zirconium rich metallic fuels for sodium fast reactors

NASA Astrophysics Data System (ADS)

Karahan, Aydın

2011-07-01

Computational models in FEAST-METAL fuel behaviour code have been upgraded to simulate minor actinide bearing zirconium rich metallic fuels for use in sodium fast reactors. Increasing the zirconium content to 20-40 wt.% causes significant changes in fuel slug microstructure affecting thermal, mechanical, chemical, and fission gas behaviour. Inclusion of zirconium rich phase reduces the fission gas swelling rate significantly in early irradiation. Above the threshold fission gas swelling, formation of micro-cracks, and open pores increase material compliancy enhance diffusivity, leading to rapid fuel gas swelling, interconnected porosity development and release of the fission gases and helium. Production and release of helium was modelled empirically as a function of americium content and fission gas production, consistent with previous Idaho National Laboratory studies. Predicted fuel constituent redistribution is much smaller compared to typical U-Pu-10Zr fuel operated at EBR-II. Material properties such as fuel thermal conductivity, modulus of elasticity, and thermal expansion coefficient have been approximated using the available database. Creep rate and fission gas diffusivity of high zirconium fuel is lowered by an order of magnitude with respect to the reference low zirconium fuel based on limited database and in order to match experimental observations. The new code is benchmarked against the AFC-1F fuel assembly post irradiation examination results. Satisfactory match was obtained for fission gas release and swelling behaviour. Finally, the study considers a comparison of fuel behaviour between high zirconium content minor actinide bearing fuel and typical U-15Pu-6Zr fuel pins with 75% smear density. The new fuel has much higher fissile content, allowing for operating at lower neutron flux level compared to fuel with lower fissile density. This feature allows the designer to reach a much higher burnup before reaching the cladding dose limit. On the other hand, in order to accommodate solid fission product swelling and to control fuel clad mechanical interaction of the stiffer fuel, the fuel smear density is reduced to 70%. In addition, plenum height is increased to accommodate for fission gases.

A theoretical model of grain boundary self-diffusion in metals with phase transitions (case study into titanium and zirconium)

NASA Astrophysics Data System (ADS)

Semenycheva, Alexandra V.; Chuvil'deev, Vladimir N.; Nokhrin, Aleksey V.

2018-05-01

The paper offers a model describing the process of grain boundary self-diffusion in metals with phase transitions in the solid state. The model is based on ideas and approaches found in the theory of non-equilibrium grain boundaries. The range of application of basic relations contained in this theory is shown to expand, as they can be used to calculate the parameters of grain boundary self-diffusion in high-temperature and low-temperature phases of metals with a phase transition. The model constructed is used to calculate grain boundary self-diffusion activation energy in titanium and zirconium and an explanation is provided as to their abnormally low values in the low-temperature phase. The values of grain boundary self-diffusion activation energy are in good agreement with the experiment.

Phase separation of metal-added corium and its effect on a steam explosion

NASA Astrophysics Data System (ADS)

Min, B. T.; Kim, J. H.; Hong, S. W.; Hong, S. H.; Park, I. K.; Song, J. H.; Kim, H. D.

2008-07-01

To simulate a relocation of molten core material and its interaction phenomenon with water during a severe accident in a nuclear reactor, a typical corium of UO 2/ZrO 2/Zr/Stainless steel mixed at a 62 wt%, 15 wt%, 12 wt% and 11 wt%, respectively, was melted and then cooled down to become a solidified ingot. It was shown that the molten corium was separated into two layers, of which the upper layer was oxide mixtures and the lower layer was metal alloys. The upper layer was UO 2 and ZrO 2 and the lower layer mostly consisted of metal mixtures such as uranium, zirconium and stainless steel. Iron content varied with the positions and about a half of it existed as an alloy such as Fe 2U. Uranium metal was produced by reduction of UO 2 by zirconium metal. The average densities of the upper oxide layer and the lower metal layer were 8.802 and 9.411 g/cm 3, respectively. In another test, metal-added molten corium was poured into water and it showed that a steam explosion could occur by applying an external trigger.

Reaction of Titanium and Zirconium Particles in Cylindrical Explosive Charges

NASA Astrophysics Data System (ADS)

Frost, David L.; Cairns, Malcolm; Goroshin, Samuel; Zhang, Fan

2007-12-01

The critical conditions for the reaction of particles of the transition metals titanium (Ti) and zirconium (Zr) dispersed during the detonation of long cylindrical explosive charges have been investigated experimentally. The charges consisted of packed beds of either spherical Ti particles or irregularly shaped Zr particles saturated with sensitized liquid nitromethane. For the Ti particles, a threshold particle diameter exists of 65±25 μm, above which self-sustained particle reaction is not observed for charge diameters up to 49 mm, although some particle reaction occurs immediately behind the detonation front then rapidly quenches. For the smallest particles (40 μm), the proportion of the conical particle cloud that reacts increases with charge diameter, suggesting that the reaction is a competition between particle heating and expansion cooling of the products. For 375 and 550 μm Zr particles, particle ignition was observed for 19 and 41 mm dia charges. In this case, interaction of the detonation wave with the particles is sufficient to initiate reaction at the particle surface after a delay time (˜5 μs), which is much less than the time required for thermal equilibration of the particles.

Synthesis of UiO-66-OH zirconium metal-organic framework and its application for selective extraction and trace determination of thorium in water samples by spectrophotometry

NASA Astrophysics Data System (ADS)

Moghaddam, Zahra Safaei; Kaykhaii, Massoud; Khajeh, Mostafa; Oveisi, Ali Reza

2018-04-01

In this study, a zirconium-based metal-organic framework (Zr-MOF), named UiO-66-OH, was synthesized by the solvo-thermal method and characterized by Fourier transform-infrared spectroscopy (FTIR), powder X-ray diffraction (PXRD), and scanning electron microscopy (SEM). This Zr-MOF was then employed as a sorbent for selective extraction and preconcentration of thorium ions after their complexation with 2-(2,4-dihydroxyphenyl)-3,5,7-trihydroxychromen-4-one (morin) from environmental water samples prior to its spectrophotometrical determination. The experimental parameters affecting extraction, such as pH of sample solution, amount of Zr-MOF, type and volume of eluting solvent, adsorption and desorption time, and concentration of complexing agent were evaluated and optimized. Under the optimized conditions, an enrichment factor of 250 was achieved. The limit of detection was calculated to be 0.35 μg·L- 1 with a linear range between 10 and 2000 μg·L- 1of thorium. The maximum sorption capacity of MOF toward thorium was found to be 47.5 mg·g- 1. The proposed procedure was successfully applied to the analysis of real water samples.

ZrB2-CNTs Nanocomposites Fabricated by Spark Plasma Sintering

PubMed Central

Jin, Hua; Meng, Songhe; Xie, Weihua; Xu, Chenghai; Niu, Jiahong

2016-01-01

ZrB2-based nanocomposites with and without carbon nanotubes (CNTs) as reinforcement were prepared at 1600 °C by spark plasma sintering. The effects of CNTs on the microstructure and mechanical properties of nano-ZrB2 matrix composites were studied. The results indicated that adding CNTs can inhibit the abnormal grain growth of ZrB2 grains and improve the fracture toughness of the composites. The toughness mechanisms were crack deflection, crack bridging, debonding, and pull-out of CNTs. The experimental results of the nanograined ZrB2-CNTs composites were compared with those of the micro-grained ZrB2-CNTs composites. Due to the small size and surface effects, the nanograined ZrB2-CNTs composites exhibited stronger mechanical properties: the hardness, flexural strength and fracture toughness were 18.7 ± 0.2 GPa, 1016 ± 75 MPa, and 8.5 ± 0.4 MPa·m1/2, respectively. PMID:28774087

ZrB₂-CNTs Nanocomposites Fabricated by Spark Plasma Sintering.

PubMed

Jin, Hua; Meng, Songhe; Xie, Weihua; Xu, Chenghai; Niu, Jiahong

2016-11-29

ZrB₂-based nanocomposites with and without carbon nanotubes (CNTs) as reinforcement were prepared at 1600 °C by spark plasma sintering. The effects of CNTs on the microstructure and mechanical properties of nano-ZrB₂ matrix composites were studied. The results indicated that adding CNTs can inhibit the abnormal grain growth of ZrB₂ grains and improve the fracture toughness of the composites. The toughness mechanisms were crack deflection, crack bridging, debonding, and pull-out of CNTs. The experimental results of the nanograined ZrB₂-CNTs composites were compared with those of the micro-grained ZrB₂-CNTs composites. Due to the small size and surface effects, the nanograined ZrB₂-CNTs composites exhibited stronger mechanical properties: the hardness, flexural strength and fracture toughness were 18.7 ± 0.2 GPa, 1016 ± 75 MPa, and 8.5 ± 0.4 MPa·m 1/2 , respectively.

Quantitative assessment of Zirconium-89 labeled cetuximab using PET/CT imaging in patients with advanced head and neck cancer: a theragnostic approach.

PubMed

Even, Aniek J G; Hamming-Vrieze, Olga; van Elmpt, Wouter; Winnepenninckx, Véronique J L; Heukelom, Jolien; Tesselaar, Margot E T; Vogel, Wouter V; Hoeben, Ann; Zegers, Catharina M L; Vugts, Daniëlle J; van Dongen, Guus A M S; Bartelink, Harry; Mottaghy, Felix M; Hoebers, Frank; Lambin, Philippe

2017-01-17

Biomarkers predicting treatment response to the monoclonal antibody cetuximab in locally advanced head and neck squamous cell carcinomas (LAHNSCC) are lacking. We hypothesize that tumor accessibility is an important factor in treatment success of the EGFR targeting drug. We quantified uptake of cetuximab labeled with Zirconium-89 (89Zr) using PET/CT imaging.Seventeen patients with stage III-IV LAHNSCC received a loading dose unlabeled cetuximab, followed by 10 mg 54.5±9.6 MBq 89Zr-cetuximab. PET/CT images were acquired either 3 and 6 or 4 and 7 days post-injection. 89Zr-cetuximab uptake was quantified using standardized uptake value (SUV) and tumor-to-background ratio (TBR), and correlated to EGFR immunohistochemistry. TBR was compared between scan days to determine optimal timing.Uptake of 89Zr-cetuximab varied between patients (day 6-7: SUVpeak range 2.5-6.2). TBR increased significantly (49±28%, p < 0.01) between first (1.1±0.3) and second scan (1.7±0.6). Between groups with a low and high EGFR expression a significant difference in SUVmean (2.1 versus 3.0) and SUVpeak (3.2 versus 4.7) was found, however, not in TBR. Data is available at www.cancerdata.org (DOI: 10.17195/candat.2016.11.1).In conclusion, 89Zr-cetuximab PET imaging shows large inter-patient variety in LAHNSCC and provides additional information over FDG-PET and EGFR expression. Validation of the predictive value is recommended with scans acquired 6-7 days post-injection.

Zirconium(IV) functionalized magnetic nanocomposites for extraction of organophosphorus pesticides from environmental water samples.

PubMed

Jiang, Li; Huang, Tengjun; Feng, Shun; Wang, Jide

2016-07-22

The widespread use of organophosphate pesticides (OPPs) in agriculture leads to residue accumulation in the environment which is dangerous to human health and disrupts the ecological balance. In this work, one nanocomposite immobilized zirconium (Zr, IV) was prepared and used as the affinity probes to quickly and selectively extract organophosphorus pesticides (OPPs) from water samples. The Fe3O4-ethylenediamine tetraacetic acid (EDTA)@Zr(IV) nanocomposites (NPs) were prepared by simply mixing Zr(IV) ions with Fe3O4-EDTA NPs synthesized by one-pot chemical co-precipitation method. The immobilized Zr(IV) ions were further utilized to capture OPPs based on their high affinity for the phosphate moiety in OPPs. Coupled with GC-MS, four OPPs were used as models to demonstrate the feasibility of this approach. Under the optimum conditions, the limits of detection for target OPPs were in the range of 0.10-10.30ngmL(-1) with relative standard deviations (RSDs) of 0.61-4.40% (n=3), respectively. The linear ranges were over three orders of magnitudes (correlation coefficients, R(2)>0.9995). The Fe3O4-EDTA@Zr(IV) NPs were successfully applied to extract OPPs samples with recoveries of 86.95-112.60% and RSDs of 1.20-10.42% (n=3) from two spiked real water. By the proposed method, the matrix interference could be effectively eliminated. We hope our finding can provide a promising alternative for the fast extraction of OPPs from complex real samples. Copyright © 2016 Elsevier B.V. All rights reserved.

Quantitative assessment of Zirconium-89 labeled cetuximab using PET/CT imaging in patients with advanced head and neck cancer: a theragnostic approach

PubMed Central

van Elmpt, Wouter; Winnepenninckx, Véronique J.L.; Heukelom, Jolien; Tesselaar, Margot E.T.; Vogel, Wouter V.; Hoeben, Ann; Zegers, Catharina M.L.; Vugts, Daniëlle J.; van Dongen, Guus A.M.S.; Bartelink, Harry; Mottaghy, Felix M.; Hoebers, Frank; Lambin, Philippe

2017-01-01

Biomarkers predicting treatment response to the monoclonal antibody cetuximab in locally advanced head and neck squamous cell carcinomas (LAHNSCC) are lacking. We hypothesize that tumor accessibility is an important factor in treatment success of the EGFR targeting drug. We quantified uptake of cetuximab labeled with Zirconium-89 (89Zr) using PET/CT imaging. Seventeen patients with stage III-IV LAHNSCC received a loading dose unlabeled cetuximab, followed by 10 mg 54.5±9.6 MBq 89Zr-cetuximab. PET/CT images were acquired either 3 and 6 or 4 and 7 days post-injection. 89Zr-cetuximab uptake was quantified using standardized uptake value (SUV) and tumor-to-background ratio (TBR), and correlated to EGFR immunohistochemistry. TBR was compared between scan days to determine optimal timing. Uptake of 89Zr-cetuximab varied between patients (day 6-7: SUVpeak range 2.5-6.2). TBR increased significantly (49±28%, p < 0.01) between first (1.1±0.3) and second scan (1.7±0.6). Between groups with a low and high EGFR expression a significant difference in SUVmean (2.1 versus 3.0) and SUVpeak (3.2 versus 4.7) was found, however, not in TBR. Data is available at www.cancerdata.org (DOI: 10.17195/candat.2016.11.1). In conclusion, 89Zr-cetuximab PET imaging shows large inter-patient variety in LAHNSCC and provides additional information over FDG-PET and EGFR expression. Validation of the predictive value is recommended with scans acquired 6-7 days post-injection. PMID:27965472

Refining As-cast β-Ti Grains Through ZrN Inoculation

NASA Astrophysics Data System (ADS)

Qiu, Dong; Zhang, Duyao; Easton, Mark A.; St John, David H.; Gibson, Mark A.

2018-03-01

The columnar-to-equiaxed transition and remarkable refinement of β-Ti grains occur in an as-cast Ti-13Mo alloy when a new grain refiner, ZrN, was inoculated at a nitrogen level as low as 0.4 wt pct. The grain refining effect is attributed to in situ-formed TiN particles that provide active nucleation sites and solute Zr that promotes constitutional supercooling. Reproducible orientation relationships were identified between TiN nucleants and β-Ti matrix, and well explained by the edge-to-edge matching model.

Electrochemical studies on zirconium and its biocompatible alloys Ti-50Zr at.% and Zr-2.5Nb wt.% in simulated physiologic media.

PubMed

Oliveira, Nilson T C; Biaggio, Sonia R; Rocha-Filho, Romeu C; Bocchi, Nerilso

2005-09-01

Different electrochemical studies were carried out for Zr and its biocompatible alloys Ti-50Zr at.% and Zr-2.5Nb wt.% in solutions simulating physiologic media, Ringer and PBS (phosphate buffered saline) solutions. The results from rest-potential measurements showed that the three materials are spontaneously passivated in both solutions and that the Ti-50Zr alloy has the greatest tendency for spontaneous oxide formation. Some corrosion parameters (such as the pitting and repassivation potentials) were obtained via cyclic voltammetry in both solutions, revealing that the Ti-50Zr has the best corrosion protection while Zr has the worst. On the other hand, the pre-anodization (up to 8 V vs. SCE) of the alloys in a 0.15 mol/L Na2SO4 solution led to a significant improvement in their protection against pitting corrosion when exposed to the Ringer solution. Elemental analyses by EDX showed that during pitting corrosion, there is no preferential corrosion of any of the alloying elements (Zr, Ti, Nb). Copyright (c) 2005 Wiley Periodicals, Inc.

Effects of ammonium hydroxide on the structure and gas adsorption of nanosized Zr-MOFs (UiO-66).

PubMed

Abid, Hussein Rasool; Ang, Ha Ming; Wang, Shaobin

2012-05-21

Several zirconium-based metal-organic frameworks (Zr-MOFs) have been synthesized using ammonium hydroxide as an additive in the synthesis process. Their physicochemical properties have been characterized by N(2) adsorption/desorption, XRD, SEM, FTIR, and TGA, and their application in CO(2) adsorption was evaluated. It was found that addition of ammonium hydroxide produced some effects on the structure and adsorption behavior of Zr-MOFs. The pore size and pore volume of Zr-MOFs were enhanced with the additive, however, specific surface area of Zr-MOFs was reduced. Using an ammonium hydroxide additive, the crystal size of Zr-MOF was reduced with increasing amount of the additive. All the samples presented strong thermal stability. Adsorption tests showed that capacity of CO(2) adsorption on the Zr-MOFs under standard conditions was reduced due to decreased micropore fractions. However, modified Zr-MOFs had significantly lower adsorption heat. The adsorption capacity of carbon dioxide was increased at high pressure, reaching 8.63 mmol g(-1) at 987 kPa for Zr-MOF-NH(4)-2.

Evaluation of zirconia, thoria and zirconium diboride for advanced resistojet use

NASA Technical Reports Server (NTRS)

Page, R. J.; Short, R. A.; Halbach, C. R.

1972-01-01

A literature survey was conducted to collect material properties data on all advanced high temperature materials. Three of these, Y2O3-stabilized ZrO2, ThO2, and ZrB2 with additives of C and SiC were selected for further study. Stabilized ZrO2 and ThO2 were found to have higher temperature oxidation resistance than any metal and great potential for use in advanced biowaste resistojets. ZrO2 has a lower electrical resistivity and sublimation and a higher creep endurance strength. ZrO2 and ThO2 tubular heat exchangers, electrically heated indirectly, were evaluated in short tests to about 1900 K in flowing CO2. ZrO2 was subjected to N2, H2, H2O and vacuum as well. X-ray diffraction and fluorescence analyses were made. The metal-to-ceramic seal technology for ZrO2 and ThO2 was developed using chemical vapor deposition of tantalum for metallizing and 82 Au - 18 Ni filler braze.

Suspensions on the basis of stabilised zirconium oxide for three-dimensional printing

NASA Astrophysics Data System (ADS)

Sokolov, P. S.; Komissarenko, D. A.; Shmeleva, I. A.; Slyusar, I. V.; Dosovitskiy, G. A.; Evdokimov, P. V.; Putlyaev, V. I.; Dosovitskiy, A. E.

2018-04-01

Present work considers the first results on rheological and photo-curing behaviour of suspension consisting of nanocrystalline stabilised zirconium dioxide powders (19 - 27 vol. %) and a liquid UV-photosensitive organic monomer. At ambient temperature compositions showed a viscosity of 2.5 and 0.8 Pa×s at 10 and 100 s-1 shear rates, respectively. Printability of these compositions was subsequently investigated by using an stereolithography machine Ember (Autodesk). 3D objects were later sintered in a separate furnace into dense translucent ZrO2 ceramics.

Improved dielectric and ferroelectric properties of Mn doped barium zirconium titanate (BZT) ceramics for energy storage applications

NASA Astrophysics Data System (ADS)

Sangwan, Kanta Maan; Ahlawat, Neetu; Kundu, R. S.; Rani, Suman; Rani, Sunita; Ahlawat, Navneet; Murugavel, Sevi

2018-06-01

Lead free Mn doped barium zirconium titanate ceramic of composition BaZr0.045 (MnxTi1-x)0.955O3 (x = 0.00, 0.01, 0.02) were prepared by solid state reaction method. Tetragonal perovskite structure was confirmed by Rietveld refinement of X-ray diffraction pattern. Analysis of Scanning electron microscope (SEM) micrographs revealed that addition of Mn up to a certain limit accelerates grain growth of BZT ceramic. Static dielectric constant was successfully extended up to high frequencies with an appreciable decrease in dielectric loss about 70% for Mn doped BZT ceramics. The experimental data fitted with Curie Weiss Law and Power Law confirmed first order transition and diffusive behavior of the investigated system. The shifting of Curie temperature (Tc) from 387 K to 402 K indicated tendency for sustained ferroelectricity in doped BZMT ceramics. High value of percentage temperature coefficient of capacitance TCC >10% near Tc was observed for all the compositions and increases with Mn content in pure BZT. At room temperature, BZT modified ceramic corresponding to x = 0.01 composition shows better values of remnant polarization (Pr = 5.718 μC/cm2), saturation polarization (Ps = 14.410 μC/cm2), low coercive field (Ec = 0.612 kV/cm), and highest value of Pr/Ps = 0.396.

Alternative Chelator for 89Zr Radiopharmaceuticals: Radiolabeling and Evaluation of 3,4,3-(LI-1,2-HOPO)

PubMed Central

2015-01-01

Zirconium-89 is an effective radionuclide for antibody-based positron emission tomography (PET) imaging because its physical half-life (78.41 h) matches the biological half-life of IgG antibodies. Desferrioxamine (DFO) is currently the preferred chelator for 89Zr4+; however, accumulation of 89Zr in the bones of mice suggests that 89Zr4+ is released from DFO in vivo. An improved chelator for 89Zr4+ could eliminate the release of osteophilic 89Zr4+ and lead to a safer PET tracer with reduced background radiation dose. Herein, we present an octadentate chelator 3,4,3-(LI-1,2-HOPO) (or HOPO) as a potentially superior alternative to DFO. The HOPO ligand formed a 1:1 Zr-HOPO complex that was evaluated experimentally and theoretically. The stability of 89Zr-HOPO matched or surpassed that of 89Zr-DFO in every experiment. In healthy mice, 89Zr-HOPO cleared the body rapidly with no signs of demetalation. Ultimately, HOPO has the potential to replace DFO as the chelator of choice for 89Zr-based PET imaging agents. PMID:24814511

Physicochemical properties of precursors of Al2O3-ZrO2 oxide ceramics prepared by electrochemical method

NASA Astrophysics Data System (ADS)

Petrova, E. V.; Dresvyannikov, A. F.; Ahmadi Daryakenari, M.; Khairullina, A. I.

2016-05-01

Scanning electron microscopy, X-ray, and thermal analysis are used to examine the structure and properties of dispersive systems based on aluminum and zirconium oxides prepared electrochemically. The effect the conditions of synthesis have on the structure and morphology of Al2O3-ZrO2 particles is studied. It is shown that the effect of an electric field on the reaction medium allows us to adjust the physicochemical properties and morphology.

Structural and morphological study of ZrO2 thin films

NASA Astrophysics Data System (ADS)

Kumar, Davinder; Singh, Avtar; Kaur, Manpreet; Rana, Vikrant Singh; Kaur, Raminder

2018-05-01

In this paper we discuss the fabrication of transparent thin films of Zirconium Oxide (ZrO2) deposited on glass substrates by sol-gel dip coating technique. Further these fabricated films were characterized for different annealing temperatures and withdrawal speed. X-ray diffraction is used to study the structural properties of deposited thin films and it reveals the change in crystallographic properties with the change in annealing temperature. Thickness of thin films is estimated by using scanning electron microscope.

On the Synergistic Catalytic Properties of Bimetallic Mesoporous Materials Containing Aluminum and Zirconium: The Prins Cyclisation of Citronellal

PubMed Central

Telalović, Selvedin; Ramanathan, Anand; Ng, Jeck Fei; Maheswari, Rajamanickam; Kwakernaak, Cees; Soulimani, Fouad; Brouwer, Hans C; Chuah, Gaik Khuan; Weckhuysen, Bert M; Hanefeld, Ulf

2011-01-01

Bimetallic three-dimensional amorphous mesoporous materials, Al-Zr-TUD-1 materials, were synthesised by using a surfactant-free, one-pot procedure employing triethanolamine (TEA) as a complexing reagent. The amount of aluminium and zirconium was varied in order to study the effect of these metals on the Brønsted and Lewis acidity, as well as on the resulting catalytic activity of the material. The materials were characterised by various techniques, including elemental analysis, X-ray diffraction, high-resolution TEM, N2 physisorption, temperature-programmed desorption (TPD) of NH3, and 27Al MAS NMR, XPS and FT-IR spectroscopy using pyridine and CO as probe molecules. Al-Zr-TUD-1 materials are mesoporous with surface areas ranging from 700–900 m2 g−1, an average pore size of around 4 nm and a pore volume of around 0.70 cm3 g−1. The synthesised Al-Zr-TUD-1 materials were tested as catalyst materials in the Lewis acid catalysed Meerwein–Ponndorf–Verley reduction of 4-tert-butylcyclohexanone, the intermolecular Prins synthesis of nopol and in the intramolecular Prins cyclisation of citronellal. Although Al-Zr-TUD-1 catalysts possess a lower amount of acid sites than their monometallic counterparts, according to TPD of NH3, these materials outperformed those of the monometallic Al-TUD-1 as well as Zr-TUD-1 in the Prins cyclisation of citronellal. This proves the existence of synergistic properties of Al-Zr-TUD-1. Due to the intramolecular nature of the Prins cyclisation of citronellal, the hydrophilic surface of the catalyst as well as the presence of both Brønsted and Lewis acid sites synergy could be obtained with bimetallic Al-Zr-TUD-1. Besides spectroscopic investigation of the active sites of the catalyst material a thorough testing of the catalyst in different types of reactions is crucial in identifying its specific active sites. PMID:21259348

Probing the Role of Zr Addition versus Textural Properties in Enhancement of CO 2 Adsorption Performance in Silica/PEI Composite Sorbents

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sakwa-Novak, Miles A.; Holewinski, Adam; Hoyt, Caroline B.

2015-08-08

Polymeric amines such as poly(ethylenimine) (PEI) supported on mesoporous oxides are promising candidate adsorbents for CO 2 capture processes. One important aspect to the design and optimization of these materials is a fundamental understanding of how the properties of the oxide support such as pore structure, particle morphology, and surface properties affect the efficiency of the guest polymer in its interactions with CO 2. Previously, the efficiency of impregnated PEI to adsorb CO 2 was shown to increase upon the addition of Zr as a surface modifier in SBA-15. But, the efficacy of this method to tune the adsorption performancemore » has not been explored in materials of differing textural and morphological nature. These issues are directly addressed via the preparation of an array of SBA-15 support materials with varying textural and morphological properties, as well as varying content of zirconium doped into the material. Zirconium is incorporated into the SBA-15 either during the synthesis of the SBA-15, or postsynthetically via deposition of Zr species onto pure-silica SBA-15. The method of Zr incorporation alters the textural and morphological properties of the parent SBA-15 in different ways. Importantly, the CO 2 capacity of SBA-15 impregnated with PEI increases by a maximum of ~60% with the quantity of doped Zr for a “standard” SBA-15 containing significant microporosity, while no increase in the CO 2 capacity is observed upon Zr incorporation for an SBA-15 with reduced microporosity and a larger pore size, pore volume, and particle size. Finally, adsorbents supported on SBA-15 with controlled particle morphology show only modest increases in CO 2 capacity upon inclusion of Zr to the silica framework. The data demonstrate that the textural and morphological properties of the support have a more significant impact on the ability of PEI to capture CO 2 than the support surface composition.« less

Probing the Role of Zr Addition versus Textural Properties in Enhancement of CO₂ Adsorption Performance in Silica/PEI Composite Sorbents.

PubMed

Sakwa-Novak, Miles A; Holewinski, Adam; Hoyt, Caroline B; Yoo, Chun-Jae; Chai, Song-Hai; Dai, Sheng; Jones, Christopher W

2015-09-01

Polymeric amines such as poly(ethylenimine) (PEI) supported on mesoporous oxides are promising candidate adsorbents for CO2 capture processes. An important aspect to the design and optimization of these materials is a fundamental understanding of how the properties of the oxide support such as pore structure, particle morphology, and surface properties affect the efficiency of the guest polymer in its interactions with CO2. Previously, the efficiency of impregnated PEI to adsorb CO2 was shown to increase upon the addition of Zr as a surface modifier in SBA-15. However, the efficacy of this method to tune the adsorption performance has not been explored in materials of differing textural and morphological nature. Here, these issues are directly addressed via the preparation of an array of SBA-15 support materials with varying textural and morphological properties, as well as varying content of zirconium doped into the material. Zirconium is incorporated into the SBA-15 either during the synthesis of the SBA-15, or postsynthetically via deposition of Zr species onto pure-silica SBA-15. The method of Zr incorporation alters the textural and morphological properties of the parent SBA-15 in different ways. Importantly, the CO2 capacity of SBA-15 impregnated with PEI increases by a maximum of ∼60% with the quantity of doped Zr for a "standard" SBA-15 containing significant microporosity, while no increase in the CO2 capacity is observed upon Zr incorporation for an SBA-15 with reduced microporosity and a larger pore size, pore volume, and particle size. Finally, adsorbents supported on SBA-15 with controlled particle morphology show only modest increases in CO2 capacity upon inclusion of Zr to the silica framework. The data demonstrate that the textural and morphological properties of the support have a more significant impact on the ability of PEI to capture CO2 than the support surface composition.

Zirconium-based metal organic frameworks loaded on polyurethane foam membrane for simultaneous removal of dyes with different charges.

PubMed

Li, Juan; Gong, Ji-Lai; Zeng, Guang-Ming; Zhang, Peng; Song, Biao; Cao, Wei-Cheng; Liu, Hong-Yu; Huan, Shuang-Yan

2018-10-01

Treating dye wastewater by membrane filtration technology has received much attention from researchers all over the world, however, current studies mainly focused on the removal of singly charged dyes but actual wastewater usually contains dyes with different charges. In this study, the removal of neutral, cationic and anionic dyes in binary or ternary systems was conducted by using zirconium-based metal organic frameworks loaded on polyurethane foam (Zr-MOFs-PUF) membrane. The Zr-MOFs-PUF membrane was fabricated by an in-situ hydrothermal synthesis approach and a hot-pressing process. Neutrally charged Rhodamine B (RB), positively charged Methylene blue (MB), and negatively charged Congo red (CR) were chosen as model pollutants for investigating filtration performance of the membrane. The results of filtration experiments showed that the Zr-MOFs-PUF membrane could simultaneously remove RB, MB, and CR not only from their binary system including RB/MB, RB/CR, and MB/CR mixtures, but also from RB/MB/CR ternary system. The removal of dyes by Zr-MOFs-PUF membrane was mainly attributed to the electrostatic interactions, hydrogen bond interaction, and Lewis acid-base interactions between the membrane and dye molecules. The maximum removal efficiencies by Zr-MOFs-PUF membrane were 98.80% for RB at pH ≈ 7, 97.57% for MB at pH ≈ 9, and 87.39% for CR at pH ≈ 3. Additionally, when the NaCl concentration reached 0.5 mol/L in single dye solutions, the removal efficiencies of RB, MB, and CR by Zr-MOFs-PUF membrane were 93.08%, 79.52%, and 97.82%, respectively. All the results suggested that the as-prepared Zr-MOFs-PUF membrane has great potential in practical treatment of dye wastewater. Copyright © 2018 Elsevier Inc. All rights reserved.

Burst Ductility of Zirconium Clads: The Defining Role of Residual Stress

NASA Astrophysics Data System (ADS)

Kumar, Gulshan; Kanjarla, A. K.; Lodh, Arijit; Singh, Jaiveer; Singh, Ramesh; Srivastava, D.; Dey, G. K.; Saibaba, N.; Doherty, R. D.; Samajdar, Indradev

2016-08-01

Closed end burst tests, using room temperature water as pressurizing medium, were performed on a number of industrially produced zirconium (Zr) clads. A total of 31 samples were selected based on observed differences in burst ductility. The latter was represented as total circumferential elongation or TCE. The selected samples, with a range of TCE values (5 to 35 pct), did not show any correlation with mechanical properties along axial direction, microstructural parameters, crystallographic textures, and outer tube-surface normal ( σ 11) and shear ( τ 13) components of the residual stress matrix. TCEs, however, had a clear correlation with hydrostatic residual stress ( P h), as estimated from tri-axial stress analysis on the outer tube surface. Estimated P h also scaled with measured normal stress ( σ 33) at the tube cross section. An elastic-plastic finite element model with ductile damage failure criterion was developed to understand the burst mechanism of zirconium clads. Experimentally measured P h gradients were imposed on a solid element continuum finite element (FE) simulation to mimic the residual stresses present prior to pressurization. Trends in experimental TCEs were also brought out with computationally efficient shell element-based FE simulations imposing the outer tube-surface P h values. Suitable components of the residual stress matrix thus determined the burst performance of the Zr clads.

Aqueous sodium borohydride induced thermally stable porous zirconium oxide for quick removal of lead ions

PubMed Central

Nayak, Nadiya B.; Nayak, Bibhuti B.

2016-01-01

Aqueous sodium borohydride (NaBH4) is well known for its reducing property and well-established for the development of metal nanoparticles through reduction method. In contrary, this research paper discloses the importance of aqueous NaBH4 as a precipitating agent towards development of porous zirconium oxide. The boron species present in aqueous NaBH4 play an active role during gelation as well as phase separated out in the form of boron complex during precipitation, which helps to form boron free zirconium hydroxide [Zr(OH)4] in the as-synthesized condition. Evolved in-situ hydrogen (H2) gas-bubbles also play an important role to develop as-synthesized loose zirconium hydroxide and the presence of intra-particle voids in the loose zirconium hydroxide help to develop porous zirconium oxide during calcination process. Without any surface modification, this porous zirconium oxide quickly adsorbs almost hundred percentages of toxic lead ions from water solution within 15 minutes at normal pH condition. Adsorption kinetic models suggest that the adsorption process was surface reaction controlled chemisorption. Quick adsorption was governed by surface diffusion process and the adsorption kinetic was limited by pore diffusion. Five cycles of adsorption-desorption result suggests that the porous zirconium oxide can be reused efficiently for removal of Pb (II) ions from aqueous solution. PMID:26980545

The role of dispersed particles in strengthening and fracture mechanisms in a Mo-ZrC alloy processed by mechanical alloying

DOE Office of Scientific and Technical Information (OSTI.GOV)

Takida, T.; Mabuchi, M.; Nakamura, M.

2000-03-01

The tensile properties of a ZrC particle-dispersed Mo, which was processed by spark plasma sintering with mechanically alloyed powder, were investigated at room temperature and at elevated temperatures of 1,170 to 1,970 K. The Mo-ZrC alloy showed much higher strength at room temperature than a fully recrystallized pure Mo. The high strength of Mo-ZrC is mainly attributed to a very small grain size (about 3 {micro}m). The main role of the ZrC particle is not to increase strength due to the particle-dislocation interaction, but to limit grain growth during sintering and to attain the very small grain size. The elongationmore » at room temperature of No-ZrC was much lower than that of pure Mo. This is probably related to the higher interstitial contents. However, Mo-ZrC showed a large elongation of 180 pct at 1,970 K and 6.7 x 10{sup {minus}4} s{sup {minus}1}. It was suggested that the ZrC particles stabilized the fine-grained microstructure yet provided no cavitation sites at 1,970 K; as a result, the large elongation was attained.« less

High-temperature studies of grain boundaries in ultrafine grained alloys by means of positron lifetime

NASA Astrophysics Data System (ADS)

Würschum, R.; Shapiro, E.; Dittmar, R.; Schaefer, H.-E.

2000-11-01

Atomic free volumes and vacancies in the ultrafine grained alloys Pd84Zr16, Cu 0.1 wt % ZrO2, and Fe91Zr9 were studied by means of positron lifetime. The thermally stable microstructures serve as a novel type of model system for studying positron trapping and annihilation as well as the thermal behavior of vacancy-sized free volumes over a wide temperature range up to ca. 1200 K by making use of a metallic 58Co positron source. In ultrafine grained Cu the thermal formation of lattice vacancies could be observed. In Pd84Zr16 an increase of the specific positron trapping rate of nanovoids and, in addition, detrapping of positrons from free volumes with a mean size slightly smaller than one missing atom in the grain boundaries contributes to a reversible increase of the positron lifetime of more than 60 ps with measuring temperature. In Fe91Zr9 similar linear high-temperature increases of the positron lifetime are observed in the nanocrystalline and the amorphous state. The question of thermal vacancy formation in grain boundaries is addressed taking into account the different types of interface structures of the present alloys.

Properties of zirconium silicate and zirconium-silicon oxynitride high-k dielectric alloys for advanced microelectronic applications: Chemical and electrical characterizations

NASA Astrophysics Data System (ADS)

Ju, Byongsun

2005-11-01

As the microelectronic devices are aggressively scaled down to the 1999 International Technology Roadmap, the advanced complementary metal oxide semiconductor (CMOS) is required to increase packing density of ultra-large scale integrated circuits (ULSI). High-k alternative dielectrics can provide the required levels of EOT for device scaling at larger physical thickness, thereby providing a materials pathway for reducing the tunneling current. Zr silicates and its end members (SiO2 and ZrO2) and Zr-Si oxynitride films, (ZrO2)x(Si3N 4)y(SiO2)z, have been deposited using a remote plasma-enhanced chemical vapor deposition (RPECVD) system. After deposition of Zr silicate, the films were exposed to He/N2 plasma to incorporate nitrogen atoms into the surface of films. The amount of incorporated nitrogen atoms was measured by on-line Auger electron spectrometry (AES) as a function of silicate composition and showed its local minimum around the 30% silicate. The effect of nitrogen atoms on capacitance-voltage (C-V) and leakage-voltage (J-V) were also investigated by fabricating metal-oxide-semiconductor (MOS) capacitors. Results suggested that incorporating nitrogen into silicate decreased the leakage current in SiO2-rich silicate, whereas the leakage increased in the middle range of silicate. Zr-Si oxynitride was a pseudo-ternary alloy and no phase separation was detected by x-ray photoelectron spectroscopy (XPS) analysis up to 1100°C annealing. The leakage current of Zr-Si oxynitride films showed two different temperature dependent activation energies, 0.02 eV for low temperature and 0.3 eV for high temperature. Poole-Frenkel emission was the dominant leakage mechanism. Zr silicate alloys with no Si3N4 phase were chemically separated into the SiO2 and ZrO2 phase as annealed above 900°C. While chemical phase separation in Zr silicate films with Si 3N4 phase (Zr-Si oxynitride) were suppressed as increasing the amount of Si3N4 phase due to the narrow bonding network m Si3N4 phase. (3.4 bonds/atom for Si3 N4 network, 2.67 bonds/atom for SiO2 network).

Effect of Ce/Zr molar ratio on the performance of Cu–Ce{sub x}–Zr{sub 1−x}/TiO{sub 2} catalyst for selective catalytic reduction of NO{sub x} with NH{sub 3} in diesel exhaust

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sun, Xiaoliang; Gong, Cairong, E-mail: gcr@tju.edu.cn; Lv, Gang

2014-12-15

Graphical abstract: The Cu–Ce{sub 0.25}–Zr{sub 0.75}/TiO{sub 2} catalyst exhibited excellent SCR activity at 165–450 °C within the range of exhaust temperatures of diesel engines. - Highlights: • Cu–Ce{sub x}–Zr{sub 1−x}/TiO{sub 2} catalysts were prepared by a wet impregnation method. • The property for NH{sub 3}-selective catalytic reduction of NO{sub x} were investigated. • The Ce/Zr molar ratio had effects on the performance of Cu–Ce–Zr/TiO{sub 2} catalysts. • The Cu–Ce{sub 0.25}–Zr{sub 0.75}/TiO{sub 2} sample exhibited 100% NO{sub x} conversion between 165 °C and 450 °C. • The factors that govern the activity enhancement were extensively investigated. - Abstract: Copper–cerium–zirconium catalysts loadedmore » on TiO{sub 2} prepared by a wet impregnation method were investigated for NH{sub 3}-selective catalytic reduction of NO{sub x}, aiming to study the effects of the Ce/Zr molar ratio on the performance of Cu–Ce–Zr/TiO{sub 2} catalysts. The Cu–Ce{sub 0.25}–Zr{sub 0.75}/TiO{sub 2} sample exhibited nearly 100% NO{sub x} conversion over a wide temperature range (165–450 °C), which is strikingly superior to that of Cu/TiO{sub 2} (210–389 °C) within the range of exhaust temperatures of diesel engines. The factors that govern the activity enhancement were extensively investigated by using a series of characterization techniques, namely X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and temperature-programmed reduction by hydrogen (H{sub 2}-TPR). The results showed that the addition of zirconium and/or cerium refined the copper dispersion, prevented copper crystallization and partially incorporated the copper ions into the zirconia (ceira) lattice, which led to enhance the redox abilities of Cu–Ce–Zr/TiO{sub 2} catalysts.« less

X-Ray Absorption Spectroscopy Studies of the Atomic Structure of Zirconium-Doped Lithium Silicate Glasses and Glass-Ceramics, Zirconium-Doped Lithium Borate Glasses, and Vitreous Rare-Earth Phosphates

NASA Astrophysics Data System (ADS)

Yoo, Changhyeon

In the first part of this work, the atomic-scale structure around rare-earth (RE = Pr, Nd, Eu, Dy, and Er) cations (RE3+) in rare-earth sodium ultraphosphate (REUP) glasses were investigated using RE LIII -edge (RE = Nd, Er, Dy, and Eu) and K-edge (RE = Pr and Dy) Extended X-ray Absorption Fine Structure (EXAFS) spectroscopy. (RE2O 3)x(Na2O)y(P2O5) 1-x-y glasses in the compositional range 0 ≤ x ≤ 0.14 and 0.3 ≤ x + y ≤ 0.4 were studied. For the nearest oxygen shell, the RE-oxygen (RE-O) coordination number decreases from 10.8 to 6.5 with increasing RE content for Pr-, Nd-, Dy-, and Er-doped sodium ultraphosphate glasses. For Eu-doped samples, the Eu-O coordination number was between 7.5 and 8.8. Also, the RE-O mean distance ranges were between 2.43-2.45 A, 2.40-2.43 A, 2.36-2.38 A, 2.30-2.35 A, and 2.28-2.30 A for Pr-, Nd-, Eu-, Dy-, and Er-doped samples, respectively. In the second part, a series of Zr-doped (3-10 mol%) lithium silicate (ZRLS) glass-ceramics and their parent glasses and a series of Zr-doped (2-6 mol% ZrO2) lithium borate (ZRLB) glasses were investigated using Zr K-edge EXAFS and X-ray Absorption Near Edge Structure (XANES) spectroscopy. Immediate coordination environments of all ZRLS glasses are remarkably similar for different compositions. For the nearest oxygen shell, the Zr-O coordination number ranges were between 6.1 and 6.3 for nucleated and crystallized samples, respectively. Also, the Zr-O mean distance remains similar around 2.10 A. For these glasses, the composition dependence of structural parameters was small. Small changes in the coordination environment were observed for ZRLS glass-ceramics after thermal treatments. In contrast, Zr coordination environment in ZRLB glasses appear to depend appreciably on the Zr concentration. For the nearest oxygen shell, the Zr-O coordination number increased from 6.1 to 6.8 and the Zr-O distance decreased from 2.18 A to 2.14 A with decreasing ZrO2 content.

ANALYTICAL METHOD FOR THE DIRECT ABSORPTIOMETRIC DETERMINATION OF BORON IN ZIRCONIUM METAL AND ITS ALLOYS

DOE Office of Scientific and Technical Information (OSTI.GOV)

None

1962-01-01

The sample is dissolved in a mixture of ammonium suifate and sulfuric acid. Rosocyanin is formed in the presence of Zr and, after separation from excess curcumin, it is dissolved in ethanol for absorptiometric measurement. (auth)

Effects of Zirconium Ions Doping on the Structural and Thermochromic Properties of VO2 Thin Films

NASA Astrophysics Data System (ADS)

Li, Yuanbao; Liu, Juncheng; Wang, Danping; Dang, Yuanyuan

2017-11-01

As an inorganic functional material, VO2 thin films are expected to be used for smart windows. However, these films are not conducive to practical applications when the phase transition temperature ( Tc) of the VO2 is approximately 68°C, which is greater than room temperature. To decrease Tc, the effect of Zr4+ doping on the structure and properties of VO2 films were investigated. The films were prepared using a sol-gel process, spin-coating on quartz glasses, and annealing at 525°C in a tube furnace within a nitrogen atmosphere. The results demonstrate that these films have a highly preferential crystalline orientation on the substrate; however, the primary two x-ray diffraction pattern peaks shift slightly toward the small angle, and when 7 at.% Zr4+ was doped in the VO2 film, the deviation angle was 0.16°, and the crystallite size was approximately 98 nm. A large number of grains were found on the surface of the pure VO2 films, but all the Zr4+ doped films had a layered structure, and the thickness of the films was approximately 200 nm. The Tc of these films was characterized using differential scanning calorimetry, and the luminous and solar transmittance was characterized using a UV-Vis-NIR spectrophotometer, which demonstrated that the effect of Zr4+ doping decreased Tc by approximately 1°C per 1 at.% on average, and the Tc of the 7 at.% film was slightly greater than that of the 5 at.% film, the phase transition temperature of which was 61.4°C. The transmittance decreased as the doping concentration increased, and 1 at.% Zr4+ doping increased the luminous regulation efficiency (Δ T lum) and solar modulation efficiency (Δ T sol). The Δ T lum of the pure VO2 film and the 1 at.% Zr4+-doped VO2 films was 10.9% and 11.2%, and Δ T sol was 14.4 and 15.2%, respectively.

Electrochemical study of pre- and post-transition corrosion of Zr alloys in PWR coolant

NASA Astrophysics Data System (ADS)

Macák, Jan; Novotný, Radek; Sajdl, Petr; Renčiuková, Veronika; Vrtílková, Věra

Corrosion properties of Zr-Sn and Zr-Nb zirconium alloys were studied under simulated PWR conditions (or, more exactly, VVER conditions — boric acid, potassium hydroxide, lithium hydroxide) at temperatures up to 340°C and 15MPa using in-situ electrochemical impedance spectroscopy (EIS) and polarization measurements. EIS spectra were obtained in a wide range of frequencies (typically 100kHz — 100μHz). It enabled to gain information of both dielectric properties of oxide layers developing on the Zr-alloys surface and of the kinetics of the corrosion process and the associated charge and mass transfer phenomena. Experiments were run for more than 380 days; thus, the study of all the corrosion stages (pre-transition, transition, post-transition) was possible.

Microstructures and Properties of the C/Zr-O-Si-C Composites Fabricated by Polymer Infiltration and Pyrolysis

NASA Astrophysics Data System (ADS)

Ma, Yan; Chen, Zhaohui

2013-09-01

A way to improve the ablation properties of the C/SiC composites in an oxyacetylene torch environment was investigated by the precursor infiltration and pyrolysis route using three organic precursors (zirconium butoxide, polycarbosilane, and divinylbenzene). The ceramic matrix derived from the precursors at 1200 °C was mainly a mixture of SiC, ZrO2, and C. After annealing at 1600 °C for 1 h, ZrO2 partly transformed to ZrC because of the carbothermic reductions and completely transformed to ZrC at 1800 °C in 1 h. The mechanical properties of the composites decreased with increasing temperature, while the ablation resistance increased due to the increasing content of ZrC. Compared with C/SiC composites, the ablation resistance of the C/Zr-O-Si-C composites overwhelms because of the oxide films which formed on the ablation surfaces. And, the films were composed of two layers: the porous surface layer (the mixture of ZrO2 and SiO2) and the dense underlayer (SiO2).

Multicomponent diffusion in molten salt NaF-ZrF4: Dynamical correlations and Maxwell-Stefan diffusivities

NASA Astrophysics Data System (ADS)

Baig, Mohammad Saad; Chakraborty, Brahmananda; Ramaniah, Lavanya M.

2016-05-01

NaF-ZrF4 is used as a waste incinerator and as a coolant in Generation IV reactors.Structural and dynamical properties of molten NaF-ZrF4 system were studied along with Onsagercoefficients and Maxwell-Stefan (MS) Diffusivities applying Green-Kubo formalism and molecular dynamics (MD) simulations. The zirconium ions are found to be 8 fold coordinated with fluoride ions for all temperatures and concentrations. All the diffusive flux correlations show back-scattering. Even though the MS diffusivities are expected to depend very lightly on the composition because of decoupling of thermodynamic factor, the diffusivity ĐNa-F shows interesting behavior with the increase in concentration of ZrF4. This is because of network formation in NaF-ZrF4. Positive entropy constraints have been plotted to authenticate negative diffusivities observed.

Oxidation behaviour of zirconium alloys and their precipitates - A mechanistic study

NASA Astrophysics Data System (ADS)

Proff, C.; Abolhassani, S.; Lemaignan, C.

2013-01-01

The precipitate oxidation behaviour of binary zirconium alloys containing 1 wt.% Fe, Ni, Cr or 0.6 wt.% Nb was characterised in TEM on FIB prepared transverse sections of the oxide and reported in previous studies [1,2]. In the present study the following alloys: Zr1%Cu, Zr0.5%Cu0.5%Mo and pure Zr are analysed to add to the available information. In all cases, the observed precipitate oxidation behaviour in the oxide close to the metal-oxide interface could be described either with delayed oxidation with respect to the matrix or simultaneous oxidation as the surrounding zirconium matrix. Attempt was made to explain these observations, with different parameters such as precipitate size and structure, composition and thermodynamic properties. It was concluded that the thermodynamics with the new approach presented could explain most precisely their behaviour, considering the precipitate stoichiometry and the free energy of oxidation of the constituting elements. The surface topography of the oxidised materials, as well as the microstructure of the oxide presenting microcracks have been examined. A systematic presence of microcracks above the precipitates exhibiting delayed oxidation has been found; the height of these crack calculated using the Pilling-Bedworth ratios of different phases present, can explain their origin. The protrusions at the surface in the case of materials containing large precipitates can be unambiguously correlated to the presence of these latter, and the height can be correlated to the Pilling-Bedworth ratios of the phases present as well as the diffusion of the alloying elements to the surface and their subsequent oxidation. This latter behaviour was much more considerable in the case of Fe and Cu with Fe showing systematically diffusion to the outer surface.

Lamellar zirconium phosphates to host metals for catalytic purposes.

PubMed

Ballesteros-Plata, Daniel; Infantes-Molina, Antonia; Rodríguez-Aguado, Elena; Braos-García, Pilar; Rodríguez-Castellón, Enrique

2018-02-27

In the present study a porous lamellar zirconium phosphate heterostructure (PPH) formed from zirconium(iv) phosphate expanded with silica galleries (P/Zr molar ratio equal to 2 and (Si + Zr)/P equal to 3) was prepared to host noble metals. Textural and structural characterization of PPH-noble metal materials was carried out in order to elucidate the location and dispersion of the metallic particles and the properties of the resulting material to be used in catalytic processes. In the present paper, their activity in the catalytic hydrodeoxygenation (HDO) reaction of dibenzofuran (DBF) was evaluated. X-ray diffraction (XRD), solid state nuclear magnetic resonance (NMR) and X-ray photoelectron spectroscopy (XPS) evidenced that the structure of the pillared zirconium phosphate material was not modified by the incorporation of Pt and Pd. Moreover, transmission electron microscopy (TEM) showed a different dispersion of the noble metal. The acidity of the resulting PPH-noble metal materials also changed, although in all cases the acidity was of weak nature, and the incorporation of noble metals affected Brønsted acid sites as observed from 31 P NMR spectra. In general, the textural, structural and acidic properties of the resulting materials suggest that PPH can be considered a good candidate to be used as a catalytic support. Thus, the catalytic results of the PPH-noble metal samples indicated that the Pd sample showed a stable behavior probably ascribed to a high dispersion of the active phase. However, the Pt sample suffered from fast deactivation. The selectivity to the reaction products was strongly dependent on the noble metal employed.

Modification and intercalation of layered zirconium phosphates: a solid-state NMR monitoring.

PubMed

Bakhmutov, Vladimir I; Kan, Yuwei; Sheikh, Javeed Ahmad; González-Villegas, Julissa; Colón, Jorge L; Clearfield, Abraham

2017-07-01

Several layered zirconium phosphates treated with Zr(IV) ions, modified by monomethoxy-polyethyleneglycol-monophosphate and intercalated with doxorubicin hydrochloride have been studied by solid-state MAS NMR techniques. The organic components of the phosphates have been characterized by the 13 C{ 1 H} CP MAS NMR spectra compared with those of initial compounds. The multinuclear NMR monitoring has provided to establish structure and covalent attachment of organic/inorganic moieties to the surface and interlayer spaces of the phosphates. The MAS NMR experiments including kinetics of proton-phosphorus cross polarization have resulted in an unusual structure of zirconium phosphate 6 combining decoration of the phosphate surface by polymer units and their partial intercalation into the interlayer space. Copyright © 2016 John Wiley & Sons, Ltd. Copyright © 2016 John Wiley & Sons, Ltd.

Aqueous Isolation of 17-Nuclear Zr-/Hf- Oxide Clusters during the Hydrothermal Synthesis of ZrO2/HfO2.

PubMed

Sung, Qing; Liu, Caiyun; Zhang, Guanyun; Zhang, Jian; Tung, Chen-Ho; Wang, Yifeng

2018-06-21

Novel 17-nuclear Zr-/Hf- oxide clusters ({Zr17} and {Hf17}) are isolated from aqueous systems. In the clusters, Zr/Hf ions are connected via μ3-O, μ3-OH and μ2-OH linkages into a pinwheel core which is wrapped with SO42-, HCOO- and aqua ligands. Octahedral hexanuclear Zr-/Hf- oxide clusters ({Zr6}oct and {Hf6}oct) are also isolated from the same hydrothermal system by decreasing the synthesis temperature. Structural analysis, synthetic conditions, vibrational spectra and ionic conductivity of the clusters are studied. Structural studies and synthesis inspection suggest that formation of {Zr6}oct and {Zr17} involves assembly of the same transferable building blocks, but the condensation degree and thermodynamic stability of the products increase with hydrothermal temperature. The role of {Zr6}oct and {Zr17} in the formation of ZrO2 nanocrystals are then discussed in the scenario of nonclassical nucleation theory. Besides, the Zr-oxide clusters exhibit ionic conductivity due to the mobility of protons. This study not only adds new members to the Zr-/Hf- oxide cluster family, but also establishes a connection from Zr4+ ions to ZrO2 in the hydrothermal preparation of zirconium oxide nanomaterials. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Polyoxometal cations within polyoxometalate anions. Seven-coordinate uranium and zirconium heteroatom groups in [(UO2)12(μ3-O)4(μ2-H2O)12(P2W15O56)4]32- and [Zr4(μ3-O)2(μ2-OH)2(H2O)4 (P2W16O59)2]14-

NASA Astrophysics Data System (ADS)

Gaunt, Andrew J.; May, Iain; Collison, David; Travis Holman, K.; Pope, Michael T.

2003-08-01

Two new composite polyoxotungstate anions with unprecedented structural features, [(UO2)12(μ3-O)4(μ2-H2O)12(P2W15O56)4]32- (1) and [Zr4(μ3-O)2(μ2-OH)2(H2O)4 (P2W16O59)2]14- (2) contain polyoxo-uranium and -zirconium clusters as bridging units. The anions are synthesized by reaction of Na12[P2W15O56] with solutions of UO2(NO3)2 and ZrCl4. The structure of 1 in the sodium salt contains four [P2W15O56]12- anions assembled into an overall tetrahedral cluster by means of trigonal bridging groups formed by three equatorial-edge-shared UO7 pentagonal bipyramids. The structure of anion 2 consists of a centrosymmetric assembly of two [P2W16O59]12- anions linked by a {Zr4O2(OH)2(H2O)4}10+ cluster. Both complexes in solution yield the expected two-line 31P-NMR spectra with chemical shifts of -2.95, -13.58 and -6.45, -13.69 ppm, respectively.

Zirconium phosphate reinforced short side chain perflurosulfonic acid membranes for medium temperature proton exchange membrane fuel cell application

NASA Astrophysics Data System (ADS)

Casciola, Mario; Cojocaru, Paula; Donnadio, Anna; Giancola, Stefano; Merlo, Luca; Nedellec, Yannig; Pica, Monica; Subianto, Surya

2014-09-01

Composite membranes, made of an 830 equivalent weight short-side-chain perfluorosulfonic acid ionomer and containing up to 10 wt% zirconium phosphate (ZrP), are prepared by casting dispersions of ZrP nanoparticles in the ionomer solution. 30 μm thick composite membranes are characterized by transmission electron microscopy, X-ray diffraction, stress-strain tests, conductivity measurements, water uptake and ion-exchange capacity determinations, as well as fuel cell tests in H2/air. In comparison with the neat ionomer, the tensile modulus (E) and the yield stress (Y) of the composite membranes increase with the ZrP content, both at room temperature (ΔE/E up to +75%, ΔY/Y up to +47%) and at 80 °C/70% relative humidity (ΔE/E up to +64%, ΔY/Y up to +103%). Despite their lower hydration, the composite membranes are as conductive as the neat ionomer and the in-plane conductivity at 110 °C ranges from ∼0.005 S cm-1 at 25% RH to 0.14 S cm-1 at 90% RH. The fuel cell performance of a catalyst coated membrane loaded with 10 wt% ZrP is weakly affected by temperature in the range 80-110 °C. The peak power density decreases from 0.36 W cm-2, at 80 °C, to 0.28 W cm-2 at 110 °C, where the composite membrane performs better than the neat ionomer.

Eco-friendly films prepared from plantain flour/PCL blends under reactive extrusion conditions using zirconium octanoate as a catalyst.

PubMed

Gutiérrez, Tomy J; Alvarez, Vera A

2017-12-15

Plantain flour (Musa ssp., group AAB, sub-group clone Harton)/poly(ε-caprolactone) (PCL) blends, containing glycerol as a plasticizer, were prepared by reactive extrusion (REx) in a twin-screw extruder using zirconium octanoate (Zr(Oct) 4 ) as a catalyst, followed by thermo-compression molding for film development. The films were then characterized in terms of their: infrared (FTIR) spectra, water solubility, thermogravimetric (TGA) curves, differential scanning calorimetry (DSC) thermograms, and X-ray diffraction (XDR) diffractograms, as well as their microstructural, mechanical and antimicrobial properties in order to (1) compare the effects of PCLs with two different molecular weights (M w ) on the characteristics of the plantain flour/PCL blends, and (2) determine whether using Zr(Oct) 4 in the production of active composite polymer materials improves their properties. The plantain flour/PCL blends were all developed successfully. The higher M w PCL gave more hydrophobic and thermally stable films with improved mechanical properties. The addition of the Zr(Oct) 4 catalyst to the plantain flour/PCL blends also resulted in films with similar characteristics to those described above, due to the cross-linking of the polymers. In addition, the films containing the catalyst showed antimicrobial activity against Escherichia coli O157:H7 and Staphylococcus aureus indicating a dual effect of Zr(Oct) 4 , and making it an attractive alternative for the development of active films. Copyright © 2017 Elsevier Ltd. All rights reserved.

Improving Corrosion Resistance of 316L Austenitic Stainless Steel Using ZrO2 Sol-Gel Coating in Nitric Acid Solution

NASA Astrophysics Data System (ADS)

Kazazi, Mahdi; Haghighi, Milad; Yarali, Davood; Zaynolabedini, Masoomeh H.

2018-03-01

In this study, thin-film coating of zirconium oxide (ZrO2) was prepared by sol-gel method and subsequent heat treatment process. The sol was prepared by controlled hydrolysis of zirconium tetrapropoxide using acetic acid and ethanol/acetylacetone mixture as catalyst and chelating agent, respectively, and finally deposited onto the 316L austenitic stainless steel (316L SS) using dip coating method in order to improve its corrosion resistance in nitric acid medium. The composition, structure, and morphology of the coated surface were investigated by x-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and atomic force microscopy (AFM). The obtained results from XRD and FTIR state the formation of tetragonal and monoclinic ZrO2 phase. Also, the obtained results from surface morphology investigation by SEM and AFM indicate the formation of smooth, homogeneous and uniform coatings on the steel substrate. Then, the corrosion behavior of stainless steel was investigated in a 1 and 10 M nitric acid solutions using electrochemical impedance spectroscopy and linear polarization test. The obtained results from these tests for ZrO2-coated specimens indicated a considerable improvement in the corrosion resistance of 316L stainless steel by an increase in corrosion potential and transpassive potential, and a decrease in passive current density and corrosion current density. The decrease in passive current density in both the concentration of solutions was two orders of magnitude from bare to coated specimens.

Development of bone-like zirconium oxide nanoceramic modified chitosan based porous nanocomposites for biomedical application.

PubMed

Bhowmick, Arundhati; Pramanik, Nilkamal; Jana, Piyali; Mitra, Tapas; Gnanamani, Arumugam; Das, Manas; Kundu, Patit Paban

2017-02-01

Here, zirconium oxide nanoparticles (ZrO 2 NPs) were incorporated for the first time in organic-inorganic hybrid composites containing chitosan, poly(ethylene glycol) and nano-hydroxypatite (CS-PEG-HA) to develop bone-like nanocomposites for bone tissue engineering application. These nanocomposites were characterized by FT-IR, XRD, TEM combined with SAED. SEM images and porosity measurements revealed highly porous structure having pore size of less than 1μm to 10μm. Enhanced water absorption capacity and mechanical strengths were obtained compared to previously reported CS-PEG-HA composite after addition of 0.1-0.3wt% of ZrO 2 NPs into these nanocomposites. The mechanical strengths and porosities were similar to that of human spongy bone. Strong antimicrobial effects against gram-negative and gram-positive bacterial strains were also observed. Along with getting low alkalinity pH (7.4) values, similar to the pH of human plasma, hemocompatibility and cytocompatibility with osteoblastic MG-63 cells were also established for these nanocomposites. Addition of 15wt% HA-ZrO 2 (having 0.3wt% ZrO 2 NPs) into CS-PEG (55:30wt%) composite resulted in greatest mechanical strength, porosity, antimicrobial property and cytocompatibility along with suitable water absorption capacity and compatibility with human pH and blood. Thus, this nanocomposite could serve as a potential candidate to be used for bone tissue engineering. Copyright © 2016 Elsevier B.V. All rights reserved.

Facile Separation of 5-O-Galloylquinic Acid from Chinese Green Tea Extract using Mesoporous Zirconium Phosphate.

PubMed

Ma, Yilong; Shang, Yafang; Zhu, Danye; Wang, Caihong; Zhong, Zhifeng; Xu, Ziyang

2016-05-01

5-O-Galloylquinic acid from green tea and other plants is attracting increasing attention for its antioxidant and antileishmanial bioactivities. It is always isolated using a silica column, a Sephadex column and high-performance liquid chromatography (HPLC) methods, which are either laborious or instrument dependent. To develop a new method to easily separate 5-O-galloylquinic acid. Mesoporous zirconium phosphate (m-ZrP) was prepared to conveniently separate 5-O-galloylquinic acid from Chinese green tea extract, and the target compound was easily obtained by simple steps of adsorption, washing and desorption. The effects of the green tea extraction conditions, extract concentrations, and m-ZrP adsorption/desorption dynamics on the 5-O-galloylquinic acid separation were evaluated. 5-O-Galloylquinic acid that was separated from a 70% ethanol extract of green tea was of moderate HPLC purity (92%) and recovery (88%), and an increased non-specific binding of epigallocatechin gallate (EGCG) on m-ZrP was observed in the diluted tea extract. The times for maximal adsorption of 5-O-galloylquinic acid in 70% ethanol extract and maximal desorption of 5-O-galloylquinic acid in 0.4% phosphoric acid solution were confirmed as 7 h and 5 h, respectively. A facile method to separate 5-O-galloylquinic acid from Chinese green tea extract using m-ZrP was established. Copyright © 2016 John Wiley & Sons, Ltd. Copyright © 2016 John Wiley & Sons, Ltd.

Stability and Marginal Bone Level Changes of SLActive Titanium-Zirconium Implants Placed with Flapless Surgery: A Prospective Pilot Study.

PubMed

Altinci, Pinar; Can, Gulsen; Gunes, Onur; Ozturk, Caner; Eren, Hakan

2016-12-01

Immediately-loaded, narrow-diameter implants can be a less invasive alternative for the implant-supported fixed rehabilitation of narrow, posterior crests. To determine the stability and marginal bone level (MBL) changes of narrow-diameter, titanium-zirconium (TiZr) implants placed with flapless surgery and loaded immediately in the posterior region. Thirty-eight TiZr implants (3.3 mm diameter, 10 mm length, Roxolid, Straumann AG) were placed in the posterior crests of 14 patients with computer-guided flapless surgery as a support of 3-unit posterior bridges. Eighteen implants were loaded immediately, and 20 implants were loaded conventionally. The implant stability quotients were determined at the 1, 2, 4, and 8. weeks of healing before conventional loading, and at the 3, 6, and 12. months after loading by resonance frequency analysis. The MBL changes were measured by digital radiography. The surgical protocols were accomplished without any biological complications. There was no significant difference in the stability changes of TiZr implants between the loading groups (p > .05). The MBL changes were -0.18 ± 0.27 mm and -0.24 ± 0.27 mm at the 12. month of immediate and conventional loading, respectively, which was not statistically significant (p > .05). The stability and MBL changes of TiZr implants supporting posterior 3-unit bridges were clinically acceptable at the first year of loading. © 2016 Wiley Periodicals, Inc.

Strontium and barium isotopes in presolar silicon carbide grains measured with CHILI-two types of X grains

NASA Astrophysics Data System (ADS)

Stephan, Thomas; Trappitsch, Reto; Davis, Andrew M.; Pellin, Michael J.; Rost, Detlef; Savina, Michael R.; Jadhav, Manavi; Kelly, Christopher H.; Gyngard, Frank; Hoppe, Peter; Dauphas, Nicolas

2018-01-01

We used CHILI, the Chicago Instrument for Laser Ionization, a new resonance ionization mass spectrometer developed for isotopic analysis of small samples, to analyze strontium, zirconium, and barium isotopes in 22 presolar silicon carbide grains. Twenty of the grains showed detectable strontium and barium, but none of the grains had enough zirconium to be detected with CHILI. Nine grains were excluded from further consideration since they showed very little signals (<1000 counts) for strontium as well as for barium. Among the 11 remaining grains, we found three X grains. The discovery of three supernova grains among only 22 grains was fortuitous, because only ∼1% of presolar silicon carbide grains are type X, but was confirmed by silicon isotopic measurements of grain residues with NanoSIMS. While one of the X grains showed strontium and barium isotope patterns expected for supernova grains, the two other supernova grains have 87Sr/86Sr < 0.5, values never observed in any natural sample before. From their silicon isotope ratios, the latter two grains can be classified as X2 grains, while the former grain belongs to the more common X1 group. The differences of these grains in strontium and barium isotopic composition constrain their individual formation conditions in Type II supernovae.

Chlorination of UO 2, PuO 2 and rare earth oxides using ZrCl 4 in LiCl-KCl eutectic melt

NASA Astrophysics Data System (ADS)

Sakamura, Yoshiharu; Inoue, Tadashi; Iwai, Takashi; Moriyama, Hirotake

2005-04-01

A new chlorination method using ZrCl 4 in a molten salt bath has been investigated for the pyrometallurgical reprocessing of nuclear fuels. ZrCl 4 has a high reactivity with oxygen but is not corrosive to refractory metals such as steel. Rare earth oxides (La 2O 3, CeO 2, Nd 2O 3 and Y 2O 3) and actinide oxides (UO 2 and PuO 2) were allowed to react with ZrCl 4 in a LiCl-KCl eutectic salt at 773 K to give a metal chloride solution and a precipitate of ZrO 2. An addition of zirconium metal as a reductant was effective in chlorinating the dioxides. When the oxides were in powder form, the reaction was observed to progress rapidly. Cyclic voltammetry provided a convenient way of establishing when the reaction was completed. It was demonstrated that the ZrCl 4 chlorination method, free from corrosive gas, was very simple and useful.

A high performance transparent resistive switching memory made from ZrO2/AlON bilayer structure

NASA Astrophysics Data System (ADS)

Tsai, Tsung-Ling; Chang, Hsiang-Yu; Lou, Jesse Jen-Chung; Tseng, Tseung-Yuen

2016-04-01

In this study, the switching properties of an indium tin oxide (ITO)/zirconium oxide (ZrO2)/ITO single layer device and those of a device with an aluminum oxynitride (AlON) layer were investigated. The devices with highly transparent characteristics were fabricated. Compared with the ITO/ZrO2/ITO single layer device, the ITO/ZrO2/AlON/ITO bilayer device exhibited a larger ON/OFF ratio, higher endurance performance, and superior retention properties by using a simple two-step forming process. These substantial improvements in the resistive switching properties were attributed to the minimized influence of oxygen migration through the ITO top electrode (TE), which can be realized by forming an asymmetrical conductive filament with the weakest part at the ZrO2/AlON interface. Therefore, in the ITO/ZrO2/AlON/ITO bilayer device, the regions where conductive filament formation and rupture occur can be effectively moved from the TE interface to the interior of the device.

Atomic and electronic structures of an extremely fragile liquid

PubMed Central

Kohara, Shinji; Akola, Jaakko; Patrikeev, Leonid; Ropo, Matti; Ohara, Koji; Itou, Masayoshi; Fujiwara, Akihiko; Yahiro, Jumpei; Okada, Junpei T.; Ishikawa, Takehiko; Mizuno, Akitoshi; Masuno, Atsunobu; Watanabe, Yasuhiro; Usuki, Takeshi

2014-01-01

The structure of high-temperature liquids is an important topic for understanding the fragility of liquids. Here we report the structure of a high-temperature non-glass-forming oxide liquid, ZrO2, at an atomistic and electronic level. The Bhatia–Thornton number–number structure factor of ZrO2 does not show a first sharp diffraction peak. The atomic structure comprises ZrO5, ZrO6 and ZrO7 polyhedra with a significant contribution of edge sharing of oxygen in addition to corner sharing. The variety of large oxygen coordination and polyhedral connections with short Zr–O bond lifetimes, induced by the relatively large ionic radius of zirconium, disturbs the evolution of intermediate-range ordering, which leads to a reduced electronic band gap and increased delocalization in the ionic Zr–O bonding. The details of the chemical bonding explain the extremely low viscosity of the liquid and the absence of a first sharp diffraction peak, and indicate that liquid ZrO2 is an extremely fragile liquid. PMID:25520236

The effect of copper, chromium, and zirconium on the microstructure and mechanical properties of Al-Zn-Mg-Cu alloys

NASA Technical Reports Server (NTRS)

Wagner, John A.; Shenoy, R. N.

1991-01-01

The present study evaluates the effect of the systematic variation of copper, chromium, and zirconium contents on the microstructure and mechanical properties of a 7000-type aluminum alloy. Fracture toughness and tensile properties are evaluated for each alloy in both the peak aging, T8, and the overaging, T73, conditions. Results show that dimpled rupture essentially characterize the fracture process in these alloys. In the T8 condition, a significant loss of toughness is observed for alloys containing 2.5 pct Cu due to the increase in the quantity of Al-Cu-Mg-rich S-phase particles. An examination of T8 alloys at constant Cu levels shows that Zr-bearing alloys exhibit higher strength and toughness than the Cr-bearing alloys. In the T73 condition, Cr-bearing alloys are inherently tougher than Zr-bearing alloys. A void nucleation and growth mechanism accounts for the loss of toughness in these alloys with increasing copper content.

Effect of phase transformation on optical and dielectric properties of zirconium oxide nanoparticles

NASA Astrophysics Data System (ADS)

Chintaparty, Rajababu; Palagiri, Bhavani; Reddy Nagireddy, Ramamanohar; subbha Reddy Imma Reddy, Venkata

2015-09-01

Zirconium oxide nanoparticle (ZrO2) is synthesized by the hydrothermal method at different calcination temperatures. The structural analysis is carried out by X-ray diffraction and Raman spectra. The sample prepared at 400 °C and 1100 °C showed the cubic and monoclinic phase, respectively, and the sample calcined at 600 °C and 800 °C showed the mixed phase with co-existence of cubic and monoclinic phases. Furthermore, the morphology and particle size of these samples were investigated by scanning electron microscope (SEM) and transmission electron microscope (TEM) analysis. The band gap estimated from UV-Vis spectra of ZrO2 (zirconia) nanocrystalline materials calcined at different temperatures from 400 °C to 1100 °C was in the range of 2.6-4.2 eV. The frequency dependence of dielectric constant and dielectric loss was investigated at room temperature. The low frequency region of dielectric constant is attributed to space charge effects.

Revisiting Zirconium: New Abundance Determinations with Improved Oscillator Strengths

NASA Astrophysics Data System (ADS)

Burris, Debra L.; Jones, M.; Nichols, R.

2006-12-01

The element Zirconium is produced via neutron capture (n-capture). It resides in the mass range where there is uncertainty about the production mechanism at early time. The rapid n-capture process (r-process) was believed to be responsible for the production, but no study (Burris et al 2000, Gilroy et al 1988 and others) has been able to successfully use the r-process to reproduce the abundance signature for elements in this mass range for metal-poor halo stars. It has been suggested (Sneden and Cowan 2003) that there may be an undiscovered component to the r-process. New transition probabilities for Zr II have been reported by Malcheva et al (2006). We utilize these values to make new abundance determinations for Zr in the Sun and the metal-poor halo star BD +17 3248. This work is supported in part by the AAS Small Grant Program, the Arkansas Space Grant Consortium and the UCA Undergraduate Research Council.

Time-resolved x-ray diffraction and electrical resistance measurements of structural phase transitions in zirconium

DOE PAGES

Velisavljevic, N.; Sinogeikin, S.; Saavedra, R.; ...

2014-05-07

Here, we have designed a portable pressure controller module to tune compression rates and maximum pressures attainable in a standard gas-membrane diamond anvil cell (DAC). During preliminary experiments, performed on zirconium (Zr) metal sample, pressure jumps of up to 80 GPa were systematically obtained in less than 0.2s (resulting in compression rate of few GPa/s up to more than 400 GPa/s). In-situ x-ray diffraction and electrical resistance measurements were performed simultaneously during this rapid pressure increase to provide the first time resolved data on α → ω → β structural evolution in Zr at high pressures. Direct control of compressionmore » rates and peak pressures, which can be held for prolonged time, allows for investigation of structural evolution and kinetics of structural phase transitions of materials under previously unexplored compression rate-pressure conditions that bridge traditional static and shock/dynamic experimental platforms.« less

Experimental studies of laser-ablated zirconium carbide plasma plumes: Fuel corrosion diagnostic development

NASA Astrophysics Data System (ADS)

Wantuck, P. J.; Butt, D. P.; Sappey, A. D.

Understanding the corrosion behavior of nuclear fuel materials, such as refractory carbides, in a high temperature hydrogen environment is critical for several proposed nuclear thermal propulsion (NTP) concepts. Monitoring the fuel corrosion products is important not only for understanding corrosion characteristics, but to assess the performance of an actual, operating nuclear propulsion system as well. In this paper, we describe an experimental study initiated to develop, test, and subsequently utilize non-intrusive, laser-based diagnostics to characterize the gaseous product species which are expected to evolve during the exposure of representative fuel samples to hydrogen. Laser ablation is used to produce high temperature, vapor plumes from solid solution, uranium-free, zirconium carbide (ZrC) forms for probing by other laser diagnostic methods, predominantly laser-induced fluorescence (LIF). We discuss the laser ablation technique, results of plume emission measurements, as well as the use of planar LIF to image both the ZrC plumes and actual NTP fuel corrosion constituents.

On the determination of growth stress during oxidation of pure zirconium at elevated temperature

NASA Astrophysics Data System (ADS)

Kurpaska, L.; Favergeon, J.; Lahoche, L.; Moulin, G.

2018-07-01

An experimental approach have been proposed to evaluate growth of stress during high temperature oxidation of pure zirconium. The development of stress in the oxide scale has been investigated experimentally in in-situ conditions by combining the Deflection Test in Monofacial Oxidation (DTMO) with Acoustic Emission analysis (AE). Microstructure of the sample were studied by using Scanning Electron Microscopy technique. Oxidation experiments were performed continuously during 24 h at 400 °C and 500 °C in air under normal atmospheric pressure. Taking into account purely elastic behaviour of the material, primary evolution of growth stress developed in the oxide scale during oxidation process have been estimated. Presented study of the Zr/ZrO2 system revealed two opposite phenomena of stress relief when cooling from 400 °C and 500 °C to room temperature. This study is presented as a tool to understand the phenomena of stress evolution in the zirconia layer during isothermal treatment at high temperature and after cooling.

Structural characterization of sputter-deposited SS304+x aluminum (x = 0, 4, 7 and 10 wt.%) coatings and mechanically milled titanium, zirconium and hafnium powders

NASA Astrophysics Data System (ADS)

Seelam, Uma Maheswara Rao

Study of the metastable phases obtained by non-equilibrium processing techniques has come a long way during the past five decades. New metastable phases have often given new perspectives to the research on synthesis of novel materials systems. Metastable materials produced by two non-equilibrium processing methods were studied for this dissertation---304-type austenitic stainless steel (SS304 or Fe-18Cr-8Ni)+aluminum coatings produced by plasma enhanced magnetron sputter-deposition (PEMS) and nanocrystalline Ti, Zr and Hf powders processed by mechanical milling (MM). The objective of the study was to understand the crystallographic and microstructural aspects of these materials. Four SS304+Al coatings with a nominal Al percentages of 0, 4, 7 and 10 wt.% in the coatings were deposited on an SS304 substrate by PEMS using SS304 and Al targets. The as-deposited coatings were characterized by x-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and three-dimensional atom probe microscopy (3DAP). Surface morphology and chemical analysis were studied by SEM. Phase identification was carried out by XRD and TEM. The microstructural features of all the coatings, as observed in the TEM, consisted of columnar grains with the columnar grain width (a measure of grain size) increasing with an increase in the Al content. The coatings had grains with average grain sizes of about 100, 290, 320 and 980 nm, respectively for 0, 4, 7 and 10 wt.% Al. The observed grain structures and increase in grain size were related to substrate temperature during deposition. XRD results indicated that the Al-free coating consisted of the non-equilibrium ferrite and sigma phases. In the 4Al, 7Al and 10Al coatings, equilibrium ferrite and B2 phases were observed but no sigma phase was found. In 10Al coating, we were able to demonstrate experimentally using 3DAP studies that NiAl phase formation is preferred over the FeAl phase at nano scale. During mechanical milling of the hexagonal close packed (HCP) metals Hf, Ti and Zr powders, unknown nanocrystalline phases with face centered cubic (FCC) structure were found. The FCC phases could be either allotropes of the respective metals or impurity stabilized phases. However, upon MM under high purity conditions, it was revealed that the FCC phases were impurity stabilized. The decrease in crystallite size down to nanometer levels, an increase in atomic volume, lattice strain, and possible contamination were the factors responsible for the transformation.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Archana, P. S.; Gupta, Arunava; Yusoff, Mashitah M.

Zirconium (Zr) is doped up to 5 at. % in anatase TiO{sub 2} nanowires by electrospinning and used as working electrode in dye-sensitized solar cells. Variations observed in the photovoltaic parameters were correlated by electrochemical impedance spectroscopy, open circuit voltage decay, and X-ray diffraction measurements. Results show that homovalent substitution of Zr in TiO{sub 2} increased the chemical capacitance and electron diffusion coefficient which in turn decreased charge transport resistance and charge transit time. However, lattice strain due to size mismatch between the Zr{sup 4+} and Ti{sup 4+} ions decreased open circuit voltage and fill factor thereby setting a trade-off betweenmore » doping concentration and photovoltaic properties.« less

SPM oxidation and parallel writing on zirconium nitride thin films

NASA Astrophysics Data System (ADS)

Farkas, N.; Comer, J. R.; Zhang, G.; Evans, E. A.; Ramsier, R. D.; Dagata, J. A.

2005-07-01

Systematic investigation of the SPM oxidation process of sputter-deposited ZrN thin films is reported. During the intrinsic part of the oxidation, the density of the oxide increases until the total oxide thickness is approximately twice the feature height. Further oxide growth is sustainable as the system undergoes plastic flow followed by delamination from the ZrN-silicon interface keeping the oxide density constant. ZrN exhibits superdiffusive oxidation kinetics in these single tip SPM studies. We extend this work to the fabrication of parallel oxide patterns 70 nm in height covering areas in the square centimeter range. This simple, quick, and well-controlled parallel nanolithographic technique has great potential for biomedical template fabrication.

Uranium-Bearing Srilankite from High-Pressure Garnetites of the Southern Urals: First Data

NASA Astrophysics Data System (ADS)

Gottman, I. A.; Pushkarev, E. V.; Khiller, V. V.

2018-04-01

This work presents the results of studying srilankite, a rare zirconium titanate (ZrTi2O6), associated with ilmenite, rutile, zircon, uraninite, and other minerals discovered in high-pressure garnetites of the lherzolite Mindyak massif (Southern Urals). Srilankite occurs as inclusions in ilmenite and rutile of up to several tens of microns in size. It was established for the first time that srilankite contains a significant UO2 admixture (up to 20%). The negative correlation between Zr and U is evidence of isomorphism in the srilankite-brannerite system. The association of srilankite with high-Zr rutile indicates that formation of these minerals occurred at T > 850°C.

Sulfuric acid functional zirconium (or aluminum) incorporated mesoporous MCM-48 solid acid catalysts for alkylation of phenol with tert-butyl alcohol

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jiang, Tingshun, E-mail: tshjiang@mail.ujs.edu.cn; Cheng, Jinlian; Liu, Wangping

2014-10-15

Several zirconium (or aluminum) incorporated mesoporous MCM-48 solid acid catalysts (SO{sub 4}{sup 2−}/Zr-MCM-48 and SO{sub 4}{sup 2−}/Al-MCM-48) were prepared by the impregnation method and their physicochemical properties were characterized by means of XRD, FT-IR, TEM, NH{sub 3}-TPD and N{sub 2} physical adsorption. Also, the catalytic activities of these solid acid catalysts were evaluated by the alkylation of phenol with tert-butyl alcohol. The effect of weight hour space velocity (WHSV), reaction time and reaction temperature on catalytic properties was also studied. The results show that the SO{sub 4}{sup 2−}/Zr-MCM-48 and SO{sub 4}{sup 2−}/Al-MCM-48 still have good mesoporous structure and long rangemore » ordering. Compared with the Zr (or Al)–MCM-48 samples, SO{sub 4}{sup 2−}/Zr-MCM-48 and SO{sub 4}{sup 2−}/Al-MCM-48 solid acid catalysts have strong acidity and exhibit high activities in alkylation reaction of phenol with tert-butyl alcohol. The SO{sub 4}{sup 2−}/Zr-MCM-48-25 (molar ratio of Si/Zr=0.04) catalyst was found to be the most promising and gave the highest phenol conversion among all catalysts. A maximum phenol conversion of 91.6% with 4-tert-butyl phenol (4-TBP) selectivity of 81.8% was achieved when the molar ratio of tert-butyl alcohol:phenol is 2:1, reaction time is 2 h, the WHSV is 2 h{sup −1} and the reaction temperature is 140 °C. - Highlights: • Sulfuric acid functional mesoporous solid acid catalysts were prepared via impregnation method. • The alkylation of phenol with tert-butyl alcohol was carried out over these solid acid catalysts. • The catalytic activity of SO{sub 4}{sup 2−}/Zr-MCM-48-25 catalyst is much higher than that of the others. • A maximum phenol conversion of 91.6% was achieved under optimum reaction conditions for SO{sub 4}{sup 2−}/Zr-MCM-48-25.« less

Optical properties of zirconium oxynitride films: The effect of composition, electronic and crystalline structures

NASA Astrophysics Data System (ADS)

Carvalho, P.; Borges, J.; Rodrigues, M. S.; Barradas, N. P.; Alves, E.; Espinós, J. P.; González-Elipe, A. R.; Cunha, L.; Marques, L.; Vasilevskiy, M. I.; Vaz, F.

2015-12-01

This work is devoted to the investigation of zirconium oxynitride (ZrOxNy) films with varied optical responses prompted by the variations in their compositional and structural properties. The films were prepared by dc reactive magnetron sputtering of Zr, using Ar and a reactive gas mixture of N2 + O2 (17:3). The colour of the films changed from metallic-like, very bright yellow-pale and golden yellow, for low gas flows to red-brownish for intermediate gas flows. Associated to this colour change there was a significant decrease of brightness. With further increase of the reactive gas flow, the colour of the samples changed from red-brownish to dark blue or even to interference colourations. The variations in composition disclosed the existence of four different zones, which were found to be closely related with the variations in the crystalline structure. XRD analysis revealed the change from a B1 NaCl face-centred cubic zirconium nitride-type phase for films prepared with low reactive gas flows, towards a poorly crystallized over-stoichiometric nitride phase, which may be similar to that of Zr3N4 with some probable oxygen inclusions within nitrogen positions, for films prepared with intermediate reactive gas flows. For high reactive gas flows, the films developed an oxynitride-type phase, similar to that of γ-Zr2ON2 with some oxygen atoms occupying some of the nitrogen positions, evolving to a ZrO2 monoclinic type structure within the zone where films were prepared with relatively high reactive gas flows. The analysis carried out by reflected electron energy loss spectroscopy (REELS) revealed a continuous depopulation of the d-band and an opening of an energy gap between the valence band (2p) and the Fermi level close to 5 eV. The ZrN-based coatings (zone I and II) presented intrinsic colourations, with a decrease in brightness and a colour change from bright yellow to golden yellow, red brownish and dark blue. Associated to these changes, there was also a shift of the reflectivity minimum to lower energies, with the increase of the non-metallic content. The samples lying in the two last zones (zone III, oxynitride and zone IV, oxide films) revealed a typical semi-transparent-optical behaviour showing interference-like colourations only due to the complete depopulation of the d band at the Fermi level. The samples lying in these zones presented also an increase of the optical bandgap from 2 to 3.6 eV.

Competitive Heterogeneous Nucleation Between Zr and MgO Particles in Commercial Purity Magnesium

NASA Astrophysics Data System (ADS)

Peng, G. S.; Wang, Y.; Fan, Z.

2018-04-01

Grain refining of commercial purity (CP) Mg by Zr addition with intensive melt shearing prior to solidification has been investigated. Experimental results showed that, when intensive melt shearing is imposed prior to solidification, the grain structure of CP Mg exhibits a complex changing pattern with increasing Zr addition. This complex behavior can be attributed to the change of nucleating particles in terms of their crystal structure, size, and number density with varied Zr additions. Naturally occurring MgO particles are found to be {100} faceted with a cubic morphology and 50 to 300 nm in size. Such MgO particles are usually populated densely in a liquid film (usually referred as oxide film) and can be effectively dispersed by intensive melt shearing. It has been confirmed that the dispersed MgO particles can act as nucleating substrates resulting in a significant grain refinement of CP Mg when no other more potent particles are present in the melt. However, Zr particles in the Mg-Zr alloys are more potent than MgO particles for nucleation of Mg due to their same crystal structure and similar lattice parameters with Mg. With the addition of Zr, Zr and the MgO particles co-exist in the melt. Grain refining efficiency is closely related to the competition for heterogeneous nucleation between Zr and the MgO particles. The final solidified microstructure is mainly determined by the interplay of three factors: nucleation potency (measured by lattice misfit), particle size, and particle number density.

Competitive Heterogeneous Nucleation Between Zr and MgO Particles in Commercial Purity Magnesium

NASA Astrophysics Data System (ADS)

Peng, G. S.; Wang, Y.; Fan, Z.

2018-06-01

Grain refining of commercial purity (CP) Mg by Zr addition with intensive melt shearing prior to solidification has been investigated. Experimental results showed that, when intensive melt shearing is imposed prior to solidification, the grain structure of CP Mg exhibits a complex changing pattern with increasing Zr addition. This complex behavior can be attributed to the change of nucleating particles in terms of their crystal structure, size, and number density with varied Zr additions. Naturally occurring MgO particles are found to be {100} faceted with a cubic morphology and 50 to 300 nm in size. Such MgO particles are usually populated densely in a liquid film (usually referred as oxide film) and can be effectively dispersed by intensive melt shearing. It has been confirmed that the dispersed MgO particles can act as nucleating substrates resulting in a significant grain refinement of CP Mg when no other more potent particles are present in the melt. However, Zr particles in the Mg-Zr alloys are more potent than MgO particles for nucleation of Mg due to their same crystal structure and similar lattice parameters with Mg. With the addition of Zr, Zr and the MgO particles co-exist in the melt. Grain refining efficiency is closely related to the competition for heterogeneous nucleation between Zr and the MgO particles. The final solidified microstructure is mainly determined by the interplay of three factors: nucleation potency (measured by lattice misfit), particle size, and particle number density.

A sensitive determination of terbutaline in pharmaceuticals and urine samples using a composite electrode based on zirconium oxide nanoparticles.

PubMed

Baytak, Aysegul Kutluay; Teker, Tugce; Duzmen, Sehriban; Aslanoglu, Mehmet

2016-10-01

An accurate and precise determination of terbutaline has been carried out using a glassy carbon electrode (GCE) modified with a composite of multi-walled carbon nanotubes (MWCNTs) and nanoparticles of zirconium oxide (ZrO2NPs). Energy dispersive X-ray and scanning electron microscopic techniques were utilized for the characterization of the composite layer. Terbutaline exhibited a broad oxidation peak at 770mV on a GCE. However, MWCNTs/GCE presented an electrocatalytic effect toward the oxidation of terbutaline with a better anodic peak at 660mV. Furthermore, the electrochemical behavior of terbutaline has greatly been improved at a GCE modified with a composite of MWCNTs and nanoparticles of ZrO2. The ZrO2NPs/MWCNTs/GCE exhibited a sharp anodic wave at 645mV with a large enhancement of the current response for terbutaline. Square wave voltammetry (SWV) was performed for the determination of terbutaline at ZrO2NPs/MWCNTs/GCE. A linear plot was obtained for the current responses of terbutaline against concentrations in the range of 10-160nM yielding a detection limit of 2.25nM (based on 3Sb/m). Improved voltammetric behavior, long-time stability and good reproducibility were obtained for terbutaline at the proposed electrode. A mean recovery of 101.2% with an RSD% of 1.9 was obtained for the analysis of the drug formulation. The accurate and precise quantification of terbutaline makes the ZrO2NPs/MWCNTs/GCE system of great interest for monitoring its therapeutic use. Copyright © 2016 Elsevier B.V. All rights reserved.

A STUDY OF THE STABILITY OF ZIRCONIUM AND HAFNIUM TETRAHALIDES ON HITTING A HOT SURFACE IN VACUUM (in Russian)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tsirel'nikov, V.I.; Komissarova, L.N.; Spitsyn, V.I.

1962-09-01

The decomposition coefficients of the chlorides, bromides, and iodides of Zr and Hf were determined as a function of the temperature of a hot surface. The tetrahalides were carefully purified in an inert atmosphere of argon. The halide compound in a quartz ampoule was heated by a removable heater. The vapors passed through a capillary opening and struck a tungsten foil 0.5 mm thick and 12 to 15 mm wide. The Mo foil was heated electrically to control the surface temperature which was measured by an optical pyrometer. The tetrahalide decomposed according to the following reaction: Me(Hal)/sub 4/ yields Memore » + 2(Hal)/sub 2/. The lower halides dissociated completely to metal and free halides, since the temperature was >600 deg C. The Mo backing was dissolved in nitric acid, and the unsupported metal deposit of Zr or Hf was weighed, The decomposition coefficient was calcuweight of metal evaporated. Zrl/sub 4/ decomposed completely (100%) at 1500 deg C, while only 96% of the HfI/sub 4/ was decomposed at this temperature. The ZrBr/sub 4/ and HfBr/sub 4/ were decomposed by 68 and 61% respectively. The ZrCl/sub 4/ and HfCl/sub 4/ were stable at l500 deg C (5% of the ZrCl/sub 4/ was decomposed at l500 deg C). In all cases, the hafnium halide was more stable than the zirconium halide, especially in the case of the iodides. The decomposition was directly proportional to the temperature of the molybdenum target. (TTT)« less

Thermal Stability of Nanocrystalline Alloys by Solute Additions and A Thermodynamic Modeling

NASA Astrophysics Data System (ADS)

Saber, Mostafa

Nanocrystalline alloys show superior properties due to their exceptional microstructure. Thermal stability of these materials is a critical aspect. It is well known that grain boundaries in nanocrystalline microstructures cause a significant increase in the total free energy of the system. A driving force provided to reduce this excess free energy can cause grain growth. The presence of a solute addition within a nanocrystalline alloy can lead to the thermal stability. Kinetic and thermodynamic stabilization are the two basic mechanisms with which stability of a nanoscale grain size can be achieved at high temperatures. The basis of this thesis is to study the effect of solute addition on thermal stability of nanocrystalline alloys. The objective is to determine the effect of Zr addition on the thermal stability of mechanically alloyed nanocrysatillne Fe-Cr and Fe-Ni alloys. In Fe-Cr-Zr alloy system, nanoscale grain size stabilization was maintained up to 900 °C by adding 2 at% Zr. Kinetic pinning by intermetallic particles in the nanoscale range was identified as a primary mechanism of thermal stabilization. In addition to the grain size strengthening, intermetallic particles also contribute to strengthening mechanisms. The analysis of microhardness, XRD data, and measured grain sizes from TEM micrographs suggested that both thermodynamic and kinetic mechanisms are possible mechanisms. It was found that alpha → gamma phase transformation in Fe-Cr-Zr system does not influence the grain size stabilization. In the Fe-Ni-Zr alloy system, it was shown that the grain growth in Fe-8Ni-1Zr alloy is much less than that of pure Fe and Fe-8Ni alloy at elevated temperatures. The microstructure of the ternary Fe-8Ni-1Zr alloy remains in the nanoscale range up to 700 °C. Using an in-situ TEM study, it was determined that drastic grain growth occurs when the alpha → gamma phase transformation occurs. Accordingly, there can be a synergistic relationship between grain growth and alpha → gamma phase transformation in Fe-Ni-Zr alloys. In addition to the experimental study of thermal stabilization of nanocrystalline Fe-Cr-Zr or Fe-Ni-Zr alloys, the thesis presented here developed a new predictive model, applicable to strongly segregating solutes, for thermodynamic stabilization of binary alloys. This model can serve as a benchmark for selecting solute and evaluating the possible contribution of stabilization. Following a regular solution model, both the chemical and elastic strain energy contributions are combined to obtain the mixing enthalpy. The total Gibbs free energy of mixing is then minimized with respect to simultaneous variations in the grain boundary volume fraction and the solute concentration in the grain boundary and the grain interior. The Lagrange multiplier method was used to obtained numerical solutions. Application are given for the temperature dependence of the grain size and the grain boundary solute excess for selected binary system where experimental results imply that thermodynamic stabilization could be operative. This thesis also extends the binary model to a new model for thermodynamic stabilization of ternary nanocrystalline alloys. It is applicable to strongly segregating size-misfit solutes and uses input data available in the literature. In a same manner as the binary model, this model is based on a regular solution approach such that the chemical and elastic strain energy contributions are incorporated into the mixing enthalpy DeltaHmix, and the mixing entropy DeltaSmix is obtained using the ideal solution approximation. The Gibbs mixing free energy Delta Gmix is then minimized with respect to simultaneous variations in grain growth and solute segregation parameters. The Lagrange multiplier method is similarly used to obtain numerical solutions for the minimum Delta Gmix. The temperature dependence of the nanocrystalline grain size and interfacial solute excess can be obtained for selected ternary systems. As an example, model predictions are compared to experimental results for Fe-Cr-Zr and Fe-Ni-Zr alloy systems. Consistency between the experimental results and the present model predictions provide a more rigorous criterion for investigating thermal stabilization. However, other possible contributions for grain growth stabilization should still be considered.

Removal of model viruses, E. coli and Cryptosporidium oocysts from surface water by zirconium and chitosan coagulants.

PubMed

Christensen, Ekaterina; Nilsen, Vegard; Håkonsen, Tor; Heistad, Arve; Gantzer, Christophe; Robertson, Lucy J; Myrmel, Mette

2017-10-01

The present work evaluates the effect of contact filtration, preceded by coagulation with zirconium (Zr) and chitosan coagulants, on model microorganisms and waterborne pathogens. River water intended for potable water production was spiked with MS2 and Salmonella Typhimurium 28B bacteriophages, Escherichia coli, and Cryptosporidium parvum oocysts prior to coagulation. The hygienic performance demonstrated by Zr comprised 3.0-4.0 log 10 removal of viruses and 5.0-6.0 log 10 removal of E. coli and C. parvum oocysts. Treatment with chitosan resulted in a removal of 2.5-3.0 log 10 of viruses and parasites, and 4.5-5.0 log 10 of bacteria. A reference coagulant, polyaluminium chloride (PACl), gave a 2.5-3.0 log 10 removal of viruses and 4.5 log 10 of E. coli. These results indicate that both Zr and chitosan enable adequate removal of microorganisms from surface water. The present study also attempts to assess removal rates of the selected microorganisms with regard to their size and surface properties. The isoelectric point of the Salmonella Typhimurium 28B bacteriophage is reported for the first time. The retention of the selected microorganisms in the filter bed appeared to have some correlation with their size, but the effect of the charge remained unclear.

Zirconium, calcium, and strontium contents in magnesium based biodegradable alloys modulate the efficiency of implant-induced osseointegration

PubMed Central

Mushahary, Dolly; Sravanthi, Ragamouni; Li, Yuncang; Kumar, Mahesh J; Harishankar, Nemani; Hodgson, Peter D; Wen, Cuie; Pande, Gopal

2013-01-01

Development of new biodegradable implants and devices is necessary to meet the increasing needs of regenerative orthopedic procedures. An important consideration while formulating new implant materials is that they should physicochemically and biologically mimic bone-like properties. In earlier studies, we have developed and characterized magnesium based biodegradable alloys, in particular magnesium-zirconium (Mg-Zr) alloys. Here we have reported the biological properties of four Mg-Zr alloys containing different quantities of strontium or calcium. The alloys were implanted in small cavities made in femur bones of New Zealand White rabbits, and the quantitative and qualitative assessments of newly induced bone tissue were carried out. A total of 30 experimental animals, three for each implant type, were studied, and bone induction was assessed by histological, immunohistochemical and radiological methods; cavities in the femurs with no implants and observed for the same period of time were kept as controls. Our results showed that Mg-Zr alloys containing appropriate quantities of strontium were more efficient in inducing good quality mineralized bone than other alloys. Our results have been discussed in the context of physicochemical and biological properties of the alloys, and they could be very useful in determining the nature of future generations of biodegradable orthopedic implants. PMID:23976848

NADH Electrooxidation Using Bis(1,10-phenanthroline-5,6-dione) (2,2′-bipyridine)ruthenium(II)-Exchanged Zirconium Phosphate Modified Carbon Paste Electrodes

PubMed Central

Santiago, Mitk’El B.; Vélez, Meredith M.; Borrero, Solmarie; Díaz, Agustín; Casillas, Craig A.; Hofmann, Cristina; Guadalupe, Ana R.; Colón, Jorge L.

2007-01-01

We present a carbon paste electrode (CPE) modified using the electron mediator bis(1,10-phenanthroline-5,6-dione) (2,2′-bipyridine)ruthenium(II) ([Ru(phend)2bpy]2+) exchanged into the inorganic layered material zirconium phosphate (ZrP). X-Ray powder diffraction showed that the interlayer distance of ZrP increases upon [Ru(phend)2bpy]2+ intercalation from 10.3 Å to 14.2 Å. The UV-vis and IR spectroscopies results showed the characteristic peaks expected for [Ru(phend)2bpy]2+. The UV-vis spectrophotometric results indicate that the [Ru(phend)2bpy]2+ concentration inside the ZrP layers increased as a function of the loading level. The exchanged [Ru(phend)2bpy]2+ exhibited luminescence even at low concentration. Modified CPEs were constructed and analyzed using cyclic voltammetry. The intercalated mediator remained electroactive within the layers (E°′ = −38.5 mV vs. Ag/AgCl, 3.5 M NaCl) and electrocatalysis of NADH oxidation was observed. The kinetics of the modified CPE shows a Michaelis –Menten behavior. This CPE was used for the oxidation of NADH in the presence of Bakers’ yeast alcohol dehydrogenase. A calibration plot for ethanol is presented. PMID:18516242

Investigations on the effect of grain size on hot tearing susceptibility of MgZn1Y2 alloy

NASA Astrophysics Data System (ADS)

Zhou, Z. J.; Liu, Z.; Wang, Y.; Mao, P. L.; Tang, W. R.; Zhou, Y.

2018-05-01

Effect of grain size on hot tearing susceptibility of MgZn1Y2 alloy was explored in the present paper. Based on the microstructure observation and phase constitution analysis results by the method of OM, SEM, EBSD and XRD, it was found that the addition of 0.2 wt% C2Cl6 or 0.5 wt% Zr could reduced the grain size significantly. The addition of Zr had the better effect than that of 0.2 wt% C2Cl6. The average grain size reduced from 55.48 μm to 20.64 μm, and the average grain shape aspect ratio reduced from 1.859 to 1.49 with the addition of Zr. Although the addition of 0.2 wt% C2Cl6 refined grain, it also reduced the amount of LPSO phase. It was also found that the dendrite coherent temperature (Tcoh) decreased with decreasing of the grain size of the alloy, while the dendrite coherent solid fraction ({{{{f}}}{{s}}}{{coh}}) increased with decreasing of the alloy. The modified Clyne-Davies model was used to predict the hot cracking susceptibility of the alloy. The predicted results indicated that the hot tearing susceptibility decreased with grain refinement. With addition of 0.2 wt% Zr, the predicted hot tearing sensitivity value was reduced by about 2.5 times than that of the alloy without the addition of Zr.

The effect of environmental factors on selected mechanical properties of zirconium dioxide

NASA Astrophysics Data System (ADS)

Wirwicki, W.; Andrzejewska, A.; Andryszczyk, M.; Siemianowski, P.

2018-04-01

In many centers around the world, research studies are carried out on the mechanical strength of dental materials and glued joints. A literature review shows the variety of testing techniques related to analyzing the strength and durability of the material itself and the glued joints. In dental ceramics, zirconium dioxide is most often used as a base material, and chemically it consists of 97% ZrO2 and 3% Y2O3. This study was to determine the mechanical properties of zirconium dioxide under different environmental conditions. The material is used for the production of dental crowns and tooth bridges in the CAD/CAM technology. This medium is currently one of the most advanced-generation materials used for prosthetic and implant restorations. They were then subjected to a three-point bending test on the Instron ElektroPlus E3000 durability machine. Storage conditions and time have a positive influence on reducing variation in zirconium resistance for active forces and destructive stresses.

Theoretical investigation of microstructure evolution and deformation of zirconium under neutron irradiation

DOE PAGES

Barashev, A. V.; Golubov, S. I.; Stoller, R. E.

2015-06-01

We studied the radiation growth of zirconium using a reaction–diffusion model which takes into account intra-cascade clustering of self-interstitial atoms and one-dimensional diffusion of interstitial clusters. The observed dose dependence of strain rates is accounted for by accumulation of sessile dislocation loops during irradiation. Moreover, the computational model developed and fitted to available experimental data is applied to study deformation of Zr single crystals under irradiation up to hundred dpa. Finally, the effect of cold work and the reasons for negative prismatic strains and co-existence of vacancy and interstitial loops are elucidated.

Crystal plasticity simulation of Zirconium tube rolling using multi-grain representative volume element

NASA Astrophysics Data System (ADS)

Isaenkova, Margarita; Perlovich, Yuriy; Zhuk, Dmitry; Krymskaya, Olga

2017-10-01

The rolling of Zirconium tube is studied by means of the crystal plasticity viscoplastic self-consistent (VPSC) constitutive modeling. This modeling performed by a dislocation-based constitutive model and a spectral solver using open-source simulation of DAMASK kit. The multi-grain representative volume elements with periodic boundary conditions are used to predict the texture evolution and distributions of strain and stresses. Two models for randomly textured and partially rolled material are deformed to 30% reduction in tube wall thickness and 7% reduction in tube diameter. The resulting shapes of the models are shown and distributions of strain are plotted. Also, evolution of grain's shape during deformation is shown.

Thermal expansion of phosphates with the NaZr2(PO4)3 structure containing lanthanides and zirconium: R 0.33Zr2(PO4)3 ( R = Nd, Eu, Er) and Er0.33(1- x) Zr0.25 x Zr2(PO4)3

NASA Astrophysics Data System (ADS)

Volgutov, V. Yu.; Orlova, A. I.

2015-09-01

Phosphates R 0.33Zr2(PO4)3 ( R = Nd, Eu, or Er) and Er0.33(1- х)Zr0.25Zr2(PO4)3 ( х = 0, 0.25, 0.5, 0.75, 1.0) of the NaZr2(PO4)3 family have been synthesized and investigated by high-temperature X-ray diffraction. The crystallochemical approach is used to obtain compounds with expected small and controllable thermal-expansion parameters. Phosphates with close-to-zero thermal-expansion parameters, including those with low thermal-expansion anisotropy, have been obtained: Nd0.33Zr2(PO4)3 with α a =-2.21 × 10-6 °С-1, α c = 0.81 × 10-6 °С-1, and Δα = 3.02 × 10-6 °С-1 and Er0.08Zr0.19Zr2(PO4)3 with α a =-1.86 × 10-6 °С-1, α c = 1.73 × 10-6 °С-1, and Δα = 3.58 × 10-6 °С-1.

Stoichiometry effect on the irradiation response in the microstructure of zirconium carbides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Young Yang; Wei-Yang Lo; Clayton Dickerson

2014-11-01

Zone-refined ultra high pure ZrC with five C/Zr ratios ranging from 0.84 to 1.17 was irradiated using a 2 MeV proton beam at 1125 C. The stoichiometry effect on the irradiation response of ZrC microstructure was examined using transmission electron microscopy following the irradiation. The irradiated microstructures generally feature a high density of perfect dislocation loops particularly at away from the graphite precipitates, and the C/Zr ratio shows a notable effect on the size and density of dislocation loops. The dislocation loops are identified as interstitial type perfect loops, and it was indirectly proved that the dislocation loop core likelymore » consists of carbon atoms. Graphite precipitates that form with excess carbon in the super-stoichiometric ZrC are detrimental, and the dramatic increases in the size of and density of dislocation loops in the vicinity of graphite precipitates in ZrC phase were observed. Irradiationinduced faceted voids were only observed in ZrC0.95, which is attributed to the pre-existing dislocation lines as biased sinks for vacancies.« less

Crystalline matrices for the immobilization of plutonium and actinides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Anderson, E.B.; Burakov, E.E.; Galkin, Ya.B.

1996-05-01

The management of weapon plutonium, disengaged as a result of conversion, is considered together with the problem of the actinide fraction of long-lived high level radioactive wastes. It is proposed to use polymineral ceramics based on crystalline host-phases: zircon ZrSiO{sub 4} and zirconium dioxide ZrO{sub 2}, for various variants of the management of plutonium and actinides (including the purposes of long-term safe storage or final disposal from the human activity sphere). It is shown that plutonium and actinides are able to form with these phases on ZrSiO{sub 4} and ZrO{sub 2} was done on laboratory level by the hot pressingmore » method, using the plasmochemical calcination technology. To incorporate simulators of plutonium into the structure of ZrSiO{sub 4} and ZrO{sub 2} in the course of synthesis, an original method developed by the authors as a result of studying the high-uranium zircon (Zr,U) SiO{sub 4} form Chernobyl {open_quotes}lavas{close_quotes} was used.« less

The Effect of Boron and Zirconium on the Structure and Tensile Properties of the Cast Nickel-Based Superalloy ATI 718Plus

NASA Astrophysics Data System (ADS)

Hosseini, Seyed Ali; Abbasi, Seyed Mehdi; Madar, Karim Zangeneh

2018-04-01

The effects of boron and zirconium on cast structure, hardness, and tensile properties of the nickel-based superalloy 718Plus were investigated. For this purpose, five alloys with different contents of boron and zirconium were cast via vacuum induction melting and then purified via vacuum arc remelting. Microstructural analysis by light-optical microscope and scanning electron microscope equipped with energy-dispersive x-ray spectroscopy and phase studies by x-ray diffraction analysis were performed. The results showed that boron and zirconium tend to significantly reduce dendritic arm spacing and increase the amount of Laves, Laves/gamma eutectic, and carbide phases. It was also found that boron led to the formation of B4C and (Cr, Fe, Mo, Ni, Ti)3B2 phases and zirconium led to the formation of intermetallic phases and ZrC carbide. In the presence of boron and zirconium, the hardness and its difference between dendritic branches and inter-dendritic spaces increased by concentrating such phases as Laves in the inter-dendritic spaces. These elements had a negative effect on tensile properties of the alloy, including ductility and strength, mainly because of the increase in the Laves phase. It should be noted that the largest degradation of the tensile properties occurred in the alloys containing the maximum amount of zirconium.

Defects versus grain size effects on the ferromagnetism of ZrO2 nanocrystals clarified by positron annihilation

NASA Astrophysics Data System (ADS)

Wang, D. D.; Qi, N.; Jiang, M.; Chen, Z. Q.

2013-01-01

Undoped ZrO2 nanocrystals were annealed in open air from 100 °C to 1300 °C. X-ray diffraction and transmission electron microscope were used to study the structure change and grain growth. Both the methods reveal that the ZrO2 grain size has very slight increase after annealing up to 900 °C. Positron annihilation measurements reveal a high concentration of vacancy defects which most probably exist in the grain boundary region. Thermal annealing above 500 °C causes recovery of these defects, and after annealing at 1200 °C, most of them are removed. Room temperature ferromagnetism is observed for the sample annealed at 100 °C and 500 °C. The magnetization becomes very weak after the nanocrystals are annealed at 700 °C, and it almost disappears at 1000 °C. It is clear that the intrinsic ferromagnetism in our ZrO2 nanocrystals is mostly related with the interfacial defects instead of grain size effects.

AN ATTEMPT TO LOCATE INTERMETALLIC PARTICLES IN ZIRCONIUM ALLOYS USING A BITTER FIGURE TECHNIQUE

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cox, B.; Harder, B.R.

1961-10-01

The compound ZrFe/sub 2/ is known to be ferromagnetic, and an attempt to locate particles of magnetic material in zircaloy-2 and dilute Zr- Fe alloys by a Bitter figure technlque is described. An Fe/sub 3/O/sub 4/ sol in water-soluble plastic was used to prepare Bitter figures of the alloy surfaces in the form of replicas, which were then examined in an electron microscope. No magnetic particles were located in either zircaloy-2 or a Zr-O.3% Fe alloy. Subsequent work on specimens of ZrFe/sub 2/ showed that the failure to detect it in the dilute alloys arose because the size of themore » intermetallic particles in the latter was smaller than the size of the magnetic domains. (auth)« less

High-voltage SPM oxidation of ZrN: materials for multiscale applications

NASA Astrophysics Data System (ADS)

Farkas, N.; Comer, J. R.; Zhang, G.; Evans, E. A.; Ramsier, R. D.; Dagata, J. A.

2005-02-01

Scanning probe microscope (SPM) oxidation was used to form zirconium oxide features on 200 nm thick ZrN films. The features exhibit rapid yet controlled growth kinetics, even in contact mode with 70 V dc applied between the probe tip and substrate. The features grown for times longer than 10 s are higher than 200 nm, and reach more than 1000 nm in height after 300 s. Long-time oxidation experiments and selective etching of the oxides and nitrides lead us to propose that as the oxidation reaches the silicon substrate, delamination occurs with the simultaneous formation of a thin layer of new material at the ZrN/Si interface. High-voltage oxide growth on ZrN is fast and sustainable, and the robust oxide features are promising candidates for multiscale (nanometre-to-micrometre) applications.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Baig, Mohammad Saad, E-mail: saad110baig@gmail.com; Chakraborty, Brahmananda; Ramaniah, Lavanya M.

NaF-ZrF{sub 4} is used as a waste incinerator and as a coolant in Generation IV reactors.Structural and dynamical properties of molten NaF-ZrF{sub 4} system were studied along with Onsagercoefficients and Maxwell–Stefan (MS) Diffusivities applying Green–Kubo formalism and molecular dynamics (MD) simulations. The zirconium ions are found to be 8 fold coordinated with fluoride ions for all temperatures and concentrations. All the diffusive flux correlations show back-scattering. Even though the MS diffusivities are expected to depend very lightly on the composition because of decoupling of thermodynamic factor, the diffusivity Đ{sub Na-F} shows interesting behavior with the increase in concentration of ZrF{submore » 4}. This is because of network formation in NaF-ZrF{sub 4}. Positive entropy constraints have been plotted to authenticate negative diffusivities observed.« less

Oxynitrides decorated 316L SS for potential bioimplant application

NASA Astrophysics Data System (ADS)

Saravanan Kaliaraj, Gobi; Kumar, N.

2018-03-01

Titanium oxynitride (TiON) and zirconium oxynitride (ZrON) were deposited onto 316L stainless steel (316L SS) using reactive magnetron sputtering technique. The monoclinic and cubic phase of TiON and ZrON were obtained by x-ray diffraction (XRD). Nanoindentation and wear test analysis exhibited the better mechanical properties of TiON and ZrON films. Wettability studies showed hydrophilic nature on coated films; whereas bare 316L SS substrate was least hydrophilic. Drastic reduction of bacterial adhesion (Pseudomonas aeruginosa), as well as biofilm formation, was observed in both the films at different time duration. TiON and ZrON films were exhibited excellent hemocompatibility by preventing the platelet activation. Furthermore, the coated films exhibited corrosion protection in presence and absence of hydrogen peroxide (H2O2) in artificial blood plasma (ABP) solution.

Spot-welding solid targets for high current cyclotron irradiation

PubMed Central

Ellison, Paul A.; Valdovinos, Hector F.; Graves, Stephen A.; Barnhart, Todd E.; Nickles, Robert J.

2016-01-01

Zirconium-89 finds broad application for use in positron emission tomography. Its cyclotron production has been limited by the heat transfer from yttrium targets at high beam currents. A spot welding technique allows a three-fold increase in beam current, without affecting 89Zr quality. An yttrium foil, welded to a jet-cooled tantalum support base accommodates a 50 μA proton beam degraded to 14 MeV. The resulting activity yield of 48 ± 4 MBq/(μA·hr) now extends the outreach of 89Zr for a broader distribution. PMID:27771445

A Highly Stable Porphyrinic Zirconium Metal–Organic Framework with shp-a Topology

DOE Office of Scientific and Technical Information (OSTI.GOV)

Feng, Dawei; Gu, Zhi-Yuan; Chen, Ying-Pin

2014-12-24

Through a kinetically controlled synthetic process, we synthesized PCN-223, a new porphyrinic Zr-MOF constructed from the newly reported hexagonal prismatic 12-connected Zr6 cluster through an unusual disordered arrangement, giving rise to the first example of the shp-a network in MOFs. With its extremely high connectivity, PCN-223 shows high stability in aqueous solutions with a wide range of pH. Cationic PCN-223(Fe) formed by postsynthetic treatment is an excellent recyclable heterogeneous catalyst for the hetero-Diels–Alder reaction.

Optical and structural studies of films grown thermally on zirconium surfaces

NASA Astrophysics Data System (ADS)

Morgan, J. M.; McNatt, J. S.; Shepard, M. J.; Farkas, N.; Ramsier, R. D.

2002-06-01

Variable angle IR reflection spectroscopy and atomic force microscopy are used to determine the thickness and morphology of films grown thermally on Zr surfaces in air. The density and homogeneity of these films increases with temperature in the range studied (773-873 K) and growth at the highest temperature follows cubic rate law kinetics. We demonstrate a structure-property relationship for these thermally grown films and suggest the application of IR reflectivity as an inspection method during the growth of environmentally passive films on industrial Zr components.

Effect of ZrO2 Source Variations on PbZrO3 - PbTiO3 Piezoelectric Properties.

DTIC Science & Technology

1980-01-15

wfatevalatediohryand wetbnde led/1cn Dipatont aod blNdigohvrywssontoyedP- aeilwt Coe 71 Wsingtongq D roC., e 20390 dnit Z-T ID 5,RM 1473 EDITION OF CAIO NOVGADN...PZ-PT 19 D . Coprecipitation of PZ-PT 26 IV SUMMARY AND CONCLUSIONS 33 V ACKNOWLEDGEMENTS 34 46 0 I 347602V ! _ _ A List of Illustrations Figure Page 1...chloride solution may be processed further to give high-purity zirconium (or zirconyl) compounds, such as the oxide, fluoride, nitrate , sulfate and

The effect of zirconium doping of cerium dioxide nanoparticles on pulmonary and cardiovascular toxicity and biodistribution in mice after inhalation.

PubMed

Dekkers, Susan; Miller, Mark R; Schins, Roel P F; Römer, Isabella; Russ, Mike; Vandebriel, Rob J; Lynch, Iseult; Belinga-Desaunay, Marie-France; Valsami-Jones, Eugenia; Connell, Shea P; Smith, Ian P; Duffin, Rodger; Boere, John A F; Heusinkveld, Harm J; Albrecht, Catrin; de Jong, Wim H; Cassee, Flemming R

2017-08-01

Development and manufacture of nanomaterials is growing at an exponential rate, despite an incomplete understanding of how their physicochemical characteristics affect their potential toxicity. Redox activity has been suggested to be an important physicochemical property of nanomaterials to predict their biological activity. This study assessed the influence of redox activity by modification of cerium dioxide nanoparticles (CeO 2 NPs) via zirconium (Zr) doping on the biodistribution, pulmonary and cardiovascular effects in mice following inhalation. Healthy mice (C57BL/6 J), mice prone to cardiovascular disease (ApoE -/- , western-diet fed) and a mouse model of neurological disease (5 × FAD) were exposed via nose-only inhalation to CeO 2 NPs with varying amounts of Zr-doping (0%, 27% or 78% Zr), or clean air, over a four-week period (4 mg/m 3 for 3 h/day, 5 days/week). Effects were assessed four weeks post-exposure. In all three mouse models CeO 2 NP exposure had no major toxicological effects apart from some modest inflammatory histopathology in the lung, which was not related to the amount of Zr-doping. In ApoE -/- mice CeO 2 did not change the size of atherosclerotic plaques, but there was a trend towards increased inflammatory cell content in relation to the Zr content of the CeO 2 NPs. These findings show that subacute inhalation of CeO 2 NPs causes minimal pulmonary and cardiovascular effect four weeks post-exposure and that Zr-doping of CeO 2 NPs has limited effect on these responses. Further studies with nanomaterials with a higher inherent toxicity or a broader range of redox activities are needed to fully assess the influence of redox activity on the toxicity of nanomaterials.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sakwa-Novak, Miles A.; Holewinski, Adam; Hoyt, Caroline B.

Polymeric amines such as poly(ethylenimine) (PEI) supported on mesoporous oxides are promising candidate adsorbents for CO2 capture processes. An important aspect to the design and optimization of these materials is a fundamental understanding of how the properties of the oxide support such as pore structure, particle morphology, and surface properties affect the efficiency of the guest polymer in its interactions with CO2. Previously, the efficiency of impregnated PEI to adsorb CO2 was shown to increase upon the addition of Zr as a surface modifier in SBA-15. However, the efficacy of this method to tune the adsorption performance has not beenmore » explored in materials of differing textural and morphological nature. Here, these issues are directly addressed via the preparation of an array of SBA-15 support materials with varying textural and morphological properties, as well as varying content of zirconium doped into the material. Zirconium is incorporated into the SBA-15 either during the synthesis of the SBA-15, or postsynthetically via deposition of Zr species onto pure-silica SBA-15. The method of Zr incorporation alters the textural and morphological properties of the parent SBA-15 in different ways. Importantly, the CO2 capacity of SBA-15 impregnated with PEI increases by a maximum of ~60% with the quantity of doped Zr for a “standard” SBA-15 containing significant microporosity, while no increase in the CO2 capacity is observed upon Zr incorporation for an SBA-15 with reduced microporosity and a larger pore size, pore volume, and particle size. Finally, adsorbents supported on SBA-15 with controlled particle morphology show only modest increases in CO2 capacity upon inclusion of Zr to the silica framework. The data demonstrate that the textural and morphological properties of the support have a more significant impact on the ability of PEI to capture CO2 than the support surface composition.« less

Isotopic Composition of Molybdenum and Barium in Single Presolar Silicon Carbide Grains of Type A+B

NASA Technical Reports Server (NTRS)

Savina, M. R.; Tripa, C. E.; Pellin, M. J.; Davis, A. M.; Clayton, R. N.; Lewis, R. S.; Amari, S.

2003-01-01

Presolar SiC grains fall into several groups based on C, N, and Si isotopic compositions. Approximately 93% are defined as mainstream, having 10 less than C-12/C-13 less than 100 and N-14/N-15 ranging from 50 to 20,000. A number of studies have shown that the most likely sources of mainstream grains are low mass asymptotic giant branch stars. Models of nucleosynthesis in AGB stars reproduce the s-process enhancements seen in the heavy elements in mainstream SiC grains. Among the less common grains, A+B grains, which comprise approximately 3-4% of presolar SiC, are perhaps the least well understood. Recent studies by Amari et al. show that A+B grains can be divided into at least 4 groups based on their trace element concentration patterns. Of 20 grains studied, 7 showed trace element patterns consistent with condensation from a gas of solar system composition, while the rest had varying degrees of process enhancements. Our previous measurements on 3 A+B grains showed Mo of solar isotopic composition, but Zr with a strong enhancement in 96Zr, which is an r-process isotope but can be made in an sprocess if the neutron density is high enough to bridge the unstable Zr-95 (T(sub 1/2)= 64 d). The observation of Mo with solar system isotopic composition in the same grains is puzzling however. Meyer et al. have recently shown that a neutron burst mechanism can produce a high Zr-96/Zr-94 without enhancing Mo-100, however this model leads to enhancements in Mo-95 and Mo-97 not observed in A+B grains. We report here results of Mo measurements on 7 additional A+B grains, and Ba measurements on 2 A+B grains, and compare these to the previous studies.

Intermetallic Growth and Interfacial Properties of the Grain Refiners in Al Alloys.

PubMed

Li, Chunmei; Cheng, Nanpu; Chen, Zhiqian; Xie, Zhongjing; Hui, Liangliang

2018-04-20

Al₃TM(TM = Ti, Zr, Hf, Sc) particles acting as effective grain refiners for Al alloys have been receiving extensive attention these days. In order to judge their nucleation behaviors, first-principles calculations are used to investigate their intermetallic and interfacial properties. Based on energy analysis, Al₃Zr and Al₃Sc are more suitable for use as grain refiners than the other two intermetallic compounds. Interfacial properties show that Al/Al₃TM(TM = Ti, Zr, Hf, Sc) interfaces in I-ter interfacial mode exhibit better interface wetting effects due to larger Griffith rupture work and a smaller interface energy. Among these, Al/Al₃Sc achieves the lowest interfacial energy, which shows that Sc atoms should get priority for occupying interfacial sites. Additionally, Sc-doped Al/Al₃(Zr, Sc) interfacial properties show that Sc can effectively improve the Al/Al₃(Zr, Sc) binding strength with the Al matrix. By combining the characteristics of interfaces with the properties of intermetallics, the core-shell structure with Al₃Zr-core or Al₃Zr(Sc1-1)-core encircled with an Sc-rich shell forms.

Monochloro non-bridged half-metallocene-type zirconium complexes containing phosphine oxide-(thio)phenolate chelating ligands as efficient ethylene polymerization catalysts.

PubMed

Tang, Xiao-Yan; Wang, Yong-Xia; Liu, San-Rong; Liu, Jing-Yu; Li, Yue-Sheng

2013-01-14

A series of novel monochloro half-zirconocene complexes containing phosphine oxide-(thio)phenolate chelating ligands of the type, ClCp'Zr[X-2-R(1)-4-R(2)-6-(Ph(2)P=O)C(6)H(2)](2) (Cp' = C(5)H(5), 2a: X = O, R(1) = Ph, R(2) = H; 2b: X = O, R(1) = F, R(2) = H; 2c: X = O, R(1) = (t)Bu, R(2) = H; 2d: X = O, R(1) = R(2) = (t)Bu; 2e: X = O, R(1) = SiMe(3), R(2) = H; 2f: X = S, R(1) = SiMe(3), R(2) = H; Cp' = C(5)Me(5), 2g: X = O, R(1) = SiMe(3), R(2) = H), have been synthesized in high yields. These complexes were identified by (1)H {(13)C} NMR and elemental analyses. Structures for 2b, 2c and 2f were further confirmed by X-ray crystallography. Structural characterization of these complexes reveals crowded environments around the zirconium. Complexes 2b and 2c adopt six-coordinate, distorted octahedral geometry around the zirconium center, in which the equatorial positions are occupied by three oxygen atoms of two chelating phosphine oxide-bridged phenolate ligands and a chlorine atom. The cyclopentadienyl ring and one oxygen atom of the ligand are coordinated on the axial position. Complex 2f also folds a six-coordinate, distorted octahedral geometry around the Zr center, consisting of a Cp-Zr-O (in P=O) axis [177.16°] and a distorted plane of two sulfur atoms and one oxygen atom of two chelating phosphine oxide-bridged thiophenolate ligands as well as a chlorine atom. When activated by modified methylaluminoxane (MMAO), all the complexes exhibited high activities towards ethylene polymerization at high temperature (75 °C), giving high molecular weight polymers with unimodal molecular weight distribution. The formation of 14-electron, cationic metal alkyl species might come from the Zr-O (in phenol ring) bond cleavage based on the DFT calculations study.

Pu-Zr alloy for high-temperature foil-type fuel

DOEpatents

McCuaig, Franklin D.

1977-01-01

A nuclear reactor fuel alloy consists essentially of from slightly greater than 7 to about 4 w/o zirconium, balance plutonium, and is characterized in that the alloy is castable and is rollable to thin foils. A preferred embodiment of about 7 w/o zirconium, balance plutonium, has a melting point substantially above the melting point of plutonium, is rollable to foils as thin as 0.0005 inch thick, and is compatible with cladding material when repeatedly cycled to temperatures above 650.degree. C. Neutron reflux densities across a reactor core can be determined with a high-temperature activation-measurement foil which consists of a fuel alloy foil core sandwiched and sealed between two cladding material jackets, the fuel alloy foil core being a 7 w/o zirconium, plutonium foil which is from 0.005 to 0.0005 inch thick.

Pu-ZR Alloy high-temperature activation-measurement foil

DOEpatents

McCuaig, Franklin D.

1977-08-02

A nuclear reactor fuel alloy consists essentially of from slightly greater than 7 to about 4 w/o zirconium, balance plutonium, and is characterized in that the alloy is castable and is rollable to thin foils. A preferred embodiment of about 7 w/o zirconium, balance plutonium, has a melting point substantially above the melting point of plutonium, is rollable to foils as thin as 0.0005 inch thick, and is compatible with cladding material when repeatedly cycled to temperatures above 650.degree. C. Neutron flux densities across a reactor core can be determined with a high-temperature activation-measurement foil which consists of a fuel alloy foil core sandwiched and sealed between two cladding material jackets, the fuel alloy foil core being a 7 w/o zirconium, plutonium foil which is from 0.005 to 0.0005 inch thick.

In situ DRIFTS investigation of NH3-SCR reaction over CeO2/zirconium phosphate catalyst

NASA Astrophysics Data System (ADS)

Zhang, Qiulin; Fan, Jie; Ning, Ping; Song, Zhongxian; Liu, Xin; Wang, Lanying; Wang, Jing; Wang, Huimin; Long, Kaixian

2018-03-01

A series of ceria modified zirconium phosphate catalysts were synthesized for selective catalytic reduction of NO with ammonia (NH3-SCR). Over 98% NOx conversion and 98% N2 selectivity were obtained by the CeO2/ZrP catalyst with 20 wt.% CeO2 loading at 250-425 °C. The interaction between CeO2 and zirconium phosphate enhanced the redox abilities and surface acidities of the catalysts, resulting in the improvement of NH3-SCR activity. The in situ DRIFTS results indicated that the NH3-SCR reaction over the catalysts followed both Eley-Rideal and Langmuir-Hinshelwood mechanisms. The amide (sbnd NH2) groups and the NH4+ bonded to Brønsted acid sites were the important intermediates of Eley-Rideal mechanism.

Enhanced pinning in YBCO films with BaZrO.sub.3 nanoparticles

DOEpatents

Driscoll, Judith L.; Foltyn, Stephen R.

2010-06-15

A process and composition of matter are provided and involve flux pinning in thin films of high temperature superconductive oxides such as YBCO by inclusion of particles including barium and a group 4 or group 5 metal, such as zirconium, in the thin film.

Thermal barrier coating

DOEpatents

Bowker, Jeffrey Charles; Sabol, Stephen M.; Goedjen, John G.

2001-01-01

A thermal barrier coating for hot gas path components of a combustion turbine based on a zirconia-scandia system. A layer of zirconium scandate having the hexagonal Zr.sub.3 Sc.sub.4 O.sub.12 structure is formed directly on a superalloy substrate or on a bond coat formed on the substrate.

USSR and Eastern Europe Scientifc Abstracts Materials Science and Metallurgy No 43.

DTIC Science & Technology

1977-03-09

Institute [Abstract] A study is made of the influence of stoichiometry on the characteristics of microplastic deformation in powders of zirconium and... microplasticity , stoichiometric carbides can be arranged in the following sequence of increasing brittleness: NbC, ZrC, TiC. References 18: 13 Soviet

Oxidant effect of La(NO3)3·6H2O solution on the crystalline characteristics of nanocrystalline ZrO2 films grown by atomic layer deposition

NASA Astrophysics Data System (ADS)

Oh, Nam Khen; Kim, Jin-Tae; Kang, Goru; An, Jong-Ki; Nam, Minwoo; Kim, So Yeon; Park, In-Sung; Yun, Ju-Young

2017-02-01

Nanocrystalline ZrO2 films were synthesized by atomic layer deposition method using CpZr[N(CH3)2]3 (Cp = C5H5) as the metal precursor and La(NO3)3·6H2O solution as the oxygen source. La element in the deposited ZrO2 films could not be detected as its content was below the resolution limit of the X-ray photoelectron spectroscopy. The alternative introduction of La(NO3)3·6H2O solution to conventionally used H2O as the oxidant effectively altered the crystalline structure, grain size, and surface roughness of the grown ZrO2 films. Specifically, the crystalline structure of the ZrO2 film changed from a mixture of tetragonal and monoclinic phases to monoclinic phase. The average grain size also increased, and the resulting film surface became rougher. The average grain sizes of the ZrO2 films prepared from La(NO3)3·6H2O solution at concentrations of 10, 20, 30, and 40% were 280, 256, 208, and 200 nm, respectively, whereas that prepared using H2O oxidant was 142 nm. However, the concentration of La(NO3)3·6H2O solution minimally influenced the crystalline characteristics of the nanocrystalline ZrO2 films i.e., the crystalline structure, grain size, and surface roughness except for crystallite size.

Thermal phase separation of ZrSiO4 thin films and frequency- dependent electrical characteristics of the Al/ZrSiO4/p-Si/Al MOS capacitors

NASA Astrophysics Data System (ADS)

Lok, R.; Kaya, S.; Yilmaz, E.

2018-05-01

In this work, the thermal phase separation and annealing optimization of ZrSiO4 thin films have been carried out. Following annealing optimization, the frequency-dependent electrical characteristics of the Al/ZrSiO4/p-Si/Al MOS capacitors were investigated in detail. The chemical evolution of the films under various annealing temperatures was determined by Fourier transform infrared spectroscopy (FTIR) measurements. The phase separation was determined by x-ray diffraction (XRD) measurements. The electrical parameters were determined via the capacitance–voltage (C–V), conductance–voltage (G/ω) and leakage-current–voltage (Ig–Vg ). The results demonstrate that zirconium silicate formations are present at 1000 °C annealing with the SiO2 interfacial layer. The film was in amorphous form after annealing at 250 °C. The tetragonal phases of ZrO2 were obtained after annealing at 500 °C. When the temperature approaches 750 °C, transitions from the tetragonal phase to the monoclinic phase were observed. The obtained XRD peaks after 1000 °C annealing matched the crystalline peaks of ZrSiO4. This means that the crystalline zirconium dioxide in the structure has been converted into a crystalline silicate phase. The interface states increased to 5.71 × 1010 and the number of border traps decreased to 7.18 × 1010 cm‑2 with the increasing temperature. These results indicate that an excellent ZrSiO4/Si interface has been fabricated. The order of the leakage current varied from 10‑9 Acm‑2 to 10‑6 Acm‑2. The MOS capacitor fabricated with the films annealed at 1000 °C shows better behavior in terms of its structural, chemical and electrical properties. Hence, detailed frequency-dependent electrical characteristics were performed for the ZrSiO4 thin film annealed at 1000 °C. Very slight capacitance variations were observed under the frequency variations. This shows that the density of frequency-dependent charges is very low at the ZrSiO4/Si interface. The barrier height of the device varies slightly from 0.776 eV to 0.827 eV under frequency dispersion. Briefly, it is concluded that the devices annealed at 1000 °C exhibit promising electrical characteristics.

Comparison of the octadentate bifunctional chelator DFO*-pPhe-NCS and the clinically used hexadentate bifunctional chelator DFO-pPhe-NCS for 89Zr-immuno-PET.

PubMed

Vugts, Danielle J; Klaver, Chris; Sewing, Claudia; Poot, Alex J; Adamzek, Kevin; Huegli, Seraina; Mari, Cristina; Visser, Gerard W M; Valverde, Ibai E; Gasser, Gilles; Mindt, Thomas L; van Dongen, Guus A M S

2017-02-01

All clinical 89 Zr-immuno-PET studies are currently performed with the chelator desferrioxamine (DFO). This chelator provides hexadentate coordination to zirconium, leaving two coordination sites available for coordination with, e.g., water molecules, which are relatively labile ligands. The unsaturated coordination of DFO to zirconium has been suggested to result in impaired stability of the complex in vivo and consequently in unwanted bone uptake of 89 Zr. Aiming at clinical improvements, we report here on a bifunctional isothiocyanate variant of the octadentate chelator DFO* and the in vitro and in vivo comparison of its 89 Zr-DFO*-mAb complex with 89 Zr-DFO-mAb. The bifunctional chelator DFO*-pPhe-NCS was prepared from previously reported DFO* and p-phenylenediisothiocyanate. Subsequently, trastuzumab was conjugated with either DFO*-pPhe-NCS or commercial DFO-pPhe-NCS and radiolabeled with Zr-89 according to published procedures. In vitro stability experiments were carried out in saline, a histidine/sucrose buffer, and blood serum. The in vivo performance of the chelators was compared in N87 tumor-bearing mice by biodistribution studies and PET imaging. In 0.9 % NaCl 89 Zr-DFO*-trastuzumab was more stable than 89 Zr-DFO-trastuzumab; after 72 h incubation at 2-8 °C 95 % and 58 % intact tracer were left, respectively, while in a histidine-sucrose buffer no difference was observed, both products were ≥ 92 % intact. In vivo uptake at 144 h post injection (p.i.) in tumors, blood, and most normal organs was similar for both conjugates, except for skin, liver, spleen, ileum, and bone. Tumor uptake was 32.59 ± 11.95 and 29.06 ± 8.66 % ID/g for 89 Zr-DFO*-trastuzumab and 89 Zr-DFO-trastuzumab, respectively. The bone uptake was significantly lower for 89 Zr-DFO*-trastuzumab compared to 89 Zr-DFO-trastuzumab. At 144 h p.i. for 89 Zr-DFO*-trastuzumab and 89 Zr-DFO-trastuzumab, the uptake in sternum was 0.92 ± 0.16 and 3.33 ± 0.32 % ID/g, in femur 0.78 ± 0.11 and 3.85, ± 0.80 and in knee 1.38 ± 0.23 and 8.20 ± 2.94 % ID/g, respectively. The uptake in bone decreased from 24 h to 144 h p.i. about two fold for the DFO* conjugate, while it increased about two fold for the DFO conjugate. Zr-DFO*-trastuzumab showed superior in vitro stability and in vivo performance when compared to 89 Zr-DFO-trastuzumab. This makes the new octadentate DFO* chelator a candidate successor of DFO for future clinical 89 Zr-immuno-PET.

Exceptional capability of nanosized CeO(2) materials to "dissolve" lanthanide oxides established by time-gated excitation and emission spectroscopy.

PubMed

Tiseanu, Carmen; Parvulescu, Vasile; Avram, Daniel; Cojocaru, Bogdan; Sanchez-Dominguez, Margarita

2014-05-28

The atomic scale homogeneity of Ce and Zr oxygen bonds represents the main reason for enhanced total oxygen storage capability of CeO2-ZrO2 (Ce/Zr = 1) as compared to that of CeO2. Here, we demonstrate that the addition of 10% Eu(3+) by wet impregnation on preformed nanosized CeO2-ZrO2 (Ce/Zr = 1) followed by calcination induces a remarkable homogeneity of 10% Eu(3+)-CeO2-ZrO2 solid solution. By use of time-resolved emission and excitation spectroscopies, the improvement of the nanoscale chemical and structural homogeneity of 10% Eu(3+)-CeO2-ZrO2 calcined at 1000 as compared to sample calcined at 750 °C is demonstrated. Based on the comparison of luminescence properties of 10% Eu(3+) impregnated on preformed nanosized CeO2-ZrO2 and CeO2, we also show that the presence of zirconium does not only preserve the ability of cerium oxide to "dissolve" lanthanide oxide, but also determines an important stabilization of defects (oxygen vacancies) generated upon Eu(3+) doping.

Effect of Zirconium Addition on Microstructure and Mechanical Property of TiC/Ti6A14V Composites

NASA Astrophysics Data System (ADS)

Ma, Xuliang; Wang, Xiang; Li, Li; Gai, Pengtao; Zhu, Chengwu

TiC/Ti6A14V composites with different Zr additions were prepared successfully in a consumable vacuum arc furnace equipped with a water-cooled copper crucible and the effect of the Zr content on the microstructure and mechanical property of 15 vol.%TiC/Ti6A14V composites was investigated by XRD, SEM and hardness testing. The results show that when the level of Zr addition is less than 4 wt.%, the morphology of the primary TiC in the composites is dendrite, and the petal-shape, piece-shape or palpus-shape eutectic TiC separates out around the primary TiC. The average size of the primary TiC decreases and the amount of eutectic TiC increases gradually with increasing Zr content. The effects of Zr on morphology of the primary TiC weaken with further addition of Zr. And the hardness (HRC) of composites was obviously increased in the whole range of Zr addition. The refinement mechanism of Zr was attributed to the combined effects of increase in nucleation rate at the constitutionally supercooled zone ahead of the solidification front and reduction in growth rate.

Ultraviolet-assisted direct patterning and low-temperature formation of flexible ZrO2 resistive switching arrays on PET/ITO substrates

NASA Astrophysics Data System (ADS)

Li, Lingwei; Chen, Yuanqing; Yin, Xiaoru; Song, Yang; Li, Na; Niu, Jinfen; Wu, Huimin; Qu, Wenwen

2017-12-01

We demonstrate a low-cost and facile photochemical solution method to prepare the ZrO2 resistive switching arrays as memristive units on flexible PET/ITO substrates. ZrO2 solution sensitive to UV light of 337 nm was synthesized using zirconium n-butyl alcohol as the precursor, and benzoylacetone as the complexing agent. After the dip-coated ZrO2 gel films were irradiated through a mask under the UV lamp (with wavelength of 325-365 nm) at room temperature and rinsed in ethanol, the ZrO2 gel arrays were obtained on PET/ITO substrates. Subsequently, the ZrO2 gel arrays were irradiated by deep UV light of 254 and 185 nm at 150 °C, resulting in the amorphous ZrO2 memristive micro-arrays. The ZrO2 units on flexible PET/ITO substrates exhibited excellent memristive properties. A high ratio of 104 of on-state and off-state resistance was obtained. The resistive switching behavior of the flexible device remained stable after being bent for 103 times. The device showed stable flexibility up to a minimum bending diameter of 1.25 cm.

Modeling of hydride precipitation and re-orientation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tikare, Veena; Weck, Philippe F.; Mitchell, John Anthony

In this report, we present a thermodynamic-­based model of hydride precipitation in Zr-based claddings. The model considers the state of the cladding immediately following drying, after removal from cooling-pools, and presents the evolution of precipitate formation upon cooling as follows: The pilgering process used to form Zr-based cladding imparts strong crystallographic and grain shape texture, with the basal plane of the hexagonal α-Zr grains being strongly aligned in the rolling-­direction and the grains are elongated with grain size being approximately twice as long parallel to the rolling direction, which is also the long axis of the tubular cladding, as itmore » is in the orthogonal directions.« less

Effects of Zr on microstructure and mechanical properties of Al-Cu base ribbons spun by planar flow casting

NASA Astrophysics Data System (ADS)

Lee, S. M.; Hong, C. P.

1998-04-01

The effects of the Zr addition on the solidification behavior and mechanical properties of the AI-Cu alloy ribbon have been investigated. Zr addition reduced the average grain size of the ribbon at the wheel-side surface, and promoted the microstructural transition into cellular/dendritic structure. Another noteworthy effect of Zr was the homogenization of the microstructure. The addition of Zr up to 0.5 wt.% in the /U-4.3 wt.% Cu ribbon resulted in a considerable increase in hardness at both the wheel-side and the air-side surfaces. The yield strength increased with the addition of Zr due to the grain refincment and more homogeneous distribution of ZrAI, particles. despite no noticeable improvement of the ductility.

Strontium and barium isotopes in presolar silicon carbide grains measured with CHILI—two types of X grains

DOE PAGES

Stephan, Thomas; Trappitsch, Reto; Davis, Andrew M.; ...

2017-05-10

Here, we used CHILI, the Chicago Instrument for Laser Ionization, a new resonance ionization mass spectrometer developed for isotopic analysis of small samples, to analyze strontium, zirconium, and barium isotopes in 22 presolar silicon carbide grains. Twenty of the grains showed detectable strontium and barium, but none of the grains had enough zirconium to be detected with CHILI. Nine grains were excluded from further consideration since they showed very little signals (<1000 counts) for strontium as well as for barium. Among the 11 remaining grains, we found three X grains. The discovery of three supernova grains among only 22 grainsmore » was fortuitous, because only ~1% of presolar silicon carbide grains are type X, but was confirmed by silicon isotopic measurements of grain residues with NanoSIMS. And while one of the X grains showed strontium and barium isotope patterns expected for supernova grains, the two other supernova grains have 87Sr/86Sr < 0.5, values never observed in any natural sample before. From their silicon isotope ratios, the latter two grains can be classified as X2 grains, while the former grain belongs to the more common X1 group. The differences of these grains in strontium and barium isotopic composition constrain their individual formation conditions in Type II supernovae.« less

Strontium and barium isotopes in presolar silicon carbide grains measured with CHILI—two types of X grains

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stephan, Thomas; Trappitsch, Reto; Davis, Andrew M.

Here, we used CHILI, the Chicago Instrument for Laser Ionization, a new resonance ionization mass spectrometer developed for isotopic analysis of small samples, to analyze strontium, zirconium, and barium isotopes in 22 presolar silicon carbide grains. Twenty of the grains showed detectable strontium and barium, but none of the grains had enough zirconium to be detected with CHILI. Nine grains were excluded from further consideration since they showed very little signals (<1000 counts) for strontium as well as for barium. Among the 11 remaining grains, we found three X grains. The discovery of three supernova grains among only 22 grainsmore » was fortuitous, because only ~1% of presolar silicon carbide grains are type X, but was confirmed by silicon isotopic measurements of grain residues with NanoSIMS. And while one of the X grains showed strontium and barium isotope patterns expected for supernova grains, the two other supernova grains have 87Sr/86Sr < 0.5, values never observed in any natural sample before. From their silicon isotope ratios, the latter two grains can be classified as X2 grains, while the former grain belongs to the more common X1 group. The differences of these grains in strontium and barium isotopic composition constrain their individual formation conditions in Type II supernovae.« less